PARALLEL ALIGNMENT OF LIQUID CRYSTALS ON CONDUCTIVE SUBSTRATES

Abstract: Parallel alignment of liquid crystals on conductive substrates for use in dc applications is accomplished by providing the conductive substrate with an essen­ tially transparent organic polymer coating and subse­ quently micromachining parallel grooves therein which sympathetically align and retain the molecules of liquid crystals brought in contact therewith.

Description: PARALLEL ALIGNMENT OF LIQUID CRYSTALS ON CONDUCTIVE SUBSTRATES TECHNICAL FIELD This invention relates, generally, to the alignment of liquid crystals in electro-optical devices and more particularly to the parallel alignment of liquid crystals in direct current (dc) electro-optical devices. BACKGROUND OF THE INVENTION 1. Field of the Invention It is desirable in the fabrication of electrooptical devices having liquid crystal therein to induce uniform molecular alignment of the liquid crystals for several reasons. For example, it is known that the temporal response of liquid crystals is dependent, inter alia, on the alignment of the liquid crystal material, and uniformity of liquid crystal alignment influences the contrast ratio of the electro-optical device by affecting the "fieldoff't appearance of the liquid crystal. This invention describes a method of inducing and maintaining parallel alignment of liquid crystals in de electro-optical devices. 2. Prior Art Parallel alignment in liquid crystal devices was first induced by rubbing (P. Chatelain, Bulletin Society France Mineral, Vol. 66, pp. 105 (1973); D. W. Berreman, Physics Review Letters, Vol. 28, pp. 1683 (1973) and U. S. Patent 3,834,792 issued to H. Sorkin in 1975). Rubbing, however, produces non-uniform striations that are readily visible with polarizers in proJection displays and In systems used for optical data processing. Improved techniques for inducing parallel alignment of liquid crystals that are costly and only applicable for alternating current (ac) applications include (1) vapor deposition of SiO at an angle (U.S. Patent 3,834,792, issued to J. L. Janning in 1974 and U.S. Patent 3,93a,242, issued to A. Sussman in 1976), (2) micromachining of SiO2 deposited onto a substrate by ion beam etching ("k New Method For Inducing Homogeneous Alignment of Nematic Liquid Crystals" by Michael J. Little et al, Liquid Grystals and Ordered Fluids, Vol. 3, pp. 499 (1978), and (3) vacuum depositing an inorganic film onto a noncondutive substrate using a vapor deposition angle of approximately 50 to the plane of the surfaces to be coated (U.S. Patent 3,885,860, issued to Howard Sorkin in 1975). Attempts to ion beam etch conductive substrates, in order to induce stable parallel alignment of liquid crystals subsequently brought in contact therewith, have not been successful. The results of these attempts were erratic and unstable (layer, G.D., "Alignment of Nematic Liquid Crystals by Surface Dipoles, presented at 7th International Liquide Crystal Conference, Bordeaux, France, July 1-5, 1978). Thus there are no suitable methods, known to this inventor, for inducing parallel alignment of liquid crystals on conductive substrates intended for use as electrodes in dc electro-optical devices which yield stable uniformly parallel alignment of the liquid crystal materials. SUMMARY OF THE INVENTION In seeking to provide dc operable electro-optical devices comprising uniformly parallel aligned liquid crystals, it has been discovered that parallel alignment of liquid crystals on conductive substrates can be inexpensively and easily achieved by coating the conductive substrate with an essentially transparent organic -polymer, and subsequently micromachining the coated substrate at a shallow angle to provide a multiplicity of substantially uniformly parallel grooves in the surface of the substrate coating. .This process provides a conductive substrate which sympathetically aligns the molecules of liquid crystals, subsequently brought in contact therewith, and liquid crystal alignment by this process is reproducible and stable. It is therefore one purpose of this invention to provide a method of inducing parallel alignment of liquid crystals on conductive substrates for dc applications. An additional purpose of this invention is to provide a relatively inexpensive method of inducing and maintaining stable parallel alignment of liquid crystals on conductive substrates. A still further purpose of this invention is to provide a method of reproducibly aligning liquid crystals on the surfaces of conductive substrates parallel to the surface of said substrates. That the above-stated purposes, which constitute advantages over prior art liquid crystal alignment methods, have been accomplished will be apparent, as will other advantages of this invention, upon reference to the following detailed description of the invention. DETAILED DESCRIPTION OF THE INVENTION In seeking to provide an improved method of inducing parallel alignment of liquid crystals on conductive substrates for use in dc electro-optical devices, it has been discovered that excellent parallel alignment of liquid crystals on conductive substrates such as indiumtin-oxide (ITO), zinc sulfide (ZnS), cadmium sulfide (ode), indium oxide (In203), tin oxide (SnO), chromium (cur) silver (Ag), gold (Au), and aluminum (Al) can be induced by first providing the surface of the conductive substrate with an essentially transparent (to light in the visual wavelength ranges) organic polymer coating, and subsequently micromachining the coated surface to provide a multiplicity of microgrooves therein which sympathetically align liquid crystals (LC) brought in contact therewith. The term "liquid crystals" as used herein means a liquid crystal compound, a mixture of liquid crystal compounds, a mixture of liquid crystal compounds containing conductive dopants, or a mixture of liquid crystal compounds in an appropriate solvent which itself is not a liquid crystal compound. Liquid crystal compounds derived from the phenylbenzoate esters are of primary interest in the fabrication of dynamic scattering mode (DSM) electrooptical devices. However, the process of this invention is not limited to the alignment of phenylbenzoate ester liquid crystal compounds. It may be employed to align other LC compounds such as the Schiff bases, azoxybenzenes, bephenyls, and phenylcyclohexanes. The surface of a selected substrate is thoroughly cleaned of adsorbed contamiants with an organic detergent such as that sold by International Products Corp. of Trenton, New Jersey under the trade name "Micro" and an organic solvent, such as that sold by Transene Company, Inc. under the trade name "Transene 100", before the polymer coating is applied. Other suitable detergents and solvents may be used to remove absorbed contaminants from the substrate surfaces. Organic polymers may be applied to the surface of the selected subset'rate by conventional techniques for applying coatings from polymer-solvent solutions or they may be formed in situ by plasma polymerization or they may be applied from a melt or they may be applied by other suitable techniques. Spin coating techniques, such as that described in "Characteristics of Resist Fibers Produced by Spinning by Dietrich Meyehofer, Journal of Applied Physics, Vol. 49(7), page 3993, July 1978, are particularly suitable inasmuch as smooth coatings of uniform thickness are obtained via the use of this method. Organic polymers found to be useful in this invention include polyvinyl alcohol, plasma-polymerized ethanes and polyimides. The best results have been obtained with 1 to 10% aqueous polyvinyl alcohol solutions, which are readily prepared from inexpensive, abundantly available materials purchased from chemical supply houses. When the polymer coating is applied from an aqueous solution, it is necessary to remove all traces of moisture from the surface coating. This is accomplished by baking the coated substrate at temperatures in excess of 100%C in a dry atmosphere. In addition, baking causes the polymers to harden and thereby become amenable to micromachining. Contrary to commonly held beliefs, polymeric coatings may be reproducibly micromachined by ion beam etching at shallow etch angles. The specific etch conditions will vary with the choice of polymer used as a coating and the choice of substrate material. However, with polyvinyl alcohol (PVA) coatings, good alignment of liquid crystals was obtained when the polymer coating was bombarded with argon ion beams at a 200 etch angle from an apparatus operating from 5 seconds to as long as 3 minutes at 2,400 volts and 0.18 ampere maximum current to yield 0.12 milliampere/cm2 current densities and the substrates were either ITO or ZnS. On the ocher hand, the same operating conditions resulted in a complete removal of the PVA coating from an ITO substrate when the etch time was five and Ïne-half minutes. While tests to optimize operating parameters such as sample distance from ion beam source, specific ion beam source, etch angle, and operating pressures have not been concluded, sample-to-source distances of two inches using argon ion beams at operating pressures of 1 x 104 torr have proven to be suitable. Etch angles ranging from 100 to 300 appear to be appropriate for inducement of parallel alignment. The key is to select operating parameters which yield substantially uniformly parallel grooves in the coating without destroying the coating. Further, the grooves should not penetrate the coating to reach the substrate surface. While ion beam etching has proven to be adaptable to, and suitable for, providing parallel grooves in.baked polymeric coatings, other suitable techniques of anisotropic etching which do not destroy the polymeric coating may be utilized. For examples of such techniques, see "Introduction to Reactive Ion Beam Etching by D. F. Downey et al, Solid State Technology, Vol. 24, No. 2, page 124, (February 1981). Specific applications of the process are shown in the following examples. Example I The electrodes used for alignment tests were 1/8 inch thick glass with indium-tin-oxIde (ITO) coatings supplied by Optical Goating Laboratory of Santa Rosa CA. (OCLI). They were cleaned with detergent and organic solvents to remove adsorbed contaminants. Each electrode was coated with polyvinyl alcohol (PVA) solution using