PROCESS FOR PREPARING LIQUID POLYISOCYANATE COMPOSITIONS, AND THEIR USE

Abstract: A method for the preparation of a liquid polyisocyana­ te composition which comprises reacting one molar pro­ portion of diphenylmethane diisocyanate containing at least 15% by weight of the 2,4′-isomer with from 0.01 to 0.8 mo­ lar proportions of a monohydric alcohol of the formula: A - OH wherein A represents an alkyl radical containing from 9 to 16 carbon atoms or a radical of the formula: wherein R represents an alkyl group containing from 1 to 12 carbon atoms, R¹ represents hydrogen or an alkyl group containing from 1 to 3 carbon atoms and x is an integer of from 1 to 58, the reaction being performed at a temperatu­ re of from 100 to 250°C and in the presence of a catalyst for the NCO/OH reaction. The liquid diisocyanate compositions are useful in the manufacture of polyurethanes, especially elastomers and flexible foams.

Description: TITLE LIQUID POLYISOCYANATE COMPOSITIONS This invention relates to liquid polyisocyanate compositions and in particular to compositions containing diphenylmethane diisocyanate and to the use of such compositions in the manufacture of polyurethanes. It is well known to manufacture polyurethanes, of a celluiar or non-cellular nature, by reacting an organic polyisocyanate with an organic polyol in the presence of additives of various kinds. Many organic polyisocyanates have been proposed for use in making polyurethanes but, since many polyurethane mazuiacturing processes involve the rapid mixing of materials at room temperature, it is preferred to use polyisocyanates that are liquid at room temperature and that remain in the liquid state without significant deposition of soli.d materials even when stored at relatively low temperatures such as may be encountered in winter. One of the polyisocyanates which has been used commercially in the manufacture of polyuret nes is diphenylmethane diisocyanate which is generally available either in a substantially pure form or in admixture with related polymethylene polyphenyl polyisocyanates of higher functionality such as may be represented by the general formula: EMI2.1 wherein n has an average value of one or more. The latter mixtures are commonly referred to in the trade as "crude MDI" and are made by the phosgenation of a mixture of polyamines obtained by the acid condensation of aniline and formaldehyde. The manufacture of both the polyamine mixtures and the polyisocyanate mixtures is well known. The condensation of aniline with formaldehyde in the presence of strong acids such as hydrochloric acid gives a reaction product containing diaminodiphenylmethane together with polymethylene polyphenyl polyamines of higher functionality, the precise composition depending in known manner on the aniline/formaldehyde ratio. The polyisocyanates are made by phosgenation of the polyamine mixtures and the various proportions of diamines, triamines and higher polwamines give rise to related proportions of di isocyanates, triisocyanates and higher polyisocyanates. I?lo diisocyanates can be isolated from this mixture by distillation, being recovered as an isomer mixture in which the predominant component is 4,4'-diphenylmethane diisocyanate, there being smaller amounts of the 2,4'- and 2,2 1-isomers. A substantially pure form of the 4,4'-isomer can be recovered from this isomer mixture by crystallisation leaving a mother liquor which can vary in composition depending upon the operating conditions but which typically might contain about 83% of the 4,4'-isomer and about 20% of the 2,4'isomer with traces of the 2,2'-isomer. The present invention is particularly concerned with diphenylmethane diisocyanate containing at least 15% by weight, based on he total diisocyanate, of the 2s4'-isomer. Both the 4,4'- and 2,4' -isomers are solids at room temperature, having melting points of 420C and 360C respectively and many of the isomer mixtures'are solid at room temperature or under the lower temperatures which can obtain during winter storage or transportation. For polyurethane manufacture, it is necessary to melt any solid material and maintain it in a molten condition. The present invention provides liquid polyisocym1ate compositions which are stable to storage at low temperatures and which provide polyurethanes having excellent properties. Thus, according to the invention, there is provided a method br the preparation of a liquid polyisocyanate composition which comprises reacting one molar proportion of diphenylmethale diisocyanate containing at least 15% by weight of the 2,4'-isomer with from 0.01 to 0.8 molar proportions of a monohydric alcohol of the formula: A - OH wherein A represents an alkyl radical containing from 9 to 16 carbon atolls or a radical of the formula: : EMI4.1 wherein R represents an alkyl group containing from 1 to 12 carbon atoms, R1 represents hydrogen or an alkyl group containing from 1 to 3 carbon atoms aAd x-is an integer of from 1 to 58, the reaction being performed at a temperature of from 100 to 250 OC and in the presence of a catalyst for the NCO/OH reaction. Preferably, the diphenylmethane dilsocyanate used as starting material contains the 4,4' isomer in addition to containing at least 15% by weight of the 2,4'-isomer. When the