PREPARATION OF SOLUBLE MOLYBDENUM CATALYSTS FOR EPOXIDATION OF OLEFINS

Abstract: The process of regenerating soluble molybdenum catalyst for epoxidation of olefins with a hydroperoxide which comprises thermally precipitating and separating a molybdenum-containing solid obtained from a spent catalyst stream derived from a molybdenum catalyzed olefin epox­ idation, and solubilizing the precipitation solid by heating with a liquid hydroxyl-containing organic compound to produce an active catalyst solution.

Description: PREPARATION OF SOLUBLE MOLYBDENUM CATALYSTS FOR EPOXIDATION OF OLEFINS Oxirane compounds such as ethylene oxide, propylene oxide, and their higher homologs are valuable articles of commerce. One of the most attractive processes for synthesis of those oxirane compounds is described by Kollar in United States Patent No. 3,351,635. According to Kollar, the oxirane compound (e.g., propylene oxide) may be prepared by epoxidation of an olefinically unsaturated compound (e.g., propylene) by use of an organic hydroperoxide and a suitable catalyst such as molybdenum. During the epoxidation reaction the hydroperoxide is converted almost quantitatively to the corresponding alcohol. That alcohol may be recovered as a coproduct with the oxirane compound. However, it is the oxirane which is of primary concern. Kollar teaches that oxirane compounds may be prepared from a wide variety of olefins. Lower olefins having three or four carbon atoms in an aliphatic chain are advantageously epoxidized by the process. The class of olefins commonly termed alpha olefins or primary olefins are epoxidized in a particularly efficient manner by the process. It is known to those in the art that primary olefins, e.g., propylene, butene-l, decene-1 hexadecene-1 etc., are much more difficulty expoxidized than other forms of olefins, excluding only ethylene. Other forms of olefins which are much more easily epoxidized are substituted olefins, alkenes with internal unsaturation, cycloalkenes and the like. Kollar teaches that notwithstanding the relative difficulty in epoxidizing primary olefins, epoxidation proceeds more efficiently when molybdenum, titanium or tungsten catalysts are used. Molybdenum is of special interest. Kollar teaches that activity of those metals for epoxidation of primary olefins is surprisingly high and can lead to high selectivity of propylene to propylene oxide. These high selectivities are obtained at high conversions of hydroperoxide (50% or higher) which conversion levels are important for commercial utilization of the technology. Kollar's epoxidation reaction proceeds under pressure in the liquid state and, accordingly, a liquid solution of the metal catalyst is preferred. Preparation of a suitable catalyst is taught by Sheng et al in United States Patent No. 3,434,975. According to Sheng, the reaction-medium soluble epoxidation catalyst may be prepared by reacting molybdenum metal with an organic hydroperoxide, peracid or hydrogen peroxide in the presence of a saturated alcohol having one to four carbon atoms. Another molybdenum epoxidation catalyst is described by Bonetti et al in United States Patent No. 3,480,563. Bonetti teaches that molybdenum trioxide may be reacted with a primary saturated acyclic alcohol have II to 22 carbon atoms or with a mono- or polyalkylene glycol monoalkyl ether. The reaction involves heating the molybdenum trioxide in the alcohol or ether to produce an organic soluble molybdenum catalyst. Maurin et al in United States Patent No. 3,822,321 describes oxidizing olefins with a hydroperoxide using a molybdenum catalyst prepared by reacting a molybdenum compound such as molybdic acid or a molybdic salt with a polyalcohol. A molybdenum catalyzed epoxidation of olefins is described by Lines et al in United States Patent No. 4,157,346. The catalyst is prepared by reacting an oxygen containing molybdenum compound with an amine (or an amine N-oxide) and alkylene glycol. In United States Patent No. 3,887,361 Lemke discloses that spent catalyst solutions obtained from the process of epoxidation of olefins with hydroperoxides in the presence of molybdenum may be treated to precipitate and separate dissolved molybdenum. The Lemke process involves mixing spent catalyst solution with 5 to 50 parts by weight of tertiary-butyl alcohol 0 and heating the mixture to 100 to 300 C in a closed vessel or under reflux. That procedure results in precipitation of molybdenum as a finely divided solid. The solid is disclosed to use suitable for recycle as such into further epoxidation reactions. Also, the solid may be dissolved in organic acids for use in the 1,Oxo process" for production of oxygenated organic derivatives. The Lemke solids typically contain about 30 to 40% by weight of molybdenum. It has now been discovered that spent soluble molybdenum catalyst can be effectively regenerated and reused in the