POLYMERIC DISPERSING AGENT,METHODS OF PREPARING THE SAME AND DISPERSION CONTAINING SAID DISPERSING AGENT

Abstract: A polymeric dispersing agent consisting of an oligo or polyamide chain, wherein all nitrogen atoms are part of amido bonds, said oligo or polyamide chain being connected with at least one polymeric chain, each polymeric chain having a molecular weight of at least 1000. The dispersing agent shows high affinity to particles of "acidic" character, such as certain pigments, and is therefore capable of effectively dispersing such particles in organic liquids. The dispersing agent is prepared (1) by reacting a diamine with an amino acid and optionally reacting the reaction product thus formed with a dicarboxylic acid so as to form a reaction product which is reacted with a polyester forming hydroxycarboxylic acid, or (2) by reacting a diamine with a dicarboxylic acid so as to form an oligo or polyamide which is reacted with a polyester forming hydroxycarboxylic acid. A dispersion of solid particles in an organic liquid and the polymeric dispersing agent contains from 1 to 20% by weight of the dispersing agent based on the weight of solid particles.

Description: , dispersion containing said dispersing agent β This invention relates to a polymeric dispersing agent for use for dispersing solid particles in an organic liquid and more parti¬ cularly a dispersing agent for use in disperging pigments in organic liquids so as to form printing inks including printing in k concentra¬ tes. Danish patent application No . 6257/71 describes pigment-con¬ taining dispersions containing as a dispersion agent one or more polyesters or polyester salts , the polyester being derived from a hydroxycarboxylic acid having a hydrocarbon group containing at least 8 carbon atoms and in which there are at least 4 carbon atoms between the hydroxy and carboxylic acid groups , or from a mixture of such a hydroxycarboxylic acid and a carboxylic acid which is free from hydroxy groups . Pigments for the preparation of printing in ks can be group¬ ed in "acidic" , "basic" , "amphoteric" and "neutral" pigments (Palle Sørensen : "Application of the Acid/Base Concept" , Journal of Paint Technology, volume 47, No . 602, March 1975, pages 31 -38) . The above mentioned prior art dispersing agent is suitable for the preparation of dispersions containing special ly composed and in particular dϊazotϊzed and coupled pigments including red pigments but is unable to form satisfactory dispersions of certain "acidic" pigments including special black and blue pigments . Furthermore, due to the strongly polar and surface active character of the above men¬ tioned prior art disperging agent it is only suitable for the prepara¬ tion of dispersions which subsequently are to be used in rotogravure and letterpress printing inks, whereas it is unsuitable for use in lithographic printing in ks which during the printing operation are brought into intimate contact with water. The object of the invention is to provide a dispersing agent which is particularly suitable for the preparation of the dispersions of particles of an "acidic" character, such as certain pigments for the preparation of high quality lithographic printing in ks . This object is achieved with the dispersing agent according to the invention , said dispersing agent being characterized in that it consists essential ly of an oligo or polyamide chain in which all nitro ¬ gen atoms are part of amide bonds and that the oligo or polyamide chain is connected with at least one polymeric chain , each polymeric chain having a molecular weight of at least 1000, and wherein free carboxylic acid groups, if any, present in the polymeric chain or chains optionally are converted into amides or esters . The invention is based on the discovery that the oligo o polyamide chain which is of basic character shows a high affinity t particles of "acidic" character, such as pigments , and are capable o effectively dispersing such particles in an organic liquid . As mentioned above the dispersing agent according to th Invention consists essentially of an oligo or polyamide chain which Is connected with one or more polymer chains . The oligo or polyamide chain preferably comprises in aver¬ age from 2 to 36 amide bonds per molecule . The polymer chain or chains which are connected with the oligo or polyamide chain preferably are polyester chains having a molecular weight of at least 1500. Examples of other suitable types of polymer chains are homopolymers of butadiene and styrene-butadϊene copolymers . Polymers of the above mentioned type and being hydroxy terminated are commercially available under the trade name "poly bd resins" (ARCO Chemical Company) . Another suitable type of polymers Is carboxy terminated po~ lybutadienes which are commercially available under the trade name "Hycar CT" (B . F. Goodrich Chemical Company, U . S . A . ) . As indicated above the dispersing agents may also contain small amounts of other compounds than the above mentioned polymers . As explained below such compounds may originate from "impurities" in the starting materials used In the preparation of the polymeric disper¬ sing agent. The dispersing agent according