Arc tube electrodeless high pressure sodium lamp

Electrodeless arc tubes for high pressure sodium discharge lamps comprise a substantially tubular, translucent body formed from a material comprising sintered polycrystalline alumina. The body has an inside diameter and an outside diameter and a given length. A fill comprising sodium and xenon are loaded within the body. At least one end-seal is provided for the body, the end-seal comprising a first alumina disc sealed within the inside diameter by compression, the first disc being spaced inwardly from an end of the body and having a substantially centrally located aperture therein. A second alumina disc seals the aperture, the second disc being bonded to the first disc and to the inner wall of the body by a sealing frit.

TECHNICAL FIELD 
This invention relates to arc tubes for discharge lamps and more 
particularly to arc tubes for an electrodeless, high pressure sodium lamp. 
BACKGROUND ART 
High pressure sodium lamps employing polycrystalline alumina arc tubes 
having tungsten electrodes at either end thereof are known, see, for 
example, U.S. Pat. No. 4,545,799. Such electrodes often employ electron 
emissive materials such as barium, strontium, calcium, yttrium, tungsten 
or mixtures thereof. During lamp operation these materials are sputtered 
from the electrodes and deposit on the interior of the arc tube envelope, 
leaving a black coating thereon which can increase the emissivity of the 
arc tube and decrease the wall temperature. These effects lead to a 
lowering of the lamp efficacy. Additionally, the use of electrodes can 
lead to cracking of the material due to the expansion differences between 
the metal and ceramic. 
DISCLOSURE OF INVENTION 
It is, therefore, an object of the invention to obviate the disadvantages 
of the prior art. 
It is another object of the invention to enhance the operation of high 
pressure sodium lamps. 
Yet another object of the invention is an increase in efficacy of high 
pressure sodium lamps. 
Still another object of the invention is the simplification of arc tube 
construction and the elimination of thermal cracking due to differences in 
thermal expansion. 
These objects are accomplished, in one aspect of the invention, by the 
provision of an electrodeless arc tube for a high pressure sodium 
discharge lamp comprising: a substantially tubular, translucent body 
formed from a material comprising sintered polycrystalline alumina, said 
body having an inside diameter and an outside diameter and a given length; 
a fill comprising sodium and xenon within said body; and at least one 
end-seal for said body, said end-seal comprising a first alumina disc 
sealed within said inside diameter by compression, said first disc being 
spaced inwardly from an end of said body and having a substantially 
centrally located aperture therein; and a second alumina disc sealing said 
aperture, said second disc being bonded to said first disc and to the 
inner wall of said body by a sealing frit. 
The elimination of the electrodes removes the deleterious materials from 
the interior of the arc tube resulting in greater transparency for longer 
periods of time, thus increasing the efficacy of the lamps employing the 
same. Also eliminated is any thermal mismatch.

BEST MODE FOR CARRYING OUT THE INVENTION 
For a better understanding of the present invention, together with other 
and further objects, advantages and capabilities thereof; reference is 
made to the following disclosure and appended claims taken in conjunction 
with the above-described drawings. 
Referring now to the drawings with greater particularity, there is shown in 
FIG. 1 an electrodeless arc tube 10 comprised of a substantially tubular, 
translucent body 12 formed from a material comprising sintered 
polycrystalline alumina, as is known in the art. This material can include 
small quantities of numerous additives such as magnesia, yttria, zirconia 
and hafnia for the control of grain growth or to prevent undesired phases 
from forming in the material. In a preferred embodiment of the invention, 
body 12 comprised alumina containing 500 ppm magnesia and 350 ppm yttria. 
Average grain size was between 25-30 .mu.m. The total transmittance was 
95-96% and the in-line transmission was 5-6%. 
The body 12 has an inside diameter and an outside diameter and a given 
length. In a preferred embodiment, the body has an inner diameter of 4.0 
mm; an outside diameter of 5.2 mm and a cavity length of 30.0 mm. At least 
one end of the body 12 is closed by an end-seal 14 which comprises a first 
alumina disc 16 sealed within the body by a compression or fritless seal, 
as discussed in the above-cited U.S. Pat. No. 4,545,799. The first disc 16 
is spaced inwardly from an end 18 of the body 12 to form a recess and has 
a substantially centrally located aperture 20 therein. The aperture 20 is 
employed as the dosing or fill aperture whereby the fill 22 can be 
inserted into the arc tube before final sealing. A second alumina disc 24 
is inserted into the recess formed by first disc 16 and the end 18 of body 
12 and is sealed therein by a sealing frit 26 which can be in the form of 
a ring positioned between the outside surface 28 of second disc 24 and the 
inner surface 30 of body 12. Alternatively, the sealing material can be 
placed beneath the second disc 24, as is shown in FIG. 2. 
The fill 22 is at least sodium and preferably comprises a sodium amalgam. 
For the arc tube having the dimensions described above it is preferred 
that the fill comprise 2.3 mg of the sodium amalgam with a weight ratio of 
sodium to mercury of 20:80. The gaseous portion of the fill comprises 
xenon at 25 torr. Excessive fill weights are to be avoided as they can 
cause problems in coupling with a high frequency power source. 
While any of the known sealing frits available for use with ceramic tubes 
can be employed the preferred frit is known as PF and comprises 45.6 
weight percent Al.sub.2 O.sub.3 ; 1.6 weight percent B.sub.2 O.sub.3 ; 5.2 
weight percent MgO; 8.6 weight percent BaO; and 39 weight percent CaO. 
When the PF frit is used the sealing furnace is preferably a graphite 
element, carbon-fiber-insulation lined, water-cooled, cold wall furnace 
with a vacuum system containing xenon gas fill provisions. The 
tube-disc-frit assembly is loaded in a copper tray, placed in the furnace 
and pumped to &lt;10.sup.-5 torr. The heating cycle employed for sealing with 
the PF frit is shown in FIG. 3. Other frits would require different 
sealing times and temperatures. 
If desired, a solid first disc 16a, such as is shown in FIG. 2, can be 
employed to seal one of the ends, the opposite end requiring an apertured 
disc 16 to allow insertion of the fill material. 
The arc tubes are energized by placement in a high energy field. A suitable 
arrangement is shown in U.S. Pat. No. 5,070,277 wherein the operational 
frequency is 915 MHz. Of course, other frequencies are useable; e.g., 
those prefered are within allowed International Scientific and Medical 
(ISM) bands and in particular the band centered about 2.45 GHz. 
Arc tubes operated thusly showed strong sodium emissions, indicating that a 
complete discharge and the light emissions of high pressure sodium lamps 
were achieved. Operation for several hours showed no end blackening which 
provides a major advantage over conventional electroded high pressure 
sodium lamps. As a result of the no-blackening, the lumen output, efficacy 
and life of the electrodeless lamps can be higher than those of the 
electroded counterparts. 
While them have been shown and described what are at present considered the 
preferred embodiments of the invention, it will be apparent to those 
skilled in the art that various changes and modifications can be made 
herein without departing from the scope of the invention as defined by the 
appended claims.