# Patent

## Title
Dendritic macromolecule and process for preparation thereof

## Abstract

This is a continuation of application Ser. No. 07/575,738, filed on Aug. 31, 1990, now abandoned, which is a continuation-in-part of our application Ser. No. 07/439,317, filed Nov. 21, 1989, now U.S. Pat. No. 5,112,923.

## Background
1. Technical Field of the Invention

The present invention relates generally to high performance structural resins for advanced aerospace applications. It relates particularly to a tough, solvent resistant, crystalline imide/arylene block copolymer with a broad melting point, and especially to adhesives and composites thereof.

2. Description of the Prior Art

Polyimides are condensation polymers commonly synthesized by the reaction of aromatic dianhydrides with aromatic diamines. The intermediate poly(amic acid) is either thermally or chemically cyclodehydrated to form the polyimide, which has a repeat unit of the general type ##STR1## Ar is a tetravalent aromatic radical which can be as simple as 1,2,4,5-tetrasubstituted benzene, or may be as complex as a bis-4-(o-diphenylene) having the general structure ##STR2## where X=nil, O, S, SO.sub.2, C.dbd.O, etc. As well, Ar may be any other appropriate tetravalent radical. Ar' is a divalent aromatic radical which may be 1,3-phenylene, 1,4-phenylene, 4,4'-biphenylene, 4,4'-oxydiphenylene, 4,4'-thiodiphenylene, 4,4'-carbonyldiphenylene, 4,4'-methanediphenylene or any other appropriate divalent radical.

Synthesis and characterization of polyimides has been extensively reported in the literature. The preparation of aromatic polyimides by reaction of an aromatic dianhydride with an aromatic diamine, followed by thermal cyclization was first reported in 1963 [G. M. Bower and L. W. Frost, Journal of Polymer Science A1, 3134 (1963)] with patents awarded in 1965 [Edwards, U.S. Pat. No. 3,179,614 and U.S. Pat. No. 3,179,634; Endrey, U.S. Pat. No. 3,179,631 and U.S. Pat. No. 3,179,633]. Several reviews on polyimides have been published [S. E. Sroog, "Polyimides" in Encyclopedia of Polymer Science and Technology, (H. F. Mark, N. G. Gaylord, and N. M. Bikales, Ed.), Interscience Publishers, New York, 1969 Vol. 11, pp. 247-272; N. A. Adrova, M. I. Bessonov, L. A. Lauis and A. P. Rudakov, Polyimides, Technomic Publishing Co., Inc., Stamford, Conn., 1970].

Wholly aromatic polyimides are known for their exceptional thermal, thermooxidative, and chemical resistance but are generally difficult to process as structural adhesives or composite matrices. Several polymides such as Kapton.RTM. [DuPont], PI-2080 [Upjohn], XU-218 [Ciba-Geigy], Ultem.RTM. [General Electric], and LARC-TPI [Mitsui Toatsu] are commonly available commercially and used as films, moldings, adhesives, and composite matrices.

Poly(arylene ethers) are condensation polymers commonly synthesized by nucleophilic displacement of activated aromatic halides in polar solvents by alkali metal phenates to form a repeat unit of the general type ##STR3## Ar is arylene and y=C.dbd.O, SO.sub.2, etc. ##STR4## Nucleophilic displacement reactions leading to high molecular weight poly(arylene ethers) were initially reported in 1958 [A. Kreuchumas, U.S. Pat. No. 2,822,351 (1958)]. Since then, numerous papers [R. N. Johnson, et al., J. Polym. Sci. A1, 5,2375 (1967); S. V. Vinogradova, et al., Polym. Sci. USSR, 14, 2963 (1972); J. B. Rose, Polymer, 15, 456 (1974); T. E. Attwood, et al., Polym. Prepr., 20(1), 191 (1979); R. Viswanathan, et al., Polymer, 25, 1927 (1984); and P. M. Hergenrother, et al., Polymer, 29, 258 (1988)] and patents [Jones, British 1,016,245 (1962), Vogel, British 1,060,546 (1963); Goodman, et al., British 971,277 (1964); Farnham, et al., British 1,078,234 (1973); and Farnham U.S. Pat. No. 4,175,175 (1979)] have appeared.

Poly(arylene ethers) are known for their good mechanical properties, good thermooxidative stability, relative ease of processing, and solubility in common organic solvents. For certain applications, resistance to common organic solvents is a requirement. Several poly(arylene ethers) such as Udel.RTM. polysulfone [Amoco], Kadel.RTM. polyketone [Amoco], PEEK.RTM. polyetherketone [ICI] are commercially available and used as films, moldings, adhesives, and composite matrices.

