DRY MIX FOR FORMING INSULATING COMPOSITIONS AND THERMALLY INSULATED CONTAINERS MADE FROM SAID COMPOSITIONS, SPRAYABLE INSULATING COMPOSITIONS PREPARABLE FROM SAID DRY MIX, AND A METHOD OF APPLYING INSULATING MATERIAL USING SAID SPRAYABLE COMPOSITIONS

Abstract: Insulation materials, paticularly sprayed insulation mat­ erials, are often based upon petro-chemical products which are expensive and present toxic gas and fire hazards. The present invention, in contrast, enables the provision of a lightweight sprayable, non-toxic, insulating composition. In one aspect the invention provides a dry mix for mixing with water to produce an insulating composition curable at ambient temperature, which dry mix comprises expanded perlite, Portland cement, hydrated lime and diatomite. The sprayable composition of the invention is curable at ambient temperature and comprises the above dry mix, or the ingredients thereof separately or in any combination, admixed with an aqueous solution of a water-soluble foaming agent, preferably containing 0.25 - 2 ounce per Imperial gallon of the agent and preferably 20-26 pounds of the dry mix being used per Imperial gallon of aqueous solution.

Description: DRY MIX FOR FORMING INSULATING COMPOSITIONS AND THERMALLY INSULATED CONTAINERS MADE FROM SAID COMPOSITIONS, SPRAYABLE INSULATING COMPOSITIONS PREPARABLE FROM SAID DRY MIX, AND A METHOD OF APPLYING INSULATING MATERIAL USING SAID SPRAYABLE COMPOSITIONS. This invention is concerned with a dry mix for mixing with water to produce an insulating composition, uses of such a composition, a sprayable insulating composition which may be prepared from the dry mix and a method of applying insulating material to an article, area or building structure. In a particularly preferred aspect the invention provides a cold mixable and cold curable non-combustible, non-toxic material that is useful as insulation and as a fire, acoustic and weather barrier and which may be sprayed onto any substrate that is capable of receiving the material. The invention also teaches the pressure feeding of pre-expanded perlite particles without destroying the geodedic structure and strength of the particles and the insulation qualities of cold state perlite. The material can also be used to fill confined spaces such as wall cavities and attics and hollow Partitions used in the construction industry and can be used for fire, acoustic and insulation barriers for vehicles, ships, transporters and any other form of container that has need of thermal insulation for high and low temperatures. Sprayed or foamed-in-place insulation materials presently in use are generally derived from petrochemical products, either as a source of the basic material mass or as a source of bonding or adhesive agents thereafter. These materials are not only becoming increasingly expensive and difficult to obtain, but also can, by virtue of their combustibility become fire hazards and give rise to toxic and lethal fumes and smoke when used in buildings or other confined areas. Petrochemical products used as external insulation can degrade from exposure to extreme weather conditions and solar radiation. Accordingly, lamination or coating to provide a barrier against weathering may be required. The usual method for overcoming fire hazard risks in insulation is to use a dry board insulation material such as Vermiculite or Gypsum. These materials have the disadvantage of both being subject to water absorption and a tendency to expand, increase drag weight and pull away in humid or extreme weather conditions. In addition, dry boards have to be cut to shape to encase angles etc. AlsQ, dry insulation panels are restricted by the very nature of their basic structures, to interior use. The present invention allows the on-site use of cold state, pre-expanded perlite particles (loose form) which may be pre-mixed in a cold state and thereafter passed to a spray gun nozzle without fracture or breakdown of the natural geodedic strength or insulation qualities of of expanded perlite particles whereby a coating on predetermined thickness, e.g. up to an immediate 2 inches, can be sprayed and thus be applied to any substrate capable of receiving it, following any angles or contours of the substrate with a uniformity of desired thickness of coating. Such coatings can provide pre-determined insulation requirements plus having the ability to act as fire barriers that will not degrade or