POLYHYDRIC ALCOHOLS

Abstract: The invention describes polyhydroxymethyl compounds of formula I CH₃(CH₂) m [C(CH₂OH)X] n (CH₂) p [C(CH₂OH)X] q (CH₂) r [C(CH₂OH)X] s (CH₂) t CH₂M (I) (wherein X represents a hydrogen atom or a hydroxymethyl group; M represents a cyano, ester or N,N-disubstituted amide group, the CH₂-M bond being a carbon-carbon bond; m, n, p, q, r, s and t are non-negative integers the sum of which is from 11 to 19; and n, q and s each has the value 0 or 1, the sum of n, q and s being 1, 2 or 3; with the provisos that where the sum of n, q and s is 1, X represents a hydroxymethyl group and where the sum of n, q and s is 2 or 3, each group represented by X is the same) and mixtures thereof. Such compounds are useful in the preparation of urethanes and urethane-based materials.

Description: Polyhydric Alcohols The present invention relates to polyhydric alcohols and in particular to polyhydric alcohols having a further polar functional group. It is now known that certain polyhydric alcohols, particularly those having a geminal-bis(hydroxymethyl) functionality are highly useful for curing urethane compositions. Such work is described in the United States patent 4,216,343 of Rogier issued August 5, 1980 which discloses geminal-bis(hydroxymethyl) alcohols which also contain a terminal hydroxyl functionality. An example of such a compound is qem-bis(hydroxymethyl) octadecanol. It has been found highly desirable to use such compounds due to the high reactivity of the hydroxyl groups and the stability of the polyol. Additional work concerning such materials is shown in a series of articles from the Northern Regional Research Laboratory (NRRL) of the United States Department of Agriculture at Peoria, Illinois, U.S.A. Representative of such materials worked on by the NRRL are 9,9(10,10)-bis(hydroxymethyl) octadecanoate esters and the corresponding acid. Such work is described by Miller and Pryde [J. Amer. Oil Chemists Soc. 54, 822A-885A (1977); ibid, 55, 469-470 (1978); U.S. Patent 4,093,637]. Further disclosure of hydroformylation technology is made in an article entitled "Obtention de derives biofunctionnels" by R. Lai in Rev. Fr. Corps Gras. 17: 455 (1970).b. Such compounds, however, have carboxyl groups or hydrolyzable ester groups and are thus not fully usable for wetting pigments in polyurethane coatings. Furthermore, compounds such as those of the present invention are miscible with polyisocyanates used to formulate coating systems.. It is, of course, necessary to have sufficient miscibility to allow the formulations of the polyhydroxy compounds of the present invention into polyurethanes. Of course, the compounds of the present invention may be utilized in any area where both a polyhydroxyl functionality and a polar group are required. Throughout the specification and claims, percentages and ratios are by weight, pressure is gauge, and temperatures are in degrees Celsius unless otherwise indicated. According to one aspect of the present invention we provide polyhydroxymethyl compounds of formula I CH3(CH2)m [C(CH2OH)X] (CH2)p[C(CH2OH)X] q(CH2)[C(CH2OH)X] 5(CH2)tCH2M (I) (wherein X represents a hydrogen atom or a hydroxymethyl group; M represents a cyano, ester or N,N-disubstituted amide group, the CH2-M bond being a carbon-carbon bond; m,n,p,q,r,s and t are non-negative integers the sum of which is from 11 to 19; and n,q and s each has the value 0 or 1, the sum of n,q and s being 1,2 or 3; with the provisos that where the sum of n, q and s is 1, X is a hydroxymethyl group and where the sum of n, q and s is 2 or 3, each group represented by X is the same) and mixtures thereof. In the compounds of the invention, the polar group M preferably represents a cyano group, an ester group of formula -COOR or an amide group of formula - CONR2 (in which R may be the same or different). The substituent R is an organic radical, preerably a C14 straight chained or branched alkyl group, optionally substituted by a hydroxyl group, or a phenyl group. Where M represents the amide group -CONR2, the moiety NR2 together may further represent a piperidino or morpholino group. The sum of m,n,p,q,r,s and t preferably is from 13 to 17. The integers m and t are each preferably at least 3, especially preferably 4,5,6 or greater. Where q is 1, it is preferred that n and s are