ACTIVATED ESTER MONOMERS, POLYMERS FORMED THEREFROM AND COATING COMPOSITIONS CONTAINING SAID POLYMERS

Abstract: Ethylenically unsaturated monomers containing activated ester groups are used to make polymers and co-polymers which are useful in coatings, adhesives and moldings. The monomers have the formula: A()(Y)X-COOR wherein A is an organic group containing a polymerizable vinyl linkage; Z is selected from O or S; m and n are integers each selected from 0 and 1, Y is a bridging unit, e.g., -OCH₂CH₂-, -OCH(CH₃)CH₂-, -OCH₂CH₂OCH₂CH₂-, -OCH₂CH₂CO-, -NHCH₂-, -NH-, -NHCOCH₂CH₂- or -NHCH₂CH₂CH₂-; X is selected from the group consisting essentially of wherein R′ is an alkyl group with 1-8 carbon atoms; and R is an aliphatic moiety.

Description: TITLE: ACTIVATED ESTER MONOMERS, POLYMERS FORMED THEREFROM AND COATING COMPOSITIONS CONTAINING SAID POLYMERS This invention relates to ethylenically unsaturated monomers which contain activated ester groups. These monomers are used to prepare polymers and copolymers with other ethylenically unsaturated monomers which are useful in the preparation of coatings and adhesives for metals, woods, textiles, and paper, and in the preparation of moldings. The resultant polymers and copolymers are readily crosslinked by reaction with compounds containing at least two primary or secondary amine groups, and the present invention further relates to the resultant cross-linked product. Previously attempts at preparing coatings had centered on using commercially available polymers and developing novel crosslinking agents for use therewith, i.e., U.S. Patents 3,519,627 and 4,026,855 for example. Alternatively, prior attempts to prepare polymers, useful with conventional diamines, had been directed to isocyanate and/or epoxide technology. However, these coatings have considerable drawbacks to their commercial use in that the ingredients are highly toxic, or are difficult to handle, or cannot be tailor-made to a sufficient degree to make a family of coatings useful for multiple purposes. U.S. Patent 3,422,139 describes the use of acrylamidoglycolic acid as a comonomer useful in coatings. Although the use of activated esters in the preparation of regular copolyamides is well known in the literature, c.f. Oyata et al. (Polymer Journal at Vol. 5, p. 186194, Vol. 6, p. 412-418, Vol. 7, p. 72-78, and Vol. 10, p. 499-504; J. Polymer Science Vol. 14, p. 783-792; and others), these compounds were copolymerized through the @@tor groups. There has been no attempt to produce wherein the activated ester remains available for subsecruent cross link- ing with commerci lly available polyamines. Accordingly, it is an object of the present invention to produce ethylenically unsaturated monomers containing activated ester groups. It is a further object to produce polymers of the monomers and copolymers thereof with ethylenically unsaturated compounds. It is a further object to produce coatings containing the polymers or copolymers and compounds containing at least two primary or secondary amine groups. And it is a still further object to produce crosslinked coatings therefrom. The monomers of the present invention contain a polymerizable ethylenically unsaturated group, i.e., a vinyl group, and an activated ester group. Suitable monomers contain the group -X-COOR wherein X is selected from -OCH2, EMI2.1 EMI2.2 wherein R is an aliphatic moiety and each R' is alkyl of 1-8 carbon atoms. This -X-COOR group may be either directly linked to the group containing a polymerizable vinyl linkage or it may be linked through a bridging unit. The nature of this bridg-ing unit has been found to have essentially no influence on the reactivity of the ester groups on the monomers of the present invention. Thus, the use of a bridging unit and/or the particular unit is basically one of convenience in preparing the monomers. If a bridging unit is used, it must be an organic group which is attachable to both the group containing the vinyl linkage and the--activated carboxylic ester group. It