SEQUENTIAL POLYMER USEFUL AS IMPACT MODIFIER FOR THERMOPLASTIC POLYMER, METHOD OF MAKING AND COMPOSITION CONTAINING THE POLYMER

Abstract: Sequential polymer useful in thermplastics such as PVC as impact modifier, comprise at least three stages, Stage A being a non-crosslinked, non-agglomerated polymer of at least 50% butadiene and at least 10% lower alkyl (C₂-C₈) acrylate, Stage B being a polymer of at least 80% styrene, and Stage C containing at least 50% methyl methacrylate and at least 1% alkyl (C₁-C₄) acrylate, the ratio of Stages A:B:C, excluding optional additional stages, being about 50-85:25-5:30-10, the ratio of stages C:B being at least 1.

Description: SEQUENTIAL POLYMER USEFUL AS IMPACT MODIFIER FOR THERMOPLASTIC POLYMER, METHOD OF MAKING AND COMPOSITION CONTAINING THE POLYMER This invention concerns sequential polymer useful as- impact modifier for thermoplastic polymer, especially PVC, method of making the polymer and composition containing the polymer such as impact modified thermoplastics, particularly impact modified PVC. U.S.-A-4,078,018 discloses PVC impact modifier graft polymers having a butadiene-alkyl acrylate backbone polymer which is agglomerated. As defined therein the agglomeration operation consists of enlarging a certain quantity of particles by processes different from polymerization The acrylic monomer and styrene monomer are successively grafted onto the backbone polymer in aqueous emulsion, *S.-A-3,842,144 concerns PVX impact modifiers obtained by graft polymerizing upon a cross-linked butadiene-styrene rubber latex a first and then a second grafting component in a sequential two stage process. U,S,-A-3,644,250 teaches PVC impact modifiers produced by grafting first styrene and then methyl methacrylate onto an elastomer of butadiene/n-butyl acrylate/styrene- U.S.-A-4,173,596 teaches a seed polymer of cross-linked poly(n-butylacrylate), an intermediate layer derived from n-but acrylate and an additional monomer, and an outer shell derived from styrene and methyl methacrylate. U.S,-A-3,264,373 discloses low butadiene level impact modifiers for PVC, having up to 20% butadiene, preferably up to 12t, and the balance alkyl acrylate in the rubber state, and a second stage free of styrene G.B.-A-It251^403 teaches impact modifier polymers havinq a butadiene based truntpolymer containing at least 60% butadiene and grafting polymers of first methyl methacrylate and cross-linking monomers then styrene, then methyl methacrylate and optional crosslinking monomer Each known impact modifier polymer suffers from one or more deficiencies. For example, the modifiers prepared in accordance with U.S.-A-4,078,018 may suffer destruction during processing in PVC, and may have insufficient impact efficiency. It is an object of the present invention to provide impact modifiers having attractive performance characteristics in PVC It is a further object to provide an impact modifier which may have good efficiency at low levels and at low temperatures Another object is to provide improved impact modified PVC compositions and a process for producing impact modifiers that may be capable of using fast polymerization cycle times and relatively low pressure polymerization equipment Accordingly, the present invention comprises sequential polymer of at least three stages, Stage A having at least 50% by weight of units of butadiene and at least 10% by weight of units of at least one (C2 to C8)-alkyl acrylate, Stage B having at least 80% by weight of units of styrene, Stage C having at least 508 by weight of units of methyl methacrylate and at least 1* by weight of units of at least one (C1 to C4)-alkyl acrylate, Stage A being nonagglomerated and comprising about 50 to 5% by weight of the modifier, and the weight ratio of Stage C to Stage B being at least 1. In another aspect, the invention comprises thermoplastic polymer, for example PVC containing at least 1% by weight based on thermoplastic polymer of said impact modifier. The invention also embraces a process for preparing said polymer comprising successively coating a non-crosslinked, non-agglomerated diene/ acrylate copolymer core with styrene