PROCESS FOR PREPARING EPOXY RESIN/PHOSPHORIC ACID REACTION PRODUCTS

Abstract: A process for preparing epoxy resin/phosphoric acid reaction products wherein a polyol polyether epoxide is reacted with a phosphoric acid source material and water in a reaction medium. The reaction product may optionally be salified with a base and diluted with water. The process is characterized by (1) employing as the acid source material one derivable by the reaction of a hydroxylic (P-OH)-blocking agent with (a) P4O10, (b) a reaction product of P4O10 with less than six molecular proportions of water or (c) an adduct of (b) with some of the oxirane groups in the epoxide, (2) employing as the reaction medium a hydrophilic solvent for the epoxide which is acceptable as a component of a coating composition, (3) phosphorylating the epoxide by reacting P-OH groups in the acid source material, effectively in the absence of free water molecules, with oxirane groupes in the epoxide until the content in the reaction mixture of species indistinguishable from H3PO4 by titration drops to a preselected level and then (4) subjecting the resultant reaction product to hydrolysis until the content in the reaction mixture of oxirane-derived phosphomonoester groups rises to at least a preselected value. These reaction products are useful in coating compositions.

Description: PROCESS FOR PREPARING EPOXY RESIN/PHOSPHORIC ACID REACTION PRODUCTS The preparation of epoxy resin/H 3 P0 4 reaction products which when amine-salified have utility as water-borne film-forming materials is disclosed in U.S. Patent 4,289,812. In the preferred version of the disclosed process, about 1 part by weight of E PO-, is reacted, in the form of the 85% acid for about 4 hours with 100 parts by weight of a nominally difunctional epoxy resin which is a copolymer of bisphenol A with it.ε diglycidyl ether and has an epoxide equivalent weight (EEW) of between 1500 and 2000. The reaction is carried out in a rela¬ tively hydrophobic solvent for the resin, such as an acetone/methylene chloride mixture, which does not strongly solvate the acid or water and results in the formation of phosphate ester groups comprising from one to three epoxide residues each. This is accompanied by hydrolysis of higher ester to monoester groups and concurrent formation of terminal glycol groups on the cleaved-off resin molecules. Acid catalyzed, direct hydrolysis of oxirane groups to glycol groups also occurs to a limited extent. Gft.:-! The reaction mixture is mixed with water and triethylamine added in excess. The solvent and unsali- fied a ine is then stripped off to yield an aqueous dispersion of the amine-salified product resin having a solids content of about 50 wt. %. For efficient operation of the foregoing process on a plant scale, it must be carried out in a continu¬ ous manner and the recovered solvents and amine sepa¬ rated and recycled. This necessarily requires a rela- tively complicated plant installation incorporating separate vessel, pump, line and control instrument assemblies for each of several stages, i.e., reaction, water and amine addition, stripping and separation stages. It is thus evident that a simpler process, requiring a less complicated and costly plant instal¬ lation, would be highly desirable. Also, a reduction in the reaction time would be desirable. * An important application of the coating resins made in the foregoing manner is as sprayed-on, beverage can interior coatings. For this use, the aqueous resin dispersion is formulated with certain coupling solvents, such as, for example, n-butanol or glycol monoethers, which are high boiling but readily volatilized at the temperatures required with curing agents such as, for example, melamine resins, to cure the coatings. Examples 11, 18 and 20 in the above-referred-to U.S. patent disclose such formulations comprising glycol monoethers and said patent also teaches that glycol ethers are suitable media for the epoxide/phosphoric acid reaction. Also, U.S.P. 4,059,550 discloses the use of the monobutyl ethers of ethylene and diethylene glycols as media for such reactions and the use of the -βlJRHAl/ MPI resulting solutions including an organic base as cata¬ lysts in multi-component resin systems. Thus, the possibility of eliminating the need for solvent removal from the reaction mixture formed in the above-described process, by utilizing a formulation solvent as the reaction medium, was considered^ an implicit assumption being that the amount of solvent required would not be such as to result in an unaccept- ably high solvent-to-water or solvent-to-solids ratio for the contemplated application. That is, because the solvent would not be removed, a high enough solids content must be attainable in the reaction mixture so that the solids level after dilution with water and/or any other solvents in the final formulation will still be adequate for the requisite mode of application and the essential film-forming properties of the coating formulation. Also, the content of volatilizeable organic components (VOC) in the final formulation would have to be low enough not to result in an unacceptable level of emissions in the curing step. The matter of reaction mixture viscosity at adequately high solids levels is also of concern with regard to stirring power requirements. The onobutyl ether of ethylene glycol, hereinafter referred to as EB, was tried as the medium for reactions of 1 part by weight of H 3 P0 4 (as 85% aq. E PO^) with 100 parts by weight of an epoxy resin represented by the following ideal formula, n having a value therein of from 12 to 14, R, being H and Q being the nucleus of bisphenol A: ( I ) The reactions were carried out under the condi- 5 tions known to be suitable when acetone/methylene chloride is employed as the reaction medium. The free H 3 P0. content of the reaction product was found to be low enough for applications not posing stringent water- -resistance requirements but undesirably high for can 10 coatings to be subjected to conditions commonly employed for pasturization. Correspondingly lower phosphomonoester contents were also experienced. These results were believed due to greater retardation of the adduction reaction than of the hydrolysis reactions, as 15 a consequence of differences in acid and water solva- tion effects by the hydrophilic reaction medium employed. * This was despite the fact that the solvent only constituted about 40 wt. % of the initial reaction mixture with 60% being solids or non-volatiles. 20. At this point, the use of an anhydrous form, 100% or higher, of phosphoric acid, which is taught as an operable option in U.S. Patent 4,289,812 was considered, as this would permit the phosphorylation step to be carried out in the absence of water. However, Example 10 25 is the only example in said patent using pyrophosphoric acid as such an acid source material. It discloses that gelling of the reaction mass occurred, requiring excessive dilution with more of the dioxane solvent in order to have a stirrable mixture, which is essential to usefully rapid, subsequent hydrolysis of phospho- polyesters and any residual P-O-P groups. The rapid development of a very high viscosity observed in the absence of concurrent hydrolysis is believed attributable primarily to formation of esters by adduction of two or three oxiranes per p=0 moiety, which occurs even if 100% H 3 P0 4 containing essentially no P-O-P groups is used as the acid. U.S.P. 2,541,027 discloses monoalkylorthophosphates as an alternative to the use of H 3 P0. in preparing adducts with epoxy resins. This was considered as a way of attaining some reduction in the number of long- chain branches per phosphopolyester group, thereby reducing the viscosity of the reaction mixture. However, this would also result in introduction of not neces- sarily desirable or readily hydrolyzed alkyl groups in the product resin. Furthermore, it was not apparent that excessive amounts of solvent would not still be required. Consideration was also given to the use of dialkyl orthophosphates as the acid, but this would result in triesters containing two alkyl groups not necessarily desirable or more readily hydrolyzed than the _>PO-OC- group formed by P-OH/oxirane adduction, thus posing the problem of whether the PO-OH required for salification could be formed without cleavage of the latter PO-OC group. A substantial reduction in the adduction rate would also be anticipated, at a given P/oxirane reactant ratio. - y*ic-A U OMPI The prior art itself does not contemplate a one-pot process or address itself to the problems inherent in attempting to use a formulation solvent as the reaction medium for preparing H 3 P0 4 /epoxide adducts of high phosphomonoester contents and low free acid contents. Neither does it make obvious a solution to those prob¬ lems. However, the process of the present invention, as defined in the following summary, does provide such a solution. The invention is an improved process for preparing epoxy resin/phosphoric acid reaction products. These products can be prepared having high enough phosphomono¬ ester contents to be water-dispersible as base salts and low enough free acid contents to yield water- -resistant cured coatings. The phosphoric acid is provided as an acid source material derivable by the reaction of a hydroxylic P-OH functionality-limiting agent blocking agent with phosphoric anhydride as such or as a reaction product thereof with less than six molecular proportions of water. A resin solvent, which may also function as the P-OH blocking agent but other¬ wise is inert and acceptable as part, of the final coating resin formulation, is employed as the reaction medium. The epoxide/acid reaction is allowed to proceed, effectively in the absence of water, until the content in the reaction mixture of species indistin¬ guishable from H 3 P0 4 by base-titration has dropped to a minimum. Then enough water to hydrolyze the phospho- polyesters present is added and the hydrolysis is carried out, thereby cleaving the ester groups formed from the blocking agent and generating the P-OH groups needed for salification. Optionally, the product can be salified and diluted with water in situ. The product can also be employed as produced as a nonaqueous solution. The above materials and procedures are essential to a one-pot mode of operation but the advantages of the process are not otherwise limited to that mode of practicing the invention. More precisely, the present invention is defined as a process for preparing epoxy resin/phosphoric acid reaction products wherein a polyol polyether epoxide is reacted with a phosphoric acid source material and water in a reaction medium, the reaction product may optionally be salified with a base and diluted with water, characterized by: (1) employing as the said acid source material one derivable by the reaction of a hydroxy¬ lic (P-OH)-blocking agent with (a) ^ A O-, Q , (b) a reaction product of P 4 O 10 with less than six molecular proportions of water, or (c) an adduct of (b) with some of the oxirane groups in the epoxide, (2) employing as the reaction medium a hydrophil- lic solvent for the epoxide which is accept¬ able as a component of a coating composition, • (3) phosphorylating the epoxide by reacting P-OH groups in the acid source material, effec¬ tively in the absence of free water molecules, with oxirane groups in the epoxide until the content in the reaction mixture of species indistinguishable from H 3 P0 4 by titration drops to a preselected level and then (4) subjecting the resultant reaction product to hydrolysis until the content in the reaction mixture of oxirane-derived phosphomonoester groups rises to at least a preselected value. It is not to be inferred that the acid source material must actually be derived by reaction of 4 °ιo with water and/or the blocking agent. It is only necessary that the acid source material be at least theoretically