Method for producing sorbents on the basis of a cellulose-containing material and clay minerals

The invention relates to a method for producing sorbents on the basis of a cellulose-containing material and at least one smectic clay mineral capable of swelling, which form lumps when absorbing liquids. The method is characterized in that: (a) the cellulose-containing material and smectic clay mineral in fine particle form are intimately mixed together, whereby total water content of the components to be mixed is between approximately 25 and 40 weight percent, or is adjusted to be within this range by the addition of water (b) this mixture is compressed by means of a matrix press, and (c) the compressed moulded bodies emerging from the matrix press are cut substantially perpendicular to the direction of emergence and dried. The invention further relates to a sorbent obtained by the above procedure and its use.

DESCRIPTION
 The invention concerns a process for production of sorbents based on
 cellulose-containing material and at least one smectitic clay mineral for
 absorption of liquid. These sorbents are suitable to absorb any liquids;
 they are particularly suited as litter for domestic animals, for which
 reason the subsequent comments refer to this area of application.
 Keeping of domestic animals, especially in a city environment, is
 increasingly connected with the use of litter. This has the task of
 absorbing liquids released by the animal. It is also supposed to remove
 the semisolid, moist animal excrements and excretions and thus reduce odor
 development. Good litters are also supposed to absorb the discharge or
 released liquid with formation of a compact clump, which can be simply and
 thriftily removed. An optimal litter should therefore have high absorption
 capacity and fully absorb the liquid discharged by the animals within the
 charge without wetting the bottom of the litter box.
 The litters found on the market are organic substances, like straw,
 sawdust, wood chips, bark, shredded paper, cellulose fibers, agricultural
 residues, etc.; these are used alone or in mixtures with inorganic
 material. The drawback of organic litters is the frequently nonexisting or
 insufficient clump formation and its consistency, as well as their
 tendency toward bacterial decomposition, especially in cooperation with
 moisture.
 A sorbent, especially a litter for domestic animals based on swellable
 smectitic clay minerals, is known from U.S. Pat. No. 5,000,115, which can
 additionally contain sand or cellulose-containing materials, like wood
 shavings or chips and ground paper. The components are mixed dry without
 compaction.
 A process to produce litters for domestic animals is known from U.S. Pat.
 No. 4,341,180, according to which water-containing wastepaper residues are
 dewatered to a water content of about 32 to 40%, pressed, pelletized and
 dried after addition of sodium bicarbonate as deodorant. The paper
 residues can contain about 10 to 50% ordinary paper fillers, like kaolin.
 The described fillers are not swellable, for which reason the litter do
 not form clumps during absorption of liquids.
 A litter and method for its production are known from DE-A-41 01 243,
 according to which cellulose, cellulose derivatives and/or
 cellulose-containing materials of agricultural or industrial origin, as
 well as wood wastes, like sawdust, with a particle size of up to 1 mm are
 mixed or agitated with ballast agents and thickeners, like bentonite, in
 the presence of water, the mixture is dewatered without compaction to a
 residual water content of no more than 10 wt % and the remaining residue
 ground to a particle size above 1 mm. The ballast agent is added in an
 amount so that the bulk density of the litter after drying lies above
 about 500 kg/m.sup.3. The higher bulk density relative to the organic
 litters is mentioned as advantageous.
 A litter based on cellulose-containing material as wet substance and a
 capillary-active, small-grained material, like ground limestone, wood
 flour, ground clay, bentonite or ground pumice is known from DE-A-38 16
 225. Recovered paper stock as wet substance with a moisture content of 50
 to 60% and ground pumice with a moisture content of less than 30% are
 preferably mixed and then dried. During use of a mixture of wood flour and
 cellulose fibers compaction occurs in a screw compactor. However,
 compaction is left out during the use of inorganic capillary-active
 substances. The litter is crumbly and has a high percentage of fine-dust
 material. During addition of liquids it does not form clumps.
 A method for production of sorbents based on smectite to absorb liquids is
 known from DE-A-4 338 362, in which (a) a smectite with a water content of
 less than 6 wt %; (b) a mass of fibrous cellulose and organic pigments
 occurring during processing of papermaking effluents; and (c) anhydrous
 calcium sulfate or calcium sulfate hemihydrate are mixed, compacted and
 pulverized; the amount ratio between (a), (b) and (c) is chosen so that
 the water content of the granular material is less than 20 wt %. During
 compaction pieces are formed with a broad particle size distribution,
 which are then ground, during which a relatively large amount of fine-dust
 material is formed.
