PROCESS FOR MANUFACTURING AROMATIC POLYESTERS

Abstract: Described is a process for manufacturing aromatic polyesters by reacting an aromatic dicarboxylic adic dichloride with an alkali metal salt of a bisphenol in an aqueous solution which comprises adding 0.01 to 100 mol %, based on the total monomer quantity, of an acid halide into the reaction system.

Description: PROCESS FOR MANUFACTURING AROMATIC POLYESTERS This invention relates to a process for manufacturing aromatic polyesters, and more particularly, to an improvement in the interfacial polymerization process for manufacturing aromatic polyesters. A number of processes, such as the interfacial, solution or melt polymerization, are known for the manufacture of aromatic polyesters. Japanese Patent Publication No. 1959/1965 discloses an interfacial polymerization process in which aromatic dicarboxylic acid chlorides dissolved in an organic solvent which is incompatible with water are mixed with bisphenols dissolved in an aqueous alkali solution. Japanese Patent Publication No. 5599/1962 discloses a solution polymerization process which comprises reacting aromatic dicarboxylic acid chlorides and bisphenols in an organic solvent. Japanese Patent Publication Nos. 15247/1963 and 28119/1968 disclose a melt polymerization process which comprises heating phenyl'esters of aromatic dicarboxylic acids and bisphenols together. The aromatic polyesters prepared by these processes have outstanding heat resistance and mechanical and electrical properties, and are useful for a wide range of applications, including the manufacture of molded products, films and fibers. According to the known interfacial polymerization process, a solution of an aromatic dicarboxylic acid chloride in an organic solvent incompatible with water, and a solution of a bisphenol in an aqueous alkali solution are mixed together under intensive agitation. A product having a high degree of polymerization can be obtained if a quaternary ammonium or phosphonium salt is used as a catalyst. If the agitation is discontinued, the reaction product usually separates into an aqueous solution phase containing inorganic salts, and a cloudy or opaque organic solvent phase containing the polymer and water in the form of an emulsion. There are some cases in which no phase separation occurs. It is, therefore, necessaryto separate a lot of water from the polymer. In order to overcome these disadvantages, it has been proposed to adjust the pH value of the aqueous phase to at least 12 and heat it in order to destroy the emulsion (Japanese Patent Publication No. 2679/1978), treat the reaction product with an aqueous solution containing a lower aliphatic alcohol which is soluble in acetone or water (Japanese Patent Publication No. 12133/1980), use a centrifugal separator (Japanese Laid-Open Patent Specification No. 55286/1973), or employ specific agitating conditions (Japanese Patent Publication No. 41249/1980). The inventors of this invention have found it possible to overcome the disadvantages if a catalyst composed of a specific compound, i.e., an oil-soluble phase transfer catalyst, is employed. The inventors have further discovered that the organic solvent phase containing the polymer, and the aqueous phase can be separated from each other quickly after the discontinuation of agitation if the specific compound is incorporated into the reactipn system. Thus, this invention provides a process for manufacturing aromatic polyesters by reacting an aromatic dicarboxylic acid dichloride with an alkali metal salt of a bisphenol, characterized by adding 0.01 to 100 mol % of an acid halide, based on the total monomer quantity, into the reaction system. DETAILED DESCRIPTION OF THE INVENTION Although various acid halides can be employed in accordance with this invention, it is particularly desirable to use acid monohalides typically represented by formula (1): R-Y-X (1) in which R stands for a monovalent organic group such as an alkyl, alkenyl