LIQUID CRYSTAL MIXTURE

Abstract: 1. Liquid crystal mixture possessing a net positive dielectric anisotropy consisting essentially of an at most weakly polar (DKA =< 3) anisotropic and non-cyano component (A) and a strongly polar (DKA >= 4) anisotropic cyano component (B), whereby, a) the non-cyano component (A) consists of one to five compounds of formula (1) see diagramm : EP0056501,P33,F1 wherein R**1 and R**2 are the same or different and are groups of the formulae CH3 (CH2 )n -, CH3 (CH2 )n-1 NH-, CH3 (CH2 )n-2 see diagramm : EP0056501,P33,F2 CH3 (CH2 )n-2 see diagramm : EP0056501,P33,F3 or CH3 (CH2 )n-1 -O- wherein n is an integer between 0 and 11, A**1 , A**2 and A**3 each represent a ring of formula (1a) to (1g), see diagramm : EP0056501,P33,F4 see diagramm : EP0056501,P33,F5 see diagramm : EP0056501,P33,F6 see diagramm : EP0056501,P33,F7 see diagramm : EP0056501,P33,F8 see diagramm : EP0056501,P33,F9 see diagramm : EP0056501,P33,F10 m is zero, one or two, and Z**1 and Z**2 are the same or different and represent covalent bonds, methyleneoxy (-CH2 O-), ethylene (-CH2 -CH2 -) or carboxyl groups see diagramm : EP0056501,P33,F11 with the provision that Z**1 and Z**2 cannot both be carboxyl groups at the same time, b) the cyano component (B) consists of one to five compounds of formula (2) see diagramm : EP0056501,P34,F1 in which R**3 is a group of formulae CH3 (CH2 )r -, CH3 (CH2 )r-1 NH-, CH3 (CH2 )r-2 see diagramm : EP0056501,P34,F2 CH3 (CH2 )r-2 see diagramm : EP0056501,P34,F3 or CH3 (CH2 )r-1 -O-, wherein r is an integer from 0 to 11, p is zero or one, Z**3 and Z**4 have the meaning given above for Z**1 and Z**2 and A**4 , A**5 and A**6 are rings of formulae (1a), (1b), (1c), (1d), (1e), (1f) or (1g) with the proviso that Z**3 and Z**4 are not both carboxyl groups and that Z**3 is not the carboxyl group when p is zero and A**4 is a ring of formula (1b), c) the non-cyano component (A) forms 50 to 95 mole of the mixture of (A) and (B) and d) either the non-cyano component (A) consists solely of compounds of formula (1) wherein in one of the groups R**1 , R**2 n =< 2, or the cyano component (B) consists solely of compounds of formula (2) wherein in the group R**3 r =< 2.

Description: Fluessigkristallmischung Die Erfindung betrifft Fluessigkristall-(FK)-Mischungen zum Betrieb von Drehzellen, d. h. FK-Anzeigen mit verdrillter nematischer Phase und mit positiver dielektrischer Anisotropie (im folgenden auch kurz als DKA oder A± bezeichnet) der FK-Mischung, insbesondere fuer den sogenannten Multiplexbetrieb der Drehzelle. Bekannte FK-Mischungen dieser Art fuer Multiplexbetrieb sind z. B. in den DE-OS 28 54 310 und 29 34 918 beschrieben, wo auch die wesentlichen Parameter des Multiplexbetriebes dargelegt sind. Im Zusammenhang mit dem Multiplexbetrieb ist es ferner bekannt (siehe J. Nehring, III, Liqu. Cryst. Conference of Socialist Countries, 1979), dass die beispielsweise in Fig. 8 der oben genannten DE-OS 29 34 918 erlaeuterte Kontrastkennlinie (Helligkeits/Steuerspannungsdiagramm) moeglichst steil sein soll und dies dadurch erreicht werden kann, dass man den Wert des Verhaeltnisses der Elastizitaetskonstanten fuer Biegung (k33) zur Elastizitaetskon stanten fuer Spreizung (k11), d. h. den Bruch k33 , sowie k11 den Wert des Verhaeltnisses der DKA (A±) zur dielektri schen Konstanten senkrecht zur nematischen Achse (E±), d.h. ## den Bruch -, so klein wie moeglich waehlt. In der Praxis ## ist dabei der fuer ein Anzeigesystem erforderlicher Wert der DKA praktisch festgelegt, weil die meist verwendeten Stromquellen (Batterien) bzw. Bausteine (C-MOS) eine definierte Schwellenspannung erfordern. Die z. B. aus den oben genannten DE-OS bekannten FK-Mischungen fuer Multiplexbetrieb koennen allgemein als Mischungen einer schwach polaren oder unpolaren (d.h. DKA 4 3) anisotropen nitrilfreien Komponente (A) und einer stark polaren (DKA a 4) anisotropen Nitrilkomponente (B) mit folgenden Grundstrukturen aufgefasst werden: EMI2.1 in welchen die Gruppen Ra und Rb Alkyl-, Alkoxy- oder Alkylcarbonylgruppen mit 1 bis 10 C-Atomen im Alkylteil bedeuten und die Ringe Va yb und Y sechsgliedrige Ringe, wie Phenylen- oder Cyclohexylengruppen darstellen, die jeweils an ihren Parapositionen mit der Kette von (A) bzw. (B) verbunden sind. Die Verbindungen (A) bzw. (B) koennen zweikernige oder dreikernige Verbindungen sein, d. h. z ist Null oder Eins, und die Brueckenglieder Xa und Xb sind Carboxylgruppen, Azomethingruppen (-CH=N-), Kovalenzbindungen (-) oder Carbonylthio-(-C(O)S-)-Gruppen. Die hoechstens schwach polaren Verbindungen (A) besitzen im allgemeinen gegenueber den Verbindungen (B) gleicher Mo ## k33 lekuellaenge relativ kleine Werte von - und -, d.h. be ## k11 sitzen verhaeltnismaessig steile Kontrastkennlinien; wegen