CHEMICAL BLOWING AGENT COMPOSITION, ITS COMPOSITION AND USE

Abstract: A composition comprising a blowing agent and an activator characterised in that a mixture of the blowing agent and activator is comminuted to a particle size less than 5 micrometres, methods of making the composition and the use of the compositions in expanding polymers.

Description: The present invention relates to a blowing agent composition, methods for making it and expandable compositions containing it. Blowing agents which decompose upon heating to give off a gas have been used for many years in the expansion of thermoplastic polymers. However, the decomposition temperature may be too high for a given polymer and/or the gas may be evolved over a comparatively wide temperature range. Therefore, an activator for the blowing agent is often mixed with the blowing agent; see for example US Patent Nos. 3305496 and 3511787 and Spanish Patent No. 444996 which describe the use of heavy metal, alkali-metal or alkaline-earth-metal salts or a special form of reactive silica as activators in azodicarbonamide blowing agents. Whilst the activators and blowing agents used may have had particle sizes less than 50 µm and may have been mixed together to form a powder additive, there has been no suggestion that the activator and blowing agent should be micronised together. Furthermore, whilst the presence of an activator may reduce the actual temperature at which decomposition begins, it will not usually affect the temperature spread over which the majority of the gas is evolved. Surprisingly, we have now found that if the blowing agent is mixed with the activator and the mixture itself is then comminuted in a fluid energy mill, enhanced results can be obtained from the mixture. This is most unexpected since mixing of separately micronised blowing agent and activator does not produce the same result. Accordingly, the present invention provides a method for making a blowing agent composition which comprises an azo compound or sulphonhydrazide blowing agent, and an activator for the blowing agent, which activator is an amine or amide, urea, a sulphonhydrazide, or a metal salt, oxide or soap, characterised in that a mixture of the blowing agent and the activator is comminuted in a fluid energy mill to give a product of mean particle size less than 5µm. The invention also provides a blowing agent composition comprising a mixture of an azo compound or sulphonhydrazide blowing agent, and an activator for the blowing agent, which activator is an amine or amide, urea, a sulphonhydrazide, or a metal salt, oxide or soap, characterised in that the mixture has been comminuted in a fluid energy mill to a mean particle size of less than 5µm. The invention further provides an expandable polymer composition comprising a thermoplastic polymer and the blowing agent composition of the invention. Suitable blowing agents for present use include azodicarbonamide and benzene sulphonhydrazide and oxy-bis(benzenesulphonhydrazide. A particularly preferred blowing agent is azodicarbonamide. Suitable activators for present use include amines and amides containing from 1 to 10 carbon atoms; oxides, mineral acid salts (e.g. the phosphates, sulphates or carbonates) and fatty acid (e.g. C₈ to C₂₀ aliphatic acid) soaps or complexes of zinc, cadmium, lead or tin. The activator and blowing agent are present in any suitable amount, typically in weight ratios of 1:20 to 1:1. If desired, other ingredients may be present in the mixture before or after micronisation. Suitable other ingredients include secondary blowing agents which may be provided by the use of excess of certain of the activators, e.g. zinc carbonate or a sulphonhydrazide; plasticizers; oils; pigments; lubricants and fillers. The composition of the invention is made by comminuting the ingredients together as opposed to separately as hitherto. The term comminution is used herein to denote the reducing in size of individual particles of a material and does not include only the mere breaking up of aggregations of smaller particles. Comminution is carried out until the mean particle size is less than 5µm, eg 2 to 4.5µm. The particle sizes quoted herein are those determined by carrying out a particle size analysis of the material using a Coulter Counter model TA and the mean particle size is that corresponding to a 50% retention in the particle size analysis. In an air powered microniser this is achieved by suitable selection of the air pressure and the feed rate of material to the mill. The blowing agent composition according to the invention may be used for expanding a wide range of thermoplastic polymers, or polymers which are thermoplastic at the outset of the expansion process but which are cross linked, vulcanised or otherwise rendered thermoset during or after the expansion process, for example natural and synthetic rubbers. Suitable polymers include polyolefins (such as polyethylene, polypropylene and polybutylene), olefin copolymers (such as copolymers of ethylene/propylene and ethylene/vinyl acetate), polystyrene, styrene copolymers (such as acrylonitrile/butadiene/styrene copolymers), polyvinyl chloride, and vinyl chloride copolymers. Preferably the polymer is polyvinyl chloride. The blowing agent composition is suitably present in the polymer as 0.01 to 30, preferably 1 to 5, parts by weight of the active blowing agent ingredient per hundred parts by weight of polymer. Because of its good dispersibility, the blowing agent composition of the invention can be incorporated directly into the thermoplastic polymer during the compounding, tumbling or mixing operation using any suitable techniques. However, if desired, the blowing agent composition can be first compounded into a pre-mix containing a relatively high proportion of the active blowing agent ingredient, for example 15 to 30 parts by weight per hundred parts by weight of polymer or plasticiser, or as much as 70 parts per 30 parts of plasticizer when preparing a pre-mix for use with polyvinyl chloride. This pre-mix can then be incorporated into the bulk of the polymer in any of the conventional ways. The expandable composition can also contain any of the usual additives; for example stabilisers, lubricants, plasticisers, fillers, dyes, pigments and secondary blowing agents. The blowing agent composition of the invention offers the advantages over the analogous conventionally blended compositions of a lower decomposition temperature, a narrower decomposition temperature range and an increase in the rate of evolution of gas from the composition. The following Examples are given to illustrate the invention, all parts and percentages are by weight. Example 1 200 Parts azodicarbonamide (available under the trade mark "Genitron AC2") were mixed with 60 parts of zinc oxide in a low speed, low shear screw-mixer. The above AC/ZnO composition was then micronised in a 30.5 cm (12 inch) microniser at an air pressure of 5,86x10⁵ N/m² (85 p.s.i.) to give a product with a mean particle size of 4.5 µm. This product is referred to as the AC/ZnO co-micronised composition. Azodicarbonamide and zinc oxide were micronised separately using the same technique and the products were them mixed in a high speed mixer to given a blend containing the same proportions as the AC/ZnO comicronised composition. The blended product is referred to as the AC blend below. The AC/ZnO composition and the AC blend were then heated to cause decomposition of the azodicarbonamide and the amount of gas evolved was measured. The results were as follows: Example 2 The process of Example 1 was repeated using 70 parts of AC and 30 parts of zinc carbonate. In this case the comicronised composition decomposed at 136-147°C and the blended composition decomposed at 143 to 164°C. Example 3 The following polymer composition was prepared from the AC/ZnO comicronised composition and AC blend prepared as in Example 1: Polyvinyl chloride 100 parts Dioctyl phthalate 57.5 parts Calcium carbonate 15 parts Blowing agent mixture 2.5 parts The mixture was then coated on to a backing sheet at a rate of 350 g/m² and pre-gelled at 125°C. A transparent non-expanding plastisol layer was coated onto the expandable layer at a rate of 200 g/m². The product was heated to 200°C for 106 seconds to decompose the blowing agent. The results are set out below in arbitrary units of thickness. Example 4 The following polymer compositions were prepared from the AC/ZnCO₃ comicronised composition and AC blend prepared as in Example 2: Polyvinyl chloride 100 parts Dioctyl phthalate 80 parts Calcium carbonate 5 parts Blowing agent mixture 3.5 parts The mixture was then coated on to a release paper at a rate of 350 g/m² and pre-gelled at 125°C. The product was heated to 200°C for times varying from 30 to 120 seconds to decompose the blowing agent and produce a foam. At various time intervals the foam thicknesses were measured and the expansion factors calculated. The expansion factor is the thickness of the foam divided by the original unexpanded thickness. The expansion factors were plotted against time and the times taken to achieve given factor values established. The results were as follows.

