LIQUID EMULSION POLYMERS, PROCESS FOR PREPARING THEM AND AQUEOUS COMPOSITIONS THICKENED WITH THESE EMULSIONS

Abstract: Novel aqueous liquid emulsion polymers are prepared by the copolymerization of (A) 15-60 weight percent of a C₃-C₈ α,β-ethylenically unsaturated carboxylic acid mono­ mer, preferably acrylic or methacrylic acid or a mixture thereof with itaconic or fumaric acid, (B) 15-80 weight per­ cent of a nonionic copolymerizable C₂-C₁₂ α,β-ethylenically unsaturated monomer, preferably a monovinyl ester such as ethyl acrylate or a mixture thereof with styrene, acrylonitrile, vinyl chloride or vinyl acetate, and (C) 1-30 weight percent of certain nonionic vinyl surfactant esters, such as nonyl­ phenoxypoly (ethyleneoxy)₉ ethyl acrylate, to give an emul­ sion copolymer stable as an aqueous colloidal dispersion at an acid pH lower than about 5.0 but responsive to pH adjustment with base. These emulsion polymers adjusted to a pH of 5.5-10.5 or higher are effective thickeners for a wide variety of aqueous systems including cosmetic products, drilling muds, and particularly aqueous coating composi­ tions such as latex paint.

Description: LIQUID EMULSION POLYMERS USEFUL AS pH RESPONSIVE THICKENERS FOR AQUEOUS SYSTEMS Polymeric water-soluble thickening agents are widely known and used in many aqueous systems including latex paints and other aqueous coating compositions-. The widespread use of latex paints, i.e., paints based on aqueous dispersions of synthetic organic polymers, has prompted continued research on product and process improvements. One particularly important concern is controlling the paint rheology to obtain proper flow and leveling with a minimum of dripping and spattering. Cellulose ethers, such as described in Glomski et al. U.S. 3,769,247, are often effectively used as thickeners for latex paints. However, solid, water-soluble polymers derived from cellulose and other natural products are becoming increasingly expensive to produce because of high capital, energy, and waste control costs. Alkali soluble latex copolymers have been known for some time. Thus, Hager and Martin U.S. 3,003,987 and 3,070,561 and Miller U.S. 3,081,198 describe copolymers of acrylic and methacrylic acids and esters which may be thickened by replacing a portion of the hydrogen ions of the copolymer carboxyl groups with ammonium or alkali metal ions. Other types of polymeric thickeners are disclosed by Junas and LaTorre U.S. 3,652,497 and 3,708,445, Zimmerman U.S. 3,657,175, Chang and McDowell U.S. 3,891,591, and Gibson U.S. 4,003,870. All contain various carboxylic acid groups which can be solubilized in water by neutralization with a water-soluble base. However, to date this technology has had limited impact on major markets for water-soluble polymeric thickeners. More recently, Evani and Corson developed, as described in U.S. 4,008,202 and related patents, a solid styrene-maleic anhydride-vinylbenzyl ether terpolymer soluble at high pH and useful as a thickener for aqueous solutions. In spite of excellent rheology, stability problems and cost have limited its use as a paint thickener. Further improvements in this technology are clearly desirable. This invention relates to new aqueous emulsion polymers which provide stable liquid emulsions having low viscosity and relatively high solids content under acidic conditions, but which become very efficient polymeric thickeners for many aqueous systems when treated with base. These new products are preferably prepared in the form of an aqueous colloidal dispersion of water-insoluble polymer by emulsion polymerization at a pH of about 2.5 to 5.0 of three essential ethylenically unsaturated monomeric components: (A) a carboxylic acid monomer, (B) a nonionic vinyl monomer and (C) a nonionic vinyl surfactant ester. More specifically, a polymer useful as a pH responsive thickener for aqueous systems has been developed comprising an aqueous emulsion copolymer of: A. 15-60 weight percent based on total monomes of at least one C3-C8 a,ss-ethylenically unsaturated carboxylic acid monomer of the formula: EMI3.1 where R is H and R' is H, C1-C4 alkyl, or -CH2COOX; R is -COOX and R' is H or -CH2COOX; or R is CH3 and R' is H; and X is H or C1-C4 alkyl; B. 15-80 weight percent of at least one nonionic, copolymerizable C2 -C12 a,ss-ethylenical1y unsaturated monomer of the formula: CH2 = CYZ (11) where Y is H and Z is -COOR, -C6H4R', CN, Cl, EMI3.2 Y is CH3 and Z is -COOR, -C6H4R', CN or -CH = CH2; or Y and Z are Cl; and R is C1-C8 alkyl or C2-C8 hydroxyalkyl; R' is H, C1, Br, or C1-C4 alkyl; and R" is C1-C8 alkyl; and C. 1-30 weight percent based on total monomers of at least one nonionic vinyl surfactant ester of the formula: EMI4.1 where R is H or CH3, each R' is C1-C2 alkyl, R" is C8-C20 alkyl or C8-C16 alkylphenyl, n is an average number from about 6-100 and m is an average number from about 0-50 provided that n > m and t(n-tm) is about 6-100; said polymer being stable as an aqueous colloidal dispersion at a pH lower than about 5.0 but becom ing an effective thickener for aqueous systems upon adjustment to a pK of 5.5-10.5 or higher. The emulsion polymerization is normally carried out under acidic conditions in which the carboxylic acid groups are in protonated form to insolubilize the polymer and give a liquid emulsion. When the polymeric thickener is added as such a liquid colloidal dispersion, the finely divided polymer particles dissolve almost instantly upon pK adjustment. The ease of handling, metering, and dispersing the liquid emulsion polymer, the rapid solubilization by controlled pH adjustment, and the highly desirable rheological properties make this liquid emulsion polymer a most effective and efficient thickening agent for a wide variety of applications including latex paints and other aqueous coating compositions. 1. Essential Monomeric Components The novel liquid emulsion polymers of this invention require three essential components: (A) 15-60 weight percent of a C3-C8 a,ss-ethylenically unsaturated carboxylic acid monomer, (B) 15-80 weight percent of a copolymerizable nonionic vinyl monomer, and (C) 1-30 weight percent of certain nonionic vinyl surfactant esters. It has been dis- covered that the effectiveness of these liquid emulsion polymers as a pH responsive thickener for many aqueous products is critically dependent on these components. The acid component A provides the requisite pH responsiveness; the nonionic vinyl comonomer B provides an extended polymer backbone and added hydrophilic -lipophilic balance; and the nonionic vinyl surfactant ester C provides an in situ, bound surfactant to control the rheology of the aqueous system containing the solubilized polymeric thickener. Within the stated limits, the proportions of the individual monomers can be varied to achieve optimum properties for specific applications. A. Carboxylic Acid Monomer The liquid emulsion polymer requires 15-60 weight percent based on total monomers of a C3-C8 a,ss-ethylenically unsaturated carboxylic acid monomer of the formula: EMI6.1 where R is H and R' is H, C1-C4 alkyl, or -CH2COOX; R is -COOX and R' is H or -CH2COOX; or R is CH3 and R' is H; and X is H or C1-C4 