DERIVATIVES OF ARYL KETONES AS SENSITIZERS OF PHOTOPOLYMERIZABLE COMPOUNDS FOR THE VISIBLE SPECTRAL RANGE, AND PHOTOPOLYMERIZABLE COMPOSITIONS COMPRISING THE SAID SENSITIZERS

Abstract: This invention concerns sensitizers of photopolymeriz­ able compounds that absorb in the visible spectral range. The sensitizers are derived from dihydro-ethano(or propano)anth­ racene, or acetyl-tetrahydronaphthalene, or acetylindane, and dialkylaminoaryl aldehydes. This invention also concerns photopolymerizable compositions comprising said sensitiz­ ers.

Description: TITLE DERIVATIVES OF ARYL KETONES AS VISIBLE SENSITIZERS OF PHOTOPOLYMERIZABLE COMPOUNDS This invention concerns visible sensitizers of photopolymerizable compositions. The sensitizers are derived from dihydro-ethano(or propano)anthracene, or acetyltetrahydronaphthalene, or acetylindane, and dialkylaminoaryl aldehydes. This invention also concerns photopolymerizable compositions comprising said sensitizers. The ketone sensitizers of this invention have the formula: EMI1.1 wherein: R1 and R2 1 2. are R2 art each H, or R + R is -CH2-; R3 is H, or R3 + R5 is selected from (CH2)2, +CH2*31 and -CH(CH3)CH2C(CH3)2-; R4 is H, or R4 + R6 is. selected from QCH2t2 and (CH2)3; R5 and R6 are alkyl groups of 1 to 5 carbon atoms, or together are selected from (CH2)4 and -CH2,CH2,OCH2,Ch2-; R7 is selected from elected from EMI1.2 wherein: R8 is H or CH3; EMI2.1 n is 0 or 1, and when n is 1, R1and R2 are H; or (B) trimethylene and tetramethylene groups, unsubstituted, or substituted with 1 to 4 alkyl groups, R7 having a maximum of 8 carbon atoms. Preferred sensitizers for best performance, when R7 is (A), are those wherein R1, R2 and R8 are H and n is 0. Most preferred are compositions where R R2, R4 and R8 are H, R5 and R6 are each CH3 or C2H5, or R3+ R5 is -CH2CH2CH2-, and n is 0. Preferred sensitizers for best performance, when R7 is (B), are those wherein R1 and R2 are H, and R7 is unsubstituted. Most preferred are sensitizer compositions where R5 and R6 are each CH3 or C2H5, or 3 5. R3 + R5 is (CH2)3. The invention also concerns photopolymerizable compositions containing the sensitizers of Formula I. The photopolymerizable compositions of this invention comprise a combination of: (i) at least one nongaseous ethylenically unsaturated compound capable of forming a high molecular weight polymer by photo initiated addition polymerization; (ii) at least one 2,4,5-triarylimidazolyl dimer initiator consisting of two 2,4,5-triaryl imidazolyl radicals bound together by a single covalent bond; and (iii) at least one a,#-unsaturated ketone sensitizer of formula I. For practical considerations, it is preferred to employ a compound (i) which has a boiling point above 100 CC at normal atmospheric pressure. The photopolymerizable compositions can contain a polymeric binder to improve strength or to improve or effect adherence to a substrate. The relative concentrations of elements (i), (ii), and (iii), and the binder are as follows. The ethylenically unsaturated compound, (i), is present in an amount of about 3 to 100 parts per 100 parts of the combined weight of (i) and binder; the binder being present in an amount of 0 to about 97 parts per 100 parts of their combined weight. The initiator, (ii), is present in an amount of about 0.01 to 20 parts per 100 parts of the combined weight of (i) and binder. The sensitizer, (iii), is present in an amount of about 0.001 to 15 parts per 100 parts of the combined weight of (i) and binder, more preferably at about 1.0 to 10 parts per 100 parts. The photopolymerizable compositions of this invention can contain other additives in addition to binders. The types and amounts of such additives will be obvious to those skilled in the art. Several types of additives will be described hereafter. Preparation of Sensitizers When R7 Is (A) The sensitizers are prepared by reacting the known 9,10-dihydro-9,10-ethanoanthracene or 9,10dihydro-9,10-propanoanthracene with acetyl chloride or acetic anhydride in the presence of aluminum chloride to obtain as an intermediate the corresponding 2-acetyl or 2,6(7)-diacetyl derivative. With an excess of acylating agent, a mixture of the 2,6- and 2,7diacetyl derivatives is usually obtained. A typical reaction sequence for preparing the intermediate is: EMI4.1 Condensation of the intermediate acetyl compounds with a p-dialkylaminobenzaldehyde in the presence of a base, e.g., sodium hydroxide, gives the a unsaturated ketones, I, of the invention. Sensitizers of this invention wherein R1 + R2 is -CH2- can be prepared, for example, by the following reaction sequence: EMI4.2 EMI5.1 In the reaction sequences depicted above, carbonylation of the starting hydrocarbon with 1,1 dichioromethyl methyl ether in the presence of Ti Cl4 gives the corresponding aldehyde C. Condensation of C with malonic acid in the well-known Perkin or related condensation reaction can give D, and catalytic hydrogenation of D can give the substituted propionic acid E. Conversion of E to the acid chloride with PC15 followed by intramolecular Friedel-Crafts cyclization can give the cyclic ketones G. Preparation Of Sensitizers When R7 Is (B) These sensitizers are prepared by condensing the appropriate acetyltetrahydronaphthalene, acetylindane, or corresponding cyclic carbonyl compound, with a p-dialkylaminobenzaldehyde in the presence of a base such as sodium hydroxide, to give the a unsaturated ketones of the invention. Ketone starting materials wherein R1 = R2 = H are generally prepared by reaction of the corresponding hydrocarbons, e.g., tetrahydronaphthalene or indane, with acetyl chloride or acetic anhydride in the presence of aluminum chloride to obtain the desired acetyl derivatives. Cyclic ketones wherein R1 + R2 is -CH2- can be prepared by reaction of the corresponding hydrocarbon, e.g., tetrahydronaphthalene or indane, with S-chloropropionyl chloride in the presence of aluminum chloride to give the ss-chloropropionyl derivative followed by cyclization of this intermediate with concentrated sulfuric acid to give the desired cyclic carbonyl compound. Photopolymerizable Compositions The Ethylenically Unsaturated Compound (i) Contemplated monomers include those which form both water-soluble and water-insoluble polymers. Typical monomers are alkylene or polyalkylene glycol diacrylate prepared from an alkylene glycol of 2 to 15 carbons or a polyalkylene ether glycol of 1 to 10 ether linkages, and those disclosed in Martin and Barney, U.S. 2,927,022, e.g., those having a plurality of addition polymerizable ethylenic linkages, particularly when present as terminal linkages, and especially those wherein at least one and preferably most of such linkages are conjugated with a doubly bonded carbon, including carbon doubly bonded to carbon and to such hetero atoms as nitrogen, oxygen and sulfur. Outstanding are such materials wherein the ethylenically unsaturated groups, especially the vinylidene groups, are conjugated with ester or amide structures. The following specific compounas are illustrative of this class: unsaturated esters of alcohols, preferably polyols and particularly such of the alphamethylene carboxylic acids, e.g., ethylene glycol diacrylate, diethylene glycol diacrylate, glycerol diacrylate, glycerol iriacrylate, ethylene glycol di- methacrylate, 1, 3-propanediol dimethacrylate, 1,2,4-butanetriol trirnethacrylate, 1, 4-cyclohexanediol diacrylate, l,4-benzenediol cimethacrylate, penta erythritol tetramethacrylate, 1,3-propanediol diacrylate, 1,3-pentanediol