# Patent

## Title
Method of forming a catalyst with inhibited mobility of nano-active material

## Abstract

A method of forming a catalyst, comprising: providing a plurality of support particles and a plurality of mobility-inhibiting particles, wherein each support particle in the plurality of support particles is bonded with its own catalytic particle; and bonding the plurality of mobility-inhibiting particles to the plurality of support particles, wherein each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles, and wherein the mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.

## Background
CROSS-REFERENCE TO RELATED APPLICATIONS:
This application is a continuation of U.S. patent application Ser. No. 12/962,508, filed Dec. 7, 2010 which claims priority to U.S. Provisional Patent Application Ser. No. 61/284,329, filed Dec. 15, 2009 and entitled “MATERIALS PROCESSING”, all of which are hereby incorporated herein by reference in their entirety as if set forth herein.


FIELD OF THE INVENTION
The present invention relates to the field of catalysts. More specifically, the present invention relates to a method of forming catalysts where the mobility of the active catalytic particles is inhibited.
BACKGROUND OF THE INVENTION
Catalysts are used to facilitate and speed up reactions. In some applications, it is desirable to utilize small-scale catalyst material, such as catalytic nano-sized particles. Furthermore, it is also oftentimes desirable to use support structures to provide a substructure upon which the catalytic particles can reside.
In FIG. 1A, catalyst 100 comprises a plurality of support particles 110a-d, each having at least one corresponding catalytic particle 120a-d. Although FIGS. 1A-C show only four support particles 110, it is contemplated that the catalyst 100 can comprise any number of support particles 110. The catalytic particles 120a-d can be chemically absorbed or bonded onto the surface of the support particles 110a-d. However, the catalytic particles 120a-d are not permanently fixed to their bonded support particles 110a-d. Rather, they are able to move from one support particle 110 to another. For example, FIGS. 1A-B show catalytic particles 120b and 120c moving from their respective support particles 110b and 110c to adjacent support particles 110a and 110d, respectively, such that catalytic particles 120a and 120b are disposed on support particle 110a and catalytic particles 120c and 120d are disposed on support particle 110d. In high temperature applications, the movement of these catalytic particles is magnified. As seen in FIG. 1C, as catalytic particles 120b and 120c move to neighboring support particles 110a and 110d, they begin to coalesce with other catalytic particles 120a and 120d on those neighboring support particles, resulting in larger catalytic particles 120ab and 120cd. 
It is understood that the effectiveness and activity of a catalyst are directly proportional to the size of the catalytic particles on the surface of the support particles. As the catalytic particles coalesce into larger clumps, the catalytic particle sizes increase, the surface area of the catalytic particles decreases, and the effectiveness of the catalyst is detrimentally affected.
SUMMARY OF THE INVENTION
The present invention inhibits this movement of catalytic particles and reduces their coalescence, thereby minimizing their individual size and maximizing their combined surface area. The present invention achieves these results by providing one or more mobility-inhibiting particles between the support particles in order to prevent the catalytic particles from moving from one support particles to another.
In one aspect of the present invention, a method of forming a catalyst is provided. The method comprises providing a plurality of support particles and a plurality of mobility-inhibiting particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The plurality of mobility-inhibiting particles is then bonded to the plurality of support particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.
In another aspect of the present invention, a method of forming a catalyst is provided. The method comprises providing a plurality of support particles and a plurality of mobility-inhibiting particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The plurality of support particles is dispersed in a dispersion liquid, thereby forming a dispersion of support particles. The plurality of mobility-inhibiting particles is dispersed in a dispersion liquid, thereby forming a dispersion of mobility-inhibiting particles. The dispersion of support particles is mixed with the dispersion of mobility-inhibiting particles, thereby forming a wet mixture. The wet mixture is freeze-dried, thereby forming a dried mixture. The dried mixture is then calcined, thereby forming a cluster of the plurality of support particles and the plurality of mobility-inhibiting particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.
In yet another aspect of the present invention, a catalyst is provided. The catalyst comprises a plurality of support particles. Each support particle in the plurality of support particles is bonded with its own catalytic particle. The catalyst also comprises a plurality of mobility-inhibiting particles bonded to the plurality of support particles. Each support particle is separated from every other support particle in the plurality of support particles by at least one of the mobility-inhibiting particles. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle.



