Multi-layer printed circuit board and process for production thereof

Abstract: A multi-layer printed circuit board produced by laminat­ ing a plurality of unit circuit sheets via prepreg resin sheets, the cured resin in said unit circuit sheet having a glass transition temperature Tg₁, said prepreg resin sheets having been prepared by impregnating a reinforcing substrate with a resin composition which can be cured at a temperature equal to or lower than both the glass transition temperature of Tg₁ and that of Tg₂ of the resin in the prepreg resin sheet after cured, and binding the laminated sheets with heating under pressure at a temperature equal to or lower than both the temperatures of Tg₁ and Tg₂, has excellent dimensional stability, heat resistance and through-hole reliability.

Description: This inventoin relates to a multi-layer printed circuit board with high dimensional precision and a process for the production thereof. An increasing tendency is seen recently to greater compactness and densification of the multi-layer printed circuit boards used in the industrial and business machines such as computers. In line with this, there are required higher heat resistance of the boards to cope with increase of heat release from elements, e.g., LSI. in use, finer pattern to accommodate increased wiring density, higher dimensional stability between layers in response to the increased number of layers and higher through-hole reliability. As a material that can answer to such requirements, polyimide type materials have come to be used in place of the conventional epoxy type materials which are rather poor in heat resistance. Dominant among such polyimide materials are aminobismaleimide resins and their epoxy-modified resins. In production of a printed circuit board, such an epoxy or polyimide resin is impregnated in reinforcing fabrics to form prepregs and separately made unit circuit sheets are laminated via such prepreg resin layers. The heating temprature used in the heat and pressure molding for lamination is usually of the order of 170 - 180°C, and the resultantly obtained cured product has a glass transition temperature (Tg) of the order of 120 - 160°C which is lower than said molding temperature. Glass transition temperature (Tg) is used as an index of heat resistance, but Tg of the order of 120 - 160°C said above cannot provide satisfactory heat resistance. In order to obtain sufficient heat resistance, it needs to perform additional 2- to 3-hour post-curing by heating the molding to 200 - 240°C to elevate Tg to a level above 170°C, prefeerably to a level of around 200°C. However, post-curing under such elevated temperatures tends to cause dislocation among the layered circuit boards and the reduction of adhesive strength between the inner copper foil and prepreg, resulting in an adverse effect to the dimensional precision of the product. While removal of such evil effects of post-curing has been desired, no positive solution to this problem has been available to date. US-A-3 899 626 discloses a process for producing a composite article comprising a layer of a prepolymer obtained by reacting a bis-imide with a polyamine (layer (a)) and a solid layer such as a copper foil (layer (b)), characterized by coating a polyamide-imide solution on a surface of the layer (a) before the adhesion, and adhering the layers (a) and (b) at 100 to 280°C. The object of this citation is to improve the adhesive strength between the copper foil and the cured product of the prepolymer. FR-A-2 463 784 discloses a process for preparing an imide type prepolymer comprising reacting a bisamide with a diamine, and further reacting with an epoxy compound. These are products as used according to the patent. In the hope of solving the above-mentioned problem, the present inventors have pursued studies on a relationship between the heating temperature (T L ) in the working process, including the heat and pressure molding for lamination of circuit boards and post-curing, and the glass transition temperature (Tg) of the cured resin in the boards, and