SHAPE SELECTIVE REACTIONS WITH CADMIUM-MODIFIED ZEOLITE CATALYSTS

Abstract: A process for the conversion of aromatic compounds to dialkylbenzene compounds rich in the 1,4-dialkylben­ zene isomer. The reaction is carried out in the presence of a particular type of zeolite catalyst having a silica to alumina mole ratio of at least 12 and a constraint index of about 1-12, said catalyst having been modified by treatment with one or more compounds of cadmium, and optionaily phosphorus, to deposit a minor propor­ tion of such elements on the zeolite.

Description: SHAPE SELECTIVE REACTIONS WITH CADMIUM-MODIFIED ZEOLITE CATALYSTS BACKGROtJND OF THE INVENTION Field of the Invention The invention disclosed herein relates to the production of dialkylbenzene compounds utilizing a modified crystalline zeolite catalyst to yield a product mixture in which the 1,4-dialkylbenzene isomer is substantially in excess of its normal equilibrium concentration. Descriction of the Prior Art The disproportionation of aromatic hydrocarbons in the presence of zeolite catalysts has been described by Grandio et al. in the OIL MlD GAS JOURNAL, Vol. 69, Number 48(1971). U.S. Patents Nos. 3,126,422; 3,413,374; 3,598,878; 3,598,879 and 3,607,961 show vapor-phase disproportionation of toluene over various catalysts. In these prior art processes, the dimethylbenzene product produced has the equilibrium composition of approximately 24 percent of 1,4-, 54 percent of 1,3- and 22 percent of 1,2-isomer. Of the dimethylbenzene isomers, 1,3-dimethylbenzene is normally the least desired product, with 1,2- and 1,4-dimethylbenzene being the more useful products. 1,4-Dimethylbenzene is of particular, value being useful in the manufacture of terephthalic acid which is an intermediate in the manufacture of synthetic fibers such as "Dacron". Mixtures of dimethylbenzene isomers, either alone or in further admixture with ethylbenzene, have previously been separated by expensive superfractionation and multistage refrigeration steps. Such process, as will be realized, involves high operation costs and has a limited yield. Various modified zeolite catalysts have been developed to alkylate or disproportionate toluene with a greater or lesser degree of selectivity to 1,4-dimethylbenzene isomer. Hence, U.S. Patents 3,972,832, 4,034,053, 4,128,592 and 4,137,195 disclose particular zeolite catalysts which have been treated with compounds of phosphorus and/or magnesium. Boron-containing zeolites are shown in U.S. Patent 4,067,920 and antimony-containing zeolites in U.S. Patent 3,979,472. Similarly, U.S. Patents 3,965,208 and 4,117,026 disclose other modified zeolites useful for shape selective reactions. N4hile the above-noted prior art is considered of interest in connection with the subject matter of the present invention, the conversion process described herein, utilizing a crystalline zeolite catalyst of specified characteristics which has undergone the partcular treatment disclosed, has not, insofar as is known, been previously described. SA !ARY OF THE INVENTION In accordance with the present invention, there has now been discovered a novel process for conversion of organic compounds (e.g. , hydrocarbon compounds) in the presence of a particular type of modified zeolite catalyst. An especially advantageous element of the invention comprises the selective production of the 1,4-isomer of dialkylated benzene compounds. The process involves contacting an alkylated aromatic compound, either alone or in admixture with a suitable alkylating agent such as methanol or ethylene, with a particular type of modified crystalline zeolite catalyst and under suitable conversion conditions to effect disproportionation or transalkylation of alkylbenzene compounds or alkylation of aromatic compounds to selectively produce the 1,4-dialkylbenzene isomer in excess of its normal equilibrium concentration. The particular type of crystalline zeolite catalysts utilized herein are zeolite materials having a silica to alumina ratio of at least about 12, a constraint index within the approximate range of 1 to 12 and which have been modified by initial treatment with a compound derived from the element cadmium to yield a composite containing a minor proportion of an oxide of that element. In addition to treatment of the catalyst with one or more cadmium-containing compounds, the zeolite may also be treated with a phosphorus-containing compound to deposit a minor proportion of an oxide of phosphorus thereon. An embodiment of the disclosed invention is a process for the alkylation of aromatic compounds, in the presence of the herein described modified zeolite catalysts, with selective production of the 1,4-dialkylbenzene isomer in preference to the 1,2- and 1,3- isomers thereof. Especially preferred embodiments involve the selective production of 1,4-dimethylbenzene from toluene and methanol and 1-ethyl-4-methylbenzene from toluene and ethylene. Another embodiment contemplates the selective disproportionation or transalkylation of alkylbenzene and polyalkylbenzene compounds in the presence of the disclosed catalysts, thereby yielding 1,4-disubstituted benzenes in excess of their normal equilibrium concentration. For example, under appropriate conditions of temperature and pressure, toluene will disproportionate in the presence of these catalysts to produce benzene and dimethylbenzenes rich in the desirable 1,4-isomer. DESCRIPTION OF SPECIFIC EMBODIMENTS The crystalline zeolites utilized herein are members of a novel class of zeolitic materials which exhibit unusual properties. Although these zeolites have unusually low alumina contents, i.e. high silica to alumina mole ratios, they are very active even when the silica to alumina mole ratio exceeds 30. The activity is surprising since catalytic activity is generally attributed to framework aluminum atoms and/or cations associated with these aluminum atoms. These zeolites retain their crystallinity for long periods in spite of the presence of steam at high temperature which induces irreversible collapse of the framework of other zeolites, e.g. of the X and A type. Furthermore, carbonaceous deposits, when formed, may be removed by burning at higher than usual temperatures to restore activity. These zeolites, used as catalysts, generally have lou coke-forming activity and therefore are conducive to long times on stream between regenerations by burning carbonaceous deposits with oxygen-containing gas such as air. An important characteristic of the crystal structure of this novel class of zeolites is that it provides a selective constrained access to and egress from the intracrystalline free space by virtue of having an effective pore size intermediate between the small pore Linde A and the