POLYCARBONATE/POLY(ETHYLENE TEREPHTHALATE) RESIN SOLUTIONS

Abstract: Thermoplastic compositions which are a solution of polycarbonate and poly(ethylene terephthalate) resins. These solutions are produced by melt admixture of a polycarbonate prepared from bis(3,5,dimethyl-4-hydroxy phenyl) sulfone and 2,2-bis(4-hydroxyphenyl) propane and poly(ethylene terephthalate) to provide the composition with a single glass transition point.

Description: POLYCARBONATE/POLY(ETHYLENE TEREPHTHALATE) RESIN SOLUTIONS This invention relates to thermoplastic compositions Λ containing polycarbonate and poly(ethylene terephthalate) resins which are admixed to provide the composition with a single glass transition point (Tg) . 5 The existence of a single glass transition point for such a composition signifies that its resin components are in solution. This state is of great significance for an admixture of different resins, because it insures homogeneity and a unity of properties. These attributes 10 greatly facilitate subsequent processing and the use of the composition. Poly(ethylene terephthalate) resins useful in accordance with the present invention are well known. They are readily available or may be specially formed by 15 condensation of ethylene glycol with terephthalic acid. Resins having intrinsic viscosities of from about 0.50 to 0.80 dl./g. (as measured in phenol/trichlorethylene) are preferred. These resins also include copolymers of ethylene 20 terephthalate with other conventional monomer(s). Thus, for example, the resins may include a proportion of other glycols, dicarboxylic acids ' (desirably aromatic), hydros carbon (desirably saturated) alcohols and similar modifiers Preferably, however, at least 65%, more preferably 85% 25 by weight of the resin is composed of ethylene terephthalate units. Polycarbonates useful in accordance with the present invention are likewise well known and any may be employed. ' Intrinsic viscosities of from 0.40 to 0.80 dl/g (as 30 measured in phenol/trichloroethylene) are preferred. This resin may be formed from hydrocarbon bisphenol monomer, ordinarily by condensation with a carbonate precursor such as carbonyl chloride. Resins formed from 2,2-bis(4-hydroxyphenyl) propane and bis(3,5-dimethyl- r Q Pi 4-hydroxyphenol) sulfone (referred to as bisphenol or bisphenol A and sulfone or diphenyl sulfone, respectively) are particularly preferred. In a preferred embodiment, for example, copolymer is formed from diphenyl sulfone as .. described in U.S. Patent 3,737,409 of Fox. For these copolymers, a mole or unit ratio of bisphenol to sulfone of 1:99 to 99:1, more preferably of 1:5 to 5:1, is desirable. The preferred diphenyl sulfone for these resins is bis- (3,5-dimethyl-4-hydroxy-phehyl) sulfone, which may be formed from 2,6-xylenol. In the present compositions, the proportions of the polycarbonate and poly(ethylene terephthalate) resins may vary widely. Each is commonly present, for example, in an amount of from about 1 to 99%, more normally about 20 to 80%, by total resin weight. While conventional non-polymeric additives may be present as discussed below, these compositions ordinarily do not contain other polymeric components because they may not dissolve in the resin solution. The resin admixtures may be achieved simply by melt mixing the components. This step is normally performed at a temperature about 300°C. for at least about 5 minutes. After melt mixing, a single glass trnasition point differnt from those of the individual resin components will be observed. This single point reflects the production of a homogeneous resin-solution. Once formed, the product composition may be employed (or further processed) in conventional manner. Its applications include, for example, tough films useful in packaging. .It may also be injection molded to produce a variety of useful thermoplastic articles. In addition to its two polymeric components, the present compositions may contain any of the conventional non-resin additives for the purposes for which they are known. These additives include fire-retardants, pigments, reinforcing materials such as glass fibers, and the like. OMPI - 3 - They may be combined with_the compositions either before or after melt mixing. The following examples are given by way of illustration only and are not intended as a limitation on the scope of this invention. Many variations are possible without departing from its spirit and scope. Unless otherwise specified herein, all proportions are provided on a weight basis. • EXAMPLE 1 A poly(ethylene terephthalate) is admixed with 45% by total resin weight of polycarbonate resin formed from dixylenol sulfone and bisphenol A in a mole ratio of 1:4. This admixture is melt mixed at a temperature of about 325°C for 30 minutes in a Brabender mixing bowl. The composition and comparative properties of the resultant prpduct are as follows: Polycarbonate Poly(ethylene terephthalate) Composition I.V. - 0.61 I.V. = 0.72 I.V. - 0.52 T , > 172 -c ig - {ii:z it™_- _t_L> τ s = i08 ' c The resolution of the distinct glass transition points of the two component resins to the single point for the melt admixed composition shows formation of a homogeneous resin solution. EXAMPLE 2 The process of Example 1 is repeated substituting 50% by weight of a polycarbonate having a 1:1 mole ratio of sulfone to bisphenol. The comparative results after melt admixture at 325°C for 5 minutes are as follows: Polycarbonate Pol (ethylene terephthalate) Composition I.V. - 0.48 I.V. = 0.72 I.V. * .46 Ig - 202-C Tg - {gig &£_££ ) Tg - 120-C " -EXAMPLE 3 The process of Example 1 is repeated substituting 45% by weight of a polycarbonate having a 3:1 mole ratio MP of sulfone to bisphenol. The comparative results after melt admixture at 325°C for 10 minutes are as follows: Polycarbonate Poly(ethylene..terephthalate) - Composition I.V. = 0.58 I.V. . - 0.72 I.V. - .48 Tg - 227-C Ig -{! 8$1°C ■ (&cr£ys£tal!l&in-e . ,) T * - 117' EXAMPLE 4 A poly(ethylene terephthalate) is admixed with 50% by total weight of polycarbonate resin formed from diphenol sulfone and bisphenol A in a mole ratio of 1:1. This admixture is melt mixed at a temperature of 270°C for 3-5 minutes in a 1 inch single screw extruder. The composition and comparative properties of the resultant product are as follows: Polycarbonate Pol (ethylene terephthalate) Composition I.V. - 0.58 I.V. - 0.72 I.V. - 0.54 Ig = 202 *0 Ig - ξj:<j T * " 103 ° C EXAMPLE 5 The process of Example 4 is repeated substituting 40% by weight of a polycarbonate having a 1:1 mole ratio of sulfone to bisphenol. The comparative results after extruding are as follows: Polycarbonate Poly(ethylene terephthalate) Composition I.V. - 0.58 I.V. - 0.72 I.V. = 0.60 τ _ _ on o n . — / ^ 67°C (amorphous) τ _ Q7 o r Tg - 202 C Tg - ^ 81 o c ( crystalline ) Tg - 97 C EXAMPLE 6 The process of Example 4 is repeated substituting 90% by weight of a polycarbonate having a 1:1 mole ratio of sulfone to bisphenol. The comparative results after extruding are as follows: Polycarbonate Poly(ethylene terephthalate) Composition I.V. - 0.45 I.V. = 0.72 I.V. = 0.41 ~ _ 1Q - 7 τ „ _ 67°C (amorphous) τ _ 1fiq o r Tg = 197 Tg - * ( 81 . c (crystalline) Tg " 169 C ^-£ΪJRE_ f OMPI Polymer Synthesis The DXS/BPA polycarbonates described in the foregoing examples were prepared employing interfacial polymeriza¬ tion in which a rapidly stirred two phase mixture of _ 5 aqueous caustic, polymer solvent, bisphenols, a phase transfer catalyst, and monofunctional chain terminators is phosgenated. The growing polymer dissolves in polymer solvent, unreacted bisphenols dissolve in the aqueous caustic phase and the polymer forms at the interface. 10 The applicable technology of the synthesis of polycarbonates is described in "Chemistry and Physics of Polycarbonates" by H. Schnell (Interscience,.1964) . The polymer is isolated by precipitation in methanol and dried. 15 All of the foregoing patents and/or publications are incorporated herein by reference. Obviously, other modifications and variation of the present invention are possible in the light of the above teachings. It is, therefore, to be understood that changes may be made in 20 the particular embodiments of the invention described which are within the full intended scope of the invention as defined by the appended claims. .

