THERMOPLASTIC COMPOSITION

Abstract: A thermoplastic composition which comprises a blend comprising 20 to 80 % by weight of a polycarbonate resin and 80 to 20 % by weight of a graft polymer obtained by grafting at least one aromatic vinyl compound and at least one of vinyl cyanides and alkyl unsaturated carboxylates onto a conjugated diene rubber or its mixture with a copolymer of at least one aromatic vinyl compound and at least one of vinyl cyanides and alkyl unsaturated carboxy­ lates in an amount of not more than 90 % by weight on the basis of the combined amount of the graft polymer and the copolymer, and a polyolefin or a plasticizer having a light transmission of not less than 70 % when determined on the film of 20 microns in thickness prepared by the use of a solution of the plasticizer (0.25 g) and acrylonitrilestyrene copolymer (weight ratio of acrylonitrile and styrene, 30:70; 0.75g) in acetone (10 ml), the weight proportion of the blend and the polyolefin or the plasticizer being 100 : 0.2-20. The resulting composition is excellent in solvent resistance, welding strength, impact resistance, molding property, etc.

Description: The present invention relates to a thermoplastic composition. More particularly, it relates to a thermoplastic resin composition excellent in solvent resistance, weld strength, impact resistance, molding property, etc. Hitherto, attempts have been made to improve the molding property and the dependency of the impact strength on thickness of polycarbonate resins by incorporating therein diene rubber graft polymers such as ABS resins (acrylonitrile-butadiene-styrene polymers) or MBS resins (methyl methacrylate-butadiene-styrene polymers) (cf. Japanese Patent Publns. (examined) Nos. 15225/1963, 71/1964 and 11496/1967). Attempts have also been made to improve the impact strength of polycarbonate resins by incorporating therein ABS resins manufactured by bulk-suspension polymerization (cf. Japanese Patent Publn. (examined) No. 11142/1976). However, the resulting compositions are only improved in apparent molding property, and when a plurality of gates are provided in injection molding as the most popular molding procedure, the strength at the welded parts is insufficient. Also, the resistance to solvent is unsatisfactory. US-A-4 172 103 and US-A-3 947 524 are disclosing generally aromatic polycarbonate resins and a thermoplastic resin on a rubber or a graft polymer. As a result of the extensive study for providing a thermoplastic composition comprising a polycarbonate resin and a graft polymer as the essential components and improved in chemical and physical properties, particularly in solvent resistance and weld strength, it has now been found that incorporation of a small amount of a polyolefin or a certain plasticizer into such composition is effective in improvement of solvent resistance and weld strength. Advantageously, the resulting composition is excellent in processability. The present invention relates to a thermoplastic composition according to claim 1. Further embodiments can be found in the dependent claims. As the polycarbonate resin, there may be used any one chosen from aromatic polycarbonates, aliphatic polycarbonates, aliphatic aromatic polycarbonates, etc. Examples are polymers comprising units of bisphenols such as 2,2-bis(4-hydroxyphenyl)alkanes, bis(4-hydroxyphenyl)ethers, bis(4-hydroxyphenyl)sulfones, bis(4-hydroxyphenyl)sulfides and bis(4-hydroxyphenyl)sulfoxides. When desired, said bisphenols may be substituted with halogen. These and other polycarbonate resins and their production are explained in detail in Encyclopedia of Polymer Science and Technology, 10 , p. 710-764 (1969) (published by John Wiley and Sons, Inc.) and literatures cited therein. As the graft polymer, there is used the one grafting at least one aromatic vinyl compound and at least one of vinyl cyanides and alkyl unsaturated carboxylates onto a conjugated diene rubber. Examples of the conjugated diene rubber are polybutadiene, butadiene-styrene copolymer, butadiene-acrylonitrile copolymer, etc. Examples of the aromatic vinyl compound are styrene, α-methylstyrene, dimethylstyrene, vinytoluene, etc. Examples of the vinyl cyanide are acrylonitrile, methacrylonitrile, etc. Examples of the alkyl unsaturated carboxylate are lower alkyl acrylates (e.g. methyl acrylate, ethyl acrylate, butyl acrylate), lower alkyl methacrylates (e.g. methyl methacrylate, ethyl methacrylate, butyl methacrylate), hydroxy(lower)alkyl acrylate (e.g., hydroxyethyl acrylate), hydroxy(lower)alkyl methacrylate (e.g. hydroxyethyl methacrylate, hydroxypropyl methacrylate), etc. The weight proportion of the conjugated diene rubber and the monomeric components in the graft polymer may be usually from 5:95 to 70:30. Further, the weight proportion of the aromatic vinyl compound and the other monomeric component(s) consisting of the vinyl cyanide and/or the alkyl unsaturated carboxylate may be normally from 50:50 to 80:20. As the copolymer, there may be used any copolymer of at least one aromatic vinyl compound with at least one of vinyl cyanides and alkyl unsaturated carboxylates. Examples of the aromatic