BRIEF DESCRIPTION OF THE DRAWINGS
FIGS. 1A-C illustrate one embodiment of a catalyst susceptible to the movement and coalescence of its catalytic particles.
FIG. 2 is a flow chart illustrating one embodiment of a method of forming a catalyst in accordance with the principles of the present invention.
FIG. 3 illustrates one embodiment of a particle production system in accordance with the principles of the present invention.
FIG. 4 illustrates another embodiment of a particle production system in accordance with the principles of the present invention.
FIG. 5A illustrates one embodiment of a plurality of support particles with their associated catalytic particles in accordance with the principles of the present invention.
FIG. 5B illustrates one embodiment of a plurality of mobility-inhibiting particles in accordance with the principles of the present invention.
FIG. 6A illustrates one embodiment of a dispersion of support particles with their associated catalytic particles in accordance with the principles of the present invention.
FIG. 6B illustrates one embodiment of a dispersion of mobility-inhibiting particles in accordance with the principles of the present invention.
FIG. 7 illustrates one embodiment of a mixture of the dispersion of support/catalytic particles of FIG. 6A and the dispersion of mobility-inhibiting particles of FIG. 6B in accordance with the principles of the present invention.
FIG. 8 illustrates one embodiment of a cluster of mobility-inhibiting particles bonded between support/catalytic particles in accordance with the principles of the present invention.



