ADHESIVE COMPOSITION

Abstract: An adhesive composition which possesses an improved adhesion strength which comprises (A) an α-cyanoacrylate ester, (B) an aliphatic polyol or a derivative thereof or a polyether or a derivative thereof and (C) an aromatic polyol.

Description: ADHESIVE COMPOSITION The present invention related to an adhesive composition. More particularly, it relates to an #-cyano- acrylate compound-containing adhesive composition which has an enhanced initial adhesion strength. A-Cyanoacrylate esters are extremely polymerizable, and they are rapidly cured by the moisture at the surface of a solid material or in the atmosphere without the use of any catalyst or heating. Because of this property, & cyanoacrylate esters are used as instantaneous adhesive agents for various materials such as rubbers, plastics, metals and glass. However, even instantaneous adhesive agents often have an inferior initial adhesive strength on the adhesion of some materials such as wood, chrome or nickel-plated surfaces, polyesters (e.g. FRP) and phenol resins and are not suitable for the quick adhesion of such materials. We have now found that the incorporation of certain specific substances into adhesive compositions comprising o & cyanoacrylate esters can enhance the initial adhesion strength without deterioration of the advantageous characteristic properties inherent in the compositions such as good storage stability and high bonding strength. According to the present invention, there is provided an adhesive composition which comprises (A) anct-cyanoacrylate ester, (B) an aliphatic polyol or a derivative thereof or a polyether or a derivative thereof and (C) an aromatic polyol. The i-cyanoacrylate ester used as component (A) has the formula: EMI2.1 wherein R is an ester residue, particularly a substituted or unsubstituted, saturated or unsaturated, cyclic or noncyclic hydrocarbon group such as substituted or unsubstituted alkyl, more specifically alkyl (e.g. methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, pentyl, hexyl, octyl, ethylhexyl, dodecyl), alkocyalkyl (e.g. methoxyethyl, ethoxy-ethyl), haloalkyl (e.g. chloroethyl, trifluorethyl), phenylalkyl (e.g. benzyl), etc., substituted or unsubstituted alkenyl (e.g. allyl), substituted or ubsubstituted alkynyl (e.g. propargyl), substituted or ubsubstituted aryl (e.g. phenyl, tolyl) or substituted or unsubstituted cycloalkyl(e.g. cyclopentyl, cyclohexyl). Alsot R may be a substituted or unsubstitued, saturated or unsaturated heterocyclic group such as tetrahydrofurfuryl. The component (B) is an aliphatic polyol or a derivative thereof or a polyether or a derivative thereof. Examples of the aliphatic polyols are alkane polyols (e.g. ethylene glycol, propylene glycol, tetramethylene glycol, hexamethylene glycol, octmethylene glycol, 3-methylpentane diol, 2,2-diethyipropane diol, 2-ethyl-l,4-butane diol, glycerol, trimetylolmethane, trimethylolethane, trimethylolpropane, 1,2,6-hexanetriol 2,5-hexanediol), alkene polyols (e.g.polybutadiene diol), halogenated alkane polyols (e.g. chloropropylene glycol), etc. The derivatives thereof may be esters,ethers, etc, and cover specifically alkyl ethers (e.g. methylcellosolve, ethylcellosolve, ethylene glycol n-butyl ether, propylene glycol methyl ether, tetramethylene glycol propyl ether, ethylene glycol diethyl ether), aryl ethers (e.g. ethylene glycol phenyl ether), aralkyl ethers (e.g. ethylene glycol benzyl ether), alkanoic esters (e.g. ethylene glycol monoacetate, ethylene glycol monolaurate, ethylene glycol monostearate, ethylene glycol distearate, ethylcellosolve stearate, glycerol monolaurate, glycerol monostearate, sorbitan monolaurate), alkenoic esters (e.g. cellosolve acrylate, cellosolve methacrylate, cellosolve crotonate), etc. The polyethers and their derivatives.are those having the repeating units of the formula: EMI4.1 wherein X1 and x2 are each