POLYAMIDE MOULDING COMPOUNDS

Abstract: 1. Thermoplastic moulding compositions comprising I. 30-94% by weight of at least one polyamide, II. 70-3% by weight of a graft product prepared from a) 50-95% by weight of a cross-linked polymer of butadiene and/or subst. butadiene, which can optionally be composed to an extent of up to 40% by weight of styrene and/or acrylonitrile, as the graft substrate, and b) 5-50% by weight of graft monomers of alpha) 3-100 by weight of an ester of (meth)acrylic acid, beta) 0-80% by weight of styrene and gamma) 0-80% by weight of (meth)acrylonitrile, wherein the gel content of the graft substrate should be => 70%, measured in toluene, the graft yield should be G >= 0.15 and the average particle diameter of the graft copolymer should be >= 0.1 mu m, III. 20-3% by weight of a plasticiser customary for polyamide and optionally other customary additives, the sum of I. -III. and of a) and b) and of, alpha) - gamma) having in each case to equal 100% by weight.

Description: Polyamid-Formmassen Die Erfindung betrifft thermoplastische Formmassen aus Polyamiden, einem Pfropfprodukt auf Polydien-Basis und Weichmachern, die sich durch hohe Zähigkeit, ausgezeichnete Flexibilität, Wechselknickfestigkeit und dauerhafter Oberflächenbeschaffenheit auszeichnen. Aus der DE-OS 2 742 176 ist bereits bekannt, die Schlagund Kerbschlagzähigkeit von Polyamiden durch Zumischen von Pfropfpolymerisaten aus vernetzten Polybutadienen und aufgepfropften (Meth)acrylsäureestereinheiten zu erhöhen. Diese Formmassen besitzen ein hohes Zähigkeitsniveau, sind jedoch für bestimmte Anwendungszwecke, z.B. Schuhsohlen und Schläuche nicht geeignet, da hierfür ihre elastischen Eigenschaften nicht immer ausreichen. Es ist bekannt, dass diese Eigenschaften durch Zusatz von Weichmachern verbessert werden können. Die üblichen niedermolekularen Weichmachern diffundieren relativ rasch an die Oberfläche von Polyamidformkörpern, wodurch diese mit der Zeit verspröden und durch die Ablagerungen des Weichmachers ein unerwünschtes, unansehnliches Aussehen zeigen. Überraschenderweise wurde nun festgestellt, dass man nicht nur eine deutliche Verbesserung der elastischen Eigenschaften, insbesondere der reversiblen Dehnbarkeit und Wechselknickfestigkeit, erzielen kann, wenn man den mit den obengenannten Pfropfpolymerisaten modifizierten Polyamiden einen für Polyamide üblichen Weichmacher zusetzt, sondern dass sich der Glanz und die Oberflächenbeschaffenheit der entsprechenden Formkörper auch bei relativ längerer Lagerung nicht merklich ändert. Gegenstand der vorliegenden Erfindung sind daher thermoplastische Formmassen bzw. daraus hergestellte Formkörper aus: 1. 30-94, vorzugstweise 50-90 Gew.-%, bezogen auf die Gesamtformmasse, wenigstens eines Polyamids, TI. 70-3, vorzugsweise 50-5 Gew.-%, bezogen auf die Gesamtformmasse, eines Pfropfproduktes hergestellt aus a) 50-95, vorzugsweise 70-90 Gew.-% eines ver netzten Polymerisats aus Butadien und/oder substituiertem Butadien, das gegebenenfalls bis zu 40 Gew.-% aus Styrol und/oaer Acryl nitril aufgebaut sein kann, als Pfropfgrund lage und b) 5-50 Gew.