DIELECTRICALLY ISOLATED HIGH VOLTAGE SEMICONDUCTOR DEVICES

Abstract: Structure for achieving closely spaced high voltage devices in integrated circuits. The devices are formed in monocrystalline tubs (11) in a polycrystalline substrate (10). To prevent the potential of the substrate from causing breakdown of the devices, there is included between the single crystalline tubs and the polycrystalline substrate a semi-insulating layer (13) which has trapping states capable of taking on charge From the monocrystalline region. The shielding provided by the semi-insulating layer permits the surface regions of the device to be made closer to the polycrystalline substrate and the tubs to be made more shallow.

Description: DIELECTRICALLY ISOLATED HIGH VOLTAGE SEMICONDUCTOR DEVICES Background of the Invention This invention relates to high voltage semiconductor circuits and devices, and in particular to a dielectrically isolated structure which permits close packing of devices in a semiconductor substrate. A great need is presently developing for integrated arrays of high voltage devices, such as those used in telephone crosspoint switching. Fabrication of such devices presents special problems due to the ralatively high bias supplied to the devices. For example- it is known to fabricate devices in elements of single crystal silicon known as "tubs" which are contained on a surface of a polycrystalline substrate and are electrically isolated from the substrate by a dielectric layer such as S θ2 (see, for example, U. S. Patent No. 3,411,051, issued to Kilby) . While such structures are adequate, their use in high voltage applications results has certain problems. In particular, it is necessary that the active regions of the devices are sufficiently far removed from the polysiliσon substrate so that the potential of the substrate will not cause breakdown. This has necessitated use of deep tubs (typically 45 m deep for a device operating at 500 volts) with wide lateral dimensions (typically 55ym from the . active region to the end of the tub) which has prevented fabrication of closely spaced structures. It is therefore an object of the invention to provide a high voltage integrated circuit with a device structure which permits close spacing of devices. Summary of the Invention The invention is an integrated circuit comprising a high voltage semiconductor device which includes a polycrystalline semiconductor substrate, a '. 2 . region of monocrystalline (single crystal) semiconductor of one conductivity type formed at a major surface of the substrate and a localized active region formed at the surface of the monocrystalline region. The structure is 5characterized by the inclusion of a semi-insulating layer between the monocrystalline region and the polycrystalline substrate. This semi-insulating layer is deigned to include trapping states which are capable of taking on charge from the monocrystalline region. The lOsemi-insulating layer therefore shields the localized surface region from the potential of the substrate when a bias is supplied thereto, and prevents breakdown. Brief Description of the Drawing FIG. 1 is a cross-sectional, partly schematic, 15view of a device in accordance with one embodiment of the invention; FIGS. 2-6 are cross-sectional views of a portion of an array of such devices during various stages of fabrication in accordance with the same embodiment; 0 FIG. 7 is a cross-sectional view of a device in accordance with a further embodiment of the invention; and FIG. 8 is a perspective view, partly cut away, of a device in accordance with a still further embodiment of the invention. 5 t will be realized that for purposes of illustration, these figures are not necessarily drawn to scale. Detailed Description The invention will first be described with 0 reference to the particular device illustrated in FIG. 1. It will be realized that this device is illustrative only, and the invention may be used for other high voltage devices as discussed below. The particular device shown is a gated diode 5 crosspoint switch. It includes a polycrystalline silicon substrate 10 typically 500μm thick with a monocrystalline tub 11 formed at a major surface of the' substrate. The tub may typically have a length of 270Um and a width of 120 m at the surface. " The bulk of monocrystalline tub 11 is lightly doped with boron to a concentration of approximately 8xl0 J cm and is 5 therefore designated p-. The tub is separated from the substrate by two layers. One layer 12 is the standard dielectric layer such as Siθ2 with a thickness of approximately 2-4μm. The second layer 13 is a semi- insulating layer which has trapping states capable of 10 taking on charge from the monocrystalline tub and has a high dielectric strength. In this particular example, the layer comprises silicon which is doped with oxygen, wherein the oxygen concentration is approximately 25 atomic percent. The thickness of the layer is 15 approximately 5000 Angstroms. The function of this layer will be described