PROCESS FOR THE PREPARATION OF LIGHT HYDROCARBON FRACTIONS

Abstract: Light hydrocarbon fractions are prepared by hydrocracking a heavy hydrocarbon oil of which at least 50% v boils above 350°C and at least 10% V above 450°C at a hydrogen partial pressure below 100 bar. A catalyst is employed which contains Ni and W on a faujasite carrier and which has a specific particle diameter (d) and specific average pore diameter (p) such that the following relation is satisfied: (P H2 being hydrogen partial pressure in bar, d in mm, p in nm).

Description: PROCESS FOR TEE PREPARATION OF LIGRU HYDROCARBON FRACTIONS The invention relates to a process for the preparation of light hydrocarbon fractions by hydrocracking a heavy hydrocarbon oil. Rydrocracking of heavy hydrocarbon oils for the preparation of light hydrocarbon fractions such as gasoline, kerosine and gasoil fractions is spplied on a large scale in the oil industry. Rydrocracking is carried out by contacting the feed, together with hydrogen, at elevated temperature and pressure with a catalyst Which contains one or more metals with hydrogenating activity çhich have been deposited on a carrier with cracking activity. As metals with hydrogenating activity are used, inter alia, platinum, palladium and combinatiorn of nickel or cobalt with molybdenum or tungsten. As carriers with cracking activity amorphous materials such as alumina and silicaalumina and crystalline materials such as faujasite are used. A drsirback of catalytic hydrocracking is that, as a rule, it should be carried out at a relatively high hydrogen partial pressure, in order to avoid rapid catalyst deactivation. Moreover, the required hydrogen partial pres- sure winl be higher according as the feed to be hydrocracked is heavier. In general, it may be said that in the catalytic hydrocracking of heavy hydrocarbon oils of which 50%v boils above 3500C and more than 10%v above 4500C, a requirement for reaching a catalyst life which makes the process acceptable for commercial use is that hydrogen partial pressures should be above 100 bar. The use of these high hydrogen partial pressures requires expensive equipment and involves a high hydrogen consumption. In view of the ample availability of the above-mentioned type of heavy hydrocarbon oils and the increasing demand for light hydrocarbon fractions, there is a need for a process for the catalytic hydrocracking of these oils at low pressure. The Applicant has carried out an investigation concerning this subject. From the above-mentioned metals with hydrogenating activity and carrier materials with cracking activity were selected combinations of nickel and tungsten and carriers which consist of more than 50%w faujasite, as it was found that catalysts built up of these components show a high activity and selectivity in the hydrocracking of the above-mentioned heavy feeds, also at hydrogen partial pressures below 100 bar. It was found in this investigation that, when hydrocracking the said heavy feeds at hydrogen partial pressures below 100 bar, the stability of these catalysts greatly depends on their porosity and particle size and that the requirements that have to be made with respect to the porosity and particle size in view of the stability are dependent on the hydrogen partial pressure used. It was found that in the hydrocracking of the said heavy hydrocarbon oils using the said catalysts at hydrogen partial pressures below 100 bar, a catalyst stability which is acceptable for commercial use of the process can be reached, if the catalyst has a specific average particle diameter (d) and a specific average pore diameter (p) such that the following relation is satisfied: ()1 .75 < 0.73 x (PH)2.5, d wherein Pg represents the hydrogen partial pressure used 2 (p in nm, d in mm, Ps in bar). The above-mentioned values 2. of d and p have been defined as follows on the basis of their method of determination. The way in which d is determined depends on the form of the catalyst particles. When this form is such that the particle diameter distribution of the catalyst can be determined with the aid of sieve analysis, d is determined as follows. After a complete sieve analysis of a representative catalyst sample has been carried out, d is read from a graph in which for each successive sieve fraction the percentage by weight, calculated on- the overall weight of the catalyst sample, has been plotted cumulatively as a function of the linear average particle