alkyl. Acrylic or methacrylic acid or a mixture thereof with itaconic or fumaric acid are preferred, but crotonic and aconitic acid and half esters of these and other polycarboxylic acids such as maleic acid with C1-C4 alkanols are also suitable, particularly if used in minor amount in combination with acrylic or methacrylic acid For most purposes, it is preferable to have at least about 25 weight percent and most preferably from about 35-55 weight percent of the carboxylic acid monomer. However, polycarboxylic acid monomers and half esters can be substituted for a portion of the acrylic or methacrylic acid, e.g., 1-15 weight percent based on total monomers. B. Nonionic Vinyl Monomer To provide the extended polymer backbone and body needed for effective thickening requires 15-80 weight percent of at least one copolymerizable nonionic C2-C12 a,ss-ethylenically unsaturated monomer selected from the group consisting of the formula: CH2=CYZ (11) where Y is H and Z is -COOR, -C6H4R', CN, Cl, EMI7.1 Y is CH3 and Z is -COOR, -C6H4R', CN or -CH = CH2; or Y and Z are Cl; and R is C1-C8 alkyl or C2-C8 hydroxyalkyl; ' is H, Cl, Br, or C1-C4 alkyl; R" is C1-C8 alkyl. Typical of such monomers are the C1-CS alkyl and C2-C8 hydroxyalkyl esters of acrylic and methacrylic acid including ethyl acrylate, ethyl methacrylate methyl methacrylate, 2-ethylhexyl acrylate, butyl acrylate, butyl methacrylate, 2-hydroxyethyl acrylate, 2-hydroxybutyl methacrylate; styrene, vinyltoluene, t-butylstyrene, isopropylstyrene, and p-chlorostyrene; vinyl acetate, vinyl butyrate, vinyl caprolate; acrylonitrile, methacrylonitrile, butadiene, isoprene, vinyl chloride, vinylidene chloride, and the like. In practice, a monovinyl ester such as ethyl acrylate or a mixture thereof with styrene, hydroxyethyl acrylate, acrylonitrile, vinyl chloride or vinyl acetate is preferred. These monomers, of course, must be copolymerizable with the carboxylic acid and vinyl surfactant ester comonomers. Normally 15-80 weight percent, and preferably 20-60 weight percent of nonionic vinyl monomer, based on total weight of monomers, is used in preparing the liquid emulsion polymer. C. Nonionic Vinyl Surfactant Ester The third required monomer component is 1-30 weight percent based on total monomers of a nonionic vinyl surfactant ester of the formula: EMI8.1 where R is H or CH3; each R' is C1-C2 alkyl; P is C8-C20 alkyl or C8-C16 alkylphenyl; n is an average number from 6-100 and m is an average number from 0-50 provided that n > m and 2(n+m) is 6-100. Preferred are the acrylate and methacrylate surfactant esters selected from the group consisting of: 1) alkylphenoxypoly(ethyleneoxy)ethyl acrylates of the formula: EMI8.2 where R is H or CH3; Y' is C8-C16 alkyl, and n is 6-100; 2) alkoxypoly(ethyleneoxy)ethyl acrylates of the formula: EMI8.3 where R is H or CH3, R" is C8-C20 alkyl, and n is 6-50; and 3) alkoxypoly(alkyleneoxy)ethyl acrylates of the formula: EMI9.1 where R is H or CH3, each R' is C1-C2 alkyl, R" is C8 -C20 alkyl, and n is 6-50 and m is 1-40. These essential vinyl surfactant esters are the acrylic or methacrylic acid esters of certain nonionic surfactant alcohols. Such surfactant esters are known in the art. For example Junas et al. U.S. 3,652,497 describe the use of alkylphenoxyethyleneoxv- ethyl acrylates in preparing several other polymeric surfactant thickeners. Dickstein U.S. 4!075,411 describes several processes for preparing such vinyl surfactant esters including the acid catalyzed condensation of commercially available nonionic polyoxyalkylene surfactant alcohols such as alkylphenoxypoly(ethrleneoxy) ethyl alcohol and block-polymeric glycols with acrylic, methacrylic, crotonic, maleic, fumaric, itaconic or aconitic acid. Alternate esterification methods includ- ing alcoholysis and transesterification are also described. Other suitable vinyl surfactant esters can be prepared from monoethers of mixed or heteric ethyleneoxy- -propyleneoxy-butyleneoxy polyglycols such as described in Patton U.S. 2,786,080. Additional surfactant alcohols which can be esterified for use herein are given in "McCutcheon's Detergents and Emulsifiers" 1973, North American Edition, Allured Publishing Corp., Pidaewood, N. J. 07450. Certain of these vinyl surfactant esters, i.e., those defined by Formula III and particularly the alkylphenoxy and alkoxyethyl esters of Formulas IV-VI, are useful in preparing the novel emulsion polymers described herein. It is essential that the surfactant be incorporated in the liquid emulsion product by copolymerization. Advantageously the requisite surfactant esters are prepared by the direct acid catalyzed esterification of the appropriate surfactant alcohol with an excess of the carboxylic acid monomer used as Component A. The resulting mixture with excess acid can be used directly in the copolymerization provided that at least 30 percent, and preferably 50-70 percent or more, of the surfactant alcohol in the mixture is esterified. The vinyl surfactant ester can also be recovered, purified by conventional means using an appropriate inhibitor such as hydroquinone or p-tert -butylcatechol to prevent undesired homopolymerization, and then used to prepare the liquid emulsion polymers. It has been found that the hydrophiliclipophilic balance (HLB) of the vinyl surfactant ester is an important factor in the performance of the resulting emulsion polymer. Thus for a given polyethyleneoxy content, increasing the chain length of the terminal hydrophobic alkoxy or alkylphenoxy group will increase the efficiency of the resulting polymer as a thickener. Also for a given lipophilic group decreasing the number of polyethyleneoxy groups increases thickener efficiency. For many surfactant esters usable herein an average of 10-40 ethyleneoxy groups (e.g., Formula III, n=10-40) is preferred. Also it has been found that the hydrophilic balance of the copolymer product can be adjusted to a degree by the judicious selection of the nonionic vinyl monomer B; e.g., a soft, (lower alkyl)poly(ethyleneoxy)ethyl ester of Formula VI can be used in a system with mixture of ethyl acrylate and a hard comonomer such as styrene. However, it is critical to the performance of these products that they contain an effective amount of an in situ, bound surfactant to control the rheology of the aqueous system thickened with the solubilized emulsion polymer. 