# Patent

## Title
Ordered oxynitride perovskites

## Abstract

This invention relates to partially ordered and ordered oxynitride perovskites of the general formula ABO2N that are polar insulators. A comprises one or more cations or set of cations that sit in sites derived from the A-site in the perovskite structure. B comprises one or more cations or set of cations that sit in sites derived from the B-site in the perovskite structure. C comprises oxygen, O, with optionally some nitrogen, N, and D comprises N, with optionally some O. The total valence of the cations A+B is equal to the total valence of the anions 2 C+D. Also disclosed are methods of producing such oxynitride perovskites and uses of such oxynitride perovskites.

## Background
CROSS REFERENCE TO RELATED APPLICATIONS
This application claims the benefit of U.S. Provisional Application 60/878,392 (filed Jan. 4, 2007), and U.S. Provisional Application 60/879,011 (filed Jan. 8, 2007), both of which are incorporated by reference in their entirety.


STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH
This invention was made with U.S. government support under grant number NOOO14-97-1-0052 (entitled “First-Principles Calculations of Physical Properties and Bonding in Ferroelectrics”) from the Office of Naval Research. The U.S. government has certain rights in the invention.


BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to oxynitride perovskites, and in particular to partially or fully ordered oxynitride perovskites of the general formula ABO2N that have a high polarization.
2. Description of Related Art
The first perovskite discovered was calcium titanium oxide (CaTiO3). The term “perovskite” is now used to describe a group of oxides that have similar structures to calcium titanium oxide and the general formula of ABO3. The parent, or high-temperature, crystal structure of an ABO3 perovskite is cubic, with an A-cation in the middle of the cube, a B-cation in the corner and the anion, commonly oxygen, in the center of the edges. The structure is stabilized by the six coordination of the B-cation (octahedron) and twelve coordination of the A cation. Thus, packing of the ions is such that the A and O ions together form a cubic close packed array, where the B ions occupy a quarter of the octahedral holes. Differences in ratio between the A and B cations can cause a number of different distortions in the structure, usually consisting of tilting of the octahedra, which leads to centrosymmetric or non-polar structures, or off-centering of the cations, leading to polar structures. Polar perovskite structures have the curious property that the central atom does not “touch” its coordination neighbors, in violation of Pauling's rules.
Perovskites have many uses such as e.g., in ferroelectrics, catalysts, sensors, and superconductors. In particular, perovskite oxides have been of great interest, as they appear to be an alternative to complementary-metal-oxide-semiconductor (C-MOS) gate dielectrics and dynamic random access memory (DRAM) storage capacitors. Many superconductors are based on the perovskite structure.
Given the interesting properties of perovskites, researchers have attempted to synthesize complex perovskites, which are variants of the general structural formula of ABO3. Such complex perovskites may contain two or more different B-site cations. This results in ordered and disordered variants. Most work has centered on variations in the cations, but the anions can also be varied. One of the latter variants gives an oxynitride perovskite, such as e.g., CaTaO2N or Na3WO3N.
U.S. Pat. No. 4,734,390 to Marchand et al. discloses non-ordered oxynitride perovskites of the general structure ABO3-nNn. A is a metal from Group IA, Group IIA, yttrium or the lanthanides; B is metal from Groups IVA to IB. In particular, A is selected from the group consisting of Li+, Na+, K+, Rb+, Cs+, Ag+, Tl+, Ca2+, Ba2+, Sr2+, Pb2+, Cd2+, Ln3+, Bi3+, Y3+, Th4+, U4+ and trans-U4+. B is selected from the group consisting of W6+, Re6+, Mo6+, Ta5+, Nb5+, Mo5+, W5+, Ti4+, Zr4+, Sn4+, Ge4+, Nb4+, Ta4+, Al3+, Ga3+, In3+, Tl3+, Fe3+, and Cr3+. Furthermore, n is equal to 1, 2, or 3. The cationic charge a of metal A and the cationic charge b of metal B have to satisfy the equations (i) a+b=6+n and (ii) a≧n. These oxynitride perovskites are synthesized via ammoniazation and sintering, which must be carried out at high temperature. This process, however, does not yield ordered, or even partially ordered, oxynitride perovskites.
In addition, Marchand et al. reportedly also prepared ATaO2N (A=Ca, Sr, Ba), AbNbO2N (A=Sr, Ba), AMON2 (A=La, Dy; M=Nb, Ta), ATiO2N (A=La, Yb) and LnWOxN3-x (Ln=La, Nd) (Grins et al. Material Research Bulletin 29(7): 801-809 (1994)).
U.S. Pat. No. 6,383,416 (the '416 patent) to Hamada et al. is directed to an electron-emitting material containing perovskite oxynitrides of the general formula MIMIIO2N and other components. U.S. Pat. No. 6,432,325 (the '325 patent) also to Hamada et al. (and filed on the same day as the '416 patent) discloses electrodes comprising electron-emitting materials, which contain MIMIIO2N type oxynitride perovskites and have restrained evaporation during electric discharge as well as a high resistance to ion sputtering.
