# Patent

## Title
Curable silicone composition that provides a highly transparent cured silicone material

## Abstract

A curable silicone composition comprises (A) (A-1) a dialkylpolysiloxane that has at least two alkenyl groups in each molecule and a viscosity of at least 1,000 mPa·s to not more than 50,000 mPa·s and (A-2) an alkenyl-containing, resin-form organopolysiloxane that comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit wherein R1 is alkyl and R2 is alkenyl and that contains the alkenyl group in the range from at least 0.5 mass % to less than 3.5 mass %; (B) an organopolysiloxane that has at least three silicon-bonded hydrogen atoms; and (C) a hydrosilylation reaction catalyst. The curable composition provides a highly transparent cured silicone material that has a hardness in the range from at least 30 to not more than 80, a parallel light transmittance at 25° C. of at least 90%, and a parallel light transmittance at 200° C. that is at least 99% of the parallel light transmittance at 25° C.

## Background
RELATED APPLICATIONS
This application claims priority to and all the advantages of International Patent Application No. PCT/JP2010/051661, filed on Jan. 29, 2010, which claims priority to Japanese Patent Application No. JP 2009-022014, filed on Feb. 2, 2009.
TECHNICAL FIELD
The present invention relates to a curable silicone composition that provides a flexible and highly transparent cured silicone material. The present invention more particularly relates to a curable silicone composition that contains a resin-form organopolysiloxane and that provides a flexible and highly transparent cured silicone material that does not undergo temperature-induced changes in its transparency.
BACKGROUND ART
Curable silicone compositions that contain a resin-form organopolysiloxane and that provide a highly transparent cured silicone material are known. For example, JP 2005-042099 (Equivalent to US 2005-0006794 A1) A describes a silicone rubber composition comprising an organopolysiloxane that has at least two aliphatically unsaturated bonds in each molecule; an organopolysiloxane having a resin structure and comprising the SiO2 unit, an R3SiO0.5 unit having 2-3 vinyl groups, and an R3SiO0.5 unit having 0-1 vinyl group, wherein the non-vinyl R in these formulas is monovalent hydrocarbyl that does not contain an aliphatically unsaturated bond, e.g., methyl and so forth; an organohydrogenpolysiloxane that has at least two silicon-bonded hydrogen atoms in each molecule; and a platinum group metal-based catalyst. In the following, the SiO2 unit is referred to as the Q unit and the R3SiO0.5 unit is referred to as the M unit.
The polyorganosiloxane composition described in JP 2006-335857 A provides a transparent cured material and comprises a straight-chain polyorganosiloxane containing silicon-bonded alkenyl and having a viscosity at 23° C. of 10 to 10,000 mm2/s; a branched polyorganosiloxane comprising the Q unit, an M unit having one vinyl group, and an M unit that does not contain an aliphatically unsaturated bond; a polyalkylhydrogensiloxane comprising the Q unit, an M unit having one silicon-bonded hydrogen atom, and an M unit that does not contain silicon-bonded hydrogen; and a platinum group metal compound.
The curable silicone composition described in JP 2007-131694 A (equivalent to US2009-0118441 A1) comprises at least a diorganopolysiloxane that has at least two alkenyl groups in each molecule; at least two resin-form organopolysiloxanes that have different mass-average molecular weights, each comprising the Q unit, an M unit having one vinyl group, and an M unit that does not contain an aliphatically unsaturated bond; an organopolysiloxane that has at least two silicon-bonded hydrogen atoms in each molecule; and a hydrosilylation reaction catalyst.
JP 2006-328102 A (equivalent to US2006-0264583 A1) describes a silicone polymer composition for lens molding, that characteristically provides a colorless and transparent cured material and that comprises as its essential components an organopolysiloxane that has at least two aliphatically unsaturated bonds in each molecule and a viscosity of at least 100 mPa·s at 25° C., an organohydrogenpolysiloxane that has at least three H(CH3)2SiO1/2 units in each molecule, and a platinum group metal catalyst.
However, the cured silicone materials provided by the cure of such compositions are prone to breakage during mold-based molding and during component assembly processes, and it has also not been possible to use them in applications that demand bendability due to use in a flexed or bent condition. In addition, the cured silicone materials provided by the cure of these compositions are subject to temperature-induced changes in transparency, and problems due to optical property variations are then produced when these cured silicone materials are used over a broad temperature range.
PATENT REFERENCES


    Patent Reference 1: JP 2005-042099 A
    Patent Reference 2: JP 2006-335857 A
    Patent Reference 3: JP 2007-131694 A
    Patent Reference 4: JP 2006-328102 A


DISCLOSURE OF INVENTION
An object of the present invention is to provide a curable silicone composition that forms a flexible and highly transparent cured silicone material that does not undergo temperature-induced changes in its transparency.
The curable silicone composition of the present invention characteristically comprises

