HETEROGENEOUS CATIONIC CATALYTIC SYSTEMS SUITABLE FOR THE OLIGOMERISATION OF LINEAR NON-TERMINAL OLEFINS, AND A PROCESS FOR PREPARING SAID OLIGOMERS USING SAID SYSTEMS

Abstract: A process is described for preparing oligomers from linear non-terminal olefins in the presence of a catalytic system comprising a strong inorganic acid, or its an­ hydride, deposited on a support having a surface area exceeding 50 m²/g, and gaseous BF₃. The acid, preferably phosphoric, or its anhydride is present on the support, which is preferably carbon, silica or aluminum, in a quantity variable between 20 and 100 parts by weight per 100 parts of support.

Description: This invention relates to an improved process for preparing non-terminal olefin oligomerswhich uses a special catalytic system comprising gaseous boron trifluoride in the presence of a strong acid or the relative anhydride, which has been previously deposited on a suitable support. It also relates to the said catalytic system. It is known to prepare synthetic bases for lubricating oils of high viscosity index by the cationic oligomerisation of suitably chosen alpha-olefins. In particular, by starting from l-decene a product is obtained which consists mainly of a C30 trimer which, after hydrogenation, constitutes an excellent base for synthetic lubricating oils of excellent characteristics in terms of their viscosity index, viscosity at 210 F, volatility, pour point etc. These products have therefore been favourably received in the synthetic lubricant field, and their use is being widely developed. The exceptional rheological properties of the said product are due both to its particular molecular structure (presence of branches of suitable length) and to the rigorous control of the molecular weight which prevents the presence both of low molecular weight substances which would increase the volatility of the product, and of higher oligomers which would cause the viscosity of the mixture to increase to unacceptable values. however, B(-olefin oligomers present a serious economical problem connected with the high cost of the initial eWolefin, because of which it would be desirable to be able to prepare products with similar rheological characteristics starting from less costly and more easily available monomers. The applicant has found it possible to prepare products with characteristics analogous to the products obtained from l-decene by starting from suitable types of linear non-terminal olefins using a controlled oligomerisation process, and has identified a particular cat ironic catalytic system suitable for this purpose. In the presence of this system it is possible to obtain products which, after hydrogenation, have excellent properties as bases for synthetic lubricants, starting from linear nonterminal olefins which constitute a raw material less costly than dWolefins, and available from the known linear alkane dehydrogenation processes, and in particular the Olex process. It is known that non-terminal olefins can also be oligomerised in the presence of Friedel-Crafts catalysts to give products with a wide molecular weight dispersion. It is likewise linown to be difficult to obtain products by this method having ood characteristics as lubricants, unless costly fractionation operations are used, and which in addition lead to large quantities of products having unacceptable characteristics, so increasing the overall cost of the process. he he present applicant is also the proprietor of a patent application, namely Italian patent application o. 20106 A/80 filed on 22.2.1980, which relates to a reaction for the selective oligomerisation of non-terminal olefins by means of which it is possible to obtain products only in the form of dimers or trimers. Thus by starting from suitable non-terminal olefin cuts, products are obtained containing only small auantities of fractions which cannot be used in the lubricating oil field. The following advantages are obtained in this manner: 1) the costly fractionation of reaction mixtures is made superfluous; 2) there is almost complete utilisation of the monomer non terminal olefins; 3) the oligomers obtained from suitable non-terminal olefin cuts have excellent rheological properties which are distinctly superior to those obtained by conventional Friedel-Crafts catalysts. In this respect, the value of the viscosity at 1000C is particularly important, as it