so preparable. Acid source materials which meet this requirement but have actually been made from other r actants are not ruled out. The term effectively in the absence of free water molecules is not intended to exclude the small amounts, such as a total of up to about 0.5% in some instances of water frequently present in the epoxide resins and those commercial solvents which may be employed as blocking agents or reaction media. However, it does emphasize the desirability of water contents approach¬ ing zero, which is a practical impossibility. * The reaction medium may also function as the P-OH blocking agent and does not necessarily have to be water-miscible in order to be acceptable as a component of the coating composition. The formula is intended to denote the actual composition of phosphoric anhydride, commonly referred to as phosphorous pentoxide and loosely represented as P 2 O 5 . The term free H-PO. includes other phosphorous acid species indistinguishable from H 3 P0 4 by titration, such as O 0 II it (H0 ) P - O - P " N group-comprising acids present as the result of equili¬ bration between P-O-P -consuming and -forming reactions with water and the blocking agent. Suitable epoxides for the practice of the present invention include polyol, polyether epoxides which can be represented by either of the following formulas I and II: (I) or wherein Q, independently, in each occurrence, is n is an integer of from 0 to 40, r is zero, 1 or 2 and, independently in each occurrence; R is H, methyl or ethyl, R 2 i.s -Br, -Cl or a C-. to C 4 alkyl or alkenyl group, R 3 i..s a C 1 -C 4 alkylene or alkenylene group. ^.C(CF 3 )2, -CO-, -S0 2 ~, -S-, -O- or a valence bond, R is -Br, -Cl or a C-, to C 4 alkyl or alkenyl group; and R is H or alkyl of 1 to 12 carbons. The most preferred epoxides are those of formula I wherein n is from 5 to 16, Q is a bisphenol A residue and R is H. Suitable phosphoric acid source materials are those derivable by the reaction of the hydroxylic blocking agent with either -P 4 0 10 as such or with reac¬ tion products of -P 4 0 10 with less than 6 molecular proportions of water. That is, if the blocking agent is to be reacted with a pre-formed hydrate of aP 4 0 10 ' that hydrate must be a partial hydrate, i.e., a con¬ densed orthophosphoric acid having an acid content greater than 100%. In other words, P-O-P groups must be available to react with the hydroxyl group in the blocking agent. EB, for example, exhibits essentially no reactivity with P-OH groups under comparable conditions. It is believed that suitable acid source materials can also be formed by first reacting the P-OH groups in the condensed acid with oxiranes in some of the epoxide molecules and then introducing the blocking agent to react out the P-O-P groups in the adducts. This pre¬ sumes that the solvent in which the epoxide is dissolved is itself not reactive with P-O-P groups and depends on the use of an amount of the acid which provides a relatively low ratio of P-OH to oxiranes. Even then, this reaction.,sequence is considered likely to result in gelling unless a low molecular weight epoxide is used and the percent solids is as low as is acceptable on the basis of other considerations. When water is to be incorporated in the acid source material, this can be done by reacting ? Λ 9- > Q first with less than 6 molecular proportions of water and then with the blocking agent hydroxyls, or vice versa. In the latter case, however, either the number of hydroxyls provided by the blocking agent must be less than six per -P 4 0 10 or the amount of water supplied must be limited to that which can be essen- tially completely consumed by hydrolysis of the phospho- triesters produced in the initial reaction to phospho- diesters. That is, the presence of free molecules of either water or H 3 P0. other than in equilibrium amounts is to be avoided, at least in effect. The acid source material may be pre-formed, i.e., in the absence of the epoxy resin, or may be formed in situ, i.e., in the presence of the resin. When the reaction medium or a component thereof also functions as the blocking agent, it is particularly convenient to take the latter tack; that is, to add ?_± -, Q or a partial hydrate thereof to a pre-formed solution of the resin in the reaction medium. Contrary to what was feared, it was found that this did not result in homopolymeri- zation of the epoxide to any substantial extent. However, in situ formation of the acid source material requires more intense agitation upon scale-up of the reaction, in order to avoid the presence of P-O-P group-containing acid materials when the hydrolysis step is initiated. Also, higher temperatures may be necessary in >rder to hold down the viscosity of the reaction mixture, due to a phosphopolyester content in the reaction mixture. In batch type operation, the acid source material may be pre-formed by reaction of the acid and blocking agent in at least a limited amount of the reaction medium, in the phosphorylation kettle, before any balance of the medium and the epoxy resin are added separately or as a pre-formed solution. It is to be noted that in situ reaction of the blocking agent with P-O-P groups even when the latter are provided as ^O- ^ Q , does not preclude conversion of a substantial proportion of the epoxide oxirane groups to phosphopolyesters comprising more than one epoxide residue by oxirane/P-OH reaction. However, the present invention does not require complete avoidance of this and it is only necessary to reduce the formation of such esters to an extent such that practicably low reaction mixture viscosities, satisfactorily low free acid contents and adequately high epoxide-derived phosphomonoester contents are achieved. It is also to be noted that reaction of the block¬ ing agent hydroxyls with P-O-P groups in a phosphoester derived by reaction of P-OH*s in a condensed phosphoric acid with oxirane groups in the epoxide is believed to ' occur to a limited extent during in situ formation of the acid source material but this, in effect, is the- same as the reverse normal sequence of the two reac¬ tions, i.e., blocking agent/P-O-P reaction followed by P-OH/oxirane reaction. Any of the condensed forms of orthophosphoric acid, such as, for example, super phosphoric (105%) acid, pyrophosphoric (110%) acid, metaphosphoric acid, or polyphosphoric (115%) acid, may be reacted as such or as adducts through their P-OH groups with oxiranes present in the epoxide with the blocking agent to form the acid source material. The choice among these may vary, according to their solubility behaviors with the particular reaction medium to be employed. However, liquid forms of the condensed acid, such as polyphos- phoric and super phosphoric acids are more easily handled without exposure to moisture and are generally more readily dissolved. Preparation of the acid source material by equili¬ bration of P 4 0 10 with only enough blocking agent to supply 4 -C-OH's results in a product which consists essentially of pyrophosphates, i.e., of (R0) 2 P0-0-P0(0H) 2 and the statistically more favored species OMPI RO-P-O-P-OH I I HO OR This is advantageous in that the equilibrium content of water-scavenging P-O-P groups will be higher and initia¬ tion of the reaction under essentially anhydrous condi¬ tions will be facilitated. When at least six blocking agent hydroxyls are provided for each R O- JQ molecule, formation of free H 3 P0. and a phosphotriester is not favored and essen¬ tially every P=0 group in the equilibrium product will be linked to at least one each of -OH and OR groups. R-OH is the blocking agent. That is, the product will consist predominantly of HO-PO(OR) 2 and (HO) 2 PO(OR), although a small amount each of P-O-P group-containing species and H^P0 4 will be present too. If not every P-O-P group in the R 4 O-, 0 is reacted out with the blocking agent and water, not every phospho¬ rous atom in the resulting acid source material will have at least one acid hydroxyl attached to it. The proportion of the P 0, Q found in the esterification product in the form of oxirane-derived ester groups will be lower and the content of free acid in the hydrolyzed end-product will be higher. However, even with an excess of the blocking agent present, conver¬ sion of the last P-O-P groups prior to reaching an equilibrium proceeds slowly. As a general rule, the higher the proportion of P-O-P groups in R 4 0 10 reacted out with the blocking agent, rather than water, in forming the acid source material, the lower the content of free H 3 P0 4 will be in the hydrolyzed product. Also, the content of phospho- ester groups derived from more than one epoxide molecule will be lower, which is advantageous in that it results in a lower maximum viscosity for the unhydrolyzed reaction mixture. Another method of preparing a suitable acid source material is to first react an alkylene oxide with P 4°10' in the manner taught in U.S.P. 3,597,511 thereby forming a bis-alkylenepyrophosphate comprising the moiety and then carefully hydrolyzing the P-O-P group as taught in U.S. . 3,652,743. In this manner, cyclic phosphodiesters of the formula which are suitable as the acid source material, can be prepared essentially free of monoesters. It will be recognized that the foregoing pyrophosphate precursors of such ring acids are theoretically derivable by direct esterification of a 1,2-glycol as the blocking agent with pyrophosphoric acid, and the ring acids therefore are within the ambit of the preceding acid source material definition, even though not actually prepared from a C-OH group-comprising compound. OMPi Cyclic phosphodiesters comprising 6-membered rings, such as can similarly be prepared from the corresponding bis-pyrophosphates as taught in U.S.P. 3,159,591. These acid source materials illustrate the suitability of . 1,3-diols as blocking agents. Suitable blocking agents are those -C-OH hydroxylic compounds which are capable of forming phosphoester groups more readily hydrolyzed than the epoxide-derived phosphomonoester groups or which are not readily evolved during curing and are acceptable in the final product. Of course, if the blocking agent-derived ester groups are not readily hydrolyzed, care must be taken to ensure that the P.O.. is not fully esterified by the blocking agent, i.e., provision for the P-OH groups essential to both oxirane adduction and product salifi¬ cation must be made. It is presently considered highly preferable that the blocking agent-derived ester groups be readily hydrolyzed, particularly when the reaction medium also functions as the blocking agent. That is, in the latter case, the molecules of reaction medium consumed in forming the acid source material are regenerated during the post-adduction hydrolysis step. EB is particularly suitable as the blocking agent because the phosphate ester groups formed from it are quite readily hydrolyzed more so than those derived from n-butanol, for example, i.e., more readily unblocked after the epoxide has been phosphorylated. When at least one of the ester groups in a phospho- diester is readily hydrolyzeable and the hydroxylic compound thereby (re)genreated is acceptable in the final resin composition, that diester may function as an acid source material in the process of the present invention. Ordinarily, however, it will not be prac¬ tical to employ a pre-formed phosphodiester separate from the monoester(s) and other species which form when the corresponding hydroxylic compound(s) is (are) reacted with a condensed phosphoric acid. It will be apparent that the acid source material may comprise ester groups derived from more than one hydroxylic compound as blocking agent. Thus, a con¬ densed phosphoacid containing a P^ 0 ^P group or two P-O-P groups may be reacted first with one molecular proportion of a first alcohol (R-OH) and then with a different alcohol (R*-OH). In this manner, at least a substantial fraction of the