Fabricating method for organic electro luminescence display device having a rib barrier of reverse taper shape and organic electro luminescence display device

This invention relates to a fabricating method of an organic electro luminescence display device that is adaptive for simplifying a process by forming a barrier rib by use of a new material, and an organic electro luminescence display device using the same.A fabricating method of an organic electro luminescence display device according to an embodiment of the present invention includes: forming an anode electrode on an upper substrate; depositing ZnO on the entire surface of the upper substrate and forming a ZnO film by making the deposited ZnO grow crystals; forming a barrier rib with a reverse taper shape that divides an area where the organic light emitting layer is to be formed on the upper substrate by patterning the ZnO film; forming an organic light emitting layer in the cell area that is divided by the barrier rib; and forming a cathode electrode on the organic light emitting layer.

This application claims the benefit of Korean Patent Application No. 2005-0133559, filed on Dec. 29, 2005, which is hereby incorporated by reference for all purposes as if fully set forth herein.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a fabricating method of an organic electro luminescence display device and an organic electro luminescence display device using the same, and more particularly to a fabricating method of an organic electro luminescence display device that simplifies its manufacturing process by forming a barrier rib by use of a new material, and an organic electro luminescence display device using the same.

2. Discussion of the Related Art

Recently, various flat panel display devices have been developed that have reduced weight and bulk to overcome the disadvantages of a cathode ray tube (CRT). Such flat panel display devices include a liquid crystal display (LCD), a field emission display (FED), a plasma display panel (hereinafter, referred to as ‘PDP’) and an organic electro luminescence (hereinafter, referred to as ‘EL’) display, etc.

Among them the PDP is simple in structure and fabrication process, thus the PDP is drawing attention as the most advantageous display device to be made in large sizes while being light and thin but there is a disadvantage in that its light emission efficiency and brightness are low and its power consumption is high. In comparison to this, an active matrix LCD having a thin film transistor (hereinafter, referred to as ‘TFT’) as a switching device uses a semiconductor process, thus it is difficult to make large LCDs due to manufacturing yield problems, and its power consumption is high due to a backlight unit. Further, the LCD has a disadvantage in that its viewing angle is narrow and there is a high light loss by optical devices such as a polarizing filter, a prism sheet, a diffusion plate, etc.

In comparison to this, the EL display device is generally divided into an inorganic EL display device and an organic EL display device in accordance with the type of material in a light emitting layer. The EL display is a self luminous device and has an advantage in that its response speed is fast, its light emission efficiency and brightness are high and its viewing angle is wide. An inorganic EL display device has higher power consumption than an organic EL display device, and the inorganic EL display device does not have high brightness and does not emit light with various colors of R (red), G (green) and B (blue). On the contrary, the organic EL display device is driven at a low DC voltage of several tens of volts, and the organic EL display device has a rapid response speed, has high brightness and can emit light with various colors of R, G, B, thus it is suitable for the next generation flat panel display device.

The organic EL display device includes sub-pixels arranged in an area defined by the crossing of gate lines and the data lines. The sub-pixel receives a data signal from the data line when a gate pulse is supplied to the gate line, and the sub-pixel emits light corresponding to the data signal, thereby displaying a picture.

The organic EL display device includes: an upper array substrate where an EL cell is formed; a lower array substrate where a drive TFT for driving the EL cell is formed; and a spacer that connects a cathode electrode of the EL cell to a drain electrode of the drive TFT.

Currently, the EL cell is formed to be separated by barrier ribs, and the barrier rib is formed in a reverse taper shape in order to divide the EL cell. The barrier ribs of the reverse taper shape effectively divide an organic light emitting layer of the EL cell and further make the cathode electrode separated by only the deposition of an electrode material without patterning. Accordingly, its yield is improved because the organic EL display device effectively separates the organic light emitting layer by the barrier ribs with the reverse taper shape, and its manufacturing cost is reduced because the cathode electrode is formed without being patterned.

Hereinafter, in reference toFIGS. 1A to 1C, a detailed description will be made for a method of forming the barrier ribs with the reverse taper shape of the organic EL display device as follows.

Referring toFIG. 1A, according to a fabricating method of a barrier rib8with a reverse taper shape in an organic EL display device of the related art, a silicon nitride SiN×18ais deposited on the entire surface of an upper substrate2, where a bus electrode5, an anode electrode4and an insulating film6are formed, at a temperature of not greater than 280° C.

