A PROCESS FOR ADVANCING EPOXY RESINS IN MOLECULAR WEIGHT AND A PROCESS FOR PREPARING RESIN IMPREGNATED SUBSTRATES

Abstract: Process for advancing epoxy resins in molecular weight and a process for preparing resin impregnated substrates in which an epoxy resin is reacted with a dihydric phenol in the presence of a sufficient quantity of a phosphonium catalyst such that the product resulting from reacting a mixture of the catalyst, epoxy resin and dihydric phenol has a percent epoxide difference from the theoretical percent epoxide of from 0.5 to 4.0.

Description: A PROCESS FOR ADVANCING EPOXY RESINS IN MOLECULAR WEIGHT AND A PROCESS FOR PREPARING RESIN IMPREGNATED SUBSTRATES Epoxy resins have heretofore been advanced in the presence of phosphonium catalysts disclosed by Dante in U.S. 3,477,990 and Perry in Canadian 893,191 and U.S. 3,948,855. However, the quantities of catalyst employed were that which would provide a resin having a percent epoxide value sufficiently close to the theo¬ retical epoxide value that no improvement in properties were envisioned. The process of the present invention provides for the production of advanced epoxy resins having an improvement in one or more physical properties such as, for example, reactivity or glass transition temperature of the cured resins. Resins having faster reactivity characteristics provide for increased productivity of articles produced therefrom over a unit time period. The increase in glass transition temperature of a cured resin permits articles prepared therefrom to be employed in higher temperature environments. Cured epoxy resins having increased glass transition temperatures provide products which can be employed in environments of higher temperatures i.e., the useful operating temperature is generally directly proportional to the glass transition temperature. The present invention pertains to a process for advancing epoxy resins in molecular weight by reacting (A) an epoxy resin which is a glycidyl ether of a dihydric phenol having an average of more than one glycidyl ether group per molecule with (B) a dihydric phenolic compound in the presence of (C) a phosphonium catalyst employing components (A) and (B) in quantities such that the phenolic hydroxyl to epoxide equivalent ratio is that which will provide a theoretical percent epoxide of-the resultant reac- tion product of from 2.7 to 14, preferably from 7 to 12.5; characterized by employing the catalyst, compo¬ nent (C), in a quantity such that the epoxy resin which would result when subjecting a mixture of com¬ ponents (A), (B) and (C) to suitable reaction conditions produces an advanced epoxy resin wherein the difference obtained by subtracting the percent epoxide obtained by analysis from the theoretical percent epoxide is from 0.5 to 4, preferably from 1 to 2. An epoxy resin produced by the process of this invention when cured with a curing quantity of a curing agent provides a composition which has an improvement in glass transition temperature and/or increased reactivity. The present invention also pertains to products resulting from curing a mixture of an epoxy resin prepared by the above procedure and a curing quantity of a curing agent therefor. The present invention also pertains to a process for preparing resin impregnated substrates for use in preparing electrical laminates by a process which comprises: (I) saturating said substrate with a resin forming mixture comprising; (A) an epoxy resin having an epoxide equiv¬ alent weight of from 300 to 600, prefer¬ ably from 375 to 475 which has been prepared by reacting (1) a glycidyl ether of a dihydric phenol having an average of more than one epoxide group per molecule and an epoxide equivalent weight (EEW) of from 156 to 400, prefer¬ ably from 177 to 190, with (2) a dihydric phenolic compound in the presence of (3) a phosphonium catalyst for effecting the reaction between (1) and (2), wherein components (1) and (2) are employed in quantities which will provide a theoretical