# Patent

## Title
Narrow spectral line-width emission phosphors with broad band excitation edge up to and including the blue wavelength region

## Abstract

Aspects of the present invention provide a family of phosphor compositions that may be used in the field of lighting applications. These phosphor compositions have crystal structures and chemical bond arrangements that enable broad band absorption and excitation using radiation up to and including the blue wavelength region. A preferred embodiment of the phosphor compositions has a general formula of (AxAy . . . Az)3−(1+q)m(W1−rMor)O6:Lnm,Dqm, wherein x+y+ . . . +z=1; 0≦r≦1; 0≦q≦1; 0<m≦0.12; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), W=tungsten with 6+ charge state, Mo=Molybdenum with 6+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−).

## Background
CROSS REFERENCE TO RELATED APPLICATIONS
The present application is the U.S. National Phase Application of PCT/US2013/037366 which claims priority to U.S. Provisional Application, Ser. No. 61/687,238, filed Apr. 20, 2012, entitled NARROW SPECTRAL LINE-WIDTH EMISSION PHOSPHORS WITH BROAD BAND EXCITATION EDGE IN THE BLUE WAVELENGTH REGION. The contents of such applications are incorporated fully herein by reference.


STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH & DEVELOPMENT
The present invention was made with United States Government support under contract number EEC-0812056, awarded by the National Science Foundation, and contract number C090145, awarded by NYSTAR. The United States Government may have certain rights to the invention.


FIELD OF THE INVENTION
The present invention generally relates to a phosphor composition for lighting and display applications. In particular, the phosphor composition enables broad band absorption and excitation of light up to and including the blue wavelength region, and wavelength conversion to longer wavelength regions.
BACKGROUND OF THE INVENTION
The development of solid state semiconductor devices, in particular light emitting diodes (LEDs), has opened up the possibility of a new generation of energy efficient lighting solutions. Development of LEDs that emit light in the blue/ultraviolet part of the electromagnetic spectrum has resulted in practical applications of white light sources based on LEDs (i.e., “white LEDs”). Due to their long operational lives and high efficiency, it is predicted that white LEDs could eventually replace incandescent, fluorescent, and other conventional light sources.
Techniques have been developed for converting the light emitted from LEDs to useful white light for illumination, as well as other purposes. For these techniques, phosphor layers are typically placed in close proximity to a light emitting surface of the LED chip from which they derive their excitation energy. The phosphor absorbs radiation energy in one portion of the electromagnetic spectrum and emits energy in another portion of the electromagnetic spectrum. Phosphors, for example, may emit radiation in the visible portion of the electromagnetic spectrum in response to excitation by electromagnetic energy outside the visible range.
There presently exist significant obstacles in the development of phosphor-converted white LEDS with superior characteristics. One such obstacle includes the lack of narrow-emitting red, orange, yellow, green or other visible wavelength phosphors that are effectively excited by blue or near-UV LEDs.
SUMMARY OF THE INVENTION
A composition according to one aspect of the invention comprises a phosphor having a general formula of (AxAy . . . Az)3−(1+q)m(W1−rMor)O6:Lnm,Dqm, wherein x+y+ . . . +z=1; 0≦r≦1; 0≦q≦1; 0<m≦0.12; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), W=tungsten with 6+ charge state, Mo=Molybdenum with 6+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). Examples of this phosphor may include the composition Ca2.88MoO6:Eu0.06Na0.06, as well as the composition (Sr0.4Ca0.2Mg0.1Ba0.2Zn0.1)2.8(Mo0.4W0.6)O6:Eu0.1Li0.1.
A composition according to another aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)1−(1+q)m(W1−rMor)O3:Lnm,Dqm, wherein x+y+ . . . +z=1; 0≦r≦1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), W=tungsten with 4+ charge state, Mo=Molybdenum with 4+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Ca0.80WO3:Eu0.1Na0.1.
A composition according to a third aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)3−(1+q)m(BxBy . . . Bz)2−k(W1−rMor)O9:Lnm+k,Dqm, wherein x+y+ . . . +z=1; 0≦k≦1; 0≦r≦1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), B=Trivalent element from group IIIA, IIIB or Rare Earth Lanthanide elements (e.g., Sc3+, Y3+, La3+, B3+, Al3+, Ga3+, Ce3+ to Lu3+, etc.), W=Tungsten with 6+ charge state, Mo=Molybdenum with 6+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Mg2.8Y1.5WO9:Eu0.6Na0.1.
A composition according to a fourth aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)2−m(W1−rMor)2O7:Lnm; wherein x+y+ . . . +z=1; 0≦r≦1; 0<m≦1; and A=Trivalent element from group IIIA, IIIB or Rare Earth Lanthanide elements (e.g., Sc3+, Y3+, La3+, B3+, Al3+, Ga3+, Ce3+ to Lu3+, etc.), W=Tungsten with 4+ charge state, Mo=Molybdenum with 4+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Y1.5Mo2O7:Eu0.5.
A composition according to a fifth aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:Lnm,Dqm; wherein x+y+ . . . +z=1; p+r+s=1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), V=Vanadium with 5+ charge state, Nb=Niobium with 5+ charge state, Ta=Tantalum with 5+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). Examples of this phosphor may include the composition Ca1.88V2O7:Eu0.06Na0.06, as well as the composition Sr0.9Ca0.9V0.8Nb1.2O7:Eu0.1Li0.1.
A composition according to a sixth aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)3−(1+q)m(VpNbrTas)2O8:Lnm,Dqm, wherein x+y+ . . . +z=1; p+r+s=1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), V=Vanadium with 5+ charge state, Nb=Niobium with 5+ charge state, Ta=Tantalum with 5+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). Examples of this phosphor may include the composition Ca2.88Nb2O8:Eu0.06Na0.06, as well as the composition Sr1.8Ca0.8V2O8:Eu0.2Li0.2.
A composition according to a seventh aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)2−(1+q)m(BxBy . . . Bz)1−k(VpNbrTas)O6:Lnm+k,Dqm, wherein x+y+ . . . +z=1; p+r+s=1; 0≦q≦1; 0≦k≦1; 0<M≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), B=Trivalent element from group IIIA, IIIB or Rare Earth Lanthanide elements (e.g., Sc3+, Y3+, La3+, B3+, Al3+, Ga3+, Ce3+ to Lu3+, etc.), V=Vanadium with 5+ charge state, Nb=Niobium with 5+ charge state, Ta=Tantalum with 5+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Sr1.88YNbO6:Eu0.06Na0.06 
A composition according to an eighth aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)3−(1+q)m(VpNbrTas)2O7:Lnm,Dqm, wherein x+y+ . . . +z=1; p+r+s=1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), V=Vanadium with 4+ charge state, Nb=Niobium with 4+ charge state, Ta=Tantalum with 4+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Sr2.8VNbO7:Eu0.1Na0.1.
A composition according to a ninth aspect of the invention provides a phosphor having a general formula of (AxAyAz)2−(1+q)m(VpNbrTas)2O5:Lnm,Dqm, wherein x+y+ . . . +z=1; p+r+s=1; 0≦q≦1; 0<m≦0.24; and A=Divalent element from group IIA and/or IIB (e.g., Mg2+, Ca2+, Sr2+, Ba2+, Zn2+, etc.), V=Vanadium with 3+ charge state, Nb=Niobium with 3+ charge state Ta=Tantalum with 3+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), D=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Mg1.6V2O5:Eu0.2Na0.2.
A composition according to a tenth aspect of the invention provides a phosphor having a general formula of (AxAy . . . Az)3(BxBy . . . Bz)1−m(W1−rMor)O6:Lnm, wherein x+y+ . . . +z=1; 0≦r≦1; 0<m≦0.48; and A=Monovalent element from group IA and/or IB (e.g., Li1+, Na1+, Cu1+, etc.), B=Trivalent element from group IIIA, IIIB or Rare Earth Lanthanide elements (e.g., Sc3+, Y3+, La3+, B3+, Al3+, Ga3+, Ce3+ to Lu3+, etc.), W=Tungsten with 6+ charge state, Mo=Molybdenum with 6+ charge state, Ln=Trivalent rare earth lanthanide element (e.g., Ce3+ to Lu3+), and O=Oxygen (O2−). An example of this phosphor composition may include the composition Na3Gd0.7MoO6:Eu0.3.
Additional embodiments of the present invention include light emitting and light modulation devices having a source for ultraviolet or visible radiation, power leads providing current to the source for emitting the radiation, and one or more phosphors of the aforementioned embodiments of the present invention.