found that said problem can be solved by a consideration from such a new standpoint. The present invention was reached as a result of such studies. According to the present invention, post-curing required to perform in succession to the heat and pressure molding for lamination in the prior art is unnecessitated and said heat and pressure molding can be accomplished at a relatively low temperature used heretofore, and further the cured resin in the molding has Tg which is high enough to unnecessitate any post-curing, allowing obtainment of a heat resistant multi-layer printed circuit board with high dimensional precision and high through-hole reliability. The innventors have found that the resins disclosed in FR-A-2 463 784 are especially suitable for the production of multi-layer circuit boards which have a high through-hole reliability. The present invention provides a multi-layer printed circuit board having a plurality of unit circuit layers connected by through-holes, which comprises (I) a plurality of unit circuit sheets having circuit layers on at least one surface of said unit circuit sheets in which a resin composition has been impregnated in a reinforcing material and cured, and (II) a plurality of prepreg resin sheets in which a resin composition has been impregnated in a reinforcing substrate and cured, wherein the unit circuit sheets and prepreg resin sheets are laminated and bonded alternatively, with heating under pressure to form a multi-layer laminate. (III) outermost layer circuit patterns, which are formed on the outermost surfaces of said laminate by etching, and (IV) through-holes on the multi-layer laminate, which connect the circuit layers and outermost layer circuit patterns with plating of the through-holes, which is characterized in that the resin composition for at least the prepreg resin comprises (I) a prepolymer obtained by preliminarily reacting with heating (a) a bisimide of the formula wherein R is a divalent organic group having at least one carbon-carbon double bond: and R 1 is a divalent organic group having at least two carbon atoms, and (b) a diamine of the formula H 2 N - R 2 - NH 2 wherein R 2 is a divalent organic group having at least two carbon atoms, (II) an epoxy resin, and (III) at least one amine selected from the group consisting of a s-triazine type amine compound of the formula: wherein R 3 , R 4 and R 5 are independently hydrogen, halogen, a hydrocarbon group, an amino group, a hydroxyl group, an amino-substituted hydrocarbon group, a hydroxyl-substituted hydrocarbon group, or a hydrocarbon-substituted amino group, and at least one of R 3 , R 4 and R 5 being an amino group or an amino-substituted hydrocarbon group said resin composition for at least the prepreg resin having been cured and the laminated sheets bound by heating at a temperature equal to or lower than both the glass transition temperature (Tg 1 ) of the cured resin in unit circuit sheets and the glass transition temperature (Tg 2 ) of the cured resin in the prepreg resin sheets after curing. Furthermore, the present invention provides a process for producing a multi-layer circuit board which comprises laminating a plurality of unit circuit sheets having circuit layers on at least one surface of said unit circuit sheets in which a resin composition has been impregnated and cured, via prepreg resin sheets, said prepreg resin sheets having been prepared by impregnating a reinforcing substrate with a resin composition, binding the laminated sheets with heating under pressure to form a multi-layer laminate, drilling through-holes on the multi-layer laminate, followed by plating of the through-holes. and forming outermost layer circuit patterns by etching, characterized in that the resin composition for the prepreg resin is cured by heating it at a temperature equal to or lower than both the glass transition temperature (Tg 1 ) of the cured resin in the unit circuit sheets and the glass transition temperature (Tg2) of the cured resin in the prepreg resin sheets after curing, and the binding of the laminated sheets