AN ABSORBENT AND A METHOD OF ITS MANUFACTURE

Abstract: Method of fabricating an oil absorbent from sulphite-reject by subjecting this to an intensive heat reducing the water content of the reject. The heating rendering the material water repellent and oil absorbing. The adhesion between oil and agent being so strong that the mixture is no longer sticky.

Description: An absorbent and a method of its manufacture This invention relates to an absorbent, primarily for oil and the like, and to a method of manufacturing and using the abs¬ orbent. A burning problem has been and still is the removal of oil at various occasions, for example at tanker accidents and unint¬ entional oil discharges, which are large, for example from oil wells, or small, for example when tanks are being filled or the like. Also oil regaining in tankers after their unloading must be removed efficiently. In consideration of the serious damages caused by oil discharges, it is not surprising that a great number of different materials and methods have been invented for so-called oil control, which term per se illustrates the wide spectrum of the problems . For oil removal a great number of absorbents, and also bacteria for oil degradation, have been invented heretofore which cover everything from sand to cellulose products . At many occasions the absorbent also must permit its application in water, because many oil leakages occur in connection with water. Absorbents, therefore, preferably must be capable to float,and they further must not absorb water. A necessary property of the absorbent, therefore, often is hydrophoby. Many different methods for ach¬ ieving this are known already, and some of them have been used with some success for producing relatively good absorbing mat¬ erials, which do not absorb water to an appreciable degree. One disadvantage, however, is that these materials are relative¬ ly expensive, because the more efficient ones are based on relatively expensive starting materials. In many cases also the chemical treatment is expensive. Absorbents of the known types, therefore, cannot be imagined to be produced in large quantit¬ ies or be applied to oil disasters of substantial scope. This the more so as the oil after absorption remains sticky and therefore remains to be risk factor, even when the absorb¬ ent is applied excessively. The known absorbents are not cap¬ able, either, to absorb oil so efficiently that, for example, contaminated sand beaches become clean again. For this purpose chemical treatment or washing must be applied. Alternatively the effect of time and the degradation by bacteria are requir¬ ed. Degradation by bacteria, however, has the disadvantage that the bacteria do not work or survive at low temperatures. A further very essential disadvantage of the conventional abs¬ orbents is, that they certainly have a satisfactory effect on light oils, but give rise to problems as soon as the oils increasingly become heavier. This is a fact so widely adopted that tests with absorbents always are carried out with heating oil 1, i.e. a very light- oil fraction, especially when -consid¬ ering that at most of the serious oil discharges in connect¬ ion with tanker accidents and the like the oil involved is heavy oil. A further disadvantage of many oil control agents both of abs¬ orbing and other types is, that they sink to the bottom and gradually cause damage thereon. It is the object of the present invention to solve the afore¬ said problems by making available an absorbent, especially for oil control, which after having absorbed the oil is not sticky, is effcient also in the case of heavy oils, floats on water, s hydrophobic, is harmless for the environment per se and to¬ gether with the oil, and is very cheap, ao that it can be manuf¬ actured in the quantities required for large-scale rehabilit¬ ation. This object is achieved according to the present invention by an absorbent, which includes, to a large extent the fine fract¬ ion or null fibres in the reject especially from sulphite paper O PI mills where the moisture content in the reject is reduced by rapid forced heating. Due to the heating, the agent becomes hydrophcbic. After some longer time, of course, say about two, three days, also this absorbent will be moistened when lying in water. For marine use, therefore, he different particles of the absorbent pref¬ erably are to be coated with a thin wax coat, which must be insoluble in water but easily soluble for the oil or chemicals, against which the absorbent is to be applied. Referring to the rapid heating for reducing the moisture cont¬ ent and for effecting hydrophoby and oleophility, it can be mentioned that it was found by tests, that rapid heating res¬ ults in much better properties of the absorbent than slow heat¬ ing. The advantages of the present invention and its properties bec¬ ome apparent from the following description of experiments car ied out with material according to the invention. Experiments regarding the absorption capacity do not show sur¬ prising results with respect to the amounts absorbed. Although the material according to the invention, hereinafter called Bregoil, has a very low density, one litre Bregoil, of course, cannot absorb more than one litre oil minus its own volume, as is the case with all other absorbents. The great difference, however, is found in the speed at which Bregoil carries out the absorption. For conventional absorbents it takes several hours to become saturated with heating oil 1, but for Bregoil is takes only a few minutes. This rapid absorption obviously is an essential advantage, because then the oil cannot cause as much damage and especially the risk of its spreading is much smaller. At a further comparative experiment the aforesaid known mater¬ ials first were saturated with heating oil 1 for some In practice this implies, that about one gram absorbent absorb¬ ed about 8,5 gram oil. The saturated known absorbent then was placed upon Bregoil, but not mixed therewith. After some time the known absorbent and Bregoil were separated. It was found that Bregoil had absorbed over 1,5 gram oil from the known absorbent. Bregoil, thus, is more oleophilic, or can be said to have a higher oil-absorbing capacity than the known mater¬ ial. It possibly can be imagined ' that it is this property, which renders saturated Bregoil not to be sticky, because the Bregoil itself has a firmer grip on oil than any other mater¬ ial.. At experiments saturated Bregoil was placed for several months on sand and concrete and also on grass. No oil damages at all could be observed, nor were they even