AN ADHESIVE CONTAINING STARCH AND A PROCESS FOR PRODUCING IT

Abstract: An adhesive, particularly for use in the making of corru­ gated cardboard, consists of starch, water and alkali in such proportions that the mixture contains 10 to 40% by weight of starch solids and has a pH value of 8 to 13, a gel point of 52 to 75°C and a Stein-Hall viscosity of 20 to 120 seconds. The starch consists of completely gelatinized starch and partly swollen starch in a weight ratio between 0.2:100 and 2:1, which results in a greatly increased gelatinization rate and thereby increased wet tack of the adhesive, and this in turn permits greater machine rates in the making of corrugated cardboard. The adhesive may be produced by first maintaining a mixture of ungelatinized starch and water at 20 to 100°C, preferably in the presence of an acid or a base, until the starch is completely gelatinized, then adding more ungelatinized starch and optionally water, adjusting pH to between 8 and 13 and maintaining the mixture at 20 to 75°C until it has reached a Stein-Hall-viscosity between 25 and 130 seconds, followed by the addition of a reaction inhibitor, preferably borax, alum, another acid material, cold water or ice, in an amount such that the gel point of the mixture will be between 52 and 75°C. The initial complete gelatinization of ungelatinized starch may optionally be replaced by an addition of completely gelatin­ ized starch powder.

Description: An Adhesive Containing Starch and a Process for It Producing It The invention relates to an adhesive consisting of starch, water and alkali in such proportions that the mixture contains between 10 and 40% by weight of starch solids and has a pH value between 8 and 13, a gel point 0 between 52 and 75 C and a Stein-Hall viscosity between 20 and 120 seconds. It also relates to a process for producing the adhesive. The adhesive is particularly suitable for use-as a paste in the making of corrugated cardboard. At present, corrugated cardboard is made in a continuous process involving several steps. A paper web, slightly wetted, is passed through heated corrugation rolls. Adhesive is applied to the crest of-each wave on one side of the heated corrugated paper. Immediately following this, a second paper web is contacted with the waves of the corrugated paper, which have been treated with adhesive, in the presence of heat and pressure, which results in the formation of a strong glue seam. This corrugated cardboard is calle.single-faced corrugated cardboard by those skilled in the art. Another type of corrugated cardboard is called doublefaced corrugated cardboard The double-faced cardboard is made by applying adhesive on the wave crests of the single- faced cardboard and subsequently applying a second paper web or substrate on the crests. The substrate may e.g. also be single-faced cardboard, and thus it is possible to make cardboard of any desired thickness. To avoid destroying the 0lngle-faced corrugated cardboard during the gluing process, less heat and pressure must be used, and thus greater requirements are made of the adhesive to be used here. It has been known for several years that adhesives containing starch may be used in the making of corrugated cardboard if at least part of the starch is ungelatinized and it is suspended in an aqueous medium. However, ungelatinized starch is not self-suspending in water as it precipitates in aqueous mixture. In contrast to this, gelatinized starch is suspended fairly readily in water, and the well-known Stein-Hall process used this fact by first gelatinizing starch in an aqueous medium and then adding ungelatinized starch which sticks to the gelatinized starch and is in this manner kept suspended in the aqueous medium. In other words, these known adhesives contain two different starch components, the gelatinized one acting as a "carrier" for the ungelatinized component. The Danish Patent No. 125 428 discloses an adhesive which only contains one starch component which is partly swelled, i.e. it is only partly gelatinized to such a small extent that practically no ruptures occur on the individual starch grains, but on the other hand, a certain loss in the double refraction of the grains may take place. This adhesive is characterized by consisting of partly swollen starch, water and alkali in such proportions that the mixture contains between 10 and 40% by weight of starch solids and has a pH value between 8 and 13, a gel point between 570 and 720C and a Stein-Hall viscosity between 20 and 90 