percent epoxide of the reaction product of from 8 to 15, preferably from 9.5 to 13; (B) a curing agent for said epoxy resin and (C) a solvent system for Components A and B; (II) heating the resultant impregnated substrate to B-stage the resin and remove the solvent system; characterized by employing as the catalyst, Component (A-3), a phosphonium salt or complex thereof which has at least one, preferably two, most preferably three aromatic ring(s) attached to the phosphorus atom of the phosphonium group and at least one aliphatic hydrocarbon group attached to said phosphorus atom, said catalyst being employed in a quantity such that the epoxy resin which would result when subjecting a mixture of components (A-l), (A-2) and (A-3) to suitable reaction conditions produces an advanced epoxy resin wherein the difference obtained by subtracting the percent epoxide obtained by analysis from the theoretical percent epoxide is from 0.5 to 4, preferably from 1 to 2. Suitable glycidyl ethers of a dihydric phenol which can be employed in the present invention include those represented by the formula wherein A is a divalent hydrocarbon group having from 1 0 0 II II to 8 carbon atoms, -S-, -S-S-, -0-, -C-, -S-, or 0 I! -S-; each X is independently hydrogen, chlorine or bromine; II 0 x has a value of zero or one and n has a value such that the EEW is from 156 to 400, preferably from 177 to 190, calculated on the basis of X being hydrogen. Particularly suitable are the diglycidyl ethers of bisphenol A and tetrabromobisphenol A. Suitable dihydric phenolic compounds include, for example, catechol, hydroquinone, resorcinol and bisphenols such as those represented by the formula wherein X, A and x are as defined above. Particularly suitable dihydric phenolic compounds are bisphenol A and tetrabromobisphenol A. Suitable phosphonium catalysts which can be employed herein include, for example, those compounds having at least one phosphonium cation group repre¬ sented by the formula I R wherein each R is independently a hydrocarbyl or substituted hydrocarbyl group having from 1 to 20, preferably from 1 to 6, carbon atoms-, or substituted hydrocarbyl groups. It is preferred that at least one, preferably two and most preferably three, of tTT l£_, the R groups be an aromatic group i.e., an aryl group or an alkaryl group such that the phosphorus atom is attached directly to the aromatic ring of such aryl or alkaryl group. By the term hydrocarbyl, it is meant that the groups can be alkyl, aryl, alkaryl, aralkyl and the alkyl can be either cyclic or acyclic. By substituted hydrocarbyl it is meant that the hydrocarbyl groups can contain one or more inert substituent groups such as, for example, Cl, Br, I, NO 2 , or mixtures thereof. The R groups can contain any substituent - group which is inert to the system, i.e. will not deactivate the catalyst under the conditions in which they are employed. It is preferred that the phosphonium cation . contain at least one aromatic ring and at least one alkyl group attached directly to a phosphorous atom. Suitable anions include the halides, such as, for example, Cl, Br, I, carboxylates, dicarboxylates, phosphates, nitrates, sulfates, nitrites, sulfites, borates, chromates, or mixtures thereof. The preferred anions are the strong acids, i.e. those having a pK value less than 4.5, prefer- ably less than 3.7, because the catalysts containing such are generally more efficient, in that it takes less catalyst to effect the lowering of the epoxide value to the desired value below the " theoretical value. The dihydric phenol and the glycidyl ether of a dihydric phenol are employed in quantities such that the theoretical percent epoxide of the resultant product is from 2.7 to 14, preferably from 7 to 12.5. The quantity of catalyst will of course vary depending upon the particular catalyst employed; however, for most catalysts, from 0.1 to 1.5, preferably from 0.2 to 0.8, parts catalyst by weight per 100 parts by weight of glycidyl ether of