# Patent

## Title
Epoxy resin curing compositions and epoxy resin systems including same

## Abstract

Disclosed are epoxy resins exhibiting a highly favorable combination of tensile strength and elongation with respect to prior art epoxy systems. The elastomeric epoxy resin systems of the invention are prepared utilizing a curing agent containing at least one monoprimary amine, and are particularly useful in applications such as, for example, castings, potting, composites, crack sealing, coatings, adhesives, roofing materials, flooring or reinforced membranes.

## Background
FIELD OF THE INVENTION
The present invention relates to curing compositions for epoxy resin systems and to epoxy resin, prepared utilizing the curing composition, and exhibiting a highly favorable combination of tensile strength and elongation with respect to prior art epoxy systems. The present invention also relates to methods of preparing elastomeric epoxy resin systems and to articles made therefrom. The elastomeric epoxy resin systems of the invention include a curing agent containing at least one monoprimary amine, and are particularly useful in applications such as, for example, castings, potting, composites, crack sealing, coatings, adhesives, roofing materials, flooring or reinforced membranes.
BACKGROUND OF THE INVENTION
In the preparation of flexible, elastomeric or high-elongation epoxy resin systems, flexibility and low Tg are typically introduced into the system through the epoxy resin, the curing agent or both.
Epoxy resins which impart flexibility to cured epoxy resin systems include epoxidized vegetable oils, glycidated dimerized fatty acids and poly(propylene oxide) glycols of various molecular weights having glycidyl end groups. Epoxidized vegetable oils are inexpensive but cure very poorly, if at all, with aliphatic amines at room temperature. They do cure with strong acid curing agents but the resultant cured materials are weak and easily torn. Glycidated dimerized fatty acids are expensive low-volume products prepared by a difficult batch process. They have limited storage stability, and cured materials prepared with them tend to have high water absorption. Glycidated poly(propylene oxide) glycols are also expensive low-volume resins which tend to cure relatively slowly, and which tend not to give high network strength.
Curing agents which impart flexibility to epoxy systems include long-chain poly(propylene oxide) diamines, “dimer diamines” produced by conversion of dimerized fatty acids to nitriles and subsequent hydrogenation of the nitrile groups to amine groups, and condensates of dimerized fatty acids with amines containing one primary and one secondary amine group (such as N-(aminoethyl)piperazine or amino ethylethanolamine) or two secondary amine groups (such as piperazine). All of these curing agents have various disadvantages. The long-chain poly(propylene oxide) diamines cure epoxy resins extremely slowly at room temperature, often taking more than a day to gel the epoxy resins even when highly accelerated. The “dimer diamines” are faster curing than the long-chain poly(propylene oxide) diamines but are very expensive and, like the poly(propylene oxide) diamines, tend to give cured systems with low tensile strength at given elongation.
The condensates of dimerized fatty acids with amines containing one primary and one secondary amine group or two secondary amine groups (e.g., U.S. Pat. Nos. 6,127,508 and 6,500,912) overcome a number of these disadvantages in that cure is fairly fast and also the cured products have relatively high tensile strength at a given elongation level. However, a major disadvantage of these dimer acid-amine condensate curing agents is their high viscosity, generally well above 10 Pa-s (10000 cP) and often above 30 Pa-s (30000 cP) at 25° C. The high viscosity renders mixing and degassing at room temperature fairly difficult. The viscosity of the curing agent can be reduced by addition of standard polyamine curing agents such as aminoethylpiperazine and other ethyleneamines, and also by nonreactive diluents such as ethoxylates of detergent-range alcohols. However, the low amine hydrogen equivalent weight of the polyamines severely limits the amount of polyamine which can be used as a diluent without unacceptable loss of cured resin elongation. This maximum amount is typically insufficient to give the desired viscosity reduction. When the nonreactive diluents such as ethoxylates of detergent-range alcohols are used, the incorporation of enough diluent to reduce viscosity significantly will tend to cause the cured resin products to become soft and weak (e.g., U.S. Pat. No. 6,127,508, Example 4).
In light of the above, there is a need in the art for curing agents for elastomeric epoxy resin systems which are inexpensive, cure rapidly at ambient temperatures, have low viscosity at ambient temperatures, and which produce cured elastomeric epoxy resins exhibiting improved tensile strength and elongation when compared to the prior art resin compositions.



SUMMARY OF THE FIGURE
FIG. 1 is a plot of combinations of tensile properties of the inventive compositions relative to those of the prior art.



