PRODUCTION OF MAGNETIC RECORDING CARDS

Abstract: A magnetic transfer sheet (3b) comprising a temporary support (5) and a magnetic recording layer (9b) or piece of island form left on the temporary support by partial die cutting and removal of superfluous parts is obtained. By transferring the magnetic recording layer of this magnetic transfer sheet onto a plastic card substrate (10) and heating and pressing the same, a magnetic card is obtained. The magnetic recording layer of the magnetic card thus obtained is imbedded in the island form with smooth and fair periph­ eral edges in the substrate, whereby it does not impart an impression that it is a magnetic recording layer, and the entire magnetic card has an aesthetically beautiful ap­ pearance.

Description: PRODUCTION OF MAGNETIC RECORDING CARDS BACKGROUND OF THE INVENTION This invention relates to a magnetic recording card and a process for producing the same and more specifically to a magnetic plastic card suitable for use as credit cards, bank cards,ID cards, and the like and to a process for producing the same. In general, a magnetic plastic card comprises an opaque core sheet made of a synthetic resin such as polyvinyl chloride and transparent oversheets similarly made of polyvinyl chloride or like resin and covering the surfaces of "the core sheet and! mdreover, has a magnetic recording layer,' for memorizing or storing neces- - sary information. -This magnetic recording layer is provided on an oversheet, and a marking such as an inscription or a picture as visible information is printed on the core sheet. Thus, in a conventional magnetic plastic card, the magnetic recording layer and the visible marking are provided¯in.a. mutually independent state. Moreover, the color of the magnetic recording layer is generally limited to brown or dark brown. For these reasons and further for the reason that the magnetic recording layer is provided on the oversheet, when a visible marking is provided on the core sheet under the magnetic recording layer, it is concealed by the magnetic recording layer, whereby the possible designs of magnetic plastic cards have, been greatly limited. Furthermore, in the case where a magnetic recording layer is provided over a visible marking, the existence of the magnetic recording layer is emphasized, and, as a consequence, the design effect of the visible marking provided in the card tends to be easily lost. For this reason, there have been instances wherein it was necessary to revise the visible marking of a card created by the card issuer to harmonize with the magnetic recording layer. Concealment of the brown color or the dark brown color of the magnetic recording layer and coloring of this layer with a bright hue are being practiced, but the concealment by the magnetic recording layer of the visible marking printed on the core sheet remains unchanged. Furthermore, a method of forming a magnetic recording layer on a card which is also being practiced comprises transferring, by using a hot die of a desired shape, a magnetic recording layer on a temporary support in a planar shape corresponding to the die shape onto a card substrate by a hot-stamping technique. However, a magnetic recording layer stock (tape), in comparison with a pigment foil or metal foil used in a hot-stamping process, ordinarily is thicker and also has a higher strength. For this reason, such a magnetic recording layer stock cannot be sheared cleanly during stamping, whereby the edges of the magnetic recording layer transferred onto the card substrate are ragged and fuzzy. As a consequence, a magnetic card thus formed by hot stamping acquires a poor external appearance in which, particularly, the impression that the magnetic recording. layer has been pasted on becomes accentuated. SUMMARY OF THE INVENTION It is an object of this invention to provide a process for producing magnetic recording cards (hereinafter referred to as magnetic cards) which process has a step in which the magnetic recording layer of each card is transferred in a state wherein it is not conspicuous was such in external appearance onto a card substrate, whereby the entire magnetic card has an excelient aesthetic quality and to provide magnetic cards produced by this process. With this object in view, we have carried out studies as a result of which we have discovered that the causes of the deleterious effect of the magnetic recording layer of a magnetic card obtained by the conventional process on the aesthetic appearance of that card are as follows. a) In general, the color of the magnetic recording layer is brown or dark brown and is in strong contrast with the background color of an ordinary card substrate or a design or pattern. b) A stripe-form magnetic recording layer which is customarily used appeals - to a viewer as a magnetic recording layer because of its shape and destroys the harmony with another design or pattern.¯ c) In the case where a magnetic recording layer of "island" form is provided in order to avoid the above difficulty b), the edges of the magnetic recording layer become ragged because of limitation of the fabrication process. d) The surfaces of the magnetic recording layer and the card substrate do not lie-flush¯in one plane and are nowt level. As a result of our further research, we have found that, if it.is.possible to overcome the above difficulties c) and d) by improving the production process and to imbed a magnetic recording layer of island form with smooth, fair-line edges in a card substrate so that the upper surfaces of both lie flush in the same plane, the magnetic recording layer itself can be utilized as one kind of pattern harmonizing with the surrounding design, and, additionally, to solve the problems of a) and b) above. We have found further that, for overcoming the difficulties of c) and d) above, the combination of the steps of carrying out a limited-depth or partial die cutting of a magnetic recording layer stock of a magnetic transfer sheet comprising a temporary support and a magnetic recording layer stock formed uniformly on the temporary support, removing the unnecessary parts thereby to form beforehand