THICKENED AQUEOUS ACID SOLUTIONS, AND THEIR USE, ESPECIALLY FOR DESCALING

Abstract: 1. Thickened aqueous acid solutions having an acid concentration by weight lower than, or equal to, 30%, a pH lower than, or equal to 2, and presenting a viscosity higher than 1 millipascal per second as determined at 20 degrees C with a Brookfield viscosimeter, model RVT, equipped with a suitable shaft rotating at the speed of 50 rotations per minute, stable in time, characterised in that they are thickened by the hydrochloric acid salified dimethylaminoethyl methacrylate homopolymer having an intrinsic viscosity of between 4 and 6 dl/g, as determined in a NaCl molar solution at 20 degrees C.

Description: "Solutions aqueuses acides épaissies et leur application notamment pour le détartrage11. La présente invention concerne des solutions aqueuses acides épaissies et leur application, notamment pour le détartrage. Des solutions aqueuses d'acide (s) minéral (aux) telles que des solutions aqueuses d'acide chlorhydrique sont utilisées depuis longtemps pour le détartrage ménager, particulièrement pour le détartrage des appareils sanitaires ainsi que dans la récupération assistée du pétrole lors de certaines opérations d'acidification et de fracturation de formations souterraines pétrolifères. Ces solutions aqueuses acides fluides présentant une viscosité sensiblement égale à celle de l'eau étaient dangereuses a manipuler et conve naient médiocrement pour ces applications, aussi ont-elles été progressivement remplacées soit par des produits solides, -en poudre ou en -granulés, soit par des compositions épaissies d'acide (s) minéral (aux) ou organique (s) protoniques. Pour ce faire, divers agents épaississants insensibles aux acides ont été préconisés tels que des amines grasses éthoxylées selon les brevets français n0 2207 984 et 2415 139, des dérivés du silicium comme par exemple la palygorskite ou la sépiolite selon la demande de brevet japonais n0 Kokai 78-139606, des polymères anioniques possédant des groupe ments sulfo comme par exemple le sel d'ammonium d'un acide -sulfo ov-octadecyloxypoly (oxy-1,2 éthylène) selon la .demande de brevet japonais n0 Kokai 76-35681 ou des homopo lymères de l'acide acrylamido-2 méthyl-2 méthyl-2 propane sulfonique selon le brevet des Etats-Unis d'Amerique n0 3931089. Mais ces divers épaississants présentent encore un certain nombre d'inconvénients. Ainsi, les amines grasses éthoxylées utilisées dans les brevets français n0 2207984 et 2415139 sont fréquemment difficiles à disperser dans ces milieux acides et elles nécessitent souvent un effort consi dérable de mélange et/ou d'agitation pour développer leur pleine efficacité. Les dérivés du silicium tels que la palygorskite ou la sépiolite sont connus comme susceptible de libérer lentement de la silice gélatineuse lorsqu'ils sont utilisés sous certaines conditions de températures et de pH acide.Les polymères anioniques possédant dans leur structure un ou plusieurs groupements sulfo, libres ou salifies, sont des produits onéreux et ils présentent très souvent une incompatibilité avec les bactéricides de type ammonium quaternaire utilisés pour la conservation des solutions aqueuses acides épaissies. Les polymères cationiques-hydrosolubles dérivés d'esters de l'acide (méth) acrylique sont des agents épaississants connus, mais ils étaient reconnus