POLYMERISABLE COMPOSITIONS, DERIVED COATINGS AND OTHER POLYMERISED PRODUCTS

Abstract: Photopolymerisable compositions capable of polymer­ isation by an acid-catalysed mechanism under the influence of ultraviolet and/or visible light comprise (a) at least one material capable of polymerisation by an acid-catalysed mechanism to a polymeric material of higher molecular weight state, (b) a photosensitive aromatic sulphonium salt and (c) a material which under the conditions of photo­ polymerisation will yield a significant proportion of free radi­ cals. These compositions yield useful coating films and other products on irradiation.

Description: PNOTOPOLYN#R1S ABLE COMPOSITIONS, DERIVED COATINGS AND OTHER POLYMERISED PRODUCTS. This invention relates to photopolymerisable compositions, to coatings and to other products obtained by polymerisation of the photopolymerisable compositions. In our British Patent 1,526,923 we have described and claimed inter alia a photopolymerisable composition comprising at least one acid-polymerisable or acid-curable material and as photosensitiser at least one salt of formula EMI1.1 wherein A is sulphur, selenium or tellurium, n is 1 or 2, R11 R2 and R3, which may be the same or different, each is a hydrocarbon or substituted hydrocarbon group or heterocyclic group or two of the groups R1, R2 and R3 together with the element A are a heterocyclic structure the other group R being a hydrocarbon or a substituted hydrocarbon group, and X is an anion derived from an acid which is capable of polymerising or curing the acid-polymerisable or acid-curable material. We have also described the preparation of a polymeric material by exposing the composition to radiation of a suitable wavelength. British Patent 1,516,511 (General Electric Company) describes and claims inter alia a curable composition comprising (A) a monoepoxide, an epoxy resin or a mixture thereof polymerisable to a higher molecular weight state, and (B) a radiation sensitive aromatic onium salt of O, S, Se, or Te in an amount capable of effecting the cure of (A) by release of a Lewis catalyst when exposed to radiant energy; and British Patent 1,518,141 (General Electric Company) describes and claims inter alia a polymerisable composition comprising (A) a monomeric or prepolymeric cationically polymerisable organic material free of oxirane oxygen selected from vinyl monomers, vinyl prepolymers, cyclic ethers, cyclic esters, cyclic sulfides, cyclic amines and organosilicon cyclics, and (B) an effective amount of a radiation sensitive aromatic onium salt of sulphur, selenium or tellurium capable of effecting the polymerisation of (A) by release of a Lewis Acid catalyst when exposed to radiant energy. U.S. Patent 4,069,054 (Minnesota Mining and Manufacturing Company) describes and claims inter alia a photopolymerisable composition comprising: (a) a cationically polymerisable monomer (b) an aromatic sulphonium compound of EMI2.1 wherein Rl, R2 and R3 are selected from the group consisting of aryl groups having 4 to 20 carbon atoms and alkyl radicals having 1 to 20 carbon atoms; wherein at least one of Rl, R2 and R3 is aryl; wherein Z is selected from the group consisting of oxygen; sulphur; EMI3.1 where R is aryl or acyl; a carbon-carbon bond; or EMI3.2 where R4 and R5 are selected from the group consisting of hydrogen, an alkyl radical having 1-4 carbon atoms, and an alkenyl radical having 2-4 carbon atoms; and n is zero or 1; and X- is a halogen-containing complex anion selected from tetrafluoroborate, hexafluorophosphate, hexafluoroarsenate, and hexafluoroantimonate; and (c) a sensitising compound selected from the group consisting of (i) aromatic tertiary amines having the formula EMI3.3 where Arll Ar2 and Ar3 are groups having 6-20 carbon atoms; Z is selected from oxygen, sulfur; EMI3.4 a carbon-carbon bond; or EMI3.5 where R4 and R5 are selected from hydrogen, alkyl radicals of 1-4 carbon atoms, and alkenyl radicals of 2-4 carbon atoms, and wherein n is zero or 1; (ii) aromatic tertiary diamines having the formula EMI4.1 where Y is a divalent radical selected from arylene and Ar8-Z-Ar9, where Z is as described above, Ar Ar5, Ar6, Ar7, Ar8 and Ar9 are aryl groups having 6-20 carbon atoms; and wherein n and m are zero or 1; and (iii) aryl polycyclic compounds having at least three fused benzene rings and further having an ionisation energy less than about 7.5 ev. U.S Patent 4,069,054 refers to the abovementioned materials as only select materials which are useful in sensitising aromatic sulphonium salts. In a review article by J.V. Crivello entitled