Sandwich glass

Abstract: A sandwich glass comprising glass plates and an intermediate layer interposed therebetween is disclosed. The intermediate layer may be formed by crosslinking a resin composition comprising an ethylene-vinyl acetate copolym­ er and an organic peroxide under heating of the resin composition above the melting point of the copolymer. Alternatively, the intermediate layer may be formed by photocrosslinking a resin composition comprising an ethylene-vinyl acetate copolymer and a photosensitizer under light irradiation during or after heating of the resin composition above the melting point of the copolymer.

Description: This invention relates to sandwich glass, to be used in windscreens for automobiles or in windows for buildings. In this type of sandwich glass, plasticized polyvinylbutyral resins have commonly been used in the intermediate layer for the sandwich glass. However, such resins are thermoplastic and have the following drawbacks when used for the production of the intermediate layer: (1) Since the softening point of the resin is relatively low, sliding between the glass plates and the occurrence of bubbles are observed when the sandwich glass is heated. (2) Since the sandwich glass is apt to be influenced by moisture content, when the sandwich glass is left to stand in a high-humidity atmosphere for a long period of time, not only does the sandwich glass become hazy from its peripheral part, but also the adhesive strength of the resin to the glass plate lowers. (3) The penetration resistance is remarkably degraded at a temperature range above room temperature (about 30°C) because the resistance to impact fracture is highly dependent upon the temperature. U.S. Patent Nos. US-A-3622440, US-A-3666614, US-A-3923757 and US-A-4137364 may be noted as examples of the prior art disclosing laminates utilizing an intermediate layer of a cross-linked ethylene-vinyl acetate (EVA) copolymer. US-A-3622440 and US-A-3666614 are particularly concerned with the bonding of glass and resin (particularly polycarbonate) sheet through an intermediate layer of EVA copolymer. US-A-3923757 and US-A-4137364 utilize a partially hydrolysed EVA copolymer. There may also be noted as prior art British Patent Specification No. GB-A-1565674 referring to cross-linked EVA copolymers for use in laminates, and French Patent Specification Nos. FR-A-2445222 referring to sandwich glasses containing a photo-cross-linked copolymer having acryloyloxy radicals. It is an object of the present invention to provide sandwich glasses which can avoid and overcome the previously mentioned drawbacks of the conventional sandwich glass by using resin material other than plasticized polyvinylbutyral resin as the intermediate layer. For this purpose, the inventors have mane various studies with respect to resin materials and have considered the use of ethylene-vinyl acetate copolymer resin (hereinafter referred to as EVA resin). The transparency and other properties of EVA resin vary in accordance with the vinyl acetate content. For instance, when the vinyl acetate content is about 40%, the transparency is good, but the tensile properties are insufficient, the strength at rupture is low and the elongation is more than 1,000%, so that the use of EVA resin having such a vinyl acetate content is not suitable for the formation of the intermediate layer in sandwich glass. On the other hand, when the vinyl acetate content is about 15%, the strength properties are satisfied to a certain extent as a material for the intermediate layer of sandwich glass, but the transparency is low, so that EVA resin having such a vinyl acetate content may not be suitable for the formation of a highly transparent intermediate layer. Moreover, the EVA resin is readily influenced by temperature owing to its thermoplasticity and in particular undergoes deterioration of its properties at high-temperature in the same manner as conventional plasticized polyvinylbutyral resin. As described above, the transparency is certainly improved by increasing the vinyl acetate content, but its so-called cloudy phenomenon (opaque white) is still a problem as compared with the transparency of the glass plate to be superposed. Now, the inventors have made further investigations and found that when non-hydrolysed ethylene-vinyl acetate copolymer is crosslinked or photocrosslinked by heating the resin composition above the melting point of the copolymer in the presence of an organic peroxide or a photosensitizer, the resulting EVA resin exhibits a surprisingly