GLASS-FILLED POLYARYLENE SULFIDE COMPOSITIONS CONTAINING ORGANOSILANES

Abstract: Properties such as flow rate and hydrolytic stability of glass-filled polyarylene sulfide compositions can be mod­ ified by the addition of certain organosilanes.

Description: GLASS-FIlm) POLYARYLENE SUICIDE COMPOSITIONS CONTAINING ORGANOSILANES This invention relates to certain organosilane-containing glass-filled polyarylene sulfide compositions. This invention also relates to a method for modifying properties of glass-filled polyarylene sulfide compositions by adding certain organosilanes to the compositions. More particularly this invention relates to methods for increasing and decreasing the flow rate of a glass-filled polyarylene sulfide and for improving the hydrolytic stability of a glass-filled polyarylene sulfide. The only patent disclosing organosilanes in glass-filled polyarylene sulfide compositions of which I am aware is U.S. 4,176,098 (Needham). The Needham patent teaches that small quantities (0.5 to 5 weight percent of the total composition) of silanes can be added to an arc resistant composition to improve its water resistance and linear coefficient of expansion. The arc resistant composition is produced by incorporating glass and other fillers and a substantial amount of clay or talc into a polyarylene sulfide. Needham states that "...it is believed that any silane can be utilized to impart improved water resistance and linear coefficient of expansion to the new arc resistant composition, presently preferred are the alkylsilanes, alkoxysilanes, and polymers thereof." Despite this broad language only a few specific silanes such as y-glycidoxypropyltrimethoxysilane, methyltrimethoxysilane, and methylmethoxysilane are recited by Needham. The utility of certain organosilanes to increase or decrease the flow rate of glass-filled polyarylene sulfide compositions is neither taught nor suggested. In a preprint from the American Chemical Society Division of Organic Coatings and Plastics Chemistry 40, 538-41 (1979) the effect of silanes on adhesion of size free glass fibers in thermoplastic (including polyphenylene sulfide) composites is examined. The organosilane compounds of my invention, however, are not disclosed. I have discovered that certain organosilanes may be used in glass-filled polyarylene sulfide compositions to improve hydrolytic stability and/or to effect a change of flow rate. Accordingly, it is an object of my invention to provide new and useful compositions. A further object of my invention is to provide a method for modifying properties of glass-filled polyarylene sulfide compositions. More particularly it is an object of my invention to provide methods for improving hydrolytic stability and increasing or decreasing flow rates of glass-filled polyarylene sulfide compositions. These and other objects of my invention will become apparent from the disclosure and claims herein provided. Any uncured or partially cured polyarylene sulfide whether homopolymer, copolymer, terpolymer, and the like, or a blend of such polymers, can be used in the practice of any aspect of this invention. In this application an uncured or partially cured polymer is a polymer the molecular weight of which can be increased by either lengthening of a molecular chain or by cross-linking or by combination of both by supplying thereto sufficient energy, such as heat. A process which increases the molecular weight of the polymer shall be designated as a curing process. Particularly suited for use in this invention are those polyarylene sulfides having inherent viscosities in chloronaphthalene (0.2 gram polymer in 100 cc chloronaphthalene) at 2060.C. (402.80.F.) of at least about 0.08, preferably between about 0.1 and about 0.3, and more preferably between about 0.13 and 0.23. Examples of polymers which can be used in this invention are disclosed in U.S. Patent No. 3,354,129. Other examples of polyarylene sulfides are poly(4,4'-biphenylene sulfide); poly(2,4-tolylene sulfide); a copolymer from p-dichlorobenzene, 2,4-dichlorotoluene, and sodium sulfide, and blends thereof. Of all of the polyarylene sulfides, polyphenylene sulfide (PPS) polymers are presently preferred for use with the invention. Generally the amount of organosilane to be used should be in excess of about 0.2 weight percent based upon total