INK COMPOSITION FOR INK JET PRINTING

Abstract: There is disclosed an ink composition for ink jet print­ ing comprising vinyl polymer latex particles which contain a hydrophobic dye and which are essentially insoluble in and non-swelling with water, an organic solvent having a hy­ drophilic-lipophilic balance of 9.5 or less, and an aqueous medium. The ink composition of the present invention exhibits less bleeding, higher print quality, and less risk of nozzle clogging. In addition, the ink composition of the present invention exhibits quick drying property on the printing paper having a high sizing degree which is called plain paper.

Description: Ink composition for ink jet printing This invention relates to an ink composition for use in ink jet printing. This invention particularly relates to an ink composition for ink jet printing, which comprises water-insoluble polymer latex particles impregnated with a hydrophobic dye, and more particularly to an ink composition for ink jet printing, which is suitable for the ink jet printing system wherein an ink projected from a nozzle by a sudden reduce in the internal volume of an ink chamber. Recently, the conventional ink jet printing method wherein the information is printed on a printing medium by projecting an ink liquid in a controlled manner without bringing the printing head into contact with the printing medium has quickly become popular for use in a terminal printer or the like because of low noise, possibility of high-speed printing, and possibility of using plain paper. The conventional ink jet printing systems include the ink jet system in which an ink projected from a vessel by a sharp reduce in the internal volume of the vessel or by pressing or suction at a specified pressure, the ink jet system in which an ink projected from a nozzle at a speed accelerated electrostatically by applying a signal voltage between the nozzle and the electrode positioned opposite thereto, and the ink mist system in which mist is generated by the oscillation of an ultrasonic wave. Ink compositions to be used for the above-described types of ink jet printing systems or ink mist printing systems are required to exhibit the following characteristics: i) The ink compositions should provide a sufficient density required for printing, ii) The ink composition should not evaporate and dry in the jet nozzle, causing clogging of the jet nozzle, iii) The ink droplets should dry immidiately after attached to and formed on paper, iv) The printed ink should not bleed due to water and sweat, br the printed section should not disappear, and v) The ink compositions should not exhibit a change in physical properties nor form precipitates during storage. In a conventional method for satisfying the quick drying -characteristics of an ink, use is made of an ink, which sparingly evaporates, and highly permeable paper such as blotting paper, and the ink is allowed to permeate through the paper to obtain apparent dry state. With this method, the ink scarcely clogs by the ink evaporation in the nozzles. However, the material of the paper must be highly permeable to the ink and, therefore, only the paper designated by the manufacturer can be used. As a result, the conventional method is disadvantageous in that the paper is relatively expensive. In another method for satisfying the quick drying characteristics of an ink, a solvent having a relatively high vapor pressure is added to the ink, and the ink is allowed to dry through evaporation of the solvent. With this conventional method, the quick drying characteristics can be satisfied, but the ink dries through evaporation of the solvent and clogs at the front end of the nozzle at the time of stoppage of the equipment or the like if the ink jet nozzle has a diameter of as small as about 50 to 100 iim ° as in the case of an ink jet printer. For this reason, the ink must be prevented from evaporating and drying in the nozzle, for example, by mounting a cover on the front end of the nozzle when the equipment is stopped. The conventional ink composition generally used for ink jet printing consists of a water-soluble dye, a polyhydric alcohol and water. The ink composition further contains a surface active agent, mildew proofing agent, or the like as required. The ink composition is prevented from clogging the nozzle by the addition of a polyhydric alcohol which is nonvolatile and highly hygroscopic. With the conventional ink composition, however, the quick drying characteristics of the printed ink are not satisfied, and it is necessary to use highly permeable paper as mentioned above or to install a heating unit such as electric heater at the paper supporting base for the purpose of promoting evaporation and drying. To eliminate the above-mentioned disadvantages of the conventional methods, the present invention intends to impart the property of drying immidiately when the ink applied to the paper, which properties conflict with each other, to the ink itself so as to provide an ink for use in ink jet printing which can be