esters formed may be expected to be mixed diesters such as HO-PO(OR)(OR' ). Similarly, a P-O-P-containing compound may simply be reacted with a mixture of two comparably reactive hydroxylic compounds. Specific types of hydroxylic compounds suitable for use as the blocking agent include alcohols, phenols, glycols and glycolmonoethers. It is believed that carbonyl compounds, such as acetonylacetone, for example, which are readily enolized under acidic conditions may also play the role of blocking agents at least when pre-reacted with a condensed phosphoacid in solvents such as toluene or dioxane, for example, which are essentially non-polar and therefore tend to shift the keto-enol equilibrium strongly toward the enolic form. The presence of two or more hydroxyls on the same molecule is not considered necessarily detrimental and may even be advantageous. Ethylene glycol, for example, is relatively high boiling and is water-miscible. The presently most preferred blocking agents are glycol monoethers, by reason of the fact that they not only are high boiling and are preferred reaction media but also form readily hydrolyzed phosphoester groups by reaction with P-O-P groups but not with PO(OH) groups. The monobutyl ether of ethylene glycol, known herein as EB is particularly preferred as a reaction medium having easily reversed blocking capability. C 4 and higher aliphatic alcohols, both linear and branched, have been found suitable as blocking agents for coatings applications. The branched alcohols tend to result in higher forms of hydrolysis-resistant triesters and, though fully operable, are accordingly less preferred. n-Butanol, another acceptable resin dispersion component, tends to yield a higher content of triesters in the adduction stage of the process but these esters are not highly resistant to hydrolysis. Phenol yields a final hydrolysis product which more readily takes up water but also contains more free acid. Benzyl alcohol and phenethyl alcohol have not been used but are considered suitable. Suitable reaction media are those solvents which meet the following specifications. That is, to be suitable, the solvent: -βURtΛt/' OMPI (1) must be acceptable as a component of the final resin formulation to be employed for a given application, (2) must be capable of dissolving or at least dispers- ing the epoxy resin, (3) must be of such a nature that the solution or dispersion of the epoxide in it is capable of dissolving, or at least dispersing, the acid source material or the precursors thereof, if formed in situ, (4) must not solvate the epoxide or acid source material in such a manner as to retard the adduction to an intolerable degree,- (5) must be chemically inert, i.e., must not detri- mentally^react with any component of the reaction mixture to an intolerable degree, (6) must dissolve or maintain dispersed both the epoxide/acid reaction product and water, without solvating either in such manner as to retard the hydrolysis reaction to an intolerable degree, and (7) if it is to also serve as the blocking agent, must form phosphoester groups more readily hydrolyzed than phosphomonoester groups formed by P-OH/oxirane adduction. Preferably, the solvent is capable of dissolving the starting epoxide, the acid source material or its precursors, the epoxide/acid reaction product, water and the amine employed for salification. MPI It is also essential that the amount of solvent which must be used in order to avoid excessive power requirements for agitation of the reaction mixture is not such as to result in an inacceptably high solvent content in the final product formulation. Although highly preferred, it is not essential that the reaction medium be water-miscible. That is, the solvent may be acceptable as a component of the final formulations, even though it is not water-miscible. However, it should at least be hydrophillic enough to permit the hydrolysis step to proceed at a practicable rate. Not very many solvents or solvent mixtures capable of dissolving epoxy resins having molecular' weights of from 900 to 2900 are presently known. Not all of those which are known are formulation acceptable. . Of those which are acceptable, not all are capable of forming solutions in which the resin contents are as high as 25 percent by weight. Yet, in order to meet current VOC limitations, and for other reasons discussed earlier herein, it is essential, at least for coatings applica¬ tions, to be able to use substantially less solvent than the amount corresponding to a 25 wt. % resin content. It has been found that total solids (resin + other non-volatiles) contents of up to 85 wt. % in the hydro¬ lyzed reaction mixture can be attained using EB as both the reaction medium and blocking agent. It is known that other glycol monoethers, such as lower alkyl ethers of ethylene glycol and diethylene glycol are capable of forming epoxy resin solutions containing at least 50% by weight of the resin. Exemplary solvents of this type which have been found suitable as reaction media in the present process are the monomethyl ether of propylene glycol, hereinafter known as PM and l-isobutoxy-2-propanol, hereinafter known as PiBt. The free acid content of the hydrolyzed P-OH/oxirane adducts made in the latter solvent tends to be lower but PiBT is not, by itself, a satisfactory coupling solvent in all types of formulations and is so hydro- phobic that, in certain formulations, it effects the viscosity of the aqueous dispersion as though it were an organic solute rather than a solvent. It imparts a higher viscosity response upon dilution of the salified hydrolysis mixture in combination with one or more coupling solvents with water. PM is a good coupling solvent but is less of a problem in the latter regard. Its use results in somewhat higher free acid contents. Although use af EB results in still higher acid contents, it is an excellent coupling solvent and an acid content of less than 1.5X10 millimoles per gram of solids will be acceptable for can-lining ap lications, for example if an acid source material of the type speci¬ fied for the present process is employed and water is essentially excluded from the reaction mixture until the free acid content therein has reached a constant value. At that time water is added to initiate hydrolysis. Other specific epoxy resin solvents considered operable alone or in solvent mixtures as reaction media are, for example, dioxane, xylene, cyclohexanone, methylene chloride, acetone and methyl ethyl ketone. Of these, however, only cyclohexanone is considered really practical. Dioxane is toxic and is of concern \j ' 4 ^r» 'j with regard to peroxide formation. Methylene chloride is highly volatile, tends to result in gelling of the reaction mixture and is not an accepted formulation solvent. Acetone and methyl ethyl ketone are volatile and/or have low flash points and are less desirable formulation solvents. Xylene is a known formulation solvent in admixture with coupling solvents but is toxic and is not as widely used as previously. It is believed that at least some of the various esters and glycol diethers known to be solvents for epoxy resins are also suitable reaction media for the process of the present invention, at least for those resins of the preceding Formulas I or II having rela¬ tively low n values and/or derived from mononuclear bis-phenols such as catechol or hydroquinone, for example. When the,solvent employed as the reaction medium is not strongly hydrophilic, it can be expected to less strongly or not at all solvate the acid P-OH groups, which is advantageous. However, it will also be a poorer solvent for the acid source material such as P 4 0 1Q and condensed varieties of Ξ 3 P0 4 , for example. In this event, use of a pre-formed acid/blocking agent reaction product, as a more soluble form of the acid source material, is indicated. The phosphorous-to-oxirane reactant ratio is controlled according to how much free acid can be tolerated in the final product. As discussed in the above-cited U.S. Patent 4,289,812, it is not necessary to convert even half of the oxiranes introduced in the epoxy resin to salifiable phosphoester groups in order to obtain a salified product which does not require the presence of a coupling solvent in order to exist as a stable, aqueous dispersion. As many as 12 out of every 13 of the oxiranes may be found in the product in the form of 1,2-dihydroxy groups without resulting in a salified product which is not water-dispersible. When the reaction medium employed in the present method is a coupling solvent, even less than the minimum amount, that which provides about 0.3 P-OH's per oxirane, of acid source material specified in said patent may suffice. However, as a general rule, the amount of the acid source material used in the present process will be such as to provide from 0.1 to 0.2, preferably about 0.1 atoms of phosphorous per oxirane when the cured product must be water insensitive. For other applica¬ tions, where water sensitivity is less of a problem, higher amounts of the acid source material will be acceptable. Jn general, however, amounts providing more than about one phosphorous per oxirane will be unnecessary and can even result in so much free acid that the corresponding salt formed from it during salification may cause phase separation in the final product mixture. Pressure is not a critical variable in the present process, except that a pressure at least equal to the autogenous pressure of the reaction mixture must be maintained if the reaction temperature is to be held at or above the initial boiling point thereof. Ordinary ambient pressures are preferred but reduced pressures are also suitable when the blocking agent and/or reac¬ tion medium are relatively high boiling. "BURE ZT OMPI The phosphorylation temperature is important in three respects: polymer solubility, reaction rate and reaction mixture viscosity; each of which varies with temperature in the expected manner. For uses of the end product in which relatively low solvent contents are essential, the solids content of the reaction mixture must be high and elevated temperatures will generally be necessary to dissolve the epoxy resin at a useful rate. Once formed, the solution may not phase-separate upon cooling to ordinary temperatures, but, at least when the epoxy resin has a relatively high n value, will be so viscous as to be practically unstirrable. Thus, .adequate dissemination of even a pre-formed, miscible acid source material, without re-warming the mixture, which will result in substantial progress of the phosphorylation reaction, will generally require the addition of extra solvent and a corresponding lowering of the solids content. Thus, carrying out the reaction at ordinary ambient temperatures, for example between 20° and 30°C, will ordinarily not be practical. However, such temperatures are considered operable for lower molecular weight epoxies such as, for example, the diglycidyl ethers of bisphenol A having an EEW between 172 and 176 and/or at higher dilutions. Reac¬ tion times of from several hours to several days should suffice. It is neither necessary nor desirable to attain an equilibrium condition. It is sufficient to proceed until the polyester including di- and triester content rises far enough and preferably peaks. The free acid content preferably drops to a minimum. Subsequently, preferably immediately, hydrolysis is initiated. R£A(; Phosphorylation temperatures of from 115°C to 130°C are generally preferred. Within this range, the reaction can be effectively terminated by initiation of hydrolysis after a reaction time of about 0.5 hour, even though the actual times required for the polyester contents to peak will vary with the particular tempera¬ ture. The peaks are gently rounded, rather than sharp. At temperatures within the range of from 100 to 115°C, the reaction can be allowed to proceed from 60 to 45 minutes before hydrolysis