    (A) 100 mass parts of an alkenyl-containing organopolysiloxane comprising
    
        (A-1) a dialkylpolysiloxane that has an average of at least two alkenyl groups in each molecule and a viscosity at 25° C. of at least 1,000 mPa·s to not more than 50,000 mPa·s, at from 50 mass % to not more than 80 mass % of component (A), and
        (A-2) an alkenyl-containing, resin-form organopolysiloxane that comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit wherein R1 is C1-10 alkyl and R2 is alkenyl and that contains the alkenyl group in the range from at least 0.5 mass % to less than 3.5 mass %, at from 20 mass % to not more than 50 mass % of component (A);
    
    
    (B) an organopolysiloxane that has an average of at least three silicon-bonded hydrogen atoms in each molecule wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, in an amount that provides 0.8 to 2 moles silicon-bonded hydrogen in this component per 1 mole of the total alkenyl in component (A); and
    (C) a hydrosilylation reaction catalyst in a catalytic quantity,

and provides a highly transparent cured silicone material that characteristically has a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 30 to not more than 80, an elongation as specified in JIS K 6251 of at least 50%, a parallel light transmittance at 25° C. measured in accordance with JIS K 7105 on a 6 mm optical path length of at least 90%, and a parallel light transmittance value at 200° C. that is at least 99% of the parallel light transmittance at 25° C.



The aforementioned component (B) preferably is an organopolysiloxane comprising

    (B-1) an organopolysiloxane that contains at least 0.7 mass % silicon-bonded hydrogen and that comprises the SiO4/2 unit and HR32SiO1/2 unit wherein R3 is C1-10 alkyl, at 50 to 100 mass % of component (B), and
    (B-2) a straight-chain organopolysiloxane that contains at least 0.3 mass % silicon-bonded hydrogen wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, at 0 to 50 mass % of component (B).


The cured silicone material of the present invention is characteristically provided by the thermosetting of the aforementioned curable silicone composition and has a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 30 to not more than 80, an elongation as specified in JIS K 6251 of at least 50%, a parallel light transmittance at 25° C. measured in accordance with JIS K 7105 on a 6 mm optical path length of at least 90%, and a value for the parallel light transmittance at 200° C. that is at least 99% of the parallel light transmittance at 25° C.
The aforementioned cured silicone material preferably has a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 65 to not more than 75.
The cured silicone composite according to the present invention characteristically comprises a substrate that forms a single article with a cured silicone layer that is provided by the cure of the previously described curable silicone composition. This cured silicone composite can be obtained by coating the previously described curable silicone composition on a substrate and then thermosetting the curable silicone composition.
The curable silicone composition of the present invention, because it comprises a special alkenyl-functional dialkylpolysiloxane and a special alkenyl-functional, resin-form organopolysiloxane, characteristically provides a flexible and highly transparent cured silicone material that can maintain its high transparency over a broad temperature range from ambient temperature to high temperatures. Because it is flexible, the cured silicone material provided by the cure of this composition characteristically resists breakage during mold-based molding and component assembly processes and thus exhibits an excellent moldability and handling characteristics, and can also be used in applications that demand bendability, for example, use in a flexed or bent condition. In addition, because the present composition does not contain silicon-bonded aryl, for example, phenyl, the cured silicone material provided by the cure of the present composition characteristically does not suffer from a reduction in transparency even when held under high temperature, high humidity conditions or when exposed to ultraviolet radiation.


