CATALYST FOR THE PREPARATION OF FURAN COMPOUNDS

Abstract: A process for preparing a furan compound by contacting a diolefin such as butadiene with a catalyst at a low pressure and a low temperature is provided. In this process, a diolefin, an oxygen-containing gas and water containing HCl are con­ tacted with a catalyst which is a support having deposited the­ reon copper chloride, and alkali metal chloride and at least one of palladium chloride and iodide, usually cuprous iodide. Tem­ perature of the reaction is usually in the range of about 80-125 °C and the pressure is usually in the range of about 1-5 atmospheres. Cyclic operation between furan production and catalyst oxidation is also provided.

Description: 1040 B TITLE CATALYST FOR THE PREPARATION OF FURAN COMPOUNDS DESCRIPTION Technical Field This invention relates to processes for the preparation of furan compounds, and more particularly to processes for the preparation of furan compounds from diolef ins, particularly butadiene. Background Art Furan is a chemical useful in furan resins and, more importantly, as a raw material for the manufacture of tetrahydrofuran. However, furan today is prepared from natural pentose contained in corn or oat hulls through furfural as an intermediate. To reduce the cost of tetrahydrofuran, it is produced today from acetylene and formaldehyde through 1,4-butynediol and 1,4-butanediol as intermediates. While this is a satisfactory process, it is moderately complex in the number of steps required to reach tetrahydrofuran as the final product. More importantly, however, acetylene is becoming more expensive due to energy inefficiencies involved in its manufacture. There have been attempts over the years to produce furan directly by the catalytic oxidation of butadiene. These attempts have generally been under harsh processing conditions, e.g., at temperatures higher than about 3750C, which result in overoxidation to carbon oxides and furan decomposition. Such high temperature, vapor phase processes are exemplified by U.S. Patents 3,238,225; 3,716,545; 3,775,508; 3,864,279'; 3,906,009; 3,912,763; 3,928,389 and 4,026,820. A process for preparing furan by oxidation of butadiene with molecular oxygen at lower tempera tures;-(40-1500C) either in a vapor phase reaction or a liquid phase reaction is described in Japanese Patent Application Publication 52-77049 dated June 29, 1977. In one aspect of the process described therein, a palladium salt and a thallium or indium salt are dissolved in acidified water and then butadiene and oxygen are passed through the solution. A similar process is described in Russian Patent 265119 dated June 24, 1970. In this process, butadiene (or butadiene and air) is passed through an acidic, aqueous solution of cupric chloride and palladium chloride at a temperature of 60-1100C. Cuprous chloride can be used in place of palladium chloride. Both of these processes suffer deficiencies of impractical rates of reaction and excessively low reaction life. Detailed Description According to the present invention, there is provided a process for preparing a furan compound, which process comprises contacting a catalyst consisting essentially of a support having deposited thereon (1) copper chloride, (2) at least one of palladium chloride and an iodide, and (3) optionally, an alkali metal chloride in a reaction zone with (4) a molecular oxygen-containing gas, (5) a diolefin of the formula R1C - CR n n RCH HCR where each R is H or an alkyl group of 1-4 carbon atoms, and each R1 is H, a halide or an alkyl group of 1-4 carbon atoms, with the proviso that the total number of carbon atoms does not exceed 8, and (6) water vapor containing about 0.5 5% by weight of HC1. In one embodiment of the present invention there is provided a process for preparing furan comprising: contacting a gaseous stream comprising (1) air, (2) butadiene, and (3) water vapor containing about 0.5-5% by weight HC1 based on the weight of the water, in a reaction zone maintained at a temperature in the range of about 80-1250C and at a pressure in the range of about 1-5 atmospheres, with a catalyst consisting essentially of a silica, alumina or silicaalumina support having deposited thereon (1) about 0.530%, by weight of the support, of copper chloride, (2) about 0.1-2%, by weight of the support, of cuprous iodide or about 0.01-2%, by weight of the support, of palladium chloride, and (3) 5-7%, by weight of the support, of calcium chloride. The present invention is a vapor phase process for the preparation of a furan compound, such as furan, from a diolefin especially butadiene, using a