DRY GRINDING CEMENTED CARBIDE WORKPIECES WITH SILVER-COATED DIAMOND GRIT

Abstract: Disclosed is an improved method for dry grinding a workpiece comprising a non-ferrous metal carbide-­ containing alloy with a resin bonded grinding element having diamond particles embedded in the grinding surface thereof. Such improvement for increasing the grinding ratio and decreasing the power required to rotate the grinding element during grinding operations comprises coating the exterior surfaces of each said diamond particle with a layer of metal consisting essentially of silver prior to embedding the diamond particles in the grinding element.

Description: DRY GRINDING CEMENTED CARBIDE WORKPIECES WITH SILVER < OATED DLAMOND GRIT Cross-Referenee to Related Applicatlons This appllcation is crossreferenced to the commonly assigned application of John W. Grenier, entitled "Electroless Application of a Silver Coating to Diamond Particles", U.S.S.N. filed on even date herewith, the disclosure of which is expressly incorporated herein by reference. Background of the Invention The present invention relates to resin bonded grinding elements containing diamond grit and more particularly to the use of silver-coated diamond grit therein for dry grinding cemented carbide workpleces Use of metal coated diamond grit embedded in the abrasive section of resin bonded grinding wheels is a well practiced commercial technique for enhancing the grinding operation. Llndstrom (U.S. Patent No. 3,957,481) proposes such metal coated diamond for use in the grinding section of a resin bonded grinding element wherein the metal coating is taught to form a mechanically strong shell for holding together fractional portions of the diamond particles and for effectively increasing the adhesion between the diamond particles and the resin material. Coatings shown include cobalt, nickel, silver, cadmium, zinc, copper, iron, tin, molybdenum, titanium, manganese, aluminum, chromlum, gold, tungsten, zirconium, platinum group metals, and combinations and alloys thereof. Otopkov (British Patent No. 1,344,237) proposes to coat diamond or boron nitride abrasive grains with two materials, one of which is silicon and the other of which is a metal selected from copper, silver, gold, aluminum, cobalt, nickel, ruthenium, osmium, lridlum, platinum, and certain transition metals. German Auslegeschrift 2,218,932 apparently is an equivalent of Otopkov's British Patent. Seal (U.S. Patent No. 3,528,788) etches the metal coating on the diamond grit ior improving the grinding ratio of resin bonded grinding wheels containing the etched grit. Seoul (U.S. Patent No. 3,779,727) proposes to Incorporate fillers into the resinous material used to formulate resin bonded abrasive tools wherein the fillers include a solid lubricant and a metal which is silver, silver coated copper, or copper powder. The diamond grit Or cubic boron nitride (CBN) abrasive further may be coated with conventional metals. As noted by Sioux in "The Evolution of Tests for Diamond Wheel Performance in Dry Tool and Cutter Sharpening," Proceedings: Diamonds in the 80's, pp 131-138, Industrial Diamond Assosiation, Chicago, '11. (October 13-15, 1980), and in Uhe Use of Silver in Dlamond and CBN Wheels for Dry Grinding Hard Materials", CutW Tool Engineering, July/Augug; 1980, pp 8-11; the silver filler in the resin apparently acts as a thermal conductivity agent to remove heat from the grinding section and workpiece area contacted by the grinding section due to the high thermal conductivity of the conductive metals silver, copper, and silver-coated coppot, Lintom (U.S. Patent Na 3,955,324) proses agglomerates of metal-coated diamonds for embedding in the grinding section of recin bonded grinding elements wherein the matrix metal of the agglomerates is a metal wtiieh possesses good heat conducting ability. Such metals are shown to include nickel, copper, cobalt, and silver or alloys thereof. Naidich (U.S. Patent No. 4,024,675) proposes such aggregate abrasive grains wherein adhesion agents are added to the metal and abrasive grains to make a porous cake which is intered and subsequently ground to produce the aggregated abrasive grains. Phaal (U. Patent No. 4,246,006) forms aggregates of diamond particles therein a powdered metal and the diamond abrasive particles are heated to sinter the metal followed by cooling and crushing of the resulting mas & Suitable metals for producing such agglomerates include copper, silver, tin, nickel, cobalt, and iron or alloys thereof. Slack (U.S. Patent no. 4,239,502) @@ips diamond or CBN in a molten Ag/Mn/Zr brazing alloy which coated particles are brazed onto Mo or W rim portions of grinding wheels U.S. Patent No. 2,411,867 mentions silver coated borrt. The present invention is based upon a discovery