2. Copolymerization The novel liquid emulsion copolymers are conveniently prepared from the above-described monomers by conventional emulsion polymerization at an acid pH lower than about 5.0 using free-radical producing initiators, usually in an amount from 0.01 percent to 3 percent based on the weight of the monomers. The free-radical producing initiators conveniently are peroxygen compounds especially inorganic persulfate compounds such as ammonium persulfate, potassium persulfate, sodium persulfate; peroxides such as hydrogen peroxide; organic hydroperoxides, for example, cumene hydroperoxide, t-butyl hydroperoxide; organic peroxides, for example, benzoyl peroxide, acetyl peroxide, lauroyl peroxide, peracetic acid, and perbenzoic acid (sometimes activated by a water-soluble reducing agent such as ferrous compound or sodium bisulfite); as well as other free-radical producing materials such as 2,2 '-azobisisobutyronitrile. Optionally, a chain transfer agent and an additional emulsifier can be used. Representative chain transfer agents are carbon tetrachloride, bromoform, bromotrichloromethane, long chain alkyl mercaptans and thioesters such as n-dodecyl mercaptan, t-dodecyl mercaptan, octyl mercaptan, tetradecyl mercaptan, hexadecyl mercaptan, butyl thioglycolate, isooctyl thioglycolate, and dodecyl thioglycolate. The chain transfer agents are used in amounts up to about 10 parts per 100 parts of polymerizable monomers. Often at least one anionic emulsifier is included in the polymerization charge and one or more of the known nonionic emulsifiers may also be present. Examples of anionic emulsifiers are the alkali metal alkyl aryl sulfonates, the alkali metal alkyl sulfates and the sulfonated alkyl esters. Specific examples of these well-known emulsifiers are sodium dodecylbenzenesulfonate, sodium disecondary-butylnaphthalene sulfonate, sodium lauryl sulfate, disodium dodecyldiphenyl ether disulfonate, disodium n-octadecylsulfosuccinamate and sodium dioctylsulfosuccinate. Optionally, other ingredients well known in the emulsion polymerization art may be included such as chelating agents, buffering agents, inorganic salts and pH adjusting agents. Polymerization at an acid pH lower than 5.0 permits direct preparation of an aqueous colloidal dispersion with relatively high solids content without problems of undue viscosity. Usually the copolymerization is carried out at a temperature between 600C and 90"C but higher or lower temperatures may be used. The polymerization is carried out batchwise, stepwise or continuously with batch and/or continuous addition of the monomers in a conventional manner. The essential monomers can be copolymerized in such proportions, and the resulting emulsion polymers can be physically blended, to give products with the desired balance of properties for specific applications. For example, if a more viscous product is desired, the acid and surfactant monomer content can be increased. Greater flexibility and coalescence can be obtained with higher amounts of ethyl acrylate. Addition of styrene as a second nonionic vinyl monomer will increase to a higher pH the adjustment required to dissolve the emulsion in an aqueous coating composition. Minor quantities of a polyfunctional monomer, such as itaconic or fumaric acid or isoprene to introduce a higher carboxylic acid content or limited crosslinking, provides further control on the solubility of the emulsion polymer after pH adjustment. Thus, by varying the monomers and their proportions, emulsion polymers having optimum properties for particular applications can be designed. In practice it is normally desirable to copolymerize 15-60 weight percent based on total monomers (more desirably from 25-60 weight percent, preferably 35-55 percent, and most preferably 40-50 percent) of the carboxylic acid monomer A, 15-80 weight percent (preferably 20-50 percent, and most preferably 35-50 percent), of the nonionic vinyl monomer B and 1-30 weight percent (preferably 2-20 percent, and most preferably about 2-12 percent) of the nonionic vinyl surfactant ester C. Particularly effective liquid emulsion polymer thickeners are obtained by copolymerization of about 40-50 weight percent of methacrylic acid, about 35-50 weight percent of ethyl acrylate, and about 2-12 weight percent of the methacrylic ester of a Cg-alkylphenoxy(ethyleneoxy)9 ethyl alcohol. 3. Copolymer Properties The copolymer products prepared by emulsion polymerization at an acid pH are in the form of stable aqueous colloidal dispersions usually with a typical milky latex appearance. Such a liquid emulsion contains the copolymer dispersed as discrete particles having average particle diameters of 500-3000 , preferably 1000-1750 , as mesured by light refraction. Dispersions containing polymer particles smaller than 500 A are difficult to stabilize while particle larger than 3000 reduce the ease of dispertion in the aqueous products to be thickened. These emulsion copolymers will normally have number average molecular weights of at least 30,000 as determined by gel permeation chromatography. To provide most effective thickening with copolymers which are water-soluble when neutralized, molecular weights within the range of 200,000 to 5,000,000 are preferred. In terms of a standard Brookfield viscosity measured as a 1 percent aqueous solution in ammonium salt form at pH 9 and 250C, a copolymer with a viscosity of 50-50,000 cps, and preferably 100-30,000 cps, is particularly desirable for many applications. In the form of a stable, aqueous colloidal dispersion at an acid pH of 2.5-5.0 the copolymer is particularly useful. Such aqueous dispersion may contain 10-50 weight percent of polymer solids yet be of relatively low viscosity. Thus it is readily metered and blended with aqueous product systems. However, the dispersion is pH responsive. then the pH of the polymer dispersion is adjusted by addition of a base such as ammonia, an amine or a non-volatile inorganic base such as sodium hydroxide, potassium carbonate or the like, the aqueous mixture becomes translucent cr transparent as the polymer dissolves at least partially in the aqueous phase with a concurrent increase in viscosity. This neutralization can occur in situ when the liquid emulsion polymer is blended with an aqueous solution containing a suitable base. Or if desired for a given application, pH adjustment by partial or complete neutralization can re carried out before or after blending the liquid emulsion polymer with an aqueous product. The term "liquid emulsion polymer" as applied to the new thickener of this specification means tnat the thickener is an emulsion polymer because the polymer was prepared b emulsion polymerization even though the polymer per se may be (and generally isj a solid at room temperature but is a "liquid! emulsion polymer because it is in the form of a liquid solution or dispersion. The pH viscosity response curves for several typical liquid emulsion polymers prepared by copoly- merizing methacrylic acid (MAA), ethyl acrylate (E > ), and nonylphenoxypoly(ethyleneoxy)9ethyl methacrylate (VSE-1A) are shown in the Figure as determined in aqueous media at a concentration of 1 percent by weight and at room temperature. Note that the pH range of initial viscosity build can be controlled by variation in the composition of the emulsion copolymer. 