COMPOSITE OXYALKOXIDES AND DERIVATIVES THEREOF

Abstract: Composite oxyalkoxides and their derivatives are novel organometallic compounds which give alkaline earth metal titanates such as barium titanate or strontium titanate by hydrolysis or thermal decomposition. The oxyalkoxides are synthesized by the reaction between an alkoxytitanium and an alkaline earth metal hydroxide, and their derivatives are synthesized by the reaction between the composite oxyalko­ xide and a cheating agent.

Description: Title of the Invention Composite oxyalkoxides and derivatives thereof The Field of Technique The present invention relates to a novel organo-metal compound and more particularly, it relates to composite oxyalkoxides and its derivatives using as a raw material for manufacturing composite oxides. The Background of Technique The composite oxides involving barium titanate and strontium titanate or the like have respectively a peculiar dielectric nature, a piezo-electric nature, a mechnical feature and a chemical feature, so that those composite oxides are a very important material to the electronical material or the fine performance ceramic material. The said oxides have been hitherto manufactured by carrying out its reaction in solid phase at a high temperature. For example, a titanate salt of alkaline earth metal has been manufactured with a reaction step of a titanium oxide with a carbonate salt of alkaline earth metals at a high temperature. The said reaction step is represented with a following reaction formula: EMI1.1 (wherein M denotes an atom of an alkaline earth metal.) However, the composite oxides obtained with above process contains a compa ratively larger amount of impurity and further, as to reactants of the composition, for example, in the event of producing the titanate salt of alkaline earth metal, the reaction compound does not necessarily show a stoichio metric value, even if its reaction is carried out with a definite condition by choosing definitely an atomic ratio (Ti/M) of titanium (Ti) in proportion to alkaline earth metal (M). Further, the said composite oxides obtained above has a granular diameter of several microns or more and a distribution of its granular diameter has a wider range. Consequently, the said composite oxides obtained with above process can not be said to have a high efficient capacity as the electronical raw material which requires a small size of mechanical structure having the high capacity. As a process for producing the composite oxides and improving the drawback of the said solid phase reaction, a method for perloraing a chemical reaction in a solution (hereinafter, this is abbreviated as the solution method11) is proposed. Generally, the solution method has features as listed below. (1) A purifying step by removing the impurity can be comparatively easily carried out and thereby, a high purity of the objective material is obtained. (2) The objective material having a granular diameter of one mili-micron or less and a narrow distribution of granular size is obtained. (3) An addition of the third material is easily carried out and even if its micro amount is added, a homogeneous composition can be obtained and consequently, the objective material having features conforming to the purpose can be obtained. However, the process for producing the composite oxide with the conventional solution method involves various drawbacks, so that it can not be adopted as an industrial process of obtaining the composite oxide. For example, in a process for producing a finely pulverized particles of barium titanate (BaTiO3) with a reaction of an aqueous solution containing barium hydroxide [Ba(OH2)] with titanium alkoxide [Ti(OR)4] as disclosed in tJ..N.C.S. 77 6194 (1954) and J.Amer.Ceram.Soc. 49 291 (1966)], it is-difficult to control a ratio of titanium/barium (Ti/Ba) in the finished product as a stoichiometric value. In a process for hydrolyzing an alcohol mixed solution barium alkoxides [Ba(OR)2] and titanium alkoxides [Ti(OR)4] and producing barium titanate [BaTiO3], as disclosed in the [U.S.Patent 3,647,364] and in another process for producing strontium titanate by using strontium alkoxides [Sr(OR) in the stead of the said barium alkoxides and the same procedure, as disclosed in the [J.Amer.Ceram.Soc. 53 91 (1970)], the alkaline earth metal alkoxides used as the raw material costs expensively and it is difficult to obtain the raw material and so, these processes are not practical. In a process for producing barium titanate [BaTiO3] with a reaction of barium hydroxide [Ba(OH)21 and titanium tetrachloride [TiCQ4] as disclosed in the [U.S.Patent 3,725,539] and in another process for producing barium titanate [BaTiO3] by treating barium chloride [BaCQ2] and titanium tetrachloride [TiCQ4] with hydrogen peroxide [H202], as disclosed in Japanese Open Patent No. 69599/1974, in the other words, in the process for producing the barium titanate, by using the compound other than the titanium alkoxide, as a titanium source, it is difficult to control a ratio of titanium/barium as a stoichiometric value and further, these reaction operations are complicated. In a process for making the barium titanate with thermal decomposition of titanyl barium oxalate which is obtained by reacting with a mixed solution containing titanium ion and barium ion and oxalic acid, as disclosed in the [U.S.Patent 2,758,911] the said titanyl barium oxalate is thermally decomposed at a high temperature of 700 C or more and consequently, a coarse grain of the