POLYMER COMPOSITIONS CONTAINING HYDRATED BASIC MAGNESIUM CALCIUM CARBONATES AS SMOKE-DEPRESSANT ADDITIVES

Abstract: Hydrated basic magnesium calcium carbonates are used as smoke-depressant additives for polymer compositions, in particular for plasticized vinyl chloride polymer compositions.

Description: POLYMER COMPOSITIONS CONTAINING HYDRATED BASIC MAGNESIUM CALCIUM CARBONATES AS SMOKE-DEPRESSANT ADDITIVES This invention relates to polymer compositions having a smoke-depressant component incorporated therein. In British Patent Specification 1 432,860 there are disclosed plasticized halogen-containing polymer compositions in which the plasticizer comprises a phosphate ester, and which contain certain metal compounds as 11reactive modifiers". The effect of the reactive modifier is to reduce smoke and flame generation, should the polymer composition ignite, compared with similar polymer compositions containing equivalent amounts of other metal compounds5 e.g. those such as calcium carbonate conventionally used as fillers, which are not reactive modifiers. A preferred reactive modifier according to Specification 1,432,860 is magnesium carbonate, and, as indicated above, calcium compounds are not considered to be reactive modifiers. We have now found that certain double carbonates of magnesium and calcium are very effective in reducing smoke emission from burning polymer compositions, and give results comparable with those obtained with magnesium carbonate while being considerably less expensive A polymer composition of the invention comprises a blend of an organic polymer and a hydrated basic magnesium calcium carbonate. A typical hydrated basic magnesium calcium carbonate has the empirical formula 2 MgCO3. Mg (OH)2. 3H2O 3CaC03 The exact molecular structures of the hydrated basic magnesium calcium carbonates are not known, but the proportions of the various elements require that they contain hydroxyl as well as carbonate anions iOeO they are basic carbonates, and also that they contain combined water. The hydrated basic magnesium calcium carbonates are commercially available, being usually referred to as "light precipitated magnesium calcium (or calcium magnesium) carbonate", Although dolomite is a double magnesium calcium carbonate, it is not a hydrated basic magnesium calcium carbonate and does not show the smoke-reduci properties of the latter. For use in the compositions of the present invention the particle size of the hydrated basic magnesium calcium carbonates should normally be of the same order as that of conventional solid fillers used in polymer compositions. Preferably all particles are less than 75 microns and at least 9OQG of the particles are less than 50 microns0 The hydrated basic magnesium calcium carbonates are especially effective as smoke depressants for halogencontaining polymers containing plasticizers, especially phosphate ester plasticizers, but these carbonates can also be used in halogen-containing polymers with other plasticizers or, with or without plasticizers, in other polymers, for example synthetic and natural rubbers Halogen-containing polymers which benefit from blending with hydrated basic magnesium calcium carbonates in accordance with the invention include polyvinyl chloride and copolymers of vinyl chloride with one or more other ethylenically unsaturated compounds copolymerisable therewith, preferably in an amount of not more than 40 molars percent relative to the vinyl chloride. Suitable copolymers are those wherein the comonomer is selected from other vinyl halides such as vinyl bromide and vinyl fluoride; vinyl esters such as vinyl acetate, vinyl chloroacetate and vinyl butyrate; vinyl alkyl sulfonates; vinyl ethers such as vinyl ethyl ether, vinyl isopropyl ether and vinyl chloroethyl ether; aromatic and cyclic unsaturated compounds such as styrene, the mono- and polychloro- styrenes, coumarone, indene, vinyl naphthalene, vinyl pyridine, vinyl pyrrole; acrylic acid and its derivatives