A POLYMER COMPOSITION HAVING IMPROVED STABILITY AGAINST MOISTURE AND ITS USE

Abstract: A polymer composition containing a vinyl-type polymer tends to increase in viscosity and harden in the air due to moisture when the vinyl-type polymer contains silyl radicals and an unsaturated ethylenic monomer with polarity. This has prevented the wider use of these kinds of polymer compositions for paints, sealants, and coating materials. However, when mixed with a hydrolytic ester and/or an alkyl alcohol, the polymer solution can be stabilized to moisture, so long as the content of the unsaturated ethylenic monomer with polarity is in the range of 0. 1 to 20% by weight.

Description: A Polymer Composition having Improved Stability against Moisture and its Use Field of the Invention: The present invention relates to a polymer composition retaining excellent stability even after being stored for a long time or used frequently in moist air, and useful for paints, sealants, adhesives and many other coating materials. More specifically, the present invention pertains to a polymer composition stabilized so as not to increase its viscosity in the presence of moisture with the passage of time by mixing a hydrolytic ester and/or an alkyl alcohol into the polymer composition, which chiefly contains a vinyltype copolymer whose main chain is substantially made up by a vinyl structure and which vinyl-type copolymer contains an unsaturated ethylenic monomer having polar radicals and has at least one silyl radical at end groups or side chains of each molecule. Background of the Invention: A variety of such kinds of vinyl-type copolymers have so far been known to persons having ordinary skill in the art. These vinyl-type copolymers adhere to inorganic matter due to the silyl radicals which they contain; they also tend to harden, forming a cross-linkage among molecules, in the presence of moisture at ambient temperature. Accordingly, they have been used in paints, adhesives, sealants, silane-coupling agents and the like, in spite of their increasing viscosity after prolonged storage or frequent use in humid air. It is thus necessary to keep these polymer compositions dry in a closed container. Even then, any trace of moisture collecting on top of the polymer compositions inevitably detracts from their -value as a commercial product before use. Therefore, there has been a need for improvement such that their solution viscosity does not increase too much in the presence of moisture with the passage of time. In regard to this point, several patent publications have been concerned with the improvement of the polymer stability against moisture. For example, United States Patent Publication No. 4043953 describes how the addition of a hydrolytic reactive silane to an organic silane polymer improves polymer stability to moisture. More specifically, this patent publication has disclosed that when 0.5 to 15 % by weight of a hydrolytic reactive silane, XnSi(OR)4 n' where X stands for an organic radical having 1 to 12 carbon atoms, R stands for methyl, ethyl, 2-methoxymethyl, 2-ethoxyethyl, and acyl radicals having less than 6 carbon atoms, and n is an integer from 0 to 2, is added to an organic silane polymer, which is produced by reacting a monomer having the radical CH2=Cs with acrylatealkoxysilane, methacrylatealkoxysilane, or vinylalkoxysilane, based upon the weight of the organic silane polymer, the pot life of the organic silane is improved in the presence of a hardening agent. What is more, in United States Patent Publication No. 4157321 there is a description concerned with an organic polymer very stable to moisture which is composed of: (a) an unsaturated ethylenic monomer possessing the radical = and a compound represented by RSiXnR? 3-n' where R stands for a monovalent organic group having double bonds,R' stands for a monovalent hydrocarbon group, and n is an integer from 1 to 3; (b) 0.5 to 25 parts by weight of a hydrolytic monomer selected from the group consisting of an organic silane monomer having a hydrolytic radical, and trialkylorthoformates, or (c) 2 to 50 parts by weight of an alkyl alcohol of which the alkyl radical has 1 to 4 carbon atoms. However, neither U.s.patent publication 4043953 nor 4157321 has an illustration of monomers with a structure CH2=Cx or zC=C' in which such polar groups as the hydroxyl, carboxylic, acid anhydride, amido, or amino radical are contained. On the contrary, the U.S. patent publication 4043953 describes that when some monomer containing an active hydrogen like those in the hydroxyl, carboxylic, and amido radical is added to an organic silane