BODY IMPLANTABLE LEAD

Abstract: Body implantable lead (10) having a polymer-based gel electrode (13).

Description: BODY LMPEANTAPLE LFAD I. DESCRIPYION Background of Prior Art Electrical stimulation of the body for medical pur- poses is well known in the prior art. An example of a device for this purpose is the well-known cardiac pacemaker. In the pacemaker context, as well as other body stimulation contexts, the stimulation is delivered to the desired body site by an electrode component of a lead. A variety of body implantable electrical leads for the delivery of electrical stimulation energy to a desired body site are known in the prior art. Recent years has seen increased usage of transvenous leads which can deliver the stimulation energy to the desired body site while significantly lowering patient risk and morbidity. For example, the use of a transvenous/endocardial lead eliminates the necessity of a thoracotomy while delivering stimulation energy to tize heart to provide a pacemaicing function. Such implantable leads may be used for sensing as well as stimulating. In many stimulation and sensing contexts, maintenance of a reliable electrical contact at the desired electrode site has proven difficult. Interactions between the lead and the body at the contact site can vitiate the desired effects of the stimulation. For example, material reactions may encourage fibrosis. In the pacemaking context, fibrosis is believed to be a major factor in the increase in chronic threshold that is usuelly experience@ mechanical trauma may result in inflammation of the tissue to be stimulated. Such inflammation may alter tile response of the tissue to the stimulation energy, both acutely and chronically. In chronic use of such leads, it has been observed that tile contractions of the heart against the lead and the mechanical pressure applied against the heart by the lead ry traumatize the contacted tissue. The traumatize tissue - y form scar tissue around the electrode (s) to reduce the stress placed upon the endocardium below the tissue damage limit. In chronic experience, it is observed that the threshold currents sufficient to stimulate the heart increase as the scar tissue is formed until the thickness of the scar tissue stabilizes. The required energy to stimulate the heart is thereby increased because of the additional potential drop across the nonresponsive cardiac cells. A discussion of this mechanisra in conjunction with the'realization of optimum electrode surface area appears in the paper entitled "Comparison of Power Sources for Advanced Pacemaker Applications" by Rasor, Spickler and Clabaugh, Proceedinges of the Seventh Intersociety Energy Conversion-Engineering Conference, January 1972, pages 752-760. Other interactions, such as electrochemical and polari- zation effects, between the lead and body tissue at the contact site, can result in the occurrence of undesirable events. In some circumstances where electrical stimulation of body tissue is indicated, the tissue portion to be stimulated is irritable. The placement of a pacemaking lead in such a case may induce a cardiac arrhytiimia. The presence of the lead may also promote thrombus formation. Pressure-induced trauma are thought to be the leading cause' of enlarged fibrotic encapsulation of the electrode tip. Cardiac tissue is also occluded under the tip and deprived of access to oxygen and other nutrients carried by the blood while also being deprived of the ability to transfer waste products from the tissue into the bjood. A large number of tissue cells are so occluded by existing endocardial electrode tips. Cells of heart tissue must corrunicate with the blood in the ventricles of the heart by. way of diffussion due to the lack of capilaries near the endocardial surface. The interactions noted above have long been recoc- nized and efforts have been made to ameliorate their consequences. For example, leads have been configured to reduce mechanical trauma and the response of irritable tissue during lead placement. Matarials have been selected for the lead body and electrodes to minimize fibrosis. Thrombus formation may also be countered by the administration of suitable druge. The administration of drugs to counter the undesir- able interactions between the lead and body noted above nas not gained widesread acceptance in that it bas heretofore required a systemic treatment to counter a localized interaction. Also, lead configuration must take into account other factors such as the efficiency of the delivery of the stimulation energy, the ease of lead place ment, maintenance of the desired electrode position and reliability of the lead over extended periods Or time. An accommodation of these interests ;ias resulted in leads whose configuration necessarily results