catalyst system consisting essentially of copper chloride, preferably a mixture of cuprous and cupric ions; optionally, an alkali metal chloride, preferably calcium chloride; and at least one of an iodide, preferably cuprous iodide, and palladium chloride, deposited on an inert support. This process, which can be conducted at low temperatures and pressures, produces the furan compound at good conversions and yields and at practical rates of reaction. A 1,3-diolefin is used as the starting material in the present process. The useful 1,3diolefins have the formula EMI4.1 where each R is H or an alkyl group of 1-4 carbon atoms (preferably methyl), and each R1 is H, an alkyl group of 1-4 carbon atoms (preferably methyl) or a halide such as chloro or iodo (preferably chloro), with the proviso that the total number of carbon atoms does not exceed 8, preferably does not exceed 5. Illustrative diolefins are 1,3-butadiene; 1,3-pentadiene; 2-chloro-1,3-butadiene; 2-methyl-1,3-butadiene; 2-iodo-l, 3-butadiene; 1,3-hexadiene, 2,4-hexadiene; 2,3-dimethyl-1,3-butadiene; 3,4-dimethyl-2,4-hexadiene; 4,6-octadiene; and 1,3-octadiene. Of these diolef ins, the first four listed are preferred due to commercial availability, with 1,3-butadiene being most preferred. Mixtures of diolefins can be used if desired. When used in the process of the invention, the diolefin can be fed separately and undiluted, mixed with a gas inert to the reaction, such as nitrogen, carbon monoxide or carbon dioxide, or mixed with an oxygen-containing gas such as air. In a preferred embodiment of the invention, the diolefin is mixed with the oxygen-containing gas and water vapor containing about 0.5-5% by weight HC1 to form a gaseous stream which is then contacted with the catalyst. However, cyclic addition of the gases to a reactor can be employed. While there does not appear to be anything critical about the gaseous stream's compositional make-up, having about 10-50% by volume of water vapor in the gaseous feed has been found useful. The stream contains about 1-50% by volume of butadiene with the balance being air. A preferred HC1 content is about 1-2% by weight, based on the weight of water, when palladium is used in the catalyst and about 3-58 by weight, based on the weight of water, when an iodide is used in the catalyst. The oxygen-containing gas employed can be molecular oxygen as such or molecular oxygen used with a diluent inert to the reaction such as nitrogen or the like. Typical molecular oxygen-containing gases are air, which is preferred, flue gases or synthesis gases which contain residual oxygen, and any source of molecular oxygen free of contaminants detrimental to the desired reaction. The catalyst used in the present invention consists essentially of an inert support, preferably of silica, alumina, silica-alumina or mixtures of these, in the form of pellets, powders or other configurations appropriate for use in a fixed, moving or fluid bed reactor. Illustrative other supports are titania, zirconia and other ceramics well known to those skilled in the art. Deposited on the support is copper chloride, preferably as a mixture of cuprous chloride and cupric chloride, optionally an alkali metal chloride, and at least one of palladium chloride and an iodide compound, typically cuprous iodide. When iodide is deposited on the support, it is usually as cuprous iodide even though iodide is fed to the reaction system as hydrogen iodide or as an alkali metal iodide. The alkali metal chloride used can be a divalent one such as calcium chloride, magnesium chloride, strontium chloride or barium chloride, or it can be a monovalent one such as sodium chloride, potassium chloride or lithium chloride. Divalent chlorides are preferred for their effectiveness, and calcium chloride is most preferred. The copper chloride is usually present on the support at a concentration in the range of about 0.530%, preferably 8-12%, by weight of the support. The alkali metal chloride, when it is used, is present at a concentration of 0.5-10%, preferably 5-7%, by weight of the support. Palladium chloride, when it is used, is present at a concentration of 0.01-2%, preferably 0.02-0.06%,by weight of the support. Iodide is ordinarily present at a concentration of 0.1-2%, preferably 0.03-0.05%, by weight of the support. The catalyst used in the process of the invention is conveniently prepared by dissolving at least one of cupric chloride and cuprous chloride, and the alkali metal chloride and palladium chloride (when they are used) in a dilute HC1 solution. One volume of solution so obtained is added to 2 volumes of catalyst