Metal reduction processes, metallurgical processes and products and apparatus

The disclosure relates to metal reduction processes, which comprise adding a mixture comprising at least one metal-containing material, at least one reducing agent, and at least one additive into a reactor, heating the reactor to a selected reduction temperature, moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, and obtaining a resulting composition comprising at least one zero-valent metal and a residue. The disclosure also relates to metallurgical processes comprising the metal reduction process, and products made by the metal reduction process. The disclosure further relates to metal reduction apparatuses, as well as metal reduction systems and metallurgical systems comprising the metal reduction apparatuses.

FIELD OF THE INVENTION

This disclosure relates to the field of metal reduction and metallurgy, specifically to metal reduction processes, metallurgical processes, and to related products and to apparatus for use therewith.

BACKGROUND OF THE INVENTION

Metals are indispensable material for human beings. They normally do not exist as simple substances, i.e., zero-valent metals, in nature; most are found, for example, in ores as compounds and mixtures. To obtain metals in simple substance form, ores need to be smelted to extract the metals.

Many methods to extract metals exist, one of which is to reduce ores at an appropriate temperature using a reducing agent. Taking iron extraction as an example, the traditional method includes the blast furnace method. Other commonly used metallurgical methods for iron reduction include, for example, direct reduction and melt reduction. Direct iron reduction falls primarily into two categories: (1) gas-based direct reduction, including, for example, the Midrex shaft kiln method and the HYL reaction tank method; and (2) coal-based direct reduction, including, for example, the Fastmet method using a ring back converter, the CRIMM method using a rotary kiln, the Fastmelt method, and the ITmk3 method. Most of those methods usually require a high concentration of iron, such as over 60% of iron, in the ores. Another coal-based direct reduction method uses tunnel kilns and the reactant materials are in a powder form before entering into the tunnel kiln. Melt reduction methods include, for example the Corex method, the Hismelt method, the Finex Method, and others such as the DIOS, AISI, and CCF methods. Another commonly-used method is the Hoganas method.

These above-mentioned methods, in general, may require high energy consumption, create serious air pollution, or require significant investments for equipment. In addition, these methods may have stringent demand for high-quality feed material, such as requiring high metal-content ores, or requires stringent control during the processing to avoid poor-quality products. Hence, there is still a great need for a new metal reduction process to solve at least one of the problems set forth above.

SUMMARY OF THE INVENTION

The present disclosure relates to a metal reduction process, comprising:adding a mixture into a reactor, wherein the mixture comprises at least one metal-containing material, at least one reducing agent, and at least one additive,heating the reactor to a selected reduction temperature,moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, andobtaining a resulting composition, wherein the resulting composition comprises at least one zero-valent metal and a residue. The resulting composition may, for example, be in the form of solid particles comprising at least one zero-valent metal core and a coating.

The present disclosure further relates to a metallurgical process, comprisinga mixing stage, comprising mixing at least one metal-containing material, at least one reducing agent, and at least one additive to form a mixture;a metal reduction stage, comprising adding the mixture into a reactor, heating the reactor to a selected reduction temperature, moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, and obtaining a resulting composition, wherein the resulting composition comprises at least one zero-valent metal and a residue; anda separation stage, wherein the at least one zero-valent metal is separated from the residue.

The present disclosure also relates to a product, made by the metal reduction process set forth above, wherein the resulting composition is in the form of solid particles comprising at least one zero-valent metal core and a coating. The resulting composition may, for example, be in the form of solid particles comprising at least one zero-valent metal core and a coating.

The present disclosure further relates to a metal reduction apparatus for recovering at least one metal from at least one metal-containing material, comprising:a reactor housing configured to receive a mixture of at least one metal-containing material, at least one reducing agent, and at least one additive;a heating device including at least one heating unit thermally coupled to the reactor housing; anda propelling blender located in the reactor housing, wherein:the propelling blender includes a plurality of shafts;each of the plurality of shafts has at least one blade; andthe thickness of an outer surface of the at least one blade varies along the arc of the at least one blade.

The present disclosure also relates to a metal reduction system, comprising:a metal reduction apparatus includinga reactor housing configured to receive a mixture of at least one metal-containing material, at least one reducing agent, and at least one additive;a heating device including at least one heating unit thermally coupled to the reactor housing, and at least one temperature controlling unit controllably coupled to the at least one heating unit; anda propelling blender located in the reactor housing; andat least one heat recovery device coupled to the metal reduction apparatus, and configured to receive a resulting composition discharged from the metal reduction apparatus.

The present disclosure further relates to a metallurgical system for recovering at least one metal from at least one metal-containing material, comprising:a material preparation system configured to prepare a mixture of the at least one metal-containing material, at least one reducing agent, and at least one additive;a metal reduction apparatus located downstream of the material preparation system, and configured to reduce the at least one metal-containing material to a resulting composition comprising at least one zero-valent metal and a residue, the metal reduction apparatus including:a heating device, anda propelling blender; anda separator located downstream of the metal reduction apparatus, and configured to separate the at least one zero-valent metal from the residue.

DETAILED DESCRIPTION OF THE INVENTION

The present disclosure relates to a metal reduction process, comprising:adding a mixture into a reactor, wherein the mixture comprises at least one metal-containing material, at least one reducing agent, and at least one additive,heating the reactor to a selected reduction temperature,moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, andobtaining a resulting composition, wherein the resulting composition comprises at least one zero-valent metal and a residue.

In one embodiment, the mixture is in the form of fine particles. For example, the fine particles can have a particle size of less than about 1 mm. As another example, the fine particles have a particle size of less than about 0.074 mm. The particle size may be measured by a method known in the art, chosen, for example, from laser density methods, settlement and precipitation methods, and electron microscopy methods.

The at least one metal-containing material disclosed herein may be chosen from ores, slag, industrial wastes, and metal oxides. In one embodiment, the at least one metal-containing material is chosen from ores. The ores include, but are not limited to, low grade ores, symbiotic ores, and refractory ores. For example, the at least one metal-containing material can be chosen from low grade ores. The phrase “low grade ores” as used herein refers to ores containing a lower amount of metal than the grade required by prior art technologies. For example, lower grade iron ores contain no higher than 60% by weight of iron, such as 20%-60% by weight of iron, relative to the total weight of the ores. In another embodiment, the at least one metal-containing material is chosen from industrial wastes.

More than one metal-containing material may be used in a single metal reduction process. For example, more than one industrial waste containing iron, albeit from different sources or with different specifications, may be combined and reduced in a single metal reduction process.

In one embodiment, the at least one metal-containing material comprises at least one metal compound. The at least one metal compound may be chosen, for example, from compounds containing at least one positive-valent metal. For example, the at least one metal compound can be chosen from metal oxides, metal carbonates and metal hydroxides. As another example, the at least one metal compound is chosen from metal sulfides, which may be transformed into metal oxides via a method known in the art before being subject to a metal reduction process. When more than one metal-containing compound is used, the at least one metal-containing compound may contain the same metal or different metals. For example, a metal-containing material may contain Fe3O4, Fe2O3, FeO, and/or any combination thereof. As another example, metal compounds containing oxides and/or sulfides of Fe and/or Ni may coexist in one metal-containing material.