inaptes a l'épaississement de solutions aqueuses acides présentant un pH inférieur ou égal a 2, vraisemblablement du fait de leur dégradation par hydrolyse dans ces milieux. Ces polymères cationiques hydrosolubles abondamment répandus dans le commerce pour leur utilisation dans le traitement des eaux sont disponibles et nettement moins onéreux que les poly mères anioniques précédemment cités. De plus, ils ne présentent aucune incompatibilité avec les bactéricides de type ammonium quaternaire. Or, la Demanderesse a trouvé d'une manière tout a fait inattendue et ce , contrairement à tous les enseigne ments admis, de nouvelles solutions aqueuses acides épaissies, de concentration pondérale en acide (s) infé rieure ou égale à 30 %, de pH inférieur ou égal à 2, présentant une viscosité supérieure à 1 centipoise, deter minée a 200 C avec un viscosimètre de Brookfield, modèle RVT, équipé d'un axe convenable tournant à la vitesse de 50 tours par minute, caractérisées par le fait qu'elles sont épaissies par l'homopolymère du méthacrylate de dimé thylaminoéthyle salifié par l'acide chlorhydrique. Généra lement, ces solutions aqueuses acides épaissies sont des solutions fluides, présentant une viscosité comprise entre 20 et 2.500 centipoises et avantageusement comprise entre 40 et 2.500 centipoises déterminée selon les conditions précédemment citées. Selon l'invention, ces nouvelles solutions aqueuses acides épaissies sont notamment des solutions aqueuses d'acide (s) minéral (aux) ou organique (s) tels que l'acide chlorhydrique, l'acide sulfurique, l'acide fluorhydrique, l'acide orthophosphorique, l'acide sulfamique, l'acide formique, l'acide acétique, l'acide oxalique, l'acide citrique, l'acide tartrique, l'acide succinique, l'acide malique, l'hydrogénosulfate de sodium, l'hydrogénodifluorure d'ammonium, etc. ou des mélange de ces acides. La concentration en acide ou en mélange d'acides dans ces solutions aqueuses épaissies est inférieure ou égale à 30 % en poids et elle est telle que le pH résultant est inférieur ou égal à 2. L'homopolymère du méthacrylate de diméthylaminoéthyle salifié par l'acide chlorhydrique sera désigné par la suite homopolymère CHM. De préférence l'homopolymère appliqué selon l'invention aura une viscosité intrinsèque comprise entre 4 et 6 dl/g déterminée en solution molaire de NaCl à 250C. Selon l'invention, les concentrations en homopolymère CHM dans les solutions aqueuses acides épaissies sont fonction de la viscosité désirée. Il est aisé de déterminer par quelques essais préliminaires les quantités nécessaires d'homopolymère CHM pour obtenir la viscosité# choisie. Ainsi, pour obtenir des solutions aqueuses acides épaissies, fluides, présentant une viscosité inférieure à 2500 centipoises, déterminée à 200C avec un viscosimètre de Brookfield, modèle RVT, équipé d'un axe convenable, tournant à 50 tours par minute, il est nécessaire d'utiliser, au maximum, 4 g d'homopolymère CHM pur pour 100 g de solution aqueuse 'acide ; mais, il est possible d'obtenir des solutions aqueuses acides gélifiées, possédant des viscosités nettement plus élevées, pouvant atteindre 20 000 centipoises, en utilisant des quantités plus importantes d'homopolymère CHM. Les solutions aqueuses acides épaissies, selon l'invention, présentent une viscosité stable dans le temps, indépendante du pH, de la nature de l'acide, et de la