A PROCESS FOR THE PREPARATION OF AN AROMATIC HYDROCARBON MIXTURE

Abstract: In a process for the preparation of an aromatic hydrocar­ bon mixture, a H₂/CO mixture is contacted with a catalyst mixture containing a first catalyst which is capable of convert­ ing the H₂/CO mixture into oxygenated compounds (e.g. a Zn-Cr mixture containing 60-80%Zn) and as a second catalyst a crystalline iron silicate with a SiO₂/Fe₂O₃ ratio of 30-50, and characterized by its X-ray powder diffraction pattern: The process is carried out at a temperature of between 200 and 500°C, a pressure of 1-150 bar and a space velocity of 50-5000 NI of gas/l of catalyst/h.

Description: A PROCESS FOR THE PREPARATION OF AROMATIC HYDROCARBONS AND AROMATIC HYDROCARBONS SO PREPARED The invention relates to a process for the preparation of an aromatic hydrocarbon mixture from a mixture of carbon monoxide and hydrogen using a mixture of two catalysts of which one is capable of catalyzing the conversion of an H2/CO mixture into acyclic oxygen-containing hydrocarbons and the other is a crystalline silicate capable of catalyzing the conversion of acyclic oxygen-containing hydrocarbons into aromatic hydrocarbons. Said crystalline silicates are characterized in that they have the following properties after calcination for one hour in air at 5000C: a) an X-ray powder diffraction pattern which comprises as strongest lines, the four lines mentioned in Table A; b) in the formula which represents the compositon of the silicate expressed in moles of the oxides and in which an oxide of a trivalent metal A occurs, in addition to oxides of hydrogen, silicon and optionally of alkali and/or alkaline earth metal, the SiO2/A203 molar ratio (for the sake of brevity further designated m in this patent application) is 10-100. TABLE A d(A) Relative intensity 11.1 + 0.2 VS 10.0 + 0.2 VS 3.84 + 0.07 S 3.72 + 0.06 s in which the letters used have the following significance: VS = very strong; S = strong. During an investigation by the Applicant as regards the above-mentioned process employing catalyst mixtures in which the crystalline silicate component used is an aluminium silicate it was found that both the activity and the selectivity of the catalyst mixtures depend on the value of m of the aluminium silicate in the above-mentioned range. The catalyst mixtures have a high activity and a low selectivity. For application of the process on a commercial scale, a catalyst mixture is required which possesses both a high activity and a high selectivity. Further investigation by the Applicant in respect of the above-mentioned process showed that this requirement can be met by using a crystalline silicate possessing the properties mentioned under a) and b) and containing iron as trivalent metal, provided that the value of m of the iron silicate is selected in a narrow range. It was found that catalyst mixtures in which the crystalline aluminium silicate is replaced by a crystalline iron silicate having a value of m of 10-100, possess an activity which is highly dependent on the value of m and -a high selectivity which is independent of the value of m. By incorporating a crystalline iron silicate having a value of m of 30-50 into the catalyst mixtures, catalyst mixtures are obtained having a high selectivity and an activity which is comparable with the high activity of a catalyst mixture in which a crystalline aluminium silicate occurs. The present patent application therefore relates to a process for the preparation of an aromatic hydrocarbon mixture in which process an H2/CO mixture is contacted with a mixture of two catalysts, one of which is capable of catalyzing the conversion of an H2/CO mixture into acyclic oxygen-containing hydrocarbons and the other is a crystalline iron silicate possessing the properties mentioned under a) and of which the value of m mentioned under b) is 30-50. In the process according to the invention an H2/CO mixture is used as starting material. Such a mixture may very suitably be prepared by steam gasification of a carbonaceous material. Examples of such mazerials are brcvncoal, anthracite, coke, crude oil and fractions thereof as well as oils derived from tar-sand and bituminous shale. The steam gasification is preferably carried out at a temperature between 900 and 1500 C and a pressure between 10 and 50 bar. In the process according to the invention it is preferred to start from an H2/CO mixture, the molar ratio of which is between 0.25 and 1.0. The process according to the invention is preferably carried out at a temperature of