Method for the manufacture of planar magnetic heads by making cavities in a non-magnetic wafer

A method of simultaneous manufacture of a plurality of planar magnetic heads on a wafer or a slab made of non-magnetic material designed to be cut out to separate each head. The method can be applied to magnetic heads of the type including a micro-gap formed between two magnetic poles, facing a gap defined between two wire-wound ferrite cores. The method consists in depositing said thin layer magnetic poles on a first face of a wafer made of non-magnetic material and in hollowing out, in the face opposite to said wafer, at least one cavity for housing said wire-wound cores so as to obtain a calibrated spacing or a junction between the upper part of each of said wire-wound cores and said thin layer magnetic poles.

BACKGROUND OF THE INVENTION 
1. Field of the Invention 
The field of the invention is that of the simultaneous manufacture of a 
plurality of magnetic heads on a wafer or slab made of non-magnetic 
material, designed to be cut out to separate each magnetic head. 
Planar magnetic heads are used notably for the writing or reading of 
magnetic tapes of the type used in tape recorders, video tape recorders 
etc. 
2. Description of the Prior Art 
In a first known structure of magnetic heads, a gap 10 is hollowed out in a 
magnetic substrate 11 with winding 12 (FIG. 1) for writing or reading on a 
moving magnetic tape 13. 
In one method for making this type of structure by which it is possible to 
work with magnetic tapes of high coercivity, magnetic layers 14, 15 with 
high magnetization at saturation (MIG heads) are added on to the opposite 
faces of the gap 10. However, this technology has the drawback of being 
complicated to implement, of not being entirely satisfactory from the 
industrial point of view because the plane of deposition of the layers is 
perpendicular to the plane in which the magnetic tracks 13 run. 
Magnetic heads with a plane structure, such as the one shown in FIG. 2, 
were then developed. According to this new known design, thin layers 16, 
17 made of a magnetic material, are added on at the gap 10 in a plane 
parallel to the plane in which the magnetic track 13 moves. The magnetic 
layer forming the thin layers 16, 17 is chosen so as to generate a field 
that is more intense than the field generated by the material of the 
magnetic substrate 13 with high coercivity. This technology corresponds to 
a different operation of the heads, which notably has valuable properties 
at high frequency. An advantageous application concerns rotating heads, 
making it possible to work at high throughput rates (several tens of 
Mbits/s). 
In planar magnetic heads of this type, it is possible to distinguish, 
firstly, the macrogap 18 which has a size, for example, of the order of 
200 to 300 .mu.m and, secondly, the microgap 10. These dimensions are 
given as a non-restrictive illustration. 
The invention concerns a method for making planar heads of this type. 
There is a known method for the batch manufacture of planar heads, as shown 
in FIG. 3. This method uses a typical slab 30 obtained by being cut out 
from a ferrite block with a circular cross-section. On its active face, 
the slab 30 has a plurality of strips 31 made of a non-magnetic material, 
parallel to one another. These non-magnetic strips are located on top of a 
cavity 32. The width 33 of each strip 31 corresponds to the macrogap 18 of 
the planar head shown schematically in FIG. 2. To make the microgaps, a 
thin layer of magnetic material with a high saturation coefficient is 
deposited. Finally "bow-ties" 34, 35 are demarcated in the deposit, in the 
form of thin layers by masking and ion machining operations. The microgaps 
36 are finally demarcated between two wings 34, 35 of the "bow-tie" 
deposits. It is finally possible to cut out the slab 30 along the two 
perpendicular sets 37, 38 of parallel planes, so as to individually 
separate each planar head 39. 
There are several known methods of implementing this method, notably the 
one described in the French patent application No. 2 641 111 filed on 
behalf of the same Applicant. One characteristic of this type of known 
planar head is that it is made of a slab of magnetic material 30. 
An aim of the invention is to provide a method for the fabrication of 
planar heads in a slab of non-magnetic material, such as silicon, or again 
Al.sub.2 O.sub.3 TiC, these being indicated as non-restrictive examples. 