Photo initiated Cationic Polymerisation" (see page 63 of "W Curing : Science & Technology", 1978, published by Technology Marketing Corporation and edited by P.Pappas.) it is stated that diaryliodonium and triarylsulphonium salts show certain parallel behaviour with respect to their photochemical properties. In particular it is stated that their photolysis is not accelerated by radical initiators. Therefore it is surprising that we have now found that the rate of polymerisation of materials polymerisable by an acid catalysed mechanism in the presence of aromatic sulphonium salts may be increased and in many cases the wavelength spectrum of sensitivity of the salts may be extended towards the visible region when there is present in a photopolymerisable composition of general type described in British Patent Specifications 1,526,923; 1,516,511; and 1,518,141, a photosensitive aromatic sulphonium salt and a material which under the conditions of photopolymerisation, by itself or by hydrogen abstraction with a component of the composition other than the sulphonium salt, will yield free radicals. This finding is of particular importance with regard to the formulation of photopolymerisable compositions in which there is present a component which plays no part in the photopolymerisation process but which absorbs radiation in that same region of the wavelength spectrum which is required for activation of the sulphonium salt. Such components include for example pigments particularly titanium dioxide which absorbs radiation substantially in the ultraviolet region. According to this invention we provide a photopolymerisable composition capable of polymerisation by an acid-catalysed mechanism under the influence of ultraviolet and/or visible light which comprises the components: (a) at least one material capable of polymerisation by an acid catalysed mechanism to a polymeric material of higher molecular weight state; (b) a photosensitive aromatic sulphonium salt as herein defined, and (c) a material which under the conditions of photo polymerisation will yield a significant proportion of free radicals as herein defined either (i) by intramolecular cleavage, or (ii) by intermolec ular abstraction in conjunction with a component of the composition other than the photosensitive aromatic sulphonium salt. Within the term "polymerisation by an acidcatalysed mechanism" we include polymerisation by an addition acid-catalysed cationic/mechanism and polymerisation by an acid-catalysed condensation mechanism. Preferably the photopolymerisable composition contains a further component (d) which plays no direct part in the photopolymerisation process but which, when the composition is irradiated to cause polymerisation absorbs at least some of that irradiation to which in the absence of said component (d) the sulphonium salt would be sensitive. Suitable such materials include, for example, pigments and other additives which may be used for example in the formulation of paints, other surface coatings and other polymerised products. A particularly appropriate pigment is titanium dioxide. The definition of component (c) does not embrace the sensitising compounds mentioned in U.S. Patent No. 4,069,054. It is believed that these compounds behave in a manner significantly different from the behaviour of the materials (c) which yield free radicals. For the formulation of a fully effective photopolymerisable composition, component (c) is preferably of good solubility in the material (a) to be polymerised. We have found that the solubility of (c) in acetone is a useful general guide to the solubility of (c) in (a) and that preferred components (c) can be usefully selected on this basis. Thus it is preferred that component (c) has a solubility in acetone which is greater than 2% by weight of (c) based on the volume of acetone. It is also preferred that the component (c) of the photopolymerisable composition is one which does not yield a coloured product when irradiated in the presence of the sulphonium salt. Since the present compositions find important application as coatings in which colour or lack of colour must be closely controlled it is clearly important that the light induced products of interaction between the polymerisable material, the sulphonium salt and component (c) are not intensely coloured and preferably they are substantially free from colour. Thus unsuitable materials as component (c) include certain amines and sulphur compounds. Suitable materials as component (c) which yield a significant proportion of free radicals useful in the present invention under