4. Use as A Thickener These emulsion polymers are useful as watersoluble thickeners for a wide variety of applications ranging from cosmetics to drilling muds. They are particularly useful as thickeners for a wide variety of water-based compositions including aqueous brine and polymer solutions as well as aqueous slurries and colloidal dispersions of water-insoluble inorganic and organic material including compositions such as natural rubber, synthetic or artificial latexes and aqueous products containing such materials. Synthetic latexes which may be thickened with the liquid emulsion polymers are aqueous colloidal dispersions of water-insoluble polymers prepared by emulsion polymerization of one or more ethylenically unsaturated monomers. Typical.of such synthetic latexes are emulsion copolymers of monoethylenically unsaturated compounds such as styrene, methyl methacrylate, acrylonitrile with a conjugated diolefin such as butadiene or isoprene; copolymers of styrene, acrylic and methacrylic esters, copolymers of vinyl halide, vinylidene halide, vinyl acetate and the like. Many other ethylenically unsaturated monomers or mixtures thereof can be emulsion polymerized to form synthetic latexes. Representative monomers are vinyl aromatic monomers such as styrene, a-methylstyrene, t-butylstyrene, chlorostyrene, vinyltoluene; conjugated dienes such as butadiene, isoprene, and 2-chloro-1,3-butadiene; vinyl chloride, vinylidene chloride, acrylonitrile, and methacrylonitrile; acrylic and ss-hydroxyalkyl acrylic esters; vinyl acetate, vinyl propionate, ethylene and methyl isopropenyl ketone. Also limited amounts of unsaturated carboxylic acid monomers such as defined by Formula I are frequently used in preparing the base polymer for latex paints The artificial latexes are latexes which are produced by the dispersion or redispersion of pre-formeÅa water-insoluble polymers or solutions thereof. The artificial latexes are produced by known emulsification processes, e.g., by addition of water with stirring until phase inversion occurs, by high shear mixing with water at elevated temperatures or by dilution of a mixture of water and a water-miscible solvent followed by stripping to remove the solvent. A surfactant is required in the emulsification process unless hydrophilic groups are attached to the polymer in sufficient quantity to assist dispersion but in insufficient quantity to produce water-solubility. Such artificial latexes are produced from polymers which are not prepared readily from monomers by emulsion polymerization, either because no substantial polymerization at a commercially acceptable rate is obtained under usual emulsion polymerization conditions, such as with isobutene, or because a particular form of the polymerized monomer is desired, for example, stereospecific polyisoprene, stereospecific polybutadiene and the like. Representative pre-formed polymers are polymers and copolymers of the mono-olefins having from 2 to 20 carbon atoms such as ethylene, propylene, l-butene, 2-butene, isobutene, pentene, hexene, octene, dodecene, hexadecene, octadecene and especially those mono-olefins having up to 8 carbon atoms. Especially common types are the various ethylene/propylene copolymers. Iilustrative of still other polymers which can be converted to artificial latexes are alkyd resins, block and graft copolymers; e.g., styrene/butadiene graft and block copolymers; epoxy resins such as the reaction products of epichlorohydrin and bisphenol-A; and thermosettable vinyl ester resins; e.g., the reaction products of approximately equivalent amounts of a polyepoxide and an unsaturated monocarboxylic acid such as acrylic acid and methacrylic acid or unsaturated fatty acids such as oleic acid. The thickeners of this invention are advantageous for use with the water-based compositions according to the foregoing description and with compositions containing those materials1 especially coating compositions of various types. Mixtures of two or more thickeners may be used, if desired. Of course the latex polymers used in coating compositions are preferably film-forming at temperatures below about 250C, either inherently or through the use of plasticizers. Such coating compositions include water-based consumer and industrial paints; sizing, adhesives and other coatings for paper, paperboard, and textiles. Usually these latex coating compositions contain added pigments, fillers and extenders such as titanium dioxide, barium sulfate, calcium carbonate, clays, mica, talc, and silica. The novel liquid emulsion polymers described herein are compatible with most latex paint systems and provide highly effective and efficient thickening. Suitable results are obtained using 0.05-5.0 weight percent of the liquid emulsion polymer based on total weight of lid; and preferably 0.1-2.0 weight percent. The aqueous compositions thickened With the liquid emulsion polymers of this Invention preferably are those in which any dispersing or solvating liquid present consists of greater than 50 percent bv weight of water. The following examples illustrate further present invention. Unless otherwise indicate, all parts and percentages are by weight. Example 1 - Preparation of Vinyl Surfactant Esters The following are typical proceduresfor the preparation of the vinyl surfactant ester (VSE). A. Nonylphenoxypoly(ethyleneoxy)9ethyl Methacrylate A stainless steel reactor was charged with 474 parts (0.68 mole) of nonylphenoxypoly(ethyleneoxy)9- ethanol (Igepal# CO-660 from GAF), 0.31 part of hydrquinone and 0.16 part of IcnolN (2,6-di-t-butyl-p-cresol from Shell Chemical Co.). Then 8.6 parts of 0+2 percent H2SO4 was added with stirring followed L 526 parts (6.1 moles) of methacrylic acid stabilized with monomethyl ether of hydroquinone (MEHQ). With a slow stream of air bubbling through the reactant mixture, the reactor was heated at 1050C for two hours, cooled and then liquid product (VSE-lA) recovered. By liquid chromatographic analysis, the neat product contained 47.2 weight percent surfactant ester (90 percent conversion), 4.8 weight percent unreacted surfactant, 46.8 weight percent excess methacrylic acid and 1.2 weight percent water, sulfuric acid and stabilizers. The vinyl surfactant ester can be used neat for the preparation of the desired emulsion copolymers or the ester can be recovered by conventional means. For use in neat form, 2 conversion to vinyl ester of at least 30-40 percent is desirable to avoid too high free surfactant level in the subsequent emulsion polymerization. With a 4-10 fold excess of carboxylic acid monomer, 70-90 percent conversion can normally be obtained at 1000-1200C in 2-4 hours. Other strong acid catalysts including p-toluenesulfonic acid and strong acid cation exchange resins such as Dowexe 50 (H+ form) can be used, but 90 percent H2 SO4 is effective and convenient. Indeed, this general H2 504 catalyzed process has been used with a wide variety of C8-C16 alkylphenoxypolytethyleneoxy)ethanols. B. Nonylphenoxypoly(ethyleneoxy)39ethyl Methacrylate A mixture of 222 parts of nonylphenoxypoly (ethyleneoxy)39ethanol, 384 parts of methacrylic acid, 0.06 part of hydroquinone and 0.08 part of Ionole was blended in a stirred glass reactor and 5.5 parts of concentrated H2 SO4 was added as esterification catalyst. The mixture was slowly heated to 110 C, held at 110 C for an additional 145 minutes and then cooled to give 611 parts of a neat ester (VSE-1B) containing 38 weight percent of the surfactant ester and 62 weight percent of unreacted methacrylic acid. C. Dodecylphenoxypoly(ethyleneoxy)10ethyl Methacrylate A mixture of 74.4 parts (0.1 mole) of dodecyl phenoxypoly(ethyleneoxy)10ethanol (T-Det DD-ll from Hayworth Chemical Co.), 129 parts (1.5 moles) of methacrylic acid and 0.06 part each of hydroquinone and IonolC was blended in a stirred glass reactor