Claims: A method for making a blowing agent composition which comprises an azo compound or sulphonhydrazide blowing agent, and an activator for the blowing agent, which activator is an amine or amide, urea, a sulphonhydrazide, or a metal salt, oxide or soap, characterised in that a mixture of the blowing agent and the activator is comminuted in a fluid energy mill to give a product of mean particle size less than 5µm. A blowing agent composition comprising a mixture of an azo compound or sulphonhydrazide blowing agent, and an activator for the blowing agent, which activator is an amine or amide, urea, a sulphonhydrazide, or a metal salt, oxide or soap, characterised in that the mixture has been comminuted in a fluid energy mill to a mean particle size of less than 5µm. An expandable polymer composition comprising a thermoplastic polymer and a blowing agent, characterised in that the blowing agent comprises a composition according to claim 2. A pre-mix composition suitable for incorporation into a polymer composition so as to form an expandable polymer composition, which pre-mix composition is characterised in that it comprises a polymer or a plasticiser for the polymer and from 15 to 30 parts by weight of a composition according to claim 2 per 100 parts by weight of the polymer or plasticiser. A method or composition according to any of claims 1 to 4 characterised in that the blowing agent is azodicarbonamide. A method or composition according to any of claims 1 to 5 characterised in that the activator for the blowing agent is an oxide or salt of zinc, cadmium, lead or tin. A method or composition according to any of claims 1 to 6 characterised in that the activator is used in a weight ratio of 1:20 to 1:1 based on the weight of the blowing agent. A composition according to claim 3 characterised in that the blowing agent is present in an amount of from 0.01 to 30 parts by weight per 100 parts by weight of the polymer.

Inventors: BATHGATE, RAYMOND JOHN
Applicants: SCHERING INDUSTRIAL PRODUCTS LIMITED
Application year: 1981
Main classification: C08J9
IPC codes: C08J9, B29B13, C09K3, B29K105