PROCESS FOR THE PRODUCTION OF SYNTHESIS GAS FROM METHANOL

Abstract: A process for the production of synthesis gas from methanol which process comprises contacting methanol in the vapour phase et elevated temperature with a catalyst comprising a crystalline silica modified by inclusion of cobalt in the crystal lattice in place of a proportion of the silicon atoms.

Description: PROCESS FOR THE PRODUCTION OF SYNTHESIS GAS FRQM METHANOL. The present invention relates to a process for the production of a mixture of carbon monoxide and hydrogen, hereinafter referred to as synthesis gas, by the catalysed decomposition of methanol and in particular to the use of a synthetic silica-based material as catalyst in the process. There is a growing awareness of the great potential of methanol as a starting material for chemicals production based on carbonylation and hydroformylation reactions, e.g. in acetic acid and oxo alcohol production. Many of the routes to such chemicals involve the use of synthesis gas, which can be produced by the decomposition of methanol, according to the following reaction: EMI1.1 Although in the past attention has principally been directed towards converting synthesis gas into products such as methanol, it is now envisaged that there will be a need in the near future to convert methanol into synthesis gas. This is being brought about by the many projects to manufacture methanol on a very large scale in certain favourable locations, e.g. the Middie East, followed by the transport of methanol in bulk to sites where a ready supply of synthesis gas is required for further procssing. Such a scheme is very advantageous, because methanol is a non-corrosive liquid under normal conditions and can consequentty be shipped without difficulty or danger over great distances. The"decomposition of methanol was studied in the early part of this century, principally because it was considered that the catalyst which gave the maximum decomposition into carbon monoxide and hydrogen would be particularly suitable for the synthesis of methanol from these gases under pressure. /Industrial and Engineering Chemistry 20, (7), page 694, (1928)7. Most of. these studies were of an academic nature and were mainly concerned with zinc-containing catalysts /e.g. Journal of Catalysis, 27, page 471, (1972)7. A study directed towards a process for the production of synthesis gas was reported in Industrial and Engineering Chemistry, 40, (4), page 583, (1948). In this, methanol is decomposed to carbon monoxide and hydrogen over a Filtros supported mixture of copper and nickel oxides maintained at a temperature in the range 350 to 4000C. The synthesis gas produced by this method was never more than 97% pure, the by-products being 0.2% carbon dioxide and 2% inerts, including nitrogen and gaseous hydrocarbons. A major disadvantage of this process was the high rate of carbon deposition and because of this the catalyst required frequent regenerations. More recently we found that a catalyst comprising a supported metal Group VIII of the Periodic Table either alone or in combination with one or more other metals from Groups I to VIII of the Periodic Table1 particularly a mixture of rhodium and copper supported on silica, carl produce synthesis gas in high yield and selectivity. Such a press is described and claimed in the complete specification of our UK Patent No: 1577069 (BP.Case No: 4430) Another catalyst found by us to be effective in decomposing methanol to synthesis gs is the amorphous aluminpsilicate produced by reacting together a source of silica, a source of alumina, a source of alkali metal, water and a polyamine other than a diamine. Such a process is described in our copending published European application No: 79302108.0 (BP Case No: 4663). UK Patent Application No: 2024790A describes a silica-based material comprising crystalline silica which has been modified with one or more elements which have entered the crystalline lattice of the silica in place of silicon atoms of the silica or in the form of salts of bisilicic or polysilicic acids. As elements which can be used for obtaining the modified silicas it is reported that chromium, beryllium, titanium, vanadium, manganese, iron, cobalt, zinc, zirconium, rhodium, silver, tin, antimony and boron are preferred. The silica-based synthetic materials are said to be useful as catalysts for a large number of reactions, including the conversion of dimethyl ether and/or methanol or other lower alcohols into