composition. The currently preferred range is about 0.2 to about 2 weighap3cCh6.3a, scope of this invention, however, encompasses a much broader range and requires only that an amount sufficient to increase or decrease the flow or to improve the hydrolytic stability of the composition be used. The amount of glass in the polyarylene sulfide should usually be at least about 10 weight percent based upon total composition. The currently preferred range is about 25 to about 60 weight percent. In addition to glass, other fillers may be present in the polyarylene sulfide so long as these fillers do not adversely affect the composition. The organosilanes found to be useful for curing or decreasing the flow rate of a glass-filled polyarylene sulfide include the following: 3-Glycidoxypropyltrimethoxysilane, 3-Mercaptopropyltrimethoxysilane, l-Benzylchloro-2-trimethoxysilylethane, beta-63,4-Epoxycyclohexyl)-ethyltrimethoxysilane, 2-p-Sufoxylazylethyltrimethoxysilane, and (p-Aminophenyl)trimethoxysilane. The scope of this aspect of my invention encompasses both uncured and at least partially cured mixtures of a glass-filled polyarylene sulfide and at least one of the above-identified organosilane flow decreasing or curing agents. When cured at a temperature greater than or about equal to its melting point, the resultant composition exhibits a substantial flow retarded characteristic. My invention also includes a method for curing and reducing the flow rate of glass-filled polyarylene sulfides by adding at least one of the above-identified organosilanes to a glass-filled polyarylene sulfide and curing the same at a temperature greater than or about equal to the melting point of the polyarylene sulfide. Although all polyarylene sulfides are contemplated to be suitable in the practice of my invention, polyphenylene sulfide is currently preferred. In the case of polyphenylene sulfide the curing temperature should be in excess of about 550?F. The currently preferred curing temperature is about 600?F but a wide temperature range is contemplated. Curing may be accomplished by mixing a glass-filled polyarylene sulfide and at least one of the organosilane curing agents in a blender and extruding the mixture at a sufficiently high temperature to effect curing. This is the currently preferred method since it obviates the need for a separate curing step after the molding process. The organosilanes found to be useful for increasing the flow rate of a glass-filled polyarylene sulfide include the following: 3-N- (Trimethoxysilylpropyl)polyethylenimine, N-beta-CAminoethyl)-gamma-aminopropyltrimethoxysilane, Diethylamino-3-trimethoxysilylpropyldisulfide, 3- (Diethylamino)propyltrimethoxysilane and 3-Aminopropyltriethoxysilane. I have found that by adding one of the above-identified organosilane flow increasing agents to a glass-filled polyarylene sulfide and heating the same at a temperature greater than or about equal to the melting point of the polyarylene sulfide, the resultant composition exhibits an increased flow rate. The scope of this aspect of my invention includes compositions of polyarylene sulfide and the above organosilanes both prior to and after heating. Polyphenylene sulfide is currently preferred, but all polyarylene sulfides are contemplated to be suitable. In the case of polyphenylene sulfide the heating temperature should be in excess of about 5500 F. The currently preferred heating temperature is about 600?F but a wide temperature range is contemplated. This aspect of my invention may be practiced by mixing a glass-filled polyarylene sulfide and at least one of the appropriate organosilanes in a blender and extruding the mixture at a temperature greater than or about equal to the melting point of the polyarylene sulfide. Operability of the invention has been demonstrated through a series of laboratory experiments. In each run 0.8 weight percent of an organosilane was added to 40 weight percent glass-filled 60 weight percent polyphenylene sulfide. The polyphenylene sulfide used is known under the trademark Ryton PR-06 (Phillips Petroleum Co.) and has a melt flow of 120+20 g/10 min. The mixture was stirred in a Welex blender and extruded at 600?F through a Davis Standard extrUudUer(.4 After extrusion the blend was dried for 3 hours at 350?F and then molded in a New Britain mold. The flow rate for each run was determined and appears in Table I. TABLE 0.8 Wt.