hydrogen, halogen, hydroxyl, alkyl, alkenyl, aryl or aralkyl, the latter four gropes optionally being any suitable substituent thereon, p is an integer of not less than 1 and q is an integer of not less than 2. The linear chain comprising the said repeating units may have any atom or group at each of the both terminal positions Alternatively, both ends of the linear chain may be combined to form a cyclic ring. In general, p is preferably fran 2 to 6, and q is preferably frdm 2 td 3,000. When q is more than 10,000, the compatibility of the resulting polyether with the a-cyanoacrylate ester is inferior. Examples of the polyethers and their derivatives are formaldehyde condensates, acetaldehyde condensates, trioxane polymers, polyalkylene glycols (e.g. diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, dipropylene glycol, polypropylene glycol, polytetramethylene oxide, poly-3,3-bis(chloromethyl)butylene oxide, poly-1,3-dioxolane, ethylene oxide-propylene oxide block polymers), polyalkylene glycol monoethers (e.g. methylcarbitol, carbitol, diethylene glycol n-butyl ether, di ethylene glycol phenyl ether, diethylene glycol benzyl ether, dipropylene glycol ethyl ether, tripropylene glycol methyl ether, polyethylene glycol methyl ether, polyethylene glycol propyl ether, polyethylene glycol lauryl ether, polyethylene glycol stearyl ether, polyoxyethylene nonylphenyl ether, polyethylene glycol allyl ether), polyalkylene glycol diethers (e.g. diethylene glycol diethyl ether, diethylene glycol di-n-butyl ether, triethylene glycol dimethyl ether, tetraethylene glycol distearyl ether, polyethylene glycol dimethyl ether), polyalkylene glycol monoesters (e.g. diethylene glycol ethyl ester, tetraethylene glycol methyl ester, propylene glycol n-butylate, polyethylene gycol methyl ester, polyethylene glycol ethylate, polyethylene glycol laurate, polyethylene glycol cetyl ester, polyethylene glycol stearate, polyethylene glycol oleate, polyoxyethylene sorbitan laurate, diethylene glycol acrylate, diethylene glycol methacrylate, diethylene glycol crotonate), polyalkylene glycol diesters (e.g. diethylene glycol dimethyl ester, diethylene glycol diethyl ester, diethylene glycol diacrylate, diethylene glycol distearate, diethylene glycol dimethacrylate, tetraethylene glycol dicrotonate, polyethylene glycol dimethylate, polyethylene glycol di-nbutylate, polyethylene glycol dilaurate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, polyethylene glycol dicrotonate, polyethylene glycol di-a-cyanoacrylate, polyethylene glycol stearyl-methacrylate, polyethylene glycol lauryl-acrylate), polyalkylene glycol monoether monoesters (e.g. acrylates, methacrylates, crotonates or acyanoacrylates of glycol monoethers such as methylcarbitol, carbitol, tetraoxyethylene methyl ether, polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether), bisphenol A-pofyalkylene oxide adducts, trimethylolpropane-poly alkylene oxide adducts, glycerin-polyalkylene oxide adducts, adipic acid-polyalkylene oxide adducts, trimellitic acid polyalkylene oxide adducts, etc. Their examples forming a cyclic ring are 18-crown-6, 15-crown-5, 18-crown-5, dithia 15-crown, dibenzo-18-crown-6, tribenzo-18-crown-6, dicyclo hexyl-18-crown-6, 1,2-naphto-15-crown-5, 1 .2-methylbenzo-18- crown-6, etc. Component (C) way be any aromatic polyols. The aromatic polyols may be represented by the formula: EMI6.1 wherein r is an integer of 2 or 3 and at least two hydroxyl groups are present at the adjacent positions. Specific examples are catechol, pyrogallol, l,2,4-benzenetriol, etc. While various combinations of specific substances of the components (A), (B) and (C) are possible, particularly preferred is the combination of the a-cyanoacrylate ester (I) as the component (A), a polyalkyl ether compound of the formula: EMI6.2 wherein X1 is a hydrogen atom or a methyl group, X2 is a hydrogen atom, a methyl group or a cyano group, X3 is a hydrogen atom, -R' or -OCR" (in which R' and R" are each a hydrocarbon group not containing any anion polymerizable group) but when X2 is a cyano group, X3 is not a hydrogen atom, t and m are each zero or a positive integer but t + m is not zero and n is a positive integer as the component (B) and pyrogallol as the component (C). A typical example of the anion polymerizable group is an ethylenically unsaturated bond. Examples of the polyalkyl ether compound (IV), which is also generally known, are monoacrylates, monomethacrylates or monocrotonates of glycols (e.g. ethylene glycol; diethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, polypropylene glycol, oxyethylene oxypropylene block polymer), monoacrylates, monomethacrylates, monocrotonates or a-cyanoacrylates of glycol monoethers (e.g. methyl cellosolve, ethyl cellosolve, butyl cellosolve, methylcarbitol, tetraoxyethylene methyl ether, polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether), acrylates, methacrylates, crotonates or a-cyanoacrylates of monoester compounds (e.g. polyoxyethylene monooleate, polyoxyethylene monostearate), etc. Among them, preferred are monoacrylates of glycol monoethers, particularly tetraoxyethylene methyl ether monoacrylate. Their molecular weights are usually not more than about 20,000. The adhesive composition may also comprise any other additive which are conventionally incorporated into a 9-cyano- acrylate ester-containing adhesive composition. Examples of such additives are a stabilizer, particularly an anionic polymerization inhibitor (e.g. sulfur dioxide, sulfonic acid, sultone) and a radical polymerization inhibitor (e.g. hydroquinone, hydroquinone monomethyl ether), a thickening agent (e.g. polymethyl methacrylate), a plasticizer, a colorant, a perfume or a solvent. In the adhesive composition of the invention, the a-cyanoacrylate ester as the component (A) is usually contained in an amount of not less than 50 % by weight, preferably of not less than 80 % by weight, based on the total weight of the adhesive composition. However, this is not limitative. The proportions of the components (B) and (C) to the component (A) may be appropriately selected taking into consider ation the adhesive property of the resulting composition. In general, the amount of component (B) may be from 0.05 to 20% by weight based on the weight of component (A), and the amount of component (C) may be from 0.0001 to 0.58 by weiaht on the same basis as above. ben these amounts are beloar the lower limits, little improvement is achieved. When these amounts are higher than the higher limits, the curing rate-and the adhesion strength of the component CA) deteriorate. The adhesive composition of the invention may be used for the bonding of various materials. It is particularly. notable that such adhesive compositions produce a remarkable initial adhesion strength for various materials, especially somewhat acidic materials such as wood chrome or nickelplated surfaces, polyesters and phenol resins. Practical and presently preferred embodiments of the present invention are illustrated shown in the following Examples wherein % is by weight. examples 1 to 7 and Comparative Examples 1 to 4 An adhesive composition comprising ethyl a-cyanoacrylate as the component (A) and sulfur dioxide as an anionic polymerization inhibitor and hydroquinone as a radical polymerization inhibitor respectively in amounts of 0.002 % and 0.1 % based on the weight of ethyl a-cyanoacrylate was incorporated with the polyalkyl ether compound (IV) as shown in Table 1 as the component (B) and pyrogallol as the component (C) respectively in amounts as shown in Table 1 based on the weight of ethyl a-cyanoacrylate. The resultant adhesive composition was subjected to measurement of adhesion strength. The results are shown in Table 1. For comparison, adhesion strength of the adhesive composition not incorporated with the components (B) and/or (C) was also