ZINC-NICKEL ELECTROPLATED ARTICLE AND METHOD FOR PRODUCING THE SAME

Abstract: A method for producing a corrosion-resistant article exhibiting low hydrogen embrittlement, comprising electroplating the article with a nickel-zinc alloy. The nickel-zinc alloy is plated from an aqueous acidic plating solution containing zinc, nickel, an electrolyte in the form of a soluble ammonium salt, and a polyoxyalkylated nonionic surfactant. The bath can also contain an anionic surfactant, a buffer such as boric acid, and a brightner.

Description: ZINC-NICKEL ELECTROPLATED ARTICLE AND METHOD FOR PRODUCING THE SAME Background of the Invention ' . The present invention relates to zinc-nickel electroplated articles exhibiting corrosion resistance, including articles that, after being plated with a corrosion-resistant, zinc-nickel alloy, exhibit low hydrogen embrittlement characteristics. High-strength steels are subject to delayed, brittle failures at relatively low stresses. Such failures have been attributed to the presence of hydrogen in the steel microstructure. The hydrogen can be introduced into the microstructure by reaction with water or with an acid, or most importantly, by cathodically discharging hydrogen at the surface of the steel. Since most high- strength steels have corrosion-resistant coatings that are applied by less than 100 percent efficient electroplating techniques, hydrogen is discharged onto the steel surface along with the corrosion-resistant coating. Therefore, the quantity of hydrogen deposited at the coating steel interface must be carefully monitored and controlled. Currently, a cadmium-titanium alloy is electroplated onto high- strength steels under carefully controlled conditions. The resulting plated product is then heat treated at elevated temperatures to achieve an acceptable low hydrogen embrittlement level. It is believed that the porosity of the electroplated cadmium-titantium alloy is the key to the removal of the hydrogen during a subsequent heat treatment operation; however, the cadmium-titanium plating bath is very sensitive to contamination, which can cause embrittlement characteristics in coated high-strength steel substrates. More importantly, however, the cadmium-titanium alloy plating bath contains both cadmium and cyanide, which create disposal problems unless expensive waste treatment equipment is employed. Zinc-nickel alloys have been suggested for electroplating onto steels to render them corrosion-resistant. The plating parameters of a zinc- nickel alloy plating bath are much easier to control and maintain than a cadmium-titanium bath. Additionally, the zinc-nickel bath is cadmium and cyanide free and contains components that are relatively nontoxic compared to those in a cadmium-titanium plating bath. Most prior zinc-nickel baths have, however, been suggested only for high-speed plating. High-speed plating techniques are unsatisfactory for rack plating of larger metal parts. Although it has been suggested that a zinc-nickel bath can be plated at low and medium current densities by employing an ammonium chloride electrolyte, prior attempts at plating at low current densities have led to pitted and spongy deposits that do not provide good corrosion resistance. In addition, these prior attempts to produce a zinc-nickel corrosion-resistant coating at low current densities have led to a relatively high degree of hydrogen embrittlement in plated high-strength steel parts to which the coating has been applied. Summary of the Invention The present invention provides a method for producing a corrosion- resistant article, such as a high-strength steel, by applying a corrosion-resistant coating of a zinc-nickel alloy with electroplating techniques. A high-strength steel article coated in accordance with the present invention exhibits low hydrogen embrittlement characteristics. The hydrogen embrittlement of the article is maintained at a relatively low level by electroplating the zinc-nickel coating on the article in an aqueous acidic plating solution containing zinc and nickel ions, an electrolyte in the form of a soluble ammonium salt, and a polyoxyalkylated nonionic surfactant. These zinc-nickel alloys are preferably electroplated from a bath containing: from about 3.0 to about 75.0 grams of zinc ions selected from the group consisting of zinc chloride, zinc sulfate, zinc fluoborate, zinc acetate and mixtures thereof; from about 3.0 to about 75.0 grams of nickel ion selected from the group consisting of nickel chloride, nickel sulfate, nickel sulfamate, nickel fluoborate, nickel acetate, and mixtures thereof; from about 3.0 to about 100 grams of ammonium ion in the form of a soluble ammonium salt of hydrochloric acid, sulfurie acid, fluoboric acid, acetic acid, or mixtures thereof; and from about 0.5 to about 20 grams per liter of a nonionic polyoxyalkylated surfactant. The bath must also contain at least about 15 grams of an anion selected from the group consisting of chloride, fluoborate, and mixtures thereof. In addition, acid anϊons selected from chloride, sulfate, fluoborate, acetate, sulfamate, and