# Patent

## Title
Partial oxidation process

## Abstract

This application is a continuation-in-part of Application Ser. No. 350,921 filed Feb. 2, 1982, now U.S. Pat. No. 4,419,106, issued Dec. 16, 1983.

## Background
This invention relates to hydrocarbon oils and more particularly to hydrocarbon oils having improved pour points.

In the storage, transportation and use of hydrocarbon fuel oils, e.g. crude oils, gas oils, distillate fuel oils, such as heating oils, diesel oils, turbo-jet fuels and residual fuel oils and the like, problems associated with the pour point of the oils have been long recognized. The pour point of an oil is defined as the lowest temperature at which the oil will flow when chilled without disturbance under specified conditions. Pour point problems arise through the formation of solid or semi-solid waxy particles in the oils when the oils are subjected to low temperatures in storage. A related problem also exists in respect of hydrocarbon residual fuel oils and waxy crude oils, in which the waxy components adversely affect the flowability and/or pumpability of the oil under low temperature conditions.

The formation of solid or semi-solid waxy particles in fuel oils and in waxy crude oils a temperatures just below their pour point causes serious distribution and/or operating difficulties. For example, the distribution of fuel oil by pumping is rendered difficult or impossible at temperatures below the pour point of the oil. Likewise, the flow of the oil at such temperatures through filters in heating systems cannot be maintained, resulting in the failure of the equipment to function. The formation of solid or semi-solid waxy particles in wax-containing crude oils gives rise to difficulties in the movement of such crude oils through pipelines at low ambient temperatures.

With respect to fuel oils, the aforementioned problems have been in part, remedied by lowering the end points of oils used for blending heating and diesel oils. It has also been suggested that the fuel oils, particularly distillate fuel oils, may be dewaxed, as for example, by urea dewaxing. However, dewaxing operations are costly and readjustment of end points causes a loss of valuable product as blending material for fuel oil stocks.

Another approach in overcoming the problem has been to attempt to find a pour point depressant which will lower the pour point of the fuel oil or crude oil. This is sometimes done to lower the pour point of lubricating oils. However, materials which are effective in lowering the pour point of lubricating oils are usually ineffective as pour point depressants for fuel oils or crude oils.

Pour point depressants appear to function by modifying the wax crystals so that they form smaller crystals having a reduced tendency to form gels. Different types of materials have been used as pour point depressants with varying degrees of success. High molecular weight polymers are among the more successfully used pour point depressants. U.S. Pat. No. 3,726,653 discloses two component residual fuel pour point depressants one component of which may be a copolymer of an alkyl ester of an unsaturated monocarboxylic acid and a mono-olefin. U.S. Pat. No. 3,447,915 discloses fuel oil pour point depressants comprised of a terpolymer of ethylene, propylene and a C.sub.1 -C.sub.12 alkyl ester of acrylic or methacrylic acid. U.S. Pat. No. 4,042,648 and other patents referred to in the second paragraph of column 1 thereof disclose thermoplastic olefin-acrylic ester copolymers. and their preparation. U.S. Pat. No. 3,968,148 discloses the preparation of oligomers of higher molecular weight olefins and higher molecular weight alkyl acylates which oligomers are useful as dispersant detergents for lube stocks. British Pat. No. 1,154,966 discloses the use of various homopolymers and copolymers as pour point depressants for petroleum fuels. Other U.S. Pat. Nos. which disclose copolymers of acrylates as pour point depressants are 2,604,453, 2,403,267, 3,304,260, 3,904,385 and 3,445,205. U.S. 3,567,639 discloses copolymers of ethylene and a vinyl ester as pour point depressants for crude oil and fuel oils.

Although the above polymeric pour point depressants may produce satisfactory results in specific applications, there is a continuing need for improved highly efficient oil pour point depressants having good pour point depressing properties in a wide range of hydrocarbon oils.

It is an object of the invention to present new hydrocarbon oil pour point depressants. It is another object of the invention to present hydrocarbon oil compositions having improved pour points. It is another object of the invention to present a method of lowering the pour points of hydrocarbon oils. These and other objects of the invention are supported in the following description and examples.

