METHOD FOR FABRICATING COMPLEMENTARY SEMICONDUCTOR DEVICES

Abstract: In a process for forming a CMOS integrated circuit (10) having polysilicon gate electrodes (28, 38) the polysilicon gate electrodes (28, 38) are simultaneously doped with impurities of a single conductivity type, independently of the semiconductor substrate (18). The invention enables the avoidance of the penetration problem which arises when boron is utilized to dope polysilicon. After forming the gate electrodes (28, 38) from a polysilicon layer (128), they are covered by a mask including a silicon oxide layer (130) and a silicon nitride layer (132). Then sources (22, 34) and drains (24, 32) of the n-channel and p-channel transistors (12, 14) are formed and an implantation or diffusion barrier (148) is grown over the sources (22, 34) and drains (24, 32). The mask (130, 132) is removed over the gate electrodes (28, 38) which are then doped with an n-type impurity. Polysilicon resistors (50) may be formed by initially doping the polysilicon layer (128) to a low level of conductivity and protecting the resistor areas (50) by a further mask (138), which may be of polysilicon or silicon nitride, during subsequent doping to a high level of conductivity.

Description: METHOD FOR FABRICATING COMPLEMENTARY SEMICONDUCTOR DEVICES Technical Field This invention relates to processes of the kind for forming an integrated circuit, including the steps of providing a body of a semiconductor material having first and second active regions therein of respective first and second conductivity types, forming a silicon dioxide gate layer' encompassing a gate region within each of said active regions, forming polysilicon gate electrodes, and forming a source and a drain of a first conductivity type and of a second conductivity type respectively in said second and first active regions Background Art Reference is first made to the following definitions which are used in the present specification: "Impurity type" refers in the conventional sense to n-type (donor) or p-type (acceptor) impurities; "Conductivity" is used in the conventional sense as being a measure of the ability to conduct current, and is the reciprocal of resistivity; "Conductivity type", "n-type conductivity" and "p-type conductivity" refer to the dominant impurity- type, n-type or p-type, which a material contains. Thus the conductivity type of a polycrystalline silicon material which is heavily doped with n-type impurities and lightly doped with p-type impurities would be n-type conductivity, while the same material doped solely with p-type impurities would have p-type conductivity. In the fabrication of CMOS (complementary metal-oxide-semiconductor) devices, it is preferable to use silicon gate technology rather than metal gate- tech¬ nology. This preference for silicon gate technology arises from several advantages inherent in this type of technology. In particular, the use of silicon gate technology provides an area savings due to the better tolerances arising from the self-aligning nature of such gate structures, due to the ability to provide an additional layer of interconnect and due to the avail- ability of buried contacts. A process of the kind specified is known from U.S. Patent No. 4,063,274. According to this known process, a p-well is formed in a body of n-type semi¬ conductor material. A gate oxide layer is grown on a surface of the semiconductor body. A polysilicon layer is formed on the gate oxide layer, and from such poly¬ silicon layer polysilicon gate structures are etched. Exposed portions of the gate oxide layer are then re¬ moved to define areas where n-type regions are to be formed. Thereafter n-type impurities (phosphorus) are diffused into these areas and into the polysilicon material. Subsequently the areas where p-type regions are to be formed are exposed. With the n-type regions protected by a layer of oxide, p-type impurities (boron) are then diffused into the desired areas and into the polysilicon. The p-type diffusion is to a lower concen¬ tration than the n-type diffusion and consequently the n-type doped polysilicon remains n-type. It will be appreciated that the known process has the advantage that the polysilicon gates are all of the same conductivity type, thereby avoiding the use of a metal bridge to connect p-type gate electrodes and/or conductors with n-type gate electrodes and/or conductors. However, the known process has the disadvantage that the introduction of boron into the gate electrodes and con¬ ductors associated with the p-channel transistors during formation of their source and drain regions pro¬ duces a potential problem when scaled small geometry (i.e. very thin gate insulator) devices are being formed. This problem arises from the propensity of boron to diffuse from the gate electrodes (associated with the p-channel transistors), through the thin oxide layer which separates the gate electrodes from the under¬ lying substrate, and into the underlying substrate, thereby changing . the threshold voltage of the p-channel transistors or producing a short