A HOT MELT ADHESIVE COMPOSITION AND A PROCESS FOR FILLING A CAVITY IN A SUBSTRATE WITH THIS COMPOSITION

Abstract: Hot melt adhesive compositions comprising a block copolymer, aluminum powder, glass fiber and hollow inor­ ganic silicate microspheres. The block copolymer is selected from the group consisting of copolyesters, copolyamides, copoly(esteramides) and copoly(ether-esters) melting at a temperature above about 150°C. and having from about 30 to about 70 weight percent of hard segments and from about 70 to about 30 weight percent of soft segments. The weight ratio of block copolymer to aluminum powder, glass fiber and silicate microspheres is in the range of about 3:7 to about 3:2, the weight ratio of block copolymer to glass fiber is at least about 2:1, the weight ratio of glass fiber to aluminum powder is at least about 1:9 and wherein the volume percent of silicate microspheres is less than about 10. The compositions are particularly useful for filling voids and cavities in substrates.

Description: A BOT > MELT ADHSIVE COMPOSITION AND A PROCESS FOR FILLING A CAVITY IN A SUBSTRATE WITH THIS COMPOSITION The present invention relates to a hot melt adhesive composition, to a method of filling voids with the adhesive composition and to articles filled or coated with the hot melt adhesive composition. More particularly, it relates to block copolymers containing glass fibers, aluminum powder and hollow inorganic silicate microspheres, to a method of filling voids with such compositions and to articles, filled or coated with the compositions. Hot melt adhesives are well known in the prior art. These materials are conveniently applied to a substrate in the molten state and upon cooling form an adhesive ond. However, a deficiency common to most of the hot melt adhesives of the prior art is their tendency to soften and flow at elevated temperatures, as, for example, 70 to 1000C. with a resulting loss of bond strength Consequently, these materials are not suitable for use over a broad temperature range. Attempts to upgrade the softening and flow temperatures have involved using very high molecular weight resinous materials and/or crosslinking of the resin. These methods have resulted in materials with higher softening points and flow temperatures. However, in mns; cases the resulting material was not adapted to thermal processing:because its higher molecular weight. and/or crosslinked structure engendered extremely high application viscosity. Thus, these materials were not suitable for use as hot melt adhesives. m the manufacture and repair of metal bodies of automobiles and appliances, solder compositions containing lead are frequently used to fill cavities and voids. These lead solders are extremely dense and can add a significant increment to the weight of the metal body. They present a health hazard which mandates special handling to protect workers engaged in the soldering and cavity filling operations, Curable adhesives such as epoxies are generally unsatisfactory for such cavity and void filling applications because they require careful metering of the components to provide good physical properties and bond strength, because they take too long to cure to a sandable state and because they have rather poor weather resistance. Conventional hot melt adhesives are also unsatisfactory for cavity and void filling applications because they cannot be sanded rapidly at assembly line speed, they do not readily accept paint, exhibiting "telegraphing" or "bleed-through", and they do not withstand the high temperatur necessary for the subsequent cure of paint overcoats. "Telegraphing" or 1,bleed-through" are terms used to describe the revelation of difference in composition of the substrate when it has been painted, because of a difference in refle tivity between the painted metal and the painted adhesive composition. U.S, Patent 3,650,999 discloses block copolymer comprising hard polyester segments and soft polyamide segments having improved adhesion and high temperature performance obtained by reacting a crystalline polyester, a C18 to C54 polycarboxylic acid and a primary diamine. This poly(esteramide) in common with other hot melt adhesives has deficienci in creep resistance at temperatures above 16O0C, in the range up to 205 C, and above and in shrinkage when the hot melt is cooled to room temperature after application, These deficien cies have been overcome to a considerable degree by incorpora ing a metal powder into the block copolymer to yield a cavity filling composition which possesses good sandability and pain acceptance. However, the metal powder copolymer composition can lack adequate impact resistance especially at low tempera tures and can sag excessively at elevated temperatures. Attempts to improve the impact resistance by introducing an energy-absorbng reinforcement were generally unsuccessful ar added a further complication of linding of the sanding disc, making sanding extremely difficult. The present invention is directed to an adhesive composition of improved impact resistance at low temperatures, which is less dense and toxic than lead smolder, forms a strong bond to metal and painted metal substrates, withstands extremes of humidity and temperature, has sag resistance at elevated temperatures, is readily trowelled to fill a cavity, sets rapidly to a sandable state, is easily sanded smooth and accepts paint without "bleed-through". The adhesive composition comprises a block copolymer, aluminum powder, glass fiber and hollow inorganic silicate microspheres; wherein the block copolymer is selected from the group consisting of copolyesters, copolyamides, copoly(esteramides) and copoly(ether-esters) melting at a temperature of at least about 1S000., having from about 30 to about 70 weight percent of hard