seconds. Today, corrugated cardboard is made with these known adhesives at machine rates of up to 200 to 250 m/min, and 100 to 120 m/min in respect of heavier qualities. These high machine rates require that the adhesive, besides being viscous, has a very great wet tack. ray wet tack is understood the time that lapses from the Rpplication of the adhesive until fibre tearing occurs in the substrate applied. It is constantly desired to increase machine rates in the making of corrugated cardboard, and, in fact, machines are constructed which can process the paper at greater speeds, but in practice the wet tack obtainable with these known adhesives sets a limit to the production rate of corrugated cardboard at said speeds. According to the invention we have found that the wet tack of the adhesive depends directly upon the heat added, the pressure applied and the gelatinization rate of the adhesive. By gelatinization rate is understood the rate at which the normal viscosity of the adhesive at the temperature of application is increased to the viscosity that produces fibre tearing. As the heat and pressure applied in a given machine are constant, it is thus the gelatinization rate of the adhesive which decides its wet tack and thereby the production rate of corrugated cardboard. Contrary to the previous assumption, viz. that completely gelatinized starch practically does not contribute to the wet tack of the adhesive, it has now surprisingly been found that an adhesive with a greatly increased gelatinization rate and thereby wet tack can be obtained by adding completely gelatinized starch to said one-component-adhesive containing partly swollen starch. This is achieved with the adhesive of the invention which is of the type that contains starch, water and alkali in such proportions that the mixture contains between 10 and 40% by weight of starch solids and has a pH value between 0 8 and 13, a gel point between 52 and 75 C and a Stein- Hall viscosity between 20 and 120 seconds, and which is characterized b that the starch consists -of completely gelatinized starch and partly swollen starch in a weight ratio between 0.2:100 and 2:1. The gelatinization rate of the adhesive is measured in a standard Brabender viscosimeter and is stated in Brabender units per minute (BU/min.). It has been found that in the ordinary adhesives it is only possible to obtain gelatinization rates of up to 2000BU/min,, and by careful laboratory work of up to 2500 BU/min. As opposed to this, gelatinization rates of 2500 to 10 000 BU/min. have been achieved in the adhesive of the invention, and it is expected that approximately 15 000 BU/min. will be achieved. The adhesive of the invention may be produced by adding a powder of completely gelatinized starch to a pre-produced one-component-adhesive containing partly swollen starch, and thoroughly dispersing the powder to produce a homogenous mixture. The powder is added in such amounts as will give an overall content of starch solids of between 10 and 40% by weight and a weight ratio of completely gelatinized to partly swollen starch of between 0.2:100 and 2:1. The adhesive may be produced particularly advantageously by the pro cess of the invention which is characterized by (a) maintaining a mixture of ungelatinized starch and water containing between 0.02 and 25% by weight of starch 0 at a temperature between 20 and 100 C, optionally in the presence of an acid or a base, until the starch is completely gelatinized, (b) adding ungelatinized starch and optionally water so that the mixture contains a total of between 10 and 40K by weight -of starch solids in a weight ratio of completely gelatinized starch to ungelatinized starch of between 0.2:100 and 2: :1, adjusting pH to between 8 and 13, and maintaining the temperature of the mixture between 20 and 750C until it has reached a Stein-Hall viscosity between 25 and 130 seconds, (c) adding a reaction inhibitor in an amount such that the gel point of the mixture will be between 52 and 750C. This process offers the advantage that only one starting material is used, viz. ungelatinized starch so that it is not necessary to provide separate tanks for each component. Moreover, it ensures a completely homogenous dispersion of both components in the mixture. The second advantage is also achieved if step (a) of the process of the invention is replaced by an addition of completely gelatinized starch powder in step (b). The adhesive of the invention may be admixed in a manner known per se with a tackifier and/or