high transparency and is very suitable for use as an intermediate layer of sandwich glass. More particularly, the present invention in a first aspect provides a sandwich glass to be used in windscreens for automobiles or in windows for buildings, consisting of glass plates and an intermediate layer interposed therebetween, characterized in that the said intermediate layer is formed by crosslinking a resin composition comprising a non-hydrolysed ethylene-vinyl acetate copolymer having a vinyl acetate content of 19 - 40% by weight and an organic peroxide and an acryloyloxy or methacryloyloxy group-containing compound or an allyl or vinyl-group containing compound as a curing assistant under heating of the said resin composition above the melting point of the copolymer; in that the said organic peroxide is utilized in an amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer; and in that the said resin composition contains not more than 50% by weight of the said curing assistant; wherein the said resin composition is thoroughly kneaded to uniformly disperse the organic peroxide into the ethylene-vinyl acetate copolymer, and then shaped into a sheet. The invention in a second aspect provides a sandwich glass to be used in windscreens for automobiles or in windows for buildings, consisting of glass plates and an intermediate layer interposed therebetween, characterized in that the said intermediate layer is formed by photocrosslinking a resin composition comprising a non-hydrolysed ethylene-vinyl acetate copolymer having a vinyl acetate content of 19 - 40% by weight and a photosensitizer and an acryloyloxy or methacryloyloxy group-containing compound or an allyl or vinyl-group containing compound as a curing assistant under light irradiation during or after heating of the said resin composition above the melting point of the copolymer; in that the said photosensitizer is utilized in amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer; and in that the said resin composition contains not more than 50% by weight of the said curing assistant; wherein the said resin composition is thoroughly kneaded to uniformly disperse the photosensitizer into the ethylene-vinyl acetate copolymer, and then shaped into a sheet. In the first aspect of the invention, an organic peroxide is used as a curing agent for the ethylene-vinyl acetate copolymer in the manufacture of the sandwich glass. As the organic peroxide, use may be made of any compound producing radicals by decomposition at a temperature above 100°C, but the use of compounds having a half-life period of 10 hours and a decomposition temperature of not less than 70°C is preferable having regard to the stability during blending. Suitable organic peroxides are 2,5 - dimethylhexane - 2,5 - dihydroperoxide, 2,5 - dimethyl - 2,5 - di(t - butylperoxy)hexane - 3, di-t-butyl peroxide, t-butylcumyl peroxide, 2,5 - dimethyl - 2,5 - di(t - butylperoxy(hexane, dicumyl peroxide, α,α' - bis(t - butylperoxyisopropyl)benzene, n - butyl - 4,4' - bis(t - butylperoxy(valerate, 2,2 - bis)t - butylperoxy)butane, 1,1 - bis(t - butylperoxy)cyclohexane, 1,1 - bis(t - butylperoxy)3,3,5 - trimethyl cyclohexane, t-butylperoxy benzoate, and benzoyl peroxide. At least one organic peroxide preferably selected from the above compounds is used in an amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer. Moreover, the organic peroxide may be used by dissolving in an organic solvent or a plasticizer. In the second aspect of the invention, a photo-sensitizer is added to the ethylene-vinyl acetate copolymer. As the photosensitizer, use may be made of any compound directly or indirectly producing radicals by irradiation of light. Suitable photosensitizers are benzoin, benzophenone, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, dibenzyl 5-nitro acetonaphthene, hexachloro cyclopentadiene, p-nitrodiphenyl, p-nitroaniline, 2,4,6-trinitroaniline, 1,2-benzanthraquinone, and 3 - methyl - 1,3 - diaza - 1,9 - benzanthrone. At least one photosensitizer preferably selected from the above compounds is used in an amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer. A plasticizer may be suitably added to the mixture of ethylene-vinyl acetate copolymer and organic peroxide or photosensitizer in an amount of 0.5-30 parts, more preferably 1-10 parts, based on 100 parts of the mixture. Such an addition amount of the plasticizer is determined having regard to the compatibility with EVA, necessary transparency, and impact resistance after the manufacture of the sandwich glass. When