BRIEF DESCRIPTION OF DRAWINGS
These and other features, aspects, and advantages of the present invention will become better understood when the following detailed description is read with reference to the accompanying drawings in which like characters represent like parts throughout the drawings, wherein:
FIG. 1 is a schematic cross-sectional view of an illumination device in accordance with an embodiment of the present invention;
FIG. 2 is a chart of the excitation spectra of four exemplary phosphors in accordance with embodiments of the present invention;
FIG. 3 is a chart of the excitation spectra of three additional exemplary phosphors in accordance with embodiments of the present invention;
FIG. 4 is a chart of the excitation spectra of seven additional exemplary phosphors in accordance with embodiments of the present invention; and
FIG. 5 is a chart of the emission spectra of an exemplary phosphor with 395 nm and 465 nm excitation wavelengths, in accordance with embodiments of the present invention.
FIGS. 6a, b-13a,b show the excitation and emission spectra of various exemplary phosphor compositions, in accordance with embodiments of the present invention.
FIG. 14 is a chart of the emission spectrum of an exemplary phosphor excited by a 400 nm LED.
FIG. 15 is a chart of the emission spectrum of another exemplary phosphor excited by a 450 nm LED.
FIG. 16 is a schematic cross-sectional view of an illumination device in accordance with another embodiment of the present invention.



