# Patent

## Title
Diacetylenic materials for sensing applications

## Abstract

Diacetylenic materials for the colorimetric detection of an analyte or exposure to certain environmental factors are disclosed as well as the polymerization reaction products of these diacetylenic compounds.

## Background
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a division of U.S. patent application Ser. No. 10/325,276, filed Dec. 19, 2002 now U.S. Pat. No. 6,963,007.


FIELD OF THE INVENTION
This invention relates to diacetylenic materials for the colorimetric detection of an analyte or exposure to certain environmental factors. In addition, the invention relates to the polymerization reaction products of at least one of the diacetylenic compounds disclosed herein.
BACKGROUND OF THE INVENTION
Various circumstances require that exposure to certain environmental factors, such as heat and ultraviolet (UV) light be monitored and recorded. For example, the need to know whether a product has been exposed either to an undesirable time-temperature history, which results in substantial degradation, or to a correct time-temperature history required during processing is frequently required. This applies, for example, to frozen foods, pharmaceuticals or photographic films that may be exposed to undesirable high temperatures for significant time periods during storage and distribution. Additionally, exposure to the ultraviolet radiation of sunlight can cause rapid aging and hardening of the skin and can cause DNA damage, which can lead to skin cancer or other cellular proliferative diseases.
Diacetylenes are typically colorless and undergo addition polymerization, either thermally or by actinic radiation. As the polymerization proceeds, these compounds undergo a contrasting color change to blue or purple. Utilization of this class of compounds is known for use as time-temperature history indicators, thermochromic indicating materials and as radiation-dosage indicators.
Efforts continue, however, to make sensing devices employing diacetylenes more accurate, more tailored to a given application, less complex and more available to non-technical personnel in a wide variety of environments. Devices, which can be conveniently transported and used individually for a particular application then discarded, are particularly desirable.
SUMMARY OF THE INVENTION
The present invention relates to compounds of the formula




where R1 is




R2 is




R3, R8, R13, R24, R31 and R33 are independently alkyl; R4, R5, R7, R14, R16, R19, R20, R22, R25, and R32 are independently alkylene; R6, R15, R18, and R26 are independently alkylene, alkenylene, or arylene; R9 is alkylene or —NR34—; R10, R12, R27, and R29 are independently alkylene or alkylene-arylene; R11 and R28 are independently alkynyl; R17 is 2,5-dioxo-1-pyrrolidinyl; R21 is alkylamino or alkyl; R23 is arylene; R30 is alkylene or —NR36—; R34, and R36 are independently H or C1-C4 alkyl; p is 1-5; and n is 1-20; and where R1 and R2 are not the same.
Also provided is a method for the detection of electromagnetic radiation in the ultraviolet range of the electromagnetic spectrum comprising contacting at least one compound described above with electromagnetic radiation in the ultraviolet range of the electromagnetic spectrum and observing a color change.
Also provided is a polymerized composition including the polymerization reaction product of at least one compound described above.
Also provided is a method for the detection of thermal radiation including contacting a polymerized composition described above with thermal radiation and observing a color change.
The above summary of the present invention is not intended to describe each disclosed embodiment or every implementation of the present invention. The detailed description that follows more particularly exemplifies these embodiments.


DETAILED DESCRIPTION
The present invention provides for diacetylenic materials. In particular, the present invention is directed to diacetylenic materials for the colorimetric detection of an analyte or exposure to certain environmental factors. While the present invention is not so limited, an appreciation of various aspects of the invention will be gained through a discussion of the examples provided below.
All numbers are herein assumed to be modified by the term “about.”
The recitation of numerical ranges by endpoints includes all numbers subsumed within that range (e.g. 1 to 5 includes 1, 1.5, 2, 2.75, 3, 3.80, 4, and 5).
For the following defined terms, these definitions shall be applied, unless a different definition is given in the claims or elsewhere in this specification.
As used herein, the term “alkyl” refers to a straight or branched chain or cyclic monovalent hydrocarbon radical having a specified number of carbon atoms. Alkyl groups include those with one to twenty carbon atoms. Examples of “alkyl” as used herein include, but are not limited to, methyl, ethyl, n-propyl, n-butyl, n-pentyl, isobutyl, and isopropyl, and the like. It is to be understood that where cyclic moieties are intended, at least three carbons in said alkyl must be present. Such cyclic moieties include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl and cycloheptyl.
As used herein, the term “alkylene” refers to a straight or branched chain or cyclic divalent hydrocarbon radical having a specified number of carbon atoms. Alkylene groups include those with one to fourteen carbon atoms. Examples of “alkylene” as used herein include, but are not limited to, methylene, ethylene, trimethylene, tetramethylene and the like. It is to be understood that where cyclic moieties are intended, at least three carbons in said alkylene must be present. Such cyclic moieties include cyclopropylene, cyclobutylene, cyclopentylene, cyclohexylene and cycloheptylene.
As used herein, the term “alkenylene” refers to a straight or branched chain or cyclic divalent hydrocarbon radical having a specified number of carbon atoms and one or more carbon-carbon double bonds. Alkenylene groups include those with two to eight carbon atoms. Examples of “alkenylene” as used herein include, but are not limited to, ethene-1,2-diyl, propene-1,3-diyl, and the like.
As used herein, the term “arylene” refers to divalent unsaturated aromatic carboxylic radicals having a single ring, such as phenylene, or multiple condensed rings, such as naphthylene or anthrylene. Arylene groups include those with six to thirteen carbon atoms. Examples of “arylene” as used herein include, but are not limited to, benzene-1,2-diyl, benzene-1,3-diyl, benzene-1,4-diyl, naphthalene-1,8-diyl, and the like.
As used herein, the term “alkylene-arylene”, refers to an alkylene moiety as defined above bonded to an arylene moiety as defined above. Examples of “alkylene-arylene” as used herein include, but are not limited to, —CH2-phenylene, —CH2CH2-phenylene, and —CH2CH2CH2-phenylene.
As used herein, the term “alkynyl” refers to a straight or branched chain or cyclic monovalent hydrocarbon radical having from two to thirty carbons and at least one carbon-carbon triple bond. Examples of “alkynyl” as used herein include, but are not limited to, ethynyl, propynyl and butynyl.
As used herein, the term “alkylamino” means alkyl group defined as above bonded to a primary, secondary or tertiary amino group, or salts thereof. Examples of “alkylamino” as used herein include, but are not limited to, —(CH2)1-15—NH3, and —(CH2)1-15—N(CH3)3.
The present invention provides compounds of the formula