dihydric phenol can be employed. The reaction conditions employed to prepare the advanced epoxy resins can vary, but temperatures of from 100°C to 200°C, preferably from 120°C to 160°C, • are suitable. Lower temperatures usually require longer reaction times whereas higher temperatures usually require shorter reaction times. The pressure employed is not particularly important and can be from 1 mm Hg vacuum (0.13 kPa) to 100 psig (791 kPa). However, it is usually pre¬ ferred to employ pressures of from 5 psig (136 kPa) to 20 psig (239 kPa). The particular reaction conditions are not important so long as for the particular phosphonium catalyst and quantity thereof employed, the reaction conditions produce the desired result i.e., the resul- tant advanced epoxy resin has the required difference between the theoretical percent epoxide and the actual percent epoxide value obtained by analysis. Any of the well known curing agents can be employed in the present invention to cure the epoxy resins. Such curing agents include amines, amides, guanidines, phenolic hydroxyl-containing materials, carboxylic acids, carboylic acid anhydrides, i idazoles, biguanides, or mixtures thereof. Particulary suitable curing agents include, for example, guanidines such as for example, dicyan- diatiide and tetramethyl guanidine and biguanides such as 1,6-xylene biguanide, polyhydric phenols, or mixtures thereof. The quantity of curing agent employed depends upon the particular curing agent employed and the propertied desired in the resultant cured resin, all of which is well known by those persons reasonably skilled in the art and discussed in HANDBOOK OF EPOXY RESINS, by Lee and Neville, McGraw Hill, 1967. The theoretical percent epoxide is calculated by the following formula: THEORETICAL % EPOXIDE = EqER = epoxide equivalents from the epoxy resin. EqDHP = phenolic hydroxyl equivalents from the dihydric . phenol. WtER = weight of epoxy resin employed. WtDHP = weight of dihydric phenol employed. The actual percent epoxide was determined experimentally by titration with perchloric acid in glacial acetic acid by the liberation of hydrogen bromide generated by the addition of t traethy1ammonium bromide in glacial acetic acid using crystal violet as an indicator. The epoxy groups react stoichiometrically with hydrogen bromide generated from the reaction of perchloric acid with tetraethyl ammonium bromide. When the epoxy groups have been reacted, the free hydrogen bromide causes the crystal violet to change color. The glass transition temperature, Tg, was determined by the method of ASTM D3418-75 on cured specimens prepared in the following manner. A mixture of 10 grams of the resultant epoxy resin, 0.3 gram of dicyanandi mide and 0.01 gram of 2-methyl imidazole was melt mixed on a 100°C hot plate for 3 minutes. The mixture was finely ground in a mortar and pestle. The powder was transferred to an aluminum weighing dish and cured at 175°C for 2 hours. The stroke cure reactivity was determined by the following procedure. An acetone solution of epoxy resin is prepared by blending 10 grams of acetone with 30 ' grams of molten epoxy resin warmed to between 80°C and 100°C. The solu- tion is allowed to cool to room temperature and then 9 grams of a 10 percent solution of dicyandiamide in the monomethy1ether of ethylene glycol and 0.75 gram of a 10 percent solution of benzyldimethylamine (BDMA) in acetone is added (3 phr dicyandiamide, 0.25 phr BDMA). The solution is mixed well and allowed to stand at room temperature for a period of 2 hours. The catalyzed resin is then drawn in an eye dropper and placed on a hotplate at 175°C ± 1°C. The stop watch is immediately started. The sample is allowed to rest on the hotplate undisturbed for 60 ± 1 seconds. At this point, begin stroking with a wooden spatula. Stroking should be done by pushing the resin puddle back and forth over an area about 1 square inch using the same side of the spatula in contact with the resin. The resin will thicken