The objects of the invention are accomplished by incorporating into hydrocarbon oils a copolymer of an alkyl acrylate, the alkyl group of which has about 8 to 30 carbon atoms, and a vinylidene olefin having at least 16 carbon atoms. The copolymer desirably has a weight average molecular weight of about 1000 to 100,000 and is usually effective in concentrations of about 0.001 to 5 weight percent, based on the weight of hydrocarbon oil. Suitable copolymers are comprised of about 10 to 90 parts by weight of at least one vinylidene olefin and about 90 to 10 parts by weight of at least one alkyl acrylate per 100 parts by weight of total copolymer. In preferred embodiments the copolymer is comprised of about 20 to 75 parts by weight of alkyl acrylate having 16 to 28 carbon atoms in the alkyl group, and 25 to 80 parts by weight of vinylidene olefin having at least 16 carbon atoms per 100 parts by weight of copolymer, the weight average molecular weight of the copolymer is in the range of about 3,000 to 50,000 and the copolymer is added to the hydrocarbon oil at a concentration of about 0.005% to 1% and most preferably at a concentration of about 0.01% to 0.5%, based on the weight of the hydrocarbon oil. In the most preferred embodiment the copolymer is comprised of about 30 to 60 parts by weight of alkyl acrylate and about 70 to 40 parts by weight of vinylidene olefin per 100 parts of total copolymer.

The alkyl acrylates useful for the preparation of the pour point depressants are those having alkyl groups containing 8 to 30 carbon atoms. The alkyl groups may be linear or branched. Typical useful acrylates include n-dodecyl acrylate, n-octadecyl acrylate, n-eicosyl acrylate, N-docosyl acrylate, n-tetracosyl acrylate, n-triacotanyl acrylate, 2-ethylhexadecyl acrylate, 1-methylheptadecyl acrylate, etc. Preferred alkyl acrylates are those having about 16 to 28 alkyl carbon atoms such as n-octodecyl acrylate, 2-ethyloctadecyl acrylate, etc.

The alkyl acrylates used in the manufacture of products of this invention may be prepared by esterifying acrylic acid with alcohols having the desired carbon chain length and configuration.

Useful alcohols include normal and branched chain alcohols having 16 to 28 carbon atoms such as octadecanol, n-eicosanol and 2-ethylhexadecanol. Mixtures of these alcohols may also be used in the preparation of the alkyl acrylate reactants. Suitable alcohol mixtures are those sold by Continental Oil Company under the trademark "Alfols".

In a typical procedure for preparing the alkyl acrylate, the alcohol or alcohol mixture is reacted with acrylic acid by means of a suitable esterification catalyst, such as p-toluenesulfonic acid, in the presence of a polymerization inhibitor, such as hydroquinone. The esterification reaction is preferably carried out at temperatures in the range of about 175 to 250.degree. F. in the presence of an azeotroping agent, such as benzene or toluene, to facilitate removal of water from the product. The method of preparation of the alkyl acrylates is not a part of this invention and the above procedure is merely illustrative.

The vinylidene olefins useable in preparing products useful in the invention are the vinylidene olefins having at least 16 and preferably 20 to 68 carbon atoms. Most preferred vinylidene olefins are vinylidene monoolefins having about 24 to 56 carbon atoms. Typical useful vinylidene olefins are those having the structure; ##STR1##

Wherein R and R.sub.1 are the same or different straight or branched-chain saturated hydrocarbon radicals having about 1 to 40 and preferably about 20 to 34 carbon atoms and R.sub.2 is a straight or branched-chain saturated hydrocarbon radical having about 1 to 12 and preferably about 1 to 6 carbon atoms. In the most preferred embodiment R and R.sub.1 are linear alkyl radicals having about 20 to 34 carbon atoms and R.sub.2 is CH.sub.2. Typical vinylidene olefins include 7-vinylpentadecane, 15-allyl hentriacotane, 21-vinyltritetracontane, etc. Mixtures of vinylidene olefins may be used in the invention and, in fact, commercially available vinylidene olefins are generally comprised of mixtures of vinylidene olefins.

The method of preparation of useful vinylidene olefins forms no part of this invention. Suitable vinylidene olefins can be prepared by dimerzation of lower olefins by Ziegler technology. Suitable vinylidene olefins are also available commercially. Typical commercially available vinylidene compounds include C40-48 vinylidene dimer sold by Gulf Chemical Company.

The copolymerization of the vinylidene olefin and the alkyl acrylate can be accomplished by any of the known methods for polymerizing higher olefins. For example, the polymerization can be carried out in bulk, in solution, in emulsion or in the vapor phase using a wide variety of catalysts. Particularly useful catalysts are the free radical catalysts, such as the organic peroxides or azonitriles. Typical organic peroxides include acylperoxides, such as benzoyl peroxide; alkyl peroxides, such as t-butyl peroxide; ketone peroxides, such as methylethyl ketone peroxide; hydroperoxides, such as cumene hydroperoxide; and peresters, such as t-butyl perbenzoate. A typical azo-nitrile is azo-bis-isobutronitrile. The particular catalyst used will depend upon the selected polymerization reaction temperature. The amount of catalyst used in the polymerization reaction generally is in the range of about 0.01 to 10 weight percent, and preferably is in the range of about 0.1 to 5 weight percent based on the total weight of monomers present in the reaction zone. The catalyst may be advantageously continuously charged to the reactor over the entire course of the reaction.

