Enhancing strength in laser cutting of ceramic components

A ceramic material, such as sapphire, is irradiated using a laser-based process to form a cut. In some implementations, a region of the ceramic material adjacent to the cut may be heated. The region may be removed to form an edge feature. In various implementations, the region of the ceramic material adjacent to the cut may be shielded from an outer portion of a laser beam used in the laser-based process using a shield, such as a polyethylene film. This removal and/or shielding operations may improve the mechanical strength of the ceramic material.

FIELD

The described embodiments relate generally to manufacture of ceramic components, such as sapphire. More particularly, the present embodiments relate to enhancing strength in ceramic components that are cut using a laser-based process.

BACKGROUND

Consumer or non-consumer devices may include components (such as protective coverings, windows, and/or surfaces) formed from ceramic materials. One example of such a ceramic material is corundum. Corundum is a crystalline form of aluminum oxide and is found in various different colors, most of which are generally referred to as sapphire. Sapphire is a hard and strong material with a hardness of 9.0 on the Mohs scale, and, as such, is capable of scratching nearly all other minerals. Because of its hardness and strength, sapphire may be an attractive alternative to other translucent materials like glass or polycarbonate. Sapphire may also be produced in thin sheets and polished to achieve exceptional optical performance.

Compared to other optically clear materials like traditional polycarbonate or other types of plastic, ceramic materials (such as sapphire) may offer improved scratch resistance and strength. However, ceramic materials may be difficult to machine because of their hardness. Embodiments described herein are directed to manufacturing ceramic materials without the drawbacks of some traditional techniques.

SUMMARY

The present disclosure relates to forming a ceramic component using laser cutting. A ceramic material, such as sapphire, may be irradiated using a laser-based process to form a cut. A region of the ceramic material adjacent to the cut may be heated and may be removed to form an edge feature in various implementations. The region of the ceramic material adjacent to the cut may be shielded from an outer portion of a laser beam used in the laser-based process using a shield in some implementations. Such removal and/or shielding may improve the mechanical strength of the ceramic material.

In various embodiments, a method for forming a ceramic component may include irradiating a ceramic material using a laser-based process to form a cut, heating a region of the ceramic material adjacent to the cut, and removing the region of the ceramic material.

In some examples, the operation of irradiating and the operation of heating may occur at different times. In various examples, the operation of heating may heat the region of the ceramic material with an outer portion of a laser beam used in the laser-based process and the outer portion may have an energy insufficient to cut the ceramic material during the operation of irradiating.

In various examples, the operation of irradiating may include irradiating the ceramic material through a first laser-based process using a first laser beam and the operation of removing the region of the ceramic material may include removing the region of the ceramic material through a second laser-based process using a second laser beam. The second laser beam may have a lower power than the first laser beam. The second laser-based process may include a shorter duration pulse than the first laser-based process.

In some examples, the operation of heating the region of the ceramic material may form a defect such as micro-cracks in the ceramic material. The operation of removing the region of the ceramic material may remove the micro-cracks in the ceramic material. The operation of removing the region of the ceramic material may introduce additional micro-cracks in the ceramic material that are smaller than the micro-cracks. The operation of removing the region of the ceramic material may remove a section of the ceramic material having a depth of approximately 15-25 microns.

In some embodiments, a method for forming a ceramic component may include irradiating a ceramic material with a laser beam to form a cut and shielding a region of the ceramic material adjacent to the cut from an outer portion of the laser beam using a shield (such as a plastic film).

In various examples, the method may further include absorbing, with the shield, at least part of the energy of an outer portion of the laser beam to reduce thermal stress within the shielded region. In some examples, the method may further include applying the shield to the ceramic material before irradiating the ceramic material.

In various examples, the method may also include heating the region through the shield to form a defect in the ceramic material and removing the defect using an additional laser beam.

In various embodiments, a ceramic component (such as at least one of sapphire, zirconia, or glass) may include a surface formed by laser cutting the ceramic component and an edge feature (such as at least one of a chamfer, a bezel, a shelf, a curve, or a rounding) formed along the surface by removing a thermally stressed region of the ceramic component.

In some examples, the ceramic component may be formed by shielding a region of the ceramic component with a shield from an outer portion of a laser beam used in the laser cutting.

