# Patent

## Title
Waterborne base coat compositions having a light metallic color

## Abstract

A waterborne base coat having a light metallic color and containing 0.5 to 2 wt.-% of poly(meth)acrylic acid thickener and 2 to 7 wt.-% of non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C., the wt.-% in each case calculated as solids and relative to the solids content of the waterborne base coat.

## Background
FIELD OF THE INVENTION
The invention relates to waterborne base coat compositions (in the following description and the claims also called “waterborne base coats”) having a light metallic color (light metallic hue). The waterborne base coats can be used for the production of the base coat layer in a process for the production of a base coat/clear coat two-layer coating having a light metallic color on a substrate, in particular on an automotive substrate.
DESCRIPTION OF THE PRIOR ART
In the description and the claims the term “light metallic color” is used. A base coat/clear coat two-layer coating having a light metallic color is one exhibiting a lightness L* (according to CIEL*a*b*, DIN 6174 (October 2007)), measured at an illumination angle of 45 degrees to the perpendicular (surface normal) and an observation angle (viewing angle) of 15 degrees to the specular (specular reflection), of at least 60 units, in particular, of at least 80 units, for example, of 60 to 145 units, in particular, of 80 to 145 units. The measurement of the lightness L* at an illumination angle of 45 degrees to the perpendicular and an observation angle of 15 degrees to the specular is known to the person skilled in the art and can be carried out with commercial professional measuring instruments, for example, the instrument X-Rite MA 68 sold by the firm X-Rite Incorporated, Grandeville, Mich., U.S.A.
Base coat/clear coat two-layer coatings having light metallic colors are well-known, in particular in automotive coating. Light metallic colors belong to the group of special-effect colors and they exhibit a so-called “lightness flop” and, dependent on the composition of the pigment content of a certain coating composition, they may exhibit a color flop as well. “Flop” means the behavior of a coating to change lightness and/or color dependent on the observation angle. Said behavior is a result of oriented special-effect pigments or flake pigments contained in a coating layer applied from a correspondingly pigmented coating composition.
Accordingly, in the sense of the present invention, a waterborne base coat having a light metallic color is a waterborne coating composition from which the base coat layer of a base coat/clear coat two-layer coating having a light metallic color can be applied.
Today's automotive coatings generally comprise an electrodeposition coating (EDC) primer, a primer surfacer layer (filler layer) as intermediate coating layer and a top coat comprising a wet-on-wet applied color- and/or special-effect-imparting base coat layer and a protective, gloss-imparting clear coat layer. In case of the application of a special-effect-imparting base coat layer it is state of the art in automotive coating to apply it in two layers, the first of which is spray-applied by electrostatically assisted high-speed rotary atomization (spray-application performed by electrostatic high rotation bells) and the second of which is pneumatically spray-applied to achieve an optimum orientation of the special-effect pigments; see A. Goldschmidt and H.-J. Streitberger, BASF Handbook on Basics of Coating Technology, Vincentz, Hannover, 2003, pages 702-705.
One disadvantage of pneumatic paint application is the huge overspray paint loss compared to paint application by electrostatically assisted high-speed rotary atomization.
SUMMARY OF THE INVENTION
It has now been found that it is possible to spray-apply the base coat layer of base coat/clear coat two-layer coatings having a light metallic color simply or just by electrostatically assisted high-speed rotary atomization (without an additional pneumatic spray-application step) and without loss of lightness flop performance of the resultant base coat/clear coat two-layer coating, if the waterborne light metallic base coat selected as the coating material for the application of the base coat layer contains a specific additive combination of poly(meth)acrylic acid thickener and non-ionically emulsified EVA (ethylene/vinyl acetate) copolymer wax with a drop point of the wax portion of 80 to 110° C.
The term “without loss of lightness flop performance” is used herein. It means that the metallic effect or the performance of the lightness flop equals that of a light metallic base coat/clear coat two-layer coating produced according to the prior art method, i.e. which—as explained above—employs an additional pneumatic spray-application step of the respective waterborne light metallic base coat prior to the application of the clear coat.
The term “(meth)acryl” used herein means methacryl and/or acryl.
In the description and the claims the term “drop point” (also called “dropping point”) is used. Drop point and melting point shall not be confused with each other, although both temperature points describe the same or almost the same, namely the temperature at which a material passes from a solid or semi-solid state into the liquid state. Melting point and drop point measurements of a material may lead to the same result; however, the drop point may also be slightly higher or slightly lower than the melting point. The drop point is determined according to DIN ISO 2176 (May 1997).
The invention is directed to waterborne base coats having a light metallic color and containing 0.5 to 2 wt.-% (weight-%) of poly(meth)acrylic acid thickener and 2 to 7 wt.-% of non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C., the wt.-% in each case calculated as solids and relative to the solids content (overall solids) of the waterborne base coats.
The invention is also related to a process for the formation of a base coat/clear coat two-layer coating having a light metallic color on a substrate, wherein the base coat layer is applied from a waterborne base coat of the present invention only by electrostatically assisted high-speed rotary atomization.


