PREPARATION OF FLUID BED-CATALYSTS CONTAINING THE MIXED OXIDES OF VANADIUM AND PHOSPHORUS

Abstract: A process for the preparation of a fluid bed oxidation catalyst containing the mixed oxides of vanadium and phosphorus, comprising: (a) preparing a catalyst precursor containing a vanadium phosphorus mixed oxide; (b) comminuting the catalyst precursor; (c) introducing the catalyst precursor into water prior or subsequent to comminution thereof to form an aqueous slurry; and (d) spray drying said slurry to form microspheroidal catalyst particles is provided, as well as the use of such catalyst in the oxidation 4-carbon atom hydrocarbons, in particular n-­ butane to produce maleic anhydride. The catalysts prepared from catalyst precursors in organic medium retain their high activity from the above method is used for their preparation.

Description: Preparation of Fluid Bed-Catalysts containing the mixed oxides of Vanadium and Phosphorus, catalysts so produced and use in oxidation of C4 hydrocarbons This invention relates to a method for preparing fluid bed catalysts useful in the production of dicarboxylic acid anhydrides by the oxidation of hydrocarbon. More particularly it is directed to the preparation of fluid bed catalysts suitable for producing maleic anhydride from 4-carbon atom hydrocarbons, such as n-butane, n-butenes, 1,3 butadiene or a mixture thereof. The advantages of fluid bed hydrocarbon oxidation processes compared to fixed bed hydrocarbon oxidation processes are well known in the art, including the improvement of temperature control and heat transfer for oxidation reactions. Catalysts which are suitable for fixed bed processes are not necessarily suitable for fluid bed processes. Despite the incentive to utilize fluid bed technology in the production of maleic anhydride from 4-carbon atom hydrocarbons, there currently is no commercial fluid bed plant of this type in operation, all such commercial plants being fixed bed operations. Catalysts containing vanadium and phosphorus oxides have been used in the oxidation of 4-carbon atom hydrocarbons, such as n-butane, n-butenes, 1, 3 butadiene or mixtures thereof with molecular oxygen or oxygen-containing gas to produce maleic anhydride. Conventional methods of preparing these catalysts involve reducing a pentavalent vanadium compound, and combining the same with a phosphorus compound, and if desired, promoter element compounds under conditions wilich will provide vanadium in a valence state below +5 to form catalyst precursors capable of being converted to an oxide. The catalyst oxide precursor is then recovered and calcined, before or after the fixed bed catalyst particles are formed to provide active catalytic material. U.S. Patents 3,888,886; 3,905,914; 3,931,046; 3,932,305 and 3,975,300 disclose the testing of promoted vanadium phosphorus oxide catalysts for maleic anhydride production from butane in one inch diameter fluid bed reactors. In most instances, the catalysts were prepared by forming the catalyst precurson in aqueous media (in 3,975,300 the precursor was formed in a paste of vanadium compound, a phosphorus compound and an organic reducing agent), drying and thereafter grinding and sieving the precursor to a powder of about 74 to 250 microns size. This manner of preparation, however, does not result in the uniform, microspheroidal catalyst particles preferred for successful fluid bed operation. Commercial fluid bed catalysts are preferably microspheroidal particles within the range of 20 to 300 microns in average diameter, preferably having 80% of the particles within the range of 30 to 80 microns in diameter. Most preferably, 25 to 40% of the particles have an average diameter of less than 45 microns. It is therefore an object of the invention to provide a process of preparing fluid bed oxidation catalysts containing a mixture of the oxides of vanadium and phosphorus. It is a further object of the invention to provide a process for producing maleic anhydride from 4-carbon atom hydrocarbons utilizing such catalysts. We have found according to the invention that excellent uniform, microspheroidal vanadium phosphorus mixed oxide containing catalysts, useful in the production of maleic anhydride from 4-carbon atom hydrocarbons in fluid bed operations, can be obtained by spray drying an aqeuous slurry of the catalyst precursor. Although this method of