emit toxics at temperatures in excess of 17000F. for periods of time depending upon the initial insulation thickness. Such insulation has no need of heat for curing apart from an ambient temperature in excess of 400F, and, by the nature of the aggregate used, i.e. expanded perlite particles, the material cost is low and the material is also abundant. According to the present invention there is provided a dry mix for mixing with water to produce an insulating compound curable at ambient temperature, which dry mix comprises expanded perlite, Portland cement, hydrated lime and diatomite. More preferably, the mix contains 100-120 parts by volume of expanded perlite, 20-30 parts by volume of Portland cement, 0.5-2.0 parts by volume of hydrated lime and 0.1-1.0 parts by volume of diatomite. Even more preferably the mix contains 105-115 parts by volume of expanded perlite, 24-26 parts by volume of Portland cement, 0.5-1.5 parts by volume of hydrated lime and 0.25-0.75 parts by volume of diatomite. In a compositional aspect, this invention also provides a sprayable insulating composition curable at ambient temperature comprising a dry mix of the invention, preferably a dry mix of 100-120 parts by volume of expanded perlite, 20-30 parts by volume of Portland cement, 0.5-2.0 parts by volume of hydrated lime and 0.1-1.0 parts by volume of diatomite, or the ingredients of the dry mix separately or in any combination admixed with an aqueous solution of water soluble foaming agent, preferably containing 0.25-2 ounce per Imperial gallon of the agent, preferably at a level of 20-26 pounds of dry mix per Imperial gallon of solution. In a method aspect, the invention provides a method of applying insulating material to an article, area (e.g. a confined area) or building structure by spraying the same with the foregoing composition at a pressure of 30.50 psi. The composition of this invention may by mixing the above-defined dry mix with water can be cold cured in a number of applications. They can be used for insulation of ventilation and window fittings and for insulation of floors, walls, ceilings structural beams etc. They can also be used to make separate insulating structures, e.g. thermally insulating doors or containers. Thus, in another aspect, the invention provides a thermally insulated box comprising an insulating wall which has been formed by hardening or setting to a desired shape a composition as described or the ingredients thereof. The container may, if desired, be provided with an outer skin, e.g. a skin made of metal. Alternatively, an "inner" skin may be provided. Furthermore, the invention embraces the possibility of only a part of the container being insulated by the use of an insulating wall as defined. However, it is preferred that the container be made entirely or in major part from an insulating wall as defined. The insulating wall in the container may be constituted by a plurality of panels which may be formed of desired dimensions using conventional tools. Where the insulating wall used in the present container is constituted by a plurality of panels, those panels may be bonded together to form the desired insulating structure by the use of an adhesive agent. A suitable adhesive agent is a paste mixture of vermiculite(exfoliated mica), talc and aqueous sodium silicate solution (preferably containing 20 to 22 parts of water per 100 parts of sodium silicate). "Portland cement" as used herein is a mixture of Ca, Si, Al, Fe and Mg, generally corresponding to calcium silicate, 3CaO.SiO2, dicalcium silicate, 2CaO.Si02, tricalcium aluminate, 3CaO.A1203, tetracalcium-aluminaferrite, 4CaO.A120 3.Fe203 and calcium sulfate, CaS04. It will be understood that the composition of Portland cement can be varied over a fairly wide range. However, the Portland cement contemplated for use in accordance with the invention will normally comprise about 75 of calcium silicates, 5-10E of calcium aluminates, 5% of Cay04, less than 1% of sodium or potassium oxides, 2-9% of MgO and 5-10% of calcium-aluminate-iron compounds, the foregoing percentages being by weight. Portland cement used in this invention can be a commercially available product, such as any commercial (hydraulic) cement. The Portland cements used in the invention generally 3 have a density of 50-55 lbs/ft 3. Therefore, "20-30 parts" by volume corresponds to about 3-5 lbs parts by weight. "Expanded perlite" as used herein will have a