Polymeric materials and thermoplastic resin compositions

Abstract: A polymeric material which is superior in mechanical strength, dimensional stability, moldability and resistances to chemicals, heat and abrasion comprises a copolymer com­ posed of polymer chain moieties of a copolymer containing an imide compound of an α,β-unsaturated dicarboxylic acid and polymer chain moieties of a polyamide, both chain moieties be­ ing bonded to each other. The material may be blended with thermoplastic resins. Furthermore, the material may be rein­ forced with glass fiber, etc.

Description: The present invention relates to production of a polymeric material obtained from a copolymer containing an imide compound of an α,β-unsaturated dicarboxylic acid as a constituent and a polyamide and a thermoplastic resin composition comprising said polymeric material to which a thermoplastic resin is added. More particularly, it relates to a method for producing a copolymer comprising polymer chain moieties derived from a copolymer containing an imide compound of an α,β-unsaturated dicarboxylic acid and polymer moieties derived from a polyamide, both chain moieties being bonded to each other, and a polymeric material containing said copolymer. Moreover, it relates to a thermoplastic resin composition which comprises said copolymer and a thermoplastic resin. Polystyrene, styrene-acrylonitrile copolymers, acrylonitrile-styrene-butadiene copolymers and similar polymeric materials have widely been used as molding materials because of their high dimensional stability and good moldability, while the improvement in their chemicals, thermal and abrasion resisting properties are still desired. On the other hand, polyamides have also been used widely as molding materials because of their superior resistance to chemicals, heat and abrasion. However, polyamides suffer from some disadvantages such as strong shrinkage during molding process which may cause "sink marks" and "warpage" in the molded articles; high hygroscopicity and significant decrease in mechanical strength and large dimensional change after they take up moisture. It has been proposed that a polyamide is melt blended with polystyrene or a styrene-acrylonitrile copolymer in order to improve the hygroscopicity and other properties of the polyamide (Japanese Patent Examined Publication No. 7380/65). However, this technique involves serious disadvantages in that the styrene polymer or copolymer has so poor compatibility with polyamides that the molded articles from such blend show laminar peeling phenomenon and possess inferior mechanical strength. Because of this, such blend is not known as satisfactory molding material. In U.S. Patent No. 3,966,839 it is disclosed that polystyrene and a polyamide are melt blended with addition of a small amount of a low molecular weight (1000 to 3000 M.W.) styrene-maleic anhydride copolymer which is used in order to improve the compatibility between the polyamide and polystyrene. By the addition of the low molecular weight styrene-maleic anhydride copolymer, an improvement is found in the compatibility between these polymers, but it is still insufficient so that when the blend is used in injection molding into complicated shape the above-mentioned peeling condition may occur. resulting in unfavourable mechanical strength of the molded article. The inventors have made an intensive research to develop materials which possess excellent properties of both non-crystalline thermoplastic polymers and polyamides. As a result, they have developed a process which produces a polymeric material which predominantly comprises a bonded copolymer composed of (a) polymer chain moieties derived from a copolymer containing imide groups of dicarboxylic acid and (b) polyamide chain moieties, both moieties being bonded to each other (hereinafter referred to merely as "bonded copolymer"). The present invention provides a method of preparing a polymeric material comprising at least 10% by weight of a copolymer, which method comprises reacting a vinyl aromatic compound trunk copolymer or an unsaturated carboxylic acid ester trunk copolymer with a polyamide by melt kneading under shear conditions at 220 to 330°C to obtain said copolymer, said copolymer being comprised of 1 to 99% by weight of said trunk copolymer comprising vinyl aromatic compound chain moieties or unsaturated carboxylic acid ester chain moieties and 99 to 1% by weight polyamide chain moieties that are bonded to each other, said vinyl aromatic compound trunk copolymer comprising 30 to 99 mol% of a vinyl aromatic compound, 1 to 30 mol% of an amine-reactive compound of an α,β-unsaturated dicarboxylic acid and 0 to 60 mol% of a monomer copolymerisable with said vinyl aromatic compound and said amine reactive compound, said unsaturated carboxylic acid ester trunk copolymer comprising 50 to 99 mol% of an α,β-unsaturated carboxylic acid ester, 1 to 30 mol% of an amine-reactive compound of an α,β-unsaturated dicarboxylic acid and 0 to 49 mol% of a monomer copolymerisable with said carboxylic acid ester and said amine-reactive compound, said amine-reactive compound containing trunk copolymer having a molecular weight of 10,000 to 300,000, characterised in that said amine-reactive compound of an α,β-un saturated dicarboxylic acid is an imide compound, and that said polyamide has a molecular weight of 10,000 to 50,000. The polymeric materials containing the bonded copolymer may be used as thermoplastic molding materials having good mechanical strength, high dimensional stability, good moldability, and good resistance to chemicals, heat and abrasion. In the accompanying drawing, Fig. 1 is an electron micrograph of a polymeric material obtained from a styrene - N - phenylmaleinimideacrylonitrile copolymer and polycaprolactam which is one preferred embodiment of the present invention. Fig. 2 is an electron micrograph of a mixture of a styrene-acrylonitrile copolymer and polycaprolactam. In order to allow a better understanding of the bonded copolymers produced by the present invention, they are explained in comparison with a mixture of a styrene-acrylonitrile copolymer and a polyamide (which is hereinafter referred to as "mixture") in the following. First, when subjected to solvent fractionation (using cresol/methyl ethyl ketone as a solvent system), the mixture is entirely separated into its individual components, i.e., the styrene-acrylonitrile copolymer and the polyamide, whereas the bonded copolymer cannot be fractionated, which indicates that the styrene copolymer containing imide groups of dicarboxylic acid is chemically bonded to the polyamide. In addition, from the facts that when the bonded copolymer is dissolved and disintegrated in conc. hydrochloric acid the styrene copolymer remains and that the bonded copolymer shows a peak in the proximity of the melting point of the polyamide in its thermal analysis, it can be seen that the bonded copolymer has a particular structure in which the styrene copolymer chain moieties having imide groups of dicarboxylic acid are bound to the polyamide moieties. Another difference is found in the electron micrographs. For example, in the electron micrograph of the polymeric material obtained by the present invention which predominantly comprises the bonded copolymer composed of styrene - N - phenylmaleinimide - acrylonitrile copolymer chain moieties and polycaprolactam chain moieties bonded to each other as shown in Fig. 1, a fine dispersion of particles is observed and it is so fine as to be unexpected from the large difference in solubility parameter between the styrene - N - phenylmaleinimide - acrylonitrile copolymer and the polycaprolactam. Such dispersion of particles is apparently distinct from the state of dispersion observed in the electron micrograph of a mixture of a styrene-acrylonitrile copolymer and polycaprolactam as shown in Fig. 2. Under consideration of the above-mentioned significant difference in the dispersion state of particles, we have found that a polymeric material comprising a copolymer in which polymer chain moiety of the styrene copolymer and polymer chain moiety of the polyamide, both of said moieties being bonded each other in the method of this invention, shows a fine dispersion state of particles (disperse phase) having an average particle diameter of not greater than 5 µ, especially preferably not greater than 2 µ. On the other hand, when no bonding above is allowed to occur between the polymer moieties, or when combinations of the styrene-acrylonitrile copolymer and the polyamide or the styrene-methyl methacrylate copolymer and the polyamide are blended without chemical bonding, only a dispersion is obtained where an average particle diameter of the dispersion phase is more than 5 µ. When evaluated as molding materials, those polymer blends in which any reaction between the polymeric components is not caused, for example, a resin mixture in the state of coarse dispersion which is prepared by melt kneading of a combination of a styrene-acrylonitrile copolymer and a polyamide or a styrene-methyl methacrylate copolymer and polyamide, are inferior in that the phenomenon of laminar peeling is observed in the molded articles formed from these mixtures by injection molding or other molding technique. In addition, these molded articles are inferior in the mechanical strength so that such unreacted polymer blends fail to provide satisfactory molded articles. On the contrary, polymeric materials containing the present bonded copolymer where vinyl aromatic compound copolymer chain moieties and polyamide chain moieties are chemically bonded to each other by a reaction between polymeric components are excellent, because no laminar peeling is observed in injection molding articles formed therefrom and satisfactory molded articles having superior mechanical strength can be obtained. There are a number of copolymers containing as a constituent an imide compound of α,β-unsaturated dicarboxylic acids which are used in the present invention and preferred are styrene copolymers containing imide groups of dicarboxylic acids and unsaturated carboxylic acid ester copolymers containing imide groups of dicarboxylic acids. Compositions of vinyl aromatic compound copolymers are 30 to 99 mol % of a vinyl aromatic compound, 1 to 30 mol % of an imide compound of α,β-unsaturated dicarboxylic acid and 0 to 60 mol % of a monomer copolymerizable with the vinyl aromatic compound and the imide compound of α,β-unsaturated dicarboxylic acid. Compositions of the unsaturated carboxylic acid ester copolymers are 50 to 99 mol % of an α,β-unsaturated carboxylic acid ester, 1 to 30 mol % of imide compound of α,β-unsaturated dicarboxylic acid and 0 to 49 mol % of a monomer copolymerizable with the α,β-unsaturated carboxylic acid ester and the imide compound of α,β-unsaturated dicarboxylic acid. Particularly important is the content of the imide groups of dicarboxylic acids which considerably affects the reactivity with polyamides. The content of the above ranges affords particularly favorable results in terms of mechanical strength of the resulting polymeric materials of the present invention. Furthermore, molecular weight of the copolymers is within the range of 10,000 to 300,000. A much lower molecular weight will result in reduction of mechanical strength and a much higher molecular weight will result in significantly decreased moldability of the resulting polymeric materials. The vinyl aromatic compound copolymers and unsaturated carboxylic acid ester copolymers include rubber material-nonreinforced copolymers and impact-resistant rubber-reinforced copolymers. These copolymers can be produced according to the methods disclosed in Japanese Patent Unexamined Publication (Kokai) No. 93091/79, German Patent No. 2,644,492, Canadian Patent No. 847437, using common techniques such as bulk polymerization, solution polymerization, suspension polymerization and emulsion polymerization wherein radical polymerization is utilized. They can also be produced by the treatment of a copolymer of a vinyl aromatic compound and an α,β-unsaturated cyclic anhydride with a basic nitrogen-containing compound as disclosed in U.S. Patent No. 3,998,907, German Patent No. 2,343,408. The imide compounds of α,β-unsaturated dicarboxylic acid which form the copolymers used in the present invention can be represented by the following general formula: wherein R₁, R₂ and R₃ represent hydrogen, alkyl group, alkenyl group, cycloalkyl group, phenyl group, phenylene group, alkylene group, etc. Examples thereof are maleinimide, N-methylmaleinimide, N-butylmaleinimide, N-cyclohexylmaleinimide, N-phenylmaleinimide, N - (p - methylphenyl)maleinimide, N - (3,5 - dimethylphenyl)maleinimide, N - (p - methoxyphenyl)maleinimide, N-benzylmaleinimide, N - (1 - naphthyl)maleinimide. As the vinyl aromatic compounds which form the copolymers used in the present invention there may be used styrene, o-methylstyrene, p-methylstyrene, dimethylstyrene, m-ethylstyrene, chlorostyrene. isopropylstyrene, tertbutylstyrene, a-methylstyrene, ethyl-vinyltoluene, or mixtures thereof. As the monomers copolymerizable with the vinyl aromatic compounds and the imide compounds of α,β-unsaturated dicarboxylic acid, there may be used α,β-unsaturated nitriles such as acrylonitrile, methacrylonitrile, α,β-unsaturated carboxylic acid esters such as methyl methacrylate, butyl methacrylate, butyl acrylate, and α,β-unsaturated carboxylic acids such as acrylic acid, methacrylic acid. As the α,β-unsaturated carboxylic acid esters which form the copolymers used in the present invention there may be used methacrylic acid esters such as methyl methacrylate, ethyl methacrylate, butyl methacrylate, 2-ethylhexyl methacrylate, 2-hydroxyethyl methacrylate, etc., acrylic acid esters such as ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, or mixtures thereof. Moreover, as the monomers copolymerizable with the α,β-unsaturated carboxylic acid esters and the imide compounds of α,β-unsaturated dicarboxylic acids there may be used styrene compounds such as styrene, a-methylstyrene, vinyltoluene, etc., α,β-unsaturated nitriles such as acrylonitrile, methacrylonitrile, α,β-unsaturated carboxylic acids such as acrylic acid, methacrylic acid, monoolefins such as ethylene, propylene, isobutene, vinyl acetate, vinyl ether. The rubber-reinforced vinyl aromatic compound copolymers and unsaturated carboxylic acid ester copolymers used in the present invention can be produced by polymerizing monomers in the presence of rubber-like polymers such as polybutadiene rubber, styrene-butadiene rubber, polybutene