monohydric alcohol is one in which A is an alkyl radical having 9 to 16 carbon atoms, it may be linear or branched but the latter is preferred. Alcohols having from 10 to 14 carbon atoms are especially suitable. A mixture of alcohols may be employed and in fact many of the alcohols are most readily available as isomer mixtures. W & en the monohydric alcohol is a monoalkoxy glycol, R is preferably an alkyl group containing from 1 to 5 carbon atoms for example methyl or ethyl. R1 is preferably hydrogen or methyl, the material then being a monoalkoxy (poly)ethylene or (poly)propylene glycol. The formula includes copolymeric monoalkoxy polyalkylene glycol, for example copolymers derived from ethylene and propylene oxides. The integer n is preferably less than 44. Mixtures of monoalkoxy glycols may be used. Under the conditions specified for the performance of the method of the inventIon, the ureth & e formed by the reaction of the monohydric alcohol with the diphenylmethane diisocyanate reacts with further isocyanate to form an allophanate. It will be appreciated,however, that the reaction product may contain a minor proportion of material that has not reacted beyond the urethane stage as well as higher functionality material where the reaction has gone beyond the allophanate stage. Particularly useful products are obtained when one molar proportion of the diphenylmethane diisocyanate is reacted with from 0.1 to 0.3 molar proportions of the monohydric alcohol. The reaction between the diphenylmcthane diisocyanate and the monohydric alcohol is preferably performed at a temperature in the range 100 to 200 C and is continued until a product of the desired constitution is obtained. The reaction catalyst may be any catalyst known for the reaction between isocyanate and hydroxyl groups. Particularly suitable catalysts are tin and dialkyl tin salts of carboxylic acids,for example stannous octoate and dibutyl tin dilaurate. Other suitable catalysts are tertiary amines in which the nitrogen atom is not directly attached to an aromatic residue, for example 1, 4-diazabicycloE2.2.2]octane. The monohydric alcohol is conveniently added slowly to the polyisocyanate and catalyst at the reaction temperature,but the reactants may alternatively be brought together at ambient temperature or at an intermediate temperature and then heated to the reaction temperature. After the reaction is complete, it is preferable to deactivate the catalyst either chemically, for example by incorporating an acidic substance, or physically, for example by adsorption on to activated carbon. It is also possible in some cases to remove the catalyst by filtration or distillation. The polyisocyanate compositions of the present invention are liquid compositions which are stable to storage, that is to say the compositions remain liquid at room temperature for long periods of time, sufficient in fact for all practical purposes, and can be transported or stored at low temperature without significant sedimentation of crystals of diphenylmethane diisocyanate. The compositions are suitable for use in the manufacture of polyurethanes using techniques fully described in the prior art. Being substantially difunctional, the compositions are particularly suitable for the manufacture of polyurethane elastomers and flexible foams including microcellular elastomers. The flexible foams obtained have improved tensile properties axd improved curing properties compared with foams obtained from corresponding diphenylmethane diisocyaaates which have not been modified by reaction with a monohydric alcohol. The invention is illustrated by the following Examples in which all parts and percentages are by weight. Example 1 To 4000 parts of an isomeric mixture of diphenylmethane diisocyanates, containing approximately 8CPó 4,4'-, 20 2,4'-, and 1% 2,2'-isomcrs, were added 9.6 parts of dibutyl tin dilaufate. The mixture was heated to 1200C, stirring under a blanket of nitrogen, and 653 parts of monomethoxy polyethylene glycol of molecular weight 213 were added slowly maintaining the temperature at 1200C. The reaction mixture was heated for a further 2 hours at 1200C and was then cooled to ambient temperature. 2.4 parts of salicylic acid were added during the cooling period. The product, a stable,brown, low viscosity liquid had an isocyanat content of 23.Wó, and remained liquid for up to one month at OOC. The product was blended with starting material to yield an isocyanate value of 30% and a flexible foam moulding prepared using the following formulation and the conventional moulding methods of the art. Parts by weight Oxypropylated glycerol, 15% ethylene 100 oxide tip 5250 molecular weight Water 2.6 Dabco 33LV (Air Products & Chem.) 0.8 Niax Catalyst Al (Union Carbide) 0.2 Silicone B4113 (Union Carbide) 1.0 Refrigerant 11 10.0 Crude MDI 14.0 Blended product as above (30% NCO value) 37.8 The foam moulding had the following physical properties. Density 44 kg.m Tensile strength 135 KNm2 Elongation 150% Tear strength 315 Nm Indentation Hardness 25% 74 N 200mum 1 40% 119 N 200mum 1 65% 252 N 200mum 1 Resilience 40% The crude MDI used in the formulation had an NCO content of 30% and contained approximately 50% of diphenylmethane diisocyanates, the remainder being polymethylene