CONTROLLED RELEASE FERTILIZER COATINGS USING HYDROPHILIC BLENDS

Coated fertilizer compositions may contain a fertilizer granule; two or more polyurethane layers on the fertilizer granule, wherein the polyurethane layer is reaction product of: an isocyanate component including one or more isocyanate compound, and an isocyanate-reactive component including a polyol component containing: (a) from 65 wt % to 80 wt % of a hydrophilic polyether polyol having an OH number in a range of 220 mg KOH/g to 400 mg KOH/g, wherein ethylene oxide is from 90 wt % to 100 wt % of a total alkylene oxide content of the hydrophilic polyether polyol, hydroxyl functionality from 2 to 3, and (b) from 20 wt % to 35 wt % of a low EW polyol having a formula of CH2OHC(R1)(R2)CH2OH, wherein R1 is CH2OH or OH, and R2 is H or a C1 to C3 alkyl group; the isocyanate index being from 120 to 160; and one or more wax layers on the fertilizer granule including a polyolefin wax.

FIELD

Embodiments relate to coated fertilizer compositions having controlled dissolution and release profiles.

INTRODUCTION

Coatings on fertilizer have been used for controlled release that increases fertilizer efficacy, reduces the quantity and frequency of applications, and lowers labor costs. This in turn lowers the risk of root burn from overdosage of fertilizer, as well as protects against nutrient loss from leaching and denitrification processes. However, defects in coatings can lead to performance irregularity and premature coating degradation. Coating degradation in turn can lead to uncontrolled release, scheduling disruptions, and plant damage from erratic concentration gradients.

SUMMARY

Coated fertilizer compositions may contain a fertilizer granule; two or more polyurethane layers on the fertilizer granule, wherein the polyurethane layer is reaction product of: an isocyanate component including one or more isocyanate compound, and an isocyanate-reactive component including a polyol component containing: (a) from 65 wt % to 80 wt % of a hydrophilic polyether polyol having an OH number in a range of 220 mg KOH/g to 400 mg KOH/g, wherein ethylene oxide is from 90 wt % to 100 wt % of a total alkylene oxide content of the hydrophilic polyether polyol, hydroxyl functionality from 2 to 3, and (b) from 20 wt % to 35 wt % of a low EW polyol having a formula of CH2OHC(R1)(R2)CH2OH, wherein R1 is CH2OH or OH, and R2 is H or a C1 to C3 alkyl group; the isocyanate index being from 120 to 160; and one or more wax layers on the fertilizer granule including a polyolefin wax.

DETAILED DESCRIPTION

Embodiments relate to coated fertilizer compositions having one or more layers, which provide a slowed release profile and controlled dissolution when compared with uncoated fertilizer. Fertilizer coatings may be multilayered in some cases and a mixture of one or more polyurethane layers having one or more wax layers interspersed therebetween. Coated fertilizer compositions may include one or more polyurethane layers produced by reacting an isocyanate component with an isocyanate-reactive component containing a mixture of hydrophilic polyether polyol and a low equivalent weight (EW) polyol.

Coated fertilizer compositions disclosed herein utilize hydrophilic polyether polyols and may provide enhanced fertilizer release profiles when compared to similar formulations utilizing hydrophobic polyols such as castor oil or propoxylated polyols. While hydrophilic polyether polyols are typically avoided as associated with erratic release rates, the incorporation of a low EW polyol in the isocyanate-reactive component may unexpectedly result in a substantial increase of the duration of controlled release of the fertilizer. Particularly, the use of an isocyanate-reactive component containing a polyol component containing a combination of low EW polyols with hydrophilic polyether polyols provides controlled release of fertilizer over longer time scales when compared to relatively hydrophobic polyols such as PO-based polyols that result in poor controlled release performance. Coated fertilizer compositions disclosed herein may be easier to handle and have a release period that can extend up to weeks or months after application.

Coated fertilizer compositions may include one or more polyurethane layers having interspersed layers of wax that enable staged and consistent fertilizer release. Coated fertilizer compositions may include a polyurethane (PU) layer as the most internal layer contacting the granule and a PU layer as the most external layer, with alternating wax layers between each PU layer. For example, if the number of PU layers=x, then number of wax layers=(x−1). Coated fertilizer compositions may have total number of layers ranging from 3 to 9. The sequence of layers in a coated fertilizer composition may include: a first PU layer, a first wax layer, a second PU layer, a second wax layer, a third PU layer, and the like. Successive layers may coat the underlying fertilizer granule or sublayers, where coating is regarding as covering from 90% to 100% of the surface area of the underlying surface.

