SODIUM SULPHUR CELLS, CATHODE STRUCTURES THEREFOR, AND THE MANUFACTURE OF SUCH CELLS AND STRUCTURES

Abstract: In a sodium sulphur cell, having a cathode structure 15 (Figure 1) between a cathode current collector 14 and a solid electrolyte 10, the cathode structure is formed of a fibre material with at least 90% of mesophase-pitch-based carbon fibre material with the fibres oriented in two dimensions parallel to the plane of a mat, the mat then being needle-punched to re-align fibres and so increase the electrical conductivity transverse to the plane of the mat. Preferably up to 10% of a material having a greater resistance to bending is incorporated before needling; these may be carbon fibres which are non-mesophase-pitch-based. Alumina or other electrically non-conductive fibres may alternatively or additionally be incorporated. These further fibres can be chosen to improve the resilience of the cathode structure. The mat is impregnated with the cathodic reactant, i.e. sulphur or sodium polysulphides, in liquid form and cooled while compressed to solidify the reactant and form a rigid unit for insertion in the cell, which unit will expand when the reactant is liquified at the operating temperature.

Description: "SODIUM SULPHUR CELLS, CATHODE STRUCTURES THEREFOR, AND THE MANUFACTURE OF SUCH CELLS AND STRUCTURES" - This invention relates to sodium sulphur cells and to cathode structures therefor-ar,d-to their manufacture. In a sodium-sulphur ceil, a solid electrolyte material which will conduct sodium ions, for example heta-alurana, separates sodium ,constituting the anode, from a cathode containing the cathodic reactant comprising sulphur and sodium polysulphides. To provide electronic conductivity in the cathodic region, this region normally contains a conductive fibre matrix, e.g. a carbon fibre matrix which is impregnated with the cathodic reactant. Reference may be made to U.S.Specifications Nos.4,052,535; 4,076,9E2; 4,118,545 and 4,176,447 as examples of such co.#i'#. The cathode matrix structure desirably has an electrical resistance which is very low and, for this reason, use has been made of a carbon felt formed of synthetic fibres, for example rayon fibres, which have been felted b#y a needle-punching operation, the felted sheet then being carbonised. The material known as Le Carbone RVC 4000 is such a material which has been extensively used in sodium sulphur cells. More recently carbon fibres manufactured from pitch have become available. The pitch base route for manufacture of carbon fibres is more efficient and produces a lower cost product than the carbonisation of fibres such as rayon. Such pitch-based fibres however heretofore have not been entirely satisfactory in sodium sulphur cells because of the form in which such fibres are commercially available. There are at present two basic types of pitch-based carbon fibre available, differing in type of pitch and precursor employed. Historically the first such fibres were made of non-mesophase pitch. Reference may be made for example to British Patent Specification No.1091890 for a description of one process for producing such fibres. Fibres produced from this material resemble vitreous carbon and typically have a tensile modulus of 5.5 x106 psi and an electrical resistivity of 7.5 x 10 Acm. Subsequently improved fibres were obtained by the use of mesophase pitch (see for example British Patent Specification No.1416614). These fibres are essentially graphitic with a high degree of alignment (greater than 908) of the graphite planes along the length of the fibre. Consequently they have both a higher tensile modulus (typically 3,5 x 107 psi) and a lower resistivity (typically 1.2 x iO 3zuc) than the nonmesophase fibres. Because of their löwer electrical resistivity, the mesophase fibres are the type which would be preferred for use in sodium sulphur cells. However mesophase fibres as commercially available have certain Arawbacks. Both mesophase and non-mesophase pitch-based fibres are produced from a liquid, the fibres being produced, for example by melt-spinning techniques,and the liquid phase material is converted by heat treatment into carbon fibres. Thus it is not possible to form a textile material before the fibres are carbonised and hence the material cannot be made into a felt by needle-punching prior to carbonisation. For this reason one form in which the mesophase material is commercially sold is a low density mat comprising a number of. thin webs superimposed one above the other, the fibres being aligned in the webs and hence being essentially two-dimensionally orientated. Material in this form has two particular disadvantages when considered for use in the cathode structure of a sodium sulphur cell. Firstly the most convenient method of forming the sulphur electrode from such a sheet results in the