SULFUR- AND NITROGEN-CONTAINING HYDROCARBON FEED CONVERSION AND CATALYST THEREFOR

Abstract: Hydrocarbon feeds containing sulfur and nitrogen con­ taminants are converted with a catalyst comprising synthetic crystalline zeolite ZSM-20 combined with a hydrogenation function, in particular palladium. Particular interesting appli­ cations are polymerisation, aromatisation, hydrocracking and catalytic cracking. Catalyst composition comprising ZSM-20 in association with palladium.

Description: SULFUR- AND NITROGEN-CONTAINTNG HYDROCARBON FEED CONVERSION END CATALYST THEREFOR This invention reiates to catalytic conversion of hydrocarbon feeds containing sulfur and nitrogen containing organic compounds, and to a catalyst therefor. Zeolitic materials, both natural and synthetic, have been demonstrated in the past to have catalytic proerties for various types of hydrocarbon conversions. Certain zeolitic materials are ordered, porous crystalline alumlnosilicates having a definite crystalline structure within which there are a large number of smaller cavities which may be interconnected by a number of channels. These cavities and channeis are uniform in size. Since the dimensions of these pores are such as to accept for absorption molecules of certain dimensions while rejecting those of larger dimensions, these materials have come to be known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic include a wide variety of positive ion-containing crystalline aluminosilicates. These aluminosilicates can be described as a rigid three-dimensional framework of Si04 and A104 in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total aluminum and silicon atoms to oxygen is 1:2. The electrovalence of the tetrahedra containing aluminum is balanced by the inclusion in the crystal of a cation, for example, an alkali met 21 or & . alkaline earth metal cation. This can be expressed wherein the ratio of aluminum to the number of various cations, such as Ca/2, Sr/2, Na, K or Li is equal to unity. One type of cation may be exchanged either entirely or partially by another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given aluminosilicate by suitable selection of the cation. The spaces between the tetrahedra are occupied by molecules of water prior to dehydration. Prior art techniques have resulted in the formation of a great variety of synthetic aluminosilicates. These aluminosilicates have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U.S. Patent 2,882,243), zeolite X (U.S. Patent 2,882,244), zeolite Y (U.S. Patent 3,130,007), zeolite ZK-5 (U.S. Patent 3,247,195), zeolite ZK-4 (U.S. Patent 3,314,752), zeolite ZSM-5 (U.S. Patent 3,702,886), zeolite ZSM-11 (U.S. Patent 3,832,449), zeolite ZSM-12 (U.S. Patent 3,832,449), and zeolite ZSM-20 (U.S. Patent 3,972,983) merely to name a few. A crystalline aluminosilicate zeolite well known in the art is faujasite. The ZSM-20 zeolite for use in the present invention resembles fauj asite- in certain aspects of structure, but has a notably higher silica/alumina ratio than faujasite. The present invention relates to the use of a hydrogenation function containing synthetic crystalline zeolite ZSM-20, or the thermally treated products thereof, for sulfur- and nitrogen-containing organic compound, e.g. hydrocarbon compound, conversion. The catalyst may be prepared by incorporating a platinum group metal (e.g. Pd) into ZSM-20. FJhen a hydrogenation component such as palladium is incorporated into the crystalline molecular sieve zeolite ZSM-20, a catalyst is produced which has the ability to 1) hydrogenate aromatic hydrocarbons at low pressure in the presence of sulfur and nitrogen poisons 2) convert sulfur and nitrogen containing poisons to H2° and NH3 and saturated hydrocarbons 3) hydrocrack hydrocarbon mixtures containing sulfur and nitrogen poisons to lower molecular weight mixtures while substantially improving the quality of the material remaining in the original boiling range of the hydrocarbon mixture. It is known that palladium and other Group VIII metals deposited on amorphous supports are unable to hydrogenate aromatic hydrocarbons at low pressure in the presence of sulfur and nitrogen poisons. In addition it is known (air. Agafonov et al, Khimiya i Tekhnologiya Topliv i Easel, No. 6 pp. 