Method for manufacturing semiconductor device

Described is a method for manufacturing a semiconductor device. A mask is formed over an insulating film and the mask is reduced in size. An insulating film having a projection is formed using the mask reduced in size, and a transistor whose channel length is reduced is formed using the insulating film having a projection. Further, in manufacturing the transistor, a planarization process is performed on a surface of a gate insulating film which overlaps with a top surface of a fine projection. Thus, the transistor can operate at high speed and the reliability can be improved. In addition, the insulating film is processed into a shape having a projection, whereby a source electrode and a drain electrode can be formed in a self-aligned manner.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method for manufacturing a semiconductor device. Note that semiconductor devices herein refer to general elements and devices which function by utilizing semiconductor characteristics.

2. Description of the Related Art

As a material having semiconductor characteristics applicable to thin film transistors, a metal oxide has attracted attention, and thin film transistors in which a channel formation region is formed using such a metal oxide having semiconductor characteristics are known (for example, see Patent Documents 1 and 2).

Further, in accordance with advance in performance of a semiconductor device, high-speed operation of a transistor has been required. For example, a technique has been reported in which high-speed operation is achieved by shortening of a channel length of a transistor (for example, see Patent Document 3).

REFERENCE

[Patent Document 1] Japanese Published Patent Application No. 2007-123861[Patent Document 2] Japanese Published Patent Application No. 2007-96055[Patent Document 3] Japanese Published Patent Application No. 2006-332603

SUMMARY OF THE INVENTION

An object of one embodiment of the present invention is to provide a semiconductor device which is capable of high-speed operation and has high reliability with the use of a transistor using an oxide semiconductor. Another object of one embodiment of the present invention is to provide a method for manufacturing the semiconductor device with high yield.

According to one embodiment of the disclosed invention, a mask is formed over an insulating film and the mask is reduced in size. An insulating film having a projection is formed using the mask reduced in size, and a transistor whose channel length is reduced is formed using the insulating film having a projection.

According to another embodiment of the disclosed invention, a planarization process is performed on at least part of a gate insulating film which is in contact with an oxide semiconductor film and provided over a top surface of the projection of the insulating film.

According to another embodiment of the disclosed invention, an insulating film is processed into a shape having a projection, a conductive film covering the projection is formed, and a planarization process is performed on the conductive film, whereby a source electrode and a drain electrode are formed in a self-aligned manner on the right and left of the projection.

Another embodiment of the disclosed invention is a method for manufacturing a semiconductor device including the steps of forming a conductive film over a first insulating film; forming a first mask over the conductive film; performing a slimming process by a plasma treatment on the first mask to form a second mask; performing an etching process on the first insulating film and the conductive film using the second mask to form a second insulating film having a projection and to form a gate electrode over a top surface of the projection of the second insulating film; forming a gate insulating film over the second insulating film and the gate electrode so as to cover the gate electrode; performing a planarization process on a surface of the gate insulating film which overlaps with the top surface of the projection of the second insulating film and then forming an oxide semiconductor film over the gate insulating film; and forming a source electrode and a drain electrode over the oxide semiconductor film so as not to overlap with the top surface of the projection of the second insulating film.

Another embodiment of the disclosed invention is a method for manufacturing a semiconductor device including the steps of forming a conductive film over a first insulating film; forming a first mask over the conductive film; performing a slimming process by a plasma treatment on the first mask to form a second mask; performing an etching process on the first insulating film and the conductive film using the second mask to form a second insulating film having a projection and to form a gate electrode over a top surface of the projection of the second insulating film; forming a gate insulating film over the second insulating film and the gate electrode so as to cover the gate electrode; forming a source electrode and a drain electrode over the gate insulating film so as not to overlap with the top surface of the projection of the second insulating film; performing a planarization process on part of a surface of the gate insulating film which overlaps with the top surface of the projection of the second insulating film; and forming an oxide semiconductor film over the gate insulating film so as to cover the source electrode and the drain electrode.

As the above plasma treatment, an ashing process can be used.

As the above planarization process, at least one of chemical mechanical polishing treatment and plasma treatment can be used.

As a method for forming the above source electrode and the above drain electrode, at least one of an etching process and chemical mechanical polishing treatment can be used.

According to another embodiment of the disclosed invention, a channel length of a transistor using an oxide semiconductor film can be reduced. Thus, high-speed operation of the transistor can be achieved.

According to another embodiment of the disclosed invention, a channel region of an oxide semiconductor film is formed over a gate insulating film which is planarized. Thus, high-speed operation of a transistor can be achieved.

According to another embodiment of the disclosed invention, an insulating film having a projection is used, whereby a source electrode and a drain electrode are formed in a self-aligned manner. Accordingly, misalignment is not caused in forming the source electrode and the drain electrode, so that a channel length can be reduced. Thus, a highly reliable semiconductor device can be manufactured, and yield and productivity can be improved.

DETAILED DESCRIPTION OF THE INVENTION

Note that the position, the size, the range, or the like of each structure illustrated in drawings and the like is not accurately represented in some cases for easy understanding. Therefore, the disclosed invention is not necessarily limited to the position, size, range, or the like as disclosed in the drawings and the like.

In this specification, ordinal numbers such as “first”, “second”, and “third” are used in order to avoid confusion among components, and the terms do not limit the components numerically.

Note that in this specification, the root-mean-square (RMS) roughness is obtained by three-dimensionally expanding the RMS roughness of a cross section curve so as to be able to apply it to the measurement surface. The RMS is expressed as the square root of the average value of squares of deviations from a reference surface to a specific surface, and can be obtained by the following formula.

Note that the measurement surface is a surface which is shown by all the measurement data, and is represented by the following formula.
Z=F(X,Y)   [Formula 2]

The specific surface is a surface which is an object of roughness measurement, and is a rectangular region which is surrounded by four points represented by the coordinates (X1, Y1), (X1, Y2), (X2, Y1), and (X2, Y2). The area of the specific surface when the specific surface is flat ideally is denoted by S0. Note that S0is obtained by the following formula.
S0=|X2−X1|·|Y2−Y1|  [Formula 3]

In addition, the reference surface refers to a surface parallel to an X-Y surface at the average height of the specific surface. In short, when the average value of the height of the specific surface is denoted by Z0, the height of the reference surface is also denoted by Z0. Note that Z0can be obtained by the following formula.

Note that in this specification, the root-mean-square (RMS) roughness is calculated in a region of 10 nm×10 nm, preferably 100 nm×100 nm, more preferably 1 μm×1 μm from an AFM image obtained using an atomic force microscope (AFM).

In this embodiment, an example of a method for manufacturing a semiconductor device will be described with reference toFIGS. 1A to 1C,FIGS. 2Ato2E,FIGS. 3A to 3E, andFIGS. 4A to 4C.

A transistor400which is an example of a semiconductor device is illustrated inFIGS. 1A to 1C.FIG. 1Ais a top view of the transistor400.FIG. 1Bis a cross-sectional view taken along line A-B ofFIG. 1A.FIG. 1Cis a cross-sectional view taken along line C-D ofFIG. 1A. The transistor400illustrated inFIG. 1Bincludes an insulating film101having a projection over a substrate500; a gate electrode111formed over a top surface of the projection of the insulating film101; a gate insulating film120formed so as to cover the gate electrode111; an oxide semiconductor film140formed over the gate insulating film120; a source or drain electrode130a;and a source or drain electrode130b.

In the transistor400illustrated inFIGS. 1A to 1C, it is preferable that the oxide semiconductor film140be highly purified by sufficient removal of an impurity such as hydrogen and sufficient supply of oxygen. Specifically, for example, the hydrogen concentration of the oxide semiconductor film140is less than or equal to 5×1019atoms/cm3, preferably less than or equal to 5×1018atoms/cm3, and more preferably less than or equal to 5×1017atoms/cm3. Note that the hydrogen concentration in the oxide semiconductor film140is measured by secondary ion mass spectroscopy (SIMS). A carrier concentration which is less than 1×1012/cm3, preferably less than 1×1011/cm3, and more preferably less than 1.45×1010/cm3is obtained in the oxide semiconductor film140which is highly purified by sufficiently reducing the hydrogen concentration in such a manner and in which defect levels in an energy gap caused by oxygen deficiency are reduced by sufficient supply of oxygen. For example, the off-state current (per unit channel width (1 μm), here) at room temperature (25° C.) is lower than or equal to 100 zA (1 zA (zeptoampere) is 1×10−21A), preferably lower than or equal to 10 zA. In this manner, with the use of an oxide semiconductor which is made to be an i-type (intrinsic) oxide semiconductor or a substantially i-type oxide semiconductor, the transistor400which has extremely favorable off-state current characteristics can be obtained.

Further, the oxide semiconductor film140is preferably a film from which impurities such as an alkali metal and an alkaline earth metal are sufficiently removed. For example, the sodium concentration of the oxide semiconductor film140is less than or equal to 5×1016atoms/cm3, preferably less than or equal to 1×1016atoms/cm3, more preferably less than or equal to 1×1015atoms/cm3. The lithium concentration of the oxide semiconductor film140is less than or equal to 5×1015atoms/cm3, preferably less than or equal to 1×1015atoms/cm3. The potassium concentration of the oxide semiconductor film140is less than or equal to 5×1015atoms/cm3, preferably less than or equal to 1×1015atoms/cm3. Note that the sodium concentration, the lithium concentration, and the potassium concentration of the oxide semiconductor film140are measured by secondary ion mass spectroscopy (SIMS).

Note that it has been pointed out that an oxide semiconductor is insensitive to impurities, and there is no problem when a considerable amount of metal impurities is contained in the film; therefore, soda-lime glass which contains a large amount of alkali metal such as sodium and is inexpensive can also be used (Kamiya, Nomura, and Hosono, “Carrier Transport Properties and Electronic Structures of Amorphous Oxide Semiconductors: The present status”,KOTAI BUTSURI(SOLID STATE PHYSICS), 2009, Vol. 44, pp. 621-633). But such consideration is not appropriate. Alkali metal is not an element included in an oxide semiconductor, and therefore, is an impurity. Also, alkaline earth metal is impurity in the case where alkaline earth metal is not included in an oxide semiconductor. When an insulating film in contact with the oxide semiconductor film is an oxide, an alkali metal, in particular, sodium (Na) diffuses into the insulating film and becomes Na+. In addition, in the oxide semiconductor film, Na cuts or enters a bond between metal and oxygen which are included in an oxide semiconductor. As a result, for example, deterioration of characteristics of the transistor, such as a normally-on state of the transistor due to shift of a threshold voltage in the negative direction, or reduction in mobility, occurs. In addition, variation in characteristics also occurs. Such deterioration of characteristics of the transistor and variation in characteristics due to the impurity remarkably appear when the hydrogen concentration in the oxide semiconductor film is very low. Therefore, the concentration of an alkali metal is preferably reduced in the case where the hydrogen concentration in the oxide semiconductor film is less than or equal to 5×1019atoms/cm3, particularly less than or equal to 5×1018atoms/cm3.

