COATED FABRIC AND MATTRESS TICKING

Abstract: Coated fiberglass fabrics especially suitable for use as mattress tickings. The fabrics comprise a woven or non-woven fiberglass fabric to which a layer of a polymeric coating composition has been applied. The coating comprises a polymeric carrier containing an effective amount of a fungicide and/or bacteriocide, an effective amount of a flame retardant, and a filler which also functions to enhance the flame retardant properties of the fabric.

Description: COATED FABRIC AND MATTRESS TICKING Field of the Invention: This invention relates to coated fiberglass fabrics which are bacteriostatic, impermeable to liquids such as urine, resistant to chemical attack, and, in addition, are flame retardant. The coated fiber- glass fabrics of the present invention are also durable and easy to care for. BACKGROUND OF THE INVENTION Flame retardant fabrics are desirable for use in the manufacture of furniture upholstery, curtains, mattress tickings, bedspreads and the like for domestic use as well as for use in institutions / hotels or other commercial establishments, where the safety element associated with such fabrics is desirable. In some states, the use of flame retardant bedding upholstery in institutions such as hospitals, nursing homes, mental institutions, prisons, universities and the like, is required by law. Flame retardance has been achieved in heavy cotto fabrics such as A.C.A. striped mattress ticking, by treatin the cotton fabric with a hydrated sodium borate compound. The sodium borate treatment functions both to reduce the rate of travel of the flame through the fabric, as well as to contribute a self-extinguishing property to the fabric, such that upon removal of the external flame source the treated fabric itself is substantially incapable of supporting a flame. In addition to the property of flame retardance, for many applications it is desirable that a fabric be bac¬ teriostatic and/or fungistatic as well as water resistant. Treated fabrics having these combined properties would be extremely well suited for use in the manufacture of mattres tickings for use in institutions such as hospitals or pri¬ sons. Of course, a fabric employed as a mattress ticking for institutional use must also be resistant to the extreme wear associated with institutional usage. The A.C.A. striped ticking mentioned above has acceptable wear re¬ sistance properties. However, the chemical resistance of this fabric is poor and, therefore, its flame retardance deteriorates as a result of exposure to conventional clean¬ ing processes. U.S. Patent No. 3,279,986 discloses a coated fabric which has acceptable wear properties, is flame re¬ tardant, and is also resistant to chemical attack. The fabric disclosed by this reference comprises a nylon scrim- coated or laminated on both sides with a flexible sheet of polyvinyl chloride which incorporates about 0.10 to 0.60% of a bis-(tri-n-alkyltin) sulfosalinsylate bacteriocidal compound. However, due to the relatively large amount of polyvinyl chloride employed by the polymeric vinyl layers of this product, when exposed to a direct flame the vinyl layer chars and releases relatively large amounts of toxic fumes. Fiberglass fabrics and wools have been employed in the manufacture of fireproof mattress pads. See, U.S. Patent Nos. 2,632,187 and 2,801,427. U.S. Patent No. 2,801,427 (hereinafter '427) discloses a fireproof bed pad or mattress cover comprised of an inner layer of aluminum foil sandwiched between two insulating layers formed from a mineral wool of fiberglass. The outermost surface layer of the mattress pad described by this reference is comprised of a waterproof cloth. U.S. Patent No. 2,632,187 (hereinafter '187) discloses a fire resistant and water repellant mattress pad comprised of a thick inner fiberglass batting layer contained between a facing or upper layer of fiberglass cloth, and a backing layer of cotton fabric. Although the fiberglass layers of the mattress pads disclosed by the *427 and '187 patents are flame re¬ tardant and flame resistant, the outer cloth layers of the mattress pads disclosed by these references provide a poten tial source of flammable material which could be hazardous in the event of fire. Woven or matted fiberglass coated with lacquer coating compositions have also been employed in the manu¬ facture of window shades which are resistant to deteriora- tion by sunlight, water, heat and cold. See U.S. Patent No. 2,381,542 (hereinafter '542). The fiberglass coatings dis¬ closed by the '542 patent are prepared from cellulose de¬ rivative fiber formers and do not include fire retardants, fungicides or bacteriocides. . In addition to fiberglass coated window shades, it is also known to coat thin fiberglass sheets with poly¬ ester. The coated fiberglass sheets are bonded as a laminat to printed circuit sheets formed from copper. " It is also known to coat burlap fabrics suitable for use as wall coverings with flame retardant coating com¬ positions. In particular, burlap fabrics have been coated ' with a fire retardant plasticized polyvinyl chloride based coating composition containing antimony pentaoxide. Although the prior art discloses coated ' fabrics* the prior art does , not provide a chemically coated fiberglass fabric which is flame retardant, fungistatic, bacteriostatic impermeable to liquids such as water or urine, ..-resistant to chemical attack, and which does not release dangerous amounts of toxic fumes when it burns. Accordingly, it is an object of the present in¬ vention to provide a coated fiberglass fabric which possesse each of the properties listed above. It is also an object of the present invention to provide a fiberglass based mattress ticking or cover possess ing each of the properties listed above, and which is par- ticularly well suited for use on mattresses employed in institutions such as hospitals or prisons or for commercial use in hotels, or in other settings where extreme usage con ditions prevail. BRIEF DESCRIPTION OF THE INVENTION In accordance with the foregoing objectives, the present invention provides a coated flame retardant, water impermeable, bacteriocidal arid fungicidal, hypo-allergenic, non-abrasive and chemically resistant mattress ticking com- prised of a woven or non-woven fiberglass fabric, a first layer of a polymer based coating composition, said coating composition comprising a polymeric carrier selected from the group consisting of polyvinyl chloride, polytetrafluoro ethylene, neopreme, polyvinyl chloride acetate copolymer, ethylene vinylidine chloride, acrylic vinyl chloride latex, vinyl chloride acrylic polymers, chlorosulfonated polyether acrylic homopolymers or copolymers, and silicone rubbers; and said polymeric carrier containing an effective amount of a flame retardant and a fungicide and bacteriocide; wherein the amount of said coating composition comprising said first coating layer is adapted to render said fiber¬ glass fabric substantially impermeable to liquids and re¬ sistant to bacteria and fungi; and a second surface coating layer on said first coating layer, said second coating laye comprising a polymeric carrier containing an effective amou of a fungicide and bacteriocide, wherein said surface coat¬ ing layer is adapted to provide a non-abrasive, bacterio¬ cidal and fungicidal surface on said mattress ticking. The present invention also provides a coated fabric which is suitable for use in the manufacture of furniture upholstery, drapery, mattress pads, mattress covers, mattress ticking and the like comprising .a woven or non-woven fiberglass fabric, a coating layer of a polyme based coating composition; said coating composition com- prising a plasticizer, an effective amount of a flame re- tardant, and an effective amount of fungicide and bacterio cide, wherein the amount of said coating composition com--- prising said coating layer is adapted to render said fiber glass fabric impermeable to liquids and resistant to bac- teria and fungi. DETAILED DESCRIPTION OF THE INVENTION The chemically coated fabric of this invention comprises a woven or non-woven fiberglass fabric base to which one or more thin layers of a polymeric coating have been applied. The fiberglass fabric base is inherently fir retardant. In addition, the coating is fire retardant, and renders the fiberglass fabric base impermeable to liquids such as urine, as well as bacteriostatic and/or fungistatic The coating layer is also chemically resistant and, hence, the coating does not deteriorate as a result of exposure to conventional cleaning processes. The fabric base may comprise any conventional woven or non-woven fiberglass fabric. However, the par¬ ticular fiberglass fabric selected will depend upon the end use intended for the coated fiberglass fabric product. For example, for the preparation of the mattress ticking of thi invention, a fiberglass fabric having a tensile strength in the range of from about 