printed satisfactorily on any kind of paper. The primary object of the present invention is to provide an ink composition for ink jet printing, which does not clog the nozzle and which exhibits quick drying characteristics. Another object of the present invention is to provide an ink composition for ink jet printing, which contains a hydrophobic dye and which exhibits the physical properties necessary for Pink jet printing and a sufficient density of print. A further object of the present invention is to provide an ink composition for ink jet printing, which allows printing of high print quality on any kind of paper. A still further object of the present invention is to provide an ink composition for ink jet printing, which does not bleed due to water and sweat, and which does not disappear after printing. Other objects of the present invention will be clarified by the descriptions of the specification hereinbelow. The above objects are accomplished by an ink composition for ink jet printing (hereinafter referred to the ink of the present invention) comprising vinyl polymer latex particles which contain a hydrophobic dye and which are essentially insoluble in and non-swelling with water, an organic solvent having a hydrophilic-lipophilic balance (hereinafter referred to as the HLB) of 9.5 or less, and an aqueous medium. The present invention will hereinbelow be described in further detail. In the case of ink jet printing, the ink droplet ejected to the paper is considered-to pass through the processes of wetting and permeating through the paper. Of these processes, permeation can be regarded as a chromato-graphic phenomenon. With the conventional ink composi- tion containing a dye uniformly dissolved in a medium, the ink droplet exhibits its density both in the wetting and permeating regions. In contrast with the above-mentioned homogenerous ink composition, in a heterogeneous or dispersion type ink composition containing a dye in a medium in the undissolved form, mainly the medium participates in the permeation, and the ink droplet ejected to the paper exhibits its density only in the wetting region Therefore, the dispersion type ink composition exhibits. little spreading of the ink droplet, yielding a highdensity print with little bleeding. However, the dispersion type ink composition is disadvantageous in that the permeation speed through the printing paper called the plain paper is slow and the ink composition does not dry quickly if the watermiscible solvent used in the aqueous medium is a conventionally used one such as ethylene glycol. The inventors have found that, if a water-miscible solvent having an HLB value of 9.5 or less is used in the aqueous medium, the aqueous medium exhibits very excellent permeability through paper, and separation between the color material and the medium occurs satisfactorily, giving a high-quality print with little spreading and little bleeding. On the other hand, the dispersion type ink composition acts advantageously over the homogeneous typeEwith respect to clogging of the front end of the nozzle of the recording equipment due to drying of the ink composition. Namely, it is generally known that the existence of a disperse phase causes the evaporation speed of the medium to decelerate and that the smaller the particle size of the disperse phase is, the slower the evaporate speed of the medium becomes. Further, in the case of the homogeneous ink composition, clogging at the front end of the nozzle due to drying of the ink composition occurs because the vehicle component changes due to evaporation and it becomes impossible to maintain the dye dissolving property. Contrarily, with the ink composition of the present invention, the stability with respect to the meidum depends on the latex particles instead of the dye and, therefore, it is expected that the tolerance can be increased. Further, it is desirable that the above-mentioned watermiscible solvent has the slow-evaporating property for the reason described above. The slow-evaporating solvent indicates the solvent which does not present the above-mentioned problem when the ink is formulated, and the solvent which is defined in the present invention and has a boiling point of 1000C or higher, preferably 1500C or higher. It is necessary that the solvent used in the present invention has an HLB value of 9.5 or less depending on the degree of sizing of the printing paper. On the other hand, solvents having an HLB value of 7.0 or less -exhibit lower miscibility with water, but some of such solvents can exhibit sufficient miscibility with water and can be used in the present invention. In the present invention, the HLB value of 9.5 or less is the value exhibited by the solvent when the solvent is a single solvent, and is the value of the whole solvent mixture when the solvent is a solvent mixture. Namely, the respective solvents of a solvent mixture need-not always have an HLB value of 9.5 or less. It is necessary only that the HLB value of the whole solvent mixture obtained by mixing several solvents