The at least one reducing agent may be any reducing agent that could achieve metal reduction, and may be chosen, for example, from materials having a high carbon content. In one embodiment, the at least one reducing agent is chosen from coals, anthracites, cokes, heavy oils, petrol-coke, and pitch. For example, the at least one reducing agent can be chosen from coals, and anthracites, and cokes.

The at least one reducing agent disclosed herein may be present in the mixture in an amount greater than the theoretical molar value. In one embodiment, the at least one reducing agent is present in an amount ranging from about 5% to about 100% greater than the theoretical molar value. The phrase “the theoretical molar value” of the at least one reducing agent as used herein is the calculated amount of the at least one reducing agent, an amount that would be required for the metal reduction reaction to be complete in accordance with the applicable chemical reaction equation, under an ideal chemical reaction condition, based on an estimated amount of the metal(s) contained in the at least one metal-containing material. For example, if a material containing Fe3O4is to be reduced by coal, the following chemical reaction would occur: Fe3O4+2 C=3 Fe+2 CO2. Under ideal chemical reaction conditions, to make the reduction reaction of 1 mole of Fe3O4complete, 2 moles of carbon would be required. That is, the theoretical molar value for reducing 1 mole of Fe3O4is 2 moles of carbon. In practice, the theoretical molar value of a reducing agent is calculated based on the estimated amount of the metal(s) contained in a metal-containing material.

The amount of the at least one additive in the mixture may be determined based on various factors, depending on the purpose of the additive. For example, if sulfur is to be removed during the metal reduction process, the amount of the at least one additive is determined based on factors such as the content of sulfur and the nature of the metal in the metal-containing material. The presence of the at least one additive may also, for example, help maintain an environment inside of the reactor to facilitate the reduction reaction. In one embodiment, the at least one additive is present in the mixture in an amount greater than the theoretical molar value. For example, the at least one additive is present in the mixture in an amount about 5% to about 100% greater than the theoretical molar value. The phrase “the theoretical molar value” of the at least one additive refers to the calculated amount of the at least one additive, which would be required, under ideal chemical reaction conditions, to remove the unwanted matter from the at least one metal-containing material, based on an estimated amount of the unwanted matter. The theoretical molar value of an additive may be calculated in a similar fashion as exemplified above for the at least one reducing agent, based on the nature of the unwanted matter.

The ratio of the at least one additive and the at least one reducing agent may be adjusted based on factors such as the quality of the at least one metal-containing material, the nature of the metal in the metal-containing material, and/or the purpose of the at least one additive. In one embodiment, the weight ratio of the at least one additive and the at least one reducing agent is about 1:1. This weight ratio may also, for example, vary to ensure that the environment inside of the reactor that is desirable for the reduction reaction could be maintained.

The reactor may be preheated before the mixture is added into the reactor, or heated after the mixture is added, or heated simultaneously as the mixture is added into the reactor. In one embodiment, the selected reduction temperature is maintained throughout the metal reduction process. “Maintained” as used herein means that the temperature of the reactor is kept roughly at the selected reduction temperature. For example, when the mixture, which may be at a lower temperature than the selected reduction temperature, is added into the reactor, it may cause a decrease of the reactor's temperature. As another example, at the end of the reaction in the reactor, i.e., when the resulting composition goes out of the reactor, the temperature of the reactor may be higher than the selected reduction temperature. The mixture could also, for example, be heated to the selected reduction temperature before being added into the reactor.

The temperature of the reactor may be controlled according to timing. For example, the timing controlled temperature may include a preheating, heating, and cooling cycle. In one embodiment, the reactor is preheated for a selected preheating time period, before being heated to a selected reduction temperature. Then, the temperature of the reactor is maintained at a selected reduction temperature for a selected reduction time period; and then the reactor is cooled for a selected cooling time period to cool the resulting composition to a desired temperature. During this cycle, different sections of the reactor might, for example, be at a different temperature. In one embodiment, at one time, the inlet of the reactor may be at a preheating temperature, the middle may be at a selected reduction temperature, and the outlet may be at a cooling temperature. In another embodiment, at one time, the temperature of the reactor is maintained at a selected reduction temperature.

Selection of the reduction temperature depends on various factors, such as the nature of the metal in the metal-containing material and/or the particle size of the grounded metal-containing material. In one embodiment, the selected reduction temperature is not lower than 500° C. For example, the selected reduction temperature can range from about 800° C. to about 1200° C. In another embodiment, the selected reduction temperature ranges from about 1000° C. to about 1050° C.

The at least one zero-valent metal may be chosen from magnetic metals and non-magnetic metals, such as cobalt, copper, iron, lead, nickel, tin, tungsten, and zinc. In one embodiment, the at least one zero-valent metal is chosen from iron, nickel, and tin. For example, the at least one zero-valent metal can be chosen from nickel and tin. In another embodiment, the at least one zero-valent metal is iron.

The metal reduction process disclosed herein can be used to extract more than one type of metal simultaneously, or sequentially, from the metal-containing material, depending on the type of the metal-containing material and/or the nature of the metal. For example, if the metal-containing material contains two types of metals, and if the two types of metals can be extracted under similar conditions, such as similar reduction temperature, the two types of metals may accordingly be simultaneously extracted from the metal-containing material. As another example, if the metal-containing material contains two types of metals, but the two types of metals ordinarily cannot be reduced under similar conditions, one metal may be reduced first, and the residue may be recovered and subject to another round of the metal reduction process as disclosed herein.

The selection of a reduction period depends on various factors, such as the nature of the metal in the metal-containing material, the selected reducing agent, and/or the particle size of the grounded metal-containing material. In one embodiment, the reduction period is not shorter than 20 minutes. For example, the reduction period can range from about 60 minutes to about 150 minutes.

In one embodiment, the moving of the mixture through the reactor while stirring the mixture is achieved by propelling and mixing the mixture inside the reactor using, for example, the metal reduction apparatus disclosed herein. For example, the mixture may be stirred continuously. Alternatively, the mixture may be stirred intermittently.

In one embodiment, as the reactor is filled with the mixture including, for example, the at least one metal-containing material, oxygen is depleted inside of the reactor during the movement of the mixture through the reactor. “Depleted” as used herein means that substantially no O2remains present in the reactor. For example, the depletion of O2may be achieved through means that seal the reactor and thus prevent O2from getting inside the reactor. Nevertheless, a trace amount of O2may be brought in when the mixture is added into the reactor. The level of the O2present within the sealed reactor may be further depleted after the O2is reacted with a reducing agent present in the mixture. An oxygen-depleted environment is desirable for metal reduction processes and could increase the reduction reaction rate and/or make the reduction reaction more complete.

The resulting composition disclosed herein comprises at least one zero-valent metal and a residue. The residue can include, for example, any unreacted additive, unreacted reducing agent, unreacted metal-containing material, by-products of the absorbed waste gas(es) that are produced during the metal reduction process, and by-products of the reaction of the metal-containing material with the additive and the reducing agent.

