PROCESS FOR THE CONTINUOUS PRODUCTION OF POLYBLENDS DERIVED FROM AN ALKENYL AROMATIC MONOMER AND A DIENE RUBBER

Abstract: In a process for the continuous mass polymerization of a solution comprising a alkenyl aromatic monomer having a diene rubber polymer dissolved therein, in which the solu­ tion is polymerized in a first reaction zone to about 15 to 50% conversion, whereby particles of the diene rubber are dispersed in a partially polymerized solution, followed by further polymerization of the partially polymerized solution in a second reaction zone to about 20 to 95% conversion, the size of the diene rubber particles can be controlled by having present in the solution, as fed to the first reaction zone, a polymer of the alkenyl aromatic monomer.

Description: PROCESS FOR THE CONTINUOUS PRODUCTION OF POLYBLENDS DERIVED FROM AN ALKENYL. AROSTIC MONOMER AND A DIENE RUBBER It is. known to polymerize solutions comprising alkenyl aromatic monomers having a diene rubber dissolved therein to form polyblends having a matrix phase of polymers of said monomers having dispersed therein particles oa said diene rubber grafted with said monomers. Mass and mass/suspension processes have been used to prepare such polyblends. U. S. Patent 3,903,202 is one such.suitable process for the continuous mass polymeriza tion of such polyblends and it is hereby incorporated by reference. The morphology of the rubber Particles dispersed in the polyblend is critical to the final properties of the polyblend. Generally, the larger the size of said rubber particles, the greater the toughness and the smaller the size, the higher the gloss. Hence, the size of the rubber particles must be controlled to insure the control of the properties of the polyblend. U. S. Patent 3,903,202 dis closes that agitation during the early phases of polymer ization disperses the dissolved rubber as particles and that higher rates of agitation generally decreases the size of said particles with lower rates of agitation producing larger particles. Controlling agitation rates then pro vides a means for sizing said rubber particles. It has been found that lower rates of agitation, however, creates problems of heat transfer and inhomogeneity that are diffi cult to control when operating at the lower agitation rates needed to produce larger particles. This is particularly true in continuous processes wherein large amounts of monomers are being polymerized and heat and homogeneity control are imperative to process and product control. The art has disclosed other methods for sizing the rubber particles other than by agitation rates. U. S. Patent 3,660,535 discloses a method wherein a.partially polymerized solution of rubber and monomers is recycled into a stratifying type polymerizing system having linear flow. The effluent from the first reactor, having a conversion of about 20 to 38%, is recycled as a partially polymerized solution in varying amounts to the feed stream at a location of essentially zero conversion and prior to phase inversion in the first reactor. This procedure has been found to vary the particle size of the rubber during the inversion of the rubber phase, however, control has been found to be difficult because the recycle stream contains grafted rubber particles that have varying levels of graft varying with levels of conversion in the recycle stream. The grafted rubber particles in the rubber phase has been found to act as a soap or dispersing agent for the rubber particles in the monomer-polymer phase during inversion of the two phases, hence, minor variations in graft or conversion have a profound effect on particle size control. This is particularly evident as polymerization is carried out in a linear flow stratifying reactor system wherein inversion gradually occurs as the feed stream is progressively polymerized from 0% to 20 to 38% conversion down through the stratified reactor. U., S. Patent 3,398,214 disclosed a batch mass poly merization process wherein a partially polymerized monomer batch of 30-40 conversion is blended with a partially polymerized rubber-monomer batch of less than 10% conversion and the blend is then completely polymerized by batch polymerization. The process is operable only when the monomer-rubber solution is prepolymerized to not greater than 10% conversion which provides very small rubber particles for high gloss in molded parts. High toughness is only developed when the monomer-rubber solution is polymerized to about 3% or less. Such processes do not provide high efficiency at such low conversions. U. S. Patent 3,488,743 discloses a process wherein a solution of monomer, low molecular weight rubbers and polymer are batch mass polymerized then finished by batch suspension polymerization. Such batch process produce polymers having relatively small rubber particles which do not efficiently toughen the polyblends having relatively low elongation at fail. Beyond properties, the batch processes require long conversion cycles to graft, invert and disperse the rubber phase, hence, having high energy requirements. The sequence of steps is critical in,providing the improved process. The first reaction zone is operating under steady state conversion of about 15 to 50% conversion, such that as said monomer-rubber solution enters said first reaction zone the dissolved rubber inverts into dispersed rubber particles. The first reaction zone is operating under back mixed steady state polymerization such that the partically polymerized solution is homogeneous as to temperature, viscosity and chemical composition causing said dissolved rubber to invert and be sized into rubber particles in a continuous and controlled operation. The improved process cf the present invention provides that the monomer-rubber solution has present a sufficient remount of a polymer of' said monomers such that said dissolved rubber phase inverts and is dispersed rapidly into rubber particles,- said rubber particles having higher levels of said polymer of said monomer 2S occluded polymer during inversion that controls the size and size distribu- tion of said particles. During the rapid inversion of the dissolved rubber, there is less grafted rubber particles in the rubber phase as a soap to decrease the particle size, hence, larger articles can e formed at the higher agitation rates needed for heat transfer. Here, the larger the concentration of the pcly..