is initiated. At a tempera¬ ture of about 145°C, 20 minutes suffices. At about 160°C, 5 to 10 minutes is sufficient. At the latter temperature, side reactions detrimental to use of the end products as coatings become of concern and still higher temperatures are considered generally impractical. The viscosity of the phosphorylation mixture goes through a maximum after the reaction has been on-going from 15 to 20.,.minutes. The effect of temperature on . this viscosity maximum is illustrated by the data, in Table I following, obtained with a diglycidyl ether of bisphenol A having an EEW of 1800 and polyphosphoric acid in amount equivalent to 0.9 parts of H 3 P0 4 per 100 parts of epoxy resin in EB at a 74% solids content. TABLE I Temperature °C Maximum Viscosity CPS (Pa.s) 1 " 45 10,000 (10) 130 32,000 (32) 120 80,000 (80) 110 180,000 (180) *BU EATΓ OMPI It is apparent from the data in Table I that a very substantial reduction in viscosity can be achieved by increasing the reaction temperature by 10°C thereby avoiding the necessity of adding excessive amounts of solvent. This effect is dramatically illustrated by the fact that, at a temperature of about 160°C, it is possible to form a stirrable, homogenous mixture of a diglycidyl ether of bisphenol A having an EEW between 1600 and 2000, EB and a pre-formed P 4 0-, Q /EB acid source material, even though the solids (resin + ^ Δ P± Q ^ content of the mixture is about 91%. It should be noted that much higher viscosities would be experienced at all temperatures, but for the effect of the blocking agent. That is, the average number of resin molecules attached to the phosphorous in each di- or triester group would not be less than two. It is preferable, from the standpoints of both processing time and product quality to terminate the phosphorylation and initiate hydrolysis within the time period extending from a few minutes before the free acid content reaches a minimum to the time when oxirane conversion is about 95% complete- At a temperature of 125°C, for example, this window extends from 25 minutes to 35 minutes. However, at the cost of higher final free acid contents and lower monoester contents the phosphorylation can be allowed to continue for up to 5 hours, or even longer, before hydrolysis is initiated. See Example 13 herein. As a rule of thumb, hydrolysis may be initiated within 10 to 15 minutes after the viscosity peak for U E 7 S the reaction mixture has been noticed. This can be done automatically in response to the time variation of the stirring power required to maintain a pre-selected rpm. In any case, once the highest permissible free acid content prior to hydrolysis is established for a given resin/acid source material/solvent combination, the hydrolysis can be initiated as soon as that level has been reached, even though the acid content would drop further if the phosphorylation were allowed to continue- The amount of water required, as a minimum, is the stoichiometric amount for the least acceptable degree of conversion of the phosphodi- and triesters present to epoxide-derived phosphomonoesters including difunc- tional such esters, i.e., those in.which both oxiranes in the epoxide molecule are converted to monoester groups. This can be calculated from the free acid, mono-, di- and triester contents of the phosphorylation mixture as determined by titration, gel permeation chromatography and phosphorus 31 nuclear magnetic resonance. However, it is generally unnecessary to do this, since the final product will be diluted with considerably more than the minimum amount of water. It has been found that as little as 1 part of water per one hundred parts of resin (phr) is adequate when the epoxide resin is a diglycidyl ether of bisphenol A having an EEW between 1600 and 2000 and from 2 to 5 phr will usually be more than sufficient, even for lower EEW resins. "BU E T * O. PI Since the reaction mixture temperature will usually be in excess of 100°C, it is convenient to add the hydrolysis water as a pre-formed solution in a high-boiling solvent such as EB. However, this is not essential and the water can be injected under pressure. The hydrolysis temperature is important with respect to the rate of hydrolysis, i.e., process time requirements, pressurization requirements and selec¬ tivity between mono- and polyester groups which involves preferential hydrolysis of blocking-agent derived PO-O-C groups. As would be expected, the rate of hydrolysis goes up as the temperature is increased. This is advanta¬ geous in that the process can be concluded more rapidly if it is not necessary to cool the phosphorylation mixture before initiating hydrolysis by adding the water. However, the higher the phosphorylation tempera¬ ture, the more rapidly the polyester content maximizes and the more rapidly it declines thereafter. The time period for water addition at the optimum reaction stage to achieve maximum oxirane-derived monoester and minimum free acid contents in the hydrolyzed product is accord¬ ingly narrower. Also, operation under pressure is necessary to maintain a given concentration of water in the liquid phase when operating at temperatures, substantially above 100°C. Although the mole fraction of water in the mixture will be relatively small, the vapor pressure of the reaction mixture is not insignificant particularly when a lower boiling solvent is used as the reaction medium at temperatures above 100°C. At least enough pressure must be maintained in the reactor to permit condensa¬ tion of the evolved vapors. It is convenient to main¬ tain temperature control by refluxing. The most important consideration as to the hydroly- sis temperature is not to exceed the temperature at which the rate of hydrolysis of oxirane-derived phospho¬ monoester groups becomes intolerable. The other ester moieties in a phosphopolyester, whether derived from blocking agent or epoxide molecules, are more readily hydrolyzed at moderate temperatures than the last oxirane-derived ester moiety. As a general rule, hydrolysis temperatures ranging from 90° to 130°C are practical, but it is preferred, at least for applica¬ tions in which low final contents of free acid are essential, to stay within the narrower range of from 115° to 125*0. As a goo>d compromise between first-stage viscosity considerations, overall process time requirements and final product quality, the same temperature, within the range of from 120° to 125°C, is maintained during both the phosphorylation and hydrolysis steps. At a tempera¬ ture of about 122°C which is the reflux temperature at 760 mmHg (0.1 MPa) for the reaction mixture described earlier on page 27 containing 2 phr H 2 0, two hours is an appropriate hydrolysis time. At a temperature of about 100°C, times of from 4 to 4.5 hours are required. Hydrolysis temperatures of up to 150°C may be operable, provided that the reaction can be effectively quenched after a short contact time of from 5 to 15 minutes. -gvJ AtT OMPI For the phosphorylation step, times ranging from about 5 minutes at 160°C to several days at from 20° to 30°C are considered suitable. All other factors being equal, the shorter the contact time the better, but in the preferred reaction temperature range of 120° to 130°C, from 35 to 25 minutes is generally satisfactory. For phosphorylation of the diglycidyl ether of bisphenol A having an EEW from 1600 to 2000, about 30 minutes at from 122° to 125°C is presently considered optimum. For the hydrolysis step, times of from about 5 minutes at 150°C to about 6 hours at 100°C are considered suitable. At 130°C, one hour will usually be sufficient. In the preferred temperature range of from 115° to 125°C, times from 3 to 1 hours are appropriate. Two hours at 122°C is presently considered optimum for the above described phosphorylation products. _r Those knowledgeable in the art will recognize that somewhat different hydrolysis times than those indicated above may be appropriate when more or less readily hydrolyzed phosphoester groups are formed by the reac¬ tion of the blocking agent with the acid source material. However, these times may readily be determined without undue experimentation. Also, it will not be necessary to attain the maximum possible monoester content in all cases. When it is desired to salify the hydrolyzed reac¬ tion product, suitable bases and the manner of introduc¬ ing them are generally as disclosed in U.S. Patent 4,289,812. Organic bases and tertiary amines in particular are preferred. An equivalent of base for every P-OH in the hydrolyzed resin product is not necessarily required. As a minimum, only as much of the base is re-quired as suffices to maintain the resin in a dispersed state during and subsequent to intro- duction of the water employed in coating formulation. A preferred base, at least for products derived from diglycidyl ethers of bisphenol A having EEWs between 1600 and 2000, is dimethylaminoethanol (DMAE). It has been found that the amine level affects not only the size of the salified hydrolyzate particles but also the viscosity of the system upon inversion by water addition and the coating rheology of the final formula¬ tion. A further complication is that the optimum amine level is dependent on the relative amounts and kinds of the other components of the organic phase. For EB solutions of hydrolyzed product resins derived from the above described epoxy resin and having low free acid contents, aboit 1.2 parts by weight of DMAE per 100 parts by weight of the starting resin is considered optimum, particularly for spray applications of the inverted system. For other reaction media or combinations thereof with various separate blocking agents, other amines such as triethylamine, for example, may be better suited to a given application. Amine to starting resin mole ratios greater or less than that corresponding to 1.2 parts of DMAE per hundred parts of the starting resin may be more appropriate. For any specific phos- phorylation/hydrolysis product, this can readily be determined by practicing coatings chemists, without resort to undue experimentation. IΪΛJ E LΓ OMPI As a general rule, it is highly preferable to salify the hydrolyzate by introducing the amine before adding very much water to the system. Better dispersions result if the hydrolysis mixture is cooled to a temperature of about 85°C or less before the amine is added. This ordinarily requires heat removal unless water addition prior to salification is practiced. The amount of heat which must be removed can also be reduced by addition of the solvent(s) such as n-butanol, for example, before the amine is added. Solvent addition prior to salification is also advanta¬ geous in reducing the viscosity of the system, thereby facilitating mixing with the amine and the water. The following examples are for purposes of illustra- tion and are not to be construed as limiting the scope of the present invention. Epoxy resin A was the diglycidyl ether of bisphenol A having an EEW of 1800.