ELECTROCHEMICAL CELL AND GAS DIFFUSION ELECTRODE FOR THE SAME

Abstract: Electrochemical cell (9), as well as a gas diffusion electrode (8) for the same. The electrode is of the type which is outwardly provided with a catalyst for converting gas to electricity and interiorly containing hydrophobic material. The distinguishing feature of the electrode is that the hydrophobic material comprises a cohesive porous plastics layer, which defines a closed gas space within the electrode, which the electrolyte cannot enter, although the electrode is immersed therein. On the other hand, gas can be sucked into and can pass out from said space. When the electrode (8) is partially immersed in the electrolyte (12), gas is automatically sucked from the atmosphere (13) above the electrolyte level in the cell and into the gas space, due to the subpressure in the space occurring during operation. By reason of the good capacity of the electrode it has been possible to make the cell according to the invention entirely closed off in relation to the surrounding atmosphere, which means a very simplified construction without gas conduits to the cell. The cell is especially utilizable as a metal/oxygen battery, fuel cell and metal oxide/hydrogen battery.

Description: TITLE OF THE INVENTION: Electrochemical Cell and Gas Diffusion Electrode for the same. TECHNICAL FIELD: The- present invention relates to an electrochemical cell and to a means for the manufacturing thereof, namely a gas diffusion electrode of a completely new type. A primary application of the electrochemical cell according to the invention, containing the new gas diffusion elec- trode, is in a battery of the type in which an oxygen electrode is utilized as the positive pole and in which the negative electrode usually consists of a metal, e.g. iron, cadmium, zinc or copper. However, the invention is not limited to the above-mentioned metal electrodes, but the negative electrode can also combust supplied fuels, e.g. hydrogen or methanol. Sources of electric current -which consist of -oxygen electrodes and metal electrodes are hereinafter referred to' as- metal/oxygen-cells (batteries) , while the latter type of current source is called a fuel cell. The gas diffusion electrode according to the invention is furthermore utilizable for the electrochemical combustion of hydrogen. In this case the positive electrode is usually a metal oxide, and this latter type of cell (battery) will be designated metal oxide/hydrogen battery hereinafter. The invention is, however, not limited to the three types of cells mentioned above, but can be applied to every electrochemical cell containing electrodes in contact with liquid electrolyte and where at least one of the electrodes is a gas diffusion electrode, which is exteriorly provided with a catalyst for converting e ~~ r-as to electricitv * , ~ and has an electricallv * conductive material as well as includes hydrophobic material, at least internally. For the sake of simplicity, the invention will hereinafter be described in conjunction with metal/oxygen batteries without being limited thereto. BACKGROUND ART: The advantage with metal/oxygen batteries compared ' with conventional batteries, is that a comparatively high energy density can be obtained, which is of great importance, e.g. if the battery is to be used for driv¬ ing a vehicle. It has thus been found possible to obtain values of over 100 Wh/kg, which can be compared with about 60 Wh/kg for alkaline nickel oxide/iron batteries and about 40 Wh/kg for lead batteries. A great drawback with the metal/oxygen cells manu¬ factured up to now,. is that an extensive auxiliary system is required to obtain a well-functioning cell. It has thus been often found necessary to circulate the electrolyte, to pump oxygen or air past the gas sides of the oxygen electrodes, and possibly introduce a special charging electrode or other * me-ans 'allowing charging the metal electrode without destroying the oxygen electrode. A summary of the systems which have been develop¬ ed, or are under development, has been presented in "Journal of Power Sources" 2 (1988/78) pp. 287-296. An oxygen electrode is disclosed in Swedish lay- -open print No. 391,609, which is characterized in that water diffuses from the gas side towards the electrolyte during the charging phase. This is achieved by the con¬ struction of a dual layer electrode, where the layer on the gas side contains a hydrophobic material, preferably of poI tetrafluoroeth lenc, and a catalyst for oxygen dissolution, while the layer towards the electrolyte side is hydrophilic. When built up into cells, the air electrodes are fixed into frames, and for building to¬ gether into a battery, two adjacent cells form an air chamber for supplying the air electrodes with oxygen from the air. OMPI In German Offenlegungsschrift 2,129,045 another metal/air or metal/oxygen battery is disclosed. In said battery a biporous oxygen (or air) electrode is used, which is layered with finely porous separators and metal electrodes to form an electrode