# Patent

## Title
Semi-insulating group III metal nitride and method of manufacture

## Abstract

A large-area, high-purity, low-cost single crystal semi-insulating gallium nitride that is useful as substrates for fabricating GaN devices for electronic and/or optoelectronic applications is provided. The gallium nitride is formed by doping gallium nitride material during ammonothermal growth with a deep acceptor dopant species, e.g., Mn, Fe, Co, Ni, Cu, etc., to compensate donor species in the gallium nitride, and impart semi-insulating character to the gallium nitride.

## Background
CROSS-REFERENCE TO RELATED APPLICATION
This patent application claims priority from U.S. patent application Ser. No. 61/313,112, filed Mar. 11, 2010, and entitled “Improved Semi-Insulating Group III Metal Nitride and Method of Making.”


BACKGROUND OF THE INVENTION
The present invention generally relates to processing of materials for growth of crystals. More particularly, the present invention provides a semi-insulating gallium-containing nitride crystal synthesized by an ammonobasic or ammonoacidic technique. The present invention provides methods suitable for synthesis of polycrystalline nitride materials, as well as other crystals and materials. Such crystals and materials include, but are not limited to, GaN, AN, InN, InGaN, AlGaN, and AlInGaN, and for manufacture of bulk or patterned substrates. Such bulk or patterned substrates can be used for a variety of applications including optoelectronic devices, lasers, light emitting diodes, solar cells, photoelectrochemical water splitting and hydrogen generation, photodetectors, integrated circuits, and transistors.
Gallium nitride containing crystalline materials serve as substrates for manufacture of conventional optoelectronic devices, such as blue light emitting diodes and lasers. Such optoelectronic devices have been commonly manufactured on sapphire or silicon carbide substrates that differ in composition from the deposited nitride layers. In the conventional Metal-Organic Chemical Vapor Deposition (MOCVD) method, deposition of GaN is performed from ammonia and organometallic compounds in the gas phase. Although successful, conventional growth rates achieved make it difficult to provide a bulk layer of GaN material. Additionally, dislocation densities are also high and lead to poorer optoelectronic device performance.
Quality substrates comprising bulk gallium nitride are available commercially, however, in most cases, these substrates are electrically conductive. In some cases, a substrate that is electrically insulating or semi-insulating is desirable. In addition, bulk gallium nitride substrates are generally expensive, and substrate diameters of 2 inches and larger are only available with a c-plane orientation.
Several authors have disclosed the addition of transition metal deep acceptor dopants, e.g., Mn, Fe, Co, Ni, Cu, etc., to compensate donor species in the gallium nitride, and impart semi-insulating character to the gallium nitride. For example, Monemar and Lagerstedt [J. Appl. Phys. 50, 6480 (1979)] added Fe or Cr to GaN grown by hydride vapor phase epitaxy (HVPE) and obtained highly resistive crystals. Heikman et al. [Appl. Phys. Lett. 81, 439 (2002)] introduced Fe into GaN films grown by metalorganic chemical vapor deposition (MOCVD) and similarly obtained semi-insulating character. Generally, these authors were not able to obtain high quality, free standing bulk GaN wafers.
U.S. Pat. No. 6,273,948, issued to Porowski et al., describes a method of fabricating highly resistive GaN bulk crystals by crystallization from a solution of atomic nitrogen in a molten mixture of gallium and Group II metal such as beryllium or calcium, under a high pressure of about 0.5-2.0 GPa and a high temperature of 1300-1700 degrees Celsius. A resistivity of 104 to 108 ohm-centimeter (ohm-cm) was achieved. The crystal obtained from the process was about 1 cm in size, whereas most commercial electronic applications require a substrate size of at least about 2 inches (>5 cm) diameter.
U.S. Pat. No. 7,170,095, issued to Vaudo et al., describes an improved HVPE method for doping free-standing GaN crystals with relatively high crystalline quality. The HVPE technique, however, generally produces bulk GaN crystals of relatively high cost. U.S. Pat. No. 7,078,731, issued to D'Evelyn et al., teaches an ammonothermal method for synthesizing semi-insulating GaN crystals, for example, by doping with Fe or Co. The Fe-doped and Co-doped GaN crystals, however, are reddish/amber or black in color, respectively, rather than transparent and colorless.
What is needed is a method for low-cost manufacturing of semi-insulating nitride materials that are transparent, colorless, and of high crystallographic quality.