measured, and the results are shown in Table 1 as Comparative Examples. In these Examples, measurement of adhesion strength was effected as follows: materials (100 x 25 x 1.6-3 mm) as shown in Table 1 were bonded each other with an adhesive area of 25 x 12.5 mm and cured at 200C under a relative humidity of 60 %; after cured for 3 minutes and for 24 hours, its tensile shear strength was measured with a pulling rate of 50 mm/min; results being expressed in kg.f/cm2. Table 1 EMI11.1 Example <SEP> Component <SEP> (B) <SEP> Component <SEP> (C) <SEP> Tensile <SEP> shear <SEP> strangth <tb> <SEP> (kg.f/cmê) <tb> <SEP> Kind <SEP> Amount <SEP> Kind <SEP> Amount <SEP> Cured <SEP> for <SEP> Cured <SEP> for <tb> <SEP> (%) <SEP> (%) <SEP> 3 <SEP> minutes <SEP> 24 <SEP> hours <tb> <SEP> A <SEP> B <SEP> A <SEP> B <tb> 1 <SEP> Tetraoxyetylene <SEP> mono- <SEP> 0.6 <SEP> Pyrogallol <SEP> 0.002 <SEP> 29 <SEP> 37 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 133 <tb> <SEP> methyl <SEP> ether <SEP> monocrylate <SEP> rial <SEP> broken <tb> 2 <SEP> Methoxypolyethylene <SEP> 0.4 <SEP> Pyrogallol <SEP> 0.01 <SEP> 25 <SEP> 36 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 122 <tb> <SEP> glycol <SEP> monomethacrylate <SEP> rial <SEP> broken <tb> 3 <SEP> Methoxypolyethylene <SEP> 0.4 <SEP> Pyrogallol <SEP> 0.05 <SEP> 32 <SEP> 41 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 128 <tb> <SEP> glycol <SEP> monomethacrylate <SEP> rial <SEP> broken <tb> 4 <SEP> Polyethylene <SEP> glycol <SEP> mono- <SEP> 0.6 <SEP> Pyrogallol <SEP> 0.01 <SEP> 27 <SEP> 30 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 138 <tb> <SEP> cromate <SEP> rial <SEP> broken <tb> 5 <SEP> Octaethylene <SEP> glycol <SEP> mono- <SEP> 0.4 <SEP> Pyrogallol <SEP> 0.01 <SEP> 23 <SEP> 35 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 142 <tb> <SEP> methacrylate <SEP> rial <SEP> broken <tb> 6 <SEP> Polyoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyrogallol <SEP> 0.02 <SEP> 21 <SEP> 33 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 120 <tb> <SEP> oleate <SEP> monoacrylate <SEP> rial <SEP> broken <tb> 7 <SEP> Polyoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyrogallol <SEP> 0.02 <SEP> 23 <SEP> 34 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 140 <tb> <SEP> stearate <SEP> monomethacrylate <SEP> rial <SEP> broken <tb> Comparative <tb> 1 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 0 <SEP> 11 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 80 <tb> <SEP> rial <SEP> broken <tb> 2 <SEP> - <SEP> - <SEP> Pyrogallol <SEP> 0.01 <SEP> 0 <SEP> 8 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 122 <tb> <SEP> rial <SEP> broken <tb> 3 <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.6 <SEP> - <SEP> - <SEP> 11 <SEP> 22 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 91 <tb> <SEP> methyl <SEP> ether <SEP> monoacrylate <SEP> rial <SEP> broken <tb> 4 <SEP> Methoxypolyethylene <SEP> 0.4 <SEP> - <SEP> - <SEP> 16 <SEP> 21 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 92 <tb> <SEP> glycol <SEP> monomethacrylate <SEP> rial <SEP> broken <tb> Materials bonded: A: Lauan/Lauan B: Chrome plated ateel/chrome plated ateel Examples 8 to 24 and Comparative Examples 5 to 7 An adhesive composition comprising the a-cyanoacrylate ester (I) as shown in Table 2 as the component (A) and sulfur dioxide as an anionic polymerization inhibitor and hydroquinone as a radical polymerization inhibitor respectively in amounts of 0.0015 % and 0.05 % based on the weight of the a-cyanoacrylate ester (I) was incorporated with the polyalkyl ether compound (IV) as shown in Table 2 as the component (B) and the aromatic polyol (III) as shown in Table 2 as the component (C) respectively in amounts as shown in Table 2 based on the weight of the a-cyanoacrylate ester (I). The resultant adhesive composition was subjected to measurement of adhesion strength. The results are shown in Table 2. For