polymer, the stability of that polymer is lowered and gelation tends to occur as a result. Thus it is a fact that no polymer composition with good stability to moisture has- been known until today, although it was to be expected that other mechanical properties like adhesion to organic matter are improved when polar radicals, such as hydroxyl, carboxylic, acid anhydride, amido, and amino radicals, are introduced into monomers to be copolymerized. Surprisingly enough, the present inventors found that a polymer composition is stabilized by mixing a hydrolytic ester and/or an alkyl alcohol, even though any monomer having polar radicals is contained in the polymer composition, so long as the content of the monomer is within the range from 0.1 to 20 % by weight, and they finally accomplished the present invention. Brief Summary of the Invention: It is an object of the present invention to provide a polymer composition retaining an excellent stability for moisture even after a prolonged storage or frequent use in air and favorably applicable to paints, sealants, and many kinds of coating materials. The object of the present invention can be accomplished by a polymer composition with an improved stability for moisture, which consists of a vinyl-type copolymer, a hydrolytic ester, and/or an alkyl alcohol, wherein the main chain of the said vinyl-type copolymer is substantially made up from a vinyl polymer and the vinyl-type copolymer has at least one silyl radical combined with a hydrolytic radical at end groups or in side chains of each molecule, and contains 0.1 to 20 56 by weight of an unsaturated ethylenic monomer having a polar radical as a copolymeric unit. Detailed Description of the Invention: The vinyl-type copolymer of this invention should contain at least one silyl radical, but may contain more than one silyl radical in each molecule. Generally, these silyl radicals can be described by the general formula EMI5.1 where X represents a hydrolytic radical;(R1)and(R2)repre- sent hydrogen atoms,or alkyl, aryl, and aralkyl radicals any of which have 1 to 10 carbon atoms; and n is an integer from 1 to 3 inclusive. The hydrolytic group (hydrolytic radical) may, for example, be a halogen alkoxy, acyloxy, ketoximate, amino, acid amide, aminoxy, mercapto or alkenyloxy group. The above unsaturated ethylenic monomer includes any monomer which has hydroxyl, carboxylic, acid anhydride, amido, or amino groups. For example, the unsaturated ethylenic monomer includes monomers which have such hydroxyl radicals as have2-hydroxyethylacrylate, 2-hydroxyethylmethacrylate, 2hydroxypropylacrylate, 2-hydroxypropylmethacrylate, 2hydroxyvinylether, N-methylolacrylamide, and Aronix 5700 (a product of Toagosei Chemical Industry Co., Ltd.) ; such carbo xlic radicals as have acrylic acid, methacrylic acid, itaconic acid, and fumaric acid; such acid anhydride radicals as has maleic acid anhydride; such amido radicals as have acrylamide, methacrylamide, itaconic acid diamide, alphaethylacrylamide, crotonamide, fumaric acid diamide, and maleic acid diamide;; such amino radicals as have diethylaminoethylacrylate, diethylaminoetbylmethacrylate, diethylaminoethylmethacrylate and aminoethylvinylether. These unsaturated ethylenic monomers are used alone or in combination; the amount to use is generally in the range from 0.1 to 20 56 by weight, preferably in the range from 0.5 to 10 56 by weight, based on the weight of the vinyl-type copolymer. Although the molecular weight of the vinyl-type copolymer is not particularly limited, it is preferred to be in the range from 1,000 to 30,000 lest the stability of the polymer composition for moisture be impaired when a large amount of the unsaturated ethylenic monomer is used. Especially, when more than one kind of ethylenic monomers are used together, the molecular weight of the vinyl-type copolymer should preferably be 10,000 or less. The process for producing the vinyl-type copolymer can be modified in various ways, but the following two processes seem to be commercially most acceptable and therefore preferred: (A) Process including a silylation reaction between a vinyl-type polymer having carbon double bonds and a hydrosilane: This reaction is catalyzed by transition elements in group VIII of the periodic system of-elements. The hydrosilane employed for the above process has the general formula EMI7.1 where R1 represents a monovalent hydrocarbon radical selected from alkyl, aryl, and aralkyl radicals any of which have 1 to 10 carbon atoms; X stands for a hydrolytic group, and n is an integer from 1 to 3 inclusive. Examples of such hydrosilanes