# Patent

## Title
Liquid crystal composition and liquid crystal display device

## Abstract

A liquid crystal composition and an AM liquid crystal display device are described. The liquid crystal composition has a negative dielectric anisotropy, contains a specific compound having a large negative dielectric anisotropy as a first component and a two-ring compound having a small viscosity as a second component, and may further contain a specific compound having a large negative dielectric anisotropy as a third component, a specific compound having a small viscosity as a fourth component and a specific compound having a large negative dielectric anisotropy as a fifth component. The AM liquid crystal display device includes the liquid crystal composition.

## Background
CROSS-REFERENCE TO RELATED APPLICATION
This application is a 371 application of an international PCT application serial no. PCT/JP2013/053114, filed on Feb. 8, 2013, which claims the priority benefit of Japan application no. 2012-029089, filed on Feb. 14, 2012. The entirety of each of the above-mentioned patent applications is hereby incorporated by reference herein and made a part of this specification.
TECHNICAL FIELD
The invention relates to a liquid crystal composition mainly suitable for use in an active matrix (AM) device and so forth, and an AM device and so forth containing the composition. More specifically, the invention relates to a liquid crystal composition having a negative dielectric anisotropy, and a device that includes the composition and has a mode such as an in-plane switching (IPS) mode, a vertical alignment (VA) mode, a fringe field switching (FFS) mode, a polymer sustained alignment (PSA) mode, or a field induced photo-reactive alignment (FPA) mode.
BACKGROUND ART
In a liquid crystal display device, a classification based on an operating mode for liquid crystals includes a phase change (PC) mode, a twisted nematic (TN) mode, a super twisted nematic (STN) mode, an electrically controlled birefringence (ECB) mode, an optically compensated bend (OCB) mode, an in-plane switching (IPS) mode, a vertical alignment (VA) mode, a fringe field switching (FFS) mode, a polymer sustained alignment (PSA) mode and a field induced photo-reactive alignment (FPA) mode. A classification based on a driving mode in the device includes a passive matrix (PM) and an active matrix (AM). The PM is classified into static, multiplex and so forth, and the AM is classified into a thin film transistor (TFT), a metal insulator metal (MIM) and so forth. The TFT is further classified into amorphous silicon and polycrystal silicon. The latter is classified into a high temperature type and a low temperature type according to a production process. A classification based on a light source includes a reflective type utilizing natural light, a transmissive type utilizing backlight and a transflective type utilizing both the natural light and the backlight.
The devices contain a liquid crystal composition having suitable characteristics. The liquid crystal composition has a nematic phase. General characteristics of the composition should be improved to obtain an AM device having good general characteristics. Table 1 below summarizes a relationship of the general characteristics between two aspects. The general characteristics of the composition will be further explained based on a commercially available AM device. A temperature range of the nematic phase relates to a temperature range in which the device can be used. A preferred maximum temperature of the nematic phase is about 70° C. or higher and a preferred minimum temperature of the nematic phase is about −20° C. or lower. Viscosity of the composition relates to a response time in the device. A short response time is preferred for displaying moving images on the device. Accordingly, a small viscosity in the composition is preferred. A small viscosity at a low temperature is further preferred.







TABLE 1







General Characteristics of Composition and AM Device










General Characteristics of
General Characteristics of AM


No.
Composition
Device





1
Wide temperature range of a
Wide usable temperature range



nematic phase


2
Small viscosity1)
Short response time


3
Suitable optical anisotropy
Large contrast ratio


4
Large positive or negative
Low threshold voltage,



dielectric anisotropy
Small electric power consumption,




Large contrast ratio


5
Large specific resistance
Large voltage holding ratio and




Large contrast ratio


6
High stability to
Long service life



ultraviolet light and heat





1)A liquid crystal composition can be injected into a liquid crystal cell in a shorter period of time.






An optical anisotropy of the composition relates to a contrast ratio in the device. A product (Δn×d) of the optical anisotropy (Δn) of the composition and a cell gap (d) in the device is designed so as to maximize the contrast ratio. A suitable value of the product depends on the type of the operating mode. The suitable value is in the range of about 0.30 micrometer to about 0.40 micrometer in a device having the VA mode, and in the range of about 0.20 micrometer to about 0.30 micrometer in a device having the IPS mode or the FFS mode. In the above case, a composition having a large optical anisotropy is preferred for a device having a small cell gap. A large absolute value of dielectric anisotropy in the composition contributes to a low threshold voltage, a small electric power consumption and a large contrast ratio in the device. Accordingly, the large absolute value of dielectric anisotropy is preferred. A large specific resistance in the composition contributes to a large voltage holding ratio and a large contrast ratio in the device. Accordingly, a composition having a large specific resistance at room temperature and also at a high temperature in an initial stage is preferred. A composition having a large specific resistance at room temperature and also at a high temperature even after the device has been used for a long period of time is preferred. Stability of the composition to ultraviolet light and heat relates to a service life of the liquid crystal display device. In the case where the stability is high, the device has a long service life. Such characteristics are preferred for an AM device for use in a liquid crystal projector, a liquid crystal television and so forth.
A composition having a positive dielectric anisotropy is used for an AM device having the TN mode. On the other hand, a composition having a negative dielectric anisotropy is used for an AM device having the VA mode. A composition having a positive or negative dielectric anisotropy is used for an AM device having the IPS mode or the FFS mode. A composition having a positive or negative dielectric anisotropy is used for an AM device having the PSA mode or the FPA mode. Examples of the liquid crystal composition are disclosed in Patent literature 1.
CITATION LIST
Patent Literature
Patent literature 1: WO 1999/021815 A.
A desirable AM device has characteristics such as a wide temperature range in which a device can be used, a short response time, a large contrast ratio, a low threshold voltage, a large voltage holding ratio and a long service life. A shorter response time even by one millisecond is desirable. Thus, desirable characteristics of a composition include a high maximum temperature of a nematic phase, a low minimum temperature of the nematic phase, a small viscosity, a suitable optical anisotropy, a large positive or negative dielectric anisotropy, a large specific resistance, a high stability to ultraviolet light and a high stability to heat.
SUMMARY OF INVENTION
Technical Problem
One of the aims of the invention is to provide a liquid crystal composition satisfying at least one of characteristics such as a high maximum temperature of a nematic phase, a low minimum temperature of the nematic phase, a small viscosity, a suitable optical anisotropy, a large negative dielectric anisotropy, a large specific resistance, a high stability to ultraviolet light and a high stability to heat. Another aim is to provide a liquid crystal composition having a suitable balance regarding at least two of the characteristics, in particular, a liquid crystal composition satisfying a low minimum temperature, a low threshold voltage and a large negative dielectric anisotropy. A further aim is to provide a liquid crystal display device including such a composition. An additional aim is to provide a composition having characteristics such as a suitable optical anisotropy to be a small optical anisotropy or a large optical anisotropy, a large negative dielectric anisotropy and a high stability to ultraviolet light, and is to provide an AM device having a short response time, a large voltage holding ratio, a large contrast ratio, a long service life and so forth.
Solution to Problem
The invention concerns a liquid crystal composition that has a negative dielectric anisotropy and contains at least one compound selected from the group of compounds represented by formula (1) as a first component and at least one compound selected from the group of compounds represented by formula (2) as a second component, and a liquid crystal display device including the composition:




wherein R1 is alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;

R2, R3 and R4 are independently alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen and at least one methylene may be replaced by oxygen;

ring A and ring B are independently





in the rings, at least one hydrogen may be replaced by halogen;

X1 and X2 are independently fluorine or chlorine;

Y1 is hydrogen or methyl;

Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and

m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3.

Advantageous Effects of Invention
An advantage of the invention is a liquid crystal composition satisfying at least one of characteristics such as a high maximum temperature of a nematic phase, a low minimum temperature of the nematic phase, a small viscosity, a suitable optical anisotropy, a large negative dielectric anisotropy, a low threshold voltage, a large specific resistance, a high stability to ultraviolet light, and a high stability to heat. One aspect of the invention is a liquid crystal composition having a suitable balance regarding at least two of the characteristics. Another aspect is a liquid crystal display device including such a composition. A further aspect is a composition having a suitable optical anisotropy, a large negative dielectric anisotropy and a high stability to ultraviolet light and so forth, and an AM device having a short response time, a large voltage holding ratio, a large contrast ratio, a long service life and so forth.


PREFERRED EMBODIMENTS OF THE INVENTION
Usage of terms herein is as described below. A liquid crystal composition or a liquid crystal display device according to the invention may be occasionally abbreviated as “composition” or “device,” respectively. The liquid crystal display device is a generic term for a liquid crystal display panel and a liquid crystal display module. “Liquid crystal compound” means a compound having a liquid crystal phase such as a nematic phase or a smectic phase, or a compound having no liquid crystal phase but being useful as a component of the composition. Such a useful compound has a six-membered ring such as 1,4-cyclohexylene and 1,4-phenylene, and a rod-like molecular structure. An optically active compound and a polymerizable compound may be occasionally added to the composition. Even in the case where the compounds are liquid crystalline, the compounds are classified as an additive herein. At least one compound selected from the group of compounds represented by formula (1) may be occasionally abbreviated as “compound (1).” “Compound (1)” means one compound or two or more compounds represented by formula (1). A same rule applies to any other compound represented by any other formula. An expression “at least one” in the context of “replaced” shows that not only a position but also the number can be freely selected.
A higher limit of a temperature range of the nematic phase may be abbreviated as “maximum temperature.” A lower limit of the temperature range of the nematic phase may be abbreviated as “minimum temperature.” An expression “having a large specific resistance” means that the composition has a large specific resistance at room temperature and also at a temperature close to the maximum temperature of the nematic phase in an initial stage, and that the composition has a large specific resistance at room temperature and also at a temperature close to the maximum temperature of the nematic phase even after the device has been used for a long period of time. An expression “having a large voltage holding ratio” means that the device has a large voltage holding ratio at room temperature and also at a high temperature in an initial stage, and that the device has a large voltage holding ratio at room temperature and also at a temperature close to the maximum temperature of the nematic phase even after the device has been used for a long period of time. When characteristics such as an optical anisotropy are explained, values obtained according to the measuring methods described in Examples will be used. A first component includes one compound or two or more compounds. “Ratio of the first component” is expressed in terms of weight percent (wt %) of the first component based on the total weight of the liquid crystal composition. A ratio of a second component or the like is also expressed in a similar manner. A ratio of the additive mixed with the composition is expressed in terms of weight percent (wt %) or weight parts per million (ppm) based on the total weight of the liquid crystal composition.
A symbol R2 is used for a plurality of compounds in chemical formulas of component compounds. In two arbitrary compounds among the plurality of compounds, a group to be selected by R2 may be identical or different. In one case, for example, R2 of compound (1) is ethyl and R2 of compound (1-1) is ethyl. In another case, R2 of compound (1) is ethyl and R2 of compound (1-1) is propyl. A same rule applies to a symbol R1, R5 or the like.
The invention includes the items described below.
Item 1. A liquid crystal composition that has a negative dielectric anisotropy and includes at least one compound selected from the group of compounds represented by formula (1) as a first component and at least one compound selected from the group of compounds represented by formula (2) as a second component:




wherein R1 is alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;

R2, R3 and R4 are independently alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen and at least one methylene may be replaced by oxygen;

ring A and ring B are independently





in the rings, at least one hydrogen may be replaced by halogen;

X1 and X2 are independently fluorine or chlorine;

Y1 is hydrogen or methyl;

Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and

m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3.

