# Patent

## Title
Process for producing a thermostable TiO2/SiO2 mixed oxide and mixed oxide produced therefrom

## Abstract

The present invention relates to a process for preparing TiO2/SiO2 mixed oxides or the hydrates and/or oxide hydrates thereof comprised of 0.5 to 95 wt % SiO2 and the balance as TiO2, each referring to the completely calcined product, by using titanium alcoholates and aqueous silica sol. Moreover, the invention relates to the use of these mixed oxides as catalyst carriers.

## Background
CROSS REFERENCE TO RELATED APPLICATION
This application claims priority from German Patent Application No. DE102005021623.4 filed on 4 May, 2005, the disclosure of which is incorporated herein by reference for all purposes.
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a process for preparing a thermostable catalyst carrier based on TiO2/SiO2 mixed oxides comprised of 0.5 to 95 wt % SiO2 and the balance as TiO2, each referring to the completely calcined product.
2. Description of the Prior Art
Supported catalysts have economically been very important for a long time and make up the largest tonnage among the heterogeneous catalysts. They are used among others for working up fossil raw materials, upgrading intermediates, and making new chemical products. Owing to the worldwide increasing concern for the environment and the legal requirements in connection therewith, these catalysts have also rapidly gained importance for the emission control of exhaust gas.
For example, in industrial countries power stations and automobiles utilising fossil fuels are only approved if they are provided with appropriate supported catalysts for controlling emissions. Said supported catalysts are employed for denitrating (DeNOx) and desulphering flue gases and cleaning the exhaust gases of automobiles.
Conventional catalyst carriers for these applications are porous powders or moulded articles based on Al2O3, SiO2, MgO, TiO2, and ZrO2. In modern processes, e.g. for cleaning exhaust gases, metallic or ceramic honeycombs coated with oxidic carrier materials are increasingly employed. The catalyst carrier or honeycomb coating has the function among others to enlarge the surface of the active component because the catalyst activity usually increases as the catalyst surface increases.
Naturally, the metal oxides used as carriers, such as Al2O3, SiO2, MgO, TiO2, and ZrO2 have different properties, e.g. with regard to possible surfaces, pore volumes, acidity, and chemical inertia. Among these metal oxides TiO2 is known for being chemically inert and, consequently, for being especially suitable as a catalytic converter utilised for detoxifying aggressive gases containing e.g. SOx or NOx at high temperatures.
Conventional TiO2 materials available on the market have the disadvantage that they have small surfaces and pore volumes so that their use is limited. These commercially available catalyst carriers based on titanium dioxide are mostly produced by precipitation reactions of titanium-containing salts or by flame pyrolysis. When using the latter method with TiCl4, titanium dioxide is obtained, which consists of a crystalline mixed phase (anatase/rutile, approx. 70%/30%) presenting a surface of approx. 58 m2/g (commercial product e.g. Degussa P 25). When using hydrolysis and calcination with titanium tetra(isopropylate), the resultant titanium dioxide, too, is comprised of a crystalline mixed phase having a surface of 106 m2/g.
Among the three natural varieties of TiO2 (anatase, brookite, rutile) rutile exhibits the highest thermodynamic stability. Rutile is not in demand as a catalyst but is rather employed in large quantities as a white pigment. For catalytic uses anatase is the appropriate variety. Anatase readily converts into rutile at temperatures above 600° C., and thus is of no use for catalysis.
Today pure-phase catalyst carriers based on TiO2 are preferred for heterogeneous catalysis. Said carriers are to have large surfaces and as few disturbing anions (e.g. SO42− or Cl−) as possible, i.e. less than 250 ppm.
The alkali content, especially sodium and potassium, and the alkaline-earth content, especially calcium and magnesium, should be less than 50 ppm each, whereas the iron content should be less than 100 ppm so that the effectiveness of the catalytically active phase when subject to heat is not destroyed by the labile chemical lattice defects.
SUMMARY OF THE INVENTION
It is the object of the present invention to provide a simple process for preparing high-purity, thermostable catalyst carriers comprising TiO2 in the anatase phase within the aforesaid limits.
It is particularly intended to avoid intricate pretreatment of the starting materials or elaborate aftertreatment of the TiO2/SiO2 mixed oxides or suspensions thereof.
It is preferable that the catalyst carrier material has the following features in particular:

    
    
        a large surface with the catalytically active anatase as the main phase
        a high pore volume associated with the catalytically active anatase as the main phase
        a high thermostability of the carrier in order to prevent transformation of the catalytically active anatase to rutile so that the durability/stability of the carrier is increased as few chemical impurities as possible.
    
    


The problem described hereinbefore can be solved by a process according to the independent claims stated hereinbelow. The preferred embodiments of the subject invention are set out in the subordinate claims or below.



BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 shows the x-ray diffraction pattern (XRD) of TiO2 prepared by hydrolysis of titanium tetra(isopropylate) in the presence of oxalic acid.
FIG. 2 shows the x-ray diffraction pattern of TiO2 prepared by hydrolysis of titanium tetra(hexanolate) in the presence of ammonium bicarbonate.
FIG. 3 shows the x-ray diffraction pattern of TiO2/SiO2 (90 wt %:10 wt %) prepared by hydrolysis in the presence of 2 wt % ammonium bicarbonate after hydrothermal aging; and
FIG. 4 shows the x-ray diffraction pattern of TiO2/SiO2 (89 wt %:11 wt %) at different temperatures.



DESCRIPTION OF THE PREFERRED EMBODIMENTS
It has surprisingly been discovered that when using titanium alcoholate as titanium component and silicic acid purified on cation-exchange resins yielding silica sol as SiO2 source, useful catalyst carriers are obtained. In this process the titanium alcoholate is hydrolysed, preferably with deionised water, and the silica sol purified on cation-exchange resins is added simultaneously, partially simultaneously, or subsequently.
The process of the invention comprises the reaction of a titanium compound having at least one C1- to C16-alcoholate group in an aqueous medium with a silicic acid compound, followed by drying or calcination of the resultant product. It is preferable to use deionised water for the hydrolysis and to add the silicic acid purified on cation-exchange resins simultaneously or subsequently.
The resultant TiO2/SiO2 mixed oxide is comprised of 0.5 to 95 wt % SiO2 and the balance as TiO2, each referring to the completely calcined product. It has been found that with less than 60 wt % SiO2 the mixed oxides do not comprise the rutile phase but comprise the catalytically active anatase variety, whereas with a SiO2 content of greater 90 wt % the mixed oxides are usually amorphous according to x-ray analysis.
Preferably, the reaction product then is calcined at >550° C. for at least 30 minutes (mean time). The products were calcined at 550° C. to 1,100° C. during 30 minutes to 24 hours.
Owing to the isomorphous incorporation of the silicic acid nanoparticles (average size 1.8 to 9.3 nm by Sears titration) when using the process of the invention, catalyst carriers with a homogenous distribution of TiO2 and SiO2 are obtained. The specific surface of the carriers is in the range from 100 to greater 725 m2/g, depending on the SiO2 content, and their surface stability is excellent. Surprisingly, the main phase of the mixed oxides exposed to calcination (3 h/550° C.) ranges from anatase to amorphous (with 90% SiO2) as the SiO2 content increases. No rutile has been found.
After calcination at 1,100° C. for 24 hours (stability test), depending on the SiO2 content, the carriers prepared according to the process of the invention have a surface stability of up to 240 m2/g (e.g. with 60% SiO2) so that the expected durability and service life make them very useful as catalyst carriers for example in combustion processes or exhaust-gas cleaning processes.
Furthermore, the chemical purity of the catalyst carriers described herein is advantageous on account of their low content of iron (especially if less than 25 ppm), sodium (especially if less than 25 ppm), potassium (especially if less than 50 ppm), calcium (especially if less than 25 ppm), magnesium (especially if less than 25 ppm), zinc (especially if less than 25 ppm), nickel (especially if less than 10 ppm), and of sulfate and chloride, especially if each is less than 200 ppm, and even with carriers containing as much as 95 wt % SiO2. After calcination, i.e. exposure to a temperature of above 550° C., these carriers have a total purity of >99.9 wt %, based on the TiO2/SiO2 ratio to the total oxidic mass. These catalyst carriers are defined as high-purity carriers within the meaning of this invention.
According to the process of the invention, titanium alcoholates having at least one alcoholate group, which can be a blend of alcoholates or just one alcoholate, are used. These alcoholates can be produced for example from titanium compounds and alcohols or by transesterification of commercially available titanium tetra(isopropylate).
The titanium alcoholates are either hydrolysed with deionised water while simultaneously adding thereto silicic acid purified on cation-exchange resin, preferably in quantities from 0.1 to 8.0 wt %, or the TiO2/water mixture obtained after the hydrolysis with deionised water is mixed with silica solution purified on cation-exchange resin in quantities from 0.1 to 8.0 wt %. After the hydrolysis a hydrothermal aging procedure may be carried out in one or several steps for at least 1 hour at temperatures from 90 to 235° C., wherein each step may be performed at a different temperature.
A special advantage of the process of the invention over conventional TiO2-based materials obtained by precipitation reaction or flame pyrolysis is the optimal chemostructural incorporation of the isomorphous SiO4 building blocks into the TiO2/water phase by means of silicic acids obtained by cation exchange. It is favourable to use a stirred reactor, e.g. as defined in DE-3823895, while taking into consideration that the stirrer speed influences crystal and pore size. A static mixer may be used as well. The hydrothermal aging is carried out at temperatures from 70 to 235° C., especially 90° to 210° C. It is performed prior to drying or calcination, preferably under pressure for example in an autoclave.
An analysis of the chemical impurities of the products of the invention has shown that the following threshold values are not exceeded:














Iron (<25 ppm)
Sodium (<25 ppm)
Potassium (<50 ppm)


Calcium (<25 ppm)
Magnesium (<25 ppm)
Zinc (<25 ppm)


Nickel (<10 ppm)
Chloride (<200 ppm)
Sulfate (<200 ppm)









These compounds are defined as high-purity within the meaning of this invention.
The same applies to pure titanium dioxide (cf. Examples 1 and 2). The anions, which are inherent when using mineral acids and organic acids in the hydrolysis, have not been determined because they decompose after calcination of the carrier substances, e.g. at 550° C. for 3 hours. Most anions do not produce lattice defects in the titanium dioxide products or mixed oxides of the invention. Not so the anions chloride and sulfate.
Titanium Dioxides from Titanium Alcoholates, Effects of Aging and Aging Additives
Examples 1 and 2 show the behaviour of pure titanium dioxide obtained by hydrolysis of different titanium alcoholates in the presence of various chemical hydrolysis additives. The physical data of these titanium dioxides have been compared with the mixed oxides of the invention.
Titanium dioxides which have not been exposed to hydrothermal aging have comparatively small pore volumes and surfaces, e.g. a pore volume of 0.11 ml/g and a surface of 54 m2/g in the case of titanium tetra(2-ethylhexanolate) (see Table 1). However, when subjecting titanium dioxide suspensions, which have been freed from the reaction alcohol, to hydrothermal aging, the pore volume is significantly higher (0.34 ml/g) and the surface is larger (80 m2/g) (see Table 2). Irrespective of the titanium alcoholate used, these improvements of the physical properties are brought about at a neutral pH value (e.g. with water), at an acidic one (e.g. in the presence of leucine or HNO3), and at a basic pH value (e.g. in the presence of NH3 or NH4HCO3) (cf. Example 2). However, the hydrothermal aging step has not brought about pore volumes of greater 0.38 ml/g in any of the all-TiO2 products comprising anatase in the main phase (see Example 2).
In crystallographic aspects it is interesting to note that the crystalline main phase of the pure titanium dioxides of Examples 1 and 2 is mostly anatase, occasionally with small amounts of Brookite, but with the following exceptions:

    1. When the hydrolysis medium contained oxalic acid, amorphous anatase was obtained without aging. The anatase then transformed to rutile by subsequent hydrothermal aging (see FIG. 1).
    2. When the hydrolysis medium contained ammonium bicarbonate, amorphous TiO2 was obtained without aging. The TiO2 then was transformed to the all-anatase phase by subsequent calcination at 550° C. (see FIG. 2).

Influence of the SiO2 Content in a Mixed Oxide Prepared with Hydrolysis of Titanium Alcoholates; Comparison Between Co-Hydrolysis and Slurry Doping