Subsequently, a silicon nitride SiN×28bis deposited on the entire surface of the silicon nitride SiN×18athat is deposited on the entire surface at a temperature of not greater than 280° C., at a temperature greater than 350° C., as shown inFIG. 1B. And then, the silicon nitride8a,8bis patterned by a photolithography process and a dry etching process, thereby forming the barrier rib8with an upright taper in a lower part and a reverse taper in an upper part, as shown inFIG. 1C.

Herein, the silicon nitride has a characteristic of being differently etched during the dry etching process in accordance with the deposit temperature. To describe this in detail, the silicon nitride deposited at the temperature of not greater than 280° C. is etched with an upright taper shape by the dry etching process, and the silicon nitride deposited at the temperature greater than 350° C. is etched in the reverse taper shape by the dry etching process. Accordingly, the barrier rib8of the organic EL display device of the related art deposits the silicon nitride at different temperatures, and thus, by use of the characteristic of the silicon nitride it is possible to form the barrier rib8having an upright taper shape in the lower part and the reverse taper shape in the upper part.

However, the fabricating method of the organic EL display device of the related art has a characteristic that the silicon nitride SiN×2 deposited at the temperature greater than 350° C. is etched to have a large reverse taper, as shown inFIG. 2, by the dry etching process. Due to this, the fabricating method of the organic EL display device of the related art produces a phenomenon where an area where the organic light emitting layer10can be formed is hidden by the big reverse taper and should form the barrier rib8with a height higher than a height by which the organic light emitting layer10is filled.

Accordingly, the fabricating method of the organic EL display device of the related art lowers the thickness of the silicon nitride deposited at the temperature greater than 350° C. in order to reduce the height of the barrier rib SiN×28bwith the reverse taper shape, thereby reducing the phenomenon that the area where the organic light emitting layer10can be formed is hidden by the barrier rib8bwith the reverse taper shape. The fabricating method forms the barrier rib8awith the upright taper by depositing the silicon nitride at the temperature of not greater than 280° C. in the lower part of the barrier rib8bwith the reverse taper, thereby forming the barrier rib8at the height by which the organic light emitting layer10can be filled.

Accordingly, the fabricating method of the organic EL display device of the related art deposits an inorganic material such as the silicon nitride at deposition temperatures that are different from each other, thus the barrier rib8awith the upright taper shape is formed at the lower part and the barrier rib8bwith the reverse taper shape is formed at the upper part, thus there is a disadvantage that the number of processes for forming the barrier rib8with the reverse taper shape is increased because the barrier rib8is formed in double layer.

Also, according to the related art, if the silicon nitride deposited on a substrate in single layer, for example, at the temperature greater than 350° C., then patterned by a dry etching process to form a barrier rib, the barrier rib is formed in an upright taper by the characteristic of the dry etching process. So, according to the related art, a barrier rib with a reverse taper can not be achieved in single layer using a silicon nitride.

According to another related art, a barrier rib can be formed by depositing photosensitive organic material on a substrate and pattering it with a photolithography process. However, as the barrier rib formed by organic material is easily contaminated, therefore it decreases processing yield and causes a break in electrodes of an organic electro luminescence display frequently.

SUMMARY OF THE INVENTION

Accordingly, the present invention is directed to a fabricating method for an organic electro luminescence display device and organic electro luminescence display device using the same that substantially obviates one or more of the problems due to limitations and disadvantages of the related art.

An advantage of the present invention is to provide a fabricating method of an organic electro luminescence display device that simplifies a process by forming a barrier rib by use of a new material, and an organic electro luminescence display device using the same.

In order to achieve these and other advantages and in accordance with the purpose of the present invention, as embodied and broadly described, a fabricating method of an organic electro luminescence display device according to an aspect of the present invention includes: forming an anode electrode on an upper substrate; depositing ZnO on the entire surface of the upper substrate and forming a ZnO film by making the deposited ZnO grow crystals; forming a barrier rib with a reverse taper shape that divides an area where the organic light emitting layer is to be formed on the upper substrate by patterning the ZnO film; forming an organic light emitting layer in the cell area that is divided by the barrier rib; and forming a cathode electrode on the organic light emitting layer.

