Ceramic capacitor, circuit substrate and manufacturing method of the same

A ceramic capacitor includes: a multilayer structure in which each of a plurality of dielectric layers and each of a plurality of internal electrode layers are alternately stacked, wherein a main component of the plurality of dielectric layers is ceramic having a perovskite structure expressed by BamTiO3 (0.9990≤m≤1.0015), wherein the plurality of dielectric layers include Mn as a first sub-component, Mg as a second sub-component, a rare earth element which is at least one of Ho and Dy as a third sub-component, V as a fourth sub-component, Si as a fifth sub-component, Ca as a sixth sub-component, wherein an average grain diameter of ceramic grains of the plurality of dielectric layers is 280 nm or more and 380 nm or less.

CROSS-REFERENCE TO RELATED APPLICATION

This application is based upon and claims the benefit of priority of the prior Japanese Patent Application No. 2018-011552, filed on Jan. 26, 2018, the entire contents of which are incorporated herein by reference.

FIELD

A certain aspect of the present invention relates to a ceramic capacitor, a circuit substrate and a manufacturing method of the ceramic capacitor.

BACKGROUND

Ceramic capacitors are widely used under a high temperature condition such as in cars. And so, the ceramic capacitors are required to have capacity stability at a high temperature, high reliability under high temperature load, and so on. Recently, it is one of important properties that the ceramic capacitors satisfy X7R characteristic of EIA standard. A capacity changing rate is within ±15% in a temperature ranges from −55 degrees C. to +125 degrees C. with respect to 25 degrees C., in the EIA standard. And so, there is disclosed a dielectric material, in which a composition or a micro structure is adjusted or designed, satisfies the X7R characteristic (for example, see Japanese Patent Application Publication No. 2010-199268).

SUMMARY OF THE INVENTION

However, it is difficult to achieve both the capacity stability and the high reliability, even if the technology of Japanese Patent Application Publication No. 2010-199268 is used.

The present invention has a purpose of providing a ceramic capacitor and a circuit substrate that are capable of achieving both capacity stability and high reliability and a manufacturing method of the ceramic capacitor.

According to an aspect of the present invention, there is provided a ceramic capacitor including: a multilayer structure in which each of a plurality of dielectric layers and each of a plurality of internal electrode layers are alternately stacked, wherein a main component of the plurality of dielectric layers is ceramic having a perovskite structure expressed by BamTiO3(0.9990≤m≤1.0015), wherein the plurality of dielectric layers include 0.05 atm % or more and 0.35 atm % or less of Mn as a first sub-component, 0.4 atm % or more and 0.8 atm % or less of Mg as a second sub-component, 0.5 atm % or more and 0.9 atm % or less of a rare earth element which is at least one of Ho and Dy as a third sub-component, 0.15 atm % or more and 0.30 atm % or less of V as a fourth sub-component, 0.4 atm % or more and 0.9 atm % or less of Si as a fifth sub-component, 0.00 atm % or more and 0.45 atm % or less of Ca as a sixth sub-component, on a presumption that an amount of Ti of the perovskite structure is 100 atm %, wherein an average grain diameter of ceramic grains of the plurality of dielectric layers is 280 nm or more and 380 nm or less.

According to an aspect of the present invention, there is provided a manufacturing method of a ceramic capacitor including: forming a green sheet by adding Mn as a first sub-component by 0.05 atm % or more and 0.35 atm % or less, adding Mg as a second sub-component by 0.4 atm % or more and 0.8 atm % or less, adding a rare earth element which is at least one of Ho and Dy as a third sub-component by 0.5 atm % or more and 0.9 atm % or less, adding V as a fourth sub-component by 0.15 atm % or more and 0.30 atm % or less, adding Si as a fifth sub-component by 0.4 atm % or more and 0.9 atm % or less, adding Ca as a sixth sub-component by 0.00 atm % or more and 0.45 atm % or less, to ceramic powder having a perovskite structure expressed by BamTiO3(0.9990≤m≤1.0015), on a presumption that an amount of Ti of the perovskite structure is 100 atm %; arranging a metal conductive paste for forming an internal electrode, on the green sheet; and firing the green sheet on which the metal conductive paste was arranged, wherein a condition of the firing is adjusted so that an average grain diameter of the BamTiO3is 280 nm or more and 380 nm or less in dielectric layers formed in the firing.

DETAILED DESCRIPTION

A description will be given of an embodiment with reference to the accompanying drawings.

