# Patent

## Title
Doped silica glass articles and methods of forming doped silica glass boules and articles

## Abstract

The present invention provides doped titania-doped silica glass articles having low thermal expansions and low variations in thermal expansion. According to one embodiment of the invention, a titania-doped silica glass article has a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; and a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C. and 30° C.

## Background
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates generally to methods of forming glass articles, and more specifically to methods of forming titania-doped silica glass articles suitable for use in extreme ultraviolet lithography applications.
2. Technical Background
The desire for faster, more powerful integrated circuits has led to rapid development of advanced ultraviolet photolithographic methods. The performance of an integrated circuit increases as the feature size decreases, since a decrease in feature size allows more circuitry to be put on a chip of a given size, and reduces the power needed for operation. The feature sizes obtainable in a photolithographic process depend on the wavelength of radiation used in the exposure step; shorter wavelengths enable smaller feature sizes. As such, there has been a trend toward shorter wavelengths in photolithographic processes. Currently, photolithography systems based on wavelengths as low as 193 nm and 157 nm are being developed for commercial use.
In order to further decrease the minimum feature size obtainable in photolithographic processes, it has been suggested to use extreme ultraviolet (EUV) radiation, for example, having a wavelength of about 13 nm. The use of EUV radiation in photolithography, while greatly reducing feature size, forces a radical departure in design from currently used photolithographic apparati. First, no currently practical condensed materials are sufficiently transparent to EUV radiation to be used as windows, lenses or photomasks. As such, any manipulation of the radiation must be performed using reflection. Mirrors constructed from alternating layers of molybdenum and silicon deposited on low thermal expansion substrates have been used as reflecting focusing mirrors, collimators, and photomasks in EUV apparati.
Titania-doped silica glass is conventionally used as the low thermal expansion substrate in EUV lithography mirrors. In one conventional method, high purity titania-doped silica glasses are formed by deposition of titania-doped silica soot formed by flame hydrolysis of silicon- and titanium-containing precursors (e.g., octamethylcyclo-tetrasiloxane and titanium isopropoxide). The soot is deposited in a revolving collection cup in a refractory furnace at a temperature high enough to consolidate the soot into a glass body. The amount of titania is adjusted so that the glass body has a coefficient of thermal expansion of about 0 ppb/° C. at a desired operating temperature. Titania-doped silica made using this method tends to have striae formed therein. Striae are periodic inhomogeneities in the glass which adversely effect many properties of the glass. For example, the striae cause an inhomogeneity in thermal expansion in the glass, causing reflective optics made therefrom to have less than optimal thermal properties. The striae can also impact the surface finishing of the glass, making it difficult to form the extremely smooth surfaces needed in EUV lithography elements. The striae also cause optical inhomogeneities, which make the glass unsuitable for use in many optical transmission elements (e.g., lenses, windows, prisms).
It would be advantageous to provide new methods for manufacturing a titania-doped silica glass having a low thermal expansion, a high homogeneity, good optical properties and a precisely controlled composition.
SUMMARY OF THE INVENTION
One embodiment of the present invention relates to a method of producing a titania-doped silica glass boule, the method including the steps of providing a substantially homogeneous titania-doped silica glass rod, the titania-doped silica glass rod having a titania content of between about 1 and about 10 wt %, the titania-doped silica glass rod being substantially non-porous; feeding the titania-doped silica glass rod into a furnace, the furnace having a glass collection surface therein, wherein the titania-doped silica glass rod is softened in the furnace to form a softened titania-doped silica glass, and the softened titania-doped silica glass is deposited on the collection surface, thereby forming a softened titania-doped silica glass mass; and cooling the titania-doped silica glass mass to produce the titania-doped silica glass boule.
Another embodiment of the present invention relates to a titania-doped silica glass article having a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; and a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C. and 30° C.
The devices and methods of the present invention result in a number of advantages over prior art devices and methods. For example, the present method allows the skilled artisan to form titania-doped silica rods using a method chosen for convenience and its ability to deliver highly pure, highly homogeneous materials, and not for its ability to form a large titania-doped silica boule. The silica-doped titania rods are then softened and collected in a furnace to form a boule of a desirably large size. The present invention provides large bodies of highly pure, highly homogeneous titania-doped silica materials having low levels of striae.
Additional features and advantages of the invention will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from the description or recognized by practicing the invention as described in the written description and claims hereof, as well as in the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description are merely exemplary of the invention, and are intended to provide an overview or framework for understanding the nature and character of the invention as it is claimed.
The accompanying drawings are included to provide a further understanding of the invention, and are incorporated in and constitute a part of this specification. The drawings are not necessarily to scale, and sizes of various elements may be distorted for clarity. The drawings illustrate one or more embodiment(s) of the invention, and together with the description serve to explain the principles and operation of the invention.



BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic view of a titania-doped silica rod being fed into a furnace; and
FIG. 2 is a schematic view of a titania-doped silica rod being fed into a furnace along an axis offset from the axis of rotation of the collection surface;



DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
One embodiment of the present invention relates to a method of producing a titania-doped silica glass boule. First, a substantially homogeneous titania-doped silica glass rod having a titania content of between about 1 wt % and about 10 wt % is provided. The titania-doped silica glass rod is fed into a furnace having a glass collection surface therein. In the furnace, the titania-doped silica glass rod is softened to form a softened titania-doped silica glass, which is deposited on the melting surface to form a softened titania-doped silica glass mass. The softened titania-doped silica glass mass is cooled to produce the titania-doped silica glass boule.
The titania-doped silica glass rod is substantially homogeneous, and is desirably substantially non-porous. It desirably has a low level of striae; for example, the index difference between striae (Δnstriae) is desirably less than 100 ppm, and the stress difference between striae (Δstressstriae) is desirably less than 0.15 MPa. The titania-doped glass rod also desirably has a high overall homogeneity; for example, the index homogeneity is desirably less than 200 ppm.
If a low thermal expansion glass material is required, the titania-doped silica glass rod should have a titania content of between about 5 wt % and about 9 wt %, and a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C. Desirably, the coefficient of thermal expansion of the titania-doped silica glass rod is between −10 ppb/° C. and about +10 ppb/° C. at a temperature between 15° C. and 30° C. More desirably, the coefficient of thermal expansion of the titania-doped silica glass rod is between −5 ppb/° C. and about +5 ppb/° C. at a temperature between 15° C. and 30° C. In certain embodiments of the invention, the coefficient of thermal expansion of the titania-doped silica glass rod is between −2 ppb/° C. and about +2 ppb/° C. at a temperature between 15° C. and 30° C. The skilled artisan will adjust the relative amounts of titania and silica in the titania-doped silica to achieve a desired coefficient of thermal expansion. For near-zero coefficient of thermal expansion at room temperature, a titanium content of between about 6.8 wt % and about 7.8 wt % is desirable.
The titania-doped silica rod may be formed using a number of suitable methods. Powder-based methods are especially desirable, as highly pure titania-doped silica powders may be made by a variety of methods (e.g., flame hydrolysis, chemical vapor deposition, sol-gel processing). When using a titania-doped silica powder, it is desirable that the powder have a mean particle diameter between about 20 nm and about 1000 nm in order to minimize seed (void) formation during consolidation. Likewise, the powder desirably has a surface area of between about 10 m2/g and about 200 m2/g. More desirably, the powder has a mean particle size of about 20 nm to about 200 nm; and a surface area of between about 15 m2/g and about 50 m2/g. A suitable flame hydrolysis method for making a titania-doped silica powder is described in U.S. patent application Ser. No. 10/378,390, which is hereby incorporated by reference herein in its entirety.
For example, one suitable powder-based method is a sol-gel process including the steps of forming a titania-doped silica sol; causing the sol to gel, thereby forming a titania-doped silica gel; drying the titania doped silica gel to form a porous titania-doped silica body; and heating the titania-doped silica body to form the titania-doped silica glass rod. The titania-doped silica sol may be formed by dispersing a titania-doped silica powder (e.g., a titania-doped silica soot made by flame hydrolysis or chemical vapor deposition) in a liquid phase (e.g., water). A suitable sol-gel process is described in more detail in the Example, below. Sol-gel methods in which the sol is formed by solution phase hydrolysis and condensation of silanes and titanates may also be used in the present invention.
