# Patent

## Title
Process and catalyst for converting alkanes

## Abstract

Methods and catalysts for producing alcohols, ethers, and/or alkenes from alkanes are provided. More particularly, novel caged, or encapsulated, metal oxide catalysts and processes utilizing such catalysts to convert alkanes to alcohols and/or ethers and to convert alcohols and/or ethers to alkenes are provided.

## Background
RELATED APPLICATIONS
This application claims priority to U.S. Provisional Application Ser. Nos. 61/194,866 filed on Oct. 1, 2008; 61/211,579, filed on Apr. 1, 2009; and 61/273,308, filed on Aug. 3, 2009, the disclosures of which are each incorporated herein by reference.


BACKGROUND OF THE INVENTION
The invention relates to methods and catalysts for producing alcohols, ethers, and/or alkenes from alkanes. More particularly, the invention relates to a novel caged, or encapsulated, metal oxide catalysts and processes utilizing such catalysts. This invention further relates to a process to convert alkanes to alcohols and/or ethers to alkenes.
Lower alkenes, such as ethylene, propylene and butylene are used for a variety of applications. For example, ethylene is one of the most produced organic compound in the world, with the majority of ethylene being used to produce ethylene oxide, ethylene dichloride, and polyethylene. Lower alkenes may be recovered from petroleum by fractional distillation but demand far exceeds recovery by this method. Therefore, the majority of lower alkenes are produced by energy intensive cracking processes that are well known in the art. For example, ethylene is commonly produced in the petrochemical industry by steam cracking in which gaseous or light liquid hydrocarbons are heated to 700-950° C., in the presence of steam followed by rapid cooling, thereby converting large hydrocarbons into smaller ones and introducing unsaturation. Ethylene is then separated from the resulting product mixture by repeated compression and distillation. More recently, efforts to overcome the energy requirements and other issues, such as CO2 issues, related to steam cracking, have resulted in processes involving catalytic cracking using a fluid-bed catalyst such as those processes described in U.S. Patent Publication No. 20090137857.
Other methods are known for producing alkenes, such as from acid dehydration of alcohols, are also well known. Such methods, however, have heretofore, only been practical in laboratory, and not industrial, settings and quantities. In such laboratory methods, alcohols may be formed by reaction of alkyl halides and metal hydroxides. For example, U.S. Pat. No. 5,334,777 shows the reaction of methyl chloride in the vapor phase with magnesium oxide and with magnesium oxide zeolite. U.S. Pat. No. 3,172,915 discloses the use of ferric oxide as a base to react with methyl chloride to form methyl alcohol, while U.S. Pat. No. 5,998,679 discloses a process in which ferric hydroxide is used as a base to react in the liquid phase with methyl bromide. Finally, U.S. Pat. Nos. 6,462,243; 6,465,696; 6,472,572; 6,486,368; 6,403,840; and 6,525,230 all disclose a process in which alkyl bromides are reacted with a metallic oxide to form alcohols and other products, such as di-methyl ether. All of these processes remain impractical for industrial use due mainly to catalyst attrition and over-halogenation problems resulting in the need for expensive re-crystallation.
There remains a need, therefore, for a process to form alcohol, ether or alkene at commercially practicable rates, with minimization or elimination of formation of other related compounds, and specially higher halides. There is a further need for catalysts to effectuate such process while minimizing or preventing the simultaneous production of higher halides during alcohol or alkene formation.
SUMMARY OF THE INVENTION
In one aspect of the invention provide a process to convert alkanes into alcohols and/or ethers including halogenating one or more alkanes with one or more halogens to form one or more alkane halides and one or more hydrogen halide acids; and reacting the alkane halides and hydrogen halide acid with one or more encapsulated metal oxide catalysts to form one or more compounds selected from the group of alkyl alcohols, ethers and alkenes and one or more metal halide; wherein the one or more encapsulated metal oxide catalysts comprises a pelletized and calcined mixture of an encapsulating material and an organic metal salt. In specific embodiments of the invention, the organic metal salt is selected from magnesium citrate and magnesium stearate. In certain embodiments, the encapsulating material is selected from bentonite, bauxite, and kaolin clays.
In another aspect of the invention, alkanes are further converted to alkenes by further conversion of the alcohols and/or ethers to alkenes by use of an appropriate catalyst. In some embodiments, the encapsulating material functions as a catalyst to convert alcohols and/or ethers to alkenes. In specific embodiments of the invention, the encapsulating material is process of claim 1 wherein the clay is bentonite.
In another aspect of the invention, a novel catalyst for the conversion of alkanes is provided wherein the catalyst is an encapsulated metal oxide. In certain embodiments of the invention, the encapsulating material is a clay having a pore size of 5 and 300 millimicrons, while in other embodiments, the pore size is between 10 and 100 millimicrons



BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic diagram of the one embodiment of the inventive process.
FIG. 2 is a schematic diagram of an alternative embodiment of the inventive process.



