INTERNALLY COATED REACTION VESSEL FOR USE IN OLEFINIC POLYMERIZATION

Abstract: A polymerization reaction vessel having a coating on the inner surfaces thereof resulting from applying thereto an aqueous coating solution of an alkali metal or ammonium salt of the reaction product or oligomers of an aliphatic aldehyde, such as acetaldehyde, and the like, and a polyhydric phenol, such as resorcinol, and the like. When polymerizing olefinic monomers, such as vinyl halides, vinylidene halides, and vinylidene monomers having at least one terminal CH<u2>u = CH < group, and mixtures thereof, while in contact with said coating, polymer buildup on the inner surfaces of the reaction vessel is substantially eliminated.

Description: "INTERNALLY COATED REACTION VESSEL FOR USE IN QLEFINΓC POLYMERIZATION" Background of The Invention In the coππnercial production of polymers and copolymers of vinyl and vinylidene halides, when polymerized alone or with other vinylidene monomers having a terminal group, or with polymeriz- able polyolefinic monomers, the buildup of polymer on the internal surfaces of the reactor is not only troublesome but costly. For example, when polymer¬ izing vinyl chloride, and other comonomers when used, the same are maintained in the form of discrete droplets in an aqueous suspension by the use of sus¬ pending agents and agitation. When the reaction is complete, the resultant polymer, or PVC, is washed and dried. However, these suspension systems are often not as stable as they should be and during the polymerization reaction, vinyl chloride polymer builds up on the interior surfaces of the reactor, including the surfaces of the baffles and agitator. Obviously, this polymer buildup must be removed since it results in further formation of polymer buildup which in turn results in a crust that adver¬ sely affects heat transfer and contaminates the polymer being produced- While various methods have heretofore been proposed to reduce the amount and nature of polymer buildup on polymerization reactor surfaces, such as solvent cleaning, various hydraulic and mechanical reactor cleaners, and the like, none has proved to be the ultimate in polymer buildup removal. That is to say, these various methods and apparatus " have done an acceptable job but there is still room for improvement in this area, particularly from an economic point of view. Various methods have been proposed to pre¬ vent, or substantially eliminate, the formation of the polymer buildup in the first instance. For ex¬ ample, it has been proposed to coat the internal surfaces of the reactor with, various polymer build¬ up resistant coating materials. For example, U.S. Pat. No's.* 4,024,330 and 4,024,301, various poly- aromatic amines are shown as useful for coating reactors to substantially eliminate buildup. Alkali soluble dyes have been shown to be useful for this purpose in U.S. Pat. No. 4,068,059. Further in U.S. Pat. No. 4,080,173 there is shown and des¬ cribed the use of selfcondensed polyhydric phenols * and polyhydric naphthols as useful coating materials to prevent polymer buildup. While all these coating materials give good to excellent results, the search continues for new and improved polymer buildup resis¬ tant materials with which to coat reactors for the purpose of preventing or eliminating polymer buildup on the inner surfaces thereof. Further, a recently published Japanese patent application discloses an interesting coating for polymerization reactors. This is Japanese Pat. Application No. 127682/78, filed October 17, 1978 in the name of Kanegafuchi Chem. . . and published April 21, 1980 under Laid-open Gazette No. 55-054317. In this case the reactor is coated with the reaction product of pyrogallol or hydroxyhydroquinone alone, or other phenolic compounds containing either or • both of them, with aromatic aldehydes. The reaction products are the acidic form and are dissolved in an organic solvent, such as methanol, and applied tc the reactor surfaces and then dried. This is an expen¬ sive and cumbersome procedure, especially in large reactors. Drying is difficult and the solvent must be recovered, for economic reasons. It would be much more desirable to use an aqueous solution of such reaction products which did not have to be dried. Summary of The Invention It has been found that polyhydric phenols and aliphatic aldehydes can be reacted together to form oligomers the salts of which are soluble in water. The aqueous salt solutions are applied to the inner sur¬ faces of a reactor forming an irreversible adsorptive coating on the surfaces which does not have to be dried and further, said coating can be rinsed with water, if so desired. The presence of said coating on the internal surfaces of the reactor substantially eliminates polymer buildup on said surfaces. Detailed Description In accordance with the present invention, a film or coating of a coating material, or oligomer, made by the reaction of a polyhydric phenol and an aliphatic aldehyde, including formaldehyde, is applied to the inner surfaces of a polymerization reactor