Electrode structure, method of manufacturing the same, secondary battery including the same

The present invention relates to an electrode structure, a method of manufacturing the same, and a secondary battery including the same, and the electrode structure may include a negative electrode part; a positive current collector which is formed of a fabric material and surrounds an outer surface of the negative electrode part; and a positive electrode coupled to an edge of the positive current collector.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority to and the benefit of Korean Patent Application No. 10-2018-0127779 filed on Oct. 24, 2018, the disclosure of which is incorporated herein by reference in its entirety.

BACKGROUND

1. Field of the Invention

The present invention relates to an electrode structure, a method of manufacturing the same, and a secondary battery including the same, and more specifically, to an electrode structure including a positive electrode coupled to an edge of a positive current collector, a method of manufacturing the same, and a secondary battery including the same.

2. Discussion of Related Art

Secondary batteries are batteries in which materials capable of electrochemical reaction are generally used for positive and negative electrodes so as to convert between chemical energy and electric energy such that charging and discharging occur. The secondary batteries are mainly used for vehicles, vessels, and the like which need to store a large amount of power.

A typical example of the secondary battery is a lithium ion battery configured to generate electric energy through a change in chemical potential when metal (for example, lithium or natrium) ions are intercalated/deintercalated between positive and negative electrodes. [Patent Document 1]

However, since the lithium ion battery has a high explosion risk and a price of a lithium metal oxide (for example, LiCoO2and LiMn2O4) used as a positive active material is high, a high expense is needed to form a large energy storage system (ESS), and an environment problem may occur when a waste battery is treated.

Accordingly, a material which has a low explosion risk, is eco-friendly, is abundant on the earth, and is inexpensive needs to be selected, but a study result thereof is still insufficient.

SUMMARY OF THE INVENTION

The present invention is directed to providing an electrode structure and a method of manufacturing the same.

In addition, the present invention is directed to providing a secondary battery including an electrode structure.

Objectives of the present invention are not limited to the above-described objectives, and other objectives which are not described above will be clearly understood through following descriptions.

According to an aspect of the present invention, there is provided an electrode structure including a negative electrode part, a positive current collector which is formed of a fabric material and surrounds an outer surface of the negative electrode part, and a positive electrode coupled to an edge of the positive current collector.

The positive electrode may be formed to have an edge frame form in which a central portion is hollow.

The positive electrode may be formed of a metallic material.

The positive electrode may be formed to have a mesh form.

The positive current collector and the positive electrode may be coupled by spot welding.

The positive current collector and the positive electrode may be coupled by coupling a bolt and a nut.

The negative electrode part may include a negative current collector in which a part of an upper end portion thereof is externally exposed to form an external connection terminal, and the external connection terminal may be insulated and sealed.

The external connection terminal may be soaked in a sealing material contained in a container, the sealing material may be solidified in a state in which the external connection terminal is soaked in the sealing material, and the solidified sealing material may be separated from the container.

According to another aspect of the present invention, there is provided a method of manufacturing an electrode structure including forming a negative electrode part, forming a positive current collector which is formed of a fabric material and surrounds an outer surface of the negative electrode part, and forming a positive electrode coupled to an edge of the positive current collector.

The forming of the positive electrode may include forming the positive electrode to have an edge frame form in which a central portion is hollow and coupling the positive electrode to the edge of the positive current collector.

The forming of the positive electrode may include forming the positive electrode to have a mesh form.

The forming of the negative electrode part may include forming a negative current collector in which a part of an upper end portion thereof is exposed to form an external connection terminal, and the method may further include insulating and sealing the external connection terminal after the forming of the positive electrode.

The insulating and sealing of the external connection terminal may include soaking the external connection terminal in a sealing material contained in a container, solidifying the sealing material in a state in which the external connection terminal is soaked in the sealing material, and separating the solidified sealing material from the container.

According to still another aspect of the present invention, there is provided an electrode structure stack including a plurality of electrode structures, wherein each of the plurality of electrode structures includes a negative electrode part, a positive current collector which is formed of a fabric material and surrounds an outer surface of the negative electrode part, and a positive electrode coupled to an edge of the positive current collector.

