# Patent

## Title
Heat curable polyepoxide resin blends

## Abstract

This application is a continuation-in-part of copending application Ser. No. 410,738, filed Aug. 23, 1982 abandoned, which is a division of application Ser. No. 306,845, filed Sept. 29, 1981, now U.S. Pat. No. 4,424,333, which in turn is a continuation-in-part of application Ser. No. 203,212, filed Nov. 3, 1980, now abandoned, and of copending application Ser. No. 203,213, also filed Nov. 3, 1980, and now abandoned.

## Background
This invention relates to a select liquid polymer composition containing a modified polyurethane oligomer having terminal ethylenic unsaturation, a process for preparing a polyurethane polymer product employing the select liquid polymer composition and a polyurethane polymer product prepared according to the process.

More particularly, it has now been discovered, according to the present invention, that a heat curable liquid polymer composition can be prepared comprising a modified polyurethane oligomer containing terminal ethylenic unsaturation and a free radical generating catalyst. Such a composition features the advantages of a one-component storage stable system that requires only heat for activation; the composition is useful in preparing a wide variety of castings, coatings and gel coats.

The polyurethane oligomer that is utilized according to the invention is prepared by reacting an organic polyisocyanate, a polyol reactant and an isocyanate reactive group-containing unsaturated monomer. The reaction is carried out using methods well known in the art and employing such relative proportions of the reactants so as to achieve an oligomer product having an equivalent ratio of NCO to OH from about 0.8/1 to about 2/1, and preferably from about 1/1 to about 1.2/1. In forming the oligomer, there is also employed an equivalent ratio of isocyanate reactive group-containing unsaturated monomer to polyol reactant in the range from about 0.6/1 to about 3/1, and preferably from about 0.8/1 to about 2/1. By reaction of the organic polyisocyanate, polyol reactant and isocyanate reactive group-containing unsaturated monomer, a controlled molecular weight polyurethane oligomer with terminal reactive unsaturation is produced.

Preferably, the reaction is accelerated by employing a catalyst; common urethane catalysts, e.g., tertiary amines and metal compounds such as stannous octoate or dibutyltin dilaurate may be used. Any catalytic amount may be employed; illustratively, such amount varies, depending on the particular catalyst utilized, from about 0.01 to about 1 percent by weight of the polyurethane oligomer. It is also preferred to carry out the reaction in the presence of a reactive copolymerizable solvent. Suitable copolymerizable solvents include vinylidene compounds such as styrene, vinyl toluene, methacrylic esters, acrylic esters, divinyl benzene, and the like, familiar to those skilled in the art. The amount of copolymerizable solvent employed may be varied over a wide range. Generally, however, the copolymerizable solvent is employed in an amount of from about 0 to about 100 parts by weight per 100 parts by weight of the polyurethane oligomer of the present invention.

Any suitable organic polyisocyanate, or mixture of polyisocyanates, may be employed in preparing the polyurethane oligomer. Illustrative are toluene diisocyanate, such as the 80:20 and the 65:35 mixtures of the 2,4- and 2,6-isomers, ethylene diisocyanate, propylene diisocyanate, methylene-bis(4-phenyl)isocyanate, xylene diisocyanate, 3,3'-bitoluene-4,4'-diisocyanate, hexamethylene diisocyanate, naphthalene-1,5-diisocyanate, the polymeric isocyanates such as polyphenylene polymethylene isocyanate, mixtures thereof, and the like. In accordance with a particularly preferred embodiment of the invention, there is employed an isomeric mixture of 2,4- and 2,6-toluene diisocyanate in which the weight ratio of the 2,4-isomer to the 2,6-isomer is from about 60:40 to about 90:10, and more preferably from about 65:35 to about 80:20.

