# Patent

## Title
Process and apparatus for manufacturing an anisotropic conductor sheet

## Abstract

This application is a Divisional of application U.S. Ser. No. 08/757,953, filed on Nov. 22, 1996, which is a continuation of application U.S. Ser. No. 08/444,866, filed on May 19, 1995 (abandoned).

## Background
The present invention relates to bodies that absorb water and aqueous liquids and which consist of foamed plastic and latex layers and superabsorbent polymers. The present invention further relates to a process for producing these bodies and to their use as absorbents, particularly in hygienics for the absorption of body fluids, such as blood, sweat, urine, and other liquid excretions. Additionally, the present invention relates to the use of these bodies as components in wound dressings, in packaging and insulating materials, in textiles for clothing and cleaning purposes, and to their use in the cultivation of plants.

Substances having a layered structure and the capacity of absorbing aqueous liquids have been known for some time. U.S. Pat. No. 4,000,028 describes materials of latex foam and cellulose fluff, but not comprising superabsorbent polymers, thus they have a very limited capability of absorbing liquids.

U.S. Pat. No. 5,128,082 describes absorbents produced from mixtures of fluff materials and superabsorbent polymers and a surrounding latex forming the outer layer. The fluff portion largely prevents the contact between polymer and latex. The polymer portion in these bodies is not distributed in a uniform manner; this results in the known difficulties with respect to the absorption of liquids connected with the disadvantages regarding the wearing behavior of these hygienic articles.

EP 0 212 618 B1 describes diaper constructions wherein these disadvantages are avoided by the fact that the polymers which have a certain particle-size distribution are distributed in the cellulose fiber layer by using a gradient. However, such constructions are insufficiently stable; in particular the distribution of the materials changes during the transport.

In general, the mixing of superabsorbent polymers with watery latex foams results in the fact that the foams collapse under water removal; this destroys the open-cell structure with the consequence that only the superficial polymer particles are capable of absorbing liquids.

Mixtures of superabsorbent polymers and latex foams are known from EP 0 427 219 A2; these are obtained by introducing the polymers into the foamed latex in the form of a powder spray. This method does not permit a defined construction of these bodies; in particular, an accurate distribution of the polymers is not possible.

The use of a tape as a component for the insulation of electric cables is known from EP 0 577 233 A1. This tape consists of a non-woven fabric layer and a foam layer, and it comprises particles of a swelling powder anchored in the region of the non-woven layer.

U.S. Pat. No. 4,649,164 describes foamed water-absorbing materials formed of CO.sub.2 -releasing blowing agents and acrylate-(meth)acrylic acid latices; here the foamed latex itself represents the absorbent material. Owing to the hydrophobic nature of the acrylate component, the absorption capacity of these foams--as compared to the known superabsorbers--is limited.

Biocompatible, open-cell polyurethane foams that can be used as wound dressing and which have guar gum as incorporated hydrogel are also known from DE 42 42 015 A1. The gel component is foamed in situ during the production. The water absorption capacity of these products is to be limited to a value below the triple of the initial weight.

EP 0 340 945 A1 describes mixtures of elastomers and water-swellable hydrocolloids, which are cationic and preferably chitosan salts, for the use as wound dressings having absorption values of at least 180%-wt.; the colloidal particles are randomly integrated in the elastomer, and the absorption capacity for aqueous liquids is also limited.

Similar hydrophilic polyurethane foam gels are known from DE 42 33 289 A1; these are produced from mixtures of polyols, diisocyanates and superabsorbent polymers, the superabsorbent polymer being evenly incorporated in the foam owing to the production-specific mixing of the components. The products are used as wound dressings having a defined adherence.

Additionally, U.S. Pat. No. 5,149,339 describes absorbent constructions comprising superabsorbent powdery polymers in fiber-containing, adjacent, cellular structures of these constructions; however, the polymer is present therein in a dense and unfixed packing configuration.

Accordingly, there was the object to provide a body that is based on layered absorbent materials for water and aqueous liquids, and which avoids the above-mentioned disadvantages.

This object could be achieved by a layered body of at least one open-cell layer of plastic and/or latex foam and at least one layer formed of a particulate, superabsorbent polymer, wherein the layered body comprises the amount of superabsorbent polymer in a defined distribution and fixed at the boundary surface of the foam layer.

Accordingly, the subject matter of the present invention is a layered body consisting of one or several plastic foam layers and/or latex foam layers and particulate, superabsorbent polymers for the absorption of water and aqueous liquids, which is characterized in that the superabsorbent polymer is comprised directly on, between, or below the foamed plastic and/or foamed latex layers in a quantitatively and/or locally predetermined and fixed areal configuration, and that the quantity ratio of foamed plastic and/or foamed latex layer to the superabsorbent polymer amounts to 1:500 to 50:1, preferably 1:50 to 25:1, and most preferably 1:5 to 10:1. The layered absorbent body may be rigid or flexible.

Most surprisingly, the swelling capacity of the polymer remains unaffected during the absorption using the layered body according to the present invention, although the plastic material or the latex and the polymer are in direct contact; for this reason, the polymer's absorption capacity for aqueous liquids is also maintained in the chosen configuration.

When a 0.9% NaCl-solution is used, the layered absorbent body according to the present invention preferably has a retention of at least 0.1 liter/m.sup.2 surface, a maximum absorption of at least 0.1 liter/m.sup.2 surface, and an absorption under load (AUL) of at least 2 g/g at 0.021 Pa.

Another subject matter of the present invention is a manufacturing process and the use of the layered absorbent bodies according to the present invention. The process for the production is characterized in that at least 1,000 g/l is formed and the preferably open-cell foam is spread out over the surface at a layer thickness of 1 .mu.m to 100,000 .mu.m, preferably of 10 .mu.m to 10,000 .mu.m, and most preferably of 200 .mu.m to 5,000 .mu.m, foam at a quantity ratio of foamed plastic and/or foamed latex layer to the superabsorbent polymer of 1:500 to 50:1, preferably 1:50 to 25:1, and most preferably 1:5 to 10:1, optionally by using at least one stencil, perforated disk, and/or sieve, at a quantitatively and superficially defined distribution, is optionally fixed by a heat treatment, wherein process step a) and/or b) is optionally repeated in desired succession, and that finally a heat treatment under cross-linkage of the foamed layers is carried out.