ihrer schwachen bzw. fehlenden Polaritaet ergeben die Verbindungen (A) aber viel zu hohe Schwellenspannungen, weswegen fuer den Multiplexbetrieb von Anzeigen mit verdrillter nematischer Phase gemaess dem oben genannten Stand der Technik Mischungen aus jeweils mindestens einer nitrilfreien Verbindung (A) mit jeweils mindestens einer Nitrilverbindung (B) verwendet werden, wobei die Nitrilverbindung(en) (B) z. B. 2 bis 50 % des Gewichtes der Mischung aus (A) und (B) bilden. Nun ist es aber aus verschiedenen Untersuchungen (siehe z. B. B. Engelen et al, Ann. Phys. 3/1978, Seiten 403-407) bekannt, dass durch das Vermischen von polaren anisotropen Verbindungen, wie es die Nitrilverbindungen sind, mit unpolaren anisotropen Verbindungen, wie es die entsprechenden nitrilfreien Verbindungen sind, im Normalfall die Bildung von smektischen Phasen in einem erheblichen bzw. ueberwiegenden Teil des Anisotropiebereiches solcher FK-Mischungen induziert wird und es versteht sich, dass derartige Mischungen fuer den Betrieb der ueblichen FK-Anzeigen nicht geeignet sind. Aufgabe der Erfindung ist es, eine FK-Mischung zum Betrieb von Drehzellen fuer Multiplexbetrieb anzugeben, die eine insgesamt positive DKA besitzt und im wesentlichen aus einer nitrilfreien Komponente und einer Nitrilkomponente besteht, wobei aber die Tendenz zur Bildung smektischer Phasen der Mischung praktisch ausgeschaltet bzw. in Richtung auf niedrige Temperaturen ausserhalb der normalen Betriebstemperatur von FK-Anzeigen verschoben wird. Diese Aufgabe wird erfindungsgemaess geloest durch eine FK-Mischung mit den in Patentanspruch 1 angegebenen Merkmalen. Die erfindungsgemaesse FK-Mischung besteht im wesentlichen, d. h. zu mindestens 90 Mol%, meist mindestens 95 Mol% und fuer viele Zwecke zu 100 Mol%, aus den beiden Komponenten (A) und (B). Vorzugsweise besteht die Mischung aus insgesamt hoechstens sechs verschiedenen Verbindungen, z. B. aus insgesamt drei bis fuenf Verbindungen. Da die erfindungsgemaess fuer die nitrilfreie Komponente (A) verwendeten Verbindungen der Formel (1) im allgemeinen tiefere Schmelz- und Klaerpunkte haben als die fuer die Komponente (B) verwendeten vergleichbaren Nitrile der Formel (2), lassen sich mit erfindungsgemaessen FK-Mischungen ausreichend breite Mesophasenbereiche erzielen, typisch mindestens ueber den Bereich von Null bis 700C, und zwar unter Vermeidung von smektischen Phasen bzw. Verschiebung solcher Phasen zu Temperaturen von unter OOC. Es wird angenommen, dass die mit erfindungsgemaessen FK Mischungen erzielbare Vermeidung von smektischen Phasen im praktisch bedeutsamen Temperaturbereich durch das Merkmal (d) von Patentanspruch 1 bedingt ist. Gemaess diesem Merkmal der erfindungsgemaessen FK-Mischung muss (I) entweder die gesamte nitrilfreie Komponente (A) ausschliesslich aus solchen Verbindungen der Formel (1) bestehen, bei welchen die eine der beiden Flügelgruppen R1, R2 eine sehr kurze Kette hat, d. h. eine solche mit hoechstens insgesamt drei Kettenatomen ist. Je nachdem, ob die kurzkettige Flügelgruppe eine Alkyl-, N-Monoalkylamino-, Alkylcarbonyloxy oder Alkoxygruppe ist, enthaelt der jeweilige Alkylteil hoechstens 3 C-Atome, wenn das kurzkettige R1 oder R2 eine n-Alkylgruppe ist, hoechstens 2 C-Atome, wenn das kurzkettige R1 oder R2 eine N-Mono-n-alkylaminogruppe oder eine n-Alkoxygruppe ist, weil dann das N- bzw. O-Atom als zusaetzliches Kettenatom wirkt, und nur 1 C-Atom, wenn das kurzkettige R1 oder R2 eine Alkylcarbonyloxygruppe oder Alkoxycarbonylgruppe ist, weil dann das Carbonyl-C-Atom und das Oxy-Sauerstoffatom als zusaetzliche Kettenatome wirken; oder muss (II) die gesamte Nitrilkomponente (B) ausschliesslich aus solchen Verbindungen der Formel (2)bestehen, bei welchen die Flügelgruppe R3 eine sehr kurze Kette hat, d. h. hoechstens drei Kettenatome enthaelt, die je nach der Bedeutung von R3 wie oben fuer R1, R 2 erlaeutert 3 C-Atome (n-Alkyl), 2 C-Atome plus ein N- oder O-Atom (N-Mono-n-alkylamino oder n-Alkoxy) oder 1 C-Atom plus 1 Carbonyl-C-Atom plus 1 Oxy-Sauerstoffatom (n-Alkylcarbonyloxy) sind. Als Beispiele fuer kurzkettige Flügelgruppen Rl, R2 bzw. R3 sind zu nennen: Methyl, Ethyl, n-Propyl, Methoxy, Ethoxy, N-Monomethylamino, N-Monoethylaminol die Acetylgruppe und die Methoxycarbonylgruppe. Fuer viele Verwendungszwecke erfindungsgemaesser FK-Mischungen wird bevorzugt, dass die nitrilfreie Komponente (A) - d. h. jede in der Mischung vorhandene Verbindung der Formel (1) aber keine Verbindung der Formel (2) - das eben erlaeuterte Kurzkettenkriterium fuer R1 oder R2 erfuellt, also n in einer der Gruppen R1, R2 4 2; dabei wird ausserdem bevorzugt, dass die andere Kette R2, R1 mindestens drei und vorzugsweise mindestens 5 Kettenatane enthält, also n fuer die andere Gruppe R2, R1 der Verbindungen (1) u 2 und vorzugsweise u 4 ist; vorzugsweise besteht die Nitrilkomponente (B) bei dieser Ausfuehrungsform der erfindungsgemaessen Mischung ausschliesslich aus solchen Verbindungen der Formel (2), bei welchen die der Nitrilgruppe entgegengesetzte Flügelgruppe mindestens drei Kettenatome und vorzugsweise mindestens fuenf Kettenatome enthaelt, d. h. n in der Gruppe R einen Wert von > e 2, vorzugsweise u 4, hat. Aber auch dann, wenn das Kurzkettenkriterium fuer die Nitrilkomponente (B) - d. h. jede in der Mischung vorhandene Verbindung der Formel (2) aber keine der Verbindungen der Formel (1) - erfuellt ist, lassen sich smektische Phasen ausschalten bzw. zu tieferen Temperaturen hin verschieben; in diesem Fall besteht die Nitrilkomponente (B) also ausschliesslich aus Verbindungen der Formel (2), bei welchen in der Gruppe R3 der Wert von r 4 2; in diesem Fall wird bevorzugt, dass die nitrilfreie Komponente (A) aus solchen Verbindungen der Formel (1) besteht, bei welchen in beiden Gruppen R1, R2 der Wert von n u 2 und vorzugsweise z 4 ist. Zum oben genannten Stand der Technik betreffend FK-Mischungen fuer Multiplexbetrieb gehoeren einige spezielle Mischungen aus nitrilfreier Komponente und Nitrilkomponente, bei welchen einzelne Verbindungen der aus mehreren Verbindungen bestehenden nitrilfreien Komponente das Kurzkettenkriterium erfuellen; aber weder gehoeren zum Stand der Technik nitrilfreie Komponenten, die ausschliesslich aus Verbindungen bestehen, die das Kurzkettenkriterium erfuellen, noch wird eine Loesung fuer das Problem der Vermeidung smektischer Phasen angegeben. Sowohl fuer die dreikernigen Verbindungen (m = 1) der Formel (1) als auch fuer die dreikernigen Verbindungen (p = 1) der Formel (2) ist es wesentlich, dass jeweils hoechstens eine Bruecke zwischen benachbarten Ringen eine Carboxylgrup pe ist, d. h. dass Z' Z1 und Z2 in Formel (1) bzw. Z3 und Z4 in Formel (2) nicht gleichzeitig Carboxyl sein duerfen, weil dies unerwuenschte Viskositaetsbeitraege zu den Mischungen aus (1) und (2) bewirken wuerde. Ferner gilt fuer die zweikernigen Verbindungen (p = Null) der Formel (2), dass Z nicht die Carboxylgruppe ist, wenn A4 den Cyclohexanring (Formel 1b) bedeutet, weil die Cyanophenylester von Cyclohexancarbonsaeuren eine vergleichsweise geringe thermische Stabilitaet haben und die bei ihrer Zersetzung entstehenden Produkte eine erhoehte Leitfaehigkeit, d. h. eine erhoehte Stromaufnahme, der Mischung verursachen. Fuer erfindungsgemaesse FK-Mischungen geeignete Verbindungen der Formeln (1) und (2) sind als solche und meist auch zur Verwendung fuer FK-Anzeigen mit den entsprechenden physikalischen Daten bekannt bzw. kommerziell erhaeltlich. Entsprechende Synthesemethoden gehoeren zum Stand der Technik, siehe z. B. DE-OS 23 44 732, 24 50 088, 24 29 093, 25 02 904, 26 36 684, 27 01 591 und 27 52 975 betreffend anisotrope Verbindungsstrukturen fuer ( ) und (B) aus Ringen der Formeln (la) und (ob), DE-OS 26 41 724 betreffend anisotrope Pyrimid-Verbindungsstrukturen fuer (A) und (B) mit Ringen der Formel (1d), D. Demus et al in Mol. Cryst. and Liqu. Cryst. 56/1979/115-121 betreffend anisotrope Tetrazin-Verbindungsstrukturen fuer (A) und (B) mit Ringen der Formel (le), H. Sorkin in Mol. Cryst and Liqu. Cryst. 56 (Letters) 279-281 betreffend anisotrope Dioxanverbindungsstrukturen fuer (A) und (B) mit Ringen der Formel - (elf) sowie G. W. Gray et al in J. Chem. Soc. 11/1980/465 betreffend anisotrope Bicyclooctan-Verbindungsstrukturen fuer (A) und (B) mit Ringen der Formel (1g). Anisotrope Pyrimidinverbindungen mit Ringen der Formel (1c) sind z.B. von A. I. Pavluchenk et al in J. Physique 40/1979, Seite 63-1, beschrieben. Wenn bestimmte, speziell gewuenschte Verbindungen der Formeln (1) und (2) nicht ohne weiteres als solche erhaeltlich sind, koennen sie nach an sich bekannten Methoden durch Modifikation aus entsprechenden erhaeltlichen Verbindungen hergestellt werden. Erfindungsgemaesse FK-Mischungen koennen nach den in der FK-Technik bekannten Methoden aus den Komponenten z. B. durch Vermischen hergestellt und in bekannter Weise in uebliche Zellen eingefuellt werden. Der weiteren Erlaeuterung der Erfindung dienen die folgenden Beispiele. Beispiel 1 Aus einer Verbindung der Formel (10) EMI9.1 und einer Verbindung der Formel (20) EMI9.2 als jeweils einzige Verbindungen der Komponenten (A) und (B) werden Testzubereitungen mit unterschiedlichen Anteilen an (A) und (B) von Null bis 100 Molg durch Vermischen hergestellt und jeweils in Testzellen eingefuellt, die Plattenabstaende von 40 m bzw. 9,3 m haben. In den Testzellen von 40 m werden nach den ueblichen Messverfahren die je ## weiligen Werte des Verhaeltnisses - bzw. des Verhaeltnis- k33 ses - untersucht. Die Messtemperatur betraegt stets 0,95 k11 des Kelvinwertes