DISPERSION PROCESS AND PRODUCT

Abstract: Preparation of aqueous dispersions of film-forming polymer particles wherein the dispersions comprise both pre-formed polymer and polymer formed in situ, and to the use of these dispersions in coating compositions which can be applied by cationic electrophoresis. Previous dispersions of the general type hereinabove described can be cationically electrodeposited but do not give films of adequate integrity and adhesion. The present invention overcomes these drawbacks by using a process wherein (a) pre-formed polymer or polymer plasticiser is dissolved in polymerisable monomer and the resulting solution stably dispersed in water in the presence of a surface active agent, and (b) the monomer is polymerised to give a particulate dispersion. Prior to polymerisation the dispersion must comply with specific pH requirements involving ensuring instability within the pH range 10-11 and the surface active agent must be cationic and have an H.L.B. value of at leat 8.

Description: DISPERSION PROCESS AND PRODUCT Thι.s mventtcn raiates to a process or preparing aqueous dispersions of particles of film- forming polymer , to aqueous dispersions so-prepared and to their use i coating ~~ * couro * _ositions at — O « licabIa to substrates by cationic eiectrophoretic coating processes. In recant years, economic and environment protection pressures have accelerated the-.; development of coating compositions in which the evolution of volatile organic solvents curing the coating process is minimised and preferably eliminated entirely. This has led to the increasing use of water-diiu ble liquid coating compositions and to the establishment of coating processes, for example eiectrophoretic deposition processes, -which inherently limit the amount of volatile organic solvents released into the atmosphere. We use the expression "organic solvents" in the art-reco nised sense of solvents for polymeric film-forming components of the liquid coating compositions. A well-known method of providing water dilutable coating compositions is to produce them in the form of stable aqueous dispersions of film-forming polymer. x i_ι*_z water evaporates from a film of such a composition, the .individual disperse particles of film-forming polymer coalesce to form a .continuous coating film. It is quite common for this type of dispersion to contain organic solvent at concentrations of from 2-5--, of the weight of volatilas, for example to aid coalescence of the film, "when the dispersion is made from ore-formed pciyner, wn---.cn --.s -i≤persεc oy πeci-mic i means in aqueous continuous phase, the practical requirements cf the trαcass may demand the use of higher levels of organic solvent, e.g. 20-25^. of the weight cf volatilas. A particularly valuable type of aqueous polymer dispersion is one i which the disperse particles comprise an addition polymer of , S-ethyl nically unsaturated monomer. This addition polymer may be the sole film-forming, polymer in the dispersion, but to meet various performance criteria, for example to meet a specified balance of minimum filming temperature, flexibility and durability, it may be necessary to blend with the addition polymer a modifier, for example a polymer plasticiser or a polymer having different physical characteristics from the said addition polymer. It has been recognised that to achieve the best results with such mixed systems, the blending should take place within each disperse particle, as distinct from just mixing the addition polymer dispersion with a separate solution or dispersion of modifier. Methods of preparing dispersions of that general type, which also avoid the necessity of " introducing organic solvents into the -system, are disclosed in, for example, British Patent Specifications Nos.1,417,413 and 1,421,114 which describe thermos ttable synthetic addition polymer solutions and .British Patent Specification No.1,515,723 which describes dispersions of thermoplastic polymer solutions. A simple process of that type is one in which a modifier, which may be pre-formed polymer or polymer plasticiser-, or both, is dissolved in ethylenicaily unsaturated monomer and the solution stably dispersed in particuiatε form in water. Polymerisation of monomer is initiated to form in situ in the disperse particles an intimate blend of addition polymer and pre-formed modifier. We are concerned in this invention with the cathodic electrodeposition of polymer onto a substrate from aqueous dispersions prepared broad!v along these lines from pre-formed modifier and ethylenically unsaturated monomer. However, we are not limited for our purpose to the particular polymers or proportions disclosed in the afore- said patent specifications. The general principles of the electrodeposition process itself are well publicised and the technique is widely used. industrially. The article to be coated is made a target electrode in a liquid electrically conducting bath. lonically charged coating materials present in that bath are urged to deposit on the target under the influence of an electric current applied to them. In a cathodic electrodeposition process, the coating materials bear a positive charge and deposit at a cathode. Our invention applies to those aqueous polymer dispersions in which the positive charge is imparted to the disperse particles by cationic surface active materials associated with them and which also serve to stabilise the dispersion. While it might appear from the foregoing that any stable aqueous dispersion of that general type would deposit coating films of adequate integrity and adhesion at a cathode, we have observed that this is not so. In practice, we have found that the pH stability of the dispersion prior to polymeri ation of ethylenically unsaturated monomer is a critical step in preparing suitable dispersions for use in this way. We have made the surprising discovery that while the aqueous dispersion of pre-formed modifier and ethylenically unsaturated monomer must be stable at the pH at which it is prepared, it must become unstable at pH 10-11 if subsequent polymerisation is to yield useful cathodically cepositable compositions. According to the present invention we now disclose a process of preparing an aqueous dispersion of particles of film-forming polymer suitable for use in a cathodic