further must be stable so as to not degrade during further processing and/or use of the compound. Examples of suitable bridging units include such as -OCH2CH2-, -OCH(CH3)CH2- , -OCH2CH2OCH2CH 2-, -OCH2CH2CO-, -NHCH2-, -NH-, and - NHCOCH2CH2 -. Any other suitable group may be used. Accordingly, the monomers herein have the structure: EMI3.1 wherein A is a group containing a polymerizable vinyl linkage; Z is O or S; m and n are each 0 or 1;-Y is the bridging unit as defined above; X is as defined above; and R is an aliphatic moiety. The exact nature of R which acts as a leaving group during crosslinking of the resultant coating by the action of an amine, has been found to be relatively insignificant so long as it is not too bulky to prevent the approach of the amine. Preferably, R is an alkyl group with 1-8 carbon atoms, a cycloalkyl group with 5-8 carbon atoms, or a cycloheteroalkyl group containing 5-8 atoms in the ring. These groups may be substituted with heteroatoms, NO2 groups, ethers, halogens, alcohols, nitriles, and amides. Thus, R may derive from alcohols such as methanol, ethanol, propanol, 2-nitroethanol, 2-chloroethanol, 2-cyanoethanol, ethyleneglycol, propyleneglycol, monoalkoxyethanols, furfuryl alcohol, tetrahydrofurfuryl alcohol, tetrahydropyran-2-methanol, tetrahydrdpyran-3-ol, thioethanol and other similar compounds. Most preferably R is selected from methyl, ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, optionally con taining a hydroxyl group. The C=Z group may be present or absent depending fipon the starting compound which is converted into the activated ester monomer herein. When C=Z is present, A is gen-, erally' a group such as acryl or methacryl. When c=z is not needed to make the monomer, A is such as styryl. Suitable monomers within the scope of the present invention include such as: Methyl acrylamidoglycolate Methyl acrylamidoglycolate methyl ether Methyl methacryloxyacetate -- Ethyl - acrylamido-N-oxalate (N-ethyloxalyl acrylamide) N,N'-Bis(ethyloxalyl)acrylamide - N-isopropyl, N-ethyloxalyl-3-propylamino methacrylamide N-Ethyloxalyl-N' -methyleneaminoacrylamide Ethyl N-2-ethyloxamatoacrylate Ethyl 3-pyruvylacrylate Ethyl methylenepyruvate Methyl acrylthiocarbonyloxyacetate (Methyl thiacryl oxyacetate) Methyl thiacrylthioglycolate Methyl acryl-2-thioglycolate Methyl thiacrylamidoacetate Methyl acrylamidoglycolate thioether Methyl acrylamido-N-methylenethioglycolate p-Ethyl oxalyl styrene. Other alkyl groups may be substituted for the methyl or ethyl groups in the above-named compounds. The activated ester monomers herein may be prepared by standard synthetic methods well known to the art such as esterification, condensation, addition, elimination and other such reactions depending upon the particular monomer to be prepared. The reactions are carried out using conventional acidic or'basic catalysts as needed and under conventional reaction conditions. For example, the alkylacrylamidoglycol ate alkyl ethers may be prepared by esterifying and etheri fying acrylamidoglycolic acid with the desired alcohol or mixture of alcohols; alkyl acryloxyacetates may be prepared by condensing an amine salt of the acrylic acid and an alkyl haloacetate. Alkyl N- w -alkylozamatoacrylate and N-alkyl-Nalkyloxalylaminoacrylamides and methacrylamides may be prepared by the condensation reaction of an appropriate acid chloride such as alkyl oxalyl chloride or acryloyl chloride with the desired alcohol or amine such asw-hydroxyalkylox- alate or alkylaminoalkylacrylamide. Other compounds may be similarly prepared.