12-14, June, 1976) that Pd deposited on NaX, NaY, Na mordenite, KNaL, and KNa Erionite are also essentially in active for the above mentioned conversion. We have also shown that the same applies to Pd/HZSM-12 and Rh H B. Catalysts containing ZSM-20 are active and stable in hydrocracking at pressures of 3447.38 10342.14 kPa(500-1500psi) and 287.77 - 371.110C (500-7000F) whereas it is not uncommon for such hydrocracking processes to operate at 13785.52 20684.28 kPa(2000-3000 psi) and 343.33 -426.660C (650-8000F). The original cations of the as synthesized ZSM-20 for use herein can be replaced in accordance with techniques well known in the art, at least in part, by ion exchange with other cations. Preferred replacing cations include metal ions ammonium ions, hydrogen ions and mixtures thereof. Particularly preferred cations are those which render the zeolite catalytically-active, especially for hydrocarbon conversion. These include hydrogen, hydrogen precursors (e.g. ammonium ions), rare earth metals, aluminum, metals of Groups IB, IIB, IIIB, IVB, VIB, IlA, IIIA, IVA and VIII of the Periodic'Table of Elements. The zeolites for use herein may be formed in a wide variety of particle sizes. Generally speaking, the particles can be in the form of a powder, a granule, or a molded product, such as extrudate having a particle size sufficient to pass through a 2 mesh (Tyler) screen and be retained on a 400 mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion, the aluminosilicate can be extruded before drying or dried or partially dried and then extruded. As in the case of many catalysts, it may be desired to incorporate the zeolite with another material resistant to the temperatures and other conditions employed in organic compound conversion processes. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides, such as alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the zeolite, i.e. combined therewith, which is active, tends to improve the conversion and/or selectivity of the catalyst in certain organic conversion processes. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate of reaction. Frequently, zeolite materials have been incorporated into naturally occurring clays, e.g. bentonite and kaolin. These materials, i.e, clays, oxides, etc., function, in part, as binders for the catalyst. It is desirable to provide a catalyst having good crush strength, because in a petroleum refinery the catalyst is often subjected to rough handling, which tends to break the catalyst down into powder-like materials which cause problems in processing. Naturally occurring clays which can be composited azith the synthetic zeolite catalysts include the montmorillonite and kaolin family, which families include the sub-bentonites, and the kaolins commonly known as Dixie, ?lcNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinlte dickite, nacrite or anaite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or cher2icai modification. In addition to the foregoing materials, the present catalyst can be composited with a porous matrix material such as silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary compositions such as silica-alum.ina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. A mixture of these components could also be used. The relative proportions of finely divided crystalline zeolite, e.g. ZSM-20, and inorganic oxide gel matrix vary widely with the crystalline aluminosilicate content ranging from about 1 to about 90 percent by weight and more usually in the range of about 2 to about 70 percent by weight of the composite. In general, organic compounds may be catalytically converted in the presence of the present zeolite catalyst material, including the product of thermal treatment thereof, over a range of catalytic conversion conditions, including a reaction temperature of from about 37.770C (1000F) to about 648.880C (12000F) preferably from about 204.44 kPa (4000F) to about 537.770C(10000F) a reaction pressure of from atmospheric to about 69048.91 kPa(10,000 psig), preferably from about atmospheric to about 24232.98 kPa (3,500 psig) and a hydrogen/organic compound ratio of from 0 to about 20,000 scf/bbl, preferably from 0 to about 10,000 scf/bbl. When the conversion is conducted in a flow apparatus, e.g. a down-flow