°r added to the monomer rubber solution, the larger the particle providing a means for readily controlling the rubber particle size. As the rubber particles move through the first and second reaction zones the rubber particles develop a grafted rubber phase which stabilizes the rubber particles at the size formed during inversion so that particle size is controlled in the final product. SUMMARY OF THE INVENTION The present invention relates to an improved process for the continuous mass polymerization of a solutidn comprising an alkenyl aromatic monomer having a diene rubber 'dissolved therein comprising the steps: A. continuously charging said solution of an alkenyl aromatic monomer having a diene rubber dissolved therein to a first flow through reaction zone, B. continuously pon etizing said solution under back mixed agitation and steady state conditions, said : :nonomer being polymerized to an average conversion of about 15 to 50% said diene rubber being dispersed as diene rubber particles waving present grafted and occluded polymers of said monomer in amounts of about 1 to 5 parts per part of said diene rubber, said solution becoming a partially polymerized solution, C. continuously withdrawing said partially polymerized solution from said first reaction zone, D. continudusly charging said partially polymerized solution to a second flow through reaction zone and further polymer izing said partially polymerized solution to about 20- to 95% conversion under sub stantially linear flow, t. continuously removing an effluent from said second reaction zone and continuously separating a polyblend from said effluent, said polyblend having a matrix phase com prising said polymerized monomer having dispersed therein said diene rubber par ticles, F. the improvement comprising: said solution being continuously charged in step (A) having present a polymer com prising said alkenyl aromatic monomer in amount sufficient to control the size of said rubber particles being dispersed in step (B). PREFERRED EMBODIMENTS Exemplary of the monomers that can be employed in the present process are styrene; alpha-alkyl monovinylidene monoaromatic compounds, e.g. alpha-methylstyrene, alphaethylstyrene, alpha-methylvinyltoluene, etc.; ring-substituted alkyl styrenes, e.g. vinyl toluene, o-ethylstyrene, p-ethylstyrene, 2,4-dimethylstyrene, etc.; ring-substituted halostyrenes, e.g. o-chlorostyrene, p-chlorostyrene, o- bromostyrene, 2,4-dichlorostyrene, etc.; ring-alkyl, ringhalo-substituted styrenes, e.g. 2-chloro-4-methylstyrene, 2,6-dichloro-4-methylstyrene, etc. If so desired, mixtures of such monovinylidene aromatic monomers may be employed. The alkenyl aromatic monomer can be used in combina tion with comonomers such as alkenyl nitrile; e.g., acrylonitrile methacrylonitrile, etc., or acrylates such as acrylic acid, methacrylic acid, methyl methacrylate, etc. The styrene-acrylonitrile monomers having, 1 to 15% by weight a diene rubber dissolved therein, can be¯continu- ously mass polymerized to polyblends known as ABS. Such polyblends can contain styrene and acrylonitrile type monomers in weight ratios of about 90:10 to 50:50 respectively, preferably 80:20 to 70:30 by weight. In addition to the monomers to be polymerized, the formulation can contain catalyst where required and other desirable components such as stabilizers, molecular weight regulators, etc. The polymerization may be initiated by thermal monomeric free radicals, however, any free radical generating catalyst may be used in the practice of this invention including actinic irradiation. Conventional monomer-soluble peroxy and perazo catalysts may be used. Exemplary catalysts are di-tert-butyl peroxide, benzoyl peroxide, lauroyl peroxide, oleyl peroxide, toluyl peroxide, di-tert-butyl diperphthalate, tert-butyl peracetate, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide isopropyl carbonate, 2,5-dimethyl-2, 5-dimethyl-2 ,5'-di- (tert-butylperoxy) hexane, 2,5-dimethyl-2,5-di(tert-butylperoxy) hexane-3 or hexyne-3, tert-butyl hydroperoxide, cumene hydroperoxide, p-menthane hydroperoxide, cyclopentane hydroperoxide, pinane hydroperoxide, 2,5-dimethylhexane-2,5-dihydroperoxide, etc., and mixtures thereof. The catalyst is generally included within the range of 0.001 to 3.0% by weight and preferably on the order of 0.005 to 1.0% by weight of the polymerizable material, depending primarily upon the monomer present. As is well known, it is often desirable to incorporate molecular weight regulators such as mercaptans, halides and terpenes in relatively small percentages by weight, on the order of 0.001 to 1.0% by weight of the polymerizable material. From 2 to 20% diluents such as ethylbenzene, ethyltoluene, ethylxylene, diethylbenzene or benzene may be added to the monomer composition to control viscosities at high conversions and also provide 'some molecular weight regulation. In addition, it may be desirable to include relatively small amounts of antioxidants or stabilizers such as the conventional alkylated phenols. Alternatively, these may be added during or after polymerization. The formulation may also contain other additives such as plasticizers, lubricants, colorants and non-reactive preformed polymeric materials which are suitable or dispersible therein. 