Synthetic woven double-velour graft

Abstract: A woven double-velour fabric of synthetic fiber provides an excellent structure for ingrowth and adhesion of tissue thereto and can be woven tightly enough so that preclotting may be omitted if so desired. The features recited are achieved through the use of appropriate combinations of preshrunk, texturized yarn with unshrunk, untexturized yarn.

Description: Background of the invention Vascular grafts of synthetic fiber are now widely used, a variety of constructions and a variety of materials being available. A principal factor in selection of a particular graft is the porosity of the fabric of which the graft is composed. This factor is significant because the porosity controls both the tendency to hemmorrhage and the ingrowth of tissue into the wall of the graft. The general procedure for implantation of a graft includes the step of preclotting, a step in which the graft is immersed in the blood of the patient after which the graft is allowed to stand for a period long enough for clotting to ensue. As a result, when the graft is implanted surgically, hemmorrhaging does not occur; yet, growth of tissue into the wall of the graft can proceed. This growth is extremely important, since, eventually, the wall of the graft simulates the wall of the vessel which it replaces and, if all goes property, provides a lumen which remains open and free of clots. The degree of adhesion of tissue to the wall of the graft varies with the material used. Thus, V. J. Lombardi in U.S. Patent No. 3,561,441 discloses the use of a non-sticking material having loops thereon for use in covering and treating wounds. The material which he proposed to use is a polyfluorinated polyolefin filament, spun on a plastic ribbon form. Lombardi discloses that, as a result of the non-stick property, the fabric can be removed from a wound periodically as a step in the changing of the dressing without tearing open the wound itself. Obviously, such a material is not suitable for use where the material is to remain within the body. L. R. Sauvage in U.S. Patent No. 3,878,565 has disclosed a tubular textile synthetic cardio-vascular prosthesis of polyester or other synthetic fiber, the prosthesis consisting of a body having a multiplicity of fiber loops extending outwardly from the surface thereof. Also, as shown in his Figures 2A, the body is crimped into irregular, circumferential corrugations. Such corrugations are intended to provide protection against kinking or collapse of the tubing and narrowing of the lumen thereof as a result of bending or other factors. However, the degree of protection afforded by such irregular corrugation varies over the lengths of tne tube and can be below the required level of protection at specific regions. While the construction of Sauvage facilitates growth of tissue exterior to the body or trellis of the tubular graft, the absence of loops on the interior of the tubing may result in exposure of the synthetic filaments of which the tubing is composed. Furthermore, the Sauvage graft is circularly-knit so that the technique which provides the fabric loops in the Sauvage graft is not applicable to woven tubing. Liebig et al in U.S. Patent No. 4,047,252 have described a synthetic vascular graft of double velour fabric material which is warp-knit from a fiber or filament to which growing tissue can adhere. The fabric is formed as a trellis of non-texturized yarn with loops formed of texturized yarn. The preferred fiber is stated to be polyester, and an especially preferred fiber is that sold under the trade name of Dacron by Dupont. As is well known, Dacron is polyethylene terephthalate. The Liebig et al fabric, while presenting an excellent substrate for ingrowth of tissue is sufficiently porous so that preclotting is generally necessary in the use of this material. Woven fabrics, in general, have lower porosities than do knit fabrics, whether warp-knit or circularly knit, but do not present so suitable a structure for tissue ingrowth. Thus, while woven fabrics of very low porosity are available, they are not so suitable for tissue ingrowth as are the double velours, namely, those having velour loops on both the inner and outer surfaces of the fabric. As is evident, it would be desirable that graft fabric whether tubular or flat, have low porosity and facilitate the growth of tissue along both the interior and exterior surfaces thereof. Summary of the invention In accordance with the present invention there is provided a low porosity synthetic velour prosthesis of a tightly woven material to which tissue can adhere characterised by a double velour fabric material having loops standing out from both faces and formed by compacting a fabric having loops on both faces and woven from a warp yarn (14, 16) of untexturised unshrunk yarn (14) and texturized preshrunk yarn (16), wherein the loops are formed from the texturised preshrunk yarn (16), the yarns being independent of each other, i.e. not twisted together, and a fill yarn (13) of either untexturized unshrunk yarn alone or of untexturized unshrunk yarn twisted together with texturized preshrunk yarn, the prosthesis being adapted to be used as a vascular graft without the need for preclotting. The invention therefore provides a synthetic graft material woven from a fiber or filament to which growing