support which absorbs essentially all the added solution. The material is then oven dried, usually under vacuum at 90-1000C. In the event iodide addition is desired, a second impregnation is made using the desired iodide concentration in aqueous solution. A second suitable method involves feeding HI solution in the aqueous HC1 feed to the catalyst vapor phase until the desired iodide has been charged. The process of the invention can be carried out at a temperature in the range of about 80-1250C, preferably about 100-1250C. As would be expected, rates of furan production are reduced at the lower temperatures. Reaction pressures are typically in the range of about 1-5 atmospheres, preferably about atmospheric pressure. It is the diolefin's partial pressure in the gas stream contacted with the catalyst that determines the particular pressure used. The diolefin flow rate through the catalyst contained in a reaction vessel does not appear to be critical. As will be apparent, the flow rate should not be so fast as to give inadequate contact time between the diolefin and the catalyst or so slow as to enable the resulting furan product time to decompose or polymerize. It is preferred that the catalyst be in a fixed bed as is known to those skilled in the art, and that the reaction off-gases containing furan product be removed from the reaction vessel promptly. The optimum contact time between the diolefin and catalyst depends on many factors and is readily determined by one skilled in the art. Since the reaction system is very corrosive, the reactor for carrying out the process of the invention should be made of a material which is not corroded. Illustrative materials are glass or ceramic-lined metals, titanium, tantalum-clad metals, impreganted graphite tubes and the like. Another embodiment of the invention is a twostep cyclic process wherein furan is produced in a first step by contacting the diolefin with the catalyst, and cuprous ion on the catalyst is oxidized to cupric ion in a second step by contacting the catalyst containing excess cuprous ion with the above-described oxygen-containing gas. In a representative cyclic operation, a feed of butadiene and nitrogen is contacted with the catalyst until butadiene starts being detected in the off-gases. It is theorized that butadiene is absorbed by the catalyst and takes some intermediate compound form. The butadiene feed is turned off and air is introduced to the reactor and fed in until oxygen consumption drops, indicating that oxidation of the catalyst is essentially complete. The atr is then turned off and butadiene again fed to the catalyst. Water with HC1 is fed at all times. Such cyclic operation seems to give a higher concentration of furan in the off-gases for a longer period of time. When the furan yield then drops below some predetermined level, air is reintroduced for reoxidation of the catalyst. To maintain a high furan production rate, at least two reactors can be operated sequentially so that while the catalyst in one reactor is being oxidized, furan is being produced in the second reactor. An advantage of cyclic operation is that less palladium can be used in the catalyst. An alternative to cyclic operation is continuous circulation of the catalyst bed. In the examples, concentrations were determined by gas chromatographic analyses. The samples were injected into a 10' X 1/8" column of "Polopak N" for determination of their air, carbon dioxide, butadiene and furan contents. Analyses were carried out at 1750C with helium carrier gas at 33 ml/min. The areas of the peaks in the chromatograph were converted to volume percents of components using factors determined by calibrations with known quantities of components. In all of the examples except Example 1, water was removed from the reaction off-gases by an air-cooled condenser prior to gas analysis. The invention can be further understood by the following examples in which percentages are by volume unless otherwise stated. Example 1 To 100 g of a silica powder were added 50 cc of water having dissolved therein 0.5 g PdC12, 4 g CuCl2.2H2O, 2 g LiCl and 2 cc of concentrated HC1 (aqueous solution of 36% by weight HC1). The resulting impregnated catalyst was dried overnight in an oven maintain; at 1300C. A 0.95 cm X 12.7 cm (3/8" X 5") stainless steel U-shaped tube reactor heated in a sand bath to a desired temperature was charged with 8.3 g of catalyst. Gaseous reactants fed to the reactor were first mixed and then fed to one end of the tube reactor. At 1250C and a feed rate of 73 cc/min with a feed composed of 45 cc of water vapor with 1% by weight