# Patent

## Title
Process for manufacturing a power semiconductor device having charge-balance columnar structures on a non-planar surface, and corresponding power semiconductor device

## Abstract

An embodiment of a process for manufacturing a power semiconductor device envisages the steps of: providing a body of semiconductor material having a top surface and having a first conductivity; forming columnar regions having a second type of conductivity within the body of semiconductor material, and surface extensions of the columnar regions above the top surface; and forming doped regions having the second type of conductivity, in the proximity of the top surface and in contact with the columnar regions. The doped regions are formed at least partially within the surface extensions of the columnar regions; the surface extensions and the doped regions have a non-planar surface pattern, in particular with a substantially V-shaped groove.

## Background
PRIORITY
The present application is a Divisional of U.S. patent application Ser. No. 12/298,025; which application claims benefit pursuant to 35 USC §371 of PCT Patent Application Serial No. PCT/IT2006/000273, published in English, filed Apr. 21, 2006, which these applications are incorporated herein by reference in their entirety.


CROSS REFERENCE TO RELATED APPLICATIONS
This application is related to U.S. patent application Ser. No. 12/296,921, filed Oct. 10, 2008, entitled PROCESS FOR MANUFACTURING A SEMICONDUCTOR POWER DEVICE COMPRISING CHARGE-BALANCE COLUMN STRUCTURES AND RESPECTIVE DEVICE, which is incorporated herein by reference in its entirety.
TECHNICAL FIELD
An embodiment of the present disclosure relates to a process for manufacturing a power semiconductor device having charge-balance columnar structures on a non-planar surface, and to a corresponding power semiconductor device. In particular, the ensuing treatment will make explicit reference, without this implying any loss of generality, to the manufacturing of a power MOS device.
BACKGROUND
In the last few years a wide range of solutions have been developed in order to increase the efficiency of power semiconductor devices, in particular in terms of increase in the breakdown voltage and decrease in the output resistance.
For example, U.S. Pat. Nos. 6,586,798, 6,228,719, 6,300,171 and 6,404,010, all commonly owned and incorporated by reference, describe vertical-conduction power semiconductor devices, wherein, within an epitaxial layer forming part of a drain region having a given conductivity type, columnar structures of opposite conductivity are formed. These columnar structures have a dopant concentration equal and opposite to the dopant concentration of the epitaxial layer, so as to enable a substantial charge balance (the so-called multi-drain or MD technology). The charge balance enables high breakdown voltages to be obtained, and, in addition, the high dopant concentration of the epitaxial layer enables a low output resistance (and hence low losses in conduction) to be obtained. The use of MD technology has enabled the so-called “ideal limit of silicon” to be overcome.
In summary, the formation of the aforesaid columnar structures envisages a sequence of steps of growth of N-type epitaxial layers, each step being followed by a step of implantation of a P-type dopant. The implanted regions are stacked so as to form the columnar structures. Next, body regions of the power device are formed in contact with the columnar structures, so that the columnar structures constitute an extension of the body regions within the drain region.
The evolution of said technology has witnessed a progressive increase in the density of the elementary strips forming the devices in order to further increase the concentration of charge of the epitaxial layer and to obtain devices which, given the same breakdown voltage (which is substantially related to the height of the columnar structures), have a lower output resistance. On the other hand, however, the increase in the density of the elementary strips entails a corresponding increase in the number of the steps of epitaxial growth and a reduction in the thermal budget of the devices, and consequently an increase in the manufacturing costs and times, and in the defectiveness intrinsically linked to the steps of epitaxial growth.
Alternative technologies have consequently been developed to obtain the charge-balance columnar structures, said technologies envisaging, for example, formation of trenches within the epitaxial layer and subsequent filling of said trenches with semiconductor material appropriately doped to obtain the charge balance.
For example, solutions are known according to which the trenches are filled via steps of epitaxial growth of semiconductor material (see for example U.S. Pat. No. 6,495,294, US 2003224588 and US 2003219933 which are incorporated by reference), possibly alternated by steps of etching of surface-growth portions. In particular, a non-selective epitaxial growth also involves a top surface of the layer in which the trenches are provided, and at the end of the epitaxial process a wrinkled surface layer of semiconductor material is consequently formed, characterized by the presence of a plurality of grooves in areas corresponding to the columnar structures. The known techniques envisage removal of the wrinkled surface layer via the CMP (Chemical-Mechanical Polishing) technique in order to planarize the top surface prior to formation of body, gate and source structures of the power devices.
As a whole, the solutions described for obtaining power devices with charge-balance structures may not be satisfactory, either as regards the complexity and costs of their manufacturing and as regards attainment of a real charge balance (for example, due to a poor uniformity of the spatial charge distribution or due to the presence of residual defects).
SUMMARY
An embodiment of the present disclosure is a process for manufacturing a charge-balance power device that enables the aforesaid problems and disadvantages to be overcome, and that is simple and inexpensive to carry out.



