PROCESS FOR PRODUCING METHACROLEIN AND METHACRYLIC ACID

Abstract: Methacrolein is produced in a high yield together with a small amount of methacrylic acid by catalytically oxidizing tert-butyl alcohol at a temperature of from 250 to 500°C by using a catalyst comprising an oxide composition of the empirical formula: Mo a Co b Fe c Bi d Cs e X f Y g O h wherein X is either both vanadium and palladium, Y is at least one member selected from titanium, tin and zirconium, a=12, b=2-12, c=0.5-7, d=0.1-5, e=0.0005-0.5, f=0.01-2, g=0-5 and h is a positive number proportional to the number of oxygen atoms satisfying the average valency of the metal atoms stated in the formula, which catalyst has a high resistance to compression and attrition and exhibits a high catalytic efficiency, mechanical strength and durability.

Description: PROCESS FOR PRODUCING METHACROLEIN AND METHACRYLIC ACID FIELD OF THE INVENTION The present invention relates to a process for producing methacrolein and methacrylic acid by the catalytic oxidation of tert-butyl alcohol in a vapor phase with molecular oxygen at an elevated temperature. More particularly, the present invention relates to a process for producing methacrolein in a high yield together with methacrylic acid by the catalytic oxidation of tert-butyl alcohol in a vapor phase with molecular oxygen at an elevated temperature by using a specific type of catalyst having a more enhanced catalytic activity, durability and mechanical strength than those of conventional catalysts containing molybdenum, bismuth, iron, cobalt, cesium and other specific elements as catalytic ingredients. BACKGROUND OF THE INVENTION Known are various types of processes and catalysts for producing methacrolein and methacrylic acid by the catalytic oxidation of tert-butyl alcohol in a vapor phase with molecular oxygen at an elevated temperature. For example, Japanese Patent Application Laid-open Nos. 50-105606 (1975) , 50-96513 (1975) , 51-113807 (1976) 55-85535 (1980), 55-62035 (1980) and other certain publications disclose various types of catalysts effective for the above-mentioned processes. These catalysts contain, as indispensable catalytic ingredients, molybdenum, bismuth, iron, cobalt and a plurality of other specific elements, for example, antimony and/or tungsten. When these catalysts are used however, the yield of methacrolein and the sum of the yields of methacrolein and methacrylic acid are usually not satisfactory and the mechanical strength and durability of the catalysts are also not satisfactory from the viewpoint of industrial use. Generally speaking, it is known that, in catalytic reactions, the catalytic effects of the catalyst used are significantly variable, depending on the types of catalytic ingredients and on the composition of the catalyst. Therefore, it is extremely difficult to make an accurate estimate of the catalytic effects of a new catalyst from the composition of the catalyst. Under these circumstances, it is desired to provide a new type of catalyst which enables methacrolein and methacrylic acid to be concurrently produced in a high yield and which exhibits an enhanced mechanical strength and durability. As a result of a study on the improvement of the catalyst it was discovered by the inventors of the present invention that the catalytic efflciency and the mechanical strength and durability of the catalyst can be enhanced by using cesium as an alkali metal catalytic ingredient and by adding an additional catalytic ingredient consisting of at least one member selected from the group of vanadium and palladium, and, optionally, a further additional catalytic ingredient consisting of at least one member selected from the group consisting of titanium, tin and zirconium to the conventional catalytic ingredients, that is, molybdenum, cobalt iron and bismuth. SUMMARY OF THE INVENTION An object of the present invention is to provide a process for producing methacrolein and methacrylic acid by the catalytic oxidation of tert-butyl alcohol in a vapor phase with molecular oxygen at an elevated temperature in the presence of a catalyst which is capable of enhancing the yield of methacrolein and which has an enhanced mechanical strength and durability. The above-mentioned object can be attained by the process of the present invention which comprises bringing a feed gas, containing tert-butyl alcohol and molecular oxygen, into contact with a catalyst at an elevated temperature, which process is characterized in that the catalyst comprises an oxide composition of the empirical formula (1): Mo Co Fe Bi Cs X Y O. a b c d e f gn wherein Mo represents a molybdenum atom, Co represents a cobalt atom, Fe represents an iron atom, Bi represents a bismuth atom, Cs represents a cesium atom, X represents at least one member selected from the group consisting of vanadium and palladium atoms, Y represents at least one member selected from the group consisting of titanium, tin and zirconium atoms, 0 represents an oxygen atom, the subscripts a through g respectively represent a positive number proportional to the number of respective metal atoms, wherein when a is 12, b through g fall respectively within the following ranges: b = 2 to 12, c = 0.5 to 7, d = 0.1 to 5, e = 0.0005 to 0.5, f = 0.01 to 2 and g = 0 to 5, and the subscript h represents a positive number corresponding to the number of oxygen atoms satisfying the average valence of the above-mentioned metal atoms. It is preferable that the values of the subscripts b through g be respectively in the ranges of b = 4 to 10, c = 1 to 5, d = 0.5 to 4, e = 0.001 to 0.3, f = 0.05 to 1.5 and g = 0.1 to 5. DETAILED DESCRIPTION OF THE INVENTION In the catalyst usable for the process of the present invention, it is important that cesium is used as an alkali metal catalytic ingredient, either or both of vanadium and palladium are added, as an additional catalytic