DETAILED DESCRIPTION OF THE INVENTION
The following description is presented to enable one of ordinary skill in the art to make and use the invention and is provided in the context of a patent application and its requirements. Various modifications to the described embodiments will be readily apparent to those skilled in the art and the generic principles herein may be applied to other embodiments. Thus, the present invention is not intended to be limited to the embodiment shown but is to be accorded the widest scope consistent with the principles and features described herein.
This disclosure refers to both particles and powders. These two terms are equivalent, except for the caveat that a singular “powder” refers to a collection of particles. The present invention may apply to a wide variety of powders and particles. Powders that fall within the scope of the present invention may include, but are not limited to, any of the following: (a) nano-structured powders(nano-powders), having an average grain size less than 250 nanometers and an aspect ratio between one and one million; (b) submicron powders, having an average grain size less than 1 micron and an aspect ratio between one and one million; (c) ultra-fine powders, having an average grain size less than 100 microns and an aspect ratio between one and one million; and (d) fine powders, having an average grain size less than 500 microns and an aspect ratio between one and one million.
FIG. 2 is a flow chart illustrating one embodiment of a method 200 of forming a catalyst in accordance with the principles of the present invention.
At step 210, a plurality of support particles and mobility-inhibiting particles are provided. Preferably, each support particle is bonded with its own distinct catalytic particle (i.e., a one-to-one ratio between the support particles and the catalytic particles). However, it is contemplated that some support particles can be free of any catalytic particles. The term “support/catalytic particle” is used in this disclosure to refer to a support particle and the catalytic particle bonded to it. The mobility-inhibiting particles are configured to prevent the catalytic particles from moving from one support particle to another support particle. In a preferred embodiment, the mobility-inhibiting particles comprise one or more materials that the catalytic particles do not like to travel to or on, thereby reducing the mobility of the catalytic particles.
In a preferred embodiment, the support particles have a non-catalytic composition, in contrast to the catalytic particles. In this respect, the support particles ideally have a different chemical composition than that of the catalytic particles. Similarly, the mobility-inhibiting particles preferably have a non-catalytic chemical composition that is different from that of both the support particles and the catalytic particles. However, it is contemplated that the particle chemical compositions can vary from embodiment to embodiment. In an exemplary embodiment, the support particles comprise or consist of aluminum oxide and the catalytic particles comprise or consist of a platinum group metal, such as platinum, ruthenium, rhodium, palladium, osmium, or iridium. In some embodiments, the mobility-inhibiting particles comprise or consist of a metal oxide (preferably, a transition metal oxide), including, but not limited to, cerium oxide, lanthanum oxide, and titanium oxide. In other embodiments, the mobility-inhibiting particles comprise or consist of a glass or a ceramic, including, but not limited to, boron nitride, titanium carbide, and titanium diboride. Preferably, the mobility-inhibiting particles do not comprise any precious metals.
In a preferred embodiment, the support particles, the catalyst particles, and the mobility-inhibiting particles are nano-particles. Preferably, the support particles and the mobility-inhibiting particles have a maximum diameter of 500 nanometers and a minimum diameter of 1-5 nanometers, while the catalyst particles have a diameter in the range of 0.5-5 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 10-15 nanometers and the diameter of the catalyst particles is in the range of 2-5 nanometers. However, it is contemplated that other particle sizes can be employed.
It is contemplated that the nano-scale structure of the particles can be achieved in a variety of ways. In a preferred embodiment, the support particles and the catalytic particles are vaporized in the hottest region of a plasma gun. The vaporized particles are then subjected to rapid quenching, causing them to condense. As a result of this vaporization and condensation, nano-sized support particles are formed with nano-sized catalytic particles bonded to them.
Examples of particle production systems employing plasma reactors to produce nano-sized particles are disclosed in U.S. patent application Ser. No. 12/151,935, filed on May 8, 2008 and entitled, “HIGHLY TURBULENT QUENCH CHAMBER”, the entirety of which is hereby incorporated by reference as if set forth herein. One such particle production system 300 is presented in FIG. 3. The system 300 comprises a precursor supply device 310 and a working gas supply device 320 both fluidly coupled to a plasma production chamber 330 having an energy delivery zone 335 formed therein. The plasma production chamber 330 is fluidly coupled with an injection port 340 of a constricting quench chamber 345, thereby allowing the energy delivery zone 335 to fluidly communicate with the quench chamber 345. One or more ports 390 also allow fluid communication of the quench chamber 345 with a controlled atmosphere system 370 (indicated by the dotted lines). The quench chamber 345 is also fluidly coupled with an ejection port 365.
Generally, the plasma production chamber 330 operates as a reactor, producing an output comprising particles within a gas stream. Particle production includes the steps of combination, reaction, and conditioning. Working gas is supplied from a gas source to a plasma reactor. Within the plasma reactor, energy is delivered to the working gas, thereby creating a plasma. A variety of different means can be employed to deliver this energy, including, but not limited to, DC coupling, capacitive coupling, inductive coupling, and resonant coupling. One or more material dispensing devices introduce at least one material, preferably in powder form, into the plasma reactor. The combination within the plasma reactor of the plasma and the material(s) introduced by the material dispensing device(s) forms a highly reactive and energetic mixture, wherein the powder can be vaporized. This mixture of vaporized powder moves through the plasma reactor in the flow direction of the working gas. As it moves, the mixture cools and particles are formed therein. The still-energetic output mixture, comprising hot gas and energetic particles, is emitted from the plasma reactor.
In an exemplary embodiment, the plasma production chamber 330 combines precursor material (preferably in powder form) supplied from the precursor supply device 310 and working gas supplied from the working gas supply device 320 within the energy delivery zone 335, where the working gas is energized to form a plasma. The plasma is applied to the precursor material within the energy delivery zone 335 to form an energized, reactive mixture. This mixture comprises one or more materials in at least one of a plurality of phases, which may include vapor, gas, and plasma.
The reactive mixture flows from the energy delivery zone 335 into the constricting quench chamber 345 through the injection port 340. As the hot mixture moves from the energy delivery zone 335, it expands rapidly within the quench chamber 345 and cools. While the mixture flows into the quench chamber 345, the ports 390 supply conditioning fluid along the inner surfaces of the quench chamber 345. The conditioning fluid combines, at least to some extent, with the mixture, and flows from the quench chamber 345 through the ejection port 365.