DETAILED DESCRIPTION OF THE EMBODIMENTS
The waterborne base coats of the present invention are aqueous coating compositions having a solids content of 15 to 25 wt.-%. In addition to water, a resin solids content, a pigment content, the poly(meth)acrylic acid thickener and the non-ionically emulsified EVA copolymer wax, the waterborne base coats may contain one or more of the following optional components: fillers (extenders), organic solvents, additives other than (other than=different from) poly(meth)acrylic acid thickeners and also other than non-ionically emulsified EVA copolymer waxes. The waterborne base coats have a ratio by weight of pigment content to resin solids content of, for example, 0.15:1 to 0.6:1.
The term “solids content” used in the present description and the claims means the sum of the non-volatile components of a coating composition, i.e. the sum of the resin solids, pigments, fillers and non-volatile additives. The rest of the coating composition is formed by volatile components, i.e. water, optionally present organic solvents and optionally present volatile additives.
The term “resin solids content” used in the present description and the claims means the sum of the solids contributions of the coating binders (binder solids) and the solids contributions of crosslinkers (crosslinker solids, crosslinking agent solids) optionally contained in a coating composition. The coating binders include paste resins optionally contained in the coating composition.
The term “pigment content” used in the present description and the claims means the sum of all the pigments contained in a coating composition. The pigment content does not comprise fillers. The term “pigments” is used here as in DIN 55944 (November 2003) and covers, in addition to special-effect pigments, inorganic white, colored and black pigments and organic colored and black pigments. At the same time, therefore, DIN 55944 distinguishes between pigments and fillers.
The waterborne base coats of the present invention contain anionically and/or non-ionically stabilized aqueous binder systems. Anionic stabilization is preferably achieved by at least partially neutralized carboxyl groups in the binder, while non-ionic stabilization is preferably achieved by lateral and/or terminal polyethylene oxide units (polyethylene glycol structures) in the binder. The waterborne base coats may be physically drying or crosslinkable by formation of covalent bonds. The crosslinkable waterborne base coats forming covalent bonds may be self- or externally crosslinkable systems.
The waterborne base coats of the present invention contain one or more conventional water-dilutable film-forming binders. They may optionally also contain crosslinking agents if the binders are not self-crosslinkable or physically drying. Examples of suitable binders are conventional water-dilutable binders familiar to the person skilled in the art, such as water-dilutable polyester resins, water-dilutable (meth)acrylic copolymer resins, water-dilutable polyester/(meth)acrylic copolymer hybrids, water-dilutable polyurethane resins and water-dilutable polyurethane/(meth)acrylic copolymer hybrids. Selection of the optionally contained crosslinking agents depends, in a manner familiar to the person skilled in the art, on the functionality of the binders, i.e., the crosslinking agents are selected in such a way that they exhibit a reactive functionality complementary to the functionality of the binders. Examples of such complementary functionalities between binder and crosslinking agent are: carboxyl/epoxy, hydroxyl/methylol ether and/or methylol (methylol ether and/or methylol preferably, as crosslinkable groups of amino resins, in particular, melamine resins). Examples of crosslinking agents include free or blocked polyisocyanates and amino resins, for example, melamine resins. The crosslinking agents may be used individually or in combination. The weight ratio between crosslinking agent solids and binder solids amounts, for example, to 10:90 to 40:60.
As already mentioned, the waterborne base coats of the present invention have light metallic colors, in particular silver metallic colors. Accordingly, they comprise an appropriate amount of at least one aluminum flake pigment; the solids contents of the waterborne base coats comprise, for example, 15 to 25 wt.-% of one or more aluminum flake pigments.
