HEAT RECOVERABLE ARTICLE

Abstract: A dimensionally recoverable article, preferably a heat-­ recoverable article, has on at least part of a surface thereof an adhesive composition that will cure by reaction of a plurality of mutually reactive components. The components are in the form of particles which are mixed together and which will fuse when heated. Preferred adhesives are based on combinations of an epoxy with a polyamide, carboxylic acid, phenolic resin or blocked isocyanate curing agent. The particulate adhesives show a synergistic increase in rate and/or level of cure when used in conjunction with a recoverable article.

Description: This invention relates to dimensionaliy-recover- able articles, especially dimensionally heat-recoverable articles and to adhesives suitable for use therewith. A heat-recoverable article is an article the dimensional configuration of which may be made substantially to change when subjected to heat treatment. Usually these articles recover, on heating, towards an original shape from which they have previously been deformed, but the term "heat-recoverable", as used herein, also includes an article which, on heating, adopts a new configuration, even if it has not been previously deformed. In their most common form, such articles comprise a heat-shrinkable sleeve made from a polymeric material exhibiting the property of elastic or plastic memory as described, for example, in U.S. Patents 2,027,962; 3,086,242 and 3,957,372. As is made clear in, for example, U.S. Patent 2,027,962, the original dimensionally heat-stable form may be a transient form in a continuous process in which, for example, an extruded tube is expanded, whilst hot, to a dimensionally heat-unstable form but, in other applications, a preformed dimensionally heat stable article is deformed to a dimensionally heat-unstable form in a separate stage. In the production of heat recoverable articles, the polymeric material may be cross-linked at any stage ir. the production of the article that will enhance the desired dimensional recoverability. One manner of producing a heat-recoverable article comprises shaping the polymeric material into the desired heat-stable form, subsequently cross-linking the polymeric material, heating the article to a temperature above a transition temperature thereof, for example, the crystalline melting point or, for amorphous materials the softening point, as the case may be, of the polymer, deforming the article and cooling the article whilst in the deformed state so that the deformed state of the article is retained. In use, since the deformed state of the article is heat-unstable, application of heat to raise the temperature above the transition temperature will cause the article to assume its original heat-stable shape. Where the term "recovery temperature" in connection with heat-recoverable articles is used herein, it is intended to refer to the transition temperature above which the article recovers even if some small degree of recovery is exhibited at temperatures slightly below the transition temperature. In other articles, as described, for example, in British Patent 1,440,524, an elastomeric member such as an outer tubular member is held in a stretched state by a second member, such as in inner tubular member, which, upon heating weakens and thus allows the elastomeric member to recover. Articles of this type have, in recent years, become widely used in a number of applications, for example for protecting objects such as electrical cables and cable splices or metal pipes from corrosion or other damage, for example damage caused by penetration of moisture. For this reason many heatrecoverable articles are provided with a coat of adhesive or sealant. One problem that is associated with the provision of adhesives on heat-recoverable articles is that, because the heat required to melt or otherwise activate the adhesive is usually supplied by heating the external surface of the heat-recoverable article, the temperature to which the adhesive is heated will be considerably lower than that of the external surface of the article due to the relatively poor thermal conductivity of the materials from which the heat-shrinkable article is formed. Thus, for example, where the heat-shrinkable article is formed from a cross-linked polyethylene, the external surface of the article may be heated up to about 2500C in order to raise the adhesive temperature to only 10G C, and, in this case, no further heating of the article would be possible without damaging the article. Also, in many cases, the maximum temperature to which the adhesive can be raised is restricted by the type of substrate that is being covered. For example, where the substrate is a metal pipe, the thermal conductivity and size of the pipe cause it to act as a heat-sink and effectively limit the adhesive temperature and, where the substrate comprises an uncrosslinked polymer as is often the case with electrical cable jackets, the adhesive temperature often cannot be raised above about 100 to 1200C without damaging the cable jacket. Whilst