comparison, adhesion strength of¯the adhesive composition not incorporated with the components (B) and/or (C) was also measured, and the results are shown in Table 2 as Comparative Examples. In these Examples, measurement of adhesion strength was effected as follows: materials (100 x 25 x 1.6 - 3 mm) as shown in Table 2 were bonded each other with an adhesive area of 25 x 12.5 mm and cured at 200C under a relative humidity of 60 %; after cured for 3 minutes and for 24 hours, its tensile shear strength was measured with a pulling rate of 50 mm/min; results being expressed in kg.f/cm2. EMI13.1 Example <SEP> Component <SEP> (A) <SEP> Component <SEP> (B) <SEP> Component <SEP> (C) <SEP> Tensile <SEP> stranght <SEP> (kg.f/cmê) <tb> <SEP> Kind <SEP> Kind <SEP> Amount <SEP> Kind <SEP> Amount <SEP> Cured <SEP> for <SEP> Cured <SEP> for <tb> <SEP> (%) <SEP> (%) <SEP> 3 <SEP> minutes <SEP> 24 <SEP> hours <tb> <SEP> A <SEP> B <SEP> A <SEP> B <tb> <SEP> 8 <SEP> Methyl <SEP> &alpha;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> 0.4 <SEP> Pyroga- <SEP> 0.01 <SEP> 23 <SEP> 30 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 125 <tb> <SEP> acrylate <SEP> monomethacrylate <SEP> llol <SEP> rial <SEP> broken <tb> <SEP> 9 <SEP> Methyl <SEP> &alpha; ;-cyano- <SEP> Tetraoxyethlene <SEP> mono- <SEP> 0.6 <SEP> Pyroga- <SEP> 0.01 <SEP> 22 <SEP> 34 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 129 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monocrylate*) <SEP> llol <SEP> rial <SEP> broken <tb> 10 <SEP> Methyl <SEP> &alpha;-cyano- <SEP> Methoxypolyethylene <SEP> 0.4 <SEP> Pyroga- <SEP> 0.01 <SEP> 26 <SEP> 32 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 127 <tb> <SEP> acrylate <SEP> glycol <SEP> monomethacrylate <SEP> llol <SEP> rial <SEP> broken <tb> 11 <SEP> Methyl <SEP> &alpha;-cyano- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.01 <SEP> 25 <SEP> 31 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 127 <tb> <SEP> acrylate <SEP> oleate <SEP> monomethacrylate <SEP> llol <SEP> rial <SEP> broken <tb> 12 <SEP> Ethyl <SEP> &alpha; ;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> 0.4 <SEP> Pyroga- <SEP> 0.02 <SEP> 27 <SEP> 29 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 130 <tb> <SEP> acrylate <SEP> monoacrylate <SEP> llol <SEP> rial <SEP> broken <tb> 13 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Polyethylene <SEP> 0.4 <SEP> Pyroga- <SEP> 0.02 <SEP> 26 <SEP> 28 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 129 <tb> <SEP> acrylate <SEP> glycol <SEP> monoacrylate*) <SEP> llol <SEP> rial <SEP> broken <tb> 14 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 28 <SEP> 31 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 133 <tb> <SEP> acrylate <SEP> monoacrylate <SEP> llol <SEP> rial <SEP> broken <tb> 15 <SEP> Ethyl <SEP> &alpha; ;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> 0.6 <SEP> Pyroga- <SEP> 0.03 <SEP> 32 <SEP> 38 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 135 <tb> <SEP> acrylate <SEP> monoacrylate <SEP> llol <SEP> rial <SEP> broken <tb> 16 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 33 <SEP> 39 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 129 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monocrylate <SEP> llol <SEP> rial <SEP> broken <tb> 17 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> mono- <SEP> 0.4 <SEP> Catechol <SEP> 0.03 <SEP> 17 <SEP> 22 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 108 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monocrylate <SEP> rial <SEP> broken <tb> 18 <SEP> Ethyl <SEP> &alpha; ;-cyano- <SEP> Polyethylene <SEP> glycol <SEP> mono- <SEP> 0.4 <SEP> 1,2,4-ben- <SEP> 0.03 <SEP> 12 <SEP> 18 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 102 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monocrylate <SEP> zentriol <SEP> rial <SEP> broken <tb> 19 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Tetraoxyethylene <SEP> monolauryl <SEP> 0.4 <SEP> Pyroga- <SEP> 0.02 <SEP> 26 <SEP> 32 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 131 <tb> <SEP> acrylate <SEP> ether <SEP> monocrotonate <SEP> llol <SEP> rial <SEP> broken <tb> 20 <SEP> Ethyl <SEP> &alpha;-cyano- <SEP> Polyoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.02 <SEP> 26 <SEP> 32 <SEP> At <SEP> 70 C <SEP> mate- <SEP> 139 <tb> <SEP> acrylate <SEP> oleate <SEP> monocyanoacrylate <SEP> llol <SEP> rial <SEP> broken <tb> Table 2 (Continued) EMI14.1 Example <SEP> Component <SEP> (A) <SEP> Component <SEP> (B) <SEP> Component <SEP> (C) <SEP> Tensile <SEP> strength <SEP> (kg.f/cmê) <tb> <SEP> Kind <SEP> Kind <SEP> Amount <SEP> Kind <SEP> Amount <SEP> Cured <SEP> for <SEP> Cured <SEP> for <tb> <SEP> (%) <SEP> (%) <SEP> 3 <SEP> minutes <SEP> 24 <SEP> hours <tb> <SEP> A <SEP> B <SEP> A <SEP> B <tb> <SEP> 21 <SEP> Propyl <SEP> &alpha;-cyano- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 18 <SEP> 22 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 134 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monoacrylate <SEP> liol <SEP> rial <SEP> broken <tb> <SEP> 22 <SEP> Propyl <SEP> &alpha; ;-cyano- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 16 <SEP> 21 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 136 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monoacrylate*) <SEP> liol <SEP> rial <SEP> broken <tb> <SEP> 23 <SEP> Butyl <SEP> &alpha;-cyano- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 11 <SEP> 17 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 110 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monoacrylate <SEP> liol <SEP> rial <SEP> broken <tb> <SEP> 24 <SEP> Ethoxyethyl <SEP> &alpha;- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.4 <SEP> Pyroga- <SEP> 0.03 <SEP> 15 <SEP> 21 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 100 <tb> <SEP> cyanoacrylate <SEP> methyl <SEP> ether <SEP> monoacrylate <SEP> liol <SEP> rial <SEP> broken <tb> Comparative <tb> <SEP> 5 <SEP> Methyl <SEP> &alpha; ;-cyano- <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 0 <SEP> 12 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 85 <tb> <SEP> acrylate <SEP> rial <SEP> broken <tb> <SEP> 6 <SEP> Methyl <SEP> &alpha;-cyano- <SEP> - <SEP> - <SEP> Pyroga- <SEP> 0.01 <SEP> 0 <SEP> 10 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 124 <tb> <SEP> acrylate <SEP> liol <SEP> rial <SEP> broken <tb> <SEP> 7 <SEP> Methyl <SEP> &alpha;-cyano- <SEP> Tetraoxyethylene <SEP> mono- <SEP> 0.6 <SEP> - <SEP> 12 <SEP> 22 <SEP> At <SEP> 70 C <SEP> mfate- <SEP> 96 <tb> <SEP> acrylate <SEP> methyl <SEP> ether <SEP> monoacrylate <SEP> rial <SEP> broken <tb> Note: *) Thickened product containing polymethyl methycrylate in an amount of 5 % by weight. Materials bonded: A: Lauan/Lauan B: Chrome plated steel/chrome plated steel As understood from the results in Tables 1 and 2, the adhesive composition incorporated with the polyalkyl ether compound (IV) only is insufficient in initial adhesion strength and that incorporated with pyrogallol only is unsatisfactory in adhesion strength, while the adhesive composition incorporated with the polyalkyl ether compound (IV) and pyrogallol produces a sufficient initial adhesion strength retaining the inherent or enhanced adhesion strength. Thus, the combined use of the polyalkyl ether compound (IV) and pyrogallol shows a synergistic effect. Examples 25 to 28 and Comparative Examples 8 to 12 An adhesive composition comprising ethyl a-cyanoacrylate as the component (A) and sulfur dioxide as an anionic polymerization inhibitor and hydroquinone as a radical polymerization inhibitor respectively in amounts of 0.002 % and 0.1 % based on the weight of ethyl a-cyanoacrylate was incorporated with the polyether or its derivative having the repeating units of the formula (II) as shown in Table 3 as the component (B) and the aromatic polyol (III) as shown in Table 3 as