METHOD FOR MAKING LIP TYPE SHAFT SEAL

Abstract: A method for molding an annular lip type shaft seal (10) of the type having an annular elastomeric shaft seal element (12) and a resin liner (14) (preferably polytetrafluoroethylene) integrally molded therewith and bonded thereto, including providing a step or shoulder (36) on the mold core (26) to prevent the resin liner (14) from flowing axially beyond a predetermined location during molding. The method includes providing a certain range of acute angles "//c" between the shoulder surface (42) and the liner forming surface (38) of the mold core surface (34), and a certain range of shoulder heights "d" relative to the liner thickness "t", for various values of the initial viscosity of the elastomeric preform (18). The percentage of rejects due to undesired flow of the resin liner (14) during molding has been greatly reduced.

Description: TECHNICAL FIELD This invention relates to shaft seals and to a method for molding an annular lip type seal of the type having a resin liner (such as polytetrafluoroethylene) and in particular to controlling the resin liner flow during molding to reduce the number of rejects. BACKGROUND OF THE PRIOR ART ' Methods are known for molding an annular lip type shaft seal of the type having an elastomeric body or seal element with a resin liner (such as of polytetrafluoroethy¬ lene) integrally molded therewith and bonded thereto. Such known method includes placing a resin washer, an elastomeric preform and metal shell in a mold and closing the mold, see for example, Japanese patent publication Sho 46-2381, announced July 7, 1971 in the Japanese Patent Agency Patent Gazette. Such prior art has the problem of control over the degree or uniformity of axial length to which the resin liner is formed or extruded axially beyond the molded or trimmed lip of the seal, during the molding operation. If the liner flows too far it can thin out and split and can become- trapped between elastomer and the metal shell causing bond problems in critical areas, or the liner can occupy part of the flex section of the seal affecting seal per¬ formance. This problem becomes more acute with increases in the viscosity or shearing force of the elastomer and with increasing lip diameters of the seal as well as with other factors involving the characteristics of the type and thickess of the resin being used. It is an object of the present invention to pro¬ vide an improved method for controlling the resin liner flow during molding and thereby to reduce the percentage of rejects occurring during molding shaft seals having resin liners due to undesired flow of the liner during molding. It is another object of this invention to prevent liner material from entering the seal flex section. / •^ foiππt^ It is another object of the present invention t provide a method for making an annular lip type shaft seal of the type having an annular elastomeric shaft seal element and a resin liner integrally molded therewith and 5 bonded thereto, wherein the mold is provided with a step or shoulder and wherein -the parameters of the angle the shoulder surface makes with the mold c#re, the shoulder, height with respect to the liner thickness, and the initia viscosity of the elastomeric preform are maintained at 0 certain relative values or ranges of values. BRIEF SUMMARY OF THE INVENTION A method for molding an annular lip type shaft seal of the type having an annular elastomeric shaft seal element and a resin liner integrally molded therewith and 5 bonded thereto comprising placing a flat washer of resin liner material, an elastomeric preform and a metal shell in a cavity of an open mold and then closing the mold to form the seal. To prevent the liner from flowing axially beyond a predetermined location, the method includes 0 providing the mold core with an annular lip forming surface facing radially outwardly and axially inwardly and providing on said lip forming surface an annular step or • shoulder having an axially inwardly facing shoulder surfac for contacting the edge of the resin liner and pre- 5 venting the resin liner material from flowing axially outwardly beyond said shoulder. The shoulder is located axially between a recessed liner forming surface and an elastomeric seal element forming surface of said lip forming surface. Certain parameters that are involved 0 are an angle "<2 " between said shoulder surface and said liner forming surface, the thickness "t" of the liner, the perpendicular height M d" of the shoulder surface above the liner forming surface and the viscosity "V" of the elastome According to the present invention, the parameters d, t 5 and 0 preferably have the following values with respect to the initial viscosity of the elastomeric preform: Polytetrafluoroethylene Initial Viscosity "v" of Flow-control step Elastomer at 375 " ° F. Dimensional Require- (Rheometer Units) ments ^ _ <10 d:> t ;*<..