A METHOD AND AN ARRANGEMENT FOR THE HEAT-SEALING OF PACKING LAMINATE

Abstract: In the manufacture of non-returnable packages for milk and other beverages the laminated packing material is sealed to itself along linear sealing zones by causing outer thermoplastic layers of the packing material to fuse togeth­ er. The strength of the seal obtained depends upon the thermoplastic surface being free of impurities, e.g. oxide coatings or residues of the contents of the package. In spite of the presence of impurities a strong seal can be obtained if the thermoplastic layers, within a limited region of the sealing zone, are pressed against each other with such a force that molten thermoplastic material is made to flow to adjoining regions (15), since in this case the thermoplastics are blended to such a degree that the seal-preventing layer of impurities is broken.

Description: A METHOD A#I) AN ARESSGEMENT FOR TES 7zA-SEALING OF PACING LAMINATE The present invention relates to a method for the heat-sealing of packing laminate,comprising an outer thermoplastic material layer,which consists in making the thermoplastic layers within a sealing-zonelie against one another and heating them temporarily to sealing temperature. The invention also relates to an arr#angement for the heat-sealing of packing laminate1 coniprising an elongated sealing jaw with a working surface which can be pressed against the laminate. Packing containers of the non-returnable type are used for milk, fruit beverages etc. and are generally manufactured from laminated packing material. The packing material comprises a central, relatively stiff carrier layer of paper which is covered on either side by thin layers of homogeneous plastic material. The material may also comprise layers of aluminium foil or other material. It is a common feature of all packing laminates of this type that they comprise on the outside, at least on the side which is to face towards the packed contents, a layer of thermoplastic material, usually polyethylene, which makes it possible for two portions of the laminate resting against each other to be sealed together in a liquid-tight manner with the help of heat and pressure. For the seal to obtain the desired strength and liquid-tightness it is necessary that the two thermoplastic layers which are sealed to one another should be clean and free of impurities. If this is the case a complete fusing together of the thermoplastic layers can take place, which results in an optimum seal from a point of view of strength as well as tightness. Since on the surface of the thermoplastic layers usually a thin oxide coating is present, which is formed in connection with the extrusion of the thermoplastic layeaon the packing laminate, a complete fusing together of the thermoplastic layers is often prevented, so that the seal does not acquire the strength and tightness which theoretically is possible. Other types of impurities may also occur on the surface of the thermoplastic layer, e.g. residues of the contents, which further impair the seal. This is a particular problem in the type of package manufacture where the sealing of the laminate material takes place whilst the contents are present, that is to say where the contents in the first place have to be forced out from the space between the thermoplastic surfaces resting against one another before the sealing can take place. However, in practice the contents are not fully squeezed out, but small residues will remain embedded in the sealing area,and this will weaken the seal. It is an object of the present invention to provide a method which will make it possible to heat-seal a packing laminate of the aforementioned type in such a manner that all the difficulties mentioned above are avoided and the seal obtained has optimum properties, It is a further object of the present invention to provide a method for the heat-sealing of a packing laminate which will make possible an optimum seal, even if the packing laminate is covered with impuritiess e.g. oxides, residues of the contents of the package or dirt. These and other objects have been achieved in accordance with the invention in that a method for the heat-sealing of the packing laminate, comprising an outer thermoplastic material layer, which consists in making the plastic layers within a sealing zone lie against one another and heating them temporarily to sealing temperature, has been given the characteristic that the thermoplastic layers within a limited region of the sealing zone are pressed against each other with so great a force that molten thermoplastic material is caused to flow from the said region to adjoining parts of the sealing zone. By this method the molten thermoplastic material, whilst being forced from the linear region to adjoining parts of the sealing zone, will entrain with it possible impurities whilst the two thermoplastic layers of the laminate placed against one another are effectively blended to such a degree that a complete fusing together is achieved. Within the linear region only a very thin thermoplastic layer remains, which is free of impurities, and is in close contact with the carrier layer of the packing laminate, whilst in the adjoining regions of the sealing zone an accumulation of well-blended thermoplastics from both thermoplastic layers guarantees a seal of good strength and tightness. Preferred embodiments of the method in accordance with the invention have been given ,moreover, the characteristics which are evident from subsidiary claims 2 and 3. It is a further object of the present invention to provide an arrangement for the heat-sealing of packing laminate of the abovementioned type. The arrangement shall ensure that a seal of optimum properties is obtained, even if the material which is to be sealed is not wholly free of impurities. It is a further object of the present invention to provide an arrangement for the heat-sealing of packing laminate,which is not subject to the disadvantages of arrangements known earlier and is simple and reliable in its design. The arrangement should be capable, moreover, to be used in known types of packing machines and to be manufactured at low cost. These and other objects have been