Process for the preparation of a homogeneous thermoplastic polymer

The invention relates to a process for the preparation of a thermoplastic polymer on the basis of an alkenyl aromatic monomer, an unsaturated dicarboxylic anhydride, and, optionally, a rubber, characterized in that the monomers and/or solution thereof are/is reacted in at least two reaction zones that are in open connection with each other at the top and at the bottom, the reaction mixture being circulated through the reaction zones by means of a mixing device and/or a conveying device. Using the process, a homogeneous product of constant composition is obtained.

BACKGROUND OF THE INVENTION 
This invention relates to a process for the preparation of a thermoplastic 
polymer on the basis of an alkenyl aromatic monomer, an unsaturated 
dicarboxylic anhydride and, optionally, a rubber. 
Copolymers from alkenyl aromatic monomers and unsaturated dicarboxylic 
anhydrides are known. An example of these copolymers are the copolymers 
from styrene and maleic anhydride (SMA). Preparation of these copolymers 
may take place both by batch processes and by continuous processes. The 
first commercial SMA copolymers were low-molecular products with molecular 
weights below 5000. These types were applied in, for instance, floor 
shampoos, floor waxes, emulsion paints and dispersing agents. 
Besides these low-molecular products, the high-molecular SMA copolymers are 
of importance in, for instance, the automotive industry and in domestic 
articles. 
Copolymers of styrene and/or .alpha.-methylstyrene and maleic anhydride are 
generally prepared by customary methods for, for instance, mass 
polymerization or solution polymerization. Thus, for instance, according 
to U.S. Pat. No. 2,971,939 copolymers of styrene and maleic anhydride can 
be obtained by reacting both monomers, styrene and maleic anhydride, in 
the presence of a peroxide. Better polymerization control is achieved by 
application of a solvent, for instance methyl ethyl ketone, acetone, 
xylene, dioxane, ethylbenzene, dimethylformamide or toluene. 
A 50:50 (molar) copolymer can be obtained by discontinuous copolymerization 
of styrene and maleic anhydride, for instance by precipitation 
polymerization of styrene and maleic anhydride in aromatic solvents. 
Copolymers with a lower maleic anhydride content can be obtained if in 
continuous copolymerization a mixture of much styrene and little maleic 
anhydride is introduced into a polymerization vessel with vigorous 
stirring and at a high temperature, while an identical amount of the 
polymerization mixture is simultaneously removed from the vessel (A. W. 
Hanson and R. L. Zimmermann, Industrial Engineering Chemistry 49, p. 1803, 
1957). 
High-molecular SMA polymers can be processed by extrusion and injection 
moulding. The theoretical upper limit of the MA content is 50 mole % 
(alternating copolymers), but as high-molecular copolymers these products 
cannot be processed on account of the high softening point (220.degree. 
C.). In addition, the brittleness and water sensitivity increase with the 
MA content. 
Copolymers with a lower MA content and a higher molar mass, on the other 
hand, can be processed much easier. Of great importance in this context is 
the small dispersion in MA incorporation, which imposes high demands on 
the homogenity of the reaction mixture. As is evident from U.S. Pat. No. 
4,141,934, there already is a large number of publications relating to 
processes aimed at mixing of styrene and maleic anhydride, without any of 
these describing a process by which polymers can be prepared without 
inhomogeneity. 
On pages 4 and 5 of European OPI patent application No. 27274, it is stated 
that the process disclosed in U.S. Pat. No. 4,141,934 does not give the 
desired result, either, yielding heterogeneous reaction products. 
The processes described cannot be used to effect complete polymerization in 
a one-tank reactor and attain the desired conversion of more than 80% 
while retaining product homogeneity. To achieve the desired result, a 
second reactor with metering equipment is used. 
During copolymerization of aromatic monomers and unsaturated dicarboxylic 
anhydrides in mass or in the presence of a solvent, the viscosity of the 
reaction mixture to be polymerized rises to values that are higher as the 
degree of conversion is higher, making it even more difficult to obtain a 
homogeneous mixture. 