During a period immediately after entering the quench chamber 345, particle formation occurs. Furthermore, the supply of conditioning fluid along the inner surfaces of the quench chamber 345 works to condition the reactive mixture, to maintain entrainment of the particles therein, and to prevent the depositing of material on the inner surfaces of the quench chamber 345.
Still referring to FIG. 3, the structure of the quench chamber 345 can be formed of relatively thin walled components capable of dissipating substantial heat. For example, the thin-walled components can conduct heat from inside the chamber and radiate the heat to the ambient. The quench chamber 345 comprises a substantially cylindrical surface 350, a cone-like (frusto-conical) surface 355, and an annular surface 360 connecting the injection port 340 with the cylindrical surface 350. The cylindrical surface 350, having a large diameter relative to the size of the injection port 340, provides accommodation for the expansion of the reactive mixture that occurs after the mixture flows into the quench chamber 345. The cone-like surface 355 extends from the cylindrical surface 350, away from the injection port 340 and towards the ejection port 365. The cone-like surface 355 is sufficiently smoothly varying so as to not unduly compress fluid flowing from through the quench chamber 345 to the ejection port 365.
Substantial heat is emitted, mostly in the form of radiation, from the mixture following its entry into the quench chamber 345. The quench chamber 345 is preferably designed to dissipate this heat efficiently. For example, the surfaces of the quench chamber 345 are preferably exposed to a cooling apparatus (not shown).
Still referring to FIG. 3, the controlled atmosphere system 370 preferably comprises a chamber 385 into which conditioning fluid is introduced from a reservoir 375 through a conduit 380. The conditioning fluid preferably comprises argon. However, other inert, relatively heavy gases are equally preferred. Furthermore, the preferable mechanism of providing the conditioning fluid into the quench chamber 345 is the formation of a pressure differential between the quench chamber 345 and the outlet 365. Such pressure differential will draw the conditioning fluid into the quench chamber 345 through the ports 390. Other less preferred methods of providing the conditioning fluid include, but are not limited to, forming positive pressure within the chamber 385.
The frusto-conical shape of the quench chamber 345 can provide a modest amount of turbulence within the quench region, thereby promoting the mixing of the conditioning fluid with the reactive mixture, and increasing the quenching rate beyond prior art systems. However, in some situations, an even greater increase in quenching rate may be desired. Such an increase in quenching rate can be achieved by creating a highly turbulent flow within a region of a quench chamber where the conditioning fluid is mixed with the reactive mixture.
FIG. 4 illustrates a particle production system 400 with a highly turbulent quench chamber 445. The system 400 comprises a precursor supply device 410 a working gas supply device 420 fluidly coupled to a plasma production and reaction chamber 430, similar to plasma production chamber 330 discussed above with reference to FIG. 3. An energy delivery system 425 is also coupled with the plasma production and reactor chamber 430. The plasma production and reactor chamber 430 includes an injection port 440 that communicates fluidly with the constricting quench chamber 445. One or more ports 490 can also allow fluid communication between the quench chamber 445 and a controlled atmosphere system 470, similar to controlled atmosphere system 370 in FIG. 3. The quench chamber 445 is also fluidly coupled to an outlet 465.
Generally, the chamber 430 operates as a reactor, similar to chamber 330 in FIG. 3, producing an output comprising particles within a gas stream. Production includes the basic steps of combination, reaction, and conditioning as described later herein. The system combines precursor material supplied from the precursor supply device 410 and working gas supplied from the working gas supply device 420 within the energy delivery zone of the chamber 430. The system energizes the working gas in the chamber 430 using energy from the energy supply system 490, thereby forming a plasma. The plasma is applied to the precursor material within the chamber 430 to form an energized, reactive mixture. This mixture comprises one or more materials in at least one of a plurality of phases, which may include vapor, gas, and plasma. The reactive mixture flows from the plasma production and reactor chamber 430 into the quench chamber 445 through an injection port 440.
The quench chamber 445 preferably comprises a substantially cylindrical surface 450, a frusto-conical surface 455, and an annular surface 460 connecting the injection port 440 with the cylindrical surface 450. The frusto-conical surface 460 narrows to meet the outlet 465. The plasma production and reactor chamber 430 includes an extended portion at the end of which the injection port 440 is disposed. This extended portion shortens the distance between the injection port 440 and the outlet 465, reducing the volume of region in which the reactive mixture and the conditioning fluid will mix, referred to as the quench region. In a preferred embodiment, the injection port 440 is arranged coaxially with the outlet 465. The center of the injection port is positioned a first distance d1 from the outlet 465. The perimeter of the injection port is positioned a second distance d2 from a portion of the frusto-conical surface 455. The injection port 440 and the frusto-conical surface 455 form the aforementioned quench region therebetween. The space between the perimeter of the injection port 440 and the frusto-conical surface 455 forms a gap therebetween that acts as a channel for supplying conditioning fluid into the quench region. The frusto-conical surface 455 acts as a funneling surface, channeling fluid through the gap and into the quench region.
While the reactive mixture flows into the quench chamber 445, the ports 490 supply conditioning fluid into the quench chamber 445. The conditioning fluid then moves along the frusto-conical surface 455, through the gap between the injection port 440 and the frusto-conical surface 455, and into the quench region. In some embodiments, the controlled atmosphere system 470 is configured to control the volume flow rate or mass flow rate of the conditioning fluid supplied to the quench region.
As the reactive mixture moves out of the injection port 440, it expands and mixes with the conditioning fluid. Preferably, the angle at which the conditioning fluid is supplied produces a high degree of turbulence and promotes mixing with the reactive mixture. This turbulence can depend on many parameters. In a preferred embodiment, one or more of these parameters is adjustable to control the level of turbulence. These factors include the flow rates of the conditioning fluid, the temperature of the frusto-conical surface 455, the angle of the frusto-conical surface 455 (which affects the angle at which the conditioning fluid is supplied into the quench region), and the size of the quench region. For example, the relative positioning of the frusto-conical surface 455 and the injection port 440 is adjustable, which can be used to adjust the volume of quench region. These adjustments can be made in a variety of different ways, using a variety of different mechanisms, including, but not limited to, automated means and manual means.
During a brief period immediately after entering the quench chamber 445, particle formation occurs. The degree to which the particles agglomerate depends on the rate of cooling. The cooling rate depends on the turbulence of the flow within the quench region. Preferably, the system is adjusted to form a highly turbulent flow, and to form very dispersed particles. For example, in preferred embodiments, the turbidity of the flow within the quench region is such that the flow has a Reynolds Number of at least 1000.