segments and from about70 to about 30 weight percent of soft segments, wherein the weight ratio of block copolymer to aluminum powder, glass fiber and silicate microspheres is in the range of about 3:7 to about 3:2, wherein the weight ratio of block copolymer to glass fiber is at least about 2:1, wherein the weight ratio of glass fiber to aluminum powder is at least about 1:9 and wherein the volume percentage of silicate microspheres is less than about 10. Another aspect of the invention is directed to substrates coated or filled with the adhesive composition and yet another aspect is directed to a method of filling a cavity in a substrate which comprises applying the adhesive composition as a hot melt to fill the cavity, cooling the adhesive composition below the crystallization temperature of the block copolymer and sanding the adhesive composition to provide a surface even with.the surrounding substrate. The block copolymer of the adhesive compositions of the present invention is selected from the group consisting of copolyesters, copolyamides, copoly(ester-amides) and copoly (ether-esters) melting at a temperature of at least about 1500C., having hard segments and soft segments to provide a balance of physical properties and processability. These are considered to exist in microscopic domains within the bulk mass of copolymer resin to provide a heterophase system in which the copolymer will have physical properties reflecting the properties which the respective segments would manifest independently. By control of the relative size, proportions, crystallinity and crystal melting points of the segments, the tack, open time and bond strength of the adhesive can be controlled. The hard segments contribute crystalline blocks to the copolymer so that optimum bulk physical properties such as tensile strength and stiffness can be achieved without incurring the disadvantage of high processing viscosity. The hard or crystalline segments can be polyester or polyamide of weight average molecular weight of from about 400 to about 16,000 to ensure that the segment will contribute the optimum ordered structure to the final polymeric product. Polyesters and polyamides with a weight average molecular weight of less than about 400 have a short chain length and cannot contribute the necessary ordered structure to the final polymeric product which also comprises soft segments. Polyesters and polyamides with a weight average molecular weight of greater than about 16,000 may require excessive reaction times or temperatures to form the final block copolymer leading to degradation of the polymer and a subsequent loss in adhesive properties. To ensure that the final polymeric product has excellent thermal properties such as resistance to flow at elevated temperatures the melting point of the hard polyester or polyamide segment should be at least about 1800C. Preferably, the melting point is in the range of from 2O00C. to 270 C. The hard or crystalline polyester segments of the block copolymer are condensed from at least one aliphatic or alicyclic diol having from 2 to 10 carbon atoms and at least one alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms selected to give a melting point in the desired range. Representative examples of such acids are terephthalic acid, isophthalic acid, hexahydroterephthalic acid, the naphthalic acids, such as 2,6-, 2,7-, 2,8-, 1,4- and 1,5naphthalene dicarboxylic acids and other such acids which form high melting polyester resins. Examples of glycols are ethylene glycol, propylene glycol, tetramethylene glycol, neopentylene glycol, 1,4-cyclohexane diol, 1,4-cyclohexane dimethanol and other such glycols, High melting polymers con tailing components such as 2,2-dimethylpropane diol, form polyesters which have melting points above 2340C. Mixtures of the foregoing polyesters can also be used. Preferably, a polyester from the following group can be used to provide the hard segments of the block copolymer: Poly(ethylene terephthalate/isophthalate), 100/0 to 75/25; Poly(ethyleneXhexameLhylene terepSthalate), 100/0 to 75/25; Poly(ethylene/neopentylene terephthalate), 100/0 to 75/25; Poly(tetramethylene terephthalate/isophthalate), 100/0 to 75/25; Poly(tetramethylene/hexamethylene teraphthalate). 100/0 to 75/25; Poly(tetramethylene/neopentylene terephthalate). 100/0 to 75/25; PolyCethylene/propylene terephthalate), 100/0 to 60/40; and Poly(tetramethylene 2,6-naphthalate/teraphthalate). 100/0 to 75/25; etc. When the hard polyester segments comprise polyethylene terephthalate, the molecular weight range corresponds to an inherent viscosity range of about 0,05 to about 0.7 dl/g 1 determined at 25 C, with a solution of 0,5 g/100 ml in a solvent pair consisting of phenol and sym-tetrachloroethane in the weight ratio of 60:40. The hard or crystalline polyamide segments of the block copolymer can be condensed from at least one aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and at least one aliphatic or alicyclic dicarboxylic acid having from 2 to 12 carbon atoms selected to provide a polyamide with a melting point in the desired range. Examples of diamines include ethylene diamine, 1,3-propane diamine, 1,4-butanediamine, 1,5-pentane diamine, hexamethylene diamine, 1,10decanediamine, cyclohexanediamine, etc, Examples of acids include oxalic, malonic, succinic, glutaric, adipic, pimelic, suberic, azelaic, and sebacic acids. The hard or crystalline polyamide segments of the block copolymer can be obtained by polymerization of g -aminocarboxylic acidswcontaining from 2 to 10 carbon atoms such a,s aminoacetic acid, 3-sminopropionic acid, 4-aminobutyric acid, 6-aminohexoic acid, 10-amindecanoic acid, etc. Polymerization of lactams such as < 2-caprolactam provides a route to several of such polyamides. Among the