bulk density of 5-15 pounds per cubic foot and a particle size of 4-100 mesh (Tyler), (4-7 mm). Preferably, the perlite will have a density of 6-15 lb/ft and a particle size of 3,500-5,500 microns. Accordingly, "100-120 parts by volume" is equivalent to 20-25 ounces parts by weight of expanded perlite having a density of 5.15 pounds per cubic foot and to 25 ounces parts by weight of expanded perlite having a density of 8-9 lb/ft3. It will be appreciated that expanded perlites are products of the expansion and vesiculation of perlitic minerals, which are volcanic glasses among which are included perlite, vitrophore, pitchstone and some kinds of obsedian. The expanded perlite is obtained by crushing the mineral to a preselected particle size and heating the crushed materials at 1700-20000F to produce plastic mineral material, from which combined water is expelled, to yield a vesicular material of considerably greater volume than before expansion. "Hydrated lime" as used herein means CaO.H20. This material has a density of 29.4 lbs/ft3, so that 0.5-2 parts by volume are equivalent to 1 ounce parts by weight. "Diatomite" as used in the specification and claims means diatomaceous earth. This material is siliceous and consists of skeletons of diatoms or small marine animals. The material used in the practice of the invention will have a density of 8-10 pounds per cubic foot, corresponding to a particle size of 3,500-5,500 mesh. Therefore "0.1-1.0 part by volume" of diatomite corresponds to 2.5 grammes parts by weight. Preferably, the density of the diatomite used is 8.10 pounds per cubic foot and the particle size 3,500-5,500 mesh, which corresponds to 2.5 grammes parts by weight of diatomite. Preferably the sprayable compositions of the invention may be made by combining the dry ingredients and blending the selected amount of dry mix with the aqueous solution of water-soluble foaming agent. The mixing can conveniently be done with a rotating mechanical paddle in a drum or container rotating in the opposite direction. Mixing is continued until the product becomes pastelike in consistency, which generally requires 2-3 minutes. The sprayable mixture thus obtained can be sprayed from a screw pump-fed sprayer at an air pressure of 30-50 psi. An air pressure of 35-45 psi is preferred. Sprayers suitable for the compositions of the invention are available commercially, for example, "Muller R-Tex" Mono Pump using the largest size feed screw to ensure that the geodedic structure of the expanded perlite particles is not crushed whilst they are being fed to the gun nozzle. The diameter of the spray nozzle can be varied from 3/16 - 9/16 inch, but a nozzle diameter of 5/16 inch is generally acceptable. It will be understood that aeration of the composition occurs along with propulsion of the mixture onto a substrate or into a confined space in a static structure or building. The shelf-life of the pastel ire material obtained from the dry mix and the aqueous solution containing foaming agent is about 1 year, beyond which the material becomes too dense for spraying. It is therefore preferred that the material to be prepared at the site of use and applied within 1 hour of mixing. It is recommended that the nozzle of the spray gun be held 8-18 inches from the surface being covered. It will be understood that thick coating can be obtained by multiple applications of the sprayable compositions of this invention, preferably with an interval of ¸ - 2 hours between applications. Preferably, the dry mix of the invention consists essentially of 105-115 parts by volume of expanded perlite, 20-30 parts by volume of Portland cement, 0.5-1.5 parts by volume of hydrated lime and 0.25-0.75 parts by volume of diatomite. In making the sprayable compositions of the invention, the dry mix is preferably combined with an aqueous solution of water-soluble foaming agent at a level of 20-26 pounds of dry mix per gallon of solution. The preferred ratio is 20-21 pounds of dry mix per Imperial gallon of solution. The water-soluble foaming agent or air-entraining agent is of the anionic type, of which alkanol sulfates and alkyl or aryl sulfonates are exemplary. Alkanol sulfates include compounds of the formula ROSA3M, wherein R is straight or branched chain alkyl group of 8-30 carbon atoms and M is sodium or potassium. An exemplary compound is sodium lauryl sulfate. Alkyl and aryl sulfonates include sodium and potassium salts