where R1 is




R2 is




R3, R8, R13R24, R31 and R33 are independently alkyl; R4, R5, R7, R14, R16, R19, R20, R22, R25, and R32 are independently alkylene; R6, R15, R18, and R26 are independently alkylene, alkenylene, or arylene; R9 is alkylene or —NR34—; R10, R12, R27, and R29 are independently alkylene or alkylene-arylene; R11 and R28 are independently alkynyl; R17 is 2,5-dioxo-1-pyrrolidinyl; R21 is alkylamino or alkyl; R23 is arylene; R30 is alkylene or —NR36—; R34, and R36 are independently H or C1-C4 alkyl; p is 1-5; and n is 1-20; and where R1 and R2 are not the same.
Examples of R1 when R1 is alkyl include C1-C20 alkyl, C6-C18 alkyl, and C12-C16 alkyl. Additional examples of R1 when R1 is alkyl include dodecyl and hexadecyl.
Examples of R2 when R2 is alkylamino include C1-C20 alkylamino, C6-C18 alkylamino, and C11-C16 alkylamino. Additional examples of R2 when R2 is alkylamino include (C1-C18 alkyl)-NR353X, where R35 is H or C1-C4 alkyl, such as methyl, for example, and X is a suitable counterion, such as F−, Br−, Cl−, I−, OH−, N3−, HCO3−, or CN−, for example. Further examples of R2 when R2 is alkylamino include —(CH2)11—NH3X, where X is defined as above, —(CH2)11—N(CH3)3X, where X is defined above, —(CH2)15—N(CH3)3X, where X is defined above, and —(CH2)15—NH3X, where X is defined above.
Examples of R3 include C1-C20 alkyl, and C6-C18 alkyl. Additional examples of R3 include undecyl and pentadecyl.
Examples of R4 include C1-C14 alkylene, and C1-C4 alkylene. Additional examples of R4 include methylene (—CH2—), trimethylene, (—CH2CH2CH2—), and tetramethylene (—CH2CH2 CH2CH2—).
Examples of R5 include C1-C14 alkylene, and C1-C3 alkylene. Additional examples of R5 include ethylene (—CH2CH2—), and trimethylene (—CH2CH2CH2—).
Examples of R6 when R6 is alkylene include C1-C14 alkylene, and C1-C3 alkylene. Additional examples of R6 when R6 is alkylene include ethylene (—CH2CH2—), and trimethylene (—CH2CH2CH2—). Examples of R6 when R6 is alkenylene include C2-C8 alkenylene, and C2-C4 alkenylene. An additional example of R6 when R6 is alkenylene includes ethenylene (—C═C—). Examples of R6 when R6 is arylene include C6-C13 arylene, and phenylene. An additional example of R6 when R6 is arylene is benzene-1,2-diyl.
Examples of R7 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R7 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), hexamethylene (—CH2CH2CH2 CH2CH2CH2—), heptamethylene (—CH2CH2CH2CH2CH2CH2—), octamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2—), and nonamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2CH2—).
Examples of R8 include C1-C16 alkyl, and C1-C8 alkyl. Additional examples of R8 include butyl, pentyl and hexyl.
R9 is independently alkylene or —NR34—, where R34 is H or C1-C4 alkyl.
Examples of R9 when R9 is alkylene include C1-C14 alkylene, and C1-C3 alkylene, such as methylene (—CH2—) for example. Examples of R9 when R9 is —NR34— include —NH—, —N(CH2CH3)—, and —N(CH3)—.
Examples of R10 when R10 is alkylene include C1-C14 alkylene, and C1-C8 alkylene. Additional examples of R10 when R10 is alkylene include methylene (—CH2—), ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), —C(CH3)2—, and —CH((CH2)1-4CH3)—. Examples of R10 when R10 is alkylene-arylene include (C1-C14 alkylene)-arylene, and (C1-C14 alkylene)-phenylene. An additional example of R10 when R10 is alkylene-arylene includes —CH2-phenylene.
Examples of R11 include C2-C30 alkynyl, and C20-C25 alkynyl. Additional examples of R11 include C2-C30 alkynyl having at least two carbon-carbon triple bonds (—C≡C—), and C20-C25 alkynyl having at least two carbon-carbon triple bonds. Further examples of R11 include C22 alkynyl having at least two carbon-carbon triple bonds, C24 alkynyl having at least two carbon-carbon triple bonds. Yet further examples of R11 include —(CH2)8—C≡C—C≡C—(CH2)9CH3, and —(CH2)8—C≡C—C≡C—(CH2)11CH3.
Examples of R12 when R12 is alkylene include C1-C14 alkylene, and C1-C8 alkylene. Additional examples of R12 when R12 is alkylene include methylene (—CH2—), ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), —C(CH3)2—, and —CH((CH2)1-4CH3)—. Examples of R12 when R12 is alkylene-arylene include (C1-C14 alkylene)-arylene, and (C1-C14 alkylene)-phenylene. An additional example of R12 when R12 is alkylene-arylene includes —CH2-phenylene.
Examples of R13 include C1-C4 alkyl, such as methyl for example.
Examples of R14 include C1-C4 alkylene, such as ethylene (—CH2CH2—) for example.
Examples of R15 when R15 is alkylene include C1-C14 alkylene, and C1-C3 alkylene. Additional examples of R15 when R15 is alkylene include ethylene (—CH2CH2—), and trimethylene (—CH2CH2CH2—). Examples of R15 when R15 is alkenylene include C2-C8 alkenylene, and C2-C4 alkenylene. An additional example of R15 when R15 is alkenylene includes ethenylene (—C═C—). Examples of R15 when R15 is arylene include C6-C13 arylene, and phenylene. An additional example of R15 when R15 is arylene is benzene-1,4-diyl.
Examples of R16 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R16 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), hexamethylene (—CH2CH2CH2 CH2CH2CH2—), heptamethylene (—CH2CH2CH2CH2CH2CH2—), octamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2—), and nonamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2CH2—).
Examples of R17 include groups that activate the neighboring ester group toward acyl transfer. Such ester activating groups include pentafluorophenol, pentachlorophenol, 2, 4, 6-trichlorophenol, 3-nitrophenol, N-hydroxysuccinimide, N-hydroxyphthalimide and those disclosed in M. Bodanszky, “Principles of Peptide Synthesis,” (Springer-Verlag, 1984), for example. An additional example of R17 is 2,5-dioxo-1-pyrrolidinyl.
Examples of R18 when R18 is alkylene include C1-C14 alkylene, and C1-C3 alkylene. Additional examples of R18 when R18 is alkylene include ethylene (—CH2CH2—), and trimethylene (—CH2CH2CH2—). Examples of R18 when R18 is alkenylene include C2-C8 alkenylene, and C2-C4 alkenylene. An additional example of R18 when R18 is alkenylene includes ethenylene (—C═C—). Examples of R18 when R18 is arylene include C6-C13 arylene, and phenylene. An additional example of R18 when R18 is arylene is benzene-1,2-diyl.
Examples of R19 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R19 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), hexamethylene (—CH2CH2CH2 CH2CH2CH2—), heptamethylene (—CH2CH2CH2CH2CH2CH2—), octamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2—), and nonamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2CH2—).
Examples of R20 include C1-C14 alkylene, C1-C9 alkylene, and C1-C4 alkylene. Additional examples of R20 include methylene (—CH2—), ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), hexamethylene (—CH2CH2CH2 CH2CH2CH2—), heptamethylene (—CH2CH2CH2CH2CH2CH2—), octamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2—), and nonamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2CH2—).
Examples of R21 when R21 is alkylamino include C1-C20 alkylamino, C6-C18 alkylamino, and C11-C16 alkylamino. Additional examples of R21 when R21 is alkylamino include (C1-C18 alkyl)—NR353X, where R35 is H or C1-C4 alkyl, such as methyl, for example, and X is a suitable counterion, such as F−, Br−, Cl−, I−, OH−, N3−, HCO3−, and CN−, for example. Further examples of R21 when R21 is alkylamino include —(CH2)10—NH3X, where X is defined as above, —(CH2)10—N(CH3)3X, where X is defined above, —(CH2)14—N(CH3)3X, where X is defined above, and —(CH2)14—NH3X, where X is defined above. Examples of R21 when R21 is alkyl include C1-C20 alkyl, C6-C18 alkyl, and C10-C17 alkyl. Additional examples of R21 when R21 is alkyl include decyl, undecyl, tridecyl, tetradecyl, pentadecyl, heptadecyl.
Examples of R22 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R22 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), and tetramethylene.
Examples of R23 include C6-C13 arylene, and phenylene. An additional example of R23 when R23 is arylene is benzene-1,4-diyl.
Examples of R24 include C1-C20 alkyl, and C6-C18 alkyl. Additional examples of R24 include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, and dodecyl.
Examples of R25 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R25 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), hexamethylene (—CH2CH2CH2 CH2CH2CH2—), heptamethylene (—CH2CH2CH2CH2CH2CH2—), octamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2—), and nonamethylene (—CH2CH2CH2CH2CH2CH2CH2CH2CH2—).
Examples of R26 when R26 is alkylene include C1-C14 alkylene, and C1-C3 alkylene. Additional examples of R26 when R26 is alkylene include ethylene (—CH2CH2—), and trimethylene (—CH2CH2CH2—). Examples of R26 when R26 is alkenylene include C2-C8 alkenylene, and C2-C4 alkenylene. An additional example of R26 when R26 is alkenylene includes ethenylene (—C═C—). Examples of R26 when R26 is arylene include C6-C13 arylene, and phenylene. An additional example of R26 when R26 is arylene is benzene-1,2-diyl.
Examples of R27 when R27 is alkylene include C1-C14 alkylene, and C1-C8 alkylene. Additional examples of R27 when R27 is alkylene include methylene (—CH2—), ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), —C(CH3)2—, and —CH((CH2)1-4CH3)—. Examples of R27 when R27 is alkylene-arylene include (C1-C14 alkylene)-arylene, and (C1-C14 alkylene)-phenylene. An additional example of R27 when R27 is alkylene-arylene includes —CH2-phenylene.
Examples of R28 include C2-C30 alkynyl, and C20-C25 alkynyl. Additional examples of R28 include C2-C30 alkynyl having at least two carbon-carbon triple bonds (—C≡C—), and C20-C25 alkynyl having at least two carbon-carbon triple bonds. Further examples of R28 include C22 alkynyl having at least two carbon-carbon triple bonds, C24 alkynyl having at least two carbon-carbon triple bonds. Yet further examples of R28 include —(CH2)8—C≡C—C═C—(CH2)9CH3, and —(CH2)8—C≡C—C≡C—(CH2)11CH3.
Examples of R29 when R29 is alkylene include C1-C14 alkylene, and C1-C8 alkylene. Additional examples of R29 when R29 is alkylene include methylene (—CH2—), ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), —C(CH3)2—, and —CH((CH2)1-4CH3)—. Examples of R29 when R29 is alkylene-arylene include (C1-C14 alkylene)-arylene, and (C1-C14 alkylene)-phenylene. An additional example of R29 when R29 is alkylene-arylene includes —CH2-phenylene.
R30 is independently alkylene or —NR36—, where R36 is H or C1-C4 alkyl.
Examples of R30 when R30 is alkylene include C1-C14 alkylene, and C1-C3 alkylene, such as methylene (—CH2—) for example. Examples of R30 when R30 is —NR36— include —NH, —N(CH2CH3)—, and —N(CH3)—.
Examples of R31 include C1-C16 alkyl, and C1-C8 alkyl. Additional examples of R31 include butyl, pentyl and hexyl.
Examples of R32 include C1-C14 alkylene, and C2-C9 alkylene. Additional examples of R32 include ethylene (—CH2CH2—), trimethylene (—CH2CH2CH2—), tetramethylene (—CH2CH2 CH2CH2—), pentamethylene (—CH2CH2CH2CH2CH2—), and hexamethylene (—CH2CH2CH2 CH2CH2CH2—).
Examples of R33 include C1-C20 alkyl, C6-C18 alkyl, and C10-C16 alkyl. Additional examples of R33 include dodecyl, tetradecyl, hexadecyl, and octadecyl.
Compounds of the present invention also include those where p can be 1 or 2 and n can be 1-20, 3-17, 6-14, or 9-11.
The invention is inclusive of the compounds described herein including isomers, such as structural isomers and geometric isomers, salts, solvates, polymorphs and the like.
The synthesis of the diacetylenic materials disclosed herein are adapted form published procedures such as those in Xu, Z.; Byun, H. S.; Bittman, R.; J. Org. Chem., 1991, 56, 7183-7186. For example, the diacetylenes the formula I can be prepared as shown in Scheme 1 where n is typically 1 to 14. Compounds of the formula I can be prepared from compounds of the formula II via anion exchange with an anion exchange resin, such as “Dowex” anion exchange resin (available from Aldrich Chemical, Milwaukee, Wis.) for example, and a suitable eluent, such as aqueous sodium chloride for example.