Other powder-based methods, such as slip casting, extrusion/firing, isostatic pressing, and hot pressing may be used to form the titania-doped silica glass rods. For example, one suitable method, described in U.S. patent application Ser. No. 10/085,838, which is hereby incorporated herein by reference, includes the steps of providing a titania-doped silica glass soot; spray-drying the soot to form an agglomerate; dry-pressing the agglomerate to form a porous titania-doped silica body; and heating the titania-doped silica body to form the titania-doped silica glass rod. Other suitable methods for forming the titania-doped silica glass rods are described in U.S. patent application Ser. Nos. 10/378,390; 10/086,231; and 10/086,238, each of which is hereby incorporated herein by reference.
When making a titania-doped silica glass rod using a sol-gel- or powder-based method, a porous titania-doped silica body is usually formed as an intermediate. It is generally necessary to heat the porous titania-doped silica body to dry it and to consolidate it into a substantially homogeneous rod. The drying process will typically include a relatively low temperature (e.g., 400° C. to 1000° C.) treatment to remove adsorbed water and any organic compounds present in the body. After the low temperature heat treatment, a higher temperature (e.g., 1300° C. to 1550° C.) treatment is performed to consolidate the porous body into a homogenous glass rod. The consolidation is desirably performed in an atmosphere of helium, which has high permeability in titania-doped silica. Any seeds (voids) in the glass rod can be removed by heating to the softening point of the glass in a non-helium containing vacuum. The helium will readily diffuse out of the seed, but no other gas will readily permeate the glass to diffuse into the seed. Hence, a vacuum will be left in the seed, which will collapse due to capillary forces when the glass approaches its softening temperature. Porous titania-doped silica bodies having a median pore size of less than 20 microns are desirable for use in the present invention, as they are easier to consolidate into virtually seed-free rods. More desirably, the porous titania-doped silica body has a median pore size of less than 1 micron.
Once the substantially homogeneous titania-doped silica glass rod is provided, it is fed into a furnace to be softened and collected into a mass. An example of this step is shown in schematic view in FIG. 1. In FIG. 1, furnace 20 includes support table 22, which is desirably configured to be rotatable. A refractory cup 24 made from a refractory material (e.g., zirconia) sits on top of the table. The shape of the cup is selected to provide a desired shape to the boule. A bait material 26 (e.g., high purity silica sand) prevents adhesion of the titania-doped silica glass to surface of the bottom the refractory cup, while glass liners 28 prevent adhesion to the sides of the cup. The bait material 26 and glass liners 28 provide a collection surface for the softened titania-doped silica glass. Furnace 20 includes refractory crown 30, which helps maintain the temperature inside the furnace, and holds burners 32 in place. Burners 32 may be, for example, methane/oxygen burners, and are configured to direct flames 36 toward the refractory cup. The sidewalls and bottom of the furnace are indicated in the schematic view of FIG. 1 by dashed line 34.
In use, a titania-doped silica glass rod 40 is fed into the furnace, and is softened to form a softened titania-doped silica glass, which is deposited on the collection surface, forming a softened titania-doped silica glass mass 42. Desirably, the temperature in the furnace is in the range of 1600° C. to 2100° C. More desirably, the temperature in the furnace is in the range of 1700° C. to 2000° C. In certain especially desirable embodiments of the invention, the temperature in the furnace is hot enough to melt the titania-doped silica glass rod 40, so that the melted glass may flow readily onto the collection surface. The titania-doped silica rod is lowered into the furnace at a controlled rate selected by the skilled artisan to provide a reasonable rate of deposition while allowing the titania-doped silica rod to soften sufficiently. Desirably, the furnace has a non-reducing atmosphere to avoid formation of reduced titanium species such as Ti(III) in the glass. Furnace atmospheres having a partial pressure of oxygen greater than 10−4 atmospheres are generally sufficiently non-reducing. Suitable furnaces are described in U.S. Pat. Nos. 5,043,002; 5,152,819; and 5,970,751, each of which is hereby incorporated herein by reference in its entirety.