reactor, or under conditions comparable to those existing in a flow apparatus, the liquid hourly space velocity (LHSV) should be maintained at between about 0.1 hr-l and about 10 hr-1. When the conversion is conducted in a batch apparatus, e.g. a stirred batch reactor, or under conditions comparable to those existing in a batch apparatus, the contact time should be maintained at between about 0.01 hour and about 48 hours, preferably between about 0.1 hour and about 24 hours. In particular, when the conversion of organic compound by the present method is olefin polymerization, catalyst conversion conditions should be maintained within certain critical ranges, including a temperature of from about 37.770C (lOQ F) to about 426.660C (800oF) preferably from about 204.440C (4000F) to about 315.550C (6000F), a pressure of from about atmospheric to about 27680.36 kPa (4,000 psig), preferably from about atmospheric to about 13890.84 kPa (2,000 psig), a LHSV (when a flow operation) of from about 0.1 hr-l to about 50 hr-1, preferably from about 1 hr¯5 to about 10 hr-1, and a contact time (when a batch operation) of from about 0.1 hour to about 48 hours, preferably from about ¯¯0.5 hour to about 24 hours and a hydrogen/hydrocarbon (i.e. olefin) ratio of from about 50 scf/bbl to about 10,000 scf/bbl, preferably from about 500 scf/bbl to about 5,000 scf/bbl. When the conversion is olefin or paraffin aromatization, catalyst conversion conditions should be maintained within critical ranges, including a temperature of from about 315.550C (6000F) to about 648.88oC (12000F), preferably from about 426.660C (8000F) to about 537.77oC (10000F), a pressure of from about 446.07 kPa (50 psig) to about 69048.91 kPa (10,000 psig), preferably from about 790.8 kPa (100 psig) to about 6996.09 kPa (1,000 psig), a LKSV (when a flow operation) of from about 0.1 hr-1 to about 10 hr-1, preferably from about 1 hr-1 to about 5 hr-1, a contact time (when a batch operation) of from about 0.1 hour to about 48 hours, preferably from about 1 hour to about 24 hours and a hydrogen/hydrocarbon (i.e. olefin or paraffin) ratio of from about 50 scf/bbl to about 10,000 scf/bbl, preferably from about 100 scf/bbl to about 1 ,000 scf/bbl. Further, when the conversion of organic compound bv the present method is cracking, catalytic conversion conditions should be maintained within certain critical ranges, including a temperature of from about 371.110C (700 F) to about 648.880C (12000F) preferably from about 426.660C (8000F) to about 537.770C (10000F) a pressure of from about atmospheric to about 1480.2E kPa (200 psig), a LHSV (when a flow operation) of from about 0.5 hr-1 to about 50 hr-1, preferably from about 1 hr-1 to about 10 hr-1, and a contact time (when a batch operation) of from about 0.01 hour to about 24 hours, preferably from about 0.1 hour to about 10 hours. When the conversion is hydrocracking, catalyst conversion conditions should be maintained within somewhat different ranges, including a temperature of from about 204.440C (4000F) to about 537.770C (10000F) preferably from about 2600C (5000F) to about 454.44oC (8500F) a pressure of from about 3548.7 kPa (500 psig) to about 24232.98 kPa (3500 psig), a LHSV (when a flow operation) of from about 0.1 hr-1, to about 10 hr-1, preferably from about 0.2 hr-1 to about 5 hr-1, a contact time (when a batch operation) of from about 0.1 hour to about 10 hours, preferably from about 0.2 hour to about 5 hours and a hydrogen/hydrocarbon ratio of from about 1000 scf/bbl to about 20,000 scf/bbl, preferably from about 3,000 scf/bbl to about 10,000 scf/bbl. In order to more fully illustrate the nature of the invention and the manner of practicing same, the following non-limiting examples are presented. EXAMPLE 1 A mixture of 193.7 gm Tetraethylorthosilicate 7.9 gm Sodium Aluminate 291 ml 2.8N Tetraethylammonium hydroxide and 72 gm Water which gives the following mole ratios Si02/A1203 = 30 H2O/SiO2 = 15 OH/SiO2 = 0.90 Na/SiO2 = 0.09 and TEA/SiO2 = 0.88 was aged for 3 days at 250C in a 300 ml polypropylene bottle and then crystallized for an additional 18 days at 100 C under static conditions to give crystalline ZSM-2Q in 90% purity with a Si02/A1203 mole ratio of 8.66. EXAMPLE 2 5% Pd/Mg/ZSM-20 The TEA, Na ZSM-20 was exchanged with 1 molar