BEST MODE FOR CARRYING OUT THE INVENTION
The alkenyl-containing organopolysiloxane that is component (A) is the base component of the present composition and comprises (A-1) a dialkylpolysiloxane that has an average of at least two alkenyl groups in each molecule and a viscosity at 25° C. of 1,000 mPa·s to 50,000 mPa·s, at 50 mass % to 80 mass % of component (A), and (A-2) an alkenyl-containing, resin-form organopolysiloxane that comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit wherein R1 is C1-10 alkyl and R2 is alkenyl and that contains the alkenyl group at from at least 0.5 mass % to less than 3.5 mass %, at 20 mass % to 50 mass % of component (A).
Component (A-1) has an average of at least two alkenyl groups in each molecule. Component (A-1) has a substantially straight chain molecular structure, but a portion of the molecular chain may be somewhat branched. The alkenyl in component (A-1) can be exemplified by vinyl, allyl, isopropenyl, butenyl, hexenyl, and cyclohexenyl wherein vinyl is preferred. The bonding position for this alkenyl is not limited and may be, for example, the terminal position and/or side chain position on the molecular chain wherein terminal position on the molecular chain is preferred. The alkyl in component (A-1) can be exemplified by C1-10 alkyl such as methyl, ethyl, propyl, cyclopentyl, cyclohexyl, and so forth, wherein methyl is preferred.
The viscosity of component (A-1) at 25° C. is in the range from 1,000 mPa·s to 50,000 mPa·s and preferably is in the range from 1,500 mPa·s to 45,000 mPa·s and more preferably is in the range from 2,000 mPa·s to 45,000 mPa·s. When component (A-1) is a mixture of two or more alkenyl-functional dialkylpolysiloxanes, the viscosity of this mixture at 25° C. must be in the range from 1,000 mPa·s to 50,000 mPa·s. As long as the viscosity at 25° C. is in the specified range, component (A-1) may be a mixture of a small amount of an alkenyl-functional dialkylpolysiloxane gum and an alkenyl-functional dialkylpolysiloxane that is a liquid at 25° C. The reasons for the preceding are as follows: when the viscosity of component (A-1) at 25° C. is less than the lower limit cited above, the cured silicone material provided by the cure of the present composition tends to have an unsatisfactory flexibility; when, on the other hand, the viscosity of component (A-1) at 25° C. exceeds the upper limit cited above, the transparency of the cured silicone material provided by the cure of the present composition tends to decline at high temperatures, while the present composition assumes an excessively high viscosity and the handling characteristics tend to decline.
This component (A-1) diorganopolysiloxane is exemplified by dimethylpolysiloxanes endblocked at both molecular chain terminals by dimethylvinylsiloxy groups, dimethylsiloxane•methylvinylsiloxane copolymers endblocked at both molecular chain terminals by dimethylvinylsiloxy groups, methylvinylpolysiloxanes endblocked at both molecular chain terminals by trimethylsiloxy groups, dimethylsiloxane•methylvinylsiloxane copolymers endblocked at both molecular chain terminals by trimethylsiloxy groups, and mixtures of two or more of the preceding.
The content of component (A-1) in the present composition is an amount that is at least 50 mass % to not more than 80 mass % of component (A) and preferably is an amount that is at least 55 mass % to not more than 70 mass % of component (A) and particularly preferably is an amount that exceeds 60 mass % but is not more than 70 mass %. The reasons for this are as follows: when the component (A-1) content is less than the lower limit on the cited range, the flexibility of the cured silicone material provided by the cure of the present composition tends to decline; when, on the other hand, the component (A-1) content exceeds the upper limit on the cited range, the hardness of the cured silicone material provided by the cure of the present composition tends to decline.
The alkenyl-containing, resin-form organopolysiloxane that is component (A-2) imparts a satisfactory hardness and flexibility to the cured silicone material provided by the cure of the present composition and comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit. In these formulas, R1 is C1-10 alkyl such as methyl, ethyl, propyl, cyclopentyl, cyclohexyl, and so forth, and R2 is an alkenyl group such as vinyl, allyl, isopropenyl, butenyl, hexenyl, cyclohexenyl, and so forth, wherein vinyl is preferred.
The component (A-2) alkenyl-containing, resin-form organopolysiloxane contains the alkenyl group at from at least 0.5 mass % to less than 3.5 mass % and preferably contains from at least 1.0 mass % to not more than 2.5 mass % alkenyl. The reasons for this are as follows: when the alkenyl content in component (A-2) is less than the cited lower limit, the hardness of the cured silicone material provided by the cure of the present composition tends to decline; when, on the other hand, the alkenyl content in component (A-2) exceeds the cited upper limit, the flexibility of the cured silicone material provided by the cure of the present composition tends to decline and the transparency of the cured silicone material provided by the cure of the present composition tends to decline at high temperatures. Component (A-2) may be a mixture of two or more alkenyl-containing, resin-form organopolysiloxanes, in which case the mixture considered as such must contain alkenyl at from at least 0.5 mass % to less than 3.5 mass % and preferably contains from at least 1.0 mass % to not more than 2.5 mass % alkenyl.
The ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit in component (A-2) is preferably in the range from 0.50 to 1.80 and particularly preferably is in the range from 0.70 to 1.10. The reasons for this are as follows: when the ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit in component (A-2) is less than the cited lower limit, component (A-2) takes on an excessively large molecular weight and the transparency of the cured silicone material provided by the cure of the present composition may decline; when, on the other hand, the ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit in component (A-2) exceeds the upper limit cited above, the cured silicone material provided by the cure of the present composition may have an unsatisfactory strength.