is.9.5 or less. The HLB value of the solvent used in the present invention is 9.5 or less, preferably 9.5 to 7.0. The HLB value can be measured by various methods and differs according to the measuring method employed. In the present invention, the HLB value is defined to be expressed by the following formula: HLB = 7 + (basic number of hydrophilic groups) - n. (basic number of hydrophobic groups) In the formula mentioned above, the number of hydrophilic groups and that of hydrophobic groups are derived from the study on the rate of coalescence of emulsifying phenomena. The typical values are listed in Table 1 below. Table 1 EMI7.1 <tb> <SEP> Number <tb> <SEP> Basic <tb> <SEP> Hydrophilic <SEP> group <SEP> Hydrophobic <SEP> group <SEP> of <tb> <SEP> Number <tb> groups <tb> -SO3Na <SEP> 38.7 <SEP> -CH2 <tb> <SEP> -COOK <SEP> 21.1 <SEP> CH3- <SEP> # <SEP> -0.475 <tb> <SEP> -COONa <SEP> 19.1 <SEP> =CH N <SEP> (quaternary <tb> <SEP> 9.4 <SEP> -(CH2-CH2-O)- <SEP> +0.33 <tb> <SEP> ammonium <SEP> salt) <tb> Ester <SEP> (sorbitan <tb> <SEP> 6.8 <SEP> -(CH2-CH-O)- <SEP> -0.15 <tb> <SEP> ring) <tb> <SEP> CH3 <tb> <SEP> Ester <SEP> (free) <SEP> 2.4 <tb> <SEP> -COOH <SEP> 2.1 <tb> <SEP> -OH <SEP> (free) <SEP> 1.9 <tb> <SEP> -O- <SEP> 1.3 <tb> <SEP> -OH <SEP> (sorbitan <tb> <SEP> ring) <tb> The measuring methods for HLB are described in detail by Davies in Proc. 2nd Intern. Congress of Surface Activity, 1, 426 (1957), and by Okada in Yukagaku (Oil Chemistry), 7, 434 (1958). The solvents having an HLB value of 9.5 or less which are used in the present invention include monohydric or polyhydric alcohols and their derivatives, cyclic ethers, lactones or the like. Examples of the polyhydric alcohols are (mono, di, tri, tetra) alkylene glycols, and the examples of polyhydric alcohol derivatives are (mono, di, tri, tetra) ethylene glycol alkyl ethers, (mono, di, tri, tetra) ethylene glycol alkyl ether acetates, fatty acid glycerine esters, sorbitan esters or the like. The typical solvents used in the present invention and their HLB values are listed in Table 2 below. However, the solvents used in the present invention are not limited to these solvents. Table 2 EMI9.1 <tb> <SEP> Solvent <SEP> HLB <tb> Propylene <SEP> glycol <SEP> 9.375 <tb> Dipropylene <SEP> glycol <SEP> 9.25 <tb> Tripropylene <SEP> glycol <SEP> 9.125 <tb> Butane-1, <SEP> 4-diol <SEP> 8.90 <tb> Pentane-1,5-diol <SEP> 8.425 <tb> 2-methyl-pentane-2 <SEP> , <SEP> 4-diol <SEP> 7.95 <SEP> <tb> Ethylene <SEP> glycol <SEP> monoethyl <SEP> ether <SEP> 8.30 <tb> Ethylene <SEP> glycol <SEP> monobutyl <SEP> ether <SEP> 7.25 <tb> Diethylene <SEP> glycol <SEP> monomethyl <SEP> ether <SEP> 9.125 <tb> Diethylene <SEP> glycol <SEP> dimethyl <SEP> ether <SEP> 8.05 <tb> Diethylene <SEP> glycol <SEP> monoethyl <SEP> ether <SEP> 8.65 <tb> Diethylene <SEP> glycol <SEP> diethyl <SEP> ether <SEP> 7-.10 <SEP> <tb> Triethylene <SEP> glycol <SEP> monomethyl <SEP> ether <SEP> 9.475 <tb> Triethylene <SEP> glycol <SEP> monoethyl <SEP> ether <SEP> 9.00 <tb> Tetraethylene <SEP> glycol <SEP> dimethyl <SEP> ether <SEP> 8.75 <tb> Furfuryl <SEP> alcohol <SEP> 7.825 <tb> Tetrahydroxy <SEP> furfuryl <SEP> alcohol <SEP> 7.825 <tb> Dioxane <SEP> 7.70 <tb> y-Butyrolactone <SEP> 7.50 <tb> y-Valerolactone <SEP> 7.025 <tb> The HLB values listed above are those determined-by the method described by Davies in Proc. 2nd Intern. Congress of Surface Activity, 1, 426 (1957). The main purpose of the use of a combination of two or more solvents is to adjust the viscosity of the ink and to control the speed of permeation of the medium through the recording paper. The proportion of the above-described solvent with respect to water in the aqueous medium of the ink of the present invention may be of any value, provided that the drying property of the ink at the front end of the nozzle, drying property thereof on the printing paper, dispersion stability of the latex particles, or the like are satisfied. Generally, the proportion of the solvent is 95 to 20 per 5 to 80 of water, preferably 80 to 60 per 20 to 60 of water. The vinyl polymer latex containing a hydrophobic dye, which is used in the present invention, may be prepared by any method capable of incorporating a hydrophobic dye to the latex particles in an amount providing a sufficient density necessary for printing. For example, the vinyl polymer latex may be impregnated with the hydrophobic dye in accordance with the method of impregnating the vinyl polymer latex with a hydrophobic material as described in United States Patent No. 4,199,363, British Provisional Patent Publication No. 2003486A, Japanese Provisional Patent Publication Nos. 137131/1978 and 50240/1980 or the like. The vinyl polymer latex used in the present invention may be of any composition, provided that it can contain the hydrophobic dye in an amount yielding a sufficient printing density necessary as an ink composition and is stable in the above-described aqueous medium. It is preferable that the polymer particles contained in the vinyl polymer latex in accordance with the present invention be synthesized from a radicalpolymerizable vinyl monomer by the emulsion polymerization. Examples of the monomers are listed below, but the present invention is not limited to the use of these monomers. 