The '416 patent and the '325 patent disclose identical electron emitting materials containing MIMIIO2N type oxynitride perovskites with identical components. As disclosed in both the '416 and the '325 patent, the electron-emitting material may also contain tantalum, zirconium, niobium, titanium, hafnium, and mixtures thereof. In addition, the material may also contain compounds of general formula MI4MIIO3, MI5MII4O15, MI7MII6O22, and MI6MIIMII4O18. MI is selected from barium (Ba), strontium (Sr) and calcium (Ca). MII is selected from tantalum (Ta), zirconium (Zr), niobium (Nb), titanium (Ti), and hafnium (Hf). In addition, the electron emitting material may contain magnesium (Mg), scandium (Sc), yttrium (Y), lanthanum (La), vanadium (V), chromium (Cr), molybdenum (Mo), tungsten (W), iron (Fe), nickel (Ni), or aluminum (Al). Preferably, this electron emitting material satisfies the equation 0.8≦X/Y≦1.5, wherein X and Y are the molar ratios of the first and second component (MI and MII), respectively. In the case of '416 patent, a range of 0.9≦X/Y≦1.2 is even more preferred. These compounds are produced by sintering and they are not ordered.
Clarke et al. (Chem. Mater. 14: 288-294 (2002)) and Kim et al. (Chem. Mater. 16: 1267-1276 (2004)) synthesized other oxynitride perovskites of the general formula MIIIMIVO2N.
None of these oxynitride perovskites has an ordered or a partially ordered structure; they all have disordered structures, and centrosymmetric space groups. Since these compounds are non-polar, they cannot be used as ferroelectrics, piezoelectrics, non-linear optics, or other polar applications.
There is a need for partially ordered and ordered oxynitride perovskites that advantageously exploit the perovskite structure or a variant thereof for practical application.
SUMMARY
The present invention relates to novel partially or fully ordered oxynitride perovskites of general structure ABC2D.
A comprises one or more cations or set of cations that sit in sites derived from the A-site in the perovskite structure. B comprises one or more cations or set of cations that sit in sites derived from the B-site in the perovskite structure. C comprises oxygen, O, with possibly some nitrogen, N, and D comprises N, with possibly some O. The total valence of the cations A+B is equal to the total valence of the anions 2 C+D. In some embodiments, C is mostly oxygen, O, with possibly some nitrogen, N. In other embodiments, D is mostly N, with possibly some O.
In one embodiment of the invention, when A is (i) a trivalent cation or cationic group, (ii) a solid solution of trivalent cations or cationic groups, or (iii) a solid solution of heterovalent cations or cationic groups with positive trivalent average charge, B is (i) a tetravalent cation, (ii) a solid solution of tetravalent cations, or (iii) a solid solution of heterovalent cations with positive tetravalent average. In that embodiment, C is (i) oxygen, (ii) an oxygen-dominant solid solution of divalent anions, or (iii) an oxygen-dominant solid solution of heterovalent cations with negative divalent average charge and D is (i) nitrogen, (ii) a nitrogen-dominant solid solution of trivalent anions, or (iii) a nitrogen-dominant solid solution of heterovalent anions with negative trivalent average charge.
The oxynitride perovskites of interest may be ordered or partially ordered and are polar and non-metallic. In one embodiment, the total valence of the cations A+B may be seven.
Oxynitride perovskites according to the instant disclosure have a large polarity. In one embodiment, the polarity of an oxynitride perovskite is more than 75 μC/cm2 or even more than about 100 μC/cm2, more than that of PbTiO3.
In one embodiment, A is selected from the group consisting of bismuth, indium, and gallium; B is selected from the group consisting of titanium, zirconium, silicon, tin, and germanium; C is oxygen and D is nitrogen. In another of the embodiment of the invention, A is yttrium and B is selected from the group consisting of titanium, zirconium, silicon, tin and germanium. Exemplary oxynitride perovskites include YSiO2N, YGeO2N, GaTiO2N, InTiO2N, BiZrO2N, YCO2N, BiTiO2N, YTiO2N, YZrO2N, and YSnO2N. In preferred embodiments, the oxynitride perovskites are YSiO2N, YGeO2N and InTiO2N.
These ordered, or even partially ordered, oxynitride perovskites may be used in compositions, as crystals and in compositions containing these crystals. One embodiment of the invention is a non-linear optic material containing a partially ordered oxynitride perovskite. In another embodiment, a partially ordered or ordered oxynitride perovskite is used as part of neutron or hard-X-ray generators.
The invention is also directed to methods of producing a partially ordered or ordered oxynitride perovskite. In one embodiment of the invention, molecular beam epitaxy is used to produce oxynitride perovskites of the instant disclosure. In another embodiment, the oxynitrides are grown from a melt under confining pressure. In another embodiment, the oxynitrides are grown from solid state synthesis from YN and SiO2 glass. In another embodiment, the perovskite oxynitrides are grown by subjecting pyroxenoid oxynitride precursors to high pressure.
Applicants note that many of the features of their invention are also discussed in their paper, Prediction of polar ordered oxynitride perovskites, Razvan Caracas and R. E. Cohen, Applied Physics Letters 91 092902 (published online Aug. 27, 2007), which published well after the priority date of the present application.
Additional features and advantages of the invention will be set forth in the description that follows, and will be apparent, in part, from the description, or may be learned by practice of the invention. The objectives and other advantages of the invention will be realized and attained by the structure particularly pointed out in the written description and claims hereof, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.