epoxidation of olefins. The method of regenerating soluble molybdenum catalyst for epoxidation of olefins with a hydroperoxide comprises thermally precipitating and separating a molybdenum-containing solid from a spent catalyst solution obtained from a molybdenum catalyzed olefin epoxidation and solubilizing the precipitated solid in a hydroxyl-containing liquid organic compound by heating the solid with such compound to produce an active catalyst solution. The present discovery makes it possible to continuously regenerate, recycle and reuse molybdenum catalyst in a continuous process for molybdenum catalyzed epoxidation of olefins with a hydroperoxide by thermally precipitating and separating a molybdenum-containing solid from a spent catalyst solution obtained from a molybdenum catalyzed olefin epoxidation and solubilizing the precipitated solid in a hydroxyl-containing organic compound by heating the solid with such compound to product an active catalyst solution, and adding a catalytic amount of the active solution to a hydroperoxide epoxidation of an olefin. As used in the present specification and the annexed claims, the term "spent catalyst solution" is intended to mean that fraction of the epoxidation reaction product effluent remaining after removal of unreacted olefin (for example, propylene), alkylene oxide (for example, propylene oxide) and a major portion of the alcohol corresponding to the hydroperoxide (for example, tertiary butyl hydroperoxide) used in the epoxidation reaction which reaction may be according to the procedure of Kollar, the teachings of which are hereby incorporated by reference in their entirety. Spent catalyst solution, apart from molybdenum compounds, contains some alcohol, acids and other low molecular weight oxygenated compounds and said spent catalyst solution is generally not subjected to any chemical treatment before being subjected to the process of the present invention. It is contemplated that spent catalyst solution as used herein includes both the distillation bottoms treated in British Patent Specification 1,317,480 and the residue obtained from the wiped film evaporation process according to Levine U.S. Patent 3,819,663, the disclosures of which are also hereby incorporated by reference, and said spent catalyst solution can contain molybdenum at levels of up to about 5% by weight. Solid precipitates of molybdenum-containing compounds are obtained from spent catalyst solutions by a variety of methods. The present invention relates to a process for dissolving those solids to produce an active soluble epoxidation catalyst for use in processes such as those taught by Kollar. Accordingly, this invention avoids the necessity of disposal of spent molybdenum catalyst solutions which is detrimental from both economic and ecological view points. These and other objects of the invention will become apparent from the following description and examples. The molybdenum catalyzed hydroperoxide epoxidation crude reaction product from processes such as Kollar, discussed above, can be purified by distillation off epoxide and alcohol corresponding to the hydroperoxide. The remaining residue contains high boiling by-products and dissolved molybdenum catalyst. If the residue is recycled directly into further epoxidations, the yield of epoxide is adversely effected. Accordingly, to reuse the molybdenum it must be separated from the polymeric by-products and regenerated. To achieve separation of the molybdenum from the distillation residue, thermal precipitation according to the teachings of Lemke, noted above is efficient. Also, separation may be achieved by the thermal precipitation procedure disclosed and claimed in my copending application entitled 1,Production of a Solid Molybdenum Precipitate from a Spent Molybdenum Epoxidation Catalyst Solution" (internal docket No.- 80-PD-19/80-PD-7) filed concurrently herewith. In general, thermal precipitation of molybdenum-containing solid involves heating the residue with dissolved molybdenum in the presence of teriary butyl alcohol or water to precipitate a solid. The solid precipitate typically contains about 30-408 molybdenum, by weight. Reuse of molybdenum in the solid precipiate requires an efficient method to solubilize the molybdenum 90 that a high quality epoxidation can be obtained. An active catalyst solution can be obtained by heating and solubilizing the solid thermal precipitate in the presence of a hydroxyl-containing organic compound. In contrast with prior art catalyst preparations, the presence of an oxidizing agent (such as a peroxide) is not necessary. However, the presence of such agent is optional for solubilizing the solid in such hydroxyl-containing organic compound. Suitable hydroxyl-containing organic compounds for use in preparing a catalyst solution from thermally precipitated molybdenum solids include aliphatic and aromatic