PRODUCTION OF PAPER AND PAPER BOARD

Abstract: The drainage and retention properties of an aqueous cellulosic suspension substantially free of filler and which is being used for the production of paper or paper board are improved by including a water soluble high molecular weight substantially non-ionic polymer and a bentonite-type clay.

Description: Many grades of paper include substantial levels of inorganic fillers such as kaolinite, calcium carbonate and titanium dioxide. For instance good quality paper, often referred to as fine paper, may be made from high grade bleached chemical pulp and may contain 5 to 35%, by weight of dry paper, of inorganic filler. In the production of such papers it is common to use retention aids and drainage aids. The cost of these is more than offset by the increased retention of filler in the sheet and by the reduction of filler in the white water and the subsequent loss in effluent discharge, especially in view of increasing costs of raw materials and pressure from environmental legislation to restrict effluent discharge. A variety of retention and drainage aids are known such as polyacrylamides (PAM), polyethyleneimines (PEI), polyamides and polyamines. In US Patent Specification No. 3052595 the use of polyacrylamides with filler is particularly described and is stated that advantageous results are obtained when bentonite provides 1 to 20% by weight of the mineral filler. In British Patent Specification No. 1265496 it is described how polyacrylamides are used to retain inorganic filler and cellulosic fines but that critical conditions have to be observed for successful operation, and particular modified acrylamides are described. Retention and drainage aids are generally used at levels of 100 to 500 grams/tonne of dry polymer on a dry paper weight. At these amounts cost effective advantages can easily be demonstrated in the production of filled or fine papers. There is, however, very large scale production of paper that is substantially unfilled, for instance as newsprint and fluting medium, for instance in the production of board. The unfilled paper is substantially free of filler, generally containing less than 5%, by weight of dry paper, of filler and often there is no deliberate addition of filler to the pulp from which the paper or board is made. Generally the pulp for the newsprint and fluting medium originates from Canada or Scandinavia and is of low grade fibres. With such pulps it would still be desirable to minimise the wastage of the components of the pulp, i.e to improve retention of pulp components in the paper, but it is not easy to demonstrate cost effective advantages by using the known retention and drainage aids for this purpose since the pulps have a high cationic demand. The cationic demand is the amount of cationic polymer that has to be added to give any significant increase in fibre retention and improvement in drainage on the forming wire. The cationic demand is often above 0.1 % so that improvements are only significant with polymer weights of above 1,000 grams dry plymer per tonne dry weight of paper and such amounts render the treatment uneconomic. The papermaking fibres used in Canada and Scandinavia for newsprint and fluting medium are low grade fibres and are predominantly of the mechanical type and include groundwood, thermomechanical pulp, deinked secondary fibres, semi-chemical pulps and semi-bleached chemical kraft pulps, normally produced in situ in an integrated pulp and paper mill system. The cellulosic fibres are thus rarely completely separated from the residual process liquors which contain substantial level of both organic and inorganic impurities derived from the pulping process itself and the resins naturally present in the wood. These impurities are present in solution and in colloidal suspension and may include such substances as lignosulphonates, rosin acids, hemicelluloses and humic acids, and impart a large negative charge on the cellulose fibres when dispersed in water as typical in the papermaking process. The level of the aforementioned impurities is further enhanced in the papermaking process by the increasing tendency for paper mills to close-up the paper machine white water systems and recycle as much white water as possible. Thus there is a need for fibre retention drainage aids which traditional aids cannot meet and so there has been extensive research into the development of new aids, but so far with limited success. In German Specification 2262906 it is proposed to improve the dewatering of cellulosic slurries by adding bentonite and a low molecular weight cationic polymer that serves as a polyelectrolyte. The results are not satisfactory and this specification does not give a solution to the problem of cost effective improvement in fibre retention and drainage of substantially filler free, low grade pulp. The suspension may be made from pulp by normal techniques and the paper or paper board may be made from the aqueous suspension also by normal techniques. Throughout this specification, unless otherwise stated all percentages are given as dry weight of added material calculated on the dry weight of the suspension or final paper. The suspension and the resultant paper or paper board are substantially free of filler and by total amount of filler, including added bentonite type clay, is less than 5% by weight. It is generally preferred that no inorganic filler other than bentonite type clay should be included in the suspension but if any such filler is included its amount is generally less than 3% and most preferably below 2%, in particular below 1.5%. If there is any filler other than bentonite the amount of