RESINS AND THEIR USE IN COATING COMPOSITIONS

Abstract: The invention provides resins suitable for solvent-based varnishes containing nitrocellulose, which resins are the reaction product of 1.5-2.5, preferably 1.75-2.25 moles of dicyclopentadiene per mole of alpha-beta unsaturated dicarboxylic acid, which resin has an average molecular weight of 600-900, an acid value of 70-100, a saponification index of 250-300, a bromine index of 60-100 and a softening point of 100-160°C. The resins are prepared by initial reacting at 100 to 140°C and subsequently at 175 to 250°C. Preferably a mineral acid catalyst is used.

Description: RESINS AND THEIR USE IN COATING COMPOSITIONS This invention relates to resins, more particularly to resinous reaction products of dicyclopentadiene and an alpha-beta unsaturated dicarboxylic acid and their use in coating compositions. It is widely known that dicyclopentadiene (DCPD) reacts with the anhydride of an alpha-beta unsaturated dicarboxylic acid like maleic anhydride to form resinous reaction products. This reaction is sometimes carried out at temperatures above 1700C (i.e. the temperature above which dicyclopentadiene dedimerizes) and sometimes below 1700C. US-A-3 890 285 (= NL-A-7314422) Nippon Oil, describes such a reaction being carried out at 2700C, resulting in products with an acid value of about 200. Free radical initiators are sometimes used. The reaction is usually of the Diels-Alder type.The resins obtained contain cyclopentadiene and anhydride groups. Such products are, inter alia, disclosed in US-A-3 188 303, J.J. Dissen, and these products also must show a high acid value. The reaction of a dicyclopentadiene and an alpha-beta unsaturated dicarboxylic acid is less known. Such a reaction product is mentioned in US Patent Specification 2 442 992, however without giving details. This reaction may lead to the formation of ester-type addition products in which one or two dicyclopentadiene molecules are attached to the dicarboxylic acid by means of ester groups. It has now been found that certain resinous reaction products of a dicyclopentadiene and an alpha-beta unsaturated dicarboxylic acid are novel and valuable compounds which are useful in coating compositions, more in particular in varnishes of the nitrocellulose type. These resins are substantially the reaction product of 1.5-2.5 moles of a dicyclopentadiene per mole of alphabeta unsaturated dicarboxylic acid, which resin has an average molecular weight of 600-900, an acid value of 70-100, a saponification value of 250-300, a bromine value of 60-100 and a softening point of 100-160 C. The molecular weight is determined by cryoscopy, the acid value according to ASTM Cd 3a-63, the saponification value according to ASTM Cd-3-25, the bromine value according to ASTM D 1491-78 and the softening point by Ring & Ball according to ASTM-E28-67. A dicyclopentadiene comprises methyldicyclopentadienes and (unsubstituted) dicyclopentadiene. An alpha-beta unsaturated dicarboxylic acid comprises any C4-C10 alpha-beta unsaturated dicarboxylic acid, such as maleic acid, fumaric acid, citraconic acid and the like. In particular the cis-isomers are preferred. There is no necessity to use the free acid itself as the starting material for the reaction, because it may well be more convenient to form the free acid in situ, e.g. from its anhydride and the appropriate amount of water. The reactants may be used in the pure form but also as technical grades containing 60-95% of the pure chemical, in particular with dicyclopentadiene. Preferably 1.75 to 2.25 moles of a dicyclopentadiene are used per mole of alpha-beta unsaturated dicarboxylic acid. A convenient process for preparing this resinous reaction product is by reacting the appropriate molar amounts of a dicyclopentadiene and alpha-beta unsaturated dicarboxylic acid, optionally in the presence of a small amount of acid catalyst at a temperature of 100-140"C, preferably 115-130"C, so as to form ester-type reaction products, followed by increasing the reaction temperature to 1750-2500C so as to obtain cyclopentadiene by cracking of dicyclopentadiene, followed by Diels-Alder addition of cyclopentadiene and dicyclopentadiene to the unsaturated esters formed in the first phase of the reaction. Although various substituted dicyclopentadienes can be used in this reaction, it is preferred to use unsubstituted dicyclopentadiene having a purity of at least 85%, preferably at least 90%. Although it is advantageous to use a minor amount of acid catalyst, say 0.5-5 o/oo of the total charge, this is not a requirement, unless the dicarboxylic acid is extremely weak. Various acid catalysts can be used but mineral acid, in particular phosphoric acid, is preferred. The progress of the reaction can be conveniently followed by means of taking samples and establishing the softening point. At the end of the reaction volatiles were stripped off. The intermediate ester mixture is normally a yellow oil and the reaction product a brittle yellow resin with characteristics set out above. The resin has a polar character and can be used in adhesives, printing inks and the like, depending on its softening point, which in turn is determined by the progress of the second reaction step (Diels-Alder) and the amount of excess (di)cyclopentadiene available. The resin can be used with advantage in coating compositions, in particular varnishes of the nitrocellulose type, where it imparts valuable properties, in particular hardness. Also it is a valuable extender of alkyds and a substitute for natural resins. In coating compositions such as varnishes 5-25% of the total composition, i.e. up to about 50% of the total solids content, may consist of the DCPD-dicarboxylic acid adduct. The remainder of the varnish is usually made up of nitrocellulose, alkyds and various organic solvents and sometimes other adjuncts. The invention is illustrated by the following example. EXAMPLE 1 Into a 2-litre round-bottomed flask equipped with a thermometer, a stirring device and a reflux condenser, two moles of dicyclopentadiene (abt. 92% purity), 1 mole of maleic anhydride and water in an amount just sufficient for the formation of the free dicarboxylic acid and 1 o/oo by weight of phosphoric acid were introduced. The reaction mixture was heated to a temperature of 120 125"C with stirring and maintained at said temperature for 4 hours, which resulted in the formation of a mixture of ester and diester. This ester mixture was a yellowish oil. Subsequently the reaction temperature was slowly raised to 1750C, with continuous stirring, which temperature was maintained for 3 hours. By increasing the temperature, the excess of free dicyclopentadiene was cracked to form cyclopentadiene, which then combined according to a Diels-Alder reaction with ester and diester which had been formed previously. The progress of this reaction was followed by regularly determining the softening point (Ring and Ball ASTM D 1491-78) after removal of the non-reactive products by distillation and the reaction was stopped at a softening point of 70-125"C, in this particular case at 1200C, at which point the hard yellow resin had a Gardner colour of 11, an average molecular weight of about 700 (cryoscopic), a saponification value of 290 and a bromine value of 90. In case technical grade DCPD of about 70% purity was used, a similar resin was obtained, however with a slightly lower softening point. The resin based on 92% pure DCPD was used in the following nitrocellulose varnish composition: 26.3 parts by weight of nitrocellulose (relative vis cosity of 1/4 second according to the Hercules method in a 40% solvent mixture of ethanol, toluene and ethyl acetate) 26.3 " " " " butyl acetate 12.5 " " " " ethyl acetate 12.5 " " " " air-drying alkyd (60t in butyl acetate) 13.5 " " " " dicyclopentadiene/maleic acid resin (above) 2.5 " " " " butanol 6.4 " " " " methyl isobutyl ketone. This nitrocellulose varnish was quick-drying, in 45 minutes dust-free and in 60 minutes fingerpint-dry, and the hardness (Persoz) was quite satisfactory, viz.: 31 seconds after 2 hours 1 min. 28 seconds after 7 hours 2 min. 20 seconds after 24 hours 3 min. 10 seconds after 48 hours.

