# Patent

## Title
Multi-component hydrogen storage material

## Abstract

A reversible hydrogen storage composition having an empirical formula of:

Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4, x+y+z=1 and “w” varies from 0 to 2x+2y+4z. This composition shows greater low temperature reversible hydrogen storage compared to binary systems such as MgH2—LiNH2.

## Background
GOVERNMENT RIGHTS
This invention was made with Government support under Contract No. DE-FC36-04GO14013 awarded by the Department of Energy. The government has certain rights in this invention.


FIELD OF THE INVENTION
The present invention relates to a composition for reversibly storing hydrogen. The composition has an empirical formula of:

Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4, x+y+z=1 and “w” has a value from 0 to about 2x+2y+4z.

BACKGROUND OF THE INVENTION
As the world's supply of fossil fuels dwindles, the search for energy resources to compliment and eventually replace fossil fuels has commenced. There are many options, including biofuels, nuclear power, wind power, solar power, and hydrogen. While all of these options are being developed, hydrogen is particularly attractive, especially in terms of environmental impact. Combustion of hydrogen only produces water, not the greenhouse gases that result from the combustion of biofuels or the dangerous wastes that result from nuclear fission. While hydrogen may be derived from natural gas or fossil fuel feedstocks, water is an abundant and obvious hydrogen resource. The technical hurdles that need to be cleared to realize a hydrogen economy include energy efficient production and storage of hydrogen. Hydrogen production issues may involve several technologies, including using vast arrays of solar cells for large scale hydrogen production via electrolysis of water or generating hydrogen via thermolytic cracking of water in nuclear power plants.
The current application focuses on the storage aspect of the problem. On a weight basis, hydrogen contains a great deal of energy, but on a volume basis it is inefficient. In gaseous form, hydrogen may be pressurized, but the tanks needed to maintain the high pressures required to have enough fuel for a hydrogen powered vehicle are prohibitively heavy. Another option is to liquefy the hydrogen, but the temperatures required are very low and use up about 1⁄3 of the stored energy in the hydrogen just for the refrigeration. Another approach that has been investigated recently is storing hydrogen in complex metal hydrides. The density of hydrogen that can be achieved in these materials is often higher than that observed for either pressurized gas systems or liquid hydrogen systems. Complex metal hydrides have been considered for utility in hydrogen storage applications for many years, but many fail to clear the hurdles presented by reversibility and high gravimetric capacity. La5NiH6 is widely used because of its excellent ability to reversibly absorb and desorb hydrogen, but with a gravimetric capacity of only 1.7 wt % hydrogen, it would be too heavy to use in vehicular applications. Other complex hydrides, such as the alanates, have good hydrogen storage capacities, up to 9 wt. %, but initially were not found to operate under practical conditions with respect to temperature and pressure. A landmark paper by Bogdanovic and Schwickardi (J. Alloys and Comp., 1997, 253-254, 1-9) showed that Ti-doped NaAlH4, could operate reversibly under 200° C. at reasonable pressures with nearly a 5 wt. % hydrogen storage capacity, close to the theoretical maximum of 5.5 wt. % for that material. Chen et al. found that the LiNH2/LiH-based systems could be decomposed in one step to Li2NH or two steps to yield Li3N, yielding 6.5 and 10.4 wt. % hydrogen, respectively (See Chen et al., Nature, 2002, 420, 302). High operating temperatures in excess of 300° C. are required to realize the higher hydrogen capacity. The LiNH2 system has been extended to include MgH2 in several ways, both by looking at reactions based on mixtures of 2 LiNH2 and MgH2 (See Xiong et al., Adv. Mater., 2004, 16, 1522) or via swapping the hydride for the amide in the starting materials, Mg(NH2)2+2 LiH (Leng et al., J. Phys. Chem. B, 2004, 108, 8763; Xiong et al., J. Alloys and Compounds, 2005, 398, 235). These systems operate at lower temperatures than the LiNH2/LiH systems. It is generally thought that the reversible hydrogen storage reactions in this system is:

Mg(NH2)2+2LiHLi2Mg(NH)2+2H2 

which yields about a 5.5 wt. % theoretical hydrogen storage capacity. Another hydrogen storage system based on 2 LiBH4 and MgH2 has been proposed by Vajo et. al. (see J. Chem Phys. B Letters, 2005, 109, 3719). This system is said to destabilize LiBH4 via the formation of MgB2 in the dehydrided form and reversibly stores up to 10 wt. % hydrogen, but the operating temperature is well over 300° C. Pinkerton et al. reported a new material derived from 2 LiNH2 and LiBH4 which yielded >10 wt. % hydrogen when heated over 250° C., but was not reversible. It was suggested that this material was Li3BH4(NH2)2, but further work has shown that this material is likely Li4BH4(NH2)3 (Pinkerton et al.).