and 1.8. parts concentrated H2 SO4 added as esteriflcation catalyst. The mixture was slowly heated to 112 C, held at 112 C for an additional 165 minutes and then cooled to give 205 parts of a neat ester (VSE-1C) containing 40.5 weight percent of the surfactant ester and 59.5 weight percent of unreacted methacrylic acid. D. n-Octyloxypoly(ethyleneoxy)19ethyl Methacrylate In a similar manner the n-octyl polyethylene glycol ether obtained by condensation of n-octanol with 20 moles of ethylene oxide was esterified with excess methacrylic acid using sulfuric acid as a catalyst. A conversion of about 90 percent was obtained in two hours at l100-l200C. E. Hexadecylpoly(ethyleneoxy)39ethyl Methacrylate A mixture of 148 parts (0.058 mole) of hexadecylpoly(ethyleneoxy)39ethanol, 255 parts (2.98 moles) of methacrylic acid, 0.06 part of hydroquinone and 0.06 part oi Ionole and 3.6 parts concentrated H2 SO4 was heated at 1000-1120C for two hours yielding 403.5 parts of a solution containing 37.7 percent of vinyl surfactant ester (VSE-lE) and 62.3 percent of excess methacrylic acid. F. Methoxypropoxypoly(butyleneoxy)4(ethyleneoxy)10 ethyl Methacrylate The direct sulfuric acid catalyzed esterification process of Example 1A was used to prepare the above ester from the monomethyl ether of propylene glycol (Dowanol PM from The Dow Chemical Company) condensed with four moles of butylene oxide and then 20 moles of ethylene oxide using an alkaline catalyst. The neat vinyl surfactant ester (VSE-1F) can be used without further purification in the preparation of the liquid emulsion copolymer. Other mono C8-C20 alkyl glycol ether surfactants can be similarly esterified to provide vinyl surfactant esters with controlled hydrophilic-lipophilic balance. Example 2 - Liquid Emulsion Polymerization Process The following are typical procedures for the preparation of the liquid emulsion polymers. LEP-2A -- 48.0 MAA/42.0 EA/10.0 VSE-1A The polymerization is carried out in a stainless steel, jacketed reactor equipped with stirrer and feed pumps using the concurrent addition technology of Miller et al. U.S. 3,563,946 in which separate monomer mix and aqueous feed solutions are added concurrently to an initial aqueous reactor charge stirred at 90 rpm and preheated to a desired temperature. When the addition of monomer and aqueous initiator is completed, normally in about 2-4 hours, the emulsion is stirred an additional 1.5 hours to finish the polymerization. Then the reactor is cooled and the liquid emulsion polymer filtered through 100 and 200 mesh screens. A typical recipe and reaction conditions are: (1) Initial Reactor Charge* 374.0 parts Condensate water 0.0075 part Versenex# 80 chelant (40% solids) 2.0 parts Gafac# RE-610 anionic surfactant (2) Monomer Mix -- Feed Rate - 4 hours 48.0 parts Methacrylic acid ( > RA) 42.0 parts Ethyl acrylate (EA) 10.0 parts Vinyl surfactant ester (vSE-lA) 6.0 parts Igepal CO-530 nonionic surfactant (3) Aqueous Feed Mix. -- Feed Rate - 4 hours 69.8 parts Condensate water 0.0025 part Versenex 80 chelant (40%) 0.4 part Sodium hydroxide 2.0 parts DowfaxX 2A1 anionic surfactant (45% solids) 1.0 part Gafac PE-610 surfactant 0.5 part Sodium persulfate * Notes: : Quantities are in parts by weight based on 100 parts total monomer Versenexe 80 - sodium diethylenetriamine pentaacetic acid, 40% active solids from The Dow Chemical Company Grace RE-610 - a nonylphenoxypoly(ethylene oxy)phosphate ester in free acid form from GAF VSE-1A - neat vinyl surfactant ester of Example 1A (100to active basis) Igepal CO-530 - nonylphenoxypoly(ethylene oxy)5ethanol from GAF DowfaxC 2Al - sodium dodecyldiphenyl ether disulfonate from The Dow Chemical Company Conditions: Addition temperature - 70 C Agitation - 230 rpm Cookdown - 800C, 1.5 hours The resulting liquid emulsion polymer contained 20.1 weight percent solids at pH 3.5 and had a 1 percent aqueous solution viscosity in ammonium salt form at pH 9 of 400 cps (Brookfield Model LVT, &num;2 spindle, 12 rpm, 250C). LEP-2B -- 42.0 MAA+6.0 IA/42.0 EA/10.0 VSE-1A Using the same polymerization recipe and conditions, a liquid emulsion polymer was prepared in which 6 parts of itaconic acid was substituted for 6 parts of methacrylic acid. The resulting liquid product contained 19.9 weight percent solids at pH 3.5 and had a 1 percent aqueous solution Brookfield viscosity of 1090 cps in ammonium salt form. LEP-2C-1 -- 48.3 MAA/41.7 EA/10.0 VSE-1A In like manner a copolymer of 48.3 MAA/41.7 EA/10.0 VSE-1A was prepared which contained 20.0 weight percent solids and had a 1 percent aqueous solution Brookfield viscosity of 390 cps in ammonium salt form (cf Figure). LEP-2C-2, LEP-2C-3, LEP-2C-4 and LEP-2C-5 These liquid emulsion polymers differ from LEP-2C-1 in the proportion of components. The compositions are shown in Table I. LEP-2D-1 -- 42.0 K37.2 EA/20.8 VSE-1B Several runs were made in 2 liter'or 2 gallon reactors using the process of LEP-2E and the methacrylic ester of nonylphenoxypoly(ethyleneoxy)39ethanol (VSE-1B) and the above monomer mix. Very clean emulsion polymers were obtained after filtration, containing about 20 weight percent solids and having an average particle size of about 1100-1300 . LEP-2D-2, LEP-2D-3, LEP-2D-4 and LEP-2D-5 These liquid emulsion polymers differ from LrP-2D-1 in the proportion of components. The compositions are shown in Table I. LEP-2E -- 47.8 MAA/42.0 EA/10.2 VSE-1C A stirred glass reactor was charged with 271 parts of water, 2.0 parts of Conco Sulfate 219 (sodium salt of ethoxylated, sulfated lauryl alcohol from Continental Chemical Co.) and 0.1 part of Versenexe 80 (40 percent). The reactor charge was purged with nitrogen while stirring and was heated to 690C. A monomer mixture of 24.7 parts of methacrylic acid, 31.6 parts of ethyl acrylate, 19.0 parts of the product solution of Example 1-C containing 40.5 percent of vinyl surfactant ester-lD and 59.5 percent of methacrylic acid and 2.0 parts Conco Sulfate 219 was prepared in a dropping funnel. To the preheated aqueous reactor charge was added 0.13 part of potassium persulfate and about 7 parts of the monomer mixture. Then the remainder of me monomer mixture was added over about 3 hours while keeping a reaction temperature of 69 -70 C. After stirring an additional 2.2 hours at 700C, the liquid emulsion polymer was cooled and filtered. The product (341 parts) contained 21. percent solids and had a Brookfield viscosity of 9200 as a 1 percent aqueous solution in ammonium salt form. LEP-2F -- 42.2 MAA/37.2 EA/20.6 VSE-1D Using the general procedure of LEP-2A, a monomer mix of 2.2 parts of methacrylic acid, 37.2 parts of ethyl acrylate and 20.6 parts of octyloxypoly (ethyleneoxy)19ethyl methacrylate (VSE-1D) was copolymerized to give a stable emulsion copolymer containing 21.7 percent solids and having a 1 percent Brookfield LVT viscosity of 450 cps when neutralized with NH4OH. LEP-2G-1--46.8 MAA/41.4 EA/11.8 VSE-1E In a similar manner a monomer mix of 18.5 parts of methacrylic acid, 28.0 parts of ethyl acrylate, 21.G parts of the solution from Example l-E which contained 37.7 percent of hexadecyloxypoly(ethyleneoxy)39- ethyl methacrylate (VSE-1E) and 62.3 percent of meth acrvlic acid