Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

A resin coating technique to achieve minimal intervention in indirect
resin composites: A clinical report
Toru Nikaido, DDS, PhD,a Akira Yoda, DDS,a Richard M. Foxton, BDS, PhD,b andJunji Tagami, DDS, PhDa
aCariology and Operative Dentistry, Department of Restorative Sciences,Graduate School, Tokyo Medical and Dental University, Tokyo, Japan, andb
Division of Conservative Dentistry, GKT Dental Institute, London, UnitedKingdom.
Minimally invasive restorative techniques can be applied with direct resin composites. However, thepreparation for an indirect restoration tends to lead to over-treatment of the tooth structures.

Aresin-coating technique has been proposed in which both a hybrid layer and a tight sealing film areproduced on the dentin surface with a dentin adhesive system and a low viscosity micro-filled resin. It
covers and protects the prepared dentin immediately after cavity preparation, and minimizes pulp irritationand post-operative sensitivity. In addition, the resin coating technique enables good bonding of the resin
cement and adaptation of composite inlays. The following case report describes treatment involving theresin coating technique in order to achieve minimal intervention for an indirect resin composite restoration.
(Int Chin J Dent 2003; 3: 62-68.)
Key Words: indirect resin composite, minimal intervention, resin coating.

Introduction
Metal-free restorations in tandem with the development of good adhesive materials have become widelyaccepted.1 However, the preparation for metal-free restorations tends to lead to over treatment of the toothstructures because of the necessity for enough space for the restorations.2 Nowadays, minimally invasive
restorative techniques can be performed using direct resin composite restorations even in posterior teeth.3,4However, this is not the case with indirect restorations.
A resin-coating technique has been proposed in which both a hybrid layer and a tight sealing film areproduced on the dentin surface with a dentin bonding system (DBS) and a low viscosity micro-filled resin(LVR).5,6 It covers and protects the prepared dentin immediately after cavity preparation, and minimizes
pulp irritation and post-operative sensitivity.7
bonding of the resin cement8-10

In addition, the resin coating technique enables good

and adaptation of composite inlays.11 If the proper combination of a DBS

and a LVR is selected, the bonding performance of resin cements is almost identical to that for a direct
resin composite restoration.12 Therefore, the resin coating technique enables us to achieve minimally62

Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

invasive indirect restorations. The following case report describes treatment involving the resin coating
technique in order to achieve minimal intervention for an indirect resin composite restoration.

Clinical Report
A 40-year-old patient with failure of a metal onlay in the right upper second molar presented forrestoration of the cavity. There was secondary caries in the second molar, and primary caries in the distal
aspect of the first molar, which had an occlusal resin composite (Fig. 1).

12Fig. 1. Preoperative condition of right upper molars. Second molar demonstrates failure of ametal onlay with secondary caries. There was primary caries in the distal aspect of the first molar,
which had an occlusal resin composite.
Fig. 2. The caries infected dentin was carefully removed with a steel round bur in a low-speed
micromoter handpiece leaving the caries affected dentin and intact dentin.
The enamel of the proximal ridges of the first and second molars was cut with a round diamond bur in an
air-turbine handpiece with water spray to approach the carious dentin lesions. The caries infected dentin
was carefully removed with a steel round bur in a low-speed micromoter handpiece leaving the caries
affected dentin and intact dentin. No local anesthesia was given and the patient did not complain of pain
while the infected caries was being removed. Neither retention nor resistance form were provided after
removal of the caries. Following this, the cavities were isolated with a rubber dam for the subsequentbonding procedures (Fig. 2).
The cavity in the first molar was restored with a direct resin composite because the small cavity waseasily accessible. However, the cavity in the second molar was too large to be restored with a direct resin
composite and also difficult to be finished and polished in the restricted space. Therefore, it was decided torestore the cavity with an indirect resin composite using the resin coating technique. A steel sectional
matrix (KerrHawe, Bioggio, Switzerland) was inserted in the interproximal space and wedged. The firstmolar was restored using a direct resin composite, Clearfil AP-X (Kuraray Medical, Tokyo, Japan) in
combination with a self-etching primer bonding system, Clearfil SE Bond (Kuraray Medical), according to
the manufacturer’s instructions (Fig. 3). Following this, Clearfil SE Bond was applied to the cavity of thesecond molar and then a low viscosity micro-filled resin, Protect Liner F (Kuraray Medical), was63Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

additionally applied to the adhesive surface and light-cured for 30 s to seal the cavity margins. The surface
was then wiped with a cotton pellet soaked in ethanol to remove the surface air-inhibited unpolymerizedlayer (Fig. 3).