DETAILED DESCRIPTION OF THE INVENTION
Embodiments of the present invention provide phosphor compositions that may be used in lighting systems, such as LEDs, fluorescent tubes, and the like. The applications of lighting systems using the phosphor compositions described throughout the specification, however, are not limited to any particular preferred general illumination purposes. They may include any lighting systems currently understood by those skilled in the art.
The phosphor compositions according to embodiments of the present invention have crystal structures and chemical bond arrangements that enable broad band absorption and excitation of light up to and including the blue wavelength regions (e.g., 400-490 nm), and wavelength conversions to longer wavelength regions. The phosphor compositions have narrow spectral line-width (e.g. full width at half maximum that is less than 5 nm) suitable for high efficiency white light LED fabrication. The phosphors provide emission in green (e.g., 550 nm), yellow (e.g., 575 nm), orange (e.g., 615), and red (e.g., 650 nm) wavelengths. In addition to wavelength conversions, phosphor compositions according to aspects of the present invention may be used for varying temporal characteristics of light, such as intensity, polarization, and spatial distribution.
Commercial phosphor-converted white LEDs employ blue (e.g., 400-470 nm) or near-ultraviolet (UV) (e.g., 380-400 nm) LED chips and RY (red-yellow) or tricolor phosphors, respectively, to produce white light with a high CRI (color rendering index) and a low CCT (correlated color temperature). These LEDs require red phosphors in order to maximize efficacy while maintaining high color quality. The phosphor compositions according to embodiments of the present invention result in phosphor-converted white LEDs with superior characteristics. In particular, the phosphor compositions of the present invention result in narrow-emitting red phosphors that are effectively excited by blue (e.g., 400-490 nm) or near-UV (e.g., 380-400 nm) LEDs.
FIG. 1 depicts an LED device 100 according to an aspect of the present invention. LED devices are known in the art. Typically, LED device 100 includes a semiconductor UV or visible radiation source, such as an LED chip 106. Power leads 112, providing current that causes LED chip 106 to emit radiation, are electrically connected to the LED chip 106. Power leads 112 may include thin wires supported by thicker package leads 108. Alternatively, package leads 108 may be directly attached to LED chip 106. LED chip 106 may be encapsulated within a shell 102. Shell 102 may be glass, plastic, or any other material known in the art. Shell 102 is typically transparent with respect to the light produced by LED chip 106.
LED device 100 may further include a phosphor compound 104 according to one embodiment of the present invention. Phosphor compound 104 is typically radiationally coupled to LED chip 106. For example, radiation from LED chip 106 is transmitted to phosphor compound 104, and vice-versa. A phosphor compound 104 that is radiationally coupled to the LED chip 106 may absorb radiation, such as blue or UV light, emitted by LED chip 106. Phosphor compound 104 may then emit radiation in longer wavelengths, such as blue, blue-green, red, or other colors of light.
Phosphor composition 104 may be deposited on LED device 100 by any method presently known by those skilled in the art. As one example, phosphor compound 104 can be formed and applied as a layer onto the surface of LED chip 106. If shell 102 is transparent, the emitted light 110 from LED chip 106 and phosphor compound 104 will be transmitted through shell 102. As another example, the phosphor compound 104 may be formed on the surface of shell 102. As yet another example, phosphor composition 104 (e.g., in powder form) may be mixed with material forming shell 102 (e.g., resin) of LED device 100. The radiation emitted by LED chip 106, mixed with phosphor compound 104, will appear as emitted light 110.
Phosphor compositions of the present invention will now be described. Generally, the phosphor compositions of the present invention may be categorized into two classes. The first class of compositions are trivalent rare earth doped (activated) Group VB and VIB transition metal double perovskites of the A2B′B′′O6 and AB′B′′2O7 type. In this first class of compositions, the transition metal is octahedrally coordinated by oxygen in a 6+ or 5+ charge state, respectively, and occupies the B′′ site. The A and B′ sites are occupied by elements from groups IA, IIA, IIIB, IIB, IIIA, and a lanthanide group. The second class of compositions include trivalent rare earth doped (activated) Group VIB transition metal oxides with the AB2O2, ABO3, and A2B2O7 types. For the second class of compositions, transition metal is in a 3+ or 4+ charge state and occupies the B site. The A site is occupied by elements from groups IA, IIA, IIIB, IIB, IIIA, and a lanthanide group.
