PREPARING P-PHENOXY-BENZOYL COMPOUNDS

Abstract: Substantially pure p-phenoxybenzoyl compounds are prepared by reacting diphenyl ether and an appropriate acyl compound in the presence of hydrogen fluoride. The result­ ing p-phenoxyaryl alkyl ketone can be converted into p-phenoxybenzoic acid or salts thereof, p-phenoxybenzoyl halide or lower alkyl p-phenoxybenzoate for use in preparing homo- and copolymers containing a p-phenyxobenzoyl repeating unit.

Description: DESCRIPTION Preparing p-phenoxy-benzoyl compounds This invention relates to the preparation of p-phenoxybenzoyl compounds. U.S. Patent No. 3,953,400 to K.J. Dahl, 27 April 1976, teaches the preparation of poly(arylene ether ketones) by polymerizing a p-phenoxybenzoyl moiety-containing monomer in the presence of a hydrogen fluoride-boron trifluoride catalyst and a capping agent. The monomer can be, for example, a p-phenoxybenzoyl halide, p-phenoxybenzoic acid or C1-C3 alkyl p-phenoxybenzoates. The polymer produced by the process described in U.S. Patent No. 3,953,400 contains the p-phenoxybenzoyl repeating unit having the structure EMI1.1 The polymer has a tensile elongation to break of at least about 50% at room temperature and a mean inherent viscosity within the range from about 0.8 to about 1.65. It has been found that in order to obtain a satisfactory polymer product using the process described in the Dahl patent, substantially pure p-phenoxybenzoyl monomer must be used. The presence of even small amounts of impurities interferes with the polymerization process. The present invention provides a method for the preparation of p-phenoxybenzoyl compounds of the formula EMI2.1 wherein R is lower alkyl, which comprises reacting diphenyl ether with an acyl compound of the formula EMI2.2 wherein R is lower alkyl and R is selected from the group consisting of halogen, hydroxyl, -OR EMI2.3 where Rê and R are each lower alkyl, in the presence of hydrogen fluoride. The resulting p-phenoxyphenyl alkyl ketone can be converted to the corresponding acid, acid salt, acid halide or lower alkyl p-phenoxybenzoate, that is, compounds of the formula EMI2.4 wherein X is halogen, hydroxyl, lower alkoxy or -OM where M is a metal ion, by known methods. Substantially pure p-phenoxybenzoyl compounds are obtained by this Friedel-Crafts acylation and these compounds are useful as monomers for preparing polymers containing a p-phenoxybenzoyl repeating unit. In the above definitions, the term "lower alkyl" refers to alkyl radicals containing 1 to 4 carbon atoms, i.e. methyl; ethyl, propyl, and butyl. The term "lower alkoxy" refers to include alkoxy radicals containing from 1 to 4 carbon atoms, i.e., methoxy, ehtoxy, propoxy and butoxy. Halogen refers to fluroine, chlorine, bromine and iodine. The metal ion, M, can be any metal. ion but is preferably sodium, potassium or calcium. The acyl compound reacted with diphenyl ether can be, for example, acetic acid, acetic anhydride, acetyl chloride, acetyl fluoride, methyl, ethyl, propyl or butyl acetate, propionic acid, anhydride, acid halide, or ester or butyric acid, anhydride, acid halide or ester. Other compounds which would form the acid in situ in the reaction medium, for example sodium acetate, can also be used and such compounds are considered to be included in the acyl compound. The reaction of diphenyl ether with the acyl compound is carried out in the presence of hydrogen fluoride. The amount of hydrogen fluoride present is preferably at least about 30 percent by weight, based on the total weight of the reactants. Preferably, hydrogen fluoride is present in an amount of about 50 percent to about 100 percent by weight based on the weight of the reactants. Additional hydrogen fluoride can be used if desired, but no advantage is derived from doing so. In general, the amount of hydrogen fluoride used should be in substantial molar excess of the total molar quantity of basic species present in the system. If less than 30 percent