Note that in the transistor400illustrated inFIGS. 1A to 1C, the oxide semiconductor film140is used without being processed into an island shape. Using the oxide semiconductor film140which is not processed into an island shape can prevent contamination of the oxide semiconductor film140due to an etching process in the processing. Note that in order to suppress a leakage current which is caused between elements due to miniaturization, the oxide semiconductor film140which is processed into an island shape may be used.

A method for manufacturing the transistor400will be described below.

First, an insulating film100is formed over the substrate500, and a conductive film110is formed over the insulating film100(seeFIG. 2A).

Although there is no particular limitation on a substrate which can be used as the substrate500, it is necessary that the substrate500has at least heat resistance high enough to withstand heat treatment to be performed later. For example, a substrate such as a glass substrate, a ceramic substrate, a quartz substrate, or a sapphire substrate can be used. Alternatively, a single crystal semiconductor substrate or a polycrystalline semiconductor substrate of silicon, silicon carbide, or the like; a compound semiconductor substrate of silicon germanium or the like; an SOI substrate, or the like may be used as long as the substrate has an insulating surface, and a semiconductor element may be provided over the substrate. Still alternatively, the substrate500may be provided with a base film.

The insulating layer100can be formed by a PVD method, a CVD method, or the like. The insulating film100can be formed using an inorganic insulating material such as silicon oxide, silicon oxynitride, silicon nitride, hafnium oxide, aluminum oxide, or gallium oxide. In this embodiment, the insulating film100having a thickness of greater than or equal to 100 nm and less than or equal to 500 nm is formed using silicon oxide by a PVD method.

The conductive film110can be formed by a PVD method such as a sputtering method or a CVD method such as a plasma CVD method. As a material of the conductive film110, an element selected from aluminum, chromium, copper, tantalum, titanium, molybdenum, and tungsten, an alloy containing any of these elements as a component, or the like can be used. Further, one or more materials selected from manganese, magnesium, zirconium, beryllium, neodymium, and scandium may be used.

The conductive film110may have either a single-layer structure or a stacked-layer structure of two or more layers. For example, the conductive film can have a single-layer structure of a titanium film or a titanium nitride film, a single-layer structure of an aluminum film containing silicon, a two-layer structure in which a titanium film is stacked over an aluminum film, a two-layer structure in which a titanium film is stacked over a titanium nitride film, or a three-layer structure in which a titanium film, an aluminum film, and a titanium film are stacked in this order. In this embodiment, the conductive film110is formed using tungsten by a PVD method to have a single-layer structure having a thickness of greater than or equal to 50 nm and less than or equal to 200 nm

The insulating film100is formed using an inorganic insulating material. When a mask is formed over such a material, the mask may fall and it may be difficult to form a fine projection. However, when the conductive film110is formed over the insulating film100, the mask can be formed stably, so that the insulating film101having a fine projection can be formed. Therefore, by the insulating film101having a fine projection, a transistor whose channel length (L) is reduced can be formed. That is, by provision of the conductive film110over the insulating film100, subsequent fine processing of the insulating film100and the conductive film110becomes possible.

Next, a mask200is formed over the conductive film110(seeFIG. 2B).

The mask200can be formed by a photolithography technique or the like using a photosensitive material such as a photoresist. For light exposure at the time of forming the mask200, extreme ultraviolet light having a wavelength as short as greater than or equal to several nanometers and less than or equal to several tens of nanometers is preferably used. In the light exposure by extreme ultraviolet light, the resolution is high and the focus depth is large. Thus, the mask200can have a fine pattern.

As long as it is possible to form the mask200having a sufficiently fine pattern, a different method such as an ink-jet method may be used to form the mask200. In this case, it is unnecessary to use a photosensitive material such as a photoresist as a material of the mask200. In this embodiment, the mask200is formed by a stepper method.

Next, a slimming process by plasma treatment is performed on the mask200to form a mask210whose line width is smaller (seeFIG. 2C). Note that the slimming process refers to a process for reducing the size of the mask.

As the slimming process by plasma treatment, for example, an ashing process in which oxygen in a radical state (an oxygen radical) or the like is used can be employed. However, the slimming process is not limited to the above ashing process as long as the mask200can be processed into a finer pattern.

The channel length (L) of the transistor400is determined by the width of the gate electrode which is formed using the mask210. That is, the channel length (L) of the transistor400is determined by the width of the mask210in the channel length direction (a direction in which carriers flow), which is formed by the slimming process. Therefore, it is preferable to employ a process with high controllability as the slimming process.

The slimming process can be performed under the following conditions: the pressure is 3.0 Pa and the atmosphere is an oxygen atmosphere (the flow rate of oxygen is 100%). By the conditions, the mask200can be formed more finely than the minimum feature size (the resolution limit) of a light-exposure apparatus. For example, the line width of the mask200can be reduced to a length of less than or equal to half of the resolution limit of the light exposure apparatus, preferably less than or equal to one third of the resolution limit of the light exposure apparatus. For example, the line width can become greater than or equal to 20 nm and less than or equal to 2000 nm (2 μm), preferably greater than or equal to 20 nm and less than or equal to 350 nm. This enables a further reduction in the channel length (L) of the transistor.

Next, the insulating film100and the conductive film110are processed using the mask210, whereby the insulating film101having a projection is formed and the gate electrode111is formed over a top surface of the projection of the insulating film101(seeFIG. 2D).

The insulating film101may be processed into a shape which has only a projection. Alternatively, as illustrated inFIG. 2D, the insulating film101may be processed into a shape which has a projection and spreads over the substrate500. However, when the insulating film101is processed into a shape which has only a projection, it may be difficult to keep the fine projection unchanged because the projection may fall. Therefore, in order to keep the projection unchanged, the insulating film101is preferably processed into a shape which has a projection and spreads over the substrate500.

As a method for processing the insulating film100and the conductive film110into the insulating film101and the gate electrode111, for example, an etching process can be employed. Although either a dry etching process or a wet etching process may be performed as the etching process, a dry etching process with high controllability is preferably used for miniaturization.

In this embodiment, in order to process the insulating film100and the conductive film110into the insulating film101and the gate electrode111, an etching process is performed on the conductive film110, and after that, an etching process is performed on the insulating film100. As the etching process of the conductive film110, a dry etching process may be performed under the following conditions: the pressure is 1.5 Pa and the atmosphere is an atmosphere of mixed gas of carbon tetrafluoride (CF4), chlorine (Cl2), and oxygen (O2) at a flow ratio of 5:5:2. As the etching process of the insulating film100, for example, a dry etching process may be performed under the following conditions: the pressure is 5.5 Pa and the atmosphere is an atmosphere of a mixed gas of trifluoromethane (CHF3) and helium (He) (a flow ratio of 1:20).

Further, the etching processes of the conductive film110and the insulating film100may be performed so that the gate electrode111and the projection of the insulating film101which are to be formed have a tapered shape. The taper angle can be, for example, greater than or equal to 60° and less than or equal to 80°.

The channel length (L) of the transistor is determined by the gate electrode111formed in the above-described manner. Since the size of the gate electrode111when viewed from above is substantially the same as the mask210, the channel length (L) of the transistor is greater than or equal to 20 nm and less than 2000 nm (2 μm), preferably greater than or equal to 20 nm and less than or equal to 350 nm

Next, the gate insulating film120is formed over the insulating film101and the gate electrode111so as to cover the gate electrode111(seeFIG. 2E).

The gate insulating film120can be formed by a CVD method, a sputtering method, or the like. The gate insulating film120is preferably formed so as to contain silicon oxide, silicon nitride, silicon oxynitride, aluminum oxide, gallium oxide, tantalum oxide, hafnium oxide, yttrium oxide, hafnium silicate (HfSixOy(x>0, y>0)), hafnium silicate to which nitrogen is added (HfSixOyNz(x>0, y>0, z>0)), hafnium aluminate to which nitrogen is added (HfAlxOyNz(x>0, y>0, z>0)), or the like. The gate insulating film120may have a single-layer structure or a stacked-layer structure. There is no particular limitation on the thickness; however, in the case where a semiconductor device is reduced in size, the thickness is preferably small for ensuring an operation of the transistor. For example, in the case where silicon oxide is used, the thickness can be greater than or equal to 1 nm and less than or equal to 100 nm, preferably greater than or equal to 10 nm and less than or equal to 50 nm

When the gate insulating film120is formed thin as described above, gate leakage due to a tunnel effect or the like becomes a problem. In order to solve the problem of gate leakage, the gate insulating film120may be formed using a high dielectric constant (high-k) material such as hafnium oxide, tantalum oxide, yttrium oxide, hafnium silicate (HfSixOy(x>0, y>0)), hafnium silicate to which nitrogen is added (HfSixOyNz(x>0, y>0, z>0)), or hafnium aluminate to which nitrogen is added (HfAlxOyNz(x>0, y>0, z>0)). The use of a high-k material for the gate insulating film120makes it possible to increase the thickness in order to suppress gate leakage as well as ensuring electric characteristics. For example, hafnium oxide is preferable as a material of the gate insulating film because the relative permittivity of hafnium oxide is about 15, which is much higher than that of silicon oxide which is 3 to 4. Note that a stacked-layer structure of a film containing a high-k material and a film containing any of silicon oxide, silicon nitride, silicon oxynitride, silicon nitride oxide, aluminum oxide, and the like may be employed.

Next, a planarization process is performed on a surface of a region of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101(a region300) (seeFIG. 3A).

As the planarization process, plasma treatment or the like can be used. Note that plasma treatment is preferably performed under conditions that the gate insulating film120is not eliminated. For example, plasma treatment may be performed under the following conditions: the thickness of the gate insulating film120is approximately 100 nm, and the atmosphere is an atmosphere of a rare gas such as helium, argon, krypton, or neon. Note that a method, conditions and the like of the planarization process may be selected as appropriate. Note that in the case of performing plasma treatment as the planarization process, plasma treatment may be performed on a region of the gate insulating film120which does not overlap with the top surface of the projection of the insulating film101in addition to the region300.

Next, the oxide semiconductor film140is formed over the gate insulating film120, and a conductive film129is formed over the oxide semiconductor film140(seeFIG. 3B).

In particular, an In—Ga—Zn-based oxide semiconductor material has sufficiently high resistance when there is no electric field and thus off current can be sufficiently reduced. In addition, with high field-effect mobility, the In—Ga—Zn-based oxide semiconductor material is suitable for a semiconductor device.

As a typical example of the In—Ga—Zn-based oxide semiconductor material, one represented by InGaO3(ZnO)m(m>0) is given. Using M instead of Ga, there is an oxide semiconductor material represented by InMO3(ZnO)m(m>0). Here, M denotes one or more metal elements selected from gallium (Ga), aluminum (Al), iron (Fe), nickel (Ni), manganese (Mn), cobalt (Co), or the like. For example, M may be Ga, Ga and Al, Ga and Fe, Ga and Ni, Ga and Mn, Ga and Co, or the like. Note that the above compositions are derived from crystal structures and are only examples.