achieved in accordance with the invention in that an arrangement for the heat-sealing of packing laminate# comprising an elongated sealing jaw with a working surface which can be pressed against the laminate# has been given the characteristic that ¯ the working surface has a substantially linear ridge. Py providing the sealing jaw with the said ridgelor elongated raised surface, a jaw is obtained which when pressed against two combined packing laminates brings about a sealing zone with a linear portion wherein the ia#iinates are pressed against one another with a very high pressure. Since the sealing jaw comprises a region heating the laminate1 which includes not only the linear ridgebut also an adjoining region, the heated thers#plastics will be forced at high speed from the linear region to the adjoining region so that an effective blending and consequently a good seal is obtained in the manner described earlier. Preferred embodiments of the arrangement in accordance with the invention have been given, moreover, the characteristics which are evident from subsidiary claims 6 to 9 inclusive. A preferred embodiment of the method as well as of the arrangement in accordance with the invention will now be described in more detail with special reference to the enclosed schematic drawing which only shows the components required for an understanding of the invention Pig. 1 shows in enlargement a cross-section through a packing laminate of z type which can be heat-sealed with the help of the method and the arrangement in accordance with the invention. Fig,2 shows in enlargement a cross-section through a sealing jaw in accordance with the invention. Fig.3 is a section through two packing laminates in accordance with fig.l which are heat-sealed with the help of the method and the arrangement in accordance with the invention. The packing laminate shown in fig. 1 is of a type used frequently for the packaging of milk and other beverages. The packing laminate has an overall thickness of 0.4 - 0.5 mm and comprises a central carrier layer 1 of fibrous material, this layer 1 being covered on either side by comparatively thin, homogeneous layers 2,3 of thermoplastic material, in particular polyethylene. Between one outer plastic layer 3 and the carrier layer 1 a further layer 4 of aluminium foil is often present, this layer being joined to the carrier layer by means of thermoplastics (not shown) and completely covered by the outer, homogeneous layer 3. Thanks to the two outer thermoplastic layers 2,3 the packing laminate can be simply heatsealed by pressing together the parts which are to be sealed to one another with simiiltaneous heating of the thermoplastics to its melting temperature. It is of course also possible to seal packing laminates of other types with the help of the method and the arrangement in accordance with the invention, but it is a prerequisite that the packing laminates must have them a layer of thermoplastic material. Fig.2 shows in section a cross-section through a sealing jaw 5 in the arrangement according to the invention. The sealing jaw 5 comprises a main body 6 which is made of an electrically non-conducting material and which is provided in one lateral surface with a groove into which a bar 7 of an electrically conducting material, preferably copper, is inserted. The bar 7}which is located centrally in the one lateral surface of the main body, forms together with the surrounding parts of the main body 6 the working surface 8 of the sealing jaw 5. The working surface 8 is provided with a linear ridge 9 formed in the bar 7. The ridge 9 is of substantially rectangular crosss-section and of a height which extends to 0.2 to 0.8 times the thickness of the laminate, but preferably 0.5 times the thickness of the laminate and of a width which is substantially equal to the thickness of the packing laminate. The working surface 8 of the sealing jaw 5 thus comprises a centrally situated. legion heating the laminate which ircludes on the one hand the linear ridge 9, on the other hand at least one z: :4st-dng region at the side of the ridgeZhe region heating the laminate can be connected via the material in the bar 7 to a power source which may be of the high-frequency type, so as to make possible the hig#-frequency welding of laminate containing aluminium foil. The region heating the laminate or the bar 7 may also be heatable and consist, for example, of an electric resistance materialwhen packing laminate without aluminium foil or other electrically conducting layers is to be joined together. The sealing jaw in -accordance with the invention may be modified within the concept of the invention in different ways so as to meet requirements which the sealing of different materials and different types of packing containers may make, A typical modification of this kind may be that the sealing is provided with one or more ducts for a cooling medium, e.g. water, which prevents harmful rises in temperature or undesirable spreading of heat to the adjoining region which should remain unheated. It is also possible to design the sealing jaw in several mutually movable parts. The por+=io3s ow the sealing jaw situated on either side of the ridge c, for erampla, may be made movable in relation to the ridge 9 and be spring-loaded in direction towards the material so that a suitable contact pressure is automatically produced. The sealing jaw may also be doubled, that is to say it may comprise two main bodies of the type described arranged at a distance from each other. This embodiment is particularly suitable when a packing material tube is to be sealed off, that is to say sealed in two transverse zones and cut off between t#ese, since a knife or some other appropriate cutting device can then operate in the space between the two main bodies of the sealing jaw. Fig. 3 illustrates the sealing sequence in the sealing together of two packing laminates with the help of the method and the arrangement in accordance with the invention. Two packing laminates 10,11 (or two parts of the same, folded, packing laminate) have been joined together in pre paration of the sealing so that tne#ie against one another with their outer thermoplastic layers 3. The packing