METHOD OF MAKING A THIN-WALLED HOLLOW OBJECT OF PLASTIC AND ARRANGEMENT THEREFOR

Abstract: A method of fast moulding a shell-shaped object of a curable mixture of monomeres or thermosetting resin com­ ponents in a movable mould. The mixture cures in short time at the mould tempera­ ture. This time is used for distribution of curable material over the mould surfaces. In a modified embodiment the object is reinforced and in another it is made with a different material thickness in different parts.

Description: Method of making a shell-shaped object of plastic and arral ueent therefor The present invention relates to a method of moulding a shell-shaped object of plastic in a mould and to an arrangement for performing the method. It is known before to produce shell-shaped bodies by so-called rotational moulding of vinyle plastisoles which are created by heating in a heated mould, which is then cooled before demoulding. With rotational moulding originally was meant a method for moulding in which the mould was rotated simultaneously around two axes perpendicular to each other. Later, the same process has been used to considerable extent for sintering or melting of fine powders of thermoplastic, which is made in a heated mould which is then cooled before removing the object from the mould. Other methods of rotational moulding are known in which one starts with a liquid phase which forms a rigid body developing reaction heat. In most cases one starts with an increased temperature in the mould in which the chemicals in liquid phase are located during a sufficiently long time before a viscosity increase occurs, whereafter the temperature of the mould is further increased in order to cause a fast curing of the material when the liquid has been spread over the mould surface. Another known method is described in British patent specification No. 1,380,791 according to which chemicals in liquid phase are cured to a rigid body at room temperature, defined as a temperature between 10 and 43 C. This method does require a low energy consumption but it has the severe drawback that each separate moulding takes too long to make the Method suitable in mass production When one starts with chemicals in liquid phase which develop reaction heat as described for rotational moulding, the time required for rotation in order to have the liquid distributed over the mould surface is several minutes and after that further tirne with rotation is required before the curing has advanced so far that the rotation can be allowed to cease. In the said patent specification it is state that rotation during at least 20 - 30 minutes is required for performing the process. The object of the present invention is to remove the said drawback by proposing a method which can be performed by simple means in short time. The method according to the invention is for this purpose characterized by a number of steps stated in the following claim 1. According to the invention a temperature of the mould increased to above ambient is used. Chemicals are selected which cure so fast that the time for curing after coating the mould surfaces with the curable material is short. The time required in which the mould has to be kept moving until the liquid has increased so much in viscosity that it is not essentially redistributed in the mould due to gravity hereby can be reduced to the least possible, i.e. so that movements of the mould after distribution of material can be dispensed with. The equipment for performing the method will be much simpler since according to the invention it is not necessary to use simultaneous rotation of the mould around two axes. When using the invention for small objects a shorter time than 1 minute can be used for the distribution of liquid over the mould surface. For large objects, of course the required time will be longer but it can still be kept shorter than 2 minutes. According to the invention the mould is heated to a temperature between 35 and 75 0C. Such heating can be made with simple means. After moulding the object is removed from the mould without any need for the mould to be cooled except for a possible cooling required to keep the mould temperature within the desired range. The process as mentioned above is very fast and therefore well suited for mass production of certain objects. Beside that it requires only a small quantity of energy. The mixture of chemicals in liquid phase to be used in the mould is preferably kept at room temperature.As material to start with for use of the method a system of chemicals in liquid phase is suitable which cures fast to a rigid body within the said temperatures of the mixture and of the mould. When hosing chemicals it has to be noted that the mixture viscosity limit for practical use whicll gives the desired time for covering of the mould surfaces with the liquid mixture. The object so created must not be deformed permanently by the forces exerted when removing the object from the mould at the prevailing mould temperature. Example 1 - The method according to the invention was tested in experiments with a mould in the geometrical shape of a cube. It had walls of 10 mm thick aluminium sheets with edges of 250 mm length. The mould was coated with a release agent and with a coating laquer layer on the release agent. The mould was heated to 45 Oc. Centrally on one side of the cube