BRIEF DESCRIPTION OF THE DRAWINGS
For a better understanding of the concepts described herein, embodiments are now described, purely by way of non-limiting example and with reference to the attached drawings, wherein:
FIGS. 1 to 8 show cross sections through a wafer of semiconductor material regarding successive steps of a manufacturing process according to a first embodiment of the present disclosure;
FIGS. 9 and 10 show possible variants of the first embodiment of the present disclosure;
FIGS. 11 to 17 show cross sections through a wafer of semiconductor material regarding successive steps of a manufacturing process according to a second embodiment of the present disclosure; and
FIGS. 18 and 19 show possible variants of the second embodiment of the present disclosure.



DETAILED DESCRIPTION
FIG. 1 shows a wafer 1 of semiconductor material, typically silicon, comprising a substrate 2 having a first type of conductivity, for example, an N++ type with resistivity of less than approximately 10 Ω·cm, and an epitaxial layer 3, which also has the first type of conductivity, for example, an N type with a resistivity of approximately between 0.1 Ω·cm and 2 Ω·cm. The wafer 1 has, for example, a surface orientation <100>, and the epitaxial layer 3 has a top surface 4. Over the entire wafer an implantation of an N type with low energy (approximately 50-100 keV) and dosage of approximately between 1011 and 1013 at/cm2 is carried out, without masking, in order to form a surface-implant layer 5 in the proximity of the top surface 4 of the epitaxial layer 3.
Next (FIG. 2), within the epitaxial layer 3 a plurality of columnar structures 6 for charge balance is formed. As has been described in detail in the copending patent application PCT/IT2006/000244 filed on Apr. 11, 2006, the process for forming the columnar structures 6 envisages in the first place formation, by means of anisotropic dry etching through a purposely provided masking, of deep trenches 8 within the epitaxial layer 3 (and hence through the surface-implant layer 5), having for example a width, at the level of the top surface 4, of approximately between 0.8 and 2 μm and a smaller width on the bottom of approximately between 0.2 and 1.4 μm. In addition, the height of the deep trenches 8 ranges, for example, from approximately 5 to 50 μm and determines, together with the thickness of the epitaxial layer 3, the voltage class of the final device (for example, a voltage class of 100 V corresponds to a height of 5 μm, whereas a voltage class of 600 V corresponds to a height of 30 μm). The cut-off voltage of the resulting device can range approximately between 100 and 1500 V, according to the thickness of the epitaxial layer 3. Then, the wafer 1 is subjected to an annealing treatment in a hydrogen environment at a temperature of approximately 1000-1150° C. for a treatment time of approximately 1 to 15 min. Said treatment, in addition to removing the damage due to the previous dry etch, leads to exposure, on the bottom of the deep trenches 8, of the crystallographic planes <100> and <130> and, along the side walls, of the plane <010> (the deep trenches 8 consequently assume the shape visible in FIG. 2). Next, the deep trenches 8 are filled via epitaxial growth with silicon doped with a second conductivity type, in the example, the P type (for instance, doped with boron ions). In particular, the epitaxial growth occurs by supplying flows of a gas containing silicon (for example, dichlorosilane) and of a gas containing boron (for example, diborane), and control of doping is ensured maintaining an approximately constant gradient of growth in the flow of diborane (for example, setting a linear ramp increasing from an initial flow value to a final flow value twice the initial one), and maintaining the flow of dichlorosilane approximately constant. Given that the growth is not selective with respect to the deep trenches 8, the epitaxial growth occurs both within the trenches starting from the side walls, at a higher rate in the proximity of the surface, and on the outside of the trenches, in particular on the top surface 4 of the epitaxial layer 3. In order to prevent premature closing of the deep trenches 8 due to the encounter of the fronts of growth from the walls, successive steps of epitaxial growth are consequently alternated with etching steps, for example with HCl, of the surface-growth portions (the so-called multi-step process). At the end of said process sequence, the structure shown in FIG. 2 is obtained, with formation of the columnar structures 6, filling the deep trenches 8 substantially completely and having a substantially uniform