electrodeposition process, the said process consisting of the following steps in combination: (1) Pre-formed polymer or polymer plasticiser dissolved in polymerisable a , β-ethylenically unsaturated monomer which has a maximum solubility in water of 10% by weight at 25°C is stably_. dispersed in water in the presence of surface active agent; and (2) unsaturated monomer in the dispersion is polymerised to form a particulate dispersion of f lm-forming polymer wherein the particles comprise blends of pre-formed polymer or polymer plasticiser and polymer formed in situ from the unsaturated monomer; characterised in that the stable dispersion in water prior to the initiation of polymerisation has a pH of less than 10 but when subjected to the pH stability test described hereinunder becomes unstable at a pH of 10-11 and the surface active agent is a cationic surface active agent which has a hydrophilic-lipophilic balance (H.L.B. value) of at least 8. As indicated above, a critical factor in the manufacture of aqueous dispersion by our process, is the stability of the aqueous dispersion prior to pol3τmerisation of monomer and within the pH range of 10-11. One method of observing this is to add five drops of the dispersion taken prior to the initiation of polymerisation (about 0.15g) to sample tubes containing lOg of ce-ionised water. One diluted sample so-produced _9 is treated with 10 >i potassium hydroxide solution to give a PH of 10-11 and allowed to stand, together with an un-treated diluted sample, for 10 hrs at 25°C. Instability at the high pH is indicated if there is a visible settling of polymer, with the formation of a clear upper layer, in the test sample after that time. The un-treated diluted sample should show little if any settling under the test conditions and is used as a control in assessing the degree of stability of the test sample. • ■ Our experience has shown, however, that the test for pH stability is more accurately and more reproducibly performed if ; it is carried out at a constant sample concentration of monomer and pre—formed polymer/polymer plasticiser and we have chosen to standardise- on a figure of 15% by weight. This is a satisfactory concentration for accurate results and being below the concentration usually selected for dispersion preparation, readily achievable by dilution of a batch sample. If much greater dilutions of test samples are used, interpretation of the results becomes less certain and while all dispersions which pass will work according to our invention, it is possible to overlook useful compositions if the testing concentration is, for example, below 1% by weight: For the best results , our pH stability test is carried out in the following manner. Five ml of the • sample of dispersion taken " prior to the initiation of polymerisation is diluted in a sample tube with de-ionised water to a concentration (monomer and pre-formed polymer/ polymer plasticiser) of 15% by wt. One molar potassium hydroxide solution is added dropwise to bring the pH to 11 (typically about 0.5 ml). The sample is allowed to stand for at least 2 hours together with an untreated sample. Instability at pH 11 is indicated if there is visible separation of the test liquid into two layers. Separation m / be limited after two hours but is usually complete giving two clear layers after 24 hours. An — '- — untreated sample should show little if' any separation- under those-, test, conditions. As will be discussed further hereinunder, it is not necessary that our process be carried out by first 5 dissolving the pre-formed polymer/polymer plasticiser in all of the monomer to be polymerised; although this may be done. For the purpose of this pH stability test, it is to be :understood that when some variation of that basic method is used, the test is, however to be carried 10 Q -__ on a. sample prepared in just that way. ' That is pre-formed polymer/polymer plasticiser is dissolved in the total amount of poiymerisable monomer to be used in the preparation and dispersed in water in the presence of the surface active agent then tested according to the 2-5 pH stability test as described hereinabove. The test sample must be free of polymerisation initiator. Our process imposes no inherent limitations on the choice of pre-formed polymer or polymer plasticiser other than that it must be soluble in the , S-ethylenically 20 unsaturated monomer in the relative proportions required in the final composition. The solution need not be completely free of any turbidity, provided it shows no obvious tendency to separate into two phases before the particulate dispersion is formed. Δ - 1 The actual choice of pre-formed polymer or polymer plasticiser is related to -the nature of the unsaturated monomer and the intended properties of the composition as a whole. For example, if the dispersion is intended to SO provide a thermoplastic coating film, the pre-formed polymer may be a thermoplastic polymer which has a glass transition temperature (Tg) significantly different from that of the polymer to be formed in situ. That is, depending on the relative physical characteristics and proportions of the two types of polymer present in the disperse particles, the effect of the pre¬ formed polymer may be, for example, to modify the hardness or to improve the flexibility and toughness 5 of coating films formed therefrom by cathodic electro¬ deposition. The pre-formed polymer may, but need not, be a single polymeric entity. It may be a mixture of two or more polymers, optionally in combination with a 2-0 polymer plasticiser, which imparts the desired properties to the pre-formed polymer component as a whole. The polymer plasticiser for use in these compositions may be, for example, a relatively involatile low molecular weight ester or epoxide plasticiser. -^ Other suitable materials include, for example, those compounds referred to as polyester plasticiser. There are few constraints on the choice of polymer to be formed in situ. However, because the composition as a " whole is to provide thermoplastic films, the. 0 polymeric components of the dispersion must be free of functional groups which would render them, either singly or in combination, thermosetting at the desired temperature of film formation. We exclude double bonds from our understanding of functional