Surface coating for metal matrix composites

A method of fabricating a metal matrix composite (MMC) tool includes coating at least a portion of an interior of a mold assembly with one or more layers of a material coating, where the mold assembly defines at least a portion of an infiltration chamber. Reinforcing materials are deposited into the infiltration chamber, and infiltrated with a binder material. One or more layers of the material coating may then be reacted with the binder material to form an outer shell on selected outer surfaces of the MMC tool.

BACKGROUND

A wide variety of tools are commonly used in the oil and gas industry for forming wellbores, in completing wellbores that have been drilled, and in producing hydrocarbons such as oil and gas from completed wells. Examples of such tools include cutting tools, such as drill bits, reamers, stabilizers, and coring bits; drilling tools, such as rotary steerable devices and mud motors; and other downhole tools, such as window mills, packers, tool joints, and other wear-prone tools. These tools, and several other types of tools outside the realm of the oil and gas industry, are often formed as metal matrix composites (MMCs), and referred to herein as “MMC tools.”

An MMC tool is typically manufactured by placing loose powder reinforcing material into a mold and infiltrating the powder material with a binder material, such as a metallic alloy. The various features of the resulting MMC tool may be provided by shaping the mold cavity and/or by positioning temporary displacement materials within interior portions of the mold cavity. A quantity of the reinforcement material may then be placed within the mold cavity with a quantity of the binder material. The mold is then placed within a furnace and the temperature of the mold is increased to a desired temperature to allow the binder (e.g., metallic alloy) to liquefy and infiltrate the matrix reinforcement material.

MMC tools are generally erosion-resistant and exhibit high impact strength. The outer surfaces of MMC tools are commonly required to operate in extreme conditions. As a result, it may prove advantageous to customize the material properties of the outer surfaces of MMC tools to extend the operating life of a given MMC tool.

DETAILED DESCRIPTION

The present disclosure relates to tool manufacturing and, more particularly, to metal matrix composite tools having a custom coating or surface preparation placed thereon during the infiltration process.

Embodiments described herein result in a customized surface coating or outer shell on metal matrix composite tools, either completely or in select locations, thereby resulting in surface properties that are different than those of bulk metal matrix composite materials. The outer shell is created by coating selected inner surfaces of a mold assembly with a material coating, where the mold assembly is used to fabricate a given metal matrix composite tool. During the manufacturing process, which includes infiltrating reinforcement materials with a binder material to form the given metal matrix composite tool, the binder material may react with the coated material in-situ and thereby result in a metallic, intermetallic, or ceramic outer shell disposed on selected outer surfaces of the given metal matrix composite tool. These outer shells may prove advantageous in altering the surface properties of the given metal matrix composite tool, such as by increasing wear resistance, erosion resistance, abrasion resistance, stiffness (elastic modulus), hardness (i.e., resistance to plastic deformation), yield strength, ultimate tensile strength, fatigue life, lubricity (i.e., reduced friction), hydrophobicity, anti-balling characteristics, and decreasing surface roughness and surface energy.

Embodiments of the present disclosure are applicable to any tool or device formed as a metal matrix composite (MMC). Such tools or devices, referred to herein as “MMC tools,” may or may not be used in the oil and gas industry. For purposes of explanation and description only, the following description is related to MMC tools used in the oil and gas industry, such as drill bits, but it will be appreciated that the principles of the present disclosure are equally applicable to any type of MMC used in any industry or field, such as armor plating, automotive components (e.g., sleeves, cylinder liners, driveshafts, exhaust valves, brake rotors), bicycle frames, brake fins, aerospace components (e.g., landing-gear components, structural tubes, struts, shafts, links, ducts, waveguides, guide vanes, rotor-blade sleeves, ventral fins, actuators, exhaust structures, cases, frames), and turbopump components, without departing from the scope of the disclosure.

Referring toFIG. 1, illustrated is a perspective view of an example MMC tool100that may be fabricated in accordance with the principles of the present disclosure. The MMC tool100is generally depicted inFIG. 1as a fixed-cutter drill bit that may be used in the oil and gas industry to drill wellbores. Accordingly, the MMC tool100will be referred to herein as the “drill bit100,” but, as indicated above, the drill bit100may alternatively be replaced with any type of MMC tool or device used in the oil and gas industry or any other industry, without departing from the scope of the disclosure.