crystal is produced and further, it is difficult to add the third material. An object of the present invention is to provide an useful novel organometal compound, the composite oxyalkoxides and its derivatives. Its another object is to provide the process for producing the said organo-metal compound and the improved process for producing the composite oxides with the solution method by using the said organo-metal compound. The inventors carried out the present invention by an eager researches to achieve above mentioned objects and as its results, they discovered a fact that the composite oxyalkoxides can be produced with a reaction of alkaline earth metal hydroxide and titanium alkoxides and further a fine crystal of alkaline earth metal titanate having a stoichiometric ratio of titanium/barium can be easily obtained with a hydrolysis of the said composite oxyalkoxides, Disclosure of the Invention The present invention comprises the composite oxyalkoxides which is represented by a composition formula (I), as a repeated constituent unit: : [.XhiOz(0R)2] ... (I), where its repeated number is in a range of 1 to 20 and the derivatives of the composite oxyalkoxides in which a substituent represented by [-OR] in the said compositicn formula (I) is partially or totally substituted with a chelating agent. In the co=position formula (I) by the present invention, M denotes alkaline earth metal atc= and for example, it denotes the same or different kinds of calcium, magnesium, barium and/or strontium. R denotes alkyl group by straight chain form or branched chain form having 1 to 6 carbon atoms, involving methyl group, ethyl group, propyl group, isopropyl group, butyl group tertiary-butyl group or hexyl group, substituted alkyl group by hydroxy group, alkoxy group having 1 to 3 carbon atom(s) or halogen, such as 1,4-butane diol residue, glycol residue or cello solve residue, a substituted or unsubstituted cyclo-alkyl group involving cyclohexyl group or l-methyl cyclopentyl group, an alkenyl group involving allyl group or crotyl group, and a subsituted or unsubstituted aralkyl group such as benzyl group, phenyl ethyl group and furthermore R denotes the same or different kinds of above mentioned substitutent(s). The said composite oxyalkoxides in the present invention is examplified as monomers of the compounds having a repeated constituent unit formlated below or oligomers of the compounds having repeated constituent unit in a range of 2 to 20. BaTiO2 [OCH(CH3)2]2, SrTiO2[OCH(CH3)2]2, BatiO2[O(CH3)3CH3]2, SrTiO2[O(CH2)3CH3]2, BaTiO2[O(C6H10)-2-C2H5]2, BaTiO2(OCH2-C6H5)2, BaTiO2(OCH2).CH2OH)2, BaTiO2(OCH3)a[OCH(CH3)2]b where a + b = 2, SrTiO2(OCH3)a[OCH(CH3)2]b where a + b = 2 and Ba Sr TiO2[O(CH2)3CH3]2 where x + y = 1. xy Another invention in the present invention comprises a composite oxyalkoxide derivatives that the substituent represented by [-OR] in the composite oxyalkoxides having the composition formula [I] as the repeated constituent unit is partially or totally substituted with chelating agent having to kinds or more of intermolecular functional groups, for example, the said chelating agent having hydroxy group, amino group or carbonyl group such as ss-diketones involving acetylacetone or benzoyl acetone and a- or ss-ketonic acids involving acetoacetic acid, propionyl butyric acid, benzoyl acetic acid or acetyl formic acid, and a- or ss-ketonic acid esters involving methyl, ethyl, propyl or butyl ester of the said ketonic acid, a- or ss-oxy acid involving glycollic acid, lactic acid, a- or ss-oxy acid esters involving methyl, ethyl, propyl, or butyl ester of the said oxy acid, a- or ss-oxy ketones involving diacetone alcohol or acetoin, a- or ss-oxy aldehydes involving glycollic aldedhyde or aldol, a-amino acids involving glycine or alanine and a- or ss-amino alcohol such as aminoethylalcohol. Thus, the derivative of the composite oxyalkoxides having the same kinds or different kinds of above specified chelating substituent is obtained. The composite 'oxyalkoxide derivatives by the present invention are examplified below. It comprises monomers of the compounds having repeated constituent unit as denoted in the following composition formula or these oligomer having repeated constituent unit in a range of 2 to 20. BaTiO2[0CP.(CH3)23-(OCOCH2COCH3), SrTiO2[0(CH2)3CH3l[(0CH2CE2)2N(CH2) 2 R]i Ba Sr TiO2[OCH(CH3)COO], where x + y = 1. xy The composite oxyalkoxides and its derivatives by the present invention are soluble in organic solvents and a high concentration of its solution can be obtained depending on the kinds of the used solvent. Further, the titanate salt(s) of alkaline earth metal can be easily produced with a hydrolysis or a thermal decomposition of these solutions. Particularly, the former compound absorbs a moisture in the atmosphere and it is subject to the kind of the substituent denoted by [-OR] in the composition formula [Ij, whereas the latter compound is almost stable in a common state without being caused the hydrolysis by the moisture in the atmosphere. The organic solvent solution containing the composite-oxyalioxides and/or its derivatives by the present invention is treated with a:direct hydrolysis or a thermal decomposition and thereby, a fine granular particles of the alkaline earth metal titanatesaltis obtained. Further, the said-organic solvent solution produces a film upon a thermal resistant base plate such as glass, ceramic or metal plate with a dipping process or a spraying process and. by means of its thermal decomposition, the film of the alkaline earth metal titanate salt is obtained on it. Furthermore, a solvent soluble polymer is added in the said organic solvent solution and a film moulding or a fiber molding is produced and then, by means of its hydrolysis or its thermal decomposition, an optional form of the alkaline earth metal titanate salt can be obtained. The composite oxyalkoxides and its derivatives are synthesized in such manner that a titanium alkoxide having a general formula [II] Ti(OR)4 ... [II] is made to react with an alkaline earth metal hydroxide having a general formula [III] M(OH)2 ... [III] as denoted in the following reaction formula [1] n!