CONTINUOUS-STREAM METHOD OF PREPARING CRYSTALLINE ZEOLITES

Abstract: A method for preparing a crystalline zeolite, with a constraint index of between 1 and 12 and a SiO₂/Al₂O₃ ratio greater than 12 on a continuous-stream basis. An aqueous reaction mixture composition having an OH/SiO₂ mole ratio less than 1 is passed in a continuous stream through a heated reactor zone to produce a slurry of zeolite.

Description: Continuous-stream method of preparing crystalline zeolite This invention relates generally to an improved method of preparing a crystalline zeolite material and particularly to an improved method of making crystalline zeolites on a continuous-stream basis. Zeolitic materials, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversions. Certain zeolitic materials are ordered, porous crystalline aluminosilicates having a definite crystalline structure within which there are a large number of channels. These cavities and channels are precisely uniform in size. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of larger dimensions, these materials have come to be known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline aluminosilicates. These aluminosilicates can be described as a rigid three-dimensional framework of Si04 and A104 in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total aluminum and silicon atoms to oxygen is 1:2. The electrovalence of the tetrahedra containing aluminum is balanced by the inclusion in the crystal of a cation, for example, an alkali metal or an alkaline earth metal cation. This can be expressed wherein the ratio of aluminum to the number of various cations, such as Ca/2, Sr/2, Na, K or Li is equal to unity. One type of cation may often be exchanged either entirely or partially by another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given aluminosilicate by suitable selection of the cation. The spaces between the tetrahedra are usually occupied by molecules of water prior to dehydration. Prior art techniques have resulted in the formation of a great variety of synthetic aluminosilicates. These aluminosilicates have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U.S Patent 2,882,243), zeolite X (U.S. Patent 2,882,244), zeolite Y (U.S. Patent 3,130,007), zeolite ZK-5 (U.S. Patent 3,247,195), zeolite ZK-4 (U.S. Patent 3,314,752) zeolite ZSM-5 (U.S. Patent 3,702,886), zeolite ZSM-11 (U.S. Patent 3,709,979), zeolite ZSM-12 (U.S. Patent 3,382,449), zeolite ZSM-20 (U.S. Patent 3,972,983), zeolite ZSM-35 (U.S. Patent 4,016,245), zeolite ZSM-21 and 38 (U.S. Patent 4,046,859), and zeolite ZSM-23 (U.S. Patent 4,076,842), merely to name a few. Zeolite crystallization commonly conducted in large autoclaves, either static or stirred, frequently requires many hours for completion, and can be, by petroleum industry standards, labor-intensive. Manufacturing processes for commercial zeolites can be classified into two groups, those using homogeneous or heterogenous hydrogels and those based on pre-formed gels, for example, pelletized gels. The hydrogel processes conventionally employ large vats or autoclaves for stepwise mixing, gel aging and final crystallization, and several examples are reviewed in Chapter 9 of the book "Zeolite Molecular Sieves" by D.W. Breck, published in 1974. Although it is possible to crystallize some of these zeolites in a continuous-stream process, stepwise, batch processes are preferred due to the meta-stability of zeolite species and to the tendency towards nucleation and growth of undesirable zeolite phases such as P, sodalite, and analcime in the cases of zeolites X and Y, zeolite A, and mordenite, respectively. Characterizing these conventional zeolite preparations, in addition to the frequent existence of competing zeolite product phases, has been a zeolite product of Si02/A1203 ratio = 10 and a high alkalinity, with pH exceeding 12 and often exceeding 14. Expressed in terms of OH/Si02 mole