Amine terminated arylene ethers have been prepared by several different methods. The preparation of amine terminated polysulfone oligomers using p-aminophenol as the end-capping compound was reported in 1974 [J. H. Kawakami, et. al., J. Polym. Sci. Poly. Chem. Ed., 12, 565 (1974)]. More recently, the preparation of amine terminated polysulfone and poly(arylene ether ketone) oligomers using m-aminophenyl-4'-hydroxyphenyl-2.2-isopropylidene has been reported [M. J. Jurek, et al., Polym. Prepr., 26(2), 283 (1985); G. D. Lyle, et al., Polym. Prepr., 28(1) 77 (1987)].

The introduction of crystallinity into a polymer has long been recognized as an effective means of improving the solvent resistance and increasing the modulus. In addition, if the proper degree and type of crystallinity is attained, the material can also display extremely high toughness. Notable examples are PEEk.RTM. polyetheretherketone [IC] and LARC-CPI [P. M. Hergenrother, et al., SAMPE Journal., 24(4) 13 (1988)] which exhibit very high fracture toughness (G.sub.IC, critical strain energy release rate) and are highly solvent resistant.

Accordingly, it is a primary object of the present invention is to provide a series of block copolymers that contain polyimide and poly(arylene ether) segments.

Another object of the present invention is to provide a block copolymer that contains polyimide and poly(arylene ether) segments, such that the copolymer has a high degree of crystallinity.

Another object of the present invention is to provide a block copolymer that contains polyimide and poly(arylene ether) segments, wherein the length of the polyimide and poly(arylene ether) segments are easily controlled, so that copolymers with various desired physical and mechanical properties can be produced.

Another object of the present invention is to provide a block copolymer that contains polyimide and poly(arylene ether) segments, wherein the copolymer forms a tough, solvent resistant film and coating material.

Another object of the present invention is to provide a block copolymer that contains polyimide and poly(arylene ether) segments, wherein the copolymer forms a film and coating material with high tensile properties.

Another object of the present invention is to provide a film and coating material useful for both industrial and aerospace applications requiring adhesives and composites, with good solvent resistance and high tensile properties, such as strength, modulus and elongation.

By the present invention, the foregoing and additional objects were obtained by synthesizing imide/arylene copolymers from the reaction of anhydride terminated poly(amic acids) and amine terminated poly(arylene ethers). After curing, the resulting block copolymers had glass transition temperatures ranging from 165.degree. C. to 220.degree. C. Some had two glass transitions, corresponding to the arylene/ether segment and the imide segment, indicating a phase separation in the films due to polymer-to-polymer incompatibility. The block copolymers also had broad crystalline melting points (T.sub.m) from 335.degree. C. to 355.degree. C. Some had two T.sub.m s and, therefore, possibly two crystalline forms. Solution cast films of the block copolymers were tough and flexible with tensile strength, tensile moduli, and elongation at break up to 16,200 psi, 535,000 psi, and 8% respectively at 25.degree. C. And, depending on the glass transition temperatures of the arylene/ether segment, some block copolymers maintained good mechanical properties at 93.degree. C. and 177.degree. C.

Moldings were prepared from polymers which were solution imidized, by distilling a toluene/water azeotropic mixture from the reaction at 155.degree. C. for 16 hours, to form powders. The powders were compression molded in stainless steel molds in hydraulic presses with electrically heated platens. The moldings were machined into compact tension specimens and tested for toughness. The values of fracture toughness, K.sub.IC, and fracture energy, G.sub.IC, for the homopolymers are extremely high and values for the copolymers are excellent and increase with increasing block length.

Wide-angle x-ray scattering data indicated that block and segmented copolymer films cured up to 300.degree. C. for 1 hour and solution imidized powders were crystalline. Furthermore, copolymers with longer imide blocks or higher imide content had more intense and sharper x-ray peaks, indicating more crystallinity than the others.

FIG. 1 demonstrates wide-angle x-ray scattering data for a copolymer film of the present invention; and

FIG. 2 demonstrates wide-angle x-ray scattering data for a copolymer powder of the present invention.

The general reaction sequence for the block copolymers of the present invention is represented by the following equation: ##STR5## wherein n is an integer from 4 to 100. The solvent is preferably N,N-dimethylacetamide, but it may be N-methylpyrrolidinone, m-cresol, N,N-dimethylformamide, dimethyl sulfoxide, or ether solvents such as diglyme.