The coated fertilizer compositions disclosed herein include one or more fertilizers provided in granular form. Suitable fertilizers include urea, nitrogen, phosphorus, or potassium sources such as ammonium nitrate, ammonium sulfate, ammonium sulfate nitrate, calcium nitrate, calcium ammonium nitrate, urea-formaldehyde, monoammonium phosphate, diammonium phosphate, polyphosphate compounds, phosphate rock, single superphosphate, triple super phosphate, potassium nitrate, potassium chloride, potassium sulfate, or combinations thereof, for instance. In some embodiments, the fertilizer can be granular urea. For instance, the fertilizer granules can have a nitrogen-phosphorus-potassium ratio of 46-0-0. The amounts of nitrogen, phosphorus, or potassium sources included in the fertilizer granules can be varied based on the intended end use and can be 0 to 60 wt % for each component, based on the total weight of the fertilizer granule.

Fertilizer granules can have any shape or size desired for their intended use. In some embodiments the fertilizer granules are substantially spherical. The fertilizer granules can have an average particle diameter of 0.5 mm to 6.0 mm, 1.0 mm to 5.5 mm, or 1.5 mm to 5.0 mm. In some embodiments at least 90% by weight of the fertilizer granules have a particle diameter of 2.0 mm to 4.0 mm. Particle diameter can be determined according to “Size Analysis—Sieve Method” IFDC S-107 issued by International Fertilizer Development Center (IFDC) which is a common and internationally approved method used to determine fertilizer particle size.

Coated fertilizer composition may include one or more polyurethane layers generated by reacting the isocyanate component with an isocyanate-reactive component containing a mixture of hydrophilic polyether polyol and a low EW polyol. Isocyanate components can include at least one compound having an isocyanate group. Isocyanate components may be the same or different in coated fertilizer compositions incorporating multiple PU layers.

The isocyanate component may include one or more isocyanates and polyisocyanates having an average of greater than 1.0 isocyanate groups per molecule. The isocyanate components may contain moieties that are aliphatic, cycloaliphatic, alicyclic, arylaliphatic, aromatic, and/or derivatives thereof. Examples of compounds suitable for use in isocyanate components include polymethylene polyphenylisocyanate, toluene 2,4-/2,6-diisocyanate (TDI), methylenediphenyl diisocyanate (MDI), polymeric MDI, and the like.

Isocyanates may have an average isocyanate functionality from 1 to 5, 1.5 to 5, 2 to 5, or 3 to 5. The isocyanate can have an isocyanate equivalent weight (EW) in a range of 80 g/eq to 200 g/eq, 90 g/eq to 175 g/eq, or 100 to 175 g/eq. The isocyanate can have an isocyanate content based on a total weight of the isocyanate in a range of 20 wt % to 45 wt %, 25 wt % to 45 wt %, or 25 wt % to 40 wt %.

Polyurethane layers may have an isocyanate index defined as the molar stoichiometric excess of isocyanate moieties in a reaction mixture with respect to the number of moles of isocyanate-reactive units (active hydrogens available for reaction with the isocyanate moiety), multiplied by 100. An isocyanate index of 100 means that there is no stoichiometric excess, such that there is 1.0 mole of isocyanate groups per 1.0 mole of isocyanate-reactive groups, multiplied by 100. Isocyanate components may have an isocyanate index in a range of from 110 to 170, 120 to 160, or 125 to 155.

Coated fertilizer compositions may include one or more polyurethane layers produced from a reaction of an isocyanate component and an isocyanate-reactive component containing a polyol component containing a mixture of one or more hydrophilic polyether polyols and one or more low EW polyols having, respectively, at least one isocyanate-reactive hydrogen atom group, such as a hydroxyl group and/or an amine group. The polyol component may consist essentially of one or more hydrophilic polyether polyols and one or more low EW polyols, where “consist essentially” or “consisting essentially” means that all polyol species within the isocyanate-reactive component are limited to only those polyols and amounts described, but that other components that do not materially affect the overall isocyanate index and/or average OH number.

