Photoresist composition, compound and process of producing photoresist pattern

A photoresist composition comprising

This nonprovisional application claims priority under 35 U.S.C. §119(a) on Patent Application No. 2014-031642 filed in JAPAN on Feb. 20, 2014, the entire contents of which are hereby incorporated by reference.

TECHNICAL FIELD

The present disclosure relates to a photoresist composition, a compound and a process of producing photoresist pattern.

BACKGROUND ART

A photoresist composition is used for semiconductor microfabrication employing a lithography process.

JP2006-257078A1 discloses a photoresist composition which comprises a resin having an acid-labile group, an acid generator having a (hydroxyadamantyl)methoxycarbonyl group at its anion, and a quencher.

SUMMARY OF THE DISCLOSURE

The present invention relates to the followings:

a resin having an acid-labile group,

an acid generator, and

a compound represented by formula (I0):

wherein R01represents a C1-C24 hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group, a nitro group or a halogen atom;
R02each independently represents a C1-C12 hydrocarbon group, a C1-C6 alkoxy group, a C2-C7 acyl group, a C2-C7 acyloxy group, a C2-C7 alkoxycarbonyl group, a nitro group, a hydroxy group or a halogen atom; and
m represents an integer of 0 to 4.
[2]A process for producing a photoresist pattern comprising the following steps (1) to (5):

(1) a step of applying the photoresist composition according [1] on a substrate,

(2) a step of forming a composition film by conducting drying,

(3) a step of exposing the composition film to radiation,

(4) a step of baking the exposed composition film, and

(5) a step of developing the baked composition film.

[3]A compound represented by formula (I):

wherein R1represents a C1-C24 saturated hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom;
R2each independently represents a C1-C12 hydrocarbon group, a C1-C6 alkoxy group, a C2-C7 acyl group, a C2-C7 acyloxy group, a C2-C7 alkoxycarbonyl group, a nitro group, a hydroxy group or a halogen atom; and
n represents an integer of 0 to 4.
[4] The compound according to [3]
wherein R1is a C1-C24 saturated hydrocarbon group having a ring structure, in which group a methylene group can be replaced by an oxygen atom or a carbonyl group and in which group a hydrogen atom can be replaced by a hydroxy group or a halogen atom.
[5] The compound according to [3]
wherein R1is represented by R3—CO—O— where R3represents a C1-C22 hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

DESCRIPTION OF PREFERRED EMBODIMENTS

The photoresist composition comprises a compound represented by formula (I0), an acid generator and a resin having an acid-labile group.

The photoresist composition may further comprise a quencher, such as a basic compound, or a solvent.

<Compound Represented by Formula (I0)>

In formula (I0), R01represents a C1-C24 hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group, a nitro group or a halogen atom;

R02each independently represents a C1-C12 hydrocarbon group, a C1-C6 alkoxy group, a C2-C7 acyl group, a C2-C7 acyloxy group, a C2-C7 alkoxycarbonyl group, a nitro group, a hydroxy group or a halogen atom; and

m represents an integer of 0 to 4.

The hydrocarbon groups represented by R01or R02include an aliphatic hydrocarbon group, an alicyclic hydrocarbon group, an aromatic hydrocarbon group and combination of the groups selected therefrom.

Examples of the aliphatic hydrocarbon group include an alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a isobutyl group, a tert-butyl group, a pentyl group, a hexyl group, an octyl group and a nonyl group.

The aliphatic hydrocarbon group has preferably 1 to 9 carbon atoms, more preferably 3 to 8 carbon atoms.

The alicyclic hydrocarbon group may be monocyclic or polycyclic.

Examples thereof include a cycloalkyl group such as a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclononyl group and a cyclododecyl group, a polycyclic hydrocarbon group such as an adamantyl group, or a norbornyl group.

The alicyclic hydrocarbon group has preferably 6 to 10 carbon atoms.

The aromatic hydrocarbon group has preferably 6 to 10 carbon atoms.

Examples of the combination for R02include an alkyl-cycloalkyl group; a cycloalkyl-alkyl group; an alkyl-aryl group such as the above-mentioned groups; an (alicyclic hydrocarbon)-aryl group such as 4-cyclohexylphenyl group; and an aralkyl group such as the above-mentioned groups.

As to R02, examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentoxy group, and a hexyloxy group.

Examples of the acyl group include an acetyl group, a propanoyl group, a benzoyl group, and a cyclohexanecarbonyl group.

Examples of the acyloxy group include an acetyloxy group, a propanoyloxy group, a benzoyloxy group, and a cyclohexanecarbonyloxy group.

Examples of the alkoxycarbonyl group include a methoxycarbonyl group, an ethoxycarbonyl group, a propoxycarbonyl group, a butoxycarbonyl group, a pentoxycarbonyl group, and hexyloxycarbonyl group.

Examples of the halogen atom in formula (I0) include a fluorine atom, a chlorine atom and a bromine atom.

R01has preferably a ring structure, a carbonyloxy group or both of them. R01has preferably a C1 to C18 hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

R01is preferably represented by R3—CO—O— where R03represents a C1-C22 hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

R03is preferably a C1-C4 alkyl group, a C6-C10 aryl group, a cycloalkyl-cycloalkyl group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom; and an (alicyclic hydrocarbon)-aryl group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

The “m” is preferably an integer of 0 to 2, more preferably an integer of 0. When m is 2, each of the groups represented by R02is the same group.

The compound represented by formula (I0) is preferably represented by formula (I):

In the formula, R1represents a C1-C24 saturated hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom;

R2each independently represents a C1-C12 hydrocarbon group, a C1-C6 alkoxy group, a C2-C7 acyl group, a C2-C7 acyloxy group, a C2-C7 alkoxycarbonyl group, a nitro group, a hydroxy group or a halogen atom; and

n represents an integer of 0 to 4.

For R1, examples of the saturated hydrocarbon group include an aliphatic hydrocarbon group such as an alkyl group, e.g. a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a tert-butyl group, a pentyl group, a hexyl group, an octyl group and a nonyl group; and

an alicyclic hydrocarbon group, which may be monocyclic or polycyclic, such as a cycloalkyl group, e.g., a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cyclononyl group and a cyclododecyl group, or a polycyclic hydrocarbon group such as an adamantyl group, or a norbornyl group.

R1is preferably a C1-C24 saturated hydrocarbon group having a ring structure, more preferably one having an alicyclic hydrocarbon group, in which group a methylene group can be replaced by an oxygen atom or a carbonyl group and in which group a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

R1is represented by R3—CO—O— where R3represents a C1-C24, preferably C1-C22, saturated hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

R3is preferably a C1-C22 saturated hydrocarbon group having a ring structure, more preferably one having an alicyclic hydrocarbon group in which a methylene group can be replaced by an oxygen atom or a carbonyl group and in which a hydrogen atom can be replaced by a hydroxy group or a halogen atom.

Specific examples of R1include the following ones:

The “n” is preferably an integer of 0 to 2. When n is 2, each of the groups represented by R02is the same group.

Specific examples of the compound represented by formulae (I0) and (I) include the following ones.

Other specific examples of the compound represented by formula (I0) include the following ones.

The content of the compound represented by formula (I0) is preferably 0.001% by mass or more, more preferably 0.005% by mass or more, still more preferably 0.01% by mass or more, based on sum of solid component. The content is also preferably 10% by mass or less, more preferably 8% by mass or less, still more preferably 5% by mass or less, based on the sum.

The compound represented by formula (I0) can be produced by reacting the compound of formula (I0-a) and the compound of formula (I0-b), at the presence of a catalyst, in a solvent.

in which R01, R02and m are as defined above.

For the reaction, examples of the catalyst include potassium persulfate and sulfuric acid. Examples of the solvent include chloroform.

Examples of the compound of formula (I0-a) include the following one.

Examples of the compound of formula (I0-b) include the following ones.

The reaction can be conducted at temperature of preferably 20° C. to 60° C., for 0.5 to 12 hour.

The compound represented by formula (I) in which R1is represented by R3—CO—O—, can be produced by reacting the compound of formula (IA-a) and the compound of formula (IA-b), preferably in a solvent such as an organic solvent including chloroform or monochlorobenzene.

in which R1, R2, R3and n are as defined above.

Examples of the compound of formula (IA-a) include the following one.

Examples of the compound of formula (IA-b) include the following one.

The reaction can be conducted at temperature of preferably 40° C. to 150° C., for 0.5 to 8 hour.

The compound in which R3is the saturated hydrocarbon group other than a methyl group can be produced by conducting ester exchange in the compound of formula (IA) where R3is a methyl group with a carboxylic compound having the saturated hydrocarbon group.

The resin having an acid-labile group, which is sometimes referred to as “Resin (A)”, usually comprises a structural unit having an acid-labile group. Hereinafter, the structural unit is sometimes referred to as “structural unit (a1)”.

Preferably Resin (A) further comprises another structural unit than the structural unit (a1), i.e. a structural unit having no acid-labile group, which is sometimes referred to as “structural unit (s)”.

The structural unit (a1) is derived from a compound having an acid-labile group which compound is sometimes referred to as “Monomer (a1)”.

Herein, “an acid-labile group” means a group which has a hydrophilic group, such as a hydroxy group or a carboxy group, resulting from removing a leaving group therefrom by the action of an acid.

For Resin (A), the acid-labile groups represented by formulae (1) and (2) are preferred:

In formula (1), Ra1, Ra2and Ra3independently each represent a C1-C8 alkyl group, a C3-C20 alicyclic hydrocarbon group or a group consisting of them, and Ra1and Ra2can be bonded each other to form a C2-C20 divalent hydrocarbon group, na represents an integer of 0 or 1, and * represents a binding site.

In formula (2), Ra1and Ra2′independently each represent a hydrogen atom or a C1-C12 hydrocarbon group, and Ra3′represents a C1-C20 hydrocarbon group, and Ra2′and Ra3′can be bonded each other to form a C2-C20 divalent hydrocarbon group, and one or more —CH2— in the hydrocarbon group and the divalent hydrocarbon group can be replaced by —O— or —S—, X represents an oxygen atom or a sulfur atom, and * represents a binding site.

For Ra1, Ra2and Ra3, specific examples of the alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group and an octyl group.

The alicyclic hydrocarbon group may be monocyclic or polycyclic. Examples of the alicyclic hydrocarbon group include a monocyclic alicyclic hydrocarbon group such as a C3-C20 cycloalkyl group (e.g. a cyclopentyl group, a cyclohexyl group, a cycloheptyl group and a cyclooctyl group) and a polycyclic alicyclic hydrocarbon group such as a decahydronaphthyl group, an adamantyl group, a norbornyl group, and the followings:

in which * represents a binding site.

The alicyclic hydrocarbon group preferably has 3 to 16 carbon atoms.

Examples of the group consisting of alkyl and alicyclic hydrocarbon group include a methylcyclohexyl group, a dimethylcyclohexyl group, a methylnorbornyl group, an adamantylmethyl group, and a norbornylethyl group.

The “na” is preferably 0.

When the divalent hydrocarbon group is formed by bonding Ra1and Ra2each other, examples of the moiety —C(Ra1)(Ra2)(Ra3) include the following groups and the divalent hydrocarbon group preferably has 3 to 16 carbon atoms.

wherein Ra3is the same as defined above and * represents a binding site.

The group represented by formula (1) wherein Ra1, Ra2and Ra3independently each represent a C1-C8 alkyl group such as a tert-butyl group, the group represented by formula (1) wherein Ra1and Ra2are bonded each other to form an adamantyl ring and Ra3is a C1-C8 alkyl group such as a 2-alkyl-2-adamantyl group, and the group represented by formula (1) wherein Ra1and Ra2are C1-C8 alkyl groups and Ra3is an adamantyl group such as a 1-(1-adamantyl)-1-alkylalkoxycarbonyl group are preferred.

For formula (2), examples of the hydrocarbon group include an alkyl group, an alicyclic hydrocarbon group, an aromatic hydrocarbon group and a group consisting of two or more of them.

Examples of the aliphatic hydrocarbon group and the alicyclic hydrocarbon group include the same as described above. Examples of the aromatic hydrocarbon group include an aryl group such as a phenyl group, a naphthyl group, a p-methylphenyl group, a p-tert-butylphenyl group, a p-adamantylphenyl group, a tolyl group, a xylyl group, a cumyl group, a mesityl group, a biphenyl group, an anthryl group, a phenanthryl group, a 2,6-diethylphenyl group and a 2-methyl-6-ethylphenyl group.

Examples of the divalent hydrocarbon group formed by bonding Ra2′and Ra3′each other include those formed by removing a hydrogen atom from the hydrocarbon group represented by Ra1′, Ra2′and Ra3′.

It is preferred that at least one of Ra1′and Ra2′is a hydrogen atom.

Examples of the group represented by formula (2) include the following.

Monomer (a1) is preferably a monomer having an acid-labile group in its side chain and an ethylenic unsaturated group, more preferably a (meth)acrylate monomer having an acid-labile group in its side chain, and still more preferably a (meth)acrylate monomer having the group represented by formula (1) or (2).

The (meth)acrylate monomer having an acid-labile group in its side chain is preferably those which comprise a C5-C20 alicyclic hydrocarbon group. The resin which comprises a structural unit derived from such monomers can provide improved resolution for a photoresist pattern to be prepared therefrom.

The structural unit derived from a (meth)acrylate monomer having the group represented by formula (1) is preferably one of structural units represented by formulae (a1-0), (a1-1) and (a1-2).

In each formula, La01, La1and La2each independently represent —O— or *—O—(CH2)k1—CO—O— in which k1 represents an integer of 1 to 7 and * represents a binding site to —CO—,

Ra01, Ra4and Ra5each independently represent a hydrogen atom or a methyl group,

m1 represents an integer of 0 to 14,

n1 represents an integer of 0 to 10, and

n1′ represents an integer of 0 to 3.

Hereinafter, the structural units represented by formulae (a1-0), (a1-1) and (a1-2) are respectively referred to as “structural unit (a1-0)”, “structural unit (a1-1)” and “structural unit (a1-2)”. Resin (A) may comprise two or more of such structural units.

La01is preferably *—O— or *—O—(CH2)f1—CO—O— in which * represents a binding site to —CO—, and f1 represents an integer of 1 to 4, and is more preferably *—O— or *—O—CH2—CO—O—, and is especially preferably *—O—.

For Ra02, Ra03and Ra04, examples of the alkyl group, the alicyclic hydrocarbon group and the group formed by combining them include the same as referred for Ra1, Ra2and Ra3.

The alkyl group preferably has 1 to 6 carbon atoms.

