Quantum dot LED

A quantum dot LED includes a first bracket, an LED chip fixed on the first bracket and connected to the first bracket, and a first inorganic barrier layer located on an upper side of the first bracket, wherein the first inorganic barrier layer encapsulates the LED chip on the first bracket. Wherein a groove is formed on the first inorganic barrier layer, a lens disposed above the first inorganic barrier layer and the first inorganic barrier layer enclose the groove into a closed space, and a silica gel body is disposed within the closed space, and multiple quantum dots are dispersed in the silica gel body. The lens and the inorganic barrier layer form a closed space, and the silica gel body is placed therein to perform water-oxygen isolation of the quantum dots. Meanwhile, the lens can scatter the light and ensure the light-emitting effect of the LED.

FIELD OF THE INVENTION

The present invention relates to an LED lighting technology field, and more particularly to a quantum dot LED.

BACKGROUND OF THE INVENTION

Due to the narrow emission peak of the quantum dot LED, the emission wavelength can depend on the size conditions so that the quantum dot LED is widely used in backlight products. However, due to the exposure of quantum dots to a water-oxygen environment, the fluorescence efficiency is irreversibly and rapidly decreased. The encapsulation of the quantum dots requires a good isolation of water and oxygen. The current quantum dot film is composed of PET with a barrier film. To make the quantum dot film have stable optical properties and service life, the oxygen barrier capability of the barrier film needs to be less than 10-1 cc/m{circumflex over ( )}2·day, and the water permeability needs to be less than 10-1 g/m{circumflex over ( )}2·day. In addition, because the quantum dots are sensitive to temperature and when the temperature is increased, the wavelength of the quantum dots will produce a red shift, and the luminous efficiency will also decrease.

As shown inFIG. 1, the conventional LED adopts a metal bracket11and a plastic bracket12. The LED chip13is fixed on the metal bracket11and is connected with the metal bracket11through a gold wire14. The phosphor and the silica gel15are encapsulated on the metal bracket11and the plastic bracket12with a packaging glue16. Since the oxygen permeability and the water permeability of the plastic bracket12and the packaging glue16do not meet the requirements of the working environment of the quantum dot, the thermal conductivity coefficient of the plastic bracket12and the packaging glue16are lower, resulting in the increase of the quantum dot temperature and the luminous efficiency of the quantum dots is decreased with increasing temperature.

With reference toFIG. 2, the higher the temperature, the worse the water vapor transmission rate (WVTR) of the material, and the operating temperature of the LED is higher, thus raising a higher demand for the barrier property of the material. In order to achieve better barrier properties, it is necessary to adopt a thin film encapsulation to prepare a dense inorganic barrier layer to isolate water and oxygen. Due to the unevenness of the surface of the LED bracket, the use of sputter coating or PECVD may cause uneven thickness and cracking of the film due to unevenness of the surface of the bracket. Therefore, an atomic layer deposition (ALD) is currently used to realize the inorganic barrier layer. When using the ALD to deposit Al2O3, ZrO2, TiO2, generally H2O or O3are injected. H2O or O3will destroy the quantum dot at the high temperature (the process temperature is about 80° C.). In addition, the refractive index of Al2O3, ZrO2, TiO2is higher (comparing to silica gel for packaging), the light extraction efficiency will be reduced.

SUMMARY OF THE INVENTION

In order to solve the above technology problem, the present invention provides with a quantum dot LED.

The quantum dot LED includes a first bracket; an LED chip fixed on the first bracket and connected to the first bracket; a first inorganic barrier layer located on an upper side of the first bracket, wherein the first inorganic barrier layer encapsulates the LED chip on the first bracket; wherein a groove is formed on the first inorganic barrier layer; wherein a lens disposed above the first inorganic barrier layer and the first inorganic barrier layer enclose the groove into a closed space; and wherein a silica gel body is disposed within the closed space, and multiple quantum dots are dispersed in the silica gel body.

Wherein a second inorganic barrier layer above the lens is provided to encapsulate the lens.

Wherein an organic layer for refracting light is provided on the second inorganic barrier layer.

Wherein the quantum dot LED further includes a second bracket, and the second bracket is disposed around the LED chip and above the first bracket, and the second bracket is encapsulated on the first bracket by the first inorganic barrier layer.

Wherein the first inorganic barrier layer and the second inorganic barrier layer are manufactured by an atomic layer deposition, a thickness of the second inorganic barrier layer is 20 nm to 200 nm.

Wherein the second inorganic barrier layer is a single-layer structure, and a composition material of the single-layer structure includes any one of alumina, zirconia and titanium dioxide.

Wherein the second inorganic barrier layer is a multi-layer structure having multiple layers, and a material of each layer includes any one of alumina, zirconia and titanium dioxide.

Wherein materials of adjacent layers of the second inorganic barrier layer are different.

Wherein the multiple quantum dots includes a red quantum dot and a green quantum dot.

Wherein the multiple quantum dots includes a green quantum dot, and a red fluorescent material is further disposed in the silica gel body.