Claims: - 6 - • CLAIMS .1. A thermoplastic composition comprising polycar¬ bonate and poly(ethylene terephthalate) resins which have been melt admixed to provide said composition with a single glass transition point. 2- The composition of Claim 1, wherein the polycarbonate is from about 1 to 99% by total resin weight. 3. The composition of Claim 2, wherein the poly(ethylene terephthalate) is from 1 to 99% by total resin weight. 4. The composition of Claim 3, wherein the agent is less than about 10,000 ppm by total resin weight. 5. The composition of Claim 1, wherein the polycar¬ bonate contains units derived from diphenyl sulfone monomer. 6. The composition of Claim 5, wherein the polycarbonate contains units derived from hydrocarbon bisphenol. 7. The composition of Claim 6, wherein the diphenyl sulfone and hydrocarbon bisphenol units are in a mole ratio of from about 1:99 to 99:1. 8. The composition of Claim 1, wherein the polycarbonate is formed from hydrocarbon bisphenol. 9. The composition of Claim 8, wherein the hydro¬ carbon bisphenol is 2,2-bis(4-hydroxyphenyl) propane.

Inventors: FOX DANIEL WAYNE, PETERS EDWARD NORMAN, SMITH GARY FRANCIS
Applicants: GEN ELECTRIC, GENERAL ELECTRIC CO
Application year: 1982
Main classification: C08L69
IPC codes: C08L67, C08L69