Applicants have developed a ternary system of LiBH4—MgH2—LiNH2 which can reversibly store up to nearly 4 wt. % hydrogen at temperatures below 220° C. These compositions show greater low temperature reversible hydrogen storage compared to binary systems such as MgH2—LiNH2.
SUMMARY OF THE INVENTION
One embodiment of the invention comprises a reversible hydrogen storage composition having an empirical formula of:

Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4 and “w” varies from 0 to 2x+2y+4z and x+y+z=1.

Another embodiment of the invention is a method of preparing the reversible hydrogen composition described above comprising forming a reaction mixture comprising amide and hydride sources of Li, Mg and B and milling the mixture under an inert atmosphere for a time sufficient to form the reversible hydrogen storage composition.
Yet another embodiment of this invention is producing a hydrogen stream by taking the above described composition and heating it at a temperature of about 150° C. to about 250° C. to provide a hydrogen stream.


DETAILED DESCRIPTION OF THE INVENTION
As stated the present invention relates to a composition which can reversibly store hydrogen, a process for preparing the composition and a process for generating a hydrogen stream using the composition. The reversible hydrogen storage composition is represented by the empirical formula:

Li(x+z)NxMgyBzHw  (1)

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4, x+y+z=1 and “w” varies from 0 to about 2x+2y+4z. When w=0, the composition is fully dehydrided and when w=2x+2y+4z, the composition is fully hydrided.

This hydrogen storage composition is prepared from amide and hydride sources of Li, Mg and B. Sources include but are not limited to LiNH2, MgH2, LiBH4, Mg(NH2)2, LiH, Li2NH, Mg(BH4)2, MgNH, Li3N, LiMgN, Li2Mg(NH)2, Mg(NH2)2, LiH and BH3NH3. Preferred sources for the preparation of the composition are LiNH2, MgH2 and LiBH4. In this case a reaction mixture is formed having the empirical formula of:

(LiNH2)x(MgH2)y(LiBH4)z  (2)

where x, y and z have the same values as in equation (1).

The composition of equation (1) is prepared by forming a reaction mixture of the desired sources and in particular the sources and ratios of equation (2) and then milling the mixture under an inert atmosphere for a time of about 10 to 120 minutes. Examples of inert atmospheres include without limitation nitrogen, argon, etc. At the end of the milling, the produced composition is separated from the milling media.
The compositions of this invention reversibly bind hydrogen and thus can be used in any process requiring a source of hydrogen. The composition as obtained above is hydrided and thus can release desorbable hydrogen under appropriate conditions. Hydrogen desorption conditions for the materials of this invention include heating the material to a temperature ranging from about 150° C. to about 250° C. Although more hydrogen can be extracted by heating these materials to higher temperatures, this can damage the reversible nature of the material. The dehydrided material can be regenerated under hydrogen pressure ranging from atmospheric pressure to 68,948 kPa (10,000 psig) H2 and preferably from 1,379 kPa (200 psig) H2 to 13,789 kPa (2,000 psig) H2 at temperatures from about 75° C. to about 250° C., and a time of about 1 minute to about 16 hours, and preferably from about 5 minutes to about 2 hours. The amount of time necessary to release substantially all the hydrogen depends on the temperature but generally varies from 1 hour to 12 hours.
It has been found that the compositions of the invention have a reversible hydrogen storage capacity of about 4 wt. % at operating temperatures below 220° C. and have capacities over 7 wt. % at higher temperatures. The hydrogen stream can be flowed to supply hydrogen to various processes including a fuel cell for generating power either for a vehicle or to generate electricity.
The following examples are set forth to illustrate the invention and are not intended as undue limitations on the generally broad scope of the invention as set out in the appended claims.
EXAMPLE 1
A combinatorial investigation of the LiNH2—MgH2—LiBH4 system was carried out in which the compositions (LiNH2)x(MgH2)y(LiBH4)z were prepared, where x, y, and z were varied from 0 to 1 in 0.1 increments with the constraint that x+y+z=1. The samples were prepared on a 1.5 g scale, using appropriate amounts of LiNH2 (95%), MgH2 (98%), and LiBH4 (95%). All synthetic manipulations and measurements were carried out under a nitrogen atmosphere usually in a glove box. Appropriate amounts of the LiNH2, MgH2, and LiBH4 powders were added to a 45 ml tungsten carbide milling bowl containing 18-10 mm tungsten carbide balls. After the addition of the powders, the milling bowls were closed and sealed with parafilm, transferred from the glove box to a planetary ball mill and the samples were milled at 350 rpm for 15 minutes in each direction. The samples were transferred back to the glove box when milling was completed.
For measurement of the hydrogen storage capacity, the samples were then transferred to another glove box which contained a reactor which could measure the hydrogen capacity of 8 samples simultaneously. The sample loading was about 0.5 g. The measurement started with a hydriding cycle as the samples were exposed to hydrogen at 125° C. for 12 hr at 8,618 kPa (1,250 psig) H2. This was followed by a desorption cycle, during which the pressure of the hydrogen evolved was measured as the temperature was ramped to 220° C. at 2° C./min, (the results denoted in the table below as first desorption), the measured pressures being converted to weight percent hydrogen for each sample. To establish reversibility, the samples were then rehydrided at 125° C.; 8,618 kPa (1,250 psig) H2, for 12 hr, as before. This was followed by a second desorption, carried out under the same conditions as the first desorption. The measured hydrogen content from the second desorption is considered to be the reversible hydrogen contained within each composition investigated. For each of the compositions investigated, the hydrogen observed in the first and second desorptions are given in Table 1 below.







