REACTIVE DYE

Abstract: A monoazo compound represented by a free acid of the formula: wherein R₁ and R₂ independently represent a hydrogen atom, or an alkyl, aralkyl or cyclohexyl group, R₃ represents a hydro­ gen atom or a methyl or sulfonic acid group: R₄ represents a hy­ drogen atom or an alkyl group; A represents an oxygen atom or -NH-; X₁ and X₂ independently represent a hydrogen or chlori­ ne atom or a methyl, methoxy, carboxyior sulfonic acid group; and Y represents -CH=CH₂ or -CH₂CH₂Z (Z represents a halo­ gen atom. -OSO₃H or -OPO₃H₂). This compound is used for dyeing cellulose fibers to give dyed products of yellow to red dish yellow having excellent fastnesses, particularly chlorine fastness.

Description: REACTIVE DYE This invention relates to novel monoazo compounds, a process for producing them and a process for dyeing cellulose fiber by using them. Dyes having B-sulfatoethylsulfonyl group are known as the so-called vinylsulfone type reactive dye for dyeing fiber materials. However, products dyed with yellow azo reactive dyes of this kind are generally low in chlorine fastness, so that they often discolor due to chlorine present in city water. Yellow dyes having monochlorotriazinyl group as a reactive group are also known. For example, the following dyes are disclosed in Published Unexamined Japanese Patent Application No. 13,790/80: EMI1.1 However, these reactive dyes generally require a high dyeing temperature and lack exhaustion dyeing ability, and thus they are used only for printing. In addition, dyed products have a fault of low acid stability. The present inventors earnestly studied to find a yellow vinylsulfone type reactive dye particularly excellent in chlorine fastness and acid stability and superior suitability for exhaustion dyeing, and as a result, it was found that particular monoazo compounds having both the so-called vinylsulfone type reactive group and a monochlorotriazinyl group can give a yellow to reddish-yellow dyed product meeting the above requirements. Thus, this invention provides a monoazo compound represented by a free acid of the formula (I): EMI2.1 wherein R1 and R2 independently represent a hydrogen atom, or an alkyl, aralkyl or cyclohexyl group; R3 represents a hydrogen atom, or a methyl or sulfonic acid group; R4 represents a hydrogen atom or an alkyl group; A represents an oxygen atom or -NH- group; X1 and X2 independently represent a hydrogen or chlorine atom, or a methyl, methoxy, carboxyl or sulfonic acid group; and Y represents -CH=CH2 or -CH2CH2Z (Z represents a halogen atom, -OSO3H or -OPO3H2); and a process for producing the monoazo compound represented by the above formula (I), which comprises (1) condensing an aromatic diamine represented by the formula (II): EMI3.1 wherein R3 is as defined above, and an aromatic amine represented by the formula (III): EMI3.2 wherein R4, X1, X2 and Y are as defined above, with cyanuric chloride to obtain an amine compound represented by the formula (IV): EMI3.3 wherein R3, R4, X1, X2 and Y are as defined above, diazotizing the amine compound (IV) and then coupling the diazotized product with a pyridone compound represented by the formula (V): : EMI4.1 wherein R1, R2 and A are as defined above, or (2) condensing the aromatic diamine of the formula (II) with cyanuric chloride, diazotizing the resulting condensate, coupling the diazotized product with the pyridone compound of the formula (V) to obtain a monoazo pyridone compound represented by the formula (VI): EMI4.2 wherein R1, R2, R3 and A are as defined above, and then condensing the monoazo compound of the formula (VI) with the aromatic amine of the formula (III). This invention also provides a process for dyeing cellulose fibers, which comprises using the monoazo compound represented by formula (I). The monoazo compounds of this invention represented by the formula (I) are excellent in various dye characteristics (high exhustion yield and fixation