METHOD FOR RECOVERING MOLYBDENUM FROM TUNGSTEN SOLUTIONS

Abstract: A method wherein molybdenum values are removed from an aqueous solution containing tungsten values by converting the molybdenum to a thiomolybdate complex ion and contacting the resulting solution with an organic extractant to remove the thiomolybdate complex ion from the aqueous solution. The organic extractant comprises an aromatic solvent and a quaternary ammonium compound.

Description: METHOD FOR RECOVERING MOLYBDENUM FROM TUNGSTATE SOLUTIONS The present invention relates to an improved process for removing molybdenum values from an aqueous solution containing tungsten and molybdenum. PRIOR ART For processing tungsten ores it- is desirable to remove molybdenum from an aqueous solution containing tungsten values. According to a process disclosed in U.S. Patent 3,158,438 to Kurtak a process is disclosed for recovering tungsten values from molybdenum contaminated aqueous solu¬ tions of tungsten. The molybdenum contaminate is precipi¬ tated as molybdenum trisulfide prior to the solvent extrac- tion of tungsten. The molybdenum precipitate is formed by adding an alkali metal sulfide prior to the solvent extraction of tungsten. The molybdenum precipitate is formed by adding an alkali metal sulfide to the tungsten and molybdenum con¬ taining solution at a proper pH to convert the molybdenum contaminate to the thiomolybdate complex ion. Acidification of the resulting solution results in the precipitation of molybdenum trisulfide. Tungsten values are then extracted into an organic phase. U.S. patent 3,804,941 to Coad et al relates to a sol- vent extraction process for the recovery of tungsten. The solution containing tungsten values is sulfidized to convert all of the tungsten to the thiotungstate species. A result ing sulfidized alkaline solution is contacted with an extra tant in an organic diluent to extract the tungsten. The amount of extractant employed is disclosed as being from about 1 to 15 percent by weight based on the organic phase with quaternary ammonium chloride being a preferred group o extractants. The extraction process as described is effec¬ tive for removing relatively low concentrations of tungsten present as the tungstate ion from a brine not disclosed as containing molybdenum values. U.S. patent 3,806,590 discloses a process wherein tung sten in an alkaline solution is sulfidized to connect it to a thiotungstate species, contacted with an organic phase comprising an extractant in an organic diluent whereby the thiotungstate is extracted into the organic phase and sub¬ sequently recovered. The improvement comprises contacting the thiotungstate containing organic phase with sulfur dioxide whereby at least a portion of the thiotungstate is converted to a tungstate species. The tungstate species is stripped from the organic phase with an aqueous salt soluti to recover the tungstate. The starting tungsten solution has a relatively low concentration of tungsten and is not disclosed as containing molybdenum values. SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to remove molybdenum values from tungsten solutions. According to the present invention, there is provided a process for removing molybdenum values from aqueous solution containing tungsten values comprising sulfidizing said solu- tion to an extent sufficient to convert substantially all of the molybdenum values to a thiomolybdate species, said sulfi dizing being substantially less than the extent necessary to convert substantially all of said tungsten values to a thio¬ tungstate species and contacting the resulting solution con- taining the thiomolybdate complex ion with a suitable amount -^- _ OM ^ of an organic extractant for a sufficient period of time to preferentially extract the thiomolybdate complex ion into the organic extractant, said organic extractant comprising an aromatic organic solvent and a quaternary ammonium com- pound of the formula [R 3 (CH- N] A~, wherein R is an alkyl group having from about 8 to 10 carbon atoms and A is an anion derived from a mineral acid. DETAILED DESCRIPTION The starting aqueous solution from which it is desired to concentrate the tungsten values and remove impurities in¬ cludes molybdenum values. The solution may be formed from the ores scheelite or wolframite including ferberite and hubnerite or a concentrate thereof. The ore is ground and digested, such as with an alkaline solution, for a period of time sufficient to dissolve both molybdenum and tungsten. Typical prior art leaching methods employ sodium carbonate to leach out the tungsten values. The digestion of scheelite with soda is preferably conducted at an elevated temperature, say about 130°C for a period of time sufficient to digest the tungsten and molybdenum to form a solution containing sodium molybdate and