The negative electrode part may include a negative current collector in which a part of an upper end portion thereof is externally exposed to form an external connection terminal, and the external connection terminals of the plurality of electrode structures may be insulated and sealed.

The external connection terminals may be soaked in a sealing material contained in a container, the sealing material may be solidified in a state in which the external connection terminals are soaked in the sealing material, and the solidified sealing material may be separated from the container.

Each of the plurality of electrode structures may include one or more holes at the same position, and the plurality of electrode structures may be coupled by commonly insertion coupling one bolt to each of the one or more holes and coupling a nut to the one bolt for each of the plurality of electrode structures.

According to yet another aspect of the present invention, there is provided an secondary battery including a negative electrode part including a plurality of solid electrolytes, a negative active material, and a negative electrolytic solution; a positive current collector which is formed of a fabric material and surrounds an outer surface of the negative electrode part; and a positive electrode coupled to an edge of the positive current collector, wherein the electrode structure is soaked in an ion containing solution including metal ions which are the same as metal ions included in the negative active material.

The negative electrode part may include a negative current collector in which a part of an upper end portion thereof is externally exposed to form an external connection terminal, and the external connection terminal may be insulated and sealed.

The external connection terminal may be soaked in a sealing material contained in a container, the sealing material may be solidified in a state in which the external connection terminal is soaked in the sealing material, and the solidified sealing material may be separated from the container.

Specific contents for realizing the above-described objectives will be clear through embodiments which will be described in detail with reference to the accompanying drawings.

However, the present invention may not be limited to the embodiments which will be described below and may be realized in various different forms and is provide in order to fully describe the scope of the present invention to those of ordinary skill in the art (hereinafter, an ordinary skilled person).

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS

Since the present invention allows for various changes and numerous embodiments, specific embodiments will be illustrated in the accompanying drawings and described in detail.

Various features appended in the claims will be more clearly understood with reference to the accompanying drawings and detailed descriptions. Apparatuses, methods, manufacturing methods, and various embodiments disclosed in the specification are provided as exemplary embodiments. The disclosed structural and functional features are for those skilled in the art to specifically realize the various embodiments and not to limit the scope of the present invention. The disclosed terms and sentences are to describe the disclosed invention such that those skilled in the art easily understand and not to limit the scope of the present invention.

In the description of the present invention, the detailed descriptions related to the present invention will be omitted in a case in which it is determined that the detailed descriptions related to known technology may unnecessarily obscure the gist of the present invention.

Hereinafter, an electrode structure, a method of manufacturing the same, and a secondary battery including the same according to embodiments of the present invention will be described.

A secondary battery described in the present specification includes an electrode structure according to one embodiment of the present invention and refers to a secondary battery including an ion containing solution as a positive electrolytic solution. In this case, the electrode structure may be soaked in the ion containing solution including metal ions, which is the same as metal ions included in a negative active material of a negative electrode part. As a non-restrictive example, the ion containing solution may be seawater including sodium ions, lithium ions, magnesium ions, and combinations thereof.

FIG.1is a view illustrating a functional configuration of an electrode structure100according to one embodiment of the present invention.FIG.2is a view illustrating an example of a negative electrode part110according to one embodiment of the present invention.FIG.3is a view illustrating an example of a positive current collector122according to one embodiment of the present invention.FIGS.4A and4Bare views illustrating a positive electrode124according to one embodiment of the present invention.

Referring toFIG.1, the electrode structure100may include the negative electrode part110and a positive electrode part120. In one embodiment, the electrode structure100may be referred to as a unit cell, a full cell, or a different name having a technical meaning equivalent thereto.

Referring toFIG.2, the negative electrode part110may include a body portion111, a laminator112, a sealing member113, a negative current collector114, and solid electrolytes115so as to form a negative electrode of the electrode structure100. In one embodiment, the negative electrode part110may include a negative active material and a negative electrolytic solution.

The body portion111may support the negative electrode part110and prevent the negative electrode part110from being bent or deformed due to an external force. The body portion111may include a plurality of openings. The solid electrolytes115may be positioned in each of the plurality of openings.