below. The layer 13, as described herein is typically amorphous. However, depending on growth conditions the layer may be polycrystalline and should work in the same 20 manner to be described. Although it has been taught to form oxygen-doped silicon layers on the surface of semiconductor devices (see, for example, ϋ. S. patent 4,114,254 issued to Aoki, et al) , it does not appear that anyone has previously suggested using such a layer as an 25 intermediate layer between a single crystal region and a polycrystalline substrate in accordance with the invention. At the surface of the monocrystalline tub, localized ρ + region 14 and p region 15 are formed, 30 typically by diffusion or ion implantation. Region 14 has a doping concentration near the surface of typically 10 x ^ cm J and has a doping distribution as a function of depth which follows a complementary error function. Region 15 typically has a concentration near the surface of 35 10 xo cm J and has a distribution following a Guassian profile. Both regions typically have depths of approximately 3V- m and have lengths of 100 m and widths -of OMPI 40um. The regions are placed approxmately 170 m apart and approximately lOμ from the edge of the monocrystalline tub. Also, formed at the surface of the tub by diffusion or ion implantation are localized n + regions 16 and 17. As shown, n + region 16 is formed between regions 14 and 15, typically 70Um from each. The region 16 typically has a depth of lO m, a length of 120nm and a width of 30 m. N + region 17 is formed within the area of p- region 15. This region typically has a depth of approximately 2ym, a length of 80um and a width of 20Um. The doping concentration of the n' regions near the surface is typically 10 19 cm " . The doping concentration of region 16 follows a Guassian profile, and that of region 17 follows a complementary error function. An insulating layer 18 such as Siθ2, is formed at the surface of the tub and substrate to passivate the device and provide insulation from the electrical contacts at the surface. The surface insulator may also comprise a multilayer of Siθ2 and Metal 19 which makes contact to the p + region 14 constitutes the anode, while metal 20 which contacts n + .region 17 serves as the cathode. Metal 21 which contacts the n + region 16 comprises the gate electrode. A layer of silicon nitride (not shown) approximately 1.3um thick is usually formed over the top surface including the metals to retard corrosion. In addition, metal layer 22 makes contact to the polysilicon substrate 10. (It will be noted that the polysilicon substrate may also be contacted on the same major surface as the monocrystalline regions.) The gated diode switch operates between a high voltage blocking- state and a low resistance conducting state. The blocking state is obtained when the gate voltage and substrate voltage are more positive by a voltage Vg than either the anode or cathode voltage. In the blocking state, a high voltage (typically +250 volts) OMPI is applied to the substrate through the contact 22 and to the gate contact 21, while a positive voltage of approximately +220 volts is applied to the anode contact 19 and a negative voltage of approximately -220 volts is applied to the cathode contact. The conducting state is obtained when the potential to the gate is removed and a potential difference of 1 volt exists between anode and cathode, in which case current is generated due to the flow of carriers laterally between p + region 14 and n region 17. The current is turned off when the positive potential (+250 volts) is reapplied to the gate in order to collect electrons and deplete the monocrystalline tub. The p region 15 keeps the depletion region produced by the gate from reaching the n + region 17 and this prevents transfer of electrons from region 16 to region 17 during the blocking state. The blocking state also allows bilateral voltages with the anode at -220 volts and the cathode at +220 volts. When the single dielectric layer 12 is utilized, it is possible for the electric field generated by the large potential difference between the substrate and surface region 15 to exceed the breakdown strength of monocrystalline silicon (approximately 2xl0 5 volts/cm) . This is due in part to the light doping of mono- crystalline region 11. This result has necessitated, in the prior art, using a deep tub, typically d=45Pm, and also providing a large lateral distance, typically l=55 m, between the localized active surface regions 14 and 15 and the edge of the tub to insure that this critical field is not obtained. FIG. 1 illustrates how the semi-insulating layer shields the localized surface region 15 from the potential of the substrate. Assuming for the sake of illustration that a bias is supplied only to electrodes 22 and 20, mobile electrons represented by "0" flow to the layer 13 and are captured by the trapping states to become fixed negative charge in the layer represented by "0". The layer 13 takes on just enough charge to reach the potential in the vicinity