METHOD OF USING HIGHER CONCENTRATION SULFURIC ACID FOR STRIPPING AND PRECIPITATION OF ADSORBED MAGNESIUM

Abstract: Adsorbed magnesium is removed from a cation ex­ change resin by elution with 20 to 70% sulfuric acid as increments of the loaded resin move upwardly in a stripping column, the regenerated resin being removed at the top of the column and the sulfuric acid of reduced concentration with the eluted magnesium is removed from the lower por­ tion of the column. The sulfuric acid concentrations are controlled so that the regenerating solution can be formed from commercial concentrations of sulfuric acid without undue dilution, and so that magnesium can be precipitated from the eluting solution by increasing the sulfuric acid concentration without adding a large amount of commercial concentration acid. The amount of dilute sulfuric acid produced as a waste material is kept to a minimum, while the principal sulfuric acid by-produkt has a usefully high concentration, such as may be employed for treatment of phosphate rock.

Description: METHOD OF USING HIGHER CONCENTRATION SULFURIC ACID FOR STRIPPING AND PRECIPITATION OF ADSORBED MAGNESIUM This invention relates to the regeneration of cation exchange resin containing adsorbed magnesium ions, and the recovery of the magnesium as a crystalline precipitate. The regeneration uses moderate to high concentration aqueous H2S04, and the recovered precipitate comprises co-- crystallization compounds of MgSO4 and H2S04. The resin for regeneration may contain other cations contained in wet process phosphoric acid. As is well known in the ion exchange arts, metal ions adsorbed on cation exchange resins can be eluted with aqueous solutions of strong mineral acids, such as hydrochloric, nitric, and sulfuric acids. The adsorbed metal ions are exchanged for hydrogen ions so that the resin is returned to its hydrogen form for further use in the removal of metal ions from solutions. Commonly, such metal ion elution and cation exchange resin regeneration is carried out with relatively dilute acid solutions, and these are prepared by adding water to commercial concentrations of the regenerating acid. Since concentrated mineral acids produce heat when diluted with water, cooling of the regenerating acid solutions may be required with energy being used for the regeneration Fur ther, the use of dilute acid solutions results in a large volume of waste solution which presents a disposal problem. The foregoing problems were encountered in the development of a system for removing principally magnesium and other cations from phosphoric acid, especially phosphoric acid prepared from phosphate rock having relatively high concentrations of magnesium, as is common with lower grades of phosphate rock. The system utilized moving folded beds of cation exchange resin for the adsorption and elution of the magnesium. A system of this kind is described in United States Patent 4,280,904. The resin regeneration as described in this patent, is carried out-with various acids including sulfuric acid. In experiments conducted prior to the present invention, the elution and regeneration was carried out with 3N sulfuric acid (approximately 17% H2S04 concentration). This eluting solution was prepared by adding water to commercial grade sulfuric acid (viz. 93%). The spent eluting solution which contained the removed magnesium together with eluted calcium gave processing and disposal problems. It was difficult and expensive to recover the magnesium as a precipitated solid, and yet it was undesirable to dispose of the large volume of spent eluting solution without further processing. These problems are overcome by the present invention. Wet process phosphoric acid prepared from phosphate rock will contain organic matter which may adhere to the resin beads as transferred for regeneration. It is therefore another important advantage of the method of this invention that such organic matter does not cause any operational problems even though the resin beads are repeatedly regenerated and recycled to the phosphoric acid treating column. The high concentration of H SO in the regenerating column chars the organic matter and facilitates its removal from the resin beads by the regenerating solution. In the accompanying drawing, Fig. 1 is a diagrammatic flow sheet illustrating a preferred embodiment of the method of the present invention for regenerating a catior exchange resin loaded with adsorbed magnesium. In accordance with the present invention, adsorbed magnesium is removed from the cation exchange resin, such as that resulting from the cation exchange resin treatment of phosphoric acid, using a sulfuric acid eluting solution of relatively high concentration (viz. 40-708). The high acid concentration regenerating solution is introduced into the top of a regeneration column containing a series of increments of the resin for regeneration. In the operation of the column, increments of the magnesium loaded resin are