polyphenyl polyisocyanates of higher functionality. Example 2 To 1000 parts of the isomeric mixture of diphenylmethane diisocyanates used in Example 1 were added 2.4 parts of dibutyl tin dilaurate. The mixture was heated to 120or, stirring under nitrogen and 160 parts of tridecanol (a C13 hydrocarbon based alcohol) were added slowly maintaining the temperature at 1200C. The reaction mixture was then heated to 2000C and held at that temperature for 2 hours; 0.52 parts of salicylic acid were added and the reaction mixture was crash cooled to ambient temperature. The product was a red/brown low viscosity liquid of NCO value 22.5%, which remained liquid for several weeks at 0 C. example 3 To 500 parts of the isomeric mixture of diphenylmethane diisocyanates used in Example 1 was added 1 part dibutyl tin dilaurate. The mixture was heated with stirring under dry nitrogen to 1200C at which point 40 parts of methyl cellosolve were added slowly, maintaining the temperature at 12000* The mixture was heated for a further 2 hours at 1200C, when 0.24 parts of salicylic acid were added, and then crash cooled. The product obtained was a yellow/brown liquid with an NCO content of 23.0%. The product was blended with a proportion of the starting isocyanate to yield an isocyanate value of 30% and a flexible foam moulding was prepared using the conventional methods known in the art and the following formulation: Parts by weight Oxzpropylated glycerol with 15% 100 ethylene oxide tip 5250 molecular weight Water 2.6 Dabco 33LV 0.8 Niax catalyst Al 0.2 Silicone B4113 1.0 Refrigerant 11 10.0 Crude MDI 14.0 Isocyanate product (NCO value 30$) 37.8 The foam moulding had the following physical properties. Density 42 kg m-3 Tensile strength 120 kN m 2 Elongation 155% Tear strength 345 Nm-1 Indentation hardness 25X 55 N 200mm-1 40% 97 N 200mm-1 65% 261 N 200mm Resilience 38% Example 4 1000 parts of 2s4'-diisocyanaro diphenylmethane were heated with stirring under a blanket of dry nitrogen to 800C and 4 parts of dibutyl tin dilaurate were added. The temperature was increased to 1200C and 80 parts of methyl Cellosolve were added slowly. The mixture was heated at 1200C for a further 4l hours and allowed to cool with the addition of 1 part of salicylic acid at a temperature of approximately 80 C. The product was a clear brows liquid with an isocyanate content of 23.6%. The product remained liquid after several weeks storage at OOC. Example 5 To 4000 parts of an isomeric mixture of diphenylmethane diisocyanate, containing approximately 18% 2,4'-, 82% 4,4'- and 1% 2,2'-isomers, were added 9.6 parts of dibutyl tin dilaurate. The mixture was heated to 1200C under dry nitrogen with stirring and 960 tarts of monomethoxy polypropylene glycol of molecular weight 406 were added slowly, maintaining the temperature at 1200C. The reaction mixture was heated for a further 2 hours at 1200C and allowed to cool to ambient temperature with the addition of 2.4 parts of salicylic acid at approximately 800C. The product was a red/brown clear liquid of low viscosity with an isocyanate content of 23.3% and excellent low temperature stability. The product was blended with starting material to yield a final isocyanate value of 27.7% and a flexible foam moulding was prepared using the following formulation. Parts by weight Oxypropylated glycerol 15% ethylene 100 oxide tip, 5250 molecular weight Water 2.6 Dabco 33LV 0.8 Niax catalyst Al 0.2 Silicone B4113 1.0 Refrigerant 11 10.0 Crude MDI 14.9 Isocyanate blend (NCO value 2?.?%) 40 The physical properties of the moulding were as follows: Density 44 kg m Tensile strength 110 KN m-2 Elongation 150% Tear strength 150 N m 1 Indentat ion hardness 25% 66 N 200mm-1 40% 105 N 200mm-1 65% 294 N 200mm-1 Resilience 37%

Claims: CLATi1S 1. A method for the preparation of a liquid polyisocyanate composition which comprises reacting one molar proportion of diphenylmethane diisocyanate containing at least 15% by weight of the 2,4'-somer with from 0.01 to 0.8 molar proportions of a monohydric alcohol of the formula: A - OH wherein A represents an alkyl radical containing from 9 to 16 carbon atoms or a radical of the formula: EMI12.1 wherein R represents an alkyl group containing from 1 to 12 carbon atoms, R represents hydrogen or an alkyl group containing from 1 to 3 carbon atoms and x is an integer of from 1 to 58, the reaction being performed at a temperature of from 100 to 250 C and in the presence of a catalyst for the NCO/OH reaction. 2. A method according to claim 1 wherein A is an alkyl radical containing from 10 to 14 carbon atoms. 3. A method according to claim 1 wherein R is an alkyl group containing from 1 to 5 carbon atoms. 4. A method according to claim 1 or claim 3 wherein R1 is hydrogen or methyl. 5. A method according to any one of the preceding claims wherein the diphenylmethane diisocyanate is reacted with from 0.1 to 0.3 molar proportions of the polyhydric alcohol. 6. The use in the manufacture of polyurethanes of a liquid diphenylmethane diisocyanate prepared according to any one of the preceding claims.

Inventors: HUGHES, JEFFREY, KEANE, KEVIN EDWARD
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1980
Main classification: C08G18
IPC codes: C08G18, C07C269, C07C265, C07C271, C07C239, C07C241, C07C67