WIRE WITH RAPIDLY QUENCHED STRUCTURE

Abstract: A wire of a normally nonforgeable composition, having improved resistance to fracture during working, handling and use is comprised of a portion with a rapidly quenched structure as a continuous stratum along its length. A preferred wire useful for fusion welding has a circular cross section with a micro-crystalline surface portion of at least 30 volume percent of the wire. Other preferred wires have elliptical or rectangular cross sections with amorphous strata continuous along their lengths.

Description: WIRE WITH RAPIDLY QUENCHED STRUCTURE BACKGROUND OF THE INVENTION 1. This invention relates to wire products, more particularly bendable wires of normally unmalleable alloys suited for uses such as weld filler metals. 5 2. The fabrication of wire of metal alloys which are readily forged or drawn is easily undertaken. How¬ ever, a considerable number of alloys can be readily cast but their metallurgical structure is such that they cannot be formed into wires by conventional cold or hot 10 working processes. It is with these types of alloys that the present invention is particularly useful. Among these alloys are high temperature cobalt and nickel base superalloys, including those used for structural and hardfacing applications. To accomplish most types of 15 welding it is desired to have filler metals in rod or wire form, and it is within this applied context that the invention is described in detail. Nonforgeable welding alloys can presently be made into suitable wires by either casting or powder metal 20 processes. In the former, wires are typically formed by centrifugally casting small rods; the mininu diam¬ eters and the maximum length-to-diameter ratios are limited according to known factors relating to cast- ability. Alternatively, the alloys can be converted 25 into a powder, as by atomization, and then pressed or extruded into wires of the desired diameter; however, these processes can be costly and small diameters are O PI IPO - 2 - difficult to obtain. In both the foregoing instances, the rod or wire will still have the unyielding charac¬ ter of the cast alloy. And the minimum diameters that are formable from most alloys using these techniques 5 are greater than those often desired for welding small workpieces. The diameter of oversize wires can be reduced by centerless grinding, for example, but such an operation is costly and results in the loss of valuable welding wire alloy. 10 Generally, even with inefficiency, most cast alloys cannot readily be made into wires of less than 1 mm diameter, and when they are made at diameters near the minimum, they tend to be rather fragile and prone to breakage during handling, if dropped or bent. Because 15 of these constraints, small diameter wires usually come in relatively short lengths of about 20-40 cm. There¬ fore, they are not suited for continuous welding pro¬ cesses such as GMA (Gas Metal Arc) , but must be used in hand-fed GTA (Gas Tungsten Arc) processes instead, 20 with attendant inefficiency in production and weld wire consumption. Thus, there is a need for an improved small diameter weld filler metal wire which has sufficient malleability to endure the moderate bending that is characteristically 25 imposed by automatic welding wire feeders. The improved wire will not be prone to undue breakage during normal handling or welding operations. O FI In our previously filed application Serial No. entitled "Interlayers With Amorphous Structure For Brazing And Diffusion Bonding" we describe metal foils wherein a portion of the interlayer has an amorphous 5 structure which imparts ductility to normally brittle alloys which melt during brazing and bonding processes. SUMMARY OF THE INVENTION An object of the invention is to provide an im¬ proved cast metal weld filler metal wire which is mal- 10 leable. A further object is to economically provide small diameter wires of normally nonforgeable alloys. A still further object is to provide cast wires which can be drawn to smaller diameters. In accord with the invention, a wire has at least 15 a portion of its cross section as a continuous stratum with a rapidly quenched metallurgical structure. The rapidly quenched structure, which may be either micro- crystalline or amorphous, is relatively ductile and thereby imparts plastic structural deformability to the 20 otherwise relatively unmalleable wire. When the wire is less than fully rapidly quenched, such portions as are of a conventional crystalline atomic structure and are prone to fracture during bending of the wire are supported and functionally held intact by the rapidly 25 quenched stratum to which they are integrally attached. The wire may be of virtually any cross section, but a preferred embodiment for welding is a generally circular cross section. In a circular cross section welding wire of the preferred embodiment, the rapidly quenched stratu may be a continuous layer around the circumference. Welding wires in accord with the invention may be made 5 by rapidly solidifying liquid metals, laser surface melting of the surface of a previously cast wire, and any other means which achieve rapid quenching