Cyclodehydration is accomplished chemically or by heating the intermediate poly(amic acid) at temperatures exceeding 150.degree. C.

PAA is representative of a poly(amic acid) synthesized by reacting excess dianhydride with a diamine as generically shown below: ##STR6## wherein n is an integer from 4 to 100. The solvent is preferably N,N-dimethylacetamide, but it may be N-methylpyrrolidinone, m-cresol, N,N-dimethylformamide, dimethyl sulfoxide or ether solvents such as diglyme.

PI is representative of a polyimide synthesized by the cyclodehydration of the PAA component as generically shown below: ##STR7##

Ar is selected from a group of radicals consisting of: ##STR8## wherein Y is not a substituent or is a substituent selected from the group consisting of O, C.dbd.O, and C(CF.sub.3).sub.2.

Ar' is selected from a group of radicals consisting of: ##STR9## wherein Y is not a substituent or is a substituent selected from the group consisting of O, C.dbd.O, and C(CF.sub.3).sub.2.

PAE is representative of a poly(arylene ether) synthesized by reacting an activated aromatic dihalide with a bisphenol as generically shown below: ##STR10## wherein n is an integer from 4 to 100. The solvent is preferably N,N-dimethylacetamide, but may be other solvents such as N-methylpryrrolidinone, N,N-dimethylformamide, or dimethyl sulfoxide.

X is either a fluorine or chlorine atom. The Base is an alkali metal hydroxide or carbonate selected from the group consisting of NaOH, KOH, Na.sub.2 CO.sub.3 and K.sub.2 CO.sub.3.

R and R' are selected from a group of aromatic radicals consisting of: ##STR11## wherein Y is not a substituent or is a substituent selected from the group consisting of O, S, C.dbd.O, SO.sub.2, CH.sub.2, C(CH.sub.3).sub.2, and C(CF.sub.3).sub.2. ##STR12## represents either 3-aminophenol or 4-aminophenol.

The following examples illustrate the reaction sequence for the synthesis of several polyimides according to the present invention. However, the invention is not limited to these examples.

The following example illustrates the reaction sequence for the synthesis of imide/arylene ether block copolymer ##STR13## X is F, and ##STR14## The theoretical number average molecular weight (M.sub.n) of both the poly(amic acid) block and the poly(arylene ether) block is 6545 g/mole. This copolymer is designated ATPAE 6545//1,3-BABB/BTDA 6545.

1,3-Bis(4-fluorobenzoyl)benzene (1,3-FBB) (0.1 m, 32.231 5 g), 2,2-bis(4-hydroxyphenyl)propane (BPA) (0.0925 m, 21.1172 g), 4-aminophenol (0.015 m, 1.637 g), powdered potassium carbonate (0.22 m, 30.4 g), N,N-dimethylacetamide (DMAc) (150 ml) and toluene (40 mi) were added to a three-neck flask equipped with a Dean-Stark trap and nitrogen purge. The reaction was heated to 155.degree. C. during approximately 4 hours while collecting a toluene/water azeotropic mixture and held at 155.degree. C. overnight. The reaction was filtered, neutralized with a small amount of acetic acid and precipitated in water. After washing and boiling in water, drying at 80.degree. C. in vacuum provided a light tan solid in greater than 95% yield. The resulting amine-terminated arylene ether oligomer had .eta..sub.inh =0.29 dL/g in DMAc at 25.degree. C.

3,3',4,4'-Benzophenonetetracarboxylic acid dianhydride (BTDA) (0.0035 m, 1.1278 g) was added to a solution of 1,3-bis(4-fluorobenzoyl)benzene (1,3-BABB) (0.003087, m, 1.5452 g) and DMAc (15.2 g) and stirred for 3 hours to provide a viscous, clear yellow solution.

The amine-terminated arylene ether (2.6730 g) was dissolved in DMAc (15.2 g) to provide a clear brown solution which was added to the anhydride-terminated poly(amic acid) solution. The combined solution became viscous immediately and gelled within approximately 10 minutes. Stirring overnight provided a viscous orange solution (.eta..sub.inh =0.89 dL/g, DMAC at 25.degree. C.). Casting onto plate glass and curing 1 hour each at 100.degree. C., 200.degree. C., and 300.degree. C. provided a tough, flexible, clear yellow film (Tg=165.degree. C., Tm=335.degree. C. and 350.degree. C., DSC at 20.degree. C./min).