der Klaertemperatur. Die Zusammensetzungen der Mischung in der Zelle und die Testergebnisse sind in der folgenden Tabelle I zusammengestellt. TABELLE I Zubereitungs-Nr. 1-1 1-2 1-3 1-4 1-5 1-6 Verbindung (10) 0 20 40 60 80 100 (Mol%) Verbindung (20) 100 80 60 40 20 0 (Mol%) 2,07 1,86 1,56 1,16 0,66 0 kr33 1,16 1,02 0,98 1,03 1,17 1,41 k11 Die Mischungen 1-2, 1-3, 1-4 und 1-5 zeigten bis hinunter zu Temperaturen von -200C keine smektischen Phasen. Die Ver und haeltniswerte fuer - und - veraendern sich mit den Mi ## k11 schungsanteilen der Komponenten (A) und (B) ausgesprochen nicht-linear und die im erfindungsgemaessen Bereich von 50 bis 95 Mol% (A) liegenden Mischungen 1-4 und 1-5 sind fuer Multiplexbetrieb gut geeignet, weil beide Verhaeltniswerte minimalisiert sind und die Mischungen daher steile Xennlinien bieten. Dabei versteht sich, dass die Testzubereitungen 1-4 bzw. 1-5 z. B. bezueglich Arbeitsbereich (Breite der Temperatur der Mesophase) noch nicht optimiert sind und in erster Linie den fuer erfindungsgemaesse FK-Mischungen charakteristischen Befund zeigen sollen, dass sich Mischungen aus polarer Nitrilkomponente (B) und nicht-polarer oder hoechstens schwach polarer nitrilfreier Komponente (A) bilden lassen, die sich fuer Multiplexbetrieb gut eignen und dennoch praktisch keine Tendenz zur Bildung von smektischen Phasen haben. Beispiel 2 Nach der Arbeitsweise von Beispiel 1 wurden aus der Verbindung der Formel (12) EMI11.1 und der Verbindung der Formel (22) EMI11.2 als jeweils einzige Verbindungen der Komponenten (A) und (B) Testzubereitungen hergestellt und untersucht; die Zusammensetzungen und Kennwerte sind in der folgenden Tabelle II zusammengestellt. TABELLE II Zubereitungs-Nr. 2-1 2-2 2-3 2-4 2-5 2-6 Verbindung (12) 0 20 40 60 80 100 (Mol%) Verbindung (22) 100 80 60 40 20 0 (Mol%) ## - 1,92 1,52 1,19 0,90 0,50 -0,09 ## k33 2@02 1@55 1@33 1@20 1@11 1@05 k,1 Die Mischungen 2-2, 2-3, 2-4 und 2-5 zeigten bis hinunter- zu Temperaturen von -200C keine smektischen Phasen. Die Mischungen 2-4 und 2-5 liegen im erfindungsgemaessen Zusammensetzungsbereich und eignen sich fuer Multiplexbetrieb. Im folgenden werden Beispiele fuer erfindungsgemaesse FK-Mischungen mit Angaben der Schmelzpunkte (TF) bzw. der Klaerpunkte (Tc) angegeben. Beispiele 3-113 Aus den in den folgenden Tabellen III und IV angegebenen Verbindungen wurden erfindungsgemaesse FK-Mischungen aus einer nitrilfreien Komponente (A) und einer Nitrilkomponente (B) hergestellt. Dabei besteht die Komponente (A) ausschliesslich aus solchen Verbindungen der Formel (1), bei welchen eine der Gruppen R1, R2 hoechstens drei Kettenatome enthaelt, das Kurzkettenkriterium also fuer die nitrilfreie Komponente (A) erfuellt ist. Die Zusammensetzungen der FK-Mischungen, die Komponentenanteile in Mol% sowie die Schmelz- und Klaerpunkte TF und TC sind in Tabelle V angegeben. Bei keiner dieser Mischungen wurden innerhalb der Temperaturspanne TF bis TC irgendwelche, den normalen Betrieb der Anzeigen stoerenden smektischen Phasen beobachtet. Alle Mischungen eignen sich fuer Multiplexbetrieb. TABELLE III Verbindungen der Formel (1) + Verb. R1 A1 1 Z' m A2 Z2 A3 R2 Nr. 141 H3C (1a) -COO- O (1a) n-C5H11 144 n-H7C3 " " " " " 156 H3CO- " " " " " 158 H5C2O- " " " " " 162 n-H7C3 (1b) " " " " 173 " " " " " -O-n-C4H9 179 n-H11C5 " " " " -O-CH3 193 n-H7C3 " - 1 (1a) -COO- " -n-C3H7 332 " " - 0 " -O-n-C4H9 TABELLE IV Verbindungen der Formel (2) R3 A4 Z3 P As Z4 A6 205 n-H11C5 (1a) - 0 (la) 207 n-H15C7 " - " " 218 n-H11C5 " - 1 (1a) - " 224 n-H11C5-N(H)- " - 0 " 226 n-H13C7-N(H)- " - " " 304 n-H11C5 (1b) - " " 305 n-H15C7 " - " " 310 n-H11C5 " - 1 " - " 401 " (1c) - 0 " 402 n-H15C7 " - " " 403 n-H9C4 (1a) - 1 (1c) - " + Bemerkung Die Kovalenzbindung ist durch einen einfachen Strich "-" angedeutet. TABELLE V Beispiel Mischung aus Ver- Mol% TF ( C) T@ (etc) Nr. bindung der Formel 3 0,6 76,7 144 71,05 403 15,70 193 13,25 4 1,7 77,5 144 72,99 403 16,17 310 10,84 5 2,3 77,2 144 74,01 403 16,42 218 9,57 6 2,7 65,2 144 74,72 193 14,11 310 11,18 7 4,5 65,2 144 78,02 310 11,83 218 10,15 8 -12,6 68,7 144 50,79 304 29,61 403 10,87 193 8,73 9 -11,9 68,7 144 51,73 304 30,30 403 11,09 310 6,88 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) TC (OC) Nr. bindung der Formel F 10 -11,7 69,1 144 51,96 304 30,46 403 11,14 218 6,44 11 -8,9 68,0 144 55,89 207 22,20 403 12,07 193 9,84 12 -8,2 68,0 144 56,95 207 22,93 403 12,32 310 7,81 13 -8,0 68,2 144 57,27 207 23,15 403 12,39 218 7,18 14 -8,8 71,1 144 56,03 305 22,00 403 12,10 193 9,87 15 -8,1 71,3 144 57,09 305 22,72 403 12,35 310 7,84 16 -7,9 71,5 144 57,43 305 22,94 403 12,43 218 7,20 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC (OC) Nr. bindung der Formel F 17 -8,1 67,7 144 57,13 162 20,40 403 12,36 193 10,11 18 -7,4 67,7 144 