Suitable MMC tools used in the oil and gas industry that may be manufactured in accordance with the present disclosure include, but are not limited to, oilfield drill bits or cutting tools (e.g., fixed-angle drill bits, roller-cone drill bits, coring drill bits, bi-center drill bits, impregnated drill bits, reamers, stabilizers, hole openers, cutters), non-retrievable drilling components, aluminum drill bit bodies associated with casing drilling of wellbores, drill-string stabilizers, cones for roller-cone drill bits, models for forging dies used to fabricate support arms for roller-cone drill bits, arms for fixed reamers, arms for expandable reamers, internal components associated with expandable reamers, sleeves attached to an uphole end of a rotary drill bit, rotary steering tools, logging-while-drilling tools, measurement-while-drilling tools, side-wall coring tools, fishing spears, washover tools, rotors, stators and/or housings for downhole drilling motors, blades and housings for downhole turbines, and other downhole tools having complex configurations and/or asymmetric geometries associated with forming a wellbore.

As illustrated inFIG. 1, the drill bit100may include or otherwise define a plurality of cutter blades102arranged along the circumference of a bit head104. The bit head104is connected to a shank106to form a bit body108. The shank106may be connected to the bit head104by welding, such as using laser arc welding that results in the formation of a weld110around a weld groove112. The shank106may further include or otherwise be connected to a threaded pin114, such as an American Petroleum Institute (API) drill pipe thread.

In the depicted example, the drill bit100includes five cutter blades102, in which multiple recesses or pockets116are formed. Cutting elements118may be fixedly installed within each pocket116. This can be done, for example, by brazing each cutting element118into a corresponding pocket116. As the drill bit100is rotated in use, the cutting elements118engage the rock and underlying earthen materials, to dig, scrape or grind away the material of the formation being penetrated.

During drilling operations, drilling fluid or “mud” is pumped downhole through a drill string (not shown) coupled to the drill bit100at the threaded pin114. The drilling fluid circulates through and out of the drill bit100at one or more nozzles120positioned in nozzle openings122defined in the bit head104. Junk slots124are formed between each adjacent pair of cutter blades102. Cuttings, downhole debris, formation fluids, drilling fluid, etc., may pass through the junk slots124and circulate back to the well surface within an annulus formed between exterior portions of the drill string and the inner wall of the wellbore being drilled.

FIG. 2is a cross-sectional side view of the drill bit100ofFIG. 1. Similar numerals fromFIG. 1that are used inFIG. 2refer to similar components that are not described again. As illustrated, the shank106may be securely attached to a metal blank (or mandrel)202at the weld110and the metal blank202extends into the bit body108. The shank106and the metal blank202are generally cylindrical structures that define corresponding fluid cavities204aand204b, respectively, in fluid communication with each other. The fluid cavity204bof the metal blank202may further extend longitudinally into the bit body108. At least one flow passageway206(one shown) may extend from the fluid cavity204bto exterior portions of the bit body108. The nozzle openings122may be defined at the ends of the flow passageways206at the exterior portions of the bit body108. The pockets116are formed in the bit body108and are shaped or otherwise configured to receive the cutting elements118(FIG. 1). The bit body108may comprise a reinforced composite material208and, according to embodiments described herein, an outer shell210may be disposed on selected outer and/or inner surfaces of the bit body108.

FIG. 3is a cross-sectional side view of a mold assembly300that may be used to form the drill bit100ofFIGS. 1 and 2. While the mold assembly300is shown and discussed as being used to help fabricate the drill bit100, those skilled in the art will readily appreciate that different configurations of the mold assembly300may be used to help fabricate any of the MMC tools mentioned above, without departing from the scope of the disclosure. As illustrated, the mold assembly300may include several components such as a mold302, a gauge ring304, and a funnel306. In some embodiments, the funnel306may be operatively coupled to the mold302via the gauge ring304, such as by corresponding threaded engagements, as illustrated. In other embodiments, the gauge ring304may be omitted from the mold assembly300and the funnel306may instead be operatively coupled directly to the mold302, such as via a corresponding threaded engagement, without departing from the scope of the disclosure.

In some embodiments, as illustrated, the mold assembly300may further include a binder bowl308and a cap310placed above the funnel306. The mold302, the gauge ring304, the funnel306, the binder bowl308, and the cap310may each be made of or otherwise comprise graphite or alumina (Al2O3), for example, or other suitable materials. An infiltration chamber312may be defined or otherwise provided within the mold assembly300. Various techniques may be used to manufacture the mold assembly300and its components including, but not limited to, machining graphite (or alumina) blanks to produce the various components and thereby define the infiltration chamber312to exhibit a negative or reverse profile of desired exterior features of the drill bit100(FIGS. 1 and 2).