According to the process of the invention including co-hydrolysis, wherein the titanium alcoholate is hydrolysed in the presence of silicic acid, the TiO2/SiO2 ratio in the catalyst carrier is adjusted by reducing or increasing the silicic acid quantity and adjusting the alcoholate feed without changing the total quantity of reactants.
It has been found that in contrast to TiO2 prepared by hydrolysis of titanium alcoholates, larger surfaces and higher pore volumes are obtained, irrespective of the titanium alcoholate used, when increasing the SiO2 quantity (see Example 3).
It is particularly remarkable that even very small quantities of SiO2 added in the form of the silicic acid mentioned hereinabove (>1.4% solids), larger surfaces (>140 m2/g) are obtained (cf. All TiO2 having a maximum surface of 83 m2/g) (see Example 1, Table 1, Example 3, and Table 4).
Looking at the surface values as a function of the hydrolysis temperature (25° C. and 70° C.) and an increasing SiO2 content, it becomes apparent that the values found at 25° C. and with a SiO2 content of approx. 30% reach a maximum of about 220 m2/g and then decline. At 70° C. the surface increases much more and reaches about 250 m2/g with a SiO2 content of only approx. 20%. Surprisingly, the surface continues to increase as the SiO2 content increases and reaches about 550 m2/g with a SiO2 content of approx. 90%.
In a binary mixed-oxide system comprising TiO2 and SiO2 these values are expected to increase only linearly. The increase is supposed not to exceed the values of the starting components in proportion to their quantities, e.g. 100% TiO2 (surface: 83 m2/g; pore volume: 0.22 ml/g) and 100% SiO2 prepared from silicic acid (surface: 345 m2/g; pore volume: 0.08 ml/g).
Consequently, the surprising result is the overproportionate increase in surface, which reaches a maximum of about 550 m2/g in the case of titanium tetra(isopropylate) and a hydrolysis temperature of 70° C. (cf. Table 4) at a TiO2/SiO2 mixed-oxide ratio of approx. 10:90 (wt %:wt %). This result exceeds the calculated value by 37% (at a TiO2/SiO2 mixed-oxide ratio of 10:90=(83 (m2/g):10)·1+(345 (m2/g):10)·9=319(m2/g)).
Another surprise is the overproportionate increase in pore volume, which reaches a maximum of 0.46 ml/g in the case of titanium tetra(isopropylate) and a hydrolysis temperature of 70° C. (cf. Table 4) at a TiO2/SiO2 mixed-oxide ratio of approx. 90:10. This result exceeds the calculated value by 120% (at a TiO2:SiO2 mixed-oxide ratio of 90:10=(0.22 (ml/g):10)·9+(0.08 (ml/g):10)·1=0.21 (ml/g)).
The co-hydrolysis of silicic acid and titanium alcoholates and the slurry-doping method (at first hydrolysis of the titanium alcoholates, followed by addition of silicic acid) have revealed that surface and pore volume increase overproportionately as the SiO2 content increases. Comparing co-hydrolysis (Example 3) and slurry doping (Example 4), similar results are obtained at a low SiO2 content (less than 20 wt %). From a SiO2 content of 20% it has surprisingly been found that the unexpectedly high surface and pore volume values reached by co-hydrolysis are even topped by slurry doping. For example, with a SiO2 content of approx. 10% a pore volume maximum of 0.46 ml/g is reached by co-hydrolysis, whereas at a SiO2 content of approx. 20% the pore volume increases to 0.67 ml/g by slurry doping. It has thus been demonstrated that the unexpected physical properties of the catalyst carriers of the invention are displayed both with co-hydrolysis and slurry doping.
The physical data of the mixed oxides show that surface and pore volume increase as the SiO2 content increases. Surprisingly, this behaviour is in the main independent of the titanium alcoholate used. It has thus been proved that both water-miscible alcohols and water-immiscible ones are suitable substitutes for the titanium alcoholates used for hydrolysis.
In addition to the process selected from the two different processes for preparing TiO2/SiO2 mixed-oxide catalysts, the SiO2 quantity, the hydrolysis temperature, and the temperature and duration of hydrothermal aging exert influence on surface and pore volume.
Crystal Structures
It can be proved by x-ray diffraction that, regardless whether co-hydrolysis or slurry doping is the method of choice, similar crystal structures are formed in the catalyst carriers at comparable TiO2:SiO2 ratios. In crystallographic aspects it is interesting that the crystalline main phase of the TiO2/SiO2 mixed-oxides is mostly anatase, optionally with small amounts of brookite (cf. Examples 4 to 6). However, it is surprising that for example by addition of 2 wt % ammonium bicarbonate to the hydrolysis water and with a TiO2:SiO2 ratio of about 90:10 a TiO2/SiO2-mixed oxide comprising the TiO2 as all anatase is obtained after hydrothermal aging at 210° C. for 5 hours (cf. Table 8, FIG. 3).
The crystallite size of unaged mixed oxides normally ranges from 5 to 12 nm (determined on the 101 reflex) and from 5 to 11 nm (measured on the 200 reflex).
Influence of Aging After Co-Hydrolysis or Slurry Doping
When comparing the products prepared by co-hydrolysis or slurry doping after hydrothermal aging, it has been found that the surfaces obtained by co-hydrolysis tend to be slightly larger than by slurry doping, the SiO2 content being the same (see Table 8). On the contrary, slightly higher pore volumes are obtained by the slurry doping process variant. So, the two processes are complementary.
Influence of the Hydrothermal Aging Temperature
The influence of the hydrothermal aging temperature on the physical properties of the novel mixed oxides is seen when taking a close look at the surfaces of mixed oxides containing for example approx. 20% SiO2 after aging at 90° C. versus 210° C. It has been found that the surface decreases as the temperature increases (see Table 8). In the case of co-hydrolysis the surface decreased from 294 to 205 m2/g, whereas in the case of slurry doping the value dropped from 282 to 156 m2/g. The pore volumes, however, increased unexpectedly at high hydrothermal aging temperatures (e.g. 210° C.). For example, the pore volume of the mixed oxides containing approx. 20% SiO2, which were prepared by the co-hydrolysis method, increased from 0.44 ml/g after hydrothermal aging at 90° C. to 1.14 ml/g after hydrothermal aging at 210° C. The same has been observed with the slurry doping process, although to a lesser extent, namely from 0.67 to 0.93 ml/g with a SiO2 content of approx. 20%. So, these surprising results have been found with either process variant.
In summary it has been discovered that by raising the hydrothermal aging temperature after co-hydrolysis to >90° C., particularly >150° C., the pore volumes increase considerably so that TiO2/SiO2 mixed oxides having pore volumes of >1.0 ml/g can be prepared. To top it all, these products are comprised of >95 wt % anatase.
Influence of the Stirrer Speed on Hydrothermal Aging
When examining the influence of the mechanical energy input at constant aging conditions on the product properties, which is described by the stirrer circumferential velocity, it has been found that the surface remains unchanged with an increasing stirrer circumferential velocity, whereas the pore volume increases steadily (cf. Table 9).
Influence of the SiO2 Source (Hydrolysed Siloxanes vs. Silicic Acid)
Silicic acid is released in an aqueous-ethanolic phase by acid-catalysed hydrolysis of silicic acid esters, such as tetraethoxysilane (TEOS), with addition of water. In the presence of titanium alcoholates a SiO2/TiO2 mixed oxide is formed because the two hydrolysis steps are carried out simultaneously.
The physical data of the mixed oxides reveal the same relations as already described hereinabove in connection with the products prepared by co-hydrolysis. Pore volume and surface increase as the SiO2 content increases. However, when comparing the absolute values of mixed oxides prepared by hydrolysis of TEOS with products prepared according to the process of the invention, it has become apparent that their surface or pore volume or both are lower.
For example, a mixed oxide prepared by hydrolysis of TEOS and containing approx. 10 wt % SiO2 was found to have a pore volume of 0.41 ml/g and a surface of 213 m2/g, whereas silicic acid prepared by means of ion-exchange resin (see Table 4) resulted in a pore volume of 0.46 ml/g and a surface of 232 m2/g.
The difference between these two SiO2 sources is even more pronounced, when comparing the results of hydrothermal aging at 210° C. after hydrolysis of TEOS (see Example 8) versus the process of the invention (see Example 6). A pore volume of 0.61 ml/g and a surface of 168 m2/g were obtained with approx. 10 wt % SiO2 in the mixed oxide (cf. Table 11), whereas according to Table 8, pore volume and surface were found to be 0.94 ml/g and 182 m2/g, respectively.
The indispensable addition of acid needed to release silicic acid e.g. from TEOS has probably an unfavourable effect.
Influence of the Silicic Acid Age
Silicic acids are also commercially available, e.g. LEVASIL 500 (pH 9.3; sodium content: 420 ppm). The threshold values for impurities are within the specified limits.
When using LEVASIL 500 for the hydrolysis of the titanium alcoholates, pore volume and surface of unaged and aged products are comparable. However, similar observations as in Example 8 were made and the advantages of the present invention have not become evident in the hydrolysis of titanium alcoholates with LEVASIL 500 either.
Thermostability
Catalyst carriers in use are frequently exposed to high temperatures. The maximum temperature a catalyst carrier can withstand without damage differs with its application.
For catalytic converters a process of measuring the thermostability has become generally accepted. The capability of the carrier surface to resist changes is assessed by long-time exposure (e.g. 3 or 24 hours) to a temperature which is typical of the particular application. Normally, the carrier surface of modern feedback catalytic converters used e.g. in Otto engines is supposed to preserve a surface of at least 50 m2/g after 24 hours at 1,100° C. On the contrary, catalyst carriers for Diesel engines need to resist considerably lower temperatures (e.g. 3 hours at 800° C.).
It has been found (cf. Table 13) that the thermostability is already remarkable from a SiO2 content of 5 wt % so that the requirements are fulfilled by catalyst carriers designed for use at lower operating temperatures. The thermostability increases as the SiO2 content increases so that with a SiO2 content of >20 wt % the catalyst carriers are suitable both for low and high operating temperatures.
When comparing the surface of the TiO2/SiO2 mixed-oxide catalyst carrier with the requirements made on catalytic converters, the economic and technical potentialities of the novel carrier material are sensational.
Phase Change
The data compiled in Tab. 14 show that the measures described hereinbelow or a combination thereof obviously have a favourable effect on the phase change from anatase to rutile allowing higher temperatures:

    
    
        1. quantity of SiO2 added to the mixed oxide
        2. temperature and duration of aging of the mixed oxide
        3. addition of chemicals at least during hydrolysis of the titanium alcoholates
    
    