 A method is known from EP-B-0 663 793 (DE-A-43 27 159) for production of
 sorbents based on smectites and cellulose-containing materials with low
 bulk density, in which a moist mixture of smectite and ground wood
 material or another cellulose-containing material of plant origin, i.e.,
 cellulose-containing primary raw material, is treated during internal
 shear with subsequent extrusion and then dried and granulated. During
 granulation a relatively high percentage of finely divided material is
 formed.
 A method to produce a clump-forming litter is disclosed In U.S. Pat. No.
 5,456,284, in which a smectitic clay is mixed before or after extrusion
 with a small percentage of a water-soluble adhesive or binder, for example
 CMC.
 Sorbents based on clay mineral particles with a particle size from 710
 .mu.m to 4 mm are known from EP-A-0 087 001, which represent compacted
 masses of particles of less than 2 mm. The clay mineral particles are
 joined together by water-soluble or water-dispersible substances, like
 cellulose derivatives, e.g., carboxymethylcellulose, or starches. Use of a
 cellulose-containing material not swellable in water is not described.
 Finally, a method is known from DE-A-43 11 488 (EP-A-0 619 140) for
 production of sorbents based on cellulose fibers, ground wood material and
 clay minerals, in which a finely divided cellulose-containing material
 with an average fiber length of 0.4 to 3 mm and residual moisture of 5 to
 15 wt % and/or a ground wood material with an average fiber length of 0.05
 to 2.0 mm and a residual moisture of 10 to 20 wt % and a smectitic clay
 mineral in finely divided form with an average particle size of 0.1 to 1.0
 mm, a residual moisture content of 5 to 15 wt % and a smectite content of
 at least 50 wt % are homogeneously mixed and the compacted mixture ground.
 Compaction occurs by means of pressing rolls (briquetting rolls or press
 granulation rolls). A relatively high percentage of finely divided
 material is formed during size reduction.
 It has now been found relative to the prior art just described that the
 properties of sorbents, especially litters, can be substantially improved
 if the components, essentially smectitic clay material(s) and finely
 divided cellulose-containing materials are compacted under high pressure
 at a precisely set water content, making sure that the percentage of
 finely divided material is kept as low as possible.
 The invention therefore concerns a method for production of sorbents based
 on cellulose-containing material and at least one swellable smectitic clay
 mineral, which form clumps on absorption of liquid; the method is
 characterized by the fact that
 (a) the cellulose-containing material and the smectitic clay material are
 thoroughly mixed in finely divided form, the total water content of the
 components being mixed lying between about 25 and 40 wt % or being
 adjusted to this range by adding water,
 (b) the mixture is compacted using a die press and
 (c) the compacted molded articles leaving the die press are cut essentially
 across the direction of emergence and dried.
 Cellulose-containing material is understood according to the invention to
 be a material that virtually does not swell in water and therefore has no
 binder properties either, in contrast to the cellulose derivatives
 described in EP-A-0 087 001.
 The sorbents produced according to the process of the invention are
 relatively light so that they can be better transported and handled by
 consumers. For example, a litter box can be easily filled and emptied. The
 sorbents so produced also exhibit excellent clump formation, in which the
 clumps to be disposed of have reduced weight; they do not form dust and
 have excellent absorption capacity. It is presumed, without being wedded
 to this theory, that the advantageous properties are attributed at least
 partially to particularly intimate bonding between the
 cellulose-containing material and the smectitic clay mineral.
 To achieve the advantages according to the invention it is important that
 the water content of the mixture lie in a very narrow range between about
 25 and 40 wt %, especially between 28 and 35 wt %. If the water content
 lies outside of this range, the properties of the obtained sorbent
 deteriorate and, for example, higher bulk density, poorer absorption
 properties or a deterioration in clump formation are obtained.
 For example, in comparison with compaction at low water content, at the
 water content according to the invention unduly severe compaction is
 prevented during molding since the water is scarcely compressible.
 Advantageous low bulk densities could therefore be achieved.
 A certain porosity can also be formed during subsequent drying of the
 composition, preferably to a residual water content of about 5 to 15 wt %,
 since cavities are formed during drying by evaporation of the water and
 shrinkage of the cellulose-containing materials, for example, wood fibers.