The following example illustrates the reaction sequence for the synthesis of imide/arylene ether block copolymer where ##STR15## X is F, and ##STR16## The theoretical number average molecular weight (M.sub.n) of both the poly(amic acid) block and the poly(arylene ether) block is 3110 g/mole. This copolymer is designated ATPE 3110//1,3-BABB/BTDA 3110.

1,3-Bis(4-fluorobenzoyl)benzene (1,3-FBB) (0.07 m, 22.562 g), 2,2-bis(4-hydroxyphenyl)propane (BPA) (0.0595 m, 13.583 g), 4-aminophenol (0.021 m, 2.292 g), powdered potassium carbonate (0.154 m, 21.3 g), N,N-dimethylacetamide (DMAc) (115 ml) and toluene (40 ml) were added to a three-neck flask equipped with a Dean-Stark tarp and nitrogen purge. The reaction was heated to 155.degree. C. during approximately 4 hours while collecting a toluene/water azeotropic mixture and held at 155.degree. C. overnight. The reaction was filtered, neutralized with a small amount of acetic acid and precipitated in water. After washing and boiling in water, drying at 80.degree. C. in vacuum provided a light tan solid in greater than 95% yield. The resulting amine-terminated arylene ether oligomer had .eta..sub.inh =0.16 dL/g in DMAc at 25.degree. C.

3,3',4,4'-Benzophenonetetracarboxylic acid dianhydride (BTDA) (0.0035 m, 1.1276 g) was added to a solution of 1,3-bis(fluorobenzoyl)benzene (1,3-BABB) (0.00266 m, 1.13315 g) and DMAc (13.9 g) and stirred for 3 hours to provide a clear yellow solution.

The amine-terminated arylene ether (2.4593 g) was dissolved in DMAc (13.9 g) to provide a clear brown solution which was added to the anhydride-terminated poly(amic acid) solution. The combined solution became viscous within 1 hour (.eta..sub.inh =0.63 dug, DMAc at 25.degree. C.). Casting onto plate glass and curing 1 hour each at 100.degree. C., 200.degree. C., and 300.degree. C. provided a tough, flexible, clear yellow film (Tg=175.degree. C., Tm=354.degree. C., DSC at 20.degree. C./min).

The following example illustrates the reaction sequence for the synthesis of the imide/arylene ether segmented copolymer when ##STR17## X is F, and ##STR18## The theoretical M.sub.n of the poly(arylene ether) block is 6545 g/mole while the poly(amic acid) segment is of random length but has an average M.sub.n of 6545 g/mole. The method of addition of starting materials leads to a final structure for this copolymer of a type which is different from the copolymer described in Example I. This copolymer is designated ATPAE 6545+1,3-BABB+BTDA (6545).

This material is the same as the material prepared in Example I.

This copolymer was prepared with the poly(amic acid) segment synthesized in the presence of the ATPAE, not separately as in Example 1.

1,3-BABB (0.002205 m, 1.1037 g) and ATPAE (0.0025 m, 1.9093 g) were dissolved in DMAc (21.6 g). Addition of BTDA (0.0025 m, 0.8056 g) produced a viscous solution immediately that gelled within approximately 15 minutes. Stirring 24 hours at 45.degree. C. produced a clear viscous solution (.eta..sub.inh =1.15 dL/g, DMAC at 25.degree. C.). Casting onto plate glass and curing 1 hour each at 100.degree. C., 200.degree. C., and 300.degree. C. provided a tough, flexible, clear yellow film (Tg=165.degree. C. and 220.degree. C., Tm=338.degree. C. and 353.degree. C., DSC at 20.degree. C./min).