BRIEF DESCRIPTION OF DRAWINGS
The accompanying drawings, which are included to provide a further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention.
FIG. 1 shows a crystal structure of oxynitride perovskites (e.g., YGeO2N and YSiO2N) according to the instant invention.
FIG. 2 shows the phonon dispersion curves for YGeO2N and YSiO2N. YGeO2N is shown in FIG. 2A and YSiO2N in FIG. 2B. The positive phonon frequencies prove the (meta)stability of the structure.
FIG. 3 shows the crystal structure of other oxynitride perovskites (e.g., InTiO2N and BiZrO2N) according to the instant invention.
FIG. 4 shows the polarization of YGeO2N (FIG. 4A) and YSiO2N (FIG. 4B) versus polar distortion.



DETAILED DESCRIPTION OF THE INVENTION
The present invention is directed to a new class of ordered and partially ordered oxynitride perovskites and perovskite-related oxynitrides with stable structures that present interesting piezoelectric properties.
The invention is based on first-principles calculations of the structures and physical properties of a new class of perovskite-related oxynitrides with polar structures. These structures have large spontaneous polarizations (larger than those of materials currently in use), large piezoelectric constants, and large non-linear optical coefficients.
The present invention is the result of an extensive search for new piezoelectric materials. Due to their properties, these new materials could successfully be used in devices including, but not limited to, non-linear optics (e.g., frequency doublers and shifters), optical relays, electrooptics (optical to electrical coupling), piezoelectric sensors, actuators, frequency standards, piezoelectric motors, ultrasonic transducers, vibration reducers, ferroelectric memory, ferroelectric gate transistors, piezoelectric voltage transformers, neutron generators, and X-ray generators.
As used herein, the term “solid solution” means a crystalline solid with variable composition; one or more crystallographic sites contains multiple elements.
As used herein, the term “ordered” means that elements are distributed in a definite pattern among the crystallographic sites. A classic, non-limiting, example is β-brass, which consists of Cu atoms at the corners of a cube with Zn in the center (CsCl or B2 structure). Disordered brass has an arrangement of Cu and Zn atoms with equal probabilities of Cu and Zn on each site, giving the average body centered cubic or bcc structure.
As used herein, the term “partially ordered” means that the atoms are not distributed completely randomly in a crystallographic site, but are somewhere between fully ordered and fully disordered. In the brass example, the Zn site would contain some Cu and the Cu site some Zn.
As used herein, the term “dielectric” means an insulator. A dielectric does not display metallic conduction and can maintain at least a small voltage differential without significant current flow except for leakage current, which is due to defects.
The present invention is directed to ordered and partially ordered oxynitride perovskites. In particular, the present invention is directed to ordered and partially ordered oxynitride perovskites of the formula:

ABC2D,

wherein
A comprises one or more cations or set of cations that sit in sites derived from the A-site in the perovskite structure. B comprises one or more cations or set of cations that sit in sites derived from the B-site in the perovskite structure. C comprises oxygen, O, with possibly some nitrogen, N, and D comprises N, with possibly some O. The total valence of the cations A+B is equal to the total valence of the anions 2 C+D. In some embodiments, C is mostly oxygen, O, with possibly some nitrogen, N. In other embodiments, D is mostly N, with possibly some O.
The total valence of the cations A+B is equal to the total valence of the anions 2 C+D. In one embodiment of the invention, the total valence of the cations A+B may be seven. The oxynitride perovskites of interest may be ordered or partially ordered and are polar and non-metallic.
In one embodiment, when A is a trivalent cation or cationic group, a solid solution of trivalent cations or cationic groups, or a solid solution of heterovalent cations or cationic groups with positive trivalent average charge, B is tetravalent cation, a solid solution of tetravalent cations, or a solid solution of heterovalent cations with positive tetravalent average. C is oxygen, an oxygen-dominant solid solution of divalent anions, or an oxygen-dominant solid solution of heterovalent cations with negative divalent average charge. D is nitrogen, a nitrogen-dominant solid solution of trivalent anions, or a nitrogen-dominant solid solution of heterovalent anions with negative trivalent average charge.
The oxynitride perovskites according to the instant disclosure are polar dielectrics and as such are insulators.
In another embodiment of the invention, A may be selected from a variety of metals, including metals from Group III. For example, A may be selected from the group consisting of bismuth, indium, yttrium, and gallium. In that embodiment of the invention, B may also be selected from a variety of suitable metals including metals from Group I. For example, B may be selected from titanium, zirconium, silicon, tin, and germanium.
In one embodiment of the invention, A is yttrium and B is silicon. In another embodiment of the invention, A is yttrium and B is germanium. In yet another embodiment of the invention A is indium and B is titanium. Other exemplary oxynitride perovskites include but are not limited to GaTiO2N, BiZrO2N, YCO2N, BiTiO2N, YTiO2N, YZrO2N, and YSnO2N.
Oxynitride perovskites according to the instant disclosure are ordered or partially ordered. The O and N ordering is consistent with the primitive cell symmetry, so the structure has no fundamental superlattice lines relating to the O and N, although a superimposed superlattice structure that does not destroy the polar symmetry is also consistent with the invention.
One of the distinguishing features of oxynitride perovskites according to the instant disclosure is that the perovskites have an extremely large polarity, larger than what is known in the art. For example, LiNbO3 has a polarization of 71 μC/cm2, and LiTaO3 has a polarization of 50 μC/cm2. The largest known polarization is 75 μC/cm2 for PbTiO3. Preferably, oxynitride perovskites according to the instant invention have a polarization of more than 75 μC/cm2. The polarization may be from about 75 to about 100 μC/cm2 or from about 76 to about 125 μC/cm2, from about 100 to about 130 μC/cm2 or greater than 100 μC/cm2. The spontaneous polarization as obtained from Berry phase calculations is 130 μC/cm2 for YSiO2N, 103 μC/cm2 for YGeO2N and 79 μC/cm2 for InTiO2N.
Oxynitride perovskites according to the instant disclosure are also stable. The oxynitride perovskites are stable in air and water.
In addition, oxynitride perovskites according to the instant invention may have but are not limited to tetragonal symmetry with a P4 mm space group with five (5) atoms per primitive cell. Alternatively, oxynitride perovskites according to the instant invention may have monoclinic symmetry with a Pm space group. Symmetry related structures are obtained by allowing for rotations of the coordination polyhedra and/or cation displacements. Symmetry group/subgroup relations can relate all these structures.
The structure of these materials is obtained from the perovskite structure by replacing in each unit cell one oxygen atom by one nitrogen atom, with a concomitant change in the cations to maintain charge balance. The resulting structure is ordered, polar, piezoelectric, as well as dynamically stable, and at least thermodynamically metastable. A partially ordered structure with some O on the N site and some N or the O site will also display a net polarization with non-linear optical and piezoelectric properties.
The physical basis of the piezoelectricity in these oxynitride perovskites is as follows. The strong covalent boding between the tetravalent cations and the nitrogen atoms and between the trivalent cations and the oxygen atoms induce large anomalous Born effective charges and large displacements of the cations away from the center of mass of the coordination polyhedra. The cation displacements break the symmetry, removing the center of symmetry, and generate large spontaneous polarization and inducing interesting piezoelectric and optical properties. As all cations have large displacement and contribute to the spontaneous polarization, the value of this latter property is very large.
In one embodiment of the invention, the oxynitride perovskite is YSiO2N. In another embodiment of the invention, the oxynitride perovskite is YGeO2N. In another embodiment, the oxynitride perovskite is GaTiO2. In an alternate embodiment, the oxynitride perovskite is InTiO2N. In yet another embodiment, the oxynitride perovskite is BiZrO2N. In another embodiment, the oxynitride perovskite is YCO2N. In another embodiment, the oxynitride perovskite is GaTiO2N.
Synthesis
Previously, non-polar, disordered, oxynitride perovskites were synthesized by firing of metal oxides and carbonates with flowing ammonia at elevated temperatures. Thus, the conventional synthesis can be described by the following equation:

ABOX+NH3→ABOYNZ+H2O

Such a reaction typically involves sintering of the reactants. Perovskite oxides produced by this conventional synthesis approach have been shown to exhibit large dielectric constants, but much smaller than oxynitride perovskites of the instant application. They are also disordered and centrosymmetic with three-dimensional arrangement such as I4/mcm and Pbnm. Thus, these oxynitride perovskites are not piezoelectric.