the conditions of polymerisation to be employed can be determined by reference to the following papers : A. Ledwith, Pure and Applied Chem., 49-431-441 (1977); Hutchinson & Ledwith, Adv. Polymer Science, 14, 49 (1974); and to "Free Radicals", Volumes I and II, by J.K.Kochi (Wiley 1973). Thus it is preferred to employ as component (c) conventional free radical generators which generate a significant proportion of free radicals and such as are disclosed in these references. Different materials (c) will in many cases yield free radicals under different conditions of irradiation and clearly in practising this invention one will normally choose that material which provides free radicals to the optimum extent under any chosen irradiation conditions. The irradiation may be desired in the ultraviolet and/or in the visible part of the spectrum for example at a wavelength in the range about 200-380 nm for ultraviolet and in the range 380-700 nm for the visible. It is a particular advantage of this invention that in many cases photopolymerisable compositions may be polymerised when irradiated with visible light, i.e. in the range 380-700 nm. Particularly suitable materials as component (c) are those which on irradiation yield free radicals which are readily converted to the corresponding carbocations by the sulphonium salt. The free radical to be oxidised may be that resulting from cleavage, hydrogen abstraction, or by any other suitable radicalforming mechanism. Particularly suitable types of material which may be used as component (c) (i) of the photopolymerisable compositions include benzoin; the benzoin alkyl ethers, for example benzoin methyl ether and benzoin ethyl ether; derivatives of acetophenone, for example alkoxy aryl acetophenones such as 2,2-dimethoxy-2-phenyl-acetophenone and 2,2-diethoxyacetophenone, and l-phenyl-l, 2-propanedione-2-0-benzoyl oxime; and halogenated acetophenones such as 2,2-dichloroacetophenone. Particularly suitable types of material which may be used as component (c) (ii) include aromatic diketones, for example 9,10-phenanthrene quinine; 9-lO-anthraquinone and benzil, and derivatives of these ketones; benzophenone and its derivatives; compounds capable of diradical formation such as O-methyl acetophenone materials of structure EMI9.1 wherein X=O, S, CH2 or a direct carbon-carbon bond, i.e. xanthone, thioxanthone, anthrone and fluorenone respectively (when R = H) and derivatives of such materials for example where R = halogen, alkyl or substituted alkyl, i.e. derivatives such as 2-isopropylthioxanthone and 2-methylthioxanthone; and certain aromatic aldehydes such as piperonal of structure EMI9.2 and derivatives thereof; and many halogenated materials such as the arylchloromethyl and arylchlorosulphonyl derivatives which are referred to in Table II at page 19 of the book mentioned above edited by P.Pappas. In the case of components (c) (ii) they will normally abstract hydrogen from a hydrogen-donor which is present in the photopolymerisable composition and this will commonly be the material which is to be polymerised. However other suitable components of a photopolymerisable composition which may act as a hydrogendonor include tetrahydrofuran, hydrocarbons and ethers or even the component (c) (ii) itself. Unsuitable materials as component (c) (ii) include those which contain groups reactive with organic carbocations e.g. certain amines and sulphur compounds. Examples of such unsuitable types are 4,4 -dimethylaminobenzophenone (Michlers Ketone) and 4,4 -diethylaminobenzophenone. The amount of material (c) is not usually critical but will usually be from 0.01% to 10% and preferably from 0.05% to 5% by weight based on the weight of polymerisable material in the composition. The optimum amount will usually be about 0.5 - 3% by weight. The aromatic sulphonium salts (b) to be used in the photopolymerisable compositions of this invention are preferably defined by the formula: EMI10.1 wherein n is 1 or 2; Rl, R2 and R3, which may be the same or different, each is a hydrocarbon or substituted hydrocarbon group or heterocyclic group or two of the groups Rl, R2 and R3 together with the S atom are a heterocyclic structure, the other group R being a hydrocarbon group or substituted hydrocarbon group, at least one group R attached to the S atom being an aromatic group. Xn- is an anion derived from an acid which is capable of polymerising (or curing) the material (a) which is polymerisable (or curable) to a higher molecular weight state. The groups R may be, for example, alkyl, cycloalkyl, aryl, alkaryl, or aralkyl groups or sub