The alicyclic hydrocarbon group preferably has 3 to 8 carbon atoms and more preferably 3 to 6 carbon atoms. The alicyclic hydrocarbon group is preferably a saturated aliphatic cyclic hydrocarbon group. The group formed by combining them preferably has 18 carbon atoms or less in total, examples of which include a methylcyclohexyl group, a dimethylcyclohexyl group, and a methylnorbornyl group. Each of Ra02and Ra03is preferably a C1-C6 alkyl group, more preferably a methyl group and an ethyl group.

Ra04is preferably a C1-C6 alkyl group and a C5-C12 alicyclic hydrocarbon group, more preferably a methyl group, an ethyl group, a cyclohexyl group, and an adamantyl group.

Each of La1and La2is preferably *—O— or *—O—(CH2)f1—CO—O— in which * represents a binding site to —CO—, and f1 is the same as defined above, and is more preferably *—O— or *—O—CH2—CO—O—, and is especially preferably *—O—.

Each of Ra4and Ra5is preferably a methyl group.

For Ra6and Ra7, examples of the alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a tert-butyl group, a pentyl group, a heptyl group, a 2-ethylheptyl group and an octyl group.

For Ra6and Ra7, examples of the alicyclic hydrocarbon group include a monocyclic alicyclic hydrocarbon group such as a cyclohexyl group, a methylcyclohexyl group, a dimethylcyclohexyl group, a cycloheptyl group and a methylcycloheptyl group, and a polycyclic alicyclic hydrocarbon group such as a decahydronaphthyl group, an adamantyl group, a norbornyl group, a methylnorbornyl group and the following. For Ra6and Ra7, examples of the group consisting of an alkyl group and an alicyclic hydrocarbon group include an aralkyl group such as a benzyl group, and a phenethyl group.

The alkyl group represented by Ra6and Ra7is preferably a C1-C6 alkyl group.

The alicyclic hydrocarbon group represented by Ra6and Ra7is preferably a C3-C8 alicyclic hydrocarbon group, more preferably a C3-C6 alicyclic hydrocarbon group.

The “m1” is preferably an integer of 0 to 3, and is more preferably 0 or 1.

The “n1” is preferably an integer of 0 to 3, and is more preferably 0 or 1.

The “n1” is preferably 0 or 1.

Examples of the structural unit (a1-0) include those represented by formulae (a1-0-1) to (a1-0-12), preferably those represented by formulae (a1-0-1) to (a1-0-10).

Examples of the structural unit (a1-0) further include such groups that a methyl group has been replaced by a hydrogen atom in any one of formulae (a1-0-1) to (a1-0-12).

Examples of the monomer from which the structural unit (a1-1) is derived include the monomers described in JP2010-204646A1, and the following monomers represented by the formulae (a1-1-1) to (a1-1-8), preferably the following monomers represented by the formulae (a1-1-1) to (a1-1-4).

Examples of the monomer from which the structural unit (a1-2) is derived include 1-ethylcyclopentan-1-yl acrylate, 1-ethylcyclopentan-1-yl methacrylate, 1-ethylcyclohexan-1-yl acrylate, 1-ethylcyclohexan-1-yl methacrylate, 1-ethylcycloheptan-1-yl acrylate, 1-ethylcycloheptan-1-yl methacrylate, 1-methylcyclopentan-1-yl acrylate, 1-methylcyclopentan-1-yl methacrylate, 1-isopropylcyclopentan-1-yl acrylate and 1-isopropylcyclopentan-1-yl methacrylate, preferably the monomers represented by formulae (a1-2-1) to (a1-2-12), more preferably the monomers represented by formulae (a1-2-3), (a1-2-4), (a1-2-9) and (a1-2-10), still more preferably the monomers represented by formulae (a1-2-3) and (a1-2-9).

The content of the structural unit having an acid-labile group in the resin is usually 10 to 95% by mole, preferably 15 to 90% by mole and more preferably 20 to 85% by mole based on 100% by mole of all the structural units of the resin. The content of the structural unit having an acid-labile group in the resin can be adjusted by adjusting the amount of the monomer having an acid-labile group based on the total amount of the monomers used for producing the resin.

When the resin comprises one or more of the structural units represented by formulae (a1-0), (a1-1) and (a1-2), the total content of the structural units is usually 10 to 95% by mole, preferably 15 to 90% by mole and more preferably 15 to 90% by mole and still more preferably 20 to 85% by mole based on 100% by mole of all the structural units of the resin.

Other examples of the structural unit (a1) having a group represented by formula (1) include a structural unit represented by formula (a1-3):

wherein Ra9represents a hydrogen atom, a carboxyl group, a cyano group, a C1-C3 aliphatic hydrocarbon group which can have a hydroxy group, or a group represented by —COORa13group in which Ra13represents a C1-C8 alkyl group or a C3-C20 alicyclic hydrocarbon group, and a group composed of a C1-C8 aliphatic hydrocarbon group and a C3-C20 alicyclic hydrocarbon group, and the aliphatic hydrocarbon group and the alicyclic hydrocarbon group can have a hydroxy group, and a methylene in the alkyl group and the alicyclic hydrocarbon group can be replaced by —O— or —CO—,
Ra10, Ra11and Ra12each independently represent a C1-C12 alkyl group or a C3-C20 alicyclic hydrocarbon group, and Ra10and Ra11can be bonded each other to form a C3-C20 ring together with the carbon atom to which Ra10and Ra11are bonded, and the alkyl group and the alicyclic hydrocarbon group can have a hydroxy group, and a methylene group in alkyl group and the alicyclic hydrocarbon group can be replaced by —O— or —CO—.

As Ra9, examples of the alkyl group which can have a hydroxy group include a methyl group, an ethyl group, a propyl group, a hydroxymethyl group and a 2-hydroxyethyl group.

Examples of the aliphatic hydrocarbon group represented by Ra13include a methyl group, an ethyl group, a propyl group.

Examples of the alicylic hydrocarbon group represented by Ra13include a cyclopropyl group, a cyclobutyl group, an adamantyl group, an adamantylmethyl group, a 1-adamantyl-1-methylethyl group, a 2-oxo-oxolan-3-yl group and a 2-oxo-oxolan-4-yl group.

The alicylic hydrocarbon group represented by Ra10, Ra11and Ra12, which may be a monocyclic or polycyclic group. Examples of the monocyclic alicyclic hydrocarbon group include cycloalkyl groups such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cycloheptyl group, a cyclodecyl group. Examples of the polycyclic alicyclic hydrocarbon group include a hydronaphthyl group, an adamantyl group, a 2-alkyladamantane-2-yl group, a 1-(adamantane-1-yl)alkane-1-yl group, a norbornyl group, a methylnorbornyl group, and an isobornyl group.

When the divalent hydrocarbon group is formed by bonding Ra10and Ra11, examples of —C(Ra10)(Ra11)(Ra12) include the following ones;

where Ra12is as defined above.

When the resin has a structural unit represented by formula (a1-3), the photoresist composition having excellent resolution and higher dry-etching resistance tends to be obtained.

When Resin (A) comprises the structural unit represented by formula (a1-3), the content of the structural unit is usually 10 to 95% by mole and preferably 15 to 90% by mole and more preferably 20 to 85% by mole based on total molar of all the structural units of the resin.

Other examples of the structural unit (a1) having a group represented by formula (2) include one represented by formula (a1-4):

wherein Ra32represents a hydrogen atom, a halogen atom, a C1-C6 alkyl group or a C1-C6 halogenated alkyl group,
Ra33is independently in each occurrence a halogen atom, a hydroxy group, a C1-C6 alkyl group, a C1-C6 alkoxy group, a C2-C4 acyl group, a C2-C4 acyloxy group, an acryloyl group or a methacryloyl group, larepresents an integer of 0 to 4,
Ra34and Ra35each independently represent a hydrogen atom or a C1-C12 hydrocarbon group, Ra36represents a C1-C20 aliphatic hydrocarbon group in which a methylene group can be replaced by —O— or —S—, and Ra35and Ra36are bonded to each other to jointly represent a C2-C20 divalent hydrocarbon group in which a methylene group can be replaced by —O— or —S—.

Examples of the alkyl group represented by Ra32and Ra33include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, and a hexyl group, preferably a C1-C4 alkyl group, more preferably a methyl group and an ethyl group, and still more preferably a methyl group.

Examples of the alkoxy group represented by Ra33include a methoxy group, an ethoxy group, a propoxy group, an isopropoxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group and a hexyloxy group. Examples of the acyl group represented by Ra33include an acetyl group, a propyonyl group and a butyryl group, and examples of the acyloxy group represented by Ra33include an acetyloxy group, a propyonyloxy group and a butyryloxy group.

Examples of halogen atom represented by Ra32and Ra33include a fluorine atom, a chlorine atom, and a bromine atom.

Examples of the groups represented by Ra34and Ra35include those as referred to for Ra1′and Ra2′.

Examples of the groups represented by Ra36include those as referred to for Ra3′.

Ra32preferably represents a hydrogen atom.

Ra33is preferably a C1-C4 alkoxy group, more preferably a methoxy group and an ethoxy group, and still more preferably a methoxy group.

The symbol “la” preferably represents 0 or 1, more preferably 1. Ra34preferably represents a hydrogen atom.

Ra35is preferably a C1-C12 monovalent hydrocarbon group, more preferably a methyl group and an ethyl group.

The hydrocarbon group represented by Ra36includes a C1-C18 alkyl group, a C3-C18 monovalent alicyclic hydrocarbon group, a C6-C18 monovalent aromatic hydrocarbon group, and any combination of them, and preferably a C1-C18 alkyl group, a C3-C18 monovalent alicyclic hydrocarbon group and a C7-C18 aralkyl group. These groups may be unsubstituted or substituted. The alkyl group and the monovalent alicyclic hydrocarbon group are preferably unsubstituted. As the substituent for the monovalent aromatic hydrocarbon group, a C6-C10 aryloxy group is preferred.

Examples of the monomer from which the structural unit (a1-4) is derived include monomers recited in JP2010-204646A1. Among them, the monomers represented by formulae (a1-4-1), (a1-4-2), (a1-4-3), (a1-4-4), (a1-4-5), (a1-4-6) and (a1-4-7) are preferred, and the monomers represented by formulae (a1-4-1), (a1-4-2), (a1-4-3), (a1-4-4) and (a1-4-5) are more preferred.

When Resin (A) comprises a structural unit represented by formula (a1-4), its content is usually 10 to 95% by mole, preferably 15 to 90% by mole and more preferably 20 to 85% by mole based on 100% by mole of all the structural units of the resin.

Other examples of the structural unit having an acid-labile group include one represented by formula (a1-5):

In formula (1-5), Ra8represents a hydrogen atom, a halogen atom, or a C1-C6 alkyl group which may have a halogen atom,

Za1represents a single bond or *—(CH2)h3—CO-L54- in which k1 represents an integer of 1 to 4 and * represents a binding site to L54,

L51, L52, L53and L54each independently represent an oxygen atom or a sulfur atom,

s1 represents an integer of 1 to 3, and s1′ represents an integer of 0 to 3.

Herein, the structural unit represented by formula (a1-5) is sometimes referred to as “structural unit (a1-5)”.

Examples of halogen atoms include a fluorine atom and chlorine atom, preferably a fluorine atom.

Examples of the alkyl group which may have a halogen atom include a methyl group, an ethyl group, n-propyl group, an isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, a pentyl group, a hexyl group, a heptyl group, a 2-ethylhexyl group, an octyl group, a fluoromethyl group, and a trifluoromethyl group.

In the formula (a1-5), Ra8preferably represents a hydrogen atom, a methyl group, or trifluoromethyl group.

It is preferred that one of L52and L53represents an oxygen atom, while the other represents a sulfur atom.

s1 preferably represents 1. s1′ represents an integer of 0 to 2.

Za1preferably represents a single bond or *—CH2—CO—O— wherein * represents a binding site to L51.

Examples of the monomer from which the structural unit (a1-5) is derived include one mentioned in JP2010-61117A1 and the following ones:

When Resin (A) comprises a structural unit (a1-5), its content is usually 1 to 50% by mole, preferably 3 to 45% by mole and more preferably 5 to 40% by mole based on 100% by mole of all the structural units of the resin.

Resin (A) comprises preferably one or more of the structural units (a1-0), (a1-1), (a1-2) and (a1-5), more preferably at least one of the structural units (a1-1), (a1-2) and (a1-5), still more preferably two or more of the structural units (a1-1), (a1-2) and (a1-5), and further more preferably the structural units (a1-1) and (a1-2) or the structural units (a1-1) and (a1-5).

Resin (A) comprises preferably the structural unit (a-1).

The structural unit (s) is derived from a monomer having no acid-labile group.

As to the monomer having no acid-labile group, monomers which have been known to in the art can be used as such monomer, and they are not limited to any specific one provided that it has no acid-labile group.

The structural unit having no acid-labile group preferably has a hydroxy group or a lactone ring. When the resin comprises the structural unit derived from the monomer having no acid-labile group and having a hydroxy group or a lactone ring, a photoresist composition capable of providing a photoresist film with good resolution and adhesiveness of photoresist to a substrate can be obtained.

Hereinafter, the structural unit having no acid-labile group and having a hydroxy group is referred to as “structural unit (a2)”, and the structural unit having no acid-labile group and having a lactone ring is referred to as “structural unit (a3)”.

The hydroxy group which the structural unit (a2) has may be an alcoholic hydroxy group or a phenolic hydroxy group.

When KrF excimer laser (wavelength: 248 nm) lithography system, or a high energy laser such as electron beam and extreme ultraviolet is used as an exposure system, the resin which comprises the structural unit (a2) having a phenolic hydroxy group is preferred. When ArF excimer laser (wavelength: 193 nm) is used as an exposure system, the resin which comprises the structural unit (a2) having an alcoholic hydroxy group is preferred and the resin which comprises the structural unit (a2-1) described later is more preferred.

Resin (A) may comprise one or more of the structural units (a2).

Examples of the structural unit (a2) having a phenolic hydroxy group include one represented by formula (a2-0):

In formula (a2-0), Ra30represents a hydrogen atom, a halogen atom, a C1-C6 alkyl group or a C1-C6 halogenated alkyl group, Ra31is independently in each occurrence a halogen atom, a hydroxy group, a C1-C6 alkyl group, a C1-C6 alkoxy group, a C2-C4 acyl group, a C2-C4 acyloxy group, an acryloyl group or a methacryloyl group, ma represents an integer of 0 to 4.