rubber, hydrogenated styrene-butadiene rubber, acrylonitrile-butadiene rubber, ethylene-propylene rubber, polyacrylate rubber, natural rubber. Suitable vinyl aromatic compound polymers used in the present invention are styrene-maleinimide copolymer, styrene - N - phenyl - maleinimide copolymer, styrene - N - phenylmaleinimide - acrylonitrile copolymer, styrene - N - phenylmaleinimide - methyl methacrylate copolymer, styrene - N - phenylmaleinimide - butyl acrylate copolymer, and these copolymers which are reinforced with rubber. The polymeric materials of the present invention obtained using styrene - N - phenylmaleinimide - acrylonitrile copolymer or styrene - N - phenylmaleinimide - methyl methacrylate copolymer which contain acrylonitrile or methyl methacrylate which has polarity provide molded products having better appearance and higher mechanical strength, wear resistance, etc. than those obtained using styrene - N - phenylmaleinimide copolymer. Reasons for those results are not clear, but it is supposed that the incorporation of the monomers having polarity brings about a homogeneous reaction of styrene copolymer and polyamide thereby to produce polymeric materials having a more uniform and finer micro-structure. Suitable unsaturated carboxylic acid ester copolymers used in the present invention include methyl methacrylate - N - phenylmaleinimide copolymer, methyl acrylate - N - phenylmaleinimide copolymer. butyl acrylate - N - phenylmaleinimide copolymer, methyl methacrylate - N - phenylmaleinimide-styrene copolymer, butyl acrylate - N - phenylmaleinimide - styrene copolymer, methyl methacrylate - N - phenylmaleinimide - acrylonitrile copolymer, butyl acrylate - N - phenylmaleinimide-acrylonitrile copolymer, and these copolymers which are reinforced with rubber. Suitable polyamides used in the present invention are nylon 6 (polycaprolactam), nylon 6/6 (polyhexa-methylene adipamide), nylon 6/10, nylon-11, nylon-12, copolymer of terephthalic acid and trimethylhexamethylenediamine (Trogamid T produced by Dynamit Nobel Inc.). From the viewpoint of heat distortion resistance and mechanical properties of polymeric materials obtained, the molecular weight of the polyamide is in the range of 10,000 to 50,000, preferably 15,000 to 40,000. The polymeric materials produced in accordance with the present invention, as previously mentioned, contain a bonded copolymer comprising vinyl aromatic compound copolymer chain moieties or unsaturated carboxylic acid ester copolymer chain moieties and polyamide chain moieties which are bonded to each other. Said polymeric materials may comprise said bonded copolymer alone or a mixture of said bonded copolymer with copolymer containing imide groups of dicarboxylic acid and polyamide which remain unreacted. Content of the bonded copolymer in the polymeric materials is at least 10% by weight, preferably at least 50% by weight. The polymeric materials obtained according to the present invention are thermoplastic and are much superior to non-crystalline polymers such as vinyl aromatic compound polymers, unsaturated carboxylic acid ester polymers in chemical resistance, heat resistance and abrasion resistance and they show greatly reduced molding shrinkage and greatly improved hygroscopicity as compared with polyamides. They also possess a good dimensional accuracy. Because of these properties, they are useful as molding materials in the production of large-sized moldings and precision moldings. Furthermore, they are so improved in melt strength over polyamides that they are also suitable for extrusion molding and blow molding and can be utilized for production of films, sheets, bottles and laminates and for wire coating. They are also suitable as materials in production of foams and fibers. Moreover, the polymeric materials obtained in the present invention are superior in heat stability at high temperatures to those obtained from styrene - α,β - unsaturated dicarboxylic anhydride copolymer which contains anhydride group in the copolymer and polyamide as disclosed in Japanese Patent Applications No. 127298/79 and No. 129467/79. They can be molded at molding temperatures in a wide range and can provide good moldings having no silver streaks even at high temperatures. The polymeric materials are prepared by reacting under melt kneading a copolymer containing an imide compound of α,β-unsaturated dicarboxylic acid as a constituent with polyamide. The reaction under melt kneading can be effected using a conventional melt kneading apparatus for resins such as a kneader. Bumbury mixer or twin-screw extruder. The melt kneading must be carried out under sufficient shearing force. If the shearing force is insufficient to achieve a proper melt kneading, it is difficult to bring about the reaction between the polymers. The temperature is in the range of 220 to 330°C, preferably 260 to 300°C. If the melt kneading temperature is too low, the reaction hardly occurs and if too high, thermal decomposition of the polymers occurs. The shearing force and temperature during melt kneading are important in the production of the polymeric materials of the present invention. A reaction accelerator may be added at the time of melt kneading. The content of imide group of dicarboxylic acid in the copolymer containing imide compound of α,β-unsaturated dicarboxylic acid is important. The content of too high or low results in improper reactivity with polyamide and thus polymeric materials having preferable mechanical strength cannot be obtained. The fact that the melt kneading of the copolymer containing an imide compound of α,β-unsaturated dicarboxylic acid as a constituent and polyamide brings about a reaction between the polymers can be confirmed by the melt and solution viscosities of the polymeric materials of the present invention which are higher than those of the copolymers containing imide compound of α,β-unsaturated dicarboxylic acid as a constituent and polyamide before reaction. On the other hand, mixture of a styrene-acrylonitrile copolymer and a polyamide which do not react therebetween shows a melt viscosity and a solution viscosity each lying between that of the styrene-acrylonitrile copolymer and that of the polyamide before mixing and the melt and solution viscosities are additive. The proportion of the copolymer containng imide compound of α,β-unsaturated dicarboxylic acid and the polyamide which are melt kneaded in production of the polymeric materials of the present invention is chosen from the range of 1-99:9-1. Furthermore, thermoplastic resin compositions having preferred properties can be obtained by blending a thermoplastic resin with the polymeric material mentioned above which comprises polymer chain moieties derived from copolymer containing imide compound of α,β-unsaturated dicarboxylic acid and polymer chain moieties derived from polyamide which are bonded to each other. Especially, there are obtained resin compositions wherein a polyamide which is a crystalline polymer and a non-crystalline polymer such as vinyl aromatic compound polymer, polycarbonate, etc. are in a good compatible state. The thermoplastic resin compositions of the present invention can be obtained from a copolymer containing imide compound of α,β-unsaturated dicarboxylic acid, a polyamide and a thermoplastic resin as a third