there was an opening of 150 by 150 mm. The mould was placed with the cube opening turned upwards. A mixture of components at a temperature of 20 0C as described below was injected through the opening and thereby the opposite inner surface was coated with a liquid mixture. Thereafter the mould was turned through about 90 in a vertical plane, whereafter it was turned somewhat less than 3600 around a horizontal axis at a low speed when a mould side with mixture floating thereon was inclined to the horizontal plane and at a high speed there between. Thereby an even and complete coating of the four side surfaces of the mould was obtained. The mixture of the compo nents and the introduction of these components into the mould took 20 seconds and coating of the inner surfaces of tlle mould took a further 20 seconds. The object could be removed from the mould after 15 minutes. Example 2 - The experiment according to Example 1 was carried out so far that the inner surfaces of the mould were coated with the component mixture. Onto this shell urethane cellular plastic was foamed giving a rigid body with a density of 35 g/l. It was foamed in situ 4 minutes after the introduction of the first mixture in the mould. The object could be removed from the mould already after 10 minutes due to the fact that tlie foam hELd been set. The mixture of components for the shell in L#aiilples 1 and 2 above consisted in: 50 parts of a threefunctional polyol with glycerol as initiator, propoxylated and with 75% primary hydroxyl groups by final etoxylation and with a hydroxyl nulnber of 32 mg KOH/g and having a viscosity of 900 centipoise at 25 C.having The densi ty was 1,011 kg/dm3 50 parts of a threefunctional polyol with triethanol amine as initiator, propoxylated to a hydroxyl number of 525 mg KOH/g and having a viscosity of 400 centipoise at 25 OC and a density of 1,05 kg/dm3 70 parts of crude methylene diphenyl <RTI ID=4.14> diisocyanate with a functionality of 2,7 and isocyanate group contents of 30,7% and a viscosity of 270 centi poise at 25 C30,7% and a density of 1,24. These components will not be fully miscible until about 20 seconds after start of mixing. After setting at a thickness of 2 mm the object of urethane plastic made according to Example 1 was cracked when it was folded double. Beside that it was relatively rigid and impact resistant. In spite of the fact that the isocyanate was not degasified and the polyoles not dewaterized a smooth laquered surface was obtained. The urethane plastic adhered to the laquer layer so effectively that this was attached to the urethane plastic. Gas bubbles formed in the urethane layer during the process tended to concentrate to the surface which did not have contact with the mould, which is supposed to be due to temperature conditions. The experiments related above are to be seen as examples of the process of the invention, which has a general al,plica- tion and extension as described above. The invention can be used for instance with a Illould for refriuerator cabinets. Several other applications are possible. Thus, a layer forming a decorative surface or tlie object can as mentioned be placed on the layer of release agent. When this new layer is free of solvent or/and has bein set (if it is a two-component system) a layer with an average thickness of about 1,5 mm of the component mixture can be applied. The tack free time of the mixture shall be long enough to admit adhesion to a reinforcement layer e.g. glass fibre with 3 mm fiber length that sticks to the surface. Then another layer with an average thickness of about 3 nmi is applied, which wets the glass fibre layer and adheres to the first layer, In this way, a glass fibre reinforced object with a decorated surface can be made. It is also possible according to the invention to insert fittings or other details of metal or some other material in the mould and have them well attached to the formed object during moulding. When operating with a mould the total surface of which is large, it might be advantageous to supply the material mixture to the mould in two batches, whereby the mould is turned between the first batch, which is supplied to one surface part, and the second batch, which is supplied to another, preferably opposite#, surface part. Then the mould is turned over followed by turning according to the above description. When the material is supplied to the mould it is an advantage if the surface part of the mould where the material is supplied is quite coated-with material already by the supply. If the surface part is mainly plane, coating can be achieved by a turning movement, but if the surface part is very curved it is essential that the material is supplied from a mixing machine through a spray head, which from the start distributes the material over the entire surface part. It is normal to make objects with an even material distribution over the surfaces of the shell. However, it is also possible to apply the invention for producing an olJJect with a larger material thickness in certain arts titan in others. In that case a shell-shaped object is Iflafie according to the above description and then the object is left in the mould in order to be used as a mould at a second moulding witlj supply of a suitable quantity of mixture and distribution of this mixture over a desired part of tiie object surface.