One surface of the laminator112may be fused to one surface of the body portion111. The laminator112may prevent external water vapor and atmospheric gas from being introduced into the negative electrode part110. A material of the laminator112may be an aluminum laminator film. Meanwhile, the laminator112may include a plurality of openings. A size of each of the plurality of openings may be less than a size of the solid electrolyte115. Accordingly, an edge of each of the plurality of openings may be fused to an edge of the solid electrolyte115.

The sealing member113may be fused to an edge of the negative electrode part110to seal the edge of the negative electrode part110. More specifically, the edge of the negative electrode part110is an edge of the laminator112, and the edge of the laminator112may be sealed by the sealing member113. The sealing member113may prevent a cut portion of the laminator112from being exposed to the outside.

One surface of a lower end portion of the negative current collector114may be in contact with a negative active material layer. In addition, a part of an upper end portion of the negative current collector114may be exposed to the outside to form an external connection terminal. The solid electrolyte115is an electrolyte capable of selectively transmitting metal ions such as lithium ions and sedum ions and may be provided as a plurality of solid electrolytes. For example, a material of the solid electrolyte115may be a sodium (Na) super ionic conductor (NASICON), a lithium super ionic conductor (LISICON), an amorphous ion conductor, a ceramic ion conductor, or a polymer-based material.

The positive electrode part120may include the positive current collector122and the positive electrode124to form a positive electrode of the electrode structure100.

Referring toFIG.3, the positive current collector122may be formed of a fabric material. In this case, the positive current collector122may have electronic conductivity and may be formed of a material which is stable against an ion containing solution (for example, seawater). For example, the positive current collector122is formed of a carbon fabric-based material having a liquid absorbent property. An example of the carbon fabric-based material may be carbon felt, carbon cloth, or the like.

The positive current collector122may absorb an external ion containing solution, and the ion containing solution absorbed in the positive current collector122may come into contact with the solid electrolyte115included in the negative electrode part110. Accordingly, as the secondary battery is charged or discharged, metal ions (for example, Li+or Na−) in the ion containing solution and the negative electrolytic solution may be exchanged through the solid electrolyte115.

Referring toFIG.4A, the positive electrode124may be formed to have a mesh form, and the positive current collector122coupled to the positive electrode124may easily absorb the external ion containing solution due to the mesh form. In one embodiment, referring toFIG.4B, the positive electrode124may be formed to have a plate form instead of the mesh form as long as the positive current collector122absorbs the external ion containing solution and does not reduce the performance of the secondary battery.

In addition, the positive electrode124may be formed to have a quadrilateral edge frame form in which a central portion is hollow and may be coupled to an edge of the positive current collector122. That is, the positive electrode124may support the edge of the positive current collector122. In this case, since a size of the positive current collector122is greater than a size of the negative electrode part110, the form of the entire electrode structure100may not be supported by only the positive current collector122formed of a fabric material. Accordingly, since the positive electrode124having a fixed form, that is, the quadrilateral edge frame form in which the central portion is hollow, is coupled to the positive current collector122, the positive electrode124, instead of the positive current collector122, may serve as a support configured to maintain the form of the entire electrode structure100.

Since the positive electrode124is formed of a metallic material and is in contact with the positive current collector122, the positive electrode124may compensate for low electronic conductivity of the positive current collector122. That is, since the positive electrode124is formed of the metallic material and compensates for high resistance of the positive current collector122, the positive electrode124may serve as a path which allows electronics to easily move therethrough. The positive electrode124may be stable against the ion containing solution (for example, seawater) and may support an entirety of the electrode structure100, and a material having electronic conductivity may be applied to the positive electrode124. For example, the positive electrode124may be formed of titanium, a polymer to which electronic conductivity is applied, or a polymer to which metal is attached.

FIG.5is a view illustrating a coupling structure of an electrode structure100according to one embodiment of the present invention.FIGS.6A and6Bare views illustrating coupling methods of an electrode structure100according to one embodiment of the present invention.

Referring toFIG.5, an electrode structure100may include a negative electrode part110, a first positive current collector122-1, a second positive current collector122-2, a first positive electrode124-1, and a second positive electrode124-2.