sequentially introduced into the bottom of the column while regenerated resin increments are removed from the top of the column. A magnesium ion-containing sulfuric acid solution is removed from the lower portion of the column at a still relatively high concentration (20 to 50%). The use of these high concentrations reduces the liquid volume required for regeneration, and facilitates the MgSO4 precipitation, and the waste dis- posal of spent acid. Magnesium is precipitated from the acid solution removed from the regeneration column by adding more highly concentrated sulfuric acid thereto, the H2S04 concentration being increased to a level at which magnesium sulfate crystallizes and precipitates. This precipitate comprises co-crystallization compounds of MgS04 and H2S04 having the formula MgS04 . xH2S04 (sometimes referred to herein as the magnesium sulfate precipitate.). The precipitate may contain from 1 to 3 moles of H2S04 per mole of MgS04. The supernatant from which the precipitate is separated has a sufficiently high concentration of sul furic acid to permit it to be reused as part of the regenerating solution, or for other purposes, such as in the treatment of phosphate rock in the manufacture of phosphoric acid therefrom. The regenerated resin increments removed from the top of the column contain sulfuric acid at the concentration of the incoming regenerating solution (viz. 40 to 7). It was found that initial water washing of the removed resin could cause serious degradation of the resin, at least with somme resins, the resin beads tending to expand as the sulfuric acid is removed. In a preferred embodiment of the present invention, therefore, the removed resin is first washed with aqueous sulfuric acid of intermediate concentration and thereafter washed with water. This staged and more gradual reduction of the acid concentration minimizes fracturing or spalling of the resin beads. Further, all or part of the acid wash and the water wash can be combined to provide additional acid wash solution at the desired intermediate concentration. The excess of the acid wash can be used for dilution of the commercial concentration acid in preparing the stripping column regenerating solution. The method of the present invention can be applied to any cation exchange resin where the predominant metal ions adsorbed thereon are magnesium ions to be removed in the regeneration column. Further, the method is applicable to the elution of magnesium adsorbed on a wide variety of cationic exchange resins. For example, a crosslinked polystyrene aryl sulfonate resin can be used. Resins are preferred which can be used with high concentrations of H2S04. Where the loaded resin contains more than one mole of calcium per 10 moles of magnesium, it is desireable to first remove part of the calcium from the resin while leaving the magnesium adsorbed thereon. The calcium to magnesium ion ratio is preferably reduced to at least 1:9 and optionally below 1:20. Calcium precipitation as calcium sulfate or a hydrate or complex thereof can occur within the magnesium removal column. It is desired to minimize such precipitation, and to recover the Mg as MgS04 separately from the CaSO4. The method of this invention is preferably employed in conjunction with a moving folded bed apparatus but can be utilized in fixed bed systems as well as other resin handling systems. Such a system is described in United States Patent No. 4,228,001, and also in United States Patent 4,280,904 with specific reference to treatment of wet process phosphoric acid prepared from phosphate rock. For the purpose of the present invention, the important feature of such folded moving bed systems is that the loaded resin is removed in increments from the top of the loading column, and either with or without further processing to remove the calcium, is introduced into the bottom of the magnesium removal column, the removal ciumn introduction also being incremental. The resin increments may be transferred as a slurry using pump pressure and a liquid transport medium, as described in United States Patent Nos. 4,228,001 and 4,280,994. Alternatively, an air-pulse transfer mechanism can be used, the resin being transferred in compacted increments by the generation of air pressure in a pulse-transfer vessel. In the magnesium removal column, increments of the magnesium containing cation exchange resin are sequentially introduced into the bottom of the column for regeneration of the resin. Regenerated increments of the resin are sequentially removed from the top of the column. Preferably, with each incremental introduction into the bottom of the column a resin increment of corresponding volume is removed from the top of the column. When the column is fully packed with resin, as preferred, this will automatically be accomplished, the pulsed increment of resin introduced into the bottom of the column automatically causing the ejection of a corresponding resin increment from the top of the column. The