PHOTOPOLYMERIZED HYDROPHILIC INTERPOLYMERS OF ACRYLIC ACID AND POLYFUNCTIONAL CROSS-LINKING AGENTS

Abstract: Highly water absorbent films and fibers are prepared by photopolymerizing an alkaline metal salt of acrylic acid, a polyfunctional cross-linking agent and a photoinitiator. The resulting interpolymers are particularly useful in the preparation of highly absorbent personal hygiene and care products.

Description: PHOTOPOLYMERIZED HYDROPHILIC INTERPOL-βlERS OF ACRYLIC ACID AND POLYFUNC IONAL CROSSLINKING AGENTS BACKGROUND OF THE INVENTION A variety of hydrophilic polymers which are useful in the manufacture of water absorbent films and fibers have been reported in the prior art. U.S. Patent 3,915,921 discloses copolymers of unsaturated carfaoxylic acid monomers with alkyl acrylate esters wherein the alkyl group contains 10 to 30 carbon atoms. However, because of the high Tg of these polymeric materials, it is difficult to extrude them in fiber or film form. Furthermore, films pressed from the powders require high temperatures, the films are brittle and fragile, and have a reduced initial rate of water absorption. U.S. Patent 4,062,817 discloses polymers of unsaturated copolymerizable carboxylic acids, at least one alkyl acrylate or methacrylate wherein the alk _1 group has 10 to 30 carbon atoms and another alkyl acry- late or methacrylate wherein the alkyl group has 1 to 8 carbons. This composition alleviated many of the de¬ ficiencies of the earlier compositions. Further im¬ provements in the hydrophilic properties were obtained by compositions disclosed in U.S. Patent 4,066,583. This patent discloses a composition comprising (1) a copolymer of the type disclosed in the '817 patent, except that after copolymerization 30 to 90 percent of the carboxylic groups were neutralized with an alkali metal or ammonia and (2) an aliphatic glycol, a plasti- cizer which is important in facilitating extrusion of the polymer. U.S. Patent 4,090,013 discloses a swellable, water absorbent composition which contains a high ' molecular weight polyelectrolyte which is a synthetic copolymer of an ethylenically unsaturated monomer and a mono-ethylenically unsaturated carboxylic acid such as acrylic acid. Additionally there may be di-functional monomer such as allyl methacrylate used in a very small amount as a chain extender (not a cross-linking agent) and a polyvalent metal cation, preferably aluminum, 5 which complexes the poly-electrolyte. After polymeri¬ zation the anionic groups of the poly-electrolyte may be neutralized with a base, such as an alkali-metal hydroxide. SUMMARY OF THE INVENTION 10 A cross-linked acrylic acid polymer is pre¬ pared by photopolymerizing 20 to 99.9 weight percent of acrylic acid, 50 to 100% of the carboxylic groups of said acid having been neutralized prior to polymeri¬ zation with an alkaline metal hydroxide, and 0.1 to 15 80 weight percent of a polyfunctional cross-linking agent. After spreading the monomer mixture to the de¬ sired thickness or after spinning it into a fiber it is polymerized upon exposure to a UV light source. The resulting film or fibers have extremely rapid and 20 high degree of absorption of water and body fluids, such as urine or blood. DETAILED DISCLOSURE This invention is directed to a photopolymer- ized interpolymer which has outstanding absorption and 25 retention properties of water and ionic body fluids such as urine or blood. The polymer is prepared from a) 20 to 99.9 weight percent of acrylic acid, 50 to 100 percent of the carboxylic groups having been neutralized with an alkali metal hydroxide or ammonia 30 base prior to polymerization, b) 0.1 to 80 weight percent of a polyfunc¬ tional cross-linking agent, and c) 0.01 to 5 weight percent of a photoini- tiator, said polymer having been polymerized by subject- 35 ing the monomer mixture to a UV light source. For economic reasons at least 50 weight per¬ cent of acrylic acid is employed and more preferably 