mixtures thereof must be present in a molar amount at least equal to the combined molar amount of zinc, " nickel, and ammonium ions present in the bath. The bath can also contain a boric acid buffer, an anionic surfactant, and a brightener if desired. The bath can be effectively operated at a pH of from about 3.0 to about 7.0 and at a temperature ranging from about 15 C to 45 C. The potential applied across the anode and the cathode workpiece is sufficient to provide current densities of about 0.05 to about 200 amperes per square decimeter at the cathode workpiece surface, although current densities below about 12.0 amperes per square decimeter are preferred to produce low hydrogen embrittlement characteristics. The electroplating bath described above is free of cadmium ions, cyanides, and chelating agents. Yet the bath has a high cathode efficiency, and produces smooth adherent, ductile leveling and fine-grained, zinc-nickel alloy deposits over a wide range of plating conditions and cathode current density. Furthermore, an article plated with the zinc-nickel alloy exhibits lower hydrogen embrittlement and substantially greater corrosion resistance than an article coated with zinc or zinc-nickel alloys of the prior art. The process can also be utilized to provide zinc-nickel alloy deposits on other substrates, both metallic and nonmetallie, as long as the substrate is conductive. For example, the process can be employed to provide a zinc-nickel alloy deposit on a graphite- epoxy composite structure. Additionally, the bath is very stable, is easy to control, has a high conductivity, while requiring only simple waste treatment procedures. Detailed Description of the Invention A zinc-nickel alloy can be electrodeposited onto a variety of electrically conductive substrates in accordance with the present invention. For example, a zinc-nickel alloy can be electrodeposited onto a graphite-epoxy article for the purpose of making that article corrosion resistant. The zinc- nickel alloy deposited in accordance with the present invention is especially efficacious, however, when applied to high-strength steel articles. Not only is the steel article rendered corrosion resistant, it also exhibits little or no hydrogen embrittlement after the electroplating process. Accordingly, the present invention provides a viable and effective substitute for prior titanium- cadmium corrosion-resistant coatings. Prior to deposition of the zinc-nickel alloy, the article to be plated is preferably cleaned and activated for electrodeposition in accordance with the following procedure. The article to be plated is first manually solvent cleaned and vapor degreased in accordance with conventional procedures normally employed in the plating arts. After cleaning and degreasing, the article is completely dried and then cleaned with an abrasive blast. Within a relatively short period of time after the abrasive cleaning, the article is rinsed in cold water for one-half to five minutes. The part is then activated by immersing it in OMPI an acid solution for from five to 30 seconds. Within two minutes from the time the part is retrieved from the acid solution, it is rinsed with cold water for a minimum of 30 seconds up to approximately six minutes maximum. Within two minutes after the completion of the cold water rinse, the part can be immersed in the zinc-nickel plating bath as described below. The plating bath formed in accordance with the present invention is an aqueous solution containing zinc, nickel and an electrolyte in the form of a soluble ammonium salt, along with a nonionic polyoxyalkylated surfactant. The cations are placed in an aqueous solution of a solubilized oxide or salt of the cation. It is preferred, as will be discussed in more detail below, that the solution contain acid anϊons, and that at least a portion of the acid anions comprise chloride or fluoborate. The addition of a buffer such as boric acid, an anionic surfactant, and brϊghteners are optional, but preferred for the commercial plating embodiment of the present invention. The zinc cations can be provided by a variety of water-soluble zinc compounds. These compounds can include zinc oxide, which is capable of forming a zinc salt in the presence of acid anions, such as chloride ions that are normally present in an aqueous bath prepared in accordance with the present invention. The water-soluble compounds also include zinc salts such as zinc chloride, zinc sulfate, zinc fluoborate, zinc acetate and, of course, the various combinations and mixtures thereof. Concentration of the zinc salt should be sufficient to provide from about 3.0 to about 75.0 grams of zinc ion per liter of solution. Preferably, the zinc ions should be present in an amount ranging from 6.0 to 30.0 grams per liter of solution. The nickel salts can be provided from a variety of water-soluble nickel salts, including nickel chloride, nickel sulfate, nickel sulfamate, nickel fluoborate, nickel acetate, and the various mixtures and combinations thereof. The nickel salt should be present in an amount sufficient to provide from about 