Where solution polymerization techniques are employed the solvent is preferably an aromatic compound, such as benzene, toluene, xylene or cumene. Cumene is advantageous because it provides significant chain-transfer activity.

The polymerization is generally carried out, for a period of several hours, at a temperature of about 50 to 120.degree. C. Temperatures in the range of about 80 110.degree. C. are generally preferred.

The alkyl acrylate-vinylidene olefin copolymer can be prepared by the following procedure: A suitable reaction vessel equipped with an agitator and cooling means is purged with nitrogen to remove oxygen, sealed and charged with the desired vinylidene olefin monomer(s) and the reactor is heated to the desired reaction temperature. While maintaining the reaction temperature, the alkyl acrylate, a solvent, if one is used, and a suitable polymerization catalyst are charged to the reaction vessel continuously during the course of the reaction, which begins upon addition of catalyst to the reactor. After all of the catalyst has been introduced, the reaction temperature may be maintained for an additional period of time, for example, about an hour. The temperature of the reactor contents is then raised to effect desired curing of the product and to deplete the catalyst. At the conclusion of the curing step the reactor contents are cooled to about room temperature and the product is recovered from the reactor. The product may be used as is or it may be separated from the solvent by any suitable means, such as by distillation. The above method of polymerization is merely illustrative and is not a part of this invention.

The additives of this invention can be used to lower the pour points of hydrocarbon oils, which includes crude oils, gas oils, hydrocarbon fuel oils such as distillate fuel oils, including kerosene, diesel oil, heating oils, etc. and residual fuel oils, such as bunker C oil and navy grade special fuel oils, and other oils which contain substantial quantities of waxy materials and which present low temperature pumping and handling problems but excludes lubricating oils. In treating such oils the alkyl acrylate-olefin copolymer is introduced into the oil at a temperature above the solution temperature of the waxy component of the oil. This is usually above about 150.degree. F. It has been found that the polymer is not as effective for producing the desired pour point depression if the mixing is carried out at a temperature substantially below the solution point of a substantial portion of the waxy component of the oil. As noted above the polymer can be in the form of a solution in the solvent in which the polymerization took place. If the polymerization solvent is an aromatic solvent and it is desired to not use a non-aromatic solvent the polymer can be separated from the aromatic solvent, as described above, and mixed with the desired solvent, such as an inert cutter stock, and the polymer-solvent mixture can be blended with the oil at an elevated temperature.

The following examples illustrate the preparation of the alkyl acrylate-vinylidene olefin copolymer and the use of the copolymer as a pour point depressant. Unless otherwise specified, parts and percentages are on a weight basis. Pour Points are determined by the procedure of ASTM D-97. The weight average molecular weights of the copolymers are determined by gel permeation chromatography using polystyrene as the calibration standard.

To a three-neck, one-liter glass reaction flask which is equipped with an agitator, a thermometer and a dropping addition funnel and which has been purged with nitrogen is charged 205 grams of the above-described Gulf Chemical Company C.sub.40 -C.sub.48 vinylidene olefin blend, 108 grams of n-octadecyl acrylate and 60 grams of cumene. The reaction mixture is heated under a nitrogen blanket to 80.degree. C. and, with continuous stirring and the temperature maintained at 80.degree. C., a solution of 1.44 grams of t-butyl peroctate in 20 grams of cumene is added to the reaction mixture over a four hour period. When the catalyst addition is completed the reaction temperature is raised to and maintained at 110.degree. C. for one hour. At the end of this period the reaction mixture is cooled to 65.degree.-70.degree. C., and 225 grams of heavy aromatic solvent, sold under the trademark Exxon 654, is added. The polymeric product obtained has a weight average molecular weight of 13,715.

The procedure of Example I is repeated except that the vinylidene olefin is omitted and 297 grams of octadecyl acrylate, 50 grams of cumene and 2.2 grams of t-butyl peroctoate in 20 grams of cumene are charged to the reactor. At the end of the reaction 225 grams of Exxon 654 solvent is added to the cooled reaction product.

The procedure of Example I is repeated except that the monomer charge consists of 205 grams of the vinylidene olefin used in Example I and 108 grams of n-octadecyl acrylate, 68.7 grams of cumene is added as solvent and 3.42 grams of 5-butyl peroctoate dissolved in 20 grams of cumene, is added as catalyst. At the end of the reaction 241 grams of Exxon 654 solvent is added to the cooled reaction product.

