# Patent

## Title
Use of MoO3 as corrosion inhibitor, and coating composition containing such an inhibitor

## Abstract

The subject matter of the invention is the use of MoO3 as a corrosion coating composition for metal parts, characterized in that it comprises: a least one particulate metal; an organic solvent; a thickener; a silane-based binder, preferably carrying epoxy functional groups; molybdenum oxide (MoO3); possibly a silicate of sodium, potassium or lithium; and water.

## Background
The object of the present invention is to develop an anti-corrosion coating for metal parts, preferably a coating free of hexavalent chromium, which is endowed with improved anti-corrosion properties.
The invention applies to metal parts of any type, in particular made of steel or cast iron, which need to have good corrosion behaviour, for example because of their application in the motor-vehicle industry. The geometry of the parts to be treated is of little importance as long as the anti-corrosion compositions may be applied by reliable and industrializable processes.
One of the objects of the present invention is in particular to improve the anti-corrosion properties of parts treated without using a composition based on hexavalent chromium in the formulation of the coatings.
Many anti-corrosion treatment solutions based on hexavalent chromium have been proposed to date. Although they are generally satisfactory with regard to the protection of treated metal parts, they are, however, becoming increasingly criticized because of their consequences with regard to the toxic risks that they entail and in particular because of their adverse consequences for the environment.
As a consequence, various anti-corrosion treatment compositions free of hexavalent chromium have been recommended. Some of these compositions are based on a particular metal, such as zinc or aluminium. However, when such compositions are in the form of an aqueous dispersion their stability is limited. This precludes long preservation and storage times.
Within the context of the present invention, the Applicant has discovered that it is possible to improve the anti-corrosion properties and the stability of various anti-corrosion coating compositions by incorporating thereinto molybdenum oxide MoO3 as corrosion inhibitor.
Hitherto, the use of molybdenum oxide MoO3 as a corrosion inhibitor in systems of aqueous phase has not been known. Certain molybdates, i.e. MoO42− ions, have already been presented as corrosion inhibitors. However, the Applicant has been able to show that in a certain number of conventional anti-corrosion compositions the addition of a molybdate, for example zinc molybdate, in no way improves its properties.
The present invention relates more particularly to the use of molybdenum oxide MoO3 as an agent for enhancing the anti-corrosion properties of a coating composition based on a particulate metal containing zinc or a zinc alloy in aqueous phase. This finding has even been extended to composition containing hexavalent chromium. This is another object of the invention.
Without in any way wishing to be limited to such an interpretation, it seems that in the particular case of an anti-corrosion coating composition based on a particulate metal, the presence of molybdenum oxide MoO3 makes it possible to improve the control of the sacrificial protection exerted by the particulate metal in suspension in the composition.
According to one particular feature, the particulate metals have a lamellar form, the thickness of the flakes being comprised between 0.05 μm and 1 μm and having a diameter equivalent (D50) measured by laser diffraction comprised between 5 μm and 25 μm the subject of the invention is more particularly the use of molybdenum oxide MoO3 in a composition containing zinc in aqueous phase.
According to another feature of the invention, the molybdenum oxide MoO3 is used in an essentially pure orthorhombic crystalline form, having a molybdenum content greater than approximately 60% by mass.
Advantageously, the molybdenum oxide MoO3 will be used in the anti-corrosion compositions in the form of particles having dimensions of between 1 and 200 μm.
More specifically, the subject of the present invention is anti-corrosion coating compositions for metal parts, which comprise:

    
    
        at least one particulate metal;
        an organic solvent;
        a thickener;
        a silane-based binder, preferably carrying epoxy functional groups;
        molybdenum oxide (MoO3);
        possibly a silicate of sodium, potassium or lithium, and;
        water.
    
    