additional filler is often less than twice the amount of bentonite and is preferably less than the amount of bentonite. If additional filler is included in the suspension it is usually a conventional predried filler, such as any of the materials listed in US Patent Specification No. 3052595. The amount of bentonite included in the pulp is between 0.02 and 2% by weight dry bentonite-type clay, based on dry weight of paper or pulp, and most preferably is from 0.1 to 1%. The bentonite-type clay used in the invention may be one of the common commercially available bentonites (known as montmorillonite clays), such as "Wyoming bentonite" and "Fullers Earth", and may or may not be chemically modified, e.g. by alkali treatment to convert calcium bentonite substantially to alkali (e.g sodium, potassium or ammonium) bentonite. Bentonites having the property of swelling in water are preferred. The polymers are polyacrylamides containing 1 to 10 mole percent acrylic acid units. For example preferred polymers contain 1 to 8 mole percent acrylic acid with the balance acrylamide, most preferably 97 mole percent acrylamide, 3% acrylic acid, often as sodium acrylate. The preferred copolymers of acrylamide and acrylic acid (or sodium acrylate) can be made by hydrolysis of the homopolymer either during or after its initial synthesis. It is easily possible, by routine experimentation, to select preferred combinations of polymers and bentonite grades. It has surprisingly been found that it is easily possible to obtain excellent retention and drainage results using polymer-bentonite combinations whereas the bentonite alone on the same pulp or the polymer alone on the same pulp give worse results than with the pulp alone. Thus there is a surprising synergistic effect between the bentonite and the polymer. The amount of polymer added is generally at least 50 but generally less than 1,000 grams dry polymer per tonne dry paper (i.e. 0.005 to 0.1%). Generally it is from 0.01 to 0.05%. The polymer may be supplied as a true solution in water, as a solid grade product or as a dispersion in a carrier oil, but in all cases should be dissolved in water and added as a dilute aqueous solution to the pulp suspension during the papermaking process. The polymer solution is added after the last point of high shear prior to sheet formation and is typically after centri-screens and just before the flow-box, to ensure good mixing, and to avoid excessive shear which can damage the retention/drainage effect. The bentonite may be added to the suspension either as a pre-hydrated aqueous slurry directly to thick stock or as a solid to the hydropulper or to the re-circulating white-water providing it is well dispersed during addition to enable adequate hydration and accomplish its characteristic swelling properties. Preferably traditional additives such as aluminium sulphate are omitted, and preferably the main, and often the only, additives to the pulp in the process of the invention are the described polymer and bentonite, and so the suspension preferably is formed from substantially only the cellulosic pulp, water, the polymer, the bentonite-type clay and, optionally, additional filler in the amounts specified above. The invention is of particular value in the production of fluting medium, for instance in the production of board, and especially in the production of newsprint. It is of particular value in the production of paper or paper board from impure pulps that have a cationic demand (as defined above) of above 1%. We have also found that the invention gives a surprising and significant improvement in the machine runnability and this enables larger quantities of lower grade fibres to be used without incresing the risk of machine stoppages. As well as providing improved retention and drainage the method of the invention also results in a significant reduction in the solvent extractable troublesome resinous pitch content of the papermachine white water system. During paper-mill trial work a reduction of the extractable pitch content of the white water of 75% was observed. The following examples illustrate the invention. In these PAM stands for polyacrylamide and all polyacrylamides and polyethylene oxides used have a molecular weight between 10⁶ and 10⁷. PAM 3% SA stands for a copolymer of 97 mole percent acrylamide with 3% mole percent sodium acrylate. In the examples where bentonite was added it was added as a prehydrated aqueous slurry prior to the polymer addition. In none of the examples is aluminium sulphate added and instead in each example the aqueous suspension consisted essentially only of water, cellulosic fibres (and associated impurities from the pulp) and, when appropriate, the added polymer and/or bentonite. Example 1 A sample of thin stock taken from a Swedish newsprint mill consisted of: 30% thermomechanical pulp 25% chemical sulphate pulp 35% groundwood 10% broke It contained a high level of impurities such as lignosulphates. The drainage efficiency of various conventional polymers was compared with bentonite-polymer systems according to this invention. The required quantity of dilute polymer solution was added to 1 litre of the stock in measuring cylinder, to give an effective polymer dose level of 0.05% polymer (i.e. 500 g/tonne of dry polymer based on the dry weight of paper). The cylinder was inverted three times to effect mixing and the contents were poured onto a typical machine wire. The time taken for 250 mls of white water to drain was noted. The shorter the time the more effective the treatment. The results are given in Table 1. Example 2 Using the same sample of thin stock as described in Example 1 above, the retention