Technical Data Sheet
HS PETG Filament
HS PETG is an FFF 3D printing ﬁlament, which is produced using a modiﬁed PETG. Itoﬀers excellent dimensional stability, bending strength, and rigidity, along withoutstanding melt ﬂuidity and rapid solidiﬁcation. It is highly suitable for use inhigh-speed FFF 3D printers.

Features:
High ﬂuidity/Easy to print/Dimensional stability/High rigidity

Properties:
Physical Properties

Test Method

Units

Typical Value

Density

ISO 1183g/cm³

1.27~1.28

Melt Flow Rate (MFR) (220℃/2.16Kg)

ISO 1133

g/10min8~12

Water Absorption (23℃/24h)

ISO 62%＜0.2Tensile Strength (X-Y)

ISO 527

Mpa

41~45

Elongation at Break (X-Y)

ISO 527%

10~12

Modulus of Elasticity (X-Y)

ISO 527

Mpa

1400~1500

Bending Strength (X-Y)

ISO 178

Mpa

64~66

Izod Impact Strength (X-Y)

ISO 180

KJ/㎡

5~6

HDT@ 0.455 MPa（66 psi）

ISO 75℃

68

Continuous Service Temperature

IEC 60216℃

65

Mechanical Properties

Thermal Properties

www.ﬂashforge.com

Testing Specimen Printing Conditions:
Test Equipment

Adventurer 5M (Flashforge)

Nozzle Diameter

0.4mm

Printing Parameter

0.02mm Standard @Flashforge AD5M 0.4 Nozzle

Inﬁll

100%Inﬁll Direction

45°

Standard Testing Specimen

Speciﬁc dimensions are shown in Attachment 1

Recommended Printing Conditions:Parameter
Nozzle Temperature

220~260℃

Build Platform Temperature

Room temperature~60℃

Build Surface Material

Tempered glass, PEI, Carbon ﬁber plate

Nozzle Diameter

φ0.4/0.6mm (φ0.4mm recommended)

Cooling Fan

50~100%Layer Thickness

0.12~0.3mm

Printing Speed

100~350mm/s

Travel Speed

150~600mm/s

Ambient Temperature for Printing

Room temperature~40℃

Retraction Distance1~2mm

Retraction Speed

30~50mm/s

Support Material

Self-supporting, PVA, BVOH

www.ﬂashforge.com

Cautions:
In order to prevent moisture absorption and contamination, supplied packaging should
be kept closed and undamaged. For the same reason, partially used ﬁlaments should bere-sealed before storage.
Exposure to moisture, oxygen in the air, and UV light will accelerate its aging. In order
not to aﬀect the ﬁnal printing quality, the HS PETG ﬁlament after its package being
opened should be used up as soon as possible.

Disclaimer:
Since the conditions of use and applicable laws may vary from place to place and fromtime to time, customers are responsible for determining whether the products andproduct information in this document are suitable for customers to use, and ensuringthat their workplaces and methods of handling products comply with applicable laws
and other government regulations. This company does not assume any responsibility orobligation for the information in this document, nor does it provide any guarantee. All
implied warranties regarding the saleability of the product or the applicability for aparticular purpose under this document are expressly excluded here.

www.ﬂashforge.com

Attachment 1:
Testing Specimen Size and Printing Direction
150.00114.00
10.00

20.00

80.00

Zaxis

4.00

4*R25

Tensile testing specimen; ASTM D638 (ISO 527, GB/T 1040)

10.00

80.00
60.00

4.00

Zaxis

Flexural testing specimen; ASTM D790 (ISO 178, GB/T 9341)

80.00

Zaxis

10.00

45.00°

4.00

Impact direction

Impact testing specimen; ASTM D256 (ISO 179, GB/T 1043)

www.ﬂashforge.com