Fluorocarbon anti-shrinkage leveling agent for coating and ink

A fluorocarbon leveling agent (fluoride-containing surfactant) for coating and ink has the surface tension of the leveling agent of 21-24 dynes, the number-average molecular weight of 1500-4500, the weight-average molecular weight of 3000-15000, and the polydispersity of 1.5-2.8. The present invention can reduce the surface tension of the coating system and has strong anti-shrinkage capability and excellent long wave leveling.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

The present invention is further detailedly explained with the accompanying drawings and preferred embodiment.

Add 50 g butyl acetate into a four-necked flask with a reflux condenser, a thermometer, an agitator, and a dropping funnel, and stir by starting the agitator. When the temperature reaches 118° C., after the reflux of the butyl acetate solvent in the reflux condenser, begin to add 15 g butyl acetate, 210 butyl acrylate trifluoroacetic, and 5.74 g azobisisobutyronitrile in drops. Finish the dropping after 3 hours, and then continue to stir for 2 hours at the maintaining temperature of 118° C., and then add the mixture of 5 g butyl acetate and 1.19 g azobisisobutyronitrile in drops for 10 minutes, and then continue to stir for 2 hours at the maintaining temperature of 118° C. After finishing maintaining the temperature, the solvent is distilled off by reducing the pressure, or the solid content is adjusted to be 50% for removing the product, and then the product is sealed and packaged.

1. Product performance is as follows. The appearance of the product is a pale yellow transparent liquid, the solid content thereof is 50% or 100%, the surface tension thereof is 21-24 dynes, the number-average molecular weight thereof is 1500-4500, the weight-average molecular weight thereof is 3000-15000, and the polydispersity thereof is 1.5-2.8.

When the surface tension is 21-24 dynes, the leveling agent can effectively reduce the surface tension of the coating system. When the number-average molecular weight, the weight-average molecular weight and the polydispersity are in the range mentioned above, the long wave leveling of the paint is excellent.

The amount of every component is as below:

The step-by-step percentage of use of the same component mentioned above is the same as that in Embodiment 1. The others are the same as those in Embodiment 1.

2. The surface tension of the obtained leveling agent is 21-24 dynes, the number-average molecular weight thereof is 1500-4500, the weight-average molecular weight thereof is 3000-15000, and the polydispersity thereof is 1.5-2.8.

1. The surface tension values of the fluoride-containing surfactant for solvent-based coatings, the fluorine-containing acrylate leveling agent, the pure acrylate leveling agent and the acrylic varnish stock solution are shown inFIG. 1.

2. If add 0.1%, 0.3%, 0.5% and 0.8% fluorine-containing leveling agent and the pure acrylate leveling agent into the acrylic varnish, respectively, the surface tension of the acrylic varnish decreases, which is shown inFIG. 2.

The above-mentioned description explains that when the surface tension value of the fluoride-containing surfactant is 22.992 dynes, the fluoride-containing surfactant can reduce the surface tension of the coating system more than the lyacrylate leveling agent and the fluorine-containing leveling agent. Furthermore, due to the decrease of the surface tension value of the varnish, the varnish has excellent anti-shrinkage capability, the substrate wettability and the leveling speed.