magnesium removal column will contain a plurality of increments in the form of resin bands or layers moving from the bottom to the top of the column, and being progressively regenerated by the magnesium removal as they ascend in the column. For example, the column may contain from 5 to 10 of such increments. In accordance with the present invention, there is introduced into the top of the regeneration column an aqueous sulfuric acid regenerating solution of relatively high concentration. The regenerating solution preferably has a concentration within the range from 40 to 70 %, such as 50 to 60 %. Higher concentrations within the range of 70 to 95 % can be used, if spalling of the resin beads can be avoided. Advantageously, a concentration of at least 40 % is used and even better results are obtained with concentrations of at least 50 %. (Concen- trations of H2S04 are weight percents). At the point of its introduction, the regenrating solution is passed downwardly through an upper increment of the resin, thereby assuring completion of the regeneration of the resin increment before it is removed from the column. Usually, although not necessarily, the first resin increment contacted will be the uppermost increment immediately prior to its removal, the regenerating solution being introduced into the top of the column. The regenerating solution may percolate through the regenerating column under gravitational action, or its flow may be assisted by pump pressure. The flow may be continuous, but is preferably interrupted during the introduction and removal of the resin increments. Concurrently with the introduction of the regenerating solution into the upper portion of the column, a magnesium ion-containing aqueous sulfuric acid solution is removed from the lower portion of the column. The acid concentration of the regenerating solution decreases as the hydrogen ions of the acid are exchanged for the magnesium so that the removed solution will have a substantially lower acid concentration, such as a concentration of from 20 to 50 % H2S04 by weight. The H2 SO4 concentration will be reduced as it moves down the column. A differential concentration of at least 10-20 % or more is desireable, such as from 50 % on introduction to 30 to 40 % on removal. The concentration of the H2 SO4 solution con tainlng the eluted magnesium as removed from the bottom o the column can range from 20 to 70 %, depending on the concentration of the regenerating solution at the top of the column. The removed solution containing the eluted magnesium is at a concentration where the magnesium sulfate is highly soluble. However, the MgS04 can be readily precipitated therefrom by increasing the sulfuric acid concentration. For example, this can be accomplished by adding concentrated aqueous sulfuric acid thereto, such as sulfuric acid having a concentration of at least 80 %, the amount of concentrated H2S04 required being determined by the amount and acid concentration of the magnesium containing solution. For this reason, and because more magnesium sulfate may be precipitated from a solution containing a high concentration of magnesium, the volume of regenerant is kept low, while the acid concentration and magnesium content are correspondingly high. For example, in one embodiment, after preparation and seeding of the solution, the magnesium sulfate is precipitated in an H2SO4 concentration of from 70 to 80 %. The supernatant solution, at a corresponding H2S04 concentration, can be separated from the magnesium sulfate precipitate, or separately removed, and used for other purposes. For example, the H2SO4 solution at a concentration of from 70 to 80 % is suitable for use in fertilizer plant phosphaterock digestion, or can be reused as the column regenerating solution. In an advantageous embodiment, 80 to 95 % H2SO4 is added to the solution -removed from the columm, which increases the H2SO4 concentration of the solution and also raises its temperature in preparation for the precipitation step. The temperature in the crystallizer is desireably maintained above 750C, such as within the range from 75 to 1000C. A good operating range is from 87 to 940C. Such temperatures tend to reduce the amount of H2 SO4 in the co-crystallization precipitate (MgSO4 . xH2 SO4) so that the loss of H 2S04 is closer to the theoretical minimum of equal moles of H 2S04 and MgSO4 (MgS04 . H2S04), and much less than three moles of H2 SO4 per mole of MgSO4 (MgSO4 . 