HOT MELT ADHESIVE

Abstract: A hot melt adhesive comprising 20 - 70% of a copolymer of maleic anhydride and a monovinyl aromatic compound such as styrene, said copolymer containing about 8 - 30% maleic anhydride, and 80 - 30% of a modifier composition comprising (a) at least one polycarboxylic acid ester as a plasticiser, (b) a highly viscous liquid extender, (c) a tackifier and (d) an antioxidant especially of the sterically hindered phenol kind.

Description: This invention relates to hot melt adhesives. In factories featuring methods which are significantly automated, advantages accrue from the use of hot melt adhesives as distinguished from adhesives featuring an organic solvent and/or water as a carrier for components having the combination of sufficient molecular weight and sufficiently polar groups to impart surface-bondiny characteristics thereto. Poly'esters, polyamides, and related resins having a significant portion of the polymeric chain comprising polarizing atoms have long been used as hot adhesives, sometimes modified by appropriate concentrations of plasticizers, tackifiers an/or nonvolatile liquid extenders. Interpolymers of the styrene-maleic anhydride type have utilized maleic anhydride in styrene type resins to increase the softening point of the resin. However, prior workers failed to develop an economically attractive lot melt adhesive featuring styrene-maleic anhydride resins. In accordance with te present invention there is provided an adhesive having at elevated temteratures an appropriate viscosity and appropriate applicability to be applicable as a hot adhesive at a temperature within a range from about 180n e to about 475"F, said aahesive consisting essentially from about 208 to 70% of an interpolymer, consisting preaoininantly of a monovinyl aromatic compouna and containing from 8 to about 30% of maleic anhydridesand trom about 80% to about 30% modifier imparting ease of application and ease of curing to said adhesive. In certain preferred embodiments, the adhesive comprises from about 10 to about 25% liquid hydrocarbonaceous extender which at ambient conditions has a high viscosity; from about 10 to about 45% tackifier hydrocarbonaceous material such as a copolymer of alpha methyl styrene and vinyl toluene; from about 10 to about 25% plasticizer consisting of esters of polycarboxylic acids; and from about 0.1 to about 58 enhancers comprising 0.05 to 0.5% stericly hindered phenol antioxidant. Said adhesive, after bonding of surfaces with a thin hot film of said adhesive, and cooling to ambient temperature, provides an effective adhesive bond between components to be adhered. The nature of the invention is further clarified by reference to a plurality of illustrative embodiments. Example 1 Styrene-maleic anhydride resin is prepared by initially preparing a xylene solution of a cation polymerized rubber, using about 90% butadiene, about 10% styrene, and secondary butyl lithium as the cationic polymerization catalyst. After the partial block rubber has been prepared, maleic anhydride and styrene are introduced into the rubber solution in the appropriate proportions, and the temperature and Lçlessure are increased to expedite the interpolymerization to produce an interpolymer containing about 8% maleic anhyride, about 15% rubber, ana about 77 styrene. A comlactcially available rubber modified scxrene-maleic anhydride resin may be employed in lieu of an experimental sample. An adhesive is prepared by kneading together in a plasticiziny mixer the following composition: Styrene-maleic anhydride resin (supra) 30 Piccolastic - A5 20 Piccatex 75 35 Flexol Z88 15 Irganox 1010 0.1 Piccolastic A5 is an extender marketed by Hercules, and is a high viscosity liquid polystyrene, an example of a hydrocarbonaceous liquid. Piccatex 75 is a tackifier marketed by Hercules and is a copolymer of vinyl toluene and alpha methyl styrene. Piccatex is an example of a hydrocarbonaceous tackifier. The methyl groups in the monomers provide steric hindrance favoring formation of copolymers having molecular weights promoting tackiness, which molecular weights are lower than desirable in high strength plastics. Flexol Z88 is a dioctyl azelate plasticizer marketed by Union Carbide and illustrative of the esters bf polycarboxylic acids which have been utilized commercially as plasticizers. Irganox 1010 is a stericly hindered phenol, a pentaerythritol tetra (hydrocinnamate) type structure described as tetrakis [methylene (3,5 di tert butyl 4-hydroxy hydrocinnamate] methane marketed by Ciba-Geigy. Such an antioxidant exemplifies the use of various enhancers which are sometimes incorporated in amounts less than about 5% in plastic and adhesive compostions. The styrene-nlaleic anhydride resin pellets were first plasticized on a 2 roll mill at about 320'OF, and as the plasticizer, extender, tackif ier, and antioxidant lowered the viscosity of the mixture, the roll tesaperature was lowered to 2100 F. The thus prepared hot adhesive was applied as a thin film to corrugated paperboard, which was laminated to another piece of corrugated paperboard. A series of thus prepared sandwiches was allowed to cool, and subjected to tests indicative of the effectiveness of the adhesive. The cooled hot melt adhesive had excellent adhesion to the paperboard, good bond strength, good flexibility and toughness comparable to a commercial hot melt adhesive. Example 2 A styrene-maleic anhydride resin was prepared by dispersing maleic anhydride in styrene and subjecting the mixture to polymerization to provide a resin of an interpolymer containing about 14% maleic anhydride, and 86% styrene. The polymerizate was devolatilized and extruded to provide pellets of a styrene-maleic anhydride molding resin generally equivalent to a commercially available styrene-maleic anhydride molding resin. A hot melt adhesive was prepared using said styrene-maleic anhydride resin and a 3/1 ratio (instead of 7/3 ratio) of Piccatex to Flexol, (i.e. tackifier to plasticizer ratio) as follows: parts b weight Styrene-maleic anhydride resin supra 30 Piccolastic A-5 20 Pica tes 37.5 Flexol Z86 12.5 Iruanox 1010 0.1 The perforntance data for the resulting adhesive were generally equivalent to the data for Example 1. These and other tests indicated that a wide range of styrene-maleic anhydride resins could be employed in a concentration from about 20% to about 70' in hot adhesives. The anhydride groups of the interpolyioer enhance the adhesive effectiveness of the hot adhesive. By a series of tests it was established that the composition of the hot melt adhesive should be: a mixture containing from about 20% to about 70% of an interpolymer consisting predominantly of a monovinylmononuclear aromatic compound and containing from about 8% to about 309 maleic anhydride, said mixture containing from about 80% to about 30% modifier imparting ease of application and ease of curing to said adhesive; said adhesive, after bonding of surfaces with a thin hot film of said adhesive, and cooling to ambient temperature, providing an effective adhesive bond between components to be adhered. Preferred embodiments comprise: from about 108 to about 25 liquid hydrocarbonaceous extender which at ambient conditions has a high viscosity; from about 108 to about 45 hydrocarbonaceous tackifier; from about 10% to about 255 plasticizer consisting of esters of polycarboxylic acids; and from about 0.1% to about 5E modifiers comprising OZONE to 0.5% stericly hindered phenol antioxidant. Certain preferred embodiments feature the use of polystyrene extenders and the use of a copolymer of a alpha methyl styrene and vinyl toluene as the tackifier. Various modifications of the invention are possible without departiny from the scope of the appended claims.