In embodiments where the mold assembly300is made of graphite, the graphite may be anisotropic. In such embodiments, the anisotropic graphite may exhibit a minimum flexural strength of about 2 ksi, a minimum compressive strength of about 5 ksi, a minimum density of about 1.6 g/cm3, and a maximum porosity of about 20%.

Materials, such as consolidated sand or graphite, may be positioned within the mold assembly300at desired locations to form various features of the drill bit100(FIGS. 1 and 2). For example, one or more nozzle displacements or legs314(one shown) may be positioned to correspond with desired locations and configurations of the flow passageways206(FIG. 2) and their respective nozzle openings122(FIGS. 1 and 2). One or more junk slot displacements315may also be positioned within the mold assembly300to correspond with the junk slots124(FIG. 1). Moreover, a cylindrically-shaped consolidated central displacement316may be placed on the legs314. The number of legs314extending from the central displacement316will depend upon the desired number of flow passageways and corresponding nozzle openings122in the drill bit100. Further, cutter-pocket displacements (shown as part of mold302inFIG. 3) may be placed in the mold302to form cutter pockets116.

The reinforcing particles described herein may have a diameter ranging from a lower limit of 1 micron, 10 microns, 50 microns, or 100 microns to an upper limit of 1000 microns, 800 microns, 500 microns, 400 microns, or 200 microns, wherein the diameter of the reinforcing particles may range from any lower limit to any upper limit and encompasses any subset therebetween.

The metal blank202may be supported at least partially by the reinforcement materials318within the infiltration chamber312. More particularly, after a sufficient volume of the reinforcement materials318has been added to the mold assembly300, the metal blank202may then be placed within mold assembly300. The metal blank202may include an inside diameter320that is greater than an outside diameter322of the central displacement316, and various fixtures (not expressly shown) may be used to position the metal blank202within the mold assembly300at a desired location. The reinforcement materials318may then be filled to a desired level within the infiltration chamber312.

In some embodiments, the binder material324may be covered with a flux layer (not expressly shown). The amount of binder material324(and optional flux material) added to the infiltration chamber312should be at least enough to infiltrate the reinforcement materials318during the infiltration process. In some instances, some or all of the binder material324may be placed in the binder bowl308, which may be used to distribute the binder material324into the infiltration chamber312via various conduits326that extend therethrough. The cap310(if used) may then be placed over the mold assembly300. The mold assembly300and the materials disposed therein may then be preheated and then placed in a furnace (not shown) at atmospheric conditions. When the furnace temperature reaches the melting point of the binder material324, the binder material324will liquefy and proceed to infiltrate the reinforcement materials318and form the reinforced composite material208(FIG. 2). After a predetermined amount of time allotted for the liquefied binder material324to infiltrate the reinforcement materials318, the mold assembly300may then be removed from the furnace and cooled at a controlled rate. Once cooled, the mold assembly300may be broken away to expose the bit body108and subsequent machining and processing according to well-known techniques may be undertaken to finish the drill bit100(FIG. 1).

According to embodiments of the present disclosure, and with continued reference toFIGS. 1-3, the drill bit100may further comprise a custom surface preparation and/or coating (e.g., the outer shell210ofFIG. 2) deposited on all or a portion of the outer surfaces of the bit body108. To accomplish this, all or a portion of the interior of the mold assembly300may be coated with a material coating328prior to the infiltration process, and thereby providing a coated mold assembly300. The material coating328may be deposited on the inner walls of some or all of the mold302and the gauge ring304(if used), i.e., the walls facing the infiltration chamber312and generally the portions of the mold assembly300where the bit body108is to be formed and where the external bit surfaces will not be machined away during post-processing. The material coating328may also be deposited on the central displacement316, the legs314, and the junk-slot displacements315. The central displacement316, the legs314, the junk-slot displacements315, the reinforcing materials318, the metal blank202, and the binder material324may then be placed in the infiltration chamber312and otherwise prepared for the infiltration process at atmospheric conditions. During the infiltration process, the material coating328may be designed to react in-situ with the binder material324that infiltrates the reinforcing materials318. The result of the in-situ reaction between the material coating328and the binder material324may be the formation of a metallic, intermetallic, or ceramic outer shell210(FIG. 2) on selected outer surfaces of the resulting drill bit100.

