ABSORBENT BODY WITH SEMIPERMEABLE MEMBRANE

Abstract: Absorbent body consisting of a fluid-absorbing substance (1) which is enclosed in a jacket (2, 5), and outside the jacket a fluid-absorbing layer (3), e.g. cellulose wadding, at least on the portion of the jacket intended to face the fluid-discharging region, and possibly outside this layer a wound-protecting layer (4), at least a portion (2) of the jacket, which is in contact with the absorbent layer (3), being made of a semipermeable membrane film which is permeable to the fluid discharged from the fluid-discharging region but which is not permeable to the fluid-absorbing substance, the remainder of said jacket (5) consisting of a liquid-tight material.

Description: Absorbent Body with Semipermeable Membrane The present invention relates to an absorbent body which comprises an absorbent layer, a jacket and possibly a ound- protecting layer. The absorbent body can be used e.g. in compresses, various types of dressings and bandages and for collecting fluids from natural or artificial bodily openings. The conventional and known materials used at present for collecting (absorbing) fluids from natural or artificia-1- bodily openings, naturally occurring or artificial wounds, discharging skin and mucous membrane surfaces, are usually cotton or cellulose, possibly covered with a permeable layer such as perforated sheet or gauze designed to lie in contact with the fluid-discharging surface or the fluid- discharging region. The fluid is absorbed by the absorbent material by simple diffusion or by a certain amount of * * capillary force. The fluid-discharging region is therefore always in direct contact with the fluid collected in the absorbent material, which causes irritation of the tissues with harmful effect on healing and risk of subsequent infection. In the fluid collected in the absorbent material there is a massive growth of bacteria, which increases the risk of infection and spreading of infection in a hospital environment for example, and produces unpleasantness due to the foul-smelling products formed when bacteria grow in the • presence of blood and blood serum. The volume of secretion or fluid which a conventional- compress of size 100x100 mm can absorb from a wound, for example, is at most 15 ml. The compress is then dripping o wet and in most cases grown-through with up to about 10 bacteria per ml of fluid. Many attempts -have been made to overcome the. disadvantages of the present dressings. Swedish Patent Specification ■ -7205809-2 reveals a non-adherent layer, possibly with a germicidal agent. US Patent Specification 3,446,208 also describes a non-adherent layer, as does US Patent Speci¬ fication 3,006,338.which de-scribes a dressing with a non- adherent, perforated layer of gauze which has been treated with a film-forming material. US Patent Specification 3,426,754 describes a dressing which is microporous to permit access of air to the wound. US Patent Specification 3,113,568 describes a styptic bandage which comprises a net-like barrier for facilitating coagulation of blood. Danish Patent Specification 138,972 describes an absorbent material containing fiber-coated hydrogel particles. S__mi_L__r polymers which, upon absorption of water, form gels are described in Swedish Patent Specification 7013465-5 and in US Patent Specifications 3,419,006, 3,664,343, 3,783,872, 3,669,103 and 3.670,731. US Patent Specification 3,888,256 describes an absorbent bandage containing a tight layer of absorbent particles which upon absorption of liquid expand and melt together into a gel. The layer then prevents the liquid absorbed into the bandage from being pressed out therefrom under pressure. US Patent Specification 3,678,933 describes a bandage with several layers with an absorbent layer in the middle and on either side a "screen" of thermo- plastic film pressed onto a scrim so that the plastic wraps itself around the. fibers in the scrim forming holes through which the liquid can penetrate to the absorbent material. None of the bandages described in the above mentioned specifications contains a semipermeable membrane or uses osmotic pressure differentials and therefore they have no similarity to the present inventive principle. The purpose of the present invention is to achieve an • absorbent body which takes up a large amount of fluid, e.g. secretion, and permanently encloses.the fluid. These purposes are achieved according to the invention with an absorbent