DETAILED DESCRIPTION

Laser cutting of ceramic materials, such as sapphire, may thermally stress ceramic materials in ways that affect the mechanical strength of the ceramic materials. For example, many laser beams have a Gaussian energy distribution (e.g., high energy concentration at a core of the laser beam that tapers to zero at the outside portions of the laser beam). As a result, the core of the laser beam may have sufficient energy to cut a ceramic material, but outer portions outside of the core of the laser beam may have insufficient energy to cut within the time of the cutting operation. Though these lower energy outer portions of the laser beam may not have sufficient energy to cut the ceramic material, they may still heat and thermally stress regions of the ceramic material adjacent to the cut. This heating may form micro-cracks or other defects in the affected region of the ceramic material. Such defects may reduce the mechanical strength of the ceramic material, such as bending strength. These defects may spread when the ceramic material is stressed (such as micro-cracks that spread or otherwise weak areas in which micro-cracks may form), such as when the ceramic material experiences an impact or shock.

As discussed herein, in accordance with various embodiments, ceramic components (such as sapphire) can be manufactured using a laser cutting process that may reduce or eliminate some issues related to manufacturing ceramic components.

The present disclosure relates to forming a ceramic component using a laser-based process. A ceramic material may be irradiated using a laser-based process to form a cut. In some implementations, a region of the ceramic material adjacent to the cut may be heated and the region may be removed to form an edge feature (such as a chamfer, a bezel, a shelf, a curve, a rounding, and so on). In various implementations, the laser-based process may use a laser beam and the region of the ceramic material adjacent to the cut may be shielded from an outer portion of the laser beam using a shield. The shield may be formed of polyethylene or another plastic and/or any material operable to shield the ceramic material from an outer portion of the laser beam. The shield may shield the ceramic material by absorbing and/or blocking at least part of the outer portion of the laser beam. Such an outer portion may have insufficient energy to cut the ceramic material during the irradiating. This removal and/or shielding may improve the mechanical strength of the ceramic material.

In accordance with various embodiments,FIGS. 1A-Bshow a device having one or more example ceramic components or parts that may be manufactured according to the techniques discussed herein. In this example, the ceramic components may be multiple hard protective sheets formed of sapphire, zirconia, glass, or other ceramic material on the exterior of the device. Such protective sheets may provide outstanding scratch resistance and enhance the mechanical integrity of the device. A protective sheet may also function as an optically transmissive window and provide visibility to underlying components, such as display screens or graphical elements. In a typical implementation, both the optical and mechanical properties of the protective sheets may be important to perception of quality and performance of the device.

As shown inFIG. 1A, the device10includes protective cover sheet11formed from a ceramic component and used as an optically transmissive protective layer. The cover sheet11is typically attached to the device10using an optically transmissive adhesive or other bonding technique. In this example, the cover sheet11is attached using a pressure sensitive adhesive (PSA) film. The cover sheet11may be attached to the face of the display screen20and protect the display screen20from scratches or other physical damage. The display screen20may include a liquid crystal display (LCD), organic light emitting diode (OLED) display, or similar display element. Because the cover sheet11overlays the display screen20, optical clarity, a polished surface finish, material thickness, and physical strength may be useful aspects of the cover sheet's11functionality, alone or in conjunction with other such aspects. The cover sheet11may also be attached to, or be integrated with, a transparent electronic sensor that overlays the display screen20. In some cases, the electronic sensor covers the entire display screen20and is used as the main input device for the user. In some implementations, the cover sheet11may be integrated with a touch sensor configured to detect finger or stylus touches on the surface of the cover sheet11, a force sensor configured to determine a force exerted on the cover sheet11, or other sensors that detect interactions with the cover sheet11.

As shown inFIG. 1A, the front surface of the device10also includes a button sheet12used to protect the surface of the control button22. In this example, the button sheet12is formed from a ceramic component and is used as an optically transmissive protective layer. The button sheet12protects the surface of the control button22and allows visibility of any graphical elements that are printed on the control button22. In some cases, it is not necessary that the button sheet12be optically transmissive. For example, the button sheet12may be opaque and itself printed with a graphical element or symbol. In this case, the button sheet12is a flat sheet, but in other embodiments, the button sheet12may be formed as a contoured or curved surface.

The button sheet12may enhance the mechanical strength of control button22, which is used as an input to the device10. In the present example, the control button22includes a tactile switch which is operated by depressing the control button22. The control button22may also include or be associated with an electronic touch sensor, such as a capacitive touch sensor or biometric sensor. The button sheet12may be attached directly to a housing of the control button22and may, alternatively be attached or integrated with the electronic touch sensor of the control button22. Similarly, a ceramic component can be used as a protective cover for a variety of input mechanisms, including a slide, wheel, key, and the like.