The material coating328may comprise one or more layers of materials or material compositions that serve to modify the resulting surface properties of the bit body108following infiltration. For instance, depending on the number of layers and/or the type and number of materials used, the material coating328may alter surface properties of the bit body108such as, but not limited to, wear resistance, erosion resistance, abrasion resistance, stiffness (elastic modulus), hardness (i.e., resistance to plastic deformation), yield strength, ultimate tensile strength, fatigue life, lubricity (i.e., reduced friction), hydrophobicity, anti-balling characteristics, surface roughness, and surface energy. Suitable materials for the material coating328include, but are not limited to, transition metals (e.g., iridium, rhenium, ruthenium, tungsten, molybdenum, hafnium, chromium, manganese, rhodium, iron, cobalt, titanium, niobium, osmium, palladium, platinum, zirconium, nickel, copper, scandium, tantalum, vanadium, yttrium), post-transition metals (e.g., aluminum and tin), semi-metals (e.g., boron and silicon), alkaline-earth metals (e.g., beryllium and magnesium), lanthanides (e.g., lanthanum and ytterbium), non-metals (e.g., carbon, nitrogen, and oxygen), any alloy thereof, and the like.

Using alloys that contain chromium, carbon, molybdenum, manganese, nickel, cobalt, tungsten, niobium, tantalum, vanadium, silicon, copper, and iron for the material coating328may produce a wear-resistant, erosion-resistant, abrasion-resistant, or hard outer shell210on the bit body108during the infiltration process. Using iridium, rhenium, ruthenium, tungsten, molybdenum, beryllium, chromium, rhodium, iron, cobalt, nickel, and alloys thereof for the material coating328may prove advantageous since such metals exhibit a relatively high modulus of elasticity, and may therefore produce a stiff, outer shell210on the bit body108during the infiltration process. For example, alloying nickel with vanadium, chromium, molybdenum, tantalum, tungsten, rhenium, osmium, or iridium increases the elastic modulus of the resulting alloy.

The formation of ceramic materials (e.g., carbides, borides, nitrides, and oxides) in the outer shell210may produce beneficial changes in any of the desired properties mentioned previously. The in-situ formation of carbides, borides, nitrides, and oxides may be achieved by including carbon, boron, nitrogen, and oxygen in the material coating328. In particular, carbides may be formed by using molybdenum, tungsten, chromium, titanium, niobium, vanadium, tantalum, zirconium, hafnium, manganese, iron, nickel, boron, and silicon in the material coating328. Borides may be formed by using titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, iron, cobalt, nickel, and lanthanum in the material coating328. Nitrides may be formed by using boron, silicon, aluminum, iron, nickel, scandium, yttrium, titanium, vanadium, chromium, zirconium, molybdenum, tungsten, tantalum, hafnium, manganese, and niobium in the material coating328. Oxides may be formed by using silicon, aluminum, yttrium, zirconium, and titanium in the material coating328.

In some embodiments, the material coating328may include and may otherwise be reinforced with reinforcing particles, such as the reinforcing particles mentioned above with reference to the reinforcing materials318.

The material coating328may be directly deposited and otherwise placed on the interior of the mold assembly300using any known process. Suitable processes that may be employed include, but are not limited to, physical vapor deposition, chemical vapor deposition, sputtering, pulsed laser deposition, chemical solution deposition, plasma enhanced chemical vapor deposition, cathodic arc deposition, electrohydrodynamic deposition (i.e., electrospray deposition), ion-assisted electron-beam deposition, electrolytic plating, electroless plating, thermal evaporation, spin coating, dipping portions of the mold assembly300in a molten metal bath, and forming and placing foils. In some embodiments, the layer(s) of the material coating328may be formed under a controlled atmosphere such as high vacuum and/or inert atmosphere during the deposition process.

The layer(s) of the material coating328may exhibit a depth or thickness330ranging from about 25 microns to about 2500 microns. As will be appreciated, the thickness330of the material coating328may vary at selected locations on the interior of the mold assembly300, and thereby result in thicker/thinner portions of the outer shell210applied to the outer surface(s) of the bit body108following infiltration. In some embodiments, the thickness330of the material coating328may vary about particular portions of the mold assembly300, and thereby resulting in portions of the outer shell210that have a varying thickness.