Item 2. The liquid crystal composition according to item 1, wherein the first component is at least one compound selected from the group of compounds represented by formula (1-1) to formula (1-4):




wherein R1 is alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;

R2 is alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen and at least one methylene may be replaced by oxygen.

Item 3. The liquid crystal composition according to item 1,
wherein the first component is at least one compound selected from the group of compounds represented by formula (1-1) according to item 2.
Item 4. The liquid crystal composition according to item 1, wherein the first component is at least one compound selected from the group of compounds represented by formula (1-3) according to item 2.
Item 5. The liquid crystal composition according to item 1, wherein the first component is at least one compound selected from the group of compounds represented by formula (1-4) according to item 2.
Item 6. The liquid crystal composition according to any one of items 1 to 5, wherein, in the first component, R1 is alkyl having 1 to 12 carbons in which one or two hydrogens are replaced by halogen in formula (1) according to item 1 or formula (1-1) to formula (1-4) according to item 2.
Item 7. The liquid crystal composition according to items 1 to 6, wherein, in the second component, R3 or R4 is alkenyl having 2 to 12 carbons in which at least one hydrogen may be replaced by halogen, or alkenyl having 2 to 12 carbons in which at least one methylene may be replaced by oxygen in formula (2) according to item 1.
Item 8. The liquid crystal composition according to any one of items 1 to 7, wherein a ratio of the first component is in the range of 3 wt % to 90 wt %, and a ratio of the second component is in the range of 10 wt % to 97 wt %, based on the total weight of the liquid crystal composition.
Item 9. The liquid crystal composition according to any one of items 1 to 8, further containing at least one compound selected from the group of compounds represented by formula (3) as a third component:




wherein R5 and R6 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons or alkenyl having 2 to 12 carbons;

ring C and ring D are independently





in the rings, at least one hydrogen may be replaced by halogen;

X3 and X4 are independently fluorine or chlorine;

Y2 is hydrogen or methyl;

Z3 and Z4 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and

p and q are independently 0, 1, 2 or 3, and a sum of p and q is 1, 2 or 3.

Item 10. The liquid crystal composition according to item 9, wherein the third component is at least one compound selected from the group of compounds represented by formula (3-1) to formula (3-12):







wherein R5 and R6 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons or alkenyl having 2 to 12 carbons.

Item 11. The liquid crystal composition according to item 9, wherein the third component is at least one compound selected from the group of compounds represented by formula (3-1) according to item 10.
Item 12. The liquid crystal composition according to item 9, wherein the third component is at least one compound selected from the group of compounds represented by formula (3-7) according to item 10.
Item 13. The liquid crystal composition according to any one of items 9 to 12, wherein a ratio of the third component is in the range of 15 wt % to 85 wt % based on the total weight of the liquid crystal composition.
Item 14. The liquid crystal composition according to any one of items 1 to 13, further containing at least one compound selected from the group of compounds represented by formula (4) as a fourth component:




wherein R7 and R8 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine;

ring E, ring F and ring G are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene or 3-fluoro-1,4-phenylene;

Z5 and Z6 are independently a single bond, ethylene, methyleneoxy or carbonyloxy;

r is 0, 1, or 2;

and when r is 0, at least one of ring F and ring G is 1,4-phenylene.

Item 15. The liquid crystal composition according to item 14, wherein the fourth component is at least one compound selected from the group of compounds represented by formula (4-1) to formula (4-12):







wherein R7 and R8 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine.

Item 16. The liquid crystal composition according to item 14, wherein the fourth component is at least one compound selected from the group of compounds represented by formula (4-5) and formula (4-6) according to item 15.
Item 17. The liquid crystal composition according to any one of items 14 to 16, wherein a ratio of the fourth component is in the range of 5 wt % to 50 wt % based on the total weight of the liquid crystal composition.
Item 18. The liquid crystal composition according to any one of items 1 to 17, further containing at least one compound selected from the group of compounds represented by formula (5) as a fifth component:




wherein R9 and R19 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine;

ring I and ring J are independently 1,4-cyclohexylene or 1,4-phenylene; Z7 and Z8 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and

s and t are independently 0, 1, 2 or 3, and a sum of s and t is 1, 2 or 3.

Item 19. The liquid crystal composition according to item 18, wherein the fifth component is at least one compound selected from the group of compounds represented by formula (5-1) to formula (5-5):




wherein R9 and R10 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine.

Item 20. The liquid crystal composition according to item 18, wherein the fifth component is at least one compound selected from the group of compounds represented by formula (5-4) according to item 19.
Item 21. The liquid crystal composition according to any one of items 18 to 20, wherein a ratio of the fifth component is in the range of 5 wt % to 40 wt % based on the total weight of the liquid crystal composition.
Item 22. The liquid crystal composition according to any one of items 1 to 21, wherein a maximum temperature of a nematic phase is 70° C. or higher, an optical anisotropy (25° C.) at a wavelength of 589 nanometers is 0.08 or more, and a dielectric anisotropy (25° C.) at a frequency of 1 kHz is −2 or less.
Item 23. A liquid crystal display device including the liquid crystal composition according to any one of items 1 to 22.
Item 24. The liquid crystal display device according to item 23, wherein an operating mode in the liquid crystal display device is a VA mode, an IPS mode, a PSA mode or a FPA mode, and a driving mode in the liquid crystal display device is an active matrix mode.
Item 25. Use of the liquid crystal composition according to any one of items 1 to 22 in a liquid crystal display device.
Item 26. Use of a compound represented by formula (1) in a liquid crystal composition:




wherein R1 is alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen;

R2 is alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, wherein, in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen, and at least one methylene may be replaced by oxygen;

ring A and ring B are independently





in the rings, at least one hydrogen may be replaced by halogen;

X1 and X2 are independently fluorine or chlorine;

Y1 is hydrogen or methyl;

Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy;

m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3; and

when m is 2 and n is 0, at least one of the two rings A is tetrahydropyran-2,5-diyl or 1,4-phenylene.

The invention further includes the following items: (1) the composition, further containing the optically active compound; (2) the composition, further containing the additive such as an antioxidant, an ultraviolet light absorber or an antifoaming agent; (3) an AM device including the composition; (4) a device including the composition, and having a TN, ECB, OCB, IPS, FFS, VA, PSA or FPA mode; (5) a transmissive device including the composition; (6) use of the composition as the composition having the nematic phase; and (7) use as an optically active composition by adding the optically active compound to the composition.
The composition of the invention will be explained in the following order. First, a constitution of the component compounds in the composition will be explained. Second, main characteristics of the component compounds and main effects of the compounds on the composition will be explained. Third, a combination of components in the composition, a preferred ratio of the component compounds and the basis thereof will be explained. Fourth, a preferred embodiment of the component compounds will be explained. Fifth, specific examples of the component compounds will be shown. Sixth, the additive that may be mixed with the composition will be explained. Seventh, methods for synthesizing the component compounds will be explained. Last, an application of the composition will be explained.
First, the constitution of the component compounds in the composition will be explained. The composition of the invention is classified into composition A and composition B. Composition A may further contain any other liquid crystal compound, the additive, an impurity or the like, in addition to the liquid crystal compound selected from compound (1), compound (2), compound (3), compound (4) and compound (5). “Any other liquid crystal compound” means a liquid crystal compound different from compound (1), compound (2), compound (3), compound (4) and compound (5). Such a compound is mixed with the composition for the purpose of further adjusting the characteristics. Of any other liquid crystal compounds, a ratio of a cyano compound is preferably as small as possible in view of stability to heat or ultraviolet light. A further preferred ratio of the cyano compound is 0 wt %. The additive includes the optically active compound, the antioxidant, the ultraviolet light absorber, a dye, the antifoaming agent, the polymerizable compound and a polymerization initiator. The impurity includes a compound mixed in a process such as preparation of the component compounds. Even in the case where the compound is liquid crystalline, the compound is classified as the impurity herein.
Composition B consists essentially of compounds selected from compound (1), compound (2), compound (3), compound (4) and compound (5). A term “essentially” means that the composition does not contain any liquid crystal compound different from the compounds, excluding the additive and the impurity. Composition B has a smaller number of components than composition A has. Composition B is preferred to composition A in view of cost reduction. Composition A is preferred to composition B in view of possibility of further adjusting physical properties by mixing any other liquid crystal compound.
Second, the main characteristics of the component compounds and the main effects of the compounds on the characteristics of the composition will be explained. The main characteristics of the component compounds are summarized in Table 2 on the basis of advantageous effects of the invention. In Table 2, a symbol L stands for “large” or “high,” a symbol M stands for “medium,” and a symbol S stands for “small” or “low.” The symbols L, M and S represent classification based on a qualitative comparison among the component compounds, and 0 (zero) means “a value is nearly zero.”