the amount of the plasticizer is less than 0.5 part, the addition effect is substantially insignificant, while when the amount exceeds 30 parts, bleeding of the plasticizer from the mixture is caused and the properties of the resulting mixture are adversely affected. Suitable plasticizers are high-purity paraffinic oil giving no colouring nor increase of haze value to the EVA intermediate layer, naphthenic oil, phthalate esters, adipate esters, sebacate esters, thioglycols, ether series plasticizers such as dibenzyl ether, phosphoric acid series plasticizers such as tricresyl phosphate, maleate esters such as dioctyl maleate, and epoxy plasticizers. The addition of the plasticizer lowers the processing temperature in the case of uniformly dispersing the organic peroxide or photosensitizer into the EVA and in the case of forming film or sheet from the resin composition by various processing machines, whereby gelation and scorching of the resin composition can be prevented. An acryloyloxy or methacryloyloxy group-containing compound preferably selected from derivatives of acrylic and methacrylic acids, or a vinyl or ally group-containing compound is added as a curing assistant to the resin composition in an amount of not more than 50% by weight per ethylene-vinyl acetate copolymer. The addition of the curing assistant contributes not only to improve the properties, particularly initial modulus, of EVA resin as an intermediate layer to enhance the penetration resistance but also to improve the degree of crosslinking and crosslinking rate in the case of photocrosslinking. As derivatives of acrylic or methacrylic acid, there are most commonly used esters and amides. As alcohol radicals of such esters, mention may be made of alkyl groups such as methyl, ethyl, dodecyl, stearyl, and lauryl, as well as cyclohexyl, tetrahydrofurfuryl, aminoethyl, 2-hydroethyl, 3-hydroxypropyl, and 3 - chloro - 2 - hydroxypropyl groups. Further, there may be used esters with polyfunctional alcohols such as ethylene glycol, triethylene glycol, polyethylene glycol, trimethylolpropane, and pentaerythritol. A typical example of a suitable amide is diacetone acrylamide. Suitable vinyl group-containing compounds are styrene and divinylbenzene. Suitable allyl group-containing compounds are triallyltrimellitate, triallylisocyanurate, and diallylphthalate. In order to improve the adhesion between the intermediate layer and the glass plates, a well known silane coupling agent may be added to the resin composition in an amount of not more than 5% by weight per the ethylenevinyl acetate copolymer. Suitable silane coupling agents are γ-chloropropyl trimethoxysilane, vinyltrichlorosilane, vinyltriethoxysilane, vinyl-tris(β-methoxy)silane, γ-methacryloxypropyl trimethoxysilane, β - (3,4 - ethoxycyclohexyl)ethyl - trimethoxysilane γ-glycidoxypropyl trimethoxysilane, vinyl-triacetoxysilane, γ-mercaptopropyl trimethoxysilane, γ-aminopropyl triethoxysilane, and N - β - (aminoethyl) - γ - aminopropyl trimethoxysilane. Alternatively, a method of subjecting the intermediate layer to corona discharge, low temperature plasma treatment (glow discharge), electron beam irradiation, or ultraviolet ray irradiation is effective for improving the adhesion. Furthermore, in order to improve the storage stability, not more than 5% by weight of a polymerization inhibitor such as hydroquinone, hydroquinone monomethyl ether, p-benzoquinone or methylhydroquinone may be added to the resin composition. In addition to the above described additives, one or more of colourant, ultraviolet absorbing agent, stabilizer, and discolouration-preventing agent may be optionally added to the resin composition in accordance with the intended use of the sandwich glass. The manufacture of sandwich glass using the EVA resin composition is performed in the same manner as in the manufacture of sandwich glass using conventional plasticized polyvinylbutyral resin. That is, the resin composition is thoroughly kneaded for example by means of a roll mill, and then shaped into a sheet using an extruder, a calender, an inflation die, or a hot press. The resulting sheet is interposed between two glass plates to be superposed and gradually heated up to about 80°C while passing through several sets of rolls, during which the sheet is softened and adhered tightly to the glass plates while expelling air from between the sheet and the glass plates by increasing the pressure between the rolls. Then, the resulting glass assembly provided with the uncured resin intermediate layer is