Compounds of formula II can be prepared from compounds of formula III by reaction with an appropriate alkylating agent in a suitable solvent. Suitable methylating agents include methyl iodide for example and suitable solvents include acetonitrile. The aforesaid reaction is run for a period of time from 1 hour to 96 hours, generally 20 hours, at a temperature from 20° C. to 70° C., generally from 20° C. to 50° C., in the presence of a base such as sodium carbonate for example.
Compounds of formula III can be prepared from compounds of formula IV by reaction with an appropriate reducing agent in a suitable solvent followed by protonation via a suitable acid to afford the salt. Suitable reducing agents include lithium aluminum hydride, sodium borohydride, and triphenylphosphine, for example. Suitable solvents include ether, tetrahydrofuran, dichloromethane, chloroform, and mixtures of these solvents with water, for example. Suitable acids include mineral acids such as HCl for example. The aforesaid reaction is run for a period of time from 1 hour to 96 hours, generally 20 hours, at a temperature from 0° C. to 40° C., generally from 10° C. to 25° C.
Compounds of formula IV can be prepared from compounds of formula VI via compounds of formula V. A compound of formula VI is reacted with a reagent suitable for the desilylation of a protected hydroxyl group in the presence of a suitable solvent. Such deprotecting reagents include tetrabutylammonium fluoride and those described in Greene and Wuts, “Protecting Groups in Organic Synthesis,” (John Wiley & Son Press, 2nd Ed), for example. Suitable solvents include ether, tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is run for a period of time from 0.5 hours to 5 hours, generally 1 hour, at a temperature from 0° C. to 40° C., generally from 10° C. to 25° C. The unpurified deprotected alcohol V is then reacted with a sulfonyl halide in the presence of a solvent. Suitable sulfonyl halides include methanesulfonyl chloride or p-toluenesulfonyl chloride. The aforesaid reaction is typically run for a period of time from 0.5 hours to 5 hours, generally 2 hours, at a temperature from 0° C. to 40° C., generally from 10° C. to 25° C., in the presence of a base such as trialkylamine or pyridine base. The resulting unpurified sulfonyl derivative is then reacted with sodium azide in a suitable solvent such as DMF. The aforesaid reaction is typically run for a period of time from 1 hour to 48 hours, generally 20 hours, at a temperature from 20° C. to 100° C., generally from 70° C. to 90° C., in the presence of a base such as trialkylamine or pyridine base.
Compounds of formula VI can be prepared from compounds of formula VII by reaction with a suitable alkyl halide or alkyl tosylate in a suitable solvent. Useful haloalkanes include primary alkyl halides such as 1-bromooctane, 1-bromododecane or 1-bromohexadecane. Suitable solvents include tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 0.5 hours to 48 hours, generally 1 hour, at a temperature from −78° C. to 40° C., generally from −78° C. to −50° C., in the presence of a base such as an alkyl lithium base for example.
Compounds of formula VII can be prepared from compounds of formula VIII by reaction with a base such as an alkyl lithium base in a suitable solvent. Suitable alkyl lithium bases include methyl lithium. Suitable solvents include tetrahydrofuran, dichloromethane, and ether, for example. The aforesaid reaction is typically run for a period of time from 0.5 hours to 48 hours, generally 1 hour, at a temperature from −78° C. to 40° C., generally from −78° C. to −50° C. The resulting reaction mixture is then added to a solution of a suitable silyl protected hydroxy alkyl halide, such as those of formula IX for example, in a suitable solvent. Suitable solvents include tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 0.5 hours to 48 hours, generally 1 hour, at a temperature from −78° C. to 40° C., generally from −20° C. to 0° C. The resulting compound was then reacted with tetrabutylammonium fluoride in a suitable solvent. Suitable solvents include tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 0.5 hours to 48 hours, generally 20 hours, at a temperature from −78° C. to 40° C., generally from 0° C. to 25° C.
Silyl protected hydroxy alkyl halides, such as those of formula IX can be purchased commercially or prepared by reacting a suitable haloalcohol, such as those of formula X for example, with TBDMSCI in a suitable solvent. Suitable solvents include tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 0.5 hours to 48 hours, generally 1 hour, at a temperature from 0° C. to 40° C., generally from 10° C. to 25° C., in the presence of a base such as imidazole for example.
Diacetylenes of the Formula XVII can be prepared as outlined in Scheme 2 where n is typically 10 to 14, m is typically 1 to 4, and p is typically 10-14.




Compounds of formula XVII can be prepared from compounds of formula XVI by reaction with an appropriate reducing agent in a suitable solvent followed by protonation via a suitable acid to afford the salt. Suitable reducing agents include lithium aluminum hydride, sodium borohydride, and triphenylphosphine, for example. Suitable solvents include ether, tetrahydrofuran, dichloromethane, chloroform, and mixtures of these solvents with water, for example. Suitable acids include mineral acids such as HCl for example. The aforesaid reaction is run for a period of time from 1 hour to 96 hours, generally 20 hours, at a temperature from 0° C. to 40° C., generally from 10° C. to 25° C.
Compounds of formula XVI can be prepared from compounds of formula XV by reaction with a compound of formula XIII and a suitable acid chloride in the presence of a suitable solvent. Suitable compounds of formula XIII include any azido functionalized acid chloride that affords the desired product such as 11-azidoundecanoyl chloride for example. Suitable acid chlorides include any acid chloride that affords the desired product such as 1-undecanoyl chloride and 1-pentadecanoyl chloride for example. Suitable solvents include ether, tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 1 hour to 24 hours, generally 3 hours, at a temperature from 0° C. to 40° C., generally from 0° C. to 25° C., in the presence of a base such as trialkylamine or pyridine base.
Compounds of formula XV can be prepared via oxidative coupling of compounds of formula XIV by reaction with copper(I) chloride in the presence of a suitable solvent. Suitable solvents include alcohols such as methyl alcohol for example. The aforesaid reaction is typically run for a period of time from 24 hour to 72 hours, generally 48 hours, at a temperature from 0° C. to 40° C., generally from 0° C. to 25° C., in the presence of oxygen and a base such as pyridine.
Compounds of formula XIII can be prepared from compounds of formula XI via compounds of the formula XII as outlined in the Canadian Journal of Chemistry, 1999, 146-154. For example commercially available halogen derivatized carboxylic acids of the formula XI are reacted with sodium azide in the presence of a suitable solvent such as DMF. The aforesaid reaction is typically run for a period of time from 1 hour to 48 hours, generally 20 hours, at a temperature from 20° C. to 100° C., generally from 70° C. to 90° C. The unpurified azido derivatized carboxylic acid is then reacted with oxalyl chloride in the presence of a suitable solvent such as benzene for example. The aforesaid reaction is typically run for a period of time from 1 hour to 48 hours, generally 20 hours, at a temperature from 0° C. to 50° C., generally from 0° C. to 25° C.
Diacetylenes of the Formula XXIII can be prepared as outlined in Scheme 3 where n is typically 1 to 4 and m is typically 10 to 14.