large pore Linde X, i.e. the pore windows of the structure are of about.a size such as would be provided by lO-membered rings of silicon atoms interconnected by oxygen atoms. It is to be understood, of course, that these rings are those formed by the regular disposition of the tetrahedra making up the anionic framework of the -crystalline zeolite, the oxygen atoms themselves being bonded to the silicon (or aluminum, etc.) atoms at the centers of the tetrahedra. The silica to alumina mole ratio referred to may be determined by conventional analysis. This ratio is meant to represent, as closely as possible, the ratio in the rigid anionic framework of the zeolite crystal and to exclude aluminum in the binder or in cationic or other form within the channels. Although zeolites with silica to alumina mole ratios of at least 12 are useful, it is preferred in some instances to use zeolites having substantially higher silica/alumina ratios, e.g., 1600 and above. In addition, zeolites as otherwise characterized herein but which are substantially free of aluminum, that is having. silica to alumina mole ratios of up to infinity, are found to be useful and even preferable in some instances. Such "high silica" or "highly siliceous" zeolites are intended to be included within this description. Also included within this definition are substantially pure silica analogs of the useful zeolites described herein, that is to say those zeolites having no measurable amount of aluminum (silica to alumina mole ratio of infinity) but which otherwise embody the characteristics disclosed. The novel class of zeolites, after activation, acquire an intracrystalline sorption capacity for normal hexane which is greater than that for water, i.e. they exhibit "hydrophobic" properties. This hydrophobic character can be used to advantage in some applications. The novel class of zeolites useful herein have an effective pore size such as to freely sorb normal hexane. In addition, the structure must provide constrained access to larger molecules. It is sometimes possible to judge from a known crystal structure whether such constrained access exists. For example, if the only pore windows in a crystal are formed by 8-membered rings of silicon and aluminum atoms, then access by molecules of larger cross-section than normal hexane is excluded and the zeolite is not of the desired type. Windows of 10-membered rings are preferred, although in some instances excessive puckering of the rings or pore blockage may render these zeolites ineffective. Although 12-membered rings in theory would not offer sufficient constraint to produce advantageous conversions, it is noted that the puckered 12-ring structure of TMA offretite does show some constrained access. Other 12-ring structures may exist which may be operative for other reasons and, therefore, it is not the present intention to entirely judge the usefulness of a particular zeolite solely from theoretical structural considerations. Rather than attempt to judge from crystal structure whether or not a zeolite possesses the necessary constrained access to molecules of larger cross-section than normal paraffins, a simple determination of the "Constraint Index" as herein defined may be made by passing continuously a mixture of an equal weight of normal hexane and 3-methylpentane over a sample of zeolite at atmospheric pressure according to the following procedure. A sample of the zeolite, in the form of pellets or extrudate, is crushed to a particle size about that of coarse sand and mounted in a glass tube. Prior to testing, the zeolite is treated with a stream of air at 5400C for at least 15 minutes. The zeolite is then flushed with helium and the temperature is adjusted between 2900C and 5100C to give an overall conversion of between 107. and 60%. The mixture of hydrocarbons is passed at 1 liquid hourly space velocity (i.e., 1 volume of liquid hydrocarbon per volume of zeolite per hour) over the zeolite with a helium dilution to give a helium to (total) hydrocarbon mole ratio of 4:1. After 20 minutes on stream, a sample of the effluent is taken and analyzed, most conveniently by gas chromatography, to determine the fraction remaining unchanged for each of the two hydrocarbons. While the above experimental procedure will enable one to achieve the desired overall conversion of 10 to 60% for most zeolite samples and represents preferred conditions, it may occasionally be necessary to use somewhat more severe conditions for samples of very low activity, such as those having an exceptionally high silica to alumina mole ratio. In those instances, a temperature of up to about 54O0C and a liquid hourly space velocity of less than one, such as 0.1 or less, can be employed in order to achieve a minimum total conversion of about 10tO. The "Constraint Index" is calculated as follows: Constraint Index = leo 10 (fraction of hexane remaining) oglo (fraction of 3-methylpentane remaining) The Constraint Index approximates the ratio of the cracking rate constants for the two hydrocarbons. Zeolites suitable for the present invention are those having a Constraint Index of 1 to 12. Constraint Index (CI) values for some typical materials are: ZST1-4 05 ZSM-5 8.3 ZSM-11 8.7 ZSM-12 2 ZSM-23 9.1 ZSM-35 4.5 ZSM-38 2 ZSM-48 3.4 TMA Offretite 3.7 Clinoptilolite 3.4 Beta 0.6 R-Zeolon (mordenite) 0.4 REY 0.4 Amorphous Silica-Alumina 0.6 Erionite 38 The above-described Constraint Index is an important and even critical definition of those zeolites which are useful in the instant invention. The very nature of this parameter and the recited technique by which it is determined, however, admit of the possibility that a given zeolite can be tested under somewhat different conditions and thereby exhibit different Constraint Indices. Constraint Index seems to vary somewhat with severity of operation (conversion) and the presence or absence of binders. Likewise, other variables such as crystal size of the zeolite, the presence of occluded contaminants, etc., may affect the constraint index. Therefore, it will be appreciated that it may be possible to so select test conditions as to establish more than one value in the range of 1 to 12 for the Constraint Index of a particular zeolite. Such a zeolite exhibits the constrained access as herein defined and is to be regarded as having a Constraint Index in the range of 1 to 12. Also contemplated herein as having a Constraint Index in the range of 1 to 12 and therefore within the scope of the defined novel class of highly siliceous zeolites are those zeolites which, when tested under two or more sets of conditions within the above-specified ranges of temperature and conversion, produce a value of the Constraint Index slightly less than e.g. 