to the invention may be prepared in several ways which are wel l known per se. Thus , the dispersing agent can be prepared by reacting an amine containing at least two amino groups with an amino acid and by optionally reacting the reaction product thus formed with a dicarbox¬ ylic acid and by reacting the compound thus formed with a hydroxy¬ carboxylic acid capable of forming a polyester. Free carboxylic acid groups which optionally may be present in the polymer formed may subsequently be converted into amϊdo groups with a base or may be esterified . The amine used is preferably a diamine having the formula: R 1 HN-R- H R / wherein R is a divalent hydrocarbon group containing between 1 and 1 2 20 carbon atoms and wherein R and R each is a hydrogen atom or a saturated or unsaturated hydrocarbon group containing from 1 to 20 carbon atoms . Examples of such diamines are ethylenedϊamlne, 1 , 2-- propanediamine, 1 ,6-hexanedϊamine, 1 ,8-octaπediamϊne, 1 , 12-dode- canediamine, 1 , 4-diaminocyclohexane and 1 , 4-phenylenediamine. The amino acid used is preferably an amino acid having the formula : R 4 HN R 5 COOH 4 wherein R is a hydrogen atom or a hydrocarbon group containing 5 1 -20 carbon atoms and R is a hydrocarbon group containing from 1 to 20 carbon atoms and optional ly being substituted . Examples of such amino acids are glycine, α-alanine, glutamic acid , arginine and 11 - amϊnoundecane acid . The dicarboxylic acid which optionally is used in the above mentioned method is for example succinic acid , adipic acid, azelaic acid , sebacϊc acid , 1 , 12-dodecanedioic acid , 1 , 2-cyclohexanedicarbox- ylic acid, 1 ,4-cyclohexanedϊcarboxylϊc acid and terephthalϊc acid . Examples of hydroxycarboxylic acids for use in the above mentioned method are 12-hydroxystearϊc acid and riclnolic acid . Other examples of suitable hydroxy carboxylic acids are disclosed in Danish patent application No. 6257/71 . The commercial ly available hydroxycarboxylic acids often contain a small amount of a carboxylic acid which is free from hydro¬ xy groups and the final product may thus contain some "Impurities" . Such "impurities" ordinarily have no significant adverse effect on the disperging activity of the product provided they are present in small amounts . If they are present in larger amounts , special precautions should be taken to remove said "impurities" or to convert them into amides or esters . The reaction of the above mentioned compounds Is preferab¬ ly effected while stirring , under an inactive gas and at a temperature of above 100 C in an aromatic solvent, e . g . xylene, and the water formed during the reaction is preferably removed by azeotropϊc distil¬ lation . When converting free carboxylic acids present in the poly¬ ester chain or chains and carboxylic acids originating from the above mentioned "impurities" into amides, a diamine of the above mentione type is preferably used . I n another method of preparing the dispersing . agent accord ing to the Invention an amine containing at least two amino groups i reacted with a dicarboxylic acid and the oligo or polyamide thus form ed is subsequently reacted with a hydroxycarboxylic acid capable o forming a polyester so as to form a polymer and free carboxylic aci groups , if any, are subsequently converted Into amido groups with base or are esterifled . The amine used is preferably a diamine of th same type as the diamine used in the first method described above. The same applies to the dicarboxylic acid and the hydroxycarboxyli acid . A diamine of the above mentioned type is preferably used t form the above mentioned amido groups . The reaction is preferably effected while stirring under an inactive gas and at a temperature of above 100 C in an aromatic sol¬ vent, e. g . xylene, and the water formed during the reaction is pre¬ ferably removed by azeotropϊc distillation . The invention also relates to a dispersion of solid particles in an organic liquid containing a dispersing agent of the above men¬ tioned type. Such a dispersion can be prepared by well known methods for the preparation of dispersions . Thus the solid particles , e. g . pigment particles, the organic liquid and the dispersing agent accor¬ ding to the invention may be mixed in any sequence and the mixture may then be subjected to a mechanical treatment to break down agglo¬ merates , if any, of solid particles, e . g . by ball-mil ling or rol ler-mil¬ ling . The solid substance may also be mil led alone or in admix¬ ture with either the organic liquid or the dispersing agent and the other component(s) may then be added, whereafter the dispersion is formed by stirring of the mixture. The amount of dispersing agent in dispersions according to the invention is preferably from 1 to 20% by weight and more prefer¬ ably from 5 to 15% by weight based on the weight of the solid partic¬ les, and the dispersions preferably contain from 40 to 60% by weight of solid particles based on the total weight of the dispersion . The organic liquids used for the preperation of said disper¬ sions may be inert organic liquids in which the dispersing agent is at -gU RE- OMPI least partially soluble at room temperature and which are stable under