# Patent

## Title
Bis(sulfonyl)alkanol-containing polythioethers, methods of synthesis, and compositions thereof

## Abstract

Bis(sulfonyl)alkanol-containing polythioethers, compositions containing bis(sulfonyl)alkanol-containing polythioethers, methods of synthesizing bis(sulfonyl)alkanol-containing polythioethers and the use of bis(sulfonyl)alkanol-containing polythioethers in aerospace sealant applications are disclosed. The bis(sulfonyl)alkanol-containing polythioethers have bis(sulfonyl)alkanol groups incorporated into the backbone of the polythioether. Cured sealant compositions comprising the bis(sulfonyl)alkanol-containing polythioethers exhibit enhanced properties suitable for aerospace sealant applications.

## Background
FIELD
The present disclosure relates to bis(sulfonyl)alkanol-containing polythioethers, compositions containing bis(sulfonyl)alkanol-containing polythioethers, methods of synthesizing bis(sulfonyl)alkanol-containing polythioethers, and uses of bis(sulfonyl)alkanol-containing polythioethers in aerospace sealant applications. The bis(sulfonyl)alkanol-containing polythioethers include bis(sulfonyl)alkanol groups incorporated into the backbone of a polythioether.
BACKGROUND
Sealants useful in aerospace and other applications must satisfy demanding mechanical, chemical, and environmental requirements. For example, it is desirable that aerospace sealants function over a temperature range such as from about −67° F. to about 360° F. Michael addition curing chemistries employing divinyl sulfone and sulfur-containing polymers have been shown to produce aerospace sealants having faster cure rates and enhanced performance including fuel resistance and thermal resistance. For example, in the systems disclosed in U.S. application Ser. No. 13/529,237, filed on Jun. 21, 2012, sulfur-containing polymer adducts such as polythioether adducts containing terminal Michael acceptor groups such as vinyl sulfone groups are reacted with a curing agent such as a thiol-terminated sulfur-containing polymer to form a cured composition. Application of Michael addition curing chemistries to sulfur-containing polymers not only results in cured sealants with faster cure rates and enhanced performance including fuel resistance and thermal resistance, but also provides a sealant with improved physical properties such as elongation.
Sulfone-containing polythioethers having one or more sulfone groups incorporated into the backbone of the polythioether are disclosed in U.S. application Ser. No. 13/883,827 filed on Mar. 15, 2013, which is incorporated by reference in its entirety.
Sulfur-containing polymers having improved adhesion to metal surfaces and that meet other performance requirements for use in aerospace and other applications are desired.
SUMMARY
In a first aspect, bis(sulfonyl)alkanol-containing polythioether comprising a moiety of Formula (10) are provided:

—S(O)2—R10—CH(—OH)—R10—S(O)2—  (10)

wherein each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.

In a second aspect, thiol-terminated bis(sulfonyl)alkanol-containing polythioethers are provided comprising the reaction product of reactants comprising:
(a) a thiol-terminated polythioether comprising a thiol-terminated polythioether of Formula (4), a thiol-terminated polythioether of Formula (4a), or a combination thereof:

HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)

{HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—V′—}zB  (4a)

wherein:

    
    
        each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 independently comprises hydrogen or methyl; and
            each X independently comprises —O—, —S—, or —NR5—, wherein R5 is selected from hydrogen and methyl;
        
        
        each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60;
        p is an integer from 2 to 6; and
        B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
        
            z is an integer from 3 to 6; and
            each V is a group comprising a terminal group reactive with a terminal thiol group; and
        
        
        each —V′— is derived from the reaction of —V with a thiol; and
    
    


(b) a bis(sulfonyl)alkanol of Formula (5):

R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)

wherein

    
    
        each R8 is independently selected from a moiety comprising a terminal group reactive with a terminal thiol group; and
        each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.
    
    


In a third aspect, thiol-terminated bis(sulfonyl)alkanol-containing polythioether prepolymers are provided comprising the reaction product of reactants comprising:
(a) a thiol-terminated bis(sulfonyl)alkanol-containing polythioether comprising thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a), or a combination thereof:

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)

wherein:

N is an integer from 1 to 10;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

    
    
        wherein:
        
            each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
            
                s is an integer from 2 to 6;
                q is an integer from 1 to 5;
                r is an integer from 2 to 10;
                each R3 independently comprises hydrogen or methyl; and
                each X independently comprises —O—, —S—, or —NR5—, wherein R5 is selected from hydrogen and methyl;
            
            
            each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
            m is an integer from 0 to 50;
            n is an integer from 1 to 60; and
            p is an integer from 2 to 6;
        
        
    
    


B represents a core of a z-valent, alkenyl-terminated polyfunctionalizing agent B(—V)z wherein:

    
    
        z is an integer from 3 to 6; and
        each V is a group comprising a terminal alkenyl group; and
    
    


each —V′— is derived from the reaction of —V with a thiol; and
(b) a polyalkenyl compound.
In a fourth aspect, methods of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) are provided, comprising reacting (N+1) moles of a thiol-terminated polythioether of Formula (4) with (N) moles of a bis(sulfonyl)alkanol of Formula (5):

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)

R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)

wherein:

N is an integer from 1 to 10;
each R8 is independently selected from a moiety comprising a terminal group reactive with a terminal thiol group;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 independently comprises hydrogen or methyl; and
            each X independently comprises —O—, —S—, or —NR5—, wherein R5 comprises hydrogen or methyl; and
        
        
        each R2 is independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6.
    
    


In a fifth aspect, methods of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a) are provided comprising reacting (z) moles of a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) with one (1) mole of a polyfunctionalizing agent of Formula (7):

{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

B{V}z  (7)

wherein:

each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

    
    
        wherein:
        
            each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
            
                s is an integer from 2 to 6;
                q is an integer from 1 to 5;
                r is an integer from 2 to 10;
                each R3 independently comprises hydrogen or methyl; and
                each X independently comprises —O—, —S—, and —NR5—, wherein R5 comprises hydrogen or methyl;
            
            
            each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
            m is an integer from 0 to 50;
            n is an integer from 1 to 60; and
            p is an integer from 2 to 6;
        
        
    
    


B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:

    
    
        z is an integer from 3 to 6; and
        each V is a group comprising a terminal group reactive with a thiol group; and
    
    


each —V′— is derived from the reaction of —V with a thiol.
In a sixth aspect, compositions comprising (a) a bis(sulfonyl)alkanol-containing polythioether provided by the present disclosure, and (b) a curing agent having two or more terminal groups that are reactive with the terminal groups of the bis(sulfonyl)alkanol-containing polythioether are provided.


DETAILED DESCRIPTION
Definitions
For purposes of the following description, it is to be understood that embodiments provided by the present disclosure may assume various alternative variations and step sequences, except where expressly specified to the contrary. Moreover, other than in the examples, or where otherwise indicated, all numbers expressing, for example, quantities of ingredients used in the specification and claims are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification and attached claims are approximations that may vary depending upon the desired properties to be obtained. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard variation found in their respective testing measurements.
Also, it should be understood that any numerical range recited herein is intended to include all sub-ranges encompassed therein. For example, a range of “1 to 10” is intended to include all sub-ranges between (and including) the recited minimum value of about 1 and the recited maximum value of about 10, that is, having a minimum value equal to or greater than about 1 and a maximum value of equal to or less than about 10. Also, in this application, the use of “or” means “and/or” unless specifically stated otherwise, even though “and/or” may be explicitly used in certain instances.
A dash (“-”) that is not between two letters or symbols is used to indicate a point of bonding for a substituent or between two atoms. For example, —CONH2 is bonded to another chemical moiety through the carbon atom.
“Alkanearene” refers to a hydrocarbon group having one or more aryl and/or arenediyl groups and one or more alkyl and/or alkanediyl groups, where aryl, arenediyl, alkyl, and alkanediyl are defined herein. In certain embodiments, each aryl and/or arenediyl group(s) is C6-12, C6-10, and in certain embodiments, phenyl or benzenediyl. In certain embodiments, each alkyl and/or alkanediyl group(s) is C1-6, C1-4, C1-3, and in certain embodiments, methyl, methanediyl, ethyl, or ethane-1,2-diyl. In certain embodiments, the alkanearene group is C4-18 alkanearene, C4-16 alkanearene, C4-12 alkanearene, C4-8 alkanearene, C6-12 alkanearene, C6-10 alkanearene, and in certain embodiments, C6-9 alkanearene. Examples of alkanearene groups include diphenyl methane.
“Alkanearenediyl” refers to a diradical of an alkanearene group. In certain embodiments, the alkanearenediyl group is C4-18 alkanearenediyl, C4-16 alkanearenediyl, C4-12 alkanearenediyl, C4-8 alkanearenediyl, C6-12 alkanearenediyl, C6-10 alkanearenediyl, and in certain embodiments, C6-9 alkanearenediyl. Examples of alkanearenediyl groups include diphenyl methane-4,4′-diyl.
“Alkanediyl” refers to a diradical of a saturated, branched or straight-chain, acyclic hydrocarbon group, having, for example, from 1 to 18 carbon atoms (C1-18), from 1 to 14 carbon atoms (C1-14), from 1 to 6 carbon atoms (C1-6), from 1 to 4 carbon atoms (C1-4), or from 1 to 3 hydrocarbon atoms (C1-3). It will be appreciated that a branched alkanediyl has a minimum of three carbon atoms. In certain embodiments, the alkanediyl is C2-14 alkanediyl, C2-10 alkanediyl, C2-8 alkanediyl, C2-6 alkanediyl, C2-4 alkanediyl, and in certain embodiments, C2-3 alkanediyl. Examples of alkanediyl groups include methane-diyl (—CH2—), ethane-1,2-diyl (—CH2CH2—), propane-1,3-diyl and iso-propane-1,2-diyl (e.g., —CH2CH2CH2— and —CH(CH3)CH2—), butane-1,4-diyl (—CH2CH2CH2CH2—), pentane-1,5-diyl (—CH2CH2CH2CH2CH2—), hexane-1,6-diyl (—CH2CH2CH2CH2CH2CH2—), heptane-1,7-diyl, octane-1,8-diyl, nonane-1,9-diyl, decane-1,10-diyl, dodecane-1,12-diyl, and the like.
“Alkanecycloalkane” refers to a saturated hydrocarbon group having one or more cycloalkyl and/or cycloalkanediyl groups and one or more alkyl and/or alkanediyl groups, where cycloalkyl, cycloalkanediyl, alkyl, and alkanediyl are defined herein. In certain embodiments, each cycloalkyl and/or cycloalkanediyl group(s) is C3-6, C5-6, and in certain embodiments, cyclohexyl or cyclohexanediyl. In certain embodiments, each alkyl and/or alkanediyl group(s) is C1-6, C1-4, C1-3, and in certain embodiments, methyl, methanediyl, ethyl, or ethane-1,2-diyl. In certain embodiments, the alkanecycloalkane group is C4-18 alkanecycloalkane, C4-16 alkanecycloalkane, C4-12 alkanecycloalkane, C4-8 alkanecycloalkane, C6-12 alkanecycloalkane, C6-10 alkanecycloalkane, and in certain embodiments, C6-9 alkanecycloalkane. Examples of alkanecycloalkane groups include 1,1,3,3-tetramethylcyclohexane and cyclohexylmethane.
“Alkanecycloalkanediyl” refers to a diradical of an alkanecycloalkane group. In certain embodiments, the alkanecycloalkanediyl group is C4-18 alkanecycloalkanediyl, C4-16 alkanecycloalkanediyl, C4-12 alkanecycloalkanediyl, C4-8 alkanecycloalkanediyl, C6-12 alkanecycloalkanediyl, C6-10 alkanecycloalkanediyl, and in certain embodiments, C6-9 alkanecycloalkanediyl. Examples of alkanecycloalkanediyl groups include 1,1,3,3-tetramethylcyclohexane-1,5-diyl and cyclohexylmethane-4,4′-diyl.
“Alkenyl” group refers to a group having the structure —CR═CR2 where the alkenyl group is a terminal group and is bonded to a larger molecule. In such embodiments, each R may be selected from, for example, hydrogen and C1-3 alkyl. In certain embodiments, each R is hydrogen and an alkenyl group has the structure —CH═CH2.
“Alkoxy” refers to a —OR group where R is alkyl as defined herein. Examples of alkoxy groups include methoxy, ethoxy, n-propoxy, isopropoxy, and n-butoxy. In certain embodiments, the alkoxy group is C1-8 alkoxy, C1-6 alkoxy, C1-4 alkoxy, and in certain embodiments, C1-3 alkoxy.
“Alkyl” refers to a monoradical of a saturated, branched or straight-chain, acyclic hydrocarbon group having, for example, from 1 to 20 carbon atoms, from 1 to 10 carbon atoms, from 1 to 6 carbon atoms, from 1 to 4 carbon atoms, or from 1 to 3 carbon atoms. It will be appreciated that a branched alkyl has a minimum of three carbon atoms. In certain embodiments, the alkyl group is C1-6 alkyl, C1-4 alkyl, and in certain embodiments, C1-3 alkyl. Examples of alkyl groups include methyl, ethyl, n-propyl, iso-propyl, n-butyl, iso-butyl, tert-butyl, n-hexyl, n-decyl, tetradecyl, and the like. In certain embodiments, the alkyl group is C1-6 alkyl, C1-4 alkyl, and in certain embodiments, C1-3 alkyl. It will be appreciated that a branched alkyl has at least three carbon atoms.
A “bis(sulfonyl)alkanol group” refers to a group having the general formula:

—S(O)2—R10—CH(—OH)—R10—S(O)2—

where each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, where the one or more substituent groups is —OH. In certain embodiments, a bis(sulfonyl)alkanol group has the structure —CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH2—CH2— and in certain embodiments, the structure, —R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9—where each R8 comprises a terminal alkenyl group; and each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein the one or more substituent groups is —OH.