'THE RUBBER SUBSTRATE Exemplary of the various rubbers onto which the polymerizable monomer formulation can be grafted during polymerization in the presence thereof to produce the graft copolymers are diene rubbers, natural rubbers, ethylenepropylene terpolymer rubbers, acrylate rubbers, polyisoprene rubbers and mixtures thereof, as well as interpolymers thereof with each other or other copolymerizable monomers. The preferred substrates, however, are diene rubbers (including mixtures of diene rubbers), i.e., any rubbery polymer (a rubbery polymer having a second order transition temperature not higher than 0 centigrade, preferably not higher than -20 centigrade, as determined by ASTM Test D-746-52T) of one or more of the conjugated, 1,3 dienes, e.g.. butadiene, isoprene, 2-chloro-1,3 butadiene, 1 chloro1,3-butadiene, piperylene,'etc. Such rubbers include copolymers and block copolymers of conjugated 1,3-dienes with up to an equal amount by weight of one or more' copolymer- izable monoethylenically unsaturated monomers, such as monovinylidene aromatic hydrocarbons (e.g. styrene; an aralkylstyrene, such as the o-, m- and p-methylstyrenes, 2 ,4-dimethylstyrene, the arethylstyrenes, p-tert-butylstyrene, etc.; an alphamethylstyrene, alphaethylstyrene, alpha-methyl-p-methyl styrene, etc.; vinyl naphthalene, etc.); arhalo monovinylidene aromatic hydrocarbons (e.g. the o-, m- and p-chlorostyrene, 2,4-dibromostyrene, 2 methyl-4-chlorostyrene, etc.); acrylonitrile; methacrylo nitrile; alkyl acrylates (e.g. methyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, etc.), the corresponding alkyl methacrylates; arcylamides (e.g. acrylamide, meth -acrylamide, N-butylacrylamide, etc.); unsaturated ketones (e.g. vinyl methyl ketone methyl isopropenyl ketone, etc.); alpha-olefins (e.g. ethylene, propylene, etc); pyridines; vinyl .esters (e.g. vinyl acetate, vinyl stear ate, etc.); vinyl and'vinylidene halides (e.g. the vinyl and vinylidene chlorides and bromides, etc.); and the like. Although the rubber may contain up to about 2.0% of a crosslinking agent,-based on the weight of the rubber forming monomer or monomers, crosslinking may present prob lems in ditssolving the rubber in the monomers for the graft polymerization reaction. In addition, excessive crosslink ing can result in los of the rubber characteristics. A-preferred group of rubbers are the stereospecific polybutadiene'rubbers formed by the polymerization of 1,3butadiene. These rubbers have a cis-isomer content of about 30-988 and a trans-isomer content of about 70-28 and generally contain at least about 85% of polybutadiene. formed by 1,4 addition with no more than about 15% by 1,2 addition. Mooney viscosities of the rubber (ML-4, 100"C) can range from about 20 to 70 with a second order transi tion temperature of from about -50 to -105 C. as determined by ASTM Test D-746-52T. GRAFTED RUBBER PHASE A monomer composition comprising at least one monoalkenyl aromatic monomer having about 2-15% by weight of a diene rubber dissolved therein is charged continuously as a monomer-rubber solution to the initial reaction zone. The monomer is polymerized at temperatures of about 1100- 1450 C. in the first zone' converting about 15-50% by weight of the monomer to a alkenyl aromatic polymer, already de scribed, as a first polymer. At least a portion of the first polymer polymerized is grafted as polymer molecules to the diene rubber as a superstrate. Although the amount of polymeric superstrate grafted onto the rubber substrate may vary from as little as 10.0 parts by weight to 100.0 parts of substrate to as much as 250.0 per 100.0 parts and even higher, the preferred graft copolymers will generally have a superstrate to substrate ratio of about 20 to 200:100 and most desirably about 30 to 150:100. With graft ratios about 30 to 150:100; a highly desirable degree of improvement in various properties generally is obtained. The remainder of the first polymer formed is dissolved in said monomer composition as polymerized forming a monomer-polymer solution. The monomer-polymer solution or phase is incompatibie with the monomer-rubber solution or phase and phase separation is observed by the well known Dobry effect. As the polymer concentration of the monomer polymer-phase increases and has a volume slightly larger than the monomer-rubber phase, the monomer-rubber phase disperses as rubber-monomer particles aided by the shearing agitation of the stirred first reaction zone. The agitation must be significant and of high enough shear to disperse and size the rubber particles uniformly throughout the monomer-polymer phase. The intensity of the stirring will vary with the size and geometry of the initial reactor, however, simple experimentation with a given stirred reactor will establish the sufficient amount of stirring needed to insure the homogeneous dispersion of the rubber particles throughout the monomer-polymer phase. The particle size of the rubber can be varied from a weight 'average particle diameter of from about 0.5 to 10 microns -preferably from 0.5 to 5 microns to provide