PROCESS FOR CONVERTING DIALKYL SULFIDES TO ALKYL MERCAPTANS

Abstract: A continuous process is provided for the vapor-phase preparation of C₁-C₁₈ alkyl mercaptans where a di C₁-C₁₈ alkyl sulfide is reacted with a molar excess of hydrogen sulfide at elevated temperature in the presence of a specified synthetic zeolite containing at least 10 percent by weight of an alkali metal, expressed as Na₂O.

Description: BACKGROUND OF THE INVENTION Introduction This invention relates to a continuous vapor-phase process for the manufacture of alkyl mercaptans by reacting a dialkyl sulfide with hydrogen sulfide in the presence of a zeolite catalyst. Alkyl mercaptans are produced commercially either by reacting an alkyl alcohol with hydrogen sulfide or by the addition of hydrogen sulfide to an alkene. In either case, the major by-product is the corresponding dialkyl sulfide, formed by the equilibrium reaction, EMI1.1 There are commercial applications for certain alkyl sulfides, but in most cases the dialkyl sulfides obtained as by-products in mercaptan-manufacturing processes are contaminated with a number of by-product impurities that make them difficult and uneconomical to purify, and they must, therefore, be disposed of as chemical waste. One possible method to reduce the volume of the by-product sulfide waste and to recover economic value from it, is to react it with hydrogen sulfide, thereby reconverting the major dialkyl sulfide component of the waste to alkyl mercaptan according to the reverse of the above equilibrium reaction. Several procedures for cracking symmetrical dialkyl sulfides with hydrogen sulfide to form the corresponding alkyl mercaptan are described in the prior art. Beach, et al. (U.S. Pat. No. 2,667,515) provides a process for converting dimethyl sulfide and hydrogen sulfide to methyl mercaptan over a catalyst consisting of 10% cadmium sulfide on alumina at about 4000C. Single-pass molar conversions to methyl mercaptan of about 59% are obtained. A Japanese patent (No. 77/046203) discloses a similar process using a tungsten trisulfide on alumina catalyst at 320:4500C. Kubicek (U.S. Pat. No. 4,005,149) discloses the use of carbon disulfide as a reaction promoter, in the presence of a sulfactive catalyst, such as cobalt molybdate on alumina, to enhance conversions to alkyl mercaptan at lower reaction temperatures. Molar ratios of dialkyl sulfide/carbon disulfide ranging from about O.1/1 to about 50/1 are employed and the process is shown in the examples of the patent to be operable for dialkyl sulfides ranging from dimethyl sulfide to di-n-dodecyl sulfide (dialkyl sulfides up to C40 are claimed). Catalyst temperatures in the range of about 400 OF (2040C) to about 6000F (3160C) can be used. In U.S. patent No. 4,059,636, Kubicek further discloses the use of a supported phosphotungstic acid catalyst, a preferred embodiment being that carbon sulfide is also present in the reaction mixture to enhance the conversion of dialkyl sulfide to alkyl mercaptan at lower temperatures. Definitions The catalyst of this invention belongs to the family of zeolites which are synthetic aluminosilicates of well-defined chemical composition and physical structure. The zeolite (or molecular sieve) catalysts are synthetic aluminosilicates characterized by high uniformity, well-defined pore size, large surface area, complete crystallinity and excellent reproductibility. Their structures are described in the Union Carbide booklet F-08 entitled, "Linde Molecular Sieve Catalysts," and D. W. Breck's textbook, "Zeolite Molecular Sieves', John Wiley & Sons (1974). The basic structural units of synthetic zeolites are Si and Al atoms tetrahedrally coordinated with four oxygen atoms. The oxygen atoms are mutually shared between tetrahedral units contributing one of the two valence charges of each oxygen atom to each tetrahedron. Since aluminum atoms are trivalent, each Alto4 is negatively charged. The charge on these units is balanced by alkali metal cations e.g., Na+ or K+, in the as-synthesized zeolites. These cations may be partially exchanged