There is a known method of this type, as described in the French patent 
application No. 86 14974. However, the slab of non-magnetic material used 
according to this prior art document has the drawback of forming an 
obstacle, owing to its thickness, to the crossing of the magnetic 
radiation between the upper thin layers and the lower gap cores. The 
invention is aimed at overcoming this drawback. 
SUMMARY OF THE INVENTION 
More precisely, the invention concerns a method for manufacturing magnetic 
heads with planar structure, notably for the encoding and reading of 
magnetic tapes, each of said magnetic heads being of the type having a 
microgap formed between two magnetic poles, facing a gap defined between 
two wire-wound ferrite cores. This method consists in the deposition of 
said magnetic poles made as thin layers on a first face of a wafer of 
non-magnetic material and in the hollowing out, in the opposite face of 
said wafer, of at least one housing cavity for said wire-wound cores, so 
as to obtain a calibrated spacing or a junction between the upper part of 
said wire-wound cores and said thin layer magnetic poles. 
It is possible to distinguish two main embodiments of the invention, 
depending on whether the cavity-making operation is used to hollow out 
housings, in the wafer of non-magnetic material, that are designed to 
receive subsequently attached wire-wound cores, or whether it can be used 
to form cores, in the very mass of the non-magnetic wafer, that are 
designed to be coated with magnetic material and then wire-wound. 
According to the first embodiment, said wire-wound cores are advantageously 
formed at least in pairs, on a common substrate, and are wire-wound before 
being inserted in batches in said housing cavities. 
In this case, the common substrate for forming the wire-wound cores 
consists either of a monoblock counter-piece made of magnetic material, 
such as ferrite, or of least a module made of magnetic material comprising 
at least one pair of cores, each module being inserted, after the 
wire-winding of the cores, between each wafer of non-magnetic material and 
a holding counter-piece also made of a non-magnetic material. 
According to a third variant of this first embodiment, the process of 
forming the cores consists in machining said non-magnetic part so as to 
form pads in said second face, and then in depositing a magnetic material 
on at least one part of the surface of said pads. 
In the second embodiment, advantageously each of the said cavities for 
housing the wire-wound cores is advantageously hollowed out at a microgap 
formed between two magnetic poles in thin layers, and a layer of magnetic 
material is deposited on two symmetrical portions of the flanks of said 
cavity to form said pair of cores associated with said microgap. 
Preferably, said cavities are made by forming cores in said second face of 
the wafer of non-magnetic material, and the windings are formed around 
said cores with flanks coated at least partially with magnetic material. 
According to one characteristic of this second embodiment of the invention, 
the process of deposition of a layer of magnetic material on the two 
symmetrical portions of the flanks of said cavity comprises the following 
steps: 
a resist layer is deposited in the bottom of said cavity; 
said magnetic material is deposited on said symmetrical flank portions of 
the cavity; 
said resist layer is removed; 
the bridge, if any, formed between said symmetrical deposits of magnetic 
material on the two symmetrical flank portions of the cavity, is broken; 
Irrespectively of the embodiment, the invention provides for the 
possibility of partially submerging said thin layer pads with microgap in 
the cavities made in the first face of the wafer of non-magnetic material.

DESCRIPTION OF THE PREFERRED EMBODIMENTS 
The method of the invention has two main modes of implementation, shown 
schematically in FIGS. 4 and 5 respectively. 
According to the first mode of implementation, the substrate 40 made of 
non-magnetic material, preferably of Si or Al.sub.2 O.sub.3 TiC, is 
provided with cavities so that two substantially symmetrical cavities 45, 
46 frame the plane 41 of the microgap 42 made between the two magnetic 
poles in thin layers 43, 44. 
The cavity-making operation is done, for example, by chemical machining of 
the slab 40 made of non-magnetic material If necessary, the two cavities 
45, 46 may form only one big cavity. In this case, this cavity should be 
wide enough to be capable of taking the attached wire-wound cores, of the 
type shown in FIGS. 8, 9, 10 and 11. 