As shown inFIG. 1B, the back surface of the device10is protected by a back sheet13. Similar to the cover sheet11, the back sheet13is also formed from a ceramic component and is used as an optically transmissive protective layer. In this case, the back sheet13provides visibility of graphical elements printed on the back face of the device10. In this case, the back sheet13covers the entire back of the device10, except for the area near the camera lens24. A separate ceramic component may be used to protect the camera lens24. In an alternative embodiment, the back sheet13also covers the camera lens24and a separate ceramic component is not used.

As shown inFIGS. 1A-B, the device10is a portable electronic device. The device10may be any one of a variety of devices utilizing a hard substrate as a covering, window, and/or surface. For example, the device10may be a portable electronic device, such as a mobile phone, portable media player, wearable electronic device, health monitoring device, and/or other portable appliance. Similar types of protective covers may be applied to other electronic devices, including, for example, tablet computers, notebook computers, and various wearable devices. Additionally, the protective covers may be applied to other types of devices including non-electronic devices, such as mechanical watches which utilize an optically transmissive face over the dial. Alternatively, the protective covers may be integrated with any device that includes a hard exterior surface, particularly if the surface includes a display screen, camera, or other optical element.

As discussed above with respect toFIGS. 1A-B, various components (e.g., cover sheet11, button sheet12, and back sheet13) of an electronic device may be formed from ceramic material, which may include various forms of aluminum oxide. Such ceramic materials may undergo a plurality of processes (e.g., laser cutting) in order to form one or more ceramic components used as a protective sheet for electronic device10. Such processes may include various techniques discussed herein that improve the mechanical strength of the ceramic material.

Techniques of forming ceramic components or parts using laser cutting will now be described. While the following examples are provided with respect to an ablation laser cutting process, the systems and techniques may also be applicable to other types of laser-based processes including, for example, laser fusion, laser etching, physical etching, laser scribing, laser stress cracking, and the like.

FIG. 2shows a flow chart of a first example process200for forming a ceramic component. Such a ceramic component may be a component such as the cover sheet11, the button sheet12, and/or the back sheet13ofFIGS. 1A-1B.

At210, a ceramic material may be irradiated using a laser-based process to form a cut. The laser-based process may use a laser beam. In some cases, the irradiation may be performed using an ablation laser cutting process where the laser beam heats a portion of the ceramic material corresponding to the cut until the portion evaporates, sublimates, or is converted to plasma and is thus removed to form the cut.

In a non-limiting example, a laser may be used in an ablation laser cutting process to form the cut. The laser may include one or more of a variety of lasers that are suitable for providing a laser beam capable of forming the cut in the ceramic material, as discussed herein. In some embodiments, the laser cut is performed using a laser that is configured to produce a laser beam at wavelengths centered at approximately 1070 nanometers and pulse durations ranging from 1 to 20 picoseconds. The laser may be configured to produce a laser beam with a power ranging from 10 watts to 100 watts average power. The laser produces multiple laser pulses in order to form the cut by evaporating portions of the ceramic material, sublimating portions of the ceramic material, and/or converting portions of the ceramic material to plasma. The laser may be configured to produce a laser beam ranging from 10 watts to 100 watts average power and may pulse the laser beam one time in order to remove a region adjacent to the cut.

The laser beam may have a Gaussian energy distribution or otherwise does not have a uniform energy distribution. The laser beam may have a core portion of a higher energy and one or more outer portions outside the core with lower energy than the core. The higher energy of the core portion may be sufficient to cut the ceramic material. The lower energy of the one or more outer portions may be insufficient to cut the ceramic material during the irradiating. However, the lower energy of the one or more outer portions may still heat the region of the ceramic material adjacent to the cut. This heating may create a thermally induced stress and may form micro-cracks and/or other defects that may adversely impact the mechanical strength (such as bending strength) of the ceramic material.

At220, the region of the ceramic material adjacent to the cut may be heated and/or a thermal stress therein may be otherwise induced. The region may be heated by the laser-based process. The heating of the region of the ceramic material may form a defect in the ceramic material, such as one or more micro-cracks. In some implementations, the region may be heated at the same time the cut is formed. However, in other implementations, the irradiating to form the cut and the heating may occur at different times. For example, the laser-based process may involve multiple passes of a laser, one or more of which may heat the region. By way of another example, various other processes performed after the irradiating may heat the region of the ceramic material.