hot-melt adhesives or mastics can be used in a number of applications, the maximum temperature to which the article may be subjected after installation is usually limited to the melting or softening point of the adhesive. The present invention provides a dimensionally recoverable article, preferably a dimensionally heat recoverable article, having, on at least part of surface thereof, an adhesive composition that will cure by reaction of a plurality of mutually reactive components, the components existing separately from one another in the form of solid particles which are mixed together and which will fuse when heated. Preferably the components are such that, if they are brought together into intimate contact for example by dissolving them in a common solvent, they will react together even at room temperature to form a cured product so that curing of the adhesive composition on the article during storage is prevented substantially solely by the separation of the particles of each component. In a number of cases it has been found that when the heat-recoverable article according to the invention is recovered onto a substrate, the adhesive will cure sooner than if it is heated on its own to the same temperature, or will cure at significantly lower temperature than it will when heated on its own. Thus it has been found that it is possible, according to the invention, to provide an adhesive coated heatrecoverable article in which the adhesive can be cured by heating the article to its recovery temperature for periods in the range of the recovery time of the article, but which will also have good storage life. The rate of curing of curable adhesives at elevated temperatures is linked to their rate of curing at ambient temperatures, and hence their storage life, by the Arrhenius equation which effectively imposes a limit on the rate of cure of an adhesive at the usual recovery temperature of a heat-shrinkable article (about 100 to 1200C) for any given storage life at ambient temperatures or vice versa. It can be shown from the Arrhenius equation that any curable adhesive that cures sufficiently rapidly at the recovery temperature of the article should suffer from a poor storage life or that an adhesive that does have a long storage life should not cure sufficiently rapidly at the recovery temperature of the article. However, according to the invention it is possible to overcome this problem by virtue of the synergistic increase in the rate of curing of certain adhesives when used in conjunction with a recoverable article. This synergistic effect is most pronounced when the fusion temperature of the components is in the region of the recovery temperature of the article or the temperature to which the adhesive is heated when the article is recovered. Preferably the fusion temperature is not more than 50 , especially not more than 300 and most especially not more than 100C above the recovery temperature of the article. Also, not more than one, and especially none, of the components has a fusion temperature of less than 500C. Each of the components preferably has a fusion temperature in the range of 70 to 1200C and most preferably from 70 to 1000C, and, instead or in addition, each has a fusion temperature that differs from the fusion temperature of the or each other reactive component by not more than 300C. In most instances the components will melt or soften at their fusion temperature although the term is intended to include sublimation of one or more components if this occurs. In many cases the reactive components will soften and low or otherwise fuse over a temperature range and the softening characteristics of the components may be observed by thermomechanical analysis (TMA) as described in "Thermal Analysis" by T. Daniels published by Kogan Page 1973. Accordingly, the fusion temperature or the melting point of the reactive components of the adhesive is defined herein as being the temperature at which the TMA probe has penetrated to 60% of the total thickness of the material, usually referred to as T60. The TMA data described herein were obtained using a 6.35T diameter flat profile probe loaded with a 50 gramme weight and by increasing the temperature of the material at a rate of 1000 per minute. Preferably the temperature at which reactive components of the adhesive initially become soft referred to as Ti on the TMA plot) is not more than 3000 below and especially not more than 2500 below the melting point (T60) of the components so that the difference between the maximum storage temperature and the minimum curing temperature can be reduced as far as possible. Another synergistic effect that may be shown by the articles according to the invention, either instead of or in addition to the increase in rate of cure of the adhesive is an increase in the level of curing of the adhesive as compared with the adhesive on its own. The increase in level of curing leads to improved properties such as solvent resistance and improved high temperature properties such as high temperature shear strength. The level of cure of the