in undesirable interactions between the lead and body. One way to avoid the waste of energy due to polarization effects has been described by Parsonnet et al, "Clinical Use Of A New Transvenous Electrode", Ann. -A.Y. Acad. Sci., Vol. 167: 756, 1969. This article describes what is termed a "Differential Current Density Electrode". In this system there is a low current density at the metal electrode to avoid polarization and a high current density at the contact to tissue to produce a significant field strength to activate responsible cells. As a result, stimulation thresholds were found which were lower than that of conventional metal electrodes. Brief Summary of the Invention This invention provides a non-@etallie repiacement electrode for the noble metal or other petal eleotrodes used heretofore in implantable leads. The replacement electrode comprises a conductive polymer which may be cast to shape or formed in situ. The polymer electrode avoids the polarization phenomena associated with metal electrode in a conductive fluid as is encountered in living bodies. The electrode of t:e invention provides a transition zone wherein it is believed the coversion of electron flow to ionic flow occurs i.e., the Helr'holtz layer. With metal electrodes, the Helmholtz layer is external to the electrode and is such that cells in its vicinity are disrupted or destroyed. With the polymer electrode of the invention a transitional synthetic layer is provided in the electrode where this reaction can take place. Significant advantages of the invention are: reduced tissue trauma; use of inexpensive gel electrode rather than expensive precious metal electrodes; improved electrode tissue interface, mechanically, chemically and electrically; use of non-corroding electrode material, improved sensing due to low polarization, improved capture efficiency, lower thresholds, lower current drain, and protection of the living cells from any electron/ion conversion reaction. Specifically then, the present invention provides implan table leads having conductive electrodes based on polmer gels which ameliorate the effects of undesirable interactions between the lead and the contacted tissue. This is accomplished by providing, as the electrode, a body of soft, compliant, water swellable, polymeric, water insoluble material non-toxic to body tissues and fluids. The material preferably consists essentially of a hydrogel which is ionically conductive. The hydrogel is permeable to water, oxygen, CO2 and the like so as to allow their diffusion through the cushioning body both to and away from the occluded tissue cells at the contact site. The,water-permeable hydrogel body is permeable to water. It is ionically conductive thereby providing electrical contact between the metal electrode and the tissue Brief Description of the Drawings Figure 1 illustrates a portion of a body implantable lead constructed in accordance with the preferred embodi- ment fthe present invention. Figure 2 is an end view of the body implantable lead shown in Figure 1. Figure 3 is a schematic showing of an electrode for a bipolar lead. Detailed Description of the Inven@ion The concert of using a conductive polymer gel as the stimulating and sensing medium in an implantable transvenous lead, particularly in a cardiac pacing leat, from considerations of the electrochemistry at the elec- trode/tissue (electrolyte) interface. The charge carriers in metal are electrons whereas charge is carried by ions in electrolyte solutions. When metal is immersed in an el&num;ctrolyte, charge flows from one phase to another until the electrochemical potentials of the metal and electrolyte phases are equal. This results in the build-up of a layer of charger called the Helmholtz layer, around the surface of the electrode. This phenomenon is termed polarization and results in a dissipative energy loss that shortens pulse generator battery life and also makes sensing difficult. Electrochemical reactions may also result in corrosion of the electrode metal. In addition to the detrimental effects of the Helmholtz layer on device operation, there is some question as to whether the chronic presence of a charge layer near the tissue causes myocardial or endocardial pathologic processes. For example, the Helmholtz layer may cnronically alter the local pH in the vicinity of the electroae. The chronic imbalance of charge may affect the membrane proper ties such that changes in myocardial or endocardial cell depolarization threshold occur. Because of the known, as well as the unknown or speculative, effects attributable to the Helmholtz layer, the gel electrode of the invention is proposed as a solu tion for, among other things, minimizin- these adverse consequences of polarization. Because the metal electrolyte