Apparatus and method for manufacturing semiconductor device

A lead frame is conveyed along a convey direction in a convey path filled with a reducing gas. A semiconductor pellet is placed on the lead frame at a die bonding portion. A bonding wire made of copper or a copper alloy is supplied to the next wire bonding portion. The lower end of the bonding wire is melted with an oxyhydrogen torch surrounded by an air curtain, thereby forming a ball. The bonding wire is guided into the convey path by a capillary. The ball is thermocompressed to an electrode pad of the semiconductor pellet. The other end of the bonding wire is fused and thermocompressed against the outer lead of the lead frame at a postbonding portion. The bonding wire is thus looped between the semiconductor pellet and the outer lead.

BACKGROUND OF THE INVENTION 
The present invention relates to an apparatus for manufacturing a 
semiconductor device. 
In conventional semiconductor fabrication techniques, an electrode pad of a 
semiconductor element (pellet) is connected to an outer lead by looping a 
gold bonding wire. When a gold wire is used, however, the following 
problems occur. 
(1) When a bonding wire is looped at a high temperature, an intermetallic 
compound of gold and aluminum is formed at a bonding region between the Al 
electrode pad and the bonding wire. For this reason, electrical 
characteristics at the bonding region are degraded. 
(2) Even if the gold bonding wire itself is not oxidized, the reliability 
of the semiconductor device is impaired due to degradation in electrical 
characteristics at the bonding region. 
(3) Since an intermetallic compound of gold and aluminum is formed after 
the bonding process, a semiconductor device with stable electrical 
characteristics cannot be manufactured. 
(4) Gold wire is expensive and increases the manufacturing cost of the 
semiconductor device. 
In order to resolve the above problems, prospective bonding regions are 
selectively activated to loop a copper bonding wire between an electrode 
pad and a copper lead frame, as disclosed in Japanese patent application 
No. 55-88318. According to this technique, however, a bonding failure 
occurs due to an oxide formed on the bonding wire. At the same time, it is 
difficult to form a ball of a predetermined size at a distal end of the 
bonding wire, thereby resulting in incomplete bonding. In addition, the 
prospective bonding region must be activated every time bonding is 
performed, thereby lowering operation efficiency. 
In Japanese patent application No. 57-51237, a distal end of a capillary 
through which a bonding wire extends is introduced into a reducing 
atmosphere in a cover to form a desired ball. At the same time, oxidation 
of the bonding wire is prevented, thereby performing bonding. According to 
this conventional technique, a complicated mechanism including a cover for 
holding the reducing atmosphere is required. A failure often occurs when a 
bonding speed is 1 second or less, so that maintenance is cumbersome. In 
addition, since an oxide on the lead frame having outer leads cannot be 
eliminated, bonding between the copper bonding wire and the copper lead 
frame cannot be performed with high reliability. 
SUMMARY OF THE INVENTION 
It is an object of the present invention to provide an apparatus for 
manufacturing a semiconductor device, wherein wire bonding can be 
performed with high reliability at low cost and provide a bonding region 
with high strength. 
In order to achieve the above object of the present invention, there is 
provided an apparatus for manufacturing a semiconductor device, wherein a 
bonding wire is looped between an electrode pad of a semiconductor element 
and an outer lead of a lead frame, comprising: 
a convey path for conveying the lead frame along a convey direction, the 
convey path being provided with a wire bonding portion and postbonding 
portion which are separated from each other along the convey direction; 
ball forming means for heating the bonding wire of copper or a copper alloy 
at the wire bonding portion and forming balls at both ends of the bonding 
wire; 
bonding wire feeding means for feeding the bonding wire to the wire bonding 
portion and compressing the ball of the bonding wire on the electrode pad; 
compressing means for compressing the ball of the bonding wire on the outer 
lead at the postbonding portion; and 
gas supply means for supplying a reducing or inert gas to the wire bonding 
portion and the postbonding portion and surrounding the bonding wire and 
the ball with the reducing or inert gas. 
According to the present invention, the bonding wire of copper or a copper 
alloy can be bonded by a simple apparatus to the electrode pad of the 
semiconductor device and the outer lead of the lead frame without causing 
incomplete bonding. A semiconductor device having high durability in a 
thermal cycle or a high-temperature exposure test can be manufactured. 