a photoresist spinner at 2000 rpm for 60 seconds. A polymer solution (polyvinyl alcohol in water) available from American Liquid Crystal Chemical Corporation of Kent, Ohio under the tradename SA-72, was used in the supplied concentration in one instance and diluted with water up to 1:4 ratio in another instance. The same result can be obtained by using an aqueous solution of 1-5% polyvinyl alcohol, such as Elvanol grade 71-30 available from Du Pont Chemical Co. of Wilmington, Delaware or a similar material. After the electrodes had been coated with the polymer, they were baked at 1000C for 16 hours under nitrogen atmosphere to eliminate any residual water from the substrate that might cause liquid crystal decomposition, thereby producing a dry, coated substrate surface. The dried substrates were ion beam etched (IBE) at a shallow angle of 200 for 2-5 seconds in a Vecco Microetch apparatus which produces randomly distributed parallel grooves spaced 20 to 100A apart. This ion beam sputtering system and its operation has been well described in the literature (see, e.g., M. J. Little et al Liauid Crystals and Ordered Fluids, Volume 3, page 497 (1978)). A typical sandwich type cell was assembled with two ITO electrodes that were coated with PVA and IBE using a 1/4 mil Mylar spacer and Merck Chemical Co. N.P. 5 liquid crystal mixture. The quality of surface alignment was evaluated between crossed polarizers under the microscope at 125x magnlSication. The alignment was good, uniform, and dark colored over the entire aperture. As the cell was operated in the variable grating mode (VGM), it showed straight parallel domain lines uniformly over the whole surface area. Alignment stability, tested by operating the VG! cell with 15 volts dc signal for 64 hours, showed no change in alignment. Example 2 The above described alignment technique with ion beam etched polymer was tested on zinc sulfide (ZnS) substrates. These ZnS electrodes were made bt evaporating a 5 micron thickness ZnS layer on ITO substrates. Due to the thickness and roughness of the ZnS layer, until now there were no successful ways of aligning these substrates by polishing and either rubbing or ion beam etching. However, polymer-coating the ZnS produced a smooth surface and enabled the use of ion beam etching alignment. The procedure for polymer coating and ion beam etching the PVA-coated ZnS was the same as for PVA-coated ITO. Two liquid crystal cells were fabricated with the ZnS photoconductor and ITO counter electrodes using Merck N.P.5 liquid crystal and 1/4 mil Mylar spacer. Both cells showed gdod uniform homogeneous alignment and uniform domain structure when dc voltage was applied to the cells. Industrial Applicability The method of inducing parallel alignment of liquid crystals on conductive substrates discussed above is relatively inexpensive and yields stable reproducible results. Penis method is therefore useful in the fabrication of electro-optical cells for numerous light display systems and data processing systems.

Claims: CLAIMS 1. An improved method for parallel aligning liquid crystals on conductive substrates used as 4 electrodes and direct current electro-optical devices comprising the steps of: first applying-a uniform coating of an essentially transparent organic polymer to the surface of a conductive substrate; and subsequently micromachining said surface coating at a shallow angle to provide a multiplicity of substantially uniform parallel grooves therein which function to align and retain liquid crystals subsequently applied thereto. 2. The method of aligning liquid crystals on the surface of conductive substrates in accordance with Claim 1 wherein said substrate is an electrode prepared from materials selected from the group consisting of indium-tin-oxide, zinc sulfide, cadmium sulfide, indium oxide, tin oxide, chromium, silver, gold and aluminum. 3. The method in accordance with Claim 1 wherein said organic polymer is an aqueous solution of polyvinyl alcohol and said surface coating is micromachined by bombarding said coating with ion beams at an etch angle not to exceed 30". 4. The method in accordance with Claim 3 wherein the etch angle ranges from 100 to 300. 5. The method of Claim 1 comprising the steps of: a, first providing an aqueous solution of polyvinyl alcohol containing from 1 to 108 polyvinyl alcohol; b. applying a coating of said polyvinyl alcohol to the surface of said substrate from said solution, thereby forming a coated substrate; c. baking said coated substrate under dry nitrogen, thereby removing all traces of moisture from said coating; and d. subsequently micromachining said coating to provide uniform grooves therein by bombarding said coating with ion beams at an etch angle not to exceed 30 thereby providing a prepared surface which causes subsequently applied liquid crystals to align themselves parallel to the axis of said grooves and adhere to said polyvinyl alcohol coating. -6. An electro-optical device prepared by the process of any of the preceeding claims.

Inventors: LACKNER, ANNA M.
Applicants: HUGHES AIRCRAFT COMPANY
Application year: 1982
Main classification: G02F1
IPC codes: G02F1, H01L31