interface in the gel electrode design is removed from the near vicinity of the tissue, the Helmholtz layer is believed to be encapsulated in the gel. Since charge transport is by ionic movement in the gel, the ions can diffuse into and out of the gel freely, presumably a charge layer is not established at the surface of the ge at which tissue contact is established. Improved sensing and lewer stimulation thresholds result from the combined effects of elimination of the Helmholtz layer and mini- mizing charge imbalances in the vicinity of the myocardial cells. Referring now to'Figures I and.2, there is illustrated a body implantable lead constructed in accordance with the present invention. The lead body, designated 10, is comprised of a coiled, flexible conductor 11 and an overlying sheath 12. Coiled, flexible conductor 11 may be of any known design and preferably has a central aperture which will accept a stylet (not shown) to provide stiffness during lead placement, in known manner. The lead body may also be non-linear such that stylet insertion will straighten the lead body to facilitate transvenous place ment, also in known manner. To facilitate the flexibility requirements of the present invention as well as for reliability considerations, flexible conductor 11 may be a multi-filar member; Conductor 11 is in electrical communication with a polymer gel electrode 13 by means of a metal crimp-sleeve 14 and a source of stimulation energy (not shown) for the delivery of stimulation energy to a desired body site. Sheath 12 may be a preformed tubular member, preferably of a body compatible polyurethane, to overlie conductor 11 and provide electrical insulation therefor, in known manner. Also, as is known, lead body 10 may be tined as indicated at 15. In the prior art, many lead bodies are formed of a molded silicone. A preferable material for sheath 12 and lead body 10 is a body-compatible polyurethane. Such polyurethanes meet the flexibility requirements of trans venous leads and are typically less thrombogenic than silicone and more resistant to tearing and eutting. In general, the physical characteristics of polyurethane are irrore suited to transvenous leads than those of silicone, although silicone or any other body compatible ma- terial may be employed in practicing the present invention. Polymer gel elecrrode 13 may be provided in varion configurations. It 'ray be pre-cas- & or polymerized in situ, as desired. In the erLOodiment shown, lead 'body 10 defines a cavity which contains polymer electrode 13 with a rounded end portion thereof extending through the open aistal ec of the lead body. The rounded end provides electrical contact between living tissue and lead means 11. A wide variety of lead configurations, including bipolar as well as unipolar, and electrode body oonfigura- tions consistent with the tissue contacting requirements of the lead may be utilized. A ring-electrode for a bipolar lead is illustrated in Figure 3 which includes a second lead means 16 and a band 13 of polymer gel forming an electrode. Electrode body 13 may consist of any conductive polymer gel. However, it preferably consists essentially of a hydrogel thick enough to accomodate the Helmholtz layer. Typically, thicknesses i.e., the dimension of body 13 extending out of the lead body, will range from about 0.5 rtrn to about 1.0 rnn. Such electrode body has been found to provide low mechanical trauma and high electro chemical interzace with endocardial tissue. Hydrogels of the invention are ionically conductive, soft, compliant, water swellable and inert to body tissues and fluids. Body 13 is also ionically conductive and permeable thereby establishing electrical communication between lead means 11 and the contacted tissue as well as providing a diffusion path to and away from the occluded tissue site. Gererally speaking, a hydrogel having the properties above described will comprise a coherent, three-dimensional polymeric network capable of imbibing water without dis solving. Usually, insolubility in water is provided by Incorporating a crosslinked structure in the polymer. Hydrogels or water-containing gels may be comprised of water and various chemical substances including gelatin; polysaccharides, crosslinked acrylamide polymers ; hydroxy ethylvethacrylate polymens ; crosslinked polyhydroxyethylacrylate ; polymerized, crosslinked 2-acrylamide-2-mathyl Profane sulfonic acid or one of its salts such as the sodium or potassium type ; crosslinked polyvinylpyrrolidone ; polyacrylic acid ; copolymers of the aforementioned monomers with each other, and copolymers of the afore;mentioned rronor:ers with other monomers such as styrene or other non-hydrogel forming monomers Hydrogels of low conductivity may be made conductive for purposes of this