150 lbs./sq. inch to about 292 Ibs./sq. inch is employed. Preferably, the woven or non- woven glass fabric employed to prepare the mattress ticking of this invention has a tensile strength of about 250 lbs./ sq. inch. Fiberglass fabrics having tensile strengths in the ranges indicated exhibit the degree of elasticity and resistance to tear considered desirable for commercial mattress tickings. A particularly suitable fiberglass fabric for - use in the manufacture of mattress tickings is a fiberglass fabric which is woven in a Jacquard weave. It has been found that the Jacquard weave functions to enhance the strength of fiberglass fabrics. The fiberglass yarn from which the Jacquard fabric may be woven is a single ply. C-fiber yarn which is one turn out-of-twist and has a Genier of 75. During the weaving process one 42 inch warp is wound around four beans of 2 x 523 and 2 x 524 ends, and a 12- harness weave is employed to provide the Jacquard pattern. The fabric has a weight of about 8.71 ounces per yard, and about 1.56 yards per pound. Fiberglass fabrics of this type are commercially available from the Clark-Schwebel Fiber Glass Corporation of White Plains, New York under the style designation number 487/2/42. The coating layer which is applied to the fabric base comprises a polymeric carrier which contains one or more component ingredients which contribute to the flame retardance of the coating, such as antimony, pentaoxide and/ or antimony trioxide. The coating formulation may also contain an effective amount of a plasticizer, and a filler as well as one or more bacteriostatic and/or fungistatic agents. Preferably, the filler also functions as a flame retardant. Suitable polymeric carriers include chlorine con¬ taining polymers such as polyvinyl chloride, polyvinyl chloride acetate copolymer, acrylic vinyl chloride latex or ethylene vinylidine chloride polymers. Suitable ethylene vinylidine chloride polymeric carriers are commercially available from the Air Products Corp. under the tradename Air Flex 45-14. Alternatively, the polymeric carrier may be polychloroprene (i.e. neoprene) ; chlorosulfonated poly¬ ethers such as Hypalon ® which is commercially available from Dow Chemical Co., or silicone rubber. The polymeric carrier may also be comprised of a vinyl chloride acrylic copolymer or an acrylic homopolymer or copolymer, or poly- tetrafluoroethylene. However, the preferred polymeric carrier is an acrylic vinyl chloride latex which is com¬ prised of a carboxylated copolymer of vinyl chloride and a softer acrylic which self cross-links upon curing. Poly " /^BU RE4 £ mers of this type are commercially available"from the B. F. Goodrich Co. of Akron, Ohio under the chemical product de¬ signation No. 460X2. Any conventional plasticizer which is compatible with the other components of the coating formulation may be employed. For example, suitable plasticizers include the phosphate plasticizers such as para-tricresyl phosphate or octyldiphenyl phosphate. Para-tricresyl phosphate is a colorless liquid which in addition to functioning as a plasticizer also contributes to the water impermeability and flame retardance of the coating. The plasticizer may also be comprised of a chlori nated or brominated paraffin compound which in addition to improving the "hand" of the coating, functions to aid in the flame retardant properties of the polymeric carrier. Preferred plasticizers of this type are the chlorinated paraffins having about a 50% chlorine content. The coating formulation may also include an in¬ gredient such as aluminum trihydrate which contributes to the flame retardance of the coating. When exposed to heat, aluminum trihydrate releases water vapor and, hence, func¬ tions as a flame retardant. The primary fire retardant component employed in the coating is antimony trioxide and/or antimony pentaoxide. These compounds impart fire retardant properties to the coating when employed in combination with the chlorine or bromine containing compounds of the coating formulation, in the proportions described. The antibacterial arid/or antifungal properties of the coating are provided by including a bacteriostatic and/ or fungistatic agent in the coating formulation. Any con¬ ventional, bacteriocide and/or fungicide which is compatible with the polymeric carrier and the other components of the formulation may be employed, e.g. bis (tri-n-alkyltin) sulfosalisylates disclosed in U.S. Patent No. 3,279,986. However, the preferred bacteriocide