In certain embodiments, a “bis(sulfonyl)alkanol group” can be a monovalent bis(sulfonyl)alkanol group or a divalent bis(sulfonyl)alkanol group. In certain embodiments, a monovalent bis(sulfonyl)alkanol can be a terminal bis(sulfonyl)alkanol group such as a “1-(ethylenesulfonyl)-n-(vinylsulfonyl)alkanol group.” A terminal bis(sulfonyl)alkanol group can be derived from the reaction of a bis(sulfonyl)alkanol and can have a terminal moiety with the general structure —R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R8 where R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with a compound having a group reactive with the bis(sulfonyl)alkanol; each R10 is independently selected from C1-3 alkanediyl, and substituted C1-3 alkanediyl, wherein the one or more substituent groups is —OH. In certain embodiments, R8 is —CH═CH2. In certain embodiments, a terminal bis(sulfonyl)alkanol group is a 1-(ethylenesulfonyl)-n-(vinylsulfonyl)alkanol group such as 1-(ethylenesulfonyl)-3-(vinylsulfonyl)propan-2-ol, i.e., —CH2—CH2—S(O)2—CH2—CH(—OH)—CH2—S(O)2—CH═CH2. In certain embodiments, a terminal bis(sulfonyl)alkanol group has the structure —CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2.
In certain embodiments, a bis(sulfonyl)alkanol group can also be divalent such as when the group is incorporated into the backbone of a prepolymer such as the polythioethers disclosed herein. In certain embodiments, a divalent bis(sulfonyl)alkanol group can have the general structure —R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9—; in certain embodiments, —CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH2—CH2—, in certain embodiments, —R9—S(O)2—CH2—CH(—OH)—CH2—S(O)2—R9—, and in certain embodiments, —CH2—CH2—S(O)2—CH2—CH(—OH)—CH2—S(O)2—CH2—CH2—, where R9 and R10 are as defined herein. In certain embodiments of a bis(sulfonyl)alkanol, each R8 is an alkenyl group, each R9 is an ethane-diyl group and/or each R10 is methane-diyl.
A “bis(sulfonyl)alkanol” refers to a compound of the general formula R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8 where each R8 is a moiety having a terminal reactive group; and each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein the one or more substituent groups is —OH. In certain embodiments, each R8 comprises a terminal group reactive with a thiol group such as, for example, an alkenyl group, an epoxy group, or a Michael acceptor group. In certain embodiments, a bis(sulfonyl)alkanol may be a bis(vinylsulfonyl)alkanol comprising terminal alkenyl groups. In certain embodiments a bis(sulfonyl)alkanol may be a bis(vinylsulfonyl)alkanol in which R8 comprises a terminal alkenyl group, such as a compound having the formula CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2. In certain embodiments, a bis(vinylsulfonyl)alkanol is 1,3-bis(vinylsulfonyl)-2-propanol. In certain embodiments, a bis(sulfonyl)alkanol can be prepared by reacting a bis(vinylsulfonyl)alkanol with a compound having a reactive terminal functional group and a terminal group reactive with the terminal alkenyl groups of the bis(vinylsulfonyl)alkanol such as a thiol group or an epoxy group. In such embodiments, the bis(sulfonyl)alkanol can have the structure R8′—CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH2—CH2—R8′ where each R8′ is a moiety derived from the reaction of the compound with the terminal alkenyl groups of the bis(vinylsulfonyl)alkanol.
A “bis(sulfonyl)alkanol-containing” polymer, prepolymer, or adduct refers to polymer, prepolymer, or adduct in which one or more divalent bis(sulfonyl)alkanol groups are incorporated into the backbone of the polymer, prepolymer, or adduct.
A divalent bis(sulfonyl)alkanol group can be incorporated in a pre polymer by reacting, for example, in a suitable ratio, a polythiol monomer or prepolymer of Formula A with a bis(sulfonyl)alkanol of Formula B:

R(—SH)w  (A)

R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (B)

where R is an organic moiety, w is an integer of at least 2 and each R8 comprises a terminal group that is reactive with a thiol group such as, for example, an alkylene group, and epoxy group, or a group comprising a saturated carbon bearing a leaving group that are well suited for nucleophilic substitution such as, for example, —Cl, —Br, —I, —OSO2CH3 (mesylate), —OSO2—C6H4—CH3 (tosylate), etc. In certain embodiments, a bis(sulfonyl)alkanol of Formula B may be a bis(vinylsulfonyl)alkanol having the formula

CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2 

where each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein the one or more substituent groups is —OH. In certain embodiments, a bis(sulfonyl)alkanol may be 1,3-bis(vinylsulfonyl)-2-propanol. Alternatively, a bis(sulfonyl)alkanol group can be incorporated into a prepolymer backbone by reacting, in a suitable ratio, a thiol-capped bis(sulfonyl)alkanol of Formula C with a reactant of Formula D:

HS—R—S(O)2—R10—CH(—OH)—R10—S(O)2—R—SH  (C)

R′′—R—R′′  (D)

where each R is a divalent moiety, each R10 is as defined herein, and each R′′ comprises a terminal group that is reactive with a thiol group such as, for example, an alkenyl group, an epoxy group, or a group consisting of a saturated carbon bearing a leaving group that are well known for nucleophilic substitution such as, for example, —Cl, —Br, —I, —OSO2CH3 (mesylate), —OSO2—C6H4—CH3 (tosylate), etc.

By choosing the appropriate ratio of the reactants of Formula A and Formula B, or Formula C and Formula D, one or more bis(sulfonyl)alkanol groups can be incorporated into a prepolymer as either a chain segment, as part of a terminal bearing a reactive group, or both. For example, bis(vinylsulfonyl)alkanol can be used to introduce one or more 1,n-bis(ethylenesulfonyl)alkanol groups into the backbone of a prepolymer chain, one or more terminal 1-(ethylenesulfonyl)-n-(vinylsulfonyl)alkanol groups, or both.
In certain embodiments, bis(vinylsulfonyl)-2-propanol can be reacted with thiol-capped monomers/polymers to incorporate 1,3-bis(ethylenesulfonyl)-2-propanol groups into the polymer chain.
In certain embodiments, bis(vinylsulfonyl)-2-propanol can be reacted with thiol-capped monomers/polymers to provide 1-(ethylenesulfonyl)-3-(vinylsulfonyl)-2-propanol terminal groups, where the terminal alkenyl group is a well-recognized Michael acceptor.
A moiety derived from the reaction of a bis(sulfonyl)alkanol with a thiol group refers to the reaction product a thiol group and a moiety containing a terminal group reactive with the thiol group. Examples of terminal groups reactive with thiol groups include epoxy groups, ethylene groups, and Michael acceptor groups. In certain embodiments, a moiety derived from the reaction of a bis(sulfonyl)alkanol with a thiol group has the structure: —CH2—CH2—R—, —CH(—OH)—CH2—R—, —CH2—CH(—OH)—R—, or —CH2—CH2—SO2—R—, where R refers to a covalent bond or an organic moiety bonded to a sulfonyl group.
A moiety derived from the reaction of a bis(sulfonyl)alkanol with a thiol group also refers to a moiety R9, which is derived from the reaction of group R8 with a thiol group, where R8 comprises a terminal group reactive with a thiol group.
In certain embodiments, R8 is derived from the reaction of a bis(sulfonyl)alkanol with a compound having a terminal group reactive with a thiol group and a group reactive with a bis(sulfonyl)alkanol. In certain embodiments R8 is derived from the reaction of a bis(ethylenesulfonyl)alkanol with a compound having a terminal group reactive with a thiol group and a group reactive with an ethylene group. In such embodiment, R9 may have the structure: —CH2—CH2—R′—CH2—CH2—, —CH(—OH)—CH2—R′—CH2—CH2—, —CH2—CH(—OH)—R′—CH2—CH2—, or —CH2—CH2—SO2—R′—CH2—CH2—, where R′ is an organic moiety derived from the reaction of the compound used to cap the bis(ethylenesulfonyl)alkanol with a functional group such as an ethylene group, an epoxy group, or a Michael acceptor group.
In certain embodiments, R9 is selected from C2-10 alkanediyl, substituted C2-10 alkanediyl, C2-10 heteroalkanediyl, substituted C2-10 heteroalkanediyl, C4-14 alkanecycloalkanediyl, substituted C4-14 alkanecycloalkanediyl, C4-14 heteroalkanecycloalkanediyl, substituted C4-14 heteroalkanecycloalkanediyl, C4-14 alkanearenediyl, substituted C4-14 alkanearenediyl, C4-14 heteroalkanearenediyl, and substituted C4-14 heteroalkanearenediyl. In certain embodiments, R9 is ethane-diyl.
In certain embodiments, R8 is selected from C2-10 alkyl, substituted C2-10 alkyl, C2-10 heteroalkyl, substituted C2-10 heteroalkyl, C4-14 alkanecycloalkyl, substituted C4-14 alkanecycloalkyl, C4-14 heteroalkanecycloalkyl, substituted C4-14 heteroalkanecycloalkyl, C4-14 alkanearyl, substituted C4-14 alkanearyl, C4-14 heteroalkanearyl, and substituted C4-14 heteroalkanearyl. In certain embodiments, R8 is ethylene, i.e., —CH═CH2.
“Cycloalkanediyl” refers to a diradical saturated monocyclic or polycyclic hydrocarbon group. In certain embodiments, the cycloalkanediyl group is C3-12 cycloalkanediyl, C3-8 cycloalkanediyl, C3-6 cycloalkanediyl, and in certain embodiments, C5-6 cycloalkanediyl. Examples of cycloalkanediyl groups include cyclohexane-1,4-diyl, cyclohexane-1,3-diyl, and cyclohexane-1,2-diyl.
“Cycloalkyl” refers to a saturated monocyclic or polycyclic hydrocarbon monoradical group. In certain embodiments, the cycloalkyl group is C3-12 cycloalkyl, C3-8 cycloalkyl, C3-6 cycloalkyl, and in certain embodiments, C5-6 cycloalkyl.
“Heteroalkanediyl” refers to an alkanediyl group in which one or more of the carbon atoms are replaced with a heteroatom, such as N, O, S, or P. In certain embodiments of heteroalkanediyl, a heteroatom is selected from N and O.
“Heteroalkanearenediyl” refers to an alkanearenediyl group in which one or more of the carbon atoms are replaced with a heteroatom, such as N, O, S, or P. In certain embodiments of heteroalkanearenediyl, the heteroatom is selected from N and O.
“Heterocycloalkanediyl” refers to a cycloalkanediyl group in which one or more of the carbon atoms are replaced with a heteroatom, such as N, O, S, or P. In certain embodiments of heterocycloalkanediyl, the heteroatom is selected from N and O. “Michael acceptor” refers to substituted alkene/alkyne compounds in which at least one alkene/alkyne group is directly attached to one or more electron-withdrawing group such as carbonyl (—CO), nitro (—NO2), nitrile (—CN), alkoxycarbonyl (—COOR), phosphonate (—PO(OR)2), trifluoromethyl (—CF3), sulfonyl (—SO2—), trifluormethanesulfonyl (—SO2CF3), p-toluenesulfonyl (—SO2—C6H4—CH3), etc. Types of compounds that function as Michael acceptor are vinyl ketones, quinones, nitroalkenes, acrylonitriles, acrylates, methacrylates, cyanoacrylates, acrylamides, maleimides, dialkyl vinylphosphonate and vinylsulfones. Other examples of Michael acceptors are disclosed in Mather et al., Prog. Polym. Sci. 2006, 31, 487-531. Michael acceptor compounds having more than one Michael acceptor group are also well known. Examples include diacrylates such as ethylene glycol diacrylate and diethylene glycol diacrylate, dimethacrylates such as ethylene glycol methacrylate and diethylene glycol methacrylate, bismaleimides such as N,N′-(1,3-phenylene)dimaleimide and 1,1′-(methylenedi-4,1-phenylene)bismaleimide, vinylsulfones such as divinyl sulfone and 1,3-bis(vinylsulfonyl)-2-propanol, etc. In certain embodiments, a Michael acceptor group has the structure of Formula (14a) or Formula (14b):

—CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2  (14a)

—CH2—CH2—S(O)2—CH2—CH(—OH)—CH2—S(O)2—CH═CH2  (14b)

where each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein the one or more substituent groups is —OH.

A “Michael acceptor compound” refers to a compound comprising at least one terminal Michael acceptor group. In certain embodiments, a Michael acceptor compound is divinyl sulfone, and a Michael acceptor group is vinylsulfonyl, i.e., —S(O)2—CH═CH2. In certain embodiments, a Michael acceptor compound is a bis(vinylsulfonyl)alkanol, and a Michael acceptor group is 1-(ethylenesulfonyl)-n-(vinylsulfonyl)alkanol (—CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2), and in certain embodiments, 1-(ethylenesulfonyl)-3-(vinylsulfonyl)propan-2-ol (—CH2—CH2—S(O)2—CH2—CH(—OH)—CH2—S(O)2—CH═CH2).
A “polyalkoxysilyl group” refers to a group having the formula:

—Si(—R3)p(—OR3)3-p 

where p is selected from 0, 1, and 2; and each R3 is independently selected from C1-4 alkyl. In certain embodiments of a polyalkoxysilyl group, p is 0, p is 1, and in certain embodiments, p is 2. In certain embodiments of a polyalkoxysilyl group, each R3 is independently selected from ethyl and methyl. In certain embodiments of a polyalkoxysilyl group, each R3 is ethyl, and in certain embodiments, each R3 is methyl. In certain embodiments of a polyalkoxysilyl group, the group is selected from —Si(—OCH2CH3)3, —Si(—OCH3)3, —Si(—CH3)(—OCH3)2, —Si(—CH3)2(—OCH3), —Si(—CH3)(—OCH2CH3)2, —Si(—CH3)2(—OCH2CH3), —Si(—CH2CH3)(—OCH3), and —Si(—CH2CH3)2(—OCH3).

“Substituted” refers to a group in which one or more hydrogen atoms are each independently replaced with the same or different substituent(s). In certain embodiments, a substituent is selected from halogen, —S(O)2OH, —S(O)2, —SH, —SR where R is C1-6 alkyl, —COOH, —NO2, —NR2 where each R is independently selected from hydrogen and C1-3 alkyl, —CN, ═O, C1-6 alkyl, —CF3, —OH, phenyl, C2-6 heteroalkyl, C5-6 heteroaryl, C1-6 alkoxy, and —COR where R is C1-6 alkyl. In certain embodiments, a substituent is chosen from —OH, —NH2, and C1-3 alkyl.
As used herein, “polymer” refers to oligomers, homopolymers, and copolymers. Unless stated otherwise, molecular weights are number average molecular weights for polymeric materials indicated as “Mn” as determined, for example, by gel permeation chromatography using a polystyrene standard in an art-recognized manner.
Reference is now made to certain embodiments of bis(sulfonyl)alkanol-containing polythioethers, compositions thereof, and methods of synthesis. The disclosed embodiments are not intended to be limiting of the claims. To the contrary, the claims are intended to cover all alternatives, modifications, and equivalents.
To enhance the tensile strength and the adhesion of cured aerospace sealants to surfaces, such as bare or anodized metal surfaces, bis(sulfonyl)alkanols are incorporated into the backbone of sulfur-containing prepolymers. The bis(sulfonyl)alkanol-containing sulfur-containing prepolymers can be adapted for any suitable curing chemistry. For example, thiol-terminated bis(sulfonyl)alkanol-containing polythioether prepolymers and polyepoxy curing agents provide sealants useful for aerospace applications.
Bis(sulfonyl)alkanol-Containing Polythioethers
Bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure are characterized by having one or more bis(sulfonyl)alkanol groups incorporated into the backbone of the polythioether.
Polythioethers useful in aerospace sealant applications are disclosed, for example, in U.S. Pat. No. 6,172,179. Polythioethers refer to compounds comprising at least two thioether, —C—S—C— linkages. Polythioethers may be prepared, for example, by reacting dithiols with divinyl ethers. In general, bis(sulfonyl)alkanol-containing polythioethers may be prepared by reacting a monomeric bis(sulfonyl)alkanol having terminal groups reactive with terminal of a polythioether.
In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether comprises a moiety of Formula (10):

—S(O)2—R10—CH(—OH)—R10—S(O)2—  (10)

wherein each R10 is independently selected from a C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.

In certain embodiments, bis(sulfonyl)alkanol-containing polythioethers comprise the structure of Formula (1):

-A-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-  (1)

wherein:

each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH; and
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 is independently selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl; and
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6.
    
