HALO-ALKYL SUBSTITUTED HALOGENATED POLYNUCLEAR KETONE PHOTOINITIATORS, PHOTOPOLYMERIZABLE COMPOSITIONS CONTAINING THEM AND METHOD OF PRODUCING POLYMERIC COMPOSITIONS THEREFROM

Abstract: Compounds having the formula in which R₁ is -CH₂X, -CHX₂, or -CX₃; R₂ is H or R₁; X is C1, or Br or I; and Y is S, O, or carbonyl, are disclosed as well as their use as ultraviolet photo­ polymerization initiators in combination with unsaturated in monomers, e.g., acrylates.

Description: HALO-ALKYL SUBSTITUTED HALOGENATED POLYNUCLEAR KETONE PHOTOINITIATORS The present invention relates to halo-alkyl substituted halogenated polynuclear ketones which are initiators for the photopolymerization of unsaturated compounds, compositions comprising such initiators and photopolymerizable monomers, and the method of effecting polymerization of such compositions with ultraviolet light. The compounds of this invention have the formula EMI1.1 in which R1 is -CH2X, -CHX2 or CX3; R2 is H or R1 X is C1, Br or I; and Y is S, O or carbonyl. A wide variety of initiators suitable for the photopolymerization of unsaturated compounds are known. Among these are substituted polynuclear aromatic ketones.. Representative members of this class of photoinitiators are disclosed in U.S. patents 3,686,084, 3,827,957 and 4,043,887. U.S. patents 3,686,084 and 4,043,887 describe benzophenones substituted with one or more halo-alkyl groups and their use as photoinitiators. U.S. patent 3,827,957 describes polynuclear ketones containing a heterocyclic ring analogous of those of the compounds II of this invention. The polynuclear ketones of the foregoing patents can be substituted with a halo-alkyl group. The compounds of this invention distinguish over those of the patents in that they require two halo groups on one aromatic ring of the polynuclear ketone and at least one halo-methyl group on the other aromatic nucleus; It is recognized that photoinitiators must be capable of promoting catalysis of an addition polymerization reaction at a reasonably rapid rate. In certain applications it is also desirable, and sometimes necessary, that the photoinitiator not be highly colored and that it be resistant to conversion to highly colored products. It is particularly advantageous that a photoinitiator be stable to heat discoloration in applications in which the polymer coating is subsequently subjected to a heat treatment. The polynuclear ketone compounds of this invention are capable of polymerizing a wide variety of unsaturated compounds under the influence of ultraviolet light at a rapid rate and exhibit minimal discoloration upon heating. In general, the photoinitiators are used in amounts from 0.1 to 10% by weight, preferably from 0.5 to 3% by weight, based on the weight of unsaturated compounds. The radiation which is most effective for initiating polymerization with the compounds of this invention are wave lengths from 2,500 to 4,000A. Suitable light sources include sunlight and mercury, tungsten and xenon lamps as well as certain fluorescent lamps. Unsaturated compounds which can be photopolymerized with the initiators of this invention are, for example, acrylic and methacrylic acid, their esters, vinyl esters, vinyl halides, vinyl ketones, vinyl ethers, vinyl cyanides, vinylidene halides and styrene. Also suitable are mixtures of different monomers and mixtures thereof with unsaturated polyesters. Additionally, the unsaturated compounds can comprise materials such as those containing epoxy-modified unsaturated monomers. Such compositions are described in U.S. patents 4,064,026 and 4,125,503. The photopolymerization reaction can be carried out in solution, in an emulsion, or preferably in the absence of solvents other than the unsaturated materials themselves. Thus, the compositions of this invention comprising the novel photoinitiators and unsaturated compounds are advantageously used as coatings on various substrates such as wood, metal, synthetic materials and textiles. It is sometimes desirable, particularly in coating applications, to conduct the initial polymerization or curing with ultraviolet light and then to bake the polymer for a period of time. - Generally, a coating is baked at a temperature of 1000C or higher for a period of two minutes or more. Typical conditions for baking are heating at a temperature of 175 C-225 C for 5-15 minutes. The photoinitiator compounds of this invention can be prepared by known techniques. A convenient method of preparation involves the halogenation of compounds corresponding to those in formulas I and II above, where R1 is methyl. Generally, halogenation results in a mixture of products including the monohalomethyl, the dihalomethyl and the trihalomethyl. Such mixtures are entirely suitable as photoinitiators in this invention even if they contain a small amount of the unhalogenated starting material. The invention is illustrated by the following nonlimiting examples. EXAMPLE 1 Preparation of 2, 5-dichloro-4 '-chloromethyl benzophenone To a three-neck round bottom flask equipped with stirrer, condenser, thermometer and addition funnel is added 50 ml of CH2C12 and 27 9 All3. The mixture is cooled to 410 C and 2,5-dichlorobenzoyl chloride is added dropwise at 120C. After addition is complete, 20 g toluene (10% excess) is added dropwise at 120C. Evolution of HC1 off gas commences almost immediately. After addition is complete reaction mixture is stirred and allowed to warm to 250C. When the reaction is complete, as evidenced by the disappearance of acid chloride, material is worked up in the usual way. Recrystallization of the crude product from 95% ethanol gives 38.8 g (73% yield based on acid chloride) of tannish crystals, m.p. 99-1010C. The 2,5-dichloro-4'-methyl-benzophenone was chlorinated at 97-1020C with chlorine gas to give 2% 2,5-dichloro4'-methyl, 52% 2,5-dichloro-4'-chloromethyl, 29% 2,5-dichloro-4'-dichloromethyl and 19% 2,5-dichloro-4'-trichloromethylbenzophenone mixture, which is referred to as 2,5-dichloro-4'- x chloromethylbenzophenone. EXAMPLE 2 Preparation and photopolymerization of photopolymerizable compositions Three photopolymerizable compositions were prepared in which each of the photoinitiators 2,5-dichloro-4'-x chloromethylbenzophenone, 4-dichloromethylbenzophenone and 3,4-bis(chloromethyl) benzophenone, were added at the 5% by weight level to a coating composition. The coating composition comprised a mixture of polyepoxide ether polyacrylate (about 20% by weight), hydroxy alkyl acrylate-monoanhydride adduct (about 70% by weight) as disclosed in U.S. Patent No. 4,064,026, the triacrylate derivative of trimethyol propane (TMPTA) (5% by weight) and about 0.5% by weight of a slip agent. These compositions were each coated on a white panel at 3 mg per square inch, ultra-violet cured in air and then postbaked at 2050C for ten minutes. The samples were analyzed on a Hunter Lab Colorimeter. The results are reported in Table 1 in which "L" is whiteness, "a" is a measure of the amount of red or green and "b" is a measure of the amount of blue or yellow (a high positive value is yellow). TABLE 1 Hunter Lab Colorimeter Values Material L a b 2,5-Dichloro-4'x chloromethyl- 82.79 -2.27 +0.36 benzophenone 3,4-bis(chloromethyl) 82.03 -2.47 +2.43 benzophenone 4-dichloromethylbenzophenone 82.82 -2.68 +2.47 Benzophenone/amine 81.46 -2.53 +3.72 Blank 84.04 -1.46 -2.84