The production of the absorbent body according to the present invention is effected by using known raw materials. A suitable basis for the plastic or latex foam layer are commercial plastic materials and/or latex dispersions for rigid, semirigid, flexible, and nonrigid plastic foams of polystyrene, styrene copolymers, rigid and flexible PVC, polycarbonates, polycarboimides, polymethacrylimides, polyamides, polystyrene-butadiene-polymers, as well as of phenolic and urea resins; preferably copolymers which are formed of at least two monomers of (meth)acrylates, styrene, butadiene, vinyl acetate, and the vinyl acetates completely or partially saponified to the polymerized vinyl alcohol units.

The plastic foam and/or latex foam is formed by using known means, for example, by intense stirring or mixing under mixing with air, in general under the addition of foaming aids.

The kind and amount of the used plastic or latex material determines in known manner the mechanical properties of the bodies according to the present invention, e.g., the degree of flexibility and the surface behavior of the constructions.

It has been found that the properties may be influenced by mixing the plastic and latex materials. The absorption rate for water or aqueous liquids is determined to a large extent by the kind of the used plastic and/or latex material. In particular, it has surprisingly been found that mixing these components improves the absorption rate in certain cases to such an extent that it is above the value of absorbent substances formed of only one plastic or latex component.

Also, it is most surprising that the absorption speed is considerably influenced by the kind and amount as well as by the distribution of the additionally used filling materials.

Suitable fillers are chalks, bentonites; silica gels and silicic acid; activated carbons, pigments, such as titanium dioxide and iron oxide; as well as natural and/or synthetic fibrous materials, such as viscose and cotton fibers and fabrics, and/or polyester and polyamide fibers, and mixtures of different fibers or corresponding fabrics. Additionally suitable are finely ground plastics, in particular those of the same kind as the used plastic or latex material. The kind, concentration, and distribution of the filler may be the same or different in each foam layer. Mixtures of different fillers may also be used. The single foam layer may have a degree of filling ranging from 0 to 1,000%-wt., relative to the amount of plastic material or latex, preferably it amounts to a maximum of 400%-wt., and most preferably to a maximum of 200%-wt. Furthermore, the described fillers may also be introduced into the absorbent body as a separate layer. The superabsorbent polymer may also be applied in admixture with the materials mentioned as suitable fillers.

The plastic or latex dispersion may also be employed by using further additives, such as blowing or foaming agents, foam stabilizers, cross-linking or vulcanizing agents; the processing conditions for the production and stabilization of such foams are known.

The latex foam may be formed in different geometric forms, the formation of an open-cell foam layer having an arbitrary thickness being preferred. As described in U.S. Pat. No. 4,000,028, surfaces removable from auxiliary supports may temporarily be used for the production, for example, metallic strips and sheets, silicone paper, glass fibers, glass surfaces, or textile fabrics; according to the present invention it is preferred that surfaces of materials becoming a component of the absorbent body be used as a base, for example, plastic films and non-woven fabrics which are permeable and impermeable to liquids, cellulose or paper layers, or textile fabrics.

The basic layer may also consist of the unexpanded plastic or latex material; it is spread as a thickened dispersion and cured to form a homogeneous, liquid-impermeable layer. Unless other materials, such as fillers or the particulate polymer itself, are used for this purpose, the materials mentioned as suitable basis or a foam layer may serve to cover the last-applied layer.

According to the present invention, the particulate superabsorbent polymers may consist of water-insoluble, water-swellable polymers and copolymers of monomer units of (meth)acrylic acid, maleic acid, itaconic acid and their anhydrides and salts; fumaric acid and its salts, in particular its alkali, alkaline earth, and ammonium salts; (meth)acrylamide, (meth)acrylonitrile, and vinyl acetate and its hydrolysis products; vinylpryrrolidone, vinylpyridine, vinylsulfonic acid and its esters and amides; as well as of N-alkyl and N,N-dialkyl-substituted esters and/or amides of (meth)acrylic acid and their salts and/or their quaternary ammonium compounds. Also suitable are natural water-swellable polymers, such as carboxymethylcellulose, hydroxyethylcellulose, guar flour, xanthans, alginates, starch, and their derivatives, as well as graft polymers of these substances and of the mentioned monomers or mixtures of the above-mentioned polymers with these substances.

The particulate, superabsorbent polymer is applied on the previously manufactured surface of the plastic or latex foam layer in distributed form as a powder having a particle-size distribution ranging from 1 .mu.m to 20,000 .mu.m. This may done, for example, by sprinkling the powder from suitable containers or by means of suitable devices.

The particle size of the powders depends on the application of the absorbent bodies. In hygienics, it is preferred that powders having grain sizes ranging between 50 .mu.m and 1,000 .mu.m be used, whereas a range below 400 .mu.m is chosen when they are to be used in cable insulation.

The bodies according to the present invention comprise finest grain portions of the superabsorbent polymers in an only very small amount, with exactly these particles being fixed in the surface region of the foam layer. In handling the bodies according to the present invention, continued formation of finest polymer particles is avoided owing to mechanical processes.

According to a special embodiment, the amount and the powder distribution relative to the surface unit may be such that only certain surface regions of the foam layer are coated and/or that the surfaces are covered with differing amounts. To this end, application may be effected by using stencils, perforated disks, screens, or suitable combinations thereof, optionally under particle size classification of the polymers. For instance, the application of fine-grained powders may provide a liquid-blocking layer, or--in contrast to this--the application of coarse-grained polymer portions may achieve an improved distribution of the liquid.

The amount, particle size, and distribution of the particulate, superabsorbent polymer on the individual foamed plastic layers and/or foamed latex layers may be different.

The layer concentration of the plastic and/or latex foam surface is in the range of from 0.1 g to 500 g of the particulate, superabsorbent polymer, relative to one square meter of the foamed surface of the body, preferably in the range of 10 to 300 g/m.sup.2, and most preferably in the range of 50 to 200 g/m.sup.2.

The superabsorbent polymer portion in the total construction of the absorbent body amounts to 15-99%-wt., preferably 40-90%-wt., and most preferably 50-80%-wt.

The absorbent body material is manufactured by applying one or several plastic and/or latex foam layers alternating with applying the particulate superabsorber on the previously formed layer. To facilitate further processing, the plastic or latex foam layer may completely or partially be vulcanized under suitable known conditions, such as by single or multiple heating, for example in the IR-field or by treatment in the UV-field, after each application of the polymer; or the same may be done with the foam using other known measures. By means of differently applying the polymer particles on or into the individual layers, bodies are manufactured wherein the absorbent polymer is distributed with a certain gradient. Finally, a vulcanization is effected to completely cross-link the plastic or latex layers; this may be connected with additionally drying the body.

Optionally, the body according to the present invention may finally be processed with a calendar and/or an embossing roll.