Component (A-2) has a mass-average molecular weight, on a standard polystyrene basis by gel permeation chromatography, preferably in the range from 3,000 to 7,000 and more preferably in the range from 4,000 to 6,000. Component (A-2) may be a mixture of two or more alkenyl-containing, resin-form organopolysiloxanes and is preferably a mixture comprising alkenyl-containing, resin-form organopolysiloxanes that have a mass-average molecular weight, on a standard polystyrene basis by gel permeation chromatography, in the range from 3,000 to 7,000.
The content of component (A-2) in the present composition is an amount that is at least 20 mass % to not more than 50 mass % of component (A), preferably is an amount that is at least 30 mass % to not more than 45 mass % of component (A), and particularly preferably is an amount that is at least 30 mass % to less than 40 mass % of component (A). The reasons for this are as follows: when the component (A-2) content is less than the lower limit on the cited range, the hardness of the cured silicone material provided by the cure of the present composition tends to decline; when, on the other hand, the component (A-2) content exceeds the upper limit on the cited range, the flexibility of the cured silicone material provided by the cure of the present composition tends to decline and the transparency of the cured silicone material provided by the cure of the present composition tends to decline at high temperatures.
The organopolysiloxane that is component (B) is a crosslinking agent for the present composition and contains at least three silicon-bonded hydrogen atoms in each molecule. Viewed from the perspective of the transparency of the cured silicone material provided by the cure of the present composition, the silicon-bonded hydrogen content in component (B) is preferably at least 0.3 mass % and more preferably is at least 0.7 mass %. For a hardness of at least 60 for the cured silicone material provided by the cure of the present composition, said hardness being measured using the type A durometer specified in JIS K 6253, the silicon-bonded hydrogen content in component (B) is preferably at least 0.7 mass %.
The molecular structure of component (B) can be, for example, straight chain, partially branched straight chain, branched chain, cyclic, or dendritic wherein straight chain, partially branched straight chain, and dendritic are preferred. There are no limitations on the bonding position of the silicon-bonded hydrogen in component (B), and the silicon-bonded hydrogen may be bonded in, for example, terminal position on the molecular chain and/or side chain position on the molecular chain. The silicon-bonded groups in component (B) other than the silicon-bonded hydrogen are alkyl such as methyl, ethyl, propyl, cyclopentyl, cyclohexyl, and so forth, wherein methyl is preferred. This provides a good compatibility with component (A) and also provides an excellent transparency for the cured silicone material provided by the cure of the present composition. While there is no limitation on the viscosity of component (B), its viscosity at 25° C. is preferably in the range from 1 to 10,000 mm2/s and particularly preferably is in the range from 1 to 1,000 mm2/s.
An example of a particularly preferred component (B) is an organopolysiloxane comprising (B-1) an organopolysiloxane that contains at least 0.7 mass % silicon-bonded hydrogen and that comprises the SiO4/2 unit and HR32SiO1/2 unit wherein R3 is C1-10 alkyl such as methyl, ethyl, propyl, cyclopentyl, cyclohexyl, and so forth, with methyl being preferred, at 50 to 100 mass % of component (B), and (B-2) a straight-chain organopolysiloxane that contains at least 0.3 mass % silicon-bonded hydrogen wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, at 0 to 50 mass % of component (B).
In addition to the SiO4/2 unit and HR32SiO1/2 unit, component (B-1) may also contain the R33SiO1/2 unit. The ratio of the total number of moles of HR32SiO1/2 and R33SiO1/2 units to 1 mole of the SiO4/2 unit in component (B-1) is preferably in the range from 1.50 to 2.50 and more preferably is in the range from 1.80 to 2.20. A specific example of a preferred component (B-1) is the organopolysiloxane given by (SiO4/2)4(H(CH3)2SiO1/2)8.
The component (B-2) straight-chain organopolysiloxane contains at least 0.3 mass % and preferably at least 0.7 mass % silicon-bonded hydrogen. The silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl such as methyl, ethyl, propyl, cyclopentyl, cyclohexyl, and so forth, wherein methyl is preferred. Component (B-2) has a substantially straight chain molecular structure, but a portion of the molecular chain may be somewhat branched. Preferred specific examples of component (B-2) are dimethylsiloxane•methylhydrogensiloxane copolymers endblocked at both molecular chain terminals by dimethylhydrogensiloxy groups, methylhydrogenpolysiloxanes endblocked at both molecular chain terminals by trimethylsiloxy groups, dimethylsiloxane•methylhydrogensiloxane copolymers endblocked at both molecular chain terminals by trimethylsiloxy groups, and mixtures of two or more of the preceding.
The content of component (B) in the present composition is an amount that provides from 0.8 to 2 moles and preferably from 0.9 to 1.5 moles silicon-bonded hydrogen atoms in this component per 1 mole of the total alkenyl in component (A). The reasons for this are as follows: when the component (B) content is less than the lower limit for the cited range, curing of the composition tends to be unsatisfactory; when, on the other hand, the upper limit for the cited range is exceeded, the flexibility and/or transparency of the cured silicone material provided by the cure of the present composition may be diminished.