__ 85° 5 :i5 d_^1.25t;*= " 80° < 20 d^l.5t ^<_^r 75° • ^>25 d_^2t ; <P<__≤ 65° * . The method also includes closing the mold and lOapplying heat and pressure thereto, forming the flat resin washer into a resin lip liner, flowing the elastomeric preform into a lip type shaft- seal element substantially simultaneously with the liner forming step during the closing step, bonding the lip liner to the seal element and sub- 15stantially simultaneously curing the elastomer while the mold is closed, opening the mold,and removing the formed,*-cured and bonded seal from the mold. In one embodiment, the resin lined seal lip is trimmed to form a finished trimmed lip shaft seal. 0 BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be more fully understood by reference to the following detailed description thereof, when read in conjunction- with the attached drawings, wherein like reference numerals refer 5to like elements and wherein; Figs. 1-3 are partial cross-sectional views through a mold showing the molding method of the present invention, with Fig. 1 showing the mold open, Fig. 2 showing the mold partially closed and Fig. 3 showing the 0mold completely closed; Fig. 4 is a partial cross-sectional view of a shaft seal made according to the method of the present invention; and Fig. 5 is an enlarged, partial view of one portion 5 of the seal and mold showing various of the parameters involved. DETAILED DESCRIPTION OF THE INVENTION With reference now to the drawings, Figs. 1-4 show the method of the present invention as applied to a trimmed lip seal and Fig. 5 is an enlarged partial cross- 5 sectional view of the step or shoulder portion of the mold and molded seal showing various ones of the critical rela¬ tionships that are involved. Figs.1-4 show the method of the present inventio for molding an annular, lip type shaft seal 10 (see Fig. 4) 10 of the type having an annular molded elastomeric shaft seal element 12 and a resin liner 14. Referring to Fig. 1 the method comprises placing a flat washer 16 of resin lin material (preferably polytetrafluoroethylene) , an elastomer preform 18, and a metal shell 20 in a cavity 22 of an open 15 compression mold 24. The mold 24 includes a mold core 26, a lower die member 28, and a moveable upper die member 30. The mold 24 is shown in its open position in Fig. 1 and in its closed position in Fig. 3. The mold is then closed as shown in Figs.2 and 3 20with heat and pressure being applied as is well-known to those skilled in the art. During this time, the flat resin washer 16 is formed into the resin lip liner 14, the elasto meric preform 18 is caused to flow into the shape of the elastomeric shaft seal element 12, the liner 14 is bonded 25 to the seal element 12 in a manner well-known to those skilled in this art, and the elastomer of the seal element 12 is cured, all substantially simultaneously. The mold 24 is then opened and a semi-finished seal assembly 32 (see Fig. 3) is removed. An excess portio 3044 of the seal assembly 32 (shown in dotted lines in Fig. 4 is then trimmed off along the line "a-a" to produce the finished shaft seal 10. The mold core 26 includes (see Figs. 1 and 5) an annular lip forming surface 34 facing radially outwardly 35and axially inwardly. The direction "radially outwardly" is of course to the left in Fig. 1 and the direction "axially inwardly" is vertically up in Fig. 1 (this later term is • with reference to the volume to be sealed by the seal 10, which is vertically up in Figs. 1 to 4). 5 The lip forming surface 34' includes an annular step or shoulder 36 separating the surface 34 into a recessed liner forming surface 38 and an elastomeric element forming surface 40. The shoulder 36 includes an axially inwardly facing shoulder surface 42. Referring further to Fig. 5, various parameters concerning the shoulder 36 are shown as follows: " ^." is the acute angle between the shoulder surface 42 and the liner forming surface 38; "d" is the perpendicular height the shoulder 36 extends above (radially outwardly of) the liner forming surface 38, and "t" is the thickness of the liner 14. According to the present invention, an important and critical relationship exists between these parameters and the initial viscosity of the elastomeric preform 18. 0 That is, in order to properly and positively control the flow of the liner 14 by having the shoulder 36 contact the outer edge of the liner 14 and prevent the liner from flowing past the shoulder (which control significantly reduces the percentage of rejects due to improper liner 5 flow) , the preferred relationships between these para¬ meters, according to the present invention, is as set forth below: Initial Viscosity of the Elastomeric Preform 18. Preferred values Q . at 375° F (in Rheometer of Parameters , . units) __ * *• • d, and t ' ._ 10 d ' ; ^85 us, where, space permits, molds will be useful with a wider range of elastomers if d is maximized and minimi zed . Thus, as the viscosity increases, the height • d should be increased relative to t and the angle <• -•.shoul be decreased, all as shown above. While the above description relates to a trimme lip seal, the present invention is also applicable to molded lip seals. The resin washer 16 can be treated prior to molding as is known by those skilled in the art, to allow the elastomer to bond to the adjacent resin liner surface. The resin liner 14 can be, for example, a fluorocarbon resin (and as stated above is preferably polytetrafluoroethylene). The present invention provides a significant reduction in the reject rate due to improper liner flow from about 15% or more when using an obtuse shoulder angle-≤ .to less than about 1%. In the preferred embodiment, the liner 14 has a thickness t of about .015 inch. Further, in the preferred embodiment the seal 10 is made with a molded approach angle of from about 10° to 15°. The molded approach angle is the angle between the axis of the mold and the surface 38 in Fig. 1, for example The method of the present invention can also be used in combination with a mold having means for forming hydro- dynamic pumping elements on the resin liner. While compression molding has been described above, the present invention can also be used with other molding methods suc as transfer and injection molding, for example. ' The invention has been described in detail with particular reference to the preferred embodiments thereof, but it will be understood that variations and modifications can be affected within the spirit and scope of the invention as described hereinafter and as defined in the appended claims.