- Optionally the monomers may be transesterified with diols such as ethylene glycol and propylene glycol. The monomers may be polymerized, or more preferably copolymerized with other vinyl monomers, according to conventional vinyl polymerization techniques using conventional initiators, temperatures, and other reaction conditions. Suitable comonomers useful herein include the acrylates, methacrylates, styrenes, acrylonitriles, vinyl ethers, vinyl esters and derivatives of these compounds. Specifcally useful are alkyl acrylates and methacrylates wherein the alkyl groups have 1-18 carbon atoms, styrene, a-methylstyrene, acrylonitrile, methacrylonitrile, acrylic acid, methacrylic acid, maleic and fumaric acids and esters, functional-containing acrylates and methacrylates such as hydroxy ethylacrylate, acrylamide, methacrylamide, and the like. Most preferably the comonomers are selected from methylacrylate, ethylacrylate, propylacrylate, butylacrylate, 2-ethylhexylacrylate, methylmethacrylate, ethylmethacrylate, butylmethacrylate, acrylic acid, methacrylic acid, maleic acid, vinyl acetate, styrene and acrylonitrile. Generally the polymerization or copolymerization is performed in the presence of an inert organic solvent such as ethylacetate, or tetrahydrofuran, or a reactive solvent such as butanol and the like, so that in either case the resultant polymer is ready for use in a coating. The polymer must contain at least 2, and preferably 3 or more, activated ester groups per polymer chain so that cross linking may be achieved. The copolymers should contain about 5 to 50 percent by weight of an activated ester monomer and the balance one or more of a comonomer such as those specified above. Pre ferably, the copolymer contains about 10 to 40 percent of an activated ester monomer and a portion, io2. , up to about 10%, of the copolymer contains acidic functionality to catalyze the resultant curing of the polymer with a polyamine compound. Preferred acidic compounds are acrylic acid, methacrylic acid and acrylamidoglycolic acid alkyl ethers where the alkyl group has 1-8 carbon atoms. The polymers so produced may be cured by reaction with compounds containing at least two primary or secondary amine groups per molecule at temperatures from as low as room temperature to 2000C. in a period of less than about 30 minutes, though longer times may be needed at the lower temperatures. The primary or secondary amine groups must be available for- entering into the curing reaction with the activated ester of the monomer. Generally, this means that they are pendantly attached to a compound. For purposes of this invention, pendant amine groups include terminal amine groups, as well as those attached to the compound or to a side chain thereon. Suitable compounds containing amine groups useful herein include such as: 1,2-ethylenediamine 1,3-propylenediamine 1,2-butylenediamine 1 ,4-butylenediamine 1,6-hexamethylenediamine 1,7-heptanediamine diethylenetriamine xylyldiamine 4,7-dioxadecan-l,l0-diamine 1,2-diaminocyclohexane Bis (p-aminocyclohexyl) methane 2,2-Bis(4-aminocyclohexyl)propane N, N-Bis (3-aminopropyl) methylamine Bis(hexamethylenetriamine) Alternatively, the amine containing compound may be a polymer which. contains at least about 1% by weight of pendant amine groups. Representative polymers containing pendant amine groups can be derived from epoxy and epoxy-modified diglycidyl ethers of bisphenol A structures, various aliphatic polyethylene or polypropylene glycol (diglycidyl ether) adducts, and glycidyl ethers of phenolic resins, such epoxy resins being commercially available and commonly used in the electrocoating field. Other useful polymers containing pendant amine groups include polyamide resins, for example, condensation products of dimerized fatty acids coreacted with difunctional amine, such as ethylene diamine. Polyamide resins generally are those having a molecular weight between about 500 and 5,000. Further useful polymers containing pendant amine groups include acrylic resins having molecular weight of about 1,000 to about 1,000,000 or more, polyester resins and polyurethane resins both having a molecular weight range of about 500 to about 5,000, and vinyl resins. Generally, the cross-linking agent is used in an amount to provide a ratio of activated ester groups to amine groups of about 0.3/1 to 3/1. Coating compositions based upon the activated ester monomer of the present invention may contain, in addition