or vessel in the form of the salt of the oligomer by merely contacting said surfaces with an aqueous alkaline solution of said coating material. All exposed sur¬ faces in the interior of the reactor, such as the baffles, agitator or mixing mechanism, etc., and the condenser, when one is employed, are likewise coated in the same manner. After the coating solu¬ tion has been applied to the inner surfaces of the reactor, the polymerization medium can be intro¬ duced into the reactor immediately and the reaction started without the necessity of drying said sur¬ faces beforehand. The elimination of the drying is most important in the present invention. However, although optional, it is preferred, when after the application of the coating to the inner surfaces, that the surfaces are rinsed with water, such as by spraying, and the like, thereby, surprisingly, leaving on said surfaces a tightly adhering coating or film of the coating material which is not affected by the polymerization medium, even though said medium is vigorously agitated during the polymerization reaction. The reaction between the polyhydric phenol and aliphatic aldehyde to form an oligomer, or mixture of oligomers of varying molecular weight, is a con¬ densation reaction using a dehydration catalyst. If a mere bulk reaction between the polyhydric phenol and aliphatic aldehyde is employed, the resulting products do not contain the desired structures useful as coating materials in the present invention. It is necessary to not only adjust the number of moles of each rεac- tant carefully, but also to control mixing thereof and the reaction conditions to obtain the desired oligomers. The oligomers that are useful as coating materials, when the salt form thereof is employed, are those having the following general formula: chained or branched, containing from 1 to 10 carbon atoms and x is an integer from 1 to 10. Among the materials that may be employed in making the reaction products, or oligomers, suitable as coating mater¬ ials in the present invention are the polyhydric phenols, such as resorcinol, hydroquinone, catechol, phloroglucinol, and the like, and the aliphatic aldehydes, such as formaldehyde, acetaldehyde, propionaldehyde, n-butyl aldehyde, isobutyl aldehyde, n-valeroaldehyde, n-caproaldehyde, n-cctyl aldehyde, n-decyl aldehyde, and the like. A good example of a OMPI coating material having the above general structure is that formed by the reaction of resorcinol and acetaldehyde. This material, or reaction product, is A water solution of resorcinol and the NaOH catalyst is prepared at 60°C. in a reaction vessel. A water solution of acetaldehyde is prepared and placed in an add funnel. The acetaldehyde solution is then added dropwise to the resorcinol/catalyst solution with good agitation. In order to obtain the desired oligomers it is necessary to maintain a high mole ratio of resorcinol (and oligomers) to acetaldehyde throughout the early stages of the reaction. Then the temperature is raised steadily (up to 180°C.) to distill off both the initial water used as solvent and the water from the condensation reactions. Evidence that the desired reaction is taking place is provided by a deep red color in the solution and the absence of precipitates. Evidence that the desired xanthene, dixanthene, etc. compounds are present in the product is provided by an intense green flouresence (UV to visible) from the material in dilute methanol solution. A number of compounds can be used to cata- lyze formation of the desired oligomers from poly¬ hydric phenols and aliphatic aldehydes. As examples of such compounds, there may be named sodium hydroxide, zinc chloride, sulfuric acid, and the like. Other dehydrating agents can be employed as catalysts for OMPI the reaction. Looking at the broad picture of preventing polymer buildup in a polymerization reactor, it is essential that the inner surfaces thereof are water- 5 wettable. An ordinary solid surface, such as stain¬ less steel, is not water-wettable due to the normal contamination of said surfaces with organic materials through contact with the atmosphere. The surfaces can be cleaned, such as with chromic acid or an abra- Q sive cleanser, for example, and it will become water- wettable. However, such cleaning alone does not solve the problem since the surfaces will not remain clean for a sufficient length of time, that is for more than the duration of a single polymerization cycle. ■ ^5 This necessitates recleaning the surfaces after each polymerization cycle. Therefore, applying a coating to the surfaces which will be water-wettable and resist polymer buildup thereon and remain on said surfaces throughout multiple reaction cycles is most 0 desirable. When a metal or solid surface is non-wettable, a liquid thereon, such as water, will form droplets and not flow out into a smooth film. The angle formed between the tangent of the side of the droplet 5 and the metal or glass surface is called the "contact angle" and is referred to as "theta" ( θ ) . A further measurement of the wettability of a solid