and fungicide is N-tri- chloromethylthio-4-cyclohexene-l,2-dicarboximide. The bacteriocidal and fungicidal properties of N-trichloro- methylthio-4-cyσlohexene-l,2-dicarboximide may also func- tion to prevent the stiffening of the coating due to plas¬ ticizer depletion caused by the activity of bacteria and fungi. This compound is commercially available from R. T. Vanderbuilt, Inc., 20 Winfield Street, Norwalk, Connecti¬ cut, and is marketed under the tradename Vancide ® 89. In order to function effectively as a fungicide and in particular to prevent unsightly mildew and bacterial growth, the fungicidal and/or bacteriocidal component must migrate to the surface of the coating layer. The rate of migration of the fungicidal and/or bacteriocidal component is determined by the compatibility of the component in the coating formulation. If this component does not migrate at a proper rate, an effective concentration of the active in¬ gredient will not be present at the surface of the coat¬ ing layer. On the other hand, if the migration of the fungicide and/or bacteriocide is too rapid, unsightly blooming of the component on the surface of the coating layer will occur. In accordance with the coating formula¬ tion of this invention from about .5 to 2 parts, and pre¬ ferably about 1 part of a fungicide and bacteriocide (based on 100 parts of the polymeric carrier) such as N-trichloro- methylthio-4-cyclohexene-l,2-dicarboximide is employed. At this concentration level the fungicide and bacteriocide are compatible with the other components of the formulation, and a concentration of the ingredient on the surface of the coating which is effective against fungi and bacteria is provided. Preferably the coating formulation contains, based on 100 parts of the polymeric carrier, from about 25 to 75 parts of the filler (e.g. aluminum trihydrate) , from about 5 to 25 parts of the plasticizer, from about 3 to 10 parts of antimony trioxide or antimony pentao ' xide, and from about .5 to 2 parts of the bacteriocidal and/or fungicidal agent. Preferably, the polymeric carrier is an acrylic vinylchloride latex, the filler is aluminum trihydrate, the plasticizer is a chlorinated paraffin having about a 50% chlorine content, and the bacteriocide and fungicide is N-trichloromethylthio-4-cyclohexene- 1,2-dicarboximide. For example, the coating formulation may comprise on a dry-weight basis about 140 parts acrylic vinyl chlorine latex, about 56 parts aluminum trihydrate, about 6 parts antimony pentaoxide, about 30 parts of a chlorinated paraffin (50% chlorine) and about 1.7 parts of N-trichloromethylthio-4-cyclohexene-1,2-dicarboximide. The coating formulation is prepared by first mixing together the polymeric carrier, antimony pentaoxide and aluminum trihydrate in the form of about 50% disper¬ sions of each of the components in water. Although aqueous solvent systems are preferred since they do not present the environmental hazards associated with more volatile solvent systems, other compatible solvent systems may be employed. Moreover, plastisoles of polyvinyl chloride or vinyl chloride acetate may be employed. Preferably, before being dispersed in water, the aluminum trihydrate is ground in a mill until the average particle size of the aluminum trihydrate is less than about 10 microns. The aluminum trihydrate is then dispersed in water in the presence of about 1% by weight (based on the dry weight of the aluminum trihydrate) of a dispersing agent. Suitable dispersing agents include the nonionic dispersing agents, or trisodium phosphate or any other compatible dispersing agent. The plasticizer and bacteriocide and/or fungicide are then added to the aqueous dispersion of the polymeric carrier, fire retardant and aluminum trihydrate. Prior to coating the formulation onto the fabric base, the viscosity of the formulation is adjusted through the addition of a suitable thickener . The viscosity to which the formulation is adjusted will be determined by the particular coating method employed. Suitable thickeners include methylcellu- lose, high molecular weight acrylic acids , or preferably a nonionic thickener such as Carbopol which is commercially available from the Union Carbide Corporation. After the viscosity of the formulation has been ad justed, the pH of the formulation is adjusted to below about 7. 