each O. The requirement for the compound of formula I to contain at least two hydroxymethyl groups (the proviso that where the sum of n,q and s is 1, X represents a hydroxymethyl group) will be satisfied where the molecule contains a gem bis hydroxymethyl group and/or where hydroxymethyl groups are located at different carbon atoms on the carbon chain backbone of the molecule of formula I. The present invention relates to polyhydroxyl compounds which contain a polar functional group which may be introduced into the molecule by one of several methods. The hydroxyl functionality may be introduced into the molecule by utilizing an unsaturated material which is hydroformylated e.g. by the use of synthesis gas (a carbon monoxide/hydrogen mixture) to introduce a formyl group at the site of the unsaturation. Catalysts may be selected such that a polyunsaturated material is either polyhydroformylated or is monohydroformylated. Rhodium catalysts give products which introduce the formyl group at substantially every location of unsaturation in the molecule. On the other hand, cobalt catalysts introduce a formyl group only at one site of unsaturation in conjugated polyunsaturated materials. The formyl groups can then be reacted via a Tollens' reaction utilizing a strong base and two moles of formaldehyde per mole of the orignal formyl group, to convert the formyl group directly to the geminal-bis(hydroxymethyl) structures. However, if it is desired, the formyl group may be converted with selective catalysts such as sodium borohydride to convert the formyl group to a hydroxymethyl group. It is noted, however, that the present invention requires that if such a reaction is conducted the intermediate aldehyde must contain more than one formyl group to ensure that a polyhydroxymethyl compound will be obtained. According to a further aspect of the present invention we provide a process for the preparation of polyhydroxymethyl compounds of formula I which process comprises (a) hydroformylating an olefinic compound of formula II CH3(CH2)a(CH=CH)b(CH2)c(CH=CH)d(CH2) e (CH=CH)f(CH2)gCH2M (11) (wherein M is as hereinbefore defined; a, b, c, d, e, f and g are non-negative integers, the sum of a, c, e, g, 2b, 2d and 2f being from 11 to 19; and b,d and f each has the value 0 or 1, the sum of b,d and f being 1,2 or 3) and (b) converting the or CHO group in the product thereby obtained (i) to a ,C(CH2OH)2 group by reacting with formaldehyde in the presence of a strong base, (ii) to a ,CH-CH2OH group by catalytic reduction, or (iii) to awC(CHO)(CH2OH) group by reacting with formlaldehyde in the presence of a weak base and subsequently to a ,C(CH2OH)2 group be reduction, subject to the proviso that where the product obtained by step (a) contains a single formyl group, the conversion of step (b) is effected by process steps (i) or (iii). The starting materials of formula II which may be converted into the desired products of this invention include oleonitrile, a commerically available compound. The reactions are shown in the following scheme: EMI4.1 EMI4.2 Cat. 9(10)-formyloctadecanonitrile (I) CH3 (CH2)8 (7)C(CH2OH) 2 (CH2)7(8)CN 9,9(10,10)-bis(hydroxymethyl)octadecanonitrile In a similar fashion, linoleonitrile can be converted into a tetrahydroxynitrile or a dihydroxy nitrile as shown in the following scheme: EMI5.1 <tb> <SEP> CH3(CH2)4CH=CH <SEP> CH2CH=CH(CH2)7CN <tb> <SEP> linoleonitrile <tb> <SEP> Rh <SEP> cat <SEP> ; <SEP> Co-H2 <tb> CH3 <SEP> (CH2) <SEP> xCH <SEP> (CHO) <SEP> (CH2) <SEP> yCH <SEP> (CHO) <SEP> (CH2) <SEP> zCN <tb> <SEP> where <SEP> x+y+z=l4. <tb> <SEP> 4 <SEP> CH20 <tb> <SEP> + <tb> <SEP> 2NaOH <tb> CK3(CH2) <SEP> C(CH20H)2(CH2) <SEP> r(CH2OH)2(CH2) <SEP> CN <tb> <SEP> NaBH4 <tb> <SEP> CH3(CH2) <SEP> CH(CH20H) <SEP> (CH2) <SEP> CH(CH20H) <SEP> (CH2) <SEP> CN <tb> Likewise, linolenonitrile can be converted intp the triformyl derivative by hydroformylation using a rhodium catalyst and synthesis gas. A tri [gembis(hydroxymethyl)] octadecanonitrile can be formed by reacting triformyl nitrile with excess formaldehyde and caustic. In this invention, unsaturated fatty compounds having 13-23 carbon atoms (excluding those in the polar substituent M) and having the above terminal polar function can be used for the preparation of the polyhydric alcohols of formula I. Similarly, 