PROCESS FOR PREPARING POLYARYLATES IN TWO STEPS

Abstract: Described herein is a process for preparing crystalline polyarylates which comprises (a) forming a crystalline polyarylate prepolymer having a reduced viscosity of from 0.05 to about 0.4 dl/g by reacting at least one diester deriva­ tive of a dihydric phenol with at least one aromatic dicarbox­ ylic acid in the presence of a solvent, at a temperature of from about 250° to about 300°C, and (b) heating the prepolymer so formed below its melting point to form a crystalline polyary­ late having a reduced ivcosity of from about 0.45 to about 1.2 dl/g.

Description: BACKGROUND OF THE INVENTION This invention is directed to a process for preparing crystalline polyarylates which comprises: (a) forming a crystalline polyarylate prepolymer having a reduced viscosity of from 0.05 to about 0.4 dl/g by reacting at least one diester derivative of a dihydric phenol with at least one aromatic dicarboxylic acid in the presence of a solvent, at a temperature of from about 250 to about 300°C, and (b) heating the prepolymer so formed below its melting point to form a crystalline polyarylate having a reduced viscosity of from about 0.45 to about 1.2 dl/g. Polyarylates are polyesters derived from a dihydric phenol, particularly 2,2-bis(4-hydroxyphenyl)propane also identified as Bisphenol-A, and an aromatic dicarboxylic acid, particularly mixtures of terephthalic and isophthalic acids. These polyarylates are high temperature, high performance thermoplastic polymers with a good combination of thermal and mechanical properties. They also have good processability which allows them to be molded into a variety of articles. Many processes have been described in the literature for the preparation of polyarylates. One such process is the diacetate process. In the diacetate process, a dihydric phenol is converted to its diester derivative, which is then reacted with an aromatic dicarboxylic acid to form the polyarylate. U.S. Patents 3,684,766 issued August 15, 1972, and 3,780,148 issued December 18, 1973, describe a four step diacetate process for producing polyarylates. In the patented process, in the first step a prepolymer is formed from, for example, a diacetate, such as Bisphenol-A diacetate, and an aromatic acid, in the presence of a catalyst. In the second step, the prepolymer so formed is comminuted into small particles. In the third step, these particles are contacted with a crystallizing agent to crystallize the polyester. This may be accomplished by placing the particles in a fluidized bed reactor and contacting them with the crystallizing agent in the reactor. The patent states that the crystallizing step is necessary because it increases the melting point of the prepolymers so that the molecular weight can be built up to a satisfactory value without fusing or sticking of the particles. The fourth step involves heating the crystallized bisphenol polyester in the presence of an inert gas, optionally in a fluidized bed, at a temperature below the melting point and for a period of time which is sufficient to achieve an inherent viscosity of at least 0.5 in the final polymer. The crystallization step described in U.S. Patents 3,684,766 and 3,780,148 is a slow, time consuming and expensive operation. In the process of the present invention high molecular weight crystalline polyarylates are achieved without such a crystallization step. U.S. Patent 4,075,173 (= FR 23 39 636) describes the preparation of copolyesters by reacting an aromatic dicarboxylic acid, a diacetate of Bisphenol-A, and an acetate of p-hydroxybenzoic acid. Various processes for producing polyarylates by the reaction of Bisphenol-A and terephthalic and isophthalic acids are reviewed in this patent. The following process for producing polyarylates, identified as route (1), is described in column 2, of the patent: This process is the diacetate process as described herein, or the "Acetate Process" as defined in the patent. Column 2 of the patent states: "The route (1) is not desirable because the undesirable coloration and deterioration of polymer are particularly remarkable as disclosed in the above-mentioned literature." Further, column 3 of the patent states: "On the other hand, the route (1), Acetate process, is economically advantageous because the materials used are cheap and the operation is simple. For example, diacetate of bisphenol-A, a monomer for Acetate process, is synthesized by merely reacting acetic anhydride and bisphenol-A. Consequently, it may be said that, if the fatal drawbacks of Acetate process, coloration and deterioration, are solved, Acetate process will become the most superior