ION PLATING WITHOUT THE INTRODUCTION OF GAS

Abstract: A process for ion plating wherein plating material is melted, vaporized, and then subjected to an ionization en­ vironment within a vacuum chamber, to create a plasma of ionized atoms by evaporating in the radio frequency field, and the process for plating such ionized material onto a substrate in the absence of any gas, inert or otherwise. It is an ion plating process without the need of an inert gas plasma wherein a high particulate energy is given to ionized particles of a plating material thus composites film build up representing a layer atomically bonded to the substrate carrier material.

Description: BACKGROUND OF THE INVENTION 1. FIELD OF THE INVENTION: This invention relates to a method of accelerating ionized particles of a plating material on to a substrate to be plated at high energy levels without the need of an inert gas plasma. 2. BRIEF DESCRIPTION OF THE PRIOR ART: In the past, substrates have been plated using vacuum evaporation methods, sputtering, and ion plating with an argon plasma. All of these methods'have some inherent disadvantages. The vacuum evaporation system deposits materials on substrates without particle acceleration resulting in a bond between the coating and the substrate of poor adhesive strength so that the coating may be easily separated from the substrate. Because of the deposition path of the evaporated material in an evaporation technique, uniform thickness on an irregularly shaped part is difficult to achieve. Sputtering methods overcome some of the problems of vapor deposition in that better adhesion of the plating material to the substrate is achieved. However, the energy levels of the plating atom to be deposited is such that the adhesive strength of the bond is not adequate for many applications. The sputtering process is dependent upon an ion of inert gas impinging upon the plating material to release an atom of plating material. The plating material is at a neutral electrical charge and must travel through the inert gas plasma and on to the substrates. In travelling through the inert gas plasma, the plating atom will strike inert gas atoms thus losing energy. This loss of energy results in a relatively low energy deposition force on to the substrate and possible contamination of the plated surface by inert gas atoms becoming entrapped in the plating material. Ion plating with an inert gas plasma overcomes some of the problems of uniformity in the plating layer and develops better bond strength. Because of the entrapment of the inert gas the coating may be contaminated with the inert gas atoms resulting in a film composition that is not suitable for many applications, especially in electronics. SUMMARY OF THE INVENTION Generally, this invention would be composed of a vacuum plating system with the high rate ion source for converting the material=to be plated onto the substrate into the plasma form in the area of the substrate. One of the objects of the present invention is to provide the ion plating process for plating both conductive and non conductive substrates with a wide variety of materials at high deposition rates. Another object of the present invention is to provide the ion plating process that will plate such wide varieties of material whether such material is flat, irregularly shaped with irregular depressions, raised surfaces or holes, and to provide unbroken coating surface over such irregularities or into the internal diameters of holes. A further object of the present invention is to provide the plating system not dependent upon the inert gas plasma to achieve the plating thereby giving a contamination free plating surface consisting solely of the plating material. A still further object of the present invention is to provide the high energy plating ion impact with the substrate to achieve an atomic bonding of the plating material with the substrate. A still more further object of the present invention is to provide the inert gas atomic cleaning method by which the substrate to be plated may be atomically cleaned by inert gas ion plasma prior to the actual plating process. The specific manner of performing the intent of the invention is shown in drawings that are part of this application. BRIEF DESCRIPTION OF THE DRAWINGS Figures 1, 2, and 3 are schematic systems of the vacuum ion plating system constructed to perform the requirements and objects of this plating invention. Fig. 4 is an enlarged fragmentary view of vapor source of the system of Fig. 3. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION The drawings show the electrical arrangement for material vaporization, ionization and substrate plating. All of the plating system is enclosed in a tank (i) to provide a vacuum enclosure, the tank having a working vacuum seal (2) and electrical feedthroughs (3) some of all of which may be made removable from the body of the system (4). The tank may be vertical or horizontal or at any other angle that may be convenient and may be made in different shapes from different materials. The baseplate (29) or tank (1) has provisions for passing through the electrical wires, the gas line (5) and vacuum evacuation connection (6) so that when the chamber is closed the internal portion can be environmentally controlled. The substrate (7) is supported by a base or fixture (8) which may be shaped in any configuration. The holding fixture (8) may be fixed or movable during the plating operation without departing from the principles of this invention. The ion plating source (9) may be a filament, a refractory boat, an electron beam gun, an induction heated crucible, or any other material vaporization source or multiples of the same that may be utilized to vaporize plating material without departing from the principles of this invention. A gas supply tube (5) is passed through the system wall or other convenient location and input gas is controlled by a metering valve (10). The input gas may be inert or other gases or combinations thereof, conducive to performing specific functions such as but not limited to cleaning of the substrate prior to the plating operation. A vacuum pumping system is connected through a valve (6) to the system through a baseplate or chamber (1) by a sealed passage (11) in the baseplate (29) or chamber (1). The radio frequency power supply (12) and the direct current power supply (13) transmit power to the substrate holder (8) through the feedthrough connectors (3 and 3t) in the baseplate (29) or chamber (1). The sequence of operations of the plating system is as follows; The system is evacuated by use of a vacuum system through the sealed passage (11). If it is desired to have a cleaning procedure for the substrate or if for chemical, metallurgical or physical process reasons, a gas is desired to be introduced into the system during any portion of the process, such gas can be admitted to the chamber through the gas supply tube (5) and the valve (10). If desired for cleaning, a plasma can be formed by the gas to bombard the surface of the substrate. After such cleaning, the argon or other gas may be withdrawn from the evacuated enclosure prior to the beginning of the plating process. Figure 1 shows one mode of operation where, after withdrawing the argon or other gas, radio frequency power from the radio frequency power supply 12), mixed with direct current positive bias from the direct current power supply (13) is supplied to the vaporization or sublimation source (9) to form positive ions of the evaporated material and accelerate those positive ions toward the substrate by repulsion from the positive bias on the source. The radio frequency and the direct current power supplies are protected from each other by inserting a radio frequency capacitor (14) and a radio frequency choke (15) in the output lines. Plating begins when the material source (9) is heated to a temperature high enough to vaporize or sublimate the plating material. In the case of resistance heated sources, this is normally done by a low voltage, high current alternating current supply (28). The substrate (7) may be at ground potential (19) as shown in figure 1. In another configuration, figure 2 the substrate (7) by means of electrical connections to the holder that supports it, has both radio frequency and negative direct current applied to it. In this case, the atoms of evaporant material (17) from the vaporization or sublimation source are positively ionized by the action of the radio frequency field (18) and are attracted by electrostatic force to the substrate by the negative direct current. If the substrate is a nonconductor, the radiation of the radio frequency field will cause it to develop a sustained negative charge on its surface. This is known as radio frequency "self bias" effect and serves to attract the positive ions of plating material which makes it possible to plate insulators by this method. Still another way to achieve ionization during the vaporization or sublimation of the plating material is to use an induction coil as shown in figures 3 and 4. The expanding and collapsing field in an induction coil (20) will cause all susceptive materials to heat as well as to release electrons from vaporized or sublimated atoms to form positive ions. Coil frequencies may vary, with higher frequencies usually improving both heating and ionization, the range of frequencies normally being above 10 kHz. The problems of low impedance arcing which may occur at higher frequencies can be eliminated by the use of a coupling transformer (21). When using such a source in most applications it is advantageous to have both radio frequency and direct current biasing on the substrate as the additional radio frequency field will increase the degree of vapor or sublimation ionization which improves the uniformity of the deposited film. The frequency of the radio frequency biasing signal, whether it be on the source or substrate, may range from 5 kHz to over 20 MHz. Energy savings can be achieved by using a ceramic crucible (25) inside a nonsusceptive heat shield. This allows for radio frequency heating of the source material while retaining the heat input by the resistance to heat transfer of the insulating materials. The ion plating material is vaporized, or sublimated, then ionized (17) to form a pure plasma of plating material. The ion plasma conforms to the configuration of the charged substrate giving coverage for irregularly shaped surfaces such as steps, curves and the inside of holes. Thus the radio frequency field causes the material to be deposited to impact with the substrate surface at very high energy levels creating excellent adhesion between the plating material and the substrate. When extremely sensitive substrates are to be coated a fixed or movable baffle (27 of figure 3) may be inserted for radiation protection without detracting from the quality of the coating. The fixed or movable baffle may also be used to prevent or reduce the possibility of deposition of unwanted deposits of less than pure material that may be formed initially at the beginning of the vaporization or sublimation process of the material to be deposited. The foregoing description of the process does not require the addition of any gas or vapor from an outside source for ionization to take place. It is recognized that with some materials to be ionized there may be gas released when the material to be evaporated or sublimated is changed to its ionized state. There are instanc-es where the need for film uniformity over very irregular surfaces may make it desirable to introduce a slight amount of inert gas for the purpose of material scattering to further film uniformity, but it should be noted that this use of inert gas is at a pressure well below the pressure needed for ionization and is low enough not to adversely affect film properties by inclusion of the inert gas molecules in the deposited film. In some applications inert gas may be introduced during the ion plating process to enhance or vary the stoichiometry of the material as deposited on the substrate. While the invention is described as fully as possible with various configurations and conditions described herein, there are various changes and configurations that may be incorporated without deviation from the basic principles shown herein.

Claims: CLAIMS 1. A process for ion plating a substrate held within a vacuum chamber and the process for plating such ionized material onto a substrate in the absence of any gas, inert or otherwise, such process comprising the steps of; a. evacuating the vacuum chamber, b. vaporizing the material to be plated, c. placing the radio frequency field from the radio frequency source to the substrate to ionize the plating material that has been vaporized, d. placing the negative electrical bias of direct current voltage on such substrate thereby creating a negative voltage on the substrate to attract positive ions of plating material. 2. The ion plating process of claim 1 wherein low background pressure of a gas is input to the system. 3. The ion plating process of claim 1 where the substrate is a conductor. 4. The ion plating process of claim 1 where the substrate is an insulator. 5. The ion plating process of claim 1 where the vapor source is an induction coil capable of generating ions of evaporant material. 6. The ion plating process of claim 1 where the substrate is optically baffled from the vapor source. 7. The ion plating process of claim 5 where the substrate is optically baffled from the vapor source. 8. The ion plating process of claim 1 where the radio frequency power supply is protected from the direct current and voltage by the radio frequency blocking capacitor inserted in the output lines. 9. The ion plating process of claim 1 where the direct current power supply is protected by the radio frequency choke inserted in the output lines. 10. A process for ion plating a substrate held in a vacuum system in the absence of inert gas input to the system, such process comprising the steps of; a. evacuating the vacuum chamber, b. vaporizing the material to be plated, c. placing the radio frequency field on the vaporization source to form positive ions of vaporized material, d. placing the direct current positive bias on the vaporization source to accelerate positive ions of plating material away from the source to the substrate. 11. The ion plating process of claim 10 wherein low background pressure of a gas is input to the system. 12. The ion plating process of claim 10 where the substrate is a conductor. 13. The ion plating process of claim 10 where the substrate is an insulator. 14. The ion plating process of claim 10 where the vapor source is an induction coil capable of generating ions of evaporant material. 15. The ion plating process of claim 10 where the substrate is optically baffled from the vapor source. 16. The ion plating process of claim 14 where the substrate is optically baffled from the vapor source. 17. The ion plating process of claim 10 where the radio frequency power supply is protected from the direct current and voltage by the radio frequency blocking capacitor inserted in the output lines. 18. The ion plating process of claim 10 where the direct current power supply is protected by the radio frequency choke inserted in the output lines.

Inventors: WADA, AYAO
Applicants: WADA, AYAO
Application year: 1981
Main classification: C23C15
IPC codes: H01L21, C23C14