BRAZE SLEEVING METHOD

Abstract: In a sleeving method a metal sleeve (16) is disposed within a tube (10) so as to bridge a defective region of the tube (10). The sleeve (16) which has a circumferential groove (40) filled with braze material is expanded in the area where the groove (40) is located which causes the braze material to closely contact the inside surface of the tube (10) and the area of the tube (10) wherein the braze is located is internally heated so as to create a brazed joint between the sleeve (16) and the tube (10).

Description: BRAZE SLEEVING METHOD This invention relates to tube repair methods and more particularly to methods for attaching a sleeve within a tube by a brazing procedure. In tube-type heat exchangers, a first fluid flows through the tubes of the heat exchanger while a second fluid surrounds the outside of the tubes such that heat exchange occurs between the two fluids. Occasionally, one of the tubes can become defective such that a leak occurs therein which allows the fluids to mingle. When this occurs, it is sometimes necessary to plug the tube so that the fluid does not flow through the tube, thereby preventing leakage from the tube. In nuclear reactor power plants, the tube-type heat exchangers are commonly referred to as steam generators. when a defect occurs in the tubes of a nuclear steam generator that allows the coolant in the tubes to mingle with the coolant outside of the tubes, a more significant problem arises. Not only does this situation create an ineffective heat exchanger, but it also creates a radioactive contamination problem. Since the fluid flowing in the tubes of a nuclear steam generator is generally radioactive, it is important that it not be allowed to leak from the tubes and contaminate the fluid surrounding the tubes. Therefore, when a leak occurs in a nuclear steam generator heat exchange tube, the heat exchange tube must either be plugged or repaired so that the coolant does not leak from the tube. This prevents contamination of the fluid surrounding the tubes. There are several methods known in the art for repairing heat exchange tubes, however, many of these methods are not applicable to repair of heat exchange tubes wherein the tube is not readily accessible. For example, in a nuclear steam generator the physical inaccessibility of defective heat exchange tubes and the radioactive nature of the environment surrounding the heat exchange tubes presents unique problems to repairing heat exchange tubes that do not normally exist in other heat exchangers. For these reasons, special methods have been developed for repairing heat exchange tubes in nuclear steam generators. Typically, the method used to repair a heat exchange tube in a nuclear steam generator is one in which a metal sleeve having an outside diameter slightly smaller than the inside diameter of the defective tube is inserted into the defective tube and attached to the defective tube to bridge the defective area of the tube. This type of repair method is generally referred to as "sleeving". Previous sleeving development work has been concerned with obtaining a relatively leakproof joint between the sleeve and the tube by brazing, arc welding, explosive welding, or other joining means. Due to the need for cleanliness, close fittings, heat application, and atmospheric control, these metallurgical bonding techniques have problems which are not easily solvable in areas such as nuclear steam generators where human access is limited. One particular method of securing a sleeve within a tube is described in United States Patent No. 4,069,573, issued January 24, 1978 to Rogers, Jr. et al. In the patent to Rogers, Jr. et al., the sleeve is positioned within the tube so that it extends coextensive with the region of degraded tube wall and partially beyond the axial extremes of the degraded area. A radially outwardly directed force is then applied to the tubular sleeve from within along a portion of the sleeve at each end, extending beyond the degraded area. The force is sufficient to cause outward plastic deformation of both the sleeve and the tube, resulting in an interference mechanical joint therebetween. As stated in the patent to Rogers, Jr. et ai,, the method as described therein does not produce a leaktight joint. In United States Patent No. 3,025,596, issued March 20, 1-962, to C. T. Ward et al., there is described a method for bonding concentric tubes or shells or other similarly mating parts that are formed of materials which are compatible with the process of brazing. While the patent to Ward et al. describes various methods for brazing tubular members together, it does not relate to and address the specific problems of securing a sleeve within a tube of a nuclear heat exchanger wherein human access is limited. The difficult environment associated with a nuclear steam generator limits the type of tube preparation, heating, and braze materials that are available for use such that common brazing techniques are not applicable to this environment. While there are methods known in the art for inserting sleeves within tubes of heat exchangers and there are methods known in the art for brazing tubes together, there do not exist methods for inserting and brazing sleeves in nuclear steam generator heat exchange