# Patent

## Title
Nano-linked metallocene catalyst compositions and their polymer products

## Abstract

The present invention provides polymerization catalyst compositions employing novel dinuclear metallocene compounds. Methods for making these new dinuclear metallocene compounds and for using such compounds in catalyst compositions for the polymerization and copolymerization of olefins are also provided.

## Background
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is division of U.S. Ser. No. 11/965,848, filed on Dec. 28, 2007, now U.S. Pat. No. 7,863,210.


BACKGROUND OF THE INVENTION
The present invention relates generally to the field of olefin polymerization catalysis, catalyst compositions, methods for the polymerization and copolymerization of olefins, and polyolefins. More specifically, this invention relates to nano-linked dinuclear metallocene compounds and catalyst compositions employing such compounds.
A dinuclear metallocene compound can be produced via an olefin metathesis reaction, for example, as shown in Chem. Eur. J., 2003, 9, pp. 3618-3622. Olefin metathesis is a catalytic reaction between compounds that contain olefinic (e.g., alkene) moieties. Catalysts that are often employed in an olefin metathesis reaction include metals such as ruthenium, tungsten, molybdenum, or nickel.
SUMMARY OF THE INVENTION
The present invention generally relates to new catalyst compositions, methods for preparing catalyst compositions, methods for using the catalyst compositions to polymerize olefins, the polymer resins produced using such catalyst compositions, and articles produced using these polymer resins. In particular, the present invention relates to nano-linked dinuclear metallocene compounds and catalyst compositions employing such compounds. Catalyst compositions containing nano-linked dinuclear metallocene compounds of the present invention can be used to produce, for example, ethylene-based homopolymers and copolymers.
The present invention discloses novel dinuclear metallocene compounds having two metallocene moieties linked by an alkenyl group. According to one aspect of the present invention, these dinuclear compounds have the formula:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
Catalyst compositions containing these nano-linked dinuclear metallocene compounds are also provided by the present invention. In one aspect, a catalyst composition is disclosed which comprises a contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof. In this aspect, the dinuclear compound is as defined above in formula (I).
In another aspect, a catalyst composition comprising a contact product of at least one dinuclear metallocene compound and at least one activator-support is provided. This catalyst composition can further comprise at least one organoaluminum compound, as well as other co-catalysts. In these and other aspects, the at least one dinuclear metallocene compound is selected from:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
The present invention also contemplates a process for polymerizing olefins in the presence of a catalyst composition, the process comprising contacting the catalyst composition with at least one olefin monomer and optionally at least one olefin comonomer under polymerization conditions to produce a polymer or copolymer. The catalyst composition can comprise a contact product of at least one dinuclear metallocene compound and at least one activator-support. Other co-catalysts, including organoaluminum compounds, can be employed in this process.
Polymers produced from the polymerization of olefins, resulting in either homopolymers or copolymers, can be used to produce various articles of manufacture.



BRIEF DESCRIPTION OF THE FIGURES
FIG. 1 presents a mass spectrum plot of Example 2.
FIG. 2 presents an expanded mass spectrum plot of Example 2.
FIG. 3 presents an NMR plot of Example 3.
FIG. 4 presents an NMR plot of the reactant metallocene of Example 3.
FIG. 5 presents a dynamic melt viscosity versus frequency plot, measured at 190° C., for the polymers of Examples 4-7.
FIG. 6 presents a Delta versus complex modulus plot, measured at 190° C., for the polymers of Examples 4-7.
FIG. 7 presents the molecular weight distribution curves for the polymers of Examples 7 and 11.
FIG. 8 presents the molecular weight distribution curves for the polymers of Examples 6 and 10.
FIG. 9 presents the molecular weight distribution curves for the polymers of Examples 5 and 9.
FIG. 10 presents the molecular weight distribution curves for the polymers of Examples 4 and 8.



DEFINITIONS
To define more clearly the terms used herein, the following definitions are provided. To the extent that any definition or usage provided by any document incorporated herein by reference conflicts with the definition or usage provided herein, the definition or usage provided herein controls.
The term “polymer” is used herein to mean homopolymers comprising ethylene and copolymers of ethylene and a comonomer. “Polymer” is also used herein to mean homopolymers and copolymers of any olefin monomer disclosed herein (e.g., propylene).
The term “co-catalyst” is used generally herein to refer to organoaluminum compounds that can constitute one component of a catalyst composition. Additionally, “co-catalyst” refers to other components of a catalyst composition including, but not limited to, aluminoxanes, organozinc compounds, organoboron or organoborate compounds, ionizing ionic compounds, as disclosed herein. The term “co-catalyst” is used regardless of the actual function of the compound or any chemical mechanism by which the compound may operate. In one aspect of this invention, the term “co-catalyst” is used to distinguish that component of the catalyst composition from the dinuclear metallocene compound.
The term “fluoroorgano boron compound” is used herein with its ordinary meaning to refer to neutral compounds of the form BY3. The term “fluoroorgano borate compound” also has its usual meaning to refer to the monoanionic salts of a fluoroorgano boron compound of the form [cation]+[BY4]−, where Y represents a fluorinated organic group. Materials of these types are generally and collectively referred to as “organoboron or organoborate compounds.”
The term “contact product” is used herein to describe compositions wherein the components are contacted together in any order, in any manner, and for any length of time. For example, the components can be contacted by blending or mixing. Further, contacting of any component can occur in the presence or absence of any other component of the compositions described herein. Combining additional materials or components can be done by any suitable method. Further, the term “contact product” includes mixtures, blends, solutions, slurries, reaction products, and the like, or combinations thereof. Although “contact product” can include reaction products, it is not required for the respective components to react with one another.
The term “precontacted” mixture is used herein to describe a first mixture of catalyst components that are contacted for a first period of time prior to the first mixture being used to form a “postcontacted” or second mixture of catalyst components that are contacted for a second period of time. Typically, the precontacted mixture describes a mixture of metallocene compound (or compounds), olefin monomer, and organoaluminum compound (or compounds), before this mixture is contacted with an activator-support and optional additional organoaluminum compound. Thus, precontacted describes components that are used to contact each other, but prior to contacting the components in the second, postcontacted mixture. Accordingly, this invention may occasionally distinguish between a component used to prepare the precontacted mixture and that component after the mixture has been prepared. For example, according to this description, it is possible for the precontacted organoaluminum compound, once it is contacted with the metallocene and the olefin monomer, to have reacted to form at least one different chemical compound, formulation, or structure from the distinct organoaluminum compound used to prepare the precontacted mixture. In this case, the precontacted organoaluminum compound or component is described as comprising an organoaluminum compound that was used to prepare the precontacted mixture.
Similarly, the term “postcontacted” mixture is used herein to describe a second mixture of catalyst components that are contacted for a second period of time, and one constituent of which is the “precontacted” or first mixture of catalyst components that were contacted for a first period of time. Typically, the term “postcontacted” mixture is used herein to describe the mixture of metallocene compound, olefin monomer, organoaluminum compound, and activator-support (e.g., chemically-treated solid oxide), formed from contacting the precontacted mixture of a portion of these components with any additional components added to make up the postcontacted mixture. Generally, the additional component added to make up the postcontacted mixture is a chemically-treated solid oxide, and, optionally, can include an organoaluminum compound which is the same as or different from the organoaluminum compound used to prepare the precontacted mixture, as described herein. Accordingly, this invention may also occasionally distinguish between a component used to prepare the postcontacted mixture and that component after the mixture has been prepared.
The term “dinuclear metallocene,” as used herein, describes a compound comprising two metallocene moieties linked by a connecting group. The connecting group can be an alkenyl group resulting from the metathesis reaction or the saturated version resulting from hydrogenation or derivatization. Thus, the dinuclear metallocenes of this invention contain four η3 to η5-cyclopentadienyl-type moieties, wherein the η3 to η5-cycloalkadienyl moieties include cyclopentadienyl ligands, indenyl ligands, fluorenyl ligands, and the like, including partially saturated or substituted derivatives or analogs of any of these. Possible substituents on these ligands include hydrogen, therefore the description “substituted derivatives thereof” in this invention comprises partially saturated ligands such as tetrahydroindenyl, tetrahydrofluorenyl, octahydrofluorenyl, partially saturated indenyl, partially saturated fluorenyl, substituted partially saturated indenyl, substituted partially saturated fluorenyl, and the like. In some contexts, the dinuclear metallocene is referred to simply as the “catalyst,” in much the same way the term “co-catalyst” is used herein to refer to, for example, an organoaluminum compound. Unless otherwise specified, the following abbreviations are used: Cp for cyclopentadienyl; Ind for indenyl; and Flu for fluorenyl.
The terms “catalyst composition,” “catalyst mixture,” “catalyst system,” and the like, do not depend upon the actual product resulting from the contact or reaction of the components of the mixtures, the nature of the active catalytic site, or the fate of the co-catalyst, the dinuclear metallocene compound, any olefin monomer used to prepare a precontacted mixture, or the activator-support, after combining these components. Therefore, the terms “catalyst composition,” “catalyst mixture,” “catalyst system,” and the like, can include both heterogeneous compositions and homogenous compositions.
The term “hydrocarbyl” is used herein to specify a hydrocarbon radical group that includes, but is not limited to, aryl, alkyl, cycloalkyl, alkenyl, cycloalkenyl, cycloalkadienyl, alkynyl, aralkyl, aralkenyl, aralkynyl, and the like, and includes all substituted, unsubstituted, branched, linear, heteroatom substituted derivatives thereof.
The terms “chemically-treated solid oxide,” “solid oxide activator-support,” “treated solid oxide compound,” and the like, are used herein to indicate a solid, inorganic oxide of relatively high porosity, which exhibits Lewis acidic or Brønsted acidic behavior, and which has been treated with an electron-withdrawing component, typically an anion, and which is calcined. The electron-withdrawing component is typically an electron-withdrawing anion source compound. Thus, the chemically-treated solid oxide compound comprises a calcined contact product of at least one solid oxide compound with at least one electron-withdrawing anion source compound. Typically, the chemically-treated solid oxide comprises at least one ionizing, acidic solid oxide compound. The terms “support” and “activator-support” are not used to imply these components are inert, and such components should not be construed as an inert component of the catalyst composition. The activator-support of the present invention can be a chemically-treated solid oxide.
Although any methods, devices, and materials similar or equivalent to those described herein can be used in the practice or testing of the invention, the typical methods, devices and materials are herein described.
All publications and patents mentioned herein are incorporated herein by reference for the purpose of describing and disclosing, for example, the constructs and methodologies that are described in the publications, which might be used in connection with the presently described invention. The publications discussed throughout the text are provided solely for their disclosure prior to the filing date of the present application. Nothing herein is to be construed as an admission that the inventors are not entitled to antedate such disclosure by virtue of prior invention.
For any particular compound disclosed herein, any general structure presented also encompasses all conformational isomers, regioisomers, and stereoisomers that may arise from a particular set of substituents. The general structure also encompasses all enantiomers, diastereomers, and other optical isomers whether in enantiomeric or racemic forms, as well as mixtures of stereoisomers, as the context requires. For example, isomerized and hydrogenated forms of the general structure illustrated in formula (I) are also contemplated.
Applicants disclose several types of ranges in the present invention. These include, but are not limited to, a range of number of atoms, a range of integers, a range of weight ratios, a range of molar ratios, and so forth. When Applicants disclose or claim a range of any type, Applicants' intent is to disclose or claim individually each possible number that such a range could reasonably encompass, including end points of the range as well as any sub-ranges and combinations of sub-ranges encompassed therein. For example, when the Applicants disclose or claim a chemical moiety having a certain number of carbon atoms, Applicants' intent is to disclose or claim individually every possible number that such a range could encompass, consistent with the disclosure herein. For example, the disclosure that a moiety is a C1 to C10 linear or branched alkyl group, or in alternative language having from 1 to 10 carbon atoms, as used herein, refers to a moiety that can be selected independently from an alkyl group having 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10 carbon atoms, as well as any range between these two numbers (for example, a C1 to C6 alkyl group), and also including any combination of ranges between these two numbers (for example, a C2 to C4 and C6 to C8 alkyl group).
Similarly, another representative example follows for the weight ratio of organoaluminum to activator-support in a catalyst composition provided in one aspect of this invention. By a disclosure that the weight ratio of organoaluminum compound to activator-support is in a range from about 10:1 to about 1:1000, applicants intend to recite that the weight ratio can be selected from about 10:1, about 9:1, about 8:1, about 7:1, about 6:1, about 5:1, about 4:1, about 3:1, about 2:1, about 1:1, about 1:5, about 1:10, about 1:25, about 1:50, about 1:75, about 1:100, about 1:150, about 1:200, about 1:250, about 1:300, about 1:350, about 1:400, about 1:450, about 1:500, about 1:550, about 1:600, about 1:650, about 1:700, about 1:750, about 1:800, about 1:850, about 1:900, about 1:950, or about 1:1000. Additionally, the weight ratio can be within any range from about 10:1 to about 1:1000 (for example, the weight ratio is in a range from about 3:1 to about 1:100), and this also includes any combination of ranges between about 10:1 to about 1:1000. Likewise, all other ranges disclosed herein should be interpreted in a manner similar to these two examples.
Applicants reserve the right to proviso out or exclude any individual members of any such group, including any sub-ranges or combinations of sub-ranges within the group, that can be claimed according to a range or in any similar manner, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application. Further, Applicants reserve the right to proviso out or exclude any individual substituents, analogs, compounds, ligands, structures, or groups thereof, or any members of a claimed group, if for any reason Applicants choose to claim less than the full measure of the disclosure, for example, to account for a reference that Applicants may be unaware of at the time of the filing of the application.
While compositions and methods are described in terms of “comprising” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components or steps.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is directed generally to new catalyst compositions, methods for preparing catalyst compositions, methods for using the catalyst compositions to polymerize olefins, the polymer resins produced using such catalyst compositions, and articles produced using these polymer resins. In particular, the present invention relates to nano-linked dinuclear metallocene compounds and catalyst compositions employing such compounds.
Nano-linked metallocenes of the present invention are dinuclear molecules in which metallocene moieties are connected by an alkenyl linking group, or nano-link. Nano-linked metallocenes can be designed with specific angstrom distances between the two metal centers, where the distance is determined principally by the connecting linkage or linking group. The length, stereochemistry, and flexibility or rigidity of the linking group can be used to design catalysts which are either capable of, or incapable of, intra-molecular metal-to-metal interactions. For instance, under the restraint of the nano-link (e.g., an alkenyl linking group), nano-linked dinuclear metallocenes can offer unique co-catalyst interactions.
Dinuclear Metallocene Compounds
The present invention discloses novel compounds having two metallocene moieties linked by an alkenyl group, and methods of making these new compounds. These compounds are commonly referred to as dinuclear compounds, or binuclear compounds, because they contain two metal centers. Accordingly, in one aspect of this invention, the dinuclear compounds have the formula:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
Formula (I) above is not designed to show stereochemistry or isomeric positioning of the different moieties (e.g., this formula is not intended to display cis or trans isomers, or R or S diastereoisomers), although such compounds are contemplated and encompassed by this formula.
In formula (I), halides include fluorine, chlorine, bromine, and iodine atoms. As used herein, an aliphatic group includes linear or branched alkyl and alkenyl groups. Generally, the aliphatic group contains from 1 to 20 carbon atoms. Unless otherwise specified, alkyl and alkenyl groups described herein are intended to include all structural isomers, linear or branched, of a given moiety; for example, all enantiomers and all diastereomers are included within this definition. As an example, unless otherwise specified, the term propyl is meant to include n-propyl and iso-propyl, while the term butyl is meant to include n-butyl, iso-butyl, t-butyl, sec-butyl, and so forth. For instance, non-limiting examples of octyl isomers include 2-ethyl hexyl and neooctyl. Suitable examples of alkyl groups which can be employed in the present invention include, but are not limited to, methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or decyl, and the like. Examples of alkenyl groups within the scope of the present invention include, but are not limited to, ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, decenyl, and the like.
Aromatic groups and combinations with aliphatic groups include aryl and arylalkyl groups, and these include, but are not limited to, phenyl, alkyl-substituted phenyl, naphthyl, alkyl-substituted naphthyl, phenyl-substituted alkyl, naphthyl-substituted alkyl, and the like. Generally, such groups and combinations of groups contain less than 20 carbon atoms. Hence, non-limiting examples of such moieties that can be used in the present invention include phenyl, tolyl, benzyl, dimethylphenyl, trimethylphenyl, phenylethyl, phenylpropyl, phenylbutyl, propyl-2-phenylethyl, and the like. Cyclic groups include cycloalkyl and cycloalkenyl moieties and such moieties can include, but are not limited to, cyclopentyl, cyclopentenyl, cyclohexyl, cyclohexenyl, and the like. One example of a combination including a cyclic group is a cyclohexylphenyl group. Unless otherwise specified, any substituted aromatic or cyclic moiety used herein is meant to include all regioisomers; for example, the term tolyl is meant to include any possible substituent position, that is, ortho, meta, or para.
In formula (I), an alkenyl linking group is an alkenyl group that links or connects the two metallocene moieties. As illustrated in the above formula, the alkenyl linking group is attached to the metallocene moieties at a bridging group. A2 represents the bridging group in formula (I). A2 can have one or more substituents in addition to the alkenyl linking group.
In one aspect of the present invention, X1 and X2 independently are a substituted or unsubstituted aliphatic group having from 1 to 20 carbon atoms. In another aspect, X1 and X2 independently are methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or trimethylsilylmethyl. In yet another aspect, X1 and X2 independently are ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, or decenyl. X1 and X2 independently are a substituted or unsubstituted aromatic group, for example, having up to 20 carbon atoms, in another aspect of the present invention.
In a different aspect, X1 and X2 are both chlorine atoms. X1 and X2 independently can be selected from phenyl, naphthyl, tolyl, benzyl, dimethylphenyl, trimethylphenyl, phenylethyl, phenylpropyl, phenylbutyl, propyl-2-phenylethyl, cyclopentyl, cyclopentenyl, cyclohexyl, cyclohexenyl, or cyclohexylphenyl in other aspects of this invention. Yet, in another aspect, X1 and X2 independently are methyl, phenyl, benzyl, or a halide. Further, X1 and X2 independently can be methyl, phenyl, benzyl, or a chlorine atom in another aspect of the present invention.
In formula (I), X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, and are necessarily substituted with a bridging group, A2, as indicated in the formula above. In one aspect of the present invention, X3 and X4 independently are either a substituted cyclopentadienyl group or a substituted fluorenyl group. In another aspect, either X3 or X4 is a substituted cyclopentadienyl group, while the other is a substituted fluorenyl group.
Any substituents on X3 and X4 other than the bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group. Hydrogen is included, therefore the notion of a substituted indenyl and substituted fluorenyl includes partially saturated indenyls and fluorenyls including, but not limited to, tetrahydroindenyls, tetrahydrofluorenyls, and octahydrofluorenyls. Exemplary alkyls that can be substituents on X3 and X4 include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, or decyl, and the like. In one aspect, excluding the bridging group, each substituent on X3 and X4 independently is a hydrogen atom, or an ethyl, propyl, n-butyl, t-butyl, or hexyl group. In another aspect, substituents on X3 and X4 are selected independently from a hydrogen atom, ethenyl, propenyl, butenyl, pentenyl, hexenyl, heptenyl, octenyl, nonenyl, or decenyl, exclusive of the bridging group.
In formula (I), A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, which connects X3 and X4. In one aspect of this invention, A2 is a silicon bridging atom, a germanium bridging atom, a tin bridging atom, or a carbon bridging atom. Yet, in another aspect, A2 is a bridging chain of 2 to 5 carbon atoms, such as, for example, a two-carbon bridging chain that connects X3 and X4.
Other than the alkenyl linking group, any substituents on A2 are selected independently from a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof. In one aspect, for example, a substituent on A2 can be a methyl, ethyl, propyl, butyl, pentyl, hexyl, ethenyl, propenyl, butenyl, pentenyl, hexenyl, phenyl, naphthyl, tolyl, benzyl, cyclopentyl, cyclohexyl, or cyclohexylphenyl group, or a hydrogen atom. Yet, in another aspect, each substituent on the bridging group, other than the alkenyl linking group, is selected independently from a hydrogen atom, methyl group, phenyl group, naphthyl group, or cyclohexylphenyl group.
In formula (I), substituted aliphatic, aromatic, or cyclic groups, and combinations thereof, are disclosed, as well as substituted alkyl or alkenyl groups. Such groups described herein are intended to include substituted analogs with substitutions at any position on these groups that conform to the normal rules of chemical valence. Thus, groups substituted with one or more than one substituent are contemplated.
Such substituents, when present, are independently selected from an oxygen group, a sulfur group, a nitrogen group, a phosphorus group, an arsenic group, a carbon group, a silicon group, a germanium group, a tin group, a lead group, a boron group, an aluminum group, an inorganic group, an organometallic group, or a substituted derivative thereof, any of which having from 1 to about 20 carbon atoms; a halide; or hydrogen; as long as these groups do not terminate the activity of the catalyst composition. Examples of each of these substituent groups include, but are not limited to, the following groups.
Examples of halide substituents, in each occurrence, include fluoride, chloride, bromide, and iodide.
In each occurrence, oxygen groups are oxygen-containing groups, examples of which include, but are not limited to, alkoxy or aryloxy groups (—ORA), —OSiRA3, —OPRA2, —OAlRA2, and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms. Examples of alkoxy or aryloxy groups (—ORA) groups include, but are not limited to, methoxy, ethoxy, propoxy, butoxy, phenoxy, substituted phenoxy, and the like.
In each occurrence, sulfur groups are sulfur-containing groups, examples of which include, but are not limited to, —SRA and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, nitrogen groups are nitrogen-containing groups, which include, but are not limited to, —NRA2 and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, phosphorus groups are phosphorus-containing groups, which include, but are not limited to, —PRA, —P(ORA)2, and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, arsenic groups are arsenic-containing groups, which include, but are not limited to, —AsRA2, —As(ORA)2, and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, carbon groups are carbon-containing groups, which include, but are not limited to, alkyl halide groups that comprise halide-substituted alkyl groups with 1 to 20 carbon atoms, aralkyl groups with 1 to 20 carbon atoms, —C(NRA)H, —C(NRA)RA, —C(NRA)ORA, and the like, including substituted derivatives thereof, wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, silicon groups are silicon-containing groups, which include, but are not limited to, silyl groups such as alkylsilyl groups, arylsilyl groups, arylalkylsilyl groups, siloxy groups, and the like, which in each occurrence have from 1 to 20 carbon atoms. For example, silicon group substituents include trimethylsilyl and phenyloctylsilyl groups.
In each occurrence, germanium groups are germanium-containing groups, which include, but are not limited to, germyl groups such as alkylgermyl groups, arylgermyl groups, arylalkylgermyl groups, germyloxy groups, and the like, which in each occurrence have from 1 to 20 carbon atoms.
In each occurrence, tin groups are tin-containing groups, which include, but are not limited to, stannyl groups such as alkylstannyl groups, arylstannyl groups, arylalkylstannyl groups, stannoxy (or “stannyloxy”) groups, and the like, which in each occurrence have from 1 to 20 carbon atoms. Thus, tin groups include, but are not limited to, stannoxy groups.
In each occurrence, lead groups are lead-containing groups, which include, but are not limited to, alkyllead groups, aryllead groups, arylalkyllead groups, and the like, which in each occurrence, have from 1 to 20 carbon atoms.
In each occurrence, boron groups are boron-containing groups, which include, but are not limited to, —BRA2, —BX2, —BRAX, and the like, wherein X is a monoanionic group such as hydride, alkoxide, alkyl thiolate, and the like, and wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
In each occurrence, aluminum groups are aluminum-containing groups, which include, but are not limited to, —AlRA, —AlX2, —AlRAX, wherein X is a monoanionic group such as hydride, alkoxide, alkyl thiolate, and the like, and wherein RA in each occurrence can be alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl having from 1 to 20 carbon atoms.
Examples of inorganic groups that may be used as substituents, in each occurrence include, but are not limited to, —OAlX2, —OSiX3, —OPX2, —SX, —AsX2, —PX2, and the like, wherein X is a monoanionic group such as hydride, amide, alkoxide, alkyl thiolate, and the like, and wherein any alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, or substituted aralkyl group or substituent on these ligands has from 1 to 20 carbon atoms.
Examples of organometallic groups that may be used as substituents, in each occurrence, include, but are not limited to, organoboron groups, organoaluminum groups, organogallium groups, organosilicon groups, organogermanium groups, organotin groups, organolead groups, organo-transition metal groups, and the like, having from 1 to 20 carbon atoms.
Formula (I), depicted above, illustrates that the dinuclear compounds of the present invention are homonuclear, because each metallocene moiety linked by the alkenyl linking group is the same and contains the same metal center. M is selected from Zr, Hf, or Ti in the present invention.
RX, RY, and RZ in the alkenyl linking group independently are selected from a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof. In one aspect of the present invention, RX, RY, and RZ independently are a substituted or unsubstituted aliphatic group having from 1 to 20 carbon atoms. For example, RX, RY, and RZ can be selected independently from methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, or trimethylsilylmethyl. In another aspect, RX, RY, and RZ are hydrogen atoms. RX, RY, and RZ independently are a substituted or unsubstituted aromatic group, for example, having up to 20 carbon atoms, in yet another aspect of the present invention.
RX, RY, and RZ independently are a methyl, ethyl, propyl, butyl, pentyl, hexyl, phenyl, naphthyl, tolyl, benzyl, cyclopentyl, cyclohexyl, or cyclohexylphenyl group, or a hydrogen atom, in other aspects of this invention. Further, RX, RY, and RZ independently can be methyl, phenyl, benzyl, or a hydrogen atom in another aspect of the present invention.
The integer n in formula (I) determines the length of the alkenyl linking group and ranges from 0 to 12, inclusive. In one aspect of this invention, n is equal to 0, 1, 2, 3, 4, 5, 6, or 7. In a different aspect of the present invention, n is 1, 2, 3, or 4.
According to yet another aspect of the present invention, both X1 and X2 are methyl groups, phenyl groups, or chlorine atoms. In this aspect, either X3 or X4 is a substituted cyclopentadienyl group, and the other is a substituted fluorenyl group. The substituted cyclopentadienyl group is substituted with the bridging group A2, and optionally can be further substituted. In one aspect, the substituted fluorenyl group is substituted with two butyl substituents, for example, two tert-butyl substituents. In these and other aspects, M is Zr or Hf; RX, RY, and RZ are hydrogen atoms; n is 0, 1, 2, 3, or 4; and A2 is a carbon atom having either methyl or phenyl as an optional substituent.
In accordance with another aspect of the present invention, both X1 and X2 in formula (I) are chlorine atoms. In this aspect, n is in range from 1 to 10, inclusive.
An example of a dinuclear compound in accordance with the present invention is the following compound, which is abbreviated “DMET 1” throughout this disclosure:




Other illustrative and non-limiting examples of dinuclear compounds of the present invention include the following:




and the like. Applicants have used the abbreviation Ph for phenyl.

Methods of making a dinuclear compound of the present invention are also provided. One such method for synthesizing a dinuclear metallocene compound is illustrated in the general reaction scheme provided below:




A metallocene catalyst having an alkenyl substituent is linked to itself via the olefin metathesis reaction in the presence of a suitable catalyst. Generally, the alkenyl substituent can be of any length, and can be, for example, a substituent on a bridging group. In the reaction product, the metallocene moieties are connected by an alkenyl linking group. Ethylene gas is also produced in this reaction.
Various metal-based catalysts can be employed in an olefin metathesis reaction. The metals often used include ruthenium, tungsten, molybdenum, and nickel. In the examples that follow, a Grubbs 1st Generation Metathesis Catalyst based on ruthenium was employed, but this invention is not limited to any particular metathesis catalyst.
Metathesis reactions can be conducted in the presence of a solvent such as, for example, aliphatic, aromatic, or saturated ester solvents. Suitable solvents useful in the production of dinuclear metallocene compounds include, but are not limited to, benzene, toluene, heptane, isobutane, methylene chloride, and the like. Solvent selection can depend upon many factors, for instance, the desired reaction temperature and solubility of either the metallocene reactant or the dinuclear metallocene in the particular solvent.
Suitable olefin metathesis reaction temperatures to produce dinuclear metallocene compounds of the present invention are generally in a range from about −50° C. to about 150° C. For example, the reaction temperature can be in the range from about 0° C. to about 100° C. The reaction temperature selected is often a compromise between many variables, such as the solvent employed, reaction pressure, reaction time, quantity and type of catalyst, product yield and selectivity, and isomer ratio, if desired. Further, the metathesis reaction equilibrium can be driven towards the dinuclear metallocene product if ethylene gas is removed or vented from the reaction system.
Generally, there is no limitation on the selection of the metallocene compound that can be used to form the dinuclear compounds of the present invention, other than the presence of an alkenyl substituent on the bridging group. Some examples of metallocene compounds that can be used to produce dinuclear compounds of the present invention via the olefin metathesis reaction scheme above include, but are not limited to:







and the like. Applicants have used the abbreviation Ph for phenyl.

Additional examples of metallocene compounds that are suitable for use to produce dinuclear compounds of the present invention are contemplated. These include, but are not limited to:



















and the like. Applicants have used the abbreviation Ph for phenyl, and Me for methyl.

Bridged metallocene compounds having, for example, two-carbon bridging chains also can be used to produce dinuclear compounds of the present invention. Representative two-carbon bridged metallocene compounds include, but are not limited to:










and the like. Applicants have used the abbreviations Ph for phenyl, Me for methyl, and t-Bu for tert-butyl. The integer n′ in these metallocene compounds generally ranges from 0 to about 10, inclusive. For example, n′ can be 1, 2, 3, 4, 5, 6, 7, or 8.

