CERAMIC TILE ADHESIVES

Abstract: An adhesive for the efficient bonding of ceramic tiles and having improved water resistance comprises an emulsion copo­ lymer composition including an acrylate or methacrylate mono­ mer, a vinyl aromatic monomer, and, for reducing water sensi­ tivity, an unsaturated organosilicon compound. Compositions which are effective in promoting water resistant adhesion may contain as little as from 0.1-1.0% by weight of the unsaturated organosilicon compound.

Description: This invention relates to ceramic tile adhesives. The earliest method of sticking ceramic tiles was to use an hydraulic cement. Since then adhesives based on 100% reactive resin systems such as epoxide or unsaturated polyester resins, solvent solutions or acrylic polymers or elastomers, natural rubber latices, synthetic rubber latices, polyvinyl acetate or copolymer emulsions and acrylic copolymer emulsions have all become available. Besides all the applicational properties required e.g. open time (i.e. time during which the adhesive remains workable), slip, speed of drying and suitable rheology, cermic tile adhesives should have good resistance to wet conditions. One method of testing this is to carry out shear tests after sticking two tiles together and immersing them in water for 7 days as described in B.S. 5385: Part 1: 1976: Section A5.8. In general those adhesives based on non-aqueous systems e.g. epoxy resins show up best on this test. However, it is desirable on ground of cost and safety to use aqueous based systems but these usually have very inferior properties. B.P. 1,407,827 discloses the use of unsaturated organo-silicon compounds as co-monomers in polyvinyl ester copolymer emulsions. However, it is well known that many polyvinyl esters especially polyvinyl acetate are prone to hydrolysis. We now find that certain copolymer emulsions modified by the use of unsaturated organo-silicon monomers can be used as a basis of ceramic tile adhesives which provide excellent resistance to water. The monomers of the copolymer emulsions are vinyl aromatic monomers, acrylate or methacrylate monomers and, in small proportions, unsaturated organic acid monomers. The acrylate and methacrylate monomers are expensive and the use of the vinyl aromatic monomers reduces the cost of the final product. The acrylates or methacrylates may in particular be C₁-C₈ alkyl esters of acrylic or methacrylic acid but the invention is not limited to these. For instance C₉ and higher alkyl esters might be employed. Typical acrylates/methacrylates wich can be used in the polymers are methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, 2-ethyl hexyl acrylate, heptyl acrylate and the corresponding methacrylates. The vinyl aromatic monomer used in a copolymer emulsion composition of the invention may, for example, be styrene, vinyl toluene, chlorostyrene or t-butyl styrene. We also use, as a component additional to the vinyl aromatic monomer and acrylate or methacrylate small proportion (up to 10% by weight) of an unsaturated organic e.g. acrylic or methacrylic acid monomer in the copolymer. Typical unsaturated organo-silicon monomers are γ-methacryloxypropyl trimethoxy silane, vinyl triethoxy silane and vinyl trimethoxy silane. Although the unsatured organo-silicon monomers are rather expensive, we find that, by using emulsion polymerization, only very low quantities, i.e. from 0.1-1.0% by weight of unsaturated organo-silicon monomers, need be added to be effective in promoting water resistant adhesion. Preferred compositions embodying the invention will now be described with reference to the following Examples, which include an example of a known composition (Example 5) for comparison. Example 1 A styrene/ethyl acrylate/acrylic acid copolymer emulsion was prepared using 384 g of a mixed monomer feed (39.7, 59.6, 0.7% by weight respectively) fed to a reaction vessel. The temperature was maintained at 60 ± 2°C until polymerization was complete, using a redox system. 56.8 g of a mixture of styrene, acrylic acid and γ-methacryloxypropyl trimethoxy silane (81.3, 16.9, 1.8% by weight respectively) was then added to the polymer emulsion and polymerised under similar conditions. By this manner a shell of polymer containing Si-OH or Si-OCH₃ groups in the chain around a core of styrene/ethyl acrylate copolymer was obtained. This emulsion had a solids content of 45%. Example 2 A ceramic the adhesive was made by mixing the following:- When this adhesive was used to stick two tiles together as described in B.S. 5358: Part 1: 1976: Section A5.8, the shear strength was 0.9 MPa after 7 days immersion in-water. This compares with 0.4 MPa minimum in the specification. Example 3 A styrene/butylacrylate/acrylic acid/methacryloxypropyl triethoxy silane (55/42/2.8/0.2% by weight) copolymer emulsion was made using an anionic surfactant, pre-emulsified monomer feed and a redox polymerization system at 60°C. The pH of the final emulsion polymer was adjusted to pH 8.0-9.0 using ammonia and the solids content was adjusted to 45%. Example 4 A ceramic tile adhesive was made by mixing the following:- When tested in the same way as the adhesive in Example 2 the shear strength was 0.7 MPa. Example 5 A ceramic tile adhesive was made up to the formulation shown in Example 4 except that an emulsion omitting the unsaturated silane component was used. In this case the British Standard test gave a shear strength below the 0.4 MPa minimum requirement.

Claims: An aqueous emulsion polymer composition for use as a ceramic tile adhesive, containing filler material and an emulsion polymer of at least one acrylate monomer selected from acrylates and methacrylates and at least one vinyl aromatic monomer, the composition being prepared in the presence of at least one unsatured organosilicon monomer and the emulsion polymer containing a small proportion of unsaturated organic acid residues derived from a small proportion of unsaturated organic acid monomer. An emulsion polymer composition according to Claim 1, wherein the unsatured organo- silicon monomer is a vinyl or acrylic monomer capable of copolymerizing with the vinyl aromatic monomer. An emulsion polymer composition according to Claim 2, wherein the unsaturated organo-silicon monomer is selected from the group consisting of γ-methacryloxypropyl trimethoxy silane, vinyl triethoxy silane and vinyl trimethoxy silane. An emulsion polymer composition according to any one of the preceding Claims, wherein the amount of organo-silicon compound present in the composition is from 0.1-1.0% by weight based on the weight of the monomers. An emulsion polymer composition according to any one of the preceding Claims, wherein the acrylate monomer is selected from the group consisting of methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, 2-ethyl hexyl acrylate, and heptyl acrylate. An emulsion polymer composition according to any one of the preceding Claims, wherein the vinyl aromatic monomer is selected from styrene, vinyl toluene, chlorostyrene and t-butyl styrene. An emulsion polymer composition according to any one of the preceding Claims, wherein the unsaturated organic acid residues are provided by acrylic or methacrylic acid. An emulsion polymer composition according to any one of the preceding Claims, wherein the polymer is a core-shell polymer.

Inventors: SAUNTSON, BARRY JOHN
Applicants: SCOTT BADER COMPANY LIMITED
Application year: 1981
Main classification: C09J4
IPC codes: C08F265, C09J125