preparation may be utilized in forming fluid bed vanadium phosphorus mixed oxide catalysts prepared in aqueous media, it is unexpectedly efficacious when utilized in forming such catalysts in which the precursor was prepared in organic liquid solution or slurry. It had previously been found that the preparation of vanadium phosphorus mixed oxide precursors in organic liquid media, solutions or slurries, particularly if maintained as essentially anhydrous, resulted in catalysts of high surface area and enhanced activity for the production of maleic anhydride from 4-carbon atom hydrocarbons. The presence of an excess of water in the final stages of preparation diminished both the surface area and activity of the catalysts. The formation of fluid bed catalysts by spray drying an organic liquid slurry of the catalyst precursor, because of flammability of the organic media, is not preferred. We have found that once the vanadium-phosphorus mixed oxide precursor has been formed, it may be introduced into water to form an aqueous slurry which may then be spray dired to form microspheroidal fluid bed catalysts, without adversely affecting the surface area or activity of the catalyst. According to the invention there is provided a process for the preparation of a fluid bed oxidation catalyst containing the mixed oxides of vanadium and phosphorus, comprising: (a) preparing a catalyst precursor containing a vanadium phosphorus mixed oxide; (b) comminuting the catalyst precursor; (c) introducing the catalyst precursor into water prior or subsequent to communition thereof to form an aqueous slurrys and (d) spray drying said slurry to form microspheroidal catalyst particles. Catalyst precursors of vanadium phosphorus mixed oxide catalysts for hydrocarbon oxidation may be prepared according to methods knows in the art. U.S. Patent No. 4,002,650 discloses the preparation of vanadium and phosphorus mixed oxide containing catalysts by reacting vanadium and phosphorus compounds in an aqueous solution, with HC1 being utilized as a solvating and reducing agent for vanadium. Similar preparational techniques are described in European Patent Appln. No. 3,431 in which the additional step of comminuting the vanadium-phosphorus precursor to a. particle size of 500 to 700 microns (0.5 to 0.7 mm) is disclosed. U.S. Patent No. 4,043,943 discloses the preparation of the catalyst precursor in a liquid organic medium, preferably anhydrous, wherein the vanadium compound is reduced and solvated by gaseous HC1 followed by reaction with the phosphorus compound. The preparation of oxidation catalysts containing the mixed oxides of vanadium and phosphorus is disclosed in European Patent Appln. 80304635.8 (0031696) wherein a vanadium compound is at least partially solubilized in an organic liquid medium capable of reducing at least a portion of the vanadium to a +4 valence state, and unsolubilized vanadium having a particle size larger than about 0.1 mm diameter is removed from the medium before addition of a phosphorus-containing compound. The preparation of such catalysts is disclosed European Patent Appln. 81300972.7 wherein partial reduction of a pentavalent vanadium compound is effected in the presence of a phosphorus compound in an organic liquid medium capable of reducing the vanadium. The catalysts precursor may be recovered from the liquid reaction medium in which it was prepared (preferably an essentially anhydrous maintained organic liquid medium) by conventional methods,- such as evaporation, filtration, centrifugation or decanting. The precursor is then preferably dried by heating. Alternatively, the recovered precursor, which is still partially wet with the organic liquid, may be treated with a low boiling solvent such as petroleum ether. In another embodiment, excess preparational reaction media may be substantially removed by vacuum filtration. In yet another embodiment, excess water can be introduced into the precursor containing organic liquid reaction medium, allowing an organic layer to separate from the aqueous layer. After recovery, the catalyst precursor is comminuted before it is introduced into water to form an aqueous slurry. The catalyst precursor as produced generally has a particle size of greater-than one micron average diameter before it is comminuted. It is preferred, however, that a substantial portion of the catalyst precursor