In the second method for making cavities, according to the invention, a 
single cavity 55 is made in the slab 50 of non-magnetic material, 
substantially at the plane 52 of the micro-break 51 hollowed out between 
two magnetic poles in the form of thin layers 53, 54. In this second 
method, the magnetic poles may advantageously be applied directly to the 
flanks 56, 57 of the single cavity 55, as illustrated in FIGS. 14 and 15. 
Advantageously, these cavities are actually made by machining projecting 
pads 58 and 59, having circular, quadrangular or other sections, in the 
second (lower) face of the slab 50 of non-magnetic material. 
The purpose of the cavity-making operation is to minimize the thickness e 
between the bottom of the cavities 45, 46, 55 and the magnetic poles in 
the form of thin layers 43, 44; 53, 54. If necessary, and as illustrated 
further below, it is also possible to cancel this thickness. 
The computation note presented in TABLE 1, accompanying the FIGS. 6 and 7, 
shows that a maximum thickness e of 5 microns is acceptable. 
In the first mode of implementation, shown in FIG. 8, the wafer 40 with 
cavities cooperates with a counter-piece 71 of magnetic material, for 
example ferrite. In this counter-piece 71, pads 72 have been formed, for 
example by machining. These pads play the role of ferrite cores After a 
winding 73 has been wound around each pad, the counter-piece 71 is mounted 
on the second (lower) face of the slab 40, so as to make each wire-wound 
pad 72 penetrate a cavity. 
The counter-piece 71 is fixedly joined by any means to the slab 40, for 
example by bonding by means of a CERAVAC (brand name) or any other type of 
bonder. The bonding zones are, for example, positioned in the bottom 74 of 
the cavities or, again, between the pads 72 of the ferrite counter-piece 
71, depending on whether the supporting plane between the parts 40 and 71 
is at one level or at the other. As an indication, the aperture at the 
base of each of the cavities may be of the order of 200 microns, for a 
length L of the order of 350 to 500 microns for each of the thin layer 
poles. 
In the mode of implementation shown in FIGS. 9 and 10, the counter-piece 90 
is made of a non-magnetic material, for example silicon, glass or Al.sub.2 
O.sub.3 TiC (these examples of materials are given on a non-restrictive 
basis). 
The counter-piece 90 is, for example, machined chemically so as to have 
poles 91, according to a geometry corresponding to that of the cavities of 
the slab 40. The poles are then coated with a deposit of magnetic material 
92, for example Sendust which may or may not be laminated. A prior masking 
or a subsequent abrasion of the zones 93 between each pair of poles makes 
it possible to break the magnetic continuity from one planar head to an 
adjacent one. 
Each of the coated poles 91, 92 is provided with a winding 94 later on. 
As shown in FIG. 10, the counter-piece provided with wire-wound poles with 
magnetic coating is then mounted on the second (lower) face of the slab 
40. Bonding zones 95 may be provided for the fixed joining of the parts 90 
and 40. 
If necessary, only one portion 96 of the poles of the counter-piece 90 may 
be coated with a magnetic material, the remaining portion 97 being left 
bare or coated with non-magnetic material. 
As an indication, the height of the poles 91 may be of the order of 300 to 
350 microns. The Sendust is advantageously deposited on a thickness of 
about 20 to 50 microns. The width of the coated poles is, for example, of 
the order of 250 microns. This corresponds approximately to the width of 
the cavity bottoms of the wafer 40. 
The zones of transition between two adjacent planar heads extends, for 
example, on some millimeters. The heads are separated into individual 
units advantageously by being cut out along the sawing plane 98. 
In the mode of implementation shown in FIG. 11, the ferrite cores 111 are 
twinned in pairs in the form of modules 112. Each module 112 is embedded 
between, firstly, the wafer 40 with cavities and, secondly, a 
counter-piece 113 provided with housings 114 for embedding the lower part 
of the modules 112 of magnetic cores 111. 