electrode having almost-all the fibres oriented perpendicular to the current flow and therefore yiving substantially higher electrical resistance than would be the case if the fibres were oented in the direction of current flows Secondly', as will be explained later, the iniivIdual fibres are subjected to bending forest whilst mes-opllase-pitch-based carbon fibres have a very high tensile strength, the elengation to break is. low, and compression of the material either across the direction of the fibres or in the direction of the fibres to cause bending stresses, results in fibre breakage and consequential loss of resilience and conduct-anee in the material. Forever, the improvement in cathode material utilisation in a sodium sulphur cell which is often seen with the use of mesophase-pitch-#based carbon fibres makes their continued use attractive. In order more fully to explain the above-mentioned disadvantages of mesophase pitch-based fibres, it is necessary to consider further the construction of -sodium--sulphur cells. In a flat plate cell, the electrode structure is arranged as a sheet, of thickness small compared with its linear dimensions, between a flat electrolyte plate and a current collector. Sheets as described above with two dimensionally orientated fibres have the fibres in the wrong direction for optimum electrical conductance across the cathode structure between the electrolyte and current collector. More commonly sodium sulphur cells are of tubular form with the cathode electrode structure in an annular region adjacent one surface of an electrolyte tube. The electrode structure may be inside or outside the electrode tube, but in each case it is in an annular region between the surface of the electrolyte and a cylindrical current collector. Again, the two-dimensionally orientated fibres of the sheets as described above, in any simple method of assembly, result in the fibres extending parallel to the electrolyte surface instead of in the preferred direction from the electrolyte surface to the current collector. In sodium sulphur cells, a particularly convenient method of forming a cathode electrode is to compress the matrix material either before or after impregnation with sulphur or with sodium polysulphides in liquid form, then to cool the material to below the freezing point of the liquid so as to form a solid preform. One or more such preforms may be assembled into a sodium sulphur cell and, Me the cell is brought up to the operating temperature, the liquid melts and, by the resilience of the fibre material, the electrode structure expands into close contact with the electrolyte and the current collector. With mesophase-pitch-based fibres, the high tensile modulus of the fibres is accompanied by low elongation to break, The compression necessary to form such preforms results in fibres being subjected to bending moments with consequent fibre breakage. If the fibres were perpendicular to the plane of the sheet, compression in this direction would also subject the fibres to bending moments because of fibre buckling, resulting again in fibre breakage. Thus, if mesophase-pitch-based fibres are to be used in a sodium sulphur cell, the low elongation to break of the material is a tsawback, particularly if preforms are used requiring compression pf the m#texiffla1. According to one aspect of the present invention, a method of making a sulphur electrode for a sodium sulphur cell comprises the steps of forming a two-dimensionally oriented mat of fibres comprising at least 908 of mesophase-pitch-based carbon fibres; the fibres being oriented generally parallel to the plane of the mat, and needle-punching the mat, the needle-punching being transverse to the orientation of the fibres. It has been found that, b needle-punching mesophase-pitch based fibres perpendicular to the plane of the fibres, a proportion of the fibres are re-aligned transversely to this plane and improvements in conductivity in this direction of up to 300% have been observed. Thus the needle punching of a two-dimensional mat of mesophase-pitch-based fibres gives a very significant improvement in the performance of this material as an electrode structure when used in a sodium sulphur cell with the aforementioned two-d4mension mat generally parallel to the plane of the electrolyte surface. In one form of the invention, the mat of fibres consists wholly of mesoDhase-pitch-based fibres which have been needle-pun#ed as described above. The needle-punching on its own however, whilst giving a s: nificant amprovement over existing cathode structures using mesophase-pitch-based fibres, does not give any improvement in the resilience. In a preferred form of the invention, a method of forming a cathode structure for a sodium sulphur cell comprises the steps of forming a two-dimension oriented mat of fibres comprising