58,23 162 21,10 403 12,62 310 8,05 19 -7,1 67,9 144 58,60 162 21,33 403 12,71 218 7,37 20 -8,1 68,8 144 57,18 156 20,32 403 12,37 193 10,12 21 -7,3 68,9 144 58,29 156 21,02 403 12,64 310 8,06 22 -7,1 69,1 144 58,65 156 21,25 403 12,72 218 7,38 23 -8,6 72,7 144 56,32 179 21,58 403 12,17 193 9,93 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T ( C) TC (OC) Nr. bindung der Formel F 24 -7,9 73,0 144 57,43 179 22,24 403 12,43 310 7,90 25 -7,7 73,2 144 57,78 179 22,45 403 12,51 218 7,25 26 -8,9 74,5 144 55,91 173 22,18 403 12,07 193 9,84 27 -8,2 74,8 144 57,05 173 22,79 403 12,34 310 7,83 28 -7,9 75,1 144 57,40 173 22,98 403 12,42 218 7,20 29 -7,1 65,1 144 58,58 173 23,62 193 10,43 218 7,37 30 -6,3 65,3 144 59,82 173 24,30 310 8,34 218 7,54 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T ( C) T ( C) Nr. bindung der Formel F C 31: -5,8 69,2 144 60,63 332 15,30 403 13,19 193 10,88 32 -5,0 69,4 144 61,86 332 15,94 403 13,49 310 8,71 33 -4,7 69,4 144 62,32 332 16,19 403 13,60 218 7,89 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) Tc ( C) Nr. bindung der Formel F 34 -5,2 72,8 144 61,47 402 14,07 403 13,39 193 11,07 35 -4,4 72,6 144 62,78 402 14,63 403 13,71 310 8,88 36 -4,1 72,7 144 63,29 402 14,85 403 13,83 218 8,03 37 -3,2 89,7 144 64,76 403 14,18 193 11,81 310 9,25 -2,5 74,5 144 65,93 403 14,18 193 12,08 401 7,53 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) Tc ( C) Nr. bindung der Formel 39 -2,8 89,8 144 65,39 403 14,33 193 11,95 218 8,33 40 -1,2 77,0 144 68,01 403 14,96 193 12,55 226 4,48 41 -1,1 77,0 144 68,12 403 14,99 193 12,58 224 4,32 42 -1,0 76,1 144 68,35 403 15,04 193 12,63 158 3,98 43 -1,5 75,0 144 67,52 403 14,84 310 9,78 401 7,86 44 -1,8 90,8 144 67,03 403 14,72 310 9,68 218 8,57 -0,2 77,7 144 69,73 403 15,38 310 10,20 226 4,69 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel F 46 -0,1 77,8 144 69,84 403 15,40 310 10,22 224 4,53 47 0 76,8 144 70,07 403 15,46 310 10,27 158 4,20 48 -1,1 74,9 144 68,23 403 15,02 401 8,01 218 8,74 49 0,3 77,5 144 70,56 403 15,58 218 9,07 226 4,79 5D 0,4 77,6 144 70,67 403 15,60 218 9t09 224 4,64 51 0,5 76,6 144 70,90 403 15,66 218 9,12 158 4,32 52 -0,9 79,8 144 68,56 193 12,68 310 9,98 218 8,79 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T ( C) TC ( C) Nr. bindung der Formel F 53 0,7 65,9 144 71,30 193 13,31 310 10,51 226 4,88 54 0,8 66,0 144 71,41 193 13,33 310 10,53 224 4,73 55 1,2 65,5 144 72,19 193 13,51 218 9,31 226 4,99 56 1,3 65,6 144 72,29 193 13,54 218 9,32 224 4,85 57 2,3 66,1 144 74,12 310 11,06 218 9,59 226 5,24 58 2,4 66,1 144 74,22 310 11,08 218 9,60 224 5,11 59 -18,6 68,1 144 43,06 205 35,36 403 9,07 193 7,11 310 5,40 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF (OC) TC ( C) Nr. bindung der Formel F 60 -18,5 68,7 144 43,13 205 35,43 403 9,08 193 7,13 218 5,23 61 -17,8 66,5 144 44,05 304 24,77 305 14,56 403 9,30 193 7,32 62 -16,6 65,4 144 45,47 304 25,78 156 13,58 403 9,62 218 5,54 63 -17,8 67,5 144 43,97 304 24,71 179 14,74 403 9,28 193 7,30 64 -17,3 67,4 144 44,64 304 25,18 179 15,08 403 9,43 310 5,67 65 -17,2 68,0 144 44,73 304 25,25 179 15,13 403 9,45 218 5,44 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) TC ( C) Nr. bindung der Formel F C 66 -18,2 68,8 144 43,48 304 24,37 173 15,79 403 9,16 193 7,20 67 -17,7 68,7 144 44,15 304 24,84 173 16,11 403 9,32 310 5,58 68 -17,6 69,3 144 44,23 304 24,90 173 16,16 403 9,34 218 5,38 69 -15,7 65,2 144 46,66 304 26,62 332 8,95 403 9,90 193 7,86 70 -15,1 65,1 144 47,40 304 27,15 332 9,24 403 10,07 310 6,13 71 -15,0 65,6 144 47,53 304 27,24 332 9,30 403 10,10 218 5,83 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T ( C) TC ( C) Nr. bindung der Formel F 72 -15,5 66,9 144 46,85 304 26,76 402 8,55 403 9,94 193 7,90 73 -14,7 78,1 144 47,93 304 27,53 403 10,19 193 8,13 310 6,22 -14,1 67,9 144 48,78 304 28,14 403 10,39 193 8,31 401 4,38 75 -14,6 78,6 144 48,07 304 27,64 403 10,23 193 8,16 218 5,90 76 -13,4 69,1 144 49,63 304 28,76 403 10,59 193 8,49 226 2.53 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) TC t C) Nr. bindung der Formel F 77 -13,8 69,1 144 49,72 304 28,83 403 10,61 193 8,51 224 2,33 78 -13,2 68,6 144 49,89 304 28,95 403 10,65 193 8,54 158 1,96 79 -12,8 69,2 144 50,51 304 29,40 403 10,80 310 6,67 226 2,61 80 -12,7 69,2 144 50,61 304 29,47 403 10,82 310 6,69 224 2,41 81 -12,6 68,7 144 50,78 304 29,60 403 10,86 310 6,72 158 2,04 82 -12,6 69,6 144 50,71 304 29,55 403 10,85 218 6,27 226 2,63 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel F C 83 -12,5 69,6 144 50,81 304 29,62 403 10,87 218 6,28 224 2,43 84 -12,4 69,1 144 50,98 304 . 