adhesive may be measured in a number of ways. For example, it may be measured as an increase in the T60 (as defined above) or, more preferably the T80 of the adhesive, where T80 is defined as the temperature at which the TMS probe has penetrated to 80% of the total thickness of the adhes ive. In some cases the composition will cure suffic iently to prevent the probe penetrating it by 80% in which case the total depth of penetration is a better measure of cure. Another measure of the level of cure of the adhesive is its gel content which is measured by weighing a quantity of the adhesive into an extraction thimble, refluxing the adhesive for 5 to 8 hours with a solvent (e.g. 1,2-dichlotoethane or tetrahydrofuran), drying the thimble in an oven for 24 hours to evaporate the solvent and, after leaving the dried thimble in the atmosphere for a further 24 hours reweighing the thimble. The gel content is then defined as the final weight of the adhesive (which is insoluble) expressed as a percentage of the initial weight of the adhesive. The adhesive cures, as stated above, by reaction of a plurality of mutually reactive components. The phrase "mutually reactive components" is defined herein as meaning components which, when mixed together in their particulate form, will react together at the fusion temperature thereof or at least at the highest fusion temperature thereof to form a composition having a T80 value that is at least 200C, preferably at least 300C and especially at least 400C above the initial fusion temperature of the blend. Preferably the components will exhibit a gel content of at least 20%. According to another aspect, the invention provides a method of enclosing at least part of a substrate, which comprises: (a) positioning thereon a dimensionally-recov erable article such that an adhesive compos ition is disposed between the article and substrate, the adhesive composition compris ing a plurality of mutually reactive compon ents that exist separately from one another in the form of solid particles which are mixed together and which will fuse when heated; and (b) recovering the article about the substrate and heating the adhesive to fuse the part icles. There is essentially no limit on the particle size of the reactive components in that the articles can still show a synergistic increase in rate and/or level of cure even with very large particles although the absolute value of the cure rate will decrease with large particles. Preferably the reactive components will have a weight average particle size of not more than 1000, especially not more than 500 and most especially not more than 300 micrometres. Preferably the reactive components have a weight average particle size of at least 1, more preferably at least 5 and especially at least 10 micrometres. The particle size of the reactive components may conveniently be adjusted by sieving the particles through an appropriately sized mesh in which case it is preferred that the particulate components are substantially free of particles greater than 500 micrometres in size. The preferred particle size ranges are from 5 to 300 and especially 10 to 200 micrometres. The adhesive composition may, if desired, consist solely of the reactive components aithough it is preferred for it to include one or more inert components. The inert components may be present with the reactive components in the particles, or may be mixed with the particles as a separate phase or both. For example, the adhesive may comprise a particulate curable resin such as an epoxy resin, preferably one based on bisphenol A or on epoxy novolak resin, as one component and a particulate curing agent such as an amine, carboxylic acid, phenolic resin or isocyanate curing agent as the other. The curing agent may itself be polymeric for example it may be a polyamide having free amino groups or a carboxylated polymer such as an acid terpolymer,in which case the particles of the curing agent need not contain any inert component. If the curing agent is not polymeric, for example an organic peroxide or other free radical initiator, it may be desirable for it to be blended with a polymeric material, e.g. a polyester or a reactive or unreactive polyamide before comminution. The curable resin may, instead, comprise a polyamide having free amine groups, in which case the curing agent preferably comprises a material having free or blocked isocyanate functional groups, e.g a cresyl blocked isocyanate. The polyamides that-are most suitable for forming one of the components are those that are conventionally used as hot-melt adhesives. These polyamides are characterized by the fact that their amide linkages are separated by an average of at least fifteen carbon atoms and have amorphous structures in contrast with the more hightly crystalline, fibre forming polyamides such as nylon 6 or nylon 6.6. The polyamides preferably have an amine number of at least 5, the upper limit for the amine number being determined by the fact that as the amine number increases the polyamides become liquid at lower temperatures. Chemical