package, where the gas electrodes are connected to a gas conduit at one or more places along the edges thereof. Distinguishing for the above-mentioned systems is that gas electrodes are assembled into a pocket which is provided with gas conduits for supply of oxygen or air. Another type of gas diffusion electrode is describ¬ ed in the article "Nouveau type d'electrode pour piles a combustible" published in "Advanced Energy Conversion", Vol. 7, pp. 159-166, Pergamon Press, 1967. The electrode is built up from finely-divided activated carbon bound together with the aid of a hydrophobic binder to a co¬ hesive body with pores alternatingly filled with gas and with electrolyte. The gas is supplied from the surroundings by means of speci-al gas supply means which can be applied anywhere on the electrode and which are described in more detail in French Patent No. 1,433,558. Also in this case, however, there is the requirement that gas conduits , and thus special means , are applied on to the electrode for -the supply of air or oxygen from out- side. DISCLOSURE OF INVENTION: According to the present invention, it has been found possible to depart from the above-mentioned principles, and to manufacture gas diffusion electrodes with a substantially simplified construction. It is true that the electrode according to the invention may appear to be similar to the type of gas diffusion electrode last mentioned, but it is considerably simpler and chea¬ per to manufacture, gives enhanced energy density and, not least, an entirely new function. By the new OΛ'.P! construction of the gas diffusion electrode according to the invention, it has thus been found possible to provide a "self-breathing" electrode when the electrode is part¬ ially submerged in the electrolyte. In turn, this enables the construction of an electrochemical cell completely closed off from the surrounding atmosphere, i.e. a cell completely without gas supply conduits. One skilled in the art will easily understand what a substantial con¬ tribution to the state of the art the new electrochemical cell in accordance with the invention hereby constitutes. Cells consisting of a plurality of interfoliated elec¬ trodes will be particularly simplified. The electrochemical cell according to the invention is distinguished in that the hydrophobic material of the gas diffusion electrode comprises a cohesive porous. plastic layer with pores impermeable to liquids but per¬ meable to gases, so that a space for gas closed off all the way round is* efined inside the electrode, gas being able to diffuse to and from said space, but to which water or electrolyte do not have access , that the gas diffusion electrode is partially immersed into the electrolyte, so that a part of the electrode is in con¬ tact gas present above the electrolyte, said gas being able to migrate via the-gas permeable pores into said space for gas defined inside the electrode, and that the cell is closed in relation to the surrounding atmosphere, whereby the gas diffusion electrode is adapt¬ ed for automatically sucking gas into the gas space, due to the subprcssure generated by the reaction when the cell is i operation. Thus, at least in connection to the interiorall defined gas space, the gas diffusion electrode has a hydrophobic porous plastic material with a pore radius and a wetting angle relative to the electrolyte such that the pores are not filled with water or electrolyte, h. O.Y.Pi so that the liquid gets through the plastic material and fills the gas space at the hydrostatic pressure occurring when the gas space is entirely or partially immersed in the electrolyte. However, at the same time, the pores are permeable to gas, primarily oxygen, for the passage of gas to and from the catalyst layer and to and from the gas in the space in the cell above the electrolyte level. If the porous electrode, or gas space, is only partially immersed in the electrolyte, there is namely formed a communication link betλveen the gas above the electrolyte and the gas space itself in the interior of the electrode. This is due to the electrode's construct¬ ion and the properties of th_e hydrophobic material. Accordingly, if the atmosphere above the electrolyte consists of oxygen, the gas space which is closed off all the way round will also contain, oxygen in the parts which are under -the liquid level. If the outsides of the gas space are provided with an electrically conductive material and a layer of cata¬ lyst suitable for oxygen electrodes, oxygen will diffuse through the pores in the walls of the gas space and be converted in the catalyticallv active layer when current is taken from the electrode. The gas pressure in the space will then decrease. In such circumstances it has been found that new oxygen is sucked into the gas space through the parts above the electrolyte level. The gas diffusion electrode will thus be "self-breathing", i.e. gas, in this case oxygen, docs not need to be fed to the cell from outside. The cell according to the invention has good energy density and works