Embodiment

FIG. 1illustrates a partial perspective view of a multilayer ceramic capacitor100in accordance with an embodiment. As illustrated inFIG. 1, the multilayer ceramic capacitor100includes a ceramic main body10having a rectangular parallelepiped shape, and a pair of external electrodes20aand20bthat are respectively provided at two edge faces of the ceramic main body10facing each other. In four faces other than the two edge faces of the ceramic main body10, two faces other than an upper face and a lower face of the ceramic main body10in a stacking direction are referred to as side faces. The external electrodes20aand20bextend to the upper face, the lower face and the two side faces of the ceramic main body10. However, the external electrodes20aand20bare spaced from each other.

The ceramic main body10has a structure designed to have dielectric layers11and internal electrode layers12alternately stacked. The dielectric layer11includes ceramic material acting as a dielectric material. The internal electrode layers12include a base metal material. End edges of the internal electrode layers12are alternately exposed to a first edge face of the ceramic main body10and a second edge face of the ceramic main body10that is different from the first edge face. In the embodiment, the first face faces with the second face. The external electrode20ais provided on the first edge face. The external electrode20bis provided on the second edge face. Thus, the internal electrode layers12are alternately conducted to the external electrode20aand the external electrode20b. Thus, the multilayer ceramic capacitor100has a structure in which a plurality of dielectric layers11are stacked and each two of the dielectric layers11sandwich the internal electrode layer12. In the ceramic main body10, the internal electrode layer12is positioned at an outermost layer. The upper face and the lower face of the ceramic main body10that are the internal electrode layers12are covered by cover layers13. A main component of the cover layer13is a ceramic material. For example, a main component of the cover layer13is the same as that of the dielectric layer11.

For example, the multilayer ceramic capacitor100may have a length of 0.25 mm, a width of 0.125 mm and a height of 0.125 mm. The multilayer ceramic capacitor100may have a length of 0.4 mm, a width of 0.2 mm and a height of 0.2 mm. The multilayer ceramic capacitor100may have a length of 0.6 mm, a width of 0.3 mm and a height of 0.3 mm. The multilayer ceramic capacitor100may have a length of 1.0 mm, a width of 0.5 mm and a height of 0.5 mm. The multilayer ceramic capacitor100may have a length of 3.2 mm, a width of 1.6 mm and a height of 1.6 mm. The multilayer ceramic capacitor100may have a length of 4.5 mm, a width of 3.2 mm and a height of 2.5 mm. However, the size of the multilayer ceramic capacitor100is not limited.

A main component of the internal electrode layers12is a base metal such as nickel (Ni), copper (Cu), tin (Sn) or the like. The internal electrode layers12may be made of a noble metal such as platinum (Pt), palladium (Pd), silver (Ag), gold (Au) or alloy thereof. The dielectric layers11are mainly composed of a ceramic material that is expressed by a general formula ABO3and has a perovskite structure. The perovskite structure includes ABO3-αhaving an off-stoichiometric composition. The perovskite structure is barium titanate including Ba (barium) and Ti (titanium) and is expressed by a formula BamTiO3. Barium titanate is a ferroelectric material and achieves a high dielectric constant.

In the multilayer ceramic capacitor100, the dielectric layers11include sub-components. Thus, the multilayer ceramic capacitor100achieves both capacity stability and high reliability. A description will be given of details of the sub-components added to the dielectric layers11.

The dielectric layers11include Mn (manganese) as a first sub-component. Mn achieves preferable sintering characteristic and has a function of improving life property of the multilayer ceramic capacitor100. It is therefore possible to achieve the high reliability of the multilayer ceramic capacitor100. However, when an amount of Mn is excessively small, the high reliability may not be necessarily achieved. On the other hand, when the amount of Mn is excessively large, insulation characteristic may be degraded and the reliability may be degraded because of reduction of boundary resistance of ceramic grains. And so, a Mn concentration in the dielectric layers11has an upper limit and a lower limit. In concrete, the dielectric layers11include 0.05 atm % or more and 0.35 atm % or less of Mn, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. It is preferable that the dielectric layers11include 0.10 atm % or more and 0.30 atm % or less of Mn, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

Next, the dielectric layers11include Mg (magnesium) as a second sub-component. Mg has a function of controlling grain growth during firing and achieves the capacity stability and the high reliability. However, when an amount of Mg is excessively small, sufficient capacity stability may not be necessarily achieved. And, grain growth may occur during sintering, and the reliability may be degraded. On the other hand, when the amount of Mg is excessively large, the reliability may be degraded because of excessive amount of acceptors. And so, a Mg concentration of the dielectric layers11has an upper limit and a lower limit. In concrete, the dielectric layers11include 0.4 atm % or more and 0.8 atm % or less of Mg, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. It is preferable that the dielectric layers11include 0.5 atm % or more and 0.7 atm % or less of Mg, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