90 to 99.5 weight percent of acrylic acid and 0.5 to 10 weight percent of a polyfunctional cross-linking agent are employed. Often materials having superior pro¬ perties are obtained when 0.2 to 5.0 weight percent of a poly-functional cross-linking agent is employed. The cross-linking agents that may be employed in this invention are mono eric compounds which contain . two or more ethylenically unsaturated groups which can be copolymerized with acrylic acid by UV light. Usually the cross-linking agents have two to six ethy- lenically unsaturated groups such as allyl, acrylate or vinyl groups. The nature of that portion of the ole- cule which does not contain ethylenic unsaturatidn is of no critical consequence as long as it does not poss¬ ess groups which would interfere with UV polymerization. Usually that part of the molecule is made up of a saturated hydrocarbon chain, a glycol or a polyglyσol moiety, an" aromatic moiety or cyanurate or isocyanurate ring or other non-polymerizable moieties. Polyfunctional compounds that may be used as cross-linking agents include, for example, diallyl esters or ethers, allyl or methallyl acrylates and acr lamides, diacrylates and dimethacrylates,divinyl compounds and the like. Illustrative examples of polyfunctional cross-linking agents are polyethyleneglycol diacrylate and dimethacrylate, ethylene glycol dime hacrylate, tetraethyleneglycol diacrylate, 1,3-butyleneglycol di- methacrylate, diethyleneglycol divinyl ether, tri e- thylolpropane diallyl ether, divinyl benzene, trimethy- lolpropane triacrylate, trimethylolpropane trimethacry- late, triallyl cyanurate, pentaerythritol triacrylate, diallyl itaconate, methylene bis(acrylamide) , allyl pentaerithritol, allyl sucrose, 1,6-hexanediol diacry¬ late, tetra ethylene diacrylate and dimethacrylate, ethylene diacrylate and dimethacrylate, triethylene- -g -EX^ glycol dimethacrylate and the like. Acrylic acid must be neutralized prior to polymerization at least 50 percent and preferably 75 percent. The most preferred degree of neutralization is 95 to 100 percent because it was noted that with higher degrees of neutralization the resulting polymers ex¬ hibit better absorbency properties. In addition to the above discussed monomers from, which the copolymers of this invention are pre- pared / minor amounts, that is usually less than 5 weight percent, but possibly up to 15 weight percent, of additional monomers may also be used. Whether these additional monomers are employed will depend on the end use and the physical properties required, that is, the speed and degree of absorption and the tear strength needed for the film or fabric. Such additional monomers are discussed below. One type of such additional monomers are ,β- olefinically unsaturated nitriles preferably the mono- olefinically unsaturated nitriles having from 3 to 10 carbon atoms such as acrylonitrile, methacrylonitrile, ethacrylonitrile, chloroacrylonitrile, and the like. Most preferred nitriles are acrylonitriles and meth¬ acrylonitrile. Another useful class of additional monomers which may be incorporated in the interpolymers of this invention is monoethylenically unsaturated amides which have at least one hydrogen on the amide nitrogen and the olefinic unsaturation is alphabeta to the carbonyl group. The preferred amides have the structure wherein R, is a member of the group consisting of hydro¬ gen and an alkyl group having from 1 to 4 carbon atoms and R. is a member of the group consisting of hydrogen and an alkyl group having from 1 to 6 carbon atoms. Representative amides include acrylamide, methacryl- amide, N-methyl acrylamide, N-t-butyl acrylamide, N- cyclohexyl acrylamide, N-ethyl acrylamide and others. Of the amides most preferred are acrylamide and eth- acrylamide. Other acrylic amides include N-alkylol amides of alpha, beta-olefinically unsaturated carboxylic acids including those having from 4 to 10 carbon atoms such as N-methylol