For use in solid-state lighting, phosphors should be well excited by near-UV (e.g., 395 nm) or blue (e.g., 465 nm) light. Alkaline earth metal molybdates, for example, have been used as materials for various applications, e.g., laser hosts, X-ray detection, etc. This class of compounds is self-activated due to the luminescence from MoO4 tetrahedral groups in the scheelite host lattice.
Alkaline earth metal tungstates and molybdates serve as excellent host materials for trivalent lanthanide ions like Eu3+. These compounds efficiently absorb far-UV radiation via charge transfer state of WO4 and MoO4 groups and then transfer this to Eu3+ ions, producing narrow emission lines due to f-f transitions. However, in these compounds, the charge transfer band edge is 330 nm, and luminescence through near-UV and blue excitation is limited to f-f transitions of Eu3+ ions. Eu3+ ions are parity-forbidden; therefore, the excitation is weak and insufficient for illumination grade LEDs.
Narrow line-width emission is particularly important to lighting. Commercial fluorescent lamps, for example, contain phosphors that emit multitudes of narrow wavelength ranges in the blue, green, and red regions of the visible light spectrum, which mix to provide white light. The narrow line-width is characterized by the wavelength range of emission from the phosphor (full-width at half-maxima of typically less than 5 nm). Narrow line-width emission results in high luminous efficacy by preventing light spill over in the wavelengths outside of the human eye sensitivity curve. For example, in order to obtain the maximum possible luminous efficacy of 375 lm/W at a CRI of 85 and CCT of 3800 K, white light produced from four narrow-emitting sources at 459 nm, 535 nm, 573 nm and 614 nm, respectively, is needed with the relative power of the sources being 0.18, 0.25, 0.22, 0.36, respectively.
The charge transfer state of MO4 (where M=Mo or W) groups is located at a higher energy as compared to that of MO6 groups. The higher coordination number of the transition metal ion in MO6 (where M=Mo or W) complexes leads to longer M-O bonds and lower M6+—O2− bond energy, which decides the energy of the charge transfer state. These MO6 complexes are found in various compounds like A2CaMO6 (where A=Ba or Sr; and M=Mo or W), R2MO6 (where R═Y or Gd; and M=Mo or W) and R6MO12 (where R═Y or Gd; and M=Mo or W), and when doped with Eu3+, the charge transfer band edges are around 430 nm, 400 nm, and 430 nm, and the emission maxima are around 594 nm and 615 nm, respectively.
While R2MO6 compounds have a shorter charge transfer band (CTB) edge, A2CaMO6 (where A=Ba or Sr; and M=Mo or W) type compounds favor the magnetic dipole transition of Eu3+ ion over the electric dipole transition, resulting in a peak emission wavelength of 594 nm instead of 615 nm. Further, the synthesis of pure hexagonal phase of R6MO12 (where R═Y or Gd; and M=Mo or W) doped with Eu3+, exhibiting a CTB edge of 430 nm, is difficult. Therefore, in embodiments of the present invention, another series of compounds have been doped with Eu3+, which comprise MO6 complexes (where M=Mo or W) with specific crystal structure that results in extension of the charge transfer band in the blue wavelength region (e.g., 400-490 nm). Using the same classes of compounds, but using different dopant species Ho3+, Dy3+, Pr3+, Sm3+, Tb3+, etc., narrow spectral lines with peak emission at different wavelengths in the visible spectrum range (e.g., 500-700 nm) is possible.
According to embodiments of the present invention, various phosphor compositions have been synthesized using solid state reaction and flux growth methods at high temperature under a variety of ambients (e.g., oxygen, inert gas, and vacuum). The phosphor compositions include samples in powder form and in crystal form. In one embodiment, the various compositions were synthesized in the temperature range of 800-1600° C. In a preferred embodiment, the various compositions were synthesized at a temperature range at or above 1000° C. In a more preferred embodiment, the various compositions were synthesized at a temperature range at or above 1300° C.
X-ray diffraction (XRD) data was recorded on a Bruker D8 Discover Diffractometer running on Cu Kα radiation at 40 kV and 40 mA. This data was used to determine the crystal structure of the synthesized phosphors and to calculate their lattice constants. Excitation and Emission Spectrum measurements were carried out using a Flourolog Tau-3 Lifetime Measurement system. The excitation spectra were recorded for specific emission wavelengths. However, aspects of the invention should not be limited to the above devices and systems for reading and measuring. Those skilled in the art will understand the other devices and systems that may be used for reading and measuring. TABLES 1, 2, 3, and 4, shown below, provide representative phosphor compositions synthesized according to embodiments of the present invention.