with other metal cations. Although many factors influence the catalytic activity of these zeolites, the three most important are: 1) the open framework structure with its attendant pore size, 2) the SiO2: A1203 ratio of the framework, and 3) the cations. As in most commercial catalytic conversion processes, however, only the large-pore zeolites having pore openings in the range of 7 to 10 Angstroms (A) are useful. The two most preferred are Type X and Type Y zeolites. The Type L, more siliceous than Type X and Type Y, also has a pore size in this range. Type X, Y, and L are distinct, commercially available compositions, well known to those skilled in the art of zeolite chemistry. Type X has a chemical composition expressed in terms of oxide ratios of Na2OA1203:2-3 :2-3 SiO2 with a typical unit cell composition in the hydrated state of: Na86!(Al02)86 (SiO2)106] 264 1120. Type Y, on the other hand, has a composition of Na20:A1203: > 3-6 SiO2. When the SiO2:A1203 molar ratio is 4.8, the hydrated unit cell composition is Na56 [(A102)56 (SiO2)136] 264 1120. Both of these zeolites crystallize in the cubic system. An important building block of these zeolites is the sodalite cage, a truncated octahedron unit consisting of 24 (Si,A104) units. In Type X and Type Y the sodalite cages are connected through 4 of the 8 hexagonal faces in a tetrahedral arrangement. The pores thus created are defined by a 12-member ring of oxygen atoms, approximately 7-9 A size, opening into a central cavity of about 11 A in diameter. Type L zeolite is composed of cancrinite-type cages linked by double six-ring oxygen bridges producing a structure characterized by planar 12-ring pores having an opening of about 7.1 Type L has a typical oxide formula of Na20: Al2 O3: 6Si02 5H2O with a typical unit cell composition in the hydrated state of Na9[(AlO2)9(SiO2)27] 221120. The preferred synthetic zeolites are Types X and Y because of their larger pore sizes. The ability of the Y type to withstand higher temperatures without losing its crystalline structure makes it the most preferred zeolite catalyst for this invention. The zeolites, as prepared, generally contain as the cation about 13 percent by weight sodium (as Na2O) or equivalent amount of other alkali metal. STATEMENT OF THE INVENTION This invention is a continuous, vapor-phase process for preparing high purity C1-C18 alkyl mercaptan, R-S-H, comprising reacting dialkyl sulfide, R-S-R, where R is C1 to Cl8 alkyl or C6 to C18 cycloalkyl, with a molar excess of hydrogen sulfide at elevated temperature in the presence of a Type X, Type Y or Type L zeolite containing at least 10% by weight of an alkali metal, expressed as Na20. The following working example demonstrates this invention. Example Crude diethyl sulfide (DES)obtained from a mercaptan plant distillation column-bottoms material (90% DES) and hydrogen sulfide (H2S) were mixed and vaporized at a feed ratio of 10 moles of H2S per mole of DES in a preheater maintained at 260-2950C. The vaporized mixture at a specified mole velocity of DES was passed continuously through the preheater at atmospheric pressure and through a reactor containing a heated catalyst bed consisting of 1/8- inch extrudate of a Type Y zeolite catalyst containing 13% by weight sodium (as Na2O). The catalyst is a commercial material purchased from Union Carbide as Linde LZ-Y52. The reactor exit stream was analyzed by gas chromatography to determine the single-pass conversions of the crude DES to ethyl mercaptan. The reaction conditions and results are summerized in the following table. Table Catalyst Run No. Mole Velocity* Bed Temp. C. % Conversions 1 44 291 15.5 2 41 277 13.7 *Gram-moles of DES per kilogram of catalyst per 24 hours. DISCUSSION-GENERIC The invention described herein is a continuous, vapor-phase process for preparing high-purity C1 to C18 alkyl mercaptan by reacting a dialkyl sulfide with a molar excess of hydrogen sulfide at elevated temperatures in the presence of a Type X, Type Y or Type L zeolite containing at least 10% by weight of an alkali metal, expressed