    


In certain embodiments of Formula (1) and Formula (2), each R1 is —[—(CHR3)s—X—]q—(CHR3)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CHR3)s—X—]q—(CHR3)r—, each X is —O— and in certain embodiments, each X is —S—. In certain embodiments, each R3 is hydrogen.
In certain embodiments of Formula (1) and Formula (2), each R1 is —[—(CH2)s—X—]q—(CH2)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CH2)s—X—]q—(CH2)r—, each X is —O— and in certain embodiments, each X is —S—.
In certain embodiments of Formula (1) and Formula (2), each R1 is —[(—CH2—)s—X—]q—(CH2)r—, where s is 2, X is O, q is 2, r is 2, R2 is ethanediyl, m is 2, and n is 9.
In certain embodiments of Formula (1) and Formula (2), each R1 is derived from dimercaptodioxaoctane (DMDO) and in certain embodiments, each R1 is derived from dimercaptodiethylsulfide (DMDS).
In certain embodiments of Formula (1) and Formula (2), each m is independently an integer from 1 to 3. In certain embodiments, each m is the same and is 1, 2, and in certain embodiments, 3.
In certain embodiments of Formula (1) and Formula (2), n is an integer from 1 to 30, an integer from 1 to 20, an integer from 1 to 10, and in certain embodiments, and an integer from 1 to 5. In addition, in certain embodiments, n may be any integer from 1 to 60.
In certain embodiments of Formula (1) and Formula (2), each p is independently selected from 2, 3, 4, 5, and 6. In certain embodiments, each p is the same and is 2, 3, 4, 5, or 6.
In Formula (1), each R9 is a group derived from the reaction of a thiol group and a group reactive with a thiol group such as a terminal alkenyl group, a terminal epoxy group, or a terminal Michael acceptor group. In certain embodiments of Formula (1) and Formula (2), each R9 is independently selected from C2-10 alkanediyl, substituted C2-10 alkanediyl, C2-10 heteroalkanediyl, substituted C4-10 heteroalkanediyl, C4-14 alkanecycloalkanediyl, substituted C4-14 alkanecycloalkanediyl, C4-14 heteroalkanecycloalkanediyl, substituted C4-14 heteroalkanecycloalkanediyl, C2-14 alkanearenediyl, substituted C4-14 alkanearenediyl, C4-14 heteroalkanearenediyl, and substituted C4-14 heteroalkanearenediyl. In certain embodiments, each R9 is the same. In certain embodiments, each R9 is ethane-diyl, i.e., —CH2—CH2—.
In certain embodiments of Formula (1), each R10 is independently selected from methane-diyl, ethane-diyl, and 1,3-propane-diyl. In certain embodiments, each R10 is methane-diyl, in certain embodiments, ethane-diyl, and in certain embodiments, 1,3-propane-diyl.
In certain embodiments of Formula (1), each R9 is ethane-diyl and each R10 is methane-diyl.
In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether is selected from a bis(sulfonyl)alkanol-containing polythioether of Formula (3), a bis(sulfonyl)alkanol-containing polythioether of Formula (3a), and a combination thereof:

R6-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-R6  (3)

{R6-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (3a)

wherein
N is an integer from 1 to 10;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 independently is selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl;
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6;
    
    


B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:

    
    
        z is an integer from 3 to 6; and
        each V is a group comprising a terminal group reactive with a thiol group; and
    
    


each —V′— is derived from the reaction of —V with a thiol; and
each R6 is independently selected from hydrogen and a moiety having a terminal reactive group.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), N is 1, 2, 3, 4, 5, 6, 7, 8, 9, and in certain embodiments N is 10. In certain embodiments of bis(sulfonyl)alkanol-containing polymers of Formula (3) and Formula (3a), the molecular weight is from 400 Daltons to 2,000 Daltons. In certain embodiments, bis(sulfonyl)alkanol-containing polythioethers of Formula (3) comprise a combination of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) with different values for N. In certain embodiments, bis(sulfonyl)alkanol-containing polythioethers of Formula (3a) comprise a combination of bis(sulfonyl)alkanol-containing polythioethers of Formula (3a) with different values for N. In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), N is 1.
In certain embodiments of Formula (3) and Formula (3a), each R9 is a group derived from the reaction of a thiol group and a group reactive with a thiol group such as a terminal alkenyl group, a terminal epoxy group, or a terminal Michael acceptor group. In certain embodiments of Formula (3) and Formula (3a), each R9 is independently selected from C2-10 alkanediyl, substituted C2-10 alkanediyl, C2-10 heteroalkanediyl, substituted C2-10 heteroalkanediyl, C4-14 alkanecycloalkanediyl, substituted C4-14 alkanecycloalkanediyl, C4-14 heteroalkanecycloalkanediyl, substituted C4-14 heteroalkanecycloalkanediyl, C4-14 alkanearenediyl, substituted C4-14 alkanearenediyl, C4-14 heteroalkanearenediyl, and substituted C4-14 heteroalkanearenediyl. In certain embodiments, each R9 is the same. In certain embodiments, each R9 is ethane-diyl, i.e., —CH2—CH2—.
In certain embodiments of Formula (3) and Formula (3a), each R10 is independently selected from methane-diyl, ethane-diyl, and 1,3-propane-diyl. In certain embodiments, each R10 is methane-diyl, in certain embodiments, ethane-diyl, and in certain embodiments, 1,3-propane-diyl.
In certain embodiments of Formula (3) and Formula (3a), each R9 is ethane-diyl and each R10 is methane-diyl.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is —[—(CHR3)s—X—]q—(CHR3)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CHR3)s—X—]q—(CHR3)r—, each X is —O— and in certain embodiments, each X is —S—. In certain embodiments, each R3 is hydrogen.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is —[—(CH2)s—X—]q—(CH2)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CH2)s—X—]q—(CH2)r—, each X is —O— and in certain embodiments, each X is —S—.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is —[(—CH2—)s—X—]q—(CH2)r—, where s is 2, X is O, q is 2, r is 2, R2 is ethanediyl, m is 2, and n is 9.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is derived from DMDO and in certain embodiments, each R1 is derived from DMDS.
In certain embodiments, each m is independently an integer from 1 to 3. In certain embodiments, each m is the same and is 1, 2, and in certain embodiments, 3.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), n is an integer from 1 to 30, an integer from 1 to 20, an integer from 1 to 10, and in certain embodiments, and integer from 1 to 5. In addition, in certain embodiments, n may be any integer from 1 to 60.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each p is independently selected from 2, 3, 4, 5, and 6. In certain embodiments, each p is the same and is 2, 3, 4, 5, or 6.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is —[(—CH2—)s—X—]q—(CH2)r—, where s is 2, X is —O—, q is 2, r is 2, R2 is ethanediyl, m is 2, and n is 9.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is selected from C2-6 alkanediyl and —[—(CHR3)s—X—]q—(CHR3)r—.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is —[—(CHR3)s—X—]q—(CHR3)r—, and in certain embodiments X is —O— and in certain embodiments, X is —S—.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), where R1 is —[—(CHR3)s—X—]q—(CHR3)r—, s is 2, r is 2, q is 1, and X is —S—; in certain embodiments, wherein s is 2, q is 2, r is 2, and X is —O—; and in certain embodiments, s is 2, r is 2, q is 1, and X is —O—.
In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), where R1 is —[—(CHR3)s—X—]q—(CHR3)r—, each R3 is hydrogen, and in certain embodiments, at least one R3 is methyl.
In certain embodiment of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R1 is the same, and in certain embodiments, at least one R1 is different.
In certain embodiment of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R6 is the same and the terminal reactive group is selected from —SH, —CH═CH2, —NH2, —OH, an epoxy group, a polyalkoxysilyl group, and a Michael acceptor group.
In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether of Formula (3) has the structure:

R11—R9—S(O)2—CH2—CH(—OH)—CH2—S(O)2—R9—R11 

wherein each R9 is as defined herein; each R11 is H—[—S—(—R12—O—)2—R12—S—(—R12—O—)3—R12—]2—S—(—R12—O—)2—R12—S—, wherein each R12 is —CH2—CH2—.

In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether of Formula (3) has the structure:

R11—CH2CH2—S(O)2—CH2—CH(—OH)—CH2—S(O)2—CH2CH2—R11 

wherein each R11 is H—[—S—(—R12—O—)2—R12—S—(—R12—O—)3—R12—]2—S—(—R12—O—)2—R12—S—, wherein each R12 is —CH2—CH2—.

In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), each R6 is hydrogen, and the bis(sulfonyl)alkanol-containing polythioethers are thiol-terminated, having the structures of Formula (6), Formula (6a), Formula (6b), or Formula (6c):

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)

H-A-[-CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH2—CH2-A-]N-H  (6b)

{H-A-[-CH2—CH2—S(O)2—R10—CH(—OH)—R10—S(O)2—CH2—CH2-A-]N-V′—}zB  (6c)

where A, N, R9, R10, V′, z, and B are defined herein.

B(—V)z represents a polyfunctionalizing agent. The polyfunctionalizing agent may be a single type of polyfunctionalizing agent or a combination of different polyfunctionalizing agents, which may have the same or different functionalities. In certain embodiments, z is 3, 4, 5, or 6. Suitable polyfunctionalizing agents include trifunctionalizing agents, that is, compounds where z is 3. Suitable trifunctionalizing agents include, for example, triallyl cyanurate (TAC), modified-1,2,3-propanetrithiol, modified-isocyanurate-containing trithiols, 1,2,4-trivinylcyclohexane (BASF), and combinations of any of the foregoing, as disclosed, for example, in U.S. Application Publication No. 2010/0010133 at paragraphs [0102]-[0105], the cited portion of which is incorporated herein by reference. Other useful polyfunctionalizing agents include trimethylolpropane trivinyl ether. Mixtures of polyfunctionalizing agents may also be used. Suitable isocyanurate-containing functionalizing agents are disclosed, for example, in U.S. Application Publication No. 2011/0319559. R6 represents a moiety having a terminal reactive group. The terminal reactive group can be selected as suitable for a particular curing chemistry. For example, in certain embodiments, each R6 is the same and the reactive group is selected from —SH, —CH═CH2, —NH2, —OH, an epoxy group, polyalkoxysilyl group, and a Michael acceptor group. The use a particular curing chemistry can be chosen to obtain a desired, for example, the curing time of a composition, the application method, surface compatibility, shelf life, pot life, and/or the properties of the cured sealant composition. For example, in certain embodiments, a bis(sulfonyl)alkanol-containing polythioether of Formula (3) and/or Formula (3a) is thiol-terminated and R6 is hydrogen or a moiety terminated in a thiol group. In certain embodiments, B(—V)z is an alkenyl-terminated polyfunctionalizing agent, where each —V comprises a terminal alkenyl group, and accordingly, each —V′— represents a moiety formed by the reaction of an alkenyl group and a group reactive with alkenyl groups.
In certain embodiments, a polyfunctionalizing agent may include one or more bis(sulfonyl)alkanol groups. For example, in certain embodiments, a polyfunctionalizing may be reacted with a bis(sulfonyl)alkanol having a terminal group reactive with a terminal group of the polyfunctionalizing agent and a terminal group reactive with a thiol group. Thus, in certain embodiments, a bis(sulfonyl)alkanol-containing polyfunctionalizing agent of Formula (20), may be formed by reacting a bis(sulfonyl)alkanol of Formula (5) with a polyfunctionalizing agent of having the formula B(—V)z:

{R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R9—V′—}zB  (20)

where R8, R9, R10, B and V′ are defined herein.

In certain embodiments of bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a), R6 is hydrogen and the bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a) are thiol-terminated.
In certain embodiments, the bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a) are thiol-terminated, e.g., each R6 is hydrogen, and can be referred to an uncapped bis(sulfonyl)alkanol-containing polythioether. In certain embodiments, an uncapped bis(sulfonyl)alkanol-containing polythioether is a liquid at room temperature. Moreover, in certain embodiments, an uncapped bis(sulfonyl)alkanol-containing polythioether has a viscosity, at 100% solids, of less than 500 poise, such as 100 poise to 300 poise or, in some cases, 100 poise to 200 poise at a temperature of about 25° C. and a pressure of about 760 mm Hg determined according to ASTM D-2849 §79-90 measured using a Brookfield CAP 2000 viscometer. Any endpoint within the foregoing ranges can also be used. In certain embodiments, an uncapped bis(sulfonyl)alkanol-containing polythioether has a number average molecular weight of 400 grams per mole to 10,000 grams per mole, such as 1,000 grams per mole to 8,000 grams per mole, the molecular weight being determined, for example, by gel permeation chromatography using a polystyrene standard. Any endpoints within the foregoing ranges can also be used. In certain embodiments, the Tg of an uncapped bis(sulfonyl)alkanol-containing polythioether is not higher than −55° C., such as not higher than −60° C.
In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether may be capped to adapt the bis(sulfonyl)alkanol-containing polythioether for use with different curing chemistries.
Bis(sulfonyl)alkanol-containing polythioethers of Formula (3) and Formula (3a) in which R6 is a moiety having a terminal reactive group may be prepared by capping the corresponding thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3) and Formula (3a) wherein each R6 is hydrogen with a moiety having a terminal reactive group and a group reactive with a thiol group. Capped analogs of polythioethers and methods of preparing capped analogs of polythioethers useful in aerospace sealant applications are disclosed, for example, in U.S. Pat. No. 6,172,179 and in U.S. Application Publication No. 2011/0319559, each of which is incorporated by reference herein. In certain embodiments, R6 comprises a terminal alkenyl group, a terminal epoxy group, a terminal polyalkoxysilyl group, a terminal amine group, or a terminal Michael acceptor group. A capping group R6 may have a molecular weight less than 500 Daltons.
Terminal-modified bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure may be prepared by a number of methods known to those skilled in the art. For example, to obtain terminal-modified bis(sulfonyl)alkanol-containing polythioether of Formula (3) and Formula (3a), a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) or Formula (6a) as disclosed herein, may be reacted with a compound having a terminal functional group and a terminal group reactive with thiol groups.
For example, to obtain an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3), a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) may be reacted with a compound containing a terminal alkenyl group and an isocyanate group such as a group derived from TMI, 2-isocyanatoethyl methacrylate, or allyl isocyanate, in the presence of dibutyltin dilaurate catalyst at about 76° C. As a further example, a bis(sulfonyl)alkanol-containing polythioether of Formula (3) may be reacted with an alkene-ol such as 3-butene-1-ol and an aldehyde such as formaldehyde in the presence of a sulfonic acid (e.g., 4.7 meq/g H+) such as AmberlystTM 15 in an organic solvent such as toluene to provide an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6). In certain embodiments, an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3) may be prepared by reacting a polyalkenyl compound such as a dialkenyl compound with a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6).
Polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) with an isocyanatoalkyltrialkoxysilane such as a 3-isocyanatopropyltrimethoxysilane or 3-isocyanatopropyltriethoxysilane in the presence of dibutyltin dilaurate at a temperature of about 76° C. to provide the corresponding polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3). In certain embodiments, a polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3) may be prepared by reacting a vinyl alkoxysilane with a thiol-terminated bis(sulfonyl)alkanol-containing polythioether.
Epoxy-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may be prepared, for example, by reacting thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) with a monoepoxide such as epichlorohydrin, or with an alkenyl glycidyl compound such as allyl glycidyl ether to provide the corresponding epoxy-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3).
Amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may be prepared, for example, by reacting an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (3) with aniline, an amino-substituted aniline such as 4-(aminomethyl)aniline, or an alkylamine such as n-butylamine, optionally in the presence of a catalyst such as 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU) in an organic solvent to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3). Alternatively, amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may be obtained by reacting an isocyanate-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) with a diamine such as 4-(aminomethyl)aniline to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3). Amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may also be obtained by reacting a hydroxyl-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) with an amino-substituted benzoate such as ethyl-4-aminobenzoate in the presence of Bu2SnO or NaOMe at elevated temperature to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3). Amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may also be prepared by reacting a tosyl-ester of an amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) with an amine-containing compound such as aniline in an organic solvent at elevated temperature to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3).
Isocyanate-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (3) may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (6) with a diisocyanate such as TDI, IsonateTM 143L (polycarbodiimide-modified diphenylmethane diisocyanate), Desmodur® N3400 (1,3-diazetidine-2,4-dione, 1,3-bis(6-isocyanatohexyl)-), IPDI (isophorone diisocyanate), or Desmodur® W (H12MDI) optionally in the presence of a catalyst such as dibutyltin dilaurate at a temperature from about 70° C. to about 80° C. Isocyanate-terminated sulfur-containing polymers may be used as intermediates in the synthesis of other terminal-modified sulfur-containing polymers such as certain amine-terminated and thiol-terminated bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure.
Similar reactions may be used to prepare capped bis(sulfonyl)alkanols of Formula (3a).
In certain embodiments, a thiol-terminated bis(sulfonyl)alkanol-containing polythioether comprises the reaction product of reactants comprising:
(a) a thiol-terminated polythioether selected from a thiol-terminated polythioether of Formula (4), a thiol-terminated polythioether of Formula (4a), and a combination thereof:

HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)

{HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—V′—}zB  (4a)

wherein:

    
    
        each R1 independently is selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl;
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60;
        p is an integer from 2 to 6; and
        B represents a core of a z-valent polyfunctionalizing agent B(—V), wherein:
        
            z is an integer from 3 to 6; and
            each V is a group comprising a terminal group reactive with a thiol group; and
            each —V′— is derived from the reaction of —V with a thiol; and
        
        
    
    


(b) a bis(sulfonyl)alkanol of Formula (5):

R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)

wherein

    
    
        each R8 is independently selected from a moiety comprising a terminal group reactive with a terminal thiol group; and
        each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.
    
