High-molecular crystalline polymer with alternating dimethylene and methyl-substituted disilene units in the main chain and method for preparing same

A novel chemical compound--a high-molecular crystalline polymer with alternating dimethylene and methyl-substituted disilene units in the main chain of the formula: ##STR1## wherein n is an integer of from 800 to 1,000. A method for preparing this polymer consists in that vapors of 1,2-bis(dimethylchlorosilyl)ethane is subjected to interaction with vapors of metallic sodium and/or potassium at a temperature within the range of from 250.degree. to 380.degree. C. under a pressure of 1,2-bis(dimethylchlorosilyl)ethane of from 0.1 to 10 mm Hg, followed by condensation of vapors of the resulting 1,1,2,2-tetramethyl-1,2-disilacyclobutane and polymerization thereof at a temperature within the range of from 20.degree. to 100.degree. C. One of embodiments of the method for preparing this polymer comprises polymerization in bulk of 1,1,2,2-tetramethyl-1,2-disilacyclobutane at a temperature within the range of from 20.degree. to 25.degree. C.

FIELD OF THE INVENTION 
The present invention relates to organo-silicon polymers and, more 
specifically, to a novel compound, viz. a high-molecular crystalline 
polymer with alternating dimethylene and methyl-substituted disilene units 
in the main chain and to a method for preparing same. 
1. Description of the Prior Art 
Such polymers and methods for preparing same have not been hitherto known. 
2. Disclosure of the Invention 
A high-molecular crystalline polymer with alternating dimethylene and 
methyl-substituted disilene units in the main chain has the formula: 
##STR2## 
wherein n is an integer of from 800 to 1,000. 
The polymer comprises a solid substance with the melting point of 
113.degree. C. and the decomposition temperature (in the air) of 
240.degree. C. The polymer is insoluble at a temperature within the range 
of from -70.degree. to +55.degree. C. in such solvents as alcohols 
(methanol, ethanol), ketones (acetone, methylethylketone), ethers and 
esters (diethyl ether, ethylacetate), halogenated hydrocarbons (carbon 
tetrachloride, chloroform, dichloroethane, trichloroethylene), paraffin 
(pentane, hexane, heptane, octane), naphthene (cyclohexane) and aromatic 
(benzene, toluene, o-, m-, and p-xylenes) hydrocarbons. The polymer swells 
in benzene, toluene, o-, m- and p-xylenes at the temperature of 55.degree. 
C. and it dissolves therein with increasing temperature to give viscous 
solutions. The polymer is resistant against concentrated aqueous solutions 
of acids (H.sub.2 SO.sub.4, HCl,HNO.sub.3) and alkalis (NaOH, KOH) and to 
the effects of light and moisture. 
The polymer has a molecular weight of from 110,000 to 140,000. 
The polymer is well machinable by cutting tools and mouldable by the 
hot-compression method. Articles manufactured from the polymer retain 
their shape for a long time at a temperature within the range of from 
-70.degree. to +95.degree. C. Furthermore, the polymer has good adhesive 
properties relative to glass. 
Chemical structure and other properties of the polymer have been 
established through the data of its elemental composition given 
hereinbelow, as well as the data of spectral and physico-chemical methods 
of analysis. 
Elemental composition (wt. percent) corresponds to that calculated for the 
fragment 
______________________________________ 
##STR3## 
C H 
______________________________________ 
Found, %: 50.01 11.12 38.76 
Calculated, %: 
50.00 11.11 38.89 
______________________________________ 
In the IR spectrum of the polymer there are bands of 828 cm.sup.-1 and 
1,237 cm.sup.-1 corresponding to valence vibrations of the group 
Si(CH.sub.3).sub.2 ; bands 2,944; 2,895; 2,877 and 2,780 cm.sup.-1 
corresponding to valence vibrations of the group .dbd.C--H in methyl and 
methylene groups; bands 1,050 and 1,126 cm.sup.-1 characteristic for the 
grouping .dbd.SiCH.sub.2 CH.sub.2 Si.dbd. and also bands 1,400, 765, 720, 
690, 610 and 300 cm.sup.-1. 