efficiency of various conventional polymers was compared with the bentonite/polymer system according to this invention. The required quantity of dilute polymer solution was added to 1 litre of thin stock in a 1 litre measuring cylinder, to give an effective polymer dose level of 0.05% of dry polymer based on the dry weight of paper. The cylinder was inverted three times to effect mixing and then the contents were poured onto a typical machine wire. The white water draining through the wire was collected and the solids content determined. The lower the solids content the more effective the retention aid treatment. The results are given in Table 2. Example 3 On an identical sample of thin stock to that used in Examples 1 and 2, the effect on drainage of varying the level of bentonite addition whilst maintaining a constant dose level of PAM 3% SA was examined. The drainage rate measurements made in the same manner as in Example 1. The shorter the drainage time the more effective the treatment. The results are given in Table 3. Example 4 On the same stock sample used in Example 3, the effect on drainage of varying the polymer (PAM 3% SA) addition level whilst maintaining a constant level of bentonite addition, was examined. The drainage rate measurements were made in the same manner as in Example 3. The shorter the drainage rate the more effective the treatment. The results are given in Table 4. Example 5 A range of various types of bentonite was evaluated at a constant addition level of 0.5% on dry paper together with a constant dose level of 0.04% on dry paper high molecular weight PAM 3% SA. A sample of the same stock was used as in Examples 3 and 4 and the bentonite/polymer system performance was again assessed by drainage rate measurements. The shorter the drainage time the more effective the treatment. The results are given in Table 5. In Wochenblatt Fur Papierfabrikation, 13, 1979, pages 493 to 502 Auhorn et al investigate the effect of troublesome materials in closed water systems for paper making and in Section 7 investigate ways of reducing the concentration of contaminants. They propose washing the pulp, the use of a combination of cationic and anionic retention aids, neutralisation of the organic contaminants for instance with sodium aluminate, treatment of the effluent, and addition of adsorption materials. In particular they describe the use of chalk or bentonite for this purpose. In an example on newsprint they dewater 8g/l stock in the presence of cationic polyelectrolyte and zero, 10 or 20g/l bentonite and show that the dewatering period is reduced with increasing amounts of bentonite. However the use of these very large amounts of bentonite with the cationic polyelectrolyte would be commercially uneconomic in the manufacture of newsprint or fluting medium. The invention provides a method in which newsprint or fluting medium is made from an aqueous suspension of cellulosic fibres that is substantially free of filler and that has been-formed from a pulp having a cationic demand of at least 0.1 % and in which the drainage and retention properties of the suspension are improved by including in the suspension a water soluble polymer and 0.02 to 2% (dry weight based on the dry weight of the suspension) of a bentonite type clay, wherein the polymer is a substantially non-ionic polyacrylamide polymer containing 1 to 10 mole % acrylic acid groups and having molecular weight above 1 million and the clay is added to the pulp and the polymer is subsequently added to the pulp containing the clay, and the newsprint or fluting, medium contains less than 5% by weight total filler.

Claims: 1. A method in which newsprint or fluting medium is made from an aqueous suspension of cellulosic fibres that is substantially free of filler and that has been formed from a pulp having a cationic demand of at least 0.1% and in which the drainage and retention properties of the suspension are improved by including in the suspension a water soluble polymer and 0.02 to 2% (dry weight based on the dry weight of the suspension) of a bentonite type clay, wherein the polymer is a substantially non-ionic polyacrylamide polymer containing 1 to 10 mole % acrylic acid groups and having molecular weight above 1 million and the clay is added to the pulp and the polymer is subsequently added to the pulp containing the clay and the newsprint or fluting medium contains less than 5% by weight total filler. 2. A method according to claim 1 characterised in that the polymer is a copolymer of acrylamide with from 1 to 8 mole % acrylic acid groups. 3. A method according to claim 1 characterised in that the polymer is a copolymer of about 97 mole % acrylamide with about 3 mole % acrylic acid. 4. A method according to any preceding claim characterised in that the amount of bentonite clay is from 0.02 to 2% and the amount of polymer is from 0.005 to 0.1%, dry weight based on the dry weight of suspension. 5. A method according to any preceding claim characterised in that the amount of inorganic filler other than the bentonite that is added to the suspension is zero or less than 3% by weight. 6. A method according to any preceding claim characterised in that the aqueous suspension is free of aluminium sulphate and is formed from substantially only pulp, water, the polymer, the bentonite type clay and, optionally, filler in an amount such that the amount of filler including bentonite type clay is less than 5% by weight based on the dry weight of the newsprint or fluting medium.

Inventors: LANGLEY, JOHN GRAHAM, LITCHFIELD, EDWARD
Applicants: ALLIED COLLOIDS LIMITED
Application year: 1980
Main classification: D21H23
IPC codes: D21H17, D21H21, D21H23