such as ethyl acrylate, methyl methacrylate, ethyl methacrylate, ethyl chloroacrylate, acrylonitrile and methacrylonitrile; vinylidene compounds such as vinylidene chloride, vinylidene bromide; unsaturated hydrocarbons such as ethylene, propylene and isobutenes; allylic compounds such as allyl acetate, allyl chloride and allyl ethyl ether; conjugated ethylenically unsaturated compounds such as butadiene, isoprene, chloroprene, 2,3-dimethylbutadiene and piperylene; and esters such as diethyl maleate and diethyl fumarate. Specific example of vinyl chloride copolymers which may be employed in the compositions of the present invention include vinyl chloride/vinyl acetate, ethylene/ vinyl chloride/vinyl acetate, and ethylene/vinyl chloride/ acrylonitrile copolymers Similarly, other halogen-containing polymers contemplated herein include polymers of halogenated olefines, e g chlorinated poiyethylene and chlorinated polypropylene, polymers of halogenated diolefins, eOgf chloroprene, and chlorosulfonated polyolefins, e.g. chlorosulfonated polyethylene, as well as polyblends of such halogen-containing polymers with non-halogenated resins. Plasticizers that can be used in the compositions of the invention where the polymer is such that it would normally be formulated with a plasticizer, eOg. vinyl chloride polymers, include phthalates, for example dialkyl phthalates, and alkyl benzyl phthalates, sebacates and adipates. Preferred plasticizers are however phosphate esters, since such esters themselves have smoke-depressant properties, and mixtures of phosphate esters with other plasticizers. Phosphate esters which can be used include trialkyl phosphates, dialkylaryl phosphates, alkyldiaryl phosphates and triaryl phosphates. The preferred phosphate esters are the trialkyl phosphates, dialkylaryl phosphates and alkyldiaryl phosphates. Examples of trialkyl phosphates which can be used include tributyl phosphate, trihexyl phosphate, tricyclohexyl phosphate, trioctyl phosphate, tridecyl phosphate, triundecyl phosphate, tri dodecyl phosphate, trihexadecyl phosphate, trioctadecyl phosphate, hexyl dioctyl phosphate, octyl didodecyl phosphate, trieicosyl phosphate and trialkyl phosphates prepared from mixtures of C7-09-C11 alcohols; examples of dialkylaryl phosphates include dibutyl phenyl phosphate, dihexyl phenyl phosphate, dioctyl phenyl phosphate, didecyl phenyl phosphate, diisodecyl phenyl phosphate, dihexadecyl phenyl phosphate, octyl dodecyl phenyl phosphate and di(C7-Cg-Cll) alkyl phenyl phosphate; and examples of alkyldiaryl phosphate include butyl diphenyl phosphate, octyl diphenyl phosp decyl diphenyl phosphate, isodecyl diphenyl phosphate, dodecyl diphenylphosphate, hexadecyl diphenyl phosphate cyclohexyl dipheisyl phosphate, and (C7-C9-C11) alkyl diphenyl. phosphate. Especially preferred phosphate esters for use in the compositions of the present invention are tri-2ethylhexyl phosphate, isodecyl diphenyl phosphate and 2-ethylhexyl diphenyl phosphate The amounts of the hydrated basic magnesium calcium carbonates which can be used in the compositions qf " t,' present invention depend on various factors, including the nature of the polymer, the presence or absence of other components having smoke depressant properties, and the amount of the hydrated basic magnesium calcium carbonate which can be tolerated without adversely affecting the physical properties of the composition. For most applications, a suitable amount of the hydrated basic magnesium calcium carbonate will be within the range 15 to 50 parts by weight per 100 parts by weight of polymer (PHR), more especially within the range 20 to 40 PHR. The hydrated basic magnesium calcium carbonates function as fillers as well as smoke depressants. They may be the only filler employed, but compositions within the scope of the invention may also contain conventional substantially inert fillers such as carbon black, calcium carbonate or silica and conventional flame-retardant fillers such