WATER-BASED HYDRAULIC FLUIDS INCORPORATING A POLYETHER AS A LUBRICANT AND CORROSION INHIBITOR

Abstract: In accordance with the instant invention, a water-based hydraulic fluid, having improved lubricity, anti-wear and corrosion inhibition properties can be obtained by blending a heteric or block polyoxyalkylene copolymer nonionic sur­ face-active agent with a conventional water-based hydraulic fluid composition. These heteric or block polyoxyalkylene copolymers are the reaction product of a linear or branched active hydrogen containing compound having from 1 to 6 carbon atoms with alkylene oxides having from 3 to 6 carbon atoms and an oxygen/carbon atom ratio of less than 0.4. Alternatively but advantageously, said copolymers may also be reacted with alkylene oxide having an oxygen/carbon atom ratio of greater than 0.4.

Description: Water-based hydraulic fluids incorporating a polyether as a lubricant and corrosion inhibitor This invention relates to water-based hydraulic fluids characterized by improved lubricity, anti-wear and corrosion inhibition properties. In the technology of hydraulic power transmission, mechanical power is imparted to a fluid called "a hydraulic fluid" in the form of pressure by means of a hydraulic pump. Power is utilized where desired by tapping a source of said hydraulic fluid thus transforming the power as pressure back to mechanical motion by a mechanism called a hydraulic motor. The hydraulic fluid is utilized as a pressure and volume transmitting medium. Any non-compressible fluid can perlform this function. Water is the goldes. fluid used for this purpose and is still sometimes used alone for this purpose. In the prior art, there has been a heavy emphasis on the deveiopment of petroleum oils for use as hydraulic fluids and, conseauently, much of the ecuinmen utilized with hydraulic fluids has been designed and manufactured specifically for use with petroleum ojis. A petroleum oil in comparison with water as a hydraulic fluid possesses the advantage of inhibiting the development of rust of the ferrous components of the mechanical esuipment utilized In conjunction with hydraulic fluids, (i.e., hydraulic pumpt zumotors, etc.) and in preventing wear of the machinery since the hydraulic fluid must lubricate the equipment. Petroleum oils have a second advantage over the use of water as a hydraulic fluid in that the petroleum oils normally exhibit a substantially higher viscosity than water and thus contribute to redüction of the leakage of the fluid in the mechanical equipment utilized. In addition, the technology relating to additives for petroleum oils has developed to such an extent that the viscosity, foam stability, wear prevention and corrosion prevention properties 9f such petroleum oil-basea hydraulic fluids can be further enhanced by the use of said additives. Over the past 25 years, various substitutes for petroleum oil-based hydraulic fluids have been developed in oraler to overcome one of the major deficiencies of petroleum oils, namely, flammability. Recent interest in the use of hydraulic fluids having up to 99 percent or more of water has resulted from the higher cost of petroleum oils and rectent emphasis on problems of ecologically suitable aispos21 of contaminated or spent petroleum oil-based hydraulic fluids. Metaiworking fluids of the so-called "soluble oil" type have been considered for use as hydraulic fluids. Such fluids contain mineral oil and emulsifiers as well as various additives to increase corrosion resistance and improve antiwear and defoaming properties. Such fluids, when used as hydraulic fluids, are not generally suitable for use in ordinary industrial equipment designer speci fically for use with the petroleum oil-based hydraulic fluids since such fluids do not adequately prevent wear damage in pumps and valves of such equipment. However, such fluids have found application in specially designed, high cost, large size equipment which, because of said large size and thus inflexibility, is not suitable for use in most industrial plants. The soluble oil hydraulic fluid usage has thus been quite limited; usage has been largely confined to large installations where flexibility and size are not critical, such as in steel mills. It is also known to use, in equipment designed for use in mineral oil-based hydraulic fluids, flame-resistant glycol-water-based hydraulic fluids such as are disclosed Ir U.S. Patent No. 2,947,699. Up until now, water-based hydraulic fluids containing about 70 to 95 percent water, have had very pcor lubricating characteristics. While hydraulic fluids are used primarily to transmit forces, it is necessary that they provide lubrication for the impeller, rings,# vanes, gears, pistons and cylinders and other mechanicol parts of hydraulic pumpt in such systems in or-er to prevent excessive wear on such parts. Many prior art fluids, such as the petroleum oil type, are highly fiammable and unsuitable for certain uses where such fluids have frequently been the source of rire. Where these fluids are used to control such industrial operations as heavy casting machines, which are operated largely by hydraulic means, danger of fire exists. There fore, there is a growing demand for hydraulic fluids characterized by reduced flammability. Hydraulic fluid compositions having water as a base are disclosed in U.S. Patents Nos. 4,151,099 and 4,138,346. These patents disclose fluids comprising. 