to the polymer and the polyamine curing agent, conventional coatings additives such as antioxidants, heat stabilizers, flow control agents, pigments, surface active agents, anticorrosion agents, catalysts, and solvents. To further illustrate the present invention, the following non-limiting examples are offered wherein all parts and percents are by weight unless otherwise specified. EXAMPLE 1 Preparation of Methyl Acrylamidoqlycolate Methyl Ether (MAGMEl To a three-necked flask equipped with a stirrer and an extractor filled with a molecular sieve drying agent was added 300 parts acrylamidoglycolic acid, 3000 parts methanol, 0.05 parts phenothiazine, 4.5 parts 98% sulfuric acid and 200 parts chloroform. The mixture was heated to reflux and the distillate was allowed to pass through the extractor for 6 1/2 hours. The jni\'ur± was cooled and allowed to stand for 16 hours at which point the mixture was warmed to about 40 C. 19 g of sodium carbonate was added, and the solution was stirred for 2 1/2 hours The mixture was filtered and vacuum stripped of solvent. The solid residue was extracted with chloroform. Diethyl ether was added to the extract and a polymeric mass precipitated which was discarded. The remaining extract was stripped of solvent to yield 264.2 parts of crude MAGME which was confirmed by chemical analysis. EXAMPLE 2 Preparation of Ethyl Methacryloxyacetate (EMA) To a flask equipped with a stirrer was added 172.8 parts methacrylic acid and 202 parts triethylamine. This mixture was allowed to stir for 5 min. To this was added 245 parts ethyl chloroacetate. The reactants were heated to 600C. and the exotherm carried the temperature up to 1000C. The temperature was kept between 90-97 C. by cooling for 1/2 hour after which heat was supplied to hold the temperature at 900 for 1 hour. The mixture was cooled and filtered. This crude product was distilled at 65.5-66 C. at 0.1 cm to yield 318 g of pure EMA as confirmed by chemical analysis. EXAMPLE 3 Preparation of Butyl Acrylamidoglycolate Butyl Ether (BAGBE) One hundred parts of acrylamidoglycolic acid (AGA); 517 parts butanol, 1 part concentrated sulfuric acid and 0.1 part monomethyl ether of hydroquinone were mixed in a flask equipped with a Dean Stark water trap and a stirrer. The mixture was heated until homogeneous. After 5-10 minutes 100 ml of toluene was added and the mixture was brought to reflux and held 5 hours until the theoretical amount of water was collected by azeotrope. The toluene and excess butanol were removed under vacuum to yield 173 parts crude BAGBE, as confirmed by chemical analysis. EXAMPLE 4 Preparation of Ethyl Acrvlamidoglvz:olate Ethvl Ether (EAG:sE) Eighteen parts of acrylamidoglycolic acid (AGA), 250 parts ethanol, 0.27 parts sulfuric acid and 0.018 g of monomethylethr of hydroquinone were added to a flask and the mixture was refluxed for 1 1/2 hours. Toluene (300 parts) was added and the azeotrope was collected and tested for water content. The solvent mixture was replenished and the azeotrope collected until the theoretical amount of water was taken off (4.5 parts). --The solvent was then removed under vacuum to yield 24.9 parts crude EAGEE which crystalized readily on standing and was identified by chemical analysis. EXAMPLE 5 .PreParation of Acrylamidoalveolic acid Methvl Ether- (AGME) 45 parts of acrylamidoglycolic acid, 90 parts trimethylorthoformate, 0.045 parts of the mono methyl ether of hydroquinone and 35 parts of methanol are mixed in a flask equipped with a stirrer, condensor and thermometer. The mixture was heated at a bath temperature of 60-65 C. for 24 hours. A small amount of insoluble material was filtered off and discarded. The filtrate was stripped of solvent under vacuum and a rubbery substance was obtained. This material was extracted with ether with stirring for 3 days. The solid which was insoluble in the ether was filtered off and was further extracted with acetone. The acetone was removed to yield 24 g of crude AGME (Mp. 100-102.5) EXAMPLE 6 Following the