yield, excellent build-up property, etc.) and are useful as a reactive dye giving yellow to reddish yellow dyed product excellent in various fastness (fastnesses to chlorine, light, perspiration-sunlight, etc.) and excellent in wash-off property. This invention will be illustrated below in more detail. The aromatic diamine of the formula (II) usable for the present invention includes; 2, 4-diaminobenzenesulfonic acid, 4,6-diaminobenzene-l,3-disulfonic acid, 2, 5-diaminobenzenesulfonic acid, 2,4-diamino-5-methylbenzenesulfonic acid and the like. Regarding the aromatic amine of the formula (III), the alkyl group represented by R4 may be unsubstituted or substituted, and includes, for example, methyl, ethyl, propyl, butyl, hydroxymethyl, 2-hydroxyethyl, 2hydroxypropyl, 3-hydroxypropyl, 2-hydroxybutyl, 4hydroxybutyl, l-methyl-2-hydroxypropyl, cyanomethyl, cyanoethyl; methoxymethyl, 2-methoxyethyl, 3-methoxypropyl, ethoxymethyl, 2-ethoxyethyl, chloromethyl, 2chloroethyl, 3-chloropropyl, 4-chlorobutyl, carboxymethyl, 2-carboxyethyl, 2-methoxycarbonylethyl, 2-ethoxycarbonylmethyl, sulfomethyl and 2-sulfoethyl groups and the like. Examples of EMI6.1 group include; o-, m- or p-(ss-sulfoxyethylsulfonyl)-phenyl group, o-, m- or p-(vinylsulfonyl)-phenyl group, o-, m- or p-(-chloroethylsulfonyl)-phenyl group, o-, m- or p-(phosphoxyethylsulfonyl)-phenyl group, 4-methoxy-3-(B-sulfoxyethylvinyl, ss-chloroethyl or 8-phosphoxyethylsulfonyl)-phenyl group, 2-methoxy-5-(ss-sulfoxyethyl, vinyl, 5-chloro- ethyl or B-phosphoxyethylsulfonyl)-phenyl group, 2-methoxy-5-methyl-4-(ss-sulfoxyethyl, vinyl, (3-chlorethyl or 3-phosphoxyethylsulionyl)-phenyl group, 2,5-dimethoxy-4-(B-sulfoxyethyl, vinyl, 6-chlor- ethyl or B-phosphoxyethylsulfonyl)-phenyl group, 2-carboxy-5-(B-sulfoxyethyl, vinyl, B-chlor- ethyl or S-phosphoxyethylsulfonyl)-phenyl group, 2-chloro-4-(B-sulfoxyethyl, vinyl, B-chlor- ethyl or 6-phosphoxyethylsulfonyl)-phenyl group, and the like. Regarding the pyridone compound of the formula (V), the alkyl and aralkyl group represented by R1 and R2 may be unsubstituted or substituted. Examples of said alkyl group include straight or branched chain unsubstituted alkyl groups such as methyl, ethyl propyl, butyl, amyl, hexyl, octyl, nonyl, dodecyl and the like; hydroxyalkyl groups such as hydroxyethyl, hydroxypropyl and the like; and alkoxyalkyl groups such as alkoxyethyl groups (for example, methoxyethyl, ethoxyethyl, butoxyethyl, etc.), and the like. Examples of said aralkyl group include benzyl group, p-methyl- or p-ethyl-benzyl group, m-methylor m-ethyl-benzyl group, p-methoxy- or p-ethoxy-benzyl grup, m-methoxy- or m-ethoxy-benzyl group, p-dimethylaminoor p-diethylamino-benzyl group, phenethyl group, and pmethyl-, p-ethyl-, p-methoxy- or p-ethoxy-phenethyl group. The pyridone compound of the formula (V) can be produced either by alkylating citrazinic acid with an alkylating agent, if necessary followed by esterification or amidation, or by subjecting a citric triester or an aconitic triester and an amine derivative to cyclizing condensation reaction. The monoazo compound represented by the formula (I) may be produced in the following manner. The aromatic diamine of the formula (II) is condensed with cyanuric chloride in an aqueous medium, in the presence of a nonionic surfactant and at a temperature of -100C ts +200C (preferably 0 C to +100C) while adjusting pH to 1-5 (preferably 2-4). Then, the condensation product is condensed with the aromatic amine of the formula (III) at a temperature of 100C to 600C (preferably 300C to 500C) at a pH of 4-7 (preferably 5-6). Thus, the amine compound of the formula (IV) is obtained. The amine compound of the formula (IV) can be also obtained by condensing the aromatic amine of the formula (III) with canuric chloride in the same manner as above and then condensing the condensation product with the aromatic diamine of the formula (II) in the same manner as above. The