WATER-SOLUBLE POLYMER SUSPENSIONS

Abstract: Suspensions of water soluble polymers are disclosed comprising 20 to 40% of a solid particulate water soluble polymer, 0.2 to 1% of an alcohol soluble thickener, 60 to 80% by weight of an organic liquid nonsolvent suspending medium and 0 to 5% of a surfactant. When added to water or aqueous salt solutions, these suspensions provide ready dis­ persibility of the polymer, followed by rapid dissolution and viscosity build-up.

Description: Water-soluble polymer suspensions. This invention relates to the preparation of non-aqueous slurries of water soluble polymers. More specifically, it relates to the preparation of slurries of solid, particulate water soluble polymers which slurries are pumpable and which, when introduced into water, permit rapid, homogeneous dispersion of polymer particles followed by rapid dissolution thereof and rapid viscosity build-up to a high percentage of the ultimate attainable viscosity. Water soluble polymers are widely used as thickeners, flow modifiers, fluid loss control agents, dispersing aids, and flocculants in many industries such as petroleum, mining, papermarking, textiles, and coatings. Many such polymers, however, are difficult to put into solution due to their tendency to hydrate so rapidly that the surfaces of the particles gel and the particles agglomerate. This gelling blocks the surface of the particles and prevents water from permeating throughout the particle to effect complete dissolution. To break up the surface gelled particles and clumps so that the entire particle can be hydrated and dissolved is a time consuming operation requiring expensive, heavy agitatiny equipment. The amount of agitation required, in addition to being time consuming and thus expensive, is also detrimental to the quality of the solution inasmuch as most water soluble polymers are shear sensitive and agitation reduces their molecular weight, resulting in loss of solution viscosity. Several methods have been proposed to overcome the stated difficulties. The most commonly used method is to treat the surface of dry particles lightly with a -crosslinking agent, sufficient to form a lightly crosslinked layer on the surface which will not gel, thus permitting water to penetrate into the interior of the particle following which the surface crosslinks are hydrolyzed slowly by the water and the entire particle is then able to be dissolved. While such techniques are very satisfactory in general, there are occasions when better techniques are needed. For example,- hydrolysis of the cross links is frequently a pH sensitive reaction, so a product treated in this way is sometimes limited as to the environment in which it can be used. Moreover, some water soluble polymers are not subject to any treatment of this type and dissolution of these must be carried out according to rigidly critical procedures. It is the object of this invention to provide water soluble polymers in a readily dispersible and readily soluble form. It is another object of this invention to develop a suspension of water soluble polymers which is pumpable and from which polymer particles will disperse readily in water or aqueous salt solutions and dissolve rapidly to provide rapid build-up of solution viscosity. Yet another object is to provide water soluble polymers in a form which is readily handled and easily metered. In accordance with this invention, there are provided suspensions of water soluble polymers, which comprise about 20 to 40% of a particulate water soluble polymer, 0.2 to 1% of an alcohol-soluble thickener, 60 to 80% by weight of an organic liquid nonsolvent suspending medium, and 0% to 5% of a surfactant having an HLB between about 10 and 20. Such suspensions are very stable, resisting settling of the polymer particles for a substantial period of time and are of a -con- sistency to be readily pumpable. When these suspensions are added to water, the polymer particles disperse readily throughout the water and dissolve rapidly to form clear, smooth solutions. The liquid, organic suspending