curing accelerators may also be present in the adhesive, either blended with one of the reactive components or as separate particles. Examples of accelerators include dimethylaminopyridine, tris (dimethylaminomethyl) phenol, tin octoate, imidazole or imidazole derivatives such as salts, substituted imidazoles or metal complexes thereof. A number of inert components may be incorporated in the compositions as long as they do not adversely affect the increase in rate or level of cure of the adhesive composition. Also it is preferred if they do not adversely affect the storage life of the adhesive. Inert components that may be incorporated in the adhesive include plasticisers such as phthalates or rosin esters, thermoplastic or thermosetting polymers, cured or uncured rubbers, inorganic materials to modify the properties of the uncured or cured adhesive such as reinforcing fillers, reinforcing fibres or microspheres, or tackifiers and the like. The other components, whether organic or inorganic, may be in any appropriate physical form, for example they may be in the form of powder, flake or fibres, and are preferably present in an amount of from 5 to 50 percent by weight based on the total weight of the composition. In a preferred aspect of the invention the adhesive composition contains one or more other components having a softening temperature range (from the initial softening temperature to T60) that is greater than that of the reactive components so that the softening temperature range of the adhesive composition as a whole is greater than that of the reactive components, preferably by at least 5 C. This has the advantage that, whilst the adhesive will cure when heated to only a relatively low temperature above the maximum storage temperature, it will possess cohesive and adhesive strength over a signIficantly greater temperature range. Alternatively, in some cases where the reactive components have a large softening temperature range it may be desirable to reduce the softening temperature range of the adhesive composition by incorporation of the appropriate components for example tackifier resins such as hydrogenated rosin esters and terpene phenols or polar waxes such as polyamide and polyester waxes. As examples of other components that may be incorporated in the adhesive compositions, there may be mentioned tacky materials such as pressure sensitive adhesives or mastics, or thermoplastic materials. The components are preferably, although not necessarily, fluid at temperatures below the melting point of the reactive components, but if they are not they should be such as to allow the reactive components to mix together at the recovery temperature of the article. The articles according to the invention may be formed in a number of configurations depending on the particular use. The articles may be in the form of a tube that has been extruded and expanded radially to render it heat-recoverable, the tube being either in continuous lengths or discrete pieces and being coated on its internal surface with the adhesive compositions. Alternatively, the articles may be in the form of a sheet or tape that can be wrapped or wound around an object. More complex shapes, commonly referred to as boots, transitions, udders or caps, may be formed by moulding the articles in the desired configuration and then expanding them or by the methods described in our copending U.K. Applications Nos. 8123069 and 8123072 (serial Nos. 2083403A and 2083859A). The present invention is also suitable for the production of wrap-around devices. So called wrap-around devices are employed for sealing, insulating or otherwise protecting a substrate where the use of a preformed tubular article such as a sleeve, is not possible or convenient e.g. in the case where the end of an elongate substrate is not accessible. In general, such wrap-around articles comprise at least a portion thereof which is adapted to be wrapped around a substrate to be covered and secured in tubular form by closure means. Thereafter, the wrap-around closure may be heat-recovered tightly onto the substrate by application of heat. Examples of wrap-around devices are described in U.S. Patents Nos. 3,379,218, 3,455,326, 3,530,898, 3,542,079 and 3,574,318 the disclosures of which are incorporated herein by reference. Another form of wrap-around device in which the curable adhesive may be used is that described in U.K. Patent Application No. 8113486 (serial No. 2076694A) in which the curable adhesive is used to form a layer of sealant that may be peeled away at any desired point to expose a closure adhesive. Yet another form of wraparound device in which the curable adhesive may be used comprises a dimensionally recoverable cover having two closure portions which can be brought into abutment to form an adhesive bond using the particulate adhesive, but which, after the adhesive bond has ben formed, will change in configuration to form a lap joint by recovery of the cover about the substrate. In this device one closure portion may be in the form of an upstanding flange and the other closure