-t, vorzugsweise 30-10, von Pfropf monomeren aus 4) 3-100 Gew.-% eines Esters der (Meth) Acrylsäure B) 0-80 Gew.-% Styrol und t) 0-80 Gew.-% (Meth)Acrylnitril, wobei der Gelanteil der Pfropfgrundlage #70 %, vorzugsweise #80 Gew.-% in Toluol gemessen, die Pfropfausbeute G 7/0,15, vorzugsweise 9,0,40, und der mittlere Teilchendurchmesser des Pfropfpolymerisats ?/ 0,1 m, vorzugsweise 0,2 0,6 m insbesondere ca. 0,3 - 0,5 Am betragen soll, III. 20-3, vorzugsweise 15-5 Gew.-%, bezogen auf die Ge samtformmasse eines für Polyamid üblichen geeigneten Weichmachers, und gegebenenfalls weiteren, üblichen Zuschlagstoffen, wobei die Summe aus I. - TII. bzw. a) und b) bzw. &alpha;) - #) jeweils 100 Gew.-% ergeben muss. Als Polyamide eignen sich alle thermoplastischen Polyamide, vorzugsweise teilkristalline Polyamide. So können als teilkristalline Polyamide für die erfindungsgemässen Formmassen Polyamid-6, Polyamid-6,6 und Copolymere aus diesen beiden Komponenten eingesetzt werden. Weiterhin kommen teilkristalline Polyamide in Betracht, deren Säurekomponente ganz oder teilweise aus Terephthalsäure und/oder Isophthalsäure und/oder Korksäure und/ oder Sebacinsäure und/oder Azelainsäure und/oder Adipinsäure und/oder Cyclohexandicarbonsäure, deren Diaminkomponente ganz oder teilweise aus m- und/oder p-Xylylendiamin und/oder Hexamethylendiamin und/oder 2,2,4-Trimethylhexamethylendiamin und/oder 2,4,4-Trimethylhexamethylendiamin und/oder Isophorondiamin besteht und deren Zusammensetzung aus dem Stand der Technik bekannt ist. Ausserdem sind Polyamide zu nennen, die ganz oder teilweise aus Lactamen mit 7-12 C-Atomen, gegebenenfalls unter Mitverwendung einer oder mehrerer der oben genannten Ausgangskomponenten, hergestellt werden. Besonders bevorzugte teilkristalline Polyamide sind Polyamid-6 und Polyamid-6,6. Die Polyamide sollen vorzugsweise eine relativen Viskosität (gemessen an einer 1 Gew.-%igen Lösung in m Kresol bei 25"C) von 2,0 -5,0, besonders bevorzugt von 2,5-4,5 aufweisen. Für die Herstellung der Pfropfprodukte werden als Pfropfgrundlage vernetzte Dienkautschuke aus Polybutadien und/oder Polyisopren, die bis zu 40 Gew.-% Styrol und/oder Acrylnitril als Co-Monomere enthalten können, verwendet. Der Gelanteil des als Pfropfgrundlage verwendeten' Polymeren sollte > 70 Gew.-%, vorzugsweise 80 Gew.-% (gemessen in Toluol) sein. Die bevorzugte Pfropfgrundlage besteht aus vernetztem Polybutadien. Pfropfmonomere im Sinne der Erfindung sind Acrylnitril, Styrol, Methacrylnitril, aliphatische Ester der Acrylsäure und Methacrylsäure mit bis zu 22 C-Atomen. Bevorzugte Pfropfmonomere sind Ester der Acrylsäure und Methacrylsäure. Von den Estern der Acrylsäure bzw. Methacrylsäure sind der Methyl-, der Ethyl-, der n-Butyl-, der tert.