A preferred example of the absorbent body according to the present invention is shown in FIG. 1.

The bodies according to the present invention can be used for the absorption of water and various kinds of aqueous liquids. In particular, they are used directly, or as a component of or additive in articles used in the hygienic and personal field, e.g., in diapers, tampons, and incontinence articles, and in sanitary articles for wound dressing. Additionally, the absorbent bodies are suitable as plant growth medium storing water and aqueous solutions; for the storage and transport of plants and parts of plants; for the insulation of pipes and ducts, in particular for electric and light transmitting cables; and as component of constructional elements, e.g., for the insulation of outer walls; and as packaging material or packaging component for commercial goods, in particular for foodstuffs and beverages. In addition, they may be incorporated into articles of clothing to improve the wearing property.

The properties of the bodies according to the present invention which absorb water and aqueous liquids may be determined by means of the following test methods.

Test methods:

A. Tea bag test (TBT)

To determine the absorption capacity, the TBT was carried out. A 0.9% NaCl-solution was used as test solution (unless stated otherwise).

In accordance with the superabsorbent polymer layer given by production, a piece of material was punched out of the absorbent body, it comprises 0.2 g of the superabsorbent polymer (SAP). The piece is weighed into a tea bag. Subsequently, the tea bag is placed into the test solution for 10 minutes. After dripping for 5 minutes, the tea bag was weighed and then centrifuged in a centrifuge (commercial spin dryer, 1,400 rpm). Then weighing was effected again.

The liquid absorption is expressed either in terms of 1 g of the body, 1 g of SAP used, or in terms of 1 m.sup.2 of the body.

B. Absorption under Load (AUL)

To determine the liquid absorption capacity under load, the "absorption under load" (AUL)--as described in EP-A-0 339 461--was determined. Deviating from this instruction, a circular piece of the superabsorbent body having the size of the inner diameter of the AUL-crucible was used as test substance. The liquid absorption is expressed either in terms of 1 g of the body, 1 g of the SAP used, or in terms of 1 m.sup.2 of the body surface.

C. Demand-Absorbency-Test

To determine another application technological property, the absorption of model urine is carried out according to the "Demand Absorbency Test" (DAT) (W. F. Schlauch, lecture index 1978, Amsterdam, DE 39 17 646) and the absorption rate determined. The measuring device consists of a burette filled with the model urine solution (2.0% urea, 0.9% NaCl, 0.1% MgSO.sub.4, and 0.06% CaCl.sub.2, dissolved in dist. water) and a test desk provided with an outlet for the model urine solution, which is connected to the measuring burette. On the test desk, a piece of the body according to the present invention comprising 1 g of the SAP is placed in the center of the liquid outlet. Then the model urine solution is brought into contact with the test substance by slight pressure on the connection hose. The liquid absorption, read at the burette, is noted after each minute. Once 50 ml of the test solution have been absorbed, the required time is noted.

A second test (DATP) is carried out in the same manner; however, the test piece is loaded with a pressure (0.3 psi). The values are read off and noted down in the same manner.

D. Inclined-Plane-Test

The "inclined-plane-test" to determine the absorption properties of the bodies according to the present invention is conducted following the test method specified in EP 0 546 587 A1.

A piece of the absorbent body according to the present invention, 10 cm.times.30 cm in size, is attached to an inclined plane (angle of inclination: 45.degree.) in the longitudinal direction. At a flow rate of 4 ml/sec., 100 ml of a 0.9% NaCl-solution are placed in the middle of the upper edge of the test body by means of a drop funnel, The liquid flowing over the surface of the test body is immediately collected in a catch-pot 1 and measured. The total amount of liquid flown from the surface of the collector 1 and out of the test body into the collector 2 is determined after 10 min. This procedure is repeated until the absorption capacity of the test body is exhausted--in general after the 4th or 5th application of liquid.

The test result is expressed as follows: (OA), (ZA),

and 1 and 2 (AV).

The present invention will be illustrated in greater detail by means of the following Examples.

The products used for the production of the plastic and/or latex foam layers are referred to in the following only by their commercial names and are characterized according to their chemical composition:

Estekoll.RTM. HL 40 acrylic ester

Estekoll.RTM. 60 vinyl copolymer

Estekoll.RTM. SU 390 acrylic-acid ester copolymer

Fixamin.RTM. PU 603 polyurethane/polyester (without free isocyanate groups)

Fixamin.RTM. PU 421 polyurethane (aliphatic)

Fixamin.RTM. PUK polyester polyurethane

Fixamin.RTM. PU 555 polyester polyurethane (without free isocyanate groups)

Sarpifan.RTM. CAW vinyl copolymer (plasticized)

Sarpifan.RTM. DFP vinyl copolymer (plasticized)

Sarpifan.RTM. BKF polyvinyl acetate (unplasticized)

Sarpifan.RTM. HP 79 vinyl copolymer (unplasticized)

Sarpifan.RTM. NL nitrile-rubber latex

Sarpifan.RTM. U 75 acrylic acid copolymer

Sarpifan.RTM. VT acrylic-acid ester copolymer

Sarpifan.RTM. VB acrylic ester

Sarpifan.RTM. WRG acrylic ester

Sarpifan.RTM. VBA butadiene copolymer

Stokal.RTM.STD ammonium stearate

Mirox.RTM.TA potassium polyacrylate

Lavoral.RTM.LO fatty alcohol sulfate

Favor.RTM.SAB 922 FAF loosely cross-linked, partially neutralized polyacrylate

Favor.RTM.SAB 990 loosely cross-linked, partially neutralized polyacrylate

Favor.RTM.922 SK loosely cross-linked, partially neutralized polyacrylate

Plantaren.RTM.2000 CS/UP alkyl polyglycoside

Favor.RTM.SXM 75 loosely cross-linked, partially neutralized polyacrylate

Favor.RTM.SXM 100 loosely cross-linked, partially neutralized polyacrylate

Bunatex.RTM.SL 3510 styrene/butadiene copolymer

Bunatex.RTM.SL 2810 styrene/butadiene copolymer

Acronal.RTM.DS 2331 X copolymer based on ethyl acrylate

Kaolin.RTM.W chalk mineral

Neogel.RTM.V 70 ZB vulcanizing paste based on sulfur

Neogel.RTM.V 77 ZB vulcanizing paste based on sulfur

Calcicoll.RTM.W 12 partially crystalline chalk

Fixapet.RTM.VNF nitrogen-containing, formaldehyde-free cross-linking agent

Vinipas.RTM.LL 778/5 ethylene/vinyl acetate copolymer

Lipolan.RTM.VD 9910 butadiene/styrene copolymer

Litex.RTM.AP 4120 butyl acrylate/styrene copolymer

80 parts of Fixamin.RTM.PUK, 3 parts of Stokal.RTM.STD, 5 parts of Mirox.RTM.TA, 11 parts of deionized water, and 1 part of Lavoral.RTM.LO were mixed and foamed with a hand mixer to a foam weight per liter of 250 g/l.