HC1, 9 cc of butadiene, 11.7 cc of air and 7.3 cc of N2, the composition of the gaseous product, by volume, analyzed at about 0.25% CO2, 26.9% water, 31.2% butadiene, 0.58 furan, 0.1% oxygen and 41.1% N2. Ninety-six minutes later the furan content in the gaseous product was about 0.26%. At 152 minutes, the furan content was about 0.28% and at 217 minutes it was about 0.24%. Butadiene in the feed was turned off and the catalyst was reoxidized by passing air through the reactor for 90 minutes. When the butadiene feed was restarted, furan content in the gaseous product was 0.38% at 1100C. Example 2 A solution of 5 g PdC12, 5 g KC1, 50 g CuC12 2H2O and 15 cc of concentrated HC1 in 200 cc water was added to 600 g of 1/8" alumina pellets (Houdry 100 S) and oven dried at 1000C for about 12 hours under vacuum. The resulting catalyst was charged to a glass reactor oil-heated to 1250C. Gaseous reactants (except water) were mixed in a manifold and fed to the reactor through a glass distributor located in the bottom of the reactor. The water-HCl feed was fed in a tube passing through the top of the reactor and the catalyst bed to preheat the water. At the bottom of the reactor, the water vaporized and mixed with the other gases discharged from the distributor. Gaseous feeds of (1) 300 cc/min steam containing 1% by weight HC1, (2) 200 cc/min air, (3) 200 cc/min N2 and (4) 25 cc/min butadiene were fed into the reactor and contacted with the catalyst. After 7 minutes, furan content in the gaseous product was 2%; after 97 minutes it was 2.6% and after 5 hours it was 1.8%. The run was terminated after 5 hours. Example 3 A catalyst was prepared as in Example 2 ex cept the KC1 was omitted. After charging the catalyst to the glass re actor heated to 1250C, a gaseous flow of 300 cc/min N2, 175 cc/min air, 300 cc/min water vapor with 1% by weight HC1, and 25 cc/min butadiene was fed into the vessel as described in Example 2. After 8 minutes at 1250C, the product gases contained 2.2% furan and in creased to 3.2% after 2 hours. The furan content in the product gases remained constant at 3.2% until the reactor was shut down after 5.5 hours. Example 4 A catalyst was prepared as in Example 2 except 5 g of CuCl was used in place of KC1 and charged to the oil-heated glass reactor. The feeds to the re actor were (1) butadiene at 10 cc/min, (2) N2 at 200 cc/min, (3) air at 125 cc/min and (4) water vapor with 1% by weight HC1 at 250 cc/min. At a reactor tempera ture of 950C, the furan content in the off-gases was 2.8% one hour after feeds were started. The run con tinued for 17 hours with the furan content in the off gases ranging from 2.4-4%. Example 5 Catalyst was prepared as in Example 2 and charged to the oil-heated reactor. Deposited on the alumina pellets were 50 g of CuC12 2H2O and 0.1 g of PdCl2. Initially, at a reactor temperature of 95 97eC, butadiene was fed to the reactor at a rate of 10 cc/min, air at a rate of 150 cc/min, N2 at a rate of 200 cc/min and water vapor with 1% by weight HC1, at a rate of 300 cc/min. Under these conditions, virtually all of the butadiene fed was consumed in the reactor with only traces of furan being analyzed in the reactor off-gases. This condition continued for a period of 2 hours, at which point the butadiene feed was turned off and the air feed increased to 250 cc/min for two hours. The air feed was then turned off and butadiene feed started at 60 cc/min with N2 feed at 100 cc/min. After 20 minutes, furan in the off-gases rose to a maximum concentration of 7% and then declined gradually over an additional period of 1 hour at 95-1000C to 2.4%. Example 6 (Best Mode) A catalyst was prepared as in Example 2 except the catalyst consisted of 50 g CuC12 2H2O, 1 g PdC12, 33 g CaC12 and 5 g CuCl on 500 g of the alumina pellets. After the catalyst was charged to the oilheated glass reactor maintained at a temperature of 95-100 C, the gas feeds were started at the following rates: 12 cc/min of butadiene, 200 cc/min of N2, 125 cc/min of air and 250 cc/min of water vapor which contained 2% by weight of HC1. For a period of 6 hours, only a trace of furan was present in the offgases. After this period of time, the butadiene and N2 feeds were turned off and the air feed increased to 250 cc/min for a period of two hours. After this period, the air feed was turned off and the butadiene feed rate increased to 70 cc/min. After 20 minutes at the new feed rates, furan was analyzed in the off-gases at a concentration of 7.2%. Furan concentration in the off-gases after 80 minutes was 15% and then declined to 5% after 120 minutes. Example 7 A catalyst consisting