Hydrophilic polyether polyols disclosed herein are produced by polymerization of ethylene oxide with an initiator, and optionally another alkylene oxide, where ethylene oxide is 90 wt % or more of the total alkylene oxide. In some cases, ethylene oxide may be a percent by weight of the hydrophilic polyether polyol (wt %) in a range from 90 wt % to 100 wt %, or 95 wt % to 100 wt %. Initiators include molecules having a hydroxyl functionality in a range of 2 to 8, such as between 2 and 4. Suitable initiators include water, glycerol, ethylene glycol, propylene glycol, trimethylolpropane, pentaerythritol, and combinations thereof. Examples of other alkylene oxides that may be utilized to prepare hydrophilic polyether polyols include propylene oxide, butylene oxide, and combinations thereof. Hydrophilic polyether polyols can be prepared according to known method and may include commercial examples sold under the trade names VORANOL™ and CARBOWAX™, available from The Dow Chemical Company.

Isocyanate-reactive components may include a polyol component containing a mixture of hydrophilic polyether polyols. The hydrophilic polyether polyols disclosed herein may have a hydroxyl functionality of 2 to 4, or 2 to 3. Hydrophilic polyether polyols may have an average hydroxyl number (OH number) as determined according to ASTM D4274-21 from 220 mg KOH/g to 400 mg KOH/g, 220 mg KOH/g to 350 mg KOH/g, or 240 mg KOH/g to 350 mg KOH/g. Hydrophilic polyether polyols may have a weight average molecular weight in the range of 200 Da to 1000 Da, 300 Da to 1000 Da, 300 Da to 800 Da, or 220 Da to 760 Da.

Isocyanate-reactive components may include a polyol component containing a mixture of low EW polyols. Low EW polyols may have a formula of CH2OHC(R1)(R2)CH2OH, wherein R1 is CH2OH or OH, and R2 is H or a C1 to C3 alkyl group. Suitable low EW polyols include C3 to C6 polyols having 2 to 3 hydroxyl functionalities such as glycerol and trimethoylpropane.

Low EW polyols may have an equivalent weight of 110 or less, 100 or less, or 60 or less. Low EW polyols may have an average hydroxyl number as determined according to ASTM D4274-21 of 500 mg KOH/g or more, 750 mg KOH/g or more, or 900 mg KOH/g or more.

Isocyanate-reactive components may include one or more hydrophilic polyether polyols at a percent by weight of the isocyanate-reactive component at 65 wt % to 85 wt %, 65 wt % to 80 wt %, 67 wt % to 80 wt %, 65 wt % to 75 wt %, or 67 wt % to 75 wt %. Isocyanate-reactive components may include one or more low EW polyols at a percent by weight of the isocyanate-reactive component ranging from 15 wt % to 35 wt %, 20 wt % to 35 wt %, 20 wt % to 33 wt %, 15 wt % to 25 wt %, or 15 wt % to 33 wt %. In some embodiments, the isocyanate-reactive component may include a mass ratio of hydrophilic polyether polyols to low EW polyols in a range of 65:35 to 85:15, 67:33 to 85:15, 67:33 to 80:20, or 75:25 to 80:20.

Isocyanate-reactive components disclosed herein may include one or more tertiary amines. Suitable tertiary amines include triethanolamine, triisopropanolamine, N-methyl-diethanolamine, N-ethyl-diethanolamine, and N,N-dimethyl-ethanolamine. The isocyanate-reactive component may further include a tertiary amine at a percent by weight (wt %) of 15 wt % or less, 10 wt % or less, or 8 wt % or less. The isocyanate-reactive component may further include a tertiary amine at a percent by weight (wt %) in a range from 1 wt % to 20 wt %, 1 wt % to 15 wt %, or 5 wt % to 15 wt %. In some cases, the isocyanate-reactive component consists essentially of from 5 wt % to 15 wt % tertiary amine, 15 wt % to 35 wt % low EW polyol, and 50 wt % to 80 wt % hydrophilic polyether polyol.

Coated fertilizer compositions may include one or more wax layers prepared from one or more waxes, and the waxes used in each layer may be the same or different. Suitable waxes include polyolefin waxes having carbon numbers ranging from C20 to C35, and can include alpha olefin waxes, natural and synthetic waxes, and the like.