DETAILED DESCRIPTION OF THE INVENTION
Approximating language, as used herein throughout the specification and claims, may be applied to modify any quantitative representation that could permissibly vary without resulting in a change in the basic function to which it may be related. Accordingly, a value modified by a term such as “about” is not limited to the precise value specified. In at least one instance, the variance indicated by the term “about” may be determined with reference to the precision of the measuring instrumentation. Similarly, “free” may be combined with a term; and, may include an insubstantial number, or a trace amount, while still being considered free of the modified term unless explicitly stated otherwise.
The metal of a metal nitride may include a group III metal. Suitable metals may include aluminum, gallium, and indium. The “one or more” refers to combination of metals in the metal nitride, and may include compositions such as aluminum gallium nitride (AlGaN), and the like. As used herein, the term “gallium nitride” will be used as an illustrative example of a metal nitride, but it is understood that other group III metal nitrides are also possible.
A metal nitride composition may contain impurities. As used herein, the term “impurity” refers to a chemical species that is distinct from the group III metal nitride that constitutes the majority composition of the single-crystal or polycrystalline metal nitride. Several classes of impurities may be distinguished, with respect to chemistry, atomic structure, intent, and effect. Impurities will generally comprise elements distinct from nitrogen, aluminum, gallium, and indium, including oxygen, carbon, halogens, hydrogen, alkali metals, alkaline earth metals, transition metals, and main block elements. The impurity may be present in a number of forms, with different atomic structure. In some cases, the impurity is present as an isolated atom or ion within the crystalline lattice of the group III metal nitride, for example, as a substitutional or interstitial impurity. In other cases, the impurity is present in a distinct phase, for example, as an inclusion within an individual group III metal nitride grain or within a grain boundary of the group III metal nitride. The impurity may be deliberately added, to enhance the properties of the group III metal nitride in some way, or may be unintentional. Finally, the impurity may or may not have a significant effect on the electrical, crystallographic, chemical, or mechanical properties of the group III metal nitride.
As used herein, and as is commonly used in the art, the term “dopant” refers to an impurity that is atomically dispersed within the group III metal nitride, for example, as a substitutional or interstitial impurity, and which is typically added intentionally. With regard to dopants and dopant precursors (collectively “dopants” unless otherwise indicated), the electrical properties of the group III metal nitride composition may be controlled by adding one or more of such dopants to the above composition during processing. The dopant may also provide magnetic and/or luminescent properties to the group III metal nitride composition. Suitable dopants may include one or more of s or p block elements, transition metal elements, and rare earth elements. Suitable s and p block elements include, for example, silicon, germanium, magnesium, and tin. Other suitable dopants may include transition group elements. Suitable transition group elements include, for example, zinc, iron, or cobalt. Suitable dopants may produce an n-type material, a p-type material, or a semi-insulating material. In some embodiments, oxygen, whether added intentionally or unintentionally, also acts as a dopant.
Suitable dopant concentration levels in a single-crystal or polycrystalline composition may be greater than about 1010 atoms per cubic centimeter. In one embodiment, the dopant concentration may be in a range of from about 1010 atoms per cubic centimeter to about 1015 atoms per cubic centimeter, from about 1015 atoms per cubic centimeter to about 1016 atoms per cubic centimeter, from about 1016 atoms per cubic centimeter to about 1017 atoms per cubic centimeter, from about 1017 atoms per cubic centimeter to about 1018 atoms per cubic centimeter, from about 1018 atoms per cubic centimeter to about 1021 atoms per cubic centimeter, or greater than about 1021 atoms per cubic centimeter.