In another aspect of the present invention, an organic electro luminescence display device according to another aspect of the present invention includes an anode electrode on an upper substrate; a ZnO barrier rib with a reverse taper shape which divides a cell area where an organic light emitting layer is to be formed on the upper substrate; an organic light emitting layer in the cell area; and a cathode electrode on the organic light emitting layer.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

With reference toFIGS. 3 to 6, embodiments of the present invention will be explained as follows.

FIG. 3is a cross sectional diagram representing an organic EL display device according to an embodiment of the present invention.

Referring toFIG. 3, an organic EL display device according to the embodiment of the present invention includes an upper array substrate101where an EL cell is formed; a lower array substrate121where a drive TFT T2for driving the EL cell is formed; and a spacer150which connects a cathode electrode112of the EL cell to a drain electrode128of the drive TFT T2.

The upper array substrate101includes: an EL cell including of an anode electrode104and a cathode electrode112that have an organic light emitting layer110formed therebetween on an upper substrate102and are insulated by an insulating film106; a barrier rib108for separating the EL cell; and a bus electrode105formed under the anode electrode104for compensating a high resistance of the anode electrode104. The organic EL display device includes the spacer150for connecting the cathode electrode112of the upper array substrate101to the drain electrode128of the drive TFT T2of the lower array substrate121.

In the upper array substrate101, the anode electrode104is formed by having a transparent conductive material such as ITO (indium tin oxide), etc deposited on the upper substrate102. A drive signal for emitting holes from a voltage supply source (VDD) is supplied to the anode electrode104.

A bus electrode105is formed to define an area where the organic light emitting layer110is to be formed and is connected to the anode electrode104to compensate for a high resistance of the anode electrode104.

The cathode electrode112is formed at an EL cell area divided by the barrier rib108. A drive signal for emitting electrons is supplied to the cathode electrode112through a drive TFT T2. At this moment, the cathode electrode112is formed to encompass the spacer150and is connected to a drain electrode128of the drive TFT T2on the lower array substrate121.

The barrier rib108is formed with a reverse taper shape by patterning ZnO by a wet etching process after depositing the ZnO on the upper substrate102at a high temperature. The barrier rib108is formed to expose an area where the organic light emitting layer110is to be formed so as to divide the EL cell area and is formed in a reverse taper shape, thereby separating the cathode electrode112without patterning when forming the cathode electrode112.

The organic light emitting layer110is formed by having a hole injection layer, a hole transport layer, a light emitting layer, an electron transport layer and an electron injection layer deposited. In the organic light emitting layer110, if the drive signal is supplied to the anode electrode104and the cathode electrode112, the holes and electrons emitted from the anode electrode104and the cathode electrode112are re-combined within the light emitting layer, thereby generating a visible ray. At this moment, the generated visible ray exits the light emitting layer110through the transparent anode electrode104thus the organic EL display device displays a designated picture or image.

The spacer150is formed on the upper substrate102that overlaps the drain electrode128of the drive TFT T2on the lower array substrate121to connect the drain electrode128of the drive TFT T2of the lower array substrate121to the cathode electrode112of the EL cell.

The lower array substrate121includes a switch TFT (T1); and a drive TFT T2of which a gate electrode124is connected to the drain electrode of the switch TFT.

In the lower array substrate121, a gate electrode of the switch TFT is connected to the gate line and a source electrode is connected to the data line and the drain electrode is connected to the gate electrode124of the drive TFT T2.

The gate electrode124of the drive TFT T2is formed on the lower substrate122together with the gate line, and the drive TFT T2includes a semiconductor layer138overlapped with the gate electrode124of the drive TFT T2with the gate insulating film136; a source electrode126and a drain electrode128of the drive TFT T2that are formed together with the data line, having the semiconductor layer138therebetween. The source electrode126of the drive TFT T2is connected to a ground voltage source (GND) and the drain electrode128of the drive TFT T2is connected to the cathode electrode of the upper array substrate101. The drain electrode128of the drive TFT T2is connected to the cathode electrode112of the upper array substrate101through a contact electrode132that is exposed on a passivation film130through a drain contact hole134which penetrates the passivation film130.

Hereinafter, in reference toFIGS. 4A to 4F, a fabricating method of an organic EL display device according to an embodiment of the present invention will be explained in detail as follows.