In the combination scattering spectrum there is observed the band of 385 
cm.sup.-1 corresponding to valence vibrations of the bond 
.tbd.Si--Si.tbd.. 
NMR spectra of a benzene solution of the polymer contain signals: 
.delta..sup.1 H.sub.(CH.sbsb.3.sub.-Si) .dbd.0.275 ppm (12H, s) 
.delta..sup.1 H.sub.CH.sbsb.2 .dbd.0.875 ppm (4H, s); .delta..sup.13 
C.sub.(CH.sbsb.3.sub.-Si) .dbd.--0.4 ppm (4C), .delta..sup.13 
C.sub.(CH.sbsb.2.sub.) .dbd.13.84 ppm (2C). 
The ratio of intensities of the signals of protons (carbons) of methyl and 
methylene groups correspond to the above-given structure of a monomer 
unit. 
The polymer crystallinity is justified by the presence of clearly 
pronounced reflexes in the X-ray pattern, as well as by the presence of an 
endothermal peak in the differential-thermal analysis curve which peak 
corresponds to the melting point of 113.degree. C. The polymer molecular 
weight of (1.1-1.4). 10.sup.5 (n=800 to 1,000) has been found through 
intrinsic viscosity in a solution of benzene at the temperature of 
60.degree. C. (n=0.20 to 0.27 dl/g) in a manner similar to that employed 
for other organosilicon polymers. 
In accordance with the present invention, the method for preparing a 
high-molecular crystalline polymer with alternating dimethylene and 
methyl-substituted disilene units in the main chain comprises reacting 
vapours of 1,2-bis(dimethylchlorosilyl)ethane with vapours of metallic 
sodium and/or potassium at a temperature within the range of from 
250.degree. to 380.degree. C. under a pressure of vapours of 
1,2-bis(dimethylchlorosilyl)ethane of from 0.1 to 10 mm Hg, followed by 
condensation of vapours of the resulting 
1,1,2,2-tetramethyl-1,2-disilacyclobutane and polymerization thereof at a 
temperature within the range of from 20.degree. to 100.degree. C. 
The selected conditions of the process are optimal. Thus lowering the 
process temperature below 250.degree. C. causes discontinuation of the 
reaction, while at a temperature above 380.degree. C. the yield of the 
polymer is lowered and a noticeable gas-formation occurs. 
The pressure range of from 0.1 to 10 mm Hg is defined by the partial 
pressure created by vapours of 1,2-bis(dimethylchlorosilyl)ethane. The use 
of pressures above 10 mm Hg causes clogging of the reactor with condensed 
products, while pressures below 0.1 mm Hg cause a lowered unit 
productivity and a reduced yield of the desired product. 
As it has been mentioned hereinbefore, vapours of 
1,2-bis(dimethylchlorosilyl)ethane are reacted with vapours of metallic 
sodium and/or potassium. The highest yield of the desired products is 
obtained in the case where a mixture of sodium and potassium is employed. 
The process of polymerization of 1,1,2,2-tetramethyl-1,2-disilacyclobutane 
is effected at a temperature within the range of from 20.degree. to 
25.degree. C. which is economically more efficient than at higher 
temperatures. 
In the reaction of vapours of 1,2-bis(dimethylchlorosilyl)ethane with 
vapours of sodium and/or potassium under the conditions selected as above 
volatile products are formed which contain up to 90-95% of 
1,1,2,2-tetramethyl-1,2-disilacyclobutane (the balance being impurities). 
The chemical structure of 1,1,2,2-tetramethyl-1,2-disilacyclobutane has 
been established by mass-spectra and NMR-spectra of .sup.1 H, .sup.13 C 
and .sup.29 Si, as well as by its specific reactivity in the reaction of 
oxidation with air oxygen with the formation of 
1,1,3,3-tetramethyl-1,3-disila-2-oxacyclobutane having characteristics 
corresponding to those described in the literature and its ability of 
forming said polymer. 