sodium tungstate and an insoluble resi¬ due. The leach liquid typically has a pH in excess of 8 and comprises less than about 5 grams per liter of sodium molyb¬ date and from about 50 to about 200 grams per liter of sodium tungstate. Minor amounts of various other contaminants are present in the liquor. The present invention is primarily concerned with removing relatively dilute molybdate values from an aqueous solution containing relatively concentrated tungsten values. The solution is sulfidized by adding sufficient alkali metal sulfide to the leach liquor to result in converting substantially all of the molybdenum values which are in the form of the molybdate ion to a thiomolybdate species. Pre¬ ferably at least 200 percent of the amount of alkali metal sulfide stoichiometrically required to convert the molybdate OMPI Λ. WIPO « * -4- ion to a thiomolybdate ion complex having the formula MoS ~ is added. More preferably alkali metal sulfide is added in excess of about five times or 500 percent the stoi chiometric amount. Excesses of greater than 10 times can be used. Included within the term alkali metal sulfide are sodium sulfide, sodium acid sulfide. Hydrogen sulfide may also be used. Sulfidizing should be carried out to an extent substan¬ tially less than the extent necessary to convert substan- tially all of the tungstate to a thiotungstate species. Preferably less than about 300 percent of the stoichiometric amount of alkali metal sulfide required to convert the tung¬ state ion to a thiotungstate ion having the formula S. ~ is added. More preferably alkali metal sulfide is added in an amount less than the stoichiometric amount. It is desirable to maximize the concentration of the thiomolybdate species and minimize the concentration of the thiotungstate species in the resulting solution since both species are extractable by the extractant utilized according to the present invention at a subsequent step. As hereinbefore discussed the present invention is par¬ ticularly effective when extracting molybdenum values from starting solutions having relatively dilute molybdenum value and containing relatively concentrated tungsten values. Whe tungsten is present in the starting solution as tungstate ions and molybdenum is present as molybdate ions, the molar ratio of tungstate to molybdate present in solution is pre¬ ferably greater than about 25 to 1. More preferably the molar ratio of tungstate to molybdate is greater than 40 to To effectively convert the molybdate ion (MoO. ~ ) to the thiomolybdate complex ion which is represented by the formul MoS 4 ~ , the pH of the leach liquor should be greater than eight. The resulting solution containing the added alkali metal sulfide preferably has a pH of from about 8.0 to about 9,5 to obtain good extraction. The resulting solution more OMPI Λ, WIPO preferably has a pH from about 8.4 to about 8.6. The use of pH's greater than 10 result in a poor subsequent extraction. The use of lower pH's, on the order of 7.5, result in the formation of an undesirable emulsion. Generally it is preferred to add the alkali metal sul¬ fide to the leach liquor prior to making a pH adjustment. Satisfactory results may be achieved if the pH adjustment is made prior to the addition of alkali metal sulfide. The resulting solution containing the thiomolybdate com- plex ion is contacted with a suitable amount of organic ex¬ tractant. for a sufficient period of time to preferentially extract the thiomolybdate complex ion into the organic ex¬ tractant. The organic extractant comprises an aromatic organic solvent and an active extractant comprising a quarter- nary ammonium compound of the formula [R~(CH-,)N] A~, in which R is an alkyl group of from about 8 to about 10 carbon atoms and A is an anion, derived from mineral acids. Particularly useful as an active extractant is tricapry- lyl monomethyl ammonium chloride. Tricaprylyl. monomethyl ammonium chloride is sold by General Mills Corporation under the name Aliquat 336. A in the foregoing formula is typi¬ cally an anion derived from a mineral acid. The organic solvent is preferably a mixture of alkyl benzenes having molecular weights of either 120, 134 or 140. Typical constituents include trimethyl benzene, ethyl ben¬ zene, dimethylethyl benzenes, methyl propyl benzene, tetra- methyl benzene, diethyl toluene, dimethylisopropyl benzene and the like. The material is sold under the tradename SC #150 by Buffalo Solvents and Chemical Corporation. In the 1972 edition of Organic ' Solvents, a trade publication of Buffalo Solvents and Chemical Corporation, SC #150 is listed as having a boiling point range of from 183°C to 210°C, a Flash Point of 151°F and specific gravity of 0.902. As previously stated the molecular weight of the alkyl benzenes contained in SC #150 are 120, 134 and 140. Thus the total carbon