amine compound (IV) thus obtained is then diazotized in a usual manner, for example, by using a small excessive amount of sodium nitrite at a temperature of -100C to +300C (preferably -5 C to +10 C). Then, the diazotized product is coupled with the pyridone compound of the formula (V) at a temperature of -10 C to +50 C(pre- ferably OOC to +200C) while adjusting pH to 4-7 (preferably 5-6), whereby the monoazo compound of the formula (I) is obtained. Alternatively, it is also possible to obtain the monoazo compound of the formula (I) in the following manner. The condensation product of the aromatic diamine of the formula (II) and cyanuric chloride obtained in the same manner as above is diazotized in a usual manner, for example, by using a small excessive amount of sodium nitrite at a temperature of -10 C to +200C (preferably -50C to +100C). Then, the diazotized product is coupled with the pyridone compound of the formula (V) at a temperature of -10 C to +40 OC (preferably -50C to +200C) while adjusting pH to 4-9 (preferably 5-7) to obtain the monoazo pyridone compound of the formula (VI). The monoazo pyridone compound is then condensed with the aromatic amine of the formula (III) at a temperature of IOOC to 700C (preferably 300C to 500C) at pH 4-7 (preferab16 at pH 5-6) to obtain the monoazo compound of the formula (I). As the monoazo compound obtainable in the abovementioned manner, the following compounds represented by the formulas, in which -CY- means field. EMI9.1 can be exempli EMI9.2 EMI10.1 EMI11.1 EMI12.1 EMI13.1 EMI14.1 EMI15.1 The monoazo compunds of this invention represented by the above formula (I) can be used for dyeing cellulose fibers yellow to reddish yellow by a usual dyeing processes, such as exhaustion dyeing, printing, continuous dyeing including cold pad batch up process, and the like. Cellulose fibers to be dyed include natural and regenerated cellulose fibers such as cotton, flax, viscose rayon, viscose staple fiber and the like. In the exhaustion dyeing, it can be carried out in a dyeing bath containing sodium sulfate or sodium chloride and an acid-bonding agent such as sodium carbonate, trisodium phosphate, sodium hydroxide or the like at a relatively low temperature, In the printing, it can be carried out by, for example7 printing a color paste comprising urea, an acid-bonding agent such as sodium bicarbonate, sodium carbonate, trisodium phosphate, sodium hydroxide or the like, and a paste (preferably, sodium alginate), to the fiber, predrying and then heating or steaming at a temperature of 100 - 2004C. The monoazo compound of this invention can give dyed products excellent particularly in chlorine fastness (3-4th to 4th grade). Because of the use of chlorine bleaching agent having become popular in washing at home, the monoazo compound of this invention excellent Ir chlorine fastness is of high value. Further, the monoazo compound of this invention excellent in fastnesses to light, perspiration-sunlight is suitable for dyeing outdoor wears such as sports wear. Further, the monoazo compounds of this invention show a high exhaustion yield and a high fixation yield in the exhaustion dyeing, and therefore they can give a dyed product having a color of deep hue. In addition, they are excellent in wash-off property, so that the unfixed dye can readily be removed. The monoazo compounds of this invention have a unique property such that in exhaustion dyeing they are unsusceptible to changes in dyeing temperature, alkaline agent, the amount of inorganic salt and bath ratio, so that they can dye the fiber with a very high reproducibility. This invention will be illustrated with reference to the following examples, wherein parts are by weight. Example 1 (Compound No. 1) 9.2 Parts of cyanuric chloride was dispersed in a solution of 0.1 part of nonionic surfactant in 100 parts of water at 0 - 100C. To the dispersion, a solution of 10.5 parts of sodium 2,4-diaminobenzenesulfonate