To facilitate carrying-out of the process under the selected conditions, 
the reaction of vapours of 1,2-bis(dimethylchlorosilyl)ethane with vapours 
of sodium and/or potassium should be preferably conducted in an inert gas 
current under a pressure of from 50 to 760 mm Hg. This permits variation 
of contact time of reagents at constant velocity of supplied vapors of 
1,2-bis(dimethylchlorosilyl/ethane). 
As the inert gas use may be made of any inert gas, preferably nitrogen, 
helium, argon. 
As it has been mentioned hereinabove, the reaction of vapours of 
1,2-bis(dimethylchlorosilyl)ethane with vapours of sodium and/or potassium 
results in the formation of a monomer- 
1,1,2,2-tetramethyl-1,2-disilacyclobutane which constitutes the major 
portion of the condensate. In addition, the condensate contains an 
insignificant amount of impurities which affect purity of the desired 
product. To remove these impurities, it is advisable that the 
polymerization of 1,1,2,2-tetramethyl-1,2-disilacyclobutane be carried out 
in the presence of an organic solvent. 
As the organic solvent it is preferable to use, for example, benzene, 
diethyl ether, pentane, hexane, cyclohexane. 
The removal of impurities from the condensate can be effected also by 
distillation. To this end, the condensate of 
1,1,2,2-tetramethyl-1,2-disilacyclobutane is distilled in vacuum of from 1 
to 15 mm Hg and at a temperature within the range of from 0.degree. to 
20.degree. C. depending on the pressure employed prior to polymerization. 
As a result of distillation there can be obtained up to 90% of 
1,1,2,2-tetramethyl-1,2-disilacyclobutane, since the distillation is 
accompanied by polymerization of the monomer in the still. 
A higher yield of the distillate of 
1,1,2,2-tetramethyl-1,2-disilacyclobutane is also obtained in the case of 
collection of the fraction of 0.degree.-2.degree. C./1 mm Hg, though the 
efficiency of purification of the condensate is decreased. For this 
reason, distillation of the condensate under pressure below 1 mm Hg is 
undesirable. 
In the case of collection of the fraction 18.degree.-20.degree. C./15 mm Hg 
there is ensured the highest purity of the distillate. However, 
distillation of the condensate at the temperature of 20.degree. C. and 
above is accompanied by a more pronounced polymerization of 
1,1,2,2-tetramethyl-1,2-disilacyclobutane in the still, wherefore the 
yield of the distillate is lowered. 
Another embodiment of the method for preparing a high-molecular crystalline 
polymer with alternating dimethylene and methyl-substituted disilene units 
in the main chain according to the present invention resides in that 
1,1,2,2-tetramethyl-1,2-disilacyclobutane is polymerized in bulk at a 
temperature within the range of from 20.degree. to 100.degree. C. 
Polymerization at the temperature of 20.degree. C. proceeds for two days; 
the rate of polymerization increases with temperature elevation and at the 
temperature of 100.degree. C. the final product is obtained with 1-2 
hours. The use of temperatures above 100.degree. C. is undesirable, since 
it results in lowering of the polymer molecular weight. 
As it has been already mentioned hereinbefore, from the economic standpoint 
the process of polymerization of 1,1,2,2-tetramethyl-1,2-disilacyclobutane 
at a temperature of from 20.degree. to 25.degree. C. is more efficient 
that at elevated temperatures. 
The high-molecular crystalline polymer with alternating dimethylene and 
methyl-substituted disilene units in the main chain can be used for the 
manufacture of gasoline-resistant gaskets, protective coatings and films 
due to its valuable properties, namely: insolubility in hydrocarbon media, 
resistance in acid and alkali aqueous solution, mechanical strength, 
adherence to glass and plasticity. It can be successfully used instead of 
teflon in sealing members of gasmetering cocks employed in chromatographic 
systems. 