3.0 to about 75.0 grams of nickel ion per liter of solution. It is preferred that about 3.0 to about 30.0 grams of nickel ion per liter of solution be employed. The nickel to zinc ratio can be varied, for example from about 0.4:1 to about 4:1, while still obtaining a satisfactory coating. At low nickel/zinc ratios hydrogen embrittlement is minimized. At low ratios, hydrogen reembrittlement tends to be aggravated. For a plated coating exhibiting optimum corrosion resistance, it is preferred that the weight ratio of nickel ion to zinc ion be on the order of about 1 to 1 to about 2 to 1. The conductivity of the electroplating bath is increased by the presence of the electrolyte. The preferred electrolytes include soluble ammonium salts of hydrochloric acid, sulfurie acid, fluoboric acid, acetic acid, and the various mixtures and combinations thereof. The ammonium salt should be present in the bath in an amount sufficient to provide from about 3.0 to about 100 grams of ammonium ion per liter of solution. Most preferably, the ammonium ion is present in the weight range of from about 50.0 to about 90.0 grams per liter of solution. While any of the aforementioned ammonium salts can be employed as the electrolyte, it is most preferred that either ammonium chloride or ammonium fluoborate be employed as the salt from which the ammonium ion is derived. These salts provide relatively uniform plating results over a wider range of current densities. It is most preferred that the bath contain at least about 15.0 grams of chloride or fluoborate anions or mixtures thereof per liter of solution. It is also preferred that the acid anions, including chloride, sulfate, fluoborate, acetate, sulfamate and mixtures thereof be present in a molar amount at least equal to the combined molar amount of zinc, nickel and ammonium present in the solution. It is preferred that the acid anions be present in the range of from about 15.0 to 200 grams per liter of solution while 120 to 200 grams of acid anions per liter of solution are preferred. Of the acid anions, the chloride anion is most preferred. Consequently, the most preferred bath is one composed primarily of zinc chloride, nickel chloride, and ammonium chloride. The presence of a nonionic polyoxyalkylated surfactant in the zinc- nickel plating bath is critical to producing a corrosion-resistant, coated high- strength steel that has low hydrogen embrittlement. The presence of the nonionic polyoxyalkylated surfactant produces a zinc-nickel coating that is smooth, adherent, ductile, leveling, and fine-grained, over a wide range of plating conditions and cathode current densities. A wide variety of surface- active polyoxyalkylated compounds can be employed in accordance with the present invention as long as they are soluble in the aqueous bath. The following are representative examples of broad classes of compounds that can be employed in accordance with the present invention: alkoxylated alkyl phenols, alkoxylated alkyl naphthols, alkoxylated aliphatic monohydric alcohols, alkoxylated polyoxy- propylene glycols, alkoxylated 2,4,7,9-tetramethyl-5-decyne-4,7-diol, alkoxy¬ lated ethylene diamine, alkoxylated fatty acids, alkoxylated amides and alkoxylated esters. The polyethoxylated alkyl phenols, however, have been found to be particularly effective in producing corrosion-resistant coated substrates having a low hydrogen embrittlement in accordance with the present invention. Particular polyethoxylated alkyl phenol surfactants that are commercially available include ethoxylated nonyl phenol sold under the trade name "Tergitol NP-15" by Union Carbide Corporation and under the trade name "Igepal CO-730" by GAF Corporation. The latter surfactant contains approximately 15 repeating ethyleneoxy units in the hydrophilie portion of the molecule. Other suitable nonionic surfactants include "Igepal CO-887" from GAF Corporation and "Nentronyx 656" from Millmaster Onyx Corporation. The nonionic surfactant must be present in the bath in accordance with the present invention in an amount ranging from about 0.5 to about 20.0 grams per liter of solution. It is most preferred, however, that from about 1.0 to about 5.0 grams per liter of solution be employed. Although the presence of the nonionic polyoxyalkylated surfactant in combination with the zinc, nickel and ammonium cations, and chloride and/or fluoborate anions are required to produce a corrosion-resistant coated high- strength steel substrate in accordance with the present invention, other materials can be added to enhance desirable characteristics in the plating process as well as in the final product. For example, boric acid may be advantageously included in the bath to function as a buffer. Boric acid can be present in the range of from about 1.0 gram per liter of solution up to saturation of boric acid in the bath. An anionic surfactant is preferably added to the bath to increase the high end of the cathode current density range and to further improve the low hydrogen embrittlement characteristics of the final product. Although anionic surfactants in general tend to