acrylamide, N-ethanol acrylamide, N-propanol acrylamide, and the like. The preferred monomers of the N-alkylol amide type are the N-alkylol amides of alpha, beta-monoolefinically unsaturated monocarboxylic acids and the most preferred is N-methylol acrylamide. Also useful are N-alkoxymethyl acrylamides which have the structure wherein R_ is selected from the group consisting of hydrogen and methyl, and R is an alkyl group having from 1 to 8 carbon atoms. It is thus intended that where references are made herein regarding the essential N-substituted alkoxymethyl amides, the term "acryla¬ mide" includes "methacrylamide" within its meaning. The preferred alkoxymethyl acrylamides are those wherein R fi is an alkyl group containing from 2 to 5 carbon atoms, and especially useful is N-butoxymethyl acryla¬ mide. The above discussed monomers are copolymeriz- ed by subjecting the monomer mixture to UV light. If a film is desired the monomer can be spread on a surface to the desired thickness, e.g. 1 mil to 25 mil, and then subjected to UV light for a short time, e.g. 1 second to several minutes. The actual length of ir- C.. I ' • ' .-,. '' - ~ radiation will depend on a number of factors, such as the thickness of the monomer film, the distance from and the intensity of the source of irradiation, the specific monomers employed and the ratio of such mono- mers to each other, the presence or absence of addition¬ al comonomers and the nature and the amount of the photoinitiator employed. The type of photoinitiator employed will depend at least in part on the type of UV irradiation employed (particularly its wave length) since various photoinitiators may be decomposed by UV light of different wavelengths) . If it is desired that the material be in the form of fibers, the monomer mixture can be thickened and then spun into fibers which, upon exposure to UV light, are polymerized. In order to effect quick and efficient poly¬ merization under UV light, 0.01 to 5 weight percent of a photoinitiator, preferably 0.1 to 5 percent and more preferably 0.3 to 1.0 weight percent, must be incor¬ porated into the monomer mixture. Any compound which dissociates into free radicals when exposed to UV radiation can be employed. There are many known photo- initiators or photosensitizers such as acetophenone, propiophenone, benzophenone, xanthone, fluorenone, benzaldehyde, fluorene, aήthraquinone, triphenylamine, carbozole, 3- or 4-meth lacetophenone, 3- or 4-penty- lacetophenone, 3-or 4-methoxyacetophenone, 3- or 4- bromoacetophenone, 3- or 4-allylacetophenone, p-di- acetylbenzene, 3- or 4-methoxybenzophenone, 3- or 4- methylbenzophenone, 3- or 4-chlorobenzophenone, 4,4- di ethoxybenzophenone, 4-chloro-4' -benzylbenzophenone, 3-chloroxanthone, 3,9-dichloroxanthone, 3-chloro-8- nonyl-xanthone, 3-methoxyxanthone, 3-iodo-7-methoxy- xanthone, 2,2-dimethoxyacetophenone, 2,2-dimethoxy-2- phenylacetophenone, 2,2-diethoxyacetophenone, 2,2- dibutoxyacetophenone, 2,2-dihexoxyacetophenone, 2,2- di(2r-ethylhexoxy) acetophenone, 2,2-diphenoxyacetophen- one, benzoin, methyl benzoin ether, ethyl benzoin ether, isopropyl benzoin ether, butyl benzoin ether, isobutyl benzoin ether, benzoin acetate, benzoin phenyl carba- mate, α,α-diethoxyacetophenone, α,α-diethoxy-α-phenyl- acetophenone, α r --dimethoxy-α-phenylacetophenone, 4,4'- dicarboethoxybenzoinethyl ether, α-chloroacetophenone, α-bromoacetophenone, benzoin phenyl ether, α-methylben- zoin ethyl ether, benzoin acrylate, α÷methylobenzoin methyl ether, α,α,α-trichloroacetophenone, o-bromo- acetophenone, cumene hydroperoxide, benzoyl peroxide, dincu yl peroxide, tert-butyl perbenzoate, α,α-aso- bisisobutyronitrile, phenyl disulfide, chloro eth lben. zanthrone, chloromethylanthraquinone, chloromethyl- naphthalene, bromomethylbenzan hrone, bromomethylan- thraquinone, bromomethylnaphthalene, and the like. In addition to the photoinitiator it may be advantageous to employ also from 0.1 to 5.0 percent