portion may be in the form of a further upstanding flange that is bent or folded downwards at its apex so that, after the closure portions have been pushed into abutment and the cover is recovered, the further flange opens out and a lap joint is formed. Another preferred article according to the invention is in the form of a continuous tape or sheet, one surface of which is coated with the adhesive composition. Such an article may be wound helically around a substrate for example a metal pipe which is preferably pre-heated, and the wound portions of the tape or sheet may be heated to recover the tape or sheet and cure the adhesive. Often it is desired to operate further on the pipe shortly after the protective article has been recovered thereon, for example to bury it in a pre-dug trench and, because of the rapid cure of the adhesive composition, it is possible to perform such operations only a few minutes after the tape or sheet according to the invention has been recovered thereon. The adhesive composition may be coated on the heat-recoverable article in a number of ways depending on the type of article and adhesive composition. For example, where the article has an open, generally uniform configuration, it may be provided with a layer of tacky material for example pressure sensitive adhesive layer e.g. by spraying or in the form of a tape, and the adhesive composition may be applied as a powder to the pressure sensitive adhesive bearing portions of the article and compressed thereon by application of pressure. Alternatively, the powder may be compressed into a coherent layer and then bonded to the article by means of a tacky material. For either of these methods, pressures in the order of 0.8 MPa (120 p.s.i.) and temperatures of about 15 to 300C have been found to be most suitable. These methods of applying the adhesive composition are suitable for applications in which the adhesive contains no components other than the particulate reactive components in addition to those in which the adhesive does contain other components. In another method of applying the adhesive composition, the particulate reactive components are mixed with the other components which preferably comprise or include a pressure-sensitive adhesive or a mastic and the whole composition is pressed onto the heat-recoverable article or pressed into a coherent film which is then adhered to the heat-recoverable article, the temperatures and pressures used preferably being the same as those mentioned above. Yet another method of application, which is suitable for coating the internal surfaces of tubes or moulded articles, comprises spraying the adhesive onto the appropriate parts of the article. The adhesive may be sprayed in the form of the dry powder onto a surface that is coated with a tacky material, e.g. a pressure sensitive adhesive, or the particulate reactive components may be dispersed in a non-solvent that contains a binder and, after the dispersion is sprayed onto the article, the non-solvent is allowed to evaporate. According to yet another aspect, the invention provides an adhesive composition that is novel per se comprising: (a) a thermoplastic polyamide having reactive amine groups; (b) a thermoplastic copolymer of an alkene, preferably ethylene, with an ethylenically unsaturated ester of an alkanol and a carboxylic acid, the ester having up to 6 carbon atoms, and optionally one or more acid comonomers; and (c) a thermoplastic epoxy resin; components (a) and (b) being present in a ratio of from 35:65 to 75:25, preferably from 35:65 to 65:35, more from 40:60 to 60:40 and especially from 45:55 to 55:45 by weight, and component (c) being present in an amount of from 8 to 79 parts per hundred parts of (a) and (b) combined by weight, components (a), (b) and (c) existing separately from one another in the form of particles that are mixed together. In this case each of components (a), (b) and (c) will react with the other two components when the composition is heated to above the melting points of the components. Component (b) preferably has an acid number of at least 1 and preferably also has an acid number of less than 100. The term "copolymer" as used herein in connection with component (b) is intended to include terpolymers and polymers containing four or more comonomers. The preferred comonomers are vinyl acetate and ethyl acrylate optionally with an unsaturated carboxylic acid e.g. acrylic acid. Examples of materials that may be used include those described in U.S. patent No. 4,018,733 to Lopez et al, the disclosure of which is incorporated herein by reference. b=poxy used for component (c) may comprise any of a number of epoxies for example those based on novolak resins or on bisphenol A, and may have a wide range of epoxy values provided it remains thermoplastic. Any of the polyamides mentioned above will in general be suitable as component (a). The components (a), (b) and (c) preferably each has a melting or softening point (T60) in the range of from 60 to 1200C, more preferably from 70 to 1200C and especially from 70 to 100 C. The