# Patent

## Title
Seed layer for a p+ silicon germanium material for a non-volatile memory device and method

## Abstract

A method of forming a non-volatile memory device includes providing a substrate having a surface, depositing a dielectric overlying the surface, forming a first wiring structure overlying the dielectric, depositing silicon material overlying the first wiring structure, the silicon layer having a thickness of less than about 100 Angstroms, depositing silicon germanium material at a temperature raging from about 400 to about 490 Degrees Celsius overlying the first wiring structure using the silicon layer as a seed layer, wherein the silicon germanium material is substantially free of voids and has polycrystalline characteristics, depositing resistive switching material (e.g. amorphous silicon material) overlying the silicon germanium material, depositing a conductive material overlying the resistive material, and forming a second wiring structure overlying the conductive material.

## Background
BACKGROUND
The present invention is generally related to resistive switching devices. More particularly, embodiments according to the present invention provide a method and a structure to form a low temperature crystalline silicon material for a resistive switching device. Embodiments according to the present invention can be applied to non-volatile memory devices but it should be recognized that the present invention can have a much broader range of applicability.
From the above, a new semiconductor device structure and integration is desirable.
BRIEF SUMMARY OF THE PRESENT INVENTION
The present invention is generally related to resistive switching devices. More particularly, embodiments according to the present invention provide a method and a structure to form a low temperature crystalline silicon material for a resistive switching device. Embodiments according to the present invention can be applied to non-volatile memory devices but it should be recognized that the present invention can have a much broader range of applicability.
In a specific embodiment, a method for forming a resistive switching device is provided. The method includes providing a substrate having a surface region and depositing a first dielectric material overlying the surface region of the substrate. A first wiring structure is formed overlying the first dielectric material. The first wiring structure is elongated in shape and spatially configured to extend in a first direction in a specific embodiment. The method includes depositing a silicon material overlying the first wiring structure. In a specific embodiment, the silicon layer is characterized by a thickness of no greater than about 60 Angstroms. A silicon germanium material is deposited at a depositing temperature raging from about 400 Degree Celsius to about 490 Degree Celsius overlying the first wiring structure using the silicon material as a seed layer. The silicon germanium material is substantially free of voids and has a crystalline characteristic in a specific embodiment. The method includes depositing a resistive switching material overlying the silicon germanium material. In a specific embodiment, the resistive switching material comprising an amorphous silicon material. A conductive material is formed overlying at least the resistive material and a second wiring structure is formed overlying at least the conductive material.
In a specific embodiment, a resistive switching device is provided. The device includes a first wiring structure. The first wiring structure is elongated in shape and spatially configured to extend in a first direction in a specific embodiment. The device includes a junction layer comprising a silicon germanium material overlying the first wiring structure. In a specific embodiment, the silicon germanium material has a p+ impurity characteristic and a crystalline characteristic. In a specific embodiment, the device includes a resistive switching material comprising an amorphous silicon material overlying the junction layer and a second wiring structure overlying the resistive switching material. In a specific embodiment, the second wiring structure is elongated in shape and spatially configured to extend in a second direction orthogonal to the first direction. In some embodiments, the resistive switching device is disposed in an N by M crossbar array in a specific embodiment, where N and M are integers (N≧1, M≧1).
Many benefits can be achieved by ways of the present invention over conventional techniques. For example, embodiments according to the present invention provide a method to form a silicon germanium material at a low temperature for fabrication of a non-volatile memory device. The low temperature is compatible with thermal budget of conventional CMOS processes (e.g. back-end CMOS process) and provide easy integration to the process flow. Additionally, the silicon germanium material may be doped using impurity species (for example a boron species) to provide for a suitable conductivity for proper operation of the non-volatile memory device in a specific embodiment. Moreover, embodiments of the methods use conventional semiconductor processing techniques without modification to the equipments. Depending upon the embodiment, one or more of these benefits may be achieved. One skilled in the art would recognize other modifications, variations, and alternatives.
In various embodiments, the resistive memory described herein may provide many benefits, including low power consumption memories, non-volatile memories, and the like. In various embodiments, devices including processors, communications interfaces, and the like may incorporate such resistive memory devices. Such devices may include computers, computing tablets, portable phones, e-readers, or the like. Accordingly, such devices may be considered within the scope of the present inventions.
According to one aspect of the invention, a method of forming a non-volatile memory device, is described. One technique includes providing a substrate having a surface region, depositing a first dielectric material overlying the surface region of the substrate, and forming a first wiring structure overlying the first dielectric material. A process includes depositing a silicon material overlying the first wiring structure, the silicon layer being characterized by a thickness of no greater than about 100 Angstroms, and depositing a silicon germanium material at a depositing temperature raging from about 400 Degree Celsius to about 490 Degree Celsius overlying the first wiring structure using the silicon material as a seed layer, the silicon germanium material being substantially free of voids and having a polycrystalline characteristic. A method includes depositing a resistive switching material comprising an amorphous silicon material overlying the silicon germanium material, depositing a conductive material overlying the resistive material, and forming a second wiring structure overlying the conductive material.
According to another aspect of the invention, a resistive switching device, comprising is described. One product includes a first wiring structure, spatially configured to extend in a first direction, and a junction layer overlying the first wiring structure comprising a silicon germanium material having a p+ impurity characteristic and a polycrystalline characteristic. A device includes a resistive switching material comprising an amorphous silicon material overlying the junction layer, and a second wiring structure, spatially configured to extend in a second direction orthogonal to the first direction.
According to yet another aspect of the invention, a device is manufactured according to various processes. One process includes providing a substrate having a surface region, depositing a first dielectric material overlying the surface region of the substrate, and forming a first wiring structure overlying the first dielectric material. A technique includes depositing a silicon material overlying the first wiring structure, the silicon layer being characterized by a thickness of no greater than about 100 Angstroms, and depositing a silicon germanium material at a depositing temperature raging from about 400 Degree Celsius to about 490 Degree Celsius overlying the first wiring structure using the silicon material as a seed layer, the silicon germanium material being substantially free of voids and having a polycrystalline characteristic. A method includes depositing a resistive switching material comprising an amorphous silicon material overlying the silicon germanium material, depositing a conductive material overlying the resistive material, and forming a second wiring structure overlying the conductive material.