of an air cure promoter. Illustrative example of air cure promoters are mercaptoacetic acid, mercaptoethanol, Michler's ketone (4,4'-dimethylaminobenzophenone) , diethanolamine, methyl diethanolamine _ ethyl p-dime- - thylaminobenzoate r ~ and the like. The monomer mixtures are prepared as aqueous dispersions which eliminates the need for organic solvents. This avoids the pollution problems caused by the removal of organic solvents or the cost associ¬ ated with the removal of the pollutants. In order to obtain a stable homogeneous dispersion of the monomers, it is preferred that the aqueous dispersions contain 0.01 to 5%, and preferably 0.1 to 1%, of a surface active agent such as an anionic, amphoteric, or nonionic dispersing agent or a mixture of dispersants. Useful anionic dispersing agents include alkali metal or ammonium salts of the sulfates of alcohols having from 8 to 18 carbon atoms such as sodium lauryl sulfate; ethanolamine lauryl sulfate, ethylamine lauryl sulfate; alkali metal and ammonium salts of sulfonated petroleum and paraffin oils; sodium salts of aromatic sulfonic acids such as dodecane-1-sulfonic acid and octadecane-1-sulfonic acid; aralkyl sulfonates such as sodium isopropyl benzene sulfonate, sodium dodecyl benzene sulfonate and sodium isobutyl naphthalene sulfonate; alkali metal and ammon¬ ium salts of sulfonated dicarboxylic acid esters such as sodium dioctyl sulfosuccinate, disodium-n-octadecyl sulfosuccinate; alkali metal or ammonium salts of free acid of complex organic mono-and diphpsphate esters, sulfosuccinic acid derivatives (AEROSOL dispersants) , organic phosphate esters (GAFAC dispersants) and the like. Nonionic dispersants such as octyl-or nonylphenyl polyethoxyethanol as well as the PLURONIC and the TRITON dispersants may also be used. Also useful are ampho¬ teric dispersants such as dicarboxylic coconut deriva¬ tives (MIRANOL) . Further examples of useful dispersants are those disclosed beginning on page 102 in J. Van Alphen's "Rubber Chemicals", Elsevier Publishing Co., 1956. The copolymers of this invention can be photor polymerized in a film or a fiber form. The resulting film or fiber is an elastic, flexible material that has an appreciable degree of strength. If a fine, flaky form is desired, the film can be converted to such a form by drying and then pulverizing or grinding it standard equipment. As water absorbent materials these polymers find many uses in film, fiber, fabric and similar forms. They are of particular utility in the disposable non- woven industry where there is need for polymers which will absorb and retain water and ionic physiological fluids. An important feature of these polymers is their enhanced thickening property even in the presence of a salt. Specific applications include disposable diapers, medical-surgical supplies and personal care products. Such applications require a polymer which must imbibe the liquid to be absorbed rapidly and be a polymer that will not dissolve. Further, the fluid must be immobil- ized or congealed in some way to be retained. The materials may also be used as suitable additives to greatly increase the absorptive power of conventional absorbents such as cotton, wood pulp and other cellu- losic absorbents used in applications such as wiping cloths, surgical sponges, catamenial devices, and the like. In a specific application, for example, a dis¬ posable diaper, there is an inner layer of a soft absorbent nonwoven material that absorbs and passes urine to an inner layer of fluffy fibrous absorbent material, wherein during the construction of this non- woven fiber agglomerates or fibers of the polymers of this invention may be included and an additional imper¬ vious plastic layer, as polyethylene. A film of the copolymers of this invention may be used between the outer plastic layer and the inner fluffy absorbent O-.