be insoluble in plating baths, the nonionic polyoxyalkylated surfactants function as a solubilizer for the anionic surfactants. Numerous anionic surfactants can be employed in accordance with the present invention. However, the alcohol sulfates and the alkyl aryl sulfonates are found to be particularly successful. A suitable alcohol sulfate includes the sodium lauryl sulfate commercially available from E.I. du Pont de Nemours and Company, Inc. under the trade name "Duponol ME Dry". A suitable alkyl aryl sulfonate is the sodium dodecylbenzene sulfonate available from Stepan Chemical Company under the trade name "Naceonol 90F". The anionic surfac¬ tant can be present in the bath in amounts ranging from about 0.2 to about 7.5 grams per liter of solution, although from 0.4 to 2.0 grams per liter of the anionic surfactant are preferred. It is also to be noted that the foregoing list of anionic surfactants is not intended to be exclusive. Other anionic surfactants that are soluble in the system otherwise formulated in accordance with the present invention and that do not detract from the superior results obtained by the present invention can be employed. Organic brighteners can also be employed to provide bright, specular deposits over the useful cathode current density ranges, that is, from about 0.3 to about 4.5 amperes per square decimeter. Suitable organic brighteners include the ring-halogenated aryl aldehydes and aryl olefinic ketones. Examples of the ring-halogenated aryl aldehydes include ortho- chlorobenzaldehyde, para-chlorobenzaldehyde, 2,4-dichlorobenzaldehyde, and 2,6-dichlorobenzaldehyde. An example of a suitable aryl olefinic ketone is benzylidene acetone. Other known organic brighteners such as aryl ketones, aryl aldehydes, ring-halogenated aryl ketones, heterocyclic ketones and aldehydes, as well as aryl olefinic aldehydes can be employed. The most preferred brighteners are ortho-chlorobenzaldehyde and benzylidene acetone. These brighteners can be employed in the bath in amounts ranging from about 0.02 to about 2.0 grams per liter of solution. The most preferred range includes the brighteners in amounts ranging from about 0.05 to about 1.0 gram per liter of solution. The zinc-nickel plating process can be carried out in the generally conventional pH, temperature, and current density ranges. When carried out with a preferred solution as outlined above and within the preferred operating ranges set forth below, an alloy containing, for example, from 80 to 95 percent by weight zinc with the balance being nickel is produced. This coating will provide excellent corrosion resistance as well as sufficient porosity to allow hydrogen embrittlement to be relieved. The bath can effectively be operated in a pH range of from about 3.0 to about 7.0 while a pH range from about 5.5 to about 6.5 is preferred. It is preferred that the pH of the bath be adjusted by the addition of ammonium hydroxide or hydrochloric acid as the need may be, so as to avoid the introduction of undesirable ions into the solution. The zinc-nickel alloy can be plated in accordance with the present invention over a wide variety of temperatures and current densities. The electrodeposition can occur over a broad temperature range of from about 15 C to about 45 C while the narrower range of from about 20°C to about 32°C is preferred. The cathode current densities can range from about 0.05 to about 12.0 amperes per square decimeter and still yield a satisfactory corrosion-resistant coating and article having a relatively low hydrogen embrittlement. However, current densities in the range of from 2.0 to 4.0 amperes per square decimeter are preferred. Although not necessary, a chromate or phosphate treatment of the part can follow the zinc-nickel plating step. In any event, within eight hours of completion of the plating step, the part is baked to relieve hydrogen embrittlement. Most steels except carburized steel and 440 steels can be baked at temperatures on the order of 350°F to 400 °F for a minimum of 12 hours. Carburized steels and 440 steels, however, should be baked at a lower temper¬ ature of from 250 °F to 300° F for only five to eight hours. If desired, the part can be chromate or phosphate treated subsequent to the hydrogen embrit¬ tlement bake. Examples The following examples are included to assist one of ordinary skill in making and using the invention. They are intended as representative examples of the present invention and are not intended in any way to limit the scope of this disclosure or the scope of protection granted by Letters Patent hereon. All parts and percentages referred to in the following examples are by weight unless otherwise indicated. Additionally, when the Hull cell is mentioned, testing was undertaken utilizing a conventional 267 ml Hull cell employing three amperes of current for three minutes. The bath was not agitated. The pH adjustments were made as necessary by utilizing appropriate acids or ammonium hydroxide. Example I An aqueous electroplating bath containing no surfactant was prepared containing per liter of solution, 15 grams