MgC12 at reflux overnight, washed until free of C1-, and air dried at 120 C. The magnesium exchanged ZSM-20 was then reslurried in distilled H20, an aqueous solution of Pd(NH4)4C12 was added dropwise, stirred overnight at 400C, washed free of C1-, air dried at 1400C, and then air calcined at 5000C for four hours. Elemental analysis of the calcined catalyst showed that Pd exchange was quantitative. A product was obtained having the oxide composition: 5% Pd/Mg/ZSM-20 wt 5 meq/gm PdO 6.2 1.0 MgO 3.3 1.6 3.24 Na20 1.98 0.64 Si02 74.00 A1203 14.50 2.84 Si02/A1203 = 8.66 EXAMPLE 3 5% Pd/Mg/Dealuminized Y 500.3 gm (2068 meq Al) of Na Y (SiO2/A1203=4.9) was slurried in 1300 ml deionized H20. 233.07 gm (692 meq) Na2 EDTA was added and the slurry heated to reflux while stirring. 262 ml 5N HC1 (1310 meq H+) was added to the refluxing stirred slurry at a rate of 3.4 ml/hr so as to remove 31.7% of the framework aluminum and give a Si02/A1203 ratio of 7.1. Elemental analysis of the dealuminized material gave a Si02/A1203 ratio of 6.8 and Na/Al ratio of 0.96 indicating the presence of some non-framework aluminum. The dealuminized sample was found to be 86% crystalline when compared to the original Na Y starting material. 50 gm of the dealuminized Na Ywas exchanged 3 times (4, 22, 4 hours) with 300 ml 1N MgC12 at reflux, given an intermediate calcination at 5000C and given one additional exchange treatment for 4 hours using the same procedure. Elemental analysis showed that 73% of the Na had been exchanged by Mg. 15 gm of the Mg exchanged-dealuminized Y was then serried in 100 ml deionized H20 and a 50 ml aqueous solution containing 0.75 gm Pd as Pd(NH3)4++ was added dropwise and stirred for 20 hours &commat; 600C. The Pd exchanged material was washed until free of C1-, dried at 1200C and calclned at 500 C for 4 hours . The calcined catalyst contained 5.2% Pd, was tan in color, and showed no evidence of metallic Pd by X-ray. * Milliequivalents of ionic species per gram of dehydrated catalyst. A product was obtained having the oxide composition: 5% Pd/Mg/Dealuminized Y wt % nieq*/gm PdO 5.9 0.98 3.25 1.62 3.52 Na2O 2.84 0.92 SiO2 71.1 A1203 16.9 3.34 Si02/A1203 = 7.15 EXAMPLES 4-6 Tetralin containing 700 ppm S as benzothiophene was converted over the above catalysts and Ht-500E, a commercially available hydrotreating catalyst which was used as a control in this work. The results obtained are summarized below. Example 4 Example 5 Example 6 Ht-500E Catalyst Pd/Mg/ZSM-20 Pd/Mg/Daly NiMo/Al2O3 T C 237.77(460 F)248.88(480 F) 260(500 F 315.55(600 F) LHSV 1.0 1.0 1.0 1.0 Pressure 3447.38kPa(500psia)3447.38kPa(500psia) 3447.38kPa(500psia) 3447.38kPa(500psia) Tetralin Conv. 94 100 100 11 Decalin Select. 80 55 79 70 C10 Select > 95 > 95 > 95 100 From the above data it is obvious that the ZSM-20 based catalyst is more active than the catalyst based on dealuminized Y (the best known catalyst of prior art) and is much more active than the commercial NiMo/A1203 catalyst. EXAMPLES 7-9 Identical experiments were performed except that 500 ppm N as quinoline was added to the sulfur-containing feed with the following esults Example 7 Example 8 Example 9 Ht-500 Catalyst Pd/Mg/ZSM-20 Pd/Mg/Da1Y NiMo/Al2O3 T C 329.44(625 F) 329.44(625 F) 332.22(630 F) LHSV 1 1 1 Pressure 5171.07kPa(750*psia) 3447.38kPa(500psia) 3447.38kPa(500psia) Tetralin Conv. 75 30 13 Decalin Select. 68 86 61 C10 Select. 99 < 95 100 Again the ZSM-20 catalyst was the most active. *Increasing pressure from 3447.38kPa(500 psi) to 5171 .07kPa (750 psi) has a significant activating effect. EXAMPLES 10-12 As further examples, a 246.11 -385 C (475-7250F) Arab Light gas oil containing 1.09% S, 60 ppm N and 13.32% H, was reacted over the three catalysts at 1.0 LHSV, 5171.07kPa (750 psi), and 6000 scflbbl H2 with the following results: Example 12 Ht-500 Catalyst Pd/Mg/2SM-20 Pd/Mg/Dally NiMo/Al2O3 Time on Stream (Hrs.) 450 210 215 T C 315.55(600 F) 335(635 F) 342.22(648 F) 420+ Conversion 29.7 31.7 > 1 %H in C5+ Prod. 14.39) 14.31 14.30 13.85 14.23) %S in C5+ Prod. .002 .12 .07 In this case the zeolite catalysts were able to produce products containing much more hydrogen than those produced over the NiMo/A1203 catalyst. Again, the ZSM-20 based catalyst was more active than that based on dealuminized Y.