As a target for forming the oxide semiconductor film140by a sputtering method, it is particularly preferable to use a target having a composition ratio of In:Ga:Zn=1:x:y (x is greater than or equal to 0 and y is greater than or equal to 0.5 and less than or equal to 5) except oxygen. For example, a target having a composition ratio of In2O3:Ga2O3:ZnO=1:1:2 [molar ratio], or the like can be used. Alternatively, a target having a composition ratio of In2O3:Ga2O3:ZnO=1:1:1 [molar ratio], a target having a composition ratio of In2O3:Ga2O3:ZnO=1:1:4 [molar ratio], or a target having a composition ratio of In2O3:ZnO=1:2 [molar ratio] can be used.

In this embodiment, the oxide semiconductor film140having an amorphous structure is formed by a sputtering method using a target for forming an In—Ga—Zn—O-based oxide semiconductor film. The thickness of the oxide semiconductor film140is greater than or equal to 1 nm and less than or equal to 100 nm, preferably greater than or equal to 2 nm and less than or equal to 50 nm, and further preferably greater than or equal to 3 nm and less than or equal to 30 nm. By employing a structure according to the invention disclosed herein, a short channel effect due to miniaturization can be suppressed even in the case of using the oxide semiconductor film140having such a thickness. Note that an appropriate thickness differs depending on an oxide semiconductor material used, the application of a semiconductor device, or the like; therefore, it is also possible to set the thickness as appropriate depending on the material to be used, the application, or the like.

The relative density of a metal oxide in the target for forming an oxide semiconductor film is greater than or equal to 80%, preferably greater than or equal to 95%, more preferably greater than or equal to 99.9%. With the use of a target for forming an oxide semiconductor film with high relative density, the oxide semiconductor film140with a dense structure can be formed.

The atmosphere in which the oxide semiconductor film140is formed is preferably a rare gas (typically, argon) atmosphere, an oxygen atmosphere, or a mixed atmosphere containing a rare gas (typically, argon) and oxygen. Specifically, it is preferable to use a high-purity gas atmosphere, for example, from which an impurity such as hydrogen, water, a hydroxyl group, or hydride is removed to less than or equal to 1 ppm (preferably, less than or equal to 10 ppb).

In forming the oxide semiconductor film140, the substrate is held in a treatment chamber that is maintained at reduced pressure and is heated so that the substrate temperature is higher than or equal to 100° C. and lower than 550° C., preferably higher than or equal to 200° C. and lower than or equal to 400° C. Alternatively, the substrate temperature in forming the oxide semiconductor film140may be a room temperature (higher than or equal to 15° C. and lower than or equal to 35° C.). Then, a sputtering gas from which hydrogen, water, and the like are removed is introduced while moisture in the treatment chamber is removed, and the aforementioned target is used, whereby the oxide semiconductor film140is formed. The oxide semiconductor film140is formed while the substrate is heated, so that impurities contained in the oxide semiconductor film140can be reduced. Moreover, damage due to sputtering can be reduced. In order to remove moisture in the treatment chamber, an entrapment vacuum pump is preferably used. For example, a cryopump, an ion pump, a titanium sublimation pump, or the like can be used. A turbo pump provided with a cold trap may be used. Since a hydrogen atom, a compound containing a hydrogen atom, such as water (H2O), or the like (preferably a compound containing a carbon atom as well) can be removed from the treatment chamber by evacuating the chamber with a cryopump or the like, the impurity concentration of the oxide semiconductor film can be reduced.

For example, conditions for forming the oxide semiconductor film140can be set as follows: the distance between the substrate and the target is 170 mm, the pressure is 0.4 Pa, the direct current (DC) power is 0.5 kW, and the atmosphere is an oxygen (100% oxygen) atmosphere, an argon (100% argon) atmosphere, or a mixed atmosphere of oxygen and argon. A pulse direct current (DC) power supply is preferable because powder substances (also referred to as particles or dust) generated in the film formation can be reduced and the film thickness can be made uniform.

Note that before the oxide semiconductor film140is formed by a sputtering method, reverse sputtering in which an argon gas is introduced and plasma is generated may be performed so that a material attached to a surface over which the oxide semiconductor film140is to be formed (e.g., a surface of the gate insulating film120) is removed. Here, the reverse sputtering is a method by which ions collide with a surface to be processed so that the surface is modified, in contrast to normal sputtering by which ions collide with a sputtering target. An example of a method for making ions collide with a surface to be processed is a method in which high-frequency voltage is applied to the surface in an argon atmosphere so that plasma is generated near a substrate. Note that an atmosphere of nitrogen, helium, oxygen, or the like may be used instead of an argon atmosphere.

After the oxide semiconductor film140is formed, heat treatment (first heat treatment) is preferably performed on the oxide semiconductor film140. Excessive hydrogen (including water and a hydroxyl group) in the oxide semiconductor film140can be removed by the first heat treatment. The first heat treatment is performed at higher than or equal to 250° C. and lower than or equal to 700° C., preferably higher than or equal to 450° C. and lower than or equal to 600° C. or lower than the strain point of the substrate.

The heat treatment can be performed in such a way that, for example, the substrate is introduced into an electric furnace in which a resistance heating element or the like is used and heated at 450° C. under a nitrogen atmosphere for an hour. During the heat treatment, the oxide semiconductor film140is not exposed to the air to prevent the entry of water and hydrogen.

The heat treatment apparatus is not limited to the electric furnace and may be an apparatus for heating a substrate by thermal conduction or thermal radiation from a medium such as a heated gas. For example, a rapid thermal annealing (RTA) apparatus such as a lamp rapid thermal annealing (LRTA) apparatus or a gas rapid thermal annealing (GRTA) apparatus can be used. An LRTA apparatus is an apparatus for heating a substrate by radiation of light (electromagnetic waves) emitted form a lamp such as a halogen lamp, a metal halide lamp, a xenon arc lamp, a carbon arc lamp, a high-pressure sodium lamp, or a high-pressure mercury lamp. A GRTA apparatus is an apparatus for performing heat treatment using a high-temperature gas. As the gas, an inert gas which does not react with an object to be processed by heat treatment, such as nitrogen or a rare gas such as argon is used.

For example, as the first heat treatment, a GRTA process may be performed as follows. The substrate is placed in an inert gas atmosphere which has been heated, heated for several minutes, and taken out of the inert gas atmosphere. The GRTA process enables high-temperature heat treatment for a short time. Moreover, the GRTA process can be used even in the conditions where the temperature exceeds the upper temperature limit of the substrate. Note that the inert gas may be switched to a gas including oxygen during the process. This is because defect levels in an energy gap due to oxygen deficiency can be reduced by performing the first heat treatment in an atmosphere containing oxygen.

Note that as the inert gas atmosphere, an atmosphere that contains nitrogen or a rare gas (e.g., helium, neon, or argon) as its main component and does not contain water, hydrogen, or the like is preferably used. For example, the purity of nitrogen or a rare gas such as helium, neon, or argon introduced into a heat treatment apparatus is greater than or equal to 6 N (99.9999%), preferably greater than or equal to 7 N (99.99999%) (that is, the concentration of the impurities is less than or equal to 1 ppm, preferably less than or equal to 0.1 ppm).

In any case, impurities are reduced by the first heat treatment so that the i-type (intrinsic) or substantially i-type oxide semiconductor film140is obtained. Accordingly, a transistor having extremely excellent characteristics can be realized.

The above heat treatment (first heat treatment) can be referred to as dehydration treatment, dehydrogenation treatment, or the like because of its effect of removing hydrogen, water, and the like. The dehydration treatment or the dehydrogenation treatment can be performed, for example, after subsequent formation of the source or drain electrode130aand the source or drain electrode130bas long as it is after the oxide semiconductor film140is formed. Such dehydration treatment or dehydrogenation treatment may be conducted once or plural times.

After the oxide semiconductor film140is formed, the oxide semiconductor film140may be processed into an island-shaped oxide semiconductor film. The oxide semiconductor film140can be processed into an island-shaped oxide semiconductor film by an etching process, for example. The etching process may be performed either before the heat treatment or after the heat treatment. Although a dry etching process is preferable in terms of element miniaturization, a wet etching process may also be used. An etching gas or an etchant can be selected as appropriate depending on a material to be etched.

The conductive film129can be formed by a PVD method such as a sputtering method or a CVD method such as a plasma CVD method. As a material of the conductive film129, an element selected from aluminum, chromium, copper, tantalum, titanium, molybdenum, and tungsten, an alloy containing any of these elements as a component, or the like can be used. Further, one or more materials selected from manganese, magnesium, zirconium, beryllium, neodymium, and scandium may be used.

The conductive film129may have either a single-layer structure or a stacked-layer structure of two or more layers. For example, the conductive film can have a single-layer structure of a titanium film or a titanium nitride film, a single-layer structure of an aluminum film containing silicon, a two-layer structure in which a titanium film is stacked over an aluminum film, a two-layer structure in which a titanium film is stacked over a titanium nitride film, or a three-layer structure in which a titanium film, an aluminum film, and a titanium film are stacked in this order.

The conductive film129may be formed using a conductive metal oxide. As the conductive metal oxide, indium oxide (In2O3), tin oxide (SnO2), zinc oxide (ZnO), indium tin oxide (In2O3—SnO2, which is abbreviated to ITO in some cases), indium zinc oxide (In2O3—ZnO), or any of these metal oxide materials in which silicon or silicon oxide is included can be used. In this embodiment, the conductive film129is formed using tungsten by a PVD method to have a single-layer structure having a thickness of greater than or equal to 150 nm and less than or equal to 500 nm.

Note that, in terms of a later etching process, the conductive film129needs to be formed to have a larger thickness than a total thickness of the gate electrode111and the height of the projection of the insulating film101(h shown inFIG. 3C). The height h of the projection of the insulating film101can be set to be greater than or equal to 150 nm and less than or equal to 300 nm, for example.

Next, the conductive film129is processed by an etching process to form a conductive film130(seeFIG. 3C). Note that the conductive film129may be etched either by a dry etching process or a wet etching process; however, a dry etching process with high controllability is preferably used for miniaturization. The conductive film130is processed into the source or drain electrode130aand the source or drain electrode130bin a later step. Therefore, the conductive film130may be processed into a desired shape as the source or drain electrode130aand the source or drain electrode130bas appropriate.

Next, a planarization process, an etching process, or the like is performed on the conductive film130so as to expose a surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101, thereby forming the source or drain electrode130aand the source or drain electrode130b(seeFIG. 3D).

A structure illustrated inFIG. 3Dhas difference in height between the surface of the oxide semiconductor film140which overlaps with the projection of the insulating film101and a surface of an uppermost portion of the source or drain electrode130a, and between the surface of the oxide semiconductor film140which overlaps with the projection of the insulating film101and a surface of an uppermost portion of the source or drain electrode130b. The structure having difference in height can be obtained in such a manner that, for example, an etching process, a polishing process, a combination thereof, or the like is performed on the conductive film130.