The at least one zero-valent metal may be in the form of metal cores, and the residue may be, in full or in part, in the form of a coating, which partially or completely covers the at least one zero-valent metal core and can be removed by, for example, grinding.

Accordingly, the resulting composition may be in the form of solid particles, which comprise the metal cores and the coatings thereof. The phrase “solid particles” as used herein means particles without holes inside. Solid particles are different from sponge particles, which have holes inside. As another example, the solid particles in the resulting composition may exist in agglomerated form. In one embodiment, the solid particles have a particle size of no greater than about 10 mm. In another embodiment, the solid particles have a particle size no greater than about 1 mm.

The metal reduction process disclosed herein may further comprise grinding the at least one metal-containing material, at least one reducing agent, and at least one additive separately into the form of fine particles and mixing them together before adding the mixture into the reactor. Alternatively, the metal reduction process disclosed herein may further comprise grinding the at least one metal-containing material, at least one reducing agent, and at least one additive together to form the mixture in the form of fine particles before adding the mixture into the reactor. When the at least one metal-containing material is chosen from ores, the grinding depends on, for example, the embedded particle size of the metal compounds in the ores. One of the main purposes of the grinding includes, for example, to expose the metal component of the metal-containing material. To this end, a pre-grinding process may be used, including crushing, to obtain an appropriate size of ores to be used in a grinder.

To further describe the metal reduction process disclosed herein, certain embodiments are, in part, presented in the Figures, e.g.,FIG. 1. S101ofFIG. 1represents a step of adding a mixture comprising at least one metal-containing material, at least one reducing agent and at least one additive in the form of fine particles to a reactor. The mixture is ground into particles having a particle size of less than about 1 mm, to increase the reaction rate of the metal reduction.

S102ofFIG. 1represents a step of heating and maintaining the reactor at a selected reduction temperature, and moving the mixture through the reactor while stirring the mixture continuously, allowing a reduction period to occur. Depending on the type of the metal to be obtained, the reactor is heated to a temperature suitable for the metal reduction to occur. An appropriately selected reduction temperature and the stirring of the mixture both could facilitate the efficiency of the reduction reaction.

S103ofFIG. 1represents a step of obtaining a resulting composition, which comprises at least one zero-valent metal and a residue, being formed following a reduction period. The resulting zero-valent metal can be further made into metal products. The residue may be further treated, for example, for use as a cement admixture.

The reduction temperature and reduction period are controllable in the metal reduction process disclosed herein. For example, if a hematite is to be reduced, a reduction temperature of about 1000° C. to about 1050° C., and a reduction period of about 60 minutes to about 150 minutes, may be selected. For another example, if an awaruite is to be reduced, a reduction temperature of about 950° C. to about 1100° C., and a reduction period of about 60 minutes to about 120 minutes, may be selected.

The present disclosure further relates to a metallurgical process, comprising:a mixing stage, comprising mixing at least one metal-containing material, at least one reducing agent, and at least one additive to form a mixture;a metal reduction stage, comprising adding the mixture into a reactor, heating the reactor to a selected reduction temperature, moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, and obtaining a resulting composition, wherein the resulting composition comprises at least one zero-valent metal and a residue; anda separation stage, wherein the at least one zero-valent metal is separated from the residue.

The mixing stage disclosed herein may, for example, comprise adding the at least one additive and the at least one reducing agent to the at least one metal-containing material to form a mixture, and grinding the mixture into a form of fine particles. The ground mixture of the metal-containing material, the at least one reducing agent, and the at least one additive may contain water. Thus, the metallurgical process may, for example, further comprise a drying step. The mixture may be dried by at least one heat conductive medium that is commonly used in the art. For example, the at least one heat conductive medium can be chosen from heat-conductive oils, water, and gas.

Alternatively, the metallurgical process may, for example, further comprise grinding the at least one metal-containing material, the at least one reducing agent, and the at least one additive separately into the form of fine particles prior to forming a mixture. The at least one metal-containing material, the at least one reducing agent, and/or the at least one additive may contain water. Thus, the metallurgical process may, for example, further comprise drying the at least one metal-containing material, the at least one reducing agent, and/or the at least one additive separately after the grinding step. In an alternative embodiment, after the grinding step, the ground at least one additive, the ground at least one reducing agent, and the ground at least one metal-containing material may be mixed together, in appropriate proportions, to form a ground mixture. The ground mixture may then be dried at least once to reach a desired water content prior to entry into the reactor.

The metal reduction stage disclosed herein is similar to the metal reduction process set forth above. It is understandable that one or more metal reduction process may be carried out simultaneously in one or more reactors.

The metallurgical process disclosed herein may further comprise, for example, a grinding step after the direct reduction stage, wherein the resulting composition is ground. The grinding step may serve to disassociate the zero-valent metal and a covering of the zero-valent metal that is formed during the metal reduction stage. In one embodiment, a wet grinding method is used to grind the resulting composition. Any liquid that can serve the purpose for wet grinding may be used. For example, water or an appropriate aqueous solution or suspension comprising, e.g., the at least one additive, may be used for wet grinding. The amount of the liquid used for wet grinding may be selected based on various factors, such as the amount of the resulting composition that need to be ground. An optimal amount of the liquid may be selected for efficiency purposes. For example, prior to the grinding, the metallurgical process comprises adding water to the resulting composition such that the weight ratio of the resulting composition to the water ranges from about 1:1 to about 4:1. As another example, the weight ratio of the resulting composition to the water is about 7 to about 3.

In an alternative embodiment, a dry grinding method is used to grind the resulting composition such that the at least one zero-valent metal core is disassociated from the covering. For example, the grinding step may last from about 5 minutes to about 40 minutes.

The metallurgical process may further comprise a heat recovery stage, wherein, after the metal reduction stage is completed but before the grinding step, the resulting composition is cooled via at least one heat-conductive medium, and the absorbed heat in the at least one heat-conductive medium is reused for drying at least one material that needs to be dried. The at least one material that needs to be dried may include, for example, the at least one metal-containing material, the at least one reducing agent, the at least one additive, and/or any mixture thereof, before the reduction reaction starts. In one embodiment, the at least one heat-conductive medium is chosen from heat-conductive oils, water, and gas.

The separation stage of the metallurgical process disclosed herein may be conducted using any separation method known in the art. For example, it could be conducted using at least one method chosen from magnetic separation methods, electrostatic separation methods, gravity separation methods, and flotation separation methods. In one embodiment, the at least one zero-valent metal is chosen from magnetic metals, such as iron. The at least one magnetic zero-valent metal may be separated from the residue using, for example, a wet magnetic separation method. In an alternative embodiment, the at least one zero-valent metal is chosen from nonmagnetic metals. In this case, the at least one zero-valent metal may be separated from the residue by using a method known in the art chosen, for example, from gravity separation methods, electrostatic separation methods, and flotation separation methods.

The metallurgical process disclosed herein may further comprise, after the separation stage, a stage for making a metal product, and/or a stage for treating the residue. The stage for making a metal product may comprise, for example, treatment of the at least one zero-valent metal, and formation of a metal product.