vinyl compound, the vinyl cyanide and the alkyl unsaturated carboxylate are those as stated above. The weight proportion of the aromatic vinyl compound and the other monomeric components(s) consisting of the vinyl cyanide and/or the alkyl unsaturated carboxylate may be usually from 55:45 to 85:15, although this is not essential. Further, the intrinsic viscosity of the copolymer is preferred to be from 0.60 to 1.50 (determined in dimethylformamide at 30°C), but this is not limitative. The contents of the polycarbonate resin and the graft polymer or its mixture with the copolymer is from 20 to 80% by weight (preferably from 30 to 70% by weight) and from 80 to 20% by weight (preferably from 70 to 30% by weight), respectively. When the polycarbonate resin is contained in a higher amount than 80% by weight, the melt viscosity of the resulting composition on the molding becomes too high so that the molding property is deteriorated. Further, the weld strength is not improved. When the polycarbonate resin is contained in a smaller amount than 20% by weight, the heat resistance is lowered. When the copolymer is employed, its amount is not more than 90% by weight on the basis of the combined amount of the graft polymer and the copolymer. When the amount exceeds 90% by weight, satisfactory impact resistance is not obtainable. In this invention, a polyolefin or a certain plasticizer is incorporated into a blend comprising the polycarbonate resin and the graft polymer with or without the copolymer. In order to assure excellent weld strength and high impact strength as polyolefin there are used polyethylene having a molecular weight of not less than 2,000 or polypropylene having a molecular weight of not less than 5,000 or their mixture. The amount of the polyolefin in the composition is from 0.2 to 10 parts by weight to 100 parts by weight of the blend. When the amount is less than 0.2 part by weight, any improvement of the weld strength and the solvent resistance is not produced. When more than 10 parts by weight, the impact strength is markedly lowered, and the weld strength is not improved. The plasticizer used in the invention is the one having a light transmission of not less than 70% when determined on the film of 20 µm in thickness prepared by a solution of the plasticizer (0.25 g) and acrylonitrilestyrene copolymer (weight ratio of acrylonitrile and styrene being 30:70; 0.75 g) in acetone (10 ml) while drying under the atmospheric condition. Further, the bleeding of the plasticizer is apt to be produced at the surface of the molded product with the resulting composition. These plasticizers may be employed alone or in combination. The amount of the plasticizer in the composition is from 0.5 to 20 parts by weight to 100 parts by weight of the blend. When the amount is less than 0.5 part by weight, any improvement of the weld strength is not produced. When the amount is more than 20 parts by weight, the heat resistance is remarkably deteriorated. The graft polymer and the copolymer as above stated may be respectively produced by conventional procedures such as emulsion polymerization, suspension polymerization, bulk polymerization, emulsion-suspension polymerization or bulk suspension polymerization. Preparation of the thermoplastic composition may be achieved by mixing the said essential and optional components by the aid of a conventional mixing apparatus such as a roll or Banbury's mixer. When desired, any additive such as a pigment, a dispersant, a lubricant, a filler, a stabilizer, an antistatic agent and a modifier may be incorporated therein. Practical and presently preferred embodiments of the invention are illustratively shown in the following Examples wherein part(s) and % are by weight, unless otherwise indicated. Examples 1 to 5 and Comparative Examples 1 to 7 1) Polycarbonate resin:- Bisphenol A (470 g) and p-t-butylphenol (9.8 g) were suspended in water (1700 ml), and the suspension was stirred while introducing nitrogen therein for 15 minutes to eliminate oxygen therefrom. Then, 45% sodium hydroxide solution (360 g) and methylene chloride (1000 g) were added thereto. The resulting mixture was cooled to 25°C, and phosgene (240 g) was added thereto in 120 minutes. After 15 to 30 minutes, 45% sodium hydroxide solution (75 g) and triethylamine (16 g) were added thereto, and the resulting mixture was stirred for 15 minutes to obtain a polymer solution of high viscosity. The aqueous layer was separated, and the organic layer was washed with water to remove salts and alkalis to obtain a polycarbonate resin. 