a balance between the impact strength and the gloss of the rubber reinforced polyblend. Higher stirring rates and shearing agitation can lower the size of the dispersed rubber particle, hence, must be controlled to provide sufficient stirring to size the particles to the predetermined size needed and insure homogeneous dispersion. At steady state polymerization, in the initial polymerization zone, the continuously charged monomer composition containing 2 to 15% by weight diene rubber dispersed rapidly under stirring, forming the rub ber-monomer particles which on complete polymerization form discrete rubber particles. The conversion of monomers to polymers in the first reaction zone is controlled between 15-508 and must have a weight percent level that provides a polymer content in excess of the rubber content of the monomer composition to insure the dispersion 'of the monomer-rubber phase to a rubber-monomer particle phase having a predetermined size and being dispersed uniformly throughout the monomer-polymer phase. The rubber particle becomes grafted with a first polymer in the first reaction zone which aids'its dispersion and stabilizes the morphology of the particle. During the dispersion of the rubber-monomer particles, some monomerpolymer phase is occluded within the particle. The total amount of occluded monomer-polymer phase and grafted polymer present in the particles can be from about 1 to 5 grams for each gram said diene rubber. The dispersed rubber phase increases the toughness of the polymeric polyblend as measured by its Izod impact strength by Test ASTM D-256-56. It has been found that the impact strength of polyblends increase with the weight percent rubber dispersed in the polyblend in the range of 2 to 15% as used in the present invention. The impact strength is also determined by the size of the dispersed rubber particles, with the larger particles providing higher impact strength in the range of 0.5 to 10 microns measured as a weight average particle size diameter with a photosedimentometer by the published procedure of Graves, M. J. et.al., "Size Analysis of Subsieve Powders Using a Centrifugal Photosedimentometer," British Chemical Engineering 9:742744 (1964). A Model 3000 Particle Size Analyzer from Martin Sweets Co., 3131 West Market Street, Louisville, Kentucky was used. The weight average diameter of the rubber particles also effects gloss with smaller particles giving high gloss and the larger particles giving low gloss to the fabricated polyblend article such as a molding or sheet product. One must balance impact strength and gloss requirements in se lecting an optimum rubber particle size. The range of 0.5 to 10 microns can be used with the'range of 0.5 to 5 microns being preferred and 0.8 to 3 microns being most preferred for optimum impact strength and gloss. - Processwise, in the initial reactor, one must (1) form and disperse the rubber particle and (2) graft and stabilize the rubber particle maintaining its size and morphology or structure. The amount of occluded monomer-polymer phase described above is held at a predetermined level described above by steady state polymerization wherein the monomer is converted to polymer, at least a portion of which, grafts to the rubber stabilizing the rubber particle. It has been found that the higher the amount of occlusion stabilized within the rubber particle the more efficiently the rubber phase is used in toughening the polyblend. The rubber particle acts much as a pure rubber particle if the occlusions are controlled at the amount described above during their stabilization in the initial reaction zone and throughout the total polymerization process. The rubber particle is also grafted externally stabilizing its structure as to size and its dispersibility in the monomer-polymer phase. The initial reactor forms a first mixture or partially polymerized solution of a monomer-polymer phase having the rubber phase described dispersed therein. The first mixture can be charged to a staged isobaric reaction zone as a second zone and described herein. The first mixture is polymerized by progressive multistage substantial linear flow polymerizations with the conversion of polymer ad vancing from about 15-508 conversion in the first stage to 50 to 90% conversion in-the final stage of the staged isobaric stirred reaction zone as a second zone. This provides a gradual progressive increase of polymer in the monomer-polymer phase. This has been found to be important in maintaining the morphology or structure of the dispersed rubber-monomer particles. It has been found unexpectedly that in the initial reaction zone as the rubber particle is formed, that the rubber-monomer particle has a monomer content that corres- ponds to the monomer content of the monomer-polymer phase. The rubber-monomer particle will stabilize at this level as the monomer polymerizes inside the rubber particle and grafted polymer is formed on the outside. Hence it has been found that the lower the level of conversion or poly mer in the monomer-polymer phase of the initial reactor the higher the amount of monomer found in the rubber-monomer particles formed as the rubber solution is charged and dis persed in the monomer-polymer phase. Conversely, if the conversion is high in the initial stage less monomer is oc cluded in the rubber phase particle on dispersion. As de scribed earlier, the first mixture is polymerized in the staged linear flow second zone and the percent by weight of polymer being formed is progressively higher with each stage having a slightly higher polymer