are halogenosilanes like methyldichlorosilanej trichlorosilane, and phenyldichlorosilane; alkoxysilanes like methyldiethoxysilane, methyldimethoxysilane, phenyldimethoxysilane, trimethoxysilane, and triethoxysilane; acyloxysilanes like methyldiacetoxysilane, phenyldiacetoxysilane, and triacetoxysilane; aminoxysilanes like methyldiaminoxysilane, triaminoxysilane, methyldiaminosilane, and triaminosilane; bis(cyclohexylketoxymate) methysilane, methyldiisophenoxysilane and triisopropenoxysilane. The amount of hydrosilanes to use is not critical; however, their amount is preferred to be 0.5 to 2 times the total amount of carbon double bonds contained in the vinyltype copolymer per mole. If, however, much more of the hydrosilane is used in the reaction, the excess amount may only be collected later for reasons of economy. For the above preparation of the polymer composition according to the present invention cheap and reactive halogenosilanes can easily be utilized. Nevertheless, the vinyl-type compolymer with silyl radicals, produced by the use of halogenosilanes, rapidly hardens at room temperature while liberating hydrogen chloride when exposed to air; accordingly, this copolymer has an intensive odour and attacks most substances near or in contact with it. This drawback limits the practical use of the polymer. In such cases, it is desirable to substitute the halogen radical contained-for some radical having a hydrolytic function in order that the vinyl-type copolymer may be employed practically using a method which is, for example, described in the published Japanese Patent Application No. 91546/79. There is virtually no restriction to the preparation of the vinyl-type copolymer for the inventive polymer composition, except that in this process variant (A) the vinyl-type copolymer should contain an unsaturated ethylenic monomer having other polar radicals than hydroxyl. That is, it is appropriate if this copolymer chiefly contains acrylic or methacrylic esters such as methylacrylate, methylethacrylate, ethylacrylate, ethylmethacrylate, butylacrylate, butylmethacrylate, 2-ethylhexylacrylate, 2-ethylhexylmethacrylate, glycidylacrylate, glycidylmethacrylate, and the like, styrene, alpha-styrene, vinyl chloride, vinyl acetate, and other analogous monomers. Further to these vinyl compounds which may be contained in the vinyl-type copolymer alone or in admixture, a small amount of allylacrylate, allylmethacrylate, ordiallylphthalate may also be included in the vinyl-type copolymer by means of radical polymerization. Thus, carbon double bonds can optionally be introduced into the end groups or side chains of the vinyl copolymer before silylation of the vinyl-type copolymer. In this case, the number of silyl radicals to be introduced to the vinyl-type copolymer can be previously determined via the amount of the above allyl monomers. The molecular weight of the vinyl-type copolymer can be adjusted freely by adding chain transfer agents like n-dodecylmercaptane or t-dodecylmercaptane, if necessary; in this case, the polymerization is carried out with or without solvents. If solvents are required, non-reactive solvents, such as ethers, hydrocarbons, and acetic esters are preferably employed. According to the described process for producing the vinyl-type copolymer of the present invention, transition elements are required as catalyst to bring the hydrosilanes into the place of the carbon double bonds of the vinyltype copolymer. The catalysts are selected from platinum, rhodium, cobalt, palladium, and nickel of group VIII of the periodic system. The silylation can be carried out at a temperature ranging from 50 to 1500 C for approximately 1 to 10 hours. (B) Process including a copolymerization of a vinyl compund and a reactive silyl compound: This process is performed by radical polymerization between a vinyl compound and a silane represented by the general formula EMI10.1 where(R1)stands for a monovalent hydrocarbon radical selected from alkyl, aryl, and aralkyl radicals any of which have 1 to 10 carbon atoms;(R2)stands for an organic radical having double bonds capable of polymerization; X stands for a hydrolytic group and n is an integer from I to 3 inclusive. Specific examples of preferred silanes which are useful for the above process for preparing the vinyl-type copolymer contained in the inventive polymer composition are: EMI10.2 EMI11.1 These silanes can be produced in various ways. For instance, they can be produced by reacting acetylene, allylacrylate, allylmethacrylate, or diallylphthalate with methyldimethoxysilane, methyldichlorosilane, trimethoxy