from the liquid of a portion of the wire. Features and advantages of the invention include: 10 making feasible the use of automatic filler metal wire feeding, reducing loss of wire due to breakage from handling, making available smaller diameter wires re¬ quiring less heat input to small workpieces, and more efficiently utilizing costly raw materials. Better 15 control of parameters and joint properties are attained with automatic welding operation which is permitted with malleable wires. Also, articles having welded areas, particularly those containing localized areas of hardfacing materials, may be more readily fabricated 20 with less deleterious effects on the substrate and less machining after welding when smaller diameter wire is available. The foregoing and other objects, features and advantages of the present invention will become more 25 apparent from the following description of preferred embodiments and accompanying drawings. OMPI /., WIPO BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a partially rapidly quenched structure wire with a circular cross section. Fig. 2 shows a rectangular cross section wire. 5 " DESCRIPTION OF THE PREFERRED EMBODIMENT The invention is described in terms of fabricating a cobalt base superalloy hardfacing wire, such as is suitable for use on gas turbine superalloy airfoils. But, as will be evident from the description, the in- 10 vention is equally applicable to other materials. PWA-694 is a commercial hardfacing alloy having the following composition: 28% chromium, 19.5% tungsten, 0.85% carbon, 5% nickel, 1% vanadium, balance cobalt, all by weight. Normally, this wire is centrifugally 15 cast into nominal 6 mm diameter rods, 30-40 cm in length. Presently, for particular applications, it is" centerless ground to a wire of about 1.5 mm, whereafter, in one application, the wire is used with the GTA process to apply a wear resistant layer of about 1.5-2.5 mm thick 20 on a substrate, such as the nickel superalloy B-1900. PWA-694 is an alloy which lacks forgeability. In this patent specification, by lack of forgeability it is meant that an alloy in its cast form lacks sufficient malleability to be shaped by application of pressure 25 and temperature, such as are used in conventional open and closed die forging and wire drawing. OMPI - 6 - According to the invention, improved weld filler metal wire is a filament having a portion with rapidly quenched structure. Methods of making continuous fila¬ ments from liquid metal are disclosed in the technical 5 literature and in various U.S. patents. Generally, these methods involve contacting or withdrawing a thin stream of metal from a melt with a cool surface or media on a continuous basis. The techniques for making fila¬ ments with partial or wholly rapidly quenched structures 10 are described and referred to in our copending applica¬ tion Serial No. , which is hereby incorporated by reference. As described in more detail below, the rapidly quenched portion of the wire must have certain metal- 15 lurgical characteristics to enable practice of the invention. Generally, these characteristics are those which impart ductility to the metal, compared to the characteristics it has when conventionally quenched. Because of the requisite high cooling rates, ' 20 currently manufactured filaments with totally rapidly quenched structure tend to be relatively small, typically having one dimension on the order of 0.15 mm or less. Wires of such small dimension are not preferred for most applications, e.g., a 0.8 mm or greater diameter being 25 preferred in the practice of the invention. In many alloys, we believe that attainable cooling rates may be insufficient in the center of the wire to convert •gfRE QM ► WIIPP that portion into a rapidly quenched structure, but that at least the surface may be rapidly quenched according to one or more of the known techniques referred to herein. A preferred embodiment of a weld filler metal wire 5 of the present invention is shown in Fig. 1. A stratum of rapidly quenched structure material 10 surrounds a core of conventionally quenched material 12. Since the rapidly quenched material will exhibit significant ducti¬ lity upon deformation beyond its elastic limit, in con- 10 trast to the conventionally quenched material 12 which will exhibit cracking, the rapidly quenched stratum pro¬ vides support to the wire and will maintain it as a single piece during bending. Of course, Fig. 1 shows a uniform stratum around the wire circumference but lesser 15 degrees of uniformity will be acceptable, so long as one stratum is continuous along the length. Another embodiment of the invention is shown in Fig. 2 wherein the filament has a generally rectangular cross section characterized by rapidly quenched stratum 20 10a integrally attached to a length-continuous conven¬ tionally quenched stratum 12a. A wire as shown in Fig. 2 would result when a filament was subjected to rapid cooling from only one of its surfaces, namely, that at which the rapidly quenched structure 10a is present. 