tissue can adhere. A preferred fiber is polyester, and an especially preferred fiber is that sold under the trade name of Dacron (Registered Trade Mark) by Dupont. However. it is to be understood that any comparable fiber or yarn is to be included as a suitable alternate or substitute. Further, the scope of the invention is to be considered as including combinations of different fibers, such combinations presenting advantages due to differences in shrinkage during compaction. In order to facilitate growth of tissue through and over both surfaces of fabric in accordance with the present invention, fiber loops are provided on both surfaces. Where the fabric is in the form of tubing, loops are provided on the interior as well as on the exterior thereof. Where the fabric is in the form of tubing, in order to avoid interference with the flow of blood in the lumen of said tubing, the fiber loops on the interior thereof are shorter. i,e,. smaller than those on the exterior thereof. The ratio of the length of the interior loops to the length of the exterior loops may be described as x/y where x varies from 1 to 4 and y varies from 5 to 8. In the preparation of the fabric of the present invention, both preshrunk, texturized yarn and unshrunk, untexturized yarn are utilized. The warp is comprised of both types of yarn, and the fill may be of the unshrunk, untexturized yarn alone or may be used in combination with preshrunk, texturized yarn, the two types of yarn being twisted together (in the fill only) prior to weaving. The method of preshrinking and texturizing the yarn is well known to those skilled in the art. A preferred weave is as follows: Warp: 1/70/54 (5z)+2/40/27 texturized. preshrunk. Fill: 1/170/54 (5z)+2/40/27 texturized preshrunk (1.5s). Pattern: 070/205/6/4, 30 dent/reed, 8 ends/dent. Greige count: 64 picks/in., (about 26 picks/cm) 122≠10% ends/in., (48≠10% ends/cm) off of the loom. The aforenoted describes the loom set-up for weaving double-velour grafts, in accepted terminology. Subsequent to weaving, the fabric is compacted as described in U.S. Patent 4,209,859, column 3, line 18. The principal features of the graft in accordance with the present invention result from the fact that the preshrunk, texturized yarn of which the loops are composed shrinks far less during compaction than does the unshrunk, untexturized material. As a result, the fabric is compacted in both the warp and the fill directions, while the loops of the preshrunk material shrink far less or not at all during the compaction process. This difference in shrinkage causes loops to stand out from the body of the fabric which may be termed a trellis. Where the fabric is in tubular form, it is generally crimped to eliminate the danger of kinking or collapse of the tubing at any point. Bifurcated grafts may also be prepared, the grafts may be viewed as having three legs coming together at a crotch. All three legs are preferably crimped. In the immediate region of the crotch the bifurcated graft mav be either crimped or uncrimped. An object of the present invention is therefore to provide a closely woven double-velour synthetic vascular graft and graft material to which tissue can adhere readily. The closely woven double-velour, synthetic vascular graft preferably has loops on the exterior of said fabric which extend outwardly further than the loops on the interior of said fabric extend inwardly. The graft may be corrugated and of uniform strength throughout. A particularly important object of the present invention is to provide a closely-woven double-velour synthetic vascular graft and graft material which provides for rapid tissue ingrowth and which is of a porosity low enough so that pre-clotting may be avoided. Brief description of the drawings For a fuller understanding of the invention, reference is had to the following description taken in connection with the accompanying drawings in which: Figure 1 is a closely-woven, double-velour fabric prepared in accordance with the present invention; Figure 2 is a view taken along line 2-2 of Figure 1; and Figure 3 is a view of a circumferentially-crimped, bifurcated vascular graft in accordance with the present invention. Description of the preferred embodiments To prepare for the weaving of a graft fabric in accordance with the present invention, yarn is first preshrunk and texturized, using techniques well known to those skilled in the art. The preferred yarn material is polyethylene terephthalate, available from Dupont under the trade name of Dacron. A suitable yarn is two-ply, 40 denier with twenty-seven filaments to each ply. However, yarn which is either heavier or lighter than 40 denier and which contains more or less than 27 filaments per bundle may be used. In weaving the fabric, the warp must contain both the preshrunk, texturized yarn and unshrunk untexturized yarn. The two yarns are independent of each other. i.e., they are not twisted together. It is significant that in subsequent treatment of the fabric (the compaction step) the unshrunk, untexturized yarn will shrink substantially whereas the texturized, preshrunk material will change in length only slightly, if at all. The fill may consist of unshrunk, untexturized yarn alone or, preferably, consists of both unshrunk, untexturized yarn and preshrunk, texturized yarn. The two yarns are twisted together