As will be appreciated, the overall composition of the material coating328, including the material, the number of layers deposited, and the type of reinforcing particles (if used), may be selected to serve different purposes in modifying the resulting surface properties of the drill bit100(or any MMC tool). In some embodiments, the material coating328may be deposited on the entire interior of the mold assembly300and, as indicated above, the exterior surfaces of one or more of the displacement members (e.g., the central displacement316, the legs314, the junk slot displacements315, etc.), thereby modifying surface properties of all exterior portions of the bit body108, including the backside (interior) of the pockets116and the interior surfaces of the fluid cavity204b, flow passageways206, and nozzle openings122. In other embodiments, however, portions of the interior of the mold assembly300may alternatively be masked to selectively deposit the material coating328at desired locations while excluding the masked locations. In such embodiments, for example, portions of the mold assembly300may be masked to prevent the material coating328from being deposited in the pockets116. This may prove advantageous when using some types of materials for the material coating328since the pockets116must be wettable in order to adequately braze the cutters118into the pockets116.

In yet other embodiments, the material coating328may comprise various materials or material compositions deposited and otherwise included in different (selected) areas of the mold assembly300to serve different purposes. For instance, the material coating328deposited in the pockets116may comprise a particular material composition that is wettable by the braze material used to braze the cutters118into the pockets116. Suitable examples include reactive metals, such as titanium, chromium, vanadium, niobium, zirconium, and hafnium. However, the material coating328deposited around and otherwise outside of the pockets116may comprise a different material composition that may result in a wear-resistant, erosion-resistant, abrasion-resistant, or hard metallic composition. Suitable examples of materials that may result in a wear-resistant, erosion-resistant, abrasion-resistant, or hard metallic composition include, but are not limited to, alloys that contain chromium, carbon, molybdenum, manganese, nickel, cobalt, tungsten, niobium, tantalum, vanadium, silicon, copper, and iron.

As another example, the material coating328deposited around and otherwise outside of the pockets116may comprise a different material composition that may result in a stiffer metallic composition. Suitable examples of materials that may result in a stiffer metallic composition include, but are not limited to, alloys that contain nickel, vanadium, chromium, molybdenum, tantalum, tungsten, rhenium, osmium, and iridium. As yet another example, the material coating328deposited in the junk slots124(e.g., on junk-slot displacements315), the central displacement316, and the legs314may comprise a hydrophobic material composition that will help mitigate bit-balling in the junk slots124during operation. Suitable examples of materials that may result in mitigating bit-balling include ceramic materials, such as the carbides, borides, nitrides, and oxides listed above.

In some embodiments, two or more layers of the material coating328may be applied and/or deposited on the cutter blades102to help erosion resistance and reduce friction. For example, a layer of nickel (or a nickel alloy) may be deposited on the cutter blades102and a layer of aluminum may subsequently be deposited atop the layer nickel, thereby providing a material coating328that results in an intermetallic outer shell210composition of nickel and aluminum following infiltration. Such layering may prove advantageous in encapsulating the aluminum layer between the nickel material and the reinforcing materials318, thereby substantially mitigating oxidation of the aluminum during the infiltration process. Similar benefits may be gained with materials that are volatile (e.g., elements that have low sublimation and boiling points) or active and that are prone to oxidation. Examples of elements that would benefit from a protective layer include titanium, zinc, magnesium, silicon, chromium, manganese, scandium, yttrium, niobium, carbon, nitrogen, boron, oxygen. In such embodiments, the volatile materials may be encapsulated by one or more layers of another material, thereby substantially preventing the volatile material from vaporizing, sublimating, or oxidizing during the infiltration process.

In some embodiments, the material coating328may comprise a three-layer symmetric configuration wherein a protective layer is disposed on both sides (i.e., inner and outer extremities) of the material coating328. In such embodiments, suitable materials used to make the material coating328include a layer of aluminum interposing opposing layers of nickel. More particularly, the material coating328may be formed by depositing a first layer of nickel, followed by a layer of aluminum, which is then followed by a second layer of nickel. As a result, the aluminum material may be encapsulated between the two nickel layers. Additional embodiments may involve the use of other oxidation-resistant metals, such as silver or copper, to protect oxidation-prone metals, such as titanium, magnesium, or zirconium, in the inner layer from oxidizing.