Coated fertilizer compositions may include one or more polyurethane layers in which the polyurethane is included at a percent by weight (wt %) of the coated fertilizer composition in a range from 1.5 wt % to 4 wt %, 2 wt % to 4 wt %, or 2 wt % to 3.5 wt %. Coated fertilizer compositions may include one or more wax layers in which the wax is included at a percent by weight (wt %) of the coated fertilizer composition in a range from 0.2 wt % to 1 wt %, 0.2 wt % to 0.9 wt %, or 0.3 wt % to 0.7 wt %.

Coated fertilizer compositions disclosed herein may release less than 30%, less than 40%, or less than 45% of the total weight of fertilizer granules after 28 days in contact with water. Coated fertilizer compositions disclosed herein may release less than 10%, less than 15%, or less than 20% of the total weight of fertilizer granules after 14 days in contact with water.

Coated fertilizer granule compositions can be made utilizing known equipment, conditions, and components, such as a drum coater with the application of heat. Methods of preparing may include providing fertilizer granules to a drum coater, forming a first polyurethane layer on the fertilizer granule; forming a first hydrophobic layer on the first polyurethane layer; and forming the second polyurethane layer on the first hydrophobic layer. The layering steps may be repeated as many times as desired. Formation of one or more of the polyurethane layers may include dividing the isocyanate component and/or isocyanate-reactive component into portions that are added at various stages of the coating process. As an example, a first portion of the isocyanate-reactive component may be added to the drum coater to coat the fertilizer granules, followed by the addition of the isocyanate component, and then the subsequent addition of the second portion of the isocyanate-reactive component to the mixture.

EXAMPLES

The following examples are provided to illustrate the embodiments of the invention, but are not intended to limit the scope thereof. Table 1 provides the materials used in the following examples.

Materials used in the examples

Ingredient
Description

of 3 and an average OH number of 270 mg KOH/g.

average OH number of 281 KOH/g

Polyol
average OH number of 238 KOH/g

BDO
1,4-Butanediol, OH number of 1246 mg KOH/g

TMP
Trimethylolpropane, OH number of 1255 mg KOH/g

Glycerol
Glycerol, OH number of 1827 mg KOH/g

number of 1121 mg KOH/g

In the following examples, urea fertilizer granules were coated with 5 alternating PU (0.9 wt %+0.9 wt %+0.9 wt %=2.7 wt % total) and wax layers (0.25 wt %+0.25 wt %=0.5 wt % total) using a roller drum coater and a layer-by-layer component coating process as follows. Fertilizer (0.5 kg to 2.0 kg) was first dried in the oven at 80° C. for at least 6 hours as per standard industry practice, before the coating process has been planned to start. Fertilizer was then transferred to a drum coater heated to 80° C. To produce the coated fertilizer compositions, each coating component was added and allowed to coat the particles for 30 seconds before subsequent component additions. The order of addition was as follows: a first portion (40%) of isocyanate, the isocyanate-reactive components, the remaining 60% of the pre-weighed isocyanate portion is added, and followed by the wax component. The process was repeated to form 5 coating layers: PU-wax-PU-wax-PU. The coated fertilizer compositions were then allowed to cool and aged for a week prior to release testing.

For release tests, 10 grams of each sample were placed into respective containers with 100 mL of deionized water. Then, at 14 days and at 28 days from contact with water, refractive index measurements were taken to determine weight percent of released fertilizer (urea). For determining refractive index, an initial calibration curve was created by measuring the refractive index, using a refractometer, of aqueous, uncoated urea (SUPERU 46-0-0; 2-4 mm uncoated urea prills) solutions with varying concentrations. The equation was solved for the wt % of dissolved urea as follows:

where X=wt % released urea. The calibration curve, which plotted urea wt % in deionized water vs refractive index, had the curve had a best fit line: y=0.0013x+1.333, and R2=0.9997.

Layer Formulations for Example 1

Polyurethane layers

First Addition (g)

glycerol

glycerol

second

Wax layers

Overall percentage by weight

Fertilizer Release Testing

Cumulative Coating Formulations

The comparative examples CE1-8 show poor release performance of urea fertilizer relative to the extended release times of the examples IE1-IE3. Surprisingly, the hydrophilic blends used to form the polyurethane layers of the coated fertilizers provides enhanced control over fertilizer release time, as compared to hydrophobic polyurethane coatings, such as the propylene oxide based formulation used in CE4.

While the foregoing is directed to exemplary embodiments, other and further embodiments may be devised without departing from the basic scope thereof, and the scope thereof is determined by the claims that follow.