DESCRIPTION OF THE PREFERRED EMBODIMENTS
Embodiments of the invention provide novel, highly effective encapsulated metal halide catalyst compositions for the formation of alcohols and alkenes.
In order that the invention be better understood the following equations illustrating the use of chlorine or bromine as the halide, magnesium as the active metal and magnesium chloride hydroxide or magnesium bromide hydroxide as the reacting base are shown:
Chlorination Step

CH4(g)+Cl2(g)→CH3Cl(g)+HCl(g)

Alcohol Formation

CH3Cl(g)+HCl(g)+2Mg(OH)Cl+3H2O(g)→CH3OH(g)+2MgCl2*2H2O

Chlorine and Base Formation

2MgCl2*2H2O+O2(g)→2Mg(OH)Cl+Cl2(g)+3H2O(g)

Alkene Formation

2CH3OH(g)→C2H4(g)+2H2O(g)

The overall reaction is

2CH4(g)+O2(g)→C2H4(g)+2H2O

Bromination Step

CH4(g)+Br2(g)→CH3Br(g)+HBr(g)

Alcohol Formation

CH3Br(g)+HBr(g)+Mg(OH)2→MgBr2*H2O+CH3OH(g)

Bromine and Hydroxide Formation

MgBr2*H2O+1⁄2O2(g)→Mg(OH)2+Br2(g)

Alkene Formation

2CH3OH(g)→C2H4(g)+2H2O(g)