be reduced in particle size to less than one micron, and preferably less than one half micron average diameter. This step of comminuting may be accomplished before the precursor is recovered from its reaction media, or after recovery. Comminution after recovery can be effected either prior or subsequent to introduction into water. For example, dried catalyst precursor particles may be dry milled, such as by ball milling, or the catalyst precursor containing aqueous slurry may be ball milled. The catalyst precursor preferably should be uncalcined when introduced into water. Substantial contacting of the calcined vanadium phosphorus mixed oxide catalyst with water (at less than 1000 c) reduces the activity of the catalyst particularly if calcined in air. The solids content of the catalyst precursor containing aqueous slurry should be adjusted to 25 to 60 weight percent. The catalyst precursor-containing aqueous slurry is then spray dried to form uniform, microspheroidal particles having a particle size range of between 20 to 300 microns, generally between 20 to 240 microns. Spray drying may be accomplished by methods known in the art. The catalyst precursor may contain promoter elements including but not limited to U, Co, Mo, Fe, Zn, Hf, Zr or mixtures thereof. These may be incorporated into the catalyst precursor in any of the methods known in the art, such as inclusion via the liquid reaction medium prior to or after reduction of the vanadium. Incrt diluents or supports may be added to the fluid bed catalyst, such as by addition of the diluent or support to the a(lueous slurry prior to spray drying. Catalyst suitable for the production of maleic anhydride from 4-carbon atom hydrocarbons generally have a phosphorus to vanadium ratio of 3:1 to 0.5:1. A P/V ratio of approximately is is preferred. These catalysts preferably exhibit an average valence for vanadium within the range of +3.5 to +4.6. The catalyst may be calcined in air or an oxygen (ontaillingr gas at a temperature of 250 C. to 600 C. for a period of up to 5 hours or more. One method of calcination of the catalyst is accomplished by heating the catalyst in a mixture of steam and air or air alone over the catalyst at a temperature of 300 C. to 5000C. for a period of 1 to 5 hours. The catalyst may also be calcined in the presence of hydrocarbon, an inert gas, or both. The fluid bed catalyst prepared by the process of the present invention may be utilized in oxidation type fluid bed reactors known in tile art. The hydrocarbon reacted to form maleic anhydride may be n-butane, n-butenes, 1,3-butandiene, or a mixture thereof. it is preferred to use n-butane or a mixture of hydrocarbons that are produced in refinery streams. The molecular oxygen is most conveniently added as air, but synthetic streams containing molecular oxygen are also suitable. In addition to the hydrocarbon and molecular oxygen, other gases may be added to the reactant feed. For example, steam or nitrogen could be added to the rcactants. Tic nitie of the rcactawlts may vary widely and is not critical. The ratio of molecular oxygen to the hydrocarbon may range from 3 to ,0 moles of oxygen per mole of hydrocarbon. Preferred oxygen/hydrocarbon ratios are from 4 to 20 moles of oxygen per of hydrocarbon. The reaction temperature may vary widely and is dependent upon the particular hydrocarbon and catalyst employed. Normally, temperatures of 2500 C. to 6000 C. are employed with-temperatures of 3250 C. to 5000 C. being preferred. The contact time may be as low as a fraction of a second or as high as 50 seconds. The reaction may be conducted at atmospheric, superatmospheric or subatmospheric pressure. Operation at superatmospheric pressure is preferred, from greater than one atmosphere to about three atmospheres. The following Examples illustrate the invention: The fluid bed catalyst described in Examples 1-8, below were used to produce maleic anhydride from n-butane in an 80cc fluid bed reactor consisting of 35.5 cm length of stainless steel tubing having an outer diameter of 3.8 cm, having a stainless steel frit at the bottom of the tube to act as a gas (air) distributor and an axial l.3cc outer diameter gas (hydrocarbon sparger/thermowell. The assembly contained an aluminium block pre-heater for the gases, and heating of the reactor unit was accomplished by placement in a temperature controlled molten