In the formula (a2-0), examples of the halogen atom include a fluorine atom, a chlorine atom, a bromine atom or iodine atom, examples of the C1-C6 alkyl group include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group and a hexyl group, and a C1-C4 alkyl group is preferred and a C1-C2 alkyl group is more preferred and a methyl group is especially preferred.

Examples of the C1-C6 halogenated alkyl group include a trifluoromethyl group, a pentafluoroethyl group, a heptafluoropropyl group, a heptafluoroisopropyl group, a nonafluorobutyl group, a nonafluoro-sec-butyl group, a nonafluoro-tert-butyl group, a perfluoropentyl group and a perfluorohexyl group. Examples of the C1-C6 alkoxy group include a methoxy group, an ethoxy group, a propoxy group, an isopropoxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group and a hexyloxy group, and a C1-C4 alkoxy group is preferred and a C1-C2 alkoxy group is more preferred and a methoxy group is especially preferred. Examples of the C2-C4 acyl group include an acetyl group, a propyonyl group and a butyryl group, and examples of the C2-C4 acyloxy group include an acetyloxy group, a propyonyloxy group and a butyryloxy group.

In the formula (a2-0), ma is preferably 0, 1 or 2, and is more preferably 0 or 1, and especially preferably 0.

Among them, the structural units represented by formulae (a2-0-1), (a2-0-2), (a2-0-3) and (a2-0-4) are preferred as the structural unit (a2-0), and those represented by formulae (a2-0-1) and (a2-0-2) are more preferred.

Resin (A) which comprises a structural unit represented by formula (a2-0) can be produced, for example, by polymerizing a monomer where its phenolic hydroxy group has been protected with a suitable protecting group, followed by deprotection. Examples of the protecting group for a phenolic hydroxy group include an acetyl group.

When Resin (A) comprises the structural unit represented by formula (a2-0), its content is usually 5 to 95% by mole and preferably 10 to 80% by mole and more preferably 15 to 80% by mole based on total molar of all the structural units of the resin.

Examples of the structural unit (a2) having an alcoholic hydroxy group include one represented by formula (a2-1):

wherein Ra14represents a hydrogen atom or a methyl group, Ra15and Ra16each independently represent a hydrogen atom, a methyl group or a hydroxy group, La3represents *—O— or *—O— (CH2)k2—CO—O— in which * represents a binding site to —CO—, and k2 represents an integer of 1 to 7, and o1 represents an integer of 0 to 10.

Hereinafter, the structural unit represented by formula (a2-1) is referred to as “structural unit (a2-1)”.

In the formula (a2-1), Ra14is preferably a methyl group. Ra15is preferably a hydrogen atom. Ra16is preferably a hydrogen atom or a hydroxy group. La3is preferably *—O— or *—O— (CH2)f2—CO—O— in which * represents a binding site to —CO—, and f2 represents an integer of 1 to 4, is more preferably *—O— and *—O—CH2—CO—O—, and is still more preferably *—O—, and o1 is preferably 0, 1, 2 or 3 and is more preferably 0 or 1.

Examples of monomers from which the structural unit (a2-1) is derived include compounds mentioned in JP2010-204646A.

Preferred examples of the structural unit (a2-1) include those represented by formulae (a2-1-1) to (a2-1-6).

Among them, more preferred are the structural units represented by formulae (a2-1-1), (a2-1-2), (a2-1-3) and (a2-1-4), still more preferred are the structural units represented by formulae (a2-1-1) and (a2-1-3).

When Resin (A) comprises the structural unit (a2-1), its content is usually 1 to 45% by mole, preferably 1 to 40% by mole, and more preferably 1 to 35% by mole, and especially preferably 2 to 20% by mole, based on total molar of all the structural units of the resin.

Examples of the lactone ring of the structural unit (a3) include a monocyclic lactone ring such as β-propiolactone ring, γ-butyrolactone ring and γ-valerolactone ring, and a condensed ring formed from a monocyclic lactone ring and the other ring. Among them, preferred are γ-butyrolactone ring and a condensed lactone ring formed from γ-butyrolactone ring and the other ring. Preferred examples of the structural unit (a3) include those represented by formulae (a3-1), (a3-2), (a3-3) and (a3-4):

In formulae, La4, La5and La6each independently represent *—O— or *—O—(CH2)k3—CO—O— in which * represents a binding site to —CO— and k3 represents an integer of 1 to 7,

Ra18, Ra19and Ra20each independently represent a hydrogen atom or a methyl group,

Ra22and Ra23are independently in each occurrence a carboxyl group, a cyano group or a C1-C4 monovalent aliphatic hydrocarbon group,

Ra24each independently represent a hydrogen atom, a halogen atom, or a C1-C6 alkyl group which may have a halogen atom,

and p1 represents an integer of 0 to 5, q1 and r1 independently each represent an integer of 0 to 3.

Examples of halogen atom represented by Ra24include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.

Examples of the alkyl group represented by Ra24include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, and a hexyl group, preferably a C1-C4 alkyl group, and more preferably a methyl group and an ethyl group.

As to Ra24, examples of the alkyl group which has an halogen atom include a trifluoromethyl group, a pentafluoroethyl group, a heptafluoropropyl group, a heptafluoroisopropyl group, a nonafluorobutyl group, a nonafluoro-sec-butyl group, a nonafluoro-tert-butyl group, a perfluoropentyl group, a perfluorohexyl group, a trichloromethyl group, a tribromomethyl group, and a triiodomethyl group.

As to La8and La9, examples of the alkanediyl group include a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group and a hexane-1,6-diyl group, a butane-1,3-diyl group, 2-methylpropane-1,3-diyl group, a 2-methylpropane-1,2-diyl group, a pentane-1,4-diyl group and a 2-methylbutane-1,4-diyl group.

It is preferred that La4, La5and La6each independently represent *—O— or *—O—(CH2)d1—CO—O— in which * represents a binding site to —CO— and d1 represents an integer of 1 to 4, and it is more preferred that La4, La5and La6are *—O— and *—O—CH2—CO—O—, and it is still more preferred that La4, La5and La6are *—O—.

Ra18, Ra19and Ra20are preferably methyl groups. Ra21is preferably a methyl group. It is preferred that Ra22and Ra23are independently in each occurrence a carboxyl group, a cyano group or a methyl group.

It is preferred that p1, q1 and r1 each independently represent an integer of 0 to 2, and it is more preferred that p1, q1 and r1 each independently represent 0 or 1.

Ra24is preferably a hydrogen atom or a C1-C4 alkyl group, more preferably a hydrogen atom, a methyl group or an ethyl group, and still more preferably a hydrogen atom or a methyl group.

La7represents preferably a single bond or *1-La8-CO—O—, more preferably a single bond, *1—CH2—CO—O— or *1—C2H4—CO—O—.

Examples of the structural unit (a3) include the following ones.

The structural unit (a3) is preferably one of formulae (a3-1-1) to (a3-1-4), formulae (a3-2-1) to (a3-2-4), formulae (a3-3-1) to (a3-3-4) and formulae (a3-4-1) to (a3-4-12), more preferably one of formulae (a3-1-1), formula (a3-1-2), formulae (a3-2-3) to (a3-2-4) and formulae (a3-4-1) to (a3-4-2), and still more preferably one of formulae (a3-1-1), (a3-2-3) and (a3-4-2).

Examples of the monomer from which the structural unit (a3) is derived include those mentioned in US2010/203446A1, US2002/098441A1 and US2013/143157A1.

When Resin (A) comprises the structural unit (a3), its content thereof is preferably 5 to 70% by mole, and more preferably 10 to 65% by mole and more preferably 10 to 60% by mole, based on total molar of all the structural units of the resin.

Examples of another structural unit having no acid-labile group include a structural unit having a fluorine atom and a structural unit which has a hydrocarbon not being removed therefrom by action of an acid.

Examples of the structural unit having a fluorine atom include the following one.

Hereinafter, the structural unit having no acid-labile group but having a halogen atom is referred to as “structural unit (a4)”. Halogen atoms for the structural unit (a4) may be a fluorine atom, a chlorine atom, a bromine atom, or an iodine atom. The structural unit (a4) has preferably a fluorine atom.

Examples of the structural unit (a4) include one represented by formula (a4-0):

wherein R5represents a hydrogen atom or a methyl group;
L4represents a single bond or a C1-C4 aliphatic saturated hydrocarbon group, preferably a C1-C4 aliphatic saturated hydrocarbon group;
L3represents a C1-C8 perfluoroalkanediyl group or a C3-C12 alicyclic perfluorohydrocarbon group; and
R6represents a hydrogen atom or a fluorine atom.

Examples of the alicyclic perfluorohydrocarbon group for L3include a perfluoroadamantandiyl group.

L4is preferably a methylene group or an ethylene group, more preferably a methylene group.

Examples of the structural unit represented by formula (a4-0) include the following ones and those in which a methyl group has been replaced by a hydrogen atom in each of the following formulae.

Examples of the structural unit (a4) include one represented by formula (a4-1)

wherein Ra41represents a hydrogen atom or a methyl group;
Aa41represents a C1-C6 divalent alkanediyl group which may have a substituent or a moiety represented by formula (a-g1):
-Aa42Xa41-Aa43sXa42-Aa44-  (a-g1)
in which s represents an integer of 0 to 1,
Aa42and Aa44respectively represent a C1-C5 divalent hydrocarbon group which may have a substituent,
Aa43represents a single bond or a C1-C5 divalent hydrocarbon group which may have a substituent,
Xa41and Xa42respectively represent —O—, —CO—, —CO—O—, or —O—CO—, provided that the sum of carbon atoms of Aa42, Aa43, Aa44, Xa41and Xa42is 6 r less;
Ra42represents a C1-C20 monovalent hydrocarbon group which may have a substituent, provided that each or both of Aa41and Ra42have a halogen atom; and
Aa44is bonded to —O—CO—Ra42

Examples of halogen atom for formula (a4-1) include a fluorine atom, a chlorine atom, a bromine atom and an iodine atom.

The divalent hydrocarbon group is preferably a divalent saturated hydrocarbon group while it may have a carbon-carbon double bond. Examples of the divalent saturated hydrocarbon group include alkanediyl groups which may be a linear or branched one, divalent alicyclic hydrocarbon groups, and combination of them.

Examples of the monovalent hydrocarbon group for Ra42include monovalent chain or cyclic saturated hydrocarbon groups, a monovalent aromatic hydrocarbon group, and combination of them.

Examples of monovalent chain hydrocarbon group include a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a decyl group, a dodecyl group, a hexadecyl group, a pentadecyl group, a hexyldecyl group, heptadecyl group and an octadecyl group.

Examples of monovalent cyclic hydrocarbons include cycloalkyl groups such as a cyclopentyl group, a cyclohexyl group, a cycloheptyl group and a cyclooctyl group; and monovalent polycyclic hydrocarbon groups such as a decahydronaphthyl group, an adamantyl group, a norbornyl group, and the following groups where * represents a binding position.

Examples of monovalent aromatic hydrocarbon groups include a phenyl group, a naphthyl group, an anthryl group, a biphenylyl group, a phenanthryl group and a fluorenyl group.

The monovalent hydrocarbon group for Ra42is preferably monovalent chain and cyclic hydrocarbon groups and combination of them, which may have a carbon-carbon double bond, and more preferably a monovalent chain hydrocarbon group and cyclic hydrocarbon group and combination of them.

Ra42is preferably a monovalent aliphatic hydrocarbon group which has a substituent, more preferably a monovalent aliphatic hydrocarbon group which has a halogen atom and/or a group represented by formula (a-g3).
Xa43-Aa45(a-g3)
in which Xa43represents an oxygen atom, a carbonyl group, a carbonyloxy group or an oxycarbonyl group,
Aa45represents a C3-C17 monovalent saturated hydrocarbon group which may have a fluorine atom.

When Ra42is a monovalent saturated hydrocarbon group which has a group represented by formula (a-g3), Ra42has preferably 15 or less carbon atoms, more preferably 12 or less carbon atoms in total including the carbon atoms of formula (a-g3). If Ra42has a group represented by formula (a-g3), the number of the group is preferably 1.

The monovalent saturated hydrocarbon group which has a group represented by formula (a-g3) is preferably a group represented by formula (a-g2):
-Aa46-Xa44-Aa47(a-g2)
in which Aa46represents a C3-C17 divalent saturated hydrocarbon group which may have a fluorine atom, Xa44represents a carbonyloxy group or an oxycarbonyl group, and Aa47represents a C3-C17 divalent saturated hydrocarbon group which may have a fluorine atom, provided that Aa46, Aa47and Xa44have 18 or less of carbon atoms in total and one or both of Aa46and Aa47have a fluorine atom.

The halogen-containing saturated hydrocarbon group represented by Ra42is preferably a monovalent fluorine-containing saturated hydrocarbon group, more preferably a perfluoroalkyl group or a perfluorocycloalkyl group, still more preferably a C1-C6 perfluoroalkyl group, and further more preferably a C1-C3 perfluoroalkyl group.

Examples of perfluoroalkyl group include a perfluoromethyl group, a perfluoroethyl group, a perfluoropropyl group, a perfluorobutyl group, a perfluoropentyl group, a perfluorohexyl group, a perfluoroheptyl group, and a perfluorooctyl group. Examples of the perfluorocycloalkyl group include perfluorocyclohexyl group.

The divalent saturated hydrocarbon group represented by Aa46has preferably 1 to 6, more preferably 1 to 3 carbon atoms.

The monovalent saturated hydrocarbon group represented by Aa47has preferably 4 to 15, more preferably 5 to 12 carbon atoms. Aa47is more preferably a cyclohexyl group or an adamantyl group.

Examples of the moiety represented by -Aa46-Xa44-Aa47include the following ones.

In each formula, * represents a binding position to a carbonyl group.

Examples of Aa41typically include a C1-C6 alkanediyl group which may be a linear chain or branched chain. Specific examples of them include linear chain alkanediyl groups such as a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group, or a hexane-1,6-diyl group; and branched chain alkanediyl groups such as a propane-1,3-diyl group, a butane-1,3-diyl group, a 1-methylbutane-1,2-diyl group, or a 2-methylbutane-1,4-diyl group. Examples of the substituents which such alkanediyl group may have include a hydroxy group or a C1-C6 alkoxy group.

Aa41is preferably a C1-C4 alkanediyl group, more preferably a C2-C4 alkanediyl group, and still more preferably an ethylene group.

Examples of the alkanediyl group represented by Aa42, Aa43and Aa44include a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a 2-methylpropane-1,3-diyl group, or a 2-methylbutane-1,4-diyl group. Examples of the substituents which such alkanediyl group may have include a hydroxy group or a C1-C6 alkoxy group.