 This not only gives the advantage of low bulk density, but the cavities
 are then also available for absorption of liquids and gases so that the
 absorption properties of the sorbent are improved. Finally, the capillary
 effects occurring in the small cavities lead to more rapid absorption of
 liquid.
 The essential water content of the mixture according to the invention
 during molding can be present either already in the individual components,
 like the cellulose-containing material and the smectitie clay material(s),
 or be set before molding, preferably by addition of water or aqueous
 solutions. According to the second variant water is added to the dry
 mixture that contains the cellulose-containing material and the smectitic
 clay mineral(s) with a total water content of less than about 25 wt %
 until the total water content lies between about 25 and 40, especially
 between about 28 and 35 wt %. In the first variant a dry mixture is not
 started with, but moist starting materials are used instead so that
 addition of water before molding is unnecessary.
 It has surprisingly turned out that during molding with the mentioned water
 content a particularly favorable energy input to the mixture occurs.
 Shifting of the layers of smectitic clay mineral (delamellation) probably
 occurs, during which the water serves as mediating element during
 formation of the internal bonding during molding. Because of this,
 advantageous properties of the finished sorbent are obtained, like
 improved clump formation and reduced dust development. A lighter
 cellulose-containing material can also be used because of this so that a
 particularly low bulk density can be achieved without loss of the positive
 properties just mentioned.
 The mixture of cellulose-containing material and smectitic clay mineral
 according to the invention is compacted using a die press. Flat die
 presses and cylindrical die presses are distinguished here.
 A flat die press represents essentially a cylindrical vessel with a flat,
 perforated bottom plate against which one or more revolving rolls are
 pressed. Two rolls are preferably arranged over the bottom plate, rotating
 on the one hand, around an axis in the center of the cylindrical vessel
 and, on the other hand, on an axis perpendicular to this in the manner of
 an edge mill. The moist mixture of cellulose-containing material and
 smectitic clay mineral is compacted, on the one hand, in the gap between
 the perforated bottom plate and the rotating roll(s) and, on the other
 hand, during passage through the openings of the perforated bottom plate
 A cylindrical die press contains a perforated outer cylinder instead of the
 flat perforated bottom plate, in which at least one roll is situated that
 rotates around its axis and/or the axis of the outer cylinder and is
 pressed against the inside wall of the outer cylinder. The moist mixture
 of cellulose-containing material and smectitic clay minerals is compacted,
 on the one hand, in the gap between the perforated outer cylinder and the
 rotating roll(s) and, on the other hand, during passage through the
 openings of the outer cylinder. In another variant of the cylindrical die
 press the perforated outer cylinder rotates, while the roll(s) is (are)
 stationary in the interior of the outer cylinder.
 Elongated molded elements that are either cylindrical or polygonal,
 depending on the shape of the openings in the flat bottom plate or in the
 outer cylinder, are obtained with both the flat die presses and with the
 cylindrical die presses. The elongated molded elements are cut essentially
 across the direction of emergence, which can occur, for example, by means
 of a blade-like stripper arranged beneath the perforated bottom plate or
 on the outer wall of the perforated cylinder. In this manner it is not
 essential to break the molded elements after drying in a separate process
 step so that the percentage of fine fractions, especially dust-like
 fractions, can be reduced.
 Should these form to a limited degree, the ground and dried molded elements
 are freed of them (for example, by screening) and the separated fine
 fractions are optionally returned to the mixing stage.
 The energy input during press granulation should generally lie between
 about 3 and 9 kWh/t, especially between about 5 and 7 kWh/t.
 Use of a swellable smectitic clay mineral is of significance in order to
 achieve the full advantages according to the invention, since nonswellable
 clay materials, like kaolin, have low water absorption capacity and no
 clump formation occurs. Swellable minerals of the montmorillonite group
 can be used as smectitic clay mineral, like bentonite, or also hectorite,
 glauconite, sauconite, illite, etc. Mixtures of different clay minerals
 can also be used.
 According to a preferred variant one starts from a Ca and/or Na smectite,
 especially a Ca and/or Na bentonite with a water absorption capacity
 (referred to dry weight) of at least about 60%, preferably at least 120%,
 especially about 120 to 300% and a smectite content of about 50 to 95 wt
 %. In addition to smectite, the smectitic clay mineral can contain other
 accessory minerals, like mica, feldspar and quartz.