component. Therefore, it can be said that they are resin compositions which comprise a copolymer containing imide compound of α,β-unsaturated dicarboxylic acid, a polyamide and a thermoplastic resin as a third component. Preferred copolymers containing imide compound of α,β-unsaturated dicarboxylic acid used in the present resin compositions are vinyl aromatic compound copolymers containing imide group of dicarboxylic acid and unsaturated carboxylic acid ester copolymers containing imide group of dicarboxylic acid. It is preferred to use copolymers having compositions and molecular weight within the ranges as previously mentioned. With reference to polyamides, it is also preferred to use polycaprolactam, polyhexamethylene adipamide having a molecular weight in the range of 10,000 to 50,000, especially preferably 15,000 to 40,000. There are many thermoplastic resins which can be used as the third component. Examples of such resins are vinyl aromatic compound resins, polymethyl methacrylate resins, polycarbonate resins. polysulfone resins, polyacrylate resins, polyamide resins, polybutylene terephthalate resins, polyethylene terephthalate resins, styrene-butadiene block copolymer elastomers, hydrogenated styrene-butadiene block copolymer elastomers, thermoplastic polyester elastomers, etc. The vinyl aromatic compound resins include polystyrene, rubber-reinforced impact-resistant polystyrene, AS resin (styrene-acrylonitrile copolymer resin), ABS resin (styrene - acrylonitrile - butadiene copolymer resin), AES resin (ethylene-propylene rubber-reinforced styrene-acrylonitrile copolymer resin), AAS resin (polyacrylate rubber-reinforced styrene-acrylonitrile copolymer resin), MS resin (styrene-methyl methacrylate copolymer resin). MBS resin (styrene-methyl methacrylate-butadiene copolymer resin), etc. Especially preferred combinations are vinyl aromatic compound copolymers containing imide compound of α,β-unsaturated dicarboxylic acid as a constituent which have the composition of 70 to 99 mol % of a styrene compound and 1 to 30 mol % of N-phenylmaleinimide in the case of polystyrene or rubber-reinforced impact resistant polystyrene and copolymers having the composition of 30 to 97 mol % of a styrene compound, 1 to 30 mol % of an imide compound of an α,β-unsaturated dicarboxylic acid and 2 to 60 mol % of an α,β-unsaturated nitrile or copolymers having the composition of 30 to 97 mol % of a styrene compound, 1 to 30 mol % of an imide compound of α,β-unsaturated dicarboxylic acid and 2 to 50 mol % of an α,β-unsaturated carboxylic acid ester in the case of AS resin, ABS resin, AES resin, AAS resin, MS resin and MBS resin. The present invention will be explained more clearly by a specific embodiment. There are conspicuous differences in mechanical properties of resin, micro-structure of polymers, between the resin composition obtained from styrene - acrylonitrile - N - phenylmaleinimide copolymer, polyamide and ABS resin by the present invention and a resin composition obtained from a polyamide and ABS resin. According to the observation by an electron microscope the micro-structure of the resin composition obtained by the present invention has fine and uniform dispersion state of less than 10 µ which shows good compatibility between polymers while that of the resin comoosition obtained from polyamide and ABS resin has coarse and uniform dispersion state of 20 µ or more which shows extremely inferior compatibility. Furthermore, excellent molded articles can be obtained from the resin composition obtained by the present invention by injection molding while molded articles obtained by injection molding from a resin composition comprising polyamide and ABS resin show laminar peeling phenomenon and are inferior in mechanical strength. The resin composition which contains a bonded copolymer comprising styrene - acrylonitrile - N - phenylmaleinimide copolymer chain moieties and polyamide moieties bonded to each other and which is obtained from a styrene - acrylonitrile - N - phenylmaleinimide copolymer, a polyamide and ABS resin by the method of this invention is far more preferred as a molding material than a mixture obtained from polyamide and ABS resin in mechanical properties. It will be recognized that the presence of the bonded copolymer has a great effect on improvement of compatibility of polyamide and ABS resin. The polymethyl methacrylate resin include polymethyl methacrylate, rubber-reinforced polymethyl methacrylate, MS resin (methyl methacrylate-styrene copolymer resin), MBS resin (methyl methacrylatestyrene-butadiene copolymer resin). It is preferred to use the polymethyl methacrylate resin in combination with a copolymer having the composition of 50 to 99 mol % of α,β-unsaturated carboxylic acid ester, 1 to 30 mol % of imide compound of α,β-unsaturated dicarboxylic acid and 0 to 49 mol % of a monomer copolymerizable with the α,β-unsaturated carboxylic acid ester and the imide compound of α,β-unsaturated dicarboxylic acid. Polycarbonate resins sold from various companies may be used. It is preferred to use polycarbonate resins in combination with a copolymer having the composition of 1 to 30 mol % of an imide compound of α,β-unsaturated dicarboxylic acid, 30 to 89 mol % of a styrene compound and 10 to 50 mol % of an α,β-unsaturated nitrile or a copolymer having the composition of 1 to 30 mol % of imide compound of α,β-unsaturated dicarboxylic acid, 10 to 90 mol % of α,β-unsaturated carboxylic acid ester and 0 to 89 mol % of styrene compound. Udel (trademark) sold from Union Carbide Corporation or Nissan Chemical Co., Ltd. is an example of polysulfone resins and U Polymer sold from Unitika Ltd. is an example of polyarylate resins. Examples of polyamide resins are nylon-6, nylon 6/6, nylon 6/10, nylon 11, nylon 12, copolymer of terephthalic acid, and trimethylhexamethylenediamine (Torogamid T produced by Dynamit Nobel Inc.). The mixing ratio of the polymeric material and thermoplastic resin in the resin composition of the present invention may be freely chosen so long as preferred dispersion state can be attained, but when content of the polymeric material is too small, fine dispersion state can hardly be obtained and it is preferably contained in an amount of at least 10% by weight in the resin composition. This content of the polymeric material may be increased to obtain finer dispersion state in the resin composition. The dispersion state of resin composition also varies depending on the kind of the thermoplastic resin in the resin composition. Average particle diameter of the dispersion phase may vary depending on the purpose. but is usually not more than 10 µ, preferably not more than 5 µ, more preferably not more than 3 µ and most preferably not more than 1 µ. Preferred resin compositions of the present invention comprise 5 to 70% by weight of a copolymer containing an imide compound of α,β-unsaturated dicarboxylic acid, 5 to 80% by weight of a polyamide and 10 to 90% by weight of a thermoplastic resin. Content of the polymeric material in the resin composition of the present invention may be such that provides a dispersion state of not more than 15 µ, but is preferably at least 10% by weight, especially preferably at least 30% by weight. With increase in the content of the polymeric material, the dispersion state becomes finer