METHOD AND APPARATUS FOR THE MANUFACTURE OF OBJECTS FROM THERMOPLASTIC STRUCTURAL FOAM

Abstract: Method and apparatus for the manufacture of objects from thermoplastic structural foam. In order to reduce the retention time required for cool­ ing of a foamed injection-moulded object inside the mould, the latter is provided with means to produce a locally in­ creased cooling effect in the mould. Such means are, for instance, cooling fingers (10). The purpose of these cooling fingers is the rapid formation of bridges which consist of solidified material (12) and connect two opposite solidified walls (11 and 11a) of the object. These bridges permit of removing the object from the mould earlier, because the object is sooner capable of resisting the internal pressure of the foaming agent. The method and the invention are mainly meant for the manufacture of thick flat or curved plate-shaped objects, such as walls and furniture. Materials which can be used are, for instance polyethylene, polypropylene, polystyrene, polycarbonate, polyamides and thermoplastic polyesters, as well as copolymers and mixtures thereof.

Description: METHOD AND APPARATUS FOR THE MANUFACTURE OF OBJECTS FROM THERMOPLASTIC STRUCTURAL FoAM The invention relates to a method and apparatus for the manufacture of objects from thermoplastic structural foambyinjection of a foamable thermoplastic synthetic substance into a cooled mould. Objects consisting of thermoplastic structural foam have a foamed core and a compact skin, with a gradual transition in material density from the core towards the surface. The injection moulding of objects from structural foam according to a known method is as follows. After addition of a blowing agent, the thermoplastic material is plasticized in an extruder and homogenized, after which it is rapidly injected into a mould by means of an injection cylinder and plunger. Up to the moment of entering the mould, the material is kept under a pressure which is higher than the foaming pressure of the blowing agent at the operating temperature in order to prevent premature foaming. The volume of the unfoamed material injected is normally smaller than the volume of the mould. As the pressure in the mould is lower than the foaming pressure of the blowing agent, the material injected will expand so that the mould is filled up completely. A large part of the volatile blowing agent escapes from the material which is at the boundary surface during the filling. The material practically free of blowing agent is then pushed against the cooled wall of the mould, where its temperature declines so far that plasticity is lost and a compact skin is formed. The object can be removed from the mould as soon as it has cooled to the point where the skin can resist the internal pressure of the blowing agent, and the heat in the core can no longer soften the skin. The cooling time of the mould takes up a relatively large part of the total time required for an injection-moulding cycle. The drawbacks of this are that the injection-moulding machine cannot be utilized optimally and that the material must be retained in the injection-moulding machine fOr a long time.These long retention times at the usual high operating temperatures are harmful to the heat-sensitive material and impair the quality of the objects to be produced. To obviate these drawbacks, a system with several moulds to each injection-moulding machine is sometimes used. This system is expensive owing to the costs of purchase and maintenance of the moulds and the appurtenant device for transport of the moulds. Another system to obviate the drawbacks mentioned involves a method of cooling which is partially effected outside the mould. with this method, the object is removed from the mould when the skin of the object is already capable of resisting the internal pressure of the blowing agent, but the heat in the core is still high enough to soften the skin of the object. To prevent softening of the skin and the resultant deformation, the object is immersed in a cooling bath immediately upon removal from the mould. This cooling bath takes over the cooling function of the mould, which becomes thus available again for a following cycle. Although this system permits of time saving with respect to the cooling time in the mould, the time involved in the formation of a skin capable of resisting the internal blowing pressure is relatively long, particularly in the case of higher wall thicknesses. Moreover, the cooling bath device involves additional costs of purchase and maintenance. The aim of the invention is to provide a method and apparatus for the manufacture of objects from thermoplastic structural foam by injection of a foamable thermoplastic synthetic substance into a cooled mould, with obviation or suppression of the above-mentioned drawbacks and with a possibility for combination with existing methods. According to the invention, this aim has been achieved in that the cooling of the object is controlled in such a manner that, prior to complete solidification of the core material, in one or more places, bridges are formed which consist of solidified material and connect two opposite solidified skin areas of the object, and in that the object is removed from the mould at the moment that the bridges, together with the solidified skin, are capable of resisting the internal pressure of the blowing agent. If necessary, continued cooling outside the mould can take place immediately after release of the object. The apparatus according to the invention comprises an injectionmoulding machine and a mould which is provided with means for producing a locally increased cooling effect. Preferably, at least one of two opposite walls of the mould is provided with cooling fingers, which are not in contact with other parts of the mould when this is in closed position. If both opposite walls of the mould are provided with cooling fingers, either these fingers pass along each other when the mould is closed, or they are in line two by two. In another design, the locally increased cooling effect is obtained in that the number of cooling channels locally in the mould wall is increased, or in that some cooling channels are connected to a source which supplies a colder cooling medium. Combination of both features is also possible. Since the method and the apparatus according to the invention permit of making bridges of solid material between opposite solid surface areas anywhere in an object which for the rest is still in a plastic condition, the moment at which the internal foam pressure is no longer able to deform the object is reached sooner than without formation of bridges. The object can thus be taken out of the mould earlier, so that a considerable time saving is reached in the overall injection-moulding cycle. It has been found that during the cooling process the object is alternately in contact with the mould wall or clear of it. An explanation for this phenomenon is that thermal shrinking causes the object to get clear of the wall and is consequently cooled at a lower rate, so that the internal heat plasticizes the previously solidified skin and the internal foam pressure makes the object expand until it is in contact with the mould wall again. This process may recur a few times until the object has lost so much of its internal heat that the residual heat is insufficient to plasticize the solidified skin. A suitable moment for removing the object from the mould is when the object gets clear of the wall for the first time and the counter-pressure in the mould is consequently low. This moment can be found by means of a pressure measurement, but it can also be determined empirically and included in the programme of the injection-moulding cycle. Thermoplastics which are processed into objects of structural foam according to the method described above are, for instance, polyethylene, polypropylene, polystyrene, polycarbonate, polyamides and thermoplastic polyesters, as well as copolymers and mixtures thereof. The action of the foaming agent may be brought about by a physical as well as a chemical process. The foaming agent may be added to the material before plasticizing, but also during the plasticizing and homogenizing. The process according to the invention is notably suitable for the manufacture of thick plates or sheets, either flat or curved, used for construction of walls and furniture. The invention will now be elucidated with reference to an embodiment represented in the drawing. Fig. 1 is a diagrammatic representation of an injectionmoulding unit; Fig. 2 is a cross-section of a mould according to the invention; Fig. 3 is a cross-section of an object manufactured according to the invention. Fig. 1 shows an extruder 1 with a feed hopper 2, an injectionmoulding cylinder 3 with plunger 4, a mould 5 consisting of two halves 6 and 7, and a valve 8 for the feed channel 9. A cross-section of the mould 5 on an enlarged scale is shown in figure 2, which also shows how the cooling fingers 10 can be arranged. In the left-hand section A and in the right-hand section C of the figure, both mould halves 6 and 7 have cooling fingers 10, which pass along each other in section A and are in line in section C. The middle section, B, shows a mould of which only one of the two opposite mould walls has cooling fingers. As shown by figure 2, the cooling fingers 10 are not in contact with other parts of the closed mould, some distance remaining between the cooling fingers and the opposite mould half or between opposite cooling fingers. The cooling fingers may be provided with cooling channels. The thermoplastic material, to which blowing agent has been added, is fed into the extruder 1 from the feed hopper 2 and subjected to Åa plasticizing and homogenizing treatment. By means of the injection-moulding cylinder 4 and the plunger 3, a certain quantity of the material is then rapidly injected into the mould 5, where it expands and fills the mould cavity. Because the mould is provided with cooling fingers, a solidified skin 11 is formed not only against the mould walls after a short time, but also along the cooling fingers 10, so that bridge-like solidified material sections 12 are formed, which connect the opposite skin areas 11 and lia (fig. 3). After a very short time these bridge-like sections connect the opposite skin areas so that the whole is capable of resisting the internal pressure prevailing in the object. Example Some test series were carried out with a mould according to the invention. One series (A) was carried out with a mould of which one half had been provided with cooling fingers placed at the points of intersection of a square network, the length of the square sides being 71 mm, and another series (B) with the same mould, the difference being that the square side was 37 mm. With the mould in closed position, the perpendicular distance between the inside walls was 10 mm; the cooling fingers, 8.5 mm in length, were round in section, with a diameter tapering from 16 mm at the wall to 15 mm at the detached end. The internal length and width of the mould were 500 x 300 mm. The material injected was high-density polyethylene, containing a quantity of blowing agent calculated to give the injection-moulded 3 object a final density of 590 kg/m The mouldings were removed from the mould after 50 seconds with intervals of 10 seconds. After half an hour, the final thickness of the mouldings was measured. The results have been plotted in a graph (see fig. 4), in which curve A and curve B represent the results of the test series A and B, respectively, while curve C represents the results of a comparative test series with the same mould, not provided with cooling fingers. The significance of the method according to the invention appears clearly from a comparison of curves B and C. In B, measurable thickness increase of the object already stops after a cooling time of 50 seconds, while in C this is the case only after 150 seconds. A reduction of the cooling cycle duration by more than 100 seconds is of essential significance in seeking optimum utilization of injection-moulding equipment.

