HYDROTREATING CATALYST AND PROCESS

Abstract: Hydrotreating catalysts comprise a hydrogenating com­ ponent and a support comprising at least one porous refractory inorganic oxide, said catalyst having BET surface area of 150 to about 190 m² g. nitrogen desorption pore volume of 0.8 to about 1.2 cc/g in micropores with radii up to 600 Å, with at least 0.7 cc/g of such micropore volume in pores having radii ranging from 50 to 600 Å, mercury penetration pore volume of 0.1 to about 0.5 cc/g in macro­ pores with radii of 600 to 25,000 Å and bulk density of about 0.3 to about 0.5 g/cc. Hydrotreating process comprises contacting a hydrocarbon feed susceptible to upgrading with hydrogen in the presence of the aforesaid catalysts under hydrotreating conditions. The catalyst and process are particularly useful in hydrotreating feeds comprising high metals or high metals and sulfur content materials.

Description: HYDROTÀTI'LG CATALYST AND PROCESS BACKGROUND OF THS INVENTION This invention relates to upgrading of hydro carbon feed materials by catalytic hydrotreating. More particularly, the invention relates to an im proved catalyst and process for hydrodemetallation of heavy hydrocarbons. Decreasing supplies of high quality crude oils have focused considerable attention on refining lower quality feeds in recent years. Among such materials are those such as medium and heavy petroleum distillate fractions, crude oil resids, whole shale oils, tar sands oils and fractions thereof that require upgrading, for example, from the standpoint of removing or reducing the content of sulfur, nitrogen and/or metals, to facilitate conversion to more useful products. Catalytic hydrotreating is a well known means for upgrading feeds in need thereof. Typically, a feed is contacted with hydrogen in the presence of catalyst under conditions that vary somewhat depending on factcrs such as the particular feed to be upgraded, the type of process being oper ated, reaction zone capacity and other factors known to persons skilled in the art. In terms of general composition, hydrotreating catalysts typically comprise a hydrogenating component and a porous, refractory inorganic oxide support. Physical properties that are important from the standpoint of demetallation activity include surface area, pore volume and pore size distribution. General guidelines with respect to catalysts suitable for demetallation use are disclosed in U.S. 3,130,S=0 (Gleim et al.). In terms of composition, the cata lysts df Gleim et al. comprise a metallic component having hydrogenating activity, e.g., a Group V, VI, iron group or platinum group metal component, com cited .sith a refractory inorganic oxide having surface areas and pore volumes that can vary over ide ranges. Catalyst physical properties include surface areas of about 50-700 m2/g, pore diameters of about 20-600 ss and pore volumes of 0.1-20 cc/g. Lacking from the generalized teaching of Gleim et al. is a consideration of the interrelationships between and among physical properties and the effects thereof on catalyst performance. For example, the desirability of maximizing catalyst surface area and pore volume in order to provide high exposure of feed components to catalytically active sites, and thus, maximum activity, is well known. At the same time, however, if surface area and pore volume are too high, bulk density and mechanical strength of a catalyst can decrease to the point that use of the catalyst in hydrotreating processes is impractical or even impossible despite high activity. For example, in expanded bed processes, bulk density must be high enough to avoid substantial carryover of catalyst particles though not so high as to require unreasonably high space veloci'ies to ensure adequate bed expansion. Gf course in both expanded and fixed bed operations, it is desirable to maximize bulk density to the extent consistent with the aforesaid considerations in order to maximize catalyst loading and thereby maintain high productivity. Mechanical strength of catalyst particles is important from the standpoint of fixed bed use in that particles must be capable of withstanding the pressure drop through the bed. In expanded bed operations pressure drop through the catalyst bed is lower than in fixed bed processes; however, if catalyst particles do not exhibit sufficient crush strength and abrasion resistance collision with each other and reactor internals can lead to excessive frac entation of the particles and inferior perfor-ance. Pore size distribution also influences both catalytic activity and suitability for process use. Subject to the aforesaid considerations with respect to bulk density and crush strenght, it is desirable to provide catalyst particles having a high level of small or intermediate-sized pores because, for a given total pore volume, distributi on thereof in many smaller pores gives higher surface area than distribution in a smaller number of larger pores While smaller pores are thus desirable fro the standpoint of maximizing surface area, such pores also are more susceptible to plugging than larger pores, and thus, if too many pores of tco small size are present, demetallation activity often ce dines substantially during process use. If activity declines too rapidly, losses in productivity and/or increases in catalyst replacement costs are incurred. From the foregoing, it can be appreciated that a balance rust be struck between and among catalyst physical properties to ensure a desirable combination of activity, activity maintenance and suitability for process use. It is an object of this invent to provide a catalyst having such a desirable balance of properties. A further object to the invention is to provide an improved hydrotreating process using such catalyst. A tore specific object is to provide an improved process for upgrading hydrocarbon feeds susceptible to upgrading in terms of reduction in metals content. Another object of the invention is to provide a catalyst useful for demetallation and desulfurization of hydrocarbon feeds containing high levels of contaminants. A further aspect is to provide an overall process for upgrading the carbon feeds in need of upgrading wherein the reac tion is conducted in the presence of @@ catalysts in a first zone and further is carried cn in one C. one or more other catalysts. Other objects of the invention will be apparent to persons skilled in the art from the following description and the appended claims. We have now found that the objects of this invention can be attained by the provision of catalysts having a specific combination of surface area, pore volume, pore size distribution and bulk density tailored to provide high hydrotreating activity and exceptional activity maintenance along with a high degree of flexibility in terms of suitability for process use. In greater detail, the catalyst of this invention have moderate-to-high surface areas and pore volumes which, in conjunction with bimodal distribution of pore sizes and concentration of micropore volume in pores large enough to accomodate metals-containing components of hydrocarbon feeds, contribute to the superior activity and activity maintenance properties of the catalyst. In fact, the invented catalysts have the capacity to continue removing metals at metals loadings as high as 150200% based upon catalyst weight. Further, depending on the choice of hydrogenating component, the catalysts can exhibit substantial desulfurization activity in addition to demetallation activity. Bulk density varies over a relatively narrow range which, at its upper end, is well suited for fixed bed use, while at its lower end, is well suited for expanded bed use. Throughout the range, bulk density is high enouugh to ensure economically acceptable catalyst loadings. While not wishing to be bound by theory, it can be speculated that the physical properties