process." Thus, the skilled workers in the field of polyarylate chemistry realize that the existing processes for producing polyarylates have one or more deficiencies, and that a need exists to develop a viable diacetate process for producing polyarylates. In U.S. Patent 4,075,173, a copolyester was prepared by the diacetate process by a solid-state polymerization of low molecular weight prepolymers without using crystallizing agents. The patentees state that their Acetate process is possible only when specific monomers are combined to form the prepolymer. These monomers are the diacetate of bisphenol-A, terephthalic acid and/or isophthalic acid and an acetate of p-hydroxybenzoic acid. The prepolymer is then converted to the desired high molecular weight polymer by solid state polymerization. Specifically, in the process of said patent, a prepolymer is first prepared by condensing the acetate of p-hydroxybenzoic acid, bisphenol-A diacetate with isophthalic and/or terephthalic acids at a temperature of from 200 to 380°C for 1 to 10 hours. Catalysts capable of accelerating an ester exchange reaction can be used. The prepolymer is pulverized or pelletized and heated under reduced pressure or in an inert gas to convert it into a high molecular weight polymer. Thus, as stated in U.S. Patent 4,075,173, the diacetate processes for producing polyarylates are generally unsuitable since they are either economically unattractive and/or produce a commercially unmarketable product. The process of said U.S. Patent 4,075,173 requires the use of p-hydroxybenzoic acid and produces a particular class of polyarylate copolymers. As previously stated, U.S. Patents 3,684,766 and 3,780,148 require the use of crystallizing agents in a crystallizing step. Therefore, a need exists for an economical and practical diacetate process for producing high molecular weight crystalline polyarylates. EP―A―00 26 684 describes a process for preparing polyarylates having a reduced viscosity of from about 0.5 to greater than 1.0 dl/gm, which process comprises reacting at least one diester derivative of a dihydric phenol with at least one aromatic dicarboxylic acid in the presence of from about 10 to about 60 weight percent, based on the polyarylate produced, of a diphenyl ether compound, at a temperature of from about 260 to about 350°C. EP―A―00 26 121 describes a process for preparing polyarylates which process comprises reacting a diester derivative of a dihydric phenol with an aromatic dicarboxylic acid in the presence of from about 10 to about 60 weight percent of a diphenyl ether compound at a temperature of from about 260 to about 350°C and in the presence of a magnesium catalyst. EP―A―00 26 120 describes a process for preparing polyarylates of improved color which process comprises reacting a diester derivative of a dihydric phenol with an aromatic dicarboxylic acid in the presence of from about 10 to about 60 weight percent of at least one cycloaliphatic, substituted aromatic or heteroaromatic compound, which compounds contain at least one benzylic and/or tertiary hydrogen atom, at a temperature of from about 260 to about 350°C. Optionally, the process may be carried out in the presence of a magnesium, manganese, or zinc catalyst. EP―A―00 35 269 describes a process for preparing polyarylates which process comprises reacting a diester derivative of a dihydric phenol with an aromatic dicarboxylic acid in the presence of from about 10 to about 60 weight percent of at least one halogenated and/or etherated substituted aromatic or heteroaromatic compound, at a temperature of from about 260 to about 350°C. In said european applications supra , reaction of one or more dihydric phenols with an aromatic dicarboxylic acid produces prepolymers and polyarylate polymers or copolymers that essentially do not crystallize during the reaction and recovery steps. The present process produces polyarylate prepolymers and high molecular weight polyarylate polymers and copolymers which are crystalline. In the diacetate process for producing polyarylates, problems exist which must be economically and practically solved in order to have a viable, economically attractive process. One problem when a diester derivative of a dihydric phenol is reacted with an aromatic dicarboxylic acid in the molten state is that sublimation of the diacid occurs. This disrupts the stoichiometry of the reaction and the polyarylate produced is not of acceptable molecular weight. To prevent sublimation of the diacid, several techniques have been developed. These include the use of large amounts of solvents together with a variety of catalysts and generally long reaction times in the polymerization