must lie between narrow limits (generally between 3 and 6 cSt) to enable the oil to be used as a base for synthetic lubricants. In addition, the product must have a high VI value, a low pour point, and an open cup inflammability temperature greater than 2000C. The process described in the said patent application is based on the use of a catalytic system chosen from adducts of AlC13 with esters, complexes of BF3 with alcohols or organic or inorganic acids, or AlCl3 dispersions on special supports. however, even though they have the aforesaid undoubted advantages, the catalytic systems of the said patent appli cation have the following drawbacks which are not always easy to obviate: 1) catalysts based on adducts of A1C13 with esters form by interaction with the monomers a viscous liquid which is insoluble in the reaction medium which constitutes the true initiator of the polymerisation, which therefore takes place by liquid-liquid contact only with difficulty in the dispersion of the two liquids, the possibility of reusing the catalyst being poor. In addition, a high reaction temperature is necessary ( > + 1400 C), and the dimer selectivity in the reaction is low. 2) catalysts based on complexes of EF3 with alcohols or organic or inorganic acids also form by interaction with the monomer a viscous liquid which is insoluble in the reaction medium, so creating problems relating to its dispersion, difficulty in the final separation of the catalyst from the reaction product, catalyst loss by entrainment, and difficulty in reusing the catalyst. 3) AlCl3 dispersions on SiO2 or Al2O3 require a high reaction temperature ( > 120 C) and have low dimer selectivity. It has now been found, and constitutes the subject matter of the present invention, that it is possible to prepare oligomers from linear non-terminal olefins without any of the aforesaid problems by simply carrying out the polymerisation reaction in the presence of a catalytic system comprising a strong inorganic acid or its anhydride deposited on a suitable support of suitable surface area, and gaseous BF, this latter being present at a pressure variable between 0.3 and 10 atmospheres, Phosphoric, pyrophosphoric, sulphuric, perchloric, hydro fluoric, fluorophosphoric and polyphosphoric acids can be used. The support is constituted by a material having a surface area greater than 50 m2/g, preferably greater than 200 m2/g, and a pore volume greater than or equal to 0.5 ccXg. Carbon, silica and alumina are particularly suitable as supports. The acid or its anhydride is present on the support in a quantity varying between 20 and 100 parts by weight per 100 parts of support. The following special advantages are obtained by using the said catalytic system: 1) The catalyst remains in the solid state finely dispersed on the surface of the support during the course of the reaction. The oligomerisation reaction takes place by solid-liquid interaction on contact between the catalyst and the monomer. The separation of the reaction mixture from the catalyst at the end of the reaction is immediate and facilitated. There is also a higher reaction rate and a more controlled and uniform reaction. 2) rlne catalyst can be used in subsequent oligomerisation reactions, if necessary making up only the gaseous BF3 consumed. In this manner the catalyst consumption can be very low. 3) The removal of sludge or pitch which collects on the bottom of the reactor is facilitated. 4) The process is greatly simplified, especially in the case of continuous operation. 5) he catalyst selectivity is very high, so that the reaction product can be used after hydrogenation, as such, in engine lubricating oil formulations without the need for distillation, by merely eliminating the unreacted monomer and small percentages of volatiles. The non-terminal olefins which can be used comprise linear chain monoolefin hydrocarbons of general formula C2H2n, with n variable from 10 to 20, and containing an unsaturated olefin bond in any position within the molecule. The unsaturated olefin bond configuration can be either of the trans or cis type. These non-terminal olefins are generally available commercially in the form of mixtures, for example a C11 - C14 mixture, a C15 - C18 mixture etc. The oligomerisation reaction can be carried out in mass or in the presence of solvents. The solvents are preferably linear or branched saturated aliphatic