In order to obtain the structure having difference in height, for example, an etching process can be performed after a polishing process by a CMP process (a chemical mechanical polishing process). Specifically, first, a CMP process is performed on the conductive film130until when its surface has the same height as the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101. After that, an etching process is performed on the conductive film130under conditions where the oxide semiconductor film140is not easily etched.

The CMP process is a method for planarizing a surface of an object to be processed by a combination of chemical and mechanical actions. More specifically, the CMP process is a method in which a polishing cloth is attached to a polishing stage, the polishing stage and the object to be processed are each rotated or swung while a slurry (an abrasive) is supplied between the object to be processed and the polishing cloth, and the surface of the object to be processed is polished by chemical reaction between the slurry and the surface of the object to be processed and by action of mechanical polishing between the object to be processed and the polishing cloth. The CMP process as the polishing process may be performed once or plural times.

As the etching process, either or both of a dry etching process and a wet etching process can be employed. Note that etching conditions where a selectivity ratio of the conductive film130with respect to the oxide semiconductor film140is high (for example, the selectivity ratio of the conductive film130with respect to the oxide semiconductor film140is 14:1) are employed. For example, a dry etching process may be performed under the following conditions: the pressure is 1.6 Pa and the atmosphere is an atmosphere of a mixed gas of carbon tetrafluoride (CF4), chlorine (Cl2), and oxygen (O2) at a flow ratio of 5:5:2.

In addition, as another example of forming the structure having difference in height, an etching process can be performed after formation of a film. Specifically, first, a film is formed over the conductive film130. The film formed over the conductive film130can be formed using liquid glass, liquid photoresist, or the like by a spin coating method, an ink-jet method, or the like. This film is formed for the purpose of planarizing the outmost surface of the transistor under manufacture, and thus is called a planarization film in this specification. The planarization film may be hardened or solidified by a treatment with light or heat.

Next, an etching process (a first etching process) is performed on the planarization film and the conductive film130until when they have the same height as the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101. After that, an etching process (a second etching process) is further performed under conditions where the oxide semiconductor film140is not easily etched.

As the second etching process, the above etching conditions where the selectivity ratio of the conductive film130with respect to the oxide semiconductor film140is high is preferably employed.

The difference in height between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130bis preferably greater than or equal to 5 nm and less than or equal to 20 nm. By the difference in height, the path of electric current in the oxide semiconductor film140is extended. This makes it possible to alleviate the concentration of an electric field in the transistor400and to suppress a short channel effect.

An etching process or a planarization process is performed so as to expose the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101in this manner, whereby the source or drain electrode130aand the source or drain electrode130bcan be formed in a self-aligned manner. Accordingly, misalignment is not caused in forming the source or drain electrode130aand the source or drain electrode130b, so that a channel length can be reduced. Accordingly, a highly reliable semiconductor device can be manufactured.

After formation of the source or drain electrode130aand the source or drain electrode130b, a second heat treatment is preferably performed in an inert gas atmosphere or an oxygen atmosphere. The temperature of the heat treatment is higher than or equal to 200° C. and lower than or equal to 450° C., preferably higher than or equal to 250° C. and lower than or equal to 350° C. For example, the heat treatment may be performed at 250° C. for 1 hour in a nitrogen atmosphere. The second heat treatment can reduce variations in electric characteristics of transistors.

Note that although the second heat treatment is performed after formation of the source or drain electrode130aand the source or drain electrode130bin this embodiment, the timing of the second heat treatment is not particularly limited thereto. For example, the second heat treatment may be performed after formation of the conductive film130. Alternatively, the second heat treatment may be performed following the first heat treatment, the first heat treatment may double as the second heat treatment, or the second heat treatment may double as the first heat treatment. Further, an insulating film may be provided over the source or drain electrode130a, the source or drain electrode130b, and the oxide semiconductor film140. After formation of the insulating film, the second heat treatment may be performed. In the case where an insulating film provided on and in contact with the oxide semiconductor film140contains oxygen, the oxide semiconductor film140is supplied with oxygen, so that oxygen deficiency in the oxide semiconductor film140can be filled. Oxygen deficiency in the oxide semiconductor film140is filled, whereby a normally-on state of the transistor400due to shift of a threshold voltage in the negative direction can be prevented and reliability of the transistor400can be improved. Note that “the insulating film contains oxygen” here means that the insulating film can release oxygen by heat treatment. The insulating film that can release oxygen by heat treatment can be formed by a sputtering method, for example.

By performing at least one of the first heat treatment and the second heat treatment as described above, the oxide semiconductor film140can be highly purified so as to include a substance including a hydrogen atom as few as possible. In this manner, an i-type (intrinsic) or substantially i-type oxide semiconductor film can be formed.

Note that an etching process is further performed after the above etching process, whereby the source or drain electrode130aand the source or drain electrode130bmay be processed into a desired pattern. Details of the etching process for processing the pattern can be similar to those of the above-described etching process.

Although the structure having difference in height between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130bis described in this embodiment, a structure having no difference in height may be also employed as a transistor401illustrated inFIG. 3E. That is, only the CMP process or the first etching process described with reference toFIG. 3Dmay be performed to provide the structure having no difference in height between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130b.

Further, although a structure is described in which the gate electrode111is formed over the top surface of the projection of the insulating film101so as not to overlap with the source or drain electrode130aand the source or drain electrode130bin this embodiment, a structure may be employed in which the gate electrode111is formed so as to overlap with the source or drain electrode130aand the source or drain electrode130bas a transistor402illustrated inFIG. 4A. The transistor402has a channel length (L) which is reduced in a manner similar to the transistor400.

Further, as a transistor403illustrated inFIG. 4B, a structure may be also employed in which the gate electrode111has a structure similar to the gate electrode111of the transistor402and which has no difference in height between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the oxide semiconductor film140which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130b. A method for manufacturing the transistor402ofFIG. 4Aand the transistor403ofFIG. 4Bis different from a method for manufacturing the transistor400ofFIGS. 1A to 1Cregarding the insulating film101and the gate electrode111. In manufacturing the transistor402and the transistor403, a mask is formed over the insulating layer100, a slimming process is performed on the mask to be reduced in size, and the insulating film101is formed using the mask reduced in size. After that, a conductive film is formed and processed into the gate electrode111.

Further, as a transistor404illustrated inFIG. 4C, a structure may also be employed in which the gate electrode111has a structure similar to the gate electrode111of the transistor400, and a conductive film112(e.g. a film formed using the same material as the gate electrode) which overlaps with the source or drain electrode130aand the source or drain electrode130bis provided over the gate electrode111. In manufacturing the transistor404, a mask is formed over the insulating layer100and the conductive layer110, a slimming process is performed on the mask to be reduced in size, and the insulating film101and the gate electrode111are formed using the mask reduced in size. After that, a conductive film is formed and processed into the conductive film112.

Thus, a transistor including an oxide semiconductor film whose channel length (L) is reduced can be formed.

According to one embodiment of the present invention, the mask is reduced in size by the slimming process, whereby the channel length of the transistor using an oxide semiconductor film can be reduced. Thus, high-speed operation of the transistor becomes possible.

Further, according to another embodiment of the present invention, a surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101(a region in contact with a channel region of the oxide semiconductor film) is planarized, whereby high-speed operation of the transistor can be achieved.

Further, according to another embodiment of the present invention, the insulating film101having a projection is used, whereby the source or drain electrode130aand the source or drain electrode130bare formed in a self-aligned manner. Accordingly, misalignment is not caused in forming the source or drain electrode130aand the source or drain electrode130b, so that the channel length can be reduced. Thus, a highly reliable semiconductor device can be manufactured, and yield and productivity can be improved.

In this embodiment, an example of a method for manufacturing a semiconductor device which is different from that described in Embodiment 1 will be described with reference toFIGS. 5A to 5C,FIGS. 6A to 6E, andFIGS. 7A to 7C. A main difference between Embodiment 1 and Embodiment 2 is the stacking order and the structure of the oxide semiconductor film140, the source or drain electrode130a, and the source or drain electrode130b. The main difference will be described in this embodiment.

FIGS. 5A to 5Cillustrate a transistor410which is an example of a semiconductor device.FIG. 5Ais a top view of the transistor410.FIG. 5Bis a cross-sectional view taken along line E-F ofFIG. 5A.FIG. 5Cis a cross-sectional view taken along line G-H ofFIG. 5A. The transistor410illustrated inFIG. 5Bincludes the insulating film101having a projection over the substrate500; the gate electrode111formed over the top surface of the projection of the insulating film101; the gate insulating film120formed so as to cover the gate electrode111; the source or drain electrode130aand the source or drain electrode130bformed over the gate insulating film120; and the oxide semiconductor film140.

A method for manufacturing the transistor410will be described below.

First, the insulating film101having a projection is formed over the substrate500, the gate electrode111is formed over the top surface of the projection of the insulating film101, and the gate insulating film120is formed over the insulating film101and the gate electrode so as to cover the gate electrode111. These steps can be performed in a manner similar to those illustrated inFIGS. 2A to 2E; therefore, detailed description thereof will be omitted.

Next, the conductive film129for forming the source or drain electrode130aand the source or drain electrode130b(including a wiring formed in the same layer as the source or drain electrode130aand the source or drain electrode130b) is formed over the gate insulating film120(seeFIG. 6A). For the material and the formation method of the conductive film129, description of the conductive film129ofFIG. 3Bin Embodiment 1 can be referred to; therefore, detailed description thereof will be omitted.

Next, the conductive film129is processed by an etching process to form the conductive film130(seeFIG. 6B). For the formation method of the conductive film130, description of the conductive film130ofFIG. 3Cin Embodiment 1 can be referred to; therefore, detailed description thereof will be omitted.

Next, a planarization process, an etching process, or the like is performed on the conductive film130so as to expose the surface of the gate insulating film120which overlaps with the projection of the insulating film101, thereby forming the source or drain electrode130aand the source or drain electrode130b(seeFIG. 6C).

A structure illustrated inFIG. 6Chas difference in height between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and a surface of an uppermost portion of the source or drain electrode130a, and between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and a surface of an uppermost portion of the source or the drain electrode130b. The structure having difference in height can be obtained in such a manner that an etching process, a planarization process, a combination thereof, or the like is performed on the conductive film130.

In order to obtain the structure having difference in height, for example, an etching process can be performed after a CMP process (a chemical mechanical polishing process) which is a planarization process. Specifically, first, a CMP process is performed on the conductive film130until when it has the same height as the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101. Thus, the source or drain electrode130aand the source or drain electrode130bare formed. In addition, the region300which is planarized is formed over the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101. After that, an etching process is performed on the conductive film130under conditions where the gate insulating film120is not easily etched. Note that for a polishing process of a CMP process, description ofFIG. 3Din Embodiment 1 can be referred to; therefore, detailed description thereof will be omitted.

