METHOD OF TREATING MICA

Abstract: Mica, for use as a filler, is coated with a chlorinated hy­ drocarbon by enveloping mica flakes in a fluid medium com­ prising the chlorinated hydrocarbon and a liquid dispersant therefor, and then drying the flakes at load temperatures. The chlorinated hydrocarbon is distributed macroscopically uni­ formly throughout the mica, as a coating, but provides a mic­ roscopically higher level of chlorine at the edges of the mica flakes, assisting in binding the flakes to plastics materials such as polypropylene.

Description: DESCRIPTION This invention relates to a method of treating mica. It is known that certain chlorinated hydrocarbons can act as coupling agents for mica on melt forming resins. One prior art method that is especially suitable method of treating mica with chlorinated hydrocarbons that act as a coupling agent therefor involves mixing mica particles with chlorinated paraffins in powder form at elevated temperature to yield a coating on the mica. Although this method serves to provide coated mica particles which are useful as reinforcing materials for melt forming resins, it has the disadvantage that relatively high temperatures must be used. According to the present invention, there is provided a method of treating mica which comprises enveloping mica flakes with a solid chlorinated hydrtcsvbon in the presence of a liquid dispersant, and drying the mica flakes. 3y exposing mica particles to a fluid medium that comprises chlorinated hydrocarbon, active sites at the edges of the mica flakes rapidly and preferentially take on a coating that beneficially aids reinforcement by the coated mica in melt forming resins such as polypropylene. When sufficient fluid is employed to surround each of the flakes, a macroscopically uniform distribution of chlorinated hydrocarbon in the mica filler is achieved. Although the mica filler coated as above can be made macroscopically uniform with respect to the chlorinated hydrocarbon, microscopic examination of dried flakes using X-ray techniques shows that chlorine concentration is highest at the edges of the flakes under conditions of this invention. Apparently, the edges of the flakes, due to many platelike layers provide more surface area for infiltration by the fluid containing the chlorinated hydrocarbon. Advantageously, treating mica filler in accordance with this invention to achieve macroscopic uniformity of coating thereon is rapid and does not require highly elevated temperatures. This quick, low temperature manner of coating therefore is not likely to permit excessive evolution of hydrochloric acid from highly chlorinated hydrocarbons thereby reducing risk of excessive wear t6 coating apparatus. Moreover, the fluid medium used in the coating operation may be reclaimed and reused in subsequent coating operations. Still further, this coating method is compatible with further coating techniques as by tumbling at elevated temperature the peripherially coated flakes of this invention and with additional chlorinated hydrocarbon, if desired. The mica that may be desirably employed in this invention includes commercially available mica filler materials comprising, for example, muscovite, biotite and phlogophite mica mineral. Mica that comprises princiapply by weight phlogopite is preferred, e.g. Marietta International Suzorite Mica. The mica filler is available in a variety of particle sizes and such size is not an important criteria for this invention although mica that passes through a 20 mesh screen and is retained on a 325 mesh screen shows particular advantage with respect to compounding with melt forming resins and chlorinated hydrocarbon of this invention. The shape of mica filler particles is platelike or flake form as is well known. One characterization of mica that is sometimes used is flake aspect ratio or average diameter of flake over thickness. The aspect ratio of mica normally suitable herein can be termed unclassified in the sense that a distribution of flakes with varying aspect ratios are within the filler. Mica that has narrow aspect ratios, however, will also be suitable for use in this invention. A preferred class of chlorinated hydrocarbons for use in this invention is chlorinated aliphatic hydrocarbons having in excess of about 50% by weight chlorine, e.g. chlorinated paraffin waxes. Especially preferred are chlorinated paraffin having between about 60-75% by weight chlorine that are commercially available,e.g0under the trade names iLorez 700,760 and ChIorowax 70 and the like, these chlorinated waxes are normally available in powder form and have molecular weights (number average) in a range between about 400-3000, desirably between 800-1500 for this invention In one embodiment of this invention, mica filler and powdered chlorinated hydrocarbon are gently tumbled together to yield a powdery blend whereupon liquid dispersant for the chlorinated hydrocarbon is added in an amount sufficient to wet the mica particles. Thereafter, the liquid is removed as by drying the flakes to leave a coated mica. The weight ratio of chlorinated hydrocarbon to mica in this embodiment is desirably about 0.5-5:100. Liquid dispersants suitable for use herein include a diverse group of organic materials that can disperse as dissolve or suspend chlorinated hydrocarbons including, for example, aliphatic and aromatic hydrocarbons, chlorinated hydrocarbons, ethers and the like as well as mixtures of any of these such as benzene, chlorobenzene, methylene chloride, xylene, etc. Aliphatic chlorides such as methylene chloride are found especially suitable, particularly in view of its low boiling point and inflamability. In another embodiment, the mica filler is passed through a fluid medium comprising chlorinated hydrocarbon and liquid dispersant therefor whereupon the mica flakes may bs removed from the medium and dried. Thus, for example, a tack containing aliphatic chloride as methylene chloride and dissolved chlorinated paraffin may serve to coat mica filler as it passes therethrough. After passage through the tank, the mica is conveniently dried at temperatures up to about 0 0 50 0-60 C. The following examples illustrate the invention. In the examples reference is made to the accompanying drawings, in which :- Figures 1 and 2 are electron scanning micrographs using an X-ray mapping technique to identify chlorine on mica treated in accordance with this invention. The chlorine is shown as light dots. Figures 3 and 4 are conventional electron scanning micrographs using secondary electron imaging technique of mica flakes shown in Figures 1 and 2, respectively. Figures 5 and 6 are also electron scanning micrographs illustrating untreated mica flakes using X-ray mapping for chlorine and secondary electron techniques, respectively. EXAMPLE 1 A dry mixture of tumbler mixed mica that is Marietta International Suzorite Mica 63-S (10,000 parts by weight) and Chlorez 700 powder (200 parts by weight) is prepared by gently tumbling together for about two minutes. The dry mixture is formed into a low density slurry by admixing methylene chloride (1000 parts by weight)with agitation for about one minute. The slurried mica particles are placed in an oven maintained at 0 approximately 38 C to dry the mica flakes in one minute. Figures 1 and 2 are scanning electron micrographs that show by X-ray mapping chlorine locations (dots) on mica flakes treated as above. Figures 3 and 4 are conventional (secondary electron) images of the same flakes, respectively as in Figures 1 and 2 at the same enlargement of 2001. A comparison of the micrographs illustrates the higher chlorine concentration at the edges of the mica flakes. Figures 5 and 6 illustrate untreated mica by Xray mapping for chlorine (dots are random noise signals of the system) and also conventional secondary electron image, enlarged 300 times. EXAMPLE 2. The procedures of Example 1 are followed except that the methylene chloride is replaced with a 1:1 mixture of toluene and benzene. Similar results are obtained. EXAMPLE 3. The procedures of Example 1 are followed except that the methylene chloride is replaced with n-hexane. Similar results are obtained. EXAMPLE 4. Using a Welding Engineers 2.0" Twin-Screw Extruder equal parts by weight of Gulk Polypropylene 6420 MHP and coated mica prepared as in Example 1 are compounded. The temperature of the extruder is maintained at 4400F and the polypropylene continuously introduced followed by continuous starve feed introduction of coated mica particles. The twin screws are counterrotating and non-intermeshing and a vacuum of approx. 22 inches is maintained. The resin becomes molten after passage of about 8" along the extruder. The rate of addition yields 600 lb./hr. of compounded product which is sent through a strand die to provide strands about 1/4" or less which are thereafter cooled and diced into pellets. The strands exit the extruder at a temperature 0 of about 450 F. The elapsed time between introducing the resin and exiting of the strands from the extruder is within 15 seconds. The pellets are molded into standard test bars by injecting at 600 psi and 4280F. The resulting bars had good reinforcement properties. EXAMPLE 5. The procedures of Example 4 are followed except that mica treated as in Example 2 herein is used. Again desirable reinforcement of polypropylene is seen when resultant ASTM sample bars are evaluated. EXAMPLE 6. The procedures of Example 1 are followed except that the Chlorez 700 is replaced by a mixture of Chlorowax 70 and Chlorez 760. Similar results are obtained. EXAMPLE 7. Using the quantities of Chlorez 700, Suzorite 60-S mica and methylene chloride set forth in Example 1, the mica flakes and Chlorez 700 are gently tumbled to provide a mixing and placed in a double bottom container that is fitted with a screen of appropriate mesh and slidable bottom. The methylene chloride is added to the mica and Chlorez 700 on the screen and left to stand for about two minutes whereupon the slidable bottom is removed and the liquid collected below. The mica is dryed and exhibits a desirable coating.