1) Acrylic ester compounds Methyl acrylate, ethyl acrylate, butyl acrylate, dodecyl acrylate, glycidyl acrylate, 2-acetoacetoxyethyl acrylate, etc. 2) Methacrylic ester compounds Methyl methacrylate, ethyl methacrylate, butyl methacrylate, dodecyl methacrylate, glycidyl methacrylate, 2-acetoacetoxyethyl methacrylate, etc. 3) Acrylamides Butylacrylamide, N,N-diethylacrylamide, N,N-diisopropylacrylamide, dodecylacrylamide, etc. 4) Methacrylamides Butylmethacrylamide, N,N-diethylmethacrylamide, N,N- diisopropylmethacrylamide, dodecylmethacrylamide, etc. 5) Vinyl ester compounds Vinyl acetate, vinyl butylate, etc. 6) Vinyl halide compounds Vinyl chloride, etc. 7) Vinylidene halide compounds Vinylidene chloride, etc. 8) Vinyl ether compounds Vinyl methyl ether, vinyl ethyl ether, vinyl hexyl ether, vinyl glycidyl ether, etc. 9) Styrene compounds Styrene, -methylstyrene, hydroxystyrene, chlorostyrene, methylstyrene, etc. 10) Other compounds Ethylene, propylene, butylene, butadiene, isoprene, acrylonitrile, etc; divinylbenzene, allyl acrylate, allyl methacrylate, N-allylmethacrylamide, 4,41 - isopropylidenediphenyl diacrylate, 1,3-butylene diacrylate, 1,3-butylene dimethacrylate, 1,4-cyclohexylene-dimethylene dimethacrylate, diethyleneglycol dimethacrylate, diisopropyleneglycol dimethacrylate, divinyloxymethylene, ethylene diacrylate, ethylene dimethacrylate, ethylidene diacrylate, ethylidene dimethacrylate, 1,6-diacrylamidehexane, 1,6-hexamethylene diacrylate, 1,6-hexamethylene dimethacrylate, N,N'-methylenebisacrylamide, neopentylglycol dimethacrylate, phenylethylene dimethacrylate, tetraethyleneglycol dimethacrylate, tetramethylene diacrylate, tetramethylene dimethacrylate, 2,2,2-trichloroethylidene dimethacrylate, triethyleneglycol diacrylate, trimethyleneglycol dimethacrylate; compounds having hydrophilic groups EMI12.1 EMI13.1 EMI14.1 EMI15.1 EMI16.1 EMI17.1 EMI18.1 n = 1 # 10 In the formulas described above, R designates hydrogen atom or a lower alkyl group, and M denotes an alkali metal, hydrogen atom or -NH4. R1, R2 and R3 are independently selected from the group consisting of a carbocyclic group having from 5 to 12 carbon atoms, for example, aryl, aralkyl and cyclohexyl such as benzyl, phenyl, p-methylbenzyl, cyclohexyl, cyclopentyl, etc.; and an alkyl group having from 1 to 12 carbon atoms, for example, methyl, ethyl, propyl, isobutyl, pentyl, hexyl, heptyl, decyl and so on. Preferably, R1 and R2 each denote methyl, and R3 denotes benzyl. is an anion, i.e., an anion of an anionic salt in which an ionic free radical forms an atom, such as halide (e.g., bromide or chloride), sulfate, alkyl sulfate, sulfonate of alkane or allene (e.g., p-toluene sulfonate), acetate, phosphate, dialkylphosphate or homologues thereof. Among the above compounds having hydrophilic groups, the compounds having a sulfonate group, a polyoxyethylene group and a quaternary ammonium group are preferred. Particularly preferred are the Compounds (3), (38) and (41). The polymer particules contained in the vinyl polymer latex in accordance with the present invention may further contain cross-linkable monomer. As preferred example of the cross-linkable monomer, divinyl benzene is mentioned. The vinyl polymer latex particles used in the present invention can be prepared by subjecting the vinyl monomer to degasification-nitrogen substitution in an aqueous medium containing a dispersing agent (surface active agent) for emulsion polymerization in an amount of about 0.1 to 20% by weight based on said vinyl monomer and water in an amount of about 2 to 50% by weight, emulsifying, adding an additive (e.g.1-molecular weight adjusting agent or antioxidant) used in usual emulsion polymerization as required, and finally adding an emulsion polymerization initiator (e.g., hydrogen peroxide or potassium peroxide), followed by emulsion polymerization according to usual procedure. A cation polymer latex containing a quaternay ammonium salt can be prepared by preparing a polymer latex containing a quaternay ammonium salt precursor preferably according to the method described above, and subjecting the polymer latex to the reaction for converting it to the quaternary form. The dispersing agent used for the emulsion polymerization is a usually employed anionic, cationic, nonionic or amphoteric surface active agent. The surface active agents may be used alone or as a mixture of two or more agents. However, it is not necessary to limit the dispersing agent for emulsion polymerization to these surface active agents. For example, the anionic surface active agent may also be a sulfate of a higher alkyl represented by the formula R-OSO3M or R4OCH2CH2+gOSO3M in which R denotes an alkyl group having from 8 to 30 carbon atoms, M denotes an alkali metal or ammonium1 and L denotes a positive integer between 0 and 30; or