and then with methyl methacrylate The sequential polymer of the invention unexpectedly imparts superior impact efficiency at relatively low levels of butadiene in the core. Lowering of butadiene content is advantageous as. this may permit reduction of polymerization cycle time and the use of lower pressure polymerization equipment Polymer according to the invention may have good impact efficiency when incorporated in thermoplastics at low levels and low temperatures and optionally includes. additional stages preceeding Stage A, between the stages, or after Stage C. Stage A is a non-crosslinked polymer of at least 50% by weight of units of butadiene and at least 10% by weight of units of one or more (C2-C8)alkyl acrylates Such acrylates may include butyl, hexyl, or octyl acrylate. It is important that Stage A be non-agglomerated and non-crosslinked. By noncrosslinked is meant not having units of cross-linking monomers such as divinyl benzene. Stage B, polymerized in the presence of Stage A, is a polymer containing at least 80% by weight of units of styrene. Stage C, polymerized in the presence of Stage B, is a polymer containing at least 50% by weight of units of methyl methacrylate and at least 1% by weight of units of one or more (C1-C4)-alkyl acrylates. Preferred acrylates include methyl, ethyl, (n- or iso-) propyl, and/or (n- or iso-) butyl acrylate The weight ratio of Stages A:B:C, excluding optional additional stages, is 50-85:25-5:30-10, the weight ratio of C:B being at least 1. Preferably the ratio of A:B:C is 70-85*10-15:10-20. While it im preferred that no additional stages other than A,. B, and C are present in the modifier, additional stages containing any of the aforementioned monomer units, or even other ethylenically unsaturated monomer units, can be present, but preferably do not constitute more than 25% by weight of the total polymer. Stages A, B, and C-may contain units of other monomers such as one or more of styrene, other alkyl acrylates and methacrylates-, vinyl esters, acrylonitrile, and, except in the case of Stage A, crosslinking monomers comprising one or more of the following: divinyl benzene, diacrylates and dimethacrylates (including for example ethylene glycol dimethacrylate, butylene glycol diacrylate, and allyl methacrylate). The sequential polymer can be prepared by gradually feeding the monomers of Stage A into a reactor either simultaneously or batchwise whereby a uniform particle size in the desired range can be obtained. The particles are grown to the desired particle size, preferably 1500 to 2000 A?, rather than to some smaller size with subsequent agglomeration. Subsequent stages are polymerized in the presence of preferred Stage A under conditions known in the art, such as soap concentration, so that the locus of polymerization is at the surface of the previously formed particles. The polymer may be incorporated in thermoplastic polymers such as PVC by conventional compounding methods, and in amounts of for example 1 to 25% by weight, preferably 3 to 15%, based on the weight of thermoplastic polymer. The following examples serve to illustrate, but not limit, the invention and provide a comparison with a known impact modifier. EXAMPLES Example 1 - Preparation of Sequential Polymer A. Preparation of butadiene-butyl acrylate polymer -Stage A The materials are: 77 parts of butadiene (Bd) 23 parts of butyl acrylate (BA) 4 parts of methyl methacrylate (MMA) T parts of butadiene/styrene seed polymer a. 05- parts of acetic acid 1.7 parts of sodium lauryl sulphate (SLS) eaw parts of sodium chloride .,parts cumene hydroperoxide (CHP) .3 parts sodium formaldehyde sulfoxylate (SFS) 95 parts of deionized water The- deionized water acid, seed polymer, and portions of the SLSr CHP, and SFS, are charged into stainless steel high pressure reactor. At a temperature of 80 C, at 4 hour gradual feed of the monomers (except MMA) is; begun The remaining materials (except the MMA and a small portion of the CHP) are added either gradually or shot wise during the 4 hour period. The reaction temperature will exotherm to 95 0C. After the completion of the 4 hour period, the monomer