INFORMATION CARRYING DISCS

Abstract: Information carrying discs, such as video discs, tend to be damaged by marking, abrading and grease or solvent. It has been found that transparent polymeric compositions having a specified resistance to abrasion may be used in the formation of information carrying discs.

Description: INFORMATION CARRYING DISCS Field of the Invention The present invention relates to information carrying systems and more particularly to discs which carry light readable or stylus readable information. These discs may be useful in carrying information which is convertible to electronic signals for such varied uses as sound recordings, audio/visual recordings, or even computer type information retrieval. Background of the Invention Information retrieval in the form of discs having information distributed in a circular or spiral pattern has been available in various forms for many years. Early forms of musical reproduction equipment, for example, used discs with either holes or protuberances to pluck an array of strings or vibrating posts to produce music. Early displays of moving pictures operated by rotation of a disc bearing consecutive images on the periphery. The most common form of storing reproductions of musical performances, which has been in use for about one hundred years, is the phonograph record which uses a spiral pattern of grooves having vertical and horizontal modulations to generate signals which can be converted to sound. With the introduction of the laser to industry, a new information storage system was developed which comprised a disc having a circular or spiral pattern of depressions or protuberances which would disturb, reflect, or refract incident light patterns. These information storing discs, often used for storage of audio/visual information and generally referred to as video discs, are well known in the art. Such U.S. Patents as 3,658,954; 3,795,534; 3,798,134; 3,855,426; 3,901,994; 4,124,672; 4,126,716; and 4,130,620 show various constructions, compositions, and processes for forming video discs. In addition to the laser readable video disc, another commercial construction is used which is more similar to the classic phonograph recording. This type o construction, as described in RCA Review, Vol. 39, "No. 1, March 1978, comprises a spiral array of grooves which is tracked by a stylus. The grooves are impressed with code information in the form of vertical and/or radial modulations. Even though these systems are read by totally different techniques, they are affected by similar, if no identical, problems. Imperfections in the depressions, protuberances, or modulations cause undesirable or spurious signals to be generated. The imperfections can be produced during manufacture of the disc or can develop from wear during use or manipulation of the disc. The present* invention relates to information storage discs for use with laser or stylus readout systems which have good fidelity, solvent and grease resistance, and resistance to wear. Summary of the Invention It has been found according to the present invention that information storage devices comprising dis blanks or discs having a circular or spiral pattern of depressions, protuberances, and/or grooves with or withou modulations can be constructed from a substrate, having as the information bearing layer on at least one surface thereof, an abrasion resistant layer formed from a composition which displays less than 25% haze when subjected to A.S.T.M. test D-1044-76, Resistance of Transparent Plastic Materials to Abrasion. These compositions are preferably comprised of from 30-100% by weight of an epoxy-terminated silane or comprised of 15-100% by weight of a polyacryloyl containing heterocyclic compound. A haze value of less than 20% is more preferred, and less than 15% is most preferred. Epoxy-ter inated silanes are known in the art as represented by U.S. Patents 3,955,035; 4,049,861;. 4,069,368; 4,101,513; and others, where the epoxy- terminated silanes are disclosed as useful in forming smooth, transparent abrasion resistant coatings. These materials may be described by the formulae: H 2 C / - 0N *CH - (R- m - Si(OR 2 ) 3 and wherein R*** is a non-hydrolyzable divalent hydro¬ carbon group (aliphatic, aromatic or aliphatic and aromatic containing) of less than 20 carbon atoms or a divalent group having less than 20 carbon atoms composed of C, H, S, N, and O .atoms as the only atoms which may appear in the backbone of the divalent group, the O atoms appearing as ether linkages if present, and with no two adjacent heteroatoms in the divalent group. This description is the definition of non-hydrolyzable divalent group for R-***; R 2 is an aliphatic group of less than 10 carbon atoms or an acyl group of less than 10 carbon atoms; and m is 0 or 1. The group R-*- is preferably alkylene of from 1 to 8 carbon atoms and most preferably is represented by the formula: (CH 2 ) n(0)p ( CH 2 )g wherein n is 1 to 4, and most preferably 1, p is 0 or 1 and most preferably 1, g is 1 to 6 and most preferably 3. The group R 2 is preferably alkyl of 1 to 6 carbon atoms, more preferably alkyl of 1 to 3 carbon atoms, and most preferably methyl. In the practice of the present invention, the epoxy-ter inated silanes may be formed into the high density information storage layers from monomers, hydrolyzates, or precondensates of these compounds. The formation of these hydrolyzates and precondensates is thoroughly described in U.S. Patents 4,049,861 and 4,100,134. The compositions used in making the information storage layer for the discs of the present invention include from 30-100% by weight of the epoxy-terminated silane. That is, the information carrying layer is the crosslinked product of the epoxy-terminated silane in combination with from 0-70% by weight of a copolymerizable material. Such copolymerizable materials include styrene, _ methyl styrene, vinyl amides, vinyl ethers, epoxy resins, polyols, silanes and other materials known to be