tem pérature dans une gamme de températures de stockage et d'utilisation habituelles des solutions aqueuses acides épaissies. Ces propriétés sont d'autant plus étonnantes qu'il est connu que les polymères cationiques hydrosolubles a base d'esters de l'acide méthacrylique sont sensibles à l'hydrolyse acide. Les viscosités des solutions acides épaissies, selon l'invention, sont sensibles à la présence éventuelle d'électrolyte (s) dissous, notamment a la présence de chlorure de sodium. La présence de chlorure de sodium dissous dans ces solutions aqueuses acides épaissies abaisse légère- -ment leur viscosité et leur stabilité dans le temps mais augmente leur limpidité. Pour certaines applications, telles que leur emploi dans la récupération assistée du pétrole, cette propriété est intéressante puisqu'au fur et à mesure que ces solutions se chargent en sels minéraux dissous au cours de leur progression dans le terrain, leur fluidité augmente, facilitant ainsi leur diffusion dans les fissures. Ces solutions aqueuses acides épaissies présen tant, simultanément un pH inférieur ou égal a 2 et une concentration pondérale en acide (s) inférieure a 30 %, sont -aisément obtenues en mélangeant à la température ambiante, sous agitation en dix minutes environ, une solution aqueuse acide contenant la quantité nécessaire d'acide ou du mélange d'acides désirés avec une solution aqueuse contenant la quantité calculée d'homopolymère CHM et éventuellement du -chlorure de sodium et/ou d'autres additifs nécessaires a leur formulation. Les additifs éventuels nécessaires a la formu lation sont, par exemple, des colorants, des parfums, des désinfectants, etc. La présente invention a également pour objet une application industrielle de ces nouvelles solutions aqueuses acides épaissies. Grâce à leur pH inférieur ou égal à 2, à leur stabilité dans le temps, à leur insensibilité a des températures pouvant atteindre 80 C, à leur limpidité et à leur viscosité élevée, habituellement comprise entre 40 et 2500 centipoises déter- minée selon les conditions précédemment citées, ces solu tions aqueuses acides épaissies, selon l'invention, conviennuent particulièrement bien au détartrage industriel ou ménager et aux opérations d'acidifications et de fractura tions de formations souterraines contenant du pétrole. Ces propriétés sont dues a leur bonne adhérence aux surfaces verticales améliorant leurs temps de contact donc leur -efficacité, à leur acidité élevée et à leur sécurité d'emploi par diminution des risques de projection. Exemples Les tableaux suivants indiquent les viscosités obtenues, exprimées en centipoises (cP) et déterminées selon les conditions citées précédemment, de différentes solutions aqueuses acides épaissies objet de la présente invention avec diverses concentrations en homopolymère CHM, en présence ou non de chlorure de sodium. Ces tableaux mentionnent aussi des viscosités de ces solutions après une durée de stockage variable a différentes températures comprises entre 0 et 600C. L'homopolymère CHM mentionné dans les tableaux 1 à 3 et 7 à 11 était un homopolymère présentant une visco sité intrinsèque de 4,75 dl/g déterminée en solution molaire de NaCl à 25oC, alors que celui des tableaux 4, 5 et 6 présentait une viscosité intrinsèque de 5,25 dl/g. 10 - Solutions aqueuses d'acide chlorhydrique à 2 % en poids EMI6.1 <tb> <SEP> Tableau <SEP> 1 <SEP> Viscosités <SEP> (cP) <tb> <SEP> mopolymère <SEP> CHM <tb> <SEP> en <SEP> g <SEP> pour <tb> <SEP> 100 <SEP> #100g <SEP> :1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> Durées <SEP> i---# <SEP> --------Températu <tb> <SEP> o <SEP> 1 <SEP> -20 C <SEP> 90 <SEP> 610 <SEP> j <SEP> 1600 <tb> <SEP> a <SEP> OOC <SEP> 90 <SEP> 620 <SEP> 1590 <tb> <SEP> 114 <SEP> a <SEP> 200C <SEP> 90 <SEP> 610 <SEP> 1580 <tb> <SEP> jours <SEP> a <SEP> 400C <SEP> 90 <SEP> 590 <SEP> 1560 <tb> I <tb> <SEP> Aspect <SEP> limpide <SEP> très <SEP> légère- <SEP> très <SEP> Iégere <tb> <SEP> ment <SEP> trouble <SEP> ment <SEP> trouble <tb> 20 - Solutions aqueuses d'acide chlorhydrique a 10 % en poids EMI6.2 <tb> <SEP> Tableau <SEP> 2 <SEP> Viscosit#s <SEP> (cP) <tb> <SEP> # <SEP> CHM <tb> <SEP> Dur <SEP> ymère <tb> <SEP> en <SEP> g <SEP> pour <SEP> 100 <SEP> g <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> Durees <SEP> <tb> <SEP> Températures <tb> <SEP> 0 <SEP> 200C <SEP> 110 <SEP> 530 <SEP> 1720 <tb> <SEP> 93 <SEP> OOC <SEP> 110 <SEP> 600 <SEP> 1720 <tb> <SEP> 93 <SEP> 200C <SEP> 100 <SEP> 500 <SEP> 1530 <tb> jours <SEP> 400C <SEP> 110 <SEP> 600 <SEP> 1770 <tb> <SEP> 600C <SEP> 100 <SEP> 500 <SEP> 1600 <tb> <SEP> Aspect <SEP> limpide <SEP> limpide <SEP> limpide <tb> 30 - Solutions aqueuses d'acide chlorhydrique à 25 % en poids EMI7.1 <tb> <SEP> Tableau <SEP> 3 <SEP> J <SEP> Viscosités <SEP> (cP) <tb> omopolymère <SEP> CHM <tb> <SEP> pour <SEP> g <SEP> pour <tb> Durées <SEP> Températures <SEP> 1 <tb> <SEP> 0 <SEP> - <SEP> 200C <SEP> 160 <SEP> 160 <SEP> 860 <SEP> 2380 <tb> <SEP> 0 C <SEP> 180 <SEP> 740 <SEP> 2320 <tb> jours <SEP> 200C <SEP> 120 <SEP> 650 <SEP> 2130 <tb> <SEP> 400C <SEP> 100 <SEP> 540 <SEP> 1880 <tb> <SEP> Aspect <SEP> légèrement <SEP> légèrement <SEP> légèrement <tb> <SEP> trouble <SEP> trouble <SEP> trouble <tb> 40 - Solutions aqueuses d'acide sulfurique à 2 % en poids EMI7.2 <tb> <SEP> Tableau <SEP> 4 <SEP> Viscosités <SEP> (cP) <tb> <SEP> ym#re <tb> <SEP> CHM <SEP> en <SEP> g <tb> Durées <SEP> Températures <tb> <SEP> 0 <SEP> 1 <SEP> 200C <SEP> ss <SEP> 100 <SEP> 1 <SEP> 610 <SEP> 1 <SEP> 1860 <tb> <SEP> 114 <SEP> OOC <SEP> 100 <SEP> 610 <SEP> 1860 <tb> <SEP> jours <SEP> 200C <SEP> 100 <SEP> 610 <SEP> 1840 <tb> <SEP> 400C <SEP> 100 <SEP> 590 <SEP> 1770 <tb> <SEP> 590 <SEP> 1770 <tb> <SEP> légèrement <SEP> légèrement <tb> <SEP> Aspect <SEP> limpide <SEP> trouble <SEP> trouble <tb> 50 - Solutions aqueuses d'acide sulfurique à 10 % en poids EMI8.1 <tb> <SEP> Tableau <SEP> 5 <SEP> | <SEP> Viscosités <SEP> (cP) <tb> <SEP> J <tb> <SEP> copolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> 100 <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> 9 <tb> <SEP> Durees <SEP> - <SEP> Températur <tb> <SEP> 93 <SEP> 0 C <SEP> 100 <SEP> 590 <SEP> 1570 <tb> jours <SEP> 200C <SEP> 110 <SEP> 590 <SEP> 1500 <tb> <SEP> 400C <SEP> 110 <SEP> 1 <SEP> 590 <SEP> 1480 <tb> <SEP> I <tb> <SEP> Aspect <SEP> limpide <SEP> limpide <SEP> limpide <tb> 6 - Solutions aqueuses d'acide sulfurique à 25 % en poids EMI8.2 <tb> <SEP> Tableau <SEP> 6 <SEP> | <SEP> Viscosités <SEP> (cP) <tb> <SEP> omopolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> ##o#o¯l <SEP> #¯¯ <SEP> 2,4 <SEP> 3,6 <tb> <SEP> 3uréez <tb> <SEP> 0 <SEP> 200C <SEP> 130 <SEP> 780 <SEP> 2360 <tb> <SEP> I <SEP> I <SEP> I <tb> <SEP> 0 C <SEP> 150 <SEP> 