of certain properties which properly coated silver-coated diamond grit displays in a resin bond grinding element when used to dry grind cemented metal carbide. These properties apparently have gone unnoticed in the prior art apparently because, although silver is among the list of many metals proposed, publIshed tests of silver-coated diamond grit have not bctn found. As wffl be set forth herein, the thermal conductivity of silver, while probably of some benefit in the grinding process, is not the property upon which the invention is based. Broad Statement of the Invention The present invention is an improvement in a method for dry grinding a woricpiece comprising either cemented metal carbide (eg. cobalt cemented tungsten carbide) or a combination of cemented metal carbide and steel with a resin bonded grinding element having diamond particles embedded in the grinding surface thereof. The improvement in the process for increasing the grinding ratio and deers the power required to rotate said grinding element during grinding operations comprises Coating the exterior surfaces of each said diamond particle with a layer of metal consisng essentiafly of elemental silver prior to embedding the diamond particles in the grinding element. Advantages of the present invention include a substantial improvement in the grinding ratio of the silversocted diamond particles compared to %rcoated diamond particles and to diamond particles coated with other metals such as, for examples nickel and copper. Another adrntage is that the power required to rotate the grinding element containing the silver-coated diamond particles is about the same or Only slightly more than the power required to rotate a grinding element containing unecated diamond particles. These Lnd other advantages will be readily apparent to those skilled in the art based upon the disclosure herein. Detailed Description of the Invention The pmperties possessed by the grinding element containing diamond particles, each of said particles having the exterior surfaces thereof coated with a layer oi silver, truly are unique and unexpected. The properties of increased grinding ratios and decreased grinding energy requirements are unique to silver compared to other metals proposed and conventionally used for coating diamond perticlese That is, while increased grinding ratios typically are experienced by coating diamond grit with various metals, necessarily the power required to rotate the grinding element also increases because the coated grit is retained better in the resin matrix of the grinding wheel. Moreover, because the coated diamond grit wally is retained in the resin bond better than uncoated diamond grit, the coated diamond grit in resin bonded grinding elements typically improves the grinding performance oi the grinding element for both wet and dry grinding. These properties and characteristics are typical of conventional commercially exploited copper and nickel coated diamond grit. These properties and characteristics, though, should be contrasted with the properties and characteristics of silver-coated diamond grit used in resin bonded grinding elements. As with other metal coatings on diamond grit, grinding ratios are improved with the silver-coated diamond grit and are improved to a much greater degree than other metal coated diamond grit. Further, contrary to other metal coatings, the power required to rotate the grinding element containing silver-coated diamond grit is substantially the same or only sightly more than the power required to rotate a grinding element containing uncoated diamond grit. This low energy or power requirement to rotate the grinding element truly is an unexpected property of silverwcosted diamond grit and a property not possessed by other metals conventionally used to coat diamond grit. While the precise explanation of the improved performance of silver-coated diamond grit in resin-bonded grinding elements is not fully understood, the following propo@@@ is given by way of explanation and not by way of limitation. As the Examples Wm adequately demon: :trate, the use ot conventional metals to coat diamond grit, for example nickel or copper, always tlates into increased grinding energies relative to the use of uncoated diamond grit in resin bond grinding elements because the metal costing provides better bond retention in the resin bond material. This is to be contested with the use of silver-coated grit wherein, a freer cutting action is seen which trates into subtiìiy equivalent grinding energies for the silvested diamond grit as for uncoated diamond grit. Further, the bond retention of the silvetsted diamond grit in the resin bond grinding element is not improved by reason of the silver coating and wally a poorer bond retention is seen in view