The object of the invention is to obtain a process for the preparation of a 
thermoplastic polymer on the basis of an alkenyl aromatic monomer, an 
unsaturated dicarboxylic anhydride and, optionally, a rubber, that does 
not exhibit the above disadvantages. 
SUMMARY OF THE INVENTION 
The process according to the invention is characterized in that the monomer 
and/or solution thereof are/is reacted in at least two reaction zones that 
are in open connection with each other at the top and at the bottom, the 
reaction mixture being circulated through the reaction zones by means of a 
mixing device and/or conveying device. 
It is preferred to use a vessel with a substantially cylindrical wall, 
provided with a coaxial guide tube, which is on both ends connected with 
the vessel, and rotating shaft, which are provided with one or more mixing 
devices, and a conveying device consisting of one or more screw ribbons, 
which are so fastened between the inner wall of the vessel and the outer 
wall of the guide tube as to allow of rotation. 
Using the process according to the invention, a homogeneous product of 
constant composition is obtained. 
The homogeneity of the product is determined from the width of the glass 
transition range (Tg range). Glass transition ranges of less than 
9.degree. C. are considered narrow transition ranges, indicating that the 
copolymer in question is of homogeneous composition. Less homogeneous 
copolymers have glass transition ranges of more than 9.degree. C. 
By application of the process according to the invention, therefore, a 
copolymer with a small dispersion in unsaturated dicarboxylic anhydride 
incorporation is obtained, leading to a narrow Tg range. 
The process according to the invention does not impose any restrictions on 
the conversion in the tank reactor, so that the entire polymerization 
process can be carried out in one step. 
As alkenyl aromatic monomers, in the process according to the invention use 
can be made of styrene, .alpha.-methylstyrene, paravinyl toluene and 
halogen-substituted styrenes. 
Apart from maleic anhydride, as unsaturated dicarboxylic anhydrides in the 
process according to the invention use can be made of chloromaleic 
anhydride, dichloromaleic anhydride, citraconic anhydride, itaconic 
anhydride, phenylmaleic anhydride, aconitic anhydride, and mixtures of 
these. 
As termonomer the styrene-maleic anhydride copolymer may contain 0-30 wt. % 
acrylonitrile, methacrylonitrile or an acrylate such as methylmethacrylate 
or ethylacrylate. Preferably, the terpolymer contains at least 5 wt. % 
acrylonitrile. 
Suitable rubbers are ethylene-propylene copolymers, ethylenepropylene 
copolymers in which other polyunsaturated monomers have been 
copolymerized, polybutadiene, styrene-butadiene rubber, 
butadieneacrylonitrile rubber, polychloroprene, acrylate rubber, 
chlorinated polyethylene rubber, polyisoprene and cycloolefin rubbers. 
Polymerization is preferably effected in mass or in the presence of a 
non-reactive solvent for the monomer, polymer and, optionally, the rubber. 
As solvent, methyl ethyl ketone is preferably chosen. Other solvents that 
may be chosen are acetone, toluene, xylene, dioxane, ethyl benzene or 
dimethylformamide. Polymerization can be effected in the presence of 1-80 
wt. % solvent, by preference in the presence of 10-50 wt. % solvent. 
Examples of the initiators that may be used are benzoyl peroxide, 
2,4-dichlorobenzoyl peroxide, di-tert-butyl peroxide, tert-butyl 
peroxybenzoate, dicumyl peroxide, cumene hydroperoxide, diisopropylbenzene 
hydroperoxide, diisopropyl peroxydicarbonate, tert-butyl perisobutyrate, 
tert-butyl peroxyisopropylcarbonate, tert-butyl peroxypivalate, methyl 
ethyl ketone peroxide, stearoyl peroxide, tert-butyl hydroperoxide, 
lauroyl peroxide, azo-bis-isobutyronitrile or mixtures thereof. 