In some embodiments, the material coating328may comprise a two- or three-layer configuration where the inner layer (i.e., the layer that will interact with the binder material324during infiltration) is thicker than the other layers and/or of a composition that prevents significant interaction between the outer shell210(FIG. 2) formed in-situ and the resulting MMC tool100. In such embodiments, the inner layer works to bond the outer shell210to the bit body108(FIGS. 1 and 2) while also preventing significant interaction between the two dissimilar materials. Examples can include a copper inner layer, a nickel outer layer, and an aluminum layer interposing the copper and nickel layers, where the copper layer is about 5 to 20 times thicker than the nickel layer. Other examples include: a copper inner layer, a titanium outer layer, and an aluminum layer interposing the copper and titanium layers; a vanadium inner layer, a nickel outer layer, and an aluminum layer interposing the vanadium and nickel layers; a vanadium inner layer, a titanium outer layer, and an aluminum layer interposing the vanadium and titanium layers; a tungsten inner layer, a nickel outer layer, and an aluminum layer interposing the tungsten and nickel layers; and a tungsten inner layer, a titanium outer layer, and an aluminum layer interposing the tungsten and titanium layers.

Additional examples include a refractory inner layer with at least two outer layers composed of materials that may form an intermetallic or ceramic compound with each other. Suitable refractory-layer materials include transition metals such as tungsten, rhenium, osmium, tantalum, molybdenum, niobium, iridium, ruthenium, hafnium, and alloys thereof. Suitable intermetallic- or ceramic-forming materials include those listed herein and any alloys thereof. Yet other examples include a thick compliant inner layer with at least two outer layers composed of materials that may form an intermetallic or ceramic compound with each other. Suitable compliant-layer materials include transition metals such as copper, palladium, niobium, silver, gold, hafnium, zirconium, and alloys thereof. Again, suitable intermetallic- or ceramic-forming materials include those listed herein and any alloys thereof.

In some embodiments, the material coating328may comprise a three-layer configuration where the material of the center layer comprises a reinforcement material such that the inner and outer layers will encapsulate the reinforcement particles on melting and/or being infiltrated by or diffused into with the infiltrating binder material324. In such embodiments, suitable material configurations include: a nickel inner layer, a nickel outer layer, and a tungsten carbide layer interposing the nickel layers; and a copper inner layer, a nickel outer layer, and a tungsten carbide layer interposing the copper and nickel layers. Additional examples include transition metals as the inner and outer layers and a reinforcing material as the interposed layer. Suitable materials for the inner and outer layers include transition metals, such as copper, palladium, niobium, silver, gold, hafnium, zirconium, tungsten, rhenium, osmium, tantalum, molybdenum, niobium, iridium, ruthenium, hafnium, and alloys thereof. Suitable materials for the interposed reinforcing layer include any of the materials listed herein as suitable for the reinforcement materials328ofFIG. 3.

Referring now toFIG. 4, illustrated is an exemplary drilling system400that may employ one or more principles of the present disclosure. Boreholes may be created by drilling into the earth402using the drilling system400. The drilling system400may be configured to drive a bottom hole assembly (BHA)404positioned or otherwise arranged at the bottom of a drill string406extended into the earth402from a derrick408arranged at the surface410. The derrick408includes a kelly412and a traveling block413used to lower and raise the kelly412and the drill string406.

The BHA404may include a drill bit414operatively coupled to a tool string416which may be moved axially within a drilled wellbore418as attached to the drill string406. The drill bit414may be fabricated and otherwise created in accordance with the principles of the present disclosure and, more particularly, with mesoscale reinforcing structures. During operation, the drill bit414penetrates the earth402and thereby creates the wellbore118. The BHA404provides directional control of the drill bit414as it advances into the earth402. The tool string416can be semi-permanently mounted with various measurement tools (not shown) such as, but not limited to, measurement-while-drilling (MWD) and logging-while-drilling (LWD) tools, that may be configured to take downhole measurements of drilling conditions. In other embodiments, the measurement tools may be self-contained within the tool string416, as shown inFIG. 4.

Fluid or “mud” from a mud tank420may be pumped downhole using a mud pump422powered by an adjacent power source, such as a prime mover or motor424. The mud may be pumped from the mud tank420, through a stand pipe426, which feeds the mud into the drill string406and conveys the same to the drill bit414. The mud exits one or more nozzles arranged in the drill bit414and in the process cools the drill bit414. After exiting the drill bit414, the mud circulates back to the surface410via the annulus defined between the wellbore418and the drill string106, and in the process returns drill cuttings and debris to the surface. The cuttings and mud mixture are passed through a flow line428and are processed such that a cleaned mud is returned down hole through the stand pipe426once again.