The relative proportions of the various constituents in such a composition may vary widely. However, it has turned out that the content of molybdenum oxide MoO3 is preferably between 0.5 and 7% and even more preferably in the region of 2% by weight of the total composition.
The particulate metal present in the composition may be chosen from zinc, aluminium, chromium, manganese, nickel, titanium, their alloys and intermetallic compounds, and mixtures thereof. It should be pointed out here that if the recommended coating composition is preferably free of CrVI, it may nevertheless contain a certain proportion of metallic chromium. In practice, it has turned out that the presence of zinc is highly desirable.
Advantageously, the particulate metal content is between 10% and 40% by weight of metal with respect to the weight of the composition.
Preferably, the anti-corrosion coating composition according to the invention contains zinc and/or aluminium, and preferably comprises zinc.
As indicated above, this type of composition is mainly of aqueous nature and therefore preferably contains from 30% to 60% by weight of water. The composition may nevertheless be enriched by the presence of an organic solvent, preferably a water-soluble organic solvent, which makes it possible to improve the anti-corrosion performance of the composition. For this purpose, the composition will contain, for example, from 1% to 30% by weight with respect to the total composition. However, it seems to be important not to exceed this organic solvent content of approximately 30%.
In an advantageous embodiment of the invention, the composition will make use of an organic solvent, for example consisting of a glycol ether, in particular diethylene glycol, triethylene glycol and dipropylene glycol.
According to another feature of the present invention, the anti-corrosion composition also contains from 0.005% to 2% by weight of a thickening agent, in particular of a cellulose derivative, more particularly hydroxymethylcellulose, hydroxyethylcellulose, hydroxypropylcellulose, hydroxypropylmethylcellulose, xanthan gum or an associative thickener of the polyurethane or acrylic type.
The composition of the present invention may also contain mineral rheologic agents of the silica or organophilic clays type.
Such a composition also makes use of a binder, preferably an organofunctional silane, used in an amount of 3% to 20% by weight. The organofunctionality can be represented by vinyl, methacryloxy and amino, but is preferably epoxy functional for enhanced coating performance as well as composition stability. The silane is advantageously easily dispersible in aqueous medium, and is preferably soluble in such medium.
Preferably, the useful silane is an epoxy functional silane such as beta-(3,4-epoxycyclohexyl) ethyltrimethoxysilane, 4(trimethoxysilyl) butane-1,2 epoxide or γ-glycidoxypropyltrimethoxysilane.
Finally, the anti-corrosion coating compositions according to the invention may also contain, in addition to the aforementioned organic solvent, up to a maximum amount of approximately 10% by weight of white spirit so as to improve the ability of the anti-corrosion compositions to be applied to the metal parts by spraying, dipping or dip-spinning.
Advantageously, the composition may also contain a silicate of sodium, potassium or lithium, preferably in an amount comprised between 0.05% to 0.5% by weight.
Naturally, the present invention also relates to anti-corrosion coatings which are applied to the metal parts using the aforementioned compositions, being applied by spraying, spinning or dip-spinning followed by a curing operation at a temperature of between 70° C. and 350° C. for a cure time of around 30 minutes.
According to an advantageous embodiment, the anti-corrosion coating will result from an application operation involving, prior to the curing operation, an operation of drying the coated metal parts, preferably at a temperature of around 70° C. for approximately 20 minutes. Under these conditions, the thickness of the coating thus applied is between 3 μm and 15 μm and preferably between 5 μm and 10 μm.



BRIEF DESCRIPTION OF THE DRAWINGS
FIGS. 1 and 2, respectively, are graphs of salt spray resistance, as a function of bath age, in the examples presented herein below.



In the examples presented hereinbelow for comparative purposes, various types of corrosion inhibitor were tested within the context of the present study, which was carried out in order to improve the anti-corrosion properties of various compositions and in particular of the reference composition called GEOMET® which has been described in U.S. Pat. No. 5,868,819 herein incorporated by reference.
These were the main commercially available corrosion inhibitors. They have been listed below by broad chemical category, specifying each time the origin of the product together with its name and its composition.












Modified zinc phosphates:








Supplier: Heubach:



HEUCOPHOS ® ZPA:
hydrated zinc aluminium



orthophosphate


HEUCOPHOS ® ZMP:
hydrated zinc molybdenum



orthophosphate


HEUCOPHOS ® SAPP:
hydrated strontium aluminium



polyphosphate (SrO: 31%; Al2O3: 12%;



P2O5: 44%; MgSiF6: 0.3%)


HEUCOPHOS ® SRPP:
hydrated strontium aluminium



polyphosphate (SrO: 28%; Al2O3: 12%;



P2O5: 42%)


HEUCOPHOS ® ZCP:
hydrated zinc calcium strontium



silicate orthophosphate


HEUCOPHOS ® ZCPP:
hydrated zinc calcium aluminium



strontium silicate orthophosphate



(ZnO: 37%; SrO: 5%; Al2O3: 3%; P2O5:



18%; CaO: 14%; SiO2: 14%)


HEUCOPHOS ® CAPP:
hydrated calcium aluminium silicate



polyphosphate (Al2O3: 7%; P2O5: 26%;