The dielectric layers11include a rare earth element Re which is at least one of Ho (holmium) and Dy (dysprosium), as a third sub-component. The rare earth element Re has a function of adjusting balance between sites in which an additive element is solid-solved (A site and B site) and achieves the high reliability. However, when an amount of the rare earth element Re is excessively small, sufficient reliability may not be necessarily achieved. On the other hand, when the amount of Re is excessively large, sintering characteristic of the dielectric layers11may be degraded and sufficient reliability may not be necessarily achieved because of increasing of sintering temperature of ceramic. And so, a concentration of the rare earth element Re of the dielectric layers11has an upper limit and a lower limit. In the following, the concentration of the rare earth element Re is a total concentration of Ho and Dy. In concrete, the dielectric layers11include 0.5 atm % or more and 0.9 atm % or less of the rare earth element Re, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. It is preferable that the dielectric layers11include 0.6 atm % or more and 0.8 atm % or less of the rare earth element Re, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

The dielectric layers11include V (vanadium) as a fourth sub-component. V has a function of suppressing oxygen defect occurrence, controlling of a micro structure of ceramic, and so on. And, V achieves the high reliability and the capacity stability. However, when an amount of V is excessively small, sufficient high reliability and sufficient capacity stability may not be necessarily achieved. On the other hand, when the amount of V is excessively large, sufficient capacity stability may not be necessarily achieved because of reduction of electric resistance or not achieving of desirable micro structure of ceramic. And so, a V concentration of the dielectric layers11has an upper limit and a lower limit. In concrete, the dielectric layers11include 0.15 atm % or more and 0.30 atm % or less of V, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. It is preferable that the dielectric layers11include 0.18 atm % or more and 0.27 atm % or less of V, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

The dielectric layers11include Si (silicon) as a fifth sub-component. Si achieves preferable sintering because Si acts as a sintering assistant. However, when an amount of Si is excessively small, sintering at an adequate temperature (for example, 1260 degrees C. or less) may be difficult and the dielectric layers11may not be necessarily formed. On the other hand, when the amount of Si is excessively large, grain growth may occur during the firing and sufficient capacity stability may not be necessarily achieved because of excessive occurrence of a liquid phase component. And so, a Si concentration of the dielectric layers11has an upper limit and a lower limit. In concrete, the dielectric layers11include 0.4 atm % or more and 0.9 atm % or less of Si, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. It is preferable that the dielectric layers11include 0.5 atm % or more and 0.8 atm % or less of Si, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

The dielectric layers11include Ca (calcium) as a sixth sub-component. Ca acts as a sintering assistant. It is possible to use Ca for adjusting an A/B ratio which is a molar ratio of A site element and B site element. However, when an amount of Ca is excessively large, sufficient capacity stability may not be necessarily achieved because of excessive amount of the A site component. And so, a Ca concentration of the dielectric layers11has an upper limit. In concrete, the dielectric layers11include 0.00 atm % or more and 0.45 atm % or less of Ca, on a presumption that an amount of Ti of BamTiO3acting as a main component of the dielectric layers11is 100 atm %. “0.00 atm % or more” means that there may be a case where the dielectric layers11does not include Ca. It is preferable that the dielectric layers11include 0.10 atm % or more and 0.40 atm % or less of Ca, on a presumption that the amount of Ti of BamTiO3acting as the main component of the dielectric layers11is 100 atm %.

When “m” of BamTiO3acting as the main component of the dielectric layers11is excessively small, the life property of the multilayer ceramic capacitor100may be degraded and high reliability may not be necessarily achieved. And so, “m” satisfies 0.9990≤m. On the other hand, “m” is excessively large, the capacity stability may not be necessarily achieved. And so, “m” satisfies m≤1.0015.

Next, when an average grain diameter of BamTiO3acting as the main component ceramic of the dielectric layers11is excessively small, the capacity stability may be degraded because of not obtaining the micro structure of ceramic. On the other hand, when the average grain diameter is excessively large, the insulation resistance may be degraded and the reliability may be degraded because of reduction of the number of grains boundaries. And so, the average grain diameter of BamTiO3has an upper limit and a lower limit. In concrete, the average grain diameter of BamTiO3is 280 nm or more and 380 nm or less. It is preferable that the average grain diameter of BamTiO3is 300 nm or more and 360 nm or less.