The treatment of the at least one zero-valent metal may comprise, for example, at least one step chosen from drying the at least one zero-valent metal, and forming an inert film on the surface of the at least one zero-valent metal. The treatment of the at least one zero-valent metal may further comprise, for example, a dewatering step wherein water is removed from the at least one zero-valent metal. In one embodiment, the dewatering step is conducted using at least one method chosen from strong magnetic dehydration, centrifugation dehydration, vacuum filtration, and pressure filtration. “Drying” as used herein means using heat or a heat conductive medium to remove water from a material. “Dewatering” as used herein means using a device to extract water from a material.

The formation of a metal product may comprise, for example, mixing at least one binder with the at least one zero-valent metal, and briquetting the mixture of the at least one zero-valent metal and the at least one binder to form a metal product. The at least one binder is chosen, for example, from cement clinkers with a specific surface area of higher than about 600 m2/kg. In one embodiment, the at least one binder may be in an amount ranging from about 0.5% to about 5% by weight relative to the total weight of the metal product. For example, the at least one binder can be present in an amount of about 2% by weight relative to the total weight of the metal product.

The stage for treating the residue may comprise, for example, at least one step chosen from dewatering the residue, and drying the residue. The dewatering step may be conducted using at least one method known in the art, chosen, for example, from strong magnetic dehydration, centrifugation dehydration, vacuum filtration, and pressure filtration. The stage for treating the residue may further comprise, for example, grinding the residue, such as for use as a cement admixture.

The metallurgical process disclosed herein may further comprise, for example, recovering the at least one additive following the separation stage. Because the metallurgical process disclosed herein can be continuous, the recovery process of the at least one additive may be continuous and may occur in cycle(s). In one embodiment, the metallurgical process may comprise a wet grinding method using water after the metal reduction stage, wherein the residue after the separation stage is dewatered to yield a solid portion of the residue, and an aqueous portion that comprise all or some of the at least one additive. The aqueous portion may be a solution, and may be in the form of a suspension. The concentration of the at least one additive in the aqueous portion after the dewatering may be adjusted to be close to the saturation concentration of the at least one additive. The at least one additive may be recovered by, for example, drying.

The metallurgical process disclosed herein is further described by the embodiment shown inFIG. 2.FIG. 2is a flowchart of an exemplary metallurgical process in accordance with the present disclosure, including a mixing stage, comprising mixing at least one metal-containing material, at least one reducing agent, and at least one additive to form a mixture; a metal reduction stage, comprising adding the mixture into a reactor, heating the reactor to a selected reduction temperature, moving the mixture through the reactor while stirring the mixture, allowing a reduction period to occur, and obtaining a resulting composition, wherein the resulting composition comprises at least one zero-valent metal and a residue; a separation stage, comprising separating the at least one zero-valent metal from the residue; and a post treatment stage, wherein the at least one zero-valent metal and the residue are treated. In one embodiment, during the metal reduction stage, the reactor is maintained at a selected reduction temperature.

As shown inFIG. 2, before the mixing stage, the metal-containing material may be crushed into particles according to a required specification, for example, to a size as allowed by the grinder, e.g., a mill to be used. In one embodiment, the metal-containing material may be crushed into particles finer than about 3 mm to avoid potential damage to the grinder, e.g., a mill. Then, during the mixing stage, the at least one additive and the at least one reducing agent may be added into the at least one metal-containing material to form a mixture. The mixture may then be ground into the form of fine particles with a particle size of less than 0.074 mm. The mixture may be further dried using a heat-conductive oil or water. The mixture may be thoroughly mixed before being fed into a metal reduction apparatus.

As shown inFIG. 2, between the metal reduction stage and the separation stage, a heat recovery stage and a grinding step may be carried out. The purpose of the heat recovery stage includes, for example, to cool the resulting composition, and transfer the heat to a thermal conducting medium. The recovered heat may then be used to dry the materials that need to be dried. During the grinding step, the resulting composition can be ground using a wet grinding method such that the metal core and the coating thereof are disassociated.

Also shown inFIG. 2, the post-treatment processes may include a stage for making a metal product, and a stage for treating the residue. During the stage for making the metal product, the reduced metal may be dewatered first using, for example, a strong magnetic dehydration method and dried, and then passivated by forming an inert film on the surface of the metal to prevent further oxidation. A binder may then be added to and mixed with the zero-valent metal. Then the metal and the binder may be briquetted to form a metal product of mass. During the stage for treating the residue, the residue may be dewatered, dried and ground to be used as a cement admixture.

The metallurgical process disclosed herein may further comprising recovering the at least one additive after the separation stage. For example, the metallurgical process disclosed herein may further comprise a wet grinding step following the metal reduction stage but before the separation stage, and at least one dewatering step after the separation stage wherein the separated residue is dewatered resulting in a solid portion and an aqueous portion, and the at least one additive is recovered by adjusting the concentration of the at least one additive in the aqueous portion to be close to the saturation concentration of the at least one additive, and drying the aqueous portion.

In another example, the metallurgical process as disclosed herein may further comprises a wet grinding step following the metal reduction stage but before the separation stage, a first dewatering step after the separation stage wherein the residue is dewatered resulting in a solid portion and a first dewatering aqueous portion, at least one washing step wherein the solid portion is washed, and at least one second dewatering step resulting in at least one second dewatering aqueous portion, wherein the at least one additive is recovered by using the first dewatering aqueous portion and the at least one second dewatering aqueous portion in the wet grinding step until the concentration of the at least one additive in the first dewatering aqueous portion or the at least one second dewatering aqueous portion is to be close to the saturation concentration of the at least one additive and drying said first dewatering aqueous portion or the at least one second dewatering aqueous portion.

The metallurgical process disclosed herein, as related to recovery of the at least one additive, is further described by the embodiments shown inFIGS. 3(A)and (B). As shown inFIG. 3(A), the metallurgical process may comprise a wet grinding step using water following the metal reduction stage but before the separation stage, a first dewatering step after the separation stage wherein the residue is dewatered resulting in a solid portion of the residue and a first dewatering aqueous portion, a first washing step using water wherein the solid portion is washed, a second dewatering step resulting in a solid portion of the residue and a second dewatering aqueous portion, a second washing step using water wherein the solid portion is washed, and a third dewatering step resulting in a solid portion of the residue, which may be substantially free of the at least one additive and a third dewatering aqueous portion. The aqueous portion after each dewatering step may be in the form of a solution or a suspension. As the metallurgical process can be continuous, the at least one additive can also be recovered continuously by adjusting the at least one additive concentration in the aqueous portion to be close to the saturation concentration of the at least one additive and by drying the combined aqueous portions collected after the dewatering steps. In this embodiment, the first dewatering aqueous portion, the second dewatering aqueous portion, and the third dewatering aqueous portion are combined and the at least one additive concentration in the combined aqueous portion is adjusted to be close to the saturation concentration of the at least one additive by, for example, controlling the amount of water that is added into the wet grinding, the first washing, and the second washing steps.