5 Of course, the filament of Fig. 2 will exhibit different structural limits of deformation, depending on the axis about which it is deformed. The circular cross section OMPI - 8 - wire shown in Fig. 1 will have structural properties primarily provided by the rapidly quenched stratum, since this portion is most favorably disposed to contri¬ bute to the section modulus during bending. Other cross- 5 sectional embodiments, both regular and irregular will be within the contemplation of the invention, but for welding generally, regular cross sections are preferred. An ellipsoid is an example of another useful cross sectio As will be evident from the description herein, wires of 10 the invention will be beπdable. Thus, wires may be formed to a first dimension, and with the integrity provided by the rapidly quenched layer, may thereafter be swaged or drawn down to a smaller second diameter in some instances. To practice the invention while welding, for example, 15 it is only required that the filler metal wire have a rapidly quenched stratum of sufficient thickness to pro¬ vide structural support to the wire when it is deformed to a degree that causes cracking in the conventionally quenched material. We have not run experiments to εva- 20 luate the limits of the relative ratios between the con¬ ventionally quenched portion and the rapidly quenched portion and, of course, the limit will be dependent on the degree and direction of deformation which is anti¬ cipated. For a wire which is usable in normal GTA welding 25 operations, where the limiting factor is the normal handling of the material, we believe that a rapidly quenched layer which comprises as little as 10 percent of the volume of the wire could be suited to practice the invention. Naturally, a greater percentages of rapidly quenched material would be even better. For applications where the wire is fed by a machine, as by 5 rollers and the like, a higher volume fraction is prob¬ ably desirable; we estimate that 20-30 volume percent or greater will be satisfactory. The structure which results when a metal is quenched depends on the metal composition and the cooling rate to 10 which it is subjected; determining this is largely a matter of experiment. In the discussion herein, quenching is divided into that characterized as conventional and that characterized as rapid. Normal casting practice for forming ingots and 15 articles entails such cooling that it is largely irrel¬ evant here. Conventional quenching, as used herein, refers to cooling rates which are characteristic of welding joints and casting small (6 mm) diameter wires. These rates are of the order of 10 C per sec. or less. 20 When such cooling rates are applied to an alloy such as PWA-6 4, the microstructure will be characterized by segregation and further may contain casting imperfections such as porosity. These substantially degrade the ductility, and hence, the handling characteristics of 25 the wire. The cooling rate is slow enough to permit the segregation of the carbide phases. Similar segregation will be observed in other alloys strengthened by other - 10 - phases. Conventionally quenched alloy grain sizes will characteristically be of the order of 60-80 microns or greater. It is the combination of the grain size and the segregated hardening phase which imparts the lack 5 of malleability and forgeability to the cast material. Rapid quenching comprises cooling a metal at rates beyond those commonly encountered. Rapid quenching, as used herein, is that quenching which achieves either a microcrystalline or amorphous structure in a metal. 10 When metal alloys are rapidly quenched, the exact struc¬ ture produced depends on the alloy composition and the cooling rate. For example, to obtain amorphous struc¬ tures, that is, those characterized by a lack of long range atomic ordering, it is necessary to cool a metal 15 at a rate sufficient to preserve the metastable struc¬ ture characteristic of a liquid. For example, to obtain amorphous structures, it is necessary to cool elemental 13 metals at rates greater than about 10 °C per sec. , to cool precipitation strengthened superalloys at rates 20 greater than about 10°°C per sec, and to cool certain favorably composed eutectic alloys at rates greater than about 10 C per sec. When metal alloys are rapidly quenched at rates between those characteristic of conventional quenching 25 and those which produce amorphous structures, fine micro crystalline structures result. Fine microcrystalline structures, as used herein, are those which have average OM /,- WIP grain sizes of the order of ten micrometers or less and in which the hardening phases, such as carbides, are well dispersed and of the order of one tenth of a micrometer. The phases are very fine and well dispersed because the 5 rapid cooling rate does not allow time for segregation to occur as it does in conventionally quenched metals. Thus, the rapidly quenched microcrystalline structure will impart improved ductility compared to that observed in the conventionally quenched metal. (Naturally, the 10 grains in quenched metals will often be columnar, and in that respect, the grain and phase sizes recited herein will be understood to be nominal, but nonetheless signi¬ ficant by their contrast.) Both the amorphous structures and the