CaO: 31%; SiO2: 28%)


Supplier: Devineau:


ACTIROX ® 213:
zinc iron phosphates (ZnO: 66%; PO4:



48%; Fe2O3: 37%)


Supplier: Lawrence Industries:


HALOX ® SZP 391:
zinc calcium strontium



phosphosilicate


HALOX ® CZ 170:
zinc orthophosphate


Supplier: Tayca:


K WHITE ® 84:
aluminium triphosphate (ZnO: 26.5 to



30.5%; Al2O3: 9 to 13%; P2O5: 36 to



40%; SiO2: 11 to 15%)







Molybdates








Supplier: Devineau:



ACTIROX ® 102:
zinc molybdates coupled to



zinc-phosphate-modified agents (ZnO:



63%; PO4: 46%; MoO3: 1%)


ACTIROX ® 106:
zinc molybdates coupled to



zinc-phosphate-modified agents (ZnO:



67%; PO4: 46%; MoO3: 1%)


Supplier: Sherwin Williams:


MOLY WHITE ® MAZP:
ZnO, CaCO3, Zn3(PO4)2, CaMoO4


MOLY WHITE ® 212:
ZnO, CaCO3, CaMoO4


Sodium molybdate:
Na2MoO4







Borates








Supplier: Buckman:



BUTROL ® 23:
calcium metaborate


BUSAN ® 11M2:
barium metaborate


Supplier: Lawrence Industries:


HALOX ® CW 2230:
calcium borosilicate







Calcium-doped silica








Supplier: Grace:



SHIELDEX ® AC5







Zinc salts








Supplier: Henkel:



ALCOPHOR ® 827:
organic zinc salt







Organic inhibitors








Supplier: Ciba-Geigy:



IRGACOR ® 1930:
complex of zirconium and 4-methyl-



γ-oxobenzenebutanoic acid


IRGACOR ® 1405:
4-oxo-4-p-tolybutyric acid with



4-ethylmorpholine


CGCI ® (IRGACOR 287):
polymeric amine salts


Supplier: Lawrence Industries:


HALOX FLASH ® X:
boric acid, phosphoric acid,



triethanolamine salts, 2-dimethyl-



aminoethanol







Zinc passivators








Supplier: Ciba-Geigy:



IRGAMET ® 42:
2,2 [[(5-methyl-1H-benzotriazol-



1-yl)methyl]imino]bisethanol


IRGAMET ® BTA M:
1H-benzotriazole.









EXAMPLE 1
The standard reference GEOMET® composition corresponds to:
















Deionized water
38.60%



DPG
10.29%



Boric acid
 0.65%



SYMPERONIC ® NP4
 1.51%



SYMPERONIC ® NP9
 1.64%



SILQUEST ® A187
 8.66%



Zinc*
32.12%



Aluminium**
 5.08%



SCHWEGO FOAM ®
 0.4%



NIPAR ® S10
 0.71%



AEROSOL ® TR70
 0.53%







*Lamellar zinc in the form of an approximately 95% paste in white spirit: zinc 31129/93 of ECKART WERKE;



**Lamellar aluminium in the form of an approximately 70% paste in DPG: CHROMAL VIII ® of ECKART WERKE.






To carry out the various comparative experiments on the aforementioned inhibitors, different baths were obtained by adding 1 g of inhibitor to 9 ml of water, the dispersion being maintained for 1 hour, then the mixture was added to 90 g of the aforementioned standard GEOMET® composition and then stirred for 3 hours.
The first layer of this composition to be tested was applied using a No. 38 Conway bar. The drying was carried out at 70° C. for approximately 20 minutes and then the curing was carried out at 300° C. for approximately 30 minutes.
The second layer was applied using an identical protocol.
The panels thus treated were then tested in a salt spray. The salt spray resistance results for the various coatings tested are given in the table below.