    


In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each R1 is —[—(CHR3)s—X—]q—(CHR3)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CHR3)s—X—]q—(CHR3)r—, each X is —O— and in certain embodiments, each X is —S—. In certain embodiments, each R3 is hydrogen.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each R1 is —[—(CH2)s—X—]q—(CH2)r— wherein each X is independently selected from —O— and —S—. In certain embodiments wherein R1 is —[—(CH2)s—X—]q—(CH2)r—, each X is —O— and in certain embodiments, each X is —S—.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each R1 is —[(—CH2—)p—X—]q—(CH2)r—, where s is 2, X is O, q is 2, r is 2, R2 is ethanediyl, m is 2, and n is 9.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each R1 is derived from DMDO and in certain embodiments, each R1 is derived from DMDS.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each m is independently an integer from 1 to 3. In certain embodiments, each m is the same and is 1, 2, and in certain embodiments, 3.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), n is an integer from 1 to 30, an integer from 1 to 20, an integer from 1 to 10, and in certain embodiments, and integer from 1 to 5. In addition, in certain embodiments, n may be any integer from 1 to 60.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), each p is independently selected from 2, 3, 4, 5, and 6. In certain embodiments, each p is the same and is 2, 3, 4, 5, or 6.
In certain embodiments of thiol-terminated polythioethers of Formula (4) and Formula (4a), R1 is derived from DMDO, R2 is derived from a divinyl ether, and the polyfunctionalizing agent is TAC.
In certain embodiments, a polythioether of Formula (4) has the structure:

H—[—S—(—CH2CH2—O—)2—CH2CH2—S—(—CH2CH2—O—)3—CH2CH2—]2—S—(—CH2CH2—O—)2—CH2CH2—SH.

In certain embodiments of Formula (5), each R10 is independently selected from methane-diyl, ethane-diyl, and 1,3-propane-diyl. In certain embodiments, each R10 is methane-diyl, in certain embodiments, ethane-diyl, and in certain embodiments, 1,3-propane-diyl.
In certain embodiments, R8 comprises a group reactive with a thiol group selected from an alkenyl group, an epoxy group, and a Michael acceptor group. In certain embodiments, each R8 is terminated with an alkenyl group. In certain embodiments, R8 is selected from C2-10 alkyl, substituted C2-10 alkyl, C2-10 heteroalkyl, substituted C2-10 heteroalkyl, C4-14 alkanecycloalkyl, substituted C4-14 alkanecyclo alkyl, C4-14 heteroalkanecyclo alkyl, substituted C4-14 heteroalkanecycloalkyl, C4-14 alkanearyl, substituted C4-14 alkanearyl, C4-14 heteroalkanearyl, and substituted C4-14 heteroalkanearyl. In certain embodiments, R8 is ethylene, i.e., —CH═CH2.
In certain embodiments, a bis(sulfonyl)alkanol of Formula (5) comprises a bis(vinylsulfonyl)alkanol. In certain embodiments, a bis(vinylsulfonyl)alkanol has the structure of Formula (5a):

CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2  (5a)

where R10 is defined herein.

In certain embodiments, a bis(vinylsulfonyl)alkanol of Formula (5) comprises 1,3-bis(vinylsulfonyl)-2-propanol and has the structure of Formula (5b):

CH2═CH—S(O)2—CH2—CH2—CH(—OH)—CH2—CH2—S(O)2—CH═CH2  (5b).

Thiol-terminated polythioethers of Formula (4) and Formula (4a) and a bis(vinylsulfonyl)alkanol of Formula (5) may be reacted in the presence of a base catalyst such as an amine catalyst. Examples of suitable amine catalysts include, for example, triethylenediamine (1,4-diazabicyclo[2.2.2]octane, DABCO), dimethylcyclohexylamine (DMCHA), dimethylethanolamine (DMEA), bis-(2-dimethylaminoethyl)ether, N-ethylmorpholine, triethylamine, 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU), pentamethyldiethylenetriamine (PMDETA), benzyldimethylamine (BDMA), N,N,N′-trimethyl-N′-hydroxyethyl-bis(aminoethyl)ether, and N′-(3-(dimethylamino)propyl)-N,N-dimethyl-1,3-propanediamine.
In certain embodiments, bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure are characterized by a mercaptan equivalent weight (MEW) from about 400 to about 4,000.
Various methods can be used to prepare thiol-terminated polythioethers of Formula (4) and Formula (4a). Examples of suitable thiol-terminated polythioethers, and methods for their production, are described in U.S. Pat. No. 6,172,179 at col. 2, line 29 to col. 4, line 22; col. 6, line 39 to col. 10, line 50; and col. 11, lines 65 to col. 12, line 22, the cited portions of which are incorporated by reference. Such thiol-terminated polythioethers may be difunctional, that is, linear polymers having two terminal thiol groups, or polyfunctional, that is, branched polymers have three or more terminal thiol groups. Suitable thiol-terminated polythioethers are commercially available, for example, as Permapol® P3.1E, from PRC-DeSoto International Inc., Sylmar, Calif.
In certain embodiments, a thiol-terminated polythioether can be prepared by reacting a polythiol and a diene such as a divinyl ether, and the respective amounts of the reactants used to prepare the polythioethers are chosen to yield terminal thiol groups. Thus, in some cases, (n or >n, such as n+1) moles of a polythiol, such as a dithiol or a mixture of at least two different dithiols and about 0.05 moles to 1 moles, such as 0.1 moles to 0.8 moles, of a thiol-terminated polyfunctionalizing agent may be reacted with (n) moles of a diene, such as a divinyl ether, or a mixture of at least two different dienes, such as a divinyl ether. In certain embodiments, a thiol-terminated polyfunctionalizing agent is present in the reaction mixture in an amount sufficient to provide a thiol-terminated polythioether having an average functionality of from 2.05 to 3, such as 2.1 to 2.8.
The reaction used to make a thiol-terminated polythioether may be catalyzed by a free radical catalyst. Suitable free radical catalysts include azo compounds, for example azobisnitrile compounds such as azo(bis)isobutyronitrile (AIBN); organic peroxides, such as benzoyl peroxide and t-butyl peroxide; and inorganic peroxides, such as hydrogen peroxide. The reaction can also be effected by irradiation with ultraviolet light either with or without a radical initiator/photosensitizer. Ionic catalysis methods, using either inorganic or organic bases, e.g., triethylamine, may also be used.
Suitable thiol-terminated polythioethers may be produced by reacting a divinyl ether or mixtures of divinyl ethers with an excess of dithiol or a mixtures of dithiols.
Thus, in certain embodiments, a thiol-terminated polythioether comprises the reaction product of reactants comprising:
(a) a dithiol of Formula (8):

HS—R1—SH  (8)

    
    
        wherein:
        
            R1 is selected from C2-6 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[—(CHR3)s—X—]q—(CHR3)r—; wherein:
            
                each R3 is independently selected from hydrogen and methyl;
                each X is independently selected from —O—, —S—, —NH—, and —NR— wherein R is selected from hydrogen and methyl;
                s is an integer from 2 to 6;
                q is an integer from 1 to 5; and
                r is an integer from 2 to 10; and
            
            
        
        
    
    


(b) a divinyl ether of Formula (9):

CH2═CH—O—[—R2—O—]mCH═CH2  (9)

    
    
        wherein:
        
            each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined above;
            m is an integer from 0 to 50;
            n is an integer from 1 to 60; and
            p is an integer from 2 to 6.

And, in certain embodiments, the reactants may comprise (c) a polyfunctional compound such as a polyfunctional compound B(—V)z, where B, —V, and z are as defined herein.

        
        
    
    


In certain embodiments, dithiols suitable for use in preparing thiol-terminated polythioethers include those having Formula (8), other dithiols disclosed herein, or combinations of any of the dithiols disclosed herein. In certain embodiments, a dithiol has the structure of Formula (8):

HS—R1—SH  (8)

wherein:

    
    
        R1 is selected from C2-6 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[—(CHR3)s—X—]q—(CHR3)r—;
        wherein:
        
            each R3 is independently selected from hydrogen and methyl;
            each X is independently selected from —O—, —S—, and —NR5— wherein R5 is selected from hydrogen and methyl;
            s is an integer from 2 to 6;
            q is an integer from 1 to 5; and
            r is an integer from 2 to 10.
        
        
    
    


In certain embodiments of a dithiol of Formula (8), R1 is —[—(CHR3)s—X—]q—(CHR3)r—.
In certain embodiments of a compound of Formula (8), X is selected from —O— and —S—, and thus —[—(CHR3)s—X—]q—(CHR3)r— in Formula (8) is —[(—CHR3—)s—O—]q—(CHR3)r— or —[(CHR32—)s—S—]q—(CHR3)r—. In certain embodiments, p and r are equal, such as where p and r are both two.
In certain embodiments of a dithiol of Formula (8), R1 is selected from C2-6 alkanediyl and —[—(CHR3)s—X—]q—(CHR3)r—.
In certain embodiments of a dithiol of Formula (8), R1 is —[—(CHR3)s—X—]q—(CHR3)r—, and in certain embodiments X is —O—, and in certain embodiments, X is —S—.
In certain embodiments where R1 is —[—(CHR3)s—X—]q—(CHR3)r—, s is 2, r is 2, q is 1, and X is —S—; in certain embodiments, wherein s is 2, q is 2, r is 2, and X is —O—; and in certain embodiments, s is 2, r is 2, q is 1, and X is —O—.
In certain embodiments where R1 is —[—(CHR3)s—X—]q—(CHR3)r—, each R3 is hydrogen, and in certain embodiments, at least one R3 is methyl.
Examples of suitable dithiols include, for example, 1,2-ethanedithiol, 1,2-propanedithiol, 1,3-propanedithiol, 1,3-butanedithiol, 1,4-butanedithiol, 2,3-butanedithiol, 1,3-pentanedithiol, 1,5-pentanedithiol, 1,6-hexanedithiol, 1,3-dimercapto-3-methylbutane, dipentenedimercaptan, ethylcyclohexyldithiol (ECHDT), dimercaptodiethylsulfide, methyl-substituted dimercaptodiethylsulfide, dimethyl-substituted dimercaptodiethylsulfide, dimercaptodioxaoctane, 1,5-dimercapto-3-oxapentane, and a combination of any of the foregoing. A polythiol may have one or more pendant groups selected from a lower (e.g., C1-6) alkyl group, a lower alkoxy group, and a hydroxyl group. Suitable alkyl pendant groups include, for example, C1-6 linear alkyl, C3-6 branched alkyl, cyclopentyl, and cyclohexyl.
Other examples of suitable dithiols include dimercaptodiethylsulfide (DMDS) (in Formula (8), R1 is —[(—CH2—)s—X—]q—(CH2)r—, wherein s is 2, r is 2, q is 1, and X is —S—); dimercaptodioxaoctane (DMDO) (in Formula (8), R1 is —[(CH2—)s—X—]q—(CH2)r—, wherein s is 2, q is 2, r is 2, and X is —O—); and 1,5-dimercapto-3-oxapentane (in Formula (8), R1 is —[(CH2—)s—X—]q—(CH2)r—, wherein s is 2, r is 2, q is 1, and X is —O—). It is also possible to use dithiols that include both heteroatoms in the carbon backbone and pendant alkyl groups, such as methyl groups. Such compounds include, for example, methyl-substituted DMDS, such as HS—CH2CH(CH3)—S—CH2CH2—SH, HS—CH(CH3)CH2—S—CH2CH2—SH and dimethyl substituted DMDS, such as HS—CH2CH(CH3)—S—CHCH3CH2—SH and HS—CH(CH3)CH2—S—CH2CH(CH3)—SH.
Suitable divinyl ethers for preparing polythioethers include, for example, divinyl ethers of Formula (9):

CH2═CH—P—(—R2—O—)m—CH═CH2  (9)

where R2 in Formula (9) is selected from a C2-6 n-alkanediyl group, a C3-6 branched alkanediyl group, a C6-8 cycloalkanediyl group, a C6-10 alkanecycloalkanediyl group, and —[(—CH2—)s—O—]q—(—CH2—)r—, where s is an integer ranging from 2 to 6, q is an integer from 1 to 5, and r is an integer from 2 to 10. In certain embodiments of a divinyl ether of Formula (9), R2 is a C2-6 n-alkanediyl group, a C3-6 branched alkanediyl group, a C6-8 cycloalkanediyl group, a C6-10 alkanecycloalkanediyl group, and in certain embodiments, —[(—CH2—)s—O—]q—(—CH2—)r—.

Suitable divinyl ethers include, for example, compounds having at least one oxyalkanediyl group, such as from 1 to 4 oxyalkanediyl groups, i.e., compounds in which m in Formula (9) is an integer ranging from 1 to 4. In certain embodiments, m in Formula (9) is an integer ranging from 2 to 4. It is also possible to employ commercially available divinyl ether mixtures that are characterized by a non-integral average value for the number of oxyalkanediyl units per molecule. Thus, m in Formula (9) can also take on rational number values ranging from 0 to 10.0, such as from 1.0 to 10.0, from 1.0 to 4.0, or from 2.0 to 4.0.
Examples of suitable vinyl ethers include, divinyl ether, ethylene glycol divinyl ether (EG-DVE) (R2 in Formula (9) is ethanediyl and m is 1), butanediol divinyl ether (BD-DVE) (R2 in Formula (9) is butanediyl and m is 1), hexanediol divinyl ether (HD-DVE) (R2 in Formula (9) is hexanediyl and m is 1), diethylene glycol divinyl ether (DEG-DVE) (R2 in Formula (9) is ethanediyl and m is 2), triethylene glycol divinyl ether (R2 in Formula (9) is ethanediyl and m is 3), tetraethylene glycol divinyl ether (R2 in Formula (9) is ethanediyl and m is 4), cyclohexanedimethanol divinyl ether, polytetrahydrofuryl divinyl ether; trivinyl ether monomers, such as trimethylolpropane trivinyl ether; tetrafunctional ether monomers, such as pentaerythritol tetravinyl ether; and combinations of two or more such polyvinyl ether monomers. A polyvinyl ether may have one or more pendant groups selected from alkyl groups, hydroxyl groups, alkoxy groups, and amine groups.
In certain embodiments, divinyl ethers in which R2 in Formula (9) is C3-6 branched alkanediyl may be prepared by reacting a polyhydroxy compound with acetylene. Examples of divinyl ethers of this type include compounds in which R2 in Formula (9) is an alkyl-substituted methanediyl group such as —CH(—CH3)—, for which R2 in Formula (9) is ethanediyl and m is 3.8) or an alkyl-substituted ethanediyl.
Other useful divinyl ethers include compounds in which R2 in Formula (9) is polytetrahydrofuryl (poly-THF) or polyoxyalkanediyl, such as those having an average of about 3 monomer units.
Two or more types of polyvinyl ether monomers of Formula (9) may be used. Thus, in certain embodiments, two dithiols of Formula (8) and one polyvinyl ether monomer of Formula (9), one dithiol of Formula (8) and two polyvinyl ether monomers of Formula (9), two dithiols of Formula (8) and two divinyl ether monomers of Formula (9), and more than two compounds of one or both Formula (8) and Formula (9), may be used to produce a variety of thiol-terminated polythioethers.
In certain embodiments, a polyvinyl ether monomer comprises 20 to less than 50 mole percent of the reactants used to prepare a thiol-terminated polythioether, and in certain embodiments, 30 to less than 50 mole percent.
In certain embodiments provided by the present disclosure, relative amounts of dithiols and divinyl ethers are selected to yield polythioethers having terminal thiol groups. Thus, a dithiol of Formula (8) or a mixture of at least two different dithiols of Formula (8), are reacted with of a divinyl ether of Formula (9) or a mixture of at least two different divinyl ethers of Formula (9) in relative amounts such that the molar ratio of thiol groups to vinyl groups is greater than 1:1, such as 1.1 to 2.0:1.0.
The reaction between dithiols and divinyl ethers and/or polythiols and polyvinyl ethers may be catalyzed by a free radical catalyst. Suitable free radical catalysts include, for example, azo compounds, for example azobisnitriles such as azo(bis)isobutyronitrile (AIBN); organic peroxides such as benzoyl peroxide and t-butyl peroxide; and inorganic peroxides such as hydrogen peroxide. The catalyst may be a free-radical catalyst, an ionic catalyst, or ultraviolet radiation. In certain embodiments, the catalyst does not comprise acidic or basic compounds, and does not produce acidic or basic compounds upon decomposition. Examples of free-radical catalysts include azo-type catalyst, such as Vazo®-57 (Du Pont), Vazo®-64 (Du Pont), Vazo®-67 (Du Pont), V-70® (Wako Specialty Chemicals), and V-65B® (Wako Specialty Chemicals). Examples of other free-radical catalysts are alkyl peroxides, such as t-butyl peroxide. The reaction may also be effected by irradiation with ultraviolet light either with or without a cationic photoinitiating moiety.
Thiol-terminated polythioethers provided by the present disclosure may be prepared by combining at least one compound of Formula (8) and at least one compound of Formula (9) followed by addition of an appropriate catalyst, and carrying out the reaction at a temperature from 30° C. to 120° C., such as 70° C. to 90° C., for a time from 2 to 24 hours, such as 2 to 6 hours.
As disclosed herein, thiol-terminated polythioethers may comprise a polyfunctional polythioether, i.e., may have an average functionality of greater than 2.0. Suitable polyfunctional thiol-terminated polythioethers include, for example, those having the structure of Formula (4a):

{HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—V′—}zB  (4a)

wherein z has an average value of greater than 2.0, and, in certain embodiments, a value between 2 and 3, a value between 2 and 4, a value between 3 and 6, and in certain embodiments, is an integer from 3 to 6.

Polyfunctionalizing agents suitable for use in preparing such polyfunctional thiol-terminated polymers include trifunctionalizing agents, that is, compounds where z is 3. Suitable trifunctionalizing agents include, for example, triallyl cyanurate (TAC), 1,2,3-propanetrithiol, isocyanurate-containing trithiols, and combinations thereof, as disclosed in U.S. Publication No. 2010/0010133 at paragraphs [0102]-[0105], the cited portion of which is incorporated by reference and isocyanurates as disclosed, for example, in U.S. Application Publication No. 2011/0319559, which is incorporated by reference. Other useful polyfunctionalizing agents include trimethylolpropane trivinyl ether, and the polythiols described in U.S. Pat. Nos. 4,366,307; 4,609,762; and 5,225,472, each of which is incorporated by reference. Mixtures of polyfunctionalizing agents may also be used.
As a result, bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure may have a wide range of average functionality. For example, trifunctionalizing agents may afford average functionalities from 2.05 to 3.0, such as from 2.1 to 2.6. Wider ranges of average functionality may be achieved by using tetrafunctional or higher functionality polyfunctionalizing agents. Functionality may also be determined by factors such as stoichiometry, as will be understood by those skilled in the art.
Thiol-terminated polythioethers and bis(sulfonyl)alkanol-containing polythioethers having a functionality greater than 2.0 may be prepared in a manner similar to the difunctional thiol-terminated polythioethers described in U.S. Application Publication No. 2010/0010133, U.S. Application Publication No. 2011/0319559, and U.S. Pat. No. 6,172,179, each of which is incorporated by reference. In certain embodiments, polythioethers may be prepared by combining (i) one or more dithiols described herein, with (ii) one or more divinyl ethers described herein, and (iii) one or more polyfunctionalizing agents. The mixture may then be reacted, optionally in the presence of a suitable catalyst, to afford a thiol-terminated polythioether or bis(sulfonyl)alkanol-containing polythioether having a functionality greater than 2.0.
In certain embodiments, polythioethers including thiol-terminated polythioethers, bis(sulfonyl)alkanol-containing polythioethers, and capped analogs of any of the foregoing represent polythioethers having a molecular weight distribution. In certain embodiments, useful polythioethers can exhibit a number average molecular weight ranging from 500 Daltons to 20,000 Daltons, in certain embodiments, from 2,000 Daltons to 5,000 Daltons, and in certain embodiments, from 3,000 Daltons to 4,000 Daltons. In certain embodiments, useful polythioethers exhibit a polydispersity (Mw/Mn; weight average molecular weight/number average molecular weight) ranging from 1 to 20, and in certain embodiments, from 1 to 5. The molecular weight distribution of polythioethers may be characterized, for example, by gel permeation chromatography.
Methods
In general, thiol-terminated bis(sulfonyl)alkanol-containing polythioethers may be prepared by reacting a thiol-terminated polythioether or a mixture of thiol-terminated polythioethers with a bis(sulfonyl)alkanol such as a bis(vinylsulfonyl)alkanol. In certain embodiments, a thiol-terminated bis(sulfonyl)alkanol-containing polythioether may be prepared by reacting a difunctional thiol-terminated polythioether or a mixture of difunctional thiol-terminated polythioethers with a bis(sulfonyl)alkanol such as a bis(vinylsulfonyl)alkanol or a bis(sulfonyl)alkanol having terminal groups reactive with thiol groups.
In certain embodiments, methods of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), comprise reacting (N+1) moles of a thiol-terminated polythioether of Formula (4) with (N) moles of a bis(vinylsulfonyl)alkanol of Formula (5):

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)

R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)

wherein:

N is an integer from 1 to 10;
each R8 is independently selected from a moiety comprising a terminal group reactive with a terminal thiol group;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 independently is selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl; and
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6.
    
    


In certain embodiments of thiol-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (6), N is 1, 2, 3, 4, 5, 6, 7, 8, 9, and in certain embodiments N is 10. In certain embodiments of bis(sulfonyl)alkanol-containing polymers of Formula (6), the molecular weight is from 200 Daltons to 2,000 Daltons. In certain embodiments, thiol-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (6) comprise a combination of bis(sulfonyl)alkanol containing polythioethers of Formula (6) with different values for N. In certain embodiments of thiol-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (6), N is 1. Thus, in practice, when preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), the molar ratios of thiol-terminated polythioether to bis(sulfonyl)alkanol need not be a whole number such that thiol-terminated bis(sulfonyl)alkanol-containing polythioethers of Formula (6) represent a mixture of thiol-terminated bis(sulfonyl)alkanol-containing polythioethers having different values of N.
In certain embodiments, methods of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a) comprise reacting (z) moles of a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) with one (1) mole of a polyfunctionalizing agent of Formula (7):

{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

B{V}z  (7)

wherein:

each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 independently is selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—,
            wherein R5 is selected from hydrogen and methyl;
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6; and
    
    


B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6;
each V is a group comprising a group reactive with a thiol group; and
each —V′— is derived from the reaction of —V with a thiol.
In certain embodiments, the reaction between a thiol-terminated bis(sulfonyl)alkanol-containing polythioether and bis(sulfonyl)alkanol such as a bis(vinylsulfonyl)alkanol is performed in the presence of a catalyst such as an amine catalyst including, for example, any of the amine catalysts disclosed herein.
Alkenyl-terminated Bis(sulfonyl)alkanol-Containing Polythioether Prepolymers
Thiol-terminated bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure can be reacted with polyalkenyls such as dialkenyl ethers and/or alkenyl-terminated polyfunctionalizing agents to provide alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether prepolymers. Alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether prepolymers may be combined with a curing agent to provide a curable composition such as a sealant composition.
For example, in certain embodiments an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether prepolymer comprises the reaction product of reactants comprising:
(a) a thiol-terminated bis(sulfonyl)alkanol-containing polythioether selected from a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a), and a combination thereof:

H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)

{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)

wherein

N is an integer from 1 to 10;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):

—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:

    
    
        each R1 independently is selected from C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
        
            s is an integer from 2 to 6;
            q is an integer from 1 to 5;
            r is an integer from 2 to 10;
            each R3 is independently selected from hydrogen and methyl; and
            each X is independently selected from —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl;
        
        
        each R2 is independently selected from C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, and —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
        m is an integer from 0 to 50;
        n is an integer from 1 to 60; and
        p is an integer from 2 to 6;
    
    


B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6;
each V is a group comprising a terminal group reactive with a thiol group; and
each —V′— is derived from the reaction of —V with a thiol; and
(b) a polyalkenyl compound.
In certain embodiments, a polyalkenyl compound is selected from a divinyl ether or a mixture of divinyl ethers including any of those disclosed herein, an alkenyl-terminated polyfunctionalizing agent, and a combination thereof.
In certain embodiments of the preceding reaction, (a) is polythioether of Formula (6), and (b) is a polyvinyl ether selected from a divinyl ether, an alkenyl-terminated polyfunctionalizing agent and a combination thereof.
In certain embodiments of the preceding reaction, (a) is an polythioether of Formula (6), and (b) is a polyalkenyl ether selected from diethylene glycol divinyl ether (DEG-DVE), TAC, and a combination thereof.
Capped Bis(sulfonyl)alkanol-Containing Polythioether Prepolymers
Bis(sulfonyl)alkanol-containing polythioethers may be adapted for use with a particular curing chemistry by capping or terminating a bis(sulfonyl)alkanol-containing polythioether such as a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with a suitable functional group. Capped analogs of thiol-terminated polythioethers are disclosed, for example, in U.S. Pat. No. 6,172,179 and in U.S. Application Publication No. 2011/0319559.
For example, in certain embodiments, a bis(sulfonyl)alkanol-containing polythioether has terminal groups other than unreacted thiol groups, such as hydroxyl, alkenyl, isocyanate, amine, epoxy, a hydrolysable functional group such as a polyalkoxysilyl group, a Michael acceptor group, or an epoxy group.
Capped analogs may be prepared by a number of methods known to those skilled in the art. For example, to obtain capped bis(sulfonyl)alkanol-containing polythioethers, a thiol-terminated bis(sulfonyl)alkanol-containing polythioether may be reacted with a compound having a terminal group reactive with thiol groups.
To obtain an alkenyl-terminated bis(sulfonyl)alkanol-containing polythioether, a thiol-terminated bis(sulfonyl)alkanol-containing polythioether may be reacted with a compound containing a terminal alkenyl group and an isocyanate group such as a group derived from TMI, 2-isocyanatoethyl methacrylate, or allyl isocyanate, in the presence of dibutyltin dilaurate catalyst at about 76° C.
Polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioethers may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with an isocyanatoalkyltrialkoxysilane such as a 3-isocyanatopropyltrimethoxysilane or 3-isocyanatopropyltriethoxysilane in the presence of dibutyltin dilaurate at a temperature of about 76° C. to provide the corresponding polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether.
Epoxy-terminated bis(sulfonyl)alkanol-containing polythioethers may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether in the presence of a monoepoxide such as allyl glycidyl ether to provide the corresponding epoxy-terminated bis(sulfonyl)alkanol-containing polythioether.
Amine-terminated bis(sulfonyl)alkanol-containing polythioether may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with a monofunctional 4-amino butyl vinyl ether with a free-radical initiator. Alternatively, an amine-terminated bis(sulfonyl)alkanol-containing polythioether may be obtained by reacting an isocyanate-terminated bis(sulfonyl)alkanol-containing polythioether with a diamine such as 4-(aminomethyl)aniline to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioether. Amine-terminated bis(sulfonyl)alkanol-containing polythioether may also be obtained by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with an amino-substituted benzoate such as ethyl-4-aminobenzoate in the presence of Bu2SnO or NaOMe at elevated temperature to provide the corresponding amine-terminated bis(sulfonyl)alkanol-containing polythioether.
Isocyanate-terminated bis(sulfonyl)alkanol-containing polythioether may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with a diisocyanate such as TDI, IsonateTM 143L (polycarbodiimide-modified diphenylmethane diisocyanate), Desmodur® N3400 (1,3-diazetidine-2,4-dione, 1,3-bis(6-isocyanatohexyl)-), IPDI (isophorone diisocyanate), or Desmodur® W (H12MDI) optionally in the presence of a catalyst such as dibutyltin dilaurate at a temperature from about 70° C. to about 80° C. Isocyanate-terminated bis(sulfonyl)alkanol-containing polythioether may be used as intermediates in the synthesis of other terminal-modified bis(sulfonyl)alkanol-containing polythioethers such as certain amine-terminated and thiol-terminated bis(sulfonyl)alkanol-containing polythioether.
Hydroxyl-terminated bis(sulfonyl)alkanol-containing polythioethers may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with a compound having a terminal hydroxyl group and a group reactive with thiol groups.
In certain embodiments, each of the Michael acceptor groups may be the same and in certain embodiments, at least some of the Michael acceptor groups are different. In certain embodiments, a Michael acceptor group is derived from a vinyl sulfone and has the structure of Formula (11):

—CH2—C(R13)2—S(O)2—CR13═CH2  (11)

wherein each R13 is independently selected from hydrogen and C1-3 alkyl. In certain embodiments of Formula (11), each R13 is hydrogen. In certain embodiments, Michael acceptor-terminated bis(sulfonyl)alkanol-containing polythioethers may be prepared, for example, by reacting a thiol-terminated bis(sulfonyl)alkanol-containing polythioether with a compound having a terminal Michael acceptor group and a group reactive with thiol groups such as a divinylsulfone, in the presence of an amine catalyst. Michael acceptor/polythioether chemistries and compounds are disclosed in U.S. application Ser. No. 13/529,237, filed on Jun. 13, 2012, which is incorporated by reference in its entirety. Examples of isocyanate- and epoxy-capped polythioethers and methods of making isocyanate- and epoxy-capped polythioethers are disclosed in U.S. Pat. No. 7,879,955 B2.