As used herein, the term “getter” refers to an impurity that is intentionally added and has a higher chemical affinity for an undesired impurity, for example, oxygen, than the principal metallic constituent of the composition, for example, gallium. The getter may become incorporated into the polycrystalline group III metal nitride in the form of an inclusion, for example, as a metal nitride, a metal halide, a metal oxide, a metal oxyhalide, or as a metal oxynitride. Examples of suitable getters include the alkaline earth metals, scandium, titanium, vanadium, chromium, yttrium, zirconium, niobium, the rare earth metals, hafnium, tantalum, and tungsten, and their nitrides and halides. In some embodiments, the getter impurity can act as both a getter and a dopant, such as magnesium. In other cases, the getter impurity atom has a larger atomic or covalent diameter than gallium and does not become incorporated as a dopant at sufficient levels to modify the electrical properties of the group III metal nitride significantly, and therefore functions predominantly or exclusively as a getter. The getter may be present in the polycrystalline group III metal nitride at a level greater than 100 ppm, from about 100 ppm to about 200 ppm, from about 200 ppm to about 500 ppm, from about 500 ppm to about 0.1%, from about 0.1% to about 0.2%, from about 0.2% to about 0.5%, from about 0.5% to about 2%, from about 2% to about 10%, or greater than 10%. Parts per million (ppm) and “%” refer to “by weight” unless otherwise indicated.
In other cases, impurities are unintended and/or undesirable inclusions in the polycrystalline group III metal nitride, and may result from, for example, processing and handling. Other unintentional impurities may result from contaminants in raw materials. Some unintentional impurities may be more closely associated with select raw materials. In some embodiments, the unintentional impurity includes oxygen present as a substitutional impurity, or dopant, in the polycrystalline group III metal nitride at higher than the desired level. In other embodiments, the unintentional impurity includes oxygen present as a group III oxide inclusion, for example, Ga2O3, Al2O3, and/or In2O3. The unintentional oxygen impurity may originate from residual oxygen in the metal raw material, from moisture or O2 present as an impurity in the gaseous raw materials used in the synthesis process, from moisture generated from outgassing of the reactor components during the synthesis process, or from an air leak in the reactor. In one embodiment, the oxygen content present as Ga2O3 or as a substitutional impurity within gallium nitride may be less than about 10 parts per million (ppm). In another embodiment, the oxygen content present as Ga2O3 or as a substitutional impurity within gallium nitride may be in a range of from about 10 parts per million to about 3 parts per million, from about 3 parts per million to about 1 part per million, from about 1 part per million to about 0.3 parts per million, from about 0.3 part per million to about 0.1 parts per million, or less than about 0.1 part per million.
A high-quality semi-insulating, transparent, gallium nitride or metal nitride crystal or wafer may be manufactured cost-effectively by the following method.
One or more high-quality gallium nitride seed crystals or plates may be provided. The seed plates may have a minimum lateral dimension of at least one centimeter. In some embodiments, the seed plates have a maximum lateral dimension of at least two centimeters and a minimum lateral dimension of at least one centimeter. In other embodiments, the seed plates have minimum lateral dimensions of at least three centimeters, at least four centimeters, at least five centimeters, at least six centimeters, at least eight centimeters, or at least ten centimeters. In some embodiments, the seed plates are bulk single crystals of gallium nitride. In some embodiments the seed plates are prepared from crystals that were grown by hydride vapor phase epitaxy. In other embodiments, the seed plates are prepared from crystals that were grown ammonothermally. In still other embodiments, the seed plates are prepared from crystals that