The temperature at which rutile is formed (Trutile) from pure TiO2 (100/0) (hydrolysis of titanium tetra(isopropylate) at 70° C. in water) is 680° C. (see Tab. 14). When the hydrolysis is carried out with a higher quantity of fresh silicic acid obtained by cation exchange (co-hydrolysis), the rutile formation temperature Trutile of mixed oxides containing 11% SiO2 shifts to 1,080° C. This phase-change temperature increase of 400° C. is exceptionally high. By addition of the SiO2 quantity e.g. to 53.8% the rutile formation temperature was found to increase further by 80° C. to 1,160° C.
On closer examination of TiO2/SiO2 mixed oxides having a mixing ratio of approx. 90:10 it becomes apparent (cf. Tab. 14) that a rutile phase change at higher temperatures can also be brought about by hydrothermal aging of the TiO2/SiO2 mixed oxides e.g. at 90° C. or 210° C., whereby the phase-change temperature is raised by at least 380° C.
The increase in the rutile phase-change temperature can be influenced by the chemicals added during hydrolysis of the titanium alcoholates (cf. Tab. 14). The temperature increases by 490° C. when the TiO2/SiO2 mixed oxide is prepared by addition of silica sol to TiO2 slurry containing NH4HCO3 and subsequent aging at 210° C. for 4 hours (Trutile=1,250° C.).
The present invention will be illustrated by reference to the following figures:
FIG. 1 shows the x-ray diffraction pattern (XRD) of TiO2 prepared by hydrolysis of titanium tetra(isopropylate) in the presence of oxalic acid, the unaged sample (cf. Example 1) is depicted below in the figure, whereas the hydrothermally aged sample (210° C./5 h) is depicted above (cf. Example 2).
FIG. 2 shows the x-ray diffraction pattern of TiO2 prepared by hydrolysis of titanium tetra(hexanolate) in the presence of ammonium bicarbonate. The uncalcined sample (cf. Example 1) is depicted below in the figure, whereas the sample calcined at 550° C. is depicted above.
FIG. 3 shows the x-ray diffraction pattern of TiO2/SiO2 (90 wt %:10 wt %) prepared by hydrolysis in the presence of 2 wt % ammonium bicarbonate after hydrothermal aging (210° C./5 h) (cf. Table 8).
FIG. 4 shows the x-ray diffraction pattern of TiO2/SiO2 (89 wt %:11 wt %) at different temperatures (for the mixed-oxide preparation, cf. Table 14: Co-hydrolysis of TiIP with silicic acid at 70° C.; aging: 90° C./5 h).
Experiments
Analyses
The trace elements content in the compounds of the invention was determined by inductively coupled plasma atomic emission spectroscopy (AES-ICP) (spectrometer manufacturer: SPECTRO).
The surface of the pure oxides or TiO2/SiO2 mixed oxides was measured by N2-sorption according to BET (see DIN 66131, apparatus: Autosorb 6 of Micromeretics company).
The pore volume was determined by nitrogen porosimetry (see DIN 66134, apparatus: Autosorb 6 of Micromeretics company) and/or mercury penetration (intrusion volume) (see DIN 66133, porosimeter: Autopore IV of Micromeretics company, contact angle: 131°).
The compounds of the invention were calcined in a muffle furnace at temperatures from 550° C. to 1,100° C. Deionised water was used for hydrolysis.
The x-ray diffraction pattern were measured by means of an apparatus (D 5000) from Siemens (angle range: 2 theta=2 to 75° in increments of 0.035°; measurement time: 1 s/°) using Cu as anode material at a wave length of 1.54051 Å.
The crystallite size was determined on the 101- and 200-reflexes of the anatase phase by means of the Scherrer formula:

crystallite size=(K·lambda·57.3)/(beta·cos theta)

    
    
        where:
        K (form factor): 0.992
        lambda (x-ray wave length): 0.154 nm
        beta (corrected apparatus line broadening): dependent on the reflex
        theta: dependent on the reflex
    
    


The silicic acid particle size of the silica sol was determined by Sears titration (G. W. Sears, Anal. Chemistry 12, 1956, pp. 1982-83).
The viscosities were measured by means of a Brookfield viscometer (DV-II, measuring element 1).
The temperature of the phase-change from anatase to rutile was measured by x-ray diffraction (XRD) using a high-temperature diffractometer (HDK S1 from Bühler) in the atmosphere of air. The measurements were carried out at temperatures from 500 to 1,250° C., depending on the sample. The heating rate was 10° C./min up to the first measurement point. The diffraction then was recorded at stagnant temperature in a 2-theta range from 21 to 29° in increments of 0.02° with a measurement time of 2 seconds per increment. Then the temperature was raised by 20° C. in increments of 10° C./min. The diffraction was recorded by means of a theta/theta diffractometer (manufacturer: Seifert company, Ahrensburg) in a diffraction geometry of parallelised Cu—Kα radiation. The resolution was found to be approx. 0.08° in 2 theta, measured on the standard Al2O3.
The excitation conditions were 40 kV and 35 mA. The detector was a scintillation counter. Prior to the measurements, the temperature was calibrated by recording the phase transformation of Ag2SO4 at 427° C. and of molten KCl and K2SO4 at 776° C. and 1,069° C. resp. Heating rate and measurement were controlled using the Rayflex software (x-ray diffraction software from Seifert).
By the term ‘rutile phase-change temperature’ as used herein is meant the temperature at which an intensity supposed to be rutile is measurable for the first time by x-ray diffraction (start of rutile formation). An example is illustrated in FIG. 4 showing a rutile formation temperature of 1,080° C.
Chemicals
Titanium Component (Titanium Alcoholates)
The titanium component used herein was commercially available high-purity titanium tetra(isopropylate) (TiIP) (e.g. from Synetix, Billingham (UK) or Nippon Soda, Tokio (Japan)). The TiIP had a melting point from 16.7 to 17.9° C. The titanium content was in the range from 16.5 to 17.0 wt %. The chemical purity with respect to the content of iron and chloride was 1 to 2 ppm and 6 to 18 ppm, resp. The other titanium alcoholates referred to herein were obtained by reaction of TiIP with the corresponding alcohols (see below).
Silicon Component (Silica Sols)
The silica sols were prepared by exchanging the sodium ions of a silicate solution for protons by means of acidic ion-exchange resins (cation-exchange resins). To this end commercially available sodium silicate solution (e.g. containing 28 wt % SiO2; from PQ Germany GmbH) was diluted with deionised water so that the SiO2 content was approx. 3 to 4 wt %. The solution then passed a column packed with ion-exchange resins, which had been packed before with a regenerated commercial cation-exchange resin (e.g. Lewatit S 100 marketed by Bayer or SYBRON Chemicals Inc., Pittsburgh, USA) and, prior to the exchange procedure, had been rinsed with deionised water until the conductivity of the eluate was less than 5 microS/cm. The cation exchange takes place according to the following reaction equation:

Na4SiO4+4H+→H4SiO4+4Na+

The eluate contains fresh silica sol having a pH of approx. 3.5. This sol contains approx. 3 to 4% SiO2, depending on the batch, and has a low sodium content of less than 10 ppm. It was used in the experiments described hereinbelow. The exhausted cation-exchange resin was regenerated according to the manufacturer's instructions, i.e. by repeated washing with a 10% hydrochloric acid solution.
Fresh silica sol was prepared by using a commercially available cation-exchange resin. As used herein, the term ‘fresh’ means that the silica sol has a low degree of oligomerisation, which can be estimated on the basis of the particle size (in nm) determined by the Sears titration described hereinabove. The fresh silica sol prepared by cation exchange (pH 3.6) had a particle size of 1.8 nm according to Sears titration and the viscosity was less than 10 mPas. The oligomerisation degree increases with time (measurable by Sears particle size). For example, 4 hours after preparation the silica sol particle size was found to be 2.4 nm, whereas after 24 hours a particle size of 2.8 nm was measured and the viscosity still was less than 10 mPas.
It has been discovered that the silicic acid nanoparticles prepared in this way are particularly suitable for the reaction described herein because of their surprisingly high reactivity among other things.
Example 1
Titanium Dioxide
Comparative Experiment with and without Hydrothermal Aging
In a stirred reactor suspensions were prepared from pure TiO2 by hydrolysis of titanium alcoholates having a titanium content from 16.8 to 4.5 wt % (see Table 1). As for titanium tetra(isopropylate) (TiIP, 16.8 wt % Ti) for example, the hydrolysis was carried out continuously with 45 kg of TiIP and 135 kg of deionised water at temperatures ranging from 30 to 90° C. and during 30 to 60 minutes. The hydrolysis proceeded in a basic medium as well as in a neutral and an acidic one. For the acidic part of the hydrolysis aqueous solutions of various mineral acids or organic acids were employed.
The resultant suspension then was subjected to azeotropic steam distillation in order to remove the alcohol released during hydrolysis and, thereafter, it was dried in a spray drier at an air-outlet temperature from 100 to 130° C. The carbon content in the resultant solids was less than 0.2 wt %, and the solids content in the products thus prepared was in the range from 75 to 85 wt % (determined by DTG, end point 1,000° C.).
The titanium alcoholates used herein included titanium tetra(isopropylate) (TiIP with 16.8 wt % Ti), titanium tetra(2-ethylhexanolate) (TiEtHex with 8.5 wt % Ti), titanium tetra(butanolate) (TiBut with 8.5 wt % Ti), titanium tetra(2-ethylbutanolate) (TiEtBut with 8.5 wt % Ti), titanium tetra(hexanolate) (TiHex with 9.5 wt % Ti), and titanium tetra(2-butyloctanolate) (TiButOct with 4.5 wt % titanium). The alcoholate/water mass ratio was overstoichiometric (water excess). The physical data of the resultant TiO2 have been compiled in Table 1.