TABLE 1







Charge Transfer Band



Phosphor composition
Crystal Structure
Edge
CT-Absorbing Group



















Mg3Y2MoO9: Eu3+
Cubic phase, with
400
nm
MoO6



octahedrally coordinated






Mo6+ ion





A3Y2MoO9: Eu3+
Cubic phase with
420-430
nm
MoO6


(A = Ca, Sr, Ba)
octahedrally coordinated






Mo6+ ion





Mg3MoO6: Eu3+
orthorhombic phase, with
400
nm
MoO6



octahedrally coordinated






Mo6+ ion





A3MoO6: Eu3+
orthorhombic phase, with
420-430
nm
MoO6


(A = Ca, Sr, Ba)
octahedrally coordinated






Mo6+ ion













A3MoxW1—xO6: Eu3+ **
orthorhombic phase with
340-430 nm;
MO6 (M = Mo, W)


(A = Mg, Ca, Sr, Ba)
octahedrally coordinated
**x = 0 exhibits the highest




Mo6+/W6+ ion
emission intensity but





shortest charge transfer





band edge












A5V2O10: Eu3+
Orthorhombic phase with
420-430
nm
VO6


(A = Mg, Ca, Sr, Ba)
five coordinated V5+ ion





A3Nb2O8: Eu3+
Rhombohedral phase with
420-430
nm
NbO6


(A = Mg, Ca, Sr, Ba)
octahedrally coordinated






Nb5+ ion





A2YBO6: Eu3+
Monoclinic phase with
420-430
nm
BO6


(A = Mg, Ca, Sr, Ba; B =
octahedrally coordinated





Ta, Nb)
B5+ ion





AMoO3: Eu3+
Orthorhombic phase in A =
415-420
nm
MoO4


(A = Ca, Sr, Ba)
Ca and cubic phases in A =






Sr, Ba with Mo4+ state





A2Mo2O7: Eu3+
Cubic phase with Mo4+
380-400
nm
MoO4


(A = Y, Gd, Lu)
state



















TABLE 2






Peak Emission
Experimentally



Phosphor
Wavelength
observed CT
Crystal


Composition
(nm)
Band Edge (nm)
Structure







Mg3Y2MoO9: Eu3+
611
397
Cubic


Mg3Y2WO9: Eu3+
615
328
Cubic


CaWO4: Eu3+
615
320
Tetragonal


CaMoO4: Eu3+
615
330
Tetragonal


Ca3Y2MoO9: Eu3+
615
418
Cubic


CaMoO3: Eu3+
615
415
Orthorhombic


SrMoO4: Eu3+
615
290
Tetragonal


SrMoO3: Eu3+
615
380
Cubic


BaMoO4: Eu3+
615
325
Tetragonal


Ba2CaMoO6: Eu3+
594
425
Cubic


BaMoO3: Eu3+
615
388
Cubic


Ba3Y2WO9: Eu3+
615
338
Cubic


Y2WO6: Eu3+
615
329
Monoclinic


Y2MoO6: Eu3+
610
400
Monoclinic


Y2Mo2O7: Eu3+
615
380
Cubic


Gd2MoO6: Eu3+
613
400
Monoclinic




















TABLE 3





Phosphor
Crystal
Peak Emission
Charge Transfer
CT- Absorbing


Composition
Structure
Wavelength (nm)
Band Edge (nm)
Group



















Ca0.88MoO4: Eu0.123+
Tetragonal
614
330
MoO4


Ca0.88WO4: Eu0.123+
Tetragonal
615
300
WO4


Y1.94(MoO4)3: Eu0.063+
Orthorhombic
611
320
MoO4


Gd1.94(MoO4)3: Eu0.063+
Orthorhombic
613
320
MoO4


Zn0.88MoO4: Eu0.123+
Tricilinic
613
330
MoO4


Y1.94MoO6: Eu0.063+
Monoclinic
609
400
MoO5


Gd1.94MoO6: Eu0.063+
Monoclinic
609
405
MoO5


Ca2.88MoO6: Eu0.123+
Orthorhombic
615
425
MoO6


Ca2.88WO6: Eu0.123+
Orthorhombic
615
330
WO6


Ba2Ca0.88MoO6: Eu0.123+
Cubic
594
430
MoO6


Y5.88MoO6: Eu0.123+
Hexagonal
615
430
MoO6


Gd5.88MoO6: Eu0.123+
Hexagonal
615
430
MoO6


Y5.88MoO6: Eu0.123+
Cubic
615
~480
MoO6


Gd5.88MoO6: Eu0.123+
Cubic
615
~480
MoO6



















TABLE 4










Charge


Phospor
Generic
Peak Emission
Transfer Band


Compositions
Formula
(nm)
Edge (nm)





Mg2.9MoO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
611
420


Eu0.13+
Lnm, Dqm


Mg2.98MoO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
594
490


Eu0.023+
Lnm, Dqm


Ca2.8MoO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
615
440


Eu0.23+
Lnm, Dqm


Sr2.88MoO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
615
410


Eu0.123+
Lnm, Dqm


Ca2.98WO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
575
400


Dy0.023+
Lnm, Dqm


Ca2.95WO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
615
400


Eu0.13+
Lnm, Dqm


Ca2.95WO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
650
400


Sm0.053+
Lnm, Dqm


Sr2.96WO6:
(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:
594
490


Eu0.043+
Lnm, Dqm


Ca0.8MoO3:
(AxAy . . . Az)1−(1+q)m(W1−rMor)O3:
615
430


Eu0.23+
Lnm, Dqm


Sr0.9MoO3:
(AxAy . . . Az)1−(1+q)m(W1−rMor)O3:
615
410


Eu0.13+
Lnm, Dqm


Ba0.8MoO3:
(AxAy . . . Az)1−(1+q)m(W1−rMor)O3:
615
410


Eu0.23+
Lnm, Dqm


Mg2.8Y2MoO9:
((AxAy . . . Az)3−(1+q)m(BxBy . . . Bz)2−k(W1−rMor)O9:
615
420


Eu0.23+
Lnm+k, Dqm


Ca2.8Y2MoO9:
((AxAy . . . Az)3−(1+q)m(BxBy . . . Bz)2−k(W1−rMor)O9:
615
440


Eu0.23+
Lnm+k, Dqm


Y1.8Mo2O7:
(AxAy . . . Az)2−m(W1−rMor)2O7:
615
420


Eu0.23+
Lnm


Ca1.8V2O7:
(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:
615
420


Eu0.23+
Lnm, Dqm


Ca1.95V2O7:
(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:
575
400


Dy0.053+
Lnm, Dqm


Ca1.95V2O7:
(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:
650
400


Sm0.053+
Lnm, Dqm


Ba1.8Nb2O7:
(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:
615
500


Eu0.23+
Lnm, Dqm


Ca2.8Nb2O8:
(AxAy . . . Az)3−(1+q)m(VpNbrTas)2O8:
615
400


Eu0.23+
Lnm, Dqm


Ca1.9YNbO6:
(AxAy . . . Az)2−(1+q)m(BxBy . . . Bz)1−k(VpNbrTas)O6:
615
400


Eu0.13+
Lnm+k, Dqm


Ca2.8V2O7:
(AxAy . . . Az)3−(1+q)m(VpNbrTas)2O7:
615
430


Eu0.23+
Lnm+k, Dqm


Ca1.8V2O5:
(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O5:
615
440


Eu0.23+
Lnm+k, Dqm


Na3Y0.9MoO6:
(AxAy . . . Az)3(BxBy . . . Bz)1−m(W1−rMor)O6:
615
420


Eu0.13+
Lnm


Na3Y0.95MoO6:
(AxAy . . . Az)3(BxBy . . . Bz)1−m(W1−rMor)O6: 
650
420


Sm0.053+
Lnm



















Charge State of


Synthesis



Phospor
Crystal
Transition
Absorbing
Coordination
Temperature



Compositions
Structure
Metal Ion
Group
Number
(° C.)