At230, an edge feature (such as a chamfer, a bezel, a shelf, a curve, a rounding, and so on) may be formed on the region of the ceramic material adjacent to the cut by removing at least a portion of the region. The removal of the region may remove ceramic material thermally stressed by the heating and thus remove micro-cracks or other defects or fill micro-cracks or other defects caused by the cutting with molten ceramic material. The removal of the region may also change the impact geometry of the region of the ceramic material such that an impact or shock to the ceramic material is less likely to cause present micro-cracks or other defects to spread and/or otherwise improve the mechanical strength of the ceramic material.

In some cases, the removal of the region may be performed using a laser-based process. The laser-based process may be the laser-based process of210and/or may be another laser-based process. For example, the laser-based process of210may be a first laser-based process using a first laser beam and the removal may be performed using a second laser-based process using a second (or additional) laser beam. In some implementations where first and second laser-based processes are used, the second laser beam used in the second laser-based process may have a lower power than a first laser beam used in the first laser-based process. In some implementations, the second laser-based process may include a shorter duration pulse than the first laser-based process.

In other cases, the removal of the region may be performed by a variety of different processes. Such processes may include machining, grinding, lapping, polishing, abrasion, blasting, etching, and/or any other process capable of removing the region.

The removal of ceramic material during the formation of the edge feature may be lower energy, performed for a shorter duration, and/or with any other parameters otherwise less likely to produce a thermal gradient that may thermally stress the ceramic material than the removal of ceramic material during the irradiating to form the cut. For example, if irradiating uses 7-15 pulses of a laser beam at 30-45 watts average power, the formation of the edge feature using the laser beam may use one pulse of the laser beam at 10-25 watts average power. By way of another example, the formation of the edge feature may remove less ceramic material than the irradiating and thus use less energy, such as where the ceramic material is cut through a thickness of 0.3 millimeters and a section of the ceramic material having a depth of approximately 15-25 microns is removed to form the edge feature. The lower energy of the edge feature formation compared to the irradiating may prevent formation of additional micro-cracks during the edge feature formation or introduce additional micro-cracks that are smaller than the micro-cracks formed by the irradiating. By way of still another example, the formation of the edge feature may be performed for a smaller amount of time than the irradiating, thus being less likely to produce a thermal gradient that may thermally stress the ceramic material.

Although the example process200is illustrated and described as including particular operations performed in a particular order, it is understood that this is an example. In various implementations, various orders of the same, similar, and/or different operations may be performed without departing from the scope of the present disclosure. For example, in some implementations, one or more operations discussed with respect toFIG. 3below may be performed without departing from the scope of the present disclosure.

In one example of the process200, a section of ceramic material may be cut from a larger piece of ceramic material by irradiating the ceramic material using a laser beam. The laser beam may be directed around a section of the larger piece of ceramic material to irradiate around a shape of the section of ceramic material (which may be round, square, oval, rectangular, triangular, irregular, and/or any other shape) to form a cut between the section of ceramic material and the larger piece of ceramic material. The section of ceramic material may thus be separated from the larger piece of ceramic material. The laser beam may then be directed around the outside region of the section of ceramic material adjacent to the cut to irradiate the region and form an edge feature by removing at least part of the region.

FIG. 3shows a flow chart of a second example process300for forming a ceramic component. Such a ceramic component may be a component such as the cover sheet11, the button sheet12, and/or the back sheet13ofFIGS. 1A-1B.

At310, a shield may be disposed on a ceramic material. In some cases, the shield may be a polyethylene or other plastic and/or any other material operable to shield the ceramic material from an outer portion of a laser beam. Such an outer portion may have insufficient energy to cut the ceramic material, may have insufficient energy to cut the ceramic material completely or in a desired manner during irradiating, and/or may be shielded for other reasons. Such materials may include a polyester sheet, plastic film, paint (e.g., ink), curable opaque material (polymer spray), or other suitable material. The shield may be optically transparent or translucent, opaque, partially opaque, and so on. The shield may be disposed on the ceramic material using a variety of different processes such as a lamination process, a physical vapor deposition (PVD) process, a printing process, a painting process, or other technique for disposing the shield on the ceramic material.