between 90 and 99% by weight of mesophase-#itch-based carbon fibres, the remaining fibres being of a material having a higher resistance to bending than the mesophase-pitch-based carbon fibres and then needle-punching the mat, the needle-punching being transverse to the orientation of the fibres. The said remaining fibres may be non-mesophase-pitch-based carbon fibres. They may be fibres of an electrically conductive material but this is not essential. These said remaining fibres may be for example glass or ceramic fibres. The introduction of these further fibres having a much higher resistance to bending results in a significant improvement in the resilience of the mat. Using 108 by weight of nonmesophase-pitch-based carbon fibres in a mat of mesophase-pitch-based fibres has been found to give an improvement in the resilience of the order of 1002. The introduction of these further fibres in general will not signifl#cant1y affect the eonductivity. The conductivity however in the direction transverse to the plane of the mat is improved, as previously described, by the needle-punching which re-aligns a proportion of the fibres in the required direction. The non-mesophase-pitch-bas-ed carbon fibres may be distributed through the body of the mat or may form a layer on one or both surfaces thereof. One particularly advantageous arrangement which may be used in some cases is to use electrically non-conducting fibres, e.g. alumina fibres, which do not have greater resistance to bending, in addition to the non-mes-ophase-pitch-based fibres and to arrange these on one surface of a sheet of the carbon fibres to form the mat. The higher electrical resistance near the electrolyte surface gives an improved distribution of the electrochemical reaction through the cathodic region. In some cases it may be preferred to use electrically nonconducting fibres as the sole addition to the mesophase-pitch-based fibres, i.e. without the addition of non-mesophase-pitch-based carbon fibres. In these cases the resilience of the material will not be improved significantly but the improved electrochemical reaction distribution may be considered advantageous. The invention furthermore includes within its scope a method of forming a sodium sulphur cell having a cathode structure arranged between a surface of a solid electrolyte material and a surface of a current collector spaced away from the electrolyte surface wherein a mat of two-dimensionally arranged fibres comprising at least 90% mesophase-pitch-based carbon fibres, with the fibres arranged parallel to the plane# of the mat, is needlepunched to re-align a proportion of fibres perpendicularly to the plane of the mat and the mat is then impregnated with sulphur and/or sodium polysulphides and inserted in the cell between the aforementioned surfaces with the plane of the mat parallel to the electrolyte surface and the re-aligned fibre extending transversely to that surface. As indicated above, preferably between 1 and 10% of the fibres in the mat are of a material having a greater resistance to bending than the mesophase-pitch-based carbon fibres, these further fibres being needled into the mat by the needle-punching operation. For a tubular cell, the mat may be arranged into an annular preform comprising one or more segments by impregnating the mat with a cathodic reactant material in liquid form, compressing the mat before or after impregnation to the required shape and cooling the mat to solidify the reactant material. The segments may be of trapezoid form in section as described in the United States Patent Specification No.4,176,447. The invention also includes within its scope a cathode structure for a sodium sulphur cell comprising a mat of substantially two-dimensionally orientated fibres, at least 90% of which by weight, are of mesophasepitch-based carbon; the mat having been subjected to needle-punching transversely to said two imrnsions to re-align a proportion of tbe fibres tr-7nsversniy to this plane. The invention furthermore includes within its scope a sodium sulphur cell having a cathodic region between one surface of. a solid electrolyte and a facing surface of a cathode current collector, which cathodic region contains a mat of fibres comprising at least 90% by weight of mesophase-pitch-based-carbon fibres, the mat being of two-dimensionally orientated fibres which have been needle-punched transversely to, the plane of orientation of the fibres thereby to re-align a proportion of the fibres transversely. to said plane, and the mat being arranged in the ceil with said plane generally parallel to said one sur-face of the electrolyte.. In the following description, reference will be made to the accompanying drawings in which: Figure 1 is a diagrammatic cross-section through a tubular sodium sulphur cell forming one embodiment of the