conversion is at least 85%. The MMA and remaining CHP are then fed during 3 hours while the reaction mixture is cooled to 650C The conversion at the end is at least 95%. B Preparation of the Grafted Polymer - Stage B The materials used are= 70 parts of Bd/BA polymer (in the form of the latex generated above) I35 parts of styrene (St) 3,3 parts of deionized water 0.1 parts of CHP OS parts of-SFS The styrene, deionized water, and SFS are added to the agitated reaction mixture at 30 C. The CHP is then added in shots over 75 min. The reaction mixture is then maintained for } hour. C Stage C The materials used are 83- parts of Bd/BA/St polymer (in the form of the latex generated above) I49 parts of methyl methacrylate IW6 parts, ethyl acrylate (EA) 3.1 parts of deionized water .015 parts SFS 034 parts CHP After adding the deionized water and SFS, a 1 hour gradual addition or monomer and CHP is begun. After maintaining for 0.5 hour, additional initiator (@017 parts butyl hydroperoxide and .005 parts SFS) is added Following this, a stabilizer based on butylated hydroxy toluene antioxidant (BHT), 1.40 parts, is added. The polymer is isolated by spray drying in one case and by coagulation in another. Example 2 - Comparative In this example, the effects of agglomeration of the Stage A rubber are demonstrated to distinguish the invention from U.S-A-4,078,018. Preparation of the Bd/BA polymer - State A The materials used are: 80 parts of butadiene 20 parts of butyl acrylate 1 part of potassium chloride 120 parts of deionized water 3 parts of potassium laurate 0.Z parts of n-dodecyl mercaptan 0.3 parts of potassium persulfate The reaction mixture is heated to 75 0C and kept at this temperature for 8 hours. The conversion is 95%, The agglomeration is performed as follows: To the latex obtained above, there is added 0.006 parts of polyethylene glycol, having a molecular mass of 20,000, in aqueous solution at 0.5 g/l The mixture is heated to 80 C for 5 min. and then cooled. Stage B The materials used are: 50 parts Bd/BA polymer (in the form of the agglomerated latex generated above) 170 parts deionized water 0.5 parts potassium persulfate in 10 parts of deionized water 25 parts methyl methacrylate (MMA) The agitated reaction mixture is heated to and maintained at 800C. Following addition of the potassium persulfate solution, the MMA is added continuously over 2 hours The mixture is maintained for another 2 hours. Stage C The materials used are: 75 parts of Bd/BA/MMA (in the form' of the latex generated above) 25 parts styrene To the agitated reaction 'mixture at 80 C, the styrene is added over 2 hours. The reaction mixture is maintained for 2 hours Following this, a stabilizer based on BHT (1.47 parts) is added. The polymer is isolated by addition of three times the theoretical amount (based on the emulsifier) of a mixture of hydrochloric acid and sodium chloride in 10% aqueous solution The coagulated product is filtered, washed and dried It should be noted that the' rubber composition of Example 1 Bd/BA/MMA = 74I/22.I/3.8 varied slightly from that of Example 2, Bd/BA = 80/20, following the teachings of the patent Particle size determinations showed the agglomerated rubber to be 1320 A0 (green light) - 1630 A (blue light) Example -3 - Evaluation For Impact Efficiency -Samples- of PVC formulations containing the impact modifier polymer prepared in Example t, in accordance with the invention, and Example 2, in accordance with U.S.-A-4,078,018, were molded into standard bars for Izod impact strength testing. For each case 15 phr of modifier was used In this Izod test, 60 bars of each formulation were tested at each of two temperatures, 10 C and 0 C. A ductile break shows impact resistance whereas a non-ductile break indicates failure. In this test the samples containing the modifier of the invention gave 59 ductile breaks at 100C and 26 ductile breaks at OOC, whereas the samples containing modifier prepared in accordance with the prior art gave no ductile breaks at either temperature, establishing an unexpected advantage of using the present sequential polymer as an impact modifier wherein Stage A is non-agglomerated.