1) a sulfur containing compound and 2) a phosphate ester salt. The U S. 4,151,099 patent also incluces a water-soluble polyoxyethylated ester of an aliphatic acid and a monohydric or polyhydric aliphatic alcohol, either one or both said acid and said alcohol being polyoxyethylated. In U.S. Patent No. 3,890,238, polyoxyalkylene polymers ¯are disclosed as useful in surfactant application problems, cutting and grinding fluids, corrosion inhibitor, lubricants and/or defoamers in aqueous systems such as cooling systems. An example of such a polymer disclosed in the patent is one having a total molecular weicht of asoroximately 2000 and prepared by adding ethylene oxide to bothtends of a polypropoxy propylene glycol base having the molecuar weight of approximately 1750. U.S. Patent No. 4,210,549 discloses an aqueous composition, wherein corrosion is inhibited, which incorporates in the composition the polymer described above for U.S. 3,890,238. However, the patent relates to an antifreeze composition rather than a hydraulic fluid and employs a water-soluble metal silicate for corrosion inhibition, and as an organic basic pH buffer and corrosion inhibitor a hydroxybenzoic acid. U.S. Patent No. 3,205,172 discloses a universal machining fluid which is an aqueous fluid that contains surface-active polypxypropylene-polyoxyethylene block polymer. However, the solution is one which incorporates a diacetyl triglyceride and employ5 the block polymer as an emulsifier therefor. It has been discovered in accordance with the instant invention that the addition of small but effective amounts of polyoxyalkylene copolymers, as specified below, to otherwise conventional water-based hydraulic fluids results in improved lubricity, antiwear and corrosion inhibiting properties. In accordance wHt the instant invention, a waterbased hydraulic fluid, having improved lubricity, znti-we2r and corrosion inhibition properties can be obtained by blending a heteric or block polyoxyalkylene copolymer nonionic surzace-active agent with a conventional water based hydraulic fluid composition. These heteric or block polyoxyalkylene copolymers are the reaction product of a linear or branched active hydrogen containing compound having from 1 to 6 carbon atoms with alkylene oxides ovi from 3 to 6 carbon atoms and an oxygen/carbon atom ratio or lessr than 0.4. Alternatively but advantageously, said copolymers may also be reacted with alkylene oxide having an oxygen/carbon atom ratio of oreater than 0.4. Suitable active hydrogen containing compounds include propylene glycol, ethylene glycol, diethylene glycol, glycerine, pentaerythritol, trimethylolpropane, ethylene diamine and the like. Suitable alkylene oxides having an oxygen/carbon atom ratio less than 0.4 are propylene oxide, butyiene oxide, and amylene oxide. Suitable alkylene oxides having an oxygen/carbon atom ratio grreater than 0.4 are ethylene oxide, butadiene dioxide and glycidol. The polyoxyalkylene block copolymers employed are co-generic mixtures of conjugated polyoxyalkylene compounds containing in their structure the residue of an active hydrogen containing compound having from 1 to 6 carbon atoms and at least one hydrophobic oxyalkylene chain in which the oxygen/carbon atom ratio does not exceed 0.4. Alternatively, but advantageously, the copolymer may also inclae at least one hydrophilic oxyalkylene chain in which the oxygen/carbon atom ratio is greater than 0.4. Sclymers of oxyalkylene groups obtained from propylene oxide, butylene oxide, amylene oxide rnixtures of such oxyalkylene groups witach other and with ininor amounts of oxyalkylene groups obtained from ethylene oxide butadiene dioxlse, and glycidol are illustrative of hydrophobic oxyalkylene chains having an oxygen/carbon atom ratio not exceeding 0.4. Polymers of oxyalkylene groups obtained from ethylene oxide, butadiene dioxide, glycol, mixtures of such oxyalkylene groups with each other and with minor amounts of oxyalkylene groups obtained from propylene oxide, butylene oxide and amylene oxide are illustrative of hydrophilic oxyalkylene chains having an oxygen/carbon atom ratio greater than 0.4. The above polyoxyalkylene copolymers have a molecular weight of the 3 to 6 carbon atom oxyalkylene groups from about 950 to 3500 and contain from about 65 to 100 weight percent of the 3 to 6 carbon atom oxyalkylene groups. Among the conjugated polyoxyalkylene compounds which can be used in the compositions of the invention are those which correspond to the formula: y organic compound having from about 1 to 6 carbon atoms and containing x reactive hydrogen atoms In which x has a value of at least one, n has a value such that the oxypropylene content of the molecule is from about 65 to 100 weight percent and the total molecular weight of the polyoxypropylene groups is from about 950 t 3500. Compositions of this type are more particularly described in U.S. Patents Nos. 2,674,619 and 2,677,700. Other suitable nonionic block copolymers correspond