The term “aluminum flake pigment” is used herein. It means aluminum pigments, in particular those of the non-leafing type, as are conventionally used as special-effect pigments in paint and coatings, in particular in waterborne base coats such as automotive waterborne base coats, to provide a metallic effect, i.e., a lightness flop dependent on the angle of observation. Examples of such commercially available aluminum flake pigments include those sold under the names Alpate® WXA, Alpate® WXT, Alpate® EMR-B and Alpate® EMR-D, in each case by Toyal, STAPA Hydrolac®, STAPA Hydrolux®, STAPA Hydrolan®, Metalure®,
Silvershine® and Hydroshine®, in each case by Eckart, Metasheen® by Ciba, Starbrite® by Silberline and Decomet® by Schlenk.
In addition to the at least one aluminum flake pigment the pigment content of the waterborne base coats of the present invention can comprise one or more pigments different from the at least one aluminum flake pigment. The pigment(s) different from the at least one aluminum flake pigment are selected by type and quantity in such a way that the waterborne base coats have a light metallic color.
Examples of pigments different from the at least one aluminum flake pigment are conventional special-effect pigments imparting to a coating a viewing angle-dependent color and/or lightness flop, such as, non-leafing metal pigments from metals different from aluminum, e.g., of copper, interference pigments, such as, e.g., metal oxide-coated metal pigments, e.g., iron oxide-coated aluminum, coated micas, such as, e.g., titanium dioxide-coated mica, pigments producing a graphite effect, platelet-shaped iron oxide, liquid crystal pigments, coated aluminum oxide pigments, coated silicon dioxide pigments, and also conventional pigments selected from white, colored and black pigments, such as, e.g., conventional inorganic or organic pigments known to the skilled person, for example, titanium dioxide, iron oxide pigments, carbon black, azo pigments, phthalocyanine pigments, quinacridone pigments, pyrrolopyrrol pigments, perylene pigments.
The waterborne base coats of the present invention may also contain fillers, for example, in proportions of 0 to 25 wt.-% relative to the resin solids content of the waterborne base coats. The fillers do not constitute part of the pigment content of the waterborne base coats. Examples of fillers are barium sulfate, kaolin, talcum, silicon dioxide, layered silicates and any mixtures thereof.
The special-effect pigments present in the waterborne base coats of the present invention are generally initially introduced in the form of a conventional commercial aqueous or non-aqueous paste, optionally, combined with preferably water-dilutable organic solvents and additives and then mixed with aqueous binder. Pulverulent special-effect pigments may first be processed with preferably water-dilutable organic solvents and additives to yield a paste.
White, colored and black pigments and/or fillers may, for example, be ground in a proportion of the aqueous binder. Grinding may preferably also take place in a special water-dilutable paste resin. Grinding may be performed in conventional assemblies known to the person skilled in the art. The formulation is then made up with the remaining proportion of the aqueous binder or of the aqueous paste resin.
The waterborne base coats of the present invention contain poly(meth)acrylic acid thickener in a proportion of 0.5 to 2 wt.-%, calculated as solids and relative to the solids content of the waterborne base coats. Poly(meth)acrylic acid thickeners are thickeners known to the person skilled in the art of aqueous paint and coating, for example, copolymers of (meth)acrylic acid and (meth)acrylic acid esters containing polymerized (meth)acrylic acid, for example, in an amount of 30 to 60% by weight. Viscalex® HV 30 from Ciba is an example of a commercially available poly(meth)acrylic acid thickener. The poly(meth)acrylic acid thickeners are used in an at least partially neutralized form in the waterborne base coats, or, after their addition to the waterborne base coats, are at least partially neutralized. Amines or aminoalcohols are particular examples of alkaline neutralizing agents which can be used for partially or totally neutralizing the poly(meth)acrylic acid thickeners.