process. However, these techniques are quite costly and do not provide an optimum process. Another problem when a diester derivative of a dihydric phenol is reacted with an aromatic dicarboxylic acid in the molten state is that the viscosity of the system increases dramatically towards the end of the reaction and therefore the reaction becomes diffusion controlled (the molecules are not close enough to insure rapid reaction) rather than kinetically controlled. Also, the polymer product is difficult to handle (i.e., removal from the reactor) due to this high viscosity. Yet another problem in the production of polyarylates by the diacetate process is that a carboxylic acid is a by-product of the reaction of a diester derivative of a dihydric phenol with an aromatic dicarboxylic acid. In order to provide an efficient, economical process and a high molecular weight polyarylate, the acid, for example, acetic acid, has to be conveniently and efficiently removed. It has now been discovered that crystalline polyarylates can be efficiently and economically produced by the process of this invention. The utilization of a solvent and the specific ratio of isophthalic to terephthalic acid in preparing a crystalline prepolymer in the process of this invention prevents sublimation of the aromatic dicarboxylic acid; thus producing polyarylates of acceptable molecular weight. Also, the solvent provides for better removal of the acetic acid by-product. Further, an additional benefit in using a solvent is that the viscosity of the system is decreased. This decrease in viscosity provides a faster reaction time since better mixing of the reactants occurs which allows the reaction to proceed under kinetic control. Further, the presence of a solvent during the preparation of the prepolymer allows for the formation of crystallites. After a certain molecular weight is reached, spontaneous crystallization takes place. Thus, a free flowing highly crystalline powder containing the solvent is obtained. This crystalline powder is suitable for further polymerization in the solid phase by heating below its melting point. Therefore, the crystallization step as is required in the process of U.S. Patents 3,684,766 and 3,780,148 is thus eliminated. The unexpected findings of this invention are thus quite important. Typical melt polymerizations are indeed very difficult with high melting, high crystalline polyarylates because of the high temperatures required. Solution polymerizations are difficult due to the general insolubility of crystalline polymers. In contrast, the process of this invention allows easy formation of crystalline intermediates as well as highly crystalline, high melting polyarylates. DESCRIPTION OF THE INVENTION The present invention is directed to a process for preparing crystalline polyarylates which comprises: (a) forming a polyarylate prepolymer having a reduced viscosity of from 0.05 to about 0.4 dl/g by reacting at least one diester derivative of a dihydric phenol with a mixture of isophthalic and terephthalic acid in the presence of a solvent at a temperature of from 250 to 300°C, and (b) heating the prepolymer below its melting point to form a crystalline polyarylate having a reduced viscosity of from about 0.45 to about 1.2 dl/g. The polyarylate prepolymer formed in step (a) is in the form of a free-flowing crystalline powder. It is heated below its melting point to form the crystalline polyarylate generally at temperatures of from about 300 to about 350°C. The polyarylate prepolymer is formed by reacting at least one diester derivative of a dihydric phenol having the following formula: wherein R is independently selected from an alkyl radical having from 1 to 6 carbon atoms, preferably methyl or cycloalkyl having from 4 to 7 carbon atoms; y is independently selected from alkyl groups of 1 to 4 carbon atoms, chlorine or bromine; z independently has a value of from 0 to 4; and R′ is independently selected from a divalent saturated aliphatic hydrocarbon radical, particularly alkylene or alkylidene radicals having from 1 to 8 carbon atoms, especially C(CH₃)₂, cycloalkylene or cycloalkylidene radicals having up to and including 9 carbon atoms, O, S, SO, SO₂, and CO; x is 0 or 1; and isophthalic and/or terephthalic acid. The diester derivative of the dihydric phenol is prepared by reacting a dihydric phenol with an acid anhydride derived from acids containing from 2 to 8 carbon atoms under conventional esterification conditions. The preferred acid anhydride is acetic anhydride. Generally, the dihydric phenol is reacted with the acid anhydride in the presence of an esterification catalyst, either in the presence or