preferred polyamides are poly(hexamethylene adipamide) and poly( #-caprolactam). The soft, amorphous or low melting segments of the block copolymer contribute wettability, elasticity and rubber character to the copolymer1 They can be polyester, poly (ether-ester) or polyamide and are generally of weight average molecular weight in the range of about 300 to about 16,000 and possess a glass transition temperature less than about 50 C, and more preferably in the range of about -30 to about 40 C, The soft polyester segments of the block copolymer can be condensed from an aliphatic or alicyclic diol having from 4 to 10 carbon atoms and an 'aliphatic, alicyclic or aromatic dicarboxylic acid having from 4 to 54 carbon atoms selected to provide a polyester with a glass transition temperature in the desired range. They can be formed by reacting a polylactone diol of number average molecular weight in the range of about 350 to 6000 with an aliphatic, alicyclic or aromatic dicarboxylic acid having from 4 to 54 carbon atoms Poly(ether-ester) segments can be prepared by condensing a poly(alkylene ether) glycol of number average molecular weight in the range of about 350 to 6000 in which the alkylene groups have from 2 to 10 carbon atoms with an aliphatic, alicyclic or aromatic dicarboxylic acid having from 4 to 54 carbon atoms., Polyamide segments can be prepared by condensing an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms with a mixture of an aliphatic or alicyclic dicarboxylic acid having from 4 to 54, carbon atoms and at least 40 weight percent of an alIphatic dicarboxylic acid having from 18 to 54 carbon atoms. The block copolymers are prepared by a one step or two step method. In the one step method the components which form the hard or soft segments are polymerized in the presence of a prepolymer of the soft or hard segments respectively. In the two step method the hard segments and soft segments are prepared separately as prepolymers and then condensed together. The preferred block copolymer component of the present invention contains about 30 to about ?0 percent by weight of hard segments and conversely about 70 to about 30 percent by weight of soft segments. It is further characterized as having a weight average molecular weight in the range of about 5500 to about 30,000, more, preferably in the range of about 8000 to about 20,000 for an optimal balance of physical properties and processability. The meltingDpoint of the copolymer component is above about 1500C. and is preferably in the temperature range of about 155 to about 2250C,.for ease of processing without degradation of the copolymer. The glass transition temperature associated with the soft segments of the copolymer is generally less than about 50 C. and is preferably in the range of about -30 to 40 C. to contribute wettability, elasticity, and rubber character to the copolymer. The melting point and glass transition temperature are conveniently determined with a duPont differential thermal analyzer Model DTA 900 with the scanning calorimeter attachment, employing a 5 to 25 mg sample heated at a rate of 200C, per minute, in a nitrogen atmosphere. The melt viscosity of the copolymer determined at 2320C. is preferably less than 150,000 centipoise at a shear rate of 4 sec. 1 and is preferably in the range of about 25,000 to 100,000 centipoise. The most preferred group of block copolymers are block copol.y(ester-amides) of the type described in U.S.Patent 3,650,999. They comprise hard segments of polyester as described hereinabove, and soft segments of polyamide formed by condensing a C18 to C54 dicarboxylic acid and a C2 to C13 aliphatic or alicyclic primary diamineq The dicarboxylic acids include the "dimer acids" obtained by dimerization of unsaturated aliphatic monocarboxylic acids, e.g., linoleic acid, available commercially as mixtures of monobasic, dibasic and tribasic acids. The aliphatic or alicyclic diami7es include ethylene diamine 1,3-propane diamine, 1, 4-butanediamine, 1,5-pentane diamine, hexamethylene diamine, 1,10-decanediamine, cyclohexanediamine, 2,2-dimethyl-1,9-propane diamine, -etc. Optionally up to 60 percent by weight of a linear aliphatic dibasic acid having from 'to 17 carbon atoms may be substituted for the corresponding amount of the C18 to C54 polycarboxylic acid used to prepare the soft polyanide. segments of the poiyesteramide. Examples of these acids include oxalic, succinic, adipic, pimelic, suberic, azelaic, sebacic, dodecanedioic and thapsic acids. The advantage of substituting the to C17 aids for the C1s to C54 acids is to provide a more heterogeneous character to the polyamide segments of the polymer and to modify the glass transition temperature, The second component of the adhesive composition is a finely. divided aluminum powder added to improve the creep resistance of the block copolymer and the sandability. It may be of average particle size in the range of about 0.2 micron to about 150 microns and is preferably of average particle size in the range of about 4 to about 50 microns I It is preferred to use an atomized aluminum of generally spheroidal shape particularly when the adhesive composition is used for cavity filling since it allows the hot melt composition to be readily smoothed and burnished when it is sanded. In general, plate-like, acicular or multi-faceted granular aluminum powers are unsatisfactory, surprisingly causing high viscosity in the hot melt and "blinding" or fling and occlusion of sand paper when the adhesive'composition is sanded. In addition to improving the creep resistance and sandability of the adhesive composition, the aluminum powder improves the rate of melting of the adhesive co > osition, allows the composition to be applied and spread qr trowelled more easily with less pressure, allows