Method of manufacturing an intermediate product for an interposer and intermediate product for an interposer

A method of manufacturing an intermediate product for an interposer including a glass substrate having a plurality of through holes is provided. The method includes a step of forming a resin layer on a support substrate, and a step of forming a laminated body by adhering the glass substrate having the plurality of through holes on the resin layer. The glass substrate having the plurality of through holes has a thickness within a range of 0.05 mm to 0.3 mm.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an interposer and a method of manufacturing an interposer.

2. Description of the Related Art

In view of the demands for high integration and miniaturization of semiconductor devices in recent years, efforts are being made to further develop the so-called “semiconductor three-dimensional (3D) packaging technology” which involves three-dimensionally integrating a plurality of LSI (large-scale integration) chips of a system into a single package.

In the semiconductor 3D packaging technology, elements have to be electrically interconnected three-dimensionally via fine conductive wiring patterns. However, it is difficult to form such fine wiring structures using conventional techniques such as wire bonding. Thus, in the semiconductor 3D packaging technology, a relay substrate having a plurality of via electrodes is used. Such a relay substrate is also referred to as an interposer. By using one or more relay substrates, a fine and complex three-dimensional conductive wiring pattern may be formed.

Such a relay substrate or interposer may be formed, for example, by forming a plurality of fine through holes in a glass substrate, and filling the through holes with conductive material thereafter. For example, International Publication No. WO2010/087483 discloses a technique that involves irradiating an excimer laser on a glass substrate to form a through hole.

A member for an interposer may be manufactured, for example, by irradiating an excimer laser on a glass substrate to form a through hole therein (hereinafter referred to as “glass substrate with through holes”).

Typically, a glass substrate used for manufacturing an interposer is extremely thin (e.g. 0.1 mm) so that a through hole may be easily formed in the glass substrate.

When such a thin glass substrate is used to manufacture a “glass substrate with through holes,” the strength of the “glass substrate with through holes” may be reduced due to the presence of through holes. For this reason, cracks and defects may be created in the “glass substrate with through holes” upon transferring the “glass substrate with through holes” for a next process and/or handling the “glass substrate with through holes” in various process steps, for example.

SUMMARY OF THE INVENTION

In view of the above, an aspect of the present invention relates to providing a method of manufacturing an intermediate product for an interposer that can reduce the risk of cracks and defects being created in a glass substrate with through holes. Another aspect of the present invention relates to providing an intermediate product for an interposer with a reduced risk of cracks and defects being formed in a glass substrate with through holes.

According to one aspect of the present invention, a method of manufacturing an intermediate product for an interposer including a glass substrate having a plurality of through holes is provided. The method includes a step of forming a resin layer on a support substrate, and a step of forming a laminated body by adhering the glass substrate having the plurality of through holes on the resin layer. The glass substrate having the plurality of through holes has a thickness within a range of 0.05 mm to 0.3 mm.

Also, in one embodiment of the method according to the present invention, the glass substrate having the plurality of through holes may be formed by irradiating laser light on a glass substrate.

In another embodiment, a maximum size of an opening of at least one of the through holes at a surface of the glass substrate on an opposite side of the resin layer may be within a range of 5 μm to 100 μm.

In another embodiment, the plurality of through holes may be formed on the glass substrate at a pitch within a range of 10 μm to 500 μm.

In another embodiment, the step of forming the resin layer may include a step of arranging a resin composition on the support substrate and solidifying the resin composition.

In another embodiment, the resin layer may have release characteristics with respect to the glass substrate.

In another embodiment, the resin layer may include at least one of a curable silicone resin and an acrylic resin that develops release characteristics upon being irradiated with ultraviolet light.

In another embodiment, the method of the present invention may include a step of filling at least one of the through holes of the glass substrate with a conductive material.

In another embodiment, the method of the present invention may include a step of forming a conductive wiring pattern on a surface of the glass substrate on an opposite side of the resin layer, the conductive wiring pattern being electrically connected to the conductive material filled in the at least one of the through holes.

In another embodiment, the method of the present invention may include a step of separating the resin layer and the glass substrate from each other.

According to another aspect of the present invention, an intermediate product for an interposer is provided that includes a glass substrate having a plurality of through holes, a support substrate, and a resin layer arranged between the support substrate and the glass substrate. The glass substrate has a thickness within a range of 0.05 mm to 0.3 mm.