between their source and drain regions. In either case, this boron penetra¬ tion has a detrimental effect upon the operation of the resulting device as fully discussed by J. T. Clemens and E. F. Labuda in their publication entitled "Impurity Diffusion in SiO Layers and Related Effects on the MOS Properties of the Si-Gate Technology", Electrochemical Society Extended Abstracts, Vol. 74-1, Abstract No. 46, p. 125, May 1974. Accordingly, this processing tech¬ nique is unsuitable for the fabrication of silicon-gate VLSI circuits and other CMOS devices having very thin gate oxide p-channel transistors. Disclosure of the Invention It is an object of the present invention to provide a process of the kind specified wherein the aforementioned disadvantage is alleviated. Therefore, according to the present invention there is provided a process for forming an integrated circuit, including the steps of providing a body of a semiconductor material having first and second active regions therein of respective first and second conduc- tivity types, forming a silicon dioxide gate layer en¬ compassing a gate region within each of said active regions, forming polysilicon gate electrodes, and forming a source and a drain of a first conductivity type and of a second conductivity type respectively in said second and first active regions, characterized by the step of simultaneously doping the polysilicon gate electrodes corresponding to said first and second active regions with impurities of a single conductivity type independently of said body of semiconductor material. It will be appreciated that a process according to the invention is effective to produce an integrated circuit having polysilicon gate electrodes of a single conductivity type and a single impurity type, and is accordingly suitable for the fabrication of silicon gate V §I circuits and other CMOS devices having very thin gate electrodes. According to a further feature of the inven¬ tion, areas of high conductivity (conductors) and areas of a low conductivity (resistors) are formed from a suitably doped single layer of polysilicon. Brief Description of the Drawings One embodiment of the present invention will now be described by way of example with reference to the accompanying drawings, in which: Fig. 1 is a partial sectional view of a CMOS device fabricated according to a process embodying the principles of the present invention; and Figs. 2A-P are flow diagrams illustrating by sequential cross-sectional representation the process of the present invention for forming a CMOS device with polysilicon gate electrodes and conductors of a single conductivity, single impurity type. . Best Mode for Carrying Out the Invention Referring now to Fig. 1, there is shown in this figure a partial sectional view of a portion of a CMOS device 10 embodying the principles of the present invention. The portion of CMOS device 10 is comprised of an n-channel transistor 12, a p-channel transistor 14 and a high resistivity line 50. While the following description is primarily directed toward the fabrication of these components of the device, the description is exemplary of the fabrication of a class of devices which embody the principles of the present invention. In addition,, it should be noted that the thickness and other dimensions shown herein are selected for clarity of illustration and not to be interpreted in a limiting ι_- -5- sense. The dimensions can be smaller or larger depend¬ ing upon the operating environment in which the device is going to be used. In this regard, it should be further pointed out at this time that the thrust of microelectronics technology is toward smaller dimensions to achieve greater device density, better performance, etc. CMOS device 10 comprises a substrate 18 of one conductivity type, illustratively, n-type silicon. A p-type surface-adjacent impurity region or well 20 is formed in the substrate by diffusing p-type impurities into the substrate. The n-channel transistor 12 includes a pair of n-type impurity regions which are diffused or implanted into the substrate within the p-well 20 to form the sourc 22 and drain 24 of the transistor. The transistor 12 also includes a thin layer of gate oxide 26 and a polysilicon gate electrode 28 which overlies the channel region between the source and drain regions of the transistor. Similarly, the p-channel transistor 14 in¬ cludes a pair of p-type impurity regions which are the source 34 and drain 32 of the transistor. These impurity regions are formed by implanting or diffusing p-type impurities into the substrate. The p-channel transistor 14 includes a thin layer of gate oxide 36 and a poly¬ silicon gate electrode 38 which overlies the channel region between the source and drain regions of transistor 14. Channel stops 42 are strategically formed on the substrate 18 to electrically isolate the components of CMOS device 10. One such channel stop is located between the p-channel and n-channel transistors and is hereinafter referred to as the center channel stop. Each of the channel stops is comprised of a p τ impurity region 