 According to another preferred variant, a mixture of calcium and sodium
 bentonite is used, since particularly advantageous properties of the
 sorbent can be set by the cooperation of these components. Such a mixture
 can be produced from calcium bentonite and natural sodium bentonite;
 however, it is also possible to convert calcium bentonite by activation
 with alkali (for example, sodium carbonate or other sodium salts)
 partially to sodium bentonite, in which case a very intimate mixture is
 obtained. Calcium bentonite has particularly rapid water absorption,
 whereas sodium bentonite has particularly high (although slower)
 absorption, but improves clump strength. The weight ratio between calcium
 and sodium bentonite is preferably about 2.5:7.5 to 7.5:2.5. Cooperation
 of these two components is further promoted by processing according to the
 invention and intimate bonding with the cellulose-containing material.
 The weight ratio between the finely divided cellulose-containing material
 and the smectitic clay material, preferably lies between about 1:9 and
 6.5:3.5, especially between about 3:7 and 6:4. Although, depending on the
 specific cellulose-containing materials and clay minerals employed in
 individual cases, weight ratios deviating from this can also be
 advantageous, excellent clump formation is achieved in the mentioned
 ranges.
 A finely ground pulp (native cellulose) and/or a cellulose material
 containing secondary fibers (for example paper fibers) is preferably used
 as cellulose-containing material, with an average fiber length of about
 0.1 to 2 mm, preferably about 0.3 to 0.8 mm. With particular preference
 wood flour and/or a material containing ground wood chips with an average
 particle size of about 0.1 to 2 mm, preferably about 0.1 to 1.0 mm is
 used. This type of material because of its resin content has a pleasant
 intrinsic odor. Mixtures of finely divided cellulose fiber-containing
 material and ground wood material can also be used.
 According to another preferred variant a limited amount of at least one
 hydrophilic binder, like starches, carboxymethylcellulose, polyacrylates,
 polyvinyl alcohol or polyvinylpyrrolidone, especially guar flour is added
 to the mixture of cellulose-containing material and smectitic clay
 material. The added amount preferably lies between 0.5 and 10 wt %.
 Addition of the hydrophilic binder has a positive effect on the properties
 of the sorbent produced according to the method of the invention, further
 intensifying bonding of the clay material to the cellulose-containing
 material. In the presence of a binder the percentage of
 cellulose-containing material in the sorbent can be further increased
 without losing the aforementioned advantageous properties. Thus, a lower
 bulk density is possible. The binder plays a dual function in the sorbent,
 reducing dust formation, on the one hand, and leading to improved clump
 formation, on the other.
 Optimization of the spreading properties can be achieved by the fact that
 the ground and dried molded elements have a size from about 0.1 to 10 mm,
 preferably from about 0.5 to 4 mm, the percentage of fraction from about
 0.5 to 2 mm being about 20 to 25 wt % and the percentage of fraction from
 2 to 4 mm being about 80 to 65 wt %.
 The size of the ground and dried molded element during use of a die press
 is dictated, on the one hand, by the size of the openings in the
 perforated bottom plate or in the perforated outer cylinder and, on the
 other hand, by the length of the molded element divided by means of the
 stripper. In this case breaking of the dried molded elements is no longer
 essential.
 The object of the invention is also a sorbent that can be obtained
 according to the method just described and forms clumps when moistened
 with liquids, characterized by a residual moisture of about 5 to 15,
 preferably about 5 to 10 wt %, and a water absorption capacity of at least
 about 100 wt %, preferably at least 120 wt % (referred to the agent dried
 to a residual moisture of 6 wt %). The clump formed during moistening with
 liquids (especially with aqueous liquids) is compact and can be fully and
 selectively removed from the sorbent without breaking with a slotted scoop
 (explained below).
 The hardness and strength of the clumps increase with residence time and
 degree of drying. The sorbent according to the invention does not form
 dust and exhibits excellent absorption properties.
 The sorbent according to the invention usually has a bulk density of about
 300 to 700 g/L, preferably about 400 to 600 g/L.
 The sorbent according to the invention can also be mixed with known
 sorbents. The known sorbent can also contain white pigments,
 disinfectants, fragrances and/or animal attractants, as well as other
 auxiliaries known in the prior art.