invention by incorporating salts such as sodium chloride or potassium chloride and like electrolytic salts in the hydrogel. This is easily accomplished by dissolving a salt in a monomer-water-initiator soluclon and polymerizing. Other methods of preparation may also be used. The specific preferred hydrogels are crosslinked polyacrylamide and crosslinked polymerized 2-acrylamido-2methylpropane sulfonic acid or one of its salts. Volume 15, pages 273-291 of the Encyclopedia of -Polymer- Science Technology (1971), John Wiley Publishers, provides a section entitled HYDROGELS which describes the preparation of a variety of water-mbibing polymers. The content thereof is incorporated herein by reference. EXAMPLE - Polyacrylamide Hydrogel The following ingredients were dissolved in 52.5 grams of deionized water: 40.0 grams acrylamide, 2.0 grams sodium chloride, 8.0 cc of a 1% aqueous solution of methy- lene-bis-acrylamide. Nitrogen was vigorously bubbled through the resultant solution for 2.5 minutes. The following reagenas were added to the solur stirring: 0.5 cc of a .382 solution of potassium bisulfite, 0.5 cc of a .38% solution of potassium persulphate, and 0.5 cc of a .24% solution of ferrous sulfate. A portion of the res'ee ure was withdrawn intn, a syringe and ejected into the, cavity of electrode tip 13 under a nitrogen atmosphere. The mixture was cured to form the hydrogel by allowing it to stand under the nitro- gen atrosphere at room temperature until solidified. It is to be understood that, within the scope of the appended claims, the invention may be practiced otherwise than as specifically described. WHAT IS CLAIMED IS:

Claims: II. CLAEMS 1. A body implantable lead of the type including a lead body, the exterior of the lead body being comprised of insulating material; a body of conductive polymer gel carried by the lead body for providing electrical contact between the body implantable lead and living tissue, and electrical lead means extending through the lead body and interiorally connected to the polymer gel body. 2. A body implantable lead of the type including a lead body having a distal end, the exterior of the body being comprised of insulating material; a body of conductive polymer gel carried at the distal end of the lead body for providing electrical contact between the body implantable lead and living tissue, and electrical lead means extending through the lead body and interiorally connected to the polymer gel body. 3. A body implantable lead of the type including a lead body having a distal end, the exterior of the lead body being comprised of insulating material, the body defining a cavity having an opening at the distal end thereof; a body of conductive polymer gel contained in the cavity with a portion thereof extending through the cavity opening for providing a lead contact surface for contacting living tissue, and electrical lead means extending through the lead body and interiorally connected to the polymer gel body. 4. The lead or any of one preceding clai'.s- 1 2 2 or 3 wherein the lead is of the transvenous type. 5. The lead of any of the preceding claims 2 or 3 wherein the tissue contacting portion of the polymer gel body defines a rounded configuration. 6. The lead of any of the preceding claims 1, 2 or 3 wherein the polymeric gel consists essentially of a hydrogel. 7. The lead of claim 6 wherein the hydrogel includes a crosslinked polymer. 8. The lead of claim 6 wherein the hydrogel includes a copolymer. 9. The lead of claim 6 wherein the polymer is an acrylamide. 10. The body implantable lead of claim 9 wherein the acrylamide polymer is crosslinked. 11. The body implantable lead of claim 6 wherein the hydrogel includes a methylacrylate polymer. 12. The body implantable lead of claim 6 wherein the hydrogel includes a crosslinked ethylacrylate polymer. 13. The body implantable lead of claim 6 wherein the hydrogel includes a crosslinked polymer of 2-acrylamido-2methylpropane sulfonic acid or one of its salts. 14. The body implantable lead of claim 13 wherein the polymer is a copolymer. 15. The body implantable lead of claim 6 wherein the hydrogel includes a crosslinked vinylpyrrolidone polymer. 16. The body implantable lead of claim 6 wherein the hydrogel includes a copolymer. 17. The body implantable lead of claim 16 wherein the copolymer is comprised of at least two copolymerized hydrogel-forming monomers. 18. The body implantable lead of claim 16 wherein the copolymer is comprised of at least one hydrogel-forming monomer and one non-hydrogel-forming monomer copolymerized together.

Inventors: CAHALAN, PATRICK T., COURY, ARTHUR J., JEVNE, ALLAN H., JUNCKER, DAVID F., KALLOK, MICHAEL J.
Applicants: MEDTRONIC, INC.
Application year: 1982
Main classification: A61N1
IPC codes: A61B5, A61N1