www.nature.com/scientificreports

OPEN

received: 27 October 2015
accepted: 26 January 2016
Published: 12 February 2016

Cesium adsorption/desorption
behavior of clay mineralsconsidering actual contamination
conditions in Fukushima
Hiroki Mukai1, Atsushi Hirose2, Satoko Motai1, Ryosuke Kikuchi1, Keitaro Tanoi2,
Tomoko M. Nakanishi2, Tsuyoshi Yaita3 & Toshihiro Kogure1
Cesium adsorption/desorption experiments for various clay minerals, considering actual contamination
conditions in Fukushima, were conducted using the 137Cs radioisotope and an autoradiography using
imaging plates (IPs). A 50 μl solution containing 0.185 ~ 1.85 Bq of 137Cs (10−11 ~ 10−9 molL−1 of 137Cs)
was dropped onto a substrate where various mineral particles were arranged. It was found thatpartially-vermiculitized biotite, which is termed “weathered biotite” (WB) in this study, from Fukushimasorbed 137Cs far more than the other clay minerals (fresh biotite, illite, smectite, kaolinite, halloysite,
allophane, imogolite) on the same substrate. When WB was absent on the substrate, the amount of137
Cs sorbed to the other clay minerals was considerably increased, implying that selective sorption
to WB caused depletion of radiocesium in the solution and less sorption to the coexisting minerals.
Cs-sorption to WB continued for about one day, whereas that to ferruginous smectite was completed
within one hour. The sorbed 137Cs in WB was hardly leached with hydrochloric acid at pH 1, particularly
in samples with a longer sorption time. The presence/absence of WB sorbing radiocesium is a key factor
affecting the dynamics and fate of radiocesium in Fukushima.
Since the accident at Fukushima Dai-ichi Nuclear Power Plant (FDNPP) in March 2011, detailed understandingof the chemical state and dynamics of radiocesium, which is responsible for the high air dose rate in the contaminated area, has been an important issue. Studies conducted before the accident proposed that micaceous
minerals are responsible for retaining radiocesium in the soil1,2. Several groups suggested that illite, a dioctahedral
interlayer-deficient mica containing aluminum as the major octahedral cation3, is the major sorbent mineral ofradiocesium in soil, and they investigated its Cs-sorption properties4–9. Some of them5,7,9 suggested that the structure of illite contains several kinds of sorption sites with different affinities and densities. Such results were also
reported for actual soils or sediments, from similar Cs-adsorption experiments10–13. In these studies, the highest
affinity (but low density) site was suggested to be located at the frayed edges of micaceous minerals, termed“frayed-edge-sites” (FES)1,14. On the other hand, several works reported that hydroxyl-intercalated vermiculite(HIV) also effectively sorbs and fixes Cs ions15–18. The origin of the high Cs-affinity of HIV is attributed to thewedge-like interlayer transition zone from mica to HIV, which offers sorption sites suitable for Cs and Rb, similar
to FES in micas18.
On the other hand, Mukai et al.19 reported that partially-vermiculitized biotite, called “weathered biotite(WB)” in their study, and which originated from the weathering of granite in Fukushima, was a major material
in the soil contaminated with radiocesium collected from Fukushima. Komarneni et al.20 reported the superior sorption property of altered phlogopite such as vermiculite. However, a recent study21 which surveyed theCs-sorption ability of various clay minerals indicated that vermiculite was not superior to the other micaceous
clay minerals like illite and smectite. Therefore, a further experiment was expected to discover whether the WB
in Fukushima is superior in adsorbing Cs to other clay minerals in Fukushima. First of all, the Cs-adsorption
1
Graduate School of Sciences, The University of Tokyo, Bunkyo, Tokyo 113-0033, Japan. 2Graduate School of
Agricultural and Life Sciences, The University of Tokyo, Bunkyo, Tokyo 113-8657, Japan. 3Quantum Beam Science
Center and Fukushima Environmental Safety Center, Japan Atomic Energy Agency, 1-1-1 Kouto, Sayo-cho, Sayogun, Hyogo 679-5148, Japan. Correspondence and requests for materials should be addressed to T.K. (email:kogure@eps.s.u-tokyo.ac.jp)

Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

1www.nature.com/scientificreports/

Figure 1. A matrix of the read-out images of IPs covering the substrates with various mineral particles (fiveparticles for each species) sorbed radiocesium from the solutions. The radioactivity input to the solution
and reaction time are at the top and left, respectively. The figure at the top-right of each image is the percentage
of radioactivity (or 137Cs) sorbed to the whole mineral particles, estimated from the IP signal. See Fig. S1 forthe arrangement of the mineral particles. The abbreviations at the bottom-right mean FB: fresh biotite, WB:
weathered biotite, K: kaolinite, H: halloysite. IL: illite, M: montmorillonite, A: allophane, IM: imogolite.

experiments21 were performed using a solution with a cesium concentration as low as sub-ppm (~10−5 molL−1).
However, the Cs-adsorption property of minerals is dependent on the concentration of cesium in the solution
and/or the ratio between the amount of the minerals and that of Cs ion in the solution22. The actual concentrationof radiocesium in the raindrops which caused the radioactive contamination is considered to be very low. For
instance, the amount of rainfall in Iitate-village, a seriously contaminated area in Fukushima, in a few weeks after
the accident was approx. 10 mm according to the records of the Japan Meteorological Agency23. On the other
hand, the amount of 137Cs per unit area deposited on Iitate-village was ~106 Bq/m2 in the literature24. From thesevalues, the concentration in the raindrops should have been in the order of 10 ppt (10−10 molL−1). In order todiscuss the cesium contamination event in the Fukushima soil, the sorption experiments should be performed
using a similar low concentration of Cs. However, this is close to or below the detection limit of the most sensitive
analytical instruments. This problem can be solved if radioactive cesium itself is used as the cesium source andthe sorption/desorption process is estimated by measuring the radiation from the radioisotope, as was done inprevious works6,13,22. Moreover, we evaluated the sorption amounts of 137Cs in the minerals by measuring the radiation in the individual mineral particles using quantitative autoradiography with imaging plates (IPs), instead ofcounting gamma-rays. By using IP autoradiography, we can investigate kinetic aspects of the reaction between asolution and multi-minerals (the details are described later). This approach is considered to reproduce better thereaction between the raindrops and soil that consists of various mineral species actually occurring in Fukushima,
than the reaction between a solution and mono-mineral. In the present study, the results of such unique adsorption/desorption experiments for clay minerals possibly present in Fukushima soils are shown. They clearly indicate the importance of WB as the radiocesium sorbent in Fukushima.

Results and Discussion

Competitive Cs-adsorption among the minerals. Eight mineral species, with four or five particles~50 μ m in size for each species, were arranged in the area of a 4 mm by 7 mm square on an acrylic substratewith Kapton double stick tape (Fig. S1). Then, 50 μ L solutions containing 3.7, 37 and 370 Bq/mL (0.185, 1.85 and18.5 Bq in the solutions) of 137Cs were dropped to cover all the particles on the substrates. The read-out imagesof the IPs are presented in Fig. 1. Under any condition with different 137Cs concentrations and immersion periods, the amount of 137Cs sorbed by WB collected from Fukushima was much higher than the other minerals. In
Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

2www.nature.com/scientificreports/

Figure 2. Read-out images of IPs covering the substrates with (a) several smectite species, (b) ferruginous
smectite (SWa-1) and several mineral species other than smectite, (c) WB and SWa-1. Four particles werearranged on the substrates for each mineral species. The radioactivity input to the solution was 1.85 Bq and thereaction period was 24 hours. The meanings of the figure at the top-right of each image and abbreviations of theminerals are the same as those in Fig. 1.