-FI layer. Use of the polymers of this invention can result in reduction in the bulk size of many disposable non- wovens. The instant copolymers can also be used as flocculants in water treatment, in metallurgical pro¬ cesses, in ore beneficiation and flotation, in agricul¬ tural applications such as in soil treatment or seed coating or in any applications where the inherent properties of the polymer are desirable, such as its thickening property in an aqueous medium. To prepare the polymers of this in¬ vention, acrylic acid, a cross-linking agent, a disper- sant and a photoinitiator are mixed in a vessel. Then either a film or fibers are produced from the monomer mixture which, upon exposure to UV light, are rapidly polymerized. The various steps in the procedure are described in greater detail below. Monomer_Mixture Preparation: The monomer mixture can be prepared by following one of two simple procedures. One method is to dissolve a previously prepared and dried alkali metal or ammonium acrylate in water to which is then added a dispersant. To the aqueous solution is then added a cross-linking agent which already contains a photoinitiator. Another method is to prepare the acrylate salt in situ by adding acrylic acid to the proper amount of cold aqueous base (e.g. KOH, NaOH or NH.OH) with cooling. To the aqueous solution is then added a cross-linking agent to which a photoinitiator was previously added; the dispersant is added last. Film Preparation: The aqueous monomer dis¬ persion is spread to a desired thickness (e.g. by the use of Boston-Bradley adjustable blade, by spraying or other known means) on a suitable substrate (e.g. Mylar, polyethylene, paper, etc.). The liquid film is then O..?I exposed to UV irradiation which polymerizes the monomer mixture into a soft, pliable form. If desired this film can be dried in an oven " at about 50°C for 1 to 15 min. After drying the film may still retain some flexibility or become brittle and flaky, depending on the length of drying. Fiber Preparation: The aqueous monomer dis¬ persion is thickened to the desired degree with a non- reactive thickening agent such as a cellulose derivative as for example hydroxypropyl cellulose, high molecular weight polyvinyl pyrrolidone. nd the like; natural ' gums such as guar gum, locust bean gum, gum tragacanth; agar, naturally occuring hydrocolloids such as alginates and the like. Fibers are then spun from a spinneret in a regular manner and immediately exposed to UV irradia¬ tion. To further illustrate the present invention the following examples are presented in table form below for illustrative purposes. The copolymers and the films were prepared according to the procedures described above. For each example in the table the amount of each ingredient employed is given. The amount of the X-linking agent in each example is preceded by a letter which identifies the specific cross-linking agents that are used in the examples and the letters by which they are identified. X-Linking Agents Used in Examples A - 1-.3-Butyleneglyσol dimethacrylate B - Polyethyleneglycol diacrylate C - Polyethyleneglycol dimethacrylate D - Ethyle eglycol dimethacrylate E - Diethyleneglycol divinyl ether F - Tetraethyleneglycol diacrylate G - Trimethylolpropane triacrylate H - Triallyl isocyanurate I - Diallyl itaconate J - Allyl methacrylate K - Allyl pentaerythritol L - N, N'-methylenebis(acrylamide) TABLE IA Example No, Sodium hydroxide 20.8g. 26.lg 26.lg 26.lg 26.Ig % Neutralization 75% 95% 95% 95% 95% Water 83.0g 102.Og 102.0g 102.0g 102.0 g Acrylic acid 50.0g 50.0g 50.0g 50.0g 50.0 g X-linking agent A 2.0g B 6.6g C 2.0g D 1.8g E 1.44g (a) AEROSOL A102 0.64g 0.72g 0.66g 0.66g 0.66g IRGACURE 65 ■ t» 0.64g 0.72g 0.66g 0.66g 0.66g to I (a)AEROSOL A102 is disodium ethoxylated alcohol half ester of sulfosuccinic acid, a dispersant (30% solution) " . (b) IRGACURE 651 is 2,2-dimethoxy-2-phenylacetophenone, a photoinitiator. TABLE IB Example No, 10 Sodium hydroxide 26.lg 12.5 g 26.lg 26.lg Potassium hydroxide 33.lg % Neutralization 95% 75% 85% 95% 95% Water 102. Og 50.Og 107.0, 102.0g 102.0g Acrylic Acid 50 . O g 30.0g 50.On 50.0 I<g -, 5 ^ 0..0«g, X-linking agent F 2 . 