as Sb203, aluminium trihydrates, or borates. Halogen-containing polymer compositions usually contain a plasticizer in an amount of from 10 to 150 PER, depending on the use for which the composition is required. As indicated above, the preferred phosphate ester plasticizers can b used in conjunction with other 1:ers; where such mixtures are employed, the phosphate ester cornpcnent preferably constitutes at least ):' height and mors preferably at least 50% by weight, of the plasticizer mixture. the polymer compositions of the invention can also c@ntain other conventional compounding ingredients, for example stabilizers, UV absorbers and pigments. The invention is illustrated by the following Example. EXAMPLE The following formulations, one for each of the carbonates shown in the table below, were prepared and cal@ndered into films 0.3 mm. thick. Inqredient Parts by Weiqht Polyvinyl chloride 100 Alkyl diphenyl phosphate 50 Stabilizer 2 Epoxy resin 2 Carbonate 30 Samples were cut from the film and mounted in an Aminco-NBS Smoke Chamber, which measures smoke generating characteristics of solid materials by the attenuation of a light beam by suspended particulate matter generated from the maternal undergoing pyrolytic decomposition (smouldering) or flame combustion within a closed chamber. The resulting measurement is expressed in terms of the maximum specific optical density (DM). The results given in the table below were obtained under smouldering conditions. The value for DM is inversely r.elated to the effectiveness of the additive as a smoke depressant. Three tests, with results as shown, were carried out on the formulation containing carbonate B. EMI6.1 <tb> Carbonate <SEP> A <SEP> B <SEP> C <SEP> D <tb> % <SEP> w/w <SEP> MgO <SEP> 20.5 <SEP> 24.6 <SEP> 20 <SEP> 41-42 <tb> S <SEP> w/w <SEP> CaO <SEP> 29 <SEP> 24.1 <SEP> 31 <tb> Combined <tb> water <SEP> (S <SEP> w/w) <SEP> 9.2 <SEP> ? <SEP> 0.3 <SEP> 18 <tb> Particle <SEP> 99.5X <SEP> 99 <SEP> 5X <SEP> 40 <SEP> microns <SEP> 32 <SEP> microns <tb> size <SEP> less <SEP> lessor <tb> <SEP> than <SEP> 44 <SEP> than <SEP> 44 <tb> <SEP> microns <SEP> microns <tb> DM <SEP> 52 <SEP> 39/37/46 <SEP> 76 <SEP> 45 <tb> A. Hydrated basic magnesium calcium carbonate, approximate formula 2 lflgC03 Mg(OH)2. 3H2O . 3CaCO3. B. Hydrated basic magnesium calcium carbonate. C Dolomite MgCa(CO3)2 D. Hydrated basic magnesium carbonate. The results show that the hydrated basic magnesium calcium carbonates have substantially the same effectiveness as smoke depressants as the hydrated basic magnesium carbonate, and that dolomite is much less effective. Calcium carbonate would be expected to give a result similar to that obtained with dolomite.

Claims: CLAIMS EMI8.1 1. A composition comprising a blend of an organic polymer h a smoke depressant characterised in that the smoke depressant is a hydrated basic magnesium calcium carbonate. 2. A composition according to Claim 1 wherein the organic polymer is a halogen-containing polymer and the composition also contains a plasticizer. 3. A composition according to Claim 2 wherein the halogencontaining polymer is polyvinyl chloride or a copolymer of vinyl chloride with one or more other ethylenically unsaturated monomers in an amount of not more than 40 molar percent relative to the vinyl chloride. 4. A composition according to either of Claims 2 and 3 wherein the plasticizer is a phosphate ester or a mixture of plasticizers containing at least 30% by weight of phosphate ester. 5. A composition according to any of Claims 1 to 4 wherein the amount of the hydrated basic magnesium carbonate is from 15 to 50 parts by weight per 100 parts by weight of the organic polymer. 6. A composition according to any of Claims 1 to 5 wherein the hydrated basic magnesium calcium carbonate has the approximate formula 2 MgC03. Mg(OH)2. 3H20. 3CaC03

Inventors: LAMBERT, JEAN-LUC JULES
Applicants: MONSANTO EUROPE S.A.
Application year: 1979
Main classification: C08K3
IPC codes: C08K3