Mg2.9MoO6:
Orthorhombic
6+
MoO6
6
≧1200



Eu0.13+



Mg2.98MoO6:
Orthorhombic
6+
MoO6
6
≧1200



Eu0.023+



Ca2.8MoO6:
Orthorhombic
6+
MoO6
6
≧1200



Eu0.23+



Sr2.88MoO6:
Orthorhombic
6+
MoO6
6
≧1300



Eu0.123+



Ca2.98WO6:
Monoclinic
6+
WO6
6
≧1300



Dy0.023+



Ca2.95WO6:
Monoclinic
6+
WO6
6
≧1300



Eu0.13+



Ca2.95WO6:
Monoclinic
6+
WO6
6
≧1300



Sm0.053+



Sr2.96WO6:
Monoclinic
6+
WO6
6
≧1300



Eu0.043+



Ca0.8MoO3:
Orthorhombic
4+
MoO4
4
≧1100



Eu0.23+



Sr0.9MoO3:
Cubic
4+
MoO4
4
≧1100



Eu0.13+



Ba0.8MoO3:
Cubic
4+
MoO4
4
≧1100



Eu0.23+



Mg2.8Y2MoO9:
Cubic
6+
MoO6
6
≧1200



Eu0.23+



Ca2.8Y2MoO9:
Cubic
6+
MoO6
6
≧1200



Eu0.23+



Y1.8Mo2O7:
Cubic
4+
MoO4
4
≧1100



Eu0.23+



Ca1.8V2O7:
Triclinic
5+
V2O7
4
≧1100



Eu0.23+



Ca1.95V2O7:
Triclinic
5+
V2O7
4
≧1100



Dy0.053+



Ca1.95V2O7:
Triclinic
5+
V2O7
4
≧1100



Sm0.053+



Ba1.8Nb2O7:
Triclinic
5+
Nb2O7
4
≧1100



Eu0.23+



Ca2.8Nb2O8:
Rhombohedral
5+
NbO6
6
≧1100



Eu0.23+



Ca1.9YNbO6:
Monoclinic
5+
NbO6
6
≧1100



Eu0.13+



Ca2.8V2O7:
Triclinic
4+
VO4
4
≧1000



Eu0.23+



Ca1.8V2O5:
Cubic
3+
VO4
4
≧1000



Eu0.23+



Na3Y0.9MoO6:
Monoclinic
6+
MoO6
6
≧1100



Eu0.13+



Na3Y0.95MoO6:
Monoclinic
6+
MoO6
6
≧1100



Sm0.053+










According to another aspect of the present invention, the crystal structures of Ca3MoO6 and Ca3WO6 phosphors were determined to be orthorhombic and monoclinic, respectively. In Ca3WO6 phosphors, the monoclinic angle (90.15°) is very close to 90°; therefore, it is almost an orthorhombic unit cell.
All peaks in the XRD were indexed to Joint Committee on Powder Diffraction Standards (JCPDS) 00-026-1068 and JCPDS 00-022-0541 for Ca3MoO6 and Ca3WO6 samples, respectively. Thus, the synthesized phosphors are considered to have high phase purity, and the lanthanide ions were uniformly incorporated in the lattice. The synthesized phosphors form a double perovskite structure with the general formula A2B′B′′O6 (1:1 ordering of B′ and B′′ site cations), wherein A site cations are 12-coordinated and B′ and B′′ site cations are octahedrally coordinated by O2− ions. Since there is only one alkaline earth metal cation (Ca2+), both A and B′ sites are occupied by the same ion. B′′ site is occupied by the transition metal ion (Mo6+, W6+).
FIG. 2 depicts the excitation spectra of Ca3MO6:Eu3+ (where M=Mo or W) phosphors according to an embodiment of the present invention. The excitation spectra of CaMO4:Eu3+ (where M=Mo or W) phosphors with tetrahedral coordination of transition metal ion are also presented for comparison. For referencing purposes, FIG. 2 depicts CaMoO4:Eu3+ as element 202, Ca3MoO6:Eu3+ as element 204, CaWO4:Eu3+ as element 206, and Ca3WO6:Eu3+ as element 208. As illustrated in FIG. 2, the excitation spectra of Ca3MO6:Eu3+ (where M=Mo or W) phosphors comprise a broad charge transfer band and narrow excitation peaks resulting from f-f transitions.
The charge transfer bands of the phosphor compositions depicted in FIG. 2 originate from Eu3+—O2−, M6++O2− (where M=Mo6+ or W6+) charge transfer, and IVCT (inter-valence charge transfer) between Eu3+ and M6+ ions. The energies of Eu3+—O2− and M6+-O2− charge transfer depend upon the covalency of the Eu3+—O2− and M6+-O2 bonds. Higher covalency leads to lower energy. IVCT is the transition of electrons from the ground 4f state of Eu3+ to the excited state of W6+/Mo6+.
Because the electro-negativity of tungsten is higher than that of molybdenum (Pauling electro-negativity of molybdenum is 2.16 and that of tungsten is 2.36), molybdenum is easily oxidized, lowering the Mo6+—O2− bond energy in comparison to W6+—O2−. Thus, the excited state in tungstates is located at a higher energy than in molybdates, which is also seen from the excitation spectra. Also, while tungsten undergoes an efficient octahedral co-ordination, molybdenum, which is a smaller ion than tungsten, cannot be efficiently coordinated by six O2− ions. Thus, the change from MoO4 to MoO6 group leads to a greater change in the charge transfer band edge than the change from WO4 to WO6 group.
FIG. 3 shows the excitation spectra of Ba2CaMoO6:Eu3+ 302, Ca3MoO6:Eu3+ 304, and Y2MoO6:Eu3+ 306 phosphors, for peak emission wavelengths of 594 nm, 615 nm and 615 nm, respectively. Ba2CaMoO6:Eu3+ 302 and Y2MoO6:Eu3+ 306 phosphors were synthesized by solid-state reaction with 12% dopant concentration for comparison. The crystal structures of these phosphors are cubic, orthorhombic and monoclinic, respectively.
As can be seen from FIG. 3, Ba2CaMoO6:Eu3+ 302 and Ca3MoO6:Eu3+ 304 phosphors exhibited a CTB edge of 430 nm. This is different than the CTB edge of Y2MoO6:Eu3+ 306, which was 400 nm. The disparity of CTB edge among the phosphor compositions depicted in FIG. 3 is attributed to the crystal structure of Y2MoO6:Eu3+ 306. Y2MoO6:Eu3+ 306 has maximum number of defining lattice parameters for the unit cell, e.g., 4, while the other two phosphors have lattice parameters in the crystal structure of 3 and 1, respectively. Thus, according to one aspect of the present invention, limiting the number of lattice parameters causes the ions to expand the unit cell dimensions. This results in longer bonds, and thus, lower bond energies. For example, a lower Mo6+—O2− bond energy results in a CTB at longer wavelengths.