dimethacrylate, the bisacrylates and methacrylates of polyethylene glycols of molecular weight 200-500, and the lie; ; unsaturated amides, particularly those of the alpha-methylene carboxylic acids, and especially those of alpha-omega- diamines and oxygen-interrupted omega-diamines, such as methylene bis-acrylamide, methylene bis-methacrylamide, ethylene bis-methacrylamide, 1, 6-hexamethylene bisacrylamide, diethylene thiamine tris-methacrylamide, bis(gamma-methacrylamidopropoxy)ethane beta-methacrylamidoethyl methacrylate, N- (beta-hydroxyethyl) -beta- (methacrylamido)ethyl acrylate and N,N-bis(beta methacryloxyethyl)acrylamide; ; vinyl esters such as divinyl succinate, divinyl adipate, divinyl phthalate, divinyl terephthalate, divinyl benzene-l , 3-disulfonate, and divinyl butane-1,4-disulfonate, styrene anc derivatives thereof and unsaturated aldehydes, such as sorbaldehyde (hexadienal). An outstanding class of these preferred addition polymerizable components are the esters and amides of alpha-rnethylenecarboxylic acids and substituted carboxylic acids with polyols arid polyamines wherein the molecular chain between the hydroxyls and amino groups is solely carbon or oxygen-interrupted carbon. The preferred monomertc compounds are polyfunctional, but monofunctional monomers can also be used. In addition, the polymerizable, ethylenically unsaturated polymers of Burg U.S. 3,043,805, Martin U.S. 2,929,710 and similar materials may be used alone or mixed with other materials. Acrylic and methacrylic esters of polyhydroxy compounds such as pentaerythritol and trimethylolpropane, and acrylic and methacrylic esters of abducts of ethylene oxide and polyhydroxy compounds such as those described in Cohen and Schoenthaler, U.S. 3,380,831 are also useful. The photocrosslinkable polymers disclosed in Schoenthaler, U.S. 3,418,295, and Celeste, U.S. 3,a48,089, may also be used. The amount of monomer added varies with the particular polymer used. Other useful ethylenically unsaturated compounds are the ethylenically unsaturated diester polyhydroxy polyethers described in U.S. Patents 3,661,576, 3,373,075 and 3,637,618. Many ethylenically unsaturated monomers are subject to thermal polymerization, especially when stored for long periods or at elevated temperatures. When such compounds are supplied commercially, it is customary for them to contain a small amount of a thermal polymerization inhibitor. These inhibitors can be left in the monomers when the photopolymerizable compositions of this invention are prepared, as was done in the Examples which follow. The resulting compositions usually have satisfactory thermal stability. If unusual thermal exposure is anticipated, or if monomers containing little or no thermal polymerization inhibitor are employed, compositions with adequate shelf life can be obtained by incorporating about 1 to 500 ppm by weight of monomer, of a thermal polymerization inhibitor such as hydroquinone, methyihydroquinone, p-methoxyphenol, and the nitroso dimer inhibitor systems described in Pazos, U.S. 4,168,982. The Initiator (ii) Dimers consisting of two 2,415-triarylimida- zolyl radicals bound together by a single covalent bond are photodissociable to the corresponding triarylimidazolyl radicals. The dimers absorb maximally in the 255 to 275 nm region, and usually show some lesser absorption in the 30.0 to 375 nm region. Although the absorption bands tend to tail out to include wavelengths as high as about 430 nm, they normally require radiation rich in the 255 to 375 nm region for their dissociation. Suitable 2,4,5-triarylimicazolyl dimmers include 2- (o-chlorophenyl) -4 ,5-diphenylimidazolyl dimer, 2- (o-chlorophenyl) -4 ,5-di (m-methoxyphenyl) imida- zolyl dimer, 2- (o-fluorophenyl) -4 ,5-diphenylimidazolyl dimer, 2-(o-methoxyphenyl)-4,5-diphenylimidazolyl dimer, 2-(p-methoxyphenyl)-4,5-diphenyllmidazolyl dimer, 2,4- di(p-methoxyphenyl)-5-phenylimidazolyl dimer, 2-(2,4 dimethoxyphenyl) -4 ,5-diphenylimidazolyl dimer, 2-tp- methylmercaptophenyl) -4, 5-diphenylimidazolyl dimer, and the like. Other suitable dimers are disclosed by Baum and Henry in U.S. Patent 3,652,275, column 5, line 44, to column 7, line 16, the disclosure of which is incorporated herein by reference. The imidazolyl dimmers can be used with a freeradical producing hydrogen or electron donor such 2-mercaptobenzoxazole, 2-mercaptobenzthiazole, Leuco Crystal Violet or tris(4-diethylamino-2-methylphenyl)methane. Other leuco dyes, e.g., those disclosed in U.S. Patent 3,652,275, column 7, line 24, to column 11, line 32, can also be used. By the term "leuco dye" is meant the colorless, i.e., reduced, form of a dye compound which can be oxidized to its colored form by the triarylimidazolyl radical. The Sensitizer (iii) The a,#-unsaturated ketone sensitizers of this invention, described broadly above, have been found to absorb radiation in the broad spectral range of about 300 to 700 nm. The maximum absorption (may) is in the range of about 350 to 550 nm and preferably about 400 to 500 nm. Other Additives It is preferred that the photopolymerizable compositions contain a polymeric binder which can serve to strengthen the composition or adhere it to a substrate. Radiation-transparent and film-forming polymer binders are preferred. Examples of suitable binders are thermoplastic macromolecular organic polymers which have number average molecular weights of at least about 1500, preferably at least about 4000, including such polymer types as: (a) copolyesters based on terephthalic, isophthalic, sebacic, adipic and hexahydroterephthalic acids; (b) nylons or polyamides; (c) vinylidene chloride copolymers; (d) ethylene/vinvl acetate copolymers; Ce) cellulosic ethers; (f) synthetic rubbers; (g) cellulose esters; (h) polyvinyl esters including polyvinyl acetate/acrylate and polyvinyl acetate/ methacrylate copolymers; (i) polyacrylate and a-alkyl- polyacrylate esters, e.g., polymethyl methacrylate, polyethyl methacrylate, and methyl methacrylate/ethyl acrylate copolymers; (j) high molecular weight polyethylene oxides of polyglycols having average molecular weights of about 4000 to 1,000,000; (k) polyvinyl chloride and copolymers; (1) polyvinyl acetal; (m) polyurethanes; (n) polycarbonates; (o) polystyrenes. In a particularly preferred embodiment of the invention, the polymeric binder is selected so that the unexposed photopolymerizable coating is soluble in predominantly aqueous solution, for example dilute aqueous alkaline solution, but upon exposure to actinic radiation becomes relatively insoluble therein. Typically, polymers which satisfy these requirements are carboxylated polymers such as vinyl addition polymers containing free carboxylic acid groups. A most preferred group of binders includes polyacrylate esters and poly-a-alkylacrylate esters which contain carboxyl groups; 'particularly prefrre are the polymethyl methacrylate esters. In preferred positive-working photopolymerizable compositions, nitroaromatic photoinhibitors as disclosed in U.S. 4,198,242 are present. These compounds are used in amounts of about 0.5 to 15 parts by weight per 100 parts of the combined weight of ethylenically unsaturated compound and binder. A wide range of nonpolymerizable plasticizers are effective in achieving improved exposure and develop- ment temperature latitude. When a macromolecular binder is present in the layer, plasticizer would be selected which is compatible with the binder as well as the ethylenically unsaturated monomer and other components of the