SUMMARY OF THE DRAWINGS
FIG. 1-11 are simplified diagrams illustrating a method of forming a non-volatile memory device according to an embodiment of the present invention.
FIG. 12 is a simplified plot illustrating a crystalline temperature of a silicon germanium material as a function of germanium composition according to an embodiment of the present invention.
FIG. 13 illustrates transmission electron microscope images of the silicon germanium material formed under different experiment conditions according to embodiments of the present invention.



DETAILED DESCRIPTION OF THE PRESENT INVENTION
The present invention is generally related to resistive switching devices. More particularly, embodiments according to the present invention provide a method and a structure to form a low temperature crystalline silicon material for a resistive switching device. Embodiments according to the present invention can be applied to non-volatile memory devices but it should be recognized that the present invention can have a much broader range of applicability.
Resistive switching behavior has been observed and studied in micrometer-scale amorphous silicon (a-Si) devices since the 1980s. A typical device consists of a pair of metal electrodes sandwiching an amorphous silicon layer in a so-called Metal/a-Si/Metal (M/a-Si/M) structure, in which the voltage applied across the pair of metal electrodes causes changes in the resistance of the a-Si material. These conventional M/a-Si/M based switching devices can have the advantages of high Ion/Ioff ratios, and can be fabricated with a CMOS compatible fabrication process and materials. However, these devices usually require high voltage for operation, have poor endurance characteristics, and cannot be scaled to nanometers, as demanded by present consumer electronics application.
To further decrease cost per bit, device shrinking and process simplification is necessary. To achieve proper switching of the device, defect level in an interface region formed between the amorphous silicon switching material and a metal electrode would have to be controlled. The defect level can be controlled by using a suitable silicon material disposed between the electrode material and the amorphous silicon switching material. Embodiments according to the present invention provide a method to form a silicon germanium material and a structure to form a non-volatile memory with desirable switching characteristic and device reliability.
The terms “bottom” and “top” are for references and illustration only and not meant to be limiting.
FIG. 1-11 are simplified diagrams illustrating a method for forming a resistive switching device for a non-volatile memory device according to an embodiment of the present invention. As shown in FIG. 1, a semiconductor substrate 102 having a surface region 104 is provided. The semiconductor substrate can be a single crystal silicon wafer, a silicon germanium material, a silicon on insulator (commonly called SOI) depending on the embodiment. In certain embodiments, the semiconductor substrate can have one or more MOS devices formed thereon. The one or more MOS devices can be controlling circuitry for the resistive switching device in a specific embodiment.
As illustrated in FIG. 2, the method includes depositing a first dielectric material 202 overlying the semiconductor substrate. The first dielectric material can be silicon oxide, silicon nitride, a dielectric stack of alternating layers of silicon oxide and silicon nitride (for example, an ONO stack), a low K dielectric, a high K dielectric, or a combination, and others, depending on the application. The first dielectric material 202 can be deposited using techniques such as chemical vapor deposition, including low pressure chemical vapor deposition, plasma enhanced chemical vapor deposition, atomic layer deposition (ALD), physical vapor deposition, including any combination of these, and others
Referring to FIG. 3, the method includes depositing a first wiring material overlying the first dielectric material. The first wiring material can be a suitable metal material including alloy materials, or a semiconductor material having a suitable conductivity characteristic. The metal material can be tungsten, aluminum, copper or silver, and others. Additionally, the first wiring metal may be a combination of conductive materials. In various embodiments, these metal materials may be deposited using a physical vapor deposition process, chemical vapor deposition process, electroplating, or electrodeless deposition process, including any combinations of these, and others. The semiconductor material can be, for example, a suitably doped silicon material in certain embodiments.
In certain embodiments, a first adhesion material 304 is first formed overlying the first dielectric material before deposition of the first wiring material to promote adhesion of the first wiring material to the first dielectric material. A diffusion barrier material 306 may also be formed overlying the metal material to prevent the metal material to contaminate other portions of the device in a specific embodiment.