TABLE 1







PHYSICAL DATA OF THE TiO2 CATALYST CARRIERS OF EXAMPLE 1


(WITHOUT HYDROTHERMAL AGING)














Hydrolysis

Pore




Hydrolysis
Temp.
Surface
Volume


Alcoholate
Medium
[° C.]
[m2/g]1)
[ml/g]2)
Crystal Structure3)















TiIP
Water
30
60
0.16
Anatase/Brookite


TiIP
Water
70
60
0.15
Anatase/Brookite


TiIP
NH3 (0.2%)
70
59
0.23
Anatase/Brookite


TiIP
HNO3 (0.2%)
70
52
0.14
Anatase/Brookite


TiIP
HCOOH (0.65%)
70
59
0.14
Anatase/Brookite


TiIP
CH3COOH (0.2%)
70
58
0.22
Anatase/Brookite


TiIP
Oxalic acid (1.25%)
70
22
0.08
Amorphous (Anatase)


TiIP
Leucine (1.0%)
70
85
0.14
Anatase/Brookite


TiEtHex
NH3 (0.2%)
90
54
0.11
Amorphous







(Anatase/Brookite)


TiEtHex
HNO3 (0.2%)
90
46
0.10
Anatase/Brookite


TiBut
NH3 (0.2%)
70
33
0.26
Anatase/Brookite


TiBut
HNO3 (0.2%)
70
52
0.12
Anatase/Brookite


TiEtBut
NH3 (0.2%)
70
38
0.07
Amorphous







(Anatase/Brookite)


TiEtBut
HNO3 (0.2%)
70
54
0.10
Anatase/Brookite


TiHex
NH4HCO3 (2%)
30
33
0.14
Amorphous


TiHex
NH3 (0.2%)
70
23
0.19
Amorphous







(Anatase/Brookite)


TiHex
HNO3 (0.2%)
70
49
0.08
Anatase/Brookite


TiButOct
NH3 (0.2%)
70
79
0.26
Anatase/Brookite


TiButOct
HNO3 (0.2%)
70
47
0.09
Anatase/Brookite





Legend:


TiIP titanium tetra(isopropylate)


TiEtHex titanium tetra(2-ethylhexanolate)


TiBut titanium tetra(butanolate)


TiEtBut titanium tetra(2-ethylbutanolate)


TiHex titanium tetra(hexanolate)


TiButOct titanium tetra(2-butyloctanolate)


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products (for low-crystalline amorphous products the crystal phase is put in brackets)






Example 2
Titanium Dioxide
Comparative Experiment with Hydrothermal Aging
The experiment was carried out as described in Example 1, the difference being that the TiO2 suspensions obtained after the synthesis were subjected to aging at different temperatures and during varying periods of time before they were spray-dried. The physical data of the resultant TiO2 have been compiled in Table 2.







TABLE 2







PHYSICAL DATA OF THE TiO2 CATALYST CARRIERS OF EXAMPLE 2


(WITHOUT HYDROTHERMAL AGING (5 h/210° C.))














Hydrolysis

Pore




Hydrolysis
Temperature
Surface
Volume


Alcoholate
Medium
[° C.]
[m2/g]1)
[ml/g]2)
Crystal Structure3)















TiIP
Water
30
88
0.30
Anatase/Brookite


TiIP
Water
70
78
0.38
Anatase/Brookite


TiIP
NH3 (0.2%)
70
85
0.30
Anatase/Brookite


TiIP
HNO3 (0.2%)
70
72
0.22
Anatase/Brookite


TiIP
HCOOH (2.5%)
70
70
0.24
Anatase/Brookite


TiIP
CH3COOH (3.3%)
70
75
0.23
Anatase/Brookite


TiIP
Oxalic acid (1.4%)
70
43
0.44
Rutile


TiIP
Leucine (1.0%)
70
87
0.24
Anatase/Brookite


TiEtHex
NH3 (0.2%)
90
80
0.34
Anatase/Brookite


TiEtHex
HNO3 (0.2%)
90
67
0.22
Anatase/Brookite


TiBut
NH3 (0.2%)
70
81
0.29
Anatase/Brookite


TiBut
HNO3 (0.2%)
70
89
0.26
Anatase/Brookite


TiEtBut
NH3 (0.2%)
70
71
0.23
Anatase/Brookite


TiEtBut
HNO3 (0.2%)
70
82
0.31
Anatase/Brookite


TiHex
NH4HCO3 (2%)
30
33
0.14
Amorphous


TiHex
NH3 (0.2%)
70
72
0.25
Anatase/Brookite


TiHex
HNO3 (0.2%)
70
62
0.19
Anatase/Brookite


TiButOct
NH3 (0.2%)
70
87
0.22
Anatase/Brookite


TiButOct
HNO3 (0.2%)
70
69
0.21
Anatase/Brookite





Legend:


TiIP titanium tetra(isopropylate)


TiEtHex titanium tetra(2-ethylhexanolate)


TiBut titanium tetra(butanolate)


TiEtBut titanium tetra(2-ethylbutanolate)


TiHex titanium tetra(hexanolate)


TiButOct titanium tetra(2-butyloctanolate)


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 3
TiO2/SiO2 
Co-Hydrolysis with Silicic Acid without Hydrothermal Aging
In a stirred reactor, for example 45 kg of titanium tetra(isopropylate) with a titanium content of 16.8 wt % were continuously hydrolysed at 25 to 70° C. with 135 kg of deionised water blended with a freshly prepared quantity of approx. 3% silica sol. The residence time was in the range from 30 to 60 minutes.
The resultant suspension then was subjected to azeotropic steam distillation in order to remove the alcohol released during hydrolysis and, thereafter, it was dried as usual in a spraydryer drier at an air-outlet temperature from 100 to 130° C. The carbon content in the resultant solids was less than 0.2%.
The different TiO2/SiO2 mass ratios for preparing catalyst carriers according to Example 3 have been compiled in Table 3. The physical data of the resultant catalyst carriers are included in Table 4.







TABLE 3







FEED QUANTITIES FOR THE SYNTHESES OF EXAMPLE 3












Alcoholate

Silicic Acid


Total


(16.8 wt % Ti)
Water
(3.0 wt %)
TiO2
SiO2
Quantity


[kg]
[kg]
[kg]
[wt %]
[wt %]
[kg]















45
135
0
100
0
180


45
128.6
6.4
98.5
1.5
180


45
113
22
95
5
180


45
88.5
46.5
90
10
180


45
30
105
80
20
180


36
0
144
70
30
180


17.5
0
162.5
50
50
180


12
0
168
40
60
180


2.1
0
177.9
10
90
180


1
0
179
5
95
180


0
0
180
0
100
180
















TABLE 4







PHYSICAL DATA OF THE TiO2/SiO2 CATALYST


CARRIERS OF EXAMPLE 3 (INFLUENCE OF THE


HYDROLYSIS TEMPERATURE IN THE CO-HYDROLYSIS)











TiO2/SiO2
Hydrolysis

Pore



Ratio
Temperature
Surface
Volume


[wt %/%]
[° C.]
[m2/g]1)
[ml/g]2)
Crystal Structure3)