copoly- erizable with either epoxy resins or silanes. The most preferred comonomers are epoxy compounds. These may generally be described by the formula: wherein R--* is an aliphatic or cycloaliphatic group, r is the valence of R 3 and is an integer of from 2 to 6, a and b are H, or when fused together, represent the atoms necessary to form a 5- or 6-membered cycloaliphatic ring. Preferably said epoxy resin, upon homopolymerization, forms a polymer having a glass transition temperature below +25°C and has a molecular weight of at least 100 per epoxy group. Preferred compounds are the diglycidyl ether of bisphenol A, 3,4-epoxycyclohexylmeth l-3,4-epoxy-cyclohexane-carboxylat l,4-bis(2,3-eρoxypropoxy)butane, limonene dioxide, and limonene oxide. The polyacryloyl containing heterocyclics are defined according to the present invention as materials described by the formulae: 1) A^-Z-A 2 wherein A**- and A 2 independently are alkoxyalkyl groups having terminal ethylenic unsaturation and having the formula wherein R-O- is a monovalent residue of an aliphatic terminally unsaturated primary alcohol, ROH, formed by the removal of the active hydrogen from the primary -OH group, R having the formula: wherein E is c is an integer of f om 1 to 6, b is zero or an integer of from 1 to 6, R-*- and ^ are independently selected from hydrogen and methyl, R-*-' is an aliphatic group having from 1 to 15 carbon atoms, and no more than two non-adjacent catenary oxygen or carboxy groups, a valence of m + 1, m is an integer of from 1 to 5, R 2 is selected from hydrogen and groups of the formula 0 -C-R b or 0 -C-NHR 7 wherein R- is selected from alkyl and alkenyl groups 7 is an aliphatic or aromatic group of up to eight carbon atoms, - is an alkylene group of from 1 to 6 carbon atoms with up to one catenary oxygen atom, and Z is a heterocyclic group of the formula - - C=0 / -N ^ C" II o wherein X is a divalent group which is required to complete a 5- or 6-membered heterocyclic ring, or where represent hydrogen or methyl, R**-^ represents hydrogen, an alkyl group, or a phenyl group, R-*- 3 and R**-^ together may represent a trimethylene or tetramethylene group, . m represents a number of from 1 to 30, n is 2 or 3, and A represents a group of the formula χi- C=0 I I -N .N- I! 0 wherein X-*- represents the divalent radical necessary to complete a 5- or 6-membered heterocyclic ring group. The preferred classes of these materials are a) from formula 1) : wherein X is selected from R 8 0 O R 8 R 8 R 9 R 8 R 10 0 A 3 f ϋ I' I I I I i |l I -C- , -C- , -C-C- , -C=C- , -C-C- , and -C-N- R9 R9 R9 R11 wherein R 8 , R* 3 , IO and R-*--*- are independently hydrogen, alkyl group of 1 to 4 carbon atoms, cycloalkyl group of 3 to 6 carbon atoms, and aryl group (e.g., phenyl group) of 6 to 12 carbon atoms, and A 3 is an alkoxyalkyl group as defined for A**- and A 2 , and b) from formula 2): wherein m is from 1 to 4, and X-*- is selected from 0 R 15 0 R!5 R15R16 R15 R 17 0 R-*- 9 !l I II I I I I j II I -C- , -C- , -C-C- , -C C- , -C C- , and -C-N- Rl6 ^16 ^16^18 wherein R 15 , R 16 , R 17 and R 18 independently represent hydrogen, an alkyl group, an alkylene group, a cycloalkyl group, or a phenyl group, and R 19 represents hydrogen, an aliphatic group, or an aromatic group. It is more preferred, with regard to the preferred compounds of formula 1) that R 2 be hydrogen, that X be R 8 I -C- l> and R 8 and R 9 be hydrogen or alkyl of 1 to 4 carbon atoms, that m be 2 to 5, that R be [ (CH 2 ) b ] m R 5 (CH2) C that R- 5 be alkylene of 1 to 15 carbon atoms, and/or that R 4 be hydrogen. It is more preferred"with regard to formula 2) that X 1 be selected from - and that R 15 , R-*- 6 , R 17 , and R 18 be independently selected from hydrogen, alkyl of 1 to 4 carbon atoms, alkylene of 1 to 4 carbon atoms and phenyl. Most preferably RIS-R-** 8 are selected from hydrogen and alkyl of 1 to 4 carbon atoms. As noted above, the information bearing layer of the disc blanks or discs of the present invention must be formed from a polymeric resin derived from a composition comprising at least 15% by weight of the polyacryloyl heterocyclics. The heterocyclics may of course constitute 100% by weight of reactive or polymeric components in the resin. The compositions used in the process of the present invention may be diluted with up to 85% by weight of any ethylenically unsaturated monomer. Preferably the majority of co onomers are at least diethylenically unsaturated monomers. Generic classes include the acrylates, methacrylates, acrylic anhydrides, ethylenically unsaturated anhydrides, olefinic compounds, acrylamides, ethylenically unsaturated amides and urethanes, vinyl esters, vinyl ethers, vinyl halides, vinyl epoxy resins, vinyl silanes and siloxanes, vinyl heterocyclics, and prepolymers and polymers of these materials. Particularly suitable ethylenically unsaturated monomers include methyl methacr late, ethyl acrylate, 2-ethylhexyl acrylate, cyclohexyl acrylate, styrene, butadiene, 2-chlorostyrene, 2,4-dichlorostyrene, acrylic acid, acrylamide, acrylonitriles, t-butyl acrylate, methyl acrylate, butyl acrylate, N-vinyl pyrrolidone, 2-(N-butylcarbamyl)ethyl methacrylate and 2-(N-butyl-carbamyl)ethyl methacrylate, and 2-(N-eth l- carba yl)ethyl methacrylate. Preferably 35 to 80% and most preferably 45 to 60% by weight of copolymerizable components comprise the heterocyclic agents of the present invention. Other diluting monomers that can be incorporated into the composition of the invention include 1,4-butylene dimethacrylate or acrylate, ethylene dimethacrylate, hexamethylene diacrylate (hexanediol diacrylate) or dimethacrylate, glyceryl diacrylate or methacrylate, glyceryl triacrylate or trimethacrylate, pentaerythritol triacrylate or trimethacrylate, pentaerythritol tetraacrylate or tetramethacrylate, diallyl phthalate, dipentaerythritol pentaacrylate, neopentylglycol triacrylate and l,3,5-tri(2-methacryloxy- ethyl)-_s-triazine. The compositions should also contain polymeriza- tion