alcohols and polyhydroxy compounds such as glycols and alkylene ethers thereof. Although such compounds may be substituted with functional groups which are inert to the reactants present, e.g. halo such as chloro or fluoro; nitro; cyano; carbonyl; and carboxyl, the readily available aliphatic and aromatic hydroxylcontaining organic compounds containing up to about 12 carbon atoms are particularly satisfactory for use in the present invention. Illustrative suitable monohydroxy compounds are methanol, ethanol, tertiary butyl alcohol, phenol and benzyl alcohol. Polyhydroxy compounds also containing up to about 12 carbon atoms, such as glycols and derivatives thereof, such as glycol ethers, are also eminently suitable for practice in the process of the present invention, provided these compounds contain at least one hydroxl group; typical illustrative polyhydroxy compounds include ethylene glycol, propylene glycol, 1,4-butanediol, catechol and alkylene ethers of such glycols, including the methyl and ethyl ethers thereof. The temperature employed to solubilize precipitated molybdenum solids may be in the range of 200C to 1300C. Temperatures lower than 200C necessitate unduly long reactives and are not favored. A particularly convenient temperature is the reflux temperature of the liquid into which solids are being solubilized. Atmospheric pressure for the solubilization reaction is convenient and effective or when the reaction is carried out at higher temperatures which would cause volatilization of the alcohol, sufficient pressure may be utilized to maintain the liquid phase. For example, if methanol is the solubilizing alcohol, use of temperatures higher than about 63 0C require that superatmospheric pressure be used to maintain the liquid state. The time required to solubilize precipitated solids is a function of both temperature and alcohol/glycol species chosen. Generally, solubilization requires from 0.5 to 4 hours. Solubilization has also been observed to be somewhat dependent on the ratio of precipitated solids to solubilizing liquid. Although molybdenum concentrations of up to 5% by weight have been found to be capable of being solubilized by the process of the present invention, preferred amount of solids to be solubilized contain up to about 2 parts, by weight, per 100 parts by weight of solubilizing liquid. As higher levels of solids are present, the stability of the solution obtained is adversely effected. Thus stability of solubilized molybdenum depends on both concentration as well as temperature. The solubilising liquid may be a monohydroxy containing compound, i.e. an alcohol, a polyhydroxy containing compound, e.g, a glycol, or a mixturee thereof. It has been surprisingly found that a mixture of alcohol and glycol has a synergistic effect on solubilizing precipitated solids in the presence of an oxidizing agent to produce a regenerated catalyst. Glycol added to alcohol appears to have the effect of stabilizing the molybdenum in solution and prevents reprecipitation. When propylene glycol is used, a minimum of 2 moles of glycol per mole of solubilized molybdenum is generally used. The molar ratio suggests that the stabilizing effect is achieved by complexing the soluble molybdenum with glycols, which bind to more than one metal site, to produce more stable complexes than those formed by monohydroxy compounds. See Basolo & Pearson, "Mechanisms of Inorganic Reactions," John Wiley & Sons, Inc. (1968) pages 223 et seq. Accordingly, when polyhydroxy glycols are reacted, somewhat less than two moles of glycol per mole of solubilized molybdenum may be effective because of the higher hydroxyl number. Also, solubilization can be effected in pure glycol (i.e., a large excess). However, large excesses of glycol should not be added to subsequent epoxidations and hence are not favored for molybdenum solubilization. While additional solubilizing agents other than the hydroxyl- containing organic compound are not required, an optional compound of the solubilizing liquid may be an oxidizing agent such as hydrogenperoxide; organic peroxides such as tertiary butyl hydroperoxide or ditertiary butyl peroxide; and peracids such as peracetic acid. Finally, the oxidizing agent may be used in an amount, up to the amount of the total reaction mixture, by weight, but preferably is used in an amount up to about 40%, by weight, of the solubilizing liquid. It is desirable also to avoid adding excess hydroxylcontaining compound, particularly primary alcohol, to the epoxidation reaction when solubilzed regenerated molybdenum catalyst of this invention is employed. Accordingly, after the solubilization of thermally precipitated solids, it is desirable to concentrate the molybdenum in solution particularly if substantial primary alcohols are used in the dissolution reaction. This is achieved by distilling the solution to remove excess