# Patent

## Title
Silicon epitaxial wafer and the production method thereof

## Abstract

A silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon wafer having a diameter of at least 300 mm produced by slicing a silicon single crystal ingot doped with boron and germanium grown by the Czochralski method, wherein boron is doped to be at a concentration of 8.5×1018 (atoms/cm3) or higher and germanium is doped to satisfy a relational expression (formula 1) below.




  
    
      
        
          
          
            3
            ×
            
              
                (
                
                  
                    
                      
                        
                          4.64
                          ×
                          
                            
                              10
                              
                                -
                                24
                              
                            
                            ·
                            
                              [
                              Ge
                              ]
                            
                          
                        
                        -
                      
                    
                  
                  
                    
                      
                        2.69
                        ×
                        
                          
                            10
                            
                              -
                              23
                            
                          
                          ·
                          
                            [
                            B
                            ]
                          
                        
                      
                    
                  
                
                )
              
              5.43
            
            ×
            
              r
              2
            
            ×
            
              
                t
                epi
              
              
                
                  (
                  
                    t
                    sub
                  
                  )
                
                2
              
            
          
          
        
        ≤
        26.
      
    
    
      
        [
        
          Forrmula
          ⁢
          
            
          
          ⁢
          1
        
        ]

## Background
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a silicon epitaxial wafer and the production method thereof. Particularly, the present invention relates to a low specific resistance and large diameter silicon epitaxial wafer that has a reduced warpage and the production method thereof.
2. Description of the Related Art
In recent years, power semiconductor devices have been used for power control, etc. As a wafer for a power semiconductor device, a silicon epitaxial wafer obtained by growing a silicon epitaxial layer almost completely free from any crystal defects on a surface of a silicon wafer obtained by slicing a silicon single crystal ingot grown by the Czochralski (CZ) method is mainly used. Generally, a silicon wafer having a low specific resistance doped with a dopant at a high concentration is used as a silicon wafer for a power semiconductor device.
For attaining a further lower power consumption of a power semiconductor device, a silicon wafer having a lower specific resistance has been demanded. In the case of a p type silicon wafer, a silicon wafer having a low specific resistance is produced by doping, for instance, boron (B) as a dopant at a high concentration. In order to improve the productivity of semiconductor devices, silicon wafers with 300 mm diameter are mainly used instead of silicon wafers with 200 mm diameter. Further, a thickness of a silicon epitaxial layer is apt to increase in connection with a high withstand voltage of a power semiconductor device.
However, when growing a silicon epitaxial layer on a surface of a silicon wafer having a low specific resistance, warpage of the silicon epitaxial wafer is caused because a lattice constant of the silicon wafer and that of the silicon epitaxial layer are different. The warpage becomes larger when a diameter of the wafer becomes larger or when a thickness of the silicon epitaxial layer increases. When the warpage increases, it becomes difficult to make a mask and to hold the silicon epitaxial wafer with vacuum chuck in the device production process and if things come to the worst, it becomes impossible to manufacture semiconductor devices. Consequently, it has become a critical problem to reduce a warpage of a silicon epitaxial wafer as much as possible (See Patent Reference 1). Particularly, in a p/p+ silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon wafer into which boron is doped at a high concentration, a lattice constant difference is large between the silicon wafer (substrate) doped with boron and the epitaxial layer without being doped, consequently, there has been a disadvantage that a warpage amount of the wafer becomes large after the epitaxial growth.
Also it was found that a silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon single crystal wafer having a crystal orientation of (110) is more liable to be warped than a silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon single crystal wafer having a crystal orientation of (100).
[Patent Reference 1] Japanese Patent Laid-open Hei 6-112120
SUMMARY OF THE INVENTION
An object of the present invention is to reduce a warpage of a silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon wafer with low specific resistance and large diameter.
The present invention provides an improvement of a silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon wafer having a diameter of at least 300 mm produced by slicing a silicon single crystal ingot added with boron and germanium grown by the Czochralski method and the production method thereof.
The feature of the present invention exists in that a silicon wafer is doped to have a boron concentration of 8.5×1018 (atoms/cm3) or higher and doped with germanium in a range of satisfying the relational expression (Formula 1) below.