composition. With acrylic binders, for example, plasticizers can include butyl phthalate and other esters of aromatic acids; esters of aliphatic polyacids such as diisooctyl adipate, and nitrate esters; aromatic or aliphatic acid esters of glycols, polyoxyalkylene glycols, aliphatic polyols; alkyl and aryl phosphates; low molecular weight polyesters of poly- > - methylstyrenes; chlorinated paraffins; and sulfonamide types can be used. In general, water insoluble plasticizers are preferred for greater high humidity storage stability, but are not necessary to get improved latitude. Other inert additives can be employed such as dyes, pigments and fillers. These additives are generally present in minor amounts so as not to interfere with the exposure of the photopolymerizable layer. Substrates For The Photopolymerizable Compositions The photopolymerizable compositions can be coated on a wide variety of substrates. By "substrate" is meant any natural or synthetic support, preferably one which is capable of existing in a flexible or rigid film or sheet form. For example, the substrate can be a metal sheet or foil, a sheet or film of synthetic organic resin, cellulose paper, fiberboard, and the like, or a composite of two or more of these materials. The particular substrate will generally be determined by the use application involved. For example, when printed circuits are produced, the substrate may be a plate which is a copper coating on fiberboard; in the preparation of lithographic printing plates, the substrate is anodized aluminum. Specific substrates include alumina-blasted aluminum, anodized aluminum, alumina-blasted polyethylene terephthalate film, polyethylene terephthalate film, e.g., resinsubbed polyethylene terephthalate film, polyvinyl alcohol-coated paper, cross-linked polyester-coated paper, nylon, glass, cellulose acetate film, heavy paper such as lithographic paper, and the like. An antihalation material can be used beneath the photopolymerizable layer, for example, in the substrate or on its surface. When an antihalation layer is used between the photopolymerizable layer and the substrate, the layer must have adequate adhesion to the substrate and the photopolymerizable layer and not react with the radiation-adsorptive material. Antihalation pigments and resin carriers are described in British Patent 1,366,769. The photopolymerizable composition is usually applied to the substrate as a solution or dispersion in a carrier solvent. The solution or dispersion can be sprayed, brushed, applied by a roller or an immersion coater, flowed over the surface, picked up by immersion or applied to the substrate by other suitable means. The solvent is then allowed to evaporate. In general, solvents are employed which are volatile at ordinary pressures. Examples of suitable solvents include water; amides such as N,N-dimethylfcrmamide and N,Ndimethylacetamide; alcohols and ether alcohols such as methanol, ethanol, 1-propanol, 2-propanol, butanol, ethylene glycol, 2-butoxyethanol, and 2-ethoxyethanol; esters such as methyl acetate and ethyl acetate; aromatic hydrocarbons and aromatic halocarbons such as benzene, o-dichlorobenzene and toluene; ketones such as acetone, 2-butanone, and 3-pentanone; aliphatic halocarbons such as l,l,l-trichloroethane, methylene chloride, chloroform, l,l,2-trichloroethane, 1,1,2,2-tetrachloroethane, 1,1,2-trichloroethylene; miscellaneous. solvents such as dimethyl sulfoxide, pyridine, tetrahydrofuran, 1 ,2-dimethoxyethane, dioxane, dicyanocyclo- butane, N-methylpyrrolidone; and mixtures of these solvents in various proportions as may be required to attain solutions. Alternatively. the photopolymerizable composition can be formed into a film and the film can be applied to the substrate. Preferably the layers of the photopolymerizable compositions have a thickness ranging from about 0.0001 inch (¯ 2 5 Vm) to 0.01 inch ( ¯250 Vm) and are applied to a thin, flexible, polymeric film support which can transmit actinic radiation to the photopolymerizable layer. The opposite side of the photopolymerizable layer can have adhered thereto a protective cover layer or cover sheet wherein the sheet has less adhesion to the layer than to the film support. A particularly preferred support is a transparent polyethylene terephthalate film having a thickness of about 0.001 inch (- 25 Ism). Polyethylene, 0.001 inch (,25 Vm) is a preferred cover sheet; polyvinyl alcohol coating is a preferred cover layer. Any convenient source of actinic radiation providing wavelengths in the region of the spectrum that overlap the ,Q-unsaturated ketone sensitizers absorption bands can be used to activate the photopolymerizable compositions for triarylimidazolyl radical formation, image formation and photopolymerization initiation. The radiation can be natural or artificial, monochromatic or polychromatic, incoherent or coherent, and for high efficiency should correspond closely in wavelengths to the sensitizer's principal absorption bands and should be sufficiently intense to activate a substantial proportion of the sensitizer. Conventional radiation sources include fluorescent lamps, mercury, metal additive and arc lamps providing narrow or broad radiation bands centered near 405, 436 and 546 nm (Hg) wavelengths. Coherent radiation sources are the pulsed xenon, argon ion and/or ionized neon-lasers whose emulsions fall within or overlap the visible absorption bands of the sensitizer. Ultraviolet and visible emitting cathode ray tubes widely useful in printout systems for writing on photosensitive materials are also useful with the subject compositions. These cathode ray tubes comprise an ultraviolet or visible-emitting phosphor internal coating as the means for converting electrical energy to light energy and a fiber optic face plate as the means for directing the radiation to the photosensitive target. Electron accelerators and electron beam sources through an appropriate mask are also suitable. The radiation exposure times can vary from fractions of a second to minutes, depending upon the intensity and spectral energy distribution of the radiation used, its distance from the photopolymerizable layer, and the nature and amounts of the unsaturated compounds in the layer. Customarily, a distance of about 1.5 to 60 inches (3.8 to 153 cm) from the photopolymerizable layer is used. Exposure temperatures are not particularly critical, but it is preferred to operate at about ambient temperatures or slightly higher, i.e., about 200 to 500C. Imagewise exposure is conveniently carried out by exposing the photopolymerizable element to actinic radiation through a process transparency, that is, an image-bearing transparency consisting of areas substantially opaque and substantially transparent to the radiation being used, where the opaque areas can be substantially of the same optical density; for example, a so-called line or halftone negative or positive. Suitable process transparencies also include those with a graded range of opaque areas; for example, a continuous tone negative. Process transparencies can be constructed of any suitable materials including cellulose acetate film and polyester film. After exposure, the image is developed. Development can be by toning, i.e., dusting with a fine pigment which selectively adheres to the tacky unhardened areas, by dye imbibition or by modulation of diffusion. Generally, however, the portions of the layer corresponding to the unexposed portions are removed, e.g., in lithographic applications. ThQk