absence of a solvent. However, this reaction may also be conducted in the absence of a catalyst. The dihydric phenols that may be used in this invention include the following: 2,2-bis-(4-hydroxyphenl)propane, bis-(2-hydroxyphenyl)methane, bis-(4-hydroxyphenyl)methane, bis-(4-hydroxy-2,6-dimethyl-3-methoxyphenyl)methane, 1,1-bis-(4-hydroxyphenyl)ethane, 1,2-bis-(4-hydroxyphenyl)ethane, 1,1-bis-(4-hydroxy-2-chlorophenyl)ethane, 1,1-bis-(3-methyl-4-hydroxyphenyl)ethane, 1,3-bis-(3-metyl-4-hydroxyphenyl)propane, 2,2-bis-(3-phenyl-4-hydroxyphenyl)propane, 2,2-bis-(3-isopropyl-4-hydroxyphenyl)propane, 2,2-bis-(2-isopropyl-4-hydroxyphenyl)propane, 2,2-bis-(4-hydroxyphenyl)pentane, 3,3-bis-(4-hydroxyphenyl)pentane, 2,2-bis-(4-hydroxyphenyl)heptane, 1,2-bis-(4-hydroxyphenyl)-1,2-bis-(phenyl)-propane, 4,4′-(dihydroxyphenyl)ether, 4,4′-(dihydroxyphenyl)sulfide, 4,4′-(dihydroxyphenyl)sulfone, 4,4′-(dihydroxyphenyl)sulfoxide, 4,4′-(dihydroxybenzophenone), hydroquinone, and naphthalene diols. These dihydric phenols may be used individually or in any combination which when reacted with an aromatic dicarboxylic acid produce polyarylate prepolymers which are crystalline. The preferred dihydric phenol is 2,2-bis(4-hydroxyphenyl)propane. As aromatic dicarboxylic acids are used in this invention terephthalic acid and isophthalic acid. The isophthalic acid to terephthalic acid ratio is within the range of from 0:100 to 25:75. The preferred ranges are from 10:90 to 0:100. Also, from 0.5 to 20 weight percent based on the reaction mixture of phthalic acids and dihydric phenol of aliphatic diacids containing from 2 to 10 carbon atoms, such as adipic acid, and sebacic acid, may be additionally used in the polymerization reaction. The polyarylate prepolymer having a reduced viscosity of from 0.05 to 0.4 dl/g is prepared by reacting at least one diester derivative of a dihydric phenol with at least one phthalic acid in the presence of a solvent at a temperature of from 250 to 300°C, preferably from 275 to 295°C. The preparation of the polyarylate prepolymer is generally conducted in an inert atmosphere (such as argon or nitrogen). The process is carried out either under atmospheric pressure, under vacuum or under positive pressure such that the solvent is refluxing at the reaction temperature, until the prepolymer has spontaneously crystallised from the solvent. The polymerization reaction is conducted for a period of time sufficient to produce a polyarylate prepolymer having a reduced viscosity of from 0.05 to 0.4 dl/g, which time is generally less than about 10 hours. The reaction time is generally in the range of from 4 hours to 8 hours, depending on the particular polyarylate being prepared. The polymerization reaction may be carried out batchwise or continuously and by using any apparatus desired. Moreover, the reactants may be added to the polymerization zone in any way or order desired. The preparation of the polyarylate prepolymer is carried out in the presence of from 10 to 60, preferably from 25 to 60, and most preferably, from 30 to 60 weight percent, based on the weight of the polyarylate prepolymer produced of an organic solvent. The preferred organic solvents are a diphenyl ether compound as described in European application 00 26 684, supra , a cycloaliphatic substituted aromatic or heteroaromatic compound, as described in European application 00 26 120, supra , and a halogenated and/or etherated substituted aromatic or heteroaromatic compound, as described in European application 00 35 269, supra , or mixtures of these. The diphenyl ether compound, as described in European application 00 26 684, supra , may be substituted. These substituents are selected from chlorine, bromine or any substituent which does not interfere with the polyarylate forming reaction or the reaction forming the diester derivative of the dihydric phenol. Additionally, the diphenyl ether compound may be used with up to 50 weight percent of other compounds, such as various biphenyls or any other compounds which do not interfere with the polyarylate forming reaction or the reaction forming the diester derivative of the dihydric phenol. The cycloaliphatic compounds, or substituted aromatic or heteroaromatic compounds, as described in European application 00 26 684, supra , contain at least one benzylic and/or tertiary hydrogen atoms. These compounds have a boiling point of 150 to 350°C preferably from 180 to 280°C, and most preferably from 180 to 220°C, at atmospheric pressure. Additionally, these compounds have a solubility parameter, at a temperature of 250°C, of ±4 within the solubility parameter of the polyarylate being produced. Solubility parameter