INSIDE TELECOMMUNICATIONS CABLE

Abstract: Inside cable (10) for buildings in which the core (12) is surrounded by a flame retardant jacket (15) and interstices between conductors (14) are filled with a flame retardant powder. The jacket may be formed from a polyvinylchloride composition but is preferably of a polyvinylidene fluoride composition. Preferred powders are polyvinylidene fluoride, calcium carbonate, and hydrated alumina. The cable con­ structions decrease flame spread and also smoke emission from a fire.

Description: INS TE l E .OMA1U CATIONS CABLE This invention rates to inside cable. An inside cable is one which is designed for use inside buildings as distinct from the open air or beneath the ground. Such cable includes power cable, central office cable, station cable, signal cable, service entrance cable, switchboard cable, and telecommunications cable. Inside cable has a requirement which does not apply to buried cable and this is that it needs to have fire retardant properties to prevent the spread of fire through the cable and thus through a building. Some cable, such as telecommunications cable, passes through air ducts and plenums of buildings. In the event of a cable commencing to burn in such a location, unless fire retardant precautions are taken, the eventual fire spread may have disastrous consequences. Also of importance, is the amount of smoke which is generated at a time of fire in a cable. Frequently, lives are lost, not because of the heat of the fire, but as a direct result of the amount and type of smoke issuing from a burning cable and flowing into rooms, stairways and elevator shafts. One way of increasing the fire retardancy and decreasing the smoke output of a cable for inside use is to employ a jacketing material which is itself fire retardant. Thus where a cable for outside use may include a jacket formed from pollyetl) ne, it is essential that the material of greater fire retardancy is used for inside cable such as one having a polyvinylchloride composition. A problem with any fire retardant is, however, that the jacketing material is not completely fire proof. One reason for this is the use of plasticizer in the jacketing composition. Such a jacketing material will not combust under certain conditions of temperature, but may only be effective in retarding the spread of fire after burning commences. Hence a jacket formed basically from a polyvinyl chloride composition may burn if the temperature of the jacketing material exceeds a specific temperature and will then produce smoke which may be a serious hazard. It would be an advantage to provide an inside cable and method for making it in which the flame retardancy is increased beyond that made available by the use of aflame retardant jacket material. According to the present invention, there is provided an inside cable comprising a plurality of insulated electrical conductors forming a core which is surrounded by a flame retardant Jacket, the interstices between conductors in the core being filled with a flame retardant powder. In the above structure, the flame retardant powder may contain IOO; calcium carbonate or bea composition of flame retardant powder materials based on calcium carbonate. Alternatively, the flame retardant powder may consist of 100% hydrated alumina or polyvinylidene fluoride or a composition of flame retardant powders based upon one of these materials. - It Is recognized that when an inside telecommunication cable burns, then the plasticizer in the jacket material assists in the flame spread. One reason for this is that the plasticizer upon being heated, nows along the jacket both along the inner and the outer surfaces. The reason for the flame retardant powder assisting in the prevention of flame spread is not clearly understood but It is thought that there is a combination of factors which minimizes the flame spread. For instance, it is considered that retardant powder restricts the flow of the plasticizer down the inside surface of the jacket material which in many inside telecommunication cable constrtrN M Y w a loose fit upon the core. Further to this, it is felt that the flame retardant powder transfers the heat from the initially localized burning area into the powder, whereby the heat available for promoting flame spread along the jacket is dissipated. A further reason is that the location of the powder immediately within the jacket displaces oxygen which would be otherwise available for the promotion of combustion and hence it is extremely difficult for the flame spread to occur down the inside of the tube. The immediate location of the powder also means that the insulated conductors on the outside of the core have a covering of powder and this increases the difficulty for flame to spread from the jacket onto the insulation of the conductors themselves. There is the added advantage, of course, that the smoke output