Through the CMP process, the root-mean-square (RMS) roughness of a surface of the region300can be less than or equal to 1 nm (preferably, less than or equal to 0.5 nm).

The CMP process as the polishing process may be performed once or plural times. When the CMP process is performed in plural times, it is preferable that the first polishing step be performed at a high polishing rate and be followed by a final polishing step at a low polishing rate. By combining polishing with different polishing rates, planarity of the surfaces of the region300can be further improved.

By such a planarization process, planarity of the surface of the region300of the gate insulating film120on which the oxide semiconductor film140is to be formed later is improved, so that characteristics of the transistor can be improved.

As the etching process, either or both of a dry etching process and a wet etching process can be employed. Note that etching conditions where a selectivity ratio of the conductive film130with respect to the gate insulating film120is high (for example, the selectivity ratio of the conductive film130with respect to the gate insulating film120is 3.2:1) are employed. For example, a dry etching process may be performed under the following conditions: the pressure is 1.6 Pa and the atmosphere is an atmosphere of a mixed gas of carbon tetrafluoride (CF4), chlorine (Cl2), and oxygen (O2) at a flow ratio of 5:5:2.

Further, as another example of forming the structure having difference in height, an etching process using a planarization film can be given.

As a specific example, first, a planarization film is formed over the conductive film130. For the material and the formation method of the planarization film, description in Embodiment 1 can be referred to; therefore, detailed description thereof will be omitted. An etching process (the first etching process) is performed on the planarization film and the conductive film130until when they have the same height as the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101. After that, an etching process (the second etching process) is further performed on the conductive film130under conditions where the gate insulating film120is not easily etched.

For the second etching process, etching conditions where the selectivity ratio of the conductive film130with respect to the gate insulating film120is high may be employed.

The difference in height between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130b, which is provided by the above process, is preferably greater than or equal to 5 nm and less than or equal to 20 nm. By the difference in height, the path of electric current in the oxide semiconductor film140is extended. This makes it possible to alleviate the concentration of an electric field in the transistor410and to suppress a short channel effect.

The above planarization process, the above etching process, or the like is performed to expose the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101, so that the source or drain electrode130aand the source or drain electrode130bcan be formed using the conductive film130in a self-aligned manner. Accordingly, the number of masks necessary for the process can be reduced and yield can be improved. Further, by the planarization process, planarity of the surface of the region300of the gate insulating film120on which the oxide semiconductor film140is to be formed later is improved, so that characteristics of the transistor410can be improved.

Next, the oxide semiconductor film140is formed over the source or drain electrode130a, the source or drain electrode130b, and the gate insulating film120(seeFIG. 6D). For the material and the formation method of the oxide semiconductor film140, description ofFIG. 3Bin Embodiment 1 can be referred to; therefore, detailed description thereof will be omitted.

Note that an etching process is further performed after the above etching process, whereby the source or drain electrode130aand the source or drain electrode130bmay be processed into a desired pattern. Details of the etching process for processing the pattern can be similar to those of the above-described etching process.

Although the structure having difference in height between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130bis described in this embodiment, a structure having no difference in height may be also employed as a transistor411illustrated inFIG. 6E. That is, only the CMP process or the first etching process described with reference toFIG. 6Cmay be performed to provide the structure having no difference in height between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130b.

Further, although a structure is described in which the gate electrode111is formed over the top surface of the projection of the insulating film101so as not to overlap with the source or drain electrode130aand the source or drain electrode130bin this embodiment, a structure may be employed in which the gate electrode111is formed so as to overlap with the source or drain electrode130aand the source or drain electrode130bas a transistor412illustrated inFIG. 7A. The transistor412has a channel length (L) which is reduced in a manner similar to the transistor400.

Further, as a transistor413illustrated inFIG. 7B, a structure may be also employed in which the gate electrode111has a structure similar to the gate electrode111of the transistor412and which has no difference in height between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130a, and between the surface of the gate insulating film120which overlaps with the top surface of the projection of the insulating film101and the surface of the uppermost portion of the source or drain electrode130b. A method for manufacturing the transistor412ofFIG. 7Aand the transistor413ofFIG. 7Bis different from a method for manufacturing the transistor400ofFIGS. 1A to 1Cregarding the insulating film101and the gate electrode111. In manufacturing the transistor412and the transistor413, a mask is formed over the insulating layer100, a slimming process is performed on the mask to be reduced in size, and the insulating film101is formed using the mask reduced in size. After that, a conductive film is formed and processed into the gate electrode111.

Further, as a transistor414illustrated inFIG. 7C, a structure may also be employed in which the gate electrode111has a structure similar to the gate electrode111of the transistor410, and a conductive film112(e.g. a film formed using the same material as the gate electrode) which overlaps with the source or drain electrode130aand the source or drain electrode130bis provided over the gate electrode111. In manufacturing the transistor414, a mask is formed over the insulating layer100and the conductive layer110, a slimming process is performed on the mask to be reduced in size, and the insulating film101and the gate electrode111are formed using the mask reduced in size. After that, a conductive film is formed and processed into the conductive film112.

Thus, a transistor410including an oxide semiconductor film whose channel length (L) is reduced can be formed.

According to one embodiment of the present invention, the mask is reduced in size by the slimming process, whereby the channel length (L) of the transistor410can be reduced, and the transistor410includes the oxide semiconductor film, whereby high-speed operation of the transistor becomes possible.

Further, according to another embodiment of the present invention, by planarization of part of the gate insulating film120in contact with the channel region of the oxide semiconductor film140, high-speed operation of the transistor can be achieved.

Further, according to another embodiment of the present invention, the insulating film101having a projection is used, whereby the source or drain electrode130aand the source or drain electrode130bare formed in a self-aligned manner. Accordingly, misalignment is not caused in forming the source or drain electrode130aand the source or drain electrode130b, so that the channel length can be reduced. Thus, a highly reliable semiconductor device can be manufactured, and yield and productivity can be improved.

In this embodiment, the appearance and a cross section of a liquid crystal display panel, which is one embodiment of a semiconductor device, will be described with reference toFIGS. 8A to 8C. The liquid crystal display panel illustrated inFIGS. 8A to 8Cincludes transistors illustrated in Embodiment 1 or 2.FIGS. 8A and 8Care plan views of panels in which transistors4010and4011and a liquid crystal element4013are sealed between a first substrate4001and a second substrate4006with a sealant4005.FIG. 8Bis a cross-sectional view taken along line M-N inFIG. 8AorFIG. 8C.

The sealant4005is provided so as to surround a pixel portion4002and a scan line driver circuit4004which are provided over the first substrate4001. The second substrate4006is provided over the pixel portion4002and the scan line driver circuit4004. Therefore, the pixel portion4002and the scan line driver circuit4004are sealed together with a liquid crystal layer4008, by the first substrate4001, the sealant4005, and the second substrate4006. Moreover, a signal line driver circuit4003, which is formed using a single crystal semiconductor film or a polycrystalline semiconductor film over a substrate prepared separately, is provided in a region different from the region surrounded by the sealant4005over the first substrate4001.

Note that the connection method of a driver circuit which is separately formed is not particularly limited, and a COG method, a wire bonding method, a TAB method, or the like can be used.FIG. 8Aillustrates an example in which the signal line driver circuit4003is mounted by a COG method.FIG. 8Cillustrates an example in which the signal line driver circuit4003is mounted by a TAB method.

The pixel portion4002and the scan line driver circuit4004provided over the first substrate4001include a plurality of transistors.FIG. 8Billustrates the transistor4010included in the pixel portion4002and the transistor4011included in the scan line driver circuit4004. InFIG. 8B, insulating layers4041,4042, and4021are provided over the transistors4010and4011.

As the transistors4010and4011, the transistors described in Embodiment 1 or 2 can be used. In this embodiment, the transistors4010and4011are n-channel transistors.

A conductive layer4040is provided over the insulating layer4021and at a position which overlaps with a channel formation region of the oxide semiconductor film in the transistor4011for the driver circuit. The conductive layer4040is provided at the position which overlaps with the channel formation region of the oxide semiconductor film, whereby the reliability of the transistor can be improved. For example, in a bias-temperature stress test (also referred to as a BT test), the amount of change in the threshold voltage of the transistor4011before and after the BT test can be reduced. The potential of the conductive layer4040may be the same or different from that of a gate electrode of the transistor4011. The conductive layer4040can also function as a second gate electrode. The potential of the conductive layer4040may be GND or 0 V, or the conductive layer4040may be in a floating state.

A pixel electrode layer4030included in the liquid crystal element4013is electrically connected to the transistor4010. A counter electrode layer4031of the liquid crystal element4013is provided for the second substrate4006. A portion where the pixel electrode layer4030, the counter electrode layer4031, and the liquid crystal layer4008overlap with one another corresponds to the liquid crystal element4013. Note that the pixel electrode layer4030and the counter electrode layer4031are provided with an insulating layer4032and an insulating layer4033respectively which each function as an alignment film, and the liquid crystal layer4008is sandwiched between the pixel electrode layer4030and the counter electrode layer4031with the insulating layers4032and4033interposed therebetween.

Note that as the first substrate4001and the second substrate4006, a light-transmitting substrate, for example, a plastic substrate such as a polyester film or an acrylic resin film, a glass substrate, or a ceramic substrate can be used.

A spacer4035is a columnar spacer obtained by selective etching of an insulating film and provided in order to control the distance (a cell gap) between the pixel electrode layer4030and the counter electrode layer4031. Alternatively, a spherical spacer may also be used. The counter electrode layer4031is electrically connected to a common potential line provided over the same substrate as the transistor4010. With use of the common connection portion, the counter electrode layer4031and the common potential line can be electrically connected to each other by conductive particles arranged between a pair of substrates. Note that the conductive particles are included in the sealant4005.

Alternatively, liquid crystal exhibiting a blue phase for which an alignment film is unnecessary may be used. In that case, the electrodes are arranged differently from those illustrated inFIGS. 8A to 8Cbecause a horizontal electric field mode is employed. For example, the pixel electrode layer and a common electrode layer are arranged over the same insulating layer, and a horizontal electric field is applied to the liquid crystal layer. A blue phase is one of liquid crystal phases, which is generated just before a cholesteric phase changes into an isotropic phase while temperature of cholesteric liquid crystal is increased. Since the blue phase appears only in a narrow temperature range, a liquid crystal composition in which several weight percent or more of a chiral material is mixed is used for the liquid crystal layer4008in order to improve the temperature range. The liquid crystal composition which includes a liquid crystal exhibiting a blue phase and a chiral agent has a short response time of less than or equal to 1 millisecond, has optical isotropy; therefore, alignment treatment is not necessary and viewing angle dependence is small.

Note that this embodiment can also be applied to a transflective liquid crystal display device in addition to a transmissive liquid crystal display device.