(OE)2 + nTi(OR)3#[MTiO2(OR)2]n 1 sr-ROH ... [lj and thereby, the said composite oN;alkoxídes is synthesized and then, the said composite oxyalkoxides is made to react with above mentioned desirable chelating agent and thereby, the composite oxylalkoxide derivative is synthesized, where R and M have the same significances defined precedently and n is an integer. In the event of synthesizing the composite oxyalkoxide derivatives, the titanium alkoxide having the general formula [II] is made to react with the desirable chelating agent and then, the resulting reaction compound may be reacted with the alkaline earth metal hydroxide. The titanium alkoxide having the general formula [II], as one of raw materials may be chosen from a titanium alkoxide containing the "R substituent" which is corresponded with the purposed composite oxyalkoxides or derivatives. The titanium alkoxide involving tetramethoxy titanium, tetraisopropoxy titanium, tetrabutoxy titanium or diethoxy-dilsopropoxy titanium is desirably used. Particularly, the tetraisopropoxy titanium and tetrabutoxy titanium which are industrially manufactured and easily obtained are desirably used. The composite oxyalkoxides having a different kind of substituent [-OR] group is obtained in such manner that a composite oxyalkoxide is produced by using the lower alkoxy-titanium as a raw material and the said composite oxyalkoxide is made to react with an alcohol having a desirable substituent [-OR] group and thereby, it is totally or partially substituted by introducing a desirable alkyl group. As the alkaline earth metal hydroxide having the general formula (III) its anhydrous or dried salt may be used and the said anhydrous or dried salt is desirably used for preventing the hydrolysis of the used titanium alkoxide and the produced composite oxyalkoxides. The synthetic reaction of the composite oxyalkoxide in the reaction formula [1] proceeds in the presence of an organic solvent or in the absence thereof, but said synthetic reaction proceeds mildly in the presence of the organic solvent. Further, as the said organic solvent, an organic solvent having a higher boiling point more than that of liberated alcohol is desirably used, because the alcohol is liberated according to the proceeding of the reaction and it mus be exhausted to the outside of reaction system. The use of the organic solvent having a high polar nature stabilizes the titanium ion and retards a reaction velocity, so that it is undesirable. Further, in the occasion that the substituent [-OR] group in a substitution reaction is totally or partially substituted with another desirable substuent, an alcohols is desirably used as the said organic solvent. The reaction denoted by the reaction formula [1] is carried out in the presence of an inert gas such as N2 gas and argon gas or a vapour atmosphere generated from the alcohol or the used solvent and thereby, it is purposed for preventing a hydrolysis reaction and an occurrence of carbonate salt which is generated by intermingling carbon dioxide gas with reactant. Its reaction temperature and its reaction time can be variable by the kinds of the raw materials and the employing organic solvent(s). Generally, the reaction temperature is chosen in a range of 50"C to 3000C, desirably is a range of 100 C to 2500C and the reaction time is chosen in a range of 0.5 to 60 hour(s), desirably in a range of 1.0 to 15 hour(s). As a desirable mode, the reaction is carried out during 1.0 to 3.0 hour(s) by refluxing the organic solvent. A non-reacted raw material by solid state and/or liquid state and impurites of the by-product and the reaction solvent in a reaction mixture, other than the composite oxyalko.ide can be separated with a conventional operation of separating a liquid component from a solid component such as a filtrating step and another conventional operation of gas-liquid seprrig such as a concentrating step and a distilling step and thereby the said composite oxyalkoxide, as the objective compound can be separated. Generally, the said composite oxyalkoxide is a monomer or a oligomer which is represented by the composition formula [I] and has an average repeated number of the constituent unit in a range of 1 to 100 and it is variable depending on the kinds of the raw materials, its blending ratio, the used solvent its kinds and its using amount, and its reaction condition such as its reaction temperature and its reaction time and the posterior treating conditions. Anoligomer having the said average repeated number of 4 to 12 is obtained under a common condition. Further, by utilizing the variations of chemical properties and physical properties being caused by mutual difference of the said repeated unit number, the material having a narrow distribution of the repeated unit number can be produced. Moreover, the said composite oxyalkoxides may be obtained