laminate is pressed together with the help of a sealing jaw 5 and a counter-jaw 12 resting against the opposite side of the packing laminate (indicated by means of dash-dotted lines). The sealing jaw 5 is of the type as shown in fig.2 whilst the counter-jaw 12 is provided with. a plane working surface resting against the laminate 11. The jaws 5,12 are suspended in the frame (not shown) of the packing machine in such a manner that they can be given a reciprocating movement by means of hydraulic or mechanical driving devices, so that during the sealing they can be pressed together with a certain, adjustable force. At the same time as the jaws are moved towards one another and start to press-together the packing laminate 10,11 situated in between, the bar 7 of the sealing jaw 5 is connected to a high-frequency power source. In this way an alternating field is induced in the aluminium layer 4 of the packing lsniiateq, so that these are heated within a region cor responding to the surface of the bar 7 to a temperature which is appreciably higher than the melting temperature of the adjacent thermoplastic layers. The heat generated is transmitted directly to the thermoplastic layers 3 located between the aluminium layers so that these melt and become fluid. Owing to the high force (approx. 100 kg/cm2 ) with which the packing laminate is pressed together on a level with the ridge 9, the molten thermoplastic will run or flow from the region 13 of high pressure to adjoining parts 14 of the total sealing zone 13,14. Since the thermoplastic layers 3 lying against one another in the region outside the sealing zone 13,14 continue to be in solid state and are pressed against one another, the molten thermoplastics cannot flow any further outside the sealing zone, but remains in the two regions indicated by reference numeral 14, where it forms bulges 15 running parallel with the elongated pressure region 13 wherein the two layers sealed to one another are blended. In the region 13 onzy insignificant amounts of plastic material remain which, because af unevenness of the surface etc., cannot be squeezed out, whilst the bulges 15 formed on either side of the region contain an excess of well-blended plastics providing a very strong and, in practice, unfreekable seal between the two layers. Since the flow from the region 13 to the regions 14 is so rapid, turbulence occurs in the flowing plastic material which ensures that the plastic material from the two layers resting against one another is well blended, so that any surface oxidation or other impurities present on the surface (e.g. from remaining resides of the contents of the packages) are effectively blended into the plastics, so that any coherent film of impurities impairing the strength of the seal will not survive. To ensure further that the bulges or accumulations 15 of molten thermoplastics are of a limited, linear appearance, the parts of the two plastic laminates situated outside the sealing zone 13,14 may be cooled. This can be achieved either by providing the two jaws 5212 with cooling ducts situated outside the sealing region through which liquid is conducted orin the type of sealing performed with simultaneous forming out of the contents, by allowing the contents to cool adjacent parts of the packing laminate. To ensure an effective flow of molten thermoplastic material from the central region 13 to the adjoining regions 14, the pressing of the ridge 9 against the packing laminate must take place with such a force that the surface pressure in the linear region 13 of the sealing zone amounts to approx. 100 kg/cn2 at the same time as the temperature of the thermoplastics should exceed approx. 1304C

Claims: CLAIMS 1. A method for the heat-sealing of packing lsminate#comprising an outer layer of thermoplastic material (2,3), which consists in making the thermoplastic layers within a sealing zone (13,14) lie against one another and heating them temporarily to sealing temperature c h a r a c t e r i z e d i n t h a t the thermoplastic layers within a limited linear region (13) of the sealing zone (13,14) are pressed against each other with so great a force that molten thermoplastic material is caused to flow from the said region (13) to adjoining parts(l4) of the sealing zone. 2. A method in accordance with claim l,c h a r a c t e r i z e d i n t h a t the flow of thermoplastic material in the outer parts of the sealing zone (13,14) is prevented by non-molten material, so that an accumulation (15) of pressed-out plastics is formed at the side of the linear region (13). 3. A method in accordance with claim 1 or 2, c h a r a c t e r i z e d i n t h a t the thermoplastic layer (3) is cooled on either side of the sealing zone (13,14). 4. An arrangement for the heat-sealing of packing laminate comprising an elongated sealing jaw (5) with a working surface (8) which can be pressed against the laminate h a r a c t e r i z e d i n t h a t the working surface (8) has a substantially linear ridge (9). 5. An arrangement in -^co-dance with claim 4, c h a r a c t e r i z e d i n t h a t the ridge (9) has a height of 0.2 - 0.8 times the thickness of the laminate0 6. An arrangement in accordance with claim 4 ot 5 c h a r a c t e r i z e d i. n t h a t the width of the ridge (9) is substantially equal to the thickness of the laminate. 7. An arrangement inaccordance with anyone of claims 4,5 or 6, c h a r a c t e r i z e d i n t h a t the working surface (8) comprises a region heating the laninate# which includes on the one hand the linear ridge (9) and on the other hand an adjoining region at the side of the ridge (9). a. An arrangement in accordance with anyone of claims 4 to 7 inclusive, c h a r a c t e r i z e d i n t h a t the region heating the laminate is constituted of an electrically conducting material which can be connected to a high-frequency power source. 9. An arrangement in accordance with claim 7 c h a r a c t e r i z e d i n t h a t the region heating the laminate is constituted of electric resistance material.

Inventors: CETRELLI, RENATO
Applicants: TETRA PAK INTERNATIONAL AB
Application year: 1982
Main classification: B29C65
IPC codes: B65B51, B29C65, B65B9, B29L9, B32B43, B29L22, B29L31