METHOD OF FABRICATING A GAAS SEMICONDUCTOR SCHOTTKY BARRIER DEVICE

Abstract: A MESFET is formed from a substrate of p-type GaAs (1), a channel layer (6) of n-type GaAs, and a gate layer (2) of GaAlAs. Layer (2) is etched to expose regions (3) of layer (6), and so that its sidewalls are indercut. Tin (8) is deposited in one step on the device, and fused, and since it is inert with respect to layer (2), it forms a Schottky barrier there, but it dissolves parts of layer (6) at regions (3) to form ohmic drain/source contacts self-aligned with, and on opposite sides of, the gate contact on region (4).

Description: METHOD OF FABRICATING A SEMICONDUCTOR JUNCTION OR BARRIER The invention relates to a method of fabricating a semiconductor junction or barrier. In such fabrication processes, the small dimensions, and the precision with which those dimensions must be held, are reaching the point where the physical properties of the materials and processes involved must be very carefully selected. Dimensions of less than a micron are under consideration at the present state of the art. One structure for which small dimensions can be desirable to achieve low power and low signal delays is the gallium arsenide metal semiconductor field effect transistor (MESFET). However there are difficulties in constructing these devices in dimensionally small form. One difficulty is that during processing impurities may outdiffuse from the semi-insulating substrate into the channel layer and adversaly affect its characteristics. To overcome this a buffer layer of GaAs material could be grown on the semi-insulating substrate followed by growth of the channel layer. Another difficulty is in achieving a Schottky barrier height greater than Q9eV to avoid significant leakage current between gate and drain. A third difficulty is in achieving a gate width of a micron or less, for which a "self-alignment" fabrication procedure should be expected. US Patent 4075652 discloses a method of fabricating a p n semiconductor junction according to the introduction of claim 1. The p n junction is between the gate region and channel region of a GaAs field effect transistor, and may be 1 micron wide. A p-type GaAIAs gate region layer, 'which is on top of an n-type GaAlAs channel layer, is selectively etched to form the p n junction of narrow width. Aluminum is applied by a single vacuum deposition step to the exposed region of the channel layer and to a cap on the remaining region of the gate region layer, so that drain and source electrodes are formed for the FET on opposite sides of, and self-aligned with, a gate electrode. The cap material is chemically substantially the same as the channel layer i.e. Ga1 kAlkAs, where 0.1 > k > 0, although of opposite conductivity type. According to the invention, there is provided a method of fabricating a semiconductor junction or barrier, from a semiconductor body having strata comprising at least first and second layers (2,1,6), portions of the first layer being selectively removed to leave a remaining region (4) of the first layer and to expose a region (3) of the second layer, a metal (5,8) being applied to said remaining region (4) and to Said exposed region (3), characterised in that after said metal is applied, it is fused to said remaining region and to said exposed region, said first and second layer having different solubility in, or reactivity with, said metal during said fusing, the metal differently affecting the semiconductor of the first and second layers so that at least a semiconductor junction or barrier is formed in said body. This method differs from US Patent 4,075,652 firstly in that the first and second layers and the metal must be chosen so that the first and second layers have different solubility in, or reactivity with, the metal during the fusing, and secondly in the fusing step itself for the metal. The method of the invention thus operates according to a different principle, and offers advantages such as reduced difficulties in implementation. In the Drawings:# FIG. 1 is a schematic of a general process of steps of the invention; FIG. 2 is a schematic of steps of a particular embodiment, and FIG. 3 is a band energy diagram. As regards the process of FIG. 1 step 1 shows a semiconductor substrate 1 of a doped semiconductor material which is provided with a thin epitaxial layer 2 of a different semiconductor material. The two materials. are selected such that a metal used in step 3 will have a different solubility in layer 1 than it will have in layer 2. Referring to step 2, a vertical differentiation is now provided to delineate areas where the difference in solubility is to be employed. This is done, for example, by etching away portions of the layer 2, leaving exposed, regions 3 of the substrate and region 4 of the epitaxial layer 2. Referring to step 3, a metal 5 is then deposited on the regions 3 and 4, and is fused thereto. The metal 5, when fused, alloys with the substrate 1 and forms ohmic contacts on opposite sides of region 4, but it will not alloy with the region 4, but it forms a Schottky barrier type rectifying contact with the region 4. The resulting structure after the single temperature step is a field effect transistor structure wherein the two ohmic contacts serve as the source and the drain contacts and the Schottky barrier contact serves as the gate contact. The invention is particularly advantageous with respect to a gallium arsenide substrate having a thin epitaxial layer of gallium aluminum arsenide thereover. Such a structure when processed in accordance with the teachings of the invention, can result in a high gate barrier FET transistor. Thus referring to FIG. 2, step 1 shows a semi-insulating gallium arsenide substrate 1 doped with chromium (i.e. so that it is p-type), provided with an epitaxial layer 2 of gallium aluminum arsenide, and an upper active GaAs channel layer 6. As an example of one way to produce this structure, the substrate 1 is soaked in an isothermal two-phase equilibrium liquid phase epitaxy melt for 15 to 30 minutes. The melt contains a conductivity type determining element such as tin, sulfur, tellurium, or another common donor dopant element. Liquid phase epitaxy is used to produce the gallium aluminum arsenide layer 2, and during this epitaxial growth unwanted impurities are gettered into the melt from the upper region of the chromium doped gallium arsenide, and simultaneously the donor dopant element diffuses into the substrate 1 of gallium arsenide and produces the n-type channel layer 6. The epitaxy technique may cause the epitaxial layer 2 to be graded in composition and in energy band-gap. The epitaxy technique described can be replaced by that described in US Patent 4122476. The structure illustrated in FIG. 2 in step 1 may be more clearly perceived by referring simultaneously to FIG. 3. As a result of the epitaxial growth, there is a 0.05 to 0.1 micron gallium aluminum arsenide layer 2 which, as may be gathered from FIG. 3, is graded in composition and energy band-gap, the band-gap being approximately 2.0eV. When a Schottky barrier is made to this layer 2 a barrier height of 1.4eV is obtained which greatly reduces the gate-drain current. A graded composition layer is more desirable than a uniform composition one of 2.0eV band-gap to avoid jumps in the energy bands at the interface 10 between the two semiconductor materials 2,6. The diffused GaAs layer 6 is about 0.3 microns thick and has about 1017 impurity atoms/cc. The layer 6 shown in FIG. 2 and as described above is a diffused region in which the'dopant has diffused into the Ga As in accordance with the diffusion coefficient. However, as an alternative the layer 6 may be produced in the lower surface region of the graded epitaxial layer 2, since this lower surface region is almost pure gallium arsenide, or as still another alternative, the doped gallium arsenide layer 6 may be epitaxially grown before the gallium aluminum arsenide layer 2 is grown. Referring next to step 2 of FIG. 2, an area of photoresist 7 is formed over a portion of the gallium aluminum arsenide layer 2 and this layer is then selectively etched with HCl acid, exposing the regions 3, and undercutting region 6 at its side walls. Referring now to step 3 of FIG. 2, a layer 8 of tin is provided in a single step selectively on the regions 3 and over the region 4 which has been exposed when the photoresist 7 is removed. The metal layer 8 may be made up of tin with a layer of tungsten on top. The structure is fused by heating to 400-6000C at which point the tin will dissolve some gallium arsenide of region 3 but will not significantly dissolve gallium aluminum arsenide of region 4, due to the different solubilities of these materials in tin. When the structure is cooled down, the result is two regions each with 2x1 18 doping atoms/cc, in the gallium arsenide channel layer 6, and each of which forms as an epitaxial layer that grows from the dissolved tin-gallium arsenide melt. The tungsten would help to keep the tin in layer form and to prevent it from balling up during the liquid phase epitaxial growth. The metal layer 8 forms ohmic contacts to the layer 6 by means of the heavily doped n+ regions 3. ,.. . * On the region 4, however, the tin does not significantly dissolve the gallium aluminum arsenide but rather it remains inert and forms a Schottky barrier contact, intermediate the ohmic contacts. The resulting structure is a particularly advantageous gallium arsenide metal semiconductor FET structure (MESFET). The structure has a number of advantages. The excess impurities have been gettered during the processing operation. There is simultaneous formation of the Schottky barrier and the ohmic contacts. The gate and source-drain regions are self-aligned. The same metallurgy is employed for all contacts and a high barrier height of 1.4eV is provided for the gate of the FET. While the technique of the invention has been illustrated in connection with the construction of a MESFET transistor, the invention can be applied to forming a p-n junction in a single temperature cycle, and can be applied to a variety of semiconductor device structures. For example, the metal 8 and layer 6 or layer 2 may be such that the fusing step produces a p n junction in or with the layer 6. The invention can also be applied to producing a simple Schottky barrier having one contact to region 4 and only one of the n+ ohmic contacts. The layers 2 and 6 can have different solubility in the metal 8, or different reactivity e.g. as by alloying, whereby the metal differently affects these layers so that at least a semiconductor junction or barrier is formed.