between 200 and 5000C and in particular between 300 and 4500C, a pressure of 1-150 bar and in particular of 5-100 bar and a space velocity of 50-5000 and in particular of 300-3000 Nl of gas/I of catalyst/h. In the process according to the invention a mixture of two catalysts is used which for the sake of simplicity will be designated catalysts X and Y. Catalyst X is the catalyst which is capable of catalyzing the conversion of an H2/CO mixture into acyclic oxygen-containing hydrocarbons and catalyst Y is the crystalline iron silicate. As catalysts X use is preferably made of catalysts which are capable of converting an H2/CO mixture into essentially methanol and/or dimethyl ether. Catalysts which contain zinc together with chromium are very suitable for the present purpose. 1hen using a catalyst of this type it is preferred to select a catalyst in which the atomic percentage of zinc based on the sum total of zinc and chromium is at least 60Ev and in particular 60-80S. It is preferred to use catalyst mixtures which contain 1-5 parts by volume of catalyst X per part by volume of catalyst Y. The crystalline iron silicate which is present in the catalyst mixtures as catalyst Y is, inter alia, defined with reference to the X-ray powder diffraction pattern. It should contain as strongest lires the four lines mentioned in Table A. The complete X-ray powder diffraction pattern of a typical example of an iron silicate eligible for application according to the invention is shown in Table B: TABLE B d(2) Rel. int. d(A) Rel. int. 11.1 100 4.oo 3 10.0 70 3.84 57 8.93 1 3.72 31 7.99 1 3.64 10 7.42 1 3.44 5 6.68 7 3.34 3 6.35 11 3.30 5 5.97 18 3.25 2 5.70 7 3.05 5 5.56 10 2.98 12 5.35 2 2.96 3 h.98 6 2.86 2 h.60 h 2.73 2 h.35 5 2.60 2 4.25 7 2.48 3 2 2 2.40 2 The crystalline iron silicates which are used in the catalyst mixtures can be prepared starting from an aqueous mixture containing the following compounds: one or more compounds which contain an organic cation(R) or from which such a cation is formed during the preparation of the silicate, one or more silicon compounds, one or more iron compounds and optionally one or more compounds of an alkali and/or alkaline earth metal(M). The preparation takes place by maintaining the mixture at elevated temperature until the silicate has been formed and by subsequently separating the silicate crystals from the mother liquor and by washing, drying and calcining the crystals. In the aqueous mixture from which the silicates are prepared the various compounds should be present in the following ratio, expressed in moles of the oxides: (M)2/nO : R2O = 0-20, P n S; = 0.01-0.5, SiO2 : Foe20 > 30-100, and H20 : SiO2 = 5-50; n is the valency of M. During the preparation of the silicates it is preferred to start from a basic mixture in which M is present in a sodium compound and R in a tetrapropyl ammonium compound. Although the crystalline silicates which are used in the process according to the invention are designated as iron silicates, they may, in addition to iron contain a small quantity of aluminium. The silicon compounds which are eligible from an economic point of view for the preparation of crystalline silicates on a technical scale, contain as a rule a small quantity of aluminium as impurity. This aluminium is usually found at least in part in the prepared silicate. The silicates prepared in the above manner may contain alkali and/or alkaline earth metal ions. Using suitable exchange methods they may be replaced by other cations such as hydrogen ions or ammonium ions. The crystalline iron silicates which are used in the catalyst mixtures preferably have an alkali metal content of less than 0.1% by weight and in particular of less than 0.05% by weight. If desired, a binder material, such as bentonite or kaolin may be incorporated in the catalyst mixtures. The process according to the invention can very suitably be carried out by passing the feed in upward or downward direction through a vertically arranged reactor in which a fixed or moving bed of the relevant catalyst mixtures is present. The process according to the invention may also very suitably be used as the first stage of a two-stage process for the conversion of an H2/CO mixture into an aromatic hydrocarbon mixture. In this case at least the C2 -fraction of the reaction product from the first stage is contacted with a catalyst containing one or more metal components having catalytic activity for the conversion of an H2/CO mixture into acyclic hydrocarbons, which metal components are selected from the group formed