70 g G 1.6g J 0.95g H 2.2g I 2.Og I H AEROSOL A102 (a) 0 . 66g 0.38g ' 1.20g 0.66g 0.66g I (b) 10 IRGACURE 651 0. 66g 0.38g 0.70g 0.66g 0.66g (a)AEROSOL A102 is disodium ethoxylated alcohol half ester of sulfoscuccinic acid, a dispersant (30% solution). (b)IRGACURE 651 is 2,2-dimethρxy-2-phenylacetophenone, a photoinitiator. TABLE IC Example No. 11 12 13 14 Sodium hydroxide 28.3g 33.3g 26.lg Ammonium hydroxide — 45.Og — — % Neutralization 85% 100% 100% 95% Water 112.5g 40.Og 132.Og 102.Og Acrylic acid 60.Og 50.Og 60.Og 50.Og X-linking agent A 1.86g A 2.0g K 0.36g L 1.38g tn AEROSOL Λ102 1.32g 0.66g 1.32g 0.66g I 10 IRGACURE 651 - 0.66g - 1.92g Photoini iator 0.90gd) 0.8g (2) ( 1 ) Photoinitiator consisted of 0.6g of benzophenone and 0.3 of ethyl p-dimethylaminobenzoate. ^'Photoinitiator is photosensitizer E-7552 sold by Stauffer 15 Chemical Co. (a benzoin ether derivative) . Polymers having substantially the same properties are obtained when in some of the above compositions potassium hydroxide is employed in place of sodium or ammonium hydroxide, 2,2-diethσxyaceto- phenone in place of IRGACURE 651 and an oligomer ' ic surfactant POLYWET KX-3 (from Uniroyal) or TRITON N-lll (monophenoxy polyethoxy ethanol) in place of AEROSOL A102. A number of tests are available to determine the absorbency of a material. Following are descrip¬ tions of several test procedures which were employed in evaluating absorbency of the compositions of this invention. Demand Wettability Test (DWT) - A test diaper is con- structed frcm a 4 inch diameter pad (10.16. cm.) using materials from a commercial diaper. A film prepared from a polymer to be tested for absorbency is placed in the center of the test diaper between two layers of fluff (wood pulp) . A diaper without the polymer film is used as a blank. The de and-wettabiiity appa¬ ratus is a burette filled with the test fluid and firmly stoppered at the top, with an air bleed on the side, and a delivery orifice on the bottom connected by a flexible tube to the sample holder. The sample holder has an opening in the center which is connected to the flexi¬ ble tube that leads to the delivery orifice of the burette. The sample holder is level with the air bleed opening in the burette. With this closed-system ar¬ rangement the fluid in the flexible tube that comes up to the opening in the sample holder is at zero pressure. Thus when the test diaper is placed on the sample holder over the opening it will absorb the fluid on its own through wicking action. The sample's own absorbent powder will determine the rate and amount of fluid that will be withdrawn from the burette. The amount of fluid withdrawn at any given time can be easily read from the burette calibration. An additional feature is that absorbency can be measured against a range of pressures that can be obtained by placing various weights on top of the test diaper. Such pressures are intended to simulate the pressures applied on a diaper in actual use. The test is described in greater detail by Lichstein, "Demand Wettability, a New Method of Measur¬ ing Absorbency Characteristics of Fabrics", Symposium Papers - INDA Technical Symposium, 1974, pp. 129-142. Compression Test (CT) - This test is a follow-up test to the Demand-Wettability Test (DWT) . After the sample has absorbed the liquid against a lower pressure in a DWTest, it is removed from the DWT apparatus and placed atop a porous filter funnel. The sample is then 2 subjected to 1.5 psi (0.105 kg/cm ) of pressure for 1 minute and the amount of liquid that is squeezed from the sample is measured. Said pressure corresponds to the maximum pressure that is exerted on portions of a diaper when a toddler is picked up or held. This is 10 to 15 times the pressure that the diaper normally would experience. The sample is then weighed to