ALKYLATION OF AROMATIC HYDROCARBONS

Abstract: A process for the alkylation of aromatic hydrocarbons with alkylating agents having from one to five, and prefer­ ably three to five, carbon atoms. The reactants are brought into contact, preferably in the liquid phase, in the presence of a crystalline zeoiite catalyst characterized by a silica to alumina ratio of at least 12 and a constraint index within the approximate range of 1-12. The reaction is conducted at 100° C to 300° C and a pressure of from about 10⁵ N/m² to about2 × 10⁷ N/m².

Description: ALKYLATION OF AROMATIC HYDROCARBONS This invention is directed to the catalytic alkylation of aromatic hydrocarbons, particularly in the liquid phase. Alkylation of aromatic hydrocarbon compounds employing certain crystalline zeolite catalysts is known, for instance from U.S. 3,251,897 which describes liquid phase alkylation in the presence of crystalline aluminosilicates such as faujasite, heulandite, clinoptilolite, mordenite, dachiardite, zeolite X and zeolite Y. The temperature of such alkylation procedure does not exceed 315.550C (6000F.), thereby maintaining the operating phase substantially liquid. U.S. 2,904,607 describes alkylation of hydrocarbon compounds in the presence of crystalline metallic aluminosilicates such as magnesium aluminosilicates. U.S. 3,631,120 and 3,641,177 describe liquid phase processes for alkylation of aromatic hydrocarbons with olefins in the presence of certain zeolites. U.S. 3,631,120 discloses use of an ammonium exchanged, calcined zeolite having a silica to alumina mole ratio of between 4.0 and 4.9. U.S. 3,641,177 discloses use of a zeolite catalyst activated in a particular manner. U.S. No. 3,755,483 discloses that the vapor phase reaction of propylene with benzene and toluene in the presence of zeolite ZSM-12 proceeds with high catalyst and activity selectivity to yield isopropylbenzene and isopropylmethylbenzene, but with operation in the vapor phase with relatively high temperatures and pressures, thereby promoting dealkylation and olefin decomposition which is especially evident when the alkylating agent comprises an olefin of three or more carbon atoms. A process has now been discovered whereby aromatic hydrocarbons, containing either polar or non-polar substituents, may be successfully alkylated with olefins or alcohols containing from one to five carbon atoms. Surprising and substantial increases in product yield, conversion and selectivity are obtained by operating at lower temperatures than heretofore and essentially in the liquid phase. This increase is especially evident when alkylating agents of three or more carbon atoms (where higher temperatures promote dealkylation and olefin decomposition) are used. According to the present invention a process for the alkylation of an aromatic hydrocarbon compound comprises contacting such compound with an alkylating agent having from one to five carbon atoms, preferably in the liquid phase, at a temperature between 1000C and 3000C and a pressure between 105 N/m2 and 2 x 107 N/m2 in the presence of a catalyst comprising a zeolite having a silica to alumina ratio of at least 12 and a constraint index from 1 to 12. The process is advantageously carried out at a temperature between 2000C and 2500C. A suitable aromatic/alkylating agent mole ratio is the range 20:1 to 1:1. The process is usually operated at a WHSV (with reference to total catalyst) of 0.1 to 100. The aromatic hydrocarbon may bear a polar or non-polar substituent; and the preferred alkylating agent is an olefin, particularly one having at least three carbon atoms. Alcohols; however, are also favoured alkylating agents. The zeolite is preferably ZSM-12; and in many applications the zeolite is composited with a binder. The significance and manner of determination of a zeolite's "constraint index'1 has been widely described in the Patent literature, for instance in British Specification 1,446,522. The Constraint Index approximates the ratio of the cracking rate constants for the two hydrocarbons. Zeolites suitable for the present invention are those having a Constraint Index of 1 to 12. Constraint Index (Cl) values for some typical zeolites are: ZEOLITE C.I. ZSM-5 8.3 ZSM-11 