completely satisfact¬ orily as a system completely closed off from the sur ¬ rounding atmosphere. It has been found preferable to provide only the parts of the gas space which are below the electrolyte level with catalysts. As already mentioned, the hydrophobic plastic material must have a pore radius and wetting angle such that it is capable of preventing the electrolyte from getting into the gas space, in spite of the subat osphe- ric pressure created in said space while the reaction is in progress. The selection of hydrophobic plastics mate¬ rial is not critical for the invention. For one skilled in the art there is no difficulty to select in each in¬ dividual case such plastics material having the proper- ties described above, i.e. to select suitable pore radius and wetting angle. Polytetrafluoroethylene (PTFE) can be mentioned as a non-restricting example of a suitable plastics material. According to one embodiment of the cell in accord- ance with the invention, the entirely closed-pff gas space in the gas diffusion electrode is formed as a peripherally totally sealed pocket, with walls in the form of films, or sheets, of the hydrophobic, porous, plastics ' material., the walls b-eiήg kept apart by spacers. According to another embodiment the peripherally totally sealed gas space is formed by a porous body, e.g. a plate, which is exteriorly coated with the hydro- phobic porous plastic material. When hydrogen is the gas used in the cell, for example, the pores inside the body in the last-mentioned embodiment can be allowed to be of the same size as the pores in the exterior plastics material. Usually, how¬ ever, e.g. when the gas is oxygen, it is suitable to impart to the porous body greater pores than the pores in the exterior porous plastics material. Still another embodiment of the cell according to the invention involves forming the peripherally totally sealed gas space from a porous body, e.g. a plate, of the hydrophobic plastics material, the body being out- wardly coated with said catalyst. This signifies an advantageous embodiment, above all from the manufact- uring aspect, enabling manufacture of a gas diffusion electrode to a low price. With regard to the relationship between the surface of the closed gas space above and below the electrolyte level, respectively, this relationship is determined by the permeability of the plastics material to gas, the maximum currents it is desired to take from the elect- trode and the total height of the electrode. Generally, however, the part of the gas diffusion electrode above the electrolyte level should constitute at least 1 % of the total area of the electrode. On the other hand, the upper limit is not equally as definite, since theoretically any amount at all could project above the electrolyte level. This will be, however, at the cost of energy density, and generally the upper limit should preferably not exceed 15 % . For optimum results with regard to the surface of the gas diffusion electrode above the electrolyte level, the lower limit should be at least 5 % and often at leas-t 10 % of the total area of the electrode. From the above it will be apparent that said surface is usually within the range of 1-15 % , preferred ranges being 5-15 % or 10-15 % . According to still another preferred embodiment of the electrochemical cell in accordance with the invent- ion, increasing, preferably gradually increasing, hydro- phobic properties are imparted to the electrode towards the end thereof, which is immersed in the electrolyte. Thus, in this way it is possible to compensate for the hydrostatic pressure of the electrolyte in this way. Instead of, or further to increasing the hydrophobic properties of the plastics material at increasing depths, one can further increase the hydrophobic properties of the catalyst layer in a corresponding way towards the electrode end immersed in the electrolyte. The embodi- ent with increasing hydrophobicity towards one end of the electrode is especially advantageous for very tall electrodes. However, even in the case with varying hydro- phobicity, the portion of the electrode above the elect¬ rolyte level must have sufficient gas permeability, while at the s.ame time being capable of excluding splashing electrolyte and condensed water drops. In the case when the oxygen electrode in accord¬ ance with the invention, described above, is used in a metal/oxygen battery, it must be possible to charge the metal electrode. How charging takes place is not criti- cal for the invention. If the electrically conductive and catalytic layer of the oxygen electrode has such properties that it withstands the generation of oxygen, the oxygen electrode can be used for charging. In other cases, a special charging electrode can be used. In this connection it may be mentioned that the Swedish Patent specification 357,104 discloses a method in charging a hybrid fuel cell, this method being distinguished by insulating an auxiliary electrode and the oxygen elec¬ trode from each other with the- aid of a gas which is supplied