# Patent

## Title
Color capsule composition for cosmetics, preparation method thereof and cosmetic formulation comprising the same

## Abstract

Disclosed herein are a color capsule composition, which contains a polymer and a plasticizer swelling the polymer so as to allow the capsule particles to easily break and in which the capsule particles have a porous structure that boosts the effects thereof, and a method for preparing the color capsule composition. The preparation method comprises: uniformly mixing a color pigment, a plasticizer and a polymer in a first solvent to produce a first mixture solution; spray-drying the first mixture solution to produce core particles in which the color pigment is covered by the polymer; uniformly mixing the obtained core particles, a functional pigment and a second solvent to produce a second mixture solution; and spray-drying the second mixture solution to produce in which a coating layer of the functional pigment is formed on the outer surface of the polymer.

## Background
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a color capsule composition, which contains a polymer and a plasticizer swelling the polymer so as to allow the capsule particles to easily break and in which the capsule particles have a porous structure that boosts the effects thereof, and a method for preparing the color capsule composition.
2. Description of the Prior Art
In conventional methods for preparing color cosmetic particles, coacervation, phase separation or modified encapsulation methods are used to form a structure, which resists swelling or some degree of external force and easily breaks under a certain formulation.
In these methods, the process steps are very complicated and it is difficult to control the particle size. In addition, due to the process characteristics, it is not easy to control the skin covering power of capsules.
Also, in most of these methods, granulation or encapsulation is performed using a wet process, and washing and filtration processes are repeated several times to remove the remaining organic solvent or impurities, thus generating a large amount of wastewater.
Accordingly, a large amount of wastewater is necessarily generated, resulting in an increase in the production cost.
SUMMARY OF THE INVENTION
Accordingly, the present invention has been made in view of the problems occurring in the prior art, and it is an object of the present invention to provide a color capsule composition, which contains a polymer and a plasticizer swelling the polymer so as to allow the capsule particles to easily break and in which the capsule particles have a porous structure that boosts the effects thereof, and a method for preparing the color capsule composition.
Another object of the present invention is to provide a color capsule composition for cosmetics having a core-shell structure and exhibiting skin covering power, which is prepared by preparing core particles made of a polymer surrounding a color pigment, and coating the core particles with a functional pigment having increased covering power, and a method for preparing the color capsule composition.
Still another object of the present invention is to provide a method for preparing a color capsule composition for cosmetics, in which a spray dryer is used to produce micro-size core particles or capsule particles such that the generation of wastewater and the discharge of a volatile solvent can be prevented, and a color capsule composition prepared thereby.
Still another aspect of the present invention is to provide a method for preparing a color capsule composition for cosmetics, in which no surfactant is used such that the physical properties of the final product can be easily controlled and the number of additional process steps can be reduced, and a color capsule composition prepared thereby.
Still another aspect of the present invention is to provide an W/O emulsion formulation, an W/S emulsion formulation and an O/W emulsion formulation using the color pigment-containing capsules.
To achieve the above objects, the present invention provides a color capsule composition for cosmetics prepared by uniformly mixing a color pigment, a plasticizer and a polymer in a first solvent to make a mixture, drying the mixture to make core particles, and uniformly mixing the core particles, a functional pigment and a second solvent.
Preferably, the polymer, the color pigment and the plasticizer are used in amounts of 5-15 wt %, 70-90 wt % and 5-15 wt %, respectively, based on the total weight of the polymer, the color pigment and the plasticizer, and the core particles and the functional pigment are used in amounts of 80-40 wt % and 20-60 wt %, respectively, based on the total weight of the core particles and the functional pigment.
The present invention also provides a method for preparing a color capsule composition for cosmetics, the method comprising the steps of: uniformly mixing a color pigment, a plasticizer and a polymer in a first solvent to produce a first mixture solution; spray-drying the first mixture solution to produce core particles in which the color pigment is covered by the polymer; uniformly mixing the obtained core particles, a functional pigment and a second solvent to produce a second mixture solution; and spray-drying the second mixture solution to produce in which a coating layer of the functional pigment is formed on the outer surface of the polymer.
Preferably, fatty acid is further added to the first mixture solution.
Preferably, the polymer is any one selected from the group consisting of polyester, a polyester emulsion, polyaminomethacrylate, polyvinylpyrrolidone, hydroxypropylmethylcellulose, and shellac.
Preferably, the plasticizer is any one selected from the group consisting of 1,3-butanediol, polyethylene glycol, and dipropylene glycol.
Preferably, the color pigment is any one selected from the group consisting of iron oxide pigments, organic pigments, lake dyes, and natural pigments.
Preferably, the first and second solvents are any one selected from the group consisting of acetone, ethanol and distilled water.
Preferably, the functional pigment is any one selected from the group consisting of titanium dioxide, zinc oxide, boron nitride, talc, mica, and a mixture of two or more thereof.
Preferably, in the step of producing the first mixture solution, 4.5 g of the polymer, 39.15 g of the color pigment and 2.25 g of the plasticizer are used, and in the step of producing the second mixture solution, 45 g of the core particles and 55 g of the functional pigment are used.



BRIEF DESCRIPTION OF THE DRAWINGS
The above and other objects, features and advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawing, in which:
FIG. 1 shows photographs of core particles prepared in Examples 1, 6 and 11;
FIG. 2 shows photographs of capsule powders prepared in Examples 1, 6 and 11;
FIGS. 3 and 4 are graphic diagrams showing the brittleness of core powders of Examples 31 to 57;
FIG. 5 is a graphic diagram showing the brittleness of core powders of Examples 58 to 63 according to a change in the amount of fatty acid;
FIGS. 6 and 7 are graphic diagrams showing the brittleness of core powders of Examples 64 to 90;
FIGS. 8 and 9 are graphic diagrams showing the brittleness of core powders of Examples 91 to 117;
FIGS. 10 and 11 are graphic diagrams showing the brittleness of core powders of Examples 118 to 144;
FIGS. 12 and 13 are graphic diagrams showing the brittleness of core powders of Examples 145 to 171;
FIGS. 14 and 15 are graphic diagrams showing the brittleness of core powders of Examples 172 to 198; and
FIG. 16 is a graphic diagram showing the change in covering power according to the content of an inorganic coating layer in capsule particles of Examples 226 to 242.