is reduced substantially when the flame spread is minimized by the presence of the powder which also effectively douses the flame. On the other hand, when hydrated alumina powder is used, it is felt that its presence causes a cooling action upon the burning area as the heat releases the water of hydration which also acts directly to douse the flames. The fire retardant material used for the jacket may be polyvinylchloride or it may be a fluorinated material which minimizes the flame spread to a more localized area than is possible with polyvinyl chloride. The smoke output from a fluorinated material is sIgnificantly less than is obtained with polytinylchloride. It is also envisaged that the insulation surrounding the conductors in the core may be formed from polyvinylchoride or a composition thereof either with the use of a polyvinyldiloride or polyvinyl chloride composition jacket or with a jacket having fluorinated materials in the composition. The present invention also includes a method of manufacturing an inside telecommunication cable, this method comprising providing a core of insulated electrical conductors, filling Interstices between the conductors in the core with a flame retardant powder and providing a jacket around the powder filled core in which the jacket is formed from alflame retardant material. Embodiments of the present invention will now be described, by way of example, with reference to the accompanying drawing which is a crossAsectional view through a cable forming one of the embodiments. In an inside telecommunication cable 10, as shown in Figure I, a core 12 is formed from a plurality of pairs of electrical conductors 14 insulated with a polyvinylchloride composition and which have been twisted together and bound with a binding tape (not shown) in conventional manner. Surrounding the core 12 is a jacket. 15 of extruded polymeric material which is, in fact, a flame retardant material of polyvinylchloride composition. This composition was a normal polyvinyl chloride composition for jacketing purposes. The cable core has its interstices between the insulated conductors filled with a flame retardant powder which in this case is 100; calcium carbonate powder of U.3 micron size. A sample of the cable according to the embodiment (designated 'B' in the following table) was tested for flame spread conditions by causing a localized area of the cable to commence burning at a temperature of around 5500C. The test was conducted in a Steiner tunnel under normal flame spread and smoke rating test conditions according to the test standards of Underwriter's Laboratory. The flame spread and smoke rating characteristics were compared with a sample of the same cable structure in which' no flame retardant powder was used. This latter sample is designated 'A' in the following table. Then a comparison was made with further samples of the same cable structure in which the powder used was 100% hydrated alumina ('C' in the table) and then in sample 'D', a cable using 100% hydrated alumina, but with a jacket of a polyvinylidene fluoride composition as sold under the trademark "Kynar"PP; All the samples were tested under the same test standards. The flame spread distances and smoke quantity scales according to criteria laid down by Underwriter's Laboratory were as follows. Cable Structure Flame Spread (ft) Smoke Scale A. Cable devoid of powder 14 3.5 B. Cable and Calcium carbonate powder 14 1.75 C. Cable and hydrated alumina powder 14 1.00 D. Cable and polyvinylidene fluoride jacket (+C) 4 0.75 As may be seen from the above test results, in cable A which was devoid of powder in the interstices between conductors, the flame spread from the point of heat application was 14 feet. This was accompanied by a smoke reading of 3.5. Cable B having exactly the same cable structure as A but with the addition of calcium carbonate powder had substantially the same flame spread as cable A, It is signflficant, however, that the smoke reading of 1.75 for cable 8 is half that for cable A, thus Indicating that the presence of the powder cut down substantially on the smoke emissions. Cable C also had a flame spread of 14 feet, but the smoke emissions were further reduced as is shown by the smoke reading of 1.00. Cable D is significantly superior to cables A, B and C, not only because it further, reduced the smoke emissions, but also because it reduced, in impressive fashion, the flame spread distance to 4 feet. The above tests show that when a flame retardant powder is used to fill the interstices in telecommunications cable, then immediately, a significant drop in smoke emissions result, thereby decreasing the possibility of fatalities being caused through smoke content in a fire even though the actual flame spread may be similar as in samples A, B and C. The actual reduction in smoke emissions is dependent upon the type of powder used. In addition, the