PRODUCING INSULATING LAYERS IN SEMICONDUCTOR DEVICES

Abstract: A process for producing a dielectric layer on a semicon­ ductor layer (1) comprises the steps of: forming a layer of ox­ ide (2′) of an element selected from the group of tantalum, tita­ nium, niobium, hafnium, yttrium, zirconium, and vanadium on the surface of said semi-conductor layer; and heating said semiconductor layer having said oxide layer thereon in an oxid­ izing atmosphere, thereby thermally oxidizing the material con­ stituting said semiconductor layer so as to form an insulating layer (3) which comprises oxide of said semiconductor materi­ al at the interface between said semiconductor layer and said oxide layer.

Description: PRODUCING INSULATING LAYERS IN SEMICONDUCTOR DEVICES. The present invention relates to the production of insulating layers in semiconductor devices. Dieletric layers are essential features of some semiconductor devices, for example, gate insulating layers in field effect transistors and dielectric layers of capacitors. Such devices may be included in components comprising transistor-diode logic, transistortransistor logic, read only memory, or dynamic random access memory. Generally, the capacitance of capacitors is proportional to the relative dielectric constant of the dielectric material inserted between electrodes and inversely proportional to the distance between the electrodes. The trans conductance gm of field effect transistors is also proportional to the relative dielectric constant of the gate -insulating dielectric layer and inversely proportional to the thickness of the layer. Thus, it is desirable to produce dielectric layers of a material which has a high relative dielectric constant and also a high dielectric breakdown voltage. Silicon dioxide (SiO2) layers have been mainly used as dielectric layers, the functions of which are set forth above, based on the fact that silicon dioxide has a relative dielectric constant of 3.8 and a dielectric breakdown voltage of 10 MV/cm. However, it has been found difficult to form a silicon dioxide layer the thickness of which is less than lOnm without pinholes which will inevitably lead to an. increased leakage of current, and, consequently, a lower breakdown voltage. Recently, in order to reduce the size of the elements and thus improve the integration of the elements, other dielectric materials having a relative dielectric constant higher than that of silicon dioxide have been used either tentatively or practically. Such dielectric materials are oxides of tantalum (Ta), titanium (Ti), niobium (Nb), hafnium (Hf), zirconium (Zr), yttrium (Y), and vanadium (V). For example, tantalum oxide exhibits a relative dielectric constant of from 20 to 28. However, each of these dielectric oxides has disadvantages in tat the breakdown voltage is low and the leakage of current is large. Of course, these disadvantages may be reduced by thickening the dielectric layer, but this leads to unfavorable lowering of the capacitance. In attempting ta increase the breakdown voltage and decrease the leakage of current, t a Ta205/Si02 double layer may besused in which a silicon dioxide layer is first formed on a substrate and then a tantalum oxide (Ta205) layer is formed thereon so as to form the Ta 205 /Sio2 double layer. However, such a Ta205/SiO2 double structure exhibits a disadvantage in that the capacitance is low due to the thickness of the oxidized silicon, which thickness cannot be reduced owing to the occurrence of pin holes, as mentioned above. Furthermore, the electrical properties of the previously formed silicon dioxide layer deteriorate during the formation of tantalum oxide thereon, thereby lowering the breakdown voltage. In addition, such a double structure exhibits an unfavorable hysteresis in respect to the capacitance-voltage characteristic of a diode due to the abrupt heterojunction thereof. According to the present invention there is provided a method of manufacturing a semiconductor device wherein a layer of an oxide of an element selected from the group made up of tantalum, titanium, niobium, hafnium, yttrium, zirconium, and vanadium is formed on a semiconductor substrate characterized in that the said semiconductor substrate having said layer of oxide thereon is heated in an oxidizing atmosphere so as to oxidize semiconductor material of the said substrate thereby to form an insulating layer made of an oxide of said semiconductor material, sandwiched between said layer of oxide and remaining semiconductor material of the said substrate. In one embodimetlt of the invention the oxide layer comprises a tantalum oxide layer, and the semiconductor layer may advantageously be made of silicon. It can be advantageous if said oxidizing atmosphere comprises wet oxygen and the oxidization is carried out at at a temperature in a range from 7000C to 