invention; and Figure 2 is a cross-section through a fibre assembly for forming a cathode structure for a sodium sulphur cell. Referring to Figure 1 there is shown a sodium sulphur cell comprising a tube 10 of solid electrolyte material, typically beta-alumina, which separates an anodic region from a cathodic region. In this particular cell, the-anodic region containing liquid sodium 11 lies around the outside of the electrolyte tube 10 in an annular region between that tube and an outer metal casing 12 forming an anode current collector. Capillary means 3a-t.ie p c:idet' Jn the anodic region to ensure that the outer surface of the electrolyte tuae iag wetted by a thin layer of liquid sodium.. Tiue cathode current collector 14 extends axially down the length of the electrolyte tube and the cathodic region between this current collector 14 and the electrolyte tube 10 contains a cathode structure comprising a fibre matrix 15 formed as a plurality of segments 16 each of which is of substantially trapezoidal section. The present invention is concerned more particularly with the cathode structure. This cathode structure is formed of a sheet of mesophase-pitch-based carbon fibre material, for example material sold under the trade name Thornel VMA, which has the fibres arranged two-dimensionally and essentially parallel to the general plane of the sheet. The sheet is flexible but may be considered initially as being a flat sheet. Additional fibres are put on one or both surfaces of the sheet, these fibres being preferably carbon fibres but being fibres which have substantially greater resistance to bending than the mesophase-pitch-based carbon fibres. Such fibres will in general have a lower tensile strength and they may have a lower electrical conductivity than the mesciphase-pitch- based carbon fibres. As one example of a suitable material for the additional fibres, we have employed Kunha TlOlT carbon fibres, these being non-mesophase-pitch-.based fibres The mat with the Qddit.ipnal fibres is needle-punched so as to needle these further fibres into the mat. This needle-punching at. the same time causes a proportion of the mesophase-pitch-based carbon fibres to be re-aligned transversely to the general plane of the mat. The mat is then formed into the trapezoidal segments, for example in the manner described in the aforementioned United States Specification No.4,17#,A47. This is. done essentially by compression of the mat transversely to its plane, for example, by using shaped moulds. The moulds may be heated and the mat can then be impregnated at the same time as it is. compressed. Alternatively it may be impregnated before compression with the cathodic reactant. The imprenation is conveniently with liquid sulphur but it is alternatively possible to use liquid polysulphides. whilst still compressed, the mat is cooled so as to form a solid block This enables the segments to be handled and to be inserted into the annular region of the cell between the electrolyte and cathode current collector. When the cell is heated to the operating temperature, the cathodic reactant is raised above its melting point permitting the fibre material of the mat to expand resiliently into good contact with the electrolyte surface and the current collector. it is convenient to compress the material as a sheet in a substantially flat plane. The trapezoidal segments conveniently therefore each have a pair of straight parallel sides which, when cut wn the cell, have to conform to circular arcs. The segments must be slightly smaller than the annular region into which dley are put in order to facilitate assembly and thus the expanSion, by reazon of the resilience of the fibre material, when the reactant is melted, is necessary to ensure good contact with the electrolyte and the current collector. The needling of the material gives a very substantial improvement in conductivity perpendicular to the plane of the mat compared with a mat having the two-dimensionally oriented fibres parallel to the plane of the mat. The needling further introduces the additional fibres into the matrix material which gives a significant improvement in the resilience of the mat In a typical example in which non-mesophase-pitch-based carbon fibres amounting to 10% by sleight of the total material in the mat were introduced into a mat formed of mesophase carbon fibres, an Xmprovement of 100% in resilience has been obtained. This improvement in resilience ensures good contact between the surfaces of the mat and the surfaces of the electrolyte and current collector. The non-mesophase-pitch-based fibres might be mixed with the mesophase-pitch-based fibres but, for convenience of manufacture, it is preferred to put these further fibres on one or both surfaces of a sheet of mesophase-pitch-based fibres. In some cases it may also be preferred