% Silane Added to 40 Wt.% Glass-Filled Polyphenylene Sulfide Flow Rate, g/10 mins. at 600?F Without Organosilane Silane With Silane 1. 3-Glycidoxypropyltrimethoxysilane 23 1 2. 3-Mercaptopropyltrimethoxysilane 23 2 35 12 3. 1-Benzylchloro-2-Trimethoxysilylethane 48 0 37 0.1 4. beta-(3,4-Epoxycyclohexyl)-ethyltrimethoxy- 49 1 silane 5. 2-p-Sufoxylazylethyltrimethoxysilane 35 5 6. (p-AminophenylZtrimethoxysilane 48 10 7. Diethylamino-3-trimethoxysilylpropyl disul- 35 177 fide 8. 3- (Diethylamino)propyltrimethoxysilane 35 136 9. N-beta-(Aminoethyl)-gamma-aminopropyltri- 35 108 methoxylsilane 58 226 10. 3-Ureidopropyltriethoxysilane 58 134 11. 3-Aminopropyltriethoxysilane 58 139 12. Vinyltriethoxysilane 58 117 64 52 13. 3-N-(Trimethoxysilylpropylzpolyethylenimine 47 336 As evidenced by a corresponding decrease in flow rate the first six organosilanes facilitated curing of the glass-filled polyphenylene sulfide during the extruding process. Associated with the other organosilanes was an increase in flow rate. The increased flow rate attributable to this latter group of organosilanas appears to be due to depolymerization. Table II displays the results when organosilanes, successfully used as curing agents for glass-filled polyphenylene sulfide, are used with non-filled polyphenylene sulfide. TABLE II 0.8 Wt. Silane Added to Polyphenylene Sulfide Flow Rate, g/10 mins. at 600?F Without Organosilane Silane With Silane 1. 1-Benzylchloro-2-Trimethoxysilylethane 519 476 519 551 2. (p-Aminophenylitrimethoxysilane 519 523 519 1008 The absence of a decrease in flow rate indicates that the organosilanes are not useful as curing agents in non-filled polyphenylene sulfide. The presence of glass in the polyarylene sulfide is thought to be necessary for the successful practice of my invention. It is believed that the flow rate of the composition is decreased by a combination of two reactions: (1) the Teaction between the silane portion of the silane molecule and the hydroxyl groups attached to the glass fiber surfaces resulting in a chemical bond; and (2) the reaction between the other end of the silane molecule and the polyarylene sulfide backbone to form another chemical bond. This chemical binding of glass fiber and polyarylene resin is believed to be, at least in part, responsible for the decrease in flow rate. This theory is offered only as a possible explanation and is not intended to further limit or define my invention. I haze also discovered that certain organosilanes when compounded into cured or partially cured glass-filled polyarylene sulfide compositions provide hydrolytic stability to the compositions. The following examples serve to identify the organosilanes which are useful for this aspect of my invention. The examples further serve to illustrate the operability of my invention. * It is noted that many of the organosilanes useful within the inventive concept contain one or more nitrogen atoms, for example. in the form of a substituted or unsubstituted amino, imino or a:zido group In the naming of the organosilanes the prefixes beta and gamma denote the 2 and 3 position, resp. and vice versa. EXAMPLE I This example describes the procedure used to prepare the samples and the subsequent testing. The method of preparation was generally as follows: 16 grams of a particular silane was added dropwise tq 800 grams of .125 inch milled glass fibers (Owen-Corning) in a Welex Blender after which the contents were placed in a fiber drum and tumbled along with 1200 grams of polyphenylene sulfide known under the trademark Ryton PR-06 (Phillips Petroleum Co.) having a melt flow of 120+20 g/10 min. The mixture was extruded through a Davis Standard extruder at 6000E (3160C), dried in a 3500F (1770. C) oven for 3 hours and molded using a New Britain molding machine (barrel 6000F, mold 2750.F) into bar specimens, 8 inches x 1 inch x .125 inch. The bars (generally 3 per set) were immersed in water in a pressure cooker at 1200C and 15 psig for 150 hrs., cooled, dried in an oven for a few hours at 110 C, conditioned overnight at rooni temperature and evaluated. Tensile strength was determined in accordance with test method ASTM D 882-56T. These results, shown in the following tables, provide a good indication of hydrolytic stability. Percent loss of tensile