Still referring to FIG. 4, the structure of the quench chamber 445 is preferably formed of relatively thin walled components capable of dissipating substantial quantities of heat. For example, the thin-walled components can conduct heat from inside the chamber and radiate the heat to the ambient.
Substantial heat is emitted, mostly in the form of radiation, from the reactive mixture following its entry into the quench chamber 445. The quench chamber 445 is designed to dissipate this heat efficiently. The surfaces of the quench chamber 245 are preferably exposed to a cooling system (not shown). In a preferred embodiment, the cooling system is configured to control a temperature of the frusto-conical surface 455.
Following injection into the quench region, cooling, and particle formation, the mixture flows from the quench chamber 445 through the outlet port 465. Suction generated by a generator 495 moves the mixture and conditioning fluid from the quench region into the conduit 492. From the outlet port 465, the mixture flows along the conduit 492, toward the suction generator 495. Preferably, the particles are removed from the mixture by a collection or sampling system (not shown) prior to encountering the suction generator 495.
Still referring to FIG. 4, the controlled atmosphere system 470 comprises a chamber 485, fluidly coupled to the quench region through port(s) 490, into which conditioning fluid is introduced from a reservoir, such as reservoir 375 from FIG. 3, through a conduit 480. As described above, the conditioning fluid preferably comprises argon. However, other inert, relatively heavy gases are equally preferred. Also, as discussed above, the preferable mechanism of providing the conditioning fluid into the quench chamber 445 is the formation of a pressure differential between the quench chamber 445 and the outlet 465. Such pressure differential will draw the conditioning fluid into the quench chamber 445 through the ports 490. Other methods of providing the conditioning fluid include, but are not limited to, forming positive pressure within the chamber 485.
The angle of the frusto-conical surface affects the angle at which the conditioning fluid is supplied into the quench region, which can affect the level of turbulence in the quench region. The conditioning fluid preferably flows into the quench region along a plurality of momentum vectors. The greater the degree of the angle between the momentum vectors, the higher the level of turbulence that will be produced. In a preferred embodiment, the high turbulent quench chamber comprises a frusto-conical surface that is configured to funnel at least two conditioning fluid momentum vectors into the quench region such that there is at least a 90 degree angle between the two momentum vectors. It is contemplated that other angle degree thresholds may be applied as well. For example, attention may also be paid to the angle formed between at least one of the conditioning fluid momentum vectors and the momentum vector of the reactive mixture. In one embodiment of a highly turbulent quench chamber, a reactive mixture inlet is configured to supply the reactive mixture into the quench region along a first momentum vector, the frusto-conical surface is configured to supply the conditioning fluid to the quench region along a second momentum vector, and the second momentum vector has an oblique angle greater than 20 degrees relative to the first momentum vector.
The size of the quench region also affects the level of turbulence in the quench region. The smaller the quench region, the higher the level of turbulence that will be produced. The size of the quench region can be reduced by reducing the distance between the center of the injection port 440 and the outlet 465.
The high turbulence produced by the embodiments of the present invention decreases the period during which particles formed can agglomerate with one another, thereby producing particles of more uniform size, and in some instances, producing smaller-sized particles. Both of these features lead to particles with increased dispersibility and increased ratio of surface area to volume.
Referring back to the method 200 in FIG. 2, particle production system 200 or 300 (or variations thereof) can be used to provide one or more of the support particles, catalytic particles, and mobility-inhibiting particles in nano-scale form. For example, these particles can be introduced as micron-sized precursor material into the particle production system, where they are vaporized and then condensed to form nano-size particles. In a preferred embodiment, the support/catalytic particles are formed and provided separately from the mobility-inhibiting particles, thereby avoiding any premature interaction (e.g., bonding) between the mobility-inhibiting particles and the support/catalytic particles. Such separation can be achieved in a variety of ways, including, but not limited to, using different particle production systems for both groups, or by using the same particle production system for both groups at different times.
FIG. 5A illustrates one embodiment of a plurality of support particles 510 provided in step 210 of method 200. Each support particle 510 has a catalytic particle 520 bonded to it (preferably to its exterior surface). Although, in some embodiments, certain support particles 510 may be absent a catalytic particle 520. It is contemplated that the size of the catalytic particle 520 on the support particle 510 can be affected by changing the amount of catalytic material provided to the particle production system or by otherwise adjusting the mix ratio of catalytic particles to support particles provided to the particle production system. The larger the concentration of catalytic particles provided to the particle production system, the larger the size of the catalytic particles 520 bonded to the support particles 510.
FIG. 5B illustrates one embodiment of a plurality of mobility-inhibiting particles 530 provided in step 210 of method 200. The stripes on the mobility-inhibiting particles 530 are provided solely for the purpose of helping to distinguish the mobility-inhibiting particles 530 from the support particles 510.
At step 220 of method 200, the support/catalytic particles and the mobility-inhibiting particles are dispersed in liquid. FIG. 6A illustrates one embodiment of a dispersion 625 of support/catalytic particles. A close-up of the dispersion 625 shows the support/catalytic particles being separated by a liquid 615a and being made up of support particles 610 having catalytic particles 620 bonded to them. FIG. 6B illustrates one embodiment of a dispersion 635 of mobility-inhibiting particles 630. A close-up of the dispersion 635 shows the mobility-inhibiting particles 630 being separated by a liquid 615b. Although FIGS. 6A-B show the support/catalytic particles and the mobility-inhibiting particles in separate dispersions 625 and 635, it is contemplated that they can also be dispersed in the same container at the same time to form one dispersion.
The dispersion liquids 615a and 615b can be any liquids configured to disperse the support/catalytic particles and the mobility-inhibiting particles, respectively. In a preferred embodiment, the dispersion liquids comprise or consist of water or any organic liquid, such as glycol ethers. In some embodiments, dispersions 625 and 635 both use the same type of dispersion liquid. In other embodiments, dispersions 625 and 635 use different types of dispersion liquids (e.g., dispersion liquid 615a is water and dispersion liquid 615b is ethylene glycol).