ratios, the alkalinity of typical reaction mixture compositions used in the production of zeolites A, X and Y are given by D.W. Breck on his page 316, as 4.8, 2 and 1, respectively. By contrast the zeolites of the present invention form a class characterized in their preparation by reaction mixtures of lower alkalinity and by a zeolite product of Si02/A1203 > 12. In addition they have a constraint index of between 1 and 12, and they are generally prepared in the presence of a N- or P-containing organic compound. The constraint index is calculated as follows: logl0 (fraction of n-hexane remaining) Constraint Index = logl0 (fraction of 3-methylpentane remaining) The constraint index approximates the ratio of the cracking rate constants for the two hydrocarbons. Catalysts suitable for the present invention are those having a constraint index in the approximate range of 1 to 12. Constraint Indices (CI) values for some typical catalysts are: CAS C.I. ZSM-5 8.3 ZSM-ll 8.7 ZSM-12 2 ZSM-38 2 ZSM-35 4.5 TMA Offretite 3.7 More specifically, the zeolites of the present invention are prepared at OH/Si02 mole ratios below '1 and often below 0.5. The combination of low OH/Si02 and highly siliceous reaction mixtures results in gels which are quite stiff and difficult to mix. It is with these reaction mixtures that a continuousstream crystallization process affords unique advantages, both in terms of production efficiency and in terms of product quality control. Possible advantages of a continuousstream process include facile and independent control of nucleation and of growth stages of crystal formation by such techniques as temperature and pH gradients, by staged injection of nutrients such as Si02 and A1203 source materials and of crystallization modifiers such as N- or P-containing organic compounds, alkali metal salts, acids and bases, and by seeding. Note also that one of the common problems of earlier commercial production, the nucleation and growth of undesirable phases, can often be attenuated by the presence of an appropriate N- or P-containing organic compound. The present invention relates to an improved method of preparing synthetic crystalline zeolite materials having a constraint index between 1 and 12 and a Si02/A1203 ratio greater than 12 on a continuous-stream basis. More particularly the present invention relates to an improved method of preparing the zeolites ZSM-5, ZSM-ll, ZSM-12, ZSM-21, ZSM-23, ZSM-35, ZSM-38 and ZSM-48 (described in our copending U.S. Application Serial No. 13,640 filed February 21, 1979). Zeolite ZSM-5 for example, has the formula, in terms of mole ratios of oxides and in the anhydrous state, as follows: 0.9+0.2 M2/nO : Al203 : Y Si02 : zH20 wherein M is at least one cation having a valance n, Y is at least 5 and z is 0-40. M can be an alkali metal, e.g. sodium and tetralkylammonium cations, the alkyl group containing 2-5 carbon atoms. The ZSM-5 composition has a characteristic X-ray diffraction pattern, the values of which are set forth in Table 1, of U.S. Patent 3,702,886. Members of the family of zeolites designated herein as ZSM-5 have an exceptionally high degree of thermal stability thereby rendering them particularly effective for use in processes involving elevated temperatures. In this connection, ZSM-5 zeolites appear to be one of the most stable families of zeolites known to date. ZSM-5 can also be prepared in the presence of amines or diamines as described in German Patent 2,442,240 or in U.S. 4,139,600. ZSN-ll can also be prepared in the presence of diamines as described in U.S. 4,108,881. ZSM-35 can also be prepared in the presence of diamines as described in U.S. 4,107,195. Zeolite ZSM-5 in accordance with this invention, for example, is prepared on a continuous-stream basis from a solution containing sources of an alkali metal oxide, preferably sodium oxide, a tetrapropylammonium oxide, an oxide of aluminum, an oxide of silicon, and