ingredient, to the conventional catalytic ingredient, that is, molybdenum, bismuth, iron, cobalt and an alkali metal, and optionally, that a further additional catalytic ingredient consisting of one, two, or more members from the group consisting of titanium, tin and zirconium is added to the above-mentioned conventional and additional catalytic ingredients. If an alkali metal, such as potassium, sodium, rubidium and lithium, which are different from cesium, is used, the resultant catalyst will result in a poor yield of methacrolein and in a poor sum of yields of methacrolein and methacrylic acid. Accordingly, the alkali metals which are different from cesium cannot be used to attain the object of the present invention. Even if cesium is used as an alkali metal catalytic ingredient, if the additional catalytic ingredient consisting of at least one member selected from vanadium and palladium is not used, the resultant catalyst will result in a poor yield of methacrolein. Also, in the case where cesium is used and the additional catalytic ingredient consisting of vanadium and/or palladium is replaced by at least one member selected from P, As, B, W, Sb, Te, Cr, Ti, Sn, Zr, Zn, Cu, Al and Se in an amount of 0.5 atoms per atom of molybdenum, the resultant catalyst results in an unsatisfactory yield of methacrolein. Furthermore, even if the additional catalytic ingredient is used, if no cesium is used, the use of the resultant catalyst will result in a poor yield of methacrolein. That is, the catalyst containing cesium and vanadium and/or palladium is effective for producing methacrolein in an increased yield thereof. However, with respect to this type of catalyst, it is desirable to enhance resistances thereof to attrition and compression. Also, it is desirable to additionally increase the yield of methacrolein. It was discovered by the inventors of the present invention that, in the catalytical production of methacrolein and methacrylic acid, the addition of the further additional catalytic ingredient, consisting of at least one member selected from the group comprising titanium, tin and zirconium, is not only effective for enhancing the mechanical strength and durability of the resultant catalyst, but also, contributive for increasing the yield of methacrolein. If the further additional catalylic ingredient is replaced by at least one element selected from P, As, B, W, Sb, Te, Cr, Zn, Cu, Al and Se, the contribution of the elements on the yield of methacrolein and the resistances to attrition and compression rupture, is very small and unsatisfactory. The further additional catalytic ingredients, namely, titanium, tin and zirconium, may be used either singly or in combination vf two or more thereof. However, the use of a combination of two or more ingredients is not remarkably superior to the use of a single ingredient in the yield of methacrolein, in the sum of yields of methacrolein and methacrylic acid and in the resistances of the resultant catalyst to attrition and compression. The catalyst usable for the present invention must have the empirical composition specified hereinbefore. If the composition of the catalyst falls outside of the specified range of the composition, the resultant catalyst will result in an unsatisfactory yield of methacrolein and in the sum of yields of methacrolein and methacrylic acid. As long as the composition of the catalyst falls within the range spe.cified above, not only is it possible for the process of the present invention to produce methacrolein and methacrylic acid, especially, methacrolein, in an extremely high yield thereof, but, also, the resultant catalyst exhibits enhanced resistance to attrition and crush strength. Therefore, the process of the present invention can be stably carried out over a long period of time without disintegration of the catalyst and change in the catalytic efficiency of the catalyst. Accordingly, it is obvious that the process of the present invention can be very advantageous for continuously producing methacrolein and methacrylic acid on an industrial scale. In the catalyst usable for the present invention, the respective catalytic ingredients are present in the form of oxides, which include those of the type in which each single element is bonded with oxygen, those of the type in which two or more elements are bonded with oxygen to form a complex and those of the type in which the above-mentioned two types of oxides are combined together. The catalyst of the above empirical formula (1), usable for the process of the present invention, may be prepared in any conventional manner by using, as the starting raw material, oxides, salts and other compounds, containing the above-mentioned catalytic ingredients. However, calcination of the catalyst, i.e., the final step of the catalyst preparation; should preferably be carried out at a temperature in the range of from 550"C to 8000C, more preferably, from 6000C to 7500C, and over a period of 1 to 20 hours, more preferably, from 2 to 10 hours, for obtaining the desired yield of methacrolein and catalyst strength. This temperature range is higher than the range of from 4000C to 5000C usually employed for preparing the conventional catalysts based on molybdenum, bismuth, iron and cobalt. A calcining temperature falling outside of the above -mentioned range may sometimes cause a decrease in the mechanical strength of the resultant catalyst and/or the yield of methacrolein. The calcining operation is carried out in a gas containing oxygen, usually an air atmosphere. The general procedures for preparing a catalyst are as follows. Oxides, salts and other compounds containing the above-mentioned metal ingredients are mixed together in an aqueous medium to prepare a uniform slurry. The aqueous slurry is dried at a temperature not exceeding 3000C. In this case, the drying operation is preferably carried