44, an n impurity region 46 and an oxide barrier 48. The impurity regions 44 and 46 serve to increase the field inversion voltage of the device. As mentioned above, the portion of CMOS device 10 which is shown in Fig. 1 also includes a conductor line which is generally designated by the numeral 50. Conductor line 50, which has a high resistivity and serves as a resistor element, is a layer of polysilicon which is formed over the oxide barrier 48 of the center channel stop and initially doped to a low level of conductivity. The top and lateral surfaces of this layer of silicon 50 are in turn encircled by a layer of oxide 130 to (1) protect the sidewalls of polysilicon 50 from being further doped in subsequent steps and (2) avoid direct contact between polysilicon 50 and the silicon nitride 132, to be formed over the polysilicon in a later step, thereby preventing transfer of stresses in the nitride to the polys-ilicon 50. Overlying the top surface of the silicon oxide layer 130 is a silicon nitride layer 132. The nitride 132 is formed to enable its removal at selected portions of the polysilicon conductor 50 and allow these portions to be independently doped to a high conductivity level. High resistivity conductor 50 is further enclosed by a layer of masking material 138, typically silicon nitride or polysilicon, which completely covers the top surface of silicon nitride layer 132, the lateral surfaces of silicon oxide layer 130 and a portion of the top surface of the oxide barrier 48 of the center channel stop. The layer 138 protects the initially doped low conductivity regions of polysilicon 50 from a subsequent high con¬ ductivity doping. Gate electrode 28, gate electrode 38 and high resistivity conductor 50 are all doped with n-type impurities to provide a CMOS device having gate elec¬ trodes and conductors of a single impurity type. It should be further noted that gate electrodes 28 and 38 are doped with the same concentration of impurities to form high conductivity electrical conductors while conductor line 50 is doped with a lower concentration of impurities to provide a resistor element. Accord¬ ingly, gate electrodes 28 and 38 are constructed to be of a single conductivity, single impurity type while high resistivity conductor line 50 is constructed to be of the same impurity type but of a lower conductivity. The processing technique used to dope these conductors independently of the substrate impurity regions such as 22, 24, 32 and 34 will be discussed in greater detail hereinafter. CMOS device 10 is also provided with a thick insulating layer 56 which is appropriately patterned to cover the gate structure of n-channel transistor 12, the gate structure of p-channel transistor 14 and the high resistivity conductor line 50. Insulating layer 56 electrically isolates the polysilicon gates and con¬ ductors from the overlying metal conductors 58, 60 and 62. Electrical conductor 58 electrically couples source 22 to associated electrical circuitry (not shown). Metal conductor 60 electrically couples drains 24 and 32 to each other as is typical for CMOS pairs. Finally, metal conductor 62 electrically couples source 34 to associated circuitry (not shown) such as a voltage supply. It should be further noted that those skilled in the art will readily recognize that other insulating materials, passivating materials, and electrical con¬ nections and interconnections (not shown herein) may be applied as needed to complete the protection of an integration of the transistors shown in this Figure with other components of the device. Reference is now made to Figs. 2A-P wherein the successive steps of the fabrication process of the present invention are illustrated in detail. It should be noted that many of the techniques for implementing the various steps of the fabrication method are well known in the art and may be implemented in a number of different ways which are readily apparent to those of ordinary skill in the art. Referring now to Fig. 2A, the fabrication process of the present invention in initiated by growing a layer of oxide 100 over the top surface of an n-type substrate 18 to a thickness of 6000 Angstroms (0.6 microns). As shown in Fig. 2B, oxide layer 100 is then selectively etched using conventional photolithographic techniques to provide a diffusion window 102 at each location of the chip where an impurity well is to be formed. The surface-adjacent p-well 20 is then formed by implanting or diffusing p-type ions (such as boron) into the substrate 18 through the diffusion window 102. If the p-well 20 is formed by the implantation technique, an oxide layer 100 of a thickness of about 1000 Angstroms (0.1 microns) may be left in the window 102. After implantation this oxide layer is etched away by using a conventional etching technique. If the p-well 20 is formed by the diffusion technique, on the other hand, the entire oxide layer in the window region 102 must be re¬ moved prior to diffusion. The preferred method of form¬ ing the p-well 20 is by implantation as this method en¬ ables control over the depth of the