Additional bridged metallocene compounds can be used to produce dinuclear compounds of the present invention. Therefore, the scope of the present invention is not limited to the starting metallocene species provided above.
Catalyst Composition
The present invention also relates to catalyst compositions employing dinuclear metallocene compounds. According to one aspect of the present invention, a catalyst composition is provided which comprises a contact product of at least one dinuclear metallocene compound and at least one activator-support. This catalyst composition can further comprise at least one organoaluminum compound. These catalyst compositions can be utilized to produce polyolefins, both homopolymers and copolymers, for a variety of end-use applications. The at least one dinuclear metallocene compound in these catalyst compositions has the formula:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
In accordance with this and other aspects of the present invention, it is contemplated that the catalyst compositions disclosed herein can contain more than one dinuclear metallocene compound and/or more than one activator-support. Additionally, more than one organoaluminum compound is also contemplated.
In another aspect of the present invention, a catalyst composition is provided which comprises a contact product of at least one dinuclear metallocene compound, at least one activator-support, and at least one organoaluminum compound, wherein this catalyst composition is substantially free of aluminoxanes, organozinc compounds, organoboron or organoborate compounds, and ionizing ionic compounds. In this aspect, the catalyst composition has catalyst activity, to be discussed below, in the absence of these additional co-catalysts.
However, in other aspects of this invention, these co-catalysts can be employed. For example, a catalyst composition comprising at least one dinuclear metallocene compound and at least one activator-support can further comprise at least one optional co-catalyst. Suitable co-catalysts in this aspect include, but are not limited to, aluminoxane compounds, organozinc compounds, organoboron or organoborate compounds, ionizing ionic compounds, and the like, or any combination thereof. More than one co-catalyst can be present in the catalyst composition.
In a different aspect, a catalyst composition is provided which does not require an activator-support. Such a catalyst composition comprises the contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or combinations thereof. In this aspect, the at least one dinuclear metallocene compound is selected from:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
Activator-Support
The present invention encompasses various catalyst compositions which can include an activator-support. In one aspect, the activator-support comprises a chemically-treated solid oxide. Alternatively, the activator-support can comprise a clay mineral, a pillared clay, an exfoliated clay, an exfoliated clay gelled into another oxide matrix, a layered silicate mineral, a non-layered silicate mineral, a layered aluminosilicate mineral, a non-layered aluminosilicate mineral, or any combination thereof.
The chemically-treated solid oxide exhibits enhanced acidity as compared to the corresponding untreated solid oxide compound. The chemically-treated solid oxide also functions as a catalyst activator as compared to the corresponding untreated solid oxide. While the chemically-treated solid oxide activates the metallocene in the absence of co-catalysts, it is not necessary to eliminate co-catalysts from the catalyst composition. The activation function of the activator-support is evident in the enhanced activity of catalyst composition as a whole, as compared to a catalyst composition containing the corresponding untreated solid oxide. However, it is believed that the chemically-treated solid oxide can function as an activator, even in the absence of an organoaluminum compound, aluminoxanes, organoboron compounds, ionizing ionic compounds, and the like.
The chemically-treated solid oxide can comprise at least one solid oxide treated with at least one electron-withdrawing anion. While not intending to be bound by the following statement, it is believed that treatment of the solid oxide with an electron-withdrawing component augments or enhances the acidity of the oxide. Thus, either the activator-support exhibits Lewis or Brønsted acidity that is typically greater than the Lewis or Brønsted acid strength of the untreated solid oxide, or the activator-support has a greater number of acid sites than the untreated solid oxide, or both. One method to quantify the acidity of the chemically-treated and untreated solid oxide materials is by comparing the polymerization activities of the treated and untreated oxides under acid catalyzed reactions.
The chemically-treated solid oxide of this invention is formed generally from an inorganic solid oxide that exhibits Lewis acidic or Brønsted acidic behavior and has a relatively high porosity. The solid oxide is chemically-treated with an electron-withdrawing component, typically an electron-withdrawing anion, to form an activator-support.
According to one aspect of the present invention, the solid oxide used to prepare the chemically-treated solid oxide has a pore volume greater than about 0.1 cc/g. According to another aspect of the present invention, the solid oxide has a pore volume greater than about 0.5 cc/g. According to yet another aspect of the present invention, the solid oxide has a pore volume greater than about 1.0 cc/g.
In another aspect, the solid oxide has a surface area of from about 100 to about 1000 m2/g. In yet another aspect, the solid oxide has a surface area of from about 200 to about 800 m2/g. In still another aspect of the present invention, the solid oxide has a surface area of from about 250 to about 600 m2/g.
The chemically-treated solid oxide can comprise a solid inorganic oxide comprising oxygen and at least one element selected from Group 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, or 15 of the periodic table, or comprising oxygen and at least one element selected from the lanthanide or actinide elements. (See: Hawley's Condensed Chemical Dictionary, 11th Ed., John Wiley & Sons; 1995; Cotton, F. A.; Wilkinson, G.; Murillo; C. A.; and Bochmann; M. Advanced Inorganic Chemistry, 6th Ed., Wiley-Interscience, 1999.) For example, the inorganic oxide can comprise oxygen and at least one element selected from Al, B, Be, Bi, Cd, Co, Cr, Cu, Fe, Ga, La, Mn, Mo, Ni, Sb, Si, Sn, Sr, Th, Ti, V, W, P, Y, Zn or Zr.
Suitable examples of solid oxide materials or compounds that can be used to form the chemically-treated solid oxide include, but are not limited to, Al2O3, B2O3, BeO, Bi2O3, CdO, CO3O4, Cr2O3, CuO, Fe2O3, Ga2O3, La2O3, Mn2O3, MoO3, NiO, P2O5, Sb2O5, SiO2, SnO2, SrO, ThO2, TiO2, V2O5, WO3, Y2O3, ZnO, ZrO2, and the like, including mixed oxides thereof, and combinations thereof. For example, the solid oxide can be silica, alumina, silica-alumina, aluminum phosphate, heteropolytungstates, Mania, zirconia, magnesia, boria, zinc oxide, mixed oxides thereof, or any combination thereof.
The solid oxide of this invention encompasses oxide materials such as alumina, “mixed oxide” compounds thereof such as silica-alumina, and combinations and mixtures thereof. The mixed oxide compounds such as silica-alumina can be single or multiple chemical phases with more than one metal combined with oxygen to form a solid oxide compound. Examples of mixed oxides that can be used in the activator-support of the present invention include, but are not limited to, silica-alumina, silica-titania, silica-zirconia, zeolites, various clay minerals, alumina-titania, alumina-zirconia, zinc-aluminate, and the like.
The electron-withdrawing component used to treat the solid oxide can be any component that increases the Lewis or Brønsted acidity of the solid oxide upon treatment (as compared to the solid oxide that is not treated with at least one electron-withdrawing anion). According to one aspect of the present invention, the electron-withdrawing component is an electron-withdrawing anion derived from a salt, an acid, or other compound, such as a volatile organic compound, that serves as a source or precursor for that anion. Examples of electron-withdrawing anions include, but are not limited to, sulfate, bisulfate, fluoride, chloride, bromide, iodide, fluorosulfate, fluoroborate, phosphate, fluorophosphate, trifluoroacetate, triflate, fluorozirconate, fluorotitanate, trifluoroacetate, triflate, and the like, including mixtures and combinations thereof. In addition, other ionic or non-ionic compounds that serve as sources for these electron-withdrawing anions also can be employed in the present invention.
Thus, for example, the chemically-treated solid oxide used in the catalyst compositions of the present can be fluorided alumina, chlorided alumina, bromided alumina, sulfated alumina, fluorided silica-alumina, chlorided silica-alumina, bromided silica-alumina, sulfated silica-alumina, fluorided silica-zirconia, chlorided silica-zirconia, bromided silica-zirconia, sulfated silica-zirconia, and the like, or combinations thereof.
When the electron-withdrawing component comprises a salt of an electron-withdrawing anion, the counterion or cation of that salt can be selected from any cation that allows the salt to revert or decompose back to the acid during calcining. Factors that dictate the suitability of the particular salt to serve as a source for the electron-withdrawing anion include, but are not limited to, the solubility of the salt in the desired solvent, the lack of adverse reactivity of the cation, ion-pairing effects between the cation and anion, hygroscopic properties imparted to the salt by the cation, and the like, and thermal stability of the anion. Examples of suitable cations in the salt of the electron-withdrawing anion include, but are not limited to, ammonium, trialkyl ammonium, tetraalkyl ammonium, tetraalkyl phosphonium, H+, [H(OEt2)2]+, and the like.
Further, combinations of one or more different electron-withdrawing anions, in varying proportions, can be used to tailor the specific acidity of the activator-support to the desired level. Combinations of electron-withdrawing components can be contacted with the oxide material simultaneously or individually, and in any order that affords the desired chemically-treated solid oxide acidity. For example, one aspect of this invention is employing two or more electron-withdrawing anion source compounds in two or more separate contacting steps.
Thus, one example of such a process by which an chemically-treated solid oxide is prepared is as follows: a selected solid oxide compound, or combination of oxide compounds, is contacted with a first electron-withdrawing anion source compound to form a first mixture; this first mixture is calcined and then contacted with a second electron-withdrawing anion source compound to form a second mixture; the second mixture is then calcined to form a treated solid oxide compound. In such a process, the first and second electron-withdrawing anion source compounds are either the same or different compounds.
According to another aspect of the present invention, the chemically-treated solid oxide comprises a solid inorganic oxide material, a mixed oxide material, or a combination of inorganic oxide materials, that is chemically-treated with an electron-withdrawing component, and optionally treated with a metal source, including metal salts, metal ions, or other metal-containing compounds. Non-limiting examples of the metal or metal ion include zinc, nickel, vanadium, titanium, silver, copper, gallium, tin, tungsten, molybdenum, and the like, or combinations thereof. Examples of chemically-treated solid oxides that contain a metal or metal ion include, but are not limited to, zinc-impregnated chlorided alumina, titanium-impregnated fluorided alumina, zinc-impregnated fluorided alumina, zinc-impregnated chlorided silica-alumina, zinc-impregnated fluorided silica-alumina, zinc-impregnated sulfated alumina, chlorided zinc aluminate, fluorided zinc aluminate, sulfated zinc aluminate, and the like, or any combination thereof.
Any method of impregnating the solid oxide material with a metal can be used. The method by which the oxide is contacted with a metal source, typically a salt or metal-containing compound, can include, but is not limited to, gelling, co-gelling, impregnation of one compound onto another, and the like. If desired, the metal-containing compound is added to or impregnated into the solid oxide in solution form, and subsequently converted into the supported metal upon calcining. Accordingly, the solid inorganic oxide can further comprise a metal selected from zinc, titanium, nickel, vanadium, silver, copper, gallium, tin, tungsten, molybdenum, and the like, or combinations of these metals. For example, zinc is often used to impregnate the solid oxide because it can provide improved catalyst activity at a low cost.
The solid oxide can be treated with metal salts or metal-containing compounds before, after, or at the same time that the solid oxide is treated with the electron-withdrawing anion. Following any contacting method, the contacted mixture of oxide compound, electron-withdrawing anion, and the metal ion is typically calcined. Alternatively, a solid oxide material, an electron-withdrawing anion source, and the metal salt or metal-containing compound are contacted and calcined simultaneously.
Various processes are used to form the chemically-treated solid oxide useful in the present invention. The chemically-treated solid oxide can comprise the contact product of at least one solid oxide compound and at least one electron-withdrawing anion source. It is not required that the solid oxide compound be calcined prior to contacting the electron-withdrawing anion source. The contact product typically is calcined either during or after the solid oxide compound is contacted with the electron-withdrawing anion source. The solid oxide compound can be calcined or uncalcined. Various processes to prepare solid oxide activator-supports that can be employed in this invention have been reported. For example, such methods are described in U.S. Pat. Nos. 6,107,230, 6,165,929, 6,294,494, 6,300,271, 6,316,553, 6,355,594, 6,376,415, 6,388,017, 6,391,816, 6,395,666, 6,524,987, 6,548,441, 6,548,442, 6,576,583, 6,613,712, 6,632,894, 6,667,274, and 6,750,302, the disclosures of which are incorporated herein by reference in their entirety.
According to one aspect of the present invention, the solid oxide material is chemically-treated by contacting it with at least one electron-withdrawing component, typically an electron-withdrawing anion source. Further, the solid oxide material optionally is chemically treated with a metal ion, and then calcined to form a metal-containing or metal-impregnated chemically-treated solid oxide. According to another aspect of the present invention, the solid oxide material and electron-withdrawing anion source are contacted and calcined simultaneously.
The method by which the oxide is contacted with the electron-withdrawing component, typically a salt or an acid of an electron-withdrawing anion, can include, but is not limited to, gelling, co-gelling, impregnation of one compound onto another, and the like. Thus, following any contacting method, the contacted mixture of the solid oxide, electron-withdrawing anion, and optional metal ion, is calcined.
The solid oxide activator-support (i.e., chemically-treated solid oxide) thus can be produced by a process comprising:
1) contacting a solid oxide compound with at least one electron-withdrawing anion source compound to form a first mixture; and
2) calcining the first mixture to form the solid oxide activator-support.
According to another aspect of the present invention, the solid oxide activator-support (chemically-treated solid oxide) is produced by a process comprising:
1) contacting at least one solid oxide compound with a first electron-withdrawing anion source compound to form a first mixture;
2) calcining the first mixture to produce a calcined first mixture;
3) contacting the calcined first mixture with a second electron-withdrawing anion source compound to form a second mixture; and
4) calcining the second mixture to form the solid oxide activator-support.
According to yet another aspect of the present invention, the chemically-treated solid oxide is produced or formed by contacting the solid oxide with the electron-withdrawing anion source compound, where the solid oxide compound is calcined before, during, or after contacting the electron-withdrawing anion source, and where there is a substantial absence of aluminoxanes, organoboron or organoborate compounds, and ionizing ionic compounds.
Calcining of the treated solid oxide generally is conducted in an ambient atmosphere, typically in a dry ambient atmosphere, at a temperature from about 200° C. to about 900° C., and for a time of about 1 minute to about 100 hours. Calcining can be conducted at a temperature of from about 300° C. to about 800° C., or alternatively, at a temperature of from about 400° C. to about 700° C. Calcining can be conducted for about 1 hour to about 50 hours, or for about 3 hours to about 20 hours. Thus, for example, calcining can be carried out for about 1 to about 10 hours at a temperature of from about 350° C. to about 550° C. Any suitable ambient atmosphere can be employed during calcining. Generally, calcining is conducted in an oxidizing atmosphere, such as air. Alternatively, an inert atmosphere, such as nitrogen or argon, or a reducing atmosphere, such as hydrogen or carbon monoxide, can be used.
According to one aspect of the present invention, the solid oxide material is treated with a source of halide ion, sulfate ion, or a combination of anions, optionally treated with a metal ion, and then calcined to provide the chemically-treated solid oxide in the form of a particulate solid. For example, the solid oxide material is treated with a source of sulfate (termed a “sulfating agent”), a source of chloride ion (termed a “chloriding agent”), a source of fluoride ion (termed a “fluoriding agent”), or a combination thereof, and calcined to provide the solid oxide activator. Useful acidic activator-supports include, but are not limited to, bromided alumina, chlorided alumina, fluorided alumina, sulfated alumina, bromided silica-alumina, chlorided silica-alumina, fluorided silica-alumina, sulfated silica-alumina, bromided silica-zirconia, chlorided silica-zirconia, fluorided silica-zirconia, sulfated silica-zirconia; a pillared clay, such as a pillared montmorillonite, optionally treated with fluoride, chloride, or sulfate; phosphated alumina or other aluminophosphates optionally treated with sulfate, fluoride, or chloride; or any combination of the above. Further, any of these activator-supports optionally can be treated with a metal ion.
The chemically-treated solid oxide can comprise a fluorided solid oxide in the form of a particulate solid. The fluorided solid oxide can be formed by contacting a solid oxide with a fluoriding agent. The fluoride ion can be added to the oxide by forming a slurry of the oxide in a suitable solvent such as alcohol or water including, but not limited to, the one to three carbon alcohols because of their volatility and low surface tension. Examples of suitable fluoriding agents include, but are not limited to, hydrofluoric acid (HF), ammonium fluoride (NH4F), ammonium bifluoride (NH4HF2), ammonium tetrafluoroborate (NH4BF4), ammonium silicofluoride (hexafluorosilicate) ((NH4)2SiF6), ammonium hexafluorophosphate (NH4PF6), analogs thereof, and combinations thereof. For example, ammonium bifluoride NH4HF2 can be used as the fluoriding agent, due to its ease of use and availability.
If desired, the solid oxide is treated with a fluoriding agent during the calcining step. Any fluoriding agent capable of thoroughly contacting the solid oxide during the calcining step can be used. For example, in addition to those fluoriding agents described previously, volatile organic fluoriding agents can be used. Examples of volatile organic fluoriding agents useful in this aspect of the invention include, but are not limited to, freons, perfluorohexane, perfluorobenzene, fluoromethane, trifluoroethanol, an the like, and combinations thereof. Gaseous hydrogen fluoride or fluorine itself also can be used with the solid oxide if fluorided while calcining. One convenient method of contacting the solid oxide with the fluoriding agent is to vaporize a fluoriding agent into a gas stream used to fluidize the solid oxide during calcination.
Similarly, in another aspect of this invention, the chemically-treated solid oxide comprises a chlorided solid oxide in the form of a particulate solid. The chlorided solid oxide is formed by contacting a solid oxide with a chloriding agent. The chloride ion can be added to the oxide by forming a slurry of the oxide in a suitable solvent. The solid oxide can be treated with a chloriding agent during the calcining step. Any chloriding agent capable of serving as a source of chloride and thoroughly contacting the oxide during the calcining step can be used. For example, volatile organic chloriding agents can be used. Examples of suitable volatile organic chloriding agents include, but are not limited to, certain freons, perchlorobenzene, chloromethane, dichloromethane, chloroform, carbon tetrachloride, trichloroethanol, and the like, or any combination thereof. Gaseous hydrogen chloride or chlorine itself also can be used with the solid oxide during calcining. One convenient method of contacting the oxide with the chloriding agent is to vaporize a chloriding agent into a gas stream used to fluidize the solid oxide while calcination.
The amount of fluoride or chloride ion present before calcining the solid oxide generally is from about 2 to about 50% by weight, where weight percent is based on the weight of the solid oxide, for example, silica-alumina, before calcining According to another aspect of this invention, the amount of fluoride or chloride ion present before calcining the solid oxide is from about 3 to about 25% by weight, and according to another aspect of this invention, from about 4 to about 20% by weight. Once impregnated with halide, the halided oxide can be dried by any suitable method including, but not limited to, suction filtration followed by evaporation, drying under vacuum, spray drying, and the like, although it is also possible to initiate the calcining step immediately without drying the impregnated solid oxide.
The silica-alumina used to prepare the treated silica-alumina typically has a pore volume greater than about 0.5 cc/g. According to one aspect of the present invention, the pore volume is greater than about 0.8 cc/g, and according to another aspect of the present invention, greater than about 1.0 cc/g. Further, the silica-alumina generally has a surface area greater than about 100 m2/g. According to another aspect of this invention, the surface area is greater than about 250 m2/g. Yet, in another aspect, the surface area is greater than about 350 m2/g.
The silica-alumina utilized in the present invention typically has an alumina content from about 5 to about 95% by weight. According to one aspect of this invention, the alumina content of the silica-alumina is from about 5 to about 50%, or from about 8% to about 30%, alumina by weight. According to yet another aspect of this invention, the solid oxide component comprises alumina without silica, and according to another aspect of this invention, the solid oxide component comprises silica without alumina
The sulfated solid oxide comprises sulfate and a solid oxide component, such as alumina or silica-alumina, in the form of a particulate solid. Optionally, the sulfated oxide is treated further with a metal ion such that the calcined sulfated oxide comprises a metal. According to one aspect of the present invention, the sulfated solid oxide comprises sulfate and alumina. In some instances, the sulfated alumina is formed by a process wherein the alumina is treated with a sulfate source, for example, sulfuric acid or a sulfate salt such as ammonium sulfate. This process is generally performed by forming a slurry of the alumina in a suitable solvent, such as alcohol or water, in which the desired concentration of the sulfating agent has been added. Suitable organic solvents include, but are not limited to, the one to three carbon alcohols because of their volatility and low surface tension.
According to one aspect of this invention, the amount of sulfate ion present before calcining is from about 0.5 parts by weight to about 100 parts by weight sulfate ion to about 100 parts by weight solid oxide. According to another aspect of this invention, the amount of sulfate ion present before calcining is from about 1 part by weight to about 50 parts by weight sulfate ion to about 100 parts by weight solid oxide, and according to still another aspect of this invention, from about 5 parts by weight to about 30 parts by weight sulfate ion to about 100 parts by weight solid oxide. These weight ratios are based on the weight of the solid oxide before calcining. Once impregnated with sulfate, the sulfated oxide can be dried by any suitable method including, but not limited to, suction filtration followed by evaporation, drying under vacuum, spray drying, and the like, although it is also possible to initiate the calcining step immediately.
According to another aspect of the present invention, the activator-support used in preparing the catalyst compositions of this invention comprises an ion-exchangeable activator-support, including but not limited to silicate and aluminosilicate compounds or minerals, either with layered or non-layered structures, and combinations thereof. In another aspect of this invention, ion-exchangeable, layered aluminosilicates such as pillared clays are used as activator-supports. When the acidic activator-support comprises an ion-exchangeable activator-support, it can optionally be treated with at least one electron-withdrawing anion such as those disclosed herein, though typically the ion-exchangeable activator-support is not treated with an electron-withdrawing anion.
According to another aspect of the present invention, the activator-support of this invention comprises clay minerals having exchangeable cations and layers capable of expanding. Typical clay mineral activator-supports include, but are not limited to, ion-exchangeable, layered aluminosilicates such as pillared clays. Although the term “support” is used, it is not meant to be construed as an inert component of the catalyst composition, but rather is to be considered an active part of the catalyst composition, because of its intimate association with the dinuclear metallocene component.
According to another aspect of the present invention, the clay materials of this invention encompass materials either in their natural state or that have been treated with various ions by wetting, ion exchange, or pillaring. Typically, the clay material activator-support of this invention comprises clays that have been ion exchanged with large cations, including polynuclear, highly charged metal complex cations. However, the clay material activator-supports of this invention also encompass clays that have been ion exchanged with simple salts, including, but not limited to, salts of Al(III), Fe(II), Fe(III) and Zn(II) with ligands such as halide, acetate, sulfate, nitrate, or nitrite.
According to another aspect of the present invention, activator-support comprises a pillared clay. The term “pillared clay” is used to refer to clay materials that have been ion exchanged with large, typically polynuclear, highly charged metal complex cations. Examples of such ions include, but are not limited to, Keggin ions which can have charges such as 7+, various polyoxometallates, and other large ions. Thus, the term pillaring refers to a simple exchange reaction in which the exchangeable cations of a clay material are replaced with large, highly charged ions, such as Keggin ions. These polymeric cations are then immobilized within the interlayers of the clay and when calcined are converted to metal oxide “pillars,” effectively supporting the clay layers as column-like structures. Thus, once the clay is dried and calcined to produce the supporting pillars between clay layers, the expanded lattice structure is maintained and the porosity is enhanced. The resulting pores can vary in shape and size as a function of the pillaring material and the parent clay material used. Examples of pillaring and pillared clays are found in: T. J. Pinnavaia, Science 220 (4595), 365-371 (1983); J. M. Thomas, Intercalation Chemistry, (S. Whittington and A. Jacobson, eds.) Ch. 3, pp. 55-99, Academic Press, Inc., (1972); U.S. Pat. No. 4,452,910; U.S. Pat. No. 5,376,611; and U.S. Pat. No. 4,060,480; the disclosures of which are incorporated herein by reference in their entirety.
The pillaring process utilizes clay minerals having exchangeable cations and layers capable of expanding. Any pillared clay that can enhance the polymerization of olefins in the catalyst composition of the present invention can be used. Therefore, suitable clay minerals for pillaring include, but are not limited to, allophanes; smectites, both dioctahedral (Al) and tri-octahedral (Mg) and derivatives thereof such as montmorillonites (bentonites), nontronites, hectorites, or laponites; halloysites; vermiculites; micas; fluoromicas; chlorites; mixed-layer clays; the fibrous clays including but not limited to sepiolites, attapulgites, and palygorskites; a serpentine clay; illite; laponite; saponite; and any combination thereof. In one aspect, the pillared clay activator-support comprises bentonite or montmorillonite. The principal component of bentonite is montmorillonite.
The pillared clay can be pretreated if desired. For example, a pillared bentonite is pretreated by drying at about 300° C. under an inert atmosphere, typically dry nitrogen, for about 3 hours, before being added to the polymerization reactor. Although an exemplary pretreatment is described herein, it should be understood that the preheating can be carried out at many other temperatures and times, including any combination of temperature and time steps, all of which are encompassed by this invention.
The activator-support used to prepare the catalyst compositions of the present invention can be combined with other inorganic support materials, including, but not limited to, zeolites, inorganic oxides, phosphated inorganic oxides, and the like. In one aspect, typical support materials that are used include, but are not limited to, silica, silica-alumina, alumina, titania, zirconia, magnesia, boria, thoria, aluminophosphate, aluminum phosphate, silica-titania, coprecipitated silica/titania, mixtures thereof, or any combination thereof.
According to yet another aspect of the present invention, one or more of the dinuclear metallocene compounds can be precontacted with an olefin monomer and an organoaluminum compound for a first period of time prior to contacting this mixture with the activator-support. Once the precontacted mixture of the metallocene compound(s), olefin monomer, and organoaluminum compound is contacted with the activator-support, the composition further comprising the activator-support is termed the “postcontacted” mixture. The postcontacted mixture can be allowed to remain in further contact for a second period of time prior to being charged into the reactor in which the polymerization process will be carried out.
Organoaluminum Compounds
In one aspect, organoaluminum compounds that can be used with the present invention include, but are not limited to, compounds having the formula:

(R2)3Al;

where R2 is an aliphatic group having from 2 to 6 carbon atoms. For example, R2 can be ethyl, propyl, butyl, hexyl, or isobutyl.

Other organoaluminum compounds which can be used in accordance with the present invention include, but are not limited to, compounds having the formula:

Al(X5)m(X6)3-m,

where X5 is a hydrocarbyl; X6 is an alkoxide or an aryloxide, a halide, or a hydride; and m is from 1 to 3, inclusive.

In one aspect, X5 is a hydrocarbyl having from 1 to about 20 carbon atoms. In another aspect of the present invention, X5 is an alkyl having from 1 to 10 carbon atoms. For example, X5 can be ethyl, propyl, n-butyl, sec-butyl, isobutyl, or hexyl, and the like, in yet another aspect of the present invention.
According to one aspect of the present invention, X6 is an alkoxide or an aryloxide, any one of which has from 1 to 20 carbon atoms, a halide, or a hydride. In another aspect of the present invention, X6 is selected independently from fluorine or chlorine. Yet, in another aspect, X6 is chlorine.
In the formula, Al(X5)m(X6)3-m, m is a number from 1 to 3, inclusive, and typically, m is 3. The value of m is not restricted to be an integer; therefore, this formula includes sesquihalide compounds or other organoaluminum cluster compounds.
Examples of organoaluminum compounds suitable for use in accordance with the present invention include, but are not limited to, trialkylaluminum compounds, dialkylaluminum halide compounds, dialkylaluminum alkoxide compounds, dialkylaluminum hydride compounds, and combinations thereof. Specific non-limiting examples of suitable organoaluminum compounds include trimethylaluminum (TMA), triethylaluminum (TEA), tripropylaluminum, diethylaluminum ethoxide, tributylaluminum, diisobutylaluminum hydride, triisobutylaluminum, diethylaluminum chloride, and the like, or combinations thereof.
The present invention contemplates precontacting at least one dinuclear metallocene compound with at least one organoaluminum compound and an olefin monomer to form a precontacted mixture, prior to contacting this precontacted mixture with the activator-support to form a catalyst composition. When the catalyst composition is prepared in this manner, typically, though not necessarily, a portion of the organoaluminum compound is added to the precontacted mixture and another portion of the organoaluminum compound is added to the postcontacted mixture prepared when the precontacted mixture is contacted with the solid oxide activator-support. However, the entire organoaluminum compound can be used to prepare the catalyst composition in either the precontacting or postcontacting step. Alternatively, all the catalyst components are contacted in a single step.
Further, more than one organoaluminum compound can be used in either the precontacting or the postcontacting step. When an organoaluminum compound is added in multiple steps, the amounts of organoaluminum compound disclosed herein include the total amount of organoaluminum compound used in both the precontacted and postcontacted mixtures, and any additional organoaluminum compound added to the polymerization reactor. Therefore, total amounts of organoaluminum compounds are disclosed regardless of whether a single organoaluminum compound or more than one organoaluminum compound is used.
Aluminoxane Compounds
The present invention further provides a catalyst composition which can comprise an aluminoxane compound. As used herein, the term “aluminoxane” refers to aluminoxane compounds, compositions, mixtures, or discrete species, regardless of how such aluminoxanes are prepared, formed or otherwise provided. For example, a catalyst composition comprising an aluminoxane compound can be prepared in which aluminoxane is provided as the poly(hydrocarbyl aluminum oxide), or in which aluminoxane is provided as the combination of an aluminum alkyl compound and a source of active protons such as water. Aluminoxanes are also referred to as poly(hydrocarbyl aluminum oxides) or organoaluminoxanes.
The other catalyst components typically are contacted with the aluminoxane in a saturated hydrocarbon compound solvent, though any solvent that is substantially inert to the reactants, intermediates, and products of the activation step can be used. The catalyst composition formed in this manner is collected by any suitable method, for example, by filtration. Alternatively, the catalyst composition is introduced into the polymerization reactor without being isolated.
The aluminoxane compound of this invention can be an oligomeric aluminum compound comprising linear structures, cyclic structures, or cage structures, or mixtures of all three. Cyclic aluminoxane compounds having the formula:




wherein R is a linear or branched alkyl having from 1 to 10 carbon atoms, and p is an integer from 3 to 20, are encompassed by this invention. The AlRO moiety shown here also constitutes the repeating unit in a linear aluminoxane. Thus, linear aluminoxanes having the formula:





wherein R is a linear or branched alkyl having from 1 to 10 carbon atoms, and q is an integer from 1 to 50, are also encompassed by this invention.