TABLE 1





Nature of the

in salt spray


inhibitor
Name of the inhibitor
without red rust

















Reference
GEOMET
112


Modified zinc
GEOMET + ZPA
134


phosphates
GEOMET + ZMP
122



GEOMET + SAPP
66



GEOMET + SRPP
66



GEOMET + ZCP
66



GEOMET + ZCPP
88



GEOMET + CAPP
66



GEOMET + ACTIROX 213
66



GEOMET + HALOX 391
66



GEOMET + K WHITE 84
88


Molybdates
GEOMET + ACTIROX 102
66



GEOMET + ACTIROX 106
88



GEOMET + MW 212
88



GEOMET + MW MZAP
88



GEOMET + Na2MoO4
66


Borates
GEOMET + BUTROL
44



GEOMET + BUSAN
112



GEOMET + HALOX 2230
66


Various
GEOMET + SHIELDEX
112



GEOMET + ALCOPHOR 827
66



GEOMET + IRGACOR 1930
88



GEOMET + IRGACOR 1405
88



GEOMET + CGCI
88



GEOMET + HALOX FLASH X
66



GEOMET + IRGAMET 42
44



GEOMET + IRGAMET BTAM
66


Invention
GEOMET + MoO3*
518





*MoO3: POR from CLIMAX Company






In addition, the more particular salt spray resistance results as a function of the age of the bath, and therefore of its stability at 4° C. and 20° C. respectively, are given in the appended FIGS. 1 and 2.
Both these figures show very clearly that, in each case, on the one hand, the anti-corrosion performance of the composition containing molybdenum oxide MoO3 is markedly improved and that, on the other hand, the anti-corrosion performance is maintained better over time when molybdenum oxide is added to the composition.
EXAMPLE 2
Two other types of comparative experiments were carried out, one on a GEOMET® composition and the other on a DACROMET® composition based on hexavalent chromium.
The formulations of these compositions are given in the tables below.







TABLE 2







GEOMET ®












Concentrations
Concentrations




in %
in %



Raw materials
without MoO3
with MoO3















Deionized water
38.60
37.83



DPG
10.29
10.08



Boric Acid
0.65
0.64



SYMPERONIC NP4 ®
1.51
1.48



SYMPERONIC NP9 ®
1.64
1.61



SILQUEST ® A187
8.66
8.47



Zinc*
32.12
31.48



Aluminium**
5.08
4.98



SCHWEGO FOAM ®
0.4
0.21



NIPAR ® S10
0.71
0.70



AEROSOL ® TR70
0.53
0.52



MoO3***
0
2







*Lamellar zinc in the form of an approximately 95% paste in white spirit: Zinc 31129/93 of ECKART WERKE;



**Lamellar aluminium in the form of an approximately 70% paste in DPG: CHROMAL VIII ® of ECKART WERKE.



***MoO3: POR from CLIMAX Company



SYMPERONIC ®: nonionic surfactants



SILQUEST ® A187: γ-glycidoxypropyltrimethoxysilane



SCHWEGO FOAM ®: hydrocarbon-type antifoam



NIPAR ® S10: nitropropane



AEROSOL ® TR70: anionic surfactant.













TABLE 3







DACROMET ®










Concentrations in %
Concentrations in %


Raw materials
without MoO3
with MoO3












Deionized water
47.86
44.90


DPG
15.95
15.63


PGME acetate
1.56
1.53


Chromic acid
3.81
3.73


REMCOPAL ® 334
0.72
0.71


REMCOPAL ® 339
0.72
0.71


Zinc*
23.61
23.14


Aluminium**
3.06
3.00


Boric acid
1.30
1.27


ZnO
1.41
1.38


MoO3***
0
2





*Lamellar zinc in the form of an approximately 95% paste in white spirit: Zinc 31129/93 of ECKART WERKE;


**Lamellar Aluminium in the form of an approximately 70% paste in DPG: CHROMAL VIII ® of ECKART WERKE.


***MoO3: POR from CLIMAX Company


REMCOPAL ®: nonionic surfactants.






It should be noted that the molybdenum oxide powder was each time introduced into the GEOMET® or DACROMET® bath by dusting. The bath was homogenized by stirring using a dispersive blade at 450 revolutions per minute.
The anti-corrosion compositions tested were applied to 10 cm×20 cm cold rolled low carbon steel panels by coating using the Conway bar, followed by predrying at 70° C. during about 20 minutes, and then cured in an oven at 300° C. for 30 minutes.
In the case of application to screws, the compositions were applied by dip-spinning and then cured under the same conditions as for the panels.
The observed salt spray resistance results according to the ISO 9227 standard are given schematically in the following table:









TABLE 4









Salt spray resistance*













Coating
Without
With 2%


PRODUCT
SUBSTRATE
weight**
MoO3
MoO3














Aqueous
Panels
32
288
>840


GEOMET ®


Aqueous
Screws
30
144
504


GEOMET ®


DACROMET ®
Screws
24
600
744





*Number of hours of exposure to salt spray before red rust appears.


**grams per square meter of coated surface, the thickness of the coatings are comprised between approximately about 6 μm and about 8 μm.