on the temporary support a magnetic recording layer of a desired shape having smooth, fair-line edges, then transferring this magnetic recording layer onto a card substrate, and imbedding this layer in the card substrate is very effective. That is, the above mentioned partial diecutting step not only produces smoother and fairer edges than the conventional hot-stamping step but also can produce a magnetic recording layer shape of greater fineness, whereby the magnetic recording layer itself can be effectively utilized as a design pattern. In seeking to achieve the aforestated object, this invention is based on the above described findings and is embodied in the following four fundamental modes of practice and in the magnetic cards produced thereby. In a first fundamental mode of practice of the invention there is provided a process for producing magnetic cards which comprises: a first step of forming a magnetic transfer sheet by making a partial die cut of a closed figure in only the magnetic recording layer stock of a magnetic transfer sheet comprising a temporary support and the magnetic recording layer stock to be transferred laminated on the temporary support and thereafter peeling off and removing, from the temporary support, parts of the magnetic recording layer stock outside of the region encompassed by said closed-figure partial die cut thereby to cause a magnetic recording' - layer of island form of said region to be left on the temporary support; ; a second step of transferring the magnetic recording layer of island form onto a card substrate by placing the surface of the magnetic recording layer of the magnetic transfer sheet thus formed against the surface of the card substrate and heating the magnetic recording layer; and a third step of imbedding the magnetic recording layer by placing a press plate withva mirror#finished surface on the magnetic recording- layer thus transferred and heating and pressing the same into the card substrate until the outer surface of the magnetic recording layer lies flush in the same plane as that of the card substrate. According to this invention in a second-fundamental mode of practice thereof, there is provided a process for producing magnetic cards comprising the three steps of the above described first fundamental mode of practice and further comprising a fourth step of printing a printed layer of characters and design on the outer surface of the magnetic recording layer of the structure obtained after the third step of imbedding the magnetic recording layer and a fifth step of leveling the card surface by placing, after the fourth printing step, a press plate with a mirror-finished surface against the printed layer thus printed and heating and pressing the printed layer-thereby to cause the outer surfaces of the printed layer and the card substrate to lie flush in the same plane. According to this invention in a third fundamental mode of practice thereof, there is provided a process for producing magnetic cards which comprises the first step of the above described process embodying the first fundamental mode of practice to form the magnetic transfer sheet having the magnetic recording layer of island form and further comprises: a second step of placing the outer surface of the magnetic recording layer of island form of the magnetic transfer sheet thus formed against a surface of an oversheet and, by heating, trans ferring the magnetic recording layer onto the oversheet; a third step of securing or tentatively securing by adhesion the oversheet to a core sheet; and a fourth step of imbedding the magnetic recording layer by placing a press plate with a mirror finished surface against the structure obtained by the third step and heating and pressing the same thereby to imbed the magnetic recording layer so that its outer surface lies flush in the same plane as that of the oversheet. According to this invention in a fourth fundamental mode of practice thereof, there is provided a process for producing magnetic cards which comprises the four steps of the above described process embodying the third fundamental mode of practice of the invention and further comprises a fifth step of printing a printed layer of characters and design on the outer surface of the magnetic recording layer of the structure obtained by the fourth step of imbedding the magnetic recording layer and a sixth step of leveling the card surface by placing, after the fifth printing step, a press plate with a mirror-finished surface against the oversheet and heating and pressing the same thereby to cause the outer surfaces of the printed layer and the oversheet to lie in the same plane. According to this invention in another aspect thereof, there are provided magnetic cards fabricated in accordance with above stated process of the invention. Each of these cards is provided on at least one surface of a card substrate with a magnetic recording layer of island form formed by die cutting and having smooth, fair-line edges. Moreover, a feature of the magnetic,. card of the invention is that its magnetic recording layer is so imbedded that its outer surface lies flush in the same plane as the outer surface of the card substrate. The card substrate can comprise a core sheet and oversheets, as in the cards produced according to the above stated third and fourth fundamental modes of practice of the process of this invention. Furthermore, in the magnetic recording layer, a printed layer of characters and/or design pattern can be inscribed or imbedded so that its surface will lie flush in the same plane as that of the magnetic recording layer, as in the cards produced according to above stated second and fourth fundamental modes of practice of the process of the invention. The term "island form" as used herein designates a physical state wherein the magnetic recording layer is formed in a position separated from the peripheral edges of the magnetic card. The nature, utility, and further features of this invention will be more clearly apparent from the following detailed description beginning with' a consideration of a conventional process and of general aspects of this