of the invented catalysts are critical from the stand point of demetallation performance in that the @@@ distribution of pores provides a high @@@@@ volume that contributes to a surface area great enough to provide a high population of active sites available for catalyzing the reactions involved in demetallation, desulfurization and so forth. Concentration of micropore volume in pores large enough to accomodate metals-containing components of hydrocarbon feeds contributes to activity and maintenance of activity in that a high level of sites is provided in pores to which metals-containing components have access and plugging of pores is minimized. The bimodal pore size distribution of the invented catalysts also provides an appreciable level of macropores which serve at low surface area channels throughout the catalyst particles which facilitate rapid diffusicn of reactants into the smaller pores where demetallation reactions occur. It can be theorized that without the macropore network, metal sulfides and/or coke would deposit rapidly in the smaller pores near the external surface of the catalyst particles. This, in turn, would result in pore mouth plugging and catalyst deactivation. The low surface area of the macropores of the invented catalysts limits the concentration of active sites to which reactants are exposed during passage through the macropore network such that reaction in macropores is limited an access to the smaller high surface area pores is maintained. Proposals that may be of interest with respect to the present invention in disclosing attempts to provide hydrotreating catalysts having specific combinations of physical properties include U.S. 3,867,455 (Hamner et al.) which discloses particulate solids of "critical pre-selected pore size distribution, extremely low density, and ultra high porosity" for use in denitrogenation, desulfurization and demetallation of heavy crudes and resids, which particulate solids stratify during use in ebullated bed processes due to deposition of netals and/or coke to as to facilitate removal of spent solids. be particulate solids ray be a catalyst comprising hydrogenating component supported on an inorganic oxide. the particulate solids have 3t least about 50% of total pore volume in pores having radii of about 50 to about 150 , less than 20% of pore volume in pores having radii of 0-50 , surface area of at least about 200-600 m2/9 and total pore volume of 0.8-3.0 cc/g. Catalyst density ranges from 0.250.7 g/cc depending largely on hydrogenating metal content. Example 1 of damner et al. illustrates stratification of a mixture of alumina pellets with catalysts having properties within the aforesaid ranges although no denitrogenation, desulfurizaton or demetallation results are reported. Examples 2 and 3 simulate use of the patentee's catalysts to reduce metals content of a heavy hydrocarbon feed from 480 pp to 50 Opp in a first stage and from 50 pp to less than 5 ppm in a second stage. Hamner et al. fails to disclose or suggest either the surf area or bimodal pore size distribution of the invented catalysts. U.S. 3,876,523 (Rosinski et al.) discloses hydrodemetallation-hydrodesulfurization catalysts comprising a hydrogenating component composited with a refractory support and having a bimodal dis- tribution of pores such that not less than 60% pore volume is in pores of 50-100 ? radis and not less than about 5 of pore volume is in pores greater than 250 radius. Unlike the invented catalysts, those according to Rosinski et al. have such areas of 40-150 mê/g, preferably less than 100 mê Catalysts similar to those of nosinski t al. disclosed in U.S. 4,016,067 (Fischer et al.) U.S. 4,082,695 (Rosinski et al.). U.S. 3,898,155 (Wilson) discloses simultane demetallation and desulfurization of hea using catalysts comprising a Group VIB metal and at least one Group VIII metal composited with an alumina support, such catalysts having a bimodal distribution of pores such that macrocore ( > 300 pore radius) volume is 10-40% of total tore volume, microcore (0-300 A pore radius) volume is 60-90% of total pore volume and at least 80 of such micropore volume is in pores having radii of at least 50 2. According to Wilson's broad teaching, the disclosed catalysts have surface areas of at least 100 m2/g, total pore volumes of at least 0.5 cc/g and average pore diameters of at least 100 calculated as 4V/A. However, the -highest total pore volume reported in the patentee's examples is 0.879 cc/g. In contrast, total pore volume of the invented catalysts is at least 0.9 cc/g and typical micropore (radii up to 500 ) volume of the invented catalysts is greater than Wilson's total pore volume, though it is noted that a portion of Wilson's macropore radius range falls within the micropore range of the invented catalysts. Further, iilson rails to disclose or suggest the inventeo catalysts' combination of surface area and bulk density. U.S. 4,102,322 (Mulaskey) discloses hydrotreat ing catalysts comprising a igidly interconnected pac of irregularly shaped particles of specified sizes. There is a bimodal distribution cf pores in the pack, with access pores or 500-75,000 A radii contributing at least 3% of pore volume. Sur face area of the disclosed catalysts ranges from 0.1 to above 500 mê/g, with 120-200 mê/g being pre ferred. The patentes also teaches that the catalyst have total pore volume of 0.5 cc/g with about @@@ thereof being in the form of micropores ( < 600 ) and about 300 being in the form of interconnected, access micropores. Column 1 lines 30-38. The patentes fails to disclose or suggest either the otal pore volume or pore size distribution of the nvented catalysts. Other proposals that may be of interest in disclosing demetallation catalysts having specific combinations of physical properties are summarized in Table I wherein "SA" stands for surface area, FV stands for tore volume and "PSD" stands for pore size distribution. TABLE 1 PSD U.S. PATENT SA PV PORE (INVENTOR) (mê/c) (cc/g) % PV RADIUS ( ) EMI9.1 <tb> 3,977,961 <SEP> # <SEP> "minimal" <SEP> 0-25 <tb> (Hamner) <SEP> #20(1) <SEP> 50-100 <tb> 3,998,722 <SEP> #200- <SEP> <SEP> 0.8-3.0 <SEP> #15(2) <SEP> <SEP> 75-125 <tb> (Mayer <SEP> et <SEP> al.) <SEP> 600 <tb> 4,014,821 <SEP> #15(3) <SEP> <SEP> 87.5-137.5 <tb> (Hamner) <tb> "minimal" 150-175 4,003,828(4) 172- 0.41- UNSPECIFIED (Eberly, Jr.) 292(5) 0.56(5) 4,089,774 125-210 0.4-0.65 #10 < 15 (Oleck et #45 15-75 al.) #15 > 150 4,119,531 #120 #0.7 UNSPECIFIED (Hopkins et al.) 4,192.736(4) UNSPECI- 0.3-1.1 #50 30-125 (Kluksdahl) FIED #3 > 500 4,225,421 140-300 0.4-1.0 3-30 #300 (Hensley, Jr. 97-70 < 300 et al.) 60-95% of 25-100 PV in R < 300 TABLE 1 (Cont'd) PSD U.S. PATENT SA PV PORE (INVENTOR) (mê/g) (cc/g) % PV RADIUS ( ) 0-15% of 100-300 PV in R < 300 4,242,236 150-300 0.75-1.3 < 10 > 500 (Blakely) 0-15; of 100-300 PV in R < 300 (1) Catalyst of average particle diameter up to 1/50". (2) Catalyst o average particle diameter o 1/50- 1/25". (3) Catalyst of average particle diameter of 1/25- 1/8" (4) Catalysts contain phosphated-alumina supports. (5) Values taken from patentee's examples. Other proposals of possible interest from the standpoint of disclosing catalysts having specific combinations of properties, though lacking in reporte demetallation activity as well as distinguishable in terms of physical properties are summarized in TABLE 2 PSD U.S. PATENT SA PV PORE (INVENTOR) (mê/g) (cc/g) PV RADIUS ( ) EMI11.1 <tb> 3,622,500(1) <SEP> 0.3- <SEP> < 125 <tb> (Alpert <SEP> et <SEP> 0.5 <SEP> cc/g <tb> <SEP> al.) <tb> <SEP> UNSPECI- <SEP> 0.4 <tb> 3,870,623 <SEP> /FIED <SEP> 1.1 <SEP> 0.1 <tb> (Johnson <SEP> et <SEP> 0.6 <SEP> cc/g <tb> <SEP> al.) <tb> 3,803,027(2) #100 0.41- 0.4- 7-300 (Christman et 0.58(3) 0.8 cc/g al.) 3,843,509(4) 181- 0.43- #0.30 cc/g 0-300 (Suto et al.) 283(3) 0.57(3) #25% of 0-30 PV in R=0-300 #40% of 75-300 PV in R=0-300 #0.25 cc/g 753,966,588(5) 225-400 1.0- > 50% < 500 (Beaty, Jr.) 2.75 TABLE 2 (Cont'd.) SD U.S. Patent SA PV PORE (INVENTOR) (mê/g) (cc/g) PV RADIUS ( ) 4,008,149(6) 250-300 0.5- #80% of 30-75 (Itch et al.) 1.0 PV in R= 0-75 < 20% of 75-150 PV in R= 0-150 0.45- 0-300 0.6 cc/g < 0.1 cc/g 75-500 4,051,021 150-450 0.3-1.0 #50 % 35-80 (Hamner) 4,066,572(7) 62-311 0.51-1.1 6-60% < 50 (Choca) (1) Bulk density = 0.4-1.0 g/cc. (2) Bulk density = 0.3-0.8 g/cc and Specific Volume of ores (defined as density x volume in pores with radii of 7-3-00 x volume % of PV in pores with radii of 50-300 ) #20. (3) Values taken rom patentee's examples. (4) Examples raport bulk density = 0.6-0.31 g/cc. (5) loosr bluk density = 7.5-25 lb/ft = 0.12 0.40 g/cc. (6) Bulk density = 0.5-1.0 g/cc. (7) Phosphated-alumina support. All values taken from patentee's examples. As will be apparent from the following description, none of the patents discussed hereinabove and summarized in TABLES 1 end 2 discloses or suggests the noval combination of physical propertier thet we have founf to yield the superior hydrotreating results, especially in terms of demetallation, that are attained according to the present invention. DESCRIPTION OF THE INVENTION Briefly, the catalysts of our invention comprise a hydrogenating component composited with a support, such catalysts having BET surface area of 150 to about 190 mê/g, pore volume of about 0.8 to about 1.2 cc/g as determined by nitrogen desorption in micropores having radii up to 600 , with at least 0.7 cc/g of such micropore volume in pores having radii of 50 to 600 , pore volume of 0.1 to about 0.5 cc/g as determined by mercury penetration in macropores having radii of 600 to 25,000 and bulk density of 0.3 to 0.5 g/cc. For use in hydrotreating hydrocarbon feeds susceptible to upgrading, a feed and hydrogen are contacted in the presence of the invented catalysts under hydrotreating conditions. The invented catalysts are particularly useful firat stage catalysts in multi-stage hydrotreating processes in which predominant first stage reactions comprise demetallation reactions and predominant subsequent stage reactions comprise desulfurization reactions. Especially good results are attained in demetallation of high metals or high metals and high sulfur content feeds. In greater detail, the hydrogenating component of the invented catalysts comprises a metallic component having hydrogenating activity. Suitable metals include these of Group VID, Group VIII and venedium as well as combinations thereof. Specific examples of the Group VIB and VIII metals include chromium, molybdenum, tungsten, iren, cehalt, nickel, ruthanium, rhedium, polledium, osmium, iridium and platinum. These can be present in elemental form, as oxides or sulfides, or as combination thereof. Among such metals, these of Group VIB are preferred becouse, unlike the Group VIII metals and vanadium, the Group VIB metals promote substantial desulfurization in addition to demetallation. Among the Group Vi metals, molydbenum is most preferred from the standpoint of overall activity, wit tungsten being less preferred and chromium being least preferred. Amoung the Group VIII metals, the non-noble metals iron, cobalt and nickel are preferred from the standpoint of demetallation activity and cost with cobalt and nickel being rost pre erres. Various combinations also are contemplated, preferred combinations being those comprising at least one Group VI3 metal in order to attain both desulfurizatic and demetallation activity. Specific examples of preferred combinations include cobalt-molydbenum, nickel-molybdenum and vanadium-molybdenum. The support component or the invented catalysts comprises at least one percus refractory inorganic oxide. The precise compositon of the support is relatively unimportant so long as the required physical properties are attained. Examples of useful supports include alumina, silica, silica-alimina, silica-stabilized-alumina, phosphated-alumina, sil stabilized-phosphated-alumina, fluorided-alumina, alumina-aluminum phosphate, boria-alumina, magnesi alumina, boria, magnesia, titenia, zirconia, and the like. Support compositions presently preferre from the standpoint of catalysts performance are these comprising alumina and at least one oxide of phospherus and these comprising alumina and silica. Silica-stabilized alumina is an example of the lat Certain of these also eifer advantages in these of easy attainmen of suitable physical properties by access of reactants to active mites; however, mechanical streangth and bulk density decrease so much that the catalysts is essily demaced during and must be replaced rapidly. Preferably, in order to maximine exposure of reactansts to active hydrogenating sites while ensuring sufficient crush strength and bulk density, BET surface area ranges from about 150 to about 1s0 mê/g. Best results are attained when the majority of catalyst particles have surface areas of about 160 to about 170 m2/g. the distribution o pores cf the invented catalysts is such that micropore volume is 0.8 to about 1.2 cc/g as determined by nitrogen desorption and macropore volume is about 0.1 to about 0.5 co/o as determined by mercury penetration. For purposes hereof, micropores are define as pores with radii up to 600 while macropores are pores wit radii of 600-25,000 A. As noted hereinabove, a relatively large micropore volume appears to be important fro the standpoint of attaining high exposure of rea to catalytically active sites, while a small b but appreciable macropore volume is necessary to ensure access to the micropores and activity meintenance. If either micro-or mapropore volume is too high, however, catalysts methenical strength and bulk densit can suffer. In order to attain maximum demetaliation activity and maintenance of such activity while maintaining a desirable level of bulk density and mechanical strength, micropore volume preferably ranges from about 0.9 to about 1.3 cc/g and macropore volume preferably renges from about 0.13 to about 0.50 cc/g. Total pore volume, i.a., the run or micropore volume and macropore volume rengens from the to about 1.5 cc/g, with about 1.1 to about 1.1 cc/g to about steaming to increase average pore diameter without appreciably decreasing pore volume. Steaming of such supports as well as other suitable supports is described in detail in our copending applications Serial Nos. 274,553 and 274,499, respectively,filed of zven date herewith. Relative proportions of hydrogenating component and support are not critical, though if too little hydrogenating component is present, initial activity will be lower than desired such that an activation period, during which feed metals are laid down on the catalysts, will be required for the catalysts to reach maximum activity. Preferably, the invented catalysts contain sufficient hydrogenating component that maximum demetallation activity is achieved before deposition of appreciable levels of metals from a feed. It also is preferred to limit hydro genating component concentration somewhat because metals holding capacity typically decreases with increasing hydrogenating metal concentration. More preferably, hydrogenating component concentration ranges from about 2.5 to about 15 wt. %, calculated as metal oxide and based on total catalysts weight, in order to balance initial activity against metals holding capacity. Must preferably, hydrogenating component content ranges from about 3.5 to about 8 wt.