of zinc oxide, 47.5 grams of nickel chloride ( iCl2""6 H 2 0 ^ ' ^® grams of ammonium chloride and 20 grams of boric acid. The pH of the bath was 5.7 and was maintained at a temperature of 40 °C. Only zinc was employed as an anode. A Hull cell panel was prepared with current densities up to 8.0 amperes per square decimeter. At a current density up to 1.5 amperes per square decimeter, the zinc-nickel alloy deposit was semi-bright with a blue tint, indicating a satisfactory deposit. At current densities ranging from 1.5 to 4.0 amperes per square decimeter, the deposit was pitted. The pitting, of course, is an undesir¬ able characteristic in a corrosion-resistant coating. At current densities from 4.0 to 8.0 amperes per square decimeter the deposit was grey, indi¬ cating a satisfactory deposit. However, above eight amperes per square decimeter, the deposit was dark grey and slightly spongey. Spongey deposits are undesirable. Example II The procedure of Example I was repeated, with the exception that 0.375 gram per liter of solution of anionic surfactant, "Duponol ME Dry", was added. The temperature of the bath was about 31° C. The bath was cloudy. A Hull cell panel was prepared. The panel generally appeared blotchy. At a current density up to 0.7 amperes per square decimeter, the zinc-nickel alloy deposit was cloudy. At a current density of from 0.7 to 2.0 amperes per square decimeter, the deposit was bright; however, the deposit was pitted at current density up to 1.5 amperes per square deci¬ meter. At current densities ranging from 2.0 to 9.0 amperes per square decimeter, the deposit was cloudy. Above 9.0 amperes per square decimeter, the deposit was a blue-black. Example III The procedure of Example II was again repeated, but this time adding 3.0 grams per liter of "Tergitol NP-15", a nonionic surfactant, to the plating bath. A Hull cell panel was prepared. There was no blotchy deposit on the panel. At a current density up to 6.0 amperes per square decimeter, the zinc-nickel alloy deposit was bluish bright. At current densities ranging from 6.0 to 12.0 amperes per square decimeter, the deposit was grey. Above 12.0 amperes per square decimeter, a blue-black deposit was obtained. No spongey deposit was noted. Both the coverage of the plating bath and the throwing power of the plating were better in the presence of the nonionic surfactant when compared with the baths of both Example I and Example II. Example IV An aqueous electroplating bath was prepared containing per liter of solution: 47 grams of zinc chloride; 61 grams of nickel chloride; 250 grams of ammonium chloride; 20 grams of boric acid. The pH of the bath was adjus¬ ted to 5.9 by the addition of ammonium hydroxide. The temperature of the bath was 24 °C. Notched tensile specimens manufactured and tested in accor¬ dance with ASTM F-519, Type la, were plated in the bath. Two nickel and two zinc rods having similar area were used as anodes and arranged symmetrically about the specimens. The specimens were plated at preselected current densities for preselected times. After plating, the specimens were baked for 12 hours at 190 °C. The specimens were then tested by static tensile loading at 75 percent of established notch ultimate tensile strength. The specimens were loaded continuously for at least 150 hours or until failure. The specimens that withstand the loading for more than 150 hours exhibit satisfactory low hydrogen embrittlement characteristics. Two specimens were plated at an average cathode current density of 1.0 ampere per square decimeter for 30 minutes. - One specimen failed the static tensile test 12.7 hours after loading. The other specimen passed the load¬ ing test and was removed from the test device after 167 hours. Another speci¬ men was plated at 2.0 amperes per square decimeter for 15 minutes. This spe¬ cimen also passed the loading test and was removed from the test apparatus after 167 hours; however, a fourth specimen plated at two amperes per square decimeter for 30 minutes failed 36.5 hours after loading. The plated deposit for specimens coated at both 1.0 and 2.0 amperes per square decimeter was found to contain about 85 percent zinc and 15 percent by weight nickel. Example V An aqueous electroplating bath was prepared containing per liter of solution: 17.8 grams of zinc oxide; 35.6 ml of hydrochloric acid (38 percent by weight HC1); 24 grams of nickel chloride; 220 grams of ammonium chloride; 20 grams of boric acid; approximately 8 ml of ammonium hydroxide (29 percent by weight NH„). The pH of the bath was 6.2. The temperature of the bath was 2 C. Notched tensile specimens were prepared in accordance with the standards set forth in the previous Example. Three specimens were plated at 1.5 amperes per square decimeter for 20 minutes and three specimens were plated at 3.0 amperes per square decimeter for ten minutes. The zinc-nickel deposited on the specimens was dull with heavy pitting and therefore unsatisfactory from the corrosion-resistance standpoint. All of the specimens were tested by loading them in accordance with the procedure set forth in Example