TABLE 2







Characteristics of Compounds









Compounds













(1)
(2)
(3)
(4)
(5)
















Maximum temperature
M to L
M
M to L
S to L
M to L


Viscosity
M to L
S
M to L
S to M
M to L


Optical anisotropy
M to L
S
M to L
S to L
M to L


Dielectric anisotropy
L
0
L
0
L


Specific resistance
L
L
L
L
L









Upon mixing the component compounds with the composition, the main effects of the component compounds on the characteristics of the composition are as described below. Compound (1) increases an absolute value of dielectric anisotropy, decreases the threshold voltage and increases the maximum temperature. Compound (2) decreases the minimum temperature and decreases the viscosity. Compound (3) increases the maximum temperature, decreases the minimum temperature and increases the absolute value of dielectric anisotropy. Compound (4) increases the maximum temperature, decreases the minimum temperature and decreases the viscosity. Compound (5) increases the absolute value of dielectric anisotropy and decreases the minimum temperature.
Third, the combination of components in the composition, the preferred ratio of the component compounds and the basis thereof will be explained. The combination of the components in the composition includes a combination of the first component and the second component, a combination of the first component, the second component and the third component, a combination of the first component, the second component and the fourth component, a combination of the first component, the second component and the fifth component, a combination of the first component, the second component, the third component and the fourth component, a combination of the first component, the second component, the third component and the fifth component, a combination of the first component, the second component, the fourth component and the fifth component, and a combination of the first component, the second component, the third component, the fourth component and the fifth component. A preferred combination of the components in the composition includes the combination of the first component, the second component, the third component and the fourth component.
A preferred ratio of the first component is 3 wt % or more for increasing the absolute value of dielectric anisotropy, and 90 wt % or less for decreasing the minimum temperature. A further preferred ratio is in the range of 10 wt % to 70 wt %. A particularly preferred ratio is in the range of 15 wt % to 50 wt %.
A preferred ratio of the second component is 10 wt % or more for decreasing the viscosity, and 97 wt % or less for decreasing the minimum temperature. A further preferred ratio is in the range of 20 wt % to 80 wt %. A particularly preferred ratio is in the range of 30 wt % to 70 wt %.
A preferred ratio of the third component is 15 wt % or more for increasing the absolute value of dielectric anisotropy, and 85 wt % or less for decreasing the viscosity. A further preferred ratio is in the range of 20 wt % to 70 wt %. A particularly preferred ratio is in the range of 30 wt % to 60 wt %.
A preferred ratio of the fourth component is 5 wt % or more for increasing the maximum temperature or decreasing the viscosity, and 50% or less for decreasing the minimum temperature. A further preferred ratio is in the range of 10 wt % to 40 wt %. A particularly preferred ratio is in the range of 15 wt % to 30 wt %.
A preferred ratio of the fifth component is 5 wt % or more for increasing the absolute value of dielectric anisotropy, and 40 wt % or less for decreasing the viscosity. A further preferred ratio is in the range of 8 wt % to 30 wt %. A particularly preferred ratio is in the range of 10 wt % to 20 wt %.
Fourth, the preferred embodiment of the component compounds will be explained.
R1 is alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen, R2, R3 and R4 are independently alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen, and at least one methylene may be replaced by oxygen, R5 and R6 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons or alkenyl having 2 to 12 carbons, R7, R8, R9 and R10 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine.
Preferred R1 is alkyl having 1 to 12 carbons in which one or two hydrogens are replaced by halogen for increasing the absolute value of dielectric anisotropy or decreasing the threshold voltage, further preferred R1 is:




wherein u is an integer from 1 to 12. Preferred R2, R6 or R10 is alkyl having 1 to 12 carbons and alkenyl having 2 to 12 carbons for decreasing the viscosity, and alkoxy having 1 to 12 carbons for increasing the absolute value of dielectric anisotropy. Preferred R3 or R4 is alkyl having 1 to 12 carbons for increasing the stability to ultraviolet light or heat, or the like, and alkenyl having 2 to 12 carbons in which at least one hydrogen may be replaced by halogen for decreasing the viscosity. Particularly preferred R3 or R4 is alkenyl having 2 to 12 carbons in which at least one hydrogen may be replaced by halogen. Preferred R7 or R8 is alkyl having 1 to 12 carbons for increasing the stability to ultraviolet light or heat, or the like, and alkenyl having 2 to 12 carbons for decreasing the viscosity. Preferred R5 or R9 is alkyl having 1 to 12 carbons for increasing the stability to ultraviolet light or heat, or the like, and alkenyl having 2 to 12 carbons for decreasing the viscosity.

Preferred alkyl is methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl or octyl. Further preferred alkyl is ethyl, propyl, butyl, pentyl or heptyl for decreasing the viscosity. In the alkyl, straight-chain alkyl is preferred to branched-chain alkyl.
Preferred alkoxy is methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy or heptyloxy. Further preferred alkoxy is methoxy or ethoxy for decreasing the viscosity. In the alkoxy, straight-chain alkoxy is preferred to branched-chain alkoxy.
Preferred alkenyl is vinyl, 1-propenyl, 2-propenyl, 1-butenyl, 2-butenyl, 3-butenyl, 1-pentenyl, 2-pentenyl, 3-pentenyl, 4-pentenyl, 1-hexenyl, 2-hexenyl, 3-hexenyl, 4-hexenyl or 5-hexenyl. Further preferred alkenyl is vinyl, 1-propenyl, 3-butenyl or 3-pentenyl for decreasing the viscosity. A preferred configuration of —CH—CH— in the alkenyl depends on a position of a double bond. Trans is preferred in the alkenyl such as 1-propenyl, 1-butenyl, 1-pentenyl, 1-hexenyl, 3-pentenyl and 3-hexenyl for decreasing the viscosity, for instance. C is preferred in the alkenyl such as 2-butenyl, 2-pentenyl and 2-hexenyl. In the alkenyl, straight-chain alkenyl is preferred to branched-chain alkenyl.
Preferred examples of alkyl in which at least one hydrogen is replaced by halogen include fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl, 5-fluoropentyl, 6-fluorohexyl, 7-fluoroheptyl or 8-fluorooctyl. Further preferred alkyl is 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl or 5-fluoropentyl for decreasing the threshold voltage.
Preferred examples of alkenyl in which at least one hydrogen is replaced by halogen include 2,2-difluorovinyl, 3,3-difluoro-2-propenyl, 4,4-difluoro-3-butenyl, 5,5-difluoro-4-pentenyl and 6,6-difluoro-5-hexenyl. Further preferred examples include 2,2-difluorovinyl and 4,4-difluoro-3-butenyl for decreasing the viscosity.
Preferred examples of alkyl in which at least one methylene is replaced by oxygen include alkoxy. Preferred examples of alkenyl in which at least one methylene is replaced by oxygen include alkenyloxy.
Preferred alkenyloxy is vinyloxy, allyloxy, 3-butenyloxy, 3-pentenyloxy or 4-pentenyloxy. Further preferred alkenyloxy is allyloxy or 3-butenyloxy for decreasing the viscosity.
Alkyl does not include cyclic alkyl. Alkoxy does not include cyclic alkoxy. The alkenyl does not include cyclic alkenyl. Alkenyloxy does not include cyclic alkenyloxy.
Then, m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3. Preferred m is 2 for increasing the maximum temperature, and 0 for decreasing the viscosity. Preferred n is 0 for decreasing the viscosity.
Then, p and q are independently 0, 1, 2 or 3, and a sum of p and q is 1, 2 or 3. Preferred p is 2 and 3 for increasing the maximum temperature, and 0 for decreasing the viscosity. Preferred q is 0 and 1 for decreasing the viscosity.
Then, r is 0, 1 or 2. Preferred r is 1 and 2 for increasing the maximum temperature, and 0 for decreasing the minimum temperature and decreasing the viscosity.
Then, s and t are independently 0, 1, 2 or 3, and a sum of s and t is 1, 2 or 3. Preferred s is 2 for increasing the maximum temperature, and preferred t is 0 for decreasing the minimum temperature.
Then, u is an integer from 1 to 12. Preferred u is an integer from 1 to 7 for decreasing the viscosity, and an integer from 1 to 5 for decreasing the threshold voltage. Further preferred u is an integer from 1 to 3.
Ring A and ring B are independently




wherein at least one hydrogen may be replaced by halogen, two arbitrary rings A when m is 2 or 3 may be identical or different, and two arbitrary rings B when n is 2 or 3 may be identical or different. Preferred ring A or ring B is 1,4-cyclohexylene for increasing the maximum temperature, 1,4-phenylene for increasing the optical anisotropy, and





preferably





for increasing the absolute value of dielectric anisotropy.

Ring C and ring D are independently




wherein, in the rings, at least one hydrogen may be replaced by halogen, two arbitrary rings C when p is 2 or 3 may be identical or different, and two arbitrary rings D when q is 2 or 3 may be identical or different. Preferred ring C or ring D is 1,4-cyclohexylene for increasing the maximum temperature, 1,4-phenylene for increasing the optical anisotropy, and





preferably





for increasing the absolute value of dielectric anisotropy.

