CATION EXCHANGE MEMBRANE WITH HIGH EQUIVALENT WEIGHT COMPONENT

Abstract: Composite fluorocarbon cation exchange membrane having at least two layers of fluorinated polymer containing pendant side chains with sulfonyl groups wherein the equivalent weight of one such layer differs from the adjacent layer by at least 100.

Description: TITLE Cation Exchange Membrane With High Equivalent Weight Component CROSS-REFERENCE TO RELATED APPLICATION This is a continuation-in-part of copending application serial number 225,652, filed January 16, 1981. BACKGROUND OF THE INVENTION Fluorinated polymers containing pendant side chains are often used to prepare ion exchange membranes. Such membranes have outstanding properties as barrier membranes to separate the anode and cathode compartments of electrolytic cells used for the production of chlorine and caustic. Fluorinated polymers containing carboxyl side chains provide excellent current efficiency in such electrolytic cells, but result in high operating voltages. By contrast, fluorinated polymers containing sulfonyl groups in the side chains permit operation at low voltages, but result in poor current efficiency in the electrolytic cell. It has previously been recognized that combinations of polymers having sulfonyl and carboxyl groups are desirable to provide an optimum balance of performance characteristics in an electrolytic cell using membranes prepared from such polymers. Under normal cell operation, the water permeation characteristics of the layers are sufficiently close that the layers remain in intimate contact with each other. However, abnormal cell conditions, such as loss of electrical power, failure of water feed to the cathode chamber and particularly interruption or loss of brine feed to the cell, can produce a large difference in water transport. For example, if the anolyte is depleted below 50 g/1 NaCl, a large 0\ϊH quantity of water will be transported through the fluorinated polymer having the sulfonyl side chains. However, the water is substantially less able to permeate a polymer having carboxyl-containing side chains. Thus, during an upset of cell operation, a composite of two such polymers may experience a buildup of water at the interface, resulting in- delamination of the composite. SUMMARY OF THE INVENTION The instant invention provides composite cation exchange membrane exhibiting improved resistance to delamination in an -electrolytic cell and a process for the production of such composite membranes. Specifically, the instant invention provides a multilayer cation exchange membrane consisting essentially of layers of a) fluorinated polymer with pendant side chains containing carboxyl groups, b) fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight of about from 1100 to 1600 and at least about 200 units higher than layer (a), and c) a fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight that is about from 1000 to 1500 and at least about 100 units lower than layer (b), the layers being bonded together in the order specified. Preferably, the cation exchange membrane further comprises a reinforcing fabric embedded in the lower equivalent weight fluoropolymer containing sulfonic functional groups. OMPI Y/IPO DETAILED DESCRIPTION OF THE INVENTION The polymers used in the instant invention are of the types generally used previously in the preparation of films for use in electrochemical cells, and especially chloral ali cells. These include fluorinated polymers with pendant side chains containing sulfonyl groups or carboxyl groups. These sulfonyl or carboxyl functional groups are generally present in such a form as to render the polymer melt-fabricable. The elt-fabricable polymer having sulfonyl functional groups has a fluorinated hydrocarbon backbone chain to which are attached functional groups or pendant side chains bearing the functional groups. The pendant side chains can contain, for example, CFCF 2 S0 2 F groups wherein R f is F, Cl, or a C, to C. Q perfluoralkyl radical. Fluorinated polymers of this type and their preparation are described in detail in United States Patents 3,282,875, 3,560,568, 3,718,627, and 3,041,317, all of which are hereby incorporated by reference. For chlor-al ali cells, perfluorinated polymers are preferred. The melt-fabricable polymer having carboxylic functional groups has a fluorinated hydrocarbon backbone chain to which are attached