The foam was knife coated onto a gray cotton cloth (layer thickness: 1.5 mm), then an extreme excess of 500 g/m.sup.2 of the superabsorbent polymer (SAP) was sprinkled thereon. Heating to 100.degree. C. in the drying oven for 6 min. followed, subsequently the samples were calendered and the nonadhering SAP was thrown off. Again, heating of the samples to 170.degree. C. for 5 min. Tea bag test SAP            (max.)  (ret.) [kind]         [l/m.sup.2 ] [l/m.sup.2 ] ______________________________________ Example 1 Favor .RTM. SAB 922 FAF 1.9     1.4 Example 2 Favor .RTM. SAB 990 6.8     4.9 Exampie 3 Favor .RTM. 922 SK 9.6     8.2 Example 4 carboxymethylcellulose 3.8     1.5 (acc. to Ex. 2 No. 50 in EP 053 8904 A2) ______________________________________

Procedure as in Examples 1-4, except that the foam was mixed with the SAP, and the mass so obtained was spread on gray cotton cloth (thickness about 3 mm). Afterwards the procedure corresponded to Examples 1-4.

None of the examined samples showed an absorption (TBT) of more than 0.2 l/m.sup.2.

20 g Caradol 48-2 (polyol of Shell), 0.2 g Tedostab (polysiloxane of Goldschmidt), 0.08 g dibutylin dilaurate, and 0.08 g N,N-dimethylaminoethanol are mixed. Favor SXM 100 is added to this mixture. Then, a mixture of 1 g of water and 10 g of toluylene diisocyanate is added under stirring. The mixture is poured on a polyethylene film. After 2 hours, the polyurethane foam is cured. The white, moderately flexible structure has a thickness of about 5 mm. TBT (ret.)* Favor SXM 100 (30 sec)  (30 min) Comparative Example (g)         (g/g)     (g/g) ______________________________________ 5             15.68       4.5       12.0 6             7.84        3.1       9.70 ______________________________________ *The measured values relate to the suberabsorber used.

A foam was prepared as in Examples 1-4. This foam was applied on a gray cotton cloth at a layer thickness of 1.5 mm. Then a screen was placed on the foam. The free foam squares were sprinkled with Favor.RTM.SAB 990 (surface concentration 150 g/m.sup.2, relative to the total surface). Subsequently, the screen was removed and a cover layer of 1 mm of the described latex foam was applied. The foam was then treated as in Examples 1-4. TST* (max.): 6.5 l/m.sup.2 TBT* (ret.): 5.0 l/m.sup.2. of the resulting bags was cut out of the manufactured body. This bag was then used for measuring the absorption values without enclosing it into a tea bag.

The procedure of Example 5 is repeated; however, a cross-linked guar flour is used instead of Favor SAP 990. The polymer foam is cross-linked at 120.degree. C. for 30/60 mins. (Example 6/7). The absorption values were determined in dependence on the dipping time: Tea bag test Dipping time max.     ret. [min.]      [g/g SAP] [g/g SAP] ______________________________________ Example 6 1             5.9      7.3 10            15.0     14.9 60            15.7     16.3 240           16.7     17.3 Example 7 1             7.3      9.0 10            13.2     11.1 30            14.6     11.8 60            14.6     13.5 240           15.9     15.2 ______________________________________

In the manner described, a foam is prepared using 0.8 g of Plantaren.RTM.2000 CS/UP, 1 g of Stokal.RTM.SR, 0.2 g of guar flour 104, 3 g of Fixamin.RTM.PUK, 15 g of Sarpifan.RTM.VBA, and 10 g of deionized water. The foam is expanded to a total volume of 400 ml and evenly distributed over a surface of 0.1 m.sup.2. Subsequently, 30 g of a SAP is evenly distributed on this area. The mass so obtained is oven-dried at 160.degree. C. for 5 minutes. Then, the same foam layer is applied on this mass, sprinkled again with the same amount of SAP, and dried again at 160.degree. C. for 5 minutes. This procedure is repeated for two more times in Examples 8 and 9. Subsequently, a last foam layer is applied, and the obtained body is heated at 160.degree. C. in the drying oven for 5 minutes without any additional sprinkling. TBT SAP          (max.)  (ret.) (kind)       [l/m.sup.2 ] [l/m.sup.2 ] ______________________________________ Example 8 Favor .RTM. SXM 75 53      36 Example 9 Favor .RTM. 922 FAF 59      46 Example 10* Favor .RTM. 922 FAF 31      22 ______________________________________ *40 g/m.sup.2 of polyamide fiber (NC 0261) is additionally incorporated into each absorbent layer.

0.8 g of Plantaren.RTM.2000 CS/UP, 0.4 g of Stokal.RTM.SR, 8 g of deionized water, and 13.8 g of Fixamin.RTM.PU 421 are expanded (foam weight per liter about 300 g/l), distributed an a metal plate having a size of 460 cm.sup.2, and heated to 160.degree. C. for 10 minutes. Subsequently, a foam of 0.4 g of Plantaren.RTM.2000 CS/UP, 0.4 g of Stokal.RTM.SR, 6 g of deionized water, and 4.9 g of Estekoll.RTM.SU 390 is prepared (foam weight per liter as before) and applied on the existing foam layer. This foam layer is sprinkled with 13.8 g of Favor.RTM.SXM 75 and then heated under the above-mentioned conditions. Subsequently, another layer of the second foam is applied, sprinkled again with the same amount of the same SAP, and subjected to a thermal aftertreatment. The same foam layer is applied once more; however, this is not sprinkled with SAP. After having been heated again to 160.degree. C. (10 minutes, the resultant body is provided with a cover layer of the above-mentioned formulation and heated again. Then the soft and flexible body thus obtained is removed from the metal surface.

TBT (max./ret.): 25/16.6 [l/m.sup.2 ]

A foam having a volume of about 0.8 l is expanded using 2 g of Plantaren.RTM.2000 CS/UP, 2 g of Stokal.RTM.SR, 5 g of Fixamin.RTM.PUK, 26 g of Sarpifan.RTM.VBA, 5 g of Estekoll.RTM.60, and 20 g of deionized water.