water under controlled concentration of the hydroxyl, silicon oxide, and aluminum oxide components, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: : BROAD PREFERRED Na/Si02 0.1 to 1.5 0.1 to 0.6 Oil /Si02 8to 1.0 0.01 to 0.20 R/Si02 0.01 to 0.60 0.02 to 0.20 H20/Si02 5 to 200 15 to 50 A1203/Si02 0 to 0.08 0.001 to 0.05 wherein R is a tetrapropylammonium (TPA) cation or an amine having a pKa greater than about 7 and M is an alkali metal cation and passed in a continuous-stream through a reaction zone heated at between 20 and 3000C at a liquid hourly space velocity (LHSV) of between 0.01 and 10 cc of gel/cc of reactor volume-hr and under a pressure of from 1 to 60 atmospheres, the space velocity and the temperature being adjusted to provide the desired degree of crystallinity in the product solid. Thereafter the crystals are separated from the liquid and recovered. The reaction zone of the present invention may be horizontally or vertically positioned and, in the latter, liquid (gel) flow may be either up or down. The reactor may be of tubular design, in which case it will best have a length: diameter ratio of between 2 and 200. Such a tubular reactor is called a plug-flow reactor. Provision can be made in the reactor for local (segmented) and variable mixing and the reactor may contain a central stirring element. In this connection see co-pending U.S. Application Serial No. 47,536 filed June 11, 1979 concurrently herewith entitle "Continuous-Stream Crystallization Apparatus" (our Docket NO. 0172). In addition, the reaction zone may contain provision for introducing crystallization nutrients and modifiers, i.e., for altering reaction mixture composition along the stream. For example, modifiers such as quaternary ammonium compounds and amines of pK greater than about 7 may be injected subsequent to gel formation and even subsequent to heating. Solutions of acids such as HC1, H2SO4, HNQ3 and of bases such as NaOil and KOH can be added to alter the pH at varied stages of crystal growth. Nutrients such as solutions of sodium silicate, silica sol, aluminum sulfate or sodium aluminate can be injected to change crystallite composition, the first two for example to produce crystals having an outer shell essentially free from aluminum. Preferably, the continuous process for making zeolites of Si02/A1203 ratio greater than 12 and with a constraint index of between 1 and 12 is initiated by pumping solutions of Si02 source material and of A1203 source material into a continuous stream at a reactor inlet. Si02 source materials are usually sodium silicate, colloidal silica dispersions, silicic acid, quaternary ammonium silicates, or tetraalkylorthosilicates. A1203 source materials commonly employed are sodium aluminate, aluminum sulfate, nitrate or chloride, or aluminum tri-alkoxides. Acids such as HC1, HN03 or H2S04, bases such as alkali metal or quarternary ammonium hydroxides, and usually the appropriate N- or P-containing organic compound are present in the SiO2 and A1203 solutions such that, on mixing, a reacton mixture is obtained having an OH/Si02 ratio of less than 1 and preferably less than 0.5 whereupon a gel results. In calculating OH/Si02 ratios, moles of acid (added as such, added in combination with A1203 as, for example, in Al2(S04)3.l41120, or added as the acid salt for an amine, for example) and twice the moles of hydroxide (added as NaOH, as NaA102 or as Na2SiO3, for example) to yield a net hydroxide (OH) value. The appropriate N- or P-containing organic compound depends on the zeolite product phase desired. In the references cited above, tetraalkyl ammonium ions wherein the alkyl group contains 2-5 carbon atoms can be used for the production of the zeolites ZSM-5, ZSN-ll, and ZSN-l2. Amines and diamines with 2-20 carbon atoms and cyclic amines such as pyrrolidine, all with PKa of at least 7, have been successfully used to prepare such zeolites as