content. The staged linear progressive polymerization was found not only to control the polymerization of the monomer giving desirable polymers but was found unexpectedly to preserve the integrity of the rubber particles. Although not completely understood, as the rubber particle becomes grafted and the monomer-polymer phase forms in the occluded monomer of the rubber particle, the monomer is not readily extracted from the rubber particle by the monomer-polymer phase as the polymer content increases gradually in the monomer-polymer phase during polymerizing in the staged reactor. It is thought that since the polymrization in the multistaged linear reaction zone is so. gradual that polymer is being formed in both the rubber particle and the monomer-polymer phase at about the same rate, hence, the total polymer content of the occluded monomer-polymer phase of 'the rubber particle is about the same as polymer content of the monomer-polymer phase and monomer is not extracted, hence, the weight percent of occlusion is stabilized and remains sub stantially constant after formation in the initial reactor. It has been found possible to analyze the amount of total occluded polymer phase and grafted polymers. The final polymerized polyblend product (1 gram) are dispersed in a 50/50 acetone/methyl ethyl ketone solvent (10 ml.) which dissolves the polymer phase matrix leaving the rubber phase dispersed. The rubber phase is separated from the dispersion by centrifuge as a gel and dried in a vacuum oven at 500C. for 12 hours and weighed as a dry gel. % Dry gel ¯ Weight of dry gel x 100 in Polyblend - Weight of polyblend % Graft and ) Occlusions ) = % dry gel - % rubber x 100 in Rubber ) Percent rubber Parts ** by weight ) of graft polymer ) % dry gel - % rubber and occluded poly- ) : Percent rubber mer per unit weight ) of rubber ) Percent rubber determined by infra-red spectrochemical analysis of the dry gel The present invention preferably has present about 0.5 to 5 gram of occluded and grafted polymer per gram of diene rubber particle. The swelling index of the rubber graft particles is determined by taking the dry gel above and dispersing it in toluene for 12 hours. The gel is separated by centrifuge and the supernatant toluene drained free. The wet gel is weighed and then dried in a vacuum oven for 12 hours at 500C. and weighed. Swelling Index : weight of wet gel wgight Index = weight of dry gel As described earlier the amount of occlusions and graft polymer present in the rubber particle is present in the amount of about 0.5 to 5 part for each part of diene rubber. The percent dry gel measured'above then is the percent gel in the polymerized polyblend and represents the dispersed rubber phase having polymeric occlusions and polymeric graft. The percent gel varies with the percent rubber charged in the monomer composition and the total amount of graft and occluded polymer present in the rubber phase. The swelling index of the rubber as determined above is important to the final properties of the polyblend. A low swelling index indicates that the rubber has been crosslinked by the monomer as it polymerizes to a polymer phase in the rubber-monomer particle during steps (B) and (D). Generally, the conversion of monomer to polymer in the occlusion follows the rate of conversion of monomer to polymer in the monomer-polymer phase being carried out in steps (B) and (D). In step (E) the temperatures of the second mixture is raised to about 2000 to 2500C. and the monomer vapors are separated in step (E) to give a finished polyblend. The rubber particles become crosslinked by heating the second mixture to from about 2000 to 2500C. for sufficient time to crosslink the rubber particles such that they have a swelling index of from about 7 to 20 preferably from about 8 to 16. Preferably, the combined polymer of the matrix phase of the polyblends produced by this invention have a dispersion index (Mw/Mn), wherein Mw is a weight average molecular weight and Mn is a number average molecular weight, ranging from about 2.0 to 4.0 preferably 2.2 to 3.5. The dispersion index is well known to those skilled in the art and represents the molecular weight distribution with the lower values having narrow molecular weight distribution and higher values having broader molecular weight distribution. The weight average molecular weight of the combined polymer of the matrix phase preferable range from 150,000 to 300,000. SECOND REACTION ZONE POLYMERIZATION The second reaction zone polymerization can be carried out in a staged isobaric stirred reaction zone maintaining conditions so as to polymerize said first mixture by progressive multistage substantially linear flow polymerization all said stages operating with shearing agitation and common evaporation vapor phase cooling under isobaric conditions in said second reaction zone, providing each said stage with steady state polymerizatidn at controlled temperature and interfacial liquid contact stage to stage establishing a hydraulic pressure gradient from the first stage downstream to the Regnal stage causing substantially linear flow through said second zone, all said stages operating at predetermined conversion levels producing a composite polymer as a second polymer in said second reaction zone having a predetermined molecular weight distribution and average molecular weight maintaining the structural integrity of said dispersed rubber particle, said second zone producing a second mixture having a total polymer content being determined by said multistage steady state polymerization and