98.6/1.4 
25
143
0.25
Anatase/Brookite


94.0/6.0 
25
177
0.31
Anatase/Brookite


86.6/13.4
25
168
0.19
Anatase/Brookite


72.8/27.2
25
222
0.19
Anatase/Brookite/






Amorphous SiO2


43.9/56.1
25
148
0.07
Anatase/Brookite/






Amorphous SiO2


100/0 
70
83
0.28
Anatase/Brookite


98.5/1.0 
70
115
0.33
Anatase/Brookite


94.3/5.7 
70
182
0.38
Anatase/Brookite


89.0/11.0
70
232
0.46
Anatase/Brookite


78.4/21.6
70
249
0.36
Anatase/Amorphous






SiO2


46.2/53.8
70
350
0.22
Amorphous






(Anatase/SiO2)


 9.6/90.4
70
549
0.14
Amorphous SiO2


 0/100
70
345
0.08
Amorphous SiO2





Legend:


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)total pore volume (Hg) [ml/g] for pore radii from 0–80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 4
TiO2/SiO2 
Silicic-Acid Slurry Doping and Aging
The experiment was carried out as described in Example 3, the difference being that titanium alcoholate was hydrolysed with an 0.2 wt % aqueous solution of ammonia during approx. 45 minutes. The aqueous titanium dioxide suspension separated from the alcohols then was blended with the required quantity of silicic acid, which had been deionised on cation-exchange resins and had a SiO2 content of approx. 3 wt %. Thereafter, the resultant suspension was aged for 5 hours at 90° C. with stirring in a closed system, followed by spray drying as described in Example 3. The physical data of the catalyst carriers prepared in this way have been compiled in Table 5.
This slurry-doping process, too, allowed to readily adjust the TiO2/SiO2 ratio in the catalyst carrier by increasing the amount of the approx. 3 wt % silicic acid, while the alcoholate feed remained unchanged. The chemical impurities thresholds stated in Example 3 were met in these experiments.
Based on the findings of Example 3 revealing that a higher value is obtained at a higher hydrolysis temperature, the hydrolysis temperature was set at 70° C. in this process variant. In addition to the influence of a higher hydrolysis temperature, the aim of Example 4 was to also examine the physical data as a function of the residence time (aging for 5 hours at 90° C.).







TABLE 5







PHYSICAL DATA OF THE TiO2/SiO2 CATALYST CARRIERS OF EXAMPLE 4


(INFLUENCE OF AGING (5 h/90° C.) ON SLURRY DOPING)











TiO2/SiO2
Hydrolysis Conditions

Pore














Ratio
Temperature
Additive
Aging
Surface
Volume



[wt %/%]
[° C.]
[wt %]
[hr/° C.]
[m2/g]1)
[ml/g]2)
Crystal Structure3)
















100/0 
70
NH3 (0.2%)
5 h/90
90
0.21
Anatase/Brookite


99.0/1.0 
70
NH3 (0.2%)
5 h/90
110
0.30
Anatase/Brookite


94.3/5.7 
70
NH3 (0.2%)
5 h/90
181
0.36
Anatase/Brookite


89.1/10.9
70
NH3 (0.2%)
5 h/90
222
0.60
Anatase/Brookite


79.2/20.8
70
NH3 (0.2%)
5 h/90
282
0.67
Anatase/Brookite


41.9/58.1
70
NH3 (0.2%)
5 h/90
417
0.63
Amorphous








(Anatase/SiO2)





Legend:


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products













TABLE 6







FEED QUANTITIES FOR THE SYNTHESES OF EXAMPLE 5

















Total



Water
Silicic Acid
TiO2
SiO2
Quantity


Alcoholate
[kg]
(3.0%) [kg]
[wt %]
[wt %]
[kg]















(9.5 wt % Ti)







[kg]


45
135
0
100
0
180


45
132.5
2.5
99.0
1
180


45
122.5
12.5
95.0
5
180


45
110
25
90
10
180


(8.5 wt % Ti)


[kg]


45
135
0
100
0
180


45
132.9
2.1
99.0
1
180


45
123.8
11.2
95.0
5
180


45
111
24
90
10
180









Example 5
TiO2/SiO2 
Co-Hydrolysis of Various Titanium Alcoholates with Silicic Acid
The syntheses were carried out as described in Example 3, the difference being that various titanium alcoholates were reacted with fresh silicic acid. The alcoholates used in these experiments included e.g. titanium tetra(2-ethylbutanolate) (TiEtBut with 8.5 wt % Ti), titanium tetra(hexanolate) (TiHex with 9.5 wt % Ti), and titanium tetra(2-ethylhexanolate) (TiEtHex with 8.5 wt % Ti). The quantities used for preparing catalyst carriers with different TiO2/SiO2 ratios have been compiled in Table 6. The physical data are listed in Table 7.
Example 5 shows that according to the process of the invention, TiO2/SiO2 ratio in the catalyst carrier can be adjusted for different titanium alcoholates and various titanium concentrations (9.5 or 8.5 wt %) by varying the amount of silica sol added, while the total amount of reactants remains unchanged. The water quantity is overstoichiometric as in all these experiments.
Since the titanium alcoholates used herein were prepared by transesterification of the titanium tetra(isopropylate) employed in Example 3, the chemical impurities in the TiO2/SiO2 products of Example 5 are as low as in Example 3.
The x-ray diffraction analysis of the TiO2/SiO2 mixed oxides revealed that all catalyst carriers of Example 5 comprise anatase but no rutile.







TABLE 7







PHYSICAL DATA OF THE TiO2/SiO2 MIXED-OXIDE


CATALYST CARRIERS OF EXAMPLE 5


(USE OF DIFFERENT TITANIUM ALCOHOLATES IN THE


CO-HYDROLYSIS WITH FRESH SILICIC ACID)












TiO2/SiO2

Hydrolysis Conditions

Pore














Ratio

Temperature

Surface
Volume
Crystal


[wt %/%]
Alcoholate
[° C.]
Additive
[m2/g]1)
[ml/g]2)
Structure3)
















99.0/1.0 
TiEtBut
70
water
119
0.21
Anatase/Brookite


94.7/5.3 
TiEtBut
70
water
192
0.28
Anatase/Brookite


89.5/10.5
TiEtBut
70
water
244
0.28
Anatase/Brookite


94.7/5.3 
TiHex
70
water
202
0.36
Anatase/Brookite


89.7/10.3
TiHex
70
water
238
0.37
Anatase/Brookite


98.9/1.1 
TiEtHex
70
water
122
0.21
Anatase/Brookite


94.6/5.4 
TiEtHex
70
water
201
0.28
Anatase/Brookite


89.3/10.7
TiEtHex
70
water
247
0.28
Anatase/Brookite


90.2/9.8 
TiEtHex
90
water
250
0.32
Anatase/Brookite





Legend:


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 6
TiO2/SiO2 
Influence of Aging on Co-Hydrolysis and Slurry-Doping Method
Suspensions doped with an increasing amount of silicic acid were prepared as described in the Examples 3 and 4. After separation of the alcohols, these suspensions were subjected to aging for at least 4 hours at temperatures of 90 and 210° C., followed by drying as described in Example 3. The physical data have been compiled in Table 8.