ZSM-5, ZSN-ll, ZSM23, ZSM-35, ZSM-38, and ZSM-48. As the reaction mixture passes through the reactor chamber it is heated at a temperature of between 50 and 2500C. Pressures are 1 to 60 atmospheres, and space velocity (cc of reaction mixture per cc of reactor volume per hour) is between 0.01 and 10 and preferably between 0.1 and 2. A slurry of zeolite is produced at the reactor outlet, and the zeolite is separated from the mother liquor by decantation or by filtration. The product crystals may be washed with water and dried at temperatures of about 1100C for up to 24 hours or they may be used directly for catalyst or for adsorbent manufacture. In the case of many catalysts and adsorbents it is desired to incorporate the new product with another material resistant to the temperatures and other conditions employed in organic conversion processes. Such materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the new composition i.e. combined therewith which is active, tends to improve the conversion and/or selectivity of the catalyst in certain organic conversion processes. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate of reaction. These materials may be incorporated into naturally-occurring clays, e.g. bentonite and kaolin, to improve the crush strength of the catalyst under commercial operating conditions. Said material, i.e. clays, oxides, etc., function as binders for the catalyst. It is desirable to provide a catalyst having good crush strength because in a petroleum refinery the catalyst is often subjected to rough handling, which tends to break the catalyst down into powder-like materials, which cause problems in processing. These clay binders have been employed normally only for the purpose of improving the crush strength of the catalyst. Naturally-occurring clays which can be composited with the zeolite crystals include the montmorillonite and kaolin family, which families include the subbentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite, or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. Binders useful for compositing with the zeolite crystals also include inorganic oxides, notably alumina. It is often desirable to replace the original cations in the as-synthesized zeolite, either before or after combination with a binder. - This is normally accomplished by calcining the zeolite to about 5000C, preferably in an inert atmosphere such as nitrogen, to destroy organic compounds present in the original crystals. After cooling alkali metal cations + + may be replaced by exchange with NH4 or H30 ions. A final heating to about 5000C will produce an active, acid catalyst. In order to more fully illustrate the nature of the invention and the manner of practicing same, the following nonlimitative examples are presented. Unless otherwise noted all examples used Q-grand (commercially available mixture of sodium silicate 27.8% SiO2, 8.4% Na20, 64% H,O), A12(S04)3.l6H20, H2S04 and TPA-Br. Example 1 In order to demonstrate the concept of this invention an upflow reactor was constructed, described in the aforesaid copending U.S. Patent Application filed concurrently herewith, of 1 1/4" o.d. stainless steel tubing which had a volume of 220 cc and a central stirring element. Solutions -of 500g Qbrand in 500g water and of 16g Al2(S04)3.16H20, 45g conc. H2S04 62g TPA-Br in 842g water were pumped at about 35 cc/hour (each) into the bottom of the reactor. The reaction mixture composition is given by the following mole ratios: SiO2/Al2O3 = 94 H20/Si02 = 39 OH/Si02 = 0.12 Na/Si02 = 0.60 TPA/Si02 = 0.10 Reactor conditions were 190-2100C stirred ( 400 rpm), with 400 psig He pressure maintained over the liquid phase, LHSV=0.3. The reactor effluent, taken off the top of the column, was filtered, dried and analyzed by X-ray diffraction. The solid ws ZSM-5, in about 80% crystallinity. Example 2 The example demonstrates that continuous-stream crystallization is possible for