The method subjects the first wiring material to a first pattern and etching process to form a first wiring structure 402 in a specific embodiment. As shown in FIG. 4, the first wiring structure includes a plurality of first elongated structures that may extend in a first direction 404 in a specific embodiment.
In a specific embodiment, the method deposits a second dielectric material 502 overlying the first wiring structure. The second dielectric material can be silicon oxide, silicon nitride, a dielectric stack of alternating layers of silicon oxide and silicon nitride (for example, an ONO stack), a low K dielectric, a high K dielectric, or a combination, and others, depending on the application. The second dielectric material can be subjected to a planarizing process to isolate the first wiring structure in a specific embodiment. As shown in FIG. 5, a surface region 504 of the diffusion barrier material may be exposed after chemical or mechanical planarizing.
Referring to FIG. 6, the method includes forming a first silicon material 602 overlying at least the first wiring structure and the exposed surface of the second dielectric material. The first silicon material can be formed using a deposition process such as a low pressure chemical vapor deposition process a plasma enhanced chemical vapor deposition process using silane (SiH4) or disilane (Si2H6), or a suitable chlorosilane depending on the application. Alternatively, the first silicon material can be deposited using a physical vapor deposition process from a suitable silicon target. Deposition temperature can range from about 380 Degree Celsius to about 450 Degree Celsius, and preferably not higher than 440 Degree Celsius. In a preferred embodiment, the first silicon material is deposited using a low pressure chemical vapor deposition process using disilane at a deposition temperature ranging from about 400 Degree Celsius to about 460 Degree Celsius. The first silicon material layer is further characterized by a thickness of no greater than about 100 Angstroms and in some cases less than about 50 Angstrom in a specific embodiment.
Referring again to FIG. 6, embodiments of the method deposit a junction material 604 overlying the first wiring structure using the first silicon material as a seed layer for junction material 604. The junction material can be a suitable semiconductor material in a specific embodiment. In a specific embodiment, the semiconductor material can be a polycrystalline silicon germanium (poly-SiGe) material. In various embodiments, the polycrystalline silicon germanium material can be doped with a suitable impurity species to have a desirable conductivity. The polycrystalline silicon germanium material can be deposited using a chemical vapor deposition process such as a low pressure chemical vapor deposition process, a plasma enhanced chemical vapor deposition process, atomic layer deposition (ALD) and others. Depending on the application, precursors such as silane and germane in a suitable carrier gas may be used. In a specific embodiment, the polycrystalline silicon germanium material can have a p+ impurity characteristic.
In various embodiments, the p+ impurity characteristic can be provided using a boron species, an aluminum species or a gallium species and the likes, depending on the application. In a specific embodiment, the p+ impurity species is provided by a boron species co-deposited with silane and germane. The boron species can be provided the using diborane in a specific embodiment. Ex-situ deposition may also be used, depending on the embodiment. Deposition temperature ranges from about 380 Degree Celsius to about 460 Degree Celsius and in some cases ranges from about 400 Degree Celsius to about 440 Degree Celsius. In a specific embodiment, the as deposited p+ silicon germanium material has a crystalline characteristic without further anneal. In a specific embodiment, the boron doped silicon germanium material has a lower crystalline temperature than an undoped silicon germanium material. Additionally, the p+ silicon germanium material is typically characterized by a sheet resistance of no greater than 0.1 ohm-cm in a specific embodiment.
Referring to FIG. 7, the method deposits a resistive switching material 702 overlying the junction layer. The resistive switching material can be a second silicon material. The second silicon material can be an amorphous silicon material or a polycrystalline silicon material, and others, depending on the embodiment. In a specific embodiment, the resistive switching material comprises an amorphous silicon material. Deposition techniques can include a chemical vapor deposition process CVD), physical vapor deposition (PVD) process, an atomic layer deposition (ALD) process, and others. The chemical vapor process can be a low pressure chemical vapor deposition process, plasma enhanced chemical vapor deposition process, deposited using precursors such as silane, disilane, a suitable chlorosilane in a reducing environment, a combination, and others. Deposition temperature can range from 250 Degree Celsius to about 500 Degree Celsius. In some cases, deposition temperature ranges from about 400 Degree Celsius to about 440 Degree Celsius and no greater than about 450 Degree Celsius.