0.9, or somewhat greater than 12, e.g. 14 or 15, with at least one other value within the range of 1 to 12. Thus, it should be understood that the Constraint Index value as used herein is an inclusive rather than an exclusive value. That is, a crystalline zeolite when identified by any combination of conditions within the testing definition set forth herein as having a Constraint Index in the range of 1 to 12 is intended to be included in the instant novel zeolite definition whether or not the same identical zeolite, when tested under other of the defined conditions, may give a Constraint Index value outside of the range of 1 to 12. The novel class of zeolites defined herein is exemplified by ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48 and other similar materials. ZSM-5 is described in greater detail in U.S. Patents Mo. 3,702,886 and Re 29,948. The entire descriptions contained within those patents, particularly the X-ray diffraction pattern of therein disclosed ZSM-5, are incorporated herein by reference. ZSM-11 is described in U.S. Patent No. 3,709,979. That description, and in particular the X-ray diffraction pattern of said ZSM-11, is incorporated herein by reference. ZSM-12 is described in U.S. Patent No. 3,832,449. That description, and in particular the X-ray diffraction pattern disclosed therein, is incorporated herein by reference. ZSM-23 is described in U.S. Patent No. 4,076,842. The entire content thereof, particularly the specification of the X-ray diffraction pattern of the disclosed zeolite, is incorporated herein by reference. ZSM-35 is described in U.S. Patent No. 4,016,245. The description of that zeolite, and particularly the X-ray diffraction pattern thereof, is incorporated herein by reference. ZSM-38 is more particularly described in U.S. Patent No. 4,046,859. The description of that zeolite, and particularly the specified X-ray diffraction pattern thereof, is incorporated herein by reference. ZSM-48 can be identified, in terms of moles of anhydrous oxides per 100 moles of silica, as follows: (0-15)RN : (0-1 .S)M2/nO : (0.2)awl203 : (100)SiO2 wherein: M is at least one cation having a valence n; and RN is a C1-C20 organic compound having at least one amine functional group of pKa#7 It is recognized that, particularly when the composition contains tetrahedral, framework aluminum a fraction of the amine functional groups may be protonated. The doubly protonated form, in conventional notation, would be (RNH)20 and is equivalent in stoichiometry to 21 + H20. The characteristic X-ray diffraction pattern of the synthetic zeolite ZSM-48 has the following significant lines: Characteristic Lines of ZSM-48 d (Amstroms) Relative Intensity 11.9 W-S 10.2 T. 7.2 w 5.9 W 4.2 VS 3.9 VS 3.6 w 2.85 w These values were determined by standard techniques. The radiation was the K-alpha doublet of copper, and a scintillation counter spectrometer with a strip chart pen recorder was used. The peak heights, I, and the positions as a function of 2 times theta, where theta is the Bragg angle, were read from the spectrometer chart. From these, the relative intensities, 100 I/Io, where Io is the intensity of the strongest line or peak, and d (obs.), the interplanar spacing in angstroms, corresponding to the recorded lines, were calculated. In the foregoing table the relative intensities are given in terms of the symbols W weak, VS = very strong and W-S = weak-to-strong. Ion exchange of the sodium ion with cations reveals substantially the same pattern with some minor shifts in interplanar spacing and variation in relative intensity. Other minor variations can occur depending on the silicon to aluminum ratio of the particular sample, as well as if it has been subjected to thermal treatment. The ZSM-48 can be prepared from a reaction mixture containing a source of silica, water, RN, an alkali metal oxide (e.g. sodium) and optionally alumina. The reaction mixture should have a composition, in terms of mole ratios of oxides, falling within the following ranges: REACTANTS BROAD PREFERRED A1203/siO2 8 0 to 0.02 0 to 0.01 Na/Si02 - 0 to 2 0.1 to 1.0 Dl/SiO2 = 0.01 to 2.0 0.05 to 1.0 OH-/SiO2 - 0 to 0.25 0. to 1.0 H2O/SiO2 = 10 to 100 20 to 70 H+(added)/SiO2 - 0 to 0.2 0 to 0.05 wherein BX is a C1 -C20 organic compound having amine functional group of pKa#7. The mixture is maintained at 80-2500C until crystals of the material are formed. H+(added) is moles acid added in excess of the moles of hydroxide added. In calculating H+(added) and OH values, the term acid (K+) includes both hydronium ion, whether free or coordinated, and aluminum. Thus aluminum sulfate, for example, would be considered a mixture of aluminum oxide, sulfuric acid, and water. An amine hydrochloride would be a mixture of amine and HCl. In preparing the highly siliceous form of ZSM-48 no alumina is added. Thus, the only aluminum present occurs as an impurity in the reactants. Preferably, crystallization is carried out under pressure in an autoclave or static bomb reactor, at 800C to 2500C. Thereafter, the crystals are separated from the liquid and recovered. The composition can be prepared utilizing materials which supply the appropriate oxide. Such compositions include sodium silicate, silica hydrosol, silica gel, silicic acid, RN, sodium hydroxide, sodium chloride, aluminum sulfate, sodium aluminate, aluminum oxide" or aluminum itself. RN is a C1-C20 organic compound containing at least one amine functional group of pkL7, as defined above, and includes such compounds as C3-C18 primary, secondary, and tertiary amines, cyclic amine (such as piperdine, pyrrolidine and piperazine), and polyamines such as NH2-CnH2n-NH2 wherein m is 4-12. The original cations can be subsequently replaced, at least in part, by calcination and/or ion exchange with another cation. Thus, the original cations are exchanged into a hydrogen or hydrogen ion precursor form or a form in which the original cation has been replaced by a metal of Groups II through VIII of the Periodic Table. Thus, for example, it is contemplated to exchange the original cations with ammonium ions or with hydronium ions. Catalytically active forms of these would include, in particular, hydrogen, rare earth metals, aluminum, manganese and other metals of Groups II and VIII of the Periodic Table. It is to be understood that by incorporating by reference the foregoing patents to describe examples of specific members of the novel class with greater particularity, it is intended that identification of the therein disclosed crystalline zeolites be resolved on the basis of their respective X-ray diffraction patterns. As discussed above, the present invention contemplates utilization of such catalysts wherein the mole ratio of silica to alumina is