with the process as set forth below: (a) The reaction which comprises making an alkoxy titanium to react wlth M-alkoxide in the presence of two multiple molar amount of water proportional to the said M-alkoxide where M denotes alkaline earth metal. (b) The reaction which comprises making Oxide as a replaced reactant for the M-hydroxide to react with alkoxy titanium in the presence of an equal molar amount of the water proportional to the said M-oxide and the said alkoxy titanium. (c) The reaction which comprises making a reaction compound of the alkoxy titanium and the water [TiO(OR)2] to react with the said Oxide. On the other hand, the composite oxyalkoxide derivative is synthesized with a process which comprises adding a desirable chelating agent in a synthetic reaction solution containing the said composite oxyalkoxide and finishing completely its reaction. Of course, it can be also synthesized with a process in which the composite oxyalkoxide, once separated is made to react with the chelating agent in an organic solvent. This synthetic reaction is carried out under the air-tight state on the basis of the same reason which occurs in the synthetic reaction of producing the composite oxyalkoxide. Its reaction condition is variable depending on the kinds of the said composite oxyalkoxides and the chelating agent, the presence or absence of the used solvent, its kinds and its amount, but generally, its reaction temperature is chosen in the range of 0 C to 300"C, desirably is the range of 20"C to 250"C and its reaction time is chosen in the range of 0.5 to 10 hour(s), desirably in the range of 1.0 to 5.0 hour(s). The composite oxyalkoxide derivative(s) obtained above is a monomer or an oligomer having an average repeated number of the standard constituent unit in the range of 1 to 100, even if the said average repeated number depends on the repeated constituent unit number of the composite oxyalkoxide. Usually, the oligomer having the said average repeated number of 4 to 12 is obtained under a common reaction condition. Further, the distribution extent of the said constituent unit repeated number can be narrowed as a similar way that was carried out for the composite oxyalkoxides. Brief Illustrations to the Drawings The Fig. 1 to the Fig. 6 show one exam?le for the infrared ray absorption curves of the composite oxyalkoxides and these derivatives. Fig. 1 : BaTiO2(OCH3)1,8[OCH(CH3)2]0.2 Fig. 2 : SrTiO2(OCH3)1.9[OCH(CH3)2]0.1 Fig. 3 : BaTiO2(OCH2CH2CH)2 Fig. 4 : BaTiO2(OCH3)1.4[OCH(CH3)2]0.6 Fig. 5 : BaTiO2[OCH(CH3)2](OCOCH2COCH3) Fig. 6 : Ba0.5Sr0.5TiO2[OCH(CH3)COO] The Best Modes for performing the Invention The present invention is more minutely explained by referring to Examples and Applied Examples, but the present invention is not defined limited by those Examples and Applied Examples. pM(OH)2 + nTi(OR)4 i [MTiO2(OR)2] + 2nROH n 26.5 g (0.155 mol) of Ba(OH)2 as the M(OH)2, 43.2 g (0.152 mol) of Ti[OCH(CH3)2]4 as the Ti(OR)4 and 60 mol of para-xylene were charged in a four inlet type of flask having 200 ml of volume capacity being fitted with a reflux- ing device combined with a cooler, an agitator and a thermometer. A temperature for above reactants was raised with a simultaneous agitating step in the presence of nitrogen atmosphere and an isopropanol was initially distilled at 1200C of reaction temperature. Further, its reaction under a refluxing step of the para-xylene was continuously carried out during two hours and then, the reaction was finished. In these times, a white muddy solution was changed and discolourized as a light yellowish solution. 17 g (0.297 mol) of the isopropanol was distilled out. After having filtered one part of insoluble BaCO3, the reaction solution was heated under a reduced pressure and the para-xylene was distilled and removed and then, 50.7 g of light yellowish solid material was obtained. This material was confirmed to have the isopropyl group by procedures of IR and NNR and further, it was identified as a material having a composition formula of BaTiO2[OCH(CH3)2]2 by an elementary analysis value of Ba and Ti. Further, it was identified to have 2,620 of molecular weight with a measurement for a depression of freezing point of the para-xylene solution and it was assumed as octamer. Subsequently, various kinds of the composite oxyalkoxides were synthesized by replacing variously the kinds of M(OH)2 and Ti(OR)4 and performing the same treatments. The synthetic condition and the synthetic results are set forth in Table 1: Table 1 EMI13.1 <tb> <SEP> Reaction <tb> <SEP> formula <SEP> n.M(OH2) <SEP> + <SEP> n.Ti(OR)4#[MTiO2(OR)2]n <SEP> + <SEP> 2nROH <tb> <SEP> No. <SEP> M <SEP> -OR <SEP> Solvent <SEP> temperature/ <SEP> Molecular <SEP> n <SEP> Elementary <SEP> Analysis <tb> <SEP> time <SEP> Weight <SEP> Analy. <SEP> Calc. <tb> <SEP> 1-(1) <SEP> Ba <SEP> -OCH(CH3)2 <SEP> para- <SEP> 120 C/2 <SEP> Hr <SEP> 2602 <SEP> 8 <SEP> Ba: <SEP> 40.6, <SEP> 40.9 <tb> <SEP> xylene <SEP> Ti: <SEP> 14.5, <SEP> 14.3 <tb> <SEP> 1-(2) <SEP> Sr <SEP> -OCH(CH3)2 <SEP> - <SEP> 180 C/2 <SEP> Hr <SEP> - <SEP> - <SEP> Sr: <SEP> 32.3, <SEP> 30.7 <tb> <SEP> Ti: <SEP> 17.6, <SEP> 16.8 <tb> <SEP> 1-(3) <SEP> Ba <SEP> -O(CH2)3CH3 <SEP> Diethyl- <SEP> 104 C/2 <SEP> Hr <SEP> - <SEP> - <SEP> Ba: <SEP> 36.9, <SEP> 37.8 <tb> <SEP> benzene <SEP> Ti: <SEP> 14.4, <SEP> 13.2 <tb> <SEP> 1-(4) <SEP> Sr <SEP> -O(CH2)3CH3 <SEP> Decalin <SEP> 185 C/11 <SEP> Hr <SEP> - <SEP> - <SEP> Sr: <SEP> 28.2, <SEP> 27.9 <tb> <SEP> Ti: <SEP> 14.9, <SEP> 15.3 <tb> <SEP> 