microcrystalline 15 structures will be characterized by chemical homogeneity and lack of large segregated phases. The differences will be in the ordering of the crystalline structure. Gene¬ rally, the amorphous structure will always be character¬ ized by improved ductility compared to the crystalline 20 state. To achieve ductility in certain inherently brittle materials, e.g., a high metalloid content metal such as AMS 4775 (nominally, by weight percent, 16.5 Cr, 4 Si, 4 Fe, 3.8 B, balance Ni), it is necessary that quenching be sufficiently rapid to achieve the amorphous 25 state. However, in other materials, such as precipitation hardened PWA-694, it is not necessary to achieve the amorphous state to attain ductility. Quenching at a OMPI_ " WIPO- < - 12 - sufficiently rapid rate to decrease grain size to the aforementioned microcrystalline range and suppress the normal tendency to carbide segregation will produce a sufficiently ductile stratum to which comprises a wire 5 within the object of the invention. Referring now again to the specific use of improved filler metal wire for welding, a usable wire will most often have a composition such that its melting point is approximately that of the workpieces. This is charac- 10 teristic of fusion-welding wire. Of course, wire used for hardfacing or other purposes may have a lower melting point than the workpieces, but it will still be adapted to melt in contact with, and metallurgically alloy with, the workpieces. When the wire is placed in proximity to 15 the workpieces and they and the workpieces are locally - heated, melting and fusion take place. On removal of the heat, the liquid metal solidifies by heat extraction into the workpieces and heat loss from the weld region surface to the environment. A crystalline atomic ' struc- 20 ture weld zone results. The weld filler metal wire of the invention will be usable in other welding processes besides the GTA and GMA processes mentioned above. Included, but not limitin are processes such as electroslag welding, gas welding, 25 and the like. The weld filler metal wire of the inven¬ tion would also be suitable for other processes where metal is provided in wire. form to be melted and applied O PI WIPO to a substrate, as for example is carried out in spray metallizing. As indicated, the invention is applicable to all types of wire for which there is a need for improved 5 ductility for handling and working. Included in this scope are iron and nickel base alloys hardened by carbide and boride compounds, as well as inherently unforgeable cast alloys of other base metals, where rapid quenching alters the structure to eliminate the deleterious phases 10 caused by conventional quenching. Although this invention has been shown and described with respect to a preferred embodiment, it will be under¬ stood by those skilled in this art that various changes in form and detail thereof may be made without departing 15 from the spirit and scope of the claimed invention.

Claims: - 14 - Claims 1. The method of improving the for ability and workability of wire and reducing fracture during working, handling, and use, which comprises providing a surface portion of the wire as a rapidly quenched structure as 5 a stratum continuous along the length of the wire. 2. The method of claim 1 where the rapidly quenched structure is a microcrystalline structure with relatively uniform grain size and microcomposition. 3. The method of claim 1 where the rapidly 10 quenched structure is an amorphous structure. 4. A filler metal wire for welding a metal work- piece, wherein the wire is of a composition which lacks- malleability and forgeability when in cast form, com¬ prising a surface portion having a rapidly quenched 15 structure, said portion being at least 10 percent by volume of the wire and being present as at least one continuous stratum along the length of the wire, and a remainder portion, integrally attached to the surface portion, having a conventionally quenched structure. 20 5. The wire of claim 2 wherein the wire is circula in cross section and has a surface portion which is a con tinuous stratum about the outer circumference of the cros section and along the length, and wherein the remainder portion is in the center of the wire. 6. A filler metal wire for welding a metal work- piece, having a composition characterized by a lack of forgeability and malleability when in cast form, a melting point substantially the same as the workpiece, a capability of alloying with the workpiece during welding, and a portion having a rapidly quenched struc¬ ture, the portion being present as a continuous stratum along the length of the wire. 7. The wires of claims 4 or 6 wherein the rapidly 10 quenched structure is a microcrystalline structure with relatively uniform grain size and microcomposition. 8. The wires of claims 4 or 6 wherein the rapidly quenched structure is an amorphous structure and the con¬ ventionally quenched structure is a crystalline structure. - IEXCT O PI /., WIPO

Inventors: KEAR B, KING W
Applicants: UNITED TECHNOLOGIES CORP, UNITED TECHN CORP
Application year: 1980
Main classification: B22D11
IPC codes: B22D11, B23K35, C22C45