spatial distribution of dopant and reduced presence of defects (for example voids). The process of non-selective epitaxial growth involves also the top surface 4 of the epitaxial layer 3, over which a wrinkled surface layer 9 of a P type is formed, with grooves in areas corresponding to the columnar structures 6. In particular, each columnar structure 6 has thus a surface extension 10, at and over the top surface 4, having a non-planar surface pattern and a characteristic grooved, in particular V-shaped, cross section. Connection portions 11 of the wrinkled surface layer 9, having a planar surface pattern, connect the surface extensions 10 of adjacent columnar structures 6. In addition, said adjacent columnar structures 6 are separated, at the top surface 4, by respective implant portions 5a of the implant layer 5.
The subsequent figures show for greater clarity an enlargement of a surface portion of the wafer 1, shown by a dashed rectangle in FIG. 2, which encloses a pair of adjacent columnar structures 6 (in practice, two strips of the device). It is clear, however, that the process steps described hereinafter regard also the remaining part of the device.
As will be clarified hereinafter, an embodiment of the present disclosure envisages providing a power device on a non-planar surface partially within the wrinkled surface layer 9, exploiting portions of said layer, in particular the surface extensions 10 of the columnar structures 6, as active areas of the device. In other words, the process according to an embodiment of the disclosure does not envisage a preventive step of planarization of the wafer surface (for example via CMP), with advantages in terms of costs and simplicity of manufacturing.
In detail (FIG. 3), in a surface region of the connection portions 11, implants of an N type are performed, through a purposely provided mask, for example, with medium energy (approximately 80-160 keV) and a dosage of approximately between 5·1011 and 1013 at/cm2, in order to form surface contact regions 12.
Then (FIG. 4), a process of thermal diffusion is performed to provide sinkers 14 of an N type, which reverse the conductivity of the respective connection portions 11 and reach the underlying implant portions 5a, which are also of an N type. The diffusion process can possibly be omitted when the conditions of the prior implant (in terms of dosage and energy) and the thickness of the wrinkled surface layer 9 enable formation of the sinkers 14 even in the absence of said process. It should be noted in any case that the sinkers 14 separate adjacent surface extensions 10, enabling, as will be described in detail hereinafter, formation of devices having a cell structure.
Next, a gate oxide layer 15 (made of thermal oxide), of a thickness of approximately between 20 nm and 150 nm, is grown over the wafer 1 in the active area, and a polysilicon layer 16, having a thickness of approximately between 200 nm and 700 nm, is then formed over the gate oxide layer 15. The polysilicon layer 16 is etched via selective dry etching through a purposely provided mask so as to obtain gate regions 18 above the sinkers 14 (FIG. 5).
Next (FIG. 6), through the gate oxide layer 15 and exploiting the gate regions 18 as hard masks, a body implant is carried out, for example, with boron atoms and an implant dosage of approximately between 1013 and 1014 at/cm2 and an energy of approximately between 80 and 200 keV (chosen as a function of the thickness of the gate regions 18), followed by a thermal process of diffusion to form body regions 19. In particular, the body regions 19 are formed within the surface extensions 10 of the columnar structures 6, consequently reproducing the non-planar pattern with grooved cross section, and partially within the sinkers 14 underneath the gate regions 18 (where they form channel regions of the power device).
Next, through a purposely provided masking (not illustrated) aligned with the mask that has defined the gate regions 18, a deep-body implantation of a P++ type is carried out using boron ions with an implantation dosage of approximately between 5·1014 and 5·1015 at/cm2 and an energy of approximately between 80 and 300 keV. There follows a thermal process of diffusion to form deep-body regions 20 in a central area of the surface extensions 10 (FIG. 7).