FIGS. 4-15 show various embodiments of the emission spectra and excitation spectra of phosphor compounds according to exemplary phosphor compositions of the present invention. In FIGS. 6a,b-15, λex represents the monochromatic excitation wavelength used to record the emission spectrum of the phosphor in the wavelength range, as depicted in the figures. In FIGS. 6a,b-13a,b, λem represents the fixed emission wavelength at which the emission intensity was recorded when the phosphor was excited by light in the depicted wavelength range. FIGS. 4-15 will further be described below.
FIG. 4 includes CaMoO4:Eu3+ 402, Y2(MoO3)4:Eu3+ 404, Gd2(MoO3)4:Eu3+ 406, Y2MoO6:Eu3+ 408, Gd2MoO6:Eu3+ 410, Ca3MoO6:Eu3+ 412, Ba2CaMoO6:Eu3+ 414 phosphors for the 615 nm emission wavelength.
FIG. 5 depicts the emission spectra of Ca3MoO6:Eu3+ phosphors with 395 nm 502 and 465 nm 504 excitation wavelengths.
FIGS. 6a, b depict exemplary embodiments of the present invention showing the excitation (FIG. 6a) and Emission Spectra (FIG. 6b) of A2.88MoO6:Eu0.123+ (where A=Mg 602, Ca 604, or Sr 606). FIG. 6a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 6b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 7a, b depict the excitation (FIG. 7a) and emission spectra (FIG. 7b) of A0.88MoO3:Eu0.123+ (where A=Ca 702, Sr 704, Ba 706). FIG. 7a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 7b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 8a, b depict the excitation (FIG. 8a) and emission spectra (FIG. 8b) of A2.58Y2MoO9:Eu0.123+ (where A=Mg 802, Ca 804). FIG. 8a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 8b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 9a, b depict the excitation (FIG. 9a) and emission spectra (FIG. 9b) of Y1.88Mo2O7:Eu0.123+. FIG. 9a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 9b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 10a, b depict the excitation (FIG. 10a) and emission spectra (FIG. 10b) of Ca1.00V2O7:Eu0.123+. FIG. 10a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 10b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 11a, b depict the excitation (FIG. 11a) and emission spectra (FIG. 11b) of Ba1.00Nb2O2:Eu0.123+. FIG. 11a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 11b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 12a, b depict the excitation (FIG. 12a) and emission spectra (FIG. 12b) of Ca2.88V2O7:Eu0.123+. FIG. 12a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 12b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIGS. 13a, b depict the excitation (FIG. 13a) and emission spectra (FIG. 13b) of Na3Y0.88MoO6:Eu0.12. FIG. 13a shows the effectiveness of blue or near-blue LED excitation wavelengths for which the emission wavelength of the phosphor composition is 615 nm (i.e., orange in the visible spectrum). FIG. 13b shows the intensity of the emission wavelengths of the phosphor composition for which the LED wavelength is 400 nm.
FIG. 14 depicts the intensity of the emission spectrum of Sr2.98MoO6:Eu0.023+, excited by a 400 nm LED.
FIG. 15 depicts the intensity of the emission spectrum of Ca2.9WO6:Pr0.13+, excited by a 450 nm LED.
Phosphor compositions 104 according to aspects of the present invention are not limited to converting wavelengths. FIG. 16 depicts a schematic of an LED device 1600 wherein the phosphor composition 104 is agitated by external stimuli 1602. External stimuli 1602 may derive from any one, or more than one, of the following sources: electromagnetic radiation of any wavelength (e.g. x-rays, gamma rays, UV, radio waves, etc.); electrical sources (e.g., electric field); heat sources (e.g., thermal); mechanical sources (e.g. shock waves, acoustic waves, high pressure); magnetic sources (e.g., magnetic field); chemical sources; and biological sources. However, external stimuli 1602 may also derive from sources not listed above. Those skilled in the art will understand the various types of external stimuli 1602 that may be used to agitate a phosphor composition 104.
As a result of the external stimuli 1602, properties of the phosphor composition 104, for example, its refractive index, electrical conductivity, thermal conductivity, magnetic state, etc., may change. These changes may result in changes in the optical absorption, excitation, wavelength conversion, transmission characteristics, etc. of the phosphor composition 104.
If the external stimuli 1602 of the phosphor composition 104 is varied on a periodic basis, the resulting change in the optical properties of the phosphor composition 104 may also be periodic. In addition, the light propagation characteristics through the phosphor composition 104 may also change. Thus, changes in the polarization of light, and the spatial distribution of light transmitted through the phosphor composition, may result. Thus, phosphor compositions 104 according to aspects of the present invention may use the resulting electro-optic, acousto-optic, magneto-optic, and thermo-optic effects to create various devices, e.g., modulators and switches.
While only certain features of the present techniques have been illustrated and described herein, many modifications and changes will occur to those skilled in the art. It is, therefore, to be understood that the appended claims are intended to cover all such modifications and changes as fall within the true spirit of the present techniques.

## Claims

1. A phosphor of formula


(AxAy . . . Az)3−(1+q)m(W1−rMor)O6:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
0≦r≦1;
0≦q≦1;
0<m≦0.12;
A=one or more divalent elements from group IIA and IIB;
W=tungsten with a 6+ charge state;
Mo=molybdenum with a 6+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

2. A phosphor according to claim 1, of formula


Ca2.88MoO6:Eu0.06Na0.06.