out in two steps. That is, in the first step, the aqueous dispersion is heated at a temperature of from 1000C to 1500C, preferably at approximately 1200 C, to evaporate water; and in the second step, the dried product is heated at a temperature, higher than that in the first step, of from 1500C to 3000C, preferably at approximately 2000C, for a time period of 3 to 20 hours to eliminate volatile substances, for example, ammonium nitrate and nitrogen oxides. The dried product is shaped into pellets or particles of a desired shape and size. The shaped pellets or particles are calcined under the above-mentioned conditions. As examples of the starting raw materials which can be used in the preparation of the catalyst are, for example, molybdenum compounds, such as molybdic acid, ammonium molybdate and molybdenum trioxide; cobalt compounds, such as cobalt carbonate, cobalt nitrate, cobaltous oxide, tricobalt tetroxide, cobalt chloride, cobaltons hydroxide and cobaltic hydroxide; iron compounds, such as ferrous nitrate, ferric nitrate, ferrous oxide, ferric oxide, ferrous carbonate, ferrous chloride, ferric chloride, ferrous hydroxide and ferric hydroxide; bismuth compounds, such as bismuth nitrate, bismuth dichloride, bismuth trichloride, bismuth pentoxide, bismuth trioxide, bismuth tetroxide, bismuth oxynitrate, bismuth hydroxide, bismuth subnitrate and bismuth oxychloride; cesium compounds, such as cesium nitrate, cesium chloride, cesium hydroxide, cesium carbonate and cesium oxide; vanadium compounds, such as vanadium chloride, ammonium metavanadate, vanadyl chloride, and vanadium pentoxide; palladium compounds, such as palladium nitrate, palladium hydroxide, palladium chloride and palladium oxide; titanium compounds, such as titanium dioxide, titanic acid, titanium trichloride and titanium tetrachloride; tin compounds, such as stannic oxide, tin hydroxide, stannic chloride, stannous oxide and stannic acid; and zirconium compounds, such as zirconium oxide, zirconium oxynitrate and zirconium hydroxide. Among the above-mentioned compounds, the compounds which are most preferable as starting raw materials are nitrates and ammonium salts of the respective ingredient metals. The procedures for preparing a catalyst usable for the present invention will be described in more detail with reference to a catalyst consisting of molybdenum, cobalt, iron, bismuth cesium, vanadium and oxygen. Predetermined amounts of ammonium molybdate and ammonium metavanadate are dissolved in water, preferably warm water, to prepare an aqueous solution. Separately, solution of a predetermined amount of bismuth nitrate in nitric acid and predetermined amounts of ferric nitrate, cobalt nitrate and cesium nitrate are dissolved in water, preferably warm water. This acidic solution of the nitrates is mixed dropwise with the above-mentioned solution of molybdenum and vanadium, while the mixture is being stirred. The so-obtained aqueous slurry is then heated at temperature of from 1000C to 1500C, preferably at approximately 1200C, by using a drum dryer or a spray dryer to evaporate water from the slurry. Next, the evaporation residue is heated at a temperature of from 1500C to 3000 C, preferably at approximately 2000 C, until no more ammonium nitrate and nitrogen oxides are evolved from the dried product and the residue is completely dried. The resultant dried product is shaped or granulated into a desired shape and size of pellets or particles. If necessary, the particles can be separated by using a screen having a desired mesh to collect particles having a particular desired size. The particles are finally calcined1 preferably at a temperature of from 5500C to 8000C, more preferably, from 6000C to 7500C. In the case where palladium is used in place of vanadium as a catalytic metal ingredient, it is preferable to use palladium nitrate as a starting raw material. A predetermined amount of palladium nitrate is dissolved together with ferric nitrate, cobalt nitrate and cesium nitrate in warm water. The solution is added dropwise into a solution of ammonium molybdate alone in warm water while the resultant mixture is being stirred. In the case where the catalyst contains a further additional catalytic ingredient, for example, titanium, it is preferable that titanium dioxide be suspended in an aqueous solution of ammonium molybdate alone or together with ammonium metavanadate. Also, in the case where the catalyst contains a further additional catalytic ingredient, it is preferable to carry out the calcining operation at a temperature of from 5500C to 8000C, more preferably, from 6000C to 7500C in an oxygen-containing atmosphere. The procedures and starting materials of the catalyst usable for the present invention are not limited to the above-mentioned examples. However, it is important that the starting materials be mixed with each other in the presence of water, the mixture be dried in two separate steps and then, the dried mixture be calcined at a temperature of from 550"C to 8000C, preferably, from 6000C to 7500C. This feature is effective for increasing the reproductivity in the catalytic activity and the durability and attrition resistance of the catalyst. The catalyst may be used alone or in combination with a carrier. Carriers, such as those known for supporting conventional oxidation catalysts and for bringing about favorable effects to the reaction involved, e.g., silica, alumina, silica-alumina, titania, diatomaceous earth and carborundum, may be used. These carriers may be combined with the catalyst either during or after preparation of the catalyst. In general, the size and shape of the catalyst particle used, and the use of a carrier are not critical factors, because they do not greatly affect the resultant catalytic activity. In carrying out the process of the present invention, an inert gas, which is not reactive to catalytic