8.7 ZSM-12 2 ZSM-23 9.1 ZSM-35 4.5 ZSM-38 2 TMA Offretite 3.7 Beta 0.6 ZSM-4 0.5 H-Zeolon (mordenite) 0.4 REY 0.4 Amorphous Silica Alumina 0.6 Erionite 38 The nature of this parameter and the technique by which it is determined admit the possibility that a given zeolite can be tested under somewhat different conditions and thereby have different Constraint Indexes. Constraint Index seems to vary somewhat with severity of operation (conversion) and the presence or absence of binders. Therefore, it will be appreciated that it may be possible to so select test conditions to establish more than one value in the range of 1 to 12 for the Constraint Index of a particular zeolite. Such a zeolite is to be regarded as having a Constraint Index of 1 to 12. Also contemplated herein as having a Constraint Index of 1 to 12 and therefore within the scope of the novel class of highly siliceous zeolites are those zeolites which, when tested under two or more sets of conditions produce a value of the Constraint Index slightly less than 1, e.g. 0.9, or somewhat greater than 12, e.g. 14 or 15, with at least one other value within the range 1 to 12. The preferred zeolites are exemplified by ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, identified respectively by the x-ray data presented in U.S. 3,702,886, 3,709,979, 3,832,449, 4,076,842, 4,016,245 and 4,046,859. The specific zeolites described, when prepared in the presence of organic cations, are substantially catalytically inactive, possibly because the intracrystalline free space is occupied by organic cations from the forming solution. They may be activated by heating in an inert atmosphere at 54O0C for one hour, for example, followed by base exchange with ammonium salts followed by calcination at 5400C in air. The presence of organic cations in the forming solution may not be absolutely essential to the formation of this type zeolite; however, the presence of these cations does appear to favor the formation of this special class of zeolite. More generally, it is desirable to activate this type catalyst by base exchange with ammonium salts followed by calcination in air at about 5400C for from about 15 minutes to about 24 hours. Natural zeolites may sometimes be converted to this type zeolite catalyst by various activation procedures and other treatments such as base exchange, steaming, alumina extraction and calcination, in combinations. Natural minerals which may be so treated include ferrierite, brewsterite, stilbite, dachiardite, epistilbite, heulandite, and clinoptilolite. In a preferred aspect of this invention, the zeolites hereof are selected as those having a crystal framework density, in the dry hydrogen form, of not less than about 1.6 grams per centimeter. The significance and manner of determination of crystal density are also described in the aforesaid British Specification 1,446,522. Crystal framework densities of some typical zeolites, including some which are not within the purview of this invention, are: Void Framework Zeolite Volume Density Ferrierite 0.28 cc/cc 1.76 g/cc Mordenite .28 1.7 ZSM-5, -11 .29 1.79 ZSM-12 1.8 ZSM-23 2.0 Dachiardite .32 1.72 L .32 1.61 Clinoptilolite .34 1.71 Laumontite .34 1.77 ZSM-4 (Omega) .38 1.65 Heulandite .39 1.69 P .41 1.57 Offretite .40 1.55 Levynite .40 1.54 Erionite .35 1.51 Game lignite .44 1.46 Chabazite .47 1.45 A .5 1.3 Y .48 1.27 When synthesized in the alkali metal form, the zeolite is conveniently converted to the hydrogen form, generally by intermediate formation of the ammonium form as a result of ammonium ion exchange and calcination of the ammonium form to yield the hydrogen form. In addition to the hydrogen form, other forms of the zeolite wherein the original alkali metal has been reduced to less than about 1.5 percent by weight may be used. Thus, the original alkali metal of the zeolite may be replaced by ion exchange with other suitable ions of Groups IB to VIII of the Periodic Table, including, by way of example, nickel, copper, zinc, palladium, calcium or rare earth metals. In practicing the desired conversion process, it may be desirable to incorporate the above described crystalline zeolite in another material resistant tc the temperature and other conditions employed in the process. Such matrix materials include synthetic or naturally occurring substances as well as inorganic materials such as clay, silica and/or metal oxides. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Naturally occurring clays which can be composited with the zeolite include those of the montmorillonite and kaolin families, which families include the sub-bentonites and the kaolins commonly known as Dixie, McMamee-Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. In addition to the foregoing materials, the zeolites employed herein may be composited with a porous matrix material, such as alumina, silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-berylia, silica-titania as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix may be in the form of a cogel. The relative proportions of zeolite component and inorganic oxide gel matrix on an anhydrous basis may vary widely, with the zeolite content ranging from between about 1 to about 99 percent by weight and more usually in the range of about 5 to about 80 percent by weight of the dry composite. Exemplary of the hydrocarbons which may be alkylated by the process of this invention are aromatic compounds such as benzenes, naphthalenes, anthracenes, and the like and substituted derivatives thereof; and alkyl substituted aromatics, e.g. toluene, xylene, and homologs thereof. In addition, other non-polar substituent groups may also be attached to the aromatic ring, including by way of example methyl, ethyl, t-butyl, alkyl, cycloalkyl, phenyl and aryl. Aromatic hydrocarbons which may be alkylated by the present process likewise include those having polar substituents on the aromatic ring or on a side chain attached thereto. Non-limiting examples include phenol, cresols and halogenated aromatics. The preferred alkylating agents are olefins, formaldehyde, alkyl halides and alcohols. Numerous other acyclic compounds having at least one reactive alkyl radical may be used. The process may be carried out as a batch-type, semi-continuous or continuous operation utilizing a fixed, fluidized or moving bed catalyst system. A preferred embodiment entails use of a fluidized catalyst zone wherein the reactants are passed concurrently or countercurrently through a moving fluidized bed of the catalyst. The fluidized catalyst after use is conducted to a regeneration zone wherein coke is burned from the catalyst in an oxygen-containing atmosphere, e.g. air, at an elevated temperature, after which the regenerated catalyst is recycled to the conversion zone for further contact with the reactants. Subsequent to leaving-the reaction zone, the desired products may be recovered from the reactor effluent, for instance by distillation, and the unreacted hydrocarbons recycled for reuse in the process. The following examples illustrate the process of this invention without limiting the scope or utility thereof. The catalyst in all cases comprised 4.6 gms of ZSM-12 prepared as disclosed in U.S. 3,832,449 and consisted of 65 wt 7o HZSM-12 and 35 wt % Al203 binder. The reaction products were analyzed with a gas chromatograph equipped with a hot wire detector. Positive identification of the various compounds was made with GC/MS, IR, and/or NMR. Example 1 Benzene was alkylated with methanol at 2500C. and atmospheric pressure using HZSM-12 extrudate as catalyst. At this relatively low temperature 90% of the methanol was converted to benzene alkylation products. Table I shows the product selectivity and also the isomer distribution of the methylbenzenes that were produced. Reactor temperatures from 2000C to 3O00C were explored. Below about 2400C there was a rapid decline in methanol conversion and at 2000C the conversion was essentially zero. Above about 2600C no additional alkylation products were formed. The main alkylation products were toluene and xylenes. The xylene fraction, formed by alkylation of the toluene, amounted to 15% of the total product and was unusual in that the ortho isomer predominated. The actual isomer distribution was 47%ortho, 40%-meta, 13%-para. Using unmodified HZSM-5 (U.S. Patent No. 3,702,886) as catalyst and similar experimental conditions, the xylene isomer ratio was 22%-ortho, 