Ring E, ring F and ring G are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene or 3-fluoro-1,4-phenylene, two rings E when r is 2 may be identical or different, and at least one of ring F and ring G when r is 0 is 1,4-phenylene. Preferred ring E, ring F or ring G is 1,4-cyclohexylene for decreasing the viscosity, and 1,4-phenylene for increasing the optical anisotropy.
Ring I and ring J are independently 1,4-cyclohexylene or 1,4-phenylene, two arbitrary rings I when s is 2 or 3 may be identical or different, and two arbitrary rings J when t is 2 or 3 may be identical or different. Preferred ring I or ring J is 1,4-cyclohexylene for increasing the maximum temperature, and is 1,4-phenylene for decreasing the minimum temperature.
With regard to a configuration of 1,4-cyclohexylene, trans is preferred to cis for increasing the maximum temperature.
X1, X2, X3 and X4 are independently fluorine or chlorine. Preferred X1, X2, X3 or X4 is fluorine for decreasing the viscosity.
Y1 and Y2 are hydrogen or methyl. Preferred Y1 or Y2 is hydrogen for decreasing the viscosity, and methyl for increasing the stability to ultraviolet light or heat, or the like.
Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy, two arbitrary Z1 when m is 2 or 3 may be identical or different, and two arbitrary Z2 when n is 2 or 3 may be identical or different. Preferred Z1 or Z2 is a single bond for decreasing the viscosity, ethylene for decreasing the minimum temperature, and methyleneoxy for increasing the absolute value of dielectric anisotropy.
Z3 and Z4 are independently a single bond, ethylene, methyleneoxy or carbonyloxy, two arbitrary Z3 when p is 2 or 3 may be identical or different, and two arbitrary Z4 when q is 2 or 3 may be identical or different. Preferred Z3 or Z4 is a single bond for decreasing the viscosity, ethylene for decreasing the minimum temperature, and methyleneoxy for increasing the absolute value of dielectric anisotropy.
Z5 and Z6 are independently a single bond, ethylene, methyleneoxy or carbonyloxy, and two Z5 when r is 2 may be identical or different. Preferred Z5 is a single bond for decreasing the viscosity, and carbonyloxy for increasing the maximum temperature.
Z7 and Z8 are independently a single bond, ethylene, methyleneoxy or carbonyloxy, two arbitrary Z7 when s is 2 or 3 may be identical or different, and two arbitrary Z8 when t is 2 or 3 may be identical or different. Preferred Z7 or Z8 is a single bond for decreasing the viscosity, and methyleneoxy for increasing the absolute value of dielectric anisotropy.
Fifth, the specific examples of the component compounds will be shown. In preferred compounds as described below, R11 is straight-chain alkyl having 1 to 12 carbons in which at least one hydrogen is replaced by halogen. R12 is straight-chain alkyl having 1 to 12 carbons or straight-chain alkenyl having 2 to 12 carbons. R13 is straight-chain alkyl having 1 to 12 carbons, or straight-chain alkoxy having 1 to 12 carbons. R14 is straight-chain alkyl having 1 to 12 carbons, straight-chain alkoxy having 1 to 12 carbons, or straight-chain alkenyl having 2 to 12 carbons.
Preferred compound (1) includes compound (1-1-1) and compound (1-4-1). Particularly preferred compound (1) includes compound (1-1-1), compound (1-2-1) and compound (1-4-1). Preferred compound (2) includes compound (2-1). Preferred compound (3) includes compound (3-1-1) to compound (3-12-1). Further preferred compound (3) includes compound (3-1-1) to compound (3-10-1). Particularly preferred compound (3) includes compound (3-1-1) to compound (3-9-1). Preferred compound (4) includes compound (4-1-1) to compound (4-12-1). Further preferred compound (4) includes compound (4-1-1) to compound (4-8-1), and compound (4-10-1) to compound (4-12-1). Particularly preferred compound (4) includes compound (4-2-1), compound (4-6-1), compound (4-8-1), compound (4-10-1) and compound (4-12-1). Preferred compound (5) includes compound (5-1-1) to compound (5-5-1). Further preferred compound (5) includes compound (5-4-1).













Sixth, the additive that may be mixed with the composition will be explained. Such an additive includes the optically active compound, the antioxidant, the ultraviolet light absorber, the dye, the antifoaming agent, the polymerizable compound and the polymerization initiator. The optically active compound is mixed with the composition for the purpose of inducing a helical structure in liquid crystals to give a twist angle. Examples of such a compound include compound (6-1) to compound (6-5). A preferred ratio of the optically active compound is 5 wt % or less. A further preferred ratio is in the range of 0.01 wt % to 2 wt %.




The antioxidant is mixed with the composition for the purpose of preventing a decrease in the specific resistance as caused by heating in air, or maintaining a large voltage holding ratio at room temperature and also at a temperature close to the maximum temperature of the nematic phase after the device has been used for a long time.




Preferred examples of the antioxidant include compound (7) where w is an integer from 1 to 9. In compound (7), preferred w is 1, 3, 5, 7 or 9. Further preferred w is 1 or 7. Compound (7) where w is 1 is effective in preventing a decrease in the specific resistance as caused by heating in air because the compound (7) has a large volatility. Compound (7) where w is 7 is effective in maintaining a large voltage holding ratio at room temperature and also at a temperature close to the maximum temperature of the nematic phase even after the device has been used for a long period of time because the compound (7) has a small volatility. A preferred ratio of the antioxidant is about 50 ppm or more for achieving the effect thereof, and about 600 ppm or less for avoiding a decrease in the maximum temperature or avoiding an increase in the minimum temperature. A further preferred ratio is in the range of about 100 ppm to about 300 ppm.
Preferred examples of the ultraviolet light absorber include a benzophenone derivative, a benzoate derivative and a triazole derivative. A light stabilizer such as an amine having steric hindrance is also preferred. A preferred ratio of the ultraviolet light absorber or the stabilizer is about 50 ppm or more for achieving the effect thereof, and about 10,000 ppm or less for avoiding a decrease in the maximum temperature or avoiding an increase in the minimum temperature. A further preferred ratio is in the range of about 100 ppm to about 10,000 ppm.
A dichroic dye such as an azo dye or an anthraquinone dye is mixed with the composition to be adapted for a device having a guest host (GH) mode. A preferred ratio of the dye is in the range of about 0.01 wt % to about 10 wt %. The antifoaming agent such as dimethyl silicone oil or methyl phenyl silicone oil is mixed with the composition for preventing foam formation. A preferred ratio of the antifoaming agent is about 1 ppm or more for achieving the effect thereof, and about 1,000 ppm or less for avoiding a poor display. A further preferred ratio is in the range of about 1 ppm to about 500 ppm.
The polymerizable compound is mixed with the composition to be adapted for the device having the polymer sustained alignment (PSA) mode. Preferred examples of the polymerizable compound include a compound having a polymerizable group, such as an acrylate, a methacrylate, a vinyl compound, a vinyloxy compound, a propenyl ether, an epoxy compound (oxirane, oxetane) and a vinyl ketone. Particularly preferred examples include an acrylate derivative or a methacrylate derivative. A preferred ratio of the polymerizable compound is about 0.05 wt % or more for achieving the effect thereof, and about 10 wt % or less for avoiding a poor display. A further preferred ratio is in the range of about 0.1 wt % to about 2 wt %. The polymerizable compound is preferably polymerized by irradiation with ultraviolet light or the like in the presence of a suitable initiator such as a photopolymerization initiator. Suitable conditions for polymerization, suitable types of the initiator and suitable amounts thereof are known to a person skilled in the art and are described in literatures. For example, Irgacure 651 (registered trademark; BASF), Irgacure 184 (registered trademark; BASF) or Darocure 1173 (registered trademark; BASF), each being a photoinitiator, is suitable for radical polymerization. A preferred ratio of the photopolymerization initiator is in the range of about 0.1 wt % to about 5 wt % of the polymerizable compound, and a particularly preferred ratio is in the range of about 1 wt % to about 3 wt %.
Seventh, the methods for synthesizing the component compounds will be explained. The compounds can be prepared according to known methods. Examples of synthetic methods will be shown. Compound (1-3-1) is prepared by the method described in WO 1999/021815 A. Compound (2-1-1) is prepared by the method described in JP S59-070624 A (1984). Compound (3-2-1) and compound (3-4-1) are prepared by the method described in JP H2-503441 A (1990). Compound (4-5-1) is prepared by the method described in JP 2006-503130 A. Compound (5-4-1) is prepared by the method described in JP 2005-035986 A. The antioxidant is commercially available. A compound represented by formula (7) where w is 1 is available from Sigma-Aldrich Corporation. Compound (7) where w is 7 and so forth are prepared according to the method described in U.S. Pat. No. 3,660,505 B.
Any compounds whose synthetic methods are not described above can be prepared according to the methods described in books such as Organic Syntheses (John Wiley & Sons, Inc.), Organic Reactions (John Wiley & Sons, Inc.), Comprehensive Organic Synthesis (Pergamon Press) and New Experimental Chemistry Course (Shin Jikken Kagaku Koza in Japanese) (Maruzen Co., Ltd.). The composition is prepared according to publicly known methods using the thus obtained compounds. For example, the component compounds are mixed and dissolved in each other by heating.
Last, the application of the composition will be explained. The composition of the invention mainly has a minimum temperature of about −10° C. or lower, a maximum temperature of about 70° C. or higher, and an optical anisotropy in the range of about 0.07 to about 0.20. The device including the composition has a large voltage holding ratio. The composition is suitable for use in the AM device. The composition is particularly suitable for use in a transmissive AM device. The composition having an optical anisotropy in the range of about 0.08 to about 0.25, and also the composition having an optical anisotropy in the range of about 0.10 to about 0.30 may be prepared by controlling the ratio of the component compounds or by mixing with any other liquid crystal compound. The composition can be used as the composition having the nematic phase and as the optically active composition by adding the optically active compound.
A preferred minimum temperature of the nematic phase of the liquid crystal composition of the invention is at least about 0° C. or lower, a further preferred minimum temperature of the nematic phase is about −20° C. or lower, and a particularly preferred minimum temperature of the nematic phase is about −30° C. or lower.
A preferred maximum temperature of the nematic phase of the liquid crystal composition of the invention is at least about 70° C. or higher, a more preferred maximum temperature of the nematic phase is about 75° C. or higher, and a particularly preferred maximum temperature of the nematic phase is about 80° C. or higher.
A preferred optical anisotropy of the liquid crystal composition of the invention, at 25° C. and at 589 nanometers, is in the range of about 0.07 to about 0.20, a further preferred optical anisotropy is in range of about 0.07 to about 0.16, and a particularly preferred optical anisotropy is in the range of about 0.08 to about 0.12.
A preferred absolute value of dielectric anisotropy of the liquid crystal composition of the invention, at 25° C., is at least about 1.5 or more, a further preferred absolute value of dielectric anisotropy is about 2 or more, and a particularly preferred absolute value of dielectric anisotropy is about 2.5 or more.
The composition can be used for the AM device. The composition can also be used for a PM device. The composition can be used for an AM device and a PM device both having a mode such as PC, TN, STN, ECB, OCB, IPS, FFS, VA, PSA or FPA. Use for the AM device having the IPS, FFS or VA mode is particularly preferred. The devices may be of a reflective type, a transmissive type or a transflective type. Use for the transmissive device is preferred. The composition can also be used for an amorphous silicon-TFT device or a polycrystal silicon-TFT device. The composition can also be used for a nematic curvilinear aligned phase (NCAP) device prepared by microencapsulating the composition, and for a polymer dispersed (PD) device in which a three-dimensional network-polymer is formed in the composition.
EXAMPLES
When a sample was a composition, the sample was measured as was, and values obtained were described. When the sample was a compound, a sample for measurement was prepared by mixing the compound (15 wt %) with mother liquid crystals (85 wt %). Values of characteristics of the compound were calculated using values obtained by measurement, according to an extrapolation method: (extrapolated value)={(measured value of a sample)−0.85×(measured value of mother liquid crystals)}/0.15. When a smectic phase (or crystals) precipitated at the ratio thereof at 25° C., a ratio of the compound to the mother liquid crystals was changed step by step in the order of (10 wt %:90 wt %), (5 wt %:95 wt %) and (1 wt %:99 wt %). Values of a maximum temperature, an optical anisotropy, viscosity and a dielectric anisotropy with regard to the compound were obtained according to the extrapolation method.
Components of the mother liquid crystals were as described below. A ratio of each component is expressed in terms of wt %.