29,75 403 10,91 218 6,30 158 2,06 85 -13,3 70,3 144 49,85 304 28,92 193 8,53 310 6t55 218 6,15 86 -14,7 65,9 144 47,88 207 17,03 305 16,80 403 10,18 193 8,12 87 -14,7 67,1 144 47,87 207 17,03 179 16,80 403 10,18 193 8,12 88 -14,2 67,0 144 48,62 207 17,48 179 17,20 403 10,36 310 8,34 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) TC (OC) Nr. bindung der Formel F C 89 -14,1 67,5 144 48,76 207 17,57 179 17,28 403 10,39 218 6,00 90 -15,1 68,5 144 47,41 207 16,75 173 17,75 403 10,08 193 8,02 91 -14,5 68,5 144 48,16 207 17,20 173 18,13 403 10,25 310 6,26 92 -14,4 69,0 144 48,30 207 17,29 173 18,20 403 10,28 218 5,93 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) T@ (etc) Nr. bindung der Formel F .93 -12,3 66,2 144 51,14 207 19,07 402 10,04 403 10,95 193 8,81 94 -11,7 66,1 144 51,98 207 19,61 402 10,34 403 11,14 310 6,93 95 -11,5 66,5 144 52,18 207 19,74 402 10,42 403 11,19 218 6,47 .96 -11,3 78,8 144 52,58 207 19,99 403 11,28 193 9,12 310 7,03 97 -10,6 67,1 144 53,46 207 20,57 403 11,49 193 9,31 401 5,16 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) T (OC) Nr. bindung der Formel F C 98 -11,1 79,2 144 52,80 207 20,14 403 11,34 193 9,17 218 6,56 99 -9,9 68,6 144 54,49 207 21,25 403 11,73 193 9,53 226 3,00 100 -9,8 68,6 144 54,58 207 21,32 403 11,76 193 9,55 224 2,79 101 -9,7 67,9 144 5-4,76 207 21,44 403 11,80 193 9,59 158 2,42 102 -10,0 67,1 144 54,40 207 21,20 403 11,71 310 7,35 401 5,33 103 -10,4 79,4 144 53,75 207 20,76 403 11,56 310 7,24 218 6,69 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel 104 -9,2 68,6 144 55,47 207 21,92 403 11,97 310 7,55 226 3,10 105 -9,2 68,7 144 55,57 207 21,98 403 11,99 310 7,56 224 2,89 106 -9,0 68,0 144 55,75 207 22,11 403 12,03 310 7,60 158 2,52 107 -9,8 67,4 144 54,66 207 21,37 403 11,78 401 5,37 218 6,82 108 -9,0 68,9 144 55,76 207 22,11 403 12,03 218 6,97 226 3,13 1 D9 -9,0 68,9 144 55,86 207 22,18 403 12,06 218 6,98 224 2,92 TABELLE V (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) Tc ( C) Nr. bindung der Formel 110 -8,8 68,3 144 56,04 207 22,30 403 12,10 218 7,01 158 2,55 -9,7 70,1 144 54,74 207 21,43 193 9,59 310 7,42 218 6,83 112 -19,0 67,3 144 42,50 205 34,88 403 8,94 193 7,00 310 5,31 158 1,37 113 -19,0 67,9 144 42,57 205 34,94 403 8,95 193 7,01 218 5,15 158 1,37 Beispiele 114-208 Die folgenden Beispiele erlaeutern erfindungsgemaesse FK Mischungen aus nitrilfreier Komponente (A) und Nitrilkomponente (B), bei welchen das Kurzkettenkriterium fuer alle Verbindungen (2) der Komponente (B) erfuellt ist. Eine Tendenz zur Bildung smektischer Phasen war nicht 2U beobachten; alle Mischungen waren fuer Multiplexbetrieb geeignet. Die Verbindungen sind in Tabelle VI, die Mischungszusammensetzungen (in Mol%) und die Schmelz- (TF) bzw. Klaer (T)-punkte sind in Tabelle VII zusammengestellt. TABELLE VI Verbindungen der Formel (1) Verb. R1 A1 Z1 m A2 Z2 A3 R2 Nr. 148 n-H11C5 (1a) -COO- 0 (1a) n-C5H11 149 " " " " " n-C7H15 152 n-H15C7 " " " " n-C5H11 153 " " " " " n-C7H15 166 n-H11C5 (1b) " " " n-C5H11 177 n-H9C4 " " " " -O-n-C4H9 193 n-H7C3 " - 1 (1a) -COO- " n-C3H7 195 H5C2 " - " " " (1b) " 196 n-H9C4 " - " " " " " 321 n-H11C5 " - 0 " n-C5H11 Verbindungen der Formel (2) R3 A4 Z P A5 Z4 A6 201 H3C (1a) - 0 (ia) 202 H5C2 " - " " 203 n-H7C3 " - " " 301 H5C2 (1b) - " " 302 n-H7C3 " - " " + Bemerkung Die Kovalenzbindung ist durch einen einfachen Strich "-" angedeutet. TABELLE VII Beispiel Mischung aus Ver- Mol% T ( C) T ( C) Nr. bindung der Formel F C 114 4,4 80,3 177 41,46 302 35,50 196 23,05 115 4,9 75,9 177 42,01 302 36,01 195 21,98 116 7,4 79,6 177 44,98 302 38,82 193 16,19 117 9,2 78,7 177 47,30 202 26,43 196 26,27 1.18 8,3 73,8 302 39,95 166 34,40 196 25,65 119 9,0 68,3 302 40,68 166 35,30 195 24,02 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C Nr. bindung der Formel C 120 -11,5 66,1 149 49,48 302 21,16 196 14,45 195 14,92 121 -9,4 66,9 149 52,20 302 22,71 196 15,40 193 9,69 122 -7,5 66,7 149 54,84 196 16,33 195 16,47 203 12,36 123 -4,9 70,6 149 58,53 196 17,65 195 17,53 201 6,30 124 -5,2 68,0 149 58,04 196 17,47 203 13,41 193 11,08 125 -2,5 72,6 149 62,13 196 18,95 193 12,07 201 6,84 126 -5,2 65,2 149 58,08 195 17,40 203 13,43 193 11,09 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF (0C) Tc (0C) Nr. bindung der Formel 127 -2,3 69,4 149 62,36 195 18,63 193 12,13 201 6,88 128 -2,3 68,6 152 38,67 178 35,44 196 19,02 201 6,87 129 -2,2 65,4 152 38,84 178 35,60 195 18,67 201 6,90 130 -0,5 66,8 152 41,67 178 38,21 193 12,81 201 7,31 131 -7,8 65,0 152 30,78 177 29,03 302 24,00 196 16,19 132 -2,0 68,6 152 3i,29 177 34,53 196 19,23 201 6,96 133 -1,8 65,2 152 39,50 177 34,66 195 18,84 201 6,99 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC (OC) Nr. bindung der Formel 134 0,1 66,6 152 42,78 177 36,68 193 13,07 201 7,47 135 -3,8 75,5 152 36,41 302 27,37 196 18,23 195 17,99 136 -1,9 77,2 152 39,37 302 29,09 196 19,26 193 12,28 137 -1,8 73,9 152 39,59 302 29,21 195 18,87 193 12,33 138 -1,0 72,6 152 40,84 202 20,20 196 19,76 195 19,20 139 1,0 74,6 152 44,32 202 21,33 196 20,93 193 13,42 140 1,2 70,8 152 44,77 202 21,48 195 20,23 193 13,52 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel 141. 