One surface of the negative electrode part110is pressed against one surface of the first positive current collector122-1, and the other surface of the first positive current collector122-1is pressed against the first positive electrode124-1. In addition, the other surface of the negative electrode part110is pressed against one surface of the second positive current collector122-2, and the other surface of the second positive current collector122-2is pressed against the second positive electrode124-2. In this case, since a size of the first positive current collector122-1and a size of the second positive current collector122-2are greater than a size of the negative electrode part110, an outer surface of the negative electrode part110is surrounded by a positive current collector, that is, the first positive current collector122-1and the second positive current collector122-2. In one embodiment, the first positive current collector122-1and the second positive current collector122-2may be pressed against the outer surface of the negative electrode part110and may be fused to at least a part of the outer surface of the negative electrode part110or adhered thereto by an adhesive. Accordingly, in the electrode structure100, since an electrolyte comes into contact with an ion containing solution through both surfaces of the electrode structure100, a reaction area can be maximized. Here, a part of an upper end portion of a negative current collector of the negative electrode part110may be exposed to the outside to form an external connection terminal.

In one embodiment, referring toFIG.6A, the first positive electrode124-1, the first positive current collector122-1, the negative electrode part110, the second positive current collector122-2, and the second positive electrode124-2are sequentially overlapped to form the electrode structure100. In this case, the first positive electrode124-1, the first positive current collector122-1, the second positive current collector122-2, and the second positive electrode124-2are parts to be welded and may be coupled to each other by performing spot welding on welding zones602and may include a stack hole604, in addition to the welding zones602, so as to be coupled to another electrode structure by coupling a bolt and a nut.

In another embodiment, referring toFIG.6B, a first positive electrode124-1, a first positive current collector122-1, a negative electrode part110, a second positive current collector122-2, and a second positive electrode124-2may be sequentially overlapped to form an electrode structure100. In this case, the first positive electrode124-1, the first positive current collector122-1, the second positive current collector122-2, and the second positive electrode124-2may be coupled by coupling a bolt and a nut to a hole606and may include a stack hole608, in addition to the holes606, so as to be coupled to another electrode structure by coupling a bolt and a nut.

FIG.7Ais a view illustrating a structure of an electrode structure stack according to one embodiment of the present invention.FIG.7Bis a view illustrating an example of adjusting distances between electrode structures according to one embodiment of the present invention.

Referring toFIG.7A, an electrode structure stack700may include a plurality of electrode structures710-1to710-5. In this case, the plurality of electrode structures710-1to710-5may be coupled by bolts702and nuts704.

Specifically, since each of the plurality of electrode structures710-1to710-5includes at least one hole at the same position, and the bolt702is commonly insertion-coupled to the holes, the nut704is coupled to each of the plurality of electrode structures710-1to710-5, a stack structure having a minimum volume may be formed, and an electrode structure may be further coupled to one common bolt702in the corresponding holes according to necessary power or energy of an application to which the plurality of electrode structures710-1to710-5are applied.

Referring toFIG.7B, distances between the plurality of electrode structures710-1to710-5may be determined according to a flow rate of an ion containing solution. Specifically, as the flow rate of the ion containing solution increases, the ion containing solution may be more easily introduced into spaces between the plurality of electrode structures710-1to710-5, and thus the distances between the plurality of electrode structures710-1to710-5can be determined to be narrow, and a volume of the electrode structure stack700can be reduced.

One or more ring members706are insertion-coupled to the bolt702to be positioned between the plurality of electrode structures710-1to710-5so as to correspond to the determined distances, and thus the distances between the plurality of electrode structures710-1to710-5can be adjusted. Specifically, since the ring members706and the bolt702are insertion-coupled such that the plurality of ring members706, in which the number thereof is to adjust the distances determined by considering a thickness of one ring member706, are positioned between the plurality of electrode structures710-1to710-5, the distances between the plurality of electrode structures710-1to710-5can be adjusted.

FIG.8is a view illustrating a sealing of a negative electrode part according to one embodiment of the present invention;

Referring toFIG.8, outer surfaces of negative electrode parts of electrode structures included in an electrode structure stack800are surrounded by positive current collectors. In this case, a part of an upper end portion of a negative current collector of the negative electrode part is exposed to the outside to form an external connection terminal811.