the case of the lower concentrations of 137Cs and/or shorter reaction periods, only 137Cs was detected at the WB
imaging position, showing that WB was the only species sorbing 137Cs. At the concentration of 18.5 Bq/50 μ L andwith a reaction for one day, the sorbed amount of 137Cs by WB was about two orders of magnitude higher than
the amount of the other clay minerals. These results definitely indicate that WB, which is abundant in weathered
granitic soil, sorbs cesium far more than the other clay minerals at a comparable cesium concentration to that for
the wet-deposition in Fukushima. This result is consistent with our previous result that WB was frequently foundin fine radioactive particles collected from contaminated soil in Fukushima19. Our recent investigation25 indicatedthat the radioactive soil particles in the field generally have radioactivity of about the order of 10−3 ~ 10−2 Bq,
which roughly corresponded to the results in Fig. 1 with a concentration ranging from 0.185 Bq/50 μ L to
1.85 Bq/50 μ L. It is not certain where the actual sorption sites of cesium are in the structure of WB at such a low
concentration level. Considering the extremely low concentration of radiocesium, it is probable that the sorption
sites are those with the highest affinity in the mineral. As proposed in previous works14,18, such sites may be FES or
the transition interlayer zone like that in HIV, where the non-hydrated cesium ion with a larger ionic radius thanthat of potassium resides stably. However, further sophisticated experiments are needed to prove this hypothesis.
On the other hand, the Cs-sorption ability of illite, which has been suggested in the previous works4–9 to be adominant Cs-adsorbent in the contaminated soil, was far lower than WB, though it is evident that mineral species
alone do not control the sorption property.
In the experiments shown in Fig. 1, we used montmorillonite as the representative of the smectite group. This
group includes various kinds of mineral species with different compositions. As is shown in Fig. 1, montmorillonite particles did not appear at all in the IP read-out images, indicating a very weak sorption ability. Hence, we
prepared several smectite species and compared their sorption abilities using the same procedure (Fig. 2a). In theexperiment, montmorillonite sorbed the least amount of 137Cs and ferruginous smectite, SWa-1, sorbed the highest amount of cesium. Saponite and nontronite were at an intermediate level. Such ferruginous smectite was also
found in the paddy soil in Iitate-village, Fukushima, as a Cs-sorbent beside WB in our previous work26. It was also
found that SWa-1 sorbed more 137Cs than the other clay minerals except for WB (Fig. 2b). However, the sorption
amount to SWa-1 was also negligible when it coexisted with WB on the same substrate (Fig. 2c).
From estimation of the total amount of radiocesium sorbed in the minerals from the IP images, it was apparent that the radiocesium in the solution was not so depleted by the sorption to WB in these experiments (Figs 1
and 2). Hence, it was suspected that the reason for the low Cs amounts sorbed in the other minerals coexistingwith WB was low Cs-affinities of these minerals at the low cesium concentration. However, Fig. 2 shows that
SWa-1 without WB on the same substrate sorbed far more cesium than that with WB, which implies the depletion of radiocesium by the sorption to WB. An interpretation of this result is that actually most of the cesium
was sorbed by WB and the cesium was depleted in the solution, but a considerable amount of sorbed cesium on
WB was not tightly sorbed; therefore, it was removed with the solution when the solution was flushed before IP
autoradiography.
Besides the amount of the cesium sorbed, the time needed to complete the adsorption was different between
WB and SWa-1. Figure 3 shows the IP read-out images of WB and SWa-1 after immersion for one hour, one day
and one week, and gives the percentage of 137Cs sorbed in the minerals. The amount of cesium sorbed to WB
gradually increased with time but the sorption to SWa-1 was almost complete after one hour and further sorption
did not occur, suggesting that there were differences of the sorption sites and/or mechanisms between the twominerals. In Fig. 3a, the amount of the sorbed cesium to WB seems to be larger after one week than after one day,showing that the sorption continued for more than one day. However, it should be noted that the mineral particles
in each run in Fig. 3 were not the same ones. It is possible that the third WB particle from the top run for one
Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

3

www.nature.com/scientificreports/

Figure 3. A matrix of the read-out images of IPs covering the substrates with four mineral particles of(top) WB and (bottom) SWa-1, reacted with 1.85 Bq 137Cs solution for various periods. Notice that only one
mineral species was placed on the substrates and the mineral particles were different for each run.
week had an extremely high sorption ability, and the amount of sorption to WB in one day and one week may becomparable.

Desorption characteristics of WB and SWa-1.