alcohol. By this concentration procedure, solutions containing 5% or more dissolved molybdenum may be obtained. As in the solubilization itself. The presence of glycol stabilizes the solution in the concentrating procedure. However, a somewhat higher level of glycol is required for this effect. It has been found that mixtures containing at least 6 equivalents of glycol per equivalent of solubilized molybendum may yield homogeneous concentrated solutions upon distillation. Lower levels of glycol permit solid separation before completion of the distillation. For solubilization, the desirable amount of glycol is more than 10 equivalents of glycol per equivalent of solubilzed molybdenum. The preferred amount of glycol is 10 to 20 equivalents per equivalent of solubilized molybdenum. The concentrated homogeneous solution of molybdenum containing glycol as the primary component is suitable for direct addition in catalytic amounts to an epoxidation reaction to supply the necessary molybdenum. In order to further illustrate the subject matter of the present invention, the following examples are provided. However, it is to be understood that the examples are merely illustrative and are not intended as being restrictive of the invention herein disclosed and as defined by the annexed claims. Parts and percentages are by weight and temperatures are given in degrees centigrade unless otherwise specified. Example 1 A spent catalyst stream from a commercial molybdenum catalyzed epoxidation of propylene was thermally treated according to Lemke U.S Patent 3,887,361 to precipitate dissolved molybdenum as a solid. To regenerate that solid as a reuseable soluble molybdenum catalyst, 0.656 parts of the solid was reacted with 23 parts of methanol, 5 parts of a solution of about 110% by weight tertiary butyl hydroperoxide in tertairy butyl alcohol, and 4 parts of propylene glycol by heating the reactants together at 600 for 30 minutes. The reaction mixture was then filtered to remove the trace of solids which remained. The filtered solution was then distilled at a temperature of 1100C to remove methanol and other low boiling materials. The resulting homogeneous solution remaining in the distillation pot had the following composition by weight: 47,500 ppm dissolved Mo 48.0% propylene glycol 42.2% t-butyl alcohol The concentrated solution was an active catalyst suitable for reuse in epoxidation of propylene. Example 2 A thermally precipitated molybdenum-containing solid was obtained according to the Lemke procedure from a spent catalyst solution from a commercial propylene epoxidation as in Example 1. To regenerate that molybdenum-containing solid as a reuseable soluble molybdenum catalyst, 0.654 parts of the solid was reacted with 27.01 parts of tertiary butyl alcohol and 5.03 parts of a solution of about 40% by weight tertiary butyl hydroperoxide in tertiary butyl alcohol, by heating the reactants together at 750 for 2 hours. The solution obtained after reaction amouted to 32.5 parts and contained 6450 ppm of dissolved molybdenum. A small amount (0.078 parts) of solid remained undissolved and that solid contained 49.5k by weight molybdenum. Thus, 100% by weight of the original molybdenum charged was recovered and accounted for as solid or solution. Dissolved molybdenum amounted to 811% by weight of that charged. This example shows that satisfactory results may be obtained where a glycol is not a solubilizing reactant. Example 3 A thermally precipitated molybdenum-containing solid was obtained from a spent catalyst solution from a commercial propylene epoxidation as in Example 1. To regenerate that molybdenum-containing solid as a reuseable soluble molybdenum catalyst, 0.655 parts of the solid was reacted with 27 parts of tertiary butyl alcohol, 5.0 parts of a solution of about 408 by weight tertiary butyl hydroperoxide in tertiary butyl alcohol, and 1.03 parts of propylene glycol by heating the reactants together at 900 for 2 hours. The solution obtained after reaction amounted to 33.56 parts and contained 7580 ppm of dissolved molybdenum. A small amount (0.031 parts) of solid remained undissolved. Dissolved molybdenum amounted to 96% by weight of that charged. This example shows that a small amount of added glycol along with alcohol results in higher levels of molybdenum solubilization when an oxidizing agent is employed, compared to Example 2. Example 11 A thermally precipitated molybdenum-containing solid was obtained from a spent catalyst solution from a commercial propylene epoxidation as in Example 1. To regenerate that molybdenum-containing solid as a reuseable soluble molybdenum catalyst, 0.328 parts of the solid was reacted with 38.12 parts of tertiary-butyl alcohol by heating the reactants together at 900 for one hour. The solution obtained after reaction amounted to 37.98 parts and contained 2470 ppm of dissolved molybdenum. A small