REFRACTORY MATERIAL

Abstract: A refractory mix comprising an acid-stabilized aqueous zirconia sol and refractory material may be used to cast refractory shapes. The refractory material comprises an "active" refractory material and, optionally an inert refrac­ tory material. Refractory shapes may be produced by forming the refractory mix into the desired shape, allowing the sol to gel and then drying and firing.

Description: REFRACTORY MATERIAL This invention relates to the use of a relatively stable acidic aqueous colloidal zirconia sol as the bonding medium for specific refractories. A procedure that is well-known has been used in the past for making ceramic-shapes, namely mixing a binder and a gelling agent with a refractory and allowing the mix to chemically set or gel to form a bond and then firing the body. Typically many shapes have been made using sodium silicate, potassium silicate, colloidal silica, and hydrolyzed ethyl silicate as bonds. However, to obtain the greatest refractoriness of a body, a bond leaving a residue of a more refractory oxide is preferable. For example, alumina and zirconia produce high temperature bonds for refractories. U.S. 4,025,350 shows the use of an aqueous solution of a zirconium salt with a gelling inducing agent and a gelling delaying agent and a refractory powder to form a refractory article. This composition requires additional gelling agents for control thereby increasing costs and control problems. Also the by-products of the gelation of the zirconium salt would need to be eliminated from the refractory during firing. There is also an added cost of the zirconium salt versus the oxide. U.S. 4,201,594 describes the binding nf refractory materials using zirconium salts and incorporating gelling agents and gel delaying agents. For the same reasons these compositions are less than desirable. U.S. 2,984,576 describes an unfired mixture of a refractory material bonded with a zirconia or hafnia sol in which the percent of solids in the dispersed phase is at least 30%. This patent does not describe the specific refractories useful with the present stable acidic zirconia sol but only as a bond for a variety of refractories. U.S. 3,758,316 describes the process for producing a refractory from a refractory powder and a binder precursor which would include colloidal zirconia, but also requires the addition of a gelling agent. The basic principle of the present invention is to make a refractory mix comprising a refractory material and a stable acidic zirconia sol having a fine particle size and acidic pH. The refractory is composed of an active portion and, if desired, a relatively inert portion. One would expect that highly refractory materials would be relatively inert to the zirconia sol. However, it has been found that a number of refractories are not totally inert to the sol and actually react with the sol to cause gelation of the sol. Very rapid gels or slow gels can be produced depending upon the particular type of active refractory, its particle size distribution, and its percentage in the refractory mix. Some examples of active refractories which will cause gelation with the zirconia sol are-alkali and alkaline earth metal aluminates, silicates, zirconates, stannates, titanates, zirconium silicates and oxides. Specific examples include calcined magnesium oxide, electrically fused magnesium oxide, calcium oxide, electrically fused calcium oxide, mono calcium aluminate, calcium aluminate cements, fused cordierite, high alkali glasses, magnesium aluminate, magnesium aluminum silicate, magnesium zirconate, magnesium silicate magnesium zirconium silicate, magnesium ferrite, magnesium titanate, magnesium stannate, calcium zirconate, calcium silicate, calcium zirconium silicate, calcium titanate, calcium stannate, barium zirconate, barium aluminum silicate, barium aluminate, barium zirconium silicate, barium stannate, barium titanate, barium silicate, strontium zirconate, strontium stannate, strontium zirconium silicate, strontium silicate, strontium aluminum silicate, strontium titanate, electrically fused calcium oxide stabilized zirconia, electrically fused magnesium oxide stabilized zirconia, iron chromite, Zeolex 23, wollastonite, bentonite, strontium aluminate, forsterite, calcium aluminum silicate, fluorspar, fluorbarite, lithium zirconate, lithium aluminate, lithium silicate, lithium aluminum silicate, lithium titanate, lithium zirconium silicate, and other refractory materials which are reactive with the zirconia sol. Some relatively nonreacting refractory materials are monoclinic zirconia, hafnia, alumina, bauxite, mullite, sillimanite, zircon, ceria, thoria, silicon nitride, silica and other minerals which do not contain any large amounts in their structure of the alkaline and alkaline earth