The products of Examples I to III are evaluated as pour point depressants in Number 6 fuel oil. In runs 1-4 the fuel oil is diluted with 30% by volume diesel oil and in runs 5-7 the fuel oil is diluted with 15% by volume diesel oil. The results are tabulated in Table I. Runs 1 and 5 are control samples and contain no pour point depressant. ______________________________________ Pour Point   Depressant Pour Point, Run     Depressant   Dosage, ppm .degree.F. ______________________________________ 1       None         --         50 2       Ex. I Product 1500        5 3       Ex. II Product 1500       35 4       Ex. III Product 1500       25 5       None         --         65 6       Ex. I Product 1000       15 7       Ex. I Product 1500       10 ______________________________________

The products of Examples I and III are evaluated as pour point depressants in heavy fuel oil derived from Ekofisk Crude oil (Norway). The heavy fuel oil had a boiling range of >650.degree. F. The results are tabulated in Table II. ______________________________________ Pour Point   Depressant Pour Point, Run     Depressant   Dosage, ppm .degree.F. ______________________________________ 1       None           0        45 2       Ex. I Product 1000       20 3       Ex. I Product 1500        0 4       Ex. III Product 2000       25 5       Ex. III Product 3000        0 ______________________________________

The above examples show that copolymers of vinylidene olefins mixture and octadecyl acrylate are excellent pour point depressants for residual fuel and heavy fuel oil. A comparison of results obtained using the Example I product and the Example II product as pour point depressants for residual fuel oil reveals that a copolymer of vinylidene olefin and octadecyl acrylate is very much superior to octadecyl acrylate homopolymer as a pour point depressant.

Although the invention has been described by specific working examples, the scope of the invention is not limited thereto. Modifications of the invention which are not illustrated are contemplated. For example, mixtures of alkyl acrylates having 8 to 30 carbon atoms may be substituted for the octadecyl acrylate. The scope of the invention is limited only by the scope of the appended claims.

## Claims

1. An oil composition comprising a hydrocarbon oil and a pour depressing amount of a copolymer of about 10 to 90 parts by weight of alkyl acrylate units containing about 8 to 30 alkyl carbon atoms and about 90 to 10 parts by weight of vinylidene olefin units having at least 16 carbon atoms per 100 parts by weight of copolymer, said copolymer having a weight average molecular weight of about 1,000 to 100,000.

2. The composition of claim 1 wherein said alkyl acrylate contains 16 to 28 alkyl carbon atoms and said vinylidene olefin contains about 20 to 68 carbon atoms and said copolymer is present in said composition at a concentration of about 0.001 to 5.0 weight percent, based on the total weight of the composition.

3. The composition of claims 1 or 2 wherein said copolymer comprises about 20 to 75 parts by weight of alkyl acrylate units and about 25 to 80 parts by weight of vinylidene olefin units per 100 parts by weight of copolymer.

4. The composition of claims 1 or 2 wherein said copolymer is about 30 to 60 parts by weight of alkyl acrylate units and about 70 to 40 parts by weight of vinylidene olefin units per 100 parts by weight of copolymer.

5. The composition of claims 1 or 2 wherein the weight average molecular weight of the copolymer is 3,000 to 50,000.

6. The composition of claim 4 wherein the weight average molecular weight of the copolymer is 3,000 to 50,000.

7. The composition of claim 5 wherein the copolymer is present in said composition at a concentration of about 0.005 to 1%, based on the total weight of the composition.

8. The composition of claim 6 wherein the copolymer is present in said composition at a concentration of about 0.005 to 1%, based on the total weight of the composition.

9. An oil composition comprised of a hydrocarbon fuel oil and a copolymer of about 25 to 75 parts of units of at least one alkyl acrylate containing 16 to 28 alkyl carbon atoms and about 25 to 80 parts of units of at least one vinylidene monoolefin containing about 20  to 68 carbon atoms, the copolymer having a weight average molecular weight of about 3,000 to 50,000 and being present in the composition at a concentration of about 0.005 to 1%, based on the total weight of the composition.

10. The composition of claim 9 wherein the alkyl acrylate is selected from the group consisting of n-octadecyl acrylate, n-eicosyl acrylate, n-docosyl acrylate, tetracosyl acrylate and mixtures of these and the vinylidene monoolefin has about 24 to 56 carbon atoms.

11. The composition of claim 10 where the alkyl acrylate is octadecyl acrylate.