54%-meta and 249o-para. Since the methylation of toluene is ortho directing it would appear that the initially formed ortho isomer is only partially isomerized by HZSM-12 whereas with HZSM-5 isomerization to equilibrium occurs. TABLE 1 BENZENE ALKYLATION WITH METHANOL OVER HZSM-12 FEED: 7/1 BENZENE/METHANOL - MOLE/MOLE TEMPERATURE: 250 C PRESSURE: ATMOSPHERIC WSHV: 5.8 BENZENE - 0.3 METHANOL CONVERSION-WT%: 10% BENZENE - > 90% METHANOL COMPOUND WT% SELECTIVITY ISOMER DISTRIBUTION TOLUENE 73.0% XYLENES 15.0% PARA - 13.0% META - 40.0% ORTHO - 47.0% C9 4.5% 1,3,5 - TRIMETHYLBENZENE - 23.0% 1,2,4 - TRIMETHYLBENZENE - 67.0% 1,2,3 - TRIMETHYLBENZENE - 10.0% C10 4.5% 1,2,3,4 - TRIMETHYLBENZENE - 55.0% 1,2,3,5 - TRIMETHYLBENZENE - 37.0% 1,2,3,4 - TRIMETHYLBENZENE - 8.0% C11 3.5% PENTAMETHYLBENZENE - 100.0% C11+ 1.5% HEXAMETHYLBENZENE - 40.0% UNKNOWN - 60.0% Examples 2-5 Benzene was alkylated with C3 through C5 alkenes in the presence of HZSM-12, at various temperatures and pressures. The reactions are summarized in Table II. TABLE II BENZENE ALKYLATION OVER HZSM-12 ALKYLATING BENZENE/ALKYLATING %CONVERSION PRODUCTS-% EXAMPLE AGENT TEMP. C PRESSURE WHSV AGENT MOLE RATIO ALKYLATING AGENT SELECTIVITY 1 METHANOL 250 ATMOSPHERIC 6 7/1 > 90 TOLUENE-73% XYLENE-15% C9.4,5% C9.7,5% 2 PROPYLENE 200 2169.76 kPa 6 7/1 > 95 ISOPROPYL (300 psig) BENZENE-92% DIISOPROPYL BENZENE-7.5% 3 1-BUTENE 190 2514. kPa 6 7/1 > 95 SEC-BUTYL OR 2-BUTENE (350 psig) BENZENE-95+% 4 ISOBUTYLENE 190 2514.14 kPa 6 7/1 > 95 TERTIARY (350 psig) BUTYLBENZENE -95+% 5 2-METHYL BUTENE-90% 200 2514.49 kPa 6 7/1 > 95 TERTIARY (350 psig) PENTYL BENZENE-52% 2-PENTENE-10% 1,2-DIMETHYL PROPYL BENZENE-38% The data illustrates the exceptional alkylation activity and selectivity of ZSM-12 catalyst at temperatures of 25O0C and below, particularly with respect to alkylating agents C3 and higher. Example 6 Toluene was alkylated with methanol in the presence of HZSM-12 catalyst at 2500C and atmospheric pressure. The operating conditions and products formed are shown in Table III. TABLE III TOLUENE ALKYLATION WITH METHANOL OVER HZSM 12 FEED: 2.2/1 TOLUENE/METHANOL - MOLE RATIO TEMPERATURE: 250 C PRESSURE: ATMOSPHERIC WHSV: 11.5 TOLUENE - 1.8 METHANOL CONVERSION - WT%: 28% TOLUENE - 70% METHANOL COMPOUND WT% SELECTIVITY ISOMER DISTRIBUTION XYLENES 76.0 PARA - 14.0% META - 25.0% ORTHO - 61.0 C9 16.0 1,3,5-TRIMETHYLBENZENE - 3.0% 1,2,3 - TRIMETHYLBENZENE - 75.0% 1,2,3 - TRIMETHYLBENZENE - 22.0% C9+ 8.0 Examples 7-10 Toluene was alkylated with C2 through C4 olefins in the presence of HZSM-12 catalyst at a variety of temperatures and pressures. Table IV is a summary of the reaction conditions and products formed. TABLE IV TOLUENE ALKYLATION OVER HZSM-12 ALKYLATING TOLUENE/ALKYLATING %CONVERSION PRODUCTS-% EXAMPLE AGENT TEMP C PRESSURE WHSV AGENT MOLE RATIO ALKYLATING AGENT SELECTIVITY 6 METHANOL 250 ATMOSPHERIC 11 22/1 70 XYLENES - 76% (61% ORTHO 25% META14% PARA) C9 - 16% C9+ - 8% 7 ETHYLENE 300 ATMOSPHERIC 6 7/1 60 ETHYLTOLUENE (40% ORTHO 38% META 22% PARA 8 PROPYLENE 250 3548.7 kPa 6 7/1 > 95 ISOPROPYL (500 psig) TOLUENE-95% (32% PARA 62% META 6% ORTHO 9 1-BUTENE or 2-BUTENE 200 2169.76 kPa 6 7/1 > 95 SECONDARY (300 psig) BUTYLTOLUENE 95%(60% PARA 40% META 10 ISOBUTYLENE 190 2169.76 kPa TERTIARY (300 psig) BUTYLTOLUENE 95% (60% PARA, 35% META Toluene alkylation differs from benzene alkylation in that the initial alkylation-product consists of isomers. Although the reactions with toluene can be made at the same temperatures as benzene, it was found necessary to vary the temperature in order to optimize the formation of a desired isomer. This is illustrated in Example 11 with toluene-propylene. Example 11 Cymene (isopropyltoluene), the product of toluene-propylene alkylation, is of commercial interest as a large volume chemical intermediate for cresol manufacture. Of the three isomers, meta cymene has the greatest potential value and ortho cymene the least value. Because of the high potential for immediate commercial application, the reaction parameters of toluene-propylene alkylation with HZSM-12 were studied in depth to optimize meta cymene production. The variable that most affected selectivity to meta cymene was found to be