DETAILED DESCRIPTION OF THE INVENTION
A color capsule composition for cosmetics according to the present invention is produced by uniformly mixing a color pigment, a plasticizer and a polymer in a first solvent, drying the mixture to produce core particles, uniformly mixing the core particles, a functional pigment and a second solvent, and drying the resulting mixture.
Also, a method for preparing the color capsule composition for cosmetics according to the present invention comprises the steps of: uniformly mixing a polymer, a plasticizer and a color pigment in a first solvent to produce a first mixture solution; spray-drying the first mixture solution to produce core particles in which the color pigment is coated with the polymer; uniformly mixing the prepared core particles, a functional pigment and a second solvent to produce a second mixture solution; and spray drying the second mixture solution to produce capsule particles in which a coating layer of the functional pigment is formed on the outer surface of the polymer.
The polymer serves to coat the color pigment so as to prevent the color pigment from being dispersed, and it is used in an amount of 5-15 wt % based on the weight of the mixture of the polymer, the plasticizer and color pigment. If the polymer is used in an amount of less than 5 wt %, it will not sufficiently cover the color pigment, and if it is used in an amount of more than 15 wt %, the viscosity of the first mixture solution will rapidly increase, thus making it difficult to control the size or sphericity of the core particles. Examples of the polymer that is used in the present invention include polyester, a polyester emulsion, polyaminomethacylate, polyvinylpyrrolidone, hydroxypropylmethylcellulose, shellac, and the like.
The plasticizer serves to swell the polymer and is used in an amount of 5-15 wt % based on the weight of the mixture of the polymer, the plasticizer and the color pigment. If the plasticizer is used in an amount of less than 5 wt %, the polymer will be weakly swollen, and thus the hardness of the particle will undesirably increase, and if it is used in an amount of more than 15 wt %, the polymer will be strongly swollen, and thus the hardness of the particle hardness will excessively decrease such that the particles will be easy to break. Examples of the plasticizer that is used in the present invention include 1,3-butanediol, polyethylene glycol, dipropylene glycol and the like.
The color pigment is used to give the color of cosmetic, and examples thereof include iron oxide pigments, organic pigments, lake dyes, natural pigments, etc. The color pigment is used in an amount of 70-90 wt % based on the weight of the mixture of the polymer, the plasticizer and the color pigment. If the color pigment is used in an amount of less than 70 wt %, the saturation of the final color will decrease, and if it is used in an amount of more than 90 wt %, the contents of the polymer and the plasticizer will relatively decrease, thus making it difficult to control the particle hardness.
The functional pigment serves to increase the covering power and feeling of the capsule particles prepared and to impart gloss to the capsule particles. It is mixed with the core particle at a ratio of 20-60 wt % (functional pigment):80-40 wt % (core particle). If the functional pigment is used in an amount of more than 60 wt %, the expression of the color of the color pigment in the core particle will be decrease, and if it is used in an amount of less than 40 wt %, the covering power and feeling of the capsule particles will decrease. As this functional pigment, titanium dioxide, zinc oxide or the like is used to improve the covering power of the core particles, boron nitride is used to increase the gloss and feeling of the core particles, and talc or mica is used to increase the feeling of the core particles. Such functional pigments may be used alone or in combination.
Meanwhile, to increase the brittleness of the core particle, fatty acid is preferably further added when preparing the first mixture solution. Examples of the fatty acid that is used in the present invention include stearic acid, palmitic acid, oleic acid, linoleic acid, linolenic acid, etc. The fatty acid is used in an amount of 2-5 wt % based on the weight of the mixture of the polymer, the plasticizer, the color pigment and the fatty acid.
In the method of preparing the color capsule composition for cosmetics, the step of preparing the first mixture solution comprises the sub-steps of: uniformly dissolving the polymer and the plasticizer in the first solvent to form a first solution; dissolving the color pigment in the first solvent to form a second solution; and mixing the first solution with the second solution and uniformly dispersing the mixture to form a third solution. It is preferable to separately prepare the solution of the polymer and the plasticizer and the solution of the color pigment, and then to mix these solutions, but the polymer, the plasticizer and the color pigment may also be mixed with each other at one time. Even when the fatty acid is further added when preparing the first mixture solution, the fatty acid may be uniformly dissolved in the first solvent, and then mixed with the first and second solutions to prepare the third solution. Alternatively, the polymer, the plasticizer, the color pigment and the fatty acid may also be mixed with each other at one time.
Also, in the step of producing the core particles, the spray-dried core particles may be sieved to desired sizes. Preferably, if only core particles having an outer diameter of 150 μm or less are screened by sieving and used, the size of the capsule particles can be controlled. The core particles prepared as described above have a porous structure that boosts the effects thereof.
In the method of preparing the color capsule composition for cosmetics according to the present invention, the step of producing the second mixture solution comprises: stirring the functional pigment in the second solvent to produce a fourth solution; dispersing the core powder, produced in step 1, in the second solvent to produce a fifth solution, mixing the fourth solution and the fifth solution, and uniformly dispersing the mixed solution to produce a sixth solution.
Herein, it is preferable to separately prepare the solution of the functional pigment and the solution of the core particles, and then to mix these solutions before use. However, the functional pigment and the core particles may also be mixed with each other at one time and used.
In the step of producing the capsule particles, the spray-dried capsule particles may be sieved to desired sizes. Preferably, if only capsule particles having an outer diameter of 150 μm or less are screened, the covering power of these particles in cosmetic formulations can be enhanced.
In the capsule particles prepared as described above, the functional pigment that forms the coating layer on the core particles can improve the color, covering power and feeling of the capsule particles.
Hereinafter, the present invention will be described in detail with reference to examples.
EXAMPLES 1 TO 30
Example 1
In 43 ml of acetone in an organic solvent, 4.5 g of a polyester polymer and 2.25 g of 1,3-butanediol as a plasticizer were dissolved by stirring at 25° C. for 15 minutes to prepare a solution. Meanwhile, 39.15 g of yellow iron oxide as an inorganic pigment was dispersed in 90 ml of acetone at 25° C. for 15 minutes to prepare a dispersion. The above solution was mixed with and uniformly dispersed in the above dispersion at the same temperature for 30 minutes. Then, the solution was fed into an atomizer (rotating at a high speed of 10,000 rpm) at a constant rate of 100 ml/min using a metering pump. Herein, the solution was fed into the atomizer at 80° C. and dried therein at 60° C. to obtain first cote powder. The obtained core powder was screened through a sieve having a mesh size of 150 μm, thus obtaining core powder having an outer diameter of 150 μm or less.
Meanwhile, 5 g of boron nitride and 50 of titanium dioxide were stirred in 100 ml of distilled water at 25° C. for 10 minutes to obtain an inorganic suspension. Then, 45 g of the obtained core powder was dispersed by stirring in a mixed solution of 207 ml and 23 ml of ethanol at 25° C. for 10 minutes. The above two solutions were mixed with stirring at 25° C. for 10 minutes, and the mixed solution was fed into an atomizer (rotating at a high speed of 10,000 rpm) at a constant rate of 120 ml/min using a metering pump. Herein, the mixed solution was fed into the atomizer at 160° C. and dried therein at 80° C., thus obtaining second capsule powder. The obtained capsule powder was screened through a sieve having a mesh size of 150 μm, thus obtaining second capsule powder having an outer diameter of 150 μm or less.
Example 2
Uniform particles were obtained in the same manner as Example 1, except that the plasticizer was used in an amount of 3.60 parts by weight.
Example 3
Uniform particles were obtained in the same manner as Example 1, except that the plasticizer was used in an amount of 4.50 parts by weight.
Example 4
Uniform particles were obtained in the same manner as Example 1, except that the plasticizer was used in an amount of 6.70 parts by weight.
Example 5
Uniform particles were obtained in the same manner as Example 1, except that the plasticizer was used in an amount of 9.00 parts by weight.
Example 6
Uniform particles were obtained in the same manner as Example 1, except that red iron oxide was used as the inorganic pigment.
Example 7
Uniform particles were obtained in the same manner as Example 6, except that the plasticizer was used in an amount of 3.60 parts by weight.
Example 8
Uniform particles were obtained in the same manner as Example 6, except that the plasticizer was used in an amount of 4.50 parts by weight.
Example 9
Uniform particles were obtained in the same manner as Example 6, except that the plasticizer was used in an amount of 6.70 parts by weight.
Example 9
Uniform particles were obtained in the same manner as Example 6, except that the plasticizer was used in an amount of 9.00 parts by weight.
Example 11
Uniform particles were obtained in the same manner as Example 1, except that black iron oxide was used as the inorganic pigment.
Example 12
Uniform particles were obtained in the same manner as Example 11, except that the plasticizer was used in an amount of 3.60 parts by weight.
Example 13
Uniform particles were obtained in the same manner as Example 11, except that the plasticizer was used in an amount of 4.50 parts by weight.
Example 14
Uniform particles were obtained in the same manner as Example 11, except that the plasticizer was used in an amount of 6.70 parts by weight.
Example 15
Uniform particles were obtained in the same manner as Example 11, except that the plasticizer was used in an amount of 9.00 parts by weight.
Measurement of Brittleness of Particles
The brittleness of each of the capsule powders prepared in Examples 1 to 15 was measured by applying a constant load of 5 gf/cm2 to 0.3 g of the capsule powder while moving the capsule powder in the up, down, left and right directions at a constant speed of 0.01 m/sec for 30 seconds. The capsule powder was observed with an optical microscope, and the number of broken particles per 1 mm×1 mm pixel was measured three times. The measurements were averaged and the results are shown in Table 1 below. In Table 1, the smaller the number of normal particles, the better the brittleness.