metallic oxides or impurities present that may react with the sol. It is also possible to use this system as a bond for various fibers made from aluminosilicates, low alkali glasses, alumina, zirconia, silica, and various organic fibers such as cotton, rayon, nylon, other synthetic fibers. The aqueous zirconia sols used in the examples given in this specification are acidic in nature ranging in pH from about 0.3 to 6.0. The particle size of the zirconia particle is generally small, on the order of 25 millimicrons and smaller. The sol is stabilized by acids such as nitric, hydrochloric, acetic, etc. The gelling action of the sol with the "active" refractory is believed to be due to a reaction of the acid with the "active" refractory, producting a"salt", which reaction raises the pH thereby lowering the sol stability. Also, the salt formed possibly catalyzes the gelling of the sol. This gelling action bonds the refractory into a strong body. Several factors govern the characteristics of the refractory body bonded with the zirconia sol. The type of acid in the sol, the particle size and age of the sol, the percentage of zirconia in the sol, the percentage and type of "active" refractory in the mix, its particle size distribution, temperature, and mixing conditions. The listing of potential "active" refractories shows the presence in many cases of an alkaline or alkaline earth type oxide present in the structure of the refractory or that the "active" refractory is subject to reaction with an acid. The presence of such "active" refractories, serving to react with the sol not only causes gelation but also might serve as sintering aids for certain refractory systems. The comparative scratch hardness of bonded refractory shapes after firing serves as a measure of sintering action by the "active" refractory. One procedure for utilizing this invention is to produce cast refractory shapes by mixing the zirconia sol with at least one "active" refractory. The balance of the refractory may include a relatively inert refractory. In some instances, depending upon the nature of the active refractory, the total refractory may be of the active type. In other instances, the "active" refractory may be a very minor portion of the total refractory in the mix. Particle size distribution and chemical nature of the active refractory are two 6f the major factors in determining the amount of "active" refractory constituent. Various refractory shapes can be cast using this invention to produce practical products, such as metal melting crucibles, boats, tundishes, pouring ladles, pouring cups, tubes, rods, slabs, bricks, saggers, kiln furniture, kiln car tops, open hearth door facing, kiln parts, pouring nozzles, furnace liners, and others. Such mixtures can also be used to cast dental and jewellery molds for metal casting. In particular, some of these mixes are especially suitable for molds for casting superalloys, stainless steels, niobium, tantalum, titanium, and molybdenum. By selection of a high temperature inert refractory, or low-activity "active" refractory, such as zirconia, hafnia, ceria, alumina, yttria, lanthana, a foundry mold can be produced having an extremely high PCE value and having low reactivity to some of the above-mentioned reactive metals. If desirable, pressing mixes can be made which will "set" or "gel" in predetermined times in order that a refractory shape may be made by pressing and then become set or gelled. Thin or thick films may be made from mixes which may be cast on a belt or form and then becoming gelled or set. Coatings may be dipped or sprayed on to a form or shape, and then allowed to gel. Mixes according to this invention may be formed into shapes by injection molding. Present ceramic injection molding techniques usually call for various temporary bonds for the refractory body to allow for ease of molding. Examples are costly waxes, resins, plastics, etc. These organic materials are burned out without leaving a high temperature bond, and shrinkage occurs during loss of organic material. The present invention provides a "green" bond and a fired bond in the refractory body. This technique can be used to mold various-intricate shapes such as spindles, nozzles, ceramic cores for metal castings, ceramic turbine blades and vanes, shell mold parts for metal casting, and various other shapes as desired. A primary application for this invention is to make cast refractory bodies which will set or gell at controlled times. A proportion of "active" refractory may be adjusted according to the set time required for the mass. This percentage varies with the particular "active" refractory. The resulting refractory mix can be then mixed with a suitable amount of the zirconia sol to a heavy pouring consistency and poured or cast into a mold form and