SUMMARY OF THE INVENTION
In one aspect, the invention is a composition including a epoxy resin system, which system includes a reaction product of an epoxy resin component and a curing agent. The curing agent includes a monoprimary amine, represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms and is substantially free of a crosslinking agent having at least 3 active hydrogen atoms. The cured reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C.
In another aspect, the invention is a composition including a epoxy resin system, which system includes a reaction product of an epoxy resin component and a curing agent. The curing agent, consisting essentially of a monoprimary amine, is represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms. The cured reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C.
In another aspect, the invention is a composition comprising an epoxy resin system, which system includes a reaction product of an epoxy resin component and a curing agent. The curing agent includes greater that 70 wt % of a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms. The cured reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C.
In another aspect, the invention is a composition comprising an epoxy resin system, which system includes a reaction product of an epoxy resin component and a curing agent. The curing agent includes less than 20 wt % of a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms. The cured reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C.
DETAILED DESCRIPTION OF THE INVENTION
The epoxy resin system of the invention includes at least one epoxy resin component and a curing agent containing at least one monoprimary amine.
A. Epoxy Resin Component
The elastomeric epoxy resin systems of the invention include at least one epoxy resin component. Epoxy resins are those compounds containing at least one vicinal epoxy group. The epoxy resin may be saturated or unsaturated, aliphatic, cycloaliphatic, aromatic or heterocyclic and may be substituted. The epoxy resin may also be monomeric or polymeric.
Epoxy Resin
In one embodiment, the epoxy resin component may be prepared by reacting epichlorohydrin with a compound containing at least one, two or more, hydroxyl groups under basic conditions, such as in an alkaline reaction medium or in the presence of a suitable base. Examples of such suitable epoxy resin components include, but are not limited to, polyglycidyl ethers of poly- or dihydric phenols, polyglycidyl ethers of glycols or polyglycols, epoxy novolacs, other glycidated polyphenolic resins, polyglycidyl esters of polycarboxylic acids, fusion reaction products between these epoxy resins and additional polyhydric phenolic compounds as those disclosed and described in U.S. Pat. Nos. 3,477,990 and 4,734,468, and mixtures thereof. Examples of suitable phenolic compounds used in preparing these epoxy resins include, but are not limited to resorcinol, catechol, t-butylcatechol, hydroquinone, bisphenol A (BPA), bisphenol E (BPE), bisphenol F (BPF), tris(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)isobutane, 2,2-bis(4-hydroxyphenyl)butane, 2,2-bis(4-hydroxy-3-tert-butylphenyl)propane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 2,6,2′,6′-tetrachloro-p,p′-bisphenol A, 2,6,2′,6′-tetrabromo-p,p′-bisphenol A, 2,6,2′,6′-tetramethyl-3,5,3′-tribromo-p-p′-biphenol, 2,6′,6′-tetramethyl-3,5,3′,5′-tetrabromo-p,p′-biphenol, tetramethylbiphenol, 1,5-dihydroxynaphthalene, bis(2-hydroxy-1-naphthypmethane, bis(4-hydroxyphenyl)sulfone, bis(4-hydroxyphenyl)ether and the like and mixtures thereof. Examples of such epoxy resin components include, but are not limited to, EPON Resins 825, 826, 828, 862 and 1001 commercially available from Hexion Specialty Chemicals, Inc.
Epoxy Resin Modified with Monofunctional or Polyfunctional Epoxy Diluents
In another embodiment, the epoxy resin component optionally includes polyglycidyl ethers of aliphatic or cycloaliphatic glycols or triols or polyols, or polyglycols. Examples of these glycols include, but are not limited to, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, neopentyl glycol, cyclohexanedimethanol, hydrogenated BPA, polyethylene glycol, polypropylene glycol, trimethylolethane, trimethylolpropane and mixtures thereof. Similar to the di- and polyhydric phenol based epoxy resins, these aliphatic glycidyl and polyglycidyl ethers are usually prepared by reacting epichlorohydrin with a selected aliphatic diol (or triol or polyol or polyglycol or mixtures) in the presence of a Lewis acid catalyst, followed by conversion of the reaction intermediate(s) with sodium hydroxide to the product(s). Commercially available examples of such epoxy resin diluent components include, but are not limited to, HELOXY Modifier 32 (a diglycidyl ether of a poly(propylene oxide) glycol), HELOXY Modifier 68 (the diglycidyl ether of neopentyl glycol) and HELOXY Modifier 107 (the diglycidyl ether of 1,4-cyclohexanedimethanol) from Hexion Specialty Chemicals, Inc.
The optional polyglycidyl ethers of aliphatic or cycloaliphatic glycols or triols or polyols, or polyglycols are blended with the epoxy resin component in a weight ratio of from 0 to up to about 100 parts of ether for each 100 parts of epoxy resin component. In another embodiment, the polyglycidyl ethers of aliphatic or cycloaliphatic glycols or triols or polyols, or polyglycols are blended with the epoxy resin component in a weight ratio of about 5 to about 100 parts of ether for each 100 parts of epoxy resin component.
Epoxy Resin Modified with a Polyacrylate or Polymethacrylate Ester of a Polyol
In another embodiment, the epoxy resin component optionally includes a polyacrylate or polymethacrylate ester of a polyol which contain more than one terminal acrylate or methacrylate group. These esters are the acrylic and methacrylic acid esters of aliphatic polyhydric alcohols such as, for example, the di- and polyacrylates and the di- and polymethacrylates of alkylene glycols, alkoxylene glycols, alicyclic glycols and higher polyols, such as ethylene glycol, triethylene glycol, tetraethylene glycol, tetramethylene glycol, hexanediol, trimethylolethane, trimethylolpropane, pentaerythritol, dipentaerythritol, tripentaerythritol and the like, or mixtures of these with each other or with their partially esterified analogs.
Typical compounds include but are not limited to trimethylolpropane triacrylate, trimethylolethane triacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, tetramethylene glycol dimethacrylate, ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, 1,6-hexanediol diacrylate, 1,6-hexanediol dimethacrylate, dipentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, and the like. Particularly preferred esters are 1,6-hexanediol diacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate, and pentaerythritol tetraacrylate.
Additional acrylate or methacrylate esters of polyols are the acrylate or methacrylate esters of epoxide resins, wherein epoxide resins as used herein are considered to be polyols. The epoxide resins useful in reacting with acrylic or methacylic acid are those epoxide resins described above. The procedures for preparing these acrylate and methacrylate esters of epoxide resins are described in U.S. Pat. No. 3,377,406 which is hereby incorporated by reference.
The optional acrylate or methacrylate esters of the polyols are blended with the epoxy resin component in a weight ratio of from 0 to up to about 100 parts of ester for each 100 parts of epoxy resin component. In another embodiment, the acrylate or methacrylate esters of the polyols are blended with the epoxy resin component in a weight ratio of about 5 to about 100 parts of ester for each 100 parts of epoxy resin component.
B. Curing Agents
The elastomeric epoxy resin systems of the invention include a curing agent containing at least one monoprimary amine.
Monoprimary Amines
Suitable monoprimary amines for use in the curing agent include monoprimary aliphatic amines containing between about 8 to about 50 carbon atoms, which may optionally contain one or more of ether, thioether or tertiary amine linkages. In one embodiment, the monoprimary amine is represented by the formula:

R—NH2  Formula 1

wherein in Formula 1, R is a hydrocarbyl group, such as for example an alkyl, alkenyl, alkynyl, cycloalkyl, arylalkyl, hydroxyalkyl, cyano alkyl, alkylthioalkyl, dialkylamino alkyl, cyanoarylalkyl, alkoxyarylalkyl, alkylthio arylalkyl and dialkylaminoarylalkyl containing about 8 to about 50 carbon atoms, including any combination or subset thereof.

In another embodiment, the monoprimary amine of Formula I may contain an ether, thioether or tertiary amine linkage. In another embodiment the monoprimary amine is represented by any one of the following formulae:

R′—O—R—NH2  Formula 2;

R′S—R—NH2  Formula 3;

R′2N—R—NH2  Formula 4;

R′2P—R—NH2  Formula 5; or

R′3Si—RNH2  Formula 6;

including any combination or subset of Formulae 2 to 6, wherein each R′ is independently a hydrocarbyl group, as described above, such that the combination of R plus all R′ groups contains a total of between about 8 and about 50 carbon atoms, and in each case, the R and R′ groups may be saturated or unsaturated.

In another embodiment, the monoprimary amine is a primary fatty amine, which may optionally include secondary amine groups. Suitable examples of such primary fatty amines include, but are not limited to octylamines, laurylamines, myristylamines, palmitylamines, stearylamines, oleylamine, tallowamines, hydrogenated tallow amines, cetylamines, N-tetradecylamine, cocoamines and soyamines, including any combination or subset thereof.
In another embodiment the monoprimary amine is an amine such as octyl 3-aminopropyl ether, 2-ethylhexyl 3-aminopropyl ether, lauryl 3-aminopropyl ether, myristyl 3-aminopropyl ether, stearyl 3-aminopropyl ether, oleyl 3-aminopropyl ether, behenyl 3-aminopropyl ether and tridecyl 3-amino propyl ether (linear or branched), including any combination or subset thereof.
In one embodiment, the monoprimary amine does not contain cyclic or aromatic groups.
In one embodiment, the monoprimary amine described above is the only curing agent component present in the epoxy resin system. In another embodiment, the monoprimary amine is present such that the ratio of amine hydrogen:epoxy group is between about 0.8 and about 1.2.
Monoprimary Amines in Combination with Amine Terminated Polyamide
In one embodiment, the monoprimary amine is optionally utilized in combination with an amine terminated polyamide which is the reaction product of a dimerized fatty acid or hydrogenated dimerized fatty acid with an amine containing one primary and one secondary amine group or two secondary amine groups. Such diamide-diamines are described in U.S. Pat. Nos. 6,127,508 and 6,500,912 B1, both incorporated herein by reference.
In one embodiment, the amine terminated polyamide is prepared by reacting a carboxylic acid selected from C18-C60 dicarboxylic acids, C18-C60 dicarboxylic acid derivatives and mixtures thereof, optionally containing di- or polycarboxylic acids or acid derivatives having from 4 to 20 carbon atoms in an amount ranging from 0-10% based on all carboxylic acids, and at least one amine having the formula:

R1—NH—R2—NH—R3  Formula 7

wherein in Formula 7, R1 has a total number of carbon atoms from 0 to about 20, is selected from the group consisting of hydrogen, alkyl, cycloalkyl, alkenyl, arylalkyl, hydroxyalkyl, alkoxyalkyl, cyanoalkyl, alkylthioalkyl, dialkylaminoalkyl, aryl, alkylaryl, cyanoaryl, alkoxyaryl, alkylthioaryl, and dialkylaminoaryl; R3 having a total number of carbon atoms from 1 to about 20, is selected from the group consisting of alkyl, cycloalkyl, alkenyl, arylalkyl, hydroxyalkyl, alkoxyalkyl, cyanoalkyl, alkylthioalkyl, dialkylaminoalkyl, aryl, alkylaryl, cyanoaryl, alkoxyaryl, alkylthioaryl, and dialkylaminoaryl; and R2 is (CR4R5)n, wherein n is from 2 to about 20, R4 is independently selected for each (CR4R5) from the group consisting of H, alkyl, aryl, hydroxyl, alkoxy, alkylthio, dialkylamino and cyano; and R5 is independently selected for each (CR4R5) from the group consisting of H, alkyl and aryl.

In another embodiment, the amine terminated polyamide is prepared by the reaction of at least one C18-C50 dicarboxylic acid, dicarboxylic acid ester or dicarboxylic acid chloride with an amino alkylpiperazine having the formula:




wherein in Formula 8, R1 is hydrogen and R2 is —R3—NH2 wherein R3 is a divalent aliphatic linkage with optional —CHR4 and —CR4R5 units wherein R4 and R5 are independently alkyl groups. In one embodiment, the divalent linkage group contains about 2 to about 6 carbon atoms.

In one embodiment, the ratio of amine terminated polyamide curing agent:monoprimary amine curing agent is between 0:100 to 99:1. In another embodiment, the ratio of amine terminated polyamide curing agent:monoprimary amine curing agent is between 50:50 to 99:1. In another embodiment, the ratio of amine terminated polyamide curing agent:monoprimary amine curing agent is between 50:50 to 95:5.
Monoprimary Amines in Combination with Diamines or Polyamines
In one embodiment, the monoprimary amine is optionally utilized in combination with a diamine or polyamine containing curing agent.
In another embodiment, the monoprimary amine is optionally used in combination with an amine-containing curing agent. Amine-containing curing agents have, on average, more than one active hydrogen atom, wherein the active hydrogen atoms may be bonded to the same nitrogen atom or to different nitrogen atoms. Such curing agents include those compounds that contain a primary amine moiety, and compounds that contain two or more primary or secondary amine or amide moieties linked to a common central organic moiety. Suitable examples include, but are not limited to ethylene diamine, diethylene triamine, polyoxypropylene diamine, triethylene tetramine, dicyandiamide, melamine, cyclohexylamine, benzyl amine, diethylaniline, methylenedianiline, m-phenylenediamine, diaminodiphenylsulfone, 2,4 bis(p-aminobenzyl)aniline, and the like, and soluble adducts of amines and polyepoxides and their salts, such as described in U.S. Pat. Nos. 2,651,589 and 2,640,037.
In another embodiment, the monoprimary amine is optionally used in combination with a polyamidoamine curing agent. Polyamidoamines are typically the reaction product of a polyacid and an amine. Examples of polyacids used in making these polyamidoamines include 1,10-decanedioic acid, 1,12-dodecanedioic acid, 1,20-eicosanedioic acid, 1,14-tetradecanedioic acid, 1,18-octadecanedioic acid and dimerized and trimerized fatty acids. Amines used in making the polyamidoamines include aliphatic and cycloaliphatic polyamines such as ethylene diamine, diethylene triamine, triethylene tetramine, tetraethylene pentamine, 1,4-diaminobutane, 1,3-diaminobutane, hexamethylene diamine, and the like. In another embodiment, polyamides are those derived from the aliphatic polyamines containing no more than 12 carbon atoms and polymeric fatty acids obtained by dimerizing and/or trimerizing ethylenically unsaturated fatty acids containing up to 25 carbon atoms.
In another embodiment, the monoprimary amine is optionally used in combination with curing agents such as aliphatic polyamines, polyglycoldiamines, polyoxypropylene diamines, polyoxypropylenetriamines, amidoamines, imidazoles, reactive polyamides, ketimines, araliphatic polyamines (i.e. xylylenediamine), cycloaliphatic amines (i.e. isophoronediamine or diaminocyclohexane), menthane diamine, 4,4-diamino-3,3-dimethyldicyclohexylmethane, heterocyclic amines (aminoethyl piperazine), aromatic polyamines (methylene dianiline), diamino diphenyl sulfone, mannich base, phenalkamine, N,N′,N′′-tris(6-aminohexyl)melamine, and the like.
In one embodiment, the ratio of diamine or polyamine containing curing agent:monoprimary amine curing agent is between 0.01:1 to about 1:1.
In another embodiment, when the monoprimary amine is optionally utilized in combination with a diamine or polyamine containing curing agent the amount of diamine or polyamine is less than about 15 wt %, based upon the weight of the curing agent mixture.
In another embodiment, when the monoprimary amine is optionally utilized in combination with a diamine or polyamine containing curing agent the diamine or polyamine contains an average of less than 3 active hydrogen atoms.
C. Accelerators
The composition may also optionally comprise an accelerator known to be compatible with amine-functional groups. Examples include sulfonates such as alkylbenzenesulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, IIA and transition metals of the Periodic Table (CAS version), preferably Mg, Ca, and Sn (II) salts and complexes. Other examples of accelerators include inorganic acids such as HBF4, H2SO4, H2NSO3H, and H3PO4, carboxylic acids, particularly hydroxyl-group containing carboxylic acids such as salicylic acid, lactic acid, glycolic acid and resorcylic acid; phenolic compounds such as phenol, t-butylphenol, nonylphenol and BPA; imidazoles; cyanamide compounds such as dicyandiamide and cyanamide; sulfonamides such as p-toluenesulfonamide; and imides such as phthalimide, succinimide, maleimide, perylenetetracarboxylic diimide, and saccharin. In one embodiment, accelerators useful for the present invention include, but are not limited to calcium nitrate, calcium alkylbenzene sulfonates, magnesium alkanesulfonates, dicyandiamide, tetrafluoroboric acid, salicylic acid, phenol, dichloroacetic acid, trifluoroacetic acid, thiocyanic acid and mercaptoacetic acid. In another embodiment, the ammonium, calcium or magnesium salt of an acid may be used in place of the acids themselves.
The amount of optional accelerator will vary depending upon the particular curing agent used (due to cure chemistry and curing agent equivalent weight) and may be readily determined by one of ordinary skill in the art. In one embodiment, the accelerator is typically used in an amount of about 5 wt % or less, based upon the total weight of the curing agent.
D. Compositions
In one embodiment, the Brookfield viscosity of the curing agent containing the monoprimary amine, as measured at 25° C., is about 3000 cP or less.
In one embodiment, the Tg of the fully cured resin composition, as measured by Differential Scanning Calorimetry (DSC), is 30° C. or less. In another embodiment, the Tg of the fully cured resin composition, as measured by DSC, is 15° C. or less.
In one embodiment, the tensile strength of the fully cured resin composition, as measured by ASTM D-638 at 25° C., is greater than 1 MPa. In another embodiment, the tensile strength of the fully cured resin composition, as measured by ASTM D-638 at 25° C., is greater than 2 MPa.
In one embodiment, the elongation of the fully cured resin composition, as measured by ASTM D-638 at 25° C., is greater than 100%. In another embodiment, the elongation of the fully cured resin composition, as measured by ASTM D-638 at 25° C., is greater than 200%. In another embodiment, the elongation of the fully cured resin composition, as measured by ASTM D-638 at 25° C., is between about 100% and about 200%.
In one embodiment, the cured product may contain some uncrosslinked fraction (leading to partial meltability) but will generally be at least primarily crosslinked. In another embodiment, a substoichiometric ratio of amine to epoxy groups may be used in order to promote some epoxy homopolymerization and resultant crosslinking. In another embodiment, the cured product may be almost completely uncrosslinked, such that it is soluble in a solvent.
In another embodiment, the fully cured epoxy resin system contains a sufficiently high amount of cross-linkage such that the resin does not fully dissolve in any solvent. In another embodiment, the fully cured resin composition is essentially free of asphalt.
In order to provide a better understanding of the present invention including representative advantages thereof, the following examples are offered. It is understood that the examples are for illustrative purposes and should not be regarded as limiting the scope of the invention to any specific materials or conditions.
EXAMPLES
The glass transition temperature (Tg) of the cured resins in these Examples was measured by Differential Scanning Calorimetry (DSC) at a heat-up rate of 20° C./minute from 50° C. to 220° C. followed by rapid cooling and a second identical heating rate scan. The midpoint of the curve in which heat capacity (Cp) increases from the glassy plateau to the rubbery plateau was take as the Tg. The DSC instrument utilized was a TA Instruments DSC Model Q20 and its temperature was calibrated using an indium and a tin standard.
The tensile strength, tensile modulus, and the tensile elongation of the cured resins in these Examples were measured by ASTM D-638 at a strain rate of 2 inches per minute. The tensile strength was determined as the maximum value in the stress-strain curve.
The viscosity of the curing agents in these Examples is the Brookfield viscosity measured at 25° C.
Example 1
Cure of EPON Resin 828 with Different Monoamines (and One Diamine)
EPON Resin 828 was blended at room temperature with essentially stoichiometric amounts of different monoamines (and one amine containing one primary and one secondary amine group) in small polypropylene beakers by stirring until homogeneous. The mixtures were then cured in the beakers for 1 hour at 60° C. and then for 1.5 hours at 100° C. The castings were removed from the beakers and tested for glass transition temperature by Differential Scanning Calorimetry (DSC). The physical appearance and feel of each casting was noted. Results are shown in Table 1 below.