well and provides a low surface concentration of impurities for the well region. The next step of the fabrication process involves formation of channel stops which define the active regions for the transistors 12 and 14. As en- tioned above, each channel stop is comprised of a p impurity region 44, an n impurity region 46 and an oxide barrier 48. To form the channel stops, initially an oxidation and implantation barrier is formed over the substrate at each location where a transistor device is to be located. These oxidation and implantation bar- riers are shown in Fig. 2C and are formed by depositing onto the top surface of the substrate a layer of oxide 104 to a thickness of 400-600 Angstroms, a layer of nitride 106 to a thickness of 600-1200 Angstroms, and a second layer of oxide 108 to a thickness of 1200— 1600 Angstroms. These three layers 104, 106 and 108 are then patterned using conventional photolithographic tech¬ niques to provide an oxidation and implantation barrier at each location of the substrate where a transistor is to be located. The second oxide layer 108 serves to delineate the nitride layer 106 using a wet nitride etch process. In addition, the layer 108 in combination with layer 106 masks the transistor active regions during the subsequent channel stop implantation step. Two oxidation and implantation barriers are shown in Fig. 2C where they are generally designated by the numeral 110 and 112. Oxidation and implantation barrier 110 corresponds to n-channel transistor 12 and is positioned to overlie the active region of this transistor. The second oxida¬ tion and implantation barrier 112 corresponds to p-channel transistor 14 and defines the active region of this transistor. After the oxidation and implantation barriers are formed, a mask 114 is formed over the oxidation and implantation barrier 110 and all of the n-channel active regions 12 to define the n -impurity regions 46 as shown in Fig. 2C. This mask is formed by depositing a layer of photoresist over the top surface of the semi- conductor body such that the layer of photoresist com¬ pletely covers the exposed portions of the barriers. Then, using conventional photolithographic techniques, the layer of photoresist is patterned to provide the desired mask configuration 114. Mask 114 and the oxi- dation and implantation barrier 112 control formation of the n—type impurity regions 46 of the channel stops. As shown in Fig. 2C, mask 114 is arranged to have a peripheral boundary 116 which is located between the active region of the n-channel transistor 12 defined by the oxidation and implantation barrier 110, and the surface adjacent boundary of p-well 20. N-type ions are then implanted into the substrate in the presence of the photoresist mask to form the n-type impurity regions 46 of the channel stops. The photoresist mask 114 is then removed. A mask 118 is then formed over the oxidation and implantation barrier 112 and all of the p-channel transistor active regions 14 to define the p^-impurity regions 44 as shown in Fig. 2D. This mask is formed by depositing a layer of photoresist over the top sur¬ face of the semiconductor body such that the layer of photoresist completely covers the exposed portions of the semiconductor body and the oxidation and implantation barriers. Then, using conventional photolithographic techniques, the layer of photoresist is patterned to provide the desired mask configuration 118. Mask 118 and the oxidation and implantation barrier 110 control formation of the p-type impurity regions 44 of the chan¬ nel stops. As shown in Fig. 2D, mask 118 is arranged to have a peripheral boundary 120 which is spaced apart from the active region of the n-channel transistor defined by oxidation and implantation barrier 112 and the surface adjacent boundary of p-well 20. P-type impurities are then implanted into the substrate to pro¬ vide the p-type impurity regions 44 of the channel stops. See Fig. 2D. 4 . Once the p -impurity regions 44 have been formed as described above, mask 118 is removed using conventional techniques. Thereafter, the oxide barrier 48 of the channel stops is thermally grown to a thick¬ ness of 8,000-16,000 Angstroms (0.8-1.6 microns). Formation of the oxide barrier layers 48 leaves the structure shown in Fig. 2E. The next steps of the fabrication process are shown in Fig. 2F and comprise removing the oxidation and implantation barrier (by etching away oxide layers 104 and 108 and nitride layer 106), then growing gate oxide 122. It should be noted that the previously- formed oxide barriers 48 are very thick and remain after the removal of the relatively thin oxide layers 104 and 108. Conventional processing techniques are then used to grow a layer of gate oxide 122 on the top surface of the substrate to a thickness of 400 to 700 Angstroms (0.04—0.07 microns). A preferred technique is dry thermal oxidation as this produces dense and high quality oxide layers. OMPI The threshold values of the p-channel and n-channel transistors are then matched by forming surface charge layers of the appropriate conductivity-type at