medium is an essentially water immiscible aliphatic alcohol or a mixture of at least one such aliphatic alcohol with at least one liquid aliphatic hydrocarbon. The mixture of alcohol and hydrocarbon is the preferred suspending medium, but only for economic reasons. When using the mixture, the upper limit of hydrocarbon is determined by the solubility of the alcohol-soluble thickener in the alcohol-hydrocarbon mixture, but will usually be a maximum of about 55%, and preferably, about 45% by weight of alcohol-hydrocarbon mixture. Up to about 45% hydrocarbon, the stability of the dispersion is not affected by the presence of the hydrocarbon. Between 45 and 55% hydrocarbon, some settling of particles takes place, but simple agitation redisperses the particles sufficiently to permit pumping of the suspension into an aqueous medium for dissolution. Any normally liquid, water immiscible aliphatic alcohol, either branched or straight chain, can be employed as the suspending alcohol. Thus, there can be used hexanol, heptanol, octanol, nonanol or decanol in either branched or straight chain configurations as well as such cyclic alcohols as cyclohexanol and cyclopentanol. The hydrocarbon portion, if used, can be any normally liquid, saturated or unsaturated aliphatic hydrocarbon, either straight or branched chain or cyclic, from C5 through about C17 or liquid aromatic hydrocarbons. The hydrocarbon can also be a mixture of such hydrocarbons and, in fact, for economic reasons will usually be such a mixture as mineral oil, kerosene, gasoline, No. 2 fuel oil, or some similar hydrocarbon mixture. The alcohol-soluble thickener is employed to maintain the polymer particles in suspension. Preferably, the thickener will be one which is also water-soluble to assure that it will not precipitate when the suspension is added to water. A highly preferred thickener is high molecular weight hydroxypropyl cellulose. Hydroxypropyl cellulose has an additional advantage in that it is generally compatible with most other water soluble polymers in aqueous solutions. It is critical, however, that the hydroxypropyl cellulose be one of high molecular weight. Such a material is "Klucel H" (Registered Trade Mark) sold by Hercules Incorporated. Other alcohol soluble thickeners which can be employed include ethyl cellulose of 1.4 to 1.8 D.S., ethyl hydroxyethyl cellulose of ethyl D.S. about 1.5 and hydroxyethyl D.S. up to about 0.5, and dihydroxypropyl hydroxypropyl cellulose DHP MS 1.6 and HP MS 7.4 (Example 7 of U.S. Patent 4,096,326). The suspension can also contain up to about 5% by weight of a surfactant. The preferred surfactant concentration is about 0.2 to 3%. This surfactant, when used, serves the dual purpose of increasing the pumpability of the slurry and aiding in the dissolution of the water soluble polymer when the slurry is added to water. Effective surfactants are those having HLB between about 10 and 20, which are effective for forming oil-in-water emulsions. Within the above limitations, substantially all classes of surfactants can be employed. Exemplary usable surfactants include ethoxylated polyol trioleates of HLB 11 (e.g., Atsurf 2822 by ICI); polyoxyethylene sorbitan stearate of HLB 14 to 15 (e.g., Tween 60 by ICI); polyoxyethylene sorbitan trioleate of HLB 11 (e.g., Tween 85 by ICI); polyoxyethylene lauryl alcohol of HLB 17 (e.g., Brij 35SP by ICI); and combinations of surfactants. Pumpability of the slurry is increased by the surfactant by virtue of a reduced slurry viscosity. In the absence of a surfactant, pumpability becomes marginal at about 40% by weight of particulate water soluble polymer. Use of the surfactant improves pumpability of a 408 by weight slurry. The second advantage gained by using a surfactant in the slurry is the improved polymer dissolution rate observed upon addition of the slurry to agitated water. While the polymer particles suspended in the liquid nonsolvent medium without a surfactant disperse in the water very readily, and ultimately dissolve to form clear solutions, they do not dissolve as rapidly as they do when