In another embodiment, the at least one additive can be recovered continuously and in a cycle. As shown inFIG. 3(B), the metallurgical process may comprises a wet grinding step using water following the metal reduction stage but before the separation stage, a first dewatering step after the separation stage wherein the residue is dewatered resulting in a solid portion of the residue and a first dewatering aqueous portion, a first washing step using water wherein the solid portion is washed, a second dewatering step resulting in a solid portion of the residue and a second dewatering aqueous portion, a second washing step using water wherein the solid portion is washed, and a third dewatering step resulting in a solid portion of the residue, which may be substantially free of additive(s) and a third dewatering aqueous portion. The aqueous portion after each dewatering step may be in the form of a solution or a suspension. The first dewatering aqueous portion, the second dewatering aqueous portion and the third dewatering aqueous portion could be delivered back to be used in the wet grinding step to form a cycle without addition of water to the wet grinding step, until, for example, the at least one additive concentration in the first dewatering aqueous portion is close to be the saturation concentration of the at least one additive. At that time, that first dewatering aqueous portion is collected and dried to recover the at least one additive. As the metallurgical process can be continuous, the at least one additive can also be recovered continuously by adjusting the at least one additive concentration in the aqueous portion to be close to the saturation concentration of the at least one additive. Such adjustment can be conducted by, for example, controlling the amount of water that is added into the wet grinding, the first washing, and the second washing steps.

It is understandable that, in other embodiments similar to those as shown inFIGS. 3(A)and (B), the washing and dewatering steps after the metal reduction, wet grinding, and separation in the metallurgical process disclosed herein may be operated once or more than once to achieve, for example, at least one of the following purposes: (1) the concentration of the at least one additive in the aqueous portion after the dewatering step could be adjusted to be close to the saturation concentration of the at least one additive so that it is easier to recover the at least one additive by drying; and (2) all or some of the at least one additive in the solid portion of the residue could be removed after the washing and dewatering steps such that the quality of a product made from the solid portion of the residue, e.g., a cement admixture, is not severely adversely affected by some of the at least one additive that may still have been retained.

The steam produced by evaporation can be used for drying those materials that are in need to be dried. The steam can also be condensed, and the resulting water can be reused.

The present disclosure also relates to a product, made by the metal reduction process set forth above, wherein the resulting composition is in the form of solid particles comprising at least one zero-valent metal core and a coating.

In one embodiment, the solid particles have a particle size of no greater than about 10 mm. As another example, the solid particles have a particle size no greater than about 1 mm.

The disclosure also provides a metal reduction system.FIG. 4illustrates such a system. The metal reduction system48comprises, in order from most upstream to most downstream, a material preparation system100, a metal reduction apparatus200, a heat recovery device300, and a separator system400. Additionally, the metal reduction system48includes, in parallel, a metal product system500and a residue utilization system600, both of which are located downstream of the separator system400. The metal reduction system48also includes an additive recovery system700, which may be located downstream of the metal product system500and/or the residue utilization system600. It is understood that the metal reduction system48may include additional or alternative components for carrying out the processes disclosed herein. Moreover, it is understood that the metal reduction system48need not be capable of carrying out every process disclosed herein, and need not include all of the components shown inFIG. 4.

The material preparation system100is used to prepare a mixture in the form of fine particles. This mixture may include at least one metal-containing material, at least one reducing agent, and at least one additive. As shown inFIG. 4, the material preparation system100may include a crusher101for crushing the at least one metal-containing material, the at least one reducing agent, and/or the at least one additive; a mixing machine102for mixing the at least one metal-containing material, the at least one reducing agent, and the at least one additive; a grinder103, for example, a ball mill, for grinding the mixture into fine particles; and a dryer104for drying the ground mixture. It is understood that the material preparation system100may include one or more alternative machines for forming the fine particles, and that such one or more machines may individually form the at least one metal-containing material, the at least one reducing agent, and the at least one additive into fine particles, or may form the fine particles from a combination of one or more of the at least one metal-containing material, the at least one reducing agent, and the at least one additive.

The metal reduction apparatus200is used to effect a reduction reaction of the metal-containing material and extract simple substance metal.FIG. 5depicts an exemplary embodiment of the metal reduction apparatus200and the heat recovery device300.FIG. 6is a cross section taken at the line6-6of the metal reduction apparatus200shown inFIG. 5, andFIG. 9is a cross section taken at the line9-9of the metal reduction apparatus200shown inFIG. 5. As shown inFIGS. 5,6, and9, the metal reduction apparatus200includes two propelling blender support devices1, a press-type loading device2, a feed hopper3, a propelling blender4, a reactor housing5, a heating device6, an insulating layer7, high-temperature seals8, two couplers9(a coupler9aand a coupler9b), a gear bank29, a speed reducer10, a motor11, a housing base support12, housing sliding supports30, and a discharge pipe13.

The parts of the metal reduction apparatus200may be made of metallic or non-metallic materials that are capable of withstanding the operating temperature of the metal reduction apparatus200. For example, the metal reduction apparatus200may be made of metallic or non-metallic materials that are capable of withstanding temperatures of between about 600° C. and about 3000° C. High temperature steel can, for example, be used for many of the parts of the metal reduction apparatus200.

During operation of the metal reduction apparatus200, the press-type loading device2, which is coupled to the feed hopper3, presses feed material (the mixture) in the feed hopper3into an upstream portion31of the housing5. It is understood, however, that other components or arrangements could be used to load the feed material into the upstream portion31of the housing5. For example, a mere gravity feed or a rotary type pump could be used to load the feed material into the upstream portion31of the housing5. The housing5is supported by the housing base support12, sealed at each end by the high-temperature seals8, and at least partially covered by the heating device6. The heating device6is at least partially covered by the insulating layer7, and provides heat to the material via the housing5. Thus, it is understood that the heating device6may be thermally coupled to the housing5. As used herein, a first structure is thermally coupled to a second structure if heat can be transferred between the first structure and the second structure either directly or indirectly. The propelling blender4is located in the housing5, and may include two shafts arranged parallel to each other. It is understood, however, that the propelling blender4may include another number of shafts (e.g., one or more shafts), and that these shafts may or may not be arranged parallel to each other.

Regardless of the number of shafts, each end of each shaft is connected to and supported by one of the propelling blender support devices1. And, one end of each shaft is connected to one coupler9(e.g., one end of a shaft61is connected to the coupler9a, and one end of a shaft62is connected to the coupler9b). The couplers9are connected to the gear bank29, which is in turn connected to the speed reducer10and the motor11. The motor11provides rotation power to the gear bank29via the speed reducer10. The gear bank29apportions the rotation power between the couplers9, and the couplers9provide the rotation power to the shafts of the propelling blender4. It is understood that the metal reduction apparatus200need not necessarily include the gear bank29. For example, in embodiments of the propelling blender4having only one shaft, the speed reducer10may receive rotation power from the motor11, and provide the rotation power directly to the coupler9connected to the one shaft. Alternatively, the metal reduction apparatus200could include one motor11and one speed reducer10for each shaft of the propelling blender4, and each motor11could provide rotation power to one shaft via one speed reducer10and one coupler9. In any case, rotation of the one or more shafts of the propelling blender4stirs and propels the feed material through the housing5to a downstream portion32of the housing5, where the material is discharged from the metal reduction apparatus200via the discharge pipe13.