12000C. A preferred embodiment of the present invention provides a process for producing a dielectric layer on a silicon semiconductor layer, characterized by the steps of: depositing a tantalum layer on the surface of said silicon semiconductor layer; oxidising said tantalum layer, thereby converting tantalum into tantalum oxide; and heating said silicon semiconductor layer having said tantalum oxide layer thereon in an oxidizong atmosphere, thereby thermally oxidizing the silicon constituting said semiconductor layer so as to form an insulating layer which comprises silicon oxide at the interface between said semiconductor layer and said tantalum oxide layer. It is desirable that said silicon semiconductor layer is of a one-conductivity type. Advantageously said process can further comprise the step of forming an electrically conductive layer on said tantalum oxide layer. An embodiment of the present invention can provide a process for producing a dielectric layer having a desirably high relative dielectric constant, a relatively high dielectric breakdown voltage, and desirably small current leakage. Such a dielectric layer can be made to exhibit very low hysteresis in respect to the capacitance-voltage characteristic of a diode. It has been noted that A.G. Revesz et al of Comsat Labratories teach in "Film-Substrate Interaction in Si/Ta and Si/Ta205 Structures" in the Journal of the Electro chemical Society, Vol. 123, No. 10, October 1976, that if a tantalum film is deposited on a silicon substrate and oxidized, the resultant tantalum oxide film contains a significant amount of silicon, and the majority of the silicon atoms incorporated into the tantalum oxide film are concentrated near the interface while a small amount of the Silicon atoms are concentrated at the outer sut face of the tantalum oxide film. During oxidation, the thus-diffused silicon atoms are also oxidised by oxygen, which diffuses through the tantalum oxide. However, Revesz et al do not suggest the forming of an effective silicon oxide layer under the tantalum oxide layer so as to realize a dielectric layer to form a necessary feature of a semiconductor device. In addition, B.E. Deal et al teach in "General Rela tionship for the Thermal Oxidation of Silicon" in the Journal of Applied Physics, Viol. 36, No. 12, December 1965, that silicon is oxidized more quickly in wet oxygen 1than in dry oxygen. However, they do not suggest that oxygen can diffuse through a tantalum oxide layer. Reference will now be made, by way of example, to the accompanying drawings, in which Figures la through lc are sectional diagrams of part of a semiconductor device at different stages of a method embodying the present invention. Figure 2 is a graph showing the relationship between the amount of elements and the depth of a, dielectric layer of Fig. Ic. Figure 3 is a graph showing the relationship between the thickness of the oxidized silicon and the oxidation temperature. Figure 4 is a graph showing the relationship between the thickness of the oxidized silicon and the oxidation time. Figure 5 is a graph showing the relationship between the leakage of current and the voltage across the dielectric layer of Fig. lc. Figures 6 through 12 are diagrams showing the steps for producing a dynamic random access memory device. Figures 13 through 16 are diagrams showing steps for producing a MOS field effect transistor. Figures 17 through 21 are diagrams showing steps for producing lateral isolation of integrated circuits. Figures 22 and 23 are diagrams showing steps for producing multilayered insulation of integrated circuits. Figures 24 through 27 are diagrams showing steps for producing a l(one)-transistor type nonvolatile memory device. Figures 28 and 29 are diagrams showing the function of a l-transistor type nonvolatile memory device. A high dielectric layer (2'), e.g., tantalum oxide (Ta205), may be formed on a semiconductor substrate (1) either by an indirect process, e.g., first depositing tantalum (2) by vacuum vapor deposition or sputtering (Fig. la) and then oxidizing tantalum into tantalum oxide (2'), or by a direct process, e.g., chemical vapor deposition or oxide sputtering (Fig. lb). The thus -obtained oxide may be further subjected to a thermal treatment, whereby the oxide may be crystallized and improved in respect to thermal stability. The low breakdown voltage of the tantalum oxide (2') is compensated for by heating the substrate (1) in an oxidizing atmosphere so as to form a layer of oxide of the semiconductor material (3), e.g., silicon oxide, mainly at the interface between the semiconductor substrate (1) and the tantalum oxide (2') (Fig. lc). The thus-formed composite oxide layer is better illustrated in Fig. 2 The composition was determined by the Auger sputtering method. At the end of the tantalum region, the silicon shifted in a