invention and concluding with specific examples of practice according to the invention when read in conjunction with the accompanying drawings, briefly described below. BRIEF DESCRIPTION OF THE DRAWINGS In the drawings, the views other than perspective views and bottom views are all elevational views in vertical section taken in planes parallel to the thickness direction of the layers shown and will be referred to as sections, the upper parts of these views corresponding to the upper or front faces of the magnetic cards. In the drawings: FIG. 1 is a perspective view of a known magnetic card; FIGS 2, 3, and 4a are sections of a magnetic card, indicating steps in a known process for hot stamping of the magnetic recording-layer; FIG 4b is a perspective view of a magnetic card fabricated by the steps indicated in FIGS. 2, 3, and 4a; ; FIGS 5 through 12 are views illustrating steps in the first fundamental mode of practice of the process of this invention, FIG. 5 being a section of one example of a magnetic transfer sheet, FIG. 6 being a bottom view of the magnetic transfer sheet after partial die cutting, FIG. 7 being a section taken along the line VII-VII in FIG. 6, FIG. 8 being a bottom view of the magnetic transfer sheet- after. removal of superfluous parts, FIG. 9 being a section taken along the line IX--IX in FIG. 8, FIGS 10, 11 and 12 being sections indicating the- steps of transfer and pressing while heating, FIG. 13 being a perspective view of the product magnetic card, and FIG. 14 being a section taken along the line XIV-XIV in FIG. 13; ; FIGS. 15 through 25 are sections respectively showing other examples of laminar construction of magnetic transfer sheets suitable for use in the process of the invention; FIGS. 26 through 36 are sections respectively showing the laminar structures of examples of product magnetic cards produced by using the magnetic transfer sheets of FIGS. 15 through 25 in accordance with the first and third fundamental modes of practice of the process of the invention; FIGS.37 through 40 are views indicating steps in the second fundamental mode of practice of the process of the invention, FIGS. 37 and 38 being sections indicating intermediate steps, FIG. 39 being a perspective view of the product magnetic card, and FIG. 40 being a section taken along the line XL-XL in FIG. 39; ; FIGS. 41 through 52 are sections of product magnetic cards produced by using the magnetic transfer sheets of FIGS. 15 through 25, respectively, according to the second and fourth fundamental modes of practice of the process of the invention; and FIGS. 53 through 56 are sections indicating intermediate steps in the third fundamental mode of practice of the process of:the 'invention. DETAILED DESCRIPTION OF THE-INVENTION As conducive to a full understanding of this invention, a typical example of a conventional magnetic card and a process for producing the same will first be described briefly with reference to FIGS. 1 through 4b. As stated hereinbefore, in thecase of a conventional magnetic card AA as shown in FIG. 1, an ordinary visible marking 1 on the card AA is concealed by a magnetic recording layer 2 of brown or dark brown color and the design effect is greatly impaired. FIGS. 2 through 4b indicate the steps of a typical example of the process for forming a planar (or laminar) magnetic recording structure or piece in "island" state by a conventional hot stamping method using a magnetic transfer sheet 3 and a heating head or hot die- 4; In this process, a magnetic transfer sheet 3 prepared by forming on a temporary support 5 a magnetic recording piece stock layer 9 comprising a separation-aiding or releasing layer 6, a colored layer 7, and a magnetizable layer 8 is superposed on a card substrate 10 so that the magnetizable layer 8 is adjacently contacting the substrate 10. Then, as shown in FIG. 2, a hot die 4 of a desired shape is pressed downward against this assembly of layers. Thereafter, the hot die 4 and the magnetic transfer sheet 3 are lifted off the substrate 10, whereupon a portion 9a of the magnetic recording piece stock layer 9 is transferred- in a shape corresponding to the hot die 4 onto' the card substrate 10 because of the adhesive strength of a binder within the magnetizable layer 8 by which it adheres to the substrate 10 as indicated in FIG. 3, the releasing layer 6 of this portion 9a separating away from the temporary support 5. Then, by means of a press plate of mirror finish, the magnetic recording layer 9a is heated and pressed and is thus forced to be imbedded in the card substrate 10, the upper surfaces of the layer 9a and the substrate becoming flush as indicated in FIGS. 4a and 4b, whereupon a magnetic card 3B is obtained. In this case, however, as mentioned hereinbefore, because of the high strength of the magnetic recording layer stock 9 due to its great thickness, the layer shearing at the time of the above described hot stamping is poor, whereby the edges of the magnetic recording piece or layer 9a thus formed (FIGS. 3 and 4) become ragged or fuzzy and not only impair the aesthetic appearance but also impart the impression that the magnetic recording layer has been pasted on the card substrate 10. The process for producing a magnetic card according to this invention will now be described with respect to a first example according to the first fundamental mode of practice thereof, with reference to FIGS. 5 through 14. First, as indicated in FIG. 5 in section taken in the thickness direction, a magnetic transfer sheet 3 in which a magnetic recording layer stock 9 comprising a releasing layer 6, a colored layer 7, and a magnetizable layer 8 is formed on a temporary support 5 is prepared. Then, as indicated in FIGS. 6 and 7, a partial or limiteddepth, die-cutting process step is carried out so as to cut the magnetic recording layer stock 9 but not to cut the temporary support 5 by means of a cutting die (not shown) of a desired shape thereby to form in the magnetic recording layer stock 9 a partial cut line 21 of a loop or closed figure corresponding to the desired island form. Then the surplus portion of the layer stock outside of the partial