oxidation, may be used as a diluent gas for the feed gas. The diluent gas may be steam, nitrogen gas, carbon dioxide gas, n-butane gas, isobutane gas or propane gas. Especially, the addition of steam as the inert gas to the feed gas is effective for increasing the yield of methacrolein and the durability in catalytic activity of the catalyst. Therefore, it is preferable that the catalytic oxidation be carried out in the presence of steam. The steam is used preferably in an amount of from 0.05 to 10 moles, more preferably, from 0.1 to 8 moles, per mole of tert-butyl alcohol. In the catalytic oxidation of the present invention, the molecular oxygen used need not be highly purified. That is, oxygen-containing gases, such as air or a mixture of pure molecular oxygen and the above-mentioned diluent gas, may be conveniently used. Air, particularly, may be advantageously used. The relative proportion of molecular oxygen in the feed gas is usually in the range of from 0.4 to 5 moles, more preferably, from 0.5 to 3 moles, per mole of tert-butyl alcohol. In the catalytic oxidation of the present invention the contact of the feed gas with the catalyst is carried out preferably at a temperature in the range of from 2500C to 5000C, more preferably from 3000C to 4500C. The contact time is usually in the range of from 0.3 to 20 seconds, preferably from 0.5 to 15 seconds. The reaction may be carried out under atmospheric pressure, although superatmospheric or subatmospheric pressure may be used if desired. However, atmospheric pressure is preferable. The catalytic oxidation reaction may be carried out in a fixed bed, a moving bed or a fluidized bed. If it is necessary, the resultant methacrolein and methacrylic acid can be isolated from the reaction mixture by using any kind of conventional isolating processes, for example, by the absorption of methacrolein and methacrylic acid by cold water followed by the stripping and distillation of methacrolein and methacrylic acid. The present invention will be further clarified by the examples and comparison examples set forth below. In all of the examples, flow is expressed by weight unless otherwise specified. In these examples, the conversion of tert-butyl alcohol and yield of methacrolein or methacrylic acid were calculated in accordance with the following equations. Percent conversion of tert-butyl alcohol = moles of tert-butyl alcohol consumed X100 moles of tert-butyl alcohol fed Percent yield of methacrolein or methacrylic acid = moles of methacrolein or methacrylic acid produced moles Ïf tert-butyl alcohol fed x 100 The moles of tert-butyl alcohol fed, the moles of tert-butyl alcohol consumed and the moles of methacrolein or methacrylic acid produced were determined after one hour had elapsed from the start of the reaction. The crush strength of the catalyst was determined as follows. A catalyst tablet (5 mm in diameter and 5 mm in height) was placed on a testing plate and compressed by using a Kiya-type hardness tester until the tablet was crushed. The value of the compressive load in Kg under which the tablet was crushed was measured. The above -mentioned testing procedures were applied to 50 tablets. The crush strength of the catalyst tablet was represented by an average value calculated from the results of 50 tablets. The resistance of the catalyst to attrition was determined as follows. A glass test tube having an inner diameter of 2.54 cm and a height of 300 cm was used. 50 tablets of a catalyst were dropped down from the top of the glass test tube to the bottom thereof. The total weight of the tablets which were crushed into particles having a mesh size of 6 or less was measured. The resistance of the catalyst to attrition was thereafter represented by a ratio (t) of the weight of the crushed tablets to the weight of the original 50 tablets. Example 1 In order to provide an aqueous solution suspension, 141.3 g of ammonium molybdate [(NH4) 6Mo7O24.4H2O], and 0.78 g of ammonium metavanadate [NH4VO3] were dissolved in 200 ml of water maintained at a temperature of 40"C. A solution of 38.8 g of bismuth nitrate jBi(NO3)3.5H2O] in 50 ml of a 15% nitric acid aqueous solution was mixed into a solution of 64.6 g of ferric nitrate (Fe(NO3)3.9H2O) 0.078 g of cesium nitrate [CsNO3] and 186.2 g of cobalt nitrate [Co(NO3)2-6H2O] in 200 ml of water having a temperature adjusted to 400C. The mixture was admixed dropwise into the above-prepared aqueous solution of ammonium molybdate and ammonium metavanadate while the admixed solution was being stirred. The admixed solution was first dried at a temperature of 1200C by using a drum dryer. The initially dried material was additionally dried at a temperature of 2000C for 10 hours by using an oven. The resultant material was shaped into tablets having a diameter of 5 mm and a length of 5 mm by means of a tablet-forming machine. The tablets were calcined at a temperature of 6500C for 5 hours in an air atmosphere to provide a catalyst. In the catalyst thus prepared, the atomic ratio of Mo:Bi:Co:Fe:Cs:V was 12:1:8:2:0.005:0.1. 