combined state with the oxygen (Fig. 2). In the following experiments, the total thickness of the oxide layer was determined by the Talystep method before and after oxidation and then the difference in thickness was assumed to be the thickness of oxidized silicon. A silicon substrate coated with tantalum oxide 45 nm thick (A) and a bare silicon substrate B were oxidized. in wet oxygen (Fig. 3). A silicon substrate coated with tantalum oxide 24 nm thick (C) and a bare silicon substrate (D) were oxidized in dry oxygen (Fig. 3). These thermal treatments were continued for 30 minutes at various temperatures. The substrates (A, B) were oxidized quickly in wet oxygen without regarding the coating of tantalum oxide and were effective at a temperature higher than 700 C. Contrary to this, the substrates (C, D) were oxidized slowly in dry oxygen, particularly in the case coated with tantalum oxide, and were oxidized only at a temperature higher than 9000C An oxidation temperature higher than 12800C exhibited no advantages in respect to the consumption of energy in relation to either wet or dry oxidation. The thickness of the oxidized silicon gradually increased as heating of the silicon semiconductor substrates A, B, C, and D used in the experiment of Fig. 3 was con tinued (Fig. 4). These substrates A, B, C, and D were heated at 1000 C. Wet oxidation (A, B) was superior to dry oxidation (C, D) in respect to their growth. As can be seen from the graphs of Figs. 3 and 4, oxygen in a wet oxygen atmosphere diffuses freely through the tantalum oxide layer. Contrary to this, oxygen in a dry oxygen atmosphere scarcely diffuses therethrough. Furthermore, it was confirmed that oxygen in a wet oxygen atmosphere diffuses several um laterally through a tantalum layer 45 nm thick. A silicon substrate coated with tantalum oxide 45 nm thick was heated in wet oxygen at 800 C. Oxidation was continued for 10 minutes (F), 20 minutes (G) and 30 minutes (H) (Fig. 5). Thus, the silicon at the interface was oxidized# so as to produce a dielectric layer according to the present invention. The dielectric layers F, G, and H, which correspond to the curves F, G, and H, had a breakdown voltage of approximately 6 V, 10 V, and 15 V, respectively, and an effective dielectric constant of 13, 11, and 9, respectively. The SiO2 layer formed at the interface of Ta205 - Si substrate by oxidation after coating the substrate with Ta 205 included almost no pin holes and consequently exhibited a breakdown voltage much higher than that of a SiO2 layer formed by thermal oxidation of a bare silicon substrate in a conventional manner. Thus, double oxide layer produced in a method embodying the present invention, can exhibit a high dielectric constant and a high breakdown#voltage. Example 1 A layer of tantalum 15 nm thick (2) was deposited on a silicon substrate (1) by RF sputtering in argon at 4 x 10 2 Torr (Fig. la). The substrate (1) was heated in dry oxygen at 5250C for 40 minutes. As a result, a tantalum oxide (2') layer 33 nm thick was formed (Fig. lb). The substrate (1) having a tantalum oxide layer (2') thereon was heated in wet oxygen at 8000C for 13 minutes. Oxide layers (3) comprising silicon oxide were produced mainly under the tantalum oxide layer, i.e., the thickness of the silicon oxide was 0.3 nm on the surface and 5 nm at the interface between the tantalum oxide layer (2') and the silicon substrate (1), respectively (Fig. lc). In addition, a very thin silicon oxide layer (not shown) was formed on the surface of the tantalum oxide layer (2') during oxidation in a wet oxygen atmosphere. The substrate was annealed in nitrogen containing 5% by volume of hydrogen at 10500C for 30 minutes and then electrodes were produced (not shown). The thus-obtained dielectric layer composite having silicon oxide in addition to tantalum oxide exhibited a relative dielectric constant of 15, a dielectric breakdown voltage of 4 MV/cm, and a leakage current on the order of 10 10 A at 5 V. The relative dielectric constant was more than three times greater than that of silicon oxide, and the breakdown voltage was several times greater than that of tantalum oxide. In addition, this composite exhibited no hysteresis in respect to the capacitance-voltage characteristic of a diode. Furthermore, it is preferable that the amount of silicon contained in an electrode of silicide of a high melting point metal, e.g., molybdenum silicide, which is formed on the tantalum oxide layer not exceed the stoichiometry ratio. Our experiment revealed that in the case where the molybdenum silicide layer of the upper electrode is MoSi3 i.e., rich in silicon, an increase in the leakage of current is evident and that, contrary to this, a layer of MoSi or MoSi2 does not exhibit an increased leakage of current even after thermal treatment at 10000C. We consider the reason for this