Examples of the moiety represented by formula (a-g1) where Xa42is an oxygen atom, a carbonyl group, a carbonyloxy group or an oxycarbonyl group include the following ones:

in which * and ** represent binding sites, and ** represents a binding site to —O—CO—Ra42

The structural unit represented by formula (a4-1) is preferably one represented by formula (a4-2) or (a4-3).

In formula, Rf1represents a hydrogen atom or a methyl group.

Rf2represents a C1-C20, preferably C1-C10, monovalent hydrocarbon group having a fluorine atom.

The alkanediyl groups represented by Af1may be a linear chain or branched chain. Specific examples of them include linear chain alkanediyl groups such as a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl group, or a hexane-1,6-diyl group; and branched chain alkanediyl groups such as a propane-1,3-diyl group, a butane-1,3-diyl group, a 1-methylbutane-1,2-diyl group, or a 2-methylbutane-1,4-diyl group. Examples of the substituents which such alkanediyl group may have include a hydroxy group or a C1-C6 alkoxy group.

The monovalent hydrocarbon group represented by Rf2includes monovalent saturated hydrocarbon groups and monovalent aromatic hydrocarbon groups. The monovalent saturated hydrocarbon groups may be a chain or cyclic saturated hydrocarbon group, or a combined group of them.

The monovalent saturated hydrocarbon groups are preferably an alkyl group or a monovalent alicyclic hydrocarbon group.

Examples of the alkyl group include a methyl group, an ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group and 2-ethylhexyl group.

The monovalent alicyclic hydrocarbon groups may be monocyclic or polycyclic groups. Examples of monovalent monocyclic hydrocarbon groups include a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a methylcyclohexyl group, a dimethylcyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cycloheptyl group and a cyclodecyl group.

Examples of monovalent polycyclic hydrocarbon groups include a decahydronaphthyl group, an adamantyl group, a norbornyl group, and an isobornyl group.

Examples of the combined group of the above-mentioned hydrocarbon group include a 2-alkyladamantane-2-yl group, a 1-(adamantane-1-yl)alkane-1-yl group, and a methylnorbornyl group.

Examples of monovalent hydrocarbon groups having a fluorine atom for Rf2include monovalent fluoroalkyl groups and monovalent fluorine atom-containing alicyclic hydrocarbon groups.

In formula (a4-2), Af1is preferably a C2-C4 alkylene group, and more preferably an ethylene group. Rf2is preferably a C1-C6 fluoroalkyl group.

In formula, Rf11represents a hydrogen atom or a methyl group.

Af13represents a C1-C18 divalent saturated hydrocarbon group which may have a fluorine atom.

Xf12represents a carbonyloxy group or an oxycarbonyl group.

Af14represents a C1-C17 divalent saturated hydrocarbon group which may have a fluorine atom, provided that one or both of Af13and

Examples of the alkanediyl group represented by Af11include those as referred to for Af12.

As to Af13, the divalent saturated hydrocarbon group includes chain saturated hydrocarbon groups, cyclic saturated hydrocarbon groups and combined groups of these groups.

As to Af13, the divalent saturated hydrocarbon group which may have a fluorine atom is preferably a divalent saturated chain hydrocarbon group which may have a fluorine atom, more preferably a perfluoroalkanediyl group.

Examples of the divalent aliphatic hydrocarbon group which may have a fluorine atom include an alkanediyl group such as a methyl group, an ethylene group, a propanediyl group, a butanediyl group and pentanediyl group; and a perfluoroalkanediyl group such as a difluoromethylene group, a perfluoroethylene group, a perfluoropropanediyl group, a perfluorobutanediyl group and perfluoropentanediyl group.

The divalent cyclic hydrocarbon group which may have a fluorine atom may be a divalent monocyclic or polycyclic group.

Examples of the divalent monocyclic hydrocarbon group which may have a fluorine atom include a cyclohexanediyl group and a perfluorocyclohexanediyl group.

Examples of the divalent polycyclic hydrocarbon group which may have a fluorine atom include an adamantanediyl group, norbornanediyl group, and a perfluoroadamantanediyl group.

In the group represented by Af14, the monovalent saturated hydrocarbon group includes chain saturated hydrocarbon groups, cyclic saturated hydrocarbon groups and combined groups of these saturated hydrocarbon groups.

As to Af14, the monovalent aliphatic hydrocarbon group which may have a fluorine atom is preferably a monovalent saturated aliphatic hydrocarbon group which may have a fluorine atom, more preferably a perfluoroalkanediyl group.

Examples of the monovalent aliphatic hydrocarbon group which may have a fluorine atom include a trifluoromethyl group, a fluoromethyl group, a methyl group, a perfluoroethyl group, a 1,1,1-trifluoroethyl group, a 1,1,2,2-tetrafluoroethyl group, an ethyl group, a perfluoropropyl group, a 1,1,1,2,2-pentafluoropropyl group, propyl group, a perfluorobutyl group, 1,1,2,2,3,3,4,4-octafluorobutyl group, a butyl group, a perfluoropentyl group, 1,1,1,2,2,3,3,4,4-nonafluoropentyl group, a pentyl group, a hexyl group, a perfluorohexyl group, a heptyl group, a perfluoroheptyl group, an octyl group and a perfluorooctyl group.

The monovalent cyclic hydrocarbon group which may have a fluorine atom may be monocyclic or polycyclic monovalent group.

Examples of the monovalent monocyclic cyclic hydrocarbon group which may have a fluorine atom include a cyclopropyl group, cyclopentyl group, cyclohexyl group, and perfluorocyclohexyl group. Examples of the monovalent polycyclic hydrocarbon group which may have a fluorine atom include an adamantyl group, a norbornyl group, and a perfluoroadamantyl group.

Examples of the combined groups of the above-mentioned aliphatic hydrocarbon group include a cyclopropylmethyl group, a cyclobutylmethyl group, an adamantylmethyl group, a norbornylmethyl group and a perfluoroadamantylmethyl group.

In formula (a4-3), Af11is preferably an ethylene group.

The divalent aliphatic hydrocarbon group represented by Af13has preferably 6 or less, more preferably 2 to 3, of carbon atoms. The monovalent aliphatic hydrocarbon group represented by Af14has preferably 3 to 12, more preferably 3 to 10, of carbon atoms. Af14has preferably a C3-C12 monovalent alicyclic hydrocarbon group, more preferably a cyclopropylmethyl group, a cyclopentyl group, a cyclohexyl group, a norbornyl group or an adamantyl group.

Examples of the structural unit of formula (a4-2) include preferably those represented by formulae (a4-1-1) to (a4-1-22).

Examples of the structural unit represented by formula (a4-3) include preferably those represented by formulae (a4-1′-1) to (a4-1′-22).

Another example of the structural unit (a4) includes those represented by formula (a4-4).

In formula (a4-4), wherein Rf21represents a hydrogen atom or a methyl group;

Af2represents —(CH2)j1—, —(CH2)j2—O—(CH2)j3— or —(CH2)j4—CO—O—(CH2)j5— where j1, j2, j3, j4 or j5 each independently represent an integer of 1 to 6; and

Rf22represents a C1-C10 monovalent hydrocarbon group having a fluorine atom.

For Rf22, examples of monovalent hydrocarbon group having a fluorine atom include those as referred to for Rf22.

Rf22is preferably a C1-C10 monovalent alkyl group having a fluorine atom or a C3-C10 monovalent alicyclic hydrocarbon group having a fluorine atom, more preferably a C1-C10 monovalent alkyl group having a fluorine atom, and still more preferably a C1-C6 monovalent alkyl group having a fluorine atom.

In formula (a4-4), Af21is preferably —(CH2)j1—, more preferably a methylene or ethylene group, and still more preferably a methylene group.

Examples of the structural unit represented by formula (a4-4) include preferably the following ones.

When Resin (A) comprises the structural unit (a4), its content is preferably 1 to 20% by mole, more preferably 2 to 15% by mole and still more preferably 3 to 10% by mole based on 100% by mole of all the structural units of the resin.

Other examples of the structural unit having no acid-labile group include one having an acid-stable hydrocarbon group.

Herein, the term “acid-stable hydrocarbon group” means such a hydrocarbon group that is not removed from the structural unit having the group by action of an acid generated from an acid generator as described later.

The acid-stable hydrocarbon group may be a linear, branched or cyclic hydrocarbon group.

The structural unit which has a hydrocarbon not being removed therefrom by action of an acid may have a linear, branched or cyclic hydrocarbon, preferably an alicyclic hydrocarbon group.

Examples of the structural unit having an acid-stable hydrocarbon group include one represented by formula (a5-1):

where R51represents a hydrogen atom or a methyl group;
R52represents a C3-C18 monovalent alicyclic hydrocarbon group which may have a C1-C8 monovalent aliphatic hydrocarbon group as a substituent, provided that the alicyclic hydrocarbon group has no substituent on the carbon atom bonded to L51; and
L51represents a single bond or a C1-C18 divalent saturated hydrocarbon group where a methylene group can be replaced by an oxygen atom or carbonyl group.

The alicyclic hydrocarbon group represented by R52may be monocyclic or polycyclic one.

Examples of the alicyclic hydrocarbon group include a monocyclic hydrocarbon group such as a C3-C18 cycloalkyl group (e.g. a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group) and a polycyclic alicyclic hydrocarbon group such as an adamantyl group, or a norbornyl group.

Examples of the aliphatic hydrocarbon group include an alkyl groups such as a methyl group, an ethyl group, n-propyl group, isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, a pentyl group, a hexyl group, an octyl group and 2-ethylhexyl group. Examples of the alicyclic hydrocarbon group having a substituent include a 3-hydroxyadamantyl group, and a 3-methyladamantyl group. R52is preferably a C3-C18 unsubstituted alicyclic hydrocarbon group, more preferably an adamantyl group, a norbornyl group or a cyclohexyl group.

Examples of the divalent saturated hydrocarbon group represented by L51include divalent aliphatic hydrocarbon groups and divalent alicyclic hydrocarbon groups, preferably divalent aliphatic hydrocarbon groups.

Examples of divalent aliphatic hydrocarbon groups include alkanediyl groups such as a methylene group, an ethylene group, a propanediyl group, a butanediyl group and a pentanediyl group.

The divalent alicyclic hydrocarbon groups may be monocyclic or polycyclic one.

Examples of divalent monocyclic hydrocarbon groups include cycloalkanediyl groups such as a cyclopentanediyl group and a cyclohexanediyl group. Examples of divalent polycyclic alicyclic hydrocarbon groups include an adamantanediyl group and a norbornanediyl group.

Examples of the divalent hydrocarbon group where a methylene group has been replaced by an oxygen atom or carbonyl group include those represented by formulae (L1-1) to (L1-4).

In these formulae, * represents a binding position to an oxygen atom.

Xx1is a carbonyloxy group or an oxycarbonyl group; and

Lx1is a C1-C16 divalent saturated hydrocarbon group, and Lx2is a single bond or a C1-C15 divalent aliphatic saturated hydrocarbon group, provided that the total number of the carbon atoms in Lx1and Lx2is 16 or less.

Lx3is a C1-C17 divalent saturated hydrocarbon group, and Lx4is a single bond or a C1-C16 divalent aliphatic saturated hydrocarbon group, provided that the total number of the carbon atoms in Lx3and Lx4is 17 or less.

Lx5is a C1-C15 divalent saturated hydrocarbon group, and Lx6and Lx7are a single bond or a C1-C14 divalent aliphatic saturated hydrocarbon group, provided that the total number of the carbon atoms in Lx5, Lx6and Lx7is 15 or less.

Lx8and Lx9are each independently a single bond or a C1-C12 divalent aliphatic saturated hydrocarbon group, and Wx1is a C3-C15 divalent cyclic saturated hydrocarbon group, provided that the total number of the carbon atoms in Lx8, Lx9and Wx1is 15 or less.

Lx1is preferably a C1-C8 divalent saturated hydrocarbon group, more preferably a methylene group or an ethylene group.

Lx2is preferably a single bond, or a C1-C8 divalent saturated hydrocarbon group, more preferably a single bond.

Lx3is preferably a C1-C8 divalent saturated hydrocarbon group, more preferably a methylene group or an ethylene group.

Lx4is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group, more preferably a single bond, a methylene group or an ethylene group.

Lx5is preferably a C1-C8 divalent saturated hydrocarbon group, more preferably a methylene group or an ethylene group.

Lx6is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group, more preferably a methylene group or an ethylene group.

Lx7is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group, more preferably a methylene group or an ethylene group.

Lx8is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group, more preferably a single bond or a methylene group.

Lx9is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group, more preferably a single bond or a methylene group.

Wx1is a preferably C3-C10 divalent cyclic saturated hydrocarbon group, more preferably a cyclohexanediyl group or an adamantanediyl group.

Examples of the divalent hydrocarbon group represented by formula (L1-1) include the following ones.

In these formulae, * represents a binding position to an oxygen atom.

Examples of the divalent hydrocarbon group represented by formula (L1-2) include the following ones.

In these formulae, * represents a binding position to an oxygen atom.

Examples of the divalent hydrocarbon group represented by formula (L1-3) include the following ones.

In these formulae, * represents a binding position to an oxygen atom.

Examples of the divalent hydrocarbon group represented by formula (L1-4) include the following ones.

In these formulae, * represents a binding position to an oxygen atom.

L51is preferably a single bond or a group represented by formula (L1-1).

Examples of the structural unit represented by formula (a5-1) include the following ones and those where a methyl group has been replaced by a hydrogen atom in each formula.

Resin (A) comprises preferably the structural unit (a1) and the structural unit having no acid-labile group.

In Resin (A), the structural unit (a1) is one of the structural unit (a1-1) and the structural unit (a1-2), more preferably the structural unit (a1-2). The structural unit (a1-2) is preferably which comprises a cyclohexyl group or a cyclopentyl group. The structural unit having no acid-labile group is preferably one of the structural unit (a2) and the structural unit (a3). The structural unit (a2) is preferably the structural unit (a2-1). The structural unit (a3) is preferably one of the structural unit (a3-1), the structural unit (a3-2) and the structural unit (a3-4). Resin (A) comprises preferably the structural unit (a1) derived from a structural unit having an adamantyl group, preferably structural unit (a1-1). The content of the structural unit having an adamantyl group is preferably 15% by mole or more of the total amount of the structural unit (a1). The more is the structural unit having an adamantyl group, the more improved is the resistance of the photoresist film to dry etching.

Resin (A) can be produced according to known polymerization methods such as radical polymerization.