Here, in a case in which the electrode structure stack800is completely soaked in an ion containing solution, the part of the upper end portion of the negative current collector, that is, the external connection terminal811, which is exposed to the outside so as to prevent a short circuit between positive electrode parts and the negative electrode parts, may be insulated and sealed. In one embodiment, in a state in which the external connection terminal811is soaked in an insulating and sealing material contained in a container and the insulating and sealing material is solidified in a state in which the external connection terminal811is soaked in the insulating and sealing material, the solidified insulating and sealing material813is separated from the container, and thus the external connection terminal811may be insulated and sealed.

In this case, the insulating and sealing material813may be a material which does not have electronic conductivity, has high adhesion to the external connection terminal811, and is stable against the ion containing solution (for example, seawater). For example, the insulating and sealing material may include an epoxy, silicone, a hot melt, rubber, a polymer, and plastic.FIG.9is a flowchart illustrating a method of manufacturing an electrode structure according to one embodiment of the present invention.

Referring toFIG.9, in operation S901, a negative electrode part is formed. In one embodiment, a negative current collector in which a part of an upper end portion thereof is exposed to form an external connection terminal may be formed.

In operation S903, a positive current collector which surrounds an outer surface of the negative electrode part is formed. In one embodiment, the positive current collector may be formed of a fabric-based material having a liquid absorbent property.

In operation S905, a positive electrode is coupled to an edge of the positive current collector. In one embodiment, the positive electrode may be formed to have an edge frame form in which a central portion is hollow and may be coupled to the edge of the positive current collector. In one embodiment, the positive electrode may be formed using a metallic material. In one embodiment, the positive electrode may be formed to have a mesh form. In one embodiment, the positive current collector and the positive electrode may be coupled by coupling a bolt and a nut. In another embodiment, a positive current collector and a positive electrode may be coupled by spot welding. In one embodiment, after the operation of forming the positive electrode, the external connection terminal may be insulated and sealed.

FIG.10is a flowchart illustrating a method of sealing a negative electrode part according to one embodiment of the present invention.

Referring toFIG.10, in operation S1001, an external connection terminal of the negative electrode part of an electrode structure is soaked in a sealing material contained in a container. In one embodiment, the sealing material may be a material which does not have electronic conductivity, has high adhesion to the external connection terminal, and is stable against an ion containing solution (for example, seawater).

In operation S1003, the sealing material is solidified. In operation S1005, the solidified sealing material is separated from the container. Accordingly, in a case in which the electrode structure is completely soaked in the ion containing solution, a short circuit between a positive electrode part and the negative electrode part of the electrode structure can be prevented.

According to one embodiment of the present invention, a positive electrode can be formed in a mesh form, and a positive current collector coupled to the positive electrode can easily absorb an external ion containing solution due to the mesh form.

In addition, according to one embodiment of the present invention, since a positive electrode is formed in an edge frame form in which a central portion is hollow, and is coupled to an edge of a positive current collector, the positive electrode can support an entirety of an electrode structure.

In addition, according to one embodiment of the present invention, since a positive electrode is formed of a metallic material and is in contact with a positive current collector, a low electronic conductivity of a positive current collector can be compensated for.

In addition, according to one embodiment of the present invention, a stack structure having a minimized volume can be formed due to a structure of an electrode structure stack, and an electrode structure can be additionally coupled to one common bolt in each hole corresponding to necessary power or energy of an application to which the electrode structure is applied.

In addition, according to one embodiment of the present invention, since a part of an upper end portion of a negative current collector exposed to the outside, that is, an external connection terminal is insulated and sealed, in a case in which an electrode structure is completely soaked in an ion containing solution, a short circuit between a positive electrode part and a negative electrode part can be prevented.

Effects of the present invention are not limited to the above-described effects, and expected provisional effects due to technical features of the present invention will be clearly understood from the above descriptions.

The above description is only an example describing a technological scope of the present invention, and various changes, modifications, and replacements may be made by those skilled in the art without departing from the spirit of the present invention.

Therefore, the embodiments disclosed above should be considered in a descriptive sense only and not for limiting the technological sprit of the present invention, and the scope of the present invention is not limited by the embodiments.

The scope of the present invention should be interpreted by the appended claims and should encompass all equivalents falling within the scope of the appended claims.