were grown from solution in a flux. In some embodiments, the dislocation density at the large-area surfaces of the seed plates is less than about 106 cm−2. In some embodiments, the dislocation density at the large-area surfaces of the seed plates is less than about 105 cm−2, less than about 104 cm−2, less than about 103 cm−2, or less than about 102 cm−2. In some embodiments, the full width at half maximum of the x-ray diffraction line corresponding to the crystallographic orientation of the large-area face is less than 300 arc seconds, less than 150 arc seconds, less than 100 arc seconds, less than 50 arc seconds, less than 40 arc seconds, less than 30 arc seconds, or less than 20 arc seconds.
In one specific embodiment, the orientation of the large-area surfaces of the seed plates is within about 5 degrees, within about 2 degrees, within about 1 degree, within about 0.5 degree, within about 0.2 degree, or within about 0.1 degree of a {1 0 −1 0} m plane. In another specific embodiment, the orientation of the large-area surfaces of the seed plates is within about 5 degrees, within about 2 degrees, within about 1 degree, within about 0.5 degree, within about 0.2 degree, or within about 0.1 degree of a (0 0 0 ±1) c plane. In another specific embodiment, the orientation of the large-area surfaces of the seed plates is within about 5 degrees, within about 2 degrees, within about 1 degree, within about 0.5 degree, within about 0.2 degree, or within about 0.1 degree of a {1 1 −2 0} a plane. In some embodiments, the seed plate has a semi-polar large-surface orientation, which may be designated by (hkil) Bravais-Miller indices, where i=−(h+k), l is nonzero and at least one of h and k are nonzero. In a specific embodiment, the orientation of the large-area surfaces of the seed plates is within about 5 degrees, within about 2 degrees, within about 1 degree, within about 0.5 degree, within about 0.2 degree, or within about 0.1 degree of {1 −1 0 ±1}, {1 −1 0 ±2}, {1 −1 0 ±3}, {2 0 −2 ±1} or {1 1 −2 ±2}.
The one or more seed plates may be affixed to a seed rack, as described in U.S. patent application Ser. No. 12/534,844, which is hereby incorporated by reference in its entirety. If the front and back faces of the seed plates are crystallographically inequivalent, as with a c-plane or semi-polar orientation, two seed plates may be placed back to back so that the outward-facing surfaces have an equivalent crystallographic orientation.
A polycrystalline group III metal nitride or gallium nitride nutrient material may be provided, as described in U.S. patent application Ser. No. 61/122,332, which is hereby incorporated by reference in its entirety. The polycrystalline group III metal nitride may have an oxygen content in the group III metal nitride material provided as a group III metal oxide or as a substitutional impurity within a group III metal nitride that is less than about 10 parts per million (ppm), less than about 1 ppm, or less than about 0.1 ppm. The polycrystalline group III metal nitride may comprise a getter at a level of at least 100 ppm with respect to the group III metal, where the getter is selected from at least alkaline earth metals, scandium, titanium, vanadium, chromium, yttrium, zirconium, niobium, rare earth metals, hafnium, tantalum, and tungsten. The polycrystalline group III metal nitride may further comprise a compensatory dopant, at a level between about 1014 cm−3 and about 1020 cm−3, where the compensatory dopant is selected from at least V, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd and Hg. The compensatory dopant may be formed in the polycrystalline group III metal nitride by addition of at least one of V, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd and Hg to gallium or a group III metal prior or during the process whereby the gallium or group III metal is reacted with ammonia in the presence of a hydrogen halide to form the polycrystalline metal nitride.
The polycrystalline group III metal nitride may be placed in a basket, which is then placed in an autoclave or a capsule, as described in U.S. Pat. Nos. 6,656,615, 7,125,453, and 7,078,731 and in U.S. patent application Ser. No. 12/133,365, each of which is incorporated by reference in their entirety. Ammonia and a mineralizer, for example, at least one of an alkali metal, amide, nitride, or azide, an alkaline earth metal, amide, nitride, or azide, ammonium fluoride, ammonium chloride, a group III metal fluoride, a group III metal chloride, or a reaction product between a group III metal, ammonia, HF, and HCl are also placed in the autoclave or capsule.