3. A phosphor according to claim 1, of formula


(Sr0.4Ca0.2Mg0.1Ba0.2Zn0.1)2.8(Mo0.4W0.6)O6:Eu0.1Li0.1.

4. A phosphor of formula


(AxAy . . . Az)1−(1+q)m(W1−rMor)O3:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
0≦r≦1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
W=tungsten with a 4+ charge state;
Mo=molybdenum with a 4+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

5. A phosphor according to claim 4, of formula


Ca0.80WO3:Eu0.1Na0.1.

6. A phosphor of formula


(AxAy . . . Az)3−(1+q)m(BxBy . . . Bz)2−k(W1−rMor)O9:Lnm+k,Dqm 


wherein,
x+y+ . . . +z=1;
0≦k≦1;
0≦r≦1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
B=one or more trivalent elements from group IIIA, IIIB or one or more rare earth lanthanide elements;
W=tungsten with a 6+ charge state;
Mo=Molybdenum with a 6+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

7. A phosphor according to claim 6, of formula


Mg2.8Y1.5WO9:Eu0.6Na0.1.

8. A phosphor of formula


(AxAy . . . Az)2−m(W1−rMor)2O7:Lnm 


wherein,
x+y+ . . . +z=1;
0≦r≦1;
0<m≦1;
A=one or more trivalent elements from group IIIA, IIIB or one or more rare earth lanthanide elements;
W=tungsten with a 4+ charge state;
Mo=molybdenum with a 4+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

9. A phosphor according to claim 8, of formula


Y1.5Mo2O7:Eu0.5.

10. A phosphor of formula


(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O7:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
p+r+s=1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
V=vanadium with a 5+ charge state;
Nb=niobium with a 5+ charge state;
Ta=tantalum with a 5+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

11. A phosphor according to claim 10, of formula


Ca1.88V2O7:Eu0.06Na0.06.

12. A phosphor according to claim 10, of formula


Sr0.9Ca0.9V0.8Nb1.2O7:Eu0.1Li0.1.

13. A phosphor of formula


(AxAy . . . Az)3−(1+q)m(VpNbrTas)2O8:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
p+r+s=1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
V=vanadium with a 5+ charge state;
Nb=niobium with a 5+ charge state;
Ta=tantalum with a 5+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

14. A phosphor according to claim 13, of formula


Ca2.88Nb2O8:Eu0.06Na0.06.

15. A phosphor according to claim 13, of formula


Sr1.8Ca0.8V2O8:Eu0.2Li0.2.

16. A phosphor of formula


(AxAy . . . Az)2−(1+q)m(BxBy . . . Bz)1−k(VpNbrTas)O6:Lnm+k,Dqm 


wherein,
x+y+ . . . +z=1;
p+r+S=1;
0≦q≦1;
0≦k≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
B=one or more trivalent elements from group IIIA, IIIB or one or more rare earth lanthanide elements;
V=vanadium with a 5+ charge state;
Nb=niobium with a 5+ charge state;
Ta=tantalum with a 5+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
=Oxygen (O2−).

17. A phosphor according to claim 16, of formula


Sr1.88YNbO6:Eu0.06Na0.06.

18. A phosphor of formula


(AxAy . . . Az)3−(1+q)m(VpNbrTas)2O7:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
p+r+s=1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
V=vanadium with a 4+ charge state;
Nb=niobium with a 4+ charge state;
Ta=tantalum with a 4+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

19. A phosphor according to claim 18, of formula


Sr2.8VNbO7:Eu0.1Na0.1.

20. A phosphor of formula


(AxAy . . . Az)2−(1+q)m(VpNbrTas)2O5:Lnm,Dqm 


wherein,
x+y+ . . . +z=1;
p+r+s=1;
0≦q≦1;
0<m≦0.24;
A=one or more divalent elements from group IIA and IIB;
V=vanadium with a 3+ charge state;
Nb=niobium with a 3+ charge state;
Ta=tantalum with a 3+ charge state;
Ln=one or more trivalent rare earth lanthanide elements;
D=one or more monovalent elements from group IA and IB; and
O=Oxygen (O2−).

21. A phosphor according to claim 20, of formula


Mg1.6V2O5:Eu0.2Na0.2.

22. A phosphor of formula


(AxAy . . . Az)3(BxBy . . . Bz)1−m(W1−rMor)6:Lnm 


wherein,
x+y+ . . . +z=1;
0≦r≦1;
0<m≦0.48;
A=one or more monovalent elements from group IA and IB;
B=one or more trivalent elements from group IIIA, IIIB or one or more rare earth lanthanide elements;
W=tungsten with a 6+ charge state;
Mo=molybdenum with a 6+ charge state;
Ln=one or more trivalent rare earth lanthanide elements; and
O=Oxygen (O2−).

23. A phosphor according to claim 22, of formula


Na3Gd0.7MoO6:Eu0.3.

24. A light emitting device, comprising:
a source for ultraviolet or visible radiation;
power leads for providing current to the source that causes the source to emit radiation; and
a phosphor as in claim 1 for converting at least a portion of the emitted radiation by the source into radiation having a longer wavelength.

25. A light modulating device, comprising:
a source for ultraviolet or visible radiation;
power leads for providing current to the source that causes the source to emit steady or time varying radiation; and
a phosphor as in claim 4 for converting at least a portion of the emitted radiation by the source into radiation having longer wavelength, wherein the phosphor having optical, electrical, thermal, mechanical, chemical, biological or magnetic properties can be temporally or spatially varied to alter or modulate the temporal or spatial light emission characteristics.