Since copper or a copper alloy can be used as a material for the bonding 
wire and the lead frame, the material cost can be low, thereby enabling 
production of low-cost semiconductor devices with a high yield. 
Furthermore, a plastic encapsulated high-power semiconductor device with 
high reliability can be easily manufactured.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS 
FIG. 1 shows an overall configuration of an apparatus for manufacturing a 
semiconductor device according to an embodiment of the present invention. 
FIGS. 2 to 6 are partially enlarged sectional views, respectively, of the 
same. A convey path 10 for a lead frame 40 is constituted by a 
substantially cylindrical cover 20. Only an upper plate of the cover 20 is 
shown in FIG. 1. A die bonding portion 12, a wire bonding portion 14, a 
postbonding portion 16 and a postbaking portion 18 are arranged in the 
convey path 10 along a convey direction (indicated by arrow 2) of the lead 
frame 40 in the order named. Windows 22, 24 and 26 are formed in the upper 
plate of the cover 20 so as to correspond to the portions 12, 14 and 16, 
respectively. Heater blocks 28, 30, 32 and 34 for heating the lead frame 
40 are provided to the convey path 10 to correspond to the portions 12, 
14, 16 and 18, respectively. A gas path (see a gas path 31 in FIG. 2) for 
introducing a reducing gas to the path 10 is formed in each of the heater 
blocks 28, 30, 32 and 34. The reducing gas can be obtained by, e.g., 
mixing 10% by volume of H.sub.2 gas with N.sub.2 gas. The reducing gas is 
supplied to the convey path 10 through the gas path. 
A gas introducing member 36 is arranged on the upper plate of the cover 20 
of the convey path 10 between the portions 14 and 16. Another gas 
introducing member 38 is arranged on the upper plate of the cover 20 of 
the convey path 10 to correspond to the portion 18. As shown in detail in 
FIGS. 4, 5 and 6, gas paths 37 and 39 are formed in the members 36 and 38, 
respectively. The reducing gas obtained by mixing H.sub.2 gas with N.sub.2 
gas is supplied to the convey path 10 through the gas paths 37 and 39 of 
the members 36 and 38, respectively. In this manner, the interior of the 
convey path 10 is filled with a reducing gas, e.g., N.sub.2 +10% H.sub.2. 
A collet 52 capable of clamping a semiconductor pellet (semiconductor 
element) 50 is provided at a position corresponding to the portion 12 so 
as to be capable of approaching and withdrawing from the convey path 10. 
The collet 52 can be inserted in the convey path 10 through the window 22 
in the portion 12. The pellet 50 is supplied to the convey path 10 through 
the collet 52. A capillary 60 can clamp a bonding wire 80 and is arranged 
in the vicinity of the portion 14 so as to be capable of approaching and 
withdrawing from the convey path 10. The capillary 60 can be inserted in 
the convey path 10 through the window 24 in the portion 14. The bonding 
wire 80 is supplied to the convey path by the capillary 60. The bonding 
wire 80 is made of copper such as oxygen free copper and phosphor 
deoxidized copper, or a copper alloy such as Cu-20% Au. A compressing 
member 70 for thermocompressing the bonding wire 80 to an outer lead of 
the lead frame 40 is arranged at a position to correspond to the portion 
16. The compressing member 70 can be inserted in and escape from the 
convey path 10 through the window 26 in the portion 16. 
A guide rail (not shown) extends along a direction indicated by arrow 2 on 
the bottom of the convey path 10. The lead frame 40 is conveyed along the 
direction indicated by arrow 2 on the guide rail. The lead frame 40 is 
made of copper such as oxygen free copper and phosphor deoxidized copper, 
or a copper alloy. A mount portion 46 for the semiconductor pellet and an 
outer lead 44 are formed on the lead frame 40, as shown in detail in FIG. 
7. Meanwhile, the gas path 31 is formed in the heater block 30 to receive 
the reducing gas from a supply source. The reducing gas is discharged to 
the convey path 10 through a gap 42 between the mount portion 46 for the 
semiconductor pellet and the outer lead 44 formed on the lead frame 40. 