surface is the critical. surface tension for wetting a solid sur¬ face and is expressed as "γ c ". The Υ c is measured in Q dynes per centimeter. Using water as the standard, in order for a solid surface to be wettable, θ must equal zero or be very close to it, and Ύ C must be 72 dynes/cm. or greater. More importantly, the material being applied 5 to the surface should not only form a wettable sur¬ face, but also form a layer or film thereon which is O not readily removable. This film adheres to the solid or metal surface by adsorption and in many cases, the film is a mono-layer of the coating material applied which is of the order of a molecule in thickness". These films, or coatings, of such thickness are invis¬ ible to the naked eye thus eliminating any color pro¬ blem, such as is the problem with many coatings here¬ tofore used for the same purpose. Of course, films of greater thickness can result when using higher solids content coating solutions, in accordance with the present invention, which films or coatings are visible to the naked eye. The film or layer formed by the coating solution is not removable by washing with water. That is to say, the coating or film is resistant to removal from the surfaces when a turbu¬ lent aqueous reaction medium is in contact therewith, caused by the agitation of the polymerization mixture in the reactor. When reacting the polyhydric phenols and aliphatic aldehydes, a concentrate of the resulting oligomers is formed which in turn is used to make the coating solution of the salts thereof. The coating solutions are made in a conventional manner, using heat and/or agitation where necessary. In making said solutions, usually a temperature in the range of about 20°C. to about 50°C. is satisfactory. Agitation during dissolution is -desirable. As pre¬ viously pointed out, the coating material is dissolved in an aqueous alkaline solution, preferably an aqueous sodium hydroxide solution. However, other aqueous alkaline solutions may be employed, such as, for example, potassium hydroxide, lithium hydroxide, ammonium hydroxide, and the like. It has been found that a concentration of coating material in the range of about 0.1% to about 5.0% by weight is satis¬ -Pfa.ctory in accomplishing the objectives of the pre- O PI sent invention. To insure against undesirable color, and for economic reasons, it is preferred to employ a concentration of coating material in said solutions in the range of about 0.5% to about 2.0% by weight. It is to be understood that since the molecular weight of the coating material affects the total solids content in the coating solution, the concen¬ tration of said material therein could, in certain instances, be greater than 5.0% or less than 0.1% by weight. The coating solutions of the instant inven¬ tion having a pH in the range of about 9 to about 14 are satisfactory to accomplish the objectives hereof. It is preferred, however, to operate at a pH in the range of 11 to 13. The pH is affected by the kind of cation used to form the salt, such as Na, K, Li, NH., and the like. The coating solution is usually applied to the inner reactor surfaces by spraying it on. However, it is also possible to apply the coating solution by flooding the reactor and then draining, or painting, or brushing on, but spraying is the most practical and economical method of application. After spraying the coating solution on the inner surfaces and draining the reactor, the polymerization reaction can be started immediately without further treatment of said surfaces. However, it has been found that excellent results are obtained when, after applying the coating solution to the inner surfaces of the reactor, the coated surfaces are sprayed with water and the reactor drained prior to charging the polymerization reactor with the polymerization mixture or recipe. It should also be pointed out that the coatings defined herein work equally well on glass or metal surfaces, such as stainless steel, and the like. One important aspect of the present inven- tion is that multiple polymerizations may be run without opening the reactor between charges since, with the spray nozzle or nozzles mounted at strategic points on the reactor, it is possible to reach all inner surfaces thereof while the reactor is closed. Although multiple charges may be run in a coated reactor without recoating the surfaces, it has been found to be expeditious to recoat the interior surfaces of the reactor periodically after several charges have been run therein, or after each charge, to insure uni¬ form and efficient production. When it is decided to recoat the reactor, the reactor is drained and the inner surfaces of the reactor are flushed with water. The coating solution is applied to the surface, pre- ferably by spraying, and the reactor is drained of the excess coating solution in such a way that the same can be sent to a recovery system, if desired. Then, optionally, the surfaces having the coating thereon are sprayed with water and the effluent is discarded, or recovered if desired. Thereafter, the reactor is