IMPREGNATED PAPER AND ITS USE

Abstract: Impregnated paper comprising a paper web, a pre-conden­ sate of a curable resin and a filler. The abrasion resistance is improved through use of an inorganic filler having particle sizes between 1 and 100 µandaspecificsurfacebetween 5 and 150 m²/g.

Description: IMPREGNATED PAPER, A PROCESS FOR ITS PRODUCTION AND ITS USE The present invention relates to an impregnated paper of the kind which comprises a paper web impregnated with a pre-condensate of a curable resin containing a filler. The invention also relates to a suitable process for production of the impregnated paper and to a suitable use for the paper. Background of the invention Impregnated paper is usually produced by passing a paper web through a solution or a dispersion of a pre-condensate of a curable resin and the impregnated paper is then dried. The obtained product is a semi-finished product to the extent that the residual adhesiveness of the resin can later be used to fix the paper to a substrate, generally a sheet material of wood or cellulose-based composite materials. The paper is hereby used to improve the surface of the sheet material, either with respect to its appearance or its chemical or mechanical resistance. There has been a need to improve the properties of the impregnated paper above what is obtained by the resin only, particularly as far as the mechanical wear resistance is concerned. Attempts with addition of wear-resistant fillers have not been succesful. For example, the fillers tend to settle in the impregnating solutions, which have a very low viscosity, with the result that the composition of the solutions will not be stable or the filler coating on the surface of the paper will not be uniform. Further, to improve the wear strength the filler must be very securely anchored in the resin layer and this has been difficult to achieve, partly because of a limited chemical bonding capability between resin and filler and partly because of the limited contact surface between these. The filler particle have consequently very easily come loose and not improved the abrasion strength to any considerable extent. Finally, as the resin layer on the impregnated papers is very thin there are especially high demands on the size distribution of the used fillers and on a very uniform mixing of the particles in the resin. It has been found that many fillers, for the above given reasons, cannot be used for impregnated papers, although the same fillers are quite satisfactory for other purposes, e.g. in moulding compositions or generally for products based on thermoplastics. The invention generally The object of the present invention is to provide an impregnated paper containing a filler, which paper does not have the above mentioned disadvantages. Particularly, the object of the invention is to provide an impregnated paper having improved wear resistance by selection of a filler which is securely anchored in the resin and which easily can be mixed into and distributed in this. A further object of the invention is to provide a particularly suitable method of production and a particularly suitable use of the impregnated paper of the invention. The above objects are achieved by means of the characteristic features given in the appended claims. According to the invention inorganic fillers are used, particularly silicates, which fillers have a considerable porosity, stated as a high specific surface in the claims. A high porosity is preferable for several reasons. A limited penetration of the resin into the particles gives a larger contact-surface between the resin and particle and an improved mechanical retention and the particles are thus more efficiently retained in the resin layer. The presence of resin in the particles reinforces these and decreases the problems of brittleness of the particles and this improves the general wear strength. As it is possible to make porous particles containing air-inclusions in the resin solution problems of sedimentation are avoided to a considerable extent and the light refraction and the brightness of the finished product are improved. Silicate materials generally have good adhesiveness towards the used resins and it has been found that particularly calcium silicates have good bonding properties to formaldehyde-based curable resins and that they are capable of influencing the reaction rate positively, near the surface of the particle. Further objects and advantages of the invention will be evident from the detailed description below. Detailed description of the invention Suitable resins for impregnation of paper according to the invention are formaldehyde-based curable resins, such as phenolic resins, melamine resins or urea resins. Phenolic resins have been found particularly suitable for the uses of the invention. The paper that is used can have a weight of between 10 and 150 g/m2 and preferably between 20 and 80 2 g/m . A suitable weight after impregnation and drying is between 30 and 400 g/m2 and preferably between 60 and 240 g/m2 . As a rule it is possible to use a lighter paper when it contains fillers according to the invention, than normally used for the corresponding purposes. The filler of the invention should have such a particle size distribution that the majority of the particles have a size of from 1 to 100/un, and preferably from 10 to 50 sm. By the majority of the particles should be understood at least 50 per cent and preferably at least 68 per cent of the number of particles. Particles having a size below 1 sm do not contribute to an improved wear strength to any extent worth mentioning and particles having a size above lOOJum tend to give the finished product an uneven surface. As has been mentioned the filler particles which are used should be porous and they can have a porosity, expressed as the ratio of bulk density to true density, of between 0.01 and 0.6 and particularly between 0.5 and 0.4. The specific surface should be high in order that the desired limited penetration of the resin into the pores will be obtained. 2 The surface (BET) is suitably between 5 and 150 m2/g and pre ferably between 15 and 100 m2 Ig. The true density should be kept below 3.5, as there might otherwise be sedimentation problems at the impregnation. It is preferred that the filler has alcaline reaction as this facilitates the curing of the resin, at and in the particles. Silicates are preferred among the inorganic filler that may be used, as the silicates have good abrasion resistance and an acceptable adhesion to the resins that are used. Calcium containin silicates are preferred as they, among other things, give a better adhesion to the resin. Calcium sili cate hydrates are particularly preferred because of their hardness, alcalinity and the possibility of a large specific surface. Suitable calcium silicate hydrates should have a mole ratio SO, to CaO above 0.7. The mole ratio should 2 not exceed 3.2 and is preferably within the range 1.0 to 3.0. The content of water of crystallization should not exceed 30 per cent by weight and preferably not exceed 20 per cent by weight. A suitable calcium silicate hydrate can be prepared by mixing a silicon dioxide raw material and a calcium oxide raw material to a mole ratio as above and suspending the finely divided components in water. The suspension is then autoclaved for a couple of hours at a temperature of from about 200 to about 400 0C and the product is subsequently dehydrated by heat treating at a temperature above 0 about 800 C. The obtained product has a large specific sur face and can be used as a filler directly. A pigment can optionally be incorporated immediately before use, or at the production so that it will be built into the crystalline structure. Treatment with coloring agent is anothermeth- od of obtaining a colored filler. The described filler can be added to the impregnated paper either by addition to the stock at the production of the paper web or by addition to the impregnating resin. The latter method is preferred with respect to wear resistance. The amount of filler should be between 2 and 40 per cent by weight, based on the amount of dry resin in the paper, and preferably between 10 and 30 per cent by weight based on the dry resin content. When a suitable impregnating solution is prepared the filler can be mixed directly into a prepared solution or dispersion of th'e pre-condensate. Slow addition and vigorous stirring are required as the porous filler otherwise easily forms lumps and precipitates. It is thus preferred that the filler is slurried in a liquid, separate from the resin solution, and that the slurry is then mixed with the resin solution. If pure water is used for preparing the slurry problems of resin precipitation in the pores of the filler will readily arise as the resin generally has limited water dilutability. It is'#thus preferred that the slurry medium at least partly consists of volatile alcohols, such as methanol and ethanol. When the slurry medium, the composition of the resin solution and the mixing conditions are selected care should be taken that only a limited penetration of the liquid phase into the pore structure of the filler particles will take place as remaining gas inclusions, among Other things, positively contributes to diminishing settling problems, according to what has been said above. When the impregnating solution has been prepared, the impregnation can be carried out in a known manner. The paper web is passed through the impregnating solution, optionally also passed through a couple of squeeze rolls to remove excess solution, and passed through a drying tunnel where it gets in contact with hot air having a temperature of about 100 to 170 0C. The obtained impregnated paper is a semi-finished product which can be used in the customary manner, e.g. for coating sheet materials of wood or cellulose-based composite materials such as particle board, plywood or fibre board. The paper is then pressed onto the sheet-formed substrate in a press at a temperature of about 110 to 150 0C and the resin then softens, moistens the substrate and is bonded to this when the resin is finally cured. The impregnated paper of the invention is particularly suitable for use when a high abrasion resistance is required, for example for use on floors, lorry platforms and moulds for concrete. Example A powder of calcium silicate hydrate having a particle diameter of between Ijum and 100 cm and a specific surface of 40 m2Sg was slurried in a liquid phase, consisting of equal parts of water and ethanol, to a solids content of the slurry of 50 per cent by weight. About 20 parts by weight of the slurry were mixed with about 80 parts by weight of an aqueous solution of a phenol-formaldehyde pre -condensate having a dry content of 50 per cent by eight. 2 A Apaper web having a basis weight of 25 g/m2 was passed through the obtained impregnating solution, passed through stripper rolls, and thereafter through a drying zone in contact with air having a temperature of 130 0C. The dried web had a basis weight of 120 g/m2. This paper was pressed onto a plywood sheet at a pressure of about 2 MPa and a temperature of about 1300C. The coated sheet was subjected to abrasion tests and was found to have about three times as high abrasion resistance as a corresponding sheet with a phenolic resin layer which did not contain a filler.