hydrogen fluoride is used, the reaction will not proceed to completion and relatively low yields of ketone will be obtained. Conducting the reaction at higher temperatures may result in driving the reaction to completion under such conditions. An inert diluent can be present if desired. Suitable inert diluents are, for example, normal alkanes containing 3 to 10 carbon atoms and geminal polychloro-, polyfluoroand poly(fluorochloro)-n-alkanes containing 1 to 10 carbon atoms, sulphur dioxide, sulpholane, and the like. In general, the reaction is preferably conducted at temperatures in the range of from about -20 to about +700C, preferably from about -20 to about +400C and most preferably from about -10 to about +300C. The reaction is preferably carried out under atmospheric pressure or the normal vapor pressure of hydrogen fluoride. Greater or less pressure can be applied, if desired. The reaction of diphenyl ether with the acyl compound in the presence of hydrogen fluoride produces very high yield of mono-acylated para-isomer. Unlike similar reactions using traditional Friedel-Crafts catalysts, such as aluminum trichloride, there is little, if any tendency for diacylation to occur. Further, there is minimal, if any, other impurities in the reaction product The high yield and high purity of the ketone produced makes it particularly suited for use in preparing monomers for formation of poly(arylene ether ketones). As discussed above, the p-phenoxyphenyl alkyl ketone can be converted by known procedures to the corresponding acid, acid salt, acid halide or ester (for example, lower alkyl p-phenoxybenzoate), and the resulting substantially pure, p-phenoxybenzoyl compounds can be used as monomers in the preparation of poly(arylene ether ketones). For example, p-phenoxyacetophenone can be oxidized by reaction with sodium or potassium hypochlorite to give the sodium or potassium salt of p-phenoxybenzoic acid which can then be acidified, e.g., by addition of hydrochloric acid, to yield p-phenoxybenzoic acid. Others methods that can be used to effect oxidation of p-phenoxy-acetophenone include air oxidation in the presence of a catalyst such as cobalt (II) acetate bromide together with manganese (II) acetate, or manganese acetate and manganese dioxide or oxidation in the presence of an oxidizing agent such as potassium permanganate or with sodium dichromate in acid solution. The acid or its salts can be readily converted into the acid chloride by reaction with thionyl chloride or phosgene in the presence of N,N-dimethyl formamide catalyst. The corresponding esters can be prepared by reacting the acid or acid salt with an alcohol in the presence of an acid catalyst. The p-phenoxybenzoyl compounds prepared in accordance with this invention can be polymerized to yield polymers having the repeating unit EMI5.1 using known polymerization procedures. Preferred methods of producing such polymers are disclosed in U.S. Patents Nos. 3,953,400, 4,229,564, 4,239,884 and 4,247,682, the disclosures of which are hereby incorporated by reference. As discussed in these patents, homopolymers and copolymers of p-phenoxybenzoyl containing monomers can be prepared. In the preparation of copolymers, a wide variety of monomers can be employed. Suitable comonomers include, for. example, p-(phenylthio)benzoyl chloride, m-phenoxybenzoyl chloride, 2-dibenzofurancarbonyl chloride,. 