The total amount of initiator required can be added simultaneously with the 
monomer feed. By using a mixture of these initiators with different 
activation temperatures or different half-life periods, or by supplying 
one and the same initiator, or different initiators, at several places, 
optimum conversion can be achieved and the product properties can be 
varied. The introduction of initiator at several places may promote good 
temperature control, especially when high-activity initiators are used. 
Polymerization may also be effected at elevated temperature in the absence 
of an initiator. 
As is customary in the polymerization of vinyl monomers, here, too, a chain 
length regulator can be added. Use can be made of the compounds 
customarily applied to this purpose. Examples are n-butyl mercaptane, 
tertiary amyl mercaptane, n-octyl mercaptane. Chain length regulators 
having a somewhat lower activity may also be used, for instance diethylene 
glycol, triethylene glycol, 2,2,4-trimethyl pentanediol, 1,5,diethylene 
glycol monobutylether and high-boiling aliphatic alcohols. These compounds 
in addition have a viscosity-reducing effect. 
To the polymerization mixture the customary additives, such as stabilizers, 
antioxidants, lubricants, fillers, pigments, etc., may be added. 
The polymerization temperature generally is between 50.degree. and 
200.degree. C. A temperature between 80.degree. and 150.degree. C. is 
preferred. 
The pressure in the reactor generally is between 2 and 100 bar, depending, 
inter alia, on mixer type, circulation rate, temperature and viscosity of 
the reaction mass. By preference the pressure is between 5 and 50 bar. If 
relatively volatile monomers or other additives are used, a pressure 
between 10 and 75 bar can be applied. 
In the process according to the invention both the circulation time and the 
mixing time, which are both influenced by the speed of the screw ribbon 
and that of the mixing device, are of major importance. 
The circulation time, defined as the time it takes a volume element to 
circulate through the entire reactor along a flow path, is between 0.1 and 
30 seconds, preferably between 1 and 10 seconds. 
The mixing time is between 0.1 and 300 seconds, preferably between 1 and 70 
seconds. 
The mixing time is defined as the time needed for equalization of the 
concentration of a fed substance to such an extent that the concentration 
at any place deviates by less than 5% from the calculated final value. 
The mixing time preferably is 10 times the circulation time or shorter. 
The copolymers prepared according to the invention have a weight average 
molecular weight of between 30,000 and 500,000, and preferably between 
75,000 and 300,000. 
The weight average molecular weight (Mw) can be determined via a method 
described in Journal of Applied Polymer Science, Vol. 20, 1619-1626 
(1976). By determination of the intrinsic viscosity at 25.0.degree. C. in 
tetrahydrofuran a method has been developed for determining, by a 
one-point determination, the weight-average molecular weight (Mw). For MA 
contents of 5-50 mole % and an Mw range of 2.times.10.sup.4 to 
7.times.10.sup.6, the following holds: 
[n]=3.98 . 10.sup.-4 . Mw.sup.0.596 
where: 
[n]=intrinsic viscosity 
Mw=weight-average molecular weight. 
The styrene maleic anhydride copolymers prepared according to the invention 
have a maleic anhydride content of between 15 and 35 wt. % and a styrene 
content of between 65 and 85 wt. %. By preference, a copolymer with a 
maleic anhydride content of between 20 and 30 wt. % and a styrene content 
of between 70 and 80 wt. % is prepared. 
For further processing of the solution, it is useful to maximize 
conversion. After removal of the solvent, this yields a highly 
concentrated solution, the solids content of which corresponds with the 
conversion, which can be extruded without prior evaporation. 
The equipment used in the invention has a conveying device consisting of 
one or more screw ribbons, which are so installed between the inner wall 
of the vessel and the outer wall of the guide tube that they can be made 
to rotate around the vessel axis. The degree to which a conveying device 
consisting of such a screw ribbon is affected by the viscosity of the 
medium is low, so that its efficiency as regards pumping action is better 
than that of other conveying devices and/or pumps. The flow through the 
guide tube that is created by the screw ribbon operating as pump can now 
bring about very rapid equalization of the concentration when use is made 
of rapidly rotating stirring devices, such as propellors, while the 
residence time of the medium in the vessel can be shortened very 
substantially. 