body which comprises an absorbent layer, a jacket and possibly a wound-protecting layer and which, according to the invention,, is characterized in that it consists of a fluid-absorbing substance which is enclosed in the jacket. Outside the jacket there is a fluid-absorbin layer, e.g. cellulose wadding, at least on the portion of the jacket intended to face the fluid-discharging region. The absorbent body possibly comprises, even outside the fluid-absorbing layer, a wound-protecting layer. At least the portion of the jacket which is in contact with the.... absorbent layer is made of a semipermeable membrane film, which is permeable to the fluid discharged from the fluid- discharging region but which is not permeable to the fluid- absorbing substance. The rest of ' the jacket is liquid-tight. In the present description and claims, "fluid-absorbing substance" refers to a substance which sucks up fluid and retains it with greater force than conventional absorbent material, e.g. cellulose wadding. This is achieved either by the fluid-absorbing substance producing an osmotic pressure differential or by it binding fluid and forming a gel for example. At constant fluid flow, the fluid is continuously removed from the fluid-discharging region. The fluid passes through the semipermeable membrane and is collected inside the absorbent body, and is thereafter no longer in contact with the fluid-discharging region, and therefore no tissue irritation occurs when using the absorbent body according to the invention. By virtue of the fact that the fluid is continuously removed and is enclosed in the absorbent body, the growth conditions for bacteria in the fluid-discharging region will be unfavourable. The fluid enclosed in the absorbent * body is sterile, i.e. bacteria-free, if the pore, size of the semipermeable membrane is less than 1 ,um. If the pore size- of the semipermeable membrane is larger. bacteria will also be enclosed in the absorbent body. In both cases, the top of the jacket or bandage will not be contaminated by bacteria coming from below. Therefore there will be no spreading of infection from the dressing to the surroundings. If there is rapid discharge of fluid from natural or arti¬ ficial bodily openings for example, the absorbent body cannot absorb all fluid immediately; rather it should first be absorbed by conventional absorbent material and then be transported into the absorbent body. - - - If there is intermittent discharge, the fluid discharging region-will be dry as soon as the fluid has been taken up by the absorbent body, thereby avoiding tissue irritation and secondary infection. The volume of secretion or fluid which an absorbent body of size 100x100 mm can absorb from a wound, for example, is at least 80 ml. The fluid-absorbing substance in the absorbent body must have a molecular weight which is large enough so that the substance cannot pass through the pores of the semipermeable * membrane. If a liquid substance is used or a substance which becomes liquid upon absorption of fluid, the osmotic pressure differential between the inside and the outside • of the -membrane will drive, the fluid into the absorbent body and retain it there. If the fluid-absorbing substance is not soluble in fluid, the fluid-absorbing capacity of the substance is dependent on the capacity of the substance to bind the fluid. It is also possible to use a mixture of a fluid-absorbing substance, which provides an osmotic effect, * e.g. polyethylene glycoϊ, and a solid gel-forming liquid-absorbing substance, e.g. a carboxy-methylated cellulose derivative. Examples of fluid-absorbing substances are polyvinyl pyrrolidone, polymers of sugars -such as OMPΪ * saccharose, polyethylene glycol, branched polymers of . starch, carboxy-methylated cellulose derivatives of cross- linked type and modified hydrophilic polyacrylates. Preferably substances with a high fluid absorption capacity per unit of weight are used, such as polyethylene glycol with a molecular weight of, for example, 500-80,000, suitably 1,500-20,-000 and especially about 20,000 branched polymers of starch, e.g. polymer 35-A-100, carboxy- methylated cellulose derivative of cross-linked type, e.g. Aqualon^ or hydrophilic polyacrylates, e.g. PermasorJo.. . The semipermeable membrane can consist of cellulose, regenerated cellulose, cellulose nitrate, cellulose acetate, cellulose acetate-butyrate, polycarbonate, polyamide, fiberglass, polysulfone, or polytetrafluoroethylene, e.g. PTFE "Sartorius". A suitable pore size for said materials is .001 ,um - 20,um, preferably .005 - 8,urn, especially f about .01 ,urn. If the membrane is made of cellulose, the mechanical strength can be increased by impregnating the membrane with a solution containing polyacrylates. The membrane can also consist of polyacrylate film with hydro¬ philic groups, e.g. carboxyl groups. The polyacrylate film can be placed on a carrier of non-woven or spun-bonded 2 material for example, with an area eight of 20-50 g per m . The membrane can also be made of cellophane with a poly¬ merization number of 300-500, suitably 400-500, preferably of dialysis quality.. The invention will be described in the following with reference to the• accompanying drawing, in which Fig..1 shows * a section through an absorbent body according to the invention, and . " Fig. 2 shows a section through another embodiment of an absorbent body according to the invention. -Fig. 1 shows an embodiment of the present absorbent body. It consists of a fluid-absorbing substance 1, which is enclosed in a jacket consisting of a tight backing material, e.g. a polyethylene film 5 -fused to a semipermeable layer 2. Beneath the semipermeable layer there is an absorbent material 3, e.g. fluff. Beneath the layer of absorbent material there is a non-adherent layer 4. Fig. 2 shows another embodiment of the invention, in which the fluid-absorbing substance 1 is completely enclosed by a semipermeable membrane 2. The semipermeable membrane -is surrounded on all sides by an absorbent layer 3 which is in turn enveloped by a non-adherent layer 4. In this embodi¬ ment of the invention, fluid is absorbed through both sides of the absorbent body. A few examples will be given below, which show different membrane materials and fluid-absorbing materials. In the examples the following abbreviations are used: PEG = poly- ethylene glycol, Mw = molecular weight, PVP = polyvinyl pyrrolidone. Uptake of liquid in absorbent body (container) with semi¬ permeable membrane Method: The bag is provided with a layer of thin gauze on the side through which the liquid is absorbed. The- bag is placed in a petri dish with liquid. Tap water with 3.5% polyvinyl pyrrolidone Mw 40,000 (PVP-40), produces an osmotic pressure of 400 mm of water corresponding to the colloid- osmotic pressure of serum. Example 1 Liquid: Tap water with 3.5% PVP-40, supplied- in -excess. Membrane: cellophane of dialysis quality, pore size .001,urn. Membrane surface: 7 x 9 cm. .. Fluid-absorbing substance Absorbed volume (ml ) after ca 2. 5 g/container 2 h 24 h 48 h PEG Mw 20 , 000 16 34 35 PEG Mw 6 , 000 21 32 32 5 PEG Mw 4 , 000 26 34 33 PEG Mw 1, 500 28 32 34 Polymer of glucose (Dextran) 6 9 9 PVP Mw 40 , 000 10 12 12 "Permasorb 30 " + PEG Mw 20 , 000 30 34 35 10 "Polymer 35-A-100 " + PEG Mw 20 , 000 3 311 34 36 Example II Liquid: Tap water with 3.5% PVP-40, supplied in excess. Membrane: thin cellophane not of dialysis quality. 15 Membrane surface: 7 x 8 cm. Fluid-absorbing substande Absorbed volum (ml)after 2 g/container 2 h 24 h 48 h PEG Mw 20,000 18 32 32 #- PEG Mw 6,000 20 0 0 20 PEG Mw 4,000 21 0 0 PEG Mw 1,500 24 0 . 0 Polymer of glucose (Dextran) 9 9 8 PVP Mw 40,000 11 10 11 "Permasorb 30" + PEG Mw 20,000 29 31 31 25 "Polymer 35-A-100" + PEG Mw 20,000 3 322 33 33 Example III Liquid: Tap water with 3.5% PVP-40, supplied in excess , Membrane: cellulose nitrate, pore size .Ol um. ' 30 Membrane surface: 7 x 8 cm. Fluid-absorbing substance Absorbed volume(ml)after ca 2 g/container 2 h 24 h 48 h PEG Mw 20,000 25 33 34 PEG Mw 6,000 28 0 0 35 PEG Mw 4,000 29 o • 0 Polymer of glucose (Dextran) 10 9 9 PVP Mw 40,000 8 . 10 9 / ό..PI Example III, cont'd "Permasorb 30" + PEG Mw 20,000 30 32 34 "Polymer 35-A-100" + PEG Mw 20,000 31 34 35 5 Example IV Liquid: Tap water with 3.5% PVP-40, supplied in excess. Membrane: cellulose nitrate, pore size .2 um. Membrane surface: 7 8 cm. Fluid-absorbing substance Absorbed volume(ml)after 10 ca 2 g/container 2 h 24 h 48 h PEG Mw 20,000 25 0 - -o PEG Mw 6,000 24 0 0 Polymer of glucose (Dextran) 8 6 6 PVP Mw 40,000 9 8 8 15 "Permasorb 30" 24 30 32 "Polymer 35-A-100" 26 32 34 Example V Liquid: Tap water with 3.5% PVP-40, supplied in excess. 