TABLE 1







Hydrogen Storage Capacities of LiNH2—MgH2—LiBH4 Compositions











moles
Moles
moles

wt %-Cycle 2


LiNH2
LiBH4
MgH2
wt %-Cycle 1
(reversible)














0.2
0.8
0
0.3
0.2


0.3
0.7
0
0.3
0.3


0.4
0.6
0
0.5
0.2


0.5
0.5
0
1.3
0.7


0.6
0.4
0
1.1
0.6


0.7
0.3
0
0.8
0.4


0.8
0.2
0
0.6
0.3


0.9
0.1
0
0.1
0.1


0.1
0.8
0.1
0.9
0.3


0.2
0.7
0.1
1.1
0.9


0.3
0.6
0.1
1.2
1.0


0.4
0.5
0.1
1.3
1.0


0.5
0.4
0.1
1.3
1.1


0.6
0.3
0.1
1.5
1.4


0.7
0.2
0.1
2.0
1.7


0.8
0.1
0.1
1.4
1.0


0.9
0
0.1
0.2
0.1


0.1
0.7
0.2
1.4
0.5


0.2
0.6
0.2
1.5
0.1


0.3
0.5
0.2
2.1
1.4


0.4
0.4
0.2
2.4
2.1


0.5
0.3
0.2
2.7
2.1


0.6
0.2
0.2
2.8
2.6


0.7
0.1
0.2
2.8
2.2


0.8
0
0.2
0.3
0.1


0.1
0.6
0.3
1.2
0.3


0.2
0.5
0.3
2.3
0.7


0.3
0.4
0.3
2.6
0.4


0.4
0.3
0.3
2.9
1.4


0.5
0.2
0.3
3.5
2.6


0.6
0.1
0.3
3.7
3.4


0.7
0
0.3
0.5
0.2


0.1
0.5
0.4
1.2
0.2


0.2
0.4
0.4
2.5
0.6


0.3
0.3
0.4
2.5
0.3


0.4
0.2
0.4
3.5
0.5


0.5
0.1
0.4
4.2
1.2


0.6
0
0.4
1.3
0.5


0.1
0.4
0.5
1.4
0.1


0.2
0.3
0.5
3.0
0.2


0.3
0.2
0.5
2.8
1.1


0.4
0.1
0.5
3.4
0.6


0.5
0
0.5
1.3
0.4


0.1
0.3
0.6
1.4
0.1


0.2
0.2
0.6
3.0
0.1


0.3
0.1
0.6
3.9
0.3


0.4
0
0.6
2.0
0.5


0.1
0.2
0.7
1.4
0.1


0.2
0.1
0.7
2.8
0.1


0.3
0
0.7
1.8
0.4


0.1
0.1
0.8
0.4
0.0


0.2
0
0.8
1.2
0.3


0.1
0
0.9
0.8
0.1


0
0.1
0.9
0.0
0.0


0
0.2
0.8
0.1
0.0


0
0.3
0.7
0.0
0.0


0
0.4
0.6
0.0
0.0


0
0.5
0.5
0.0
0.0


0
0.6
0.4
0.0
0.0


0
0.7
0.3
0.0
0.0


0
0.8
0.2
0.0
0.0









EXAMPLE 2
The formulation 5LiNH2:2.2MgH2:LiBH4 was prepared by combining 1.191 g LiNH2 (95%), 0.582 g MgH2 (98%), and 0.226 g LiBH4 (95%) in a 45 ml tungsten carbide milling bowl with 18-10 mm tungsten carbide balls. The procedure for the synthesis and the hydrogen capacity measurement is the same as setforth in example 1. On the first desorption the material contained 3.89 wt. % hydrogen upon desorption to 220° C. After rehydriding, the material showed a reversible capacity of 3.41 wt. % hydrogen.
EXAMPLE 3
Binary compositions were prepared according to literature references and compared to the ternary composition from example 2 and the 0.6LiNH2:0.3MgH2:0.1 LiBH4 ternary composition from the combinatorial study in example 1. The compositions are given in Table 2 along with the hydrogen storage capacities. For this set of samples, the measurements used a 200° C. rehydriding temperature and 8,618 kPa (1,250 psig) H2 for 12 hr. The same conditions were employed for desorption, the complete cycle being 200° C. hydride-220° C. desorb-200° C. hydride-220° C. desorb. The hydrogen storage capacities and reversibility shown for the ternary materials are superior to the binary compositions in the literature for this low temperature operation.