of surface region 15. This means that most of the lines of electric field, represented by arrows, will terminate at the s.emi-insulating layer and the field between the substrate and the region 15 essentially goes to zero. Thus, the negatively biased region 15 is effectively shielded from the potential of the substrate. It will be realized that more than one potential is applied to the single crystal tub, as when the anode is also biased. The semi-insulating layer will locally reach whatever the potential of the single crystal region is in the vicinity at a particular time during operation. Thus, for example, on the left-hand portion of the device, when the anode is positively biased, the trapping states of the semi-insulating layer in that vicinity will capture negative charge until the layer reaches the potential of that region of the device. Less charge is captured in this portion since the voltage difference between the anode and substrate is much less than that between the region 15 and the substrate. This will not affect the shielding action in the vicinity of the cathode previously described. It should also be realized that the device in FIG. 1 is typically coupled in anti-parallel with a similar device in the array to form a bidirectional switch with bilateral blocking. Thus, during portions of the operation, the localized region 14 will be biased negatively creating the same problem previously described. During such portions of the operation, the semi-insulating layer on the left-hand portion of the device will perform in the same manner as that described for the right-hand portion in FIG. 1. Thus, in general, .the^semi-insulating layer will shield any localized surface region biased with a polarity opposite to that of the substrate and thereby prevent any large electric field from being generated between the region and substrate so that no breakdown occurs. As a result of the shielding, the distance, 1_, of the locali-zed region from the edge of the single crystalline tub can be significantly reduced resulting in considerable reduction in device area. For example, in typical prior devices, this distance is now approximately 55μm whereas with shielding the distance can be reduced to 10μm or less. Furthermore, the depth of the single crystalline tub can be reduced, probably to approximately 2 for a 500 volt device. A further advantage which accrues from the shielding action is the elimination of corner breakdown. This problem results from the negative potential of metal 20 and the positive potential of the substrate near the edges of the monocrystalline regions. This creates a field from the substrate to the metal 20 across the corners of the tub which can exceed the critical field for breakdown of silicon. The shielding of the semi-insulating layer in accordance with the invention blocks the field as illustrated. In order to provide shielding in accordance with the invention, the layer 13 should be semi-insulating, have trapping states which can take on charge from the mono- crystalline region, and have a high dielectric strength. In this example, the silicon semi-insulating layer preferably has an oxygen concentration in the range 10-40 atomic percent and a thickness within the range .05-5Um to provide adequate shielding when a dielectric layer (12) is also utilized. The dielectric strength is typically in excess of 2x10 volts/cm. In general, proper shielding should result for any semi-ins-ulating layer with trapping states capable of taking on charge from the single crystal region in an amount of at least 5xlO l electronic charges/cm . The resistivity of the semi- insulating layer should be sufficiently great so that there is little lateral current in the layer in relation to the lateral current of the device. Preferably, the resistivity is within the range 10 -10 ohm-cm. Trapping states are created in semiconductor layers by disorder in the crystal structure or by doping the layer. Thus, most polycrystalline semiconductors such as polycrystalline silicon and GaAs should provide sufficient trapping states to be used in accordance with the invention without the requirement of any dopant impurities. In addition, semiconductor layers doped with impurities other than oxygen may also be utilized. For example, amorphous or polycrystalline silicon doped with nitrogen, or GaAs doped with chromium are likely alternatives to the oxygen-doped silicon described above. The minimum concentration of trapping states needed for shielding will basically be a function of the potential difference generated between the substrate and surface regions and the thickness of the dielectric layer 12. For example, for a 500 volt device with a dielectric layer thickness of ly m, a minimum concentration of approximately 1x10 J cm would be needed to shield the entire potential. For a 4μm thick layer of dielectric, a minimum concentration would be approximately 2.5x10 12 cm—2. The requirements for various other parameters can be easily calculated according to standard capacitance