strength values below about 15% are preferred but any value below that of the control (i.e. no silanes) is acceptable. Effect of Various Organosilanes on the Hydrolytic Stability of PPS-Glass Compositions Tensile Strength, MPa Organosilane (a) % Loss After No. Tradename Chemical Identity Initial 150 hrs/120C/15 psi TABLE III 1 - Control - no silane 63.0 29.4 2 An-1120 N-beta-(Aminoethyl)-gamma-aminopropyl- 67.5 22.1 trimethoxysilane 3 A-1160 3-Ureidopropyltrimethoxysilane 62.7 11.4 4 A-1100 gamma-Aminopropyltriethoxysilane 71.5 10.8 5 A-151 Vinyltriethoxysilane 71.7 7.0 TABLE IV 6 - Control - no silane 44.9 40.5 7 Z6032 N-{2-[3-(Trimethoxysilyl)propylamino]ethyl} -p-vinylbenzylammonium chloride 58.5 11.3 8 T2902 2-(Benzylchloro)ethyltrimethoxysilane 52.2 6.9 9 Z6070 Methyltrimethoxysilane 49.7 29.0 TABLE V 10 - Control - no silane 136.3 26.9 11 A-1893 beta-Mercaptoethyltrimethoxysilane 88.1 28.9 12 Z-6040 gamma-Glycidoxypropyltrimethoxysilane 100.3 31.7 13 A-189 3-Mercaptopropyltrimethoxysilane 86.9 4.9 TABLE VI 14 - Control - no silane 65.5 25.8 15 T2905 2-(Trimethoxysilyl)ethylphenylsulfonyl- 86.4 41.9 azide 16 A-189 3-Mercaptopropyltrimethoxysilane 75.3 25.5 17 Silar 1104 3-(Diethylamino)propyltrimethoxysilane 72.5 12.7 18 Si-69 Bis(3-triethoxysilylpropyl)tetrasulfide 62.4 10.7 19 A-1120 N-beta(Aminoethyl)-gamma-aminopropyltri- 64.7 9.0 methoxysilane 20 - Trimethylsilylpropylazide 76.6 8.1 21 Silar 1249 n-Propyltriethoxysilane 57.4 5.9 22 - N,N'-Diethyltrimethoxysilylpropylthio- 62.4 3.4 sulfenamide TABLE VII 23 - Control - no silane 66.6 37.4 24 P0156 N-Phenylaminopropyltrimethoxysilane 66.5 59.2 25 P09830 Octyltrichlorosilane 48.5 33.2 26 PS076 3-N-(Trimethoxysilylpropyl)poly- 60.7 24.9 (ethylenimine) 27 T4250 Tris(trimethoxysiloxy)phenylsilane 60.0 23.8 28 A-172 Vinyl tris(2-methoxyethoxy)silane 77.0 20.9 29 P0330 Phenyltrimethoxysilane 59.7 17.3 30 Z6062 3-Mercaptopropyltrimethoxysilane 73.8 4.5 31 P09775 Octadecyltriethoxysilane 39.1 1.8 (a) A series from Union Carbide Z series from Dow Corning T,P series from Petrarch Systems, Inc. Silar from DeGussa SummarY of Tables III, IV, V, VI, and VII Eor the convenience of comparison, the data in the preceding tables were normalized by averaging the five control runs from each table and proportionating each individual silane-containing composition value, in each table, relative to the control in each table and relative to the average control value. The values listed in Table VIII are shown in descending value. Organosilanes associated with a normalized percent loss less than that of the control (i.e. 32.0) are the hydrolytic stabilizing agents of my invention. TABLE VIII Summary of Tables III, IV, V, VI and VII Normalized Reference % Loss in Tensile Strength No. Table Organosilane After 150 hrs/120C/15 psi 31 VII Octadecyltriethoxysilane 1.5 30 (13, 16) VII (V, VI) 3-Mercaptopropyltrimethoxysilane 3.8 (5.8, 31.6) 22 VI N,N'-Diethyltrimethoxysilylpropylthio- 4.2 sulfenamide 8 IV 2-(Benzylchloro)ethyltrimethoxysilane 5.5 7 IV N-{2-[3-(Trimethoxysilyl)propylamino]ethyl}p-vinylbenzylammonium chloride 8.9 21 VI n-Propyltrimethoxysilane 7.3 5 III Vinyltriethoxysilane 7.6 20 VI Trimethylsilylpropylazide 10.0 19 (2) VI (III) N-beta-(Aminoethyl)-gamma-aminopropyltri- 11.6 (24) methoxysilane 4 III gamma-Aminopropyltriethyoxysilane 11.7 3 III 3-Ureidopropyltrimethoxysilane 12.4 18 VI Bis(3-triethoxysilylpropyl)tetrasulfide 13.2 29 VII Phenyltrimethoxysilane 14.8 17 VI 3-(Diethylamino)propyltrimethoxysilane 15.7 28 VII Vinyl tris(2-methoxyethoxy)silane 17.8 27 VII Tris(trimethoxysiloxy)phenylsilane 20.4 26 VII 3-N-(Trimethoxysilylpropyl)poly- 21.3 (ethylenimine) 9 IV Methyltrimethoxysilane 22.9 25 VII Octyltrichlorosilane 28.4 -------------------------Control - No Silane-------------------------------- 32.0 11 V beta-Mercaptoethyltrimethoxysilane 34.3 12 V gamma-Glycidoxypropyltrimethoxysilane 37.7 15 VI 2-(Trimethoxysilyl)ethylphenylsulfonylazide 51.9 EXAMPLE II This example illustrates the use of mixed glass-filled polyphenylene sulfide compositions. The procedure described in Example I was repeated with the exception that a mixture of silanes was used at the same total organosilane concentration. These results, listed in Table IX, suggest mixtures of organosilanes can be used but with no particular advantage from a tensile strength standpoint. The