and more preferred molding materials can be obtained. Proportion of chain moieties of copolymer containing imide compound of α,β-unsaturated dicarboxylic acid and polyamide chain moieties in the bonded copolymer may be such that provides preferred resin composition of the present invention and it has no specific limitation. However, if either one of them is too high or too low, dispersibility cannot be favourably affected and so such proportion should be avoided. The resin composition of the present invention can be produced by preparing a polymeric material from a copolymer containing imide compound of α,β-unsaturated dicarboxylic acid and a polyamide and melt mixing thus obtained bonded copolymer with a thermoplastic resin. Furthermore, the resin composition of the present invention can be obtained simultaneously with formation of the bonded copolymer by melt mixing a copolymer containing imide compound of α,β-unsaturated dicarboxylic acid, a polyamide and a thermoplastic resin. The reaction under melt kneading can be effected using a conventional melt kneading apparatus for resins such as a kneader, Banbury mixer or twin-screw extruder. The melt kneading must be carried out under sufficient shearing force. If the shearing force is insufficient to achieve a proper melt kneading, it is difficult to bring about the reaction between the polymers. The temperature is in the range of 220 to 330°C, preferably 260 to 300°C. If the melt kneading temperature is too low, the reaction hardly occurs and if too high, thermai decomposition of the polymers occurs. The shearing force and temperature during melt kneading are important in the production of the polymeric materials by the present invention. A reaction accelerator may be added at the time of melt kneading. The thermoplastic resin compositions according to the present invention are much superior to non-crystalline polymers such as vinyl aromatic compound resins, polymethyl methacrylate resins, polycarbonate resins, etc. in chemical resistance, heat resistance and abrasion resistance and they show greatly reduced molding shrinkage and greatly improved hygroscopicity as compared with polyamide resins. They also possess a good dimensional accuracy. Because of these properties, they are useful as molding materials in the production of large-sized moldings and precision moldings. Furthermore, they are so improved in melt strength over polyamides that they are also suitable for extrusion molding and blow molding and can be utilized for production of films, sheets, bottles and laminates and for wire coating. They are also suitable as materials in production of foams and fibers. Pigments, dyes, thermal stabilizers, UV absorbers, plasticizers, nucleating agents, flame retardant, etc. may be added to the polymeric materials and the thermoplastic resins of the present invention. Particularly, weathering deterioration of the polymeric material and the novel thermoplastic resin can be greatly controlled by adding antioxidants such as bisphenol, propionate and phosphite compounds and UV absorbers such as phenyl salicylate, benzophenone, benzotriazole compounds. It is possible to use the polymeric materials and thermoplastic resin compositions of the present invention as composite materials in combination with fibrous reinforcing materials such as glass fiber, carbon fiber, aromatic polyamide fiber, asbestos, etc. and/or inorganic fillers such as calcium carbonate, talc, zinc oxide, silica. A conspicuous improvement in heat resistance can be achieved, particularly by combination with glass fiber thereby providing molding materials with good mechanical properties. As a further favorable feature, such composite materials show much better paintability than that of glass fiber-reinforced polyamides and glass fiber-reinforced styrene resins. Moreover, the glass fiber-reinforced resin compositions of the present invention cause less warp in molded articles than that in molded articles obtained from glass fiber-reinforced polyamides. Therefore, they will provide the most preferable molding materials that have ever been proposed in the field of the production of large-sized molded articles and precision molded articles such as automobile parts, appliance parts. Content of the glass fiber in the glass fiber-reinforced resin composition of the present invention is preferably 5 to 60% by weight. When it is more than this range, processability decreases and when less than this range, sufficient reinforcing effect cannot be obtained. The glass fiber-reinforced resin composition may be obtained by previously making the polymeric material or resin composition, then blending them with glass fiber and melt mixing them by an extruder. Furthermore, a mixture of the copolymer containing imide compound of α,β-unsaturated dicarboxylic acid as a constituent and a polyamide and, optionally a thermoplastic resin as a third component with glass fiber may directly be put in a hopper of an injection molder to obtain a molded article simultaneously with melt mixing of them or said mixture may be melt kneaded by an extruder to obtain a glass fiber-reinforced resin composition. Furthermore, a part of the glass fiber in the resin composition of the present invention may be replaced with fibrous reinforcing materials such as asbestos, carbon fiber, aromatic polyamide fiber, potassium titanate fiber, etc. or inorganic fillers such as calcium carbonate, talc, titanium oxide, zinc oxide, magnesium hydroxide. The following examples will further illustrate the present invention. Example 1 and Comparative Example 1 Fifty parts by weight of polycaprolactam (Amilan [trademark] CM1017, Toray Co., Ltd.) was mixed with 50 parts by weight of styrene - N - phenylmaleinimide - acrylonitrile copolymer (content of N-phenylmaleinimide 12 mol % and content of acrylonitrile 35 mol %) having ηsp/c= 1.05 (measured in a mixed solvent of m-cresol/methyl ethyl ketone=9/1 at 30°C) [Example 1] and with 50 parts by weight of styrene-acrylonitrile copolymer (content of acrylonitrile 45 mol %) having ηsp/c= 1.30 [Comparative Example 1] in pellet form, respectively. Each of the mixtures was melt kneaded at 260°C by a twin-screw extruder. Thus obtained reaction product of polycaprolactam with styrene - N - phenylmaleinimide - acrylonitrile copolymer and mixture of polycaprolactam with styrene-acrylonitrile copolymer were subjected to the following tests. (1) Observation by electron microscope The electron micrograph (Fig. 1) of the reaction product of styrene - N - phenylmaleinimide - acrylonitrile copolymer with polycaprolactam shows very fine dispersion of particles of 500 to 5000 Å. On the other hand, the electron micrograph (Fig. 2) of the mixture of styrene-acrylonitrile copolymer with polycaprolactam shows coarse dispersion of particles of about 10 µ and incompatible state between the polymers is observed. A great difference is seen between these electron micrographs. (2) Solvent fractionation test A 10 g sample each of the reaction product styrene - N - phenylmaleinimide - acrylonitrile copolymer with polycaprolactam and the mixture of styrene-acrylonitrile copolymer with polycaprolactam was weighed and dissolved in a mixed solvent of cresol and methyl ethyl ketone (9/1). Both were completely dissolved remaining no insolubles. The resulting solution