Although the drilling system400is shown and described with respect to a rotary drill system inFIG. 4, those skilled in the art will readily appreciate that many types of drilling systems can be employed in carrying out embodiments of the disclosure. For instance, drills and drill rigs used in embodiments of the disclosure may be used onshore (as depicted inFIG. 1) or offshore (not shown). Offshore oil rigs that may be used in accordance with embodiments of the disclosure include, for example, floaters, fixed platforms, gravity-based structures, drill ships, semi-submersible platforms, jack-up drilling rigs, tension-leg platforms, and the like. It will be appreciated that embodiments of the disclosure can be applied to rigs ranging anywhere from small in size and portable, to bulky and permanent.

Further, although described herein with respect to oil drilling, various embodiments of the disclosure may be used in many other applications. For example, disclosed methods can be used in drilling for mineral exploration, environmental investigation, natural gas extraction, underground installation, mining operations, water wells, geothermal wells, and the like. Further, embodiments of the disclosure may be used in weight-on-packers assemblies, in running liner hangers, in running completion strings, etc., without departing from the scope of the disclosure.

A. A method of fabricating a metal matrix composite (MMC) tool that includes coating at least a portion of an interior of a mold assembly with one or more layers of a material coating, the mold assembly defining at least a portion of an infiltration chamber, depositing reinforcing materials into the infiltration chamber, infiltrating the reinforcing materials with a binder material, and reacting at least one of the one or more layers of the material coating with the binder material and thereby forming an outer shell on selected outer surfaces of the MMC tool

B. A drill bit that includes a bit body comprising a reinforced composite material made by infiltrating reinforcement materials with a binder material, a plurality of cutting elements coupled to an exterior of the bit body, and an outer shell disposed on selected outer surfaces of the bit body, the outer shell being made from one or more layers of a material coating deposited on at least a portion of an interior of a mold assembly used to fabricate the drill bit, wherein the outer shell results from at least one of the one or more layers of the material coating reacting with the binder material during infiltration.

C. A drilling assembly that includes a drill string extendable from a drilling platform and into a wellbore, a drill bit attached to an end of the drill string, and a pump fluidly connected to the drill string and configured to circulate a drilling fluid to the drill bit and through the wellbore, wherein the drill bit comprises a bit body comprising a reinforced composite material made by infiltrating reinforcement materials with a binder material, a plurality of cutting elements coupled to an exterior of the bit body, and an outer shell disposed on selected outer surfaces of the bit body, the outer shell being made from one or more layers of a material coating deposited on at least a portion of an interior of a mold assembly used to fabricate the drill bit, wherein the outer shell results from at least one of the one or more layers of the material coating reacting with the binder material during infiltration.

Each of embodiments A, B, and C may have one or more of the following additional elements in any combination: Element 1: wherein the MMC tool is a tool selected from the group consisting of oilfield drill bits or cutting tools, non-retrievable drilling components, aluminum drill bit bodies associated with casing drilling of wellbores, drill-string stabilizers, a cone for roller-cone drill bits, a model for forging dies used to fabricate support arms for roller-cone drill bits, an arm for fixed reamers, an arm for expandable reamers, an internal component associated with expandable reamers, a sleeve attachable to an uphole end of a rotary drill bit, a rotary steering tool, a logging-while-drilling tool, a measurement-while-drilling tool, a side-wall coring tool, a fishing spear, a washover tool, a rotor, a stator and/or housing for downhole drilling motors, blades for downhole turbines, and any combination thereof. Element 2: wherein the one or more layers of the material coating further comprise reinforcing particles selected from the group consisting of a metal, a metal alloy, a superalloy, an intermetallic, a boride, a carbide, a nitride, an oxide, a ceramic, a diamond, and any combination thereof. Element 3: wherein the MMC tool is a drill bit and the mold assembly includes one or more of a mold, a gauge ring, and a funnel, and wherein coating at least the portion of the interior of the mold assembly comprises coating an inner wall of one or more of the mold and the gauge ring with the one or more layers of the material coating. Element 4: wherein the mold assembly includes at least one flow passageway, and wherein coating at least the portion of the interior of the mold assembly further comprises coating an exterior surface of the at least one flow passageway. Element 5: further comprising modifying outer surface material properties of the MMC tool with the one or more layers of the material coating, the outer surface material properties being selected from the group consisting of wear resistance, erosion resistance, abrasion resistance, stiffness, hardness, yield strength, ultimate tensile strength, fatigue life, lubricity, hydrophobicity, anti-balling characteristics, surface roughness, and surface energy. Element 6: wherein the one or more layers of the material coating comprise a material selected from the group consisting of a transition metal, a post-transition metal, a semi-metal, an alkaline-earth metal, a lanthanide, a non-metal, and any alloy thereof. Element 7: wherein reacting at least one of the one or more layers of the material coating with the binder material comprises at least one of alloying with, diffusing into, and inter-diffusing with and thereby forming at least one of an alloy, an intermetallic, and a ceramic in-situ. Element 8: wherein the one or more layers of the material coating includes at least a first layer and a second layer, the method further comprising reacting the first layer with the second layer by at least one of alloying with, diffusing into, and inter-diffusing with and thereby forming at least one of an alloy, an intermetallic, and a ceramic in-situ. Element 9: wherein coating at least the portion of the interior of the mold assembly with the one or more layers of the material coating comprises depositing the one or more layers of the material coating with a process selected from the group consisting of physical vapor deposition, chemical vapor deposition, sputtering, pulsed laser deposition, chemical solution deposition, plasma enhanced chemical vapor deposition, cathodic arc deposition, electrohydrodynamic deposition, ion-assisted electron-beam deposition, electrolytic plating, electroless plating, thermal evaporation, spin coating, dipping the portion of the interior of the mold assembly in a molten metal bath, and forming and placing foils. Element 10: further comprising masking the interior of the mold assembly to selectively deposit the one or more layers of the material coating at desired locations on inner surfaces of the mold assembly. Element 11: further comprising varying a thickness of the one or more layers of the material coating at desired locations on inner surfaces of the mold assembly.