values shown are normalized in the manner previously described herein. TABLE IX Effect of Mixtures of Organosilanes in PPS Compositions Normalized % Loss in Reference Organosilane Mixture Tensile Strength After No. Table (Equal Wts of Each) 150 hrs/120C/15 psi 4 III A-1100 11.7 30 VII A-Z6062 3.8 5 III A-151 7.6 - - A-1100/Z6062 16.0 - - A-151/Z6062 13.6 - A-1100/Z6062/A-151 119 EXAMPLE III This example demonstrates that organosilanes can be useful in glass-filled polyarylene sulfide compositions containing other ingredients such as fillers, pigments, etc. The procedure described in Example I was again repeated but with a mineral filled composition as shown below in Table X. The organosilane was added to the talc in a Welex blender before further compounding. The data listed suggest that adding the organosilane to the talc before compounding with the other ingredients, particularly glass, may be beneficial. TABLE X Effect of Organosilanes in Mineral Filled PPS-Glass Compositions Composition: Wt. % Grams Ingredient 34.3 682 PPS 34.3 682 Glass Unsized Fibers, 0.125 inch 29.6 589 Talc .3 5 TR-885 (Polyethylene lubricant) 1.0 20 Acrawax (N,N'-Ethylene bis stearamide, corrosion inhibitor) .5 9 Pigment - - Organosilane Tensile Strength, MPa Organosilane % Loss After No. Grams Chemical Identity Initial 150 Hrs/120C/15 psi 1 - Control - No silane 62.0 48.7 2 13.2 Z6032, N-{2-[3-(Trimethoxysilyl)propyl- 50.9 0 amino]ethyl}-p-vinylbenzylammonium chloride 3 5.3 A-189, 3-Mercaptopropyltrimethoxy- 53.1 6.4 silane 4 9.0 A-189, 3-Mercaptopropyltrimethoxy- 52.0 9.4 silane The following part of the description are specific embodiments 1 to 92 presented in the form of claims. 1. A composition comprising: a glass-filled polyarylene sulfide and a property modifying amount of at least one organosilane selected from the group consisting of Octadecyltriethoxysilane, Vinyltriethoxysilane, N-beta-(Aminoethyl)-gamma-aminopropyl trimethoxys ilane, 2-(Benzylchloro)ethyltrimethoxysilane, 3-Ureidopropyltrimethoxysilane, gamma-Aminopropyltrimethoxysilane, N-{2-[3-(trimethoxysilyl)propylamino]ethyl} p-vinylbenzylammonium chloride, N,N'-Diethyltrimethoxysilylpropylthiosulfenamide, n-Propyltrimethoxysilane, Trimethylsilylpropylazide, bis(3-Triethoxysilylpropyl)tetrasulfide, Phenyltrimethoxysilane, Vinyl tris (2-methoxyethoxy)silane, Tris(Trimethoxysiloxy)phenylsilane, 3-N- (Trimethoxvsilylpropyl)polyethylenimine, Octyltrichlorosilane, 3- (Diethylamino)propyltrimethoxysilane, beta-(3,4-epoxycyclohexyl)-ethyltrimethoxysilane, 2-p-Sufoxylazylethyltrimethoxysilane, (p-AminophenylJtrimethoxysilane, 3-Mercaptopropyltrimethoxysilane, 1-Benzylchloro-2-trimethoxysilylethane, Diethylamino-3-trimethoxysilylpropyldisulfide and 3-Aminopropyltriethoxysilane. 2. A composition in accordance with claim 2 wherein said glass-filled polyarylene sulfide is glass-filled polypropylene sulfide. 3. A composition in accordance with claim I wherein the amount of said organosilane is about 0.2 to about 2 weight percent based upon total composition. 4. A composition in accordance with claim 1 wherein said organosilane is Vinyltrietboxysilane. 5. A composition in accordance with claim 1 wherein said organosilane is Octadecyltriethoxysilane. 6. A composition in accordance with claim 1 wherein said organosilane is N,N'-Diethyltrimethoxysilylpropylthiosulfenamide. 7. A composition in accordance with claim 1 wherein said organosilane is 2- (Benzylchloro)ethyltrimethoxysilane. 8. A composition in accordance with claim 1 wherein said organosilane is N-{2-[3-(Trimethoxysilyl)propylamino]ethyl}p-vinylbenzylammonium chloride. 9. A composition in accordance with claim 1 wherein said organosilane is n-Propyltrimethoxysilane. 10. A composition in accordance with claim 1 wherein said organosilane is Phenyltrimethoxysilane. 11. A composition in accordance with claim 1 wherein said organosilane is Trimethylsilylpropylazide. 12. A composition in accordance with claim 1 wherein said organosilane is N-beta- (Aminoethyl)-gamma-aminopropyltrimethoxysilane. 13. A composition in accordance with claim 1 wherein said organosilane is gamma-Aminopropyltriethyoxysilane. 14. A composition in accordance with claim 1 wherein said organosilane is 3-Ureidopropyltrimethoxys ilane. 15. A composition in accordance with claim 1 wherein said organosilane is Bis(3-triethoxysilylpropyl)tetrasulfide. 