heated on a hot plate, whereby the intermediate layer is crosslinked to provide a sandwich glass having a substantially completely transparent intermediate layer. In this case, there may be used any heating means conventionally used such as hot air, an oven, an autoclave, infrared or far infrared irradiation, or dielectric heat. Moreover, in order to completely expel air from between the glass plates and the intermediate layer, the glass assembly may be housed in a rubber bag and then the pressure inside the bag may be reduced under heating, whereby the intermediate layer may be adhered tightly to the glass plates. When the intermediate layer contains a photosensitizer, light is irradiated to the glass assembly during the heating, whereby the intermediate layer is photocrosslinked. In this case, various light sources emitting light in the ultraviolet to visible regions can be adopted, for example an extra-high pressure mercury lamp, a high pressure mercury lamp, a low pressure mercury lamp, a chemical lamp, a xenon lamp, a halogen lamp, a mercury-xenon lamp, a carbon arc lamp, sun light, an incandescent lamp, or a laser beam as disclosed by S. P. Pappers in "UV Curing", Science and Technology , Technology Marketing Corporation, 1980. The irradiation time is dependent upon the kind of lamp and light intensity, but it is usually within a range of several tens of seconds to several tens of minutes. In order to perform the heating before or during the light irradiation, heat radiated from the light source may be locally or wholly utilized. In addition, a known heat source such as hot air, electric heat, dielectric heat, warm water, steam, or far infrared irradiation can be used directly or indirectly. In other words, the heating means may be optionally selected provided the intermediate layer is heated above the predetermined temperature during the light irradiation. In any case, it is necessary to heat the intermediate resin layer to a temperature above its melting point because the transparency of the resulting sandwich glass is insufficient when the heating is performed at a temperature below the melting point. As mentioned above, the production of sandwich glass using ethylene-vinyl acetate resin according to the invention is the same as in the case of using conventional plasticized polyvinylbutyral resin. However, there is a notable difference in technique between the two production methods because when the glass assembly according to the invention is heated on a hot plate, the intermediate resin layer is crosslinked and at the same time changed from a cloudy state into a transparent state, which can overcome the disadvantages produced by the use of the conventional plasticized polyvinylbutyral resin. In a sandwich glass according to the invention, the intermediate resin layer is strongly bonded to the glass plates by crosslinking or photocrosslinking without adjustment of moisture content after the removal of salt sprayed on the sheet by washing with water as required in the case of the conventional plasticized polyvinylbutyral resin, so that there is no formation of bubbles and no sliding between the glass plates due to the softening of the intermediate layer even when the sandwich glass is exposed to high temperatures. Furthermore, even when the sandwich glass is broken due to impact, no peeling-off is caused between the intermediate layer and the glass plates, so that scattering of broken glass pieces is largely prevented. Moreover, the temperature dependence of penetration resistance of the sandwich glass according to the invention is small as compared with that of conventional sandwich glass using plasticized polyvinylbutyral resin as an intermediate layer. The invention will be further described with reference to the following illustrative Examples. In the following Examples, only Examples 6 to 8 and 13 to 15 are within the scope of the invention claimed. Examples 1-5 (a) Preparation of EVA resin composition Five EVA resin compositions each having a compounding recipe as shown in the following Table 1 were prepared by mixing in a roll mill heated at a temperature of about 80°C-130°C. Example 1 2 3 4 5 Commercially available ethylene-vinyl acetate copolymer (part by weight) vinyl acetate content: 40 wt% 100 vinyl acetate content: 33 wt% 100 vinyl acetate content: 28 wt% 100 100 vinyl acetate content: 19 wt% 100 Dicumyl peroxide 1 1 1 1 0.5 γ-Glycidoxypropyl trimethoxysilane 0.5 0.5 0.5 0.5 0.5 (b) Manufacture of sandwich glass The resin composition described in the above item (a) was