At320, a ceramic material may be irradiated with a laser beam to form a cut. The ceramic material may be cut using a laser beam as part of an ablation laser cutting operation (and/or another laser-based process such as laser fusion). At330, a region of the ceramic material adjacent to the cut may be shielded during the irradiating using the shield disposed on the ceramic material. This shielding may reduce and/or eliminate the thermal stress of the laser beam on the region of the ceramic material adjacent to the cut.

In some cases, the shield may absorb at least part of the energy of one or more outer portions of the laser beam (such that the shield reduces thermal stress within the shielded region) and/or otherwise block at least part of the energy of such outer portions from the ceramic material. As the shield absorbs or blocks at least part of such outer portions, thermal stress of such portions on the region of the ceramic material adjacent to the cut may be reduced and/or eliminated (though such outer portions of the laser beam may still heat and/or otherwise induce some amount of thermal stresses in the region). The mechanical strength of the ceramic material may thus be improved by the reduction and/or elimination of the thermal stress.

In various cases, the shield may be formed of a material that does not burn or melt from irradiation by the outer portion of the laser beam to which the shield is exposed. This may enable the shield to optimally shield the region of the ceramic material adjacent to the cut and/or prevent molten portions of the shield from adhering to the ceramic material. In other cases, the shield may be sacrificial. As the shield may be removed in such cases, it may not matter if the shield burns or melts.

The shield may also perform various other functions during the irradiating operation. For example, the irradiating operation may scatter molten portions of ceramic material and the shield may protect the surface of the ceramic material on which it is disposed from such scattering molten portions of ceramic material. By way of another example, the shield may prevent scratching of the ceramic material and/or other damage during handling.

In various implementations, the process300may optionally include one or more additional operations, such as340and350. At340, the shield may be removed. The shield may be removed by a variety of different processes, such as peeling the shield from the ceramic material, dissolving the shield using a solvent, and/or any other such removal process.

At350, an edge feature may be formed on the region of the ceramic material adjacent to the cut by removing at least a portion of the region. In some cases, the shield may not totally protect the region of the ceramic material adjacent to the cut from being thermally affected by the laser beam. In such cases, the mechanical strength of the ceramic material may be further improved by forming an edge feature in such regions.

For example, a first laser-based process may be used at320to form the cut and heat the region through the shield to form a defect in the ceramic material and the defect may be removed using a second laser-based process. In other examples, the same laser-based process may both form and remove the defect. In yet other examples, a laser-based process may be used to form the cut and one or more mechanical processes (such as machining, grinding, lapping, polishing, abrasion, blasting, etching, and/or any other process) may be used to remove a region adjacent to the cut.

For example, although340and350are illustrated and described as removing the shield after irradiating the ceramic material and then removing the region of the ceramic material adjacent to the cut, it should be understood that this is an example. In some implementations, the edge feature may be formed before the shield is removed, thus also removing a region of the shield. In other implementations, the shield may not be removed, such as in cases where the shield functions as a surface treatment (such as a scratch resistant coating, an oleophobic coating, a hydrophobic coating, a glare resistant coating, and so on) for the ceramic material.

By way of another example, the process300is illustrated and described as disposing the shield on (and/or otherwise applying the shield to) the ceramic material before irradiating the ceramic material. However, in other implementations, irradiating may be performed iteratively and the shield may be applied partway through the iterative irradiating process.

FIGS. 4A-4Hshow cross-sectional views of a ceramic material401undergoing a process of forming a ceramic component for an electronic device such as the cover sheet11, the button sheet12, and/or the back sheet13ofFIGS. 1A-B. The process may correspond to the first example process200ofFIG. 2.

FIG. 4Aillustrates a ceramic material401, such as sapphire, having a surface402. One or more portions of the ceramic material401, such as the surface402, may be subjected to one or more treatments such as grinding, palling, and polishing for a variety of purposes such as achieving a fine surface finish on the surface402. Additionally, the ceramic material401may undergo various pre-processing procedures prior to a laser cutting operation. In a non-limiting example, the ceramic material401may be sliced from a boule, ground down to a particular thickness, and/or polished to provide a particular surface finish.

FIG. 4Billustrates irradiation of a portion of the surface402using a first laser-based process. The first laser-based process may use a laser beam492produced by a laser491. The ceramic material401is irradiated with the laser beam492to form a cut406, as shown inFIG. 4C.FIGS. 4B and 4Cmay correspond to operations210-220ofFIG. 2.