As shown in FIG. 8, the method includes depositing a second conductive material overlying the resistive switching material. The second conductive material 802 can be a metal material such as copper, silver, gold, platinum, palladium, nickel, zinc or others. The second conductive metal material is characterized by a suitable diffusivity in the resistive switching material in a presence of an electric field in a specific embodiment. For amorphous silicon material as the resistive switching material, the metal material can be silver or an alloy of silver. The alloy of silver comprises at least 80 percent of silver in a specific embodiment.
In various embodiments, the silver material forms a silver region in a portion of the amorphous silicon material upon application of the electric filed. The silver region comprises a plurality of silver particles, including silver ions, silver clusters, silver atoms and a combination. The plurality of silver particles may be formed in defect sites of the amorphous silicon material in a specific embodiment. The silver region further comprises a silver filament structure extending towards the first wiring structure. The filament structure can be characterized by a length, a distance between the silver particles, and a distance between the filament structure and the first electrode structure. In a specific embodiment, the resistive switching material (for example, the amorphous silicon material) is characterized by a resistance depending at least on a length, a distance between the silver particles, and a distance between the filament structure and the first electrode structure. Due to material mismatch, defect density is higher at an interface region formed between the amorphous silicon material 702, and junction material layer 604, and may cause a short. In various embodiments, the junction layer (for example, p+ polycrystalline silicon germanium material) controls an interfacial defect density for proper switching behavior of the resistive switching device in a specific embodiment.
Depending on the embodiment, the method can deposit an adhesion material and a diffusion barrier material overlying the second conductive material. The adhesion material can be a titanium material, tungsten material, or the like, in various embodiments. The diffusion barrier material can include titanium nitride, titanium tungsten, tantalum nitride, and others depending on the application. The adhesion material and the diffusion barrier material can be deposited using a chemical vapor deposition process, a physical vapor deposition process, atomic, including a combination of these, and others.
Various embodiments of the present invention then subjects the junction material 604 including the seed layer 602, the resistive switching material 702, the second conductive material 802, including the adhesion material and the diffusion barrier material to a pattern and etching process to form one or more pillar structures 902 overlying a respective first wiring structure 302-306, as shown in FIG. 9.
A third dielectric material 1002 is deposited overlying the one or more pillar structures and to fill the gaps between the pillar structures to isolate the pillar structures in a specific embodiment, and the third dielectric material 1002 may be planarized as shown in FIG. 10. In various embodiments, the third dielectric material can be silicon oxide, silicon nitride, a dielectric stack comprising alternative layers of silicon oxide and silicon nitride (for example, an ONO), a high K dielectric, a low K dielectric, or a combination, and others depending on the application. When the third dielectric material is subjected to one or more mechanical or chemical planarizing processes a top surface region 1004 of the diffusion barrier material may be exposed, and isolate each of the pillar structure in a specific embodiment. In various embodiments, the planarizing process can be a chemical mechanical polishing process using the diffusion barrier material as a polish stop layer in a specific embodiment. Alternatively, an etch back process or a combination of etch back process and chemical mechanical polishing process may be used.
As shown in FIG. 11, the method includes depositing a second wiring material 1102 overlying the one or more pillar structures and the third dielectric material. The second wiring material can be aluminum, copper, tungsten, silver or a semiconductor material having a suitable conductivity. In a specific embodiment, the second wiring material can include at least one adhesion material and at least one diffusion barrier material in a specific embodiment. For example, titanium can be formed overlying the pillar structure and the third dielectric material and titanium nitride can formed overlying titanium for adhesion/diffusion barrier material. In various embodiments, the second wiring material is subjected to a pattern and etch process to form a second wiring structure overlying the structure illustrated in FIG. 11. The second wiring structure may be locally elongated in shape and spatially configured to extend in a second direction. The second direction is at an angle with respect to the first direction of the first wiring structure. In a specific embodiment, the second direction is orthogonal to the first direction in a specific embodiment.