an alkyl benzene sulfonate represented by the formula EMI20.1 in which R' designates hydrogen or an alkyl group having from 1 to 18 carb atoms, R" designates an alkyl group having from 1 to 18 carbon atoms, M designates an alkali metal or ammonium, m designates a positive integer between 0 and 30, and n designates a positive integer 0, 3 or 4. The nonionic surface active agent may, for example, be polyoxyethylene derivatives, higher fatty acid esters or the like, and the amphoteric surface active agent may be a sulfobetaine type, an amino acid type or the like. Any particle size of aqueous polymer latex can be obtained by varying the amount of the dispersing agent for emulsion polymerization, the amount of the monomer, the amount of the polymerization initiator, the speed of agitation, the polymerization temperature or the like. The particle size of the polymer latex preferably used in the present invention is within the range between 0.01 pm and 1.0 pm, particularly between 0.02 llm and 0.5 ijm. Examples of the hydrophobic dyes used in the present invention are monoazo, anthraquinone, metal complex type monoazo, diazo, phthalocyanine, triallylmethane dyes or the like which is soluble in an organic solvent, subliming dyes and organic pigments. Examples of the hydrophobic dyes used in the present invention are listed below for respective colors. Yellow: C.I. Solvent Yellow 19 (C.I. 13900A), C.I. Solvent Yellow 21 (C.I. 18690), C.I. Solvent Yellow 61, C.I. Solvent Yellow 80, Aizen Spilon Yellow GRH Special (Hodogaya Chemical Co., Ltd,), Diaresin Yellow F (Mitsubishi Chemical Industries Ltd.), Yellowfluer G (Sumitomo Chemical Co., Ltd.). Orange: C.I. Solvent Orange 1 (C.I. 11920), C.I. Solvent Orange 37, C.I. Solvent Orange 40, Diaresin Orange K (Mitsubishi Chemical Industries Ltd.), Diaresin Orange G (Mitsubishi Chemical Industries Ltd.), Sumiplast Orange 3G (Sumitomo Chemical Co., Ltd.). Red: C.I. Solvent Red 8 (C.I. 12715), C.I. Solvent Red 81, C.I. Solvent Red 82, C.I. Solvent Red 84, C.I. Solvent Red 100, Orient Oil Scarlet &num;308 (Orient Chemical CO. r Ltd.), Soldan Red 3R (Chugai Kasei Co., Ltd.), Diaresin Red S (Mitsubishi Chemical Industries Ltd.), Sumiplast Red AS (Sumitomo Chemical Co., Ltd.), Diaresin Red K. (Mitsubishi Chemical Industries Ltd.), Sumiplast Red 3B (Sumitomo Chemical Co., Ltd.), Diaresin Red EL (Mitsubishi Chemical Industries Ltd.), Diaresin Red H (Mitsubishi Chemical Industries Ltd.), Diaresin Red LM (Mitsubishi Chemical Industries Ltd.), Diaresin Red G (Mitsubishi Chemical Industries Ltd.), Aizen Spilon Red GEH Special (Hodogaya Chemical Co., Ltd.). Pink: Diaresin Pink M (Mitsubishi Chemical Industries Ltd.), Sumiplast Pink R FF (Sumitomo Chemical Co., Ltd.). Violet: C.I. Solvent Violet 8 (C.I. 42535B), C.I. Solvent Violet 21, Diaresin Violet A (Mitsubishi Chemical Industries Ltd.), Diaresin Violet D (Mitsubishi Chemical Industries Ltd.), Sumiplast Violet RR (Sumitomo Chemical Co., Ltd.). Blue: C.I. Solvent Blue 2 (C.I. 42563B), C.I. Solvent Blue 11 (C.I. 61525), C.I. Solvent Blue 25 (C.I. 74350), C.I. Solvent Blue 36, C.I. Solvent Blue 55, Aizen Spilon Blue GNH (Hodogaya Chemical Co., Ltd.), Diaresin Blue G (Mitsubishi Chemical Industries Ltd.), Diaresin Blue C (Mitsubishi Chemical Industries Ltd.), Diaresin Blue J. A. H. K. N. (Mitsubishi Chemical Industries Ltd.), Vali Past Blue &num;2604 (Orient Chemical Co., Ltd.). Green: C.I. Solvent Green 3 (C.I. 61565). Brown: C.I. Solvent Brown 3 (C.I. 11360), Diaresin Brown A (Mitsubishi Chemical Industries Ltd.). Black: C.I. Solvent Black 3 (C.I. 26150), C.I. Solvent Black 5 (C.I. 50415), C.I. Solvent Black 7 (C.I. 50415), C.I. Solvent Black 22, C.I. Acid Balck 123 (C.I. 12195), Sumisol Black AR sol (Sumitomo Chemical Co., Ltd.), Vali Fast Black +1802 (Orient Chemical Co., Ltd.). Besides the typical examples of the hydrophobic dyes listed above, the hydrophobic dyes used for photographic materials for silver dye bleaching process and for diffusion transfer process are also used effectively in the present invention. Further, the hydrophobic dyes used in the present invention may be formed by loadining the dye precursors in the vinyl polymer latex, and then converting the dye precursors to dyes by a physical or chemical means such as heat treatment, pH change or addition of a developer. This method -is effective when the dye itself is sparingly soluble in a solvent for impregnation. The dye precursor may, for example, be a photographic coupler, and the developer may, for example, be a developing agent for photographic purpose. The ink of the present invention contains, as the main constituents, the vinyl polymer latex containing the hydrophobic dye, and an aqueous medium containing an organic solvent having an HLB value of 9.5 or less. The ink of the present invention may further contain various additives as required. For example, the ink is likely to be stored for long period of time, it is possible to add an antiseptic agent and a mildewproofing agent to.the ink of the present invention so as to prevent or