groups as used 5 herein, but it should be borne in mind that during polymerisation of unsaturated monomer it is possible for some cross-linking reactions to occur. Hence, the selection of polymerisation conditions should be made with due regard to eliminating, so far as is practicable, a level of cross-linking detrimental to the subsequent coating film formation. In the embodiment of our invention which is intended to provide thermoset coating films, the film-forming _ a _ ooivmer must be inherently thermosettable. That is the pre-formed polymer, polymer formed in situ or both of them must contain reactive groups capable of entering into a cross-linking reaction. In addition, the composition as a whole must contain the means of carrying out that cross-linking reaction. This may be accomplished in a number of ways. For example, the pre-formed polymer may contain reactive groups and complementary reactive groups which will enter into the required crosslinking _ reaction. The reactive and complementary reactive groups may be on the same polymer or on different polymers. That is the pre-formed polymer can, if desired, be a mixture of two polymers, each of which contains one specific type of reactive group. For example, one polymer may contain hydroxyl groups and the other methylol amide groups. Alternatively, the polymer formed in situ may provide both types of reactive groups either on the same polymer or, for example, in different polymer species built up as a layered structure within the disperse particles. In another embodiment, the pre-formed polymer may provide one type of reactive group and the polymer formed in situ the .complementary 'type.of reactive group. Polymer plasticiser present in the compositions need not necessarily take part in the cross-linking reaction. However, in some cases, for example when the polymer plasticiser is a flexible polyester or epoxiάe condensate, it can be advantageous to have the plasticiser react with and hence be chemically bonded to other polymeric film-for ins components. Thermosetting polymer systems of the above- described types will usually cross-link on heating and/ 01 on the addition of added catalysts. Gross-linking takes place by reaction between the reactive and complementary reactive groups on the film-forming polymers themselves. That is the system is self cross- linking. However, it is well known that many cross-linking reactions take place by the reaction of polymers or polymer precursors containing reactive groups with cross-linking agents bearing complementary reactive groups. Our • invention is equally applicable to such thermosetting systems. The cross-linking agents themselves may be, but are not necessarily, polymeric. Thus, our invention comprehends the use of cross- linking agents which will react with reactive groups in either or both of the pre-formed polymer or polymer formed in situ. In one such system, both. types of polymer may contain the same reactive group and be cross- linked at film formation by a common co-reactive cross- linking agen . The cross-linking agent may be incorporated in either phase of the dispersion. In fact, the choice and location of cross-linking agent is a practical one depending in each case on the nature and source of reactive groups intended to take part in the cross- linking reaction. For example, on the one hand the cross-linking agent may be a di-epoxide which is dissolved in the pre-formed polymer and polymerisable monomer prior to preparation of the dispersion. On the other hand, the cross-linking agent may be a water-soluble polymer containing suitable reactive groups, which is added to the aqueous continuous phase of the dispersion after the dispersion has been prepared. Suitable cross-linking agents for incorporation in our dispersions include, for example, etherified urea- formaldehyde resins, hexamethoxy methyl and other alkoxy alkyl mela ines, eg. "Cymel" (Trade Mark) 1125 and 1141 and blocked isocyanate cross-linking agents as disclosed in, for example, United States patent specification No.3,799,854 and British Patent specification No. 1,303,430. One particularly useful embodiment of our invention is a dispersion in which the disperse particles contain a pre-formed polymer or polymer plasticiser and polymer formed in situ, both of which contain hydroxyl groups, in combination with a cross-linking agent containing complementary reactive groups. For example, the pre-formed polymer or polymer plasticiser may be an epoxy resin derived from epichlorhydrin and diphenylcl propane and the polymer formed in situ an addition compolymer derived from monomer comprising hydroxy ethyl methacrylate, hydroxy- propyl methacrylate or hydroxy isopropyl methacrylate. The cross-linking agent may then be, for example, a butylated urea-formaldehyde resin. The means of formulating both thermoplastic and thermosetting polymers and their use in combination with plasticisers and cross-linking agents are well known to the art. Many typical examples applied to aqueous polymer dispersions are disclosed for example, in the above-mentioned patent specifications, the contents of which are incorporated herein by reference. The selection of surface-active agent to be used in our process is limited in the first place to those cationic materials which have an H.L.3. value of at least 8. In general, any material of this type, can give an aqueous dispersion with our pre-formed polymer/monomer solutions at a pH below 10. However, as described hereinabove, unless that dispersion becomes unstable at a pH of 10-11 under our specified test conditions, the final polymer dispersion does not deposit satisfactory coating films under cathodic electrodeposition conditions. The principles underlying the choice of the most effective surface active agent for use with a particular polymer dispersion are not clear to us. However, it is a relatively straight forward matter to determine this experimentally. The dispersion of pre-formed polymer or polymer plasticiser and polymerisable monomer is formed at a pH of less than 10, the typical useful working range being pH 4-8. An acceptable surface active agent will produce a stable dispersion of particles of the order of 0.5-5.0 μ dia. If the chosen surface active agent does not produce a stable disp _ersion, ~ or one which fails to pass our