the component (C) respectively in amounts as shown in Table 3 based on the weight of ethyl acyanoacrylate. The resultant adhesive composition was subjected to measurement of adhesion strength. The results are shown in Table 3. For comparison, adhesion strength of the adhesive composition not incorporated with the components (B) and/or (C) was also measured, and the results are shown in Table 3 as Comparative Examples. In case of polyethylene glycol distearate, it was employed in the form of solution in an equal amount of di oxane'thereto. No material influence on storage stability was observed. In these Examples, measurement of adhesion strength was effected as follows: two steel pl'ates (100 x 25 x 1.6 mm) were bonded each-other with an adhesive area of 25 x 12.5 mm and cured at 200C under a relative humidity of 60 %; after cured for 5 minutes and for 24 hours, its tensile shear strength was measured with a pulling rate of 50 mm/min; ; 2 results being expressed in kg.f/cm Table 3 EMI17.1 Example <SEP> Component <SEP> (B) <SEP> Component <SEP> (C) <SEP> Tensile <SEP> shear <SEP> strangth <tb> <SEP> (kg.f/cmê) <tb> <SEP> Kind <SEP> Amount <SEP> Kind <SEP> Amount <SEP> Cured <SEP> for <SEP> Cured <SEP> for <tb> <SEP> (%) <SEP> (%) <SEP> 5 <SEP> minutes <SEP> 24 <SEP> hours <tb> <SEP> 25 <SEP> Polyethylene <SEP> glicol <SEP> #400 <SEP> 1.0 <SEP> Pyrogallol <SEP> 0.05 <SEP> 31 <SEP> 152 <tb> <SEP> 26 <SEP> Polyethylene <SEP> glicol <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 36 <SEP> 177 <tb> <SEP> monomethacrylate <tb> <SEP> 27 <SEP> Polyethylene <SEP> glicol <SEP> monomethyl <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 41 <SEP> 202 <tb> <SEP> ether <SEP> monomrthacrylate <tb> <SEP> 28 <SEP> Polyethylene <SEP> glicol <SEP> monostearate <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 38 <SEP> 190 <tb> <SEP> monoacrylate <tb> <SEP> 29 <SEP> Polyethylene <SEP> glicol <SEP> methoxy <SEP> ether <SEP> 1.0 <SEP> Pyrogallol <SEP> 0.05 <SEP> 29 <SEP> 141 <tb> <SEP> 30 <SEP> Polyethylene <SEP> glicol <SEP> diethyl <SEP> ether <SEP> 1.0 <SEP> Pyrogallol <SEP> 0.05 <SEP> 30 <SEP> 163 <tb> <SEP> 31 <SEP> Polyethylene <SEP> glicol <SEP> monolaurate <SEP> 1.0 <SEP> Pyrogallol <SEP> 0.05 <SEP> 33 <SEP> 176 <tb> <SEP> 32 <SEP> Polyethylene <SEP> glicol <SEP> distearate <SEP> 0.1 <SEP> Pyrogallol <SEP> 0.1 <SEP> 20 <SEP> 225 <tb> <SEP> 33 <SEP> Polyethylene <SEP> glicol <SEP> distearate <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 41 <SEP> 203 <tb> <SEP> 34 <SEP> Polyethylene <SEP> glicol <SEP> distearate <SEP> 1.0 <SEP> Pyrogallol <SEP> 0.01 <SEP> 47 <SEP> 152 <tb> <SEP> 35 <SEP> Polyethylene <SEP> glicol <SEP> distearate <SEP> 1.0 <SEP> Catechol <SEP> 0.05 <SEP> 25 <SEP> 158 <tb> <SEP> 36 <SEP> Polyethylene <SEP> glicol <SEP> monoethyl <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 37 <SEP> 198 <tb> <SEP> ether <SEP> monolaurate <tb> <SEP> 37 <SEP> Polyethylene <SEP> glicol <SEP> diacrylate <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 16 <SEP> 197 <tb> <SEP> 38 <SEP> 15-Crown-5 <SEP> 0.5 <SEP> Pyrogallol <SEP> 0.05 <SEP> 23 <SEP> 190 <tb> Comparative <tb> <SEP> 8 <SEP> Polyethylene <SEP> glicol <SEP> distearate <SEP> 0.5 <SEP> - <SEP> - <SEP> 30 <SEP> 145 <SEP> rial <SEP> broken <tb> <SEP> 9 <SEP> Polyethylene <SEP> glicol <SEP> monomethyl <SEP> 0.5 <SEP> - <SEP> - <SEP> 29 <SEP> 146 <tb> <SEP> monomethaceylate <tb> <SEP> 10 <SEP> - <SEP> - <SEP> Pyrogallol <SEP> 0.05 <SEP> 5 <SEP> 224 <SEP> rial <SEP> broken <tb> <SEP> 11 <SEP> - <SEP> - <SEP> Catachol <SEP> 0.05 <SEP> 4 <SEP> 152 <tb> <SEP> 12 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 8 <SEP> 148 <tb> From the results in Table 3, it is understood that the combined use of the polyether or its derivative having the repeating units of the formula (II) and the aromatice polyol (III) in a broad range of mixing ratio is effective in enhancement of the initial adhesion strength.

