POLYAMIDE RESINS AND PROCESS FOR PREPARING THE SAME

Abstract: Melt compounded polyamide resins blends of a nylon resin and a small amount of an adduct which contains a requisite amount of anhydride functionality. The adduct polymer is found to provide nucleating effects to the resul­ tant blend.

Description: POLYAMIDE RESINS AND PROCESS FOR PREPARING THE SAME Nucleating agents are usually employed as processing aids primarily to accelerate crystallization from a melt. Acceleration of crystallization results in faster molding cycles, which of course means greater productivity in molding operations. Generally, nucleatina agents are believed to provide sites for crystallization of molten polyamide. However, nucleating agents are also identified bv their ability to increase tensile strength and stiffness of the polyamide, dear2 se elongation, and decrease mold shrinkage The term "nucleating agent" as employed herein, is meant to denote those additives which increase tensile strength and decrease tensile elongation and mold shrinkage. A deficiency of many nucleating agents is' that they also significantly lower the Izod impact strength of the resin compared with that of the polyamide without nucleating agent. In contrast, the nucleating agents employed herein provide nucleating properties to polyamides but do not result in a significant lowering of Izod impact strength. SUMMARY OF THE INVENTION The product of this inventicn is a melt compounded blend consisting essentially of a) a polyamide resin having a molecular weight of at least 5000, and b) an adduct of maleic or fumaric anhydride and a copolymer of ethylene, at least one C3 to C6 a-olefin, and at least one nonconjugated diene, said adduct having an anhydride functionality of between about 0.1 and 4.0 milliequivalents of carboxyl groups per 1 gram of adduct, said adduct being present in the blend in an amount such that the anhydride functionality comprises between about 0.9 and 10 equivalents per 106 g of polyamide present; provided that the maximum amount of adduct present is less than 1 percent based on weight of polyamide and adduct. The process of this invention is a process for preparing the melt compounded blend described above by mixing the polyamide resin and the adduct and melt extruding the mixture. DESCRIPTION OF THE INVENTION The polyamide resins used in the blends of this invention are well known in the art and embrace those resins having a molecular weight of at least 5000 and commonly referred to as nylons. Suitable polyamides include those described in U.S. Patents 2,071,250; 2,071,251; 2,130,523; 2,130,948; 2,241,322; 2,312,966; 2,512,606; and 3,393,210. Preferably, the polyamides are those made by the condensation of linear diamines represented by the fornla H2N-(CH2)x-N32, where x is a integer between 6 and 1X, with linear diarboxlic acids represented by the formula I02C-(CH2)y¯CO2Ht where y is an integer between 2 and 8. Equally well, these polyamides may be m.aze from amine-formlng derivatives of said amines and acids such as esters, acid chlorides, amine salts, etc. Representative dicarboxylic acids used to make the polyamides include adipic acid, pimelic acid, suberic acid, sebacic acid, and dodecanedioic acid, while representative diamines include hexamethylene diamine and octamethylene diamine. Examples of polyamides include polyhexamethylene adipamide (66 nylon), polyhexamethylene azelamide (59 nylon), polyhexamethylene sebacamide (610 nylon), and polyhexamethylene dodecanoamide (612 nylon), polycaprolactam, (nylon 6), polylauryl lactam, poly-ll-amino-undecanoamide, bis-(paraaminocyclohexyl) methane dodecanoamide. It is also possible to use polyamides prepared by the copolymerization of two of the above polymers or terpolymerization of the above polymers or their components, as for example, a polymer made of adipic acid, and isophthalic acid and hexamethylene diamine. Preferably the polyamides are linear with a melting point in excess of 2000C. Also included in the blends of this invention are copolymers, such as a copolymer of nylon 6,6, and polylactams, e.g., nylon 6 (polycaprolactam); and blends of polyamides, such as a mixture of nylon 6,G and nylon 6. Preferably the condensation polyamide employed herein is polyhexamethylene adipamide (nylon 6,6). By the term "anhydride functionality" is meant the group EMI3.1 The concentration of anhydride in the adduct is measured by infrared spectroscopy of hot pressed films. The amount of the adduct present to achieve the nucleation effect in the blend depends on the amount of anhydride functionality present in the adduct, provided the amount of polymer present is less than 1%. The amount of anhydride functionality present in the adduct is preferably between about 0.1 and 7 and most preferably between about 0.1 and 2 milliequivalents per gram. Preferably also the amount of adduct present in the blend is between about 0.9 and 7 equivalents of carboxyl groups per 106g of polyamide polymer. It is believed, although not conclusively demonstrated, that the anhydride function of the adduct polymer reacts with amine ends of the polyamide to provide the nucleating effect seen in the blends. The adduct may be prepared as described in Flexman U.S. 4,026,067 or Caywood U.S. 3,884,882 and U.S. 4,010,223. It preferably has an inherent viscosity of at least one as measured on O.lg of adduct in 100 ml of perchloroethylene at 300C. Propylene is preferably the C3-C6 