0,4 76,1 152 43,25 196 20,57 195 19,84 203 16,34 142 3,2 81,1 152 48,35 196 22,26 195 21,14 201 8,25 143 2,4 78,4 152 46,80 196 21,75 203 17,47 193 13,97 144 5,2 84,3 152 52,41 196 23,56 193 15,21 201 8,82 145 2,7 74,3 152 47,36 195 20,89 203 17,65 193 14,10 146 5,7 79,6 152 53,31 195 22,35 193 15,40 201 8,94 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% T (0C) TC (OC) Nr. bindung der Formel F C 147 -14,4 76,0 149 45,73 302 19,08 196 13,16 195 13,83 193 8,20 148 -12,5 74,4 149 48,15 202 14,58 196 13,99 195 14,53 193 8,75 149 -11,0 77,8 149 50,14 196 14,68 195 15,11 203 10,86 193 9,21 150 -11,6 76,0 152 26,00 178 23,72 302 21,04 196 14,38 195 14,86 151 -10,1 76,9 152 27,83 178 25,41 302 22,19 196 15,09 193 9,48 152 -10,2 74,7 152 27,72 178 25,30 302 22,12 195 15,41 193 9,45 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF (OC) TC ( C) Nr. bindung der Formel F C 153 -9,9 73,8 152 28,02 178 25,58 202 15,73 196 15,16 195 15,50 154 -8,3 74,7 152 30,07 178 27,47 202 16,48 196 15,93 193 10,04 155 -8,4 72,3 152 30,00 178 27,41 202 16,46 195 16,11 193 10,02 1;6 -7,1 78,0 152 31,63 178 28,92 196 16,51 203 12,52 193 10,43 157 -7,2 75,5 152 31,59 178 28,88 195 16,60 203 12,51 193 10,42 158 -12,2 76,1 152 25,34 177 25,28 302 20,62 196 14,12 195 14,64 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel F 159 -10,5 76,8 152 27,29 177 26,65 302 21,85 196 14,88 193 9,34 160 -10,6 74,8 152 27,15 177 26,55 302 21,77 195 15,23 193 9,30 161 -10,4 73,8 152 27,46 177 26,76 202 15,52 196 14,94 195 15,32 162 -8,6 74,7 152 29,67 177 28,28 202 16,34 196 15,78 193 9,94 163 -8,7 72,4 152 29,58 177 28,22 202 16,30 195 15,99 193 9,92 164 -7,3 78,0 152 31,37 177 29,42 196 16,41 203 12,43 193 10,36 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) Tc (OC) Nr. bindung der Formel F 165 -7,4 75,5 152 31,32 177 29,39 195 16,52 203 12,42 193 10,35 166 -7,0 77,5 152 31,85 301 24,40 196 16,59 195 16,67 193 10,48 167 -8,8 72,5 152 29,39 302 23,16 166 15,84 196 15,68 195 15,93 168 -7,2 73,3 152 31,53 302 24,46 166 17,13 196 16,47 193 10,40 169 -7,2 70,8 152 31,50 302 24,44 166 17,10 195 16,57 193 10,40 170 -7,6 71,0 152 30,95 302 24,11 196 16,26 195 16,40 203 12,29 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF (OC) TC ( C) Nr. bindung der Formel 171 -7,0 88,1 t52 31,75 302 24,59 196 16,55 195 16,64 193 10,46 172 -5,7 74,5 152 33,67 302 25,74 196 17,25 195 17,21 201 6,13 1.73 -5,9 71,9 152 33,36 302 25,56 196 17,14 203 13,10 193 10,85 174 -3,8 75,9 152 36,36 302 27,33 196 18,21 193 11,57 201 6,53 175 -3,8 72,9 152 36,46 302 27,39 195 18,00 193 11,60 201 6,55 176 -5,1 70,6 152 34,44 166 18,88 202 18,04 196 17,53 193 11,11 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel F 177 -3,9 73,9 152 36,24 166 19,99 196 18,17 203 14,06 193 11,55 178 -3,8 70,8 152 36,33 166 20,04 195 17,97 203 14,09 193 11,57 1.7 -4,7 86,4 152 35,09 202 18,27 196 17,76 195 17,62 193 11,27 180 -3,1 71,7 152 37,41 202 19,06 196 18,58 195 18,27 201 6,69 181 -1,2 73,3 152 40,54 202 20,10 196 19,66 193 12,55 201 7,14 182 -3,3 90,3 152 37,17 196 18,49 195 18,20 203 14,36 193 11,77 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel 183 -1,8 75,0 152 39t61 196 19,34 195 18,87 203 15,16 201 7,01 184 0,1 77,0 152 42,82 196 20,43 203 16,20 193 13,08 201 7,47 185 0t4 73,2 152 43,18 195 19t82 203 16.32 193 13,16 201 7,52 186 -12,2 76,3 153 27,61 178 23,07 302 20,60 196 14,10 195 14,63 187, -10,6 77,2 153 29,34 178 24,77 302 21,76 196 14,82 193 9,30 188 -10,8 75,2 153 29,21 178 24,65 302 21,68 195 15,18 193 9,27 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% T ( C) TC ( C) Nr. bindung der Formel F 0 189 -10,5 74,2 152 29,47 178 24,91 202 15,46 196 14,88 195 15,27 190 -8,8 75,2 153 31,39 178 26,83 202 16,23 196 15,67 193 9,87 191 -8,9 73,0 153 31,31 178 26,75 202 16.20 195 15,90 193 9,85 192 -7,6 78,7 153 32,86 178 28,31 196 16,27 203 12,30 193 10,27 .193 -7,7 76,2 153 32,81 178 28,26 195 16,40 203 12,28 193 10,25 94 -12,9 76,3 153 26,93 177 24,73 302 20,14 196 13,82 195 14,39 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) TC ( C) Nr. bindung der Formel 195 -11,2 77,2 153 28,77 177 26,12 302 21,38 196 14,59 193 9,15 196 -11,3 75,1 153 28,62 177 26,01 302 21,28 195 14,98 193 9,11 197 -11,1 74,2 153 28,88 177 26,21 202 15,22 196 14,63 195 15,07 198 -9,2 75,2 153 30,95 177 27,76 202 16,05 196 15,49 193 9,75 199 -9,3 73,0 153 30,85 177 27,68 202 16,01 195 15,74 193 9,72 200 -7,9 78,7 153 32,55 177 28,94 196 16,14 203 12,19 193 10,18 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% T (OC) T ( C) Nr. bindung der Formel F C 201 -7,9 76,2 153 32,49 177 28,89 195 