Compounds of formula XXIII can be prepared via oxidation from compounds of formula XXII by reaction with a suitable oxidizing agent in a suitable solvent such as DMF for example. Suitable oxidizing agents include Jones reagent and pyridinium dichromate for example. The aforesaid reaction is typically run for a period of time from 1 hour to 48 hours, generally 8 hours, at a temperature from 0° C. to 40° C., generally from 0° C. to 25° C.
Compounds of formula XXII can be prepared from compounds of formula XXI by reaction with a suitable acid chloride. Suitable acid chlorides include any acid chloride that affords the desired product such as lauroyl chloride, 1-dodecanoyl chloride, 1-tetradecanoyl chloride, 1-hexadecanoyl chloride, and 1-octadecanoyl chloride for example. Suitable solvents include ether, tetrahydrofuran, dichloromethane, and chloroform, for example. The aforesaid reaction is typically run for a period of time from 1 hour to 24 hours, generally 3 hours, at a temperature from 0° C. to 40° C., generally from 0° C. to 25° C., in the presence of a base such as trialkylamine or pyridine base.
Compounds of formula XXI are either commercially available (e.g. where n is 1-4) or can be prepared from compounds of the formula XVIII via compounds XIX and XX as outlined in Scheme 3 and disclosed in Abrams, Suzanne R.; Shaw, Angela C. “Triple-bond isomerizations: 2- to 9-decyn-1-ol,” Org. Synth. (1988), 66 127-31 and Brandsma, L. “Preparative Acetylenic Chemistry,” (Elsevier Pub. Co.: New York, 1971), for example.
Diacetylenic compounds as disclosed herein can also be prepared by reacting compounds of formula XXII with an anhydride such as succinic, glutaric, or phthalic anhydride in the presence of a suitable solvents such as toluene. The aforesaid reaction is typically run for a period of time from 1 hour to 24 hours, generally 15 hours, at a temperature from 50° C. to 125° C., generally from 100° C. to 125° C.
The diacetylenic compounds as disclosed herein self assemble in solution to form ordered assemblies that can be polymerized using any actinic radiation such as, for example, electromagnetic radiation in the UV or visible range of the electromagnetic spectrum. Polymerization of the diacetylenic compounds disclosed herein result in polymerization reaction products that have a color in the visible spectrum less than 570 nm, between 570 nm and 600 nm, or greater than 600 nm depending on their conformation and exposure to external factors. Typically, polymerization of the diacetylenic compounds disclosed herein result in meta-stable blue phase polymer networks that include a polydiacetylene backbone. These meta-stable blue phase polymer networks undergo a color change from bluish to reddish-orange upon exposure to external factors such as heat, a change in solvent or counterion, if available, or physical stress for example. Polymerization products of some of the diacetylenic compounds disclosed herein can exhibit a reversible color change and/or a three state color change. For example, after polymerization the resulting blue-phase polymer network can change color to a reddish-orange state upon exposure to heat, a change in solvent or counterion, or physical stress. This reddish-orange polymer network can then change color to a yellowish-orange state upon further exposure to heat, a change in solvent or counterion, or physical stress. Additionally, polymer networks disclosed herein can cycle between these reddish-orange and yellowish-orange states in a reversible manner.
The ability of the diacetylenic compounds and their polymerization products disclosed herein to undergo a visible color change upon exposure to a variety of elements, including ultraviolet light, physical stress, a change in solvent and a change in counter ion, for example, make them ideal candidates for the preparation of various sensing devices. Such sensing devices can employ the diacetylenic compounds and their polymerization products disclosed herein in solution or in their solid state. For example, the diacetylenic compounds and their polymerization products disclosed herein can be used as ultraviolet light dosimeters to measure exposure to ultraviolet radiation. The diacetylenic compounds disclosed herein respond to UV-A, UV-B, and UV-C light in a manner similar to the human skin, thereby closely matching the erythemal response. Thus, such dosimeters could serve as a warning to a user against excessive solar UV exposure.
The structural requirements of diacetylenic molecule for a given sensing application are typically application specific. Features such as overall chain length, solubility, polarity, crystallinity, and the presence of functional groups for further molecular modification all cooperatively determine a diacetylenic molecule's ability to serve as a useful sensing material.
The diacetylenic compounds disclosed herein possess the capabilities described above and can be easily and efficiently polymerized into networks that undergo the desired color changes in response to heat, a change in solvent or counterion, if available, or physical stress. The diacetylenic compounds disclosed herein require mild conditions for the ordering of the compounds in solution. With respect to diacetylenic compounds of the present invention that include an ammonium moiety the use of high temperatures and high intensity probe sonication is not required. Additionally, the diacetylenic compounds disclosed herein allow for the incorporation of large excesses of unpolymerizable monomer while still forming a stable, polymerizable solution. The diacetylenic compounds disclosed herein can be synthesized in a rapid high-yielding fashion, including high-throughput methods of synthesis. The presence of functionality in the backbones of the diacetylenic compounds disclosed herein, such as heteroatoms for example, provides for the possibility of easy structural elaboration in order to meet the requirements of a given sensing application. The diacetylenic compounds disclosed herein can be polymerized into the desired polydiacetylene backbone containing network by adding the diacetylene to a suitable solvent, such as water for example, heating or sonicating the mixture, and then irradiating the solution with ultraviolet light, typically at a wavelength of 254 nm. Upon polymerization the solution undergoes a color change to bluish-purple.
EXAMPLES
The present invention should not be considered limited to the particular examples described below, but rather should be understood to cover all aspects of the invention as fairly set out in the attached claims. Various modifications, equivalent processes, as well as numerous structures to which the present invention may be applicable will be readily apparent to those of skill in the art to which the present invention is directed upon review of the instant specification. All parts, percentages, ratios, etc. in the examples and the rest of the specification are by weight unless indicated otherwise. All solvents and reagents without a named supplier were purchased from Aldrich Chemical; Milwaukee, Wis. Water was purified by the use of a UV Milli-Q water purifier with a resistivity of 18.2 Mohms/cm (Millipore Corp., Bedford, Mass.).










Table of Abbreviations








Abbreviation



or Trade Name
Description





11-Bromo-1-undecanol
Br(CH2)11OH Commercially available from



Aldrich Chemical; Milwaukee, WI


11-Bromoundecanoic
Br(CH2)10C(O)OH Commercially available


acid
from Aldrich Chemical; Milwaukee, WI


TBDMSC1
Tert-butyldimethylsilyl chloride



Commercially available from Aldrich



Chemical; Milwaukee, WI


Diyne-1
Bis(trimethylsilyl)butadiyne commercially



available from Gelest; Tullytown, PA


THF
Tetrahydrofuran


1-Bromododecane
Br(CH2)11CH3 Commercially available from



Aldrich Chemical; Milwaukee, WI


TBAF
Tetrabutylammonium fluoride Commercially



available from Aldrich Chemical; Milwaukee,



WI


HMPA
Hexamethylphosphoramide Commercially



vailable from Aldrich Chemical; Milwaukee,



WI


1-Bromohexadecane
Br(CH2)15CH3 Commercially available from



Aldrich Chemical; Milwaukee, WI


Methanesulfonyl chloride
Commercially available from Aldrich



Chemical; Milwaukee, WI


CH2Cl2
Dichloromethane


DMF
Dimethylformamide


oxalyl chloride
ClCOCOCl commercially available from



Aldrich Chemical, Milwaukee, WI


PDC
Pyridinium dichromate, commercially



available from Aldrich Chemical, Milwaukee,



WI


DMAP
4-(dimethylamino)pyridine, commercially



available from Aldrich Chemical, Milwaukee,



WI


KAPA
Potassium 3-aminopropylamide prepared



according to Abrams, S. R.; Shaw, A. C.



Organic Syntheses, 1988, 66, 127-131.