Claims: CLAIMS 1. An adhesive having at elevated temperatures an appropriate viscosity throughout an appropriate range to be applicable as a hot adhesive at a temperature within a range from about 1800F to about 4750F, said adhesive consisting essentially of: from about 207. to about 70Z of an interpolymer consisting predominantly of a monovinylmononuclear aromatic compound and containing from about 8Z to about 30Z maleic anhydride; and from about 807. to 307. modifier imparting ease of application and ease of curing to said adhesive; said adhesive, after bonding of surfaces with a thin hot film of said adhesive, and cooling to ambient temperature, providing an effective adhesive bond between components to be adhered. 2. The adhesive of claim I containing: from about 107. to about 25Z liquid extender which at ambient conditions has a high viscosity; from about 10 to about 45 tackifier; from about 107. to about 25 plasticizer consisting of esters of polycarboxylic acids; and from about 0.017. to about 57. enhancers comprising 0,05 to 0.57. stericly hindered phenol antioxidant. 3. The adhesive of claim 2 in which the extender is a liquid polystyrene and in which the tackifier is a copolymer of alpha methyl styrene and vinyl toluene. 4. The adhesive of claim I, claim 2 or claim 3 in which the interpolymer is derived from about 9Z maleic anhydride and about 917. styrene. 5. The adhesive of claim 1, claim 2 or claim 3 in which the interpolymer is derived from about 7 maleic anhydride, about 177. rubber and about 767. styrene.

Inventors: LORDI, FRANK EUGENE
Applicants: ATLANTIC RICHFIELD COMPANY
Application year: 1982
Main classification: C09J3
IPC codes: C09J133, C09J135