Claims: CLAIMS 1. A method of fabricating a semiconductor junction or barrier from a semi conductor body having strata comprising at least first and second layers (2,1,6), portions of the first layer being selectively removed to leave a remaining region (4) of the first layer and to expose a region (3) of the second layer, a metal (5,8) being applied to said remaining region (4) and to said exposed region (3), characterised in that after said metal is applied, it is fused to said remaining region and to said exposed region, said first and second layers having different solubility in, or reactivity with, said metal during said fusing, the metal differently affectins.the semiconductor of the first and second layers so that at least a semiconductor junction or barrier is formed in said body. 2 A method as claimed in claim 1 in which said first layer is gallium aluminum arsenide and said second layer is gallium arsenide. 3. A method as claimed in claim 2 wherein said metal is tin. 4-. A method as claimed in- any preceding claim applied to fabricating a MESFET, said metal applied to said remaining region (4) forming a Schottky barrier thereto, and said metal applied to said exposed region (3) forming two ohmic contacts to said second layer on opposite sides of said Schottky barrier. 5. A method as claimed in¯any preceding claim in which said remaining region (4) is undercut at its side walls, and said metal is applied to said remaining region and to said exposed region in one step, whereby separate but aligned contacts are formed to said remaining region and to said exposed region.

Inventors: HOVEL, HAROLD JOHN, WOODALL, JERRY MCPHERSON
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1980
Main classification: H01L21
IPC codes: H01L29, H01L21