method of development can be achieved by pressure transfer, differential adhesion of the exposed versus unexposed areas, use of peel apart transfer, and, preferably, by solvent washout. The solvent liquid used for development should have good solvent action on the nonpolymerized portions of the composition, and little action on the insolubilized image in the time required to remove the soluble portions. U 4 t'J The photopolymerizable compositions of this invention have very little residual color and good solubility and shelf life, They are useful in printing plates for offset and letter press, engineering drafting films, as well as photoresists in making printed circuits or in chemical milling, and as solder masks. They are also useful in the preparation of video disks. In #rinting plate applications, an important use is in a positive/ negative two-exposure imaging system of a positive photopolymer litho printing plate. The compositions are also useful in positive working photopolymer litho films. Still other uses are for preparing colored images from color separation negatives suitable for color-proofing. The images formed with these elements can be used for making copies by thermal transfer to a substrate. Other specific uses will be evident to those skilled in the art. In photoresist applications, thin film resists prepared from the composition are useful in the preparation of microcircuits. The resists can be either solvent soluble or aqueous developable. Solder masks are protective coatings which are selectively applied to portions of a printed circuit board surface to confine solder to pad areas on the board and to prevent bridging between conductors during tinning operations and during soldering of components. A solder mask also functions to prevent or minimize corrosion of the base copper conductors and as a dielectric to insulate certain components for adjacent circuitry. Photopolymerizable compositions containing the a,#-unsaturated ketone sensitizers of this invention show good visible light sensitization. The increase in speed results in a saving of energy and costs related thereto since lower energy exposure sources can be used in exposure of the photopolymerizable element or more elements can be exposed and developed in a given amount of time. Alternatively, the photopolymerizable layer can be exposed by means of an exposure source maintained at a greater distance than normal for known sensitized elements. This permits the exposing radiation to be collimated which is of particular advantage in forming halftone dots having substantially perpendicular sides. The broad sensitization range coupled with the effectiveness of sensitization enables useful positive polymeric images to be formed by a double exposure process, first, imagewise in the ultraviolet region of the spectrum and when overall in the visible region of the spectrum utilizing specific nitroaromatic photoinhibitors. The following Examples illustrate the invention. All parts and percentages are by weight and all degrees are Celsius unless otherwise stated. Examples 1 to 5 and 16 to 18 describe preparation of sensitizers wherein R7 is (A) and Examples 6 to 15 and 19 to 21 describe the preparation of photopolymerizable compositions containing said sensitizers. Examples 22 to 30 describe preparation of sensitizers wherein R7 is (B) and Examples 31 to 39 describe preparation of photopolymerizable compositions containing said sensitizers. EXAMPLES 1 TO 21 Preparation Of Intermediates For Making Sensitizers Wherein R7 Is (A) The reactant, 2-acetyl-9 , 10-dihydro-9 , 10- ethanoanthracene, was prepared by the following procedure. To a stirred solution of 100 g (0.485 M) of 9,10-dihydro-9,10-ethanoanthracene and 50 g (0.49 M) of acetic anhydride in 500 ml of dichloroethane was added 135 g (1.01 M) of aluminum chloride in portions at 0 to 100 over a 1.5-hour period. The pale brown mixture was stirred at room temperature overnight and decomposed by successive addition of 500 ml of water and 100 ml of 6N HC1. The organic layer was separated and the aqueous layer was extracted twice with CH2Cl2; washed with brine, dried and evaporated. The residual viscous oil was crystallized from hexane to give 100.8 g (84.4%) of 2-acetyl-9 ,10-dihydro-9 ,10-ethanoanthracene. M.p., 910 to 920; Pmr (CDC13) 6 1.67 (t, 4H, bridge), 2.52 (s, 3H, Cm3), 4.37 (s, 2H, bridge head), 6.95-7.35 (m, 5H), 7.60-7.90 (dxd and d, 2H). The reactant, 2,6(7)-diacetyl-9,10-dihydro-9, 10-ethanoanthracene, was prepared as follows. To a gray suspension of 100 g (0.75 M) of AlCl3 in 125 ml of dichloroethane was added 35 ml (0.37 M) of acetic anhydride at 200 to 250 over 1 hour. A solution of 21 g (0.10 M) of 9,10-dihydro-9,10-ethanoanthracene in 125 ml of dichloroethane was added at 200 over a 30 minute period. The dark brown- suspension was stirred at room temperature overnight, heated to distill about 125 ml of the solvent, cooled, and poured into ice water containing 80 ml of concentrated HC1. The organic layer was separated and the aqueous layer was extracted with CH2Cl2 twice. The combined organic extracts were washed with saturated sodium chloride solution, dried and evaporated. A toluene solution of the dark residual oil was treated with charcoal, filtered, evaporated, and the residue was vacuum distilled by a bulb-to-bulb distillation from a 2000 air bath to give 18.0 g (62%) of a mixture of 2,6(7)-diacetyl-9 ,l0-dihydro-9 ,l0-ethanoanthracene as an amber glass. The pmr in CDC13 showed excess acetyl group. Pmr in CDCl3: 1.65 (s, 4.1H, bridge), 2.50 (s, 6.9H, CH3), 4.45 (s, 2.0 H, bridgehead), 7.30 (d J# ¯ 8 Hz, 2.3 H, arom), 7.73 (d x d J#8, 1.5 Hz, 2.0 H, arom), 7.90 (d J¯ 1.5 Hz, 2.0 H, arom). EXAMPLE 1 3-[4-(Dimethylamino)phenyl]-1-(9,10-dihydro-9,10- ethanoanthracen-2-yl)-2-propen-1-one (2) EMI19.1 A solution of 2.3 g of p-dimethylaminobenzaldehyde (15 mmole), 3.7 g of 2-acetyl-9,10-dihydro-9, 10-ethanoanthracene (1) (15 mmole) and 0.66 g of sodium hydroxide (16.5 mmole) in 100 ml of ethanol was stirred under nitrogen at 40e to 456 for 18 hr. A yellow solid precipitated which was separated by filtration and recrystallized from 300 ml of ethanol to give 1.1 g of the product i, 3- [ 4-(dimethylamino)phenyl3-1-(9,10- dihydro-9 , 10-ethanoanthracen-2-yl) -2-propen-1-one. Partial evaporation of the filtrate and addition of water to a final volume of about 100 ml (25% water) gave, on cooling, an additional 2.1 g of product. On standing, an additional 1.0 g of 8 was precipitated from the reaction mixture: total yield, 4.2 g (74%). Mp 1840 to 1860. Xmax (C2H5OH): 418 nm (e = 33,500), 270 nm (15,200). Calcd for C27H25NO: C, 85.45; H, 6.64; N, 3.69. Found: C, 85.06, 84.91; H, 6.89, 6.92; N, 3.66, 3.65. EXAMPLE 2 3- [ 4-(Diethylamino)phenyl ] -1-(9,10-dihydro-9,10- ethanoanthracen-2-yl)-2-propen-l-one EMI20.1 A solution of 14.3 g of p-diethylaminobenzaldehyde (0.0805 M), 20.0 g of #1 (0.0805 M) and 3.6 g of sodium hydroxide (0.090 M) in 400 ml of ethanol was stirred under nitrogen at about 620 for 48 hr. The reaction mixture was cooled to 0 and the precipitated solid product was separated by filtration and washed with cold ethanol to give 17.6 g (54% yield) of the product #,4, [ 4- (diethylamino)phenylj -1(9 ,10-dihydro- 9,10-ethanoanthracen-2-yll-2-propen-1-one. The filtrate was evaporated and the residue taken up in ether and water. The organic layer was washed with water, dried, and evaporated to give a red oil which was dissolved in ether and the solution was passed through a column