Compositions
Compositions provided by the present disclosure may comprise one or more bis(sulfonyl)alkanol-containing polythioethers and/or one or more bis(sulfonyl)alkanol-containing polythioether prepolymers. Curable compositions may further include a curing agent. Compositions may further include additives, catalysts, fillers, and/or other sulfur-containing prepolymers including for example, polythioethers, polyformals, and/or polysulfides.
A suitable curing agent is selected to be reactive with the terminal groups of the bis(sulfonyl)alkanol-containing polythioether and optional sulfur-containing prepolymers.
In certain embodiments in which a bis(sulfonyl)alkanol-containing polythioether or prepolymer thereof is terminated with thiol groups, a suitable curing agent is a polyepoxide. Examples of suitable polyepoxies include, for example, polyepoxide resins such as hydantoin diepoxide, diglycidyl ether of bisphenol-A, diglycidyl ether of bisphenol-F, Novolac® type epoxides such as DENTM 438 (Dow Chemical Company), certain epoxidized unsaturated resins, and combinations of any of the foregoing. A polyepoxide refers to a compound having two or more reactive epoxy groups. In certain embodiments, an epoxy curing agent is selected from EPONTM 828 (Momentive Specialty Chemicals, Inc), DENTM 431 (Dow Chemical Company), and a combination thereof. Examples of useful curing agents that are reactive with thiol groups include diepoxides.
Other examples of useful curing agents that are reactive with terminal epoxy groups include amines such as diethylenetriamine (DTA), triethylenetetramine (TTA), tetraethylenepentamine (TEPA), diethylaminopropylamine (DEAPA), N-aminoethylpiperazine (N-AEP), isophoronediamine (IPDA), m-xylenediamine, diaminodiphenylmethane (DDM), diaminodiphenylsulfone (DDS); aromatic amines, ketimine; polyamines; polyamides; phenolic resins; anhydrides such phthalic anhydride, trimellitic anhydride, pyromellitic anhydride, benzophenone tetracarboxylic anhydride, ethylene glycol bistrimellitate, glycerol tristrimellitate, maleic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, endomethylene tetrahydrophthalic anhydride; polymercaptans; polysulfides; and other curing agents known to those skilled in the art.
In certain embodiments, a polyepoxy curing agent comprises an epoxy-functional polymer. Examples of suitable epoxy-functional polymers include the epoxy-functional polyformal polymers disclosed in U.S. patent application Ser. No. 13/050,988 and epoxy-functional polythioether polymers disclosed in U.S. Pat. No. 7,671,145. In general, when used as a curing agent, an epoxy-functional polymer has a molecular weight less than about 2,000 Daltons, less than about 1,500, Daltons, less than about 1,000 Daltons, and in certain embodiments, less than about 500 Daltons.
In certain embodiments, a polyepoxy may comprise about 0.5 wt % to about 20 wt % of the composition, from about 1 wt % to about 10 wt %, from about 2 wt % to about 8 wt %, from about 2 wt % to about 6 wt %, and in certain embodiments, from about 3 wt % to about 5 wt %, where wt % is based on the total solids weight of the composition.
In certain embodiments in which a bis(sulfonyl)alkanol-containing polythioether or prepolymer is terminated with thiol groups, a suitable curing agent is an unsaturated compound such as an acrylic or methacrylic ester of a polyol, unsaturated synthetic or naturally occurring resin compounds, triallyl cyanurate, and olefin terminated derivatives of sulfur-containing compound such as polythioethers.
In certain embodiments, such as when amine and/or hydroxyl-terminated bis(sulfonyl)alkanol-containing polythioethers or prepolymers thereof are used, compositions provided by the present disclosure may comprise an isocyanate curing agent such as a diisocyanate and/or triisocyanate curing agent. Examples of suitable isocyanate curing agents include toluene diisocyanate, and combinations of any of the foregoing. Isocyanate curing agents are commercially available and include, for example, products under the tradenames Baydur® (Bayer MaterialScience), Desmodur® (Bayer MaterialScience), Solubond® (DSM), ECCO (ECCO), Vestanat® (Evonik), Irodur® (Huntsman), RhodocoatTM (Perstorp), and Vanchem® (V.T. Vanderbilt). In certain embodiments, a polyisocyanate curing agent comprises isocyanate groups that are reactive with thiol groups and that are less reactive with Michael acceptor groups. Examples of useful curing agents that are reactive with amine groups include polymeric polyisocyanates, non-limiting examples of which include polyisocyanates having backbone linkages chosen from urethane linkages (—NH—C(O)—O—), thiourethane linkages (—NH—C(O)—S—), thiocarbamate linkages (—NH—C(S)—O—), dithiourethane linkages (—NH—C(S)—S—), and combinations of any of the foregoing.
In certain embodiments, an isocyanate curing agent comprises an isocyanate-functional polymer. Examples of suitable isocyanate-functional polymers include the isocyanate-functional polyformal polymers disclosed in U.S. patent application Ser. No. 13/051,002. In general, when used as a curing agent, an isocyanate-functional polymer has a molecular weight less than about 2,000 Daltons, less than about 1,500, Daltons, less than about 1,000 Daltons, and in certain embodiments, less than about 500 Daltons.
In such compositions, an isocyanate curing agent may comprise about 0.5 wt % to about 20 wt % of the composition, from about 1 wt % to about 10 wt %, from about 2 wt % to about 8 wt %, from about 2 wt % to about 6 wt %, and in certain embodiments, from about 3 wt % to about 5 wt % of the composition, where wt % is based on the total solids weight of the composition.
In certain embodiments, such as when isocyanate-terminated bis(sulfonyl)alkanol-containing polythioethers or prepolymers thereof are used, compositions provided by the present disclosure comprise an amine curing agent. Examples of useful curing agents that are reactive with isocyanate groups include diamines, polyamines, polythiols, and polyols, including those disclosed herein.
In certain embodiments, such as when Michael acceptor-terminated bis(sulfonyl)alkanol-containing polythioethers or prepolymers thereof are used, compositions provided by the present disclosure comprise a curing agent selected from a monomeric thiol, a polythiol, a polyamine, and a blocked polyamine.
Curing agents useful in compositions provided by the present disclosure include compounds that are reactive with the terminal groups of the bis(sulfonyl)alkanol-containing polythioether, such as compounds that are reactive with hydroxyl groups, alkenyl groups, epoxy groups, thiol groups, amine groups, or isocyanate groups.
Examples of useful curing agents that are reactive with hydroxyl groups include diisocyanates and polyisocyanates, examples of which are disclosed herein.
Examples of useful curing agents that are reactive with alkenyl groups include dithiols and polythiols, examples of which are disclosed herein.
Polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure can hydrolyze in the presence of water inducing self-polymerization via condensation. Catalysts for use with polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether include organotitanium compounds such as tetraisopropoxy titanium, tetra-tert-butoxy titanium, titanium di(isopropoxy)bis(ethylacetoacetate), and titanium di(isopropoxy)bis(acetylacetoacetate); organic tin compounds dibutyltin dilaurate, dibutyltin bisacetylacetoacetate, and tin octylate; metal dicarboxylates such as lead dioctylate; organozirconium compounds such as zirconium tetraacetyl acetonate; and organoaluminum compounds such as aluminum triacetyl-acetonate. Other examples of suitable catalysts for moisture curing include diisopropoxy bis(ethyl acetoacetonate)titanium, diisopropoxy bis(acetyl acetonate)titanium, and dibutoxy bis(methyl acetoacetonate)titanium. It can be appreciated that because the curing agent for polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether can be atmospheric moisture, it is not necessary to include a curing agent to a curable composition containing polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether. Therefore, compositions comprising polyalkoxysilyl-terminated bis(sulfonyl)alkanol-containing polythioether and a curing agent for the polyalkoxysilyl group refer to atmospheric moisture.
Compositions provided by the present disclosure may contain from about 90% to about 150% of the stoichiometric amount, from about 95% to about 125%, and in certain embodiments, from about 95% to about 105% of the amount of the selected curing agent(s).
Additional Sulfur-Containing Polymers
In certain embodiments, compositions provided by the present disclosure comprise, in addition to a bis(sulfonyl)alkanol-containing polythioether or prepolymer thereof, or a reaction product of any one of the reactions disclosed herein, or a combination of any of the foregoing, one or more additional sulfur-containing polymers. A sulfur-containing polymer can be any polymer having at least one sulfur atom in the repeating unit, including, but not limited to, polymeric thiols, polythiols, thioethers, polythioethers, polyformals, and polysulfides. A “thiol,” as used herein, refers to a compound comprising a thiol or mercaptan group, that is, an “SH” group, either as the sole functional group or in combination with other functional groups, such as hydroxyl groups, as is the case with, for example, thioglycerols. A polythiol refers to such a compound having more than one SH group, such as a dithiol or higher functionality thiol. Such groups are typically terminal and/or pendant such that they have an active hydrogen that is reactive with other functional groups. A polythiol can comprise both a terminal and/or pendant sulfur (—SH) and a non-reactive sulfur atom (—S— or —S—S—). Thus, the term polythiol generally encompasses polythioethers and polysulfides.
Examples of additional sulfur-containing polymers useful in compositions provided by the present disclosure include, for example, those disclosed in U.S. Pat. Nos. 6,172,179, 6,509,418, and 7,009,032. In certain embodiments, compositions provided by the present disclosure comprise a polythioether having the structure:

—R1—[—S—(CH2)2—O—[—R2—O—]m—(CH2)2—S—R1—]n—

wherein R1 is selected from a C2-6 alkanediyl, C6-8 cycloalkanediyl, C6-10 cycloalkanealkanediyl, —[(—CH2—)s—X—]q—(—CH2—)r—, and —[(—CH2—)s—X—]q—(—CH2—)r— in which at least one —CH2— unit is substituted with a methyl group; R2 is selected from C2-6 alkanediyl, C6-8 cycloalkanediyl, C6-10 cycloalkanealkanediyl, and —[(—CH2—)s—X—]q—(CH2—)r—; X is selected from O, S, and —NR5—, where R5 is selected from hydrogen and methyl; m is an integer from 0 to 10; n is an integer from 1 to 60; p is an integer from 2 to 6; q is an integer from 1 to 5, and r is an integer from 2 to 10. Such polythioethers are described in U.S. Pat. No. 6,172,179 at col. 2, line 29 to col. 4, line 34.