The hydrosilylation reaction catalyst that is component (C) is a catalyst for promoting curing of the present composition and can be exemplified by platinum-type catalysts, rhodium-type catalysts, and palladium-type catalysts, wherein the platinum-type catalysts are particularly preferred. These platinum-type catalysts can be exemplified by platinum micropowder, platinum black, platinum supported on silica micropowder, platinum supported on active carbon, chloroplatinic acid, alcohol solutions of chloroplatinic acid, and platinum compounds such as olefin complexes of platinum, alkenylsiloxane complexes of platinum, and so forth.
The component (C) content in the present composition is a catalytic quantity and in specific terms is a quantity that provides 0.01 to 1,000 mass-ppm catalyst metal atoms with reference to the present composition. The reasons for this are as follows: when the component (C) content is less than the lower limit for the cited range, the risk arises that the cure of the resulting composition will not proceed adequately; on the other hand, curing is not significantly promoted by exceeding the upper limit for the cited range, while the risk arises that problems will appear such as discoloration of the cured silicone material.
As other, optional components, the present composition may contain, for example, a reaction inhibitor in order to adjust the cure rate of the present composition, e.g., an alkyne alcohol such as 2-methyl-3-butyn-2-ol, 3,5-dimethyl-1-hexyn-3-ol, 1-ethynyl-1-cyclohexanol, phenylbutynol, and so forth; ene-yne compounds such as 3-methyl-3-penten-1-yne, 3,5-dimethyl-3-hexen-1-yne, and so forth; as well as 1,3,5,7-tetramethyl-1,3,5,7-tetravinylcyclotetrasiloxane, 1,3,5,7-tetramethyl-1,3,5,7-tetrahexenylcyclotetrasiloxane, benzotriazole, and so forth. There is no limitation on the content of this reaction inhibitor in the present composition, and this content may be selected as appropriate as a function of the molding method and curing conditions; however, an amount within the range from 10 to 5,000 mass-ppm with reference to the present composition is generally preferred.
The present composition may incorporate, insofar as the object of the present invention is not impaired, for example, an adhesion promoter, flame retardant, inorganic filler, and so forth. However, as a general matter, an adhesion promoter, flame retardant, and inorganic filler are preferably not incorporated from the perspective of the transparency of the cured silicone material provided by the cure of the present composition.
When the cured silicone material provided by the cure of the present composition is to be used in electrical•electronic applications, the content in the present composition of low molecular weight organopolysiloxane having a molecular weight not more than 650 is preferably not more than 350 ppm.
The viscosity of the present composition at 25° C. is not particularly limited, but considered from the standpoint of the moldability and handling characteristics, i.e., ease of pouring or injection, ease of degassing, and so forth, the viscosity of the present composition at 25° C. is preferably 1 to 100 Pa·s and particularly preferably is 2 to 50 Pa·s.
The present composition forms a cured silicone material when cured by heating to 100 to 250° C. This cured silicone material according to the present invention has a hardness, as measured using the type A durometer specified in JIS K 6253, in the range from at least 30 to not more than 80, preferably in the range from at least 50 to not more than 80, and more preferably in the range from at least 60 to not more than 75. The reasons for this are as follows: the cured silicone material may have insufficient strength when its hardness is less than the lower limit for the cited range; when, on the other hand, the upper limit for the cited range is exceeded, the flexibility of the cured silicone material under consideration tends to be inadequate. When this cured silicone material is to be used as an optical member or component, the hardness, as measured using the type A durometer specified in JIS K 6253, is particularly preferably in the range from at least 60 to not more than 80 based on a consideration of the moldability and the handling characteristics.
In order to exhibit a satisfactory flexibility, this cured silicone material must have an elongation as specified in JIS K 6251 of at least 50%. The reason for this is that the flexibility of the cured silicone material becomes unsatisfactory at below the indicated range.
The present cured silicone material must have a parallel light transmittance at 25° C., measured in accordance with JIS K 7105 on the 6 mm-thick cured silicone material, i.e., on a 6 mm optical path length, of at least 90%, and must have a parallel light transmittance at 200° C. that is a value that is at least 99% of the parallel light transmittance at 25° C. The reason for this is that deficiencies tend to occur in optical component applications when the present cured silicone material has a parallel light transmittance at 200° C. that is less than 99% of the parallel light transmittance at 25° C.
In addition, the present cured silicone material may be a composite in which the cured silicone material is formed into a single article with any of various substrates. The substrate can be exemplified by various metals, thermoplastic plastics, thermosetting plastics, rubbers such as silicone rubbers and so forth, backing fabrics such as those made of nylon or polyester, electronic parts and components, and light-emitting elements. Such a cured silicone composite can be obtained by coating the present composition on a substrate and then thermosetting.
EXAMPLES
The curable silicone composition of the present invention will be described in detail through examples and comparative examples. In the examples, the viscosity is the value at 25° C. and parts indicates mass parts.
The nature and designation of the materials used in the following examples for components (A)-(C) and the reaction inhibitor as a cure retarder are as indicated below. Here, Vi designates the vinyl group while Me designates the methyl group.
Component A-1