tubes which are capable of being performed where personnel access is limited and where a leaktight joint is needed. Therefore, it is the principal object of the present invention to provide a method for securing a sleeve within a heat exchange tube of a nuclear steam generator by a brazing process that produces a leaktight joint between the sleeve and the tube. With this object in view, the present invention resides in a method for brazing a metal sleeve within a metal tube wherein the inner surface of said tube is cleaned and a metal sleeve is positioned in said tube and brazed therein, characterized in that, before said metal sleeve is positioned in said tube, an annular groove is formed around a portion of the outside surface of said sleeve and said groove is substantially filled with braze material, a portion of said sleeve near each end thereof is then expanded into contact with the inner surface of said tube thereby placing said braze material in close contact with the inner surface of said tube, and the portion of said sleeve wherein said braze material is located is internally heated to between 9850C and 11000C for 10 to 20 seconds. The invention will become more readily apparent from the following description of a preferred embodiment thereof shown, by way of example only, in the accompanying drawings, wherein: Figure 1 is a cross-sectional view in elevation of a sleeve and expander apparatus disposed within a heat exchange tube; Figure 2 is an enlarged view of the sleeve and tube in the expanded configuration; Figure 3 is a cross-sectional view in elevation of the sleeve with the heater disposed therein; and Figure 4 is a cross-sectional view in elevation of the sleeve within a tube in an alternate arrangement. Referring now to Figure 1, the nuclear steam generator (not shown) comprises a plurality of heat exchange tubes 10 which may be U-shaped tubes and are attached at each end to a tubesheet 12. During operation of the nuclear steam generator, reactor coolant flows through the heat exchange tubes 10 in a manner so as to heat fluid surrounding tubes 10. The fluid around tubes 10 is converted to steam to produce electricity in a conventional manner. Since the reactor coolant flowing through heat exchange tubes 10 has passed through the nuclear reactor, it is radioactive. Therefore, it is important to isolate the coolant flowing through the tubes from the fluid surrounding the tubes. When a defect develops in heat exchange tube 10 such as defect 14, it is necessary to either plug heat exchange tube 10 or repair the area surrounding defect 14 so that no coolant leaks through defect 14. One method of repairing defect 14 is by insorting a metal sleeve 16 into heat exchange tube 10 in a manner so as to bridge the defective area. Still referring to Figure 1, when it is necessary to repair a defect such as defect 14, the nuclear steam generator is drained of its coolant and deactivated so that the end of a tube 10 can be reached by either remote access manipulators or by working personnel. Tube 10 is then cleaned to remove the internal oxide layer therefrom. The cleaning process may comprise the use of a rotatable abrasive hone which may be a wire brush with a high pressure water mist coolant. The honing process takes approximately 1 minute and extends approximately 6 inches above and 6 inches below the proposed joint. In this cleaning process, the entire oxide layer is removed from the interior of the tube and washed out by the high pressure water so that a reliable braze bond may be achieved. The oxide layer that is on the interior of tube 10 may be approximately 0.001 inches in thickness and can be removed using a rotatable hone moving at approximately 6 feet per minute in a linear direction and at about 800 rpm. The honing apparatus used for this cleaning process may be one such as that described in copending United States Patent Application Serial No. 085,444, filed October 16, 1979 in the name of E. H. Smith et al. and entitled "Decontamination Apparatus" or Serial No. 930,076 filed August 1, 1978, in the name of F. W. Cooper, Jr. and entitled "Segmented Flexible Hone" both of which are assigned to the Westinghouse Electric Corporation. Once the oxide layer has been removed from the interior of tube 10, the tube may then be cleaned with a solvent such as methyl-ethyl ketone or acetone. This may be accomplished by using a rotatable member having a cotton swab attached thereto and which disburses the solvent in mist form. The device used to apply the solvent and clean the interior of tube 10 may be similar to that described in copending United States Patent Application Serial No. 085,444, filed October 16, 1979 in the name of E. H. Smith et al. and entitled "Decontamination Apparatus"; however, in this instance the abrasive hone is replaced with a cotton swab. In this step, as the rotating apparatus rotates within tube 10, the solvent is sprayed from the apparatus and onto the cotton swab. Also, as the apparatus is rotated within tube 10, the cotton swab having the solvent thereon contacts the interior of tube 10 thereby removing any remaining loose oxides. As with the abrasive hone, the cotton swab hone is used to clean the interior of tube 10 approximately 6 inches above and 6 inches below the joint area. when the