cut line 21 is cut away and removed and a magnetic transfer sheet 3b, as shown in FIGS. 8 and 9, in which a magnetic recording layer or piece 9b of island form is left remaining is formed. This transfer sheet 3a thus obtained is superposed, as indicated in FIG. 10, on the oversheet 12 of a card substrate 10 comprising a core sheet 11 and the oversheet 12 and is then heated by suitable heating means such as heating plates (not shown). Then, by peeling off the temporary support 5, the magnetic recording layer 9b of island form is transferred onto the oversheet 12 of the card substrate as indicated in FIG. 11. The magnetic recording layer 9b on the substrate 10 is then heated and pressed by press plates (not shown) having a mirror-finished surface thereby being imbedded in the card substrate 101, until the upper surfaces ö the magnetic recording-layer 9b and of the substrate 10 are flush, that is, lie in the same plane, as indicated in FIG. 12. By cutting the structure of FIG. 12 thus obtained along the planes indicated by lines C - C, one example CC of a magnetic card of this invention, as shown in FIGS. 13 and 14, is obtained. FIGS. 12 and 14 are sections respectively corresponding to views in the directions of lines D-D and E-E in FIG. 13. A feature of a magnetic card produced in the above described manner according to this invention is that the edges of its magnetic recording layer 9b are very smooth, fair, and definite in com- parison with those of the -aforedescribed conventional card. The magnetic card CC, as shown in FIGS. 13 and 14, has an ordinarily printed layer 23 for displaying visible information in harmony with the pattern of the magnetic recording layer 9b (that is, not concealed thereby or being of such a color or pattern that the concealment by the magnetic recording layer will not be harmful.) This visible information layer 23 is formed beforehand in accordance with an ordinary card printing process on the core sheet 11. In FIGS. 10, 11, and 12, this layer 23 is omitted for the purpose of brevity. The process of producing the magnetic card of this invention, including the various materials used, will now be described in greater detail. First, for the core sheet 11, white opaque polyvinyl chloride, for example, can be used. For the oversheets 12, transparent polyvinyl chloride, for example, can be used. The oversheets 12 can be bonded by heat fusion onto the opposite surfaces of the core sheet 11, or the oversheets 12 and the core sheet can be tentatively secured together with an adhesive at parts thereof other than the forming part of the final product card to obtain a laminated structure which is used as the card substrate 10. The tentatively secured core sheet 11 and the oversheets 12 are formed into an integral card substrate in the transfer step or in the heating and pressing step for imbedding the magnetic recording layer 9b. Next, the materials of the various parts of the magnetic transfer sheet 3 will be described. First, the temporary support 5 is made of a sheet of a thickness of the order of 25 to 100 ijm of a polymer such as polyester, polyethylene, polypropylene, or polycarbonate. The releasing layer 6 is obtained by coating the temporary support 5 with a paint comprising a resin such as an acrylic ester resin or a rosin derivative resin to a coating thickness (dried) of 0.2 to 2 p. As described hereinafter, this releasing layer 6 is not indispensible in all cases but is preferably used for carrying out the transfer step smoothly and for protecting the colored layer 7 and the magnetizable layer 8. The colored layer 7 is provided for the purposes of concealing the color of the magnetizable layer 8 and of utilizing the magnetic recording layer 9b positively and aesthetically and is preferably provided except where the color of the magnetizable layer 8 itself is desirable, or where the color of the magnetizable layer 8 has a cryptic color relation to the color of the surrounding card substrate. This colored layer 7 is obtained by coating the releasing layer 6 with a coloring paint prepared by dispersing a desired coloring matter (pigment or dyestuff) in a binder having as its predominant ingredient a- thermo- plastic resin such as a vinyl chloride-vinyl acetate copolymer, an acrylic resin, or a cellulose derivative resin, the coloring paint being applied by a gravure coating method, a roll coating method, or like suitable method to a coating thickness of 0.5 to 10 p (dried). It is desirable that this colored layer 7 be thin when the electric-magnetic conversion characteristics are considered. On the other hand, when the hue is considered, a thick colored layer 7 is desirable, in general. Accordingly, this thickness should be determined in view of the magnetization process apparatus, standards, and other pertinent conditions. The magnetizable layer 8 is formed by applying by the roll coating method or some other effective method a magnetic paint prepared by dispersing a magnetic powder of y-Fe203, Co-Fe304, CrO2, or the like in a binder having as its predominant ingredient a thermoplastic resin such as a vinyl chloride - vinyl acetate copolymer, a cellulose derivative resin, or a vinyl chloride resin, the magnetic paint being applied as a coating of a thickness of approximately 5 to 25 p .