a-olefin, although it can be l-butene, l-pentene or l-hexene. The nonconjugated dienes include linear aliphatic dienes of at least six carbon atoms which have one terminal double bond and one internal double bond, and cyclic dienes wherein one or both of the carbon-to-carbon double bonds are part of a carbocyclic ring. Of the linear dienes, copolymers of ethylene, propylene, and 1,4-hexadiene are especially preferred. Class of cyclic dienes useful for adduct formation includes alkylidene bicycloalkenes, alkenyl bicycloalkenes, bicycloalkadienes, and alkenyl cycloalkenes. Representative of alkylidene bicycloalkenes are 5-alkylidene-2-norbornenes such as 5-ethylidene-2-norbornene and 5-methylene2-norbornene. Representative of alkenyl bicycloalkenes are 5-alkenyl-2-norbornenes such as 5- (1' -propenyl) -2-norbornene, 5-(2'-butenyl)-2-norbornene, and 5-hexenyl-2-norbornene. Dicyclopendadiene and 5-ethyl-2,5-norbornadiene are illustrative of bicycloalkadienes, and vinyl cyclohexene is representative of alkenyl cycloalkenes which may be selected as the diene monomer. Another class of copolymers include branched tetrapolymers made from ethylene, at least one C3 to C6 a-monoolefin with propylene being preferred, at least one nonconjugated diene, defined above, and at least one nonconjugated diene such as 2,5-norbornadiene or 1,7-octadiene. The adducts used in this invention can be prepared by any process which intimately mixes maleic or fumaric anhydride with the copolymer without appreciable generation of free radicals, and which concurrently or subsequently heats the mixture to a temperature at which thermal addition occurs. Selected temperatures will generally be at least 2250C to obtain adduct formation at acceptable rates and less than about 3500C to avoid any significant polymer breakdown. Preferred temperature ranges will vary with the particular polymer and can readily be determined by one skilled in the art. Mixing of the anhydride and copolymer can be by blending molten anhydride with copolymer in an internal mixer or extruder, or by blending finely divided dry maleic anhydride with copolymer on a well-ventilated rubber mill with concurrent or subsequent heating, such as in a hot press or mold. Temperatures necessary to achieve thermal grafting are sufficiently high to dehydrate the diacid, forming the anhydride in situ. Thus, diacid can be compounded with the copolymer instead of the anhydride when such is desired. Preferred copolymers of ethylene, propylene, and 1,4-hexadiene are very resistant to free radical formation under high shear stress conditions and are readily mixed on conventional bulk processing equipment without gel formation. Care must be exercised, however, in selecting the mixing conditions for copolymers derived from strained ring dienes such as ethylidene norbornene. Such copolymers will readily generate free radicals when sheared at low temperatures, and are preferably mixed with the anhydride at high temperature, such as above 90"C. to avoid appreciable gel formation. It is generally desired to form adducts containing about 0.5 to 9 percent, and preferably about 1 to 4 percent, by weight anhydrie. Unreacted anhydride is conveniently removed from the adduct by extraction with water. To prepare the melt compounded blends of this invention, the polyamide and the adduct are simply mixed by any usual means and melt extruded through any usual polyamide extruder. This procedure is referred to herein as "melt compounding". If the adduct is in finely ground form it can be mixed directly with the polyamideq If, however, it is in coarse or pellet form, it is preferable to first mix and extrude it with the polyamide in amounts of about 10-20 percent to form a concentrate, and then mix and extrude the concentrate with additional polyamide. Werner Pfleiderer twin screw, Brabender, Banbury mill or the like are common useful extruders that can be employed to melt compound the blends of this invention. Ordinarily, the ingredients are dry blended and then extruded at a temperature above the melting point of the polyamide. The blends of this invention may contain one or more conventional additives such as stabi lizers and inhibitors of oxidative, thermal, and ultraviolet light degradation; lubricants and mold release agents, colorants including dyes and pigments, fibrous and particulate fillers and re inforcements, plasticizers, and the like. These additives are commonly added during the mixing step. Representative oxidative and thermal stabilizers which may be present in blends of the present invention include Group I metal halides, e.g., sodium, potassium, lithium with cuprous halides, e.g., chloride, bromide, iodide; hindered phenols, hydroquinones, and varieties of substituted members of those groups and combinations thereof. Representative ultraviolet light stabi lizers, include various substituted resorcinols, salicylates, benzotriazoles, benzophenones, and the like. Representative lubricants and mold release agents include stearic acid, stearyl alcohol, and stearamides. Representative organic dyes include nigrosine, while representative pigments, include titanium dioxide, cadmium sulfide, cadmium selenide, phthalocyanines, ultramarine blue, carbon black, and the like. Representative fillers include carbon fibers, glass fibers, amorphous silica, asbestos, calcium silicate, aluminum silicate, magnesium carbonate, kaolin, chalk, powdered quartz, mica, feldspar, and