# Patent

## Title
Initiation of controlled radical polymerization from lactide monomer

## Abstract

A lactide-functionalized polymer is synthesized by polymerizing a monomer capable of undergoing radical polymerization (e.g., styrenic, vinylic, acrylic, etc.) using a brominated lactide initiator via atom transfer radical polymerization (ATRP). In some embodiments of the present invention, the brominated lactide initiator is 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione prepared by reacting lactide with N-bromosuccinimide in the presence of benzoyl peroxide.

## Background
CROSS-REFERENCE TO RELATED APPLICATION
This patent application is a continuation application of pending U.S. patent application Ser. No. 14/243,034, filed Apr. 2, 2014, entitled “INITIATION OF CONTROLLED RADICAL POLYMERIZATION FROM LACTIDE MONOMER”, which is hereby incorporated herein by reference in its entirety.


BACKGROUND
The present invention relates in general to the field of biobased materials. More particularly, the present invention relates to lactide-functionalized polymers prepared from brominated lactide monomer using atom transfer radical polymerization (ATRP).
SUMMARY
In accordance with some embodiments of the present invention, a lactide-functionalized polymer is synthesized by polymerizing a monomer capable of undergoing radical polymerization (e.g., styrenic, vinylic, acrylic, etc.) using a brominated lactide initiator via atom transfer radical polymerization (ATRP). In some embodiments of the present invention, the brominated lactide initiator is 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione prepared by reacting lactide with N-bromosuccinimide in the presence of benzoyl peroxide.



BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS
Embodiments of the present invention will hereinafter be described in conjunction with the appended drawings, where like designations denote like elements.
FIG. 1 is a chemical reaction diagram showing the preparation of the lactide-functionalized polymer 3-poly(styrene)-3,6-dimethyl-1,4-dioxane-2,5-dione from the atom transfer radical polymerization (ATRP) of styrene using the brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione as an initiator in accordance with some embodiments of the present invention.
FIG. 2 is a chemical reaction diagram showing the preparation of the lactide-functionalized polymer 3-poly(butyl acrylate)-3,6-dimethyl-1,4-dioxane-2,5-dione from the atom transfer radical polymerization (ATRP) of butyl acrylate using the brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione as an initiator in accordance with some embodiments of the present invention.