prior to weaving. The preferred weave for the fabric is described as follows: Warp: 1/70/54 (5z)+2/40/27 texturized, preshrunk. Fill: 1/70/54 (5z)+2/40/27 texturized, preshrunk (1.5s). Pattern: 070/205/6/4, 30 dent/reed, 8 ends/dent. Greige count: 64 picks/in., (about 26 picks/cm.) 122≠10% ends/in., (48≠10% ends/cm.) off of the loom. It should be noted that the warp must include both the preshrunk texturized yarn and the unshrunk untexturized yarn; the fill may consist of untexturized, unshrunk yarn alone. A fabric in accordance with the present invention is shown in Figure 1 in which the warp direction is shown by the arrow 11 and the fill direction is indicated by the arrow 12. The fill yarns 13 are shown in Figure 1 as being spaced apart for convenience in representation. However, in general, the fill yarns 13 are woven as tightly as possible with warp yarns 14. The yarns indicated by reference numeral 13 are to be considered as representing either unshrunk, untexturized yarn twisted together with preshrunk, texturized yarn or the unshrunk, untexturized yarn by itself. The yarns indicated by the reference numeral 14 are the unshrunk, untexturized material and the yarns indicated by the reference numerals 16 are the preshrunk, texturized material. Figure 2 is a view taken along line 2-2 of the Figure 1 and shows fill yarns 13, each yarn 13 consisting of filaments 15. As aforenoted, fill yarns 13 may consist of unshrunk, untexturized material alone or of the two types of yarn twisted together, that is, both the preshrunk and unshrunk yarns. Fill yarn 13 is tightly interwoven with warp yarn 14 which is the untexturized material. Also, loosely interwoven with fill 13 is loop yarn 16 which is the preshrunk, texturized yarn. In the pattern shown in Figure 2, the interior 18 of the fabric is the lowermost side and the exterior 19 is the uppermost side. As shown in Figure 2, interior loop 16 passes under four fill yarns and passes over six fill yarns. Two of these loop yarns are shown in Figure 1 and are indicated by the reference numeral 16. As will be noted, adjacent warp loops need not pass over and pass under the same fill yarns. Thus, a variety of patterns becomes available and easily made. After weaving, the fabric, whether flat or woven in tubular form, is compacted. The method of compaction is described in U.S. Patent No. 4,209,859, or other suitable means may be used. The compaction is an extremely important step in that the unshrunk, untexurized yarn shrinks substantially while the preshrunk texturized yarn shrinks very little during this treatment with the result that the loops of the preshrunk material stand out from the two surfaces of the fabric. An extremely important use of the fabric is as a vascular graft. For this purpose, the fabric must be woven in tubular form, either straight, or bifurcated. In either form, it is desirable that the fabric be circumferentially crimped in order to prevent kinking or collapse of the lumen at any point along the tubes. A bifurcated tube is shown in Figure 3 in which both the larger and the smaller-diameter tubes, indicated by the reference numerals 21 and 22 are crimped, except in the immediate vicinity of crotch 23, the three legs of the vascular graft being in the form of a Y. In general, the diameters of legs 22 are substantially less than the diameter of main tube 21. Tests have shown that the porosity of the woven double-velour is not quite as low as that of a woven fabric prepared with an untexturized warp. While the very lowest porosity is desirable so far as hemmorrhaging is concerned, a fabric woven with the untexturized warp does not provide so advantageously for growth of tissue through the trellis as does the woven double-velour described herein. Accordingly, the combination of relatively low porosity with both interior and exterior loops on the surfaces of the fabric is such that preclotting may be omitted if desired while yielding an excellent substrate for tissue ingrowth.

Claims: A low porosity synthetic velour prosthesis of a tightly woven material to which tissue can adhere characterised by a double velour fabric material having loops standing out from both faces and formed by compacting a fabric having loops on both faces and woven from a warm yarn (14, 16) of untexturised unshrunk yarn (14) and texturized preshrunk yarn (16), wherein the loops are formed from the texturised peshrunk yarn (16), the yarns being independent of each other, i.e. not twisted together, and a fill yarn (13) of either untexturized unshrunk yarn alone or of untexturized unshrunk yarn twisted together with texturized preshrunk yarn, the prosthesis being adapted to be used as a vascular graft without the need for preclotting. A low porosity, synthetic velour prosthesis according to claim 1 wherein said fabric is woven in tubular form and, circumferentially crimped. A low porosity, synthetic velour prosthesis according to claim 2, wherein said tubular form is in the form of a Y, having two legs and a crotch at the junction of the legs, said woven fabric being uncrimped in the region immediately proximate said crotch.

Inventors: CUMMINGS DENNIS E, LIEBIG WILLIAM J, CUMMINGS, DENNIS E., LIEBIG, WILLIAM J.
Applicants: MEADOX MEDICALS INC, MEADOX MEDICALS, INC.
Application year: 1982
Main classification: A61F2
IPC codes: A61L27, A61F2, D03D27