to the formula: Y[(C2H4O)m(C3H6O)nH]x wherein Y, n, m and x have values as set forth above. Compositions of this type are more particularly described in U.S. Patent No. 3,036,118. In either of the above formulas, compounds falling within the scope of the definition for Y include, for example, propylene glycol, ethylene glycol, dipropylene glycol, diethylene glycol, glycerine, pentaerythritol, trimethylolpropane, ethylene diamine and the like. Also, the oxypropylene chains optionally, but advantageously, contain small amounts of ethylene oxide and the oxyethylene chains also optionally, but advantageously, contain small amounts of propylene oxide. Preferred compounds of the above type are those wherein v is the residue of propylene glycol or ethylene glycol and x is 2. The concentration of the polyoxyalkylene copolymer in the hydraulic fluid of the invention is at least about 0.05 percent by weight. There is no known maximum amount, the maximum being determined by economics, i.e., cost of the copolymer. The beneficial effects of the addition level off at'about 0.4 percent by weight. It is not believed that any one would want to use more than about 2.0 percent by weight of the copolymer. The polyoxyalkylene copolymers described above may be employed with any conventional high-water hydraulic fluid incorporating any or all of the following prior art components. For example, the hydraulic fluid may contain, as disclosed in U.S. Patents Nos. 4,151,099 and 4,138,346, a phosphate ester, a sulfur compound, and a water-soluble polyoxyethylated aliphatic ester or ether. Optionally, the fluids of the invention can include an additional corrosion inhibitor, a defoamer and a metal deactivator (chelating agent) as well as other conventional additives, such as dyes in normal amounts. In accordance with this invention, it has been discovered that compositions useful as hydraulic fluids can be prepared having desirable lubricity, antiwear and corrosion inhibiting properties. Generally, concentrates oz the hydraulic fluids of the invention are shipped to the point of use where they are diluted with tap water. The compositions of the invention provide improved reslrs over prior art fluids even when diluted with hard water. Water-soluble esters of ethoxylated aliphatic acids anchor water soluble ethers of ethoxylated alcohols may be incorporated in the hydraulic fluid as an addi-#onal anti-wear .lubricant component. Preferred water-soluble esters or ethers are those of the ethoxylated C8 C36 aliphatic monohydric or polyhdyric alcohols or aliphatic acids, and aliphatic dimer acids. Suitable esters of ethoxylated aliphatic acids or alcohols are disclosed in U.S. Patent 4,151,099 particularly beginning in cofun 3 thereof which is hereby incorporated by reference. Representative water-soluble polyoxyethylated esters having about 5 to about 20 moles of oxide per mole are the polyoxyethylene derivatives of the follcwing esters; sorbitan monooleate, sorbitan trioleate, sorbitan mono stearate, sorbitan tristearate, sorbitan monopalmitate, sorbitan monoisostearate, and sorbitan monolaurate. Conventional sulfur compound additives may also be incorporated in the hydraulic fluid such as the ammonia, amine or metal salts of 2-mercaptobenzothiazole or 5-, 6and 7-substituted 2-mercaptoben:othiazole, said salts being formed on neutralization of the free acid form of 2-mercaptobenzothiazole with a base. Such sulfur compounds are d scloseà particuiarly beginning in column 5 of tj.S. Patent 4,138,346 which is hereby incorporated by reference. The sulfur-containing compound may * also be sulfurized oxymolybdenum, and oxyantimony compounds represented by: EMI10.1 wherein, M is molybdenum or antimony and R is organic and is selected from the group consisting of C3-C20 alkyl, aryl, alkylaryl radicals and mixtures thereof. Representataive useful molyDdenum and antimony compounds are sulrurized oxymolybdenum or oxyantimony organo-phosphorodithioate where the organic portion is alkyl, aryl or alkylaryl and wherein said alkyl has a chain length of 3 to 20 carbon atoms. The compositions of the invention may also contain a phosphate ester selected from the group consisting of EMI11.1 and mixtures thereof wherein ethylene oxide groups are represented by EO; R is selected from the group consisting of linear or branchea chain alkyl groups wherein said alkyl groups have about 6 to 30 carbon atoms, preferably about 8 to 20 carbon atoms, or alkylaryl groups wherein the alkyl groups have about 6 to 30 carbon atoms, preferably about 8 to 18 carbon atoms, and X preferably is selected from the group consisting of hydrogen, alkali or alkaline earth metal, the residue of ammonia or an amine and mixtures thereof, and n is a number from 1 to 50. Metalls such as lithium, sodium' potassium, rubidium, cesium, calcium, strontium, and barium are examples of the alkali or aikaline earth metal. The free acid form of the phosphate ester is preferably utilized in preparing hydraulic fluids in accordance with compositions of the invention. These are more fully disclosed in U.S. Patent 3,004,056 and U S. 3,004,057, incorporated herein by reference. The free acid form may be converted to the salt form in situ in