TABLE 2





Composition

Cycle 1
Cycle 2


















2 LiNH2:MgH2
Chen
0.49%
0.50%


2 LiBH4:MgH2
Vajo
0.0
0.0


2 LiNH2:LiBH4
Pinkerton
0.23%
0.20%


0.6 LiNH2:0.3 MgH2:0.1 LiBH4
Ex. 1
3.81%
3.37%


5 LiNH2:2.2 MgH2:LiBH4
Ex. 2
3.38%
3.29%

## Claims

1. A reversible hydrogen storage composition having an empirical formula of:


Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0≦z≦0.4 and w varies from 0 to 2x+2y+4z; and wherein x+y+z=1.

2. The composition of claim 1 where w has a value of 2x+2y+4z.

3. The composition of claim 1 where w has a value of 0.

4. A process for preparing a reversible hydrogen storage composition having an empirical formula of:


Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4 and w varies from 0 to 2x+2y+4z and wherein x+y+z=1; the process comprising forming a reaction mixture comprising amide and hydride sources of Li, Mg and B and milling the mixture under an inert atmosphere for a time sufficient to form the reversible hydrogen storage composition.

5. The process of claim 4 where the sources of Li, Mg and B are selected from the group consisting of Li2NH, LiNH2, MgH2, Mg(BH4)2, Li3N, LiMgN, Li2Mg(NH)2, Mg(NH2)2, LiH and BH3NH3.

6. The process of claim 4 where the reaction mixture has a composition represented by an empirical formula of:


(LiNH2)x(MgH2)y(LiBH4)z 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4 and x+y+z=1.

7. A process for generating a hydrogen stream comprising taking a hydrided reversible hydrogen storage composition having an empirical formula of:


Li(x+z)NxMgyBzHw 

where 0.4≦x≦0.8; 0.2≦y≦0.6; 0<z≦0.4 and w varies from greater than 0 to 2x+2y+4z and wherein x+y+z=1 and heating to a temperature from about 150° C. to about 250° C. thereby releasing hydrogen and providing a dehydrided composition.

8. The process of claim 7 further comprising taking the dehydrided composition and hydriding it by treating it with hydrogen at a temperature of about 75° C. to about 250° C., a pressure of about atmospheric to about 68,948 kPa of hydrogen for a time of about 1 minute to about 16 hours.

9. The process of claim 7 further comprising passing the hydrogen stream to a fuel cell to generate power.