-Butyl-, der Octyl- und der Ethylhexylester besonders bevorzugt. Die erfindungsgemässen Pfropfprodukte können nach allen bekannten Polymerisationsverfahren (Emul sions-, Lösungs-, Masse-, Suspensions-, Fällungspolymerisation), sowie nach Kombinationen aus diesen Verfahren hergestellt werden. Zur Herstellung der Pfropfprodukte wird das aufzupfropfende Monomere in Gegenwart der vorgebildeten Pfropfgrundlage polymerisiert. Es bildet sich dabei neben dem eigentlichen Pfropfpolymerisat auch freies Homopolymerisat. Unter Pfropfprodukte wird die Summe der eigentlichen Pfropfcopolymerisate und der freien Polymerisate verstanden. Die Menge des aufgepfropften Monomeren und sein Molekulargewicht kann in weiten Grenzen durch Variation der Polymerisationsbedingungen beeinflusst werden. Hierzu gehören vor allem: Art des Polymerisationsverfahrens, Temperatur, Kativatorsystem, Molekulargewichtsregler, Rührbedingungen und Art der Monomer tösierung. Erfindungsgemäss sollte die Pfropfausbeute G in0,15, vorzugsweise G > ,,,,0,40 beträgen. Die Pfropfausbeute G bezeichnet das Plengenverhältnis von aufge pfropftem Monomer zur Gesamtmenge der Monomeren in der Pfropfauflage und ist dimensionslos. Bevorzugtes Polymerisationsverfahren für die erfindungsgemässen Pfropfpolymeren ist die Emulsionspolymerisation. Für die Herstellung der Pfropfprodukte durch Emulsionspolymerisation werden vernetzte, vorzugsweise durch Emulsionspolymerisation gewonnene Butadienpolymerisate als Pfropfgrundlagen bevorzugt. Erfindungsgemäss werden bevorzugt solche Pfropfprodukte, die einen "mittleren Teilchendurchmesser" d50 von 0,2-0,6 pm, vorzugsweise 0,3-0,5 pm, insbesondere ca. 0,4 pm aufweisen verwendet. (Zur Bestimmung vgl. W. Scholtan und H. Lange, Kolloid-Z. und Z. Polymere 250 (1972) 782-796 bzw. G. Kämpf, H. Schuster, Angew. Makromolekulare Chemie 14 (1970), S. 111-129J. Statt nur einer Pfropfgrundlage können auch Abmischungen verschiedener Pfropfgrundlagen zur Herstellung der Pfropfprodukte eingesetzt werden. Weiterhin können statt nur eines Pfropfproduktes auch Abmischungen mehrerer erfindungsgemässer Pfropfprodukte mit unterschiedlichem Aufbau zur Abmischung mit den Polyamiden herangezogen werden. Zur Herstellung der erfindungsgemässen Formmassen werden ganz besonders bevorzugt Pfropfprodukte hergestellt aus a) 70-95 Gew.-%, vorzugsweise 75-90 Gew.-% eines vernetzten Polymerisates aus Butadien und/oder substituiertem Butadien, das zumindest aus 95 Gew.-% gegebenenfalls substituierten Butadien-Einheiten aufgebaut ist, als Pfropfgrundlage und b) 5-30 Gew.-%, vorzugsweise 10-25 Gew.-% von Methyl methacrylat als aufzupfropfendes Monomeres, wobei der Gelanteil der Pfropfgrundlage > 70 %, vorzugs weise > 80 Gew.-%, in Toluol gemessen, die Pfropf- ausbeute G a 0,15, vorzugsweise 3 0,40 und der mittlere Teilchendurchmesser des Pfropfcopolymeri sats 0,2 - 0,6, vorzugsweise 0,3 - 0,5, insbe sondere ca. 0,4 pm betragen soll, verwendet. Als Weichmacher sind die für Polyamide üblichen, bekannten, vorzugsweise niedermolekulare Verbindungen geeignet. Insbesondere -sind dies alle Substanzen, die in der Lage sind, die Einfriertemperatur der Polyamide abzusenken, ohne die chemische Natur der Polyamid Makromoleküle zu verändern. Hierzu gehören folgende Substanzklassen bzw. Substanzen: Aromatische Hydroxyverbindungen, wie z.B.: p-Oxybenzoesäure-2-ethylhexylester, Dioxybenzoesäureester, Phenole, aromatische Hydroxyaldehyde; aromatische Sulfonamide., wie z.B.: Benzolsulfonsäure-N-monomethylamid, Benzolsulfonsäure