N,N'-BIS-2(3(3,5-T-BUTYL-4-HYDROXYPHENYL)PROPIONYLOXY)ETHYL OXAMIDE, A METHOD OF MAKING IT AND COMPOSITIONS INCORPORATING IT

Abstract: A novel form of N,N¹-BIS-(2-(3-(3,4-DI-TERT.-BUTYL-4 -HYDROXYPHENYL)PROPIONYLOXY)ETHYL) OXAMIDE is disclosed having a melting point of about 178°C. The compound may be made by recrystallising the crude or pure low melting point form from a suitable solvent such as ethanol, isopropanol or acetone, preferably by seeding the solution with crystals of the higher melting species. The compound is useful as an antioxydant for polymeric materials, in particular polyolefins such as polyethylene or polypropylene, having a high degree of permanence.

Description: N, N'-bis-2 [3 (3, 5-t-butyl-4-hydroxyphenyl) propionyloxy] ethyl oxamide The present invention relates to N,N'-bis-2[3(3 ,5-t-butyl-4- hydroxyphenyl)propionyloxy] ethyl oxamide melting at about 178"C. U.S. Patent 4,145,556 (Hirsch et al.) discloses a N,N1-bis-2[3 (3, 5-t-butyl-4-hydroxyphenyl )propionyloxy lethyl oxamide having a melting point of 134 - 13600. The same compound is disclosed in U.S. Patent Application S.N. 931,087 filed August 4, 1978. All organic polymeric materials are to a smaller or larger degree affected by heat and oxygen. Antioxidants are incorporated into polymers to protect them against heat and oxygen both during processing and during their service lifetime. Besides the obvious criterion of activity, such antioxidants have to meet a number of other requirements, depending on the intended end use of the polymer. Such criteria include color, odor, hydrolytic stability, resistance to leaching and permanence or lack of volatility. (See Kirk-Othmer Encyclopedia of Chemical Technology. Vol. 3 p. 133, John Wiley and Sons, 1978). Since higher processing temperatures are desirable in order to increase processing productivity, antioxidant volatility or lack thereof becomes a very important factor because such processing temperatures may cause volatilization, sublimation or decomposition of the antioxidant, reducing or even eliminating antioxidative stabilization. It is the object of this invention to provide an antioxidant with improved temperature permanence. The antioxidant is N, N'-bis-2- [3 (3,5-di-tert. -butyl-4-hydroxyphenyl)propionyloxy] ethyl oxamide melting at about 1780C. It was found, unexpectedly, that the high melting form has much improved permanence/volatility characteristics. In a thermo gravimetric experiment described in Example 2, the higher melting form lost 18% of its weight while the lower melting species lost 63% of its weight: The high melting form can be made readily by recrystallizing the crude or pure low melting form from a suitable solvent such as ethanol, isopropanol or acetone, preferably by seeding the solution with crystals of the higher melting species. Such seed crystals are readily prepared by column chromatography or by slow crystallization. The compound of the present invention is useful in stabilizing organic materials normally subject to oxidative degradation. Materials that are thus stabilized include a multitude of synthetic polymers. Among those polymers are various polyolefins such as polyethylene, polypropylene, polybutylene, polybutadiene and polymethylpentene. Other polymers stabilized by the compounds of the present invention include acetal resins, polyacrylates, polydialkylpthalate, cellulosics, polyamides, polyesters, polyurethanes, polycarbonate, polystyrene, polyvinyl chloride and polyvinylidene chloride. Copolymers can also be stabilized by the compound of the present invention. Representative copolymers include ethylene/propylene copolymers, butadiene/styrene copolymers, ethylene/vinyl acetate copolymers, and ethylene/ethyl acrylate copolymers. Copolymers also include terpolymers such as ethylene/propylene/non-conjugated diene terpolymers and acrylonitrile/butadiene/styrene interpolymers. Polymer blends such as polystyrene/polyphenylene oxide and ethylene propylene copolymer or terpolymer with polypropylene can also be stabilized by the compound of the present invention. Other materials stabilized by the compound of the present invention include hot melt adhesives such as those based on polyesters, polyamides or ethylene/vinyl acetate. Also stabilized are petroleum products such as fuels, lubricating oils, petrolatum jellies, and natural products such as natural rubber, waxes, fat, tallow, linseed oil, corn oil, cottonseed oil and cod-liver oil. The preceding list is representative, though by no means exhaustive, of the products that can benefit from the compound of the present invention. To achieve protection against oxidative degradation, the compound of the present invention is added in the amounts generally used for known antioxidants which may have similar properties to achieve such protection. Depending on the substrate used, the antioxidant is added in amounts of 0.001 to 10 percent by weight based on the weight of the substrate, with the usual range being from 0.05 to 2.0 percent. The compound of the present invention can be used by itself to stabilize organic materials, or it can be used in combination with other stabilizers. Such other stabilizers might include other pheno lics, thio compounds of various kinds, such as thiodipropionate esters, phosphites and phosphonates, ultraviolet stabilizers of various kinds as well as other additives where the use of such additives has been found bèneficial. The following non-limiting examples further illustrate the use of the invention. Example 1 Preparation of high melting N,N'-bis-2-[3(315-di-tert.-butyl- 4-hydroxyphenyl )propionyloxy] ethyl oxamide A 25 g. sample of N,N1-bis-2-[3(3,5-di-tert. -butyl-4-hydroxy- phettyl)propionyloxy3 ethyl oxamide (melting at 128 - 1310C) was dissolved in 200 ml of a 50% ethyl acetate/50% hexane mixture and passed through a 6 inch x 2 inch column packed with Davison Chemical grade 62 silica gel. On evaporation of the eluent, the residue was crystallized from ethanol. It gave a material melting at 177 - 1780C. All but 6 g. of the sample was recovered. Example 2 Comparison of volatility of low and high melting N,N'-bis-2-[3 (3,5-di-tert.-butyl-4-hydroxyphenyl )propionyloxy 3 ethyl oxamide Thermograms on 10.6 mg samples of the pure (melting at 177 1780 C) high melting product and the pure (melting at 136 - 1380C) low melting product were run in air at a heating rate of 100C/ minute. The low melter had lost 62% of its initial weight by the time a temperature of 300"C was reached, but the high melting species of this invention had lost only 18% in the same period. Example 3 This example shows the usefulness of the compound of the present invention as a stabilizer in polypropylene. The compound, was incorporated into Profax 6501 (trademark of Hercules Inc. for polypropylene) at a concentration of 0.1% by weight, based on the weight of the poly- pr & y-lene, on a Banbury mill at 1650C. Seventy five mil (1.9mm) thick plaques were prepared by compression molding in a press at 27,000 psig (186 MPa) and 1770 C. One inch diameter buttons were punched from the plaques and the specimens were placed in a forced air oven at 1490C and the number of days to embrittlement was noted. When two out of three buttons embrittied, the specimen was considered to have failed. The compound of the present invention protected polypropylene for 51 days. Unprotected polypropylene embrittles in one day.