adhesives according to the invention have a softening point that Increases on application from the melting or softening points of the components, e.g. in the order of 90 to 950C to a value of about 130 to 1400C or even higher and so combine low initial application temperatures with relatively high use temperatures. Furthermore, whilst the adhesive exhibits relatively high bond strengths when subject to shear stresses it also exhibits surprisingly high bond strengths at high temperatures in the peel mode, e.g. in the order of 80 to 100 N(25mm) -1 at between polyethylene substrates in contrast with conventional epoxy adhesives which have extremely low peel strengths. The following Examples illustrate the invention, all parts expressed therein being by weight: EXAMPLE 1 20 Parts of a cryogenically ground dimerised fatty acid reactive polyamide sold under the trade nnr "Macromelt 6071" (formerly called "Versamid 871") (Ti=60 C; T60=67 C) were mixed with 77 parts of a powdered epoxy resin based on bisphenol A sold under the trade name "DER 66211 (Ti = 470 C; T60 = 67 C) and 3 parts of powdered dimethylamlnopyrldine accelerator (T60 = 105 C). The mixture was graded so that no particles were greater than 300 micrometres in size. The composition was pressed onto a heat-shrinkable ethylene vinyl acetate sheet having a recovery temperature of 800C to an amount of 0.75 to 1 kgm 2 ! The ethylene vinyl acetate sheet having a recovery temperature of 80 C to an amount of 0.75 to 1 kgm 2. The sheet had a recovery ratio of 3.75:1 and was wrapped around a mandrel that had been preheated to a predetermined temperature in an oven, and the edges of the sheet were secured. The mandrel and sheet had dimensions such that when the sheet recovered onto the mandrel it had recovered by 608 of its total possible recovery. The sheet and mandrel were placed in the oven and strips of the sheet and adhesive were removed after time Intervals. As a comparison, samples of the adhesive were placed in a irrim thick bakelite pan and were heated in the oven for the same length of time. The comparison samples had a thickness of about 0.8 to 0.9 kgm (corresponding to the initial thickness of adhesive on the shrinkable sheet) and about 1.5 kgm 2 (corresponding to the final thickness of the adhesive on the recovered sheet). The extent of cure of the adhesive was measured as the gel content. The results are shown in Table I. TABLE I Oven Temperature = 100 C Time Gel Content (%) (minutes) Heat Shrink Comparison (0.8-0.9gm 2 (1.5 kgm 2) 0 0 0 0 5 27 15 18 10 25 17 15 15 26 20 18 20 39 23 24 30 68 42 56 Example 2 An adhesive was prepared by blending 19 parts of a polyamide sold by Henkel under the trade name "Macromelt 6301 " (formerly called Versaion 1300) with 19 parts of a reactive polyamide sold by Henkel under the trade name "Macromelt 6071" (formerly called Versamid 871) and the blend was cryogenically ground and sieved to a particle size of less than 300 micrometres. The so melting point was 73 C. To the polyamide was added 60 parts of a bisphenol A epoxy resin sold by Shell Chemicals under the trade name "Epikote 1001" (ground and sieved to a particle size of less than 300 microns) (T60 = 50 - 70 C), 2.5 parts of powdered dimethylaminopyridine and 0.3 parts of a silica flow agent. The adhesive was coated onto a heat-shrinkable crosslinked ethylene vinyl acetate sheet (Elvax 460 - trade name) having a recovery temperature of 800C and a recovery ratio of 16%, to an amount of 0.75 to 1 kqm 2. The curing of the adhesive and of compar ison samples was observed by the procedure described in Example 1, and the results are shown in table II, comparison A and B samples having an adhesive thickness of 0.8-0.9 kgm-2 ! and 1.5 kgm 2 respectively. TABLE II GEL CONTENT (%) Oven Temperature 80 C 1200C Time (Minutes) Heat Shrink Comparison Heat Shrink Caparison A B A B 0 8 8 8 8 8 8 5 16 7 5 82 12 7 10 20 7 18 85 13 7 15 24 10 16 79 50 50 20 22 10 34 78 57 57 30 42 10 30 84 58 66 EXAMPLE 3 An adhesive was prepared by mixing the following particulate components: : Parts T@ %@@ by weight (a) Polyamide sold under the trade name Macranelt 6301 45 C 800C 9 modified by milling in 108 by weight of a plasticise5r sold under the trade name "santicizer 8" by Monsanto (b) Macromelt 6301 polyamide modified by milling in 700C 840C 9 10% by weight of a polymercaptan sold by Diamond Shamrock under the trade name Capcure 3-800" (c) Epoxy cresyl novolak resin sold under the trade 42 C 670C 59 name "ECN 1280" by CIBA DEITY (d) dimethylaminopyridine (accelerator) 1050C 3 (e) Talc 20 The composition was graded to exclude particles greater than 300 micrometres and pressed onto a heat shrinkable sheet as described in Example 1. Curing of the adhesive was observed by the procedure described in Example 1 and the results are shown in Table III. TABLE III Oven temperature = 1400C Time Gel Content (%) Heat Shrink Comparison (0.8-0.9kgm-2) (1.5 kgm-2) -------------------------------------------- 0 0 0 0 5 51 35 24 10 50 42 36 15 55 52 48 20 49 56 48 30 57 55 56 EXAMPLE 4 50 parts of a cryogenically