It is possible to calculate the average grain diameter by an arithmetical mean. For example, SEM observation is performed with a field in which 100 to 200 numbers of crystal grains can be observed. For example, a magnification factor is 40 thousand times or the like. In the obtained SEM image, grains which are visually observed are arranged in a single direction. And a diameter of the grains is measured. For example, the direction of the grains in the SEM image is unified in a lateral direction. A total of measured diameters is divided by the number of the measured grains, and an average value is calculated. The direction of the image and the direction of the measurement may be optional.

As mentioned above, the amounts of the first sub-component to the sixth sub-component are regulated in the dielectric layers11. “m” in BamTiO3is regulated. And the average grain diameter of BamTiO3is regulated. Thus, both the capacity stability and the high reliability can be achieved. The main component of the material of the cover layer13is the same as the main component of the ceramic material of the dielectric layers11. However, it is preferable that the amounts of the first sub-component to the sixth sub-component are regulated in the cover layer13, “m” in BamTiO3is regulated, and the average grain diameter of BamTiO3is regulated, as well as the dielectric layers11.

FIG. 2illustrates a circuit substrate200. As illustrated inFIG. 2, the circuit substrate200has a structure in which the multilayer ceramic capacitor100is mounted on a substrate201. A wiring pattern202a, a wiring pattern202band so on are provided on a mounting face of the substrate201. The external electrode20ais connected to the wiring pattern202avia a solder203aand is electrically coupled with the wiring pattern202a. The external electrode20bis connected to the wiring pattern202bvia a solder203band is electrically coupled with the wiring pattern202b. In this manner, the multilayer ceramic capacitor100may be mounted on the substrate201.

Next, a description will be given of a manufacturing method of the multilayer ceramic capacitor100.FIG. 3illustrates a manufacturing method of the multilayer ceramic capacitor100.

(Making Process of a Raw Material Powder)

A dielectric material for forming the dielectric layer11is prepared. Generally, an A site element and a B site element are included in the dielectric layer11in a sintered phase of grains of ABO3. For example, barium titanate is tetragonal compound having a perovskite structure and has a high dielectric constant. Generally, BaTiO3is obtained by reacting a titanium material such as titanium dioxide with a barium material such as barium carbonate and synthesizing barium titanate. The titanium material and the barium material are reacted so that “m” satisfies 0.9990≤m≤1.0015 in the general formula AmBO3expressing the perovskite structure of the barium titanate. Various methods can be used as a synthesizing method of the ceramic structuring the dielectric layer11. For example, a solid-phase method, a sol-gel method, a hydrothermal method or the like can be used. The embodiment may use any of these methods.

Additive compound may be added to the resulting ceramic powders, in accordance with purposes. The additive compound may be an oxide of Mg, Mn, V, Cr (chromium) or a rare earth element (Y (yttrium), Sm (samarium), Eu (europium), Gd (gadolinium), Tb (terbium), Dy (dysprosium), Ho, Er (erbium), Tm (thulium) and Yb (ytterbium)), or an oxide of Co (cobalt), Ni, Li (lithium), B (boron), Na (sodium), K (potassium) and Si, or glass.

In the embodiment, Mn is added as the first sub-component by 0.05 atm % or more and 0.35 atm % or less, Mg is added as the second sub-component by 0.4 atm % or more and 0.8 atm % or less, the rare earth element Re which is at least one of Ho and Dy is added as the third sub-component by 0.5 atm % or more and 0.9 atm % or less, V is added as the fourth sub-component by 0.15 atm % or more and 0.30 atm % or less, Si is added as the fifth sub-component by 0.4 atm % or more and 0.9 atm % or less, and Ca is added as the sixth sub-component by 0.00 atm % or more and 0.45 atm % or less, on a presumption that an amount of Ti of BamTiO3acting as the main component of the ceramic material is 100 atm %.

In the embodiment, it is preferable that barium titanate particles are mixed with compound including additives and are calcined in a temperature range from 820 degrees C. to 1150 degrees C. Next, the resulting ceramic particles are wet-blended with additives, are dried and crushed. Thus, ceramic powder is prepared. For example, it is preferable that an average grain diameter of the resulting ceramic powder is 200 nm to 300 nm from a viewpoint of thickness reduction of the dielectric layer11. The grain diameter may be adjusted by crushing the resulting ceramic powder as needed. Alternatively, the grain diameter of the resulting ceramic power may be adjusted by combining the crushing and classifying.

