ADDITIVE FOR FERTILISERS

Abstract: Additives for fertilisers, processes for their manufacture, and their use as nitrification inhibitors are described. These additives comprise dicyandiamide and a water-insoluble inorganic compound having a large specific surface area, such as, for example, various types of silica, furnace dusts resulting from the manufacture of silicon or ferrosilicon, and magnesium aluminium hydrosilicates. The additives remain dispersed in fertiliser solutions for a long time, even at low temperatures.

Description: Additive for fertilisers The invention relates to an additive for fertilisers, especially fertiliser solutions for the inhibition of nitrification. In addition to other nitrification-inhibiting substances, it has recently become increasingly common to add dicyandiamide to nitrogen fertilisers for the better exploitation of the nitrogen content. The use of dicyandiamide in liquid fertilisers (fertiliser solutions) is of particular interest. However, because of the physical properties of dicyandiamide, there are a number of difficulties, for example the difficulty of incorporating the dicyandiamide, which is relatively only sparingly soluble, in such solutions. In many cases the solubility of dicyandiamide is in fact too low to obtain the concentration desired for practical purposes. For example, DE-OS 27 02 284 discloses dicyandiamide-containing nutrient solutions and, in particular, NP and NPK fertiliser solutions, but the solubility of dicyandiamide therein is very low. In addition, fluctuations in temperature of the solutions result in coarse-crystalline dicyandiamide precipitates which settle, so that, at least to some extent, the product is incapable of fulfilling its task of inhibiting nitrification. Furthermore, when the solutions containing dicyandiamide are stored for a relatively long period, even with slight temperature differences, large dicyandiamide crystals may separate out and these prevent uniform spraying of the solution. A further disadvantage is the low rate of dissolution of the dicyandiamide which is a result of its moderate solubility. We have now found that use of an inorganic component, and in particular a water-insoluble inorganic compound having a large specific surface area, is advantageous in ensuring that the dicyandiamide remains dispersed even at low temperatures and there is no appreciable change as a result of separation or crystallisation effects. Accordingly, the present invention provides a nitrogen fertiliser comprising the fertiliser, an inorganic dispersion-forming agent and dicyandiamide. The fertiliser is preferably a fertiliser solution and the inorganic dispersion-forming agent and the dicyandiamide may, for example, be added together to the fertiliser and for this purpose may be formulated as a mixture. Accordingly, the present invention also provides a nitrification-inhibiting additive for fertilisers comprising dicyandiamide and an inorganic dispersionforming agent. The inorganic dispersion-forming agent is generally finely ground and may comprise, for example, (i) a water-insoluble inorganic compound having a large specific surface area or (ii) a water-insoluble inorganic compound having a large specific surface area and a dispersing or wetting agent. Generally, the inorganic compound is substantially insoluble in water at normal temperatures (ca. 20"C) and has a specific surface area of at least 10 m2/g as measured by the BET method (see Rmpp's Chemie Lexikon, 7 Aufl., Vol. 1, page 355). Suitable water-insoluble inorganic substances are, for example, various types of silica, such as, for example, aerosil, kieselguhr and diatomaceous earth, furnace dusts resulting from the manufacture of silicon or ferrosilicon, aluminium oxide, zinc oxide, kaolin, bentonite and montmorrillonite. Attapulgite, a needle-like magnesium aluminium hydrosilicate, is preferably used The effective surface area of such inorganic compound, as determined by the BET method, preferably is at least 10 m2/g, preferably up to 300 m2/g, more especially at least 15 m2/g and more especially up to 250 m2/g. Combining these oxides or silicates with dicyandiamide compensates for the disadvantage of the low solubility of dicyandiamide and low rate of dissolution. The dicyandiamide particles are maintained in suspension until the fertiliser solution is applied. Surprisingly, in addition, the dicyandiamide is reliably prevented from crystallising out when stored for a relatively long period or when cooled. Such dispersions are therefore extremely stable and can be applied using conventional spraying apparatus since there is no danger of recrystallisation. The dicyandiamide used may be of any quality, provided it is substantially free from phytotoxic