As illustrated inFIGS. 4B and 4C, the laser beam492produced by the laser491may have a core493and one or more outer portions494outside of the core493. The core493may have a higher energy density than the outer portions494such that the energy of the core493is sufficient to cut the ceramic material401whereas the lower energy of the outer portions494to which one or more regions (corners405, or edges) adjacent to the cut406are subjected is insufficient to cut the ceramic material401during irradiating. For example, the core493may have a power ranging from 10 watts to 100 watts, the outer portions494may have a power below 10 watts, and a power below 10 watts may be insufficient to cut the ceramic material401during irradiating. Though the outer portions494of the laser beam492have insufficient energy to cut the ceramic material401, they may still heat (or otherwise induce thermal stresses in) the side surfaces404or other regions of the ceramic material401adjacent to the cut406, particularly the corners405of the surface402that is irradiated by the laser beam492.

Described another way, the laser beam492may have a non-uniform (e.g., Gaussian) energy distribution such that a first region of the ceramic material401is irradiated with sufficient energy that the first part evaporates, sublimates, or is converted to plasma (or melts or is otherwise cut) whereas a second region of the ceramic material401is irradiated with only enough energy to heat (and/or only partially evaporate, sublimate, convert to plasma, melt, and/or otherwise cut) the second region of the ceramic material401. The first region of the ceramic material401may correspond to the cut406that is subjected to the core493. The second region of the ceramic material401may correspond to the corners405that are subjected to the outer portions494.

FIG. 4Dis a detail view of one of the corners405of the surface402. As illustrated, the heating of the ceramic material401by the outer portions494of the laser beam492may form micro-cracks410or other defects in the ceramic material401.

FIG. 4Eillustrates removal of a region of one of the corners405of the surface402to produce an edge feature407on one of the side surfaces404of the ceramic material401.FIG. 4Fshows the ceramic material401after formation of an edge feature407on the other corner405.FIGS. 4E and 4Fmay correspond to operation230ofFIG. 2.

As shown inFIGS. 4E and 4F, the formation of the edge feature407may be performed using a laser-based process (whether the first laser-based process or another, second laser-based process) that uses the laser beam492. The formation of the edge feature407may remove at least part of the portions of the region of the ceramic material heated by the laser beam492, thus removing at least part of the micro-cracks410and improving the mechanical strength of the ceramic material. The formation of the edge feature407may also cause molten ceramic material401to flow into some of the micro-cracks410, sealing those micro-cracks410and improving the mechanical strength of the ceramic material. The formation of the edge feature407may further change the geometry of the side surfaces404to reduce contact point sharpness, thus reducing the possibility that the side surfaces404will be affected by an impact or shock that will transfer to weaknesses such as present micro-cracks410and improving the mechanical strength of the ceramic material401.

The formation of the edge feature407may be a lower energy and/or shorter duration process than the irradiating to form the cut such that the formation of the edge feature407does not introduce additional micro-cracks410in the ceramic material and/or introduce additional micro-cracks410in the ceramic material that are smaller than the micro-cracks formed by the irradiating. In some cases, this may be accomplished by configuring the laser491to produce the laser beam492differently during formation of the edge feature407than during irradiating. For example, the laser491may produce the laser beam492at 30-45 watts average power for 7-15 pulses during irradiating and at 10-25 watts average power for 1 pulse during formation of the edge feature407. In other cases, this may be accomplished by the formation of the edge feature407removing a smaller amount of the ceramic material401than is removed by the irradiating. For example, the cut406may be formed through 0.3 millimeters of the thickness of the ceramic material401whereas the edge features407may be formed approximately 15-25 microns in depth into the surface402and from the side surfaces404.

Although the edge features407are shown as being formed with a particular geometry, it is understood that this is an example. In various implementations, the edge features407may be formed with a variety of different geometries without departing from the scope of the present disclosure. For example,FIGS. 4Gand H show the edge features407with a shelf geometry with rounded corners and a shelf geometry with sharp corners, respectively.

FIGS. 5A-5Dshow cross-sectional views of a ceramic material501undergoing a process of forming a ceramic component for an electronic device such as the cover sheet11, the button sheet12, and/or the back sheet13ofFIGS. 1A-B. The process may correspond to the second example process300ofFIG. 3.