IV, with the exception that the specimens were loaded for 200 hours. All specimens passed the 200-hour loading test. Example VI The procedure of Example V was repeated with the exception that the pH of the bath was adjusted to 5.8 and 2.25 grams per liter of solution of a nonionic polyoxyalkylated surfactant ("Tergitol NP-15") were added. Five notched tensile specimens were plated at 3.0 amperes per square decimeter for 7.5 minutes. The deposit was satisfactory. The fractured cross-section had a grainy look when viewed under magnification. All specimens passed the 200-hour loading test. Example VII The procedure of Example VI was repeated with the exception that 0.75 gram per liter of an anionic surfactant ("Duponol ME Dry") was also added to the bath. Three notched tensile specimens were plated at 3.0 amperes per square decimeter for 7.5 minutes. When viewed under magnification, an improvement in the ductile nature of the deposits was observed. All specimens passed a 200-hour loading test. Example VIII The procedure of Example VII was repeated with the exception that the pH of the bath was adjusted to 6.2 by the addition of ammonium hydroxide. Two notched tensile specimens were plated at 3.0 amperes per square decimeter for 7.5 minutes. The ductile appearance of the deposits was observed under magnification. All specimens passed the 200-hour loading test. Example IX An aqueous electroplating bath was prepared containing per liter of solution: 50 grams of zinc oxide; 100 ml of hydrochloric acid; 167 grams of nickel chloride; 90 grams of ammonium chloride; 20 grams of boric acid; approximately 75 ml of ammonium hydroxide. The pH of the bath was 5.9. The temperature of the bath was about 28 C. A copper wire was plated at a current density of approximately 100 amperes per square decimeter for approximately 20 seconds at a linear speed of 98 feet per minute. The deposit was dark grey and grainy. Another copper wire was plated at the same condition as before, with the exception that 2.25 grams per liter of solution of a nonionic polyoxyalkylated surfactant ("Igepal CO-730)") and 0.75 grams per liter of an anion surfactant ("Duponol ME Dry") were also added to the bath. Now the deposit was light grey and fine grained. Conclusion In summary, the zinc-nickel coating plated in accordance with the present invention not only provides excellent corrosion resistance to steel articles but also yields an end product that, when baked, has very low hydrogen embrittlement characteristics. The key to producing such a product in accord¬ ance with the present invention is the presence of the nonionic polyoxyalkylated surfactant. Although the primary use of the present invention is currently producing a corrosion-resistant coating on steel parts that results in low hydrogen embrittlement of the steel, the invention can also be employed to plate metal strips and wires, as well as other articles. Electroplating of steel parts to produce a product exhibiting low hydrogen embrittlement is generally performed at relatively low current densities. It is, however, generally desirable to plate metal strips and wires at high current densities while still producing a good corrosion-resistant coating. For example, a plating solution containing an ammonium chloride electrolyte and a nonionic surfactant can be employed to plate at current densities up to about 200 amperes per square decimeter. At such high current densities, it is preferable to agitate the solution during plating and also to increase the zinc and nickel content in the solution over that normally used at low current densities. The present invention has been described in relation to a preferred embodiment thereof and several alternatives thereto. One of ordinary skill, after reading the foregoing specification, will be able to effect various changes, ' substitutions of equivalents and other alterations without departing from the broad concepts disclosed herein. It is therefore intended that the scope of Letters Patent granted hereon be limited only by the definition contained in the appended claims and equivalents thereof.

Claims: -13- The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows: 1. A method for producing a corrosion-resistant article, said article being conductive, said method comprising: electroplating a zinc-nickel coating on said article in an aqueous, acidic plating solution containing zinc and nickel ions, an electrolyte in the form of a soluble ammonium salt, and a polyoxyalkylated nonionic surfactant. 2. The method of Claim 1 wherein said article comprises high- strength steel, said article when coated being characterized by low hydrogen embrittlement, said article being plated at a current density of from about 0.5 to about 12.0 amperes per square decimeter. 3. The method of Claim 1 wherein said zinc ion is present in the form of zinc oxide, zinc chloride, zinc sulfate, zinc fluoborate, zinc acetate and mixtures thereof; wherein said nickel is present in the form of nickel chloride, nickel sulfate, nickel sulfamate, nickel fluoborate, nickel acetate and mixtures thereof; and wherein said electrolyte is present in the form of a soluble salt of hydrochloric acid, sulfurie acid, fluoboric acid, acetic acid and mixtures thereof. 