temperature. This is illustrated in the following Table V: TABLE V TOLUENE- PROPYtENE AtKYLATION HZSM-12 CATALYST Isopropyltoluene Isomer Distribution Temp. C Ortho Meta Para 200 18.4% 31.8% 49.8% 230 6.9% 60.3% 32.8% 260 5.3% 63.7% 31.0% WHSV - 5.7 Toluene/0.4 C3H6 Pressure - 3548.7 kPa (500 psig) Molar Feed Ratio - 6.25/1 Toluene/C3H6 Increasing the temperature above 2600C did not give a higher meta cymene content. Propylene conversion at 230-2400C averaged 90-95% during a 5 day run. The only indication of a decrease in catalyst activity was a change in isomer distribution versus time on stream. This was denoted by a decrease in the meta isomer and an increase in the para and ortho isomers. Examples 12-15 Alkylation of ethylbenzene with methanol, propylene, butenes and isobutylene, respectively, in the present of ZSM-12 catalyst, is summarized in Table VI. TABLE VI ETHYLBENZENE ALKYLATION OVER HZSM-12 EXAMPLE ALKYLATING TEMP C PRESSURE WHSV ETHYLBENZENE/ALKYLA- % CONVERSION PRODUCTS -% AGENT TING AGENT MOLE/RATIO AGENT SELECTIVITY 12 METHANOL 200 ATMOSPHERIC 6 3.5/1 55 BENZENE-12% TOLUENE- 4% ETHYL TOLUENE-64% (47% ORTHO 34% METHA 19% PARA C9+ - 20% 13 PROPYLENE 200 ATMOSPHERIC 11 7/1 > 95 ISOPROPYL ETHYLBENZENE 90%(41% PARA 59% META ORTHO 14 1-BUTENE or 2-BUTENE 200 2169.76 kPa 6 7/1 > 95 SECONDARY (300 psig) BUTYLETHYL BENZENE-90% (60% PARA, 40% META 15 ISOBUTYLENE 200 2169.76 kPa 6 7/1 > 95 TERTIARY (300 psig) BUTYLETHYL BENZENE-90% (90% PARA, 10% META) Alkylation of ethylbenzene with methanol using HZSM-12 as catalyst was studied to determine if para-ethyltoluene could be selectively produced. As can be seen in Table VI, selectivity for total ethyltoluene was 64%. Of this 64% the isomer ratio was 47% ortho, 34% meta and 19% para. This isomer distribution is similar to that obtained by alkylating toluene with ethylene over HZSM-12. The alkylation of ethylbenzene with propylene was found to proceed smoothly at 2000C and atmospheric pressure. Propylene conversion was > 95% and the selectivity to isopropylethylbenzene was 90%. Operating in the liquid phase, butene conversion was > 95% with 90% selectivity to butylethylbenzene. 1-butene or 2-butene alkylated to produce secondary butylethylbenzene. The isomer ratio was 6090 para and 40% meta at the temperature used for the experiment. No ortho isomer was found. At the same operating conditions; isobutylene alkylated to give identical olefin conversion and selectivity to product as was found. with 1-butene or 2-butene. The isomer ratio of the tertiary butylethylbenzene was 90% pars and 10% meta. This ratio is close to the 92/8 ratio obtained with conventional Freidel-Kraft catalysts, but conversion and selectivity are higher with HZSM-12. Examples 16-19 The alkylation of isopropylbenzene over HZSM-12 is summarized in Table VII. TABLE VII ISOPROPYLBENZENE ALKYLATION OVER HZSM-12 ISOPROPYLBENZENE/ ALKYLATING ALKYLATING AGENT % CONVERSION PRODUCTS¯% AGENT TEMP C PRESSURE WHSV MOLE RATIO ALKYLATING AGENT SELECTIVITY 16 METHANOL 200 C ATMOSPHERIC 11 3.5/1 30 BENZENE-26% TOLUENE-6% DIISOPROPYL BENZENE-41% ISOPROPYL BENZENE-20% C10+ -9% 17 PROPYLENE 200 C ATMOSPHERIC 11 7/1 > 95 DIISOPROPYL BENZENE-95% (60% PARA 40% META) 18 1-BUTENE or 2-BUTENE 200 C 2169.76 kPa 6 7/1 > 95 SECONDARY (300 psig) BUTYL ISO PROPYLBEN ZENE - 95% (75% PARA, 25% META) 19 ISOBUTYLENE 200 C 2169.76 kPa 6 7/1 > 95 TERTIARY (300 psig) BUTYL ISO PROPYLBEN ZENE (95% PARA) Isopropylbenzene could not be selectively alkylated with methanol to form isopropyltoluene. At 2000C disproportionation of the isopropylbenzene was the predominate reaction. The product was 41% diisopropylbenzene, 24% benzene and 20% isopropyltoluene. Part of the benzene was alkylated as shown by the presence of 6% toluene. The meta or para isomers of diisopropylbenzene can be oxidized to the corresponding dihydroperoxides and subsequently rearranged with an acid catalyst to make resorcinol, hydroquinone and acetone. Resorcinol has the potential of becoming a large volume chemical for use in thermosetting plywood laminates if the selling price could be substantially reduced. Because of this the alkylation reaction parameters of isopropylbenzene-propylene were studied to determine if the