silane, or trichlorosilane in the presence of the above mentioned transition element catalyst. According to this process, it is possible to use not only any monomer applicable in the first mentioned process A, but also unsaturated ethylenic monomers1 not mentioned in process A. The copolymerization is performed by ordinary solution polymerization, in which process the vinyl compounds and the silanes are reacted with the aid of a radical initiator at a temperature ranging with the aid of a radical initiator at a temperature ranging from 50 to 1500 C. Chain transfer agents, such as n-dodecyl mercaptane and t-dodecylmercaptane, are also added to the reaction in order to suitably adjust the molecular weight of the copolymer if required. Solvents may or may not be used; if solvents are used, non-reactive ones like ethers, hydrocarbons, and acetic esters are preferred. The hydrolytic group in the silyl group containing vinyl resin obtained by the method (B) can be changed as described hereinbefore in connection with the method (A). In this way a vinyl-type copolymer can be obtained the main chain of which is substantially made up from a vinyl polymer which has at least one silyl radical combined with a hydrolytic radical at the end groups or side chains of each molecule, and contains 0.1 to 20 % by weight of an unsaturated ethylenic monomer having a polar radical. Hydrolytic esters which are preferably used in the polymer composition according to this invention include trialkylorthoformates, such as trimethylorthoformate, triethylorthoformate, tripropylorthoformate, and tributylorthoformate, and hydrolytic organic silicone compounds represented by the general formula R4 nSiXn, in which X stands for a hydrolytic radical; R stands for a monovalent organic radical which may or may not contain functional groups; and nis an integer from 1 to 4, preferably either 3 or 4, such as-Xethy-ltrimethöxysilate,r-chloropropyltri- methoxysilane, methyltriethoxysilane, ethyltriethoxysilane, phenyltriethoxysilane, methyltriacetoxysilane, vinyltrimethoxysilane, y -methacryloxypropyltrimethoxysilane, y -mercaptoprOpyltrimethoxysilane, tetramethylorthosilicate, tetraethylorthosilicate, tetrapropylorthosilicate and tetrabutylorthosilicate. Preferred alkyl alcohols used in the polymer composition of this invention have preferably 1 to 10 carbon atoms in their alkyl moiety. Specific examples of preferred alkyl alcohols include methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, iso-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, n-amyl alcohol, iso-amyl alcohol, hexyl alcohol, octyl alcohol and cellosolve z . The amount of these alkyl alcohols is preferably in the range from 0.1 to 100 parts by weight per 100 parts by weight of the vinyl-type copolymer. The vinyl-type copolymer of this invention becomes hard while forming a cross-linkage of net-work structure when exposed to air. The hardening rate varies with the ambient temperature, relative humidity, and types of hydrolytic radicals employed. Therefore, before preparing the vinyl-type copolymer, some thought should be given to the type of hydrolytic radical to be used. In the polymer composition of the present invention, a hardening agent may or may not be used for hardening the vinyl-type copolymer. If a hardening agent is required, the following agents are preferably employed: alkyltitanium; metal salts of carboxylic acids, such as tin octylate, dibutyltin dilaurate, lead octylate; organic tin compounds of the sulfide or mercaptide type, such as monobutyltin sulfide, and dioctyltin dioctylmercaptide; acidic catalysts, such as phosphoric acid, p-toluenesulfonic acid, and phthalic acid; amines, such as tetraethylenepentamine, triethylenediamine, and n-P - aminoethyly - aminopropyltrimethoxysilane; alkaline catalysts such as potassium hydroxide, and sodium hydroxide. The amount of these hardening agents is preferred to be within the range from 0.001 to 10 56 by weight based upon the weight of the vinyl-type copolymer. A polymer composition of the present invention, which is made up from the vinyl-type copolymer, the hydrolytic ester, and/or the alkyl alcohol by mixing, is useful not only per se but also as a base material for paints and other- coating materials, because it is able to harden at ambient temperature and below. As a matter of fact, the polymer composition rapidly hardens at room temperature, and leaves an extremely lusterous coat on surfaces. In addition, it is also possible to increase the hardness of the coat by further adding compounds like-ethylsilicate and/or silane coupling agents to the polymer