Also, in one embodiment of the intermediate product according to the present invention, a maximum size of an opening of at least one of the through holes at a surface of the glass substrate on an opposite side of the resin layer may be within a range of 5 μm to 100 μm.

In another embodiment, the plurality of through holes may be formed on the glass substrate at a pitch within a range of 10 μm to 500 μm.

In another embodiment, the resin layer may have release characteristics with respect to the glass substrate.

In another embodiment, the resin layer may include at least one of a curable silicone resin and an acrylic resin that develops release characteristics upon being irradiated with ultraviolet light.

In another embodiment, the resin layer may have a thickness within a range of 1 μm to 50 μm.

In another embodiment, the plurality of through holes of the glass substrate may be filled with a conductive material.

In another embodiment, the intermediate product according to the present invention may include a conductive wiring pattern that is arranged on a surface of the glass substrate on an opposite side of the resin layer and is electrically connected to at least one of the conductive material filled in the through holes.

In another embodiment, the support substrate may have a thickness within a range of 0.3 mm to 1.1 mm.

In another embodiment, the glass substrate may have a thermal expansion coefficient within a range of 3×10−6/K to 1×10−5/K.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

First, terms used in the present description are defined below.

In the present description, “interposer” refers to a glass substrate having a through hole that is filled with a conductive material. In the present description, an “interposer” may also be referred to as “glass substrate with via electrode”.

(Glass Substrate with Through Holes)

In the present description, “glass substrate with through holes” refers to a glass substrate having a first surface and a second surface opposing each other and having at least one through hole penetrating through the first surface and the second surface.

When a conductive material is filled in a through hole of a “glass substrate with through holes”, the “glass substrate with through holes” becomes a “glass substrate with via electrode”, namely, an “interposer”.

(Intermediate Product for an Interposer)

In the present description, an “intermediate product for an interposer” (or simply “intermediate product”) collectively refers to a combination of members including a “glass substrate with through holes” and other members. For example, a laminated body including a “glass substrate with through holes,” which is described in detail below, is a representative example of an “intermediate product for an interposer”.

Also, in the present description, for the sake of convenience, a combination of members including a “glass substrate with via electrode”, namely, an “interposer”, and other members may also be referred to as “intermediate product for an interposer”. In other words, a member only made up of a “glass substrate with via electrode” is referred to as “interposer”, whereas a combination of members including a “glass substrate with via electrode” and one or more other members is referred to as “intermediate product for an interposer”.

In the following, a basic concept relating to the present invention is described.

According to an aspect of the present invention, a laminated body is used in a process of manufacturing an interposer, the laminated body including a glass substrate having a plurality of through holes formed thereon, a support substrate, and a resin layer that is arranged between the support substrate and the glass substrate.

As described above, when a glass substrate with through holes is manufactured using a thin glass substrate, the strength of the glass substrate with through holes is decreased due to the thinness of the glass substrate and the existence of through holes in the glass substrate. Thus, the glass substrate with through holes may be prone to cracks and defects upon being handled in various processes and/or being transferred for a next process step, for example.

In view of the above, according to an aspect of the present invention, a laminated body including a glass substrate with through holes, a resin layer, and a support substrate is used upon manufacturing an interposer.

By using such a laminated body, the strength of the glass substrate with through holes may be increased owing to the rigidity of the support substrate. Thus, by using such a laminated body, the risk of cracks and defects being created in the glass substrate with through holes upon transfer and/or handling in various processes may be reduced.

In the following, an intermediate product for an interposer according to an embodiment of the present invention is described with reference to the accompanying drawings. Note that in the descriptions below, a laminated body is illustrated as an example of an intermediate product for an interposer according to an embodiment of the present invention.

FIG. 1is a schematic cross-sectional view of a first laminated body100according to a first embodiment of the present invention.

As illustrated inFIG. 1, the first laminated body100according to the first embodiment includes a support substrate110, a resin layer120, and a glass substrate with through holes130stacked in this order.

The glass substrate with through holes130includes a glass substrate140with a first surface142and a second surface144wherein a plurality of through holes150penetrating through the first surface142and the second surface144are formed on the glass substrate140.