of neutral alumina. The ether was evaporated and the residue dissolved in 100 ml of hot ethanol. Slow cooling of this solution until precipitation occurred followed by cooling in an ice bath yielded an additional 7.6 g (23% yield) of A sample of product prepared on a 0.015 M scale was recrystallized from cyclohexane. Mp 1000 to 1010. Amax (CHC13): 423 nm (E = 27,700), 280 nm (16,900). Calcd for C29H29NO: C, 85.46; H, 7.17; N, 3.44. Found: C, 85.11; H, 7.10; N, 3.21. EXAMPLE 3 1- (9 ,10-Dihvdro-9 ,10-ethanoanthracen-2-vl) -3- (1,2,6,7- tetrahydro-3H,5E-benzot uinolizin-9-vl)-2- propen-l-one (4,) EMI21.1 A solution of 3.0 g of 9-formyl-1,2,6,7- tetrahydro-3H,5H-benzc Li, j ] quinoline (15 mmole), 3.7 g of 1 (15 mmole) and 0.66 g of sodium hydroxide (16.5 mmole) in 75 ml of ethanol was stirred under nitrogen at about 600 for 30 hr. After the reaction mixture stood at room temperature for 64 hr, a red solid separated which was isolated by pouring off the supernatant liquid. The solid was dissolved in boiling cyclohexane, and the solution was filtered to remove a small amount of dark solid. After cooling, 1.4 g (22%) of orange solid 1-(9,10-dihydro-9,10-ethanoanthracen- 2-yl)-3-(1,2,6,7-tetrahy ro-3H,5H-benzo [ i,j ] quinolizin- 9-yl)-2-propen-1-one was obtained. Mp 1030 to 1050 with some initial softening at 840 to 860. Amax (CHCl3): 440 nm CE = 25,700), 363 nm (8,920), 274 nm (15,400). Calcd for C31H29NO: C, 86.27, H, 6.77; N, 3.24. Found: C, 84.43, 84.35; H, 6.69, 7.01; N, 3.20, 3.05. Water and ether were added to the supernatant liquid and the organic layer was washed with water, dried and evaporated to give a dark oil. The oil was dissolved in boiling cyclohexane and filtered to remove some dark material. The filtrate was combined with the mother liquor of the previous recrystallization, evaporated to about 100 ml, and allowed to stand overnight. A dark oil separated. On cooling in ice the dark oil became solid and yellow crystals separated. The yellow crystals were filtered off and dried to give an additional 1.0 g of product. Evaporation of'the mother liquor gave an additional 0.8 g. Total yield: 3.2 g (49%). EXAMPLE 4 2,6(7)-Bis[p-(diethylamino)cinnamoyl]-9,10-dihydro- 9,10-ethanoanthracene C6) EMI23.1 A solution of 1.77 g of p-diethylaminobenzaldehyde (10 mmole), 1.45 g of a mixture of 2,6-diacetyl9,10-dihydro-9,10-ethanoanthracene and 2,7-diacetyl-9, 10-dihydro-9,10-ethanoanthracene (? (5 mmole) and 0.22 g of sodium hydroxide (5.5 mmole) in 30 ml of ethanol was stirred under nitrogen at about 600 for 4 hr. Then the volume was increased to 50 ml by addition of ethanol, and the reaction mixture was heated at reflux for 18 hr. On cooling a dark yellow solid separated which was filtered off. Yield of condensation product, 6, was 0.70 g (23%). Melting range 1700 to 1750. The filtrate was diluted with chloroform and the organic layer was washed with water. Evaporation gave a dark red oil which was chromatographed on silica gel. Elution with methylene chloride gave 0.6 g (20%) of a dark yellowred solid. X max (CHCl3) 424 nm (e = 33,400), 265 nm (e = 36,200) . Calcd for C42H49N2O2: C, 82.86; H, 7.28; N, 4.60. Found: C, 80.14, 80.76; H, 7.08, 6.93; N, 3.93, 3.85. EXAMPLE 5 2,6(7) -Bis[p-(dimethylamino) cinnamoyl]-9,10-dihydro- 9,10-ethanoanthracene () EMI24.1 A solution of 0.745 g (5 mmole) of p-dimethylaminobenzaldehyde, 0.725 g (2.5 mmole) of a mixture of 2,6(7) -diacetyl-9 ,10-dihydro-9 ,10-ethanoanthracene (5), and 0.11 g (2.75 mmole) of sodium hydroxide in 30 ml of ethanol was heated and stirred at 600 under nitrogen for 65 hours. An additional 10 ml of ethanol was added and the reaction mixture was heated under reflux an additional 8 hr and then cooled slowly to 00. The precipitated solid was separated, washed with ethanol, and dried to give 0.6 g (43% yield) of condensation product, 7. Amax (CHCl3) 423 nm (± = 29,200); 263 nm (± = 32,200). Calcd for C38H36N2O2: C, 82.58; H, 6.57; N, 5.07. Found: C, 78.35, 78.38; H, 6.23, 6.18; N, 3.92, 4.03. EXAMPLES 6 TO 11 The oriented polyester films employed as substrates in Examples 6 to 11 were 4-mil (102 #m) polyethylene terephthalate films which were sub-coated with a copolymer resin comprising a sequentially polymerized mixture of a vinylidene chloride/alkyl acrylate/itaconic acid copolymer and an alkyl acrylate polymer as described by Rawlins in U.S. Patent 3,443,950. To the copolymer resin, before coating, was added a methyl methacrylate:ethyl acrylate:acrylic acid (37:56:7) terpolymer (molecular weight 260,000 and acid number 76-85), dispersed with ammonia. The coated films were stretched and a thin layer of the terpolymer in water was added onto the first sub-coating. The radiation source used for the exposure of the photosensitive elements of these Examples was a 4 KW pulsed xenon arc (Macbeth) at a distance of 60 inches (152 cm). The exposed elements were processed through an automatic processor in which the film is fed, image up, in a straight through path into a development section, then to a rinse section, and finally to a drier section, as described by Hamlin in U.S. Patent 4,142,194, at rates as specified in each Example. Processing temperature was 22.2 , and the solvent was an aqueous solution of a mixture of potassium carbonate and potassium bicarbonate. The processed elements were rinsed with water in the rinse chamber at 32.2 . EXAMPLE 6 The following photopolymerizable composition was prepared: Aqueous ComPonent Wt. Used (g) Distilled water 68.6 Acryliclatex binder ("Acrysol" I-94, 34.8 Rohm & Haas Co.) 40% Polyethylene wax dispersed in 10.0 water C"Misco" AC-392, Misco Products Co., Wheeling, Illinois) Octylphenory polyethoxyethanol dispersing 3.0 agent, ("Triton" X-100, Rohm & Haas Co.), 10% solution Zinc complex solution (ammonium carbonate, 3.1 ammonia,'zinc oxide, water solution; 7.2% zinc) Organic Component Tetraethylene glycol dimethacrylate 1.7 Trimethylolpropane triacrylate 1.7 Sensitizer from Example 2 0.1 6-Nitroveratraldehyde photoinhibitor 0.56 2- (o-Chlorophenyl) -4, 5-diphenylimidazolyl 0.6 diner 2- (o-Chlorophenyl) -4, 5-di (m-methoxyphenyl) - 0.6 imidazolyl diner Methylene chloride 8.5 Both components were combined and the mixture was emulsified for 5 minutes in a blender. To the emulsion was added 2 g of a 25% water solution of a fluorinated hydrocarbon surfactant having the following chemical structure: (C8F17SO2N(C2H5)CH2CO2) K The mixture was coated on the resin-subbed side of an oriented polyethylene terephthalate film substrate using a 2-mil (#51-um) doctor knife. The coating was dried with a hot air gun. The dried film was heated at 950 to 1000 for 5 minutes and an oriented polyethylene terephthalate film cover sheet was laminated thereon. Portions of this photosensitive element were exposed to radiation for periods of 5 to 25 seconds through a process transparency in contact with the cover sheet. The process transparency was removed and the elements reexposed overall for 40 seconds to radiation through a cut-off filter which absorbed all radiation below 400 nm. The elements were processed through the automatic processor at a rate of 87 in/min (221 cm/min) to produce a good clean positive image. EXAMPLE 7 The photopolymerizable composition of Example 6 was prepared except that the sensitizer from Example 2 was replaced with 0.22 g of the sensitizer from Example 3. A portion of the photosensitive element prepared from the emulsified composition was exposed to radiation for 10 seconds through a process transparency in contact with the