of sulfonic acids derived from alkanes, alkenes and aromatic hydrocarbons including alkylated aromatic hydrocarbons. Exemplary sulfonates are sodium/potassium hexadecyl sulfonate, benzyl sulfonate, phenyl sulfonate, naphthyl sulfonate and alkylarylsulfonates of the formula R-Ar-S03M in which R is alkyl of 3-35 carbon atoms, aryl is phenylene or naphthylene with R and S03M at any ring position and M is Na or K. Preferred foaming agents are of the R-Ar-S03M type, that is, alkylaryl sulfonates. Most preferred are sodium alkylbenzenesulfonates derived from alkylbenzenes of 8-12 carbon atoms in the alkyl chain, e.g. nonyphenylsulfonates or dodecylbenzenesulfonates. The amount of foaming agent is preferably 0.5-1.5 ounces per gallon of solution. When the mixture is to be sprayed on a surface, the preferred level is 0.5-1.0 ounce per gallon. If the mixture is to be sprayed into a confined area, e.g. between structural partitions, higher levels of 1.0-1.5 ounce per gallon are preferred. Compositions thus sprayed into cavities or onto surfaces will generally set up within e to 1 hour under ambient conditions (that is, become bonded to the inner surfaces of said cavities). Complete curing under ambient conditions requires 12-16 hours depending upon the composition of substrate surfaces, at which point the product is a rigid hard set material that is bonded and joined to any surface that it touches. After a further 20 hours, any attempt to remove the material will result in the destruction of the substrate. When thick coatings of the sprayable compositions of the invention are to be applied, addition of up to 2.5 parts by volume (5-10 grammes parts by weight) of bentonite decreases the tendency of the uncured composition to delaminate from the surface being coated. The bentonite is preferably added to the dry-mix component prior to combination with the aqueous solution of foaming agent. The ultimate strength of the cured composition of this invention can be improved by inclusion of up to 5 parts by volume of glass fibre or mineral wool in the dry mix. The fibres will generally be 1/4 - 1% inches in length, preferably 3/4 inches and have a density of 1 1/4 lbs/ft3. The mineral wool should be free from oils or grease and dry-faced. Contemplated equivalents of fibre glass and mineral wool are sawdust, wood chips and paper shavings, provided that their density is 2-5 pounds per cubic foot and particle size is 2,000-3,500 microns, preferably 2,500 microns. The most preferred compositions of this invention are those wherein the dry mix contains 105-115 parts by volume of expanded perlite, 20-30 parts by volume or Portland cement, 0.5-1.5 parts by volume of hydrated lime and 0.250.75 parts by volume of diatomite; the aqueous solution contains 0.5-1.5 ounce per gallon of alkylaryl sulfonate foaming agent; and the level of dry mix is 20-21 pounds per gallon of solution. Examples are given to illustrate the invention and are to be construed as merely illustrative and not limiting upon the scope of the invention. EXAMPLE 1 Dry mix was obtained by blending the following ingredients: Parts by Volume Parts by Weight Expanded Perlite Particles 109 20 ounces Portland Cement 24 56 ounces Diatomite 0.50 3-4 grammes Hydrated Lime 1 1 ounce The blend was stored in moisture proof bags prior to use. The dryamix, at time of use, was mixed by rotating mixing mechanical paddle in a drum container rotating in the opposite direction with an aqueous solution of 0.75 ounce per gallon of an air entraining agent (sodium alkylbenzenesulfonates). The amount of dry mix was 22 pounds and the amount of solution was 10 lbs. The composition was made by adding dry mix in portions to the solution and mixing until a paste the consistency of thick gruel was obtained. The resulting paste was fed to a screw fed pump and pressure fed to an air nozzle at a pressure of 40 psi at the point of ejection and mixing through an orifice of 5/16 inch diameter. The mixture was aerated and carried to the surface being covered, the spray gun being beld at a distance of from 8 to 18 inches from the surface. The sprayed covering set up within 1 hour and was completely cured overnight at ambient conditions. A coating produced as described above was applied to a structural steel member following and covering the steel contours to a 1 1/4 inch ( one and a quarter) thickness, to evaluate the insulating qualities of the coating as a protective membrane