1-(5) <SEP> Ba <SEP> -O(C6H10)- <SEP> - <SEP> 215 C/13 <SEP> Hr <SEP> - <SEP> - <SEP> Ba: <SEP> 40.9, <SEP> 40.3 <tb> <SEP> 2-C2H5 <SEP> Ti: <SEP> 14.3, <SEP> 14.5 <tb> Example 2 A solution consisting of 6.2 g (0.036 mol) of Ba(OH)2 and 50 ml of methanol (CH3OH) was charged in four inlet type of flask having 200 ml of volume capacity and being fitted with a refluxing cooler. an agitator and a thermometer. The said solution was heated at 800C of temperature in the presence of nitrogen gas atmosphere and by maintaining above temperature 9.6 g (0.034 mol) of Ti[OCH(CH3)2]4 and 30 ml of isopropanol [(CH3)2CHOH] were dropped in the said flask. The isopropanol [(CH3)2CHOH] and the methanol [CH3OH] were distilled off from the homogeneous reaction solution at a temperature of 800C or less and a vacuum state and 10.0 g of the reaction compound was obtained. The said reaction compound was identified as a compound having a compo- sition formula BaTiO2(OCH3)1.8[OCH(CH3)2]0.2 with the identification result of the IR and NMR procedures and the elerentary analysis. Further, it was assumed to have 1,190 of molecular weight by a measure ment for the depression of freezing point of para-xylene solution. The IR curve cf the obtained compound of BaTiO2(OCH)1.8[OCH(CH3)2]0.2 is set forth in Fig. 1. The elementary analysis value: Ba (49.6 %) Ti (16.9 %) The calculation value : Ba (48.2 ) Ti (16.8 %) Example 3 6.1 g (0.050 mol) of Sr(OH)2 and 160 g of methanol (CH3OH) were charged in tp same apparatus employed in the Example 1. Those reactants were heated at 65 C of temperature with an agitating step and thereby, the methanol (CH3OH) was refluxed. In continuance of the methanol (CH3OH) refluing step, a solution consists ing of 14.4 g (0.C50 mol) of Ti[OCH(CH3)2]4 and 35 g of benzene was dropped in the reaction system during 3 hours and thereby, a reaction slurry was obtained. The solvent was distilled off and removed from it under a reduced pressure and thereby, the reaction compound was obtained. The reaction compound was identified as a composition of SrTiO2(OCH3)1.9 [OCH(CH3)2]0.1 by the identification results of the IR and NMR procedures and the elementary analysis. It was assumed to have 1,800 of molecular weight and to be octamer. The IR curve of SrTiO2(OCH3)1.9[OCH(CH3)2]0.1 is set forth in Fig. 2. Elementary analysis value : Sr: 37.2 (%) Ti: 21.0 (%) Calculation value : Sr: 37.7 (Z) Ti: 20.6 (%) Example 4 3.4 g (0.01 mol) of BaTiO2[OCH(CH3)2]2 obtained in the Example: 1-(1) was dissolved in 20 ml of xylene and by maintaining it in a heating step at 80 C of temperature, 1.2 g (0.02 mol) of ethylene glycol was dropped in it and thereby a white precipitate was obtained. The white precipitate was filtered and it was dried and thereby, 3.4 g of the composition of BaTiO2(OCE2CH2OH) 2 was obtained. The IR curve of BaTiO2(OCH2CH2OH)2 is sez forth in Fig. 3. The Elementary analysis value : Ba (39.8 %) Ti (14.2 %) The calculation value : Ba (40.5 %) Ti (14.1 %) Example 5 3.4 g (0.01 mol) of the BaTiO2[OCH(CH3)2]2 obtained in the Example: 1-(1) was dissolved in 20 ml of xylene and by maintaining it in a heating step at 80 C of temperature, 2.2 g (0.02 mol) of benzyl alcohol was dropped in it and thereby, the homogeneous reaction solution was obtained. By distillating off the xylene from the said reaction solution 4.2 g of a composition of BaTiO2(OCH2.C6Hs)2 was obtained. It was assumed as a tetramer having 1,800 of molecular weight. The elementary analysis value : Ba (31.3 %) Ti (11.3 %) The calculation value : Ba (31.8 %) Ti (11.1 %) Example 6 8.6 g (0.05 mol) of Ba(OH), 28.4 g (0.1 mol) nf Ti[OCH(CH3)2]4 and 50 ml of decalin was charged in the same apparatus employed for the Example 2 and it was heated at 190 0C of temperature and simultaneously agitated and an isopropanol was distilled off with the solvent refluxing step. After having finished the reaction during three hours, a homogeneous reaction solution was obtained. By distilling off the solvent from the said reaction solution under a vacuum state and it was dried and thus, the composition of Bac.5.Sro.5.TiO2[OCH(GH3)2]2 was obtained. Example 7 3.7 g (0.020 mol) of Ti[OCH(CHi)2]4, 3.2 g (0.020 mol) of BaO and 30 ml of methanol were charged in the same apparatus employed in the Example 2 and by heating it at 650C of temperature with a simultaneous agitating and refluxing step, the reaction was carried out during two hours and thus, a homogeneous reaction solution was obtained. The solvent was distilled off from the said reaction solution and it was dried and the composition of BaTiO2(OCH3)1.4[OCH(CH3)2]0.6 was obtained. The IR curve of a composition : BaTiO2(OCH)1.4[OCH(CH3)2]0.6 is set forth in Fig. 4. The elementary analysis value : Ba (50.9 %) Ti (20.1 %) The calculation value : Ba (52.6 %) Ti (18.3 %) Example 8 2S.5 g (0.085 mol) of BaTiOz[OCH(CH3)z]2 prepared in the Example: 1-(1) and 22.8 g of para-xylene were charged in a four inlet type of flask having 200 ml of volume capacity and being fitted with a reflexing cooler, an agitator and a thermometer. Then, 8.5 g (0.85 mol) of acetylacetone (CH3COCH2COCH3) was gradually dropped in above reactants at room temperature in the presence of nitrogen gas atmosphere. In the proceeding of the dropping step, an exothermic phenomenon did occur and a partial precipitation arose in a reaction system. Then, it was heated and, in the occasion that its reaction temperature reached to about 1000C of temperature, an isopropanol was initially distilled out. Sitrulta- neously, the precipitate was dissolved in it. 4.3 g (0.072 mol) of the isopropanol was distilled out kith the heating step during about two hours. The reaction solution obtained above was transparent without causing any sediment, even if it was exposed in the atmosphere during six hours. The solvent was distilled out from the obtained reaction solution at a temperature of 50"C or less and under a reduced pressure. 