of 100 g CuC12 2H2O, 10 g CuCi on 400 g of 1/8" silica-alumina pellets was charged to the oil-heated reactor described in Example 2. Temperature was raised to 1100C and 5 cc of 78% HI aqueous solution in 25 cc of 1% aqueous HC1 was fed to produce cuprous iodide on the pellets. The catalyst was conditioned at 1100C with a stream of butadiene in nitrogen at 20 cc and 200 cc/min, respectively, for a period of 90 minutes. At that time the butadiene and nitrogen feeds were turned off and the system oxidized with an air flow rate of 250 cc/min at 1100C for one hour. After that time a feed composition consisting of 200 cc/min water vapor containing 5% by weight HC1, 70 cc/min butadiene and 120 cc/min air was fed at 98 C. After one hour furan was 5% in the product and remained at that level for an additional four hours when the test was terminated. Example 8 A catalyst, prepared as in Example 2, consisting of 100 g CuC12 2H2O, 10 g CuCl and 0.1 g PdC12 on 600 g of 100 S Houdry alumina 1/8" pellets was charged to the oil-heated glass reactor maintained at 1000C. The feed streams to the reactor were fed as in Example 2 at the following rates: butadiene at 60 cc/min, N2 at 75 cc/min and water vapor containing 1% by weight HC1 at 300 cc/min. No air was fed to the reactor. These feeds were continued for 90 minutes with only a trace of furan being detected in the offgases. At this point, the butadiene and N2 feeds were stopped and the air feed turned on to give a flow rate of 350 cc/min. The air and water vapor flows continued for 2 hours and then the butadiene and N2 feeds restarted at the above-described rates. At a reactor temperature of 980C, furan was detected in the offgases for 2 hours at a concentration ranging from 8-10%. Again, the butadiene and N2 feeds were stopped and the air and water vapor feeds continued for another 1 hour. After the 1 hour, the butadiene and N2 feeds were restarted as above and furan was produced at a concentration of 8% in the off-gases for an additional period of 2 hours. Example 9 A catalyst consisting of 550 g of steamtreated alumina-silica pellets (sold by Grace Chemicals) impregnated with 100 g CuC12 2H2O, 20 g CuCl and 0.2 g PdC12 was prepared as in Example 2. The catalyst was charged to an oil-heated glass reactor as described in Example 2 which was maintained at 1170C. Water vapor containing 3% by weight HC1 was fed to the reactor, as described in Example 1, at a rate of 300 cc/min. The butadiene and N2 feeds were started at 25 cc/min and 200 cc/min, respectively. For a period of 1 hour and 18 minutes, virtually all of the butadiene was absorbed on the catalyst as only traces of furan were detected in off-gases. The butadiene and N2 feeds were turned off and air was fed to the reactor for copper regeneration at a rate of 180 cc/min. During 111 minutes of feeding air, only a trace of furan was produced. The air feed was then turned off and the butadiene and N2 feeds restarted at 70 cc/min and 75 cc/min, respectively. After 34 minutes, the furan concentration in the off-gases rose to a maximum of 12.6% and then dropped to 4% after 84 minutes. At this point, the N2 feed was turned off and air feed was restarted at a rate of 180 cc/min. Furan concentration in the off-gases increased to 5.7% and remained constant during the next 3-hour period before the run was terminated.

Claims: CH 1040 B CLAIMS 1. A catalyst consisting essentially of a support having deposited thereon (a) 0.5-30%, by weight of the support, of copper chloride, (b) 0.5-10%, by weight of the support, of an alkali metal chloride, and (c) at least one of (1) 0.01-2%, by weight of the support, of palladium chloride, and (2) 0.1-2%, by weight of the support, of an iodide compound. 2. The catalyst of claim 1 in which the copper chloride is a mixture of cuprous chloride and cupric chloride. 3. The catalyst of claim 1 in which the component in (c) is palladium chloride. 4. The catalyst of claim 1 in which the component in (c) is cuprous iodide. 5. The catalyst of claim 1 in which the alkali metal chloride is of a divalent alkali metal. 6. The catalyst of claim 5 in which the alkali metal chloride is calcium chloride. 7. A catalyst consisting essentially of a support having deposited thereon (a) 0.5-30%, by weight of the support, of a mixture of cupric chloride and cuprous chloride, (b) 0.5-10%, by weight of the support, of calcium chloride, (c) 0.01-2%, by weight of the support, of palladium chloride.

Inventors: FREMONT, JOSEPH MELVIN, GARNETT, DONALD IRWIN
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1980
Main classification: B01J27
IPC codes: C07D307, B01J27