ground reactive polyamide sold under the trade name "Macromelt 6071" (T. = 52 C; T60 = 72 C) were mixed with 50 parts of a powdered blocked isocyanate sold by Mobay Chemical Co. under the trade name "Mondur SH"(T60 = 97 C) to form an adhesive composition. The procedure of Example 1 was repeated with the exception that the extent of cure of the adhesive was determined by measuring the T80 value of the samples of the adhesive after removal from the ovenand that an aluminium pan was used for the comparison samples. The results are shown in Table IV. TABLE IV TIME (Minutes) T8y0C (Oven temperature = 120 C) Heat Shrink Comparison (1.5 kgm 0 88 88 5 97,99 10 121,123 15 120,119 118 20 136,155 116,126 30 205,172 109,180 EXAMPLE 5 150 parts of Macromelt 6301 polyamide that had been modified by milling in 5% by weight of a reactive liquid polyamide sold under the trade name Euredor 115 (formerly called Versamid 115) and had been cryogenic ally ground to form a powder (T60 = 74 C) were mixed with 100 parts of a powdered ethylene -vinyl acetate acid terpolymer sold by du Pont under the trade name Elvax 4260, 80 parts of a bisphenol A epoxy resin sold by Shell Chemicals under the type No. Epikote 1004 (T60 = 80 -10G C), and 6 parts of a dimethyl aminopyridine accelerator. Each of the components had been sieved to remove all particles greater than 300 micrometres in size. The adhesive was applied onto a heat-shrinkable sheet and cured as described in Example 1, the curing being measured by the T80 value of the adhesive. The oven temperature was of 1 200 C. The results are shown in Table V. TABLE V T@@/ C Time (minutes) Heat Shrink Comparison (0.8-0.9 kgm-2) (1.5 kgm-2) 5 94 100 10 98 15 107 84 20 116 109 96 30 118 93 Example 6 An adhesive was prepared by blending 48 parts of a reactive polyamide (Macromelt 6071) with 3 parts dimethylaminopyridine, then cryogenically grinding the blend to form a powder and sieving the powder to a particle size of less than 300 micrometers. To this were added 34 parts of a powdered multifunctional epoxy cresyl novolak resin sold by Dow Chemicals under the trade name "XD 7855"(T60 = 69-77 C, particle size less than 300 microns), 10 parts of powdered decabromo diphenyl ether (flame retardant) and 5 parts antimony trioxide. The adhesive was applied onto a heat-shrinkable article and its curing measured as described in Example 1 at an oven temperature of 1400C with the exception that an aluminium pan was used for the comparison samples. The results are shown in Table VI. ThBLE VI Time Gel Content (%) (Minutes) Heat Shrink Caparison (1.5 kgm ) 0 15 15 5 35 19 10 43 20 15 46 23 20 50 24 30 54 27 Example 7 Example 4 was repeated with the exception that the 50 parts of polyamide (Macromelt 6071) were replaced by 50 parts of a difunctional bisphenol A epoxy resin sold by Shell Chemicals under the trade name "Epikote 1001"(T60 = 50 - 70 C). The oven temperature was 140 C and the T80 values are shown in Table VII. TABLE VII Time T80/CC (Minutes) Heat Shrink Comparison (1.5 0 85 85 5 100 91 10 107 83 15 109 96 20 107 82 30 106 86 Example 8 Example 1 was repeated using, as the adhesive, a commercially available powdered phenolic resin (melting point 80 C) which included 9% by weight of powdered hexamethylene tetramine as the curing agent (sublima tion temperature 1500C). The rate of curing was determined by gel content and the results are shown in Table VIII. TABLE VIII Time Gel content (%) (Minutes) Heat shrink ComparIson (0.8-0.9 kgm-2) (1.5 kgm-2) 0 13 5 9 9 9 10 50 9 5 15 84 8 6 20 108 15 8 30 112 83 71 Example 9 Example 4 was repeated using an adhesive compris ing 60 parts by weight of a particulate epoxy resin (either GT 7004 or Araldite 6100 sold by CIBA GEIGY), 40 parts of a particulate bisphenol A novolak resin sold by CIBA GEIGY under the trade name XD4049, and 2 parts dimethylaminoppyridine. Examples 10 to 19 Samples of adhesive compositions according to the invention were prepared by cryogenically grinding a polyamide hot-melt adhesive or blend of adhesives, an ethylene copolymer and an epoxy resin, sieving the components to exclude particles of greater than 300 micrometres and mixing the particles together. The rolling drum peel strength of the adhesive was measured at 700C in accordance with the procedure described in U.S. Patent No. 4,018,733 column 12. The compositions and results are shown in Table IX. TABLE IX EXAMPLE 10 11 12 13 14 15 16 17 18 19 Comparison Invention Comparison Components Trade name Parts by weight Polyamide Macromelt 6301+ blend Durelon 100 (9:1) 50 50 50 50 50 50 50 50 50 50 E.V.A. CXA 2002 50 50 50 50 50 50 50 50 50 50 Epoxy resin Epikote 1004 0 1 6 10 43 75 80 100 200 400 Peel strength at 70 C/N (25mm)-1 50 20 29 83 88 99 30 Brittle Examples 20 to 35 The procedure of Examples 10 to 19 was repeated with a number of compositions to demonstrate the limits for the proportions of polyamide and ethylene copolymer. In addition to the peel strength, the lap shear strength of the adhesive was measured at 700C in accordance with ASTM-D638 between aluminium substrates. The