essentially unbounded. The incorporation of the identified patents should therefore not be construed as limiting the disclosed crystalline zeolites to those having the specific silica-alumina mole ratios discussed therein, it now being known that such zeolites may be substantially aluminum-free and yet, having the same crystal structure as the disclosed materials, may be useful or even preferred in some applications. It is the crystal structure, as identified by the X-ray diffraction "fingerprint", which establishes the identity of the specific crystalline zeolite material. The specific zeolites described, when prepared in the presence of organic cations, are substantially catalytically inactive, possibly because the intracrystalline free space is occupied by organic cations from the forming solution. They may be activated by heating in an inert atmosphere at 5400C for one hour, for example, followed by base exchange with ammonium salts followed by calcination at 5400C in air. The presence of organic cations in the forming solution may not be absolutely essential to the formation of this type zeolite; however, the presence of these cations does appear to favor the formation of this special class of zeolite. More generally, it is desirable to activate this type catalyst by base exchange with ammonium salts followed by calcination in air at about 5400C for from about 15 minutes to about 24 hours. Natural zeolites may sometimes be converted to zeolite structures of the class herein identified by various activation procedures and other treatments such as base exchange, steaming, alumina extraction and calcination, alone or in combinations. Natural minerals which. may be so treated include ferrierite, brewsterite, stilbite, dachiardite, epistilbite, heulandite, and clinoptilolite. The preferred crystalline zeolites for utilization herein include ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, and ZSM-48, with ZSM-5 being particularly preferred. In a preferred aspect of this invention, the zeolites hereof are selected as those providing among other things a crystal framework density, in the dry hydrogen form, of not less than about 1.6 grams per cubic centimeter. It has been found that zeolites which satisfy all three of the discussed criteria are most desired for several reasons. When hydrocarbon products or by-products are catalytically formed, for example, such zeolites tend to maximize the production of gasoline boiling range hydrocarbon products. Therefore, the preferred zeolites useful with respect to this invention are those having a Constraint Index as defined above of about 1 to about 12, a silica to alumina mole ratio of at least about t and a dried crystal density of not less than about 1.6 grams per cubic centimeter. The dry density for known structures may be calculated from the number of silicon plus aluminum atoms per 1000 cubic Angstroms, as given, e.g., on Page 19 of the article ZEOLITE STRUCTURE by W. M. Meier. This paper, the entire contents of which are incorporated herein by reference, is included in PROCEEDINGS OF THE COMFEPENCE ON MOLECULAR SIEVES, (London, April 1967) published by the Society of Chemical Industry, London, 1968. When the crystal structure is unknown, the crystal framework density may be determined by classical pycnometer techniques. For example, it may be determined by immersing the dry hydrogen form of the zeolite in an organic solvent which is not sorbed by the crystal. Or, the crystal density may be determined by mercury porosimetry, since mercury will fill the interstices between crystals but will not penetrate the intracrystalline free space. It is possible that the unusual sustained activity and stability of this special class of zeolites is associated with its high crystal anionic framework density of not less than about 1.6 grams per cubic centimeter. This high density must necessarily be associated with a relatively small amount of free space within the crystal, which might be expected to result in more stable structures. This free space, however, is important as the locus of catalytic activity. Crystal framework densities of some typical zeolites, including some which are not within the purview of this invention, are: Void Framework Volume Density Ferrierite 0.28 cc/cc 1.76 g/cc Mordenite .28 1.7 ZSM-5, -11 .29 1.79 ZSM-1 2 1.8 ZSM-23 2.0 Dachiardite .32 1.72 L .32 1.61 Clinoptilolite .34 1 71 1.71 Laumontite .34 1.77 ZSM-4 (Omega) .38 1.65 Heulandite .39 1.69 P .41 1.57 Offretite .40 1.55 Levynite .40 1.54 Erionite .35 1.51 Gmelinite .44 1.46 Chabazite .47 1.45 A .5 1.3 Y .48 1.27 FJhen synthesized in the alkali metal form, the zeolite is conveniently converted to the hydrogen form, generally by intermediate formation of the ammonium form as a result of ammonium ion exchange and calcination of the ammonium form to yield the hydrogen form. In addition to the hydrogen form, other forms of the zeolite wherein the original alkali metal has been reduced to less than about 1.5 percent by weight may be used. Thus, the original alkali metal of the zeolite may be replaced by ion exchange with other suitable metal cations of Groups I through VIII of the Periodic Table, including, by way of example, nickel, copper, zinc, palladium, calcium or rare earth metals. In practicing a particularly desired chemical conversion process, it may be useful to incorporate the above-described crystalline zeolite with a matrix comprising another material resistant to the temperature and other conditions employed in the process. Such matrix material is useful as a binder and imparts greater resistance to the catalyst for the severe temperature, pressure and reactant feed stream velocity conditions encountered in many cracking processes. Useful matrix materials include both synthetic and naturally occurring substances, as well as inorganic materials such as clay, silica and/or metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Naturally occurring clays which can be composited with the zeolite include those of the montmorillonite and kaolin families, which families include the sub-bentonites and the kaolins commonly known as Dixie, McNamee-Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the zeolites employed herein may be composited with a porous matrix material, such as alumina, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, and silica-titania, as well as ternary compositions, such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix may be in the form of a cogel. The relative proportions of zeolite component and inorganic oxide gel matrix, on an anhydrous basis, may vary widely with the zeolite content ranging from between about 1 to about 99 percent by weight and more usually in the range of about 5 to about 