%. Catalysts physical properties that are important from the standpoint of demetallation activity and suitability for proceas use include surface area, pore volume, pore size distribution, and bulk density. BET surface area ranges from 150 about 190 mê/g. Surface areas less than 150 mê/g are disolventageous because contact between active hydrogenation sites and feed components is limited such that catalytic activity suffers. Contact areas greater than about 190 mê/g are suitable from the standpoint of ensuring steaming to increase average pore diameter without appreciably decreasing pore volume. Steaming of such supports as well as other suitable supports is described in detail in our copending applications Serial Nos. 274,553 and 274,499, respectively,filed of zven date herewith. Relative proportions of hydrogenating component and support are not critical, though if too little hydrogenating component is present, initial activity will be lower than desired such that an activation period, during which feed metals are laid down on the catalysts, will be required for the catalysts to reach maximum activity. Preferably, the invented catalysts contain sufficient hydrogenating component that maximum demetallation activity is achieved before deposition of appreciable levels of metals from a feed. It also is preferred to limit hydro genating component concentration somewhat because metals holding capacity typically decreases with increasing hydrogenating metal concentration. More preferably, hydrogenating component concentration ranges from about 2.5 to about 15 wt. %, calculated as metal oxide and based on total catalysts weight, in order to balance initial activity against metals holding capacity. Must preferably, hydrogenating component content ranges from about 3.5 to about 8 wt.%. Catalysts physical properties that are important from the standpoint of demetallation activity and suitability for proceas use include surface area, pore volume, pore size distribution, and bulk density. BET surface area ranges from 150 about 190 mê/g. Surface areas less than 150 mê/g are disolventageous because contact between active hydrogenation sites and feed components is limited such that catalytic activity suffers. Contact areas greater than about 190 mê/g are suitable from the standpoint of ensuring access of reactants to active sites; however, mechanical strenght and bulk density decrease so much that the catalyst is easily damaged during use and must be replaced rapidly. Preferably, in order to maximize exposure of reactants to active hydrogenating sites while ensuring sufficient crush strenght and bulk density, BET surface area ranges from about 150 to about 180 mê/g. Best results are attained when the majority of catalyst particles have surface areas of about 160 to about 170 mê/g. The distribution of pores of the invented catalysts is such that micropore volume is 0.8 to about 1.2 cc/g as determined by nitrogen desorption and macropore volume is about 0.1 to about 0.5 cc/g as determined by mercury penetration. For purposes hereof, micropores are defined as pores with radd up to 600 while macropores are pores with radii of 60-25,000 . As noted hereinabove, a relatively large micropore volume appears to be important from the standpoint of attaining high exposure of reactants to catalytically active sites, while a small but appreciable macropore volume is necessary to ensure access to micropores and activity maintenance. If either micro- or macropore volume is too high, however, catalyst mechanical strenght and bulk density can suffer. In order to attain maximum demetallation activity and maintenance of such activity while maintaining a desirable level of bulk density and mechanical strenght, micropore volume preferably ranges from about 0.9 to about 1.3 cc/g and macropore volume preferably ranges from about 0.15 to about 0.55 cc/g. Total pore volume, i.e., the run of micropore volume and macropore volume range from 0.9 to about 1.5 cc/g, with about 1.1 to about 1.9 is @@@teing preferred from the standpoint of attaining a desir- able overall combination of demetallation activity, activity maintenance and other properties Micropore distribution also is important from the standpoint of demetallation activity and activity maintenance. As noted hereinabove, at least 0.7 cc/g ofmicropore volume is concentrated in pores having radii of 50 to 600 2. Preferably, at least 0.75 cc/g of micropore volume is in pores having radii of 50-600 in order to maximize activity and minimize activity decline. Micropore volume in pores 50-600 in radius preferably is distributed such that about 15 to about 60% thereof is provided by pores having radii of 50-100 A and about 40 to about 85% thereof is provided by pores having radii of 100-600 . Though not recuired, it also is desir able to limit micropore volume in pores having radii less tan 50 A to below about 0.15 cc/g as such pores contribute only insubstantially, if at all, to activity. Best results in terms of demetallation activity and activity maintenance are attained with catalysts containing up to about 0.15 cc/g micropore volume in pores having radii less than a-C 5 at least about 0.S cc/ of micropore volume in oreos having radii of 50-600 , and of that, about 20 to about 55% in pores having radii of 50 to 100 and about 45 to about 30 in pores having radii cf 100 to 600 . Bulk density, while not critical from the point of demetallation activity per se, is impo in terms of utility of the invented catalysts i wide range of processes and under a wide range process conditions. Bulk density of the invent catalysts ranges from about 0.3 to about 0.5 with bulk densities in the upper portion of the range being best suited for fixed bed use and densites in the lower portion of the range the ent suited for expanded bed use. Below about @d @yse it is difficult to load enough catalyst nto typical reactors to attain economically feasible results, and the catalyst is too li9ht to be used in expanded bed processes without substantial carryover. Dulk densities above about 0.5 g/cc are suitable from the standpoint of process utility but are difficult to attain given the surface areas and tore volumes of the invented catalysts. Bulk densities that are preferred from the standpoint of balancing catalyst loading requirements against physical properties important with respect to de netallation range rrom about 0.38 to about 0.45 g/cc. Other physical properties which are not critical with respect to catalyst activity or process use but may influence performance include mechanical strength, abrasion resistance and average particle size. Mechanical strength should be at least high enough to permit use in a given process without undesirable fragmentation or other damage. Similarly, abrasion resistance should be high enough to permit the catalyst particles to withstand particle to particle contact as well as contact between particles d reaction zone internal, particularly in expanded bed processes. Preferably, crush strenght of the invented catalysts is such tat a particle 1/8-inch in lenght and 1/32-inch in diameter will withstand at least about three pounds of pressure. Catalyst size varies somewhat depending on the particular process to be used. Preferred catalysts range from about 1/50 to about 1,15-inch diameter. Catalyst shape can vary widely depending on process requirements. The invented catalysts can be prepared by any suitable method. Conveniently, a support of predetermined shape and size is impregnated with appropriate amounts of one or more solutions of compound of toe metal or metals of the hydrogenating component, such compounds being convertible to metal oxides on calcination. Alternately, a solution or solutions of metal compounds convertible to oxides is mized with powdered support and then shaped. The preferred solvent for the impregnating solutions is water cwing to its cost; however, alcohols as well as various other solvents for the metal compounds can be used if desired. Soluble compounds of the hydrogenating metals are well known to persons skilled in the art. Following incorporation of hydrogenating metal compound or compounds with the support, the result is heated in the presence of a gas containing molecular