Claims: CLAIMS 1. An adhesive composition which comprises (A) an-cyanoacrylate ester, (B) an aliphatic polyol or a derivative thereof or a polyether or a derivative thereof and (C) an aromatic polyol. 2. A composition as claimed in Claim 1 wherein the-cyanoacrylate ester has the formula EMI19.1 wherein R is an ester residue. 3. A composition as claimed in Claim 2 wherein the ester residue is a substituted or unsubstituted,saturated or unsaturated, cyclic or non-cyclic hydrocarbon group. 4. A composition as claimed in Claim 2 wherein the ester residue is a substituted or unsubstituted, saturated or unsaturated heterocyclic group. 5. A composition as claimed in Claim 2 wherein R is C1-C16 alkyl, C1-C4 alkoxy(C1-C4)alkyl or tetrahydrofurfuryl. 6. A composition as claimed in any one of the preceding claims wherein the aliphatic polyol or the derivative thereof is an alkane polyol, alkene polyol or a halogenated alkane polyol, or an ester or ether thereof. 7. A composition as claimed in any one of the preceding claims wherein the polyether or the derivative thereof has repeating units of the formula; EMI20.1 wherein X1 and x2 are each hydrogen, halogen, hydroxyl, alkyl, alkenyl, aryl or aralkyl, the latter four groups optionally bearing any substituent thereon, p is an integer of not less than 1 and q is an integer of not less than 2. 8. A composition as claimed in any one of the preceding claims wherein the polyether or the derivative thereof is a polyalkyl ether compound of the formula: EMI20.2 wherein X1 is a hydrogen atom or a methyl group, X2 is a hydrogen atom, a methyl group or a cyano group, X3 is a hydrogen atom, -R' or -OCR" (in which R' and R" are each a hydrocarbon group not containing any anion polymerizable group) provided that when X2 is a cyano group, X3 is not a hydrogen atom, eand m are each zero or a positive integer but l + In m is not zero and n is a positive integer. 9. A composition as claimed an any one of the preceding claims wherein the aromatic polyol has the formula EMI21.1 wherein r is an integer of 2 or 3 and at least two hydroxyl groups are present at adjacent positions of the ring. 10. A composition as claimed in Claim wherein the aromatic polyol is pyrogallol. 11. A composition as claimed in any one of the preceding claims wherein the content of the component (A) is not less than 50% by weight based on the total weight of the composition. 12. A composition as claimed in Claim 11 wherein the content of component (A) is not less than 80% by weight based on the total weight of the composition. 13. A composition as claimed in any one of the preceding claims wherein the content of component (B) is from 0.05 to 20% by weight based on the weight of component (A). 14. A composition as claimed in any one of the preceding claims wherein the content of component (C) is from 0.0001 to 0.58 by weight based on the weight of component (A). 15. A process for preparing a composition as claimed in Claim 1 which comprises mixing together the components (A), )(B) and (C) as defined therein. 16. A process as claimed in Claim 15 which is further limited by any one of the features as claimed in any one of the subsidiary claims 2 to 14.

Inventors: NAKAGAWA, KAZUHIRO, NAKATO, CHIAKI, OHASI, KOITI, SHIRAISHI, YOSHIHISA
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED, TAOKA CHEMICAL CO., LTD
Application year: 1982
Main classification: C09J3
IPC codes: C08F222, C09J4, C08F299, C08F22, C08F2, C08F220, C08F290