or aromatic such as aryl or aralkyl group, or the substituted product thereof, Y stands for a divalent group such as -CO-, -SO2-, -SO-, -PO2 - or -PO-, and X stands for a halogen atom such as F, Cl or Br. It is usually suitable to use as R a group having l to 30 carbon atoms. Specific samples of these halides may include acetic acid chloride, bultyrlc acid chloride, octylic acid chloride, benzoyl chloride, benzenesulfonyl chloride, benzenesulfinyl chloride, and benzenephosphonyl chloride, and the substituted products thereof. The quantity of the specific compound may usually be in the range of 0.01 to 100 mol %, or preferably 1 to 100 mol %, or from an economical view not more than 30mol iO,b-ased on the total monomer quantity, depending on the poly merization conditions. The specific compound may be added during the course of the polymerization reaction, or preferably at a time after the polymerization conversion, which means polymer per monomers in weight % becomes 50 or more preferably after when the polymerization reaction terminates substantially. In order to obtain a higher molecular weight, however, it is desirable to add the compound after the completion of the polymerization, i.e., after the intended degree of polymerization has been reached. If the compound is added after the completion of the polymerization reaction, it is sufficient to effect agitation for a period of 5 to 30 minutes thereafter. Even if agitation is continued for a longer time, the two phases can be separated from each other quickly after the agitation has been discontinued. Any inorganic salt resulting from the polymerization is completely extracted into the aqueous phase at a temperature usually between 0 and 100 C. According to the earlier invention of the inventors, the use of an oil-soluble phase transfer catalyst (hereinafter called PTC) made it possible to produce aromatic polyesters having a high molecular weight, while preventing the reaction system from emulsification. This invention provides a further improved process which enables an improved separation of the organic solvent phase containing the polymer from the aqueous phase. If a crown ether, which is one of the oil-soluble PTC, is employed, however, this invention does not produce any greatly improved result, since the crown ether itself is very effective for the phase separation. In order to manufacture aromatic polyesters in accordance with this invention, it is possible to use any known aromatic dicarboxylic acid dihalide and any known bisphenol. The preferred dihalides, especially dichlorides are shown by the formula: EMI4.1 wherein Ar is a divalent aromatic group usually containing from 8 to 30 carbon atoms such EMI4.2 EMI5.1 where X i, m are each 0 or 1 and preferably both m and n are not 0 at the same time, A is a divalent hydrocarbon group containing 1 to 10 carbon atoms such as an alkylene, cyzloalkylene, alkylidene or cylo- alkylidene group, the halogen substituted groups thereof or a nucleus substituted group thereof or a member selected from -0-, -S-, -SO2-, -CO-, -PO2- and -PO-, Z and Z' are each halogen atoms. Examples of the dichlorides include terephthalic and isophthalic acid chloride, or other compounds having a functional group in the same aromatic ring, 2,2- (4,4 '-dichlorocarbonyl-diphenyl)propane, (4,4'-dichlorocarbonyl-diphenyl)ether, polynuclear aromatic dicarboxylic acid dichlorides, 1,4-naphthalene dicarboxyl acid dihalide, 2,6-naphthalene dicarboxyl acid dihalide, the nuclear-substituted compounds thereof and mixtures of the foregoing compounds. Any of the known bisphenols may be employed for the present invention The preferred bisphenols usually contain 6 - 30 carbon atoms and are shown by the formula: EMI5.2 where, n, p are whole numbers of 0 to 4, R1, R2 are each a member selected from a hydrocarbon or a substituted hydrocarbon group containing 1 to 20 carbon atoms such as alkyl, alkenyl, alkynyl, aryl, aralkyl, alkoxy, aryloxy, aralkoxy, thioalkyl, alkylamino