10 ml of the catalyst tablets were charged into a U-shaped glass tube having an inner diameter of 8 mm. A feed gas-containing tert-butyl alcohol, air and steam in a molar ratio of 1:10:6 was passed through the U-shaped tube at a temperature of 3900C at a flow rate of 180 ml/min so that the contact time of the feed gas with the catalyst tablets was 3.3 seconds. The percent conversion of tert-butyl alcohol, and the yields of methacrolein and methacrylic acid were determined. The results are shown in Table 1. Examples 2 through 6 In each of Examples 2 through 6, the same catalyst -preparing procedures as those described in Example 1 were carried out, except that the atomic ratio of Mo:Bi:Co:Fe:Cs:V was varied for each of the Examples 2 through 6 in accordance with the ratios shown in Table 1. The same catalytic oxidation procedures as those described in Example 1 were carried out, except that in Example 3, the catalytic oxidation was carried out at a temperature of 380"C. The results are shown in Table 1. Examples 7 and 8 In each of Examples 7 and 8, procedures identical to those described in Example 1 were carried out, except that 1.84 g of palladium nitrate [Pd(NO3)2] were added to the mixed solution. The atomic ratio of Mo:Bi:Co:Fe:Cs:V:Pd for each of Examples 7 and 8 is respectively shown in Table 1. Also, in Example 7, the catalytic oxidation was carried out at a temperature of 380"C. The results are shown in Table 1. Exmples 9 and 10 In each of Examples 9 and 10, the same procedures as those used in Example 8 were carried out, except that no ammonium metavanadate was used. The atomic ratio of Mo:Bi:Co:Fe:Cs:Pd for each of the two examples is respectively shown in Table 1. In Example 9, the reaction temperature (catalytic contacting temperature) was 3600C. The results of Examples 9 and 10 are shown in Table 1. Table I Composition of catalyst Conversion of Yield of Yield of Sum of(*)1 Exaample (Atomic ratio) Reaction tert-butyl methacrolein methacrylic yields No. Temperature alcohol acid Mo Co Fe Bi Cs V Pd ( C) (%) (%) (%) (%) 1 12 8 2 1 0.005 0.1 - 390 100 85.2 2.3 87.5 2 10 8 2 1 0.05 0.1 - 390 100 84.3 2.1 86.4 3 10 8 2 1 0.1 0.5 - 380 100 83.0 2.0 85.0 4 12 7 4 1 0.01 0.1 - 390 100 84.8 2.1 86.9 5 12 8 3 2 0.01 0.1 - 390 100 85.1 2.2 87.3 6 11 6 4 1 0.01 0.1 - 390 100 84.9 2.0 86.9 7 10 8 2 1 0.05 0.1 0.1 380 100 85.0 2.3 87.3 8 11 8 3 1 0.01 0.1 0.1 390 100 84.7 2.1 86.8 9 10 8 2 1 0.005 - 0.1 360 100 84.6 2.2 86.8 10 10 8 2 1 0.1 - 0.5 390 100 85.6 2.0 87.6 Note: (*)1- Sum of yield of methacrolein and yield of methacrylic acid Comparison Example 1 The same procedures as those described in Example 1 were carried out, except that neither cesium nitrate nor ammonium metavanadate were used, the atomic ratio of the catalytic ingredients was the same as that shown in Table 2 and the reaction temperature was 3700C. The results are shown in Table 2. Comparison Examples 2 and 3 In each of Examples 2 and 3, the same procedures as those described in Example 1 were carried out, except that no ammonium metavanadate was used and the atomic ratio of the catalytic ingredients in the catalyst for each of the two Comparison Examples was the same as that respectively shown in Table 2. The results are shown in Table 2. Comparison Examples 4 through 7 In each of Examples 4 through 7, the same procedures as those described in Example 1 were carried out, except that no ammonium metavanadate was used, cesium nitrate which served as the raw material for the alkali metal catalytic ingredient was replaced respectively by sodium nitrate in Comparison Example 4, by rubidium nitrate in Comparison Example 5 and by potassium nitrate in Comparison Examples 6 and 7 in accordance with the amounts respectively shown in Table 2, and the atomic ratio of the catalytic ingredients in the resultant catalyst for each of these Comparison Examples was the same as that respectively shown in Table 2. In Comparison Examples 4 and 7, catalytic oxidation was carried out at a temperature of 370"C. The results are shown in Table 2. Comparison Example 8 The same procedures as those described in Example 1 were carried out, except that no cesium nitrate was used, the atomic ratio of the catalytic ingredients in the resultant catalyst was the same as that shown for this Comparison Example in Table 2, and catalytic oxidation was carried out at a temperature for a contact time as specified in Table 2 for this Comparison Example. The results are shown in Table 2. Comparison Example 9 A comparison catalyst having an atomic ratio of the catalytic ingredients as shown in Table 2 was prepared by following procedures similar to those used in Example 9, except that no cesium nitrate was used. The same reaction procedures as those described in Example 1 were carried out, except that the reaction temperature and the contact time followed were those shown in Table 2 for this Comparison Example 9. The results are shown in Table 2. Comparison Examples 10 through 12 In each of Comparison Examples 10 through 12, a comparison catalyst was prepared by following the same procedures as those described in Example 1, except that cesium nitrate was replaced respectively by potassium nitrate in Comparison Example 10, by sodium nitrate in Comparison Example 11 and by rubidium nitrate in Comparison Example 12. Also, a catalytic conversion of tert-butyl alcohol was carried out by carrying out the same procedures as those described in Example 1, except that the above-prepared comparison catalyst was used, and the reaction temperature and the contact time followed were those respectively specified in Table 2 for Comparison Examples 10 through 12. The comparison catalysts of Comparison Examples 11 and 12 were prepared by calcining at temperatures of 6600C and 6200C, respectively. The results are shown in Table 2. Table 2 Compar- Composition of catalyst Contact Reaction Conversion of Yield of Yield of Sum of(*)1 ison (Atomic ratio) time temperature tert-butyl methacrolein methacrylic yields Example alcohol acid No. Mo Co Fe Si Alkali metal V Pd (sec) ( C) (%) (%) (%) (%) 1 10 8 2 1 - - - 3.3 370 100 50.1 2.8 52.9 2 10 8 2 1 Cs=0.03 - - 3.3 390 99.1 61.9 2.3 64.2 3 10 8 2 1 Cs=0.1 - - 3.3 390 98.0 25.3 1.8 27.1 4 10 8 3 1 Na=0.5 - - 3.3 370 100 65.8 2.0 67.9 5 10 8 3 1 Rb=0.05 - - 3.3 390 100 67.3 2.3 69.6 6 10 8 2 1 K=0.01 - - 3.3 370 100 65.2 2.0 67.2 7 10 8 2 1 K=0.3 - - 3.3 390 100 66.6 1.9 68.5 8 10 8 2 1 - 0.1 - 3.0 360 100 62.4 2.1 64.5 9 10 8 2 1 - - 0.1 3.0 340 100 57.7 2.0 59.7 10 10 8 2 1 K=0.05 0.1 - 3.0 370 100 65.4 2.9 68.3 11 10 8 2 1 Na=0.1 0.1 - 3.0 370 100 67.1 2.0 69.1 12 10 8 2 1 Rb=0.1 0.1 - 3.0 390 99.9 65.8 2.7 68.5 Comparison Examples 13 through 17 In each of Comparison Examples 13 