is performed at a temperature equal to or lower than both the temperatures of Tg 1 and Tg 2 and the resin composition for at least the prepreg resin comprises (I) a prepolymer obtained by preliminarily reacting with heating (a) a bisimide of the formula wherein R is a divalent organic group having at least one carbon-carbon double bond; and R 1 is a divalent organic group having at least two carbon atoms, and (b) a diamine of the formula H 2 N - R 2 - NH 2 wherein R 2 is a divalent organic group having at least two carbon atoms, (II) an epoxy resin, and (III) at least one amine selected from the group consisting of a s-triazine type amine compound of the formula: wherein R 3 , R 4 and R 5 are independently hydrogen, halogen, a hydrocarbon group, an amino group. a hydroxyl group, an amino-substituted hydrocarbon group, a hydroxyl-substituted hydrocarbon group, or a hydrocarbon-substituted amino group, and at least one of R 3 , R 4 and R 5 being an amino group or an amino-substituted hydrocarbon group. Most preferred is an embodiment where as an amine there is selected one from the group benzoguanamine. 2,4-diamino-s-triazine, 2,4-diamino-6-methyl-5-triazine, melamine. In the accompanying drawings, FIG. 1 is a sectional view illustrating a laminate of unit circuit sheets as laminated with the medium of prepreg resin sheets for forming a multi-layer printed Circuit board according to this invention, and FIGS. 2 to 4 are sectional views of the multi-layer printed boards having through-holes as produced according to the embodiments of this invention. The present invention is first described by referring to FIG. 1. Each unit circuit sheet 1 comprises a resin-impregnated sheet 3 (said resin being cured) having circuit layers 2 on at least one surface thereof. As the resin used for the resin-impregated sheet 3 of each unit circuit sheet 1, there may be exemplified the addition polymerization type polyimide resins such as those prepared from polymaleimides and diamines, dehydration condensation type polyimide resins, triazine type resins such as BT resins (mfd, by Mitsubishi Gas-Chemical Co., Inc., Japan), cyanate series resins (mfd. by Bayer A.G., etc.). It is also possible to use the same resin compositions as used for preparing prepreg resin sheets mentioned below. Each prepreg resin sheet 4 can be formed by impregnating a reinforcing substrate, for example a reinforcing fiber cloth such as glass cloth, carbon fibers, polyamide fibers, etc., with a specific polyimide resin composition such as shown below by dissolving the composition in an ordinary varnish solvent, and drying the same in a usual way (with the varnish solvent being evaporated away at 120 - 150°C). The glass transition temperature (Tg 1 ) of the polyimide resin obtained from a polymaleimide and a diamine in the unit circuit sheets after curing is mostly in the range of 180 - 300°C, while the glass transition temperature (Tg 2 ) of the polyimide resin composed of said components (I), (II) and (III) in the prepreg resin sheets after curing is also in the range of 180 - 300°C, but its curable temperature is below said range of Tg 2 . Now, the resins used for the prepreg resin sheets consisting of said components (a) and (b) are described in detail. The resins are known from FR-A-2 463 784 As examples of the bisimides of component (a) represented by the formula: wherein R is as defined above and preferably having 2 to 10 carbon atoms: and R 1 is as defined above and preferably having 2 to 40 carbon atoms, there may be cited N,N'-ethylenebismaleimide, N,N'-hexamethylenebismaleimide, N,N'-m-phenylenebismaleimide, N,N'-p-phenylenebismaleimide, N,N'-4,4'-diphenylmethanebismaleimide, N,N'-4,4'-diphenyletherbismaleimide, N,N'-methylenebis(3-chloro-p-phenylene)bismaleimide, N,N'-4,4'-diphenylsulfonebismaleimide, N,N'-4,4'-dicyclohexylmethanebismaleimide, N,N'-α,α'-4,4'-dimethylenecyclohexanebismaleimide, N,N'-m-methaxylenebismaleimide, N,N'-4,4'-diphenylcyclohexanebismaleimide. These compounds may be used either singly or in combination. The effect of this invention can be