TABLE 1







Cure of EPON Resin 828 with Various Monoamines and One Diamine













Amine hydrogen


Tg




equivalent
EPON Resin
Amine,
(midpoint
Appearance


Amine
weight
828, grams
grams
by DSC)
of casting















2-Aminoethanol, parts
30.54
8.6
1.4
72.16
Hard, brittle


N-(3-aminopropyl)morpholine, parts
72.1
7.2
2.8
61.89
Hard, somewhat







tough


CORSAMINE1 PCD, parts (coconut-
96
6.6
3.4
21.09
Hard, very


derived distilled fatty monoamine)




tough


CORSAMINE PO, parts
135
5.8
4.2
7.58
Rubbery


(oleylamine)


TOMAMINE2 PA-12 EH, parts
96.4
6.6
3.4
12.28
Rubbery


(3-(2-ethylhexyloxy)propylamine)


TOMAMINE PA-17, parts
130.5
5.9
4.1
12.06
Rubbery


(3-(branched


tridecyloxy)propylamine)


CORSAMINE DO, parts
109.8
6.3
3.7
31.4
Hard, tough


(3-(oleylamino)propylamine)





1CORSAMINE amines are commercially available from Corsicana Technologies, Inc.


2TOMAMINE amines are commercially available from Air Products






A number of the cured mixtures, including the one cured with CORSAMINE PO, appeared to be melted at 100° C. and a thread could be drawn from the melt with a stick. However, when the mixtures were cooled to room temperature, they became tough rubbery or hard plastic materials.
The results above illustrate the tough rubbery or tough hard plastic nature of EPON Resin 828 cured with a number of the monoamines, particularly in the 12-22 carbon chain length range.
Example 2
Cure of EPON Resin 828 with Different Long-Chain Monoamines at Different Stoichiometric Ratios
Mixtures of EPON Resin 828 were prepared with a distilled oleylamine (CORSAMINE POD), a distilled monoamine derived from coconut fatty acid (CORSAMINE PCD), 3-(2-ethylhexyloxy)propylamine (TOMAMINE PA-12EH) and crystalline solid octadecylamine. The blends with the three first amines (which were liquids) were prepared at room temperature by simple hand mixing and then degassed in a centrifuge. The blends with the crystalline solid octadecylamine were prepared by melting the amine, mixing similarly with EPON Resin 828 and then degassing in a centrifuge. Castings 1⁄8′′ (3.175 mm) thick were prepared by pouring the mixtures into molds made from two sheets of glass (previously treated with a mold release agent) and curing overnight at room temperature and then for 4 hours at 60° C. and 2 hours at 100° C. The castings were tested for solubility in tetrahydrofuran (THF) at room temperature. Those insoluble in THF at room temperature were then tested for solubility in 1,3-diisopropylbenzene (DIPB) at 140° C. Those insoluble in DIPB at 140° C. were then tested for solubility at 140° C. in a 2:1 mixture of DIPB with N-methylpyrrolidone (NMP). Specimens from the castings were put in a 150° C. oven and their ability to flow at this temperature was determined. Molecular weights of the soluble cured castings (or of the THF-soluble material, if the casting was not completely soluble) were determined by gel permeation chromatography (GPC) with a UV absorption detector at 254 nm wavelength. Bars for tensile testing were cut from the castings and tensile properties were determined (ASTM D-638). Results are shown in Tables 2A through 2D below.







TABLE 2A







Cure of EPON Resin 828 with Distilled Oleylamine (CORSAMINE POD)












Casting #26932-
133-1
143-1
133-2
143-2
133-3















NH/epoxy ratio
0.75
0.875
1
1.125
1.25


EPON Resin 828,
100
122.5
100
110.4
100


grams


Corsamine POD, grams
54.1
77.5
72.2
89.6
90.2


Casting appearance
Tacky, flowing;
Self-adherent but
Nontacky,
Tacky,
Tacky,



became hard and
retracts after
flexible
flowing
flowing



tough after a
deformation



few days


Completely soluble in
Yes
No
No
Yes
Yes


THF at 25° C.?