The polyol reactant used in the polyurethane oligomer formation comprises a select combination of polyols, i.e., a high functionality polyol and a chain extender. More in detail, the high functionality polyol is selected from polyether polyols and mixtures of two or more such compounds. The high functionality polyol, or mixture of high functionality polyols, should have an average equivalent weight ranging from about 75 to about 500. Preferably, the average equivalent weight is about 75 to about 350, and more preferably about 90 to about 200. The average functionality of the high functionality polyol or high functionality polyol blend is at least about 3, preferably about 3 to about 8, and more preferably about 3.3 to about 6.

Suitable high functionality polyether polyols include various polyoxyalkylene polyols and mixtures thereof. These can be prepared, according to well-known methods, by condensing an alkylene oxide, or a mixture of alkylene oxides using random or step-wise addition, with a polyhydric initiator or a mixture of polyhydric initiators. Illustrative alkylene oxides include ethylene oxide, propylene oxide, butylene oxide, amylene oxide, aralkylene oxides such as styrene oxide, and the halogenated alkylene oxides such as trichlorobutylene oxide and so forth. The most preferred alkylene oxide is propylene oxide or a mixture thereof with ethylene oxide using random or step-wise oxyalkylation.

The polyhydric initiator used in preparing the high functionality polyether polyol reactant comprises a carbohydrate or a carbohydrate derivative. Illustrative are sucrose, dextrose, methyl glucoside and mixtures thereof. In a particularly preferred embodiment, the polyhydric initiator includes a mixture of a carbohydrate or a carbohydrate derivative with at least one aliphatic diol or triol. Exemplificative of the latter are water, ethylene glycol, propylene glycol, the butylene glycols, glycerol, trimethylolpropane, triethylolpropane, the alkanolamines, and the like, and mixtures thereof.

The most preferred group of polyhydric initiators for use in preparing the high functionality polyether polyol reactant is one which comprises mixtures of sucrose or dextrose or methyl glucoside with an aliphatic triol, preferably glycerol.

The alkylene oxide-polyhydric initiator condensation reaction is preferably carried out in the presence of a catalyst such as KOH as is well known in the art. In effecting the reaction, a sufficient proportion of alkylene oxide is used as to provide a final polyol product having an average equivalent weight of about 75 to about 500, preferably about 75 to about 350, and more preferably about 90 to about 200. The catalyst is thereafter preferably removed, leaving a high functionality polyether polyol which is ready for use in preparing the polyurethane oligomer of the invention.

As indicated above, in forming the polyurethane oligomer, a chain extender is included in the polyol reactant. These chain extenders have an average equivalent weight ranging from about 31 to about 4,000, preferably from about 31 to about 500, and an average functionality of about 2. Suitable chain extenders include the following and mixtures thereof: (a) low molecular weight diols, such as ethylene glycol, butane diol, pentane diol, hexane diol, 2-ethyl-1,3-hexane diol, diethylene glycol, dipropylene glycol, triethylene glycol, tripropylene glycol, bisphenol A, and the like; and (b) polyether diols, such as propylene oxide diols, propylene oxide-ethylene oxide diols, and the like. Tripropylene glycol, polyether diols having an equivalent weight of about 100 to about 500, and mixtures thereof are particularly preferred. Usually, a proportion of chain extender is employed which ranges from about 20 to about 1,500, and preferably from about 50 to about 900, parts by weight per 100 parts by weight of the high functionality polyol.

Suitable isocyanate reactive group-containing unsaturated monomers include hydroxyalkyl acrylates, hydroxyalkyl methacrylates and hydroxyalkyl acrylamides, such as hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxyethyl acrylamide, hydroxypropyl acrylamide, and the like, and mixtures thereof. Hydroxyalkyl acrylates and hydroxyalkyl methacrylates are preferred, with hydroxyethyl acrylate, hydroxypropyl acrylate, and hydroxyethyl methacrylate being the most preferred.