composition. Moreover,the inventive polymercomposition can readily be mixed into any kind of conventional paints, and coat ing materials. such as lacquer, acrylic lacquer, thermo setting acrylic paint, alkyd-type paint, melamine-type paint, epoxy-type paint, etc. in order to improve their adhesion, weathering resistance, and other properties desirehese paints. On the other hand, various kinds of fillers or pigments, for example silica, calcium carbonate, magnesium carbonate, titanium oxide, iron oxide, or fiberglass, can be mixed into the polymer composition as well. In view of such a variety of modifications, the present polymer composition can be effectively applied to coatings and sealants for aircraft, buildings, automobiles, glassware, as well as in treating agents for various inorganic materials Similarly, the polymer composition is so adherent that it can be used alone or in combination with other adhesives to stick an inorganic material to another inorganic material, an organic material to another organic one, or an inorganic material to an organic material. Particularly in the last case, the inventive composition proves to be much more effective in improving adhesion than the conventional adhesives. The present invention will be understood more easily in reference to the following examples; however, those examples are intended to illustrate the invention and are not to be construed as limiting the scope of the invention. Example 1: A solution of 2 g of azoisobutyronitrile dissolved in a mixture of 30 g of styrene, 16 g of allylmethacrylate, 20 g of methylmethacrylate, 19 g of n-butylmethacrylate, 14 g of butylacrylate, 3 g of diethylaminoethylacrylate, and 2 g of n-dodecylmercaptane were added dropwise to 70g of xylene and heated at 900C in a reactor. The reaction was conducted for 10 hours. As a result, there was obtained a vinyl-type copolymer with allyl-type unsaturated radical having a molecular weight of 8,000. Infrared spectroscopy showed that there was an absorption band attributed to carbon double bond at 1648 cm 1. After that, 40 g of the solvent was removed from the polymer solution. Subsequently, an isopropanol solution containing 1.5 g of methyldimethoxysilane and 0.0005 g of chloroplatinic acid was added to 16 g of the vinyl-type copolymer, and the reaction was carried out at 90 OC for 6 hours in a closed vessel. Infrared spectroscopy showed that the absorption band at 1648 cm 1 disappeared. In this way, the vinyltype copolymer with silyl radicals was produced. Example 2: A solution of 2 g of azobisisobutyronitrile dissolved in a mixture of 30 g of styrene, 22 g of y- methacryloxypropyltrimethoxysilane, 22 g of methylmethacrylate, 15 g of n-butylmethacrylate, 18 g of butylacrylate, 4 g of acrylamide and 10 g of n-butanol was added dropwise to 70g of xylene and heated at 900C in a reactor. The reaction was conducted for 10 hours. As a result, a vinyl-type copolymer with silyl radicals which has a molecular weight of 14,000 was produced. Example 3: A solution of 2 g of azobisisobutyronitrile dissolved in a mixture of 22 g of CH2=C(CH3)COo(CH2)3Si(OCH3)3, 52 g of methylmethacrylate, 15 g of n-butylmethacrylate, 18 g of butylacrylate 2 g of maleic acid anhydride, was added dropwise to 70 g of xylene and heated at 700C in a reactor, and the re-- action was performed for 10 hours. A vinyl-type copolymer with silyl radical having a molecular weight of 9,000 was obtained. Example 4: A solution of 2 g of azobisisobutyronitrile dissolved in a mixture of 30 g of styrene, 22 g of CH2=C(CH3)COO(CH2)3 Si(OCH3)3, 22 g of methylmethacrylate, 15 g of n-butylmethacrylate, 18 g of butylacrylate, 4 g of 2-hydroxyethylmethacryl ate and 4 g of n-dodecylmercaptane was added dropwise to 70 g of xyLene and heated at 900C in a reactor, and the reaction was performed for 10 hours. A vinyl-type copolymer with silyl radicals having a molecular weight of 6,000 was obtained. Example 5: In the reaction mixture of Example 4, 4 g of 2hydroxyethylmethacrylate was replaced by 2 g of methacrylic acid. The reaction was conducted in similar manner- and a vinyltype copolymer with silyl radicals having a molecular weight of 6,500 eas obtained. Example 6: In the reaction mixture of Example 4, 4 g of ndodecylmercaptane, and 4 g of 2-hydroxyethylmethacrylate were replaced by 4 g of acrylamide, 2 g of maleic acid anhydride, and 10 g of n-butanol. The reaction was conducted in similar manner and a vinyl-type copolymer with silyl radicals having a molecular weight of 5,000 was obtained. Titanium oxide was mixed into the polymer solutions obtained in the examples 1 to 6 respectively to