DETAILED DESCRIPTION
The depletion of fossil fuels from which the majority of polymers are derived, combined with supply chain instability and cost fluctuations of feed chemicals used to make these polymers, is driving the development and utilization of biobased plastics for commodity applications. Polylactic acid (PLA), derived from starch and sugars, is a particularly appealing biobased plastic that is inexpensive and already being produced in large commercial quantities. In comparing polymers' material properties, polystyrene is often considered the petrochemical-based counterpart to PLA. Thus PLA is capable of replacing many petroleum-derived polymers in some applications. However, several of PLA's material properties—such as low heat-distortion temperature, high water adsorption, low flame retardancy, and low toughness—exclude the use of PLA in many applications. Moreover, additives to improve such properties are often expensive and/or come at the cost of sacrificing PLA's beneficial material properties. Hence much effort has been dedicated to directly incorporate chemical functionalities into the backbone of PLA (or PLA's monomer lactide) in order to tailor its properties, but because of the chemical lability of both lactide and PLA, examples of such chemical modification in the prior art typically are complex and low-yielding. A versatile and high-yielding approach to modify either PLA or lactide would greatly expand the profitability of PLA by virtue of its extension to many new end uses.
For purposes of this document, including the claims, the term “lactide” includes all stereoisomers of lactide (e.g., (S,S)-lactide, (R,R)-lactide, and (S,R)-lactide). (S,S)-lactide is also referred to as “L-lactide”. (R,R)-lactide is also referred to as “D-lactide”. (S,R)-lactide is also referred to as “meso-lactide”. A racemic mixture of D-lactide and L-lactide is often referred to as “DL-lactide”.
In accordance with some embodiments of the present invention, a simple, two-step method is employed to chemically modify lactide (PLA's monomer) in such a way that it can be functionalized with a wide array of different polymers designed to engineer specific properties to PLA. Brominated lactide (which may be formed in a one-step process from lactide monomer) can be used directly to initiate polymerization of a variety of monomers through a well-known, often-utilized process called atom-transfer radical polymerization (ATRP). This results in a lactide-functionalized polymer, i.e., a lactide molecule that is functionalized with a polymer. By using lactide as an ATRP-based initiator, it is possible to form well-defined, “living”, and low polydispersity index (PDI) polymers. Hence, in accordance with some embodiments of the present invention, only two well-defined, high-yielding chemical reactions are required to synthesize a lactide-functionalized polymer.
ATRP is a polymerization technique that is well known to those skilled in the art. ATRP is a controlled “living” free radical polymerization technique. A low concentration of active radicals is maintained to promote slow growth of the molecular weight and, hence, the “living” ATRP process is controlled. Lactide-functionalized polymers synthesized in accordance with some embodiments of the present invention are “living” polymers in the same sense. These polymers present no inherent termination mechanism.
The polydispersity index (PDI) is a measure of the distribution of molecular mass in a given polymer sample. PDI is defined as Mw/Mn, where Mw is the weight-average molecular weight and Mn is the number-average molecular weight. Lactide-functionalized polymers synthesized in accordance with some embodiments of the present invention have low PDI (e.g., PDI≦1.1).
Lactide-functionalized polymers synthesized in accordance with the present invention may be used in numerous applications. In an exemplary application, lactide-functionalized polymers synthesized in accordance with some embodiments of the present invention may be used as macromonomers. Generally, macromonomers are oligomers with a number-average molecular weight Mn between about 1000 and about 10,000 that contain at least one functional group suitable for further polymerization. In another exemplary application, the lactide endgroup of lactide-functionalized polymers synthesized in accordance with some embodiments of the present invention may be modified through hydrolysis or esterification to liberate more useful functional endgroups (e.g., hydroxyl, carboxylic acid, alkenyl, alkynl, and other endgroups) from which subsequent chemistry can be performed. In yet another exemplary application, lactide-functionalized polymers synthesized in accordance with some embodiments of the present invention may be used to functionalize surfaces, particles, or other functional polymers via a facile reaction of the lactide endgroup to hydroxyl or amine groups on the surface, particle, or other functional polymer.