The foam is divided in 2 halves. The first half is spread out over a plate on an area of 0.1 m.sup.2 ; subsequently, the SAP Favor.RTM.SXM 75 is evenly sprinkled on this area in a defined amount which is listed in the following Table. This mass is then dried at 160.degree. C. for 5 minutes, covered with the second half of the expanded foam, and dried again under the same conditions. The substance so obtained is removed from the plate and examined with respect to its absorption capacity. Tea bag test (10') Amount of sprinkled SAP (max.)  (ret.) Example  [g/m.sup.2 ]      [l/m.sup.2 ] [l/m.sup.2 ] ______________________________________ 12       150               10.2    6.1 13       200               11.6    7.3 14       250               14.7    9.9 15       300               16.0    10.5 16       400               18.2    11.4 ______________________________________

1 g of Plantaren.RTM.2000 CS/UP, 1 g of Stokal.RTM.SR, 12 g of Sarpifan.RTM.VBA, 6 g of Fixamin.RTM.PUK, and 10 g of deionized water are expanded as described above and spread out over a plate on an area of 0.1 m.sup.2 (base layer). The mass is sprinkled with a mixture of 30 g of Favor.RTM. SAB 990, and 0.3 g of polyamide fiber and then dried at 150.degree. C. for 5 minutes. Subsequently, a foam of 0.8 g of Plantaren.RTM.2000 CS/PU, 0.8 g of Stokal.RTM. SR, 6.7 g of Sarpifan.RTM.VBA, 3.1 g of Estekoll.RTM. SU 390, and 10 g of deionized water, expanded to about 400 ml, is spread out. This layer is also sprinkled with the above amounts of Favor.RTM. SAB 990 and polyamide fiber and dried at 150.degree. C. for 5 minutes. Two more of the same layers are applied. Then this body is provided with a cover layer which corresponds to the base layer.

In another test (Example 18) the above test was repeated, except that 1.5 g of Fixamin.RTM.PUK and 16.5 g of Sarpifan.RTM.VBA were used for the cover layer and base layer.

The absorption values after one and 10 minutes and the AUL-value were determined in these Examples. The values were based on the amount of SAP used. TBT (1 minute) TBT (10 minutes) (max.)     (ret.) (max.)  (ret.) AUL Example [g/g]      [g/g]  [g/g]   [g/g] [g/g] ______________________________________ 17     20.4       18.9   41.8    28.0  24.4 18     19.8       18.2   44.0    28.8  25.6 ______________________________________

Examples 17 and 18 were repeated without the addition of an SAP. The obtained absorption values were expressed in terms of 1 g of the body. TBT (10 minutes) (max.)      (ret.)  AUL Comparative Example [g/g]       [g/g]   [g/g] ______________________________________ 5             1.2         0.5     1.3 6             7.3         0.7     4.0 ______________________________________

Another dispersion (see Table) is added to a mixture of 0.8 g of Plantaren.RTM.2000 CS/UP, 0.8 g of Stokal.RTM. SR, 9.4 g of Sarpifan.RTM.VBA, and 10 g of water. A foam is prepared thereof and spread on 0.1 m.sup.2, sprinkled with 20 g of Favor.RTM.SXM 75, and subsequently dried at 150.degree. C. for 5 minutes. The same foam layer as above is spread on the body thus obtained; subsequently, 10 g of the mentioned SAP are sprinkled and dried as described above. Two more foam layers having the above-mentioned formulation are then applied on this mass; the last one is covered with a paper web (Kleenex). Dispersion    DAT      DAT (max.) DATP DATP (max.) Example TBT      [Amount] [1 min.] [Amount] [Time] [1 min.] [Amount] [Time] [max.] [ret.] [No.] [Kind]   [g]  [g/g] [g/g] [sec.] [g/g] [g/g] [sec.] [g/g] [g/g] __________________________________________________________________________ 19   Estekoll .RTM. 60 3.35 14.0 29.5 455 3.3 22.7 1285 18.5 10.2 20   Estekoll .RTM. HL40 3.66 14.2 30.0 505 5.6 22.6 1155 17.8 10.3 21   Fixamin .RTM. PU 421 4.67 11.9 22.0 475 3.8 22.1 1520 14.8 10.1 22   Fixamin .RTM. PUK 4.02 13.1 27.0 590 3.1 22.2 1390 15.2 10.0 23   Fixamin .RTM. PU 555 6.70 12.0 25.0 505 6.2 23.6 815 14.5 9.9 24   Sarpifan .RTM. BKF 4.02 13.9 26.3 540 2.3 21.5 1950 15.7 10.1 25   Sarpifan .RTM. CAW 4.02 14.2 28.3 465 3.4 20.1 1315 16.0 10.3 26   Sarpifan .RTM. DFP 3.35 12.8 26.7 600 2.9 24.5 1480 17.5 10.2 27   Sarpifan .RTM. HP79 3.87 13.7 27.1 540 3.7 28.1 1240 18.4 10.2 28   Sarpifan .RTM. MKD 4.02 13.1 27.7 620 4.5 27.0 990 16.4 10.0 29   Sarpifan .RTM. NL 4.47 13.9 25.2 550 2.9 24.1 1325 17.5 9.8 30   Sarpifan .RTM. U 75 4.02 16.4 29.5 570 5.0 21.8 1225 17.2 10.6 31   Sarpifan .RTM. VT 4.47 9.0 21.5 635 3.8 20.2 1490 15.8 10.0 32   Sarpifan .RTM. WRG 4.47 13.7 30.4 670 3.0 28.0 1280 16.0 9.8 __________________________________________________________________________

50 g of a latex dispersion, 3 g of Mirox.RTM.TA, and 5 g of deionized water are made into a paste. Half of this paste is spread out over an area of 1000 cm.sup.2 and dried at 160.degree. C. for 1 minute in the circulating air drier. Then, the second half of the paste is spread out over the resultant film, and 20 g of Favor.RTM.SXM 100 are sprinkled thereon. This body is heated to 160.degree. C. for 1 minute.

A foam of 30 g of the same latex dispersion, 3 g of Plantaren.RTM.2000 CS/UP, and 10 g of water are expanded in the known manner to a foam weight per liter of about 250 g/l. This mass is evenly distributed on the produced body and immediately heated for 1 minute in the IR-field (10 kW/m.sup.2). Heating to 150.degree. C. for 5 minutes in the drying oven follows.