the conditions at which the dispersions are to be used . If desired , mixtures of organic liquids may be used . Preferred organic liquids are hydrocarbons and halogenated hydrocarbons , such as toluene, xylene, white spirit, chlorobenzeπe, carbontetrachloride and per- chloroethylene . Also other organic liquids can be used , for example esters , such as butyl acetate, alcohols , such as n-butanol , and linseed oil , the viscosity of which optionally is increased by heat treatment. It Is particularly preferred to use petroleum fractions . I n general the selection of the organic liquids or mixtures thereof used for the preparation of the dispersions will depend on the uses to which the dispersions are to be put. As mentioned above the solid particles preferably are pig¬ ment particles . I n case of inorganic pigments, these are preferably such which contain a metal atom, and as examples of such pigments there may be mentioned titanium dioxide, prussian blue, cadmium sulphide, iron oxides, vermilion , ultramarine and chrome pigments including chromates of lead , zinc, barium and calcium and mixtures and modifications thereof . Such pigments are commercial ly available as greenish-yellow to red pigments under the names primrose, lemon , middle, orange, scarlet and red chromes . The organic pigments are preferably water-insoluble metal salts or complexes , particularly calcium or barium salts or complexes of soluble or sparingly soluble organic dyes , especial ly azodyes and phthalocyanines . Other examples of suitable pigments are for example de¬ scribed in the third edition of Colour I ndex (1975) . The dispersions according to the invention are fluid or semi-fluid compositions containing the solid In finely divided and usually deflocculated form and they can be used for any purpose for which the dispersions of such solids are conventionally used . Disper¬ sions of pigments are of particular use in the manufacture of printing inks by admixing the dispersions with other components conventional ly used in the manufacture of such inks . The dispersions are also of value in the manufacture of paints in which they may be admixed with e. g . conventional alkyd and/or other resins . The invention wil l be described In further detail by the fol¬ lowing examples : EXAMPLE 1 A mixture of 400 g (2 moles) of 1 , 12-diamϊnododecane an 690 g (3 moles) of 1 ,2-dodecanedϊoic acid is heated while stirring in 10 litres glass flask under an atmosphere of nitrogen to 190 C and i maintained at said temperature for about 2,5 hours until 4 moles o water have been formed . The water thus formed is removed azeotrop Ically by means of xylene. The resulting oligo amide which contains free end-terminating acid groups is then reacted with 6000 g (abou 20 moles) of 12-hydroxystearIc acid at 220°C for 24 hours so as t form 20 moles of water. The water thus formed Is removed azeotropϊc ally with xylene. The acid number is determined (between 10 and 20 and 1 ,2-dϊaminododecane is added in an amount which is equal to 1 , ttiimmeess tthhee eeqquuiivvaalleenntt aammount while heating to 220 C until the wate generation Is terminated . The xylene Is removed in vacuum at 190 C . The product thus obtained is a brownish highly viscou mass having an acid number of 0 mg KOH/g and being soluble i aromates and aromate-contaϊnϊng liquids . EXAMPLE 2 A mixture of 200 g (1 mole) of 1 , 12-dϊaminododecane an 402 g (2 moles) of 11 -aminoundecane acid is reacted at 190 C whil removing 2 moles of reaction water. Subsequently 460 g (2 moles) o 1 , 12-dodecanedϊoic acid are added and the temperature is raised t 200 C . This temperature is maintained until 2 additional moles o water have been formed and removed azeotropically with xylene. Subsequently 6000 g (about 20 moles) of ricϊnolic acid ( " Nouracid C 80" from Akzo Che ϊe) are added and the temperature is maintaine at 200 C for 48 hours, whereby 20 moles of esterification water ar formed and removed azeotropically. The acid number is measured , and the equivalent amount o al kylpropylenediamine ( " Duo en T" from Armour Hess Chemicals Ltd . is added . The temperature is maintained at 200 C for 2 hours or until no more reaction water Is formed . The xylene is removed by distillation at 190 C under va cuum . The product thus obtained is a brownish highly viscous mass having an acid number of 3 mg KOH/g and is soluble in toluene. EXAMPLE 3 A reaction vessel having a volume of 700 litres and made from stainless steel is filled with 28.1 kg al kylpropylenediamϊne (" Duo- men T" ) and 31 .4 kg 11 -amϊnoundecane acid . After addition of 100 kg of xylene, stirring is started and the contents are heated to 143 C at which temperature the xylene is refluxing . From the start to the end of the process nitrogen is bubb¬ led through the reaction mixture . After 1 hour at 143 C 46.5 kg "Nouracid CS 80" containing 87% rlcinollc acid are added and the temperature is raised to 195 C at which it is maintained until no more reaction water is formed . The reaction water is removed azeotropically with xylene. Subsequently 465.8 kg "Nouracid CS 80" are added and the temperature is maintained at 195°C for 8 hours, at 220°C for 8 hours and at 240°C for 8 