4. The method of Claim 3 wherein at least about 15 grams per liter of anion selected from chloride and fluoborate and mixtures thereof are present in said solution. 5. The method of Claim 4 wherein the acid anions selected from the group consisting of chloride, sulfate, fluoborate, acetate, sulfamate and mixtures thereof are present in molar proportions at least equal to the combined zinc, nickel and ammonium ions present in said solution. 6. The method of Claim 5 wherein said nonionic, polyoxy¬ alkylated surfactant is selected from the group consisting of alkoxylated alkyl phenols, alkoxylated alkyl naphthols, alkoxylated aliphatic monohydric alcohols, alkoxylated polyoxypropylene glycols, alkoxylated 2,4,7,9-tetramethyl-5-decyne- 4,7-diol, alkoxylated ethylene diamine, alkoxylated fatty acids, alkoxylated amides and alkoxylated esters. 7. The method of Claim 6 wherein said nonionic surfactant comprises a polyethoxylated alkyl phenol. 8. The method of Claim 6 wherein said bath is maintained at a pH in the range of from about 3.0 to about 7.0. 9. The method of Claim 8 wherein the temperature of said bath is maintained in the range of from about 15 C to about 45 C. 10. The method of Claim 9 wherein said article is the cathode, and an anode is immersed in said solution, the voltage applied between said cathode and anode being sufficient to provide a current density in the range of from 0.05 amperes per square decimeter to about 200 amperes per square 5 decimeter. 11. The method of Claim 10 wherein said zinc ion is present in an amount ranging from about 3.0 to about 75.0 grams per liter of solution. 12. The method of Claim 11 wherein said nickel ion is present in an amount ranging from about 3.0 to about 75.0 grams per liter of solution. 10 13. The method of Claim 12 wherein said ammonium ion is present in an amount ranging from about 3.0 to about 100 grams per liter of solution. 14. The method of Claim 13 wherein said acid anions are present in a molar amount at least equal to the combined molar amount of 15 nickel, zinc and ammonium ions, the sum total of said acid anions being present in said solution in the range of from about 15.0 to about 200 grams per liter. 15. The method of Claim 14 wherein said nonionic surfactant is present in an amount ranging from about 0.5 to about 20.0 grams per liter of solution. 0 16. The method of Claim 15 wherein said zinc ion is present in an amount ranging from about 6.0 to about 30.0 grams per liter of solution. 17. The method of Claim 16 wherein said nickel ion is present in an amount ranging from about 3.0 to about 30.0 grams per liter of solution. 18. The method of Claim 17 wherein said ammonium ion is 25 present in an amount ranging from about 50 to about 90 grams per liter of solution. 19. The method of Claim 18 wherein said acid anions are present in said solution in an amount ranging from about 120 to about 200 grams per liter of solution. 30 20. The method of Claim 19 wherein said nonionic surfactant is present in an amount ranging from about 1.0 to about 5.0 grams per liter of solution. 21. The method of Claim 20 wherein the ratio of nickel ion to zinc ion in said solution is about 0.4. ^ 22. The method of. Claim 1 wherein said bath further contains boric acid in an amount ranging from about 1.0 grams per liter of solution to saturation in said solution. 23. The method of Claim 1 wherein said bath further contains an anionic surfactant in an amount ranging from about 0.2 to about 7.5 grams per liter of solution. 24. The method of Claim 23 wherein said anionic surfactant comprises an alcohol sulfate, an alkyl aryl sulfonate, or mixtures thereof. 25. The method of Claim 23 wherein said anionic surfactant is present in an amount ranging from about 0.4 to about 2.0 grams per liter of solution. 26. The method of Claim 1 wherein said bath further contains a brightener in an amount ranging from about 0.02 to about 2.0 grams per liter of solution. 27. The method of Claim 26 wherein said brightener is present in said bath in an amount ranging from about 0.05 to about 1.0 grams per liter of solution. 28. The method of Claim 8 wherein said pH is maintained in the range of from about 5.5 to about 6.5. 29. The method of Claim 9 wherein said temperature is maintained in the range of from about 20 C to about 32 C. 30. The method of Claim 4 wherein said acid anion consists essentially of chloride ion. 31. The method of Claim 22 wherein said acid anion consists essentially of chloride ion. 32. The method of Claim 23 wherein said acid anion consists essentially of chloride ion. 33. The method of Claim 26 wherein said acid anion consists essentially of chloride ion. 34 ' . An article produced by the method of Claim.1, 2, 3, 4, -5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32 or 33. 35. An electroplating bath for producing a corrosion-resistant article, said article being conductive, said bath comprising: an aqueous, acidic solution containing zinc and nickel ions, an electrolyte in the form of a soluble ammonium salt, and a polyoxyalkylated nonionic surfactant. 