shaped into a sheet having a thickness of 0.36 mm through polyethylene terephthalate film by a hot press. After cooling to room temperature, the resulting resin sheet was peeled off from the polyethylene terephthalate film and interposed between two previously washed and dried float glasses with a thickness of 3 mm. Then, the resulting glass assembly was deaerated under vacuum in a rubber bag, subjected to a preliminary contact bonding at a temperature above 80°C and thereafter heated on a hot plate at a temperature of 160°C for 20 minutes. The thus obtained sandwich glass had a high transparency and no optical distortion. (c) Impact test A steel ball having a weight of 225 g and a smooth surface was dropped from a height of 5 m onto a central portion of a sandwich glass according to an impact test method of JIS R 3025. In all sandwich glasses of Examples 1-5, the steel ball did not penetrate through the sandwich glass, and also cracks of the intermediate resin layer and scattering of glass pieces were hardly produced. (d) Transparency test The transmittance and haze value of the sandwich glasses in Examples 1-5 were measured by using an integral-type turbidimeter made by Tokyo Denshoku Co., Ltd. For comparison, the same test was made with respect to sandwich glass using only the EVA resin of each of Examples 1-5 as an intermediate layer. The measured results are shown in the following Table 2. Transmittance (%) Haze value (%) Comparative Example 1 (EVA resin, vinyl acetate content: 40 wt%) 82.5 1.1 Example 1 81.5 0.1 Comparative Example 2 (EVA resin, vinyl acetate content: 33 wt%) 82.5 3.1 Example 2 82 0.1 Comparative Example 3 (EVA resin, vinyl acetate content: 28 wt%) 80.7 3.1 Example 3 82 0.1 Comparative Example 4 (EVA resin, vinyl acetate content: 19 wt%) 79.0 35.4 Example 4 83 0.6 Example 5 83 0.2 As apparent from Table 2, the effect of improving the haze value in the sandwich glasses of Examples 1 to 5 is remarkable and the resulting sandwich glasses are sufficiently suitable for practical use. Examples 6-8 (a) Preparation of EVA resin composition Three EVA resin compositions were prepared in the same manner as described in Example 1 using a compounding recipe (part by weight) as shown in the following Table 3. Example 6 7 8 EVA resin, vinyl acetate content: 28 wt% 90 80 90 Ethylene glycol dimethacrylate 10 20 - Trimethylpropane trimethacrylate - - 10 Dicumyl peroxide 1 1 1 γ-Glycidoxypropyl trimethoxysilane 0.5 0.5 0.5 (b) Manufacture of sandwich glass The sandwich glass was manufactured by using the above EVA resin composition in the same manner as described in Example 1, except that the thickness of the resin sheet was 0.90 mm. The resulting sandwich glass of Examples 6-8 had a high transparency and no optical distortion. (c) Impact test A steel ball having a weight of 2.3 kg and a smooth surface was dropped from a height of 4 m onto a central portion of a sandwich glass according to an impact test method of JIS 3211 and 3212. In all sandwich glasses of Examples 6-8, the steel ball did not penetrate through the sandwich glass, and also there was produced no scattering of glass pieces. (d) Transparency test The haze value in the sandwich glasses of Examples 6-8 was measured in the same manner as described in Example 1 to obtain a result as shown in the following Table 4. For comparison, the haze value of sandwich glass using only the EVA resin as an intermediate layer with a thickness of 0.90 mm is also shown in Table 4. Haze value (%) Comparative Example 5 (EVA resin, vinyl acetate content: 28 wt%) 3.8 Example 6 0.1 Example 7 0.1-0 Example 8 0.1 (e) Tensile test of resin sheet Each of the EVA resin compositions of Examples 6-8 was shaped into a cured sheet having a thickness of 1 mm by means of a hot press under curing conditions of 160°C and 20 minutes. A sample was punched out from the cured sheet by a punch of DIN No. 3, whose tensile properties were measured by an autograph (tensile testing machine, made by Shimazu Seisakusho) at a crosshead speed of 200 mm/min to obtain results as shown in the following Table 5. Comparative Example 5 Example 6 Example 7 Example 8 50% Modulus (kPa) 2871 3842 4900 4273 100% Modulus (kPa) 3126 4214 5557 5214 300% Modulus (kPa) 3822 7526 10780 8761 Tensile strength at break (kPa) 11662 26362 26754 26657 Elongation at break (%) 650 590 500 540 Examples 9-12 (a) Preparation of EVA resin composition Three EVA resin compositions A-C were prepared according to a compounding recipe as shown in the following Table 6 by means of a roll mill heated at 