impurities. A dicyandiamide having a degree of purity of at least 98.5 % is preferably used. Generally, finely ground dicyandiamide is used. Preferably, the grain size should not exceed 0.5 mm. Thus, for example, substantially all particles may be 4 0.5 mm, more especially 4 0.2 mm. Dicyandiamide of average particle size X 0.3 mum, for example 4 0.2 mm, and commercial dicyandiamide in which 60 to 70 % of the particles are 4 0.075 mm may also be used. The preparation of an additive of the invention may be carried out by mixing an appropriate quantity of the inorganic component with finely ground dicyandiamide. The operation may be carried out, for example, in a concrete mixer, DRAIS mixer or double cone mixer. The content of the inorganic component should preferably not greatly exceed 50 % by weight. Dispersion in the fertiliser solution may then be carried out by sprinkling in an appropriate quantity of additive and then pumping round or stirring round. In a different embodiment, the additive is advantageously added to the fertiliser solution as a highly concentrated aqueous suspension. For this purpose, a quantity of the inorganic component sufficient to form a viscous slurry that is still capable of being poured is first mixed with water and the desired quantity of dicyandiamide added subsequently. In this case too, the proportion of the inorganic component preferably does not greatly exceed 50 % by weight of the total additive. The advantage of an aqueous suspension of this type is the simple and rapid dispersion of the additive in the fertiliser solution even without special mixing apparatus. This, for example, may be advantageous for the farmer who wishes to add the agent immediately before applying the fertiliser solution. A further variant of the process is, for example, to mix the inorganic component homogeneously with the dicyandiamide which is still moist from the manufacturing process and which has a water content of, for example, up to 25 % by weight, and then, optionally, to dry them together. Such premixed additives are distinguished by particularly good flowability and ready dispersibility in fertiliser solutions. Because of their excellent flowability, these additives can also be accurately metered into solid fertilisers. The additive is preferably made up of from 1 to 50, more especially 2 to 30, parts by weight of the inorganic component together with from 50 to 99, more especially 70 to 98, parts by weight of dicyandiamide. When using the additive in highly concentrated aqueous form, the solids content of the dispersion is preferably at least 30%, preferably up to 95 %, more especially 30 to 70 %, by weight. Certain types of silicic acid (readily ascertained by those skilled in the art) are preferably used with the addition of a dispersing agent whereby they are more readily suspensed in the fertiliser solution. Examples of such dispersing agents are, for example, lignin sulphonates or sulphite modified amino-striazine formaldehyde condensation products. Preferably such dispersing agents are added in an amount of from 0.1 to 5 % by weight, more especially 1 to 3 % by weight, calculated on the total additive. The additive may be added as a nitrification inhibitor to nitrogen fertilisers, especially aqueous nitrogen fetiliser solutions. Suitable fertilisers are, for example, those mentioned in DE-OS 27 02 284. More especially, the present invention provides a liquid nitrogen fertiliser solution containing a composition comprising from 50 to 99 % by weight of dicyandiamide and from 1 to 50 % by weight of magnesium aluminium hydrosilicate capable of forming an aqueous suspension. The following Examples illustrate the invention. In the Examples the Attagel 40 and Attagel 150 used have a surface area of 210 m2/g determined by BET. Example 1 Dicyandiamide having a grain size of < 0.2 mm was mixed in a tumbling barrel with a finely disperse pyrogenic silica (BET surface area 18 m2/g) formed in the manufacture of ferrosilicon in an electric furnace. Three different batches of additive, containing respectively 10, 30 and 50 % by weight of silica, were manufactured. The resulting products were incorporated by means of a slow-speed stirring apparatus into an ammonium nitrate/urea fertiliser solution having a 28 % nitrogen content and consisting of 39.5 % by weight of ammonium nitrate, 30.5 % by weight of urea and 30 % by weight of water. The quantity of additive introduced was in each case 7 % by weight of dicyandiamide calculated on the fertiliser solution. This quantity was above the saturation limit of dicyandiamide in this solution, which, at 200C is only 5.5 t. The stirring time required for the complete dispersion of the additive after introduction into the fertiliser solution and the