well attained by using with said bismaleimide a polyvalent maleimide of the formula: wherein n is 0.1 to 3.0 on the average. As examples of the diamines, or component (b), represented by the formula: H 2 N - R 2 - NH 2 wherein R 2 is as defined above and preferably having 2 to 40 carbon atoms, there may be cited the following: 4,4'-diaminodicyclohexylmethane, 1,4-diaminocyclohexane, 2,6-diaminopyridine, m-phenylenediamine, p-phenylenediamine, 4,4'-diaminodiphenylmethane, 2,2'-bis(4-aminophenyl)propane, benzidine, 4,4'-diaminophenyl oxide, 4,4'-diaminodiphenylsulfone, bis(4-aminophenyl)phenylphosphone oxide, bis(4-aminophenyl)methylamine, 1,5-diaminonaphthalene, m-xylenediamine, p-xylenediamine, hexamethylenediamine, 6,6'-diamine-2,2'-pyridyl, 4,4'-diaminobenzophenone, 4,4'-diaminoazobenzene, bis(4-aminophenyl)phenylmethane, 1,1-bis(4-aminophenyl)cyclohexane, 1,1-bis(4-amino-3-methylphenyl)cyclohexane, 2,5-bis(m-aminophenyl)-1,3,4-oxadiazole, 2,5-bis(p-aminophenyl)-1,3,4-oxadizole, 2,5-bis(m-aminophenyl)thiazo (4,5-d)thiazole, 5,5'-di(m-aminophenyl)-(2,2')-bis(1,3,4-oxadiazolyl), 4,4'-diaminodiphenylether, 4,4'-bis(p-aminophenyl)-2,2'-dithiazole, m-bis(4-p-aminophenyl-2-thiazolyl)benzene, 4,4'-diaminobenzanilide, 4,4'-diaminophenyl benzoate, N,N'-bis(4-aminobenzyl)-p-phenylenediamine, 4,4'-methylenebis(2-chloroaniline), etc., and these compounds may be used either alone or in admixture. In the present invention, a bisimide of the formula (1) and a diamine of the formula (2) are preliminarily reacted at 80 - 160°C for 10 - 90 minutes to form a prepolymer (I). The molar ratio of bisimide to diamine is preferably within the range of 1:0.1 to 1:1. A too small amount of amine leads to very poor curing characteristics, causing insufficient curing at the desired molding temperature, while an excess amount of amine results in a short useful life as varnish and prepreg. As the epoxy resin (II) used in the present invention, there may be employed epoxy compounds having at least two epoxy groups, for example bifunctional epoxy compounds such as bisphenol A diglycidyl ether, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate, 4,4'-(1,2-epoxyethyl)biphenyl, 4,4'-di(1,2-epoxyethyl) diphenyl ether, resorcindiglycidyl ether, bis(2.3-epoxycyclopentyl) ether, N,N'-m-phenylenebis(4,5'-epoxy-1,2-cyclohexanedicarboxyimide). etc.., and trifunctional or higher-order polyfunctional epoxy compounds such as triglycidyl compounds of p-aminophenol, 1,3,5-tri(1,2-epoxyethyl)benzene, tetraglycidoxytetraphenylethane, polyglycidyl ether of phenol-formaldehyde novolak resin, etc. It is also possible to use epoxy compounds having a hydantoin skeleton or halogen-containing epoxy compounds. Such an epoxy resin may be used directly for preparing a prepreg resin composition, or it may be preliminarily reacted with a prepolymer (I) obtained from said bisimide and diamine combination. It is desirable that said epoxy resin is used in an amount within the range of 15 - 70% by weight based on said resin composition (that is, the total amount of the prepolymer (I) and epoxy resin). A too small amount of epoxy resin leads to poor curing characteristics, making it unable to obtain the desired properties of the cured resin by curing at a temperature of. for example, around 170°C, while too much epoxy resin loading results in poor heat resistance of the cured laminate resin. Another component (III) of the prepreg resin composition used in this invention is at least one amine compound selected from the group consisting of amine compounds having an s-triazine ring represented by the formula: wherein R 3 , R 4 and R 5 are as defined before. Examples of the amine compounds of the formula (3) having an s-triazine ring are: melamine, 2-amino-s-triazine, 2-amino-4-phenyl-s-triazine, 2-amino-4,6-diethyl-s-triazine, 2-amino-4,6-diphenyl-s-triazine, 2-amino-4,6-bis(p-methoxyphenyl)-s-triazine, 2-amino-4-anilino-s-triazine, 2-amino-4-phenoxy-s-triazine, 2-amino-4-chloro-s-triazine, 2-amino-4-aminomethyl-8-chloro-s-triazine, 2-(p-aminophenyl)-4,6-dichloro-s-triazine, 