9,9(10,10)-bis(hydroxymethyl)- N,Ndisubstituted octadecanamide can be obtained from oleic acid as a starting material as illustrated in the following scheme: EMI6.1 (A 9,9(10,10)-bis(hydroxymethyl)-N,N-disubstituted octadecanamide.) The value of R in the disubstituted amide above may be for example dimethyl, diethyl, diphenyl, dibutyl, piperidene or morpholine. Again, while oleic acid is used as an example of the starting material, linoleic and linolenic acids could alternatively be used. It has been found that one particular ester of oleic acid may be converted very usefully through the use of isobutylene to give the tertiary butyl ester denominated as t-butyl 9,9(10,10)-bis(hydroxymethyl) octadecanoate. The t-butyl esters of linolenic and linoleic acids may also be employed analogously. Another class of compounds are noted as starting materials for reacting with synthesis gas to obtain compounds having formyl groups in more than one position in the molecule. This class includes linoleyl or linolenyl acids and alcohols as such starting materials are required to have more than one site of unsaturation. The two or three formyl groups, which result from hydroformylation of a starting material containing two or three carbon-carbon double bonds, may be reduced with sodium borohydride to obtain the di-or tri hydroxy methyl product, e.g. using a linolenyl starting material the product will be, for instance, a 9(10), 12(13) di-hydroxymethyloctadecanonitrile, amide or ester, (such as a tertiary butyl ester). Suggested values for R are those having from 1 to 4 carbon atoms such as methyl, ethyl, propyl, butyl, sec-butyl, hydroxypropyl, hydroxyethyl or mixtures thereof, and, for the moiety NR2, morpholino and piperidino groups. To conduct the synthesis gas reaction, hydrogen and carbon monoxide are added in a closed vessel at temperatures of from 100 to 150 degrees C. The hydrogen and carbon monoxide may be maintained conveniently at molar ratios of from 1.5:0.5 to about 0.5:1.5. It is noted that the ratio is not critical so long as the pressure is maintained in the reaction vessel by the component gases and the amount of hydrogen is not so great as to substantially reduce the unsaturated starting materials. In practice, hydroformylation with the synthesis gas may be conducted at from about 90 degrees C to about 170 degrees C, preferably from 110 degrees C to about 130 degrees C. Above the higher temperatures described above, increased amounts of unwanted byproducts are formed in the reaction mixture. The pressure conditions suitably are maintained in this sealed system at from about 20 to about 500 atmospheres (20.3 to 506.6 bar), preferably from about 30 to about 100 atmospheres absolute (30.4 to 101.3 bar) during the hydroformylation. Conventional cobalt catalysts may be employed to obtain a single formyl group, but are not particularly suitable for polyunsaturated compounds due to reduction of the unsaturation. Conveniently, however, the practical catalyst to use during the synthesis gas reaction is a rhodium-based catalyst. The rhodium may be in any convenient form such as rhodium metal, rhodium oxide, and various other rhodium salts such as rhodium chloride, rhodium dicarbonyl chloride dimer, rhodium nitrate, rhodium trichloride and other similar materials. The rhodium catalyst is also best utilized with a ligand such as trisubstituted phosphine or trisubstituted phosphite. The term trisubstituted includes both alkyl and aryl-compounds and the substituted compounds of alkyl and aryl compounds. A particulalry valuable ligand for the rhodium carbonyl hydride is triphenylphosphite or triphenylphosphine in that both compounds are particularly useful in minimizing migration of the double bond thereby avoiding a large number of isomers with respect to the formyl group. In general, triarylphosphines or triarylphosphites may be used for this purpose in the formation of the rhodium carbonylhydride ligand. In addition, the foregoing materials are extremely valuable in minimizing the undesired saturation of the double bond or the reduction of the formyl group. As was previously noted, materials such as sodium borohydride may be utilized to reduce the formyi group to a hydroxymethyl group thereby obtaining desired compounds of the invention. However, in most cases it is desirable to