Cement paint

It is disclosed a cement paint comprising a pigmenting substance (2), a cement binder (6) and a fluidizing liquid (4) and further comprising: a calcareous aggregate (7) including calcareous granules of calcium carbonate CaCO3 having maximum sizes smaller than 100 microns, a vitreous aggregate (8) including vitreous granules having maximum sizes smaller than 100 microns, and a photocatalyst (9) adapted to oxidize polluting substances in the presence of light and air.

FIELD OF THE INVENTION

The present invention relates to a cement paint to be used for coating various different surfaces with thin films, of the type comprising a pigmenting substance, a cement binder and a fluidizing liquid.

DESCRIPTION OF THE PRIOR ART

It is known that paint is currently defined as a mixture of a pigment and a suitable “vehicle”. The “vehicle” usually aims at hardening the pigment and giving it some consistency, forming with the same a film adhering to the treated surface.

In particular, the pigment or coloring matter is a chemically stable product with a good covering power so that it can be used to give some dyeing to any item.

The “vehicle” is on the contrary a fluid product that when spread in a thin layer over any item dries leaving a solid and hard film thereon, which film adheres to the item itself and can withstand the action of the atmospheric agents.

Cement paints are so-called because the “vehicle” in which the pigment is inserted and mixed comprises cement material, a common cement for example. Also considered as cement paints are those having a dye which is a direct consequence of the color of the “vehicle” consisting of cement material, in which addition of a pigment is actually superfluous either because the suitable color is already that of the “vehicle” or because the naturally existing color is not of importance since application of other paint layers is foreseen.

Cement paints are distinguishable due to their qualities in terms of resistance to the atmospheric agents and duration in time. Therefore they are also suitable for application on surfaces exposed to the inclemency of the weather.

They also have a high consistency and covering capacity and, while being in the form of films, help in making the treated surfaces smooth, homogeneous and well finished.

The consistency of cement paints, in spite of the reduce thickness of the formed films, makes the same also adapted to reduce emerging of humidity from the walls.

Beside the above qualities there are some drawbacks typical of paints and also connected with the presence of cement material.

First there is the possibility that cracks or breaks in the paint may spontaneously take place over time, due to a phenomenon of paint shrinkage or to the fact that said paint becomes brittle.

Secondly, flow ability or workability of cement paints is not optimal due to the pasty quality of the cement material present therein.

This may give rise to a marked application slowness or difficulty, above all when spreading takes place by means of a brush.

In addition, the non optimal flow ability or workability makes it difficult to set very thin films, which will result in a greater paint consumption by users and consequent higher application costs.

Then the presence of a “vehicle” of the cement type, naturally opaque, does not facilitate achievement of a satisfactory paint brightness, when this is required.

Finally, cement paints—like paints in general—retain dust and pollutants present in the atmosphere and also allow possible flourishing of bacteria and fungi thereon.

Therefore they must be submitted to periodical cleaning and/or sanitizing operations, above all when said paints are applied in very frequented or polluted environments, or in hospital environments.

SUMMARY OF THE INVENTION

Under this situation the technical task underlying the present invention is to devise a cement paint capable of substantially obviating the mentioned drawbacks.

This technical task is achieved by a cement paint, comprising a pigmenting substance, a cement binder and a fluidizing liquid, and further comprising at least: a calcareous aggregate comprising calcareous granules of calcium carbonate CaCO3having maximum sizes smaller than 100 microns, a vitreous aggregate comprising vitreous granules having maximum sizes smaller than 100 microns; and a photo catalyst adapted to oxidize polluting substances in the presence of light and air.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The cement paint or inventive paint is denoted at1. In the FIGURE said paint is shown in the last block of the block diagram already packaged in tins and ready for use.

The cement paint1comprises at least one pigmenting substance or pigment2mixed with a “vehicle”3.

The coloring matter or pigment2is a chemically stable solid product provided with a covering power and can be in any case selected from those known and currently usable.

“Vehicle”3is on the contrary a fluid substance that spontaneously hardens in the air and gives consistency to pigment2, forming with the latter a film adhering to the treated surface.

“Vehicle”3is in turn formed of an appropriate fluidizing liquid4that in paint1advantageously is mere water, and of a powdered dry preparation5.