Characteristics were measured according to the methods described below. Most of the methods were applied as described in a Standard of the Japan Electronics and Information Technology Industries Association (hereafter abbreviated as JEITA) (JEITA ED-2521B) as discussed and established in JEITA, or as modified thereon.
Phase Structure:
A sample was placed on a hot plate of a melting point apparatus (FP52 Hot Stage made by Mettler Toledo International Inc.) equipped with a polarizing microscope, and a state of phase and a change thereof were observed with the polarizing microscope while the compound was heated at a rate of 3° C. per minute, and a kind of the phase was specified.
Transition Temperature (° C.):
A sample was heated and then cooled at a rate of 3° C. per minute using a differential scanning calorimeter, DSC-7 System or Diamond DSC System, made by PerkinElmer, Inc. A starting point of an endothermic peak or an exothermic peak caused by a change of phase of the sample was obtained by extrapolation, and thus a transition temperature was determined. Temperature at which a compound changes from a solid to a liquid crystal phase such as a smectic phase or a nematic phase may be occasionally abbreviated as “minimum temperature of the liquid crystal phase.” Temperature at which a compound changes from a liquid crystal phase to a liquid may be occasionally abbreviated as “clearing point.”
The crystals were expressed as C. When kinds of crystals were distinguishable, the kinds were expressed as C1 or C2, respectively. The smectic phase and the nematic phase were expressed as S and N, respectively. When smectic A phase, smectic B phase, smectic C phase or smectic F phase was distinguishable among the smectic phases, the phases were expressed as SA, SB, SC or SF, respectively. The liquid (isotropic) was expressed as I. Transition temperature was expressed as “C 50.0 N 100.0 I”, for example. The expression shows that a transition temperature from the crystals to the nematic phase is 50.0° C., and a transition temperature from the nematic phase to the liquid is 100.0° C.
Maximum Temperature of a Nematic Phase (NI; ° C.):
A sample was placed on a hot plate in a melting point apparatus equipped with a polarizing microscope and was heated at a rate of 1° C. per minute. Temperature when part of the sample began to change from the nematic phase to the isotropic liquid was measured. A maximum temperature of the nematic phase may be occasionally abbreviated as “maximum temperature.”
Minimum Temperature of a Nematic Phase (Tc; ° C.):
Samples each having a nematic phase were put in glass vials and kept in freezers at 0° C., −10° C., −20° C., −30° C. and −40° C. for 10 days, and then liquid crystal phases were observed. For example, when the sample maintained the nematic phase at −20° C. and changed to the crystals or the smectic phase at −30° C., Tc was expressed as “Tc<−20° C.” A minimum temperature of the nematic phase may be occasionally abbreviated as “minimum temperature.”
Viscosity (bulk viscosity; η; measured at 20° C.; mPa·s):
A cone-plate (E type) rotationally viscometer was used for measurement.
Optical Anisotropy (Refractive Index Anisotropy; Δn; Measured at 25° C.):
Measurement was carried out by means of an Abbe refractometer with a polarizing plate mounted on an ocular, using light at a wavelength of 589 nanometers. A surface of a main prism was rubbed in one direction, and then a sample was added dropwise onto the main prism. A refractive index (n∥) was measured when the direction of polarized light was parallel to the direction of rubbing. A refractive index (n⊥) was measured when the direction of polarized light was perpendicular to the direction of rubbing. A value of optical anisotropy was calculated from an equation: Δn=n∥−n⊥.
Dielectric Anisotropy (Δ∈; measured at 25° C.):
A value of dielectric anisotropy was calculated from an equation: Δ∈=∈∥−∈⊥. Dielectric constants (∈∥ and ∈⊥) were measured as described below.
(1) Measurement of dielectric constant (∈∥: An ethanol (20 mL) solution of octadecyl triethoxysilane (0.16 mL) was applied onto a well-washed glass substrate. After rotating the glass substrate with a spinner, the glass substrate was heated at 150° C. for 1 hour. A sample was put in a VA device in which a distance (cell gap) between two glass substrates was 4 micrometers, and the device was sealed with an ultraviolet-curable adhesive. Sine waves (0.5 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (∈∥) in the major axis direction of liquid crystal molecules was measured.
(2) Measurement of dielectric constant (∈1): A polyimide solution was applied onto a well-washed glass substrate. After calcining the glass substrate, rubbing treatment was applied to the alignment film obtained. A sample was put in a TN device in which a distance (cell gap) between two glass substrates was 9 micrometers and a twist angle was 80 degrees. Sine waves (0.5 V, 1 kHz) were applied to the device, and after 2 seconds, a dielectric constant (∈⊥) in the minor axis direction of the liquid crystal molecules was measured.
Threshold Voltage (Vth; Measured at 25° C.; V):
An LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used for measurement. A light source was a halogen lamp. A sample was put in a normally black mode VA device in which a distance (cell gap) between two glass substrates was 4 micrometers and a rubbing direction was anti-parallel, and the device was sealed with an ultraviolet-curable adhesive. A voltage (60 Hz, rectangular waves) to be applied to the device was stepwise increased from 0 V to 20 Vat an increment of 0.02 V. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and the amount of light transmitted through the device was measured. A voltage-transmittance curve was prepared, in which the maximum amount of light corresponds to 100% transmittance and the minimum amount of light corresponds to 0% transmittance. A threshold voltage is a voltage at 10% transmittance.
Voltage Holding Ratio (VHR-1; Measured at 25° C.; %):
A TN device used for measurement had a polyimide alignment film, and a distance (cell gap) between two glass substrates was 5 micrometers. A sample was put in the device, and then the device was sealed with an ultraviolet-curable adhesive. A pulse voltage (60 microseconds at 5 V) was applied to the TN device and the device was charged. A decaying voltage was measured for 16.7 milliseconds with a high-speed voltmeter, and area A between a voltage curve and a horizontal axis in a unit cycle was determined. Area B is an area without decay. A voltage holding ratio is a percentage of area A to area B.
Voltage Holding Ratio (VHR-2; Measured at 80° C.; %):
A TN device used for measurement had a polyimide alignment film, and a distance (cell gap) between two glass substrates was 5 micrometers. A sample was put in the device, and then the device was sealed with an ultraviolet-curable adhesive. A pulse voltage (60 microseconds at 5 V) was applied to the TN device and the device was charged. A decaying voltage was measured for 16.7 milliseconds with a high-speed voltmeter, and area A between a voltage curve and a horizontal axis in a unit cycle was determined. Area B is an area without decay. A voltage holding ratio is a percentage of area A to area B.
Voltage Holding Ratio (VHR-3; Measured at 25° C.; %):
Stability to ultraviolet light was evaluated by measuring a voltage holding ratio after a device was irradiated with ultraviolet light. A TN device used for measurement had a polyimide alignment film, and a cell gap was 5 micrometers. A sample was injected into the device, and then the device was irradiated with light for 20 minutes. Alight source was an ultra high-pressure mercury lamp USH-500D (made by Ushio, Inc.), and a distance between the device and the light source was 20 centimeters. In measurement of VHR-3, a decaying voltage was measured for 16.7 milliseconds. A composition having a large VHR-3 has a large stability to ultraviolet light. A value of VHR-3 is preferably 90% or more, further preferably, 95% or more.
Voltage Holding Ratio (VHR-4; Measured at 25° C.; %):
A TN device into which a sample was injected was heated in a constant-temperature bath at 80° C. for 500 hours, and then stability to heat was evaluated by measuring a voltage holding ratio. In measurement of VHR-4, a decaying voltage was measured 1 for 6.7 milliseconds. A composition having a large VHR-4 has a large stability to heat.
Response Time (τ; Measured at 25° C.; ms):
An LCD-5100 luminance meter made by Otsuka Electronics Co., Ltd. was used for measurement. A light source was a halogen lamp. A low-pass filter was set at 5 kHz. A sample was put in a normally black mode VA device in which a distance (cell gap) between two glass substrates was 4 micrometers and a rubbing direction was anti-parallel, and the device was sealed with an ultraviolet-curable adhesive. Rectangular waves (60 Hz, 10 V, 0.5 second) were applied to the device. On the occasion, the device was irradiated with light from a direction perpendicular to the device, and the amount of light transmitted through the device was measured. The maximum amount of light corresponds to 100% transmittance, and the minimum amount of light corresponds to 0% transmittance. A response time is a period of time required for a change from 90% transmittance to 10% transmittance (fall time; millisecond).
Specific Resistance (ρ; Measured at 25° C.; Ωcm):
Into a vessel equipped with electrodes, 1.0 milliliter of a sample was injected.
A DC voltage (10 V) was applied to the vessel, and a DC current after 10 seconds was measured. A specific resistance was calculated from the following equation: (specific resistance)={(voltage)×(electric capacity of a vessel)}/{(direct current)×(dielectric constant of vacuum)}.
1H-NMR Analysis:
As a measuring apparatus, DRX-500 (made by Bruker BioSpin Corporation) was used. A sample prepared in Example and so forth was dissolved in a deuterated solvent such as CDCl3 in which the sample was soluble, and measurement was carried out under the conditions of room temperature, 500 MHz and 24 times of accumulation. In addition, in explaining nuclear magnetic resonance spectra obtained, s, d, t, q and m stand for a singlet, a doublet, a triplet, a quartet and a multiplet, respectively. Tetramethylsilane (TMS) was used as a reference material for a zero point of chemical shifts (δ values). 19F-NMR analysis was also conducted by means of the same apparatus.
Gas Chromatographic Analysis:
GC-14B Gas Chromatograph made by Shimadzu Corporation was used for measurement. A carrier gas was helium (2 mL per minute). A sample injector and a detector (FID) were set to 280° C. and 300° C., respectively. A capillary column DB-1 (length 30 m, bore 0.32 mm, film thickness 0.25 μm; dimethylpolysiloxane as a stationary liquid phase, non-polar) made by Agilent Technologies, Inc. was used for separation of component compounds. After the column was kept at 200° C. for 2 minutes, the column was heated to 280° C. at a rate of 5° C. per minute. A sample was prepared in an acetone solution (0.1 wt %), and then 1 microliter of the solution was injected into the sample injector. A recorder was C-R5A Chromatopac made by Shimadzu Corporation or the equivalent thereof. The resulting chromatogram showed a retention time of a peak and a peak area corresponding to each of the component compounds.
As a solvent for diluting the sample, chloroform, hexane and so forth may also be used. The following capillary columns may also be used for separating the component compounds: HP-1 (length 30 m, bore 0.32 mm, film thickness 0.25 μm) made by Agilent Technologies, Inc., Rtx-1 (length 30 m, bore 0.32 mm, film thickness 0.25 μm) made by Restek Corporation and BP-1 (length 30 m, bore 0.32 mm, film thickness 0.25 μm) made by SGE International Pty. Ltd. A capillary column CBP1-M50-025 (length 50 m, bore 0.25 mm, film thickness 0.25 μm) made by Shimadzu Corporation may also be used for the purpose of avoiding an overlap of peaks of the compounds.
A ratio of liquid crystal compounds contained in the composition may be calculated by the method as described below. The liquid crystal compounds can be detected by means of a gas chromatograph. A ratio of the peak areas in the gas chromatogram corresponds to a ratio (in the number of moles) of the liquid crystal compounds. When the capillary columns described above were used, a correction coefficient of each of the liquid crystal compounds may be regarded as 1 (one). Accordingly, a ratio (wt %) of the liquid crystal compounds was calculated from the ratio of the peak areas.
The invention will be explained in detail byway of Examples. The invention is not limited by the Examples described below. The compounds in Comparative Examples and Examples were described using symbols according to definitions in Table 3 below. In Table 3, a configuration of 1,4-cyclohexylene is trans. A parenthesized number next to a symbolized compound corresponds to the number of the compound. A symbol (−) means any other liquid crystal compound. A ratio (percentage) of the liquid crystal compounds is expressed in terms of weight percent (wt %) based on the total weight of the liquid crystal composition. The liquid crystal composition contains an impurity. Last, values of characteristics of the composition were summarized.