  
    
      
        
          
          
            3
            ×
            
              
                (
                
                  
                    
                      
                        
                          4.64
                          ×
                          
                            
                              10
                              
                                -
                                24
                              
                            
                            ·
                            
                              [
                              Ge
                              ]
                            
                          
                        
                        -
                      
                    
                  
                  
                    
                      
                        2.69
                        ×
                        
                          
                            10
                            
                              -
                              23
                            
                          
                          ·
                          
                            [
                            B
                            ]
                          
                        
                      
                    
                  
                
                )
              
              5.43
            
            ×
            
              r
              2
            
            ×
            
              
                t
                epi
              
              
                
                  (
                  
                    t
                    sub
                  
                  )
                
                2
              
            
          
          
        
        ≤
        26
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          1
        
        ]
      
    
  




Particularly, the crystal orientation of the silicon wafer is preferably (110). Further, the thickness of the silicon epitaxial layer is preferably in the range from 4 μm through 20 μm. When the thickness is smaller than 41 μm, a warpage will not occur. When the thickness exceeds 20 μm, it requires that a doping amount of germanium into a silicon wafer (substrate) becomes high, leading to a rise of production cost.
According to the present invention, when obtaining a silicon epitaxial wafer obtained by growing a silicon epitaxial layer on a surface of a silicon wafer into which boron is doped at a high concentration, a doping amount (concentration) of germanium having a larger lattice constant than that of silicon is controlled to be in the range of the Formula 1; therefore, a warpage amount can be controlled to be smaller even in a large-diameter wafer having a diameter of 300 mm or larger.



BRIEF DESCRIPTION OF DRAWINGS
These and other objects and features of the present invention will become clearer from the following description of the preferred embodiments given with reference to the attached drawings, in which:
FIG. 1 is a sectional view of a silicon epitaxial wafer according to an embodiment of the present invention; and
FIG. 2 is a sectional view for explaining a warpage amount of the silicon epitaxial wafer shown in FIG. 1.



DESCRIPTION OF THE PREFERRED EMBODIMENT
Below, an embodiment of the present invention will be explained based on the drawings.
A silicon epitaxial wafer of the present embodiment is, as shown in FIG. 1, formed by growing a silicon epitaxial layer 2 on a surface of a silicon wafer 1. The silicon wafer 1 is obtained by slicing a silicon single crystal ingot grown by the Czochralski method and, during growing the ingot, boron and germanium are added to silicon melt. Boron is doped to attain a boron concentration of 8.5×1018 (atoms/cm3) or higher and germanium is doped to attain a concentration range of satisfying the above Formula 1.
The silicon wafer of the present embodiment has a large diameter of at least 300 mm and, in particular, has a crystal orientation of (110).
Next, an explanation will be made on the above Formula 1.
As shown in FIG. 2, when there is a thin film on a wafer, distortion ε in the film is given by the formula (2) below. Note that an initial wafer warpage amount δ is assumed to be 0. Namely, it is to obtain a change of a warpage amount before and after growing an epitaxial layer.
In the Formula (2), tsi indicates a thickness of a wafer, tepi a thickness of an epitaxial layer, δ a warpage amount of the wafer, and “r” a radius of the wafer.




  
    
      
        ɛ
        =
        
          
            1
            3
          
          ⁢
          
            (
            
              
                t
                si
                2
              
              
                t
                epi
              
            
            )
          
          ⁢
          
            (
            
              δ
              
                r
                2
              
            
            )
          
        
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          2
        
        ]
      
    
  




Also, a distortion e due to a lattice constant difference between p+ and p− layers is obtained by the Formula (3) below. Here, ΔαSi—B—Ge is a lattice constant difference between p+ crystal containing [B] and [Ge] and p− crystal without any doping, and αSi is a lattice constant of the p− crystal.