The glass substrate140has a thickness in the range of 0.05 mm to 0.3 mm.

The support substrate110has a greater rigidity than the glass substrate with through holes130and is capable of enhancing the strength of the first laminated body100.

The resin layer120is arranged on the second surface144of the glass substrate140. The resin layer120binds the glass substrate with through holes130and the support substrate110together.

The strength of the first laminated body100having the configuration as illustrated inFIG. 1may be substantially increased as compared with the glass substrate with through holes130alone. Thus, by using the first laminated body100, the risk of cracks and defects being created in the glass substrate with through holes130upon transfer or handling in various processes may be reduced, for example.

Note that the resin layer120of the first laminated body100preferably has “release characteristics” with respect to the glass substrate with through holes130.

In the present description, “release characteristics” refers to characteristics of the resin layer120being easily separable from a member that is attached thereto (the glass substrate with through holes130in the present case) without leaving a part of the resin layer120remaining on the member.

Oftentimes, the support substrate110and the resin layer120included in the laminated body100are unnecessary elements of an interposer corresponding to the final product. Thus, when the laminated body100is used, the glass substrate with through holes130may desirably be separated from the resin layer120at their interface during a suitable process step before the interposer is provided as a final product.

In such a case, if the glass substrate with through holes130and the resin layer120are firmly bonded together, the resin layer120may not be properly separated from the glass substrate with through holes130, or defects such as cracking may occur in the glass substrate with through holes130upon separating the resin layer120. For example, when a part of the resin layer120remains on the surface of the glass substrate with through holes130, extra work may be required to remove such residue.

However, if the resin layer120has release characteristics with respect to the glass substrate with through holes130, the resin layer120may be properly separated from the glass substrate with through holes130and the above-described problem may be prevented.

Note that the resin layer120does not necessarily have to have such release characteristics at all times. For example, the release characteristics of the resin layer120may be arranged to develop right before separating the resin layer120from the glass substrate with through holes130. For example, some types of acrylic resin develop release characteristics upon being irradiated with ultraviolet light. By using such acrylic resin as the resin layer120, adequate adhesion between the glass substrate with through holes130and the resin layer120may be secured while handling the laminated body100under normal circumstances, and ultraviolet light may be irradiated on the resin layer120at a suitable stage to separate the glass substrate with through holes130from the laminated body100.

Also, in the first laminated body100having the configuration as illustrated inFIG. 1, because the second surface144of the glass substrate with through holes130is covered by the resin layer120, defects such as voids may be prevented from being formed in a via electrode upon performing a process step of forming the via electrode by filling the through hole150with conductive material, for example.

In the following, the above effect is described in greater detail with reference toFIGS. 2 and 3.

FIGS. 2 and 3illustrate process steps for forming a via electrode by filling a through hole of a glass substrate with conductive material in a plating process.FIG. 2is a cross-sectional view of conventional process steps for forming a via electrode in a glass substrate with through holes.FIG. 3is a cross-sectional view of process steps for forming a via electrode in the glass substrate with through holes130using the laminated body100having the configuration as illustrated inFIG. 1.

As illustrated inFIG. 2, in the conventional process steps for forming a via electrode in a glass substrate with through holes, first, a glass substrate40having a though hole50is prepared (seeFIG. 2 (a)).

Then, a conductive layer is arranged on a first surface42, a second surface44, and the through hole150of the glass substrate40in an electroless plating process (not shown).

Then, in an electrolytic plating process, a conductive material55is deposited on regions of the glass substrate40where the conductive layer has been formed. During the electrolytic plating process, an electric field tends to be concentrated around the edges of the opening of the through hole50due to influences of the so-called “edge effect”. As a result, the conductive material55grows around the edges of the opening of the through hole50to protrude outward as illustrated inFIG. 2 (b).

As the plating process time is increased, this tendency becomes more conspicuous. That is, growth of the plating layer may be concentrated around the edges of the opening of the through hole50and the plating layer may hardly be grown at a side face portion of the through hole50(the side wall of the glass substrate40). As a result, after a certain time elapses, the opening of the through hole50may be closed by the conductive material55at the edges of the opening of the through hole50even though the interior of the through hole50is not sufficiently filled with the conductive material55as illustrated inFIG. 2 (c).