TABLE 8







PHYSICAL DATA OF THE TiO2/SiO2 MIXED-OXIDE


CATALYST CARRIERS OF EXAMPLE 6


(INFLUENCE OF TEMPERATURE (90° C. AND 210° C.) AND DURATION


OF AGING ON CO-HYDROLYSIS AND SLURRY DOPING METHOD)













TiO2/SiO2

Hydrolysis Conditions

Pore
Pore















Ratio


Aging
Surface
Volume
Radius
Crystal


[wt %/%]
Alcoholate
T [° C.]/Additive/pH4)
[hr/° C.]
[m2/g]1)
[ml/g]2)
[nm]3)
Strucutre5)










a) Co-Hydrolysis














94.3/5.7 
TiIP
70/silica sol/3.8
5 h/90
194
0.35
5.5
Anatase/Brookite


89.0/11.0
TiIP
70/silica sol/3.6
5 h/90
247
0.52
4.9
Anatase/Brookite


82.2/17.8
TiIP
70/silica sol/3.3
5 h/90
294
0.44
4.7
Anatase/Brookite


 9.6/90.4
TiIP
70/silica sol/2.9
5 h/90
724
0.11
2.8
Amorphous (SiO2)


94.6/5.4 
TiIP
70/silica sol/3.8
4 h/210
180
0.51
7.4
Anatase/Brookite


89.0/11.0
TiIP
70/silica sol/3.6
4 h/210
182
0.94
11.4
Anatase/Brookite


79.3/20.7
TiIP
70/silica sol/3.3
4 h/210
205
1.14
11.4
Anatase/Brookite


 9.6/90.4
TiIP
70/silica sol/2.9
5 h/210
326
1.18
4.7
Amorphous (SiO2)







b) Slurry Doping














89.3/10.7
TiHex
30/NH4HCO3 (2%)/6.7
5 h/90
205
0.20
3.2
Amorphous (Anatase)


89.4/10.6
TiHex
30/NH4HCO3(2%)/6.7
5 h/210
150
0.52
5.6
Anatase


95.5/4.5 
TiIP
70/NH3 (0.2%)/8.5
5 h/90
179
0.39
6.3
Anatase/Brookite


89.1/10.9
TiIP
70/NH3 (0.2%)/8.5
5 h/90
222
0.60
8.2
Anatase/Brookite


79.2/20.8
TiIP
70/NH3 (0.2%)/8.5
5 h/90
282
0.67
8.1
Amorphous (Anatase)


95.5/4.5 
TiIP
70/NH3 (0.2%)/8.5
4 h/210
112
0.38
7.5
Anatase/Brookite


89.4/10.6
TiIP
70/NH3 (0.2%)/8.5
5 h/210
167
0.49
5.5
Anatase/Brookite


82.4/17.6
TiIP
70/NH3 (0.2%)/8.5
4 h/210
156
0.93
14.8
Anatase/Brookite


89.9/10.1
TiIP
70/HNO3 (0.2%)/2.1
5 h/90
213
0.26
3.7
Anatase/Brookite


90.2/9.8 
TiIP
70/Leucine (1.0%) and
5 h/90
218
0.44
4.2
Anatase/Brookite




NH3 (0.2%)/6.0


89.3/10.7
TiIP
70/HNO3 (0.2%)/2.1
5 h/210
180
0.56
7.2
Anatase/Brookite


90.8/9.2 
TiIP
70/Leucine (1.0%) and
4 h/210
189
0.55
6.6
Anatase/Brookite




NH3 (0.2%)/6.0





Legend:


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)average pore radius calculated from intrusion volume (2V/A) for pore radii from 0-80 nm


4)pH values after hydrolysis


5)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 7
TiO2/SiO2 
Variation of the Stirrer Circumferential Velocity
Suspensions were prepared utilising the co-hydrolysis method as described in Example 5. The alcoholate used was titanium tetra(2-ethylhexanolate). These suspensions then were subjected to aging at 210° C. as described in Example 6. The stirrer circumferential velocity was varied during the aging procedure. The resultant suspensions were spray-dried as described in Example 3. The physical data of the catalyst carriers have been compiled in Table 9.







TABLE 9







PHYSICAL DATA OF THE TiO2/SiO2 CATALYST


CARRIERS OF EXAMPLE 7


(INFLUENCE OF THE STIRRER CIRCUMFERENTIAL VELOCITY


[m/s]* DURING THE AGING OF SUSPENSIONS PREPARED


BY CO-HYDROLYSIS)














Stirrer





TiO2/

Circum-





SiO2

ferential

Pore


Ratio

Velocity
Surface
Volume
Crystal


[wt %/%]
Alcoholate
[m/s]*
[m2/g]1)
[ml/g]2)
Structure3)















100/0 
TiEtHex
0
82
0.30
Anatase/Brookite


100/0 
TiEtHex
1.04
80
0.34
Anatase/Brookite


100/0 
TiEtHex
2.61
81
0.44
Anatase/Brookite


90.2/9.8
TiEtHex
0
211
0.55
Anatase/Brookite


90.2/9.8
TiEtHex
1.04
210
0.56
Anatase/Brookite


90.2/9.8
TiEtHex
2.61
205
0.68
Anatase/Brookite





Legend:


*stirrer circumferential velocity: V (m/s) = DR (m) · 3.14 · N · 1/60 (1/s);


where: DR = stirrer diameter, N = rpm


Hydrolysis Conditions T = 90° C./Additive = NH3 (0.2%)


TiEtHex = titanium tetra(2-ethylhexanolate)


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 8
TiO2/SiO2 
Silicic Acid Ester (TEOS) without and with Aging
The silicic acid ester tetraethoxysilane (TEOS) (27.2 wt % SiO2) was hydrolysed as described below in a batch reaction with addition of a 1.0 wt % nitric acid. TEOS was placed into a stirred reactor and heated to boiling point at which point the ester was hydrolysed by addition of aqueous nitric acid with reflux cooling. The reaction was complete once the initially turbid solution turned clear.







TABLE 10







FEED QUANTITIES FOR THE SYNTHESES OF EXAMPLE 8













TEOS with 27.2
HNO3
Alcoholate



Total


wt % SiO2
(1 wt %)
(16.8 wt % Ti)
Water
TiO2
SiO2
Quantity


[kg]
[kg]
[kg]
[kg]
[wt %]
[wt %]
[kg]
















0.7
0.14
44.6
133.9
98.5
1.5
179.3


2.4
0.48
44.3
132.8
95
5
180.0


5.0
1.0
43.7
131.0
90
10
180.7









The titanium tetra(isopropylate) then was hydrolysed in a stirred reactor at 70° C. by simultaneous addition of completely hydrolysed, clear, aqueous TEOS solution and alcoholate. The hydrolysis took 45 minutes. The resultant suspension was treated as described in Example 3. The ethanol/isopropanol mixture was removed by azeotropic steam distillation. The spray drier had the usual air-outlet temperature of 100 to 130° C.







TABLE 11







PHYSICAL DATA OF THE TiO2/SiO2 MIXED-OXIDE


CATALYST CARRIERS OF EXAMPLE 8


(CO-HYDROLYSIS performed with nitric acid and TEOS at 70° C.)











TiO2/SiO2

Surface
Pore Volume



[wt %/%]
Alcoholate
[m2/g]1)
[ml/g]2
Crystal Structure3)










a) TEOS without Thermal Aging











  100/0*)
TiIP
52
0.14
Anatase/Brookite


98.75/1.25
TiIP
141
0.29
Anatase/Brookite


 94.7/5.3
TiIP
199
0.37
Anatase/Brookite


 89.4/10.6
TiIP
218
0.45
Anatase/Brookite







b) TEOS with Thermal Aging (5 h/210° C.)#)











  100/0*)
TiIP
72
0.22
Anatase/Brookite


 89.5/10.5
TiIP
168
0.61
Anatase





Legend:


*)reference sample (hydrolysed in 0.2 wt % HNO3)


#)stirrer speed: 400 rpm


TEOS tetraethoxysilane


TiIP titanium tetra(isopropylate)


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0-80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






This experiment was carried out in two variants: without aging of the alcohol-free suspension and with aging for 5 h at 210° C. The mass ratios used for making catalyst carriers with different TiO2/SiO2 ratios as described in Example 8 have been listed in Table 10. The physical data have been compiled in Table 11, which also includes for comparison the physical data of the catalyst carriers obtained by aqueous nitric hydrolysis of titanium tetra(isopropylate) at 70° C. (cf. Tables 1 and 2).
Example 9
TiO2/SiO2 
Slurry Doping with Levasil
Example 4 was repeated, the difference being that a commercially available silicic acid prepared by cation exchange (LEVASIL 500 from H.C. Starck company, Goslar) was used. This silicic acid had a particle size of 9.3 nm according to Sears, a solids content of 15%, and a pH of 9.3. The experiment was carried out in two variants: with aging of the alcohol-free suspension for 5 h at 90° C. and for 5 h at 210° C. The physical data of the resultant catalyst carriers have been compiled in Table 12.