The remaining heater blocks 28, 32 and 34 have similar structures to that 
of the heater block 30. In the heater blocks 28, 32 and 34, the reducing 
gas is introduced to the convey path 10 from the gas path 31 directly or 
through the gap 42. 
As shown in detail in FIG. 2, a burner 90 is arranged outside the cover 20 
and in the vicinity of the window 24 through which the capillary 60 
provided at the portion 14 is inserted. As shown in detail in FIG. 8, the 
burner 90 comprises an inner tube 92 and an outer tube 94 coaxially 
surrounding it. The outer tube 94 has a distal end slightly projecting 
from the inner tube 92. A gas mixture of H.sub.2 and O.sub.2 is sprayed 
from the tube 92 to form an oxyhydrogen torch 100. A lower end of the 
bonding wire 80 is heated by the torch 100 to, e.g., 1,000.degree. C. or 
higher and melted, thereby forming a ball 82. A gas mixture of O.sub.2 and 
N.sub.2 gases is discharged from a space 96 between the tubes 94 and 92 to 
form an air curtain 102 around the torch 100. As shown in FIG. 2, a 
peripheral portion of the cover 20 defining the window 24 is movable so as 
to change the opening area of the window 24. When movable portions 36 are 
actuated to decrease the opening area of the window 24, only a portion 
near a distal end of the wire 80 is surrounded by the portions 36. When 
the reducing gas is supplied to the convey path 10 through the gas path 31 
in the heater block 30, the reducing gas flows as indicated by arrow 4 
through the window 24 having a small opening area, and the space 
surrounding the lower end of the wire 80 is set in a reducing gas 
atmosphere. 
The operation of the apparatus having the above-described structure will 
now be described. As shown in FIG. 1, the lead frame 40 is conveyed on the 
guide rail (not shown) along the direction indicated by arrow 2, and 
stopped at the portion 12. The lead frame 40 is heated by the heater block 
28 to about 400.degree. C. When the collet 52 is moved downward, the 
semiconductor pellet 50 clamped by the collet 52 is guided into the convey 
path 10 through the window 22. Solder is applied by an appropriate means 
to a lower surface of the pellet 50. The pellet 50 is then mounted on the 
mount portion of the lead frame 40 through a solder layer 54. Thereafter, 
the lead frame 40 is moved along the direction indicated by arrow 2, and 
stopped at the portion 14 as shown in FIG. 2. The lead frame 40 is heated 
by the heater block 30 to about 300.degree. C. The pellet 50 on the lead 
frame 40 has an electrode pad 56 formed thereon. The pad 56 is also heated 
by the heater block 30 to about 300.degree. C. The capillary 60 is moved 
downward together with the wire 80 to an inlet port of the convey path 10 
in the vicinity of the window 24. A gas mixture of H.sub.2 and O.sub.2 
gases is sprayed from the tube 92 of the burner 90 to form the torch 100. 
A gas mixture of O.sub.2 and N.sub.2 gases is sprayed from a space 96 
between the tubes 94 and 92 to form the curtain 102 around the torch 100. 
A reducing gas obtained by mixing H.sub.2 and N.sub.2 gases is supplied to 
the convey path 10 through the gas path 31 in the heater block 30. The 
reducing gas is heated to 200.degree. C. or higher by the heater block 30. 
The movable portions 36 are moved to decrease the opening area of the 
window 24. The reducing gas flows in the convey path 10 along a direction 
indicated by arrow 4 to surround the lower end portion of the wire 80 and 
the torch 100. In this manner, in a high-temperature reducing gas 
atmosphere, the lower end portion of the wire is heated and melted by the 
torch 100 to form the ball 82. Therefore, the copper is not subjected to 
oxidation, thus preventing a bonding failure. 
The mixing ratio of H.sub.2 gas to N.sub.2 gas of the reducing gas is 
preferably selected to be 5 to 20% and 95 to 80% by volume, i.e., 1:19 to 
1:4. In order to increase the reducing power, the amount of the H.sub.2 
gas may be increased. However, when the amount of the H.sub.2 gas is 
increased to 20% or higher, an explosion may result. When the amount of 
the H.sub.2 gas is decreased below 5%, the reducing power is decreased. 