The assembly is fixedly joined advantageously by bonding, for example at a 
location 115 for the connection of the modules 112 and the wafer 40 having 
cavities, and/or to the bottom of the embedding housing 114. 
Advantageously, the counter-part 113 made of non-magnetic material is 
provided with additional pads 116, formed in the non-magnetic mass itself 
and designed to get embedded in a specific cavity 117 for fixed joining. 
The bottom of the cavity then forms a bonding zone 118 with the pad 116. 
These pads 116 may be used specifically for the operation for the batch 
manufacture of the planar heads, and may then removed during the operation 
for separating each planar head into an individual unit, for example by 
sawing along the cutting-out plane 119. 
As an indication, the height of the module 112 may be of the order of 200 
to 300 microns. The height Z of the counter-piece of magnetic material is, 
for example, of the order of 500 microns to 2 millimeters. This part may 
be made of silicon, Al.sub.2 O.sub.3 or other materials. 
It will be noted that the intermediate part 100 between the cavities and 
also, as the case may be, either or both of the solid layers 101, 102 
separating the magnetic poles from the core module 112 may be eliminated. 
They are therefore replaced by the surrounding environment, i.e. generally 
air. In this case, the supporting surface of the assembly is formed by the 
planes 103 for connecting the parts 40 and 113, in which channels have 
been made, if necessary, for the winding wires to pass through. 
FIGS. 12 and 13 relate to an advantageous variant of the invention in which 
the thin layer magnetic poles with microgap are submerged in the first 
(upper) face of the wafer of non-magnetic material. 
The submerging of the poles has many advantages, i.e. notably resistance to 
wear, as well as the elimination of the batch machining of the poles at 
the end of the manufacturing process. 
The submerging is advantageously done after the silicon wafer 40 has been 
hollowed out, preferably by chemical machining, with appropriate resin 
masking. The submerging depth is about two to three microns, for example, 
with a length L of the order of 600 microns, for example, for the bow-ties 
121. 
As shown in FIG. 13, the poles are then deposited in the form of successive 
layers of Sendust 131, insulator material 132 such as Al.sub.2 O.sub.3 and 
again Sendust 133. The thickness of the intermediate layer 132, made of 
Al.sub.2 O.sub.3, is of the order of 0.2 microns for example. 
If necessary, a preliminary layer 134 may be deposited before the three 
layers 131, 132, 133. This preliminary layer is advantageously a layer 
that is a barrier to the chemical machining of the substrate of the 
silicon wafer 40 and can be used, for example, in the method of FIGS. 14 
and 15 described further below. 
Before or after the planar heads are separated into individual units, the 
first (upper) face of the silicon slab is then advantageously polished so 
as to have a rounded profile 135 with high resistance to wear. 
It is therefore seen that the submerged structure of the poles has the 
advantage of making it easy to create a rounded feature followed, if 
necessary, by the deposition of a protective layer. For example, if the 
poles of the planar head have a thickness of the order of two microns and 
a length of 200 microns, the radius of curvature that will be adapted to 
the ideal chord will have a maximum value of 20 millimeters. In this way, 
the poles always remain in a state of geometrical continuity with the 
profile of the head, irrespectively of the degree of wear and tear, since 
the head no longer has any specific leading edge. 
The mode of implementation shown in FIGS. 14 and 15 corresponds to the use 
of the cavity structure shown in FIG. 5. 
In this mode of implementation, a single cavity 140 is hollowed out in the 
lower face of the wafer 50 of non-magnetic material. This cavity 140 is, 
for example, made so that it reaches the chemical barrier layer 134 
mentioned with respect to FIG. 13. 
Advantageously, a localized resist layer 141 is deposited in the bottom of 
the cavity 140. This layer 141 is, for example, made of resin, SiO.sub.2, 
Al.sub.2 O.sub.3, Ceravac or other materials. A layer 142, 143 of magnetic 
material is then selectively deposited, in a substantially symmetrical 
way, on the two opposite flanks of the cavity 140. These two deposits 142, 
143 are used to form the cores of each magnetic head, and these cores will 
subsequently be provided with a winding 145, 146 (FIG. 15). 