of the wet grinding test results as reported herein. Thus, it appears that while improved heat transfer characteristic of the silver necessarily must be print to some degree, the prime charactertic of the silver-coated diamond grit in the present invention is the lubricity which the silver coating provides during grinding operations. Thus, while poorer bond retention are seen, the reduced wheel temperature because of the free cutting action of the silver-coated grit com- pensate: for the reduced bond retention during dry grinding of carbide workpieces. The lubricity function of silver-coated diamond grit is an unexpected property which has not been reported in the art. The coated diamond grit of the present invention comprises individual diamond particles, each of said particles being coated with a layer of metal consisting essentially of elemental silver. While a variety of techniques for individually coating the diamond grit may be possible, the preferred method for coating the diamond grit with elemental silver is that method disclosed in commonly assigned application of John W. Grenier, U.S.S.N. , filed on even date herewith, the disclosure of which is expressly incorporated herein by reference. The Grenier process for coating diamond grit utilizes a formulation known in the art as the Brashear formula The Brashear formula involves an ammoniacal silver solution and a reducing solution. The ammoniacal silver solution preferably is formed from silver nitrate and potassium hydroxide dissolved in water to which ammonia is added. The seducing solution preferably is aqueous invert sugar. The essence of the Grenler process for coating diamond grit with a coating consisting essentially of elemental silver involves suspending the diamond grit in the ammoniacal .silver solution, preferably by physical agitation thereof, followed by the slow addition of the reducing solution thereto chile maintaining the agitation and diamond suspension in the silver solution. The mitered rate of addition of the reducing solution is crarled on until the silver has been coated onto the individual bond grit and scch process repeated until the desired coating weight (or thickness) has been attatned. Advar tages oi the Grader process include a subtantially uniform, continuous grany coating of silver on the diamond grit of closely controlled weight percent. The proportion of elemental silver coating on the diamond grlt generally ranges from about 10 to 75 percent by weight of the coated grit and advantageously between about 25 and 65 percent by weight. As noted above, the Grenier process for coating diamond grit with silver can be practiced advantageously to produce a fairly precise, predetermined weight of silver coating on the diamond grit which coating is substantially uniform in thickness on all surfaces of each diamond particle coated. The particle size of the diamond grit coated is not a limitation of the Grenier process nor is the particle size a limitation on the present invention as those damond grlt particles sizes conventionally used in resin bond grinding elements are used according to the precepts of the present invention. Gcnerally, the diamond grit can range in particle size from about 400 mesh (37 microns) upwards to 40 mesh (420 microns). Preferably, though, narrow particles size distributions are used according to conventional grinding technology with particle size distributions of 80/100 mesh (177-149 microns), liO/170 mesh (105-88 microns), and 200/230 mesh (74-62 microns) being typicsl preferred particle size distributions of the diamond grit for use in the present invention. The resin most frequently used in resin bonded grinding elements or other abrasive elements is a phenol-formaldehyde reaction product However, other resins or organic polymers may be used such as melamine or urea formaldehyde resins, epoxy resins, polyesters, polyamides, and polpmidess A resinoid grinding wheel with the silver coated diamond grit of the present invention can be formed, for example, in the manner as taught in U.S. Patent No 3,645,706. Further details on resins can be found in U.S. Patents Nos. 3,385,684; 3,664,819; 3,779,727; and 3,957,461. The concentration of silverweoated diamond grit in the resin bonded grinding element broadly ranges from about 25 to 200 (100 concentration conventionally being defined in the art as 4.4 carats/cm with 1 carat equal to 0.2g wherein the concentration of diamond grains is linearly related to its carat per unit volume concentration). Preferably, the concentration of coated diamond grit ranges from about 50-100. The size and shape of the grinding element is conventional and typically grinding wheels are of a disc shape or cup shape. Of course, a secondary distribution of silicon carbide or other secondary abrasive