In accordance with the invention, the dry preparation5is made up of many components originally selected and combined.

It is distinguishable a cement binder6known in itself and from which the paint name originates, which is preferably a white-colored cement-based product. Then a combination of two aggregates is provided: a calcareous aggregate7and a vitreous aggregate8.

The calcareous aggregate7is substantially defined by calcareous granules of calcium carbonate CaCO3obtained in the industry or from natural products. In the industry calcium carbonate is obtained through saturation of lime milk with CO2for example, so as to obtain the so-called “precipitated carbonate” whereas from natural products it is obtained by a very fine grinding of a calcareous stone, for example.

The calcareous aggregate7to be used is provided to be in the form of calcareous granules of very small particle sizes, i.e. with sizes smaller than 100 microns, and preferably with sizes smaller than 50 microns.

However the amount of calcareous aggregate7can vary within wide limits depending on the mechanical features desired in the paint. For example, the calcareous aggregate can be in an amount by weight included between the same amount as that of the cement binder6or twice that amount.

The vitreous aggregate8is substantially defined by vitreous granules.

Each granule comprises a single glass fragment or several glass fragments bound together. Each glass fragment is preferably obtained by grinding and advantageously is of the E-AR type.

The abbreviation “E” identifies a glass having optimal qualities of resistance and high modulus of elasticity, high melting point. It can be defined as a calcium and aluminum borosilicate with a low alkali content.

The abbreviation “AR” (alkali-resistant) identifies a glass with the additional feature of having a high content of zirconium oxide ZrO2and a high resistance to acid and alkaline attacks, in particular cement attacks.

In vitreous granules made of a plurality of E-AR glass fragments agglomerated with each other, the binding agent forming the agglomeration is preferably an aminosilane.

In particular it is an aminosilane having the formula: NH2(CH2)3Si(OC2H5)3. The vitreous granules of the above described type are identified with “perlex” from Saint Gobain Vetrotex International S.A.

These granules are selected with sizes smaller than 100 microns and preferably with sizes smaller than 50 microns, of 45 microns for example.

They have a white color with a high roughness or surface unevenness and an apparent density equal to or less than 1.5 grams per cubic centimeter.

Said vitreous granules are inserted in the cement paint in amounts lower than 25% by weight of the cement binding agent, equal to 3% of said weight itself, for example.

The vitreous aggregate8improves the properties of the cement paint1to a great degree.

A characteristic of said vitreous granules in fact consists in improving flow ability of the paint when said paint is still in a fluid state, because in this case the granules behave like very movable “microballs” promoting spreading of the paint and arrangement of same in thin layers.

Another feature is that of improving the mechanical features of the cement paint1when the latter is hardened and in the form of film. In fact the vitreous granules greatly increase hardness of the cement paint film and therefore the resistance to impact and abrasion of same.

Another quality of said granules resides in that they also increase the paint brightness, due to their vitreous nature.

Above all, the vitreous aggregate8increases the dimensional stability of the paint, reducing the paint tendency to shrinkage and cracking.

The last-mentioned property is due to the fact that the granules that are substantially non-deformable, have a rough surface that stably clings to the surrounding material, hindering cracking of same.

The action of the vitreous granules is enhanced by the fact that the maximum sizes of the vitreous granules and calcareous granules are similar and by the fact that it is advantageously provided for said granules to have real sizes similar or substantially equal to each other.

In this way a uniform and optimal dispersion of the vitreous granules in the mass of the calcareous aggregate may easily take place and in addition said calcareous aggregate cannot by its sizes surpass the action of said microballs of the aggregate or make it fruitless.

Another component of the cement paint1preferably already inserted in the dry preparation5is defined by a photo catalyst9adapted to oxidize polluting substances in the atmosphere in the presence of light, air or oxygen.

The photo catalyst9can be any substance capable of oxidizing pollutants present in the atmosphere and preferably it consists of an additive including titanium oxide TiO2or a precursor of the titanium oxide, the so-called titanium paste TiO2H2O for example, in any case always including titanium oxide.

The photo catalyst features are known by themselves and are disclosed in the European patent application EP 0946450 for example.

The photo catalyst9too is provided in amounts lower than 25% by weight of the cement binding agent6, of 3% for example.

Introduction of a photo catalyst9in the paint gives rise to many important advantages.