The titania-doped silica glass mass 42 takes the shape of the inside of the refractory cup 24. Advantageously, the refractory cup dimensions can be much larger than the diameter of the titania-doped silica glass rod. For example, the refractory cup can have an inner diameter more than three times greater than that of the titania-doped silica glass rod. In certain embodiments of the invention, the refractory cup has an inner diameter more than six times greater than that of the titania-doped silica glass rod. In the present invention, large homogeneous titania-doped silica boules may be made using much smaller titania-doped silica rods as a feedstock; as such, processes which are limited in size (e.g., powder-based methods, sol-gel-based methods) may be used to provide highly pure and highly homogeneous feedstock, which is then transformed to a boule of a desirably large size. There may be relative rotation between the titania-doped silica glass rod and the collection surface. As shown in FIG. 2, the titania-doped silica glass rod 60 may be fed into the furnace 62 along an axis 64 that is offset from the axis of rotation 66 of the collection surface in order to more easily allow the softened glass 68 to fill the refractory cup.
Once a titania-doped silica glass mass of a desired size is formed in the refractory cup, it is cooled to form a titania-doped silica glass boule. The skilled artisan will recognize that it will be desirable to cool the titania-doped silica glass mass slowly to a temperature below its fictive temperature, and that it may be desirable to anneal the boule once it is formed.
The titania-doped silica boule made in the present invention desirably has a low level of striae; for example, Δnstriae is desirably less than 100 ppm, and Δstressstriae is desirably less than 0.15 MPa. The titania-doped glass boule also desirably has a high overall homogeneity; for example, the index homogeneity (through the bulk of the boule, and not counting the surfaces that contacted the bait material or the glass liners) is desirably less than 200 ppm. If a low thermal expansion glass material is required, the titania-doped silica glass boule should have a titania content of between about 5 wt % and about 9 wt %, and a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C. Desirably, the coefficient of thermal expansion of the titania-doped silica glass boule is between −10 ppb/° C. and about +10 ppb/° C. at a temperature between 15° C. and 30° C. More desirably, the coefficient of thermal expansion of the titania-doped silica glass boule is between −5 ppb/° C. and about +5 ppb/° C. at a temperature between 15° C. and 30° C. In certain embodiments of the invention, the coefficient of thermal expansion of the titania-doped silica glass boule is between −2 ppb/° C. and about +2 ppb/° C. at a temperature between 15 ° C. and 30° C. The titnaia-doped silica boule desirably has a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C. and 30° C. The boule desirably has a thickness of between about 25 mm and about 1000 mm, and is more desirably greater than 100 mm in thickness. The boule desirably has a diameter of at least about 20 cm, and more desirably greater than about 50 cm.
Depending upon the method by which the titania-doped silica glass rod is made, a single titania-doped silica glass rod may not provide sufficient glass material for the formation of a desirably large titania-doped silica boule. In such a case, it may be desirable to form the titania-doped silica rod by fusing together a plurality of homogeneous titania-doped silica glass bars, each of which is made by a desired method (e.g., sol-gel processing of titania-doped silica soot). Desirably, the method used to fuse together the titania-doped silica glass bars does not form a substantial interface between the bars, since any interfacial structures (e.g., air-filled gaps) in the titania-doped silica rod may be carried into the titania-doped silica glass mass during deposition. One suitable method for fusing titania-doped silica bars into a rod is direct bonding, such as is described in U.S. patent application Ser. No. 10/255,926 and 10/035,659, each of which is hereby incorporated herein by reference in its entirety. Optical wringing, flameworking, and other heat fusion methods may also be used by the skilled artisan. Alternatively, titania-doped silica glass rods can be fed into the furnace one at a time. In such a process, each titania-doped silica glass rod (except the first) is held just above the titania-doped silica glass mass in the furnace until its end softens sufficiently to flow into the mass; once flow has begun, the titania-doped silica glass rod can be fed into the furnace as described above.