stability test, we the ' check the effect of using a surface active agent with a different cationic group or H. .B. value. The concentration of surface active agent required is typically of the order of 2-10% based on the weight of disperse particles. However, we are not limited in the performance of this invention to concentrations of that order. For example the selected surface active agent may be polymeric and " contributing significantly to the nature of the ultimate coating film itself. In particular, if the dispersion is intended to provide thermosetting coating films the surface active agent may also contain a suitable reactive group allowing it to take part in the film- orming cross-1inking reaction. - 1 ~ That is, surface active agent required to stabilise the dispersion may be provided, at least in part, by pre-formed polymer or polymer plasticiser comprising stabilising cationic groups and optionally reactive Ogr*oups which subseαuently enter into a film-forming cross-linking: reaction-. The concentration of surface- active agent may then constitute, for example, as much as 40%, or even more, of the total weight of disperse particles. Although the dispersions are essentially stabilised in our process by cationic surface active agents, they may also contain non-ionic surface active agents and may also tolerate the presence of some anionic material. It is also permitted to use a mixture of two or more cationic surface-ac ive agents. The over-riding criterion in all cases is that the dispersion must pass our pH stability test. Surface active agents having an H.L.3 value of at least 8 include, for example, lower alkyl salts of fatty mono- and di-aminas, e.g. the acetate salts of tallow and oleyl fatty primary amines and of a fatty primary amine with a f_t. _γ chain length of 18 covalently bonded carbon atoms. Similar diamines are, for example, the acetate salts of tallow and oleyl propyiene diamine. Some quaternary ammonium compounds also provide satisfactory surface active agents, for example the proprietary product Ξthoquod (Trade Mark) 012. Polymeric surface active agents' inlcude, for example, copcl3rmers of ethylenically unsaturated monomers, the copolπners providing both lipophilic components and cationic groups. Such materials include for example, ccpoiymers of lauryl nethacrylate/methyl methacrylate/hydroxy propyl methacrylate/diethylamino- ethyl methacrylate and 2-ethyl hexyl aerylate/methyl methacrylate/hydroxy ethyl methacrylate/dimethyla ino- ethyl methacrylate; when protonatεd by an acid, e.g. acetic acid. The polymeric surface active agent need not, however, be an addition copol]τmer. A most useful material of this type is, for example, an epσxy- phenol adduct reacted with diethanolamine and activated with acetic acid. Numerous methods have been proposed for the determination of H.L.B. values of surface active agents, several of which are reviewed in Part II of "Emulsions and Emulsion Technology", Marcel Dekker Inc., New York, edited by Kenneth J. Lissant. Particularly in the case of polymeric, cationic materials, most determinations are time-consuming and tedious. For the purpose of this invention, we have found that satisfactory accuracy is given by the approximate determination given on page 740 of that publication. According to that method, the H.L.3. value of a surface active agent is estimated by observing its dispersibiiity in water aided if necessary by first melting or softening it in water, then cooling to room temperature. The formation of a stable, milky dispersion, translucent dispersion or clear solution, approximates to various levels of H.L.B value from 8 upwards. Materials which will not disperse or give poor dispersions in water have lower H.L.B values than are desirable for our purpose. Methods of making aqueous dispersions of polymer solutions are well known and directly applicable to our process. Suitable techniques are described, for example, in the above-mentioned patent specifications, which also exemplify the manner in which polymerisation of monomer in the. disperse particles may be initiated. For example, pre-formed polymer or polymer plasticiser may be dissolved in polymerisable monomer and that solution poured into mechanically agitated water where, 5 in the presence of cationic surface active agent, a stable rticul te dispersion of polymer solution is formed. The surface active agent may be pre-dissolved in the water cr, if suitably soluble, added as a solution in the pre-formed polτ er solution. An -9 alternative method which can be useful when the pre-formed polymer or polymer plasticiser is liquid at the temperature of addition, is to add both that component and the polymerisable monomer concurrently to- the water in the presence of the surface active -5 agent. Dissolving of pre-formed polymer or polymer plasticiser in polymerisable monomer and the formation of liquid disperse particles then proceeds concurrently. A further useful variation is to add the solution in polymerisable monomer continuously over a period of -0 time to water in the presence of the surface active agent and polymerisation initiator. The formation of liquid disperse particles and initiation of polymerisation then takes place concurrently and continuously. When the pre-formed polymer or polymer plasticiser 25 comprises polymeric surface active agent, we usually prefer to dissolve it in part or all of the polymerisable monomer, before proceeding to make the initial aqueous dispersion. It will be apparent from the above description of JU our process, that considerable latitude is available in the manner in which initiation of olderisaticn may be carried out. That is, polymerisation initiator may be added to the solution in pol3-rmerisable monomer, the aqueous phase of the dispersion or to both. Alternatively, in the case of a redox catalyst for example, one component may be segregated into each phase and only become effective when they are mixed. In general we have found that a more stable process results if the complete initiator system is not contained in the polderisable monomer solution. The relative proportions of pre-formed poljπrter or polder plasticiser, cross-linking agent when present and pol f mer formed in situ are selected according to the properties required in the final coating film. Usually, however, the