0 , and preferably within the range of from about 5.5 to - 6. with acid or base as required. Preferably the acid employed for pH adj stment is acetic acid and the preferred base is aπmαnia. Any conventional coating process may be employed to apply the coating formulation onto the fabric base. For example, a • floating knife process , a knife over-roll process, or a reverse-roll coating process may be employed. For use in a floating knife coating process , the viscosity of the formulation should be adjusted through the addition of -a thickener to from about 4 , 000 to 16 , 000 centipoises , and preferably about 16 , 000 centipoises . When a knife over-roll coating process is employed, the viscosity of the formulation is preferably adjusted from about 50 , 000 to 60 , 000 centipoises . For use in a re¬ verse-roll coating process the viscosity of the formulation is preferably adjusted to from about 4 , 000 to 5 , 000 centi- poises. The preferred coating process for use in applying the coating foπrmlation to the fiberglass fabric base is the floating knife process, • wherein the viscosity of the coating formulation is adjusted to about 16,000 centipoises through the addition of about 1. 6 parts of the thickener (on a dry weight basis) to the coating formulation. Upon application to the fabric base, the coatings are cured by passing the coated fabric through an oven at a temperature of about 325 β F. The coating may be applied to one or both sides of the fiberglass fabric base. The weight of the coating applied should not exceed about 6 ounces per square yard of fabric, nor be less than about 1 ounce per square yard. Preferably the weight of coating layer applied is about 2 to about 3 ounces per square yard of the fabric base. The coating layer adheres well to the fiberglass fabric base and does not require' auxiliary adhesion promo¬ ters. However, adhesion promoters may be included in the coating formulation, and their use may be desired where particularly adhesion resistant fiberglass fabrics are utilized. Useful adhesion promoters include N-(β-amino- ethyl-γ-aminopropyl)-trimethoxy silane. Adhesion promoters of this type are commercially available from the Union Carbide Corp. under the produce designation A1120. When the polymeric carrier of the coating cαπposi- t tion is a latex type carrier, such as the acrylic vinyl ' chloride latex carrier discussed above, the surface texture of the cured fabric coating may be tacky or sticky. The surface of the cured fabric coating is finished by applying additional coating layers of a polymeric material to the cured coating layer. The outer coating layer provides a smooth and abrasion resistant surface on the fabric surface. For example, a thin finishing layer of a vinyl chloride acrylic compound may be applied to the fabric by any of the coating processes discussed above. In order to insure the presence of an effective amount of the fungicide and/or bacteriocide on the surface of the fabric coating, an ef¬ fective amount of a fungicide and/or bacteriocide may also be included in the composition employed as the surface coat¬ ing layer. For example, about 1 part by weight of N-tri- chloromethylthio-4-cyclohexene-l,2-dicarboximide may be in- eluded in the foππulation employed as the surface coating layer. The surface coating layer is preferably employed in an amount of from about .1 to about .5 ounces per square yard of fabric. However, the amount of material coated onto the first cured coating layer will depend to a great extent upon the particular coating material employed, and the sur- ' face textures desired. Preferably, however, " the coating material employed is a vinyl chloride acrylic polymer which is coated onto the first fabric coating layer in an amount of about .25 ounces per square yard. Moreover, the total weight of the first and second coating layers preferably should not exceed about 6 ounces per square yard of the fabric base. Vinyl chloride acrylic compounds suitable for use as the surface coating layer are commercially available from the B. F. Goodrich Company, under the chemical product designation number 460X1. The invention will be described further-with re¬ ference to the following detailed Examples. EXAMPLE 1 A coating formulation was prepared containing on a dry weight basis: Parts Acrylic Vinyl Chloride Latex 140 (460X2 - B. F. Goodrich Co.) Aluminum Trihydrate 56 Antimony Pentaoxide 6 Chlorinated Paraffin Plasticizer 30 (50% Chlorine) Vancide 89 1.7 (N-trichloromethylthio-4- cyclohexene-1,2-dicarboximide) The formulation is prepared by mixing together a 50% aqueous dispersion of the acrylic vinyl chloride