In such a state, the plating solution cannot be adequately diffused within the through hole50. As a result, after the plating process is completed, a void90is created within the through hole50as illustrated inFIG. 2 (d).

Then, as illustrated inFIG. 2 (e), the conductive material55adhered to the first surface42and the second surface44of the glass substrate40is removed to form a via electrode60. However, the void90still remains in the via electrode60such that a uniform via electrode60cannot be created.

On the other hand, in the case of forming a via electrode by a plating process using the first laminated body100according to the first embodiment, as illustrated inFIG. 3, the resin layer120is arranged on the second surface144of the glass substrate140.

In this way, influences of the above-described edge effect may be suppressed when a plating process is performed on the through hole150. More specifically, as illustrated inFIG. 3 (b), the growth and outward protrusion of a conductive material155may be substantially suppressed at least at the second surface144of the glass substrate140. Also, because influences of the edge effect are mitigated, uniform growth of the conductive material155within the through hole150may be promoted, and growth of the conductive material155at a side surface portion of the through hole150(the side wall of the glass substrate140) may be promoted.

Further, in general, a plating layer is more easily formed on the surface of the resin layer120as compared to the surface of the glass substrate140. Thus, by using the laminated body100including the resin layer120arranged on the second surface144of the glass substrate140, growth of the conductive material155from the second surface144side may be promoted within the through hole150.

When the plating process is continued, as illustrated inFIG. 3 (c)toFIG. 3 (d), the through hole150may be filled up with the conductive material155before the opening at the first surface142of the glass substrate140is closed by a portion of the conductive material155protruding at the edge of the opening.

Then, after the plating process is completed, and the conductive material155adhered to the first surface142and the second surface144of the glass substrate140is removed, a via electrode160with less voids and defects may be formed within the through hole150as illustrated inFIG. 3 (e).

As can be appreciated from the above, by using the laminated body100in the process step of forming a via electrode by filling the through hole150with a conductive material, defects such as voids are less likely to be created in the resulting via electrode.

In the following, a laminated body according to another embodiment of the present invention is described with reference toFIG. 4.

FIG. 4is a schematic cross-sectional view of a second laminated body200according to a second embodiment of the present invention.

As illustrated inFIG. 4, the second laminated body200has a configuration basically similar to that of the laminated body100as illustrated inFIG. 1. Thus, inFIG. 4, elements corresponding to those illustrated inFIG. 1are given reference numerals equal to 100 more than the reference numerals of the corresponding elements inFIG. 1.

Note, however, that in contrast to the first laminated body100, the second laminated body200includes via electrodes260that are formed by filling a conductive material in through holes250of a glass substrate with through-holes230. Thus, the glass substrate with through-holes230of the laminated body200also constitutes a glass substrate with via electrodes230. Note that the type of conductive material filled in the through holes250is not particularly limited.

In the second laminated body200having the above-described configuration, effects similar to those obtained in the first laminated body100as described above may be obtained. For example, the risk of cracks and other defects being created in the glass substrate with through-holes230(glass substrate with via electrodes230) may be reduced during transfer and/or handling of the laminated body200in various processes.

In the following, a laminated body according to another embodiment of the present invention is described with reference toFIG. 5.

FIG. 5is a schematic cross-sectional view of a third laminated body according to a third embodiment of the present invention.

As illustrated inFIG. 5, the third laminated body300has a configuration basically similar to that of the laminated body200illustrated inFIG. 4. Thus, inFIG. 5, elements corresponding to those ofFIG. 4are given reference numerals that are equal to 100 more than the reference numerals of the corresponding elements inFIG. 4.

Note, however, that in contrast to the second laminated body200, the third laminated body300includes a conductive wiring pattern370arranged on top of a glass substrate with via electrodes330.

The conductive wiring pattern370includes an insulating layer375and a conductive wiring portion380formed inside and on the surface of the insulating layer375. A part of the conductive wiring portion380may be electrically connected to via electrodes360of the glass substrate with via electrodes330.

In the third laminated body300having the above-described configuration, effects substantially similar to those obtained in the first laminated body100and the second laminated body200as described above may be obtained. For example, the risk of cracks and other defects being created in the glass substrate with through-holes330(glass substrate with via electrodes330) may be reduced during transfer and/or handling of the laminated body300in various processes.