salt bath. The fluid bed catalyst described in Examples 9-47, below were used to produce maleic anhydride from n-butane in a 440cc fluid bed reactor consisting of a 61 cm length of stainless steel tubing having an outer diameter of 3.8cm having a stainless steel sparger at the bottom of the tube to act as a gas (air) distributor, with an axial 0.64cm outer diameter thermowell and a separate hydrocarbon inlet at the bottom of the tube. The reactor was fitted with internal gas redistributing baffles. Gas preheating and reactor temperature control was accomplished by placement of the reactor unit in a thermostated fluidized sand bath. Flasks for receiving the product maleic anhydride were air cooled, and tail gases were routed to a Carle Analytical Gas Chromatograph III for analysis. Reaction conditions and results of the tests run are described in Tables I through III. The results are stated in terms as follows: Single Pass Yield = Moles of Maleic Anhydride Formed x 100 Moles of.Butane Fed Total Conversion = Moles of Butane Reacted x 100 Moles of Butane Fed Selectivity = Single Pass Yield x100 Total Conversion The throughput of hydrocarbon feed in the production of maleic anhydride, or the working rate imposed upon the catalyst is designated in the tables as WWH, or weight of feed/weight of catalyst/hour. Examples 1-7 A fluid bed catalyst having the formula V1.0P1.2Co0.20x, (where x = number of oxygens needed to satisfy the valence requirements of the other elements) was prepared by the following procedure. 1008g vanadium pentoxide and 528.2g cobaltous chloride dihydrate were added to 5.5 litres isobutanol with stirring to form a slurry. Anhydrous hydrogen chloride gas was bubbled through the liquid medium which was maintained by cooling at a temperature of about 20 + 50C. After dissolution and reduction of the vanadium (about 4 hours, at which time the temperature of the now-homogenous red-brown solution began to drop) 1303 g 100% ortho-phosphoric acid in 2 litres isobutanol was added to the liquid medium. The liquid medium was then refluxed for 2 hours, acquiring a blue-green colour. The solution was dried by evaporation at a temperature of 1500 C. The dried material was ground to yield a powdered catalyst precursor. 1500 g of the catalyst precursor powder was mixed with 3 litres water and the resulting slurry was milled for 12 ours. The comminuted catalyst precursor containing slurry was spray dried and calcined in air at 4000C for 16 hours. The resulting catalyst particles were dark green in colour and were microspheroidal in form. Results of the fluid bed (80cc) production of maleic anhydride from n-butane using the catalyst of Examples 1-7 are listed in Table I. Example 8 A fluid bed catalyst having the formula V1.0P1.2Co0.2Ox were prepared according to the procedure set forth in Examples 1-7 above, except that 935.5g uranyl acetate dihydrate was substituted for the cobalt compound. Results of the fluid bed (80cc) production of maleic anhydride from n-butane using the catalyst of Example 8 are listed in Table I. Examples 9-20 A fluid bed catalyst having the formula V1.0P1.2Co0.20x was prepared according to the procedure set forth in Examples 1-7 above. Results of the fluid bed (440 cc) production of maleic anhydride from n-butane using the catalyst of Examples 9-20 are listed in Table II. Examples 21-27 A fluid bed catalyst having the formula V1.0P1.20x was prepared according to the following procedure. Catalyst precursor was prepared by introducing 7.276 kg V205, and 10.5 kg mixed phosphoric acid (including 1.2 kg H20) into 120 litres isobutanol with stirring, and refluxing the resulting slurry for 6 hours. The mixed phosphoric acid source contained 87% orthophosphoric acid, 11.5% pyrophosphoric acid and 1.5% triphosphoric acid based upon total weight of phosphoric acid. The slurry was cooled, the catalyst precursor recovered by filtration and dried for 3 hours at 1500 C. The dried catalyst precursor was ball milled for 5.5 hours, and 3000 g comminuted catalyst precursor was thereafter introduced into 3667g water with stirring. The resulting slurry was spray dried to yield uniform, microspheroidal catalyst particles. Results of the fluid bed (440 cc) production of maleic anhydride from n-butane using the catalyst of Examples 21-27 are listed in Table III. Examples 28-37 A fluid bed catalyst having the formula 80 wt.