In some embodiments, one or more surfactants or other dispersing aids, such as cationic, anionic, zwitterionic, and/or non-ionic carbon based oligomers and/or polymers, can be added to the dispersion liquid. Certain surfactants can be added to the dispersion in order to adjust its acidity and make it stable. Acids can be added to the dispersion in order to acidify the surface of N-oxide particles. The surfactants are carefully chosen so that they will not be harmful to the catalyst material. In preferred embodiments, no sulfates or phosphates are added to the dispersion. Examples of surfactants that can be added to the dispersion liquid are carboxylic acids, polyamines, and polyethers. It is contemplated that other surfactants or dispersing aids can be used as well.
It is contemplated that the different variations of particle, dispersion liquid, and surfactant concentrations can be employed. In a preferred embodiment, the dispersion comprises a 5-25% by weight concentration of powder, meaning that the support/catalytic particles and the mobility-inhibiting particles each make up approximately 5-25% by weight of their respective dispersions. In a preferred embodiment, the dispersion comprises a 1-10% by weight concentration of surfactant or other dispersing aid. Preferably, the surfactant or other dispersing aid accounts for approximately 5% or less of the dispersion.
At step 230 of method 200, the dispersed support/catalytic particles and mobility-inhibiting particles are mixed to form a mixture. If the support/catalytic particles and the mobility-inhibiting particles were not originally dispersed together, or not subsequently placed into the same container to form a single dispersion, then they are at this time placed into the same container where they can be mixed together. In a preferred embodiment, the mixing is performed by sonication, mechanical mixing, and/or shear mixing. However, it is contemplated that a variety of other agitation methods can be employed in order to perform this mixing.
FIG. 7 illustrates one embodiment of a mixture 745 of the dispersions in one container. The mixture 745 comprises a plurality of support particles 710, each having a catalytic particle 720 bonded to it, and mobility-inhibiting particles 730. The particles are separated by the liquid 715, which can comprise any dispersion liquids and surfactants (or other dispersing aids) used in the prior steps.
At step 240, the dispersion liquid is removed from the mixture to form a dried mixture. It is contemplated that the liquid can be removed in a variety of ways. In one embodiment, the dispersion of particles is freeze-dried. The mixture is poured into a freeze-dry appropriate vessel. It is then frozen with liquid nitrogen or some other medium that is cool enough to freeze the dispersion of particles. In one embodiment, the liquid nitrogen, or other freezing medium, is at approximately −60 degrees Celsius. However, it is contemplated that the liquid nitrogen, or other freezing medium, can be used at other temperatures as well. The mixture is then placed into a vacuum system, where the dispersion of particles remains frozen as the water, or other dispersing liquid, is removed via vacuum pressure. In one embodiment, a vacuum pressure of approximately 10 microns is employed. In other embodiments, a vacuum pressure of between approximately 2 microns and approximately 5 microns is employed.
The vacuum pressure removes the water and any other liquid in the mixture having a higher vapor pressure than water. However, in some embodiments, the surfactant remains with the frozen dispersion of particles. The removal of the water leaves a porous powder structure of the support/catalytic particles and the mobility-inhibiting particles, with the surfactant disposed within the pores. The resulting powder is in an intermediate state, being loosely bonded together, yet dry to the touch, providing mechanical handling ability.
At step 250, the dried mixture is calcined, thereby baking off any surfactant and forming clusters of mobility-inhibiting particles bonded between the support/catalytic particles. In some embodiments, the powder is placed in a crucible. It is contemplated that the crucible can be made of ceramic or a variety of other materials. The crucible is then placed in a calcining furnace, where it is heated at a given temperature for a given time. In some embodiments, the crucible is heated in the calcining furnace at approximately 550 degrees Celsius for approximately 2 hours. However, it is contemplated that other temperatures and heating time can be employed as well. In some embodiments, the crucible is placed in a furnace that has already been preheated to the desired baking temperature. Test results have shown that by preheating the furnace before placing the crucible inside, instead of ramping up the temperature to the desired temperature while the crucible is in the furnace, the dispersion of the metal particles can be maximized. However, it is contemplated that, in some embodiments, the furnace temperature can be ramped up while the crucible is in the furnace. In some embodiments, a ramp rate of 1-50 degrees Celsius is employed to raise the temperature of the furnace while the crucible is inside. In a preferred embodiment, the furnace provides an ambient air environment within which the crucible, and consequently the powder, can be heated. It is contemplated that the environment within the furnace need not comprise air. However, it preferably contains some amount of oxygen.
The calcining of the dried mixture takes it from a Van der Waals or proximity attraction between the particles to an actual covalent bond between the particles, resulting in a surfactant-free agglomeration of the support/catalytic particles and the mobility-inhibiting particles. FIG. 8 illustrates one embodiment of a cluster of mobility-inhibiting particles 830 bonded between support particles 810, which have catalytic particles 820 bonded to them. In some embodiments, the present invention produces clusters in the range of 0.5-50 microns. In some embodiments, the present invention produces clusters in the range of 5-10 microns. However, it is contemplated that other cluster sizes can be produced as well.
In some embodiments, the loading percentages of the powders (support, catalyst, and mobility-inhibiting) are adjusted in order to achieve a desired powder concentration for each particular type of powder in the resulting clusters. In some embodiments, a 0.01-15% loading of catalyst powder is employed. In a preferred embodiment, a 0.5-3% loading of catalyst powder is employed. However, it is contemplated that other loading percentages can be employed as well.
In a preferred embodiment, the support particles, the catalyst particles, and the mobility-inhibiting particles in the resulting clusters are nano-particles. Preferably, the support particles and the mobility-inhibiting particles have a maximum diameter of 500 nanometers and a minimum diameter of between 1-5 nanometers, while the catalyst particles have a diameter in the range of 0.5-5 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 5-20 nanometers. In some embodiments, the diameter of the support particles and the mobility-inhibiting particles is in the range of 10-15 nanometers and the diameter of the catalyst particles is in the range of 2-5 nanometers. However, it is contemplated that other particle sizes can be employed.
The introduction and bonding of mobility-inhibiting particles to and between the support/catalytic particles prevents the catalytic particles from moving from one support particle to another, thereby preventing the coalescence of the catalytic particles. As a result, the size of the individual catalytic particles can be minimized and the total catalytic surface area of the cluster can be maximized.
The present invention has been described in terms of specific embodiments incorporating details to facilitate the understanding of principles of construction and operation of the invention. Such reference herein to specific embodiments and details thereof is not intended to limit the scope of the claims appended hereto. It will be readily apparent to one skilled in the art that other various modifications may be made in the embodiment chosen for illustration without departing from the spirit and scope of the invention as defined by the claims.