weight of polymer formed in situ will be 20-98% of the total weight of film-forming pol3τmer present. As mentioned hereinabove, our dispersions can be made essentially free of volatile organic solvents. However, if desired, for example to enhance the flow of coating films formed from them, they may be made with a proportion of such solvents present. The aqueous dispersions may be compounded in conventional manner into pigmented coating compositions by the incorporation therein of pigment, anti-corrosive additives and other conventional auxiliary materials. When the dispersions are thermosettable, they may contain accelerators for the crosslinking reaction. Although intended specifically for use in -cationic electrodeposition baths and processes, the aqueous ' dispersions of our process may also be applied to substrates, including non-conducting substrates, e.g. wood and plastics mouldings, by other conventional means, e.g. by spraying, curtain coating, roller coating, dipping or the like. The invention is illustrated by the fallowing examples in which all parts are given 03/ weight: - 15 - EXAMPLE 1 Preparation of an aqueous dispersion ^ of particles of pre-formed polyester resin blended with an addition copol3τmer formed in situ, according to the invention. The polyester resin used in this example was a saturated polrester formulation made from neopentyl glycol, adipic acid, isophthalic acid, terephthaiic acid and trimellitie anhydride. It was dissolved in methyl methacrylate monomer to give a solution containing 82.3% by weight of solid polyester resin. A portion of 60.8 parts of the above solution was thinned further with 14.2 parts methyl methacrylate monomer, 20 parts of butyl acr3late, 5 parts of -(n- butoxymethyl) aery1 mide and 1 part of cumene hydro- peroxide. The solution so-formed was added with stirring to 30 parts of demineralised water containing 8 parts of a tallow propylene diamine acetate salt (Duomac* T - Trade Mark), which has an H.L.B. value of greater than 8. During this addition the batch was stirred at 2500-3000 r.p.m with a disc cavitation stirrer. Stirring was maintained for 10 mn- . A dispersion of pre-formed polymer in polymerisable monomer was formed and this was further diluted by the addition of 200 parts of -demineralised water. The disperse particles had an average diameter of about 1 μm. The dispersion had a pH of 5.2. A sample of the dispersion was subjected both zo the above-described stabilit3r test at 15% solids by weight and to an inspection when five drops thereof were diluted with Ig de-ionised water, adjusted to a pH of 10.5 and allowed to stand for 10 hours at 25°C. In each case, the test sample showed clear evidence of loss of stabilitv, with marked settling of particles. That is, the selected stabiliser was satisfactory for use in our process. A solution of 0.5 parts of sodium ascorbate in 20 parts of demineralised water was stirred into the dispersion to initiate polymerisation. An exother was observed, the batch temperature rising 20 C in 47 mn„.. On completion of pol^erisation, the batch was used as a bath in an electrodeposition process, using phosphated steel panel electrodes and a potential drop of 200 V for 30 seconds deposition time. An even, well-coalesced film of polymer was deposited on and adhered well to the cathode. On removing from the bath and curing by baking for 30 mri at 190°C a smooth, glossy, adherent film was formed. EXAMPLE 2 An attempt was made to repeat the process of example 1, but substituting a blend of surface active agents for the one used in that example. A duplicate solution of pre-formed polymer in polymerisable monomer to that used in example 1 was prepared and added in like manner to an aqueous solution of surface active agent. In this example, the 8 parts of Duo ac T dissolved in 30 parts of demineralised water was replaced by a mixed surface active agent consisting of 8 parts of Duomac T and 5 parts of a nonyl alcohol ethoxylate (4C ethylene oxide units) known as Triton (Trade Mark) N 4Q. That mixture of surface active agents had an HL3 value in excess of 8. A further 16 parts of demineralised water was added and mixing continued for another 10 mins The batch was then thinned with a further 179 parts of demineralised water, yielding a dispersion of polymer particles of 1.0-2.5 μm dia. , which was stable at pH 5.2. When subjected to the above-mentioned stability 5 test, the dispersion remained stable at a pH of 10-11 for the full duration of the test. The dispersion was subjected to the polymerisation conditions described in example 1 and similarly subjected to testing in a cathodic electrodeposition - ■ - bath. The deposit on the cathode was thick but lacked adhesion to the electrode; in contrast to the film of example 1. EXAMPLE 3 15 Preparation of a thermose ting aqueous dispersion according to the invention in which both pre-formed polymer and polymer formed in situ contain reactive groups and the disperse particles comprise a cross- linking agent. 20 A solution of 37.5 parts of a 16% by wt. solution . of the di-acεtate of a tallow propylene diamine (Duomac T - Trade Mark) in 100 parts de-ionised water dispersed under high shear using a Silverson emulsifier, into the following solution: 25 epoxy resin * 4 400.0 0 parts methyl methacrylate 0 butyl aerylate 22 . 0 hydrσxyisopropyl methacrylate - * Q cross- ,i.n,kεrxx 25 r . υ 3onυ ai-!1ky1l t--_er_t--. amm• eXXX 12. 0 cumene hydroperoxide -! n U x epoxide equivalent 182-194. Epikote (Trace Mark) 323 xx Cymel (Trade Mark) 1125 or 1141 xxx Ethcmeen (Trade Mark) C 12 A further 112 parts of de-ionised water was added and the high shear maintained for a further 5 minutes. The surface active agent had an HL3 value in excess of 8 and the stable dispersion so-formed when tested as hereinabove described at a solids of 15% by wt. destabilised at a pH of 11. A solution of 0.4 parts ascorbic acid in 20 parts of de-icnised water was then added with gentle stirring and the batch allowed to exotherm (typically 25— i* 45 C) When the temperature returned to ambient, a further 200 parts de-ionised water were added and the dispersion so-formed was dialysed overnight according to common commercial electrodeposition practices. The dispersion had a pH of 6.3 and particle size of 0.3 μm. A coating of good integrity and adhesion was deposited electrophoreticaily on a cathode at a film build of 80 μm, with a coulomb yield of 120 mgm per coulomb. Cross-linking of the coating was achieved by stcving the film for 20 ran at 130°C. Similar results were obtained when a blocked isocyanate cross-linking agent of the type described in example III of United States Patent specification No. 3,799,854 was substituted from the Cymel resin. When using the blocked isocyanate it was also necessar37 to include 0.5 parts of dibutyl tin dilaurate in the initial dispersion. EXAMPLE ' 4 Preparation of polymeric surface active agents with an HL3 value in excess of 8. 