evaporation of said monomers. The reactor operates under controlled isobaric conditions. For the range of temperatures normally of interest for alkenyl aromatic monomers, e.g. styrene polymerization (130-1800C.), the operating pressure will range from 0.49 to 1.97 Kg/cmê . The styrene reaction is exothermic,and cooling is provided primarily by vaporization of a part of the monomer from the reacting mass. Further cooling can be provided by a jacket. Cooling by the condensed recycle monomer feeding into either the first or second reaction zone is also provided. The mass is in a boiling condition and temperature is determined by the natural relationship between vapor pressure and boiling point. This relationship is also a function of the relative amounts of polymer, monomer, and other substances (e.g. dissolved rubber, solvents and additives). Since, as material progresses through this reactor the amount of polymer continuously increases and the amount of monomer corresponding decreases via polymerization and monomer content further decreases due to vaporization loss, the temperature progressively increases from inlet to outlet stages. To accommodate the natural swell of the boiling mass and to provide space for vapor disengagement, the reactor is usually run at a fillage of about 10 to 90% preferably 40 to 60% of its volume. Vapor passes out of the reactor to an external con denser where it is condensed and may also be sub-cooled. This condensate may then be handled in several ways, for example: 1. If the reactor used this invention is- preceded by another reactor in a multi reactor train, the condensate may be're- turned to a preceding reactor. 2. The condensate may be returned to the inlet compartment of the reactor that used this invention, wherein it is re heated by condensation of a fraction of the previously evolved vapors and mixed other incoming free materials. In a multi-compartment staged reactor, each stage is well mixed and the reaction mass is substantially homogeneous within itself. The discs which separate the stages discourage backflow of material between compartments. The clearance between disc and shell does permit some backflow and also permits the necessary forwarding of material through the compartments from reactor inlet to. outlet giving substantially linear flow. In a compartmented staged reactor as here described, the first stage has a relatively low conversion level, since it is being continuously fed by monomer and low conversion prepolymerized syrup. However, the rate of conversion in this stage is relatively high because of the high concentration of monomer. In each succeeding stage, the conversion level is higher than in the preceding one, which tends to lower the rate of conversion. Offsetting this effect, however, are the facts that the temperature is higher and that monomer is being vaporized out of the mass. Thus, the total conversion-to polymer obtained per unit fillage volume of the staged reactor is higher than that which could be obtained in a single stage reactor producing an equal final conversion level at equal temperature. Clearance between rotating disc compartment baffles and cylindrical wall may be from 1 to 10% of shell radius, the larger values being appropriate to the high conversion end of the reactor where viscosity. is at maximum. Stage to stage forward flow of the polymerizing first mixture is through this clearance and vapor from the polymerizing first mixture also counterflow through the clearance, above the surface level of the mass. If the alkenyl monomer is used in combination with an alkenyl nitrile monomer, operations are essentially the same except for controlling the styrene-acrylonitrile composition of the monomers during polymerization. The styrene type monomer adds to the copolymer at a faster rate than the acrylonitrile monomer, hence, the acrylonitrile monomer is generally charged'at higher weight percentages in the charged monomer formulation to insure a desired weight percent in the polymerized copolymer. The two monomers form an azeotrope at about 75% styrene and 25% acrylonitrile so that no shift in monomer or polymer composition occurs during polymerization, hence, generally the azeotropic monomer mixture is used in the continuous mass polymerizing of ABS polyblends from monomer-rubber solutions. The polyalkenyl aromatic monomer. polymer or copolymer to be dissolved in the monomer-rubber solutions to be fed in step (A) is preferably a polystyrene type polymer or styrene-acrylonitrile type copolymer having a weight average molecular weight of about 20,000 to 300,000 preferably about 150,000 to 250,000. The matrix polymer or copolymer can have a weight average molecular weight of about 150,000 to 300,000. The amount of polymer or copolymer to be added is dependent on the particle size desired in the polyblend. Generally, the more polymer-present, the larger is the rubber particle size as dispersed. The amount to be used is also based on the amount of rubber dissolved in the monomer to be fed in step (A). The amount of polymer or copolymer present in the monomer-rubber solution is about 10 to 150% by weight based on the diene rubber dissolved in said monomer, e.g. if the rubber is present in an amount of about 10 parts in the solution then the polymer or copoly mer can be present in an amount of about 1 to 15 parts. The following examples are set forth to more clearly illustrate the principles and practice of the present in vention. They are intended to be illustrative and not limiting as to the scope of the invention EXAMPLE 1 - CONTROL A