The process for the production of the polymer according to the present 
invention can be implemented on a commercial scale. The process can be 
performed continuously. It does not necessitate the use of large amounts 
of a solvent and can be effected therewithout. The starting 
1,2-bis(dimethylchlorosilyl)ethane is a readily available starting 
material, since it can be readily prepared from acetylene and 
dimethylchlorosilane--an organosilicon monomer which is a product 
resulting from the commercial synthesis of methylchlorosilanes. 
The most preferred embodiment of the invention. 
The process is simple and preferably embodied in the following manner. 
Into a reactor provided with an external electric heating sodium and 
potassium are charged in a current of an inert gas such as argon or 
nitrogen. The reactor is connected with a trapping system and a vacuum 
pump. Into a vessel for the starting material also provided with an 
external electric heating 1,2-bis(dimethylchlorosilyl)ethane is charged. 
The vessel for the starting material is connected with the reactor by 
means of a pipe provided with a stop valve. When the predetermined 
temperature (250.degree.-380.degree. C.) is achieved, the concentration of 
vapours of alkali metals necessary for the process is obtained. Vapours of 
1,2-bis(dimethylchlorosilyl)ethane are admitted into the reactor from the 
vessel for the starting material. The supply rate of vapours of 
1,2-bis(dimethylchlorosilyl)ethane fed from the vessel for the starting 
material is varied by the temperature of its heating (15.degree. to 
90.degree. C.). Pressure of the product vapours ranges from 0.1 to 10 mm 
Hg. A dry inert gas such as helium or nitrogen under a pressure of from 50 
to 760 mm Hg is supplied into the reactor simultaneously with vapours of 
1,2-bis-(dimethylchlorosilyl)ethane. 
The volatile products formed in the reactor and containing 
1,1,2,2-tetramethyl-1,2-disilacyclobutane (up to 90-95%) and impurities 
pass into a trap cooled by dry ice or liquid nitrogen with the formation 
of a condensate. Then the condensate is mixed with an organic solvent at a 
volumetric ratio between the condensate and the organic solvent of 1:5-10 
and heated at a temperature of from 20.degree. to 25.degree. C. (heating 
of the condensate in the presence of an organic solvent is effected for 
the removal of impurities). During heating the polymer precipitates as 
white flakes and the impurities remain in the solution. The polymer is 
separated from the organic solvent by filtration. Then the polymer is 
washed with an organic solvent and dried in vacuum. 
In another embodiment of the present invention, a high-molecular 
crystalline polymer with alternating dimethylene and methyl-substituted 
disilene units in the main chain is prepared in the following manner. A 
frozen ampule with 1,1,2,2-tetramethyl-1,2-disilacyclobutane is heated and 
kept at the selected temperature for a period of time ranging, depending 
on the selected temperature, from two hours to two days.

For a better understanding of the present invention some specific examples 
are given hereinbelow by way of illustration. 
EXAMPLE 1 
Into a reactor provided with an external electric heater 16 g of a mixture 
of sodium and potassium (in the molar ratio therebetween of 1:1) are 
charged in a current of dry argon. The reactor is connected with a system 
of traps and a vacuum pump. Into a vessel for the starting material there 
are charged 10.7 g of 1,2-bis(dimethylchlorosilyl)ethane. The vessel with 
the starting material is connected with the reactor by means of a pipe 
provided with a stop cock. The contents of the reactor and the vessel for 
the starting material are heated. When temperature in the reactor is 
250.degree.-260.degree. C. and temperature of 
1,2-bis(dimethylchlorosilyl)ethane is 55.degree.-60.degree. C., the vacuum 
pump is switched on and the stop cock is carefully opened. The starting 
1,2-bis(dimethylchlorosilyl)ethane in the form of vapours is admitted into 
the reactor; its vapour pressure is 1.0-1.1 mm Hg. The resulting volatile 
products are passed into a trap cooled with dry ice and condensed therein. 
Then the thus-obtained condensate is heated to a temperature of from 
20.degree. to 25.degree. C. for 18-20 hours. The desired product is 
obtained as a solid white mass. 
The resulting polymer weight is 4.90 g (68.0% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.21 dl/g 
(at 60.degree. C.). 