The modified polyurethane oligomer liquid polymer system is polymerized and cured in the presence of a heat activated, free radical generating catalyst. The actual curing conditions may vary over wide ranges and are generally dependent on the nature and amount of the particular catalyst employed. Suitable free radical generating catalysts include peroxide or azo type compounds, known to those in the art. Typical peroxide catalysts are illustrated by organo peroxides and hydroperoxides such as benzoyl peroxide, dicumyl peroxide, methyl ethyl ketone peroxide, lauryl peroxide, cyclohexanone peroxide, t-butyl perbenzoate, t-butyl hydroperoxide, t-butylbenzene hydroperoxide, cumene hydroperoxide, t-butyl peroctoate, and the like. Typical azo compounds are azobis-isobutyronitrile, 2-t-butylazo-2-cyano-4-methylpentane, and 4-t-butylazo-4-cyano-valeric acid. The preferred catalysts are peroxide catalysts. In particular, preferred peroxide catalysts are t-butyl peroctoate, t-butyl perbenzoate, and mixtures thereof. Any suitable catalytic amount may be employed; however, the catalyst generally is used in an amount from about 0.1 to about 10 parts by weight per 100 parts by weight of the polyurethane oligomer.

The composition of the present invention also may include other standard ingredients, if desired, such as internal mold release agents, e.g., calcium, zinc, magnesium, or sodium stearate. Pigments, dyes, stabilizers, viscosity modifiers (e.g., Group II metal oxides and hydroxides, such as magnesium oxide), thixotropes and various other additives familiar to those skilled in the art also may be added.

The polyurethane liquid polymer composition is generally stable over a reasonable period of time, and can be stored usually for at least about 2 to about 4 weeks prior to use. The composition can then be cured upon the application of heat to a polyurethane polymer product demonstrating properties particularly desirable for coating applications. The cured products exhibit hardness characteristics which are generally highly satisfactory, yet also have sufficient flexibility as to resist cracking.

The following examples are provided to further illustrate the invention. All parts are by weight unless otherwise specified.

To 174 grams (2.0 eq.) of diisocyanate .sup..circle.1 , 285 grams of styrene, 0.071 grams of hydroquinone and 0.142 grams of 2,6-di-tertiary-butyl-4-methylphenol (BHT) were added dropwise with stirring a mixture of 117.5 grams (0.8 eq.) of a polyether polyol .sup..circle.2 , 19.2 grams (0.2 eq.) of a chain extender .sup..circle.3 and 116 grams (1.0 eq.) of unsaturated monomer .sup..circle.4  over a period of 2 hours. The reaction temperature rose from 21.degree. to 36.degree. C., and the mixture was stirred without heating for 2 hours after completion of the addition. At this point, 2.84 grams of catalyst .sup..circle.5  were added. After stirring without heating for 15 minutes, the reaction mixture was heated to 70.degree. C. and was stirred at 70.degree. C. for 41/2 hours. The product had a viscosity of 5200 cps at 25 C. mixture of 2,4/2,6-isomers). about 650 and an average functionality of about 4.25 and prepared by condensing a sucrose/glycerol mixture with propylene oxide to a final hydroxyl number of about 375. a commercial product of Witco Chemical Corporation purchased under the designation "T-10".