The liquid crystal display device may be provided with a polarizing plate and a coloring layer. A position where the polarizing plate and the coloring layer are provided and the stacked-layer structure thereof may be set as appropriate depending on materials of the polarizing plate and the coloring layer or conditions of manufacturing process. Further, a light-blocking film serving as a black matrix may be provided in a portion other than the display portion.

Over the transistors4011and4010, the insulating layer4041is formed in contact with the oxide semiconductor film. The protective insulating layer4042is formed on and in contact with the insulating layer4041. Note that in order to reduce the surface roughness of the transistors, the protective insulating layer4042may be covered with the insulating layer4021functioning as a planarization insulating film.

The insulating layer4021is formed as the planarization insulating film. As the insulating layer4021, an organic material having heat resistance such as polyimide, acrylic resin, benzocyclobutene resin, polyamide, or epoxy resin can be used. Other than such organic materials, it is also possible to use a low-dielectric constant material (a low-k material), a siloxane-based resin, PSG (phosphosilicate glass), BPSG (borophosphosilicate glass), or the like. Note that the insulating layer4021may be formed by stacking a plurality of insulating films formed using these materials.

A formation method of the insulating layer4021is not particularly limited, and the following method can be employed depending on the material: a method such as a sputtering method, an SOG method, a spin coating method, a dipping method, a spray coating method, a droplet discharge method (e.g., an ink-jet method, screen printing, offset printing, or the like), or a tool (equipment) such as a doctor knife, a roll coater, a curtain coater, a knife coater, or the like. The baking step of the insulating layer4021also serves as annealing of the semiconductor layer, whereby a semiconductor device can be manufactured efficiently.

Further, a variety of signals and potentials are supplied to the signal line driver circuit4003which is formed separately, the scan line driver circuit4004, or the pixel portion4002from an FPC4018.

A connection terminal electrode4015is formed using the same conductive film as the pixel electrode layer4030included in the liquid crystal element4013. A terminal electrode4016is formed using the same conductive film as a source or drain electrode of each of the transistor4010and the transistor4011.

The connection terminal electrode4015is electrically connected to a terminal included in the FPC4018via an anisotropic conductive film4019.

Note thatFIGS. 8A to 8Cillustrate the example in which the signal line driver circuit4003is formed separately and mounted on the first substrate4001; however, this embodiment is not limited to this structure. The scan line driver circuit may be separately formed and then mounted, or only part of the signal line driver circuit or part of the scan line driver circuit may be separately formed and then mounted.

The liquid crystal display panel described in this embodiment includes transistors having favorable electric characteristics and high reliability described in Embodiment 1 or 2; therefore, the liquid crystal display panel having favorable quality can be provided.

In this embodiment, an example of electronic paper will be described as an embodiment of a semiconductor device.

The transistor described in Embodiment 1 or 2 can be used for electronic paper in which electronic ink is driven by an element electrically connected to a switching element. The electronic paper is also referred to as an electrophoretic display device (an electrophoretic display) and is advantageous in that it has the same level of readability as plain paper, it has lower power consumption than other display devices, and it can be made thin and lightweight.

Electrophoretic displays can have various modes. Electrophoretic displays contain a plurality of microcapsules dispersed in a solvent or a solute, each microcapsule containing first particles which are positively charged and second particles which are negatively charged. By applying an electric field to the microcapsules, the particles in the microcapsules move in opposite directions to each other and only the color of the particles gathering on one side is displayed. Note that the first particles and the second particles each contain pigment and do not move without an electric field. Moreover, the first particles and the second particles have different colors (which may be colorless).

Thus, an electrophoretic display is a display that utilizes a so-called dielectrophoretic effect by which a substance having a high dielectric constant moves to a high-electric field region.

A solution in which the above microcapsules are dispersed in a solvent is referred to as electronic ink. This electronic ink can be printed on a surface of glass, plastic, cloth, paper, or the like. Furthermore, by using a color filter or particles that have a pigment, color display can also be achieved.

In addition, if a plurality of the above microcapsules are arranged as appropriate over an active matrix substrate so as to be interposed between two electrodes, an active matrix display device can be completed, and display can be performed by application of an electric field to the microcapsules. For example, the active matrix substrate obtained by the transistors described in Embodiment 1 or 2 can be used.

Note that the first particles and the second particles in the microcapsules may each be formed using a single material selected from a conductive material, an insulating material, a semiconductor material, a magnetic material, a liquid crystal material, a ferroelectric material, an electroluminescent material, an electrochromic material, and a magnetophoretic material or formed using a composite material of any of these.

FIG. 9illustrates active matrix electronic paper as an example of a semiconductor device. A transistor581used for the semiconductor device can be manufactured in a manner similar to that of the transistors described in Embodiment 1 or 2 and has favorable electric characteristics and high reliability.

The electronic paper inFIG. 9is an example of a display device using a twisting ball display system. The twisting ball display system refers to a method in which spherical particles each colored in black and white are arranged between a first electrode layer and a second electrode layer which are electrode layers used for a display element, and a potential difference is generated between the first electrode layer and the second electrode layer to control orientation of the spherical particles, so that display is performed.

InFIG. 9, the transistor581is a bottom-gate transistor. The transistor described in Embodiment 1 or 2 can be used for the transistor581.

A source electrode or a drain electrode of the transistor581is in contact with and electrically connected to a first electrode layer587in an opening portion formed in an insulating layer583and an insulating layer585. Between the first electrode layer587and a second electrode layer588, spherical particles589each having a black region590aand a white region590baround which is filled with liquid, are provided between a pair of substrates580and596. A space around the spherical particles589is filled with a filler595such as a resin.

In addition, the first electrode layer587corresponds to a pixel electrode, and the second electrode layer588corresponds to a common electrode. The second electrode layer588is electrically connected to a common potential line provided over the same substrate as the transistor581. With the use of a common connection portion, the second electrode layer588and the common potential line can be electrically connected to each other through conductive particles arranged between the pair of substrates580and596.

Further, instead of the twisting ball, an electrophoretic element can also be used. A microcapsule having a diameter of about 10 μm to 200 μm in which transparent liquid, positively charged white microparticles, and negatively charged black microparticles are encapsulated, is used. In the microcapsule which is provided between the first electrode layer and the second electrode layer, when an electric field is applied by the first electrode layer and the second electrode layer, the white microparticles and the black microparticles move to opposite sides, so that white or black can be displayed. A display element using this principle is an electrophoretic display element and is generally called electronic paper. The electrophoretic display element has higher reflectance than a liquid crystal display element, and thus, an auxiliary light is unnecessary, power consumption is low, and a display portion can be recognized in a dim place. Further, even when power is not supplied to the display portion, an image which has been displayed once can be maintained. Accordingly, a displayed image can be stored even if a semiconductor device having a display function (which may simply be referred to as a display device or a semiconductor device provided with a display device) is distanced from an electric wave source.

Through the above steps, an electronic paper including any of the transistors described in Embodiment 1 or 2 can be manufactured. The electronic paper described in this embodiment includes the transistor having favorable electric characteristics and high reliability described in Embodiment 1 or 2; therefore, the electronic paper having favorable quality can be provided.

This embodiment can be combined with any of the structures described in the other embodiments as appropriate.

In this embodiment, as an example of a semiconductor device, a memory medium (a memory element) will be described. In this embodiment, the transistor using an oxide semiconductor described in Embodiment 1 and a transistor including a material other than an oxide semiconductor are formed over one substrate.

FIGS. 10A to 10Cillustrate an example of a structure of a semiconductor device.FIG. 10Aillustrates a cross section of the semiconductor device, andFIG. 10Billustrates a plan view of the semiconductor device. Here,FIG. 10Aillustrates a cross section taken along line A1-A2and line B1-B2inFIG. 10B.FIG. 10Cillustrates an example of a diagram of a circuit including the semiconductor device as a memory element. The semiconductor device illustrated inFIGS. 10A and 10Bincludes a transistor160including a first semiconductor material in a lower portion, and a transistor including a second semiconductor material in an upper portion. In this embodiment, the transistor160which is a first transistor includes a semiconductor material other than an oxide semiconductor. As a second transistor, the transistor400including an oxide semiconductor which is described in Embodiment 1 is used. As the semiconductor material other than an oxide semiconductor, for example, silicon, germanium, silicon germanium, silicon carbide, gallium arsenide, or the like can be used, and a single crystal semiconductor is preferably used. A transistor including such a semiconductor material other than an oxide semiconductor can operate at high speed easily. On the other hand, the transistor400including an oxide semiconductor can hold charge for a long time because of its characteristics. Note that as the second transistor, the transistor described in Embodiment 1 or 2 can be used as appropriate.

The transistor160inFIGS. 10A to 10Cincludes a channel formation region116provided in a substrate301including a semiconductor material (such as silicon), impurity regions118provided such that the channel formation region116is sandwiched therebetween, metal compound regions124in contact with the impurity regions118, a gate insulating layer108provided over the channel formation region116, and a gate electrode109provided over the gate insulating layer108.

As the substrate301including a semiconductor material, a single crystal semiconductor substrate or a polycrystalline semiconductor substrate made of silicon, silicon carbide, or the like; a compound semiconductor substrate made of silicon germanium or the like; an SOI substrate; or the like can be used. Note that although the term “SOI substrate” generally means a substrate in which a silicon semiconductor layer is provided on an insulating surface, the term “SOI substrate” in this specification and the like also includes a substrate in which a semiconductor layer including a material other than silicon is provided on an insulating surface. That is, a semiconductor layer included in the “SOI substrate” is not limited to a silicon semiconductor layer. Moreover, the SOI substrate can be a substrate having a structure in which a semiconductor layer is provided over an insulating substrate such as a glass substrate, with an insulating layer interposed therebetween.

An electrode126is connected to part of the metal compound region124of the transistor160. Here, the electrode126functions as a source electrode or a drain electrode of the transistor160. Further, an element isolation insulating layer106is formed so as to surround the transistor160, and an insulating layer128is formed to cover the transistor160. Note that in order to realize higher integration, the transistor160preferably has a structure without a sidewall insulating layer as illustrated inFIGS. 10A. On the other hand, when importance is put on the characteristics of the transistor160, sidewall insulating layers may be provided on side surfaces of the gate electrode109, and the impurity region118may include regions with different impurity concentrations.

The transistor160can be formed by a known technique. A feature of the transistor160including, for example, silicon, germanium, silicon germanium, silicon carbide, gallium arsenide, or the like, as a semiconductor material is that it can operate at high speed. Thus, when the transistor is used as a reading transistor, data can be read at a high speed.

After the transistor160is formed, as treatment prior to the formation of the transistor400and a capacitor164, the insulating layer128is subjected to CMP treatment so that the top surface of the gate electrode109is exposed. As treatment for exposing the top surface of the gate electrode109, as well as CMP treatment, etching treatment or the like can be employed; in order to improve characteristics of the transistor400, the surface of the insulating layer128is preferably made as planar as possible.