tubes 10 have been cleaned as described above, the tubes are then dried to remove any liquid from the interior of tube 10. For example, a blower may be placed in fluid communication with one end of tube 10 so as to blow hot dry air through the tube and out the other end of tube 10. This drying process is continued until the tube 10 is dry. Then a sleeve 16, which may be an Inconel sleeve, is positioned over an expander 18 which may be a hydraulic expander or a roll expander chosen from those well known in the art. Sleeve 16 is positioned over expander 18 such that one end of sleeve 16 is placed on ledge 20 of expander 18. Expander 18 with sleeve 16 mounted thereon is then inserted into tube 10 as shown in Figure 1. Ledge 20 of expander 18 is brought into contact with the bottom end of tube 10 so that the bottom end of sleeve 16 and the bottom end of tube 10 are in alignment. This provides an indexing point from which operators can determine the location of the top and bottom ends of sleeve 16 with respect to tube 10. Still referring to Figure 1, expander 18 comprises a central metal member 22 having a bore 24 therein for passage of a fluid therethrough. Central member 22 is attached at its lower end to end piece 26 whereon ledge 20 is located. End piece 26 also has a second bore 28 therein which is in colinear alignment with first bore 24. A flexible conduit 30 may be attached to the lower end of end piece 26 for conducting a fluid through second bore 28 and into first bore 24. A guide mechanism 32 may be attached to the top end of central member 22 for positioning expander 18 centrally within tube 10. Guide member 32 may be annular plastic strips attached to central member 22 or may be brush-like members for maintaining central member 22 in the proper relationship within tube 10 while allowing guide member 32 to pass through constricted portions of tube 10. A set of first seals 34 and a set of second seals 36 are disposed on central member 22 so as to define an annular area wherein sleeve 16 is to be expanded. In the case where sleeve 16 is to be expanded in several locations along its length, an additional first set of seals 34 and second set of seals 36 are located at that location. The seals may comprise a rubber O-ring and a neoprene backup ring chosen from those well known in the art. The seals are arranged to tightly contact the inside surface of sleeve 16. A transverse bore 38 is also provided in central member 22 and in fluid communication with first bore 24 for conducting a fluid from first bore 24 to the annular area defined between first seals 34 and second seals 36 for expanding sleeve 16 into contact with tube 10. Still referring to Figure 1, sleeve 16 has a notch or annular groove 40 cut in the outside surface of sleeve 16 into which the braze material may be deposited. Groove 40 may be approximately 0.38 mm. in depth and approximately 9.9 mm. inch long. This creates a volume in which the braze material may be deposited prior to sleeve 16 being placed on expander 18. The volume of groove 40 is approximately 1.5 to 3.0 times the volume of the joint to be created such that when filled with braze material, the volume of the braze material in the groove is approximately 1.5 to 3.0 times the joint volume also. The braze material may be 82% gold and 18% nickel. Before the braze material is placed in groove 4Q sleeve 16 is cleaned with a mildly abrasive cloth such as an emery cloth to remove all foreign substances. After this cleaning, a flux such as sodium tetraborate in solution is applied to sleeve 16 in the area wherein sleeve 16 is to be joined to tube 10 and the braze material is placed in groove 40. The flux is applied to the exterior of the sleeve to form a hard layer suitable for storage and transportation of the braze material to the joint. Then, sleeve 16 is placed on expander 18 and positioned within tube 10 as shown in Figure 1. Once sleeve 16 and expander 18 have been positioned in tube 10 as shown in Figure 1, a fluid such as water is introduced from a fluid source (not shown) through flexible conduit 30 at a pressure of between approximately 844 kg/cm2 and 1125 kg/cm2. The fluid flows through second bore 28, through first bore 24, and through transverse bore 38. From transverse bore 38 the fluid enters the annular chamber defined between first seals 34 and second seals 36. The fluid pressure causes sleeve 16 to expand into contact with and also expand tube 10 by approximately 0.13 mm. The deformation of tube 10 may not be visually noticeable but can be felt by manual inspection. The expansion causes permanent plastic deformation of both tube 10 and sleeve 16 so that sleeve 16 is in close contact with tube 10. The expansion of both sleeve 16 and tube 10 causes the braze material in groove 40 to be in close contact with the inside surface of tube 10. However, a small capillary gap of approximately 0.05 mm. generally remains between sleeve 16 and tube 10 into which the braze material flows when heated. Generally, the length of sleeve 16 to be expanded in the region of groove 40 is approximately 38 mm. In this manner, sleeve 16 is positioned firmly within tube 10 but is not yet completely sealed. Approximately 50.8 mm. length of sleeve 16 in the tubesheet area is placed in close contact with tube 10 in that