suppress the growth of bacteria or mildew in the ink. It is known that various antiseptic agents are useful for this purpose. Preferable antiseptic agents are for example Bacillat 35 (1,3,5-hexahydrotriazine derivative available from Forbwerke Höechst A.G.) and the like. Further, it is possible to add a surface active agent for the purpose of adjusting the surface tention which governs the wetting of the ink of the present invention. It is desirable that the surface active agent used for this purpose is a nonionic surface active agent or an ionic surface active agent having the same electrostatic charge as that of the surfaces of the polymer latex particles. Examples of the nonionic surface active agent are alkyl ethers and alkyl phenyl ethers of polyoxyalkylene, siloxane-oxialkylene copolymers (e.g., L-5340 available from Union Carbide), and fluorine-based surface active agents (e.g., FC430 available from 3M). If a surface active agent having an HLB value of 9.5 or less is used, it is possible to further enchancing the permeation of the hydrophobic dye. The surface active agent is generally used in a proportion of 1% by weight or less, particularly 0.05 to 0.1% by weight, based on the whole ink composition. In addition, it is also possible to add various inorganic or organic buffers for the purpose of preventing the pH value of the ink from changing due to absorption of carbon dioxide gas mainly from ambient air when the ink is stored in a vessel or exists in the nozzle. Preferable buffers are for example carbonates such as sodium carbonate and potassium carbonate. It is practicable that the buffers are used in a proportion of 0.1 to 5% by weight, preferably 0.1 to 2% by weight based on the whole ink composition. Further, it is possible to add various kinds of chelating agents for the purpose of mask the metal and metal ion in the ink composition. Typical examples of the chelating agents are sodium glucinate, ethylenediamine tetraacetic acid (EDTA), disodium salt of EDTA, trisodium salt of EDTA, tetrasodium salt of EDTA, and sodium salt of diethylenetriaminopentaacetic acid. The chelating agent is generally used in a proportion of 0.1 to 5% by weight based on the whole ink composition. As described above, the ink composition of the present invention exhibits less bleeding, higher print quality, less risk of nozzle clogging and quick drying property on the printing paper, particularly the printing paper having a high sizing degree which is called the plain paper, as compared with the ink composition in which the dye is dissolved in medium, even in cases when it is a homogeneous ink composition in which a direct dye or an acid dye is dissolved in water and polyhydric alcohols or it is a dispersion type ink composition using a polymer latex. The present invention is described hereinbelow in further detail by the following non-limitative examples. Example 1 To 100 g of a vinyl polymer latex (solid content: 6% by weight) having the composition shown below, 100 g of acetone and 10 g of ethyl acetate were added. To the mixture thus obtained, 6 g of C.I. Solvent Blue 2 (C.I. No. 42563B) was gradually added with stirring by use of a stirrer. After the dye was dissolved uniformly, the solvent was removed on an evaporator to obtain a hydrophobic dye-containing aqueous dispersion having a dye concentration of 6% by weight. EMI27.1 To the aqueous dispersion thus obtained, 140 g of tetraethylene glycol dimethyl ether (HLB = 8.75) was added. The resulting mixture was then stirred uniformly to obtain the ink of the present invention. The ink of the present invention could be filtered through the Toyo Filter Paper No. 131 (available from Toyo Roshi Co., Ltd.) without clogging the filter paper. The ink of the present invention thus obtained exhibited a viscosity of 7.3 centipoise (cp) at normal temperature (250C) and a surface tension of 42.5 dyn/cm. Example 2 In 150 g of acetone, 6 g of C.I. Solvent Red 8 (C.I. No. 12715) was dissolved. Then, 100 g of a vinyl polymer latex (solid content : 8% by weight) having the composition shown below was gradually added dropwise to the resulting solution with stirring by use of stirrer. After adding all latex dropwise, the solvent was removed on an evaporator to obtain a hydrophobic dye-containing vinyl polymer latex having a dye concentration of 6% by weight. EMI27.2 To the thus obtained aqueous dispersion, 140 g of diethylene glycol monobutyl ether (HLB = 7.70) was added. The resulting mixture was then stirred uniformly to obtain the ink of the present invention. The ink of the present invention could be filetered through the Toyo Filter Paper No. 131 without clogging the filter paper. The ink of the present invention thus obtained exhibited a viscosity of 7.6 cp at the normal temperature (259C) and a surface tension of 30.5 dyn/cm. Example 3 To 100 g of a cation polymer latex (solid content: 10% by weight) having the composition shown below, 60 g of diethylene glycol monoethyl ether (HLB = 8.65), 60 g of diethylene glycol diethyl ether (HLB = 7.10), 20 g of