The insulating layer7may be applied to the exterior surface of the heating device6, and may help prevent heat from escaping the heating device6and the housing5. The high-temperature seals8are attached to both ends of the housing5, and may withstand the operating temperature of the metal reduction apparatus200. The high-temperature seals8may help retain an oxygen-depleted environment in the housing5(e.g., by preventing oxygen from entering the housing5), and may help prevent dust in the housing5from escaping into mechanical parts of the metal reduction system48.

An enlarged view of the propelling blender4is shown inFIG. 7. As noted above, the propelling blender4may include two shafts61,62that may be arranged parallel to each other. Each of shafts61,62may have a plurality of blades63configured intermittently along its circumference (FIG. 8) and along its length (FIG. 7). It is understood, however, that each of shafts61,62could have fewer or more blades63. For example, each of shafts61,62could have a single blade extending along its length, and this single blade could be formed in a helical configuration.

Referring to the shaft62illustrated inFIG. 7, each of the blades63may have an upstream face50and a downstream face55. The upstream face50of each blade63may be generally normal to a longitudinal axis70of the shaft62, and the downstream face55of each blade63may be tilted with respect to a plane72extending normal to the longitudinal axis70of the shaft62. In particular, the downstream face55of each blade63may include an angle of tilt a of between about 1° and about 45°. It is understood that the downstream face55may be planar or nonplanar, and that the angle of tilt α of a nonplanar downstream face55would be determined using a line between points U and L, as shown inFIG. 7. The angle of tilt α may be the same for each of the blades63of the shaft62, in which case the blades63are said to be arranged parallel to each other. Alternatively, the angle of tilt α may vary between the blades63of the shaft62, and may increase or decrease along the length of the shaft62. For example, the angle of tilt α of a blade63at an upstream end of the shaft62may differ from the angle of tilt α of a blade63at a downstream end of the shaft62by between about 5° and about 15°. Such variation in the angle of tilt α may improve the propulsion and stirring of the feed material by the propelling blender4.

The blades63may also be slightly bent. Specifically, the radially inner edge64of each blade63may be twisted relative to the radially outer edge65of the blade63. Moreover, the thickness of each blade63may vary along the arc of the blade63, and the inner edge64of each blade63may be positioned within a recess67of the shaft62, as illustrated inFIG. 8. This recessed coupling engagement of the blade63to the shaft62may help prevent the blade63from being bent or broken during operation of the metal reduction apparatus200. Additionally, the blade63may be covered by at least one abrasion resistant material, which may help to prevent and/or slow wearing of the blade63during operation of the metal reduction apparatus200. For example, the wear resistant material may include nickel, chrome, titanium, diamond, and/or another material or combination of materials that is resistant to wear. Alternatively, the blade63may be treated to resist abrasion. For example, the blade63may be heat treated or otherwise treated to resist abrasion.

As illustrated inFIG. 8, each blade63may be substantially C-shaped, as viewed in a longitudinal direction of the shaft62, and may extend for an arc β around the shaft62. For example, β may be between about 120° and about 160°, and may be about 140°. Alternatively, β may be smaller than about 120° or larger than about 160°. As shown inFIG. 7, the C-shaped blades63may be located at the same circumferential position along shaft62. Alternatively, the C-shaped blades63may be located at different circumferential positions along the shaft62. Finally, it is understood that the above discussion of the various configurations of blade63on shaft62is equally applicable to the blades63on shaft61, and that shafts61,62may have the same or varying configurations. For example, the blades63on the shaft61may be positioned at varying longitudinal positions relative to the blades63on the shaft62. This may allow the blades63on the shaft61to overlap the blades63on the shaft62, as viewed in a longitudinal direction of the propelling blender4. Thus, the blades63on the shaft61may mesh with the blades63on the shaft62during operation of the metal reduction apparatus200.

Referring toFIGS. 5 and 6, the motor11, along with the speed reducer10, the gear bank29, and the couplers9, provides rotating power with adjustable speed to the shafts61,62of the propelling blender4. The motor11may include an AC motor, an AC variable-frequency motor, or another type of electric motor. Alternatively, the motor11may include a diesel engine, a gasoline engine, or another type of combustion engine.

The speed reducer10is used to coordinate the rotation speed of the shafts61,62and the rotation speed of the motor11. This coordination may be useful because the rotation speed of the motor11may be much higher than the desired rotation speed of the shafts61,62, and the amount of torque required by the shafts61,62may be greater than the motor11can provide. The speed reducer10may take the form of a cylindrical gear reducer. But, it is understood that the speed reducer10may alternatively include a planetary gear reducer or another appropriate gear reducing arrangement.

The gear bank29may be used to apportion rotation power between the shafts61,62of the propelling blender4. For example, the gear bank29may evenly or unevenly distribute rotation power between the shafts61,62. The gear bank29may include, for example, one or more gears. Alternatively or additionally, the gear bank29may include, for example one or more chains, belts, pulleys, or other devices capable of apportioning rotation power between the shafts61,62.

The couplers9are used to compensate for radial, axial, and/or angular misalignment of the shafts61,62of the propelling blender4. The couplers9may improve the reliability of the metal reduction apparatus200by helping reduce the effect of deformations of the shafts61,62caused by gravity and/or the operation of metal reduction apparatus200. For example, the couplers9may each include one or more universal joints, Oldham couplings, Thompson couplings, or other couplers capable of transmitting torque while permitting radial, axial, and/or angular misalignment of the shafts61,62.

The propelling blender support devices1are used to support the shafts61,62of the propelling blender4. This support may improve the stability of the shafts61,62by preventing the shafts61,62from deforming and/or deflecting as a result of their own weight. Each propelling blender support device1may include one or more bearings, which may allow for relative longitudinal movement of the shafts61,62as the shafts61,62expand longitudinally. For example, the shafts61,62may expand longitudinally (e.g., up to or more than about 10 cm) when high temperatures (e.g., about 1100° C.) are reached during operation of the metal reduction apparatus200. The one or more bearings may include, for example, one or more of a bushing or sleeve bearing, a fluid bearing, a magnetic bearing, or another type of bearing that is designed to allow for relative longitudinal movement of the shafts61,62.

Referring toFIGS. 5 and 9, the housing base support12may support the housing5, and may include a frame having one or more beams. Alternatively or additionally, the housing base support12may include one or more hangers, brackets, and/or other elements capable of supporting the housing5, and/or other parts of the housing base support12. Although the housing base support12may directly support the housing5, it is contemplated that the housing base support12may alternatively or additionally support the housing5via the sliding supports30, as illustrated inFIGS. 5 and 9. The plurality of sliding supports30may be located along the length and width of the housing5. In any case, the housing base support12and/or sliding supports30may prevent the housing5from deforming and/or deflecting as a result of the weight of the housing5. By preventing deformation and/or deflection of the housing5, the housing base support12and/or the sliding supports30may also prevent the housing5from inhibiting rotation of the shafts61,62of the propelling blender4.