Desorption experiments were conducted using theCs-sorbed particles of WB and SWa-1, and various electrolyte solutions for elution. We selected four kinds ofelectrolyte solutions; 1 mol L−1 of ammonium acetate (CH3COONH4), 1 mol L−1 of cesium chloride (CsCl), 1 mol
L−1 of magnesium nitrate (Mg(NO3)2) and 0.1 mol L−1 of hydrochloric acid (HCl). 1 mol L−1 of ammonium acetate is a typical solution to extract ion-exchangeable cations from soil samples7,27. Cesium chloride was adopted
to examine the isotopic exchangeability at the sorption sites. Magnesium nitrate has been reported to efficiently
remove cesium sorbed in vermiculite28. Finally, 0.1 molL−1 (pH 1) of hydrochloric acid was selected to examine
whether sorbed cesium in the minerals is desorbed or not with gastric fluid of organism. Desorption was conducted by immersing the mineral particles with sorbed radiocesium in each of these solutions of 50 μ L for one
day. The results are presented in Fig. 4. Radiocesium in WB was hardy decreased with ammonium acetate andcesium chloride solutions, but was decreased to about half with magnesium nitrate and hydrochloric acid. In contrast, half of the sorbed cesium in SWa-1 was eluted by ammonium acetate and cesium chloride, and almost completely eluted by magnesium nitrate and hydrochloric acid. Finally, the desorption experiments were conductedwith WB particles as shown in Fig. 3, to which 137Cs was sorbed with reaction times of one hour, one day and one
Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

4www.nature.com/scientificreports/

Figure 4. A matrix of the IP read-out images, to show the desorption feature of 137Cs from (top) WB
and (bottom) SWa-1 using various electrolyte solutions. Initially 137Cs was sorbed to the mineral particles
from a 50 μ L solution with 1.85 Bq for one day. The elution was performed by immersing the substrates in theelectrolyte solutions (50 μ L) for one day. The figure at the bottom of each image represents the percentage of137
Cs remaining in the mineral particles after the immersion.

Figure 5. IP read-out images to show the desorption of 137Cs by HCl solution (pH 1) from WB particles,
which sorbed 137 Cs from the solution (18.5 Bq) with different reaction periods, and that from “natural”
radioactive WB particles collected in Fukushima. Notice that the images before the elution are the same as
those at the top of Fig. 3, except for the “natural” particles. Total radioactivity before the elution is shown at thetop, and the percentage of 137Cs remaining in the mineral particles after the elution is shown at the bottom.
week, and with “natural” radioactive WB particles collected from Fukushima19 (Fig. 5). The percentage of cesium
desorbed was larger in the particles sorbed for one hour than those sorbed for one week, though the sorbed 137Cs
amount was much higher in the particles reacted for one week. Although the actual mechanism is not clear, akind of “aging” effect may exist to increase the affinity of the sorption with time. On the other hand, actual WB
particles that sorbed radiocesium in Fukushima released almost half of the radiocesium by the hydrochloric acidsolution. Since these particles had been in the field for more than two years, more immobilization of the sorbed
radiocesium was expected than that prepared in the laboratory for the one-week treatment, but actually there wasno notable difference between the samples from the field and those in the laboratory. The reason is not clear but it
might be due to the difference in the weathering stage between the two WB specimens.
In conclusion, the experimental results in the present study clearly indicated that WB can be the major adsorbent of radiocesium if this material is present in the soil, and the dynamics (retention/diffusion) of radiocesium inthe soil are strongly dependent on whether WB is present or not. A recent work29 reported that the transfer factorof radiocesium from the soil to rice in Fukushima was completely different in soils with and without vermiculite.
Our results clearly support the view that such a phenomenon actually occurred in Fukushima.

Methods

Mineral Description. WB and its original (fresh biotite: FB) were collected from an outcrop in Ono-City,
Fukushima, Japan, where granodiorite of the older type of Abukuma granitic rocks30 is exposed. This area islocated about 40 km south-west of the FDNPP. The biotite crystals are a few millimeters in width and thickness. The composition of FB was determined to be (K0.88Na0.01Ca0.01)(Fe1.33Mg1.08Mn0.02Al0.24Ti0.16)(Si2.83Al1.17)
Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