20 Membrane: cellulose, pore size >5,um. Membrane surface: ' 6 x 8 cm. Fluid-absorbing substance Absorbed volume(ml)after ca 2.5 g/container 2 h 24 h 48 h PEG Mw 20,000 20 0 0 25 PEG Mw 6,000 22 0 ' 0 PEG Mw 4,000 18 0 0 PEG Mw 1,500 16 0 0 Polymer of glucone (Dextran) 8 8 8 PVP Mw 40,000 7 7 7 " 30 "Permasorb 30" 28 31 31 "Polymer 35-A-100" 28 32 32 As is evident from the above examples, different fluid- absorbing substances require different pore sizes. Pore size 35 .OOl Um retains PEG which is dissolved in the absorbed fluid down to a molecular weight of 1,500. At pore size .01,um PEG is retained with molecular weight 20,000 and at pore size O * * ,2/ m even this leaks out. The gel-forming substances "Permasorb" and Polymer 35-A-100 which do not provide any osmotic effect, require on the other hand larger pore size to provide sufficient sucking force. They bind the liquid in the form of a gel and no leakage is obtained even at pore sizes > 5,um. When an absorbent body with a fluid- absorbing substance which provides osmotic effect is used, a pore size <.5 ,um, especially ca .01,um, is preferred. In a fluid-absorbing substance which binds liquid, a ore 10 size >.2/Um, especially >5,um, is preferred. In a combina¬ tion of the two types of liquid-absorbing substances, -both small and large pore sizes can be used. Example VI 15 Clinical study. Patient material: a patient with leg wound ca 100 x 250 mm on both sides of the left lower leg. Material: compresses with layers closest to the wound surface of conventional absorbent material. Container with * * membrane of cellulose nitrate, pore size .01 ,um and with 20 PEG Mw 20,000. " The size of the compresses varied from 50 70 to 80 x 120 mm. The amount of PEG per container was 1.5-3 g. Conventional compresses .were placed on one side, on the other compresses according to the invention. They were changed every other day. The result was registered at every 25. change. .Even at the first change, the wound had improved markedly on the side where the compresses according to the invention had been placed. After four changes the wound on that side was clean, with fresh granulation tissue and in¬ growth of normal skin, while ' the wound which had been 0 treated with conventional compresses was worse. The con¬ tainer of the compresses used contained .2 - 12 ml liquid. Example VII A flat bag of size about 50 x 50 mm is made of dialysis 5 cellophane film. After filling with 10 g polyethylene glycol in powder form with molecular weight 1,500, the bag is closed so that it is entirely sealed. The bag- is then placed in the OMP IF -. centre of a self-adhesive tape material about 10 x 10 cm in size. Over the bag, an about 7 x 7 cm compress of gauze or similar absorbent material is placed on top of the bag, so that the extending edges.of the compress can be pressed onto the tape material. To prevent ' adhesion to the wound, the surface of the compress, which is to be in contact with the wound, is provided with a layer of permeable synthetic material, e.g. Monsanto's spun-bonded polyamide material "Cerex". Finally the entire surface is covered with a suit- ably divided siliconized protective paper. After steriliza¬ tion with y-radiation or ethylene oxide, the dressing-is - ready to be used for a heavily discharging leg wound, for example. Example VIII A film-forming polyacrylate dispersion with hydrophilic groups in the form of carboxyl groups, e.g. Rδhm's "Plextol 4871D", is mixed with another film-forming acrylate disper- * * sion which produces a fusable film, e.g. Rδhm's "Plextol B500", and an acrylate dispersion which in mixture with the others provide a non-sticking and non-blocking film, e.g. Rδhm's "Plextol DV580". _A suitable mixture can consist of 20% "Plextol 4871D", 60% "Plextol B500" and 20% "Plextol DV580", computed as dry substance. -The mixture obtained is cast on a film-casting paper into a transparent, elastic film which can be fused into the same type of bags as in Example VII.. Dressings are made in the manner described ih-Example VII. The thickness of the cast film should be in the range of 50 - 100 ,um and be adapted to the desired size and use of the finished dressing. In the same manner, a vinyl acetate-acrylate copolymer with hydrophilic groups, in the form of N-methylol groups, e.g. Wacker-Che ie's dispersion "Vinnapas LL420/5", is mixed with a polyvinyl acetate-polyethylene dispersion, which produces a fusable film, e.g. Wacker-Chemie's "Vinnapas EP1". The mixture should contain about 50% of each component,, computed as dry substance. In this case as well, the mixture obtained is cast into film. The thickness of the film should be in the range of 50 - 100- r m, and dressings can be made as in Example VII.