or arylamino groups, halogen atoms and nitro groups. One can observe a further advantage which is shown as a remarkable decrease in clouring which otherwise occurs in the stage of drying the resulting polymer, when a bisphenol having at least one substituted group located in the ortho position to the phenolic OH group, this case meeting 1Cn + p < 8 in the above formula, is employed. Specific Examples o= the bisphenols are bis(3 methyl-4 -hydroxyphenyl) methane, 2, 2-bis (3-methyl- 4 -hydroxy- phenyl)-propane, bis(3-methoxy-4-hydroxyphenyl)methane, 2,2-bis (3-methoxy-4-hydroxyphenyl)propane, bis(3-chloro-4-hydroxyphenyl) methane, (3-isopropyl-4-hydroxyphenyl) ether, bis (4-hydroxy-2,6-dimethyl-3-methoxyphenyl)methane, 2,2-bis (2,6-dimethyl-3-methoxyphenyl)methane, 2,2-bis(3,5-dimethyl -4-hydroxyphenyl)propane, 2,2-bis-(3,5-di-sec-butyl-4-hydroxyphenyl)propane, 2,2-bis-(3,5-di-tert-butyl-4-hydroxyphenyl)propane, bis(3,5-dimethyl-4-hydroxyphenyl)methane, 1,1-bis( 3,5-dimethyl-4-hydroxyphenyl)ethane, 1,1-bis(3,5-dimethyl-4hydroxyphenyl)cyclohexane, 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane, 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane, 2,2-bis(3-bromo-4-hydroxy-5-methylphenyl)propane, bis(3,5dimethyl-4-hydroxyphenyl)sulfone, bis(3,5-dimethyl-4 hydroxyphenyl) ketone, bis (3, 5-dimethyl-4-hydroxyphenyl) - ether, bis (3, 5-dimethyl-4-hydroxyphenyl) sulfide, 2,2bis(3,5-dimethyl-4-hydroxyphenyl)hexafluoropropane, 2,2bis(3,5-dimethoxy-4-hydroxyphenyl)propane, bis(3,5dimethoxy-4-hydroxyphenyl)methane, 2,2-bis(3-methoxy-4hydroxy-5-methylphenyl)propane, bis (3-methoxy-4-hydroxy- 5-methylphenyl)methane, 2,2-bis(3,5-diphenyl-4-hydroxyphenyl)propane, bis(3,5-diphenyl-4-hydroxyphenyl)methane, 2,2-bis(3,5-diphenoxy-4-hydroxyphenyl)propane, bis(3-phenoxy-4-hydroxy-5-methyl)methane, 3,3',5,5'tetramethyl-4,4'-dihydroxy-biphenyl, 3,3', 5,5'-tetraphenyl 4,S'-dihydroxy-biphenyl, 1,4-dihydroxy-2-methoxy-benzene, 1,3-dihydroxy-6-methoxy-benzene. The bisphenols are used either alone or, in a mixture, or in combination of (A) the above compounds having a nucleus substituted group with (B) those having no such substitution or with a polyaromatic diol such as 1,4-dihydroxy-naphtalene. When using the above combination the molar ratio of (A)/(B) is 100/0 to 1/99, preferably 100/0 to 10/90. The bisphenols are introduced into the reaction system in the form of an alkali solution. The phase transfer catalysts used in the present invention are e.g. guaternary ammonium salts1 quarternary phosphonium salts or crown ethers. Specific examples of the quaternary ammonium salts are tetraethyl ammonium chloride, tetrabutyl ammonium chloride, trioctylmethylammonium chloride, benzyltributylammonium chloride, benzyltriethylammonium chloride, benzyltrimethylammonium chloride, cetyldimethylbenzylammonium chloride, octyltriethylammonium bromide, decyltriethylammonium bromide, lauryltriethylammonium bromide, cetyltriethylammonium bromide, N-lauryl-pyridinium chloride, N-laurylpyridinium bromide and N-heptylpyridinium bromide. Specific examples of the quaternary phosphonium salt are tetrabutylphosphonium bromide, triethyloctadecylphosphonium bromide, tetraphenylphosphonium bromide, triphenylmethylphosphonium bromide, trioctylethylphosphonium bromide and cetyltriethylphosphonium bromide. As crown ether all of those can be used which are capable of forming a complex with an alkali metal ion so as to activate a phenolate ion to be paired, e.g. 18-crown-6, dibenzo-18-crown-6, dicyclohexyl-1 8-crown-6, dibenzo-24-crown-8, 12-crown-4, 15-crown-5, cyclohexyl12-crown-4, tribenzo-1 8-crown-6, tetrabenzo-18-crown-6 and dibenzo-26-crown-6. The catalyst is used in an amount of from 0.01 to 20% by mole, preferably 0.1 to 10% by mole, based on the total acid dichloride. It is possible to use any organic solvent if it is substantially insoluble in water. Usually chlorinated hydrocarbons are employed, such as methylene chloride, chloroform, ethylene