Next, an insulating film and a conductive film are stacked over the gate electrode109, the insulating layer128, and the like. A mask formed over the conductive film is reduced (slimmed) by a plasma treatment or the like, and the insulating film and the conductive film are processed using the mask, whereby the insulating film101having a projection is formed and the gate electrode111is formed over the top surface of the projection of the insulating film101. After formation of the gate electrode111, by a method similar to that described in Embodiment 1, the gate insulating film120and the oxide semiconductor film140are formed. After that, the insulating film101, the gate insulating film120, and the oxide semiconductor film140are selectively etched, whereby the gate electrode109of the transistor160and the electrode126are exposed.

Note that as illustrated inFIG. 10A, in the case where the insulating film101, the gate insulating film120, and the oxide semiconductor film140are processed so as to expose part of the insulating layer128, the material and etching conditions are adjusted as appropriate so that the insulating layer128is not removed. Note that depending on the material and etching conditions, part of the insulating layer128which is exposed is partially etched in some cases. Further, this embodiment is not limited to the structure illustrated inFIG. 10A. The insulating film101, the gate insulating film120, and the oxide semiconductor film140may be processed so that an end portion of the insulating film101overlaps with the gate electrode109and/or the electrode126. Alternatively, an opening portion (a contact hole) is formed in the insulating film101, the gate insulating film120, and the oxide semiconductor film140, whereby the gate electrode109and the electrode126may be partially exposed.

After that, a conductive film is formed so as to cover the gate electrode109, the electrode126, the insulating layer128, the oxide semiconductor film140, and the like, which are exposed, and the conductive film is processed in a manner similar to the method described in Embodiment 1, thereby forming the source or drain electrode130aand the source or drain electrode130b. The source or drain electrode130ais electrically connected to the gate electrode109of the transistor160. The source or drain electrode130bis electrically connected to the electrode126of the transistor160.

In the semiconductor device illustrated inFIG. 10A, an insulating layer157is provided over the transistor400, and a conductive layer158is provided over the insulating layer157so as to at least partially overlap with the source or drain electrode130a. That is, the conductive layer158functions as one of electrodes of the capacitor164. The insulating layer157can be formed using the same material as the gate insulating film120, and the conductive layer158can be formed using the same material as the gate electrode111.

An insulating layer150is provided over the insulating layer157and the conductive layer158. A wiring154is provided over the insulating layer150. The wiring154is connected to the source or drain electrode130bthrough an opening portion formed in the insulating layer157, the insulating layer150, or the like. The wiring154is provided so as to overlap with at least part of the oxide semiconductor film140of the transistor400. Further, an insulating layer156is provided so as to cover the wiring154. Note that at least one of the insulating layer157and the insulating layer150is preferably an insulating film from which oxygen can be released by heat treatment. With the use of the insulating film, oxygen can be supplied to the oxide semiconductor film140, so that oxygen deficiency in the oxide semiconductor film140can be filled.

In the semiconductor device illustrated inFIG. 10A, the transistor160and the transistor400are provided so as to at least partially overlap with each other. In particular, a source region or a drain region of the transistor160is provided so as to overlap with part of the oxide semiconductor film140. Further, the wiring154is provided so as to overlap with at least part of the oxide semiconductor film140. In addition, the transistor400and the capacitor164are provided so as to overlap with the transistor160. For example, the conductive layer158of the capacitor164is provided so as to at least partially overlap with the gate electrode109of the transistor160. With such a planar layout, the semiconductor device can be highly integrated. For example, in the case of forming a memory cell using the semiconductor device, given that the minimum feature size is F, the area occupied by a memory cell can be 15 F2to 25 F2.

In addition,FIG. 10Cillustrates an example of a diagram of a circuit using the semiconductor device as a memory element. InFIG. 10C, one of a source electrode and drain electrode of the transistor400, one electrode of the capacitor164, and a gate electrode of the transistor160are electrically connected to one another. A first wiring (a 1st line, also referred to as a source line) is electrically connected to a source electrode of the transistor160. A second wiring (a 2nd line, also referred to as a bit line) is electrically connected to a drain electrode of the transistor160. A third wiring (a 3rd line, also referred to as a first signal line) is electrically connected to the source or drain electrode of the transistor400. A fourth wiring (a 4th line, also referred to as a second signal line) is electrically connected to the gate electrode of the transistor400. A fifth wiring (a 5th line, also referred to as a word line) and the other electrode of the capacitor164are electrically connected to each other.

The transistor400including an oxide semiconductor has extremely low off current; therefore, when the transistor400is turned off, the potential of a node (hereinafter, a node FG) where one of the source electrode and drain electrode of the transistor400, one electrode of the capacitor164, and the gate electrode of the transistor160are electrically connected to each other can be held for an extremely long time. The capacitor164facilitates holding of charge given to the node FG and reading of the held data.

When data is stored in the semiconductor device (writing), first, the potential of the fourth wiring is set to a potential at which the transistor400is turned on, whereby the transistor400is turned on. Thus, the potential of the third wiring is applied to the node FG and a predetermined amount of charge is accumulated in the node FG. Here, charge for applying either two different potential levels (hereinafter referred to as low-level charge and high-level charge) is given to the node FG. After that, the potential of the fourth wiring is set to a potential at which the transistor400is turned off, whereby the transistor400is turned off. This makes the node FG floating and the predetermined amount of charge remains held in the node FG. The predetermined amount of charge is thus accumulated and held in the node FG, whereby the memory cell can store data.

Since the off current of the transistor400is extremely small, the charge supplied to the node FG is held for a long time. This can remove the need of refresh operation or drastically reduce the frequency of the refresh operation, which leads to a sufficient reduction in power consumption. Moreover, stored data can be stored for a long time even when power is not supplied.

When stored data is read out (reading), while a predetermined potential (a fixed potential) is applied to the first wiring, an appropriate potential (a read-out potential) is applied to the fifth wiring, whereby the transistor160changes its state depending on the amount of charge held in the node FG. This is because, in general, when the transistor160is an n-channel transistor, an apparent threshold voltage Vth—Hof the transistor160in the case where a high-level charge is held in the node FG is lower than an apparent threshold voltage Vth—Lof the transistor160in the case where a low-level charge is held in the node FG. Here, an apparent threshold voltage refers to the potential of the fifth line, which is needed to turn on the transistor160. Thus, by setting the potential of the fifth wiring to a potential V0which is between Vth—Hand Vth—L, charge held in the node FG can be determined For example, in the case where a high-level charge is given in writing, when the potential of the fifth wiring is set to V0(>Vth—H), the transistor160is turned on. In the case where a low level charge is given in writing, even when the potential of the fifth wiring is set to V0(<Vth—L), the transistor160remains in an off state. In such a manner, by controlling the potential of the fifth wiring and determining whether the transistor160is in an on state or off state (reading out the potential of the second wiring), stored data can be read out.

Further, in order to rewrite stored data, a new potential is applied to the node FG that is holding the predetermined amount of charge given in the above writing, so that the charge of the new data is held in the node FG. Specifically, the potential of the fourth wiring is set to a potential at which the transistor400is turned on, whereby the transistor400is turned on. The potential of the third wiring (a potential of new data) is applied to the node FG, and the predetermined amount of charge is accumulated in the node FG. After that, the potential of the fourth wiring is set to a potential at which the transistor400is turned off, whereby the transistor400is turned off. Thus, charge of the new data is held in the node FG. In other words, while the predetermined amount of charge given in the first writing is held in the node FG, the same operation (a second writing) as in the first writing is performed, whereby the stored data can be overwritten.

The off current of the transistor400described in this embodiment can be sufficiently reduced by using the highly-purified, and intrinsic oxide semiconductor film140. Then, by using such a transistor, a semiconductor device in which stored data can be stored for an extremely long time can be obtained. Further, with the use of the transistor400whose channel length (L) is reduced, the degree of integration of the semiconductor device can be increased.

In the semiconductor device described in this embodiment, the transistor160and the transistor400are overlapping with each other; therefore, a semiconductor device in which the degree of integration is sufficiently improved can be realized.

A semiconductor device disclosed in this specification can be applied to a variety of electronic devices (including game machines). Examples of electronic devices are a television set (also referred to as a television or a television receiver), a monitor of a computer or the like, a camera such as a digital camera or a digital video camera, a digital photo frame, a mobile phone handset (also referred to as a mobile phone or a mobile phone device), a portable game console, a portable information terminal, an audio reproducing device, a large-sized game machine such as a pachinko machine, and the like.

In this embodiment, examples of an electronic device on which a transistor with favorable electric characteristics and high reliability which can be obtained in any of the above embodiments is mounted will be described with reference toFIGS. 11A to 11E.

FIG. 11Aillustrates a laptop personal computer, which includes a main body3001, a housing3002, a display portion3003, a keyboard3004, and the like. Note that the laptop personal computer includes a semiconductor device. The semiconductor device includes the transistor described in any of the above embodiments. Therefore, the laptop personal computer with favorable quality and high reliability can be realized.

FIG. 11Billustrates a portable information terminal (PDA) which includes a display portion3023, an external interface3025, operation buttons3024, and the like in a main body3021. A stylus3022is included as an accessory for operation. Note that the portable information terminal (PDA) includes a semiconductor device. The semiconductor device includes the transistor described in any of the above embodiments. Therefore, the portable information terminal (PDA) with favorable quality and high reliability can be realized.

FIG. 11Cillustrates an e-book reader on which the electronic paper described in Embodiment 4 is mounted as a component.FIG. 11Cillustrates an example of an e-book reader. For example, the e-book reader2700includes two housings, a housing2701and a housing2703. The housings2701and2703are bound with each other by an axis portion2711, along which the e-book reader2700can be opened and closed. With such a structure, the e-book reader2700can operate like a paper book.

A display portion2705and a display portion2707are incorporated in the housing2701and the housing2703, respectively. The display portion2705and the display portion2707may display one image or different images. In the structure where different images are displayed on different display portions, for example, the right display portion (the display portion2705inFIG. 11C) can display text and the left display portion (the display portion2707inFIG. 11C) can display graphics. At least one of the housings2701and2703includes a semiconductor device. The semiconductor device includes the transistor described in any of the above embodiments. Therefore, the e-book reader with favorable quality and high reliability can be realized.

FIG. 11Cillustrates an example in which the housing2701is provided with an operation portion and the like. For example, the housing2701is provided with a power switch2721, operation keys2723, a speaker2725, and the like. With the operation key2723, pages can be turned. Note that a keyboard, a pointing device, or the like may also be provided on the surface of the housing, on which the display portion is provided. Further, a rear surface or a side surface of the housing may be provided with an external connection terminal (an earphone terminal, a USB terminal, a terminal which can be connected with an AC adapter or a variety of cables such as a USB cable), a storage medium inserting portion, or the like. Moreover, the e-book reader2700may have a function of an electronic dictionary.

The e-book reader2700may have a configuration capable of wirelessly transmitting and receiving data. Through wireless communication, desired book data or the like can be purchased and downloaded from an electronic book server.