diethylene glycol (HLB = 10.20, for viscosity adjustment), and 250 g of tetrahydrofuran were added. To the mixture thus formed, 7.2 g of a blue hydrophobic dye t2-tert-butylsulfamoyl-4-(2-methylsulfonyl-4-nitro- phenylazo)-5-(3-aminosulfonylbenzenesulfonamido)-1naphthol] was gradually added. The dye was dissolved uniformly, and tetrahydrofuran was removed on an evaporator to obtain the ink of the present invention consisting of a hydrophobic dye-containing polymer latex having a dye concentration of 3% by weight. The ink of the present invention filtered through the Toyo Filter Paper No. 131 exhibited a viscosity of 8.0 cp at normal temperature (250C) and a surface tension of 38.3 dyn/cm. EMI28.1 Comparative Example 1 For comparison, 140 g of ethylene glycol (HLB = 9.85) was added to 100 g of vinyl polymer latex obtained in the same way in Example 1, and the resulting mixture was stirred uniformly to obtain an ink for comparison. The ink for comparison thus obtained exhibited a viscosity of 7.7 cp and a surface tension of 47.1 dyn/cm. Comparative Example 2 Further, an ink for comparison having the composition described below, in which the solvent used had an HLB value of below 9.5 but which is of homogeneous type, was prepared. EMI29.1 C.I. Acid Red 80 3 parts Distilled water 57 parts Diethylene glycol monobutyl ether (HLB = 7.70) 30 parts Polyethylene glycol &num;400 10 parts The ink for comparison thus formed exhibited a viscosity of 5.8 cp at normal temperature (250 C) and a surface tension of 30.1 dyn/cm. Example 4 The ink compositions obtained in the above-described Examples and Comparative Examples were used for ink jet printing on two kinds of printing paper. In the ink jet printing, the ink printing equipment shown in Figs. 1 to 3 of United Stated Patent No. 4,189,734 was used by adjusting it to the parameters listed in Table 3. The results were as shown in Table 4. From Table 4, it will be clear that the ink of the present invention is superior to those of Comparative Examples. Table 3 EMI30.1 <tb> Printing <SEP> speed <SEP> 2,000 <SEP> dots/sec. <tb> Static <SEP> pressure <SEP> -0.07 <SEP> PSi <tb> Pulse <SEP> peak <SEP> pressure <SEP> 25.3 <SEP> PSi <tb> Pulse <SEP> voltage <SEP> 120 <SEP> V <tb> Pulse <SEP> width- <SEP> 110 <SEP> uS <tb> Olifice <SEP> diameter <SEP> 0.003 <SEP> inch <tb> Table 4 EMI31.1 <tb> <SEP> Drying <SEP> speed <SEP> on <tb> <SEP> paper <SEP> 1) <SEP> Dot <SEP> quality <SEP> Nozzle <SEP> clogging <tb> Ink <SEP> Plain <SEP> Absorptive <SEP> Plain <SEP> Absorptive <SEP> After <SEP> standing <tb> com <SEP> paper* <SEP> paper** <SEP> paper <SEP> paper <SEP> 2 <SEP> hours <SEP> in <SEP> room <tb> Ink <SEP> of <SEP> Within <SEP> Within <SEP> Good <SEP> Good <SEP> None <tb> <SEP> q4 <SEP> o <tb> Ink <SEP> of <SEP> II <SEP> ID <SEP> II <SEP> II <tb> <SEP> a <SEP> 2 <tb> <SEP> Ink <SEP> of <SEP> DI <SEP> ID <SEP> DI <tb> <SEP> Pita) <SEP> a <SEP> 3 <tb> Ink <SEP> m <SEP> a <SEP> of <SEP> O <SEP> w <SEP> razzMore <tb> n <SEP> ;2 <SEP> ffi <SEP> 5 <SEP> 3 <SEP> 10 <SEP> sec. <SEP> II <SEP> ID <SEP> DI <tb> 3 <SEP> crJ <SEP> Ya <tb> Ink <SEP> of <SEP> Within <SEP> Within <SEP> Bad <SEP> Somewhat <SEP> bad <tb> <SEP> a <tb> <SEP> Example <SEP> 2 <SEP> < <tb> <SEP> + <SEP> a) <SEP> g <SEP> g <tb> <SEP> < <SEP> z <SEP> O <SEP> : <SEP> : <SEP> : <SEP> 1O <tb> <SEP> z <SEP> z <SEP> O <SEP> Q <SEP> O <tb> <SEP> Q <tb> <SEP> e <SEP> o <tb> <SEP> n <SEP> > &num; <SEP> X <tb> <SEP> O <SEP> z <SEP> h <SEP> < <SEP> O <SEP> C <SEP> <SEP> e <SEP> ^ <SEP> h <SEP> &commat; <SEP> <SEP> C} <SEP> ¯I <SEP> e <tb> <SEP> &commat;H <SEP> O <SEP> z <SEP> z <SEP> &commat; <SEP> : <SEP> : <SEP> &commat; <SEP> X <tb> <SEP> X <SEP> XU <SEP> Wu <SEP> a- <SEP> &num;X <tb> <SEP> X <SEP> h <SEP> i <SEP> t <SEP> H <SEP> 3 <SEP> H <tb> <SEP> Se <tb> <SEP> ,4 <SEP> ffi <SEP> &num; <SEP> a <SEP> . <SEP> n <SEP> e <tb> <SEP> > <SEP> = <SEP> z <SEP> < <SEP> U <SEP> A <SEP> d <SEP> V <tb> <SEP> S4 <SEP> ,1 <SEP> 0 <SEP> = <SEP> ZU <SEP> S <SEP> = <SEP> O <SEP> < <SEP> d <SEP> z <SEP> &commat; ; <tb> <SEP> n <SEP> H <SEP> 4 <SEP> 4 <SEP> al <SEP> <SEP> X <SEP> X <tb> <SEP> z <SEP> 2 <SEP> 31 <SEP> <SEP> X- <SEP> S <tb> <SEP> / <SEP> e <SEP> o <tb> <SEP> / <SEP> l <SEP> <SEP> X <SEP> > <SEP> H <SEP> > <SEP> N <tb> <SEP> / <SEP> X <SEP> X <SEP> 4 <tb> <SEP> / <SEP> UX <SEP> q-l <SEP> ¯I <SEP> I <SEP> t <SEP> w <SEP> hI <SEP> q4 <SEP> hI <tb> <SEP> / <SEP> 0 <SEP> O <SEP> z <SEP> O <SEP> Q <SEP> O <SEP> z <SEP> O <SEP> Z <SEP> S <SEP> O <SEP> e <SEP> ffi <tb> <SEP> / <SEP> aS <SEP> aX <SEP> a <SEP> 2S <SEP> aSH <SEP> XtX <tb> <SEP> / <SEP> CO <SEP> NX <SEP> AX <SEP> X <SEP> AOX <SEP> OX <tb> <SEP> / <SEP> H <SEP> U <SEP> H <SEP> 14 <SEP> H <SEP> lil <SEP> H <SEP> gl <SEP> H <SEP> U <SEP> IY <SEP> H <SEP> U <SEP> li3 <tb> * The sizing degree of the plain paper was 23 sec. ** The sizing degree of the absorptive paper was 3 sec. The sizing degree was determined by the Stöckigt method according to JIS P 8122. 1) Drying speed on paper: Time of drying until the ink showed no scratches when touched by fingers.