TABLE 1










Yellow
Boron
Titanium
Brittleness of capsule particles



Polymer
Plasticizer
pigment
nitride
dioxide
(number of normal particles)





Example 1
4.5
2.25
38.25
5
50
14-18


Example 2
4.5
3.60
38.25
5
50
 9-14


Example 3
4.5
4.50
38.25
5
50
5-9


Example 4
4.5
6.75
38.25
5
50
2-5


Example 5
4.5
9.00
38.25
5
50
0-2








Red
Boron
Titanium
Brittleness of capsule panicles



Polymer
Plasticizer
pigment
nitride
dioxide
(number of normal particles)





Example 6
4.5
2.25
38.25
5
50
15-20


Example 7
4.5
3.60
38.25
5
50
10-15


Example 8
4.5
4.50
38.25
5
50
 6-10


Example 9
4.5
6.75
38.25
5
50
3-6


Example 10
4.5
9.00
38.25
5
50
0-3








Black
Boron
Titanium
Brittleness of capsule panicles



Polymer
Plasticizer
pigment
nitride
dioxide
(number of normal particles)





Example 11
4.5
2.25
38.25
5
50
15-20


Example 12
4.5
3.60
38.25
5
50
10-15


Example 13
4.5
4.50
38.25
5
50
 6-10


Example 14
4.5
6.75
38.25
5
50
3-6


Example 14
4.5
9.00
38.25
5
50
0-3









As can be seen in Table 1 above, as the amount of the plasticizer decreased, the brittleness of the capsule particles decreased. It can be seen that, if this brittleness is low, when W/O emulsion type cosmetic, W/S emulsion type cosmetic and O/W emulsion type cosmetic products which contain the capsule particles are used, the polymer can be easily applied to the skin. Also, it can be seen that the non-smooth feeling caused by the non-brittle particles on the skin can be reduced.
Measurement of Color Coordinates of Particles
FIG. 1 shows core particles prepared in Examples 1, 6 and 11, and FIG. 2 shows photographs of capsule powders. Also, the covering capacity obtained by the color coordinates of the capsule particles prepared in Examples 1, 6 and 11 is shown in Table 2 below. Herein, the term “covering capacity” refers to the capacity to change one value of coordinates (L, a and b), the term “increase in covering capacity” means that, in the case of the capsule particles containing the yellow pigment, the change Δb* between the color coordinates (L, a and b) of the core and the color coordinates of the capsule is greater than zero, and in the case of the capsule particles containing the red pigment, the change Δa* between the color coordinates (L, a and b) of the core and the color coordinates (L, a and b) of the capsule is greater than zero, and also in the case of the capsule particles containing the black pigment, the change ΔL* between the color coordinates (L, a and b) of the core and the color coordinates (L, a, and b) of the capsule is greater than zero. Namely, “ΔL*”, “Δa*” and “Δb*” mean ΔL*=[Lcapsule−Lcore], Δa*=[acore−acapsule], and Δb*=[bcore−bcapsule], respectively. Meanwhile, “a*” is the saturation for red, and a higher a* value indicates a deeper red. “b*” is the saturation for yellow, and a higher b* value indicates a deeper yellow. In addition, and a higher L* value indicates a lighter color.







TABLE 2







Change in color coordinates according to the kind of particles














Core
Capsule


Kind


particles
particles
















Yellow






pigment particles




Color
L*
75.512
59.477
81.608


coordinates
a*
13.400
11.472
4.827



b*
49.854
41.263
11.129



Δa*
30.134






Red






pigment particles





L*
40.706
28.716
68.823



a*
30.153
19.266
10.595



b*
29.945
17.906
7.626



Δa*
 8.671






Black






pigment particles





L*
16.552
14.094
65.366



a*
−2.077
−2.435
−3.014



b*
−1.079
−0.950
−4.618



Δa*
51.272









As can be seen in FIGS. 1 and 2 and Table 2 above, even when the yellow pigment, the red pigment and the black pigment were used, ΔL* generally increased, and thus the covering power of the capsule particles increased compared to the covering power of the core particles. In the case of the capsule particles containing the red pigment, the saturation Δa* for red generally decreased, and in the case of the capsule particles containing the yellow pigment, the saturation Δb* for yellow generally decreased. This suggests that the covering power of the capsule particles was higher than that of the core particles.
Measurement of Color Expression of Capsule Particles
Examples 16 to 20
Uniform particles were obtained in the same manner as Example 1 using constant amounts of the polymer, the plasticizer and boron nitrogen while changing the amounts of yellow pigment and titanium dioxide added, as shown in Table 3 below. The capsule particles were subjected to color analysis (ΔE*), and the results of the analysis are shown in Table 3 below.
Examples 21 to 25
Uniform particles were obtained in the same manner as Example 1 using constant amounts of the polymer, the plasticizer and boron nitrogen while changing the amounts of red pigment and titanium dioxide added, as shown in Table 3 below. The capsule particles were subjected to color analysis (ΔE*), and the results of the analysis are shown in Table 3 below.
Examples 26 to 30
Uniform particles were obtained in the same manner as Example 1 using constant amounts of the polymer, the plasticizer and boron nitrogen while changing the amounts of yellow pigment and titanium dioxide added, as shown in Table 3 below. The capsule particles were subjected to color analysis (ΔE*), and the results of the analysis are shown in Table 3 below.