under pressure to a. space between said electro¬ des. Such methods complicate the battery cell substan¬ tially, the energy density being reduced at the same time, since more inactive components must be added. A particularly preferable embodiment of the in- vention, especially as it relates to a closed cell, is to utilize the oxygen generated during charging, so that it can be used during subsequent discharging. Such a system is disclosed in the German Offenlegungsschrift 1,771,803. In this publication a special charging elect- rode i described, provided with means for leading away the oxygen generated during charging. Λs a result of the present invention, the technique disclosed in said publication has also been substantially simplified, since the space above the electrolyte level serves as an oxygen reservoir. The size of the reservoir is determin¬ ed by the metal/oxygen cell's metal electrode, since the oxygen quantity corresponds to a given quantity of ampere hours. In cells with relatively high capacity, it has been found suitable to pass the oxygen to a special chamber for compression. In most cases, the metal electrode generates hydrogen gas during the latter part of charging. When hydrogen gas is mixed with oxygen there is the risk of explosion. However, in such a case, the electrochemical cell according to the present invention can be supple- mented by a hydrogen-oxygen reactor, known per se. The real task of this reactor is to' lower the content of hydrogen in the gas mixture developed from the cell or battery during charging to values which are below the limit of explosion for hydrogen-oxygen-water mixtures in the system in question. Many metal electrodes also generate hydrogen when they are discharged and xhen they stand unloaded. However, there are reactor embodiments which also take .into consideration this situation. The ' reactor, known per se, can be of the catalytic type or of the combustion type. The catalytic type can comprise a catalyst mass arranged inside the battery it¬ self. The German Offenlegungsschrift 1,812,518 discloses a method of decreasing the quantity of gas generated during charging. It is known that metals from the plati- num group can catalytically combust hydrogen in the presence of oxygen. In claim 6 ' there is disclosed an embodiment where the catalyst material is separated from the electrode chamber by means of a filter material. The pub] ication docs not disclose a method where one gas is purified from the other for subsequent storage of the purified gas. It is also possible to arrange the catalyst mass outside the hatter)' and then, if required, during discharging and/or in an unloaded state conti¬ nuously or intermittentlv oxidize riskv amounts of hv- drogen or amounts thereof injurious to the function by circulating the gas mixture between the battery and the reactor. The oxygen gas necessary for oxidization is naturally obtained from the oxygen in the pressure vessel. However, it is also possible to divide the cata- lyst mass, one portion being arranged within the battery while the other is arranged between the battery and the pressure vessel. The combustion reactor can be some suitable type of a gas combustor. The flame must not propagate backwards into the battery, and some kind of liquid trap can therefore be arranged between the battery and the burner. The combustion reactor can furthermore be combined with a catalytic reactor arrang¬ ed after the former, to further reduce the content of hydrogen in the gas mixture, before it is compressed and passed to the pressure vessel. The product water formed in the hydrogen-oxygen reactor is recycled to the elec¬ trolyte in the simplest possible way. In certain -cases it can moreover be suitable to provide the bottom of the closed gas space in the gas diffusion electrode with a hydrogen-oxygen catalyst to oxidize the hydrogen which can possibly accompany the oxygen and thereby be accumulated at the bottom of the space. The corresponding characteristic features apply for the new gas diffusion electrode in accordance with the present invention as have been set forth above in conjunction with the electrochemical cell. Distinguish¬ ing for the gas diffusion electrode according to the invention is thus that the hydrophobic material cons i- tutes a cohesive porous plastics layer with pores which are impermeable to liquid and permeable to gas, so that a peripherally totally sealed gas space is defined in¬ side the electrode, gas being able to diffuse from said space, which does not allow the entrace of water or electrolyte. _OMPI The specially preferable embodiments of the peri¬ pherally totally closed gas space in the electrode have been described above, and therefore do not need to be repeated here. Furthermore, in the same way as has been mentioned above, the gas diffusion electrode in accord¬ ance with the invention preferably has gradually increas¬ ing hydrophobicity from one end to the other. The invention will now be described in more detail while referring to drawing figures relating to special