Example 1
Preparation of CH3(CH2)10CH2C≡C—C≡C(CH2)11NR3X
Step 1: Preparation of Br(CH2)11OSi(Me2(CMe3))
In a glass reaction vessel, a solution of 3.0 grams (12 mmol) 11-Bromo-1-undecanol in 40 milliliters CH2Cl2 was prepared and to this was added 2.7 grams (18 mmol) TBDMSCI and 1.2 grams (18 mmol) imidazole. The resulting mixture was stirred at room temperature for 18 h, and the reaction was worked up using dichloromethane and brine. The dichloromethane layer was dried (MgSO4), filtered, and concentrated to yield 4.5 grams of Br(CH2)11OSi(Me2(CMe3)).
Step 2: Preparation of HC≡C—C≡C(CH2)11OSi(Me2(CMe3))
In a glass reaction vessel, 710 milligrams (3.6 mmol) Diyne-1 was dissolved in 15 milliliters THF and cooled to −78° C. To this stirred solution was added 1 equivalent of methyl lithium (as complex with lithium bromide, 1.5 molar solution in Et2O). The mixture was stirred for 30 minutes and added via cannula to a −15° C. solution of 1.47 grams (4.0 mmol) Br(CH2)11OSi(Me2(CMe3)) in 8 milliliters HMPA and 16 milliliters THF. The resulting mixture was worked up using pentane and brine. The pentane layer was dried (MgSO4), filtered, and concentrated. To the resulting solid was added 3.6 milliliters TBAF (1 molar solution in THF) dissolved in 35 milliliters THF and 1 milliliters water. The solution was filtered and concentrated under vacuum to provide a crude solid. This material was purified using column chromatography eluting with 3% by volume of ethyl acetate in hexanes to yield 510 milligrams HC≡C—C≡C(CH2)11OSi(Me2(CMe3)).
Step 3: Preparation of CH3(CH2)10CH2C≡C—C≡C(CH2)11OSi(Me2(CMe3))
In a glass reaction vessel, 1.31 grams (3.9 mmol) HC≡C—C≡C(CH2)11OSi(Me2(CMe3)) prepared in Step 2, was dissolved in 20 milliliters THF and cooled to −78° C. To this stirred solution was dropwise added a solution of 2.8 milliliters n-butyl lithium (1.6 molar solution in hexanes). This solution was added via cannula to a −15° C. solution 7 milliliters of HMPA and 1.02 grams (4.10 mmol) 1-Bromododecane in 25 milliliters THF. The resulting mixture was worked up using heptane and brine. The heptane layer was dried (MgSO4), filtered and concentrated. This material was purified using column chromatography eluting with 10% by volume of dichloromethane in hexanes to yield 680 milligrams CH3(CH2)10CH2C≡C—C≡C(CH2)11OSi(Me2(CMe3)).
Step 4: Preparation of Compound 1A: CH3(CH2)10CH2C≡C—C≡C(CH2)11NH3Cl
In a glass reaction vessel, 650 milligrams (1.3 mmol) CH3(CH2)10CH2C≡C—C≡C(CH2)11OSi(Me2(CMe3)) was dissolved in 6.5 milliliters THF. To this stirred solution was added 2.0 milliliters TBAF (1 molar solution in THF). After 1 h of stirring, the reaction mixture was filtered and concentrated to 520 milligrams of CH3(CH2)10CH2C≡C—C≡C(CH2)11OH which was used without further purification. In a glass reaction vessel, the CH3(CH2)10CH2C≡C—C≡C(CH2)11OH was dissolved in 6.5 milliliters CH2Cl2 and 150 μL (2.0 mmol) methanesulfonyl chloride and 360 μL (2.6 mmol) triethyl amine were added. The reaction was stirred for 2 h and worked up using CH2Cl2 and brine. The CH2Cl2 layer was dried (MgSO4), filtered, and concentrated to 680 milligrams of CH3(CH2)10CH2C≡C—C≡C(CH2)11OS(O2)CH3 which was used without further purification. In a glass reaction vessel, the CH3(CH2)10CH2C≡C—C≡C(CH2)11OS(O2)CH3 was dissolved in 6.5 milliliters DMF and 570 milligrams (8.8 mmol) sodium azide was added. The reaction was stirred for 20 h and worked up using pentane and brine. The pentane layer was dried (MgSO4), filtered and concentrated. This material was purified using column chromatography eluting with 9% dichloromethane in hexanes to yield 260 milligrams of CH3(CH2)10CH2C≡C—C≡C(CH2)11N3. In a glass reaction vessel, the CH3(CH2)10CH2C≡C—C≡C(CH2)11N3 was dissolved in 10 milliliters THF and 0.5 milliliters water and 330 milligrams (1.3 mmol) triphenyl phosphine was added. After 20 h of stirring, hydrogen chloride gas was bubbled through the mixture for 30 seconds. The resulting solid was filtered and washed with diethyl ether to yield 190 milligrams CH3(CH2)10CH2C≡C—C≡C(CH2)11NH3Cl.
Step 5: Preparation of Compound 1B: CH3(CH2)10CH2C≡C—C≡C(CH2)11NMe3I
In a glass reaction vessel, 55 milligrams (0.13 mmol) CH3(CH2)10CH2C≡C—C≡C(CH2)11NH3Cl was dissolved in 5 milliliters acetonitrile and 100 μL (1.6 mmol) methyl iodide and 170 milligrams (1.6 mmol) sodium carbonate. The solution was stirred at room temperature for 20 h and filtered to yield 65 milligrams CH3(CH2)10CH2C≡C—C≡C(CH2)11NMe3I.
Step 6: Preparation of Compound 1C: CH3(CH2)10CH2C≡C—C≡C(CH2)11NMe3Cl
A sample of Compound 1B was converted to Compound 1C by passing it through a Dowex anion exchange resin with sodium chloride solution.
Example 2
Preparation of CH3(CH2)14CH2C≡C—C≡C(CH2)11NR3X
Step 1: Preparation of Br(CH2)11OSi(Me2(CMe3))
The same procedure described in Example 1 Step 1 was followed.
Step 2: Preparation of HC≡C—C≡C(CH2)11OSi(Me2(CMe3))
The same procedure described in Example 1 Step 2 was followed.
Step 3: Preparation of CH3(CH2)14CH2C≡C—C≡C(CH2)11OSi(Me2(CMe3))
The same procedure described in Example 1 Step 3 was followed with the exception that 1-Bromohexadecane was used instead of 1-Bromododecane.
Step 4: Preparation of Compound 2A: CH3(CH2)14CH2C≡C—C≡C(CH2)11NH3Cl
The same procedure described in Example 1 Step 4 was followed.
Step 5: Preparation of Compound 2B: CH3(CH2)14CH2C≡C—C≡C(CH2)11NMe3I
The same procedure described in Example 1 Step 5 was followed.
Step 6: Preparation of Compound 2C: CH3(CH2)14CH2C≡C—C≡C(CH2)11NMe3Cl
The same procedure described in Example 1 Step 6 was followed.
Example 3
Preparation of CH3(CH2)10C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10NH3Cl
Step 1: Preparation of HOCH2C≡C—C≡CCH2OH
Oxidative coupling of 3-Propyn-1-ol (HOCH2C≡CH) was carried out in a glass reaction vessel by dissolving 122 grams (2.26 mol) 2-Propyn-1-ol in 70 milliliters pyridine and adding 11.1 grams (112 mmol) CuCl followed by the addition of 220 milliliters methyl alcohol. The reaction was stirred for 48 h in the presence of oxygen. The reaction was worked up using concentrated HCl and ethyl acetate. The ethyl acetate layer was dried (MgSO4), filtered and concentrated to yield 61 grams HOCH2C≡C—C≡CCH2OH.
Step 2: Preparation of N3(CH2)10C(O)Cl
In a glass reaction vessel, 10.6 grams (40 mmol) of 11-Bromoundecanoic acid was dissolved in 225 milliliters DMF and 26 grams (400 mmol) sodium azide was added. The resulting stirred mixture was heated to 80° C. for 16h, and then the reaction mixture was worked up with ether and brine. The ether layer was dried (MgSO4), filtered, and concentrated to 9.5 grams of N3(CH2)10C(O)OH as a pale yellow oil which was used without purification. In a glass reaction vessel, the N3(CH2)10C(O)OH was dissolved in 120 milliliters benzene and 12.7 grams (100 mmol) oxalyl chloride was added. The reaction was allowed to stir for 20 h, at which time the volatiles were removed in vacuo. The resulting residue was dissolved in pentane and filtered in a nitrogen atmosphere to remove solids. Concentration of the filtrate afforded N3(CH2)10C(O)Cl as a clear, yellow oil.
Step 3: Preparation of CH3(CH2)10C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10NH3Cl
In a glass reaction vessel, 400 milligrams (3.75 mmol) HOCH2C≡C—C≡CCH2OH prepared in Step 1, was dissolved in a mixture of 25 milliliters THF and 1 milliliters pyridine. To this stirred solution was added 1.0 gram (4.1 mmol) N3(CH2)10C(O)Cl prepared in Step 2, and 950 μL (4.1 mmol) CH3(CH2)10C(O)Cl. The resulting mixture was stirred for 3 h, concentrated, dissolved into hexanes and filtered to remove the salts. The filtrate was concentrated and purified using column chromatography eluting with 10% by volume of ethyl acetate in hexanes to yield 750 milligrams CH3(CH2)10C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10N3. In a glass reaction vessel, 280 milligrams (0.56 mmol) CH3(CH2)10C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10N3 was dissolved in 1 milliliters water and 8 milliliters THF. To this solution, 350 milligrams (1.3 mmol) triphenylphosphine was added. After 20 h of stirring, hydrogen chloride gas was bubbled through the mixture for 30 seconds. The resulting solid was filtered and washed with diethyl ether to yield 150 milligrams CH3(CH2)10C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10NH3Cl.
Example 4
Preparation of CH3(CH2)10C(O)O(CH2)3C≡C—C≡C(CH2)3OC(O)(CH2)10NH3Cl
Step 1: Preparation of HO(CH2)3C≡C—C≡C(CH2)3OH (also commercially available as 4,6-decadiyn-1,10-diol from GFS; Powell, Ohio)
The same procedure was followed as for Example 3 Step 1, except that 4-Pentyn-1-ol (HO(CH2)3C≡CH) was used instead of 2-Propyn-1-ol.
Step 2: Preparation of N3(CH2)00C(O)Cl
The same procedure was followed as for Example 3 Step 2.
Step 3: Preparation of CH3(CH2)10C(O)O(CH2)3C≡C—C≡C(CH2)3OC(O)(CH2)10NH3Cl
The same procedure was followed as for Example 3 Step 3 except that HO(CH2)3C≡C—C≡C(CH2)3OH (prepared in Step 1) was used instead of HOCH2C≡C—C≡CCH2OH.
Example 5
Preparation of CH3(CH2)10C(O)O(CH2)4C≡C—C≡C(CH2)4OC(O)(CH2)10NH3Cl
Step 1: Preparation of HO(CH2)4C≡C—C≡C(CH2)4OH (Also commercially available from GFS Chemicals; Powell, Ohio as 5,7-dodecadiyn-1,12-diol).
The same procedure was followed as for Example 3 Step 1, except that 5-Hexyn-1-ol (HO(CH2)4C≡CH) was used instead of 3-Propyn-1-ol.
Step 2: Preparation of N3(CH2)10C(O)Cl
The same procedure was followed as for Example 3 Step 2.
Step 3: Preparation of CH3(CH2)10C(O)O(CH2)4C≡C—C≡C(CH2)4OC(O)(CH2)10NH3Cl
The same procedure was followed as for Example 3 Step 3 except that HO(CH2)4C≡C—C≡C(CH2)4OH (prepared in Step 1) was used instead of HOCH2C≡C—C≡CCH2OH.
Example 6
Preparation of CH3(CH2)14C(O)OCH2C≡C—C≡CCH2OC(O)(CH2)10NH3Cl
Step 1: Preparation of HOCH2C≡C—C≡CCH2OH
The same procedure was followed as for Example 3 Step 1.
Step 2: Preparation of N3(CH2)10C(O)Cl
The same procedure was followed as for Example 3 Step 2.
Step 3: Preparation of CH3(CH2)14C(O)O(CH2)4C≡C—C≡C(CH2)4OC(O)(CH2)10NH3Cl
The same procedure was followed as for Example 3 Step 3 except that Hexadecanyl chloride was used instead of Dodecanyl chloride.
Example 7
Preparation of CH3(CH2)14C(O)O(CH2)3C≡C—C≡C(CH2)3OC(O)(CH2)10NH3Cl
Step 1: Preparation of HO(CH2)3C≡C—C≡C(CH2)3OH
The same procedure was followed as for Example 4 Step 1.
Step 2: Preparation of N3(CH2)10C(O)Cl
The same procedure was followed as for Example 3 Step 2.
Step 3: Preparation of CH3(CH2)14C(O)O(CH2)3C≡C—C≡C(CH2)3OC(O)(CH2)10NH3Cl
The same procedure was followed as for Example 4 Step 3 except that Hexadecanyl chloride was used instead of Dodecanyl chloride.
Example 8
Preparation of CH3(CH2)14C(O)O(CH2)4C≡C—C≡C(CH2)4OC(O)(CH2)10NH3Cl
Step 1: Preparation of HO(CH2)4C≡C—C≡C(CH2)4OH
The same procedure was followed as for Example 5 Step 1.
Step 2: Preparation of N3(CH2)10C(O)Cl
The same procedure was followed as for Example 3 Step 2.
Step 3: Preparation of CH3(CH2)14C(O)O(CH2)4C≡C—C≡C(CH2)4OC(O)(CH2)10NH3Cl
The same procedure was followed as for Example 5 Step 3 except that Hexadecanyl chloride was used instead of Dodecanyl chloride.
Example 9
Samples of 1.0 milliMolar concentration solutions of Compounds 1A, 1B, 1C, 2A, 2B, 2C in water were prepared in glass vessels, heated in a 70° C. oven for 30 minutes, bath sonicated in a Bronson Model #1510 bath sonicator (commercially available from VWR Scientific Products; West Chester, Pa.) for 30 minutes, filtered through a 0.45 micrometer syringe filter and placed in a 4° C. refrigerator for about 16 hours. The solutions were removed from the refrigerator and polymerized by stirring while irradiating beneath a 254 nanometer wavelength UV lamp (commercially available from VWR Scientific Products; West Chester, Pa.) at a distance of 3 centimeters for 10 minutes. Whether polymerization occurred upon irradiation and the presence or absence of a color change is noted in Table 1. The samples in which polymerization occurred and a color change was observed were heated to 70° C. for 15 seconds. The resulting color change is noted in Table 1.