2,4-diamino-s-triazine, 2,4-diamino-6-methyl-5-triazine, 2,4-diamino-6-phenyl-s-triazine-2,4-diamino-6-benzyl-s-triazine, 2,4-diamino-6-(p-aminophenyl)-s-triazine, 2,4-diamino-6-(m-aminophenyl)-s-triazine, 4-amino-6-phenyl-s-triazine-2-ol, 6-amino-s-triazine-2,4-diol, etc. These amine compounds may be used either singly or in combination. Said amine compound is preferably used in an amount in the range of 0.2 - 25 parts by weight based on 100 parts by weight of the sum of the components (I) and (II) of the resin composition. It was found in this invention that these amine compounds of the formula (3) having an s-triazine ring, when blended as a curing agent in the composition comprising a bisimide-diamine prepolymer (I) and an epoxy resin (II) or in a prepolymer obtained by preliminarily reacting said both components, show a so-called latent curing characteristic, that is, when they are blended as said above, the reaction advances very slowly at a temperature below 150°C while progresses very rapidly at a temperature above 160°C, in contrast with the ordinary amine type curing agents. Therefore, they can be favorably used for the preparation of the products such as prepregs which are required on one hand to have a long pot life and also required on the other hand to show a desired resin fluidity during molding and cure sufficiently at a molding temperature of around 170°C. In the present invention, the following excellent effect is provided by use of the polyimide resin composition comprising the prepolymer (I) containing said materials (a) and (b) and further comprising said components (II) and (III). That is, desired adhesion molding (multi-layer lamination) can be accomplished under the conditions of about 160 - 180°C for 60 - 90 minutes, which are on a par with the preparation conditions for the ordinary epoxy prepregs. Further, the glass transition temperature of the cured resin can reach over 180°C by one molding operation. This is a surprising improvement in comparison with the conventional polyimide resins with which it has been possible to merely give a cured resin laminate with Tg of the order of 120 - 160°C under such adhesion (laminating) molding conditions. Thus, the process of this invention dispenses with the post-cure at an elevated temperature, which has been a serious problem in the preparation of the polyimide prepregs in the prior art. This, accordingly, can solve the problems such as reduction of adhesive strength between inner copper foil and prepreg, lowering of dimensional precision, etc., resulting from post-cure at an elevated temperature in the production of the conventional imide resin multi-layer printed circuit boards. Further, the heat resistant properties of the multi-layer printed circuit board, that is, soldering heat resistance, glass transition temperature, etc., are not affected as heat resistance peculiar to polyimide resins is maintained at its original level. Particularly, considering that soldering heat resistance at 300°C has influences not only on heat resistance of the resin but also on said inner copper foil-prepreg adhesive strength, the multi-layer printed board of this invention is superior to the conventional polyimide type printed circuit boards in this respect, too. Moreover, the polyimide resin composition used in this invention has an excellent pot life at room temperature and the reaction advances very slowly at around the varnish-solvent-drying temperature (120 - 150°C) during production of prepregs, that is, said composition has so-called latent curing characteristics, so that there is no likelihood of the reaction advancing too fast. Therefore, the produced prepregs show good flow characteristics at the molding temperature of the level used for epoxy resins and hence are very excellent in moldability. This, too, contributes to the improvement of dimensional precision in the present invention. The multi-layer printed circuit board according to this invention is produced by laminating a plurality of said unit circuit sheets by interposing a corresponding number of said prepreg