convert the formyl group completely to the gem-bis(hydroxymethyl) structure via a Tollens' reaction. Such may be achieved by utilizing a strong base as a reactant. Should it be desired for some reason, weak base and one mole formaldehyde may be used to obtain the hydroxymethyl formyl compound which may be utilized for various purposes including subsequent reduction of the formyl group to give the gem-bis(hydroxymethyl) variety of the claimed compounds. In either case, formaldehyde (which is relatively inexpensive) may be used in for example up to 1.5, preferably up to 1.2 times the amount actually required to obtain the hydroxymethyl formyl or the gem-bis(hydroxymethyl) compounds. A convenient manner of adding the formaldehyde and conducting the Tollens' reaction is by using a methanol solution of formaldehyde. As a strong base sodium hydroxide conveniently may be employed, although potassium or calcium hydroxide may alternatively be employed. The Tollens' reaction is generally conducted at a temperature of from about 0 degrees to about 100 degress C, preferably from about 20 degrees C to about 70 degrees C. The compounds of the present invention are particularly suitable for use in reaction with polyisocyanates to form urethanes. A substantial advantage in the compounds of the present invention is that the polar group of the molecule enhances miscibility of the respective urethane forming components. Another significant advantage is the wetting ability of the polar groups which allows for the introduction of pigments such as organic or inorganic pigments, e.g. titanium dioxide, chrome yellow, calcium or barium Lithol, phthocyanines and oxide pigments thereby providing urethane coatings with a high pigment carrying capability. According to a further aspect of the present invention we therefore provide coating and moulding compositions comprising a compound of formula I or the reaction product thereof with a polyisocyanate. The following Examples are provided to illustrate the present invention without serving to restrict the scope of protection sought therefor: PREPARATIVE EXAMPLE A PREPARATION OF FORMYLOCTADECANONITRILE (FON) Into a 1 litre 316 SS autoclave equipped with stirrer and heat exchange coil is place 617 grams of oleonitrile, 3.0 grams of 5 percent rhodium on aluminium (Englehardt Industries) and 3.2 grams of triphenylphosphite. The autoclave is flushed with nitrogen then pressurized with carbon monoxide-hydrogen (1:1) to 1080 psig (7.446 MPa guage). The temperature is increased to 127-133 degrees C and maintained for 3.3 hours with a CO-H2 pressure of 970-1080 psig (6.688 to 7.446 MPa guage). At this point a GC analysis indicated complete reaction of oleonitrile with the formation of FON. The reaction was cooled, the pressure vented and the product filtered. The yield of FON is 681g. Rhodium is removed from the product by vacuum distillation. EXAMPLE I PREPARATION OF gem-BIS (HYDROXYMETHYL) OCTADECANONITRILE (BHMON) Into a 3 litre glass reaction flask is placed 762 grams (2.60 moles) of formyloctadecanonitrile, 321 grams (5.84 moles) of a 54.6 percent solution of formaldehyde in methanol (Methyl Formcel, a product of Celanese Chemical Company), and 6.6 millilitres of 40 percent solution of sodium hydroxide in water. The temperature of the system is maintained at 40 degrees C for 36 minutes then increased to 50 degrees C. After .25 minutes, a 40 percent solution of sodium hydroxide in water is added at a rate of 5.3 millilitres/minute until, including the 6.6 millilitres initially added, a total of 297 grams has been added. Temperature is maintained at 45-50 degrees C throughout the addition and then held at 50 degrees C for an additional 2 hours. The reaction mixture was cooled to 16 degrees C and 27.9 grams of a 12 percent solution of sodium borohydride in 43 percent sodium hydroxide is added. The reaction temperature is maintained between 1627 degrees C for 20 minutes. The reaction mixture is stripped under vacuum at 49 degrees C to remove methanol and water. The residual product is washed at 54 degrees C with 500 millilitres of water plus 100 millilitres of saturated sodium sulfate solution. The upper organic phase is separated and washed successively with 500 millilitres of 0.1 N sodium hydroxide solution and 4X with 500 millilitres portions of