atoms in the alkyl chains attached to the benzene _ ring are either 3, 4 or 5. When the organic solvent comprises a mixture of alkyl benzenes and the active extractant is a quaternary ammonium compound as hereinbefore discussed, the molybdenum values a compared to the tungsten values in the sulfidized solution are preferentially extracted. As the volume percent of act extractant is decreased based on a given total extractant volume, active extractant plus organic solvent, the amount molybdenum and tungsten values extracted as a percentage of these species present in the sulfidized solution decreases. Preferably an amount of active extractant as a volume percent of total extractant is utilized to result in greate than about 90 percent of the molybdenum values and less tha about 5 percent of the tungsten values present in the sul¬ fidized solution being extracted. Based on total volume of extractant, it is preferable to use less than about 3% by volume active extractant to extract a high percentage of molybdenum values and a low percentage of tungsten values from the sulfidized solution. To reduce the tungsten value extracted, it is more preferred to use less than 2% and more preferred to use less than 1% by volume active extractant. If it is desirable to extract substantially all of the molybdenum values it may be desirable to use greater than about 3% by volume active extractant. Generally the use of active extractant volumes in excess of 5% results in greater than 99% removal of molybdenum values accompanied by the removal of greater than about 10% of the tungsten values. The ratio of organic extractant to aqueous solution being extracted can be varied within practical limits. Either a batch or continuous process can be utilized. Gen¬ erally the organic to aqueous volumetric ratios can vary from about 1 to 10 to about 10 to 1. The organic extractant containing the thiomolybdate complex is separated from the aqueous solution containing tungsten values by permitting a phase separation due to the differences ' in densities between the aqueous and organic liquids. The aqueous solution containing tungsten may be further processed according to conventional methods to 5 recover sodium tungstate. Typical methods are evaporation to produce crystalline sodium tungstate or treatment with calcium to precipitate calcium tungstate therefrom. The organic phase comprising the organic extractant which includes molybdenum values in the form of the thio o- 10 lybdate complex ion is contacted with an aqueous solution containing a sufficient amount of oxidizing agent to oxidize the thiomolybdate complex to the molybdate ion. The molyb¬ denum values are transferred from the organic extractant to the aqueous phase in the form of the molybdate ion. Typical l**-" oxidizing agents are nitric acid, hydrogen peroxide, and metallic salt of hypochlorous acid. Preferably an aqueous hypochlorite solution is preferably from about 10 to about 13. The organic extractant with the molybdenum values re¬ 20 moved is then recycled for contacting with the solution containing the thiomolybdate complex ion. To more fully illustrate the invention, the following example is given. All parts, proportions and percentages are by volume unless otherwise indicated. 25 EXAMPLE 1 A solution containing 184 grams of sodium tungstate per liter and 1.7 grams of sodium molybdate per liter was pre¬ pared. The pH was adjusted to 9.5 by the addition of sodium hydroxide and sodium hydrogen sulfide was added. The appro- 30 priate amount of sodium hydrogen sulfide solution was added to each of five one liter samples of the sodium tungstate and molybdate solution to give resulting solutions containing the moles per liter of sodium hydrogen sulfide set forth in column one, of Table I. Each solution was adjusted from a 35 H of about 8.4 - 8.6 by slowly adding sulfuric acid. An organic extractant comprising 2.3 percent by volume Aliquat 336 and 97.7 percent by volume SC #150 was prepared. Sepa¬ rate 50 ml. portions of the organic extractant were each mechanically shaken in a 125 milliliter separator funnel for about 10 minutes with 50 ml. samples of the solutions of column one, Table I. After settling, equal volume of the organic and aqueous phases were analyzed for tungsten and molybdenum content. The following Table I shows the results when various concentrations of sodium hydrogen sulfide solu¬ tion is utilized. The Distribution Ratio is the concentration of the particular material in the organic phase divided by its con¬ centration in the aqueous phase. TABLE I Distribution Distribution Separation NASH Ratio of Ratio of Factor mole/liter Molybdenum Tungsten D Mθ/° D Mθ D W 0.11 5.69 0.033 172 0.22 35.71 0.032 1116 0.45 170.92 0.034 5027 0.67 194.77 0.036 5410 0.89 168.11 0.035 4803 EXAMPLE 2 A solution containing 58 