In various embodiments, a third dielectric material overlying the second wiring structure may be applied to isolate each of the second wiring structures. The method may then include formation of one or more passivation layers and global wiring structures and others depending on the application.
Depending on the embodiment, there can be other variations. For example, the seed layer can be optional for certain embodiments while the p+ silicon germanium material deposited has the desirable crystalline and conductive characteristics at a deposition temperature not higher than 450 Degree Celsius. Additionally, the active metal material (for example, the silver material can be formed in a via structure to further reduce an effective size of the device. Of course one skilled in the art would recognize other variations, modifications, and alternatives.
Referring now to FIG. 12. A simplified plot of deposition temperature of crystalline silicon germanium material as a function of germanium composition. As illustrated, deposited silicon germanium material may be polycrystalline without further anneal. As shown, the minimum deposition temperature for a polycrystalline silicon germanium material decreases monotonically (dotted line) as the germanium concentration increases.
In various embodiments, CMOS processes typically use copper and aluminum as interconnects, accordingly, the deposition temperature for silicon germanium may be limited as a CMOS process. As illustrated, when a process uses copper interconnects, the temperature of subsequent processes should not be higher than about 400 Degree Celsius; and when the process uses aluminum interconnects, the process temperature should not be higher than about 480 Degree Celsius.
Referring back to FIG. 12, in some embodiments, one germanium composition in the germanium material is greater than about x=0.65 when the process uses copper interconnects. In such a case, the deposition temperature of the germanium material should be no higher than about 400 degrees C. As the ratio of germanium increases, the deposition temperature may be lowered. For example, at x=0.8 germanium, the deposition temperature may range from about 380 degrees C. to no higher than about 400 degrees C. In other embodiments, a composition of about x=0.4 or greater of germanium may be used when the process uses aluminum interconnects. In such a case, the deposition temperature of the germanium material should be about 480-490 degrees C. As the ratio of germanium increases, the deposition temperature may be lowered. For example, at x=0.5 germanium, the deposition temperature may range from about 450 degrees C. to no higher than about 490 degrees C.; at x=0.65 germanium, the deposition temperature may range from about 400 degrees C. to no higher than about 490 degrees C.; and the like. As indicated above, a useful end deposition temperature for the germanium material may range from about 400 degrees C. to about 450 degrees C.
As shown in FIG. 12, impurity material such as a boron species provides a dopant source to increase conductivity of the silicon germanium material and does not affect the polycrystalline characteristic but can further lower the crystallization temperature.
Referring to FIG. 13, transmission electron microscope (TEM) images are shown. As shown in image 1302, p+ silicon germanium material layer 1306 is formed overlying a silicon seed layer 1308. P+ silicon germanium material layer 1306 is substantially amorphous, only irregular and non-continuous crystals are formed resulting in a rough surface. Due to lack of crystallization, the p+ silicon germanium material has a high sheet resistance.
In contrast, image 1304 is obtained from a p+ silicon germanium material 1310 deposited overlying a silicon seed layer 1312. P+ silicon germanium material layer 1310 has polycrystalline grains extending continuously throughout and has a low sheet resistance (about 0.02 ohm-cm). Additionally, in this example, P+ silicon germanium material layer 1310 is free of voids and exhibits desirable conductivity. As shown, seed layer 1308 is at least twice as thick as seed layer 1312. From the experiment results, the silicon seed layer should have an optimized thickness and in some cases no greater than 100 Angstroms in a specific embodiment.
In one example, p+ silicon germanium material has a measured thickness of about 59.5 nm overlying a silicon seed layer of a measured thickness of about 6.9 nm. In various examples, the p+ silicon germanium material is continuous, free of voids, and exhibits desirable conductivity. The process parameters is summarized as follow:















Parameter
Si Seed
SiGe









Temperature (° C.)
425
425° C.



Pressure (mTorr)
300
300 mTorr



Time (minute)
1-3
12 min (6 min POR)



Flow Rates



Si2H6
150 sccm 
 0 sccm



SiH4
0 sccm
200 sccm



GeH4
0 sccm
100 sccm



BCl3
0 sccm
 10 sccm










In various embodiments, the memory structures illustrated in FIGS. 1-11 may be performed as part of a back-end CMOS process. Structures underlying these memory structures may include memory control circuitry, processing circuitry (e.g. CPU, GPU), logic structures (e.g. FPGA), or the like. In various embodiments, a component or device including the memory structures may be combined with one or more components upon a common chip substrate, upon a common circuit board, or the like. The other components may include processing components (e.g. CPU, GPU), communications components (e.g. RF, WiFi), output display and display controllers, and the like. A resulting device may include a computer, a hand-held device (e.g. cell phone, tablet device), or the like. Such devices, and others are contemplated to be within the scope of the present invention.
Though the present invention has been described using various examples and embodiments, it is also understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or alternatives in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application and scope of the appended claims.

## Claims

1. A method of forming a non-volatile memory device, comprising:
providing a substrate having a surface region;
depositing a first dielectric material overlying the surface region of the substrate;
forming a first wiring structure overlying the first dielectric material;
optionally forming a diffusion barrier material overlying and in contact with the first wiring structure;
depositing a silicon material overlying the first wiring structure and in contact with the first wiring structure or optionally in contact with the diffusion barrier material, the silicon layer being characterized by a thickness of greater than 0 Angstroms but no greater than about 60 Angstroms, wherein depositing the silicon material comprises depositing the silicon material using a physical vapor deposition process;
depositing a silicon germanium material at a depositing temperature ranging from about 400 Degree Celsius to about 490 Degree Celsius overlying the first wiring structure and in contact with the silicon material, using the silicon material as a seed layer, wherein the silicon germanium as-deposited being substantially free of voids and as-deposited having a polycrystalline characteristic;
depositing a resistive switching material comprising an amorphous silicon material overlying and in contact with the silicon germanium material;
depositing a conductive material overlying the resistive material; and
forming a second wiring structure overlying the conductive material.