stituted derivatives thereof, and substituted or un substituted heterocyclic groups such as pyridyl or furfuryl. Preferably each of the groups R is an aryl or substituted #aryl group or one of such groups may be an alkyl or substituted alkyl group. Examples of substitutes which may be present in the groups R are halogen, alkoxy, -COOR, -COR, -N02, -NO or -OH. Particularly suitable substituents are those which extend the absorption of the sulphonium compound towards the visible region e.g. nitro groups. The anion X(n-) may be for example a halogencontaining complex ion. The complex ion may be a halogenide of a metal or a metalloid element, for example a polyhalide of boron, antimony, phosphorous, tin, bismuth, arsenic or iron. Examples of suitable anions are 3F4 , SbCl6#, SbF6 , SnCl6 , PF6 , AsF6 FeCl4 , BiCl5 , or R5S03, where R5 is an aromatic hydrocarbon radical having 6-13 carbon atoms, an alkyl radical having 1-8 carbon atoms, halogenated derivatives thereof or R5 is fluorine; or ClO4#, or CF3 COO or ArS03 , or HIS04, or N03 or the picrate ion. Particularly suitable sulphonium salts include those which are disclosed in our British Patent 1,526,925. The ability of a particular sulphonium salt to yield fragments capable of polymerising a particular material (a) reflects the ability of the corresponding proton acid, i.e. the proton acid containing the same anion as the salt, to polymerise that material. If the proton acid polymerises the material, then the sulphonium salt containing the same anion also will be capable of providing fragments which will polymerise the material. Thus the suitability of a particular salt for use with a particular polymerisable material is readily determined simply by mixing the corresponding proton acid with the material. The sulphonium salts used in this invention are normally solids at ordinary temperatures and they are usually incorporated in the polymerisable material (a) in the form of a solution in some suitable liquid. Any inert liquid diluent in which the salt is sufficiently soluble may be used, and example of suitable diluents are halogenated hydrocarbons, e.g. methylene chloride, ketones, e.g. acetone. We prefer to employ 0 a liquid diluent of low boiling point, e.g. below 150 C in order to facilitate removal of the diluent from the composition. The amount of the diluent used is not critical but preferably is just sufficient to dissolve the appropriate amount of the sulphonium salt. After incorporation of the salt in the composition, the diluent may be removed, if desired, before the composition is irradiated. Removal of the diluent prior to irradiating the composition, may be desirable in cases where the diluent is a solvent for the polymerisable material. In the case where the material is, or contains, a monomer, the salt may be soluble in the material and a diluent may not be required. The amount of the sulphonium salt is not critical but will usually be from 0.01% to 10.0%, and preferably from 0.5% to 5.0% by weight based on the weight of polymerisable material in the composition. In general increasing the amount of the sulphonium salt results in an increase in the rate of polymerisation or curing achieved although in practice there is little point in using an amount of greater than 10% by weight. The sulphonium salt preferably should be soluble in the polymerisable material (a) into which it is incorporated and the solubility of a particular salt in the material may limit the amount of that salt which can be incorporated. The polymerisation reaction initiated by irradiating the composition is exothermic and use of too large an amount of the sulphonium salt may result in a very rapid rise in temperature and loss of control over the reaction conditions. The optimum amount of the sulphonium salt will usually be about 3% to 570 by weight but will depend upon the particular salt and polymerisable material employed and the radiation source, and can be determined by simple experiment. In general, polymerisation or curing of the composition proceeds readily when the composition is irradiated at ambient temperature although the reaction is exothermic and may be accompanied by a rise in temperature of the composition. The rate of polymerisation or curing in general may be increased by irradiating the composition at an elevated temperature. The present invention thus provides a method of producing a polymeric composition which consists in irradiating with ultraviolet and/or visible light a photopolymerisable composition as described above. The invention also provides a polymeric composition when