2) Graft polymer:- As the graft polymer, commercially available acrylonitrile-butadiene-styrene copolymer ("Kralastic MV" manufactured by Sumitomo Naugatuck) was used. 3) Polyolefin:- The following commercially available polyolefins were used: 4) Thermoplastic composition:- The polycarbonate resin, the graft polymer and the polyolefin as stated above were mixed together in a proportion as shown in Table 1 by the aid of Banbury's mixer at 230°C for 4 minutes to give a thermoplastic composition. The physical properties of the obtained thermoplastic composition are shown in Table 1. The solvent resistance and the weld strength were determined in the following manners: (a) Solvent resistance:- Onto the surface of a press molded plate of the thermoplastic composition, a mixture of toluene and cyclohexane (weight ratio, 3:7) was applied, and the critical strain was calculated according to the following equation: Critical strain= 3h · Xc · δ 2l³ ×100 (%) wherein h is the thickness of the test piece (3 mm), Xc is the distance between the maximum deflection point and crack produced point, δ is the distance between the fixed edge and the maximum deflection point and l is the maximum deflection amount. These values were determined by a measuring apparatus as shown in Fig. 1 of the accompanying drawing. This Figure shows illustratively the section view of the measuring apparatus, and A and A' are press bars, B is the test piece and other symbols have the same meanings as above. (b) Weld strength:- The thermoplastic composition was molded at 260°C through two gates (each 2.5x2.0 mm), the distance between them being 100 mm, to make a test piece having 3 mm in thickness and 150 mm in length and in width. The test piece was placed on a cylindrical support of 80 mm in height, 120 mm in inner diameter and 126 mm in outer diameter in a low temperature room adjusted to -30°C, and a steel ball of 1 kg was fallen down at the center of the test piece. The maximum energy value (kg.cm) producing no breakage was determined. Examples 6 to 15 and Comparative Examples 8 to 19 1) Polycarbonate resin:- As the polycarbonate resin, commercially available polycarbonate resin ("Panlite® L-1250W" manufactured by Teijin Kasei) was used. 2) Graft polymer:- Polybutadiene (50 parts (as solid components)), potassium persulfate (0.5 part), potassium oleate (0.5 part) and dodecylmercaptan (0.3 part) were mixed together, styrene (36 parts) and acrylonitrile (14 parts) were added thereto, and the resulting mixture was subjected to polymerization at 70°C for 3 hours, followed by aging for 1 hour. The reaction mixture was salted out, and the precipitate was collected and dried to obtain a graft polymer. 3) Copolymer:- (A) To a mixture of styrene and acryonitrile in a weight proportion of 70:30 (100 parts), t-dodecylmercaptan (0.1 part) was added, and the resultant mixture was subjected to prepolymerization in a bulk state at 90°C for 3 hours. Thereafter, water (210 parts), methyl cellulose (1.0 part) and benzoyl peroxide (0.3 part) were added thereto. The resulting aqueous dispersion was heated from 30°C to 90°C, and polymerization was carried out for 10 hours. By dehydration from the reaction mixture, there was obtained a copolymer (A) (intrinsic viscosity, 0.50). (B) As the copolymer (B), commercially available styrene-acrylonitrile copolymer ("Sevian® NJD" manufactured by Daicel; intrinsic viscosity, 0.63) was used. 4) Plasticizer:- The following plasticizers were used: 5) Thermoplastic composition:- The polycarbonate resin, the graft polymer and the copolymer were mixed together with the plasticizer in a proportion as shown in Table 2 by the aid of Banbury's mixer to give a thermoplastic composition. The physical properties of the obtained thermoplastic composition are shown in Table 2.

Claims: A thermoplastic composition which comprises a blend comprising 20 to 80% by weight of a polycarbonate resin and 80 to 20% by weight of a graft polymer obtained by grafting at least one aromatic vinyl compound and at least one of vinyl cyanides and alkyl unsaturated carboxylates onto a conjugated diene rubber or its mixture with a copolymer of at least one aromatic vinyl compound and at least one of vinyl cyanides and alkyl unsaturated carboxylates in an amount of not more than 90% by weight on the basis of the combined amount of the graft polymer and the copolymer, and a polyolefin or a plasticizer, characterized by the weight proportion of the blend and the polyolefin being 100:0.2-10, the weight portion of the blend and the plasticizer being 100:0.5-20, and the light transmission of the plasticizer being not less than 70% when determined on the film of 20 µm in thickness prepared by the use of a solution of the plasticizer (0.25 g) and acrylonitrilestyrene copolymer (weight ratio of acrylonitrile and styrene, 30:70; 0.75 g) in acetone (10 ml), whereby the plasticizer is selected from the group consisting of diisododecylphthalate, dibutylsebacate, citric acid triester, trimellitic acid ester, methylphthalyl glycolate, methylacetyl ricinioleate, tricresyl phosphite and epoxy soybean oil and the polyolefin comprising polyethylene having a molecular weight of not less than 2,000 or polypropylene having a molecular weight of not less than 5,000, or their mixture. The composition according to claim 1, wherein the blend comprises the polycarbonate and the graft polymer. The composition according to claim 2, wherein the polyolefin is contained in an amount of 0.2 to 10 parts by weight based on 100 parts of the blend.

Inventors: FUJIMORI, YOSHITUGU, ITO, AKITOSHI, SAKANO, HAJIME, TAKABORI, YASUO
Applicants: HONDA MOTOR CO., LTD., SUMITOMO NAUGATUCK CO., LTD.
Application year: 1982
Main classification: C08L69
IPC codes: C08L51, C08L69