charged with the polymerization medium and ingredients in the usual manner and the reaction com¬ menced immediately with no particular modification of processing techniques being necessary due to the pre- sence of the coating. It is understood, of course, that one can recoat the reactor as often as desired without opening the same, even after every charge is polymerized. Further, utilization of the internally coated reaction vessel of the present invention does not adversely affect the heat stability or other physical and chemical properties of the polymers pro¬ duced therein. While the present invention is specifically ' illustrated with regard to the suspension polymer- ization of vinyl chloride, it is to be understood that the process and apparatus may likewise to applied in the emulsion, or suspension polymerization of any polymerizable ethylenically unsaturated monomer or monomers where undesirable polymer buildup occurs. Examples of such monomers are other vinyl halides and vinylidene halides, such as vinyl bromide, vinylidene chloride, etc.; vinylidene monomers having at least one terminal CΞ 2 =C\ grouping, such as esters of acrylic acid, for example methyl acrylate, ethyl acry- late, butyl acrylate, octyl acrylate, cyaonethyl acry- late, and the like; vinyl acetate; acrylonitrile; esters of methacrylic acid, such as methyl methacry- late, butyl methacrylate, and the like; styrene and styrene derivatives including α-methyl styrene, vinyl toluene, chlorostyrene, etc.; vinyl naphthalene; diolefins, including butadiene, isoprene, chlo oprene, and the like;- and mixtures of any of these types of monomers and other vinylidene monomers copolymerizable therewith; and other vinylidene monomers of the type known to those skilled in the art. The present invention, however, is particul¬ arly applicable to the suspension polymerization of vinyl chloride, either alone or in a mixture with one or more other vinylidene monomers having at least one terminal grouping copolymerizable therewith in amounts as great as about 80% or more, by weight, based on the weight of the monomer mixture, since polymer buildup in the reaction vessel is a particul¬ arly bad problem here. The polymerization process is usually con- ducted at a temperature in the range of about 0°C. to about 100°C. depending upon the particular monomer or monomers being polymerized. However, it is preferred to employ temperatures in the range of about 40°C to to about 70°C, since, at these temperatures, polymers having the most beneficial properties are produced. The time of the polymerization reaction will vary from OMPI about 2 to about 15 hours. The polymerization process may be carried ou at autogenous pressures although superatmospheric pressures of up to 10 atmospheres or more may be employed with some advantage with the more volatile monomers. Superatmospheric pressures may also be em¬ ployed with those monomers having the requisite vol¬ atilities at reaction temperatures permitting reflux cooling of the reaction mixture. Further, the polymerization process may be carried out utilizing a full reactor technique. That is, the reaction vessel is completely filled with the polymerization medium and kept that way throughout the reaction by constant addition thereto of water or add- itional makeup liquid containing the monomer or mono¬ mers in the same proportions as at start-up. Upon the addition of a certain predetermined amount of liquid, the polymerization reaction is terminated, usually by the addition thereto of a shortstopping agent. The necessity for the addition of liquid is due to the shrinkage in volume of the reaction medium produced by the conversion of the monomer or monomers to the poly¬ meric state. In order to rate the various coatings, there has been devised a rating scale with respect to "paper" and "sandy" buildup. An uncoated reactor, where normal amounts of both types of buildup occur, is given a rating of 1.5 to 2.0. Any rating below 1.0 is good, or a definite improvement. In other words, 0.0 rating is perfect, and so on. To further illustrate the present invention, the following specific examples are given. It is to be understood, however, that this is merely intended in an illustrative and not limitative sense. In the examples, all parts and percents are by weight unless otherwise indicated. Example I In this example, the coating material employe was the sodium salt of the reaction product of resor¬ cinol and acetaldehyde. 