through 17, a comparison catalyst was prepared by following the same procedures as those described in Example 1, except that the amounts of the raw materials of the respective catalytic ingredients used were changed so that the resultant comparison catalysts had a catalytic ingredient composition, as shown in Table 3, which is outside of the scope of the present invention. In addition, the calcining temperature was adjusted to 6O00C in Comparison Examples 13 and 14, to 6500C in Comparison Example 15, to 570QC in Comparison Example 16 and to 6600C in Comparison Example 17. By using the comparison catalysts, the same procedures for converting tert-butyl alcohol as those described in Example 1 were carried out, except that the reaction temperature and the contact time were changed to those shown respectively in Table 3 for Comparison Examples 13 through 17. The results are shown in Table 3. Comparison Example 18 A comparison catalyst was prepared in accordance with the same procedures as those used in Example 9, except that the cesium nitrate as a raw material of an alkali metal catalytic ingredient was replaced by potassium nitrate and the resultant catalyst had the composition described in Table 3. Next, the same procedures for catalytically converting tert-butyl alcohol as those described in Example 1 were carried out, except that the reaction temperature and the contact time were changed to those shown in Table 3 for Comparison Example 18. The results for this Comparison Example are shown in Table 3. Comparison Example 19 A comparison catalyst was prepared by following the same procedures as those used in Example 9, except that the amount of palladium nitrate employed was changed to a value which caused the composition of the resultant catalyst to be changed to that shown in Table 3 for Comparison Example 19, and the calcining temperature of 6500C was changed to 6700C. The resultant catalyst was used for carrying out the same procedures as those mentioned in Example 1 for catalytically converting tert-butyl alcohol, except that the reaction temperature and the contact time were changed to those shown in Table 3 for Comparative Example 19. The results for this-Comparative Example are shown in Table 3. Table 3 Compar- Composition of catalyst Contact Reaction Conversion of Yield of Yield of Sum of(*)1 ison (Atomic ratio) time temperature tert-butyl methacrolein methacrylic yields Example alcohol acid No. Mo Co Fe Bi Alkali metal V Pd (sec) ( C) (%) (%) (%) (%) 13 12 1 6 1 Cs=0.01 0.1 - 3.3 390 100 66.2 2.4 68.6 14 13 8 0.5 1 Cs=0.01 0.1 - 3.3 390 100 65.1 2.2 67.3 15 12 8 3 0.05 Cs=0.01 0.1 - 3.0 390 100 63.4 2.9 66.3 16 11 8 2 1 Cs=0.75 0.1 - 3.3 410 98.3 29.7 1.7 31.4 17 12 8 3 1 Cs=0.01 3 - 3.0 370 100 53.8 2.0 56.8 18 10 8 2 1 K=0.05 - 0.1 3.0 370 100 61.5 2.3 63.8 19 12 8 3 1 Cs=0.01 - 3 3.0 360 100 51.2 2.1 53.3 Comparison Examples 20 through 33 In each of the Comparison Examples 20 through 33, the same catalyst-preparing procedures as those described in Example 1 were carried out, except that ammonium metavanadate was replaced by phosphoric acid, arsenic pentaoxide, boric acid, ammonium paratungstate, antimony trioxide, tellurium oxide, chromium nitrate, titanium dioxide, stannic oxide, zirconium oxide, zinc nitrate, cupric nitrate, aluminium nitrate or selenium dioxide, as indicated in Table 4. By using this catalyst, the same catalytic oxidation procedures of tert-butyl alcohol as those described in Example 1 were carried out, except that the reaction temperature was as indicated in Table 4. The results are indicated in Table 4. Table 4 Compar- Composition of catalyst Reaction Conversion of Yield of Yield of Sum of(*)1 ison (Atomic ratio) temperature tert-butyl methacrolein methacrylic yields Example alcohol acid Additional No. Mo Co Fe Bi Cs ingredient ( C) (%) (%) (%) (%) 20 12 8 2 1 0.1 P=0.5 400 99.7 68.3 2.0 70.3 21 10 8 2 1 0.1 As=0.5 400 99.9 70.0 2.1 72.1 22 10 8 2 1 0.1 B=0.5 400 100 66.1 1.9 68.0 23 12 8 2 1 0.1 W=0.5 380 100 68.5 2.6 71.1 24 12 8 2 1 0.1 Sc=0.5 390 100 71.9 2.1 74.0 25 12 8 2 1 0.1 Te=0.5 390 100 70.3 2.2 72.5 26 12 8 2 1 0.1 Cr=0.5 380 100 67.6 2.5 70.1 27 10 8 2 1 0.1 Ti=0.5 400 100 76.3 2.3 78.6 28 10 8 2 1 0.1 Sn=0.5 380 100 75.9 2.6 78.5 29 10 8 2 1 0.1 Zr=0.5 400 100 74.9 2.2 77.1 30 10 8 2 0.5 0.05 Zn=1 400 100 70.2 2.0 72.2 31 10 7 2 1 0.05 Cu=0.5 380 100 68.3 2.4 70.7 32 10 7 2 1 0.05 Al=1 370 100 62.1 2.9 65.0 33 10 7 2 1 0.05 Se=1 380 100 65.3 2.6 67.9 Comparison Examples 34 through 38 The same catalyst-preparing procedures as those described in Example 1 were carried out, except that the atomic ratio Mo:Co:Fe:Bi:Cs:V was as indicated in Table 5 and phosphoric acid, arsenic pentaoxide, boric acid, ammonium paratungstate or cupric nitrate was added as a comparative further additional ingredient. Also, the same catalytic oxidation procedures of tert-butyl alcohol as those described in Example 1 were carried out by using the above-mentioned catalyst, except that the flow rate of the feed gas was 200 ml/min and the contact time was 3 seconds. The results are indicated in Table 5. Comparison Example 39 The same catalyst-preparing procedures as those described in Example 1 were carried out, except that palladium nitrate and arsenic pentaoxide were added each in amounts indicated in Table 5. The same catalytic oxidation of tert-butyl alcohol as that described in Comparison Example 34 was carried out by using the above-mentioned catalyst. The results are indicated in Table 5. Comparison Examples 40 and 41 The same catalyst-preparing procedures as those described in Comparison Example 39 were carried out, except that ammonium metavanadate was replaced by palladium nitrate and arsenic pentaoxide was replaced by tellurium oxide or phosphoric acid so as to provide an atomic ratio of the ingredients in the resultant catalyst indicated in Table 5. By using the resultant