The one or more additional sulfur-containing polymers may be difunctional or multifunctional, for example, having from 3 to 6 terminal groups, or a mixture thereof.
In certain embodiments, compositions provided by the present disclosure comprise from about 10 wt % to about 90 wt % of a sulfur-containing polymer provided by the present disclosure, from about 20 wt % to about 80 wt %, from about 30 wt % to about 70 wt %, and in certain embodiments from about 40 wt % to about 60 wt %, where wt % is based on the total weight of all non-volatile components of the composition (i.e., the dry weight).
As used herein, the term polysulfide refers to a polymer that contains one or more sulfide linkages, i.e., —Sx— linkages, where x is from 2 to 4, in the polymer backbone and/or in pendant positions on the polymer chain. In certain embodiments, the polysulfide polymer will have two or more sulfur-sulfur linkages. Suitable polysulfides are commercially available, for example, from Akzo Nobel and Toray Fine Chemicals under the names Thiokol-LP and Thioplast®. Thioplast® products are available in a wide range of molecular weights ranging, for example, from less than 1,100 to over 8,000, with molecular weight being the average molecular weight in grams per mole. In some cases, the polysulfide has a number average molecular weight of 1,000 Daltons to 4,000 Daltons. The crosslink density of these products also varies, depending on the amount of crosslinking agent used. The —SH content, i.e., thiol or mercaptan content, of these products can also vary. The mercaptan content and molecular weight of the polysulfide can affect the cure speed of the polymer, with cure speed increasing with molecular weight.
Polyformal prepolymers useful in aerospace sealant applications are disclosed, for example, in U.S. Application Publication No. 2012/0234205 and in U.S. Application Publication No. 2012/0238707.
In certain embodiments, the sulfur-containing polymer is selected from a polythioether and a polysulfide, and a combination thereof. In certain embodiments a sulfur-containing polymer comprises a polythioether, and in certain embodiments, a sulfur-containing polymer comprises a polysulfide. A sulfur-containing polymer may comprise a mixture of different polythioethers and/or polysulfides, and the polythioethers and/or polysulfides may have the same or different functionality. In certain embodiments, a sulfur-containing polymer has an average functionality from 2 to 6, from 2 to 4, from 2 to 3, and in certain embodiments, from 2.05 to 2.5. For example, a sulfur-containing polymer can be selected from a difunctional sulfur-containing polymer, a trifunctional sulfur-containing polymer, and a combination thereof.
Compositions provided by the present disclosure may include one or more catalysts. A catalyst can be selected as appropriate for the curing chemistry employed. In certain embodiments, for example, when curing thiol-terminated bis(sulfonyl)alkanol-containing polythioethers or prepolymers and polyepoxides, the catalyst is an amine catalyst. A cure catalyst may be present in an amount from 0.1 to 5 weight percent, based on the total weight of the composition. Examples of suitable catalysts include 1,4-diazabicyclo[2.2.2]octane (DABCO®, commercially available from Air Products, Chemical Additives Division, Allentown, Pa.) and DMP-30® (an accelerant composition including 2,4,6-tris(dimethylaminomethyl)phenol.
In certain embodiments, compositions provided by the present disclosure comprise one or more than one adhesion promoters. A one or more additional adhesion promoter may be present in amount from 0.1 wt % to 15 wt % of a composition, less than 5 wt %, less than 2 wt %, and in certain embodiments, less than 1 wt %, based on the total dry weight of the composition. Examples of adhesion promoters include phenolics, such as Methylon® phenolic resin, and organosilanes, such as epoxy, mercapto or amino functional silanes, such as Silquest® A-187 and Silquest® A-1100. Other useful adhesion promoters are known in the art.
Compositions provided by the present disclosure may comprise one or more different types of filler. Suitable fillers include those commonly known in the art, including inorganic fillers, such as carbon black and calcium carbonate (CaCO3), silica, polymer powders, and lightweight fillers. Suitable lightweight fillers include, for example, those described in U.S. Pat. No. 6,525,168. In certain embodiments, a composition includes 5 wt % to 60 wt % of the filler or combination of fillers, 10 wt % to 50 wt %, and in certain embodiments, from 20 wt % to 40 wt %, based on the total dry weight of the composition. Compositions provided by the present disclosure may further include one or more colorants, thixotropic agents, accelerators, fire retardants, adhesion promoters, solvents, masking agents, or a combination of any of the foregoing. As can be appreciated, fillers and additives employed in a composition may be selected so as to be compatible with each other as well as the polymeric component, curing agent, and or catalyst. Examples of electrically non-conductive fillers include materials such as, but not limited to, calcium carbonate, mica, polyamide, fumed silica, molecular sieve powder, microspheres, titanium dioxide, chalks, alkaline blacks, cellulose, zinc sulfide, heavy spar, alkaline earth oxides, alkaline earth hydroxides, and the like.
In certain embodiments, compositions provided by the present disclosure include low density filler particles. As used herein, low density, when used with reference to such particles means that the particles have a specific gravity of no more than 0.7, in certain embodiments no more than 0.25, and in certain embodiments, no more than 0.1. Suitable lightweight filler particles often fall within two categories—microspheres and amorphous particles. The specific gravity of microspheres may range from 0.1 to 0.7 and include, for example, polystyrene foam, microspheres of polyacrylates and polyolefins, and silica microspheres having particle sizes ranging from 5 to 100 microns and a specific gravity of 0.25 (Eccospheres®). Other examples include alumina/silica microspheres having particle sizes in the range of 5 to 300 microns and a specific gravity of 0.7 (Finite), aluminum silicate microspheres having a specific gravity of from about 0.45 to about 0.7 (Z-Light®), calcium carbonate-coated polyvinylidene copolymer microspheres having a specific gravity of 0.13 (Dualite® 6001AE), and calcium carbonate coated acrylonitrile copolymer microspheres such as Dualite® E135, having an average particle size of about 40 μm and a density of 0.135 g/cc (Henkel). Suitable fillers for decreasing the specific gravity of the composition include, for example, hollow microspheres such as Expancel® microspheres (available from AkzoNobel) or Dualite® low density polymer microspheres (available from Henkel). In certain embodiments, compositions provided by the present disclosure include lightweight filler particles comprising an exterior surface coated with a thin coating, such as those described in U.S. Application Publication No. 2010/0041839 at paragraphs [0016]-[0052], the cited portion of which is incorporated herein by reference.
In certain embodiments, a low density filler comprises less than 2 wt % of a composition, less than 1.5 wt %, less than 1.0 wt %, less than 0.8 wt %, less than 0.75 wt %, less than 0.7 wt % and in certain embodiments, less than 0.5 wt % of a composition, where wt % is based on the total dry solids weight of the composition.
In certain embodiments, compositions provided by the present disclosure comprise at least one filler that is effective in reducing the specific gravity of the composition. In certain embodiments, the specific gravity of a composition is from 0.8 to 1, 0.7 to 0.9, from 0.75 to 0.85, and in certain embodiments, is 0.8. In certain embodiments, the specific gravity of a composition is less than about 0.9, less than about 0.8, less than about 0.75, less than about 0.7, less than about 0.65, less than about 0.6, and in certain embodiments, less than about 0.55.
In certain embodiments, compositions provided by the present disclosure comprise an electrically conductive filler. Electrical conductivity and EMI/RFI shielding effectiveness can be imparted to composition by incorporating conductive materials within the polymer. The conductive elements can include, for example, metal or metal-plated particles, fabrics, meshes, fibers, and combinations thereof. The metal can be in the form of, for example, filaments, particles, flakes, or spheres. Examples of metals include copper, nickel, silver, aluminum, tin, and steel. Other conductive materials that can be used to impart electrical conductivity and EMI/RFI shielding effectiveness to polymer compositions include conductive particles or fibers comprising carbon or graphite. Conductive polymers such as polythiophenes, polypyrroles, polyaniline, poly(p-phenylene)vinylene, polyphenylene sulfide, polyphenylene, and polyacetylene can also be used. Electrically conductive fillers also include high band gap materials such as zinc sulfide and inorganic barium compounds.
Other examples of electrically conductive fillers include electrically conductive noble metal-based fillers such as pure silver; noble metal-plated noble metals such as silver-plated gold; noble metal-plated non-noble metals such as silver plated cooper, nickel or aluminum, for example, silver-plated aluminum core particles or platinum-plated copper particles; noble-metal plated glass, plastic or ceramics such as silver-plated glass microspheres, noble-metal plated aluminum or noble-metal plated plastic microspheres; noble-metal plated mica; and other such noble-metal conductive fillers. Non-noble metal-based materials can also be used and include, for example, non-noble metal-plated non-noble metals such as copper-coated iron particles or nickel plated copper; non-noble metals, e.g., copper, aluminum, nickel, cobalt; non-noble-metal-plated-non-metals, e.g., nickel-plated graphite and non-metal materials such as carbon black and graphite. Combinations of electrically conductive fillers can also be used to meet the desired conductivity, EMI/RFI shielding effectiveness, hardness, and other properties suitable for a particular application.
The shape and size of the electrically conductive fillers used in the compositions of the present disclosure can be any appropriate shape and size to impart electrical conductivity and EMI/RFI shielding effectiveness to the cured composition. For example, fillers can be of any shape generally used in the manufacture of electrically conductive fillers, including spherical, flake, platelet, particle, powder, irregular, fiber, and the like. In certain sealant compositions of the disclosure, a base composition can comprise Ni-coated graphite as a particle, powder or flake. In certain embodiments, the amount of Ni-coated graphite in a base composition can range from 40 wt % to 80 wt %, and in certain embodiments can range from 50 wt % to 70 wt %, based on the total weight of the base composition. In certain embodiments, an electrically conductive filler can comprise Ni fiber. Ni fiber can have a diameter ranging from 10 μm to 50 μm and have a length ranging from 250 μm to 750 μm. A base composition can comprise, for example, an amount of Ni fiber ranging from 2 wt % to 10 wt %, and in certain embodiments, from 4 wt % to 8 wt %, based on the total weight of the base composition.
Carbon fibers, particularly graphitized carbon fibers, can also be used to impart electrical conductivity to compositions of the present disclosure. Carbon fibers formed by vapor phase pyrolysis methods and graphitized by heat treatment and which are hollow or solid with a fiber diameter ranging from 0.1 micron to several microns, have high electrical conductivity. As disclosed in U.S. Pat. No. 6,184,280, carbon microfibers, nanotubes or carbon fibrils having an outer diameter of less than 0.1 μm to tens of nanometers can be used as electrically conductive fillers. An example of graphitized carbon fiber suitable for conductive compositions of the present disclosure include Panex® 3OMF (Zoltek Companies, Inc., St. Louis, Mo.), a 0.921 μm diameter round fiber having an electrical resistivity of 0.00055 Ω-cm.
The average particle size of an electrically conductive filler can be within a range useful for imparting electrical conductivity to a polymer-based composition. For example, in certain embodiments, the particle size of the one or more fillers can range from 0.25 μm to 250 μm, in certain embodiments can range from 0.25 μm to 75 μm, and in certain embodiments can range from 0.25 μm to 60 μm. In certain embodiments, composition of the present disclosure can comprise Ketjenblack® EC-600 JD (Akzo Nobel, Inc., Chicago, Ill.), an electrically conductive carbon black characterized by an iodine absorption of 1,000 mg/g to 11,500 mg/g (J0/84-5 test method), and a pore volume of 480 cm3/100 g to 510 cm3/100 g (DBP absorption, KTM 81-3504). In certain embodiments, an electrically conductive carbon black filler is Black Pearls® 2000 (Cabot Corporation, Boston, Mass.).
In certain embodiments, electrically conductive polymers can be used to impart electrical conductivity or modify the electrical conductivity of compositions of the present disclosure. Polymers having sulfur atoms incorporated into aromatic groups or adjacent to double bonds, such as in polyphenylene sulfide, and polythiophene, are known to be electrically conductive. Other electrically conductive polymers include, for example, polypyrroles, polyaniline, poly(p-phenylene)vinylene, and polyacetylene. In certain embodiments, the sulfur-containing polymers forming a base composition can be polysulfides and/or polythioethers. As such, the sulfur-containing polymers can comprise aromatic sulfur groups and sulfur atoms adjacent to conjugated double bonds to enhance the electrical conductivity of the compositions of the present disclosure.
Compositions of the present disclosure can comprise more than one electrically conductive filler and the more than one electrically conductive filler can be of the same or different materials and/or shapes. For example, a sealant composition can comprise electrically conductive Ni fibers, and electrically conductive Ni-coated graphite in the form of powder, particles or flakes. The amount and type of electrically conductive filler can be selected to produce a sealant composition which, when cured, exhibits a sheet resistance (four-point resistance) of less than 0.50 Ω/cm2, and in certain embodiments, a sheet resistance less than 0.15 Ω/cm2. The amount and type of filler can also be selected to provide effective EMI/RFI shielding over a frequency range of from 1 MHz to 18 GHz for an aperture sealed using a sealant composition of the present disclosure.
In certain embodiments, an electrically conductive base composition can comprise an amount of electrically non-conductive filler ranging from 2 wt % to 10 wt % based on the total weight of the base composition, and in certain embodiments, can range from 3 wt % to 7 wt %. In certain embodiments, a curing agent composition can comprise an amount of electrically non-conductive filler ranging from less than 6 wt % and in certain embodiments ranging from 0.5% to 4% by weight, based on the total weight of the curing agent composition.
Galvanic corrosion of dissimilar metal surfaces and the conductive compositions of the present disclosure can be minimized or prevented by adding corrosion inhibitors to the composition, and/or by selecting appropriate conductive fillers. In certain embodiments, corrosion inhibitors include strontium chromate, calcium chromate, magnesium chromate, and combinations thereof. U.S. Pat. No. 5,284,888 and U.S. Pat. No. 5,270,364 disclose the use of aromatic triazoles to inhibit corrosion of aluminum and steel surfaces. In certain embodiments, a sacrificial oxygen scavenger such as Zn can be used as a corrosion inhibitor. In certain embodiments, the corrosion inhibitor can comprise less than 10% by weight of the total weight of the electrically conductive composition. In certain embodiments, the corrosion inhibitor can comprise an amount ranging from 2% by weight to 8% by weight of the total weight of the electrically conductive composition. Corrosion between dissimilar metal surfaces can also be minimized or prevented by the selection of the type, amount, and properties of the conductive fillers comprising the composition.
In certain embodiments, a bis(sulfonyl)alkanol-containing polythioether and/or bis(sulfonyl)alkanol-containing polythioether prepolymer may comprise from about 50 wt % to about 90 wt % of a composition, from about 60 wt % to about 90 wt %, from about 70 wt % to about 90 wt %, and in certain embodiments, from about 80 wt % to about 90 wt % of the composition, where wt % is based on the total dry solids weight of the composition.
A composition may also include any number of additives as desired. Examples of suitable additives include plasticizers, pigments, surfactants, adhesion promoters, thixotropic agents, fire retardants, masking agents, and accelerators (such as amines, including 1,4-diazabicyclo[2.2.2]octane, DABCO®), and combinations of any of the foregoing. When used, the additives may be present in a composition in an amount ranging, for example, from about 0% to 60% by weight. In certain embodiments, additives may be present in a composition in an amount ranging from about 25% to 60% by weight.
Uses
Compositions provided by the present disclosure may be used, for example, in sealants, coatings, encapsulants, and potting compositions. A sealant includes a composition capable of producing a film that has the ability to resist operational conditions, such as moisture and temperature, and at least partially block the transmission of materials, such as water, fuel, and other liquid and gases. A coating composition includes a covering that is applied to the surface of a substrate to, for example, improve the properties of the substrate such as the appearance, adhesion, wettability, corrosion resistance, wear resistance, fuel resistance, and/or abrasion resistance. A potting composition includes a material useful in an electronic assembly to provide resistance to shock and vibration and to exclude moisture and corrosive agents. In certain embodiments, sealant compositions provided by the present disclosure are useful, e.g., as aerospace sealants and as linings for fuel tanks.
In certain embodiments, compositions, such as sealants, may be provided as multi-pack compositions, such as two-pack compositions, wherein one package comprises one or more thiol-terminated polythioethers provided by the present disclosure and a second package comprises one or more polyfunctional sulfur-containing epoxies provided by the present disclosure. Additives and/or other materials may be added to either package as desired or necessary. The two packages may be combined and mixed prior to use. In certain embodiments, the pot life of the one or more mixed thiol-terminated polythioethers and epoxies is at least 30 minutes, at least 1 hour, at least 2 hours, and in certain embodiments, more than 2 hours, where pot life refers to the period of time the mixed composition remains suitable for use as a sealant after mixing.
Compositions, including sealants, provided by the present disclosure may be applied to any of a variety of substrates. Examples of substrates to which a composition may be applied include metals such as titanium, stainless steel, aluminum, and alloys thereof, any of which may be anodized, primed, organic-coated or chromate-coated; epoxy; urethane; graphite; fiberglass composite; Kevlar®; acrylics; and polycarbonates. In certain embodiments, compositions provided by the present disclosure may be applied to a coating on a substrate, such as a polyurethane coating. In particular, compositions comprising bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure exhibit enhanced adhesion to bare metal and to anodized metal surfaces.
Compositions provided by the present disclosure may be applied directly onto the surface of a substrate or over an underlayer by any suitable coating process known to those of ordinary skill in the art.
Furthermore, methods are provided for sealing an aperture utilizing a composition provided by the present disclosure. These methods comprise, for example, applying a composition provided by the present disclosure to a surface to seal an aperture, and curing the composition. In certain embodiments, a method for sealing an aperture comprises (a) applying a sealant composition provided by the present disclosure to one or more surfaces defining an aperture, (b) assembling the surfaces defining the aperture, and (c) curing the applied sealant composition, to provide a sealed aperture.
In certain embodiments, apertures sealed with a sealant composition of the present disclosure are provided.
In certain embodiments, a composition may be cured under ambient conditions, where ambient conditions refers to a temperature from 20° C. to 25° C., and atmospheric humidity. In certain embodiments, a composition may be cured under conditions encompassing a temperature from a 0° C. to 100° C. and humidity from 0% relative humidity to 100% relative humidity. In certain embodiments, a composition may be cured at a higher temperature such as at least 30° C., at least 40° C., and in certain embodiments, at least 50° C. In certain embodiments, a composition may be cured at room temperature, e.g., 25° C. In certain embodiments, a composition may be cured upon exposure to actinic radiation, such as ultraviolet radiation. As will also be appreciated, the methods may be used to seal apertures on aerospace vehicles including aircraft and aerospace vehicles.
In certain embodiments, the composition achieves a tack-free cure in less than about 2 hours, less than about 4 hours, less than about 6 hours, less than about 8 hours, and in certain embodiments, less than about 10 hours, at a temperature of less than about 200° F.
The time to form a viable seal using curable compositions of the present disclosure can depend on several factors as can be appreciated by those skilled in the art, and as defined by the requirements of applicable standards and specifications. In general, curable compositions of the present disclosure develop adhesion strength within 24 hours to 30 hours, and 90% of full adhesion strength develops from 2 days to 3 days, following mixing and application to a surface. In general, full adhesion strength as well as other properties of cured compositions of the present disclosure becomes fully developed within 7 days following mixing and application of a curable composition to a surface.
Cured compositions disclosed herein, such as cured sealants, exhibit properties acceptable for use in aerospace applications. In general, it is desirable that sealants used in aviation and aerospace applications exhibit the following properties: peel strength greater than 20 pounds per linear inch (pli) on Aerospace Material Specification (AMS) 3265B substrates determined under dry conditions, following immersion in JRF Type I for 7 days, and following immersion in a solution of 3% NaCl according to AMS 3265B test specifications; tensile strength between 300 pounds per square inch (psi) and 400 psi; tear strength greater than 50 pounds per linear inch (pli); elongation between 250% and 300%; and hardness greater than 40 Durometer A. These and other cured sealant properties appropriate for aviation and aerospace applications are disclosed in AMS 3265B, the entirety of which is incorporated herein by reference. It is also desirable that, when cured, compositions of the present disclosure used in aviation and aircraft applications exhibit a percent volume swell not greater than 25% following immersion for one week at 60° C. (140° F.) and ambient pressure in JRF Type I. Other properties, ranges, and/or thresholds may be appropriate for other sealant applications.
In certain embodiments, therefore, compositions provided by the present disclosure are fuel-resistant. As used herein, the term “fuel resistant” means that a composition, when applied to a substrate and cured, can provide a cured product, such as a sealant, that exhibits a percent volume swell of not greater than 40%, in some cases not greater than 25%, in some cases not greater than 20%, in yet other cases not more than 10%, after immersion for one week at 140° F. (60° C.) and ambient pressure in Jet Reference Fluid (JRF) Type I according to methods similar to those described in ASTM D792 (American Society for Testing and Materials) or AMS 3269 (Aerospace Material Specification). Jet Reference Fluid JRF Type I, as employed for determination of fuel resistance, has the following composition: toluene: 28%±1% by volume; cyclohexane (technical): 34%±1% by volume; isooctane: 38%±1% by volume; and tertiary dibutyl disulfide: 1%±0.005% by volume (see AMS 2629, issued Jul. 1, 1989, §3.1.1, etc., available from SAE (Society of Automotive Engineers)).
In certain embodiments, compositions provided herein provide a cured product, such as a sealant, exhibiting a elongation of at least 100% and a tensile strength of at least 400 psi when measured in accordance with the procedure described in AMS 3279, §3.3.17.1, test procedure AS5127/1, §7.7.
In certain embodiments, compositions provide a cured product, such as a sealant, that exhibits a lap shear strength of greater than 200 psi, such as at least 220 psi, at least 250 psi, and, in some cases, at least 400 psi, when measured according to the procedure described in SAE AS5127/1 paragraph 7.8.
In certain embodiments, a cured sealant comprising a composition provided by the present disclosure meets or exceeds the requirements for aerospace sealants as set forth in AMS 3277.
Apertures, including apertures of aerospace vehicles, sealed with compositions provided by the present disclosure are also disclosed.
In certain embodiments, a cured sealant provided by the present disclosure exhibits the following properties when cured for 2 days at room temperature, 1 day at 140° F. and 1 day at 200° F.: a dry hardness of 49, a tensile strength of 428 psi, and an elongation of 266%; and after 7 days in JRF Type I, a hardness of 36, a tensile strength of 312 psi, and an elongation of 247%.
In certain embodiments, compositions provided by the present disclosure exhibit a Shore A hardness (7-day cure) greater than 10, greater than 20, greater than 30, and in certain embodiments, greater than 40; a tensile strength greater than 10 psi, greater than 100 psi, greater than 200 psi, and in certain embodiments, greater than 500 psi; an elongation greater than 100%, greater than 200%, greater than 500%, and in certain embodiments, greater than 1,000%; and a swell following exposure to JRF Type I (7 days) less than 20%.
Cured sealants prepared from bis(sulfonyl)alkanol-containing polythioethers provided by the present disclosure exhibit enhanced tensile strength and enhanced adhesion to metal surfaces. Bis(sulfonyl)alkanols can serve as polydentate ligands in metal chelates. It is believed that similar chelation occurs with exposed metals such as aluminum that enhances the bonding of the bis(sulfonyl)alkanol-containing polythioethers to metal surfaces.
EXAMPLES
Embodiments provided by the present disclosure are further illustrated by reference to the following examples, which describe the synthesis, properties, and uses of certain bis(sulfonyl)alkanol-containing polythioethers and compositions comprising bis(sulfonyl)alkanol-containing polythioethers. It will be apparent to those skilled in the art that many modifications, both to materials, and methods, may be practiced without departing from the scope of the disclosure.
Example 1
Thiol-Terminated Polythioether
1,8-Dimercapto-3,6-dioxaoctane (DMDO; 1995.60 g; 10.95 moles) was charged into a 5-liter 4-necked round-bottomed flask. The flask was equipped with a gas adapter for nitrogen, a paddle stirrer, and a temperature probe. The flask was flushed with nitrogen and the contents heated to 60° C. while stirring. A free radical initiator Vazo®-67 (0.4 1 g) was added into to the flask. Diethylene glycol divinyl ether (1154.51 g, 7.30 moles) was introduced into the reaction mixture over a period of 6.25 h during which time a temperature of 60° C. to 65° C. was maintained. The reaction temperature was raised to 77° C. and two portions of Vazo®-67 (0.045 g each) were added with an interval of 3 hr. The reaction mixture was heated at 94° C. for 2 hr, cooled to 66° C., and evacuated at 66° C. to 74° C./15 mm Hg for 1 hr. The resulting polymer, a dithiol, had a mercaptan equivalent weight of 430.
Example 2
Thiol-Terminated Bis(sulfonyl)alkanol-Containing Polythioether
The dithiol of Example 1 (55.04 g; 0.064 mole) was charged into a 250-mL, 3-necked round-bottomed flask. The flask was equipped with a gas adapter for nitrogen and a paddle stirrer. The contents were evacuated at 7 mm for 30 min and the vacuum was released under nitrogen. Under stirring, base catalyst DBU (1,8-diazabicycloundec-7-ene; 0.013 g) was added followed by ethanol (10 g) and the flask equipped with a temperature probe. Under cooling (with a water bath), a solution of 1,3-bis(vinylsulfonyl)-2-propanol (7.69 g; 0.032 mole) in tetrahydrofuran (90 g) was dropped over a period of 2 h at temperature from 19° C. to 20° C. The water bath was removed and the reactants stirred at ambient temperature for an additional 2 hr. The mercaptan equivalent was used to determine when the reaction was complete. After the solvents were removed, a liquid difunctional polymer was provided having a mercaptan equivalent weight of 1,166 and a viscosity of 81 poise.
Example 3
Thiol-Terminated Bis(sulfonyl)alkanol-Containing Polythioether Prepolymer
The dithiol of Example 2 (62 g; 0.0177 mole) was charged into a 250-mL, 3-necked round-bottomed flask. While stirring, a solution of triallylcyanurate (TAC) (0.93 g; 0.0037 mole) and diethylene glycol divinyl ether (0.22 g; 0.0014 mole) in toluene (1.0 g) were introduced into the reaction mixture and the contents heated at 77° C. Seven portions (0.016 g each) of radical initiator Vazo®-67 were added at an interval of 1 h to complete the reaction. Removal of solvents under vacuum provided a polymer having theoretical thiol functionality of 2.21, a mercaptan equivalent weight of 1,659; and a viscosity of 195 poise.
Example 4
Bis(sulfonyl)alkanol-Containing Polythioether Sealant
The prepolymer of Example 3 (14.93 g; 0.009 equivalent) and calcium carbonate (Socal® N2R; 4.48 g) were charged into a mixing cup (capacity: 60 g) of a Hauschild mixer (model: DAC 600 FVZ). The contents were combined by hand mixing and then mixed in Hauschild mixer for 30 seconds (speed: 2300 RPM). The contents were again blended by hand and then mixed in the Hauschild mixer for another 30 seconds. An epoxy accelerator S-5304 (available from PPG Aerospace; 3.60 g, 0.009 equivalent) was added. The contents were combined by hand mixing and then mixed in a Hauschild mixer for 30 seconds. A base catalyst DABCO 33-LV (0.12 g) was added. The contents were hand mixed and then mixed in a Hauschild mixer for 30 seconds.
Part of the mix was used to make a cure plug for hardness and remaining was used to make adhesion specimens (approximate dimension: 4 cm×1.4 cm×0.3 cm) on seven surfaces: Scotchbrited bare aluminum; Mil-C-27725; Scotchbrited Titanium B; Scotchbrited Titanium C; Alodine 1200; Anodized SAA and Anodized CAA. All specimens were subjected to a cure cycle of room temperature/20 h; 60° C./27 h. After the samples were cured, the hardness was 40 (Shore A). The adhesion, estimated by peeling/cutting the cured sealant from the metal surface, for six out of seven surfaces was very good (100% cohesive failure); however, the cured specimen did not adhere to Alodine 1200 (0% cohesive failure).
Example 5
Thiol-Terminated Bis(sulfonyl)alkanol-Containing Difunctional Polythioether
The dithiol of Example 1 (636.40 g; 0.74 mole) was charged into a 2-liter, 4-necked round-bottomed flask. The flask was equipped with a gas adapter for nitrogen and a paddle stirrer. The contents were evacuated at 8 mm for 1 h and the vacuum was released under nitrogen. While stirring, ethanol (116 g) was added followed by base catalyst DBU (0.145 g) and the flask. Under cooling (with a water bath), a solution of 1,3-bis(vinylsulfonyl)-2-propanol (88.91 g; 0.37 mole) in tetrahydrofuran (1.04 kg) was dropped over a period of about 2 h at temperature from 23° C. to 27° C. The mercaptan equivalent was used to determine the progress of the reaction. The water bath was removed and the reactants stirred at room temperature for an additional 3 h. Removal of solvents provided a difunctional polymer having a mercaptan equivalent weight of 1,296 and a viscosity of 107 poise.
Example 6
Thiol Terminated Bis(sulfonyl)alkanol-Containing Polythioether Prepolymer
The difunctional polymer of Example 5 (725.29 g; 0.2798 mole) was charged into a 2-liter, 4-necked round-bottomed flask. The flask was equipped with a gas adapter for nitrogen and a paddle stirrer. The contents were flushed with nitrogen. While stirring, a solution of triallylcyanurate (10.22 g; 0.041 mole) and diethylene glycol divinyl ether (0.49 g; 0.0031 mole) in toluene (5.0 mL) was introduced to the reaction mixture and the contents were heated at 70° C. Fifteen portions (0.084 g each) of radical initiator Vazo®-67 were added at intervals of 1 h to complete the reaction. Removal of solvents under vacuum provided a polymer having a theoretical functionality of 2.21, mercaptan equivalent weight of 1675 and viscosity of 238 poise.
Example 7
Bis(sulfonyl)alkanol-Containing Polythioether Sealant
The prepolymer of Example 6 (30 g; 0.0179 equivalent) and calcium carbonate (Socal® N2R; 9.00 g) were charged into a mixing cup (capacity: 100 g) of a Hauschild mixer. The contents were handmixed and mixed in Hauschild mixer for 30 seconds (speed: 2300 RPM). The contents were subjected to two rounds of handmixing and further mixing in the Hauschild mixer for 4 min. The contents were cooled to ambient temperature. An epoxy accelerator, S-5304 (available from PPG Aerospace; 7.16 g, 0.0179 equivalent), was added. The contents were subjected to two rounds of handmixing and further mixing in the Hauschild mixer for 30 seconds. Base catalyst DABCO 33-LV (0.24 g) was added. The contents were handmixed, mixed further in the Hauschild mixer for 30 seconds and poured in a grid to make a flowout (approximate dimension: length: 6 inches; width: 3.2 inches; thickness: 0.1 inches). The sealant specimen was subjected to a cure cycle of room temperature/7 days; followed by curing at 140° F./24 h. The cured sealant had a hardness of 48 Shore A, a tensile strength of 373 psi, and an elongation of 472%.
Finally, it should be noted that there are alternative ways of implementing the embodiments disclosed herein. Accordingly, the present embodiments are to be considered as illustrative and not restrictive. Furthermore, the claims are not to be limited to the details given herein, and are entitled to their full scope and equivalents thereof.

