# Patent

## Title
Method of producing an identity document

## Abstract

This application is a continuation-in-part of application Ser. No. 178,775, filed Aug. 18, 1980, the priority of which is claimed under 35 U.S.C. 120.

## Background
Lithium-organic electrolyte secondary batteries suffer of limited rechargeability mainly due to the poor cyclability of the lithium metal electrode. In fact lithium is unavoidably attacked and/or passivated by any organic electrolyte: this results in non-uniform lithium deposits which, on cycling, assume a progressively dendritic morphology. Furthermore, part of the deposited lithium is isolated from the substrate and thus cannot be electrostripped in the subsequent discharge; accordingly, the cycling efficiency rapidly declines.

A possible solution to this problem consists in replacing the lithium metal electrode with a non-metal lithium electrode having no tendency to be attacked and/or passivated by the organic electrolyte. This approach has been proposed in the particular case of rechargeable lithium batteries based on two dichalcogenide electrodes (U.S. Pat. No. 4,194,062). However, in order to attain high-voltage, high-energy density lithium batteries, the non-metal negative electrode must fulfil the following requirements: reversibly react per mole of electrode material;

These requirements are not simultaneously fulfilled by the transition metal chalcogenides which have been so far proposed as positive electrodes (U.S. Pat. No. 4,035,555) or both for negative and positive electrodes (U.S. Pat. No. 4,194,062).

According to the present invention, a non-aqueous secondary lithium cell uses as the negative electrode a material Li.sub.x M.sub.2 O.sub.3 * obtained by electrochemically reacting with lithium a metal oxide of the M.sub.2 O.sub.3 type, where M is Co, Fe, Cr. The composition of the material Li.sub.x M.sub.2 O.sub.3 may vary within the range 1.0.ltoreq.x.ltoreq.5.5. The positive electrode may be selected from various classes of materials, according to the desired voltage and performances of the cell. does not imply any hypothesis about the mechanism of the reaction of lithium with M.sub.2 O.sub.3.

FIG. 1 shows the cell voltage, as a function of the depth of discharge, of a Li/LiClO.sub.4,PC**/Li.sub.x Fe.sub.2 O.sub.3 cell at room temperature.

FIGS. 2a through 2c show a cycling test, at a current density of 0.25 mA cm.sup.-2 of a Li/LiClO.sub.4,PC/Li.sub.x Fe.sub.2 O.sub.3 cell around various lithium concentrations at room temperature.

FIGS. 3a and 3b show the cell voltage during discharge and the cycling behavior at 0.5 mA cm.sup.-2 of a Li.sub.6-x Fe.sub.2 O.sub.3 /LiClO.sub.4,PC/Li.sub.x TiS.sub.2 cell at room temperature.

FIG. 4a and 4b show the cell voltage during discharge and the recycling behaviour at 0.5 mA cm.sup.-2 of a Li.sub.6-x Fe.sub.2 O.sub.3 /LiClO.sub.4,PC/Li.sub.x V.sub.2 O.sub.5 cell at room temperature.

It has been discovered that the oxides of the M.sub.2 O.sub.3 type where M is Co, Fe, Cr and related elements can react electro-chemically with lithium, and the resulting materials, which are here indicated as Li.sub.x M.sub.2 O.sub.3, fulfil the requirements previously mentioned for a non-metal negative electrode in lithium secondary cells. In FIG. 1, as a typical example, the discharge curve of the cell Li/LiClO.sub.4,PC/Fe.sub.2 O.sub.3 at 0.25 mA cm.sup.-2 and at room temperature is shown. A typical electrolyte, such as LiClO.sub.4,PC, has been chosen for assembling this cell and the others quoted in the following examples, but any electrolyte which is stable with respect to the electrode materials and has a sufficiently low resistivity may be employed. The curve of FIG. 1 illustrates the capability of this electrode material to react with a large amount of lithium with a small voltage variation, especially for lithium content higher than 1 and lower than 5.5 equivalents of lithium per Fe.sub.2 O.sub.3 mole. The latter feature (high capacity) and the low and almost constant voltage with respect to lithium, are particularly significant when compared with those of known intercalation materials which can operate in the same voltage range.

Furthermore the reaction with lithium is highly reversible as indicated in the example of FIG. 2, where the cycling behaviour of Fe.sub.2 O.sub.3 around various compositions is shown. It is apparent that the cycling behaviour improves in the range of medium-high lithium activity, i.e. just where the application of the material as an alternative to the lithium electrode is optimised.

The active material may be prepared electrochemically by discharging cells of the type Li/LiClO.sub.4,PC/Fe.sub.2 O.sub.3 (see FIG. 1), where Fe.sub.2 O.sub.3 is preferably in the alpha phase; the discharge is interrupted when the desired composition Li.sub.x Fe.sub.2 O.sub.3 is reached. The active material may then be removed and used as the negative electrode in another cell. For the realisation of the latter, positive electrodes may be selected from various classes of materials, such as transition metal dichalcogenides (TiS.sub.2, NbS.sub.2, TaS.sub.2, VS.sub.2, etc.), metal oxides (TiO.sub.2, MoO.sub.3, WO.sub.3, etc.), and related compounds. The choice of the positive is made according to the desired performances (voltage, specific capacity, energy and power) of the battery.

FIGS. 3a, 3b, and 4a, 4b show typical examples of cells obtained by coupling Li.sub.6 Fe.sub.2 O.sub.3 with two intercalation positives.

FIGS. 3a and 3b the behaviour of the cell Li.sub.6-x Fe.sub.2 O.sub.3 /LiClO.sub.4,PC/Li.sub.x TiS.sub.2 is reported: the curve a is the discharge curve of the cell at 0.5 mA cm.sup.-2 at room temperature, while b is a typical cycle at the same current density. The corresponding performances of the cell Li.sub.6-x Fe.sub.2 O.sub.3 /LiClO.sub.4,PC/Li.sub.x V.sub.2 O.sub.5 are reported in FIGS. 4a and 4b.

## Claims

1. A rechargeable lithium battery with non-metal electrodes which comprises a positive electrode, a negative electrode and a non-aqueous electrolyte, said negative electrode being a material of the formula Li.sub.x M.sub.2 O.sub.3 where M is a transition metal and x ranges from 1 to 6, said material being obtained by electrochemically reacting with lithium a metal oxide of the formula M.sub.2 O.sub.3.

2. The battery according to claim 1, wherein M is Fe.

3. The battery according to claim 1, wherein M is Co or Cr.

4. The battery according to claim 1, wherein x ranges from 0.1 to 5.5.

5. The battery according to claim 1, wherein said non-aqueous electrolyte is LiClO.sub.4 in propylene carbonate.

6. The battery according to claim 1, wherein said material of the formula Li.sub.x M.sub.2 O.sub.3 is prepared by discharging cells of the type Li/LiClO.sub.4, propylene carbonate/Fe.sub.2 O.sub.3.