(dried)'. The cutting die used for the partial die cutting of the magnetic recording layer can be of any type provided that it has a closed-figure shape for producing the desired island shape and has ample hardness and sharpness for die cutting of plastics. The partial die cutting can be effectively carried out by means of, for example, a sealprinting die-cutting press. The transfer of the magnetic recording layer 9b of island shape (FIG. 10) can be carried out, for example, by using a hot die (not shown) of dimensions somewhat greater than those of the magnetic recording layer of island shape to apply heat and pressure under the conditions of a heating temperature of 150 to 2000C, a pressure of 50 to 250 kg/cmê, and an application time of 0.5 to 2 seconds thereby to cause the magnetic recording layer ,9b to adhere to the card substrate 10. The press plate (not shown) used for imbedding the magnetic recording layer 9b thus transferred into the card substrate 10 (FIGS. 11 and 12) is, for example, astainless-steel plate of 0.5-mm thickness having a mirrorfinished surface. The heating and pressing conditions for this imbedding step are, for example, a heating temperature of 120 to 1800C, a pressure of 10 to 50 kgfcm2, and a process time of 5 to 30 seconds. In the foregoing part of this disclosure, the process of producing magnetic cards ofthis"invention and resulting product have been described with respect to a representative example of the first fundamental mode of practice and an example of the resulting magnetic card structure. By using magnetic transfer sheets of the laminar structural arrangements as shown in FIGS. 15 through 25 instead of that of the magnetic transfer sheet 3 illustrated in FIG. 5, other examples of magnetic cards respectively of the laminar constructions shown in FIGS. 26 through 36 are obtained according to the first fundamental mode of practice of the process of the invention in correspondence with that shown in FIG. 14. The magnetic transfer sheets shown in FIGS. 15 through 25 are obtained by respectively changing the combinations of the temporary support 5 and the magnetizable layer 8, which are indispensible elements, and, in addition according to necessity, the releasing layer 6, the colored layer 7, aKnonmagnetic metal layer 15, and a heat-sensitive adhesive layer 16. Here, the releasing layer 6 and the colored layer 7 are as described hereinbefore. The nonmagnetic metal layer 15 of thin film thickness effectively conceals the magnetizable layer 8 and is provided according to necessity for the purpose of imparting a good hue by merely providing a relatively thin colored layer 7 on this nonmagnetic metal layer 15, while retaining good electric-magnetic conversion characteristics. This layer 15 is formed by vapor deposition of, for example, aluminum, tin, or the like to -o a thickness of the order of 500 A, for example. By using this nonmagnetic metal layer 15, a beautiful coloring can be amply imparted with a thickness of the colored layer 7 of 0.5 to a number of p. The heat-sensitive adhesive layer 16 is provided when necessary for imparting good heat transferability of the magnetic transfer sheet relative to the card substrate while retaining a high concentration of magnetic particles in the magnetizable layer 8 and therefore retaining good magnetic characteristics. For this layer 16, a layer containing a thermoplastic resin such as an acrylic resin or a vinyl chloride-vinyl acetate copolymer as its predominant ingredient and having a thickness of the order of 1 to 15 p is used. Next an-example in accordance with the second fundamental mode of practice of the process for produc ing magnetic cards of this invention will be described. In this case, the structure shown in FIG. 12 is first prepared according to the first fundamental mode of practice. Then, as shown in FIG. 37, a printed lettering layer 24 of a thickness of 1 to 20 p (dried) is formed by a process such as siLk-screen printing on the magnetic recording layer 9b imbedded in the card substrate 10 of the structure thus prepared. The material constituting this printed lettering layer 24 is sub stantially the same as that of the colored layer 7. If this printed lettering layer 24 ,s excessively thick, it will, affect the electric-magnetic 'conversion character istics and give rise to a great drop in the output. For this reason, it is desirable that this layer 24 be made as thin as possible without losing its desired display effect. Then, by heating and pressing this printed lettering layer 24 with a mirror-finished press plate (not shown), it is imbedded into the magnetic recording layer 9b, and a structure as shown in FIG. 38 wherein the upper surfaces of the card substrate 10, the magnetic recording layer 9b, and the printed lettering layer 24 all lie flush in the same plane is obtained. Then, by cutting this structure along the planes indicated by lines F-F, a magnetic card as shown in FIGS. 39 and 40 is obtained. In this case, also, magnetic cards of modified structures shown in FIGS. 41 through 51 can be obtained by using magnetic transfer sheets of the structures shown in FIGS. 15 through 25, respectively, in place of that shown in FIG. 5. In the second fundameqtal mode of practice of the process for producing magnetic cards according to this invention as described above, the magnetic recording layer 9b not only is caused to contribute, itself, to the aesthetic appearance of the card as a pattern but also affords an area for forming an additional pattern such as a printed layer of characters and/or a picture pattern. Thus, a magnetic card which is superior by that much in design effect can be obtained. In correspondence to FIG. 14, it is also possible as shown in FIG. 52 to provide additionally a commonly used magnetic stripe separate from the magnetic recording layer 9b of island form for both the first and second fundamental modes of practice. The third fundamental mode of practice of the process of this invention for producing magnetic cards is a repetition -of the aforedescribed first fundamental mode with the use of an oversheet 12 instead of a card substrate 10 comprising a laminated structure of a core sheet 11 and oversheets 12. More specifically, in accordance with the first fundamental mode, the magnetic transfer sheet 3b shown in FIG. 9 is superposed on an oversheet 12 (FIG. 53), and after heating, the temporary support 5 is peeled off to transfer the magnetic recording layer 9b in island form onto the oversheet 12 (FIG. 54). The oversheet 12 of the structure shown in FIG. 54 obtained in this manner is then bonded or tentatively bonded with an adhesive to a core sheet 11, and the resulting laminated structure is heated and pressed with a press plate of mirror-finish surface (not shown) thereby to imbed the magnetic recording layer 9b so that its upper surface lies flush -in the same plane as that of the card substrate as shown in FIG. 56 and, at the same time, to bond by heat fusion the tentatively bonded oversheet 12 to the