visible on the support. With Bregoil, thus, it is hot necessary to remove rehabilitated oil immediately, nor does it matter if small amounts of Bregoil with absorbed oil enclosed remain in the nature. It can possibly also be imagined to add oil degrading bacteria to Bregoil for effecting final rehabilitation in one operation. As regards the rapidity of absorption, it can also be mentioned that at experiments with heating oil 4, i.e. a relatively heavy' oil, it took 10-12 hours with Bregoil to absorb 85%, which can be compared with the aforesaid absorption time for the other agent in the case of heating oil 1. After Bregoil has absorbed oil and is saturated, it is possible, of course, after its collection to press out a certain oil amount by compressing Bregoil. The oil pressed out can be re- -used, and Bregoil together with the remaining oil can be com¬ busted without harmful side products resulting from Bregoil. As sulphite reject is a waste product from sulphite paper mills and heretofore has not been put to practical use, Bregoil can be manufactured cheaply and in very large quantities. The sul- ^Zπo-& J phite reject, of course, can be mixed with other suitable mat¬ erials prior or subsequent to the drying, for example with sulphate reject. It is, of course, not necessary, either, to exclusively use the fine fraction in the sulphite reject, but also the coarse fraction can be imagined to be used, although the favourable properties of Bregoil seem to originate from the fine fraction of the sulphite reject. The purely physical reason why Bregoil is so superior to other materials in its capacity of absorbing oil is not clear, but it can be imagined that the fibres in the fine fraction of sul¬ phite reject are fringy or are burst open at the rapid heat¬ ing, so that oil can be sucked into the fibres in a way diff¬ erent from that at other materials . As a result of this superior sucking capacity as demonstrated at the aforesaid experiments, the agent can also remove oil from sand, concrete, stone etc. Consequently, the agent cannot be used only for the removal of oil from a water surface, but also for removing oil from beaches, to which it adheres. Labor¬ atory tests have shown that, when oil at the ebbing tide of water precipitates on a sand beach, and Bregoil is sprayed over the oil during ebb tide, Bregoil sucks up the oil. At returning tide water Bregoil is lifted up together with the oil as a more or less coherent cake. The beach is clean, and Bregoil simply can be collected by pumps. Due to the fact that Bregoil better than other materials abs¬ orbs oil and after having absorbed oil is not sticky (most of the known oil absorbents practically are sticky although they do not absorb oil to 100%), it is possible to treat oil,and possibly more liquids detrimental to the environment than the aforementioned ones, in ways which heretofore w ere almost out of imagination. It can be imagined, for example, to clean oil tanks in tankers by spraying or applying Bregoil on the oil-contaminated surfaces and let it act thereon for some time, whereafter Bregoil can be flushed off together absorbed oil. Bregoild can then be filtered from the water. The problems caused by waste oil in the flushing water are hereby reduced and, besides, the oil tanks are cleaner, where¬ by the explosion risks are reduced substantially. It is, of'course, also imaginable to manufacture filters for water mixed with oil which permit the water to pass there¬ through, but absorb the oil. A further possible idea is to sinter together Bregoil or by means of nets or the like to collect Bregoil to booms for restricting the spread of oil. A further possibility of applying Bregoil is, in connection with oil discharge on water to discharge or spray Bregoil beneath the oil in the water, so that Bregoil rises to the oil and absorbs it from below. Hereby not only the risk of stickiness on the upper surface is reduced, but also on the lower surface, and.at the same time .the oil spots are better held together. This is essential especially in the case of heavy oil, because the heavy oil hereby can be collected much more simply than if it were sticky.-.Bregoil, namely, has the property of ad¬ hering even to heavy oil immediately. It may certainly take several hours for Bregoil to absorb the heavy oil, but it elim¬ inates the stickiness on the surface immediately. Heavy oil thus treated, i.e. sprayed on the lower and upper surface with Bregoil, can be collected immediately or whenever its collect¬ ing is deemed most suitable. The total absorption capacity for Bregoil is about seven litre oil per kilogram Bregoil. The Bregoil can possibly be manufactured in a plant of the kind shown in the accompanying drawing. Said plant comprises a furnace 2 with a burner 1, which heats the inlet air to a rotary drying chamber 4. Said chamber comprises several con¬ centric inner cylinders, which are flown through by air, which thereafter flows out at an outlet 5. The startinp; material for Bregoil, i.e. primarily sulphite reject, is supplied in a suit¬ able manner at 3. The sulphite reject here has a very high degree of moisture, but is dried in the chamber 4 to a moisture content of only a few per cent.At the outlet 5 from the drying chamber 4 a suction fan 6 is located, which ejects the air and the dried sulphite reject via a pipe to one or more cyclones 8 for separating air from Bregoil. The Bregoil then precipitates on the lower side of the cyclones 8 and is trans¬ ported away to be packed in a way not shown in detail. In the pipe from the fan 6 and, respectively, in the cyclones 8 nozzl¬ es can be arranged in a way not shown in detail for spraying a mist of chemically pure wax with a fusing point of proposedly 53 solved in ether petroleum, when Bregoil is desired to have long-time hydrophobic properties. No wax, however, must be added when this property is unessential. The hot air emitted from the plant can be utilized for heating or via heat exchang¬ ers be re-used in the plant for improving its economy. It is to be observed that Bregoil, though intended to be used primarily for oil, also can be used very well when other subst¬ ances detrimental to environment are to be rehabilitated, for example petroleum products and substances from the chemical ind¬ ustry. In addition to not being sticky, Bregoil also reduces the skidding risk. It further is to be pointed out that Bregoil does in no way chemically affect the oil or contaminates it in some other way, but the oil, to the extent it -can be pressed out of the Bregoil, can be used for the purpose it originally was intend¬ ed for.