degree of deposition after a stirring time of 10 minutes at a stirring speed of 140 rev/min were ascertained. The results are given below. Table 1 EMI6.1 <tb> Proportion <SEP> of <SEP> silica <SEP> in <tb> additive <SEP> (% <SEP> by <SEP> weght) <SEP> 10 <SEP> 30 <SEP> 50 <tb> Stirring <SEP> time <SEP> in <SEP> minutes <tb> until <SEP> complete <SEP> dispersion <SEP> ca.0.5 <SEP> ca.l.O <SEP> a.1.0 <tb> Proportion <SEP> of <SEP> the <SEP> disper <tb> sion <SEP> remaining <SEP> in <SEP> suspen <tb> sion <SEP> (t <SEP> by <SEP> volume) <SEP> after <tb> <SEP> 1 <SEP> hour <SEP> 35 <SEP> 78 <SEP> 93 <tb> <SEP> 2 <SEP> hours <SEP> 27 <SEP> 54 <SEP> 77 <tb> <SEP> 4 <SEP> hours <SEP> 22 <SEP> 40 <SEP> 70 <tb> The pulverulent additives had a good flowability and could be metered without difficulty. The dispersion was carried out in each case within 1 minute by slight mechanical agitation, such as slow stirring, shaking or pumping round. As long as the movement continued, the homogeneous suspension did not settle. Similar results were obtained using bentonite and montmoril lonite. In contrast, the inorporation of dicyandiamide alone into fertiliser solutions of the same composition presented considerable difficulties: in powder form it did not flow freely and agglomerated in the fertiliser solution to form relatively large lumps which stuck to the wall and base. Example 2 Dicyandiamide having a grain size of < 0.2 mm was mixed by roller-burnishing (in a mill containing rods and balls) with a needle-like type of attapulgite (Attagel 40, Engelhard) having an average particle size of 0.00014 mm. Three batches of additive, containing respectively 10, 30 and 50 % by weight of attapulgite, were manufactured. The pulverulent free-flowing additive was stirred under the same conditions as in Example 1 into the same ammonium nitrate/urea fertiliser solution. The stirring time in which the additive was completely dispersed and also the relationship of its suspendability to the standing time were ascertained and the results given below. Table 2 EMI7.1 <tb> Proportion <SEP> of <SEP> attapulgite <SEP> in <tb> the <SEP> additive <SEP> in <SEP> % <SEP> by <SEP> weight <SEP> 10 <SEP> 30 <SEP> 50 <tb> Stirring <SEP> time <SEP> in <SEP> minutes <tb> until <SEP> complete <SEP> dispersion <tb> (140 <SEP> rev/min) <SEP> ca.O.5 <SEP> ca.5.0 <SEP> ca.7.0 <tb> Proportion <SEP> of <SEP> the <SEP> disper <tb> sion <SEP> remaining <SEP> in <SEP> suspen <tb> sion <SEP> in <SEP> % <SEP> by <SEP> volume <SEP> after <tb> <SEP> 1 <SEP> hour <SEP> 49 <SEP> 100 <SEP> 100 <tb> <SEP> 2 <SEP> hours <SEP> 33 <SEP> 100 <SEP> 100 <tb> <SEP> 4 <SEP> hours <SEP> 28 <SEP> 99 <SEP> : <SEP> 100 <tb> The powders, which gave a very good flowabiiity, could be metered rapidly and without difficulty and could be dispersed rapidly. The suspension could be maintained by slight mechanical agitation. Example 3 Commercial dicyandiamide having a grain size distribution of from 60 to 70 % < 0.075 mm and approximately 1 % > 0.5 mm was mixed by roller burnishing with a needle-like attapulgite (Attagel 150) having an average particle size of 0.00012 mm and 8 % > 0.044 mm and introduced into the fertiliser solution described in Example 1. Dispersion was then carried out by means of a heavy-duty mixer (Turrax) at 2000 rev/min. Two solutions were prepared as follows: (i) by adding 4.7 % by weight, calculated on the fertiliser solution, of additive consisting of 90 % by weight of dicyandiamide and 10 % by weight of attapulgite, (ii) by adding 6.2 % by weight, calculated on the fertiliser solution, of additive consisting of 67 % by weight of dicyandiamide and 33 % by weight of attapulgite. The relationship of suspendability to standing time of the solutions was as follows: Table 3 EMI8.1 <tb> <SEP> Proportion <SEP> of <SEP> the <SEP> disper <tb> <SEP> sion <SEP> remaining <SEP> in <SEP> suspen <tb> <SEP> sion <SEP> in <SEP> % <SEP> by <SEP> volume <SEP> after: <tb> <SEP> 1 <SEP> day <SEP> 7 <SEP> days <SEP> 14 <SEP> days <tb> Addition <SEP> according <SEP> to <SEP> (i) <SEP> 100 <SEP> 40 <SEP> 30 <tb> Addition <SEP> according <SEP> to <SEP> (ii) <SEP> 100 <SEP> 100 <SEP> 100 <tb> Even after 10 weeks' storage at 50C, the fertiliser solution according to addition (ii) did not precipitate any dicyandiamide crystals larger than 0.2 mm. Example 4 Mixtures of dicyandiamide (grain size < 0.2 mm) and attapulgite (Attagel 150) manufactured by rollerburnishing were mixed with water. These liquid mixtures were added to the ammonium nitrate/urea fertiliser solution described in Example 1. After a stirring time of 10 minutes with a slow-speed stirrer (140 rev/ min), the suspendability was assessed. The quantity of dicyandiamide added was in each case 7 %, calculated on the