15,29 203 12,16 193 10,17 202 -7,5 78,2 153 32,99 301 23,93 196 16,32 195 16,46 193 10,30 203 -9,4 73,1 153 30,75 302 22,72 166 15,42 196 15,41 195 15,71 204 -7,7 74,0 153 32,76 302 24,06 166 16,72 196 16,22 193 10,24 205 -7,7 71,6 153 32,70 302 24,02 166 16,69 195 16,36 193 10,23 206 -8,2 71,8 153 32,15 302 23,65 196 15,98 195 16,18 203 12,04 TABELLE VII (Forts.) Beispiel Mischung aus Ver- Mol% TF ( C) Tc ( C) Nr. bindung der Formel 201 -7,6 88,6 153 32,89 302 24,14 196 16,28 195 16,42 193 10,27 208 -6,2 75,4 153 34,66 302 25,32 196 16,99 195 17,00 201 6,03 Die erfindungsgemaessen FK-Mischungen eignen sich insbesondere fuer die ueblichen Drehzellen. Sie koennen ferner mit Vorteil auch fuer FK-Anzeigen verwendet werden, die nach dem sogenannten Guest/Host-Prinzip arbeiten und eine Farbstoffkomponente als "Guest"-Anteil in einer nematischen "Host"-Phase und gegebenenfalls eine optisch aktive (chole- sterische) Komponente enthalten. Erfindungsgemaesse FK-Mischungen fuer diese Zwecke enthalten zusaetzlich zu der Mischung aus der nitrilfreien Komponente (A) und der Nitrilkomponente (B) ausserdem die Farbstoffkomponente und gegebenenfalls die cholesterische Komponente als restlichen Anteil von bis zu etwa 10 Mol%. Geeignete dichroitische Farbstoffe bzw. Farbstoffmischungen und cholesterische Komponenten sind in der Literatur, z. B. den DE-OS 2 627 215 und 2 658 568, beschrieben und technisch erhaeltlich.

Claims: Patentansprueche 1. Fluessigkristallmischung mit einer insgesamt positiven DK-Anisotropie, bestehend im wesentlichen aus einer hoechstens schwach polaren (DKA 3), anisotropen und nitrilfreien Xomponente (A) und einer stark polaren (DKA a 4) anisotropen Nitrilkomponente (B), dadurch ge kennzeichnet, dass (a) die nitrilfreie Komponente (A) aus 1 bis 5 Verbin dungen der Formel (1) EMI52.1 in der R1, R2 jeweils gleich oder verschieden und Gruppen der Formeln CH3 (CH2)n-, CH3(CH2)n¯1NH-, EMI52.2 sind, worin n eine Zahl von Null bis 11 ist, A1, A' und A3 jeweils einen Ring der Formeln (la) bis (Ig) EMI52.3 darstellen, m Null, Eins oder Zwei ist und Z1 1 und Z2 gleich oder verschieden sind und Kovalenzbindungen, die Methylenoxy- (-CH2O-), Ethylen- (-CH2-CH2-) oder Carboxylgruppen EMI53.1 mit der Massgabe darstellen, dass Z1 und Z2 nicht beide die Carboxylgruppe bedeuten, (b) die Nitrilkomponente (B) aus 1 bis 5 Verbindungen der Formel (2) EMI53.2 in der R3 eine Gruppe der Formeln CH3 (CH2)r-, CH3(CH2) r-1 NH-, EMI53.3 oder CH3(CH2)r 1-O- ist, worin r eine Zahl von Null bis Elf darstellt, p Null oder Eins ist, Z und Z4 die oben fuer 1 und Z2 genannte Bedeutung haben und A4, A5 und A6 Ringe der Formeln (1a), (1b), (1c), (ld), (1e), (1f) oder (1g) mit der Massgabe darstellen, dass Z3 und Z4 nicht beide die Carboxylgruppe bedeuten und dass Z nicht die Carboxylgruppe ist, wenn p Null ist und A4 den'Ring der Formel (1b) bedeutet, (c) die nitrilfreie Komponente (A) 50 bis 95 Mol% der Mi schung aus (A) und (B) bildet und (d) entweder die nitrilfreie Komponente (A) ausschliess lich aus Verbindungen der Formel (1) besteht, bei wel chen in einer der Gruppen R1, R2 n d 2, oder die Ni trilkomponente (B) ausschliesslich aus Verbindungen der Formel (2) besteht, bei welchen in der Gruppe R3 r 4 2. 2. Mischung nach Patentanspruch 1, dadurch gekennzeichnet, dass sie aus hoechstens 6 Verbindungen und z. B. insgesamt aus 3 bis 5 Verbindungen besteht. 3. Mischung nach Patentanspruch 1 oder 2, dadurch gekenn zeichnet, dass die Nitrilkomponente (B) fuer sich eine positive DKA von mindestens 8 besitzt. 4. Mischung nach einem der Patentansprueche 1-3, bei wel cher die nitrilfreie Komponente (A) ausschliesslich aus Verbindungen der Formel (1) besteht, bei welcher in ei ner der Gruppen R , R2 der Wert von n s 2, dadurch ge kennzeichnet, dass in der anderen Gruppe R2, R1 n einen Wert von a 2, vorzugsweise > 4 hat. 5. Mischung nach Patentanspruch 4, dadurch gekennzeichnet, dass die Komponente (B) aus Verbindungen der Formel (2) besteht, bei welchen in der Gruppe R3 n einen Wert von u 2, vorzugsweise # 4 hat. 6. Mischung nach einem der Patentansprueche 1-3, bei wel cher die Nitrilkomponente (B) ausschliesslich aus Ver bindungen der Formel (2) besteht, bei welcher in der Gruppe R3 der Wert von r < 2, dadurch gekennzeichnet, dass die nitrilfreie Komponente (A) aus Verbindungen der Formel (1) besteht, in welchen in mindestens einer Gruppe Rr, R2 den Wert von n u 2, vorzugsweise u 4 hat. 7. Mischung nach einem der Patentansprueche 1-6, dadurch gekennzeichnet, dass sie eine Farbstoffkomponente und/ oder eine cholesterische Komponente enthaelt.

Inventors: OSMAN, MAGED A., DR., SCHAD, HANSPETER, DR.
Applicants: MERCK PATENT GESELLSCHAFT MIT BESCHRANKTER HAFTUNG
Application year: 1981
Main classification: C09K3
IPC codes: C09K19, G02F1, C07D319