hours . Subsequently 28.1 kg "Duomen T" are slowly added to neutralize the free acid groups and to form amides, and the reaction is continued at 240 C until no more reaction water is formed . The total amount of water formed is 33 kg . After cooling to 195 C xylene is removed by distil lation under vacuum . The final product is a dark brown transparent highly vis¬ cous gel-lϊke mass having an acid number of 0 mg KOH/g . The product i soluble in pure aromates and aromate-contain- ing mineral oils . EXAMPLE 4 8.5 parts of the product prepared according to example 3 are dissolved in 41 .5 parts of mineral oil (containing 22% aromates and having a boiling range of 260-290 C) and 50 parts of carbonblack (pH = 3-5) are admixed with a slo ly moving stirrer. After 30 minutes of predispergϊng the dispersion is mil led once in a 3-roller mill . The dispersion thus obtained is fluid and contains carbon- black In finely divided and deflocculated state and is excellently suit¬ able for use in e. g . paints , lacquers and printing inks including li¬ thographic printing in ks . EXAMPLE 5 The method according to example 4 is repeated except that 50 parts of litholrubin , C . I . pigment red No . 57 (15850) are used instead of the carbonblack. The product obtained is a liquid dispersion in which th pigment is finely divided . The dispersion is suitable for the sam purposes as the dispersion according to example 4. EXAMPLE 6 The method according to example 4 is repeated except that the pigment used is 50 parts of a yellow pigment, C. I . pigment yellow No. 13 (21100) are used . The product obtained is a liquid dispersion in which the pigment is finely divided . The dispersion is suitable for the same purposes as the dispersion according to example 4. EXAMPLE 7 The method according to example 4 is repeated except that the pigment used is 50 parts of β-Cu-phthalocyanine blue, C . I . pigment blue No. 15.4 (74160) . The result obtained corresponds to that obtained according to example 5. EXAMPLE 8 The method according to example 4 is repeated except for the use of 10 parts of the product prepared according to example 3, 5 parts of mineral oil and 85 parts of titaniumdioxide (" R/U/F" from Bayer A. G . ) . The dispersion obtained is liquid and contains titaniumdio¬ xide in finely divided and deflocculated state . The dispersion is suit¬ able for the same purposes as the dispersion according to example 4. EXAMPLE 9 A mixture of 2880 g (8 moles) of al kylprcpylenedϊamine (" Duomen T" ) , 1610 g (7 moles) of 1 ,12-dodecanedϊoic acid and 402 g (2 moles) of 11 -amϊnouπdecane acid is reacted at 220 C while removing 16 moles of esterifϊcation water . 6600 g (about 22 moles) of ricinolic aciα are added to the polyamide formed (containing in average 16 ami¬ do groups per molecule) and the components are reacted at 200°C for 48 hours . 400 g (about 22 moles) of esterifϊcation water are formed and the water formed is removed azeotropically with xylene. The acid number of the products obtained is 22 mg KOH/g . 460 g (2.3 moles) of 1 , 2-diaminododεcane are added and the mixture is reacted at 220 C until no more reaction water is formed . The acid number is 0.5 mg KOH/g . The product obtained is tested as described in example 4. A similar result is obtained . EXAMPLE 10 - a) A mixture of 360 g of alkylpropylenediamine ("Duomen T") , 402 g of 11 -aminoundecane acid and 50 g of xylene is heated while stirring in a 1 litre glass flask while removing reaction water azeotropically with xylene. The temperature is gradually raised to 250 C and is maintained at 250 C until no more water Is generated . 36 ml of water are formed . The xylene is then removed at 180 C under vacuum . The product thus formed Is a diamϊde having free amino groups and is white and has a melting point of about 50 C . b) 4800 g of liquid carboxyl -terminated polybutadiene ( " Hy- car CTB" from B . F. Goodrich Chemical Company, U . S .A. ) having an acid equivalent weight of 2400 and a functionality of 2.01 , 327 g of behenyl alcohol , 5 g of hydroquinonεmonomethylether and 5 g of dibu- tyltinoxide are reacted at 210°C until no more reaction water is form¬ ed . The esterified product is a monofunctional compound having a measured acid equivalent weight of 4561 . c) 1820 of the esterϊflcation product prepared as described under b) are reacted with 145 g of the diamide prepared as described under a) at 220 C until no more reaction water originating from the amide formation resulting from the reaction between the amino groups of the diamide and the carboxylic acid groups of the esterified pro¬ duct is formed . Subsequently 490 g of mineral oil (boiling range 230-260 C and containing 18% aromates) are added . At room temperature the product thus obtained is a dark brown highly viscous wax-like paste which is soluble In aromates and aromate-containϊng mineral oils . 10 parts of said product are dissolved in 45 parts of mine¬ ral oil (boiling range 230-260°C and containing 18% aromates) and 45 parts of β-Cu-phthalocyanine blue are admixed . The mixture thus OMPI obtained is liquid and is milled twice on a 3-roller mill so as to form mixture containing the pigment in finely divided and deflocculate state.