Therefore, the mixing ratio is preferably set in the range described 
above. In order to further increase the reducing power, a gas discharge 
port 48 can be provided in the vicinity of the portions 14, 16 and 18 of 
the heater blocks 30, 32 and 34, respectively, and the reducing gas can be 
supplied to the convey path 10 through each port 48. 
A gas mixture obtained by mixing the H.sub.2 and O.sub.2 gases in the 
volume ratio of 2:1 is preferably sprayed from the tube 92 to form the 
torch 100. Meanwhile, a gas mixture of the O.sub.2 and N.sub.2 gases is 
sprayed from the space between the tubes 94 and 92 to form the curtain 
102. The air curtain 102 is formed to prevent the torch 100 from being 
extinguished due to the reducing atmosphere of the portion 14. Preferably, 
the mixing ratio of O.sub.2 to N.sub.2 to the gas mixture forming the 
curtain 102 is a ratio sufficient to keep a reducing gas atmosphere and 
torch 100 in a stable state. If the amount of the O.sub.2 gas is 
excessive, the portion 14 (around the lower end portion of the wire 80) 
cannot be kept in a reducing gas atmosphere. 
After the ball 82 is formed, the capillary 60 is lowered as shown in FIG. 3 
to urge the ball 82 against the pad 56, thereby thermocompressing the wire 
80. In this case, the diameter of the bonding region of the electrode pad 
56 and the ball 82 is set to be twice or more that of the cross section of 
the wire 80. FIG. 9B is a graph of the occurrence rate of defective 
connections when the final product is subjected to a temperature cycling 
test. In FIG. 9B, the diameter D of the bonding region shown in FIG. 9A is 
plotted along the abscissa and the occurrence rate of defective 
connections is plotted along the ordinate axis. Reference symbol d denotes 
the cross section diameter of the wire 80. As is apparent from FIGS. 9A 
and 9B, when the diameter of the bonding region becomes 2.0 d or more, the 
occurrence rate of defective devices becomes substantially zero. For these 
reasons, the diameter of the bonding region must be set to 2 times or more 
that of the wire 80. 
In wire bonding, the flat end portion of the ball 82 preferably extends 
into the pad 56 to a depth of 0.4 to 3 .mu.m. Referring to FIG. 10A, 
reference symbol X denotes a depth to which the ball 82 extends into the 
pad 56 having thickness Y. FIG. 10C is a graph showing a relationship 
between the extending depth X of the ball 82 and the occurrence rate of 
defective products when the final products are subjected to the 
temperature cycling test. As apparent from FIG. 10C, when the depth X is 
0.4 .mu.m or more, the occurrence rate of defective products becomes 
substantially zero. For this reason, the flat end portion of the ball 82 
is set to extend into the pad 56 to a depth of 0.4 .mu.m or more. When the 
pad 56 comprises an aluminum layer having a thickness of 1 to 3 .mu.m and 
the wire 80 comprises a copper wire having a diameter of 25 .mu.m, a load 
of 50 to 100 g can be applied to the wire 80 so that depth X becomes 0.5 
to 2.5 .mu.m. 
The bonding wire made of copper or a copper alloy has a hardness about 
twice that of a gold wire. Therefore, if the pad 56 is thin, cracking 
tends to occur in the surface of the pad 56. FIG. 11 is a graph showing a 
relationship between the thickness of the pad and the occurrence rate of 
defective products. In FIG. 11, the thickness of the pad 56 is plotted 
along the abscissa and the occurrence rate of defective products is 
plotted along the ordinate axis. As apparent from FIG. 11, when the 
thickness of the pad 56 is set to be 1 .mu.m or more, the occurrence rate 
of defective products can be decreased to substantially zero. 
Subsequently, the wire 80 is fused by the oxyhydrogen torch of the burner 
90 at a predetermined length as shown in FIG. 3. In this case, balls 82 
and 84 are formed at distal ends of a wire 81 connected to the pad 56 and 
the wire 80 left in the capillary 60, respectively. The wires 80 and 81 
are surrounded by the reducing gas during this fusing. 