36. The bath of Claim 35 wherein said zinc ion is present in the form of zinc oxide, zinc chloride, zinc sulfate, zinc fluoborate, zinc acetate and mixtures thereof; wherein said nickel is present in the form of nickel chloride, nickel sulfate, nickel sulfamate, nickel fluoborate, nickel acetate and mixtures - Λ EE thereof; and wherein said electrolyte is present in the form of a soluble salt of hydrochloric acid, sulfurie acid, fluoboric acid, acetic acid and mixtures thereof. 37. The bath of Claim 36 wherein at least about 15 grams per liter of anion selected from chloride and fluoborate and mixtures thereof are present in said solution. 38. The bath of Claim 37 wherein the acid anions selected from the group consisting of chloride, sulfate, fluoborate, acetate, sulfamate and mixtures thereof are present in molar proportions at least equal to the combined zinc, nickel and ammonium ions present in said solution. 39. The bath of Claim 38 wherein said nonionic, polyoxy¬ alkylated surfactant is selected from the group consisting of alkoxylated alkyl phenols, alkoxylated alkyl naphthols, alkoxylated aliphatic monohydric alcohols, alkoxylated polyoxypropylene glycols, alkoxylated 2,4,7,9-tetramethyl-5-decyne- 4,7-diol, alkoxylated ethylene diamine, alkoxylated fatty acids, alkoxylated amides and alkoxylated esters. 40. The bath of Claim 39 wherein said nonionic surfactant comprises a polyethoxylated alkyl phenol. 41. The bath of Claim 39 wherein said bath is maintained at a pH in the range of from about 3.0 to about 7.0. 42. The bath of Claim 41 wherein the temperature of said bath is maintained in the range of from about 15 C to about 45 C. 43. The bath of Claim 42 wherein said article is the cathode and an anode is immersed in said solution, the voltage applied between said cathode and anode being sufficient to provide a current density in the range of from 0.05 amperes per square decimeter to about 12.0 amperes per square decimeter. 44. The bath of Claim 43 wherein said zinc ion is present in an amount ranging from about 3.0 to about 75.0 grams per liter of solution. 45. The bath of Claim 44 wherein said nickel ion is present in an amount ranging from about 3.0 to about 75.0 grams per liter of solution. 46. The bath of Claim 45 wherein said ammonium ion is present in an amount ranging from about 3.0 to about 100 grams per liter of solution. 47. The bath of Claim 46 wherein said acid anions are present in a molar amount at least equal to the combined molar amount of nickel, zinc and ammonium ions, the sum total of said acid anions being present in said solution in the range of from about 15.0 to about 200 grams per liter. 48. The bath of Claim 47 wherein said nonionic surfactant is present in an amount ranging from about 0.5 to about 20.0 grams per liter of solution. OMPI * 49. The bath of Claim 48 wherein said zinc ion is present in an amount ranging from about 6.0 to about 30.0 grams per liter of solution. 50. The bath of Claim 49 wherein said nickel ion is present in an amount ranging from about 3.0 to about 30.0 grams per liter of solution. 51. The bath of Claim 50 wherein said ammonium ion is present in an amount ranging from about 50 to about 90 grams per liter of solution. 52. The bath of Claim 51 wherein said acid anions are present in said solution in an amount ranging from about 120 to about 200 grams per liter of solution. 53. The bath of Claim 52 wherein said nonionic surfactant is present in an amount ranging from about 1.0 to about 5.0 grams per liter of solution. 54. The bath of Claim 53 wherein the ratio of nickel ion to zinc ion in said solution is about 0.4. 55. The bath of Claim 35 wherein said bath further contains boric acid in an amount ranging from about 1.0 grams per liter of solution to saturation in said solution. 56. The bath of Claim 35 wherein said bath further contains an anionic surfactant in an amount ranging from about 0.2 to about 7.5 grams per liter of solution. 57. The bath of Claim 56 wherein said anionic surfactant comprises an alcohol sulfate, an alkyl aryl sulfonate, or mixtures thereof. 58. The bath of Claim 56 wherein said anionic surfactant is present in an amount ranging from about 0.4 to about 2.0 grams per liter of solution. 59. The bath of Claim 35 wherein said bath further contains a brightener in an amount ranging from about 0.02 to about 2.0 grams per liter of solution. 60. The bath of Claim 59 wherein said brightener is present in said bath in an amount ranging from about 0.05 to about 1.0 gram per liter of solution. 61. The bath of Claim 41 wherein said pH is maintained in the range of from about 5.5 to about 6.5. 62. The bath of Claim 42 wherein said temperature is maintained in the range of from about 20 C to about 32 C. 63. The bath of Claim 37 wherein said acid anion consists essentially of chloride ion.

Inventors: HSU GRACE FENG, HSU, GRACE, FENG
Applicants: BOEING CO, THE BOEING COMPANY
Application year: 1981
Main classification: C25D3
IPC codes: C25D3, C25D5