for structural steel fire protection. The structural steel member was a W10 x 46 section 30 inches -(3.762 m) long and was submitted to ASTM Designation E119-73 Standard Fire Test of Building and Construction Materials. The coating was subjected to fire exposure for 3 hours, and the maximum allowable individual thermocouple temperature was reached at 2 hours 52 minutes. After testing the coating was still adhering to the steel member. Further tests have shown that an increase of coating thickness will substantially increase the fire protection time given to structural steel, or any other area of fire hazard risk. EXAMPLE 2 A wet paste adapted for application to a confined space, such as a wall cavity or partition, was made as in Example 1, except that the level of sodium alkylbenzenesulfonates was 1.6 ounces per gallon. The same procedure was used as in Example 1, except that the nozzle of the spray apparatus was placed inside the cavity being filled and withdrawn gradually as the foamed material being applied was pushed back behind the nozzle. The material thus filling the cavity set up in %- 1 hour and reached a complete cure in 36 hours. The confined space was insulated and structurally strengthened. In addition, the composition acted as a fire barrier and prevented the space from acting as a flue or chimney for fire, flames or toxic smoke. EXAMPLE 3 A coating suitable for direct application by spraying without risk of the uncured composition delaminating from the coated surface is made by adding 2.25 parts by volume (5-10 grammes parts by weight) or bentonite to the dry mix of Example 1. In this way, a coating build-up of 2 inches can be achieved. The thus-applied coating will remain stable until cured. Bentonite suitable for this purpose can be acquired commercially. EXAMPLE 4 Compositions of Example 1 can include 0.5-4.0 parts by volume (.675-4.5 ounces parts by weight) of a fibrous filler, e.g., glass fibre averaging 3/4 inches in length and having a density of 3 pounds (1.28 kgs) per cubic foot. Cured compositions containing fibre glass are stronger than the compositions of Example 1. The preceding Examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding Examples. From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

Claims: CLAIMS: 1. A dry mix for mixing with water to produce an insulating composition curable at ambient temperature, which dry mix comprises expanded perlite, Portland cement, hydrated lime and diatomite. 2. A dry mix as claimed in claim 1 containing 100-120 parts by volume of expanded perlite, 20-30 parts by volume of Portland cement, 0.5 - 2.0 parts by volume of hydrated lime and 0.1 - 1.0 parts by volume of diatomite. 3. A dry mix as claimed in claim 2 containing 105-115 parts by volume of expanded perlite, 24-26 parts by volume of Portland cement, 0.5 - 1.5 parts by volume of hydrated lime and 0.25 - 0.75 parts by volume of diatomite. 4. A dry mix as claimed in any one of claims 1 to 3 also containing up to 2.5 parts by volume of bentonite. 5. A dry mix as claimed in any one of claims 1 to 3 also containing up to 5 parts by volume of glass fibre or mineral wool. 6. A sprayable insulating composition curable at ambient temperature and comprising a dry mix as claimed in any one of claims 1 to 5, or the ingredients thereof separately or in any combination, admixed with an aqueous solution of a water-soluble foaming agent, preferably containing 0.25 - 2 ounce per Imperial gallon of the agent and preferably 20-26 pounds of the dry mix being used per Imperial gallon of aqueous solution. 7. A composition as claimed in claim 6, wherein the aqueous solution contains 0.5 - 1.5 ounce per Imperial gallon of the water-soluble foaming agent. 8. A composition as claimed in claim 5 or claim 7, wherein the water-soluble foaming agent is an alkylaryl sulfonate. 9. A method of applying insulating material to an article, area or building structure which comprises spraying the article, area or building structure, at a pressure of 30-50 psi, with a composition as claimed in any one of claims 6 to 8. 10. A thermally insulated box comprising an insulating wall which has been formed by hardening or setting to a desired shape a composition comprising water and a dry mix as claimed in any one of claims 1 to 5 or the ingredients thereof.

Inventors: HACKER, DENNIS JON
Applicants: HEWHAND LIMITED
Application year: 1980
Main classification: C04B14
IPC codes: C04B28