to include non-conductive f#br..es on one surface Of themat in a¯dYtton to the non-mesophase-pitch-based carbon fibres to form a layer of rednee: eleetrical conduftivity (compared with the rest of the mat) at the surface which is to be adjacent the electrolyte material in the cell. One construction of this kind is illustrated in Figure 2 which is a section (to an enlarged scale compared with Figure 1) through a mat of fibre material, for forming a cathode structure for a sodium sulphur cell, prior to needling and impregnating with the cathodic reactant, i.e. sulphur or sodium polysulphides. In Figure 2, the bulk of the material, shown at 20, is a mesophase-pitch-based carbon fibre such as Thornel VMA but, over one surface of the mat is a layer 21 of alumina fibres and non-mesophase-pitch-based carbon fibres. It is preferred to use a polycrystalline alumina in a transitional form with a small percentage of other inorganic oxides as crystal phase stabilisers, for example, material sold under the Trade Mark "Saffil". This material is microporous and has a large surface area. It is electrically non-conductive. It is chemically inert to sulphuripolysulphides forming the cathodic reactant. It has a further advantage that, at the operating temperature of the cell, it is more easily wetted by the polysulphides than is the carbon material. The layer 21 of alumina fibres and non-mesophase-pitch-based carbon fibres is thin compared with the carbon fibre sleet 20, the alumina being less. than 105 by weight of the total fibre content. The needle- punching results in re-alignment of some of the fibres of the three materials. The re-alignment of the carbon fibres gives a very substantial improvement in electric conductivity measured in the direction between electrolyte and current collector, i.e. normal to the sheet. The thin layer of alumina fibres however causes the cathode structure to have a higher electrical resistance nearer the electrolyte; this is desirable to give a better distribution of the electrochemical reaction through the body- of the fibre matrix. The non- mesophase-pitch-based carbon fibres give the des-ired improvement in resilience of the structure compared with a cathode structure using only mesophase5 pitch-based carbon fibres.

Claims: cLAIMs.#- 1. A method oç m.a#i.#g a sulphur electrode for a sodium sulphur cell from a mat of fibre material characterised by comprising the steps of forming said mat as a mat of two#di.mensionally oriented fibres comprising at least 908 of mesophase-pitch-based carbon fibres, the fibres being oriented generally parallel to the plane of the mat, and then needlepunching the mat, the needle-punching being transverse to the orientation of the fibres. 2. A method as claimed in claim 1 characterised in that said mat is formed wholly of mesophase-pitch-based carbon fibres. 3. A methoa of forming a cathode structure for a sodium sulphur cell from a mat of fibre material cizaracterised by comprising the steps of forming said mat as a mat of two-dimension oriented fibres comprising between 90 and 99% by weight of mesophase-pitch-based carbon fibres, the remaining fibres being of a material having a higher rcsistance to bending than the mesophase-pitch-based carbon fibres, and then needlepunching the mat, the needle-punching being transverse to the orientation of#the fibres. 4. A method of .m##i),#g a cathode structure for a So;zuzn sulphur cell from a mat of fibre material. charaeteri'se# by comprising the steps of forming a two- dimens1;#nally oriented mat of fibres comprising between 90 and 99g by weight of mesophase-pitch-based carbon fibres, the remaining fibres being of an electrically non conductive material, and needle-panehing the mat, the needle-punching being transverse to the orientation of the fibres. 5. A method as claimed in claim 3 characterised in that said remaining fibres are non- -mesophase-pitch-based carbon fibres. 6. A method as claimed in claim 3 characterised in that said remaining fibres are fibres of. an electrically conductive material. 7. A method as claimed in claim 3 characterised in that said remaining fibres are glass or ceramic fibres. 8. A method as claimed in claim 3 characterised in that the mat is formed with said remaining fibres mixed with said mesophasepitch-based carbon fibres. 9. A method as claimed in claim 3 characterised in that the mat is formed of a sheet of said mesophase-pitch-based carbon fibres with said remaining fibres on one or both surfaces of the sheet. 10. A method as claimed in claim 4 characterised in that said remaining fibres are arranged on one surface of the sheet. 11. A method as claimed in claim 4 characterised in that said remaining fibres are of glass or ceramic. 