TABLE 3










Yellow
Boron
Titanium




Polymer
Plasticizer
pigment
nitride
dioxide
ΔE*





Example 16
4.5
3.60
28
5
58.9
30.32


Example 17
4.5
3.60
39
5
47.9
25.05


Example 18
4.5
3.60
50
5
36.9
19.48


Example 19
4.5
3.60
61
5
25.9
13.51


Example 20
4.5
3.60
72
5
14.9
 9.45








Red
Boron
Titanium



Polymer
Plasticizer
pigment
nitride
dioxide
ΔE*





Example 21
4.5
3.60
28
5
58.9
48.78


Example 22
4.5
3.60
39
5
47.9
41.23


Example 23
4.5
3.60
50
5
36.9
33.04


Example 24
4.5
3.60
61
5
25.9
20.78


Example 25
4.5
3.60
72
5
14.9
10.35








Black
Boron
Titanium



Polymer
Plasticizer
pigment
nitride
dioxide
ΔE*





Example 26
4.5
3.60
28
5
58.9
45.43


Example 27
4.5
3.60
39
5
47.9
38.75


Example 28
4.5
3.60
50
5
36.9
27.42


Example 29
4.5
3.60
61
5
25.9
17.49


Example 30
4.5
3.60
72
5
14.9
 7.58









1 g of each of the capsule powders prepared in Examples 16 to 30 was applied to a gauze of 5 cm×5 cm by repeatedly moving the capsule powders in the up, down, left and right directions at a constant speed of 0.01 m/sec for 30 seconds while applying a load of 10 gf/cm2 so as to be broken. The expressed color of the capsule powders was measured three times using the L*a*b* color system, and the measurements were averaged. Also, the color coordinates of the capsule particles before application were measured. Based on the measured values, the ΔE* value of the capsule particles was calculated, and the results of the calculation are shown in Table 3 above.
Herein, ΔE* means the change between the color coordinates (L1, a1 and b1) of the capsule particles and the color coordinates (L2, a2 and b2) of the broken capsule particles applied to the gauze. Namely, ΔE*=√{square root over ((L2−L1)+(a2−a1)+(b2−b1))}{square root over ((L2−L1)+(a2−a1)+(b2−b1))}{square root over ((L2−L1)+(a2−a1)+(b2−b1))}.
As can be seen in Table 3 above, the yellow capsules containing the yellow pigment had a color value of 9.45≦ΔE≧30.52, the red capsules containing the red pigment had a color value of 10.35≦ΔE≧48.78, and the black capsules containing the black pigment had a color value of 7.58≦ΔE≧45.43.
Examples 31 to 225
Preparation of Core Powders Having Color
Example 31
Preparation of Core Powder Consisting of Polymer-Plasticizer-Iron Oxide Pigment
The preparation of core particles, which is the first step of the process for preparing the core particles having a color, was performed in the following manner.
Inner cores containing an iron oxide pigment (yellow iron oxide, black iron oxide, red iron oxide, or a mixture of two or more thereof) were prepared in the following manner. In 43 ml of acetone, 3.6 g of a polyester polymer and 2.25 g of 1,3-butanediol were dissolved by stirring at 25° C. for 15 minutes to prepare a solution. Meanwhile, 39.15 g of an iron oxide pigment was dispersed in 90 ml of acetone at 25° C. for 15 minutes to prepare a dispersion. The above solution was mixed with and uniformly dispersed in the above dispersion for 30 minutes at the same temperature.
Then, the resulting solution was fed into an atomizer (rotating at a high speed of 10,000 rpm) at a rate of 100 ml/min using a metering pump. Herein, the solution was fed into the atomizer at 80° C. and dried therein at 60° C. to obtain core powder. Herein, the obtained core powder had an outer diameter ranging from 10 μm to 150 μm.
Examples 32 to 57
Preparation of Core Powders Using Varying Kinds and Contents of Plasticizer
Core powders were prepared in the same manner as Example 31. The specific kinds and contents of compounds used herein are shown in Table 4 below. The brittleness of the core powders according to changes in the amount of the plasticizer and the amount of the polyester polymer was measured, and the results of the measurement are shown in FIGS. 3 and 4.









TABLE 4









Step 1











Polymer
Plasticizer
Pigment

















Example 31
Polyester
3.60
1,3-butanediol
2.25
Iron oxide pigment
39.15


Example 32
Polyester
3.60
1,3-butanediol
3.15
Iron oxide pigment
38.25


Example 33
Polyester
4.50
1,3-butanediol
2.25
Iron oxide pigment
38.25


Example 34
Polyester
4.50
1,3-butanediol
3.15
Iron oxide pigment
37.35


Example 35
Polyester
4.50
1,3-butanediol
4.50
Iron oxide pigment
36.00


Example 36
Polyester
6.75
1,3-butanediol
2.25
Iron oxide pigment
36.00


Example 37
Polyester
6.75
1,3-butanediol
3.15
Iron oxide pigment
35.10


Example 38
Polyester
6.75
1,3-butanediol
4.50
Iron oxide pigment
33.75


Example 39
Polyester
6.75
1,3-butanediol
6.75
Iron oxide pigment
31.50


Example 40
Polyester
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 41
Polyester
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 42
Polyester
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38.25


Example 43
Polyester
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 44
Polyester
4.50
Polyethylene glycol
4.30
Iron oxide pigment
36.00


Example 45
Polyester
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 46
Polyester
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 47
Polyester
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 48
Polyester
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 49
Polyester
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 50
Polyester
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.35


Example 51
Polyester
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38.25


Example 52
Polyester
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 53
Polyester
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 54
Polyester
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 55
Polyester
6.75
Dipropylene glycol
3.15
Iron oxide pigment
35.10


Example 56
Polyester
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 57
Polyester
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31.50









As can be seen from the graphs of FIGS. 3 and 4, with respect to brittleness according to the kind of plasticizer, 1,3-butanediol or dipropylene glycol having a relatively low molecular weight showed improved brittleness compared to polyethylene glycol having a relatively high molecular weight. Also, dipropylene glycol or polyethylene glycol having a high volatilization temperature had a relatively excellent brittleness. Also, it can be seen that, as the amount of the plasticizer increased, the brittleness of the capsule particles increased (the number of normal particles decreased), and as the amount of the polymer increased, the brittleness of the capsule particles decreased (the number of normal particles increased). It can be seen that the dipropylene glycol plasticizer satisfying such two conditions is preferable. In addition, it can be seen that, as the amount of the plasticizer increased, the brittleness of the core powders increased (the number of normal particles decreased), and as the amount of the polymer increased, the brittleness of the core particles decreased (the number of normal particles increased).
Examples 58 to 63
Preparation of Core Powders Using Varying Amounts of Polyester Polymer and Plasticizer with Addition of Fatty Acid
Core powders were prepared in same manner as Example 31, except that a mixture of polyethylene glycol and dipropylene glycol was used as the plasticizer and that stearic acid as fatty acid was also added during the dissolution process. The specific kinds and contents of compounds used herein are shown in Table 5 below. The brittleness of core powders according to changes in the amount of fatty acid was measured, and the results of the measurement are shown in FIG. 5.









TABLE 5









Sep 1












Polymer
Plasticizer
Fatty acid
Pigment





















Example 58
Polyester
4.50
Polyethylene glycol
1.00
Dipropylene glycol
2.15
Stearic acid
2.00
Iron oxide pigment
35.35


Example 59
Polyester
4.50
Polyethylene glycol
2.00
Dipropylene glycol
2.50
Stearic acid
2.00
Iron oxide pigment
34.00


Example 60
Polyester
4.50
Polyethylene glycol
1.00
Dipropylene glycol
2.15
Stearic acid
1.50
Iron oxide pigment
35.85


Example 61
Polyester
4.50
Polyethylene glycol
2.00
Dipropylene glycol
2.50
Stearic acid
1.50
Iron oxide pigment
34.50


Example 62
Polyester
4.50
Polyethylene glycol
1.00
Dipropylene glycol
2.15
Stearic acid
1.00
Iron oxide pigment
36.35


Example 63
Polyester
4.50
Polyethylene glycol
2.00
Dipropylene glycol
2.50
Stearic acid
1.00
Iron oxide pigment
35.00









As can be seen from the graph of FIG. 5, when the fatty acid was added as the plasticizer, the brittleness of the core particles rapidly increased (the number of normal particles decreased).
Examples 64 to 90
Preparation of Core Powders Using Varying Kinds and Contents of Polyacrylate Polymer and Plasticizer
Core powders were prepared in the same manner as Example 31, except that ethanol was used in place of the acetone solvent, used in step 1 of the preparation process of Example 31, to disperse or dissolve the polymer and the iron oxide pigment. The specific kinds and contents of compounds used herein are shown in Table 6 below. The brittleness of the core particles according to changes in the amounts of plasticizer and polyaminomethacrylate polymer used was measured, and the results of the measurement are shown in FIGS. 6 and 7.









