RADIATION PROCESSING OF POLYMERIC PRODUCTS

Abstract: A method of radiation processing a product made at least in part from an oxygen sensitive cross-linkable polymeric material, especially PVC covered wire. The pro­ duct is sealed in a flexible container, which may be simply a heavy gauge polyethylene film bag, and is subjected to gamma radiation in the container. The volume and permea­ bility of the flexible container are such that the ratio of the sum of the volume of oxygen contained in it and the volume of oxygen that will diffuse into it during the irradiation period to the exposed surface area of the polymeric material is less than a critical value which can be determined empirically for each particular polymeric material. For PVC coated wires, the critical value is normally in the range 50 to 150cm³ per m².

Description: RADIATION PROCESSING OF POLYMERIC PRODUCTS This invention relates to the radiationprocessing of products made wholly or in part from polymeric materials, an important application being the processing of insulated wires and cables. It has long been known that many polymeric materials can be cross-linked, and certain physical properties, notably at high temperatures, thereby improved, by exposure to ionizing radiations. It is also well-known that unless the irradiation dose rate is high the cross-linking reaction may be inhibited by oxygen, and this effect has discouraged the use of the technique when electron-beam irradiation facilities have not been available. When gamma-processing (which, with practicable sources, takes around half a day rather than the second or so for electron-beam irradiation) has been used for this purpose, it has been the practice to use gas-tight containers filled with nitrogen to ensure that irradiation took place under substantially oxygen-free conditions. This has numerous disadvantages, including (1) that the expensive containers, which must fit both the products to be contained and the irradiation facility in which they are to be processed, are of limited application and liable to stand idle for long periods; (2) that the containers, and unfillable spaces in them, represent wasted space in the irradiation facility and so wasted radiation flux; (3) that the containers themselves absorb radiation; (4) that seals are liable to leak, especially after many passes through the irradiation plant, leading to the need for regular monitoring to ensure effectiveness of the precautions; and (5) that the containers add to the weights to be handled. We have discovered that equivalent results can be obtained with much simpler and cheaper precautions. In accordance with the invention, a method of radiation-processing a product made at least in part from an oxygen-sensitive cross-linkable polymeric material comprises sealing the product in a flexible container and subjecting it to gamma irradiation therein, the volume and permeability of the flexible container being such that the ratio of the sum of the volume of oxygen contained in it and the volume of oxygen that will diffuse into it during the irradiation period to the exposed surface area of the polymeric material is less than a critical value to be determined empirically for the particular polymeric material. In principle the critical value of the ratio depends upon the formulation of the polymeric material and the irradiation dose and length of the irradiation time, but as the dose rate in gamma-irradiation plant is relatively constant at about 0.5 Mrad /hr and total dose required is largely determined by the material, formulation is ordinarily the only significant factor. For PVC-coated wires with conventional radiation sensitisers the critical ratio can be expected to be in the range 50 to 150 cm3 per m2 of exposed PVC surface, depending on the grade (softer grades demanding a lower value). Preferably the ratio is less than half the critical value, to allow an adequate margin of safety. Provided these limits are observed, substantially identical results can be obtained compared with the use of a pure nitrogen atmosphere. For coils of PVC-coated wires, and other PVC products of comparable compactness and surface-to-volume ratio, if the flexible containers are of reasonably low permeability (for example polyethylene bags of 500 gauge) it will often be sufficient to fill the bags in ambient air, avoiding unnecessary air space, and close by heat sealing or adhesive tape. When this is insufficient to satisfy the oxygen ratio requirement, a more impermeable material may be used for the flexible containers; examples include laminates of PVC with either polyvinyl fluoride or polyvinylidene fluoride, and laminates of polyethylene or of ethylenevinyl acetate copolymer with aluminium foil. Alternatively, or in addition, the volume of contained oxygen can be reduced by: (1) filling unavoidable spaces with inert fillers, preferably hollow to minimise radiation absorbtion -- inflated "balloons" of polyethylene film are ideal; (2) reducing the volume of the flexible container by shrinking it onto the product, as by applying a small degree of suction to the interior (a high degree of suction is undesirable as encouraging leakage) or by using a heat-shrinkable film to form the container, or (3) reducing the proportion of oxygen inside the container by injecting nitrogen or other inert gas (unless impermeability is very high, this should be done only shortly before irradiation commences). In the case of materials that evolve gas (usually hydrogen) during irradiation, venting may be necessary; in some cases a pinhole may be adequate. It will be apparent that the flexible container may need to be protected fron abrasion before and possibly during irradiation; lightweight cartons or stout paper bags (either of which may form part of the final packaging in some cases) can be used for this purpose. Example: Five spools, each holding 400 m of twisted pair of PVC insulated wires, were sealed in a polyethylene bag formed from 500 gauge low-density polyethylene "lay flat" tubing 305 mm wide and 480 mm long. One end of the tube was first sealed, the five spools were then inserted and the other end of the tube heat sealed. From the dimensions of the package the internal volume was calculated to be 12200 cm . The dimensions of the wire were: conductor diameter 0.5 mm; radial insulation 0.3 mm; overall diameter 1.1 mm, volume 0.95 cm3/m, surface area 34.6 cm2/m; and the insulation was a conventional hard grade of irradiation cross-linkable PVC compound made from a vinyl chloride homopolymer of high molecular weight (K-value 70) produced by the suspension polymerisation process, a monomeric phthalate ester plasticiser, a polyfunctional methacrylate monomer acting as a crosslinking promoter, and a lead-based stabiliser. The volume of the material in each spool was approximately 140cm3, the volume of wire on each spool 760 cm3, and the total surface area of wire per spool 2 was 2.76 m The total volume of wire and spool substance within the bag was therefore 4500 cm# and consequently the volume of air entrapped within the bag was 12200 - 4500 = 7700 cm3. . Thus the oxygen content of the bag was approximately 1540 cm3. The total surface area of the wires within the bag was 13.8 m2 approximately and consequently the available oxygen to surface area ratio (AOR) was 32 1540/13.8 = 110 cm The bag was placed in a cardboard carton, to protect it from possible damage during handling, and was subjected to gamma radiation to receive a dose of 5 Mrad, equal to that normally given this product when processed in nitrogen filled metal containers. For control purposes five additional spools of wire were placed in a similarly constructed bag, which was not sealed at one end, and were irradiated under identical conditions. Subsequently about 30 samples of wire were taken from the spools in each bag and then were subjected to scrape abrasion tests and to a solvent extraction test. The results are shown in the table and are compared with the results obtained on identical wire processed to the same dose in nitrogen filled metal containers. TABLE EMI6.1 <tb> <SEP> SAMPLE <SEP> TEST <tb> <SEP> Scrape <SEP> Abrasion <SEP> Toluene <SEP> Extraction <tb> <SEP> Strokes <SEP> to <SEP> Failure <SEP> % <SEP> <SEP> Weight <SEP> Loss <tb> Nitrogen <SEP> control <SEP> 270 <SEP> 1 <SEP> <SEP> 21.5 <tb> Sealed <SEP> bag <SEP> 280 <SEP> 1 <SEP> <SEP> 20.6 <tb> Unsealed <SEP> bag <SEP> 227 <SEP> 25.7 <tb> Toluene extraction was estimated using a standard Soxhlet extraction apparatus using about 1 g. of 50 mm lengths of stripped insulation, refluxed in toluene for 20 hours, following by drying in vacuo for two hours at 1000C. Wires from the unsealed bag showed a significantly lower scrape abrasion resistance and increase in extractables both results indicating a significant reduction in crosslinking of the insulation. The differences in the corresponding values obtained on the nitrogen controls and the sealed bag wires are within the normal experimental spread for this type of insulation and for practical purposes these wires would be considered to have identical properties.