longer working time or longer "open" time between application of the hot melt and closing of the bond and higher "green" strength or faster onset of bond strength, and reduces the degree of shrinkage of the adhesive composition when it is cooled from the hot melt temperature to ambient temperature When the adhesive composition comprises only the block copolymer and the aluminum powder, the impct. rsistancetends to be low particularly at low temperatures such us -300C, and the molten composition tends to sag at the elevated temperatares at which is appl'ied; Addition of glass fiber as the hlrd component of the adhesive composition improves the impact resistance at low temperatures, reduces the tendency of the adhesive composition to sag at elevated temperatures and permits greater latitude in overcoming shrinkage and minimizing coefficient of expansion differences with the substrate. The glass fiber is of the type conventionally used for reinforcement of thermoplastic resins. It is preferred to use relatively soda-free glasses comprising lime-aluminum borosilicate glass such as types ,C" and "E" glass. The glass fiber should preferably be in the form of milled fibers or chopped fibers of average length in the range of about 1/32 inch (0.8 mm) to about 1/4 inch (6.4 mm) and longer and of diameter-in the range of about 2 to about 20 microns. The preferred average length is in the range of about 1/16 inch (1.6 mm) to about 1/4 inch (6.4 mm). The introduction of glass fiber into the adhesive composition comprising block copolymer and aluminum powder can cause an undesirable decrease in the flow and workability particularly at higher weight ratios of these inorganic components and can require such higher temperatures for application and smoothing of the composition that decompositian of the block copolymer may tend to occur. The addition of a minor amount of inorganic silicate microspheres can cause a further increase in melt viscosity and hence sag resistance but surprisingly the pressure required to extrude the adhesive composition is not appreciably affected and the flow and workability of the hot melt extrudate are not impaired and indeed in the preferred compositions are actually improved. Consequently, a sufficient amount of inorganic silicate microspheres is included in the adhesive composition to obtain this increase in melt viscosity but the amount is limited so that the flow and workaility are not impaired, Generally up to about 10 volume percent and preferably from about 2 to about 8 volume percent of the total composition is required. The silicate microspheres are hollow synthetic inorganic silicate microspheres of average particle size in the range of about 10 to about 150 microns, and preferably in the range of about 50 to about 100 microns. Their average effective particle density is in the range of about 100 g per liter to about 400 g per liter and is preferably in the range of about 150 g per liter to about 250 g per liter. Such microspheres are sold for example by the Philadelphia Quartz Company under the registered trademark Q-Cel. Because of the low density of the silicate microspheres, they comprise less than 2.5 weight percent of the adhesive composition, and preferably less than 1.5 weight percent depending upon the effective particle density of the microspheres. In contrast to the effect obtained with the hollow microspheres, when an equivalent volume of solid microspheres is added to the adhesive composition significant increases in melt viscosity and the pressure required to extrude the melt are observed and the flow and workability of the hot melt composition is impaired. The inorganic components of the adhesive composition may optionally be treated with an effective amount of coupling agent by methods well known to those skilled in the art before or while being blended into the block copolymer. Such coupling agents include organosilane coupling agents exemplified by triethoxy vinyl silane, vinyl methyl dichlorosilane, 2-(trimethoxysilyl)ethyl methacrylate, 3-amino-1-triethoxysilylpropane, etc.; organotitanium coupling agents such as the alkyl alkanoyl titanates. exemplified by C1 to -C40 alkyl stearyl titanates; fatty acids exemplified by oleic and stearic acid, fatty amides exemplified by methacrylato chromic chloride. These coupling agents can cause a significant reduction in the melt viscosity of the blend, can improve the wetting and dispersion of the inorganic components (i.e. the aluminum powder and the glass fiber) and can enhance the physical properties of the adhesive composition. The ratio of the components of the adhesive composition is selected so that the desired balance of flow and workability, adhesion, sag resistance, impact resistance and sandability is achieved. Excessive amounts of glass fiber and silicate microspheres should be avoided since they contribute to very high melt viscosity, cause poor workability as manifested by the difficulty with which the composition can be spread or trowelled and feathered onto a substrate, and decrease the adhesion of the adhesive composition to the sub strate. It is therefore, preferred to select the components so that the weight ratio of block copolymer to inorganic components, i.e., to the sum of aluminum powder, glass fiber and inorganic silicate microspheres, is in the range of about 3:7 to about 3:2 and is preferably in the range of about 1:2 to about 1:1; the weight ratio of block copolymer to glass fiber is at least about 2:1 and is preferably in the range of about 2:1 to about 10:1; the weight ratio of glass fiber to aluminum powder is at least about 1:9 and is preferably in the range of about 1:4 to about 1:1; and the inorganic silicate microspheres comprise up to about 10 volume percent of the adhesive composition. The component