50 gms. (0.454 mole) of resorcinol was added to a 250 ml. round bottom flask and 1 milliliter (ml.) of a 50% aqueous NaOH solution was added thereto. The mixture was heated and just enough water was added to form a liquid at 60°C. 13 ml. (0.225 mole) of acetaldehyde and 45 ml. of water were mixed in an add funnel which was connected to the re¬ action flask. The acetaldehyde solution was added dropwise (1 drop every 2 - 4 seconds) to the reaction mixture with vigorous stirring and maintaining the temperature at 60°C. After the reactants were mixed, the stirring was maintained at 60°C. for one hour. The add funnel was then removed and replaced with a still- head and condenser. The temperature was increased steadily and the water distilled off. The distillation was terminated when crystals of unreacted resorcinol appeared in the stillhead. This occurred when the oil bath temperature was 180°C. and the stillhead vapor temperature was 110°C. The finished reaction mixture was a dark red liquid. The mixture was cooled to 100°C. and then poured into 1000 cc's of 5% aqueous NaOH. The aqueous base solution of the oligomeric coating material was diluted to give a 1% by weight solution of the coating material in 1% by weight of NaOH. After cleaning the internal surfaces of a 3 liter stainless steel reactor with an abrasive cieaner, the surfaces were sprayed with the coating solution and then rinsed with water. Thereafter, the following polymerization recipe was charged to the reactor: Ingredient Parts Vinyl Chloride 100 Water (demineralized) 207 Polyvinyl alcohol ^ 0.05 Ingredient Parts Di-(sedondary butyl) peroxydicarbonate 0.05 88% hydrolyzed polyvinyl acetate The contents of the reactor were heated to 57°C. and the temperature maintained there throughout the reaction cycle. Water was -continuously added to the reactor in order to maintain the volume, due to shrinkage by reason of formation of polymer. When 33.45 parts of water had been added, the reaction was stopped by cooling the mixture rapidly. The reactor was emptied and the polymer recovered by filtration and drying. The interior surfaces were then rated for any buildup and then rinsed with water. Without recoating the internal surfaces of the reactor, the same procedure was followed in two additional runs or polymerization cycles. The surfaces were evaluated after each run. Also, a control run was made using the same recipe but in an uncoated reactor. The buildup ratings are set out in the following table: TABLE I RUN NO. Paper Sandy Build Up Build Up Control (Uncoated) 1.5 2.0 1. (Coated) 0 0.05 2. (Coated) 0.1 0.1 3. (Coated) 0.2 0.1 The above results clearly show the vastly improved results obtainable with the present inven- tion. Coating of the internal surfaces of the poly¬ merization reactor, in accordance with the present invention, substantially reduces, and in many cases, practically eliminates polymer buildup on said sur- faces during the polymerization reaction and thus OMPI results in increased production over a unit period of time. More importantly, the present invention enables one to operate a closed polymerization system, which, in the case of vinyl chloride polymerization, has the advantage of drastically reducing the parts per million of vinyl chloride in the atmosphere of the plant. Such reduction of vinyl chloride in the atmosphere meets U.S. Government requirements. Numerous other advant¬ ages of the present invention will be apparent to those skilled in the art. While the present invention has been des¬ cribed in terms of its specific embodiments, certain modifications and equivalents will be apparent to those skilled in the art and are intended to be includ- ed within the scope of the present invention, which is to be limited only by the scope of the appended claims. OMPI

Claims: CLAIMS 1. A process for substantially eliminating the buildup of polymers on the internal surfaces of a polymerization reaction vessel which comprises apply¬ ing to said surfaces an aqueous coating solution of an alkali metal or ammonium salt of an oligomer(s) having the general structure ' wherein R is H or an alkyl group, straight chained or branched, containing from 1 to 10 carbon atoms and χ is an integer from 1 to 10, and conducting the polymerization of monomer(s) while in contact with the coated internal surfaces of said vessel. 2. A process as defined in claim 1 wherein the monomer is vinyl chloride. 3. A process as defined in claim 1 wherein the oligome (s) is formed by the reaction of an aliphatic aldehyde and a polyhydric phenol. 4. A process as defined in claim 1 wherein the coating solution contains from about 0.1% to about 5.0% by weight of the salt of the oligomer(s). 5. A process as defined in claim 1 wherein the coated internal surfaces are rinsed with water prior to conducting the polymerization of monomer(s). 6. A process as defined in claim 1 wherein the coating solution has a pH in the range of about 9 to about 14. 7. A process as defined in claim 3 wherein the aliphatic aldehyde is acetaldehyde. 8. A process as defined in claim 3 wherein the polyhydric phenol is resorcinol. 9. A process as defined in claim 8 wherein the aliphatic aldehyde is acetaldehyde. Ol.lPI 10. A polymerization reaction vessel having on all the internal surfaces thereof a coating com¬ prised of an alkali metal or ammonium salt of an oli¬ gomerCsl having the general structure wherein R is H or an alkyl group, straight chained or branched, containing from 1 to 10 carbon atoms and χ is an integer from 1 to 10.. O PI

Inventors: DORSCH JOHN LAWRENCE, SMITH DAVID JOHN
Applicants: GOODRICH CO B F
Application year: 1981
Main classification: C08F2
IPC codes: C08F2, C08F14, C08F114