Claims: Claims 1. An absorbent, especially for oil, petroleum products and similar chemicals harmful for the environment, c h a r a c t ¬ e r i z e d i n that it includes as essential constituent sulphite fibres and preferably the fine fraction of reject from a sulphite process, the moisture content thereof was reduced by rapid forced heating. 2. An absorbent as defined in claim 1, c h a r a c t e r ¬ i z e d i n that the separate particles of the absorbent are coated with wax. 3. An absorbent as defined in claim 2, c h a r a c t e r ¬ i z e d i n that the wax has a fusion point of about 53 C. 4. A method of manufacturing an absorbent, intended especi*- ally for oil, petroleum products and substances and chemicals harmful for the environment, c h a r a c t e r i z e d i n that the fine fraction in the sulphite reject or a mixture therewith as essential constituent is heated forcefully during a short period. 5. A method as defined in claim 4, c h a r a c t e r i z e d i n that the temperature during the drying is maitained between 300°C and 1000°C. 6. A method as defined in any one of the claims 4 or 5, c h a r a c t e r i z e d i n that the drying takes place with the raw material atomized more or less suspended in air with high temperature. 7. A method as defined in any one of the claims 4-8, c h a r a c t e r i z e d i n that the drying is effected by means of oil burner. $&*ιm\i 8. A method as defined in any one of the claims 4-7, c h a r a c t e r i z e d i n that the absorbent is coated with wax after the drying. 9. A method as defined in claim 8, c h a r a c t e r i z e d i n that the wax is applied solved in a volatile solvent, as for example ether petroleum, which thereafter is allowed to evaporate. " 10. A method as defined in any one of the claims 8 or 9, c h a r a c t e r i z e d i n that the wax solution is applied to the particles of the absorbent, in that .the part¬ icles are passed through a spray mist of solved wax. 11. A system for manufacturing an absorbent, .intended especi¬ ally for oil and the like, c h a r a c t e r i z e d i n that it comprises a boiler with burner for heating air, to the outgoing air of the boiler can be supplied via a connection sulphite reject or mixtures therewith as a main constituent in a drying chamber, where the particles to be dried partially are suspended freely in the air, that a fan is provided for sucking the dried sulphite reject particles out of the drying chamber and for supplying said particles to separation cyclones for separating the hot moist air from the sulphite reject now being dry, and that in the conduits to the cyclones and altern¬ atively in said cyclones spray nozzles are provided for wax coating the sulphite reject .particles by means of a wax mist. 12. A method for the absorbent according to any one of the preceding claims to recover or collect, for example, oil or other chemicals floating on water and harmful to the environ¬ ment, c h a r a c t e r i z e d i n that the absorbent is sprayed on the lower surface of the oil to be recovered. 13. A method of recovering. oil or chemicals on beaches, c h a r a c t e r i z e d i n that the absorbent according to any one of the preceding claims is distributed on the upper surface of the waste material, and the absorbent together with the oil sucked up is flushed off with water and collected, and alternatively the tide water is allowed to lift up the absorbent, so that it easily can be collected on the water surface together with the oil. 14. A method of cleaning oil tanks by the absorbent accord¬ ing to any one of the preceding claims, c h a r a c t e r i z- . e d i n that the absorbent is applied on the inner surfac¬ es of the oil tanks and, after having acted and sucked up the oil alternatively encased the same, is flushed of with water, from which the " absorbent together with the recovered oil is filtered off. 15. A filter for removing oil or similar substances harmful to environment from water, c h a r a c t e r i z e d i n that it consists of absorbent according to any one of the preceding claims which has been collected on a filter body, through which water can flow, but which has a large contact surface, so that all water passing through the filter is brought into close contact with the absorbent, which thereby is brought into contact with the oil, which hereby is absorbed. 16. A method of preventing oil damages on beaches, c h a r ¬ a c t e r i z e d i n that the absorbent according to any one of the preceding claims is spread out on the beach edge when oil is on its way to the beach, in such a manner, that the absorbent lies between the beach and the oil arriving at the beach, whereby the chances of the oil to contaminate the beach are reduced. OMPI ^^NATθ

Inventors: GRENTHE B
Applicants: GRENTHE B
Application year: 1980
Main classification: C09K3
IPC codes: B01J20, C09K3