 The object of the invention is also a use of the aforementioned sorbent as
 a packing material, absorbent for liquids (like body fluids, urine, blood,
 sputum), oil, liquid chemicals, as well as litter for domestic animals,
 especially cat litter, for example in litter boxes.
 The properties of the sorbent according to the invention are generally
 determined as follows:
 1. Water absorption capacity
 According to a modification of method 17-A of Westinghouse, 20 g of
 granular sorbent is weighed into a weighed conical wire sieve with a
 diameter of 7 cm and a height of 7.6 cm.
 The filled sieve is then suspended in a beaker filled with water so that
 the material is fully covered with water. After an absorption time of 20
 minutes the sieve is suspended for another 20 minutes in an empty beaker
 for draining. After completion of the drainage time the sieve is weighed
 again with the contents. The water absorption capacity (%) corresponds to
 the equation 100.times.E/D, in which E is the amount of absorbed water and
 D is a weighed amount of the granular material.
 2. Water content
 A granulate sample is dried in a desiccator to constant weight; the content
 of adsorbed water is determined from the weight difference before and
 after drying. In particular, 10 to 20 g granulate is weighed into a flat
 dish to within 0.01 g and dried in a desiccator at 100.degree. C. to
 constant weight (at least 2 hours). The sample is then allowed to cool off
 in the desiccator to room temperature and weighed. The water content is
 calculated as follows:
EQU Water content (%)=[(Initial weight-Final weight)/Initial weight].times.100
 The water content of the cellulose-containing material with a smectitic
 clay mineral (100.degree. C.) can be determined accordingly.
 3. Absorption test
 Water is added from a 50 mL buret to a leveled and not compacted charge of
 granular sorbent in a glass dish (diameter 140 mm, height 75 mm, filling
 height 50 mm) and the penetration depth observed. The outlet of the buret
 is introduced at a height of 3 to 4 cm into the center of the charge,
 whereupon 60 mL of tap water is allowed to run out within 55 to 60
 seconds. After a waiting time of 3 minutes it is checked on the bottom of
 the dish whether water has passed through the layer; passage is
 recognizable by discoloration of the granular material on the bottom of
 the dish. Evaluation is carried out as follows:
 discoloration on bottom of dish not visible: test passed;
 discoloration on bottom of dish visible: test not passed.
 4. Clump formation
 The conical clump formed during the absorption test, which generally has a
 horizontal diameter of about 30 to 50 mm and a vertical dimension of about
 10 to 50 mm, is removed with a slotted scoop with a diamond-shaped pattern
 (dimensions of the scoop surface 80.times.120 mm; mesh width 11.times.11
 mm, crosspiece width 0.3 mm) and evaluated according to the following
 criteria:
 Solid clump:
 the clump can be fully removed with the slotted scoop and remains stable
 during and after removal;
 the clump exhibits plastic behavior and only breaks into larger fragments
 during stronger pressure between the fingers.
 Moderately strong clump:
 the clump is deformed during and after removal, but can be fully removed
 with the slotted scoop;
 the clump breaks down into smaller fragments during slight pressure between
 the figures.
 5. Bulk density
 A 500 mL graduated cylinder is first weighed while empty. A powder funnel
 with an opening of about 15 cm and an outlet opening of about 3 cm is
 placed on it and filled with the sorbent granulate within about 5 seconds.
 The powder funnel is then removed from the graduated cylinder so that the
 granulate in it forms a protruding cone. This is scraped off with a wide
 spatula along the rim of the graduated cylinder. The filled graduated
 cylinder is freed on the outside of adhering grains or dust and reweighed.
 The bulk density is calculated as follows:
EQU Bulk density (g/L)=2.times.net weight (g/500 mL)

The invention is explained by the following examples.
 EXAMPLE 1
 Comparison
 About 2 kg of a mixture consisting of 50 wt % ground wood flour (about 10
 wt % water, particle size about 0.5 mm) and 50 wt % of a ground mixture of
 20 wt % Ca bentonite and 30 wt % Na bentonite (water absorption capacity
 of the bentonite mixture about 200%) with a water content of about 12.5 wt
 % is set at a moisture content of 23.4 wt % by addition of water. The wood
 flour and bentonite mixture are intimately mixed and compacted in a flat
 die press from the Kahl Co. (type 14-175) by compression molding. This
 flat die press is an essentially cylindrical vessel with an inside
 diameter of about 20 cm with a perforated bottom plate (hole diameter 3
 mm), in which two rolls that rotate around the cylinder axis are provided.