resin sheets, and then subjecting the laminate to molding under pressure with heating at a temperature equal to or lower than both the glass transition temperature Tg 1 of the cured resin in the unit circuit sheets and the glass transition temperature Tg 2 attained by the resin in the prepreg resin sheets when said resin is cured. It is desirable that both Tg 1 and Tg 2 are 170°C or higher, more preferably above 180 - 190°C, and such desirable glass transition temperatures Tg 1 and Tg 2 can be well obtained in this invention by using a molding temperature of the order of 160 - 180°C which temperature range has been generally employed for lamination heating in the art. That the glass transition temperature of the resin in the circuit board can be raised to 170°C or higher by using a relatively low molding temperature and without post-curing is extremely advantageous as it can markedly enhance productivity in industrial production. The pressure used in heat and pressure molding for multi-layer lamination is preferably within the range of 5 to 30 kg/cm 2 . The present invention is described in further detail hereinbelow by way of the following Examples, in which all "parts" and "%" are by weight unless otherwise specified. The resins per se and the prepreg resin per se as used in the examples do not belong to the invention. Example 1 An inner layer circuit pattern was formed by photoetching on a copper-clad laminate prepared by using a prepolymer derived from N,N'-4,4'-diphenylmethanebismaleimide and 4,4'-diaminodiphenylmethane and also using a glass cloth and copper foil as substrate (the laminate having a thickness of 0.27 mm and coated with 70 µm thick copper foil on both sides; Tg 1 : 220°C), and then the copper surface of the circuit pattern was treated according to the following process to form a two-sided wiring unit circuit sheet. Process Trichloroethylene washing → immersion in copper chloride/hydrochloric acid solution (1) (40 - 50°C, 2 min.) → washing with water → immersion in 10% sulfuric acid (room temperature, 2 min.) → washing with water → air blowing → immersion in oxide layer forming solution (2) (70 - 80° C, 2 min.) → washing with water → drying (100°C, 30 min.) Composition of solutions (1) and (2): (1) 300 g concentrated hydrochloric acid. 50 g cupric chloride and 650 g distilled water. (2) 5 g sodium hydroxide, 10 g trisodium phosphate, 30 g sodium chlorite and 955 g distilled water. The thus formed unit circuit sheets were then subjected to adhesion molding along with the prepreg resin sheets (A) specified below, under the conditions of 170°C, 20 kg/cm 2 (pressure) and 80 minutes, in the manner illustrated in FIG. 1 to form a multi-layer laminate (with five unit circuit sheet layers). In FIG. 1, numeral 1 indicates unit circuit sheets, 2 circuits, 3 resin-impregated sheets (with resin cured), and 4 prepreg resin sheets. Then through-holes were formed for electroconduction between the circuits on the respective layers of the multi-layer laminate as shown in FIG. 2, and after applying through-hole plating, the outermost layer circuit was formed by etching to produce a multi-layer printed circuit board. In FIG. 2, numeral 5 indicates through-hole plating films, 6 through-holes and 7 outermost layer circuit. Preparation of prepreg resin sheet (A) 40 Parts of N,N'-4,4'-diaminodiphenylmethanebismaleimide and 10 parts of 4.4'-diaminodiphenylmethane were reacted at 90 - 120°C for 40 minutes, and then this reaction mixture was mixed with 50 parts of a cresol novolak type epoxy resin (epoxy equivalent weight: approx. 230) and reacted at 80 - 110°C for 30 minutes to prepare a prepolymer. 