Claims: Claims 1. Impregnated paper comprising a paper web, re- -condensate of a curable resin and a filler, characterized in that inorganic particles are used as a filler,:which particles have sizes in the range of from 1 to 10 sm and a specific surface in the range of from 5 to 150 m /g. 2. Impregnated paper according to claim 1, character ized in that the inorganic particles are made up from cal cium silicate hydrate. 3. Impregnated paper according to claim 2, character ized in that the mole ratio of SiO2 to CaO in the calcium silicate hydrate is between 0.7 and 3.2. 4. Impregnated paper according to claim 3, character ized in that the mole ratio is between 1.0 and 3.0. 5. Impregnated paper according to claim 1, character ized in that the specific surface is between 15 and 100 m2 Ig. 6. Impregnated paper according to claim 1, character ized in that the curable resin in the pre-condensate is a phenolic resin. 7. Impregnated paper according to claim 1, character ized in that the amount of inorganic particles is from 10 to 30 per cent by weight of the amount of dry resin in the paper. 8. A process for the production of an impregnated paper according to claim 1, characterized in that an aqueous solution or dispersion of a pre-condensate of a curable resin is prepared, that inorganic particles having sizes in the range of from I to l00?1m and a specific 2 surface in the range of from 5 to 150 m Ig are slurried in a liquid phase, that the slurry is mixed with the aqueous solution of the pre-condensate and that a reaper is passed through the mixture, which paper is subsequently dried. 9. A process according to claim 8, characterized in that the inorganic particles are slurried in a mixture of water and a lower alcohol. 10. Use of an impregnated paper comprising a paper web, a pre-condensate of a curable resin and a filler consisting of inorganic particles having a size between 1 and 100 sm 2 and a specific surface between 5 and 150 m ig as an abrasion resistant coating material on wood or on cellulose-based composite materials.

Inventors: INGE, MATS
Applicants: AB CASCO
Application year: 1981
Main classification: D21H3
IPC codes: C08J3, D21H17