3H2S04). The present invention also preferably involves a procedure for washing the regenerated resin increments after their removal from the top of the regeneration column. As removed, the resin increments will contain sulfuric acid at the concentration of therogennrnting solution in the upper portion of the column, such as 40 to 70 % H2SO4. In removing the sulfuric acid, solution from the regenerated resin preparatory to the reuse of the resin for further processing of phosphoric acid it is preferred to first wash the removed resin with aqueous sulfuric acid at a concentration of from 20 to 50 % H2S04 by weight Optionally, a second acid wash, at a lower-concentration than the first wash is used before the resin is washed with water. Preferably, at least part of the acid and water washes after removal from the resin are combined for reuse as the acid wash for further increments of regenerated resin. This procedure will be described more specifically in connection with Fig. 1 of the accompanying flow sheet. The effluent from the first wash, being of highest acid concentration can be reused. Further, at least part of the combined wash solutions can be used for dilution of a 95 % sulfuric acid starting material. For example, the combined washes at concentrations of from 20 to 70 % H2S04 by volume may be mixed with portions of the removed supernatant from the magnesium sulfate precipitation. With the resin wash procedure described, rapid changes in the concentration of H2S04 in contact with the resin beads are avoided. For example, as removed, the sulfuric acid in contact with the resin may have a concentration of 50 %. The first acid wash may comprise sufuric acid of a concentration of 30 %, and that wash solution will be removed by the final water wash. Such staged reduction of sulfuric acid concentration tends to avoid degradation of the resin beads, such as by fracturing or spalling of the beads. A typical operating sequence will be described with reference to the flow sheet of Fig. 1. As shown, the cation exchange resin with the adsorbed magnesium is introduced into the bottom of the magnesium removal column. In the illustration given, the column is shown as containing resin increments 1 to 7, the resin beads being packed and filling the column from top to bottom. The uppermost increment (7) is contacted with the incoming regenerating solution (viz. 40-70 % H2SO4). The newly introduced increment (1) at the bottom of the column is contacted with the H2SO4 solution of reduced concentration (viz. 20-50 % H2 SO4), which is being removed from the column bottom through a valve-controlled line. This solution contains the magnesium ions, and is transferred to MgSO4 precipitation. As each new increment 6f resin is introduced into the column an increment of corresponding volume is ejected from the upper portion of the column through a line provided with an appropriate resin valve, being transferred to the resin receiver vessel for further processing. In the receiver vessel the regenerated increment of resin beads is treated to remove the residual concentrated sulfuric acid (40 - 70 % H2S04). In a preferred sequence, the free sulfuric acid liquid is first ex pelled from the resin by the introduction of compressed air, the expelled liquid being discharged through a valvecontrolled outlet line. The resin is then washed with aqueous H2SO4 of intermediate concentration (viz. 30 40 % H2SO4). If needed to avoid damage to the resin beads, a further lower concentration acid wash can then be used (viz. 5 - 20 % H2S04). Water is used as the final wash, and the resin beads are dried in the receiver by a compressed air expulsion of the liquid. The dried resin may be rewet with product H3P04 and passed to the regenerated resin-transfer vessel. In transferring the resin increment from the resin receiver vessel, the resin valve on the line to the regenerated resin transfer vessel is opened, and the resin increment falls into the lower vessel, which may contain a pool of product H3P04. The transfer can be accomplished by air pressure generated in the resin receiver vessel, and/or by introducing liquid into the resin receiver vessel, such as the product phosphoric acid (after removal of the magnesium and calcium). In one mode of operation, the Mg ion solution of 20 to 50 % H2 SO4 is removed from the bottom of the column and passed to a crystallization operation. As shown in Fig. 1, the solution can be introduced into a pre-crystallizer to which is added concentrated H2S04 (80 - 95 %), which heats the solution. In practice, the added H2 SO4 may be commercial grade H 2S04 of 93 % concentration. The heated mixed solution is passed to a crystallizer. Crystallizer concentrations of 70'- 80 % H2S04 and temperatures of 75 - 850C are desireable. For example, a concentration of about 75 % H2 SO4 can be used advantageously with a temperature of about 800C. Seeding with preformed crystals promotes the crystallization. The crystalline precipitate comprises co-crystallization compounds of MgSO4 and H2S04, as explained above. With the preferred conditions ratios of as low as 1.4 moles of H2 504 per mole of MgS04 can be obtained. This precipitate collects in the conical bottom portion of the crystallizer for periodic removal through-a solidstransfer valve, as indicated. The removed precipitate can be centrifuged to separate residual liquid. The supernatant from the outer portion of the crysta-llizer is removed, and, if required, further separated from any precipitate therein.