allowed to set. Particle size distribution of the refractory mix may be varied according to the desired results, strength, settling within the mold, and gel times. It is usually advantageous to allow adequate time for satisfactory mixing of the refractory before casting into a mold. This depends upon the size of the mold and the equipment used to handle the mix. If a small volume hand mix is used, mixing can usually be carried out in a very short period of time such as one to two minutes and then the mix can be adjusted to gel or set very rapidly. I prefer a relatively fast gel time of 5 to 30 minutes for relatively fast production of shapes. It may be desirable to remove bubbles from the mix and to incorporate suitable wetting and defoaming agents to make a relatively bubble-free or void-free mass. Time may be needed to completely wet in the mass and to deair before casting can be made. Ideally, gelation should occur as soon as practical after pouring. To illustrate this invention, the data in Table l shows the percentage of active refractory that might be mixed with an inert refractory, such as tabular alumina, to produce specific set or gel times. The refractory is mixed with the zirconia sol containing 20% ZrO2 and having a pH of 0.6. The alumina portion was composed of 50% 325 mesh and finer tabular alumina and 50% 60 mesh and finer tabular alumina as supplied by Alcoa. The active refractory percentage is calculated on the basis of the total amount of refractory used for the final mix. The samples indicated in Table 1 all had good green strength and when fired separately to 12000F, 18000F, 20000F, and 25000F had excellent fired strengths. Another series of similar experiments to those in Table l were carried out according to Table 2 in which the tabular alumina refractory base was 25% 325 mesh and finer and 75% 60 mesh and finer. This Table shows the gel times for the various mixes using the active refractory. These were mixed with the same zirconia sol as was used in Table 1. After gelling these samples had excellent green strength and after firing to the same temperature conditions had excellent fired strength. In all cases, 0 the strength at 2500 F was greater than that fired to temperatures below 25000F. Some unique characteristics were noted about the compositions described in Table 1. A series of test specimens approximately l" thick, l" wide and 2.375" long were prepared in a mold using the same compositions as prepared in Table 1. They were allowed to set after gelation for 30 minutes and then removed from the mold. After removing from the mold, the specimen was set out in the air to air dry overnight and then oven dried for 4 0 hours at 120 C to remove all the water from the shape and then placed into a dessicator for cooling. It was then removed and immediately measured. It was noted that all specimens showed some shrinkage from the mold dimension on the order of about one-half to one percent. After the specimens were dried, they were then heated to a 0 temperature of 1200 F and maintained at that temperature for 2 hours and then allowed to cool to room temperature and remeasured. After measuring, the specimens were then reheated to 18000F and held for 2 hours at temperature, cooled, and then remeasured. This same heating was carried out separately at 20000F and 25000F, after which time measurements were made on the specimens. It was noted that on many specimens some very small to fairly sizeable permanent expansion occured after cooling. The data in Table 2 shows the permanent expansion obtained on a number of the specimens cast. The negative value indicates shrinkage. The remainder of the figures indicate permanent expansion. It can be observed from this Table that some substantial expansions occur on certain specimens. These expansions are not necessarily related to the proportion of active refractory but are definitely attributed to the presence of the active refractory. Each composition probably acts in a different manner and produces different reaction products which govern the amount of expansion obtainable. This may be a means for minimizing shrinkageduring firing of refractory bodies utilizing this zirconia sol bonded system. Normally when considerable sintering occurs on firing a refractory to a high temperature, considerable shrinkage occurs with the sintering. It should be noted that several compositions in the tabulation show relatively low shrinkage even when fired at 25000F. Table 3 shows a similar series of measurements made on specimens using the tabular alumina refractory containing 25% 325 mesh and finer and 75% 60 mesh and finer particle sizes with the corresponding "active" refractory. The following are examples of other refractory mixes used with the acid stabilized zirconia sol and illustrating the use