450 parts of an epoxy resin - Epikote (Trade Mark) 1001 - and 70 parts of phenol were melted and blended together. A charge of 26 parts of diethanolamine was added to the batch cautiously at 100 C, the temperature raised to 150°C and maintained for 2 hrs or until the epoxide value of the batch dropped to zero. The product is referred to hereinunder as Agent A. A second surface-active agent was prepared in a similar manner from 900 parts of Epikote (Trade Mark) 1004, 76 parts of p-nitrophenol and 43 parts of diethanolamine. In this case, after the two components were blended, stirring was carried out at 170°C, not 150°C. The product is referred to hereinunder as Agent 3. EXAMPLE " 5 Preparation of a dispersion according to the invention using Agent A from example 4 as surface-active agent to stabilise the dispersion. 250 parts of de-ionised water were added under conditions of high shear as described in example 3 to the following solution: Agent A 40.0 parts methyl methacrylate 32.5 butyl aerylate 7.5 hydroxybutyl acrylate 15.0 Cymel 1125 (ref. example 1) 25.0 cu ene hydroperoxide 2.0 octyl mercaptan 0.5 acetic acid i - This dispersion showed the desired instability at pH 11, when subjected to our stability test. A solution of 0.3 parts ascorbic acid and 0.15 parts of ferrous sulphate in 50 parts of de-ionised water was added with gentle stirring to the batch, which then exothermed gently (typically 25 -> 45°C) . The dispersion so-formed had a pH of 4.5, particle size of the order of 2.5 μ and deposited a coating film to a thickness of 40 μm on a cathodic in an eiectrophoretic deposition bath with a coulomb yield of 95 mg/coulomb. Deposition time was approx. 2 n at 25°C and at a pressure of 200 volts. The film cured to a hard, smooth coating when stoved for 20 mn at 180°C. It showed excellent toughness and adhesion and resistance to salt spray corrosion. As with the .dispersion of example 3, the alternative cross-linking agents Cymεl 1141 and the blocked isocyanate gave equally satisfactory results. A soluble urea-formaldehydε resin also produced acceptable films when used as an alternative cross- linking agent. EXAMPLE ' 6 Preparation of a dispεrsion according to the invention using Agent B from example 4 as surface active agent to stabilise the dispersion. This dispersion was prepared by the general method of example 3, but using the components listed herεunder as the corresponding addition stages and starting with 250 parts of de-ionised water. _ 9? _ Agent B 40.0 parts methyl methacrylate 22.0 butyl methacrylate 10.0 butyl aeryla e 13.0 hydroxyethyl methacrylate 10.0 hydroxybutyl aerylate 5.0 Cymel 1125 (or 1141) 25.0 n-butanol 2.0 cumene hydroperoxide 2.0 octyl mercaptan 0.5 acεtic acid 1.2 The dispersion became unstable at pH 11 as required by our oH stability test. Polymerisation was then initiated as in example 5 usins: the following initiator S7ste ; ascorbic acid 0.4 parts ferrous sulphate 0.15 " de-ionised water 40.00 " The dispersion so-formed had a- particle size of about 0.28 μm and a pH of 4.6. It deposited in a cathodic electrodeposition cell to a thickness of 43 μm at 2 mn at 2S°C and under a pressure of 200 volts The coulomb yield was 72 mg per coulomb. When cross-linked by stoving for 20 minutes at 180°G the deposited coating film was smooth and tough, with good adhesion to thε substrate. ' It had good resistance to salt soray corrosion. EXAMPLE ' 7 Preparation of a dispersion according to the invention using Agent A of example 4 and thermal polymerisation initiation. 250 parts of de-ionised water were dispersed by the general method of example 3 into the following solution: Agent A 40.0 parts methyl methacrylate 33.0 " butyl acrylate 22.0 " hydroxy isopropyl methacrylate . 5.0 " Cyme! 1125 25.0 acetic acid 1.0 " azodiisobutyronitrile 1.0 " The resulting aqueous dispersion was unstable at ■ pH 11 when subjected to our pH stability test. It was heated on a steam bath to 90-100°C with gentle stirring for 5 hrs then cooled-to room temperature. The final dispersion had a particle diameter of the order of 0,35 μm and when tested as described in example 3 it produced smooth coating films of good integrity and adhesion. -The alternative cross-linking agents of that example ag " ain produced satisfactory cross -ϋrJr.ed films when used with this dispersion. EXAMPLE ' 8 Effect of varying the- level of pre-formed- pσl πner or pol τ er stabiliser on the properties of a dispersion of the t τpe disclosed in example 3 . Five dispersions were prepared by the general method of example 3 but using the components listed hereinunder as the corresponding preparation stages . DTSPEKSTO NO. - Parts 1 2_ 1 4 5_ 16% Duomac T solution 25 25 25 25 25 de-ionised water 225 225 225 225 225 Epikote 828 60 50 40 30 20 methyl methacrylate 21 27 33 38 44 butyl acrylate 14 18 22 27 31 hydroxy isopropyl methacrylate 5 5 5 5 5 Cy el 1125 20 20 20 20 20 Ethomeen C12 12 12 12 12 12 cumene hydroperoxide 1 1 1 1 1 ascorbic acid 0. 4 0. 4 0. 4 0. 4 0.4 water 20. 0 20. 0 20. 0 20. 0 20.0 All dispersions prior to polymerisation were stable and passed our pH stability test. All produced stable dispersions which deposited films of good integrity and adhesion under the test conditions described in example 3. This was not materially affected by changes in the selected cross--Linking agent. Compositions comprising higher levels of epoxy resin showed decreasing long-term stability and less satisfactory cure. The cured films were somewhat sticky. At the same time, the films derived from higher epoxy content dispersions showed generally superior resistance to corrosion. The preferred compositions comprised 30-50% bγ wt epoxy resin with the overall best balance of properties being shown at 40% epoxv resin content. EXAMPLE 9 Effect of some alternative cross-linking agents on dispersions stabilised with Agent A of example 4. The following dispersions were prepared by the general method of example 3, but using the components listed hereunder as the corresponding addition stages and starting each preparation with an initial change of 250 parts of de-ionised water. Dispersion No. - Parts 1 2. 