results are shown in Table X. TABLE X Components Trade name 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 INVENTION COMPARASION PARTS BY WEIGHT Polyamide blend Macromelt 6301+ 70 60 50 50 40 100 80 80 70 60 50 40 30 30 20 20 Euredor 100 Epoxy resin Epikote 1004 10 10 10 10 10 10 Epoxy resin Epikote 1001 10 10 EVA CXA 2002 30 40 50 50 60 20 20 30 40 50 60 70 70 80 80 du Pont Peel strength at 70 C/N (25mm)-1 31 81 83 147 82 45 31 40 20 48 50 55 24 15 43 30 Shear strength at 70 C/N(25 mm)-2 543 515 840 690 358 620 550 431 425 497 283 350 ExamPles 36 to 41 The procedure of Examples 10 to 19 was repeated using a number of different ethylene copolymer components. The peel and shear strengths were measured at 700C and in each case the composition was compared with a corresponding composition containing no epoxy. The results are shown in Table XI. TABLE XI Components Trade name EXAMPLE 36 37 38 39 40 41 PARTS BY WEIGHT Polyamide blend Macromelt 6301+ 50 50 50 50 50 50 50 50 50 50 50 50 50 Euredor 100 (9:1) Epoxy resin Epikote 1001 10 Epoxy resin Epikote 1004 10 10 10 10 10 10 EVA (acid N0=1) Elvax 460 50 50 50 (du Pont) EVA (acid No=6) Elvax 4320 50 50 EVA (acid No=36) CXA 2002 50 50 Ethylene ethyl DP6169 acrylate (Union Carbide) 50 50 Ethylene butyl Lupolene A2910 acrylate acrylic (BASF) acid 50 50 Ethynene acrylic AC540A acid (Allied Chem) 50 50 Peel strength at 70 C/N (25 mm)-1 40 56 9 79 9 49 46 56 6 29 29 31 35 Shear strength at 70 C/N (25 mm)-2 505 404 374 323 853 815 404 358

Claims: Claims: 1. A dimensionally recoverable article having, on at least part of a surface thereof, an adhesive composition that will cure by reaction of a plurality of mutually reactive components, the components existing separately from one another in the form of solid particles which are mixed together and which will fuse when heated. 2. An article as claimed in claim 1 which is dimensionally heat-recoverable. 3. An article as claimed in claim 2, wherein each of the reactive components has a fusion temperature that is not more than 500C above the recovery temperature of the article, preferably not more than 10 C above the recovery temperature of the article. 4. An article as claimed in any one of claims 1 to 3, wherein each of the reactive components has a fusion temperature of at least 50 C. 5. An article as claimed in any one of claims 1 to 4, wherein each of the reactive components has a fusion temperature in the range of from 70 to 1200C. 6. An article as claimed in any one of claims 1 to 5, wherein the particles have a weight average particle size of not more than 1000, preferably not more than 300 micrometres. 7. An article as claimed in any one of claims 1 to 6, wherein one of the reactive components comprises an epoxy resin and the other reactive component comprises a thermoplastic polyamide resin having free amine groups. 8. A method of enclosing at least part of a substrate, which comprises: (a) positioning thereon a dimensionally-recov erable article such that an adhesive compos ition is disposed between the article and substrate, the adhesive composition compris ing a plurality of mutually reactive compon ents that exist separately from one another in the form of solid particles which are mixed together and which will fuse when heated; and (b) recovering the article about the substrate and heating the adhesive to fuse the part icles. 9. An adhesive composition which comprises: (a) a thermoplastic polyamide having reactive amine groups; (b) a thermoplastic copolymer of an alkene with an ethylenically unsaturated ester of an alkanol and a carboxylic acid, the ester having up to 6 carbon atoms, and optionally one or more acidic comonomers; and (c) a thermoplastic epoxy resin; components (a) and (b) being present in a ratio of from 35:65 to 75:25 by weight and component (c) being present in an amount of from 8 to 79 parts per hundred parts of components (a) and (b) by weight, components (a), (b) and (c) existing separately from one another in the form of particles that are mixed together. 10. An adhesive as claimed in claim 9, wherein component (b) has an acid number of less than 100. 11. An adhesive as claimed in claim 9 or claim 10, wherein the ethylenically unsaturated ester of component (b) is vinyl acetate or ethyl acrylate. 12. An adhesive as claimed in any one of claims 9 to 11, wherein the alkene of component (b) is ethylene. 13. An adhesive as claimed in any one of claims 9 to 12, wherein components (a) and (b) are present in a ratio of from 4:6 to 6:4 by weight. 14. An adhesive as claimed in any one of claims 9 to 13r wherein components (a), (b) and (c) each has a melting point in the range of from 60 to 1200C 15. A dimensionally recoverable article having on at least part of a surface thereof an adhesive as claimed in any one of claims 9 to 14.

Inventors: BARKER, DAVID JOHN, CORKE, NICHOLAS THOMAS, PARK, GEORGE BARRY, PITHOUSE, KENNETH BRIAN, READ, MICHAEL ROSSER
Applicants: RAYCHEM LIMITED
Application year: 1982
Main classification: C09J7
IPC codes: C09J177, C09J7, C09J179, C09J5, B29C61, C09J123, F16L58, C09J163