Completely soluble in

Yes
Yes


DIPB at 140° C.?


Flow at 150° C.?
Yes

Questionable

Yes


GPC, Mn
1523
1297
 3167 (a)
3380
4269


GPC, Mw
3785
6051
13495 (a)
11916
7912


GPC, Mz
5786
11505
25044 (a)
19989
11960


Tensile strength, MPa


6.21


Tensile modulus, MPa


1.62


Tensile elongation, %


869





(a) GPC data for the portion of the cured casting which was soluble in THF at room temperature













TABLE 2B







Cure of EPON Resin 828 with Distilled


Coconut Fatty Amine (Corsamine PCD)










Casting #26932-
143-5
143-6
143-7













NH/epoxy ratio
0.875
1
1.125


EPON Resin 828, grams
126.7
122.5
110.4


Corsamine POD, grams
54.1
77.5
89.6


Casting appearance
Flexible but
Flexible,
Self-adherent;



easily broken
tough
somewhat flowing;





brittle at low





temp.


Completely soluble in
No
Yes
Yes


THF at 25° C.?


Completely soluble in
Yes


DIPB at 140° C.?


GPC, Mn
1441
4642
5473


GPC, Mw
5451
14605
12404


GPC, Mz
9950
28395
20085


Tensile strength, MPa
5.83
13.7
0.24


Tensile modulus, MPa
114.3
15.0
18.8


Tensile elongation, %
392
608
277
















TABLE 2C







Cure of EPON Resin 828 with 3-(2-ethylhexyloxy)propylamine (Tomamine PA-12 EH)












Casting #26932-
133-4
143-3
133-5
143-4
133-6















NH/epoxy ratio
0.75
0.875
1
1.125
1.25


EPON Resin 828, grams
100
137.8
100
126.6
100


Tomamine PA-12 EH,
38.7
62.2
51.6
73.4
64.4


grams


Casting appearance
Tacky, flowing;
Nontacky,
Nontacky,
Tacky,
Tacky,



became hard and
retracts after
flexible
flowing
flowing



tough after a
deformation



few days


Completely soluble in
Yes
Yes
No
Yes
Yes


THF at 25° C.?


Completely soluble in


No


DIPB at 140° C.?


Completely soluble in 2:1


Yes


DIPB:NMP at 140° C.?


Flow at 150° C.?
Yes

Questionable

Yes


GPC, Mn
1477
1625
 2576 (a)
4741
2965


GPC, Mw
3987
5555
10325 (a)
13326
7619


GPC, Mz
6513
10323
19292 (a)
23994
12743


Tensile strength, MPa

0.065
3.54


Tensile modulus, MPa

9.93
1.00


Tensile elongation, %

2305 (b)
685





(a) GPC data for the portion of the cured casting which was soluble in THF at room temperature


(b) High tensile elongation value showed flow with little retractive force (apparent modulus dropping dramatically after the initial application of force). This is seen in the extremely low tensile strength of this sample.













TABLE 2D







Cure of EPON Resin 828 with Octadecylamine (Aldrich)










Casting #26932-
133-7
133-8
133-9













NH/epoxy ratio
0.75
1
1.25


EPON Resin 828,
100
100
100


grams


Octadecylamine,
54.1
72.2
90.2


grams


Casting
Tacky, flowing;
Nontacky,
Tacky, flowing;


appearance
became brittle
flexible
became brittle



after a few

after a few



days

days


Completely soluble
Yes
Yes
Yes


in THF at 25° C.?


Flow at 150° C.?
Yes
Yes
Yes


GPC, Mn
1454
10626
3685


GPC, Mw
4371
23115
6788


GPC, Mz
7135
34135
9899


Tensile strength, MPa

3.85


Tensile modulus, MPa

0.922


Tensile elongation, %

724









From the tables above one can see that the castings which were significantly off stoichiometric balance (with an amine/epoxy ratio less than or equal to 0.875 or greater than or equal to 1.125) generally tended to be tacky, self-adherent and sometimes flowing. The amine-rich castings tended to retain this adhesiveness and flowability with time. By contrast, some of the epoxy-rich castings (26932-133-1, -133-4 and -133-7) tended to become hard and tough (or in the case of the octadecylamine casting, brittle) after standing for several days or weeks, possibly due to slow polymerization of the residual epoxy groups. The castings at stoichiometric balance were typically strong and flexible with extremely high elongation values typical of rubbers.
All of the as-prepared castings were soluble in some solvent, showing the absence of crosslinking. Most were soluble in THF at 25° C., with all of the others being soluble either in DIPB or in a DIPB/NMP mixture at 140° C. GPC results generally showed that molecular weight was maximum at an NH/epoxy ratio of 1, as would be expected. The higher molecular weight may have given some tenacity (and resistance to flow) to these castings in the absence of crosslinking. Three of the epoxy-rich castings (26932-133-1, -133-4 and -133-7), which were soft and tacky after the initial cure cycle but became hard and tough after standing at room temperature for 6 weeks, were tested again for solubility after this time. By then they had become insoluble in THF at room temperature and were also insoluble in DIPB or DIPB/NMP at 140° C. These solubility results suggested that these epoxy-rich castings had indeed become crosslinked on standing.
The off-stoichiometric castings made with octadecylamine (Table 2D), which were initially soft and tacky, tended to become brittle (though still soft) and translucent (rather than transparent as they initially were) upon standing at room temperature. This embrittlement may have been caused by wax-type crystallization of the linear saturated hydrocarbon chains of the octadecylamine. The casting made with octadecylamine at stoichiometric balance did not seem to have this problem, perhaps because the higher molecular weight and viscosity made side-chain crystallization more difficult. The results were particularly surprising given the poor properties claimed in Example 1 of U.S. Pat. No. 2,915,485 for a casting of stoichiometrically equivalent amounts of octadecylamine and a resin similar to EPON Resin 828. In that prior art example, the casting was claimed to be very weak and easily shattered under impact—differing completely from the behavior of materials of the invention prepared from octadecylamine and similar monoamines.
Example 3
Cure of EPON Resin 828 (Optionally Diluted with Neopentyl Glycol Diacrylate) with Distilled Oleylamine (CORSAMINE POD) and an Optional Crosslinker
Blends of EPON Resin 828 (optionally diluted with neopentyl glycol diacrylate, NPGDA) with a distilled oleylamine (CORSAMINE POD) and an optional crosslinker (Jeffamine D-400, a poly(propylene oxide) diamine with a molecular weight of approximately 400) were prepared in paper gel time cups by hand-mixing rapidly at room temperature (or at slightly elevated temperature when indicated) with a tongue depressor. Except where noted, the resins and curing agents were mixed in approximate stoichiometric balance (one amine hydrogen atom per epoxy group). The cups were then placed into a Shyodu gel timer set at the indicated temperature with a rotating probe. The elapsed time at which probe rotation stopped was taken as the gel time. Results are shown in Table 3 below.
Castings were also prepared by pouring the mixture into a mold made from two sheets of glass (previously treated with a mold release agent) and curing overnight at room temperature and then for 4 hours at 60° C. and 2 hours at 100° C. Bars for tensile testing were cut from the castings and tensile properties were determined (ASTM D-638). Results are shown in Table 3 below.







