# Patent

## Title
Method for preparing polyethylene with high melt strength

## Abstract

The present invention is a method for increasing the melt strength of a polyethylene resin comprising reacting the polyethylene resin with an alkoxy amine derivative corresponding to the formula:

(R1)(R2)N—O—R3 

    
    
        where R1 and R2 are each independently of one another, hydrogen, C4-C42 alkyl or C4-C42 aryl or substituted hydrocarbon groups comprising O and/or N, and where R1 and R2 may form a ring structure together; and where R3 is hydrogen, a hyrdrocarbon or a substituted hydrocarbon group comprising O and/or N. Preferred groups for R3 include —C1-C19alkyl; —C6-C10aryl; —C2-C19akenyl; —O—C1-C19alkyl; —O—C6-C10aryl; —NH—C1-C19alkyl; —NH—C6-C10aryl; —N—(C1-C19alkyl)2. R3 most preferably contains an acyl group.

## Background
BACKGROUND AND SUMMARY OF THE INVENTION
Polyethylene has desirable properties that have helped to make it the highest volume polymer manufactured. Polyethylene can be made in different processes in order to give different properties. Known families of polyethylene include high density polyethylene (HDPE), linear low density polyethylene (LLDPE), and low density polyethylene made using high pressure reactors (LDPE). Within these broad classes many variations exist resulting from different types of reactors (for example, solution, slurry or gas phase) or from the use of different catalysts (for example, Ziegler-Natta or constrained geometry catalysts). The desired application requires a careful balance of rheological properties which will lead a person of skill in the art to select one type of polyethylene over another. In many applications, such as blow-molding and blown film applications, melt strength of the polyethylene is a key parameter, frequently measured as elongational viscosity of the polymer.
The melt strength is a practical measurement that can predict material performance when submitted at elongational deformations. In melt processing good elongational viscosity is important to maintain stability during processes such as coating, blow film production, fiber spinning and foamed parts. The melt strength is related with a number of molecular entanglements on molten polymers and relaxation times of each molecular structure, which is basically dependant on overall molecular weight and number of branches over critical molecular weight.
Melt strength directly effects several processing parameters such as bubble stability and therefore thickness variation during blow film production; parison formation during blow molding process; sagging during profile extrusion; cells formation during foaming process; more stable thickness distribution during sheet/film thermoforming.
This property can be enhanced by using resins with higher molecular weight, but such resins will generally require more robust equipment and more energy use because they tend to generate higher extrusion pressure during the extrusion process. Therefore, properties must be balanced to provide an acceptable combination of physical properties and processability.
The use of highly branched polymers such as LDPE to increase melt strength or specific catalyst system that incorporates a high level of long-chain branching into the polyethylene are other alternatives to enhance material processability during extrusion. However, while some properties are improved, high levels of long-chain branching can hurt other properties. It would be desirable to be able to prepare polyethylene with excellent blow-molding properties with Ziegler-Natta catalyst systems while avoiding tradeoffs of other catalysts and high pressure process. For example, the poorer physical properties caused by long-chain branching and cost limitations of single-site catalysts are preferably avoided.
Currently, when increase melt strength is desired, the most common approach is to include peroxides to crosslink the polyethylene. For example, U.S. Pat. No. 5,486,575 improves the properties of a polyethylene resin prepared from a chromium catalyst by using an organic peroxide. U.S. Pat. Nos. 4,390,666 and 4,603,173 use peroxides to crosslink a polyethylene blend containing high and low molecular weight components. U.S. Pat. No. 6,706,822 uses peroxides with polyethylene having a broad molecular weight distribution to reduce melt swell. U.S. Pat. No. 5,486,575 uses peroxides with polyethylene prepared with chromium catalysts. While some properties can be improved by crosslinking with peroxides, there are issues with this approach. The radicals produced can interact deleteriously with other additives. It is difficult to predict the effect of crosslinking on rheological properties. Reported results vary significantly from resin to resin, even when the resins are produced using similar catalyst technologies. Peroxides add an extra component to the composition, and they require careful handling and storage, which adds to the cost. It would be desirable to improve properties without using peroxides.
The present invention is a new process for increasing the melt strength of polyethylene involving reacting molten polyethylene with an alkoxyamine derivative through regular extrusion processing. Accordingly, one aspect of the invention is a method for increasing the melt strength of a polyethylene resin comprising first selecting a polyethylene resin having a density, as determined according to ASTM D792, in the range of from 0.865 g/cm3 to 0.962 g/cm3, and a melt index, as determined according to ASTM D1238 (2.16 kg, 190° C.), in the range of from 0.01 g/10 min to 100 g/10 min and then reacting an alkoxy amine derivative with the polyethylene resin in an amount and under conditions sufficient to increase the melt strength of the polyethylene resin.
The present invention is a new process for increasing the elongational viscosity of polyethylene involving reacting molten polyethylene with an alkoxyamine derivative through regular extrusion processing. Accordingly, one aspect of the invention is a method for increasing the melt strength of a polyethylene resin comprising first selecting a polyethylene resin having a density, as determined according to ASTM D792, in the range of from 0.865 g/cm3 to 0.962 g/cm3, and a melt index, as determined according to ASTM D1238 (2.16 kg, 190° C.), in the range of from 0.01 g/10 min to 100 g/10 min and then reacting an alkoxy amine derivative with the polyethylene resin in an amount and under conditions sufficient to increase the elongational viscosity of the polyethylene resin.



BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a plot of melt strength versus stretching velocity with increasing additive concentration.



DETAILED DESCRIPTION OF THE INVENTION
In its broadest sense, the present invention is a method for increasing the melt strength of a polyethylene resin. Polyethylene resin includes all polymers or polymer blends which are derived at least 50% by weight from ethylene monomer units. This includes materials known in the art as high density polyethylene (HDPE), linear low density polyethylene (LLDPE), and low density polyethylene made using high pressure reactors (LDPE).
The polyethylene resin selected should have a density, as determined according to ASTM D792, in the range of from 0.865 g/cm3 to 0.962 g/cm3, more preferably from 0.905 g/cm3 to 0.957 g/cm3 and a melt index, as determined according to ASTM D1238 (2.16 kg, 190° C.), in the range of from 0.01 g/10 min to 100 g/10 min, more preferably 0.1 g/10 min to 15 g/10 min. Polyethylene with a melt index (I2) of 2.5 g/10 min or less may particularly benefit from this invention. Suitable polyethylene resins can be produced with conventional Ziegler Natta or Chromium catalysts but also with metallocene or single site catalysts. Such resins may have monomodal or multimodal molecular weight distributions.
Once the polyethylene resin is selected, it is reacted with an alkoxy amine derivative. For purposes of the present invention “alkoxy amine derivatives” includes nitroxide derivatives. The alkoxy amine derivative is added in an amount and under conditions sufficient to increase the melt strength of the polyethylene resin. The alkoxy amine derivatives correspond to the formula:

(R1)(R2)N—O—R3 

where R1 and R2 are each independently of one another, hydrogen, C4-C42 alkyl or C4-C42 aryl or substituted hydrocarbon groups comprising O and/or N, and where R1 and R2 may form a ring structure together; and where R3 is hydrogen, a hyrdrocarbon or a substituted hydrocarbon group comprising O and/or N. Preferred groups for R3 include —C1-C19alkyl; —C6-C10aryl; —C2-C19akenyl; —O—C1-C19alkenyl; —O—C1-C19aryl; —NH—C1-C19alkyl; —NH—C6-C10aryl; —N—(C1-C19alkyl)2. R3 most preferably contains an acyl group.
The preferred compound may form nitroxylradical (R1)(R2)N—O* or amynilradical (R1)(R2)N* after decomposition or thermolysis.
A particularly preferred species of alkoxy amine derivative is 9-(acetyloxy)-3,8,10-triethyl-7,8,10-trimethyl-1,5-dioxa-9-azaspiro[5.5]undec-3-yl]methyl octadecanoate which has the following chemical structure:




Examples of some preferred species for use in the present invention include the following:




In general hydroxyl amine esters are more preferred with one particularly favored hydroxyl amine ester being 9-(acetyloxy)-3,8,10-triethyl-7,8,10-trimethyl-1,5-dioxa-9-azaspiro[5.5]undec-3-yl]methyl octadecanoate.
The alkoxy amine derivatives are added in an amount sufficient to increase the melt strength and/or increase the elongational viscosity to the desired level. In general the alkoxy amine derivatives are added in an amount of from 1 to 1000 ppm of the polyethylene polymer by weight, more preferably from 40 to 800 ppm. In another embodiment, the alkoxy amine derivative is added in an amount of from 0.01% to 5% of the polyethylene polymer by weight.
The addition to the polyethylene polymer can be carried out in all customary mixing machines in which the polymer is melted and mixed with the additives. Suitable machines are known to those skilled in the art. They are predominantly mixers, kneaders and extruders.
The process is preferably carried out in an extruder by introducing the additive during processing. Particularly preferred processing machines are single-screw extruders, contra rotating and co rotating twin-screw extruders, planetary-gear extruders, ring extruders or cokneaders. It is also possible to use processing machines provided with at least one gas removal compartment to which a vacuum can be applied. Suitable extruders and kneaders are described, for example, in Handbuch der Kunststoftextrusion, VoL 1 Grundlagen, Editors F. Hensen, W. Knappe, H. Potente, 1989, pp. 3-7, ISBN.3-446-14339-4 (VoL 2 Extrusionsanlagen 1986, ISBN 3-446-14329-7). For example, the screw length can be 1-60 times the screw diameter, preferably 35-48 times the screw diameters. The rotational speed of the screw is preferably 10-600 rotations per minute (rpm), more preferably 25-300 rpm.
The maximum throughput is dependent on the screw diameter, the rotational speed and the driving force. The process of the present invention can also be carried out at a level lower than maximum throughput by varying the parameters mentioned or employing weighing machines delivering dosage amounts.
If a plurality of components is added, these can be premixed or added individually.
The polymers need to be subjected to an elevated temperature for a sufficient period of time, so that the desired degradation occurs. The temperature is generally above the softening point of the polymers. In a preferred embodiment of the process of the present invention, a temperature range lower than 280° C., particularly from about 160° C. to 280° C. is employed. In a particularly preferred process variant, the temperature range from about 200° C. to 270° C. is employed.
The period of time necessary for degradation can vary as a function of the temperature, the amount of material to be degraded and the type of, for example, extruder used. It is usually from about 10 seconds to 20 minutes, in particular from 20 seconds to 10 minutes.
The alkoxy amine derivative can advantageously be added to the mixing device by use of a masterbatch. As will be appreciated by those of ordinary skill in the art, the carrier resin for the masterbatch should be chosen to be compatible with the resin to be modified. LDPE High pressure low density polyethylene polymers (referred to in the industry as “LDPE”) were unexpectedly found to be the preferred carrier due to the lower reactivity as evidenced by little variation of the extrusion pressure during masterbatch production.
Melt strength was determined using a Göttfert Rheotens apparatus. The air gap—distance from the die exit to the take-up wheels—is set to 100 mm, and the wheels acceleration is 2.4 mm/s2. The melt is produced by a Göttfert Rheotester 2000 at 190° C. unless otherwise specified, equipped with a 12 mm barrel and a die with flat entrance (L=30 mm and ID=2 mm) at a piston speed of 0.265 mm/s. The Rheotens Melt strength values, which are reported in centi-Newtons (cN), correspond to the force experienced by the wheels at the maximum velocity, that is, right before rupture of the sample.
Resin modified according to the methods of the present invention will exhibit an increase in melt strength of at least 25%, preferably in the range of from 30 to 50% as compared to the same or substantially similar resin which has not been reacted with the alkoxy amine derivative. Similar performance improvement will also be seen with respect to elongational viscosity
With the increase in melt strength and/or elongational viscosity, resins made according to the present invention are particularly well suited for fabricated articles such as films, sheets, pipes or blow molded articles.
EXAMPLES
The four examples described below have a similar molecular weight, with different concentrations of an alkoxy amine derivative additive. The specific additive used is 9-(acetyloxy)-3,8,10-triethyl-7,8,10-trimethyl-1,5-dioxa-9-azaspiro[5.5]undec-3-yl]methyl octadecanoate, which was added as an LDPE masterbatch having less than 4% of the additive (note that the ppm levels reported below refer to the active ingredient only and not the entire masterbatch). The melt strength of each of these examples is measured using Göttfert Rheotester 2000 at 190° C.
FIG. 1 shows the melt strength curve versus stretching velocity with increasing additive concentration. The incorporation of the additive changes the behavior of Resin B, increasing the force need to stretch the molten polymer.
Resin Description:


    Resin A is a Ziegler-Natta catalyzed polyethylene resin made in a solution process having melt index of 0.5 g/10 min (at 190° C., 2.16 kg ASTM D-1238) and a density 0.921 g/cm3 (ASTM D792)
    Resin B is a Ziegler-Natta catalyzed polyethylene resin made in a solution process having a melt index of 1.0 g/10 min (at 190° C., 2.16 kg ASTM D-1238_and a density 0.920 g/cm3 (ASTM D792)
    Resin C is a Ziegler-Natta catalyzed polyethylene made in a slurry process having a melt index of 0.27 g/10 min (at 190° C., 2.16 kg ASTM D-1238) and a density of 0.956 g/cm3 (ASTM D792).

















Density g/cm3
Conventional GPC
Melt Strength













Samples
(ASTM D792)
Mn
Mw
Mz
Mw/Mn
(cN)
















Resin A
0.921
27,530
125,820
378,600
4.57
5.8


Resin B (no
0.920
25,860
114,470
369,300
4.43
3.9


additive)


Resin B +
0.920
26,830
115,690
353,900
4.31
8.1


200 ppm


additive


Resin B +
0.920
25,470
117,120
359,600
4.6
11.2


400 ppm


additive


Resin C
0.956
11.730
183.070
1052.000
15.61
7.7









From the above examples, it is demonstrated that addition of the additive results in changes to the molecular weight distribution and significantly increases melt strength, at levels compared to blow molding resins produced via slurry polymerization (Resin C), without significant increasing molecular weight. It can also be seen that the addition of the additive results in resins having higher melt strength than resins with higher molecular weight that were made using same polymerization technology (Resin A).

## Claims

1. A method for increasing the melt strength of a polyethylene resin comprising the steps of:
a. selecting a polyethylene resin having a density, as determined according to ASTM D792, in the range of from 0.865 g/cm3 to 0.962 g/cm3, and a melt index, as determined according to ASTM D1238 (2.16 kg, 190° C.), in the range of from 0.01 g/10min to 100 g/10 min, wherein the polyethylene resin is selected from the group consisting of high density polyethylene (HDPE), linear low density polyethylene (LLDPE) and blends thereof;
b. reacting an alkoxy amine derivative with the polyethylene resin in an amount and under conditions sufficient to increase the melt strength of the polyethylene resin, wherein the alkoxy amine derivative is added to the polyethylene resin as a masterbatch comprising the alkoxy amine derivative along with a carrier resin comprising LDPE.

2. The method of claim 1 wherein the alkoxy amine derivative corresponds to the formula:


(R1)(R2)N—O—R3 

where R1 and R2 are each independently of one another, hydrogen, C4-C42 alkyl or C4-C42 aryl or substituted hydrocarbon groups comprising O and/or N, and where R1 and R2 may form a ring structure together; and R3 is hydrogen, a hydrocarbon or a substituted hydrocarbon group comprising O and/or N.

3. The method of claim 1 wherein the alkoxy amine derivative is a hydroxylamine ester.

4. The method of claim 3 wherein the hydroxyl amine ester is hydroxyl amine ester being 9-(acetyloxy)-3,8,10-triethyl-7,8,10-trimethyl-1,5-dioxa-9-azaspiro[5.5]undec-3-yl]methyl octadecanoate.

5. The method of claim 1 wherein the alkoxy amine derivative is reacted with the polyethylene resin in a reactive extrusion process.

6. The method of claim 1 wherein the melt strength is increased by at least 25% compared to a substantially similar polyethylene resin which has not been reacted with an alkoxy amine derivative.

7. The method of claim 1 wherein the alkoxy amine derivative is added in an amount of from 0.01% to 5% of the polyethylene polymer by weight.

8. The method of claim 1 wherein the polyethylene resin has a melt index less than 2.5 g/10 min.

9. The method of claim 1 wherein the alkoxy amine derivative is added in an amount of from 0.0001% to 0.1% of the polyethylene polymer by weight.