As shown inFIG. 5, each sliding support30may include a first element35and a second element40movably coupled to the first element35. The first element35may be fixedly attached to the housing5, and the second element40may be fixedly attached to the housing base support12. The first and second elements35and40may, however, be moveable relative to each other. This relative movement allows the housing5to move relative to the housing base support12when the housing5expands longitudinally. For example, the housing5may expand longitudinally (e.g., by up to or more than about 10 cm) when high temperatures (e.g., about 1100° C.) are reached during operation of the metal reduction apparatus200. In particular, each of first and second elements35and40may include flat and polished surfaces. And, the flat and polished surface of the first element35may be positioned on top of the flat and polished surface of the second element40. The flat and polished surface of the first element35may then slide along the flat and polished surface of the second element40as the first element35moves relative to the second element40. Alternatively, the first and second elements35and40may not include elements having flat and polished surfaces. For example, the first element35may alternatively include a wheel and the second element40may include a track so that the first element35may roll along the second element40as the housing5expands longitudinally. In yet another alternative, the first element35may include a track and the second element40may include a wheel, or first and second elements35and40may include other elements that are capable of moving relative to each other while supporting the housing5.

The heating device6provides heat for the reduction reaction via the housing5. The heating device6may include one or more low energy consumption heating units that are thermally coupled directly or indirectly to the housing5. For example, each of the heating units may include a resistance heater, an infrared tube heater, a gas furnace, a mid-frequency heater, a coal furnace, a hot stove, a boiling furnace, a circulating fluidized bed furnace, a conveyor furnace, a heat exchange casing, or another unit capable of providing heat for metal reduction. Additionally, the heating device6may include one or more temperature controlling units, which may be controllably coupled to the heating unit. For example, each of the temperature controlling units may include one or more sensors and/or a controller. Each of the sensors of a temperature controlling unit may sense and communicate to the controller a parameter indicative of a temperature of the housing5and/or the mixture located within the housing5. Based on this temperature, the controller may then adjust the operation of one or more of the heating units to maintain the temperature at a selected reduction temperature.

During a reduction process, the feed material (the mixture of the at least one metal-containing material, the at least one reducing agent, and the at least one additive) is fed from the feed hopper3into the housing5. In the housing5, the mixture is stirred and propelled by the propelling blender4. The reduction reaction takes place in the housing5, where the metal-containing material reacts with the reducing agents to produce a high temperature resulting composition, which includes simple substance metal and other products like waste gas and residue. The waste gas contains harmful elements, such as sulfur and phosphorus, which may be absorbed by the additives in the residue, minimizing environmental pollution. The high temperature resulting composition is then discharged through discharge pipe13, and subjected to post-reduction processing.

The waste heat recovery device300is used to recover and reuse the heat from the reduction process. As shown inFIG. 5, the waste heat recovery device300is coupled to the metal reduction apparatus200. The waste heat recovery device300is configured to receive the high temperature resulting composition from the metal reduction apparatus200, and recover heat from the high temperature resulting composition.

As shown inFIG. 5, the waste heat recovery device300may include two conveyor support devices14, a feed pipe15, a conveyor16, a heat recovery device housing17, heat exchange casings18and19, an insulating layer20, high-temperature seals21, a coupler22, a speed reducer23, a motor24, a housing base support26, and a discharge pipe25.

During operation of the waste heat recovery device300, the resulting composition discharged from the metal reduction apparatus200is fed into an upstream portion80of the housing17via the feed pipe15. For example, the discharge pipe13of the metal reduction apparatus200may be connected to the feed pipe15, and the resulting composition may be fed directly from the metal reduction apparatus200into the housing17via the feed pipe15. Alternatively, other structures may be positioned between the discharge pipe13and the feed pipe15, and the resulting composition may be fed indirectly into the housing17via the feed pipe15. The housing17is supported by the housing base support26, sealed at each end by the high-temperature seals21, and at least partially covered by the heat exchange casings18and19. The heat exchange casings18and19are at least partially covered by the insulating layer20, and recover heat from the resulting composition via the housing17. Thus, it is understood that the heat exchange casings18and19are thermally coupled to the housing17. The conveyor16is located in the housing17, and may include a shaft. Each end of the shaft is connected to and supported by one of the conveyor support devices14. And, one end of the shaft is connected to the coupler22, which is in turn connected to the speed reducer23and the motor24. The motor24provides rotation power to the shaft of the conveyor16via the speed reducer23and the coupler22. Rotation of the shaft of the conveyor16propels the resulting composition through the housing17to a downstream portion85of the housing17, where the resulting composition is discharged from the heat recovery device300via the discharge pipe25.

Some structures of the heat recovery device300are similar to those of the metal reduction apparatus200. In particular, the conveyor support devices14are similar to the propelling blender support devices1, the heat recovery housing17is similar to the reactor housing5, the insulating layer20is similar to the insulating layer7, the high-temperature seals21are similar to the high-temperature seals8, the coupler22is similar to the couplers9, the speed reducer23is similar to the speed reducer10, the motor24is similar to the motor11, the housing base support26is similar to the housing base support12, and the discharge pipe25is similar to the discharge pipe13.

The heat exchange casings18and19recover heat from the resulting composition via the housing17. Each of the heat exchange casings18and19may include a heat-conductive medium, which may absorb and/or store heat from the resulting composition, thereby helping to cool the resulting composition. This heat may be used to assist in drying the materials that need drying, and may reduce the total energy consumption of the metal reduction system48. For example, the heat-conductive medium of the heat exchange casing18may include oil, and the heat-conductive medium of the heat exchange casing19may include water. Alternatively, the heat-conductive medium of the heat exchange casing18may include water, and the heat-conductive medium of the heat exchange casing19may include oil. In yet another alternative, the heat-conductive mediums of the heat exchange casings18and19may include gas or other mediums capable of absorbing and/or storing heat, and may each include the same or different mediums. In any case, the heat-conductive medium(s) may be circulated among various components of the metal reduction system48to transfer heat between the various components.

Referring toFIG. 4, the separator system400is used to separate the reduced metal exiting the metal reduction apparatus200from the residue. As shown inFIG. 4, the separator system400may include a grinder401for grinding the resulting composition. For example, the grinder401may include a ball mill, a supergravity mill, or another type of grinder capable of grinding the resulting composition. Additionally, the separator system400may include a separator402for separating the reduced metal from the residue. For example, the separator402may include a magnetic separator for separating magnetic metal from the residue. Alternatively, the separator402may include a gravity separator for separating nonmagnetic metal from the residue. In yet another alternative, the separator402may include a flotation separator, an electrostatic separator, or another type of separator capable of separating nonmagnetic metal from the residue.

The metal product system500may be used to manufacture metal products with the reduced metal. As shown inFIG. 4, the metal product system500may include a treatment system505for treating the reduced metal. The treatment system505may include a dehydrator for removing water from the reduced metal. For example, the dehydrator may include a strong magnetic dehydrator, a centrifuge (e.g., a horizontal-type spiral centrifuge), a vacuum filtration unit, a pressure filtration unit, or another device capable of removing water from the reduced metal. Additionally, the treatment system505may include a dryer for drying the reduced metal. The treatment system505may also include a passivation system for forming an inert film on the surface of reduced metal (e.g., for treating the reduced metal to be inert, for example, to be difficult to be reoxidized). Alternatively or additionally, the treatment system505may include a device for heat treating or otherwise treating the reduced metal.