100 Parts of this prepolymer and 6 parts of benzoguanamine were dissolved in a methyl ethyl ketone/methyl cellosolve (1:1 by weight) mixed solvent to form a varnish with 50% solid content. This varnish was used for impregnating an aminosilane-treated glass cloth (0.1 mm thick, mfd. by Nitto Boseki Co., Ltd., Japan), followed by drying at 130 - 140°C for 10 minutes to make a prepreg resin sheet with 40 - 50% resin content. Comparative Example 1 A multi-layer printed circuit board was produced by carring out the same operations as in Example 1 described above except that the prepreg resin sheets (B) specified below were used instead of those (A) employed in Example 1, that the adhesion molding time was prolonged from 80 minutes to 100 minutes and that an additional 180 minute post-curing treatment was conducted at 220°C for elevating the glass transition temperature Tg. Preparation of prepreg resin sheet (B) A prepolymer obtained by preliminarily reacting 78 parts of N,N'-4,4'-diaminodiphenylmethanebis-maleimide and 22 parts of 4,4'-diaminodiphenylmethane at 120 - 150°C for 20 minutes was formed into a varnish with about 50% solids by using N-methyl-2-pyrrolidone as solvent, and this varnish was used for impregnating an aminosilane-treated glass cloth (the same as used in Example 1) and dried at 140 - 160°C for 10 minutes to obtain a prepreg resin sheet with 45 - 50% resin content. The principal properties, as determined in the following ways, of the four multi-layer printed circuit board specimens produced in the Examples and Comparative Example 1 are shown in Table 1. Also shown in Table 1 are the determined properties of a commercially available epoxy type multi-layer printed circuit board using an epoxy resin for both unit circuit sheets and prepregs. The properties were determined in the following ways. Soldering heat resistance: Each multi-layer printed circuit board was cut to a test piece of 100 x 150 mm and floated in a soldering bath (300°C), and the time (see.) that passed till occurrence of any abnormality such as swelling in the board was measured. Inner copper foil adhesive strength: The adhesive force between the inner copper foil and the prepreg layer was expressed by the peel strength (g/cm) measured according to JIS C-6481. Positional shift: The maximum value of positional shift between pad and through-hole in each layer was given. Glass transition temperature Tg: A coefficient of thermal expansion along the thickness of the laminate (10 mm square) was measured at a heating rate of 2°C/min, and the temperature corresponding to the inflexion point on the thermal expansion coefficient-temperature curve was given as Tg. Example 2 Two specimens of multi-layer printed circuit board (with three layers of unit circuit sheets) were produced in the same way as Example 1. Preparation of prepreg resin sheet: 40 Parts of N,N'-4,4'-diaminodiphenylmethanebismaleimide and 13 parts of 4.4'-diaminodiphenylmethane were reacted in 50 parts of methyl cellosolve at 120°C for 30 minutes, and this reaction mixture was additionally mixed with 47 parts of a bisphenol A type epoxy resin (epoxy equivalent weight: approx. 188) and further reacted at 90 - 110°C for 30 minutes. Then, after adding and dissolving 8 parts of 2,4-diamino-6-methyl-s-triazine, the reaction mixture was further added with about 58 parts of methyl ethyl ketone to form a varnish with 50% solids. This varnish was then impregnated in an aminocyan-treated glass cloth (0.1 mm thick) to make a prepreg resin sheet with 30 - 50% resin content. Then said multi-layer printed boards 8 were heat bonded with two said prepreg sheets 9 as shown in FIG. 3(a) to form a multi-layer printed circuit board with six layers of unit circuit sheets as shown in FIG. 3-(b), followed by formation of the outermost layer circuits for finishing in the same way as Example 1. Example 3 On each side of a multi-layer printed board (with three layers of unit circuit sheets) prepared after the manner of Example 1 was additionally laminated a unit circuit sheet through a prepreg resin sheet 9 completely the same as used in Example 2 as shown in FIG. 4(a), which was followed by heat bonding to form a multi-layer laminate (see FIG. 4(b)). The surface treatment for circuit copper coating before laminate adhesion and the laminate adhering conditions were the same as in Example 1. The properties of the multi-layer printed circuit boards obtained in Examples 2 and 5 were determined in the manner described above and shown in Table 2.