## Claims

1. A method of forming a catalyst, comprising:
nano-sizing a precursor support powder;
nano-sizing a precursor catalytic powder; and
bonding the nano-sized catalytic powder to the nano-sized support powder to form combined support/catalytic particles; and
bonding a plurality of mobility-inhibiting particles to the combined support/catalytic particles,
wherein the mobility-inhibiting particles are configured to inhibit movement of the catalytic particles on the support particles.

2. The method of claim 1, wherein
the precursor support powder has an average grain size equal to or greater than 1 micron; and
the catalytic powder has an average grain size equal to or greater than 1 micron.

3. The method of claim 1, wherein:
nano-sizing the precursor support powder and the precursor catalytic powder comprises applying a plasma stream to the precursor support powder and to the precursor catalytic powder, thereby vaporizing the precursor support powder and the precursor catalytic powder; and
bonding the nano-sized catalytic powder to the nano-sized support to form the combined support/catalytic particles comprises condensing the vaporized support powder and the vaporized catalytic powder to form the combined support/catalytic particles.

4. The method of claim 1, wherein the plurality of mobility-inhibiting particles are formed by nano-sizing a precursor mobility-inhibiting powder that has an average grain size equal to or greater than 1 micron.

5. The method of claim 4, wherein nano-sizing the precursor mobility-inhibiting powder comprises:
applying a plasma stream to the precursor mobility-inhibiting powder, thereby vaporizing the precursor mobility-inhibiting powder; and
condensing the vaporized mobility-inhibiting powder.

6. The method of claim 1, comprising:
dispersing the support/catalytic particles in a dispersion liquid;
dispersing the plurality of mobility-inhibiting particles in a dispersion liquid; and
mixing the dispersed support/catalytic particles particles with the dispersed mobility-inhibiting particles, thereby forming a mixture of the dispersed support/catalytic particles and the dispersed mobility-inhibiting particles.

7. The method of claim 6, wherein the dispersion liquid for at least one of the support/catalytic particles and the mobility-inhibiting particles comprises water.

8. The method of claim 6, wherein the dispersion liquid for at least one of the support/catalytic particles and the mobility-inhibiting particles comprises an organic liquid.

9. The method of claim 8, wherein the organic liquid is a glycol ether.

10. The method of claim 6, wherein at least one of dispersing the plurality of support/catalytic particles and dispersing the plurality of mobility-inhibiting particles comprises adding a surfactant to the dispersion liquid.

11. The method of claim 10, wherein the surfactant is selected from the group consisting of a carboxylic acid, a polyamine, and a polyether.

12. The method of claim 6, wherein the dispersed support/catalytic particles and the dispersed mobility-inhibiting particles are mixed using a sonication process.