the surfactant is present. Thus, within two minutes of charging into water, the polymer from a surfactant-free higher alcohol suspension may generate 508 of its ultimate viscosity, whereas from the same suspension containing a suitable surfactant, the polymer will usually generate at least 85% of its ultimate viscosity within two minutes. The method of the invention is useful with all known water soluble, alcohol insoluble polymers. In particular, it is useful with the cellulose ethers such as hydroxyethyl cellulose (HEC), carboxymethyl cellulose (CMC) and carboxymethyl hydroxyethyl cellulose (CMHEC). Cellulose ethers of any substitution level within the water soluble range can be treated by the method of the invention. Other examples of water soluble polymers are polysaccharides such as xanthan gum, carageenan, pectin, and guar gum, derivatized polysaccharides such as hydroxyalkyl guar; acrylamide polymers and copolymers; and ethylene oxide polymers. Not all of these polymers are subject to the dispersibility problems discussed above. All, however, can benefit from being handled in the suspension form provided by this invention as this form constitutes an excellent way of handling and charging of the polymer into a solvent system at a metered rate. In the examples which follow, parts and percentages are by weight unless otherwise specified. Viscosities are measured with a Brookfield Viscometer, using the i4 spindle at 30 r.p.m. When evaluating dispersibility and viscosity build-up, an amount of suspension sufficient to result in 1% polymer being present in the resultant solution was used. References to ultimate viscosity are to the viscosity measured 24 hours after adding the suspension to water. Example 1 A 1% solution of high m.w. hydroxypropyl cellulose (M.S. 3.6) was prepared by slowly adding 0.4 part of the HPC to the vortex of 39.7 parts of vigorously agitated 2-ethyl-lhexanol. Stirring was continued for four hours at a speed sufficient to effect adequate mixing without splashing. The solution was allowed to stand overnight and then stirred an additional two hours. A surfactant, 1.8 parts of an ethoxlated polyol trioleate of HLB 11 (Atsurf 2822 by ICI), was dissolved in 21.1 parts of deodorized kerosene. The two solutions were then combined and stirred for fifteen minutes. The mixture was then agitated sufficiently vigorously to form a good vortex and 37 parts of granular hydroxyethyl cellulose (HEC - high molecular weight, 2.5 M.S.) was added slowly to the vortex. When all the HEC was added, agitation was continued until a uniform suspension was prepared. No settling of the HEC was observed after the suspension had sat overnight. The viscosity of the suspension was 2200 cps. The suspension dispersed well with no lumping when added to water. Within two minutes, the solution viscosity was 4600 cps. or 84% of the ultimate viscosity of 5500 cps. measured after 24 hours. The solution was smooth and clear. When the same materials, omitting the surfactant, were employed in a suspension, dispersability was again excellent, but the viscosity of the solution after two minutes was only 2365 cps. or 39% of the 6000 cps. measured after 24 hours. When the dry granular HEC, with no dispersibility treatment, was added to water, it lumped very badly, indicating poor dispersibility. Example 2 A suspension which showed no settling on sitting for 72 hours was prepared, as in Example 1, consisting of 40 parts HEC, 38.8 parts 2-ethyl-l-hexanol thickened with 0.4 part of high molecular weight hydroxypropyl cellulose, 19 parts deodorized kerosene, and 1.8 parts Atsurf 2822 surfactant. Thissuspension had a viscosity of 4700 cps. Upon addition to water, dispersibility was excellent. Within two minutes a viscosity of 4860 cps. was measured, which is 86% of the 24 hour viscosity of 5640 cps. Examples 3 and 4 Example 2 was repeated using 40 parts HEC, 39.6 parts cyclohexanol, 0.4 part hydroxypropyl cellulose, and 20 parts deodorized kereosene with no surfactant. Dispersibility was excellent. The 2-minute viscosity was 4000 cps. or 70% of the 