dichloride, 1,1,2-trichloroethane, 1,1 ,2, 1 -tetrachloroethane, or orthodichlorobenzene, but it is also possible to use an organic solvent which is inactive (inert) under the reaction conditions, for example, nitrobenzene, toluene or xylene. Further, monofunctional compounds such as phenols, thiols or amines may be added in order to obtain a polymer having the exact desired molecular weight. The polymerization reaction is effected usually at a temperature between 0 to 1000C for about 2 to 5 hours. The aromatic polyester thus produced can be recovered by conventional methods after the organic phase containing the polymer has been separated from the aqueous phase. For example, it is possible to precipitate the polymer by adding an organic solvent which does not dissolve the polymer, or to pour the reaction product into hot water to evaporate the solvent and solidify the polymer. It is also possible to obtain a polymer film directly by casting the solution. The polymer can, thus, be collected in the form of powder, particles, a film or fibers. The invention will now be described in further detail with reference to several examples which do not limit the scope of this invention. EXAMPLE 1 5.7 g (0.025 mol) of 2,2-bis(4-hydroxyphenyl)propane and 3.2 g (0.0125 mol) of bis(3,5-dimethyl-4hydroxyphenyl)methane were dissolved in 150 ml of water containing 5.63 g of sodium hydroxide. 7.62 g (0.0375 mol) of terephthalic acid chloride were dissolved in 150 ml of methylene chloride, and 0.38 g of trioctylmethylammonium chloride was added. The two solutions thus prepared were mixed, and reacted with each other for two hours at room temperature under intensive agitation. When the agitation was discontinued, a polymer solution in the form of oil droplets was was found in the reaction system. To this polymer solution were added 1.22 g (0.0087 mol) of benzoyl chloride, and agitation was continued again for five minutes. The agitation was discontinued, and the content of the reactor was separated completely into an aqueous phase and an organic phase within five minutes. The inherent viscosity [N ] of the resulting polymer was Q.6. The viscosities were measured in CHC13 at 32"C in all examples. EXAMPLE 2 2.28 g (0.01 mol) of 2,2-bis(4-hydroxyphenyl)propane were dissolved in 20 ml of water containing 1 g of sodium hydroxide. 1.02 g (0.005 mol) of terephthalic acid chloride and 1.02 g (0.005 mol) of isophthalic acid chloride were dissolved in 40 ml of methylene chloride, and 0.12 g of benzyltriethylammonium chloride was added. The two solutions thus prepared were mixed at a temperature of 0 to 100C under intensive agitation. When the agitation was discontinued after three hours, the methylene chloride phase was cloudy, and not completely separated from the aqueous phase. To the mixture were added 0.61 g (0.0043 mol) of benzoyl chloride, and agitation was continued again for five minutes, whereby the reaction mixture immediately separated into a transparent organic phase and an aqueous phase. A polymer having an inherent viscosity ] of 0,5 was obtained after reprecipitation with methanol from the organic phase employing a separatory funnel. EXAMPLE 3 A 300 ml flask, equipped with a stirrer and a condenser was charged under a nitrogen atmosphere with 1.52 g (6.67 m mol) 2,2-bis(4-hydroxyphenyl)-propane and 3.41 g (13.33 m mol3 of bis(3.5-dimethyl-4-hydroxyphenyl)-methane, and then with a solution cooled to 10C containing 0.38 g (0.40 m mol) of laurylpyridinium chloride (30% by wt aqueous solution), 4.00g (50 m mol) of sodium hydroxide and 40 ml of water. Into the flask 4.10 g (20.2 m mol) of terephthalic acid dichloride dissolved in 40 ml of methylenechloride and held at 10C was gradually added under stirring. During the progress of the reaction the system became more and more emulsified. 