3_ 4 _ e> Agent A 40 40 40 40 40 40 40 methyl methacrylate 33 33 33 33 33 33 33 butyl acrylatε 22 22 22 22 22 22 22 methylisobutyl methacrylate 5 5 ς 5 5 5 5 Duo een C 12 12 12 12 12 12 12 12 cu ene hy roperoxide 1 1 1 1 ___ 1 acetic acid 1 1 1 1 1 1 tt 1141 - 23 - - - - - TI 1156 - - 20 - - - - II 1125 - - - 23 - - - 11 1170 - - - - 20 - - UFP. 65 - - - - - 20 - UFR 80 — _ _ - _ - 20 ascorbic acid 0.4 0.4 0.4 0.4 0.4 0.4 0.4 de-icnised water 20.0 20.0 20.0 20.0 20.0 20.0 20.0 Cross-linking agents in these formulations are further identified, as -fellows: Cymel 303 - highly mεthylatεd M.F. resin " 1141 - highly alkylated M.F. resin " 1156 - highly butylated M.F. resin " 1125 - highly alkylated benzoguanamine resin " 1170 - highly alkylated glycoluril resin UFR 65 - highly methylated U.F. resin " 80 - highly butylated U.F. resin ("Cy el" is a Trade Mark of American Cyanamid Co. , USA) The resulting dispersions had the following characteristics : 1 2 3 4 5 6 7 Particle size (μm) 0.27 0.25 0.19 0.34 0.4 0.34 0.22 oH 6.6 6.4 6.4 6.2 6.0 6.2 6.2 Films deposited electrophoretically on a cathode in 2 mn at 25 C and at 200 volts had the followin characteristics : - 2 3 4 5 6 7 Film thickness (μm) 3 300 23 20 25 26 27 21 Coulomb yield ( gm/coulomb) 91 90 107 83 93 67 94 Cure fair good fair good poor good poor EXAMPLE 10 Effect of surface active agent level on film characteristics The following dispersions were prepared b^ the general method of example 3, but using the components listed hereunder as the corresponding addition stages. Dispersion No. - parts 1 2 3 , 4 de-ionised water 500.0 500.0 500.0 500.0 Duomac T 16.0 8.0 4.0 Ξpikote 323 40.0 40.0 40.0 40.0 methyl methacrylate 33.0 33.0 33.0 33.0 butyl'aer late 22.0 ■ 22.0 22.0 22.0 hydrox3/isopropyl mεthacr37late 5.0 5.0 5.0 5.0 cross-linking agent 20.0 20.0 20.0 20.0 Ethomeen C 12 12.0 12.0 12.0 12.0 hexyl Cellosolve (Trade Mark) 5.0 5.0 5.0 cumene hvcrOPeroxide 1.0 1.0 1.0 1.0 Dispersion No. - oarts 1 2_ 3 , 4 ascorbic acid 0. 4 0. 4 0. 4 0. 4 de-ionised water 20. 0 20. 0 20. 0 20. 0 * may be chosen from Cy el 1125, Cyme! 1141, U.F.R. 65 (see example 9) or a blocked isocyanate according to example.3. All dispersions prior to polymerisation destabilised according to our pH stability test at pH 11. 0 The particle sizes were of the order of 0.13 μm, ...28 μm, .25 μm and .27 μm respectively. Satisfactory films of good adhesion werε produced by cathodic electrodeposition using 200 volts for 2 mn at 25°C and cross-linking the films by stoving for 30 mn -5 at 180°C- The cathode was a phosphate pre-treated steel panel Depositioncharacteristics were as follows: I 1 1 _. Film thickness (μm) 20 45 57 100 0 Yield (mgm/coulomb) 36 70 122 190 It is apparent, for the particular dispersion studied, that both deposited film thickness and coulomb yield increased as the surface active agent level decreased. 5 EXAMPLE 11 Effect of different fatty surface active agents cn dispersion deposition characteristics . The following dispersions were prepared by the general method of example 3 , but starting in each case 0 with 250 parts of de-ionised water and using the components listed hereunder as the corresponding addition stages . - EAI OMPI n a _- Dispersion No. - Parts Epikotε 1001 40.0 40.0 40,D 40.0 0.0 40.0 40.0 40.0 methyl meth¬ acrylate 33.0 33.0 33.0 33.0 33.0 33.0 33.0 33.0 butyl acrylate 22.0 22.0 22.0 22.0 22.0 22.0 22.0 22.0 hydroxyisopropyl methacrylate 5.0 5.0 5.0 5.0 5.0 5.0 5.0 5.0 cross-linkins agentx 20.0 20.0 20.0 20.0 20.0 20.0 20.0 20.0 Ξ Ξtthhoommeeeenn^^ CCl12 12.0 12.0 12.0 12.0 12.0 12.0 12.0 12.0 cu ene hydro- peroxide 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 Duomeen ^'____ 0 3.0 D Duuccmmeeeenn CC - - 5.7 - Duomeen S - 3.0 Duσmeen T - 3.0 Ξthoquad 0/12 - Ξthoduomeen X * X T/13 - Ξthoduomeen T/20 - 3.5 - Ξthcmeen T/I2 - - 3.4 acetic acid 1.0 1.1 1.0 1.0 - 0.7 O.5 0.6 ascorbic acid 0 .4 0. 4 0 .4 0 . 4 0 .4 0 . 4 0 . 4 0.4 de- ionised water 100.0 100. Q 100.0 100, 0 100.0 100.0 100.0 100.0 ~_ζ___Z. .. x may be selected from C7 el 1125, Cymεl 1141 UFP.80 or blocked isocyanate according to example 3. xx Trade mark. The individual surface active agents under test are ' further identified as follows: Duo eens - alkyl propylene diamines, the alkyl group of thε particular member being derived as follows : 0 - oleic C - coco S - soya T - tallow Ξthoαuad 0/12 a polyethoxylated quaternary ammonium salt, containing an oleyl alkyl group and 2 mol of ethylene oxide. Ξthoduomeen T/13 a reaction product of an N-alkyl trimethylenediamine containing a "tallow" alkyl group and 3 mol of ethylene oxide. Ξthoduomeen T/20 as for T/13 but with 10 mol ethylene oxide. Ξthomeen T/12 a tertiary a ine having a "tallow" alkyl group and 2 ethylene oxide groups attached to the nitrogen. All dispersions prior to polymerisation exhibited instability as required by our pH instability test at a pH of 11. The dispersion so-prepared had the following characteristics: 1 _2 ' _3_ _4 _5 _6 _7 • 8_ Particle size 0.35 0.43 0.43 0.31 0.27 0.22 0.28 0.23 (μm). PtL 6.2 6.1 6.2 6.4 7.4 7.0 7.0 6.7 All dispersions deposited coherent films of good adhesion when tested as for example 10. The deposition characteristics wers as follows : O E ^ 1 2 4 5_ 6. Film thickness (μm) 55 40 55 60 200 x 80 Yield (mgm/ coulomb) 104 89 100 130 200 200 m b m_ ISO x thick but uneven films , EXAMPLE 12 Effect of using epoxy resins of increasing molecular weight as pre-formed polymer or polymer plasticiser. The following dispersions were prepared by the general method of example.3, but starting in each case with a solution of 16 parts of Duomac T in 300 parts of de-ionised water and using the components listed hereunder as the corresponding addition sta g es . Dispersion No, - parts 1 2 3_ * •_. Ξpikotε 823 40.0 - - - ;ooι - 40.0 - - 1004 - - 40.0 - 1007 - - - 40.0 methyl methacrylate 33.0 33.0 33.0 33.0 butyl aerylate 22.0 22.0 22.0 22.0 n-butoxy tiethacrylate 5.0 5.0 5.0 5.0 UF3.30 22.0 22.0 22.0 22.0 Ethcmeen C 12 6.0 ' 6.0 6.0 6.0 cumene hyάroperoxide 1.0 1.0 1.0 1.0 ascorbic acid 0.4 0.4 0.4 0.4 de-icnised water 20.O 20.0 20.0 20.0 - 3 - All dispersions were unstable at pH 11 when subjected to our pH stability test. The dispersions so-formed had the following characteristics: 1 2_ 3_ 4 Particle size (μm) 0 . 