Claims: CLAIMS: 1. N,N -BIS-(2-(3-(3,5-DI-TERT.-BUTYL-4- HYDROXYPHENYL)PROPINYLOXY)ETHYL)OXAMIDE characterised in that it has a melting point of about 1780C. 2. A method of making- N,N -BIS-(2-(3-(3,5- DI-TERT.-BUTYL-4- HYDROXYPHENYL) PROPIONYLOXY) ETHYL) OXAMIDE characterised by recrystaflising the crude or pure low melting point form from a solvent. 3. A method as claimed in claim 2 in which the solvent is ethanol, isopropanol or acetone. 4. A method as claimed in either or claims 2 or 3 in which the recrystallisation is initiated by seeding the solution with crystals of the higher melting species. 5. A method as claimed in claim 4 in which the seed crystals are prepared by column chromatography or by slow crystallisation. 6. A polymeric composition comprising a polymeric compound and N,N1-BIS-(2- (3- (3,5-DI-TERT.-BUTYL-4- HYDROXYPHENYL) PROPIONYLOXY) ETHYL) OXAMIDE having a melting point of about 1780C. 7. A composition according to claim 6 in which the N,N1-BIS- (2- (3- (3 ,5-DI-TERT.-BUTYL-4- HYDROXYPHENYL) PROPIONYLOXY)ETHYL)OXAMIDE is present in an amourtof 0.001 to 10% by weight based on the weight of the polymeric compound. 8. A composition as claimed in claim 7 in whch the N,N -BIS-(2-(3-(3,5-DI-TERT.-BUTYL-4- HYDROXYPHENYL)PROPIONYLOXY)ETHYL)OXAMIDE is present in the range of from .05 to 2% by weight. 9. A composition as claimed in any of claims 6 to 8 in which the polymeric compound is a polyolefin. 10. A composition as claimed in claim 9 in which the polyolefin is polyethyelene or polypropylene. 11. A composition according to any of claims 6 to 10 in which N,N1-BIS(2-(3-(3,5-DI-TERT.- BUTYL-4-HYDROXYPHENYL)PROPIONYLOXY)ETHYL)OXAMIDE is used in combination with another stabilise-r selected from phenolic stabilisers, thio-compounds, phospbites, phosphonates, and ultra-violet stabilisers.

Inventors: JANCIS, ELMAR HARRY
Applicants: UNIROYAL, INC.
Application year: 1980
Main classification: C07C102
IPC codes: C08L23, C08K5, C07C233, C08L101, C07C231, C07C67