to be as follows. Silicon atoms pile up from the molybdenum silicide layer at the interface between the molybdenum silicide layer and the tantalum oxide layer (22) so as to form an apparent Si Ta 205 interface in the case where the molybdenum silicide layer is rich in silicon, and, thus, Si and Ta2O5 diffuse and react with each other. Contrary to this, MoSi2 satisfies the stoichiometry ratio, i.e., it does not discharge silicon atoms. Molybdenum atoms which pile up from a MoSi layer, however, do not react with Ta205 , which is thermodynamically stable in the Mo - Ta205 system. Thus, the upper electrode 4 of the molybdenum silicide layer formed on the tantalum oxide layer 3 must not contain silicon in an amount in excess of the stoichiometry ratio. This holds true not only for the MoSi - Ta205 system but also for other silicide-oxide systems which comprises silicide, e.g., of tungsten, tantalum, or platinum and oxide of a metal in the group 3A, 4A, or 5A of the periodic table of elements. Example 2 Figures 6 through 12 are diagrams showing the steps for producing a dynamic random access memory device by a method embodying the present invention. Field oxide layers (12) 1 um thick were produced on a p type silicon semiconductor substrate (11) in a usual manner. A tantalum layer (13) 20 nm thick was produced on -2 the substrate by RF sputtering in argon at 4 x 10 Torr with an accerelating voltage of 2.3 KV (Fig. 6). The tantalum layer (13) was converted to a tantalum oxide layer (13') 44 nm thick by heating it at 5000C and then heating the substrate (11) at 8000C in wet oxygen, and thereby a silicon oxide layer (14) 6 nm thick was produced at the interface between the silicon substrate (11) and the tantalum oxide layer (13') (Fig. 7). A molybdenum (Mo) or molybdenum silicide electrode (15) for capacitor electrode was sputtered on the tantalum oxide layer (13') and then an insulating layer (16) of silicon oxide was deposited by chemical vapor deposition (Fig. 8). The insulating layer (16), the capacitor electrode (15), and the tantalum oxide layer (13') were partly removed by dry etching with a CHF3 etchant, thus ss partially exposing the silicon oxide layer (14) at the interface (Fig. 9). A silicon oxide layer (17) was further deposited by chemical vapor deposition (Fig. 10). The silicon oxide layer (17) was removed, except for the portion coating the side surface (side wall) of the capacitor electrode (15), by dry etching. Then a transfer gate insulating layer (18) 40 nm thick was formed on the silicon substrate (11) by thermal oxidation (Fig. 11). A transfer gate electrode (19) was formed by depositing and patterning polycrystalline silicon. Then, a n type bit line contact region (20) was formed by arsenic (As) ion implantation, whereby arsenic was implanted into the transfer gate electrode (19). An electrode contact window was opened by forming and patterning the silicon oxide layer (21). A bit line (22) was formed by depositing and patterning an aluminum layer (Fig. 12). The thus-obtained dynamic random access memory device exhibited a significantly small leakage current and a higher integration. Example 3 Figures 13 through 16 are diagrams showing the steps for producing a MOS field effect transistor by a method embodying the present invention. A tantalum oxide layer (32) 50 nm thick was produced on a p type silicon semiconductor substrate (31) in a manner similar to that of Example 2 (Fig. 13) and was removed, except for the portion coating the positive regions, by a conventional process. Field oxide layers (33) were produced on the field region in a usual manner. A silicon oxide layer (34) was formed by thermal oxidation in wet oxygen at 000C for 50 minutes at the interface between the tantalum oxide layer (32) and the silicon substrate (31). A###Y-dr#stalIi# silicon gate electrode (35) was formed by chemical vapor deposition and dry etching with a CC14 etchant (Fig. 149. An oxide layer (36) was formed on the gate electrode (35) by heating the substrate in dry oxygen (Fig. 15). Contact windows were opened by exposing the positive regions in the insulating silicon oxide layer (34) by selfalignment patterning of the tantalum oxide layer (32). Then n type source and drain regions (37, 38) were formed by soft etching and ion implantation. Source and drain electrodes (39, 40) were formed by self-alignment patterning of the insulating layer (36) and by depositing and patterning aluminum by means of conventional photolithography technique (Fig. 16). As contact windows are opened by self-alignment, a short channel gate transistor can be easily realized. A tantalum oxide layer is used as a mask for selective oxidation, and, consequently, the occurrence of so-called bird beak, white ribbon, and strain in the substrate is prevented. Example 4 Figure 17 through 21 are diagrams showing the steps