diameter of the sieve fraction concerned; d is the particle diameter corres- ponding with 50S of the overall weight. This method can be used for the d-determination of spherical and granular materials and of materials of a similar shape, such as extrudates and pellets with a length/diameter ratio between 0.9 and 1.1. The d-determination of extrudates and pellets with a length/diameter ratio which is smaller than 0.9 or larger than 1.1, and of similar cylindrical materials, whose particle diameter cannot be determined by sieve analysis, is carried out as follows. After a complete length distribution analysis (in case the length/diameter ratio is smaller than 0.9) or after a complete diameter distribution analysis ( in case the length/diameter ratio is greater than 1.1) of a representative catalyst sample has been carried out, d is read from a graph in which for each successive length or diameter fraction the percentage by weight, calculated on the overall weight of the catalyst sample, has been plotted cumulatively as a function of the linear average size of the fraction concerned; d is the value which corresponds with 50S of the overall weight. After the pore diameter distribution of a catalyst sample has been determined, p is read from a graph in which, for the pore diameter range of 10 - 15000 nm, for each successive increase in pore volume which is smaller than or equal to 10X of the pore volume present in pores with a diameter of 10 - 15000 nm, the quotient of the increase in pore volume and the corresponding pore diameter interval has been plotted cumulatively as a function of the linear average pore diameter over the relevant pore diameter interval; p is the pore diameter corresponding with 50% of the overall quotient at 15000 nm. The determination of the pore diameter distribution of the catalyst is carried out by means of the mercury penetration method as described by H.L. Ritter and L.C. Drake in Industrial and Engineering Chemistry, Analytical Edition 17, 787(1945), using mercury pressures of 1 - 1500 bar. The pore diameter distribution of the catalyst in the pore diameter range above 10 nm is calculated by means of the formula: pore diameter (in nm) = 15000 mercury pressure, absolute (in bar) The present patent application therefore relates to a process for the preparation of light hydrocarbon fractions by hydrocracking a heavy hydrocarbon oil, in which a heavy hydrocarbon oil of which more than 50%v boils above 3500C and more than 10%v above 4500C is contacted, together with hydrogen, at elevated temperature and a hydrogen partial pressure below 100 bar with a catalyst which contains the metal combination nickel-tungsten deposited on a carrier comprising more than 501x fauuasite, which catalyst has a specific average particle diameter (d) and specific average pore diameter (p) such that the following relation is satisfied: #ff5 < 0.73 x (PH2)2.5 , wherein PH2 is the hydrogen d partial pressure used (p in nm, d in mm, PH in bar). H2 The catalysts that can be used according to the invention are characterized by a certain relation between their p and d at a given pH2 It is important that p and d, which are used for characterizing the catalysts, are determined in accordance with the methods described above, because when for characterizing the catalysts use is made of an average pore diameter or an average particle diameter which has been determined by methods other than those mentioned above (e.g. an average pore diameter calculated as )I x the quotient of the pore volume and the surface or an average particle diameter calculated as the linear average), different results may be obtained. The relation found between p, d and P can be used 2 for three different purposes. In the first place, the relation provides the opportunity to find out whether it is indeed possible to reach an acceptable stability with a catalyst which has a given p and d, when carrying out the process at a P below 100 bar, and if so, above what H2 value PH2 should at any rate be chosen in order to achieve this. Further, the relation may be used to determine the value above which d of a catalyst material with a given p should be chosen in order to obtain an acceptable stability at a given PH2 below 100 bar. Finally, the relation provides the opportunity to determine the value below 'which p of a catalyst material with a given d should be chosen in order to obtain an acceptable stability at a given P below 100 