meta isomer could be selectively produced. At 2000C and atmospheric pressure, the meta/para ratio was 40/60 as shown in Table VII. Increasing the reactor temperature to 2350C reverse this and the meta/para ratio became 61/39. A further increase in the temperature did not improve the meta/para ratio beyond 61/39. The ortho isomer was not found. However, this is a difficult chromatographic analysis and it is possible 2-3% could have gone undetected. Cumene (isopropylbenzene) can be alkylated with butenes at 2000C. The reaction must be carried out in the liquid phase to prevent catalyst deactivation. Conversion of the olefins was > 95% with 95% selectivity. The 1- and 2- butenes alkylated to produce secondary butylcumene and isobutylene gave tertiary butylcumene. Example 20 Experimentally the alkylation of xylene with methanol was limited to the ortho isomer because only two trimethylbenzene isomers should be formed, assuming an absence of isomerization. These are: 1,2,3,- and 1,2;4-trimethylbenzene. Any 1,3,5- isomer would require an isomerization step. Table IX lists reaction parameters and isomer distribution for the experiment. Using a 1/1 molar ratio of o-xylene/methanol the ratio of 1,2,3- to 1,2,4isomer was 1/1. Only 2% of the 1,3,5- isomer was present. With the conditions of this experiment, little isomerization of either the o-xylene or the trimethylbenzenes occurred. Increasing the reactor temperature to 3500C resulted in an almost equilibrium mixture of the alkylation products. TABLE IX ORTHO XYLENE ALKYLATION WITH METHANOL OVER HZSM-12 FEED: 1/1 o-xylene/Methanol Mole Ratio TEMPERATURE: 300 C PRESSURE: Atmospheric WHSV: 10.0 o-xylene - 1.7 Methanol CONVERSION: 18% o-xylene - 60% Methanol WT % SELECTIVITY COMPOUND OF LIQUID PRODUCT ISOMER DISTRIBUTION C9 62.4 1,3,5-TRIMETHYLBENZENE-2.0% 1,2,4-TRIMETHYLBENZENE-49.0% 1,2,3-TRIMETHYLBENZENE-49.0% C10 24.0 1,2,4,5-TETRAMETHYLBENZENE-82.0% 1,2,3,5-TETRAMETHYLBENZENE-16.0% 1,2,3,4-TETRAMETHYLBENZENE-2.0% C10+ 13.6 Examples 21-23 ortho-Xylene was alkylated with C3 and C4 olefins over HZSM-12 at 1900-2000C. The reaction conditions and products are given in Table X. TABLE X ORTHO-XYLENE ALKYLATION OVER H2SM-12 ALKYLATING XALENE/ALKYLATING % CONVERSION PRODUCTS-% EXAMPLE AGENT TEMP. C PRESSURE WHSV AGENT MOLE RATIO ALKYLATING AGENT SELECTIVITY 20 METHANOL 300 ATMOSPHERIC 12 1/1 60 C9 - 62% C10 - 24% C10+ - 14% 21 PROPYLENE 200 ATMOSPHERIC 6 7/1 > 90 1,2-DIMETHYL-4 ISOPROPYLBENZENE 93% 1,2-DIMETHYL-3 ISOPROPYLBENZENE 7% 22 1-BUTENE or 2-BUTENE 200 2169.76 kPa 6 7/1 95 1,2-DIMETHYL-4 (300 paig) sec BUTYLBENZENE 96% 23 ISOBUTYLENE 190 2169.76 kPa 6 7/1 95 1,2-DIMETHYL-4 (300 paig) t BUTYLBENZENE 97% Example 21 The xylenes were reacted with propylene at atmospheric pressure and temperatures varying from 200-2500C. Under these conditions only ortho-xylene gave a significant alkylation product. These results are not consistent with published relative alkylation rates of the xylene isomers and propylene. Operating in the liquid phase with a low WHSV might induce alkylation with all isomers. The two major alkylation products formed from o-xylene and propylene were 1,2-dimethyl-4-isopropyl benzene and 1,2-dimethyl-3-isopropylbenzene. The ratio of these compounds was 93/7. Using a liquid catalyst of BF3-H3P04 it has been reported these compounds were found in a ratio of 96/. During the experiments with o-xylene essentially no isomerization of the xylene was noted. With meta and para xylenes as the temperatures was increased to force alkylation, isomerization occurred and the only alkylation product was that associated with o-xylene. The experimental conditions and product selectivity for xylene-butene alkylation experiments are shown in Table X. With the indicated reaction conditions only ortho-xylene could be appreciably alkylated. Example 22 At 2000C and 2169.76 kPa (300 psig) o-xylene was alkylated with l-butene or 2-butene to make l,2-dimethyl-4-sec- butylbenzene with 96% selectivity. Conversion of the olefin was 95%. Example 23 At 1900C o-xylene was alkylated with isobutylene to give 1,2-dimethyl-4-t-butylbenzene. The selectivity was 97% and conversion of the olefin 95%. The reaction was maintained for 48 hours without