34Fig. 3. The cavity in the first molar was restored with a direct resin composite. Following this, theresin coating with Clearfil SE Bond and Protect Liner F was applied to the cavity of the secondmolar.
Fig. 4. An impression was made for the preparation of the second molar with a reversiblehydrocolloid-an alginate combination.
After finishing and polishing the composite restoration in the first molar, an impression was made for thepreparation of the second molar. A reversible (Aromaloid, GC, Tokyo, Japan) and irreversible (AromaFine DF III, GC, Tokyo, Japan) hydrocolloid combination was used as the impression material for theresin-coating (Fig. 4). Following this, a water-setting temporary filling material (Cavit-G, 3M-ESPE,Seefeld, Germany) was placed in the cavity (Fig. 5).

56Fig. 5. A water-setting temporary filling material, Cavit-G, was placed in the cavity.
Fig. 6. A resin composite onlay was fabricated in the laboratory.
A resin composite onlay was fabricated in the laboratory using a highly filled indirect composite (Estenia,Kuraray Medical) according to the manufacturer’s instructions (Fig. 6).

The cavity surface of therestoration was air-abraded with 50 µm alumina for 5 s to peel the cross-linked resin matrix covering the64

Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

surface.
At the second visit, the temporary filling material was ultrasonically removed from the cavity. However,there was no pain because the resin coating protected the pulp. After the preparation was isolated using arubber dam, the resin-coating surface was cleaned with a cotton pellet soaked in ethanol. After trial seatingof the composite onlay in the cavity, the cavity surface of the onlay and the resin-coated cavity wereprepared for bonding. Thirty-seven % phosphoric acid (K-etchant, Kuraray Medical) was applied to thecavity surface of the composite onlay for 5 s, rinsed and dried. Following this, a mixture of SE Primer inClearfil SE Bond and Porcelain Bond Activator (Kuraray Medical) was applied to the surface for 5 s, thengently air-blown for silanization of the surface (Fig. 7). For bonding of the resin-coated surface, 37 %phosphoric acid was also applied for 5 s, rinsed and air-dried. ED Primer II (Kuraray Medical, Tokyo,Japan) was then applied to the surface for 5 s and gently air-blown (Fig. 8).

78Fig. 7. Phosphoric acid was applied to the cavity surface of the composite onlay for 5 s, rinsedand dried. A mixture of SE Primer in Clearfil SE Bond and Porcelain Bond Activator was applied tothe surface for 5 s, then gently air-blown for silanization of the surface.
Fig. 8. Phosphoric acid was applied for 5 s, rinsed and air-dried. ED Primer II was then applied tothe surface for 5 s and gently air-blown.

Fig. 9. Postoperative view of the second molar
restored with an indirect resin composite using
the resin-coating technique.
For cementation, the two pastes of a dual-cured resin cement (Panavia F, Kuraray Medical) was mixedand placed in the cavity. After seating of the composite onlay in the cavity, excess cement was removed
with an explorer and floss. The cement was then light-cured from the occlusal, buccal and lingual sides for65

Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

30 s each. Following this, the interocculsal contacts of the restoration were adjusted, and the restoration
was finished and polished again (Fig. 9). The patient was recalled one week after cementation to check for
any remaining cement at the cervical and interproximal area.

At this point, there were no clinicalsymptoms including postoperative sensitivity of the restoration.