Claims: CLAIMS 1. Method for the manufacture of objects from thermoplastic structural foam by injection of a foamable thermoplastic synthetic substance into a cooled mould, this method being characterized in that the cooling is controlled in such a manner that, prior to complete solidification of the core material, in one or more places bridges are formed which consist of solidified material and connect two opposite solidified skin areas of the object, and in that the object is removed from the mould at the moment that the bridges, together with the solidified skin, are capable of resisting the internal pressure of the blowing agent. 2. Method according to claim 1, characterized in that the moment at which the object is removed from the mould is determined by means of a pressure measurement. 3. Method according to claim 1, characterized in that the object is subjected to continued cooling in a cooling bath immediately after release from the mould. 4. Apparatus for carrying out the method according to claim 1, consisting of an injection-moulding machine and a mould provided with cooling channels, characterized in that the mould design incorporates means for producing a locally increased cooling effect. 5. Apparatus according to claim 4, characterized in that the means for producing a locally increased cooling effect consist of cooling fingers on at least one of two opposite mould walls, which cooling fingers are not in contact with other parts of the mould when this is in closed position. 6. Apparatus according to claims 4 and 5, characterized in that, with the mould in closed position, each cooling finger on the one mould wall is in line with a cooling finger on the opposite wall. 7. Apparatus according to claims 4 and 5, characterized in that, with the mould in closed position, the cooling fingers of two opposite moulds pass along each other. 8. Apparatus according to claim 4, characterized in that the locally increased cooling effect is obtained by locally increasing the number of cooling channels. 9. Apparatus according to claim 4, characterized in that the locally increased cooling effect is obtained by incorporating channels which can be connected to a source supplying a cooling medium with a temperature lower than that in the other channels. 10. Object manufactured by means of the method according to claims 1, 2 and 3.

Inventors: KERSEMAKERS JOSEF JOHANNES FRANCISCUS MARIA, LEYEN, JOANNES JACOBUS PETRUS
Applicants: STAMICARBON B.V.
Application year: 1979
Main classification: B29D27
IPC codes: B29C44, B29C33