is a measure for correlating polymer solvent interaction. It is defined in "Properties of Polymers", D. W. Van Krevelen, Elsevier Scientific Publishing Co., Amsterdam-Oxford-New York, 1976, pp. 141-155, as the square root of the cohesive energy density. The cycloaliphatic compounds are of the following formulae: or; wherein R₁ is independently alkyl of 1 to 6 carbon atoms, cycloalkyl of 6 to 18 carbon atoms, and a is an integer of 1 or 2. The substituted aromatic compounds are of the following formulae: wherein R₂ is independently alkyl of 1 to 6 carbon atoms, cycloalkyl of 6 to 18 carbon atoms and aralkyl or alkaryl of 7 to 18 carbon atoms and wherein the carbon atom of R₂ attached directly to the benzene nucleus has 1 or 2 attached hydrogen atoms, and b is an integer of 1 to 6. wherein R₃ is independently alkyl of 1 to 6 carbon atoms, cycloalkyl of 6 to 18 carbon atoms, c is an integer of 1 or 2, and n is an integer of 1 to 6 The heteroaromatic compounds are of the following formula: wherein A is S, O, or ―CH=N―, R₄ is independently alkyl of 1 to 6 carbon atoms, or cycloalkyl of 6 to 18 carbon atoms and wherein the carbon atom of R₄ attached directly to the heteroarmatic nucleus has 1 or 2 attached hydrogen atoms, and d is an integer of 1 to 4. The preferred compounds encompassed by structures (I) through (V) include xylenes, cumene, diethylbenzene, diisopropyl benzene, tetrahydronaphthalene or decahydronaphthalene. Additionally, the cycloaliphatic, substituted aromatic or heteroaromatic compounds may be used with up to 90 weight percent of other compounds such as diphenyl ether or dimethylsulfone. The halogenated and/or etherated substituted aromatic or heteroaromatic compounds, as described in European application 00 35 269, supra , are of the formulae: wherein X is independently Cl, Br, F, or OR₆, a is an integer of 1 to 5, R₅ is independently alkyl of 1 to 16 carbon atoms, cycloalkyl of 6 to 18 carbon atoms, aryl of 6 to 18 carbon atoms, or aralkyl or alkaryl of 7 to 18 carbon atoms, R₆ is independently alkyl of 1 to 16 carbon atoms or cycloalkyl of 6 to 18 carbon atoms, and b is integer of 0, 1, or 2; wherein X, R₅ and a are as previously defined, and c is an integer of 0 to (8-a). The heteroaromatic compounds are of the following formula: wherein A is 0, S, or ―CH= N―, X and R₅ are as previously defined, d is an integer of 1 to 4 and f is integer of 0 to (4-d). The compounds encompassed by structures (VI) through (VIII) include 1,2,3-trichlorobenzene; 1,2,4-trichlorobenzene, 1,2- or 1,3- or 1,4-dichlorobenzene; 1,2,3- or 1,2,4- or 1,3,5-trimethoxybenzene; 1,2- or 1,3- or 1,4-dibromobenzene; chlorobenzene; bromobenzene; 1-chloronaphthalene; 2-chloronaphthalene; 1-bromonaphthalene; 2-bromonaphthalene; 1,2- or 1,3- or 1,4-dimethoxybenzene; 2-bromotoluene; 2-chlorotoluene; 4-bromotoluene; 4-chlorotoluene; anisole; 2-methylanisole; 3-methylanisole; 4-methylanisole; 2-chloroanisole; 3-chloroanisole; 4-chloroanisole; 2-bromoanisole; 3-bromoanisole and 4-bromoanisole. Additionally, the halogenated and/or etherated substituted aromatic or heteroaromatic compounds may be used with up to 90 weight percent of other compounds such as diphenyl ether or dimethylsulfone. The amount of said solvents could vary during the polymerization reaction. For example, it may be advantageous to increase progressively the amount of these solvents to maintain the reaction medium at constant viscosity. A catalyst may be used to accelerate the rate of polyarylate prepolymer formation. All the conventional catalysts capable of accelerating an ester exchange reaction are suitable for use herein. These include metal salts, generally the Group VII and VIII metal salts, such as magnesium, manganese or zinc salts. The salts are generally organic acid salts and include acetates, propionates, benzoates, oxylates, acetylacetonates, or mixtures thereof. A preferred catalyst is magnesium acetate. The catalyst is present in the reaction in a catalytically effective amount which can be, for example, from 1 to 1,000, preferably from 10 to 50, parts per million, based on the weight of the polyarylate prepolymer produced. The diester derivative of the dihydric phenol may be formed, in situ , by adding the dihydric phenol together with the acid anhydride, an aromatic dicarboxylic acid and solvent to the reactor and the reaction carried out in a single reaction zone under combined esterification and polymerization conditions as described above. Additionally, the diester derivative of the dihydric phenol may be first prepared in the presence or absence of solvent, and then an aromatic dicarboxylic acid, and optionally, a solvent added directly to