Claims: CLAIMS: 1. A compound having the formula EMI7.1 in which R1 is -CH2X, -CHX2 or CX3; R2 is H or R1; X is C1, Br or I; and Y is S, 0, carbonyl. 2. A compound having the formula EMI7.2 in which R1 is -CH2S, -CHX2 or CX3; R2 is H or R1; X is Cl, Br or I; and Y is S, 0, or carbonyl. 3. The compound of Claim 1 having the formula II. 4. A compound of Claim 2 or 3 in which X is C1. 5. A compound of Claim 4 in which X is C1 and R2 is H. 6. A photopolymerizable composition comprising a photopolymerizable unsaturated compound and an effective amount of photopolymerization initiator as claimed in any of Claims 1 to 5. 7. A composition of Claim 6 in which the photopolymerization initiator comprises 0.1% to 10% by weight based on the photopolymerizable unsaturated compound. 8. The composition of Claim 7 in which said photopolymerizable unsaturated compound comprises arcylic acid, arcylic acid ester, methacrylic acid, methacrylic acid ester. 9. A method of producing a polymeric composition which comprises exposing the composition of Claims 6, 7 or 8 to ultraviolet light for a period of time sufficient to effect polymerization. 10. The method of Claim 9 in which polymeric composition is subjected to baking at a temperature of 1000C or higher for a period of two minutes or more.

Inventors: ZARNEGAR, BIZHAN MOHAMMED
Applicants: MOBIL OIL CORPORATION
Application year: 1980
Main classification: C08F2
IPC codes: C07D335, C08F2, C07D311, C07C45, C07C67, C07C49