TABLE 3







Method for Description of Compounds using Symbols


R—(A1)—Z1— . . . —Zn—(An)—R′











1) Left-terminal Group R—
Symbol





CnH2n+1—
n-


CnH2n+1O—
nO—


CmH2m+1OCnH2n—
mOn—


CH2═CH—
V—


CnH2n+1—CH═CH—
nV—


CH2═CH—CnH2n—
Vn—


CmH2m+1—CH═CH—CnH2n—
mVn—


CF2═CH—
VFF—


CF2═CH—CnH2n—
VFFn—


F—CnH2n—
Fn


CnH2n+1—CF2—
nCF2-


 






<3>n-


 






<3>nO—


 


CmH2m+1CF2CnH2n—
m(CF2)n—





2) Right-terminal Group —R′
Symbol





—CnH2n+1
-n


—OCnH2n+1
—On


—CH═CH2
—V


—CH═CH—CnH2n+1
—Vn


—CnH2n—CH═CH2
—nV


—CmH2m—CH═CH2—CnH2n+1
—mVn


—OCnH2n—CH═CH2
—OnV


—CH═CF2
—VFF


 






—On<3>


 


—OCnH2n—F
—OnF





3) Bonding Group —Zn—
Symbol





—CnH2n—
n


—COO—
E


—CH═CH—
V


—CH2O—
1O





4) Ring Structure —An—
Symbol









H


 






G


 






B


 






B(2F)


 






B(F)


 






B(F,F)


 






B(2F,3F)


 






B(2F,3CL)


 






B(2CL,3F)


 






B(3F,6F)


 






B(2F,3F,6Me)


 






dh


 






Dh


 






Cro(7F,8F)










5) Example of Description





Example 1 F2-HB(2F,3F)—O2


 








 


Example 2 2(CF2)1-HHB(2F,3F)—O2


 








 


Example 3 5-HBB(F)B-3


 








 


Example 4 3-HHB(2F,3F)—O2<3>


 















Example 1
Among types of compound (1-1-1), a compound as described below was manufactured.




A phase transition temperature was C 47.5 I. Moreover, the compound was mixed with mother liquid crystals, and values of characteristics of the compound were obtained according to an extrapolation method as follows: NI=−30.7° C.; Δn=0.053.
1HNMR (CDCl3) (σ): 6.83 (ddd, J=8.5, 8.2, 2.4 Hz, 1H), 6.67 (ddd, J=8.5, 8.2, 1.9 Hz, 1H), 4.53 (dt, J=47.4, 6.1, 2H), 4.09 (q, J=7.0 Hz, 2H), 2.76 (tt, J=12.2, 3.3 Hz, 1H), 1.92-1.85 (m, 4H), 1.65 (ddt, J=26.5, 6.4, 6.1 Hz, 2H), 1.57-1.42 (m, 3H), 1.43 (t, J=7.0 Hz, 3H), 1.15 (dddd, J=13.0, 12.9, 12.2, 3.3 Hz, 2H).
19FNMR (CDCl3) (σ): −143.82 (dd, J=19.7, 8.2 Hz, 1F), −160.15 (ddd, J=−19.7, 8.2, 2.4 Hz, 1F), −218.63 (tt, J=47.4, 26.5 Hz, 1F).
Example 2
Among types of compound (1-1-1), a compound as described below was manufactured.




A phase transition temperature was C 58.8 I. Moreover, the compound was mixed with mother liquid crystals, and values of characteristics of the compound were obtained according to an extrapolation method as follows: NI=4.6° C.; Δ∈=−6.8; Δn=0.074.
1HNMR (CDCl3) (σ): 6.83 (ddd, J=8.4, 8.2, 2.6 Hz, 1H), 6.66 (ddd, J=8.3, 8.2, 1.9 Hz, 1H), 4.45 (dt, J=47.4, 6.3 Hz, 2H), 4.09 (q, J=7.0 Hz, 2H), 2.75 (tt, J=12.2, 3.0 Hz, 1H), 1.88-1.86 (m, 4H), 1.79-1.68 (m, 2H), 1.49-1.40 (m, 2H), 1.43 (t, J=7.0 Hz, 3H), 1.10 (dddd, J=12.7, 12.4, 12.2, 2.9 Hz, 2H).
19FNMR (CDCl3) (σ): −143.77 (dd, J=19.7, 8.4 Hz, 1F), −160.15 (ddd, J=19.7, 8.3, 2.6 Hz, 1F), −218.23 (tt, J=47.4, 12.2 Hz, 1F).
Example 3
Among types of compound (1-3-1), a compound as described below was manufactured.




A phase transition temperature was C 89.8 N 183.8 I. Moreover, the compound was mixed with mother liquid crystals, and values of characteristics of the compound were obtained according to an extrapolation method as follows: NI=150.6° C.; Δ∈=−6.2; Δn=0.114; η=51.4 mPa·s.
1HNMR (CDCl3) (σ): 6.83 (ddd, J=8.2, 7.7, 2.2 Hz, 1H), 6.66 (ddd, J=8.2, 8.1, 1.9 Hz, 1H), 4.43 (dt, J=47.5, 6.3 Hz, 2H), 2.72 (tt, J=12.2, 3.1 Hz, 1H), 1.88-1.65 (m, 10H), 1.44-1.37 (m, 2H), 1.43 (t, J=7.0, 3H), 1.30-1.25 (m, 2H), 1.20-0.86 (m, 9H).
19FNMR (CDCl3) (σ): −143.83 (dd, J=19.7, 7.7 Hz, 1F), −160.21 (ddd, J=19.7, 8.1, 2.2 Hz, 1F), −218.06 (tt, J=47.5, 24.4 Hz, 1F).
Example 4
Among types of compound (1-4-1), a compound described below was manufactured.




A phase transition temperature was C 91.4 N 172.5 I. Moreover, the compound was mixed with mother liquid crystals, and values of characteristics of the compound were obtained according to an extrapolation method as follows: NI=150.6° C.; Δ∈=−6.5; Δn=0.180; η=56.8 mPa·s.
1HNMR (CDCl3) (σ): 7.43 (dd, J=8.2, 1.3 Hz, 2H), 7.27 (d, J=8.2 Hz, 2H), 7.08 (ddd, J=8.5, 8.2, 2.3 Hz, 1H), 6.78 (ddd, J=8.2, 8.1, 1.8 Hz, 1H), 4.45 (dt, J=47.4, 6.2 Hz, 1H), 4.14 (q, J=7.1 Hz, 2H), 2.51 (tt, J=12.2, 2.8 Hz, 1H), 1.95-1.89 (m, 4H), 1.80-1.70 (m, 2H), 1.55-1.46 (m, 2H), 1.47 (t, J=7.1 Hz, 3H), 1.36-1.34 (m, 3H), 1.13-1.07 (m, 2H).
19FNMR (CDCl3) (σ): −142.35 (dd, J=19.5, 8.5 Hz, 1F), −159.41 (dd, J=19.5, 8.1 Hz, 1F), −218.17 (tt, J=47.4, 24.3 Hz, 1F).
Comparative Example 1
Use Example 2 was selected from the compositions disclosed in WO 1999/021815 A. The reason is that the composition contains compound (1) and compound (4), and has a negative dielectric anisotropy.

