procedure of Example 1, the following. additional monomers are prepared: Methyl acrylamidoglycolate ethyl ether Ethyl acrylamidoglycolate methyl ether Cyclohexyl acrylamidoglycolate cyclohexyl ether EXAMPLE 7 Preparation of Polymer A To a flask equipped with a-stirrer, condensor, nitrogen inlet and thermometer was added 78 parts ethyl acetate as solvent, 25.5 parts butyl acrylate, 41 parts methyl methacrylate, 31 parts- MAGME from Example L, 2.5 parts acrylamidoglycolic acid methyl ether from Example 5, 2.0 parts dodecyl mercaptan, and 2.0 parts azobisisobutyronitrile catalyst. The solution was purged with nitrogen for 30 minutes and then heated to 760C for 2 1/2 hours. The polymer so form- ed was then used in the preparation 0F the coatings tested below. EXAMPLE 8 Preparation of Polymer B The procedure of Example 7 was repeated except that tetrahydrofuran (70 parts) was used as the solvent and the following ratio of monomers were used: 30 parts butylacrylate 40 parts methylmethacrylate 30 parts MAGME EXAMPLE 9 Preparation of Polymer C The procedure of Example 7 was repeated using 45 parts ethyl acetate and the following ratio of monomers: 25.5 parts butylacrylate 37 parts methylmethacrylate 35 parts EMA from Example 2 2.5 parts AGME from Example 4 EXAMPLE 10 Following the procedure of Example 7, polymers are prepared from the following monomer compositions using toluene as the solvent: : Monomer D E F G H I Butylacrylate 5.25 5.25 16.1 25 25.5 25.5 Methylmethacrylate 20.5 19.25 29,0 39 - 41.0 BAGBE 24.5 24.5 - - - - Methacrylic acid 1.25 2.5 l8 5 2.5 2.5 EAGEE - - 25;0 - - - MAGME - - - 31 31.0 31.0 Styrene - - - - 21.0 Acrylonitrile - - - - 20.0 EXAMPLE 11 20 parts Polymer B, and 1.16' parts of 1,6-hexamethylene diamine were blended together. A glass tube was filled with the free flowing mixture and after about 112 minutes the mixture set up as a gel. This shows that the polymer has the capability of crosslinking with the diamine at room tempera ture. The same mixture after aging for 50 minutes was cast into films on cold rolled steel and baked at 100"C./20 min These films exhibit solvent resistance as shown in Table I. EXAMPLE 12 To 30 parts of Polymer A was added 9.8 parts of butanol and 1.05 parts-f 1,3-propylenediamine. This blend was cast into a film on Bonderite 1000 cold rolled steel panels and was shown to cure at room temperature as shown in Table I. An identical blend without the butanol placed in a glass tube showed a gel effect point of 15 minutes at room temperature. EXAMPLE 13 To 40 parts of Polymer A was blended 4.1 parts of 1,6-hexamethylenediamine and 13 parts of butanol. The blend was cast into films as in previous examples and was shown to cure at ambient temperatures as well as 500 C. and 100"C. (Table I). EXAMPLE 14 Polymer A was cast into a film on cold rolled steel panels without adding any diamine and was baked at 1000C. for 20 minutes. As can be seen from Table I no cure was observed even after allowing the panels to age up to 60 days at room temperature. EXAMPLE 15 To 15 parts Polymer C was added 11.4 parts of ethyl acetate and 2.3 parts of 1,6-hexamethylenediamine. This blend was cast into films on cold rolled steel panels and baked at 100 C. for 20 minutes. As can be seen from Table I the cure of the coating continued after the initial bake to produce excellent solvent resistance EXAMPLE 16 Following the procedures of Examples 11 to 15 additional coatings are prepared from the polymers of Example 10. TABLE I PROPERTIES OF COATING CURED BY ACE MONOMERS Post Cure Post Cure Exam- Gel Effect Initial Cure Film Properties Days MEK Days MEK ple Point (min.) Conditions Thick Knh MEK Rubs At RT Khn Rubs At RT Khn Rubs 11 112 ambient; 24 hrs. 1.0 3 2 30 11.4 200+ 12 15 ambient; 24 hrs. 1.5 5.7 30 5 8.0 80 12.1 200+ 13 20 ambient; 24 hrs. 1.5 1 1 200+ 14 10.6 200+ 50 C., 20 min. 1.2 2 200+ 5 4.6 200+ 14 10.5 200+ 100 C., 20 min. 0.9 12.8 200+ 5 13.1 200+ 14 14.2 200+ 14 - 100 C., 20 min. 1.0 0 2 60 2 15 2400 100 C., 20 min. 2.0 55 5 4.9 200+ 14 8.2 200+ Note: Knh = Knoop Takon Hardness Thick = thickness of films in mils. EXAMPLE 17. Preparation of Ethyl N-2-ethyloxymatoacrylate To a mixture of 500 arts ethanolamine in methylene chloride (900 ml), cooled to -70 C., was added dropwise 2405 parts diethyloxalate After stirring at room tempera- ture for 16 hours, the mixture was filtered 7 concentrated and purified by chromatography to yield pure ethyl 2-hydroxyethyloxamate. A mixture of the oxamate (77 parts), sodium carbonate (50.2 parts) and an inhibitor in chloroform were cooled to 0 C and acryloylchloride (43.3 parts) was added dropwise. After stirring at 0 for 2 hours and room temperature for 3 hours the mixture was filtered to yield 1011 parts crude ethyl N-2-ethyloxamatoacrylate. EXAMPLE 18 Preparation of Polymer from Ethyl N-2-ethyloxyamatoacrylatef One part ethyl N-2-ethyloxamatoacrylate of Example 17 was mixed with 2 parts dioxane and .005 parts azobisiso- butyronitrile and was purged with nitrogen. The mixture was heated to 700C. for 60 minutes and the homopolymer was formed. Four tenths part 1,3-diaminopropane was added to cure the polymer after it had cooled. Thore as an immediate evolution of heat and the sample solidified indicating rapid crosslinking. EXAMPLE 19 Preparation of N-isopropyl-N-ethyl oxalyl-3-aminopropyl methacrylamide (EOMAM) Sixty-six parts of icproyl;llainopropylethacryla- mide was mixed with 400 parts chloroform and 36.4 parts triethylamine. The mixture was cooled to 40C. and a mixture of ethyl oxalyl chloride (49 parts in chloroform (100 parts) was added dropwise over 35-45 minutes. The mixture was held at 0-50C. for 1/2 hour and then warmed to room temperature overnight. The mixture was filtered, stripped and purified by column chromatography to yield N-isopropyl-N-ethyl oxalyl -3- aminopropylmethacrylamide (99.6 parts). he product was confirmed by chemical analysis. EXAMPLE 20 Preparation of polymer from N-isopropyl-N-ethyl- oxalyl-3-aminopropylmethacrylamide (EOMAM) The polymerization of Example 7 was repeated with the following reactants: Butyl acrylate 25 Methyl Methacrylate 30 EOMAM (from Example 19) 45 The resulting polymer (5 parts) was gelled by 1,3propylene diamine ( .15 parts) within 18 hours or 1,6-hexamethylenediamine (.23 parts) after 45 hours at room temperature. EXAMPLE 21 Preparation of Methyl acrylamidoglycolate (MAG) Acrylamide (141.7 parts), methylglyoxylate (144 parts), acetone (1200 ml) and phenothiazine (0.05 parts) were mixed and heated to reflux for 6 hours. After filtration and crystallization 180 parts MAG were received as confirmed by chemical analysis EXAMPLE 22 Preparation of polymer from Methylacrylamidoglycolate The procedure of Example 7 was repeated with the following monomers: Butyl acrylate 7.5 parts Methyl methacrylate 11.8 MAG (from Example 21) 5.75 The polymer (15 parts) was readily gelled using 1,3-diaminopropane (0.39 parts) within 7-10 minutes at room temperature indicating rapid crosslinking. EXAMPLE 23 Preparation of N-Ethyl oxalyl-N'-methylene aminoacrylamide Methoxymethyl acrylamide (19.7 parts), ethyl oxamate (40 parts), sulfuric acid (2 parts), methanol (10.9 parts) and chloroform (350 ml.) were mixed and ref fluxed for 32 hours. Excess sodium carbonate was added and the mixture was stirred for 3 days. Filtration, stripping, and fractional crystallization yielded 16 parts of the desired product as confirmed by chemical analysis. EXAMPLE 24 Preparation N-Ethyl oxalylacrylamide and N,N-Bis(ethyl oxalylacrylamide) The above monomers are jointly prepared by the condensation reaction of acrylamide with diethyl oxalate or ethyl oxalyl chloride in the presence of potassium tertiary butoxide. The mixture is stirred at room temperature for 1-5 days and the mixed product is purified and each component is separated by chromatography or the mixed product is used to make a polymeric coating. The present polymers and copolymers are also useful in the production of molding and adhesives by conventional procedures well known to those skilled in the art.