by cobalt, nickel and ruthenium, with the proviso that if the feed for the second stage has an H2/CO molar ratio of less than 1.5, water is added to this feed and that in the second stage a bifunctional catalyst combination is used which in addition to the metal components with catalytic activity for the conversion of an H2/CO mixture into acyclic hydrocarbons, also contains one or more metal components with catalytic activity for the conversion of an H20/CO mixture into an H2/CO2 mixture. The invention also relates to the aromatic hydrocarbons prepared with the aid of the present process. The invention will now be elucidated with reference to the following Example. EXA1 2'LE Six crystalline silicates (silicates 1-6) were prepared by heating mixtures of SiO2, NaOH, (C3H7)4NOH and either Nay102 2 or Fe(N03)3 in water in an autoclave at autogenous pressure at 150 C for 24 hours. After cooling of the reaction mixtures the resultant silicates were filtered off, washed with water until the pH of the washing water was approximately 8, dried at 1200C and calcined at 500 C. The silicates 1-6 had the following properties: a) thermally stable to a temperature above 8000C; b) an X-ray powder diffraction pattern essentially corresponding to that mentioned in Table B; c) a value for m as indicated in Table C: TABLE C Silicate No. SiO2/Fe203 SiO2/A1203 1 25 2 33 3 37 4 70 5 - 40 6 ¯ 70 The molar composition of the aqueous mixtures from which the silicates 1-6 were prepared may be represented as follows: 25 SiO2 . x Fe203 . y A1203 33 Na20 . 4.5[(C3H7)4N]2O . 450 H2O wherein x and y have the values shoun in Table D: : TABLE D Silicate No. x y 1 0.80 - 2 0.66 3 0.50 4 0.25 5 - 0.33 6 - 0.20 From the silicates 1-6 the silicates 7-12 were prepared by boiling the silicates 1-6 with 1.0 molar NH4N03 solution, washing with water, boiling again with 1.0 molar NH4N03 solution and by washing, drying at 1200C and calcining at 500 C. Six catalyst mixtures (catalyst mixtures A-F) were subsequently prepared by mixing a ZnO-Cr203 composition with each of silicates 7-12. The atomic Zn percentage of the ZnO-Cr203 composition was 70%. A7l catalyst mixtures contained 10 parts by weight of the ZnO-Cr203 composition per part by weight of silicate. The catalyst mixtures A-F were tested for the preparation of an aromatic hydrocarbon mixture from an H /CO mixture. Testing was carried out in a 50 ml 2 reactor which contained a fixed catalyst bed having a volume of 7.5 ml. In six experiments an H2/CO mixture having an H2/CO molar ratio of 0.5 was passed over each of the catalyst mixtures A-F at a temperature of 375 C, a pressure of 60 bar and a space velocity of 1000 Nl.l .h . In all cases a product was obtained, + the C5+ fraction of which consisted for over 30% by weight of aromatics. The other results of the experiments are given in Table E: TABLE E Exp. Catalyst Silicate Conversion C + selectivity No. mixture No. of the syn- by weight % on thesis gas C after 10 h d to 1 A 7 32 75 2 B 8 65 75 3 C 9 64 75 4 D 10 55 73 5 E 11 66 6 F 12 66 Of the experiments mentioned in Table E only experiments 2 and 3, in which use was made of a catalyst mixture which contained a crystalline iron silicate having an m value between 30 and 50, are experiments according to the invention. The experiments 1 and 4, in which a catalyst mixture was used which contained a crystalline iron silicate having an m value below 30, and above 50 respectively, and the experiments 5 and 6, in which a catalyst mixture was used containing a crystalline aluminium silicate, fall outside the scope of the invention. They have been incorporated for comparison. It appears from the results mentioned in Table E of the experiments 4 and 5 relating to the conversion of an H2/CO mixture into an aromatic hydrocarbon mixture using catalyst mixtures which contain a crystalline aluminium silicate having an m value of 10-100 that both the activity and the selectivity of these catalyst mixtures are independent df the m value of the aluminium silicate and also that these catalyst mixtures have a high activity and a low selectivity. From the results mentioned in Table E of the experiments 1-4 relating to the conversion of an H2/Co mixture into an aromatic hydrocarbon mixture using catalyst mixtures which contain a.crystalline iron silicate having an m value of 10-100, it appears that the selectivity of these catalyst mixtures has a high value which does not depend on m and that the activity of these catalyst mixtures is highly dependent on m and has a high value at an m value of 30-50.