or free radical initiators in order to provide more photosensitivity to the system to speed up the cure. Polymerization initiators suitable for use in the composi¬ tions of the invention are compounds which liberate or generate a free-radical on addition of energy. Such initiators include peroxy, azo, and redox systems each of which are well known and are described frequently in polymerization art, e.g. Chapter II of Photochemistry, by Calvert and Pitts, John Wiley and Sons (1966). Included among free-radical catalysts are the conventional heat activated catalysts such as organic peroxides and organic hydroperoxides; examples are benzoyl peroxide, tertiary- butyl perbenzoate, cumene hydroperoxide, azobis(isobuty- ronitrile) and the like. The preferred initiators are photopolymerization initiators which facilitate polymeriza¬ tion when the composition is irradiated. Included among such initiators are ac loin and derivatives thereof, such as benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isoprσpyl ether, benzoin isobutyl ether, and α-methylbenzoin; diketones such as benzil and diacetyl, etc.; organic sulfides such as diphenyl monosulfide, diphenyl disulfide, decyl phenyl sulfide, and tetramethylthiuram monosulfide; S-acyl dithiocarbamates, such as S-benzoyl- N,N-dimethyldithiocarbamate; phenones such as acetophenone, α,α,α-tribromoacetophenone, α,α-diethoxyacetophenone, 2,2-dimethoxy-2-phenyl- acetophenone, o-nitro-α,α f α-tribomacetophenone benzophenone, and p,p'-tetramethyldiaminobenzophenone; aromatic iodonium and aromatic sulfonium salts; sulfonyl halides such as p-toluenesulfonyl chloride, 1-naphthalene- sulfonyl chloride, 2-naρhthalenesulfonyl chloride, 1-3- benzenedisulfonyl chloride, 2,4-dinitrobenzenesulfonyl bromide and p-acetamido-benzenesulfonyl chloride. Normally the initiator is used in amounts ranging from about 0.01 to 5% by weight of the total polymerizable composition. When the quantity is less than 0.01% by weight, the polymerization rate becomes extremely low. If the initiator is used in excess of 5% by weight, no correspondingly improved effect can be expected. The structure of the information carrying discs of the present invention comprises a substrate having the information impressed or blank groove impressed epoxy- terminated silane coating layer on at least one side thereof. The substrate may be substantially any solid material, including but not limited to polymeric materials such as polycarbonates, polyesters, polyacrylates, polyurethanes, polyolefins, polyvinyl resins, polyamides, and polysiloxanes; ceramic or glass materials; fibrous materials; metals; etc. The surface of the substrate to 5 be coated should itself be smooth. It would not be desirable to have surface irregularities having dimensions in excess of 2 μ . The backing may be transparent or opaque depending upon the readout system used. If the backing is opaque, a master transparent to the curing 0 radiation must be used. Primer layers may be used between the substrate and the • information carrying layer, but this is not essential depending upon the ability of the coating to adhere to the base. On polyesters, for example, polyvinylidene chloride is a useful primer. The substrate 5 may be of any thickness, but is usually from 50 to 5000 ym. The information carrying layer is critical in its dimensions and must be between 1.0 and 25 m in its maximum thickness for a video disc and up to 100 ym for an audio disc. The term maximum thickness is used, because 20 the layer, having depressions, protuberances, or grooves thereon, varies in thickness. This limit therefore applies to the maximum thickness of the layer above the substrate. Preferably it is between 2.0 and 20 ym in maximum thickness and most preferably between 3.0 and 25 10 ym for a video disc. The preferred dimensions are between 15 and 75 ym for an audio disc. The information is encoded on the information carrying layer as depressions, protuberances, and/or grooves with or without modulations in either a circular, 30 arc-like (e.g., semicircular, hyperbolic, etc., or spiral pattern on the layer. The depth or height of the information carrying deformity from the plane of the surface or the mean height of the surface is normally between 0.03 to 2 ym. In laser readout systems, this 35 dimension is usually between 0.03 and 1.5 ym, preferably between 0.05 and 0.8 ym, and more preferably between 0.07 and 0.5 ym. In stylus readout systems, this dimension is US- usually between 0.05 and 2 ym, preferably between 0.08 and 1.5 ym, and more preferably between 0.10 and 1.0 y . For an LP record, this dimension is preferably between 25 and 75 ym. The width (peak to peak) between grooves in audio systems is about 60-80 ym. The light read systems may have a metallized coating over the information carrying surface and another polymer layer, preferably of an abrasion resistant material, over the metal layer, if a reflective rather than transmissive readout system is being used. These coatings can be laid by a variety of manners including vapor deposition or reduction of metal salt solutions. Alternatively, two reflectively metallized discs may be adhesively secured together so that the two information bearing surfaces are sandwiched in the middle of the composite and information is then read reflectively through a transparent substrate. ' Capacitively read discs may have a metallized coating applied to the replicated information bearing surface to provide electrical conductivity. The metallized coating may then be provided with an electric¬ ally insulative overlayer. Replicas to be read with a stylus may also use a lubricant or lubricating layer on the information bearing surface to minimize stylus wear. Preferably the information is encoded into the information carrying layer in a spiral pattern rather than a circular pattern so that the reading element can follow a single path rather than having to shift from one concentric circle to another. If the information carrying