Next, a binder such as polyvinyl butyral (PVB) resin, an organic solvent such as ethanol or toluene, and a plasticizer are added to the resulting dielectric material and wet-blended. With use of the resulting slurry, a green sheet with a thickness of 3 μm to 10 μm is molded by, for example, a die coater method or a doctor blade method, and then dried.

Then, a pattern of the internal electrode layer12is provided on the surface of the dielectric green sheet by printing metal conductive pastes for forming an internal electrode with use of screen printing or gravure printing. The conductive pastes include an organic binder. A plurality of patterns are alternatively exposed to the pair of external electrodes. As co-materials, ceramic particles are added to the conductive pastes. A main component of the ceramic particles is not limited. However, it is preferable that the main component of the ceramic particles is the same as that of the dielectric layer11. For example, BaTiO3of which an average particle sire is 50 nm or less is evenly dispersed.

A cover sheet is formed by stacking a plurality of the green sheets. A plurality of the pattern-formed sheets are stacked on the cover sheet. And, another cover sheet is stacked on the plurality of the pattern-formed sheets by stacking a plurality of the green sheets. An obtained multilayer structure is stamped into a predetermined size.

The binder is removed from the compact in N2atmosphere of a temperature range of 250 degrees C. to 500 degrees C. After that, the resulting compact is fired for ten minutes to 2 hours in a reductive atmosphere having an oxygen partial pressure of 10−9to 10−12atm in a temperature range of 1100 degrees C. to 1300 degrees C. Thus, each compound of the dielectric green sheet is sintered and grown into grains. In this manner, it is possible to form the ceramic main body10. The firing condition may be adjusted so that an average grain diameter of BamTiO3acting as the main component ceramic of the dielectric layers11after the firing is 280 nm or more and 380 nm or less.

After that, a re-oxidizing process may be performed in N2gas atmosphere in a temperature range of 600 degrees C. to 1000 degrees C.

(Forming of External Electrodes)

After that, a conductive paste for forming the external electrodes20aand20bis coated on two edge faces of the obtained sintered structure to which the internal electrode layers are exposed. Cu or the like may be used as the conductive paste. The conductive paste is fired in N2atmosphere at a temperature (for example, 800 degrees C. to 900 degrees C.) lower than the firing temperature for forming the sintered structure. Thus, the external electrodes20aand20bare formed. After that, a metal such as Cu, Ni, Sn or the like may be coated by plating. The conductive paste for forming the external electrodes20aand20bmay be coated on the two edge faces before the firing process, and the multilayer structure and the conductive paste may be fired in the firing process together with each other.

In the embodiment, Mn is added as the first sub-component by 0.05 atm % or more and 0.35 atm % or less, Mg is added as the second sub-component by 0.4 atm % or more and 0.8 atm % or less, the rare earth element Re which is at least one of Ho and Dy is added as the third sub-component by 0.5 atm % or more and 0.9 atm % or less, V is added as the fourth sub-component by 0.15 atm % or more and 0.30 atm % or less, Si is added as the fifth sub-component by 0.4 atm % or more and 0.9 atm % or less, and Ca is added as the sixth sub-component by 0.00 atm % or more and 0.45 atm % or less, to the ceramic powder having a perovskite structure expressed by BamTiO3(0.9990≤m≤1.0015), on a presumption that an amount of Ti of BamTiO3acting as the main component of the ceramic material is 100 atm %. The condition of the firing process is adjusted so that the average grain diameter of BamTiO3is 280 nm or more and 380 nm or less in the dielectric layers11after the firing process. Thus, the multilayer ceramic capacitor100can achieve both the capacity stability and the high reliability.

The embodiment focuses on a multilayer ceramic capacitor. However, the embodiment may be applied to a ceramic capacitor having a single dielectric layer.

EXAMPLES

The multilayer ceramic capacitor was fabricated. And characteristic of the multilayer ceramic capacitor was measured.

BamTiO3powder was prepared as the main component ceramic of the dielectric layers11and the cover layers13. As the first sub-component, MnCO3was prepared. As the second sub-component, MgO was prepared. As the third sub-component, Dy2O3and Ho2O3were prepared. As the fourth sub-component, V2O5was prepared. As the fifth sub-component, SiO2was prepared. As the sixth sub-component, CaCO3was prepared.