oxygen at a temperature and for a time sufficient to convert the metal compound or compounds to metal oxices. Preferred temperatures range from about 800 to about 1,200 F (about 427 to about 649 C) and preferred times range from about 1/2 o about 20 hours. As noted hereinabove, the support component of the invented catalyst can vary widely, in terms or composition so long as ha saquired physical proper- ties of the final catalyst can ac attained. In order to attain suc properties it often is necessary to employ pre-shaped support having appropriate properties in preparation of the catalyst. Prefer- ably, surface area and/or core volume of the support is at least slightly greater than that of the final catalyst as incorporation of metals and calcination tend to slightly decrease surface area and pore volume. Pore size distribution also must be similar Certain support materials having higher than desired surface area and/cr insufficient core volume In pores of sizes that ccntr ihute significantly to activity and maintenance thereof can be rendered suitable for use accord 'g to this invention, for example, by heating in the presence of steam as discussed in greater detail hereinbelow. Of course, it also is contemplated to use supports that are not pre-shaped, in which case steps should be taken to ensure that the final catalyst ill have the proper physical properties after calcination and shaping operations. specific catalyst according to the present invention is one comprising a hydrogenating component and a phosphated-alumina support which, prior to incorporation of hydrogenating component, is calcined in the presence of steam to open its pores as described in detail in our aforesaid, copending application Serial No. 274,553 filed of even date herewith and incorporated herein by reference. Prior to calcina ticn in the presence of steam, the phosphated alumina preferably has a surface area of about 190 to about 400 mê/g and pore volume o about 0.9 to about 1.5 cc/g; however, steaming serves to increase average pore diameter without appreciably decreasing pore volume such that a final catalyst having physical properties required according to the present invention can be attained. Another specific catalyst according to the present invention 5 one comprising a hydrogenating component an a support comprising at least two refractory inorganic oxides. Supports comprising alumina and silica, particularly those such as silica stabilized aluminas having about 2 to about 10 wt. @ silica based upon support weight, give particularly good results in terms of demetallation activity and activity maintenance. Such supports can be heated in the presence of steam prior to deposition of hydrogenating component if necessary or desirable from the standpoint of attaining suitable physical properties. @@@@ of such supports is described in detail in the @@@ depending application Serial No. 271,499 filed of even data herewith and incorporated herein by reference. A preferred combination of refractory oxides that gives good results in terms of steaming and ultirnate catalyst performance is alumina in combination with silica, particularly about 2 to about 10 wt 5 silica based upon support weight. It is to be understood that methods other than heating in the presence of steam in accordance with the aforesaid applications are contemplated for attaining support materials of suitable pore volume and surface area. Prior to use in hydrotreating of hydrocarbon feeds the invented catalysts may be subjected to a presulfiding treatment if desired. When the hydrogenating component consists of one or more Group VIB metals, presulfiding treatment has little effect on catalyst performance. However, when the hydrogenat ing component contains other metals it is preferred to conduct the presulfiding treatment to convert the metals of the hydrogenating component to partially reduced metal sulfides which typically are more active than the elemental metals or the metal oxides. A sulfiding pretreatment that is preferred from the standpoint of cost and convenience involves contacting a catalyst with a mixture of hydrogen and hydrogen sulfide at varying pressure and increasing temperature over a period or time. Other suitable presulfiding treatments involve contacting -he catalyst with hydrogen and carbon disulfide or a light hydrocarbon oil containing sulfur compounds at elevated tempera ture for a period of time sufficient to affect con version of the metal components of the hydrogenating component to metal sulfides. The process according to this invention comprises contacting a hydrocarbon feed susceptible to upgrading with hydrogen tn e presence of the above-described catalysts under hydrotreating conditions. Owing to the high demetallation activity of the invented catalysts, the same preferably are used to hydrotreat reeds having at least appreciable metals content, e.g., at least about 30 ppm. Examples include crude oils, topped crude oils, petroleum hydrocarbon residua, atmospheric and vacuum resids, oils obtained from tar sands, residua derived from tar sand oil, and hydrocarbon streams derived from coal or oil shale. Fixed and expanded bed hydrotreating processes are contemplated herein. In fixed bed processes, hydrocarbon feed and a hydrogen-containing gas are passed downwardly through a packed bed of catalyst under conditions, such as temperature, pressure, hydrogen flow rate, space velocity, etc., that vary somewhat depending on the choice of feed, reactor capacity and other factors known to persons of skill in the art. As noted hereinabove, catalyst crush strength is important in fixed bed operations due to the pressure drop resulting from passage of hydrocarbon feed and hydrogen-containing gas through the packed catalyst bed. Catalyst size and shape also can be important in fixed bed operations due to their effect not only on pressure drop througt the bed but also cn catalyst loading an ccntact between catalyst and feed components. The use of larger catalyst particles at the t of a catalyst bed and smaller articles throughout the remainder of the bed can lead to decreased pressure crop. Catalyst in the form of spheres or extrudate, preferably about 0.01 to about 0.1 inch (about 0.25 to about 2.5 mm) in diameter, give good results in terms of promoting adequate contact between catalyst and feed components while avoiding excessive pressure drop through a catalyst bed. More preferably, particles of about 1/32 to about 1/16-inch (about 0.79 to about 1.6 mm) diameter are used. T@@@ cloverleaf, cross and "C"-shaped catalysts such as are disclosed in commonly assigned S. 3,674,680 (Hoekstra et al.) give particularly good results in terms or maximizing catal"st efficiency nd promoting a high level of contact between catalyst and feed components. Further details with respect to fied bed use of the invented catalysts are found in our above-referenced, copending applications Serial Nos. 274,553 and 274,499. In expanded bed processes, a packed catalyst bed is expanded and mobilized by upflow of hydro carbon feed and hydrogen-containing gas at space velocities effective to provide adequate mobilization and expansion, and thereby promote contact between catalyst particles and reactants, without substantial carryover of catalyst particles. As noted herein above, catalyst bulk density is important from the standpoint of attaining appropriate bed expansion and mobilization at economically practical space velocities. Catalyst particle size ano shape also are important in this regard. Preferred catalysts for expanded bed use are ex rudates of about 0.02 to acout 0.05 ine (about 0.5 to about 1.3 mm) diameter, with about 1/32-inch (about 0-79 mm) being most preferred. A preferred expanded bed process, particularly for treatment of high metals or high metals and sulfur content feed is an ebullated bed process. In such