EXAMPLE 2 
The polymer is prepared following the procedure described in the foregoing 
Example 1, except that the temperature of 
1,2-bis(dimethylchlorosilyl)ethane is maintained within the range of from 
30.degree. to 35.degree. C. and it is fed into the reactor under the 
pressure of its vapours of 0.50-0.55 mm Hg. To obtain the desired product 
with a higher degree of purity, the condensate is mixed with benzene at 
the volumetric ratio therebetween of 1:5, followed by heating to a 
temperature of from 20.degree. to 25.degree. C. During heating (after 6 
hours) white flakes of the polymer precipitate; they are separated by 
filtration, washed with benzene and dried in vacuum. 
The resulting polymer weight is 3.98 g (55.3% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.23 dl/g 
(at the temperature of 60.degree. C.). 
EXAMPLE 3 
The polymer is prepared following the procedure described in Example 1. The 
difference resides in that 16 g of a mixture of sodium and potassium are 
charged into the reactor at the molar ratio of 2:1 between sodium and 
potassium. Into the vessel for the starting material there are charged 
10.7 g of 1,2-bis(dimethylchlorosilyl)ethane having temperature of 
15.degree.-20.degree. C. The pressure of vapours of 
1,2-bis(dimethylchlorosilyl)ethane is equal to 0.1 mm Hg. Into the reactor 
heated to a temperature of from 300.degree. to 320.degree. C. dry helium 
is also fed under the pressure of 50 mm Hg. 
The resulting polymer weight is 2.15 g (29.9% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.22 dl/g 
(at the temperature of 60.degree. C.). 
EXAMPLE 4 
The polymer is prepared following the procedure described in Example 1 
hereinbefore. The difference resides in that 16 g of a mixture of sodium 
and potassium are charged into the reactor at the molar ratio of 3:1 
between sodium and potassium; into the vessel for the starting material 
there are charged 10.7 g of 1,2-bis(dimethylchlorosilyl)ethane at a 
temperature of 70.degree.-75.degree. C. The pressure of vapours of 
1,2-bis(dimethylchlorosilyl)ethane is 4.0-4.5 mm Hg; temperature in the 
reactor is 350.degree.-360.degree. C. 
The removal of impurities is effected following the procedure described in 
Example 2, except that the condensate is heated in the presence of pentane 
at the volumetric ratio between the condensate and pentane equal to 1:10. 
The resulting polymer weight is 4.01 g (55.8% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.24 dl/g 
(at the temperature of 60.degree. C.). 
EXAMPLE 5 
The polymer is produced following the procedure described in Example 1 with 
the exception that 1,2-bis(dimethylchlorosilyl)ethane having temperature 
of 85.degree.-90.degree. C. (with the pressure of its vapours of 9.5-10 mm 
Hg) is passed into the reactor heated to the temperature of 
370.degree.-380.degree. C. Simultaneously with vapours of 
1,2-bis(dimethylchlorosilyl)ethane fed into the reactor is dry nitrogen 
under pressure thereof of 200 mm Hg. 
Impurities are removed following the procedure described in Example 2, 
except that the condensate is heated in the presence of hexane at the 
volumetric ratio between the condensate and hexane equal to 1:7. 
The resulting polymer weight is 3.82 g (53.1% of the theoretical value), 
intrinsic viscosity (benzene solution of the polymer) [.eta.] is equal to 
0.23 dl/g (at the temperature of 60.degree. C.). 
EXAMPLE 6 
The polymer is prepared following the procedure described in Example 1. The 
distinction resides in that into the vessel for the starting material 10.7 
g of 1,2-bis(dimethylchlorosilyl)ethane are charged which is then heated 
to a temperature of 40.degree.-45.degree. C. The pressure of vapours of 
1,2-bis(dimethylchlorosilyl)ethane is equal to 0.60-0.65 mm Hg. The 
temperature in the reactor is maintained within the range of from 
370.degree. to 380.degree. C. Simultaneously with vapours of 
1,2-bis(dimethylchlorosilyl)ethane into the reactor dry helium is fed 
under the pressure of 50 mm Hg. The resulting volatile products are passed 
into a trap cooled with liquid nitrogen. 