Claims: . A metho or molding an annular lip type shaft seal of the type having an annular elastomeric shaft seal element and a resin liner integrally molded there¬ with and bonded thereto, said method comprising the steps of: (a) placing a resin liner element having a thick¬ ness t, an elastomeric preform and a seal shell in a- old having an annular lip forming surface; (b) providing, on said lip forming surface, an annular shoulder having a shoulder surface facing said liner element and adapted to con¬ tact an outer edge of said liner element during molding for preventing said resin liner element from flowing axially past said shoulder, said shoulder being located axially between a liner forming surface and an elastomeric seal element forming surface, said shoulder making an anglecKwith said liner forming surface and having a perpendicular height d above said liner forming surface; (c) providing©< and d with the values*^ —85° and d Ξ t; and (d) operating said mold for forming said liner element into said liner and causing said elastomer to flow to form said shaft seal element and applying heat and pressure there¬ to for forming said seal. 2. The method according to claim 1 wherein said placing step comprises placing in said mold an elasto- meric preform having an initial viscosity "V" in rheometer units at about 375° of V- 10. 3. The method according to claim 1 wherein said placing step comprises placing in said mold an elastomeric preform having an initial viscosity "V" in rheometer units at 375° F of V £15, and wherein said providing step includes providing σ>. ^___ 80° and providing d:≥1.25t. 4. The method according to claim 1 wherein said placing step comprises placing in said mold an elast meric preform having an initial viscosity "V" in rheomete units at 375° F of V - 20, -and wherein said providing ste includes providing© l 75° and providing d ≥ 1.5t. 5. The method according to claim 1 wherein said placing step comprises placing an elastomeric preform having an initial viscosity "V" in rheometer units at 375° F of V ψ-- 25, and wherein said providing step includes providing σ- ^ 70° and providing ^l.75t. 6. The method according to claim 1 wherein said placing step comprises placing an elastomeric preform having an initial viscosity "V" in rheometer units at 375° F of V£ 25, and wherein said providing step includes providinga β j≤r 65° and providing d^_ 2t. 7. The method according to claim 1 wherein said resin liner element,*, is a fluorocarbon resin. 8. The method according to claim 1 wherein said resin liner element is polytetrafluoroethylene. 9. The method according to claim 1 further including forming hydrodynamic pumping elements on said resin liner substantially simultaneously with said forming step. 10. The method according to claim 1 wherein sai providing step comprises providing <S in the range o ' f from about 85° to 65° and providing d in the range of from about It to 2t. OMP 11. The method according to claim 1 including placing said resin liner element in said mold as a flat washer and including forming said flat resin washer into a resin lip liner; flowing said elastomeric preform into a lip. type shaft seal element substantially simultaneously with said forming step during said closing step; bonding said lip liner to said seal element and substantially simultaneously curing said elastomer while said mold is closed; opening said mold; and removing the formed, cured and bonded seal from the mold. 12. A method for molding an annular lip type shaft seal of the type having an annular elastomeric shaft seal element and a resin liner integrally molded therewith and bonded thereto, comprising: (a) placing a resin liner having a thickness t and an elastomeric preform in a mold having a mold core with a radially outwardly facing lip forming surface, (b) forcing the elastomeric preform to flow in said mold and form said liner against said lip forming surface, (c) providing on said lip forming surface an annular shoulder located axially betweena liner forming surface and an elastomeric seal element forming surface, said shoulder having a shoulder surface facing said liner and adapted to contact an outer edge of said liner during molding and to prevent said liner from flowing past said shoulder, said shoulder surface making an acute angle ~ with said liner forming surface and having a perpendicular height d above said liner forming surface, and (d) d with the values: ■ * ■ *-* • '■— 85° OMPI β » 13. The method according to claim 12wherein said placing step comprises placing in said mold an elasto meric -preform having an initial viscosity "V" in rheo¬ meter units at about 375° F of V-^10. ^' The method according to claim12wherein said placing step comprises placing in said mold an elasto meric preform having an initial viscosity "v" in rheo¬ meter units at about 375° F of V'<15, and including providing d 2L 1.25t and providing^ — 80°. 