2-thianthrenecarbonyl chloride, 2-phenoxathiincarbonyl chloride, 2-phenodioxincarbonyl chloride, 2-dibenzothiophenecarbonyl chloride, 4(4'-biphenyloxy)benzoyl chloride, 4-(1' naphthoxy)benzoyl cloride, 4-(2' naphthoxy)benzoyl fluoride, terphenyl carbonyl chloride, quaterphenyl carbonyl fluoride and the like. In the following examples, p-phenoxyacetophenone is produced by reacting diphenyl ether with an acetylation agent, specifically, acetic anhydride, acetyl chloride or acetic acid. In Examples 1-8, the reaction is conducted in the presence of hydrogen fluoride in accordance with this invention. In each case, the product is analyzed for the presence of a diacylation product and impurities and the yield determined. Example 9 is a comparative example in which p-phenoxyacetephenone is produced by reacting diphenyl either with acetic anhydride in the presence of aluminum trichloride, a traditional Friedel-Crafts catalyst. In example 10, p-phenoxyacetephenone produced in accordance with this invention is oxidized to yield p-phenoxybenzoic acid suitable for use as a monomer. Example 1 To a frozen solution of 1.70 g. (0.010 mole) diphenyl ether in 1.30 g. (0.012 mole; a 20 mole % excess) acetic anhydride, was added 3.0 ml anhydrous hydrogen fluoride (50% by weight of reactants). A magnetic stirrer was added and the reaction mixture was stirred magnetically and degassed several times while warming to 240 C in air, and stirred for 18 hours at 240 C. The resultant red solution was poured into a plastic beaker and allowed to evaporate in an air stream/24" C, leaving a crystalline residue. This was crushed in about 30 ml ice water, collected by filtration, partly air dried and further dried at 40 C under a vacuum for about 2 hours, yielding 2.0 g. (94.2%) of nearly colorless crystals with a yellow tinge. Analysis showed only 0.73% unreacted diphenyl ether or 99.25% yield of p-phenoxyacetophenone by gas-liquid chromatography GLC. Thin layer chromatography (TLC) showed a very weak fast moving impurity spot corresponding to diphenyl ether while no trace of a slower moving spot which would correspond to a diacylation product was observed. The product had a melting point of 47-50 C. Examples 2-8 The procedure decribed in Example 1 was repeated using diphenyl ether in the amounts specified in the following Table with an acetylation agent, namely acetic anhydride, acetic acid or acetyl chloride as identified in the Table and in the amount specified. The reaction was conducted in the presence of hydrogen fluoride in the amounts specified in the Table. In Examples 3, 5, 6, 7 and 8, the reaction was conducted at 240C for about 24 hours. In Example 2, the temperature of the reaction ranged from -10 C to +100C and the reaction took place over 39 hours. In Example 4, the reaction was conducted at 240C for 66 hours. In each example the product was analyzed by gas-liquid chromatography and the yield determined by calculation on a weight -percent basis and by gas-liquid chromatography. The results are reported in the Table. Each product was also analyzed for the presence of diacylation product by thin-layer chromatography. In each case no evidence of diacylation product was observed. A fast moving spot indicating unreacted diphenyl ether was observed in each case. -As indicated in the Table, Example 8 resulted in incomplete reaction. This is believed to be due to the relatively low amount of hydrogen fluoride used (32.5% by weight based on the weight of the reactants). Example 9 This is a comparative example in which p-phenoxyacetophenone is prepared by reaction of diphenyl ether and acetic anhydride in the presence of a traditional Friedel Crafts Catalyst, aluminum trichloride. To-a cooled (2-10"C), stirred solution of 17.02 g. (0.100 mole) diphenyl ether, 10.21 g. (0100 mole) acetic anhydride and 50 ml methylene dichloride was gradually added 29.87 g. (o. 224 mole) anhydrous aluminum trichloride under a nitrogen atmosphere over a half hour period. The reaction mixture was heated at 430C (reflux) for an hour, then allowed to cool to room temperature (24"C) and then poured on stirred ice. The resulting yellow oil was extracted with methylene dichloride, dried over anhydrous magnesium sulphate, filtered and the solvent removed by evaporation at 240C. The resulting orange syrup was dried at 800C under a reduced pressure of 0.1 mm mercury to yield 19.66 g. (93%) orange melt that crystallized on -cooling. The product had a melting point of 0-450C. The product was analyzed by gas-liquid chromatography and the results are