the preparation of the hydraulic fluids of the invention. Alternatively, the phosphate ester salts can be used directly. The hydraulic fluid compositions of the invention may also contain an alkyldialkanolamide of the formula EMI12.1 wherein R1 is alkyl of about 4 to about 54, preferably about 4 to about 30, carbon atoms and R2 is alkyl of about 2 to about 6 carbon atoms. The alkyldialkanolamides are known compositions in the prior art. In general, these compositions are prepared sy esterifying a alalsanolamine with an alkyl dicarsoxylic acid and removing water of esterification. Useful alkyl aicarboxylic acids include branchea or straight chain satu#rated or unsaturated aliphatic monocarboxylic or dicarboxylic acids as described below. Preferably, te saturated straight chain acids are used and the preferred amines are diethanolamides. Examples of useful alkyldialkanolamides are the alkyl diethanolamides and alkyl dipropanol amides where the alkyl group is derived from a C8-C54 dicarboxylic acid. The advantageous properties contributed to the hydraulic fluid by the alkyldialkanolamide component of the hydraulic fluid of the invention are resistance to precipi tation in the presence of hard water, that is, in the presence of large amounts of calcium and magnesium ions in the water utilized to prepare the hydraulic fluid of the invention. In addition, the alkyldielkanolamides contribute to the antiwear and extreme pressure performance of the composition as well as to the metal corrosion resistance which is desirable in such fluids. The alkyldialkanolamides in aqueous solution are completely stable under neutral and alkaline conditions and show little tendency to hydrolyse or decompose on storage. The hydraulic fluids and metalworking compositions of the invention generally consist of about 60 percent to about 99 percent water and about 40 percent to about 1 percent of additives. A high water hydraulic fluid will generally contain 95 percent or more of water. These additives -can consist of concentrates comprisihg the polyoxyalkylene compound possibly in combination with the water-soluble esters of ethoxylated aliphatic acid and/or ethoxylated alcohol ethers and/or sulfur containing compound; and/or phosphate ester, ana/or alkyldialkanolamide and, in addition, can contain defoamers, thickeners, additional corrosion inhibitors and metal deactivators or chelating agents. Preferably, said fluids consist of about 75 percent to 99 percent water and about 25 percent to about 1 percent concentrate. The fluids are easily formulated at room temperature using distilled or deionized water although tap water can also be used without adverse effects on the fluid properties. The amount of polyoxyalkylene block copolymer in the concentrate is preferably from about 5.0 to 40 percent by weight of the concentrate. The amount of sulfur-containing compound in the hydraulic fluid concentrate of the invention is generally about 0 to 10 percent by weight and when employed is at a minimum of 1.0 percent. The concentration of the phosphate ester in the hydraulic fluid Concentrate of the invention is generally about 1.0 to 7.0 percent by weight of the concentraten The concentration of the water-soluble ester of the ethoxylated aliphatic acid and/or ethoxylated alcohol ether in the hydraulic fluid concentrate of the invention is generally about 1.0 percent to about 7.0 percent by weight. Prefe#ably, the proportion by weight of each of these components is 1.0 to 5.0 percent. The percent by weight alkyldialkanolamide in the concentrate is about 1 to 7, preferably about 1 to 5 based upon the total weight of the concentrate. Most preferably1 eaual amounts of the ester of an ethoxylated aliphatic alcohol and the alkyldialkanolamide are used. The thickeners, metal deactivators and additional corrosion inhibitors which can be added einher to the concentrate or to the hydraulic fluid or metalworking compositions of the invention are as follows: The thickener can be of the polyglycol type. Such thickeners are well known in the art and this type of thickener is the preferred thickener. The polyglycol thickeners are polyoxyalkylene polyols prepared by reacting an alkylene oxide with a linear or branched chain polyhydric alcohol. Suitable polyols contain ethylene oxide and propylene oxide and/or higher molecular weight oxides in a mole ratio of between about 100:0 to about 70:30 ethylene oxide-propylene oxide. Such thickeners are commercially available and sold under the trademark "Ucon 75H-90,000" by Union Carbide and Carbon Chemical Corporation. The specifi- cations for this material call for a pour point of 40 e F, a flash point of 485 F, a specific gravity at 200C of approximately 1.1 and a viscosity of about 90,000 S.U.S. at a temperature of 100 ¯F. Other types of thickeners or viscosity inc.easin agents can be used in the hydraulic fluid and metalworking compositions of the inswention such as polyvinyl alcohol, polymerization product of acrylic acid and methacrylic acid, polyvinyl pyrrolidone polyvinyl ether ,naleic anhydride copolymer and sorbitol. These materials are weil known in the art and are utilized in varying proportions depending upon the desired viscosity and