It is therefore apparent that introducing molybdenum oxide MoO3 into compositions in aqueous phase, GEOMET® or DACROMET® containing particulate zinc, improves the salt spray resistance of the said compositions very substantially.
Another aspect of the invention consists in adding an alkaline silicate to the composition in an amount comprised between 0.05% to 0.5% by weight.
The addition of alkaline silicate, for example sodium silicate, surprisingly enhances the film cohesion in a worthy way.
This is particularly illustrated in the following comparative example given in Table 5.
EXAMPLE 3
In this example, the cohesion is evaluated by applying a transparent adhesive paper on the coating surface and by quick pulling off. The cohesion is evaluated according to a scale from 0 (complete pulling off of the coating film) to 5 (no pulling off at all of the coating film).









TABLE 5






Composition
Composition



without silicate
with silicate



(concentrations
(concentrations


Raw materials
in %)
in %)

















Deionized water
38.13
37.96


Dipropylene glycol
10.08
10.08


Boric acid
0.64
0.64


Sympéronic NP4 ®
1.48
1.48


Sympéronic NP9 ®
1.61
1.61


Silane A187 ®
8.47
8.47


Zinc 31129/93
31.48
31.48


Aluminium CHROMAL VIII ®
4.98
4.98


Schwegofoam ®
0.21
0.21


NIPAR S10 ®
0.7
0.7


AEROSOL TR70 ®
0.52
0.52


MoO3
1
1


Silicate of sodium grade 42
0
0.17


Xanthan gum (1)
0.7
0.7





(1) Thickening agent in order to control the viscosity of the composition during application






The composition is applied onto steel panels which have previously been degreased, with a Conway rod, in order to obtain a weight of a coating layer of 30 g/m2. The plates are then cured under the same conditions as previously described.
They are then submitted to the salt spray test according to ISO 9227 and to the cohesion test. The results are shown in following Table 6.











TABLE 6








Without
With




alkaline
alkaline




silicate
silicate









Salt spray
694
720



(number of hours before appearance of red



rust)



Cohesion
1/5
5/5










This table shows that even if the resistance to the cohesion is not significantly modified, the cohesion on the contrary, is highly improved.

## Claims

1. An aqueous anti-corrosion coating composition for metal parts, which composition comprises
at least one particulate metal;
an organic solvent;
a thickener;
a silane-based binder;
molybdenum oxide; and
water.

2. The anti-corrosion coating composition of claim 1, which composition contains from 0.5% to 7% by weight of molybdenum oxide.

3. The anti-corrosion coating composition of claim 2, which composition contains approximately 2% by weight of molybdenum oxide.

4. The anti-corrosion coating composition of claim 1, which composition contains from 10% to 40% by weight of the at least one particulate metal.

5. The anti-corrosion coating composition of claim 1, in which said particulate metal is chosen from lamellar zinc and/or lamellar aluminum.

6. The anti-corrosion coating composition of claim 5, in which said particulate metal comprises lamellar zinc.

7. The anti-corrosion coating composition of claim 1, in which composition the organic solvent is a glycolether.

8. The anti-corrosion coating composition of claim 7, in which composition the organic solvent is diethylene glycol, triethylene glycol, or dipropylene glycol.

9. The anti-corrosion coating composition of claim 1, which composition contains from 0.005% to 2% by weight of the thickener.

10. The anti-corrosion coating composition of claim 9, in which thickener is a cellulose derivative.

11. The anti-corrosion coating composition of claim 10, in which thickener is hydroxymethylcellulose, hydroxypropylcellulose, or hydroxypropylmethylcellulose.

12. The anti-corrosion coating composition of claim 9, in which the thickener is xanthan gum or a polyurethane or acrylic thickener.

13. The anti-corrosion coating composition of claim 1, which composition contains from 3% to 20% by weight of silane, as the silane-based binder.

14. The anti-corrosion coating composition of claim 13, in which composition the silane comprises γ-glycidoxypropyltrimethoxysilane.

15. The anti-corrosion agent of claim 1, in which composition the silane-based binder carries epoxy functional groups.

16. The anti-corrosion coating composition of claim 1, in which composition the organic solvent contains up to approximately 10% by weight of white spirit.

17. The anti-corrosion coating composition of claim 1, which composition contains a silicate of sodium, potassium, or lithium.

18. The anti-corrosion coating composition of claim 1, which composition contains approximately 30% to 60% by weight of water.