was added to a large amount of methyl ethyl ketone to completely separate out a precipitate. This precipitate was collected and was referred to as polymer (I). Weight of polymer (I) in the case of the reaction product was 8.0 g and that in the case of the mixture was 5.1 g. From the remaining solution the dissolved polymer was recovered and was referred to as polymer (II). Weight of polymer (II) in the case of the reaction product was 1.7 g and that in the case of the mixture was 4.6 g. Then, polymers (I) and (II) were subjected to infrared spectroscopic analysis. In the case of the reaction product, both the polymers (I) and (II) showed the spectrum each of the styrene - N - phenylmaleinimide-acrylonitrile copolymer and polycaprolactam while in the case of the mixture, the spectrum of polymer (I) corresponded to that of polycaprolactam and the spectrum of polymer (II) corresponded to that of the styrene-acrylonitrile copolymer. It is apparent from the results of this solvent fractionation test that there was formed a copolymer where the styrene - N - phenylmaleinimide - acrylonitrile copolymer and the polycaprolactam are bonded to each other. Test pieces were prepared from the reaction product, the mixture, the styrene - N - phenylmaleinimide-acrylonitrile copolymer and the styrene-acrylonitrile copolymer by injection molding and the tensile strength, Izod impact strength and heat distortion temperature of these test pieces were measured in accordance with JIS Test Method K6871. Melt flow index of them was measured in accordance with ASTM D1238 (at 230°C under a load of 3.8 kg). The peeling state of the molded articles was determined by subjecting the test pieces to peeling test which comprises applying an adhesive tape to rupture cross-section and then removing the tape and observing the state of cross-section by naked eye. Furthermore, solution viscosity was also measured. The results are shown in Table 1. As recognized from them, the molded article obtained from the reaction product is much improved in both tensile strength and impact strength over that obtained from the styrene - N - phenylmaleinimide - acrylonitrile copolymer while the molded article from the mixture is lower in mechanical strength than the styrene-acrylonitrile copolymer. The melt flow index of the reaction product is lower than that of the styrene - N - phenylmaleinimide - acrylonitrile copolymer (namely, melt viscosity of the reaction product is higher than that of the copolymer) while the melt flow index of the mixture is much higher than that of the styrene-acrylonitrile copolymer (namely, melt viscosity of the mixture is much lower than the copolymer). Moreover, solution viscosity of the reaction product is much higher than that of both the polycaprolactam (ηsp/c=1.25) and styrene - N - phenylmaleinimide - acrylonitrile copolymer while no such result is seen in the case of the mixture. Abrasion resistance and chemical resistance of the styrene - N - phenylmaleinimide - acrylonitrile copolymer used in Example 1 and those of the reaction product of Example 1 are shown in Table 2. The abrasion resistance is expressed by abrasion wear (mg) when subjected to Taber machine and the chemical resistance is expressed by % critical strain at which a crack occurs when the test piece is in contact with the chemical. Molding shrinkage at injection molding of the polycaprolactam used in Example 1 and the reaction product of Example 1 is shown in Table 3. The shrinkage was measured using a plate of 150×150×3 mm. Water absorption of the polycaprolactam and the reaction product of Example 1 is shown in Table 4. The water absorption was measured from increment in weight of the injection molded test pieces when they were dipped in warm water of 80°C for 40 minutes. Examples 2-6 Reaction products were obtained by carrying out the melt kneading under the same conditions as in Example 1 except that the styrene - N - phenylmaleinimide - acrylonitrile copolymer used in Example 1 was substituted with a styrene - N - phenylmaleinimide - acrylonitrile copolymer having different composition from that of Example 1 (ηsp/c=0.93, content of the N-phenylmaleinimide 7 mol % and content of the acrylonitrile 25 mol %) [Example 2], a styrene - N - phenylmaleinimidemethyl methacrylate copolymer (ηsp/c=0.95, content of N-phenylmaleinimide 10 mol % and content of methyl methacrylate 15 mol %) [Example 31, a styrene - N - phenylmaleinimide copolymer (ηsp/c=0.87, content of N-phenylmaleinimide 14 mol %) [Example 4], a styrene-maleinimide copolymer (ηsp/c=0.85, content of maleinimide 10 mol %) [Example 5] and a rubber-reinforced styrene-N-phenylmaleinimide copolymer (content of rubber-like polymer 8% by weight and content of N-phenylmaleinimide 12 mol %) [Example 6]. The resultant reaction products were subjected to the solvent fractionation test of Example 1 to confirm that copolymers where styrene copolymer chain and polycaprolactam chain are bonded to each other were formed in all reaction products. Moreover, observation by an electron microscope showed fine dispersion state of particles of 2 µ or less. Measurement of properties was effected and the results are shown in Table 5. Comparative Examples 2-4 Resin mixtures were obtained by effecting the melt kneading under the same conditions as in Comparative Example 1 except that the styrene-acrylonitrile copolymer of Comparative Example 1 was substituted with a styrene-methyl methacrylate copolymer (ηsp/c=1.02, content of methyl methacrylate 15 mol %) [Comparative Example 2], a polystyrene (ηsp/c=0.90) [Comparative Example 3], and a rubber-reinforced polystyrene (content of rubber-like polymer 8% by weight) [Comparative Example 4]. The resultant mixtures were subjected to the solvent fractionation test of Example 1, but formation of copolymers comprising styrene copolymer chain and polycaprolactam chain which were bonded to each other was not recognized. Electron micrographs shows coarse dispersion state of particles of 10 µ or more. Injection molded articles therefrom showed serious peeling phenomena and were inferior in mechanical strength. Example 7 Reaction products were obtained under the same conditions as in Example 1 except that the polycaprolactam in Example was substituted with polyhexamethylene adipamide (Leona [trademark] 1200S, Asahi Chemical) and melt kneading temperature was 280°C. Formation of copolymers comprising styrene copolymer chain and polyhexamethylene adipamide chain which were bonded to each other was confirmed by the solvent fractionation test. Results of the tests for properties are shown in Table 5. Examples 8 and 9 Reaction product were obtained in the same manner as in Example 1 with mixing ratios of the polycaprolactam and the styrene - N - phenylmaleinimide - acrylonitrile copolymer as shown in Table 6. The resultant reaction products were subjected to the solvent fractionation test of Example 1 to confirm formation of copolymers comprising styrene copolymer chain and polycaprolactam chain which were bonded to each other. Properties measured are shown in Table 6. Example 10 and Comparative Example 5 Fifty parts by weight of polycaprolactam (Amilan [trademark] CM1017, Toray Co., Ltd.) was mixed with 50 parts by weight of a methyl methacrylate - N - phenylmaleinimide-styrene copolymer (content of