16. A composition in accordance with claim 1 wherein said organosilane is 3-N-(Trimethoxysilylpropyl)polyethylenimine. 17. A composition in accordance with claim 1 wherein said organosilane is 3-(Diethylamino)propyltrimethoxysilane. 18. A composition in accordance with claim 1 wherein said organosilane is Diethylamino-3-trimethoxysilylpropyldisulfide. 19. A composition in accordance with claim 1 wherein said organosilane is 3-Aminopropyltriethoxysilane. 20. A composition in accordance with claim 1 wherein said organosilane is 3-Glycidoxypropyltrimethoxysilane. 21. A composition in accordance with claim 1 wherein said organosilane is 3-Mercaptopropyltrimethoxysilane. 22. A composition in accordance with claim 1 wherein said organosilane is l-Benzylchloro-2-trimethoxysilylethane. 23. A composition in accordance with claim 1 wherein said organosilane is beta-(3,4-Epoxycyclohexyl)-ethyltrimethoxysilane. 24. A composition in accordance with claim 1 wherein said organosilane is 2-p-Sufoxylazylethyltrimethoxysilane. 25. A composition in accordance with claim 1 wherein said organosilane is (p-Aminophenylztrimethoxysilane. 26. A composition in accordance with claim 1 wherein said organosilane is octyltrichlorosilane. 27. A composition consisting essentially of a glass-filled polyarylene sulfide and at least one organosilane selected from the group consisting of 3-Glycidoxypropyltrimethoxysilane and Methyltrimethoxys ilane. 28. A composition in accordance with claim 27 wherein the amount of said organosilane is about 0.2 to about 2 weight percent based upon total composition. 29. A method for modifying a property of a glass-filled polyarylene sulfide which comprises: (a) adding to said glass-filled polyarylene sulfide an organosilane selected from the group consisting of Octadecyltriethoxysilane, Vinyltriethoxysilane, N-beta- (Aminoethyl)-gamma-aminopropyl trimethoxysilane, 2- (Benzylchloro) ethyltrimethoxysilane, 3-Ureidopropyltrimethoxysilane, gamrda-Aminopropyltrimethoxysilane, N- - [3- (Trimethoxysilyl)propylaminoj ethylJ p-vinylbenzylamommium chloride, N ,N' -Diethyltrimethoxysilylpropylthiosulfenamide, n-Propyltrimethoxysilane, Trimethylsilylpropylazide, bis (3-Triethoxysilylpropyl)tetrasulfide, Phenyltrimethoxysilane, Vinyl tris (2-methoxyethoxy)silane, Tris (trimethoxysiloxy)phenylsilane, 3-N- (Trimethoxysilylpropyl)polyethylenimine, Octyltrichlorosilane, 3-(Diethylamino)propyltrimethoxysilane, beta- (3 ,4-epoxycyclohexyl)-ethyltrimethoxysilane, 2-p-Sufoxylazylethyltrimethoxysilane, (p-Aminophenyl) trimethoxysilane, 3-Mercaptopropyltrimethoxysilane, l-Benzylchloro-2-trimethoxysilylethane, I)iethylamino-3-trimethoxysilylpropyldisulfide, 3-Aminopropyltriethoxysilane, 3-Glycidoxypropyltrimethoxysilane and Hethyltrimethoxysilane to produce a mixture; and (b) raising the temperature of said mixture to a temperature equal to or above about the melting point of said polyarylene sulfide. 30. A method for decreasing the flow rate of a glass-filled polyarylene sulfide in accordance with claim 29 wherein said organosilane is selected from the group consisting of 3-Glycidoxypropyltrimethoxysilane, 3-Mercaptopropyltrimethoxysilane, l-Benzylchloro-2-trimethoxysilylethane, beta- (3, 4-Epoxycyclohexyl)-ethyltrimethoxy- silane, 2-p-Sufoxylazylethyltrimethoxysilane and (p-Aminophenyl)trimethoxysilane; and said mixture is subjected to a temperature equal to or above about the melting point of said polyarylene sulfide for a time sufficient to effect at least a partial cure of said mixture. 31. A method in accordance with claim 30 wherein said glass-filled polyarylene sulfide is glass-filled polyphenylene sulfide. 32. - A method in accordance with claim 30 or 31 wherein said organosilane is 3-Glycidoxypropyltrimethoxysilane. 33. A method in accordance with claim 30 or 31 wherein said organosilane is 3-Mercaptopropyltrimethoxysilane. 34. A method in accordance with claim 30 or 31 wherein said organosilane is 1-Benzylchloro-2-Trimethoxysilylethane. 35. A method in accordance with claim 30 or 31 wherein said organosilane is beta- (3, 4-epoxycyclohexyl) -ethyltrimethoxysilane. 36. A method in accordance with claim 30 or 31 wherein said organosilane is 2-p-Sufoxylazylethyltrimethoxysilane. 37. A method in accordance with claim 30 or 31 wherein said organosilane is p-Aminophenyltrimethoxysilane. 