Synthesis of an oxynitride perovskite according to the instant disclosure would not proceed via use of the currently known methods for producing oxynitrides. Using such a conventional synthesis approach to produce oxynitride perovskites will not produce ordered replacement of O by N, and thus would not achieve the high polarization exhibited by oxynitride perovskites of the instant disclosure. The use of sintering produces a disordered structure. Thus, the conventional synthesis cannot achieve production of an oxynitride perovskite, which is ordered, or even partially ordered, and a dielectric.
Production of oxynitride perovskites according to the present invention could be achieved using metal nitrides and oxides as precursors. An example of such a reaction would be:

YN+SiO2→YSiO2N

Or

InN+TiO2→InTiO2N

Both YN and SiO2 or InN and TiO2 are readily available reagents.

This synthesis reaction may be carried out under higher pressure and temperature. Synthesis pressures may be as low as 1-10 GPa, and temperatures of 1000-2000K. Such higher temperature and pressure would be particularly advantageous to provide extra energy necessary to accelerate the kinetics of the ordering of the perovskite structure. In one embodiment of the invention, pressure could be produced via shock or static conditions. At the higher temperatures, the crystals can be grown from a melt. In another embodiment crystals are grown from a melt at zero pressure is a controlled atmosphere.
The oxynitride perovskites may be produced utilizing molecular beam epitaxy (MBE) (see S. A. Chambers, Surface Science Reports 39 (5), 105-180 (2000)). In MBE, ultra pure reactants are heated separately until they slowly begin to evaporate. The reactants are then deposited on top of each other as they condense onto an inert substrate such as a wafer. The process takes place under high vacuum or ultra high vacuum. The evaporated reactants do not interact with each other or any other vacuum chamber gases until they reach the wafer, due to the large mean free path lengths of the beams. MBE allows for a slow deposition rate, laying down one atom at a time, to obtain an ordered or partially ordered oxynitride perovskite. For example, ultra-pure elements such as e.g., solid Y, Si, and gaseous O2, gallium and arsenic are heated until they each slowly begin to evaporate, and are combined with oxygen gas.
In alternative synthesis paths, the reaction is carried out via chemical vapor deposition (CVD) or by use of pulsed laser deposition.
Exemplary Uses
Oxynitride perovskites according to the instant invention have many uses. They may be used in compositions containing one or more oxynitride perovskite crystals. Alternatively, oxynitride perovskites may be used as films. For example, an oxynitride perovskite layer may be deposited on a substrate.
In one embodiment, the oxynitride perovskites are used as non-linear optic materials. Such materials are used as e.g., frequency doublers, optical switches, and optical logic elements. In another embodiment of the invention, the optical properties would also be tunable by applying a bias electric field. This would be useful in controlling optical systems.
In another embodiment, the oxynitride perovskites are used to produce high energy x-rays, or neutrons, electrons, or plasma via the pyroelectric effect generating large voltages at their polar surfaces. For example, a crystal of an oxynitride perovskite may be used with deuterium to produce neutrons under appropriate conditions (see B. Naranjo, J. K. Gimzewski, and S. Putterman, Nature 434 (7037), 1115-1117 (2005)). The large polarization can be used along with the pyroelectric effect to accelerate deuterium ions with sufficient energy to undergo fusion and generate neutrons (see D. Yarmolich, V. Vekselman, H. Sagi et al., Plasma Devices and Operations 14 (4), 293-302 (2006)).
Alternatively, the oxynitride perovskite may be used for capacitors, resonators, ferroelectric random-access memories, and switches. Thus, the dielectric perovskite oxynitride according to the instant disclosure may be used as a gate insulating film of a MIS transistor, a capacitor dielectric film of a DRAM, a ferroelectric film such as e.g., a data holding film in a FeRAM, or a transistor such as a MFIS transistor.
EXAMPLES
Non-limiting illustrative examples of embodiments of the present invention follow. These examples are not intended to limit the scope of any embodiment of the present invention, but rather are intended to illustrate features of partially ordered oxynitride perovskites.
Different chemical compositions were explored to find thermodynamically stable structures with interesting piezoelectric properties. Calculations were performed on several oxynitride perovskites including BiTiO2N, GaTiO2N, InTiO2N, YTiO2N, BiZrO2N, YZrO2N, YGeO2N, YSiO2N, YCO2N, and YSnO2N. Different structures are predicted to exist, all of which can be derived from the perovskite structure by allowing for rotation of the coordination polyhedra and/or cation displacements. Symmetry group/subgroup relations can relate all these structures. The resulting structures are dynamically stable, polar, and piezoelectric.
As a matter of example, the results of calculations on some of these compounds follow. The method used for these calculations, the density functional theory (DFT) as implemented in the ABINIT using planewaves and pseudopotentials, was successfully tested on a variety of materials including polar perovskites. The methods included first-principles calculations of the local density approximation (LDA) of density functional theory. The method also employed Troullier-Martins pseudopotentials within a 40 Ha kinetic energy cut-off. Dynamical properties and higher-order non-linear dielectric properties were determined using the density functional perturbation theory and spontaneous polarization using the Berry phase approach. For all these materials (as listed below), the theoretical experiments are within the standard DFT error bar.
A. Crystal Structure
FIG. 1 exemplifies the crystal structure of some oxynitride perovskites according to the instant disclosure. Structures of ordered tetragonal modifications, e.g., of YGeO2N and YSiO2N were computed using first-principles calculations. For reference, Y is indicated is by 101, Si/Ge by 102, O by 103 and N by 104. FIG. 1 also includes the cation displacements relative to the centrosymetric structure of (1) Y and Ge in YGeO2N and (2) Y and Si and YSiO2N. FIG. 1 also shows the displacements of the actions from the ideal positions in the centrosymmetric structure. These large displacements lead to large spontaneous polarization.
The structure of oxynitride perovskites (as shown in FIG. 1) was determined as follows. Starting with an ABO3 cubic simple ordered perovskite with Pm3m symmetry, one oxygen atom was replaced with a nitrogen atom and the bivalent cation with a trivalent cation. These replacements generate a P4 mm structure for ABO2N chemistry. Octahedral tilts of the BO4N2 octahedra around the 4-fold axis doubles the cell: P4bm symmetry. Unstable phonon mode in the zone-center of the P4 mm and P4bm structure distorts the structure to monoclinic symmetry Pm.
Overall, the structure of oxynitride perovskite according to one embodiment of the invention, as shown in FIG. 1, has tetragonal symmetry with a P4 mm space group. For YGeO2N and YSiO2N, the atoms in this structure lie as follows: Y on 1 b (1⁄2 1⁄2 z), Si/Ge on 1 a (0 0 z′), O on 2 c (1⁄2 0 z′′) and N on 1a (0 0 z′′′) Wyckoff sites.
The cation displacements relative to the centrosymetric structure are also shown. For YGeO2N, the cation displacement for Y and Ge are 0.816 Å and 0.766 Å, respectively. For YSiO2N, the cation displacement for Y and Ge are 0.758 Å and 0.613 Å, respectively. The depth of the potential well is −0.135 Ha per YGeO2N molecule. These large structural displacements enhance the polar character of the structure but also deepen the potential wells. Table 1 below lists the relevant parameters.