deter¬ mine the amount of fluid in grams retained per one gram of polymer. Static Test (ST) - A weighed film sample is iinmersed in a test liquid for 10 minutes. It is then removed from the liquid, the excess liquid drained for a few seconds and then shaken lightly several times. The swelled sample is weighed again to determine the weight of liquid absorbed by the polymer. In Table II below is presented data showing the absorbency properties of the various polymers of this invention. Each polymer in Table II is identified by the Example No. in which it was prepared. The absorbency tests in the Table belowwere carried out with simulated urine which had the following composi¬ tions: 97.09% distilled water, 1.94% urea, 0.80% sodium chloride, 0.11% magnesium sulfate heptahydrate and 0.06% calcium chloride. The values expressed in the Table are grams or milliliters of liquid (as indicated) absorbed per one gram of the copolymer. TABLE II LIQUID ABSORPTION DATA DWT CT ST Polymer of Example (ml/g) ( g/g ) 1 37 32 35 2 31 26 22 « 3 34 29 31 4 38 31 40 5 37 33 27 6 34 25 24 7 34 28 25 8 38 37 44 9 44 32 48 10 33 " 27 25 11 42 33 52 12 25 - 44 13 31 - 60 14 22 20 19 O PI

Claims: CLAIMS 1. An interpolymer prepared by photopoly- merization of: a) 20 to 99.9 weight percent of acrylic acid, 50 to 100 percent of the carboxylic groups having been neutralized with an alkali metal or ammonium base prior to polymerization, b) 0.1 to 80 weight percent of a poly¬ functional cross-linking agent, and c) 0.01 to 5 weight percent, based on the weight of acrylic acid and a cross-linking agent, of a photoinitiator. ' 2. An interpolymer of Claim 1 containing additionally 0.1 to 5 percent of a dispersant. 3. An interpolymer of Claim 2, wherein a) acrylic acid is in the amount of from 50 to 99.5 weight percent, the carboxylic groups having been neutralized from 75 to 100 percent, b) polyfunctional cross-linking agent is in the amount of from 0.5 to 50 weight percent, c) photoinitiator is in the amount of from 0.3 to 1.0 percent, and d) a dispersant is in the amount of from 0.1 to 1.0 percent. 4. An interpolymer of Claim 3 wherein the polyfunctional cross-linking agent is a monomeric - compound which contains two or more ethylenically un¬ saturated groups which can be copolymerized with acrylic acid by UV light. 5. An interpolymer of Claim 4 wherein the photoinitiator is 2,2-dimethoxy-2-phenylacetophenone, N,N' -bis (diethylamino)benzophenone, ethyl p-dimethylamino benzoate, benzophenone, a benzoin ether, or a mixture thereof. 6. An interpolymer of Claim 5 wherein a) acrylic acid is used in the amount of from 90 to 99.5 weight percent, b) polyfunctional cross-linking agent is used in the amount of from 0.5 to 10 weight percent. 7. An interpolymer of Claim 6 wherein " the polyfunctional cross-linking agent is selected from the group consisting of 1,3-butyleneglycol dimethacrylate polyethyleneglycol diacrylate polyethyleneglycol dimethacrylate ethyleneglycol dimethacrylate diethyleneglycol divinyl ether tetraethyleneglycol diacrylate trimethylolpropane trimethacrylate triallyl isocyanurate diallyl itaconate allyl methacrylate llyl pentaerythritol N, N * -methylenebis(acrylamide) 8. An interpolymer of Claim 2 prepared from a) from 94 to 98 weight percent of acry¬ lic acid, b) from 2 to 5 weight percent of a cross-linking agent of Claim 7, and c) from 1 to 3 weight percent of a photoinitiator of Claim 5. 9. An interpolymer of Claim 1 in the form of a film which is highly absorbent of aqueous liquids. 10. An interpolymer of Claim 1 in the form of a fiber which is highly absorbent of aqueous liquids. 11. An article of manufacture designed for absorbing body fluids comprising an absorbent cellu¬ lose material and a polymer of Claim 1 in the form of a film or fibers. O..PI

Inventors: GEORGE P
Applicants: GOODRICH CO B F
Application year: 1980
Main classification: C08F2
IPC codes: A61F13, A61L15, C08F2, C08F20, C08F220, C08F222, C08J5