The waterborne base coats of the present invention contain non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C. in a proportion of 2 to 7 wt.-%, calculated as solids and relative to the solids content of the waterborne base coats. To avoid misunderstandings, the 2 to 7 wt.-% include the solids contribution of the non-ionic emulsifier or non-ionic surfactant. The EVA copolymer waxes having a drop point of 80 to 110° C. contain, in particular, 6 to 14 wt.-% of copolymerized vinyl acetate. The weight ratio between non-ionic emulsifier or non-ionic surfactant and the EVA copolymer wax of the non-ionically emulsified EVA copolymer wax is, for example, 0.1:99.9 to 10:90, or, in an embodiment, for example, 0.5:99.5 to 5:95.
The poly(meth)acrylic acid thickener and the non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C. may be introduced into the waterborne base coats of the present invention as separate components and/or in the form of an intermediate product containing both additives in combination. Aquatix® 8421 from BYK is an example of such a commercially available intermediate product.
In addition to the poly(meth)acrylic acid thickener and the non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C., the waterborne base coats of the present invention may contain conventional paint additives other than poly(meth)acrylic acid thickeners and other than non-ionically emulsified EVA copolymer waxes.
Such conventional paint additives may be contained in conventional quantities, for example, of 0.1 to 5 wt.-%, relative to the solids content of the waterborne base coats. Examples of such conventional paint additives include neutralizing agents, antifoaming agents, wetting agents, adhesion promoters, catalysts, levelling agents, anticratering agents and thickeners other than poly(meth)acrylic acid thickeners.
The waterborne base coats of the present invention may contain conventional organic solvents, for example, in a proportion of preferably less than 25 wt.-%, particularly preferably less than 20 wt.-%, based on total waterborne base coat. Examples of such organic solvents are alcohols, for example, propanol, butanol, hexanol; glycol ethers or esters, for example, diethylene glycol di-C1-C6-alkyl ether, dipropylene glycol di-C1-C6-alkyl ether, ethoxypropanol, ethylene glycol monobutyl ether; glycols, for example, ethylene glycol and/or propylene glycol, and the di- or trimers thereof; N-alkylpyrrolidone, such as, for example, N-ethylpyrrolidone; ketones such as methyl ethyl ketone, acetone, cyclohexanone; aromatic or aliphatic hydrocarbons, for example, toluene, xylene or linear or branched aliphatic C6-C12 hydrocarbons.
The waterborne base coats of the present invention can be used to spray-apply the base coat layer of base coat/clear coat two-layer coatings having light metallic colors by electrostatically-assisted high speed rotary atomization and without a need for the hitherto inevitably necessary additional pneumatic spray-application step. In other words, the waterborne base coats of the present invention allow for the spray-application of the base coat layer of base coat/clear coat two-layer coatings having light metallic colors just by electrostatically-assisted high speed rotary atomization, wherein the resultant base coat/clear coat two-layer coatings exhibit a lightness flop which satisfies great demands like the specifications of car manufacturers. In still other words, the waterborne base coats of the present invention satisfy a long-felt need for waterborne base coats having light metallic colors and which exhibit the aforementioned excellent lightness flop performance although the waterborne base coats are applied only by electrostatically-assisted high speed rotary atomization.
The invention is therefore also related to a process for the production of a base coat/clear coat two-layer coating having a light metallic color, wherein the base coat layer is spray-applied from a waterborne base coat of the present invention onto a substrate only by electrostatically-assisted high speed rotary atomization. The process comprises the steps:

    (1) providing a substrate to be provided with a base coat/clear coat two-layer coating having a light metallic color,
    (2) spray-applying a waterborne base coat of the present invention on the substrate only by electrostatically-assisted high speed rotary atomization to form the base coat layer,
    (3) spray-applying a clear coat composition on the base coat layer formed in step (2) to form the clear coat layer, and
    (4) jointly curing the base coat layer and the clear coat layer at an object temperature at or above the drop point of the wax portion of the non-ionically emulsified EVA copolymer wax having a drop point of 80 to 110° C.


The substrate provided in process step (1) can be a plastics or a metal substrate. Plastics substrates may have a precoating like a conductive primer layer, metal substrates may have a precoating like a conventional EDC primer layer and, optionally, also a conventional primer surfacer layer. Examples of substrates include in particular automotive bodies and body parts, which typically have a suitable precoating. Automotive bodies may in particular have a precoating consisting of a conventional EDC primer layer or of a conventional EDC primer layer plus a conventional primer surfacer layer. Automotive body metal parts may in particular have a precoating consisting of a conventional EDC primer layer or of a conventional EDC primer layer plus a conventional primer surfacer layer, whereas automotive body plastics parts may in particular have a precoating consisting of a conductive primer layer.
The substrate provided in process step (1) is provided with a base coat/clear coat two-layer coating having a light metallic color by carrying out the wet-on-wet coating process comprising process steps (2) to (4) in the course of which the base coat layer and the clear coat layer both are applied and jointly cured.
In process step (2) the (precoated) substrate is spray-coated with a waterborne base coat of the present invention only by electrostatically-assisted high-speed rotary atomization. It is possible that the electrostatically-assisted high-speed rotary atomization is performed in two spray passes, i.e. in two subsequent spray operations, each of which being performed by electrostatically-assisted high-speed rotary atomization. It is however preferred that the electrostatically-assisted high-speed rotary atomization of the waterborne base coat is performed in one single spray pass.
In any case, the process of the present invention comprises no application of the waterborne base coat by an application method other than electrostatically-assisted high-speed rotary atomization; there is no other step of application of the waterborne base coat than that of process step (2); in particular, there is no pneumatic spray-application of the waterborne base coat.
The waterborne base coat is applied in a total dry film thickness of, for example, 7 to 20 μm.
The applied base coat layer is preferably briefly flashed off before process step (3) is performed. The flash-off phase takes, for example, 30 seconds to 10 minutes at an air temperature of 20 to 80° C.
In process step (3), a clear coat composition is spray-applied on the not yet fully cured or even uncured base coat layer formed in process step (2). Application of the clear coat may be performed by any known spray-application method like, for example, pneumatic spray-application or electrostatically-assisted high-speed rotary atomization, the latter spray-application method being the preferred one. The clear coat composition is applied in a total dry film thickness of, for example, 30 to 60 μm.