the efficiency of the thickening or viscosity increasing effect. Generally about 20 to 60 percent of such thickener in the concentrate will provide the desired viscosity in the final hydraulic fluid. By the use of such thickening agents, it is believed that the hydraulic fluids of the invention can be used in hydraulic pumps and other equipment without significant wear resulting from cavitation effects and use of such thickeners also substantially prevents internal and external leakage in the mechanical parts of the hydraulic system during the pumping of such hydraulic fluids. Liquid-vapor corrosion inhibitors may be employed and can be any of the alkali metal nitrites, nitrates and benzoates. Certain amines are also useful. The inhibitors can be used individually or in combinations. Representative examples of the preferred alkali metal nitrates and benzoates which are useful are Es follows: sodium nitrate, potassium nitrate, calcium nitrate, barium nitrate, lithium nitrate, strontium nitrate, sodium benzoate, potassium benzoate, calcium benzoate, barium benzoate, lithium benzoate and strontium benzoate. Representative amine-type corrosion inhibitors are Es follows: butylamine, propylamine, n-octyl2mine, hexyl- amine, morpholine, N-ethyl morpholine, N-methyl morpholine, aniline, triphenylamine, aminotoluene, ethylene diamine, dimelhylaminopropylamine, N,N-dimethyl ethanolamwne, tr#ethanolamine, diethanolamine, monoethanolamine, 2-met.hyl pyr# > dine, 4-methyl pyridine, piperazine, dimethyl morpholine, methoxypropylamine, z- and y-picoline, isopropylaminoethanol and 2-amino-2-methylpropanol. These eines also function to neutralize the free acid form of the phosphate ester converting it to the salt form. Imidazolines can be used for their known corrosion inhibiting properties with respect to cast iron and steel. Userul imidazolines are heterocyclic nitrogen compounds having the formula: EMI17.1 wherein R4 is hydrogen or a monovalent radikal selected from the group consisting of alkyl of 1 to 18 carbon atoms, alkylene of 1 to 18 carbon atoms, aryl, alkylaryl having to 18 carbon atoms in the alkyl portion, wherein R3 is a divalent radical selected from the group consisting of alkyl and alkoxy having 2 to 18 carbon atoms where the alkoxy is derived from alkylene oxides selected from the group consisting of ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran and mixtures thereof and wherein M is an alkali metal. It is also contemplated to add other known corrosion inhibitors. beides the amines, alkali metal n trates, benzoates and nitrites listed above, the alkoxyz latex fatty acids are useful as corrosion inhibitors. The above acaiWional corrosion inhibitors are employed in the hydraulic fluid concentrates in total amount of about 2 to 25 percent by weight, preferably about 5 to 15 percent by weight. More specifically, it is preferred to employ benzoates or benzoic acid in amount of about a to 5 percent, amines in amount of about 2 to 10 percent, and imidazolines in amount of about 2 to 10 percent all by weight of the total amount of concentrate. Metal deactivators may be used primarily to chelate copper and copper alloys. Such materials are well known in the art and individual compounds can be selected from the broad classes of materials useful for this purpose such as the various triazoles and thiazoles as well as the amine derivatives of salicylidenes. Representative specific examples of these metal deactivators are Es follows: benzotriazole, tolyltriazole, 2-mercaptobenzothiazole, sodium-2-mercaptobenzothiazole, and N,N'-disalicylidene-1,2propanediamine. The concentration of metal deactivator to water in the hydraulic fluid concentrates of the invention is generally about 2 to 10 percent by weight and preferably about 3 to 5 percent by weight. Conventional defoamers such as the weil known organic surfactant defoamers, for example nonionic defoamers such as the polyoxyalkylene type nonionic surfactnnis, may also be employed in normal amounts. Preferred amounts are about 0.5 to 5.0 percent by weight of the total amount of concentrate. The concentrate may contain other conventional hyuraulic fluid additives and possibly some impurities in normal minimal amounts. The phosphate esters and esters of ethoxylated aliphatic acids and alcohols are water-soluble in the sense that no special method is required to disperse these materials in water and keep them in suspension over long periods of time. As a means of reducing corrosion, the ph of the water in the fluids of the invention is maintained aocve 7.0, preferably 7.0 to about 11.0, and most preferably 9 to about 10.5. Preferably, pH of the fluid concentrates is adjusted with an alkali metal or alkaline earth metal hydroxide, or carbonate, ammonia or an amine Where these are employed, benzoic acid may be employed in lieu of alkali metal benzoates. The sulfurized molybdenum or antimony compounds on the other hand are insoluble in water and require emulsificaticn prior to use, for instance, with anionic or nonionic surfactants. Useful representative anionic or nonionic surfactants are: sodium petroleum sulfonate, i.e., sodium dodecylbenzene sulfonate; polyoxyethylated fatty alcohol or fatty