The resulting polymer weight is 3.87 g (53.8% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.23 dl/g 
(at the temperature of 60.degree. C.). 
EXAMPLE 7 
The polymer is produced following the procedure described in Example 1. The 
difference resides in that 16 g of a mixture of sodium and potassium are 
charged into the reactor at the molar ratio between sodium and potassium 
of 1:3; into the vessel for the starting material there are charged 10.7 g 
of 1,2-bis(dimethylchlorosilyl)ethane which is heated to a temperature of 
from 50.degree. to 55.degree. C. The pressure of vapours of 
1,2-bis(dimethylchlorosilyl)ethane is equal to 0.85-0.90 mm Hg. The 
temperature in the reactor is maintained at 300.degree.-310.degree. C. 
Simultaneously with vapours of 1,2-bis(dimethylchlorosilyl)ethane dry 
helium is fed into the reactor under the pressure of 500 mm Hg. The 
resulting volatile products are passed into a trap cooled with liquid 
nitrogen. 
The removal of impurities is effected following the procedure described in 
Example 2 hereinbefore, except that the condensate is heated in the 
presence of cyclohexane at the volume ratio between the condensate and 
cyclohexane equal to 1:5. 
The weight of the resulting polymer is equal to 3.66 g (50.8% of the 
theoretical yield), intrinsic viscosity (benzene solution of the polymer) 
[.eta.]=0.23 dl/g (at the temperature of 60.degree. C.). 
EXAMPLE 8 
The polymer is produced following the procedure described in Example 1. The 
distinction resides in that into the vessel for the starting material 
there are charged 10.7 g of 1,2-bis(dimethylchlorosilyl)ethane which is 
heated to a temperature of from 60.degree. to 65.degree. C. The pressure 
of vapours of 1,2-bis(dimethylchlorosilyl)ethane is 1.8-2.0 mm Hg. The 
temperature in the reactor is maintained within the range of from 
340.degree. to 350.degree. C. Simultaneously with vapours of 
1,2-bis(dimethylchlorosilyl)ethane dry argon is fed into the reactor under 
atmospheric pressure. The removal of impurities is effected following the 
procedure described in Example 2, except that the condensate is heated in 
the presence of diethyl ether at the volumetric ratio between the 
condensate and diethyl ether equal to 1:5. 
The weight of the resulting polymer is 4.03 g (56.2% of the theoretical 
yield, intrinsic viscosity (benzene solution of the polymer [.eta.]=0.26 
dl/g (at the temperature of 60.degree. C.). 
EXAMPLE 9 
The interaction of vapours of 1,2-bis(dimethylchlorosilyl)ethane with 
vapours of sodium and potassium is effected in a tubular-type reactor 
connected, through an outlet pipe, with a system of traps and a vacuum 
pump. 
Sodium and potassium (in the molar ratio of 1:3) preheated to a temperature 
of from 100.degree. to 110.degree. C. are fed into the upper part of the 
reactor through a nozzle at the rate of 0.1 g/min. Vapours of 
1,2-bis(dimethylchlorosilyl)ethane at the temperature of 
70.degree.-75.degree. C. under the pressure of 4.0-4.5 mm Hg are fed into 
the same part of the reactor. In the middle section of the reactor, 
wherein temperature is maintained at 370.degree.-380.degree. C., sodium 
and potassium are sublimed and their vapours of 
1,2-bis(dimethylchlorosilyl)ethane. The non-volatile reaction products 
formed in the reactor and the unreacted sodium and potassium are condensed 
in the lower part of the reactor and flow down into a special vessel, 
while the volatile reaction products containing mainly 
1,1,2,2-tetramethyl-1,2-disilacyclobutane are passed, through an outlet 
pipe, into a trap cooled with dry ice. As a result, a condensate is 
formed. The resulting condensate is distilled in vacuum 
(18.degree.-20.degree. C./15 mm Hg) to give 1,1,2,2-tetramethyl-1,2 
-disilacyclobutane as a transparent liquid with a geranium scent. The 
monomer is maintained for two days at the temperature of 25.degree. C. 