Claims: CLAIMS: 1. A process for effecting catalytic conversion of a sulrut- and nitrogen-containing organic compound charge while comprises contacting said charge under catalytic conversion conditions with a catalyst comprising a hydrogenation function-containing synthetic crystalline zeolite ZSM-20 2. A process according to Claim 1 wherein said hydrogenation function comprises a Group VIII metal present in an amount between 0.1 and 10.0 wt.%. 3. A A pro C±S according to Claim 2 wherein said Group VIII metal is palladium. 4. A process according to any preceding claim wherein said zeolite has its original cations replaced, at least in part by non exchanges with one or more cations selectee for hydrogen and hydrogen precursors, rare earth metals, aluminum, ano metals from Groups IIA, IIIA, IVA, IB, IIB, IIIB, IVB, and VIII of the Periodic Table of Elements. 5e E process according to any preceding claim wherein said catalytic conversion is conducted in a flow apparatus and said conversion conditions include a temperature of 37.77 C (100 F) to 648.880C (12000F), a pressure of atmospheric to 69048.91kPa (10,000 psig), a hydrogen/organic compound ratio of 0 to 20,000 scf/bbl and a liquid hourly space velocity of 0.1 to hr-1 to 50 hr-1. 6. A process according to any of claims 1 to 4 wherein said catalytic conversion is conducted in a batch apparatus and said conversion conditions include a temperature of 37.77 C (100 F) to 648.88 C (1200 F) a pressure of atmospheric to 69048.9kPa (10j000 psig), a hydrogen/organic compound ratio of O to 20,000 scf/bbl and a contact tire of 0.01 hour to 48 hours. 7. A process according to Claim 5 wherein said conversion is olefin polymerization and said conversion conditions include a temperature of 37.770C (1000F) to 426.660C (8000F), a pressure of atmospheric to 27680.36kPa (4,000 psig) a hydrogen/hydrocarbon ratio of 50 scf/bbl to 10,000 sef/bbl and a space velocity of 0.1 hr-1 to 50 hr-1 8. A process according to Claim 6 wherein said conversion is olefin polymerization and said conversion conditions include a temperature of (1000F) to 426.660C (8000F) a pressure of atmospheric to 27680.36kPa (4000 psig), a hydrogen/hydroca-rbon-ratio of 50 scf/bbl to 10,000 scf./bbl and a contact time of O.J hour to 48 hours. 9. A process according to Claim 5 wherein said conversion is aromatization and said conversion conditions include a temperature of 315.550C (600 F) to 648.880C (12000F), a pressure of 446.07 kPa(50 psig) to 69048.91kPa (10,000 psig), a hydrogen/hydrocarbon ratio of 50 scf/bbl to 10,000 scf/bbl and a liquid hourly space velocity of 0.1 hr-1 to 10 hr -1 10. A process according to Claim 6 wherein said conversion is aromatization and said conversion conditions include a temperature of 315.550C (6000F) to 648.880C (12000F), a pressure of 446.07kPa(50 psig) to 69048.91kPa (10;000 psig) a hydrogen/hydrocarbon ratio of 50 scf/bbl to 10,000 scf/bbl and a contact time of 0.1 hour to 48 hours. 11. A process according to Claim 5 wherein said conversion is cracking and said conversion conditions include a temperature of 371.11 C (7000F) to 648.880C (1200 F), a pressure of atmospheric to 1480.28kPa (200 psig) and a liquid hourly space velocity of 0.5 hr-1 to 50 hr-1. 12. A process according to Claim 6 wherein said conversion is cracking and said conversion conditions include a temperature of 371.110C (7000F) to 648.880C (12000F), a pressure of atmospheric to 1480.28 kPa(200 psig) and a contact time of 0.01 hour to 24 hours. 13. A process according to Claim 5 wherein said conversion is hydrocracking and said conversion conditions include a temperature of 204.440C (4000F) to 537.770C (1000oF), a pressure of 3548.7kPa (500 psig) to 24232.98 kPa (3500 psig), a hydrogen/hydrocarbon ratio of 2000 scf/bbl and a liquid hourly space velocity of 0.1 hr-1 to 10 hr-1. 14. A process according to Claim 6 wherein said conversion is hydrocracking and said conversion conditions include a temperature of 204.440C (4000F) to 537.770C (10000F), a pressure of 3548.7kPa(500 psig) to 24232.98 kPa (3500 psig), a hydrogen/hydrocarbon ratio of 4000 scf/bbl to 20,000 scf/bbl and a contact time of 0.1 hour to 10 hours. 15. A catalyst composition comprising zeolite ZSM-20 in association with palladium. - 16. A composition according to claim 15 whereof palladium constitutes between 0.1 and 10% wt. 17. A composition according to claim 15 or claim 16 wherein the ZSM-20 contains magnesium cations.

Inventors: GORRING, ROBERT LEE, LA PIERRE, RENE BERNARD
Applicants: MOBIL OIL CORPORATION
Application year: 1979
Main classification: B01J29
IPC codes: C10G35, C07C67, C07C1, C10G11, C10G49, C07B61, C07C15, C07C2, B01J29, C10G47