12. A method as claimed in any of elas: 3 to 2 characterised in that, for use Fin R tubular cell, the mat is arr#c#,d aa an annular prevorR comprising a plurality of segments by am.pregnatIng the mat with a cathodic reactant in liquid form, compressing the mat before or after impregnation to the required shape and then cooling the mat to solidify the reactant material. 13. A method of making a sodium sulphur cell having a cathode structure of fibre material arranged between a surface of a solid electrolyte material and a surface of a current collector spaced a,7ay from the electrolyte, surface characterised by the steps of making a mat of two-dimensionally arranged fibres comprising at least 90% mesophase-pitch-based carbon fibres, with the fibres arranged parallel to the plane of the mat, needle-punching the mat to re--align a proportion of fibres perpendicularly to the plane of the mat, impregnating the mat with sulphur and/or sodium polysulphides, and inserting the impregnated mat in the cell between the aforementioned surfaces to constitute said cathode structure with the plane of the mat parallel to the electrolyte surface and the re-aligned fibres extending transversely to that surface. 14. A method a claimed in claim 13 characterised in -thRt between q and 10% on the fibres' in the mat are -of a material having a greater resistance to, bending than the mesophase-pitch-based carbon fibres, these further fibres being needled into the mat by the needle-punching operation. 15. A raethod as claimed in claim 34 characterised in that the mat iS formed as a sheet of mesophase-pitchbased fibres with said fibres of a material having a greater resistance to bending and being, fibres of an electrically non-conducting material arranged on one surface of said sheet, to form a layer adjacent the electrolyte when the impregnated mat is inserted in the cell. 16. A cathode structure for a sodium sulphur cell comprising a mat of fibre material characterised in that said mat is formed of substantially two-dimensionally oriented fibres, at least SOt of which, by weight, are of mesophase-pitch-based carbon, the mat having been subJected to needle-punching transversely to said two dimensions to re-align a proportion of the fibres transversely to the plane. iT. A cathode structure as claimed in claim 16 charaeternsed in that said mat is topRe: wholly of iaeso'ph#e--pit & ±b#ased carbon fibres. 18. A cathode structure as claimed in claim 16 characterised in that between 1 and 10% by weight of the fibres are of a material having a higher resistance to bending than said mesophase-pitch-based carbon fibres. 19. A cathode structure as claimed in claim 14 characterised in that said mat is a sheet of carbon fibres having a layer of electrically non-conducting fibres on one surface thereof. 20. A cathode structure as claimed in claim 16 characterised in that between 1 and 10% by weight of the fibres comprise non-mesophase-pitch-based carbon fibres together with electrically non-conducting fibres. 21. A sodium sulphur cell having a cathodic region between one surface of a solid electrolyte and a facing surface of a cathode current collector, which cathodic region contains a mat of fibres characterised in that said mat comprises at least 90% by weight of mesophase-pitch-based carbon fibres, the mat being of two-dimensionally oriented fibres which have been needlepunched transversely to the plane of orientation of the fibres thereby to re-align a proportion of the fibres transversely to said plane, and in that the mat is arranged in the cell with said plane generally parallel to said one surface of the electrolyte. 22.. A cell, as. #1#i#,#,d 42. c.l#%m 2i characterised in that the Rat is wholly formed of mesophase-pitch-based carbon fibres. 23. A cell as claimed in clam 21 characterised in that the mat comprises at least 90% by eight of mesophasepitch-based carbon fibres, the remainder comprising carbon fibres having a higher resistance to bending than the mesophase-pitch-based carbon fibres. 24. A cell as- claimed in claim 21 characterised in that the mat comprises at least 90% by weight of mesophase #itch-based carbon fibres, the remainder being fibres of an electrically non--conducting material. 25. A cell as claimed in claim 24 characterised in that said fibres of electrically non-conducting material are alumina fibres. 26. A cell as claimed in either claim 24 or claim 25 characterised in that said mat comprises a sheet of said mesophase-pitch-based fibres with the electrically non-conduftive fibres on one surface of said sheet, and in that the mat is arranged in the cell with the electrically non-conductive fibres forming a layer of lower electrical conductivity, compared with the bulk of the z¯t, between the surface of the electrolyte and the carbon fibres.

Inventors: BRENNAN, MICHAEL PATRICK JOSEPH
Applicants: CHLORIDE SILENT POWER LIMITED
Application year: 1980
Main classification: H01M4
IPC codes: H01M4, H01M10