HYDROGENATION PROCESS

Abstract: Chloronitrobenzenes are reduced with short reaction time and high selectivity to the corresponding chloroanilines using a combination ruthenium-platinum catalyst. The ratio of ruthenium to platinum in the catalyst is from 75:1 to 8:1, the reaction pressure is from 200 to 800 psi and the reaction temperature is from 70°C to 160°C.

Description: HYDROGENATION PROCESS The present invention relates to a process of reducing chloronitrobenzenes to the corresponding chloroaniline. Russian Patent No. 188,982 and "Catalytic Reduction of Chloronitrobenzenes to Chloroanilines" by N.P. Sokolova et al. N.D. Zelinskii Institute of Organic Chemistry, Academy of Sciences of the USSR, pp 1830-1833 (1966) translated from Izvestiya Akademii Nauk SSSR, Seriya Khimicheskaya, No. 11, pp 1891-1895, November 1966, disclose the use of ruthenium supported on barium sulfate as the catalyst for reducing chloronitrobenzene to chloroaniline at pressures of 50 atm. and 100 atm. and temperatures up to 900C. British Patent Specification No. 1,064,959 discloses the hydrogenation of halonitrobenzene to haloaniline using a sulfide of platinum, rhodium, ruthenium or platinum as the catalyst. The use of platinum metal catalyst as the control runs is also disclosed. U.S. Patent 4,164,481 discloses the regeneration of noble metal catalysts which have been used to hydrogenate nitrobenzene to aniline. U.S. Patent 4,059,627 discloses the hydrogenation of chloronitrobenzene to chloroaniline in the presence of a sulfur compound such as a thioether. U.S. Patent 4,169,853 discloses the use of solubilized ruthenium-containing complexes in combination with quaternary ammonium hydroxides to effect the reduction of various ortho-substituted nitroaromatics. The present invention relates to an improved process for the reduction of chloronitrobenzenes to the corresponding chloroanilines. The improvement resides in the use of a supported catalyst which contains both ruthenium and platinum. Surprisingly, the use of this mixed catalyst provides the high selectivity associated with the use of ruthenium along with the rapid hydrogenation associated with the use of platinum. In accordance with the present invention, reduction of a chloronitrobenzene to its corresponding chloroaniline is accomplished by introducing elemental hydrogen, or equivalent sou-ce of hydrogen, into a reaction mixture containing halonitrobenzene and a suitable quantity of catalyst. Generally, from 0.1 to 5.0 percent by weight catalyst including ruthenium, platinum and support, as based on the chloronitrobenzene, will be used. Preferably, the reaction is performed in the liquid phase and to this end temperatures and pressures which admit of a liquid phase are preferably used. Further, it is preferred to perform the reaction at a temperature which not only permits a liquid phase reaction, but also which favors most efficient conversion with respect to rate of reaction, byproduct format ion and minimum dechlorination. In this regard, temperatures from about 700C to 1600C are operable, with 1100C to 1500C constituting the best range. At temperatures above about 1600C, the desired conversion takes place, but the product is contaminated with byproducts. Below 700C, the reaction rate is such that undesirably prolonged reaction periods are required in order to obtain an economical degree of conversion. Generally, the pressure should be from 200 to 800 psi with from 400 to 600 being the preferred range. Above about 800 psi, the expense of creating the pressure becomes excessive with little gain in reactivity. Below about 200 psi, the reaction rate becomes excessively slow. The catalyst will generally contain from 0.5 to 10 wt. % ruthenium as based on the total amount of catalyst and catalyst support present. Generally, the ratio of ruthenium to platinum present in the catalyst will vary from 75:1 to 8:1, with from 60:1 to 30:1 being the preferred range. The ruthenium and platinum may be present on the same catalyst support or the two metals may be separately supported and the two catalysts co-mixed in the reactor. The ruthenium and platinum catalyst may be prepared in various ways in order that a large surface area of metallic ruthenium or platinum per unit weight thereof is provided. A typical preparation includes depositing metallic ruthenium or platinum, for example by spraying, saturating, or precipitating a salt followed by reduction or the like, on a finely divided inert support such as activated alumina or activated carbon. Generally, the support will have a particle size of less than 200 mesh. Other suitable supports include finely divided silicon dioxide, carbon black, alumina, calcium silicate, sodium silicate, mixed silicates such as calcium-aluminium silicate and calcium-sodium silicate, talc, calcium carbonate, and clay. Generally, the reaction time will be from 20 to 300 minutes. The reaction may be run in either the batch or continuous mode. While the process of the present invention is generally applicable to any chloronitrobenzene, the chloronitrobenzenes containing one to three chlorine atoms and one nitro group are preferred. The preferred chloronitrobenzenes are 1-nitro-3, 4-dichlorobenzene, l-nitro-2-chlorobenzene, l-nitro-4-chlorobenzene, l-nitro-2,5-dichlorobenzene and 1-nitro-2, 3-dichlorobenzene. The process of the present invention minimizes production of the chloroazobenzene corresponding to the nitrochlorobenzene starting material. 3,3',4,4'-Tetrachloroazobenzene is an acnegen, and, therefore, its production is undesirable. The chloroanilines produced by the process of the present invention are useful as intermediates in the production of herbicides, dyes and pigments. The following specific Examples are intended to illustrate the invention. In each of Examples 1-12 as reported in Table I, a 1 litre titanium autoclave is charged with 300 g of nitrodichlorobenzene containing 86.3 of the 1 nitro-3,4-dichlorobenzene isomer and 1.2 g of a commercial 5 wt.% ruthenium on finely divided carbon catalyst. The platinum catalyst (pt-Cat) used in Examples 1-10 is a commercial 5 wt.% platinum on finely divided carbon catalyst. The platinum catalyst used in Examples 11 and 12 contains 5 wt.% platinum, 1.25 wt.% nickel and 1.25 wt.% chromium supported on finely divided carbon, prepared by the process of U.S. Patent 3,546,297. In each of Examples 1-12, the autoclave is pressured to 500 psig (3450 kPag) and repressured to 500 psig (3450 kPag) whenever the pressure drops to 400 psig (2760 kPag). In control Example 1, a higher temperature of 140/1500C is used which effectively doubles the reaction rate obtained when 130/1400C is used. In Table I "DECHL" means dechlorination, "DCA" means the 3,4-dichioroaniline product and "TCAB" means 3,3'4,4'-tetrachloroazobenzene. The "DCA" yields reported in Table I are based on the 1-nitro-3,4dichlorobenzene in the starting material. TABLE I Ex Pt-Cat Time Temp DECHL DCA TCAB ----- Min. OC % PPM 1 0 122 140/150 0.747 97.8 2 0.02 165 130/140 0.827 96.3 3 0.02 163 130/140 0.711 95.6 4 0.03 105 130/140 0.786 96.8 217 5 0.03 106 130/140 0.689 97.0 64 6 0.04 72 130/140 1.051 96.0 15 7 0.04 97 130/140 0.704 9.65 483 0.04 89 130/140 0.486 95.8 96 9 0.05 56 130/140 0.742 95.5 2830 10 0.0v 58 130/140 1.056 96.3 2953 11 0.1 67 130/140 0.405 97.8 1346 12 0.1 66 130/140 0.383 98.0 2725