- Epoxy resin B was the diglycidyl ether of bisphenol A having an EEW of 174. Epoxy resin C was the diglycidyl ether of bisphenol A having an EEW of 1750. Epoxy resin D was the diglycidyl ether of bisphenol A having an EEW of 1181. Curing agent A was a melamine/formaldehyde crosslmker under the product desingation of Cymel 303, a trademark of American Cyanamid Co. Analytical Free acid and ester contents of the reaction mixtures, after successively longer contact times, were determined by titration as follows. -^U EAiT I Samples of about 10 g were removed from the reac¬ tion mixtures at regular intervals, dissolved in 50 ml of methylene chloride and added to 100 ml of a 3:1 toluene/butanol solution. They were extracted 3 times with 75 ml each of distilled water, adding 10 ml of butanol when needed to control emulsion formation. The aqueous extractions were combined and titrated to first and second end points with 0.1 N NaOH using a Metrohm Herisan, E 535 and E 536, automatic titration instru- ment to determine water extractable acids. The differ¬ ence between the first and second end points was taken to represent the molar value for free acid. The organic raffinate was titrated in much the same manner using methanolic tetrabutylammonium hydroxide (TBAH) as the base. The difference between the first and second end point was taken to be the molar equivalent for monoester. The first end point minus the monoester equivalents was taken as the diester molar equivalents and the triester concentration^was calculated from total charged phosphate molar equivalents minus the values for free acid, monoester and diester. Solids determinations were performed using 1 to 2 g samples of material which were weighed before and after heating at 200°C for 2 hours. Phosphorus 31 nuclear magnetic resonance (NMR) analyses utilized as a check on titration results and to provide additional information about phosphorylate and hydrolysate compositions were carried out on a JEOL FX-60 NMR instrument equipped with a 10 mm phosphorous probe insert operating at 24.15 MHz and ambient tempera- tures. The phosphorous observe frequency typically had an offset of 56.2 KHz, the proton signal was decoupled at a setting of 47.7 KHz (Hetero/Noise, 0.5 KHz) and a deuterium source, usually acetone-d, was used as the OMPI internal lock frequency. A 12 μ sec (90°) single pulse sequence with a 1 second pulse delay and an acquisition time of 8 seconds was routinely used. The spectral width and filter were set at 500 Hz, thereby yielding 8000 data points per spectrum. Identification of the H 3 P0 4 absorption was performed by spiking samples with a 1:1 solution of acetone-dioxane containing 1% amine neutralized H 3 P0 4 and observing an increase in the H 3 P0 4 peak. The chemical shift of this absorption was highly dependent upon concentration and the pH of the neutralized samples. An external sample of tri-n-butyl-orthophosphate (1% in acetone/dioxane) was placed in a 5 mm tube inside the larger 10 mm NMR tube to reference the phosphate multiple esters. Resin samples were prepared by dissolving 2 g of 65-85% N.V. material in 2 g of dioxane and neutralizing this mixture o a pH greater than 10 with from 0.2 to 0.4. g of triethylamine (TEA). Then 2 g of this mixture was placed into a 10 mm NMR tube with 1 g of acetone-d g and mixed until homogeneous. Fourier Transform Spec- troscopy was used, collecting from 1000 to 5000 tran¬ sients, and displaying the region of interest as either a 250 Hz or 500 Hz full width scan. The peak assigned to the dominant isomer of the resin monoester, believed to be the 2-hydroxy isomer, ( 0-CH 2 -CH-CH 2 -0-P0(0H) 2 ) OH was conveniently utilized as an internal reference in a number of scans. The peak assigned to the EB ono- orthophosphate was also so utilized in some scans. Phosphorus 31 NMR provides information as to the distribution of the phosphorus charged as the acid source material among different phospho species but does not provide a direct indication of the proportions of oxirane in the starting resin found as 1,2-glycol and phosphoester groups in the hydrolysate. However, the latter information can be deduced from the equiva¬ lents of oxirane converted and the amounts of free acid, mono-, di- and triesters formed (as disclosed in the above-referenced application) . Comparative Runs A to F are representative of processes NOT meeting all of the limitations in the foregoing definition of the invention. In all of the Comparative Runs but F, 85% aqueous H 3 P0 4 was employed as the acid source material and the reaction medium consisted predominantly of a glycol- onoether. The solids (epoxy resin + H 3 P0 4 ) contents of the phosphory¬ lation mixtures ranged from 61 wt. % to 74 wt. %. In Comparative Run F, the acid source material was a preformed EB/P 4 0 10 reaction product but a formulation- acceptable solvent was not employed as the reaction medium. Comparative Run A A one-liter flask was charged with 250 grams of Epoxy Resin A, 135 grams of EB and 3 grams of water. The mixture was heated to 110°C with stirring and a solution of 3 grams of 85% aq. H 3 P0 4 in 10 grams of methyl ethyl ketone (MEK) was added. Heating was continued for four hours at the reflux temperature of 110°C. The reaction mixture was cooled, neutralized with triethylamine and tested for dispersibility in ' water with negative results. Failure to obtain a dispersion despite the presence of the EB and MEK is attributed to the continuation of a relatively high water-to-acid ratio (7.4 moles/mole) and a strongly acid-solvating reaction medium. Comparative Run B The reaction of Comparative Run A was essentially duplicated, except that the monomethylether of propyl- ene glycol (PM), a less strongly acid-solvating solvent was employed with no other solvents as the reaction medium. When neutralized with triethyl amine, the hydrolysis mixture was not dispersible in water alone but was dispersible in a 1:1 EB / Ε O solution. The ability of the dispersion to wet tin-free steel was poor. Comparative Run C A two-liter- flask was charged with 300 grams of Epoxy Resin A» 100 ml of isobutoxy-2-propanol (PiBT), 25 ml of MEK and 2 ml of water. The mixture was heated to 95°C, 3.5 grams of 85% H 3 P0 4 in 25 ml MEK was added and the temperature raised to 100°C. Stirring difficul¬ ties were encountered at a solids content of 69% and, after 2 hours of heating, 60 ml of EB had to be added to lower the viscosity enough to permit withdrawal of analytical samples. This lowered the solids content to about 61%. After 5 hours total contact time, the reaction was terminated by cooling and the resulting mixture neutralized with triethylamine. The neutralized mixture was completely dispersible in water. The dispersion exhibited good wetting charac- teristics and, when formulated with 8.75% of curing agent A and cured 2 minutes at 200°C, produced a coating which exhibited only a slight blush after one hour in boiling water. However, the viscosity of the reaction mixture, even after dilution to a relatively low solids content, was such as to require excessive power for stirring in commercial scale operations. A comparison of free acid contents for the unneutra- lized hydrolysis mixtures of Comparative Runs A, B and C is given below. Compara¬ tive Predominant Solvent Free Acid Runs In Reaction Medium Millimoles/gram of Solids A EB 2.3 x 10 "2 B PM 1.9 x 10 "2 C PiBt 1.2 x 10 "2 It will i>e ' seen that an acid content equal to or _2 lloowweerr tthhaann 11..55xx1100 "' mmoles/g was obtained only m Comparative Run C. Comparative Run D A two-liter flask was charged with 600 grams of Epoxy Resin A, 110 ml of EB, 55 ml of xylene and 40 ml of MEK. The mixture was heated to 110°C and 7 grams of 85% aq. H 3 P0 4 (1:1 mole ratio H 2 0/H 3 P0 4 ) in 25 ml of MEK added. Heating was continued at reflux temperature of 110°C for thirty minutes and then 10 ml of water in 50 grams of EB was added and the reaction continued an additional 3.5 hours. The viscosity of the resulting hydrolysis mixture containing 73.5% solids was so high that dilution with 83 ml of n-hexanol was necessary in order to retain sufficient fluidity upon cooling. When neutralized with triethylamine, the diluted mixture was completely dispersible in water. The dispersion wet tin-free steel coupons well but, when cured with Curing Agent A, the resulting coating exhibited only fair water resistance. Comparative Run E A two-liter flask was charged with 600 grams of Epoxy Resin A, 280 ml of PiBT and 25 ml of MEK. The mixture was heated to 108°C, 7.5 grams of 85% H 3 P0 4 in 25 ml MEK was added and heating was continued at reflux temperature of 108°C for another 30 minutes. At this point, 10 ml of water was added slowly enough to avoid dropping the temperature below 106°C and refluxing was continued another 3.3 hours. 100 ml of n-hexanol was added to.ensure adequate fluidity of the mixture upon cooling. A sample of the hydrolysis mixture, when neutra¬ lized with triethyl-amine, was dispersible in water. The dispersion had excellent wetting properties on tin-free steel and when applied as a mixture with solution of Curing Agent A in the hexyl ether of diethy- lene glycol and cured 2 minutes at 200°C, gave a coating exhibiting no blush or loss of adhesion after one hour in boiling water. it is evident from the results of Comparative Runs D and E that maintaining a lower water-to-acid ratio until oxirane conversion is substantilly complete, i.e., for about 30 minutes, is quite helpful but running the reaction in PiBT apparently would be necessary to achieve adequately low free acid contents. PiBT solu¬ tions of the Epoxy Resin A derived hydrolysate having O PI satisfactorily high solids contents, however, are so viscous as to require excessive stirring power on a commercial scale. Also, the hydrolysis rate is lower in the less hydrophilic PiBT. Comparative Run F EB was added under anhydrous conditions to a stirred slurry of R 0-, 0 in hexane over a period of one hour. The temperature rose to about 55°C. The ratio of moles of EB to gram atoms of P was about 1. The reaction mixture was allowed to cool while stirring was continued for two hours. A little more EB was added, to ensure complete R^O- Q conversion, and stirring continued without application of heat for 2 hours more. The reaction mixture was allowed to stand overnight. Analysis by 31P NMR of a sample of the product mixture showed that over 80% of the R O-. Q was present in the form of the symmetrical bis-butoxyethyl pyrophosphate. The latter product was isolated, essentially free of other phospho species, as a hexane-insoluble, and dissolved in toluene. Separate portions of the solution were combined with separate solutions of Epoxy Resin B at mole ratios of 1:1, 2:1 and 4:1. A reaction ensued, upon heating each of the result¬ ing mixtures, with formation of a rubbery gel in each case. It was found that the 1:1 and 2:1 gels would slowly dissolve in hot water with hydrolysis to produce water-soluble, acidic monophosphoesters, which, when neutralized with ammonia or amines and cured with Curing Agent A, gave tough, resinous products. Water resistance of these products was not checked. The 4:1 gel would only partially dissolve in hot water. The foregoing results tend to confirm the results disclosed in U.S. Patent 4,289,812 as obtained when a condensed form of phosphoric acid is employed, even though the P-OH functions of the acid have been par- . tially blocked by esterification with EB. That is, gelling occurs at least in a medium-like toluene when water is not added until the phosphorylation has run its course. Example 1 2.2 Grams of P 4 0, Q was mixed, at room temperature, with 5.8 grams of phenol (2 moles of phenol per gram atom of P) and 2 grams of methylene chloride. The P 4 0 10 dissolved slowly and not quite completely, so 5 grams of EB was added. The 0-, 0 still did not com- pletely dissolve but the mixture was washed into a dropping funnel with another 10 grams of EB and the resulting solution added over a ten minute period to an agitated solution of 300 grams of Epoxy Resin A, 100 grams of EB and 10 grams of MEK, maintained at 110°C in a 1-liter, 3-necked flask. The resulting mixture was stirred at 120°C for 1 hour and allowed to cool for 1 hour and 20 minutes to 80°C. Five ml of water was added and the resulting mixture heated to 105°C" in 15 minutes and maintained at between 111° and 114°C for a total heating time of 4 hours. The course of the hydrolysis was followed by titration of successive samples taken at the point of water addition and hourly thereafter. The contents of free acid, mono-, di- and triester based on a 71% solids content in the hydroly- " sate are given, for samples 1, 2, 3 and 5, below. Hydrolysis Mill-Lmoles per gram of soliets x 102 Sample Time in Free No. Hours Acid Monoester Diester Tr ester 1 0 0.52 1.72 3.17 4.09 2 1 0.80 4.50 2.62 1.58 3 2 0.98 6.01 1.74 0.77 5 4 1.26 7.23 0.96 0.05 When neutralized with triethylamine, the hydrolysate took up water very well and, in the form of the following formulation containing 30% solids and a VOC 0.27, exhibited good wetting properties on tin-free steel and cured to a coating which showed no blushing when boiled 1 hour in water: hydrolysate, 24.9 grams; water, 35 grams; triethylamine, 0.4 grams; dimethylaminoethanol- amine, 0.17 grams; and 0.415% solution of Curing Agent A, 3.70 grams. The results of 31P NMR analysis of the final hydrolysate utilizing the dominant monoester oxirane- derived peak tentatively assigned to the 2-hydroxy-l- phosphoester isomer as an internal standard (O Hertz). 