reported in the Table. Thin-layer chromatography resulted in two slow moving impurity spots indicating formation of a diacylation product. TABLE Catalyst Gas-Liquid Chromatography (GLC) Acetyl Acetic Acetic Diphenyl AlCl3 Yield Chloride Anhydride Acid Ether HF +CH2Cl2 Diphenyl Diacryl- % Example g g g g ml g Ether ation Impurities by by No. (Moles) (Moles) (Moles) (Moles) (Wt %) (mol.) (%) (%) (%) wt. GLC 1 - 1.30 - 1.70 3.0 - 0.70 0 0.017 94.2 99.3 (0.012) (0.010) (50) 2 - 929.2 - 1549.0 3400 - 11.0 0 0.04 96 89 (9.10) (9.10) (57.8) 3 - - 1.44 3.40 10 - 26.8 0 0.03 - 73 (0.024) (0.02) (67) 4 - 1.44 3.40 10 - 13.8 0 0.107 80 86 (0.024) (0.02) (67) 5 7.94 - - 17.02 33 - 0.80 0 0.01 96.0 99.2 (0.101) (0.10) (57) 6 1.21 - - 2.17 3.0 - 0.99 0 0.02 84.5 98.9 (0.0154) (0.0128) (47) 7 1.41 - - 2.55 1.7 - 27.5 0 0.038 - 72.5 (0.018) (0.015) (30) 8 7.94 - - 17.09 12 - * * * * * (0.101) (0.10) (32.5) 9 - 10.21 - 17.02 - 29.87 1.76 0.80 0.23 93 97.4 (0.10) (0.10) (0.224) *Incomplete reaction-yield estimated to be 70% bythin-layer chromatography Example 10 In this example, p-phenoxyacetephenone produced in accordance with Example 2 in the presence of hydrogen fluoride and p-phenoxyacetephenone produced in accordance with Example 9 in the presence of aluminum trichloride were each converted into benzoic acid. In each case a 5.25% sodium hypochlorite solution (85.1 g.: 0.060 mole) was added slowly in portions to a solution of 3.18 g. (0.0150 mole) of the p-phenoxyacetophenone sample while heating from 40 to 1000C. The resulting solution was concentrated at 1000C, producing a crystalline precipitate. Acetone was then added to consume excess sodium hypochlorite followed by boiling, acidification with some excess concentrated hydrochloric acid (10 ml of 12N), stirring, filtration, water wash and then drying at 700C/under vacuum for about 1 hr. The p-phenoxybenzoic acid obtained from the p-phenoxyacetephenone produced in the presence of hydrogen fluoride was white with a melting point of 159-162 C. In contrast, the p-phenoxybenzoic acid produced in the presence of aluminum trichloride had a yellow (or light beige) discolouration and a strongly depressed melting point of 137-7490C, indicating the presence of considerable impurities.

Claims: CLAIMS 1. A method of preparing p-phenoxybenzoyl compounds of the formula EMI11.1 wherein R is lower alkyl, which comprises reacting diphenyl ether with an acyl compound of the formula EMI11.2 wherein R is lower alkyl and R1 is selected from the group consisting of halogen, hydroxyl, EMI11.3 where R2 and R3 are each lower alkyl, in the presence of hydrogen fluoride. 2. A method according to Claim 1, wherein the acyl compound is selected from acetyl chloride, acetic acid and acetic anhydride. 3. A method in accordance with Claim 1 or 2, wherein hydrogen fluoride is present in an amount of at least 30 percent by weight based on the total weight of the diphenyl ether and acyl compound. 4. A method in accordance with Claim 3, wherein said hydrogen fluoride is present in an amount of at least 50% by weight based on the total weight of the diphenyl ether and acyl compound. 5. A method in accordance with any preceding claim, wherein said reaction is conducted at a temperature in the range of from about -20 to about +700C. 6. A method in accordance with Claim 5, wherein said reaction is conducted at a temperature in the range of from about -10 to about +300C. 7. A method according to any of the preceding claims, comprising the further step of oxidizing the compound of formula (I) to yield substantially pure p-phenoxybenzoic acid. 8. A substantially pure p-phenoxybenzoyl compound of the formula EMI12.1 wherein R is alkyl, prepared by a method according to any one of Claims 1 to 6. 9. Substantially pure p-phenoxybenzoyl acid prepared by a method according to Claim 7.

Inventors: JANSONS, VIKTORS
Applicants: RAYCHEM CORPORATION
Application year: 1982
Main classification: C07C49
IPC codes: C07C49, C07C51, C07C45