the same reaction vessel, with the polymerization being carried out under the conditions described above. The polyarylate prepolymer produced is in the form of a free-flowing crystalline powder containing the solvent. It is a crystalline powder in that it displays patterns characteristic of crystallinity under x-ray diffraction and it has a well defined melting point which is a characteristic of its crystallinity. In the second step of the process of this invention, the polyarylate prepolymer as prepared above, is heated below its melting point to form a crystalline polyarylate having a reduced viscosity of from 0.45 to 1.2 dl/g. The heating step may be accomplished in many different ways. The polyarylate prepolymer may be heated in the reaction vessel below its melting point generally from 300°C to 350°C in an inert atmosphere in order to increase its molecular weight to the desired level. Alternatively, the polyarylate prepolymer may also be heated below its melting point under reduced pressure, or in a fluid bed reactor. The parameters for advancing molecular weight depend upon a number of factors, such as the initial reduced viscosity, the final reduced viscosity desired and the particular polyarylate. Nitrogen is the preferred fluidization gas, but other inert gasses may be used. Generally, the polyarylate prepolymer is heated from 0.5 to 8 hours. The process of this invention produces crystalline polyarylates having a reduced viscosity of from 0.45 to 1.2, preferably from 0.6 to 0.8 dl/g, as measured in an appropriate solvent such as p-chlorophenol, m-cresol, or others known in the art (0.2 g/dl at 49°C). The polyarylates may be prepared in the presence of materials such as molecular weight regulators, antioxidants, and the like. The polyarylates obtained by the process of this invention may be used together with the well-known additives such as plasticizers, pigments, lubricating agents, mold release agents, stabilizers or inorganic fillers. Examples In these examples, all parts and percentages are on a weight basis unless otherwise specified. Comparative Example A Preparation of Prepolymer The apparatus used herein consisted of a 500 ml round bottom flask fitted with a nitrogen inlet, mechanical stirrer, a vacuum jacketed vigreux column connected to a distillation head and collector flask. 124.8 grams of bisphenol-A diacetate, 33.2 grams of isophthalic acid, 33.2 grams of terephthalic acid, and 63 grams of diphenyl ether were added to the flask. The reaction mixture was purged with nitrogen for about 20 minutes. The reaction mixture was then heated to 275°C by immersion of the apparatus in a heating medium. Acetic acid started to distill when the temperature reached 260°C. The reactants were maintained at 275°C for 2 hours. The temperature was then raised to 290―295°C and the reactants maintained at this temperature for 2 hours. No apparent distillation of acetic acid was observed during the last hour. A clear yellow product formed. This was allowed to cool to ambient temperature. 3 grams of the product was dissolved in methylene chloride (10 percent solids) and coagulated in isopropanol. The resultant material, which was in the form of a fluff, was washed with isopropanol 2 times and then dried at 120°C (for 24 hours at <1.33 mbar. The reduced viscosity of this polymer was 0.25 dl/gm as measured in chloroform (0.50 g/100 ml at 25°C). Preparation of Polymer To a test tube (25 by 200 mm) fitted with a vacuum adapter, was added 6 grams of the prepolymer as prepared above. The pressure in the test tube was reduced to < 5.32 mbar. After 2 minutes at ambient temperature, the test tube was heated to 345―350°C, and the prepolymer was maintained at this temperature for 30 minutes. It appeared as a foaming mass. The test tube was allowed to cool to ambient temperature. The polymer was recovered by breaking the test tube. The solid material recovered had a deep yellow color. The reduced viscosity of this polymer was 0.70 dl/g as measured in chloroform (0.50 g/dl at 25°C). Example 1 Preparation of Prepolymer To the apparatus described in Comparative Example A was added 124.8 grams of bisphenol-A diacetate, 16.6 grams of isophthalic acid, 49.8 grams of terephthalic acid and 60 grams of diphenyl ether. The resulting mixture was purged with nitrogen for 20 minutes. The mixture was then heated to 275°C. Distillation of acetic acid started when the reaction temperature reached 260°C. The reaction mixture was heated to 275°C and maintained at this temperature for 2 hours and then heated to 290―295°C maintained at this temperature for 2 hours. No apparent distillation of acetic acid occurred during the last hour. The