TABLE 1







Some Structural Parameters for YSiO2N and YGeO2N.













Compound
a
c
ZY
ZGe/Si
ZO
ZN
















YSiO2N
3.228
4.435
0.342
0.889
0.027
0.513


YGeO2N
3.307
4.66
0.325
0.874
0.038
0.500





Y lays in 1b (1⁄2, 1⁄2 z), Ge/Si lay in 1a (0 0 z), O in 2c (1⁄2 0 z) and N in 1a (0 0 z′) Wyckoff positions






B. Properties
Oxynitride perovskites according to the instant disclosure have many interesting properties. Tables that list some of these properties for YGeO2N and YSiO2N follow below. All values should be considered to have a confidence bar of about ±20%. Table 2 below lists some computed properties of YGeO2N and YSiO2N. Both YGeO2N and YSiO2N have similar values for dielectric tensor ∈∞. However, the values for the dielectric tensor ∈0 vary. For YGeO2N, the piezoelectric constants tensor d (pC/N), which describe the magnitude of the induced polarization due to mechanical strain, are d121=−20.5, pC/N, d333=−5.5 pC/N, and d113=−0.5 pC/N. For YSiO2N, the piezoelectric constants tensor d are d121=−12.5 pC/N, d333=−8.3 pC/N, and d113=0.4 pC/N. By way of comparison, BaTiO3 ceramics have a d333 of 350, KPD has a d333 of 21, and ADP has a d333 of 48.
The non-linear optical coefficients d (pmN) are coefficients of the square terms in the polynomial expansion that relates the polarization induced by an applied electric field. The non-linear optical coefficients d (pm/V) are as follows. For YGeO2N, d15=2.6 pm/V and d33=−4.5 pm/V. For YSiO2N, d15=2.0 pm/V and d33=−5.5 pm/V. For comparison, for the organic compound AANP, d31=d15=80 pm/V, for KDP the coefficients are approximately 0.6-0.7 pm/V and for ADP on the order of 0.8 pm/V.
The electro-optic tensor is a measurement of the change in refractive index due to an applied electric field. The values for the electro-optic tensor for YGeO2N are c15=−0.84 pm/V, c33=1.0 pm/V, and c51=−1.8 pm/V. For YSiO2N, the values electro-optic tensor values are c15=−1.4 pm/V, c33=0.64 pmN, and c51=−1.3 pm/V.