80 percent by weight of the dry omposite. The above crystalline zeolites employed are, in accordance with the present invention, contacted with a solution of one or more compounds of the element cadmium (Cd). Solutions of such compounds may be in any suitable solvent which is inert with respect to the metal-containing compound and the zeolite. Non-limiting examples of some suitable solvents include water, aliphatic and aromatic hydrocarbons, alcohols, organic acids (such as acetic acid, formic acid, propionic acid and so forth), and inorganic acids (such as hydrochloric acid, sulfuric acid and nitric acid). Other commonly available solvents such as halogenated hydrocarbons, ketones, ethers, etc. may also be useful to dissolve some metal compounds or complexes. Generally, the most useful solvent will be found to be water. However, the solvent of choice for any particular compound will, of course, be determined by the nature of that compound and for that reason the foregoing list should not be considered exhaustive of all of the suitable possibilities. Representative cadmium-containing compounds include cadmium acetate, cadmium bromide, cadmium chloride, cadmium fluoride, cadmium iodide, cadmium formate, cadmium futnarate, cadmium lactate, cadmium maleate, cadmium nitrate, cadmium oxalate, cadmium phosphate, cadmium oxide, cadmium sulfide, cadmium sulfate, cadmium iodate, cadmium chlorate, cadmium carbonate, cadmium benzoate, cadmium ammonium sulfate, cadmium ammonium chloride and cadmium cyanide. This listing is not to be taken as encompassing all of the utilizable cadmium-containing compounds. It is merely intended to be illustrative of some of the representative metal compounds which those in the art will find useful in practicing the disclosed invention. The knowledgeable reader will readily appreciate that there are numerous other known cadmium salts and complexes which would prove useful herein to provide solutions containing cadmium suitable for combination with the zeolite in the manner hereinafter described. Reaction of the zeolite with the treating cadmium compound is effected by contacting the zeolite with such compound. Where the treating compound is a liquid, such compound can be in solution in a solvent at the time contact with the zeolite is effected. Any solvent relatively inert with respect to the treating cadmium compound and the zeolite may be employed. Suitable solvents include water and aliphatic, aromatic or alcoholic liquid. The treating compound may also be used without a solvent, i.e. may be used as a neat liquid. There the treating compound is in the gaseous phase, it can be used by itself or in admixture with a gaseous diluent relatively inert to the treating compound and the zeolite (such as helium or nitrogen) or with an organic solvent such as octane or toluene. Heating of the cadmium compound impregnated catalyst subsequent to preparation and prior to use is preferred, and heating can be carried out in the presence of oxygen - for example, in ir. Although heating can be at a temperature of about 1500C, higher temperatures, e.g. up to about 5000C, are preferred. Heating is generally carried out for 1-5 hours but may be extended to 24 hours or longer. While heating temperatures above about 5000C may be employed, they are generally not necessary, and at temperatures of about 10000C the crystal structure of the zeolite tends to deteriorate. After heating in air at elevated temperatures, and without being limited by any theoretical considerations, it is contemplated that the cadmium is actually present in the zeolite in an oxidized state, such as CdO. The amount of cadmium oxide incorporated in the zeolite should be at least about 0.25 percent by weight. However, it is preferred that the amount be at least about 2.0 percent by weight, particularly when the zeolite is combined with a binder, e.g. 35 weight percent of alumina. The amount of cadmium oxide can be as high as about 40 percent by weight or more depending on the amount and type of binder present. Preferably, the amount of cadmium oxide added to the zeolite will be between about 2 and about 35 percent by weight. The amount of cadmium incorporated with the zeolite by reaction with elemental cadmium or cadmiumcontaining compound will depend upon several factors. One of these is the reaction time, i.e., the time that the zeolite and the cadmium-containing source are maintained in contact with each other. With greater reaction times, all other factors being equal, a greater amount of metal is incorporated with the zeolite. Other factors upon which the amount of cadmium incorporated with the zeolite is dependent include reaction temperature, concentration of the treating compound in the reaction mixture, the degree to which the zeolite has been dried prior to reaction with the metal-containing compound, the conditions of drying of the zeolite after reaction with the treating compound, and the amount and type of binder incorporated with the zeolite. A further embodiment of this invention includes additional modification of the above metal oxide - zeolite composites with phosphorus, whereby from about 0.25 weight percent to about 30 weight percent of an oxide of phosphorus, calculated as P2O5, is combined with the zeolite. The preferred amount of phosphorus oxide will be between about 1 weight percent and about 25 weight percent, based on the weight of the treated zeolite. The phosphorus treatment of the zeolite catalyst will preferably be carried out before the previously described modification with one or more of the specified metals. Reaction of the zeolite compound with the phosphorus-containing compound is carried out essentially as described above with respect to the metal-containing compounds and it is preferred that the total amount of oxides combined with the zeolite, i.e. the phosphorus oxides plus the metal oxides, fall within the approximate range of 2 percent to 40 percent by weight, based on the weight of the treated zeolite. Representative phosphorus-containing compounds which may be used include derivatives of groups represented by PX3, RPX2, R2PX, R3P, X3PO, (XO)3PO, (XO)3P, R3P-O, R3P=S; RPO2, RPS2, RP(O)(OX)2, RP(S)(SX)2, R2P(O)OX, R2P(S)SX, PS(SX)2, ROP(OX)2, RSP(SX)2, (RS)2PSP(SR)2, and (RO)2POP(OR)2, where R is an alkyl or aryl, such as a phenyl radical and Y. is hydrogen, R, or halide. These compounds include primary, RPH2, secondary, R2PH and tertiary, R3P, phosphines such as butyl phosphine; the tertiary phosphine oxides R3PO, such as tributylphosphine oxide, the tertiary phosphine sulfides, R3PS, the primary, RP(O)(OX)2, and secondary, R2P(O)OX, phosphonic acids such as benzene phosphonic acid; the corresponding sulfur derivatives such as RP(S)(SX)2 