Claims: -. . CLAIMS 1. Absorbent body comprising an absorbent layer (3) , a jacket (2,5) and possibl _a wound-protecting layer (4), characterized in that it consists of a fluid-binding substance (1), which is enclosed in the jacket (2,5), and outside the jacket the fluid-absorbent layer (3) , e.g. cellulose wadding, at least on the portion of the jacket intended to face the fluid-discharging region, and possibly outside this layer the wound-protecting layer (4) , at least the portion (2) of the jacket, which is in contact with- - the absorbent layer (3) , being made of a porous semi¬ permeable membrane film which is permeable to the fluid discharged from the luid-discharging region but which is not permeable to the fluid-binding substance, the remainder (5) of the jacket consisting of material which is liquid- tight, and the fluid-binding substance being for example a substance which, is either solid and turns to liquid upon r absorption of fluid, or is liquid, the semipermeable membrane being liquid-tight when the osmotic pressure differential between its inside and outside is zero and is permeable to the fluid discharged from the fluid-discharging area due to osmotic pressure differential between the two sides of the membrane, or consists of a substance which is solid and binds the fluid while in solid or gel form. 2. Body according to Claim 1, characterized in that the fluid-absorbing substance consists of polyethylene glycol with ' a molecular weight of 500-80,000, suitably 1,500-20,000 and particularly ca 20,000. 3. Body according to Claim 1, characterized in that the fluid-absorbing substance consists of a polymer of a sugar, - e.g. saccharose, with a molecular weight of 10,000-400,000, suitably ca 70,000. OMPI 4. Body according to Claim 1, characterized in that the fluid-absorbing substance consists completely or partially of a carboxylated cellulose derivative of cross-linked type, e.g. Aqualon^, a branched p.olymer of starch, e.g. Polymer 5 35-A-100, or a modified hydrophilic * polyacrylate, e.g. Permasorb. 5. Body according to Claim 1 or 4, characterized in that the fluid-absorbing substance consists to 5-50% by weight 10 of polyethylene glycol with a molecular weight of 500-80,000 or a polymer of a sugar with a molecular weight of 10,-000 ; - 400,000, suitably 1,500-20,000, particularly ca 20,000. 6. Body according to one of Claims 1-5, characterized in 15 that the semipermeable ' embrane has a pore size of 0.001- 120,1 * ^, preferably 0.001-20,um. 7. Body according to one of Claims 1-3, characterized in that the semipermeable membrane has a pore size < 0.5 ,um,. 20 suitably ca O.OlΛim. 8. Body according to Claim 1 or 4, characterized in that the semipermeable membrane has a pore size > 0.2..um. especially > 5 Asm . 25 9. Body according to one of Claims 6-8, characterized in that the semipermeable membrane consists of cellulose nitrate or cellulose acetate. . ' 30 10. Body according to. one of Claims 6-8, characterized in that the semipermeable membrane consists of cellulose acetate butyrate, a polycarbonate, a polyamide or a poly- sulphone. 35 11. Body according to one of Claims 6-8, characterized in that the seiiipermeable membrane consists of fiberglass, polytetrafluoroethylene, e.g. PTFE "Sartorius", cellulose • or regenerated cellulose. • -.12. Body according to Claim 11, characterized in that the cellulose membrane is mechanically reinforced by impregnation with polyacrylates, e.g. Vinnapas LL 420/5. 13. Body according to Claim 6 or 7, " characterized in that the semipermeable membrane consists of cellophane with a polymerization number of 300-500, suitably 400-599. 14. Body according to one of Claims 6-8, characterized in that the semipermeable membrane consists of a plastic film, suitably an acrylate film with hydrophilic groups, e.g.- - carboxyl groups, or a copolymer of vinyl acetate-acrylate and ethylene vinyl acetate containing hydrophilic groups. 15. Body according to Claim 14, characterized in that the plastic film is provided with fiber reinforcement, suitably of spun-bonded or non-woven material with an area weight of 20-50 g/cm 2 .

Inventors: KAMME CARL GUSTAF, KAMME, CARL, GUSTAF
Applicants: KAMME CARL GUSTAF, KAMME, CARL, GUSTAF
Application year: 1982
Main classification: A61F13
IPC codes: A61F13, A61L15