as it is continuously stroked. Eventually the resin will become stringy and immediately after, becomes a rubber gel that releases from the hotplate. This is the end point. Stop the stopwatch and record the reading. The fewer the number of seconds, the higher the reactivity. The following examples are illustrative of the present invention, but are not to be construed as to limiting the scope thereof in any manner. Various catalysts employed in the examples and comparative experiments were prepared by the following procedures. CATALYST PROCED.URΞ A To a single necked 100 ml round bottom flask (RBF) was charged the particular phosphonium catalyst precursor as a 70 percent solution in methanol. The particular acid employed was dissolved in methanol and charged to the RBF. The solvents and excess acetic acid were removed under vacuum while heating to a final temperature of 75°C at 1 mm Hg (0.13 kPa). The resultant liquor was acetone washed thereby yielding a white solid phosphonium salt of the acid employed. CATALYST PROCEDURE B To a 500 ml single neck RBF was charged the particular precursor as a 70 percent solution in methanol. The particular acid employed was slowly added to the solution while swirling the flask. The solvent and excess acetic acid were removed under vacuum while heating to a final temperature of 120°C at 1 mm Hg (0.13 kPa). The resultant product was acetone washed thereby yielding the phosphonium salt of the acid employed. CATALYST PROCEDURE C To a single neck 500 ml RBF was charged the phosphonium bicarbonate precursor in methanol. The particular acid employed was dissolved in methanol in a beaker and then slowly added to the RBF while swirl¬ ing the RBF. Swirling was maintained until C0 2 evolution subsided. The solution was then rotoevapo- • rated until a vacuum could be maintained at 1 mm Hg (0.13 kPa) at 75°C. The resultant liquor was washed twice with acetone to remove excess acid impurities to yield a white solid phosphonium salt of the acid. CATALYST PROCEDURE D To a one inch diameter glass column equipped with a stopcock was charged a methanol slurry of 65 g (70 percent by weight H 2 0) of an anion exchange resin in the acetate form (200-400 mesh; .8 meq. per ml resin bed; 3.5 meq. per dry gram; 70 to 78 wt. percent moisture; styrene type quaternary ammonium; wet mesh range 80-200) available from BIO*RAD Laboratories as AG1-X2. A 5 percent solution in methanol of potassium hydroxide was slowly eluded through the column at a rate of 2 drops per second. The column was then washed with methanol until neutral to litmus paper. The phosphonium catalyst precursor, as a 70 percent solution in methanol, was then added to the column and slowly eluded through the ion exchange resin until the dark band was washed through the column. The eluded material was caught in a RBF containing an excess molar ratio of the acid. This solution was then rotoevaporated and acetone washed to yield a white solid phosphonium salt of the acid. CATALYST PROCEDURE E To a 4 oz (0.12 liter) bottle was charged 100 g (0.17 mol) of a 70 percent methanol solution of ethyltriphenylphosphonium acetate*acetic acid com- plex followed by the addition of 20.44 g (0.1622 mol) of oxalic acid dihydrate. The mixture was mixed until all of the oxalic acid had dissolved. The resultant solution contained about 51.14 wt. percent ethyltri¬ phenylphosphonium oxalate. CATALYST PROCEDURE F To a 2 gallon (7.6 liter) bottle was charged 1000 g (1.707 mol) of a 70 percent methanol solution of ethyltriphenylphosphonium acetate•acetic acid complex followed by the addition of 204.4 g (1.622 mol) of oxalic acid dihydrate. The mixture was mixed until all the oxalic acid had dissolved and then 31.5 g of methanol was added to give a resultant solution of 50 wt. percent ethyltriphenylphosphonium oxalate. The precursors and acids employed, reaction conditions and results are provided in the- following Table I for which the abbreviations employed therein have the following meaning. BTPP = butyltriphenylphosphonium ClAc = chloroacetate ETPP = ethyltriphenylphosphonium ETPPAc-HAc = ethyltriphenylphosphonium acetate acetic acid complex HC0 3 = bicarbonate - Ϊ: C - ACID EMPLOYED No. CATALYST PROCEDURE TYPE g/moles pKa 1 BTPP FORMATE C Formic 2.73/0.06 3.6 2 ETPP FORMATE C Formic 2,73/0.06 3.6 3 ETPP FORMATE D Formic 4.1/0.09 3.6 4 BTPP OXALATE C Oxalic 2.47/0.027 1.3 5 ETPP PHOSPHATE B Phosphoric 6.38/0.065 2.1 6 ETPP SUCCINATE B Succinic 14/0.119 4.2 7 ETPP MALONATE B Malonic 1.56/0.016 2.85 8 ETPP OXALATE A Oxalic 1.94/0.015 1.2 9 BTPPClAc C Chloro-acetic 2.84/0.03 2.9 10 ETPP OXALATE E Oxalic 20.44/0.1622 1.2 11 ETPPAc•HAc Purchased from Cincinatti Milacron, Inc. 12 ETPP OXALATE F Oxalic 204.4/1.622 1.2 dl TABLE I (Continued) PRECURSOR EMPLOYED No. TYPE g/moles pKa 1 BTPPHCO 13.2/0.035 6.5 2 ETPPHCO- 13.2/0.035 6.5 3 ETPPAc•HAc 3.5/0.009 4.6 4 BTPPHCO- 9.9/0.026 6.5 5 ETPPAc-HAc 26.7/0.0651 4.6 6 ETPPAc•HAc 48.8 /0.119 4.6 7 ETPPAc-HAc 5.88/0.014 4.6 8 ETPPAc•HAc 6.3/0.015 4.6 υi 9 BTPPHC0 3 9.9/0.026 6.5 10 ETPPAc•HAc 70/0.171 4.6 11 N.A. N.A. N.A 12 ETPPAc•HAc 700/1.71 4.6 TABLE I (Continued) METHANOL SOLVENT REACTION MELTING POINT (total Quant. ) TEMP. AND YIELD No. grams °C °c/% COMMEl. ITS 1 37 100 190/N.D. 1 white solid 2 37 100 N.A.VN.D. brown liquid 3 200 100 N.A./95 brown liquid 4 35 75 155/78 white solid 5 11 25 175-189/100 white solid 6 21 120 .A./N.D. brown liquid , 7 40 120 N.A./N.D- brown liquid c 8 23 70 151/91 white solid 9 13 75 212-215/76 white solid 10 30 25 N.A./N.D. mixture contains free acetic acid 11 N.A. N.A. N.A. 70% solution in methanol 12 81.6 25 N.A./N.D. mixture contains free acetic acid 1 N.D. - not determined 2 N.A. - not applicable * s. GENERAL PROCEDURE FOR RESIN PREPARATION To a reaction vessel equipped with a means for stirring, temperature control and indication and nitrogen purge was charged the desired weight of the specified liquid diglycidyl ether of bisphenol A and the desired weight of the specified dihydric phenol. The mixture was heated at a rate of 5°C/minute. When the temperature of the mixture reached 70°C, the desired amount of the specified phosphonium catalyst dissolved in methanol was added. The mixture ' was heated at the desired reaction conditions to give the resultant product. EPOXY RESIN A Epoxy Resin A was a liquid diglycidyl ether of bisphenol A having an average epoxide equivalent weight of 189, percent epoxide of 22.75 percent and an aliphatic chloride content of 3410 ppm. EPOXY RESIN B Epoxy Resin B was a liquid diglycidyl ether of bisphenol A having an average epoxide equivalent weight of 188, percent epoxide of 22.82 percent and an aliphatic chloride content of 3700 ppm. EPOXY RESIN C Epoxy Resin C was a liquid diglycidyl ether of bisphenol-A having an average epoxide equivalent weight of 186.5, percent epoxide of 23.06 and an aliphatic chloride content of 2200 parts per million. DIHYDRIC PHENOL A Dihydric phenol A was tetrabromobisphenol A having a phenolic hydroxyl equivalent weight of 272 and percent bromine content of 58.8 percent. DIHYDRIC PHENOL B Dihydric phenol B was a bisphenol A having a phenol hydroxyl equivalent weight of 114. EXAMPLES 1-21 and COMPARATIVE EXPERIMENTS A-G The components, reaction conditions and results are given in the following Tahle II. TA3LE I I EX. OR REACTION CONDITIONS COMP. DIHYDRIC 1st 2nd 3rd 4th EXPT. EPOXY RESIN PHENOL CATALYST Hour Hour Hour Hour NO. Type/Equiv. Type/Equiv. Type/moles °C °C °C °C A A/1.244 A/0.422 No. 10/0.0002 120 130 150 150 B A/1.164 A/0.333 No. 10/0.00022 120 130 150 150 1 A/11.64 A/3.33 No. 10/0.0087 120 130 150 150 2 A/11.64 A/3.33 No. 10/0.0174 120 130 150 150 3 A/11.64 A/3.33 No. 10/0.013 120 130 150 150 4 A/11.64 A/3.33 No. 10/0.0174 120 130 150 150 5 A/11.64 A/3.33 No. 10/0.0256 120 130 150 1,50 6 A/11.64 A/3.33 No. 10/0.0337 120 130 150 150 C A/1.06 A/0.303 No. 11/0.00024 120 130 150 150 D A/1.06 A/0.232 No. 11/0.00024 120 130 150 150 7 A/1.335 A/0.359 No. 11/0.00730 120 130 150 150 8 A/1.06 A/0.28 