and R2P(S)SX, the esters of the phosphonic acids such as diethyl phosphonate, (RO)2P(O)H, dialkyl alkyl phosphonates, (PwO)2P(O)R, and alkyl dialkylphosphinates, (RO)P(O)R2; phosphinous acids, R2POX, such as diethylphosphinous acid, primary, (RO)P(OX)2, secondary; (RO)2POX, and tertiary, (RO)3P, phosphites; and esters thereof such as the monopropyl ester, alkyl dialkylphosphinites, (RO)PR2, and dialkyl alkylphosphinite, (RO)2PR esters. Corresponding sulfur derivatives may also be employed including (PXS)2P(S)H, (RS)2P(S)R, (RS)P(S)R2, R2PSX, (RS)P(SX)2, (RS)2PSX, (RS)3P, (RS)PR2 and (RS)2PR. Examples of phosphite esters include trimethylphosphite, triethylphosphite, diisopropylphosphite, butylphosphite; and pyrophosphites such as tetraethylpyrophosphite. The alkyl groups in the mentioned compounds contain from one to four carbon atoms. Other suitable phosphorus-containing compounds include the phosphorus halides such as phosphorus trichloride, bromide, and iodide, alkyl phosphorodichloridites, (RO)PCl2, dialkyl phosphorochloridites, (RO)2PCl, dialkylphosphinochloridites, R2PCl, alkyl alkylphosphono- chloridates, (RO)(R)P(O)C1, dialkyl phosphinochloridates, R2P(O)Cl and RP(O)Cl2. Applicable corresponding sulfur derivatives include (RS)PCl2, (RS)2PC1, (RS)(R)P(S)Cl and R2P(S)Cl. Preferred phosphorus-containing compounds include diphenyl phosphine chloride, trimethylphosphite and phosphorus trichloride, phosphoric acid, phenyl phosphine oxychloride, trimethylphosphate, diphenyl phosphinous acid, diphenyl phosphinic acid, diethylchlorothiophosphate, methyl acid phosphate and other alcohol-P2O5 reaction products. Particularly preferred are ammonium phosphates, including ammonium hydrogen phosphate, (NH4)2HP04, and ammonium dihydrogen phosphate, NH4H2?04. Still another modifying treatment entails steaming of the zeolite by contact with an atmosphere containing from about 5 to about t00 percent steam at a temperature of from about 2500 to about 10000C for a period of between about 15 minutes and about 100 hours and under pressures ranging from sub-atmospheric to several hundred atmospheres. Preferably, steam treatment is effected at a temperature of between about 4000C and about 7000C for a period of between about 1 and about 24 hours. Another modifying treatment involves precoking of the catalyst to deposit a coating of between about 2 and about 75, and preferably between about 15 and about 75, weight percent of coke thereon. Precoking can be accomplished by contacting the catalyst with a hydrocarbon charge, e.g. toluene, under high severity conditions or alternatively at a reduced hydrogen to hydrocarbon concentration, i.e. 0 to 1 mole ratio of hydrogen to hydrocarbon, for a sufficient time to deposit the desired amount of coke thereon. It is also contemplated that a combination of steaming and precoking of the catalyst under the above conditions may be employed to suitably modify the crystalline zeolite catalyst. Alkylation of aromatic compounds in the presence of the above-described catalyst is effected by contact of the aromatic with an alkylating agent. A particularly preferred embodiment involves the alkylation of toluene wherein the alkylating agents employed comprise methanol or other well known methylating agents or ethylene. The reaction is carried out at a temperature of between about 2500C and about 7500C, preferably between about 3000C and 6500C. At higher temperatures, the zeolites of high silica/alumina ratio are preferred. For example, ZSM-5 having a SiO2/Al203 ratio of 30 and upwards is exceptionally stable at high temperatures. The reaction generally takes place at atmospheric pressure, but pressures within the approximate range of 105 21/m2 to 1a7 N/m2 (1-100 atmospheres) may be employed. Some non-limiting examples of suitable alkylating agents would include olefins such as, for example, ethylene, propylene, butene, decene and dodecene, as well as formaldehyde, alkyl halides and alcohols, the alkyl portion thereof having from 1 to 16 carbon atoms. Numerous other aliphatic compounds having at least one reactive alkyl radical may be utilized as alkylating agents. Aromatic compounds which may be selectively alkylated as described herein would include any alkylatable aromatic hydrocarbon such as, for example, benzene, ethylbenzene, toluene, dimethylbenzenes, diethylbenzenes, methylethylbenzenes, propylbenzene, isopropylbenzene, isopropylmethylbenzenes, or substantially any mono- or di-substituted benzenes which are alkylatable in the 4-position of the aromatic ring. The molar ratio of alkylating agent to aromatic compound is generally between about 0.05 and about 5. For instance, when methanol is employed as the methylating agent and toluene is the aromatic, a suitable molar ratio of methanol to toluene has been found to be approximately 1-0.1 moles of methanol per mole of toluene. Reaction is suitably accomplished utilizing a feed weight hourly space velocity (WHSV) of between about 1 and about 1000, and preferably between about 1 and about 200. The reaction product, consisting predominantly of the 1,4-dialkyl isomer, e.g. 1,4-dimethylbenzene, 1-ethyl-4-methylbenzene, etc., or a mixture of the 1,4- and 1,2- isomers together with comparatively smaller amounts of 1,3-dialkylbenzene isomer, may be separated by any suitable means. Such means may include, for example, passing the reaction product stream through a water condenser and subsequently passing the organic phase through a column in which chromatographic separation of the aromatic isomers is accomplished. when transalkylation is to be accomplished, transalkylating agents are alkyl or polyalkyl aromatic hydrocarbons wherein alkyl may be composed of from 2 to about 5 carbon atoms, such as, for example, toluene, xylene, trimethylbenzene, triethylbenzene, dimethylethylbenzene, ethylbenzene, diethylbenzene, ethyltoluene, and so forth. Another aspect of this invention involves the selective disproportionation of alkylated aromatic compounds to produce dialkylbenzenes wherein the yield of 1 ,4-dialkyl isomer is in excess of the normal equilibrium concentration. In this context, it should be noted that disproportionation is a special case of transalkylation in which the alkylatable hydrocarbon and the transalkylating agent are the same compound, for example when toluene serves as the donor and acceptor of a transferred methyl group to produce benzene and xylene. The transalkylation and disproportionation reactions are carried out by contacting the reactants with the above described modified zeolite catalyst at a temperature of between about 2500C and 7500C at a pressure of between atmospheric (105 t1/m2) and about 100 atmospheres (107 t1/m2). The reactant feed WHSV will normally fall within