(Component Members of Laminated Body)

In the following, component members of the laminated body are described in greater detail.

Note that although component members of the third laminated body300as illustrated inFIG. 5are described as an example below, the first laminated body100and the second laminated body200may be made of similar component members.

The support substrate310is a member for supporting the resin layer320and the glass substrate with through holes330(or glass substrate with via electrodes330) arranged thereon. The support substrate310provides rigidity to the laminated body300, and in this way, the strength of the laminated body300may be increased.

The material of the support substrate310is not particularly limited.

For example, the support substrate310may be made of a metal such as stainless steel or copper. Alternatively, the support substrate310may be made of glass such as alkali-free glass or soda lime glass, for example. Alternatively, the support substrate310may be made of glass epoxy resin or plastic (synthetic resin), for example. Examples of plastic materials include, but are not limited to, polyethylene terephthalate resin, polycarbonate resin, polyimide resin, fluorine resin, polyamide resin, aromatic polyamide resin, polyamide-imide resin, polyether sulfone resin, polyether ketone resin, polyether ketone ketone resin, polyether ether ketone resin, polyethylene naphthalate resin, polyacrylic resin, various liquid crystal polymer resins, and silicone resin.

Note that when a heating process has to be performed on the laminated body300in the interposer manufacturing process, the support substrate310preferably has heat resistance.

The thickness of the support substrate310is not particularly limited but may be in the range of 0.3 mm to 1.1 mm, for example. Note that if the thickness of the supporting substrate310is too thin, the support substrate310may be unable to provide adequate rigidity to the laminated body300.

The resin layer320binds together the support substrate310and the glass substrate with through holes330.

The resin layer320may be made of curable silicone resin and/or acrylic resin, for example, but is not limited thereto.

As described above, the resin layer320preferably has release characteristics with respect to the glass substrate with through holes330. In this way, the portion of the laminated body300including the glass substrate with through holes330and the conductive wiring pattern370may be easily separated from the portion of the laminated body300including the resin layer320and the support substrate310at a suitable stage.

An example of a resin composition having such release characteristics includes the resin composition disclosed in Japanese Laid-Open Patent Publication No. 2011-46174 (curable silicone resin composition including organo alkenyl polysiloxane and organohydrogen polysiloxane having a hydrogen atom bonded to a molecular end of a silicon atom). Also, some types of acrylic resin develop release characteristics upon being irradiated with ultraviolet light.

Note that the adhesion between the support substrate310and the resin layer320is preferably greater than the adhesion between the resin layer320and the glass substrate with through holes330. In this way, the resin layer320may be prevented from being separated from the support substrate310at their interface upon separating the resin layer320from the glass substrate with through holes330. Thus, the portion of the laminated body300including the glass substrate with through holes330and the conductive wiring pattern370may be separated from the portion of the laminated body300including the resin layer320and the support substrate310.

The thickness of the resin layer320is not particularly limited. For example, the thickness of the resin layer320may be in the range of 1 μm to 50 μm.

(Glass Substrate with Through Holes330)

The glass substrate340for the glass substrate with through-holes330may be made of any type of glass such as soda lime glass or alkali-free glass, for example.

However, assuming through holes are to be formed in the glass substrate340through laser processing, the thermal expansion coefficient of the glass substrate340is preferably in the range of 3×10−6/K to 1×10−5/K. In this way, the glass substrate340may be substantially prevented from chipping and/or cracking when laser processing is performed thereon.

The glass substrate with through holes330has a thickness in the range of 0.05 mm to 0.3 mm.

The through holes350may be formed in the glass substrate340in any number, size, shape, and pitch.

For example, the shape of the through holes350may be substantially cylindrical, substantially elliptical, or have a substantially prismatic shape. Also, the through holes350may be tapered from the first surface342toward the second surface344of the glass substrate340.

Also, the maximum size of the through holes350at the first surface342or the second surface344of the glass substrate340(i.e. opening portions) may be in the range of 5 μm to 100 μm, for example. Note that the above maximum size may refer to the diameter or the long diameter of the openings of the through holes350in the case where the through holes350are substantially cylindrical or substantially elliptical.

Also, the through holes350may be arranged at a pitch of 10 μm to 500 μm in the glass substrate340, for example.