the functional groups or pendant side chains which in turn carry the functional groups. The pendant side chains can contain, for example, roups wher ( einr W Z i ) s.F or CF„, t is 1 to 12, and W is -COOR or -CN, wherein R is lower alkyl. Preferably, t is 1 to 3. Preferably, the functional group in the side chains of the polymer will be present i groups. polymers containing carboxylic functional groups and their preparation are disclosed in British Patent 1,145,445 and United States Patents 3,506,635 and 4,116,888, all hereby incorporated by reference. Preferred monomers for use in the preparation of such polymers are found in United States Patents 4,131,470 and 3,852,326, also hereby incorporated by reference. For chlor-alkali cells, perfluorinated polymers of this type are preferred. In general, the polymers having carboxylic functional groups exhibit an equivalent weight of about from 500 to 1500, and preferably from about 900 to 1200. The polymers having sulfonyl groups exhibit an equivalent weight of about from 1100 to 1600. The lower equivalent weight polymer having sulfonyl groups should be at least about 100 units lower than the adjacent polymer, and accordingly has an equivalent weight of about from 1000 to 1500. In addition, the higher molecular weight polymer having sulfonyl groups should have an equivalent weight at least about 200 units higher than the polymer having carboxylic functional groups. This difference in equivalent weights permits the operation of an electrolytic cell at lower brine concentration than would otherwise be possible. The particular method of preparing the laminates of the instant invention is not critical, so long as the basic arrangement of carboxylic polymer, high equivalent weight sulfonic polymer and low equivalent weight sulfonic polymer is maintained. Accordingly, the component layers can be preformed into film and subsequently laminated. Laminating techniques which can be used for this process are disclosed in detail in South African Patent No. 78/2225, hereby incorporated by reference. Another apparatus which can be used is the horizontal laminator shown in U.S. Patent 3,770,567, also hereby incorporated by reference. An alternative method of preparing the present laminar structures is by coextruding the polymers above the melting point of each polymer. A wide variety of mechanical variations can be used, including commercially available coextrusion equipment such as that manufactured by Johnson Plastics Machinery Company of Chippewa Falls, Wisconsin. For example, the laminates can be prepared using multiple extruders feeding into separate zones of a common chamber, following which the layered stream is fed to a single die. Another embodiment of the present invention involves the use of a single die known in the film processing industry as a "coat hanger" die. In the use of such a die, multiple extruders feed separate streams into the specialized die. The die expands the width of the streams and joins the streams before they leave a single exit orifice of the die. Within the requirement that the polymers be above the melting point, the particular processing temperature will depend on known operational requirements for extrusion of films. The temperature will be adjusted to obtain continuous smooth films of uniform caliper without die drip or other defects. Using the sulfonyl-containing and carboxyl-containing polymers of the present invention , an extrusion temperature range of about from 260° to 330 °C is preferred . A reinforcing layer can also be added to the composi te ' str ucture if desi red . A wide variety of suppor t materials can be used , including woven fabric or nonwoven material. In the case of woven fabric , weaves such as ordinary basket weave and leno weave can be used. The reinf orcement threads can be either monofilament or multistranded . Particularly preferred reinforcement materials are perhalocarbon polymer threads . As used he rein , the term "perhalocarbon polymer" means a polymer which has a carbon chain optionally containing ether linkages and which is totally substituted by fluorine or by fluorine and chlorine atoms . Particularly prefer red because of its inert character is a per fluorocarbon polymer. Typical of such polymers are those made from tetrafluoroethylene a-nd copolymers of tetraf luoroethylene with hexafluoropropylene and/ or perfluoro (alkyl vinyl