bar. Although, when using the relation between p, d and according to the invention it will always be possible to indicate for a catalyst material with a given p a minimum value for d above which an acceptable stability can be reached at a P below 100 bar, the choice of d is partly determined 2 by the activity and selectivity of the catalyst. In the process according to the invention it will be preferred to use a catalyst material with a d-value between 0.5 and 25 mm, because it has been found that catalysts of the present type as a rule have too low an activity and selectivity for hydrocracking the said heavy hydrocarbon oils, if they have a d-value which is smaller than 0.5 mm or larger than 25 un. In the process according to the invention it is preferred to use a catalyst with a d-value between 1 and 5 mm. As with the choice of d, the choice of p is partly determined by the activity and selectivity of the catalyst. By using the relation between p, d and P according 2 to the invention it is always possible to rind for a catalyst material with a given d a p-value below which an acceptable stability can be reached at P below 100 bar. H2 In view of the required activity of the catalyst it will be preferred to use in the process according to the invention no catalysts with a value below 10 nm and in view of the required selectivity of the catalyst it will be preferred to avoid the use of catalysts with a p-value above 1000 nm. In the process according to the invention it is preferred to use a catalyst with a p-value between 50 and 200 nm. In the process according to the invention a catalyst should be used which contains the metal combination nickeltungsten, deposited on a carrier which consists of more than 50$w faujasite. As regards the metal load preference is given to catalysts which contain 0.1 to 25 pbw nickel and 1 to 50 pbw tungsten per 100 pbw carrier. Particular preference is given to the use of catalysts which contain 0.5 to 5 pbw nickel and 5 to 25 pbw tungsten per 100 pbw carrier. As regards the carrier preference is given to carriers which consist of more than 60%w faujasite and in particular of from 70 to 80Sw faujasite and the rest of inert binder material. A very suitable binder material of the present catalyst is alumina. The catalysts according to the invention are preferably used in the sulphidic form. Sulphiding may be carried out by one of the known techniques for sulphidation of catalysts such as contacting the catalysts with a sulphur-containing gas, for instance a mixture of hydrogen and hydrogen sulphide, or contacting the catalyst with hydrogen and sulphur-containing hydrocarbon oil, for instance gas oil. In addition to the metals nickel and tungsten the catalysts may also contain promoters such as phosphorus, boron and halogen, in particular fluorine. The preparation of light hydrocarbon fractions by hydrocracking according to the invention can very suitably be carried out at a temperature of from 250 to 450 0C and a space velocity of from 0.2 to 5.0 1 feed per I catalyst per hour. The preferred conditions are: a temperature of from 300 to 425 C aoaa space velocity of from 0.5 to 3.0 1 feed per 1 catalyst per hour. The process according to the invention is carried out at a P which is at any rate below H2 100 bar. In respect of the choice of P at which the process will be carried out the following remarts should bye made. If it is found that, when using the relation according to the invention, for a catalyst material with given p and d values.a PH2-value below 100 bar is obtained above which with the catalyst material concerned an acceptable stability can be reached, the process according to the invention will preferably be carried out at a P as low as possible. H2 Naturally, the P used will have to lie above the P which H2 H2 follows from the relation. There are no restrictions here in the choice of the P in connection with activity or H2 selectivity as was the case with the choice of p and d. However, care should be taken to ensure that there is sufficient hydrogen in the reactor in view of the hydrogen consumption of the occurring hydrocracking reactions. In the process according to the invention the starting material is a heavy hydrocarbon oil of which more than 501v boils above 3500C and more than 10Sv above 4500C. The preferred starting materials are heavy hydrocarbon oils of which more than 60%v boils above 350 C and more than 15%v above 4500C, and in particular heavy hydrocarbon