latex and a 50% aqueous dispersion of the antimony oxide. Prior to adding the aluminum trihydrate, the compound is ground in a mill until the. average particle size is about 5 microns A 50% aqueous dispersion of the milled aluminum trihydrate is prepared by dispersing the compound in water in the pre¬ sence of about 1% by weight of trisodium phosphate. The aqueous dispersion of the aluminum trihydrate is then added to the aqueous dispersion of the polymer and the antimony oxide. " Thirty parts of a chlorinated paraffin (60% chlorine 13 content) plasticizer, and 1.7 parts of N-tric ' hloromethylthi 4-cyclohexene-l,2-dicarboximide are then added to the aqueo dispersion of the other ingredients, and the formulation is mixed in a high speed mixer until uniform. " The viscosity of the formulation is adjusted to about 16,000 centipoises through the addition of about 1.6 parts by weight of Carbopol®. The pH of the formulation is then adjusted to preferably within the range of from about 5 to 6.5 through the addition of acetic acid. The coating formulation is applied to a fiberglass f bric base by a floating knife coating process. The fabric base is a Clark-Sσhwebel ' . Fiber Glass Corp. (Style No. 487/2/42) fiberglass fabric which is woven in a Jacquard weave.. The fabric is woven from a C-fiber which is one turn out-of-twist and has a Denier of about 75. The coating layer is applied to both sides of the fabric in one or sever al passes in a weight of about 3 ounces per square yard of fabric, and the coating is cured by passing it through an oven at a temperature of about 325°F. A surface coating formulation is prepared by adding 1.7 parts of N-trichloromethylthio-4—cyclohexene-1,2- dicarboximide to a 50% aqueous dispersion of 140 parts of a vinyl chloride acrylic polymer (B. F. Goodrich 460X1) . The mixture is then thoroughly blended, and the viscosity is adjusted to about 16,000 centipoises through the addition of Carbopol®. The pH is adjusted with acid to about 6.5. The surface coating formulation is applied to the cured coated fabric described above. About .25 ounces of the surface coating is applied per yard of fabric treated. The coating is cured by passing it through an oven at about 325 β F. The coated fiberglass fabric has a non-abrasive and abrasion resistant surface. Moreover, the coated fabric prepared in accordance with this example is flame retardant, and is also resistant to conventional chemical cleaning agents. Due to the inclusion of an effective"amount of a bacteriocide and fungicide in the coating layers, the fabric product will not support fungi growth and is resistant to both gram negative and gram positive bacteria. Thus, the fabric is free of the odors associated with the presence of bacteria or fungi. Moreover, the coating layers render the fabric entirely impermeable to liquids. EXAMPLE 2 A mattress is prepared from the coated fabric pro- duct of Example 1, by sewing the fabric about a conventional mattress unit. For example, the mattress unit may comprise a box spring mattress unit, an inner spring unit, or foam rubber. The mattress employing the mattress ticking of this invention has a smooth, non-abrasive surface, not generally associated with fiberglass fabrics. The coated fiberglass ticking is also hypo-allergenic. The durability and other properties which inhere in the coated fabric of this invention render mattress tickings, and mattresses . employing them ideally suited for use in institutions or in other settings where extreme usage conditions prevail. In order to evaluate its flame retardant property, a mattress employing the mattress ticking of Example 1 was wrapped around an inner core of newspapers and drenched in gasoline. The newspapers were ignited in order to evaluate the flame retardant property of the mattress. After the fire was naturally exhausted due to consumption of the news¬ paper filler, the mattress was unwrapped, and the surface of the mattress ticking was examined. The .mattress ticking was entirely free. of char, and only a very slight discoloration was noted on the ticking surface. While specific embodiments of the coated fiber- • glass fabric of this invention have been described with particularity herein, it should be understood that this in- vention is intended to cover all changes and modifications of the embodiments of the invention chosen herein for pur¬ poses of illustration, which do not constitute departures from the spirit and scope of the present invention.