All known clear coat compositions are in principle suitable. Usable clear coats are here both solvent-containing one-component (1 pack) or two-component (2 pack) clear coats and water-dilutable 1 pack or 2 pack clear coats.
After an optional, but preferred flash-off phase the applied base coat layer and the clear coat layer are jointly cured in process step (4). The joint curing is performed at an object temperature at or above the drop point of the wax portion of the non-ionically emulsified EVA copolymer wax having a drop point of 80 to 110° C. The object temperature is, for example, 80 to 160° C., in particular, 120 to 160° C., and the joint curing is carried out, for example, by baking.
EXAMPLES
Example 1
Preparation of an Aqueous Binder Latex
A reactor was charged with 688 pbw (parts by weight) of deionized water and 16 pbw of Rhodapex EST30 (anionic surfactant available from Rhodia; 30 wt. % in water). The water and surfactant charge was heated to 80° C. under nitrogen atmosphere and held at that temperature throughout the reaction. A first stirred monomer emulsion consisting of 45 pbw of Rhodapex EST30, 349 pbw of deionized water, 270 pbw of methyl methacrylate, 189 pbw of butyl acrylate, 175 pbw of styrene, 36 pbw of hydroxyethyl acrylate, 36 bpw of methacrylic acid and 7 pbw of allyl methacrylate was prepared separately. A solution of 3.2 pbw of ammonium peroxodisulfate (APS) in 100 pbw of deionized water was added to the reactor content and the first monomer emulsion was then added within 90 minutes to the reactor content. After all of the first monomer emulsion was in, the reactor content was held for an additional hour at 80° C., during which a second stirred monomer emulsion consisting of 15 pbw of Rhodapex EST30, 378 pbw of deionized water, 277 pbw of methyl methacrylate, 180 pbw of butyl acrylate, 175 pbw of styrene, 72 pbw of glycidyl methacrylate and 7 pbw of allyl methacrylate and a solution of 13 pbw of 2-amino-2-methyl-1-propanol (90wt. % in water) in 98 pbw of deionized water were separately prepared. The aqueous 2-amino-2-methyl-1-propanol solution was added slowly to the reaction mixture and then, a solution of 1.1 pbw of ammonium peroxodisulfate (APS) in 70 pbw of deionized water was added slowly to the reactor content. The second monomer emulsion was then added within 90 minutes to the reactor content. After the addition was complete, the reactor content was held at 80° C. for an additional hour. The aqueous binder latex obtained was then cooled to room temperature.
Example 2
Preparation of an Aqueous Polyurethane Binder Dispersion
1005 g of a straight-chain polyester (composed of adipic acid, isophthalic acid and hexanediol having a hydroxyl value of 102 mg KOH/g) were heated to 90° C. and 1.8 g of trimethylolpropane and 393 g of isophorone diisocyanate were added. The reaction was carried out at 90° C. until the NCO value was constant. After cooling to 60° C., a solution of 35.3 g of dimethylol propionic acid, 26.1 g triethylamine and 250 g N-ethylpyrrolidone was added. After heating to 80° C., the reaction temperature was maintained until the NCO value was constant. The batch was mixed with a molar amount, based on the molar NCO-content, of deionized water, and the solution was kept at 80° C., until no more NCO was detectable. The batch was then converted into an aqueous dispersion having a solids content of 35 wt. % by adding deionized water.
Examples 3a to 3d
Preparation of Waterborne Metallic Base Coats
Waterborne metallic base coats 3a to 3d were prepared by mixing the constituents listed in Table 1. Proportions are in pbw. Table 1 also shows colorimetric data (lightness L* according to CIEL*a*b*, DIN 6174 (October 2007)) of multi-layer coatings prepared with the waterborne base coats.