The present invention has the following beneficial effects:

The lens and the inorganic barrier layer form a closed space, and the silica gel body is placed therein to perform water-oxygen isolation of the quantum dots in the silica gel body. At the same time, the lens can scatter the light and ensure the light-emitting effect of the LED.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

In the present invention, a lens and an inorganic barrier layer are used together to form a closed space, and a silica gel body containing quantum dots is disposed in the closed space. The closed space provides a water-oxygen-isolated environment for the quantum dots in the silica gel body. At the same time, utilizing the lens to scatter the light in order to ensure luminous efficiency. The specific implementation of the system will be further described below with reference to the accompanying drawings and embodiments.

An embodiment of a quantum dot LED provided by the present invention will be described in detail below.

In an embodiment of the present invention, as shown inFIG. 3, a quantum dot LED provided by an embodiment of the present invention includes a first bracket311, an LED chip32fixed on the first bracket311and connected to the first bracket311, a first inorganic barrier layer33located on an upper side of the first bracket311, wherein the first inorganic barrier layer33encapsulates the LED chip32on the first bracket311. A groove34is formed on the first inorganic barrier layer33. A lens35disposed above the first inorganic barrier layer33and the first inorganic barrier layer33enclose the groove34into a closed space; a silica gel body36is disposed within the closed space, and multiple quantum dots37are dispersed in the silica gel body36.

In the embodiment of the present invention, the “first” in the first bracket does not represent the sequence, and is only used to distinguish the brackets. Here, the first bracket is made of a metal material and is divided into two parts by a middle plastic material, and an intermediate plastic plate312is used for insulating, a portion of the first bracket is connected to an anode of the LED chip32, and another portion of the first bracket is connected to a cathode of the LED chip32. Of course, the first bracket here may also adopt a ceramic bracket or a polymer material without using the intermediate plastic plate312.

A second bracket313may be selectively disposed around the LED chip32and above the first bracket311. The second bracket313is made of a plastic material, generally an EMC (Epoxy Molding Compound) is used, and the purpose of the second bracket313is to prevent a light emitted from the LED chip32to irradiate to a side surface. Here, the second bracket313is used for reflecting the lateral light, so that the direction of light irradiation is more concentrated and the efficiency is higher. The second bracket313is encapsulated on the first bracket311by the first inorganic barrier layer33

The “first” in the first inorganic barrier layer does not represent the sequence, and is used only for identifying the inorganic barrier layer, and distinguishes the second inorganic barrier layer; the purpose of forming the groove on the first inorganic barrier layer is to place the silica gel body, The silica gel body is heated and cured by a silica gel, and the mixed quantum dots in the silica gel are also cured together in the silica gel body.

The purpose of disposing the lens35is to scatter the light to achieve a better light transmission effect, but the lens35is limited by the material, and the effect of isolating water and oxygen is not particularly good. For the purpose of isolating water and oxygen, the present invention provides with a second inorganic barrier layer38above the lens35to encapsulate the lens35. A thickness of the second inorganic barrier layer is 20 nm to 200 nm. If the thickness is too thin, the effect of isolating water and oxygen is not good, and if the thickness is too thick, a refractive index of the light is too high.

In order to reduce a refractive index of light, an organic layer39for refracting light is optionally provided in the second inorganic barrier layer38. The above disposition is an integrated design for balancing water oxygen penetration and light transmission.

For the inorganic barrier layer, using a sputter coating or PECVD will generate a problem that the thickness of the film is uneven and the film layer is easily cracked due to the unevenness of the surface. Therefore, the first inorganic barrier layer and the second inorganic barrier layer are manufactured by an atomic layer deposition.

The second inorganic barrier layer38can be a single-layer structure or a multi-layered structure. When the second inorganic barrier layer38is a single-layer structure, a composition material of the above single-layer structure includes any one of alumina, zirconia and titanium dioxide; when the second inorganic barrier layer38is a multi-layer structure, each layer includes any one of alumina, zirconia and titanium dioxide. In order to achieve a better isolation of the water and oxygen, the multi-layer structure of the second inorganic barrier layer38can use different materials in different layers.

According to the light emitting characteristics of quantum dots, the quantum dots include red quantum dots and green quantum dots. Although the luminous efficiency of the quantum dots is high, most of the materials used in quantum dots are heavy metals, which seriously pollute the environment. In order to reduce environmental pollution, red fluorescent materials are generally used to replace the red quantum dots to emit light, so only green quantum dots are used, and red fluorescent materials are further disposed in the silica gel. Red fluorescent materials and green quantum dots are used to ensure the emission efficiency without polluting the environment.

Persons of ordinary skill in the art may understand that all or part of the processes in implementing the methods of the foregoing embodiments may be performed by a computer program to instruct the relevant hardware, and the program may be stored in a computer-readable storage medium. When executing, the flow of the embodiment of each method may be included. The storage medium may be a disk, an optical disk, a Read-Only Memory (ROM) or a Random Access Memory (RAM), etc.

The following content combines with the drawings and the embodiment for describing the present invention in detail. It is obvious that the following embodiments are only some embodiments of the present invention. For the person of ordinary skill in the art without creative effort, the other embodiments obtained thereby are still covered by the present invention.