5www.nature.com/scientificreports/
O10(OH)2, by electron-probe microanalyses. There were various WB crystals with different weathering stages, thevariation mainly depending on their location in the outcrop. In this study, we selected the one that appeared themost weathered. Although the chemical composition significantly varied between individual crystals and also
inside a crystal (Fig. S2), the averaged composition is roughly expressed as (K0.16,Ca0.07)(Fe0.71Mg0.64Al0.25Ti0.22)(Si2.67Al1.33)O10(OH)2, showing a dioctahedral character with the oxidation of iron and leaching of potassiumby the hydration of the interlayer, or “vermiculitization”. The XRD patterns of WB and FB are shown in Fig. S3.
For several clay mineral species, clay specimens distributed by the Japanese Clay Science Society (JCSS) wereused. They were montmorillonite (JCSS-3101), saponite (JCSS-3501), and illite (JCSS-5101)31. The ferruginous
smectite and nontronite adopted were SWa-1 and NG-1, respectively, supplied from the source clay minerals of
the Clay Mineral Society32. The kaolinite specimen originated from Oguni, Yamagata, Japan. X-ray diffraction
showed that the specimen was completely mono-mineral with ordered stacking. Halloysite was from Eureka,
Nevada, USA33. The allophane specimen originated from Kitakami, Iwate, Japan34 and the imogolite came from
Kurayoshi, Tottori, Japan35.
The biotite crystals and consolidated clay minerals were crushed in agate mortar and sieved to 25–53 μ m insize. The minerals in a fine powder form were consolidated into a pellet with a hydraulic press, then crushed andsieved to obtain a similar particle size. Typical appearances of these mineral particles are shown in Fig. S4.

RI solutions.

The carrier-free 137Cs solution (3.7 MBq mL−1 nominal, Eckert & Ziegler Isotope Products,
California, USA) was diluted to 370 Bq mL−1 (8.4 × 10−10 molL−1), 37 Bq mL−1 (8.4 × 10−11 molL−1), and 3.7 Bq
mL−1 (8.4 × 10−12 molL−1) with reverse osmosis water. Since the 137Cs solution is a “reactor produced” isotope
product, it probably contains a comparable amount of 133Cs with 137Cs in the solution.

Adsorption/desorption experiments.

Mineral grains of similar size were selected under a stereomicroscope and arranged on acrylic substrates with Kapton double stick tape, using vacuum tweezers attached to a
micro-manipulator (Quick Pro, Micro Support Co., Ltd.) (Fig. S1). Solutions of 50 μ L which contained 0.185, 1.85
and 18.5 Bq of 137Cs were dropped onto the minerals on the substrate with a micropipette. Then the substrates
were enclosed in a styrol box to avoid desiccation, and afterwards, gently flushed with ~10 mL of running water.
For the desorption experiments the Cs-sorbed minerals were reacted with four kinds of electrolyte solutions;
CH3COONH4 (1 molL−1), CsCl (1 molL−1), Mg(NO3)2 (1 molL−1) and HCl (0.1 molL−1). The pH values of thesesolutions were 6.97, 4.26, 5.06 and 1.06, respectively. Each 50 μ L solution was dropped onto the substrates andgently flushed after 24 hours.
The adsorbed amounts of 137Cs in the minerals were estimated by IP autoradiography. The substrates withminerals were covered with a water-soluble oblate sheet 20 μ m in thickness and placed in contact with an IP(BAS-MS, Fuji Film) in the dark for 24 hours. The IP image produced was scanned with an IP reader (FLA7000, Fuji Film). The read-out images were colored up to be linearly proportional to the IP signal using a Gatan
Digital Micrograph 3.10.0. The amount of 137Cs in each mineral particle was estimated from the calibration curve
between the IP signal integrated over the spot formed by radioactive particles and the radioactivity from the particles measured by a germanium radiation spectrometer (Fig. S5). On the other hand, the total amount of 137Cs on
a substrate was measured using a germanium radiation spectrometer and compared with the sum of the amountof 137Cs for individual particles on the same substrate estimated from the IP signals. The discrepancy between
the two measurements was 13%, which indicates the accuracy of the estimation of the amount of 137Cs using IP.