core sheet 11. The structure thus obtained as shown in FIG. 56 is essentially the same as the structure shown in FIG. 12. By subsequently cutting this structure similarly as in the first fundamental mode of practice, a magnetic card similar to that shown in FIGS. 13 and 14 is obtained. Furthermore, in the fourth fundamental mode of practice of the process of this invention for producing magnetic cards, with respect to the structure as shown in FIG. 56 obtained by the third fundamental mode of practice, a printed layer 24 of characters and/or a picture pattern is formed on the magnetic recording layer 9b as indicated in FIGS. 37 and 38 in the second fundamental mode of practice. Then, with the use of a press plate of mirror-finish surface, the structure is heated and pressed so that the upper surface of the printed layer 24 of characters and/or a picture pattern lies flush in the same plane as those of the magnetic recording layer 9b and the card substrate 10. A magnetic card produced by this fourth fundamental mode of practice is identical to that produced by the aforedescribed second fundamental mode of practice. By using magnetic transfer sheets respectively of different laminated construction, the structures as indicated in FIGS. 39 through 51 can be obtained. In order to indicate more fully, the nature and utility of this invention, the following specific examples of practice in concrete form are set forth, it being understood that these examples are presented as illustrative only and are not intended to limit the scope of the invention. Example 1 (according to the first fundamental mode of practice) The surface of a temporary support comprising a polyester film of 50-p thickness was coated with a paint of an acrylic ester resin to a coating thickness of 0.5 p by a gravure coating process thereby to form a releasing layer. This layer was then coated with a coloring paint to a coating thickness of 2 p by a gravure coating process, the coloring paint comprising a vinyl chloride-vinyl acetate copolymer as a principal binder and a desired coloring matter dispersed therein. Thus a colored layer was formed. This colored layer was then coated with a magnetic paint to a coating thickness of 15 p by a roll coating process, the magnetic paint comprising a vinyl chloridevinyl acetate copolymer as a principal binder and magnetic powder particles of y-Fe2O3 dispersed therein. Thus a magnetizable layer was formed, and a magnetic transfer sheet corresponding to that shown in FIG. 5 was obtained. Then, with the use of a seal-printing, die-cutting press and, moreover, a cutting die of a desired shape, partial die cutting from the magnetic recording layer side was so carried out as-not to cut the temporary support. Superfluous parts of the magnetic recording layer, other than the desired part thereof of island form, were then removed, thereby to form a magnetic transfer sheet, as shown in FIGS. 8 and 9, in which the magnetic recording layer of island form was caused to remain. Separately, a card substrate was fabricated by laminating oversheets of ;transparent polyvinyl chloride of a thickness of 0.1 mm on the front and back surfaces of a core sheet of bluish white polyvinyl chloride on the front and back faces of which patterns had been printed by offset printing The above described magnetic transfer sheet was placed on this card substrate at a desired position thereof and was heated and pressed against the card substrate with a hot die, which was one size larger than the shape of the magnetic recording layer of island form, under the conditions of a temperature of 1800C, a pressure of 100 kg/cm2, and a process time of 0.5 second. The polyester film was peeled off thereby to transfer the magnetic recording layer onto the card substrate (FIG. 11). The laminated structure thus formed was clamped between stainless-steel plates of 0.5-mm thickness which had been mirror finished and was heated and pressed under the conditions of 1500C and 25 kg/cmê for 20 minutes. After cooling, a card structure in which the oversheets and t-he core, sheet had been heat fused and laminated was obtained, and the desired magnetic plastic card, as shown in FIGS. 13 and 14, having a magnetic recording layer of island form, which had been imbedded in the card substrate so that their outer surfaces lay flush in the same plane, was obtained. Example 2 (according to the first fundamental mode of practice) The surface of a temporary support comprising a polyester film of 50-p thickness was coated to a coating thickness of 0.5 p with a paint of an acrylic ester by a gravure coating process thereby to form a releasing layer. Onto this releasing layer, a coloring paint comprising-a vinyl chloride-vinyl acetate copolymer as a principal binder and a desired coloring matter dispersed therein was applied as a coating of a thickness of 2p by a gravure coating process thereby to form a colored layer. This colored layer was coated to a coating thickness of 15 p with a magnetic paint by a roll coating process, the magnetic paint comprising a vinyl chloridevinyl acetate copolymer as a principal binder and powder particles of y-Fe203 dispersed therein. Thus a magnetizable layer was formed. Onto this magnetizable layer, a varnish having an acrylic resin as a predominant component was applied as an adhesive coating layer of a thickness of lOp by a roll coating process, whereupon a magnetic transfer sheet as shown in FIG. 39 was¯obtain-éd. With the use of this magnetic transfer sheet, the procedures of Example 1 were followed to carry out partial die cutting, removal of superfluous parts of the magnetic recording layer, transferring of the magnetic recording layer, and heating and pressing. The magnetic recording layer of island form was.thus imbedded within the card substrate so that its outer surface lay flush in the same pla,ne as that of the card substrate. As a result, the desired magnetic plastic card, as shown in FIG. 30, having a magnetic recording layer of island form was obtained. Example 3 (according to the second fundamental mode of practice) On the magnetic recording layers of island form with respect to the magnetic