The resin has usually 2,000 or more of the weight-average molecular weight, preferably 2,500 or more of the weight-average molecular weight, more preferably 3,000 or more of the weight-average molecular weight. The resin has usually 50,000 or less of the weight-average molecular weight, preferably more 30,000 or less of the weight-average molecular weight, and preferably more 15,000 or less of the weight-average molecular weight.

The weight-average molecular weight can be measured with gel permeation chromatography.

Examples of another resin than Resin (A) include what consists of structural units having no acid-labile group, preferably what comprises, not the structural unit (a1), but the structural unit (a4). Here, such another resin is referred to as “Resin (X)”.

Resin (X) may be one which consists of the structural unit having a fluorine atom, or one which further comprise the structural unit (a2), the structural unit (a3) or another structural unit having no acid-labile group, known in the art.

In Resin (X), the content of the structural unit (a4) is preferably 40% by mole or more, more preferably 45% by mole or more, still more preferably 50% by mole or more, and further more preferably 80% by mole or more, based on sum of the structural units in the resin.

Resin (X) usually has 8000 or more of the weight-average molecular weight, preferably 10000 or more of the weight-average molecular weight. The resin usually has 80,000 or less of the weight-average molecular weight, preferably has 60,000 or less of the weight-average molecular weight.

The weight-average molecular weight can be measured with known methods such as liquid chromatography or gas chromatography.

When the photoresist composition comprises Resin (X), the content of the resin is preferably 1 to 60 weight parts, more preferably 1 to 50 weight parts, and still more preferably 1 to 40 weight parts, and further still more preferably 2 to 30 weight parts, relative to 100 parts of Resin (A). Its content may be in the range of 7 to 30 weight parts relative to 100 parts of Resin (A)

The total content of the resins in the photoresist composition of the present invention is usually 80% by mass or more based on sum of solid component, and usually 99% by mass or less.

In this specification, “solid component” means components other than solvent in the photoresist composition.

In the photoresist composition, an acid generates from the acid generator by exposure. The acid catalytically acts against an acid-labile group in the resin to cleave the acid-labile group.

The acid generator includes a nonionic acid generator, an ionic acid generator and the combination thereof. Examples of the nonionic acid generator include an organo-halogen compound, a sulfonate compound such as a 2-nitrobenzylsulfonate, an aromatic sulfonate, an oxime sulfonate, an N-sulfonyloxyimide, a sulfonyloxyketone and diazonaphthoquinone 4-sulfonate, and a sulfone compound such as a disulfone, a ketosulfone and a sulfonyldiazomethane. Examples of the ionic acid generator include an onium salt compound such as a diazonium salt, a phosphonium salt, a sulfonium salt and an iodonium salt. Examples of the anion of the onium salt include a sulfonic acid anion, a sulfonylimide anion and a sulfonylmethide anion.

The acid generator for the photoresist composition is preferably a fluorine-containing acid generator.

Preferable examples of the acid generator include a salt represented by the formula (B1):

wherein Q1and Q2each independently represent a fluorine atom or a C1-C6 perfluoroalkyl group,
Lb1represents a single bond or a C1-C24 divalent saturated hydrocarbon group in which a methylene group can be replaced by —O— or —CO— and in which a hydrogen atom can be replaced by a fluorine atom or a hydroxy group, and
Y represents a hydrogen atom or a C3-C18 alicyclic hydrocarbon group which can have a substituent and in which a methylene group can be replaced by —O—, —CO— or —SO2—, and
Z+represents an organic cation.

Examples of the perfluoroalkyl group include a trifluoromethyl group, a pentafluoroethyl group, a heptafluoropropyl group, a nonafluorobutyl group, an undecafluoropentyl group and a tridecafluorohexyl group, and a trifluoromethyl group is preferable. Q1and Q2each independently preferably represent a fluorine atom or a trifluoromethyl group, and Q1and Q2are more preferably fluorine atoms.

Examples of the divalent saturated hydrocarbon group represented by Lb1include an alkandiyl group, a monocyclic or polycyclic divalent saturated hydrocarbon group and a group formed by combining two or more groups selected from the group consisting of the alkandiyl group and the monocyclic or polycyclic divalent saturated hydrocarbon group.

Examples thereof include a linear alkanediyl group such as a methylene group, an ethylene group, a propane-1,3-diyl group, a butane-1,4-diyl group, a pentane-1,5-diyl, a hexane-1,6-diyl group, a heptane-1,7-diyl group, an octane-1,8-diyl group, a nonane-1,9-diyl group, a decane-1,10-diyl group, an undecane-1,11-diyl group, a dodecane-1,12-diyl group, a tridecane-1,13-diyl group, a tetradecane-1,14-diyl group, a pentadecane-1,15-diyl group, a hexadecane-1,16-diyl group and a heptadecane-1,17-diyl group,

a branched chain alkanediyl group such as a butane-1,3-diyl group, a2-methylpropane-1,3-diyl group, a2-methylpropane-1,2-diyl group, a pentane-1,4-diyl group and a 2-methylbutane-1,4-diyl group, a monocyclic divalent saturated hydrocarbon group such as a cyclobutane-1,3-diyl group, a cyclopentane-1,3-diyl group, a cyclohexane-1,2-diyl group, a 1-methylcyclohexane-1,2-diyl group, a cyclohexane-1,4-diyl group, a cyclooctane-1,2-diyl group and a cyclooctane-1,5-diyl group, and
a polycyclic divalent saturated hydrocarbon group such as a norbornane-2,3-diyl group, a norbornane-1,4-diyl group, a norbornane-2,5-diyl group, an adamantane-1,2-diyl group, an adamantane-1,5-diyl group and an adamantane-2,6-diyl group.

Examples of the aliphatic hydrocarbon group in which a methylene group has been replaced by —O— or —CO— include those represented by formulae (b1-1), (b1-2) and (b1-3).

In formula (b1-1), Lb2represents a single bond or a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, and Lb3represents a single bond or a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or carbonyl group, provided that total number of the carbon atoms of Lb2and Lb3is up to 22.

In formula (b1-2), Lb4represents a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, and Lb5represents a single bond or a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or carbonyl group, provided that the total carbon atoms of Lb4and Lb5is up to 22.

In formula (b1-3), Lb6represents a single bond or a C1-C23 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, and Lb7represents a single bond or a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or carbonyl group, with the proviso that total carbon number of Lb6and Lb7is up to 23 and with the proviso that formula (b1-3) excludes group having a structure represented by -Lb6-O—CO—.

In these formulae, * represents a binding position, * of the left side represents a binding position to —C(Q1)(Q2)-, and * of the right side represents a binding position to the ring W.

In formulae (b1-1), (b1-2) and (b1-3), the divalent saturated hydrocarbon group includes linear chain alkanediyl groups, branched chain alkanediyl groups, monocyclic or polycyclic divalent saturated hydrocarbon groups, and a group combining two or more of the above-mentioned groups.

Specific examples of the divalent saturated hydrocarbon group include those as referred to for Lb1.

Lb2is preferably a single bond.

Lb4is preferably a C1-C8 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom.

Lb5is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group.

Lb6is preferably a single bond or a C1-C4 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom.

Lb7is preferably a single bond or a C1-C7 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or carbonyl group.

Among them, those of formulae (b1-1) and (b1-3) are preferred. Examples of the group represented by formula (b1-1) include those represented by formulae (b1-4), (b1-5), (b1-6), (b1-7) and (b1-8).

In formula (b1-4), Lb8represents a single bond or a C1-C22 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom or a hydroxyl group.

In formula (b1-5), Lb9represents a C1-C20 divalent saturated hydrocarbon group, and Lb10represents a single bond or a C1-C19 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom, provided that the total carbon atoms of Lb10and Lb9is up to 20.

In formula (b1-6), Lb11represents a C1-C21 divalent saturated hydrocarbon group, and Lb12represents a single bond or a C1-C20 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom, with the proviso that total carbon number of Lb11and Lb12is up to 21.

In formula (b1-7), Lb13represents a C1-C19 divalent saturated hydrocarbon group, Lb14represents a single bond or a C1-C18 divalent saturated hydrocarbon group, and Lb15represents a single bond or a C1-C18 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom, with the proviso that total carbon number of Lb13, Lb14and Lb15is up to 19.

In formula (b1-8), Lb16represents a C1-C18 divalent saturated hydrocarbon group, Lb17represents a C1-C18 divalent saturated hydrocarbon group, and Lb18represents a single bond or a C1-C17 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom, with the proviso that total carbon number of Lb16, Lb17and Lb18is up to 19.

In these formulae, * represents a binding position, * of the left side represents a binding position to —C(Q1)(Q2)-, and * of the right side represents a binding position to the ring W.

In these formulae, the divalent saturated hydrocarbon group includes linear chain alkanediyl groups, branched chain alkanediyl groups, monocyclic or polycyclic divalent saturated hydrocarbon groups, and a group combining two or more of the above-mentioned groups. Specific examples of the divalent saturated hydrocarbon group include those as referred to for Lb1.

Lb10is preferably a single bond or a C1-C19 divalent saturated hydrocarbon group, and more preferably a single bond or a C1-C8 divalent saturated hydrocarbon group.

Lb12is preferably a single bond or a C1-C8 divalent saturated hydrocarbon group.

Lb14is preferably a single bond or a C1-C6 divalent saturated hydrocarbon group.

Lb15is preferably a single bond or a C1-C18 divalent saturated hydrocarbon group, and more preferably a single bond or a C1-C8 divalent saturated hydrocarbon group.

Lb18is preferably a single bond or a C1-C17 divalent saturated hydrocarbon group, and more preferably a single bond or a C1-C4 divalent saturated hydrocarbon group.

Examples of the group represented by formula (b1-3) include those represented by formulae (b1-9), (b1-10) and (b1-11).

In formula (b1-9), Lb19represents a single bond or a C1-C23 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, and Lb20represents a single bond or a C1-C23 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or carbonyl group, provided that the total carbon atoms of Lb19and Lb20is up to 23. In formula (b1-10), Lb21represents a single bond or a C1-C21 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, Lb22represents a single bond or a C1-C21 divalent saturated hydrocarbon group and Lb23represents a single bond or a C1-C21 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or a carbonyl group, provided that the total carbon atoms of Lb21, Lb22and Lb23is up to 21.

In formula (b1-11), Lb24represents a single bond or a C1-C21 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a fluorine atom, Lb25represents a single bond or a C1-C21 divalent saturated hydrocarbon group, and Lb26represents a single bond or a C1-C20 divalent saturated hydrocarbon group where a hydrogen atom may be replaced by a hydroxyl group or a fluorine atom and where a methylene group may be replaced by an oxygen atom or a carbonyl group, provided that the total carbon atoms of Lb24, Lb25and Lb26is up to 21.

In these formulae, * represents a binding position, * represents a binding position to Y.

In these formulae, the divalent saturated hydrocarbon group includes linear chain alkanediyl groups, branched chain alkanediyl groups, monocyclic or polycyclic divalent saturated hydrocarbon groups, and a group combining two or more of the above-mentioned groups. Specific examples of the divalent saturated hydrocarbon group include those as referred to for Lb1.

Examples of the divalent saturated hydrocarbon group where a methylene group has been replaced by an oxygen atom or a carbonyl group include those having an acyloxy group where a hydrogen atom may be replaced by a hydroxyl group and where a methylene group may be replaced by an oxygen atom or a carbonyl group.

Examples of acyloxy group include an acetyloxy group, a propyonyloxy group, a butyryloxy group, a cyclohexylcarbonyloxy group and an adamantylcarbonyloxy group.

Examples of acyloxy group where a hydrogen atom has been replaced by a hydroxyl group or where a methylene group has been replaced by an oxygen atom or a carbonyl group include an oxoadamantylcarbonyloxy group, a hydroxyadamantylcarbonyloxy group, an oxocyclohexylcarbonyloxy group, and a hydroxycyclohexylcarbonyloxy group.

Examples of the group represented by formula (b1-4) include the following ones.

Examples of the group represented by formula (b1-5) include the following ones.

Examples of the group represented by formula (b1-6) include the following ones.

Examples of the group represented by formula (b1-7) include the following ones.

Examples of the group represented by formula (b1-8) include the following ones.

Examples of the group represented by formula (b1-2) include the following ones.

Examples of the group represented by formula (b1-9) include the following ones.

Examples of the group represented by formula (b1-10) include the following ones.

Examples of the group represented by formula (b1-11) include the following ones.

Preferred examples of the alicyclic hydrocarbon group represented by Y include those represented by the formula (Y1), the formula (Y2), the formula (Y3), the formula (Y4), the formula (Y5), the formula (Y6), the formula (Y7), the formula (Y8), the formula (Y9), the formula (Y10) and the formula (Y11).

When a methylene group has been replaced by an oxygen atom, a sulfonyl group or a carbonyl group in the alicyclic hydrocarbon group represented by Y, preferred examples of Y include those represented by the formula (Y12), the formula (Y13), the formula (Y14), the formula (Y15), the formula (Y16), the formula (Y17), the formula (Y18), the formula (Y19), the formula (Y20), the formula (Y21), the formula (Y22), the formula (Y23), the formula (Y24), the formula (Y25) and the formula (Y26).

Among the groups represented by the formula (Y1) to the formula (Y26), preferred are those represented by formulae (Y1) to (Y19); more preferred are those represented by the formulae (Y11), (Y14), (Y15) and (Y19); and still more preferred are those represented by the formulae (Y11) and (Y14).

Substituents of the alicyclic hydrocarbon groups represented by Y include a halogen atom, an C1-C12 alkyl group, a hydroxyl group, a C1-C12 alkoxy group, a C3-C16 alicyclic hydrocarbon group, a C6-C18 aromatic hydrocarbon group, a C7-C21 aralkyl group, a C2-C4 acyl group, a glycidyloxy group, and —(CH2)j2—O—CO—Rb1— in which Rb1and j2 are defined as above. Each of the alkyl group, the alicyclic hydrocarbon group, the aromatic hydrocarbon group and the aralkyl group, which is the substituent for the alicyclic hydrocarbon groups represented by Y may have a substituent such as an alkyl group, a halogen atom or a hydroxyl group.

Examples of hydroxyl-containing alkyl group include a hydroxymethyl group and a hydroxyethyl group.

Examples of the C1-C12 alkoxy group include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a heptyloxy group, an octyloxy group, a decyloxy group and a dodecyloxy group.

Examples of the aromatic hydrocarbon group include an aryl group such as a phenyl group, a naphthyl group, an anthryl group, a p-methylphenyl group, a p-tert-butylphenyl group, a p-adamantylphenyl group, a tolyl group, a xylyl group, a cumyl group, a mesityl group, a biphenyl group, a phenanthryl group, a 2,6-diethylphenyl group and a 2-methyl-6-ethylphenyl group.