TABLE 3







Cure of EPON Resin 828 (optionally diluted with neopentyl glycol diacrylate (NPGDA)) with


distilled oleylamine (CORSAMINE POD) and an optional crosslinker (Jeffamine D-400)



















Jeffamine3
Gel time,
Tensile
Tensile
Tensile


Expt. #
EPON Resin
NPGDA,
Corsamine
D-400,
50° C. start (not
strength,
modulus,
elong.,


26932-
828, parts
parts
POD, parts
parts
thermostatted)
MPa
MPa
%


















97-3
58

42

345′ 18′′
2.89
0.431
1203


99-1
59.3

34.6
6.1

4.73
1.41
606


99-2
60.5

27.6
11.9

5.42
1.91
379


97-2
51
5.7
43.3

688′ 03′′
0.089
0.538
1533


99-3
52.2
5.8
35.7
6.3

2.05
0.607
460


99-4
53.3
5.9
28.6
12.2

1.72
0.780
278





3JEFFAMINE amines are commercially available from Huntsman Corporation






From Table 3 above one can note that a number of the cured castings have extremely high elongation values, values which are typical of commercial vulcanized and thermoplastic rubbers rather than of prior art flexible epoxies (which typically have tensile elongation values in the 100% range). Combinations of tensile properties are shown relative to prior art epoxies in FIG. 1. Casting 97-3 in Table 3 above would partially “melt” and form a bond to an aluminum surface when heated to 200° C. The bond became strong when the material was cooled to room temperature. The casting would not completely dissolve in THF at room temperature but would completely dissolve in DIPB at 140° C., indicating that crosslinking was not present.
Example 4
Accelerated Cure of EPON Resin 828 (Diluted with Trimethylolpropane Triacrylate (TMPTA) or Neopentyl Glycol Diacrylate (NPGDA)) with Distilled Oleylamine (CORSAMINE POD) and an Optional Crosslinker
To a 2-liter glass round bottom flask (fitted with a paddle stirrer) were added 50 grams of ammonium tetrafluoroborate and 450 grams of CORSAMINE POD (distilled oleylamine). The mixture was heated to 50-60° C. and stirred for one hour in this temperature range to dissolve the ammonium tetrafluoroborate. The solution (26932-100) was filtered to remove a small amount of insoluble material and then used as a masterbatch for introducing the ammonium tetrafluoroborate accelerator into the following curing compositions.
Blends of EPON Resin 828 (diluted with trimethylolpropane triacrylate (TMPTA) or neopentyl glycol diacrylate (NPGDA)) with a distilled oleylamine (CORSAMINE POD) and an optional crosslinker (Jeffamine D-400, a poly(propylene oxide) diamine with a molecular weight of approximately 400) and ammonium tetrafluoroborate accelerator (introduced as the above solution in CORSAMINE POD) were prepared in paper gel time cups by hand-mixing rapidly at room temperature (or at slightly elevated temperature when indicated) with a tongue depressor. Except where noted, the resins and curing agents were mixed in approximate stoichiometric balance (one amine hydrogen atom per epoxy group). The cups were then placed into a Shyodu gel timer set at the indicated temperature with a rotating probe. The elapsed time at which probe rotation stopped was taken as the gel time. Results are shown in Table 4 below.







TABLE 4







Cure of EPON Resin 828 (diluted with trimethylolpropane triacrylate (TMPTA) or neopentyl


glycol diacrylate (NPGDA)) with distilled oleylamine (CORSAMINE POD) and an optional


crosslinker (Jeffamine D-400) accelerated with ammonium tetrafluoroborate



















Jeffamine

Gel time,


Expt. #
EPON Resin
TMPTA,
NPGDA,
Corsamine
D-400,
NH4BF4,
50° C. start (not


26932-
828, parts
parts
parts
POD, parts
parts
parts
thermostatted)

















103-8
51.2
5.1

43.7

1.0
59′ 39′′


103-7
44.3
10.2

45.5

1.0
18′ 27′′


102-5
52.2

5.8
35.7
6.3
1.0
33′ 47′′


102-6
53.3

5.9
28.6
12.2
1.0
45′ 22′′









From the results in Table 4 above one can see that addition of approximately 1% of ammonium tetrafluoroborate accelerator, based on the weight of the total system, dramatically shortens gel times for cure with the monoamine or monoamine-diamine mixtures in comparison with similar but unaccelerated systems in Table 3.
Comparative Example 5
Cure of EPON Resin 828 (Optionally Diluted with Trimethylolpropane Triacrylate) with a Standard Flexibilizing Curing Agent (Jeffamine D-2000) Blended with a Small Amount of a Low-Viscosity Monoprimary Amine (N-(3-aminopropyl)morpholine)
Blends of EPON Resin 828 (optionally diluted with trimethylolpropane triacrylate, TMPTA) with a standard “flexible” curing agent (Jeffamine D-2000, a poly(propylene oxide) diamine with a molecular weight of approximately 2000) blended with a small amount of a low-viscosity monoamine (N-(3-aminopropyl)morpholine, APM) were prepared in paper gel time cups by hand-mixing rapidly at room temperature (or at slightly elevated temperature when indicated) with a tongue depressor. Except where noted, the resins and curing agents were mixed in approximate stoichiometric balance (one amine hydrogen atom per epoxy group). The cups were then placed into a Shyodu gel timer set at the indicated temperature with a rotating probe. The elapsed time at which probe rotation stopped was taken as the gel time. Results are shown in Table 5 below.
Castings were also prepared by pouring the mixture into a mold made from two sheets of glass (previously treated with a mold release agent) and curing overnight at room temperature and then for 4 hours at 60° C. and 2 hours at 100° C. Bars for tensile testing were cut from the castings and tensile properties were determined (ASTM D-638). Results are shown in Table 5 below.







TABLE 5







Cure of EPON Resin 828 (optionally diluted with trimethylolpropane triacrylate (TMPTA))


with a long-chain flexibilizing poly(propylene oxide) diamine (Jeffamine D-2000) blended


with a small amount of a low-viscosity monoamine (N-(3-aminopropyl)morpholine, APM)


















Jeffamine

Gel time,
Tensile
Tensile
Tensile


Expt. #
EPON Resin
TMPTA,
D-2000,
APM,
50° C. start (not
strength,
modulus,
elong.,


26932-
828, parts
parts
parts
parts
thermostatted)
MPa
MPa
%


















92-2
41

50.1
8.9
Ungelled after
1.85
1.86
160


(98-2)




4328 minutes


92-1
20.4
13.6
56.1
9.9
2464′ 07′′
0.598
0.877
90


(98-1)