If use is made of various propellors, placed at a distance from one 
another, the feeding device for each of the components to be mixed can now 
be installed before a stirring device, viewed in the direction of flow. 
Thus, various components can fully separately be mixed with the 
circulating medium by a stirring device. 
According to Dutch Patent Specification No. 158393, such equipment would 
have the disadvantage that during polymerization the low-viscosity monomer 
that is continuously supplied through the connection for the main stream 
is not instantaneously mixed uniformly with the high-viscosity reaction 
mixture. As a result, the monomer forms a layer, separate from the 
reaction mixture near the reactor inlet, which is not constant but changes 
from time to time, and which at one moment occupies about 20% of the 
volume of the reaction vessel, while the next moment it has disappeared 
altogether. Such an unstable monomer layer renders it very difficult to 
control the temperature in the reaction mixture and gives rise to 
fluctuations in the quality of the polymers prepared.

DESCRIPTION OF PREFERRED EMBODIMENTS 
A reactor vessel is made up of a substantially cylindrical shell, 
consisting of two detachable halfs 1' and 1", that are connected, for 
instance, by means of flanges 2' and 2". In the vessel there is a coaxial 
partition wall 3, which does not continue to the end faces of the vessel 
and which forms guide tube 4. For support purposes, the wall of this tube 
is one side attached rigidly to shell 1', and this side is provided with 
openings 5 that are large enough to admit a liquid flow without offering 
much resistance. Within guide tube 4, stirrers 6, 6', etc. are provided, 
for instance propellor mixers with two blades. Thus, the guide tube in 
fact forms a mixing chamber. The propellors are rigidly fastened to a 
rotating shaft 7, which is extended through a stuffing box 8 to outside 
the vessel, where this shaft can be driven. Each propellor brings about 
extremely good micromixing within a small distance from the mixing tube, 
provided speed and propellor are suitably chosen so that the product of 
revolutions per second times (diameter in meters).sup.2 is at least 0.05 
m.sup.2 per second. The components to be mixed can now be introduced 
separately into the reactor, for instance such that each component is 
separately mixed into the main stream before a propellor, seen in the 
direction of flow. The polymerization referred to can effectively be 
brought about in this vessel by using a feed tube for suitably 
distributing a second component and raw materials, dispersing agent, and 
the like between these two streams, or feeding these separately. To this 
end, feed tubes 9, 9', etc., are provided, which can be used to feed a 
component to propellor 6, 6', etc., respectively. The supply and discharge 
of the main stream can take place via connections 10 and 10'. 
Between the wall of vessel section 1' and the wall of mixing tube 4, screw 
ribbons 11 and 11' are installed. These screw ribbons are attached to a 
fork 12, which can make the ribbons rotate around the vessel axis by means 
of rotating shaft 13, at the end of which fork 12 is rigidly attached. 
This shaft is also extended through a stuffing box, 14, to outside the 
vessel, where it can be driven. If use is made of two ribbons, the screw 
ribbon dimension are preferably such that, at a customary ribbon pitch of 
at most 0.75 times the vessel diameter, the blade width of a ribbon equals 
0.2 times the vessel diameter, while the product of speed and circulation 
time is at most 20, both calculated over the same unit of time. It follows 
that there are no limitations on the actual vessel size if the advantages 
as described above are to be obtained, provided the above-mentioned 
conditions are satisfied. Through their pumping action, the screw ribbons 
effect rapid circulation of the liquid through the mixing chamber, as is 
indicated by arrows in the drawing. 
For completeness' sake it is pointed out that such equipment is described 
in Dutch patent application laid open to public inspection No. 6516783. 
Moulding compounds prepared according to the invention are suitable for 
many applications. A wide variety of objects can be prepared from them, 
such as tubes, bottles, furniture, car dashboards, cabinets and housings 
for electronic and domestic appliances, shoe heels, caravans, skis and 
surf boards. 
The invention will be elucidated on the basis of the following examples and 
comparative experiments, without being restricted thereto. 