cover sheet. The process transparency was removed and the element reexposed overall for 25 seconds to radiation through the cut-off filter. The element was processed through the automatic processor at a rate of 49 inches/min (124 cm/min) to produce a clear positive image with a low level of background. EXAMPLE 8 The photopolymerizable composition of Example 6 was prepared except that the sensitizer from Example 2 was replaced with 0.20 g of the sensitizer from Example 1. A portion of the photosensitive element prepared from the emulsified composition was exposed to radiation for 10 seconds through a process transparency in contact with the cover sheet. The process transparency was removed and the element reexposed overall for 25 seconds to radiation through the cut-off filter. The element was processed through the automatic processor at a rate of 49 inches/min (124 cm/min) to produce a sharp positive image on an almost clear background. EXAMPLES 9 TO 11 Photopolymerizable compositions were prepared as described in Examples 6 to 8 and photosensitive elements were prepared from each of these compositions. Portions of the photosensitive elements were exposed to radiation through the cut-off filter without a process transparency for a time sufficient to obtain a full density, shiny, image in each Example. The exposed elements were processed through the automatic processor at the maximum rate in which the unexposed composition was removed (clearing rate). Results are summarized in Table 1. TABLE 1 Relative Example Sensitizer from Example Photospeed 9 2 1.2 10 3 1.5 11 1 1.0 EXAMPLE 12 The following stock solution was prepared: Component Wt. (g) Tetraethylene glycol dimethacrylate 15.0 Terpolymer of ethyl acrylate/methyl 35.3 methacrylate/acrylic acid (56/37/7) MW 260,000 Copolymer of styrene/maleic anhydride 36.7 (58/42), esterified, MW 10,000 2- (o-Chlorophenyl) -4, 5-diphenylimidazolyl 8.6 dimer Methylene chloride 527 Methanol 40 To 10 g of this stock solution were added 0.0407 g of 6-nitroveratraldehyde photoinhibitor and 0.0140 g of the sensitizer from Example 1. Portions of this solution were board coated with a 2-mil (51-pm) doctor knife on the resin-subbed side of the oriented polyester film substrate described in Example 6, and the coatings were air-dried. The dried coatings were laminated with a 1-mil (25-prll) oriented polyester film coversheet at 820 at a rate of 4 ft/min (1.22 m/min) at 40 psi (276 kPa). One half the surface of a photosensitive element was covered by a black polyethylene sheet. A t2 step wedge process transparency was placed over the uncovered side and the plate was placed in a vacuum printing frame. An imagewise exposure (positive exposure) was made to radiation from a 2 KW Berkey mercury photopolymer lamp at a distance of 38 in (96 cm) for a time which corresponds to a radiation dosage of 10 units. The polyethylene sheet was removed and a Y2 step wedge was placed over the previously blocked-off section. A U.V. cut-off filter which absorbed essentially all radiation below about 420 nm was placed over the plate and the entire plate was given a 30 unit exposure. This final exposure gave a negative exposure to the blocked-off section and completed the two-exposure positive sequence on the other half. The exposed element was developed at 220 in a solution prepared from 1536 g of distilled water, 84 g of potassium carbonate¯1,5 B20, and 5 g of potassium hydrogen carbonate, and the developed element was rinsed with a 320 water spray at 40 psi (276 kPa). A development time of 10 seconds gave a positive mode speed of 1, i.e., the first step of the positive image was completely unpolymerized, and a negative mode speed of 10, i.e., the negative image showed 10 full and partial polymerized steps. EXAMPLES 13 TO 15 Photopolymerizable compositions were prepared, exposed, and developed as described in Example 12 except that the sensitizer from Example 1 was replaced with the sensitizers shown in Table 2 and a development time of 6 seconds was used. The results, summarized in Table 2, show that a good image was obtained in each instance. Table 2 Photopolymerization Speed Positive Negative Example Sensitizer, g Mode Mode 13 Example 2, 2 10 0.0151 14 Example 3, 6 10 0.0160 15 Example 4, 7 5 0.0112 EXAMPLE 16 3-[4-(1-Pyrrolidino)phenyl]-1-(9,10-dihydro-9,10- ethanoanthracen-2-yl) -2-propen-l-one (t) EMI30.1 A solution of 3.7 g of 2-acetyl-9,10-dihydro9,10-ethanoanthracene t15 mmole), 2.6 g of p-(lpyrrolidino)benzaldehyde (15 mmole), 0.66 g of sodium hydroxide (16.5 mmole) in 100 ml of ethanol was stirred under nitrogen at 40e to 500 for 30 hr. The reaction mixture was allowed to stand an additional 60 hr at 250. A yellow solid which precipitated was separated from the cooled (ice bath) reaction mixture and washed with cold ethanol to give 4.2 g (69% yield) of the reaction product 8, mp 1620 to 1640. Amax (CHC13) 422 nm (e = 31,300), 330 nm (Sh; 4240), 277 nm (22,700). The nmr spectrum was consistent with the assigned structure. Calcd. for C29H27NO: C, 85.89; H, 6.71; N, 3.45. Found: C, 85.01, 85.32; H, 6.60, 6.63; N, 3.24, 3.19. EXAMPLE 17 3-14-(4-Morpholino)phenyl ] -l-(9,10-dihydro-9,10- ethanoanthracen-2-yl)-2-propen-1-one (Q) EMI31.1 A solution of 3.72 g of 2-acety1-9,10#dihydro 9,10-ethanoanthracene (15 mmole), 2.87 g of p-(4morpholino)benzaldehyde (15 mmole), and 0.66 g of sodium hydroxide (16.5 mmole) in 100 ml of ethanol was stirred under nitrogen at about 500 for 26 hr. The reaction mixture was cooled to 0 and the yellow solid product separated by filtration and washed with cold ethanol to give 4.1 g C65% yield) of the product, #, mp 1423 to 1450. Amax CCHCl3): 382 nm (s = 21,100), 272 nm (16,400). Calcd. for C29H27NO2: C, 82.63; H, 6.46; N, 3.32. Found: C, 82.60; H, 6.42; N, 3.17. EXAMPLE 18 3- (1-Ethyl-1,2, 3 ,4-tetrahydroguinol-6-yl) -1- (9 ,10-di- hydro-9, l0-ethanoanthracen-2-yl )-2-propen-l-one (#) EMI32.1 EMI32.2 A solution of 3.7 gof 2-acetyl-9,10-dihydro- 9,10-ethanoanthracene (15 mmole), 2.8 g of l-ethyl 1,2,3, 4-tetrahydroquinoline-6-carboxaldehyde (15 mmole), and 0.66 g of sodium hydroxide (16.5 mmole) in 90 ml of ethanol was stirred under nitrogen at about 500 for 24 hr. The reaction mixture was poured into a mixture of ether and water, the organic layer was separated washed with water, and dried over sodium sulfate. Evaporation of the ether left 4.0 g (64% yield) of yellow solid product 10, mp 700 to 720. The nmr spectrum was consistent with the assigned structure. Amax (CHCl3): 433 nm (E = 21,500), 356 nm (9490), 272 nm (15,300). EXAMPLES 19 TO 21 Photopolymerizable compositions were prepared, exposed, and developed as described in Example 12 except that the sensitizer from Example 1 was replaced with the sensitizers shown in Table 3, and a development time of 7 seconds was used. The results, summarized in Table 3, show that a good image was obtained in each instance. TABOR 3 Photoolymerization Speed Positive Negative Example Sensitizer, g Mode Mode 19 Example 16, 1 10 0.0150 20 Example 17, 4 7 0.0156 21 Example 18, 6 9 0.0155 EXAMPLES 22 TO 39 Preparation Of Intermediates For Making Sensitizers Wherein R7 is (B) The reactant, 1- (2,3-dihydro-lH-inden-5-yl) - ethanone (5), was prepared by the following procedure. To a 3-necked 1 liter round bottom flask equipped with a stirrer was added 60 g of indane and 50 g of acetyl chloride dissolved in 500 ml of methylene chloride. The reaction flask was cooled in an ice bath, and aluminum chloride (75 g) was added slowly through a piece of large