an extended period of time in the equipment described in Example 1. In this example run conditions were LHSV=0.2 and 2250C, with stirring at 300 rpm. Mole ratios were as for Example 1 except that OH/Si02 was 0.05. As shown in Table 1, the experiment was on stream for 51 hours and yielded 80.7 grams of zeolite product with crystallinity of 80-90%. TABLE 1 Continuous-Stream ZSM-5 Crystallization Sample Time on Stream Prod. Wt. ZSM-5 Prod. Crystallinity (hrs.) I 3.5 0.1 Too small to analyze II 4.5 0.1 50% III 5.5 0.02 IV 7.0 0.4 75% V 11.0 1.1 80% VI overnight 2.2 85% VII 27.5 2.6 85% VIII 29.2 2.5 80% IX 31.2 4.9 80% X 35.3 4.7 90% XI overnight 34.6 85% XII 51 5.3 80% XIII Reactor Residue= 22.2 80% Total Zeolite= 80.7 gms Example 2A In this example the stirring blades on the central stirring element were adjusted to provide greater lift to the product crystals. The reaction mixture composition was the same as in Example 2; reaction conditions were LHSV 0.27, 2300C, 46Q rpm. As shown in Table 2, the experiment was run for 48 hours and produced 153g of zeolite with 90-100% crystallinity. TABLE 2 Continuous-Stream ZSM-5 Crystallization Sample Time on Stream # t Samp Prod. Wt. ZSM-5 Prod. Crystallinity I 7.5 hrs 4.7 hr 0.8 99% II overnight, 18.5 10.9 6.9 100 III 21.0 2.4 2.6 99 IV 23.0 2.0 4.8 100 V 25.4 2.4 4.9 90 VI 26.7 1.3 4.9 90 VII 31.7 5.0 7.1 90 VIII overnight, 41.2 9.5 8.0 90 IX 45.4 3.0 8.0 90 X 47.9 2.5 8.6 100 XI Reactor residue = 96.7 100 Total ZSM-5 = 153.3g In the examples below, a process variable study on rates and crystal morphology in ZSM-5 synthesis, are examined using as variables the following mole ratios of reaction mixture components: (1600C with stirring) SiO2/A1203 Na/Si02 H20/SiO2 TPA/Si02 OH/SiO2 TMA/SiO2 Unless noted all experiments used Q-brand, A12(S04)3.16H20, H2S04 and TPA-Br. EXAMPLES 3-52 Process Variables in ZSM--5 Crystallization 1600c, Stirred Unless Noted Example Si/A12 H20/Si OH/Si Na/Si TPA/Si R'/Si Hrs Product 3 00 40 0.01 0.59 0.10 - 7 100% ZSM-5 4 00 40 0.10 0.59 0.10 - 7 100% ZSM-5 5 90 40 0.30 0.59 0.05 - 7 Amorphous 6 90 40 0.30 0.59 0.10 - 7 Amorphous 7 90 40 0.30 0.59 0.10 - 18 Amorphous 8 90 40 0.30 0.59 0.10 - 30 30% ZSM-5 9 90 40 0.30 0.59 0.10 - 63 90% ZSM-5 10 90 40 0.30 0.59 0.10 - 88 100% ZSM-5 11 90 40 0.20 0.59 0.10 - 3 Amorphous 12 90 40 0.20 0.59 0.10 - 7 85% ZSM-5 13 90 40 0.10 0.59 0.10 - 3 50% ZSM-5 14 90 40 0.10 0.59 0.10 - 7 100% ZSM-5 15 90 40 0.10 0.59 0.10 - 7 100% ZSM-5 16 90 40 0.10 0.59 0.10 - 16 100% ZSM-5 17 90 40 0.10 0.59 0.10 - 48 100% ZSM-5 18 90 40 0.10 0.59 0.10 - 7a 25% ZSM-5 19 90 40 0.05 0.59 0.10 - 3 60% ZSM-5 20 90 40 0.01 0.59 0.10 - 3 10% ZSM-5 21 90 40 0.01 0.59 0.10 - 7 100% ZSM-5 22 90 40 0.10 0.59 0.60 - 3b 458 ZSM-5 23 90 40 0.10 0.59 0.60 - 7 100% ZSM-5 24 90 40 0.05 0.59 0.60 - 7 100% ZSM-5 25 90 40 0.10 0.59 0.05 - 3 10% ZSM-5 26 90 40 0.10 0.59 0.05 - 7 100% ZSM-5 27 90 40 0.10 0.59 0.03 - 7 80% ZSM-5 28 90 40 0.10 0.59 0.02 - 7 50% ZSM-5 29 90 40 0.10 1.18 0.10 - 1.5 Amorphous 30 90 40 0.10 1.18 0.10 - 3b 90% ZSM-5 31 90 40 0.10 1.18 0.10 - 3 Amorphous 32 90 40 0.10 1.18 0.10 - 7 100% ZSM-5 33 90 40 0.10 1.18 0.05 - 7 100% ZSM-5 34 90 40 0.10 1.18 0.02 - 7 75% ZSM-5 35 90 20 0.10 0.59 0.10 - 3 85% ZSM-5 36 90 20 0.10 0.59 0.10 - 7 100% ZSM-5 37 90 40 0.10 0.59 0.10 C 3 100% ZSM-5 38 90 40 0.10 0.59 0.10 - 1.5 100% ZSM-5 39 90 40 0.10 1.18 0.10 - 1.5 100% ZSM-5 40 90 40 0.10 0.59 0.10 O.1OTMA 7 808 ZSM-5 41 90 40 0.01 0.59 0.10 0.05TMA 7 80% ZSM-5 42 90 40 0.01 0.59 0.10 O.O5TMA 16 100% ZSM-5 43 90 40 0.01 0.59 0.10 O.lOTMA 7 25% ZSM-5 44 90 40 0.01 0.59 0.05 0.05TMA 21 100% ZSM-5 45 60 40 0.30 0.59 0.10 - 7 Amorphous 46 60 40 0.10 0.59 0.10 - 7 95% ZSM-5 47 60 40 0.10 0.59 0.10 - 7 80% ZSM-5 48 30 40 0.30 0.59 0.60 - 7 Amorphous 49 30 40 0.30 0.59 0.10 - 7 Amorphous 50 30 40 0.30 0.59 0.10 - 64 65% ZSM-5 35 Mordenite 51 30 40 0.10 0.59 0.10 - 7 Amorphous 52 30 40 0.10 0.59 0.10 - 7 20% ZSM-5 a--Stopped stirrer when temperature reached 1600C b--If 16 hours at 250C before heating, only 90% (Example 23) c--2250C. From the foregoing Examples 3-52 the process variable effects can be summarized as follows, first as they influence rates and then crystal morphology. The rates are strongly dependent on Si02/A1203 and OH/Si02 ratios, as shown in Figures 1 and 2, and decrease with decreasing Si02/Al 203 ratio. The data suggests that this trend is intrinsic, i.e., that it can be only partially overcome by changes in reaction mixture formulation, such as TPA/Si02. Concentrating on a single ZSM-5 preparation (from gels of Si02/A1203 = 90), OH/Si02 emerges as the dominant variable. As shown in Figure 2, a pronounced optimum exists in the rate curve at low OH/Si02 ratio (about 0.05). H20/Si02 and Na/Si02 have little effect on rate at 1600C, over a range of compositions. It is known that TPA is incorporated into ZSM-5 in a stoichiometry corresponding to 3-4 TPA/unit cell (0.03-0.04 TPA/Si02). The data in Figure 3 reflect this stoichiometry in that effects of TPA/Si02 became pronounced only at or below about 0.05. In a stirred crystallization at OH/Si02 = 0.1, the lack of further increase in rate with TPA/Si02 (Figure 3, 3 hours) suggests that surface nucleation predominates (over solution-phase) and that TPA is not ratelimiting. Morphology effects (see below) support this assertion. TMA (tetramethylammonium ion) addition to the reaction mixture is known to produce large, well-shaped ZSM-5 crystals as described in U.S. 4,139,600. The data in Figure 4 shows that rates decline as TMA is added to a conventional reaction mixture. Accompanying changes in rates are changes in shape and size of the product crystals. Superimposed on any correlation with reaction mixture components was a time-dependence of crystal size as shown in Figure 5. As expected, crystals, in equilibrium with the solution phase, are constantly growing in size. Crystal morphology, like rate, is most sensitive to Si02/Al203 and to OH/Si02 ratio. Figure 6 shows that well defined, large crystals form more readily as the Si02/A1203 ratio increases, a trend paralleling ease (rate) of formation of these various samples and suggesting that incorporation of aluminum into the framework is a disruptive, difficult process. OH/Si02 influences both size and agglomeration, as shown in Figure 7. At high OH/Si02 (0.3) small, highly dispersed crystals are found whereas large, well-defined ones result at the other extreme (OH/Si02 = 0.01). At the very high OH/Si02, crystal growth and dissolution would be competing and an equilibrium, to produce smaller crystals, would result. At OH/SiO2 0.01 the dissolution process would be largely absent and crystallization more orderly, yielding the larger, well-defined materials. Figure 8 shows the influence of TPA/Si02 a ratio which 2, should alter the relative importance of surface and solutionphase nucleation. As TPA/Si02 increased, the agglomerate intergrowths broke up to yield dispersed crystals. Combining the two effects (high TPA/Si02 and lower OH/Si02) produced a further improvement, to larger but still well-dispersed crystals. The comparison in Figure 9 shows the influence of TMA and how.it can be supplemented by controlling OH/Si02. It seems probable that TMA primarily inhibits surface nucleation. Thus, at higher OH/Si92, where (Figure 7) surface and solutionphase nuclation compete to produce agglomerates, TMA has spectacular effects. At low OH/Si02 however, as in Figure 9, these effects, and the differences, become less pronounced. One last variable is significant, the temperature. In Figure 10 are compared ZSM-5 samples prepared at 1600 and 2250C, with and without added sodium. Evident at the higher temperature are both very large, misshapen crystals and "new" smaller ones, suggesting the absence of distinct nucleation and growth stages in the crystallizing mixture.