plastic cards produced in Example 1 and Example 2, characters, designs, etc. were provided with silk screen ink of a desired coloring matter and by silk screen printing as printed layers of the characters and designs of a thickness of 3 Fr. The aforedescribed card substrates were again clamped between stainless-steel plates of 0.5-mm thickness with mirror-finished surfaces, heated and pressed under the conditions of 1500C and 25 kg/cmê for 20 minutes, and cooled. As a result, the printed layers of the characters and design were imbedded within the magnetic recording layers, and magnetic plastic cards having island-form, magnetic recording layers with desired characters and designs, in each of which the outer surfaces of the card substrate, the magnetic recording layer, and the printed layer of the characters and design lay flush in the same plane, were obtained (FIGS. 40, 45). Example 4 (according to the third fundamental mode of practice) The surface of a temporary support comprising a polyester film of 50-p thickness was coated to a coating thickness of 0.5 p with a paint comprising an acrylic ester resin by a gravure coating process thereby to form a releasing layer. Onto this releasing layer was applied as a coating of 2-p thickness a coloring paint comprising a vinyl chloride-vinyl acetate copolymer as a principal binder and a desired coloring matter dispersed therein, which was applied by a roll coating process. A colored layer was thus formed. Onto this colored layer, a magnetic paint compris ing a vinyl chloride-vinyl acetate copolymer as a principal binder and powder particles of y-Fe203 dis persed therein was applied as a coating of 15- thick ness by a roll coating process thereby to form a magnetizable layer (FIG. 5). -Then, with the use of a seal-printing, die-cutting press and, moreover, a cutting die of a desired shape, partial die cutting from the magnetic recording layer side was so carried out as not to cut the support structure for - transferring Superfluous parts of the magnetic record ing layer, other -than the desired part thereof of island form, were then removed thereby to form a magnetic transfer sheet, as shown in FIGS. 8 and 9, in which the magnetic recording layer of island form was caused to remain. In this connection, the pitch or spacing interval with which the partial die cutting of the magnetic transfer sheet was made the same as the pitch of the multiple repeated pattern printed in succession on the core sheet. The above described magnetic transfer sheet was then superposed on an oversheet for surface purpose, and heat transferring was carried out under the conditions of a heating temperature of 1800C, a speed of 5 meters/min., and a pressure of 10 kg/30 cmê as indicated in FIGS. 53 and 54. The above mentioned oversheet was then tentatively secured (with an adhesive at parts outside of the finished product) in register with a desired position with respect to the pattern of the core sheet which had been offset printed, and on the back face, also, a transparent oversheet was similarly secured tentatively as indicated in FIG. 55. The structure thus formed was clamped between stainless-steel plates of 0.5-mm thickness with mirrorfinished surfaces and was heated and pressed under the conditions of 1500C and 25 kg/cm2 for 20 minutes. After this structure was cooled, a card structure in which the oversheet and the core sheet had' been laminated by heat fusion was obtained, and magnetic plastic card as shown in FIGS. 13 and 14 having a magnetic recording layer of a desired island form whose outer surface lay flush in the some plane as that of the card substrate was obtained. Example 5 With respect to the magnetic plastic card produced in Example 4, characters, designs, etc. were provided with silk screen ink of a desired coloring matter and by silk screen printing as a printed layer of characters and designs of a thickness of 3 p on the magnetic record layer of island form. The aforedescribed card substrate was again clamped between stainless-steel plates of 0.5-mm thickness with mirror-finished surfaces, heated and pressed under the conditions of 150 C and 25 kg/cmê for 20 minutes, and cooled. As a result, the printed layer of the characters and design was imbedded within the magnetic recording layer, and a magnetic plastic card having a magnetic recording layer of island form with desired characters and designs, in which the outer surfaces of the card substrate, the magnetic recording layer, and the printed layer of the characters and design lay flush in the same plane, was obtained. Example 6 The surface of a temporary support comprising a poly ester-film of 50- > thickness was coated to a coating thickness of 0.5- with paint comprising an acrylic ester resin by a gravure coating process thereby to form a releasing layer. Onto this releasing layer was applied as a coating of 0.5-p thickness a coloring paint comprising a vinyl chloride-vinyl acetate copolymer as a principal binder and a desired coloring matter dispersed therein, which paint was applied by a gravure coating process. A colored layer was thus formed. Onto this colored layer was formed a layer of 500-A thickness of aluminum by vacuum evaporation. This aluminum layer was further coated to a coating thickness of 15 p with a magnetic paint comprising a vinyl chloride-vinyl acetate copolymer as a principal binder and fine particles of y-Fe2O3 dispersed therein, the magnetic paint being applied by a roll coating process. A magnetic transfer sheet having a magnetizable layer (FIG. 17) was thus formed. With the use of magnetic transfer sheets as described hereinabove, magnetic plastic cards, each having magnetic recording layer of island form containing a pattern, were respectively produced by procedures according to Examples 1, 3, 4 and 5 (FIGS. 28, 43 and 47). The rate of decrease of output due to the effect of the printed layer of characters and design in the electricmagnetic conversion characteristics of 'each of the cards produced according to Examples 1 through 6 was within 10 percent at a magnetic writing-in density of 210 FRPI, which was of an order well within allowable limits.