Next (FIG. 8), through a purposely provided masking, a source implantation of an N+ type is carried out, for example with atoms of phosphorus P or arsenic As with an implantation dosage of approximately between 5·1014 and 5·1015 at/cm2 and an energy of approximately between 60 and 200 keV, to form first and second source regions 22a, 22b within the body regions 19 and deep-body regions 20. In particular, the first source regions 22a occupy surface portions of body regions of first columnar structures 6a entirely, whilst the second source regions 22b are arranged in outer surface portions of body regions of second columnar structures 6b, which alternate with the first columnar structures 6a within the epitaxial layer 3 (so as to obtain subsequently, for known reasons, a short circuit between the source and body regions of the power device).
Next, a process of deposition of an intermediate dielectric layer 23 with a thickness of approximately between 500 nm and 1 μm is carried out, as well as a thermal activation process. Then contacts are opened, by means of masking and subsequent etching of the intermediate dielectric layer 23 and gate oxide layer 15; said etching being entirely dry, or wet for a first part and dry for a second part. Next, for example by means of a sputtering process, metallization of the front of the wafer 1 is performed, with formation of a metal layer 24, the thickness of which depends upon the capacity to sustain current to be guaranteed for the device.
The process ends with final steps of a known type, including etching of the metal layer 24, deposition of a passivation layer and a subsequent step of masking and etching of the passivation layer, and a process of finishing of the back.
At the end of the manufacturing process, a power MOS device 25 is obtained on a non-planar surface, with the oxide and the gate region in the planar area, and the body region in the non-planar area (in particular within the surface extension of a charge-balance columnar structure).
FIG. 9 shows a variant of the structure of FIG. 8, in which the columnar structures 6 extend throughout the thickness of the epitaxial layer 3 and terminate at the bottom within the substrate 2.
FIG. 10 shows a further variant of the structure of FIG. 8, in which a buffer layer 26, of an N type, extends between the substrate 2 and the epitaxial layer 3. In this case, the columnar structures 6 terminate inside the buffer layer 26. In particular, the presence of the buffer layer 26 enables a greater control over the dopant concentration in the proximity of the bottom of the columnar structures 6 to be achieved, and consequently also control of concentrations of electric field that could lead to phenomena of breakdown of the device.
A second embodiment of the present disclosure is now described, with reference to FIGS. 11-17, in which elements corresponding to the ones previously described are designated by the same reference numbers.
In detail, in an initial step of the manufacturing process, the charge-balance columnar structures 6 are formed in the epitaxial layer 3 overlying the substrate 2, in a way altogether similar to what has been described previously. At the end of said step, the wrinkled surface layer 9 is formed on the top surface 4 of the epitaxial layer 3, said wrinkled surface layer 9 comprising the surface extensions 10 of the columnar structures 6 and the connection portions 11 having a substantially planar pattern (FIG. 11).
Once again, the subsequent figures show, for reasons of greater clarity, an enlargement of a surface portion of the wafer 1, shown by a dashed rectangle in FIG. 11, which encloses a pair of adjacent columnar structures 6.
Then, over the surface of the wafer 1 an implantation of a P type is carried out, without masking, for example using boron with an implantation dosage of approximately between 1013 and 1014 at/cm2 and an energy of approximately between 80 and 200 keV, to form a body layer 30 (FIG. 12). Possibly, the implantation can be carried out through a sacrificial oxide of appropriate thickness (ion pre-implantation oxide) and be followed by a purposely provided process of diffusion. The body layer 30 extends within the wrinkled surface layer 9, and in particular at the surface extensions 10 of the columnar structures 6.
Next (FIG. 13), over the surface of the wafer 1, once again without masking, a blanket implantation of an N type is carried out, for example using phosphorus or arsenic with an implantation dosage of between 5·1014 and 5·1015 at/cm2 and an energy of between 60 and 200 keV, to form a source layer 32 in a surface portion of the wafer 1.