water. The product is finally dried in partial vacuum (1 mm Hg (1.33 mbar)) at 70 degrees C. The yield of crude BHMON was 832 grams. PREPARATIVE EXAMPLE B PREPARATION OF 9(10), 12(13)-DIFORMYLOCTADECANONITRILE Hydroformylation of 9,12-linoleonitrile was carried out similar to conditions described in Preparative Example A, except that the CO-H2 pressure is maintained at 2000 psig (13.79 MPa guage). EXAMPLE II PREPARATION OF 9(10),12(13)-BIS(HYDROXYMETHYL) OCTADECANONITRILE Into a solution of 8.86 grams of 9(10), 12(13)diformyloctadecanonitrile (containing about 47 percent 9(10)-formyloctadecanonitrile) in 8.3 grams of isopropyl alcohol at 25 degrees C is added 0.77 grams of sodium borohydride over a period of 5 minutes. After 4 hours at 28 degrees C, additional sodium borohydride (9.24 grams) is added. After 44 minutes the reaction is worked up by addition of 5 millilitres acetone, distillation of the volatiles in vacuo. The residue is dissolved in a mixture of ether-water and the ether layer is washed with water. Evaporation of the ether yielded 7.60 grams of 9(10), 12(13)-bis(hydroxymethyl) octadecanontrile containing some 9(10)-hydroxymethyloctadecanonitrile. Identification of the products was made by I.R., NMR and GC-MS. EXAMPLE III PREPARATION OF 9(10),12(13)-BIS(HYDROXYMETHYL) OCTADECANONITRILE Into a solution of 8.86 grams of 9(10), 12(13)diformyloctadecanonitrile (containing about 47 percent 9(10)-formyloctadecanonitrile) in 8.3 grams of isopropyl alcohol at 25 degrees C is added 0.77 grams of sodium borohydride over a period of 5 minutes. After 4 hours at 28 degrees C, additional sodium borohydride (0.24) grams is added. After 44 minutes the reaction is worked up by addition of 5 millilitres acetone and distillation of the volatiles in vacuo. The residue is dissolved in a mixture of ether-water and the ether layer is washed with water. Evaporation of the ether yielded 7.60 grams of 9(10), 12(13)-bis(hydroxymethyl)octadecanonitrile. Identification of the products is made by I.R., NMR and GC-MS. EXAMPLE IV Thermoplastic and thermosetting polymers are prepared as shown in the Table. TABLE I NCO Terminated Prepolymer Curative Split tear 1 equivalent 0.95 equivalent in psi A. BHON/PM 1000 BHON/80 1344 (9.27) 4:1 MDI 1:2 B. BHON/PM 1000 1,4 BD/BHON/C-20 triol 1288 (8.88) 4:1 MDI 8:2:1 *Figures in brackets are in MPa These products show exceptional split tear strength. BHON is used to indicate 9(10) gem-bis (hydroxymethyl) octadecanonitrile. MDI is methylene diisocyanate and PM 1000 is PolyMeg 1000 a polyoxytetramethylene glycol. The ratios are in equivalents. BD indicates 1,4 butane diol and C-20 triol is 9(10)gem-bis(hydroxymethyl) octadecanol. A is a thermoplastic elastomer and B is thermosetting elastomer.

Claims: CLAIMS 1. Polyhydroxymethyl compounds of formula I CH3 (C H2) m [C (CH2OH)X] (CH2)p [C(CH2OH)X]q(CH2)r[C(CH2OH)X]s(CH2)tCH2M (I) (wherein X represents a hydrogen atom or a hydroxymethyl group; M represents a cyano, ester or N,N-disubstituted amide group, the CH2-M bond being a carbon-carbon bond; m,n,p,q,r,s and t are non-negative integers the sum of which is from 11 to 19; and n,q and s each has the value 0 or 1, the sum of n,q and s being 1,2 or 3; with the provisos that where the sum of n,q and s is 1, X represents a hydroxymethyl group and where the sum of n,q and s is 2 or 3, each group represented by X is the same) and mixtures thereof. 2. Compounds of formula I as claimed in claim 1 wherein M is a cyano group. 3. Compounds of formula I as claimed in claim 1 wherein M is a group -COOR or -CONR2 in which R,-which may be the same or different where M represents an amide group, represents a C14 straight chained or branched alkyl group, optionally substituted by a hydroxyl group, or a phenyl group and where M represents an amide group, the NR2 moiety may further represent a piperidino on morpholino group. 4. Compounds of formula I as claimed in any one of claims 1 to 3 for which at least one of the following conditions is satisfied: (a) the sum of m,n,p,q,r,s and t is from 13 to 17; (b) q is 0 and n and s are each zero; (c) m and t are each 3 or greater; and (d) m and t are each 4 or greater. 