EXAMPLE 1 
A reactor as described with reference to the figure, with a reactor volume 
of 0.004 m.sup.3, is continuously charged with a feed consisting of 42 wt. 
% styrene, 13 wt. % maleic anhydride (MA), 0.2 wt. % benzoyl peroxide 
(BPO) and 44.8 wt. % methyl ethyl ketone (MEK). 
The reaction temperature is 110.degree. C., the residence time 4 hours. 
The propellor mixers in the guide tube have a speed of 2500 rpm, the ribbon 
mixer operates at 25 rpm. The solution leaving the reactor is collected in 
acetone and coagulated in methanol. The polymer is subsequently dried in a 
drying stove and then analyzed. 
Under the stirring conditions in this test, the circulation time of the 
solution is 7 seconds and the mixing time 42 seconds. The results 
presented in Table 1 show that a homogeneous product is obtained, the 
glass transition range being 6.degree. C. 
EXAMPLE 2 
In this example the ribbon mixer speed is 110 rpm, all other conditions 
being the same as in Example 1. The circulation time is 2.2 seconds and 
the mixing time 13 seconds. The copolymer obtained is of homgeneous 
composition. 
COMATIVE EXAMPLE A 
The propellor mixer is taken out of the reactor. The ribbon mixer speed is 
100 rpm. All other conditions are as in Example 1. 
The circulation time is 6.6 seconds and the mixing time is undefined, but 
more than 70 seconds. 
A copolymer having a deterogeneous composition is obtained. 
EXAMPLE 3 
A reactor as described with reference to the figure, with a reactor volume 
of 0.004 m.sup.3, is continuously charged with a feed consisting of 58.56 
wt. % styrene, 10.30 wt. % MA, 31.00 wt. % MEK and 0.14 wt. % BPO. 
The reaction temperaure is 110.degree. C., the residence time 2 hours. The 
propellor mixer and the ribbon mixer operate at a speed of 2000 and 23 
rpm, respectively. 
The circulation time is 8.6 seconds, as is the mixing time. 
The copolymer obtained has a homogeneous composition. 
COMATIVE EXAMPLE B 
This experiment was carried out in the same way as Example 3. The propellor 
mixer speed is 2000 rpm, the ribbon mixer speed 6 rpm. 
The circulation time and the mixing time both are 34.0 seconds. 
A copolymer of heterogeneous composition is obtained. 
EXAMPLE 4 
A reactor as described with reference to the figure, with a reactor volume 
of 0.004 m.sup.3, is continuously charged with a feed consisting of 42.2 
wt. % styrene, 14.8 wt. % maleic anhydride (MA), 42.8 wt. % methyl ethyl 
ketone (MEK) and 0.2 wt. % benzoyl peroxide (BPO). The reaction 
temperature is 130.degree. C., the residence time 4 hours. 
The propellor mixers in the guide tube operate at 2000 rpm, and the ribbon 
mixer at 100 rpm. 
The circulation time is 3.0 seconds and the mixing time 18.0 seconds. 
The polymer obtained is of homogeneous composition. 
TABLE I 
__________________________________________________________________________ 
Circula- 
Mixing 
MA con- 
Styrene 
Overall- 
MA in end 
Exam- 
tion time 
time 
version 
conversion 
conversion 
product Tg-range 
.DELTA. Tg 
ple (sec.) 
(sec.) 
(%) (%) (%) (%) -- Mw 
( C) ( C) 
__________________________________________________________________________ 
1 7.0 35 80.8 72.4 74.5 27.1 91000 
164-170 
6 
2 2.2 13 85.1 72.3 75.4 27.1 103000 
164-170 
6 
A 6.6 -- 75.6 54.9 60.2 30.3 61000 
171-183 
12 
3 8.6 8.6 80.9 54.7 58.8 20.7 177000 
150-156 
6 
B 34.0 34.0 
77.4 55.7 59.2 19.7 173000 
148-159 
11 
4 3.0 18.0 
82.5 79.4 80.2 26.6 83000 
163-170 
7 
__________________________________________________________________________