80-90°C. A B C Commercially available EVA copolymer vinyl acetate content: 33 wt% 100 vinyl acetate content: 28 wt% 100 vinyl acetate content: 25 wt% 100 Benzoin isopropyl ether 1 1 1 γ-Glycidoxypropyl trimethoxysilane 0.5 0.5 0.5 (b) Manufacture of sandwich glass Each of the EVA resin compositions A-C was shaped into a sheet having a thickness of 0.4 mm through polyester films by a press at 100°C. After the polyester film was peeled off, the resulting resin sheet was interposed between two washed and dried float glasses with a thickness of 3 mm and deaerated under vacuum in a rubber bag at a temperature of 100°C for 5 minutes to obtain a bubble-free glass assembly. Immediately, ultraviolet rays were irradiated on the resulting glass assembly by means of a 4 kw ultraviolet ray irradiation apparatus from a distance of 15 cm for 1 minute, provided that the irradiation was performed on one surface of the glass assembly for 30 seconds, to manufacture a sandwich glass corresponding to each of Examples 9-11. Moreover, the sandwich glass of Example 12 was manufactured by heating the glass assembly provided with the intermediate layer of the EVA resin composition C at a temperature of 160°C and irradiating the ultraviolet rays in the same manner as described above. (c) Impact test The same impact test according to JIS R 3025 as described in Example 1 was repeated with respect to the sandwich glasses of Examples 9-12. In these sandwich glasses, the steel ball did not penetrate through the sandwich glass, and also there were produced no cracks of the intermediate layer and no scattering of glass pieces. (d) Transparency test The haze value of each sandwich glass of Examples 9-12 was measured in the same manner as described in Example 1 to obtain a result as shown in the following Table 7. Haze value (%) Example 9 0.12 Example 10 0.3 Example 11 0.8 Example 12 0.6 Examples 13-15 (a) Preparation of EVA resin composition The EVA resin composition was prepared according to a compounding recipe as shown in the following Table 8 in the same manner as described in Example 9. Example 13 14 15 EVA resin, vinyl acetate content: 25 wt% 90 80 80 Trimethylolpropane trimethacrylate 10 20 10 Ethyleneglycol dimethacrylate 10 Benzoin isopropyl ether 1 1 1 γ-Glycidoxypropyl trimethoxysilane 0.5 0.5 0.5 (b) Manufacture of sandwich glass The sandwich glass was manufactured by using the above EVA resin composition in the same manner as described in Example 9 except that the thickness of the intermediate layer was 1.0 mm. (c) Impact test The same impact test as described in Example 6 was repeated with respect to the sandwich glass. In all sandwich glasses of Examples 13-15, the steel ball did not penetrate through the sandwich glass, and also there was produced no scattering of glass pieces. (d) Measurement of properties The EVA resin composition was shaped into a sheet having a thickness of about 1 mm through polyester films by a press heated at 100°C. Immediately after removal from the press, the resulting sheet was photocrosslinked by irradiating ultraviolet rays emitted from a 4 kw ultraviolet ray irradiation equipment on both surfaces of the sheet at a distance of 15 cm for a total time of 1 minute. After peeling-off of the polyester film, the tensile properties of the sheet were measured in the same manner as described in Example 6 to obtain results as shown in the following Table 9. Comparative Example 6 Example 13 Example 14 Example 15 50% Modulus (kPa) 2871 3332 4606 4214 100% Modulus (kPa) 3126 3724 5390 4900 300% Modulus (kPa) 3822 6272 11564 10192 Tensile strength at break (kPa) 11662 17542 21364 19404 Elongation at break (%) 650 560 450 450 Haze value (%) 3.8 0.95 0.24 0.24 Note) In Comparative Example 6, only the EVA resin composition having a vinyl acetate content of 25% by weight was used as an intermediate layer. As apparent from Table 9, the addition of methacrylate ester improves the properties of the intermediate layer. Example 16 This example shows the addition effect of a plasticizer with regard to the EVA resin composition. The EVA resin composition having a compounding recipe as shown in the following Table 10 was uniformly kneaded by means of a roll mill. In this case, the roll temperature for kneading was measured to obtain a result as shown in Table 10. Then, the resulting resin composition was shaped into a sheet by extruding through a T-die (slit: 0.5 mm, width: 400 mm, die temperature: 100°C) mounted to a small extruder having a screw diameter of 40 mm, which was interposed between two