processes, catalyst preferably is present in an amount sufficient to occupy at least about 10 volume z of the expanded bed and is continuous lv added to the reaction zone to compensate or scent catalyst which is continously withdrawn. Speci details with respect to ebullated bed processes are found in Example III hereinbelow and U.S. 3,138,286 (Van Driesen), U.S. 2.987,465 and its U.S. Re 25, (both Johanson) and U.S. 3,630,387 (Mounce et al.), which are incorporated herein by reference. Irrespective of whether a fi::ed or expanded bed operation is employed, hydrotreating conditions according to tis invention will vary depending largely on the particular feed employed. Suitable conditions for various feeds are summarized in the following table: : SPACE TEMPER- H2 VELOCITY PRESSURE ATURE RATE (lb/hr/lb FEED (psig) ( F) (SCFB) Catalyst) DISTILLATES* 300-750 600-725 400-1000 2-5 GAS OILS* 500-1000 600-750 800-1600 1-4 ATMOSPHERIC 500-2000 600-850 500-3000 0.5-2 RESIT VACUUM 1000- 600-850 1000- 0.2-3 RESID 10,000 10,000 *Specific examples of distillates and gas oils particularly well suited for hydrotreating according to the invention are those derived from oil shales which often contain substantial levels of arsenic. According to a preferred embodiment of the invention, high metals cr high metals and high sulfur content feed comprising resid is contacted with hydrogen in the presence of an ebullating bed of the invented catalyst at an average temperature of about 700 to about 900 F (about 371 to about 482 C) total pressure of about 500 to about 6,000 psig (about 3.55 to about 41.5 MPa), hydrogen partial pressurer of about 500 to about 3,000 psig (about 3.45 to about 20.7 MPa), hydrogen flow rate or hy hydrogen addition rate of about 1,000 to about 10,000 SCFB (about 178 to about 1780 m3/m3) (gas volumes measured at 15.6 C and 101.3 kPa), and LHSV of about 0.2 to about 2.5 volumes of hydrocarbon per hour per volume of catalyst. Preferred operating conditions comprise an average temperature of about 730 to about 910 F (about 335 to about 432 C), total pressure of about 1.200 to about 3,000 psig (about 8.4 to about 20.3 MPa), hydrogen partial pressure of about 1,200 to about 2,000 psia (about 8.3 to about 13.8 MPa), hydrogen flow rate or hydrogen addition rate of about 8,000 SCFB (712 m /m ), and LHSV of about 0.4 to about 2.0 volumes of hydrocarbon per hour per volume of catalyst. Preferred feeds for such operations include vacuum and atmospheric resids derived from petroleum crudes, coal and shale oils having at least 100 ppm metals and an appreciable level of sulfur as well as blends of such resids with lighter materials e.g., heavy vacuum gas oils. A particularly preferred process for using the invented catalysts is in multi-stage hydrotreating of high metals and sulfur content feeds wherein metals content of te feed is reduced by treatment in an initial stage in which the invented catalyst is used, followed by one or more subsequent stage or stages In which a catalyst having high hydrode- sulfurization activity is used. Individual stages can be conducted in single or multiple zones. Hydro- desulfurization catalysts particularly well suited for use in conjunction wit the inventec catalysts in such multi-stage processes are disclosed in our commonly assigned U.S. 4,131,502, and 4,212,729, commonly assigned U.S. 4,224,144 (Hensley et al.), our commonly assigned, allowed application Serial No. 168,297 filed July 14, 1980 and commonly assigned application Serial No. 131,433, filed August 4, 1980, in the name of Hensley, Quick and Hopkins. All # of such patents and applications are incorporated herein by reference. The following examples illustrate the present invention, it being understood that the same are for purposes of illustration and not limitation. In all examples, micropore volume and pore size distribution were determined by nitrogen desorption using a Digisorb 2500 instrument. Macropore volumes were determined by mercury penetration using a mercury porosimeter. EXAMPLE I A pilot scale catalyst comprising 4 wt.% MoO3 composited with a support comprising 96 wt.% A1203 and 4 wt.% SiO2 was prepared for us by American Cyanamid, Inc. Physical properties of the catalyst were as follows: BET SURFACE AREA 186 m2/g PORE VOLUME MACROPORE 0.49 cc/g MICROPORE 1.00 cc/g TOTAL 1.489 cc/g AVERAGE POINT DIAMETER (D= 104/A) SOD A PORE SIZE DISTRIBUTION PORE VOLUME PORE RADII ( ) RELATIVE (%) ABSOLUTE (cc/g) 0-50 8.3 0.13 50-100 30.7 0.46 100-600 27.3 0.41 600-25,000 33.2 0.49 BULK DENSITY: 0.33 g/cc CRUSH STRENGTH: 2.4 lbs/1/8 Demetallation activity of the catalyst was tested according to the following procedure. Prior to usem, the catalyst was screened to 14-20 mesh (U.S. Steve Ferier), corresponding to 1.41-0.85 mm particle size, and calcined in still air at 538"C (10000) for 1 hour. Subsequently, the catalyst was cooled in a desiccator. Catalyst was packed into a bench-scale test unit having automatic controls for pressure, flow of reactants, and temperature. The reactor was made of 0.953 cm (3/8-inch) inside-diameter stainlesssteel, heavy-walled tubing. A 0.318 cm (1/8-inch) outside-diameter thermowell extended up through the center of the reactor. The reactor was heated by an electrically-heated steel block. The 14-20-mesh catalyst material was supported on 8-10 mesh (2.381.68 mm) alundum particles. Approximately 15 cubic centimeters of catalyst were employed as the catalyst bed in each test. This amount of catalyst provided a catalyst bed length of about 25.4 cm (10 in). A 25.4 cm (10 in) layer of 8-10 mesh (2.38-1.68 mm) alundum particles was placed over the catalyst bed in the reactor for each test. The catalyst that was employed was located in the annular space between the thermowell and the internal wall of the 0.953 cm (3/8-inch) inside-diameter reactor. The unit was brought to operating conditions and hydrogen and hydrocarbon feed were charged to the reactor, the latter by means of a positive displacement pump (Ruska). Hydrogen addition rate ranged from 890 to 1424 m3/m3 (5000-8000 SCFB) and hydrocarbon space velocity (LHSV) was 1 cc hydrocarbon per hour per cc of catalyst,. Operating conditions included a total pressure of 12.5 MPa (1800 psig) and temperature of 416eC (780OF). In order to determine demetallation activity at increasing metals loadings, the hydrocarbon feed to the reactor was varied intermittently between an Ardeshir vacuum resid and a Jobo vacuum resid. Feed Stock.'prcparties are reported in Table 3. TABLE 3 (Feed s toc k Properties) FEED: ARDESHIR JOBO GRAVITY ( (0API) 3.2 5.2 COMPOSITION (wt %) OILS 12.7 22.9 ASPHALTENES 15.5 14.6 RESINS 71.8 62.5 CARBON RESIDUE (wt %) 27.8 22.0 CARBON (wt %) 83.65 83.54 HYDROGEN (wt %) 9.73 9.78 NITROGEN (wt %) 0.50 0.97 SULFUR (wt %) 5.7 4.85 OXYGEN (wt %) 0.3 0.96 NICKEL (ppm) 72 167 VANADIUM (ppm) 262 799 The Ardeshir feed is representative of typical high metals, high sulfur feeds of the type particu larly well suited for hydrotreating with the invented catalysts while the Jobo feed, also well suited for treatment according to this invention, is an extremely high metals feed and was used primarily to attain high metals loading at a rapid rate. The Ardeshir feed was run on days 1 to 6, resulting in a metals loading of 10 wt z based upon catalyst weight. On day 7, the feed was changed to Jobo which then was run through day 20 resulting in 51.7 wt to metals loading. Ardeshir was again run from day 21 to day 24 and metals loading increased to 57.8 wt t . Jobs was run from day 25 to day 41, resulting in 110 wt 9 .metals loading. From day 42 to day 45, Ardeshir was again run such that at day 45, metals loading was 116 wt t. The results of the tests are presented in the accompanying Figure 1 in which the above described catalyst is identified as CATALYST A. Also shown in Figure 1 are results obtained with another cata- lyst (CATALYST NO. 3) according to the invention. Preparation, composition and properties of CATALYST NO. 3 are described in detail in EXAMPLE TI as is the method of testing that catalyst. Relative activity of each catalyst is plotted against the wit.