Claims: WHAT IS CLAIMED IS: 1. A method for preparing a crystalline zeolite having a constraint index between 1 and 12 and a Si02/A1203 ratio greater than 12 on a continuous stream basis which comprises preparing a mixture containing sources of an alkali metal oxide, R20, an oxide of aluminium, an oxide of silicon and water under controlled amounts of the resultant hydroxyl, silica and alumina components and having a composition, in terms of mole ratios of oxides, falling within the following ranges: : OH /Si02 10-8 to 1.0 R/Si02 0.01 to 0.6 H20/Si02 5 to 200 Na/Si02 0.1 to 1.5 A1203/Si02 0.08 to 0 wherein R is a tetrapropylammonium cation or an amine having a pK greater than about 7, said mixture being introduced in a continuous stream, and maintaining the mixture at a temperature between about 50 and 2500C, at LHSV between 0.01 and 10 at a pressure between about 1 and 60 atmospheres until crystals of said zeolite are formed. 2. The method of Claim 1 wherein the mixture has a composition, in terms of mole ratios of oxides, falling within the following ranges: OH /Si02 0.01 to 0.2 R/Si02 0.02 to 0.2 H20/Si02 15 to 50 Na/Si02 0.1 to 0.6 A1203/Si02 0.05 to 0.001 3. The method according to Claims 1 and 2 wherein the temperature is maintained between from about 1600C to about 2100C. 4. The method of Claims 1, 2 and 3 wherein said sources of an alkali metal oxide, R20, an oxide bf aluminum, and an oxide of silicon are introduced step-wise. 5. The method according to Claim 4 wherein modifiers including acids and bases are introduced step-wise into the - reaction mixture for pH control during crystallization. 6. The method according to Claims 1 and 2 wherein seed crystals of the product zeolite are introduced into the reaction mixture. 7. In a method for preparing a crystalline zeolite having a constraint index between about 1 and 12 and a silica/alumina ratio greater than 12 from a reaction mixture containing sources of an alkali metal oxide, R20, an oxide of aluminum, an oxide of silicon and water, wherein R is a tetrapropylammonium cation or an amine having a PXa greater than about 7, and maintaining said mixture under crystallization conditions, the improvement which comprises conducting said crystallization at a resultant OH /Si02 ratio of less than 1 and on a continuous stream basis. 8. The method according to Claim 7 wherein a further improvement comprises introducing said sources of an alkali metal oxide, R2O, an oxide of aluminum, and an oxide of silicon step-wise. 9. The method of Claim 1 wherein said zeolite is ZSM-5. 10. The crystalline zeolites produced by the method of Claims 1, 2, 3, 4, 5, 6, 7, 8, and 9.

Inventors: ROLLMANN, LOUIS DEANE, VALYOCSIK, ERNEST WILLIAM
Applicants: MOBIL OIL CORPORATION
Application year: 1980
Main classification: C01B33
IPC codes: C01B39, B01D9, B01J29