and 0.2 part of dodecyl mercaptan was copolymerized at 590-620C using 0.09 part potassium persulfate initiator to give a stable emulsion copolymer containing 20.5 percent solids and having a 1 percent Brookfield LVT viscosity of 450 cps when neutralized with NH4OH. LEP-2G-2 49.6 MAA/44.1 EA/6.3 VSE-1E This liquid emulsion polymer differs from LEP-2G-1 in the proportion of components. LEP-2H--48.3 MAA/41.7 EA/10.0 VSE-1F In another run a copolymer of 48.3 MAA/41.7 EA/10.0 VSE-1F was prepared from the methoxypropoxypoly (butyleneoxy)(ethyleneoxy)ethyl methacrylate of Example '-F. It contained about 20 weight percent Solids and had 1 percent aqueous solution Broolfleld viscosity of 288 cps in ammonium salt form. It was found that increasing the polymeriza- tion temperature fro 60 -80 C had little effect on product efficiency in paint. But, the thickening efficiency of these products decreased as the nonionic vinyl comonomer was changed from ethyl acrylate to butyl acrylate to 2-ethylhexyl acrylate and to methyl methacrylate. Thickening efficiency increased with increasing alkyl chain length from C8-C16 alkyl in the alkylphenoxy surfactant ester. Example 3 - Use as a Thickener for Latex Paint The utility of the new liquid emulsion polymers as a thickener for latex paint is illustrated by data obtained with several latex paint formulations and tests. Formulation 3A -- Interior Flat Latex Paint Ingredients* Lbs (Kg) Gallons (1) A. Water 300 (136) 36.06 (136.5) Pigment dispersant 12 (5.5) 1.31 (5.0) (25% TamolX 731) Defoamer (Drew L-475) 2 (0.90) 0.26 (1.0) Preservative (Dowicil 75) 1 (0.45) 0.08 (0.3) Surfactant (Triton# X-100) 5 (2.3) 0.56 (2.1) Aluminum silicate (ASP-400) 100 (45.5) 4.66 (17.6) CaCO3 (snowflake white) 125 (56.7) 5.54 (21.0) Titanium dioxide (Ti-Puree 250 (113.4) 7.79 (29.5) R-931) E. Ethylene glycol 25 (11.3) 3.00 (11.4) Glycol ether (Texanol) 10 (4.5) 1.26 (4.8) Everflex Es latex (55%) 250 (113.4 27.78 (105.1) C. LEP Thickener and water** 95.6 (43.4) 11.47 (43.4) 1175.6 (533.2) 99.77 (377.6) * Notes: Tamol# 731 - sodium salt of maleic anhydride/ diisobutylene copolymer from Rohm & Haas Drew 1-475 - liquid defoamer from Drew Chemical Corp., Parsippany, NJ 07054 Dowicil 75 - 1-(3-chloroallyl)-3,5,7 -triaza-l-azoniaadamantane chloride to which sodium bicarbonate has been added, from The Dow Chemical Co. Tritone X-100 - octylphenoxypoly ethoxyethanol from Rohm & Haas ASP-400 - Pigment grade aluminum silicate from Engelhard Minerals & Chem Corp., Iselin, NJ Snowflake White - Pigment grade calcium carbonate from Thompson, Weinmann & Co., Cartersville, GA 30120 Ti-Pures R-931 - TiO2 pigment from duPont Texanol-2,2,4-trimethylpentanediol-1,3 monoisobutyrate from Eastman Chemical Products, Inc., Kingsport, TN 37662 Everflex Ee latex - vinyl acetate-acrylic copolymer latex, sometimes called "vinyl -acrylic latex" or less commonly - "vinyl -acrylate latex" from W. R. Grace Co. **LEP Thickener - normally 1.0-6.0 lbs (100% solids basis)/100 gal (1.2-7.2 kg/m ) plus water to balance To prepare a stock paint base, the A ingredients are ground together at high speed for 20 minutes using a Cowles grinder. Then at reduced speed premixed ethylene glycol and glycol ether are added followed by the Everflex EX latex. The liquid emulsion polymer thickener (20 percent solids) and appropriate amount of water can be added immediately or later as desired for test purposes. Formulation 3B -- Interior Semigloss Latex Paint Ingredients* Lbs (kg) Gallons (1) A. Water 93 (42.1) 11.18 (42.3) Pigment dispersant 11 (5.0) 1.20 (4.5) (25% Tamole 731) Defoamer (Nopco# NDW) 2(0.9) 0.27(1.0) Propylene glycol 32 (14.5) 3.84 (14.5) Preservative (Dowicil# 75) 1.3 (0.6) 0.10 (0.4) Titanium dioxide (Ti-Pure 275 (124.6) 7.95 (30.0) R-900) Defoamer (Ncpco NDW) 4 (1.8) 0.53 (2.0) Surfactant (Triton GR7M) 2 (0.9) 0.23 (0.9) Surfactant (Dowfax# 2Aì 2 (0.9) 0.21 (0.8) Rholex# AC 490 (46%) 590 (267.3) 66.67 (252.3) Propylene glycol 32 (14.5) 3.84 (14.5) Phenmoxyethanol coalescing agent 10 (4.5) 1.09 (4.1) LEP Thickener and water 74.0 (33.5) 8.87 (33.6) 1128.3 (511.1) 105.98 (401.1) * Notes: Tamol# 731 - sodium salt of maleic anhydride/ diisobutylene copolymer from Rohm & Haas Nopco# NDW-nonionic liquid deformer from Diamond Shamrock Chemical Process Div. Dowicil# 75 - l-(3-chloroallyl)-3,5,7 -triaza-l-azoniaadamantane chloride to which sodium bicarbonate has been added, from The Dow Chemical Co. Ti-Pure# R-900 - TiO2 pigment from duPont Tritone GR7M - dioctyl sodium sulfo succinate from Rohm & Haas DowfaxS 2A1 - sodium dodecyldiphenyl ether disulfonate from The Dow Chemical Co. Rhoplex# AC 490 - acrylic emulsion latex from Rohm & Haas **LEP Thickener - normally about 1.0-6.0 lbs (100% solids basis)/100 gal (1.2-7.2 kg/m plus water to balance To prepare a stock paint base, the A ingredients are ground together at high speed for 20 minutes using a Cowles grinder. Then at reduced speed the B ingredients including premixed propylene glycol and phenoxyethanol are added. The emulsion polymer thickener (20 percent solids) and the balance of the water can be added immedi- ately or later as desired for test purposes. Procedures A. Thickener Audition - The liquid emulsion polymers can be incorpoeated in latex paints in ways: 1. Addition of the emulsion polymer to the final paint as liquid dispersion with subsequent neutralization with aqueous NH4OH (26 percent) to a pH > 7. 2. Presolubilization of the dispersion by dilute it with water and then adding sufficient alkali (NH4OH or NaOH) with agitation. Once a clear solution has been obtained this can be post added to the final paint. 3. Addition of the thickener to the pigment grin after the pigment has been dispersed and then the addition of sufficIent alkali (NH4OH or NaOH) to solubilize the thickener. It is recommended that the pigment grind be as dilute as possible prior to solubil at n the thickener dispersion. For experimental purposes, addition of the liquid emulsion polymer to a stock base paint followed by pH adjustment as necessary is particularly convenient (Method 1). B. Evaluation - Properties of paint thickened with the liquid emulsion polymers are evaluated using standard procedures recommended by ASTM Committee D-1 Subcommittee D-42 and paint companies for determining such properties as paint viscosity, stability, flow and leveling, brushability, spatter, hiding power, color compatibility and gloss. For research purposes, the following tests for the paint viscosity, flow and leveling are particularly useful: 1. Stormer Viscosity - (ASTM Method D 562-55). The paint viscosity is measured with a Stormer Viscosimeter 24 hours after preparation. A viscosity of about 85-105 Kreb Unit (KU) is desired for most commercial latex paints. Accelerated stability tests often use Stormer viscosity measurements at 250C of samples held at 1200F (490C) for 2-4 weeks. 2. Leneta Leveling Test - (The Leneta Co., HoHo-Kus, NJ 07423). A paint sample is drawn down using a Leneta leveling test blade and the dried paint film compared visually with eleven Leneta levelness standards numbered 0-10 with 10 being perfect leveling. 