The absorption rate for synthetic urine is determined by means of DAT and DATP using 100 cm.sup.2 pieces each times. In this case it is necessary that the foam layer lies on the liquid outlet since the base layer manufactured with the paste is impermeable to liquid. DAT     DATP Example Dispersion     [1']   [5'] [1'] [5'] [10'] [No.]  [kind]         [g]    [g]  [g]  [g]  [g] ______________________________________ 33     Bunatex .RTM. SL 3510 23.2   46.1 9.8  30.5 41.6 34     Bunatex .RTM. SL 2810 20.2   42.2 6.2  19.7 31.8 35     Sarpifan .RTM. WRG 16.8   42.5 2.2  2.2  2.2 36     Acronal .RTM. DS 2331 X 16.8   38.6 7.6  21.8 31.6 37     Sarpifan .RTM. NL 17.7   45.5 6.0  25.1 34.5 ______________________________________

A foam is prepared (foam weight per liter=350 g/cm.sup.2) from a foam of 0.3 g of Plantaren.RTM.2000 CS/UP, 0.6 g of Bunatex.RTM.SL 3510, 0.6 g of VP-Non-Gel, and 3.0 g of deionized water and spread on an area of 300 cm.sup.2. The foam is sprinkled with 3 g of Favor.RTM.SXM 100, treated in the IR-field for 1 minute, and then heated in the drying oven for a certain time at a defined temperature. Then, a cover layer of the same foam is applied and the aftertreatment repeated.

50 cm.sup.2 pieces of these bodies are each examined in the DAT with respect to their absorption rate. To this end, the absorption after one, two, three, and four minutes, and the time required to absorb 50 ml of the synth. urine solution are noted. Temperature/ DAT Example Time      [1']   [2']  [3'] [4'] [50 g reached] [No.]  [.degree.C.]/[min.] [g]    [g]   [g]  [g]  [sec.] ______________________________________ 38     100/12    11.5   26.8  39.2 47.3 270 39     120/10    17.6   32.4  42.5 45.1 250 40     140/8     23.4   46.0  50.0 50.0 140 41     160/6     21.7   41.8  50.0 50.0 165 42     180/4     22.5   42.8  50.0 50.0 150 ______________________________________

Bodies are prepared according to the same method as in the preceding Examples; however, differing amounts of VP-Non-Gel are added to the foams. All foams are heated to 140.degree. C. for 8 minutes. The bodies are tested as in Examples 38-42. DAT Example VP-Non-Gel [1']   [2'] [3'] [4'] [50 g reached] [No.]  [g/foam layer] [g]    [g]  [g]  [g]  [sec.] ______________________________________ 43     0          22.9   31.7 37.2 42.2 350 44     0.6        20.4   39.2 44.4 48.0 290 45     1.2        24.3   42.5 50.0 50.0 165 46     2.4        7.8    17.7 29.5 38.8 345 ______________________________________

Example 45 is repeated; however, differing amounts of titanium dioxide (Rutil-type) are incorporated as filler into each foam layer. DAT Example Titanium dioxide [1']   [2']  [3'] [50 g reached] [No.]   [g]         [g]    [g]   [g]  [sec.] ______________________________________ 47      0.6         18.1   37.0  50.0 155 48      1.2         22.1   43.6  50.0 135 49      2.4         22.6   43.7  50.0 145 50      4.8         12.8   25.1  38.8 220 ______________________________________

The preceding Examples are repeated, except that 2.4 g of differing fillers are incorporated into the foams. DAT Example Filler     [1']   [2'] [3'] [4'] [50 g reached] [No.]  [kind]     [g]    [g]  [g]  [g]  [sec.] ______________________________________ 51     bentonite  16.0   32.3 50.0 50.0 170 52     chalk      22.2   45.2 50.0 50.0 130 53     Kaolin .RTM. W 1.5    2.9  4.3  7.0  -- 54     talc       21.5   40.9 50.0 50.0 145 ______________________________________

Experiment 52 is repeated using 4.8 and 10 g of chalk as filler. In the DAT, the test pieces have an absorption of 50 ml after 120 and 105 seconds, respectively.

Experiment 52 is repeated; except that the amount of Favor.RTM. SXM 100 is increased to 300 g/m.sup.2 ; in addition, the concentration of the chalk in the foam is further increased. Test pieces of 33.3 cm.sup.2 are tested in the DATP. The liquid amount absorbed after fixed periods, and the time until 50 ml of test urine solution are absorbed served as test criteria. Exam-          DATP ple   Chalk    [1']   [2'] [3'] [4'] [5'] [50 ml reached] [No.] [g/fo.lay.] [g]    [g]  [g]  [g]  [g]  [sec.] ______________________________________ 57    9.6      16.5   28.3 35.5 41.0 44.9 350 58    14.5     23.6   38.7 47.4 50.0 50.0 290 59    19.3     15.5   27.1 35.5 41.2 45.5 165 ______________________________________

20 g of Estekoll.RTM. HL 40 are spread on a 500 cm.sup.2 piece of polyethylene film (1.8 g); this layer is evenly sprinkled with 15 g of Favor.RTM. SXM 100. This mass is dried at 100.degree. C. for 10 minutes. Subsequently, a foam of 0.5 g of Plantaren.RTM.2000 CS/UP, 10 g of Bunatex.RTM.SL 3510, 2 g of VP-Non-Gel, and 5 g of deionized water is prepared (weight of foam per liter about 250 g/l); 8.05 g of chalk are additionally incorporated into this foam.

The mass from the drying oven is evenly spread with this foam; this body is then aftertreated for 1 minute in the IR-field first and then 10 minutes at 100.degree. C. in the drying oven.

In the DAT, a piece of this body having an area of 33.3 cm.sup.2 has an absorption of 50 ml synth. urine after 9 minutes. The applied polyethylene film is impermeable to liquids, i.e., the DAT-test is conducted such that the foam layer is in contact with the liquid.

Procedure as in Example 60; however, a mixture of 10 g of Estekoll.RTM. HL 40, 10 g of water, and 2.5 g of Mirox.RTM. TA is applied on the polyethylene film as base layer. In addition, another foam layer having the same formulation is applied.

In the DAT, a 33.3 cm.sup.2 piece of this body has an absorption of 50 ml synth. urine solution after 4.25 minutes.

Example 58 was repeated; however, Neogel.RTM. V 70 ZB and Neogel.RTM. V 77 ZB, respectively, were used instead of the Non-Gel-Paste. In case of Neogel.RTM.V 70 ZB, the test substance had an absorption of 50 ml synth. urine (DAT) after 230 seconds, and in case of Neogel.RTM. V 77 ZB after 200 seconds.