  
    
      
        
          
            
              ɛ
              =
              
              ⁢
              
                
                  Δα
                  
                    si
                    ⁢
                    
                      -
                    
                    ⁢
                    B
                    ⁢
                    
                      -
                    
                    ⁢
                    Ge
                  
                
                
                  α
                  si
                
              
            
          
        
        
          
            
              =
              
              ⁢
              
                
                  
                    4.64
                    ×
                    
                      10
                      
                        -
                        24
                      
                    
                    ×
                    
                      [
                      Ge
                      ]
                    
                  
                  -
                  
                    2.69
                    ×
                    
                      10
                      
                        -
                        23
                      
                    
                    ×
                    
                      [
                      B
                      ]
                    
                  
                
                5.43
              
            
          
        
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          3
        
        ]
      
    
  




Note that ΔαSi—B—Ge is obtained as explained below. Namely, a lattice constant change (ΔαSi—B, the unit is angstrom) due to a change of a boron concentration is calculated by the formula (Vegard's Law) below.

ΔαSi—B=αSi×(rB−rSi)/rSi×[B]/[Si]  [Formula 4]

In the formula 4, rSi indicates a radius of a silicon (Si) atom, rB a radius of a boron (B) atom, [B] a boron concentration, and [Si] a silicon concentration. The radius of a silicon atom is 1.17 angstroms, and the radius of a boron atom is 0.88 angstrom. A lattice constant of a high purity silicon crystal (αSi) is 5.43 angstroms. A Si atom density of a silicon single crystal is 5.0×1022 atoms/cm3.
Consequently, the formula (4) becomes a formula (5) below.

ΔαSi—B=−2.69×10−23×[B]  [Formula 5]

As is obvious from the formula (5), in the case of a silicon wafer doped with boron at a high concentration, the lattice constant becomes smaller comparing with that in the case of not adding any boron.

On the other hand, a lattice constant change in the case of doping germanium (ΔαSi—Ge, the unit is angstrom) is also calculated in the same way by using the Vegard's Law.

ΔαSi—Ge=αSi×(rGe−rSi)/rSi×[Ge]/[Si]  [Formula 6]

Here, rGe is a radius of a germanium atom, which is 1.22 angstroms, and [Ge] is a germanium concentration. Accordingly, the formula (6) can be expressed as a formula (7) below.

ΔαSi—Ge=4.64×10−24   [Formula 7]

Accordingly, the lattice constant becomes larger by adding germanium when comparing with that in the case of not adding any germanium.

From the above, a lattice constant change in the case of adding boron and germanium at the same time (ΔαSi—Ge—B, the unit is angstrom) is obtained from a sum of the formula (5) and formula (7).

ΔαSi—Ge—B=ΔαSi—Ge+ΔαSi—B=4.64×10−24×[Ge]−2.69×10−23×[B]  [Formula 8]

This ΔαSi—Ge—B above is the numerator in the formula (3), and the lattice constant of high purity silicon crystal (αSi) is 5.43 angstroms as explained above, therefore, the formula (3) can be solved.
Then, by eliminating ε from the formula (2) and formula (3), it is possible to obtain a relationship of δ, [B], tSi, tepi and r. Namely,




  
    
      
        
          
          
            3
            ×
            
              
                (
                
                  
                    
                      
                        
                          4.64
                          ×
                          
                            
                              10
                              
                                -
                                24
                              
                            
                            ·
                            
                              [
                              Ge
                              ]
                            
                          
                        
                        -
                      
                    
                  
                  
                    
                      
                        2.69
                        ×
                        
                          
                            10
                            
                              -
                              23
                            
                          
                          ·
                          
                            [
                            B
                            ]
                          
                        
                      
                    
                  
                
                )
              
              5.43
            
            ×
            
              r
              2
            
            ×
            
              
                t
                epi
              
              
                
                  (
                  
                    t
                    sub
                  
                  )
                
                2
              
            
          
          
        
        =
        δ
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          9
        
        ]
      
    
  




from the formula (9), it is known that a warpage amount of the p/p+ epitaxial wafer due to the epitaxial growth is proportional to a boron concentration, epitaxial layer thickness and a square of a wafer diameter and is in inverse proportion to a square of a wafer thickness.