15. The method according to claim12wherein said placing step comprises placing in saidmold an- elasto¬ meric preform having an initial viscosity "y" in rheo¬ meter units at about 375° of V ■ 20 and including providing dj^l.5t and providingβ ___: 75°. iδ. The method according to claim12 wherein said placing step comprises placing in saidmold an elasto¬ meric preform having an initial viscosity "V" in rheo¬ meter units at about 375° of V___.25 and including providing d^l.75 and providing-^ 70°. 17. The method according to claim12 wherein said placing step comprises placing in saidmold an elasto¬ meric preform having an initial .viscosity "v" in rheo¬ meter units at about 375° of ^≥.! ' ). and including providing d2_.2t and providing^ — 65 " "°. OM WIP 18. A method for molding an annular lip type shaft seal of the type having an annular elastomeric shaft seal element and a resin liner integrally molded there¬ with and bonded thereto, said method comprising the steps of: (a) placing a flat washer of resin liner material having a thickness t, an elastomeric preform and a seal shell in an open mold having an annular lip forming surface facing radially 0 outwardly and axially inwardly; (b) providing on said lip forming surface an annular shoulder having an axially inwardly facing shoulder surface for preventing said resin liner material from flowing axially 5 outwardly beyond said shoulder, said shoulder being located axially between a liner forming surface and an elastomeric seal element forming surface of said lip forming surface, said liner forming surface being recessed radi- 0 ally inwardly relative to said seal ele- ' ent forming surface, said providing step including providing an angle «%.-between said shoulder surface and said liner form¬ ing surface, and providing a height d for 5 the perpendicular height said shoulder surface extends above said liner forming surface; (c) providing σ ^Z 85° and providing d^ t; OMPI /», WIPO „ (d) closing said open mold and applying heat and pressure thereto; (e) forming said flat resin washer into a resin lip liner; 5 (f) flowing said elastomeric preform into a lip . • type shaft seal element substantially . simultaneously with said forming step durin ' said closing step; - ' (g) bonding said lip liner to said seal element -10 ; and substantially simultaneously curing said elastomer while said mold is closed; . (h) opening said mold; (i) removing the formed, cured -an bonded semi¬ finished seal assembly from the mold; and 15 (j) trimming an excess portion of the resin line seal lip off of said assembly to form a finished shaft seal. 19. The method according to claim 18 -wherein sai .placing step comprises placing an elastomeric prefor 20 having an initial viscosity "V" in rheometer units at abo 375° F of V^.10. 20. The method according to claim 18 wherein said placing step comprises placing an elastomeric prefor having an initial viscosity "V" in rheometer units at 25 375° F of V___-15, and wherein said " providing step include providing gζ _ 80° and providing d^ l.25t. 21. The method according to claim 18wherein said placing step comprises placing an elastomeric . preform having an initial viscosity "V" in rheometer units at 375° F of V ^20, and wherein said providing step includes 5 providing<■- .__? 75° and providing * ≤ 1.5t. 22. The method according to claim 18wherein . ' said placing step comprises placing an elastomeric preform having an initial viscosity. "V" in rheometer units at 375° F of V ^ r 25, and wherein said providing step, includes yy providing ø ^ 70° and providing d i≥:1.75t. 23. The method according to claim 18wherein said placing step comprises placing an elastomeric preform having an initial viscosity "V" In rheometer units at 375° F of V^_:25, and.wherein said providing step includes 15 providinga β -Cj "? 65° and providing d*^ 2t.

Inventors: BAINARD D, ONEAL R
Applicants: GARLOCK INC
Application year: 1980
Main classification: B29H9
IPC codes: B29C43, B29D31, F16J15