layer is to be penetrated by light during readout, it must be trans- missive of the reading radiation. Ordinarily a fairly narrow band of radiation is used to read the discs so that the information carrying layer may have to be transmissive of at least 50% of the radiation in a 100 nm, 50 nm, or even 30* nm band. Preferably the layer is transmissive of at least 75 to 90% of the radiation within such a band. The composition of the information carrying layer may include various materials which may improve or not adversely affect the properties of the layer. For example, the use of alkoxy substituted metals in epoxy- terminated silanes such as disclosed in column 5, lines 36-59 of U.S. Patent 4,049,861 will improve the conduc¬ tivity of the layer and reduce static charge buildup. Polymeric additives such as those disclosed for epoxy- terminated silanes in U.S. Patents 3,955,035 and 4,082,846 may be useful. Flow control aids and surfactants, as are well known in the art, could be added to compositions of the present invention. Dyes could be added to the compositions which would be transmissive of the radiation used to read the encoded information. There will also, of course, be a residue or an unchanged amount of catalyst or delatentized catalyst in the composition. A broad range of catalysts has been found useful, but with some more preferred than others. U.S. Patent No. 3,955,035 broadly disclosed the use of Lewis or Bronstad acids for curing epoxy silanes, U.S. Patent No. 4,049,861 discloses highly fluorinated aliphatic sulfonic or sulfonylic acids as catalysts for these materials, U.S. Patent No. 4,101,513 discloses light sensitive polyaromatic onium catalysts, some of which are particularly useful for curing materials according to the present invention, and U.S. Patent No. 4,130,690 shows a class of Lewis acid catalysts of high efficiency for curing epoxy-terminated silanes. The more preferred catalysts are the highly fluorinated aliphatic sulfonylic catalysts, the high efficiency Lewis acid catalysts (PFg, SbFg and HSbFs) and the complex polyaromatic sulfonium and iodonium salts (i.e., those having BF4~ , PFg" , SbFg" , SbF5 ~ OH and ArFg" as anions). One important aspect of the present invention is that the low applied pressures and low temperatures associated with the use of liquid compositions allows for the use of non-metallic stampers and masters. These and other aspects of the present invention will be shown in the following examples. 5 Example 1 A highly hydrolyzed precondensate of γ-glycidoxy- propyltrimethoxy silane (about 80-90% of methoxy groups removed) (70 gm) was mixed with 30 gm of 1,4-diglycidoxyl- butane and 2 gm of triarylsulfonium hexafluoro-antimonate 0 photocatalyst (described in assignee's U.S. Patent No. 4,173,476) by shaking for 3 hours. Bubbles were then removed from the mixture by placing it in an evacuated chamber for 15 minutes. The resulting photopolymerizable material was used to make a video disc replica according 5 to the following roll coating process. A nickel video disc stamper was utilized. Approximately 2.0 cm 3 of the material prepared as described above was spread by a cylindrical coating roller between a video disc stamper and a primed 0.18 mm 0 polyester film. The sheet of 0.18 mm thick polyester film was positioned between the stamper and the roller to serve as a base element. This rolling process spread out a bubble free coating of resin composition over the surface of the stamper and simultaneously covered it with the 25 polyester sheet. The stamper covered in this manner was then passed at 3 cm/sec under a 200 watt/inch high intensity medium pressure Hg vapor lamp. The UV exposure cured and hardened the resin composition. After this exposure, the laminated structure containing the repli- ■30 cated information was easily peeled from the nickel stamper. The sheet was then cut to produce a circular center hole and a circular outside edge, both concentric with the replicated information tracks. The resulting video disc replica had an -35 information bearing layer which was approximately 10 t 5 ym thick which did not curl when layed on a flat surface. It retained this flatness after more than one year under ambient conditions and produced a good television picture when played on a commercial video disc player. A haze value of less than 20% was obtained according to A.S.T.M. D-1044-76. Example 2 A video disc replica was made as in Example 1. However, the resin composition used was made by mixing 90 gm of the precondensate of Example 1 with 10 gm of the diglycidyl ether of 1,4-butanediol and 2 gm of the photocatalyst of Example 1. The video disc replica made by this process has an information bearing layer which was 8 i 5 ym thick. The replica was initially flat, but in three months, developed a curl which then made it unsuit- able for playing on a video disc player. It has been found that it is desirable to have increasingly thinner coating layers and, to some degree, thicker substrates, as higher percentages of epoxy-terminated silane are used. The disc of this example was highly abrasion resistant and initially produced an excellent video image upon being played. Example 3 A video disc replica was made as in Example 1 with the following changes. The resin composition was made by mixing 50 gm of the precondensate, 50 gm of the diepoxide of Example 1 and 2 gm of the photocatalyst. The resulting disc replica had a cured information bearing layer which was 7 t 3 ym thick. This replica did not curl when laid on a flat surface. It retained its flatness even after a one month period of time. The replica produced a good television picture when played on a video disc player. Example 4 A video disc replica was again made as in Example 1, however, the resin composition was a mixture of 100 gm of the precondensate of Example 1 and 2 gm of the photocatalyst. The resulting video disc had an informa¬ tion bearing layer which is 14 ± 4 ym thick. It was initially flat, but upon standing for