monomer composition consisting of 5 parts by weight of stereospecific polybutadiene ruberin 95 parts by weight of styrene monomer is prepared by agitating the mixture at 40 C. for 8 hours. The rubber used contains approximately 35% cis-1,4 structure; approximately 55% trans-l,4 structure and approximately 10% vinyl-1,2 struc- ture naming a Mooney viscosity of the rubber (ML-4, 1000C.J at 55. To the above monomer composition is added 0.5 parts of white mineral oil, 0.1 part by weight of octadecyl 3-(3',5'-di-tertbutyl-4-hydroxyphenyl) propion ate and 40 parts by weight of recycled styrene monomer. This monomer composition is fed continuously at approxi mately 65.8 Kgm./hr. to a 379 1. , anchor-agitated initial reactor operated at approximately 508 fillage and 1240C, under 1.36 Kg/cm2 nitrogen pressure. The agitator is approxi mately 79 cm. wide and turns at 65 rpm. A first mix- ture containing approximately 18% polystyrene is.pumped from the above reactor at a continuous rate such as to maintain essentially constant fillage therein and flows to the inlet of the second reactor, a staged isobaric stirred reactor. The second reactor has approximately a 189 1. capacity and operates at about 40$ fillage. The reactor is about 135 cm. long. The agitator consists of a horizontal shaft'on which are fixed a series of paddles about 5 Cm. wide alternating at right angles to one another in a manner similar to that shown in U. S. Patent 3,903,202. Along the shaft and rotating with it are four circular discs'with an average radial wall clearance of about 0.95 cm. rotating at 15 rpm. These discs are positioned to divide the reactor into five stages of approximately equal volume. The pressure in this reactor is maintained at approximately 1.41 Kg/cmê. The second mixture in the final stage is maintained at about 166 C. and contains about 62% polystyrene. Styrene vapor-evaporated from the second reactor is condensed and the condensate is returned to the first compartment. The second mixture is pumped continuously from the final stage at a rate to maintain essentially constant fillage in the second reactor and is delivered to the inlet of the devolatilizer preheater. The second mixture exits from the preheater at approximately 240 C. and enters a devolatilizer chamber maintained 2 at 0.069 Kg/cm . Second mixture volatile vapors exiting the devolatilizer chamber are condensed and recycled to the first reactor preheater.feed system. Approximately 1.36 Kg/hr. of the condensed devolatilized vapors are withdrawn as purge. The devolatilized melt is fed from the devolatilizer chamber an extruder which forms it into a plurality of strands which are then cooled and cut into pellets. The combined polymer has a molecular weight of about 210,000 and a dispersion index about 3.1. Typical Properties Izod Impact 1.25 cm. x 1.25 cm. 23 C. Kg.cm/cm.notch bar 7.1 Tensile strength at yield kg/cm2 267.1 Tensile strength at fail kg/cm2 263.6 Tensile elongation at fail (Z) 62 Swelling index 9 Parts graft and occlusions/rubber 1.43:1 Rubber particle size (microns) 1.5 EXAMPLE 2 Example 1 was repeated using 5 parts of rubber and 6 parts of polystyrene having a molecular weight of about 210,000 dissolved in 89 parts of styrene monomer. The monomerrubber-polystyrene composition was fed continuously as in Example 1. The dispersed rubber phase of the poly merized polyblend had an average rubber particle size of about 5 microns and an impact strength of about 9.6 kg.cm/cm. notch. EXAMPLES 3-12 Example 1 was repeated using varying amounts of dissolved-rubber and polystyrene in the monomer-rubber solution. Rubber Impact Rubber Polystryene Particle Strength Example Parts Parts Size( Kg cm/cm notch 3 5 3 2.4 8.2 4 5 1 1.6 7.6 5 7.5 10 7.3 12.0 6 7.5 5 6.2 10.4 7 7,5 3 3.6 10.1 8 7.5 0 1.0 6.5 9 10 12 9.3 14.0 10 10 6 7.6 12.5 11 10 3 4.2 10.19 12 10 0 1.6 8.7 EXAMPLE 13 - CONTROL Example 1 was repeated using 5 parts of the diene rubber dissolved in 95 parts of styrene and acrylonitrile monomers wherein the weight ratio of styrene to acrylonitrile was 75 to 25. The ABS polyblend produced had a rubber particle size of about 0.9 microns and an impact strength of about 19.1 kg.c/cm. notch. EXAMPLE 14 Example 13 was repeated using a feed stream of 90 parts of styrene-acrylonitrile monomers having a styrene to acrylonitrile weight ratio of 75 to 25 having dissolved therein about 5 parts of a polybutadiene rubber and 5 parts of a styrene-acrylonitrile copolymer having a composition of the monomer feed stream and a weight average molecular weight of about 200,000. The ABS polyblend recovered had a particle size of about 4.3 microns and an impact strength of about 35 Kg cm/cm notch. It is evident from Examples 1-12 that the size of the rubber particle can be readily changed and controlled by the' amount of dissolved polymer present in the monomerrubber solution keeping the rate of agitation essentially constant. As disclosed supra, the present invention of controlling rubber particle size is preferred and superior to regulating particle size by agitation rates in that agitation rate variations upset reactor conditions such as heat control and polymerization kenetics. EXAMPLE 15 Example 1 was repeated using an agitation rate of about go rpm in the first reaction zone and an average particle size of about 0.5 microns was formed. EXAMPLE 16 Example 15 was repeated using about 5 parts of poly styrene dissolved in the monomer-rubber solution fed to the first reaction zone and an average particle size of about 1. 