As below, it was confirmed that a warpage amount of a wafer didn't exceed 18 μm when growing a silicon epitaxial layer to be in a range of 2.75 to 20 μm on a surface of a silicon wafer having a diameter of at least 300 mm produced by slicing a silicon single crystal ingot grown by the Czochralski method, doped to have a boron concentration of at least 8.5×1018 (atoms/cm3) and doped with germanium in a range of satisfying the formula (1).
EXAMPLE 1
When growing a silicon single crystal ingot having a crystal orientation of (110) by the CZ method, silicon melt was doped with boron and germanium, so that the boron concentration becomes 2.01×1019 atoms/cm3 and the germanium concentration becomes 2.03×1019 atoms/cm3. Then, the ingot was sliced to produce a wafer having a diameter of 300 mm and a thickness of 774 μm.
The 300 mm-diameter wafer was placed in an epitaxial growth apparatus, hydrogen baking at 1150° C. was performed, then, a SiHCl3 gas was supplied under a condition of 1075° C. in the epitaxial growth apparatus to grow an epitaxial layer having a thickness of 2.75 μm on a surface of the wafer and a p/p+ silicon epitaxial wafer was obtained.
A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
EXAMPLE 2
Other than changing the boron concentration of doping in the silicon melt to 1.98×1019 atom s/cm3, the germanium concentration to 1.01×1020 atoms/cm3, the wafer thickness to 775 μm and the thickness of the epitaxial layer to 6 μm, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
EXAMPLE 3
Other than changing the boron concentration of doping in the silicon melt to 1.21×1019 atom s/cm3, the germanium concentration to 9.00×1018 atoms/cm3 and the thickness of the epitaxial layer to 4 μm, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
EXAMPLE 4
Other than changing the boron concentration of doping in the silicon melt to 1.21×1019 atom s/cm3, the germanium concentration to 4.03×1019 atoms/cm3, the wafer thickness to 775 μm and the thickness of the epitaxial layer to 6 μm, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
EXAMPLE 5
Other than changing the boron concentration of doping in the silicon melt to 9.81×1018 atom s/cm3, the germanium concentration to 2.01×1019 atoms/cm3, the wafer thickness to 775 μm and the thickness of the epitaxial layer to 6 μm, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
EXAMPLE 6
Other than changing the boron concentration of doping in the silicon melt to 1.95×1019 atom s/cm3, the germanium concentration to 1.01×1020 atoms/cm3, the wafer thickness to 775 μm and the thickness of the epitaxial layer to 20 μm, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
COMPARATIVE EXAMPLE 1
As a comparative example of the Example 1, other than changing the boron concentration of doping in the silicon melt to 2.02×1019 atom s/cm3 and the wafer thickness to 773 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 2
As a comparative example of the Example 3, other than changing the boron concentration of doping in the silicon melt to 2.01×1019 atom s/cm3 and the wafer thickness to 775 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 3. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 3
As a comparative example of the Example 2, other than changing the boron concentration of doping in the silicon melt to 1.90×1019 atom s/cm3 and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 2. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 4
As a comparative example of the Example 2, other than changing the boron concentration of doping in the silicon melt to 2.01×1019 atom s/cm3 and the germanium concentration to 3.04×1019 atoms/cm3, a silicon epitaxial wafer was produced under the same condition as that in the Example 2. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
COMPARATIVE EXAMPLE 5
As a comparative example of the Example 3, other than changing the boron concentration of doping in the silicon melt to 1.23×1019 atom s/cm3 and the wafer thickness to 775 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 3. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 6
As a comparative example of the Example 4, other than changing the boron concentration of doping in the silicon melt to 1.20×1019 atom s/cm3 and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 4. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 7
As a comparative example of the Example 5, other than changing the boron concentration of doping in the silicon melt to 9.70×1018 atom s/cm3 and the wafer thickness to 774 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 5. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
COMPARATIVE EXAMPLE 8
As a comparative example of the Example 5, other than changing the germanium concentration to 2.10×1018 atoms/cm3, a silicon epitaxial wafer was produced under the same condition as that in the Example 5. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1. A calculated value of the left-hand side of the formula (1) above is also shown in Table 1.
REFERENCE EXAMPLE 1
As a reference example of the Example 1, other than changing the wafer diameter to 200 mm, the wafer thickness to 723 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
REFERENCE EXAMPLE 2
As a reference example of the Example 3, other than changing the wafer diameter to 200 mm, the boron concentration of doping in the silicon melt to 1.80×1019 atom s/cm3 and the wafer thickness to 726 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 3. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
REFERENCE EXAMPLE 3
As a reference example of the Example 2, other than changing the wafer diameter to 200 mm, the wafer thickness to 721 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 2. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
REFERENCE EXAMPLE 4
As a reference example of the Example 1, other than changing the boron concentration of doping in the silicon melt to 1.20×1019 atom s/cm3 and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.
REFERENCE EXAMPLE 5
As a reference example of the Example 1, other than changing the boron concentration of doping in the silicon melt to 9.70×1018 atom s/cm3, the thickness of the epitaxial layer to 2.27 μm and not doping any germanium, a silicon epitaxial wafer was produced under the same condition as that in the Example 1. A measurement of warpage of the silicon epitaxial wafer was made before and after the epitaxial growth, and an absolute value of a change of the warpage amount was calculated. The result is shown in Table 1.