F2-HHB(2F,3F)-O2
(1-3-1)
3%



4-HEB-O2
(4)
20%



5-HEB-O1
(4)
20%



3-HEB-O2
(4)
18%



5-HEB-O2
(4)
14%



5-HHB(2F,3F)-O3F
(—)
3%



3-HB(2F)B(2F,3F)-O4F
(—)
3%



3-HB(2F,3F)-O3F
(—)
5%



F3-GHB(2F,3F)-O2<3>
(—)
2%



3-HHB(2F,3F)-O2<3>
(—)
3%



<3>2-HHB(2F,3F)-O2
(—)
3%



3-HB(2F)B(2F,3F)-O2<3>
(—)
3%



<3>2O-HHB(2F,3F)-O2
(—)
3%







NI = 82.1° C.;



Δn = 0.117;



η = 23.9 mPa · s;



Δε = −2.1.






Example 5
Part of compound (4) in Comparative Example 1 was replaced by compound (2-1) to obtain a composition in the scope of claims of the present application. The composition was prepared and measured by the method described above. Components and characteristics of the composition are as described below. The composition in Example 5 has a higher maximum temperature and a lower viscosity, as compared with the composition in Comparative Example 1.

















F2-HHB(2F,3F)-O2
(1-3-1)
3%



3-HH-V1
(2-1)
14%



4-HEB-O2
(4)
20%



5-HEB-O1
(4)
20%



3-HEB-O2
(4)
18%



5-HHB(2F,3F)-O3F
(—)
3%



3-HB(2F)B(2F,3F)-O4F
(—)
3%



3-HB(2F,3F)-O3F
(—)
5%



F3-GHB(2F,3F)-O2<3>
(—)
2%



3-HHB(2F,3F)-O2<3>
(—)
3%



<3>2-HHB(2F,3F)-O2
(—)
3%



3-HB(2F)B(2F,3F)-O2<3>
(—)
3%



<3>2O-HHB(2F,3F)-O2
(—)
3%







NI = 84.7° C.;



Δn = 0.114;



η = 20.2 mPa · s;



Δε = −2.0.






Example 6

















F3-HB(2F,3F)-O2
(1-1-1)
10%



2-HH-3
(2-1)
10%



3-HH-4
(2-1)
8%



3-HH-5
(2-1)
4%



F3-HH-V
(2)
7%



F3-HH-2V1
(2)
3%



5-H2B(2F,3F)-O2
(3-3-1)
10%



4-HHB(2F,3F)-O2
(3-4-1)
10%



5-HHB(2F,3F)-O2
(3-4-1)
8%



2-HHB(2F,3F)-1
(3-4-1)
7%



3-HHB(2F,3F)-1
(3-4-1)
6%



V-HHB(2F,3F)-O2
(3-4-1)
3%



2-HH1OB(2F,3F)-O2
(3-7-1)
6%



5-HH1OB(2F,3F)-O2
(3-7-1)
8%







NI = 84.7° C.;



Tc < −20° C.;



Δn = 0.075;



η = 21.8 mPa · s;



Δε = −3.8;



VHR-1 = 99.5%;



VHR-2 = 98.1%;



VHR-3 = 97.3%.






Example 7

















F2-HB(2F,3F)-O2
(1-1-1)
5%



F3-HB(2F,3F)-O2
(1-1-1)
5%



F3-HBB(2F,3F)-O2
(1-4-1)
5%



2-HH-5
(2-1)
8%



3-HH-4
(2-1)
12%



3-HH-5
(2-1)
6%



3-HH-O1
(2-1)
5%



3-HH-VFF
(2)
5%



5-BB(2F,3F)-O2
(3-1-1)
5%



3-HB(2F,3F)-O2
(3-2-1)
5%



3-HHB(2F,3F)-O2
(3-4-1)
10%



5-HHB(2F,3F)-O2
(3-4-1)
10%



V2-HHB(2F,3F)-O2
(3-4-1)
5%



5-HH2B(2F,3F)-O2
(3-5-1)
3%



5-HH1OB(2F,3F)-O2
(3-7-1)
3%



3-HDhB(2F,3F)-O2
(3-9-1)
8%







NI = 83.1° C.;



Tc < −20° C.;



Δn = 0.082;



η = 22.7 mPa · s;



Δε = −3.7;



VHR-1 = 99.4%;



VHR-2 = 97.9%;



VHR-3 = 97.1%.






Example 8

















F3-HHB(2F,3F)-O2
(1-3-1)
8%



3-HH-4
(2-1)
11%



3-HH-5
(2-1)
7%



5-HH-V
(2-1)
13%



5-BB(2F,3F)-O2
(3-1-1)
5%



2O-BB(2F,3F)-O2
(3-1)
5%



3-H2B(2F,3F)-O2
(3-3-1)
7%



5-H2B(2F,3F)-O2
(3-3-1)
8%



5-HHB(2F,3F)-O2
(3-4-1)
7%



2-HHB(2F,3F)-1
(3-4-1)
8%



3-HBB(2F,3F)-O2
(3-6-1)
10%



4-HBB(2F,3F)-O2
(3-6-1)
3%



3-DhHB(2F,3F)-O2
(3-8-1)
3%



3-HDhB(2F,3F)-O2
(3-9-1)
5%







NI = 84.5° C.;



Tc < −20° C.;



Δn = 0.094;



η = 22.1 mPa · s;



Δε = −4.0;



VHR-1 = 99.3%;



VHR-2 = 97.7%;



VHR-3 = 96.8%.






Example 9

















F2-HHB(2F,3F)-O2
(1-3-1)
7%



F3-HHB(2F,3F)-O2
(1-3-1)
7%



2-HH-3
(2-1)
5%



3-HH-4
(2-1)
7%



3-HH-5
(2-1)
3%



3-HH-V1
(2-1)
7%



1-HH-2V1
(2-1)
4%



3-HH-O1V
(2)
7%



3-H2B(2F,3F)-O2
(3-3-1)
5%



5-H2B(2F,3F)-O2
(3-3-1)
5%



5-HHB(2F,3F)-O2
(3-4-1)
7%



2-HHB(2F,3F)-1
(3-4-1)
8%



3-DhHB(2F,3F)-O2
(3-8-1)
3%



3-HDhB(2F,3F)-O2
(3-9-1)
5%



3-dhBB(2F,3F)-O2
(3-10-1)
5%



2-BB(2F,3F)B-3
(3-12-1)
5%



2-BB(2F,3F)B-4
(3-12-1)
5%



8-H1OB(2F,3F)-O2
(3)
5%







NI = 84.1° C.;



Tc < −20° C.;



Δn = 0.095;



η = 21.2 mPa · s;



Δε = −3.9;



VHR-1 = 99.4%;



VHR-2 = 98.1%;



VHR-3 = 97.4%.






Example 10

















F2-HB(2F,3F)-O2
(1-1-1)
5%



F3-HB(2F,3F)-O2
(1-1-1)
10%



F3-HHB(2F,3F)-O2
(1-3-1)
5%



2(CF2)1-HHB(2F,3F)-O2
(1-3-1)
5%



F3-HBB(2F,3F)-O2
(1-4-1)
8%



3-HH-V
(2-1)
10%



3-HH-V1
(2-1)
5%



3-HH-2V1
(2-1)
3%



5-HH2B(2F,3F)-O2
(3-5-1)
7%



5-HH1OB(2F,3F)-O2
(3-7-1)
5%



5-HDhB(2F,3F)-O2
(3-9-1)
3%



3-HHB(2F,3CL)-O2
(3-11-1)
3%



3-HB-O1
(4-1-1)
5%



1-BB-3
(4-2-1)
8%



V-HHB-1
(4-3-1)
7%



V2-HHB-1
(4-3-1)
5%



2-BB(F)B-3
(4-5-1)
3%



3-B(F)BB-2
(4-6-1)
3%







NI = 85.6° C.;



Tc < −20° C.;



Δn = 0.105;



η = 20.9 mPa · s;



Δε = −3.1;



VHR-1 = 99.4%;



VHR-2 = 98.0%;



VHR-3 = 97.5%.






Example 11

















F2-HB(2F,3F)-O2
(1-1-1)
6%



F3-HHB(2F,3F)-O2
(1-3-1)
5%



3-HH-V
(2-1)
12%



4-HH-V
(2-1)
5%



3-HH-V1
(2-1)
3%



F2-HH-V3
(2)
5%



2-BB(2F,3F)-O2
(3-1-1)
3%



2O-BB(2F,3F)-O2
(3-1)
3%



V-HB(2F,3F)-O2
(3-2-1)
3%



1V2-HB(2F,3F)-O2
(3-2-1)
3%



5-HHB(2F,3F)-O2
(3-4-1)
8%



1V2-HHB(2F,3F)-O2
(3-4-1)
3%



3-HH1OB(2F,3F)-O2
(3-7-1)
3%



3-dhBB(2F,3F)-O2
(3-10-1)
5%



1O-BB(2F,3F)B-3
(3-12)
3%



5-H1OB(2F,3F)-O2
(3)
5%



V-H1OB(2F,3F)-O2
(3)
3%



5-HB-3
(4-1-1)
5%



V-HHB-1
(4-3-1)
5%



1V-HBB-2
(4-4-1)
3%



3-HBBH-3
(4-9-1)
3%



5-HB(F)HH-V
(4-10-1)
3%



5-HB(F)BH-5
(4-11-1)
3%







NI = 85.3° C.;



Tc < −20° C.;



Δn = 0.100;



η = 20.2 mPa · s;



Δε = −3.2;



VHR-1 = 99.1%;



VHR-2 = 97.3%;



VHR-3 = 96.9%.