Claims: CLAIMS: 1. Sequential polymer comprising at least three stages, Stage A being a non-crosslinked, non-agglomerated polymer comprising at least 50% by weight of units of butadiene and at least 10% by weight of units of one or more (C2-C8)-alkyl acrylates, Stage B polymer comprising at least 80% by weight of units- of styrene,'and Stage C polymer comprising at least 50* by weight of units of methyl methacrylate and at least 1% by weight of units of one or more (C1-C4)-alkyl acrylates, the weight ratio of Stages A:B:C, excluding optional additional stages, being 50-85:25-5:-30-10, the ratio of Stages C:B being at least 1. 2 Polymer according to claim 1 wherein the (Cl-C4)-alkyl acrylate in Stage C comprises ethyl acrylate 3 Polymer according to either preceding claim wherein the alkyl acrylate in Stage A comprises butyl acrylate. 4. Polymer according to any preceding claim wherein the ratio of Stages A-B:C is 70-85t10-15=10-2.0, 5 Polymer according to any preceding claim containing no additonal stages other than Stages A, B, and C.- 6. Polymer according to any preceding claim wherein the butadiene:alkyl acrylate ratio in Stage A is 75-95:25-5. 7. Polymer according to any preceding claim wherein optional additional monomer units are included in Stages A, B, or C and comprise one or more of: styrene, lower alkyl acrylates, methacrylates, vinyl esters, acrylonitrile and crosslinking monomer units comprising one or more of: divinyl benzene, ethylene glycol dimethacrylate butylene glycol diacrylate, and allyl methacrylate; provided that said crosslinking monomer units are not included in Stage A. 8. Polymer according to any preceding claim wherein Stage A comprises copolymer of butadiene and butyl acrylate units, Stage B consists of styrene units, and Stage C comprises copolymer of methyl methacrylate and ethyl acrylate units, 9. A method of preparing polymer according to any preceding claim which comprises feeding the monomers of Stage A into a reactor in a manner so as to yield a Stage A polymer of uniform particle size in the range 1500 to 2000 A , and polymerizing subsequent stages B and C in the presence of previously formed particles of said stage A polymer under conditions such that the locus of polymerization is at the surface of the previously formed particles. 10 Polymer; composition comprising thermoplastic polymer and 1,to 258 by weight based on thermoplastic polymer of polymer according to any of claims 1 to 8. 11. Polymer composition according to claim 10 wherein said thermoplastic polymer comprises PVC. EMI12.1 CLAIMS: 1. A method of making sequential polymer comprising at least three stages, Stage A being Åa ,non-crosslinked, non-agglomerated polymer comprising at least 50% by weight of units of butadiene and at least 10% by weight of units of once or more (C2-C8)-alkyl acrylates, Stage B polymer comprising at least 80 by weight of units of styrene and Stage C polymer comprising at least 50% by weight of units of methyl methacrylate and at least 1% by weight of units of one or more (C1-C4)alkyl acrylates, the weight ratio of Stages A:B:O, excluding optional additional stages, being 50-85: 25-5:30-10, the ratio of Stages C: :B being at least I, which method comprises feeding the monomers of Stage A into a reactor in a manner so as to yield a Stage A polymer of uniform particle size in the range 1500 to 2000 A , and polymerizing subsequent stages B and C in the presence of previously formed particles of said stage A polymer under conditions such that the locus of polymerization is at the surface of the previously formed particles 2 Method according to claim 1 wherein the (Cl-C4)-alkyl acrylate in Stage C comprises ethyl acrylate 3. Method according to either preceding claim wherein the alkyl acrylate in Stage A comprises butyl acrylate. 4. Method according to any preceding claim wherein the ratio of Stages A:B:C is 70-85:10-15:10-20. 5. Method according to any preceding claim containing no additonal stages other than Stages A, B, and C. EMI13.1 6. Method according to any-preceding claim wherein the butadiene:alkyl acrylate ratio in Stage A is 75-95:25-5. 7. Method according to any preceding claim wherein optional additional monomer units are included in Stages A, B, or C and comprise one or more of: styrene, lower alkyl acrylates, methacrylates, vinyl esters, acrylonitrile and crosslinking monomer units comprising one or more of: divinyl benzene, ethylene glycol dimethacrylate; butylene glycol diacrylate, and allyl methacrylate; provided that said crosslinking monomer units are not included in Stage A, 8. Method according to any preceding claim wherein Stage A comprises copolymer of butadiene and butyl acrylate units, Stage B consists of styrene units, and Stage C comprises copolymer of methyl methacrylate and ethyl acrylate units. Use of a sequential polymer produced by a method according to any preceding claim as impact modifier in thermoplastic polymer. 10 Use according to claim 9 wherein said thermoplastic polymer is PVC, the sequential polymer comprising from 1 to 25% by weight based on the weight of PVC

Inventors: GOLDMAN, THEODORE DANIEL
Applicants: ROHM AND HAAS COMPANY
Application year: 1982
Main classification: C08F285
IPC codes: C08L51, C08F285, C08F220, C08L1, C08L27