Further, aluminoxanes can have cage structures of the formula Rt5r+αRbr−αAl4rO3r, wherein Rt is a terminal linear or branched alkyl group having from 1 to 10 carbon atoms; Rb is a bridging linear or branched alkyl group having from 1 to 10 carbon atoms; r is 3 or 4; and α is equal to nAl(3)−nO(2)+nO(4), wherein nAl(3) is the number of three coordinate aluminum atoms, nO(2) is the number of two coordinate oxygen atoms, and nO(4) is the number of 4 coordinate oxygen atoms.
Thus, aluminoxanes which can be employed in the catalyst compositions of the present invention are represented generally by formulas such as (R—Al—O)p, R(R—Al—O)qAlR2, and the like. In these formulas, the R group is typically a linear or branched C1-C6 alkyl, such as methyl, ethyl, propyl, butyl, pentyl, or hexyl. Examples of aluminoxane compounds that can be used in accordance with the present invention include, but are not limited to, methylaluminoxane, ethylaluminoxane, n-propylaluminoxane, iso-propylaluminoxane, n-butylaluminoxane, t-butyl-aluminoxane, sec-butylaluminoxane, iso-butylaluminoxane, 1-pentylaluminoxane, 2-pentylaluminoxane, 3-pentylaluminoxane, isopentylaluminoxane, neopentylaluminoxane, and the like, or any combination thereof. Methyl aluminoxane, ethyl aluminoxane, and isobutyl aluminoxane are prepared from trimethylaluminum, triethylaluminum, or triisobutylaluminum, respectively, and sometimes are referred to as poly(methyl aluminum oxide), poly(ethyl aluminum oxide), and poly(isobutyl aluminum oxide), respectively. It is also within the scope of the invention to use an aluminoxane in combination with a trialkylaluminum, such as that disclosed in U.S. Pat. No. 4,794,096, incorporated herein by reference in its entirety.
The present invention contemplates many values of p and q in the aluminoxane formulas (R—Al—O)p and R(R—Al—O)qAlR2, respectively. Is some aspects, p and q are at least 3. However, depending upon how the organoaluminoxane is prepared, stored, and used, the value of p and q can vary within a single sample of aluminoxane, and such combinations of organoaluminoxanes are contemplated herein.
In preparing a catalyst composition containing an aluminoxane, the molar ratio of the total moles of aluminum in the aluminoxane (or aluminoxanes) to the total moles of dinuclear metallocene compound (or compounds) in the composition is generally between about 1:10 and about 100,000:1. In another aspect, the molar ratio is in a range from about 5:1 to about 15,000:1. Optionally, aluminoxane can be added to a polymerization zone in ranges from about 0.01 mg/L to about 1000 mg/L, from about 0.1 mg/L to about 100 mg/L, or from about 1 mg/L to about 50 mg/L.
Organoaluminoxanes can be prepared by various procedures. Examples of organoaluminoxane preparations are disclosed in U.S. Pat. Nos. 3,242,099 and 4,808,561, the disclosures of which are incorporated herein by reference in their entirety. For example, water in an inert organic solvent can be reacted with an aluminum alkyl compound, such as (R2)3Al, to form the desired organoaluminoxane compound. While not intending to be bound by this statement, it is believed that this synthetic method can afford a mixture of both linear and cyclic R—Al—O aluminoxane species, both of which are encompassed by this invention. Alternatively, organoaluminoxanes are prepared by reacting an aluminum alkyl compound, such as (R2)3Al with a hydrated salt, such as hydrated copper sulfate, in an inert organic solvent.
Organoboron/Organoborate Compounds
According to another aspect of the present invention, a catalyst composition comprising organoboron or organoborate compounds is provided. Such compounds include neutral boron compounds, borate salts, and the like, or combinations thereof. For example, fluoroorgano boron compounds and fluoroorgano borate compounds are contemplated.
Any fluoroorgano boron or fluoroorgano borate compound can be utilized with the present invention. Examples of fluoroorgano borate compounds that can be used in the present invention include, but are not limited to, fluorinated aryl borates such as N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, lithium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, and the like, or mixtures thereof. Examples of fluoroorgano boron compounds that can be used as co-catalysts in the present invention include, but are not limited to, tris(pentafluorophenyl)boron, tris[3,5-bis(trifluoromethyl)phenyl]boron, and the like, or mixtures thereof. Although not intending to be bound by the following theory, these examples of fluoroorgano borate and fluoroorgano boron compounds, and related compounds, are thought to form “weakly-coordinating” anions when combined with organometal or metallocene compounds, as disclosed in U.S. Pat. No. 5,919,983, the disclosure of which is incorporated herein by reference in its entirety. Applicants also contemplate the use of diboron, or bis-boron, compounds or other bifunctional compounds containing two or more boron atoms in the chemical structure, such as disclosed in J. Am. Chem. Soc., 2005, 127, pp. 14756-14768, the content of which is incorporated herein by reference in its entirety.
Generally, any amount of organoboron compound can be used. According to one aspect of this invention, the molar ratio of the total moles of organoboron or organoborate compound (or compounds) to the total moles of dinuclear metallocene compound (or compounds) in the catalyst composition is in a range from about 0.1:1 to about 15:1. Typically, the amount of the fluoroorgano boron or fluoroorgano borate compound used as a co-catalyst for the dinuclear metallocene is from about 0.5 moles to about 10 moles of boron/borate compound per mole of dinuclear metallocene compound. According to another aspect of this invention, the amount of fluoroorgano boron or fluoroorgano borate compound is from about 0.8 moles to about 5 moles of boron/borate compound per mole of dinuclear metallocene compound.
Ionizing Ionic Compounds
The present invention further provides a catalyst composition comprising an ionizing ionic compound. An ionizing ionic compound is an ionic compound that can function as a co-catalyst to enhance the activity of the catalyst composition. While not intending to be bound by theory, it is believed that the ionizing ionic compound is capable of reacting with a metallocene compound and converting the metallocene into one or more cationic metallocene compounds, or incipient cationic metallocene compounds. Again, while not intending to be bound by theory, it is believed that the ionizing ionic compound can function as an ionizing compound by completely or partially extracting an anionic ligand, possibly a non-alkadienyl ligand such as X1 or X2, from the metallocene. However, the ionizing ionic compound is an activator regardless of whether it is ionizes the dinuclear metallocene, abstracts an X1 or X2 ligand in a fashion as to form an ion pair, weakens the metal-X1 or metal-X2 bond in the dinuclear metallocene, simply coordinates to an X1 or X2 ligand, or activates the metallocene by some other mechanism.
Further, it is not necessary that the ionizing ionic compound activate the metallocene compounds only. The activation function of the ionizing ionic compound can be evident in the enhanced activity of catalyst composition as a whole, as compared to a catalyst composition that does not contain an ionizing ionic compound.
Examples of ionizing ionic compounds include, but are not limited to, the following compounds: tri(n-butyl)ammonium tetrakis(p-tolyl)borate, tri(n-butyl) ammonium tetrakis(m-tolyl)borate, tri(n-butyl)ammonium tetrakis(2,4-dimethylphenyl)borate, tri(n-butyl)ammonium tetrakis(3,5-dimethylphenyl)borate, tri(n-butyl)ammonium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tri(n-butyl)ammonium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis(p-tolyl)borate, N,N-dimethylanilinium tetrakis(m-tolyl)borate, N,N-dimethylanilinium tetrakis(2,4-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis(3,5-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoro-methyl)phenyl]borate, N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis (p-tolyl)borate, triphenylcarbenium tetrakis(m-tolyl)borate, triphenylcarbenium tetrakis(2,4-dimethylphenyl)borate, triphenylcarbenium tetrakis(3,5-dimethylpheny)borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, tropylium tetrakis(p-tolyl)borate, tropylium tetrakis(m-tolyl)borate, tropylium tetrakis(2,4-dimethylphenyl)borate, tropylium tetrakis(3,5-dimethylpheny)borate, tropylium tetrakis[3,5-bis(trifluoro-methyl)phenyl]borate, tropylium tetrakis(pentafluorophenyl)borate, lithium tetrakis(pentafluorophenyl)borate, lithium tetraphenylborate, lithium tetrakis(p-tolyl)borate, lithium tetrakis(m-tolyl)borate, lithium tetrakis(2,4-dimethylphenyl)borate, lithium tetrakis(3,5-dimethylpheny)borate, lithium tetrafluoroborate, sodium tetrakis(pentafluorophenyl)borate, sodium tetraphenylborate, sodium tetrakis(p-tolyl)borate, sodium tetrakis(m-tolyl)borate, sodium tetrakis(2,4-dimethylpheny)borate, sodium tetrakis(3,5-dimethylphenyl)borate, sodium tetrafluoroborate, potassium tetrakis-(pentafluorophenyl)borate, potassium tetraphenylborate, potassium tetrakis(p-tolyl)borate, potassium tetrakis(m-tolyl)borate, potassium tetrakis(2,4-dimethyl-phenyl)borate, potassium tetrakis(3,5-dimethylphenyl)borate, potassium tetrafluoro-borate, lithium tetrakis(pentafluorophenyl)aluminate, lithium tetraphenylaluminate, lithium tetrakis(p-tolyl)aluminate, lithium tetrakis(m-tolyl)aluminate, lithium tetrakis(2,4-dimethylphenyl)aluminate, lithium tetrakis(3,5-dimethylphenyl)aluminate, lithium tetrafluoroaluminate, sodium tetrakis(pentafluoro-phenyl)aluminate, sodium tetraphenylaluminate, sodium tetrakis(p-tolyl)aluminate, sodium tetrakis(m-tolyl)aluminate, sodium tetrakis(2,4-dimethylphenyl)aluminate, sodium tetrakis(3,5-dimethylphenyl)aluminate, sodium tetrafluoroaluminate, potassium tetrakis(pentafluorophenyl)aluminate, potassium tetraphenylaluminate, potassium tetrakis(p-tolyl)aluminate, potassium tetrakis(m-tolyl)aluminate, potassium tetrakis(2,4-dimethylphenyl)aluminate, potassium tetrakis (3,5-dimethylphenyl)aluminate, potassium tetrafluoroaluminate, and the like, or combinations thereof. Ionizing ionic compounds useful in this invention are not limited to these; other examples of ionizing ionic compounds are disclosed in U.S. Pat. Nos. 5,576,259 and 5,807,938, the disclosures of which are incorporated herein by reference in their entirety.
Olefin Monomers
Unsaturated reactants that can be employed with catalyst compositions and polymerization processes of this invention typically include olefin compounds having from about 2 to 30 carbon atoms per molecule and having at least one olefinic double bond. This invention encompasses homopolymerization processes using a single olefin such as ethylene or propylene, as well as copolymerization reactions with at least one different olefinic compound. The resulting copolymers generally contain a major amount of ethylene (>50 mole percent) and a minor amount of comonomer (<50 mole percent), though this is not a requirement. The comonomers that can be copolymerized with ethylene often have from 3 to 20 carbon atoms in their molecular chain.
Acyclic, cyclic, polycyclic, terminal (α), internal, linear, branched, substituted, unsubstituted, functionalized, and non-functionalized olefins can be employed in this invention. For example, typical unsaturated compounds that can be polymerized with the catalyst compositions of this invention include, but are not limited to, ethylene, propylene, 1-butene, 2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-hexene, 3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, the four normal octenes, the four normal nonenes, the five normal decenes, and the like, or mixtures of two or more of these compounds. Cyclic and bicyclic olefins, including but not limited to, cyclopentene, cyclohexene, norbornylene, norbornadiene, and the like, can also be polymerized as described above. Styrene can also be employed as a monomer.
When a copolymer is desired, the monomer can be, for example, ethylene or propylene, which is copolymerized with a comonomer. Examples of olefin comonomers include, but are not limited to, 1-butene, 2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, 1-octene, and the like. According to one aspect of the present invention, the comonomer is selected from 1-butene, 1-pentene, 1-hexene, 1-octene, 1-decene, or styrene.
Generally, the amount of comonomer introduced into a reactor zone to produce the copolymer is from about 0.01 to about 50 weight percent of the comonomer based on the total weight of the monomer and comonomer. According to another aspect of the present invention, the amount of comonomer introduced into a reactor zone is from about 0.01 to about 40 weight percent comonomer based on the total weight of the monomer and comonomer. In still another aspect, the amount of comonomer introduced into a reactor zone is from about 0.1 to about 35 weight percent comonomer based on the total weight of the monomer and comonomer. Yet, in another aspect, the amount of comonomer introduced into a reactor zone is from about 0.5 to about 20 weight percent comonomer based on the total weight of the monomer and comonomer.
While not intending to be bound by this theory, where branched, substituted, or functionalized olefins are used as reactants, it is believed that a steric hindrance can impede and/or slow the polymerization process. Thus, branched and/or cyclic portion(s) of the olefin removed somewhat from the carbon-carbon double bond would not be expected to hinder the reaction in the way that the same olefin substituents situated more proximate to the carbon-carbon double bond might. According to one aspect of the present invention, at least one monomer/reactant is ethylene, so the polymerizations are either a homopolymerization involving only ethylene, or copolymerizations with a different acyclic, cyclic, terminal, internal, linear, branched, substituted, or unsubstituted olefin. In addition, the catalyst compositions of this invention can be used in the polymerization of diolefin compounds including, but not limited to, 1,3-butadiene, isoprene, 1,4-pentadiene, and 1,5-hexadiene.
Preparation of the Catalyst Composition
In one aspect, the present invention encompasses a catalyst composition comprising a contact product of a dinuclear metallocene compound and an activator-support. Such a composition can further comprise an organoaluminum compound. Additionally, this catalyst composition can further comprise at least one optional co-catalyst, wherein the at least one optional co-catalyst is at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof. In another aspect, a catalyst composition is provided which comprises the contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof.
This invention further encompasses methods of making these catalyst compositions, such as, for example, contacting the respective catalyst components in any order or sequence.
The at least one dinuclear metallocene compound can be precontacted with an olefinic monomer if desired, not necessarily the olefin monomer to be polymerized, and an organoaluminum compound for a first period of time prior to contacting this precontacted mixture with an activator-support. The first period of time for contact, the precontact time, between the metallocene compound or compounds, the olefinic monomer, and the organoaluminum compound typically ranges from a time period of about 0.1 hour to about 24 hours, for example, from about 0.1 to about 1 hour. Precontact times from about 10 minutes to about 30 minutes are also employed.
Alternatively, the precontacting process is carried out in multiple steps, rather than a single step, in which multiple mixtures are prepared, each comprising a different set of catalyst components. For example, at least two catalyst components are contacted forming a first mixture, followed by contacting the first mixture with at least one other catalyst component forming a second mixture, and so forth.
Multiple precontacting steps can be carried out in a single vessel or in multiple vessels. Further, multiple precontacting steps can be carried out in series (sequentially), in parallel, or a combination thereof. For example, a first mixture of two catalyst components can be formed in a first vessel, a second mixture comprising the first mixture plus one additional catalyst component can be formed in the first vessel or in a second vessel, which is typically placed downstream of the first vessel.
In another aspect, one or more of the catalyst components can be split and used in different precontacting treatments. For example, part of a catalyst component is fed into a first precontacting vessel for precontacting with at least one other catalyst component, while the remainder of that same catalyst component is fed into a second precontacting vessel for precontacting with at least one other catalyst component, or is fed directly into the reactor, or a combination thereof. The precontacting can be carried out in any suitable equipment, such as tanks, stirred mix tanks, various static mixing devices, a flask, a vessel of any type, or combinations of these apparatus.
In another aspect of this invention, the various catalyst components (for example, dinuclear metallocene, activator-support, organoaluminum co-catalyst, and optionally an unsaturated hydrocarbon) are contacted in the polymerization reactor simultaneously while the polymerization reaction is proceeding. Alternatively, any two or more of these catalyst components can be precontacted in a vessel prior to entering the reaction zone. This precontacting step can be continuous, in which the precontacted product is fed continuously to the reactor, or it can be a stepwise or batchwise process in which a batch of precontacted product is added to make a catalyst composition. This precontacting step can be carried out over a time period that can range from a few seconds to as much as several days, or longer. In this aspect, the continuous precontacting step generally lasts from about 1 second to about 1 hour. In another aspect, the continuous precontacting step lasts from about 10 seconds to about 45 minutes, or from about 1 minute to about 30 minutes.
Once the precontacted mixture of the metallocene compound, olefin monomer, and organoaluminum co-catalyst is contacted with the activator-support, this composition (with the addition of the activator-support) is termed the “postcontacted mixture.” The postcontacted mixture optionally remains in contact for a second period of time, the postcontact time, prior to initiating the polymerization process. Postcontact times between the precontacted mixture and the activator-support generally range from about 0.1 hour to about 24 hours. In a further aspect, the postcontact time is in a range from about 0.1 hour to about 1 hour. The precontacting step, the postcontacting step, or both, can increase the productivity of the polymer as compared to the same catalyst composition that is prepared without precontacting or postcontacting. However, neither a precontacting step nor a postcontacting step is required.
The postcontacted mixture can be heated at a temperature and for a time period sufficient to allow adsorption, impregnation, or interaction of precontacted mixture and the activator-support, such that a portion of the components of the precontacted mixture is immobilized, adsorbed, or deposited thereon. Where heating is employed, the postcontacted mixture generally is heated to a temperature of from between about 0° F. to about 150° F., or from about 40° F. to about 95° F.
According to one aspect of this invention, the molar ratio of the moles of dinuclear metallocene compound to the moles of organoaluminum compound in a catalyst composition generally is in a range from about 1:1 to about 1:10,000. In another aspect, the molar ratio is in a range from about 1:1 to about 1:1,000. Yet, in another aspect, the molar ratio of the moles of dinuclear metallocene compound to the moles of organoaluminum compound is in a range from about 1:1 to about 1:100. These molar ratios reflect the ratio of total moles of dinuclear metallocene compound or compounds to the total amount of organoaluminum compound (or compounds) in both the precontacted mixture and the postcontacted mixture combined, if precontacting and/or postcontacting steps are employed.
When a precontacting step is used, the molar ratio of the total moles of olefin monomer to total moles of dinuclear metallocene in the precontacted mixture is typically in a range from about 1:10 to about 100,000:1. Total moles of each component are used in this ratio to account for aspects of this invention where more than one olefin monomer and/or more than dinuclear metallocene is employed. Further, this molar ratio can be in a range from about 10:1 to about 1,000:1 in another aspect of the invention.
Generally, the weight ratio of organoaluminum compound to activator-support is in a range from about 10:1 to about 1:1000. If more than one organoaluminum compound and/or more than one activator-support is employed, this ratio is based on the total weight of each respective component. In another aspect, the weight ratio of the organoaluminum compound to the activator-support is in a range from about 3:1 to about 1:100, or from about 1:1 to about 1:50.
In some aspects of this invention, the weight ratio of dinuclear metallocene to activator-support is in a range from about 1:1 to about 1:1,000,000. If more than one dinuclear metallocene and/or more than one activator-support is employed, this ratio is based on the total weight of each respective component. In another aspect, this weight ratio is in a range from about 1:5 to about 1:100,000, or from about 1:10 to about 1:10,000. Yet, in another aspect, the weight ratio of the dinuclear metallocene compound to the activator-support is in a range from about 1:20 to about 1:1000.
According to some aspects of this invention, aluminoxane compounds are not required to form the catalyst composition. Thus, the polymerization proceeds in the absence of aluminoxanes. Accordingly, the present invention can use, for example, organoaluminum compounds and an activator-support in the absence of aluminoxanes. While not intending to be bound by theory, it is believed that the organoaluminum compound likely does not activate the metallocene catalyst in the same manner as an organoaluminoxane compound.
Additionally, in some aspects, organoboron and organoborate compounds are not required to form a catalyst composition of this invention. Nonetheless, aluminoxanes, organozinc compounds, organoboron or organoborate compounds, ionizing ionic compounds, or combinations thereof can be used in other catalyst compositions contemplated by and encompassed within the present invention. Hence, co-catalysts such as aluminoxanes, organozinc compounds, organoboron or organoborate compounds, ionizing ionic compounds, or combinations thereof, can be employed with the dinuclear metallocene compound, either in the presence or in the absence of an activator-support, and either in the presence or in the absence of an organoaluminum compound.
Catalyst compositions of the present invention generally have a catalyst activity greater than about 100 grams of polyethylene per gram of activator-support per hour (abbreviated gP/(gAS·hr)). In another aspect, the catalyst activity is greater than about 150, greater than about 200, or greater than about 250 gP/(gAS·hr). In still another aspect, catalyst compositions of this invention are characterized by having a catalyst activity greater than about 500, greater than about 1000, or greater than about 1500 gP/(gAS·hr). Yet, in another aspect, the catalyst activity is greater than about 2000 gP/(gAS·hr). This activity is measured under slurry polymerization conditions using isobutane as the diluent, at a polymerization temperature of about 90° C. and an ethylene pressure of about 550 psig.
Other aspects of the present invention do not require an activator-support. These catalyst compositions comprise a contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof. Such catalyst compositions of the present invention generally have catalyst activities greater than about 100 grams of polyethylene per hour per gram of the respective aluminoxane compound, organozinc compound, organoboron or organoborate compound, ionizing ionic compound, or combination thereof. In another aspect, the catalyst activity is greater than about 250, or greater than about 500 grams of polyethylene per hour per gram of the respective aluminoxane compound, organozinc compound, organoboron or organoborate compound, ionizing ionic compound, or combination thereof. Yet, in another aspect, the catalyst activity is greater than about 1000, or greater than about 2000 grams of polyethylene per hour.
As discussed above, any combination of the dinuclear metallocene compound, the activator-support, the organoaluminum compound, and the olefin monomer, can be precontacted in some aspects of this invention. When any precontacting occurs with an olefinic monomer, it is not necessary that the olefin monomer used in the precontacting step be the same as the olefin to be polymerized. Further, when a precontacting step among any combination of the catalyst components is employed for a first period of time, this precontacted mixture can be used in a subsequent postcontacting step between any other combination of catalyst components for a second period of time. For example, the dinuclear metallocene compound, the organoaluminum compound, and 1-hexene can be used in a precontacting step for a first period of time, and this precontacted mixture then can be contacted with the activator-support to form a postcontacted mixture that is contacted for a second period of time prior to initiating the polymerization reaction. For example, the first period of time for contact, the precontact time, between any combination of the metallocene compound, the olefinic monomer, the activator-support, and the organoaluminum compound can be from about 0.1 hour to about 24 hours, from about 0.1 to about 1 hour, or from about 10 minutes to about 30 minutes. The postcontacted mixture optionally is allowed to remain in contact for a second period of time, the postcontact time, prior to initiating the polymerization process. According to one aspect of this invention, postcontact times between the precontacted mixture and any remaining catalyst components is from about 0.1 hour to about 24 hours, or from about 0.1 hour to about 1 hour.
Polymerization Process
Catalyst compositions of the present invention can be used to polymerize olefins to form homopolymers or copolymers. One such process for polymerizing olefins in the presence of a catalyst composition of the present invention comprises contacting the catalyst composition with at least one olefin monomer and optionally at least one olefin comonomer under polymerization conditions to produce a polymer or copolymer, wherein the catalyst composition comprises a contact product of at least one dinuclear metallocene compound and at least one activator-support. The at least one dinuclear metallocene compound is selected from the following formula:




wherein:

X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.
The catalyst compositions of the present invention are intended for any olefin polymerization method using various types of polymerization reactors. As used herein, “polymerization reactor” includes any polymerization reactor capable of polymerizing olefin monomers to produce homopolymers or copolymers. Such homopolymers and copolymers are referred to as resins or polymers. The various types of reactors include those that may be referred to as batch, slurry, gas-phase, solution, high pressure, tubular or autoclave reactors. Gas phase reactors may comprise fluidized bed reactors or staged horizontal reactors. Slurry reactors may comprise vertical or horizontal loops. High pressure reactors may comprise autoclave or tubular reactors. Reactor types can include batch or continuous processes. Continuous processes could use intermittent or continuous product discharge. Processes may also include partial or full direct recycle of un-reacted monomer, un-reacted comonomer, and/or diluent.
Polymerization reactor systems of the present invention may comprise one type of reactor in a system or multiple reactors of the same or different type. Production of polymers in multiple reactors may include several stages in at least two separate polymerization reactors interconnected by a transfer device making it possible to transfer the polymers resulting from the first polymerization reactor into the second reactor. The desired polymerization conditions in one of the reactors may be different from the operating conditions of the other reactors. Alternatively, polymerization in multiple reactors may include the manual transfer of polymer from one reactor to subsequent reactors for continued polymerization. Multiple reactor systems may include any combination including, but not limited to, multiple loop reactors, multiple gas reactors, a combination of loop and gas reactors, multiple high pressure reactors or a combination of high pressure with loop and/or gas reactors. The multiple reactors may be operated in series or in parallel.
According to one aspect of the invention, the polymerization reactor system may comprise at least one loop slurry reactor comprising vertical or horizontal loops. Monomer, diluent, catalyst and optionally any comonomer may be continuously fed to a loop reactor where polymerization occurs. Generally, continuous processes may comprise the continuous introduction of a monomer, a catalyst, and a diluent into a polymerization reactor and the continuous removal from this reactor of a suspension comprising polymer particles and the diluent. Reactor effluent may be flashed to remove the solid polymer from the liquids that comprise the diluent, monomer and/or comonomer. Various technologies may be used for this separation step including but not limited to, flashing that may include any combination of heat addition and pressure reduction; separation by cyclonic action in either a cyclone or hydrocyclone; or separation by centrifugation.
A typical slurry polymerization process (also known as the particle form process), is disclosed, for example, in U.S. Pat. Nos. 3,248,179, 4,501,885, 5,565,175, 5,575,979, 6,239,235, 6,262,191 and 6,833,415, each of which is incorporated by reference in its entirety herein.
Suitable diluents used in slurry polymerization include, but are not limited to, the monomer being polymerized and hydrocarbons that are liquids under reaction conditions. Examples of suitable diluents include, but are not limited to, hydrocarbons such as propane, cyclohexane, isobutane, n-butane, n-pentane, isopentane, neopentane, and n-hexane. Some loop polymerization reactions can occur under bulk conditions where no diluent is used. An example is polymerization of propylene monomer as disclosed in U.S. Pat. No. 5,455,314, which is incorporated by reference herein in its entirety.
According to yet another aspect of this invention, the polymerization reactor may comprise at least one gas phase reactor. Such systems may employ a continuous recycle stream containing one or more monomers continuously cycled through a fluidized bed in the presence of the catalyst under polymerization conditions. A recycle stream may be withdrawn from the fluidized bed and recycled back into the reactor. Simultaneously, polymer product may be withdrawn from the reactor and new or fresh monomer may be added to replace the polymerized monomer. Such gas phase reactors may comprise a process for multi-step gas-phase polymerization of olefins, in which olefins are polymerized in the gaseous phase in at least two independent gas-phase polymerization zones while feeding a catalyst-containing polymer formed in a first polymerization zone to a second polymerization zone. One type of gas phase reactor is disclosed in U.S. Pat. Nos. 5,352,749, 4,588,790 and 5,436,304, each of which is incorporated by reference in its entirety herein.
According to still another aspect of the invention, a high pressure polymerization reactor may comprise a tubular reactor or an autoclave reactor. Tubular reactors may have several zones where fresh monomer, initiators, or catalysts are added. Monomer may be entrained in an inert gaseous stream and introduced at one zone of the reactor. Initiators, catalysts, and/or catalyst components may be entrained in a gaseous stream and introduced at another zone of the reactor. The gas streams may be intermixed for polymerization. Heat and pressure may be employed appropriately to obtain optimal polymerization reaction conditions.
According to yet another aspect of the invention, the polymerization reactor may comprise a solution polymerization reactor wherein the monomer is contacted with the catalyst composition by suitable stirring or other means. A carrier comprising an inert organic diluent or excess monomer may be employed. If desired, the monomer may be brought in the vapor phase into contact with the catalytic reaction product, in the presence or absence of liquid material. The polymerization zone is maintained at temperatures and pressures that will result in the formation of a solution of the polymer in a reaction medium. Agitation may be employed to obtain better temperature control and to maintain uniform polymerization mixtures throughout the polymerization zone. Adequate means are utilized for dissipating the exothermic heat of polymerization.
Polymerization reactors suitable for the present invention may further comprise any combination of at least one raw material feed system, at least one feed system for catalyst or catalyst components, and/or at least one polymer recovery system. Suitable reactor systems for the present invention may further comprise systems for feedstock purification, catalyst storage and preparation, extrusion, reactor cooling, polymer recovery, fractionation, recycle, storage, loadout, laboratory analysis, and process control.
Conditions that are controlled for polymerization efficiency and to provide resin properties include temperature, pressure and the concentrations of various reactants. Polymerization temperature can affect catalyst productivity, polymer molecular weight and molecular weight distribution. Suitable polymerization temperature may be any temperature below the de-polymerization temperature according to the Gibbs Free energy equation. Typically this includes from about 60° C. to about 280° C., for example, and from about 70° C. to about 110° C., depending upon the type of polymerization reactor.
Suitable pressures will also vary according to the reactor and polymerization type. The pressure for liquid phase polymerizations in a loop reactor is typically less than 1000 psig. Pressure for gas phase polymerization is usually at about 200 to 500 psig. High pressure polymerization in tubular or autoclave reactors is generally run at about 20,000 to 75,000 psig. Polymerization reactors can also be operated in a supercritical region occurring at generally higher temperatures and pressures. Operation above the critical point of a pressure/temperature diagram (supercritical phase) may offer advantages.
The concentration of various reactants can be controlled to produce resins with certain physical and mechanical properties. The proposed end-use product that will be formed by the resin and the method of forming that product determines the desired resin properties. Mechanical properties include tensile, flexural, impact, creep, stress relaxation and hardness tests. Physical properties include density, molecular weight, molecular weight distribution, melting temperature, glass transition temperature, temperature melt of crystallization, density, stereoregularity, crack growth, long chain branching and rheological measurements.
The concentrations of monomer, co-monomer, hydrogen, co-catalyst, modifiers, and electron donors are important in producing these resin properties. Comonomer is used to control product density. Hydrogen can be used to control product molecular weight. Co-catalysts can be used to alkylate, scavenge poisons and control molecular weight. Modifiers can be used to control product properties and electron donors affect stereoregularity. In addition, the concentration of poisons is minimized because poisons impact the reactions and product properties.
The polymer or resin may be formed into various articles, including, but not limited to, bottles, drums, toys, household containers, utensils, film products, drums, fuel tanks, pipes, geomembranes, and liners. Various processes may be used to form these articles, including, but not limited to, blow molding, extrusion molding, rotational molding, thermoforming, cast molding and the like. After polymerization, additives and modifiers can be added to the polymer to provide better processing during manufacturing and for desired properties in the end product. Additives include surface modifiers such as slip agents, antiblocks, tackifiers; antioxidants such as primary and secondary antioxidants; pigments; processing aids such as waxes/oils and fluoroelastomers; and special additives such as fire retardants, antistats, scavengers, absorbers, odor enhancers, and degradation agents.
Homopolymers and copolymers of ethylene produced in accordance with this invention generally have a melt index from about 0.01 to about 100 g/10 min. For example, a melt index in the range from about 0.1 to about 50 g/10 min, or from about 0.5 to about 25 g/10 min, are contemplated in some aspects of this invention.
The density of ethylene-based polymers produced using one or more dinuclear metallocene compounds of the present invention typically falls within the range from about 0.88 to about 0.97 g/cc. In one aspect of this invention, the polymer density is in a range from about 0.90 to about 0.95 g/cc. Yet, in another aspect, the density is generally in a range from about 0.91 to about 0.94 g/cc.
If the resultant polymer produced in accordance with the present invention is, for example, a polymer or copolymer of ethylene, it can be formed into various articles of manufacture. Such articles include, but are not limited to, molded products, household containers, utensils, film or sheet products, drums, fuel tanks, pipes, geomembranes, liners, and the like. Various processes can be employed to form these articles. Non-limiting examples of these processes include injection molding, blow molding, film extrusion, sheet extrusion, profile extrusion, and the like. Additionally, additives and modifiers are often added to these polymers in order to provide beneficial polymer processing or end-use product attributes.
EXAMPLES
The invention is further illustrated by the following examples, which are not to be construed in any way as imposing limitations to the scope of this invention. Various other aspects, embodiments, modifications, and equivalents thereof which, after reading the description herein, may suggest themselves to one of ordinary skill in the art without departing from the spirit of the present invention or the scope of the appended claims.
Nuclear Magnetic Resonance (NMR) spectra were obtained on a Varian Mercury Plus 300 NMR spectrometer operating at 300 MHz for 1H NMR (CDCl3 solvent, referenced against the peak of residual CHCl3 at 7.24 ppm) and 75 MHz for 13C NMR (CDCl3 solvent, referenced against central line of CHCl3 at 77.00 ppm).
In addition to NMR, a thermal desorption mass spectrometry procedure (direct insertion probe mass spectrometry or DIPMS) was used to characterize and identify the dinuclear metallocene compounds in the examples. The mass spectrometer had the following capabilities: 70 ev electron impact ionization, mass range from 35 to 1200 amu, direct probe insertion accessory with maximum temperature to at least 650° C., and software capable of integrating broad peaks typical of probe runs. The method was developed using a FinniganTM TSQ 7000TM instrument, scan range of 35 to 1400 (1 second scan time), conventional thin wire (with loop at tip) probe tips, source temperature of 180° C., 2×10−6 manifold vacuum, and FinniganTM ExcaliburTM software for peak integration and instrument control. Other instruments having comparable mass range and probe capabilities could be utilized.
In the DIPMS procedure, the sample is placed on the probe tip using a micro syringe. In practice, the smallest drop of sample which can be transferred to the probe usually gives the best results. After placing the sample on the probe, it is allowed to stand for about 5-10 min to allow for evaporation of the bulk of the diluent/solvent containing the compound of interest. Allowing the diluent/solvent to evaporate before inserting the probe into the instrument will, among other things, lessen the chance that the drop will fall off of the tip during the insertion process. After inserting the probe, the temperature program and data acquisition cycles begin. The temperature program used was 50° C. (hold 1 min), 30° C./min temperature ramp, 650° C. final temperature (hold 5 min). This program takes 26 minutes to complete. The filament was turned on 0.5 min into the run and kept on until the completion of the temperature program. After a couple of minutes to allow the probe tip to cool, the probe was removed from the instrument and the analysis cycle was complete.
The FinniganTM instrument had removable ion volumes; these were changed and cleaned after every two runs to minimize buildup of residue on the lens and other source components. The results are typically outputted as plots showing total ion current versus time.
Melt index (MI, g/10 min) was determined in accordance with ASTM D1238 at 190° C. with a 2,160 gram weight.
High load melt index (HLMI, g/10 min) was determined in accordance with ASTM D1238 at 190° C. with a 21,600 gram weight.
Polymer density was determined in grams per cubic centimeter (g/cc) on a compression molded sample, cooled at about 15° C. per hour, and conditioned for about 40 hours at room temperature in accordance with ASTM D1505 and ASTM D1928, procedure C.
Melt rheological characterizations were determined by suitable methods. For example, small-strain (10%) oscillatory shear measurements were performed on a Rheometrics Scientific, Inc. ARES rheometer using parallel-plate geometry. All rheological tests were performed at 190° C.
Molecular weights and molecular weight distributions were obtained using a PL 220 SEC high temperature chromatography unit (Polymer Laboratories) with trichlorobenzene (TCB) as the solvent, with a flow rate of 1 mL/minute at a temperature of 145° C. BHT (2,6-di-tert-butyl-4-methylphenol) at a concentration of 0.5 g/L was used as a stabilizer in the TCB. An injection volume of 200 μL was used with a nominal polymer concentration of 1.5 mg/mL. Dissolution of the sample in stabilized TCB was carried out by heating at 150° C. for 5 hours with occasional, gentle agitation. The columns used were three PLgel Mixed A LS columns (7.8×300 mm) and were calibrated with a broad linear polyethylene standard (Phillips Marlex® BHB 5003) for which the molecular weight had been determined Molecular weight distributions and branch profiles were obtained through size exclusion chromatography (SEC) using an FTIR detector. Chromatographic conditions are those described above. However, the sample injection volume was 500 μL. Samples were introduced to the FTIR detector via a heated transfer line and flow cell (KBr windows, 1 mm optical path, and ca. 70 μL cell volume). The temperatures of the transfer line and flow cell were kept at 143±1° C. and 140±1° C., respectively. A Perkin Elmer FTIR spectrophotometer (PE 2000) equipped with a narrow band mercury cadmium telluride (MCT) detector was used in these studies.
All spectra were acquired using Perkin Elmer Timebase software. Background spectra of the TCB solvent were obtained prior to each run. All IR spectra were measured at 8 cm−1 resolution (16 scans). Chromatograms were generated using the root mean square absorbance over the 3000-2700 cm−1 spectral region (i.e., FTIR serves as a concentration detector). Molecular weight calculations were made as previously described using a broad molecular weight polyethylene (PE) standard [see Jordens K, Wilkes G L, Janzen J, Rohlfing D C, Welch M B, Polymer 2000; 41:7175]. Spectra from individual time slices of the chromatogram were subsequently analyzed for comonomer branch levels using chemometric techniques. All calibration spectra were taken at sample concentrations which far exceeded that needed for good signal to noise (i.e., >0.08 mg/mL at the detector).
Branching content was determined as follows. Narrow molecular weight (weight-average molecular weight to number-average molecular weight ratio (Mw/Mn) of about 1.1 to 1.3), solvent gradient fractions of ethylene 1-butene, ethylene 1-hexene, polyethylene homopolymers, and low molecular weight alkanes were used in calibration and verification studies. The total methyl content of these samples ranged from 1.4 to 82.7 methyls per 1000 total carbons. Methyl content of samples was calculated from Mn or measured using C-13 NMR spectroscopy. C-13 NMR spectra were obtained on 15 weight percent samples in TCB using a 500 MHz Varian Unity Spectrometer run at 125° C. as previous described [see Randall J C, Hsieh E T, NMR and Macromolecules; Sequence, Dynamic, and Domain Structure, ACS Symposium Series 247, J. C. Randall, Ed., American Chemical Society, Washington D.C., 1984.]. Methyl content per 1000 carbons by NMR was obtained by multiplying (times 1000) the ratio of total methyl signals to total signal intensity.
A partial least squares (PLS) calibration curve was generated using Pirouette chemometric software (Infometrix) to correlate changes in the FTIR absorption spectra with calculated or NMR measured values for methyls/1000 total carbons for 25 samples. The FTIR absorption spectra used in the calibration model were made from co-added spectra collected across the whole sample. Only a portion of the spectral region (2996 and 2836 cm−1) was used in the calibration step in order to minimize the effects of residual solvent absorption. Preprocessing of spectral data included area normalization, taking the first derivative of the spectra and mean centering all data.
A four component calibration model was calculated and optimized using the process of cross validation (RSQ=0.999, SEV=0.7). The calibration model was verified using 23 additional samples. The predicted versus actual values for the validation data showed excellent correlation (RSQ=0.987) and exhibited a root mean square error of prediction equal to +/−0.4 methyl groups per 1000 total carbon molecules.
Short chain branching levels were calculated by subtracting out methyl chain end contributions. The amount of methyl chain ends were calculated using the equation Mece↑C(2−Vce)/Ms, where Mece is the number of methyl chain ends per 1000 total carbon molecules, C is a constant equal to 14000, Vce is the number of vinyl terminated chain ends (e.g., 1 for chromium catalyzed resins), and Ms is the molecular weight calculated for a particular slice of the molecular weight distribution.
Sulfated alumina was formed by a process wherein alumina was chemically-treated with a sulfate or bisulfate source. Such a sulfate or bisulfate source may include, for example, sulfuric acid, ammonium sulfate, or ammonium bisulfate. In an exemplary procedure, a commercial alumina sold as W.R. Grace Alumina A was sulfated by impregnation with an aqueous solution containing about 15-20% (NH4)2SO4 or H2SO4. This sulfated alumina was calcined at 550° C. in air (240° C./hr ramp rate), with a 3 hr hold period at this temperature. Afterward, the sulfated alumina was collected and stored under dry nitrogen, and was used without exposure to the atmosphere.
Example 1
Synthesis of 3-hexenyl-1,6-bis-[1-(methyl)-1-(cyclopentadienyl)-1-(2,7-di-tert-butylfluoren-1-yl)methane zirconium dichloride], C62H72Zr2Cl4 (DMET 1) Using Olefin Metathesis
DMET 1 is a nano-linked, dinuclear compound of the presented invention. It is produced using a single metallocene reactant and is, therefore, a homonuclear compound. The reactant metallocene used to produce DMET 1 is 1-(methyl)-1-(3-butenyl)-1-(cyclopentadienyl)-1-(2,7-di-tert-butylfluoren-1-yl)methane zirconium dichloride, C32H38ZrCl2 (abbreviated “MET 1”). The reaction scheme for this inventive example is illustrated below:




The MET 1 metallocene starting material can be prepared in accordance with suitable methods. One such technique is described in U.S. Pat. No. 7,064,225, the disclosure of which is incorporated herein by reference in its entirety.
Approximately 1 mg of bis(tricyclohexylphosphine)benzylidine ruthenium (IV) dichloride (Grubbs first generation metathesis catalyst) was charged to a reactor under an inert nitrogen atmosphere. After about 118 mg of MET 1 were added to the reactor, approximately 2 mL of benzene-d6 were added via syringe. The reaction was allowed to proceed at ambient temperature. Initially, an orange solution resulted and ethylene was released from the reaction mixture. As the reaction proceeded, the reaction mixture became a turbid orange color. After about 5 hours, approximately 2 mL of benzene-d6 were added to the reaction mixture. After 4 days, an orange suspension resulted. After 14 days, a few milligrams of the resulting solid suspension were removed from the reactor. This reaction product was dissolved in D-chloroform to form a dilute sample and was subsequently analyzed by 1H-NMR. Although the sample was very dilute, NMR confirmed the presence of the desired dinuclear compound, DMET 1.
Example 2
Hydrolysis of DMET 1, C62H72Zr2Cl4, to the Free Ligand, C62H76 
Approximately 25 mg of the solid DMET 1 reaction product of Example 1 were placed in a vial and hydrolyzed using about 10 microliters of water in about 0.5 mL of toluene. As shown in the following reaction scheme, the metal was hydrolyzed to the free ligand (C62H76) and the ligand was subsequently characterized.




The free ligand (C62H76) sample was analyzed using the thermal desorption mass spectrometry procedure, DIPMS, outlined above. As illustrated in FIGS. 1-2, the prominent molecular ion observed was consistent with the expected molecular mass of 820 Daltons of the free ligand (C62H76).
Example 3
Larger Scale Synthesis of DMET 1, C62H72Zr2Cl4, Using Olefin Metathesis
This olefin metathesis reaction used the same metallocene MET 1 reactant employed in Example 1. Approximately 2.4 g (approximately 5 mmol) of MET 1 were charged to a reactor under an inert atmosphere. About 100 mL of toluene were added to the reactor, creating a clear bright red-orange solution. A ruthenium catalyst mixture was prepared in a vial by mixing approximately 6 mg of bis(tricyclohexylphosphine)benzylidine ruthenium (IV) dichloride (Grubbs first generation metathesis catalyst) and about 6 ml of toluene. The resulting purple ruthenium catalyst solution was added to the MET 1 solution in the reactor in small portions over about 1 hour. After about 2.5 hours, the reaction mixture became cloudy. After 24 hours, another 10 mg of the ruthenium catalyst were added to the reaction mixture, which subsequently became very turbid. After 44 hours at ambient temperature, an insoluble red complex was observed sticking to the reactor walls and the solution became thicker. Another 8 mg of the ruthenium catalyst were added to the reaction mixture. After stirring for 5 more days (a total of 8 days at ambient temperature), the resulting red-orange mixture was capped and allowed to settle. Following a settling period of 11 days, the supernatant liquid was decanted from the solid phase. After 3 more days, the residual liquid was removed via filtration through a course frit over about 8 hours. The remaining solids were washed with four 15-mL portions of pentane under a mild vacuum. Drying under vacuum resulted in about 2.4 grams of a red-orange powder.
A portion of this reaction product was dissolved in D-chloroform and subsequently analyzed by 1H-NMR (see FIG. 3). NMR analysis confirmed that MET 1 was converted into isomeric dinuclear metallocene compound DMET 1. Isomers are derived from both the stereochemistry of the alkenyl double bond, cis or trans, as well as R or S chirality of the bridging carbon atom of the metallocene moiety.
FIG. 4 shows the NMR spectra for the MET 1 reactant in D-chloroform. Terminal vinyl protons are located between about 5.0 to 5.5 ppm. The disappearance of these proton resonances in FIG. 3 also demonstrates the conversion and metathesis of MET 1 to DMET 1.
Examples 4-11
Polymerization Runs Using Catalyst Systems Based on Dinuclear Metallocene DMET 1 and Metallocene MET 1
Dinuclear metallocene compounds of the present invention were used as part of a catalyst system to polymerize olefins. All polymerizations were conducted in a one-gallon stainless steel semi-batch reactor. Two liters of isobutane and alkyl aluminum co-catalyst were used in all polymerization experiments. The typical polymerization procedure was conducted as follows: alkyl aluminum, the activator-support and the metallocene were added in order through a charge port while venting isobutane vapor. The charge port was closed and about 2 liters of isobutane were added. The contents of the reactor were stirred and heated to the desired run temperature, and ethylene was then introduced along with the desired amount of hexene. Ethylene was fed on demand to maintain the specified pressure for the specified length of the polymerization run. The reactor was maintained and controlled at the desired run temperature throughout the polymerization. Upon completion, the ethylene flow was stopped and the reactor pressure slowly vented off. The reactor was opened and the polymer product was collected and dried under vacuum at approximately 50° C. for at least two hours.
Table I summarizes the catalyst system employed and resultant polymer properties of Examples 4-11. In Examples 4-11, the dinuclear metallocene product of Example 1 (DMET 1) and the reactant metallocene of Example 1 (MET 1) were compared. The specific polymerization conditions employed were a 30 minute run time, reaction temperature of 80° C., 450 psig ethylene feed, and 45 grams of 1-hexene with 0.5 mmol of triisobutylaluminum (TIBA) per 100 mg of sulfated alumina. The loading of the metallocene or dinuclear metallocene (MET 1 or DMET 1) was varied from about 5 micromoles Zr per gram of sulfated alumina to about 40 micromoles Zr per gram of sulfated alumina.
The dinuclear metallocene compound, DMET 1, was supplied from a solution containing 10 mg of DMET 1 in 20 mL of toluene. Thus, for instance, Example 4 was conducted using a 2.5 mg loading of DMET 1 on 100 mg of sulfated alumina (5 mL of DMET 1 in toluene solution), plus 0.5 mL of 1.0 M TIBA in hexanes.
The results in Table I indicate that polyolefin copolymer production (g PE produced) was similar between catalyst systems using both DMET 1 and MET 1. However, the results at low Zr loadings infer that DMET 1 has superior productivity to that of MET 1.
As shown by the short chain branch content in Table I, DMET 1 incorporated higher levels of 1-hexene than did MET 1 throughout the whole range of zirconium loadings. DMET 1 also enhanced incorporation of the comonomer as Zr loading is decreased, while MET 1 had a relatively flat response to Zr loadings.
MET 1 produced higher molecular weight copolymers than did DMET 1, whether compared using Mw or Mn in Table I. As Zr loadings decreased, Mw decreased for both catalysts, but the response was less for DMET 1. The enhanced incorporation of the DMET 1 dication, it appears, enhances chain transfer. Consequently, with DMET 1, molecular weight decreases less significantly as Zr loading is decreased.
FIGS. 5-6 illustrate rheology curves for the polymers of Examples 4-7 produced using a catalyst system including the dinuclear metallocene, DMET 1. The higher viscosity at low shear rates in FIG. 5 follows a pattern of increasing rheological breadth as the metallocene loading is decreased. Such polymers could be used in applications requiring a better shear response, such as a easier processing metallocene linear low density polyethylene.
FIGS. 7-10 show the molecular weight distributions of the polymers of Examples 4-11, plotted for comparison at the same Zr loadings. This data was generated using size exclusion chromatography, in accordance with the procedure discussed above. The broader molecular weight distributions for the polymers produced at high Zr loadings using DMET 1 are illustrated in FIGS. 9-10.







TABLE I







Comparison of DMET 1 with MET 1 at varied Zr loadings.


















μmol
g








Example
Catalyst
Zr/g
PE
SCB
Mn/1000
Mw/1000
PDI
MI
HLMI



















4
DMET 1
40
151
8.4
95.9
241.3
2.52
0.02
0.95


5
DMET 1
20
82
8.9
107.8
289.7
2.69
0
0.44


6
DMET 1
10
47
10.2
103.0
303.0
2.94
0
0.41


7
DMET 1
5
17
10.9
91.2
309.2
3.39
—
—


8
MET 1
40
181
6.7
116.4
253.7
2.18
0
0.72


9
MET 1
20
94
6.1
137.0
331.5
2.42
0
0.30


10
MET 1
10
27
7.6
111.2
413.8
3.72
0
0.12


11
MET 1
5
10
7.1
143.7
471.1
3.28
—
—





Notes on Table I:


μmol Zr/g—micromoles Zr per gram sulfated alumina.


g PE—grams ethylene/hexene copolymer produced.


SCB—number of short chain branches per 1000 carbon atoms.


Mn—number-average molecular weight.


Mw—weight-average molecular weight.


PDI—polydispersity index, Mw/Mn.


MI and HLMI—units of g/10 min.

## Claims

1. A catalyst composition comprising a contact product of at least one dinuclear metallocene compound and at least one activator-support,
wherein the at least one dinuclear metallocene compound has the formula:





wherein:
X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group connecting X3 and X4, the substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.

2. The catalyst composition of claim 1, wherein the at least one dinuclear metallocene compound is:







or a combination thereof; wherein Ph is an abbreviation for phenyl.