Claims: C L A I M S 1. A process for the preparation of an aromatic hydrocarbon mixture, characterized in that a mixture of carbon monoxide and hydrogen is contacted with a mixture of two catalysts one of which is capable of catalyzing the conversion of an H2/CO mixture into acyclic oxygen containing hydrocarbons and the other is a crystalline iron silicate which silicate has the following properties after calcination for one hour in air at 5000C: a) an X-ray powder diffraction pattern which comprises as strongest lines the four lines mentioned in Table A, and b) in the formula which represents the composition of the silicate expressed in moles of the oxides and in which iron oxide occurs in addition to oxides of hydrogen, silicon and optionally of alkali and/or alkaline earth metal, the SiO2/Fe203 molar ratio is 30-50. TABLE A d Relative intensity 11,1 + 0.2 VS 10.0 + 0.2 VS 3.84 + 0.07 s 3.72 + o.o6 .- S in which the letters used have the following significance: VS = very strong; S = strong. 2. A process as claimed in claim 1, characterized in that it is carried out at a temperature between 200-500 C, a pressure of 1-150 bar and a space velocity of 50-5000 Nl of gas/l of catalyst/h. 3. A process as claimed in any one of claims 1 and 2, characterized in that the catalyst mixture is made up of a catalyst X and a catalyst Y, catalyst X being capable of converting an H2/CO mixture into essentially methanol or dimethyl ether and catalyst Y being the crystalline iron silicate. 4. A process as claimed in claim 3, characterized in that catalyst X is a composition which contains zinc together with chromium. 5. A process as claimed in claim 4, characterized in that in the catalyst X the atomic percentage of zinc based on the sum total of zinc and chromium is at least 60%. 6. A process as claimed in claim 5, characterized in that in the catalyst X the atomic percentage of zinc based on the sum total of zinc and chromium is 60-80%. 7. A process as claimed in any one of claims 3-6, characterized in that the catalyst mixture contains 1-5 parts by volume of catalyst X per part by volume of catalyst Y. 8. A process as claimed in any one of claims 1-7, characterized in that the catalyst mixture contains a crystalline silicate having an alkali metal content of less than 0.05 by weight. 9. A process as claimed in any one of claims. 1-8, characterized in that it is used as the first stage of a two-stage process for the preparation of an aromatic hydrocarbon miiture from an H2/CO mixture, at least the C2 -fraction of the reaction product from the first stage being contacted in a second stage with a catalyst containing one or more metal components having catalytic activity for the conversion of an H2/CO mixture into acyclic hydrocarbons, which metal components are selected from the group formed by cobalt, nickel and ruthenium, with the proviso that if the feed for the second stage has an H2/CO molar ratio of less than 1.5, water is added to this feed Elnd that in the second stage a bi-functional catalyst is used 7,which in addition to the metal components with catalytic activist for the conversion of an H2/CO mixture into acyclic hydroc-arbons, also contains one or more metal components with catalytic activity for the conversion of an H20/CO mixture into am H2/C02 mixture. 10. Aromatic hydrocarbon mixtures prepared using a process as claimed in any one of claims 1-9.

Inventors: BOERSMA, MICHAEL ADRIAAN MARIA, POST, MARTIN FRANCISCUS MARIA, SCHAPER, LAMBERT
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1981
Main classification: C07C15
IPC codes: B01J23, C10G2, C07C1, C07B61, B01J29, C07C67, C07C15