three months, it developed a curl which then made it unsuitable for playing on a video disc player. Example 5 A resin composition was made by mixing 70 gm of a 50 to 60% hydrolyzed precondensate of γ-glycidoxypropyl- tri ethoxy silane with 30 gm of the diepoxide of Example 1 and 2 gm of the photocatalyst of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1. The video disc replica made in this way had a cured information bearing layer .7 1 3 ym thick. This disc lay flat when placed on a level surface. It maintained its flatness after aging under normal room conditions for three months. It provided a good tele¬ vision picture when played on a video disc player. Example 6 A video disc replica was made as in Example 5. However, the resin composition was made by mixing 50 gm of the precondensate of Example 5, 50 gm of the same diepoxide of Example 1 and 2 gm of the photocatalyst of. Example 1. The resulting disc replica had an information bearing layer thickness of 7.5 t 2.5 ym. It lay flat when placed on a level surface and maintained this flatness after aging at normal room conditions for three months. It produced a -good television picture when used with a video disc player. C 'Jl Example 7 A video disc replica was made as in Example 5. However, the resin composition was made by mixing 30 gm of the precondensate of Example 5, 70 gm of the diepoxide of Example 1, and 2 gm of the photocatalyst of Example 1. The resulting replica had an information bearing layer with a thickness of 3 i 2 ym. Both before and after aging three months under normal room conditions, this disc lay flat when placed on a level surface. It produced a good television picture when used with a video disc player. Example 8 A video disc replica was made according to the procedure of Example 1. The resin composition was made by mixing 100 gm of the precondensate of Example 5 with 2 gm of the photocatalyst of Example 1. The resulting replica had an information bearing layer which was 6.5 1 1.5 ym thick. When first made, this disc lay flat when placed on a level surface. However, after aging under normal room conditions for three months, it curled up when placed on such a surface and was then not suitable for playing on a video disc player. Example 9 A video disc replica was made according to the procedure of Example 1. The resin composition used was a mixture of 90 gm of the precondensate of Example 5, 10 gm of the diglycidyl ether of 1,4-butanediol and 2 gm of the photocatalyst of Example 1. The resulting disc had an information bearing layer with a thickness of 6.5 1 1.5 ym. When first made, the disc lay flat when placed on a level surface. However, after aging for three months under normal room conditions, the disc curled up when placed on such a surface and was then not suitable for use on a video disc player. c_*: Examples 10-14 Video disc replicas were made according to the procedure of Example 1. The resin composition was a mixture of γ-glycidoxypropyltrimethoxysilane, the diglycidyl ether of 1,4-butanediol and the catalyst of Example 1. The amount of each component used for the corresponding example is shown below. Table 1 Epoxy-silane Diepoxide Ϊ Photocatalyst Thickness Ex. (gm) (gm) (gm) (y ) 10 100 0 2 4-6 11 90 10 2 3-5 12 70 30 2 5-13 13 50 50 2 2-6 14 30 70 2 8-14 All of these discs lay flat when placed on a level surface both before and after aging for three months under normal room conditions. They all provided a very good television picture when used with a commercial video disc player with the exceptions of Examples 10, 11 and 12 which were acceptable, but in which the signal level was slightly low. Examples 15-22 A series of discs were made according to the procedure of Example 1. The hydrolyzable silane or precondensate thereof and the amount of diglycidyl ether of 1,4-butanediol in the resin composition are shown below. These discs were then cured by placing them for 7 minutes under a bank of low intensity "black lights." All these discs were flat and produced a good television picture when first produced. Examples 15-18 were then aged for 71-1/2 hours at 55°C, 16% R.H. All discs retained their flatness in this aging. Exa ples 19-22 were aged 71-1/2 hours at 50°C, 85% R.H. None of the discs curled appreciably when subjected to this environment. However, because of the low levels of epoxy-terminated silane (ETS), Examples 15-22 were not abrasion resistant. TABLE 2 % Methoxy ETS Diepoxide Photocatalyst Thickness Groups Ex. Removed (gm) (gm) (gm) (ym) 15 0 100 2 8-15 16 0 10 90 2 3-10 17 50 10 90 2 3-10 18 90 10 90 2 3-8 19 - 0 100 2 3-13 20 0 10 90 2 3-14 21 50 10 90 2 3-15 22 90 10 90 2 3-10 Exampl<as 23- -30 A series of discs was made according to the procedure of Example 1. The hydrolyzable silane or precondensate thereof and the components of resin composition are shown below. All of these discs were adequately flat immediately after preparation. However, after aging 74 hours at 55°C, 17% R.H. , the disc of Example 28 had developed an excessive curl. When these discs were further aged for 88 hours at 50°C and 85% R.H., the discs of Examples 23, 24 and 27 also developed excessive curl. These results and the results of Example 15-22 tend to indicate that adding a flexibilizer helps t maintain disc flatness. - It is also important to note tha the discs with thick information bearing layers curled more than those with thin coatings. C - Table 3 % Methoxy ETS Diepoxide Photocatalyst Thickness Groups Ex. Removed (gm) (gm) (gm) (um) 23 0 100 0 2 0-8 24 0 100 0 2 5-18 25 0 50 50 2 8-18 26 0 50 50 2 8-23 27 90 100 0 2 8-11 28 90 100 0 2 13-25 29 90 50 50 2 5-13 30 90 50 50 2 8-18 Example 31 A resin composition was made by mixing 50 gm of the precondensate of Example 1 with 50 gm of the diepoxide of Example 1, 2 gm diphenyliodonium hexafluorophosphate and 0.4 gm 2-ethyl-9,10-dimethoxyanthracene. The resulting material was used to make a video disc according to the procedure of Example 1 except that the resin was cured under a bank of