Claims: WHAT WE CLAIM IS: 1. A process for producing magnetic cards which comprises: a first step of forming a magnetic transfer sheet by making a partial die cut of a closed figure in only the magnetic recording layer stock of a magnetic transfer sheet comprising a temporary support and the magnetic recording layer stock to be transferred laminated on the temporary support and thereafter peeling off and removing, from the temporary support, parts of the magnetic recording layer stock outside of the region encompassed by said closed-figure partial die cut thereby to cause a magnetic recording layer of island form of said region to be left on the temporary support; ; a second step of transferring the magnetic recording layer of island form onto a card substrate by placing the surface of the magnetic recording layer of the magnetic transfer sheet thus formed against the surface of the card substrate, heat ing the magnetic recording layer and removing the temporary support; and a third step of imbedding the magnetic recording layer by placing a press plate with a mirror-finished surface on the magnetic recording layer thus transferred and heating and pressing the same into the card substrate until the outer surface of the magnetic recording layer lies flush in the same plane as that of the card substrate. 2. A process according to claim 1 which further comprises a fourth step of printing a printed layer of characters and design on the outer surface of the magnetic recording layer of the structure obtained after the third step of imbedding the magnetic recording layer and a fifth step of leveling the card surface by placing, after the fourth printing step, a press plate with a mirror-finished surface against the printed layer thus printed and heating and pressing.the printed layer thereby to cause the outer surfaces of the.printed layer and the card substrate to lie flush in the same plane. 3. A process for producing magnetic cards which comprises: a first step of forming a magnetic transfer sheet by making a partial die cut of a closed figure in only the magnetic recording layer stock of a magnetic transfer sheet comprising a temporary support and the magnetic recording layer stock to be transferred laminated on the temporary support and thereafter peeling off and removing, from the temporary support, parts of the magnetic recording -layer stock outside of the region encompassed by said closed-figure partial die cut thereby to cause a magnetic recording layer of island form of said region to be left on the temporary support; ; a second step of placing the outer surface of the magnetic recording layer of island form of the magnetic transfer sheet thus formed against a surface of an oversheet and transferring the magnetic recording layer onto the oversheet by heating the transfer sheet and removing the temporary support; a third step of securing or tentatively securing by adhesion the oversheet to a core sheet; and. a fourth step of imbedding the magnetic recording layer by placing a press plate with a mirror finished surface against the structure obtained by the third step and heating and pressing the same thereby to imbed the magnetic recording layer so that its outer surface lies flush in the same plane as that of the oversheet. 4. A process according to claim 3 which further comprises a fifth step of printing a printed layer of characters and design on the outer surface of the magnetic recording layer of the structure obtained by the fourth and a sixth step of leveling the card surface by placing, after the fifth printing step, a press plate with a mirror finished surface against the oversheet and heating and pressing the same thereby to cause the outer surfaces of the printed layer and the oversheet to lie in the same plane. 5. A process according to any of claims 1 through 4 in which the magnetic recording layer stock formed on the temporary support of the magnetic transfer sheet has a magnetizable layer comprising a binder resin and magnetic powder particles dispersed therein. 6. A process according to claim 5 in which the magnetic recording layer stock further has a colored layer between the temporary support and the magnetizable layer. 7. A process according to claim 6 in which the magnetic recording layer stock further has a nonmagnetic metal layer formed by vapor deposition between the magnetizable layer and the colored layer. 8. A process according to claim 5, 6, or 7 in which the magnetic recording layer stock further has a releasing layer inserted between the magnetizable layer and the temporary support and being in contact with the support for transferring. 9. A process according to any of claims 5 through 8 in which the magnetic recording layer stock further has a heat-sensitive adhesive layer on the magnetizable layer. 10. A magnetic card comprising a card substrate and a planar magnetic recording piece of island form formed by die cutting and having smooth, fair peripheral edges, the magnetic recording piece being provided on at least one surface of the card substrate and being so imbedded therein that the outer surface of the magnetic recording piece lies flush in the same plane as that of the card substrate. 11. A magnetic card according to claim 10 in which a printed layer of characters and design is provided on and so imbedded in the magnetic recording piece that the outer surfaces of the magnetic recording piece and the printed layer lie flush in the same plane as the outer surface of the card substrate. 12. A magnetic card according to claim-l0 or 11 in which the card substrate comprises a laminated structure of an opaque core sheet and an oversheet made of a transparent resin, and the magnetic recording piece is so imbedded in the oversheet that their outer surfaces lie flush in the same plane. 13. A magnetic card according to claim 12 in which visible' information in harmony with the pattern of the magnetic recording piece is printed on the core sheet. 14. A magnetic card according to claim 10, ill, or 12 in which the magnetic recording piece has a magnetizable layer comprising a binder resin and magnetic powder particles dispersed in the binder resin. 15. A magnetic card according to claim 14 in which the magnetic recording piece further has a colored layer on the magnetizable layer. 16. A magnetic card according to claim 15 in which the magnetic recording piece further has a nonmagnetic metal layer formed by vapor deposition and interposed between the magnetizable layer and the colored layer. 17. A magnetic card according to claim 14- > 15 or 16 in which the magnetic recording piece has a releasing layer constituting an outer layer. 18. A magnetic card according to any of claims 14 through 17 in which the magnetic recording piece has a heat-sensitive adhesive layer underneath the magnetizable layer.

Inventors: INOUE, SHUNJI, NISHIKAWA, SEIICHI, SUZUKI, NORIMOTO
Applicants: DAI NIPPON INSATSU KABUSHIKI KAISHA
Application year: 1982
Main classification: G06K19
IPC codes: C09D5, G11B5, C09D127, G06K19