catalyst, the same catalytic oxidation procedures of tert-butyl alcohol as those described in Comparison Example 34 were carried out, except that in Comparison Example 41, the reaction temperature was 3900C. The results are indicated in Table 5. Table 5 Compar- Composition of catalyst Reaction Conversion of Yield of Yield of Sum of(*)1 ison (Atomic ratio) temperature tert-butyl methacrolein methacrylic yields Example Fürther alcohol acid No Additional Mo Co Fe Bi Cs V Pd ingredient ( C) (%) (%) (%) (%) 34 12 8 2 1 0.005 0.1 - P=0.5 400 100 77.3 2.1 79.4 35 12 8 2 1 0.005 0.1 - As=0.5 400 100 75.6 2.6 78.2 36 12 8 2 1 0.005 0.1 - B=0.5 400 100 76.3 2.0 78.3 37 12 8 2 1 0.005 0.1 - W=0.5 390 100 75.9 1.8 77.7 38 10 7 2 1 0.05 0.1 - Cu=0.5 390 100 76.3 2.1 78.4 39 10 8 2 1 0.1 0.1 0.1 As=0.5 400 100 76.3 2.4 78.7 40 10 8 2 1 0.1 - 0.1 Te=0.5 400 100 77.6 2.1 79.7 41 10 8 2 1 0.1 - 0.1 P=0.5 390 100 77.2 1.9 79.1 Example 11 The same procedures as those described in Example 1 for catalytically converting tert-butyl alcohol into methacrolein and methacrylic acid were continuously carried out for 1000 hours by using the same catalyst (Moa2Co8 Fe2Bi1Cs0005V01) as that mentioned in Example 1. After 1000 hours had elapsed from the start of the reaction, the percent conversion of tert-butyl alcohol was 100%, the percent yield of methacrolein was 85.38 and the percent yield of methacrylic acid was 2.5%. The average crush strength of 50 catalyst tablets was 5.1 Kg before the start of the reaction, and 5.1 Kg 1000 hours after the start of the reaction. That is, it was confirmed that the crush strength of the catalyst tablets did not change at all, even though the tablets were continuously used for a long period of time. Example 12 By using the same catalyst (Mol0Co8Fe2BilCs0 lPdo 5) as that mentioned in Example 10, the same contacting procedures as those described in Example 1 were continuously carried out for 1000 hours. After 1000 hours had elapsed from the start of carrying out the contacting procedures, the percent conversion of tert-butyl alcohol was 100%, the percent yield of methacrolein was 85.5% and the percent yield of methacrylic acid was 2.2% which were similar to those described in Example 10. Example 13 In 200 ml of warm water maintained at a temperature of 400C, 141.3 g of ammonium molybdate [{NH4)6Mo7O24.4H2O] and 0.78 g of ammonium metavanadate [NH4VO3] were dissolved and 6.39 g of titanium dioxide were suspended. A mixture of a solution of 38.8 g of bismuth nitrate [Bi(NO3) 3 5H2O]in 50 ml of a 15% nitric acid aqueous solution and a solution of 64.6 g of ferric nitrate [Fe(NO3) DH2O] , 0.078 g of cesium nitrate [CsNO3] and 186.2 g of cobalt nitrate [Co(NO3)2 6H20] in 200 ml of warm water maintained at a temperature of 40 C, was admixed dropwise into the thus-prepared aqueous solution suspension while the admixed solution was being stirred. The admixed aqueous slurry was initially dried at a temperature of 1200C by using a drum dryer, and then the first dried product was dried for -a second time at a temperature of 2000C for 10 hours by using an oven. The second dried product was shaped into tablets each having a diameter of 5 mm and a length of 3 mm by using a tablet -forming machine. The resultant tablets were calcined in an air atmosphere at a temperature of 6500C for 5 hours. The resultant catalyst had an atomic ratio of Mo:Bi:Co:Fe:Cs:V:Ti = 12:1:8:2:0.005:0.1:1. The measured crush strength and resistance to attrition of the catalyst tablets are shown in Table 6. 10 ml of the catalyst tablets were placed in a U-shaped glass reaction tube having an inner diameter of 8 mm. A feed gas consisting of tert-butyl alcohol, air and steam in a molar ratio of 1:10:6 was passed through the reaction tube at a flow rate of 200 ml/min under such a condition that the contact of the feed gas with the catalyst was maintained for 3.0 seconds at a temperature of 3900C. The results of Example 13 are shown in Table 6. Examples 14 through 17 The same procedures as those described in Example 13 were carried out, except that the titanium dioxide was replaced by zirconium oxide in Example 14, by stannic oxide in Example 1-5, by a mixture of zirconium oxide and stannic oxide in Example 16 and by a mixture of titanium dioxide and stannic oxide in Example 17 respectively in the amounts shown in Table 6, and that, in only Example 15, the conversion of tert-butyl alcohol was carried out at a temperature of 3700C. The obtained catalysts had the compositional make-ups, the crush strength and the resistance to attrition as shown in Table 6. The results of the conversion of tert-butyl alcohol in the respective Examples 14 through 17 are shown in Table 6. Example 18 Procedures identical to those described in Example 13 were carried out, excerpt that no ammonium metavanadate was used and palladium nitrate was contained in the aqueous solution of ferric nitrate, cesium nitrate and cobalt nitrate. The resultant catalyst tablets had the compositional make-ups, the crush strength and the resistance to attrition as shown in Table 6. Also, the results of the catalytic conversion of tert-butyl alcohol are shown in Table 6. Examples 19 and 20 Procedures identical to those used in Example 18 were conducted, except that the titanium dioxide employed in Example 18 was replaced by zirconium oxide in Example 19, and by stannic oxide in Example 20 and that the resultant catalyst had the compositional make-ups, the crush strength and resistance to attrition as shown in Table 6. Also, the results of the catalytic conversion of tert-butyl alcohol are shown in Table 6. Examples 21 and 22 Procedures identical to those described in Example 13 were carried out, except that in both Examples 21 and 22, palladium nitrate was added to the aqueous solution of ferric nitrate, cesium nitrate and cobalt nitrate and the conversion of tert-butyl alcohol was conducted at