If necessary, when the step for depositing the layers 142, 143 leads to the 
formation of a connecting bridge 144 of magnetic material, the bridge 144 
is broken and removed by selective attacking of the resist layer 142, and 
then by a mechanical breaking action. 
The magnetic material deposited on the layers 142, 143 is advantageously 
Sendust which may or may not be laminated. 
As shown in FIG. 15, the windings 145, 146 are, for example, made to go 
round the pads 58, 59, the facing flanks of which are coated with Sendust 
layers 142, 143. 
It will be noted that there is almost a junction between the magnetic cores 
142, 143 and the poles 130 in thin layers, separated only by the chemical 
barrier layer 134. 
The fixed joining of the assembly is done, for example, by mounting a 
connecting part 147, made of magnetic material, providing for the magnetic 
junction of the two poles 142, 143, on the second (lower) face of the 
wafer 50 made of non-magnetic material. The fixed joining is done, for 
example, by the bonding, in the connecting zones 148, of the magnetic 
wafer 147 with the pads 58, 58, made in the wafer 50 of non-magnetic 
material. 
Advantageously, the cavity 140 is filled beforehand with an embedding 
material, for example Ceravac. 
As an indication, it may be noted that the thickness of the layers 142, 143 
of magnetic material deposited on the flanks of the cavity 140 may be of 
the order of 20 to 50 microns. A separation distance of the order of three 
to five millimeters may be provided for between each cavity 140. 
TABLE 1 
COMPUTATION OF THE MAXIMUM PERMISSIBLE THICKNESS "e" 
If we assume, in relation with FIGS. 6 and 7, that: 
R.sub.f =equivalent leakage resistance of the thin layer poles 
R.sub.g =equivalent resistance of the microgap 
i.sub.g =equivalent current crossing the microgap 
R.sub.Si =equivalent resistance of the unmachined thickness of Si 
R.sub.N =equivalent resistance of each ferrite core 
g =width of the microgap 
i.sub.t =total current 
w=width of the poles (length of the microgap) 
h=depth of the microgap 
L=length of the thin layer poles 
.theta.=angle of aperture of the microgap 
e=thickness of the slab of Si between each core and the corresponding pole 
S=ferrite/Sendust pole facing area 
we have 
##EQU1## 
whence the efficiency: 
##EQU2## 
which corresponds to: 
##EQU3## 
When: 
##EQU4## 
To obtain .eta. maximum, we must have: 2R.sub.Si &lt;&lt;R.sub.g now R.sub.g 
.apprxeq.g/(w.h) and R.sub.Si =e/S 
with S: facing area of the poles (S=4.10.sup.4 .mu.m.sup.2) if g=0.2 .mu.m, 
h=2 .mu.m, w=20 .mu.m the e&lt;&lt;100 .mu.m, i.e. e.apprxeq.10 .mu.m for 
example. 
When: 
EQU .R.apprxeq.R.sub.g 
then 
##EQU5## 
the condition 6 R.sub.Si &lt;&lt;R.sub.g leads to e&lt;&lt;30 giving e.apprxeq.3 .mu.m 
We have R.sub.g =g/ (wh) =5.10.sup.-3 
##EQU6## 
In splitting up the bow-tie given by the two thin layer poles into two 
parts, in the form of two squares R.sub.1 and R.sub.2, respectively 100 
.mu.m square and 200 .mu.m square, we arrive at R.sub.F =R.sub.1 +R.sub.2 
=4.10.sup.-3 +1.6.10.sup.-3 =5.6.10.sup.-3 
EQU whence R.sub.F =R.sub.g 
We therefore have the case where R.sub.f .apprxeq.R.sub.g and e is of the 
order of some microns. 
A technological compromise of 5 .mu.m is therefore acceptable.