fertiliser solution. The additives had the following compositions: EMI9.1 <tb> <SEP> dicyandiamide <SEP> attapulgite <SEP> water <SEP> content <SEP> of <tb> <SEP> % <SEP> by <SEP> weight <SEP> % <SEP> by <SEP> weight <SEP> the <SEP> mixtures <SEP> <tb> <SEP> % <SEP> by <SEP> weight <tb> (a) <SEP> 93 <SEP> 7 <SEP> 35 <tb> (b) <SEP> 90 <SEP> 10 <SEP> 40 <tb> (c) <SEP> 87 <SEP> 13 <SEP> 40 <tb> (d) <SEP> I <SEP> 67 <SEP> 33 <SEP> 55 <tb> These mixtures were stirred into the fertiliser solution by hand using a rod and, after their dispersion, were stirred for a further 3 minutes. The suspendability at 1 day, 7 days and 14 days was measured and the results are given below. EMI10.1 <tb> additive <SEP> proportion <SEP> of <SEP> the <SEP> dispersion <SEP> remaining <SEP> in <tb> <SEP> suspension <SEP> (% <SEP> by <SEP> volume) <tb> <SEP> after <SEP> 1 <SEP> day <SEP> after <SEP> 7 <SEP> days <SEP> after <SEP> 14 <SEP> days <tb> <SEP> (a) <SEP> 50 <SEP> n/m <SEP> n/m <tb> <SEP> (b) <SEP> 100 <SEP> 70 <SEP> n/m <tb> <SEP> (c) <SEP> 100 <SEP> 100 <SEP> 90 <tb> <SEP> (d) <SEP> 100 <SEP> 100 <SEP> 100 <tb> n/m = not measured The experiments show that, by the preliminary step cf making a paste of the additive and water, a very good suspendability of the dispersion was possible even with very little stirring. The amount of dicyandiamide added was greater than its solubility at 200C; nevertheless, no precipitation of dicyandiamide crystals was observed. In addition, the crystal growth of the dicyandiamide was so greatly retarded that, even after many weeks' storage, no crystals over 0.2 mm were formed. (Without the addition of attapulgite, a fertiliser solution of this type shows dicyandiamide crystals of over 1 mm and crystal intergrowth after only a few days.) When the fertiliser solution containing additive (d) was cooled to 0 C, no appreciable crystal growth was observed even after several weeks, so that dispersions of this type can be applied without restriction using commercial spraying apparatus Example 5 The additive consisting of dicyandiamide 66 % (grain size < 0.2 mm) attapulgite (Attagel 150) 32 % calcium lignin sulphonate 2 % was mixed with water (dispersion with 40 % water) and stirred by hand into the same nitrogen fertiliser solution as in Example 1. The amount of additive dispersion added to the fertiliser solution was such that that solution contained 7 % dicyandiamide. The additive dispersed very rapidly and homogeneously in the fertiliser solution even though added by hand. After 3 minutes' continuous stirring round by hand the solution was left; no deposits were observed after 7 days. The solution was subjected to a 3-week varying temperature test in which it was stored in succession for 1 day at 200C, 1 day at 100C, 1 day at 200C, 1 day at 50C etc.. No dicyandiamide deposits larger than 0.2 mm were observed. Example 6 Moist dicyandiamide (water content approximately 10 %; average grain size 300 p) was mixed with attapulgite (Attagel 40) in a paddle mixer at approximately 500C for 10 minutes. The additive manufactured in this manner and containing 5 % by weight attapulgite was stirred in an amount of 4.9 % by weight into the 70 % ammonium nitrate/urea fertiliser solution (28 % N) of Example 1 using a slowly rotating stirring apparatus (140 rev/min). The mixture was completely dispersed after only approximately 1 minute after its introduciton. An additive manufactured in the same manner and containing 10 % by weight of attapulgite was homogeneously dispersed within only approximately 30 seconds after the addition of 5.2 % by weight of additive. Example 7 The additive was manufactured by first mixing the attapulgite (Attagel 150) in water and then dispersing the dicyandiamide (1 % > 0.5 mm, remainder < 0.076 mm) in this suspension. When the additive was added to the fertiliser solution of Example 1 by hand, particularly rapid mixing took place and the suspendability was also especially good. If, for example, 13.8 % by weight of a liquid dispersion of this type which had a 55 % water content and in which the weight ratio of dicyandiamide to attapulgite was 67 : 33, was added to the ammonium nitrate/urea fertiliser solution, after shaking round vigorously once no crystal precipitates were observed even after 14 days. Example 8 1.65 % by weight of an additive consisting of 90 % by weight of dicyandiamide (grain size < 0.2 mm) and 10 % by weight of attapulgite (Attagel 40) were stirred into a nitrogen/phosphorus fertiliser solution, which contained 10 % nitrogen and 34 % P205 and which had a density of 1.4 g/cm3, and were then dispersed with a heavy-duty stirring apparatus at 2000 rev/min. The dispersion was so stable that, even after 3 weeks' storage at 0 C, there were still no deposits whatever.