the interface between the substrate and gate oxide layer at each location where a p-channel and/or n-channel trans¬ istor is located. Formation of the p-channel surface charge layers is accomplished, as shown in Fig. 2G, by initially forming a photoresist mask 124 which covers the active region of each of the n-channel transistors. Thereafter, p-type dopant ions are implanted into the exposed surface areas of the substrate to form a surface charge layer 150 at the interface between the top sur¬ face of the substrate and the layer of gate oxide 122. The surface charge layer adjusts the threshold voltage of the p-channel transistors to the desired level. Mask 124 is then removed using conventional techniques. Referring to Fig. 2H, formation of the n- channel surface charge layer is done by forming a photo¬ resist mask 126 which covers the active areas of the p- channel transistors, then implanting p-type ions into the exposed n-transistor active areas of the substrate to form a surface charge layer 151 of p-type impurities at the interface between the surface of th semiconductor substrate and the layer of gate oxide thereon. Mask 126 is thereafter removed using conventional techniques. The gate electrodes and conductors are formed during the next step of the fabrication process. A layer of polycrystalline silicon 128 (polysilicon) is deposited onto the semiconductor substrate to a typical thickness of 5000 Angstroms (0.5 microns) (Fig. 21). The polysilicon 128 is then doped using n-type ions. The amount of doping is determined by the value of con¬ ductance (or resistance) desirable for the polysilicon conductor line (or resistor) 50 to be formed from the polysilicon layer 128 in a subsequent step. Then, using conventional techniques, the upper surface of the layer of polysilicon 128 is converted into a layer of silicon oxide 130 by thermal oxidation or a layer of silicon oxide 130 is deposited onto the upper surface of the polysilicon layer, to a thickness of 400-500 Angstroms (0.04-0.05 microns). A layer of silicon nitride 132 ' is then formed over the layer of silicon oxide 130 using conventional processing techniques such as chemical vapor deposition using a silicon containing gas and ammonia reactants. This layer of nitride is shown in Fig. 21 and is typically 1200-1500 Angstroms (0.12-0.15 microns) thick. The dual layer of oxide and nitride 130-132, which is also referred to herein as the oxida¬ tion and diffusion mask, serves a multiple purpose. First, it serves as an oxidation mask. Second, it serves as an implantation or diffusion mask during the n-channel and p-channel source and drain formation. Third, the oxidation and diffusion mask lends itself for selective removal after forming the source and drain barrier oxide to expose the underlying polysilicon for a high conductivity doping, as explained below. Referring to Fig. 2J, conventional photolitho- graphic techniques are then used to pattern nitride layer 132, silicon oxide layer 130 and polysilicon layer 128 into the desired combination of conductors and gate structures. Two such gate structures and one such con¬ ductor line are shown in Fig. 2J: gate structures 134 and 136 are for n-channel transistor 12 and p-channel trans¬ istor 14, respectively; conductor line 50 is formed on top of the oxide barrier 48 of the center channel stop. Once these gate structures and conductors have been formed, a short oxidation cycle is used to cap the exposed side portions of the polysilicon gates and con¬ ductors thereby protecting these portions from pene¬ tration of impurities during subsequent doping steps. This oxidation cycle forms side extensions 130A and 130B to layer 130 so that oxide layer 130 completely covers the polysilicon layer of each gate electrode and conduc¬ tor. The resulting structure is shown in Fig. 2K. Thereafter, a layer of material such as silicon nitride or polysilicon is deposited over the entire structure O PI and is patterned by conventional photolithographic techniques, forming a mask over those regions, such as conductor line 50, where low conductivity conductors (resistors) are desired. One such resistor masking layer is shown in Fig. 2K where it is designated by the numeral 138. The resistor mask 138 protects the previously doped polysilicon conductor line 50 from further doping during the high conductivity doping of the polysilicon gates and conductors. Typical thickness range of nitride mask 138 is 1200-1500 Angstroms (0.12- 0.15 microns). If the mask 138 is polysilicon, the thickness is typically 2000-4000 Angstroms, (0.2-0.4 microns) . The next step of the process, shown in Fig. 2L, is the formation of the source and drain regions of the n-channel transistors. An exemplary technique for forming this step of the process involves depositing a layer of photoresist 140 onto the substrate such that it uniformly covers the previously formed gate structures and conductor structures, then exposing and developing the photoresist to provide a window corresponding to the active region of each n-channel transistor. Such a window 142 is shown in