in 100 parts of water was added dropwise over a time period of 1 hour at 0 - 50C while maintaining pH at 2-3, and then the resulting mixture was stirred for about 2 hours. Subsequently, 16.9 parts of l-aminobenzene-3 8-sulfatoethylsulfone was added. The resulting mixture was heated to 30 - 400C while adjusting its pH to 5 - 6 with aqueous solution of sodium carbonate, and then it was stirred at that temperature for 5 hours. In the resulting reaction mixture was dissolved 3.5 parts of sodium nitrite, and 13 parts of concentrated hydrochloric acid was added thereto at 0 - 50C to perform diazotization. Subsequently, the diazonium liquor was added to a solution prepared by dissolving 8.5 parts of 1-methyl-6-hydroxy-4-hydroxyzarbonyl-2-pyri one in 100 parts of water, and adjusting pH of the resulting solution to 5 - 6 with aqueous solution of sodium hydroxide, while maintaining pH at 5 - 6. Then, 100 parts of sodium chloride was added to the reaction mixture to precipitate a crystalline product. It was filtered with suction, washed and dried at 600C to obtain 51.3 parts of a dye having the following formula: EMI18.1 (Xmax 420 nm) Example 2 (Compound No. 3) 9.2 Parts of cyanuric chloride was dispersed in a solution of 0.1 part of nonionic surfactant in 100 parts of water at 0 to 100C. To the dispersion, a solution of 10.5 parts of sodium 2,4-diaminobenzenesulfonate in 100 parts of water was added dropwise at 0 - 50C over a time period of 1 hour while maintaining pH at 2 - 3, and then the resulting mixture was stirred for about 2 hours. The mixture was adjusted to pH 7 - 8 by adding 20% aqueous solution of sodium carbonate, and then 3.5 parts of sodium nitrite was added and dissolved therein. Thereafter 12.7 parts of concentrated hydrochloric acid was added thereinto to carry out diazotization. The resulting diazonium liquor was added to a suspension prepared by suspending 9.3 parts of l-methyl-6-hydroxy4-methoxycarbonyl-2-pyridone into 100 parts of water and adjusting pH to 5 - 6 with aqueous solution of sodium hydroxide, and then 5 parts of sodium bicarbonate was added thereto. To this reaction mixture was added 18.4 parts of 1-N-ethylaminobenzene-3-ss-sulfatoethylsulfone. The resulting mixture was heated to 30 - 400C while adjusting its pH to 5 - 6, and stirred at that temperature for 5 hours. Then, 100 parts of sodium chloride was added to precipitate a crystalline product, and it was filtered with suction, washed and dried at 600C to obtain 51.7 parts of a dye having the following formula: : EMI20.1 (Xmax 420 nm) Example 3 (Compound No. 5) 9.2 Parts of cyanuric chloride was dispersed in a solution of 0.1 part of nonionic surfactant in 100 parts of water at 0 to lO0C. Into the resulting dispersion, a solution of 10.5 parts of sodium 2,4-diaminobenzenesulfonate in 100 parts of water was added dropwise at 0 - 5"C over a time period of 1 hour while maintaining pH at 2 - 3, and then the mixture was stirred for about 2 hours. The mixture was adjusted to pH 7 - 8 by adding 20% aqueous solution of sodium carbonate and then 3.5 parts of sodium nitrite was added and dissolved therein. Thereafter 12.7 parts of concentrated hydrochloric acid was added thereinto at 0 - 50C to carry out diazotization. The resulting diazonium liquor was added to a suspension prepared by suspending 9.3 parts of 1-methyl-6-hydroxy 4-methoxycarbonyl-2-pyridone into 100 parts of water and adjusting pH value to 5 - 6 with aqueous solution of sodium hydroxide, and then 5 parts of sodium bicarbonate was added thereto. To this reaction!