ratios are preferably selected so that the melt viscosity of the hot melt composition is less than about 600,000 centipoise and preferably less than. about 300,000 centipoise at a temperature of 2500C. and a shear rate of 4 sec 1 measured in a Brookfield Thermocel Unit Model HBT, When the melt viscosity is greater than 600,000 centipoise, the hot melt is difficult to apply and spread, and tends to be dragged from the point of application. The'hot melt composition is formed by mixing the aluminum powder, the glass fiber and the hollow inorganic silicate microspheres with the melted polymer in any convenient way such as by melt blending in a blender-extruder. A good mix is considered to have been obtained if the filler particles are evenly distributed throughout the melt. In poor mixes, the filler particles are not adequately wet by the melt, and tend to be unevenly distributed remaining aggregated within the melt. Melt stability of the mix is determined by maintaining the mix at 2160C. for two hours. If the melt viscosity changes + less than - 10 percent during this time, the mix is considered to have melt stability, Creep resistance of the compositions of the present invention is determined by observing the sag of a 10 to 15 gram sample of the composition placed on an aluminum plane inclined at SO0 to the vertical. The observations are carried oct at i750 and 2050C. Creep or sag in less than 60 minutes at the designated temperature is recorded as a failure to meet the test. Impact strength is determined by applying the composition as a hot melt at 5000F. (2600C.) to a smooth steel panel 7.5 cm X 22.5 cm to provide a strip 4 cm wide and in the range of 25 to 250 microns thick. The panels are conditioned for 24 hours at -300C. one lb.(454. g)steel balls are dropped onto the strip of composition from heights of 18 inch (46 cm) and 36 inch (92 cm). The impact is repeated three times at 15 minute intervals. If chipping or cracking of the composition or separation from the steel panel occurs, the composition is considered to have failed the test. Similar test panels are prepared for testing of the sandability of the composition. In the preparation of the panels, the pressure needed to extrude the hot melt composition at2600C. through a 3/16 (4.76 mm) nozzle is noted, and the ease of flow of the hot melt extrudate and its ability to be worked by spreading, trowelling and feathering it to a smooth cohesive strip is observed. The panel is cooled to room tem perature.and a disc sander, 12.5 cm. diameter, with 80 grit medium tungsten carbide abrasive, is applied to the composition at 1000 rpm to further smooth and feather the composition. If the surface of the composition becomes smooth enough to accept paint without "telegraphing" or showing a difference in reflectivity between the painted steel and the painted composition, and without blinding or blocking the abrasive surface of the sander, the composition is rated sandable. Depending upon the particular substrate and especially when the substrate is bare metal, it can be advantageous to apply a primer coat to improve the adhesion of the hot melt composition. Suitable primers include the commercially available primer coatings, and the etherified methylolmelamines described in U.S. Patent 4,053,682, Also suitable, can be organic solvent solutions and aqueous dispersions of the block copolymer component of the hot melt adhesive composition. The hot melt adhesive compositions of the preset invention find widespread utility in a wide variety of applications, They are especially valuable in those applications where resistance to creep at elevated temperatures is a necessary requirement. The adhesive compositions of the present invention may be used to great advantage to bond a variety of substrates including metal, glass, synthetic and natural textiles, leathers, synthetic polymeric sheet material, wood, paper, etc. The present invention also includes the concept of incorporating various ingredients into the adhesive composition to improve processing and/or performance of these materials. these additives and adjuncts include antioxidants, thermal stabilizers, extenders, dyes, pigments, adhesion promoters, plasticizers, etc. The following examples are set forth in illustration of the invention and should not be construed as a limitation thereof. Unless otherwise indicated, all parts and percentages are by weight. EXAMPLE 1 A block copolymer which s approximately 65 percent by weight crystalline polyethylene terephthalate segements and 35 percent by weight amorphous polyamide made from dimer acid and hexamethylene diamine is prepared in two steps. In the first step 157.5 parts (0.272 mol) of a C36 dibasic acid and 30.8 parts (0.266 mol) of hexamethylenediamine are charged to a reaction vessel and heated with agitation at about 2150C. for one hour to form a polyamide resin. During the first 30 minutes the pressure rises to 1000 kPa after which time the reaction vessel is vented to reduce the pressure to 600 kPa. At the end of one hour the pressure is released and 332 parts of a crystalline polyethylene terephthalate (M.P. -2600C./ inherent viscostiy 0.147) and 7.5 parts (0,095 mol) of ethylene glycol are charged to the vessel along with a minor amount of an antioxidant, The vessel is flushed with nitrogen and the mixture is heated to about 2800C, while maintaining a nitrogen pressure olf 240 kPa. After 0.5 hour the vessel is vented and vacuum applied and the reaction is continued ur.der full vacuum (0.1 to 5 mm. of mercury)- for two hours. At the end of this time the resulting molten poly(ester-amide) is discharged under pressure into a water bath to quench the material. The polymer obtained melts at 205oC. and the inherent viscostiy is 0.50. To a stainless steel reactor fitted with