Claims: Claims for all Contracting States designated except Austria 1. An agent suitable for addition to fertilisers comprising dicyandiamide and a water-insoluble inorganic compound having a specific surface area of at least 10 m2/g, and, if desired, a dispersing agent. 2. An agent as claimed in claim 1, wherein the specific surface area of the water-insoluble inorganic compound is at least 15 m2/g. 3. An agent as claimed in claim 1 or claim 2, comprising 50 to 99 % by weight of dicyandiamide and 1 to 50 % by weight of water-insoluble inorganic compound, calculated on the sum of the dicyandiamide and water-insoluble inorganic compound. 4. An agent as claimed in claim 3, comprising 70 to 98 % by weight of dicyandiamide and 2 to 30 % by weight of water-insoluble inorganic compound, calculated on the sum of the dicyandiamide and waterinsoluble inorganic compound. 5. An agent as claimed in any one of claims 1 to 4, in the form of an aqueous solution having a solids content of at least 30 % by weight. 6. An agent as claimed in any one of claims 1 to 5, wherein the inorganic compound is a silicate or oxide. 7. An agent as claimed in claim 6, wherein the water insoluble inorganic compound is a magnesium aluminium hydrosilicate. 8. A process for the preparation of an agent as claimed in any one of claims 1 to 7, which comprises (a) mixing the inorganic compound with dicyandiamide, or (b) mixing the inorganic compound with water to form an viscous slurry that is capable of being poured and then adding dicyandiamide, or (c) mixing the inorganic compound with dicyandiamide having a moisture content of up to 25 % by weight, and, if desired, drying the mixture. 9. A nitrogen fertiliser composition comprising a fertiliser and an agent as claimed in any one of claims 1 to 7. 10. A fertiliser composition as claimed in claim 9, which is in the form of an aqueous solution. Claims for Austria 1. A process for preparing an agent suitable for addition to fertilisers, which comprises (a) mixing a water-insoluble inorganic compound having a specific surface area of at least 10 m2/g with dicyandiamide, or (b) mixing the inorganic compound specified in (a) with water to form a viscous slurry that is capable of being poured and then adding dicyan diamide, or (c) mixing the inorganic compound specified in (a) with dicyandiamjde having a moisture content of up to 25 % by weight, and, if desired, drying, and, if desired, in method (a), (b) or (c) incorporating a dispersing agent into the agent by mixing with either or both of the specified components and/or with the mixed components. 2. A process as claimed in claim 1, wherein the specific surface area of the water-insoluble inorganic compound is at least 15 m2/g. 3. A process as claimed in claim 1 or claim 2, wherein the dicyandiamide and water-insoluble inorganic compound are mixed in the proportions of 50 to 99 parts by weight of dicyandiamide and 1 to 50 parts by weight of water-insoluble inorganic compound, calculated on the sum of dicyandiamide and waterinsoluble inorganic compound. 4. A process as claimed in claim 1 or claim 2, wherein the dicyandiamide and water-insoluble inorganic compound are mixed in the proportions of 7Q to 98 parts by weight of dicyandiamide and 2 to 30 parts by weight of water-insoluble inorganic compound, calculated on the sum of dicyandiamide and waterinsoluble inorganic compound. 5. A process as claimed in any one of claims 1 to 4, wherein the agent is prepared in the form of an aqueous solution having a solids content of at least 30 % by weight. 6. A process as claimed in any one of claims 1 to 5, wherein the inorganic compound is a silicate or oxide. 7. A process as claimed in claim 6, wherein the water insoluble inorganic compound is a magnesium aluminium hydrosilicate. 8. A process for preparing a nitrogen fertiliser composition, which comprises incorporating the components of an agent specified in any one of claims 1 to 7 in a nitrogen fertiliser. 9. A process as claimed in claim 8, wherein the fertiliser is in the form of an aqueous solution. 10. Use of an agent as specified in any one of claims 1 to 7 as a nitrification-inhibitor in nitrogen fertilisers.

Inventors: MICHAUD, HORST, RAVELING, HERMANN, SEEHOLZER, JOSEF
Applicants: SKW TROSTBERG AKTIENGESELLSCHAFT
Application year: 1982
Main classification: C05C7
IPC codes: C05G3, C05C7