TABLE 1












Warpage Amount








Epitaxial
Change Before



Wafer
Boron
Germanium
Wafer
Film
and After
Calculated Value



Diameter
Concentration of
Concentration of
Thickness
Thickness
Epitaxial Film
of Left-Hand



(mm)
Wafer (atoms/cc)
Wafer (atomc/cc)
(μm)
(μm)
Growth (μm)
Side of Formula 1























Example 1
300
2.01 × 1019
2.03 × 1019
774
2.75
17.1
25.6


Example 2
300
1.98 × 1019
1.01 × 1020
775
6
5.7
9


Example 3
300
1.21 × 1019
9.00 × 1018
774
4
13.4
23.9


Example 4
300
1.21 × 1019
4.03 × 1019
775
6
6.5
17.2


Example 5
300
9.81 × 1018
2.01 × 1019
775
6
10.7
20.9


Example 6
300
1.95 × 1019
1.01 × 1020
775
20
17.8
23.2


Comparative Example 1
300
2.02 × 1019
—
773
2.75
22.8
—


Comparative Example 2
300
2.01 × 1019
—
775
4
28.3
—


Comparative Example 3
300
1.90 × 1019
—
775
6
35.1
—


Comparative Example 4
300
2.01 × 1019
3.04 × 1019
775
6
28.6
47.6


Comparative Example 5
300
1.23 × 1019
—
775
4
22.7
—


Comparative Example 6
300
1.20 × 1019
—
775
6
29.2
—


Comparative Example 7
300
9.70 × 1018
—
774
6
21.8
—


Comparative Example 8
300
9.81 × 1018
2.10 × 1018
775
6
21.3
31.3


Reference Example 1
200
2.01 × 1019
—
723
2.75
7.8
—


Reference Example 2
200
1.80 × 1019
—
726
4
11.2
—


Reference Example 3
200
1.98 × 1019
—
721
6
17.5
—


Reference Example 4
300
1.20 × 1019
—
774
2.75
12
—


Reference Example 5
300
9.70 × 1018
—
774
2.27
8.5
—









Consideration
As shown in the Examples 1 to 6, in the 300 mm epitaxial wafers wherein an epitaxial layer is grown on wafers having a germanium concentration satisfying the formula (1), changes of the warpage amounts were preferable as 17.8 μm at maximum.
On the other hand, as the Comparative Examples 1 to 8 exhibit, in wafers without doping any germanium or wafers doped with germanium at a concentration being out of the formula (1), changes of the warpage amounts were 21.31 μm at minimum.
Note that, as in the Reference Examples 1 to 3, wafers having a small diameter of 200 mm do dot exhibit large changes in the warpage amount. Also, as in the Reference Examples 4 and 5, changes of the warpage amounts are not large in those having a thin epitaxial layer.
The embodiments explained above are for easier understanding of the present invention and not to limit the present invention. Accordingly, respective elements disclosed in the above embodiments include all modifications in designs and equivalents belonging to the technical field of the present invention.
Explanation of References