low intensity "black lights" for 7 minutes. The video disc replica made in this way had a cured information bearing layer 7.5 i 2.5 ym thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player. A haze value of less than 25% was obtained according to A.S.T.M. D-1044-76. Example 32 A resin composition was made by mixing 50 gm of the precondensate of Example 5 with 50 gm of the diepoxide of Example 1, 2 gm diphenyliodonium hexafluorophosphate and 0.4 g 2-ethyl-9,10-dimethoxyanthracene. The resulting material was used to make a video disc according to the procedure of Example 1 except that the resin was cured under a bank of low intensity "black lights" for 7 Til ' A^ c:π minutes. The video disc replica made in this way had a cured information bearing layer 7.5+ 2.5 ym thick. This disc lay flat when placed on a level surface. It provide a good television picture when played on a video disc player. Example 33 A sample of commercially available PVC film 14 inches square was prepared for use as a video disc substrate in the following two steps. In the first step, the sheet was placed between two flat, smooth chrome-stee plates. The plates were in turn sandwiched between four layers of cardboard and the resultant stack pressed for 1 minutes in a hydraulic press. The press was operated wit a force of 114 metric tons, and the press platens were held at a temperature of 160°C. The pressing operation reduced the surface roughness present on the manufactured film and provided suitable flatness. In the second step, in order to promote adhesio of the photopolymerizable material to the PVC substrate, the substrate was next placed in a Vecco Model 776 radio frequency diode sputtering apparatus operating at a frequency of 13.56 MHz. The substrate was then subjected to a radio frequency sputter etch as disclosed in assignee's copending application S.N. 80,530 (filed 10 October 1979). The substrate thus prepared was used to make a video disc replica according to the procedure and composition of Example 1. The resulting video disc showed good adhesion of the cured polymer layer to the PVC substrate. The disc lay flat when placed on a level surface. It retained this flatness after aging for 7 months under normal room conditions. The disc produced a good television picture when played on a video disc player. Information could be read from this disc with the laser beam incident from either side of the disc. Exa ple 34 A sheet of cast acrylic material (poly ethyl- methacrylate) 1 mm thick was sputter-etched according to the procedure of Example 33 in order to promote adhesion of the photopoly er. The resin composition of Example 1 was used. The roll-coating technique of Example 1 was used, but the semi-flexible base element was allowed to bend slightly when it was simply lowered slowly onto the stamper as the roller moved along. The resin composition was cured with a bank of low intensity UV lamps, and the replica stripped from the stamper. An aluminum coating 30 nm thick was vapor coated on the surface of the information bearing layer. A circular hole was cut in the center of the disc, and a circular outer edge was cut. The resulting disc was then placed on a commercial video disc player. The laser beam was incident through the uncoated acrylic surface. A good television picture was obtained. The following Table 4 is presented to show at a glance the preferred compositions for producing a video disc article according to this invention. Table 4 Epoxy-Terminated Diepox- Silane Monomer ide Photocatalyst Thickness Ex. (gm) (gm) (gm) (ym) Remarks 10 100 0 2 4-6 Signal level sαnewhat low 11 90 10 2 3-5 π 12 70 30 2 5-13 π 13 50 50 2 4-6 14 30 70 2 8-14 16 10 90 2 3-10 20 10 90 2 3-14 23 100 0-8 Curls upon aging 24 100 0 2 5-18 n 25 50 50 2 8-18 26 50 50 2 8-23 31 50 50 2 8-30 - - Epoxy-Terminated Diepox- Silane Monomer ide Photocatalyst Ωickness EX. (gm) (gm) (gm) (ym) Remarks % Methoxy Precon Group densate Removed (gm) 50 100 5-8 Curls upon aging 9 50 90 10 2 5-8 It 5 50 70 30 2 4-10 6 50 50 50 2 5-10 7 50 30 70 2 1-5 17 50 10 90 2 3-10 21 50 10 90 2 3-15 32 60 50 50 2 8-23 27 90 100 0 8-11 Curls upon aging 28 90 100 0 2 13-25 It 4 90 100 0 2 10-18 π 2 90 90 10 2 3-13 II 1 90 70 30 2 5-15 3 90 50 50 2 4-10 29 90 50 50 2 5-13 30 90 50 50 2 8-18 18 90 10 90 2 3-8 22 90 10 90 2 3-10 33(PVC)90 70 30 2 34(PMMA) 100 70 30 2 15 0 100 2 8-15 19 0 100 2 3-13 Table 4 thus helps to illustrate that, for the base elements chosen and thicknesses of information bearing layers produced, in order to avoid curl with hydrolyzed monomer and low signal level with non- hydrolyzed monomer, at least about 30% by weight of comonomer flexibilizing material is preferred. It is als useful to observe where the information bearing layer begins to lose its abrasion resistance. Thus, for substantial abrasion resistance, it appears desirable to use less than about 70 percent by weight of comonomer flexibilizing agent. Example 35 A video recording was made in a commercially available polymeric photoresist layer which was developed by standard wash-development techniques after exposure. The recording was then vapor coated with 10 nm of chrome. The resulting photoresist master was used in place of a - nickel stamper to make a video disc replica according to the procedures of Example 1. This replica was playable. When vapor coated with 10mm of chrome and used in place o a nickel stamper, repeated playable replications were made. Example 36 An audio record replica was prepared using commercially available 1 mm polyvinylchloride as the base element. The resin composition of Example 3 was used wit the roll-coating technique of Example 1. The semi- flexible base element was allowed to bend slightly as it was lowered slowly onto the audio record stamper as the roller moved along. The resin composition was cured with a bank of low intensity UV lamps, and the replica strippe from the stamper. A circular hole was cut in the center of the record and a circular outer edge was cut. The