Element 12: wherein the one or more layers of the material coating further comprise reinforcing particles selected from the group consisting of a metal, a metal alloy, a superalloy, an intermetallic, a boride, a carbide, a nitride, an oxide, a ceramic, a diamond, and any combination thereof. Element 13: wherein the mold assembly includes one or more of a mold, a gauge ring, and a funnel, and wherein an inner wall of one or more of the mold and the gauge ring is coated with the one or more layers of the material coating to produce the outer shell. Element 14: wherein the mold assembly further includes at least one flow passageway, and wherein an exterior surface of at least one of the fluid cavity and the at least one flow passageway is coated with the one or more layers of the material coating to produce the outer shell. Element 15: wherein the one or more layers of the material coating modify outer surface material properties of the drill bit selected from the group consisting of wear resistance, erosion resistance, abrasion resistance, stiffness, hardness, yield strength, ultimate tensile strength, fatigue life, lubricity, hydrophobicity, anti-balling characteristics, surface roughness, and surface energy. Element 16: wherein the one or more layers of the material coating comprise a material selected from the group consisting of a transition metal, a post-transition metal, a semi-metal, an alkaline-earth metal, a lanthanide, a non-metal, and any alloy thereof. Element 17: wherein reacting at least one of the one or more layers of the material coating with the binder material comprises at least one of alloying with, diffusing into, and inter-diffusing with and thereby forming at least one of an alloy, an intermetallic, and a ceramic in-situ. Element 18: wherein the one or more layers of the material coating includes at least a first layer and a second layer, the method further comprising reacting the first layer with the second layer by at least one of alloying with, diffusing into, and inter-diffusing with and thereby forming at least one of an alloy, an intermetallic, and a ceramic in-situ. Element 19: wherein the one or more layers of the material coating are deposited on the interior of the mold assembly using a process selected from the group consisting of physical vapor deposition, chemical vapor deposition, sputtering, pulsed laser deposition, chemical solution deposition, plasma enhanced chemical vapor deposition, cathodic arc deposition, electrohydrodynamic deposition, ion-assisted electron-beam deposition, electrolytic plating, electroless plating, thermal evaporation, spin coating, dipping the portion of the interior of the mold assembly in a molten metal bath, and forming and placing foils. Element 20: wherein the interior of the mold assembly is masked to selectively deposit the one or more layers of the material coating at desired locations on inner surfaces of the mold assembly.

Element 21: wherein the one or more layers of the material coating further comprise reinforcing particles selected from the group consisting of a metal, a metal alloy, a superalloy, an intermetallic, a boride, a carbide, a nitride, an oxide, a ceramic, a diamond, and any combination thereof. Element 22: wherein the one or more layers of the material coating comprise a material selected from the group consisting of a transition metal, a post-transition metal, a semi-metal, an alkaline-earth metal, a lanthanide, a non-metal, and any alloy thereof.