References

1. Sawhney, B. L. Selective sorption and fixation of cations by clay-minerals - review. Clays Clay Miner. 20, 93-& (1972).
2. Francis, C. W. & Brinkley, F. S. Preferential adsorption of cs-137 to micaceous minerals in contaminated freshwater sediment. Nature
260, 511–513 (1976).
3. Rieder, M. et al. Nomenclature of the micas. Can. Mineral. 36, 905–912 (1998).
4. Brouwer, E., Baeyens, B., Maes, A. & Cremers, A. Cesium and rubidium ion equilibria in illite clay. J. Phys. Chem. 87, 1213–1219(1983).
5. Comans, R. N. J., Haller, M. & Depreter, P. Sorption of cesium on illite - nonequilibrium behavior and reversibility. Geochim.
Cosmochim. Acta 55, 433–440 (1991).
6. Poinssot, C., Baeyens, B. & Bradbury, M. H. Experimental and modelling studies of caesium sorption on illite. Geochim. Cosmochim.
Acta 63, 3217–3227 (1999).
7. de Koning, A. & Comans, R. N. J. Reversibility of radiocaesium sorption on illite. Geochim. Cosmochim. Acta 68, 2815–2823 (2004).
8. Fuller, A. J. et al. Caesium incorporation and retention in illite interlayers. Appl. Clay Sci. 108, 128–134 (2015).
9. Brouwer, E., Baeyens, B., Maes, A. & Cremers, A. Cesium and rubidium ion equilibria in illite clay. J. Phys. Chem. 87, 1213–1219(1983).
10. Evans, D. W., Alberts, J. J. & Clark, R. A. Reversible ion-exchange fixation of cesium-137 leading to mobilization from reservoir
sediments. Geochim. Cosmochim. Acta 47, 1041–1049 (1983).
11. Cremers, A., Elsen, A., Depreter, P. & Maes, A. Quantitative-analysis of radiocesium retention in soils. Nature 335, 247–249 (1988).
12. Bradbury, M. H. & Baeyens, B. A generalised sorption model for the concentration dependent uptake of caesium by argillaceous
rocks. J Contam. Hydrol. 42, 141–163 (2000).
13. Fuller, A. J. et al. Ionic strength and pH dependent multi-site sorption of Cs onto a micaceous aquifer sediment. Appl. Geochem. 40,
32–42 (2014).
14. Jackson, M. L. Weathering of primary and secondary minerals in soils. Trans. Int. Soil. Sci. 4, 281–292 (1968).
15. Elprince, A. M., Rich, C. I. & Martens, D. C. Effect of temperature and hydroxy aluminum interlayers on adsorption of trace
radioactive cesium by sediments near water-cooled nuclear-reactors. Water Resour. Res. 13, 375–380 (1977).
16. Nakao, A., Funakawa, S. & Kosaki, T. Hydroxy-Al polymers block the frayed edge sites of illitic minerals in acid soils: studies insouthwestern Japan at various weathering stages. Eur. J. Soil Sci. 60, 127–138 (2009).
17. Goto, M. et al. Interactions of radioactive and stable cesium with hydroxy-interlayered vermiculite grains in soils of the Savannahriver site, South Carolina, USA. Clays Clay Miner. 62, 161–173 (2014).
18. Zaunbrecher, L. K., Cygan, R. T. & Elliott, W. C. Molecular Models of Cesium and Rubidium Adsorption on Weathered Micaceous
Minerals. J. Phys. Chem. A 119, 5691–5700 (2015).