TABLE 6









Step 1











Polymer
Plasticizer
Pigment

















Example 64
Polyaminomethacrylate
3.60
1,3-butanediol
2.25
Iron oxide pigment
39.15


Example 65
Polyaminomethacrylate
3.60
1,3-butanediol
3.15
Iron oxide pigment
38.25


Example 66
Polyaminomethacrylate
4.50
1,3-butanediol
2.25
Iron oxide pigment
38.25


Example 67
Polyaminomethacrylate
4.50
1,3-butanediol
3.15
Iron oxide pigment
37.35


Example 68
Polyaminomethacrylate
4.50
1,3-butanediol
4.50
Iron oxide pigment
36.00


Example 69
Polyaminomethacrylate
6.75
1,3-butanediol
2.25
Iron oxide pigment
36.00


Example 70
Polyaminomethacrylate
6.75
1,3-butanediol
3.15
Iron oxide pigment
35.10


Example 71
Polyaminomethacrylate
6.75
1,3-butanediol
4.50
Iron oxide pigment
33.75


Example 72
Polyaminomethacrylate
6.75
1,3-butanediol
6.75
Iron oxide pigment
31.50


Example 73
Polyaminomethacrylate
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 74
Polyaminomethacrylate
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 75
Polyaminomethacrylate
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38.25


Example 76
Polyaminomethacrylate
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 77
Polyaminomethacrylate
4.50
Polyethylene glycol
4.50
Iron oxide pigment
36.00


Example 78
Polyaminomethacrylate
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 79
Polyaminomethacrylate
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 80
Polyaminomethacrylate
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 81
Polyaminomethacrylate
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 82
Polyaminomethacrylate
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 83
Polyaminomethacrylate
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.25


Example 84
Polyaminomethacrylate
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38.25


Example 85
Polyaminomethacrylate
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 86
Polyaminomethacrylate
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 87
Polyaminomethacrylate
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 88
Polyaminomethacrylate
6.75
Dipropylene glycol
3.15
Iron oxide pigment
35.10


Example 89
Polyaminomethacrylate
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 90
Polyaminomethacrylate
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31.50









As can be seen from the graphs of FIGS. 6 and 7, like the case of Examples 31 to 57, the use of dipropylene glycol as the plasticizer showed the most excellent brittleness (the number of normal particles decreased), even when polyaminomethacrylate was used as the polymer. Also, it can be seen that, as the amount of the polymer increased, the brittleness of the capsule particles decreased (the number of normal particles increased).
Examples 91 to 171
Preparation of Core Powders from Water-Dispersible or Water-Soluble Polymer Using Varying Kinds and Contents of Plasticizer
Core powders were prepared in the same manner as Example 31, except that distilled water was used in place of the acetone solvent, used in step 1 of the preparation process of Example 31, to disperse or dissolve the polymer and the iron oxide pigment. The specific kinds and contents of compounds used herein are shown in Table 7 below. The brittleness of the core powders of Examples 91 to 117 according to changes in the amounts of plasticizer and polyester polymer used was measured, and the results of the measurement are shown in FIGS. 8 and 9. Also, the brittleness of the core powders of Examples 118 to 144 according to changes in the amounts of plasticizer and polyvinylpyrrolidone used was measured, and the results of the measurement are shown in FIGS. 10 and 11. In addition, the brittleness of the core powders of Examples 145 to 171 according to changes in the amounts of plasticizer and hydroxypropylmethylcellulose used was measured, and the results of the measurement are shown in FIGS. 12 and 13.









TABLE 7









Step 1











Polymer
Plasticizer
Pigment

















Example 91
Polyester emulsion
3.60
1,3-butanediol
2.25
Iron oxide pigment
39.15


Example 92
Polyester emulsion
3.60
1,3-butanediol
3.15
Iron oxide pigment
38.25


Example 93
Polyester emulsion
4.50
1,3-butanediol
2.25
Iron oxide pigment
38.25


Example 94
Polyester emulsion
4.50
1,3-butanediol
3.15
Iron oxide pigment
37.35


Example 95
Polyester emulsion
4.50
1,3-butanediol
4.50
Iron oxide pigment
36.00


Example 96
Polyester emulsion
6.75
1,3-butanediol
2.25
Iron oxide pigment
36.00


Example 97
Polyester emulsion
6.75
1,3-butanediol
3.15
Iron oxide pigment
35.10


Example 98
Polyester emulsion
6.75
1,3-butanediol
4.50
Iron oxide pigment
33.75


Example 99
Polyester emulsion
6.75
1,3-butanediol
6.75
Iron oxide pigment
31.50


Example 100
Polyester emulsion
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 101
Polyester emulsion
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 102
Polyester emulsion
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38.25


Example 103
Polyester emulsion
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 104
Polyester emulsion
4.50
Polyethylene glycol
4.50
Iron oxide pigment
36.00


Example 105
Polyester emulsion
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 106
Polyester emulsion
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 107
Polyester emulsion
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 108
Polyester emulsion
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 109
Polyester emulsion
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 110
Polyester emulsion
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.25


Example 111
Polyester emulsion
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38.25


Example 112
Polyester emulsion
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 113
Polyester emulsion
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 114
Polyester emulsion
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 115
Polyester emulsion
6.75
Dipropylene glycol
3.15
Iron oxide pigment
35.10


Example 116
Polyester emulsion
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 117
Polyester emulsion
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31.50


Example 118
Polyvinylpyrrolidone
3.60
1,3-butanediol
2.25
Iron oxide pigment
39.15


Example 119
Polyvinylpyrrolidone
3.60
1,3-butanediol
3.15
Iron oxide pigment
38.25


Example 120
Polyvinylpyrrolidone
4.50
1,3-butanediol
2.25
Iron oxide pigment
38.25


Example 121
Polyvinylpyrrolidone
4.50
1,3-butanediol
3.15
Iron oxide pigment
37.35


Example 122
Polyvinylpyrrolidone
4.50
1,3-butanediol
4.50
Iron oxide pigment
36.00


Example 123
Polyvinylpyrrolidone
6.75
1,3-butanediol
2.25
Iron oxide pigment
36.00


Example 124
Polyvinylpyrrolidone
6.75
1,3-butanediol
3.15
Iron oxide pigment
35.10


Example 125
Polyvinylpyrrolidone
6.75
1,3-butanediol
4.50
Iron oxide pigment
33.75


Example 126
Polyvinylpyrrolidone
6.75
1,3-butanediol
6.75
Iron oxide pigment
31.50


Example 127
Polyvinylpyrrolidone
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 128
Polyvinylpyrrolidone
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 129
Polyvinylpyrrolidone
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38.25


Example 130
Polyvinylpyrrolidone
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 131
Polyvinylpyrrolidone
4.50
Polyethylene glycol
4.50
Iron oxide pigment
36.00


Example 132
Polyvinylpyrrolidone
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 133
Polyvinylpyrrolidone
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 134
Polyvinylpyrrolidone
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 135
Polyvinylpyrrolidone
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 136
Polyvinylpyrrolidone
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 137
Polyvinylpyrrolidone
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.25


Example 138
Polyvinylpyrrolidone
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38.25


Example 139
Polyvinylpyrrolidone
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 140
Polyvinylpyrrolidone
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 141
Polyvinylpyrrolidone
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 142
Polyvinylpyrrolidone
6.75
Dipropylene glycol
3.15
Iron oxide pigment
35.10


Example 143
Polyvinylpyrrolidone
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 144
Polyvinylpyrrolidone
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31,50


Example 145
Hydroxypropylmethyl cellulose
3.60
1,3-butanediol
2.25
Iron oxide pigment
39.15


Example 146
Hydroxypropylmethyl cellulose
3.60
1,3-butanediol
3.15
Iron oxide pigment
38.25


Example 147
Hydroxypropylmethyl cellulose
4.50
1,3-butanediol
2.25
Iron oxide pigment
38.25


Example 148
Hydroxypropylmethyl cellulose
4.50
1,3-butanediol
3.15
Iron oxide pigment
37.35


Example 149
Hydroxypropylmethyl cellulose
4.50
1,3-butanediol
4.50
Iron oxide pigment
36.00


Example 150
Hydroxypropylmethyl cellulose
6.75
1,3-butanediol
2.25
Iron oxide pigment
36.00


Example 151
Hydroxypropylmethyl cellulose
6.75
1,3-butanediol
3.15
Iron oxide pigment
35.10