theory. Although a 500 volt device has been described, the invention would be useful in general for devices operated at 30 volts or more. The invention could be used in any such device employing lateral conduction and a lightly doped monocrystalline region, i.e., one having a doping concentration of less than 10 16 cm " . A typical fabrication sequence for an array of such devices is illustrated in FIGS. 2-6 wherein elements corresponding to those of FIG. 1 are similarly numbered. A wafer of monocrystalline silicon 11 is provided with a thickness of approximately 500μm and typically having major surfaces lying in the (100) plane. V-shaped grooves 30 are etched into one surface of the wafer to a depth of approximately 70μ m. The usual etchant is a mixture of potassium hydroxide and water and a useful etching mask^ 1U ^gX3R OM /». IP (not shown) is a layer of thermally grown Siθ2- Next, as shown in FIG. 3, the semi-insulating layer 13 is formed on the surface including the walls of the grooves. Advantageously, the layer can be formed by standard chemical vapor deposition. For example, the wafer may be placed in a deposition chamber and heated to a temperature of approximately 650 degrees. Reactant gases of silane and nitrous oxide can be caused to flow over the wafer with a nitrogen carrier gas. Silicon doped with oxygen will then be deposited on the surface including the walls of the groove at a rate of approximately 100 Angstroms per minute. To achieve a 20 percent doping with oxygen, the relative amounts of gases are 3 parts silane to 1 part nitrous oxide and the total flow rate is approximately 250 cm J /min. Next, as shown in FIG. 4, a layer 12 of Si0 2 12 is formed over the semi-insulating layer. This can be done, for example, by chemical vapor deposition using silane and oxygen as reactant gases with a nitrogen carrier gas. The wafer is typically heated to a temperature of 400 degrees C and the relative amounts of gases are 1 part silane to 9 parts nitrous oxide. The total flow rate is r> 580 cm-vmin. The deposition rate of Siθ2 is approximately 120 Angstroms/min. . Then, as shown in FIG. 5, the polycrystalline silicon substrate 10 is formed by deposition over the Si0 2 layer. This is typically accomplished in two stages. First, in order to cause nucleation of the polycrystalline silicon, a reactant gas of silane with a carrier gas of hydrogen is caused to flow over the structure which is heated to a temperature of approximately 1000 degrees C for a time of approximately 10 min. This produces a polycrystalline film which is typically several microns thick. Then, a reactant gas of trichlorosilane (SiHCl 3 ) with a hydrogen carrier gas is caused to flow over the resulting structure which is heated to a temperature of approximately 1190 degrees C. The rate of deposition o'f polycrystalline silicon for this process is approximately 7μm/min. Deposition continues until more than 500Um of polycrystalline silicon is formed. The surface of the polycrystalline layer is then planarized by grinding. The monocrystalline wafer is then ground and polished down to the line indicated so as to expose portions of the polycrystalline silicon in the grooves. The resulting inverted structure is shown in FIG. 6. It w . ill be noted that individual tubs of single crystal silicon 11 are therefore formed in one major surface of the polycrystalline silicon substrate 10 and electrically isolated therefrom by the layers 12 and 13. The particular device configurations, such as that shown in FIG. 1, can then be formed in the single crystalline tubs. One alternative device configuration which may also utilize the present invention is illustrated in FIG. 7. This is an example of a standard integrated silicon controlled rectifier (SCR) . As in the case of the gated diode switch, the structure includes a polycrystalline silicon substrate 31 with a tub 32 of single crystalline silicon formed in a major surface. Again, the tub is electrically insulated from the substrate by a dielectric layer, 33, , and between this layer and the tub is a semi-insulating layer 34 in accordance with the present invention. In this example, the tub 32 is again doped to produce p- conductivity type with an impurity concentration of typically 0.5-5xl0 14 cm "3 . N-type region 35 and n + region 36 are formed at the surface of the single crystal region by standard diffusion or ion implantation. The n_ region 35 typically has a doping concentration following a Guassian profile and a surface concentration of approximately 10 18 cm -3 and the n + type region 36 has a doping concentration following a complementary error function and a surface concentration of 10 19 J cm—3. P+ type region, 37, is formed within n-type region 35, again, by diffusion or ion implantation. Tϊiis OM region typically has an impurity concentration following a complementary errror function and a surface concentration of approximately 10 9 cm " ~^. P-type region 44 is formed surrounding n + region 36 to prevent punch through and typically has a