Examples of the aralkyl group include a benzyl group, phenylpropyl group, a phenethyl group, a naphthylmethyl group, or a naphthylethyl group.

Examples of the acyl group include an acetyl group, a propyonyl group and a butyryl group.

Examples of Y include the groups as follow.

where * represents a binding position.

Y represents preferably a C3-C18 alicyclic hydrocarbon group which may have a substituent, more preferably an amadantyl group which may have a substituent, and still more preferably an amadantyl group, a hydroxyamadantyl group or an oxoamadantyl group.

Preferred examples of the sulfonic acid anion of the salt represented by formula (B1) include salts represented by the formulae (B1-A-1) to (B1-A-33), preferably the formulae (B1-A-1) to (B1-A-4), (B1-A-9), (B1-A-10) and (B1-A-24) to (B1-A-33).

In these formulae, the symbols Q1, Q2, L4, Y and Z+are defined as above, Ri2, Ri3, Ri4, Ri5, Ri6and R17each independently represent a C1-C4 alkyl group, preferably a methyl group or an ethyl group, Ri8represents a C1-C12 aliphatic hydrocarbon group [preferably a C1-C4 alkyl group], a C5-C12 monovalent alicyclic hydrocarbon group, or a combined group of them, preferably a methyl group, an ethyl group, a cyclohexyl group or an adamantyl group, and L4represents a single bond or a C1-C4 alkanediyl group.

Specific examples of the sulfonic acid anion of the salt represented by formula (B1) include anions mentioned in JP2010-204646A1.

Among them, preferred examples of the sulfonic acid anion of the salt represented by formula (B1) include anions represented by formulae (B1a-1) to (B1a-15).

Among them, preferred are those represented by formulae (B1a-1) to (B1a-3) and (B1a-7) to (B1a-15).

Examples of the organic counter ion represented by Z+include an onium cation such as a sulfonium cation, an iodonium cation, an ammonium cation, a benzothiazolium cation and a phosphonium cation, and a sulfonium cation and an iodonium cation are preferred, and a sulfonium cation, specifically arylsulfonium cation, is more preferred.

Preferred examples of the organic cation include the organic cations represented by the formulae (b2-1), (b2-2), (b2-3) and (b2-4):

In the formulae (b2-1) to (b2-4), Rb4, Rb5and Rb6independently represent a C1-C30 aliphatic hydrocarbon group, a C3-C36 alicyclic hydrocarbon group and a C6-C36 aromatic hydrocarbon group. The aliphatic hydrocarbon group can have a substituent selected from the group consisting of a hydroxy group, a C1-C12 alkoxy group, a C3-C12 alicyclic hydrocarbon group and a C6-C18 aromatic hydrocarbon group. The alicyclic hydrocarbon group can have a substituent selected from the group consisting of a halogen atom, a C1-C18 aliphatic hydrocarbon group, a C2-C4 acyl group and a glycidyloxy group. The aromatic hydrocarbon group can have a substituent selected from the group consisting of a halogen atom, a hydroxy group, a C1-C18 aliphatic hydrocarbon group and a C1-C12 alkoxy group.

Rb4and Rb5can be bonded to form a ring together with the adjacent S+, and a methylene group in the ring may be replaced by —CO—, —O— or —SO—.

Rb7and Rb8are independently in each occurrence a hydroxy group, a C1-C12 alkyl group or a C1-C12 alkoxy group, m2 and n2 independently represents an integer of 0 to 5.

Rb9and Rb10independently represent a C1-C36 aliphatic hydrocarbon group or a C3-C36 alicyclic hydrocarbon group.

Rb9and Rb10can be bonded to form a ring together with the adjacent S+, and a methylene group in the divalent acyclic hydrocarbon group may be replaced by —CO—, —O— or —SO—.

Rb11represents a hydrogen atom, a C1-C36 aliphatic hydrocarbon group, a C3-C36 alicyclic hydrocarbon group or a C6-C18 aromatic hydrocarbon group.

Rb12represents a C1-C12 aliphatic hydrocarbon group in which a hydrogen atom can be replaced by a C6-C18 aromatic hydrocarbon group, a C3-C18 saturated cyclic hydrocarbon group and a C6-C18 aromatic hydrocarbon group in which a hydrogen atom can be replaced by a C1-C12 alkoxy group or a (C1-C12 alkyl)carbonyloxy group.

Rb11and Rb12can be bonded each other to form a C1-C10 divalent acyclic hydrocarbon group which forms a 2-oxocycloalkyl group together with the adjacent —CHCO—, and a methylene group in the divalent acyclic hydrocarbon group may be replaced by —CO—, —O— or —SO—.

Lb31represents —S— or —O— and o2, p2, s2 and t2 each independently represents an integer of 0 to 5, q2 and r2 each independently represents an integer of 0 to 4, and u2 represents 0 or 1.

Preferred examples of the aliphatic hydrocarbon group represented by Rb4to Rb12include an alkyl group such as a methyl group, an ethyl group, a propyl group, an isopropyl group, 2,2-dimethylethyl group, 1-methylpropyl group, a 2-methylpropyl group, a 1,2-dimethylpropyl group, a 2,2-dimethylpropyl group, a 1-ethylpropyl group, a butyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a 1-methylbutyl group, a 2-methylbutyl group, a 3-methylbutyl group, a hexyl group, a 1-propylbutyl group, a 1-methylpentyl group, a 2-ethylhexyl group, a 1,4-dimethylhexyl group, a 1-methylheptyl group, an octyl group, a decyl group, a dodecyl group, a hexadecyl group, a pentadecyl group, a heptadecyl group and an octadecyl group, and more preferred examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, an octyl group and a 2-ethylhexyl group. The aliphatic hydrocarbon group represented by Rb9, Rb10, Rb11and Rb12has preferably 1 to 12 carbon atoms, more preferably 4 to 12 carbon atoms.

The alicyclic hydrocarbon group may be monocyclic or polycyclic. Preferred examples thereof include a cycloalkyl group such as a cyclopentyl group, a cyclohexyl group, a methylcyclohexyl group, a dimethylcyclohexyl group, a cycloheptyl group and a cyclooctyl group, a group obtained by hydrogenating a condensed aromatic hydrocarbon group such as a hydronaphthyl group, a bridged cyclic hydrocarbon group such as an adamantyl group, a norbornyl group and a decahydronaphtyl group, and the following groups.

Examples of the alicyclic hydrocarbon group in which a hydrogen atom has been replaced by an aliphatic hydrocarbon group include a methylcyclohexyl group, a dimethylcyclohexyl group, a methylnorbornyl group, and an isonorbornyl group.

The alicyclic hydrocarbon group in which a hydrogen atom has been replaced by an aliphatic hydrocarbon group has preferably 20 or less carbon atoms in total.

When the aromatic hydrocarbon group has an alicyclic hydrocarbon group or an aliphatic hydrocarbon group, it is preferred that the alicyclic hydrocarbon group and the aliphatic hydrocarbon group have respectively 1 to 18 carbon atoms and 3 to 18 carbon atoms.

Examples of the aromatic hydrocarbon group in which a hydrogen atom has been replaced by an alkoxy group include p-methoxyphenyl group.

Examples of the aliphatic hydrocarbon group in which a hydrogen atom has been replaced by an aromatic hydrocarbon group include a benzyl group, a phenethyl group, a phenylpropyl group, trityl group, naphthylmethyl group, and a naphthylethyl group.

Examples of the alkoxy group include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a heptyloxy group, an octyloxy group, a decyloxy group and a dodecyloxy group.

Examples of the acyl group include an acetyl group, a propyonyl group and a butyryl group.

The ring group formed by bonding Rb4and Rb5together with the adjacent S+may be monocyclic or polycyclic, saturated or unsaturated, aromatic or nonaromatic group. The ring is generally 3 to 12-membered one, preferably 3 to 7-membered one. Examples of the ring include the following ones.

The ring group formed by bonding Rb9and Rb10together with the adjacent S+may be monocyclic or polycyclic, saturated or unsaturated, aromatic or nonaromatic group. The ring has generally C3-C12, preferably C3-C7 carbon atoms. Examples of the ring include a thiolan-1-ium ring (tetrahydrothiphenium ring), a thian-1-ium ring and a 1,4-oxathian-4-ium ring.

The ring group formed by bonding Rb11and Rb12together with —CH—CO— may be monocyclic or polycyclic, saturated or unsaturated, aromatic or nonaromatic group. The ring has generally C3-C12, preferably C3-C7 carbon atoms. Examples of the ring include an oxocycloheptane ring, an oxocyclohexane ring, an oxonorbornane ring, and an oxoadamantane ring.

Preferred examples of the cation for the acid generator include an arylsulfonium cation, specifically cation of formula (b2-1), and more specifically a phenylsulfonium cation.

The cation of formula (b2-1) is preferably represented by formula (b2-1-1).

wherein Rb19, Rb20and Rb21are independently in each occurrence a halogen atom (preferably a fluorine atom), a hydroxyl group, a C1-C18 aliphatic hydrocarbon group, C3-C18 alicyclic hydrocarbon group or a C1-C12 alkoxy group, and v2, w2 and x2 independently each represent an integer of 0 to 5.

The aliphatic hydrocarbon group has preferably 1 to 12 carbon atoms, and a C1-C12 alkyl group is preferred. The v2, w2 and x2 independently each preferably represent 0 or 1.

Preferably, Rb19, Rb20and Rb21are independently in each occurrence a halogen atom, a hydroxyl group, a C1-C12 alkyl group or a C1-C12 alkoxy group, and v2, w2 and x2 independently each represent an integer of 0 to 5. More preferably, Rb19, Rb20and Rb21are independently in each occurrence a fluorine atom, a hydroxyl group, a C1-C12 alkyl group or a C1-C12 alkoxy group, and v2, w2 and x2 independently each represent 0 or 1.

Specific examples of formula (b2-1-1) include those recited in JP2010-204646A1, specifically a triphenylsulfonium cation which is represented by formula (b1-1-1) where each of v2, W2 and x2 is 0, a diphenyltolylsulfonium cation which is represented by formula (b1-1-1) where v2 and W2 are 0, x2 is 1, and Rb21is a methyl group, and a tritolylsulfonium cation which is represented by formula (b1-1-1) where v2, W2 and x2 are 0, and Rb19, Rb20and Rb21are a methyl group.

Examples of the cation represented by the formula (b2-1) include the followings.

Examples of the cation represented by the formula (b2-2) include the followings.

Examples of the cation represented by the formula (b2-3) include the followings.

Examples of the cation represented by the formula (b2-4) include the followings.

The acid generator may consist of any one of the above-mentioned sulfonic acid anions and any one of the above-mentioned organic cations. The acid generator preferably consists of one anion selected among from those of formulae (B1a-1) to (B1a-3) and (B1a-7) to (B1a-15) and one cation selected from among those of formulae (b1-1-1) and (b2-3).

Specific examples of the acid generator include the following salts represented by formulae (B1-1) to (B1-28). Among them, those which comprise an arylsulfonium cation are preferred, the salts represented by formulae (B1-1), (B1-2), (B1-3), (B1-5), (B1-6), (B1-7), (B1-11), (B1-12), (B1-13), (B1-14), (B1-20), (B1-21), (B1-22), (B1-23), (B1-24), (B1-25) and (B1-26) are more preferred.

The content of the acid generator represented by formula (B1) is preferably 30 parts by mass or more, more preferably 50 parts by mass or more, per 100 parts by mass of the total acid generators. The acid generator for the photoresist composition may consist of the acid generator represented by formula (B1). The total content of the acid generator is preferably 1 part by mass or more, more preferably 3 parts by mass or more, per 100 parts by mass of the resin.

The photoresist composition of the present invention may comprise a solvent.

The amount of the solvent is usually 90% by weight or more, preferably 92% by weight or more preferably 94% by weight or more based on total amount of the photoresist composition of the present invention. The amount of the solvent is usually 99.9% by weight or less and preferably 99% by weight or less based on total amount of the photoresist composition of the present invention. The content can be measured with known methods such as liquid chromatography or gas chromatography.

Examples of the solvent include a glycol ether ester such as ethyl cellosolve acetate, methyl cellosolve acetate and propylene glycol monomethyl ether acetate; a glycol ether such as propylene glycol monomethyl ether; an ester such as ethyl lactate, butyl acetate, amyl acetate and ethyl pyruvate; a ketone such as acetone, methyl isobutyl ketone, 2-heptanone and cyclohexanone; and a cyclic ester such as γ-butyrolactone.

The photoresist compositions of the present invention may further comprise a quencher such as a basic compound. The “quencher” has the property that it can trap an acid, especially an acid generated from the acid generator by applying a radiation.

Examples of the quencher include a basic compound, such as a basic nitrogen-containing organic compound, and a salt which generates an acid having acidity weaker than an acid generated from the acid generators.

Examples of the basic nitrogen-containing organic compound include an amine compound such as an aliphatic amine, an aromatic amine and an ammonium salt. Examples of the aliphatic amine include a primary amine, a secondary amine and a tertiary amine. Examples of the aromatic amine include an aromatic amine.

Herein, the acidity in the salts is shown by the acid dissociation constant (pKa).

The acid dissociation constant of acid generated from the salt for a quencher is usually a salt of −3<pKa.

The salt for a quencher is preferably a salt of −1<pKa<7, and more preferably a salt of 0<pKa<5.

Specific examples of the salt for a quencher include the following ones, the salt of formula (D), and salts recited in US2012/328986A1, US2011/171576A1, US2011/201823A1, JP2011-39502A1, and US2011/200935A1.

The symbols m′ and n′ each independently represent an integer of 0 to 4, preferably an integer of 0 to 2, and more preferably 0.

The hydrocarbon group represented by RD1and RD2includes a C1-C12 alkyl group, a C3-C12 monovalent alicyclic hydrocarbon group, a C6-C12 monovalent aromatic hydrocarbon group, and any combination of them.

Examples of the monovalent hydrocarbon group include alkyl groups such as a methyl group, an ethyl group, n-propyl group, an isopropyl group, n-butyl group, sec-butyl group, tert-butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group. Examples of the alicyclic hydrocarbon group, which may be a monocyclic or polycyclic one, include cycloalkyl groups such as a cyclopropyl group, a cyclobutyl group, a cyclopentyl group, a cyclohexyl group, a cycloheptyl group, a cyclooctyl group, a cycloheptyl group, a cyclodecyl group, and norbonyl group and adamantyl group.