hydrocarbons such as n-pentane, n-hexane, n-heptane or their mixtures. The reaction is carried out at a temperature of between 10 and 1300C, and the reaction time can vary from 1 to 8 hours. The reaction products are oligomers of the starting monomers, mainly dimers with small quantities of trimers, as shown by gas chromatography analysis coupled with mass spectrometry. They are freed from the unreacted residual monomers by vacuum distillation at suitable temperature. The distillation residue can be either subjected directly to analysis and to an evaluation of technical properties, or can be subjected to vacuum distillation in which case a small quantity (about 5) of high boiling products is discarded. For use in the synthetic lubricating oil sector, the oligomers produced must be hydrogenised in the manner already described in previous patent applications (application 2593 A/74, application 25811 A/77). The rheological characteristics of the oligomers do not vary substantially during the hydrogenation process. Both the physico-chemical and technical characteristics relevant to use in the synthetic lubricant field were determined for the final reaction products thus obtained. The degree of unsaturation is expressed as the bromine number (g of Br absorbed by 100 g of oil) and was determined as described in "Organic Analysis" Vol. III, Interscience Fub. New York (1956). The iÇ distribution was determined by the GPC method (gel permeation chromatography) using the Waters instrument mod. I1CfGPC - 201 in toluene. The viscosity was determined both at 100 and 210 F by the ASTM D 445-74 method. The viscosity index (VI) was calculated by the ASTM D 2270-75 method. The pour point was calculated by the ASTM D 97 method. The open cup inflammability temperature was determined by the ASDIC D 92 method. The foregoing together with the operatin details are apparent from the following non-limiting examples of the invention. EXAMPLE 1 50 g of activated carbon in the form of small cylinders (# 4 mm) having a surface area of 1400 m2/g and a pore volume of 0.8 cc/g are previously dried in an oven at 1200C for 4 hours. 65 g of H3PO4 (conc. 85% by weight) are weighed out separately and poured slowly on to the carbon sample kept under agitation. The acid is completely absorbed in the pores of the support. The sample is transferred to an oven and dried at 120 0C for 14 hours in air. The acid content calculated as the quantity of P205 present on the support is 80 g per 100 g of carbon. 1.8 g of catalyst are withdrawn and subjected to a vacuum of 0.2 torr at 1200C for 2 hours. The system is then returned to atmospheric pressure with dry N2, and operating in a dry N2 atmosphere is transferred into a container in the form of a cylindrical basket made from a stainless steel mesh with ASrili 20 mesh apertures. The container is suspended inside an autoclave of capacity 200 ml provided with a magnetic stirrer, and into which 100 ml of a fraction consisting of C13- C16 non-terminal olefins are fed under a dry N2 atmosphere, this fraction having the following % composition by weight: C13 23.7 C14 35.1 C 26 8 15 C16 14.4 The double bonds present are mainly of trans type (61%), and they are disposed statistically in each position of the molecule. The autoclave is temperature controlled at 1000 C, at which gaseous BF3 is introduced from a suitable cylinder until a final pressure of 3 atm is obtained. An increase in the liquid temperature of 60C is observed, and this is reabsorbed by the system over a period of ten minutes. The reaction is continued under stirring while maintaining the temperature constant at 1000 C for 5 hours, during which the BF3 pressure falls to 0.8 atm. Stirring is stopped, the reaction product is discharged, 100 ml of monomer are reintroduced, and the BF3pressure is raised to its initial value. The previously described procedure is repeated, during which the 3F3 pressure remains practically constant over the course of the reaction, and the cycle of operations is repeated for a further three times without varying the pressure of the gaseous BF3 present. rihe products obtained during the various operation cycles were examined separately after quenching with an ammonia cal solution, to give the following results: a) Conversion % b) Selectivity % 1st test 80 84 2nd test 81 82 3rd test 79 79 4th test 78 79 5th test 75 78 a) determined by GC; b) dimer/(dimer + higher oligomer) ratio determined by GC. The quantity of H3PO4 found on the reactor bottom after the test cycle was determined by acidimetric titration, and was found to be very low and less than 2% of the overall quantity of H3PO4 present in the system. It can be seen that the catalyst performance remained practically unchanged in subsequent tests, and that under the conditions used there were no noticeable signs of ageing or poisoning of the catalytic system. The products obtained during the various tests are added together and washed with a solution of NH3 (conc. 3' by weight) in water and then with water until neutral They are then subjected to vacuum treatment (0.2 mm Hg) in order to remove the unreacted monomers (2l,%'), and then hydrogenated by operating in mass in the presence of Pd supported on carbon (5% of Pd) to the extent of 4 , by weight with respect to the oil, at a temperature of 1500C and at a H2 pressure of 10 atn for 5 hours. The hydrogenated oil separates from the catalyst by filtration, and is subjected to further vacuum treatment (1600C, vacuum 0.2 mm ng) in order to remove the last traces of volatile products (2W). Their physico-chemical and technical characteristics are then evaluated. The product has the following characteristics: d = 0.8284 icc Br No. = 0.31 100 g oil. Open cup inflammability temperature = 205 C. Fraction distilled off up to 206 C under a vacuum of 5 torr = 2% (distillation ASTM D 1160). The rheological properties are as follows: #100 C = 4.25 cSt #40 C = 20.30 cSt V.I. = 114 Pour point = 42 C These indicate that the oil under examination, even though not having undergone any rectification operation, completely satisfies the characteristics required for its use as a base for synthetic lubricants of high viscosity index. EXAMPLE 2 The procedure described in example 1 is followed, feeding into the same reactor 0.30 g of E3P04 of 98,%' concentration, and 100 ml of the same mixture of non-terminal olefins. BF3 is then fed into the autoclave under a pressure of 3 atm, on which a temperature increase of 80C is noted. The reaction proceeds for 5 hours during which the BF3 pressure falls to 0.6 atm. 'he operations described in example 1 are repeated for the sane number of experiments, to give the following results: Conversion ,- Selectivity ;o 1st test 82 2nd test 80 74 3rd test 68 73 4th test 58 72 5th test 24 72 The results show a progressive reduction in catalytic activity with obvious signs of catalyst poison. At the end of the reaction, the formation of black sludge is noted on the bottom of the reactor. EXAMPLE 3 50 g of active carbon (cylinders # 4 mm) having a surface area of 820 m2/g and a pore volume of 1 cc/g are dried in an oven at 120 C for 4 hours. 40 g of H3PO4 (conc. 85%) are diluted separately with 25 ml of H2O, and are added to the carbon sample kept under agitation. The procedure described in example 1 is followed, to give a product containing 50 g of P 0 per 100 g of carbon. 25 2.4 g of catalyst are withdrawn and the procedure described in example 1 is repeated, using 100 ml of the following mixture of non-terminal C13-C15 olefins. C13 26.9% C14 44.3% C15 28.8^ Two successive tests are carried out using 3F3 at a pressure of 3 atm, to give the following results: Conversion ,% Selectivity ,0 1st test 81 85 2nd test 82 84 The reaction products are treated as described in example 1, and after hydrogenation give an oil of the following characteristics: #100 C = 4.30 cSt #40 C = 21.42 cSt V.I. = 107 inflammability T = 203 C pour point = 45 C These correspond fully to the characteristics required for using the product as a base for synthetic lubricants. EXAMPLE 4 The catalyst described in example 3 is treated at 30000 for 14 hours in air, cooled in a dry N2 atmosphere and used in oligomerisation reactions in the same manner as described in the preceding example. 