concentration following a Guassian profile and a surface concentration of 10 cm . Insulating layer 38 is formed on the surface of the monocrystalline region and polycrystalline substrate. Metal 39 makes contact to the p + region 37 and constitutes the anode, while metal 40 contacts the n + region 36 and constitutes the cathode. Metal 41 makes contact to r region 35 and constitutes the gate electrode. Contact is made to the substrate by means of metal 42. The operation of such a device is well known and will not be discussed. For purposes of the present invention, it will be noted that this device also conducts laterally (between p + region 37 and n + region 36) when an appropriate bias is supplied to the cathode, anode and gate electrodes. Again, in ' order to reduce the device area, it is necessary to shield the surface regions (in this case n region 35 and p-regions 44) from the potential of the polycrystalline substrate. This is accomplished by the semi-insulating layer, 34, in the manner previously described. The invention could also be used to reduce the size of other components typically used in a semiconductor array forming a high voltage integrated circuit. For example, FIG. 8 illustrates a standard pinched resistor used for high voltage applications. Portions of the surface oxide and electrodes are shown as transparent for the sake of illustration. The resistor is formed in a region, 50, of monocrystalline silicon having a p- conductivity type. Again, the monocrystalline region is formed at a surface of a polycrystalline silicon substrate 51 and separated therefrom by dielectric layer 52 and semi-insulating layer 53 in accordance with the invention. Localized p regions 54 and 55 are formed in the surface of the monocrystalline region by standard ion implantation or diffusion. Localized n + region, 56, is formed in the surface of the monocrystalline region adjacent to region 55 and electrically coupled thereto by means of electrode 57. Electrode 58 makes electrical contact to region 54. When a sufficient positive potential is applied to electrode 57 (typically +250 volts) and negative potential to electrode 58 (typically -220 volts) , the device will operate as a standard pinched resistor with lateral conduction between the p + regions (n + region 56 serves to collect electrons from the p~ region 50) . As before, by shielding the localized surface region (in this case the negatively biased region 54) from the effects of the polycrystalline substrate potential, the distance of the surface regions to the edge of the tub and the thickness of the tub can be made considerably smaller to conserve space. With pinched resistor structures, this provides the additional advantages of low limiting current since it is easier to deplete the smaller single crystal volume. Further, the variable resistor characteristics which can result from variable charge in the dielectric 52 are avoided by use of the semi-insulating layer 53. Further device modifications are possible consistent with the invention. For example, by making the semi-insulating layer thicker (approximately 5-20l J m) it may perform the additional function of electrically insulating the monocrystalline region and thus use of the dielectric layer might be eliminated to reduce processing steps. With such a structure, it might also be possible to eliminate the nucleation step required for polycrystalline silicon deposition. It may also be desirable to incorporate a very thin layer (of the order of 70 Angstroms) of Si02 between the semi-insulating layer and the single crystalline region to reduce surface recombination at the interface. Alternatively, it may be desirable to anneal the semi-insulating layer in an H 2 ( O * I ^ - environment to reduce surface recombination. Further, it may also be desirable to form the semi-insulating layer at only portions of the interface between the single crystalline tub and the polycrystalline substrate. For example, if the semi-insulating layer is formed only between the side walls of the tub and the substrate, and not at the bottom of the tub, possible surface recombination in the area at the bottom caused by the semi-insulating layer could be eliminated. In such cases, shielding at the bottom of the tub could be provided with a sufficiently deep tub while preserving the advantage of bringing the localized suface regions closer to the edge of the tub. It will be understood that the appended claims include such embodiments where the layer is formed in selective areas of the interface unless specifically provided otherwise. It will also be noted that in the particular devices illustrated, all polarities shown could be reversed, and, in addition, several other types of device structures may utilize the present invention. Various additional modifications will become apparent to those skilled in the art. All such variations which basically rely on the teachings through which the invention has advanced the art are properly considered within the spirit and scope of the invention.