TABLE 12







PHYSICAL DATA OF THE TiO2/SiO2 CATALYST CARRIERS OF EXAMPLE 9


(SLURRY FROM HYDROLYSIS OF TiIP IN NH3 (0.2%) DOPED WITH LEVASIL


AT 70° C.; WITH THERMAL AGING)













TiO2/SiO2

Hydrolysis


Pore



Ratio

Conditions
Aging
Surface
Volume
Crystal


[wt %/%]
Alcoholate
T [° C.]/Additive
[hr/° C.]
[m2/g]1)
[ml/g]2)
Structure3)





88.3/11.7
TiIP
70/NH3 (0.2%)
5 h/90 
196
0.26
Anatase/Brookite


88.3/11.7
TiIP
70/NH3 (0.2%)
5 h/210
162
0.65
Anatase/Brookite





Legend:


TiIP titanium tetra(isopropylate)


1)multipoint BET (N2) [m2/g] (calcination 3 h/550° C.)


2)intrusion pore volume (Hg) [ml/g] for pore radii from 0–80 nm (calcination 3 h/550° C.)


3)x-ray diffraction analysis of the main/side phases of uncalcined products






Example 10
TiO2/SiO2 
Thermostability Examinations of the Catalyst Carriers
Various catalyst carriers were selected from among the group prepared in Example 4 (cf. Table 5) and were calcined for 3 h at 550° C. in a lab-scale muffle furnace. Moreover, the products then were exposed for several hours to 800 and 1,100° C. The physical data have been compiled in Table 13.







TABLE 13







THERMOSTABILITY EXAMINATION ACCORDING TO


EXAMPLE 10 OF THE TiO2/SiO2 MIXED-OXIDE CATALYST


CARRIERS OF EXAMPLE 4












TiO2/SiO2
Calcination
Surface1)
Pore Volume2)



[wt %/%]
[hr/° C.]
[m2/g]
[ml/g]
















94.3/5.7 
3 h/550
181
0.39




3 h/800
117
0.31




 24 h/1,100
0.6
0.01



89.1/10.9
3 h/550
222
0.59




3 h/800
151
0.43




 24 h/1,100
4.0
0.02



79.2/20.8
3 h/550
282
0.53




3 h/800
200
0.49




 24 h/1,100
168
0.42



41.9/58.1
3 h/550
417
0.65




3 h/800
361
0.62




 24 h/1,100
239
0.63







Legend:



1)multipoint BET (N2) [m2/g]



2)intrusion pore volume (Hg) [ml/g] for pore radii from 0–80 nm






Example 11
TiO2/SiO2 
Influence of the SiO2 Content on the Rutile Formation
Various TiO2 and TiO2/SiO2 mixed-oxide catalyst carriers prepared according to the Examples 1 to 9 were selected after spray drying for a thermogravimetric analysis in order to examine the influence of different process variants, the SiO2 content, and the SiO2 source on the rutile formation temperature.
The peak temperatures of the rutile formation according to DTA/DTG are shown in Table 14. The rutile formation at the temperatures stated below has been proved by x-ray powder diffraction.







TABLE 14







PHYSICAL DATA OF THE TiO2/SiO2 CATALYST CARRIERS OF


EXAMPLES 1, 3 AND 6


INFLUENCE OF SiO2 CONTENT AND AGING ON THE


ANATASE/RUTILE PHASE CHANGE MEASURED BY X-RAY


DIFFRACTION










Rutile



TiO2/SiO2
Formation


Ratio
Temperature


[wt %/%]
[° C.]
Mixed-Oxide Synthesis Conditions












100/0 
680
TilP hydrolysis at 70° C.; with NH3 (0.2 wt %);




aging: 5 h/90° C.


100/0 
760
TilP hydrolysis at 70° C.; with NH3 (0.2 wt %);




aging: 4 h/210° C.


89.0/11.0
1080
TilP/silicic acid co-hydrolysis at 70° C.; aging:




5 h/90° C.


89.0/11.0
1140
TilP/silicic acid co-hydrolysis at 70° C.; aging:




4 h/210° C.


82.2/17.8
1150
TilP/silicic acid co-hydrolysis at 70° C.; aging:




5 h/90° C.


79.3/20.7
1160
TilP/silicic acid co-hydrolysis at 70° C.; aging:




4 h/210° C.


46.2/53.8
1180
TilP/silicic acid co-hydrolysis at 70° C.;




without aging


 9.6/90.4
1160
TilP/silicic acid co-hydrolysis at 70° C.;




without aging


89.3/10.7
1080
Hydrolysis of TiHex in NH4HCO3(2 wt %) at




30° C.; aging: 5 h/90° C.


89.4/10.6
1250
Hydrolysis of TiHex at 30° C. in NH4HCO3




(2 wt %); aging: 4 h/210° C.

## Claims

1. A process for the manufacture of TiO2/SiO2 mixed oxides or the hydrates and/or oxide hydrates thereof comprising 0.5 to 95 wt % Si, referring to the total Ti and Si and calculated as SiO2 and TiO2, respectively, comprising:
contacting a titanium compound or the hydrolysis product thereof with a silicic acid compound in an aqueous medium, wherein the titanium compound comprises a titanium alcoholate having at least one C1- to C16 alcoholate group, the silicic acid compound comprises an aqueous silicic acid sol, the silicic acid compound in aqueous solution has an average particle size of 1.8 to 3.0 nm, and the silica acid sol has a viscosity of less than 10 mPas at 25° C.; and
hydrolyzing the titanium compound.

2. The process according to claim 1, characterised in that the process further includes drying the resultant product and/or calcination at above 350° C., for at least 30 minutes.

3. A process according to any one of claims 1 or 2, characterised in that the titanium compound is hydrolysed at 25 to 100° C.

4. A process according to any one of claims 1 or 2, characterised in that the silica acid sol comprises 1.0 to 8.0 wt % silicic acid, calculated as SiO2.

5. A process according to any one of claims 1 or 2, characterised in that the process comprises the removal of excess alcohol by azeotropic steam distillation, wherein the removal takes place after hydrolysis of the titanium compound and preferably after addition of the silicic acid compound.

6. A process according to any one of claims 1 or 2, characterised in that before, during or after addition of the silicic acid compound, hydrothermal aging is carried out at temperatures from 90 to 235° C., for at least 1 hour, at the pressure established at these temperatures in a closed vessel.

7. A process according to any one of claims 1 or 2, characterised in that hydrolysis and/or hydrothermal aging is (are) carried out in the presence of additives selected from the group consisting of ammonia, ammonium bicarbonate, amino acids, mono-, di- and tri-carboxylic acids and mixtures thereof.

8. The process according to claim 7, characterised in that the additives are employed in quantities from 0.1 to 8.0 wt %.

9. A process according to any one of claims 1 or 2, characterised in that hydrolysis and/or hydrothermal aging is (are) performed at a pH value of the resultant aqueous slurries of less than 10.0.

10. A process according to any one of claims 1 or 2, comprising spray drying the resultant mixed-oxide product.

11. A process according to any one of claims 1 or 2, characterised in that the TiO2/SiO2 mixed oxide or the hydrates and/or oxide hydrates thereof contain more than 5 and less than 40 wt % Si, based on the total Ti and Si as SiO2 and TiO2, respectively.

12. A process according to any one of claims 1 or 2, characterised in that the titanium compound is hydrolysed in the presence of the silicic acid compound.

13. A process according to any one of claims 1 or 2, characterised in that at first the titanium compound is hydrolysed, the alcohol compounds are optionally removed, and the silicic acid compound is added thereafter.

14. A process according to any one of claims 1 or 2, characterised in that the silicic acid compound is prepared using cation-exchange resins.

15. A process according to any one of claim 1 or 2, characterised in that during hydrolysis and/or hydrothermal aging the mixing energy input corresponds to a stirrer circumferential velocity of 1 to 6 m/s.

16. A process according to any one of claims 1 or 2, characterised in that at least 90 wt % of the titanium compound is hydrolysable and irrespective of the latter at least 60 wt % is a titanium alcoholate.

17. A process according to any one of claims 1 or 2, characterised in that the silicic acid compound comprises a maximum of 300 ppm of silicic acid salt and a maximum of 200 ppm metal.