-mixture was added 16.9 parts of l-aminobenzene-3-ss-sulfatsethylsulfone, and the resulting mixture was heated to 30 - 400C while adjusting its pH to 5 - 6, and stirred at that temperature for 5 hours. Then, 100 parts of sodium chloride was added to precipitate a crystalline product, and it was filtered with suction, washed and dried at 600C to obtain 50.2 parts of a dye having the following formula: EMI21.1 (Amax 420 nm) Example 4 (Compound No. 20) 9.2 Parts of cyanuric chloride was dispersed in a solution of 0.1 Part of nonionic surfactant in 100 parts of water at 0 to 100C. Into the dispersion, a solution of 10.5 parts of sodium 2,5-diaminobenzenesulfonate in 100 parts of water was added dropwise at 0 - SOC over a time period of 1 hour while maintaining pH at 2 - 3, and then the resulting mixture was stirred for about 2 hours. The mixture was adjusted to pH 7 - 8 by adding 20% aqueous solution of sodium carbonate and then 3.5 parts of sodium nitrite was added and dissolved therein. Thereafter 12.7 parts of concentrated hydrochloric acid was added thereinto at 0 - 5 C to carry out diazotization. The resulting diazonium liquor was added to a suspension prepared by suspending 11.9 parts of l-cyclohexyl-6-hydroxy-4-hydroxycarbonyl-2-pyridone into 100 parts of water and adjusting its pH to 5-6 with aqueous solution of soium hdyroxide, and 5 parts of sodium bicarbonate was added thereto. To this reaction mixture was added 16.9 parts of l-aminobenzene-3-B-sulfatoethylsulfone sulfate, and the resulting mixture was heated to 30-400C while adjusting pH to 5-6 and stirred at that temperature for 5 hours. Then, 75 parts of sodium chloride was added to precipitate a crystalline product, and it was filtered with suction, washed and dried at 600C to obtain 49.7 parts of a dye having the following formula: EMI22.1 <tb> <SEP> C 2Na <tb> <SEP> N=N <SEP> NH <SEP> ft <SEP> NThN <SEP> NH <tb> <SEP> N <SEP> N <tb> OOH <SEP> Cl <SEP> S02C2HqOS03Na <tb> <SEP> CL <tb> <SEP> (Xmax <SEP> 435 <SEP> nm) <tb> Example 5 0.3 Part of the dye of Compound No. 1 was dissolved in 200 parts of water, and 20 parts of sodium sulfate and 10 parts of cotton were added in this order, and the bath was heated to 500C. 30 Minutes thereafter, 4 parts of sodium carbonate was added, and dyeing was continued at that temperature for 1 hour. After completion of the dyeing, the cotton was washed with water and soaped to obtain a yellow dyed product excellent in fastnesses, particularly in chlorine fastness. Example 6 0.3 Part of the dye of Compound No. 3 was dissolved in 200 parts of water, and 20 parts of sodium sulfate and 10 parts of cotton were added in this order, and the bath was heated to 400C. 20 Minutes thereafter, 3 parts of trisodium phosphate was added, and dyeing was continued at that temperature for 1 hour. After completion of dyeing, the cotton was washed with water and soaped to obtain a yellow colored dyed product excellent in fastnesses, particularly in chlorine fastness. Example 7 Color paste composition: Dye of Compound No. 1 5 parts Urea 5 parts Raw paste containing 5% of sodium alginate 50 parts Hot water 25 parts Sodium bicarbonate 2 parts Balance 13 parts The color paste having the above composition was printed on a mercerized cotton broad cloth. After predrying, the cloth was steamed at 1000C for 5 minutes, and thereafter washed with hot water, soaped, washed with hot water and then dried. Thus, a yellow printed product excellent in chlorine fastness was obtained. Example 8 Thirty parts of the dye of Compound No. 3 was dissolved in 925 parts of hot water and then the solution was cooled to room temperature (about 200C). To this solution were added 15 parts of 3Z.58 aqueous solution of sodium hydroxide and 30 parts of sodium sulfate to prepare a dye liquor. A cellulose fabric was dipped in this liquor, squeezed up to a pick-up 65% by a known method to carry out a padding. After winding up, the padded cellulose fabric was tightly wrapped with polyethylene film and allowed to stand for 20 hours at room temperature (about 200C). Subsequently, the cellulose fabric was washed with cold water and then with hot water, soaped in a boiling detergent solution, again washed with cold water and then dried. Thus, a dyed product having a very deep yellow color and free from unevenness in color was obtained.