% V1 0 P1 0X/20 wt. 54 SiO2 was prepared according to the following procedure. 2.5 kg dry, comminuted catalyst precursor, prepared as ill Examples 21-*27 was introduced into 2.6 kg water, containing 1.8 kg Nalco 1034A silica sol (trade designation of Nalco Chemical Co.), with stirring. The resulting slurry was spray dried to yield uniform, microspheroidal catalyst particles. Results of the fluid bed (440 cc) production of maleic anhydride from n-butane using the catalyst of Examples 28-57 are listed in Table III. Examples 38-47 A fluid bed catalyst having the formula 70 wt.%. V1.0P1.2Ox/ wt. % SiO2 was prepared according to the following procedure. Catalyst precursor was prepared by introducing 7.276 kg V2O5 and 9.39 kg orthophosphoric acid (100%) in 120 litres isobutanol with stirring, and refluxing the resulting slurry for 16 hours. The scurry was cooled, the catalyst precursor recovered by filtration and dried for 2 ours at 1500C. The dried catalyst precursor was ball milled for 24 hour, s, and 884 g eomminuted catalyst precursor was introduced into 2000 g water containing 1063 g Nalco 1034A silica sol, with stirring. The resulting slurry was spray dried to yield uniform, microspheroidal catalyst particles. Results of the fluid bed (440 cc) production of maleic anhydride from n-butane using the catalyst of Examples 38-47 arc listed in Table III. As can be seen from the results listed i Table I through III, fluid bed catalysts containing the mixed oxides of vanadium and phosphorus may be prepared according to the present invention, such catalysts being useful in the productioii of maleic anhydride from 4-carbon atom hydrocarbons. The fluid bed catalysts thus prepared are uniform, mcrospheroidal, and are suitable for use as commercial fluid bed catalysts, a substantial portion of tlie mi crospheroidal particles of such catalysts having particle size. within the range of 20 microns to 100 midrons. The partiele size requirement for fluid bed catalysts, set forth above, are met by these catalysts. Catalyst precursors which have been prepared in organic media, unexpectedly retain their high activity for the production of maleic anhydride, when further treated according to the process of the present invention. TABLE I FLUID (80CC) PRODUCTION OF MALEIC ANHYDRIDE FROM n-BUTANE Example Temperature C Ratio Air/ Contact WWH No. Bath Bed Hydrocarbon Time (sec.) V1.0P1.2Co0.2Ox Catalyst 1 389 390 66.7 6.6 0.015 2 389 390 64.0 6.6 0.016 3 375 373 72.3 6.2 0.011 4 375 373 61.8 6.0 0.014 5 376 375 65.7 6.0 0.013 6 377 375 67.0 6.1 0.012 7 375 375 65.8 6.1 0.013 V1.0P1.2Co0.2Ox Catalyst 8 397 78.4 6.1 TABLE (Continued) Time on Example % Maleic Anhydride Stream No. Conveesion % Yield % Selectivity (Hrs.) V1.0P1.2Co0.2Ox Catalyst 1 92.0 58.6 63.7 66 2 76.6 48.8 63.7 165 3 93.9 64.1 68.3 72 4 86.1 58.5 68.0 139 5 89.0 58.8 66.5 166 6 79.6 50.5 63.6 265 7 81.7 52.6 64.7 310 V1.0P1.2Co0.2Ox Catalyst 8 95 52.8 55.7 TABLE II Fluid Bed (440 CC) Production of Maleic Anhydride from n-Butane using V1.0P1.2Co0.2Ox Catalyst Example Temperature C Ratio Air/ Contact WWH No. Bath Bed Hydrocarbon Time (sec.) 9 371 380 61.9 5.84 0.015 10 377 385 64.6 5.20 0.016 11 376 383 64.6 5.20 0.016 12 378 386 59.9 6.08 0.014 13 394 398 59.8 5.86 0.015 14 411 422 40.4 6.15 0.019 15 409 420 39.3 7.04 0.017 16 410 422 39.6 6.95 0.018 17 416 428 26.6 8.53 0.021 18 400 409 61.5 5.31 0.016 19 409 422 35.5 5.19 0.027 20 431 443 39.0 6.79 0.018 TABLE II (Continued) % Time on Example Conversion Maleic Anhydride Stream No. % Yield % Selectivity (Hrs.) 9 91.6 59.5 65.0 24 10 81.3 56.5 69.5 134 11 74.8 50.6 67.6 240 12 75.8 52.8 69.6 328 13 80.6 55.8 69.3 435 14 92.4 59.2 64.1 647 15 87.0 57.0 65.5 834 16 90.6 56.4 62.3 1,026 17 76.3 49.0 68.8 1,290 18 85.2 54.6 64.1 1,481 19 74.9 70.4 52.8 1,630 20 93.2 57.0 61.2 1,847 TABLE III Fluid Bed (440 CC) Production of Maleic Anhydride from n-Butane using V1.0P1.2Co0.2Ox Catalyst Example Temperature C Ratio Air/ Contact WWH No. Bath Bed Hydrocarbon Time (sec.) V1.0P1.2Co0.2Ox Catalyst 21 386 394 29.0 6.7 0.020 22 394 405 29.5 6.8 0.020 23 403 411 36.4 9.1 0.020 24 426 440 26.4 8.6 0.028 25 425 439 29.8 8.8 0.024 26 425 440 28.9 8.9 0.024 27 425 442 22.4 10.8 0.026 80% V1.0P1.2Co0.2Ox/20% SiO2 28 376 380 61.7 6.0 0.014 29 405 414 27.6 5.7 0.031 30 431 439 27.4 5.6 0.030 31 438 446 28.4 8.5 0.019 32 438 446 28.8 8.2 0.019 33 438 446 