The barium titanate powder and the first to sixth sub-components were weighed so that the ratio of the barium titanate powder and the first to sixth sub-components was a predetermined value. The resulting power was sufficiently wet-blended and crushed by a ball mil, and the dielectric materials was obtained. Next, as an organic binder, butyral was added to the resulting dielectric material. As a solvent, toluene or ethanol was added to the resulting dielectric material. A zirconia bead was used as a dispersing media. And, slurry was obtained. A usage amount of the zirconia bead was adjusted so that an amount of Zr was 0.20 atm % or more and 0.26 atm % or less when an amount of Ti of BamTiO3was 100 atm %.

In an example 1, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.05 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, and CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9997.

In an example 2, MnCO3was added so that the amount of Mn acting as the first sub-component was 0.15 atm %. Other conditions were the same as those of the example 1.

In an example 3, MnCO3was added so that the amount of Mn acting as the first sub-component was 0.35 atm %. Other conditions were the same as those of the example 1.

Comparative Example 1

In a comparative example 1, the first sub-component was not added. “m” was 0.9996. Other conditions were the same as those of the example 1.

Comparative Example 2

In a comparative example 2, MnCO3was added so that the amount of Mn acting as the first sub-component was 0.45 atm %. “m” was 0.9996. Other conditions were the same as those of the example 1.

In an example 4, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.40 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9996.

In an example 5, MgO was added so that the amount of Mg acting as the second sub-component was 0.60 atm %. “m” was 0.9997. Other conditions were the same as those of the example 4.

In an example 6, MgO was added so that the amount of Mg acting as the second sub-component was 0.80 atm %. “m” was 0.9993. Other conditions were the same as those of the example 4.

Comparative Example 3

In a comparative example 3, MgO was added so that the amount of Mg acting as the second sub-component was 0.20 atm %. “m” was 0.9995. Other conditions were the same as those of the example 4.

Comparative Example 4

In a comparative example 4, MgO was added so that the amount of Mg acting as the second sub-component was 1.0 atm %. “m” was 0.9998. Other conditions were the same as those of the example 4.

In an example 7, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.50 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9999.

In an example 8, Ho2O3was added so that the amount of Ho acting as the third sub-component was 0.70 atm %. “m” was 0.9997. Other conditions were the same as those of the example 7.

In an example 9, Ho2O3was added so that the amount of Ho acting as the third sub-component was 0.90 atm %. “m” was 0.9998. Other conditions were the same as those of the example 7.

Comparative Example 5

In a comparative example 5, Ho2O3was added so that the amount of Ho acting as the third sub-component was 0.20 atm %. “m” was 0.9996. Other conditions were the same as those of the example 7.

Comparative Example 6

In a comparative example 6, Ho2O3was added so that the amount of Ho acting as the third sub-component was 1.10 atm %. “m” was 0.9996. Other conditions were the same as those of the example 7.

In an example 10, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.15 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.60 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 1.0001.

In an example 11, V2O5was added so that the amount of V acting as the fourth sub-component was 0.25 atm %. “m” was 1.0002. Other conditions were the same as those of the example 10.

In an example 12, V2O5was added so that the amount of V acting as the fourth sub-component was 0.30 atm %. “m” was 1.0002. Other conditions were the same as those of the example 10.

Comparative Example 7

In a comparative example 7, the fourth sub-component was not added. “m” was 1.0002. Other conditions were the same as those of the example 10.

Comparative Example 8

In a comparative example 8, V2O5was added so that the amount of V acting as the fourth sub-component was 0.35 atm %. “m” was 0.9998. Other conditions were the same as those of the example 10.

In an example 13, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.40 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9998.

In an example 14, SiO2was added so that the amount of Si acting as the fifth sub-component was 0.60 atm %. “m” was 0.9995. Other conditions were the same as those of the example 13.

In an example 15, SiO2was added so that the amount of Si acting as the fifth sub-component was 0.90 atm %. “m” was 1.0000. Other conditions were the same as those of the example 13.

Comparative Example 9

In a comparative example 9, SiO2was added so that the amount of Si acting as the fifth sub-component was 0.30 atm %. “m” was 1.0000. Other conditions were the same as those of the example 13.

Comparative Example 10

In a comparative example 10, SiO2was added so that the amount of Si acting as the fifth sub-component was 1.00 atm %. “m” was 0.9996. Other conditions were the same as those of the example 13.

In an example 16, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. The sixth sub-component was nod added. And, “m” was 1.0002.

In an example 17, CaO was added so that the amount of Ca acting as the sixth sub-component was 0.25 atm %. Other conditions were the same as those of the example 16.

In an example 18, CaO was added so that the amount of Ca acting as the sixth sub-component was 0.45 atm %. Other conditions were the same as those of the example 16.