Example 152
Hydroxypropylmethyl cellulose
6.75
1,3-butanediol
4.50
Iron oxide pigment
33.75


Example 153
Hydroxypropylmethyl cellulose
6.75
1,3-butanediol
6.75
Iron oxide pigment
31.50


Example 154
Hydroxypropylmethyl cellulose
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 155
Hydroxypropylmethyl cellulose
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 156
Hydroxypropylmethyl cellulose
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38.25


Example 157
Hydroxypropylmethyl cellulose
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 158
Hydroxypropylmethyl cellulose
4.50
Polyethylene glycol
4.50
Iron oxide pigment
36.00


Example 159
Hydroxypropylmethyl cellulose
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 160
Hydroxypropylmethyl cellulose
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 161
Hydroxypropylmethyl cellulose
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 162
Hydroxypropylmethyl cellulose
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 163
Hydroxypropylmethyl cellulose
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 164
Hydroxypropylmethyl cellulose
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.25


Example 165
Hydroxypropylmethyl cellulose
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38.25


Example 166
Hydroxypropylmethyl cellulose
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 167
Hydroxypropylmethyl cellulose
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 168
Hydroxypropylmethyl cellulose
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 169
Hydroxypropylmethyl cellulose
6.75
Dipropylene glycol
3,15
Iron oxide pigment
35.10


Example 170
Hydroxypropylmethyl cellulose
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 171
Hydroxypropylmethyl cellulose
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31.50









As can be seen from the graphs of FIGS. 8 to 13, even when the water-dispersible or water-soluble polymer was used and distilled solvent was used as the solvent, the brittleness of the capsule particles increased (the number of normal particles decreased). This suggests that the capsule particles can be prepared using an environmentally friendly process. Accordingly, it can be seen that the costs of supplementary facilities such as a solvent recovery apparatus and process costs can be reduced, and thus environmentally friendly products can be prepared.
Examples 172 to 198
Preparation of Core Powders from Natural Polymer Using Kinds and Contents of Plasticizer
Capsule particles were prepared in the same manner as Example 31, except that shellac was used as the polymer in step 1 of the preparation process of Example 31 and that ethanol was used in place of the acetone solvent to disperse or dissolve the iron oxide pigment. The specific kinds and contents of compounds used herein are shown in Table 8 below. The brittleness of the core powders according to changes in the amounts of plasticizer and shellac polymer used was measured, and the results of the measurement are shown in FIGS. 14 and 15.









TABLE 8









Step 1











Polymer
Plasticizer
Pigment

















Example 171
Shellac
3.60
1,3-butanedio
2.25
Iron oxide pigment
39.15


Example 173
Shellac
3.60
1,3-butanedio
3.15
Iron oxide pigment
38.25


Example 174
Shellac
4.50
1,3-butanedio
2.25
Iron oxide pigment
38/25


Example 175
Shellac
4.50
1,3-butanedio
3.15
Iron oxide pigment
37.35


Example 176
Shellac
4.50
1,3-butanedio
4.50
Iron oxide pigment
36.00


Example 177
Shellac
6.75
1,3-butanedio
2.25
Iron oxide pigment
36.00


Example 178
Shellac
6.75
1,3-butanedio
3.15
Iron oxide pigment
35.10


Example 179
Shellac
6.75
1,3-butanedio
4.50
Iron oxide pigment
33.75


Example 180
Shellac
6.75
1,3-butanedio
6.75
Iron oxide pigment
31.50


Example 181
Shellac
3.60
Polyethylene glycol
2.25
Iron oxide pigment
39.15


Example 182
Shellac
3.60
Polyethylene glycol
3.15
Iron oxide pigment
38.25


Example 183
Shellac
4.50
Polyethylene glycol
2.25
Iron oxide pigment
38/25


Example 184
Shellac
4.50
Polyethylene glycol
3.15
Iron oxide pigment
37.35


Example 185
Shellac
4.50
Polyethylene glycol
4.50
Iron oxide pigment
36.00


Example 186
Shellac
6.75
Polyethylene glycol
2.25
Iron oxide pigment
36.00


Example 187
Shellac
6.75
Polyethylene glycol
3.15
Iron oxide pigment
35.10


Example 188
Shellac
6.75
Polyethylene glycol
4.50
Iron oxide pigment
33.75


Example 189
Shellac
6.75
Polyethylene glycol
6.75
Iron oxide pigment
31.50


Example 190
Shellac
3.60
Dipropylene glycol
2.25
Iron oxide pigment
39.15


Example 191
Shellac
3.60
Dipropylene glycol
3.15
Iron oxide pigment
38.25


Example 192
Shellac
4.50
Dipropylene glycol
2.25
Iron oxide pigment
38/25


Example 193
Shellac
4.50
Dipropylene glycol
3.15
Iron oxide pigment
37.35


Example 194
Shellac
4.50
Dipropylene glycol
4.50
Iron oxide pigment
36.00


Example 195
Shellac
6.75
Dipropylene glycol
2.25
Iron oxide pigment
36.00


Example 196
Shellac
6.75
Dipropylene glycol
3.15
Iron oxide pigment
35.10


Example 197
Shellac
6.75
Dipropylene glycol
4.50
Iron oxide pigment
33.75


Example 198
Shellac
6.75
Dipropylene glycol
6.75
Iron oxide pigment
31.50









As can be seen from the graphs of FIGS. 14 and 15, even when the core powders prepared using the natural polymer, the brittleness of the capsule particles increased (the number of normal particles decreased). This suggests that environmentally friendly products and Ecocert products can be prepared.
Examples 199 to 207
Preparation of Core Powders Consisting of Polyester Polymer-Plasticizer-Organic Pigment
Core powders were prepared in the same manner as Example 31, except that the acetone solvent used in step 1 of the preparation process of Example 31 was used to dissolve dipropylene glycol, a polyester polymer and an organic pigment and that an azo-, indigo- or phthalocyanine-based pigment compound was used as the organic pigment. The kinds and contents of compounds used herein are shown in Tables 9 below.









TABLE 9









Step 1











Polymer
Plasticizer
Pigment

















Example
Polyester
3.60
Dipropylene glycol
2.25
Organic pigment
39.15


Example
Polyester
3.60
Dipropylene glycol
3.15
Organic pigment
38.25


Example
Polyester
4.50
Dipropylene glycol
2.25
Organic pigment
38.25


Example
Polyester
4.50
Dipropylene glycol
3.15
Organic pigment
37.35


Example
Polyester
4.50
Dipropylene glycol
4.50
Organic pigment
36.00


Example
Polyester
6.75
Dipropylene glycol
2.25
Organic pigment
36.00


Example
Polyester
6.75
Dipropylene glycol
3.15
Organic pigment
35.10


Example
Polyester
6.75
Dipropylene glycol
4.50
Organic pigment
33.75


Example
Polyester
6.75
Dipropylene glycol
6.75
Organic pigment
31.50









The use of the organic pigments could provide excellent color Clarity and strength and various and rich colors compared to the use of the inorganic pigments.
Examples 208 to 216
Preparation of Core Powders Consisting of Polyester Polymer-Plasticizer-Lake Dye
Core powders were prepared in the same manner as Example 31, except that the acetone solvent used in step 1 of the preparation process of Example 31 was used to dissolve the plasticizer dipropylene glycol, a polyester polymer and a lake dye and that Yellow No. 5 lake, Red No. 230 lake or a mixture thereof was used as the lake dye. The specific kinds and contents of compounds used herein are shown in Table 10 below.