ethers) wherein alkyl is from 1 to 10 carbon atoms . A preferred ether of this type is perfluoro (propyl vinyl ether) . The reinforcing material can be conveniently applied to the outer sulfonyl-containing polymer in conj unction with another sulfonyl-containing polymer of the same equivalent weight. These two sulfonyl-containing polymers can then be laminated , with the reinf orcing materi al embedded in the composite layer of lower equivalent weight , sulfonyl-containing polymer . After preparation of the laminates , they are cooled to a temperature below the melting point of each polymer and treated according to known techniques to convert the functional groups to forms more suitable for use in electrolytic cell applications. Such conversion also renders the polymers substantially less melt-fabricable. The composite membranes of the present invention exhibit excellent performance as a membrane in an electrochemical cell, especially an electrolytic cell used for the production of chlorine and caustic. The membranes, at the same time, exhibit improved resistance to delamination in use, even under conditions of low anolyte sodium chloride concentration. When the sodium chloride concentration in the anolyte is sufficiently low and other cell conditions are such as to promote delamination, the frequency of delamination and the area of delamination of the present membranes is less than that experienced with membranes composed of a carboxyl film and a sulfonyl film of only one equivalent weight. The instant invention is further illustrated by the following specific examples. EXAMPLE 1 Fluoropolymers having carboxyl and sulfonyl groups were prepared according to the procedures of U.S. Patent Numbers 4,131,740 and 3,282,875, respectively. Films were prepared from the polymers to give a two-mil film of carboxylic ester copolymer having an equivalent weight of 1,080, a 1.4 mil sulfonyl fluoride copolymer having an equivalent weight of 1,350, and a 2 mil film of a sulfonyl fluoride copolymer having an equivalent weight of 1,100. The carboxylic film, the high equivalent weight sulfonyl film and the low equivalent weight sulfonyl film were pressed together to exclude air between layers and then laminated with a reinforcing cloth and another 2 mil film of the low equivalent weight sulfonyl copolymer. The reinforcing cloth consisted of 200-denier extruded onofilament of a " copolymer of 96 weight percent tetrafluoroethylene and 4 weight percent perfluoro(propyl vinyl ether) prepared in accordance with Comparison C of U.S. Patent No. 4,029,868. The thread had a circular cross-section with a diameter of 127 microns (5 mils) and an aspect ratio of 1. The cloth was a leno weave with a warp thread count of 13.8 threads per centimeter and a weft thread count of 6.7 threads per centimer. The cloth was hot calendered so that the total thickness of the cloth was 239 microns (9.4 mils). The threads were slightly flattened at the cross-over points with the thread aspect ratio increased from 1 to 1.13. The four films and reinforcing cloth were continuously laminated on a horizontal laminator at a temperature which varied from 230° to 240 β C and using a turning drum. The final composite had a size of one square foot. A piece of this composite was hydrolyzed for 1 hour at 80 β C in a standard hydrolysis bath. The bath was composed of potassium hydroxide, dimethylsulfoxide and water in a ratio of 12%, 30% and 50% by weight, respectively. It was washed in water and mounted in a 4-inch diameter NaCl electrolysis cell. Performance was as follows: O ?I ^> *•m-. YYϊvIIPPOO - Days PC on Volt- (KWH/ Line NaOH/% NaCl/% Cl /PPM*CE/% age MT) 2 30.5 18.0 31 91.5 3.80 2775 3 31.4 96.4 3.82 2645 4 31.8 18.9 96.3 3.83 2656 8 31.8 - 18.2 96.1 3.80 2640 9 29.7 13.1 262 95.3 3.73 2614 10 27.4 90.4 3.71 2741 11 28.3 11.8 63 91.1 3.71 2721 15 30.0 11.1 91.8 3.77 2742 16 31.6 41 93.3 3.80 2720 17 31.5 93.0 3.81 2738 18 31.7 11.5 93.0 3.83 2751 * In NaOH corrected to 50% At a brine concentration as low as 11.1%, only slight drop in performance was observed. The chloride content in the caustic was low at these low .brine concentrations. The membrane blistered after approximately 20 days on line due to a feed brine stoppage since the anolyte NaCl concentration was already low. EXAMPLE 2 The general procedure of Example 1 was repeated. Performance and conditions after 60 days 2 on line at 31 amps/dm were as follows: 33% NaOH 18.2 % NaCl in anolyte 80 °C 94. 9% Current Efficiency 3 . 87 Volts 2725 KWH/MT NaOH E.XAMPLE 3 The general procedure of Example 1 was repeated, except that the films and the reinforcing fabric were laminated on a horizontal lamina tor at a temperature of from 240° to 250°C. The membrane, after hydrolysis, was tested as in Example 1. Cell performance after 22 days on 2 line at 3.1 KA/m was as follows: 30.5% NaOH 17.2% NaCl in anolyte 79.0°C 95.54% current efficiency 3.95. olts 2761 KKH/MT OMP