rubber tubing. After the addition had been completed, the reaction mixture was heated under reflux for 2 hr with vigorous evolution of hydrogen chloride gas. The reaction mixture was cooled and poured into ice water which contained 50 ml of concentrated hydrochloric acid. The reaction mixture was extracted with ether and the ether extracts were combined and dried. The ether was evaporated and the residue distilled at 1500 and water aspirator pressure to give 33.1 g (41%) of 1-(2,3-dihydro-lH-inden-5-yl)ethanone. The reactant, 6-acetyl-1,2,3,4-tetrahydronaphthalene (1), is prepared from 1,2,3,4-tetrahydronaphthalene by a similar procedure. The preparations of 3,5,6,7-tetrahydro-5 indacen-1(2H)-one (8, s-hydrindacen-l-one) and 2,3,5,6,7,8-hexahydro-lH-benz(f)inden-l-one (12) are described in detail by Dufour et al., J.C.S. Perkin I, p 527 to 530 (1972). Compound 8 was prepared as follows: Into a solution of hydrindene and e-chloro- propionyl chloride in methylene chloride, powdered aluminum chloride was stirred during 1 hr at 180; the solvent was then distilled off, the cooled residue was treated dropwise with sulphuric acid, and the mixture was heated. After decomposition with ice and extraction of the product in ether, the ketone was purified by distillation in vacuo and recrystallization from hexane. Compound 12 was prepared by an alternate procedure as follows. Tetralin was formylated with dichloromethyl methyl ether and titanium tetrachloride catalyst to give 6-formyltetralin. Reaction of the aldehyde with malonic acid in the presence of an amine catalyst gave the substituted acrylic acid. Catalytic hydrogenation of the double bond gave the corresponding substituted propionic acid, 3-(6-tetralyl)propionic acid. Conversion of the acid to the acid chloride with phosphorus pentachloride followed by cyclization with aluminum chloride gave the desired. 2,3,5,6,7, 8-hexahydro-lH-benz (f ] inden-l-one. EXAMPLE 22 3-[4-(Dimetnylamino)phenyl]-1-(5,6,7,8-tetrahydro- naphthalen-2-yl-propen-l-one (12) EMI35.1 EMI35.2 A solution of 2.61 g of 6-acetyl-1,2,3,4tetrahydronaphthalene (15 mmoles) (11), 2.23 g of p-dimethylaminobenzaldehyde (15 mmoles), and 0.66 g of sodium hydroxide in 50 ml of ethanol was stirred under nitrogen at about 600 for 90 hr. The reaction mixture was cooled in an ice bath, and the precipitated solid 3- [ 4-(dimethylamino)phenyl)-l-(5,6,7,8- tetrahydronaphthalen-2-yl) -2-propen-l-one was collected by filtration and washed with cold ethanol. Yield: 3.0 g (61%); m.p. 1340 to 1350. Amax (CHC13); 410 rim (e = 17,200); 266 nm (17,600). Calcd for C21C23NO: C, 82.59; H, 7.59; N, 4.59. Found: C, 80.38, 80.41; H, 7.30, 7.30: n, 3.59, 3.97. EXAMPLE 23 3- [ 4-(1-Pyrrolidinyl)phenyl ] -1-(5,6,7,8-tetrahydro- naphthalen-2-yl) -2-propen-1-one (13) EMI36.1 A solution of 2.6 g of 11 (15 mmol), 2.6 g of p-pyrrolidinylbenzaldehyde (15-mmol), and 0.66 g of sodium hydroxide in 100 ml of ethanol was stirred under nitrogen at 500 for 24 hr. The reaction mixture was cooled in an ice bath, and the precipitated yellow solid 3-t4-(l-pyrrolidinyl)phenyl ] -l-(5,6,7,8-tetra- hydronaphthalen-2-yl) -2-propen-l-one was collected by filtration and washed with cold ethanol. Yield: 3.2 g (64%); m.p. 1670 to 1690. Amax (CHCl3): 420 nm = =36,800); 330 nm (4,300); 276 nm (16,400). Calcd for C23H25NO: C, 83.34; H, 7.60; N, 4.23. Found: C, 82.68, 82.67; H, 7.57, 7.55; N, 4.03, 4.15. EXAMPLE 24 3- [ 4-(4-Morcholinyl)phenyl ] -1-(5,6,7,8-tetrahydro- naphthalen-2-yl) -2-propen-l-one (14) EMI36.2 A solution of 1.74 g of 11 (10 mmoles), 1.91 g of p-C4-morpholinyllbenzaldehyde (10 mmoles), and two pellets of sodium hydroxide (about 0.4 g) in 40 ml of ethanol was stirred under nitrogen at room temperature for 70 hr. The reaction mixture was cooled in an ice bath and the precipitated yellow solid 3- [ 4-(4-morpholinyl)phenyl)-l-(5,6,7,8-tetra- hydronaphthalen-2-yl) -2-propen-l-one was collected by filtration and washed with cold ethanol. Yield: 2.9 g (83%); m.p. 1380 to 1400. Amax (EtOH): 390 nm (e = 28,100), 270 nm (e = 13,700). Calcd for C23H25NO2: C, 79,51; H, 7.25; N, 4.03. Found: C, 78.72, 79.02, 78.75; H, 7.22, 7.26, 7.23; N, 3.88, 3.87, 3.91. EXAMPLE 25 3-[4-(Dimethylamino)phenyl]-1-(2,3-dihydro-lH-inden- 5-yl) -2-propen-l-one (16) EMI37.1 EMI37.2 A solution of 4.8 g of 1-(2,3-dihydro-lHinden-5-yl)ethanone (15; 30 mmoles), 4.5 g of pdimethylaminobenzaldehyde (30 mmoles), and 1.32 g of sodium hydroxide in 40 ml of methanol was stirred under nitrogen at room temperature for 48 hr. The reaction mixture was cooled in an ice bath and the precipitated solid 3- [ 4- (dimethylamino)phenyl ] -l- (2,3-dihydro-lH-inden-5-yl)-2-propen-1-one was collected by filtration and washed with cold methanol. Yield: 4.2 g (48%); m.p. 1060 to 1080. Amax (EtOH): 416 nm (e = 34,700); 272 nm (15,400). Calcd for r NO: C, 82.44; H, 7.26; N, 4.81. Found: C, 82.19, 82.12; H, 7.21, 7.24; N, 4.70, 4.67. EXAMPLE 26 3-[4-(1-Pyrrolidinyl)phenyl]-1-(2,3-dihydro-lH-inden- 5-yl) -2-propen-l-one (17) EMI38.1 A solution of 1.47 g (9.14 mmoles) of 15, 1.60 g (9.14 mmoles) of p-pyrrolidinylbenzaldehyde and two pellets of sodium hydroxide (about 0.4 g) in 20 ml of methanol was stirred under nitrogen at room temperature for 112 hr. The reaction mixture was cooled in an ice bath and the precipitated solid 3- [ 4-(1-pyrrolidinyl)phenyl ] -1-(2,3-dihydro-lH-inden 5-yl)-2-propen-1-one was collected by filtration and washed with cold methanol. Yield: 1.2 g (41%); m.p. 1620 to 1640. Evaporation of the filtrate gave a residue which was dissolved in methanol-toluene (9:1). The solution was filtered, evaporated to 100 ml, and cooled. The precipitated product was collected by filtration and washed with cold methanol. Yield: 0.9 g (31%); m.p. 1770 to 1790. Amax (EtOH): 275 nm (f = 16,600); 328 nm (4170); 425 nm (37,800). Calcd for C22H23NO: C, 83.24; H, 7.30; N, 4.41. Found: C, 82.99; H, 7.49; N, 4.32. EXAMPLE 27 2-1(4-(Dimethylamino)phenyl)methylene3-3,5,6,7- tetrahydro-5 -indacen-l (2H) -one '(19) EMI39.1 EMI39.2 A solution of 2.06 g (12 mmoles) of 3,5,6,7 tetrahydro-5-indacen-l(2H)-one (-18), 1.79 g (12 mmoles) of p-dimethylaminobenzaldehyde, and 0.59 Ç of sodium hydroxide in 40 ml of methanol was stirred under nitrogen at 500 for 24 hr. The reaction mixture was cooled in an ice bath and the precipitated solid 2-[(4-(dimethylamino)phenyl)methylene]-3,5,6,7-tetra- hydro-5-indacen-1(2H)-one was collected by filtration and washed with cold methanol. Yield: 3.2 g (88%); m.p. 2100 to 2250. Amax (EtOH): 425 nm (# = 39,400); 325 nm (,7,l00); 273 nm (16,500). Calcd for C21H2lNO: C, 83.13; H, 6.98; N, 4.62. Found: C, 83.27; H, 7.04; N, 4.53. EXAMPLE 28 2- [ (l,2,6,7-Tetrahydro-3H,5H-benzo [ i,j ] guinolizin-9- yl)methylene]-3,5,6 ,7-tetrahydro-5-indacen-1(2H)- one (20) EMI39.3 A solution of 2.06 g of 18, 2.41 g of 9-formyl-1,2,6,7-tetrahydro-3H,5H-benzo [ quinoline, and about 0.5 g of sodium hydroxide in 40 ml of methanol was stirred under nitrogen at 500 for 24 hr. The reaction mixture was cooled in an ice bath and the precipitated solid.2- [ (1,2,6,7-tetrahy- dro-3H,5H-benzo[i,j]quinolizin-9-yl)methylene]-3,5,6,7- tetrahydro-5-indacen-1(2H)-one was collected by filtration and washed with cold methanol. Yield: 3.2 g (75%); m.p. 1860 to 1890. Amax (EtOH): 458 nm (e = 42,300); 285 nm (20,300). Calcd for C25H25NO: C, 84.47; H, 7.09; N, 3.94. Found: C, 83.68, 83.57; H, 7.09, 7.15; N, 3.85, 3.84. EXAMPLE 29 2-[(1-Ethyl-1,2,3,4-tetrahydro-6-quinolinyl)- methylene]-3,5,6,7-tetrahydro-5-indacen-l(2H)- one (21) EMI40.1 EMI40.2 A solution of 1.72 g of 18, 1.89 g of l-ethyl-6-formy1-l,2,3, 4-tetrahydroquinoline and 0.44 g of sodium hydroxide in 25 ml of methanol was stirred under nitrogen at 600 for 48 hr. The reaction mixture was cooled in an ice bath and the precipitated solid 2- [ (1-ethyl-1,2,3,4-tetrahydro-6-cuinolinyl- methylene-3,5,6,7-tetrahydro-5-indacec-l(2H)-one was collected by filtration and washed with cold methanol. Yield: 1.8 g (52%); m.p. 1670 to 1720. Bmax (EtOH) 282 nm # = 18,800); 320 nm (7240); 332 nm (6280); 447 nm (43,300). Calcd for C24H25NO: C, 83.93; H, 7.34; N, 4.08. Found, C 83.45, 83.20, 83.10; H, 7.73, 7.33, 7.55; N, 3.94, 4.02, 4.01. EXAMPLE 30 2-[(4-Dimethylamino)phenyl)methylene]-2,3,5,6,7,8- hexahydro-lH-benz [ f) inden-l-one (23) EMI41.1 EMI41.2 A solution of 1.84 g (10 mmoles) of 2,3,5,6,7,8-hexahydro-lH-benz [ f ] inden-1-one (22), 1.49 g (10 mmoles) of p-dimethylaminobenzaldehyde, and 0.44 g of sodium hydroxide in 25 ml ethanol was stirred under nitrogen at 500 to 600 for 19 hr. The reaction mixture was cooled in an ice bath and the precipitated solid 2- [ 4-(dimethylamino)phenyl)- methylene ] -2,3,5,6,7, 8-hexahydro-lH-benz [ f ] inden- l-one was collected by filtration and washed with cold ethanol. Yield: 2.5 g (79%); m.p. 1610 to 1630. Amax (EtOH): 274 nm (E = 16,700); 422 nm (36,500). Calcd for C22H23NO: C, 83.24; H, 7.30; N, 4.41. Found: C, 83.01; H, 7.73; N, 4.34. 'EXAMPLE 31 The oriented polyester films employed as substrates in Examples 31 to 39 were 4-mil (102 From) polyethylene terephthalate films sub-coated with a copolymer resin. The copolymer resin comprised a sequentially polymerized mixture of a vinylidene chloride/alkyl acrylate/itaconic acid copolymer and an alkyl acrylate polymer as described in more detail in U.S. Patent 3,443,950. To the copolymer resin, before coating, was added a methyl methacrylate: ethyl acrylate:acrylic acid (37:56:7) terpolymer (molecular weight 260,000 and acid number 76 to 85), dispersed with ammonia. The coated films were stretched and a thin layer of the terpolymer in water was added onto the first sub-coating. The following stock solution was prepared: Component Wt (g) Tetraethylene glycol dimethacrylate 15.0 merpolymer of ethyl acrylate/methyl 35.3 methacrylate/acrylic acid (56/37/7), MW 260,000 Copolymer of styrene/maleic anhydride 36.7 (58/42), esterified, MW 10,000 2- (o-Chlorophenyl) -4 ,5-diphenyl- 8.6 imidazolyl dimer Methylene chloride 527 Methanol 40. To 10 g of this stock solution was added 0.0407 g of 6-nitroveratraldehyde photoinhibitor and 0.0113 g of the sensitizer from Example 22. Portions of this solution were board coated with a 2-mil (51-pm) doctor knife on the resin-subbed side of the oriented polyester film substrate, and the coatings were air-dried. The dried coatings were laminated with a 1-mil (25-pm) oriented polyester film coversheet at 820 at a rate of 4 ft/min (1.22 m/min) at 40 psi (276 kPa) One half the surface of a photosensitive element was covered by a black polyethylene sheet. A t32 step wedge process transparency was placed over the uncovered side and the element was placed in a vacuum printing frame. An imagewise exposure (positive exposure) was made to radiation from a 2KW mercury photopolymer lamp at a distance of 38 in (96 cm) using an "Ascor" Light Integrator Platemaker Model 1415-12 with a Berkey "Ascor" 1601-40 light source for a time which corresponds to a radiation dosage of 10 units. The polyethylene sheet was removed and a t step wedge was placed over the previously blocked-off section. A U.V. cut-off filter which absorbed essentially all radiation below about 420 nm was placed over the element and the entire element was given a 30 unit exposure. This final exposure gave a negative exposure to the blocked-off section and completed the twoexposure positive sequence on the other half. The exposed element was developed at 220 in a solution prepared from 1536 g of distilled water, 84 g of potassium carbonate¯1.5 H2O, and 5 g of potassium hydrogen carbonate, and the developed element was rinsed with a 320 water spray at 40 psi (276 kPa). A development time of 6 seconds gave a positive mode speed of 3, i.e., the first three steps of the positive image were unpolymerized, and a negative mode speed of 10, i.e., the negative image showed 10 full and partial polymerized steps. EXAMPLES 32 AND 33 The photopolymerizable compositions of Examples 32 and 33 were prepared, exposed and developed as described in Example 31 except: (1) the sensitizers of Table 4 were employed and (2) development time of 7 seconds was used in Example 32. Positive mode speeds of 1 and < 1 were obtained for Examples 32 and 33, respectively. Negative mode speeds were 11 and 16, respectively. A good image was obtained in each instance. TABLE 4 Example Sensitizer of, g 32 Example 23, 0.0123 33 Example 30, 0.0117 EXAMPLES 34 TO 39 Photopolymerizable compositions were prepared, exposed, and developed as described in Example 31 with the following modifications. No 6-nitroveratraldehyde photoinhibitor was added to the compositions. The photosensitive elements were given one 10-unit negative exposure to the photopolymer lamp. A development time of 8 seconds was used. The results, summarized in Table 5, indicate that a good image was obtained in each instance. TABLE 5 Photopolymerization Example Sensitizer of, g Speed 34 Example 24, 11 0.0129 35 Example 25, 12 0.0108 36 Example 26, 12 0.0117 37 Example 27, 12 0.0112 38 Example 28, 12 0.0132 39 Example 29, 12. 0.0127

Claims: CLAIMS: The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows: 1. A composition having the formula EMI45.1 wherein: R1 and R2 are each H, or R1 + R2 is -CH2-; R is H, or R3 + R5 is selected from (CH2)2, (CH2)3, and -CH(CH3)CH2C(CH3)2-; R is H, or R + R6 is selected from (CH2)2 and *CH2*3; R5 and R6 are alkyl groups of 1 to 5 carbon atoms, or together are selected from (CH2)4 and -CH2C OCH2CH2-; R7 is selected from (A) EMI45.2 wherein: R8 is H or CH3; EMI45.3 n is 0 or 1, and when n is 1, R1 and R2 are H; or (B) trimethylene and tetramethylene groups, unsubstituted, or substituted with 1 to 4 alkyl groups, R7 having a maximum of 8 carbon atoms. 2. A composition according to Claim 1 wherein R7 is (A). 3. A composition according to Claim 2 wherein R1, R2 and R8 are H and n is 0. 4. A composition according to Claim 2 wherein R1, R2 R4 and R8 are H, R5 and R6 are each CH3 or C2H5, or R3 + R5 is -CH2CH2CH2-, and n is 0. 5. A composition according to Claim 1 wherein R7 is (B). 6. A composition according to Claim 5 wherein R1 and R2 are H and R7 is unsubstituted. 7. A composition according to Claim 5 wherein R1 and R2 are H, R7 is unsubstituted, Ri + R6 are each CH3 or C2H5, or R3 + R5 is XCH2t3. 8. A photopolymerizable composition comprising the components: (i) at least one nongaseous ethylenically unsaturated compound capable of forming a high molecular weight polymer by photoinitiated addition polymerization; (ii) at least one 2,4,5-triarylimidazolyl dimer initiator consisting of two 2,4,5-triaryl imidazolyl radicals bound together by a single covalent bond; and (iii) at least one a,#-unsaturated ketone sensitizer according to Claim 1. 9. A composition according to Claim 8 wherein R7 in sensitizer (iii) is (A). 10. A composition according to Claim 8 7 wherein R in sensitizer (iii) is (B).

Inventors: ANDERSON, ALBERT GORDON
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1981
Main classification: C07C97
IPC codes: C07C225, G03C1, C07D215, C07D295, C08F2, G03F7, C07D455