In some embodiments a getter is also placed in the autoclave or capsule. The added getter may be provided in addition to a getter composition that may be present in the polycrystalline group III nitride. The added getter may comprise at least one of alkaline earth metals, Sc, Ti, V, Cr, Y, Zr, Nb, Hf, Ta, W, rare earth metals, and their nitrides, halides, oxynitrides, oxyhalides, amides, imides, and azides. In one specific embodiment, at least a portion of the getter is added in the form of a metal and at least a portion of the mineralizer is added as an azide in such a ratio that the hydrogen generated by reaction of the getter metal with ammonia and the nitrogen generated by decomposition of the azide are present in a ratio of approximately 3:1, as described in U.S. patent application Ser. No. 61/086,799, which is hereby incorporated by reference in its entirety. The added getter may be useful for removing unintentional impurities, for example, oxygen, that are present in the mineralizer or other raw material. In one set of embodiments, the mineralizer comprises an alkali metal and the getter comprises a nitride, imide, or amide of Be, Mg, Ca, Sr, Ba, Sc. Y, a rare earth metal, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, or W. In another set of embodiments, the mineralizer comprises Cl and the getter comprises a nitride, chloride, oxynitride, or oxychloride of Sc, Cr, Zr, Nb, Hf, Ta, or W. In still another set of embodiments, the mineralizer comprises F and the getter comprises a nitride, fluoride, oxynitride, or oxyfluoride of Cr, Zr, Nb, Hf, Ta, or W.
After all the raw materials have been added to the autoclave or capsule, the autoclave or capsule is sealed.
The capsule, if employed, is then placed within a suitable high pressure apparatus. In one embodiment, the high pressure apparatus comprises an autoclave, as described by U.S. Pat. No. 7,335,262, which is hereby incorporated by reference in its entirety. In another embodiment, the high pressure apparatus is an internally heated high pressure apparatus, as described in U.S. Pat. No. 7,125,453, and in U.S. Patent Applications 2006/0177362A1 and U.S. Ser. No. 12/133,364, which are hereby incorporated by reference in their entirety. The polycrystalline group III metal nitride and seed crystals are then processed in supercritical ammonia at a temperature greater than about 400 degrees Celsius and a pressure greater than about 0.2 gigaPascal (GPa), during which at least a portion of the polycrystalline group III metal nitride is etched away and recrystallized onto at least one group III nitride crystal with a wurtzite structure. In some embodiments, the polycrystalline group III metal nitride is processed in supercritical ammonia at a temperature greater than about 500 degrees Celsius, greater than about 550 degrees Celsius, greater than about 600 degrees Celsius, greater than about 650 degrees Celsius, greater than about 700 degrees Celsius, or greater than about 750 degrees Celsius. In some embodiments, the polycrystalline group III metal nitride is processed in supercritical ammonia at a pressure greater than about 0.3 GPa, greater than about 0.4 GPa, greater than about 0.5 GPa, greater than about 0.6 GPa, greater than about 0.7 GPa, or greater than about 0.8 GPa.
Residual getter in the polycrystalline group III metal nitride is released into solution gradually, as the polycrystalline group III metal nitride is etched. Once in solution, the getter may react to form a getter metal nitride, amide, or halide. The getter may also be chemically bound to oxygen. The getter may remove residual oxygen in the supercritical ammonia solution, enabling growth of group III nitride single crystals with improved purity and transparency, enabling semi-insulating character at lower concentrations of the compensatory dopant.