The product system500may also include a forming system510for forming the reduced metal. For example, the forming system510may include a cold press configured to briquette a mixture of the reduced metal and a binder into a metal product. Alternatively or additionally, the forming system510may include a device for cutting, stamping, bending, rolling, or otherwise forming the reduced metal into a metal product.

The residue utilization system600is used for comprehensive utilization of the residue. As shown inFIG. 4, the residue utilization system600may include a dehydrator601for removing water from the residue. For example, the dehydrator601may include a strong magnetic dehydrator, a centrifuge (e.g., a horizontal-type spiral centrifuge), a vacuum filtration unit, a pressure filtration unit, or another device capable of removing water from the residue.

Alternatively or additionally, the residue utilization system600may include a dryer602for drying the residue. The residue utilization system600may also include a grinder603for grinding the residue so that it is suitable for, for example, use as a cement admixture. For example, the grinder603may include a ball mill, a supergravity mill, or another type of grinder capable of grinding the residue.

The additive recovery system700is used to recover and reuse at least one additive contained in the water removed by the dehydrators of the metal product system500and/or the residue utilization system600. As shown inFIG. 4, the additive recovery system700may include a sedimentation tank701or another device capable of increasing the concentration of the at least one additive in the water. Additionally, the additive recovery system700may include a dryer702for drying the water, and recovering the at least one additive.

The metal reduction system48of the present disclosure may provide at least one of the following benefits:

1. Low energy consumption. As show inFIG. 5, the heating device6, which includes, for example, a low energy consumption heating unit such as an infrared tube heater, at least partially covers the housing5, and thus heats the feed materials where the reduction reaction occurs. Therefore, the proximity of the low energy consumption heating unit to the housing5allows the metal reduction system48to avoid needlessly heating other structures. The metal reduction system48uses the propelling blender4to propel and stir the feed material, increasing contact between the fine particles of the feed material. This increased contact greatly reduces the reaction time and enhances heat conductivity between the feed material and the components of the metal reduction system48. The feed material is ground into fine particles before entering the housing5, and thus reacts at a low reduction temperature. The exterior surface of the housing5is at least partially covered by the insulating layer7, and thus heat loss is reduced. These features greatly reduce energy consumption.

2. Low investment. Using the propelling blender4to propel and stir the feed material alleviates the need for pelletizing the feed material. Thus, investment in pelletizing equipment is unnecessary. Moreover, during the reduction reaction as disclosed herein, a solid reducing agent such as, for example, coal is used, and thus the present disclosure no longer needs devices for generating and transporting gaseous reducing agents such, for example, CO and H2. Additionally, due to its simple structure, the manufacturing costs of the metal reduction apparatus200are much lower than those of other metal reduction apparatuses.

3. Use of low-grade ores and reactants. The metal reduction system48allows for the use of low-grade ores and reactants. Before being fed into the metal reduction apparatus200, the at least one metal-containing material, the at least one reducing agent (e.g., coal), and the at least one additive are well ground and mixed. The at least one metal-containing material, the at least one reducing agent, and the at least one additive are then further mixed by the propelling blender4. This “double mixing” increases contact between the at least one additive, the at least one metal-containing material, and the at least one reducing agent. The increased contact helps lower the grade requirement of the at least one metal-containing material and increase the reduction rate of the metal.

4. Modular design. The metal reduction system48may have a modular design. With a modular design, the metal reduction system48can accommodate different production needs by combining a flexible number of modules in a flexible way. The metal reduction system48may integrate systems having five functions: heating the feed material with minimum energy; propelling and stirring the feed material; reducing the metal; recycling waste heat; and absorbing harmful waste gas generated in the metallurgical process with the at least one additive, and maintaining the waste gas in the residue. This greatly reduces the quantity and complexity of equipment, rendering the metal reduction process simple and reliable.

5. Superior quality product. As discussed above, matters that are harmful to the environment and quality of the metal products, such as sulfur and phosphorous, are absorbed by the at least one additive and maintained in the residue. Thus, only very low levels of the harmful matters are present in the reduced metal, and superior quality products are produced by the metal reduction system48.

6. Flexibility. The power units may include motors, speed reducers, and couplers, all of which are highly adaptable and reliable, and can accommodate a wide range of material qualities and production conditions.

7. Self-protection of the equipment. The materials move intensely in the housing5, driven by the propelling blender4. And a protection layer of the resulting composition may be formed on an inner wall of the housing5in an area not reached by the blades63of the propelling blender4. The protection layer provides an isolated environment, such as an oxygen depletion environment, for the reduction reaction and can help reduce wearing and corrosion of the inner wall of the housing5.

8. Environmentally friendly. The metal reduction system48may remove sulfur, phosphorus, and other harmful matters during the reduction reaction process.

In summary, the metal reduction system48of the present disclosure may have the advantages of low investment, high productivity, low energy consumption, and low environmental pollution. The metal reduction system48can be used to handle ores that are hard to separate and reduce, for example, ultra low-grade ores, and metal-containing industrial waste. The metal reduction system48may have a high metal recovery rate, may produce a product having quality, and may comprehensively utilize resources.

The present disclosure could be illustrated by the following non-limiting example.

Example of a Metallurgical Process in Accordance With the Present Disclosure

Vanadium titano-magnetite containing iron was used in this example. The ores were dried and mixed with anthracite, calcium carbonate, and other additives to form a mixture. The mixture was ground and fed into a metal reduction apparatus to extract the metal. After the reduction, the resulting composition was cooled and subject to wet grinding and magnetic separation to separate iron from the residue. The iron and residue were dried, and then were used to produce final products.

Dried vanadium titano-magnetite (TFe 52.08%,), containing no more than 5% by weight of water relative to the weight of the vanadium titano-magnetite, anthracite in an amount of 16.9% by weight of the vanadium titano-magnetite; lime stone (primarily containing calcium carbonate) in an amount of 2.5% by weight of the vanadium titano-magnetite; and other additives in an amount of 14.9% by weight of the vanadium titano-magnetite were mixed. The mixture was ground using a ball mill to fine particles with a particle size of less than about 0.074 mm.

(2) Reduction Reaction

The reduction reaction was carried out at a temperature ranging from 1000° C. to 1050° C. for a period of time ranging from 60 minutes to 150 minutes. The resulting composition was cooled by a heat exchanger, and the heat was recovered and reused.

The cooled resulting composition was mixed with water at a mass ratio of 7 to 3, and then ground and washed using a ball mill. The iron was separated from the residue by a wet magnetic separation method. The collected iron had a grade of about 92%, and the iron recovery rate was about 85%.

While the present disclosure has been described in connection with what is considered to be the most practical embodiments, it should be noted that the disclosure is not limited to the disclosed embodiments; the scope of protection for this disclosure should be interpreted according to the claims, applying their broadest interpretation. A person of ordinary skill in this technical field would be able to make certain improvements and modifications, within the spirit and scope of this invention; such improvements and modifications should be considered within the scope of this invention.