type of powder used may also increase resistance to flame spread as is clear when polyvinylidene fluoride powder was used in cable D. Flame spread in this case was below 3016 of that in the other cables. In the sample D tested, it is believed that the presence of the powder prevented the plasticizer in the polyvinylchloride from progressing down the inside of the jacket material, and, as plasticizer tends to detract from the flame retardant characteristics of the jacket, then avoidance of flow of a plasticizer assists in ninimifng the flame spread. Further, It is believed that the heat in the burning area is absorbed by the powder thus minimizing the amount of heat available to promote flame spread into adjacent areas of the jacket. The oxygen available to promote combustion is also reduced by the replacement of. oxygen within the interstices of the core with the powder which also covers the outer insulated conductors, thus reducing the chance of flame spread to the insulation on the conductors themselves. Finally, a further test was conducted to show that a change in the composition of the jacket could effect a reduction in smoke emission. In this further test, a cable sample the same as cable 'D', but with the polyvinylidene fluoride jacket replaced by another PVC composition shown below, was tested in the same manner as the other samples. This test showed a flame spread of 4 feet but the smoke scale reading was reduced to 0.5 from 0.75 in test 'D'. The PVC composition for this further test was: Parts by Weight PVC resin 100.00 dioctyl azelate plasticizer 28.00 *hydrated alumina 23.00 *antimony oxide 3.00 *cupric oxide 2.00 *zinc borate 4.00 *molybdenum complex (911A) 2.00 dibasic lead phthalate 6.00 dibasic lead stearate lubricant 1.00 titanium oxide 3.00 In the above composition, those marked * have smoke retarding characteristics. The cable according to the embodiments exemplified by cables B, C and D is'made by manufacturing the core, complete with its interstices filled with powder, and then enclosing the core within the jacket by a conventional jacket extrusion process. The powder may be added to the core in various ways for instance as described in U.S. Patent No. 4,100,002entitled "Method For Producing Powder Filled Cable", granted July 11, 1978 to L.E. Woytiuk, R.Y Mayer and G.B. Kepes.

Claims: CLAIMS: 1. An inside cable comprising a plurality of insulated electrical conductors (14) forming a core which is surrounded by a flame retardant jacket (15), characterised in that interstices between conductors in the core are filled with a flame retardant powder. 2. A cable according to claim 1, characterised in that it is a telecommunications cable (10) with the jacket formed from a polyvinylchloride composition and the flame retardant powder is polyvinylidene fluoride. 3. A cable according to claim 1, characterised in that it is a telecommunications cable (10) with the jacket formed from a polyvinylchloride composition and the flame retardant powder is hydrated alumina. 4. A cable according to claim 1-, characterised in that it is a telecommunications cable (10) with the jacket formed 16rom a polyvlnylchloride composition and the flame retardant powder is calcium carbonate. 5. A cable according to claim 1, characterised in that the flame retardant powder is calcium carbonate. 6. A cable according to claim 1, characterised in that the flame retardant powder is a mixture of flame retardant powders based on calcium carbonate. 7. A cable according to either claim 2 or claim 3, characterised in that the calcium carbonate powder particles are around .3 microns in size. 8. A cable according to claim 1, characterised in that the jacketing material i-s a composition containing a fluorinated substance. 9. A cable according to claim 1, characterised in that the flame retardant powder is hydrated alumina. 10. A cable according to claim 1, characterised in that the flame retardant powder is a mixture of flame retardant powders based on hydrated alumina. .11. A cable according to claim 1, characterised in that the flame retardant powder is polyvinylidene fluoride. 12. A cable according to claim 1, characterised in that the flame retardant powder is a mixture of flame retardant powders based on polyvinylidene fluoride. 13. A cable according to claim 1, characterised in that the insulation on the conductors is a polyvinylchloride composition and the jacketing material contains a fluorinated substance. 14. A method of making an inside cable comprising providing a core of insulated electrical conductors; and characterised in filling the core with a flame retardant powder and then providing around the powder filled core a jacket formed of a flame retardant polymeric material.

Inventors: CHECKLAND, JOHN ANTHONY, WOYTIUK, LEO VICTOR
Applicants: NORTHERN TELECOM LIMITED
Application year: 1982
Main classification: H01B7
IPC codes: G02B6, H01B7, H01B3