 The rolls exert a pressure on the moist mixture of wood flour and
 bentonite mixture so that the moist mixture is forced through the
 perforated bottom plate. The energy input is about 6 kWh/t. The molded
 elements passing through the perforated plate are divided by a cutting
 device arranged beneath the perforated plate (stripper) across their
 longitudinal axis into pieces with a length of about 3 mm. Smaller
 fragments already appear during cutting. The obtained granulate is dried
 for about 6 hours at 80.degree. C. to a residual water content of 7.5 wt
 %, during which it already crumbles at limited pressure. The granulate is
 screened, the fine fraction (&lt;0.5 mm) amounting to about 30%.
 The other properties of the obtained granulate are shown in the table.
 EXAMPLE 2
 Comparison
 The working method of example 1 was repeated with the deviation that the
 water content of the wood flour-bentonite mixture was set at 40.3 wt %.
 The granulate was dried to a residual water content of 6.5 wt %. After
 drying and screening the fine fraction (&lt;0.5 mm) was less than 2 wt %.
 The other properties of the obtained granulate are shown in the table.
 EXAMPLE 3
 Invention
 The working method of example 1 was repeated with the deviation that the
 water content of the wood flour-bentonite mixture was set at 30.2 wt %
 before compaction. After drying the residual water content was 4.5 wt %.
 The other properties of the obtained granulate are shown in the table.
 EXAMPLE 4
 Invention
 The working method of example 3 was repeated with the deviation that 3 wt %
 guar flour was added to the moist wood flour-bentonite mixture before
 compaction. The water content before compaction was 30.9 wt %. After
 drying the granulate had a residual water content of 6.8%
 Other properties of the obtained granulate are shown in the table.
 EXAMPLE 5
 Invention
 The working method of example 3 was repeated with the deviation that
 cellulose fibers with an average fiber length of 1 mm and a water content
 of 35 wt % were used as cellulose-containing material. This material was
 intimately mixed with the same amount of bentonite mixture of example 1
 (water content 12.5 wt %) in a 1:1 ratio, during which water was added so
 that the water content of the mixture before compaction was 34.0 wt %.
 After drying the granulate had a residual water content of 5.8%.
 The other properties of the obtained granulate are shown in the table.
 TABLE
 Water content Water
 Fine
 Before After Bulk absorption
 fraction
 compaction drying density capacity Absorption
 (&lt;0.5 mm)
 Example (wt %) (wt %) (d/L) (wt %) test Clump
 formation (wt %)
 1 (comparison) 23.4 5.7 602 509 passed firm
 30
 2 (comparison) 40.3 6.5 481 319 did not pass
 moderately firm &lt;2
 3 (invention) 30.2 5.4 507 488 passed firm
 2
 4 (invention) 30.9 6.8 497 423 passed firm
 2
 5 (invention) 34.0 5.8 492 495 passed firm
 2
 The table shows a very high fine fraction of the sorbent according to
 comparative example 1, which is caused by the low water content before
 compaction. Otherwise this sorbent passed the absorption test and clump
 formation was satisfactory.
 The sorbent according to comparative example 2 because of its high water
 content before compaction had low water absorption capacity. Its fine
 fraction was relatively low, but it did not pass the absorption test. The
 clumps were also only moderately firm.
 The sorbent according to the examples 3 to 5 of the invention with a water
 content in the claimed range before compaction had a very low percentage
 of fines and passed both the absorption test and the clump formation test.
 They were also characterized by a high water absorption capacity.
 Comparative examples 1 and 2 also show that the use of a die press alone is
 not sufficient to achieve the objective of the invention, i.e., a
 combination of this feature with the feature of a specified water content
 before compaction matters.
 SUMMARY
 A method is described to produce sorbents based on cellulose-containing
 material and at least one swellable smectitic clay mineral, which form
 clumps on absorption of liquid. The method is characterized by the fact
 that (a) a cellulose-containing material and the smectitic clay mineral
 are intimately mixed in finely divided form, the total water content of
 the components being mixed lying between about 20 and 40 wt % or being set
 at this range by addition of water, (b) the mixture is compacted using a
 die press and (c) the compacted molded elements emerging from the die
 press are cut essentially across the direction of the emergence and dried.
 The invention also concerns a sorbent obtainable according to this method
 and its use.