the range of about 0o1 to about 5Q. Preferred alkylated aromatic compounds suitable for utilization in this embodiment comprise toluene, ethylbenzene, propylbenzene or substantially any mono-substituted alkylbenzene. These aromatic compounds are selectively converted to, respectively, 1,4-dimethylbenzene, 1,4-diethylbenzene, 1 ,4-dipropylbenzene, or other 1,4-dialkylbenzene, as appropriate, with benzene being a primary side product in each instance. The product is recovered from the reactor effluent by conventional means, such as distillation to remove the desired products of benzene and dialkylbenzene, and any unreacted aromatic component is recycled for further reaction. The hydrocarbon conversion processes described herein may be carried out as a batch type, semi-continuous or continuous operation utilizing a fixed or moving bed catalyst system. The catalyst after use in a moving bed reactor is conducted to a regeneration zone wherein coke is burned from the catalyst in an oxygen-containing atmosphere, eog. air, at an elevated temperature, after which the regenerated catalyst is recycled to the conversion zone for further contact with the charge stock. In a fixed bed reactor, regeneration is carried out in a conventional manner where an inert gas containing a small amount of oxygen (0°5-2%) is used to burn the coke in a controlled manner so as to limit the temperature to a maximum of around 5000-5500C. The following examples will serve to illustrate certain specific embodiments of the hereindisclosed invention. These examples should not, however, be construed as limiting the scope of the novel invention as there are many variations which may be made thereon without departing from the spirit of the disclosed invention, as those of skill in the art will recognize. EXAMPLE 1A - [Alkylation reaction with unmodified ZSM-5] Five grams of HZSM-5 (silica/alumina mole ratio = 70; 65 on alumina binder) were placed in a quartz flow reactor and heated to various temperatures between 3500C and 5000C. A mixture of toluene and methanol, at a 4/1 molar ratio, was passed thru the zeolite catalyst at a weight hourly space velocity (TJHSV) of 10. The reactor effluent was monitored and the results obtained at the various temperatures are shown below. Temperature Percent toluene Percent para-isomer ¯ C conversion in xvlenes 350 47.2 24.8 400 58.0 24.4 450 68.0 24.3 500 87.6 24.2 EXAMPLE 1B In a similar manner, toluene was alkylated with ethylene by passing toluene and ethylene, at WHSV of 7.0 and 0.5, respectively, over the unmodified zeolite. The results at various temperatures are shown below. Temperature Percent toluene Isomer ratios of C conversion ethyltoluene ç m o 400 76.4 29.9 58.5 11.6 425 76.4 29.9 57.5 12.7 450 79.0 29.6 57.1 13.4 EXAMPLE 2 [Disproportionation reaction with unmodified ZSM-5] Toluene was passed over a 6,0g sample, of HZSM-5 (Si02/A1203 mole ratio = 70; 65% on alumina binder) at a feed WHSV of 3.5-3.6 and at temperatures between 4500C and 6000C. The results are summarized below. Temperature WHSV Toluene Conversion %Selectivity, wt %para in C Mole % Benzene Xylenes xylene products 450 3.6 7.4 43.5 55.5 24.7 500 3.5 20.5 44.6 53.8 24.5 550 3.5 38.8 48.0 48.8 24.2 600 3.5 49.2 54.4 41.7 24.1 EXAMPLE 3 [Preparation of Cd-modified zeolite To a solution of 5.0g cadmium acetate in 5.Q ml water heated at 800C was added 3.0g HZSM-5 (SiO2/Al203 = 70). The mixture was maintained at 800C for 2 hours. After filtration and drying at about 900C for 16 hours, the residue was calcined at 5000C for 2 hours to give 3.65g of Cd-ZSM-5. The content of cadmium was analyzed to be 21.3%. EXAMPLE 4A [Alkylation reaction with Cd-modified zeolites Alkylation of toluene with methanol was carried out by passing a toluene/methanol mixture (molar ratio of 4/1) over 1.1g of the Cd-ZSM-5 catalyst of Example 3 at WHSV of 10 and 5000C. Toluene conversion was 19.6% and selectivity to p-xylene in xylenes was 64.3. Under substantially the same conditions the unmodified ZSM-5 (Example. 1A) resulted in only 24.2% selectivity to para-isomer. EXAMPLE 4B In a similar manner, ethylation of toluene was carried out by passing toluene (at WHSV - 7) and ethylene at (WHSV = 0.5) over 1 .1g of the Cd-ZSM-5 catalyst of Example 3 at 4000C. Conversion of toluene was 40.3Z and selectivity to p-ethyltoluene in ethyltoluenes was 89.5, EXAMPLE 5 [Disproportionation reaction with Cd-modified zeolitel Disproportionation of toluene was carried out by passing toluene over 1.1g of the Cd-ZSM-5 catalyst of Example 3 at tESV 8 3.5 and 50O0C. Toluene conversion was 7.1% and selectivity to p-xylene in xylene was 68.9%. This represents a very significant increase in para-selectivity compared to the 24.5% selectivity shown for the unmodified zeolite under the same conditions of reaction (Example 2). EXAMPLE 6 [Preparation of P-modified zeolite] Two hundred grams of ammonium-ZSM-5 (6574 on alumina binder) were added to a solution of 80g of diammonium hydrogen phosphate in 300 ml of R20 at about 900C. After standing at about 900C for 2 hours, the zeolite was filtered, dried at 900C for 2 hours and then calcined at 5O00C for another 2 hours. The recovered P-ZSM-5 zeolite contained 3.43 wt.% phosphorus. EXAMPLE 7A [Alkylation reaction wtih P-modified zeolite Alkylation of toluene with methanol was carried out by passing a toluene/methanol feed stream (molar ratio = 4/1) over 5.0g of the P-ZSM-5 zeolite of Example 6. The feed t4HSV was 10 and the reactor temperature was varied between 4000C and 6000C. The results obtained are summarized below. Temperature Percent Toluene Percent para-isomer C Conversion in Xvlenes 400 43.6 66.6 450 54.4 57.7 500 70.4 53.7 550 85.2 52.0 600 85.2 58.0 EXAMPLE 7B In a similar manner, ethylation of toluene was accomplished utilizing a feed stream of toluene (x4HSV a 7.0) and ethylene (WHSV = 0.5) in the presence of the P-ZSM-5 catalyst at 4000C. Conversion of toluene was 74.8% and selectivity to the para-isomer of ethyltoluene was 55.5%. EXAMPLE 8 [Disproportionation reaction with P-modified zeolite] Toluene disproportionation was tested by passing a stream of toluene over the P-ZSM-5 catalyst of Example 6 at a feed WHSV of 3.5 at temperatures of between 4750C and 5500C. The results are summarized below. Temperature Toluene Conversion %Selectivity, mole %para in C Mole % Benzene Xylenes xylene products 475 14.9 52.8 47.6 39.1 500 27.1 53.3 45.4 35.1 525 37.4 56.1 42.2 32.1 550 44.0 60.4 37.3 30.1 EXAMPLE 9 [Preparation of Cd-P-modified zeolite] To a solution of 8.0g cadmium acetate in 10 ml water heating at approximately 80 C was added 6.0g of the P-ZSM-5 of Example 6, and the mixture maintained at 80-900C to 2 hours. After filtration and drying at about 900C, the residue was calcined