Claims: A multi-layer circuit board having a plurality of unit circuit layers connected by through-holes, which comprises (I) a plurality of unit circuit sheets having circuit layers on at least one surface of said unit circuit sheets in which a resin composition has been impregnated in a reinforcing material and cured, and (II) a plurality of prepreg resin sheets in which a resin composition has been impregnated in a reinforcing substrate and cured, wherein the unit circuit sheets and prepreg resin sheets are laminated and bonded alternatively, with heating under pressure to form a multi-layer laminate, (III) outermost layer circuit patterns, which are formed on the outermost surfaces of said laminate by etching, and (IV) through-holes on the multi-layer laminate, which connect the circuit layers and outermost layer circuit patterns with plating of the through-holes, characterized in that the resin composition for at least the prepreg resin comprises (I) a prepolymer obtained by preliminarily reacting with heating (a) a bisimide of the formula wherein R is a divalent organic group having at least one carbon-carbon double bond; and R 1 is a divalent organic group having at least two carbon atoms, and (b) a diamine of the formula H 2 N - R 2 - NH 2 wherein R 2 is a divalent organic group having at least two carbon atoms, (II) an epoxy resin, and (III) at least one amine selected from the group consisting of a s-triazine type amine compound of the formula: wherein R 3 , R 4 and R 5 are independently hydrogen, halogen, a hydrocarbon group, an amino group, a hydroxyl group, an amino-substituted hydrocarbon group, a hydroxyl-substituted hydrocarbon group, or a hydrocarbon-substituted amino group, and at least one of R 3 , R 4 and R 5 being an amino group or an amino-substituted hydrocarbon group. said resin composition for at least the prepreg resin having been cured and the laminated sheets bound by heating at a temperature equal to or lower than both the glass transition temperature (Tg 1 ) of the cured resin in unit circuit sheets and the glass transition temperature (Tg 2 ) of the cured resin in the prepreg resin sheets after curing. A process for producing a multi-layer circuit board according to claim 1 which comprises laminating a plurality of unit circuit sheets having circuit layers on at least one surface of said unit circuit sheets in which a resin composition has been impregnated and cured via prepreg resin sheets, said prepreg resin sheets having been prepared by impregnating a reinforcing substrate with a resin composition, binding the laminated sheets with heating under pressure to form a multi-layer laminate, drilling through-holes on the multi-layer laminate. followed by plating of the through-holes, and forming outermost layer circuit patterns by etching, characterized in that the resin composition for the prepreg resin is cured by heating it at a temperature equal to or lower than both the glass transition temperature (Tg 1 ) of the cured resin in the unit circuit sheets and the glass transition temperature (Tg 2 ) of the cured resin in the prepreg resin sheets after curing, and the binding of the laminated sheets is performed at a temperature equal to or lower than both the temperatures of Tg 1 and Tg 2 and the resin composition for at least the prepreg resin comprises (I) a prepolymer obtained by preliminarily reacting with heating (a) a bisimide of the formula wherein R is a divalent organic group having at least one carbon-carbon double bond; and R 1 is a divalent organic group having at least two carbon atoms, and (b) a diamine of the formula H 2 N - R 2 - NH 2 wherein R 2 is a divalent organic group having at least two carbon atoms. (II) an epoxy resin, and (III) at least one amine selected from the group consisting of a s-triazine type amine compound of the formula: wherein R 3 , R 4 and R 5 are independently hydrogen, halogen, a hydrocarbon group, an amino group, a hydroxyl group, an amino-substituted hydrocarbon group, a hydroxyl-substituted hydrocarbon group, or a hydrocarbon-substituted amino group, and at least one of R 3 , R 4 and R 5 being on amino group or an amino-substituted hydrocarbon group. A process according to claim 2, characterized in that as an amine there is selected one from the group benzoguanamine, 2,4-diamino-s-triazine, 2,4-diamino-6-methyl-s-triazine, melamine.

Inventors: MORISHITA HIROSADA, SHIMAZAKI TAKESHI, TAKAHASHI AKIO, WAJIMA MOTOYO, MORISHITA, HIROSADA, SHIMAZAKI, TAKESHI, TAKAHASHI, AKIO, WAJIMA, MOTOYO
Applicants: HITACHI LTD, HITACHI, LTD.
Application year: 1982
Main classification: C08L79
IPC codes: C08G59, B32B27, H05K3, H05K1, C08G73, B32B15, C08J5, C08L79, H01B3