hydrocarbons such as olefins and aromatic hydrocarbons. We have now found that crystalline silica modified by inclusion of cobalt in the crystal lattice in place of a proportion of the silicon atoms is an active catalyst for the decomposition of methanol to synthesis gas. Accordingly the present invention provides a process for the production of synthesis gas from methanol which process comprises contacting methanol in the vapour phase at elevated temperature with a catalyst comprising a crystalline silica modified by inclusion of cobalt in the crystal lattice in place of a proportion of tne silicon atoms. Methanol is available commercially on a very large scale and using the process of the invention it can be readily converted into a stream of synthesis gas for further down-stream processing. The methanol may be arihydrous or it may contain water up to, for example, 90% w/w. Alternatively water may be introduced as a separate feed in the form of steam. Furthermore the methanol may be diluted with carbon monoxide, carbon dioxide or recycled synthesis gas. Since the decomposition of methanol is endothermic the use of diluents offers a convenient method for introducing heat into the reaction. With regard to the catalyst, modified crystalline silicas are characterised by the presence of a single crystalline phase, and an atomic ratio of cobalt to silicon in the range from 1:5 to 1:500. The modified crystalline silica may be prepared by mixing in a liquid medium comprising water, an alcohol or a mixture thereof, a source of silicon, a source of cobalt, a nitrogeneous base and optionally, a mineralisitly agent and/or an inorganic base, maintaining the mixture under such conditions of temperature and pressure and for a time sufficient to effect crystallisation of the modified crystalline silica, separating the modified crystalline silica product from the liquid medium and thereafter calcining the product. Suitable sources of silica include, for example, sodium silicate, silica hydrosol, silica gel, silica sol and silicic acid. The preferred source of silica is an aqueous colloidal dispersion of silica particles. A suitable commercially available source of silica is LUDOX Colloidal Silica marketed by Du Pont (LUDOX is a Registered Trade Mark). Suitable sources of cobalt include the oxide, hydroxide, salts such as the nitrate and alkoxy derivatives such as the acetate. Suitable sources of nitrogenous base include amines and substituted Imines such as the alkanolamines. A preferred nitrogenous base is a quaternary ammonium compound, which may be a tetraalkylammonium compound in which the alkyl group contains from 1 to 5 carbon atoms or a tetraarylammonium compound in which the aryl group is a phenyl or an alkylphenyl group. Suitable mineralising agents include alkali metal and alkaline earth metal hydroxides and halides, for example LiOH, NaOH, Ca(OH)2, KBr, NaBr, NaI, CaI21 CaBr2, NaN03 and KNO 3. Suitable inorganic bases include alkali metal and alkaline earth metal hydroxides, for example NaOH, KOH and Ca(OH)2, and ammonia. The amount of nitrogenous base and/or inorganic base employed may suitably he lower than the toichiometric amount relative to silica and is preferably from 0.05 to 0.50 mole % per mole of silica. The mixture may suitably be maintained at a temperature of from 100 to 220, preferably from 100 to 2000C for a period of from a few hours to several days, preferably for about 7 days. The mixture is preferably maintained at the required temperature in a closed vessel such ets an autoclave under autogenous pressure. The modified crystalline silica may suitably be separated from the liquid medium after cooling by filtration. After separation the silica is preferably washed to remove any exchangeable cationic impurities, preferably with boiling distilled water having dissolved therein an. ammonium salt such as the nitrate or acetate. Calcination of the modified crystalline silica may be effected by heating in air at a temperature in the range from 300 to 7000C, preferably at about 5500C for a period of from 2 to 24 hours. With regard to the process for the production of synthesis gas the methanol may suitably be contacted with the modified crystalline silica catalyst at a temperature in the range from 200 to 600, preferably from 300 to 4500C, and at a pressure up to 10 atmospheres. Since the decomposition of methanol is equilibrium limited it is preferred to employ high temperatures in combination with low pressures. The process