Claims: CLAIMS: 1. A monoazo compound represented by a free acid ( the formula, EMI25.1 wherein R1 and R2 independently represent a hydrogen atom or an alkyl, aralkyl or cyclohexyl group; R3 represents a hydrogen atom or a methyl or sulfonic acid group; R4 represents a hydrogen atom or an alkylgroup; A represents an oxygen atom or -NH-; X1 and X2 independently represent a hydrogen or chlorine atom, or a methyl, methoxy, carboxyl or sulfonic acid group; and Y represents -CH=CH2 or -CH2CH2Z (Z represents a halogen atom, -OSO3H or -OP03H2). 2. The compound according to Claim 1, wherein R3 is a hydrogen atom. 3. The compound according to Claim 1, wherein R4 is a hydrogen atom or a C1-C3 alkyl, 2-carboxyethyl, 2-carbamoylethyl or 2-hydroxyethyl group. 4. A moRoazo compound represented by a free acid of the formula, EMI26.1 wherein R1 and R2 independently represent a hydrogen atom or an alkyl, aralkyl or cyclohexyl group; R3 represents a hydrogen atom or a-methyl or sulfonic acid group; R4 represents a hydrogen atom or an alkyl group; A represents an oxygen atom or -NH-; and Y represents -CH=CH2 or -CH2CH2Z (Z represents a halogen atom, -OSO3H or -OPO3H2). 5. The compound according to Claim 4, wherein R3 is a hydrogen atom. 6. The compound according to Claim 5, wherein R4 is a hydrogen atom or a C1-C3 alkyl, 2-carboxylethyl, 2-carbamoylethyl or 2-hydroxyethyl group. 7. A process for producing a monoazo compound represented by a free acid of the formula (I), EMI26.2 wherein R1 and R2 independently represent a hydrogen atom, or an alkyl, aralkyl or cyclohexyl group; R3 represents a hydrogen atom or a methyl or sulfonic acid group; R4 represents a hydrogen atom or an alkyl group; A represents an oxygen atom or -NH-; X1 and X2 independently represent a hydrogen or chlorine atom, or a methyl, methoxy, carboxyl or sulfonic acid group; and Y represents -CH=CH2 or -CH2CH2Z (Z represents a halogen atom, -OSO3H or -OPO3H2), which comprises (1) condensing an aromatic diamine represented by the formula (II), EMI27.1 wherein R3 is as defined above, an aromatic amine represented by the formula (III), EMI27.2 wherein R4, X1, X2 and Y are as defined above, with cyanuric chloride to obtain an amine compound represented by the formula (IV), EMI28.1 wherein R3, R4, X1, X2 and Y are as defined above, diazotizing the amine compound (IV) thus obtained and coupling the diazotized product with a pyridone compound represented by the following general formula (V), EMI28.2 wherein R1, R2 and A are as defined above, or (2) condensing the aromatic diamine represented by the formaul (II) with cyanuric chloride, diazotizing the condensate, coupling the diazotized product with the pyridone compound represented by the formula (V) to obtain a monoazo pyridone compound represented by the formula (VI), EMI28.3 wherein R1, R2, R3 and A are as defined above, and then condensing the monoazo compound (VI) with the aromatic amine represented by the formula (III). 8. A process for dyeing cellulose fibers, which comprises using a monoazo compound represented by a free acid cf the formula, EMI29.1 wherein R1 and R2 independently represent a hydrogen atom, or an alkyl, aralkyl or cyclohexyl group; R3 represents a hydrogen atom or a methyl or sulfonic acid group; R4 represents a hydrogen atom or an alkyl group; A represents an oxygen atom or -NH-; X1 and X2 independently represent a hydrogen cr chlorine atom, or a methyl, methoxy, carboxyl or sulfonic acid group; and Y represents -CH=CH2 or -CH2CH2Z (Z represents a halogen atom, -OSO3H or -OPO3H2). 9. Cellulose fibers dyed by the process of Claim 8.

Inventors: HARADA, NAOKI, SHIMIDZU, YASUTAKA, TEZUKA, YASUO
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1982
Main classification: C09B62
IPC codes: C09B62