Another embodiment of the invention relates to a titania-doped silica glass article. The titania-doped silica glass article is made by forming a titania-doped silica boule as described above, then finishing the boule into the titania-doped silica glass article. As the skilled artisan will appreciate, the finishing process may include operations such as cutting, grinding, polishing, embossing, flameworking, etching and coating. The titania-doped silica article may be, for example, a lens, a mirror blank, a photolithography mask, a support structure, a window or a prism.
Another embodiment of the invention relates to a titania-doped silica glass article having low thermal expansion and high homogeneity. The titania-doped silica glass article according to this embodiment of the invention has a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; and a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C. and 30° C. Desirably, the absolute value of the coefficient of thermal expansion is less than 10 ppb/° C. at a temperature between 15° C. and 30° C. More desirably, the absolute value of the coefficient of thermal expansion is less than 5 ppb/° C. at a temperature between 15° C. and 30° C. In certain especially desirable embodiments of the invention, the absolute value of the coefficient of thermal expansion is less than 2 ppb/° C. at a temperature between 15° C. and 30° C. The titanium doped article according to this embodiment of the invention may have at least one dimension larger than 20 cm in length. Desirably, the titania-doped silica glass article has refractive index inhomogeneity of less than 150 ppm. More desirably, the titania-doped silica glass article has a refractive index inhomogeneity of less than 50 ppm. Desirably, the titania-doped silica glass article has a Δnstriae less than 100 ppm. The titania-doped silica glass article according to this embodiment of the invention may be made, for example, according to the process described hereinabove.
The titania-doped silica powders and glasses used in the present invention may be made to be extremely pure, and have a desired composition. In one embodiment of the present invention, the titania-doped silica materials consist essentially of oxides of titanium and silicon along with a small amount of dissolved water. Alternatively, other species may be included in the titania-doped silica. For example, the titania-doped silica may include small amounts of cerium and/or aluminum. The skilled artisan will determine the desired chemical composition of the titania-doped silica material depending on the end use and requirements of the final silica-doped titania boule or article.
The invention will be further described by the following non-limiting examples.
EXAMPLE 1
Titania-doped silica powder having a titania concentration of about 7 wt % was formed using a flame hydrolysis process as described in [SP02-028]. Titanium tetraisopropoxide and octamethylcyclotetrasiloxane (1:4.5 weight ratio) were injected into a vaporizer at 140° C. with 8 slpm nitrogen as a carrier gas. The precursor stream was carried to two burners, and combusted with 6 slpm oxygen, and 2 slpm methane/oxygen (1:1). Enough prefiltered air to cool the overall temperature to 100° C. was flowed through the furnace. The titania-doped silica powder so formed was collected. The powder had a titania concentration of about 7 wt %, and a surface area of about 25 m2/g.
The titania-doped silica powder was dispersed in aqueous solution to make a series of sols, as detailed in Table 1. Tetramethylammonium hydroxide was dissolved in water, and titania-doped silica powder was added at 50-70 wt % to form a slurry. The slurry was rolled overnight, then tris(2-aminoethyl)amine was added. The slurry was rolled or mixed for a few minutes, then 1-chloro-2-propanol was added. After a few more minutes of mixing, the sol was ready for further processing.
Lengths of glass tubing sealed on one end with plastic film (SARAN wrap) were used as molds. Typically, molds 25 mm in diameter and 200 mm long were used, but molds up to 160 mm in diameter were used with success. The insides of the molds were treated with a long chain alkyltrialkoxysilane (e.g., octadecyltrimethoxysilane) as a release coating. The sols described above were poured into the molds, then degassed (25-35 Torr for 2-5 minutes) to minimize the presence of bubbles. After degassing, the molds were capped with plastic film, and the sols were allowed to gel at room temperature for 15-72 hours. The results of the gelling operation are shown in Table 1. Strong gels were stiff and released well from the mold. Weak gels were more rubbery in character.