N-butylamid, Toluolsulfonsäureamid, Toluolsulfonsäureethylamid, N-Cyclohexyl-p-toluolsulfonamid; Phthalsäureester, wie z.B.: Di-isopropylphthalat, Di-tert.butylphthalat, Di-2-ethylhexylphthalat, Di-isononylphthalat, Di-isononyl-poly-tri-ethylenglykol-phtha- lat; Lactame, wie z.B. 1 -Caprolactam, Laurinlactam; Lactone, Umsetzungsprodukte aus Hydroxycarbonsäuren und Alkylenoxyden, Acrylcyclohexanol, Abietylalkohol, Tetrahydrofurfuryalkohol-Carbonsäureester, Pentantriol und seine Ester. Geeignete Weichmacher im Sinne der Erfindung sind auch Alkylsulfonsäureester, die aus Alkylsulfochloriden, die 1-4, vorzugsweise 1-2, über die Kohlenwasserstoffkette statistisch oder regelmässig verteilte -SO2-Cl-Gruppen enthalten, und Phenolen hergestellt werden. Geeignete Phenole sind Monophenole, wie z.B. Phenyl-, Diphenyl- und Naphthyl-Derivate sowie Bisphenole wie Hydrochinon, Resorcin, Dihydroxydiphenyl, Bis(hydroxyphenyl)-alkane, Bis(hydroxyphenyl)-cycloalkane, Bis(hydroxyphenyl)-sulfide, Bis(hydroxyphenyl)-ether, Bis (hydroxyphenyl)-sulforide, Bis-(hydroxyphenyl)-sulfon. Beispiele für geeignete Sulfonsäureester sind (C12-C18)-Alkylsulfonsäure-p-phenylester (C12-C18) -Alkyldi (sulfonsäure-p-phenylester) (C12-C18) -Alkylsulfonsäure-p-phenyl-octyl-ester (C12-C18) -Alkylsulfonsäure-p-hydroxybenzoesäure-iso- butylester 2,2-Bis(C12-C18) -alkylsulfonsäure-4-phenylester) propan 2,2-Bis- ( (c12-C18) -alkylsulfonsäure-3,5-dichlor-4- phenylester)propan. Den erfindungsgemässen Formmassen werden als Weichmacher bevorzugt aromatische Sulfonamide und Lactame zugesetzt. Die Herstellung der erfindungsgemässen Polyamid-Formmassen kann in den üblichen Mischaggregaten wie Walzen, Kneter-, Ein- und Mehrwellenextruder bei üblichen Bedingungen erfolgen. Besonders geeignet sind Doppelwellenextruder. Die Formmassen können auf den genannten Mischaggregaten hergestellt werden, indem die drei Komponenten I, II und III gemeinsam aufgeschmolzen und homogenisiert werden oder indem das Pfropfprodukt II in die Schmelze des Weichmacher (III)-haltigen Polyamids I oder indem die Weichmacher III in die aufgeschmolzene Mischung aus Polyamid I und Pfropfprodukt II eingearbeitet wird. Die erfindungsgemässen Formmassen können übliche Additive, wie Gleit- und Entformungsmittel, Nucleierungsmittel, Stabilisatoren, Flammschutzmittel sowie Farbstoffe, enthalten. Die Zusatzstoffe werden vorzugsweise bei der Compoundierung in reiner Form oder als Konzentrate zugesetzt. Die erfindungsgemässen Formmassen eignen sich aufgrund ihrer hervorragenden elastischen Eigenschaften besonders zur Herstellung von Schuhsohlen, Dichtungen oder Schläuchen. Beispiele Herstellung des Pfropfproduktes In einem druckfesten Rührgefäss wird eine Lösung aus 80 Gew.-Teilen salzfreiem Wasser, 1,5 Gew.-Teilen Natriumsalz der disproportionierten Abietinsäure und 0,3 Gew.-Teilen Kaliumperoxidisulfat vorgelegt. Nach Verdrängen der Luft durch Stickstoff und Einstellung der Innentemperatur auf 550C werden 0,35 Gew.-Teile Dodecylmercaptan und X Gew.-Teile Butadien zugesetzt und polymerisiert. Mit absinkender Reaktionsgeschwindigkeit bei fortschreitender Polymerisation wird die Temperatur langsam auf 680C angehoben. Nach beendeter Polymerisation werden geringe Mengen des nicht umgesetzten Butadiens durch Ausrühren des erhaltenen Latex unter vermindertem Druck entfernt. 