a-1: a dimethylpolysiloxane endblocked by dimethylvinylsiloxy groups at both molecular chain terminals, that has a viscosity of 500 mPa·s and a vinyl group content of 0.45 mass %.
a-2: a dimethylpolysiloxane endblocked by dimethylvinylsiloxy groups at both molecular chain terminals, that has a viscosity of 2,000 mPa·s and a vinyl group content of 0.23 mass %.
a-3: a dimethylpolysiloxane endblocked by dimethylvinylsiloxy groups at both molecular chain terminals, that has a viscosity of 10,000 mPa·s and a vinyl group content of 0.14 mass %.
a-4: a dimethylpolysiloxane endblocked by dimethylvinylsiloxy groups at both molecular chain terminals, that has a viscosity of 40,000 mPa·s and a vinyl group content of 0.10 mass %.
a-5: a dimethylpolysiloxane endblocked by dimethylvinylsiloxy groups at both molecular chain terminals, that has a viscosity of 80,000 mPa·s and a vinyl group content of 0.07 mass %.
Component A-2
a-6: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.04(Me3SiO1/2)0.40(SiO4/2)0.56, that has a mass-average molecular weight of approximately 4,600, a vinyl group content of 1.6 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 0.79.
a-7: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.06(Me3SiO1/2)0.38(SiO4/2)0.56, that has a mass-average molecular weight of approximately 4,600, a vinyl group content of 2.3 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 0.79.
a-8: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.04(Me3SiO1/2)0.46(SiO4/2)0.50, that has a mass-average molecular weight of approximately 4,000, a vinyl group content of 1.6 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 1.00.
a-9: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.06(Me3SiO1/2)0.44(SiO4/2)0.50, that has a mass-average molecular weight of approximately 4,000, a vinyl group content of 2.3 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 1.00.
a-10: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.02(Me3SiO1/2)0.42(SiO4/2)0.56, that has a mass-average molecular weight of approximately 4,600, a vinyl group content of 0.75 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 0.79.
a-11: an organopolysiloxane given by the average unit formula (ViMe2SiO1/2)0.11(Me3SiO1/2)0.33(SiO4/2)0.57, that has a mass-average molecular weight of approximately 4,800, a vinyl group content of 4.2 mass %, and a ratio of the total number of moles of R12R2SiO1/2 and R13SiO1/2 units to 1 mole of the SiO4/2 unit of 0.77.
Component B
b-1: an organopolysiloxane given by the average unit formula (HMe2SiO1/2)8(SiO4/2)4, that has a kinematic viscosity of 18 mm2/s and a silicon-bonded hydrogen atom content of approximately 0.97 mass %.
b-2: a polymethylhydrogensiloxane endblocked at both molecular chain terminals by trimethylsiloxy groups, that has a kinematic viscosity of 21 mm2/s and a silicon-bonded hydrogen atom content of approximately 1.57 mass %.
b-3: a dimethylsiloxane•methylhydrogensiloxane copolymer endblocked by trimethylsiloxy groups at both molecular chain terminals, that has a kinematic viscosity of 5 mm2/s and a silicon-bonded hydrogen atom content of approximately 0.75 mass %.
b-4: a dimethylsiloxane•methylhydrogensiloxane copolymer endblocked by trimethylsiloxy groups at both molecular chain terminals, that has a kinematic viscosity of 5 mm2/s and a silicon-bonded hydrogen atom content of approximately 0.45 mass %.
Component C
platinum catalyst: a 1,3-divinyltetramethyldisiloxane solution of a 1,3-divinyltetramethyldisiloxane complex of platinum. The platinum metal content is approximately 6500 ppm.
Reaction Inhibitor as a Cure Retarder
3,5-dimethyl-1-octyn-3-ol
Examples 1 to 8 and Comparative Examples 1 to 3
The materials shown in Tables 1 and 2 were mixed to uniformity in the quantity proportions shown in Tables 1 and 2 to produce curable silicone compositions. The resulting compositions were heated for 5 minutes at 150° C. to produce the 1 mm-thick cured sheet, which was submitted to measurement of the tensile strength and elongation. The compositions were also heated for 10 minutes at 150° C. to produce the 6 mm-thick cured silicone material, which was submitted to measurement of the hardness, parallel light transmittance at 25° C., and parallel light transmittance at 200° C. The results are given in Tables 1 and 2. The SiH/Vi in Tables 1 and 2 indicates the ratio of the number of moles of silicon-bonded hydrogen in component (B) per 1 mole of the vinyl group in components (A-1) and (A-2).
Test, Measurement, and Evaluation Methods
The properties (hardness, tensile strength, elongation, and light transmission) of the cured silicone material were tested, measured, or evaluated using the following methods.
(1) Hardness
A 6 mm-thick cured silicone material was fabricated by curing the curable silicone composition by heating for 10 minutes at 150° C. The hardness of this cured silicone material was measured using the type A durometer specified in JIS K 6253.
(2) Tensile Strength and Elongation
A 1 mm-thick cured silicone material was fabricated by curing the curable silicone composition by heating for 5 minutes at 150° C. The tensile strength and elongation of this cured silicone material were measured according to the methods specified in JIS K 6251.
(3) Light Transmission
A 6 mm-thick cured sheet was fabricated by heating the curable silicone composition for 10 minutes at 150° C. The parallel light transmittance at 25° C. and 200° C. for a 6 mm optical path length was measured on the resulting cured sheet based on JIS K 7105 using a Water Analyzer-200N from Nippon Denshoku Industries Co., Ltd. Air was used as the reference. The parallel light transmittance at 200° C. is the value measured as follows: the cured sheet is fixed in advance in a sample holder and is then heated for 10 minutes in a 200° C. oven, after which the cured sheet is removed from the oven; measurement is then performed within 20 seconds. The parallel light transmittance at 200° C. measured as described in the preceding was calculated as the percentage with respect to the parallel light transmittance at 25° C., and this is reported in Tables 1 and 2 as the parallel light transmittance retention rate in %.