TABLE 2







Selected Properties of YGeO2N and YSiO2N










YGeO2N
YSiO2N

















Electronic dielectric tensor -
4.6
4
5.0
4.4
4.4
4.5


ε∞


Dielectric tensor - ε0
16.1
16.1
9.8
13.4
13.4
9.7









Predicted Spontaneous polari-
103 μC/cm2
130 μC/cm2


zation, Ps


Piezoelectric constants tensor
d121 = −20.5
d121 = −12.5


d (pC/N)
d333 = −5.5 
d333 = −8.3 



d113 = −0.5 
d113 = 0.4   


Non-linear optical coefficients
d15 = 2.6  
d15 = 2.0  


d (pm/V)
d33 = −4.5
d33 = −5.5


Electro-optic tensor (pm/V)
  c15 = −0.84
  c15 = −1.42



c33 = 1.05
c33 = 0.63



  c51 = −1.77
  c51 = −1.32









Because of the high symmetry of the atomic positions, the Born Effective Charge (BEC) tensors, defined as the change in polarization due to atomic displacements under zero-electric field, are diagonal. The values are listed below in Table 3. The BEC appear to be slightly anomalous, because there are not enough d electrons in the structure from the cations to couple with the p electrons of the anions. This suggests that assuming ordered phases and given the proper ratio between the cation radii to stabilize the high-symmetry P4 mm structure, the introduction of transition metals with more d electrons might result in larger anomalies for the BEC and thus in an enhancement of the polarization. For determinations of spontaneous polarization, the contribution of each atom to the polarization, the dipole, is calculated as the product between the BEC and the position difference between the centrosymmetric and the polar structures. Using Berry phase theories to calculate the spontaneous polarization Ps, the values of Ps for YGeO2N and YSiO2N are approximately 103 μC/cm2 and 130 μC/cm2, respectively. Based on the classical (dipole summation) theory, the values of Ps for YGeO2N and YSiO2N are approximately 170 μC/cm2 and 184 μC/cm2, respectively.







TABLE 3







Born effective charge tensors, Z*ij and corresponding dipole


contributions to polarizations in YGeO2N and YSiO2N













Element
Z*11
Z*22
Z*33
dipole

















YGeO2N







Y
3.481
3.481
3.379
5.206



Ge
3.582
3.582
3.842
4.278



O
−2.744
−1.915
−2.341
0.782



N
−2.404
−2.404
−2.539
0.001



YSiO2N



Y
3.475
3.475
3.216
4.250



Si
3.491
3.491
3.988
3.717



O
−2.661
−1.836
−2.224
0.505



N
−2.469
−2.469
−2.755
0.306







Due to symmetry Z*ij = 0 for ij.






The values for spontaneous polarization (Ps) for YGeO2N and YSiO2N are compared to those of other compounds including perovskites in Table 4. As can be seen from Table 4, YGeO2N and YSiO2N have larger spontaneous polarization values (Ps) than those for any of the other listed perovskites. The Ps values for these perovskite are significantly larger than what is currently used. The values obtained for the polarization are the highest values ever reported for a polar solid. For comparison, the polarization in PbTiO3 is about 75 μC/cm2, in LiNbO3, it is only 71 μC/cm2, and in LiTaO3, it is only about 50 μC/cm2. It should be noted that the Ps of 75 μC/cm2 for PbTiO3 is thought to be the highest known.







TABLE 4







Values for spontaneous polarization (Ps) of selected compounds











Spontaneous polarization,



Material
Ps (μC/cm2)














Bi.5Na.5TiO
36



KDP
4.75



KNO3
6.3



LiH3(SeO3)2
15



LiNbO3
71



LiTaO3
50



NaNbO3
12



PMN
24



PZN
24



PbTiO3
75



SbSI
25



YGeO2N
103



YSiO2N
129










FIG. 2 shows the phonon band structures as computed in the density functional perturbation theory for YGeO2N and YSiO2N. YGeO2N is shown in FIG. 2A and YSiO2N in FIG. 2B. Surprisingly, both structures are dynamically stable. Both structures are dynamically stable. All optical modes are positive. The bands corresponding to octahedral rotations have similar dispersions to those observed in not ordered oxynitride perovskites. In particular, the positive phonon frequencies prove the (meta)stability of the structure. The elastic constants are all positive and listed in Table 5.







TABLE 5







Elastic Constants computed from linear response














C11
C33
C12
C13
C44
C66

















YSiO2N
466
317
211
100
135
231


YGeO2N
374
345
176
86
90
167









The zone-center modes and the Modes in gamma are shown in Table 6.







TABLE 6







Modes in Gamma for YGeO2N and YSiO2N










Compound
Modes in Gamma (cm−1):
















YGeO2N
A1 (z)
328
342





553
692





819
879




B1
408




E (x, y)
188
200





282
340





462
640





761
801



YSiO2N
A1 (z)
373
415





648
750





927
1058




B1
400




E (x, y)
249
281





380
402





534
721





854
930







4A1 + B1 + 5 E; A1, E are IR- and Raman active; B1 are Raman active






FIG. 3 shows the monoclinic crystal structure of other oxynitride perovskites (e.g., InTiO2N and BiZrO2N) according to the instant invention. In particular, InTiO2N distinguishes by large values of the non-linear optical coefficients (see Table 7).