24-hour viscosity (5700 cps.). When n-hexanol was employed, dispersibility was excellent but the 2-minute viscosity (2730 cps.) was only 468 of the 24-hour viscosity (5900 cps.). Examples 5-10 Example 4 was repeated except that the ratio of components was varied as shown in Table I. The decrease of suspension viscosity with decreasing HEC content is also shown. TABLE I Composition (t by wt.) Ex. &num; HEC HPC Hexanol Kerosene Viscosity 5 38 0.4 40.9 20.7 4800 cps. 6 37 0.4 41.6 21 3500 cps. 7 36 0.4 42.2 21.4 3000 cps. 8 35 0.4 42.9 21.7 2700 cps. 9 34 0.3 43.7 22 2400 cps. 10 33 0.3 44.4 22.3 2100 cps. All of these suspensions were stable, and dispersed excellently in water and all dissolved rapidly. Example 11 The procedure according to Example 8 was repeated except that a fibrous HEC was employed instead of the granular material. The results were similar except that the suspension viscosity was about 1200 cps. greater than that experienced with the granular material. Examples 12 and 13 A suspension was prepared by stirring 37 parts of HEC (high M.W. - 2.5 M.S.) into 62.6 parts of n-hexanol thickened with 0.4 part of high molecular weight hydroxypropyl cellulose. No settling of the HEC was noted after sitting overnight. Viscosity of this suspension was 3500 cps. Similar results were observed with a suspension of 37 parts REC in 62.6 parts cyclohexanol thickened with 0.4 part hydroxypropyl cellulose. A suspension with 2-ethyl-l-hexanol in place of n-hexanol gave similar results. Example 14 Example 2 was repeated, using, as a surfactant, polyoxyethylene sorbitan trioleate ester of HLB 11 (Tween 85 by ICI). The suspension viscosity was 4400 cps. No settling was observed on sitting overnight. When added to water, the suspension had excellent dispersibility and no lumping was observed. The two minute viscosity in water was 5345 cps. or 79% of the ultimate viscosity of 6800 cps. Example 15 Example 2 was repeated using a polyoxyethylene sorbitan stearate ester of HLB between 14 and 15 (Tween 60 by ICI). The suspension viscosity was 4700 cps. and the suspension was stable with no settling overnight. Upon being added to water, the dispersibility of the suspension was excellent. The two minute viscosity was 5405 cps. or 82% of the ultimate viscosity of 6600 cps. Example 16 Example 2 was repeated using a polyoxyethylene lauryl alcohol of HLB about 17 (Brij 35 SP by ICI). Viscosity of this suspension was 4600. cps and there was no settling observed after overnight storage. When added to water, the dispersibility of the suspension was excellent. The two minute viscosity was 5565 cps. or 80% of the ultimate viscosity of 7000 cps. Example 17 Using the procedure described in Example 1, a slurry was prepared of a water soluble particulate carboxymethyl cellulose (CMC). This suspension had a viscosity of 1500 cps. It separated only very slightly after overnight storage. When added to water, dispersibility was excellent with no lumping observed. The two minute viscosity was 790 cps. or 79% of the ultimate viscosity. In contrast, the dry particulate CNC with no dispersibility treatment lumped excessively when added to water, indicating very poor dispersibility. The two minute viscosity was 380 cps. or about 548 of the ultimate viscosity of 700 cps. When this example was repeated using the polyoxyethylene lauryl alcohol surfactant instead of the surfactant of Example 1, the suspension was more stable, with no settling being observed after 48 hours of storage. Suspension viscosity was 2900 cps. When added to water, no lumping was observed. The two minute viscosity was 795 cps. o4 79.5% of the ultimate viscosity. Example 18 The procedure of Example 1 was repeated to prepare a suspension of a particulate carboxymethyl hydroxyethyl cellulose (carboxymethyl D.S. 0.4; hydroxyethyl MS. 2). The suspension viscosity was 1600 cps. and the suspension showed only slight settling after overnight storage. When added to water, no lumping was observed, indicating excellent dispersibility. The two minute viscosity was 1,00 cps. or 89% of the 24 hour viscosity. Equally