TABLE 1







Example 1
Example 2
Example 3
Example 4
Example 5
Example 6























(A-1) (parts)
a-1









a-2
55
55
55
45



a-3



20
20



a-4




47
55



a-5


(A-2) (parts)
a-6
45
45
45



a-7



35
33



a-8





45



a-9



a-10



a-11


(B) (parts)
b-1
5


5.2
4.6
6



b-2

4.6



b-3


8.5



b-4


(C) (parts)

0.08
0.08
0.08
0.08
0.08
0.08













reaction Inhibitor (parts)
0.1
0.1
0.1
0.1
0.1
0.1


SiH/Vi
1.6
2.4
1.9
1.5
1.5
2.1


hardness
67
65
70
62
66
68


Tb (MPa)
12.4
7.8
10.4
7.2
8.1
10.6


Eb (%)
95
130
75
150
115
90


parallel light transmittance (%)
93
93
93
93
93
93


parallel light transmittance retention
100
100
100
100
100
100


rate (%)






















TABLE 2









Comp.
Comp.
Comp.



Example 7
Example 8
Example 1
Example 2
Example 3






















(A-1)
a-1


55




(parts)
a-2
50
45



a-3

20

57



a-4



a-5




65


(A-2)
a-6


45


(parts)
a-7

35



a-8



a-9




35



a-10
50



a-11



43


(B)
b-1
3.5

5
10.8


(parts)
b-2




3



b-3



b-4

11












(C) (parts)
0.08
0.08
0.08
0.08
0.08


reaction inhibitor (parts)
0.1
0.1
0.1
0.1
0.1


SiH/Vi
1.9
1.4
1.4
1.6
1.5


hardness
55
40
69
89
74


Tb (MPa)
11.8
4.5
6.4
8.5
8.8


Eb (%)
120
300
40
43
60


parallel light transmittance (%)
93
93
93
93
93


parallel light transmittance retention
100
100
100
98
92


rate (%)









INDUSTRIAL APPLICABILITY
The curable silicone composition of the present invention, because it forms a flexible and highly transparent cured silicone material, is useful as an optical member or component that is permeable to light, e.g., visible light, infrared, ultraviolet, far ultraviolet, x-ray, laser, and so forth. In particular, because the cured silicone material provided by the cure of the curable silicone composition of the present invention does not undergo temperature-induced variations in transparency, this cured silicone material is well suited for use as an optical member or component for devices involved with high energy, high output light. In addition, a flexible and highly transparent cured silicone layer can be formed on the surface of any of various substrates, e.g., silicone rubbers, backing fabrics made of nylon or polyester, and so forth, by the formation of a single article with a substrate by coating the surface of the substrate with the curable silicone composition of the present invention and then thermosetting, and as a consequence the curable silicone composition of the present invention is also useful as a coating material and a surface layer material.
The cured silicone material of the present invention, because it is flexible and highly transparent, is useful as an optical member or component that is permeable to light, e.g., visible light, infrared, ultraviolet, far ultraviolet, x-ray, laser, and so forth. The cured silicone material of the present invention is also useful as an optical member or component that must be flexible, e.g., due to use in a flexed or bent condition, and is also useful as an optical member or component for devices involved with high energy, high output light. In addition, an article or component having a flexible and highly transparent cured silicone layer can be made by making a composite in which the cured silicone material of the present invention is formed into a single article or body with any of various substrates, and an impact- and stress-relaxing function can also be expected from the cured silicone layer.