## Claims

1. A bis(sulfonyl)alkanol-containing polythioether comprising a moiety of Formula (10):


—S(O)2—R10—CH(—OH)—R10—S(O)2—  (10)


wherein each R10 is independently selected from a C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.

2. The polythioether of claim 1, comprising a moiety of Formula (1):


-A-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-  (1)


wherein:
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):


—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently comprises —O—, —S—, and —NR5—, wherein R5 is selected from hydrogen and methyl; and

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60; and
p is an integer from 2 to 6.

3. The polythioether of claim 1, wherein each R9 is ethane-diyl and each R10 is methane-diyl.

4. The polythioether of claim 1, wherein the polythioether comprises a bis(sulfonyl)alkanol-containing polythioether of Formula (3), a bis(sulfonyl)alkanol-containing polythioether of Formula (3a), or a combination thereof:


R6-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-R6  (3)



{R6-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (3a)

wherein:
N is an integer from 1 to 10;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):


—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)


wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently —O—, —S—, or —NR5—, wherein R5 is selected from hydrogen and methyl;

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60; and

p is an integer from 2 to 6; B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6;
each V is a group comprising a terminal group reactive with terminal thiol groups; and
each —V′— is derived from the reaction of —V with a thiol; and

each R6 independently comprises hydrogen or a moiety having a terminal reactive group.

5. The polythioether of claim 4, wherein each R6 is hydrogen.

6. The polythioether of claim 4, wherein each R9 is ethane-diyl and each R10 is methane-diyl.

7. The polythioether of claim 4, wherein each R6 is the same and the terminal reactive group is selected from —SH, —CH═CH2, —NH2, —OH, an epoxy group, a polyalkoxysilyl group, an isocyanate group, and a Michael acceptor group.

8. A thiol-terminated bis(sulfonyl)alkanol-containing polythioether comprising the reaction product of reactants comprising:
(a) a thiol-terminated polythioether comprising a thiol-terminated polythioether of Formula (4), a thiol-terminated polythioether of Formula (4a), or a combination thereof:


HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)



{HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—V′—}zB  (4a)


wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently comprises —O—, —S—, or —NR5—, wherein R5 is selected from hydrogen and methyl;

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60;
p is an integer from 2 to 6; and
B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6;
each V is a group comprising a terminal group reactive with terminal thiol groups; and

each —V′— is derived from the reaction of —V with a thiol; and

(b) a bis(sulfonyl)alkanol of Formula (5):


R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)


wherein
each R8 is independently selected from a group having a terminal group reactive with a terminal thiol group; and
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH.

9. The polythioether of claim 8, wherein the bis(sulfonyl)alkanol comprises a bis(vinylsulfonyl)alkanol of Formula (5a):


CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2  (5a).

10. The polythioether of claim 8, wherein the polythioether of Formula (4) comprises the reaction product of 1,8-dimercapto-3,6-dioxaoctane and diethylene glycol divinyl ether.

11. The polythioether of claim 8, wherein the polythioether of Formula (4a) comprises the reaction product of 1,8-dimercapto-3,6-dioxaoctane, diethylene glycol divinyl ether, and triallyl cyanurate.

12. A thiol-terminated bis(sulfonyl)alkanol-containing polythioether prepolymer comprising the reaction product of reactants comprising:
(a) a thiol-terminated bis(sulfonyl)alkanol-containing polythioether comprising a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a), or a combination thereof:


H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)



{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)



wherein:
N is an integer from 1 to 10;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):


—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently —O—, —S—, or —NR5—, wherein R5 is selected from hydrogen and methyl;

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60; and
p is an integer from 2 to 6;


B represents a core of a z-valent, alkenyl-terminated polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6; and
each V is a group comprising a terminal alkenyl group; and

each —V′— is derived from the reaction of —V with a thiol; and
(b) a polyalkenyl compound.

13. The prepolymer of claim 12, wherein the thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), and the polyalkenyl compound comprises diethylene glycol divinyl ether, triallyl cyanurate, or a combination thereof.

14. A method of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6), comprising reacting (N+1) moles of a thiol-terminated polythioether of Formula (4) with (N) moles of a bis(sulfonyl)alkanol of Formula (5):


H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)



HS—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—SH  (4)



R8—S(O)2—R10—CH(—OH)—R10—S(O)2—R8  (5)


wherein:
N is an integer from 1 to 10;
each R8 is independently selected from a moiety comprising a terminal group reactive with a terminal thiol group;
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is independently selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):


—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently comprises —O—, —S—, or —NR5—, wherein R5 comprises hydrogen or methyl; and

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60; and
p is an integer from 2 to 6.

15. The polythioether of claim 14, wherein the bis(sulfonyl)alkanol comprises a bis(vinylsulfonyl)alkanol of Formula (5a):


CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2  (5a).

16. A method of preparing a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6a) comprising reacting (z) moles of a thiol-terminated bis(sulfonyl)alkanol-containing polythioether of Formula (6) with one (1) mole of a polyfunctionalizing agent of Formula (7):


{H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-V′—}zB  (6a)



H-A-[-R9—S(O)2—R10—CH(—OH)—R10—S(O)2—R9-A-]N-H  (6)



B{V}z  (7)


wherein:
each R9 is a moiety derived from the reaction of a bis(sulfonyl)-alkanol with thiol groups;
each R10 is selected from C1-3 alkanediyl and substituted C1-3 alkanediyl, wherein one or more substituent groups is —OH;
each A is independently a moiety of Formula (2):


—S—R1—[—S—(CH2)p—O—(R2—O)m—(CH2)2—S—R1—]n—S—  (2)

wherein:
each R1 independently comprises C2-10 alkanediyl, C6-8 cycloalkanediyl, C6-10 alkanecycloalkanediyl, C5-8 heterocycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein:
s is an integer from 2 to 6;
q is an integer from 1 to 5;
r is an integer from 2 to 10;
each R3 independently comprises hydrogen or methyl; and
each X independently comprises —O—, —S—, or —NR5—, wherein R5 comprises hydrogen or methyl;

each R2 independently comprises C1-10 alkanediyl, C6-8 cycloalkanediyl, C6-14 alkanecycloalkanediyl, or —[(—CHR3—)s—X—]q—(—CHR3—)r—, wherein s, q, r, R3, and X are as defined for R1;
m is an integer from 0 to 50;
n is an integer from 1 to 60; and
p is an integer from 2 to 6; and


B represents a core of a z-valent polyfunctionalizing agent B(—V)z wherein:
z is an integer from 3 to 6;
each V is a group comprising a terminal group reactive with a terminal thiol group; and
each —V′— is derived from the reaction of —V with a thiol.

17. The polythioether of claim 16, wherein the bis(sulfonyl)alkanol comprises a bis(vinylsulfonyl)alkanol of Formula (5a):


CH2═CH—S(O)2—R10—CH(—OH)—R10—S(O)2—CH═CH2  (5a).

18. A composition comprising:
(a) the bis(sulfonyl)alkanol-containing polythioether of claim 1; and
(b) a curing agent comprising two or more terminal groups that are reactive with terminal groups of the bis(sulfonyl)alkanol-containing polythioether of claim 1.

19. The composition of claim 18, wherein the terminal groups of the bis(sulfonyl)alkanol-containing polythioether is thiol terminated and the curing agent comprises a polyepoxy.

20. The composition of claim 18, comprising a sulfur-containing prepolymer, wherein the sulfur-containing prepolymer is selected from a polythioether prepolymer, a polysulfide prepolymer, a polyformal prepolymer, and a combination of any of the foregoing.