Scientific Reports | 6:21543 | DOI: 10.1038/srep21543

6

www.nature.com/scientificreports/
19. Mukai, H. et al. Speciation of Radioactive Soil Particles in the Fukushima Contaminated Area by IP Autoradiography andMicroanalyses. Environ. Sci. Technol. 48, 13053–13059 (2014).
20. Komarneni, S. & Roy, R. A Cesium-selective ion sieve made by topotactic leaching of phlogopite mica. Science 239, 1286–1288(1988).
21. National Institute of Material Science (NIMS). Database of Promising Adsorbents for Decontamination of Radioactive Substances
after Fukushima Daiichi Nuclear Power Plants Accident. Available at: http://reads.nims.go.jp/index_en.html (Accessed December
28, 2015).
22. Ohnuki, T. & Kozai, N. Adsorption behavior of radioactive cesium by non-mica minerals. J. Nucl. Sci. Technol. 50, 369–375 (2013).
23. Japan Meteorological Agency. Archives of the past meteorological data (in Japanese). Available at: http://www.data.jma.go.jp/obd/stats/etrn/index.php (Accessed December 28, 2015).
24. Japan Atomic Energy Agency (JAEA). Extension site of distribution map of radiation dose, etc. Available at: http://ramap.jmc.or.jp/
map/eng/(Accessed December 28, 2015).
25. Satoko, M. et al. Mineralogical characterization of radioactive particles in Fukushima soil using m-XRD with synchrotron radiation.
J. Miner. Petrol. Sci., in review.
26. Fujii, E. et al. Cesium sorption to paddy soil in Fukushima. Clay Sci. 19, 17–22 (2015).
27. Tessier, A., Campbell, P. G. C. & Bisson, M. Sequential extraction procedure for the speciation of particulate trace-metals. Anal.
Chem. 51, 844–851 (1979).
28. Morimoto, K. et al. Desorption of Cs+ Ions Intercalated in Vermiculite Clay through Cation Exchange with Mg2+ Ions. Chem. Lett.
41, 1715–1717 (2012).
29. Kato, N. et al. Potassium fertilizer and other materials as countermeasures to reduce radiocesium levels in rice: Results of urgent
experiments in 2011 responding to the Fukushima Daiichi Nuclear Power Plant accident. Soil Sci. Plant Nutr. 61, 179–190 (2015).
30. Kamei, A., Takagi, T. & Kubo, K. Geology and petrography of the Abukuma granites in the Hiyama district, Fukushima Prefecture,
NE Japan. Bull. Geol. Surv. Jpn 54, 395–409 (2003). (in Japanese with English abstract)
31. Miyawaki, R. et al. Some reference Data for the JCSS clay specimens. Nendo Kagaku (Journal of the Clay Science Society of Japan) 48,
158–198 (2010). (in Japanese with English abstract)
32. Manceau, A. et al. Oxidation-reduction mechanism of iron in dioctahedral smectites: I. Crystal chemistry of oxidized reference
nontronites. Am. Mineral. 85, 133–152 (2000).
33. Kogure, T., Mori, K., Kimura, Y. & Takai, Y. Unraveling the stacking structure in tubular halloysite using a new TEM with computerassisted minimal-dose system. Am. Mineral. 96, 1776–1780 (2011).
34. Henmi, T. Effect of SiO2-Al2O3 ratio on the thermal-reactions of allophane. Clays Clay Miner. 28, 92–96 (1980).
35. Yoshinaga, M. & Yamaguchi, N. Occurrence of imogolite as gel film in the pumice and scoria beds of western and central Honshu
and Hokkaido. Soil Sci. Plant nutr. 16, 215–223 (1970).

Acknowledgements

We are grateful to M. Pentrak and J.W. Stucki for donating the SWa-1 specimen, to N. Matsue for donating theallophane specimen, and to S. Wada for donating the imogolite specimen. Part of this work was supported by aGrant-in-Aid for science research (15H04222, 15H02149 and 24340133) by Japan Society for the Promotion of
Science (JSPS), Japan. This work was also supported by a contracted study with JAEA for Fukushima environment
recovery, entitled “Study on Cs adsorption and desorption process on clay minerals”.

Author Contributions

T.K. designed the research, supervised the experiments and wrote the manuscript; H.M. performed most of
the adsorption/desorption experiments and compiled the results. A.H. prepared the radiocesium solution andassisted H.M. in performing his experiments. S.M. mainly worked on making the calibration curve between
the IP signal and radioactivity. R.K. collected the WB specimens in Fukushima. K.T., T.N. and T.Y. gave T.K. a
number of important ideas and suggestions for the research.

Additional Information

Supplementary information accompanies this paper at http://www.nature.com/srep
Competing financial interests: The authors declare no competing financial interests.
How to cite this article: Mukai, H. et al. Cesium adsorption/desorption behavior of clay minerals considering
actual contamination conditions in Fukushima. Sci. Rep. 6, 21543; doi: 10.1038/srep21543 (2016).
This work is licensed under a Creative Commons Attribution 4.0 International License. The images
or other third party material in this article are included in the article’s Creative Commons license,
unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license,
users will need to obtain permission from the license holder to reproduce the material. To view a copy of thislicense, visit http://creativecommons.org/licenses/by/4.0/