% of metals (nickel and vanadium) that were retained on the catalyst. This relative activity was obtained by dividing the volume of a reference catalyst (CATALYST NO. 2, EXAMPLE II), having an assigned activity value of 100, by the volume of the experimental catalyst that is needed to reduce the metals content of the feed to the same metals content when operating at constant temperature and pressure. As can be seen from the figure, relative demetallation activity of CATALYST A was high at the start of the test and remained hiqh even at 100% metals loading. EXAMPLE 11 The catalysts and testing described in this example are identical to those described in Example I of application Serial o. 274,553 and 274,499. The accompanying Figure 2 is identical to Figure 2 of such applications. Four catalysts were prepared in the laboratory as described hereinafter. Each of the laboratory preparations involved adding an aqueous solution of ammonium heptamolybdate to a support material, thoroughly mixing the result, permitting the resulting mixture to stand for a period of time as designated hereinafter, drying the material under a heat lamp and calcining the dried material in air for 2 hours at a temperature of 1,000OF (5380C). Two of the catalysts, (Catalysts Nos. 1 and 4), were prepared using supports obtained from Katalco Corporation which were prepared to contain from about 8 wtt to about 10 wt%'oxides of Phosphorus, calculated as P205. Bulk densities of the supports used to prepare Catalysts Nos. 1 and 4 were 0.35 and 0.42 g/cc respectively. Catalyst No. 2 was prepared by steaming the support of Catalyst No. 1, and then incorporating the hydrogenating component while Catalyst No. 3 was prepared by steaming the support of Catalyst No. 4 and then incorporating the hydrogenating component. In preparation of Catalysts Nos. 2 and 3, steaming was performed at a temperature of approximately 816"C (1,500OF) for 30 minutes at a steam pressure of 0.8 atm. in a 3.8-cm (1.5-in) inside diameter quartz tube that was held in a vertical position within a tube furnace. A mixture of steam and nitrogen (approximately 80 volume % steam) was controlled by operating needle valves and was measured by flow meters. The steam-nitrogen mixture was introduced into the bottom of the quartz tube and flow was adjusted to be maintained at a rate of about 200 cc/min. The support material was rapidly heated to the temperature desired'. After the appropriate temperature was obtained, the steam-nitrogen gas stream was permitted to pass through the support material bed for the time desired. At the end of the steaming step, the steam flow was stopped while nitrogen flow was continued. The steamed material was rapidly cooled by turning off the furnace and removing the quartz tube from t,he furnace while nitrogen flow was maintained. Further details with respect to preparation and properties of Catalysts Nos. 1-4 are presented in Table 4. TABLE 4 CATALYST DATA CATALYST NO. 1 2 3 SUPPORT NO. 1 1 2 2 SUPPORT WT. (gm) 229.4 187 1,056 192 IMPREGNATION SOL'N. PREPARED WITH: ammonium heptamolybdate (gm) 11.7 9.5 54.0 9.8 distilled water (ml) 400 350 2,000 250 TABLE 4 (Cont'd.) CATALYST NO. 1 2 3 4 STANDING TIME DURING IMPREGNATION (hr.) 16 16 2 - SUPPORT STEAMED NO YES YES NO MoO3/SUPPORT (gm/gm) 0.04 0.04 0.04 0.04 SUPPORT PROPERTIES: SURFACE AREA (m2/gm) 219 179 173 232 PORE VOL. (cc/gm) 1.433 1.427 1.108 1.172 CALC. A.P.D. (A) 261 319 256 202 % OF P.V. IN PORES OF RADIUS (A): 0-50 13.8 7.7 14.1 25.4 50-100 25.2 22.7 29.6 36.5 100-600 51.5 59.6 39.0 26.7 600-25,000 9.5 10.0 17.3 11.4 CATALYST PROPERTIES: SURFACE AREA (m2/gm) * 162 * 217 PORE VOL. (cc/gm) MICROPORES * 1.25 * 0.98 MACROPORES * 0.13 * 0.15 TOTAL * 1.382 * 1.131 CALC. A.P.D. ( ) * 341 * 209 % OF P.V. IN PORES OF RADIUS ( ): 0-50 * 6.7 * 22.8 50-100 * 16.7 * 33.8 100-600 * 67.2 * 30.2 600-25,000 * 9.4 * 13.2 *Values estimated to be comparable to those of support. Catalysts Nos. 1 and 2 were prepared in the form of 0.79mm (1/32-in) extrudates while Catalysts Nos. 3 and 4 were prepared as 0.1 cm (1/25-in) spheres. Bulk densities of all of the catalysts were about 0.4 gcc. A fifth catalyst, identified herein after as Catalyst No. 5 and containing 1 wt MoO3 on a catalytically active alumina, was obtained from the American Cyanamid Company. This catalyst, which was obtained in the form of 0.79-mm (1/32-in) extrudates, had a BET surface area of 187 m2/gm, a pore volume of 1.042 cc/gm and an average pore dia meter of 222 A. Macropore volume was 0.17 cc/g and micropore volume was 0.86 cc/g with 0.68 cc/g of that in pores having radii of 50-600 A. Its pore size distribution provided 17.7% of the pore volume in 0-50 A pores, 45.5% of the pore volume in 50 100 A pores, 20.6% of the pore volume in 100-600 A pores, and 16.2% of the pore volume in 600-25,000 pores. Bulk density was 0.47 g/cc. Demetallation performance of catalysts 1-5 was evaluated in accordance with the procedure of Example I except that an Ardeshir feed was used in each test. In the test using Catalyst No. 1 three points (the first three in Figure 2) were generated using an Ardeshir vacuum resid having API gravity of 9.80 and containing 24.0 wt.t oils, 14 wt.% asphaltenes, 61.3 wt.% resins, 25.6 wt.% carbon residue, 83.68 wt.% carbon, 9.88 wt.% hydrogen, 0.52 wt.% nitrogen, 5.1 wt.E sulfur, 63 ppm nickel and 227 ppm vanadium. The remaining points for Catalyst No. 1 were gener ated using the Ardeshir feed described in Table 3. All other data in Figure 2 was generated with the Ardeshir feed described in Table 3. As can be seen from the results shown in Figure 2, Catalysts Nos. 2 and 3, having properties according to the present invention, exhibited hiqh initial activity and excellent activity maintenance even at high metals loadings. Comparative Catalysts 1 and 4, which had higher surface areas than Catalysts Nos. 2 and 3, and inferior pore structure, also had good initial activity but activity declined rapidly. Comparative Catalyst No. 5, which had insufficient volume in micropores having radii of 50-600 A and low metals content, had poor initial activity though it increased somewhat on deposition of metals from the feed. Activity maintenance of Catalyst No. 5 was inferior. The following examples and their accompanying figures are based on catalysts and testing also reported in the examples of our copending applications Serial Nos. 274,553 and/or 274,499. EXAMPLE I I I An embodiment of the process of the present invention wherein the catalyst was employed in the form of an ebullating bed was conducted in a relatively large multi-stage pilot plant. Only the first stage of the unit was employed for the per for mance of this test. A large pilot plant batch of catalyst was obtained from the Katalco Corporation. This catalyst, which is identified hereinafter as Catalyst No. 6, was found to contain 4.0 wt% molybdenum trioxide, based upon the weight of the catalyst, supported on a support containing alumina and 8.7 wt% phosphorus calculated as P205 and based upon the weight of the support. Bulk density was about 0.4 g/cc. A 6,500 cc portion of this catalyst in the form of 0.079 cm (1/32-in) extrudates was charged to the first stage of the pilot plant. Catalyst No. 6 had the properties presented hereinbelow in Table 5. TABLE 5 PROPERTIES OF CATALYST NO. 6 PORE VOLUME (cc/gm) MICROPORES 0.98 MACROPORES 0.13 TOTAL 1.113 BET SURFACE AREA (m2/gm) 169 AVERAGE PORE DIAMETER (A) 263 P.V. IN PORES OF RADIUS (R % cc/g 0-50 13.3 0.15 50-100 33.2 0.37 100-600 41.7 0.46 600-25,000 11.8 0.13 The test was conducted to show the ability of Catalyst No. 6 to demetallize