As previously discussed processes utilizing these reaction steps have heretofore been commercially impracticable because of attrition. Embodiments of the invention provide encapsulated metal oxide catalysts and processes using such novel catalysts to produce alcohols and alkenes from alkanes. In some embodiments of the invention, the material used to encapsulate the metal oxide catalyst may also function as a catalyst for the conversion of alcohols to alkenes. In certain embodiments of the present invention, one or more metal oxides are encapsulated in clay particles. The encapsulated metal oxide catalyst is produced by mixing one or more insoluble or slightly soluble high molecular volume organic metal salt with one or more porous materials, in a preferred embodiment, a clay material, including without limitation, kaolin, bentonite, and bauxite, and water to form a dough which is then pelletized, dried in air at typical room temperatures. The dried pellets are then heated in air to a temperature between 600° C. and 1000° C. to form a strong ceramic, porous pellet. Because the clay is annealed and hardened, it is important that the pore size be sufficiently large to house the metal halide hydrate, which is formed by exposure of the metal salt to water, without fracturing the clay structure. In preferred embodiments of the invention, the metal salt is a metal organic salt.
Alkanes useful in embodiments of the present invention include any alkanes having one or more carbon atoms. In a preferred embodiment, the alkane is methane. In other embodiments of the invention, the alkane feed includes more than one alkane.
The proportions of the organic metal salt to clay may vary from about 30 wt % clay to metal salt to clay to about 50 wt % metal salt to clay. The higher the proportion of clay to organic metal salt, the harder the pellet but the lower the capacity for alcohol production. The pellets can be made spherical or in any other shape, by hand or by machine techniques known in the art. Other types of clays may be used. The particle size may be any of the known particle sizes for known clays. In a preferred embodiment, the clay particle size is between 1 and 40 millimicrons.
Metals useful in embodiments of the invention may include any alkaline earth, alkali, basic or transition metal. Group 2 metals are preferred and zinc and magnesium are most preferred for use in the metal salt. Any halogen may be used to form the metal salt. Metal chlorides and bromides are used in preferred embodiments of the invention.
In a first preferred embodiment of the invention, the metal halide is magnesium chloride and in a second preferred embodiment the metal halide is magnesium bromide. In yet other embodiments of the invention the metal salt is zinc chloride or zinc bromide. In some embodiments of the invention, one or more metal halides are used wherein the metals may be the same or different metals and the halogen component may be the same or different halogens.
The weight proportion of the clay in the combined mixture of water, clay, and organic metal salt should be at least 30% by weight of clay. The weight percent of water may range from 20% to 30%. The weight percent of the organic metal salt may range from 50% to 70%. Without intending to be bound to any particular theory, it is believed that the clay particles in the mixture provide a highly porous material. For example, if magnesium citrate, having a molar volume of about 460 cubic centimeters per mole, is used as the organic metal salt, the pores left in the pellets formed from the mixture would be sufficient to accommodate the maximum size of the magnesium chloride hydrate, which is 130 cubic centimeters per mole for the hexa-hydrate MgCl2*6H2O. Thus, the clays used to produce the novel catalysts provide sufficiently large openings to accommodate the hexa-hydrate and not burst the clay structure. In a preferred embodiment of the invention, the pore size of the final ceramic clays is between 5 and 300 millimicrons. In a more preferred embodiment, the pore size is between 10 and 100 millimicrons.
Bentonite clay is a known catalyst for alkene formation from alcohols. Thus, when bentonite is used to encapsulate the metal halide hydrate, no additional activation agents are required to catalyze the formation of alkenes from alcohols. Other known clays and/or support structures are also known to catalyze the formation of alkenes from alcohols and the use of such supports and/or clays is within the scope of this invention. For example, montmonillonite, illite, chorite clays and certain phylosilicates also are known to catalyze the conversion of alcohols to alkenes and may be used as the encapsulating material in certain aspects of the invention. In embodiments of the invention utilizing kaolin and/or bauxite, additional activation agents or catalysts must be used to convert the alcohol into alkene.
In those embodiments of the invention in which the encapsulating material does not catalyze the conversion of alcohols to alkenes, or does not catalyze such conversion with adequate efficiency, small amounts, i.e., from 1 wt % to 10% and preferably about 2 wt % of finely ground X-type zeolite (also known as molecular sieves) in the acid form may be added to the mixture prior to formation of the dough and polarization. Alternatively, Y-type zeolite or an excess (i.e., over about 10%) of a finely ground X-type zeolite powder may be added to the mixture prior to formation of the dough and pelletization.
Halogenation of methane may be accomplished by means of any of a number of catalysts known in the art. However, industrially useful catalysts for methane halogenation include ultraviolet light and/or heat. Embodiments of the invention include the use of methyl halides, however produced or supplied. When temperature is used as a catalyst, the temperature for the methane halogenation step may range from 100° C. and 500° C., more preferably from 150° C. to 400° C. and most preferably from 250° C. to 350° C.
For formation of alcohol from the alkane halide utilizing the novel catalysts of the invention, the temperature is preferably between 120° C. and 200° C. but temperatures as low as 100° C. and as high 250° C. may be utilized. Likewise the alcohols may be converted to alkenes in the presence of the encapsulated metal oxide catalysts of the invention at similarly low temperatures, i.e., from between about 100° C. and 300° C., preferably between about 100° C. and 200° C. and most preferably between about 120° C. and 150° C.
FIG. 1 shows schematically one possible process equipment and materials flow for the inventive process. Referring to FIG. 1, to form halide vapor, heated air is led from line 1 and opened valve 2 through line 3 and opened valve 4 to tubular reactor 5. The tubes of tubular reactor 5 contain the inventive encapsulated metal halide. Halide vapor together with excess air leaves reactor 5 through opened valve 6 and is led through line 7 to condenser 8 where most of the alkyl halide is condensed and flows down to line 9. Excess air and nitrogen containing traces of halide are led through line 8a from condenser 8 to absorber 11 where the halide is absorbed and concentrated in an appropriate solvent down flowing through absorber 11. Halide containing solvent flows downwardly through line 12 to stripper 13 where it meets a counter flow of methane coming through line 14 which strips the halide from the down flowing solvent. The halide-stripped solvent leaves stripper 13 through line 15 and is led through pump 16 to line 17 which feeds absorber 11. Excess air and nitrogen are exhausted from absorber 11 trough line 18.