Examples of the aromatic hydrocarbon group include an aryl group such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 2-methylphenyl group, a 3-methylphenyl group, 4-methylphenyl group, a 4-ethylphenyl group, a 4-propylphenyl group, a 4-isopropylphenyl group, a 4-butylphenyl group, a 4-t-butylphenyl group, a 4-hexylphenyl group, a 4-cyclohexylphenyl group, an anthryl group, a p-adamantylphenyl group, a tolyl group, a xylyl group, a cumenyl group, a mesityl group, a biphenyl group, a phenanthryl group, a 2,6-diethylphenyl group and a 2-methyl-6-ethylphenyl group. Examples of the combination include alkyl-cycloalkyl groups, cycloalkyl-alkyl groups, aralkyl groups such as a benzyl group, a 1-phenylethyl group, a 2-phenylethyl group, a 1-phenyl-1-propyl group, a 1-phenyl-2-propyl group, a 2-phenyl-2-propyl group, a 3-phenyl-1-propyl group, a 4-phenyl-1-butyl, a 5-phenyl-1-pentyl group and 6-phenyl-1-hexyl group.

Examples of alkoxy groups include a methoxy group and an ethoxy group.

Examples of acyl groups include an acetyl group, a propanoyl group, a benzoyl group and a cyclohexanecarbonyl group.

Examples of acyloxy group include groups where an oxy group [—O-] is attached to any one of the acyl groups as mentioned above.

Examples of alkoxycarbonyl group include groups where a carbonyl group [—CO-] is attached to any one of the alkoxy groups as mentioned above.

Examples of halogen atoms include fluorine atoms, a chlorine atom, and a bromine atom.

Examples of the compounds of formula (D) include the following ones.

The compound represented by formula (D) can be produced according to the method recited in Tetrahedron Vol. 45, No. 19, p 6281-6296. The compound is available on the market.

The content of quencher is preferably 0.01 to 5% by mass, more preferably 0.01 to 4% by mass, still more preferably 0.01 to 3% by mass, and further more preferably 0.01 to 1% by mass, based on sum of solid component.

The photoresist compositions of the present invention may comprise, if necessary, a small amount of various additives such as a sensitizer, a dissolution inhibitor, other polymers, a surfactant, a stabilizer and a dye as long as the effect of the present invention is not prevented.

The photoresist compositions of the present invention can usually be prepared by mixing, in a solvent, an acid generator and Resin (A), and if necessary a quencher, and/or additives at a suitable ratio for the composition, optionally followed by filtrating the mixture with a filter having 0.003 μm to 0.2 μm of a pore size.

The order of mixing these components is not limited to any specific order. The temperature at mixing the components is usually 10 to 40° C., which can be selected in view of the resin or the like.

The mixing time is usually 0.5 to 24 hours, which can be selected in view of the temperature. The means for mixing the components is not limited to specific one. The components can be mixed by being stirred.

The amounts of the components in the photoresist compositions can be adjusted by selecting the amount to be used for production of them.

The photoresist compositions of the present invention are useful for a chemically amplified photoresist composition.

The photoresist compositions of the present invention are useful for a chemically amplified photoresist composition.

A photoresist pattern can be produced by the following steps (1) to (5):

(1) a step of applying the photoresist composition of the present invention on a substrate,

(2) a step of forming a composition film by conducting drying,

(3) a step of exposing the composition film to radiation,

(4) a step of baking the exposed composition film, and

(5) a step of developing the baked composition film with an alkaline developer.

The applying of the photoresist composition on a substrate is usually conducted using a conventional apparatus such as spin coater. The photoresist composition is preferably filtrated with filter having a pore size of 0.01 to 0.2 μm before applying. Examples of the substrate include a silicon wafer or a quartz wafer on which a sensor, a circuit, a transistor or the like is formed.

The formation of the composition film is usually conducted using a heating apparatus such as hot plate or a decompressor, and the heating temperature is usually 50 to 200° C. When the pressure is reduced during heating, the operation pressure is usually 1 to 1.0*105Pa. The heating time is usually 10 to 180 seconds.

The composition film obtained is exposed to radiation using an exposure system. The exposure is usually conducted through a mask having a pattern corresponding to the desired photoresist pattern. Examples of the exposure source include a light source radiating laser light in a UV-region such as a KrF excimer laser (wavelength: 248 nm), an ArF excimer laser (wavelength: 193 nm) and a F2laser (wavelength: 157 nm), and a light source radiating harmonic laser light in a far UV region or a vacuum UV region by wavelength conversion of laser light from a solid laser light source (such as YAG or semiconductor laser).

The temperature of baking of the exposed composition film is usually 50 to 200° C., and preferably 70 to 150° C.

The development of the baked composition film is usually carried out using a development apparatus. The development method includes dipping methods, paddle methods, spray methods and dynamic dispense method. The developing temperature is preferably 5 to 60° C., and the developing time is preferably 5 to 300 seconds.

The positive and negative type photoresist patterns can be obtained by the development depending on a developer to be used therefor.

When a positive type photoresist pattern is prepared from the photoresist composition of the present invention, the development can be conducted with an alkaline developer. The alkaline developer to be used may be any one of various alkaline aqueous solution used in the art. Generally, an aqueous solution of tetramethylammonium hydroxide or (2-hydroxyethyl)trimethylammonium hydroxide (commonly known as “choline”) is often used. The alkaline developer may comprise a surfactant.

After development, the photoresist film having photoresist pattern is preferably washed with ultrapure water, and the remained water on the photoresist film and the substrate is preferably removed therefrom.

When a negative type photoresist pattern is prepared from the photoresist composition of the present invention, the development can be conducted with a developer containing an organic solvent, such developer is sometimes referred to as “organic developer”.

Examples of an organic solvent for organic developer include ketone solvents such as 2-hexanone, 2-heptanone; glycolether ester solvents such as propyleneglycolmonomethylether acetate; ester solvents such as butyl acetate; glycolether solvents such as propyleneglycolmonomethylether; amide solvents such as N,N-dimethylacetamide; and aromatic hydrocarbon solvents such as anisole.

The content of organic solvent is preferably from 90% to 100% by weight, more preferably from 95% to 100% by weight, in an organic developer. Preferred is that the organic developer essentially consists of an organic solvent.

Among them, the organic developer is preferably a developer comprising butyl acetate and/or 2-heptanone.

The total content of butyl acetate and 2-heptanone is preferably from 50% to 100% by weight, more preferably from 90% to 100% by weight. Preferred is that the organic developer essentially consists of butyl acetate and/or 2-heptanone.

The organic developer may comprise a surfactant or a very small amount of water.

Development with an organic developer can be stopped by replacing the developer by other solvent than it such as alcohol.

The photoresist composition of the present invention is suitable for KrF excimer laser lithography, ArF excimer laser lithography, EUV (extreme ultraviolet) lithography, EUV immersion lithography and EB (electron beam) lithography.

EXAMPLES

The present invention will be described more specifically by Examples, which are not construed to limit the scope of the present invention.

The “%” and “part(s)” used to represent the content of any component and the amount of any material used in the following examples and comparative examples are on a mass basis unless otherwise specifically noted.

The weight-average molecular weight of any material used in the following examples was determined with gel permeation chromatography under the following condition.

Column: Three of TSKgel Multipore HXL-M with guard column, manufactured by TOSOH CORPORATION

Standard reference material: Standard polystyrene (manufactured by TOSOH CORPORATION)

Structures of compounds were determined by mass spectrometry (Liquid Chromatography: 1100 Type, manufactured by AGILENT TECHNOLOGIES LTD., Mass Spectrometry: LC/MSD Type, manufactured by AGILENT TECHNOLOGIES LTD.).

Here, the values at the peaks of the spectrum are referred to as “MASS.”

To a reactor, 10 parts of the compound represented by formula (I-1-a), 40.87 parts of the compound represented by formula (I-1-b) were added and then they were stirred at 140° C. for 10 minutes.

Then the obtained mixture was cooled to 23° C., and 10 parts of tert-butylmethylether were added thereto and stirred at 23° C. for 30 minutes, followed by being filtrated. As a result, 11.30 parts of the compound represented by formula (I-1) were obtained.

To a reactor, 1 part of the compound represented by formula (I-1) and 5 parts of chloroform were added and stirred at 23° C. for 30 minutes, and then 0.63 part of the compound represented by formula (I-2-a) were added thereto and then stirred at 40° C. for 30 minutes, followed by conducting vacuum concentration at 40° C.

To the collected concentrated residues, 2 parts of chloroform and 20 parts of ethyl acetate were fed and stirred at 23° C. for 30 minutes. The obtained mixture was filtrated to obtain 0.55 parts of the compound represented by formula (I-1-2).

To a reactor, 13.04 parts of compounds represented by formula (I-3-a), 15.22 parts of the compound represented by formula (I-3-b) and 200 parts of chloroform were added and stirred at 23° C. for 30 minutes, and 0.61 parts of sulfuric acid were added thereto. Then the mixture was refluxed at 60° C. for 12 hours at the presence of a molecular sieve and then cooled to 23° C. To the obtained reaction mixture, 65 parts of 10% aqueous potassium carbonate solution were added and then stirred at 23° C. for 30 minutes, followed by being separated by being left.

To the collected organic layer, 80 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer. This washing step was conducted four times.

Then the washed one was concentrated and 25 parts of methanol and 25 parts of ion exchanged water were added to the concentrated residue and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 12.93 parts of the compound represented by formula (I-3-c).

To a reactor, 12.93 parts of compounds represented by formula (I-3-c) and 65 parts of acetone were added and then stirred at 0° C. for 30 minutes, and 44 parts of 5% aqueous sodium hydroxide solution were added thereto and then stirred at 23° C. for 18 hours.

To the obtained reaction mixture, 280 parts of 5% aqueous oxalic acid solution and 250 parts of ethyl acetate were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 150 parts of ion exchanged water were added and stirred at 23° C. for 30 minutes, followed by being left for separating into an organic layer: The washing step with water was conducted three times.

Then the washed layer were concentrated, 50 parts of n-heptane were added to the concentrated residue and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 9.54 parts of the compound represented by formula (I-3-d).

To a reactor, 4 part of the compound represented by formula (I-1) and 4 parts of monochlorobenzene were added and stirred at 23° C. for 30 minutes, and then 6.63 part of the compound represented by formula (I-3-d) were added thereto and then stirred at 40° C. for 30 minutes, followed by conducting vacuum concentration at 40° C. To the collected concentrated residues, 2 parts of chloroform and 20 parts of monochlorobenzene were fed and stirred at 23° C. for 30 minutes. The obtained mixture was filtrated and then the obtained filtrates were concentrated. To the collected concentrated residues, 15 parts of methanol were fed and then stirred at 23° C. for 30 minutes, and then filtrated to obtain 3.12 parts of the compound represented by formula (I-3).

To a reactor, 1 part of the compound represented by formula (I-1) and 5 parts of chloroform were added and stirred at 23° C. for 30 minutes, and then 0.58 part of the compound represented by formula (I-4-a) were added thereto and then stirred at 40° C. for 30 minutes, followed by conducting vacuum concentration at 40° C.

To the collected concentrated residues, 2 parts of chloroform and 20 parts of ethyl acetate were fed and stirred at 23° C. for 30 minutes. The obtained mixture was filtrated and then the obtained filtrates were concentrated to obtain 0.44 parts of the compound represented by formula (I-4).

To a reactor, 1 part of the compound represented by formula (I-1) and 5 parts of chloroform were added, and stirred at 23° C. for 30 minutes, and then 0.46 part of the compound represented by formula (I-5-a) were added thereto and then stirred at 40° C. for 30 minutes, followed by conducting vacuum concentration at 40° C.

From the collected concentrated residues, 0.29 parts of the compound represented by formula (I-5) were separated by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/ethyl acetate=1/4].

To a reactor, 9.78 parts of compounds represented by formula (I-6-a), 15.22 parts of the compound represented by formula (I-3-b) and 200 parts of chloroform were added and stirred at 23° C. for 30 minutes, and 0.61 parts of sulfuric acid were added thereto. Then the mixture was refluxed at 60° C. for 8 hours at the presence of a molecular sieve and then cooled to 23° C. To the obtained reaction mixture, 65 parts of 10% aqueous potassium carbonate solution were added and then stirred at 23° C. for 30 minutes, followed by being separated by being left.

To the collected organic layer, 80 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer. This washing step was conducted four times.

Then the washed one was concentrated and 11.43 parts of the compound represented by formula (I-6-c) were separated from the collected concentrated residue by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/methanol=1/4].

To a reactor, 11.02 parts of compounds represented by formula (I-6-c) and 65 parts of acetone were added and then stirred at 0° C. for 30 minutes, and 44 parts of 5% aqueous sodium hydroxide solution were added thereto and then stirred at 23° C. for 18 hours.

To the obtained reaction mixture, 280 parts of 5% aqueous oxalic acid solution and 250 parts of ethyl acetate were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 150 parts of ion exchanged water were added and stirred at 23° C. for 30 minutes, followed by being left for separating into an organic layer: The washing step with water was conducted three times.

Then the washed one was concentrated and 9.32 parts of the compound represented by formula (I-6-d) were separated from the collected concentrated residue by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/ethyl acetate=1/4].

To a reactor, 4 part of the compound represented by formula (I-1) and 4 parts of monochlorobenzene were added and stirred at 23° C. for 30 minutes, and then 5.61 part of the compound represented by formula (I-6-d) were added thereto and then stirred at 40° C. for 30 minutes, followed by conducting vacuum concentration at 40° C. To the collected concentrated residues, 2 parts of chloroform and 20 parts of monochlorobenzene were fed and stirred at 23° C. for 30 minutes. The obtained mixture was filtrated and then the obtained filtrates were concentrated. Then the washed one was concentrated and 2.21 parts of the compound represented by formula (I-6) were separated from the collected concentrated residue by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/methanol=1/1].

Synthesis Example 1

To a reactor, 1 part of the compound represented by formula (I0-4-a) and 1.6 parts of potassium persulfate were added and stirred at 5° C. for 30 minutes, and then 5.89 part of sulfonic acid were added thereto and stirred at 23° C. for 30 minutes.

To the obtained mixture, 0.82 part of the compound represented by formula (I0-4-b) and 4.12 part of chloroform were added and stirred at 23° C. for 2 hours. To the obtained reaction mixture, 10 part of chloroform and 3.4 part of saturated aqueous sodium hydrogen carbonate were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 3.4 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer.

To the separated concentrated residue, 10 parts of ethyl acetate was added and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 0.89 parts of the compound represented by formula (I0-4).

Synthesis Example 2

To a reactor, 5 part of the compound represented by formula (I0-4-a) and 8 parts of potassium persulfate were added and stirred at 5° C. for 30 minutes, and then 29.45 part of sulfonic acid were added thereto and stirred at 23° C. for 30 minutes.