FIG. 11Dillustrates a mobile phone, which includes two housings, a housing2800and a housing2801. The housing2801includes a display panel2802, a speaker2803, a microphone2804, a pointing device2806, a camera lens2807, an external connection terminal2808, and the like. The housing2801is provided with a solar battery cell2810for charging of the portable information terminal, an external memory slot2811, and the like. Further, an antenna is incorporated in the housing2801. Note that the mobile phone includes the transistor described in any of the above embodiments at least as a component.

The display panel2802is provided with a touch panel. A plurality of operation keys2805which is displayed as images is illustrated by dashed lines inFIG. 11D. Note that a boosting circuit by which a voltage output from the solar battery cell2810is increased to be sufficiently high for each circuit is also included. Note that a boosting circuit by which a voltage output from the solar battery cell2810is increased to be a voltage necessary for each circuit is also included.

In the display panel2802, the display direction can be appropriately changed depending on a usage pattern. Further, the mobile phone is provided with the camera lens2807on the same surface as the display panel2802, and thus it can be used as a video phone. The speaker2803and the microphone2804can be used for videophone calls, recording and playing sound, and the like as well as voice calls. Moreover, the housings2800and2801in a state where they are developed as illustrated inFIG. 11Dcan shift by sliding so that one is lapped over the other; therefore, the size of the mobile phone can be reduced, which makes the mobile phone suitable for being carried.

The external connection terminal2808can be connected to an AC adapter and various types of cables such as a USB cable, and charging and data communication with a personal computer are possible. Moreover, a large amount of data can be stored by inserting a storage medium into the external memory slot2811and can be transferred. As the recording medium, the semiconductor device described in Embodiment 5 can be used. According to Embodiment 5, with the use of the transistor in which the off current can be sufficiently reduced, a semiconductor device capable of holding stored data for an extremely long time can be obtained.

Further, in addition to the above functions, an infrared communication function, a television reception function, or the like may be provided.

FIG. 11Eis a digital camera which includes a main body3051, a display portion (A)3057, an eyepiece3053, operation switches3054, a display portion (B)3055, a battery3056, and the like. Note that the digital camera includes a semiconductor device. The semiconductor device includes the transistor described in any of the above embodiments. Therefore, the digital camera with favorable quality and high reliability can be realized.

As described above, the electronic devices described in this embodiment each include the semiconductor device described in any of the above embodiments. Therefore, electronic devices having favorable qualities can be realized.

One embodiment of an oxide semiconductor film that can be used for the semiconductor layers of the transistors in Embodiments 1 to 6 will be described with reference toFIGS. 12A to 12C.

The oxide semiconductor film of this embodiment has a stacked-layer structure including a first crystalline oxide semiconductor film and a second crystalline oxide semiconductor film thereover which is thicker than the first crystalline oxide semiconductor film.

An insulating layer437is formed over an insulating layer420. In this embodiment, an oxide insulating layer with a thickness greater than or equal to 50 nm and less than or equal to 600 nm is formed as the insulating layer437by a PCVD method or a sputtering method. For example, a single layer selected from a silicon oxide film, a gallium oxide film, an aluminum oxide film, a silicon oxynitride film, an aluminum oxynitride film, and a silicon nitride oxide film or a stack of any of these films can be used.

Next, a first oxide semiconductor film with a thickness greater than or equal to 1 nm and less than or equal to 10 nm is formed over the insulating layer437. The first oxide semiconductor film is formed by a sputtering method, and the substrate temperature in the film formation by a sputtering method is set to be higher than or equal to 200° C. and lower than or equal to 400° C.

In this embodiment, the first oxide semiconductor film is formed to a thickness of 5 nm in an oxygen atmosphere, an argon atmosphere, or an atmosphere including argon and oxygen under conditions where a deposition target for an oxide semiconductor (a target for an In—Ga—Zn-based oxide semiconductor including In2O3, Ga2O3, and ZnO at 1:1:2 [molar ratio]) is used, the distance between the substrate and the target is 170 mm, the substrate temperature is 250° C., the pressure is 0.4 Pa, and the direct current (DC) power is 0.5 kW.

Then, first heat treatment is performed with the substrate placed in an atmosphere of nitrogen or dry air. The temperature of the first heat treatment is higher than or equal to 400° C. and lower than or equal to 750° C. Through the first heat treatment, a first crystalline oxide semiconductor film450ais formed (seeFIG. 12A).

Depending on the substrate temperature at the time of deposition or the temperature of the first heat treatment, the deposition or the first heat treatment causes crystallization from a film surface and crystal grows from the film surface toward the inside of the film; thus, c-axis aligned crystal is obtained. By the first heat treatment, large amounts of zinc and oxygen gather to the film surface, and one or more layers of graphene-type two-dimensional crystal including zinc and oxygen and having a hexagonal upper plane are formed at the outermost surface; the layer(s) at the outermost surface grow in the thickness direction to form a stack of layers. By increasing the temperature of the heat treatment, crystal growth proceeds from the surface to the inside and further from the inside to the bottom.

By the first heat treatment, oxygen in the insulating layer437that is an oxide insulating layer is diffused to an interface between the insulating layer437and the first crystalline oxide semiconductor film450aor the vicinity of the interface (within ±5 nm from the interface), whereby oxygen deficiency in the first crystalline oxide semiconductor film is reduced. Therefore, it is preferable that oxygen be included in (in a bulk of) the insulating layer437used as a base insulating layer or at the interface between the first crystalline oxide semiconductor film450aand the insulating layer437at an amount that exceeds at least the amount of oxygen in the stoichiometric composition ratio.

Next, a second oxide semiconductor film with a thickness more than 10 nm is formed over the first crystalline oxide semiconductor film450a. The second oxide semiconductor film is formed by a sputtering method, and the substrate temperature in the film formation is set to be higher than or equal to 200° C. and lower than or equal to 400° C. By setting the substrate temperature in the film formation to be higher than or equal to 200° C. and lower than or equal to 400° C., precursors can be arranged in the oxide semiconductor film formed over and in contact with the surface of the first crystalline oxide semiconductor film and so-called orderliness can be obtained.

In this embodiment, the second oxide semiconductor film is formed to a thickness of 25 nm in an oxygen atmosphere, an argon atmosphere, or a mixed atmosphere of argon and oxygen under conditions that a target for an oxide semiconductor (a target for an In—Ga—Zn—O-based oxide semiconductor containing In2O3, Ga2O3, and ZnO at 1:1:2 [molar ratio]) is used, the distance between the substrate and the target is 170 mm, the substrate temperature is 400° C., the pressure is 0.4 Pa, and the direct current (DC) power source is 0.5 kW.

Then, second heat treatment is performed with the substrate placed in an atmosphere of nitrogen atmosphere, an oxygen atmosphere or a mixed atmosphere of nitrogen and oxygen. The temperature of the second heat treatment is higher than or equal to 400° C. and lower than or equal to 750° C. Through the second heat treatment, a second crystalline oxide semiconductor film450bis formed (seeFIG. 12B). The second heat treatment is performed in a nitrogen atmosphere, an oxygen atmosphere, or a mixed atmosphere of nitrogen and oxygen, whereby the density of the second crystalline oxide semiconductor film is increased. The second heat treatment is preferably performed in an atmosphere containing oxygen because defects in the second crystalline oxide semiconductor film450bare reduced. By the second heat treatment, crystal growth proceeds in the thickness direction with the use of the first crystalline oxide semiconductor film450aas a nucleus, that is, crystal growth proceeds from the bottom to the inside; thus, the second crystalline oxide semiconductor film450bis formed.

It is preferable that steps from the formation of the insulating layer437to the second heat treatment be successively performed without exposure to the air. The steps from the formation of the insulating layer437to the second heat treatment are preferably performed in an atmosphere which is controlled to include little hydrogen and moisture (such as an inert gas atmosphere, a reduced-pressure atmosphere, or a dry-air atmosphere); in terms of moisture, for example, a dry nitrogen atmosphere with a dew point of lower than or equal to −40° C., preferably a dew point of lower than or equal to −50° C. may be employed.

Next, the stack of the oxide semiconductor layers, the first crystalline oxide semiconductor film450aand the second crystalline oxide semiconductor film450b, is processed into an oxide semiconductor film453including a stack of island-shaped oxide semiconductor layers (seeFIG. 12C). In the drawing, the interface between the first crystalline oxide semiconductor film450aand the second crystalline oxide semiconductor film450bis indicated by a dotted line, and the first crystalline oxide semiconductor film450aand the second crystalline oxide semiconductor film450bare illustrated as a stack of oxide semiconductor layers; however, the interface is actually not distinct and is illustrated for easy understanding.

The stack of the oxide semiconductor layers can be processed by being etched after a mask having a desired shape is formed over the stack of the oxide semiconductor layers. The mask may be formed by a method such as photolithography or an ink-jet method.

For the etching of the stack of oxide semiconductor layers, either wet etching or dry etching may be employed. It is needless to say that both of them may be employed in combination.

Further, one feature of the first crystalline oxide semiconductor film and the second crystalline oxide semiconductor film obtained by the above formation method is that they have c-axis alignment. Note that the first crystalline oxide semiconductor layer and the second crystalline oxide semiconductor layer comprise an oxide including a crystal with c-axis alignment (also referred to as C-Axis Aligned Crystal (CAAC)), which has neither a single crystal structure nor an amorphous structure. Further, the first crystalline oxide semiconductor film and the second crystalline oxide semiconductor film partly include a crystal grain boundary.

Without limitation to the two-layer structure in which the second crystalline oxide semiconductor film is formed over the first crystalline oxide semiconductor film, a stacked-layer structure including three or more layers may be formed by repeatedly performing a process of film formation and heat treatment for forming a third crystalline oxide semiconductor film after the second crystalline oxide semiconductor film is formed.

The oxide semiconductor film453including the stack of the oxide semiconductor layers formed by the above formation method can be used as appropriate for a transistor (e.g., the transistor in Embodiment 1 and Embodiment 2) which can be applied to a semiconductor device disclosed in this specification.

In the transistor4011according to Embodiment 3, in which the stack of the oxide semiconductor layers of this embodiment is used as the oxide semiconductor film453, an electric field is not applied from one surface to the other surface of the oxide semiconductor film and current does not flow in the thickness direction (from one surface to the other surface; specifically, in the vertical direction in the transistor4011inFIG. 8B) of the stack of the oxide semiconductor layers. The transistor has a structure in which current mainly flows along the interface of the stack of the oxide semiconductor layers; therefore, even when the transistor is irradiated with light or even when a BT stress is applied to the transistor, deterioration of transistor characteristics is suppressed or reduced.

By forming a transistor with the use of a stack of the first crystalline oxide semiconductor film and the second crystalline oxide semiconductor film, like the oxide semiconductor film453, the transistor can have stable electric characteristics and high reliability.

This application is based on Japanese Patent Application Serial No. 2010-204187 filed with Japan Patent Office on Sep. 13, 2010, the entire contents of which are hereby incorporated by reference.