820 <SEP> 2440 <tb> <SEP> 110 <SEP> 20 > C <SEP> 150 <SEP> 720 <SEP> 2230 <tb> jours <SEP> 400C <SEP> 130 <SEP> 740 <SEP> 2220 <tb> <SEP> ¯ <SEP> ¯ <SEP> ¯ <SEP> .. <SEP> . <tb> <SEP> Aspect <SEP> légèrement <SEP> légèrement <SEP> légèrement <tb> <SEP> laiteux <SEP> laiteux <SEP> laiteux <tb> tic - Solutions aqueuses d'acide chlorhydrique a 2 % en poids et contenant du chlorure de sodium EMI9.1 <tb> <SEP> Tableau <SEP> 7 <SEP> I <SEP> Viscosités <SEP> (cP) <tb> omopolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> our <SEP> 100 <SEP> g <tb> <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> Cîlia <SEP> en <SEP> g <SEP> pour <tb> <SEP> 100 <SEP> 100 <SEP> g <SEP> 0,6 <SEP> 1 <SEP> 1,2 <SEP> 1,8 <tb> Durées <SEP> Températures <tb> <SEP> o <SEP> 200C <SEP> 50 <SEP> 176 <SEP> 450 <tb> <SEP> 0 C <SEP> 50 <SEP> 150 <SEP> 460 <tb> <SEP> 114 <SEP> 200C <SEP> 40 <SEP> 160 <SEP> 450 <tb> <SEP> jours <SEP> 400C <SEP> 40 <SEP> 160 <SEP> 440 <tb> <SEP> ¯ <tb> <SEP> Aspect <SEP> limpide <SEP> limpide <SEP> j <SEP> limpide <tb> <RTI ID=9.2> 80 - Solutions aqueuses d'acide chlorhydrique à 10 % en poids et contenant du chlorure de sodium EMI9.2 <tb> <SEP> Tableau <SEP> 8 <SEP> Viscosités <SEP> (cP) <tb> <SEP> Homopolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> pour <SEP> 100 <SEP> g <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> I <SEP> 1 <tb> <SEP> Na <SEP> en <SEP> g <SEP> pour <SEP> 100 <SEP> g <SEP> 0,6 <SEP> 1,2 <SEP> 1,8 <tb> urées <SEP> I <SEP> Températures <tb> <SEP> 0 <SEP> 200C <SEP> 50 <SEP> 200 <SEP> 560 <tb> <SEP> 0 C <SEP> 50 <SEP> 200 <SEP> 560 <tb> <SEP> 88 <SEP> 200C <SEP> 50 <SEP> 210 <SEP> 470 <tb> <SEP> ours <SEP> 400C <SEP> 50 <SEP> 210 <SEP> 530 <tb> <SEP> Aspect <SEP> limpide <SEP> limpide <SEP> 1limpide <tb> 90 - Solutions aqueuses d'acide sulfurique a 2 % en poids et contenant du chlorure de sodium EMI10.1 <tb> <SEP> Tableau <SEP> 9 <SEP> Viscosités <SEP> (cP) <tb> mopolymêre <SEP> CHM <SEP> en <SEP> g <tb> <SEP> our <SEP> 100 <SEP> g <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> CiNa <SEP> en <SEP> g <SEP> pour <SEP> 100 <SEP> 9 <SEP> 0,6 <SEP> 1,2 <SEP> |- <SEP> 18 <tb> urées <SEP> Températures <SEP> -# <tb> <SEP> 0 <SEP> 1 <SEP> 200C <SEP> 50 <SEP> 190 <SEP> 510 <tb> <SEP> 0 C <SEP> 50 <SEP> 190 <SEP> 510 <tb> <SEP> jours <SEP> 200C <SEP> 45 <SEP> 190 <SEP> 500 <tb> <SEP> 400C <SEP> 50 <SEP> 200 <SEP> 500 <tb> <SEP> Aspect <SEP> Limpide <SEP> Limpide <SEP> | <SEP> Limpide <tb> 100 - Solutions aqueuses d'acide sulfurique a 10 % en poids et contenant du chlorure de sodium EMI10.2 <tb> <SEP> Tableau <SEP> 10 <SEP> Viscosités <SEP> (cP) <tb> <SEP> Homopolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> our <SEP> 100 <SEP> g <SEP> 1,2 <SEP> 2,4 <SEP> 3,6 <tb> <SEP> X <tb> lNaengpour <SEP> 100 <SEP> g <SEP> 0,6 <SEP> 1,2 <SEP> 2,8 <tb> Durées <SEP> Températures <tb> <SEP> 0 <SEP> 200C <SEP> t <SEP> 50 <SEP> 1 <SEP> 200 <SEP> 1 <SEP> 540 <tb> <SEP> OOC <SEP> 50 <SEP> 210 <SEP> 550 <tb> <SEP> 88 <SEP> 200C <SEP> 50 <SEP> 200 <SEP> 470 <tb> jours <SEP> 20 C <SEP> 50 <SEP> 210 <SEP> 530 <tb> <SEP> 40 C <SEP> 50 <SEP> 210 <SEP> 530 <tb> <SEP> Aspect <SEP> limpide <SEP> limpide <SEP> |limpide <SEP> |limpide <tb> 110 - Solutions aqueuses d'acide sulfurique a 25 % en poids et contenant du chlorure de sodium EMI11.1 <tb> <SEP> Tableau <SEP> 11 <SEP> Viscosités <SEP> (cP) <tb> <SEP> omopolymère <SEP> CHM <SEP> en <SEP> g <tb> <SEP> Out <SEP> 100 <SEP> g <SEP> 1,2 <SEP> 1,8 <SEP> 3,6 <tb> <SEP> Sour <SEP> en <SEP> g <SEP> pour <SEP> 100 <SEP> g <tb> Durées <tb> <SEP> o <SEP> 1 <SEP> 20 C <SEP> 1 <SEP> 70 <SEP> 310 <SEP> 785 <tb> <SEP> 00± <SEP> 70 <SEP> 300 <SEP> 760 <tb> <SEP> 110 <SEP> - <SEP> 0 C <SEP> 90 <SEP> 310 <SEP> 780 <tb> <SEP> . <SEP> 20 C <SEP> 90 <SEP> 310 <SEP> 780 <tb> <SEP> jours <SEP> 40 C <SEP> 60 <SEP> 300 <SEP> 730 <tb> <SEP> Ipect <tb> <SEP> Aspect <SEP> limpide <tb> Il va de soi que la présente invention nta été décrite qu'a titre purement explicatif et nullement limitatif et que toute modification utile pourra y être apportée sans sortir de son cadre tel que défini dans les revendications ci-après.

Claims: REVENDICATIONS 1. Solutions aqueuses acides épaissies, de concentration pondérale en acide (s) inférieure ou égale à 30 %, de pH inférieur ou égal à 2, présentant une viscosité supérieure à 1 centipoise déterminée à 200C avec un viscosimètre de Brookfield, modèle RVT, équipé d'un axe convenable tournant à la vitesse de 50 tours par minute} stables dans le temps, caractérisées par le fait qu'elles sont épaissies par l'homopolymère du méthacrylate de diméthylaminoéthyle salifié par 11 acide chlorhydrique présentant une viscosité intrinsèque comprise çntre 4 et 6 dl/g déterminée en solution molaire de NaCl à 250C. 2. Solutions aqueuses acides épaissies selon la revendication 1 présentant une viscosité inférieure à 2500 centipoises déterminée à 200C avec un viscosimètre de Brookfield, modèle RVT, équipé d'un axe convenable tournant à la vitesse de 50 tours par minute caractérisées par le fait qu'elles contiennent une quantité inférieure ou égale à 4 g dudit homopolymère du méthacrylate de diméthylaminoéthyle salifié par l'acide chlorhydrique pour 100 g de solution. 3. Solutions aqueuses acides épaissies selon la revendication 1 ou 2; caractérisées par le fait qu'elles contiennent, seul ou en mélange, un acide protonique minéral ou organique. 4. Solutions aqueuses acides épaissies selon la revendication 3, caractérisées par le fait que l'acide minéral est choisi parmi les suivants : acide chlorhydrique, acide orthophosphorique, acide sulfurique, acide fluorhydrique, hydrogénosulfate de sodium, acide sulfamique, hydrogénodifluorure d'ammonium. 5. Solutions aqueuses acides épaissies selon la revendication 3, caractérisées par le fait que l'acide organique est choisi parmi les acides suivants : acide oxalique, acide tartrique, acide malique, acide citrique, acide formique, acide acétique, acide succinique. 6. - Solutions aqueuses acides épaissies selon l'une quelconque des revendications 1 à 5, caractérisées par le fait qu'elles contiennent en outre au moins un sel minéral. 7. - Solutions aqueuses acides épaissies selon l'une quelconque des revendications 1 à 6, caractérisées par le fait qu'elles peuvent renfermer d'autres additifs nécessaires à leur formulation tels que des colorants, des-parfums, des désinfectants et autres additifs connus. 8. - Application des solutions aqueuses acides épaissies selon l'une quelconque des revendications 1 à 7 au détartrage industriel ou ménager.

Inventors: SIEGEL, DANIEL, SOREAU, MICHEL
Applicants: SOCIETE FRANCAISE HOECHST SOCIETE ANONYME DITE:
Application year: 1982
Main classification: C02F5
IPC codes: C09K8, C02F5