Fig. 2L. Thereafter, referring to Fig. 2L, the source 22 and drain 24 of the n-channel transistors are formed by implanting n-type impurities through the window 142. In performing this implantation step, the gate structure 134 associated with each n- channel transistor acts as a mask which serves to align the transistor's source and drain regions with the gate electrode. The source and drain regions of the p-channel transistors are then formed as shown in Fig. 2M. As shown in Fig. 2M, conventional photolithographic tech¬ niques are used to provide a mask 144 having a window 146 corresponding to the active region of each p-channel transistor. P-type impurity ions are then implanted through the windows 146 to form the source 34 and drain 32 regions of the p-channel transistors. As with the n-channel transistors, the gate structure 136 acts as a further mask which serves to properly align the gate structure with its associated source and drain regions. Referring now to Fig. 2N, the mask 144 is removed and the oxide layer 122 overlying the source and drain regions is increased to a thickness of 2000- 2500 Angstroms (0.2-0.25 microns) to form an implantation or diffusion barrier to isolate the source and drain regions from subsequent doping of the gate electrodes and the high conductivity conductors. This step is performed by thermal oxidation of the previously formed gate oxide 122 to provide a thicker layer of oxide 148 over the source and drain regions of p-channel and n- channel transistors. It will be appreciated that during this oxidation step the oxide layer 148 is also formed over the resistor mask 138 when the mask 138 is poly¬ silicon. When mask 138 is silicon nitride the oxide barrier layer 148 is formed only over the source and drain regions of transistors 12 and 14. After this thick layer of oxide 148 has been formed over the source and drain regions, the substrate is selectively etched by using conventional photomasking techniques to remove nitride layer 132 and silicon oxide layer 130 (the oxidation and diffusion mask) from the top of each gate structure and high conductivity con¬ ductor^), thereby exposing the polysilicon layer of these gate structures and conductors. Referring now to Fig. 2P, the above-mentioned etching operation causes the polysilicon gate electrode layer 28 and 38 of the gate structures of the p-channel and n-channel transis¬ tors 14 and 12 respectively to be exposed. It should be noted, however, that the resistor masking layer 138 (or 138-148 when 138 is silicon) overlying the resistor 50 is not removed when 138 is polysilicon and only partially removed when 138 is silicon nitride because mask 138 is used to prevent this resistor from being doped simul¬ taneously with the gate electrodes. Thereafter, the exposed polysilicon gate electrodes 28 and 38 and other conductors (except 50, which is a resistor) are doped to a high conductivity using n-type impurities and conven¬ tional diffusion or ion implantation techniques. . " Typically, the polysilicon conductors and gate electrodes are doped to a high conductivity level such that their sheet resistance is less than about 100 ohms per square, typically 30 ohms per square. This is accomplished when using ion implantation techniques, for example, by means of phosphorus ions of energy 80 kev and a dose of 6 x 10 ' ions/square cm. By forming the oxide layer 148 to a thickness of 2000-2500 Angstroms (0.2-0.25 microns), the source and drain regions of the p-channel and n-channel trans¬ istors are protected during this doping step and, as a result, are not affected by it. Accordingly, the process of the subject invention dopes the source and drain regions independently of the gate electrodes and the high conductivity conductors. In addition, the process of the subject invention permits all of the gate elec- trodes and ' high conductivity conductors to be doped simultaneously to provide gate electrodes and conductors of a single conductivity, single impurity type. Referring to Fig. 1, after the gate electrodes and conductors have been doped as described above, a thick layer of insulator 56 is deposited over the device, contact cuts such as 70, 72 are made, and a layer of metal is deposited over the substrate and patterned using conventional photolithographic techniques to form metal conductors 58, 60 and 62. After metallization, a passivation coating of material such as phospho-silicate glass (not shown) may be formed over the device. From the foregoing, it can be seen that the present process is well adapted to attain all of the objects set forth hereinabove. Doping the poly gates and conductors in the manner described yields not only a CMOS VLSI circuit with all n -doped polygates and inter¬ connect lines which may be connected together without the need for an area consuming metal bridge, but also eliminates the channel doping problems associated with the p-channel transistors. In addition, this process has a feature of formation of selected portions of the interconnect lines into resistor elements by subjecting them to different doping levels.