3. Leneta Anti-Sag Test - (The Leneta Co., Ho-Ho-Kus, NJ 07423). A presheared sample of paint is drawn down with the Leneta anti-sag meter on Leneta drawdown chart form 7B positioned horizontally on a flat glass or metal plate. The chart is then immediately placed in a vertical position with the paint stripes horizontal and left edge (thinnest stripe) at the top, and allowed to dry. Each stripe, ranging in wet film thickness from 3 to 12 mils, is considered as having the same rating number as the notch by which it has been applied. The highest number (thickest) stripe that does not touch the one below itself is referred to as the index stripe, and its number is the Anti-Sag index of the paint. The practical interpretation of ratings is empirical and strongly subjective. Optimum sag resistance depends on the type of coating, but in general, an index of 8 through 12 is considered good to excellent. 4. Scrub Resistance - ASTM Method D-286-66T. This test is normally run without the shim and provides an accelerated measure of wall paints to scrub erosion. 5. Color Acceptance - A test paint is prepared by mixing 0.5 g of color tint with 24.5 g of formulated paint and drawn down on a primed-unprimed chart (Leneta lB) using a 7 mil gap clearance blade. A 2-3 cm diameter circular area overlapping the primed-unprimed chart surface is rubbed with a finger until decided resistance is felt. The film is dried and rated as: (1) acceptableno visual difference in rubbed area; (2) pigment flocculation-rubbed area lighter in color or (3) colorant flocculation-rubbed area darker in color. 6. Gloss - ASTM Method D-523-67 is used to measure the Gardner 600 gloss of paint test panels. A gloss rating of 30-65 is generally desirable for interior semigloss latex paints. C. Table I Table I presents typical test results for an interior flat latex paint and an interior semigloss latex paint prepared as described for Formulations 3A and 3B using the representative liquid emulsion polymers described in Example 2. Test results such as shown in Table I demonstrate the utility of the water-based liquid emulsion polymers described herein as a pH responsive thickener for aqueous compositions. By appropriate adjustment of monomer ratios, polymerization conditions and final product formulations, the liquid emulsion polymers can be tailored to give optimum thickening for many applications including particularly those containing natural, synthetic and artificial latexes. TABLE I -LIQUID POLYMER IN LATEX PAINT Emulsion Polymer Comonomers, Wt % (1)* (2)* Evaluation (3)* Paint Lep Visc LEP (A) R COOH (B) Co- (C) VSE % Solids 1% Visc Base Wt KU LL LAS 2A 48.0 MAA 42.0 EA 10.0 1A 20.1 400 3A 4.5(5.4) 101 7 12 3B 2.75(3.3) 85 5 12 2B 42.0 MAA 42.0 EA 10.0 1A 19.9 1090 3A 3.0(3.6) 86 7 F3 +6.2 IA 3B 2.5(3.0) 79 5 12 2C-1 48.3 MAA 41.7 EA 10.0 1A 19.8 390 3A 4.5(5.4) 99 5 12 3B 2.5(3.0) 82 5 12 2C-2 48.3 MAA 31.7 EA 20.0 1A 19.8 310 3A 4.5(5.4) 94 6 12 3B 2.5(3.0) 79 5 12 2C-3 38.3 MAA 51.7 EA 10.0 1A 20.1 870 3A 4.5(5.4) 96 5 12 3B 2.5(3.0) 81 5 12 2C-4 38.3 MAA 41.7 EA 20.0 1A 19.8 220 3A 4.5(5.4) 83 7 10 3B 2.5(3.0) 78 5 12 2C-5 31.2 MAA 45.0 EA 10.0 1A 21.9 7300 3A 5.0(6.0) 101 6 12 +13.8 3B 2.75(3.3) 106 5 12 2D-1 42.0 MAA 37.2 EA 20.8 1B 21.6 1100 3A 5.0(6.0) 70 - - 3B 3.5(4.2) 119 - -2D-2 42.1 MAA 18.6 EA 20.8 1B 21.8 800 3A 5.0(6.0) 94 8 9 +18.6 S 3B - - - -2D-3 42.0 MAA 37.2 EA 20.8 1B 21.5 600 3A 5.0(6.0) < 61 - - 3B 3.5(4.2) 83 - -- TABLE I -(Cont.) Emulsion Polymer Comonomers, Wt % (1)* (2)* Evaluation (3)* Paint Lep Visc LEP (A) R COOH (B) Co- (C) VSE % Solids 1% Visc Base Wt KU LL LAS 2D-4 42.2 MAA 32.6 EA 6.6 1B 19.8 400 3A - - - - +18.6 VAc 3B 5.0(6.0) 106 3 12 2D-5 18.7 MAA 55.1 EA 11.5 1B 20.1 18400 3A - - - - +15.0 HEA (5%) 3B - - - -2E 47.8 MAA 42.0 EA 10.2 1C 21.4 9200 3A 3.5(4.2) 110 5 12 3B 2.0(2.4) 106 3 12 2F 42.2 MAA 37.2 EA 20.6 1D 21.7 450 3A 5.0(6.0) 77 - - 3B 5.0(6.0) 98 3 12 2G-1 46.8 MAA 41.4 EA 11.8 1E 20.5 21000 3A 5.0(6.0) 130 4 12 3B 2.5(3.0) 128 4 12 2G-2 49.6 MAA 44.1 EA 6.3 1E 19.0 325 3A 5.0(6.0) 98 9 10 3B 3.0(3.6) 112 5 12 2H 48.3 MAA 41.7 EA 10.0 1F 20.0 288 3A 4.5(5.4) 102 3 12 3B 2.5(3.0) 93 4 12 Notes*: (1) Comonomers, wt% based on total monomers (a) MAA-methacrylic acid IA-itaconic AA-acrylic acid (b) EA-ethyl acrylate S-styrene HEA-2-hydroxyethyl acrylate VAc-vinyl acetate TABLE I (Cont.) (c) Vinyl surfactant ester from 1A nonylphenoxypoly(ethyleneoxy)9ethanol 1B nonylphenoxypoly(ethyleneoxy)39ethanol 1C dodecylphenoxypoly(ethyleneoxy)10ethanol 1D octyloxypoly(ethyleneoxy)39ethanol 1F methoxypropoxypoly(butyleneoxy)4(ethyleneoxy)19ethanol (2) Liquid emulsion polymer 1 percent Brookfield Model LVT viscosity, pH 9, #2 spindle at 12 rpm, 25 C (3) Evaluation in latex paint base Formulation 3A-interior vinyl acrylic flat latex paint Formulation 3B-interior acrylate semigloss latex paint LEP, wt lbs LET thickener [100% solids basis]/100 gallons (kg/m ) Viscosity 24 hr Stormer viscosity, KU LL Leneta Leveling 0-10 LAS Leneta Anti-Sag 0-12 D. Table II Table II presents typical test results comparing two liquid emulsion polymer thickeners with three commercial cellulose ether thickeners commonly used in latex paints. The effective thickening observed even with a lower viscosity LEP product suggests association of the LEP thickener with other components of the paint formulation as well as hydration by water. TABLE I I - COMPARISON OF THICKENERS Paint Thickener Haake Visc. Test Thickener 1 Visc. Base wt Visc. KU 3D-1 LEP-2A 400 3A 4.5 (5.4) 3.65 101 3E 2.75 (3.3) 0.9 85 3D-2 LEP-2E 9200 3A 3.5 (4.2) - 110 3B 2.0 (2.4) - 106 3D-3 HEC 1100-1450 3A 5.0 (6.0) - 96 3B 3.25 (3.9) - 94 3D-4 HEMC 800-1050 3A 5.25 (6.3) - 88 3B 3.5 (4.2) - 91 3D-5 MC-J 1000-1500 3A 4.5 (5.4) 1.75 95 3B 2.5 (3.0) 1.3 80 Notes*: LEP-2A: 48.0 MAA/42.0 EA/10.0 VSE-1A LEP-2E: 47.8 MAA/42.0 EA/10.2 VSE-1C HEC: Hydroxyethyl cellulose QP 15,000 (.Union Carbide Corp) HEMC: Hydroxyethyl methylcellulose XD-7603.03 (The Dow Chemical Co.) MC-J: Hydroxypiopyl methylcellulose Methocel J20MS (The Dow Chemical Co.) Paint Base: Formulation 3A or 3B Thickenr, wt: Lbs [100% solids]/100 gal (kg/m ) -1 Haake visc.: Viscosity(poise) at 10,000 sec Visc. KU: 24 hr Stormer viscosity E. To illustrate a more detailed evaluation of a liquid emulsion polymer as a thickener for a latex paint1 Table III presents typical data for the liquid emulsion polymer described in Example 2A (48.0 MAA/42.0 EA/10.0 VSE-lA; 20.1 percent solids, 1 percent viscosity of 305 cps at pH 9.0) used as a thickener in two paint formulations. For comparison, similar data for a commercial cellulose ether thickener is also given. Note that the liquid emulsion polymer is more efficient as a thickener, provides improved flow and leveling with markedly reduced spattering and yet retains many of the desirable properties of the cellulose ether thickener. Further rheological study of the liquid emulsion polymers suggests a controlled interaction or association of the LEP with the latex and pigment particles as a significant factor in the improved film build (one coat hiding) and reduced spray and spattering from roller application. TABLE III - LATEX PAINT PERFORMANCE Paint Type Vinyl-Acrylic Flat Acrylic Semigloss* Thickner LEP-2A MC-J LEP-2A MC-J Loading [lbs/100 gal](kg/m ) 4.5 (5.4) 4.5 (5.4) 2.5 (3.0) 2.5 (3.0) Stromer Visc. (24 hr KU) 101 95 84 80 Leneta Leveling 7/10 4/10 5/10 4/10 Leneta Anti-Sag 11/12 9/12 12/12 12/12 Gardner 60 Gloss - - 43 43 Scrub (cycles) 4631 6581 1075ê 1081 Color Acceptance4 OK OK OK Poor Stromer Visc. (4 wks, 120 F; KU) 103-107 95 81 94-92 Paint pH 9.4 8.5 9.2 9.1 Spattering Minimal Excessive Minimal Excessive Notes*: Vinyl-Acrylic Interior Flat Latex -- Formulation 3A Acrylic Semigloss Latex -- Formulation 3B MC-J -- Methocel J20MS (The Dow Chemical Company) (1) Avg. of 4 tests (2) Avg. of 2 tests (3) One test (4) Color acceptance: Borden Aquablak G; Tenneco Thalo Blue, Thalo Green and Medium Yellow - Rubbed up. Example 5 - LEP Thickeners in Other Aqueous Systems The wide utility of the liquid emulsion polymers as thickeners for aqueous compositions including inorganic solutions and slurries is indicated by data such as the following: A. Varying amounts of several inorganic salts were added to 1 percent aqueous solutions of LEP-2A (pH 9) and the Brookfield viscosity of the resulting solutions determined. Typical results are shown in Table IV. TABLE IV - VISCOSITY, CPS AT 250C, pH 9 Salt Conc: 0% 0.25% 0.50% 0.75% 1.00% NaCl 300 1090 1200 1125 850 Na2 SO4 300 780 910 920 905 MgCl2 300 > 2500 470 Floc B. To a slurry of 48.8 g of titanium dioxide (Ti-Puree R-931 from duPont) and 50.2 g water having a 1 percent Brookfield viscosity of about 100 cps was added 51.0 g of a 2 percent aqueous solution of LEP-2A having a pH of about 9 and a 1 percent Brookfield viscosity of 300 cps. The resulting thickened slurry had a 1 percent Brookfield viscosity of 4200 cps. C. The effect of LEP-2A as a thickener for several unformulated vinyl-acrylic paint latexes was determined using several commercial latexes blended with a 2 percent aqueous solution of LEP-2A neutralized to pH 9 with NH40H. The blended aqueous compositions were adjusted to 21 percent total solids and Brookfield viscosities were determined with results shown in Table V. TABLE V - BROOKFIELD VISCOSITY* Latex* Initial 2% LEP-2A Everflex E 10 cps 170 cps Airflexs 500 7.5 cps 600 cps UcarX 366 10 cps 290 cps * Everflexe E - Vinylacrylic copolymer (55% solids; W. R. Grace & Co.) Airflexe 500 - Vinyl acetate-ethylene latex (55% solids; Air Products & Chemicals) Ucar# 366 - Vinyl acetate-acrylic copolymer latex, sometimes called "vinyl-acrylic latex" (55% solids; Union Carbide Corp.) Brookfield Viscosity &num;2 Spindle, 12 rpm, 250C, pH 9.0

Claims: 1. A liquid emulsion polymer useful as a pH responsive thickener for aqueous compositions comprising an aqueous emulsion copolymer of: A. 15-60 weight percent based on total monomers of at least one C3-C8 a, -ethylenically unsaturated carboxylic acid monomer of the formula: EMI43.1 where R is H and R' is H, C1-C4 alkyl, or -CH2COOX; R is -COOX and R' is H or -CH2COOX; or, R is CH3 and R' is H; and X is H or C1-C4 alkyl; B. 15-80 weight percent of at least one nonionic, copolymerizable C2-C12 a,P-ethylenically unsaturated monomer of the formula: CH2 = CYZ (Il) where Y is H and Z is -COOR, -C6H4R', CN, C1, EMI43.2 Y is CH3 and Z is -COOR, -C H R', CN or -CH = CH2; or Y and Z are Cl; and R is C1-C8 alkyl or C2-C8 hydroxyalkyl; R' is H, Cl, Br, or C1-C4 alkyl; and R" is C1-C8 alkyl; and C. 1-30 weight percent based on total monomers of at least one nonionic vinyl surfactant ester of the formula: EMI44.1 where R is z or CH3, each R' is C1-C2 alkyl, R" is C8-C20 alkyl or C8-C16 alkylphenyl, n is an average number from 6-100 and m is an average number from 0-50 provided that n > m and #(n#m) is 6-100; said polymer being stable as an aqueous colloidal dispersian at a pH lower than about 5.0 but becoming an effective thickener for aqueous systems upon adjustment to a pH of 5.5-10.5 or higher. 2. The polymer of Claim 1 where the carboxylic acid monomer (A) is methacrylic acid, acrylic acid, or a mixture thereof with fumaric or itaconic acid. 3. The polymer of Claim 1 where the comonomer (B) is a monovinyl ester or a mixture thereof with styrene, 2-hydroxyethyl acrylate, acrylonitrile, vinyl chloride or vinyl acetate. 4. The polymer of Claim 1 where the vinyl surfactant ester is selected from the group consisting of: 1) alkylphenoxypoly(ethyleneoxy)ethyl acrylates of the formula: EMI45.1 where R is H or CH3; Y' is C8-C16 alkyl, and n is 6-100; 2) alkoxypoly(ethyleneoxy)ethyl acrylates of the formula: EMI45.2 where R is H or CH3, R" is C8-C20 alkyl, and n is 6-50; and 3) alkoxypoly(alkyleneoxy)ethyl acrylates of the formula: EMI45.3 where R is H or CH3, each R' is C1-C2 alkyl, R" is C8 -C20 alkyl, and n is 6-50 and m is 1-40. 5. The polymer of Claim 1 consisting essentially of: A. 35-55 weight percent of methacrylic acid, acrylic acid or mixtures thereof with fumaric or itaconic acid; B. 35-50 weight percent of ethyl acrylate or mixtures thereof with styrene, 2-hydroxyethyl acrylate, acrylonitrile, vinyl chloride or vinyl acetate; and C. 2-20 weight percent of a vinyl surfactant ester of Formula III. 6. The polymer of Claim 1 consisting essentially of: A. 40-50 weight percent of methacrylic acid; B. 35-50 weight percent of ethyl acrylate; and C. 2-12 weight percent of the methacrylic esther of a nonylphenoxypoly(ethyleneoxy)n ethanol where n is 6-40. 7. The polymer of Claim 6 containing 40- < 5 weight percent of methacrylic acid and 2-10 weight percent of itaconic acid and having an average particle size of 500-3000 and a Brookfield viscosity of 50-50,000 cps as a 1 percent aqueous solution in ammonium salt form at p9 9.0 and 25OC. 8. A liquid aqueous colloidal dispersion useful as a pH responsive polymeric thickener for aqueous compositions containing 10-50 weight percent of the emulsion polymer of Claims 1 to 7 and having a pH of about 2.5-5.0. 9. A process for making the liquid aqueous colloidal dispersion of Claim 8 comprising emulsion copolymerizing the monomeric mixture at a pH of about 2.5-5.0 in the presence of a free-radical producing inItiator at a temperature between 609-900C. 10. A thickened aqueous composition having a pH within the range of about 6.5-11.0 comprising an aqueous composition containing a water-soluble or dispersible material and an effective amount of the emulsion polymer of Claims 1 to 7. 11. The thickened aqueous composition of Claim 10 wherein the emulsion polymer consists essentially of: A. 40-50 weight percent of methacrylic acid; B. 35-50 weight percent of ethyl acrylate; ana C. 2-.12 weight percent of the methacrylic ester of an alkylphenoxypoly(ethylenoxy)ethyl acrylate of the formula: EMI47.1 where R is E or CH3; y is C8-C16 alkyl; and n is 6-100. 12. A process for making a thickened aqueous composition which comprises: (1) blending with the aqueous composition a sufficient amount of the emulsion copolymer of Claims 1 to 7 to thicken the aqueous composition and (2) adjusting the pH of said blend within a range of about 6.5-11.0 as necessary to dissolve the emulsion polymer therein and thus thicken the aqueous composition.

Inventors: SONNABEND, LAWRENCE FAYE
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1979
Main classification: C08F220
IPC codes: C08F290, C08F220, C08F246, C09D7, C07C69