32.1 g of the reaction compound was obtained. The said reaction compound was identified as a compound having a composition formula : BaTiO2[0CH(CH3)2][0COCH2COCH2] with the identifying results of the IR and NMR procedures and the elementary analysis. Further, it was assumed as a dimer having 840 of molecular weight by measuring the depression of the freezing point of the para-xylene solution. The IR chart for the reaction compound obtained in this Example are set forth in Fig. 5. The elementary analysis value : Ba (37.2 Z) Ti (13.4 %) The calculation value : Ba (36.6 ,0) Ti (12.8 %) Example 9 25.0 g (0.080 mol) of SrTiO2[0(CH2)3CH3] prepared in the Example: 1-(4) and 50 ml of decalin were charged in the same apparatus employed in the Example 8. 6.0 g (0.040 mol) of triethanolamine was gradually added in it at room temperature and in the presence of nitrogen gas atmosphere. In the proceeding of above dropping step, its exothermal phenomenon did occur. Its temperature was still raised with a heating step and in the event of reaching to about 125"C of temperature, a normal butanol was initiated to distill out. The normal butanol was distilled out by an amount of 5.7 g (0.077 nol). The reaction solution was transparent without generating any sediment, even if it was exposed in the atmosphere during 6 hours. A gelled material obtained above was heated at a temperature of 90"C or less and under a reduced pressure and thereby the decalin was distilled out and thus, 25.4 g (0.081 mol) of the reaction compound was obtained. The said reaction compound was identified as the composition formulated by : SrTiO2[O(CH2)3CH3].[(OCH2CH2)2N(CH2)2OH]¸ by means of the IR and NMR procedures and its elementary analysis. Further, it was assumed as a heptamer having 2,050 of molecular weight by measuring the depression of the freezing point of the para-xylene solution. The elementary analysis value : Sr (28.4 %) Ti (15.2 %) The calculation value : Sr (27.9 %) Ti (15.3 %) Example 10 14.5 g (0.043 mol) of the BaTiO2[0CH(CH3)2]2 prepared in the Example 1-(1), 11.6 g of para-xylene, 12.3 g (0.043 mol) of SrTiO2[0CH(CH3)2]2 prepared with the same process in the Example : 1-(2) and 24.5 g of decalin were charged in the same apparatus employed in the Example 8. 7.7 g (0.086 mol) of lactic acid was dropped in above reactants with a simultaneous agitating step. The reaction system being accompanied with an exotherral phenomenon was initiated to separate a white precipitate. By keeping the same condition, it was heated at a temperature of 980C or less and then, its temperature was raised and thereby, an isopropanol was distilled out. The distilled isopropanol was an amount of 9.6 g (0.16 mol). The obtained reaction solution was transparent without separating any sediment, even if it was exposed in the atomosphere during 6 hours. The white precipitate separated was filtered and the filtrate was washed with 50 ml of para-xylene and it was dried and thus, 24.5 g of the reaction compound was obtained. The reaction compound was identified as a compound having a composition formula : BaosSro.sTiO2[0CH(CH2)COO] with the measurements of the IR and NoR procedure (i.e. the measument by decomposing the white powders in a system of concentrated DCQ-D20) and the elementary analysis. The IR chart for the reaction compound is set forth in Fig. 6. The elementary analysis value : Sr (28.4 %) The calculation value : Sr (27.9 %) Reference Example A stability test for the stability of the composite oxyalkoxide obtained is the Examples 1-(1) and 1-(4) is comparison with the stability of the composite oxyalkoxide derivatives obtained in the Examples 8 to 10 was carried out. This comparison results are set forth in Table 2. Table 2 EMI20.1 <tb> <SEP> Stability <SEP> of <SEP> the <SEP> solid <tb> Example <SEP> 8 <SEP> Even <SEP> if <SEP> exposed <SEP> in <SEP> the <SEP> atomsphere <SEP> during <SEP> one <SEP> day, <SEP> its <tb> <SEP> weight <SEP> was <SEP> not <SEP> decreased <SEP> and <SEP> any <SEP> charge <SEP> did <SEP> not <SEP> appear <tb> <SEP> in <SEP> the <SEP> IR <SEP> chart. <tb> Example <SEP> 9 <SEP> Ditto <SEP> as <SEP> that <SEP> in <SEP> the <SEP> above <SEP> column. <tb> Example <SEP> 10 <SEP> After <SEP> exposed <SEP> in <SEP> the <SEP> atmosphere, <SEP> its <SEP> weight <SEP> was <SEP> not <tb> <SEP> decreased. <tb> Example <SEP> 1-(1) <SEP> After <SEP> exposed <SEP> in <SEP> the <SEP> atmosphere, <SEP> its <SEP> weight <SEP> was <SEP> not <tb> <SEP> decreased <SEP> and <SEP> the <SEP> absorption <SEP> of <SEP> TiOiPr <SEP> in <SEP> the <SEP> IR <tb> <SEP> chart <SEP> was <SEP> decreased. <tb> Example <SEP> 1-(4) <SEP> After <SEP> exposed <SEP> in <SEP> the <SEP> atmosphere <SEP> during <SEP> one <SEP> day, <SEP> its <tb> <SEP> weight <SEP> was <SEP> not <SEP> decreased <SEP> and <SEP> the <SEP> absorption <SEP> of <tb> <SEP> TiO-nSu <SEP> in <SEP> the <SEP> IR <SEP> chart <SEP> was <SEP> decreased. <tb> Applied Example 1: 10 g (0.0298 mol, as a converted rate to the monomer) of the compound of BaTiO2[0CH(CH3)2]2 synthesized in the Example: 1-(1) was dissolved in about 100 ml of para-Xylene and