a decline in catalyst activity. Examples 24-26 Halogenated aromatics are difficult to alkylate because of the deactivating effect of the halogen upon the aromatic ring. However, using HZSM-12 as catalyst it was possible to non-selectively alkylate chlorobenzene with methanol or ethylene. The results are shown in Table XI. In each instance, the ortho isomer is the major product. TABLE XI CHLOROBENZENE ALKYLATION OVER H2SM-12 CHLOROBENZENE ALKYLATING ALKYLATING AGENT % CONVERSION PRODUCTS-% EXAMPLE AGENT TEMP. C PRESSURE WHSV MOLE/RATIO ALKYLATING AGENT SELECTIVITY 24 METHANOL 275 ATMOSPHERIC 6 7/1 65 CHLOROTOLUENE 70% (20% PARA 20% META 60% ORTHO) 25 ETHYLENE 325 ATMOSPHERIC 6 7/1 50 ETHYLCLORO BENZENE-80% (24% PARA 20% META 56% ORTHO) 26 PROPYLENE 250 2169.76 kPa 6 10.6/1 99 ISOPROPYL (300 psig) CHLOROBENZENE 99% (60% PARA 20% META 20% ORTHO) Example 26 The results shown in Table XII were obtained using propylene as the alkylating agent and operating. in the liquid phase. This reaction was exceptional because 95% of the propylene was converted to isopropylchlorobenzene with a selectivity of 99%. This compares to published data which indicate aluminosilicate or H2S04 catalysts gave approximately 85% conversion of the propylene. In the case of H2S04, the published isomer distribution was 80%-ortho, 20%-para. The meta isomer was not found. With HZSM-12 as catalyst the isomer ratio was 60%-para, 20%-meta, 20%-ortho. TABLE XII EXAMPLE 26 CHLOROBENZENE ALKYLATION WITH PROPYLENE Temperature - 250 C Presure - 1825.02 kPa (250 psig) WHSV chlorobenzene/propylene 8.1/0.25 Chlorobenzene/propylene - Mole/mole 10.6/1 Reactor Effluent Wt.% Selectivity, % Lt. Ends 0.19 1.59% Chlorobenzene 88.05 Ortho chlorocumene 2.14 17.91% Meta chlorocumene 2.39 20.00% Para chlorocumene 7.22 60.42% Other Trace Feed-Wt. %: Chlorobenzene-96.6% Propylene- 3.4% Table XIII summarizes the results of Examples 1 through 26, listing the aromatics versus alkylating agent used. Plus and minus signs are used to qualitatively indicate, in a very general sense, the activity and selectivity obtained. TABLE XIII ALKYLATION WITH HZSM-12 ZEOLITE EXAMPLES AROMATIC OLEFIN C1a C2 C3 C4 C5 1-5 BENZENE + + +++ +++ +++ 6-11 TOLUENE + + +++ +++ 12-15 ETHYLBENZENE - - +++ +++ 16-19 ISOPROPYLBENZENE - - +++ +++ 20-23 o-XYLENE + - +++ +++ 24-26 CHLOROBENZENE + + +++ - a Alcohol only From the foregoing it is apparent that zeolite ZSM-12 has exceptional alkylation activity and selectivity with respect to aromatic molecules, particularly with C3 and higher olefins at temperatures of approximately 2000-2500C. It is shown to be selective for ethylation reactions, but overall conversions are lower than those encountered with ZSM-5 catalyst. Example 27 Benzene was alkylated with propylene in the presence of HZSM-12 catalyst to show the effect of temperature on the reaction. Keeping the benzene/ propylene feed and the pressure substantially constant, the reactor temperature was varied from 100o-3000C and the reaction products analyzed for changes in composition. The parameters and results are given in Table XIV. TABLE XIV ALKYLATION OF BENZENE WITH PROPYLENE TO PRODUCE ISOPROPYLBENZENE EFFECT OF TEMPERATURE Temperature, C 100 125 150 175 200 200 115 150 275 300 WHSV Benzene 15.2 15.2 15.3 15.2 18.8 18.8 18.8 18.8 18.8 18.8 WHSV Propylene 1.2 1.2 1.2 1.2 1.2 2.4 2.4 2.4 2.4 2.4 Mole Ratio: Benzene/Propylene 6.7 6.7 6.7 6.7 6.7 6.7 6.7 6.7 6.7 6.7 % Conversion Benzene 0.9 7.1 12.0 10.4 11.8 11.3 11.3 12.2 12.2 12.1 % Conversion Propylene 14.9 59.0 97.9 98.4 98.1 98.1 99.4 98.1 98.0 97.8 para-diisopropylbenzene - 100 100 100 67.0 72.2 55.4 32.6 31.9 29.8 Selectivity to isopropylbenzene 86.04 92.23 97.06 97.64 96.99 95.74 94.92 93.20 91.46 85.89 m+p diisopropylbenzene - 2.92 2.67 2.06 2.70 3.96 4.54 5.56 4.96 3.75 n-propylbenzene 0 0 0 0 0 0 .17 .89 3.22 9.99 Material Balance 97.5 97.8 98.2 96.5 96.6 100.2 99.6 98.0 98.1 97.9 Note: Pressure in all cases 2169.76 kPa (300 psig). Example 28 As in Example 27, benzene was again alkylated with propylene over ZSM-12 to produce isopropylbenzene, this time maintaining the temperature at 2000C and varying the pressure from 101.33 - 3548.7 kPa (O to 500 psig). The results are shown in Table