Comparative Example 11

In a comparative example 11, CaO was added so that the amount of Ca acting as the sixth sub-component was 0.55 atm %. Other conditions were the same as those of the example 16.

In an example 19, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9990.

In an example 20, “m” was 1.0002. Other conditions were the same as those of the example 19.

In an example 21, “m” was 1.0015. Other conditions were the same as those of the example 19.

Comparative Example 12

In a comparative example 12, “m” was 0.9985. Other conditions were the same as those of the example 19.

Comparative Example 13

In a comparative example 13, “m” was 1.0020. Other conditions were the same as those of the example 19.

In an example 22, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.15 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.60 atm %, Dy2O3was added so that an amount of Dy acting as the third sub-component was 0.68 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.25 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.50 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.15 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 0.9997.

Comparative Example 14

In a comparative example 14, MnCO3was added so that an amount of Mn acting as the first sub-component was 0.12 atm %, MgO was added so that an amount of Mg acting as the second sub-component was 0.80 atm %, Ho2O3was added so that an amount of Ho acting as the third sub-component was 1.30 atm %, V2O5was added so that an amount of V acting as the fourth sub-component was 0.18 atm %, SiO2was added so that an amount of Si acting as the fifth sub-component was 0.90 atm %, CaCO3was added so that an amount of Ca acting as the sixth sub-component was 0.20 atm %, on a presumption that an amount Ti of BamTiO3powder was 100 atm %. And, “m” was 1.0002.

FIG. 4illustrates the added amounts of the first to sixth sub-components and the values of “m”. An empty ofFIG. 4indicates that the component was not intentionally added.

A dielectric green sheet having a thickness of 7 μm was formed from the slurry of the examples 1 to 22 and the comparative examples 1 to 14 by a doctor blade method. A paste for forming an internal electrode of which a main component was Ni was printed on the resulting green sheet. Thus, a pattern-formed sheet was formed. 10 numbers of the pattern-formed sheets were stacked on a cover sheet (50× green sheet). And, another cover sheet (50× green sheet) was stacked on the multilayer structure. After that, the resulting multilayer structure was pressed at 100 degrees C. to 120 degrees C.

And the resulting multilayer structure was cut into a predetermined shape. After binder removal process in a N2atmosphere, the resulting multilayer structure was fired for 2 hours at a temperature of 1230 degrees C. in a reductive atmosphere. In a temperature cooling process after the firing, an oxygen partial pressure was increased and a re-oxidation process was performed. Thus, the ceramic main body10was obtained. After that, a Cu external paste including glass frit was coated on the two edge faces of the ceramic main body10. The Cu external paste was fired in a N2atmosphere. And, the multilayer ceramic capacitor100of which a size was 3.2 mm×1.6 mm×0.6 mm was obtained. The thickness of the dielectric layers11was 5 μm.

An average grain diameter of the ceramic grains in the dielectric layers11after the firing was 330 nm in the example 1, 327 nm in the example 2, 335 nm in the example 3, 345 nm in the example 4, 327 nm in the example 5, 337 nm in the example 6, 331 nm in the example 7, 320 nm in the example 8, 323 nm in the example 9, 313 nm in the example 10, 311 nm in the example 11, 315 nm in the example 12, 308 nm in the example 13, 343 nm in the example 14, 330 nm in the example 15, 320 nm in the example 16, 306 nm in the example 17, 314 nm in the example 18, 340 nm in the example 19, 311 nm in the example 20, 307 nm in the example 21 and 330 nm in the example 22. The average grain diameter of the ceramic grains in the dielectric layer11after the firing was 329 nm in the comparative example 1, 331 nm in the comparative example 2, 1000 nm or more in the comparative example 3, 335 nm in the comparative example 4, 343 nm in the comparative example 5, 317 nm in the comparative example 6, 307 nm in the comparative example 7, 319 nm in the comparative example 8, 403 nm in the comparative example 10, 310 nm in the comparative example 11, 385 nm in the comparative example 12, 302 nm in the comparative example 13, and 198 nm in the comparative example 14.

Each measurement test was performed with respect to the multilayer ceramic capacitors100of the examples 1 to 22 and the comparative examples 1 to 14.