28.1 8.5 0.019 34* 438 449 28.5 10.9 0.024 35* 438 449 31.2 11.1 0.023 36* 438 451 27.0 8.9 0.031 37* 439 451 24.0 10.0 0.031 *Reactor outlet pressure 10 PSIG TABLE III (Continued) Time on Example % Maleic Anhydride Stream No. Conveesion % Yield % Selectivity (Hrs.) V1.0P1.2Co0.2Ox Catalyst 21 97.9 60.0 61.2 78 22 83.3 55.8 67.0 145 23 82.2 57.6 70.0 196 24 89.8 56.4 62.8 246 25 91.0 55.9 61.4 334 26 93.3 57.1 61.2 429 27 92.4 53.6 58.0 479 80% V1.0P1.2Co0.2Ox/20% SiO2 28 88.0 41.5 47.1 43 29 78.3 46.8 59.8 257 30 76.2 46.8 61.4 527 31 94.4 50.7 53.7 720 32 93.1 51.0 54.7 882 33 91.5 51.9 56.7 957 34* 94.6 50.9 53.8 1,074 35* 95.6 46.0 48.2 1,285 36* 86.4 48.1 55.7 1,375 37* 86.3 46.2 53.6 1,400 * Reactor outlet pressure 10 PSIG Example Temperature C Ratio Air/ Contact WWH No. Bath Bed Hydrocarbon Time (sec.) 70% V1.0P1.2Co0.2Ox/30% SiO2 38 358 367 58 7.0 0.014 39 359 369 58 7.0 0.014 40 360 368 58 7.0 0.014 41 360 375 29.7 9.1 0.021 42 371 384 28.8 9.8 0.019 43 370 382 26.8 9.8 0.020 44 382 394 27.8 9.6 0.020 45 480 393 28.7 9.8 0.019 46 480 392 27.3 8.7 0.021 47 480 388 37.6 9.4 0.014 TABLE III (Continued) Time on Example % Maleic Anhydride Stream No. Conveesion % Yield % Selectivity (Hrs.) 80% V1.0P1.2Co0.2Ox/20% SiO2 38 90.5 51.9 57.4 114 39 91.4 52.3 57.2 138 40 90.9 53.7 59.1 210 41 78.6 46.3 58.9 329 42 78.4 45.5 58.1 659 43 76.2 48.9 64.2 775 44 77.2 45.0 58.3 965 45 76.8 44.4 57.8 1,085 46 72.6 44.0 60.6 1,443 47 77.6 46.7 60.1 1,826

Claims: GLAIMS:- 1. A process for the preparation of a fluid bed oxidation catalyst containing the mixed oxides of vanadium and phosphorus, comprising: (a) preparing a catalyst precursor containing a vanadium phosphorus mixed oxide; (b) comminuting the catalyst.precursor; (c) introducing the catalyst precursor into water prior or subsequent to comminution:r thereof to form an aqueous slurry; and (d) spray drying said slurry to form microspheroidal catalyst particles. 2. A process as claimed in claim 1 characterised in that it includes an additional step of calcining the microspheroidal catalyst particles. 3. A process as claimed in claim 1 or claim 2 characterised in that the precursor is prepared in an organic liquid. 4 A process as claimed-in claim 1 or claim 2 characterised in that the catalyst precursor is prepared in an organic liquid slurry. 5. A process as claimed in any of claims 1 to 4 characterised in that the catalyst precursor is substantially dried prior to introducing it into water. 6. A process as claimed in any of claims 1 to 5 characterised in that a substantial portion of said catalyst precursor is comminuted to a particle size of less than one micron average diameter. 7. A process as claimed in any qf claims 1 to 6 characterised in that the slurry has a solids content of 25 to 60 weight percent. 8. A process as claimed in any of claims 1 to 7 characterised in that a substantial portion of the said microspheroidal particles has a particle size of less than 300 microns, preferably from 20 to 240 microns 9. A process as claimed in any of claims 1 to 8 in which the precursor additionally comprises promoter elements selected from the group consisting of U, Co, Mo, Fe, Zn, Hf, Zr and mixtures thereof. 10. A process as claimed in any of claims 1 to 9 characterised in that the catalyst precursor is introduced into the water prior to the calcining thereof. 11. A fluid bed oxidation catalyst when prepared by a process as claimed in any of claims 1 to 10. 12. A process for the production of maleic anhydride by the oxidation of 4-carbon atom hydrocarbons with molecular oxygen or an oxygen-containing gas in a fluid bed reactor at a reaction temperature of 2500C to 6000C in the presence of a microspheroidal fluidizable catalyst containing the mixed oxides of vanadium and phosphorus, wherein the catalyst used in as claimed in claim 12. 13. A process as claimed in claim 12 characterised in that the hydrocarbon is n-butane. 14. A process as claimed in claim 12 or 13 characterised in that the oxidation is effected at a reactor pressure greater than one atmosphere (0,07 kg/cmê) 15. A process as claimed in any of claims 12 to 14 characterised in that a temperature 3250C to 5000 is used.

Inventors: LEMANSKI, MICHAEL FRANCIS, MILBERGER, ERNEST CARL, SPITNALE, GREGORY GENE
Applicants: THE STANDARD OIL COMPANY
Application year: 1981
Main classification: B01J27
IPC codes: B01J27, C07C51