A lactide-functionalized polymer is synthesized, in accordance with some embodiments of the present invention, by ATRP of a monomer capable of undergoing radical polymerization (e.g., styrenic, vinylic, acrylic, etc.) using 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione as a brominated lactide initiator. 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione may be prepared, for example, by reacting lactide with N-bromosuccinimide (NBS) in the presence of benzoyl peroxide. One skilled in the art will appreciate, however, that 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione may be prepared using any number of methods known to those skilled in the art. For example, 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione may be prepared by reacting lactide with bromine (Br2) in the presence of benzoyl peroxide.
Lactide is a commercially available biobased cyclic ester monomer that can be obtained from biomass. Lactide is the cyclic di-ester of lactic acid. Lactide may be prepared by heating lactic acid in the presence of an acid catalyst. Lactide is a solid at room temperature. The melting point temperature of each of L-lactide and D-lactide is between 95 and 97° C. Racemic lactide has a melting point temperature between 116 and 119° C. The melting point temperature of meso-lactide is less than 60° C. ( ̃53° C.).
The brominated lactide initiator, in the presence of a copper (I) and, optionally, copper (II) complex, an appropriate ligand (e.g., N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA)) and a monomer capable of undergoing radical polymerization (e.g., styrenic, vinylic, acrylic, etc.) undergoes an ATRP reaction to form a lactide-functionalized polymer with a polymer backbone (the identity of polymer may be chosen to tailor material properties) and a lactide endgroup capable of, for example, being polymerized through traditional PLA synthetic methods or using as a standalone initiator. As an illustrative example, polymerization of styrene via ATRP may be performed in tetrahydrofuran (THF) at 60-70° C. In this example, the concentration of styrene may be approximately 1.6 M and the ratio of styrene to 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione may be approximately 200. Alternatively, the ATRP reaction may be performed in a melt state (e.g., no solvent) using melt polymerization. Melt polymerization techniques are well known in the art.
As noted above, ATRP is a polymerization technique that is well known to those skilled in the art. ATRP can be used with myriad different monomers to produce myriad different polymers without undue experimentation. Generally, polymerization via ATRP is conducted under extremely low steady state concentration of active radicals, allowing propagation of the polymer chain to proceed with suppressed radical-radical coupling. For example, in some embodiments of the present invention, the monomer and initiator are added to a solution containing a catalytic copper/ligand complex (i.e., an ATRP catalyst and a ligand). Exemplary ATRP catalysts include, but are not limited to, copper(I) complexes such as copper(I) bromide (CuBr) and, optionally, copper(II) complexes such as copper(II) dibromide (CuBr2). Traditional ATRP can be done with added copper(II), but still must have some copper(I) added. Exemplary ligands include, but are not limited to, bipyridines such as 4,4′-dinonyl-2,2′bipyridine (DNBP) and bi-, tri- and tetradentate amines such as N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA).
In some embodiments of the present invention, the catalytic copper/ligand complex is deoxygenated using known techniques such as successive cycles of freeze-pump-thaw. One skilled in the art will appreciate, however, that other techniques for deoxygenating the mixture may be used in lieu of, or in addition to, successive cycles of freeze-pump-thaw.
The ratio of ATRP catalyst (e.g., CuBr) to monomer (e.g., styrene) can vary, although suitable results are obtained with ratios of 10:1-50:1. The ratio of monomer (e.g., styrene) to initiator (e.g., 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione) may also vary, although ratios of about 1:10-1:200 (or more) provide suitable results.
The polymerization is performed at an appropriate temperature, for example, 60-70° C. The appropriate temperature can vary, however, depending on a number of factors including, but not limited to, the identity of the monomer, the initiator, the ATRP catalyst, and the ligand, as well as the boiling point of the solvent, if any.
The order of addition of the reagents can have a profound affect on the initiator efficiency. To optimize this, the copper/ligand complex must be formed with a slight excess of copper prior to exposure to the brominated lactide initiator. Reaction Scheme 1, described below, is a general synthetic example of the polymerization in accordance with some embodiments of the present invention. In the first step of Reaction Scheme 1, brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione is prepared by reacting lactide with N-bromosuccinimide (NBS) in the presence of benzoyl peroxide. In the second step of Reaction Scheme 1, a lactide-functionalized polymer is obtained by ATRP of a monomer capable of undergoing radical polymerization (e.g., styrenic, vinylic, acrylic, etc.) initiated from the brominated lactide monomer in the presence of a copper (I) complex/PMDETA.