Example 12

















F3-HB(2F,3F)-O2
(1-1-1)
10%



F3-HHB(2F,3F)-O2
(1-3-1)
5%



3-HH-V
(2-1)
37%



3-HH2B(2F,3F)-O2
(3-5-1)
10%



3-HH1OB(2F,3F)-O2
(3-7-1)
3%



5-HH1OB(2F,3F)-O2
(3-7-1)
5%



2-H1OB(2F,3F)-O2
(3)
5%



3-HHB(2CL,3F)-O2
(3)
3%



3-HHEH-5
(4-7-1)
5%



3-HHEBH-3
(4-8-1)
3%



5-HBB(F)B-2
(4-12-1)
5%



5-H2Cro(7F,8F)-5
(5-1-1)
3%



3-H1OCro(7F,8F)-5
(5-2-1)
3%



3-HH2Cro(7F,8F)-5
(5-3-1)
3%







NI = 85.4° C.;



Tc < −20° C.;



Δn = 0.076;



η = 20.7 mPa · s;



Δε = −3.3;



VHR-1 = 99.2%;



VHR-2 = 97.5%;



VHR-3 = 96.7%.






Example 13

















F2-HB(2F,3F)-O2
(1-1-1)
6%



F3-HBB(2F,3F)-O2
(1-4-1)
5%



5-HH-V
(2-1)
10%



3-HH-V1
(2-1)
5%



2O-BB(2F,3F)-O2
(3-1)
3%



V-HB(2F,3F)-O2
(3-2-1)
5%



3V-HB(2F,3F)-O2
(3-2-1)
3%



5-HH2B(2F,3F)-O2
(3-5-1)
7%



5-HH1OB(2F,3F)-O2
(3-7-1)
3%



3-H1OB(2F,3F)-O2
(3)
10%



3-HH1OB(2F,3F,6Me)-O2
(3)
3%



1-BB-1
(4-2-1)
3%



1-BB-3
(4-2-1)
7%



2-BB-3
(4-2-1)
5%



V-HHB-1
(4-3-1)
5%



3-HHEBH-3
(4-8-1)
6%



3-HHEBH-4
(4-8-1)
2%



3-HHEBH-5
(4-8-1)
3%



3-HH1OCro(7F,8F)-5
(5-4-1)
3%



5-HB1OCro(7F,8F)-5
(5-5-1)
3%



1O1-HBBH-5
(—)
3%







NI = 85.5° C.;



Tc < −20° C.;



Δn = 0.099;



η = 20.5 mPa · s;



Δε = −3.3;



VHR-1 = 99.1%;



VHR-2 = 97.1%;



VHR-3 = 96.9%.






Example 14

















F3-HHB(2F,3F)-O2
(1-3-1)
7%



F3-HBB(2F,3F)-O2
(1-4-1)
8%



3-HH-V
(2-1)
11%



3-HH-V1
(2-1)
7%



V2-BB(2F,3F)-O2
(3-1-1)
3%



3-HH1OB(2F,3F)-O2
(3-7-1)
5%



3-HH1OB(2F,3F)-1
(3-7-1)
5%



5-dhBB(2F,3F)-O2
(3-10-1)
5%



3-BB(2F,3F)B-2V
(3-12-1)
5%



3-H1OB(2F,3F)-O2
(3)
5%



5-H1OB(2F,3F)-O2
(3)
7%



V-H1OB(2F,3F)-O2
(3)
4%



5-HB-3
(4-1-1)
5%



1-BB-3
(4-2-1)
7%



V-HHB-1
(4-3-1)
5%



3-BB(F)B-2V
(4-5-1)
5%



5-HB(F)HH-V1
(4-10-1)
3%



5-HBB(F)B-3
(4-12-1)
3%







NI = 84.9° C.;



Tc < −20° C.;



Δn = 0.119;



η = 20.9 mPa · s;



Δε = −3.2;



VHR-1 = 98.9%;



VHR-2 = 96.7%;



VHR-3 = 96.5%.






As compared with the composition in Comparative Example 1, the compositions in Example 5 to Example 14 have a higher maximum temperature and a smaller viscosity. Therefore, the liquid crystal composition according to the invention has superior characteristics.
INDUSTRIAL APPLICABILITY
The invention concerns a liquid crystal composition satisfying at least one of characteristics such as a high maximum temperature of a nematic phase, a low minimum temperature of the nematic phase, a small viscosity, a large optical anisotropy, a large dielectric anisotropy, a large specific resistance, a high stability to ultraviolet light and a high stability to heat, or a liquid crystal composition having a suitable balance regarding at least two of the characteristics. A liquid crystal display device including such a composition is applied to constitute an AM device having a short response time, a large voltage holding ratio, a large contrast ratio, a long service life and so forth, and thus can be used for a liquid crystal projector, a liquid crystal television and so forth.

## Claims

1. A liquid crystal composition that has a negative dielectric anisotropy and contains at least one compound selected from the group of compounds represented by formula (1) as a first component and at least one compound selected from the group of compounds represented by formula (2) as a second component:



wherein R1 is


FCH2u 


wherein u is an integer from 1 to 12;
R2, R3 and R4 are independently alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen and at least one methylene may be replaced by oxygen;
ring A and ring B are independently




in the rings, at least one hydrogen may be replaced by halogen;
X1 and X2 are independently fluorine or chlorine;
Y1 is hydrogen or methyl;
Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and
m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3.

2. The liquid crystal composition according to claim 1, wherein the first component is at least one compound selected from the group of compounds represented by formula (1-1) to formula (1-4):



wherein R1 is


FCH2u 


wherein u is an integer from 1 to 12;
R2 is alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, and in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen and at least one methylene may be replaced by oxygen.

3. The liquid crystal composition according to claim 1, wherein, in the second component, R3 or R4 is alkenyl having 2 to 12 carbons in which at least one hydrogen may be replaced by halogen, or alkenyl having 2 to 12 carbons in which at least one methylene may be replaced by oxygen in formula (2).

4. The liquid crystal composition according to claim 1, wherein a ratio of the first component is in a range of 3 wt % to 90 wt %, and a ratio of the second component is in a range of 10 wt % to 97 wt %, based on a total weight of the liquid crystal composition.

5. The liquid crystal composition according to claim 1, further containing at least one compound selected from the group of compounds represented by formula (3) as a third component:



wherein R5 and R6 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons or alkenyl having 2 to 12 carbons;
ring C and ring D are independently




in the rings, at least one hydrogen may be replaced by halogen;
X3 and X4 are independently fluorine or chlorine;
Y2 is hydrogen or methyl;
Z3 and Z4 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and
p and q are independently 0, 1, 2 or 3, and a sum of p and q is 1, 2 or 3.

6. The liquid crystal composition according to claim 5, wherein the third component is at least one compound selected from the group of compounds represented by formula (3-1) to formula (3-12):







wherein R5 and R6 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons or alkenyl having 2 to 12 carbons.

7. The liquid crystal composition according to claim 5, wherein a ratio of the third component is in a range of 15 wt % to 85 wt % based on a total weight of the liquid crystal composition.

8. The liquid crystal composition according to claim 1, further containing at least one compound selected from the group of compounds represented by formula (4) as a fourth component:



wherein R7 and R8 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine;
ring E, ring F and ring G are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene or 3-fluoro-1,4-phenylene;
Z5 and Z6 are independently a single bond, ethylene, methyleneoxy or carbonyloxy;
r is 0, 1, or 2; and
when r is 0, at least one of ring F and ring G is 1,4-phenylene.

9. The liquid crystal composition according to claim 8, wherein the fourth component is at least one compound selected from the group of compounds represented by formula (4-1) to formula (4-12):







wherein R7 and R8 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine.

10. The liquid crystal composition according to claim 8, wherein a ratio of the fourth component is in a range of 5 wt % to 50 wt % based on a total weight of the liquid crystal composition.

11. The liquid crystal composition according to claim 1, further containing at least one compound selected from the group of compounds represented by formula (5) as a fifth component:



wherein R9 and R10 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine;
ring I and ring J are independently 1,4-cyclohexylene or 1,4-phenylene;
Z7 and Z8 are independently a single bond, ethylene, methyleneoxy or carbonyloxy; and
s and t are independently 0, 1, 2 or 3, and a sum of s and t is 1, 2 or 3.

12. The liquid crystal composition according to claim 11, wherein the fifth component is at least one compound selected from the group of compounds represented by formula (5-1) to formula (5-5):




wherein R9 and R10 are independently alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons, alkenyl having 2 to 12 carbons, or alkenyl having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine.

13. The liquid crystal composition according to claim 11, wherein a ratio of the fifth component is in a range of 5 wt % to 40 wt % based on a total weight of the liquid crystal composition.

14. The liquid crystal composition according to claim 1, wherein a maximum temperature of a nematic phase is 70° C. or higher, an optical anisotropy (25° C.) at a wavelength of 589 nanometers is 0.08 or more, and a dielectric anisotropy (25° C.) at a frequency of 1 kHz is −2 or less.

15. A liquid crystal display device including the liquid crystal composition according to claim 1.

16. The liquid crystal display device according to claim 15, wherein an operating mode in the liquid crystal display device is a VA mode, an IPS mode, a PSA mode or a FPA mode, and a driving mode in the liquid crystal display device is an active matrix mode.

17. A method for using the liquid crystal composition according to claim 1, including putting the liquid crystal composition according to claim 1 in a liquid crystal display device.

18. A method for using a compound represented by formula (1), including mixing the compound represented by formula (1) in a liquid crystal composition:



wherein R1 is


FCH2u 


wherein u is an integer from 1 to 12;
R2 is alkyl having 1 to 12 carbons or alkenyl having 2 to 12 carbons, wherein in the alkyl or the alkenyl, at least one hydrogen may be replaced by halogen, and at least one methylene may be replaced by oxygen;
ring A and ring B are independently




in the rings, at least one hydrogen may be replaced by halogen;
X1 and X2 are independently fluorine or chlorine;
Y1 is hydrogen or methyl;
Z1 and Z2 are independently a single bond, ethylene, methyleneoxy or carbonyloxy;
m and n are independently 0, 1, 2 or 3, and a sum of m and n is 1, 2 or 3; and
when m is 2 and n is 0, at least one ring A is tetrahydropyran-2,5-diyl or 1,4-phenylene.