Gel times of these systems, as can be seen from Table 5, were extremely long, with very poor cure speed at room temperature compared with the invention compositions. Also, the combinations of tensile strength and elongation were relatively poor compared to the invention compositions (cf. FIG. 1 in Example 7).
Example 6
Preparation of a Condensate (26932-85) of N-(2-aminoethyl)piperazine (AEP) with Dimerized Fatty Acid (AEP-Dimer Condensate), Blending with Monofunctional Amines, and Use of a Number of the Mixtures of AEP-Dimer Condensate and Monofunctional Amines to Cure Epoxy Resins and their Mixtures with Multifunctional Acrylate Esters
In a 4-neck, 5-liter round bottom flask fitted with a paddle stirrer and a distillation takeoff were mixed 1824 grams of N-(2-aminoethyl)piperazine (AEP) and 1976 grams of dimerized fatty acid (Unidyme 18, Arizona Chemical). Heating was started at atmospheric pressure with stirring. Distillation of a mixture of reaction water and excess AEP started at 169° C. When the pot temperature reached 225° C. (after about 11⁄2 hours of heating), the atmospheric pressure distillate was drained from the receiver and vacuum was applied to distill the remaining unreacted AEP. In about 45 minutes of further heating, the temperature was raised to 235° C. and the pressure was gradually dropped to about 800-1000 Pa. The pressure was kept in this range for about 20 minutes until distillation stopped. The final residual product in the pot had an amine nitrogen equivalent weight of 213 (corresponding to an amine hydrogen equivalent weight of approximately 400) and a Brookfield viscosity of 194.6 Pa-s (194600 cP) at 25° C. and of 27 Pa-s (27000 cP) at 40° C. The product is referred to as “AEP-dimer condensate”.
Blending experiments were carried out with the AEP-dimer condensate and a number of monoprimary aliphatic amines. The AEP-dimer condensate and monoprimary amine were mixed (with slight heating as necessary) until homogeneous and 25° C. Brookfield viscosity was determined. Results are shown in Table 6A below (indicating the very strong ability of the monoprimary amines to lower the viscosity of the AEP-dimer condensate).







TABLE 6A







Blending of AEP-dimer condensate with various monoprimary


amines and viscosity determination of blends

















Experiment# 26932-90-
1
2
10
3
9
7
4
8
11
5




















AEP-dimer condensate, grams
16
14
17
16
15
16
16
15
15
14


Surfonamine4 B-30, g (1)
4
6


3-Aminopropyl-morpholine,


3
4
5


grams


2-Aminoethanol, g





4


Armeen5 OL, g






4
5

6


Corsamine PO, g








5


25° C. Brookfield viscosity,
8125
2625
8075
4220
2115
6963
5463
3000
3105
1825


mPa-s (cP)





4SURFOAMINE amines are commercially available from Hunstman Corporation


5ARMEEN amines are commercially available from Akzo Nobel






Blends for gel time tests were prepared in paper gel time cups (as in Example 3) by hand-mixing rapidly at room temperature (or at slightly elevated temperature when indicated) with a tongue depressor. Except where noted, the resins and curing agents were mixed in approximate stoichiometric balance (one amine hydrogen atom per epoxy group or acrylate double bond). The cups were then placed into a Shyodu gel timer set at the indicated temperature with a rotating probe. The elapsed time at which probe rotation stopped was taken as the gel time. Results are shown in Table 6B below.
Castings were also prepared by pouring the mixture into a mold made from two sheets of glass (previously treated with a mold release agent) and curing overnight at room temperature and then for 4 hours at 60° C. and 2 hours at 100° C. Bars for tensile testing were cut from the castings and tensile properties were determined (ASTM D-638). Results are shown in Table 6B below.







TABLE 6B







Cure of EPON Resin 828 (optionally diluted with trimethylolpropane triacrylate (TMPTA) or neopentyl glycol diacrylate


(NPGDA)) with AEP-dimer condensate blended with oleylamine (CORSAMINE PO) or N-(3-aminopropyl)morpholine (APM)

















Expt. #



AEP-dimer


Gel time, 50° C.
Tensile
Tensile
Tensile


26932-
EPON Resin
TMPTA,
NPGDA,
condensate,
Corsamine
APM,
start (not
strength,
modulus,
elong.,


94-
828, parts
parts
parts
parts
POD, parts
parts
thermostatted)
MPa
MPa
%




















2-A
41.7


43.7
14.6


26.2
258
378


1-A
21
14

48.8
16.2

 4′ 01′′
1.37
0.405
517


3-A
36.4

4
44.7
14.9

50′ 03′′
9.98
3.24
670


2-B
49.0


39.8

11.2

49.7
1229
59


1-B
25
16.7

45.5

12.8
 3′ 33′′
1.17
0.554
296


3-B
42.7

4.8
41.0

11.5
28′ 29′′
34.8
856
134









Example 7
Comparison of Tensile Data for Systems from Examples 2-6 with Prior Art Systems
FIG. 1 is a plot of tensile elongation versus tensile strength for systems described in the above examples versus a number of prior art systems (including those in Comparative Example 5). Optimum properties are in the upper right of the graph. Tensile strength, in the normal pattern, decreases as tensile elongation increases in the systems. One can see from FIG. 1, however, that the prior art systems, with one exception (828/AEP-dimer condensate), generally fall well below and/or to the left of the curve of the systems having a combination of the highest tensile strength and highest elongation. These prior art systems include 1) a commercial membrane system (based on a diluted bisphenol A epoxy resin cured with an amine adduct of a glycidated poly(propylene oxide) as disclosed in U.S. Pat. No. 6,127,508, FIG. 1, plot symbol “C”, a diglycidyl ester of a dimerized fatty acid cured with isophoronediamine, EPON Resin 828 cured with a commercial “dimer diamine” produced by making the dinitrile from a dimer acid followed by hydrogenation as disclosed in U.S. Pat. No. 6,500,912, FIG. 1, plot symbol “K”, EPON Resin 828 cured with a condensate of N-(2-aminoethyl)piperazine and dimerized fatty acid (“AEP-dimer condensate”) as disclosed in U.S. Pat. No. 6,127,508, FIG. 1, plot symbol “E” and two systems cured predominantly with Jeffamine D-2000 (from Comparative Example 5). The only prior art system rivaling the invention systems in balance of tensile properties was that based on EPON Resin 828 cured with AEP-dimer condensate (similar to the material made in Example 6). As noted in Example 6, however, the AEP-dimer condensate is extremely high in viscosity and hence EPON Resin 828 cured with AEP-dimer condensate is also very high in viscosity (and deficient in processability) compared with the invention systems. This high viscosity significantly limits commercial applications.
While the present invention has been described and illustrated by reference to particular embodiments, those of ordinary skill in the art will appreciate that the invention lends itself to variations not necessarily illustrated herein. For this reason, then, reference should be made solely to the appended claims for purposes of determining the true scope of the present invention.

## Claims

1. A composition comprising an epoxy resin system, the epoxy resin system comprising a reaction product of:
an epoxy resin component;
a curing agent comprising a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms; and
an accelerator selected from the group consisting of sulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, IIA and transition metals of the Periodic Table (CAS version); inorganic acids, carboxylic acids, phenolic compounds, imidazoles, cyanamide, sulfonamides, and imides;
wherein the curing agent is substantially free of a crosslinking agent having at least 3 active hydrogen atoms; and
wherein, when cured, the reaction product exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C., wherein the composition is free of asphalt.