TABLE 10









Step 1











Polymer
Plasticizer
Dye

















Example 208
Polyester
3.60
Dipropylene glycol
2.25
Lake dye
39.15


Example 209
Polyester
3.60
Dipropylene glycol
3.15
Lake dye
38.25


Example 210
Polyester
4.50
Dipropylene glycol
2.25
Lake dye
38.25


Example 211
Polyester
4.50
Dipropyiene glycol
3.15
Lake dye
37.35


Example 212
Polyester
4.50
Dipropylene glycol
4.50
Lake dye
36.00


Example 213
Polyester
6.75
Dipropylene glycol
2.25
Lake dye
36.00


Example 214
Polyester
6.75
Dipropylene glycol
3.15
Lake dye
35.10


Example 215
Polyester
6.75
Dipropylene glycol
4.50
Lake dye
33.75


Example 216
Polyester
6.75
Dipropylene glycol
6.75
Lake dye
31.50









Even the use of the lake dye could provide a rich color.
Examples 217 to 225
Preparation of Core Powders Consisting of Polyester Polymer-Plasticizer-Natural Pigment
Core powders were prepared in the same manner as Example 31, except that the acetone solvent used in step 1 of the preparation process of Example 31 was used to dissolve the plasticizer dipropylene glycol, the polyester polymer and a natural pigment and that turmeric, Gardenia, a graph skin pigment or a mixture of two or more thereof was used as the natural pigment. The specific kinds and contents of compounds used herein are shown in Table 11 below.









TABLE 11









Step 1











Polymer
Plasticizer
Pigment

















Example 217
Polyester
3.60
Dipropylene glycol
2.25
Natural pigment
39.15


Example 218
Polyester
3.60
Dipropylene glycol
3.15
Natural pigment
38.25


Example 219
Polyester
4.50
Dipropylene glycol
2.25
Natural pigment
38.25


Example 220
Polyester
4.50
Dipropylene glycol
3.15
Natural pigment
37.35


Example 221
Polyester
4.50
Dipropylene glycol
4.50
Natural pigment
36.00


Example 222
Polyester
6.75
Dipropylene glycol
2.25
Natural pigment
36.00


Example 223
Polyester
6.75
Dipropylene glycol
3.15
Natural pigment
35.10


Example 224
Polyester
6.75
Dipropylene glycol
4.50
Natural pigment
33.75


Example 225
Polyester
6.75
Dipropylene glycol
6.75
Natural pigment
31.50









Even the use of the natural pigment provided the core particles having high brittleness in the same manner as the use of the iron oxide pigment.
Examples 226 to 242
Preparation of Capsule Powders Comprising Inorganic Material Coated on Core Powders
Example 226
45 g of the core powder prepared in Example 31 was stirred and dispersed in a mixed solution of 207 ml of distilled water and 23 ml of ethanol at 25° C. for 10 minutes to make a solution. Meanwhile, 5 g of boron nitride and 50 g of titanium dioxide were stirred in 100 ml of distilled water at 25° C. for 10 minutes to make an inorganic suspension. Then, the inorganic suspension and the solution were mixed and stirred at 25° C. for 10 minutes, and the mixed solution was fed into an atomizer (rotating at a high speed of 10,000 rpm) at a constant rate of 120 ml/min using a metering pump. Herein, the mixed solution was fed into the atomizer at 160° C. and dried therein at 80° C. to obtain capsule powder. The obtained capsule powder had an outer diameter ranging from 10 μm to 150 μm.
Examples: 227 to 228
Capsules powders were prepared in the same manner as Example 226, except that the contents of titanium dioxide and boron nitride used to form the inorganic coating layer were changed. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.
Examples 229 to 231
Capsule powders were prepared in the same manner as Example 226, except that varying amounts of titanium dioxide and zinc oxide were used to form an inorganic coating layer. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.
Examples 232 to 234
Capsule powders were prepared in the same manner as Example 226, except that varying amounts of titanium dioxide, boron nitride and zinc oxide were used to form an inorganic coating layer. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.
Examples 235 to 236
Capsule powders were prepared in the same manner as Example 226, except that varying amounts of titanium dioxide, boron nitride and talc were used to form an inorganic coating layer. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.
Examples 237 to 239
Capsule powders were prepared in the same manner as Example 226, except that varying amounts of titanium dioxide, zinc oxide and talc were used to form an inorganic coating layer. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.
Examples 240 to 242
Capsule powders were prepared in the same manner as Example 226, except that varying amounts of titanium dioxide, zinc oxide and mica were used to form an inorganic coating layer. The specific kinds and contents of compounds used herein are shown in Table 12 below. The covering power of the inorganic coating layer according to its content is graphically shown in FIG. 16.








TABLE 12






Step 2





















Raw
Core
Titanium
Boron




material
powder
dioxide
nitride





Example 226
Content (%)
45
50
 5



Example 227
Content (%)
45
45
10



Example 228
Content (%)
45
40
15






Raw
Core
Titanium
Zinc




material
powder
dioxide
oxide





Example 229
Content (%)
45
50
 5



Example 230
Content (%)
45
45
10



Example 231
Content (%)
45
40
15






Raw
Core
Titanium
Boron
Zinc



material
powder
dioxide
nitride
oxide





Example 232
Content (%)
45
30
 5
20


Example 233
Content (%)
45
35
 5
15


Example 234
Content (%)
45
40
 5
10






Raw
Core
Titanium
Boron




material
powder
dioxide
nitride
Talc





Example 235
Content (%)
45
40
 5
10


Example 236
Content (%)
45
45
 5
 5






Raw
Core
Titanium
Boron




material
powder
dioxide
nitride
Talc





Example 237
Content (%)
45
30
15
10


Example 238
Content (%)
45
40
10
 5


Example 239
Content (%)
45
40
 5
10






Raw
Core
Titanium
Boron




material
powder
dioxide
nitride
Mica





Example 240
Content (%)
45
30
15
10


Example 241
Content (%)
45
40
10
 5


Example 242
Content (%)
45
40
 5
10









As can be seen in FIG. 16, the step of forming the inorganic coating layer on the color capsule in Example 226 showed the effect of increasing the covering power of the color capsule.
In Examples 227 to 228, as the content of titanium dioxide constituting the inorganic coating layer of the color capsule increased, the covering power of the color capsule increased, and as the content of boron nitride increased, the covering power, feeling and gloss of the color capsule increased.
In Examples 229 to 231, titanium dioxide used as a white pigment increased the covering power of the color capsule while showing the SPF blocking ability (UVB region). Likewise, the use of zinc oxide, which has somewhat lower covering power compared to titanium dioxide, but has the ability to block SPF in other UV region (UVA), could increase the covering power of the color capsule while providing color capsules capable of blocking light in the UV AB regions.
In Examples 232 to 234, the effects of Examples 227 to 231 could be expected, and the case having the highest content of titanium dioxide showed the highest covering power.
In Examples 235 to 236, the same effects as those of Examples 227 to 228 could be obtained, and talc was added in order to increase the feeling improvement effect which can be obtained using boron nitride. This feeling improvement effect was further increased as the content of talc increased.
In Examples 237 to 239, the same effects as those of Examples 229 to 231 could be obtained, and the feeling improvement effect could be obtained using talc in place of boron nitride.
In Examples 240 to 242, the same effects as those of Examples 229 to 231 could be obtained, and the feeling improvement effect could be obtained using mica in place of boron nitride or talc. As the content of mica increased, the feeling of the color capsules was further improved.
Examples 243 to 245
Preparation of Cosmetic Compositions Containing Color Capsules
Example 243
Preparation of W/O Emulsion Cream Emulsion Containing Color Capsules
4.56 g of the coated color capsules prepared in Example 226 were added to and mixed with 95.44 g of a W/O cream based composition, thereby preparing cream. The specific components and contents of the W/O cream base composition are shown in Table 13 below.