175 Gew.-Teile entsalztes Wasser und 0,3 Gew.-Teile Kal iumperoxidsul fat werden zugesetzt Nach Verdrängen der Luft durch Stickstoff und Erwärmen auf 650C werden 2 Gew.-Tle. Emulgator (Na-Salz der disproportionierten Abietinsäure oder Alkylsulfonate), gelöst in 25 Gew.-Teilen Wasser sowie Y Gew.-Teile der in Tabelle 1 angegebenen Monomeren zugesetzt. Die Zulaufdauer beträgt ca. 4 Stunden. Zur Vervollständigung der Reaktion wird nach beendetem Zulauf noch 2 Stunden bei 650C weiter'gerührt. Der so erhaltene Pfropfprodukt-Latex wird nach Zusatz von 1 Gew.-Teil eines phenolischen Antioxidans (2,6 Di-tert.-butyl-p-kresol) mit 2 %iger MgSO4/Essigsäure- Lösung (Mischungsverhältnis 1:1 Gew.-Teile) koaguliert, das Koagulat abgetrennt, salzfrei gewaschen und bei 700C im Vakuum getrocknet. Die Zusammensetzung der Pfropfprodukte ist der Tabelle 1 zu entnehmen. Tabelle 1: Zusammensetzung der Pfropfprodukte Typ @ Gew.-Teile Buta- @ Ges.-Teile Pfropf- mittlerer Teilchendien monomeres durchmesser um A 80 20 n-BA/t-BA 0,4 (8:2) B 80 20 S/AN 0,4 (72/28) C 80 20 MMA 0,4 D 60 40 MMA 0,4 n-BA = n-Butylacrylat t-BA = tert.-Butylacrylat S = Styrol AN = Acrylnitril MMA = Methylmethacrylat Beispiele 1 - 19 Herstellung der Formmassen Die Einarbeitung der Pfropfprodukte A bis D in Polyamid erfolgt in einem handelsüblichen, kontinuierlich arbeitenden Doppelwellenextruder ZSK 32 der Fa. Werner & BR< Pfleiderer, in der das Polyamid bei Temperaturen von 270-2900C aufgeschmolzen wurde. Durch einen zweiten Einfüllstutzen wurde das Pfropfprodukt in die Polyamid-Schmelze eindosiert. Stickstoffbeschleierung ist zweckmässig. Das Pfropfprodukt verteilt sich homogen im aufgeschmolzenen Polyamid. Über eine gesonderte Zuleitung wurde der Weichmacher mit Hilfe einer Dosierpumpe in die homogenisierte Schmelze von Polyamid und Pfropfpolymerisat eindosiert. Es kann vorteilhaft sein, die Schmelze vor dem Austritt aus der Düse zu entgasen. Die Zylindertemperaturen wurden so eingestellt, dass eine Massetemperatur von 270-2900C gewährleistet war. Der Schmelzestrang der Mischung aus Polyamid, Pfropfprodukt und Weichmacher wurde in Wasser abgekühlt, granuliert und getrocknet. An diesem Granulat wurde die Weichermacher-Migration durch Gewichtsverluste nach Wasserlagerung (24 h bei 600C) ermittelt. Die entsprechenden Werte sind der Tabelle 3 zu entnehmen. Vom Granulat wurden ausserdem auf einer üblichen Spritzgussmaschine bei 2600C Normkleinstäbe (nach DIN 53 453), Flachstäbe (nach DIN 53 453) und Zugstäbe (nach DIN 53 455) verspritzt. Geprüft wurde an den Normkleinstäben die Kerbschlag zähigkeit bei 250C (nach DIN 53 453), an den Flachstäben die Wechselknickfestigkeit (in Anlehnung an DIN 53 359) und an den Zugstäben die relative reversible Dehnung (nach DIN 53 455). Die Zusammensetzung und die Eigenschaften der Formmassen sind der Tabelle 2 zu entnehmen. Tabelle 2 Bei- Pfropfprodukt polyamid Weichmacher rel. rev. Wechselknick- Kerbschlagzäspiel Typ Gew.-% Typ 1) Gew.-% Typ Gew.