Claims: P a t e n t C l a i m s 1. A polymeric dispersing agent for use in dispersing solid particles in an organic liquid, c a r a c t e r i z e d in that it consists essentially of an oligo or polyamide chain in which all nitro¬ gen atoms are part of amide bonds and that the oligo or polyamide chain is connected with at least one polymeric chain, each polymeric chain having a molecular weight of at least 1000, and wherein free carboxylic acid groups, if any, present In the polymeric chain or chains optionally are converted into amides or esters. 2. A polymeric dispersing agent according to claim 1, c h a r a c t e r i z e d in that the oligo or polyamide chain com¬ prises in average between 2 and 36 amido bonds per molecule. 3. A polymeric dispersing agent according to claim 1, c h a r a c t e r i z e d in that the polymer chain(s) connected with the oligo or polyamide chain are polyester chains having a mole¬ cular weight of at least 1500. 4. A polymeric dispersing agent according to claim 1, c h a r a c t e r i z e d in that the oligo or polyamide chain con¬ tains segments formed by reaction of amino acids. 5. A polymeric dispersing agent according to claim 4, c h a r a c t e r i z e d in that the segments are formed by react¬ ing 11-amϊnoundecane acid or arginine. 6. A method of preparing a dispersing agent according to claim 1, wherein the polymer chains are polyester chains, c h a r¬ a c t e r i z e d In that an amine containing at least 2 amino groups is reacted with an amino acid, that the reaction product thus formed is optionally reacted with a dicarboxylic acid, that the product thus obtained is reacted with a hydroxycarboxylic acid capable of forming a polyester and that free carboxylic acid groups, if any, are convert¬ ed into amido groups with a base or into ester groups. 7. A method of preparing the dispersing agent according to claim 1, wherein the polymer chains are polyester chains, c h a r ¬ a c t e r i z e d in that an amine containing at least two amino groups is reacted with a dicarboxylic acid and that the oligo or poly¬ amide thus formed is reacted with a hydroxycarboxylic acid capable of forming a polyester and that free carboxylic acid groups, if any, are converted into amido groups with a base or into ester groups. 8. A method according to claim 6 or 7, c h a r a c t e r i ¬ z e d in that the carboxylic acid groups are converted into amido OMPI /*, IPO < groups with a diamine. 9. A method according to claim 6 or 7, c h a r a c t e r i z e d in that the reaction is carried out under stirring an under an inactive gas and at a temperature of above 100 C in a aromatic solvent. 10. A dispersion of solid particles in an organic liquid con taining a dispersing agent, c h a r a c t e r i z e d in that th dispersing agent essentially consists of an oligo or polyamide chain i which all nitrogen atoms are part of amido bonds and that the oligo o polyamide chain is connected with at least one polymeric chain, eac polymeric chain having a molecular weight of at least 1000, and where in free carboxylic acid groups, If any, present in the polymeric chain or chains optionally are converted into amides or esters. 11. A dispersion according to claim 10, c h a r a c t e ¬ r i z e d in that it contains from 1 to 20% by weight of the disper¬ sion agent based on the weight of the solid particles. OMPI /L. WIPO

Inventors: CANESTRI G, GULEV N
Applicants: CANESTRI G, GULEV N, SADOLIN & HOLMBLAD AS
Application year: 1981
Main classification: B01F17
IPC codes: B01F17, C08G69, C09B67