The material of the via electrodes360formed in the through holes350is not particularly limited as long as it is a conductive material. For example, the via electrodes360may be made of zinc, a zinc alloy, nickel, a nickel alloy, copper, or a copper alloy. As described below, the via electrodes360may be formed in the through holes350by a plating process.

The conductive wiring pattern370is arranged on top of the first surface342of the glass substrate340.

For example, the conductive wiring pattern370may include an insulating layer375and a conductive wiring portion380formed inside and on the surface of the insulating layer375.

The insulating layer375may be made of resin, for example, but is not limited thereto. The conductive wiring portion380may be made of a conductive metal material such as copper, for example. At least a part of the conductive wiring portion380may be electrically connected to the via electrodes360of the glass substrate with via electrodes330.

(Method of Manufacturing Laminated Body)

In the following a method of manufacturing a laminated body according to another embodiment of the present invention is described with reference to the drawings.

Note that a method of manufacturing the third laminated body300as illustrated inFIG. 5is described below as an illustrative example. Accordingly, reference numerals indicated inFIG. 5are used below. However, note that similar process steps may be implemented to manufacture the first laminated body100and the second laminated body200.

FIG. 6is a flowchart illustrating process steps of a method of manufacturing a laminated body according to an embodiment of the present invention.

As illustrated inFIG. 6, the method of manufacturing a laminated body according to the present embodiment includes:

a step of forming a resin layer on a support substrate (step S110);

a step of adhering a glass substrate having a plurality of holes and having a thickness of 0.05 mm to 0.3 mm on the resin layer to form a laminated body (step S120);

a step of filling at least one of the through holes of the glass substrate with a conductive material (step S130); and

a step of forming, on a surface of the glass substrate on the opposite side of the resin layer, a conductive wiring pattern that is electrically connected to the conductive material filled in the through hole (step S140).

In a method of manufacturing a laminated body according to another embodiment, if necessary or desired, the method may further include:

a step of separating the resin layer and the glass substrate from each other (step S150).

Note that a glass substrate with via electrodes having a conductive material filled in its through holes may have a greater strength than a glass substrate with through holes that does not have the conductive material filled therein. Accordingly, in some cases, the glass substrate with via electrodes may not be susceptible to cracking and defects even when the glass substrate with via electrodes is transferred alone or handled alone in various process steps, for example. In such a case, the execution order of step S140and step S150may be reverse, for example.

In the following, the above process steps are described in greater detail.

First, the resin layer320is formed on the support substrate310.

Note that the method of forming the resin layer320on the support substrate310is not particularly limited. For example, the resin layer320may be formed by arranging a liquid or non-liquid resin composition on the support substrate310and solidifying the resin composition.

The resin composition may contain an organic solvent as is necessary or desired.

Exemplary methods for arranging the resin composition on the support substrate310include spray coating, die coating, spin coating, dip coating, roll coating, bar coating, screen printing, and gravure coating.

Note that the method for solidifying the resin composition is not particularly limited. For example, the resin composition may be solidified by a heating process and/or an ultraviolet light irradiation process.

For example, in a case where a curable silicone resin is used as the resin layer320, the above-described resin composition (curable silicone resin composition including organo alkenyl polysiloxane and organohydrogen polysiloxane having a hydrogen atom bonded to a molecular end of a silicon atom) may be coated on the support substrate310after which the resin composition may be maintained in the atmosphere under a temperature of 50° C. to 300° C. to solidify the resin composition.

Note that the adhesion between the support substrate310and the resin layer320is preferably arranged to be relatively high such that when separating the glass substrate with through holes330from the laminated body300in a subsequent step (step S150), the support substrate310and the resin layer320may be prevented from separating at their interface.

Accordingly, in some embodiments, before arranging the resin composition on the support substrate310, a surface modification process may be performed on the surface of the support substrate310. Examples of the surface modification process include a chemical process such as a primer process for improving chemical bonding using a silane coupling agent, for example, a physical process such as a flame treatment for increasing the surface active group, and an a mechanical process such as sandblasting for increasing the roughness of the surface to promote the development of the wedge effect, for example.