DiscussionDirect composite restorations are the preferred treatment over indirect resin composites even for
posterior restorations because they require minimal intervention and cavity preparation.2,4 Indirect resin
composites are usually recommended when teeth require large restorations with a limited approach. If an
indirect resin composite is selected, a resin coating consisting of a DBS and a LVR should be applied to thedentin surface to improve the bonding8-10 and to protect the prepared dentin and pulp.7 The combination ofPanavia F with Clearfil SE Bond and Protect Liner F was one of the optimal combinations for resin
coating.9,12 It provided the highest bond strength to dentin, which was almost identical to that for a direct
resin composite restoration.12 Therefore, the resin coating technique enables us to achieve minimallyinvasive indirect restorations, because of the improvement in bonding of the resin cement.
Adhesion of direct resin composite to dentin occurs as a result of hybrid layer formation,13 which is also
true for indirect resin composite using a resin coating.5,12 The thickness of the hybrid layer with resin
coating depends on the adhesive systems used in combination with the resin cements. The thickness of thehybrid layer with the combination of Clearfil SE Bond and Protect Liner F was approximately 0.5 to 1.0µm.12
A single application of a DBS to the prepared cavity before taking an impression has been shown toprotect the exposed dentin and prevent post-operative sensitivity.14-16 However, a previous study has also
shown that an additional application of a LVR on the cured adhesive significantly improved the sealing ofthe dentinal margins.17 A significantly higher resin cement/dentin bond strength was obtained when theteeth were resin coated with a DBS and a LVR compared to the teeth that were bonded with a dentin
bonding system only.9 By coating the DBS with a LVR, the oxygen inhibition layer containing uncured
resin of the DBS can be reduced.17 Moreover, any uncured resin of the oxygen inhibition layer may
subsequently polymerize by the diffusion of free radicals from the LVR.9 In addition, at the time ofremoval of the temporary cement, a LVR may prevent the DBS from being torn away. Furthermore, as theelastic modulus of the LVR is centered between the bonding resin and resin cement, it can function as astress breaker.9,17
Selection of the materials for impression making and temporization after application of the resin coating
is important for successful cementation of the final restoration.

A reversible hydrocolloid-alginate

combination impression is more suitable than silicone rubber impression materials. When a reversiblehydrocolloid impression material is used, bonding of the resin cement to resin coated dentin is not
influenced by the impression material. However, an addition type silicone rubber impression material
reduces the bonding of Panavia F. The reduction in bonding performance was found to be more remarkable66

Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

when the resin-coated surface was not wiped with a cotton pellet soaked in ethanol to remove theair-inhibited layer.18 It was considered that oxygen in the inhibition layer or the residual monomer may
interfere with the setting of the silicone rubber impression material, resulting in contamination of theresin-coated surface. Therefore, when a silicone rubber impression material is used, the resin-coatedsurface should be wiped with an ethanol cotton pellet to remove the air-inhibited layer. Better surface
characteristics of resin-coating materials were obtained with a condensation type of silicone rubber
impression than an addition type.19
The effect of temporary filling materials on bond strength to resin-coated surface was evaluated after
removal of the temporary filling materials.20 The highest bonding was obtained when Cavit G was used as
the temporary filling. The air-inhibited layer, which is considered to be effective for bonding with the resin
cement, might be protected by this material. A resin-based temporary filling material should not be used,since it may react with the resin coating material. Resin-based temporary filling materials attached to theresin-coated surface are extremely difficult to remove, and any remaining material may affect bonding.
Eugenol-based and non-eugenol materials did not show any reduction in bonding, however, the use of
eugenol based materials is not recommended since the polymerization inhibition effect of these materials isstill unclear.
Currently, a resin coating is being applied in all indirect resin composite restorations in clinic.
Long-term clinical evaluation of this new technique should be carried out.

References
1. Markus BB. Long-term clinical success of all-ceramic posterior restorations. Quintessence Int 2002; 33: 415-26.
2. Heyman HO, Swift EJ Jr. Perspectives - Is tooth structure not sacred anymore? J Esthet Restor Dent 2001; 13: 283.
3. Mount GJ, Ngo H. Minimal intervention: a new concept for operative dentistry. Quintessence Int 2000; 31: 527-33.
4. Peters MC, McLean ME. Minimally invasive operative care. I. Minimal intervention and concepts for minimally invasive
cavity preparations. J Adhes Dent 2001; 3: 7-16.
5. Nikaido T, Takada T, Burrow MF, Tagami J. The early bond strength of dual cured resin cement to enamel and dentin. JJpn Dent Mater 1992; 11: 910-5.
6. Otsuki M, Yamada T, Inokoshi S. Establishment of a composite resin inlay technique. Part 7. Use of low viscous resin. J
Jpn Conserv Dent 1993; 36: 1324-30.
7. Satoh M, Inai N, Nikaido T, et al. How to use Liner Bond System as a dentin and pulp protector in indirect restorations.
Adhes Dent 1994; 12: 41-7.
8. De Goes MF, Nikaido T, Pereira PNR, Tagami J. Early bond strengths of dual-cured resin cement to resin-coateddentin. J Dent Res 2000; 79(Special Issue): 453.
9. Jayasooriya PR, Pereira PNR, Nikaido T, Tagami J. Effect of resin coating on bond strengths of resin cement to dentin.
J Esthet Restor Dent 2003; 15: 38-45.
10. Kitasako Y, Burrow MF, Nikaido T, Tagami J. Effect of resin coating technique on dentin bond strengths over 3 years. JEsthet Restor Dent 2002; 14: 115-22.
11. Jayasooriya PR, Pereira PNR, Nikaido T, Tagami J. Effect of a “Resin-coating” on the interfacial adaptation ofcomposite inlays. Oper Dent 2003; 28: 28-35.
12. Nikaido T, Cho E, Nakajima M, et al. Tensile bond strengths of resin cements to bovine dentin using resin coating. Am J
Dent (in press).