13. The method of claim 6, wherein the step of bonding the plurality of mobility-inhibiting particles to the support/catalytic particles, comprises freeze-drying the mixture of dispersed support/catalytic support particles and dispersed mobility-inhibiting particles, thereby forming a dried mixture of dispersed support/catalytic particles and dispersed mobility-inhibiting particles.

14. The method of claim 13, wherein the step of bonding plurality of mobility-inhibiting particles to the support/catalytic particles comprises calcining the dried mixture of dispersed support/catalytic particles and dispersed mobility-inhibiting particles.

15. The method of claim 1, wherein the nano-sized support powder comprises alumina.

16. The method of claim 1, wherein the nano-sized catalytic powder comprises platinum.

17. The method of claim 1, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the support/catalytic particles.

18. The method of claim 17, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.

19. The method of claim 17, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.

20. The method of claim 1, wherein:
the nano-sized support powder has a diameter of between 1 nanometer and 500 nanometers;
the nano-sized catalytic powder has a diameter between 0.5 nanometers and 5 nanometers; and
the mobility-inhibiting particles have a diameter between 1 nanometer and 500 nanometers.

21. A method of forming a catalyst, comprising:
nano-sizing a precursor support powder;
nano-sizing a precursor catalytic powder; and
bonding the nano-sized catalytic powder to the nano-sized support powder to form combined support/catalytic particles;
dispersing the support/catalytic particles in a dispersion liquid, thereby forming a dispersion of support/catalytic particles;
dispersing a plurality of mobility-inhibiting particles in a dispersion liquid, thereby forming a dispersion of mobility-inhibiting particles;
mixing the dispersion of support/catalytic particles with the dispersion of mobility-inhibiting particles, thereby forming a wet mixture;
freeze-drying the wet mixture, thereby forming a dried mixture; and
calcining the dried mixture, thereby forming a cluster of the support/catalytic particles and the plurality of mobility-inhibiting particles, wherein the mobility-inhibiting particles are configured to inhibit movement of the catalytic particles on the support particles.

22. The method of claim 21, comprising:
nano-sizing a precursor support powder that has an average grain size equal to or greater than 1 micron;
nano-sizing a precursor catalytic powder that has an average grain size equal to or greater than 1 micron; and
nano-sizing a precursor mobility-inhibiting powder that has an average grain size equal to or greater than 1 micron.

23. The method of claim 21, wherein nano-sizing the precursor powders comprise:
applying a plasma stream to the precursor powders, thereby vaporizing the precursor powders; and
condensing the vaporized powders.

24. The method of claim 21, wherein the dispersion liquid for at least one of the support/catalytic particles and the mobility-inhibiting particles comprises water.

25. The method of claim 21, wherein the dispersion liquid for at least one of the support/catalytic particles and the mobility-inhibiting particles comprises an organic liquid.

26. The method of claim 25, wherein the organic liquid is a glycol ether.

27. The method of claim 21, wherein at least one of dispersing the support/catalytic particles and dispersing the plurality of mobility-inhibiting particles comprises adding a surfactant to the dispersion liquid.

28. The method of claim 27, wherein the surfactant is selected from the group consisting of a carboxylic acid, a polyamine, and a polyether.

29. The method of claim 21, wherein the step of mixing the dispersion of support/catalytic particles with the dispersion of mobility-inhibiting particles comprises using a sonication process.

30. The method of claim 21, wherein the nano-sized support powder comprises alumina.

31. The method of claim 21, wherein the nano-sized catalytic powder comprises platinum.

32. The method of claim 21, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the support/catalytic particles.

33. The method of claim 32, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.

34. The method of claim 32, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.

35. The method of claim 21, wherein:
nano-sized support powder has a diameter of between 1 nanometer and 500 nanometers;
the nano-sized catalytic powder has a diameter between 0.5 nanometers and 5 nanometers; and
the mobility-inhibiting particles have a diameter between 1 nanometer and 500 nanometers.

36. A catalyst comprising:
a plurality of support particles comprising alumina and having a diameter between 1 nanometer and 500 nanometers, the plurality of support particles are bonded to a plurality catalytic particles to form support/catalytic particles; and
a plurality of mobility-inhibiting particles having a diameter between 1 nanometer and 500 nanometers bonded to the plurality of support/catalytic particles,
wherein the mobility-inhibiting particles are configured to inhibit the catalytic particles from moving on the support particles.

37. The catalyst of claim 36, wherein the catalytic particles comprise platinum.

38. The catalyst of claim 36, wherein the plurality of mobility-inhibiting particles comprises a different chemical composition than the plurality of support particles.

39. The catalyst of claim 38, wherein the plurality of mobility-inhibiting particles comprises a plurality of ceramic particles.

40. The catalyst of claim 38, wherein the plurality of mobility-inhibiting particles comprises a plurality of metal-oxide particles.