region to provide a good joint. As an alternative to or in addition to hydraulic-ally expanding sleeve 16 in the region of tubesheet 12, sleeve 16 may be mechanically hard rolled using conventional apparatus. In either case, sleeve 16 is expanded approximately 0.05 mm. -0.13 mm. on the diameter. It should be noted that since both the lower end of sleeve 16 and the lower end of tube 10 have greater accessibility than does the upper section of sleeve 16, these lower ends can be welded by conventional methods or may be brazed as described above. The expansion of the lower end of sleeve 16 into contact with tube 10 is performed to increase the contact between sleeve 16 and tube 10 in that area and to enhance the weldability of sleeve 16 and tube 10 in that area. It should be further noted that since the end of sleeve 16 and tube 10 are capable of being welded, it is not necessary to braze that section of sleeve 16. Referring now to Figure 3, a heater such as electrical induction coil 42 is inserted in sleeve 16 so that induction coil 42 is positioned in the area of sleeve 16 wherein the braze material is located. Induction coil 42 may be a water-cooled copper coil capable of carrying between approximately 2-4 kilowatts of power. Induction coil 42 may incorporate a quartz-fiber optical feedback mechanism to monitor and control temperatures of sleeve 16 in the joint region. Once placed in proper relationship, induction coil 42 is activated so as to heat sleeve 16 and the braze material therein to a temperature between approximately 9850C and 11000C. Preferably, the braze material should be heated to a temperature of between approximately 10100C to 10750C. Generally, it takes approximately 30 seconds for the induction coil 42 to heat the braze material to this temperature. Once in the recommended temperature range, the temperature should be held at that range for approximately 15 seconds. when heated to this temperature, the braze material flows out of groove 40 and into the small gap between sleeve 16 and the inner surface of tube 10. The braze material flows into the gap between sleeve 16 and the inner surface of tube 10 filling the gap therebetween so as to create an effective braze joint therebetween. Next, induction coil 42 is removed from sleeve 16 and the braze material is allowed to cool. Once cooled, a solid brazed joint is formed between sleeve 16 and tube 10. In this configuration, sleeve 16 prevents leakage from tube 10 through defect 14. As an alternative, due to the location of defect 14, it may be necessary to position sleeve 16 above tubesheet 12. In this case, an expander 18 as shown in Figure 4 may be utilized to expand a plurality of grooves 40 into contact with tube 10. In this embodiment, since sleeve 16 is removed from the lower end of tube 10 and cannot be welded at its lower end, at least two brazed joints are needed. The process is the same as that previously described except that both joints are made by brazing. Because there are at least two brazed joints, an induction coil 42 as shown in Figure 3 may be employed so as to heat both braze regions simultaneously. Therefore, it can be seen that the invention provides a method for brazing a sleeve within a heat exchange tube of a nuclear steam generator in a quick and efficient manner thereby yielding a leak-tight joint between the sleeve and tube.

Claims: What we claim is: 1. A method for brazing a metal sleeve within a metal tube wherein the inner surface of said tube is cleaned and a metal sleeve is positioned in said tube and brazed therein, characterized in that, before said metal sleeve is positioned in said tube, an annular groove is formed around a portion of the outside surface of said sleeve and said groove is substantially filled with braze material, a portion of said sleeve near each end thereof is then expanded into contact with the inner surface of said tube thereby placing said braze material in close contact with the inner surface of said tube, and the portion of said sleeve wherein said braze material is located is internally heated to between 9850C and 11000C for 10 to 20 seconds. 2. A method according to claim 1, characterized in that said groove is filled with 1.5 to 3.0 times the volume of braze material needed to achieve a satisfactory brazed joint. 3. A method according to claim 1 or 2, characterized in that said portion of said sleeve is heated to about 10450C for approximately 15 seconds. 4. A method according to claim 3, characterized in that for heating said sleeve an induction coil is inserted into said sleeve. 5. A method according to any of claims 1 to 4, characterized in that said sleeve is coated with a thin layer of flux before it is positioned in said tube. 6. A method according to any of claims 1 to 5, characterized in that, for cleaning of the interior of said tube, the tube is abrasively honed and swabbed with a solvent to remove foreign substances and said tube is then blow-dryed with hot, dry air. 7. A method according to any of claims 1 to 6, characterized in that at least one end of said sleeve is welded to said tube before said sleeve is internally heated.

Inventors: BURACK, ROBERT DAVID
Applicants: WESTINGHOUSE ELECTRIC CORPORATION
Application year: 1981
Main classification: B23K1
IPC codes: F28F11, B23K1, F16L55