5. Compounds of formula I as claimed in claim 1 selected from the following: (a) 9,9(10,10) - bis(hydroxymethyl) octadecanonitrile; (b) 9,9(10,10),12,12(13,13)-tetra (hydroxymethyl) octadecanonitrile; (c) 9,9(10,10),12,12(13,13),15,15(16,16)-hexa(hydroxymethyl) octadecanontrile; (d) 9(10),12(13)-di(hydroxymethyl)octadecanonitrile; and (e) 9(10),12(13),15(16)-tri(hydroxymethyl)octadecanonitrile. 6. A process for the preparation of polyhydroxymethyl compounds of formula I (as defined in claim 1) which process comprises (a) hydroformylating an olefinic compound of formula II. H (CH (CH=CH)b(CH2)c(CH=CH)d(CH2)e(CH=CH)f(CH2)gCH2M (II) (wherein M is as defined in claim 1; a,b,c,d,e,f and g are non-negative integers, the sum of a,c,e,g,2b, 2d and 2f being from 11 to 19; and b,d and f each has the value 0 or 1, the sum of b,d and f being 1,2 or 3) and (b) converting the or each ,CH-CHO group in the product thereby obtained (i) to a CH(CH2OH)2 group by reacting with formaldehyde in the presence of a strong base, (ii) to a CH.CH2OH group by catalytic reduction, or (iii) to a ,C(CHO) (CH2OH) group by reacting with formaldehyde in the presence of a weak base and subsequently to a C(CH2OH)2 group by reduction, subject to the proviso that where the product obtained by the step (a) contains a single formyl group, the conversion of step (b) is effected by process steps (i) or (iii). 7. A process as claimed in claim 6 wherein the hydroformylation of step (a) is performed in the presence of a rhodium based catalyst. 8. A process as claimed in claim 6 or claim 7 wherein the starting compound of formula II is an oleyl, linoleyl or linolenyl compound. 9. Coating and moulding compositions comprising a compound of formula I as claimed in claim 1 or the reaction product thereof with a polyisocyanate. AUSTRIAN CLAIMS 1. A process for the preparation of polyhydroxymethylcompounds of formula I. CH3(CH2)m[C(CH2OH)X]n(CH2)p[C(CH2OH)X]q(CH2)r[C(CH2OH)X]s(CH2)tCH2M (wherein X represents a hydrogen atom or a hydroxymethyl group; M represents a cyano, ester or N,N-disubstituted amide group, the CH2-M bond being a carbon-carbon bond; m,n,p,q,r,s and t are non-negative integers the sum of which is from 11 to 19; and n,q and s each has the value 0 or 1, the sum of n,q and s being 1,2 or 3; with the provisos that where the sum of n,q and s is 1, X represents a hydroxymethyl group and where the sum of n,q and s is 2 or 3, each group represented by X is the same) and mixtures thereof, which process comprises (a) hydroformylating an olefinic compound of formula II CH3 (CH2) (CK=CH) b (CH2) (CH=CH) d (CH2)e(CH=CH)f(CH2)gCH2M (Il) (wherein M is as defined above;a,b,c,d,e,f and g are non-negative integers, the sum of a,c,e,g,2b, 2d and 2f being from 11 to 19; and b,d and f each has the value 0 or 1, the sum of b,d and f being 1,2 or 3) and (b) converting the or each zCH-CHO group in the product thereby obtained (i) to a ,CH(CH2OH)2 group by reacting with formaldehyde in the presence of a strong base , (ii) to a ,CH. CH2OH group by catalytic reduction, or (iii) to a,C(CHO) (CH2OH) group by reacting with formaldehyde in the presence of a weak base and subsequently to a :e ,C(CH2OH)2 group by reduction, subject to the proviso that where the product obtained by the step (a) contains a single formyl group, the conversion of step (b) is effected by process steps (i) or (iii). 2. A process as claimed in claim 1 wherein the hydroformylation of step (a) is performed in the presence of a rhodium catalyst. 3. A process as claimed in claim 1 or claim 2 wherein the starting compound of formula II is an oleyl, linoleyl or linolenyl compound. 4. A process as claimed in either of claims 1 and 2 wherein the starting compound of formula II is a compound for which at least one of the following conditions is satisfied: (a) M represents a cyano group or a group -COOR or CONR2 in which R, which may be the same or different where M represents an amide group, represents a C14 straight chain or branched alkyl group, optionally substituted by a hydroxyl group, or a phenyl group and, where M represents an amide group, the NR2 moiety may further represent a piperidino or morpholino group; (b) the sum of a,c,e,g,2b,2d and 2f is from 13 to 17; (c) b is 1 and d and f are each zero; (e) a and g are each 3 or greater; and (f) a and g are each 4 or greater.

Inventors: ROGIER, EDGAR ROBERT
Applicants: HENKEL CORPORATION
Application year: 1982
Main classification: C07C69
IPC codes: C08G18, C07C69