an anchor agitator and a jacketed hot oil heating system is added 100 parts by weight of the poly(ester-amide) and heating is begun. When the contents have reached 2500C., agitation is begun at 80 rpm and 200 parts by weight of a mixture of 149 parts dry aluminum powder of average particle size about 17 microns, sold by the Aluminum Company of America under the tradeneme Atomized Powder 123, 49 parts milled glass fiber of average length 1/16 inch C1.59 mm), and 1.8 parts hollow inorganic silicate microspheres sold by Philadelphia Quartz Company under the registered tradename Q-Cel 300, of average particle size 75 microns, is fed into the mass at a rate of 10 parts by weight per minute. The agitation is continued and the temperature raised to 2660C, under a nitrogen blanket. Agitation is continued for 15 minutes after the addition of the mixture is complete and the molten mass is discharged under slight N? pressure (250 kPa), quenched in a bath, ground and retried; The melt viscosity of the composition at 2500C. is 198 X 103 centipoise. The pressure required to extrude the hot melt at 2600C. through an orifice of 3/16 inch diameter (4.76 mm) is 70 psi (482 kPa). The adhesive composition is used as a hot melt to fill dents and orifices in a metal plate. It flows and is readily trowelled to yield a smooth coherent mass. It is cooled to room temperature, sanded smooth with 80 grit tungsten carbide abrasive and painted with an automotive surface coating No "telegraphing t' is observed. The composition passes the 18 inch pound (2.03 Joule) and the 36 inch'pound (4.07 Joule) impact tests.- EXAMPLES 2-11 Hot 'melt adhesive compositions are prepared by the procedure of Example 1 from the block copolymer of Example 1. The weight ratio of block copolymer to inorganic components in Examples 2-7 is 1:2 and in Examples 8-11 is 2;3. The weight ratio of aluminum powder to glass fiber is 3:1. In Examples 2-4, 10 and 11 hollow inorganic silicate microspheres are incorporated into the adhesive composition, Examples 5 and a contain no microspheres and Examples 6, 7 and 9, included for comparative purposes, contain solid glass microspheres of average particle size 25 microns. The processability of time hot melt adhesive compositions is evaluated by determining the melt viscosity, the pressure required to cause flow through a 3/16 inch (4.76 mm) orifice and the ease of flow and workability of the hot melt composition applied at a temperature of 2600C. The data including results of Example 1 are presented in Table 1. Examples- 4, 9 and 11 show the increase in melt viscosity obtained with the hollow microspheres. Examples 1, 3 and 10 containing hollow microspheres in the volume percentage range of about 2 to about 6 show improved flow and/or workability in comparison with Examples 5 and 8 without microspheres. In contrast when the microspheres are solid.(Examples 6, 7 and 9) or when the concentration is greater than 10 volume percent (Examples 4 and 11) a very significant increase in pressure for melt extrusion accompanies the increase in melt viscosity and the flow and workability of the hot melt composition is substantially impaired. The lap bond tensile strength of the adhesive composition of Example 10, determined by ASTM Test Method D-1002-72 is 149 kg cm . TABLE I EFFECT OF MICROSPHERES ON PROCESSABILITY OF HOT MELT COMPOSITIONS Pressure Melt needed Weight Ratio Viscosity for flow Flow Workability Block Copolymer Weight % Volume % at 250 C. at at (applied at Example Inorganic Compounds Microspheres Microspheres cps X 10-3 260 C. 260 C. 260 C.) 1 1:2 0.61 (h) 6 198 70 good v.good 2 1:2 0.14 (h) 1.2 228 75 poor poor 3 1:2 0.30 (h) 2.5 208 75 fair fair 4 1:2 1.5 (h) 11.7 > 4000 100 v.poor untrowelable 5 1:2 0 0 216 70 fair poor 6 1:2 6.1 (s) 4.8 452 95 poor v.poor 7 1:2 30 (s) 10.4 > 4000 100 v.poor untrowelable 8 2:3 0 0 120 40 good good 9 2:3 7.1 (s) 5.2 200 100 fair poor 10 2:3 0.78 (h) 5.9 282 25 excellent v.good 11 2:3 1.38 (h) 10.1 > 4000 100 no flow untrowelable h - hollow, s - solid EXAMPLE 12 ; A block copolyester of inherent viscosity about 0.6 containing 65 weight percent of polyethylene terephthalate as the hard segments interlinked by means of terephthaloyl bis N-buryrolactam with 35 weight percent of copoly(hexamethylene isophthalate-terephthalate)- (I:T, 80:20), as the soft segments, is melt blended with the aluminum powder, glass fiber and hollow microspheres of Example 10 and in the weight ratios disclosed therein. The blending process is effected by the method described in Example 1. The blend is used as a hot melt to fill dents and orifices in a metal plate. EXAMPLE 13 By the melt blend process of Example 1, a blend of a block copoly(ether-ester) of inherent viscosity about 0.6 containing 65 weight percent of polybutylene terephthalate as the hard segments and 35 weight percent of the copolyisophthalate- terephthalate (I:T, 80:20) of polytetramethylene ether glycol (having a number average molecular weight about 600) as the soft segments, is prepared from the aluminum powder, glass fiber and hollow microspheres described in Example 1, in the weight ratio of Example 10. The blend is used as a hot melt to fill dents and orifices in a metal plate. EXAMPLE 14 The polyamide of dimer acid and hexamethylene diamine described in Example 1 is melt reacted with a polyhexamethylene adipamide of number average molecular weight about 8000, in the weight ratio of 40:60 to provide a block copolyamide. The copolyamide is melt blended with the aluminum powder, glass fiber and hollow microspheres described in Example 1 and by the process set forth in Example 1. The weight ratio of copolymer, aluminum powder, glass fiber and microspheres is 40:44.6:14,6:0.8, The blend is used as a hot melt to fill dents and orifices in a metal plate.