90 minutes later the organic phase containing the polymer and the aqueous phase did not separate even after standing for a long time. Thereafter, 0.5 ml of benzoyl chloride was added to the system and the system was stirred for 20 minutes. This time the two phases separated completely after standing for a few minutes. After separating the aqueous phase by decantation, the organic phase was neutralized using diluted-hydrochloric acid and then washed with water. A precipitation of a white and fibrous polymer was observed when the resulting organic phase was poured into methanol. The polymer was then filtered off, washed with acetone and finally dried at 1200C under reduced pressure. A white, non-coloured polymer having an [?1]of 0.950 was obtained in 100% yield. EXAMPLE 4 A solution was prepared by dissolving 1.14 g(5 m mol) of 2,2-bis(4-hydroxyphenyl)-propane and 1.28 g (5 m mol) of bis(325-dimethyl-4-hydroxyphenyl)-methane in an aqueous solution containing 1.5 g of sodium hydroxide and 40 ml of water. Another solution was prepared by dissolving 2.10 g of terephthalic acid dichloride in a mixed solvent containing 30 ml of methylene dichloride and 10 ml of toluene and then adding thereto 0.1 g (2.5 mol% of terephthalic acid dichloride) of trioctylmethyl ammonium as a catalyst. The two solutions were mixed and the reaction between the monomers was effected under vigorous agitation. An emulsification occurred between the organic phase containing the polymer and the aqueous phase during the progress of the reaction. After 90 minutes the two phases could not be separated even after standing for a long time. A small portion of the emulsion was taken out and dried. The polymer thus obtained was colored purple. On the other hand 0.5 ml of benzoyl chloride was added to the rest of the emulsion. The emulsion was stirred for 20 minutes and then two phases separated after allowing to stand for a few minutes. The procedure to obtain the polymer from the emulsion follows Example 3. The polymer obtained was not at all coloured even when dried at 1000C. The polymer has an [71] of 0.4.

Claims: WHAT IS CLAIMED IS: 1. In a process for manufacturing aromatic poly esters buy reacting an aromatic dicarboxylic acid dichloride with an alkali metal salt of a bisphenol in an aquous solution, the improvement which comprises adding 0.01 to lOOmol %, based on the total monomer quantity, of an acid halide into the reaction system. 2. A process of claim 1, wherein said acid-halide is added at a time when the conversion degree is not lower than 50%. 3. A process of claim 1, wherein said acid halide is added at a time after substantially terminating the polymerisation reaction. 4. A process of claim 1, wherein said acid halide is at least one of the compounds of the formula: R-Y-X where R stands for a monovalent organic group, Y stands for a group selected from the group consisting of -CO-, -S02- -SO-, -P02 - and -PO-, and X stands for an halogen. 5. A process of claim 4, wherein said monovalent organic group is a divalent hydrocarbon group containg from one to 30 carbon atoms. 6. A process of claim 5, wherein said divalent hydro carbon group is a member selected- from a group consisting of alkyl group, alkenyl group, aryl group and aralkyl group. 7. A process of claim l, wherein the amount of said acid halide is 0.01 to 100 mol% based on the total monomer quantity. 8. A process of claim 5, wherein the amount of said acid halide is one to 30 mol % based on the tatal monomer quantity. 9. A process of claim 1, wherein said aromatic polyesters are prepared by polymerizing aromatic carboxylic acid dihalides and bisphenols. 10, A process of claim 7, wherein said carboxylic acid dihalide is a carboxylic acid dichloride containing fr6m 8to 30 carbon atoms. 11. A process of claim 7, wherein said bisphenol contains from 6 to 30 carbon atoms. 12. A process of claim 1, wherein said aromatic polyester is prepared in the presence df a phase transfer catalyst.

Inventors: ASADA, MASAHIRO, AZUMA, MIYUKI, YONEZAWA, KAZUYA
Applicants: KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1981
Main classification: C08G63
IPC codes: C08G63