4 Component % P 17 Chemical Shift, Hertz -C-C-OPO(OH).- 65 t *• OH -C-C-OH 16 -17.0 OPO(OH) 2 Free acid 3 -43.8 Diesters 9 -82.3 Triesters 7 •98.4 to -114.5 1/ Percent of phosphorus charged which was found in component. 'BUR E ATT OMPI It is evident from the foregoing results that delaying initiation of hydrolysis by more than two hours, with the first hour at 120°C, then declining to 80°C did not result in an excessive free acid content or an unacceptably low monoester content. Phenol regenerated by ester hydrolysis presumably would not be acceptable as a component of a beverage can lining but could be acceptable in other applications. Example 2 A pre-reaction mixture of 4.65 g (0.0165 mole) of P 4 0 1Q in 10 grams (0.135 mole) of n-butanol was added to a dropping funnel with 10 ml of EB. A two-liter, three-neck flask with 600 g (0.333 equiv. ) of Epoxy Resin A in 190 ml of EB and 20 g of MEK for viscosity control was heated to 101°C and the premix-phosphate ester solution added with stirring. The mixture was heated to 125^C for 1 hour, yielding.a viscous mixed phosphate ester solution. Titration analysis of the water-insoluble portion of the phosphorylated material indicated it was predominately a triester of orthophos- phate containing both hydrolyzed epoxide and solvent. Phosphate hydrolysis was performed by the addition of 10 g of water and heating to 116°C with stirring for* 4.5 hours to obtain a mixed reaction product in which 68% of the charged R 4 O 1Q was present as epoxide-derived phosphomonoester groups. Upon neutralization with triethylamine this product was found to be water- dispersible. The latter product included 75 grams of hexanol, which had to be added to the hydrolysate to thin it sufficiently to pour it out of the reaction flask. • fUREA/" OMPI The free acid and ester contents of the reaction mixture at the point of water addition (sample #1) and at hourly intervals thereafter are given below. Millimoles per gram solids x 10 2 Sample Free acid Monoester Diester Triester 1 0.26 1.31 2.37 6.06 2 0.48 3.14 2.52 3.86 3 0.65 4.83 2.35 2.17 4 0.88 5.92 1.81 1.39 5 0.87 6.77 1.32 1.04 31 P NMR confirmed the relatively high content of polyesters in the product and the scan included a peak at -109 Hertz from the dominant monoester peak attrib¬ uted to tributyl phosphate. It is evident by comparison with Example 1 that the phosphoester groups derived from n-butanol are substantially more resistant to hydrolysis than those derived from phenol. However, the consequently higher polyester and lower monoester contents obtained with n-butanol as the blocking agent are apparently compen¬ sated by the lower free acid content and a water- -dispersible product results. Example 3 A pre-reaction mixture of 5.5 grams (0-0194 moles) of 4 0 1Q and 15 grams (0.2025 moles) of n-butanol was rinsed with 20 grams of EB into a stirring, hot (105°C) solution of 750 grams of Epoxy Resin A in 180 grams EB and 20 grams of MEK in 5 minutes. The resulting mixture was stirred at 105°C for 1.5 hours and then hydrolyzed 'BU E U OMPI for 6.5 hours at about 102°C, a total of three 10 ml portions of water being added during that time. The acid and ester contents in samples of the hydrolysate taken after 5 and 6.5 hours of hydrolysis were as follows. Hydrolysis Millimoles per gram solids x 10 2 Time Free acid Monoester Diester Triester 5 hrs. 0.67 5.98 1.37 1.98 6.5 hrs. 0.84 6.89 1.21 1.06 The final hydrolysate containing 68.5% solids, by calculation, and 70.5% non-volatiles by oven test, which includes residual EB was diluted with 70 grams of n-butanol and the resulting solution neutralized and formulated to an aqueous, 25% solids, dispersion as in Example 1. The formulation wet tin-free steel well and gave a cured coating which passed the one hour water boil test. It is evident by comparison with the results in Example 2 above that further diester conversion results upon prolonged hydrolysis but the residual triester, presumably tributyl phosphate, is essentially unchanged. However, the hydrolysis-resistant ester does not detri¬ mentally affect the utility of the neutralized hydroly¬ sate to a noticeable extent. Exam —ole 4 To a solution of 750.8 grams (417 milliequiv. ) of Epoxy Resin A in 125 grams n-hexanol, 100 grams n-butanol and 25 grams of MEK, was added a solution of 5.75 grams (20.2 millimoles) of R 4 0 10 in 25 grams (337.8 millimoles) of n-butanol. The mixture was stirred 1.5 hours at a temperature of 120±1°C, then 15 grams (833.3 millimoles) of water was added slowly, to avoid excessive refluxing. The temperature dropped to 105°C. After 2 hours of hydrolysis, the heat was turned off and the reaction mixture allowed to cool to and stand overnight (16.25 hours) at room temperature. A sample was taken for analysis and heating resumed for 4 hours more of hydrolysis at between 103° and 104°C. A final analytical sample was then taken; the acid and ester contents were as follows: free acid 0.74x10 -2 millimoles/g solids monoesters 2.65x10 -2 millimoles/g solids diesters 3.14x10 -2 mialliamoles/g solids tπesters 3.47x10 -2 mialli.moles/g soliads • . The evident incompleteness of hydrolysis (even after 6 hours at between 103° and 105°C) was confirmed by 31P NMR. Although substantial additional hydrolysis occurred in the second 4 hour heating period, the overall extent of conversion of polyesters to monoesters and free acid was unusually low. This is attributed to the essentially hydrophobic nature of the reaction medium as n-hexanol is only slightly soluble in water and illustrates the necessity of using a reaction medium which is substantially hydrophillic. Example 5 800 Grams (0.444 equivalents) of Epoxy Resin A containing 0.45% (3.6 grams, 0.2 mole) H 2 0 was dissolved with 180 grams EB and 20 grams of MEK at 105°C To this solution was added dropwise a solution prepared from j DRE a ATT OMPI 46 6.0 grams (0.0211 mole) of 4 O 10 reacted with 15 grams (0.202 moles) of 2-butanol with 20 grams of EB added after the reaction. The addition, carried out at between 105° and 110°C, required 10 minutes. The resulting mixture was stirred at between 110° and 125°C for 1.5 hours, at which time the temperature was 118°C and the viscosity of the reaction mixture was noticeably higher. The mixture was cooled to 100°C and 15 grams (0.83 mole) of water was added. Total water was then 18.6 grams or ~1.8%. The temperature was then raised to 105°C in 15 minutes and held between 105° and 110°C for 3 hours, at which point an analytical sample was taken and hydrolysis continued for another 2 hours at 106°C. A final sample was taken for analysis. The acid and ester contents in millimoles/gram solids after 3 and 5 hours hydrolysis ignoring whatever hydrolysis may have resulted from concurrent action of the water in the resin during esterification were as follows: Millilmoles per gram Solids x 10 2 Time Free acid Monoesters Diesters Triesters 3 hrs. 0.65 4.24 2.67 2.5 5 hrs. 0.73 4.89 2.28 2.1 A 40% non-volatiles dispersion was prepared by neutralization and water-thinning and had the composi¬ tion: 100 parts by wt. of starting resin, 25 parts by wt. of EB, 120 parts by wt. of water, 1.03 parts by wt. of DMAE, 0.67 parts by wt. of TEA and 0.75 parts by wt. of the converted P ■ .tO.±,,U,. 1.75 Grams of Curing Agent A in 3.75 grams of n-hexanol were added to 50 grams of the dispersion, plus 4 grams EB, 25 grams of n-butanol and 27 grams of water, thereby converting it to a 25% non-volatiles formulation capable of being coated onto tin-free steel and cured thereon to an adherent, water-resistant film. It is apparent from this example that the esteri- fication and hydrolysis steps can be carried out, according to the present invention, at solids contents of 80% and with an epoxide which is not anhydrous, without development of unmanageable viscosities or excessive free acid contents. A water-thinnable product can be obtained under such conditions, even though the blocking agent used results in difficultly hydrolyze- able polyesters and a correspondingly low monoester content. Example 6 A 100-gallon (379 liter) reactor equipped with condenser and agitator was charged with 159 kg (88.4 equivalents) of Epoxy Resin A and 53.6 kg (453 moles) of EB. The mixture was heated to 110°C and approxi¬ mately 6 liters of phosphate ester solution prepared from 3.95 moles R 4 0 1Q and 38.88 moles EB was added in 0.5 hour at 110°C with agitation. The mixture heated at 120°C for one hour, at which time more than 95% of the charged oxirane groups had been converted. The resulting phosphate ester mixture was then hydrolyzed by adding 2 liters of water, heating for two hours at 112°C, adding another 2 liters of water and heating at 112°C for an additional 1.5 hours. The hydrolyzed product was analyzed and it was found that 76% of the charged 4 0 10 was P resent as epoxide-derived phospho¬ monoester groups. Free phosphoric acid was found to account for less than 10% of the total R 4 O 10 charged. Upon neutralization with amine, this hydrolysis mixture was found to be water-dispersible. The percent non- -volatiles including residual EB in the hydrolysate was found by heating a sample 3 hours at 200°C in an air- -swept oven to be 74.4%. The acid and ester contents found by titration of a final hydrolysate sample are given below. _2 free acid 0.97x10 millimoles/g solids _2 monoester 7.58x10 millimoles/g solids _»2 diester 0.53x10 millimoles/g solids _2 triester 0.62x10 millimoles/g solids An aqueous dispersion containing 45.6% non-volatiles and having a particle size judged by appearance to be between 700 and 1000 Angstroms (0.01-O.lμm) was prepared by adding 423.8 grams of n-butanol to 3255 grams of the final hydrolysis mixture, stirring in 24.22 grams each of txiethylamine and dimethylethanolamine and then mixing in 3192.76 grams of water. 