produced by this method. Particularly useful photopolymerisable comp- ositions according to the invention are those which are to be applied as coatings to surfaces and which are preferably pigmented. Compositions comprising combinations of components (b) and (c), which together effect polymerisation on irradiation by near ultraviolet and/ or visible light, is less affected by the absorption of ultraviolet light by certain pigments, (notably titanium dioxide) which may be contained in the composition, compared with compositions free from (c). The photopolymerisable material (a) capable of polymerisation by an acid-catalysed mechanism to a polymeric material of a higher molecular weight state is of very wide scope. Clearly the choice of such material will be limited to an extent which depends upon the nature of the aromatic sulphonium salt (b) and on the nature of the material (c) and also upon the nature of the ultraviolet and/or visible light with which the photopolymerisable material is irradiated. As already stated it is one advantage of the compositions of the present invention that they may be sensitive to, and hence can be polymerised on irradiation with, visible light. The term "polymerisable material" also includes curable materials, for example materials which are already of high molecular weight and which are cross-linked by the process of the present invention. Mixtures of polymerisable or curable materials (a) may be employed, as also may mixtures of one or more polymerisable or curable materials (a) with resins which are not polymerisable by an acid-catalysed mechanism for example alkyd resins. Materials containing polymerisable cyclic groups may be employed, notably cyclic ethers for example lactones and acrolein tetramer and especially epoxides and episulphides, and polymers thereof containing polymerisable cyclic groups. Epoxides and episulphides containing from 2 to 20 carbon atoms are suitable, for example the cycloaliphatic epoxides, ethylene oxide, ethylene sulphide, propylene oxide and propylene sulphide, as also are compounds containing two or more epoxide or episulphide groups. Epoxy and episulphide resins may be used, for example the epoxy resins commonly known as Araldite epoxy resins. Other resins curable by an acid-catalysed mechanism which may be used include phenolic resins, for example phenol/formaldehyde resins, aminoplastics, for example urea/formaldehyde and melamine/formaldehyde resins, methylol compounds, methylol ethers of polycarboxylic acid amides, for example derivatives of polyacrylic and polymethacrylic acid amides, alkyd resins containing urethane groups and resins containing carbonic acid esters of N-methylolamides. Acid-polymerisable or acid-curable ethylenically unsaturated materials may also be used, for example vinyl carbazole, vinyl ethers and diketene (which is both ethylenically unsaturated and a lactone). Resinous materials containing cross-linking agents which can be cured by acids are included. Preferably the polymerisable compositions of this invention do not contain any significant proportion of material which is polymerisable by free radicals, for example radical-polymerisable ethylenically unsaturated materials, since it is our intention that the significant proportion of free radicals which is generated by material (c) on radiation, although capable of polymerising such materials is utilised to the fullest extent in promoting the acid-catalysed polymerisation. The compositions of the invention may be used in any of the applications for which materials polymerisable by a cationic mechanism are normally employed, provided that, if the composition is to be polymerised or cured in situ, irradiation of the composition is possible. Thus the compositions may be used, for example, for forming surface coatings on a variety of substrates, e.g. wood, paper, metals and textiles, and in printing inks. The may be used as adhesives in applications where they can be subjected in situ to radiation, for example in the formation of laminates wherein one or both of the lamina is permeable to radiation, e.g. glass lamina and some plastic lamina. The compositions have the property that only those regions contacted by radiation are polymerised or cured so that they may be used for example in the production of decorative articles having a contoured surface by exposing parts of the surface to radiation to cure those parts and subsequently removing uncured material from the surface. Thus they may be used, for example in the production of printing plates and printed circuits. The invention is illustrated by