Claims: CLAIMS : 1. A process for forming an integrated circuit, including the steps of providing a body (18) of a semiconductor material having first and second active regions therein of respective first and second 5 conductivity types, forming a silicon dioxide gate layer (122) encompassing a gate region within each of said active regions, forming polysilicon gate electrodes (28, 38), and forming a source (22, 34) and a drain (24, 32) of a first conductivity type and of a second conduc- 10 tivity type respectively in said second and first active regions, characterized by the step of simultaneously doping the polysilicon gate electrodes (28, 38) corres¬ ponding to said first and second active regions with impurities of a single conductivity type independently " 15 of said body (18) of semiconductor material. 2. A process according to claim 1, charac¬ terized in that said step of forming polysilicon gate electrodes (28, 38) includes the steps of forming a layer of polysilicon (128) over said silicon dioxide 5 gate layer (122) and defining said polysilicon layer (128) into said gate electrodes (28, 38). 3. A process according to claim 2, charac¬ terized in that said step of defining said polysilicon layer into gate electrodes (28, 38) includes the steps of forming a mask (130, 132) over said polysilicon layer 5 (128), and patterning the polysilicon layer (128) in the presence of said mask (130, 132) to form said gate elec¬ trodes (28, 38). 4. A process according to claim 3, charac¬ terized in that said step of forming a source and a drain includes doping said body (18) of semiconductor material in the presence of said mask (130, 132) to form OMPI wi p o " 4. (concluded) the sources (22, 34) and drains (24, 32) in said first and second active regions such that said sources (22, 34) and drains (24, 32) are aligned with their corres¬ ponding gate electrodes (28, 38). 5. A process according to claim 4, charac¬ terized in that said step of doping said gate electrodes (28, 38) includes forming an implantation barrier (148) over said first and second active regions, removing said mask (130, 132) over each gate electrode (28, 38), and implanting impurities of a single conductivity type into said gate electrodes (28, 38). 6. A process according to claim 5, charac¬ terized in that said" implantation barrier (148) is formed of silicon dioxide and is relatively thick com¬ pared with said silicon dioxide gate layer (122). 7. A process according to claim 6, charac¬ terized by the step of covering the side surfaces of said gate electrodes (28, 38) with a layer of silicon dioxide (130A, 130B) prior to said step of implanting impurities. 8. A process according to claim 6, charac¬ terized in that said mask includes a further layer of silicon dioxide (130) and a layer of silicon nitride (132). 9. A process according to claim 8, charac¬ terized in that the thickness of said silicon dioxide gate layer (122) is in the range of 400 to 700 Angstroms, the thickness of said polysilicon layer (128) is 5000 Angstroms, the thickness of said further layer of silicon dioxide (130) is 400-500 Angstroms, the thick¬ ness of said silicon nitride layer (132) is 1200-1500 Angstroms, and the thickness of the silicon dioxide im¬ plantation barrier (148) is 2000-2500 Angstroms. 10. A process according to claim 2, charac¬ terized by the step of doping said polysilicon layer (128) with impurities of a single conductivity type before defining the polysilicon layer (128) into said gate electrodes (28, 38), defining the doped polysilicon layer (128) into areas where conductors and resistors (50) are desired, and forming a further mask (138) over the areas where resistors are desired to protect these areas during doping of those areas where conductors are desired. 11. A process according to claim 10, charac¬ terized in that said further mask (138) is formed of polysilicon or of silicon nitride.

Inventors: PFEIFER ROBERT FREDERICK, TRUDEL MURRAY LAWRENCE
Applicants: NCR CO, NCR CORP
Application year: 1981
Main classification: H01L21
IPC codes: H01L21, H01L27, H01L29