128.52 Grams of this dispersion was combined with 4.4 grams of Curing Agent A dissolved in 8.75 grams hexanol, 0.88 grams n-butanol and 2.02 grams of EB. The resulting mixture was adjusted to a non-volatiles content of 25% by addition of 55.43 grams more of water. The final formulation had a #2 Zahn viscosity of between 36 and 37 and demonstrated good wetting when drawn down on tin-free steel with a #18 wire wound rod. When cured 2 minutes at 200°C, the resulting film passed the one hour water boil test with no blushing and no loss of adhesion using the standard tape pull test. A pre-reaction product of P 10 and EB, essentially identical to that employed in the esterification of this example, was examined by 31P NMR. The proton decoupled peak furthest upfield was assigned to the monobutoxyethyl ester of orthophosphoric acid and was utilized as an internal standard (O Hertz). A second peak at -27 Hertz was assigned to the bisbutoxyethyl ester of orthophosphoric acid and a third peak at -300 Hertz was assigned to the bisbutoxyethyl ester of pyrophosphoric acid. A very small peak at -48 Hertz was assigned to orthophosphoric acid. From the un-decoupled spectrum, the relative amounts of the three major components were roughly estimated as: monoorthophosphate, 30%; diorthophosphate, 30% and bis-pyrophosphate, 40 mol %. A comparison by 31P NMR of a neutralized hydroly¬ sate made in essentially the foregoing manner with an otherwise closely comparable one made from Epoxy Resin A in methylene chloride/acetone solution with 1 phr of 85% H 3 P0 4 by the method described in the above-refer¬ enced U.S.P. 4,289,812, showed essentially identical monoester peaks. However, the material made by the method of this example contained less free acid and included hydrolysis-resistant di- and triesters. Using the predominant β-hydroxy monoester as an internal standard, the composition of the two materials compare as follows: 50 Approximate Chemical Shift Mole % Phosphorus Component USP 4,289 ,812 Present Invention β-hydroxy, α-monoester 0 Hz/ 76% 0 Hz/ 67% a-hydroxy, β-monoester -17 Hz 19 -17 Hz 16 H 3 P0 4 -41 Hz 5 -41 Hz 2 Diester - 0 -78 Hz 9 Triester — 0 -95 to 6 -105 Hz It should be noted that no MEK or other diluent was employed with the EB in this example. This resulted in an increased stirring power requirement in the earlier stages of the esterification. Comparison of the results in the foregoing examples 1, 2, 3, 5 and 6 shows that the ease of hydrolysis of the phosphoes ers of the hydroxylic blocking agent decreases as its acidity decreases. That is, the ease of hydrolysis decreases in the order phenol, n-butoxy- ethanol (EB), 1-butanol and 2-butanol. It will be recognized that the amount of water (0.2 mole) in the resin solution of Example 6 was more than enough to convert all of the charged R 4 0, 0 (0.0211 mole) to H^PO ^j . However, it is believed that the residual water normally present in polyhydroxy, poly- ether epoxide resins is rather tenaciously associated by hydrogen bonding. Accordingly, the esterification is considered to have taken place effectively in the absence of free water molecules. See also Example 7. " U ElT P Example 7 4.5 Grams (15.85 millimoles) of 4 0 10 was dissolved in 30 grams (254 mmols) of EB and 1 gram (55.6 mmols) of water added to the solution. The resulting mixture was added dropwise to a solution of 600.25 grams (333 milliequivalents) of Epoxy Resin A in 170 grams of EB and 20 grams of MEK, in six minutes and at a tempera¬ ture of 100°C. The temperature rose rapidly to 115°C and the phosphorylation was allowed to proceed for 1.5 hours at between 115° and 132°C. 10 Grams of water were added. The temperature dropped to 116°C and the hydrolysis continued for 1 hour. 4 Grams more of water was added, and the temperature dropped to 114°C. After 2 hours more of hydrolysis, 5 grams of water were added and the hydrolysis was continued another hour at 113°C. ' An analytical sample was taken at this point, total 4 hours hydrolysis time, and the hydrolysis prolonged another hour before taking a final sample and cooling the reaction mixture. The acid and ester contents in the final product having 65% non-volatiles were found by titration to be: free acid, 1.28x10 -2 mmols/g solids; monoester, 7.77x10 -2; ' diaester and triester, 1.03x10-2 each. 31P NMR comparison of the two samples taken after 4 and 5 hours total hydrolysis time showed a substantial difference in the extent of hydrolysis. ' B U E U OMPI Chemical Shift/Mole % P Hydrolysis -OH -OH Time Monoester Monoester Free Acid Diester Triesters 4 hours 0 Hz/59.2% -16 Hz/19.7% -47 Hz/2.2% -72 Hz/11.0% -92 to -110 Hz/7.9% 5 hours 0 Hz/61.8% -16 Hz/20.6%* -47 Hz/3.1% -72 Hz/7.4% -92 Hz/5.9% -103 Hz/1.3% t_π 21 Grams of the hydrolysate solution was neutralized with 0.15 grams of TEA and formulated to 25.7% non- volatiles with 35.5 grams of water, 0.15 grams of DMAE and 3.23 grams of a 0.4154% solution of Curing Agent A in hexanol. The resulting dispersion exhibited good draw down and wetting on tin-free steel and gave a good coating when cured 2 minutes at 200°C. It is apparent from the foregoing results that inclusion in the P 4 0-, 0 /EB pre-reaction product of a substantial amount of water (3.51 moles H 2 0 per mole P 4 0 1Q ) did not detrimentally affect the phosphorylation. This may be due to any or all of the facts that (1) the amount of water was less than that (6 moles/mole) required to completely convert the R 4 -, 0 to H 3 P0 4 , i.e., the R 4 O 10 + the H 2 0 was equivalent to 113% H 3 P0 4 ; (2) the water to EB mole ratio in the pre-reaction mixture was low (0.22/1) and (3) once formed, the phosphoesters of EB are somewhat resistant to hydroly¬ sis and the time between water addition and introduc- tion of the pre-reaction product to the epoxide was far short of that required for equilibration. The oxirane/- P-OH reaction is initially quite rapid. In any case, the phosphorylation is again considered to have taken place effectively in the absence of free water molecules. It is also apparent that at hydrolysis temperatures of between 113° and 116°C, about 5 hours is required to achieve essentially complete hydrolysis when EB is employed in a pre-formed acid source material as the blocking agent. Example 8 A 25 wt. % (18 mole %) solution of pyrophosphoric acid in EB was made up at room temperature and a portion of it neutralized with triethylamine, diluted with dioxane and hexadeuteroacetone and examined by 31P NMR, using tri-n-butyl phosphate as an external standard. Additional samples were spiked with different amounts of 100% H 3 P0 4 and similarly treated, to verify the chemical shift assigned to H 3 P0 4 . The results were as follows: Chemical Relative Mole Species Shift Hz Peak Areas Ratios Tributylphosphate 0 - - Mono(butoxyethyl) + 74.5 3 3 ester of H,-P0 4 H 3 P0 4 + 48.1 3 3 Pyrophosphoric ' -168.6 2 1 acid It is not known whether the composition found represents an equilibrium but it at least is evident that the EB/P-O-P reaction is relatively facile and was complete after about an hour at about 25°C. A solution of 700 grams (0.389 equiv. ) of Epoxy Resin A in 225 grams of EB was heated to 120°C and 29 grams of a 24.6 wt. % solution of 98% pyrophosphoric acid in EB (0.080 gram atoms P) added dropwise over a 5-minute period, with stirring. The temperature rose slowly to 130°C. 0.5 Hour after the addition was complete, a sample was taken and 15 grams of water added. The temperature dropped to 113°C, then slowly rose to 117°C. Heating was continued for two hours, samples being withdrawn after 1 and 2 hours of hydroly¬ sis. The reaction mixture was allowed to cool to room temperature and was found to contain 75% non-volatiles. The acid and ester contents of the samples were found by titration to be as follows: H j _ H o_ιuurs s —— Millimoles/gram solids x 10 2 Hydrolysis Free^ acid Monoesters Diester Triester 0 0.98 2.90 4.58 1.5 1 1.45 6.89 1.49 0.2 2 1.53 7.82 0.69 1/ Includes any pyrophosphoric acid present. 31 P NMR analysis of the final reaction product showed the following phosphorus distribution: free acid, 6.2%; monoester of EB, 5.4%; oxirane-derived monoesters, 73.8%; oxirane-derived multi-esters, 14.6%. In addition to the two isomeric, oxirane-derived monoester peaks, a third peak, about 13 Hz upfield of the more dominant isomer is generally present but small and poorly defined in the phosphorus NMR scans of reaction products made according to the present process. This peak in this case was well defined and had a peak area about 1/5 of the area for the less dominant isomer. The additional peak is believed attributable to a cyclic alkylene ester which has the structure "BU EIT OMPI and is an intermediate through which the two isomeric monoesters readily come to an equilibrium with the alcohol or water in which the ratio of the major to minor isomer is consistently about 3:1. 900 Grams of the hydrolysis mixture was neutralized with 12 grams of dimethylaminoethanol (DMAE) and diluted with 888 grams of water. 63.4 Grams of the resulting dispersion containing 36% non-volatiles was combined with 2.19 grams of Curing Agent A, 4.3 grams of n-hexanol, 4.3 grams of n-butanol and 25 grams more of water. The resulting coating formulation containing 0.7/1 solvent to solids ratio and 25% non-volatiles was coated on a tin-free steel panel and cured 2 minutes at 200°C. No blush or loss of adhesion by the standard tape-pull test was observed after the coated panel was boiled in water for 30 minutes. -r It is evident from the foregoing results that even when the acid source material includes no higher esters and consists predominantly of free H 3 P0 4 and the mono EB ester of H 3 P0 4 in equivalent amounts, an acceptable coating can be prepared from its reaction products with epoxy resins such as diglycidyl ethers of bisphenol A having an EEW from 1600 to 2000. It is also apparent that esterification and hydrolysis times of 0.5 and 2 hours, respectively, were adequate at esterification and hydrolysis temperatures of 130° and 117°C, respectively. Example 9 A solution of 750 grams (0.4167 equiv.) of Epoxy Resin A in 225 grams of EB was heated with stirring to JU EATJ 0 P1 110°C and 6.37 grams of 98% polyphosphoric (115%) acid equivalent to 7.179 grams H 3 P0 4 or 0.073 gram atoms P was added. The temperature rose rapidly to 132°C and was maintained at that level for a total phosphoryla- tion time of 0.5 hour. A solution of 15 grams of water in 10 grams of EB was added and the temperature dropped to 122°C. 0.25 Hour later, a sample was taken. The hydrolysis was continued at 119°C for another 2 hours, additional samples being taken at 1 and 2 hours and the reaction mixture allowed to cool. The non-volatiles content of the hydrolysis mixture was 77%. The acid and ester contents by titration were: Hydrolysis Millimoles/gram solids x 10 2 Time Free acid Monoesters Diester Triester 0.25 r. 0.60 3.02 3.34 2.80 1.25 0.99 5.97 1.58 1.30 2.25 1.12 7.10 0.78 0.79 On comparison with Example 8, it will be seen that the free acid content was substantially lower in the product derived from polyphosphoric acid than in that derived from pyrophosphoric acid but the extent of conversion of polyesters to monoesters was somewhat lower, despite a somewhat more prolonged hydrolysis at a slightly higher temperature. Further hydrolysis would increase the mono- to polyesters ratio, without excessively raising the free acid level. However, the foregoing end product is considered quite satisfactory as is for coating and other applications. jυREA tr OMPI Example 10 5.50 Grams (0.0190 moles) of 98% R 4 0 10 (0.076 gram atoms P) was weighed out, in a dry atmosphere, into a flask which was then stoppered. Most of the flask contents was rapidly added with stirring to a 100°C solution of 750 grams (0.4167 equiv. ) of Epoxy Resin A in 225 grams of EB. The rest of the R 4 O 10 was rinsed into the resulting mixture with 25 grams more of EB. After the phosphorylation had been in progress for 1 hour, lumps of undissolved solid (presumably ester- -coated R 4 0 10 ) were still present. 