glass plates and adhered tightly to the glass plate under reduced pressure in a rubber bag. In this case, the temperature for adhering to the glass plate was visually measured to obtain a result as shown in Table 10. For comparison, the temperatures for an EVA resin composition having no plasticizer (which substantially corresponds to Example 4) were measured to obtain results as shown in Table 10. Example 16 Control Commercially available EVA copolymer vinyl acetate content: 19 wt% 100 100 Dicumyl peroxide 1 1 Dioctylphthalate 10 - γ-Glycidoxypropyl trimethoxysilane 1 1 Roll temperature for kneading (°C) 85 105 Temperature for adhering to glass plate (°C) 75 100 As apparent from Table 10, the roll temperature for kneading and the temperature for adhering to glass plate can be reduced by adding the plasticizer to the EVA resin composition. Examples 17-21 The EVA resin composition having a compounding recipe as shown in the following Table 11 was kneaded by means of a roll mill and shaped into a sheet having a size of 300 mm × 300 mm × 0.4 mm by a press. The resulting resin sheet was interposed between two float glasses each having a size of 300 mm × 300 mm × 3 mm and deaerated at 75°C under a reduced pressure in a rubber bag to obtain a bubble-free glass assembly. Then, the glass assembly was placed on a hot press, where crosslinking of the resin sheet was performed under heating conditions of 160°C and 20 minutes to obtain a transparent sandwich glass. The haze value of the sandwich glass was measured in the same manner as described in' Example 1 to obtain a result as shown in Table 11. Example 17 18 19 20 Commercially available EVA copolymer vinyl acetate content: 28 wt% (15) 100 vinyl acetate content: 25 wt% (2) 100 vinyl acetate content: 19 wt% (25) 100 100 Dioctylphthalate 10 10 10 Dioctyladipate 10 Dicumyl peroxide 1 1 1 1 γ-Glycidoxypropyl trimethoxysilane 0.5 0.5 0.5 0.5 Stearic acid 0.5 0.5 0.5 0.5 Haze value (%) 0 0.1 0.2 0.5 As apparent from Table 11, the reduction of haze value (or the improvement of transparency) is achieved even when plasticizer is added to the EVA resin composition. The impact test for the sandwich glass was made by dropping a steel ball having a weight of 2.3 kg and a smooth surface from a height of 1.5 m according to JIS 3211 and 3212 to obtain a result as shown in Table 12. In this case, the sandwich glass was manufactured by using as an intermediate layer having a thickness of 0.45 mm the resin sheets of Examples 18 and 19 as well as a resin sheet of Example 21 having the same compounding recipe as in Example 18 except that a commercially available EVA copolymer having a vinyl acetate content of 19% was used. Example 18 19 21 Dropping of steel ball from height of 1.5 m no penetration no penetration no penetration As apparent from Table 12, deterioration of impact resistance hardly occurs each when plasticizer is added to the EVA resin composition. Example 22 An EVA resin composition consisting of 100 parts by weight of commercially available EVA copolymer (vinyl acetate content: 28% by weight, melt flow index: 15) and 1 part by weight of 2,5 - dimethyl - 2,5 - di(t - butylperoxy)hexane was kneaded by means of a roll mill and shaped into three sheets each having a size of 300 mm × 300 mm × 0.4 mm by a press. Among these sheets, a first sheet was subjected to electron beam irradiation using an electron beam accelerator under such conditions that the acceleration voltage was 300 KeV and the irradiation dose was 5 Mrad. A second sheet was subjected to a corona discharge using a corona discharge device under such conditions that the front and rear surfaces of the sheet were charged at a treating power of 1.34 kw/m²/min, respectively. A third sheet was not subjected to a special treatment. Each of these three sheets was interposed between two glass plates and heated at 160°C for 20 minutes in the same manner as described in Example 1 to obtain a transparent sandwich glass. The impact test was made with respect to the resulting sandwich glass in the same manner as described in Example 18 to obtain results as shown in the following Table 13. First sheet Second sheet Third sheet Dropping of steel ball from height of 1.5 m no penetration no penetration no penetration Amount of glass pieces scattered very few very few much Haze value (%) 0.2 0.1 0.1 As apparent from Table 13, the amount of glass pieces scattered is considerably reduced in the first and second sheets, which results in a considerable improvement of the adhesion between the sheet and the glass plates.

