Local dry etching method

In a local dry etching method, position-thickness data of a semiconductor wafer is previously obtained by measuring the wafer surface, components of position-thickness data shorter than a predetermined spatial wavelength are cut off by filtering and nozzle-wafer relative speed for planarizing the surface is calculated using the filtered data.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to wafer planarization technology for planarizing the thickness distribution of a semiconductor wafer by local dry etching of a relatively thick portion of the semiconductor wafer with activated species gas.

2. Description of Related Art

FIG. 1is an explanatory diagram for explaining a wafer planarization method and apparatus by means of local dry etching method with plasma. InFIG. 1, reference numeral100denotes a plasma generator, and activated species gas G in plasma generated in the plasma generator100is injected on the surface of a semiconductor wafer W from a nozzle101. The semiconductor wafer W is placed and fixed on a stage120, and the stage120is moved (scanned) horizontally at a controlled speed with respect to the nozzle101.

The thickness of the semiconductor wafer W is different locally. Prior to local dry etching process, the thickness of divided local areas of the semiconductor wafer W is measured to obtain position data of individual areas and thickness data of the positions (position-thickness data).

The amount of removed material of respective local areas removed by local dry etching depends on the exposing time period to activated species gas G and etching profile (removing speed distribution) of a local area. Based on the above, the relative speed (nozzle-wafer relative speed) to be applied when the nozzle passes over the respective local areas is calculated so that the wafer surface is planarized throughout, and the respective local areas are scanned at the calculated speed and pitch to planarize the entire surface of the wafer. At this occasion, the nozzle moves slow on the relatively thick portion and convex portion (relatively thick portion) Wa, and moves fast relatively on the relatively thin portion.

The surface of a semiconductor wafer is uneven with various levels as shown inFIG. 2, and the unevenness causes a low yield in semiconductor device production. Among these unevennesses, an unevenness called as flatness has the spatial wavelength of about λ=10−2m or larger level and wave height of h=10−7to 10−5m level. This unevenness is a target to be processed by a local dry etching apparatus. An unevenness called as nanotopography has the distribution center at the spatial wavelength of about λ=10−3m level and wave height of about h=10−8m level. Further, an unevenness called as micro-roughness has the distribution center at about λ=10−6m level and wavelength of about h=10−9m level.

A flatness measurement apparatus not only measures the above-mentioned flatness level but also detects smaller unevenness for the wavelength and wave height generally. The measurement result obtained from a flatness measurement apparatus has been used as it is as the basic data for calculating the nozzle-wafer relative speed formerly, and the measured nozzle-wafer relative speed value includes excessive acceleration and deceleration. Such nozzle-wafer relative speed that is input to a dry etching apparatus as the command value results in frequent acceleration and deceleration of a drive motor.

FIG. 3is a graph obtained by plotting a command value (input speed) of the nozzle-wafer relative speed and the measured stage moving speed when a nozzle moves from one end to the other end of a diameter of a wafer having a diameter of 200 mm.FIG. 3shows that there is large speed difference d between the measured value and command value and the nozzle-wafer relative speed cannot follow the command value exactly. The speed difference is absorbed in the form of instantaneous overload or out-of-step of a drive motor in a dry etching apparatus or deformation of some members of the dry etching apparatus. Such frequent acceleration and deceleration results in severe load on the drive motor and movable parts, and causes poor process precision and short machine life while the machine is used for a long time.

SUMMARY OF THE INVENTION

The present invention has been developed to control the nozzle-wafer relative speed to be given to a dry etching apparatus as the command value within minimum acceleration and deceleration and also to obtain the sufficient accuracy required for planarization by processing the position-thickness data obtained by a flatness measurement apparatus, and to thereby reduce the overload on a drive motor and deformation of members of the drive motor and to maintain the process precision and machine life.

The above-mentioned problem will be resolved by applying means described below. According to one aspect of the present invention, the invention provides a local dry etching method in which the nozzle-wafer relative speed to be given to a local dry etching apparatus is calculated using the position-thickness data of a semiconductor wafer obtained by a flatness measurement apparatus and material on the wafer surface is removed and planarized with activated species gas injected from a nozzle that is moving along the wafer surface according to the calculated nozzle-wafer relative speed. In this method, the above-mentioned position-thickness data is subjected to filtering when the nozzle-wafer relative speed is calculated to thereby cut off the component having a predetermined wavelength or shorter.

According to another aspect of the present invention, the present invention provides the local dry etching method described in the above-mentioned invention, wherein the above-mentioned predetermined spatial wavelength is 10 mm and the component having this spatial wavelength or shorter is cut off from the above-mentioned position-thickness data.