Claims: CLAIMS: 1, A process of reducing a chloronitrobenzene to the corresponding chloroaniline which process comprises contacting said chloronitrobenzene with hydrogen at a temperature of from 700C to 1600C and a pressure of from 200 to 800 psi in the presence of a catalytic amount of a platinum group metal catalyst, as the platinum group metal catalyst ruthenium and platinum being used in a weight ratio of from 75:1 to 8:1. 2. A process as claimed in Claim 1 wherein the catalyst is supported on a finely divided inert carrier, said ruthenium comprising from 0.5 to 10 weight percent of the carrier. 3. A process as claimed in Claim 1 or Claim 2 wherein the catalyst including ruthenium, platinum and support is present in an amount of from 0.1 to 5 percent by weight based on the chloronitrobenzene starting material. 4. A process as claimed in any preceding claim wherein the chloronitrobenzene starting material contains from 1 to 3 chlorine atoms and one nitro group. 5. A process as claimed in any preceding claim wherein the contact is effected at a temperature of from 1100to 1500C. 6. A process as claimed in any preceding claim wherein the contact is effected at a pressure from 400 to 600 psi. 7. A process as claimed in any preceding claim wherein the chloronitrobenzene starting material is 1-nitro-3,4-dichlorobenzene, 1-nitro-2-chlorobenzene, l-nitro-4-chlorobenzene, 1 -nitro-2 , 5-dichlorobenzene or 1-nitro-2 , 3-dichlorobenzene. 8. A process as claimed in any preceding claim wherein the catalyst support is carbon black or alumina.

Inventors: KOSAK, JOHN RICHARD
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1982
Main classification: C07C85
IPC codes: C07C209, C07C67, B01J23, C07B61, C07C211