of "active" refractories. EXAMPLE I Composition: Electrically fused calcium oxide stabilized zirconium oxide - 325 mesh 30 grams Fused Magnesium Oxide - 325 mesh l gram Tabular alumina 60 mesh and finer 150 grams Tabular alumina - 28 + 43 mesh 120 grams This refractory composition was mixed with 35 ml acid stabilized zirconia sol containing 20% ZrO2. It was then poured into a rubber mold. The gel time was determined to be approximately 5 minutes. After 30 minutes, the sample was removed from the mold and by means of a diamond saw was cut into test specimens for modulus of rupture measurements. Unfired strength of this mix was approximately 57 psi. Samples were fired to 25000F, held for two hours and cooled to room temperature, and modulus of rupture was determined as 575 psi. A similar firing to 27000F for two hours and then cooling showed a modulus of rupture of 910 psi. A firing to 29000F for two hours and cooled showed a modulus of rupture of 1888 psi. EXAMPLE II Composition: Tabular alumina - 325 mesh 240 grams Electrically fused magnesium oxide 2 grams This was mixed with 45 ml of the same zirconia sol as in Example I. The gel time on this mix was approximately 4 1/2 minutes. The green modulus of rupture was not 0 determined but specimens fired to 2000 F for two hours and cooled showed a modulus of rupture of 234 psi. Firing to 0 2500 F for two hours and cooled showed the modulus of rupture to be 1164 psi. Firing to 27000F for two hours and cooling showed a modulus of rupture of 2995 psi. A specimen fired to 29000F for two hours showed a modulus of rupture of 5674 psi. EXAMPLE III Composition: EF zirconium oxide, calcium stabilized, - 325 mesh 170 grams - 50 + 100 mesh - 325 mesh 160 grams - 12 + 35 mesh - 325 mesh 80 grams This refractory composition was mixed with 30 ml of the zirconia sol used in Example I. The gel time was 8 minutes. The modulus of rupture measurements after firing specimens to the particular temperatures for two hours and testing after cooling are as follows: Modulus of Rupture pounds per sg. inch Unfired 278 20000F 479 25000F 1888 27000F 2019 29000F 2623 Test specimens from Examples I, II and III were also measured before firing and after each firing and showed the following percentage permanent expansion (+) or shrinkage (-): Firing Examples Temperature 0F I II III 2000 +0.08 -0.09 -0.11 2500 +0.29 -0.46 -0.51 2700 +0.40 -1.60 -0.50 The development of some permanent expansion couid be helpful in eliminating or minimizing settling and drying shrinkage on some compositions, thereby increasing dimensional accuracy in making shapes. The following is an example of typical shell mold system possible by the use of this invention: Composition: Electrically fused calcium oxide stabilized zirconium oxide 2000 grams Zirconia sol containing 20% ZrO2 500 grams Concentrated hydrochloric acid 17 ml. Wetting agent - Sterox NJ 15 drops. This slurry was prepared to a viscosity of 34 seconds as measured by the Zahn + 4 cup. Sheets of wax, approximately 1/8" thick and 2 1/2" wide by 5 1/2" long were dipped into this slurry and immediately stuccoed while wet with a - 50 + 100 mesh zirconia of the same composition.as used in the slurry. After dipping several specimens, the slurry was diluted with the zirconia sol to a viscosity of 15 seconds and a further dip was applied after the first dip had dried overnight. While the second coating was still wet, it was stuccoed with a relatively coarse zirconia granule of a - 12 + 35 mesh of the same composition as the material in the slurry. This was repeated for additional coatings and a final seal coat was applied, making a total of 6 stucco layers and 7 slurry layers. Two dips were applied per day through the final dip. The dipped specimens were then allowed to dry for 2 days and the wax was melted out. The specimens were then cut into strips 1" wide, dried, and then tested for unfired strength. Six specimens were tested giving an average modulus of rupture value of 500 psi. Additional specimens were fired for 2 hours to various temperatures beginning at 20000F and cooled back to room temperature and tested. The MOR after firing two 20000F was 220 psi. The MOR after firing to 22000F and cooling to room temperature was 300 psi. The MOR increased to 1200 psi after firing to 2500 F. This indicated a substantial strength was obtainable on a shell mold composition utilizing this invention. TABLE 1 Sample Type of Active Wt.% Active Gel Refractory Refractory Time 1 Calcium Aluminate Cement 5.0 Immed. 2 Calcium Aluminate Cement 1.0 3 min. 3 Calcium Aluminate Cement 2.0 4 min. 4 Calcium Aluminate Cement 0.5 45 min. 5 Magnesium Zirconate 1.0 6 min. 6 Magnesium Zirconate 0.5 2 hr.