(Test of Relative Dielectric Constant εrand Tan δ)

The multilayer ceramic capacitors100were subjected to 150 degrees C. four 1 hour. After leaving 24 hours at room temperature, a capacity and Tan δ of the multilayer ceramic capacitors100were measured by an LCR meter. The measurement condition was 1 kHz-1 Vrms. The relative dielectric constant εrof the dielectric layers11was calculated from the capacity C in accordance with the following formula (1) with use of an active area S, a number of layers n, a thickness t of the dielectric layer11and a vacuum dielectric constant ε0. The active area is a total area of facing areas of all pairs of the internal electrode layers12next to each other in a capacity region in which the internal electrode layers12that are connected to the different external electrode and are next to each other face with each other.
εr=(C×t)/(ε0×S×n)  (1)

Next, a MAX temperature at which the capacity C was maximum was measured. A ratio of the capacity C at the MAX temperature and the capacity C at 125 degrees C. (MAX/125 degrees C.) was measured. When the MAX temperature was within 35 degrees C. to 125 degrees C. and the ratio (MAX/125 degrees C.) was 0.8 to 1, X7R was determined as OK. When at least one of the MAX temperature and the capacity C was out of the ranges, X7R was determined as NG.

MTTF (Mean Time to Failure) was measured by measuring a time until a resistance value was smaller than an insulation resistance before the test by 3 digit when a voltage (electric field) of 30 V/μm was applied at 150 degrees C.

FIG. 5illustrates each measurement result of the examples 1 to 22 and the comparative examples 1 to 14. In the comparative example 1, the MTTF was a short value which was 1 hour. And, sufficient reliability was not achieved. It is thought that this was because the first sub-component was not added. Next, in the comparative example 2, the MTTF was a short time which was 12 hours. And, sufficient reliability was not achieved. It is thought that this was because the added amount of the first sub-component was more than 0.35 atm %.

In the comparative example 3, grain growth occurred, and reliability was degraded. And, sufficient capacity stability was not achieved. It is thought that this was because the added amount of the second sub-component was less than 0.40 atm %. In the comparative example 4, the MTTF was a short value which was 14 hours. And sufficient reliability was not achieved. It is thought that this was because the added amount of the second sub-component was more than 0.8 atm %.

In the comparative example 5, the MTTF was a short value which was 18 hours. And sufficient reliability was not achieved. It is thought that this was because the added amount of the third sub-component was less than 0.5 atm %. In the comparative example 6, sintering characteristic was degraded. And sufficient reliability was not achieved. It is thought that this was because the added amount of the third sub-component was more than 0.9 atm %.

In the comparative example 7, the MTTF was a short value which was 5 hours. And sufficient reliability was not achieved. And sufficient capacity stability was not achieved. It is thought that this was because the fourth sub-component was not added. In the comparative example 8, sufficient capacity stability was not achieved. It is thought that this was because the added amount of the fourth sub-component was more than 0.30 atm %.

In the comparative example 9, it was not possible to densify and form the dielectric layer11. It is thought that this was because the added amount of the fifth sub-component was less than 0.4 atm %. In the comparative example 10, the grain growth occurred. And sufficient capacity stability was not achieved. It is thought that this was because the added amount of the fifth sub-component was more than 0.9 atm %.

In the comparative example 11, sufficient capacity stability was not achieved. It is thought that this was because the added amount of the sixth sub-component was more than 0.45 atm %.

In the comparative example 12, the grain growth occurred. And sufficient capacity stability was not achieved. It is thought that this was because “m” of BamTiO3was less than 0.9990. In the comparative example 13, sufficient capacity stability was not achieved. It is thought that this was because “m” was more than 1.0015.

In the comparative example 14, sufficient capacity stability was not achieved. It is thought that this was because a grain diameter in the dielectric layer11was less than 280 nm.

On the other hand, in the examples 1 to 22, the MTTF was a large value, and X7R was determined as OK. That is, it was possible to achieve both the high reliability and the capacity stability. It is thought that this was because Mn was added as the first sub-component by 0.05 atm % or more and 0.35 atm % or less, Mg was added as the second sub-component by 0.4 atm % or more and 0.8 atm % or less, the rare earth element Re which was at least one of Ho and Dy was added as the third sub-component by 0.5 atm % or more and 0.9 atm % or less, V was added as the fourth sub-component by 0.15 atm % or more and 0.30 atm % or less, Si was added as the fifth sub-component by 0.4 atm % or more and 0.9 atm % or less, and Ca was added as the sixth sub-component by 0.00 atm % or more and 0.45 atm % or less, to the ceramic powder having a perovskite structure expressed by BamTiO3(0.9990≤m≤1.0015), on a presumption that an amount of Ti of BamTiO3was 100 atm %, and the average grain diameter of BamTiO3was 280 nm or more and 380 nm or less in the dielectric layers11after the firing process.