oils of which more than 70%v boils above 350 C and more than 20%v above 450 C. Very suitable feeds for the present process are distillates obtained in the vacuum distillation of atmospheric distillation residues of crude oils, oils obtained in the deasphalting of vacuum residues of crude oils and mixtures of the said vacuum distillates and deasphalted oils. The hydrocracking according to the invention is preferably applied to heavy hydrocarbon oils which contain less than 100 ppmw organically bound nitrogen. Particular preference is given to heavy hydrocarbon oils which-contain less than 10 ppmw organically bound nitrogen. Heavy hydrocarbon oils with a high content of organically bound nitrogen are preferably subjected to a catalytic hydrodenitrogenation before being used as the feed for the process according to the invention. A very suitable catalyst for hydrodenitrogenizing the present heavy hydrocarbon oils is a catalyst containing the metal combination nickel-molybdenum on alumina as the carrier. When using a catalytic hydrodenitrogenation previous to the catalytic hydrocracking according to the invention, it is preferred to use the complete reaction product from the hydrodenitrogenation (without ammonia, hydrogen sulphide or other volatile components being separated from it) as the feed for the hydrocracking. The catalytic hydrociacking according to the invention may be performed in the vapour phase, in the liquid phase or partly in the vapour phase and partly in the liquid phase. It is preferred to use a fixed catalyst bed. A very suitable embodiment is one in which the feed to be converted, which is partly in the liquid phase and partly in the gas phase, is conducted over a fixed catalyst bed, the trickle phase" method. The invention will now be explained with reference to the following example. Example Five catalysts (A-E) were prepared by impregnating carrier materials which consist of 75%w .faujasite and 251n alumina with aqueous solutions, which contain either a nickel and a tungsten salt or a platinum salt, followed by drying and calcining of the composites. The compositions of the catalysts and their p and d-values, determined according to the method described earlier, are given in Table A. This table also gives for (p)1.75 each catalyst the value of x : d Table A (p)1.75 Cat. Metal load in p, d, x = d No. pbw per 100 nm mm - pbw carrier A 3Ni/9.5W 240 1.5 9756 B 3Ni/9.5W 470 2.2 21565 C- 3Ni/9.5W - 240 0.6 24390 - - D 0.5Pt 240 1.5 9756 0.SPt 240 0.6 24390 Catalysts A-E were used for hydrocracking two feeds (I and II). Feed I was a distillate obtained in the vacuum distillation of an atmospheric distillation residue of a crude oil from the Middle East. Feed I had a content of organically bound nitrogen of 630 ppni and a sulphur content of 2.655w. Feed I had an initial boiling point of 250 C; 80Sv of it boiled above 3500C and 30Sv above 4500C. Feed II was a distillate obtained in the atmospheric distillation of a crude oil from the Middle East. Feed II had a content of organically bound nitrogen of 200 ppmw and a sulphur content of 2.04%w. Feed II had a final boiling point of 3730C and 28% of it boiled above 350 C. The experiments were carried out in a standard test, in which the feed - in the presence of hydrogen - was conducted successively through two reactors, each reactor containing a fixed catalyst bed in which the complete reaction product from the first reactor was used as the feed for the second reactor. In the first reactor a NitMo/Al203 denitrogenation catalyst was present which contained per 100 pbw alumina carrier 4 pbw nickel and IT pbw molybdenum. The second reactor contained the cracking catalyst to be tested. All the catalysts were used in the sulphide form. Sulphidation of the catalysts was performed by contacting them for 6 hours at a temperature of 375 C and an overall pressure of 10 bar with a mixture of hydrogen and hydrogen sulphide with an E2/E2volume ratio otT . t. The conditions under wnich the experiments were carried out were as follows. The denitrogenation step was carried out at a temperature of 375 0C, a space velocity of 1 1 oil/ 1 catalyst/h, an H2/oil ratio of 150O- Nl B2/kg oil and a PH equal to the one used in the hydrocracking step of the 2 experiment concerned. The hydrocracking step was carried out at a temperature of 365 0C, a space velocity of 1 1 oil/ 1 catalyst/h, an H2/oil ratio of 1500 Nl H2/kg oil and a PHa varying between 35 and 60 bar. Under the conditions of the standard test the stability of a cracking catalyst is considered acceptable only if after 300 hours the yield of 180 C-minus product calculated on the feed is at least 60%w for feed I and at least 80%w for feed I1. The results of the experiments are shown in Table B. This table also gives for each experiment the value of y = 0.73 x (PH2)2.5. Table B Exp. Cat. Feed PH2, y=0.73x(PH2 )2.5 Yield of 180 C product No. No. No. bar ¯¯¯¯¯¯¯¯¯¯¯¯¯¯ after 300h, %w 1 A I 60 20356 75 2 B I 60 20356 56 3 C I 60 20356 54 4 A I 35 5290 18 5 A II 60 20356 96 6 C II 60 20356 95. 