thick yellow product formed was cooled to ambient temperature. The product displayed a yellow opaque color. Attempts to dissolve the prepolymer in methylene chloride were not successful. This resulted in a slurry of the prepolymer in the solvent. The material was soluble in chloroform and the reduced viscosity was measured therein and found to be 0.21 dl/g. The opaque nature of the prepolymer was indicative of a crystalline material. Preparation of Polymer The procedure described in Comparative Example A for preparing a polymer from a prepolymer was exactly repeated with the prepolymer formed above. The polyarylate produced had a reduced viscosity of 0.80 dl/g as measured in chloroform (0.50 g/dl at 25°C). The prepolymer prepared in Comparative Example A was formed into a polymer by heating it at 300, 320 and 350°C. The prepolymer prepared in Example 1 was formed into a polymer by heating it at 320 and 350°C. The procedure as described in Comparative Example A was used to form the polymer. The prepolymers were heated at said temperatures for 30 minutes to advance their molecular weight (hereinafter described as advancement temperature). The amount and percent of terephthalic acid used to prepare the polymer, the reduced viscosity of the prepolymer, the advancement temperature, the reduced viscosity of the polymer, and the physical state of the polymer are shown in Table I. Examples 2 to 7 The procedure as described in Example 1 for forming a prepolymer was exactly repeated except that the amounts of terephthalic and isophthalic acids shown in Table II were charged to the reaction vessel. The prepolymer was then formed into a polymer by the procedure as described in Comparative Example A. Table II shows the weight in grams of the terephthalic and isophthalic acids used, the mole percent terephthalic acid used, based on the total amount of acid used, the reduced viscosity of the prepolymer, the advancement temperature (the polymer was advanced at this temperature for 30 minutes), the reduced viscosity of the polymer formed, the physical state of the polymer formed, and the melt transition temperature of the polymer as measured by differential scanning calorimetry. Du Pont Model 990 at 5°K/min. The melting point is a function of molecular weight and degree of crystallinity. Comparative Example B Formation of Prepolymer The procedure of Example 1 was exactly repeated using the materials of Example 5, i.e., 124.8 grams of bisphenol-A diacetate, 56.4 grams of terephthalic acid, and 10 grams of isophthalic acid, except that no diphenyl ether solvent was used. The prepolymer formed had a reduced viscosity of 0.31 dl/g as measured in p-chlorophenol (0.20 g/100 ml, at 49°C). Preparation of Polymer The procedure described in Comparative Example A for forming a polymer from a prepolymer was exactly repeated except that the prepolymer was heated at 350°C for 30 minutes. The polymer formed was non-homogeneous. It was a partially crystalline, partially foamed, and partially sintered mass. It had a reduced viscosity of 0.47 dl/g as measured in p-chlorophenol (0.20 g/100 ml, at 49°C). This Example shows that the presence of diphenyl ether (Example 5) allows the prepolymer to reach a higher degree of crystallinity while the absence of diphenyl ether in the preparation of the prepolymer (this Example) produces a semi-crystalline, semi-amorphous polymer which would be difficult to process. Example 8 Preparation of Prepolymer The reactor system consisted of an oil heated one gallon stainless steel reactor fitted with a nitrogen inlet, mechanical agitator, and fractionating column (packed with ceramic saddles) connected to an overhead take-off device consisting of a reflux splitter condenser and a collection device. The reactor was charged 1,200 grams of Bisphenol-A diacetate, 95.7 grams of isophthalic acid, 542.5 grams of terephthalic acid and 740 grams of diphenyl ether (35 weight percent based on polymer). The reactor system was purged with nitrogen for 20 minutes. The oil heater was turned on to raise the temperature of the reactor to 280°C (oil temperature was about 300°C). Acetic acid started to distill when the temperature reached 260°C. After about 2 hours at reflux conditions, the agitator stalled. The reactor could not be discharged. After cooling to ambient temperature, one gallon of chlorobenzene was charged to the reactor. The reactor was heated to 180°C under a nitrogen pressure of 3.5 bar. After 15 minutes, the agitator was started, the pressure dropped and the chlorobenzene began to distill off. After 60 minutes, the reactor was cooled and a free flowing particulate material was recovered. It had a reduced viscosity