    1 . . . silicon wafer
    2 . . . silicon epitaxial layer

## Claims

1. A silicon epitaxial wafer, obtained by growing a silicon epitaxial layer on a surface of a silicon wafer having a diameter of at least 300 mm produced by slicing a silicon single crystal ingot doped with boron and germanium grown by the Czochralski method, wherein
boron is doped to be at a concentration of 8.5×1018 (atoms/cm3) or higher, and
germanium is doped to satisfy a relational expression (formula 1) below:





  
    
      
        
          
          
            3
            ×
            
              
                (
                
                  
                    
                      
                        
                          4.64
                          ×
                          
                            
                              10
                              
                                -
                                24
                              
                            
                            ·
                            
                              [
                              Ge
                              ]
                            
                          
                        
                        -
                      
                    
                  
                  
                    
                      
                        2.69
                        ×
                        
                          
                            10
                            
                              -
                              23
                            
                          
                          ·
                          
                            [
                            B
                            ]
                          
                        
                      
                    
                  
                
                )
              
              5.43
            
            ×
            
              r
              2
            
            ×
            
              
                t
                epi
              
              
                
                  (
                  
                    t
                    sub
                  
                  )
                
                2
              
            
          
          
        
        ≤
        26.
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          1
        
        ]

2. The silicon epitaxial wafer as set forth in claim 1, wherein a crystal orientation of the silicon wafer is (110).

3. The silicon epitaxial wafer as set forth in claim 1, wherein a thickness of the silicon epitaxial layer is in the range from 4 μm through 20 μm.

4. The silicon epitaxial wafer as set forth in claim 2, wherein a thickness of the silicon epitaxial layer is in the range from 4 μm through 20 μm.

5. A production method of a silicon epitaxial wafer, comprising the steps of:
growing a silicon single crystal ingot added with boron and germanium by the Czochralski method;
producing a silicon wafer having a diameter of at least 300 mm by slicing the ingot; and
growing an epitaxial layer on a surface of the silicon wafer;
wherein
the silicon wafer is doped to have a boron concentration of 8.5×1018 (atoms/cm3) or higher; and
germanium is doped to satisfy a relational expression (formula 1) below:






  
    
      
        
          
          
            3
            ×
            
              
                (
                
                  
                    
                      
                        
                          4.64
                          ×
                          
                            
                              10
                              
                                -
                                24
                              
                            
                            ·
                            
                              [
                              Ge
                              ]
                            
                          
                        
                        -
                      
                    
                  
                  
                    
                      
                        2.69
                        ×
                        
                          
                            10
                            
                              -
                              23
                            
                          
                          ·
                          
                            [
                            B
                            ]
                          
                        
                      
                    
                  
                
                )
              
              5.43
            
            ×
            
              r
              2
            
            ×
            
              
                t
                epi
              
              
                
                  (
                  
                    t
                    sub
                  
                  )
                
                2
              
            
          
          
        
        ≤
        26.
      
    
    
      
        [
        
          Formula
          ⁢
          
            
          
          ⁢
          1
        
        ]

6. The production method of a silicon epitaxial wafer as set forth in claim 5, wherein a crystal orientation of the silicon wafer is (110).

7. The production method of a silicon epitaxial wafer as set forth in claim 5, wherein a thickness of the silicon epitaxial layer is in the range from 4μm through 20 μm.

8. The production method of a silicon epitaxial wafer as set forth in claim 6, wherein a thickness of the silicon epitaxial layer is in the range from 4 μm through 20 μm.