at 5000C for 2 hours to give 6.81g Cd-P-ZSM-5. Analysis showed the content of cadmium to be 17.8% and that of phosphorus to be 2.03%. EXAMPLE 1 OVA [Alkylation reaction with Cd-P-modified zeolite] Alkylation of toluene with methanol was carried out by passing a toluene/methanol mixture (molar ratio of 4/1) over 1.1g of the Cd-P-ZSM-5 catalyst of Example 9 at WHSV of 10 and 4000C. Toluene conversion was 6.8% and selectivity to p-xylene in xylenes was 94.6%. This is a dramatic increase over the selectivity of the catalyst modified with phosphorus alone [Example 7A]. EXAMPLE 10B In a similar manner, ethylation of toluene was made by passing toluene (at t4HSV = 7) and ethylene (at TJHSV = 0.5) over 1.1g of the Cd-P-ZSM-5 catalyst of Example 9 at 400 C. Conversion of toluene was 2.1% and selectivity to p-ethyltoluene in ethyltoluene was over 99%. Again, a startling increase in selectivity compared to the P-ZSM-5 alone [Example 7B]. EXAMPLE 11 [Disproportionation reaction with Cd-P-modified zeolite] Disproportionation of toluene was carried out by passing toluene over 1.1g of the Cd-P-ZSM-5 catalyst of Example 9 at I4HSV = 3.5 and 5000C. Toluene conversion was 6.5% and selectivity to p-xylene in xylene was 96%. By contrast, disproportionation of toluene with P-ZSM-5 (Example 8) resulted in only 35.1% selectivity to para-isomer under the same conditions. EXAMPLE 12A [Alkylation reaction with unmodified ZSM-113 A toluene/methanol feed stream, having a 4/1 molar ratio of the respective reactants, was passed over unmodified HZSM-11 zeolite (SiO2/Al203 = 70) at 400-6000C and a feed WHSV of 10. The results are shown below. Temperature Percent Toluene Percent para-xylene 0C Conversion in Xylenes 400 67.6 23.4 500 90.4 24.0 600 157.2 22.7 EXAMPLE 12B A toluene/ethylene feed stream was similarly brought into contact with the unmodified HZSM-11. The feed t;HSV was 7.5 and 0.55, respectively, and the temperature of reaction 4000-4500C. The results are summarized below. Temperature Percent Toluene Isomer ratios of C Conversion ethyltoluene p m o 400 80.2 27.3 58.4 14.3 450 81.9 27.2 57.9 14.9 EXAMPLE 13 [Disproportionation reaction with unmodified ZSM-11] A 1.0g portion of unmodified HZSM-11 zeolite (silica to alumina mole ratio t 70) was placed in a quartz flow reactor and heated to temperature. Toluene was passed over the zeolite at WHSV of 3.8 and various temperatures between 4000C and 6000C. The results are summarized below. Temperature Toluene Conversion %Selectivity, mole %para in C % Benzene Xylenes Xylene products 400 3.0 51.7 47.8 24.3 450 8.7 48.1 50.7 24.1 500 21.7 49.0 48.9 23.7 550 39.1 53.7 42.6 23.7 600 49.9 58.6 36.8 23.4 EXAMPLE 14 [Preparation of Cd-modified ZSM-11 To a solution of 4.0g cadmium acetate in 5 ml water heated at 80 C was added 1.5 HZSM-11 (SiO2/Al2O3 = 70). The mixture was maintained at SOC - 90 C for 2 hours. After filtration and drying at about 900C for 15 hours, the residue was calcined at 5CC C for 2 hours to give 2.1 Cd-modified ZSM-11] The content of cadmium was analyzed to be 26.2k. EXAMPLE 15A [Alkylation reaction with Cd-modified ZSM-11] Alkylation of toluene with methanol was carried out by passing a toluene/nethanol mixture (molar ratio of 4/l) over 1.1g of the Cd-ZSM-11 catalyst of Example 14 at WHSV of 10 and 400 C. Toluene conversion was 27.6% and selectivity to p-xylene in xylenes was 31.0%. EXAMPLE 15B - In a similar manner, ethylation of toluene was caried out by passing toluene (at t2HSV = 7) and ethylene at (WHSV = 0.5) over 1.1g of the Cd-ZSM-11 catalyst of Example 14 at 400 C. Conversion of toluene was 15.1% and selectivity to p-ethyltoluene in ethyltoluene was 45.0%. As the foregoing ably demonstrate, modification of the ZSM-11 zeolite with cadmium as herein described results in significant increases in para-selectivity as compared to the active of the unmodified zeolite (Example 12). EXAMPLE 16 [Disproportionation reaction with Cd-modified ZSM-11] Disproportionation of toluene was carried out by passing toluene over 1.1g of the Cd-ZSM-11 catalyst of Example 14 at l;1HSV = 3.5 and 4509C. Toluene conversion was 1.3% and selectivity to p-xylene inxylene was 48.1%. This represents approximately twice the level of para-selectivity shown by the unmodified ZSM-11 zeolite in the same reaction [Example 13]. It is to be understood that the foregoing is intended to be merely illustrative of certain specific embodiments of the disclosed invention. As those of skill in the art will readily appreciate, there are many variations which may be made on these specific embodiments without departing from the spirit of the herein described invention and such variations are clearly to be encompassed within ambit of the following claims.

Claims: CLAIMS: 1. A process for conversion of organic compounds, comprising contacting said organic compounds with a crystalline zeolite catalyst at a temperature of 2500C to 7500C and a pressure of lO5N/m2 to 107N/m2, said zeolite having a silica to alumina mole ratio of at least 12 and a constraint index of 1 to 12 and having undergone prior modification by treatment with one of more cadmium compounds to deposit thereon at least 0.25 weight percent of cadmium. 2. The process of claim l wherein said temperature is between 300oC and 6500C. 3. The process of claim 1 or claim 2 wherein cadmium comprises between 2 and 35 weight percent of the modified zeolite catalyst. 4. The process of any of claims 1 to 3 wherein said zeolite is also modified by treatment with a phosphorus compound to deposit thereon at least 0.25 weight percent of phosphorus. 5. The process of any preceding claim wherein said zeolite is admixed with a binder therefor. 6. The process of any preceding claim wherein said conversion is the alkylation of an aromatic compound by contacting said compound with an alkylating agent to produce dialkylbenzene compounds wherein the 1,4-dialkyl- benzene isomer is present in excess of its normal equilibrium concs ation. 7. The process of any of claims 1 to 5 wherein said conversion is the transalkylation of aromatic compounds to produce dialkylbenzene compounds wherein the 1,4-dialkyl- benzene isomer is present in excess of its normal equilibrium concentration. 8. The process of any of claims l to 5 wherein said conversion process is disproportionation of alkylbenzenes to produce benzene and dialkylbenzenes in which the proportion of 1,4-dialkylbenzene isomer is in excess of its normal equilibrium concentration. 9. The process of any preceding claim wherein said zeolite is ZSM-5, ZSM-ll, ZSIA-12, ZSM-23, ZSM-35, ZSM-38 or ZSM-48.

Inventors: CHU, CHIN CHIUN
Applicants: MOBIL OIL CORPORATION
Application year: 1981
Main classification: C07C2
IPC codes: C07C15, B01J29, C07B61, C07C2, C07C1, C07C67, C07C6