## Claims

1. A curable silicone composition comprising
(A) 100 mass parts of an alkenyl-containing organopolysiloxane comprising
(A-1) a dialkylpolysiloxane that has an average of at least two alkenyl groups in each molecule and a viscosity at 25° C. of at least 1,000 mPa·s to not more than 50,000 mPa·s, at from 50 mass % to not more than 80 mass % of component (A), and
(A-2) an alkenyl-containing, resin-form organopolysiloxane that comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit wherein R1 is C1-10 alkyl and R2 is alkenyl, and that contains the alkenyl group in the range from at least 1 mass % to less than 3.5 mass %, at from 20 mass % to not more than 50 mass % of component (A);

(B) an organopolysiloxane that has an average of at least three silicon-bonded hydrogen atoms in each molecule wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, in an amount that provides 0.8 to 2 moles silicon-bonded hydrogen in this component per 1 mole of the total alkenyl in component (A),
wherein component (B) is an organopolysiloxane comprising
(B-1) an organopolysiloxane that contains at least 0.7 mass % silicon-bonded hydrogen and that comprises SiO4/2 units and HR32SiO1/2 units in a ratio ranging from 1.50 to 2.50 moles of HR32SiO1/2 units per 1 mole of SiO4/2 units wherein R3 is C1-10 alkyl, at 50 to 100 mass % of component (B), and
(B-2) a straight-chain organopolysiloxane that contains at least 0.3 mass % silicon-bonded hydrogen wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, at 0 to 50 mass % of component (B); and

(C) a hydrosilylation reaction catalyst in a catalytic quantity, and provides a highly transparent cured silicone material that has a hardness measured using the type A durometer specified in JIS K 6253 is in the range from at least 30 to not more than 80, the elongation as specified in JIS K 6251 is at least 50%, the parallel light transmittance at 25° C. measured in accordance with JIS K 7105 on a 6 mm optical path length is at least 90%, and the parallel light transmittance at 200° C. is a value that is at least 99% of the parallel light transmittance at 25° C.

2. A highly transparent cured silicone material provided by the thermosetting of a curable silicone composition comprising
(A) 100 mass parts of an alkenyl-containing organopolysiloxane comprising
(A-1) a dialkylpolysiloxane that has an average of at least two alkenyl groups in each molecule and a viscosity at 25° C. of at least 1,000 mPa·s to not more than 50,000 mPa·s, at from 50 mass % to not more than 80 mass % of component (A), and
(A-2) an alkenyl-containing, resin-form organopolysiloxane that comprises the SiO4/2 unit, R12R2SiO1/2 unit, and R13SiO1/2 unit wherein R1 is C1-10 alkyl and R2 is alkenyl and that contains the alkenyl group in the range from at least 1 mass % to less than 3.5 mass %, at from 20 to not more than 50 mass % of component (A);

(B) an organopolysiloxane that has an average of at least three silicon-bonded hydrogen atoms in each molecule wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, in an amount that provides 0.8 to 2 moles silicon-bonded hydrogen in this component per 1 mole of the total alkenyl in component (A),
wherein component (B) is an organopolysiloxane comprising
(B-1) an organopolysiloxane that contains at least 0.7 mass % silicon-bonded hydrogen and that comprises SiO4/2 units and HR32SiO1/2 units in a ratio ranging from 1.50 to 2.50 moles of HR32SiO1/2 units per 1 mole of SiO4/2 units wherein R3 is C1-10 alkyl, at 50 to 100 mass % of component (B), and
(B-2) a straight-chain organopolysiloxane that contains at least 0.3 mass % silicon-bonded hydrogen wherein the silicon-bonded groups other than the silicon-bonded hydrogen are C1-10 alkyl, at 0 to 50 mass % of component (B); and

(C) a hydrosilylation reaction catalyst in a catalytic quantity, and having a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 30 to not more than 80, an elongation as specified in JIS K 6251 of at least 50%, a parallel light transmittance at 25° C. measured in accordance with JIS K 7105 on a 6 mm optical path length of at least 90%, and a value for the parallel light transmittance at 200° C. that is at least 99% of the parallel light transmittance at 25° C.

3. The highly transparent cured silicone material according to claim 2, which has a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 65 to not more than 75.

4. A cured silicone composite comprising a substrate that forms a single article with a cured silicone layer that is provided by the thermosetting of a curable silicone composition according to claim 1.

5. A cured silicone composite obtained by coating the curable silicone composition according to claim 1 on a substrate and then thermosetting the curable silicone composition.

6. The highly transparent cured silicone material according to claim 2, which has a hardness measured using the type A durometer specified in JIS K 6253 in the range from at least 65 to not more than 75.

7. The curable silicone composition according to claim 1, wherein component (A-1) is included in an amount ranging from 55 mass % to not more than 70 mass % of component (A).

8. The highly transparent cured silicone material according to claim 2, wherein component (A-1) is included in an amount ranging from 55 mass % to not more than 70 mass % of component (A).

9. The curable silicone composition according to claim 1, wherein component (A-2) is included in an amount ranging from 30 mass % to not more than 45 mass % of component (A).

10. The highly transparent cured silicone material according to claim 2, wherein component (A-2) is included in an amount ranging from 30 mass % to not more than 45 mass % of component (A).