The ammonothermally-grown crystalline group III metal nitride may be characterized by a wurzite structure substantially free from any cubic entities and have an optical absorption coefficient of about 2 cm−1 and less at wavelengths between about 385 nanometers and about 750 nanometers. An ammonothermally-grown gallium nitride crystal may comprise a crystalline substrate member having a length greater than about 5 millimeters, have a wurtzite structure and be substantially free of other crystal structures, the other structures being less than about 0.1% in volume in reference to the substantially wurtzite structure, an impurity concentration greater than 1014 cm−3, greater than 1015 cm−3, or greater than 1016 cm−3 of at least one of Li, Na, K, Rb, Cs, Mg, Ca, F, and Cl, and an optical absorption coefficient of about 2 cm−1 and less at wavelengths between about 385 nanometers and about 750 nanometers. The ammonothermally-grown gallium nitride crystal may be semi-insulating, with a resistivity greater than 105 Ω-cm, greater than 106 Ω-cm, greater than 107 Ω-cm, greater than 108 Ω-cm, greater than 109 Ω-cm, greater than 1010 Ω-cm, greater than 1011 Ω-cm, or greater than 1012 Ω-cm at room temperature. The ammonothermally-grown crystalline group III metal nitride may be characterized by a concentration of at one or more compensatory dopants that is less than about than 1014 cm−3, less than about than 1015 cm−3, less than about than 1016 cm−3, less than about than 1017 cm−3, less than about than 1018 cm−3, or less than about than 1019 cm−3. The compensatory dopant may be selected from at least V, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd and Hg. In a preferred embodiment, the concentration of the compensatory dopant in the ammonothermally-grown crystalline group III metal nitride is greater than the sum of the concentrations of oxygen and silicon. The optical absorption coefficient of the ammonothermally-grown crystalline group III metal nitride at wavelengths between about 395 nm and about 460 nm may be less than about 10 cm−1, less than about 5 cm−1, less than about 2 cm−1, less than about 1 cm−1, less than about 0.5 cm−1, less than about 0.2 cm−1, or less than about 0.1 cm−1.
By growing for a suitable period of time, the semi-insulating ammonothermally-grown crystalline group III metal nitride may have a thickness of greater than about 1 millimeter and a length, or diameter, greater than about 20 millimeters. In a preferred embodiment, the length is greater than about 50 millimeters or greater than about 100 millimeters. After growth, the ammonothermally-grown crystalline group III metal nitride may be sliced, polished, and chemical-mechanically polished according to methods that are known in the art to form one or more wafers or crystalline substrate members. In a preferred embodiment, the root-mean-square surface roughness of the at least one wafer or crystalline substrate member is less than about one nanometer, for example, as measured by atomic force microscopy over an area of at least about 10 micrometers by 10 micrometers.
The semi-insulating ammonothermally-grown crystalline group III metal nitride crystal, or a wafer sliced and polished from the crystal, may be used as a substrate for fabrication into optoelectronic and electronic devices such as at least one of a light emitting diode, a laser diode, a photodetector, an avalanche photodiode, a transistor, a rectifier, and a thyristor; one of a transistor, a rectifier, a Schottky rectifier, a thyristor, a p-i-n diode, a metal-semiconductor-metal diode, high-electron mobility transistor, a metal semiconductor field effect transistor, a metal oxide field effect transistor, a power metal oxide semiconductor field effect transistor, a power metal insulator semiconductor field effect transistor, a bipolar junction transistor, a metal insulator field effect transistor, a heterojunction bipolar transistor, a power insulated gate bipolar transistor, a power vertical junction field effect transistor, a cascade switch, an inner sub-band emitter, a quantum well infrared photodetector, a quantum dot infrared photodetector, a solar cell, and a diode for photoelectrochemical water splitting and hydrogen generation.
While the above is a full description of the specific embodiments, various modifications, alternative constructions and equivalents may be used. Therefore, the above description and illustrations should not be taken as limiting the scope of the present invention which is defined by the appended claims.