TABLE 1








Color of



Did
Color of
polymerized


Example
polymerization
polymerized
solution after


Compound
occur
solution
heating to 70° C.







1A
Yes
Blue
Red


1B
Yes
Purple
Red


1C
No
NA
NA


2A
Yes
Blue
Red


2B
Yes
Purple
Red


2C
No
NA
NA





NA = Not applicable






Example 10
Samples of 1.0 milliMolar concentration solutions of the compounds prepared in Examples 3-8 in water were prepared in glass vessels, heated in a 70° C. oven for 30 minutes and placed in a 4° C. refrigerator for about 16 hours. The solutions were removed from the refrigerator and polymerized by stirring while irradiating beneath a 254 nanometer wavelength UV lamp (commercially available from VWR Scientific Products; West Chester, Pa.) at a distance of 3 centimeters for 10 minutes. The color change observed upon polymerization is noted in Table 2. The samples were heated to 70° C. for 15 seconds and the resulting color change is noted in Table 2. A third color transition was produced by heating the solutions to 90° C., and this color transition, if present is also noted in Table 2.










TABLE 2







Color of



Compound
Color of
polymerized
Third


Example
polymerized
solution after
transition


Number
solution
heating to 70° C.
color







3
Yellow
Orange
NA


6
Yellow
Orange
NA


4
Purple
Orange
Yellow


7
Purple
Orange
Yellow


5
Blue
Red
Orange


8
Blue
Red
Orange





NA = Not applicable






Example 11
Samples of 1.0 milliMolar concentration solutions of Compound 2B prepared in Example 2 in water were prepared in a glass vessels, heated in a 70° C. oven for 30 minutes, bath sonicated in a Bronson Model #1510 bath sonicator (commercially available from VWR Scientific Products; West Chester, Pa.) for 30 minutes, filtered through a 0.45 micrometer syringe filter and placed in a 4° C. refrigerator for about 16 hours. The solutions were removed from the refrigerator and polymerized by stirring while irradiating beneath a 254 nanometer wavelength UV lamp at a distance of 3 centimeters for 10 minutes. Salts containing other anions were added to the solutions. The presence or absence of an observed color change is recorded in Table 3.










TABLE 3







Anion
Color Change Observed?









Cl−
Yes



Br−
Yes



CO32−
Yes



SO42−
Yes



N3−
Yes



I−
No










Example 12
Preparation of HO(O)C(CH2)3C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 
Step 1: Preparation of HO(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 
In a glass reaction vessel, 600 milligrams of 5,7-dodecadiyn-1,12-diol (HO(CH2)4C≡C—C≡C(CH2)4OH), 0.275 milliliters of pyridine and 10 milliliters of THF were mixed. To this solution was added 676 milligrams of lauroyl chloride and the resulting mixture was stirred for 15 hours. The mixture was then diluted with diethyl ether and washed with 0.1 N HCl and brine. The organic layer was separated, dried over MgSO4, filtered and the solvent was removed to yield a white solid. The solid was purified over silica gel (gradient from 25% to 50% ethyl acetate in hexanes by volume) to yield 570 milligrams of HO(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 as a white solid.
Step 2: Preparation of HO(O)C(CH2)3C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 
In a glass reaction vessel, 377 milligrams of HO(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 prepared in Step 1 was dissolved in 3 milliliters of DMF and 1.32 grams of PDC was added. The resulting mixture was stirred for 8 hours, and then worked up with water and diethyl ether. The combined ether layers were dried over MgSO4, filtered and the solvent was removed to yield a white solid. The solid was purified over silica gel eluting with 25/74/1 of ethyl acetate/hexanes/formic acid by volume to yield 0.21 grams of HO(O)C(CH2)3C≡C—C≡C(CH2)4O(O)C(CH2)10CH3 as a white solid.
Examples 13-16
Preparation of HO(O)C(CH2)a-1C≡C—C≡C(CH2)aO(O)C(CH2)bCH3 
The same procedure described in Example 12 was followed using the diol and acid chloride in Step 1 shown in Table 4 to give the compounds with the general structure HO(O)C(CH2)a-1C≡C—C≡C(CH2)aO(O)C(CH2)bCH3 (a and b are defined in Table 4).









TABLE 4





Ex-

Acid


ample
Diol, a value
Chloride, b value







13
HO(CH2)3C≡C—C≡C(CH2)3OH, a = 3
CH3(CH2)14C(O)Cl,




b = 14


14
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)12C(O)Cl,




b = 12


15
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)14C(O)Cl,




b = 14


16
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)16C(O)Cl,




b = 16









Example 17
Preparation of HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 
Step 1: Preparation of HO(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 
In a glass reaction vessel, 4.99 grams of 5,7-dodecadiyn-1,12-diol (HO(CH2)4C≡C—C≡C(CH2)4OH), 2.2. grams of pyridine and 50 milliliters of THF were mixed. To this solution was added 6.34 grams of myristol chloride and the resulting mixture was stirred for 15 hours. The mixture was then diluted with diethyl ether and washed with 0.1 N HCl and brine. The organic layer was separated, dried over MgSO4, filtered and the solvent was removed to yield a white solid. The solid was purified over silica gel (15% by volume of ethyl acetate in dichloromethane to 100% ethyl acetate gradient) to yield 5.0 grams of HO(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 as a white solid.
Step 2: Preparation of HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 
In a sealable tube, 1.41 grams of HO(CH2)3C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 prepared in Step 1, 0.435 grams of succinic anhydride, 13 milliliters of toluene and 0.106 grams of DMAP were combined and the tube was sealed. The mixture was heated to 105° C. for 14.5 hours, the reaction was cooled to room temperature, 0.15 milliliters of water was added, the tube was resealed and again heated to 105° C. for 30 minutes. The mixture was then diluted with diethyl ether and washed with 0.1 N HCl and brine. The organic layer was separated, dried over MgSO4, filtered and the solvent was removed to yield a white solid. The solid was purified over silica gel eluting with 10/89/1 of ethyl acetate/dichloromethane/formic acid by volume to yield 1.70 grams of HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 as a white solid.
Examples 18-28
Preparation of HO(O)C(CH2)2C(O)O(CH2)aC≡C—C≡C(CH2)aO(O)C(CH2)bCH3 
The same procedure described in Example 17 was followed using the diol and acid chloride in Step 1 shown in Table 5 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)aC≡C—C≡C(CH2)aO(O)C(CH2)bCH3 (a and b are defined in Table 5).