2. The method of claim 1 wherein the silicon germanium material has a p+ impurity characteristic.

3. The method of claim 2 wherein the p+ impurity species is provided by a species selected from a group consisting of: boron species, an aluminum species, and a gallium species.

4. The method of claim 2 wherein the silicon germanium material having the p+ impurity characteristic is characterized by a sheet resistance of less than about 0.1 ohm-cm.

5. The method of claim 3 wherein the p+ impurity species in the silicon germanium material is activated free from an anneal process.

6. The method of claim 1 wherein the silicon germanium material has a composition Si1-xGex, where x is within a range given by: 0.0<x≦ about 0.7.

7. The method of claim 1 wherein depositing the resistive switching material comprises depositing the amorphous silicon material using a process selected from a group consisting of: a low pressure chemical vapor deposition process, a plasma enhanced chemical vapor deposition process, a physical vapor deposition process, or a combination thereof.

8. The method of claim 7 wherein depositing the amorphous silicon material comprises depositing the amorphous silicon material at a deposition temperature ranging from about 400 Degree Celsius to about 450 Degree Celsius.

9. The method of claim 1 wherein the substrate comprises one or more CMOS devices formed thereon, and wherein the one or more CMOS devices comprise controlling circuitry for the non-volatile memory device.

10. The method of claim 1 wherein forming the first wiring structure comprises depositing a first conductive material selected from a group consisting of: a doped polysilicon material, a copper material, an aluminum material, a tungsten material, and a combination thereof.

11. The method of claim 1 wherein forming the first wiring structure further comprises etching the first conductive material to form the first wiring structure, wherein the first wiring structure is elongated in shape and configured to spatially extend in a first direction.

12. The method of claim 1 wherein forming the second wiring structure comprises:
depositing a metal material in physical and electrical contact with the switching material; and
etching the metal material to form the second wiring structure, wherein the second wiring structure is elongated in shape and configured to spatially extend in a second direction orthogonal to the first direction.

13. A method of forming a non-volatile memory device, comprising:
providing a substrate having a surface region;
depositing a first dielectric material overlying the surface region of the substrate;
forming a first wiring structure overlying the first dielectric material;
optionally forming a barrier layer or an adhesion layer overlying and in contact with the first wiring structure;
depositing an undoped silicon material overlying and in contact with the first wiring structure, or optionally in contact with the barrier layer or the adhesion layer, the undoped silicon layer being characterized by a thickness of no greater than about 100 angstroms;
depositing a silicon germanium material at a depositing temperature ranging from about 400 Degrees Celsius to about 490 Degrees Celsius overlying and in contact with the undoped silicon material and utilizing the undoped silicon material as a seed layer, the silicon germanium material having a polycrystalline characteristic;
depositing a resistive switching material comprising an amorphous silicon material overlying and in contact with the silicon germanium material;
depositing a conductive material overlying the resistive switching material; and
forming a second wiring structure overlying the conductive material.

14. The method of claim 13, further comprising depositing the resistive switching material in contact with the silicon germanium material.

15. The method of claim 13, further comprising selecting an active metal for the conductive material, the active metal comprising particles capable of drifting or diffusing within the resistive switching material.

16. The method of claim 15, wherein the particles are responsive to a voltage applied to the non-volatile memory device to form a conductive filament at least in part through the resistive switching material from a first surface of the resistive switching material near the conductive material toward a second surface of the resistive switching material near the silicon germanium material.

17. The method of claim 13, further comprising depositing a second adhesion layer between the first dielectric material and the first wiring structure, wherein the adhesion layer is in contact with at least one of the first dielectric material or the first wiring structure.

18. The method of claim 13, further comprising doping the silicon germanium material with a p+ impurity characteristic.

19. The method of claim 18, further comprising controlling the doping of the silicon germanium material with the p+ impurity characteristic to achieve a sheet resistance of the silicon germanium material of less than about 0.1 ohm-cm.

20. The method of claim 13, wherein depositing the silicon germanium material further comprises depositing a silicon germanium alloy having a composition Si1-xGex, where x is within a range given by: 0.0<x≦ about 0.7.