Claims: CLAIMS; 1. A coated fabric comprising a woven or non- woven fiberglass fabric having a coating layer of a polymer based coating composition, said coating composition com- prising an effective amount of a flame retardant, and an effective amount of a fungicide and bacteriocide, wherein the amount of said coating composition comprising said coating layer is adapted to render said fiberglass fabric impermeable to liquids and resistant to bacteria and fungi. 2. The coated fabric according to Claim 1 wherein said polymer based coating composition comprises about 100 parts of a polymer selected from the group consisting of the polyvinyl chlorides, polytetrafluoroethylenes, neoprenes, polyvinyl chloride acetate copolymers, ethylene vinylidine chlorides, an acrylic vinyl chloride latex, vinyl chloride acrylic polymers, chlorosulfonated polyethers, acrylic homopolymers or copolymers, and silicone rubbers; from about 3 to about 10 parts of a flame retardant which is antimony trioxide or antimony pentaoxide, about .5 to 2 parts of a bacteriocide and fungicide; and said composition further com¬ prising from about 25 to about 75 parts of a filler which is aluminum trihydrate. 3. The coated fabric according to Claim 2 wherein said polymer is an acrylic vinyl chloride latex, said bac- teriocide and fungicide is N-trichloromethylthio-4-cyclo- hexene-1,2-dicarboximide; said filler is aluminum trihydrate, and said coating composition also includes from about 5 to about 25 parts of a plasticizer which is a chlorinated paraf¬ fin compound having about a 50% chlorine content, and said coating layer comprising from about 1 to about 6 ounces per square yard of said fabric. 4. The coated fabric according to Claim 2 wherein said polymer is neoprene. 5. The coated fabric according to Claim 3 wherein said fiberglass fabric is woven in a Jacquard weave from a ' single ply C-fiber fiberglass yarn. 6. The coated fabric according to Claim 5 where said fabric further includes a surface coating layer on sai polymer based coating layer, said surface coating layer bei comprised of a polymeric carrier containing an effective amount of a fungicide and bacteriocide, said surface coatin layer being adapted to provide a non-abrasive, fungicidal and bacteriocidal surface on said fabric. 7. The fabric according to Claim 6 wherein said surface coating layer is comprised of a vinyl chloride acrylic polymer containing an effective amount of N-tri- chloromethylthio-4-cyσlohexene-l,2-dicarboximide, and where in said surface coating layer comprises about .25 ounces pe square yard of said fabric, and wherein the combined weight of said polymer based coating layer and said surface coatin layer comprises from about 1 to about 4 ounces per square yard of fabric. 8. A flame retardant, water impermeable, bac¬ teriocidal and fungicidal, hypo-allergenic , abrasion-resis- tant, non-abrasive and chemically resistant mattress ticking or cover comprised of a woven or non-woven fiberglass fabric a first coating layer of a polymer based coating composition said coating composition comprising a polymeric carrier se¬ lected from the group consisting of the polyvinyl chlorides, polytetrafluoroethylenes, neoprenes, polyvinyl chloride acetate copolymers, ethylene vinylidine chlorides, an acryli vinyl chloride latex, vinyl chloride acrylic polymers, chlorosulfonated polyethers, acrylic homopolymers or co¬ polymers, and silicone rubbers; and said polymeric carrier containing an effective amount of a flame retardant, and an effective amount of a fungicide and bacteriocide; wherein the amount of said coating composition comprising said first coating layer is adapted to render said fiberglass fabric substantially impermeable to liquids and resistant to bac- teria and fungi; and a second surface coating layer on said first coating layer, said second coating layer comprising a polymeric carrier containing an effective amount of a fungicide and bacteriocide, wherein said surface coating layer is adapted to provide a non-abrasive, bacteriocidal and fungicidal surface on said mattress ticking. 