75 microns was formed. It is evident that the present process can .be operated such that a wide range of particle sizes can be produced consistent with the balance of impact strength and gloss desired. The present process as demonstrated in the examples removes a reaction mixture from second reaction zone defined as the second mixture or effluent from the second reaction zone. Said effluent contains the matrix phase polymer having dispersed therein the grafted rubber par tides as a polyblend containing residual unpolymerized monomers. The effluen. is heated and passed .through a devolatilizer and the monomers separated from the polyblend as volatile vapors for recycle to the process. The polyblend is removed from the devolatilizer as a melt and passed through a pelletizing die providing a polyblend in pellet form having utility as.a plastic for molding or extrusion fabrication. The present process has been adapted to a second reaction zone described as a flow through reaction zone wherein the partially polymerized solution is polymerized further to about 20 to 95% conversion under substantially linear flow. The second reaction zone hereindescribed is -adaptable to such polymerization. Other types of second reaction zones can be adapted to the present process such as continuous flow through towers (one or more) having substantially plug or linear flow through a plurality of stages or temperature zones that gradually increase the temperature to finish the polymerizatidn. Various tube reactors have been used in the art as continuous flow through reactors having substantially linear or plug flow which can be adapted to the present process. Hence, the particular reactor used as a second reaction zone can be of the several types known to the art providing the second reaction zone provides continuous flow through and sub stantially linear flow capability to further polymerize the partially polymerized 'solution from the first reaction zone.

Claims: CLAIMS 1. An improved process for the continuous mass polymerization of a solution comprising an alkenyl aromatic monomer having a diene'rubber dissolved therein comprising the steps: A. continuously charging said solution of an alkenyl aromatic monomer having a diene rubber dissolved therein to a first flow through reaction zone, B. continuously polymerizing said solution under back mixed agitation and steady state conditions, said monomer being polymerized to an average conversion of about 15 to 50%, said diene rubber being dis persed as diene rubber particles having present grafted and occluded polymers of said monomer in. amounts of about 1 to 5 parts per part of said diene rubber, said solution becoming a partially polymerized solution, C. continuously withdrawing said par tially polymerized solution from said first reaction zone', D. continuously charging said partially polymerized solution to a second flow through reaction zone and fur ther polymerizing said partially polymerized solution to about 20 to 95% conversion under substantially linear flow, E. continuously removing an effluent from said second reaction zone and continuously separating a polyblend from said effluent, said polyblend having a matrix phase comprising said polymerized monomer having dispersed therein said diene rubber particles, characterized wherein said solution being continuously charged in step (A) has present therein a polymer including said monomer in amount sufficient to control the size of said rubber particles being dispersed in step (B). 2. A process of Claim 1 wherein said alkenyl aromatic monomer is styrene, Oc-methylstyrene, chlorostyrene, dichlorostyrene, bromostyrene or dibromostyrene or mixtures thereof. 3, A process of Claim 1 wherein said diene rubber is polybutadiene, polyisoprene, poly-2-chlorobutadiene, poly-l-chlorobutadiene, copolymers and block copolymers of butadiene-styrene, butadiene chloroprene, chloroprene-styrene, chloroprene-isoprene, 2-chlorobutadiene-l-chlorobutadiene or mixtures thereof. -4. A process of Claim 1 wherein said diene rubber is polybutadiene. 5. A process of Claim 4 wherein said polybutadiene rubber has a cis isomer content of 30 to 98 percent and a Tg range of from -500C. to -1050C. 6. A process of Claim 1 wherein said alkyl aromatic monomer is styrene. 7. A process of Claim 1 wherein said first reaction zone operates with essentially constant fillage of 10 to 90% of its volume with said solution at a temrerature of 100 to 140 C. and under a pressure of 1 Kg/cmê to 11.6 Kg/cmê with isothermal and steady state polymerization. 8. A process of Claim 1 wherein said second reaction zone is a staged, isobaric, stirred reaction zone, said partially polymerized solution being polymerized by progressive multistage substantially linear flow polymerization, all said stages operating with agitation and common evaporative vapor phase cooling under isobaric conditions, providing each said stage with steady state polymerization at a controlled temperature of 130 to 180 C. and a pressure of 0.49 to 1.97 Kg/cmê. 9. A process of Claim 1 wherein the continuous charging of said solution in step (A) is at a rate about equal to the rate at which said effluent is removed in step (E). 10. A process of Claim 1 wherein said solution has present 0.001 to 3.0 percent by weight of a free radical generating catalyst of di-tert-butyl peroxide, tert-butyl peracetate, benzoyl peroxide, lauroyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide and isopropyl carbonate or mixtures thereof.

Inventors: BURK, RAYMOND DAVID
Applicants: MONSANTO COMPANY
Application year: 1980
Main classification: C08F279
IPC codes: C08F291, C08F279, C08F2