may be operated batchwise or continuously, continuous operation being preferred. The contact time, as hereinafter defined, for continuous operation may be up to 30 seconds, preferably from 1 to 5 seconds. For the purpose of this specification the contact time is defined as follows: Volume of catalyst in millilitres Total volume of gas (in millilitres/second at NTP) The catalyst may be used either as a fixed bed or as a fluidised bed. The decomposition of methanol produces 2 volumes of hydrogen for every volume of carbon monoxide. This ratio can be altered if so desired by treating the hydrogen/carbon monoxide mixture in a manner well-known to those skilled in the art i.e. by the so-called "shift reaction". The catalytic activity of the modified crystalline silica catalyst may be further enhanced by the addition of a metal of Group VIII of the Periodic Table either alone or in combination with one or more other metals of Groups I to VIII of the Periodic Table. The Periodic Table referred to is that contained in the Handbook of Chemistry and Physics, 44th Edition, published by the Chemical Rubber Publishing Company. Group VIII metals which are particuldrly effective include, for example, rhodium and cobalt, both alone and in combination with other metals. The Group VIII metal may be admixed with one or more other Group VIII metals and/or with metals of Groups I to VII of the Periodic Table, such as iron, copper, cranium, gold and zinc. A particularly preferred combination is a mixture of rhodium and copper. The metal or metals may be added by any of the known-techniques. Preferably the metal or metals are added by impregnating the modified crystalline silica with a solution of a compound of the metal or metals in a suitable solvent, such as water, and thereafter removing the solvent. The catalyst may suitably contain from 0.1 to 20%, preferably frown 0.2 to 10%, by weight of the metal or metals. It will be apFreciated that although the metal may be added in the form of a compound of the metal, under the conditions pertaining during the methanol decomposition process such compounds may well be chemically reduced. Alternatively or in addition the modified crystalline silica may be mixed with other materials such as the amorphous alumino- silicate described in our published copending European application No: 79302108.0 (Case 46632 or dispersed on a supporting body such as clays, silica, alumina and silica/alumina. The mixtures of hydrogen and carbon monoxide produced by the process of the present invention may be used in a variety of chemical reactions, including carbonylation, hydrocarbonylation and chemical reduction. The invention will now be particularly described by reference to the following Examples. In the Examples reference will be made to the molar yield of a particular product which is defined as: - Moles of methanol converted to a particular product x 100 Moles of methanol fed Example 1 Preparation of Catalyst Sodium nitrate (0.35 g) was dissolved in aqueous tetrapropyl ammonium hydroxide solution (22.9g, 20% wt/wt) and then cobalt nitrate hexahydrate (2.9 g) was added. A blue solid was formed. Ludox sili:a -sol, Type AS40 (21.89, containing 406 silica) was added witll vigorous stirring at room temperature and the suspension was allowed to stand for two hours. The mixture was placed in a pressure vessel which was rotated and heated at 1500C for 24 hours and then at 1700C for 60 hours. At this point the mixture was cooled to room temperature, filtered and the solid washed by heating with a 1 molar ammonium chloride solution (150 ml). This operation was repeated twice. Finally the solid was washed with deionised water (300 ml), dried at 1200C for. 16 hours and broken down to form 8 - 16 mesh granules. Analysis of the solid showed Si 40.5 and Co 6.06X wt/wt. Use of catalyst in a process for the production of synthesis gas from methanol. A gaseous feed of methanol was passed over the catalyst contain in a glass reactor at 4000C and 3.9 second contact time. The molar yields of carbon monoxide and carbon dioxide, based on the total methanol fed were 83 and o.n respectively and 16% of the methanol was recovered unchanged. The hydrogen to carbon monoxide ratio of the synthesis gas obtained was 2:1. Carbon monoxide and carbon dioxide were analysed by gas chromatography using a thermal conductivity detector and hydrogen was determined by difference. Example 2 Preparation of Catalyst The following solutions were prepared: Solution