1.7 g of Plantaren.RTM.2000 CS/UP, 5.21 g of Neogel.RTM.V 70 ZB, 13.02 g of deionized water are mixed with a polymer dispersion and expanded to about 300 g/l. Subsequently, a filler is optionally mixed into the foam. Then this is spread out over an area of 1302 cm.sup.2 and sprinkled with 39.06 g of Favor.RTM.SXM 100. The mass is then heated for 4 minutes at 180.degree. C. in the drying oven, spread another time with the same foam layer, and again dried at 180.degree. C. for 4 minutes. Pieces having a size of 10.times.30 cm are cut out of the resultant body; the surface test is conducted with these pieces. Example Dispersion/Amount Filler/Amount ______________________________________ 64      Bunatex .RTM. SL 3510/26.04 g --/-- 65      Sarpifan .RTM. MKD/35.41 g --/-- 66      Bunatex .RTM. SL 3510/26.04 g chalk/82.39 g 67      Bunatex .RTM. SL 3510/26.94 g Calcicoll .RTM. W12/82.39 g 68      Sarpifan .RTM. MKD/35.41 g chalk/82.39 g 69      Bunatex .RTM. SL 3510/26.04 g chalk/41.2 g 70      Bunatex .RTM. SL 3510/26.04 g Calcicoll .RTM. W 12/41.2 g 71      Sarpifan .RTM. MKD/35.41 g chalk/41.2 g ______________________________________ 1           2        3        4        5 OA ZA AV OA ZA AV OA ZA AV OA ZA AV OA ZA AV Ex. [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] __________________________________________________________________________ 64 0.5 0  43 0  20 21 0  25 21 0  25 32 0  20 55 65 0  20 10 0  25 2  -- -- -- -- -- -- -- -- -- 66 0  15 23 0  45 5  0  40 15 0  40 29 0  30 63 67 0  40 3  0  -- 0  0  -- 0  0  30 0.5 -- -- -- 68 14 -- 14 0  -- 0  0  -- 0  0  300 5  -- -- -- 69 1  0  32 0  20 15 0  35 20 0  40 35 0  30 52 70 0.5 0  33 0  30 18 0  30 25 0  40 32 0  35 55 71 0  15 14 0  -- 0  0  -- 0  0  60 25 -- -- -- __________________________________________________________________________

0.48 g of Plantaren.RTM.2000 CS/UP, 0.17 g of magnesium chloride (x 6 H.sub.2 O), 2.38 g of deionized water are expanded with 6.48 g of Sarpifan.RTM.MKD, 0.33 g Fixapet.RTM.VNF, and chalk to about 300 g/l (calculated without chalk). This foam is spread on a surface of 14.times.34 cm and sprinkled with 4.5 g of Favor.RTM.SXM 100 on an area of 10.times.30 cm. The mass is then heated for 3 minutes at 180.degree. C. in the drying oven, covered another time with the same foam layer, sprinkled once again with the same amount of Favor.RTM.SXM 100, and dried again at 180.degree. C. for 3 minutes. A cover layer of the same foam material is spread thereon and oven-dried for the third time at 180.degree. C. (cf. FIG. 1).

Subsequently, the samples are calendered. 1- 2- 3- 4- Chalk OA ZA AV OA ZA AV OA ZA AV OA ZA AV Ex. [g] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] __________________________________________________________________________ 72 5.71 0  -- 0  0  30 0.1 0  30 18 0  20 62 73 3.81 0  -- 0  7.0 15 11 0  30 19 0  20 60 74 1.90 0  40 0.5 24 0  25 13 5 18 23 10 58 75 0.00 0  20 11 28 5  30 45 5 47 52 5 54 __________________________________________________________________________

0.50 g of Plantaren.RTM.2000 CS/UP, 0.09 g of magnesium chloride (x 6 H.sub.2 O), 2.4 g deionized water are expanded with 3.2 g of Sarpifan.RTM.MKD, 0.17 g of Fixapet.RTM.VNF, and 5.44 g of chalk, and under the addition of a certain amount of a second polymer dispersion to about 300 g/l (calculated without chalk. Then this foam is spread on a surface of 14.times.34 cm and sprinkled with 4.5 g of Favor.RTM.SXM 100 on an area of 10.times.30 cm. This mass is then heated for 3 minutes at 180.degree. C. in the drying oven, spread another time with the same foam layer, sprinkled once again with the same amount of Favor.RTM.SXM 100, and dried once more at 180.degree. C. for 3 minutes. A cover layer of the same foam material is spread thereon and oven-dried for the third time at 180.degree. C. Then the samples are calendered (unless stated otherwise). Example No. Remarks  Polymer dispersion Initial weight ______________________________________ 76       Fixamin .RTM. PUK 3.20 g 77       Sarpifan .RTM. BKF 3.20 g     unstable 78       Sarpifan .RTM. CAW 3.20 g 79       Sarpifan .RTM. DFP 2.67 g 80       Sarpifan .RTM. HP79 3.08 g 81       Sarpifan .RTM. NL 3.56 g 82       Sarpifan .RTM. U 75 3.20 g 83       Sarpifan .RTM. VBA 3.20 g 84       Sarpifan .RTM. VT 3.56 g 85       Sarpifan .RTM. WRG 3.56 g 86       Estekoll .RTM. 60 2.67 g 87       Estekoll .RTM. HL 40 2.91 g 88       Bunatex .RTM. SL 2800 2.39 g 89       Bunatex .RTM. SL 3510 2.35 g 90       Acronal .RTM. DS 2331 X 3.59 g 91       Vinipas .RTM. LL 778/5 3.20 g 92       Lipolan .RTM. VD 9910 3.20 g     not calendered 93       Litex .RTM. AP 4120 3.20 g ______________________________________ 1- 2- 3- 4- 5- OA ZA AV OA ZA AV OA ZA AV OA ZA AV OA ZA AV Ex. [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] [ml] [s] [ml] __________________________________________________________________________ 76 0  100 2  3.0 5 5  0  45 16 0  30 60 0  30 77 77 -- -- -- -- -- -- -- -- -- -- -- -- -- -- -- 78 0  -- 0  0  -- 0  0  30 15 0  20 60 0  20 78 79 0  45 3  15 10 18 0  30 18 0  30 52 0  30 76 80 0  -- 0  0  15 8  0  25 18 0  30 52 0  30 75 81 0  -- 0  0  -- 0  0  120 4 0  45 47 0  45 76 82 0  -- 0   --* -- -- -- -- -- -- -- -- -- -- -- 83 0  -- 0  0  -- 0  0  70  9 0  30 55 0  30 80 84 10 15 23 34 0 37 28  0 35 20  0 45 16 15 67 85 0  -- 0  0  -- 0  0  60 10 0  30 58 0  30 77 86 0  -- 0  0  40 1  0  45 15 0  30 56 0  20 -- 87 0  35 1  14 5 17 0  30 20 0  20 60 -- -- -- 88 10 -- 10 3  15 7  0  30 13 0  20 -- -- -- -- 89 14 0  30 0  30 4  0  30 10 0  30 -- -- -- -- 90 0  30 18 6  10 12 0  30 14 -- -- -- -- -- -- 91 0  45 6  0  20 8  0  45 20 -- -- -- -- -- -- 92 0  10 65 0  20 36 0  30 32 -- -- -- -- -- -- 93 0  40 2  0  35 1  0  35 18 0  25 56 -- -- -- __________________________________________________________________________ *The experiments were terminated before the 5th run when the test body ha torn dring the experiment.