XV. TABLE XIV ALKYLATION OF BENZENE WITH PROPYLENE TO PRODUCE ISOPROPYLBENZENE EFFECT OF TEMPERATURE Temperature, C 200 200 200 200 200 200 200 200 Pressure, kPa (psig) 101.33 273.7 446.07 618.43 790,8 963,17 790,8 1135,54 (0) (25) (50) (75) (100) (125) (100) (150) WHSV Benzene 31.0 31.0 1.2 31.0 31.0 31.0 30 30 WHSV Propylene 1.8 1.8 1.8 1.8 1.8 1.8 24 24 Mole Ratio: Benzene/Propylene 9.5 9.5 9.5 9.5 9.5 9.5 66 66 % Conversion Benzene 8.4 9.5 9.6 10.3 10.3 10.3 14.0 14.3 % Conversion Propylene 92.6 97.0 97.5 94.8 95.1 94.8 97.9 95.4 para-diisopropylbenzene In total DIPB 67 68 71 77 78 77 66 76 Selectivity to isopropylbenzene 83.8 86.8 88.6 88.5 89.8 90.4 88.5 90.3 Material Balance 101.6 101.4 102.6 100.5 99.7 99.7 99.1 102.4 TABLE XIV ALKYLATION OF BENZENE WITH PROPYLENE TO PRODUCE ISOPROPYLBENZENE EFFECT OF TEMPERATURE Temperature, C 200 200 200 200 200 200 200 200 Pressure, kPa (psig) 1480.28 1825.02 2169.76 2514.49 1480.28 2169.76 2859.23 3548.7 (200) (250) (300) (350) (200) (300) (400) (500) WHSV Benzene 30 30 30 30 15.4 15.4 15.4 15.4 WHSV Propylene 24 24 24 24 1.2 1.2 1.2 1.2 Mole Ratio: : Benzene/Propylene 66 66 66 66 6.8 6.8 6.8 6.8 % Conversion Benzene 14.1 13.7 13.1 14.0 10.8 11.8 9.3 13.3 % Conversion Propylene 96.8 97.1 95.7 46.8 98.3 48.1 87.7 97.9 para-diisopropylbenzene In total DIPB 61 81 86 9 78 67 100 80 Selectivity to Isopropybenzene 94.0 94.8 96.3 96.7 95.7 97.0 97.9 96.4 Material Balance 98.3 99.6 100.0 99.1 97.1 96.6 97.2 99.6 Example 29 Benzene was alkylated with isobutylene in the vapor phase with HZSM-12 catalyst at 1900 and atmospheric pressure. The reaction is summarized in Table XVI. TABLE XVI BENZENE ALKYLATION WITH ISOBUTYLENE-VAPOR PHASE Feed: 10.1/1 Benzene/Isobutylene-mole/mole Temperature: 190 C Pressure: Atmospheric WHSV 11.7 Benzene 0.8 Isobutylene Conversion, Wt.% 3.4% Benzene 39% Isobutylene Component Wt.%In Effluent Light Ends 4.0 Benzene 90.2 C8 0.1 Tertiary butylbenzene 5.1 See butylbenzene 0.5 C10+ 0.1 Example 30 Using the same reactants and catalyst as Example 29, the alkylation was carried out in the liquid phase by increasing the pressure to 2480.02 kPa (345 psig). The results are shown in Table XVII. TABLE XVII BENZENE ALKYLATION WITH ISOBUTYLENE-LIQUID PHASE Feed: 8.6/1 Benzene/Isobutylene-mole Temperature: 185 C Pressure: 2480.02 kPa (345 psig) WHSV: 9.2 Bwnzene 0,8 Isobutylene Conversion, Wt. % 10.9% Benzene 91.0% Isobutylene Component Wt.%In Effluent Light Ends 0.7 Benzene 82.2 C8 0.1 Tertyary butylbenzene 16.7 Sec.butylbenzene 0.3 A comparison of Example 29 (vapor phase) with Example 30 (liquid phase) demonstrates the surprising and substantial increase in conversion and selectivity encountered by operating in the liquid phase at low temperature and in the presence of ZSM-12 catalyst.

Claims: CLAIMS 1. A process for the alkylation of an aromatic hydrocarbon compound comprising contacting such compound with an alkylating agent having from one to five carbon atoms at a temperature between 100 C and 3000C and a pressure between 105 N/m2 and 2 x 107 N/m2 in the presence of a catalyst comprising a zeolite having a silica to alumina ratio of at least 12 and a constraint index from 1 to 12. 2. A process according to claim 1 wherein said compound and alkylating agent are in the liquid phase when contacted. 3. A process according to claim 1 or claim 2 wherein said temperature is between 2000C and 2500C. 4. A process according to any preceding claim wherein the aromatic hydrocarbon bears a non-polar substituent. 5. A process according to any preceding claim wherein the aromatic hydrocarbon bears a polar substituent. 6. A process according to any preceding claim wherein the alkylating agent is an olefin. 7. A process according to claim 6 wherein the olefin has at least three carbon atoms. 8. A process according to any of claims 1 to 5 wherein the alkylating agent is an alcohol. 9. A process according to any preceding claim wherein the zeolite is ZSM-12. 10. A process according to any preceding claim wherein the zeolite is composited with a binder.

Inventors: BURRESS, GEORGE THOMAS
Applicants: MOBIL OIL CORPORATION
Application year: 1979
Main classification: C07C15
IPC codes: C07C1, C07B61, C07C67, C07C2, C07C15, C07C17, B01J29