3. The catalyst composition of claim 1, wherein the at least one activator-support is fluorided alumina, chlorided alumina, bromided alumina, sulfated alumina, fluorided silica-alumina, chlorided silica-alumina, bromided silica-alumina, sulfated silica-alumina, fluorided silica-zirconia, chlorided silica-zirconia, bromided silica-zirconia, sulfated silica-zirconia, or any combination thereof.

4. The catalyst composition of claim 1, wherein the at least one activator-support comprises a solid oxide treated with an electron-withdrawing anion, wherein:
the solid oxide is silica, alumina, silica-alumina, aluminum phosphate, heteropolytungstates, titania, zirconia, magnesia, boria, zinc oxide, any mixed oxides thereof, or any mixture thereof; and
the electron-withdrawing anion is fluoride, chloride, bromide, phosphate, triflate, bisulfate, sulfate, or any combination thereof.

5. The catalyst composition of claim 1, wherein the at least one activator-support further comprises a metal or metal ion, and wherein the metal or metal ion is zinc, nickel, vanadium, silver, copper, gallium, tin, tungsten, molybdenum, or any combination thereof.

6. The catalyst composition of claim 1, wherein the at least one activator-support comprises a clay mineral, a pillared clay, an exfoliated clay, an exfoliated clay gelled into another oxide matrix, a layered silicate mineral, a non-layered silicate mineral, a layered aluminosilicate mineral, a non-layered aluminosilicate mineral, or any combination thereof.

7. The catalyst composition of claim 1, further comprising at least one organoaluminum compound having the formula:


Al(X5)m(X6)3-m;


wherein:
X5 is a hydrocarbyl;
X6 is an alkoxide or an aryloxide, a halide, or a hydride; and
m is from 1 to 3, inclusive.

8. The catalyst composition of claim 7, wherein the at least one organoaluminum compound is trimethylaluminum, triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide, tri-n-butylaluminum, diisobutylaluminum hydride, triisobutylaluminum, diethylaluminum chloride, or any combination thereof.

9. The catalyst composition of claim 1, further comprising at least one optional co-catalyst, wherein the at least one optional co-catalyst is at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof.

10. The catalyst composition of claim 1, wherein in formula (I):
X1 and X2 independently are a methyl group, a phenyl group, or a chlorine atom;
X3 is a substituted cyclopentadienyl group and X4 is a substituted fluorenyl group;
A2 comprises a carbon bridging atom;
M is Zr or Hf;
RX, RY, and RZ are hydrogen atoms; and
n is 0, 1, 2, 3, or 4.

11. A catalyst composition comprising a contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof;
wherein the at least one dinuclear metallocene compound has the formula:





wherein:
X1 and X2 independently are a halide or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom or a substituted or unsubstituted alkyl or alkenyl group;
A2 is a substituted bridging group connecting X3 and X4, the substituted bridging group comprising either a silicon bridging atom, a germanium bridging atom, a tin bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, or a substituted or unsubstituted aliphatic, aromatic, or cyclic group, or a combination thereof; and
n is an integer in a range from 0 to 12, inclusive.

12. The catalyst composition of claim 11, wherein the at least one compound is at least one aluminoxane compound, and the at least one aluminoxane compound comprises:
(a) a cyclic aluminoxane having the formula:





wherein:
R is a linear or branched alkyl having from 1 to 10 carbon atoms; and
p is an integer from 3 to 20;

(b) a linear aluminoxane having the formula:





wherein:
R is a linear or branched alkyl having from 1 to 10 carbon atoms; and
q is an integer from 1 to 50;

(c) a cage aluminoxane having the formula Rt5r+αRbr−+Al4rO3r,
wherein:
Rt is a terminal linear or branched alkyl group having from 1 to 10 carbon atoms;
Rb is a bridging linear or branched alkyl group having from 1 to 10 carbon atoms;
r is 3 or 4; and
α is equal to nAl(3)−nO(2)+nO(4), wherein nAl(3) is the number of three coordinate aluminum atoms, nO(2) is the number of two coordinate oxygen atoms, and nO(4) is the number of 4 coordinate oxygen atoms; or

any combination thereof.

13. The catalyst composition of claim 11, wherein the at least one compound is at least one organoboron or organoborate compound, and the at least one organoboron or organoborate compound is N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, lithium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tris(pentafluorophenyl)boron, tris[3,5-bis(trifluoromethyl)phenyl]boron, or any combination thereof.

14. The catalyst composition of claim 11, wherein the at least one compound is at least one ionizing ionic compound, and the at least one ionizing ionic compound is tri(n-butyl)ammonium tetrakis(p-tolyl)borate, tri(n-butyl)ammonium tetrakis(m-tolyl)borate, tri(n-butyl)ammonium tetrakis(2,4-dimethyl)borate, tri(n-butyl)ammonium tetrakis(3,5-dimethylphenyl)borate, tri(n-butyl)ammonium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tri(n-butyl)ammonium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis(p-tolyl)borate, N,N-dimethylanilinium tetrakis(m-tolyl)borate, N,N-dimethylanilinium tetrakis(2,4-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis(3,5-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis(p-tolyl)borate, triphenylcarbenium tetrakis(m-tolyl)borate, triphenylcarbenium tetrakis(2,4-dimethylphenyl)borate, triphenylcarbenium tetrakis(3,5-dimethylphenyl)borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, tropylium tetrakis(p-tolyl)borate, tropylium tetrakis(m-tolyl)borate, tropylium tetrakis(2,4-dimethylphenyl)borate, tropylium tetrakis(3,5-dimethylphenyl)borate, tropylium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tropylium tetrakis(pentafluorophenyl)borate, lithium tetrakis(pentafluorophenyl)borate, lithium tetraphenylborate, lithium tetrakis(p-tolyl)borate, lithium tetrakis(m-tolyl)borate, lithium tetrakis(2,4-dimethylphenyl)borate, lithium tetrakis(3,5-dimethylphenyl)borate, lithium tetrafluoroborate, sodium tetrakis(pentafluorophenyl)borate, sodium tetraphenylborate, sodium tetrakis(p-tolyl)borate, sodium tetrakis(m-tolyl)borate, sodium tetrakis(2,4-dimethylphenyl)borate, sodium tetrakis(3,5-dimethylphenyl)borate, sodium tetrafluoroborate, potassium tetrakis(pentafluorophenyl)borate, potassium tetraphenylborate, potassium tetrakis(p-tolyl)borate, potassium tetrakis(m-tolyl)borate, potassium tetrakis(2,4-dimethylphenyl)borate, potassium tetrakis(3,5-dimethylphenyl)borate, potassium tetrafluoro-borate, lithium tetrakis(pentafluorophenyl)aluminate, lithium tetraphenylaluminate, lithium tetrakis(p-tolyl)aluminate, lithium tetrakis(m-tolyl)aluminate, lithium tetrakis(2,4-dimethylphenyl)aluminate, lithium tetrakis(3,5-dimethylphenyl)aluminate, lithium tetrafluoroaluminate, sodium tetrakis(pentafluorophenyl)aluminate, sodium tetraphenylaluminate, sodium tetrakis(p-tolyl)aluminate, sodium tetrakis(m-tolyl)aluminate, sodium tetrakis(2,4-dimethylphenyl)aluminate, sodium tetrakis(3,5-dimethylphenyl)aluminate, sodium tetrafluoroaluminate, potassium tetrakis(pentafluorophenyl)aluminate, potassium tetraphenylaluminate, potassium tetrakis(p-tolyl)aluminate, potassium tetrakis(m-tolyl)aluminate, potassium tetrakis(2,4-dimethylphenyl)aluminate, potassium tetrakis (3,5-dimethylphenyl)aluminate, potassium tetrafluoroaluminate, or any combination thereof.

15. The catalyst composition of claim 11, wherein the at least one dinuclear metallocene compound is:







or a combination thereof; wherein Ph is an abbreviation for phenyl.

16. The catalyst composition of claim 11, wherein in formula (I):
X1 and X2 independently are a methyl group, a phenyl group, or a chlorine atom;
X3 is a substituted cyclopentadienyl group and X4 is a substituted fluorenyl group;
A2 comprises a carbon bridging atom;
M is Zr or Hf;
RX, RY, and RZ are hydrogen atoms; and
n is 0, 1, 2, 3, or 4.

17. A catalyst composition comprising a contact product of at least one dinuclear metallocene compound and at least one activator-support,
wherein the at least one dinuclear metallocene compound has the formula:





wherein:
X1 and X2 independently are a methyl group, a phenyl group, a benzyl group, or a halide;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom, a methyl group, an ethyl group, a propyl group, a n-butyl group, a t-butyl group, or a hexyl group;
A2 is a substituted bridging group connecting X3 and X4, the substituted bridging group comprising either a silicon bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, a methyl group, a phenyl group, or a benzyl group;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a phenyl group, a tolyl group, or a benzyl group; and
n is an integer in a range from 0 to 7, inclusive; and
the at least one activator-support comprises a solid oxide treated with an electron-withdrawing anion, wherein:
the solid oxide is silica, alumina, silica-alumina, aluminum phosphate, heteropolytungstates, titania, zirconia, magnesia, boria, zinc oxide, any mixed oxides thereof, or any mixture thereof; and
the electron-withdrawing anion is fluoride, chloride, bromide, phosphate, triflate, bisulfate, sulfate, or any combination thereof.

18. The catalyst composition of claim 17, further comprising at least one organoaluminum compound, wherein the at least one organoaluminum compound is trimethylaluminum, triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide, tri-n-butylaluminum, diisobutylaluminum hydride, triisobutylaluminum, diethylaluminum chloride, or any combination thereof; and
wherein the at least one activator-support is fluorided alumina, chlorided alumina, bromided alumina, sulfated alumina, fluorided silica-alumina, chlorided silica-alumina, bromided silica-alumina, sulfated silica-alumina, fluorided silica-zirconia, chlorided silica-zirconia, bromided silica-zirconia, sulfated silica-zirconia, or any combination thereof.

19. A catalyst composition comprising a contact product of at least one dinuclear metallocene compound and at least one compound selected from at least one aluminoxane compound, at least one organozinc compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof;
wherein the at least one dinuclear metallocene compound has the formula:





wherein:
X1 and X2 independently are a methyl group, a phenyl group, a benzyl group, or a halide;
X3 and X4 independently are a substituted cyclopentadienyl, indenyl, or fluorenyl group, any substituents on X3 and X4 other than a bridging group independently are a hydrogen atom, a methyl group, an ethyl group, a propyl group, a n-butyl group, a t-butyl group, or a hexyl group;
A2 is a substituted bridging group connecting X3 and X4, the substituted bridging group comprising either a silicon bridging atom, a carbon bridging atom, or a bridging chain of 2 to 5 carbon atoms, any substituents on A2 other than an alkenyl linking group independently are a hydrogen atom, a methyl group, a phenyl group, or a benzyl group;
M is Zr, Hf, or Ti;
RX, RY, and RZ independently are a hydrogen atom, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a phenyl group, a tolyl group, or a benzyl group; and
n is an integer in a range from 0 to 7, inclusive.

20. The catalyst composition of claim 19, wherein the at least one compound is at least one aluminoxane compound, and the at least one aluminoxane compound comprises:
(a) a cyclic aluminoxane having the formula:





wherein:
R is a linear or branched alkyl having from 1 to 10 carbon atoms; and
p is an integer from 3 to 20;

(b) a linear aluminoxane having the formula:





wherein:
R is a linear or branched alkyl having from 1 to 10 carbon atoms; and
q is an integer from 1 to 50;

(c) a cage aluminoxane having the formula Rt5r+αRbr−αAl4rO3r,
wherein:
Rt is a terminal linear or branched alkyl group having from 1 to 10 carbon atoms;
Rb is a bridging linear or branched alkyl group having from 1 to 10 carbon atoms;
r is 3 or 4; and
α is equal to nAl(3)−nO(2)+nO(4), wherein nAl(3) is the number of three coordinate aluminum atoms, nO(2) is the number of two coordinate oxygen atoms, and nO(4) is the number of 4 coordinate oxygen atoms; or
any combination thereof.

21. The catalyst composition of claim 19, wherein the at least one compound is at least one organoboron or organoborate compound, and the at least one organoboron or organoborate compound is N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, lithium tetrakis-(pentafluorophenyl)borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tris(pentafluorophenyl)boron, tris[3,5-bis(trifluoromethyl)phenyl]boron, or any combination thereof.

22. The catalyst composition of claim 19, wherein the at least one compound is at least one ionizing ionic compound, and the at least one ionizing ionic compound is tri(n-butyl)ammonium tetrakis(p-tolyl)borate, tri(n-butyl)ammonium tetrakis(m-tolyl)borate, tri(n-butyl)ammonium tetrakis(2,4-dimethyl)borate, tri(n-butyl)ammonium tetrakis(3,5-dimethylphenyl)borate, tri(n-butyl)ammonium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tri(n-butyl)ammonium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis(p-tolyl)borate, N,N-dimethylanilinium tetrakis(m-tolyl)borate, N,N-dimethylanilinium tetrakis(2,4-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis(3,5-dimethylphenyl)borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, triphenylcarbenium tetrakis(p-tolyl)borate, triphenylcarbenium tetrakis(m-tolyl)borate, triphenylcarbenium tetrakis(2,4-dimethylphenyl)borate, triphenylcarbenium tetrakis(3,5-dimethylphenyl)borate, triphenylcarbenium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbenium tetrakis(pentafluorophenyl)borate, tropylium tetrakis(p-tolyl)borate, tropylium tetrakis(m-tolyl)borate, tropylium tetrakis(2,4-dimethylphenyl)borate, tropylium tetrakis(3,5-dimethylphenyl)borate, tropylium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tropylium tetrakis(pentafluorophenyl)borate, lithium tetrakis(pentafluorophenyl)borate, lithium tetraphenylborate, lithium tetrakis(p-tolyl)borate, lithium tetrakis(m-tolyl)borate, lithium tetrakis(2,4-dimethylphenyl)borate, lithium tetrakis(3,5-dimethylphenyl)borate, lithium tetrafluoroborate, sodium tetrakis(pentafluorophenyl)borate, sodium tetraphenylborate, sodium tetrakis(p-tolyl)borate, sodium tetrakis(m-tolyl)borate, sodium tetrakis(2,4-dimethylphenyl)borate, sodium tetrakis(3,5-dimethylphenyl)borate, sodium tetrafluoroborate, potassium tetrakis(pentafluorophenyl)borate, potassium tetraphenylborate, potassium tetrakis(p-tolyl)borate, potassium tetrakis(m-tolyl)borate, potassium tetrakis(2,4-dimethylphenyl)borate, potassium tetrakis(3,5-dimethylphenyl)borate, potassium tetrafluoro-borate, lithium tetrakis(pentafluorophenyl)aluminate, lithium tetraphenylaluminate, lithium tetrakis(p-tolyl)aluminate, lithium tetrakis(m-tolyl)aluminate, lithium tetrakis(2,4-dimethylphenyl)aluminate, lithium tetrakis(3,5-dimethylphenyl)aluminate, lithium tetrafluoroaluminate, sodium tetrakis(pentafluorophenyl)aluminate, sodium tetraphenylaluminate, sodium tetrakis(p-tolyl)aluminate, sodium tetrakis(m-tolyl)aluminate, sodium tetrakis(2,4-dimethylphenyl)aluminate, sodium tetrakis(3,5-dimethylphenyl)aluminate, sodium tetrafluoroaluminate, potassium tetrakis(pentafluorophenyl)aluminate, potassium tetraphenylaluminate, potassium tetrakis(p-tolyl)aluminate, potassium tetrakis(m-tolyl)aluminate, potassium tetrakis(2,4-dimethylphenyl)aluminate, potassium tetrakis (3,5-dimethylphenyl)aluminate, potassium tetrafluoroaluminate, or any combination thereof.