FIG. 5Aillustrates disposition of a shield502on a surface503of a ceramic material501. By way of example, in some implementations, the shield502may be a polyethylene or other plastic film. However, in other implementations, the shield502may be any material that absorbs, blocks, and/or otherwise shields outer portions of a laser beam (such as those outer portions with energy insufficient to cut the ceramic material501during irradiating) from the ceramic material. The shield502may be disposed on the surface503of the ceramic material501by lamination, PVD, printing, painting, or other disposition process. By way of non-limiting example, the ceramic material501may have a thickness of approximately 0.3 millimeters and the shield may have a thickness of approximately 0.15-0.25 millimeters for a total thickness of approximately 0.45-0.55 millimeters.FIG. 5Amay correspond to operation310ofFIG. 3.

FIG. 5Billustrates irradiating a portion of the shield502and the surface503using a laser beam592produced by a laser591to form a cut506. The laser beam592has a core593with an energy sufficient to cut the ceramic material501and one or more outer portions594outside of the core593with energy insufficient to cut the ceramic material501during irradiating. As shown, the shield502shields or blocks the side surfaces504adjacent to the cut506or other regions from the outer portions594(and/or absorbs at least part of the energy of the outer portions594and/or otherwise protects the side surfaces504from the outer portions594), preventing or reducing thermal stress of the outer portions594on the side surfaces504of the ceramic material501and thus reducing or eliminating formation of micro-cracks or other defects. As a result, the mechanical strength of the ceramic material501is improved over a cut made without the shield502.FIG. 5Bmay correspond to operations320and330ofFIG. 3.

As shown, the material of the shield502may not burn or melt from irradiation by the outer portions594of the laser beam592. This may allow the shield502to shield the ceramic material501during the entire irradiating process as opposed to burning away or melting and exposing portions of the side surfaces504of the ceramic material501partway through. This may also prevent molten portions of the shield502from adhering to the ceramic material501.

AlthoughFIGS. 5A-5Billustrate the laser beam592cutting the shield502as well as the ceramic material501, it is understood that this is an example. In various implementations, the shield502may be configured with one or more gaps that correspond to the core593. As such, the portions of the shield502around the gap shield the ceramic material501from the outer portions594but the shield502is not irradiated by the core593and is not cut during cutting of the ceramic material. Various procedures are possible and contemplated.

FIG. 5Cillustrates optional removal of the shield502from the ceramic material501that may be performed in some implementations.FIG. 5Cmay correspond to the optional operation340ofFIG. 3.

FIG. 5Dillustrates optional removal of a region of one of the corners (edges) of the surface503by laser ablating using the laser beam592produced by the laser591to produce an edge feature507on one of the side surfaces504of the ceramic material501. In some cases, the shield502may not completely shield the side surfaces504from the laser beam592and the side surfaces504may still be heated and/or thermal stresses may be otherwise induced therein that may form one or more defects. By forming the edge feature507, damage caused to the ceramic material501by the irradiating may be partially or fully mitigated and the mechanical strength of the ceramic material may be further improved.FIG. 5Dmay correspond to operation350ofFIG. 3.

Although a particular process is illustrated and described with respect toFIGS. 5A-5D, it is understood that this is an example. In various implementations, various combinations of the same, similar, and/or different operations may be performed in a variety of orders without departing from the scope of the present disclosure. For example, in some implementations, the edge feature507may be formed prior to removal of the shield502and/or removal of the shield502may be omitted.

By way of another example, althoughFIG. 5Dillustrates removal of the region using the laser beam592, it should be understood that this is an example. In various implementations, such removal may be performed using one or more mechanical processes, such as machining, grinding, lapping, polishing, abrasion, blasting, etching, and/or any other process capable of removing the region.

As described above and illustrated in the accompanying figures, the present disclosure relates to forming a ceramic component using laser cutting. A ceramic material may be irradiated using a laser-based process to form a cut. In some implementations, a region of the ceramic material adjacent to the cut may be heated and the region may be removed to form an edge feature (such as a chamfer, a bezel, a shelf, a curve, a rounding, and so on). In various implementations, the laser-based process may use a laser beam and the region of the ceramic material adjacent to the cut may be shielded from an outer portion of the laser beam using a shield (which may be formed of polyethylene or another plastic and/or any material operable to shield the ceramic material from an outer portion of the laser beam, such as by absorbing and/or blocking at least part of the outer portion of the laser beam, with insufficient energy to cut the ceramic material during irradiating). This removal and/or shielding may improve the mechanical strength of the ceramic material.