15 Grams of dis¬ tilled water were added and the hydrolysis allowed to proceed at 118°C for 2 hours. The non-volatiles content of the hydrolysis mixture at this point was 75.6%. Titration of a sample of the mixture gave the following results: Free acid 1.53x10 -2 mialliamoles/g solids _ 2 Monoeste s 6.62x10 millimoles/g solids _ 2 Diester 1.00x10 millimoles/g solids _2 Triester 0.85x10 millimoles/g solids Again, a relatively high free acid content and low monoester content were experienced. However, this result was attributed to the presence of a substantial proportion of unconverted P 4 0 1Q when hydrolysis was commenced; it will be noted that the di- and triester contents were no higher than in Example 9. Polyphosphoric acid is less expensive than pyro¬ phosphoric acid and is more practical to use than I> 4 O 10* Assuming a little more time for hydrolysis of the phosphorylation mixture is allowed, it is evident that just as good a product can be obtained with the poly (115%) acid as with the pyro (110%) acid. -BURE-TΓ Example 11 To a 100°C solution of 1200 grams (0.6857 equiv. ) of Epoxy Resin C 1750) in 260 grams of EB was added all at once a solution of 10.57 grams of super phosphoric acid (0.1133 gram atom of P) in 50 grams of EB. The temperature rose to 120°C. The resulting mixture was stirred and heated at 120°C for between 1 and 2 hours until the EEW of the mixture exceeded 70,000, then 24 grams of water was added and hydrolysis allowed to proceed for 2 hours at reflux between 125° and 130°C. A sample was taken for analysis. The reaction mixture was then cooled to 100°C and neutralized by addition of 14.4 grams -DMAE in admixture with 48 grams of n-butanol. The resulting solution was stirred for 0.5 hour- at 90°C and 2 liters of water then added over a 1.5 hour period while holding the temperature at about 80°C. The resulting dispersion contained 34% non-volatiles, • had . an average particle size of 2000 Angstroms (0.2000 μm) and had excellent film properties. The acid and ester contents in the sample of the hydrolysis mixture were: Free acid 1.22x10 -2 m moles/g solids Monoesters 6.68x10 -2 moles/g solids Diester 0.85x10 -2 moles/g solids Triester 1.25x10 -2 m moles/g solids. Example 12 A solution of 100 parts by weight of the Epoxy Resin A in 35 parts by wt. of EB was heated to 105°C and 0.8 parts by wt. of polyphosphoric (115%) acid was added with stirring. The temperature was allowed to ^U E ∑Γ OMPI rise to and maintained at 125°±1°C for 30 minutes. Two parts by wt. of water was then added and the hydrolysis allowed to proceed under reflux at the same temperature for 2 hours. 17.5 Parts by wt. of 1-butanol was added, the resulting solution was cooled to 80°±2°C and 1.2 parts by wt. of DMAE was added. 129.21 Parts by wt. of water was added over a 30 minute period with stirring. The resulting aqueous dispersion contained 35% by weight of the resin and the non-volatiles content, including the resin, the reacted acid as H 3 P0 4 and residual reacted and associated EB, is 36.05%. The acid and ester contents after 2 hours hydroly¬ sis time were within the following specifications: Free acid—' 2.0x10 " millimoles per gram solids Monoester 4.0x10 —2 millimoles per gram solids Diester 2.0x10 —2 millimoles per gram solids Triester 7.0x10 —3 millimoles per gram solids 1/ Species indistinguishable from H 3 P0. by titration.* * Includes any phosphomonesters having sufficient water solubility to report in the aqueous extract of the analytical sample, such as monoesters of EB, which partition between the organic and aqueous phases. Results in somewhat high free acid and low monoester numbers. For spray application the dispersion was formu¬ lated as follows: Component % by weight Dispersion 60.84 Additional EB 2.65 Additional n-butanol 1.33 n-Hexanol 4.84 Additional DMAE 0.16 CYMEL-303 1.92 Additional water 28.26 This formulation is the subject of U.S. Patent 4,316,922. Generally equivalent results were obtained when the foregoing phosphorylation step was carried out at 145°C with hydrolysis initiated after 20 minutes and carried out at 122°C, or when the phosphorylation step was carried out at 115°C with hydrolysis initiated after 1 hour and carried out at 122°C. Example 13 The phosphorylation procedure of Example 12 was followed, except that hydrolysis was not initiated until the reaction had been in progress for 4.5 hours and the hydrolysis was continued for 4 hours. The acid and ester contents of the reaction mixture varied as follows: -BUREATT OMPI Hours Since Phosphorylation Millimoles per gram of Solids xlO 2 Initiated Free acid Monoesters Diesters Triesters 0.5 0.59 2.24 2 .89 3 .60 1.5 0.68 2 . 92 3 .43 2 .36 3 .0 0.76 2 .86 3 .66 2.11 4. 5^/ 0.81 2.63 3.78 2.17 5.0 1.12 3 .43 2 . 60 2/ 2 .20 6.0 1.16 4.95 1.05 2 .23 7. 0 1.43 5.10 1. 00 1.86 8.5 1. 63 4.93 1.07 1.76 1/ Hydrolysis initiated. 2/ Corrected, by curve fitting, from the actual titration result of 2.00.- It is evident from the foregoing results that the monoester content attainable, even by prolonged hydroly¬ sis, is definitely suppressed if the phosphorylation is allowed to continue at 125°C for several hours before the hydrolysis is initiated. However, if the hydrolysis time is extended an additional half hour to 2.5 hours total, the resulting monoester content will still be close to an acceptable minimum for water-resistant coatings applications and the free acid content, although undesirably high, will also be acceptable. A similar experiment, in which the phosphonylation was carried out 145°C showed the usual rise in diester content during the first hour but thereafter reaction being terminated after total of 2.5 hours, the diester content fell. The free acid and monoester contents remained essentially level. It thus appears that at 145°C, the diester P-OH, which is more strongly acid than H 3 P0 4 , will react with the EB and the equilibrium between the resulting triester and the water evolved by the reaction favors the triester. Accordingly, exten¬ sion of the normal phosphorylation time by a couple of hours would appear to be less deleterious at 145°C than at 125°C. Example 14 A series of six runs was made with different solvents or solvent mixtures as the reaction medium in the procedure of Example 12, except that super phospho- ric acid or a pre-formed EB/polyphosphoric acid reac¬ tion product was used as the acid source material. These runs are summarized in the following table: ■ υ EA r 0MP1 Run Acid Source Reaction Initial Millimoles/gram of solids x 10 2 # Material Medium % Solids Free acid Monoester Diester Triester 1 PP/EB-^ EB 74 2/ 1.15 6.53 0.72 0.98 2 EB 85% 2/ 66 1.13 4.91 1.30 2.04 n-butanol 15% 2a 3/ (After 3 hrs. 4 1.17 5.50 1.07 1.64 hydrolysis) 3 Super-acid-/ EB 40% 80.5 0.84 5.80 2.63 0.73 n-butanol 60% 4 DB 74.1 0.52 6.80 1.31 1.37 5 PiBT 40% 72.6 1.00 5.13 3.60 0.24 OΛ n-butanol 60% 6 Cyclohexanone 50% 70.0 0.42 5.20 1.58 2.80 n-butanol 50% Notes: 1. 35 grams polyphosphoric acid per 100 grams EB. t 2. Percents by weight. It will be seen that free acid levels acceptable for water-resistant coatings applications were attained in each run but that, except for DB and 40:60 EB/butanol, reaction media other than EB resulted in undesirably low, but not inoperable, monoester contents. The highest monoester/free acid ratio resulted when DB was used as the reaction medium. Example 15 A reaction product of 4 gram moles of EB per gram mole of R 4 O-, Q was prepared by stirring a mixture of 283.2 grams of EB and 85.2 grams of ^_* >-, Q , at a tempera¬ ture below 50°C, in a bath-cooled, 3-necked, round- bottom flask, until the mixture was a water white, viscous solution. To a pre-formed solution of 200 grams (111.111 meg), of Epoxy Resin A in 133.3 grams of cyclohexanone was added, with stirring, 6.26 grams of the P 4 0 1Q /EB solution equivalent to 20.3918 mmols or 0.9.992 phr of H 3 P0 4 . The resultant solution was heated to 125°C and held 0.5 hour at that temperature. 30.34 Grams of xylene were then stirred into the reaction mixture. Five grams of water was added and the mixture stirred at 113°C for a total of 4.5 hours, with samples being removed after 0.25, 1.50, 3 and 4.5 hours of hydrolysis time. The percent non-volatiles prior to xylene addi¬ tion was 60.7%. The analytical results were as follows: "BJ EACT OMPI Millimoles Per Gram of Solids xlO 2 Hydrolysis Free Time , hours H 3 P0 4 Mono- Ester Diesters Triesters Total 0.25 0.23 4.04 2.13 3.8 10.20 1.50 0.42 8.59 0.56 0.63 10.20 3 .00 0.46 9.28 0 0.46 10.20 4.50 0.49 9.87 0 0 10.36 The proportion of the total phosphorus finally recovered as monoester was 95.27%. Since all higher esters were hydrolyzed, the percent of oxirane actually converted to monoester can be taken assuming no EB ester groups remained as 17.49%. This corresponds to a 1,2-glycol to beta-hydroxy monoester group ratio of 4.72:1. The greater than 95% conversion of R 4 0 10 phospho¬ monoester experienced in the foregoing experiment is the highest achieved by the method of either the present application or U.S.P. 4,289,812. The hydrolysis mixture was neutralized with dimethylaminoethanol using a proportion of 2 moles per mole H 3 P0 4 charged as P 4 O 10 /EB product and diluted with water to provide an aqueous dispersion having a total solids content of 31 wt. %. Coatings resistant to boiling water and to acetone were obtained by drawing films on tin-free steel coupons from the dispersion containing Curing Agent A as a 20% solution in R-O and curing them. Example 16 A 100-liter pressure reactor equipped with a condenser and an agitator was charged with 70 Kg (59.3 equivalents) of Epoxy Resin D and 27.9 Kg of EB. The mixture was heated to 121°C and 240.8 g of a 25% solu¬ tion of polyphosphoric acid in EB was added with agita¬ tion. The mixture was heated at 124°C for 1.75 hours. The resulting phosphate ester mixture was then hydro¬ lyzed by adding through the bottom valve of the reactor a solution of 4.211 Kg of EB and 2.674 Kg of water at 124°C under a pressure of 18 psig (224 KPa). The solution was maintained at 140°C for 2 hours at 18 psig (224 KPa) and then cooled to 70°C and filtered and drummed. The resulting acid resin had a viscosity of 6325 cks (0.006325 m 2 /s) at 60°C as measured with a Canon Fenske viscosity tube at a solids content of 68.2%. The acid and ester concentrations found by titration of the final acid resin are: _2 free acid 1.62x10 millimoles/g solids _2 monoester 7.82x10 millimoles/g solids -2 a a diester 1.04x10 millimoles/g solids -2 triester 0.72x10 millimoles/g solids. The acid resin could be made water-dispersible by neutralization with a suitable amine. .An accelerated storage stability test at 80°C for 25 days revealed the following acid and ester concentrations: -BU E U OMPI ' -2 free acid 2.21x10 millimoles/g solids -2 monoester 9.47x10 millimoles/g solids di- and triesters *BTJ EAIΓ

Claims: CLAIMS 1. A process of preparing epoxy resin/phosphoric acid reaction products wherein a polyol polyether epoxide is reacted with a phosphoric acid source material and water in a reaction medium, the reaction product may optionally be salified with a base and diluted with water characterized by: (1) employing as the acid source material one derivable by the reaction of a hydroxylic (P-OH)-blocking agent with (a) R 4 0 10 / (k) a reaction product of P 4 0, Q with less than six molecular proportions of water or (c) an adduct of (b) with some of the oxirane groups in the epoxide, (2) employing as the medium a hydrophilic solvent for the epoxide which is acceptable as a component of a coating composition, (3) phosphorylating said epoxide by reacting P-OH groups in the acid source material, effectively in the absence of free water molecules, with oxirane groups in the epoxide until the content in the reaction mixture of species indistinguishable from H 3 P0 4 by titration drops to a preselected level and then -Bυ fT OMPI (4) subjecting the resultant reaction product to hydrolysis until the content in the reaction mixture of oxirane-derived phosphomonoester groups rises to a preselected value. 2. The process of Claim 1 characterized in that the acid source material is preformed in the absence of the epoxide. 3. The process of Claim 1 characterized in that the acid source material is formed in situ by the introduction of R 4 O-1 Q / ° r a reaction product thereof with less than six molecular proportions of water, to a solution of the epoxide comprising said blocking agent. 4. The process of Claim 1 characterized in that the acid source material is a reaction product of the blocking agent with super, pyro- or polyphosphoric acid. ^ 5. The process of Claim 1 characterized in that the blocking agent is phenol, n-butanol or a 2-alkoxyethanol. 6. The process of Claim 1 characterized in that the blocking agent and the reaction medium are the same. 7. The process of Claim 6 characterized in that the blocking agent and reaction medium are both 2-n-butoxyethanol. -^U E lT'

Inventors: CAMPBELL KENT DOUGLAS, KLEIN DIETER, LANGER HORST GUNTER, MARTIN PATRICK HENRY, CAMPBELL, KENT, DOUGLAS, KLEIN, DIETER, LANGER, HORST, GUNTER, MARTIN, PATRICK, HENRY
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1982
Main classification: C08L63
IPC codes: C08G59