the like. EXAMPLES In the Examples which follow, the concentration of anhydride functionality in the adduct was measured by pressing it to form a film. The film is then subjected to infrared wavelengths in an infrared spectrometer and the maxima of anhydride is compared to a standard to determine the anhydrive functonality. Tensile strength and elongation measurements were made by ASTM D638 on 1/8-inch thick specimens pulled at 2 inches per minute, and IzQd impact strength was determined by ASTM D256 on 1/8-inch thick specimens, except that specimens were used dry as molded. Mold shrinkage was determined by measuring the length cf five 1/8-inch thick tensile test bars and subtracting the average from the length of the mold cavity. The difference is divided by the length of the cavity to give mold shrinkage in dimensionless units of in/in. The following adducts were employed: Adduct Polymer 1A A polymer of fumaric acid grafted onto a terpolymer of ethylene and propylene and 1,4hexadiene prepared as described in Example 4 of U.S. 4,026,967 was employed. The graft polymer was analyzed for an anhydride functionality was 0.42 meq/g acid. Adduct Polymer 1B Another sample of polymer was prepared as described for Polymer 1A. The anhydride function alloy was 0.71 meq/g acid. In the Examples and controls, the appropriate adduct was mixed with nylon pellets or powder by tumbling in a polyethylene bag. The mixture was extruded at 2700C. in a 28mm Werner and Pfleiderer twin screw extruder. Test on resins were fun dry as molded. Adducts 1A and 1B were obtained in pellet -!rmZ and to ensure good mixing, a two-step mixing cdure was employed. A 10 per cent by weight mixture of adduct in the nylon was first obtained by tumbling and extrusion. Then this 10 per cent mixture was diluted with more nylon and tumbled and extruded again to obtain blends of desired adduct concentration. The blends prepared were molded by injection molding. A melt temperature of 2850C., a mold temperature of 90"C., and an injection melt pressure of 10700 psi were employed at a cycle time of 50 seconds. EXAMPLE 1 Properties of Nylon 66 Containing Adduct Polymer 1A (EPHDE-g-F) Adduct Izod Mold Concentration Tensile Elonga- Impact Shrink Wt Acid Strength tion Strength age Eq/l06 psi % Ft lb/in in/in Nonel 12,200 72 1 .017 .252 1.1 12,600 46 1.1 .015 52 2.1 12,800 36 1.1 .013 52,3 2 1 13,000 28 1.1 .013 None1 12,200 50 .9 .006 .5 2.1 12,400 34 1.1 .013 1. Nylon 66 control (Zytelo 101) 2. These also contained .3 percent N-stearyl erucamide lubricant for mold release. 3. This also contains .7 percent Nigrosine - a black dye. As seen from the table, the adduct increased tensile strength and Izod Impact strength and decreased elongation and mold shrinkage. (The mold shrinkage of .006 for the second nylon 66 control is considered to be an anomalous result). EXAMPLE 2 Properties of Nylon 66 Containing Adduct Polymer 1B (EPHDE-g-F) Adduct Izod Mold Concentration Tensile Elonga- Impact Shrink Wt Acid Strength tion Strength age % Eq/106g psi % Ft lb/in in/in None1 12,000 65 1.0 .017 .3 2.1 12,800 31 1.0 .015 .9 6.3 12,900 26 1.1 .013 1. Nylon 66 control (Zytel# 101) As seen from the table, the same results are generally obtained as with Example 1. CROSS REFERENCE TO RELATED APPLICATION This application is a continuation-in-part of application serial number 945,323 filed September 25, 1978. FIELD OF THE INVENTION This invention is directed to polyamide resins containing certain additives which provide nu- cleating characteristics to the resins.

Claims: CLAIMS The embodiments of the invention in which an exclusive property or privilege is claimed are as follows: 1. Melt compounded polyamide resins blends consisting essentially of a) a polyamide resin having a molecular weight of at least 5000, and b) an adduct of maleic or fumaric anhydride and a copolymer of ethylene, at least one C3 to C6 a-olefin, and at least one nonconjugated diene, said adduct having an anhydride functionality of between about 0.1 and 4.0 milliequivalents of carboxyl groups per 1 gram of adduct, said adduct being present in the blend in an amount such that the anhydride functionality comprises between about 0.9 and 10 equivalents per 106 g of polyamide present; provided that the maximum amount of adduct present is less than 1 percent based on weight of polyamide and adduct. 2. The blend of Claim 1 wherein the anhydride functionality in the adduct is between about 0.1 and 2 milliequivalents per gram and the adduct is present in an amount such that the amount of carboxyl groups available for anhydride functionality comprises between about 0.9 and 7 equivalents of carboxyl groups per 106 g of polyamide present, provided the maximum amount of adduct present is less than 1 percent based on weight of polyamide and adduct. 3. The blend of Claim 2 wherein copolymer of the adduct is a copolymer of ethylene, propylene, and at least one linear aliphatic diene of at least 6 carbon atoms. 4. The blend of Claim 3 wherein the diene is 1,4-hexadiene. 5. The blend of Claims 3 or 4 wherein the adduct is derived from maleic acid. 6. The blend of Claims 3 or 4 wherein the adduct is derived from fumaric acid. 7. Process for preparing the blend of Claim 1 wherein components a) and b) of Claim 1 are physically mixed and then melt extruded.

Inventors: RICHARDSON, PAUL NOEL
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1979
Main classification: C08L77
IPC codes: C08L77