Referring toFIG. 4A, first, a bus electrode105is formed by patterning a metal material, for example molybdenum Mo or chrome Cr, after depositing the metal material on the upper substrate102.

Subsequently, a transparent conductive material such as ITO, etc. is patterned after being deposited on the entire surface of the upper substrate102, thereby forming the anode electrode104, as shown inFIG. 4B.

Then, an insulating material is patterned after being deposited on the entire surface of the upper substrate102, thereby forming an insulating film106that exposes an area where the organic light emitting layer110is to be formed on the anode electrode104, as shown inFIG. 4C.

After this, ZnO is deposited on the entire surface of upper substrate102where the insulating film106is formed, at a high temperature greater than about 150° C., and then the ZnO is patterned by a wet etching process, thereby forming a barrier rib108with a reverse taper shape, as shown inFIG. 4D.

Herein, a fabricating method of an organic EL display device may form the barrier rib108in a reverse taper shape by use of a crystal growing characteristic of the ZnO film in accordance with the temperature at which the ZnO is deposited.

To describe this in detail, the ZnO film grows crystals in a shape as shown inFIG. 5when deposited at a temperature greater than about 150° C. That is to say, the ZnO film deposited at the temperature of greater than about 150° C. is crystallized in a structure where the distribution of the crystalline ZnO film is high in the upper part, the crystalline ZnO film and an amorphous ZnO film are mixed in the middle part, and the distribution of the amorphous ZnO film is high in the lower part.

Accordingly, the fabricating method of the organic EL display device according to the present invention deposits the ZnO at a temperature greater than about 150° C., makes the ZnO grow, and then patterns the ZnO film by the wet etching process by use of a physical characteristic where the amorphous film is over-etched in the wet etching process in comparison to the crystalline film, thereby forming the barrier rib108with a reverse taper shape, as shown inFIG. 6.

As a depositing process, for example, Pulsed Laser Deposition PLD, RF sputtering, Chemical Vapor Deposition CVD, Plasma Enhanced Chemical Vapor Deposition PECVD, Metal Organic Chemical Vapor Deposition MOCVD, magnetron sputtering, Molecular Beam Epitaxy MBE or Ion Beam Sputtering can be used. By using such a depositing process, ZnO can be deposited at a temperature from a room temperature (about 20° C.) to about 600° C. Especially, if the ZnO is deposited at a temperature greater than about 150° C., the ZnO film can be formed well in a structure where the upper part is mainly composed of the crystalline ZnO film and the lower part is mainly composed of the amorphous ZnO film.

Subsequently, an insulating material is patterned after being spread over the entire surface of the upper substrate102where the barrier rib108with the reverse taper shape is formed, thereby forming the spacer150in an area which overlaps with the drain electrode128of the drive TFT of the lower array substrate121, as shown inFIG. 4E.

An organic light emitting material is next deposited in the EL cell area by use of a mask to form the organic light emitting layer110, and then the cathode electrode112is formed in the EL cell area, as shown inFIG. 4F, by depositing an electrode material on the entire surface and by being separated by the barrier rib108with the reverse taper shape. Next, the cathode electrode112is formed to encompass the spacer150to be connected to the drain electrode128of the drive TFT of the lower array substrate121after bonding the upper array substrate101and the lower array substrate121together.

In this way, the fabricating method of the organic EL display device when depositing the ZnO at the temperature greater than about 150° C., patterns the ZnO film by use of the characteristic of the ZnO film that the distribution of the crystalline film is high in the upper part of the deposited ZnO film and the distribution of the amorphous film is high in the lower part and the physical characteristic that the amorphous film is over-etched during the wet etching process in comparison with the crystalline film, thereby forming the barrier rib108with the reverse taper shape. Accordingly, the fabricating method of the organic EL display device according to the present invention may reduce the number of processes by replacing the process where the silicon nitride is deposited at different temperatures in order to form the barrier rib with the reverse taper shape of the related art.

As described above, the fabricating method of the organic electro luminescence display device according to the embodiment of the present invention forms the barrier rib with the reverse taper shape by depositing the ZnO at the temperature greater than about 150° C. and etching the ZnO by a wet etching process. Accordingly, the fabricating method of the organic EL display device according to the present invention replaces the process of depositing the silicon nitride at different temperatures in order to form the barrier rib of the reverse taper shape of the related art, thereby being able to reduce the number of processes.