the following Examples in which parts and percentages are by weight unless otherwise stated: EXAMPLE 1 A mixture containing 3 parts of triphenyl sulphonium hexafluorophosphate and 1 part of isopropylthioxanthone in 100 parts of 3,4 -epoxy-cyclohexylmethyl- 3,4 -epoxy-cyclohexyl carboxylate (commercially available as ERL 4221 from Union Carbide) was coated onto a glass plate to form a film of 25 > thickness. When this film was irradiated at a distance of 4 inches using a Thorn Graph-X 400w lamp (which emitted radiation in the wavelength range 330-500 nm but predominantly in the visible region) a clear, hard, teckfree coating was produced after 30 seconds. A similar mixture which did not contain isopropylthioxanthone was still tacky after 700 seconds irradiation. When the isopropylthioxanthone was replaced by an equal weight of first benzil and then by tetracetyl robiflavin, the film was tack-free after 60 seconds in each case. EXAMPLE 2 A mixture containing 3 parts of triphenyl sulphonium hexafluorophosphate and 100 parts of the diglycidyl ether of bisphenolA (commercially available as DER 331" from Dow Chemical) was pigmented with rutile titanium dioxide to a PVC of 10.8% and was coated onto a glass plate to form a film of 25p thickness. When the film was irradiated at 20 feet/ minute beneath a 200w/linear inch medium pressure mercury vapour lamp (providing predominantly ultraviolet radiation but also a proportion of visible radiation) 6 passes were needed to achieve a hard, tack-free coating. When there was also present 1% of isopropylthioxanthone only 4 passes were required. EXAMPLE 3 Each of a series of compositions containing 3 parts of triphenyl sulphonium fluoroborate in 100 parts of the commercially available aliphatic epoxide "ERL 4221", used in Example 1, was mixed with 1 part of one of the additives listed below and these compositions were coated onto glass as films of 12 > thickness. The films were irradiated using a Thorn Graph-X 400w lamp emitting radiation in the wavelength range 330 500 nm but predominantly in the visible region at a distance of 4 inches from the lamp, and the time taken for curing to a hard, tack-free coating was determined Additive Cure Time (minutes) None uncured after 15 Benzil 13 2,2-dimethoxy, 2-phenyl acetophenone 13.5 2-isopropylthioxanthone 9.5 Benzoin isopropylether 8 2-tertbutyl anthraquinone 10.5 (2-isopropylthioxanthone has a solubility in acetone of 30% w/v whereas 2-chlorothioxanthone and 2-tertbutyl anthraquinone have a solubility of less than 2% w/v.) When only 1 part of the sulphonium salt was employed in 100 parts of the epoxide together with 1 part of 2lisopropylthioxanthone, a coating applied to glass was only partially cured after 15 minutes. EXAMPLE 4 I II A mixture containing 3 parts of 4,4 ,4 -trimethylphenyl sulphonium hexafluorophosphate, 100 parts of "DER 331" as used in Example 2 (and which is less readily polymerised than the aliphatic epoxide ERL4221), and l part of 2-isopropylthioxanthone was coated onto glass as a film (a) of thickness 12 > . Another mixture without the 2-isopropylthioxanthone was similarly coated as a film (b) on glass. After irradiation as described in Example 3 for 13 minutes film (a) had cured whereas film (b) remained uncured after 15 minutes. When only 0.5 parts of the 2-isopropylthioxanthone were employed, the film was not fully cured after 15 minutes of irradiation. EXAMPLE 5 Two compositions (a) and (b) each containing ll 3 parts of 4,4 , 4 - trimethylphenyl sulphonium hexafluoroarsenate and 100 parts of the aliphatic epoxide "ERL 4221" as used in Example 1, were mixed respectively with 1 part of 2-isopropylthioxanthone and 1 part of 2,2-dimethoxy 2-phenylacetophenone. The compositions were applied to glass and irradiated as described in Example 3. Composition (a) cured in lo seconds and composition (b) cured in 80 seconds. In the absence of either additive the composition was uncured after 80 seconds. When the amount of sulphonium salt was reduced to 1 part and the amount of additive was reduced to 0.5 part the times of curing were increased to 20 and 170 seconds respectively. In the absence of either additive the composition was uncured after 180 seconds. EXAMPLE 6 A mixture containing 0.5 part of triphenylsulphonium hexafluoroantimonate, 100 parts of the aliphatic epoxide "ERL 4221" used in Example 1, and 2 parts of benzoin isopropyl ether was coated onto glass and irradiated as described in Example 2. The coating was cured after 4 passes whereas in the absence of the benzoin isopropyl ether a coating remained wet and uncured after 8 passes.