grams of sodium tungstate per liter and 0.8 grams of sodium molybdate per liter was pre¬ pared. The pH was adjusted to about 9 by the addition of sodium hydroxide. About 7 grams of sodium hydrosulfide (NaSH.2H 2 0) which corresponds to about 5 times the stoichio¬ metric amount was added. The pH of the solution was adjuste to about 8.5. Separate 50 ml. portions of the sulfidized solution were extracted with an organic extractant containin the percentage of active Aliquat 336 extractant shown in TABLE II which is a volume percent of the total extractant icluding SC #150. The samples were shaken, settled, and OMPI WIPO the organic phase analyzed for tungsten and molybdenum con¬ tent. The following TABLE II shows the percent of the total molybdenum and tungsten values present in the sulfidized so¬ lution extracted with various percent Aliquat 336 extract- ants. TABLE " ϊϊ % of % by Volume Molybdenum % of Tungsten Aliquat ' Values ' Extracted Value;3 " Extracted 1% 91.7 0.66 2% 95.8 3.58 3% 98.8 7.3 4% 99.1 9.23 5% 99.73 12.08 6% 99.72 14.33 7% 99.81 15.63 8% 99.75 17.64 10% 99.84 19.48 While there has been shown and described what are con- sidered the preferred embodiments of the present invention, it will be obvious to those skilled in the art that various changes and modifications may be made therein without depart¬ ing from the scope of the invention as described in the appen¬ ded claims. INDUSTRIAL APPLICABILITY The present invention is useful industrially when pro¬ cessing tungsten ores to remove molybdenum from an aqueous solution containing tungsten values. OMPI /-. V/IPO

Claims: CLAIMS 1. A process for removing molybdenum values from an aqueous solution containing tungsten values sulfidizing said solution to an extent sufficient to convert substan- tially all of the molybdenum values to a thiomolybdate spe¬ cies, said sulfidizing being substantially less than the ex¬ tent necessary to convert substantially all of said tung¬ sten values to a thiotungstate species, and contacting the resulting solution containing molybdate complex ion with a suitable amount of organic extractant for a sufficient perio of time to preferentially extract the thiomolybdate into the organic extractant, said organic extractant comprising an aromatic organic solvent and a quaternary ammonium compound of the formula [R 3 (CH_,)N] A~, wherein R is an alkyl group having from about 8 to 10 carbon atoms and A is anion derive from a mineral acid. 2. A process for removing molybdenum values from an aqueous solution containing tungsten according to Claim 1 wherein the pH of said resulting solution is from about 8 to about 10 during said extraction. 3. A process for removing molybdenum values from an aqueous solution according to Claim 2 containing tungsten wherein said resulting solution has a pH from about 8 to about 9.5. 4. A -process for removing molybdenum values from an aqueous solution according to Claim 3 wherein said organic extractant containing the thiomolybdate complex is separated from the aqueous solution containing tungsten values. 5. A process for removing molybdenum values from an aqueous solution according to Claim 4 wherein the molar ratio of tungsten values to molybdenum values present in the aqueous solution is greater than 25 to 1. 6. A process for removing molybdenum values from an aqueous solution according to Claim 5 wherein said solution is sulfidized by adding at least 200 percent of the stoi- chiometric amount of alkali metal sulfide required to con¬ vert the molybdate to a thiomolybdate ion having the formula Mo S 4 = . 7. A process for removing molybdenum values from an aqueous solution according to Claim 6 wherein less than about 300 percent of the stoichiometric amount of alkali metal sul¬ fide required to convert the tungstate to a thiotungstate ion having the formula W S ~ is added. 8. A process for removing molybdenum values from an aqueous solution according to Claim 7 wherein said aqueous solution comprises less than about 5 grams per liter of sodium molybdate and from about 50 to about 200 grams per liter of sodium tungstate. 9. A process for removing molybdenum values from an aqueous solution according to Claim 4 wherein the amount of quaternary ammonium compound as a volume percent of total extractant utilized results in greater than about 90 percent of the molybdenum values and less than about 5 percent of the tungsten values present in the resulting solution being ex- tracted. 10. A process for removing molybdenum values from an aqueous solution according to Claim 9 wherein the extractant comprises less than about 3 percent by volume quaternary am¬ monium based on total volume of extractant. "-

Inventors: KIM T, MACINNIS M
Applicants: GTE PROD CORP
Application year: 1980
Main classification: C01G39
IPC codes: B01D11, C01G39, C01G41, C22B3, C22B34