resulting replica had an information bearing layer approximately 50 ym thick. The audio record replica was successfully played on a conventional stereo audio system. It has been found that the quality of signal replication, as measured by the level of the radio frequency (RF) signal obtained on playback, is improved by prehydrolyzing the epoxy-terminated silane. Evidence for this is shown in Table 5. Table 5 lists the RF signal level obtained when replicas of Examples 2 to 14 were played on the same player. All of the replicas were made from the same stamper. In this table, the examples are grouped according to the amount of diepoxide in the formulation. It can be seen that, for a given amount of diepoxide, the signal level increases with increasing prehydrolysis of the epoxy-terminated silane. For this reason at least 30% removal of alkoxy groups is preferred. Table 5 t. % % Methoxy RF Signal Example Diepoxide Groups Prehydrolyzed Level,mV 8 0 50-60 600 10 0 0 450 2 10 90 675 9 10 50-60 650 5 29 - 50-60 550 12 29 0 525 3 49 90 575 6 49 50-60 550 13 49 0 500 7 69 50-60 600 14 69 0 600 ^ E yy Example 37 A resin composition was prepared by mixing 60 gms of 1,3-bis 3-[2,2,2-(triacryloyloxymethyl)ethoxy]-2- hydroxypropyl -5,5-dimethyl-2,4-imidazolidinedione (hereinafter referred to as Compound A) containing about 25% by weight of pentaerythritol tetraacrylate, 40 gms of 1,6-hexanediol diacrylate and 2 gms of 2,2-dimethoxy-2- phenyl-acetophenone. This composition was mixed by shaking and then filtered through a 5ym filter. The resulting photopolymerizable material was used to make a video disc with a nickel video disc stamper. Approximately 2.0 cm 3 of this photopolymerizable liquid material was spread by a cylindrical coating roller between a nickel video disc stamper and a primed 0.18 mm polyester film. The sheet of polyester film was positioned between the roller and the stamper to serve as the base substrate. The rolling process spread out a bubble free coating of photopolymerizable resin over the surface of the stamper and simultaneously covered it with the polyester sheet. The stamper covered in this manner was then passed several times at 3 cm/sec under a 200 watt/inch high intensity, medium pressure Hg vapor lamp. The ultraviolet radiation exposure cured the photo¬ polymerizable liquid, hardening it and bonding it to the primed polyester film. After the exposure, the laminated structure containing the replicated information was easily peeled from the nickel stamper. The sheet was then cut to produce a circular center hole and a circular outside shape, both concentric with the replicated information tracks. The resulting video disc replica had an informa¬ tion bearing layer 10 ± 5 ym thick. The disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player. The surface displayed a haze value of less than 15% when tested according to A.S.T.M. D-1044-76. Example 38 A video recording was made in a comercially available polymeric photoresist layer and the layer developed by standard wash-development techniques after exposure to light. The recording was then vapor coated with 10 nm of chrome. The resulting photoresist master was used in place of a nickel stamper to make a video disc replica according to the procedures of example 1. This replica was capable of producing a good television picture when played on a video disc player and was also useful as a stamper for repeated replications. Example 39 A resin composition was prepared by mixing 70 gm of Compound A with 30 gm of hexanediol diacrylate and 2 gm of the photoinitiator of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1. The video disc replica made in this way had a cured information bearing layer 6 - 2 μm thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player. A haze value of less than 10% was obtained according to A.S.T.M. D-1044-76. Example 40 A resin composition was prepared by mixing 30 gm of Compound A with 70 gm of hexanediol diacrylate and 2 gm of the photoinitiator of Example 1. The resulting material was used to make a video disc according to the procedure of Example 1. The video disc replica made in this way had a cured information bearing layer 5 - 2.5 ym thick. This disc lay flat when placed on a level surface. It provided a good television picture when played on a video disc player. Example 41 A sample of commercially available polyvinyl- chloride film 14 inches square was prepared for use as a video disc substrate in the following way. The sheet was placed between two flat, smooth, chrome-steel plates. The plates were in turn sandwiched between four layers of cardboard and the resulting stack pressed for ten minutes in a hydraulic press. The press was operated with a force of 11 metric tons, and the press platens were heated to 160°C. This pressing operation reduced the surface roughness of the manufactured film and provided a substrate of suitable flatness. The substrate thus prepared was used to make a video disc replica according to the procedure of Example 1, except that the surface of the polyvinylchloride opposite the information bearing layer was also coated with the resin composition. The cured polymer showed good adhesion to the otherwise untreated surface of the polyvinylchloride substrate. The disc lay flat when placed on a level surface and provided a good television picture when played on a video disc player. Information was read from this disc with the laser beam incident from either side of the disc. Example 42 A sheet of cast acrylic material (polymethyl- methacrylate) 1000 ym thick was sputter etched according to the following procedure to promote adhesion of the polymer. The acrylic substrate was placed in a Vecco Model 776 radio frequency diode sputtering apparatus operating at a frequency of 13.56 MHz. The substrate was then subjected to a radio frequency sputter etch as described in assignee's copending application Serial No. 80,530, filed 10 October 1979. The resin composition of Example 1 and the roll coating