Claims: CLAIMS 1. A method of radiation processing a product made at least in part from an oxygen sensitive crosslinkable polymeric material comprising sealing the product in a flexible container and subjecting it to gamma irradiation therein, the volume and permeability of the flexible container being such that the ratio of the sum of the volume of oxygen contained in it and the volume of oxygen that would diffuse into it during the irradiation period to the exposed surface area of the polymeric material is less than a critical value determined empirically for the particular polymeric material. 2. A method of radiation processing PVC coated wire comprising sealing it in a flexible container and subjecting it to gamma irradiation therein, the volume and permeability of the flexible container being such that the ratio of the sum of the volume of oxygen contained in it and the volume of oxygen that would diffuse into it during the irradiation period and the exposed surface area of the PVC coating is less than 150 cm3 per m2. 3. A method as claimed in Claim 2 in which the ratio referred to is less than 50cm per 2 ratio referred to is less than 50cm per m 4. Cross-linked PVC coated wire resulting from the process claimed in any one of Claim 2 or Claim 3. 5. An irradiated product made by the process claimed in Claim 1.

Inventors: BATES, PHILIP ARTHUR, WILLS, GRAHAM BOYCE
Applicants: BICC PUBLIC LIMITED COMPANY
Application year: 1982
Main classification: B29C71
IPC codes: H01B3, B29C71, B29C35