embodiments and certain preferred specific working examples . FIGURES: Fig. 1 is a cross section of an embodiment of a gas diffusion electrode in accordance with the present invention, Fig. 2 is a cross section of a gas diffusion electrode in an -electrochemical cell in accordance with the invention, and Fig. 3 illustrates a current voltage graph obtain- ed in testing the cell in Fig. 2. The electrode illustrated in Fig. 1 is made as a peripherally totally closed off pocket from two foils 1 welded to each other. An electrically conductive materi¬ al in the form of a net 2 has been pressed into the porous hydrophobic plastics foil 1. The outer layer of the electrode, said layer containing the catalyst, has been given the reference numeral 3. The pocket is formed by both foils 1 being heatwelded to each other at the welded joint 4. Inside the pocket there is a plastic net 5 solely serving as a spacer. A part 6 of the electrical¬ ly conductive material 2 extends above the electrode pocket and a current collector 7 is spot-welded to this part 6. A gas diffusion electrode 8 in a cell 9 is illu- strated in Fig. 2, where two nickel plates 10, 11 are used as counter electrodes. The electrolyte 12 consists of 5 M potassium hydroxide solution, and the electrode 8 extends up into the gas space 13 containing pure oxygen gas. Current collectors 14,15,16 pass through the cell wall 17 via gas- and liquid-tight grommets 18,19 and 20, respectively. When current is taken from the cell, oxygen is sucked into the oxygen electrode in the part which is above the electrolyte level, as indicated by the arrow 21. The oxygen diffuses through the porous hydrophobic layer and reacts in the catalytically active layer, as indicated by the arrow 22. The counter electrodes 10 and 11 simultaneously generate oxygen which is passed to the gas chamber 13. When the cell illustrated in Fig. 2 was- tested, the current-voltage graph was obtained which is illu¬ strated in Fig. 3. Reproducible values were obtained under load for an extended time with varying current' take-offs. EXAMPLES: Example 1 A gas diffusion electrode in accordance with the invention was manufactured according to the following method. Sheets of PTFE were manufactured by sedimentat¬ ion of a PTFE-suspension, subsequent to which the sedi¬ ment was dried and sintered. Alternatively, commercial- US' ( ) ly available sheets, e.g. Millipore or Gote-Tcx ^ can be use . Nickel netting with the dimensions 1 0 x 200 mm was pressed into the sheets at a pressure of 500 kg/cm " . The netting was somewhat longer than the sheet. Two sheets provided with nettings were heat-welded along three sides with the nettings outside, thus form- ing a pocket. A metal spacer net was thrust down into the pocket and the fourth side welded together. The now closed pocket was provided with a catalyt¬ ic layer by painting the outsides thereof with a mixture of a silver catalyst, a PTFE-suspension and a liquid pore forming agent. When the catalyst layer had dried, the whole pocket was heat treated for 30 minutes at 350 C, the catalyst layer sintering fast against the pocket. Current collectors were attached to the net portions extending above the pocket. The gas diffusion electrode manufactured in this way was tested in a half cell with two nickel plate counter electrodes. 5 M Potassium hydroxide solution was poured into a height such that 2 cm (= 101 of the pocket area) projected up above the electrolyte level. The vessel was provided with a tightly closing cover and gas-tight current collector through-passages. Before testing was started, the gas space was flushed clean from inert gases (primarily nitrogen) -with oxygen via two valves . Flus'hing continued long enough for the interior of the pocket also to be free from inert gas. The gas in the half cell thus consisted of pure oxygen in this case. During testing, the gas diffusion electrode was loaded with current for several hundred hours. The polarization graph according to Fig. 3 was not altered hereby. . The pocket was not filled with electrolyte al¬ though a gauge pressure of 2 m of water column was tried. The vacuum in the pocket compared with the gas outside the pocket was measured to 20 mm of water column - * . at a load of 100 mA/cm ^ . Example 2 The same gas diffusion electrode as in Example 1, apart from the catalyst being platinum black, was manu- factured and assembled into a half cell. The gas above and in the pocket was pure hydrogen in this case. On loading, a voltage relative to a Hg/HgO- 2 -reference electrode of -875 mV at 200 mA/cm was obtain¬ ed. Example 5 A p-orous PTFE-plate with a thickness of 7 mm was manufactured by the same sedimentation method as in Example 1. The plate was painted with catalyst in the form of platinum black (in a PTFE-suspension) and sintered. Current collecting nickel net was pressed against the surface by a tight packing in a half cell. . The electrode was tested as a hydrogen electrode, a potential of -875 mV being obtained relative to the 2 reference electrode at a load of 100 mA/cm .