Claims: CLAIMS WHAT IS CLAIMED IS: 1. An adhesive composition comprising a block copolymer, aluminum powder, glass fiber and hollow inorganic silicate microspheres; characterized in that the block copolymer is a copolyester, copolyamide, copoly (esteramide) or copoly(ether-ester) melting at a temperature of above 1500C., said comp sition having from 30 to 70 weight percent of hard segments and from 70 to 30 weight percent of soft segments; the weight ratio of block Co- polymer to aluminum powder, glass fiber and silicate microspheres is in the range of 3:7 to 3:2, the weight ratio of said block copolymer to glass fiber is at least 2:1, the weight ratio of glass fiber to aluminum powder being at least 1:9 and the volume percentage of silicate microspheres is less than 10. 2. An adhesive composition according to Claim 1 characterized wherein said hard segments of the block Co- polymer are: a) polyester condensates of an aliphatic or alicyclic diol having from 2 to 10 carbon atoms and an alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms, b) polyamide condensates of an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and an aliphatic or alicyclic dicarboxylic acid having from 2 to 12 carbon atoms, or c) polyamide condensates of an amino-carboxylic acid having from 2 to 12 carbon atoms; said soft segments of said block copolymer being polyester condensates of d) an aliphatic or alicyclic diol having from 4 to 10 carbon atoms, e) a polylactone diol of molecular weight in the range of 350 to 6000 and f) an aliphatic, alicyclic or aromatic dicarboxylic acid having from 4 to 54 carbon atoms, poly(ether-ester) condensates of a poly(alkylene ether) glycol of molecular weight in the range of 350 to 6000 in which the alkylene gr ups have from 2 to 10 carbon atoms and an aliphatic, alicyclic or aromatic dicarboxylic acid having from 4 to 54 carbon atoms, or polyamide condensates of an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and a mixture of an aliphatic or alicyclic dicarboxylic acid having from 4 to 54 carbon atoms containing at least 40 weight percent of an aliphatic dicarboxylic acid having from 18 to 54 carbon atoms. 3. An adhesive composition of Claim 1 wherein said block copolymer is a copolyester, said hard segments being condensed from an aliphatic or alicyclic diol having from 2 to 10 carbon atoms and an alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms and said soft segments being condensed from an aliphatic or alicyclic diol having from 4 to 10 carbon atoms, a polylactone diol of molecular weight in the range of 350 to 6000 or a poly(alkylene ether) glycol of molecular weight in the range of 350 to 6000 in which the alkylene groups have from 2 to 10 carbon atoms and an aliphatic, alicyclic or aromatic dicarboxylic acid having from 6 to 54 carbon atoms. 4. An adhesive composition according to Claim 1 characterized in that said block copolymer is a copolyamide wherein said hard segments are condensed from an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and an aliphatic or alicyclic dicarboxylic acid having from 2 to 12 carbon atoms or an g -aminocarboxylic acid having from 2 to 12 carbon atoms, said soft segments being condensed from an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and a mixture of aliphatic and alicyclic dicarboxylic acids having from 4 to 54 carbon atoms containing at least 40 weight percent of an aliphatic dicarboxylic acid having from 18 to 54 carbon atoms. 5. An adhesive composition according to Claim 1 characterized wherein said block copolymer is a copoly (ester-amide) said hard segments being condensed from an aliphatic or alicyclic diol having from 2 to 10 carbon atoms and an alicyclic or aromatic dicarboxylic acid having from 8 to 20 carbon atoms, said soft segments being condensed from an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and a mixture of aliphatic or alicyclic dicarboxylic acids having from 4 to 54 carbon atoms containing at least 40 weight percent of an aliphatic dicarboxylic acid having from 18 to 54 carbon atoms. 6. An adhesive composition according to Claim 1 characterized wherein said block copolymer is a copoly (ester-amide), said hard segments being condensed from an aliphatic or alicyclic diamine having from 2 to 12 carbon atoms and an aliphatic or alicyclic dicarboxylic acid having from 2 to 12 carbon atoms or an U)-aminocarboxylic acid having from 2 to 12 carbon atoms, said soft segments being condensed from an aliphatic or alicyclic diol having from 4 to 10 carbon atoms or a poly(alkylene ether) glycol of molecular weight in the range of about 350 to about 6000 in which the alkylene groups have from 2 to 10 carbon atoms and an aliphatic, alicyclic or aromatic dicarboxylic acid having from 6 to 54 carbon atoms. 