Also, as described above, the resin layer320is preferably arranged to have release characteristics at its interface with the glass substrate with through holes330to be arranged in a subsequent step (step S120). In this way, in the step of separating the glass substrate with through holes330of the laminated body300(step S150), the glass substrate with through holes330and the resin layer320may be easily separated from each other at their interface.

Then, the glass substrate with through holes330is arranged on the resin layer320that has been formed in step S110, and the laminated body300is formed.

The glass substrate with through holes330is prepared by forming a plurality of through holes350in the glass substrate340.

The method for forming the through holes350is not particularly limited. For example, the through holes350may be formed in the glass substrate340by irradiating laser light such as an excimer laser having a suitable energy on the glass substrate340. Alternatively, the through holes350may be formed by a laser-guided discharge process, for example.

As described above, the number, size, shape, and pitch of the through holes350are not particularly limited. For example, the shape of the through holes350may be substantially cylindrical, substantially elliptical, or may have a substantially prismatic shape. Also, the through holes350may be tapered from the first surface342toward the second surface344of the glass substrate340.

The method of bonding the glass substrate with through holes330to the resin layer320is not particularly limited. For example, after arranging the glass substrate with through holes330on the resin layer320, the two members may be pressure bonded using a roll or a press, for example. Alternatively, after arranging the glass substrate with through holes330on the resin layer320, the members may be placed in a pressure chamber and bonded together by a non-contact bonding process, for example. Note that other various processes may be used to bond the glass substrate with through holes330and the resin layer320.

By performing the above steps, a laminated body including the support substrate310, the resin layer320, and the glass substrate with through holes330may be formed.

For example, the first laminated body100as illustrated inFIG. 1may be manufactured by the above steps.

In the case of manufacturing the third laminated body300(and the second laminated body200), at least one through hole350of the glass substrate with through holes330is filled with a conductive material to form a via electrode360.

Note that the type of conductive material used in the via electrode360is not particularly limited. For example, the conductive material may be nickel, a nickel alloy, copper, a copper alloy, zinc, or a zinc alloy.

Also, the method of forming the via electrode360is not particularly limited.

For example, the via electrode360may be formed by filling the through hole350with a conductive material in a plating process.

For example, in a case where copper is used as the conductive material and the through hole350is filled with copper in a plating process, the following process steps may be implemented.

First, a copper electroless plating process is performed to form an electroless copper plating film on the first surface342of the glass substrate340and the side wall of the through hole350.

Then, a copper electrolytic plating process is performed to form a copper electroplating layer on the copper electroless plating film formed in the first process.

In this way, the through hole350may be filled with copper and the via electrode360may be formed.

Note that in a laminated body according to an embodiment of the present invention, the second surface344of the glass substrate with through holes330is covered by the resin layer320. Thus, as described above, influences of the edge effect may be mitigated upon forming the via electrode360by a plating process, and the via electrode360may be formed with less voids and defects (seeFIG. 3).

Then, a desired conductive wiring pattern370is formed on the glass substrate with through holes330.

The method of forming the conductive wiring pattern370is not particularly limited, and various conventional methods may be used. For example, the conductive wiring pattern370may be formed by patterning an insulating layer on top of the glass substrate with through holes330via a mask and depositing a conductive material at desired positions thereafter. In another example, the conductive wiring pattern370may be formed by repeatedly performing the processes of depositing and partially etching an insulating film and depositing and partially etching a conductive material, for example, to form the conductive wiring portion380inside and/or on the surface of the insulating layer375.

By performing the above steps, the third laminated body300as illustrated inFIG. 5may be manufactured.

Then, if necessary or desired, the glass substrate with through holes330and the resin layer320may be separated from each other at their interface.

In this way, an intermediate product for an interposer including the glass substrate with through holes330and the conductive wiring pattern370formed thereon may be manufactured.

The above-described method of manufacturing a laminated body does not include a step of transferring or handling the relatively fragile glass substrate with through holes330alone. Accordingly, the risk of cracks and defects being created in the glass substrate may be reduced in manufacturing a laminated body or an intermediate product for an interposer that is ultimately obtained, for example.

Aspects of the present invention may be applied, for example, to an interposer that may be used in semiconductor 3D packaging technology.

Although the present invention has been described above with respect to illustrative embodiments, the present invention is not limited to these embodiments and various variations and modifications may be made without departing from the scope of the present invention.