particles may be used in the resin bond grinding elements without detrimentally effecting the performance of the grinding element containing the silvecoated diamond grit of the prtecnt invention. The improved resinoid grincErg elements of the present invention having silver-coated diamond grit in the grinding area are extremely useful in dry grinding of non-ferrous wokkpieces such as cemented tungsten carbide and cemented tungsten carbide/steel combinations. Cemented tungsten carbide and similar non- ferrous workpieces are well known in the art and little more need be said about them hera. The following Erampies show how the present invention can be practiced, but should not be construed as limiting. In this application, all units are in the metric system, all mesh sizes are in United States Standard Sieve Series, and all percentages are by weight, unless otherzrlse expressly indicated. Also, all refer- ences cited herein are expressly incorporated herein by reference. IN THE EXAMPLES In the Examples, the silver-coated diamond grit was manufactured by coating the diamond Errit of indicated particle size with a coating consisting essentially of silver according to the Grenier process. A typical procedure according to the Grerder process is given here. Such process was used to coat all the diamond grit in the Examples with the exception that the proportion of silver coated onto the diamond grit was adjusted in order to coat the diamond grit with a desired proportion of the coating. Initially, the diamond grit is cleaned with aqua regia to remove residual impurities of graphite, oil, and like Impurities. The surfaces of the diamond grit then were activated by stirring the diamond grit in a stannous chloride solution made from 20 grams stannous chloride, 20 ml HCl, and one liter of hot water. After 20 minutes of stirring in the stannous chloride solution, the diamond grit was rinsed once with deionized water. The surface-activated diamond grit (50g sample) then was added to a vessel containing the ammoniacal silver solution which was made by the following procedure: 20 grams silver nitrate was added to 300 ml water followed by the addition of 10 grams of potaium hydroxide in 100 ml of water. Next, 50 ml of ammonium hydroxide was added to the vessel and the contents of the vessel stirred until the contents were clear. The diamond grit was suspended in this ammoniacal silver solution by agitation with a conventional bladed stirrer which stirrer was set at a rate sufficient so that the diamond grit was suspended in the solution. A reducing solution of invert sugar wag made by- adding 90 grams table sugar to 1 Utter of deionized water followed by the fourths addition of 4 ml nitric aid. This solution was heated at about 90µ C for onAlf hour and then cooled. The reducing solution was added to the ammoniacal silver solution with suspended diamond therein at a rate of about 25 drops per minute while agitation of the ammoniacal silver solution was continued. At the conclusion of the addition of the reducing solution, the diamond was separated and rinsed with additional water. Preferably, the silvering solution is subjected to a silver recovery operation by techniques conventional in the art. This silvering procedure then was repeated a successive number of times until the desired weight percent of silver on the diamond grit was achieved. For example, coating 80/100 mesh diamond grit at about 50% silver coating by weight has taken 9 repeats of the foregoing procedure. The number of repeats of the silvering proedcre for various size diamond particles for various weight percent of silver coating can be established readily by thase skilled in the art. The recovered silver-coated dialnond grit then was used in forming resinoid grinding elements as indicated in the Examples which follow. EXAMPLE 1 In order to demonstrate the effectiveness using silver coated diamond grit in resin bond grinding wheels for dry grinding cemented tungsten carbide workpieces, a 1 series of phenolic resin bonded grinding wheels were prepared containing 25 volume percent (100 concentration) of various types of diamond grit. The grinding wheels were standard DllV9 test wheels, 9.525 cm x 3.81 cm x 3.175 cm (3.75n x 1.5" x 1.25"), with a 0.3175 cm (0.125n) wide abrasive rim. The diamond grit was either uncoated or coated at various levels with copper, nickel, or silver. The workpieces ground were 6.4 mm x 19.1 mm bars of CARBOLOY Grade 44A cemented tungsten carbide (CARBOLOY is a registered trademark of General Electric Company). The two sets of dry grinding conditions used are given below: Condition & um; 1 Condition & um;2 Wheel speed 22 m/sec 18 m/sec. Table speed 1.5 m/min. 1.5m/min. Infeed 0.064 mm. 0.075 mm Coolant dry dry The weight-percent of the coating, the size of the diamond grit, and the results obtained (grinding ratio and grinding energy) are displayed in the following table TABLE 1 Mesh Size Nickel Coating Copper Coating Silver Coating Test Coatlrg (1) (2) (3) Condi- 96 of Grit(1) GR(2) GE( ) GR GE GR GE tion 1 0 80/100 16 73 16 73 16 73 1 25 80/100 20 79 23 83 41 72 1 50 80/100 22 86 28 97 65 67 1 65 80/100 31 92 97 99 772 72 2 0 80/100 24 47 24 47 24 47 2 25 80/100 37 57 41 62 101 49 2 50 80/100 44 70 58 72 197 42 2 65 80/100 53 78. . 