Claims: CLAIMS 1. A method of treating mica which comprises enveloping mica flakes with a solid chlorinated hydrocarbon in the presence of a liquid dispersant, and drying the mica flakes. 2. A method according to claim 1 wherein the mica flakes are enveloped in a fluid medium that comprises chlorinated hydrocarbon having 50-75% chlorine by weight and a molecular weight of from 500 to 3000 in a liquid dispersant therefor, and dried at a temperature above 250 C. 3. A method in accordance with Claim 1 or Claim 2 wherein the chlorinated hydrocarbon comprises chlorinated paraffin having from 60 - 80% by weight chlorine. 4. A method according to Claim 1, 2 or 3 wherein the liquid dispersant has a boiling point below 1000C. 5. A method in accordance with any one of Claims 1 to 4 wherein the liquid dispersant comprises a chlorinated aliphatic hydrocarbon. 6. A method in accordance with any one of claims 1 to 5 wherein the mica flakes are enveloped in the said fluid medium by tumbling the mica filler and chlorinated hydrocarbon together to provide a dry blend and wetting the dry blend with the liquid dispersant. 7. A method in accordance with claim 6 wherein the weight ratio of the chlorinated paraffin to mica in the dry blend is 0.5-5:100. 8. A method in accordance with any one of claims 1 to 7 wherein the mica flakes are dried at a temperature below 1000G.

Inventors: BARTOSIEWICZ, LESLIE
Applicants: FORD FRANCE SOCIETE ANONYME, FORD MOTOR COMPANY, FORD MOTOR COMPANY LIMITED, FORD-WERKE AKTIENGESELLSCHAFT
Application year: 1979
Main classification: C08K9
IPC codes: C09C1, C08K9, C08L23, C08L101