good results with regard to dispersibility and dissolving rate in water were obtained with the polyoxyethylene lauryl alcohol surfactant, an additional advantage was a more stable suspension which showed no settling after overnight storage. Example 19 The procedure of Example 1 was repeated, using a water soluble particulate acrylamide sodium-acrylate copolymer as the suspended polymer and the polyoxyethylene lauryl alcohol surfactant. This suspension was stable and showed no separation or settling after 48 hours at room temperature. The suspension viscosity was 2800 cps. When adding the suspension to water, no lumping of the polymer was observed, indicating excellent dispersibility. The two minute viscosity was 4645 cps. or 95% of the ultimate viscosity of 4900 cps. Example 20 Following the procedure of Example 1, a suspension of dry particulate hydroxypropyl guar was prepared. The suspension showed no settling or separation after overnight storage. The suspension viscosity was 1600 cps. When added to water, no lumping was observed, indicating excellent dispersibility. The two minute viscosity was 89% of the ultimate viscosity of 3800 cps. Example 21 Example 1 was repeated using a glyoxal treated hydroxyethyl cellulose and the polyoxyethylene lauryl alcohol surfactant. The suspension was stable, showed no settling or separation after overnight storage. The suspension viscosity was 3000 cps. When adding the suspension to dilute sodium hydroxide solution at pH 12.5, no lumping was observed and the dispersibility in water was rated as excellent. The two minute viscosity build-up was 76% of the ultimate viscosity. In comparison, when the dry particulate glyoxal treated hydroxyethyl cellulose was added to the dilute sodium hydrox- ide solution at pH 12.5, some lumping was observed and the two minute viscosity build-up was only 37% of the ultimate viscosity. Example 22 Example 1 was repeated using toluene in place of deodorized kerosene, and polyoxyethylene lauryl alcohol surfactant. The suspension was stable, with no settling observed after a storage time of 48 hours The suspension viscosity was 3100 cps. When the suspension was added to water, no lumping was observed and the dispersibility was excellent. The two minute viscosity build-up was 77% of the ultimate viscosity. Example 23 Example 1 was repeated using Fractol A (Primol 205) a very high-boiling petroleum fraction, in place of deodorized kerosene, and polyoxyethylene lauryl alcohol surfactant. The suspension was stable, as no settling was observed after overnight storage. The suspension viscosity was 2200 cps. Dispersibility of the suspension in water was excellent, with no lumping being observed. The two minute viscosity build-up was 76% of the ultimate viscosity. Example 24 Example 1 was repeated using 0.18 part polyoxyethylene lauryl alcohol surfactant with 37 parts HEC, 39.7 parts 2ethyl-l-hexanol, 0.4 part hydroxypropyl cellulose, and 22.7 parts deodorized kerosene. The suspension was stable with no settling after overnight storage. Suspension viscosity was 2800 cps. When the suspension was dispersed in water, no lumping was observed and the dispersibility was rated as excellent. The two minute viscosity build-up was 93.5% of the ultimate viscosity. Example 25 Example 1 was repeated replacing hydroxypropyl cellulose with dihydroxypropyl hydroxypropyl cellulose (DHPHPC) (described in Example 7 of U.S. patent 4,096,326) and using polyoxyethylene lauryl alcohol surfactant. The composition of the suspension was 37 parts HEC, 1.5 parts DHPHPC, 38.6% 2-ethyll-hexanol, 21.1 parts kerosene, 1.8 parts surfactant. The suspension was stable after overnight storage with no settling observed. Suspension viscosity was 6800 cps. When added to water, the dispersibility was excellent, with no lumping observed. The two minute viscosity was 5060 cps. or 94% of the ultimate viscosity. Example 26 Example 25 was repeated using 1.1 parts of DHPHPC (described in Example 7 of U.S. patent 4,096,326). Concentration of other components in the suspension were 37 parts HEC, 39.0 parts 