## Claims

1. A bulk gallium-containing nitride crystal comprising:
a length greater than about 5 millimeters;
a wurtzite crystal structure;
a concentration of oxygen from about 1010 atoms per cubic centimeter to about 1017 atoms per cubic centimeter;
an impurity concentration greater than about 1015 cm−3 of at least one of Li, Na, K, Rb, Cs, Ca, F, and Cl;
a compensatory dopant selected from V, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Hg, and a combination of any of the foregoing, wherein the concentration of the compensatory dopant is between about 1014 cm−3 and about 1016 cm−3;
an optical absorption coefficient less than about 10 cm−1 at wavelengths between about 395 nm and about 460 nm; and
an electrical resistivity at room temperature greater than about 107 ohm-centimeter.

2. The gallium-containing nitride crystal of claim 1, comprising an impurity concentration of oxygen less than about 1016 cm−3.

3. The gallium-containing nitride crystal of claim 1, comprising an impurity concentration of oxygen less than about 1015 cm−3.

4. The gallium-containing nitride crystal of claim 1, wherein the concentration of the compensatory dopants is less than about 1016 cm−3.

5. The gallium-containing nitride crystal of claim 1, wherein the optical absorption coefficient at wavelengths between about 395 nm and about 460 nm is less than about 2 cm−1.

6. The gallium-containing nitride crystal of claim 1, wherein the optical absorption coefficient at wavelengths between about 395 nm and about 460 nm is less than about 0.2 cm−1.

7. The gallium-containing nitride crystal of claim 1, wherein the gallium-containing nitride crystal has a thickness of greater than about 1 millimeter.

8. The gallium-containing nitride crystal of claim 7, wherein the length is greater than about 20 millimeters.

9. The gallium-containing nitride crystal of claim 1, wherein the length is greater than about 100 millimeters.

10. The gallium-containing nitride crystal of claim 1, wherein the crystal is characterized by a crystallographic radius curvature of greater than 100 meters.

11. The gallium-containing nitride crystal of claim 1, comprising a large-area surface characterized by-a root-mean-square surface roughness of 1 nanometer and less.

12. The gallium-containing nitride crystal of claim 11, wherein the large-area surface has a crystallographic orientation within about 5 degrees of (0 0 0 ±1) c-plane.

13. The gallium-containing nitride crystal of claim 11, wherein the large-area surface has a crystallographic orientation within about 5 degrees of (1 0 −1 0) m-plane.

14. A device comprising the gallium-containing nitride crystal of claim 1, wherein the device is selected from a light emitting diode, a laser diode, a photodetector, an avalanche photodiode, a transistor, a rectifier, a thyristor; a transistor, a rectifier, a Schottky rectifier, a thyristor, a p-i-n diode, a metal-semiconductor-metal diode, high-electron mobility transistor, a metal semiconductor field effect transistor, a metal oxide field effect transistor, a power metal oxide semiconductor field effect transistor, a power metal insulator semiconductor field effect transistor, a bipolar junction transistor, a metal insulator field effect transistor, a heterojunction bipolar transistor, a power insulated gate bipolar transistor, a power vertical junction field effect transistor, a cascode switch, an inner sub-band emitter, a quantum well infrared photodetector, a quantum dot infrared photodetector, a solar cell, and a diode for photoelectrochemical water splitting and hydrogen generation.

15. The gallium-containing nitride crystal of claim 1, wherein the electrical resistivity at room temperature is greater than about 109 ohm-centimeter.

16. The gallium-containing nitride crystal of claim 1, wherein the electrical resistivity at room temperature is greater than about 1011 ohm-centimeter.

17. The gallium-containing nitride crystal of claim 1, comprising an oxygen content as a substitutional impurity less than about 10 parts per million.

18. The gallium-containing nitride crystal of claim 1, comprising an oxygen content as a substitutional impurity less than about 1 parts per million.

19. The gallium-containing nitride crystal of claim 1, wherein the gallium-containing nitride crystal is semi-insulating.

20. The gallium-containing nitride crystal of claim 1, wherein the room temperature resistivity is from 107 ohm-centimeters to 1012 ohm-centimeters.

21. The gallium-containing nitride crystal of claim 1, wherein the crystal is free-standing.

22. A bulk gallium-containing nitride crystal, comprising:
a wurtzite structure;
an impurity concentration greater than about 1015 cm−3 of at least one of Li, Na, K, Rb, Cs, Ca, F, and Cl;
a concentration of oxygen from about 1010 atoms per cubic centimeter to about 1017 atoms per cubic centimeter;
a compensatory dopant selected from V, Cr, Mo, W, Mn, Re, Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, Pt, Cu, Ag, Au, Zn, Cd, Hg, and a combination of any of the foregoing, wherein the concentration of the compensatory dopant is between about 1014 cm−3 and about 1016 cm−3;
an optical absorption coefficient less than about 2 cm−1 at wavelengths between about 395 nm and about 460 nm; and
an electrical resistivity at room temperature greater than about 107 ohm-centimeter.