technique of Example 1 was used to prepare a video disc replica with the above described substrate. The semi-flexible substrate was allowed to bend slightly when it was lowered slowly onto the stamper as the roller moved along. The resin composition was cured with a bank of low intensity UV lamps, and the replica removed from the stamper. An aluminum coating 30 nm thick was vapor coated onto the surface of the information bearing layer. A circular hole was cut in the center of the disc, and a circular outer edge was cut. The resulting disc was then played on a video disc player; a good television picture was obtained. The laser beam of the player was incident through the uncoated acrylic surface and reflected by the aluminum coating on the information bearing surface. Example 43 An audio record replica was prepare using commercially available 1 mm polyvinylchloride as the base element. The resin composition of Example 1 was used within the roll-coating technique of Example 1. The semi-flexible base element was allowed to bend slightly as it was lowered slowly on to the audio record stamper as roller moved along. The resin composition was cured to 75 μm maximum thickness by several passes at 3 cm/sec. under a 200 watt/inch high intensity, medium pressure Hg vapor lamp. The replica was then stripped from the stamper. A circular hole was cut in the center of the record and a circular outer edge was cut. The resulting replica was successfully played on a conventional stereo audio system. -^yv y ir

Claims: CLAIMS : 1. An information carrying element comprising a substrate having adhered to at least one surface thereof a separate layer having a maximum thickness of 1.0 to 100 ym and a circular or spiral pattern of surface variations in the form of depressions, protuberances, and/or grooves with or without modulations, said separate layer comprising an abrasion resistant polymer layer displaying less than 25% haze according to A.S.T.M. D-1044-76. 2. The element of claim 1 wherein said polymer is derived from a composition comprising from 30-100% by weight of an epoxy-terminated silane described by either of the formulae: wherein R 1 is (CH2* "t°^ O ^ CH 2^9 wherein n is 1 to 4, p is 0 or 1, g is 1 to 6, R 2 is alkyl of 1 to 6 carbon atoms and m is O or 1. 3. The element of claim 2 wherein is 1 and p is 1. 4. The element of claim 1 wherein said epoxy- terminated silane is γ-glycidoxypropyltrimethoxy silane. 5. The element of claim 1 wherein said polymer is derived from a composition comprising from 15-100% by weight of a polyacryloyl heterocyclic compound selected from the formulae: 1) A^Z-A 2 1 2 wherein A and A independently are alkoxyalkyl groups having terminal ethylenic unsaturation and having the formula wherein R-O- is a monovalent residue of an aliphatic terminally unsaturated primary alcohol, ROH, formed by the removal of the active hydrogen from the primary -OH group, R having the formula: O II wherein E is CH =C-C-0- c is an integer of f om 1 to 6, R 1 and R4 are independently selected from hydrogen and methyl, 5 R is an aliphatic group having from 1 to 15 carbon atoms, and no more than two catenary oxygen or carboxy groups, a valence of m + 1. is an integer of from 1 to 5, 2 RR 2 is selected from hydrogen and groups of the formula O II 7 -C-NHR wherein R is selected from alkyl and alkenyl groups * R is an aliphatic or aromatic group of up to eight carbon atoms. R is an alkylene group of from 1 to 6 carbon atoms with up to one catenary oxygen atom, and Z is a heterocyclic group of the formula wherein X is a divalent group which is required to complete a 5- or 6-membered heterocyclic ring , or or methyl, ER 14 represents hydrogen, an alkyl group, or a phenyl group, R 13 and R14 together may represent trimethylene or tetramethylene group, m represents a number of from 1 to 30, n is 2 or 3, and A represents a group of the formula „1 -C=0 I -N N- \ / wherein X represents the divalent radical necessary to complete a 5- or 6-membered heterocyclic ring group, said process comprising exposing said composition to radiation while the composition is in the presence of an atmosphere of at least 2% by volume of oxygen to polymerize said components having formula 1) or 2) . 6. The element of claim 5 wherein said heterocyclic is selected from formula 2), m is 1 to 4, and X is selected from 0 R 15 O R 15 R 1 5 R 16 R 15 R 17 O R 19 II 1 li • 1 1 1 1 -c- , -c- , II 1 -C-C- , -C C- , -C C- , and -C-N- R 16 A 16 R 16 R 18 ■ I C C. 1 *7 T O wherein R , R , R and R independently represent hydrogen, an alkyl group, and alkylene group, a cycloalkyl group, or a phenyl group, and RR 1 199 rreepprreeεsents hydrogen, an aliphatic group, or an aromatic group. 7. The element of claim 3 wherein said heterocyclic is selected from formula 1) and X is selected from: R 8 0 O R 8 R 8 R 9 R 8 R 10 O A 3 I II II ! I 1 I I ' II I -C- , -C- , -C-C- , -C=C- , -C-C- , and -C-N- i q I 9 J 9 1 11 τ Έ R R wherein R 8, R9, R10, and R11 are independently hydrogen, alkyl group of 1 to 4 carbon atoms, cycloalkyl group of 3 to 6 carbon atoms, and phenyl group of 6 to 12 carbon atoms, and 3 1 2 A is an alkoxyalkyl group as defined for A and A . R 8 8. The element of claim 6 wherein X is -C- and R 8 and R9 are hydrogen or alkyl of 1 to 4 carbon atoms and 2 R is hydrogen. R 8 9. the element of claim 7 wherein X is --fC-- m CH 3 is 2 to 5, R is [-frCH 2 * b _- R 5 *- H 2 * C E is CH 2 =C-C-0-, and R 5 R 4 0 is alkylene of 1 to 15 carbon atoms. 10. The element of claims 2, 3, 4, 5, 6, 7, 8, and 9 wherein said substrate is transparent and said pattern is a spiral pattern of depressions and/or protuberances having vertical dimensions of between 0.03 to 2 y . 11. The element of claim 10 wherein said separate layer has a metal coating thereon. ;τ* c r

Inventors: ANDERSON R, KERFELD D, LEWIS T, LIEN L
Applicants: MINNESOTA MINING & MFG, MINNESOTA MINING & MFG CO
Application year: 1980
Main classification: B32B3
IPC codes: C08G59, C08G77, G11B3, G11B7, G11B11, G11B23