Claims: Claims: 1. An ink composition for ink jet printing comprising vinyl polymer latex particles which contain a hydrophobic dye and which are essentially insoluble in and non-swelling with water, an organic solvent having a hydrophilliclipophillic balance of 9.5 or less, and an aqueous medium. 2. The ink composition according to Claim 1, wherein said organic solvent having a hydrophilic-liphophilic balance of 7.0 to 9.5. 3. The ink composition according to Claim 1 or 2, wherein said organic solvent is at least one solvent selected from the group consisting of monohydric or polyhydric alcohols and their derivatives, cyclic ethers, and lactones. 4. The ink composition according to any one of Claims 1 to 3,wherein si vinyl polymer latex particles are constituted of a polymer of at least one monomer selected from the group consisting of an acrylate, a methacrylate, an acrylamide, a methacrylamide, a vinyl ester, a vinyl halide, a vinylidene halide, a vinyl ether, a sty ene, an a,8-ethylenically unsatu ated monomer, an acrylonitrile, a diacrylate, a dimethacrylate, and a compound having a hydrophilic group. 5. The ink composition according-to Claims 4, wherein said compound having a hydrophilic group is a sulfonate. 6. The ink composition according to Claim 5, wherein said sulfonate is 2-methyl propane sulfonate-2-acrylamide. 7. The ink composition according to Claim 4, wherein said compound having a hydrophilic group is a compound having a polyoxyethylene group. 8. The ink composition according to Claim 7, wherein said compound having a polyoxyethylene group is a compounds having a following formula [I]: EMI34.1 (wherein R represents a hydrogen atom or a methyl group, and n is an integer of 1 to 101. 9. The ink composition according to Claim 4, wherein said compound having a hydrophilic group is a quaternary ammonium salt. 10. The ink composition according to Claim 9, wherein said quaternary ammonium salt is a compound having a following formula [II]: EMI34.2 [wherein R represents a hydrogen atom or a methyl group; R1, R2 and R3 represent independently selected from the group of a lower alkyl group; and 23 re presents an anion). 11. The ink composition according to any one of the preceding claims wherein said vinyl polymer latex particles further contain a cross-linkable monomer. 12. The ink composition according to Claim 11, wherein said cross-linkable monomer is a divinyl benzene. 13. The ink composition according to any one of the preceding claims wherein said vinyl polymer latex particles contain polymer particles consisting of radical-polymerizable vinyl monomer by use of the emulsion polymerization. 14. The ink composition according to any one of the preceding claims wherein said vinyl polymer latex particles have a particle size of 0.01 to 1.0 pm. 15. The ink composition according to Claim 14, wherein said vinyl polymer latex particles have a particle size of 0.02 to 0.5 pm. 16. The ink composition according to any one of the preceding claims1 wherein said hydrophobic dye is selected from the group consisting of monoazo, anthraquinone, metal complex type monoazo, diazo, phthalocyanine, and triallylmethane dyes. 17. The ink composition according to any one of the preceding claims, wherein the ink further comprises a surface active agent. 18. The ink composition according to claim 17, wherein said surface active agent is selected from the group consisting of nonionic surface active agent and ionic surface active agent having the same electrostatic charge as that of the surfaces of the polymer latex particles. 19. The ink composition according to Claim 17, wherein said surface active agent is contained in an amount of 0.05 to 1% by weight in said ink composition. 20. The ink composition according to any one of the preceding claims, wherein the ink further comprises a buffer. 21. The ink composition according to Claim 20, wherein said buffer is selected from the group consisting of an inorganic buffer and an organic buffer. 22. The ink composition according to Claim 20, wherein said buffer is selected from the group consisting of sodium carbonate and potassium carbonate. 23. The ink composition according to any one of Claims 20 to 22, wherein said buffer is contained in an amount of 0.1 to 5% by weight in said ink composition. 24. The ink composition according to any one of the preceding claims, wherein the ink further comprises a chelating agent. 25. The ink composition according to Claim 24, wherein said chelating agent is selected from the group consisting of sodium glucinate, ethylenediamine tetraacetic acid (EDTA), disodium salt of EDTA, trisodium salt of EDTA, tetrasodium salt of EDTA, and sodium salt of diethylenetriaminopentaacetic acid. 26. The ink composition according to Claim 24 or 25, wherein said chelating agent is contained in an amount of 0.1 to 5% by weight in said ink composition.

Inventors: KITAMURA, SHIGEHIRO, KOBAYASHI, TATSUHIKO
Applicants: KONISHIROKU PHOTO INDUSTRY CO. LTD.
Application year: 1982
Main classification: C09D11
IPC codes: C09D11, B41M5