amount (0.,053 parts) of solid remained undissolved and that solid contained 56.7% by weight molybdenum. Thus 99% by weight of the original molybdenum charged was recovered and accounted for as solid or solution. Dissolved molybdenum amounted to 75% by weight of that charged. This example shows that alcohol alone is a suitable reactant for solubilizing molybdenum. Example 5 A thermally precipitated molybdenum-containing solid was obtained from a spent catalyst solution from a commercial propylene epoxidation as in Example 1. To regenerate that molybdenum-containing solid as a reuseable soluble molybdenum catalyst, 0.654 parts of the solid wqas reacted with 27 grams of propylene glycol and 5.0 parts of a solution of about 110% by weight tertiary butyl hydroperoxide in tertiary butyl alcohol, by heating the reactants together at 900 for 2 hours. The solution obtained after reaction amount to 32.10 parts and contained 9160 ppm of dissolved molybdenum. A small amount (0.008 parts) of solid remained undissolved. Dissolved molybdenum amounted to greater than 99% by weight of that charged. This example shows that glycol and oxidate alone without alcohol provides good dissolution. Example 6 A thermally precipitated molybdenum-containing solid was obtained from a spent catalyst solution from a commercial propylene epoxidation as in Example 1. To regenerate that molybdenum-containing solid as a reuseable soluble molybdenum catalyst, 0.654 parts of the solid was reacted with 26 parts of methanol, 5 parts of a solution of about 110% by weight tertiary butyl hydroperoxide in tertiary butyl alcohol, and 1.0 part of propylene glycol by heating the reactants together at 600 for 30 minutes. The solution obtained after reaction amounted to 33.05 parts and contained 8700 ppm of dissolved molybdenum. A small amount (0.005 parts) of solid remained undissolved. Dissolved molybdenum amounted to greater than 99% by weight of that charged. This example is similar to Example 1; but shows that lower levels of propylene glycol are satisfactory for stabilization of the dissolved molybdenum then required to obtain a homogeneous solution upon concentration. A stainless steel autoclave is charged with 70 parts propylene and heated to 1300. At that point, is added to the reactor a mixture of 20 parts of tertiary butyl hydroperoxide (TBHP) and 50 parts of tertiary butyl alcohol which contains 100 ppm molybdenum from the solution obtained above. After 60 minutes, reaction at 1300, the mixture is quenched and analyzed for propylene oxides (PO) and unreacted tertiary butyl hydroperoxide. The TBHP reacted amounts to 93% of that charged, and PO is produced in 88% selectivity versus hydroperoxide reacted.

Claims: CLAIMS 1. A process of regenerating soluble molybdenum catalyst for epoxidation of olefins with a hydroperoxide characterised in that it comprises: (a) thermally precipitating and separating a molybdenum containing solid from a spent catalyst stream from a molybdenum catalyzed olefin epoxidation; and (b) solubilizing the precipitated solid from (a) in a liquid hydroxyl-containing organic compound by heating said solid in the liquid to produce an active catalyst solution. 2. A continuous process for molybdenum catalyzed epoxidation of olefins with a hydroperoxide characterised in that spent molybdenum catalyst is regenerated and recycled by (a) thermally precipitating and separating a molybdenum containing solid from a spent catalyst stream obtained from a molybdenum catalyzed olefin epoxidation; (b) solubilizing the precipitated solid from (a) in a liquid hydroxyl-containing organic compound by heating said solid in the liquid to produce an active catalyst solution; and (c) adding a catalytic amount of the solution from (b) to a hydroperoxide epoxidation of an olefin. 3. The process according to claim 1 or claim 2 wherein the hydroxyl-containing organic compound is selected from monohydroxy alcohols, polyhydroxy alcohols, alkylene ethers of either of said alcohols, and mixtures of the aforementioned compounds. 4. The process according to claim l or claim 2 wherein the hydroxyl-containing organic compound is methanol or tertiary butyl alcohol. 5. The process according to claim l or claim 2 wherein the hydroxyl-containing organic compound is selected from ethylene glycol, propylene glycol, butylene glycol and glycerol. 6. The process according to any one of claims l to 5 wherein the thermally precipitated molybdenum is reacted at a temperature of 20 C to 1300C. 7. The process according to any one of claims 1 to 6 characterised in that a mixture of glycol and alcohol is employed as the hydroxyl-containing organic compound-and step (b) is conducted in the presence of an oxidizing agent.

Inventors: MOCELLA, MICHAEL THOMAS
Applicants: ATLANTIC RICHFIELD COMPANY
Application year: 1982
Main classification: C07D301
IPC codes: B01J23, C07D301, C07B61, B01J38