preservative. Said agents may be added at any step of the process of the invention. The type of starch used in the following examples is corn starch, but wheat, potato, tapioca and similar types of starch are equally useful. Said types of starch may be unmodified or chemically modified, e.g. oxidized, acid modi- fied, enzyme modified or chemically derivatized, i.e. starch ethers and esters. The reaction inhibitor in step (c) may actually consist of any addition or change which causes the properties of the reaction mixture to differ from those required for swelling the starch. In that respect it has been found particularly effective that the.reaction inhibitor is borax, alum, another acid material, sold water or ice. In the following examples the Stein-Hall viscosity is measured in a standard Stein-Hall cup at 38 to 430C, and the viscosities found are stated in seconds. A Stein-Hall cup is a viscosimeter which measures the time it takes for 100 ml of adhesive to pass between two pins through a narrow opening. Distilled water at room temperature passes between the two pins in 15 seconds. As mentioned, the gelatinization rate is measured in a standard Brabender viscosimeter, and the gelatinization rates found are stated in BU/min. A Brabender device measures the viscosity as a function of temperature and/or time. The viscosities found do not correspond to any other forms of viscosity measurements. The base used in the examples is sodium hydroxide, but potassium hydroxide or other basic materials are equally useful. The invention will be illustrated more fully in the folvowing examples. EXAMPLE 1 A mixture of 15 g of unmodified corn starch and 160 ml of 0 water was heated to 95 C. Af-ter 10 minutes the starch was completely gelatinized, and 480 ml of cold water and 205 g of unmodified corn starch were added. This suspension was admixed with 4 g of NaOH in 40 ml of water at 25 0C. The mixture was stirred and allowed to react for 15 minutes, and then 3 g of boric acid were added, and after 15 minutes' stirring the mixture was realty, The resulting adhesive had a Stein-Hall viscosity of 50 , a gel point of 650C, a pH value of 11.9 and a gelatinization rate of 3400 BU/min. EXAMPLE 2 This example illustrates the use of a completely gelatinized corn starch powder. A mixture of 5 g of completely gelatinized corn starch and 96 g of unmodified corn starch was mixed with 310 g of wa ter at a temperature of 38 C. This suspension was admixed with 60 g of water containing 3 og of NaOH at a temperature of 540C. The mixture was stirred and allowed to react for about 15 minutes, then 2 g of boric acid were added, and the mixture was stirred for 15 minutes. The resulting adhesive had a Stein-Hall viscosity of 52 s, a gel point of 620C, and a gelatinization rate of 4200 BU/min. The obtained adhesive was used for the production of a cardboard composed of 150 g/m2 liner / 112 g/m2 fluting / 110 g/m2 testliner / 112 g/m2 fluting / 150 g/m2 liner, and the machine rate could be increased by 69% in comparison with a conventional "NO-CARRIER" adhesive 0 having a gel point of 58 C and a gelatinization rate of 1800 BU/min. EXAMPLE 3 This example illustrates the use of a preservative and a tackifier together with the completely gelatinized starch. A mixture of 73 ml of water, 0.5 g of 37% formalin, 0.5 g of boric acid and 7 g of corn starch was heated to 950C. After 10 minutes the starch was completely gelatinized, and 218 ml of cold water and 93 g of corn starch were added. This suspension was admixed with 2 g of NaOH in 160 ml of water at 25 0C. The mixture was stirred and allowed to react for 15 minutes, then 1 g of boric acid was added, and after 15 minutes' stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 60 s, a gel point of 660C, a pH value of 12 and a gelatinization rate of 3000 BU/jn. The obtained adhesive was used for the production of a cardboard composed of 175 g/m2 liner / 127 g/m2 fluting / 127 g/m2 fluting / 127 g/m2 fluting / 175 g/m2 liner, and the machine rate could be increased by 38% in comparison with a conventional 1,NO-CARRIER" adhesive having a gel point of 570C and a gelatinization rate of 1600 Bu/min. EXAMPLE 4 This example illustrates the use of completely gelatinized starch at the end of the process. A mixture of 100 g of unmodified corn starch and 310 ml of water at 400C was admixed with 2.9 g of NaOH in 60 ml-of water at 520C. The mixture was stirred and allowed to react for 30 minutes, then 1.7 g of boric acid, 0.7 g of formalin and 2.5 g of completely