The wire 81 is bent by an appropriate means (not shown) to a side of the 
outer lead 44 of the lead frame 40 as shown in FIG. 4. The lead frame 40 
is then moved from the portion 14 to the portion 16. In this case, the 
temperature of the reducing gas in the convey path 10 is kept at 
200.degree. to 300.degree. C., thereby keeping the wire 81 in the reducing 
atmosphere. 
The lead frame is then stopped at the portion 16 as shown in FIG. 5. The 
heater block 32 heats the lead frame 40 to about 300.degree. C. or higher. 
The compressing member 70 is moved downward and inserted in the convey 
path 10 through the window 26. The member 70 thermocompresses the ball 84 
of the wire 81 against the outer lead 44 made of copper or copper alloy. 
When the diameter of the wire 81 is 25 .mu.m, a load of 300 to 500 g is 
preferably applied thereto so that the ball 84 extends into the outer lead 
44 to a depth of 20 to 50 .mu.m (indicated by Z in FIG. 10B) as shown in 
FIG. 10B. By thermocompressing the ball 84 of the wire 81 to the outer 
lead to the depth as described, the occurrence rate of defective products 
can be reduced to substantially zero. The wire 81, the ball 84 and the 
member 70 are surrounded by the reducing gas during this postbonding. 
Thereafter, as shown in FIG. 6, the lead frame 40 is conveyed to the 
portion 18 and heated by the heater block 34 to about 300.degree. C. or 
higher, thereby being baked. In this case, the reducing gas is supplied to 
the convey path 10 through the gas path 35 in the heater block 34, and 
simultaneously the reducing gas is blown into the convey path 10 through 
the path 39 in the gas introducing member 38. In this manner, the 
semiconductor pellet 50, the wire 81 and lead frame 40 are also kept in 
the reducing atmosphere at the portion 18. 
In this manner, the bonding wire 81 is looped between the pad 56 of the 
pellet 50 and the outer lead 44 of the lead frame 40 as shown in FIG. 7. 
Although a single wire is shown in FIGS. 1 to 6, two bonding wires are 
looped in practice as shown in FIG. 7. According to the present invention, 
a bonding wire made of copper or a copper alloy is used so that various 
above-mentioned drawbacks inherent in bonding using a gold wire can be 
prevented. In addition, the bonding wire can be securely connected, and 
degradation in electrical characteristics at the connecting portion can be 
decreased to a minimum. The bonding wire can be fused not only by using 
the oxyhydrogen torch as in the embodiment described above but also by 
using a laser or electric torch. The ball can be formed at each of the cut 
ends of the bonding wire not only by the ball to ball method but also by 
cutting the bonding wire by a wedge of the capillary. 
A high-temperature exposure test was performed for a semiconductor device 
manufactured in the manner described above. The results of the test are 
shown in FIG. 12. FIG. 12 is a graph showing the occurrence rate of 
defective products according to the embodiment of the present invention 
together with that according to a conventional apparatus. In FIG. 12, the 
exposure time is plotted along the abscissa and the occurrence rate of 
defective products is plotted along the ordinate axis. In the conventional 
method, the bonding wire is made of gold and the diameter of the bonding 
region of the ball and the electrode pad is 1/2 that of the cross section 
of the bonding wire. The other conditions are the same as in the 
embodiment of the present invention. With the conventional apparatus, 25% 
of the final products became defective after 100 hours, and substantially 
50% became defective after 200 hours. In contrast to this, in the 
embodiment of the present invention, the occurrence rate of defective 
products was substantially zero even after 200 hours. 
The temperature cycling test was performed for the semiconductor devices 
manufactured by the apparatus of the embodiment of the present invention 
and the conventional method. Also, the mechanical strength test was 
performed for the looped bonding wire of the devices manufactured by both 
apparatuses. In the temperature cycling test, the semiconductor device 
according to the preset invention exhibited a performance considerably 
superior to that of the conventional apparatus as a comparative example. 
In the mechanical strength (tensile strength) test, the bonding wire made 
of a copper alloy according to the present invention exhibited a strength 
2 to 2.5 times that of the bonding wire made of gold as a comparative 
example.