acid and polyoxyethylated alkyl phenol. The concentrates of the hydraulic fluids of this invention can be made uo completely free of water or contain any desired amount of water but preferably contain up to 85 percent by weight of water to increase fluidity and provide ease of blending at the point of use. As pointed out above, these concentrates are typically diluted with water in Whe prooor';on of 1:99 to 40:60 to make up the final hycrauliz fluid. The preferred final hydraulic fluid of the invention contains 0.05 to 2 percent by weight of the polyoxyalkylene copolymer and optionally may include by weigAt one or more of the following: about 0.01 to 3.0 percent water soluble ester of exothylated aliphatic acid and/or ethoxylated alcohol ether, about 0.01 to 2.0 percent sulfur-containing compound, about 1 to 7 percent thickener, about 0.01 to 3.0 percent ethoxylated phosphate ester, or salt thereof, about 0.01 to 3 percent alkyldialkanolamide, about 0.05 to 10 percent additional corrosion inhibitors and most preferably about 0.01 to 2 percent benzoic acid and/or benzoates, about 0.02 to 2 percent amine type corrosion inhibitors and about 0.02 to 2 percent ethoxylated imidazoline, about 0.02 to 5 percent metal deactivators, about 0.02 to 1 percent defoamers plus other conventional additives such as dyes and impurities in normal amounts. For a high water fluid the total amount of additives should not exceed 5 percent. High water fluids generally do not contain thickeners.. The following examples more fully describe the hydraulic fluids of the invention and show the unexpected results obtained by their use. In the following examples of the invention, the wear properties of the hydraulic fluids were tested utilizing the Shell four-ball test method which is a standard test method for lubricants. In these tests, a 7.5 kilogram load at 1800 rpm was used at room temperature using 50 to 100 steel balls. The test was run for 20 minutes. The degree of corrosion inhibition of the additives was determined by a rust test usina cast iron chips and steel plates measuring 3 inches by 8 inches. More specifically, 10 grams of cast iron chips are placed in a small mixing dish, 10 milliliters of the sample are added, and they are stirred for one minute. The excess liquid is then decanted with the dish held in a pouring position for 15 seconds. A short piece (approxlmately 3/8 inches long) of radiator hose 1-1/2 inches ID is placed on the steel plate and the iron chips are poured into the piece of hose spreading as eveniy as possible. The piece of hose is then removed and the chips are allowed to stand on the plate for 24 hours. The chips are then removed and the amount of rust neft on the plate is measured using a scale of 0 to 100 percent of the area covered. In the examples, the polyoxyalkylene copolymers are as follows: Copolymer i1 - defines the polyoxyethylene adduct of a polyoxypropylene hydrophobic base, said hydrophobic base having a molecular wcight of about 1750 wherein the oxypropylene content is about 90 weight percent of the molecule. This product is readily available on the market under the trademark Pluronic0t6l. Copolymer 2 - deines the polyoxyethylene adduct of a polyoxypropylene hydrophobic base, said base having a molecular weight of about 1750 wherein the oxypropylene content is about 20 percent by weight of the molecule. This product is readily available on the market under the trademark Pluronic#F68. Copolymer 3 - defines the polyoxyethylene adduct of a polyoxypropylene hydrophobic base, said base having a molecular weight of about 950 wherein the oxypropylene content is about 90 percent of the molecule. This product is readily available on the market under the trademark Pluronic#L31. Copolymer #4 - defines the polyoxyethylene adduct of a polyoxypropylene hydrophobic base, said base having a molecular weight of about 4000 wherein the oxypropylene content is about 80 percent by weight of the molecule. This product is readily available on the market under the trademark Pluronic#L122. Copolymer 5 - deines the polyoxyethylene adduct ot a polyoxypropylene hydrophobic base, said base having a molecular weight of about 1750 wherein the oxypropylene content is about 60 percent by weight of the molecule. This product is readily available on the market under the trademark Pluronic#L64. The phosphate ester utilized in the examples is reputed to be produced by the reaction of one mole of phosphorus pentoxide with a ccndensation product of one mole of nonylphenol and approximately 4 moles of ethylene oxide in accordance with the methode disclosed in U.S. Patent Nos. 3,004,056 and 3,004,057. The examples are intended for the purpose of illustration. Throughout the application, all parts, proportions, and percentages are by weight and all temperatures are in degrees centigrade unless otherwise noted. Examole 1 A hydraulic fluid concentrate, indicated herein as concentrate A, was prepared by blending 78.45 parts by weight of water, 3 parts by weight of ethoxylated phosphate ester, 3 parts by weight of a C21 diethoxylated diacid mixed with a C21 diethanol diamide, 5 parts by weight of 2-amino2-methyl-1-propanol (95 percent aqueous solution), 4.5 parts