TABLE 5





Example
Diol, a value
Acid Chloride, b value







18
HO(CH2)2C≡C—C≡C(CH2)2OH, a = 2
CH3(CH2)10C(O)Cl, b = 10


19
HO(CH2)2C≡C—C≡C(CH2)2OH, a = 2
CH3(CH2)12C(O)Cl, b = 12


20
HO(CH2)2C≡C—C≡C(CH2)2OH, a = 2
CH3(CH2)14C(O)Cl, b = 14


21
HO(CH2)2C≡C—C≡C(CH2)2OH, a = 2
CH3(CH2)16C(O)Cl, b = 16


22
HO(CH2)3C≡C—C≡C(CH2)3OH, a = 3
CH3(CH2)10C(O)Cl, b = 10


23
HO(CH2)3C≡C—C≡C(CH2)3OH, a = 3
CH3(CH2)12C(O)Cl, b = 12


24
HO(CH2)3C≡C—C≡C(CH2)3OH, a = 3
CH3(CH2)14C(O)Cl, b = 14


25
HO(CH2)3C≡C—C≡C(CH2)3OH, a = 3
CH3(CH2)16C(O)Cl, b = 16


26
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)10C(O)Cl, b = 10


27
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)14C(O)Cl, b = 14


28
HO(CH2)4C≡C—C≡C(CH2)4OH, a = 4
CH3(CH2)16C(O)Cl, b = 16









Example 29
Preparation of HO(O)C(CH2)2C(O)O(CH2)5C≡C—C≡C(CH2)5O(O)C(CH2)10CH3 
Step 1: Preparation of HO(CH2)5C≡C—C≡C(CH2)5OH
HO(CH2)5C≡CH was prepared by the KAPA-promoted isomerization of HOCH2C≡C(CH2)3CH3 (prepared according to Millar, J. G.; Oehlschlager, A. C. J. Org. Chem. 1984, 49, 2332-2338) or HO(CH2)2C≡C(CH2)2CH3 (commercially available GFS Chemicals; Powell, Ohio). Oxidative coupling of HO(CH2)5C≡CH was carried out in a glass reaction vessel by dissolving 6.95 grams of HO(CH2)5C≡CH in pyridine/methanol (2.0 milliliters/6.2 milliliters) and adding 307 grams of CuCl followed by stirring in the presence of oxygen until all the staring material was consumed. The reaction mixture was worked up with diethyl ether and 4N HCl, the combined organic layers were dried over MgSO4, filtered and concentrated. Recrystallization of the residue from 1/1 hexanes/tert-butyl methyl ether to yield 5.35 grams of HO(CH2)5C≡C—C≡C(CH2)5OH as a pink solid.
Step 2: Preparation of HO(CH2)5C≡C—C≡C(CH2)5O(O)C(CH2)10CH3 
The same procedure described in Example 17 Step 1 was followed except that instead of 5,7-dodecadiyn-1,12-diol the diol prepared in Step 1 above was used.
Step 3: Preparation of HO(O)C(CH2)2C(O)O(CH2)5C≡C—C≡C(CH2)5O(O)C(CH2)10CH3 
The same procedure described in Example 17 Step 2 was followed.
Examples 30-32
Preparation of HO(O)C(CH2)2C(O)O(CH2)5C≡C—C≡C(CH2)5O(O)C(CH2)bCH3 
The same procedure described in Example 29 was followed using the diol and acid chloride in Step 2 shown in Table 6 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)5C≡C—C≡C(CH2)5O(O)C(CH2)bCH3 (b is defined in Table 6).









TABLE 6





Ex-




ample
Diol
Acid Chloride, b value







30
HO(CH2)5C≡C—C≡C(CH2)5OH
CH3(CH2)12C(O)Cl, b = 12


31
HO(CH2)5C≡C—C≡C(CH2)5OH
CH3(CH2)14C(O)Cl, b = 14


32
HO(CH2)5C≡C—C≡C(CH2)5OH
CH3(CH2)16C(O)Cl, b = 16









Examples 33-36
Preparation of HO(O)C(CH2)2C(O)O(CH2)6C≡C—C═C(CH2)6O(O)C(CH2)bCH3 
The same procedure described in Example 29 Step 1 was followed to prepare the diol HO(CH2)6C≡C—C≡C(CH2)6OH starting from 1-heptyne. The remaining procedure for Example 29 was followed using the diol and acid chloride in Step 2 shown in Table 7 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)6C≡C—C≡C(CH2)6O(O)C(CH2)bCH3 (b is defined in Table 7).









TABLE 7





Ex-




ample
Diol
Acid Chloride, b value







33
HO(CH2)6C≡C—C≡C(CH2)6OH
CH3(CH2)10C(O)Cl, b = 10


34
HO(CH2)6C≡C—C≡C(CH2)6OH
CH3(CH2)12C(O)Cl, b = 12


35
HO(CH2)6C≡C—C≡C(CH2)6OH
CH3(CH2)14C(O)Cl, b = 14


36
HO(CH2)6C≡C—C≡C(CH2)6OH
CH3(CH2)16C(O)Cl, b = 16









Examples 37-39
Preparation of HO(O)C(CH2)2C(O)O(CH2)7C≡C—C≡C(CH2)7O(O)C(CH2)bCH3 
The same procedure described in Example 29 Step 1 was followed to prepare the diol HO(CH2)7C≡C—C≡C(CH2)7OH staring from 1-octyne. The remaining procedure for Example 29 was followed using the diol and acid chloride in Step 2 shown in Table 8 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)7C≡C—C≡C(CH2)7O(O)C(CH2)bCH3 (b is defined in Table 8).









TABLE 8





Ex-




ample
Diol
Acid Chloride







37
HO(CH2)7C≡C—C≡C(CH2)7OH
CH3(CH2)10C(O)Cl, b = 10


38
HO(CH2)7C≡C—C≡C(CH2)7OH
CH3(CH2)12C(O)Cl, b = 12


39
HO(CH2)7C≡C—C≡C(CH2)7OH
CH3(CH2)16C(O)Cl, b = 16









Examples 40-43
Preparation of HO(O)C(CH2)2C(O)O(CH2)9C≡C—C≡C(CH2)9O(O)C(CH2)bCH3 
The same procedure described in Example 29 Step 1 was followed to prepare the diol HO(CH2)9C≡C—C═C(CH2)9OH starting from 1-decyne. The remaining procedure for Example 29 was followed using the diol and acid chloride in Step 2 shown in Table 9 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)9C≡C—C≡C(CH2)9O(O)C(CH2)bCH3 (b is defined in Table 9)









TABLE 9





Ex-




ample
Diol
Acid Chloride, b value







40
HO(CH2)9C≡C—C≡C(CH2)9OH
CH3(CH2)10C(O)Cl, b = 10


41
HO(CH2)9C≡C—C≡C(CH2)9OH
CH3(CH2)12C(O)Cl, b = 12


42
HO(CH2)9C≡C—C≡C(CH2)9OH
CH3(CH2)14C(O)Cl, b = 14


43
HO(CH2)9C≡C—C≡C(CH2)9OH
CH3(CH2)16C(O)Cl, b = 16









Example 44
Preparation of HO(O)C(CH2)3C(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 
The same procedure described in Example 17 was followed except that in Step 2 glutaric anhydride was used in place of succinic anhydride.
Example 45
Preparation of HO(O)CHC≡CHC(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)14CH3 
The same procedure described in Example 17 was followed except that in Step 1 CH3(CH2)14C(O)Cl was used instead of CH3(CH2)12C(O)Cl and in Step 2 maleic anhydride was used in place of succinic anhydride.
Example 46
Preparation of HO(O)C(1,2-C6H4)C(O)O(CH2)4C≡C—C≡C(CH2)4O(O)C(CH2)12CH3 
The same procedure described in Example 17 was followed except that in Step 2 phthalic anhydride was used in place of succinic anhydride.
Example 47
Preparation of HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 
Step 1: Preparation of HO(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 
In a glass reaction vessel, a suspension of 120 milligrams of sodium hydride was prepared in 10 milliliters dry DMF and 972 milligrams of 5,7-dodecadiyn-1,12-diol (HO(CH2)4C≡C—C≡C(CH2)4OH), was added. After stirring for 5 minutes 1.31 grams of CH3(CH2)11Br was added and the resulting mixture was stirred for 15 hours. The mixture was then quenched by addition of saturated NH4Cl solution and diluted with 100 milliliters of diethyl ether. The organic layer was separated and washed 3 times with brine, dried over MgSO4, filtered and the solvent was removed to yield a yellow oil. The oil was purified over silica gel (25%-35% by volume of ethyl acetate in hexanes gradient) to yield 606 milligrams of HO(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 as a white solid.
Step 2: Preparation of HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 
In a sealable tube, 181 milligrams of HO(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 prepared in Step 1, 63 milligrams of succinic anhydride, 2 milliliters of toluene and 15 milligrams of DMAP were combined and the tube was sealed. The mixture was heated to 110° C. for 16 hours, the reaction was cooled to room temperature, 3 drops of water was added, the tube was resealed and again heated to 110° C. for 30 minutes. The mixture was then diluted with diethyl ether and washed with 0.1 N HCl and brine. The organic layer was separated, dried over MgSO4, filtered and solvent was removed to yield a white solid. The solid was purified over silica gel eluting with 10/89/1 of ethyl acetate/dichloromethane/formic acid by volume to yield HO(O)C(CH2)2C(O)O(CH2)4C≡C—C≡C(CH2)4O(CH2)11CH3 as a white solid.
Examples 48-52
Preparation of HO(O)C(CH2)2C(O)O(CH2)aC≡C—C≡C(CH2)aO(CH2)bCH3 
The same procedure described in Example 47 was followed using the diol and alkyl bromide in Step 1 shown in Table 10 to give the compounds with the general structure HO(O)C(CH2)2C(O)O(CH2)aC≡C—C≡C(CH2)aO(CH2)bCH3 (a and b are defined in Table 10).