According to another aspect of the present invention, the present invention provides the local dry etching method described in the above-mentioned invention, wherein the predetermined spatial wavelength is 20 mm and the component having this spatial wavelength or shorter is cut off from the above-mentioned position-thickness data.

According to another aspect of the present invention, the present invention provides a method for processing the position-thickness data of the semiconductor wafer surface, wherein the position-thickness data of the semiconductor wafer surface measured for calculating the nozzle-wafer relative speed of the local dry etching apparatus is subjected to filtering under an assumption that the thickness data at respective positions is equal to the average value of all thickness data in a predetermined radius.

According to another aspect of the present invention, the present invention provides a method for processing the position-thickness data of the semiconductor wafer surface, wherein the above-mentioned predetermined radius is about half of the spatial wavelength to be cut off.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Now, preferred embodiments of the present invention will be described in detail while referring to the accompanying drawings.

FIG. 4is an explanatory diagram describing an embodiment of a local plasma etching apparatus. The local plasma etching apparatus is provided with a plasma generator1, gas supplier3, and X-Y driving mechanism5. The plasma generator1is an apparatus that converts gas in an alumina discharge tube to plasma to generate activated species gas G containing neutral radical and comprises a microwave oscillator10and waveguide11. The microwave oscillator10is a magnetron that oscillates microwave M of a predetermined frequency.

The waveguide11that is inserted through the alumina discharge tube2is served to transmit the microwave M generated from the microwave oscillator10. A reflection plate (short plunger)12that reflects the microwave M to form a standing wave is fixed inside in the left side end of the waveguide tube11. A stub tuner13that is served for phase matching of the microwave M and an isolator14that is served for bending the reflected microwave M heading toward the microwave oscillator10in a 90° direction (surface direction inFIG. 4) are mounted on the middle of the waveguide tube11.

The alumina discharge tube2that is a cylinder having a nozzle20at the bottom end is connected to a supply pipe30of the gas supplier3at the top end of the alumina discharge tube2. The gas supplier3that is served to supply gas into the alumina discharge tube2has an SF6(sulfur hexafluoride) gas bomb31, and the bomb31is connected to the supply pipe30through a valve32and flow controller33. Only sulfur hexafluoride gas may be used solely, or mixed gas containing sulfur hexafluoride gas and other gases, which is formed by supplying other gases to the supply pipe30simultaneously, may be used.

When gas is supplied to the alumina discharge tube2from the gas supplier3and the microwave M is oscillated from the microwave oscillator10simultaneously, the gas is converted to plasma in the alumina discharge tube2and activated species gas G generated by plasma-conversion is injected from the nozzle20because the plasma generator1has the structure as described hereinabove.

A silicon wafer W is attracted electrostatically on a wafer table40when the silicon wafer W is placed on the wafer table40in a chamber4. The chamber4is provided with a vacuum pump41, and the vacuum pump41is served to evacuate the internal of the chamber4(reduce pressure). A hole42is formed on the top face of the chamber4at the center, and the nozzle20of the alumina discharge tube2is inserted into the chamber4from the outside through the hole42. An O-ring43is fitted between the hole42and the alumina discharge tube2to keep the gap between the hole42and the alumina discharge tube2airtight. A duct44is provided around the nozzle20inserted into the hole42, and reaction product gas generated during etching is exhausted outside from the chamber4by driving the vacuum pump45.

An X-Y driving mechanism5is provided in the chamber4and supports the wafer table40on the bottom of the table. The X-Y driving mechanism5moves the wafer table40in the right-left direction inFIG. 4by means of an X drive motor50and moves the wafer table40and the X drive motor50together in the front-back direction of the paper inFIG. 4by means of a Y drive motor51. In other words, the X-Y driving mechanism5moves the nozzle20in X-Y direction relatively to the silicon wafer W.

SF6gas in the bomb31flows into the supply pipe30and is supplied to the alumina discharge tube2when the valve32of the gas supplier3is opened. At this occasion, the flow rate of SF6gas is controlled by adjusting opening of the valve32.

SF6gas or mixed gas containing SF6gas is supplied and the microwave oscillator10is driven simultaneously. The simultaneous operation converts SF6gas to plasma by microwave M and generates activated species gas G containing F (fluorine) radical (neutral activated species), namely neutral radial. The activated species gas G is guided to the nozzle20of the alumina discharge tube2thereby, and injected toward the silicon wafer W from an aperture20aof the nozzle20.