by weight of a 50 percent by weight aqueous solution of tolyltriazole, 4 parts by weight of a 95 percent 2-heptyl-1 (ethoxypropionic acid) imidazoline, sodium salt in 5 percent of ethanol, 2 parts by weight of benzoic acid, and 0.05 percent by weight dye. From Concentrate A, the following fluids were prepared: Weight % Fluid 1 2 3 4 Concentrate A 5 5 5 5 Polyoxyalkylene Copolymer #1 0 0.15 6,4 0.8 Water 95 94.85 94.6 94.2 The wear scar diameter and percent rust on a steei panel were determined as set forth above witfl the following results: Fluid tt 2 3 4 Wear scar diameter (mm) 0.38 0.37 0.30 0.28 % Rust on steel panel 62 25 20 30 *Average of 3 tests Both the wear scar diameter and the percent of rust on a steel panel decreased in solutions containing at least 0.15 percent polyoxyalkylene copolymer. Example 2 - A hydraulic fluid concentrate, indicated herein as concentrate B, was prepared by blendung 81.5 parts by weight of water-, 3 parts by weight of ethoxylated phosphate ester, 5 parts by weight of 2-amino-2-methyl-1-propanol (95 percent aqueous solution), 4.5 parts by weight of a 50 percent by weight aqueous solution of tolyltriazole, 4 parts by weight of-a 95 percent 2-heptyl-1-(ethoxypropionic acid) imidazoline, sodium salt in 5 percent of ethanol, and 2 parts by weight of benzoic acid. From Concentrate B, the following fluids were prepared: Weight % Fluid ¯ 5 6 Concentrate B : 5 Polyoxyalkylene Copolymer #1 -- 0.15 C21 diethoxylated diacid mixed with a C21 diethanol diamide. 0.15 - Water 94.85 94.85 The wear scar diameter was determined as set forth above with the following results: Fluid 5 6 Wear scar diameter 0.35 0.26 This example demonstrates that polyoxyalkylene copolymer #1 is more effective than C21 diethoxylated diacid mixed with a C21 diethanol diamide in the wear scar diameter test. Example 3 A hydraulic fluid concentrate, indicated herein as concentrate C, was prepared by blending 83.5 parts by weight of water, 3 parts by weight of ethoxylated phosphate ester, 3 parts by weight of a C21 diethoxylated diacid mixed with a C21 diethanol diamide, 5 parts by weight of 2-amino-2 methyl-1-propanol (95 percent aqueous solution), 4.5 oart by weight of a 50 percent by weight aqueous solution of tolyltriazole, 4 parts by weight of a 95 percent solution o: 2-heptyl-1-(ethoxypropionic acid) imidazoline, sodium salt in 5 percent ethanol, and 2 parts by weight of benzoic acid From Concentrate C, the following fluids were prepared: : Weight % Fluids 7 8 Concentrate C 5 5 Polyoxyalkylene Copolymer #1 -- 0.25 Polyoxyalkylene Copolymer #2 1 1 Water 94 93.73 The wear scar diameter was determined as set forth above with the following results: Fluid 7 8 Wear scar diameter 0.64 0.42 This demonstrates that a copolymer containing only 20 percent oxypropylene groups is-ineffective in reducing wear scar diameter. Examtle 4 A hydraulic fluid- concentrate, indicated herein Es concentrate D, was prepared by blending i8.5 parts by weight of water, 3 parts by weight of ethoxylated phosphate ester, 3 parts by weight of a C21 diethoxylated diacid mixed with a C21 diethanol diamide, 5 parts by weight of 2-amino-2methyl-l-propanol (95 percent aqueous solution), 4.5 parts by weight of a 50 percent by weight acueous solution of tolyltriazole, 4 parts by weight of a 95 percent solution of 2-heptyl-1-(etnoxypropionic acid) imidazoline, sodium salt i 5 percent ethanol, and 2 parts by weight of benzoic acid. From Concentrate D, the following fluids were preparea: Weight r Fluid t 10 11 12 Concentrate D 5 5 5 5 Polyoxyalkylene Copolymer 33 0.8 -- -- - Polyoxyalkylene Copolymer 1 -- 0.8 -- - Polyoxyalkylene Copolymer 54 -- -- 0.8 - Polyoxyalkylene Copolymer ; -- -- -- 0.8 Water 94.2 94.2 94.2 94.2 The percent rust on a steel panel was determined Es set forth above with the following results: : Fluid 9 10 11 12 % Rust on steel panel 15 10 60 40 This example demonstrates that the percent of oxypropylene groups in the copolymer must exceed 60 percent even with a molecular weight of the oxypropylene groups as low as 1750 and that even with a percentage of oxypropylene groups as high as ao the molecular weight of the oxypropylene groups must be less than 4000. Examcle 5 Two complete hydraulic fluid compositions were prepared by blending 98.53 parts by weight of water, 0.25 parts by weight of 2-amino-2-methyl-1-propanol (95 percent acueous solution) 0.225 parts by weight of a 50 percent by weight aqueous solution of tolyltriazole, and 1 part by weight of Copolymer 89 in the first fluid (*13) and no polyoxyalkylene copolymer in the second fluid (*14). The percents rust on a steel panel were determined as set forth above with the following results: Fluid 13 14 % Rust on steel panel 5% 608 This example demonstrates that even with a Fluid having minimum protection from other additives, 2 pronounced corrosion inhibiting effect is achieved by the addition of a small amount of the polyoxyalkylene polymer in accordance with the instant invention. While this invention has been described with reference to certain specific embodimentst it will be recognized by those skilled in the art that many variations are possible without departing from the scope and spirit of the invention.