2. The composition of claim 1 wherein the curing agent further comprises an amine terminated polyamide which is the reaction product of a dimerized fatty acid or hydrogenated dimerized fatty acid with an amine containing one primary and one secondary amine group or two secondary amine groups.

3. The composition of claim 2 wherein the amine terminated polyamide is prepared by reacting:
(a) carboxylic acids selected from C18-C60 dicarboxylic acids, C18-C60 dicarboxylic acid derivatives and mixtures thereof, wherein the carboxylic acids optionally contain di- or polycarboxylic acids or acid derivatives having from 4 to 20 carbon atoms in an amount ranging from 0-10% based on all carboxylic acids; and
(b) at least one amine having the formula:


R1—NH—R2—NH—R3 



wherein R1 has a total number of carbon atoms from 0 to about 20 and is selected from the group consisting of hydrogen, alkyl, cycloalkyl, alkenyl, arylalkyl, hydroxyalkyl, alkoxyalkyl, cyanoalkyl, alkylthioalkyl, dialkylaminoalkyl, aryl, alkylaryl, cyanoaryl, alkoxyaryl, alkylthioaryl, and dialkylaminoaryl;
R3 has a total number of carbon atoms from 1 to about 20 and is selected from the group consisting of alkyl, cycloalkyl, alkenyl, arylalkyl, hydroxyalkyl, alkoxyalkyl, cyanoalkyl, alkylthioalkyl, dialkylaminoalkyl, aryl, alkylaryl, cyanoaryl, alkoxyaryl, alkylthioaryl, and dialkylaminoaryl; and
R2 is (CR4R5)n, wherein n is from 2 to about 20, R4 is independently selected for each (CR4R5) from the group consisting of H, alkyl, aryl, hydroxyl, alkoxy, alkylthio, dialkylamino and cyano; and R5 is independently selected for each (CR4R5) from the group consisting of H, alkyl and aryl.

4. The composition of claim 2 wherein the amine terminated polyamide is prepared by reacting:
at least one C18-C50 dicarboxylic acid, dicarboxylic acid ester or dicarboxylic acid chloride with an aminoalkylpiperazine having the formula:





wherein R1 is hydrogen and R2 is —R3—NH2 wherein R3 is a divalent aliphatic linkage with optional —CHR4 and —CR4R5 units, wherein R4 and R5 are independently alkyl groups.

5. The composition of claim 1 wherein the epoxy resin system further comprises a monofunctional or polyfunctional epoxy diluent.

6. The composition of claim 1 wherein the epoxy resin system further comprises a polyacrylate ester of a polyol or polymethacrylate ester of a polyol.

7. The composition of claim 1 wherein the epoxy resin system further comprises one or more amine-containing curing agents comprising a primary amine moiety or two or more primary or secondary amine or amide moieties linked to a common central organic moiety.

8. The composition of claim 1 wherein the monoprimary amine comprises one or more primary fatty amines selected from the group consisting of octylamines, laurylamines, myristylamines, palmitylamines, stearylamines, oleylamine, tallowamines, hydrogenated tallow amines, cetylamines, N-tetradecylamine, cocoamines, soyamines, and combinations thereof.

9. The composition of claim 1 wherein the curing agent has a Brookfield viscosity of 3000 cP or less at 25° C.

10. The composition of claim 1 wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a Tg below 30° C. as measured by Differential Scanning Calorimetry.

11. A composition comprising a curable epoxy resin system, the curable epoxy resin system comprising a reaction product of:
an epoxy resin component;
a curing agent consisting essentially of a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms; and
an accelerator selected from the group consisting of sulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, IIA and transition metals of the Periodic Table (CAS version); inorganic acids, carboxylic acids, phenolic compounds, imidazoles, cyanamide, sulfonamides, and imides:
wherein the curing agent is substantially free of a crosslinking agent having at least 3 active hydrogen atoms;
wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C, wherein the composition is free of asphalt.

12. A composition comprising an epoxy resin system, the epoxy resin system comprising a reaction product of:
an epoxy resin component;
a curing agent comprising greater that 70 wt % of a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms; and
an accelerator selected from the group consisting of sulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, HA and transition metals of the Periodic Table (CAS version); inorganic acids, carboxylic acids, phenolic compounds, imidazoles, cyanamide, sulfonamides, and imides;
wherein the curing agent is substantially free of a crosslinking agent having at least 3 active hydrogen atoms;
wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C, wherein the composition is free of asphalt.

13. The composition of claim 12 wherein the curing agent further comprises an amine terminated polyamide which is the reaction product of a dimerized fatty acid or hydrogenated dimerized fatty acid with an amine containing one primary and one secondary amine group or two secondary amine groups.

14. The composition of claim 11 wherein the curing agent has a Brookfield viscosity of 3000 cP or less at 25° C.

15. The composition of claim 11 wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a Tg below 30° C. as measured by Differential Scanning Calorimetry.

16. The composition of claim 12 wherein the curing agent has a Brookfield viscosity of 3000 cP or less at 25° C.

17. The composition of claim 12 wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a Tg below 30° C. as measured by Differential Scanning Calorimetry.

18. A composition comprising an epoxy resin system, the epoxy resin system comprising a reaction product of:
an epoxy resin component;
a curing agent comprising less than 20 wt % of a monoprimary amine represented by the formula R—NH2 wherein R is a hydrocarbyl group containing between about 8 and about 50 carbon atoms; and
an accelerator selected from the group consisting of sulfonates, phosphonates, sulfates, tetrafluoroborates, carboxylates and nitrates of Groups IA, IIA and transition metals of the Periodic Table (CAS version); inorganic acids, carboxylic acids, phenolic compounds, imidazoles, cyanamide, sulfonamides, and imides;
wherein the curing agent is substantially free of a crosslinking agent having at least 3 active hydrogen atoms;
wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a tensile strength of >1 MPa and an elongation of >100% as measured by ASTM D-638 at 25° C, wherein the composition is free of asphalt.

19. The composition of claim 18 wherein the curing agent has a Brookfield viscosity of 3000 cP or less at 25° C.

20. The composition of claim 18 wherein, when cured, the reaction product of the epoxy resin component and the curing agent exhibits a Tg below 30° C. as measured by Differential Scanning Calorimetry.

21. The composition of claim 7 wherein the one or more amine-containing curing agents comprise a diamine.

22. The composition of claim 7 wherein the one or more amine-containing curing agents comprise an aliphatic diamine, a polyoxypropylene diamine, and a cycloaliphatic diamine.

23. The composition of claim 1, wherein the accelerator is selected from the group consisting of alkylbenzenesulfonates, HBF4, H2SO4, H2NSO3H, and H3PO4, salicylic acid, lactic acid, glycolic acid, resorcylic acid, phenol, t-butylphenol, nonylphenol, bisphenol A, dicyandiamide, cyanamide, p-toluenesulfonamide, phthalimide, succinimide, maleimide, perylenetetracarboxylic diimide, saccharin, calcium nitrate, calcium alkylbenzene sulfonates, magnesium alkanesulfonates, tetrafluoroboric acid, dichloroacetic acid, trifluoroacetic acid, thiocyanic acid and mercaptoacetic acid.