The weight of the resulting polymer is 4.63 g (64.7% of the theoretical 
yield), intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.27 
dl/g (at the temperature of 60.degree. C.). 
EXAMPLE 10 
The polymer is produced following the procedure described in the foregoing 
Example 9. The distinction resides in that simultaneously with sodium, 
potassium and vapours of 1,2-bis-(dimethylchlorosilyl)ethane dry helium is 
fed under atmospheric pressure. 
The removal of impurities is effected following the procedure described in 
Example 2, except that the condensate is heated in the presence of pentane 
at the volumetric ratio of the condensate and pentane equal to 1:7. 
The weight of the resulting polymer is 4.49 g (62.4% of the theoretical 
yield), intrinsic viscosity [.eta.]=0.24 dl/g (at the temperature of 
60.degree. C.). 
EXAMPLE 11 
The polymer is produced following the procedure described in Example 1. The 
distinction resides in that the resulting condensate is subjected to 
distillation in vacuum (18.degree.-20.degree. C./15 mm Hg), whereafter 
purified 1,1,2,2-tetramethyl-1,2-disilacyclobutane is subjected to 
polymerization by heating to the temperature of 60.degree. C. 
The weight of the resulting polymer without the account of the polymer 
formed in the still is equal to 2.21 g (30.7% of the theoretical yield), 
intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.22 dl/g 
(at the temperature of 60.degree. C.). 
EXAMPLE 12 
The polymer is produced following the procedure described in Example 1. The 
distinction resides in that the resulting condensate is subjected to 
distillation in vacuum (0.degree.-2.degree. C./1 mm Hg), whereafter 
purified 1,1,2,2-tetramethyl-1,2-disilacyclobutane is subjected to 
polymerization by heating to the temperature of 100.degree. C. 
The weight of the resulting polymer is 3.94 g (54.7% of the theoretical 
yield), intrinsic viscosity (benzene solution of the polymer) [.eta.]=0.20 
dl/g (at the temperature of 60.degree. C.). 
EXAMPLE 13 
An ampule with 4.16 g of 1,1,2,2-tetramethyl-1,2-disilacyclobutane frozen 
in liquid nitrogen is maintained at a temperature of from 20.degree. to 
25.degree. C. for two days. There are obtained 4.16 g of the polymer (100% 
of the theoretical yield), intrinsic viscosity (benzene solution of the 
polymer) [.eta.] is equal to 0.24 dl/g (at the temperature of 60.degree. 
C.). 
EXAMPLE 14 
An ampule with 3.74 g of 1,1,2,2-tetramethyl-1,2-disilacyclobutane frozen 
in liquid nitrogen is heated to the temperature of 80.degree. C. and 
maintained at this temperature for two hours. There are obtained 3.74 g of 
the polymer (100% of the theoretical yield). The intrinsic viscosity 
(benzene solution of the polymer) [.eta.] 0.22 dl/g (at the temperature of 
60.degree. C.). 
EXAMPLE 15 
An ampule with 2.97 g of 1,1,2,2-tetramethyl-1,2-disilacyclobutane frozen 
in liquid nitrogen is heated to the temperature of 100.degree. C. and 
maintained at this temperature for two hours. There are obtained 2.97 g of 
the polymer (100% of the theoretical yield). The intrinsic viscosity 
(benzene solution of the polymer) [.eta.]=0.20 dl/g (at the temperature of 
60.degree. C.). 
INDUSTRIAL APPLICABILITY 
The high-molecular crystalline polymer with alternating dimethylene and 
methyl-substituted disilene units in the main chain according to the 
present invention is useful as a gasoline-resistant material in fuel lines 
of automobiles and other transport vehicles, for the manufacture of 
gasoline-resistant films and as protective coatings. 
The method for preparing this polymer is useful in the industry of 
heteroorganic synthesis.