Additional polyurethane oligomers were prepared employing the same conditions as in Example 1, except that the time was varied for the reaction at 70.degree. C. in the final step of the procedure. Different reactants and proportions of reactants were also used. Table I outlines the oligomer compositions prepared according to Examples 2-10. __________________________________________________________________________ OLIGOMER COMPOSITIONS Polyether Polyol Chain Extender Unsaturated Monomer Diisocyanate.sup. .circle.1 (eq.)    (eq.)   (eq.)      Viscosity Reaction Time Example (eq.)   A.sup. .circle.2 B.sup. .circle.3 C.sup. .circle.4 D.sup. .circle.5 E.sup. .circle.6 F.sup. .circle.7 G.sup. .circle.8 (cps at 25.degree. C.) at 70.degree. C. __________________________________________________________________________ (hrs.) 1    2.0     0.8  --  0.2 --  1.0 -- --  5200     41/2 2    2.0     --   0.6 0.4 --  --  1.0 --  4000     31/2 3    2.0     --   0.2 0.6 0.2 0.5 0.5 --  640     4 4    2.0     0.2  --  0.8 --  --  1.0 --  650     10 5    2.0     0.6  --  0.2 0.2 --  1.0 --  3300    5 6    2.0     0.8  --   0.15 0.05 0.5 0.5 --  5350     71/2 7    2.0     0.1  0.1 --  0.8 --  1.0 --  350      61/2 8    2.0     0.8  --  0.2 --  --  -- 1.0 355      51/2 9    2.0     0.2  --  0.8 --  --  -- 1.0 500     7 10   2.0     --   0.2 0.8 --  1.0 -- --  --       31/2 __________________________________________________________________________ .sup. .circle.1  The diisocyanate is a mixture of toluene diisocyanate isomers (80:20 mixture of 2,4/2,6isomers). .sup. .circle.2  A polyether polyol having a molecular weight of about 65 and an average functionality of about 4.25 and prepared by condensing a sucrose/glycerol mixture with propylene oxide to a final hydroxyl number of about 375. .sup. .circle.3  A polyether polyol having a molecular weight of about 48 and an average functionality of about 4.54 and prepared by condensing a sucrose/glycerol mixture with propylene oxide to a final hydroxyl number of about 530. .sup. .circle.4  Tripropylene glycol. .sup. .circle.5  A polyether polyol having a molecular weight of about 42 and prepared by condensing propylene glycol with propylene oxide to a final hydroxyl number of about 265. .sup. .circle.6  Hydroxyethyl acrylate. .sup. .circle.7  Hydroxypropyl acrylate. .sup. .circle.8  Hydroxyethyl methacrylate.

Test panels were prepared containing polyurethane oligomers prepared according to Examples 1-9. The following procedure was followed in the preparation of the cured panels. catalyst .sup..circle.1 , and the resulting mixture was degassed by placement in a vacuum dessicator at about 1-10 torr pressure for approximately 1-2 minutes or until initial foaming subsided. coated with a liquid mold release agent, such as "MR515" commercially available from Greenchem Products, Inc., and held apart by one-sixteenth inch spacers.

The physical properties of panels prepared in this manner are included in Table II below. The physical properties were determined in accordance with standard test procedures: Flexural modulus and flexural strength--ASTM D790; tensile strength and elongation--ASTM D3574; and izod--ASTM D256. The barcol hardness was determined by using a Colman Model GYZJ 934-1 Impressor. peroctoate (commercially available from Lupersol Co. under the designation "PDO", understood to consist of 50% tertiary butyl peroctoate and 50% dioctyl phthalate) and 0.5% tertiary butyl perbenzoate as initiator.

For purposes of comparison, a test panel containing a polyester resin was prepared following the procedure of Examples 11-19. In forming the panel, in place of a polyurethane oligomer of Examples 1-9, there was employed a vinyl ester resin commercially available from Dow Chemical Company under the designation "Derakane 470".

The physical properties of the panel prepared in this manner are included in Table II below. The physical properties were determined in accordance with standard test procedures: Flexural modulus and flexural strength--ASTM D790; tensile strength and elongation--ASTM D3574; and izod--ASTM D256. The Barcol hardness was determined by using a Colman Model GYZJ 934-1 Impressor.