156 . 65 964 52 1 0 200/230 19 46 19 46 19 46 1 25 200/230 42 50 71 52 73 46 1 50 200/230 102 53 199 57 448 47 1 65 200/230 72 56 622 59 902 57 2 0 200/230 17 28 17 28 17 28 2 25 2Q0/230 40 30 52 33 62 27 2 50 200/230 85 33 247 . 43 332 30 2 65 200/230 - - - - (1) 80/100 mesh is 177/149 microns. 200/230 mesh is 74/62 microns. (2) GR is grinding ratio (ratio of the volume of workpiece material removed to the volume of grinding wheel material removed during the grinding operation) (3) GE is grinding energy (watt-hour/cm3 of workpiece removed) Several unexpected benefits of the invention are deen in the above-tabulated results. Grinding ratios of the wheels increase with increasing metal coating levels for all metals, yet for the silver coating the grinding ratio4 far excecd those of the other metal coatings at all coatings levels Note that the grinding energies increased with increasing coating levels for the nickel and copper coated diamond grit. Such results should be contrasted with the grinding energies of the silver coated diamond grit where grinding energies remained substantially the same as the uncoated diamond grit for coatings levels up to 50% and only increased slightly at the 65% coating level. The combination of improved grinding ratios and lower grinding energies is unique to silver coatings and truly unexpected. Practical benefits of these ties translate into longer wheel lives; significantly higher grinding rate: (wokkpiece removal rate); and the ability to use high performance grinding wheels on grinding machines with smaller (horsepower) motors, which because of power requirements have been limited to uncoated grit or a low grinding ratee EXAMPLE '2 Additional phenolic resin bonded grinding wheels were prepared containing uncoated 140/170 mesh (105/88 microns) diamond grit and other wheels containing silver coated (29% coating level) and nickel coated (59% coating level) diamond grit. The diamond concentration in all wheels was 19 volume percent. The wheels were used to wet surface grind CARBOLOY Grade 370 tungsten carbide workpieces under the following grinding conditions. Condition v 1 Condition t a Wheel speed 24.5 m/sec 24.5 m/sec Table weed 15 m/min. 15 m/min. Downfeed 0.025 mm. 0.038 mm. Crossfeed 1.27 mm. 1.27 mm. Coolant H2 + water-soluble oil H2O+ water-soluble oil The following grinding results were obtained: TABLE 2 Test Uncoated Grit Nickel Coating Silver Coating Condition GR GE GR GE GR GE 1 90 24 207 31 59 22 2 38 20 123 23 20 19 These wet grinding results demonstrate that while nickel coating, as in dry grinding, results in higher grinding ratios as compared to uncogted grit, the silver coating results in lower grinding ratios compared to uncoated grit. Apparently, the silver coating, unlike the nickel coating, does not improve but le5the retention of the grit in the resin bond as these results demonstrate.

Claims: CLAIMS 1. In a method for dry grinding a workpiece selected from the group consisting of cemented metal carbide and combinations of cemented metal carbide and steel with a resin bonded grinding. element having metal coated diamond particles embedded in the grinding surface thereof, the Improvement for increasing the grinding ratio and decreasing the power required to rotate said grinding element during grinding operations, which comprises using diamond particles coated with a layer of metal consisting essentially of silver. 2. The method of claim 1 wherein the ption of silver coating on each diamond particle ranges between about 109S and 75% by weight of said diamond particle. 3. The method of claim 2 wherein said proportion is between about 25% and 65% bjweight. 4. The method of claim 1 therein said diamond particles range in size from between about 37 microns and 420 microns. 5. The method of claim 4 wherein said diamond particles are restricted in size to a narrow particle size distribution. 6. The method of clam 1 wherein the concentration of said silver coated diamond particles in said grinding element is between about 1 and 9 carats/cm3. 7. The method of claim 6 wherein said concentration is between about 2*2 and 4.4 carats/cm3.

Inventors: PASCOE, EDWIN ALBERT, RUARK, WILLIAM WEBSTER
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1982
Main classification: B24D3
IPC codes: B24D3, C09K3