Data for polymer and copolymer inherent viscosities and glass transition temperatures are presented in Tables I and II. ______________________________________ CHARACTERIZATION OF OLIGOMERS AND POLYMERS Oligomer or Polymer .eta..sub.inh, dL/g T.sub.g (T.sub.m), .degree.C. by ______________________________________ DSC ATPAE 3110      0.16 (CHCl.sub.3) 133 ATPAE 6545      0.29 (CHCl.sub.3) 146 ATPAE 3110 + BTDA 0.79 (DMAc) 165 ATPAE 6545 = BTDA 1.10 (DMAc) 222 (350) 1,3-BABB + BTDA 0.80 (DMAc) 155 FBB + BPA       0.70 (CHCl.sub.3) 155 PI + PAE (1:1 blend) --         155, 222 (361) ATPAE 6545 +    1.15 (DMAc) 165, 220 (338, 353) 1,3-BABB + BTDA (6545) ______________________________________ __________________________________________________________________________ CHARACTERIZATION OF BLOCK COPOLYMERS Polyamic Acid, .eta..sub.inh (dL/g) DSC T.sub.g (T.sub.m), .degree.C. Copolymer          DMAc   NMP   DMAc NMP  TBA Transition, __________________________________________________________________________ .degree.C. ATPAE 3110//1,3-BABB/BTDA 3110 0.63   0.90  175  175  193 (354) (338, 352) ATPAE 3110//1,3-BABB/BTDA 6545 0.87   1.73  170  --   249 (354) (358) ATPAE 6545//1,3-BABB/BTDA 3110 0.81   1.00  168  168  185 (353) (335, 352) ATPAE 6545//1,3-BABB/BTDA 4565 0.89   1.03  165  164, 220 168, 205 (335, 350) (343, 355) __________________________________________________________________________

Data for polymer and copolymer properties, including tensile strength, tensile modulus, elongation, fracture toughness, and fracture energy, are presented in Table III. __________________________________________________________________________ FILM PROPERTIES Tensile Strength, Ksi Tensile Modulus, Ksi Elongation, % K.sub.ic, psi .sqroot.in G.sub.ic, in-lb/in.sup.2 Polymer        RT 93.degree. C. 177.degree. C. RT 93.degree. C. 177.degree. C. RT 93.degree. C. 177.degree. C. RT    RT __________________________________________________________________________ ATPAE 3110/BTDA 10.9 9.1 1.2  367 333 124 4.0 3.3  80  --    -- ATPAE 6545/BTDA 11.1 8.5 --   367 329 --  5.7 5.2  >100 --    -- ATPAE 3110//1,3-BABB/ 15.0 12.7 3.4  514 449 135 3.5 3.2  38  3370  22 BTDA 3110 ATPAE 3110//1,3-BABB/ 16.2 14.5 5.9  535 516 304 3.8 3.7  30  3900  28 BTDA 6545 ATPAE 3110//1,3-BABB/ 13.2 10.5 1.4  435 433  35 3.1 15.1 74  3930  35 BTDA 3110 ATPAE 3110//1,3-BABB/ 14.2 10.9 2.7  519 437 114 4.3 3.3  49  4750  44 BTDA 6545 ATPAE 6545 + 1,3-BABB + 16.0 12.7 2.2  457 443  85 6.1 3.8  53  3350  25 BTDA (6545) 1,3-BABB + BTDA 22.0 --  15.2 630 --  540 8.3 --   21  4890  38 FBB + BPA      12.7 7.5 --   381 340 --  136 124  --  5070  62 __________________________________________________________________________

FIGS. 1 and 2 show wide-angle x-ray scattering data for the ATPAE 6454//1,3-BABB/BTDA 6545 copolymer film and powder, respectively.

## Claims

States is:

1. A crystalline imide/arylene ether block copolymer prepared by reacting an anhydride terminated polyamic acid and an amine terminated poly(arylene ether) in a polar aprotic solvent and cyclodehydrating the intermediate poly(amic acid), the anhydride terminated poly(amic acid) having the formula: ##STR19## n is an inter from 4 to 100; wherein ##STR20## and the amine terminated poly(arylene ether) having the formula ##STR21## wherein n is an integer from 4 to 100; R is ##STR22## and R' is ##STR23##

2. The crystalline imide/arylene ether block copolymer of claim 1, wherein the theoretical number average molecular weight of both the poly(amic acid) block and the poly(arylene ether) block is between about 1000 g/mole and 10,000 g/mole.

3. The crystalline imide/arylene ether block copolymer of claim 1, wherein the theoretical number average molecular weight of both the poly(amic acid) block and the poly(arylene ether) block is about 3000 g/mole.

4. The crystalline imide/arylene ether block copolymer of claim 1, wherein the theoretical number average molecular weight of both the poly(amic acid) block and the poly(arylene ether) block is about 6500 g/mole.

5. The crystalline imide/arylene ether block copolymer of claim 1, wherein the theoretical number average molecular weight of the poly(arylene ether) block is 6545 g/mole, and the poly(amic acid) block is of random length, but whose number average molecular weight is 6545 g/mole.

6. The crystalline imide/arylene ether block copolymer of claim 1, wherein the theoretical number average molecular weight of the poly(arylene ether) block is between about 1000-10,000 g/mole, and the poly(amic acid) block is of random length, but whose number average molecular weight is about 1000-10,000 g/mole.