Claims: c 1#1'##i5 The embodiments of the invention in which an exclusive privilege or property is claimed are defined as follows: 1. A hydraulic fluid composition containing a heteric or block polyoxyalkylene copolymer which is the reaction product of a. linear or branche active hydrogen containing compound having from 1 to 6 carbon atoms with alkylene oxides having from 3 to 6 carbon atoms and an oxygen/carbon atom ratio of less than 0.4, and optionally alkylene oxides having an oxygen/carbon atom ratio greater than 0.4, said copolymer having a molecular weight of the 3 to 6 carbon atom oxyalkylene groups from about 950 to 3500 and containing about 65 to 100 percent by weight of the 3 to 6 carbon atom oxyalkylene groups. 2. A hydraulic fluid composition containing a nonionic polyoxyalkylene block copolymer which is a cogeneric mixture of conjugated polyoxyalkylene compounds containing in their structure the residue of an active hydrogen containing compound having from 1 to 6 carbon atoms and at least one hydrophobic chain of 6 carbon atom oxyalkylene groups in which the oxygen/carbon atom ratio does not exeed 0.4 and optionally, in addition, at least one hydrophilic chain of oxyalkylene groups in which the oxygen/carbon atom ratio is greater than 0.4, and wherein the molecular weight of the 3 to 6 carbon atom oxyalkylene groups is from about 950 to 3500 and the copolymer contains from about 65 to 100 percent by weight of the 3 to 4 carbon atom oxyalkylene groups. 3. The hydraulic fluid of claim 2 wherein said fluid is a concentrate in which the amount of said conjugated polyoxyalkylene compounds is at least about 0.5 percent by weight of the concentrate. 4. The concentrate of claim 3 wherein said nonionic copolymer corresponds to the formula Yt Y[(C3H6O)n(C2H4O)mH]x wherein Y is the residue of an organic compound having from about 1 to 6 carbon atoms and containing x reactive hydrogen atoms in which x has a value of at least one, n has a value such that the oxypropylene content of the molecule is from about 65 to 100 weight percent and the total molecular weight of the polyoxypropylene groups is from about 950 to 3500. 5. The composition of claim 3 wherein said concentrate includes a phosphate ester or salt thereof selecto"a from the group consisting of EMI30.1 and mixtures thereof wherein ethylene oxide groups are represented by EO; R is selected from the group consisting of linear or branched chain alkyl groups wherein said alkyl groups have about 6 to 30 carbon atoms, preferably about 8 to 20 carbon atoms, or alkylaryl groups wherein the alkyl groups have about 6 to 30 carbon atoms, preferably about 8 to 18 carbon atoms, and X is selected from the group consisting of hydrogen, alkali or alkaline earth metal, the residue of ammonia or an amine and mixtures thereof, and n is a number from 1 to 50E an alkyldialkanolamide of the formula EMI31.1 wherein R1 is alkyl of about 4 to about 54 carbon atoms and R2 is alkyl of about 2 to about 6 carbon atoms, a metal deactivator; and an additional conventional corrosion inhibitor.

Inventors: LABADIE, ERNEST JACOB, SCHWARTZ, ELLEN SHIRLEY, TINCHER, CLINE AWYN
Applicants: BASF WYANDOTTE CORPORATION
Application year: 1982
Main classification: C10M173
IPC codes: C08G65, C10M173