-% Dehnung festigkeit higkeit #rel (Zahl der (23 C,kJ/m2) Hübe 1 A 30 PA-6 3,95 60 I 10 26 42.000 42 2 B 30 PA-6 3,95 60 I 10 25 35.000 23 3 C 30 PA-6 3,95 60 I 10 35 62.000 48 4 D 30 PA-6 3,95 60 I 10 32 48.000 26 5*) A 40 PA-6 3,95 60 - 0 18 7.000 47 6*) B 40 PA-6 3,95 60 - 0 17 4.000 25 7*) C 40 PA-6 3,95 60 - 0 20 8.000 53 8*) D 40 PA-6 3,95 60 - 0 19 7.500 28 9 C 10 PA-6 3,95 80 I 10 23 36.000 29 10*) C 20 PA-6 3,95 80 - 0 16 3,500 51 11*) C 10 PA-6 3,95 90 - 0 15 2.000 9 12 C 40 PA-6 3,95 50 I 10 41 95.000 43 13*) C 50 PA-6 3,95 50 - 0 22 8.000 47 14 C 30 PA-6 3,95 60 II 10 36 76.000 49 15 C 20 PA-66 3,05 62,5 I 12,5 33 53.000 36 16*) C 32,5 PA-66 3,05 67,5 - 0 15 2.500 41 1) gemessen in m-Kresol bei 23 C I = Benzolsulfonsäure-N-monomethylamid *) Vergleichsbeispiel II = Benzolsulfonsäure-N-butylamid Tabelle 3: Versuche zur Weichmacher-Migration Beispiel Pfropfprodukt Polyamid Weichmacher migrierter Weichmacheranteil Typ Gew.-% Typ #rel Gew.-% Typ Gew.-% nach 5 nach 10 Tagen/Gew.-% Tagen/Gew.-% 17*) - - PA-6 3,95 90 I 10 2,8 3,1 18*) - - PA-6 3,95 90 II 10 1,6 1,9 12 C 40 PA-6 3,95 50 I 10 1,6 1,95 13 C 30 PA-6 3,95 60 I 10 1,8 2,1 19 C 40 PA-6 3,95 50 II 10 0,57 0,95

Claims: Patentansprüche 1) Thermoplastische Formmassen aus I) 30-94 Gew.-% wenigstens eines Polyamids II) 70-3 Gew.-% eines Pfropfproduktes, herge stellt aus a) 50-95 Gew:-% eines vernetzten Polymeri sats aus Butadien und/oder subst. Butadien, das gegebenenfalls bis zu 40 Gew.-% aus Styrol und/oder Acrylnitril aufgebaut sein kann, als Pfropfgrund- lage und b) 5-50 Gew.-% von Pfropfmonomeren aus &alpha;) 3-100 Gew.-% eines Esters der (Meth)- Acrylsäure, ss) ) 0-80 Gew.-% Styrol und #) 0'-80 Gew.-% (Meth)acrylnitril, wobei der Gelanteil der Pfropfgrundlage #70 % in Toluol gemessen, die Pfropfausbeute 7,0,15 und der mittlere Teilchendurchmesser des Pfropfcopolymerisats 7/0,1 am betragen soll, III) 20-3 Gew.-% eines für Polyamid üblichen Weichmachers und gegebenenfalls IV) weitere übliche Hilfs- und Zuschlagsstoffe, wobei die Summe I. - IV. bzw. a) und b) bzw. - - ?) jeweils 100 Gew.-% ergeben muss. 2) Formmassen nach Anspruch 1, enthaltend 50 - 90 Gew.-% der Komponente I, 50 - 5 Gew.-t der Kompo nente II und 15 - 5 Gew.-% der Komponente III. 3) Formmassen nach Anspruch 1 oder 2, dadurch gekenn zeichnet, dass die Komponente II aus 70 - 90 Gew.-% der Komponente a) und 30 - 10 Gew.-% der Komponen te.b) hergestellt wurde. 4) Formmassen nach Ansprüchen 1 - 3, dadurch gekenn zeichnet, dass die Komponente a) ein vernetztes Polybutadien ist und die Komponente b) aus dem Ple- thyl-, n-Butyl-, tert.-Butyl-, Octyl oder Ethyl hexylester der (Meth)acrylsäure aufgebaut ist. 4) Formmassen nach Ansprüchen 1 - 4, dadurch gekenn zeichnet, dass als Weichmacher aromatische Hydroxy verbindungen, aromatische Sulfonamide, Phthalsäu reester, Lactame, Lactone oder Sulfonsäureester verwendet werden. 6) Formkörper hergestellt aus Formmassen nach Ansprv- chen 1 - 5.

Inventors: BINSACK, RUDOLF, DR., FAHNLER, FRIEDRICH, GRIGO, ULRICH, DR., LINDNER, CHRISTIAN, DR., MORBITZER, LEO, DR.
Applicants: BAYER AG
Application year: 1982
Main classification: C08L77
IPC codes: C08L51, C08L7, C08L21, C08L77