1.2 g of catalyst are withdrawn and treated with the same quantity of non-terminal olefins as described in example 3. Two successive tests are carried out using BF at a pressure of 3 atm to give the following 3 results: Conversion % Selectivity % 1st test 84 83 2nd test 81 82 The results show that the activity of the catalytic system supported on carbon is higher the higher the catalyst drying temperature. EXAI;2LS 5 1.2 g of the catalyst described in example 4 are used, and the same procedure is followed using as monomer a fraction consisting of pure C13 non-terminal olefins. By operating at a temperature of 850C in the presence of BF3 at a pressure of 3 atm, a C13 olefin conversion to oligomers of 78% is obtained. ^eC analysis combined with mass spectrometry shows the presence of the various oligomers and monomers in the following concentrations: monomers 22% dimers 63% trimers 13.5s tetramers The analysis shows the high selectivity of the catalytic system and the absence of secondary reactions. EXAMPLE 6 50 g of silica in the form of extruded pieces of diameter 3 mm, of surface area 330 m2/g and pore volume of 1 ml/g are previously dried in an oven at 120 C for 4 hours and then treated with a mixture of 68 g of EDP04 (conc. 3) and 8 ml of Ei20, this mixture being added slowly while keeping the silica under agitation. The sample is transferred to an oven and dried at 1200C for 14 hours in air. The acid content calculated as the P205 quantity present on the support is 84 g per 100 g of silica. 1*8 g of catalyst are withdrawn, and operating as described in example 1, are used for reaction with 100 ml of the C13 - C16 mixture described in example 1 in the presence of BF3 at a pressure of 3 atm for a time of 5 hours. The oligomerisation reaction is repeated as described heretofore, and the products obtained in the two tests are subjected to CC analysis to give the following results: Conversion % selectivity 1st test 72 76 2nd test 70 75 EXASLE 7 50 g of alumina in the form of pellets of diameter 4 mm, surface area 220 m2/g and pore volume 0.7 ml/g are previously dried in an oven at 1200C for 4 hours and treated with 41.5 g of H3P04 (conc. 85.;';) to which 5 ml of water are added. The acid is completely absorbed by the support, and the product is transferred to an oven and dried at 1200C for 14 hours in air. The acid content calculated as the P O 25 quantity present on the support is 60 g per 100 g of alumina. 2.4 g of catalyst are withdrawn and used with the same quantities and same type of C13 - C16 fraction as described in example 1 in the presence of BF3 at a pressure of 5 atm for a time of 5 hours. Two oligomerisation tests are carried out, to give the following results based or: analysis of the products obtained: Conversion , Selectivity ;- 1st test 64 78 2nd test 62 ?9 On termination of the reaction, the solid catalyst is found to be unaltered, and the % H3PO4 quantity on the bottom of the reactor is found by acidimetric titration to be less than 2i3 of the total quantity present in the system.

Claims: CLAIMS: 1. A composition suitable for the oligomerisation of nonterminal linear olefins, comprising a strong inorganic acid or the corresponding anhydride deposited on a support having a surface area exceeding 50 m2/g and a pore volume equal to or greater than 0.5 cc/g, and gaseous BF3. 2. A composition as claimed in the preceding claim, wherein the acid is chosen from phosphoric, pyrophosphoric, sulphuric, perchloric, hydrofluoric and fluorophosphoric acid, and the polyphosphoric acids. 3. A composition as claimed in claim 1, wherein the support is preferably chosen from those having a surface area exceeding 200 m2/g. 4. A composition as claimed in one or more of the preceding claims, wherein the support is chosen from carbon, silica and alumina. 5. composition as claimed in one or more of the preceding claims, wherein the gaseous BF3 is present at a pressure variable between 0.3 and 10 atmospheres. 6. A process for the oligomerisation of non-terminal linear olefins, consisting of bringing the relative olefin into contact with the catalytic composition claimed in one or more of the receding claims. 7. 5 process for the oligomerisation of non-terminal linear olefins as claimed in the preceding claim, characterised in that the reaction is carried out in the presence of a solvent. 8. A process for the oligomerisation of non-terminal linear olefins as claimed in the preceding claim, characterised in that the solvent is preferably chosen from saturated linear or branched aliphatic hydrocarbons. 9. A process for the oligomerisation of non-terminal linear olefins as claimed in claim 5, characterised in that the reaction is carried out at a temperature variable between +10 and +130 C.

Inventors: ARRIGHETTI, SERGIO, FATTORE, VITTORIO, MANCINI, GIUSEPPE, PRIOLA, ALDO
Applicants: ANIC S.P.A.
Application year: 1982
Main classification: B01J21
IPC codes: B01J21, C07C2