Halide-enriched methane from striper 13 is led through line 19 to line 9 where it meets more halide coming from condenser 8 and together with re-circulated excess methane from line 20 is led into halogenating reactor 21 where they react at the proper temperatures to form methyl halide and hydro-halide acid. Reactor 21 works continuously while reactor 5, 5A, 5B and 5C operate batch wise. Reacted gasses from reactor 21 are led trough line 22 to cooler 23A. Cooled gasses are led through line 24 to a series of reactors 5, (5A, 5B, and 5C not shown) one of which is in the metal basic form. Assuming reactor 5 is in the metal basic form the following procedure follows: Gasses containing methyl halide, hydro-halide acid and excess methane coming from line 24 are led through line 23 and opened valve 26 to reactor 5, valve 6 being closed. Upward moving gasses through reactor 5 react with metal basic form to form ethylene, propylene etc., which together with excess methane are led through opened valve 27 and line 28 to separator 29, where products are separated and delivered through product line 30. Excess methane is led from separator 29 to line 14, again to re-circulate in the system. Separator 29 can include compression, distillation, diffusion process equipment, as known in the art. Other standard equipment, well known in the art such as sampling ports, are not shown.
For continuous operation, besides the halogenation reactor there may preferably be four reactors containing the inventive encapsulated metal halide/metal halide hydroxide catalyst. In a first reactor the metal may be oxidized. These gasses in the second are being displaced with steam and cooled to the temperature of the ethylene reaction. The third reactor is treating the gasses to form alkenes and the forth reactor is being treated with steam to sweep out remaining gasses and also being heated to the oxidation temperature. Steam is also used to displace remaining gasses in the reactors to prevent possible explosions or contaminations.
If the encapsulated pellets are made spherical and prove strong enough they can be moved around in a system as shown in FIG. 2.
Referring to FIG. 2, methane is fed through line 4 to striper 5, striping halide from halide solution coming down from striper 6 through line 7. Methane with halide vapor from striper is led to saturation vessel 9 through line 8 where the balance of the required halide is added through line 10. The resulting mixture of methane and halide is fed through line 11 to reactor 1 where methyl halide and through line 8 where the balance of the required halide is added through line 10. The resulting mixture of methane and halide is fed through line 11 to reactor 1 where methyl halide and hydro-halide acid are produced. The methyl halide and hydro-halide acid are led through line 12 from reactor 1 to bottom of reactor 2 where they meet in countercurrent the magnesium base reacting to form a product gas containing methanol, di-methyl ether and ethylene which are exhausted from reactor 2 through line 13. Metal halide formed in reactor 2 is led by gravity to lower reactor 3 through line 14 where it meets a counter flow of oxygen or air forming halide which together with excess oxygen or air are led through line 15 to cooler 16 where the halide condensed is led through line 10 to saturation vessel 9.
Line 17 leads excess oxygen or air to striper 6 where it meets a countercurrent flow of solvent which strips halide from gasses which leaves striper 6 through line 18 to exhaust to the atmosphere. Solvent loaded with halide flows downwardly through line 7 to striper 5. Spent solvent is led through line 19 to pump 20 which pumps solvent to striper 6 through line 21. Oxygen or air is fed into reactor 3 through line 22. Magnesium base produced in reactor 3 is led to ejector 23 through line 24 which is fed with air through line 25 and conveys the magnesium base through line 26 to cyclone 27 which empties the basic magnesium through line 28 to reactor 2 and exhausts air to the atmosphere through line 28. Steam through line 29 into line 14 prevents gasses from reactor 2 to pass into reactor 3. Steam through line 30 prevents gasses from cyclone 27 to pass into reactor 2.
EXAMPLE 1
Highly porous encapsulated magnesium oxide catalyst of one embodiment of the invention can be made as follows 50 parts by weight of fine powder magnesium stearate Mg(C18H35O2)2 are well mixed with 50 parts by weight of fine powder bentonite and enough water added to form a doughy mixture which is then kneaded until smooth. The mixture is then pelletized and air dried at typical room temperatures. Once dried the pellets are calcined at to a minimum temperature of 600 degrees C. to form highly porous magnesium oxide, encapsulated in a ceramic clay matrix.
Highly porous encapsulated magnesium oxide can be made as follows 50 parts by weight of fine powder magnesium citrate, Mg(C6H5O7)2—14H2O, are well mixed with 50 parts by weight of fine powder kaolin, 1 part by weight of ground X-type zeolite in the acid form and 50 parts by weight of water added to form a dough which is then kneaded till smooth and then pelletized and dried. Once dried the pellets are calcined to at least about 600° C. to form the magnesium oxide encapsulated in a matrix of hard clay or porcelain. The proportions of magnesium citrate to clay can vary. The higher the proportion of clay, the harder the pellet but the lower the capacity for halide or alcohol production, and thus, for alkene production. The pellets can be made spherical or in any other shape, by hand or machine, known in the art. Other types of clays and inorganic porous agglutinates, as are known in the art, may be used as the encapsulating material in embodiments of the invention.

## Claims

1. A process to produce one or more compounds comprising:
halogenating one or more alkanes with one or more halogens to form one or more alkane halides and one or more hydrogen halide acids; and
reacting the alkane halides and hydrogen halide acid with one or more encapsulated metal oxide catalysts to form one or more compounds selected from the group of alkyl alcohols, ethers and alkenes and one or more metal halide;
wherein the one or more encapsulated metal oxide catalysts comprises a pelletized and calcined mixture of clay and an organic metal salt.

2. The process of claim 1 wherein the organic metal salt is selected from magnesium citrate and magnesium stearate.

3. The process of claim 1 wherein the clay is selected from bentonite, bauxite, and kaolin.

4. The process of claim 1 wherein the clay is bentonite and wherein the reacting the alkane halide and hydrogen halide acid with one or more encapsulated metal oxide catalysts forms one or more alcohols and further wherein encapsulating material is bentonite and the one or more alcohols are converted to one or more alkenes by conversion catalyzed by the bentonite.