Product Data Sheet
Q11N series
Tenax™ ThermoSet Prepreg 11N series is a 130 °C curing epoxy system with good performance
characteristics especially for automotive and sport applications. This prepreg system can be used withinvarious molding techniques due to its robust behavior and flexibility.

Brand name

Tenax™

Product name

ThermoSet Prepreg 11N series

Production site

Japan, Vietnam

Resin typeEpoxy

Resin name11N

Product benefits

Process benefits•General Use•

Flexible system for various processes(Application: Sports, Leisure, Industry)•Cost effective•

Low void content•

Suitable for inner pressure molding•

Good tack and drape••

No post cure necessary

Typical prepreg shelf life

Chemical properties
Glass Transition Temperature

TEIJIN LIMITEDTEIJIN CARBON EUROPE GMBHTEIJIN CARBON AMERICA, INC.

•

Test method
ASTM D 7028, E2160(Three-point bending, E’)customer@teijin.co.jp
sales@teijincarbon.com
info@teijincarbon.us

Unit

Typical values°C127

www.teijincarbon.com

Version 1.0
2023-09-15
Page 1/5

Product Data Sheet
Q11N series
Mechanical Properties
Style UD
Product designation

Q-111N0-150350

Fiber type
Fiber areal weight
Resin contentTensile (0°)
ASTM D3039

Tensile (90°)
ASTM D3039

In-plane Shear
ASTM D3518

Compression (0°)
ASTM D6641

Flexural (0°)
ASTM D790

STS40
150 g/m²
35 %Q-U11N0-100360
UTS50
100 g/m²
36%

Q-D11N0-075350
IMS65
75 g/m²
35%

strength

[MPa]

2290

2670

2930

modulus[GPa]

130131

154

Poisson´s ratio

-0.31

0.32

0.33

FVC (normalised)[%]

555555strength

[MPa]

8480

72

modulus

[GPa]

8.7

8.2

8.0

Poisson´s ratio

-0.02

0.02

0.01

FVC (normalised)[%]555454strength[MPa]130134144

modulus

[GPa]

3.7

3.7

3.6

Poisson´s ratio

-0.80

0.81

0.84

FVC (normalised)[%]545354strength[MPa]949943931

modulus

[GPa]

115

117

136

Poisson´s ratio

-

0.32

0.33

0.33

FVC (normalised)[%]

555555strength

[MPa]

1620

1530

1470

modulus

[GPa]

120

115

138

FVC (normalised)[%]555454

TEIJIN LIMITEDTEIJIN CARBON EUROPE GMBHTEIJIN CARBON AMERICA, INC.

customer@teijin.co.jp
sales@teijincarbon.com
info@teijincarbon.us

www.teijincarbon.com

Version 1.0
2023-09-15
Page 2/5

Product Data Sheet
Q11N series

Product designation

Q-J11N0-100350

Fiber type
Fiber areal weight
Resin content

Tensile (0°)
ASTM D3039

Tensile (90°)
ASTM D3039

In-plane Shear
ASTM D3518

Compression (0°)
ASTM D6641

Flexural (0°)
ASTM D790

UMS40
100 g/m²
35 %Q-R11N0-092350
UMS45
92 g/m²
35%

Q-T11N0-075350
UMS55
75 g/m²
35%

strength

[MPa]

2370

2320

2050

modulus

[GPa]

207

241

307

Poisson´s ratio

-0.29

0.29

0.31

FVC (normalised)[%]

555555strength[MPa]766548modulus

[GPa]

7.5

7.1

6.2

Poisson´s ratio

-

0.01

0.01

<0.01

FVC (normalised)[%]

545552

strength[MPa]128121

104

modulus

[GPa]

3.8

3.9

3.7

Poisson´s ratio

-

0.86

0.88

0.91

FVC (normalised)[%]

535551

strength

[MPa]

988

803

708

modulus

[GPa]

176

204261

Poisson´s ratio

-

0.30

0.28

0.29

FVC (normalised)[%]

555555strength

[MPa]

1350

1270

940

modulus

[GPa]

183

210231

FVC (normalised)

[%]

5555

52

TEIJIN LIMITEDTEIJIN CARBON EUROPE GMBHTEIJIN CARBON AMERICA, INC.

customer@teijin.co.jp
sales@teijincarbon.com
info@teijincarbon.us

www.teijincarbon.com

Version 1.0
2023-09-15
Page 3/5

Product Data Sheet
Q11N series
Bagging procedure

1. Debulk when laying up material
2. It is recommended that material have a pre-cure vacuum hold depending on size
3. Before starting cure cycle, the vacuum should be checked for leaks
Recommended Prepreg curing conditions (Autoclave cure)
These conditions are recommended for reference purpose only.

1. Apply minimum vacuum (80 kPa)
2. Apply typically 0.5 MPa of pressure to the laminate
3. Set heat up to 130 ℃ with heat-up rate 2 ℃/minute
4. Hold at 130 ℃ for 120 minutes
5. Cool component to 60 ℃ or below at a cool-down rate of 2-5 ℃/minutes

TEIJIN LIMITEDTEIJIN CARBON EUROPE GMBHTEIJIN CARBON AMERICA, INC.

customer@teijin.co.jp
sales@teijincarbon.com
info@teijincarbon.us

www.teijincarbon.com

Version 1.0
2023-09-15
Page 4/5

Product Data Sheet
Q11N series
Dynamic viscosity at 2 °C /minute

Storage condition and shelf life•••Storage at -18 °C: 12 months from date of manufacture
Storage at 23 °C: 30 days from date of manufacture

It is recommended that Tenax™ Thermoset Prepregs be stored in a dry cool area. User should
allow the prepreg to reach room temperature before opening the sealed bag. The thawing timestrongly depends on the amount of material on a single roll. Please contact us for moreinformation.

General Information••••

All data are typical values representative of the material and cannot be guaranteed. Properties may varydepending on samples preparation and test methods.
For each shipment an inspection certificate is generated and supplied.
A detailed customer specification is arranged on request.
The export or transfer of carbon fiber products can be subject to authorization, depending on end-use
and final destination.

TEIJIN LIMITEDTEIJIN CARBON EUROPE GMBHTEIJIN CARBON AMERICA, INC.

customer@teijin.co.jp
sales@teijincarbon.com
info@teijincarbon.us

www.teijincarbon.com

Version 1.0
2023-09-15