In the second step of Reaction Scheme 1, R is a hydrogen atom or a methyl group, and R′ is a phenyl group or C(O)OR′′, wherein R′′ is an alkyl group having one or more carbon atoms. Suitable examples of monomers capable of undergoing radical polymerization include, but are not limited to, styrene, butyl acrylate, methyl acrylate, 2-ethylhexyl acrylate, ethyl acrylate, 2-ethylhexl methacrylate, ethyl methacrylate, butyl methacrylate, and combinations thereof.
Lactide-functionalized polymers in accordance with some embodiments of the present invention are synthesized using L-lactide as the starting material. In the first step of Reaction Scheme 1, a bromine addition on the L-lactide is employed to synthesize brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione. In the second step of Reaction Scheme 1, a monomer capable of undergoing radical polymerization is polymerized via ATRP using the brominated lactide monomer as an initiator.
In the first step of Reaction Scheme 1, a mixture of L-lactide, benzene and N-bromosuccimide (NBS) are added to a three-neck flask and heated to reflux. Generally, stoichiometric amounts of L-lactide and NBS are used. Mechanical stirring is employed throughout reflux. A solution of benzoyl peroxide in benzene is then added dropwise over time through a dropping funnel, syringe or other suitable technique. Generally, any catalytic amount of benzoyl peroxide may be used. One skilled in the art will appreciate that any suitable solvent may be used in these solutions in lieu, or in addition to, benzene. Suitable solvents include, but are not limited to, benzene and acetonitrile. After the monomer is consumed, the reaction mixture is cooled to room temperature. The reaction product, which is brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione, may be purified using techniques well known in the art.
In the second step of Reaction Scheme 1, CuBr and N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA) are added to a first flask, along with a magnetic stirrer. The first flask is fitted with a rubber septum and degassed with three successive cycles of freeze-pump-thaw. Generally, the catalytic complex must be formed with a slight excess of copper ([Cu]0/[PMDETA]0>1) before exposure to the lactide initiator. Providing a slight excess of copper prevents undesirable side reactions. To a second flask are added some of the 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione prepared in the first step of Reaction Scheme 1, THF, and a monomer capable of undergoing radical polymerization. Generally, the ratio of [monomer]0/[3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione]0 that may be used ranges from 1:10-1:200 (or more). The second flask is fitted with a rubber septum and degassed by bubbling with N2 flow for at least 30 minutes. This mixture is then transferred into the first flask and the polymerization is carried out under stirring at a suitable temperature. Polymerization typically occurs over a period of hours. Generally, the polymerization of the monomer via ATRP may be performed in THF at 60-70° C. The reaction product, which is lactide-functionalized polymer 3-poly(monomer)-3,6-dimethyl-1,4-dioxane-2,5-dione, may be purified using techniques well known in the art.
One skilled in the art will appreciate that any suitable catalytic complex may be used in lieu, or in addition to, CuBr/PMDETA catalytic complex. Suitable catalytic complexes include both a suitable ATRP catalyst and a suitable ligand. Suitable ATRP catalysts include, but are not limited to, copper(I) complexes such as CuBr or other copper halides. Suitable ligands include, but are not limited to, bipyridines and bi-, tri- and tetradentate amines. Specific examples of suitable ligands include 4,4′-dinonyl-2,2′bipyridine (DNBP), N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA), and 1,1,4,7,10,10-hexamethyltriethylenetetramine (HMTETA).
PROPHETIC EXAMPLE 1
Synthesis of 3-poly(styrene)-3,6-dimethyl-1,4-dioxane-2,5-dione by polymerizing styrene via ATRP using 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione as an initiator
In this prophetic example, lactide-functionalized polymer 3-poly(styrene)-3,6-dimethyl-1,4-dioxane-2,5-dione is synthesized using L-lactide as the starting material. For this synthesis, as illustrated in FIG. 1, a bromine addition on the L-lactide is employed to synthesize brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione, followed by polymerization of styrene via ATRP using the brominated lactide monomer as an initiator.
Synthesis of 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione
To a 1 L three-neck flask are added L-lactide (100.0 g, 0.694 mol), benzene (500 mL) and N-bromosuccimide (NBS) (136.0 g, 0.764 mmol). The mixture is heated to reflux (approximately 80° C.). Mechanical stirring is employed throughout reflux.
A solution of benzoyl peroxide (3.36 g, 13.9 mmol) in benzene (50 mL) is then added dropwise through a dropping funnel over 20 minutes.
After the monomer is consumed, the reaction mixture is cooled to room temperature. Then, filtration is employed to separate the solid filtride from the liquid filtrate.
The solid filtride from the filtration is evaporated to dryness forming a pale yellow solid. The solid is dissolved in dichloromethane (750 mL) and the solution is washed with saturated sodium bisulfate solution three times and saturated NaCl solution once. The organic layer is dried over MgSO4, and the solution is evaporated to dryness. The orange solid is recrystallized from ethyl acetate and hexanes to produce 68.9 g of white crystals. One skilled in the art will appreciate that recrystallization may be performed in other suitable solutions.
The liquid filtrate from the filtration is evaporated to dryness, and the solid is recrystallized from ethyl acetate and hexanes to produce 27.1 g of white crystals. Here too, one skilled in the art will appreciate that recrystallization may be performed in other suitable solutions.
The combined yield (from both the solid filtride and the liquid filtrate) is 96.1 g (62%).