In particular the photo catalyst9has a partly synergic action to the vitreous aggregate because it tends to set off and increase brightness of the paint.

In fact it exerts a self-cleaning action in the paint helping in keeping the same clean and bright.

Experimental tests conducted by the same Applicant have proved that with the use of photo catalysts of said preferred type surfaces soiled with cigarette tobacco ash extract and carbon black have been substantially brought back to their original color.

In addition photo catalysts have an anti-pollution action by virtue of which, in the presence of light and air, polluting substances such as benzene, carbon black, polycondensate aromatic compounds, nitrogen oxides, etc. are oxidized and converted to sodium nitrates and calcium nitrates for example that precipitate. These positive and advantageous actions are combined with further important positive effects for paints: it has been experimentally found that photo catalysts9of said preferred type have an antimicrobial activity and that their oxidizing action inhibits development of fungi and bacteria.

A consequence of this situation is also a deodorizing action of the surfaces to which paint is applied.

The dry preparation5generally described above is joined to the already mentioned fluidizing liquid4, consisting of mere water, so as to form said “vehicle”3.

Varying amounts of water are set, depending on the paint density that is wished to be obtained. It is in principle provided that the amount by volume of water may vary between about one third of, and about half the amount by volume of the dry preparation5.

Addition of the pigmenting substance2can be carried out at various moments.

For example, it can be added to “vehicle”3, as in usual paints, or it can be introduced more upstream, so as to form a further component of the dry preparation.

As said, the pigmenting substance2can by of any kind.

If the color of “vehicle”3is already the desired one, also in the absence of the pigmenting substance2, said substance can be omitted, which will bring about a reduction in the paint costs. This may for example happen when the desired color is white, since the above described “vehicle”3is of a white color, due to use of white cement and aggregates7and8of a white or clear color.

The pigmenting substance2can be omitted also when the cement paint1is provided to be used as a background layer or a preparation layer for application of other paints, or as an additional layer to be applied before other paints so as to obtain the qualities mentioned above.

Generally it is also possible to point out that the dry preparation5is a powdered material with an apparent specific weight of about 1.50 kilograms per cubic decimeter on an average.

The dry preparation can be marketed in an independent manner, since it can also include the pigmenting substance, or it can be dispensed with the need for said pigmenting substance since in these cases it can be applied by mere addition of water.

“Vehicle”3resulting from mixing of the dry preparation5with water has a varying consistency between a fluid and a plastic one depending on the amount of water, pH of about 13.

“Vehicle”3too can be marketed in an independent manner, to enable addition of a coloring substance at will, or when said substance is not provided for the reasons set out above. In this case the “vehicle” embodies the final product.

The cement paint in its entirety has an application temperature preferably included between 5 and 35 degrees centigrade and its maximum application thickness, in connection with a single layer, is about 2 millimeters. The minimum thickness can be less than 0.5 millimeters.

It is also pointed out that additives of various types in accordance with a normal knowledge in the field can be added to the above specified individual components, to the dry preparation5or to “vehicle”3.

The invention achieves important advantages.

In fact a cement paint is made in which cracks and shrinkage typical of cement are substantially avoided, due in particular to the presence of said vitreous aggregate8and also due to the fact that the calcareous aggregate7and vitreous aggregate8have similar sizes, which will enable a homogeneous dispersion of the vitreous aggregate.

The vitreous aggregate also helps in making spreading of very thin layers quick and easy, or promotes quick spreading of the cement paint on wide surfaces.

For spreading of said cement paint, brushes, rollers, spatulas or spray guns can be indifferently used.

When paint reaches its final condition of dry film, the vitreous aggregate also gives the film hardness and brightness.

Brightness in the applied color is also a consequence of the action of photo catalyst9giving the paint self-cleaning capacity and helping in greatly reducing the environmental pollution.

The paint is also very suitable for application in environments such as hospitals and nursing centers, due to the antibacterial and fungicide action of the catalyst.

The invention is susceptible of many modifications and variations.

For instance, the amounts of the different components can be widely varied and various additives can be added, depending on specific requirements.

In forming the paint, the mixtures can be done in many ways depending on the existing opportunities: for example the photo catalyst can be either immediately associated with the cement binding agent or inserted in the paint as the last element.