38. A method in accordance with claim 30 or 31 wherein said mixture is extruded at a temperature above about 550F. 39. A method in accordance with claim 30 or 31 wherein the weight percentage of said organosilane in said mixture is about 0.2 to about 2. 40. A method for increasing the flow rate of a glass-filled polyarylene sulfide in accordance with claim 29 wherein said organosilane is selected from the group consisting of 3-N- (Trimethoxysilylpropyl)polyethylenimine, N-beta-CAminoethyl)-gamma-aminopropyltrimethoxysilane, Diethylamino-3-trimethoxysilylpropyldisulfide, 3- (Diethylamino)propyltrimethoxysilane and 3-Aminopropyltriethoxysilane. 41. A method in accordance with claim 40 wherein said glass-filled polyarylene sulfide is glass-filled polyphenylene sulfide. 42. A method in accordance with claim 40 or 41 wherein said organosilane is 3-N- (Trimethoxysilylpropyl)polyethylenimine. 43. A method in accordance with claim 40 or 41 wherein said organosilane is N-beta- (Aminoethyl)-gamma-aminopropyltrimethoxysilan. 44. A method in accordance with claim 40 or 41 wherein said organosilane is Diethylamino-3-trimethoxysilylpropyldisulfide. 45. A method in accordance with claim 40 or 41 wherein said organosilane is 3- (Diethylamino)propyltrimethoxysilane. 46. A method in accordance with claim 40 or 41 wherein said organosilane is 3-Aminopropyltriethoxysilane. 47. A method in accordance with claim 40 or 41 wherein said mixture is extruded at a temperature above 550F. 48. A method in accordance with claim 40 or 41 wherein the weight percent, based upon total composition, of said organosilane is about 0.2 to about 2. 49. A method for improving the hydrolytic stability of a glass-filled polyarylene sulfide in accordance with claim 29 wherein said organosilane is selected from the group consisting of Octadecyltriethoxysilane, Vinyltriethoxysilane, N-beta-(Aminoethyl)-gamma-aminopropyl trimethoxysilane, 2-(Benzylchloro)ethyltrimethoxysilane, 3-Ureidopropyltrimethoxys ilane, gamma-Aminopropyltrimethoxysilane, 3-Mercaptopropyltrimethoxys ilane, N-{2-[3-(Trimethoxysilyl)propylamino]ethyl} p-vinylbenzylammonium chloride, N,N' -Diethyltrimethoxysilylpropylthiosulfenamide, n-Propyltrimethoxysilane, Trimethylsilylpropylazide, Bis (3-triethoxysilylpropyl)tetrasulfide, Phenyltrimethoxysilane, Vinyl tris (2-methoxyethoxy) silane, Tris (trimethoxysiloxy)phenylsilane, 3-N- (Trimethoxysilylpropyl)polyethylenimine, Octyltrichlorosilane and 3- (Diethylamino)propyltrimethoxysilane. 50. A method in accordance with claim 49 wherein said glass-filled polyarylene sulfide is glass-filled polyphenylene sulfide. 51. A method in accordance with claim 49 or 50 wherein said organosilane is Vinyltriethoxysilane. 52. A method ik accordance with claim 49 or 50 wherein said organosilane is Octadecyltriethoxysilane. 53. - A method in accordance with claim 49 or 50 wherein said organosilane is 3-Mercaptopropyltrimethoxysilane. 54. A method in accordance with claim 49 or 50 wherein said organosilane is N,N'-Diethyltrimethoxysilylpropylthiosulfenamide. 55. A method in accordance with claim 49 or 50 wherein said organosilane is 2- (Benzylchloro)ethyltrimethoxysilane. 56. A method in accordance with claim 49 or 50 wherein said organosilane is N- 2- [3- (Trimethoxysilyl)propylaminoJethylJ- p-vinylbenzylammonium chloride. 57. A method in accordance with claim 49 or 50 wherein said organosilane is n-Propyltrimethoxysilane. 58. A method in accordance with claim 49 or 50 wherein said organosilane is Trimethylsilylpropylazide. 59. A method in accordance with claim 49 or 50 wherein said organosilane is N-beta- (Aminoethyl)-gamma-aminopropyltrimethoxysilane. 60. A method in accordance with claim 49 or 50 wherein said organosilane is gamma-Aminopropyltriethyoxysilane. 61. A method in accordance with claim 49 or 50 wherein said organosilane is 3-Ureidopropyltrimethoxysilane. 62. A method in accordance with claim 49 or 50 wherein said organosilane is Bis (3-triethoxysilylpropyl)tetrasulfide. 63. A method in accordance with claim 49 or 50 wherein said organosilane is Phenyltrimethoxysilane. 64. A method in accordance with claim 49 or 50 wherein said mixture is extruded at a temperature in excess of 550?F. 65. A method in accordance with claim 49 or 50 wherein the weight percent, based upon total composition, of said organosilane is about 0.2 to about 2. 