7 D I 60 20356 36 8 E r 60 20356 34 Of the experiments in Table B only no. 1 is an experiment according to the invention. In this experiment, for the hydrocracking of a heavy feed using a Ni/W catalyst with given p and d the value of P was chosen such that the relation x < y 2 was satisfied. In this experiment the stability requirement found to be amply met by the catalyst. Experiments 2-8 are outside the scope of the invention and have been included for comparison. In experiments 2-4, for the hydrocracking of a heavy feed using Ni/W catalysts with given p and d the value of P was chosen such that the relation H2 x < y was not satisfied. In these experiments the catalysts were found not to satisfy the stability requirement. In experiments 5 and 6, for the hydrocracking of a light feed using Ni/W catalysts with given p and d the value of PH was chosen such that the relation x < y was satisfied experiment 5 and not in experiment 6. Nevertheless, in both experiments the stability requirement was found to be amply met by the catalysts. In experiments 7 and 8, for the hydrocraking of a heavy feed using Pt catalysts with given p and d the value of PH2 was chosen such that the relation x < y was satisfied in experiment 7 and not in experiment 8. Nevertheless, in both experiments the catalysts were found not to meet the stability requirement. The results of experiments 5-8 clearly demonstrate the specific character of the relation found between p, d and both as regards the nature of the metals present on the carrier and as regards the heaviness of the feed to be cracked.

Claims: CLAIMS 1. A process for the preparation of light hydrocarbon fractions by hydrocracking a heavy hydrocarbon oil, characterized in that a heavy hydrocarbon oil of which more than 50%v boils above 3500C and more than 10%v above 450 C is contacted, together with hydrogen, at elevated temperature and a hydrogen partial pressure below 100 bar with a catalyst which contains the metal combination nickel-tungsten deposited on a carrier which comprises at least 50%w faujasite, which catalyst has a specific average particle diameter (d) and specific average pore diameter (p) such that the following relation is (p)1.75 satisfied: d < 0.73 x (pH2)2.5 , wherein PH2 is the hydrogen partial pressure used (p in nm, d in mm, PH2 in bar). 2. A process according to claim 1, characterized in that the catalyst has a d-value between 0.5 and 25 mm and a p-value between 10 and 1000 nm. 3. A process according to claim 1 or 2, characterized in that the catalyst contains 0.1 to 25 pbw nickel and 1 to 50 pbw tungsten per 100 pbw carrier. 4. A process according to any one of claims 1-3, characterized in that the catalyst carrier consists of more than 60%w faujasite and the rest of inert binder material. 5. A process according to any one of claims 1-4, characterized in that the catalyst carrier contains alumina as inert binder material. 6. A process according to any one of claims 1-5, characterized in that the catalyst is used in the sulphidic form. 7. A process according to any one of claims 1-6, characterized in that it is carried out at a temperature of from 250 to 450 C and a space velocity of from 0.2 to 5.0 1 feed per 1 catalyst per hour. 8. A process according to any one of claims 1-7, characterized in that the heavy hydrocarbon oil contains less than 100 ppmw organically bound nitrogen. 9. A process according to claim 8, characterized in that the heavy hydrocarbon oil is subjected to a catalytic hydrodenitrogenaton before being hydrocracked. 10. A process according to claim 9, characterized in that the complete reaction product from the hydrodenitrogenation is used as the feed for the hydrocracking.

Inventors: BODE, DIRK, JANSSEN, MARTINUS MARIA PETRUS
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1980
Main classification: C10G47
IPC codes: C10G65, C10G47