A foam having a weight per liter of 300 g/l is prepared from 8 g of Plantaren.RTM.2000 CS/UP, 8 g of Stokal.RTM.SR, x g of Sarpifan.RTM.VBA, 100 g of H.sub.2 O, and y g of Sarpifan.RTM.MKD. This is spread on an area of 1 m.sup.2, evenly sprinkled with 200 g of Favor.RTM.SXM 100, and then dried for 5 minutes at 160.degree. C. A same foam layer is applied on this structure, evenly sprinkled with 100 g of Favor.RTM.SXM 100, and then dried again at 160.degree. C. for 5 minutes.

Subsequently, the same foam layer is applied for two more times, followed by drying as above.

The absorption rate is determined after one minute in the DAT-test. Sarpifan .RTM. VBA Sarpifan .RTM. MKD DAT (1 minute) Example No. [g/foam layer] [g/foam layer] [g] ______________________________________ 94      114.1       20.1         9.3 95      94.0        40.2         13.1 96      67.1        67.1         12.3 ______________________________________

12.5 g of Plextol MV 604, 12.5 g of Plextol DV 440 (acrylate dispersions of Rohm GmbH), 1 g of Fixapret VNF, 0.1 g of magnesium chloride, 2 g of water, and 1 g of Glucosid 81 S (alkyl polyglycoside of Huls AG, Marl) are mixed.

The mixture is expanded to a foam weight per liter of 40 g/l by means of a hand mixer. Half of the resulting foam is spread on surfaces of 40 * 50 cm and sprinkled with 40 g Favor SXM 100. The resultant structure is covered with the second half of the foam. Subsequently, drying for 4 minutes at 200.degree. C. in circulating air drier follows. The resulting surface has a high flexibility.

TBT (ret.): 6.61(0.9% NaCl)/m.sup.2.

Example 97 is repeated; however, prior to foaming, 2 g of the alkyl glycoside and 7.5 g of water are added additionally. The foam weight per liter of the foam prepared with this mixture amounts to 30 g/l.

The resultant sheet material has a coarser pore structure than that of Example 97, the absorption capacity amounts also to 6.61 /m.sup.2.

## Claims

1. A process consisting of: thereof having a weight per liter of 50-1,000 g/l at a layer thickness of 1-100,000 .mu.m; amount such that the quantity ratio of foamed plastic, foamed latex or combination thereof layer to the superabsorbent polymer ranges from 1:500-50:1; and foamed layers, thereby preparing a layered body of at least one foamed plastic layer, foamed latex layer or combination thereof and a particulate, superabsorbent polymer which absorbs water or aqueous liquids.

2. The process of claim 1, wherein said foamed layer ranges in thickness from 10-10,000 .mu.m and the quantity ratio of latex layer to superabsorbent polymer ranges from 1:50-25:1.

3. The process of claim 2, wherein said foamed layer has a layer thickness of 200-5,000 .mu.m and the quantity ratio of foamed layer to superabsorbent polymer ranges from 1:5-10:1.

4. The process of claim 1, wherein said superabsorbent, particulate polymer is applied to said foamed layer through a stencil, perforated disk, sieve, in a quantitatively and superficially defined distribution on said foamed layer.

5. The process of claim 1, wherein, after performing steps (a) and (b), repeating (a) and/or (b) and then heat treating the composite material after each repeated step.

6. The process of claim 1, wherein the surface of step (a) is the surface of an auxiliary material selected from the group consisting of metal, glass, plastic, foil, silicone, paper or combinations thereof and said superabsorbent polymer has a particle size distribution ranging from 1-20,000 .mu.m.

7. A process of claim 1, wherein at least one cellulose, non-woven fabric, paper layer, textile non-woven material, fabric or combination thereof is applied to said layered body as a central layer, a base layer or cover layer of the layered body.

8. The process of claim 1, wherein when the layered body is comprised of several foamed plastic or latex layers necessitating accompanying layers of superabsorbent particulate polymer, the amount, particle size and distribution of the particulate superabsorbent polymer varies in each layer.

9. The process as claimed in claim 1, wherein prior to, during or after formation of the foamed plastic layer, the foamed latex layer or combination thereof, said layer is filled in an amount of 0-400 wt. % with a material selected from the group consisting of bentonites, silica gels, silicic acids, activated carbon, inorganic pigments, ground plastic materials, natural fibers, synthetic fibers and combinations thereof, relative to the weight of the foamed layer, optionally with at least one material selected from the group consisting of thickeners, cross-linking agents and stabilizers.

10. The process of claim 9, wherein the amount of material filled into the foamed layer ranges from 0-200 wt. %.

11. The process of claim 1, wherein said foamed layer is a combination of two or more plastic materials, latices or combination thereof in combination with at least one auxiliary agent selected from the group consisting of foaming agents, blowing agents, foam stabilizers, cross-linking agents and vulcanizing agents.

12. The process of claim 1, wherein said layered body is finally treated with a calendar, embossing roll or combination thereof.

13. A method of preparing a hygienic article, comprising: plastic or latex in at least one layer of particulate superabsorbent polymer fixedly attached to a surface of at least one of said foamed layers by depositing particulate superabsorbent polymer on a wet polymer containing layer which is foamed to form the foamed layer to which surface the superabsorbent polymer particles are fixedly attached, said superabsorbent polymer being employed in a predetermined amount to cover at least a portion of said surface in a predetermined areal configuration, the quantity ratio of the foamed layer to the superabsorbent layer ranging from 1:500-50:1, which imparts water or aqueous liquid absorptivity to the hygienic article, among the other layers of said hygienic article.

14. The method of claim 13, wherein said hygienic article is diapers or incontinence articles.

15. The method of claim 13, wherein said layered body is a component of articles of clothing.