66. A composition produced by the method of claim 32. 67. A composition produced by the method of claim 33. 68. A composition produced by the method of claim 34. 69. A composition produced by the method of claim 35. 70. A composition produced by the method of claim 36. 71. A composition produced by the method of claim 37. 72. A composition produced by the method of claim 38. 73. A composition produced by the method of claim 42. 74.. A composition produced by the method of claim 43. 75. A composition produced by the method of claim 44. 76. A composition produced by the method of claim 45. 77. A composition produced by the method of claim 46. 78. A composition produced by the method of claim 48. 79. A composition produced by the method of claim 51. 80. A composition produced by the method of claim 52. 81. A composition produced by the method of claim 53. 82. A composition produced by the method of claim 54. 83. A composition produced by the method of claim 55. 84. A composition produced by the method of claim 56. 85. A composition produced by the method of claim 57. 86. A composition produced by the method of claim 58. 87. A composition produced by the method of claim 59. 88. A composition produced by the method of claim 60. 89. A composition produced by the method of claim 61. 90. A composition produced by the method of claim 62. 91. A composition produced by the method of claim 63. 92. A composition produced by the method of claim 65.

Claims: Claims 1. A composition comprising a glass-filled polyarylene sulfide and at least one organosilane c h a r a c t e r i z e d i n that said organosilane is selected from 1. Octadecyltriethoxysilane, 2. N-beta-(Aminoethyl)-gamma-aminopropyl-trimethoxysilane, 3. 2- (Benzylchloro) ethyltrimethoxysilane, 4. 3-Ureidopropyltrimethoxysilane, 5. N,N'-Diethyltrimethoxysilylpropylthiosulfenamide, 6. n-Propyltrimethoxysilane, 7. Trimethylsilylpropylazide, 8. bis (3-Triethoxysilylpropyl) tetrasulfide, 9. Phenyltrimethoxysilane, 10. tris (Trimethoxysiloxy)phenylsilane, 11. 3-N-(Trimethoxysilylpropyl)polyethylenimine, 12. Octyltrichlorosilane, 13. 3-(Diethylamino)propyltrimethoxysilane, 14. 2-p-Sulfoxylazylethyltrimethoxysilane, 15. (p-Aminophenyl) trimethoxysilane, 16. 1-Benzylchloro-2-trimethoxysilylethane, 17. Diethylamino-3-trimethoxysilylpropyldisulfide, and 18. 3-Aminopropyltriethoxysilane, 2. A method for modifying a property of a glass-filled poly arylene sulfide characterized by (a) combining polyarylene sulfide, glass and an organo silane selected from at least one of the compounds 1 to 18 recited in claim 1 to produce a mixture; and (b) raising the temperature of said mixture to a tempe rature equal to or above about the melting point of said polyarylene sulfide. 3. A method for decreasing the flow rate of a glass-filled polyarylene sulfide in accordance with claim 2 characte rized in that in step (a) said organosilane is selected from compounds 14 to 16 recited in claim 1; and in step (b) said mixture is maintained at said tempera ture for a time sufficient to effect at least a partial cure of the polyarylene sulfide. 4. A method for increasing the flow rate of a glass-filled polyarylene sulfide in accordance with claim 2 charac terized in that said organosilane is selected from com pounds 2, 11, 13, 17 and 18 recited in claim 1. 5. A method for improving the hydrolytic stability of a glass-filled polyarylene sulfide in accordance with claim 2 characterized in that said organosilane is selec ted from compounds 1 to 13 recited in claim 1. 6. A composition or method in accordance with one of claims 1 to 5 characterized in that the weight percent, based upon total composition, of said organosilane is from 0.2 to 2. 7. A composition or method in accordance with one of claims 1 to 6 characterized in that said polyarylene sulfide is polyphenylene sulfide. 8. A method in accordance with one of claims 3 to 7 charac terized in that said mixture is extruded at said tempera ture. 9. A method in accordance with claim 7 and 8 characterized in that said polyphenylene sulfide mixture is extruded at a temperature in excess of 2880C. 10. A composition produced by the method of one of claims 2 to 9.

Inventors: BLACKWELL, JENNINGS PRICE
Applicants: PHILLIPS PETROLEUM COMPANY
Application year: 1982
Main classification: C08L81
IPC codes: C08K5, C08K7, C08L81