Claims: A sandwich glass to be used in windscreens for automobiles or in windows for buildings, consisting of glass plates and an intermediate layer interposed therebetween, characterized in that the said intermediate layer is formed by crosslinking a resin composition comprising a non-hydrolysed ethylene-vinyl acetate copolymer having a vinyl acetate content of 19 - 40% by weight and an organic peroxide and an acryloyloxy or methacryloyloxy group-containing compound or an ally] or vinyl-group containing compound as a curing assistant under heating of the said resin composition above the melting point of the copolymer; in that the said organic peroxide is utilized in an amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer; and in that the said resin composition contains not more than 50% by weight of the said curing assistant; wherein the said resin composition is thoroughly kneaded to uniformly disperse the organic peroxide into the ethylene-vinyl acetate copolymer, and then shaped into a sheet. A sandwich glass as claimed in claim 1, characterized in that said organic peroxide is at least one substance selected from 2,5 - dimethylhexane - 2,5 - dihydroperoxide, 2,5 - dimethyl - 2,5 - di(t - butylperoxy)hexane - 3, di-t-butyl peroxide, t-butylcumyl peroxide, 2,5 - dimethyl - 2,5 - di(t - butylperoxy)hexane, dicumyl peroxide, α,α' - bis(t - butylperoxyisopropyl)benzene, n - butyl - 4,4 - bis(t - butylperoxy)valerate, 2,2 - bis(t - butylperoxy)butane, 1,1 - bis(t - butylperoxy)cyclohexane, 1,1 - bis(t - butylperoxy)3,3,5 - trimethyl cyclohexane, t-butylperoxy benzoate and benzoyl peroxide. A sandwich glass to be used in windscreens for automobiles or in windows for buildings, consisting of glass plates and an intermediate layer interposed therebetween, characterized in that the said intermediate layer is formed by photocrosslinking a resin composition comprising a non-hydrolysed ethylene-vinyl acetate copolymer having a vinyl acetate content of 19 - 40% by weight and a photosensitizer and an acryloyloxy or methacryloyloxy group-containing compound or an allyl or vinyl-group containing compound as a curing assistant under light irradiation during for after heating of the said resin composition above the melting point of the copolymer; in that the said photosensitizer is utilized in amount of not more than 5 parts by weight based on 100 parts by weight of the ethylene-vinyl acetate copolymer; and in that the said resin composition contains not more than 50% by weight of the said curing assistant; wherein the said resin composition is thoroughly kneaded to uniformly disperse the photosensitizer into the ethylene-vinyl acetate copolymer, and then shaped into a sheet. A sandwich glass as claimed in claim 3, characterized in that the said photosensitizer is at least one substance selected from benzoin, benzophenone, benzoin methyl ether, benzoin ethyl ether, benzoin isopropyl ether, benzoin isobutyl ether, dibenzyl, 5-nitro acetonaphthene, hexachloro cyclopentadiene, p-nitrodiphenyl, p-nitroaniline, 2,4,6-trinitroaniline, 1,2-benzanthraquinone and 3 - methyl - 1,3 - diaza - 1,9 - benzanthrone. A sandwich glass as claimed in any of claims 1 to 4, characterized in that the said resin composition further contains 0.5-30 parts by weight of a plasticizer selected from high-purity paraffinic oil, naphthenic oil, phthalate ester, adipate ester, sebacate ester, thioglycol, dibenzyl ether, tricresyl phosphate, dioctyl maleate and epoxy plasticizers. A sandwich glass as claimed in any of claims 1 to 5, characterized in that the said resin composition contains not more than 5% by weight of a silane coupling agent. A sandwich glass as claimed in any of claims 1 to 6, characterized in that the said curing assistant is triallylisocyanurate.

Inventors: FUKUURA YUKIO, NAITO KAZUO, OHYACHI TOMIO, TAKEICHI HIDEO, TANUMA ITSUO, FUKUURA, YUKIO, NAITO, KAZUO, OHYACHI, TOMIO, TAKEICHI, HIDEO, TANUMA, ITSUO
Applicants: BRIDGESTONE TIRE CO LTD, BRIDGESTONE TIRE COMPANY LIMITED
Application year: 1982
Main classification: B32B17
IPC codes: C09J123, B32B17