Claims: WE CLAIM 1. A photopolymerisable composition capable of polymer isation by an acid-catalysed mechanism under the influence of ultraviolet and/or visible light which comprises the components: (a) at least one material capable of polymerisation by an acid catalysed mechanism to a polymeric material of higher molecular weight state; (b) a photosensitive aromatic sulphonium salt and (c) a material which under the conditions of photo polymerisation will yield a significant propor tion of free radicals either (i) by intramole cular cleavage, or (ii) by intermolecular abstraction in conjunction with a component of the composition other than the photosensitive aromatic sulphonium salt. 2. A photopolymerisable composition according to claim 1 wherein the photosensitive sulphonium salt is represented by the formula : EMI20.1 wherein n is 1 or 2; R1, R2 and R3, which may be the same or different, each is a hydrocarbon or substitu ed hydrocarbon group or heterocyclic group or two of the groups R11 R2 and R3 together with the S atom are a heterocyclic structure, the other group R being a hydrocarbon group or substituted hydrocarbon group, at least one group R attached to the S atom being an aromatic group; Xn- is an anion derived from an acid which is capable of polymerising the material (a) of the composition by an acid-catalysed mechanism to a higher molecular weight state. 3. A photopolymerisable composition according to claim 2 wherein Xn is selected from BF4#, SbC16 , SbF6 , 6 6 t Pug , AsF6 , FeCl4#, BiC15 , or R5S03 where R5 is an aromatic hydrocarbon radical having 6-13 carbon atoms, an alkyl radical having 1-8 carbon atoms, and halogenated derivatives thereof, or R5 is fluorine. 4. A photopolymerisable composition according to any one of claims 1 to 3 wherein a component (c) (i) is selected from benzoin and benzoin alkyl ethers; alkoxy aryl acetophenones; and halogenated aceto phenones, or a component (c) (ii) is selected from aromatic diketones and derivatives thereof; benzo phenone and derivatives thereof; materials of EMI21.1 where X=O, S, CH2 or a direct carbon-to-carbon bond and derivatives thereof where R = halogen, alkyl or substituted alkyl. 5. A photopolymerisable composition according to any one of claims 1 to 4 wherein there is present 0.01 to 10% by weight based on the composition of the component (c). 6. A photopolymerisable composition according to any one of claims 1 to 5 wherein the material capable of polymerisation to a higher molecular weight state is selected from epoxides, episulphides, and other cyclic ethers and thioethers; epoxy resins; episulphide resins; vinyl ethers; phenolic resins; and aminoplasts. A photopolymerisable composition according to any one of claims 1 to 6 which is substantially free of material polymerisable by free radicals. A A photopolymerisable composition according to any one of claims 1 to 7 comprising a further component (d) which plays no part in the polymerisation process but which, when the composition is irrad iated with ultraviolet and/or visible light, absorbs at least some of that radiation to which, in the absence of said component (d), the sulphon ium salt would be sensitive. A A coating composition which comprises a photopoly merisable composition according to claim 8 and in which the component (d) is a pigment, it. Apolymerised composition obtained by irradiating with ultraviolet and/or visible light a composition according to any one of claims 1 to 9.

Inventors: LEDWITH, ANTHONY, MCGUINESS, ROBERT CLAYTON
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1979
Main classification: G03C1
IPC codes: C08L61, C08F2, C08G75, C08G65, C08G85, C08G59, G03F7