for producing lateral isolation of integrated circuits. A tantalum oxide layer (52) ca. 100 nm thick was deposited on a single crystalline silicon substrate (51) by reactive sputtering (Fig. 17) and was cut open in the desired region by means of photolithography and dry etching with a CHF3 etchant so as to form lattice-like openings (52') (Fig. 18). A polycrystalline silicon layer (53) ca. 3 pm thick was deposited on the substrate (51) by chemical vapor deposition and was transformed by laser annealing into a single crystalline layer, since the surface of substrate (51) contacting the polycrystalline silicon layer (53) acted as crystallizing nuclei. A silicon nitride layer (66) 100 nm thick was formed on the single crystalline silicon layer (53) by chemical vapor deposition. Windows 67 were opened through the silicon nitride layer (66) and the single crystalline silicon layer (53) by reactive ion etching with a CC14 etchant (Fig. 19). The substrate was treated in wet oxygen at 10000C for 80 minutes, and oxygen flowed through the windows (67) and diffused through the tantalum oxide layer (52) since the tantalum oxide acted as an oxygen passage. Consequently, not only the side wall (65) of the windows (67) but also the surface (54') of the silicon substrate (51) and the lower portion (55) of the transformed single crystalline silicon layer (53) were oxidized so as to form a silicon oxide insulating layer (Fig. 20). Silicon oxide layers (68) were deposited into the windows (67) by chemical vapor deposition so as to separate the single crystalline silicon islands (53), on which circuit elements could be produced. The silicon nitride layer (66) was removed with hot phosphoric acid. Thus, a large scale integrated circuit, particularly bipolar type semiconductor devices, with complete insulation could be produced. In addition, in the case where spacing of the lattice structure of the tantalum oxide layer (52) is selectively broaden in an oxidation process, there remains between the silicon substrate (51) and the single crystalline silicon layer (53) an unoxidized silicon layer. Thereby an electrical connection is obtained between the silicon substrate (51) and the single crystalline silicon layer (53). Example 5 Figures 22 and 23 are diagrams showing the steps for producing multilayered isolation of integrated circuits A tantalum oxide layer (72) 50 nm thick and a polycrystalline silicon layer (73) were sequentially formed on a silicon substrate (71) in a manner similar to that of Example 4. Another tantalum oxide layer (72') and another polycrystalline silicon layer (73') were further formed thereon. Then these layers (72, 73, 72', 73') were patterned so as to expose the side surfaces of the tantalum oxide layers (72, 72') (Fig. 22). These layers were oxidized in wet oxygen at 10000C for 20 minutes. As the tantalum oxide layers (72, 72') acted as passages for the diffusion of oxygen, the surface of both polycrystalline silicon layers (73, 73sir and the silicon substrate (71) were oxidized so as to form silicon oxide layers (74', 75', 75", 75"'). The silicon surfaces (74, 75) were oxidized by direct contact with oxygen. The polycrystalline silicon layers (73, 73') which were retained without being oxidized acted as electrical passages. Thus the separation of elements and also multilayered wiring could be effected easily and exactly. Example 6 Figures 24 through 29 are diagrams showing the steps for producing a l(one)-transistdr type nonvolatile memory device. Field oxide layers (88) and a tantalum oxide layer (89) 44 nm thick were produced on a p type silicon substrate (81) in a manner similar to that of Example 2. Then a polycrystalline silicon layer (86) 500 nm thick was formed on the tantalum oxide layer (89) by chemical vapor deposition (Fig. 24). These layers (86, 89) were selectively removed so as to form a polycrystalline, silicon gate electrode (86') and the second insulating layer of tantalum oxide (89'). N type source and drain regions (82, 83) were produced by masking with these layer (86', 89') and implanting arsenic as a donor type impurity into the substrate (81) (Fig. 25). The substrate was subjected to thermal oxidation in wet oxygen at 8000C for 10 minutes. Thus, the exposed silicon surfaces (90, 91) of the substrate and the gate electrode were oxidized. In addition, oxygen diffused through the tantalum oxide layer (89') so as to form the first and the third insulating layers of silicon oxide (91', 90') under the gate electrode (86') (Fig. 26). The substrate was annealed in a mixture of nitrogen and 5% by volume of hydrogen at 10000C for 20 minutes so as to reduce the tantalum oxide layer (89'). Consequently, a number of traps were produced due to the vacancy of oxygen in the reduced oxide layer (89"), which traps could accumulate electric charge (Fig. 27). During the annealing, silicon