Synthesis of 3-poly(styrene)-3,6-dimethyl-1,4-dioxane-2,5-dione
To a first flask are added CuBr (70.5 mg, 0.49 mmol) and N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA) (77.5 mg, 0.45 mmol), as well as a magnetic stirrer. The first flask is fitted with a rubber septum and degassed with three successive cycles of freeze-pump-thaw. Generally, the catalytic complex must be formed with a slight excess of copper ([Cu]0/[PMDETA]0>1) before exposure to the lactide initiator. Providing a slight excess of copper prevents undesirable side reactions.
To a second flask are added some of the 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione (99.7 mg, 0.45 mmol) prepared in the first step of this example, THF (10 mL), and styrene (5 mL, 43.64 mmol). Generally, the ratio of [styrene]0/[3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione]0 that may be used ranges from 10 to 200. The second flask is fitted with a rubber septum and degassed by bubbling with N2 flow for at least 30 minutes. This mixture is then transferred into the first flask and the polymerization is carried out under stirring at 70° C. Polymerization occurs over a period of 0.5-4 hours. Generally, the polymerization of styrene via ATRP may be performed in THF at 60-70° C. for a [styrene]0 of 0.5-5 M and [styrene]0/[3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione]0 of 10-200.
Copper catalyst is removed by passing the reaction mixture diluted with THF through an alumina gel column.
The 3-poly(styrene)-3,6-dimethyl-1,4-dioxane-2,5-dione is recovered by precipitation in 7-fold excess of cold methanol, filtrated and dried up to constant weight.
PROPHETIC EXAMPLE 2
Synthesis of 3-poly(butyl acrylate)-3,6-dimethyl-1,4-dioxane-2,5-dione by polymerizing butyl acrylate via ATRP using 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione as an initiator
In this prophetic example, lactide-functionalized polymer 3-poly(butyl acrylate)-3,6-dimethyl-1,4-dioxane-2,5-dione is synthesized using L-lactide as the starting material. For this synthesis, as illustrated in FIG. 1, a bromine addition on the L-lactide is employed to synthesize brominated lactide monomer 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione, followed by polymerization of butyl acrylate via ATRP using the brominated lactide monomer as an initiator.
Synthesis of 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione
To a 1 L three-neck flask are added L-lactide (100.0 g, 0.694 mol), benzene (500 mL) and N-bromosuccimide (NBS) (136.0 g, 0.764 mmol). The mixture is heated to reflux (approximately 80° C.). Generally, stoichiometric amounts of L-lactide and NBS are used. Mechanical stirring is employed throughout reflux.
A solution of benzoyl peroxide (3.36 g, 13.9 mmol) in benzene (50 mL) is then added dropwise through a dropping funnel over 20 minutes.
After the monomer is consumed, the reaction mixture is cooled to room temperature. Then, filtration is employed to separate the solid filtride from the liquid filtrate.
The solid filtride from the filtration is evaporated to dryness forming a pale yellow solid. The solid is dissolved in dichloromethane (750 mL) and the solution is washed with saturated sodium bisulfate solution three times and saturated NaCl solution once. The organic layer is dried over MgSO4, and the solution is evaporated to dryness. The orange solid is recrystallized from ethyl acetate and hexanes to produce 68.9 g of white crystals. One skilled in the art will appreciate that recrystallization may be performed in other suitable solutions.
The liquid filtrate from the filtration is evaporated to dryness, and the solid is recrystallized from ethyl acetate and hexanes to produce 27.1 g of white crystals. Here too, one skilled in the art will appreciate that recrystallization may be performed in other suitable solutions.
The combined yield (from both the solid filtride and the liquid filtrate) is 96.1 g (62%).
Synthesis of 3-poly(butyl acrylate)-3,6-dimethyl-1,4-dioxane-2,5-dione
To a first flask are added CuBr (70.5 mg, 0.49 mmol) and N,N,N′,N′,N-pentamethyldiethylenetriamine (PMDETA) (77.5 mg, 0.45 mmol), as well as a magnetic stirrer. The first flask is fitted with a rubber septum and degassed with three successive cycles of freeze-pump-thaw. Generally, the catalytic complex must be formed with a slight excess of copper ([Cu]0/[PMDETA]0>1) before exposure to the lactide initiator. Providing a slight excess of copper prevents undesirable side reactions.
To a second flask are added some of the 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione (99.7 mg, 0.45 mmol) prepared in the first step of this example, THF (10 mL), and butyl acrylate (5 mL, 34.85 mmol). Generally, the ratio of [butyl acrylate]0/[3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione]0 that may be used ranges from 10 to 200. The flask is fitted with a rubber septum and degassed by bubbling with N2 flow for at least 30 minutes. This mixture is then transferred into the first flask and the polymerization is carried out under stirring at 70° C. Polymerization occurs over a period of 0.5-4 hours. Generally, the polymerization of butyl acrylate via ATRP may be performed in THF at 60-70° C. for a [butyl acrylate]0 of 0.5-5 M and [butyl acrylate]0/[3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione]0 of 10-200.
Copper catalyst is removed by passing the reaction mixture diluted with THF through an alumina gel column.
The 3-poly(butyl acrylate)-3,6-dimethyl-1,4-dioxane-2,5-dione is recovered by precipitation in 7-fold excess of cold methanol, filtrated and dried up to constant weight.
One skilled in the art will appreciate that many variations are possible within the scope of the present invention. Thus, while the present invention has been particularly shown and described with reference to preferred embodiments thereof, it will be understood by those skilled in the art that these and other changes in form and details may be made therein without departing from the spirit and scope of the present invention.