9. The mattress ticking according to Claim 8 wherein said fiberglass fabric is woven in a Jacquard weave from a single ply C-fiber fiberglass yarn. 10. The mattress ticking according to Claim 8 or 9 wherein said first coating layer comprises about 100 parts of said polymeric carrier; from about 5 to about 25 parts of a plasticizer; from about 3 to about 10 parts of a flame retardant which is antimony trioxide or antimony pentaoxide, and said first coating layer further comprising from about 25 to about 75 parts of a filler; said first coating layer comprising about 1 to about 6 ounces per square yard of said fabric. 11. The mattress ticking according to Claim 9 wherein said first coating layer comprises about 100 parts of acrylic vinyl chloride latex, containing from about 5 to about 25 parts of a chlorinated paraffin plasticizer having about a 50% chlorine content; from about 5 to about 10 parts of a flame retardant which is antimony trioxide or antimony pentaoxide; and from about .5 to about 2 parts of a fungicide and bacteriocide which is N-trichloromethylthio- 4-cyclohexene-l,2-dicarboximide; and from about 25 to about 75 parts of aluminum trihydrate filler; and wherein said surface coating layer comprises a vinyl chloride acrylic polymer containing an amount of N-trichloromethylthio-4- cyclohexene-1,2-dicarboximide which is effective against fungi and bacteria, said surface coating layer being pre¬ sent in an amount effective to provide a smooth and non- abrasive surface on said mattress ticking. 12. The mattress ticking according to Claim 10 wherein said first coating layer comprises on a dry-weight 19 basis about 140 parts of an acrylic chloride latex, about 56 parts of aluminum trihydrate having an average particle size of about 5 microns, about 6 parts of antimony trioxide and about 30 parts of a chlorinated paraffin plasticizer having about a 50% chlorine content, said first coating layer comprising about 3 ounces per square yard of said fabric layer; ' and said surface coating layer comprising about 140 parts of a vinyl chloride acrylic polymer containing about 1.7 parts of N-trichloromethylthio-4-cyclohexene-l,2- dicarboximide; said surface coating layer comprising about .25 ounces per square yard of said fabric layer. 13. The mattress ticking according to Claim 10 wherein said polymer is neoprene. 14. A mattress comprising the inner mattress unit and an outer mattress ticking, wherein said mattress •ticking is of the mattress ticking of Claim 8, 9, 12 or 13. 15. A mattress comprising an inner mattress unit and an outer mattress ticking, wherein said outer ticking is the mattress ticking of Claim 10. 16. A method of making a mattress ticking or cover which is flame retardant, water impermeable, bacterio¬ cidal and fungicidal, hypo-allergenic, abrasion resistant, non-abrasive, and chemically resistant which comprises the step of coating from about 1 to about 6 ounces per square yard of a first layer of a polymer based coating composi¬ tion onto the surface of a woven or non-woven fiberglass fabric; said coating composition comprising a polymeric carrier selected from the group consisting of the polyvinyl chlorides, polytetrafluoroethylenes, neoprenes, polyvinyl chloride acetate copolymers, ethylene vinylidine chlorides, an acrylic vinyl chloride latex, vinyl chloride acrylic polymers, chlorosulfonated polyethers, acrylic homopolymers or copolymers, and silicone rubbers; and said polymeric carrier containing a plasticizer and an effective amount of flame retardant, and an effective amount of a fungicide and/ or bacteriocide; coating onto said first coating layer a surface coating layer; said surface coating layer compris¬ ing a polymeric carrier containing an effective amount of a fungicide and/or bacteriocide, said surface coating layer being adapted to provide a non-abrasive, bacteriocidal and/ or fungicidal surface on said mattress ticking.

Inventors: FERZIGER D, LIPPMAN J
Applicants: FERZIGER D, LIPPMAN J
Application year: 1981
Main classification: B32B17
IPC codes: A47C27, A47C31, B32B19, B32B27, C03C25, D06M11, D06M15, D06M101