Claims: CLAIMS 1. The resinous reaction product of 1.5-2.5 moles of a dicyclopentadiene per mole of alpha-beta unsaturated dicarboxylic acid, which resin has an average molecular weight of 600-900, an acid value of 70-100, a saponification index of 250-300, a bromine index of 60-100 and-a softening point of 100-1600C. - 2. The resinous reaction product according to claim 1 in which 1.75-2.25 moles of a dicyclopentadiene are used per mole of alpha-beta unsaturated dicarboxylic acid. 3. A process for preparing a resinous reaction product according to claim 1 or 2, consisting of reacting dicyclopentadiene and alpha-beta unsaturated di -cmrMcXw id73ftriattymrntTp- tmmbst amount of acid catalyst, at a temperature of 100-140"C, preferably 115-130"C, so as to form ester-type addition products, followed by increasing the reaction temperature to 175-2500C so as to obtain a cyclopentadiene by cracking of dicyclopentadiene, followed by Diels-Alder addition of cyclopentadiene and dicyclopentadiene to the unsaturated esters formed in the first phase. 4. A process according to claim 3, in which unsubstituted dicyclopentadiene is used. 5. A process according to claim 3 or 4, in which the acid catalyst is a mineral acid. 6. A process according to claim 3 or 4, in which the alpha-beta unsaturated acid is maleic acid. 7. A solvent-based varnish comprising nitrocellu- lose, a solvent and a resin as defined in claim 1 or 2.

Inventors: BILLAULT, GEORGES, HANSLIN, ROBERT AENIS, RUNAVOT, YVES, SALVETAT, JACQUES
Applicants: DSM RESINS BV
Application year: 1982
Main classification: C08F2
IPC codes: C09D101, C08F2