+ 7 Magnesium Zirconium Silicate 1.0 Overnight 8 Magnesium Zirconium Silicate 5.0 55 min. 9 Magnesium Zirconium 7.5 12 min. Silicate 10 Magnesium Zirconium 10.0 10 min. Silicate 11 MgO T-1391- 325 Mesh 1.0 90 sec. 12 MgO T-139 - 325 Mesh 0.8 2 min. 13 MgO T-139 - 325 Mesh 0.6 4 min. 14 MgO T-139 - 325 Mesh 0.4 10 min. 15 Calcium Zirconium 1.0 Overnight Silicate 16 Calcium Zirconium 5.0 20 min. Silicate 17 Calcium Zirconium 3.0 28 min. Silicate 18 Calcium Zirconium 7.5 7 min. Silicate 19 Calcium Zirconate 1.0 Overnight 20 Calcium Zirconate 5.0 1 hr. + 21 Calcium Zirconate 7.5 90 sec. TABLE 1 Cont'd...... Sample Type of Active Wt. % Active Gel Refractory Refractory Time 22 Calcium Zirconate 10.0 Immed. 23 CaO 1.0 Instant 24 CaO 0.1 1 hr. + 25 CaO 0.25 60 sec. 26 CaO 0.5 Instant 27 Iron Chromite 1.0 Overnight 28 Iron Chromite 5.0 30 sec. 29 Iron Chromite 3.0 Overnight 30 Iron Chromite 4.0 2 hrs. 31 Iron Chromite 5.0 9 min. 32 Iron Chromite 6.0 5 min. 33 Zeolex 232 1.0 Overnight 34 Zeolex 23 5.0 Instant 35 Zeolex 23 2.0 8 min. 36 Zeolex 23 3.0 Instant 3 37 Winco Cordierite3-200 Mesh 1.0 Overnight 38 Winco Cordierite-20O Mesh 5. 0 1 hr. + 39 Winco Cordierite-200 Mesh 7.0 12-15 min. 40 Winco Cordierite-20O Mesh 8.0 8 min. 41 Wollastonite 1.0 7-11 min. 1. Manufactured by C.E. Minerals, King of Prussia, Pa. 2. Trademark of J.M. Hubr Corp., Baltimore, Md. 3. Manufactured by Winco Minerals, E. Aurora, N.Y. TABLE 2 Permanent Expansion in Thousandths of Inch at Firing Temperature Sample Gel Time 12000F 1800 F 20000F 25000 F 3 4 min. .010 .003 .001- .005 2 8 min. .002 .001- .003 .004 5 6 min. .006 .004 .003 .006 7 Overnight .004 .003 .004 .009 10 10 min .008 .001 .001- .037 11 1 1/2 min. .005 .004 .011 .011 12 2 min. .008 .003 .002 .016 13 4 min. .002 .000 .002- .020 14 10 min. .002 .005 .003 .011 16 Overnight .016 .015 .016 .013 18 7 min. .006 .009 .005 .026 17 28 min. .005 .006 .004 .022 19 Overnight .004 .003- .001- .007 27 Overnight .008 .010 .000 .012 30 2 hrs. .002 .005 .009 .002 31 9 min. .003 .001- .008 .010 37 Overnight .002 .004 .002- .013 39 15 min. .001 .005 .007 .024 40 8 min. .004 .004 .021 41 11 min. .005- .005 .004 .025 24 60 min. + .004 .006 .015

Claims: CLAIMS 1. A refractory mix comprising: an acid stabilized aqueous rconia sol, and an active refractory material in an amount effec ve to gel said sol, with or without an inert refractory material. 2. A refractory mix comprising an acid stabilized aqueous rconia sol and an active refractory material selected from the group )nsisting of alkali and alkaline earth aluminates, silicates, zir nates, 'stannates, titanates, zirconium silicates and oxides, with r without an inert refractory material. 3. A method of making an unfired refractory shape comprising ixing an acid stabilized zirconia sol with a refractory material, said efractory material comprising an active refractory with or without relatively inert refractory, said active refractory being present n an amount effective to gel said sol, forming the mix into a shape, nd allowing-the sol to gel. 4. A method of making an unfired refractory shape according :o claim 3 wherein the active refractory material is selected from the group consisting of alkali and alkaline earth aluminates, silicates, circonates, stannates, titanates, zirconium silicates and oxides, with Dr without an inert refractory material. 5. The method of making a fired refractory shape comprising nixing an acid stabilized zirconia sol, with a. refractory material, said refractory material comprising an active refractory with or with DUt a relatively inert refractory, said active refractory being present in an amount effective to gel said sol, and forming the mix into a shape, drying the shape and firing to a-temperature sufficient to harden the shape. 6. The method of making a fired refractory shape according to claim 4 which further comprises drying the shape and then firing to a temperature sufficient to harden the shape. 7. The method of making a refractory shape according to claim 3 wherein the mix is of a pourable consistency and the shape is formed by pouring the mix into a mold, allowing the mix to harden, and removing the hardened shape from the mold. 8. The method of making a refractory shape according to claim 3 wherein the mix is made to a consistency suitable for injection molding, then adding the mix to an injection molding means whereby said mix is then injected into a closed mold, allowing the mix to gel and removing the shape from the mold. 9. The method of making a refractory shape according to claim 3, comprising placing the mix into a mold form, molding the mix into final shape, allowing the mix to gel and removing the gelled refractory shape from the mold. 10. The refractory shape produced by the method of claim 3 or 4.

Inventors: FEAGIN, ROY CHESTER C/O REMET CORPORATION
Applicants: REMET CORPORATION
Application year: 1982
Main classification: C04B35
IPC codes: C04B35