N-phenylmaleinimide 7 mol % and content of styrene 20 mol %) of ηsp/c=0.85 (measured in a mixed solvent of m-cresol/methyl ethyl ketone=9/1 at 30°C) [Example 10] and 50 parts by weight of methyl methacrylatestyrene copolymer (content of styrene 20 mol %) of ηsp/c=1.05 [Comparative Example 5] in pellet form, respectively and each of the mixtures was melt kneaded by a twin-screw extruder at 260°C. The resultant reaction product of polycaprolactam and methyl methacrylate - N - phenylmaleinimide-styrene copolymer and mixture of polycaprolactam and methyl methacrylate-styrene copolymer were subjected to the following test. Observation by electron microscope The observation of the reaction product of methyl methacrylate - N - phenylmaleinimide - styrene copolymer and polycaprolactam according to the present invention by electron microscope showed fine dispersion state of particles of 2 µ or less. On the other hand, the observation of the mixture of methyl methacrylate-styrene copolymer and polycaprolactam showed coarse dispersion state of particles of about 10 µ and there was seen incompatibility between the polymers. Test pieces were prepared from the reaction product and the mixture by injection molding. Tensile strength, Izod impact strength and heat distortion temperature of these test pieces were measured in the same manner as in Example 1. Also, the degree of peeling of the test pieces was evaluated. Solution viscosity was also measured. The results are shown in Table 7. Solution viscosity of the reaction product was much higher than that of the polycaprolactam (ηsp/c=1.25) and the methyl methacrylate - N - phenylmaleinimide - styrene copolymer while no such result was seen in the case of the mixture. Example 11 Reaction products were obtained in the same manner as in Example 10 except that the polycaprolactam in Example 10 was substituted with polyhexamethylene adipamide (Leona [trademark] 1200S, Asahi Chemical) and melt kneading temperature was 280°C. The reaction products were also subjected to the solvent fractionation test of Example 1 to confirm formation of copolymers comprising α,β-unsaturated carboxylic acid ester copolymer chain and polyhexamethylene adipamide chain which were bonded to each other. The properties measured are shown in Table 7. Example 12 Fifty parts by weight of the polycaprolactam used in Example 1, 25 parts by weight of the styrene - N - phenylmaleinimide - acrylonitrile copolymer used in Example 1 and 25 parts by weight of ABS resin (obtained by emulsion graft polymerization of 25 parts by weight of a styrene monomer and 15 parts by weight of acrylonitrile in the presence of 60 parts by weight of polybutadiene latex) were mixed and melt kneaded by a twin-screw extruder at 260°C to obtain a thermoplastic resin composition. Observation of this composition by electron microscope showed homogeneous dispersion of rubber particles and good compatibility between polymers. Results of measurement of properties are shown in Table 8. Comparative Example 6 Melt kneading was effected in the same manner as in Example 12 except that the styrene - N - phenylmaleinimide-acrylonitrile copolymer in Example 12 was substituted with a styrene-acrylonitrile copolymer (content of acrylonitrile 45 mol %) of ηsp/c=1.30 to obtain a thermoplastic resin composition. Observation of the composition by an electron microscope showed coarse, nonhomogeneous dispersion state of about 20 µ and incompatibility between polycaprolactam and ABS resin. Results of measurement of properties are shown in Table 8. Example 13 Fifty parts by weight of the polycaprolactam used in Example 10, 30 parts by weight of the methyl methacrylate - N - phenylmaleinimide - styrene copolymer used in Example 10 and 20 parts by weight of a rubber-reinforced polymethyl methacrylate (obtained by emulsion graft polymerization of 40 parts by weight of methyl methacrylate in the presence of 60 parts by weight of polybutadiene latex) were mixed and melt kneaded by a twin-screw extruder at 260°C to obtain a thermoplastic resin composition. Observation of this composition by electron microscope showed homogeneous dispersion state of polymers. Results of property tests are shown in Table 8. Example 14 Fifty parts by weight of the reaction product of polycaprolactam and styrene - N - phenylmaleinimide - acrylonitrile copolymer which was obtained in Example 1 and 50 parts by weight of ABS resin (obtained by emulsion graft polymerization of 40 parts by weight of styrene monomer and 20 parts by weight of acrylonitrile in the presence of 40 parts by weight of polybutadiene latex) were mixed and melt kneaded by a twin-screw extruder at 260°C to obtain a thermoplastic resin composition. Observation of this composition by electron microscope showed homogeneous dispersion state of polymers. Results of property tests are shown in Table 8. Example 15 Fifteen parts by weight of the styrene - N - phenylmaleinimide copolymer used in Example 4, 15 parts by weight of polycaprolactam used in Example 4, 67 parts by weight of a rubber-reinforced impact-resistant polystyrene (content of polybutadiene 20% by weight and obtained by solution polymerization) and 3 parts by weight of a hydrogenated styrene-butadiene block copolymer (Kraton G1650 Shell Co.) were mixed and melt kneaded by a twin-screw extruder at 260°C to obtain a thermoplastic resin composition. Observation of this composition under electron microscope showed homogeneous dispersion state of polymers. Results of property tests are shown in Table 8. Example 16 Fifty parts by weight of the polycaprolactam used in Example 1, 25 parts by weight of the styrene - N - phenylmaleinimide - acrylonitrile copolymer used in Example 1 and 25 parts by weight of polycarbonate resin (Panlite L-1225 Teijin Chemical) were mixed and melt kneaded by a twin-screw extruder at 280°C to obtain a thermoplastic resin composition. Observation of this composition by electron microscope showed homogeneous dispersion state of polymers. Results of property tests are shown in Table 8. Example 17 Eighty parts by weight of the reaction product obtained in Example 1 and 20 parts by weight of glass fiber were mixed and the resultant mixture was introduced into a vent extruder and kneaded at 250 to 270°C to obtain a glass fiber-reinforced resin composition in pellet form. This composition was subjected to property tests and paintability test. The paintability was evaluated by coating a molded test piece with an acrylic paint and then visually observing the appearance of the coated test piece. Adhesion test of the coated film was effected with a molded test piece which had been subjected to moisture resistance test at 50°C and at least 98% RH for 72 hours. The results are shown in Table 9 together with the results obtained with glass fiber-reinforced polystyrene and glass fiber-reinforced nylon-6. It is recognized that the glass fiber-reinforced resin composition of the present invention had high heat resistance, good paintability and excellent mechanical properties. It should be understood throughout the specification and claims that such an expression as, for example, "a copolymer containing an imide compound of α,β-unsaturated dicarboxylic acid" means a copolymer containing, as one of monomeric components, an imide compound of α,β-unsaturated dicarboxylic acid.