To the obtained mixture, 4.6 part of the compound represented by formula (I0-5-b) and 23 parts of chloroform were added and stirred at 23° C. for 2 hours. To the obtained reaction mixture, 60 parts of chloroform and 20 parts of saturated aqueous sodium hydrogen carbonate were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 20 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer.

To the separated concentrated residue, 30 parts of ethyl acetate were added and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 2.65 parts of the compound represented by formula (I0-5).

Synthesis Example 3

To a reactor, 5 part of the compound represented by formula (I0-4-a) and 8 parts of potassium persulfate were added and stirred at 5° C. for 30 minutes, and then 29.45 part of sulfonic acid were added thereto and stirred at 23° C. for 30 minutes.

To the obtained mixture, 5.49 parts of the compound represented by formula (I0-6-b) and 25 parts of chloroform were added and stirred at 23° C. for 2 hours. To the obtained reaction mixture, 60 parts of chloroform and 20 parts of saturated aqueous sodium hydrogen carbonate solution were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 20 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer.

Then the washed one was concentrated and, 2.72 parts of the compound represented by formula (I0-6) were separated from the collected concentrated residue by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/methanol=1/1].

Synthesis Example 4

To a reactor, 5 part of the compound represented by formula (I0-4-a) and 8 parts of potassium persulfate were added and stirred at 5° C. for 30 minutes, and then 29.45 part of sulfonic acid were added thereto and stirred at 23° C. for 30 minutes.

To the obtained mixture, 5.55 parts of the compound represented by formula (I0-7-b) and 25 parts of chloroform were added and stirred at 23° C. for 2 hours. To the obtained reaction mixture, 60 parts of chloroform and 20 parts of saturated aqueous sodium hydrogen carbonate were added and stirred at 23° C. for 30 minutes, followed by being left for separation. To the separated organic layer, 20 parts of ion exchanged water was added and then stirred at 23° C. for 30 minutes, followed by being separated for collecting an organic layer.

Then the washed one was concentrated and 2.51 parts of the compound represented by formula (I0-7) were separated from the collected concentrated residue by silica gel column chromatography [silica gel 60N, manufactured by KANTO CHEMICAL, Co., Inc.; spherical shape, neutral, 100-210 μm, eluent: chloroform/methanol=1/1].

Synthesis Example 5

To a reactor, 50.49 parts of the salt represented by formula (B1-5-a) and 252.44 parts of chloroform were added and they were stirred at 23° C. for 30 minutes. Then 16.27 parts of the salt represented by formula (B1-5-b) were dropped thereto and then stirred at 23° C. for an hour to obtain a solution containing the salt represented by formula (B1-5-c).

To the obtained solution, 48.8 parts of the salt represented by formula (B1-5-d) and 84.15 parts of ion-exchanged water were added then stirred at 23° C. for 12 hours to obtain a reaction solution with two separated phases. Then chloroform layer was separated therefrom, and 84.15 parts of ion-exchanged water were added thereto for washing: This washing step was conducted 5 times.

To the washed chloroform layer, 3.88 parts of active carbon were added and then they were stirred, followed by conducting filtration. The collected filtrate was concentrated. To the obtained residue, 125.87 parts of acetonitrile was added and stirred, followed by being concentrated.

To the obtained residue, 20.62 parts of acetonitrile and 309.30 parts of tert-butylmethylether were added and stirred at 23° C. for 30 minutes, followed by removing its supernatant therefrom. Then To the residue, 200 parts of n-heptane were added and stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 61.54 parts of the salt represented by formula (B1-5).

Synthesis Example 6

In a reactor, 30.00 parts of the salt represented by formula (B1-21-b) which had been produced according to the method described in JP 2008-209917 A, 35.50 parts of the salt represented by formula (B1-21-a), 100 parts of chloroform and 50 parts of ion-exchanged water were fed and stirred at 23° C. for 15 hours. From the obtained reaction mixture which had two phases, a chloroform phase was collected with separation.

The chloroform phase was washed with 30 parts of ion-exchanged water for washing: This washing was conducted five times.

The washed chloroform phase was concentrated. To the obtained residue, 100 parts of tert-butylmethylether was added and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 48.57 parts of the salt represented by formula (B1-21-c).

Into a reactor, 20.00 parts of the salt represented by formula (B1-21-c), 2.84 parts of the compound represented by formula (B1-21-d) and 250 parts of monochlorobenzene were fed and then they were stirred at 23° C. for 30 minutes.

To the resultant mixture, 0.21 part of copper (II) dibenzoate was added. The resultant mixture was stirred at 100° C. for 1 hour.

The mixture was concentrated, and then 200 parts of chloroform and 50 parts of ion-exchanged water were added to the obtained residue, followed by being stirred at 23° C. for 30 minutes. Then the organic phase was collected by separation. The organic layer was washed with 50 parts of ion-exchanged water and then they were stirred at 23° C. for 30 minutes, followed by collecting an organic phase by separation: This washing was conducted five times.

The washed organic layer was concentrated. To the residue, 53.51 parts of acetonitrile was added, and the resultant mixture was concentrated. To the residue, 113.05 parts of tert-butylmethylether was added and then they were stirred, followed by being filtrated to obtain 10.47 parts of the salt represented by formula (B1-21).

Synthesis Example 7

Into a reactor, 11.26 parts of the salt represented by formula (B1-22-a), 10.00 parts of the compound represented by formula (B1-22-b), 50 parts of chloroform and 25 parts of ion-exchanged water were fed and then they were stirred at 23° C. for 15 hours.

From the obtained reaction mixture which had two phases, a chloroform phase was collected with separation.

The chloroform phase was washed with 15 parts of ion-exchanged water for washing: This washing was conducted five times.

The washed chloroform phase was concentrated. To the obtained residue, 50 parts of tert-butylmethylether was added and then stirred at 23° C. for 30 minutes, followed by being filtrated to obtain 11.75 parts of the salt represented by formula (B1-22-c).

Into a reactor, 11.71 parts of the salt represented by formula (B1-22-c), 1.70 parts of the compound represented by formula (B1-22-d) and 46.84 parts of monochlorobenzene were fed and then they were stirred at 23° C. for 30 minutes.

To the resultant mixture, 0.12 part of copper (II) dibenzoate were added. The resultant mixture was stirred at 100° C. for 30 minutes. The mixture was concentrated, and then 50 parts of chloroform and 12.50 parts of ion-exchanged water were added to the obtained residue, followed by being stirred at 23° C. for 30 minutes. Then the organic phase was collected by separation. The organic layer was washed with 12.50 parts of ion-exchanged water and then they were stirred at 23° C. for 30 minutes, followed by collecting an organic phase by separation: This washing was conducted eight times.

The washed organic layer was concentrated. To the residue, 50 parts of tert-butylmethylether was added, followed by being filtrated to obtain 6.84 parts of the salt represented by formula (B1-22).

Compounds used as monomers in the following Synthesis Examples are shown as follow.

Here, each of the compounds is referred as to “monomer (X)” where “X” is the symbol of the formula representing the monomer.

Synthesis Example 8

There were mixed monomers (a1-1-3), (a1-2-9), (a2-1-3) and (a3-4-2) in a molar ratio of 45/14/2.5/38.5 (monomer (a1-1-3)/monomer (a1-2-9)/monomer (a2-1-3)/monomer (a3-4-2)) as well as propyleneglycolmonomethylether acetate in 1.5 times part based on total parts of all monomers to prepare a mixture. To the mixture, azobisisobutyronitrile as an initiator in the ratio of 1 mol % based on all monomer molar amount and azobis(2,4-dimethylvaleronitrile) as an initiator in the ratio of 3 mol % based on all monomer molar amount were added, and the obtained mixture was heated at 73° C. for about 5 hours. The reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation. The precipitate was collected by filtration.

Then the filtrates were dissolved in propyleneglycolmonomethylether acetate and the resultant solution was poured into a large amount of a mixture of methanol and water to cause precipitation, followed by being filtrated: This operation was conducted twice for purification.

As a result, a resin having a weight-average molecular weight of about 7.6×103was obtained in yield of 68%. This resin is called as Resin A1. Resin A1 had the following structural units.

Synthesis Example 9

There were mixed monomers (a1-1-2), (a2-1-1) and (a3-1-1) in a molar ratio of 50/25/25 [monomer (a1-1-2)/monomer (a2-1-1)/monomer (a3-1-1)] as well as propyleneglycolmonomethylether acetate in 1.5 times part based on total parts of all monomers to prepare a mixture.

To the mixture, azobisisobutyronitrile as an initiator in the ratio of 1 mol % based on all monomer molar amount and azobis(2,4-dimethylvaleronitrile) as an initiator in the ratio of 3 mol % based on all monomer molar amount were added, and the obtained mixture was heated at 75° C. for about 5 hours. The reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation. The precipitate was collected by filtration.

Then the filtrates were dissolved in propyleneglycolmonomethylether acetate and the resultant solution was poured into a large amount of a mixture of methanol and water to cause precipitation, followed by being filtrated: This operation was conducted twice for purification.

As a result, a resin having a weight-average molecular weight of about 9.1×103was obtained in yield of 66%. This resin is called as resin A2. Resin A2 had the following structural units.

Synthesis Example 10

There were mixed monomer (a4-1-7) and 1,4-dioxane in 1.5 times part based on total parts of all monomers to prepare a mixture. To the mixture, azobisisobutyronitrile as an initiator in the ratio of 0.7 mol % based on all monomer molar amount and azobis(2,4-dimethylvaleronitrile) as an initiator in the ratio of 2.1 mol % based on all monomer molar amount were added, and the obtained mixture was heated at 75° C. for about 5 hours.

The reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation. The precipitate was collected by filtration.

Then the reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation. The precipitate was collected by filtration: This operation was conducted twice for purification.

As a result, a resin having a weight-average molecular weight of about 1.8×104was obtained in yield of 77%. This resin is called as resin X1. Resin X1 had the following structural unit.

Synthesis Example 11

There were mixed monomers (a5-1-1) and (a4-0-1) in a molar ratio of 75/25 [monomers (a5-1-1)/monomer (a4-0-1)] as well as methylisobutylketone in 1.2 times part based on total parts of all monomers to prepare a mixture.

To the mixture, azobisisobutyronitrile as an initiator in the ratio of 2 mol % based on all monomer molar amount was added, and the obtained mixture was heated at 70° C. for about 5 hours.

The reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation.

As a result, a resin having a weight-average molecular weight of about 1.7×104was obtained in yield of 87%. This resin is called as resin X2. Resin X2 had the following structural units.

Synthesis Example 12

There were mixed monomers (a5-1-1) and (a4-0-12) in a molar ratio of 50/50 [monomers (a5-1-1)/monomer (a4-0-12)] as well as methylisobutylketone in 1.2 times part based on total parts of all monomers to prepare a mixture.

To the mixture, azobisisobutyronitrile as an initiator in the ratio of 3 mol % based on all monomer molar amount was added, and the obtained mixture was heated at 70° C. for about 5 hours.

The reaction mixture was poured into a large amount of a mixture of methanol and water to cause precipitation.

As a result, a resin having a weight-average molecular weight of about 1.0×104was obtained in yield of 91%. This resin is called as resin X3. Resin X3 had the following structural units.

Examples 7 to 21 and Comparative Example 1

Production of Photoresist Compositions

The following components as listed in Table 1 were mixed and dissolved in the solvent as mentioned below, and then filtrated through a fluorine resin filter having pore diameter of 0.2 μm, to prepare photoresist compositions.

In Table 1, each of symbols represents the following component:

B1-5: Salt represented by formula (B1-5)

B1-21: Salt represented by formula (B1-21)

B1-22: Salt represented by formula (B1-22)

B1-2: Salt represented by formula (B1-2)

I-1: The compound represented by formula (I-1)

I-2: The compound represented by formula (I-2)

I-3: The compound represented by formula (I-3)

I-4: The compound represented by formula (I-4)

I-5: The compound represented by formula (I-5)

I-6: The compound represented by formula (I-6)

I0-4: The compound represented by formula (I0-4)

I0-5: The compound represented by formula (I0-5)

I0-6: The compound represented by formula (I0-6)

I0-7: The compound represented by formula (I0-7)

D1: The compound of the following formula, which was manufactured by Tokyo Chemical Industries, Co., Ltd.

Mixture of the following solvents

Silicon wafers (12 inches) were each coated with “ARC-29”, which is an organic anti-reflective coating composition available from Nissan Chemical Industries, Ltd., and then baked at 205° C. for 60 seconds, to forma 78 nm-thick organic anti-reflective coating. Each of the photoresist compositions prepared as above was spin-coated over the anti-reflective coating so that the thickness of the resulting film became 100 nm after drying. The silicon wafers thus coated with the respective photoresist compositions were each prebaked on a direct hotplate at a temperature shown in the column “PB” in Table 1 for 60 seconds. Using an ArF excimer stepper for immersion exposure (“XT: 1900Gi” manufactured by ASML, NA=1.35, σout=0.9, σin=0.7, X-Y polarization), each wafer thus formed with the respective resist film was subjected to exposure with the exposure quantity being varied stepwise. For the exposure, a photomask for forming a trench pattern, which has 500 nm of its pitch and 64 nm of its trench width, was used. Ultrapure water was used as an immersion medium.

After the exposure, each wafer was subjected to post-exposure baking on a hotplate at a temperature shown in the column “PEB” in Table 1 for 60 seconds and then to development in the manner of dynamic dispense method at 23° C. for 20 seconds with butyl acetate (manufactured by Tokyo Chemical Industries, Co., Ltd) to make a photoresist pattern.

Effective sensitivity (ES): It was expressed as the exposure quantity that the width of the trench pattern became 35 nm after exposure and development.

Focal margin upon exposure from plus-defocal points [DOF+]:

The photoresist patterns were obtained at the exposure amount of ES, with the focal point distance being varied stepwise in the manner that the wafer was moved from its optimal focal position closer to the exposure source.

Each of patterns developed on the organic anti-reflective coating substrate after the development were observed and the focal point distances when the patterns of which trench width were within 35 nm±5% (between 33.25 nm and 36.75 nm) were measured and the difference between the max value of the focal point distance and the minimum value of the focal point distance was calculated. Each of the differences is also shown in parentheses in a column of “DOF+(nm)”. The difference is bigger, the better focus margin the photoresist composition has. The results are listed in Table 2.

The photoresist composition according to the present invention can provide a good photoresist pattern with excellent focal margin upon exposure from plus-defocal points.