in the gate electrode (86') and the substrate (81) was oxidized very slightly, probably due to the discharge of oxigen generated by the reduction of Tea205 with hydrogen. Then, a word line (92) of aluminum was produced on the gate electrode (86'), after a contact hole was opened in the silicon oxide layer (88'), in a usual manner (Fig. 27). Figure 28 is a plan of a l-transistor type nonvolatile semiconductor random access memory device and indicates the following elements: field insulating oxide layers (88), gate electrodes (86'), contact holes (93) opened on the gate electrodes (86'), an n type region (83) constituting bit lines defined by the adjacent dot-dash lines B, and an n type region (82) constituting earth lines defined by the adjacent broken lines C. However, insulating silicon oxide layers (88' in Fig. 27) and aluminum word lines (92 in Fig. 27) are not shown (Fig. 28). The operation principle of the l-transistor type nonvolatile semiconductor memory will be illustrated with reference to Fig. 29, which shows an equivalent circuit of the random access memory shown in Fig. 28. Figure 29 illustrates bit lines B1 , B2 and earth lines C1 , C2 connected to-drains and sources of each transistor, respectively, and word lines D1 , D2 t D3 connected to gates of each transistor. These constitute the memories 101 through 106. In order to write only in cell 101, a potential 10 V is applied to word line D1 , and bit line B1 is grounded. Thus, a writing voltage of 10 V is applied to the gate of cell 101. Electrons are injected and accumulated from n type region constituting the bit line into the second insulating layer of tantalum oxide in the gate. At the same time, bit lines B2 of cell 103 is maintained at an open potential so as to inhibit writing in cell 103 connected to the same word line as cell 101, and earth lines C1, C2 are also maintained at an open potential so as to inhibit electron injection from the earth lines into cells 101 and 103. In order to read out from cell 101, potentials 3 V and +5 V are applied to word line D1 and bit line B, r respectively, and, then, it is determined whether the cell is ON or OFF, i.e., the absence of and the accumulation of electrons in the gate result in a current and no current between the source and drain, respectively. Erasing the memory is carried out inversely to the writing procedure. Word line D1 is grounded and a potential 10 V is applied to bit line B1. Consequently, electrons accumulated in the gate are erased by the tunnel effect up to the n type region constituting the bit line. Bit line B1 is connected to other cells 102, 104, 105. In order to avoid erasing of information written in these cells, a potential +5 V is applied to word lines D2 , D3. Thus, the effective electron discharge voltage is 5 V, which does not cause the tunnel effect. In addition, earth lines C1 , C2 on both sides of bit line B1 are maintained at an open potential, thereby inhibiting current flow into the adjacent cells.

Claims: CLAIMS 1. A method of manufacturing a semiconductor device, wherein a layer (2') of an oxide of an element selected from the group made up of tantalum, titanium, niobium, hafnium, yttrium, zirconium, and vanadium is formed on a semiconductor substrate (1) characterized in that the said semicondutor substrate having said layer of oxide thereon is heated in an oxiodizing atmosphere so as to oxidize bemiconductor material of the said substrate thereby to form an insulating layer (3) made of an oxide of said semiconductor material, sandwiched between said layer of oxide and remaining semiconductor material of the said substrate. 2. A method as claimed in claim 1, wherein the said semiconductor material comprises silicon. 3. A method as claimed in claim 1 or 2 wherein the said element is tantalum. 4. A method as claimed in claim 1, 2 or 3, further characterized in that said oxidizing atmosphere comprises wet oxygen. 5. A method as claimed in claim 4 characterized in that the heating in the said oxidizing atmosphere is carried out at a temperature in a range from 700or to 1200 C. 6. A method as claimed in any preceding claim, including the steps of depositing a layer (2) of the said element on the said semiconductor substrate, and oxidizing that layer so as to produce the said layer of an oxide. 7. A method as claimed in any preceding claim, wherein the said semiconductor substrate is of p-type conductivity 8. A method as claimed in any one of the preceding claims 1 to 6, wherein the said semiconductor substrate is of n-type conductivity. 9. A method as claimed in any preceding claim characterized by a further step of forming an electrically conductive layer on the said layer (2') of an oxide.

Inventors: KATO, TAKASHI, TOYOKURA, NOBUO
Applicants: FUJITSU LIMITED
Application year: 1982
Main classification: H01L21
IPC codes: H01L21, H01L27