7. An adhesive composition according to Claim 5 characterized wherein said polyester is poly(ethylene terephthalate), poly(tetramethylene terephthalate), co-poly (butylene terephthalate)-(ethylene terephthalate), co-poly (ethylene terephthalate)-(ethylene isophthalate) or copoly (ethylene terephthalate) - (propylene terephthalate), said polyamide segments being condensed from a C36 dimer acid and hexamethylene diamine. 8. An adhesive composition according to Claim 1 having a melt viscosity at 2500C. of less than 600,000 centi -1 poise at a shear rate of 4 sec. 9. An adhesive composition of Claim 1, 5 or 6, characterized wherein said hard segment prior to incorporation in the block copolymer has a weight average molecular weight in the range of 400 to 16,000 and a melting point in the range of 180 to 2700C. 10. An adhesive composition according to Claim 9 characterized wherein said block copolymer has a weight average molecular weight in the range of 5500 to 30,000 and a glass transition temperature in the range of -30 to 400C. 11. An adhesive composition according to Claim 10 characterized wherein said aluminum powder is spheroidal and has an average particle size in the range of 0.2 to 150 microns. 12. An adhesive composition according to Claim 11 characterized wherein said glass fiber is milled glass fiber of average length at least 0.8 mm. 13. An adhesive composition according to Claim 12 characterized wherein said silicate microspheres comprise from 2 to 8 volume percent of the adhesive composition and are of average particle size in the range of 10 to 150 microns. 14. A substrate characterized by being bonded with the composition of Claim 10 or 13. 15. A method of filling a cavity in a substrate characterized by applying excess adhesive composition as a hot melt into the cavity, spreading the adhesive composition to fill the cavity, cooling the adhesive composition below its crystallization temperature and sanding the adhesive composition to provide a surface even with the surrcunding substrate, wherein the adhesive composition comprises: : c., a poly(ester-amide) block copolymer of weight average as,ecl;lar weight in the range of 5500 to 3O,000 and of melting point in the range of 1550C. to 2250C., having from 30 to 70 percent by weight of crystalline polyester segments of poly(ethylene terephthalate), poly(tetra methylene terephthalate), co-poly(butylene terephthalate) (ethylene terephthalate), co-poly(ethylene terephthalate) (ethylene isophthalate) and co-poly(ethylene terephthalate) (propylene terephthalate) which prior to incorporation in the poly(ester-amide), have a weight average molecular weight in the range of 400 to 16,000 and a melting point in the range of 180 to 2700C., and from 70 to 30 percent by weight of amorphous polyamide segments of glass transi tion temperature in the range of -30 to 400C., condensed from a C18 to C54 dibasic acid and an aliphatic or alicy clic diamine containing from 2 to 10 carbon atoms; b) spheroidal aluminum powder of average particle size in the range of 4 to 50 microns; c) milled glass fiber of average length in the range of 1.6mm to 6.4 mm; and d) hollow inorganic silicate microspheres of average particle size in the range of 10 to 150 microns; the weight ratio of block copolymer to aluminum powder, glass fiber and silicate microspheres being in the range of 1:2 to 1:1, the weight ratio of block copolymer to glass fiber being in the range of 2:1 to 10:1, the weight ratio of glass fiber to aluminum powder is in the range of 1:4 to 1:1 and the silicate microspheres comprise from 2 to 8 volume percent of the adhesive composition. 16. A method according to Claim 15 characterized wherein said dibasic acid is a C36 dimer acid and the diamine is hexamethylene diamine. 17. A method according to Claim 16 characterized wherein said crystalline polyester segments are poly(ethylene terephthalate). 18. A method according to Claim 15 characterized wherein said adhesive composition has a melt viscosity at 250"C. of less than 600,000 centipoise at a shear rate of -1 4 sec.

Inventors: DONERMEYER, DONALD DAVID, MARTINS, JOSEPH GALVAM
Applicants: MONSANTO COMPANY
Application year: 1979
Main classification: C09J5
IPC codes: C08G63, C09J167, C09D5, C09J177