Claims: d 1 a i In s 1. Method of moulding a shell-shaped object of plastic in a mould comprising the following steps: a) the mould, possibly coated with a release assent, is heated to a temperature above room temperature b) a mixture of monomeres or thermo-setting resin colsponents curable at this temperature is made in liquid form, preferably with an addition of polyinerizing catalyst and hardener c) the mixture is supplied to the mould d) the mould is given a movement so that the material mixture due to the gravity is caused to float over the mould surface once e) hardening of the material to a rigid body is awaited and thereafter the object is removed from the mould. 2. Method according to Claim 1, c h a r a c t e r i z e d therein that the mould after supply of the material mixture is turned over about 900 in a mainly vertical plane, whereafter it is turned around a preferably horizontal axis so that its surfaces will be coated with liquid material before the material mixture has gelled. 3. Method according to Claim 1, c h a r a c t e r i z e d therein that the mould is turned over first through 180 in one plane and thereafter back 900. 4. Method according to Claim 1, c h a r a c t e r i z e d therein that the mould is turned over through 2700 in a plane. 5. Method according to Claim 2, c h a r a c t e r i z e d therein that the mixture is supplied to the mould in two batches, and that the mould is turned between the first batch, which is supplied to a surface part, and the second batch, which is supplied to another preferably opposite surface part of the mould. 6. Method according to Claim 1, c h a r a c t e r i z e d therein that the mould is turned during at the most 2 minutes. 7. Method according to Claim 1, char act e r i z e d therein that the mould is turned through less than 3600. 8. Method according to Claim 1, c h a r a c t e 2 i z e d therein that the mould is turned fast when tlle mixture is flowing on mould surfaces forming an angle to eacll other and slowly or with an interruption when the mixture is flowing over an even surface. 9. Method according to Claim 1, c h a r a c t e r i z & e d therein that an isocyanate-based liquid col-lwosition is used as curable mixture. 10. Method according to any of Claims 1 - 9, c h a r a c t e r i z e d therein that first a layer of mixture coating the surfaces of the mould is applied and then a foaiiiable and curable material supplied to the mould. 11. Method according to Claim 10, c h a r a c t e r i z e d therein that the mould is provided with a male mould before foaming so that the foamed body created in the mould has a certain shape on the surfaces. 12. Method according to Claim 1, c h a r a c t e r i z c d therein that a curable mixture with foaming property is used. 13. Method according to any of the preceding Claims, c h a r a c t e r i z e d therein that first a layer of mixture coating the mould surfaces is applied to the mould and that without delay glass fibre flock or other fibre flock is supplied, that the mould movement is repeated so that the fibres are distributed over the liquid surface while the mixture is still tacky and that thereafter a further layer with a mixture, which at least in part wets the fibres and coats the surfaces, is applied. 14. Method according to any of Claims 1 - 13, c h a r a c t e r i z e d therein that the mould surface before supply of the curable mixture is coated with a colour layer, for instance a fast drying lacquer. 15. Method according to any of Claims 1 - 14, c h a r a c t e r i z e d therein that fittings or other details of metal or other material are applied to the mould and moulded'into the object. 16. Method according to any preceding claim, c 11 a A a c t e r i z e d therein that the mould witn all object is ust:'d as a mould in a second moulding with supply of mixture and distribution thereof over part of the object surface in oiler to obtain parts having a larger material thickness titan others. 17. Arrangement for moulding of an object of plastic in a mould in the way proposed in any of Clans 1 - 16, c h a r a c t e r i z e d by a mould with means for turning it over through about 90 in about a vertical plane and other means for turning it around a preferably horizontal axis. 18. Arrangement according to Claim 17, c h a r a c t e r i z e d therein that the means for turning of the mould have control means with which the turning speed during a process can be varied after a programme adjusted in advance.

Inventors: MARD, ROLAND INGVAR EMANUEL
Applicants: AKTIEBOLAGET ELECTROLUX
Application year: 1979
Main classification: B29C5
IPC codes: B29C39, B29C41, B29C31, B29C44