25 0. 25 0. 31 0. 9 pH 4. 6 4. 6 4. 6 4. 7 Films deposited from thes e dispersions and tested according to example 10 had the following characteristics : 1 2 3 4 Film thicknes s (μ ) 41 24' 14 44 Corrosion protection after 21 days in salt spray - - Excellent V . Good V. Good Adequatε Film appearance Good Good Seme Poor orange peel effect }_____T_7; 13 Preparation of a thermoplastic aqueous dispersion according to the invention, in which the polymer formed in situ contains no reactive group. Example 1 was repeated but with the 5 parts of N-(n-butoxy methyl) acrylamide being replaced with 5 parts of n-butyl acrylate. The dispersion was prepared and evaluated as for the dispersion in Example 1. The dispersion behaved in a similar fashion in the stability test and after polymerisation and deposition gave films similar in appearance to those of Example 1. The films were, however, thermoplastic. OMPI Λ. IIPPOO EXAMPLE 14 Comparative example showing the effect of a surface active agεnt which leads to the ' dispεrsion not destabilising at pK 11 in the above mentioned stability test. Example 3 was repeated except that the 12.0 parts of the alkyl tert. amine were replaced with 12.0 parts of a long ethoxylate (50 moles ethylene oxide) fatty amine, Ξthomeεn T60 (Tradε Mark) which has a H.L.3 value greater than 8. When subjected to the stability test the dispersion remained stable at PH 11. After polymerisation it was found that this composition failed to deposit satisfactory films.

Claims: CLAIMS 1. A process of preparing an aqueous dispersion of particles of film-forming polymer suitable for use in a cathodic electrodeposition process, the said process consisting of the following steps in combination: (1) Pre-formed polymer or polymer plasticiser dissolved in polymerisable , β-ethylenically unsaturated monomer which has a maximum solubility in water of 10% by weight at 25°C is stably dispersed in water in the presence of surface active agent; and (2) unsaturated monomer in the dispersion is polymerised to form a particulate dispersion of film-forming polymer wherein the particles comprise blends of pre-formed polymer or polymer plasticiser and polymer formed in situ from the unsaturated monomer; characterised in that the stable dispersion in water prior to the initiation of polymerisation has .a pK of less than 10 ' but when subjected to the pH stability test descrfbεd hereinunder becomεs unstable at a pH of 10-11 and the surface active agent is a cationic surface active agent which has a hydrophilic-lipophilic balance (H.L.B. value) of at least 8. . 2. A process of preparing an aqueous dispersion according to claim 1, characterised in that when five drops of the dispersion taken prior to the initiation of polymerisation are added to lOg of de-ionised water, treated with 10 * "M potassium hydroxide solution to give a pH of 10-11 and allowed to stand for 10 hr at 25°C, a visible settling of polymer with the formation of a clear, upper layer takes place in the sample under test. 3. A process of preparing an aqueous dispersion according to claim 1 characterised in that the particulate dispersion of film-forming polymer provides a thermoplastic coating film. 5 4. A process of preparing an aqueous dispersion according to claim 3 characterised in that the pre¬ formed polymer is a mixture of two or more polymers, optionally in combination with a polymer plasticiser. 5. A process of preparing an aqueous dispersion 10 according to claim 1 characterised in that the particulate dispersion of film-forming polymer provides a ther oset coating film. 6. A process of preparing an aqueous dispersion according to claim 5 characterised in that the pre- -5 formed polymer contains reactive groups and complementary reactive groups which will enter into a cross-linking reaction. 7. A process of preparing an aqueous dispersion according to claim 5 characterised in that polymer 0 formed in situ contains reactive groups and complementary reactive groups which will enter into a cross-linking reaction. 8. A process of preparing an aqueous dispersion according to claim 5 charactεrised in that the 5 pre-formed polymer provides one type of reactive group and the polymer " formed in situ the complementary type of reactive group. 9. A process of preparing an aqueous dispersion according to claim 5 characterised in that it contains 0 polymer plasticiser which will bond chemically.-.to othe: polymeric film-forming components.. i REΛ c OMPI 10. A process of preparing an aqueous dispersion according to claim 5 characterised in that the dispersion contains cross-linking agent which will react with reactive groups in pre-formed polymer or polymer plasticiser, polymer formed in situ, or in both αf them.. 11. A process of preparing an aqueous dispersion according to claim 10 charactεrisεd in that both pre-formed polymer or polymer plasticiser and polymer formed in situ contain hydroxyl groups and the cross-linking agent contains complementary reactive groups 12. A process of preparing an aqueous dispersion according to claim 11 characterised in that the cross-linking agent is incorporated in the disperse phase of the dispersion. 13. A process of preparing an aqueous dispersion according to claim 5 charactεrisεd in that the surface active agεnt is polymeric and contains a reactive group allowing it to take part in the film-forming cross-linking reaction. 14. An aqueous dispersion of particles of film- forming,polymer prepared by a process as claimed in claim 1. 15. A process of depositing a coating film on a substrate by cationic elεctrodεposition characterised in that the deposition bath consists essentially of an aqueous dispεrsion of particlεs of film-forming polymεr according :to claim 15. ORE

Inventors: GIBSON D, MCKAY G, SWALWELL J
Applicants: DULUX AUSTRALIA LTD
Application year: 1981
Main classification: C08J3
IPC codes: C08F2, C08F283, C08F291, C08J3, C09D5, C09D151, C25D13