Claims: Cla ims 1. An integrated circuit including a high voltage semiconductor device comprising a polycrystalline semiconductor substrate (10) , a region of monocrystalline semiconductor (11) the bulk of which has a first conductivity type formed at a major surface of said substrate, and a localized region (e.g., 15,) formed at the surface of said monocrystalline region, CHARACTERIZED IN THAT said device further comprises a semi-insulating layer (13) between said polycrystalline substrate and said monocrystalline region, said semi-insulating layer having trapping states capable of taking on charge from said monocrystalline region, thereby to shield said localized surface region from the potential of the substrate when a bias voltage is supplied thereto. 2. The circuit according to claim 1 CHARACTERIZED IN THAT the localized surface region (16, 17) has a conductivity type opposite to that of the bulk of said monocrystalline region. 3. The circuit according to claim 1 CHARACTERIZED IN THAT the localized surface region (14, 15) has the same conductivity type as the bulk of said monocrystalline region but a higher impurity concentration. 4. The circuit according to claim 1 CHARACTERIZED IN THAT the doping concentration of the bulk of the monocrystalline region is less than 10 " cm -3 . 5. The circuit according to claim 1, CHARACTERIZED IN THAT a dielectric layer (12) is disposed between the substrate and the semi-insulating layer. 6. The circuit according to claim 1 i. *** gtJRE OMP CHARACTERIZED IN THAT the thickness of the semi-insulating layer is within the range .05 - 20 μ m. 7. The circuit according to claim 1 CHARACTERIZED IN THAT the dielectric strength of the semi-insulating layer is greater than 2xl0 5 volts/cm. 8. The circuit according to claim 1 CHARACTERIZED IN THAT the resistivity of the semi-insulating layer is within the 10 4 —10 2 ohm-cm. 9. The circuit according to claim 1 CHARACTERIZED IN THAT the concentration of trapping states in the layer is sufficient to take on charge from the monocrystalline region in an amount of at least 5xl0 electronic charges/cm 2 . 10. The circuit according to claim 1 CHARACTERIZED IN THAT the semi-insulating layer comprises silicon doped with oxygen. 11. The circuit according to claim 10 CHARACTERIZED I ~~ THAT the doping concentration of oxygen lies within the range 10-40 atomic percent. 12. The circuit according to claim 1 CHARACTERIZED IN THAT the semi-insulating layer is formed selectively between the side walls of the monocrystalline region and the substrate. 13. The circuit according to claim 1 CHARACTERIZED IN THAT there is included at the surface of said monocrystalline region first and second localized regions (14 and 15) of the same conductivity type but higher doping concentration than the bulk of the single crystalline region, a third localized region (16) of opposite conductivity type disposed between the first and second regions, a fourth localized region (17) formed within the boundaries of the second region, electrical contacts to. said first and fourth regions (19 and 20) and a gate electrode making electrical contact to the third region to form a gated diode switch in the monocrystalline region. 14. The circuit according to claim 1 CHARACTERIZED IN THAT there is included at the surface of said monocrystalline region a first localized region (37 of FIG. 7) of the same conductivity type but higher doping concentration than the bulk of the monocrystalline region, a second localized region (35) of opposite conductivity type surrounding said first region, a third localized region (36) of opposite conductivity type spaced from said first and second regions, a fourth localized region of the same conductivity type but higher doping concentration than the bulk of the monocrystalline region surrounding said third localized region, electrical contacts (39 and 40) to said- first and third regions, and a gate contact (41) to said second region to form a controlled rectifier in said monocrystalline region. 15. The circuit according to claim 1 CHARACTERIZED IN THAT there is formed at the surface of the monocrystalline region first and second localized regions (54 and 55 of FIG. 8) of the same conductivity type but higher doping concentration than the bulk of the monocrystalline region, a third localized region (56) of opposite conductivity type which is electrically coupled to said second localized ' region, and electrical contacts to said regions so as to form a pinched resistor in said monocrystalline region. ^ ^"URE OMP Λ IP

Inventors: BERTHOLD J, HARTMAN A, SHACKLE P
Applicants: WESTERN ELECTRIC CO, WESTERN ELECTRIC CO INC
Application year: 1980
Main classification: H01L27
IPC codes: H01L21, H01L27, H01L29