67

Nikaido et al.

Int Chin J Dent 2003; 3: 62-68.

13. Nakabayashi N, Kojima K, Masuhara E. The promotion of adhesion by infiltration of monomers into tooth substrates. JBiomed Mater Res 1982; 16: 265-73.
14. Christensen GJ. Resin cements and post-operative sensitivity. J Am Dent Assoc 2000; 131: 1197-9.
15. Dagostin A, Ferrari M. Effect of resins sealing of dentin on the bond strength of ceramic restorations. Dent Mater 2002;
18: 304-10.
16. Paul SJ, Scharer P. The dual bonding technique: A modified method to improve adhesive luting procedures. Int JPeriodont Rest Dent 1997; 17: 537-45.
17. Belli S, Inokoshi S, Ozer F, Pereira PNR. Ogata M. Tagami J. The effect of additional enamel etching and a flowablecomposite to the interfacial integrity of class II adhesive composite restorations. Oper Dent 2001; 26: 70-5.
18. Nakano M, Takada T, Nikaido T, Tagami J. Effect of impression material on adhesion of resin cement to resin coatedteeth. Adhes Dent 1999; 17: 198-204.
19. Takano Y, Nikaido T, Tagami J. Visual and SEM observation of resin coated dentine after taking impression. J Jpn
Adhes Dent 2001; 19: 117-24.
20. Nikaido T, Koh Y, Satoh M, et al. Effect of temporary filling materials on adhesion of dual cured resin cement to lowviscosity resin, J Jpn Dent Mater 1993; 12: 655-61.

Reprint request to:
Dr. Toru Nikaido
Cariology and Operative Dentistry, Department of Restorative Sciences
Graduate School, Tokyo Medical and Dental University
1-5-45, Yushima, Bunkyo-ku, Tokyo, 113-8549, Japan
FAX: +81-3-5803-0195 E-mail: nikaido.ope@tmd.ac.jp
Received on June 17, 2003. Revised on August 3, 2003. Accepted on August 9, 2003.
Copyright ©2003 by the Editorial Council of the International Chinese Journal of Dentistry.

International Chinese Journal of Dentistry 2003 Outstanding Article AwardInternational Chinese Journal of Dentistry announces the second Outstanding Article Award.
Award:A cash prize of US$ 600 and a certificate of commendation are awarded for the most outstanding article published in
the International Chinese Journal of Dentistry.
Criteria:
Original articles, clinical reports, and dental technology articles published in the Journal between issue 1 and issue 4
are considered for the award. The winning article will be selected by a committee on the basis of scientific impact on
the dental professional communities, and interest to the readers. The 2003 Award is sponsored by the International
Chinese Journal of Dentistry and the following award sponsors.
Award Sponsors:
Kuraray Medical Inc., Tokyo, Japan, http://www.kuraray.co.jp/dental
Sun Medical Co., Ltd., Moriyama, Japan, http://www.sunmedical.co.jp
Toho Dental Products, Saitama, JapanTokuyama Dental Corp., Tokyo, Japan, http://www.tokuyama-dental.co.jp
3M Health Care Limited, Sagamihara, Japan, http://www.3m.com/espe/
2002 Award Winner:
Miyazaki M, Onose H, Hirohata N, Nishizawa O, Moore BK.
Influence of cutting of enamel surface with Er: YAG laser on bond strength. Int Chin J Dent 2002; 2(2): 75-85.

68