TABLE 10







Alkyl Bromide,


Example
Diol, a value
b value







48
HO(CH2)2C≡C—C≡C(CH2)2OH,
CH3(CH2)bBr, b = 13



a = 4


49
HO(CH2)2C≡C—C≡C(CH2)2OH,
CH3(CH2)bBr, b = 15



a = 4


50
HO(CH2)2C≡C—C≡C(CH2)2OH,
CH3(CH2)bBr, b = 17



a = 4


51
HO(CH2)2C≡C—C≡C(CH2)2OH,
CH3(CH2)bBr, b = 11



a = 5


52
HO(CH2)3C≡C—C≡C(CH2)3OH,
CH3(CH2)bBr, b = 13



a = 5









Example 53
A sample of 10.1 milligrams of the compound prepared in Example 17 was placed in a glass vessel and suspended in 5 milliliters of isopropanol. The mixture was heated to boiling and 10 milliliters of 70° C. water was added. The resulting solution was boiled until the temperature reached 95° C. indicating the nearly all of the isopropanol had boiled off. The solution was cooled to room temperature and then to 4° C. for 16 hours. A 2 milliliter aliquot of the solution was exposed 254 nanometer light for 10 minutes, producing a dark blue color indicative that polymerization had occurred.

## Claims

1. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula



wherein R1 is dodecyl or hexadecyl;
R2 is,





R24, R31 and R33 are independently C1-C20 alkyl;
R22, R25, and R32 are independently C1-C14 alkylene;
R26 is C1-C14 alkylene, or C2-C8 alkenylene,
R27, and R29 are independently C1-C14 alkylene or (C1-C14 alkylene)-(C2-C8 arylene);
R28 is C2-C30 alkynyl;
R23 is C6-C13 arylene;
R30 is C1-C14 alkylene;
p is 1-5;
and

wherein R1 and R2 are not the same.

2. The polymerized composition of claim 1, wherein R24 is methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or dodecyl.

3. The polymerized composition of claim 1, wherein R33 is dodecyl, tetradecyl, hexadecyl, or octadecyl.

4. The polymerized composition of claim 1, wherein R25 is independently ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene.

5. The polymerized composition of claim 1, wherein R22 is ethylene, trimethylene, or tetramethylene.

6. The polymerized composition of claim 1, wherein R32 is ethylene, trimethylene, tetramethylene, pentamethylene, or hexamethylene.

7. The polymerized composition of claim 1, wherein R26 is ethylene, trimethylene, ethenylene, or phenylene.

8. The polymerized composition of claim 1, wherein R31 is C1-C14 alkyl.

9. The polymerized composition of claim 8, wherein R31 is butyl, pentyl or hexyl.

10. The polymerized composition of claim 1, wherein R27 and R29 are independently methylene, ethylene, trimethylene, tetramethylene, —C(CH3) 2—, —CH((CH2)1-4CH3)—, or —CH2-phenylene.

11. The polymerized composition of claim 1, wherein R28 is C2-C30 alkynyl having at least two carbon-carbon triple bonds.

12. The polymerized composition of claim 11, wherein R28 is (CH2)8—C≡C—C≡C—(CH2)9CH3, or —(CH2)8—C≡C—C≡C—(CH2)11CH3.

13. The polymerized composition of claim 1, wherein R23 is phenylene.

14. The polymerized composition of claim 1, wherein p is 1 or 2.

15. The polymerized composition of claim 1, wherein the composition has a color in the visible spectrum less than 570 nm.

16. The polymerized composition of claim 1, wherein the composition has a color in the visible spectrum between 570 nm and 600 nm.

17. The polymerized composition of claim 1, wherein the composition has an observed color in the visible spectrum greater than 600 nm.

18. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula



wherein R1 is




R2 is (C7-C18 alkyl)—NR353X, wherein R35 is H and each X is independently F—, 
Br—, Cl—, I—, OH—, N3—, HCO3—, or CN—;
R3, R8 and R13, are independently C1-C20 alkyl;
R4, R7, R14, R16, and R19, are independently C1-C14 alkylene;
R6, R15, and R18 are independently C1-C14 alkylene, or C2-C8 alkenylene, or C6-C13 arylene;
R9 is C1-C14 alkylene;
R10 and R12, are independently C1-C14 alkylene or (C1-C14 alkylene) —(C2-C8 arylene);
R11 is independently C2-C30 alkynyl;
R17 is an ester activating group;
p is 1-5;
n is 1-20; and

wherein R1 and R2 are not the same.

19. The polymerized composition of claim 18, wherein R2 is —(CH2)11—NH3X, —(CH2)11—N(CH3)3X, —(CH2)15—N(CH3)3X, or —(CH2)15—NH3X, wherein each X is independently Cl—, or I—.

20. The polymerized composition of claim 18, wherein R2 is (C1-C18 alkyl)—NR353X, wherein R35 is C1-C4 alkyl and each X is independently F—, Br−, Cl−, I−, OH−, N3−, HCO3−, or CN−.

21. A method of making a polymerized composition of claim 1, the method comprising:
mixing one or more compounds of claim 1 in water;
processing the aqueous mixture to cause self-assembly of the one or more compounds; and
polymerizing the one or more compounds.

22. The method of claim 21 wherein processing the aqueous mixture to cause self-assembly comprises heating or sonicating the mixture, and polymerizing comprises irradiating the mixture with actinic radiation.

23. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R7 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene, and R6 is ethylene, trimethylene, ethenylene, or phenylene; and
wherein R2 is




wherein R22 is ethylene, trimethylene, or tetramethylene, R23 is phenylene, and R24 is methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or dodecyl; and
wherein p is 1.

24. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R7 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene, and R6 is ethylene, trimethylene, ethenylene, or phenylene; and
wherein R2 is




wherein R32 is ethylene, trimethylene, tetramethylene, pentamethylene, or hexamethylene and R33 is dodecyl, tetradecyl, hexadecyl, or octadecyl; and

wherein p is 1.

25. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R8 is butyl, pentyl or hexyl, R9 is methylene, and R10 is methylene, ethylene, trimethylene, tetramethylene, —C(CH3) 2—, —CH((CH2)1-4CH3)—, or —CH2-phenylene; and
wherein R2 is




wherein R29 is methylene, ethylene, trimethylene, tetramethylene, —C(CH3) 2—, —CH((CH2)1-4CH3)—, or —CH2-phenylene, R30 is methylene, and R31 is butyl, pentyl or hexyl; and

wherein p is 1.

26. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R11 is C1-C20 alkynyl having at least two carbon-carbon triple bonds, and R12 is methylene, ethylene, trimethylene, tetramethylene, —C(CH3) 2—, —CH((CH2)1-4CH3)—, or —CH2-phenylene; and
wherein R2 is




wherein R27 is methylene, ethylene, trimethylene, tetramethylene, —C(CH3) 2—, —CH((CH2)1-4CH3)—, or —CH2-phenylene, and R28 is C1-C20 alkynyl having at least two carbon-carbon triple bonds; and

wherein p is 1.

27. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R3 is undecyl or pentadecyl, and R4 is methylene, ethylene, or tetramethylene; and
wherein R2 is




wherein R20 is methylene, trimethylene, or tetramethylene, and R21 is
—(CH2)10—NH3X, —(CH2)10—N(CH3)3X, —(CH2)14—N(CH3)3X, or
—(CH2)14—NH3X, wherein each X is independently Cl— or I—; and

wherein p is 1.

28. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R5 is ethylene or trimethylene; and
wherein R2 is




wherein R20 is trimethylene or tetramethylene, and R21 is undecyl, tridecyl, pentadecyl, or heptadecyl; and

wherein p is 1.

29. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R7 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene, and R6 is ethylene, trimethylene, ethenylene, or phenylene; and
wherein R2 is




wherein R20 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene, and wherein R21 is undecyl, tridecyl, pentadecyl, heptadecyl; and

wherein p is 1.

30. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R16 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene, R15 is ethylene, trimethylene, ethenylene, or phenylene, R14 is ethylene, R13 is methyl; and
wherein R2 is




wherein R20 is methylene, trimethylene, or tetramethylene, and R21 is tridecyl; and

wherein p is 1 and n is 9-11.

31. A polymerized composition comprising the polymerization reaction product of at least one compound of the formula




wherein R1 is



wherein R17 is 2,5-dioxo-1-pyrrolidinyl, R18 is ethylene, trimethylene, ethenylene, or phenylene R19 is ethylene, trimethylene, tetramethylene, pentamethylene, hexamethylene, heptamethylene, octamethylene, or nonamethylene; and
wherein R2 is




wherein R20 is methylene, trimethylene, or tetramethylene, and R21 is tridecyl; and

wherein p is 1.