of 0.32 dl/g as measured in p-chlorophenol (0.20 g/100 ml, 49°C). Preparation of Polymer The procedure as described in Example 1 for preparing a polymer from a prepolymer was exactly repeated except that the prepolymer was heated at 350°C for 30 minutes. Samples before and after chlorobenzene treatment of the prepolymer, as described above, were advanced. Table III shows the reduced viscosity of the prepolymer, the advancement temperature, the reduced viscosity of the polymer, the melt transition temperature, and the heat of fusion. Heat of fusion (ΔH f ) is a measure of the enthalpy difference between the crystalline and amorphous state. For a series of polymers with a given backbone architecture, it is also a measure of the degree of crystallinity, i.e., the greater the ΔH f , the more crystalline the polymer. The heat of fusion is proportional to the area under the melting transition curve as recorded by the Differential Scanning Calorimeter. This Example demonstrates that the treatment with chlorobenzene has no effect on the crystallinity of the polymer. Example 9 100 grams of the prepolymer prepared in Example 8 was placed in a 500 milliliter round bottom flask. The flask was placed on a rotary evaporator and a vacuum applied 0.67―1.33 mbar. The flask was heated at 340―350°C for 1 hour and rotated during this period. A free flowing polymer was recovered. It had a reduced viscosity of 0.61 dl/gm as measured in p-chlorophenol (0.02 g/100 ml, at 49°C). Examples 10 to 13 4 grams of the prepolymer prepared in Example 8 were placed in a fluid bed reactor. The prepolymer was fluidized with nitrogen gas preheated to the temperature and at the gas velocity, shown in Table IV. Table IV also shows the fluid bed temperature, time of advancement of the prepolymer, the reduced viscosity of the polymer formed (measured in p-chlorophenol, 0.02 g/100 ml, at 49°C) and the physical state of the polymer.

Claims: 1. A process for preparing polyarylates having a reduced viscosity of from 0.45 to 1.2 dl/g by reacting a polyarylate prepolymer having a reduced viscosity of from 0.05―0.4 dl/g ― produced by reacting at least one diester derivative of a dihydric phenol having the following formula: wherein R is independently selected from an alkyl radical having from 1 to 6 carbon atoms or cycloalkyl having from 4 to 7 carbon atoms, Y is independently selected from alkyl groups of 1 to 4 carbon atoms, chlorine, or bromine, z independently has a value of from 0 to 4 inclusive, and R′ is independently selected from a divalent saturated aliphatic hydrocarbon radical having 1 to 8 carbon atoms, a cycloalkylene or cycloalkylidene radical having up to and including 9 carbon atoms, O, S, SO, SO₂, CO, x is 0 or 1; with isophthalic and/or terephthalic acid in the presence of a solvent at a temperature of from 250 to 300°C and heating the prepolymer characterized in that for the production of crystalline polyarylates a crystalline prepolymer ― prepared by reacting the diester derivative(s) with the acids the ratio of isophthalic to terephthalic acid being from 0:100 to 25:75 in the solvent until the prepolymer has spontaneously crystallized from the solvent and in the form of a free flowing high crystalline powder is heated below its melting point. 2. A process as defined in claim 1 wherein the solvent is selected from a diphenyl ether compound, a cycloaliphatic compound or a substituted aromatic or heteroaromatic compound, and a halogenated and/or etherated substituted aromatic or heteroaromatic compound, or mixtures thereof. 3. A process as defined in claim 1 or 2, wherein the solvent is present in an amount of from 10 to 60 weight percent, preferably from 25 to 60 weight percent, based on the weight of the polyarylate prepolymer produced. 4. A process as defined in claim 1 to 3, wherein a catalyst for producing the prepolymer is used. 5. A process as defined in claim 1 to 4, wherein the prepolymer is heated under reduced pressure. 6. A process as defined in claim 1 to 5, wherein the prepolymer is fluidized in the heating. 7. A process as defined in claim 1 to 6, wherein the prepolymer is heated at a temperature of from 300 to 350°C. 8. A process as defined in claims 1 to 7 wherein the diester derivative of a dihydric phenol comprises a diester of Bisphenol A. 9. A process as defined in claim 8 wherein the diester derivative of a dihydric phenol comprises Bisphenol A diacetate. 10. A process as defined in claims 1 to 9 wherein the solvent is a diphenyl ether compound.

Inventors: BERGER, MITCHELL HARVEY, MATZNER, MARKUS, TIBBITT, MICHAEL
Applicants: AMOCO CORPORATION
Application year: 1981
Main classification: C08G63
IPC codes: C08G63