TABLE 7





Non-linear optical coefficients of InTiO2N (in pm/V)




















−8.089
−3.224
6.642
0.000
13.565
0.000


0.000
0.000
0.000
17.684
0.000
−3.224


13.565
17.684
−6.016
0.000
6.642
0.000









The lattice polarizations were calculated using modern theory of polarization (R. D. King-Smith and D. Vanderbilt, Phys. Rev. B 47, 1651 (1993); D. Vanderbilt and R. D. King-Smith, Phys. Rev. B 48, 4442 (1994); R. Resta, Rev. Mod. Phys. 66, 899 (1995)). The Berry's phase polarization is a lattice of values, with a lattice spacing of 2eR/Ω, where e is the electron charge and R are the lattice vectors. Polarization differences, however, are unambiguous. Experiments measure polarization changes (usually via hysteresis loops) and absolute polarizations are not measurable using standard methods. For ferroelectrics with small polarizations comparison between theory and experiment is straightforward, but in materials with large polarizations the lattice of polarizations measured for a single polar structure cannot be unambiguously reduced to an experimentally meaningful value, called the effective polarization, without additional computations (J. B. Neaton, C. Ederer, U. V. Wahmare, N. A. Spaldin, and K. M. Rabe, Phys. Rev. B 71, 014113 (2005); R. Resta and D. Vanderbilt, in Physics of Ferroelectrics: A Modern Perspective, edited by C. H. Ahn, K. M. Rabe and J. M. Triscone (Springer-Verlag, New York, 2007)). For tetragonal symmetry, only the z component of P is nonzero, the formal polarization value along the polar axis z as PBerry=130 (±n308) μC/cm2 for YSiO2N and 103 (±n293) μC/cm2 for YGeO2N, where the polarization lattice spacing is indicated in parentheses, were obtained. As discussed in reference to Table 4, these values are extremely large compared to other compounds. In order to find the effective polarization, its value was computed using the Born effective charges, Z* (see Table 3) and the displacement vectors from the ideal perovskite structure u, ΔP=ΣZ*u. This gives effective polarizations Pz=−163 μC/cm2 for YSiO2N and Pz=−171 μC/cm2 for YGeO2N. These values are not identical to Berry's phase because of the linear approximation, but are very close. Using these values, the effective PBerry is estimated to be −178 μC/cm2 for YSiO2N and −190 μC/cm2 for YGeO2N. The direction of polarization is from the B ion toward the closer N. Born effective charges vary with distortion, the absolute values of the charges being slightly larger for the centrosymmetric phase than the ferroelectric phase.
FIG. 4 shows the polarization of (a) YGeO2N and (b) YSiO2N versus polar distortion. This figure illustrates the computation of the effective polarization. The ground state structure is a distortion of 1 and the symmetric non-polar (unstable) structure is at 0. Multiple lines are shown because the polarization was computed for an idealized infinite perfect lattice, but the experimentally observable polarization is nevertheless unambiguous. The polarization was computed in two ways. It was computed directly using the modern Berry's phase approach from the electronic wavefunctions, and from ΣuiZi*, where ui is the displacement of each atom and Z*i; is the effective charge of each ion, computed theoretically. The two computations agree.
As the present invention may be embodied in several forms without departing from the spirit or essential characteristics thereof, it should also be understood that the above-described embodiments are not limited by any of the details of the foregoing description, unless otherwise specified, but rather should be construed broadly within its spirit and scope as defined in the appended claims, and therefore all changes and modifications that fall within the metes and bounds of the claims, or equivalence of such metes and bounds are therefore intended to be embraced by the appended claims.

## Claims

1. An oxynitride perovskite of the formula YSiO2N
wherein the oxynitride perovskite is ordered, polar and non-metallic.

2. The oxynitride perovskite of claim 1, wherein the oxynitride perovskite is dielectric.

3. The oxynitride perovskite of claim 1, wherein the oxynitride perovskite is a polar insulator.

4. The oxynitride perovskite of claim 1, wherein the oxynitride perovskite is piezoelectric.

5. The oxynitride perovskite of claim 1, wherein the oxynitride perovskite is ferroelectric.

6. A composition comprising an oxynitride perovskite of claim 1.

7. A crystal comprising an oxynitride perovskite of claim 1.

8. A composition comprising one or more crystals of claim 7.

9. A non-linear optic material comprising an oxynitride perovskite of claim 1.

10. A neutron generator comprising an oxynitride perovskite of claim 1.