TABLE 1







Tris(2-amino-
1-Chloro-2-





TMAH
ethyl)amine
propanol
Wt %


Sample
(wt %)
(wt %)
(wt %)
powder
Result




















1
2.5
1.4
2.6
55
Strong gel


2
2.5
1.4
1.3
55
No gel


3
2.5
0.7
2.6
55
Weak gel


4
2.5
0.7
1.3
55
Strong gel


5
1.3
1.4
2.6
55
Strong gel


6
1.3
1.4
1.3
55
No gel


7
1.3
0.7
2.6
55
Strong gel


8
1.3
0.7
1.3
55
Weak gel


9
2
1.3
2.4
60
Strong gel


10
1.6
1.2
2.2
65
Strong gel


11
1.4
1.1
2.1
70
Strong gel









The gels were demolded and placed in glass sleeves that were slightly larger in diameter and length than the gel. The sleeves provide maximal support of the somewhat fragile gel, which minimizes stress in the final rod, as well as serve to maintain high relative humidity during the initial drying. The gels were allowed to dry overnight at room temperature, then heated at 120° C. for 24 hours. The dried gels were heated slowly to 700-800° C. in air to remove organics, leaving powder preforms having a density of about 1.2 g/cm3 and a pore size distribution of 0.02-0.07 μm, centered at 0.04 μm.
A powder preform (sample 7) was heated at 800° C. in flowing helium for 10 minutes. The sample was heated at 2° C./min to 1410° C. in helium, and held at that temperature for 10 minutes. The sample was then heated at 2° C./min at 1670° C. in air and held for 10 minutes, forming a homogenous titania-doped silica rod having a variation in coefficient of thermal expansion less than 2 ppb/K. This titania-doped silica rod is suitable for use in the boule forming processes of the present invention.
It will be apparent to those skilled in the art that various modifications and variations can be made to the present invention without departing from the spirit and scope of the invention. Thus, it is intended that the present invention cover the modifications and variations of this invention provided they come within the scope of the appended claims and their equivalents.

## Claims

1. A titania-doped silica glass article having a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; a variation in coefficient of thermal expansion of less than about 5 ppb/° C. at a temperature between 15° C. and 30° C.; and a Δnstriae of less than 100 ppm.

2. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a refractive index inhomogeneity of less than 200 ppm.

3. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article consists essentially of silica and titania.

4. The titania-doped silica glass article of claim 1 having at least one dimension longer than about 20 cm in length.

5. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a refractive index inhomogeneity of less than 100 ppm.

6. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a refractive index inhomogeneity of less than 50 ppm.

7. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a coefficient of thermal expansion of less than 5 ppb/° C. at a temperature between 15° C. and 30° C.

8. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a coefficient of thermal expansion of less than 2 ppb/° C. at a temperature between 15° C. and 30° C.

9. The titania-doped silica glass article of claim 1, wherein the titania-doped silica glass article has a titania content of between about 6.8 wt % and 7.8 wt %.

10. A titania-doped silica glass boule having a titania content of between about 5 wt % and about 9 wt %; a coefficient of thermal expansion of between about −30 ppb/° C. and about +30 ppb/° C. at a temperature between 15° C. and 30° C.; a Δnstriae of less than 100 ppm, and a Δstressstriae less than 0.15 MPa.

11. The titania-doped silica glass boule of claim 10, wherein the boule has a coefficient of thermal expansion of between about −10 ppb/° C. and about +10 ppb/° C. at a temperature between 15° C. and 30° C.

12. The titania-doped silica glass boule of claim 10, wherein the boule has a coefficient of thermal expansion of between about −5 ppb/° C. and about +5 ppb/° C. at a temperature between 15° C. and 30° C.

13. The titania-doped silica glass boule of claim 10, wherein the boule has a coefficient of thermal expansion of between about −20 ppb/° C. and about +20 ppb/° C. at a temperature between 15° C. and 30° C.

14. The titania-doped silica glass article of claim 10, wherein the titania-doped silica glass article has a titania content of between about 6.8 wt % and 7.8 wt %.