as Na Reactants The dialkyl sulfide used herein may be from any source but is preferably a crude by-product from an alkyl mercaptan, especially methyl or ethyl mercaptan, manufacturing process. The dialkyl sulfide is represented by R-S-R where R is a C1-C18 alkyl, preferably a C1-Cl2 alkyl group or a C6¯18 cycloalkyl group. The hydrogen sulfide reactant is obtained from any source and is used in excess of the stoichiometric quantity required to form the mercaptan with a dialkyl sulfide. A molar excess of hydrogen sulfide over the dialkyl sulfide is required for high conversions to alkyl mercaptan. The molar ratio of hydrogen sulfide to dialkyl sulfide preferably ranges from about 3/1 to 20/1, most preferably from 5/1 to 15/1. Reaction Conditions Elevated temperatures in the range of from about 250 up to about 4000C are used herein. The dialkyl sulfide reactant is preferably first vaporized by passage through a preheater. The reactants can be mixed in the preheater at the desired molar ratio and passed into the reactor containing the catalyst. The preheater temperature will generally be within the same temperature range as the catalyst bed i.e., about 250 to about 4000C, preferably from about 290 to 3900C although lower preheat temperatures are useful. The pressure in the reactor will range from atmospheric to about 600 psig, perferably between about 50 and 350 psig. The rate at which the dialkyl sulfide is passed over the zeolite catalyst ranges from about 10 to about 300 gram-moles, preferably about 30 to about 150 gram-moles of dialkyl sulfide per kilogram of catalyst per 24 hours. In commercial operation, a rate of about 50-150 pound-moles of dialkyl sulfide per one-thousand pounds of catalyst per 24 hour day. is used. In preferred operation, the crude product from the reactor is passed into a series of at least two continuous distillation towers where the excess unreacted hydrogen sulfide is separated in one tower and recycled to the reactor. High-purity alkyl mercaptan is separated as an overhead product in another tower and, optionally, any unconverted dialkyl sulfide is collected as a tower bottoms product and recycled to the preheator leading to the reactor. It is an advantage of the zeolite catalyst that it is active in this process at relatively low temperatures and with short contact times obviating the need for a reaction promoter such as carbon disulfide.

Claims: Claims 1. A continuous, vapor-phase process for preparing high- purity C1-C18 alkyl mercaptan, R-S-H, comprising reacting dialkyl sulfide, R-S-R, where R is C1 to C18 alkyl or C6 to r 8 cycloalkyl, with a molar excess of hydrogen sulfide at elevated temperature in the presence of a Type X, Type Y or Type L zeolite containing at least 10% by weight of alkali metal expressed as Na20. 2. The process of claim 1 wherein R is C1 to C12 alkyl and the alkali metal is sodium or potassium. 3. The process of claim 1 wherein R-S-R is a crude by-product from an alkyl mercaptan manufacturing process. 4. The process of claim 2 wherein the dialkyl sulfide and hydrogen sulfide are first preheated to a temperature within the range of about 250 to about 4000C. 5. The process of claim 4 wherein the pressure in the reactor ranges from atmospheric to 600 psig. 6. The process of claim 5 wherein the molar ratio of hydrogen sulfide to dialkyl sulfide ranges from 3:1 to 20:1. 7. The process of claim 6 wherein the rate at which the dialkyl sulfide is passed over the catalyst bed ranges from 10 to 300 gram-moles of dialkyl sulfide per kilogram of catalyst per 24 hours. 8. The process of claim 7 wherein the catalyst bed temperature ranges from about 290 to about 3900C and the pressure in the reactor ranges from about 50 to about 350 psig. 9. The process of claim 7 wherein the unconverted dialkyl sulfide is continuously separated and recycled to the reactor to form additional alkyl mercaptan.

Inventors: HAGER, ROBERT BONNER
Applicants: PENNWALT CORPORATION
Application year: 1982
Main classification: C07C148
IPC codes: C07C321, C07C67, C07C319, C07C313, C07B61, B01J29