Claims: A method of preparing a polymeric material comprising at least 10% by weight of a copolymer, which method comprises reacting a vinyl aromatic compound trunk copolymer or an unsaturated carboxylic acid ester trunk copolymer with a polyamide by melt kneading under shear conditions at 220 to 330°C to obtain said copolymer, said copolymer being comprised of 1 to 99% by weight of said trunk copolymer comprising vinyl aromatic compound chain moieties or unsaturated carboxylic acid ester chain moieties and 99 to 1% by weight polyamide chain moieties that are bonded to each other, said vinyl aromatic compound trunk copolymer comprising 30 to 99 mol% of a vinyl aromatic compound, 1 to 30 mol% of an amine-reactive compound of an α,β-unsaturated dicarboxylic acid and 0 to 60 mol% of a monomer copolymerisable with said vinyl aromatic compound and said amine reactive compound, said unsaturated carboxylic acid ester trunk copolymer comprising 50 to 99 mol% of an α,β-unsaturated carboxylic acid ester, 1 to 30 mol% of an amine-reactive compound of an α,β-unsaturated dicarboxylic acid and 0 to 49 mol% of a monomer copolymerisable with said carboxylic acid ester and said amine-reactive compound, said amine-reactive compound containing trunk copolymer having a molecular weight of 10,000 to 300,000, characterised in that said amine-reactive compound of an α,β-un saturated dicarboxylic acid is an imide compound, and that said polyamide has a molecular weight of 10,000 to 50,000. A method according to claim 1, wherein the copolymerisable monomer is at least one α,β-unsaturated nitrile, α,β-un saturated carboxylic acid ester or α,β-unsaturated carboxylic acid. A method according to claim 1, wherein the vinyl aromatic compound copolymer contains 70 to 99 mol% (based on the total of monomers) of a vinyl aromatic compound and 1 to 30 mol% of an imide compound of a α,β-unsaturated dicarboxylic acid. A method according to claim 1, wherein the vinyl aromatic compound copolymer comprises 30 to 97 mol% of a vinyl aromatic compound, 1 to 30 mol% of an imide compound of α,β-unsaturated dicarboxylic acid and 2 to 60 mol% of an α,β-unsaturated nitrile. A method according to claim 1, wherein the vinyl aromatic compound copolymer comprises 30 to 97 mol% of a vinyl aromatic compound, 1 to 30% of an imide compound of unsaturated dicarboxylic acid and 2 to 50 mol% of an α,β-unsaturated carboxylic acid ester. A method according to claim 1, wherein the copolymerisable monomer is at least one vinyl aromatic compound, mono-olefin, α,β-unsaturated nitrile or α,β-unsaturated carboxylic acid. A method according to claims 1 or 6, wherein the α,β-unsaturated carboxylic acid ester is at least one alkyl ester of acrylic acid or methacrylic acid. A method according to any one of claims 1 to 7, wherein the imide compound of α,β-unsaturated dicarboxylic acid is N-phenylmaleinimide. A method according to any one of claims 1 to 8, wherein the polyamide is polycaprolactam or polyhexamethylene adipamide. A thermoplastic resin composition which comprises (1) the product of the method of any one of claims 1 to 9 mixed with (2) a different thermoplastic resin. A resin composition according to claim 10, wherein the thermoplastic resin (2) is a vinyl aromatic compound resin, a polymethyl methacrylate or a rubber reinforced polymethyl methacrylate copolymer resin, a polycarbonate resin, a polysulfone resin, a polyarylate resin, a polyamide or at least one elastomer selected from ethylene-butadiene block copolymer elastomers, hydrogenated styrene-butadiene block copolymer elastomers and thermoplastic polyester elastomers. A resin composition according to claim 10 wherein the resin (2) is a polystyrene or rubber-reinforced impact resistant polystyrene, and the copolymer (1) is a vinyl aromatic compound copolymer comprising 70 to 99 mol% of a vinyl aromatic compound and 1 to 30 mol% of N-phenylmaleinimide. A resin composition according to claim 10 wherein the resin (2) is selected from AS resin (styrene-acrylonitrile copolymer resin), ABS resin (styrene-acrylonitrilebutadiene copolymer resin), AES resin (ethylenepropylene rubber reinforced styrene-acrylonitrile copolymer resin), and AAS resin (polyacrlic ester rubber-reinforced styrene acrylonitrile copolymer resin) and the copolymer (1) is a vinyl aromatic compound copolymer comprising 30 to 97 mol% of a vinyl aromatic compound, 1 to 30 mol% of an imide compound of α,β-unsaturated dicarboxylic acid and 2 to 60 mol% of an α,β-unsaturated nitrile or 2 to 50 mol% of an α,β-unsaturated carboxylic acid ester. A resin composition according to claim 10 wherein the resin (2) is MS resin (styrene-methyl methacrylate copolymer resin) or MBS resin (styrene-methyl-methacrylic-butadiene copolymer resin), and the vinyl aromatic compound copolymer of the polymeric material (1) comprises 30 to 97 mol% of a vinyl aromatic compound, 1 to 30 mol% of an imide compound of α,β-unsaturated dicarboxylic acid and 2 to 50 mol% of an α,β-unsaturated carboxylic acid ester or 2 to 60 mol% of an α,β-unsaturated nitrile. A resin composition according to claim 10 wherein the resin (2) is a polycarbonate resin and the vinyl aromatic compound polymer (I) of the polymeric material (1) comprises 1 to 30 mol% of the imide compound of α,β-unsaturated dicarboxylic acid, 30 to 89 mol% of a vinyl aromatic compound and 10 to 50 mol% of an α,β-unsaturated nitrile. A resin composition according to claim 10 wherein the resin (2) is a polycarbonate resin and the unsaturated carboxylic acid ester copolymer (II) of the polymeric material (1) comprises 1 to 30 mol% of the imide compound of α,β-unsaturated dicarboxylic acid, 10 to 90 mol% of an α,β-unsaturated carboxylic acid ester and 0 to 89 mol% of a vinyl aromatic compound. A glass fiber-reinforced resin composition which comprises 40 to 95% by weight of the product of the method of any of claims 1 to 9 or a resin composition according to claim 10 and 5 to 60% by weight of glass fiber. A molded article produced from a resin composition according to any one of claims 10 to 17.

Inventors: KASAHARA HIDEO, SUZUKI HIROSHI, UMEDA NORIAKI, KASAHARA, HIDEO, SUZUKI, HIROSHI, UMEDA, NORIAKI
Applicants: ASAHI CHEMICAL IND, ASAHI KASEI KOGYO KABUSHIKI KAISHA
Application year: 1981
Main classification: C08G81
IPC codes: C08G81, C08G69