prepare white enamels by means of a ball-mill. Mixing was conducted such that the ratio of the polymer to the titanium oxide was 1 : 1 in the solid state. After stabilizers (see Table I) had been added, these white enamels were diluted to a specific consistency and left to stand in a closed atmosphere at 500 C for 1 month to investigate the change in viscosity (case I). Independently, the six kinds of clear polymer solutions of examples 1 to 6 containing no titanium oxide were left to stand in a closed atmosphere under the same conditions as the above in order to see the change in viscosity after 3,000 ppm of water had been added (case II). The results are summarized in Table I. It can easily be seen from these examples that the polymer compositions of the present invention all prove to be excellent in stability against moisture, because they show only a slight change in viscosity. In Table I OFM and OSE stand for trimethylorthoformate and tetraethylorthoformate, respectively. TABLE I white enamel clear solution (case I) (case II) stabilizer added original one month original one month later later Example 1 methanol (10 pts) 250 cps 300 cps - Example 2 (i) no stabilizer 250 2,000 250 cps 5,000 cps (ii) methanol (3 pts) 250 400 250 300 OSE (5 pts) Example 3 vinyltrimethoxy- 250 600 250 500 silane (5 pts) Example 4 methanol (10 pts) OFM (1 pts) 250 500 250 300 OSE (10 pts) Example 5 methanol (10 pts) 250 600 250 300 OSE (7 pts) Example 6 (i) no stabilizer 250 2,000 250 5,000 (ii) methanol (10 pts) OFM (1 pts) OSE (10 pts)

Claims: EMI20.1 <tb> What <SEP> Is <SEP> Claimed <SEP> Is: <tb> <SEP> (1) <SEP> A <SEP> polymer <SEP> composition <SEP> having <SEP> improved <SEP> stability <tb> against <SEP> moisture, <SEP> comprising <SEP> a <SEP> vinyl-type <SEP> copolymer, <SEP> a <SEP> hydro <tb> lytic <SEP> ester, <SEP> and/or <SEP> an <SEP> alkyl <SEP> alcohol, <SEP> in <SEP> which <SEP> the <SEP> main <SEP> chain <tb> of <SEP> the <SEP> vinyl-type <SEP> copolymer <SEP> is <SEP> substantially <SEP> made <SEP> up <SEP> from <SEP> a <tb> vinyl <SEP> polymer <SEP> and <SEP> in <SEP> which <SEP> the <SEP> vinyl-type <SEP> copolymer <SEP> has <SEP> at <tb> least <SEP> one <SEP> silyl <SEP> radical <SEP> and <SEP> hydrolytic <SEP> radical <SEP> at <SEP> end <SEP> groups <tb> or <SEP> in <SEP> side <SEP> chains <SEP> of <SEP> each <SEP> molecule, <SEP> and <SEP> in <SEP> which <SEP> the <SEP> vinyl <tb> type <SEP> copolymer <SEP> contains <SEP> 0.1 <SEP> to <SEP> 20 <SEP> % <SEP> by <SEP> weight <SEP> of <SEP> an <SEP> un <tb> saturated <SEP> ethylenic <SEP> monomer <SEP> as <SEP> a <SEP> copolymeric <SEP> unit <SEP> having <tb> at <SEP> least <SEP> one <SEP> polar <SEP> radical. <tb> (2) ' A polymer composition as claimed in claim 1, in which the unsaturated ethylenic monomer contains an amido radical of a carboxylic acid as the polar radical. (3) A polymer composition as claimed in claim 1, in which the unsaturated ethylenic monomer contains a carboxylic radical as the polar radical. (4) A polymer composition as claimed in claim 1, in which the unsaturated ethylenic monomer contains an acid anhydride radical as the polar radical. (5) A polymer composition as claimed in claim 1, in which the unsaturated ethylenic monomer contains a hydroxyl radical as the polar radical. (6) A polymer composition as claimed in claim 1, in which the hydrolytic ester is trialkylorthoformate. (7) A polymer composition as claimed in claim 1, in which the hydrolytic ester is an organic silicone compound. (8) A polymer composition as claimed in claim 1, in which the hydrolytic ester is a mixture of trialkylorthoformate and a hydrolytic organic silicone compound. (9) A polymer composition as claimed in claim 1, in which 0.1 to 50 parts by weight of the hydrolytic ester are contained per 100 parts by weight of the vinyltype copolymer. (10) A polymer composition as claimed in claim 1, in which the alkyl alcohol has 1 to 10 carbon atoms in its alkyl moiety. (11) A polymer composition as claimed in claim 1, in which 0.1 to 100 parts by weight of alkyl alcohol are contained per 100 parts by weight of the vinyl-type copolymer. (12) A polymer composition as claimed in claim 1 in which the molecular weight of the vinyl-type copolymer is in the range of 1,000 to 30,000. (13) Use of the polymer composition according to any of claims 1 to 12 in coating materials, especially n paints, and as adhesives.

Inventors: FURUKAWA, HISAO, KATO, YASUSHI
Applicants: KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1981
Main classification: C08L43
IPC codes: C08K5, C09J143, C08L33, C08F8, C09D143, C08F230, C08L57