Claims: AMENDED CLAIMS (received by the International Bureau on 4 November 1980 (04.11.80)) 1. An electrochemical cell (9), particularly a metal/oxygen battery, a fuel cell or a metal oxide/ hydrogen battery, comprising electrodes (8,10,11) in contact with a liquid electrolyte (12), at least one of the electrodes (8) being a gas diffusion electrode, which is externally provided with a catalyst (3) for convert¬ ing gas to electricity and with an electrically conduct¬ ing material (2) and interiorly comprises hydrophobic material, characterized in that the hydrophobic material of the gas diffusion electrode comprises a cohesive porous plastics layer (1) with pores which are impermeable to liquid but permeable to gas, so that a peripherally totally sealed gas space is defined inside the electrode, gas being able to diffuse to and from said space, which does not permit entry of water or electrolyte; that the gas diffusion electrode (8) is partially immersed in the electrolyte (12) so that a portion of the electrode is in contact with gas above the electrode, said gas being able to pass through the gas-permeable pores into the gas space defined inside the electrode; and that the cell is closed off in relation to the surrounding atmoshpere, whereby the gas diffusion electrode is adapted for automatically sucking gas into the gas space by means of a subpressure generated therein during operation of the cell. 2. An electrochemical cell as claimed in claim 1, characterized in that the peripherally totally sealed gas space is formed as a peripherally totally closed pocket with walls in the form of sheets (1) of the hydrophobic, porous plastics material, the walls being kept apart by spacer elements (5) . 3. An electrochemical cell as claimed in claim 1, characterized in that the peripherally totally sealed gas space is formed by a porous body, e.g. a plate, which is exter orally coated with the hydrophobic porous 1ast ics materi a1. 4. An electrochemical cell as claimed in claim 3, characterized in that the porous body has greater pores " than the pores in the exterior porous plastics material. 5. An electrochemical cell as claimed in any of the preceding claims, characterized in that the gas diffusion electrode has increased hydrophobicity towards the end which is immersed in the electrolyte, to compen¬ sate the hydrostatic pressure of the electrolyte. ( >. An electrochemical cell as claimed in any of the preceding claims, characterized in that the part of the gas diffusion electrode above the electrolyte con¬ stitutes at least 1 % , preferably at least 5 %,and especially at " least 10 % , of the total surface of the electrode. 7. An electrochemical cell as claimed in claim 6, characterized in that the surface of the gas diffusion electrode above the electrolyte level is within the range of 1-15 % , preferably 5-15 _ , and particularly 10-15 _ , of the total surface of the electrode. 8. An electrochemical cell as claimed in any of the preceding claims, characterized in that the gas diffusion electrode is provided with a catalyst only on the parts which are disposed under the electrolyte surface. 9. An electrochemical cell as claimed in any of the preceding claims, characterized in that in contact with the gas above the electrolyte said cell contains a hydrogen-oxygen catalyst. OMPi ~~~~ 10. A gas diffusion electrode (8) for an electro¬ chemical cell, especially for a metal/oxygen battery, a fuel ce l l or a metal oxide/hydrogen battery, said electrode being exteriorly provided with a catalyst (3) Cor converting gas to electricity and with an electrical¬ ly conductive material (2) as well as interiorly comprises hydrophobic material, characterized in that the hydro- " phobic material comprises a cohesive porous plastics layer (1) with pores impermeable to liquid and permeable to gas, so that a peripherally totally sealed gas space is defined inside the electrode, gas being able to diffuse from and to said space, does not allow the entry of water or electrolyte. 11. A gas diffusion electrode as claimed in claim 1Q, characterized in that the peripherally totally en¬ closed gas space is formed as a peripherally totally closed pocket with walls in the form of sheets (1) of the hydrophobic porous plastics material, the walls being kept apart by spacer elements (5) . 12. A gas diffusion electrode as claimed in claim 1.0, characterized in that said gas space is formed by a porous body, e.g. a plate, which is exteriorly coated with the hydrophobic, porous plastics material. 15. A gas diffusion electrode as claimed in claim 12, characterized in that the porous body has greater pores than the pores i'n the exterior porous plastics material. 14. A gas diffusion electrode as claimed in any of claims 10-15, characterized in that it has gradually increasing hydrophobicity from one end to the other. EDITORIAL NOTE The claims amended by the applicant under Article 19 (1) of the PCT have not been renumbered in accordance with Section 205 of the Administrative Instructions under the PCT. The following information is given hereafter in order to facilitate the understanding of the amended claims: Correspondence between original and amended claims: Original claims Amended claims 1 1 2 2 3 3 4 4 5 (cancelled) 6 5 7 6 8 7 9 8 10 9 11 10 12 11 (amended) 13 12(amended) 14 13(amended) 15(cancelled) 16 14(amended)

Inventors: BURSELL M
Applicants: BURSELL M, SVENSKA UTVECKLINGS AB
Application year: 1980
Main classification: H01M12
IPC codes: H01M4, H01M8, H01M10, H01M12