A control computer49drives the X-Y driving mechanism5to move the wafer table40in an X-Y direction, on which the silicon wafer W has been attracted, simultaneously with injection of activated species gas. The movement in an X-Y direction allows the nozzle20to scan the wafer W.FIG. 5shows the scanning pattern of the nozzle20, and the scanning pattern covers the entire surface of the wafer W with a pitch p.

The surface material of the silicon wafer reacts chemically with activated species gas and generated gaseous product flows out from the place together with injected gas, and then the material is removed from the surface of the silicon wafer W thereby. The thickness reduction amount is controlled by controlling the relative speed between the silicon wafer W and the nozzle20because the amount to be removed is approximately proportional to the time period of exposure to activated species gas.

The above-mentioned relative speed is determined as described below. At first, the surface flatness of each wafer is measured previously by means of a flatness measurement apparatus. The measurement result is obtained in the form of thickness data of individual lattice-like small areas on the wafer surface (position-thickness data). The total thickness reduction amount is adjusted for all the individual areas and the nozzle-wafer relative speed that is to be applied when the nozzle20passes over each area is calculated so that the entire wafer surface is planarized using the etching profile data, predetermined pitch p, and position-thickness data.

As described in the section “Description of Related Art”, the measurement data measured using a flatness measurement apparatus is used as it is as the position-thickness data to be used for obtaining the nozzle-wafer relative speed in the conventional local dry etching method. Consequently, the nozzle-wafer relative speed with large speed fluctuation is obtained as a calculation result. In a real dry etching apparatus, a drive motor or machine cannot follow such large speed fluctuation (acceleration), and the large speed fluctuation causes instantaneous overload or out-of-step on the drive motor or causes deformation of members. Such overload, out-of-step, and deformation cause poor process precision and short machine life of the dry etching apparatus while the apparatus is used for a long time.

Local dry etching is carried out as described below according to the present invention.FIG. 6is a flowchart for describing the operation. At the starting of the local dry etching operation (step S00), the flatness of the surface of each wafer is measured using a flatness measurement apparatus in step S01. In step S02, the measurement result (position-thickness data) is subjected to filtering to thereby cut off component having a predetermined spatial wavelength or shorter. This operation is carried out on each wafer, and needless noise is removed from the respective position-thickness data.

In the next step S03, the nozzle-wafer relative speed is calculated in a usual manner from the position-thickness data from which the noise has been removed. The calculated nozzle-wafer relative speed from which the noise has been removed does not include large speed fluctuation but can be used for removing excessive material as required. In step S04, the obtained nozzle-wafer relative speed is input to a control computer49in the dry etching apparatus, and dry etching is carried out using the nozzle-wafer relative speed (step S05)

Naturally, the magnitude of the nozzle-wafer relative speed is different depending not only on individual wafers but also on the nozzle position (relative position to a wafer) on a wafer. The operation ends when planarization of all wafers is completed (step S99). The filtering may be executed by the control computer49or may be executed by other computer.

The filtering is described exemplarily with reference to FIG.7. The wafer surface is divided into fine lattice-like areas, and the position-thickness data is represented as the thickness of respective divided areas T(x, y). As shown in the equation 1 ofFIG. 8, an average value of the thickness T(x+i, y+j) of an area in a circle having a radius fs at the center of one certain addressed area is obtained, and this value is regarded as a new thickness Ta (x, y). A group of thickness Ta data obtained respectively for areas is regarded as new position-thickness data.

In the above-mentioned processing, the spatial wavelength component having wavelength of about double radius fs or shorter (namely, short wavelength component that is noise for the dry etching apparatus) is cut off. Otherwise, the square having a side of 2fs−1 (shown in a dashed line,FIG. 7) may be employed instead of the above-mentioned radius fs. The thickness average value is calculated by means of an arithmetic average method in the above-mentioned description, but other average calculations such as weighted average method in which peripheral data is weighted (multiplied by a factor) or other noise removing methods may be employed.

It is preferable that the cutoff wavelength is 10 mm or 20 mm depending on the nozzle diameter. The spatial wavelength component having wavelength of 10 mm or 20 mm or shorter is cut off from the measurement data thereby. In this case, the number of radius fs corresponds to 5 to 10 (numbers 5 and 10 correspond to number of areas respectively) for the side length of a divided area of 1 mm.

Although only preferred embodiments are specifically illustrated and described herein, it will be appreciated that many modifications and variations of the present invention are possible in light of the above teachings and within the purview of the appended claims without departing from the spirit and intended scope of the invention.