Claims: CLAIMS; 1. A compound Qf the formula: EMI16.1 wherein A is an organic group containing a polymerizable vinyl linkage; Z is selected from 0 or S; m and n are integers each selected from 0 and 1, Y is a bridging unit; X is selected from the group consisting essentially of EMI16.2 wherein R' is an alkyl group with 1-8 carbon atoms; and R is an aliphatic moiety. 2. A compound of Claim 1, wherein A is an acryl or methacryl group. 3. A compound of Claims 1 or 2, wherein Z is oxygen and m is 1. 4. A compound of any preceding claim, wherein Y is selected from the group consisting of - OCH2CH2-, OCH(CH ) CH2-. -OCH2CH2OCH2CH2-, - OCH2CH2CO -, - NHCH2-, -NH-, -NHCOCH2CH2-, and - NHCH2CH2CH2-. 5. A compound of any preceding claim, wherein X is selected from the group consisting of -OC,112 EMI16.3 EMI16.4 6. A compound of any preceding claim, wherein R is selected from the group consisting of alkyl with 1-8 carbon atoms, cycloalkyl with 5-8 carbon atoms, and cycloheteroalkyl with 5-8 atoms, each of which is optionally substituted with one or more groups selected from heteroatom, NO2, ether, halogen, alcohol, nitrile or amide groups 7. A compound according to any preceding claim, wherein the compound is an alkyl acrylamidoglycolate alkyl ether wherein the alkyl groups are the same or different and have 1-8 carbon atoms. 8. A compound according to any preceding claim, wherein the compound is selected from the group consisting essentially of methyl acrylamidoglycolate methyl ether, ethyl methacryloxyacetate, butyl acrylamidoglycolate butyl ether, and ethyl acrylamidoglycolate ethyl ether. 9. A polymer of the compound of any preceding claim. 10. A copolymer of the compound of any one of Claims 1-8 and one or more copolymerizable vinyl monomers. 11. A copolymer of Claim 10, wherein the copolymerizable vinyl monomers are selected from the group consisting essentially of alkyl acrylates and alkyl methacrylates having 1-18 carbon atoms in the alkyl group, styrene, -methylstyrene, acrylonitrile, methacrylonitrile, acrylic acid, methacrylic acid, maleic acid, fumaric acid, acrylamide, methacrylamide, and hydroxyethylacrylate. 12. A copolymer of Claim 11, further containing acrylamidoglycolic acid methyl ether. 13. A copolymer of any of Claims 10-12, which contains up to about 10% by weight of a monomer having acidic functionality. 14. A coating composition comprising a copolymer of any one of Claims 9-13 having at least two ester groups per polymer chain and a compound containing at least two primary or secondary amine groups per molecule. 15. A coating composition of Claim 14, wherein the amine-containing compound is selected from the group consisting essentially of 1,2-ethylenediamine, 1,3 -propylenediamine, 1,2-butylenediamine, 1,4-butylenediamine, 1,6-hexamethylenediamine, 1,7-heptanediamine, diethylenetriamine, xylyldiamine, 4, 7-dioxadecan-1, 10- -diamine, 1 ,2-diaminocyclohexane, bis(p-amìnocyclohexyl) -methane, 2,2-bis(4-aminocyclohexyl)propane, N,N-bis -(3-aminopropyl)methylamine, bis(hexamethylenetriamine) and a polymer containing at least about 1% weight pendant amine groups. 16. The cured product of Claims 14 or 15.

Inventors: BLANK, WERNER JOSEF, PAREKH, GIRISH GIRDHAR, SCHIRMANN, PETER JUDE
Applicants: AMERICAN CYANAMID COMPANY
Application year: 1980
Main classification: C07C69
IPC codes: C08F220, C09D133, C08F20, C08F22, C07C69, C07C325, C07C233, C07C205, C07C201, C07C313, C08F246, C07C67, C09D201, C07C229, C08F8, C07C323, C07C327, C07C227, D21H19, C08F218