A Cobalt nitrate hexahydrate 1.45g Tetrapropylammonium hydroxide (20%) 22.9 g Sodium nitrate 0.85g Deionised water 22.8 g Solution B Ludox silica sol, AS40 21.8 g Solution A was added slowly to solution B and stirred for 10 mins. The mixture was transferred to a round bottomed flask and heated under reflux for 7.days with rapid stirring. At this point the mixture was cooled to room-temperature, filtered and the filter-cake washed with deionised water (300ml). The solid product was dried at 1200C and calcined by heating in air at 5000C for 16 hours. X-ray diffraction (XRD) analysis of the solid showed it to be crystalline and the XRD pattern is given in the Table. The X-ray diffraction data was measured by standard techniques. The radiation was the K-alpha doublet -of copper. Use of catalyst in a process for the production of synthesis gas. The catalyst was tested as described in Example 1 and converted methanol selectively into a mixture of carbon monoxide and hydrogen (synthesis gas). Example 3 Preparation of Catalyst Example 1 was repeated but the following reactants were used: Cobalt nitrate hexahydrate 3.26 g Tetrapropylammonium hydroixde (20%) 39. 78 g Sodium nitrate 3.33 g Deionised water 9.21 g Ludox silica sol, AS40 21.8 g X-ray diffraction analysis of the product showed it to be a crystalline material with an XRD pattern similar to that shown in the Table. Use of catalyst in a process for the production of synthesis gas. The catalyst was tested as described in Example 1 and converted methanol selectively into a mixture of carbon monoxide and hydrogen (synthesis gas). TABLE X-ray Diffraction Pattern of Cobalt Silicate INTER RELATIVE TWO PLANAR INTENSITIES THETA SPACING I/I (A ) O 7.879 11.221 100 8.750 10.106 9.038 9.784 16 13.í75 6.720 6 13.886 6.378 8 14.457 6.127 2 14.717 6.019 11 14.922 5.937 3 15.446 5.737 5 15.839 5.595 7 16.423 5.398 2 16.566 5.351 2 17.571 5.047 3 17.771 4.991 4 19.190 4.625 3 20.318 4.371 4 20.802 4.270 5 21.740 4.088 2 22.111 4.020 3 23.005 3.866 38 23.291 3.819 18 23.624 3.766 12 23.889 3.725 21 24.269 3.667 7 24.504 3.633 7 25.453 3.499 2 25.757 3.459 4 25.921 3.437 3 26.147 3.408 2 26.496 3.364 3 26.806 3.326 4 26.949 3.309 5 27.324 3.264 2 29.113 3.067 3 29.365 3.042 2 29.833 2.995 8 30.169 2.962 4

Claims: Claims: 1. A process for the production of synthesis gas from methanol which process comprises contacting methanol in the vapour phase at elevated temperature with a catalyst comprising a crystalline silica modified by inclusion of cobalt in the crystal lattice in place of a proportion of the silicon atoms. 2. A process according to claim 1 wherein the atomic ratio of cobalt to silicon in the modified crystalline silica is in the range from 1:5 to 1:500. 3. A process according to either claim 1 or claim 2 wherein the modified crystalline silica is prepared by mixing in a liquid medium comprising water, an alcohol or a mixture thereof, a source of silicon, a source of cobalt, a nitrogenous base and, optionally a mineralising agent and/or an inorganic base, maintaining the mixture under such conditions of temperature and pressure and for a time sufficient to effect crystallisation of the modified crystalline silica, separating the modified crystalline silica product from the liquid medium and thereafter calcining the product. 4. A process according to claim 3 wherein the nitrogenous base is an alkanolamine. 5. A process according to claim 3 wherein the nitrogenous base is a tetraalkylammonium compound in which the alkyl group contains from 1 to 5 carbon atoms. 6. A process according to claim 3 wherein the nitrogenous base is a tetraarylammonium compound in which the aryl group is a phenyl or an alkylphenyl group. 7. A process according to any one of the preceding claims wherein to the modified crystalline silica catalyst is added a metal of Group VIII of the Periodic Table either alone or in combination with one or more other metals of Groups I to VIII of the Periodic Table. 8. A process according to claim 7 wherein there is added a mixture of rhodium and copper. 9. A process according to any one of the preceding claims wherein the methanol is contacted with the catalyst at a temperature in the range from 200 to 6000C, 10. A process according to claim 9 wherein the temperature is in the range from 300 to 450 C.

Inventors: BALL, WILLIAM JOHN, STEWART, DAVID GORDON
Applicants: THE BRITISH PETROLEUM COMPANY P.L.C.
Application year: 1981
Main classification: C01B3
IPC codes: C01B3, B01J23, B01J29