Through a purposely provided mask, two successive implantations of a P type are then carried out (FIG. 14): a first surface implantation for enriching contact with the region of a P type, with a dosage of approximately between 1014 and 1015 at/cm2 and an energy of approximately between 30 and 100 keV; and a second deep implantation to obtain deep-body regions, designated once again by 20, with a dosage of approximately between 5·1014 and 5·1015 at/cm2 and an energy of approximately between 80 and 300 keV. In particular, the deep-body regions 20 are formed in positions corresponding to the surface extensions of first columnar structures 6a, and not in second columnar structures 6b that alternate with the first columnar structures 6a within the epitaxial layer 3.
Next (FIG. 15), at the connection portions 11 of the wrinkled surface layer 9, surface trenches 34 are opened, which traverse said connection portions 11 and reach the underlying epitaxial layer 3. The surface trenches 34 also define body regions 19 of the power device. It should be noted that the surface trenches 34 separate adjacent surface extensions 10.
In the active area a gate oxide layer 15 (thermal oxide) of a thickness of between 20 nm and 150 nm is then deposited over the wafer 1, and on top of it a polysilicon layer 16, of a conformable type, is deposited. In particular, the polysilicon layer 16 fills the surface trenches 34 previously formed (FIG. 16).
The polysilicon layer 16 is then etched by means of selective dry etching and a purposely provided masking so as to obtain gate regions 18 at the surface trenches 34 (FIG. 17). There follows the deposition of an intermediate dielectric layer 23 with a thickness of approximately between 500 nm and 1 μm. Then contacts are opened, by means of masking and subsequent etching of the intermediate dielectric layer 23 and of the gate oxide layer 15; said etching being entirely dry or wet in a first part and dry in a second part. A sputtering process leads to the metallization of the front of the wafer 1, with formation of a metal layer 24, the thickness of which depends upon the capacity to sustain current to be guaranteed for the device. The process terminates with final steps of a known type, in a way altogether similar to the one described previously.
At the end of the manufacturing process according to the second embodiment, a power MOS device 35 is consequently obtained on a non-planar surface, with the oxide and the channel region in an area defined by a trench-formation process. In particular, the channel region extends vertically within the body layer 30 between the source layer 32 and the epitaxial layer 3, at the sides of the trenches 34. Once again, the body region is in the non-planar area, within the surface extension of a charge-balance columnar structure.
FIGS. 18 and 19 show variants of the structure of FIG. 16, in which the columnar structures 6 extend until the substrate 2 and a buffer layer 26, of an N type, arranged between the substrate 2 and the epitaxial layer 3 are, respectively, reached.
Advantages of the manufacturing process and of the corresponding power device are evident from the above description.
In any case, it is emphasized once again that the processes described enables charge-balance power devices to be obtained without resorting to a preventive step of planarization of the surface of the wafer of semiconductor material after the formation of the charge-balance columnar structures. The resulting power device has a cell structure with high-density strips, and is formed on a non-planar surface, with body regions within the surface extensions of the columnar structures that are formed in the process of non-selective epitaxial filling.
In particular, power MOS devices may be obtained with the channel and the gate structure formed in a planar area (first embodiment), or else in an area obtained by means of processes of trench formation (second embodiment).
Thanks to charge balance, it is possible to achieve values of resistivity of the epitaxial layer of less than approximately 2 Ω·cm, and values of cut-off voltage of approximately between 100 and 1500 V as a function of the thickness of the epitaxial region.
It is clear that modifications and variations can be made to what is described and illustrated herein, without thereby departing from the scope of the disclosure.
In particular, by applying the concepts described, it is possible to provide different power devices, for example an IGBT (Insulated-Gate Bipolar Transistor), a bipolar diode, or a Schottky diode.
Furthermore, the possibility of providing dual structures is evident, in which charge balance is obtained by formation of columnar structures with an N doping in an epitaxial layer having a P doping.
Moreover, a system such as an automobile may include first integrated circuit that includes a described power device, and included a second integrated circuit, such as a controller, coupled to the first integrated circuit.