## Claims

1. A method for synthesizing a lactide-functionalized polymer, comprising:
polymerizing a monomer using a brominated lactide initiator via atom transfer radical polymerization (ATRP), wherein the brominated lactide initiator is 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione and wherein the monomer is represented by the following formula:




wherein R is a hydrogen atom or a methyl group, and wherein R′ is a phenyl group or C(O)OR′′, wherein R′′ is an alkyl group having one or more carbon atoms.

2. The method as recited in claim 1, wherein the monomer is selected from the group consisting of styrene, butyl acrylate, methyl acrylate, 2-ethylhexyl acrylate, ethyl acrylate, 2-ethylhexl methacrylate, ethyl methacrylate, butyl methacrylate, and combinations thereof.

3. The method as recited in claim 1, wherein the monomer is styrene.

4. The method as recited in claim 1, wherein the monomer is butyl acrylate.

5. The method as recited in claim 1, wherein the step of polymerizing a monomer using the brominated lactide initiator via atom transfer radical polymerization (ATRP) comprises the step of preparing a catalytic copper/ligand complex comprising a copper(I) complex and a ligand with a slight excess of copper prior to adding the brominated lactide initiator to the copper/ligand complex.

6. The method as recited in claim 1, further comprising the step of:
reacting lactide with N-bromosuccinimide in the presence of benzoyl peroxide to prepare the bromated lactide initiator.

7. The method as recited in claim 1, further comprising the step of:
reacting lactide with bromine (Br2) in the presence of benzoyl peroxide to prepare the bromated lactide initiator.

8. A method for synthesizing a lactide-functionalized polymer, comprising:
preparing a brominated lactide initiator, wherein the brominated lactide initiator is 3-bromo-3,6-dimethyl-1,4-dioxane-2,5-dione;
polymerizing a monomer using the brominated lactide initiator via atom transfer radical polymerization (ATRP), wherein the monomer is represented by the following formula:




wherein R is a hydrogen atom or a methyl group, and wherein R′ is a phenyl group or C(O)OR′′, wherein R′′ is an alkyl group having one or more carbon atoms.

9. The method as recited in claim 8, wherein the monomer is selected from the group consisting of styrene, butyl acrylate, methyl acrylate, 2-ethylhexyl acrylate, ethyl acrylate, 2-ethylhexl methacrylate, ethyl methacrylate, butyl methacrylate, and combinations thereof.

10. The method as recited in claim 8, wherein the monomer is styrene.

11. The method as recited in claim 8, wherein the monomer is butyl acrylate.

12. The method as recited in claim 8, wherein the step of polymerizing a monomer using the brominated lactide initiator via atom transfer radical polymerization (ATRP) comprises the step of preparing a catalytic copper/ligand complex comprising a copper(I) complex and a ligand with a slight excess of copper prior to adding the brominated lactide initiator to the copper/ligand complex.

13. The method as recited in claim 8, wherein the step of preparing a brominated lactide initiator comprises the step of reacting lactide with N-bromosuccinimide in the presence of benzoyl peroxide.

14. The method as recited in claim 8, wherein the step of preparing a brominated lactide initiator comprises the step of reacting lactide with bromine (Br2) in the presence of benzoyl peroxide.