Claims: CLAIMS: 1. The method or regenerating a cation exchange resin loaded with adsorbed magnesium ions and precipitating the stripped magnesium ions, characterized by the steps of: (a) sequentially introducing increments of said loaded resin into the bottom of a regeneration column while sequentially removing regenerated increments of said resin from the top of said column;. (b) introducing an aqueous sulfuric acid (H2S04) regenerating solution into the upper portion of said column at a concentration of 40 % or higher H2SO4 by weight andpassing said regenerating solution downwardly through an upper increment of said resin before removal of said increment from said column; (c) removing a magnesium ion-containing sulfuric acid solution from the lower portion of said column at a concentration of'20 % or higher H2S04 by weight, said concentration being reduced from the introduction to the removal of said acid; and (d) precipitating magnesium sulfate from said removed solution by adding concentrated sulfuric acid thereto having a sufficiently higher H2 SO4 concentration to cause the magnesium sulfate to crystallize as co-crystallization compounds of MgS04 and H2SO4. 2. The method of claim 1 in which said H2SO4 as introduced in step (b) has a concentration of at least 50 %, and said- added H2 SO4 in step (d) has a concentration of at least 80 %. 3 The method of claims 1 and 2 further characterized in that the regenerating solution introduced into said column has a concentration of 40 to 70 % H2S04 by weight. 4. The method of claims 1 and 2 further characterized in that said magnesium sulfate is precipitated at a concentration of at least 70 % H2 504 by weight, and a supernatant solution of at least 70 % H2 SO4 by weight is separated from the said precipitate. 5. The method of claims and 4 further characterized in that the precipitation of step (d) is carried out at a temperature above 7500 6. The method of claims 1 and 4 further characterized in that the precipitation of step (d) is carried out at a temperature from 87 to 940cm 7. The method of claims 5 and 6 further characterized in that the temperature of the solution removed in step (c) is increased by adding thereto sulfuric acid of 80 to 95 % concentration for precipitation in step (d). 8. The method of claims 1, 2 and 3 further characterized in that said resin for regeneration contains adsorbed calcium ions together with the magnesium ions but not over one mole of calcium being present per 9 moles of magnesium. 9. The method of claims 1, 2 and 3 further characterized in that said resin for regeneration contains organic matter from wet process phosphoric acid. 10. The method of claims 1, 2 and 3 further character:zed in that said resin for regeneration contains adsorbed calcium ions together with the adsorbed magnesium ions but not over one mole of calcium being present per 20 moles of magnesium, and in that said resin contains, organic matter from wet process phosphoric acid. 11. The method of claims 1, 2 and 3 in which the resin increments removed from the top of said column contain sulfuric acid at the high concentration of the regenerating solution as introduced, and in which the removed increments are first washed with aqueous sulfuric acid of an intermediate concentration with respect to the regenerating solution and water, and thereafter the increments are washed with water.

Inventors: HEDRICK, HAROLD NELSON, WHITNEY, SOLON GENE
Applicants: AMERICAN PETRO MART, INC.
Application year: 1982
Main classification: B01J49
IPC codes: C01F5, C01B25, B01J49, B01D15