a high-sulfur vacuum residual oil blend, which is identified hereinafter as Feed No. 2. The test was carried out at an inlet pressure of 2,000 psig (13.89 MPa) , a catalyst bed temperature of 4020C (7560F) , a LHSV of 0.6 cc of hydrocarbon per hour per cc of catalyst, and a hydrogen addition rate of about 712 m3/m3 (4,000 SCFB) Samples of product coming from the reactor section were obtained on the eighth day and the twentyfirst day of operation. The temperature of operation on the eighth day was 4020C (7560F) while the temperature on the twenty-first day was 4030C (7570F) The other conditions remained the same. Results of this test are presented hereinbelow in Table 6. TABLE 6 RESULTS OBTAINED WITH CATALYST NO. 6 Feed Sample- Sample ProDerties No. 2 Day 8 Day 21 Nickel (ppm) 56 27 32 Vanadium (ppm) 229 64 83 Sulfur (wt%) 3.9 2.3 1.8 Gravity (DAPI) 7.3 10.4 13.0 Rams Carbon (wt%) 20.7 12.8 13.6 The above data demonstrate effective ebullating bed hydrodemetallation of a high-sulfur, vacuum residual oil. EXAMPLE IV This example shows the performance of a catalyst having only a small amount of macropores, i.e., pores having radii within the range of 600-25,000 . A com;nercial catalyst was obtained from the Katalco Corporation. This catalyst, which is identified hereinafter as Catalyst No. 7, possessed the composition and properties presented hereinbelow in Table 7. TABLE 7 COMPOSITION AND PROPERTIES OF CATALYST NO. 7 COMPOSITION (wt%) A1203 84.0 P205 8.5 MoO3 4.1 SiO2 1.3 Na20 1.5 S04-- 0.5 BET SURFACE AREA (m2/gm) 168 PORE VOLUME (cc/gm) 0-600 A 0.9815 600-25,000 A 0.0380 Total 1.0195 CALC. A.P.D. ({) 243 P.V. IN PORES OF RADIUS ( ): % cc/g 0-50 15.3 0.16 50-100 81.0 0.83 100-50,000 3.7 0.04 As indicated in Table 7, the macropore volume of Catalyst No. 7 is less than half of that of the invented catalysts. Catalyst No. 7 was tested as described hereinabove in Example II under operating conditions similar to those employed in the tests of Example II using the Ardeshir feed described in Table 3. The results of this test are presented in the accompanying Figure 3. Also shown in Figure 3 are the results of the test described hereinabove with Catalyst No. 3 of Example II which had 17.3% of its total pore volume, corresponding to 0.19 cc/g, provided by macropores. Figure 3 shows that Catalyst No. 7 had a higher rate of deactivation than did Catalyst No. 3. Hence, Catalyst No. 7, which had only 3.7% of its pore volume in macropores, performed in a manner that was inferior to that of Catalyst No. 3, an embodiment of the catalyst of the present invention. Catalyst No. 3 is an improved catalyst for the demetallization of heavy hydrocarbon streams containing a substantial amount of metals. EXAMPLE V An experimental catalyst was prepared for us by the Davison Chemical Division of W. R. Grace and Co. in the form of 0.8 mm (1/32-in) extrudates. This catalyst, identified hereinafter as Catalyst No. 8, was prepared to contain 4 wt96 MoO3, based upon the weight of the catalyst, on a support of alumina and 6 wt% silica, based upon the weight of the support. The catalyst support had been steamed according to Serial No. 274,499. Catalyst No. 8 was found to have the properties presented hereinbelow in Table 8. TABLE 8 PROPERTIES OF CATALYST NO. 8 PORE VOLUME (cc/gm) MICROPORES 0.96 MACROPORES 0.15 TOTAL 1.108 BET SURFACE AREA(m2/gm) 151 CALC. A.P.D. (R) 293 P.V. IN PORES OF' KhDIUS (R) % cc/g 0-50 5.5 0.06 50-100 32.2 0. 36 100-600' 48.9 0.54 600-25,000 13.4 0.15 BULK DENSITY (g/cc) 0.45 Catalyst No. 8 was tested as described hereinabove in Example II under conditions similar to those employed in Example II using the Ardeshir feed described in Table 3. The results of this test are presented in the accompanying Figure 4. Also shown in Figure 4 are the results of the test described hereinabove with Catalyst No. 3 of Example II. Figure 4 shows that Catalyst No. 8, having properties in accordance with the present invention, provided performance similar to that of Catalyst No. 3. These data indicate that Catalyst No. 8 is an improved catalyst for the demetallization of heavy hydrocarbon streams containing a substantial amount of metals.

Claims: We Claim: 1. A catalyst composition comprising a hydrogenating component and a support comprising at least one porous refractory inorganic oxide, said catalyst having a BET surface area of 150 to about 190 m2/g, pore volume of about 0.8 to about 1.2 cc/g as determined by nitrogen desorption in micropores having radii up to 600 R, with at least 0.7 ccg of such micropore volume in pores with radii ranging from 50 to 600 A, pore volume of 0.1 to about about 0.5 cc/g as determined by mercury penetration in macropores having radii of 600 to 25,000 R, and bulk density of about 0.3 to about 0.5 g/cc. 2. The catalyst of Claim 1 wherein the hydrogenating component comprises at least one metal selected from the group consisting of the Group VIS metals, the Group VIII metals and vanadium. 3. The catalyst of Claim 1 wherein the support comprises a phosphated-alumina which has been steamed prior to incorporation of compound or compounds of the metal or metals of the hydrogenating component. 4. The catalyst of Claim 1 wherein the support comprises alumina and silica. 5. The catalyst of Claim 4' wherein said support has been heated in the presence of steam prior to incorporation of compound or compounds of the metal or metals of the hydrogenating component. 6. The ,catalyst of Claim 1 wherein the hydrogenating component comprises molybdenum. 7. The catalyst of Claim 1 wherein the hydrogenating component is molybdenum and is present in an amount ranging from about 2.5 to about 15 wt% calculated as MoO3 and based on total catalyst weight. 8. A process for hydrotreating hydrocarbon feeds comprising contacting a hydrocarbon feed susceptible to upgrading with hydrogen under hydrotreating conditions in the presence of a catalyst according to claim 1. 9. The process of Claim 8 wherein the hydrocarbon feed comprises a distillate and hydrotreating conditions comprise a pressure of about 300 to about 750 psig (about 21 to about 53 kg/cm2) , temperature of about 600 to about 7250F (about 315 to about 3850C) , hydrogen rate of about 400 to about 1000 SCFB and space velocity of about 2 to about 5 lb hydrocarbon per hour per ib catalyst. 10. The process of Claim 8 wherein the hydrocarbon feed comprises a gas oil and hydrotreating conditions comprise a pressure of about 500 to about 1000 psig (about 35 to about 70 kg/cm2), temperature of about 600 to about 7500F (about 315 to about 399eC), hydrogen rate of about 800 to about 1600 SCFB and space velocity of about 1 to about 4 Ib hydrocarbon per hour per lb catalyst. 11. The process of Claim 8 wherein the hydrocarbon feed comprises an atmospheric or vacuum resid and hydrotreating conditions comprise a pressure of about 500 to about 10,000 psig (about 35 to about 703 kg/cm2), temperature of about 600 to about 9500F (about 315 to about 510 C), hydrogen rate of about 1000 to 10,000 SCFB and space velocity of about 0.2 to about 3 lb hydrocarbon per hour per lb. catalyst. 12. The process of Claim 8 wherein the hydrogenating component comprises at least one metal selected from the group consisting of the Group VIB metals, the Group VIII metals and vanadium. 13. The process of any of Claims 9-11 wherein the hydrogenating component comprises molybdenum. 14. The process of any of claims 8-12 wherein the hydrocarbon feed and hydrogen are contacted in the presence of a fixed bed of said catalyst. 15. The process of any of Claims 8-12 wherein the hydrocarbon feed and hydrogen are contacted in the presence of an expanded bed of said catalyst.

Inventors: HENSLEY, ALBERT LLOYD, JR., QUICK, LEONARD MICHAEL
Applicants: AMOCO CORPORATION
Application year: 1982
Main classification: B01J35
IPC codes: B01J27, B01J37, B01J23, B01J35, C10G49, C10G45