gelatinized corn starch were added, and after 20 minutes' stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 60 s, a gel point of 630C, a pH value of 12.2 and a gelatinization rate of 4600 BU/min. EXAMPLE 5 This example illustrates the production of an adhesive having a high gel paint. A mixture of 0.5 g of completely gelatinized corn starch and 100 g of unmodified corn starch was mixed with 310 ml of water at a temperature of 390C. This suspension was admixed with 60 g of water containing 0 2.9 g and NaOH at a temperature of 53 C. The mixture was stirred and allowed to react for 20 minutes, then 1.7 g of boric acid, 0.7 g,of formalin, 14.5 g of completely gelatinized corn starch and 5.6 g of citric acid were added, and after 30 minutes' stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 85 s, a gel point of 75 C and a gelatinization rate of 3900 BUimin. EXAMPLE 6 This example illustrates the use of a modified starch. A mixture of 15 g of greatly oxidized corn starch and 160 ml of water was heated to 95 C. After 10 minutes the starch was completely gelatinized, and 480 ml of cold water and 205 g of unmodified corn starch were added. This suspension was admixed with 4.5 g of NaOH in 40 ml of water at 25 0C. The mixture was stirred and allowed to react for .25 minutes, then 3 g of boric acid were added and after 30 minutes stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 62 s, a gel point of 620C, a pH value of 12 and a gelatinization rate of 3300 BU/min. EXAMPLE 7 This example illustrates the production of an adhesive having a low gel point. A mixture of 15 g of completely gelatinized corn starch and 160 ml of water at a temperature of 20 0C was admixed with 480 ml of water at 46 C and 205 g of unmodified corn starch. This suspension was admixed with 4.5 g of NaOH in 40 ml of water at 300C. The mixture reacted for 10 minutes, then 3 g of boric acid were added, and after 20 minutes' stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 70 s, a gel point of 55 C, a pH of 12.2 and a gelatinization rate of 2400 BU/min. EXAMPLE 8 This example illustrates the production of a mixture having a particularly high gelatinization rate. A mixture of 100 g of unmodified corn starch and 310 ml of water at 380C was admixed with 2.9 g of NaOH in-60 ml of water at 550C. The mixture was stirred and allowed to react for 20 minutes, then 1.7 g- of boric acid, 0.7 g of formalin, 5 g of completely gelatinized corn starch and 4.3 g of citric acid were added, and after 25 minutes' stirring the mixture was ready. The resulting adhesive had a Stein-Hall viscosity of 51 s, a gel point of 75or, a pH value of 11v9 and a gelatinization rate of 7100 BU/min.

Claims: Patent Claims: 1. An adhesive consisting of starch, water and alkali in such proportions that the mixture contains between 10 and 409/0 by weight of starch solids and has a pH value between 8 and 13, a gel point between 52 and 750C and a Stein-Hall viscosity between 20 and 120 seconds, c h a r a c t e r i z e d in that the -starch consists of completely gelatinized starch and partly swollen starch in a weight ratio between 0.2:100 and 2:1. 2. An adhesive according to claim 1, c h a r a c t e r i z e d in that the starch isunmodified corn starch, and that the weight ratio of completely gelatinized starch to partly swollen starch is between 0.5:100 and 1:1.. 3. A process for producing an adhesive according to claim 1 or 2, c h a r a c t e r i z e d by (a) maintaining a mixture of ungelatinized starch and was ter containing between 0.02 and 25% by weight of starch 0 at a temperature between 20 and 100 C, optionally in the presence of an acid or a base, until the starch is completely gelatinized, (b) adding ungelatinized starch and optionally water so that the mixture contains a total of between 10 and 40% by weight of starch solids in a weight ratio of completely gelatinized starch to ungelatinized starch of between 0.2:100 and 2: :1, adjusting pH to between 8 and 13 and maintaining the temperature of the mixture between 20 and 750C until it has reached a Stein-Hall viscosity between 25 and 130 seconds, (c) adding a reaction inhibitor in an amount such that the gel point of the mixture will be between 52 and 750C. 4. A process according to claim 3, c h a r a c t e r i z e d by replacing step (a) by an addition of completely gelatinized starch powder in step (b).

Inventors: JENSEN, PER OLE, KOFOED, HANS HENNING
Applicants: CPC INTERNATIONAL INC.
Application year: 1981
Main classification: C09J3
IPC codes: C09J103