No. 8/0.0026 120 130 150 150 9 1 A/1.06 A/0.28 No. 11/0.0026 120 130 150 150 XVO.0026 c. cn σ. -» Q y CO rH l © rz* r- Q Q tn ol o o rH • CN CN cn CN rH y CN • Ho 1 rH rH rH Z rH rH rH rH y y rH z Z W J Q O © O © o 1—1 rH in in in un in in in in O © © © W 5X a O © rH rH rH rH y rH rH y CN CN CN CN EH CM rH rH rH rH rH y rH rH y y rH rH rH W C ζri - ' S CM O < f_q .H cN cn <# i-. vo θ Q - ^ co σ. X OS O X Z ω o u w tfl O O tfl to to to y r- 1 y y t-* y y α o Z X O 50 X t H-" Tl o tfl oo -O σ* n tf* ω to O TJ2 • • ι-3 TJ y y y y y y y y y y y y y y y y K to vo cn n cπ ^ cn to cn to to cn to to to to o O V ) © cn o cn o © © © © © © © © © o o o fi rt 50 H tfl > y y y y y y y y y y y y y y y y H co vo u. cπ uι rf* u. co u. co co u. co co co co o Sow O 3 . o cn o n o © © © © © o © o © o © O fi C_o If z y y y y y y ~ y y y y y y o a ω σ> vo cπ n ui rf* • cn cn cπ cn cn n cπ cn cn OO r-{ toέ-j © ui © ui © © > o © o o © © o © o O fi O- O l-{ HM ω H 3 1—1 Z y y z y z y y y y y y y y y a rf* vo n ui rf • cπ cn cπ cn tn cπ cn cn cπ o o rto tf> n © cn > © > o © o © © o © © © ac tr Z O H TS TABLE II (Continued) EX. OR 175°C COMP. THEORY ACTUAL • DIFF. STROKE EXPT. % % IN % CURE Tg NO. EPOXIDE EPOXIDE EPOXIDE Sec. _C 10 12.00 9.8 2.2 N.D. N.D. 11 12.00 10.65 1.35 N.D. 130 12 12.00 10.66 1.34 290 127 13 12.00 11.00 1 293 N.D. 14 11.89 8.6 3.29 N.D. N.D. to 15 12.00 10.00 2 N.D. N.D. to 16 12.00 9.8 2.2 N.D. N.D. 17 11.89 10.2 1.69 N.D. N.D. 18 12.00 9.8 2.2 205 130 E 14.00 13.99 0.01 274 N.D. 19 .14.00 12.13 1.87 255 N.D. F 4.65 4.39 0.26 300 N.D. 20 4.65 3.51 1.14 280 N.D. G 2.70 2.46 0.24 255 N.D. 21 2.70 1.70 1 164 N.D. 22 11.50 10.00 1.50 N.D. 130 1 Insitu preparation of catalyst (ETPP Oxalate) by adding the catalyst precursor (ETPPAc'HAc) plus acid (oxalic acid dihydrate designated X) to the mixture of epoxy resin and dihydric phenol. 2 N.D. = not determined. EXAMPLE 23 (PREPARATION OF ELECTRICAL LAMINATE) A. Preparation of Prepreg Varnish Formulation A prepreg varnish formulation was prepared by blending 5411 g of a 75 percent solution by weight in acetone of the resin of example #22 with 1225 g of a 10 percent solution of dicyandiamide in the monomethylether of ethylene glycol (^3 phr dicyandi¬ amide), 6.13 g of benzyldimethyl mine (~0.15 phr BDMA) and 200 g acetone. The viscosity of the solution at 25°C was 25 seconds using a #2 Zahn cup. The 175°C stroke cure reactivity of the prepreg varnish was about 245 seconds. B. Preparation of Laminate Fiberglass cloth (type 7628 with 1399 finish) was impregnated by passing it through the prepreg varnish described in A above, followed by a pair of doctor bars set at 15 mils (0.38 mm) clearance to control resin pickup, and finally through an oven at 300°F_ (149°C) for a dwell time of approximately 4 minutes. The resulting B-staged impregnated cloth of prepreg had a gel time of 93 seconds at 175°C. A laminate was then prepared from the above prepared preimpregnated fiberglass employing 6 plys of 12 in. x 12 in. x 0.13 in. (3 cm x 3 cm x .33 mm) sheets of 7628 style glass all of which were 1399 finish. The laminate was prepared by pressing at 500 psig (3549 kPa) for 60 minutes at 175°C. The laminate was then tested. The pressure cooker-solder test was conducted by (i) cutting 2 in. x 4 in. (5 cm x 10 cm) coupons from prepared laminate, (ii) placing 3 coupons edgewise on a rack in a pressure cooker and maintaining 15 psig (205 kPa) steam pressure for ' ~1.5 hour, and (iii) then immersing the coupons in 500°F (260°C solder for 20 seconds. Six sides of the 3 coupons were evaluated and rated by the number of sides passing. In order to pass, the side must be free of blisters after immersion in hot solder. A 1/2 side pass consisted of the side having only 1 edge blister. The laminate had a glass transition temper- ature (Tg) of 130°C. After subjecting to 15 psig (205 kPa) steam pressure for 1-1/2 hours and immersion in 500°F (260°C) solder for 20 seconds, 5-1/2 sides of the laminate out of six sides passed the test.