TABLE 1








Waterborne base coats










silver-metallic
grey-metallic












3a**)
3b*)
3c**)
3d*)





Constituents:






BE
2.5
2.5
5.5
5.5


Aluminum paste1)
15
15
12
12


NEP
1
1
1
1


Binder dispersion of Example 2
13
13
12
12


Deionized water
15
10
15
15


Aqueous binder latex of Example 1
10
10
11
11


Deionized water
15
10
15
10


Layered silicate composition2)
0
17
0
8


Maprenal ® MF 9003)
3
3
2
2


Cymel ® 3254)
2
2
2
2


Deionized water
12.4
8.9
11.9
10.9


Thickener5)
0
3
0
5


Aquatix ® 8421
5
0
5
0


DMEA, 10 wt. % solution in water
3.5
2
3.5
1.5


BuOH
2.6
2.6
2.2
2.2


Carbon Black Dispersion6)
0
0
1.9
1.9


L*7)
137
136
65
60





*)comparative example


**)according to the invention


BE, Butoxy ethanol


BuOH, n-Butanol


DMEA, Dimethylethanolamine


NEP, N-Ethyl pyrrolidone


1)Mixture of 50 pbw BE with 50 pbw Stapa Hydrolan ® IL 2156 from Eckart.


2)Mixture of 3 pbw Laponite ® RD from Rockwood Additives Ltd., 3 pbw polypropylene glycol 900 and 94 pbw of deionized water.


3)Melamine resin from Surface Specialties.


4)Melamine resin from Cytec.


5)Mixture of 33 pbw Viscalex HV 30 from Allied Colloids, 2.5 pbw DMEA and 64.5 pbw of deionized water.


6)Mixture of 15 pbw carbon black, 10 pbw of a nonionic surfactant, 22 pbw DMEA and 53 pbw deionized water.


7)The water-borne base coats were each applied by electrostatically-assisted high-speed rotary atomization in one single spray pass to steel test panels provided with a precoating consisting of EDC primer and primer surfacer in 12 μm dry film thickness. After flashing-off for 5 minutes at 20° C. and additional 5 minutes at 80° C. the test panels were each spray coated with a commercial two-component polyurethane clear coat in 40 μm dry film thickness and after flashing-off for 5 minutes at 20° C. baked for 20 minutes at 140° C. object temperature.


The L* values at an illumination angle of 45 degrees to the perpendicular and an observation angle of 15 degrees to the specular were measured with the instrument X-Rite MA 68 sold by the firm X-Rite Incorporated, Grandeville, Michigan, U.S.A. (illumination with standard illuminant D65).

## Claims

1. A waterborne base coat having a light metallic color and containing 0.5 to 2 wt.-% of poly(meth)acrylic acid thickener and 2 to 7 wt.-% of non-ionically emulsified EVA copolymer wax with a drop point of the wax portion of 80 to 110° C., the wt.-% in each case calculated as solids and relative to the solids content of the waterborne base coat.

2. The waterborne base coat of claim 1, wherein the light metallic color exhibits a lightness L* (according to CIEL*a*b*, DIN 6174), measured at an illumination angle of 45 degrees to the perpendicular and an observation angle of 15 degrees to the specular of 60 to 145 units.

3. The waterborne base coat of claim 1, wherein the light metallic color is a silver metallic color.

4. The waterborne base coat of claim 1, wherein the EVA copolymer wax having a drop point of 80 to 110° C. contains 6 to 14 wt.-% of copolymerized vinyl acetate.

5. The waterborne base coat of claim 1 containing a crosslinking agent selected from the group consisting of free polyisocyanates, blocked polyisocyanates, amino resins and any combinations thereof.

6. A process for the production of a base coat/clear coat two-layer coating having a light metallic color comprising the steps:
(1) providing a substrate to be provided with a base coat/clear coat two-layer coating having a light metallic color,
(2) spray-applying a waterborne base coat of any one of the preceding claims on the substrate only by electrostatically-assisted high speed rotary atomization to form the base coat layer,
(3) spray-applying a clear coat composition on the base coat layer formed in step (2) to form the clear coat layer, and
(4) jointly curing the base coat layer and the clear coat layer at an object temperature at or above the drop point of the wax portion of the non-ionically emulsified EVA copolymer wax having a drop point of 80 to 110° C.

7. The process of claim 6, wherein the substrate is selected from the group consisting of uncoated plastics substrates, precoated plastics substrates, uncoated metal substrates and precoated metal substrates.

8. The process of claim 6, wherein the substrate is selected from the group consisting of automotive bodies and body parts.

9. The process of any one of claims 6, wherein the electrostatically-assisted high-speed rotary atomization is performed in one single or in two spray passes.