Claims: WE CLAIM: 1. A multilayer cation exchange membrane cons isting essentially of layers of a) fluorinated polymer with pendant side chains containing carboxyl groups , b) f luorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight of about from 1100 to 1600 and at least about 200 uni ts higher than layer (a ) , and c) f luor inated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight that is about from 1000 to 1500 and at least about 100 units lower than layer (b) , the layers being bonded together in the order specifi ed . 2. A laminar structure of claim 1 wherein the higher equivalent weight fluorinated polymer has an equivalent weight at least about 200 units higher than the lower equivalent weight polymer . 3. A laminar structure of claim 1 wherein each fluorinated polymer is perfluorinated . 4. A laminar structure of claim 1 wherein the carboxylic fluoropolymer is a copolymer of tetraf luoroethylene and methylperf luoro (4 , 7-dioxa- 5-methyl-8-nonenoate) . 5. A laminar structure of claim 1 wherein the sulfonic fluorinated polymer is a copolymer of tetraf luoroethylene and perf luoro (3 , 6-dioxa-4-methyl- 7-octene sulfonyl fluoride) . 6. A laminar structure of claim 1 fur ther compr ising a reinf orcing fabric embedded in the lower equivalent weight fluoropolymer containing sulfonic functional groups . 7. A laminar structure of claim 6 wherein the reinforcing fabric is a woven cloth of a copolymer of tetrafluoroethylene and perfluoro(propyl vinyl ether) . 8. A laminar structure of claim 6 wherein the reinforcing fabric is a perfluorinated polymer. 9. In a process for the continuous production of alkali metal hydroxide which comprises continuously providing an aqueous alkali metal halide solution to the anode compartment of an electrolytic cell having an anode, a cathode, and a cation exchange membrane separating the anode and the cathode ? electrolyzing the solution; and continuously removing alkali metal hydroxide solution, hydrogen, and halogen from the electrolytic cell, the improvement wherein the cation exchange membrane consists essentially of layers of a) fluorinated polymer with pendant side chains containing carboxyl groups, b) fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight of about from 1100 to 1600 and at least about 200 units higher than layer (a), and c) fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight that is about from 1000 to 1500 and at least about 100 units lower than layer (b) , the layers being bonded together in the order specified. 10. A process of claim 9 wherein the cation exchange membrane further comprises a reinforcing fabric embedded in the lower equivalent weight fluoropolymer containing sulfonic functional groups. 11. In an electrolytic cell having an anode, a cathode, and a cation exchange membrane separating the anode and the cathode, the improvement wherein the cation exchange membrane consists essentially of layers of a) fluorinated polymer with pendant side chains containing carboxyl groups, b) fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight of about from 1100 to 1600 and at least about 200 units higher than layer (a) , and c) fluorinated polymer having pendant side chains containing sulfonyl groups and having an equivalent weight that is about from 1000 to 1500 and at least about 100 units lower than layer (b) , the layers being bonded together in the order specified. 12. An electrolytic cell of claim 11 wherein the cation exchange membrane further comprises a reinforcing fabric embedded in the lower equivalent weight fluoropolymer containing sulfonic functional groups.

Inventors: SILVA RAIMUND HEINRICH, SMITH ROGER ALTON, SILVA, RAIMUND, HEINRICH, SMITH, ROGER, ALTON
Applicants: DU PONT, E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1982
Main classification: B32B7
IPC codes: B01J47, B32B27, C08J5, C25B13