Claims: CLAIMS 1. A process for advancing epoxy resins in molecular weight by reacting (A) an epoxy resin which is a glycidyl ether of a dihydric phenol hav¬ ing an average of more than one glycidyl ether group per molecule with (B) a dihydric phenolic compound in the presence of (C) a phosphonium catalyst employ¬ ing components (A) and (B) in quantities such that the phenolic hydroxyl to epoxide equivalent ratio is that which will provide a theoretical percent epoxide of the resultant reaction product of from 2.7 to 14; characterized by employing the catalyst, component (C), in a quantity such that the epoxy resin which would result when subjecting a mixture of components (A), (B) and (C) to suitable reaction conditions produces an advanced epoxy resin wherein the difference obtained by subtracting the percent epoxide obtained by analysis from the theoretical percent epoxide is from 0.5 to 4. 2. The process of Claim 1 characterized in that component (C) is employed in a quantity which will provide a difference obtained by sub- racting the percent epoxide obtained by analysis from the theoretical percent epoxide of from 1 to 2. 3. A process for preparing resin impreg¬ nated substrates for use in preparing electrical • laminates by a process which comprises: (I) saturating said substrate with a resin forming mixture comprising; (A) an epoxy resin having an epoxide equiv¬ alent weight of from 300 to 600 which has been prepared by reacting (1) a glycidyl ether of a dihydric phenol having an average of more than one epoxide group per molecule and an epoxide equivalent weight (EEW) of from 156 to 400; with (2) a dihydric phenolic compound; in the presence of (3) a phosphonium catalyst for effecting the reaction between (1) and (2), wherein components (1) and (2) are employed in quantities which provide a.theoretical percent epoxide of the reaction product of from 8 to 15; (B) a curing agent for said epoxy resin and (C) a solvent system for Components (A) and (B); (II) heating the resultant impregnated substrate to B-stage the resin and remove the solvent system; characterized by employing as the catalyst, component (A-3), a phosphonium salt or complex thereof which has at least one aromatic ring attached to the phos¬ phorus atom of the phosphonium group and at least one aliphatic hydrocarbon group attached to said phosphorus atom, said catalyst being employed in a quantity such that the epoxy resin which would result when subjecting a mixture of components (A-l), (A-2) and (A-3) to suitable reaction conditions produces an advanced epoxy resin wherein the difference obtained by subtract¬ ing the precent epoxide obtained by analysis from the theoretical percent epoxide is from 0.5 to 4. 4. The process of Claim 3 characterized in that component (A-3) has two aromatic rings attached to the phosphorous atom and is employed in a quantity which provides a difference obtained by subtracting the percent epoxide obtained by analysis from the theoretical percent epoxide of from 1 to 2. 5. The process of Claim 4 characterized in that component (A-3) has three aromatic rings attached to the phosphorus atom. -

Inventors: DOORAKIAN GEORGE A, GIST ALDOLPHUS V, WHITESIDE ROSS C
Applicants: DOW CHEMICAL CO, DOW CHEM CO
Application year: 1981
Main classification: C08G59
IPC codes: C08G59, C08J5, C08L63