## Claims

1. A system, comprising:
a first integrated circuit, comprising
a first semiconductor layer of a first conductivity, at least a portion of the first semiconductor layer including a drain region,
a first trench disposed in the first semiconductor layer,
a filler of a second conductivity disposed in the first trench,
a heavily-doped, deep-body region of the second conductivity disposed in contact with the filler and forming non-planar surface extensions that extend laterally beyond sides of the filler,
a body region of lighter doping than the deep-body region and located adjacent an end of one of the surface extensions, and
a source region of the first conductivity disposed in contact with the body region; and
a second integrated circuit coupled to the first integrated circuit.

2. The system of claim 1, wherein the first and second integrated circuits are disposed on a same die.

3. The system of claim 1, wherein the first and second integrated circuits are respectively disposed on first and second dies.

4. The system of claim 1, wherein the second integrated circuit comprises a controller.

5. The system of claim 1, wherein the first integrated circuit comprises a controller.

6. The system of claim 1, further comprising:
a second semiconductor layer of the first conductivity disposed over the first semiconductor layer and in contact with the first semiconductor layer and the body region; and
a gate disposed over the second semiconductor layer and over a portion of the body region adjacent to the second semiconductor layer.

7. The system of claim 1, further comprising:
a second semiconductor layer of the first conductivity disposed over the first semiconductor layer and in contact with the body region;
a second trench disposed in the second semiconductor layer and contiguous with the body region; and
a gate disposed in the second trench.

8. The system of claim 1, further comprising:
a second semiconductor layer of the first conductivity disposed over the first semiconductor layer and in contact with the body region;
a second trench disposed in the second semiconductor layer, extending into the first semiconductor layer, and contiguous with the body region; and
a gate disposed in the second trench.

9. The system of claim 1, further comprising:
a second semiconductor layer over which the first semiconductor layer is disposed; and
wherein the first trench and filler extend into the second semiconductor layer.

10. The system of claim 1, further comprising a source conductor in contact with the source region and isolated from the body region.

11. The system of claim 1, further comprising a source conductor in contact with the source and body regions.

12. The system of claim 1, further comprising:
a second trench disposed in the first semiconductor layer;
a second filler of the second conductivity disposed in the second trench;
a second heavily-doped, deep-body region of the second conductivity disposed in contact with the second filler;
a second body region of lighter doping than the second heavily-doped, deep-body region and contacting the second heavily-doped, deep-body region; and
a second source region of the first conductivity disposed in contact with the second body region.

13. A system, comprising:
a first integrated circuit, comprising a first semiconductor layer of a first conductivity, at least a portion of the first semiconductor layer comprising a drain region,
a plurality of trenches disposed in the first semiconductor layer,
a plurality of filler regions of a second conductivity respectively disposed in each of the plurality of trenches,
at least one heavily-doped, deep-body region of the second conductivity disposed in contact with at least one filler region and forming non-planar surface extensions that extend laterally beyond sides of the at least one filler and over material of the first conductivity in the first layer,
at least one body region of the second conductivity and of lighter doping than the at least one deep-body region and located adjacent an end of one of the surface extensions, and
at least one source region of the first conductivity disposed in contact with the at least one body regions, and
a second integrated circuit coupled to the first integrated circuit.

14. The system of claim 13, further comprising:
a second semiconductor layer of the first conductivity disposed over the first semiconductor layer and in contact with the first semiconductor layer and the at least one body region; and
at least one gate disposed over the second semiconductor layer and over a portion of the at least one body region adjacent to the second semiconductor layer.

15. The system of claim 13, wherein, the at least one source region extends along a non-planar surface of the at least one deep-body region.

16. A system, comprising: a first integrated circuit having
a body of semiconductor material having a first layer of a first type of conductivity,
a plurality of columnar regions having a second type of conductivity disposed in the first layer, the columnar regions further comprising non-planar surface extensions that extend laterally away from the columnar regions at a first surface of the first layer,
a plurality of heavily-doped, deep-body regions having the second type of conductivity and disposed within the non-planar surface extensions of the plurality of columnar regions and extending laterally beyond the columnar regions, and
body regions having the second type of conductivity of lighter doping than the deep-body regions and contacting the deep-body regions.

17. The system of claim 16, wherein the non-planar surface extensions and the deep-body regions comprises a non-planar surface pattern.

18. The system of claim 16, wherein the non-planar surface extensions and the deep-body regions comprise a grooved, substantially V-shaped, surface pattern.

19. The system of claim 16, wherein the columnar regions further comprise:
a plurality of deep trenches within the first layer; and
epitaxially-grown semiconductor material within the deep trenches, wherein the columnar regions have a doping level such as to substantially balance a doping level of an opposite type of the first layer.

20. The system of claim 13, further comprising at least one gate structure in contact with the at least one body region, wherein the at least one gate structure comprises a gate oxide and a conductive gate.

21. The system of claim 20, wherein the conductive gate is disposed in a gate trench.

22. The system of claim 13, wherein the trenches taper to a narrower width as they extend into the first layer.

23. The system of claim 13, wherein the trenches are regularly spaced apart in an array.

24. The system of claim 13, wherein at least some of the plurality of trenches extend through the first layer and into a semiconductor layer below the first layer that has a higher dopant concentration than the first layer.

25. The system of claim 13, wherein at least some of the plurality of trenches have a height between approximately 5 microns and approximately 50 microns.