it was heated at a temperature of 90"C to 100"C. 1.07 g (0.060 mol) of water was gradually dropped in above reactants under the heated condition by using a micro-Syringe. In the course of two hours, the precipitate produced was filtered and the filtrate was washed with water 'and it was dried at 1000C of temperature under a reduced pressure and thus, 6.9g of the compound of BaTiO with 99.3 percent of yield rate. The said RaTiO3 was identified as a cubic Crystal (a=4.051) with X ray diffraction meter. Further, it was observed as a coagulated material having a diameter of 1 to 2 micron which consists of coagulated fine particles having a granular diameter of 0.1 micron or less by using a scanning electronical microscope. Applied Example 2: 5 g (0.0149 mol) of the BaTiO2[OGH(GH3)2]2 synthesized in the Example: 1-(1) was calcined at 900 C of temperature during two hours under the air ventilation, whereby 3.5 g (0.0149 mol) of BaTlO3 powders was obtained. This material was identified as a cubic crystal (a=4.0 b=26 & c=4,000) with X ray diffraction. Further, by using the scanning electrical microscope, it was observed as the coagulated material having a diameter of 1 to 2 micron with consists of the fine particles having 0.2 micron of granular diameter. Applied Example 3: 5.9 g (0.018 mol) of the BaTiO2[0CH(CH3)2]2 synthesized in the Example l-(1) was dissolved in 40.1 g of normal butanol and thereby, the adjusted solution containing 8.9 weight percent of the converted BaTiO3. A silica glass plate having a size of width (30 mm) x Lenghth (50 mm) x thickness (3 mm) was immersed in the said adjusted solution during one minute in the presence of nitrogen atmosphere and the silica glass plate was lifted with a constant velocity of 3 cm/minute. Its solvent was blown off from the said silica glass plate in the presence of nitrogen gas and then, it was dried at 1000C of - temperature during one hour in the air and subsequently, it was baked at 700"C of temperature during 3 hours in an electric furnace. Thus, a semi-transparent film of BaTlO3 was obtained. Applied Example 4: 5 g (0.0175 mol) of the SrTIO3[OCH(GHs)2j2 obtained in the Example 1-(2) was calcined at 900"C of temperature during two hours under an air ventilation, whereby 3.1 g (0.0169 mol) of the SrTiO3 powders was obtained. It was identified as SrTiO3 having the cubic crystal with X ray diffraction method (a=3.884). Further, it was observed as the coagulated material of 1 to 2 micron grains consisting of fine particles having 0.1 micron of granular diameter by using the scanning electronical microscope. Applied Example 5: The one part of the homogeneous solution obtained in the Example 1-(3) was sampled in a petri dish and it was exposed in the air and thereby it was changed as a transparent gelled compounds. It was dried with irradiation of infrared ray lamp, whereby it was decomposed as the fine particles. It was manifested with the IR process and the elementary analysis that the said fine particles is corresponded as the powders of BaTiO2CO3. The fine particles was baked at 7000C of temperature during two hours and the fine particles of BaTlO3 having a cubic crystal was obtained. It was a coagulated material having a size of 1 to 2 micron which consists of the fine particles having a granular diameter of 0.1 micron or less. Applied Example 6: 15.5 g (0.043 mol) of the powders obtained in the Example 8 was dissolved in 370 g of normal butanol and the solution was adjusted as a solution contain- ing 5 weight percent of converted concentration of BaIiO3. The adjusted solution was stable, even if it was exposed in the air so that a quartz glass plate having a size of width (30 mm) x length (50 mm) x thickness (3 mm) was immersed in the adjusted solution in the presence of the air. In the course of one minute, the quartz glass plate was lifted up with a constant velocity of 40 cm/minute. It was air-dried during 10 minutes and further, it was dried at 1000C of temperature during one hour and then, it was baked at 1,100 C of temperature during 3 hours in an electric furnace, whereby a transparent film of BaTiOb was obtained. Applied Example 7: The composite oxyalkoxldes and the composite oxyalkoxide derivatives obtained in the Examples 2 to 10 were hydrolyzed or thermally decomposed and thereby the salts of alkaline earth metal titanate were obtained. This results are set forth in Table 3. Table 3 EMI24.1 <tb> <SEP> The <SEP> reaction <SEP> compound <tb> <SEP> Example <SEP> Decompcsition <tb> <SEP> Composition <SEP> External <SEP> Granular <tb> No. <SEP> process <SEP> formula <SEP> * <SEP> appearance* <SEP> diameter** <tb> <SEP> 2 <SEP> Hydrolysis <SEP> BaTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> 3 <SEP> Thermal <SEP> SrTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> decomposition <tb> <SEP> 4 <SEP> Thermal <SEP> BaTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> decomposition <tb> <SEP> 5 <SEP> Hydrolysis <SEP> BaTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> 6 <SEP> Thermal <SEP> Ba0.5#Sr0.5#TiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> decomposition <tb> <SEP> 7 <SEP> Hydrolysis <SEP> <RTI ID=24.2> RaTIO3 <SEP> crystal <SEP> <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> Thermal <tb> 8 <SEP> 8 <SEP> decomposition <SEP> BaTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> 9 <SEP> Thermal <SEP> SrTiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> decomposition <tb> <SEP> 10 <SEP> Thermal <SEP> Ba0.5#Sr0.5#TiO3 <SEP> crystal <SEP> 0.1 <SEP> micron <SEP> or <SEP> less <tb> <SEP> decomposition <tb> Note By the X ray diffraction method ** : By the scanning electronical microscope Feasibitity of Industrial Utilization The composite oxyalkoxides and its derivatives by the present invention are a novel useful, organo-metal compound for producing the titanate salts of alkaline earthmetalby the solution method and these compounds and its derivatives have the following features. (1) The composite oxyalkoxides and its derivatives are able to produce easily the titanate salts of alkaline earth metal by means of a hydrolysis or a thermal decomposition under appropriate condition. (2) The composite oxyalkoxides and its derivatives have solubility in organic solvent and consequently, by adding a moulding agent, the mouldings such a film, a plate or a fibers can be produced. Further, the said mouldings or a non-moulded material is treated with a hydrolysis step or a thermally decomposing step and thereby, the titanate salts of alkaline earth metal by a fine particle form, a film form, a plate form or a fibrous form as a desirable form can be obtained. (3) The composite oxyalkoxides and its derivatives have the solubility i the organic solvent, so that by adding preliminarily a shifer, a depressor, a semiconductively denaturing agent or a sintering aid in the titanate salt(s) of alkaline earth metal,a homogeneous mixture is obtained. (4) The composite oxyalkoxides and its derivatives have a ratio of Ti/.M as a stoichiometric value, so that the ratio of Ti/M in the titanate salt(s) of alkaline earth metal obtained with the hydrolysis or the thermal decomposition is a stoichiometric value or its extremely approximate value. (5) By using the raw material, obtained easily with a comparatively low cost, a simple manufacturing process can be carried out. (6) The composite oxwalkoxide derivative have a more superior storage stability in comparison with the composite oxyalkoxides. The present invention is to provide the composite oxyalkoxides and its derivative as a novel material which are useful for manufacturing the titanate salt(s) of alkaline earth metal and its industrial significance is very large.

Claims: What is clal-ed is 1. A composite oxyalkoxides represented by a composition formula (I) as a formula of repeated constituent unit: [MTiO2(OR)2] ... (I) in which M denotes the same or different kinds of alkaline earth metal atom(s) and R denotes the same or difference kind of group being chosen from straight or branched chain alkyl group having 1 to 6 carbon atom(s), substituted alkyl group by hydroxy group, alkoxy group having 1 to 3 carbon atom(s) or chlorine, substituted or unsubstituted cycloalkyl group, alkyl group and alkyl group and the repeated number o con- stituent unit is in a range of 1 to 20. 2. According to the Claim 1, the said composite oxyalkoxide is synthe- sized with a process which comprises making an alkoxy titanium havIng a general formula (II): [II] to react than alkaline earth hydroxide having a gen formula (III): [III] in the presence of a solvent or in the absence thereof. 3. According to the Claim 1, the said composite oxyalkoxide is synthe sized with a process which comprises obtaining the composite oxyalkoxide with a reaction of lower alkoxy titanium and alkaline earth metal hydroxide and further making the said composite osyalkoxide to react with an alcohol(s) having a desirable (-OR) group and thereby introducing the desirable (-OR) group in it. 4. In the said reaction, according to the Claim 3, the said lower alkoxy titanium involves tetraisopropoxy titanium and tetrabutoxy titanium. 5. In the said reaction, according to the Claims 2 and 3, a reaction con dition comprises a time of 1 to 3 hours at a refluxing temperature in the presence of a non-polar organic solvent. 6. A composite oxyalkoxide derivative in which the said composite oxy- alkoxides consisting of the repeated consistuent. unit having the composition formula [I]: [MTiO2(OR)2] ... [I] is partially or totally substituted with a chelating agent as a susti tuent(s) of (-OR) group, lGnere the repeated number of the constituent unit is in a range of 1 to 20, M denotes the same or different kind(s) of alkaline earth metal atom and R denotes the same or different kind(s) of the group(s) being chosen from straight or branched chain alkyl group having 1 to 6 carbon atom(s), substituted alkyl group by hydroxy group, alkoxy group having 1 to 3 carbon atom(s), or chlorine atom, a substituted or unsubstituted cycloalkyl group, alkenyl group or aralkyl group. 7. According to the Claim 6, the said chelating agent comprises the same or different kinds of compounds being chosen from the chelating agent having intermolecularly two kinds or more of functional group such as ss-diketones, a- or ss-ketonic acids, a- or ss-ketonic acid esters, a or -oxy-acids, a- or ss-oxt-acid esters, a- or -oxv-ketones, a- or oxy-aldehydes, amino acids, or a- or ss-amino alcohols. 8. According to the Claim 6, the said composite oxyalkoxides derivates is synthesized by performing the reaction of the composite oxyalko xides with the desirable chelating agent. 9. In the said reaction, according to the Claim 7, the reaction condition comprises a reaction time of 1 to 50 hours at a refluxing temperature of the non-polar organic solvent.

Inventors: ASAI, MAKOTO, IWAMORI,MASANORI, KATO, IWAO, NAKAMURA, YOSHIHIKO, OZAWA, KAZUO, YOSHIMOTO, TETSUO
Applicants: NIPPON SODA CO., LTD.
Application year: 1982
Main classification: C07F7
IPC codes: C07F7