In comparing the results, the panels prepared from polyurethane oligomers of the invention showed overall properties at least comparable to, or better than, those demonstrated by the panel made from the vinyl ester. In particular, these panels exhibited improved elongation values, indicating desirable flexibility and toughness characteristics. These properties are important in coating applications where crack resistance is generally sought. __________________________________________________________________________ PHYSICAL PROPERTIES OF POLYURETHANE OLIGOMER CASTINGS Tensile    Flexural Flexural Strength Elongation Strength Modulus .times. Izod (ft.-lb./in.) Barcol Example Oligomer (psi) (%)   (psi) 10.sup.6 (psi) Notched Unnotched Hardness __________________________________________________________________________ 11   Example 1 9770 4.39  17750 0.544 2.29 4.45  38 12   Example 2 7000 2.92  15760 0.567 2.80 4.46  42 13   Example 3 9620 4.04  18300 0.541 3.90 5.41  39 14   Example 4 10300 4.65  18600 0.544 2.23 4.97  41 15   Example 5 10200 4.58  17300 0.505 2.37 4.44  34 16   Example 6 10000 4.39  17600 0.521 3.04 5.01  40 17   Example 7 9500 4.35  14500 0.466 2.32 5.96  25 18   Example 8 11680 5.29  18000 0.518 2.28 4.36  38 19   Example 9 10500 4.61  19800 0.572 2.25 5.42  43 CE-1 --     6680 3.02  16600 0.585 2.75 3.68  46 __________________________________________________________________________

## Claims

1. A process for preparing a polyurethane polymer product comprising mixing a polyurethane oligomer and a heat activated free radical generating catalyst, and then heating said mixture at a temperature adequate to activate said catalyst and cure said mixture, said polyurethane oligomer having an equivalent ratio of NCO to OH from about 0.8/1 to about 2/1 and being prepared by reacting about 75 to about 500 and an average functionality of at least about 3, said high functionality polyol being prepared by reacting an alkylene oxide, or a mixture of alkylene oxides, with a polyhydric initiator comprising a carbohydrate or a carbohydrate derivative, and about 4,000 and an average functionality of about 2, said chain extender being employed in an amount ranging from about 20 to about 1,500 parts by weight per 100 parts by weight of said high functionality polyol; and from the group consisting of said isocyanate reactive group-containing unsaturated monomer to said polyol reactant in the range from about 0.6/1 to about 3/1.

2. The process of claim 1, wherein: to about 350, 1/1 to about 1.2/1, and unsaturated monomer to said polyol is in the range from about 0.8/1 to about 2/1.

3. The process of claim 2, wherein said high functionality polyol has an average equivalent weight of about 90 to about 200 and an average functionality of about 3.3 to about 6 and is prepared by reacting a polyhydric initiator selected from mixtures of sucrose, dextrose or methyl glucoside and an aliphatic triol with an alkylene oxide selected from propylene oxide and mixtures of propylene oxide and ethylene oxide.

4. The process of claim 3, wherein said chain extending agent is selected from the group consisting of tripropylene glycol, polyether diols having an equivalent weight of about 100 to about 500, and mixtures thereof.

5. The process of claim 4, wherein said unsaturated monomer is selected from hydroxyethyl acrylate, hydroxypropyl acrylate, hydroxyethyl methacrylate, and mixtures thereof.

6. The process of claim 5, wherein said reaction is carried out in the presence of a copolymerizable solvent.

7. The process of claim 6, wherein said solvent is styrene.

8. The process of claim 7, wherein said heat activated free radical generating catalyst is a peroxide catalyst.

9. The process of claim 8, wherein said peroxide catalyst is selected from t-butyl perbenzoate, t-butyl peroctoate, and mixtures thereof, and said organic polyisocyanate is toluene diisocyanate.

10. The process of claim 9, wherein said reaction is accelerated by employing a urethane catalyst.

11. The polyurethane polymer product prepared according to the process of claim 1.

12. The polyurethane polymer product prepared according to the process of claim 2.

13. The polyurethane polymer product prepared according to the process of claim 3.

14. The polyurethane polymer product prepared according to the process of claim 4.

15. The polyurethane polymer product prepared according to the process of claim 6.

16. The polyurethane polymer product prepared according to the process of claim 10.