TABLE 13







WO emulsion formulation










Components
Contents (parts by weight)













KF-6033
2.00



Tegosoft CT
3.00



TIO2 CR50 OTS
4.50



Mica SDM
1.50



Perfomalene 400
0.30



Ozokerite
0.50



Abil WE-09
4.00



LP/Phytosqualane/Nexbase 2006
3.00



CEH
5.00



Vit E acetate
0.20



Bentongel GTCC V
6.00



BSG 250/Puresil CM
2.00



SF0015Z/DC 345
6.00



MP
0.20



1,3 BG (80° C.)
1.00



MGSO47H2O
1.20



EDTA-2NA
0.04



Elestab CPN (chlorphenesin)
0.15



1,3 BG
5.00



Glycerin
3.00



Keltrol F
0.06



DI-water
46.79



FeO (Yellow)
3.50



FeO (Red)
0.80



FeO (Black)
0.26



Total
100









Example 244
Preparation of W/O Emulsion Cream Containing Color Capsules
4.56 g of the coated color capsules prepared in Example 226 were added to and mixed with 95.44 g of a W/S cream base composition, thereby preparing cream. The specific components and contents of the W/S cream base composition are shown in Table 14 below.







TABLE 14







W/S emulsion formulation










Components
Contents (parts by weight)













KF-6028
2.00



SF0015Z/DC345
3.00



TiO2 CR50 OTS
4.00



Mica SDM
1.50



Abil wax 9801
1.00



Abil EM-90
2.00



DC 9040
4.00



Sf0015Z/DC345
5.00



KF56/DC556/SF5600
3.00



DC200F 16cs/SF1000N-20
4.00



Bentongel VS 5 PCV
6.00



MP
0.20



1,3 BG (80° C.)
1.00



NaCl
1.50



EDTA-2Na
0.02



Elestab CPN (chlorphenesin)
0.15



1,3 BG
5.00



Glycerin
3.00



DI-water
47.07



1% Na-Hyaluronate
2.00



FeO (Yellow)
3.50



FeO (Red)
0.80



FeO (Black)
0.26



Total
100.00









Example 245
Preparation of O/W Emulsion Cream Formulation Containing Color Capsules
4.56 g of the coated color capsules prepared in Example 226 were added to and mixed with 95.44 g of an 0/W cream base composition, thereby preparing cream. The specific components and contents of the W/O cream base composition are shown in Table 15 below.







TABLE 15







O/W emulsion formulation










Components
Contents (parts by weight)













CETOS KD
1.50



GMS 105
1.50



Arlacel #165
1.50



Tween #60
1.00



Arl #83
0.50



D-M
0.10



D-P
0.10



Phytosqualane
3.00



Puresyn 4
3.00



DC200 100 cs
0.50



DI-Water
77.24



1,3 BG
5.00



Sepiplus #400
0.50



FeO (Yellow)
3.50



FeO (Red)
0.80



FeO (Black)
0.26



Total
100.00









Measurement of Color Coordinates of Particles
The color coordinates of each of the cream formulations prepared in Examples 243, 244 and 245 were measured, and the results of the measurement are shown in Table 16 below.








TABLE 16








Color coordinates











L*
a*
b*





Example 243 (W/O emulsion formulation)
74.866
13.958
31.359


Example 244 (W/S emulsion formulation)
73.872
14.914
32.540


Example 245 (O/W emulsion formulation)
63.549
13.231
30.479









As can be seen in Table 16 above, the color capsules prepared according to the present invention showed similar color coordinates in the above formulations (the reason why the lightness of the O/W emulsion formulation was low because no TiO2 was used in the base cream), suggesting that the color capsules can be stably used in all formulations. This indicates that the prevent invention solves the problem in that, because the swelling properties of capsules differ between emulsion formulations, the color expressed when the capsules particles break differs between the emulsion formulations.
According to the present invention, the above-described problems occurring during the preparation of the color capsule particles can be solved, and a color cosmetic composition having improved unique properties, such as improved color coordinates and covering power, can be obtained.
As described above, in the color capsule composition of the present invention, the polymer and the plasticizer that swells the polymer are used such that the capsules easily break under specific conditions. Porosity can be imparted to the capsule particles using a simple spray dryer so as to boost the effects of the capsule particles.
Also, according to the present invention, core-shell particles having covering power can be prepared by simply forming on the outer wall of the core a coating layer of carbon dioxide, boron nitride, etc., which have covering power.
Moreover, according to the present invention, because no surfactant is used during the formation of the capsule particles, the physical properties of the final product can be easily controlled, and thus the number of additional process steps can be reduced. When the spray dryer is used, a drying process can be performed at the same time as the particle-forming process, and thus no wastewater is generated, thus reducing the production cost.
Furthermore, because the closed spray-drying system is used, a volatile solvent that is generated during the drying process can be recycled without being discharged, and the preparation process is environmentally friendly.
Meanwhile, color capsules containing natural or synthetic organic or inorganic pigments can be prepared which can express a wide range of colors.
In addition, the color capsules prepared according to the present invention can be used to prepare W/O emulsion formulations, W/S emulsion formulations and O/W emulsion formulations.
Although the preferred embodiments of the present invention have been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.

## Claims

1. A method for preparing a color capsule composition for cosmetics, the method comprising the steps of:
uniformly mixing a color pigment, a plasticizer and a polymer in a first solvent to produce a first mixture solution, wherein the polymer and the plasticizer are dissolved in the first solvent by stirring at 25° C. to prepare a solution, meanwhile the color pigment is dispersed in the first solvent at 25° C. to prepare a dispersion of the color pigment in the first solvent, and the solution is mixed with and uniformly dispersed in the dispersion at the same temperature, so as to produce the first mixture solution;
spray-drying the first mixture solution to produce core particles in which the color pigment is covered by the polymer;
uniformly mixing the obtained core particles, a functional pigment and a second solvent to produce a second mixture, wherein the functional pigment is stirred in the second solvent at 25° to obtain an inorganic suspension of the functional pigment in the second solvent, the obtained core powder is dispersed by stirring in the second solvent at 25° C., and the inorganic suspension and the dispersed core powder are mixed with each other stirring at 25° C.; and
spray-drying the second mixture to produce capsule particles, in each of which a coating layer of the functional pigment is formed on the outer surface of the polymer,
wherein, in the step of producing the first mixture solution, the polymer, the color pigment and the plasticizer are used in amounts of 5-15 wt %, 70-90 wt % and 5-15 wt %, respectively, based on the total weight of the polymer, the color pigment and the plasticizer, and in the step of producing the second mixture, the core particles and the functional pigment are used in amounts of 80-40 wt % and 20-61) wt %, respectively, based on the total weight of the core particles and the functional pigment,
wherein each of the first and second solvents consists of distilled water.

2. The method of claim 1, wherein the polymer is any one selected from the group consisting of polyester, a polyester emulsion, polyaminomethacrylate, polyvinylpyrrolidone, hydroxypropylmethylcellulose, and shellac.

3. The method of claim 1, wherein the plasticizer is any one selected from the group consisting of 1,3-butanediol, polyethylene glycol, dipropylene glycol, and a mixture of two or more thereof.

4. The method of claim 1, wherein the color pigment is any one selected from the group consisting of iron oxide pigments, organic pigments, lake dyes, and natural pigments.

5. The method of claim 1, wherein fatty acid is further added to the first mixture solution.

6. The method of claim 5, wherein the fatty acid is any one selected from the group consisting of stearic acid, palmitic acid, oleic acid, linoleic acid, and linolenic acid.

7. The method of claim 1, wherein the functional pigment is any one selected from the group consisting of titanium dioxide, zinc oxide, boron nitride, talc, mica, and a mixture of two or more thereof.

8. The method of claim 1, further comprising a step of sieve-screening dried core particles right after the step of spray-drying the first mixture solution, and a step of sieve-screening dried capsule particles right after the step of spray-drying the second mixture solution.