2-ethyl-l-hexanol, 21.1 parts deodorized kerosene, 1.8 parts surfactant. The suspension was stable after overnight storage, with no settling observed. Suspension viscosity was 4200 cps. The dispersibility was excellent, with no lumping observed when added to water. The two minute viscosity was 5040 cps. or 93% of the ultimate viscosity of 5400 cps. Examples 27 to 39 Example 1 was repeated except that polyoxyethylene lauryi alcohol was employed, and the proportions of 2-ethyl-l- hexanol, deodorized kerosene and HPC were varied as shown in the Table II. The effect of these changes on suspension stability and viscosity are shown also. TABLE II Composition (% by Weight) Alcohol Suspension Properties Example 2-Ethyl % HPC Hydrocarbon Overnight Viscosity (a) No. HEC HPC 1-Hexanol Kerosene Surfactant in Alcohol Ratio Stability (cps) 27 37 0.2 61 0 1.8 0.3 - VSS 600 28 37 0.2 39.7 21.1 1.8 0.5 1.88 S 200 29 37 0.4 39.7 21.1 1.8 1.0 1.88 NS 1600 30 37 0.3 38.5 22.6 1.8 0.8 1.70 S 400 31 37 0.6 38.5 22.6 1.8 1.6 1.70 NS 5000 32 37 0.3 36.7 24.7 1.8 0.8 1.49 S 200 33 37 0.6 36.7 24.7 1.8 1.6 1.49 NS 5200 34 37 0.3 35.1 26.1 1.8 0.85 1.34 S 300 35 37 0.6 35.1 26.1 1.8 1.7 1.34 NS 3800 36 37 0.3 33.3 27.8 1.8 0.9 1.18 S 200 37 37 0.6 33.3 27.8 1.8 1.8 1.18 NS 2400 38 37 0.6 30.6 30.6 1.8 2.0 1.00 S 600 39 37 0.6 27.5 33.7 1.8 2.2 0.82 S 200 (a) VSS - very slight settling S - settling NS - no settling This data shows that the quantity of HPC thickener required for a stable suspension depends on the alcohol/hydrocarbon ratio. If the alcohol/hydrocarbon ratio is too low, even 2.2% HPC based on alcohol will not yield a stable suspension. On the other hand, as little as 0.2% HPC based on the alcohol will yield a suspension with good overnight stability (only very slight settling) in the absence of hydrocarbon. TABLE III DISPERSIBILITY AND DISSOLVING RATE DATA Example No. 27 31 33 35 37 38 Dispersibility of Suspension* Excellent No lumping Two-Minute Viscosity Buildup (% of Ultimate Viscosity) 87 84 82 95 99 99* *Unstable suspensions were stirred to form a homogenous mixture prior to the disparsibility and dissolving rate test.

Claims: CLAIMS 1. A suspension consisting essentially of about 20 to 40% by weight of a particulate water soluble polymer, 0.2 to 1% by weight of an alcohol soluble thickener, 60 to 80% by weight of an organic liquid nonsolvent suspending medium, and 0 to 5% by weight of a surfactant having an HLB between about 10 and 20. 2. A suspension according to claim 1 wherein the liquid nonsolvent medium is a water immiscible aliphatic alcohol. 3. A suspension according to claim 1 wherein the liquid organic nonsolvent suspending medium is a mixture of-a water immiscible aliphatic alcohol and up to about 55% of a liquid aliphatic hydrocarbon or a mixture of such hydrocarbons. 4. A suspension according to claim 1 wherein the thickener is high molecular weight hydroxypropyl cellulose. 5. A suspension according to claim 1 wherein the water soluble polymer is hydroxyethyl cellulose, carboxymethyl cellulose, hydroxyethylcarboxymethyl cellulose, a polysaccharide, or a copolymer of acrylamide. 6. A stable suspension consisting essentially of about 20 to 40% by weight of particulate hydroxyethyl cellulose, 0.2 to 1% of alcohol soluble hydroxypropyl cellulose, 60 to 80% by weight of an organic liquid nonsolvent suspending medium, and 0.2 to 3% by weight of a surfactant having an HLB between about 10 and 20. 7. The suspension according to claim 6.wherein the liquid nonsolvent suspending medium comprises a water immiscible aliphatic alcohol. 8. The suspension according to claim 6 wherein the organic liquid nonsolvent suspending medium comprises a water immiscible aliphatic alcohol containing up to about 45% by weight of at least one liquid hydrocarbon. 9. The suspension according to claim 7 or 8 wherein the water immiscible aliphatic alcohol is hexanol, heptanol, octanol, nonanol, cyclohexanol or 2-ethyl-l-hexanol.

Inventors: REID, ALBERT RICHARD
Applicants: HERCULES INCORPORATED
Application year: 1981
Main classification: C08J3
IPC codes: C08J3