a temperature of 370"C. Additionally, in Example 22, the titanium dioxide was replaced by stannic oxide The catalyst tablets prepared had the compositional make-ups, the crush strength and the resistance to attrition as shown in Table 6. The results of the conversions of tert-butyl alcohol in both Examples 21 and 22 are also shown in Table 6. Comparison Example 42 The same procedures as those carried out in Example 22 were effected, except that no ammonium metavanadate and no stannic oxide were used. The properties of the resultant catalyst and the results of the conversion of tert-butyl alcohol in the presence of the catalyst are indicated in Table 6. Table 6 Composition of catalyst Resistance Conversion of Yield of Yield of Sum of(*)1 Example (Atomic ratio) Crush strength to attrition tert-butyl methacrolein methacrylic yields No alcohol acid Mo Co Fe Bi Cs X Y (Kg/tablets) (wt %) (%) (%) (%) (%) 13 12 8 2 1 0.005 V=0.1 Ti=1 6.6 0.02 100 86.7 2.9 89.6 14 10 8 2 1 0.01 V=0.1 Zr=1 6.7 0.02 100 85.4 2.7 88.1 15 10 8 3 1 0.005 V=0.2 Sn=2 6.2 0.04 100 85.3 2.7 88.0 Zr=1 16 10 8 2 1 0.01 V=0.1 Sn=1 6.5 0.03 100 86.5 2.4 88.9 Ti=1 Example 17 10 8 2 1 0.01 V=0.2 Sn=1 6.7 0.02 100 85.0 2.6 87.6 18 10 8 2 2 0.05 Pd=0.1 Ti=1 7.1 0.02 100 86.0 2.6 88.6 19 10 8 3 2 0.01 Pd=0.2 Zr=2 6.5 0.02 100 86.1 2.5 88.6 20 10 8 2 1 0.01 Pd=0.2 Sn=2 7.0 0.02 100 85.3 2.3 87.6 V=0.1 21 10 8 2 1 0.01 Pd=0.1 Ti=1 6.0 0.02 100 85.2 2.8 88.0 V=0.1 22 10 8 2 0.5 0.01 Pd=0.1 Sn=2 7.2 0.04 100 86.7 2.6 89.3 Comparison 42 10 8 2 0.5 0.01 Pd=0.1 0 5.3 0.30 100 82.9 2.3 85.2 Example Comparison Examples 43 through 48 In each of the Comparison Example 43 through 48, the same procedures as those described in Example 13 were carried out with the following exceptions. (1) The resultant catalyst in each Comparison example had the compositional make-up indicated in Table 7. (2) In Comparison Example 44, the contacting temperature was 3700C. The results are indicated in Table 7. Table 7 Compar- Composition of catalyst Conversion of Yield of Yield of Sum of(*)1 ison (Atomic ratio) tert-butyl methacrolein methacrylic yields Example alcohol acid No Mo Co Fe Bi Alkali metal X Y (%) (%) (%) (%) 43 10 8 3 1 0 0 Ti=2 100 60.3 2.4 62.7 44 10 8 2 1 0 V=0.5 Sn=1 100 67.5 2.0 69.5 45 10 8 3 1 0 Pd=0.1 Zr=1 100 78.3 2.1 70.4 46 10 8 2 2 0 0 Zr=3 100 67.2 2.3 69.5 47 10 8 2 2 Cs=0.1 V=0.1 Ti=7 100 61.9 2.5 64.4 48 10 8 2 1 0 0 Ti=1 100 76.5 2.2 78.7

Claims: CLAIMS 1. A process for producing methacrolein and methacrylic acid by the catalytic oxidation of tert-butyl alcohol, comprising bringing a feed gas containing tert-butyl alcohol and molecular oxygen into contact with a catalyst at a elevated temperature, which process is characterized in that said catalyst comprises an oxide composition of the empirical formula (1): : Mo Co Fe Bi Cs X Y O a b c d e f g h wherein Mo represents a molybdenum atom, Co represents a cobalt atom, Fe represents an iron atom, Bi represents a bismuth atom, Cs represents a cesium atom, X represents at least one member selected from the group consisting of vanadium and palladium atoms, Y represents at least one member selected from the group consisting of titanium, tin and zirconium atoms, 0 represents an oxygen atom, the subscripts a through g respectively represent a positive number corresponding to the number of respective metal atoms, wherein when a=12, b through g fall respectively within the following ranges: b=2 to 12, C=0.5 to 7, d=0.1 to 5, e=0.0005 to 0.5, f=0.01 to 2 and g=O to 5, and the subscript h represents a positive number corresponding to the number of oxygen atoms satisfying the average valency of the respective metal atoms. 2. A process as claimed in claim 1, wherein the contact of said feed gas with said catalyst is carried out at a temperature of from 250 to 5000C. 3. A process as claimed in either of claims 1 and 2, wherein the contact time is in a range of from 0.3 to 20 seconds. 4. A process as claimed in any one of claims 1 through 3, wherein said catalyst is combined with a carrier consisting of at least one member selected from the group consisting of silica, alumina, alumina-silica, titania, diatomaceous earth and carborundum. 5. A process as claimed in any one of claims 1 through 4, wherein said feed gas contains at least one dilute gas selected from the group consisting of steam, nitrogen, carbon dioxide, n-butane, isobutane and propane. 6. A process as claimed in any one of claims 1 through 5, wherein said feed gas contains 0.05 to 10 moles of steam per mole of tert-butyl alcohol. 7. A process as claimed in any one of claims 1 through 6, wherein the amount of said molecular oxygen in said feed gas is in a range of from 0.4 to 5 moles per mole of tert-butyl alcohol. 8. A process as claimed in any one of claims 1 through 7, wherein said catalyst is one prepared by uniformly mixing, in an aqueous medium, respective metal-containing compounds in the form of an oxide, salt or a mixture of said oxide and salt, by drying said mixture at a temperature not exceeding 3000C, by shaping said dried mixture, and by calcining said shaped mixture at a temperature of from 550 to 8000C. 9. A process as claimed in claim 8, wherein said drying operation is effected in two steps, in the first step of which, said mixture is heated at a temperature of from 100 to 1500C and in the second step of which, said first dried mixture is heated at a temperature of from 150 to 3000C. 10. A process as claimed in claim 1, wherein in the empirical formula (1), the values of said subscripts b through g are respectively in the ranges of: b=4 to 10, c=l to 5, d=0.5 to 4, e=0.001 to 0.3, f=0.05 to 1.5 and g=0.1 to 5.

Inventors: OHDAN, KYOJI C/O CHUOKENKYOSHO, SUZUKI, KENICHI C/O CHUOKENKYUSHO, YAMAO, TAKESHI C/O CHUOKENKYUSHO
Applicants: UBE INDUSTRIES, LTD.
Application year: 1982
Main classification: C07C47
IPC codes: C07C45, B01J23, C07C51