Semiconductor device with vertical gate and method of manufacturing the same

A gate electrode is formed in a trench reaching a drain region so as to leave a concave portion on the top of the trench. A first insulating film is formed, which fills the concave portion and of which the thickness increases as the distance from an end of the trench increases on the substrate surface on both sides of the trench. First and second source regions are formed in a self-alignment manner by introduction of impurities through the first insulating film.

This application is a U.S. national phase application of PCT international application PCT/JP2012/002382 filed on Apr. 5, 2012, which claims priority to Japanese Patent Application No. 2011-094415 filed on Apr. 20, 2011. The disclosures of these applications including the specifications, the drawings, and the claims are hereby incorporated by reference in its entirety.

BACKGROUND

1. Technical Field

The present invention relates to a semiconductor device with vertical gate having a vertical gate electrode and a method of manufacturing the semiconductor device with vertical gate.

2. Description of the Related Art

With recent requirements for a decrease in power consumption, an improvement in functional performance, and an increase in operation speed in electronic apparatuses, a decrease in power consumption and an increase in operation speed have been also required in semiconductor devices built therein. In order to cope with these requirements, it is necessary to reduce on-resistance of semiconductor devices such as power MOS (Metal Oxide Semiconductor) transistors used in a DC-DC converter or the like of the electronic apparatuses.

Such a type of power semiconductor device employs a vertical-gate structure in which a gate electrode of a semiconductor device is arranged in a direction (hereinafter, referred to as a vertical direction) perpendicular to a principal surface of a semiconductor substrate. For example, in a vertical-gate MOS transistor, a source region on the top of the gate electrode arranged in the vertical direction, a body region in an intermediate portion of the gate electrode, and a drain region on the bottom of the gate electrode are arranged to face each other. In order to further reduce the on-resistance of such a semiconductor device with vertical gate, it is necessary to raise the density of unit cells per unit area.

In the vertical-gate MOS transistor, a source region and a body contact region are formed in the surface of a semiconductor substrate adjacent to the gate electrode. A source electrode electrically connected to the source region and the body contact region is formed on the surface of the semiconductor substrate. An insulating film electrically isolating the gate electrode and the source electrode is formed on the top surface of the gate electrode. In this structure, when the insulating film on the gate electrode protrudes from the surface of the semiconductor substrate and when the vertical gate electrodes are arranged with a small pitch to raise the density of unit cells per unit area, the insulating films get close to each other to form concave portions. These concave portions cause a problem in that voids are formed in the source electrodes embedded in the concave portions, or the like.

As a countermeasure, for example, Unexamined Japanese Patent Publication No. 2005-209807 proposes a technique of forming the top surface of an insulating film on a vertical gate electrode and the surface of a silicon substrate in which a source region exists to form the same plane (including substantially the same plane) in a semiconductor device with vertical gate having plural vertical gate electrodes arranged in parallel. In this technique, the top surface of the vertical gate electrode retreats downward from the surface of the silicon substrate and the source region is then formed on the surface of the silicon substrate. The insulating film is formed on the vertical gate electrode and then a body contact region is formed using a mask patterning (lithography technique). Other examples of such a technique are disclosed in Unexamined Japanese Patent Publication No. 2007-500454 and Japanese Patent No. 4,545,679.

SUMMARY

However, in the semiconductor device with vertical gate disclosed in Unexamined Japanese Patent Publication No. 2005-209807, Unexamined Japanese Patent Publication No. 2007-500454 and Japanese Patent No. 4,545,679, when the gap between the neighboring gate electrodes needs to be further reduced with requirements for a decrease in size, it is necessary to secure a margin of mask superposition shift for used masks and thus the decrease in gate electrode pitch is limited.

The present invention provides a semiconductor device with vertical gate which can stably form a source region even for a small gate electrode pitch without considering mask superposition shift and a method of manufacturing the semiconductor device with vertical gate.

The present invention employs the following technical means. That is, according to an aspect of the present invention, there is provided a method of manufacturing a semiconductor device with vertical gate, including the steps of: (a) forming a drain region of a first conductivity type on a semiconductor substrate; (b) forming a first body region of a second conductivity type, which is opposite to the first conductivity type, on the drain region; (c) forming a trench penetrating the first body region and reaching the drain region; (d) forming a gate electrode in the trench so as to leave a concave portion on the top of the trench after the step of (c); (e) forming a first insulating film that is formed in the concave portion and that has a portion in which a thickness increases with an increase in distance from an end of the trench in the first body region on both sides of the trench after the step of (d); and (f) forming a first source region of the first conductivity type, which is disposed along the trench and which is adjacent to the trench and the top of the gate electrode, by introduction of impurities through the first insulating film after the step of (e).

By employing the method of manufacturing a semiconductor device with vertical gate according to this aspect, it is possible to form the source region without using a lithography technique. Accordingly, it is not necessary to secure a margin of mask superposition shift and it is possible to further reduce the gate electrode pitch, compared with the conventional technique. As a result, it is possible to implement a semiconductor device with vertical gate with smaller on-resistance. The first source region may be formed in a self-alignment manner by introduction of impurities through the etched-back first insulating film, instead of the introduction of impurities through the non-etched-back first insulating film.

According to another aspect of the present invention, the present invention provides a semiconductor device with vertical gate. That is, there is provided a semiconductor device with vertical gate including: a drain region of a first conductivity type that is disposed in a semiconductor substrate; a first body region of a second conductivity type that is disposed on the drain region and that has a conductivity type opposite to the first conductivity type; a trench that penetrates the first body region and that reaches the drain region; a gate electrode that is formed in the trench in a state where a top surface of the gate electrode is located at a position lower than the top end of the trench; a source region of the first conductivity type that is formed on the surface of the first body region along the trench so as to be adjacent to the trench; a first insulating film that is formed in the trench on the gate electrode; a second insulating film that is formed on the first insulating film; and a conductive film that electrically connects the source region and the body region to each other, wherein the first insulating film has a concave portion and the second insulating film is disposed to fill the concave portion.

An embedded insulating film including the first insulating film and the second insulating film may include, for example, the same type of impurities as in the second source region at least in the bottom portion and includes the same type of impurities as in the second body region at least in the top portion.

By employing the semiconductor device with vertical gate according to this aspect, it is possible to form the source region without using a lithography technique. Accordingly, it is not necessary to secure a margin of mask superposition shift and it is possible to further reduce the gate electrode pitch, compared with the conventional technique. As a result, it is possible to implement a semiconductor device with vertical gate with smaller on-resistance. In the semiconductor device with vertical gate, the interface between the source region and the first body region may be formed in a planar shape inclined with respect to the side wall of the trench.

According to the aspects of the present invention, since the first and second source regions as the source region can be formed in a self-alignment manner without using a lithography technique, it is possible to further reduce the gate electrode pitch, compared with the conventional technique. As a result, it is possible to implement a semiconductor device with vertical gate with smaller on-resistance at a low cost.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

Hereinafter, a semiconductor device according to an exemplary embodiment of the present invention along with a method of manufacturing the semiconductor device will be described with reference to the accompanying drawings. In the following exemplary embodiment, the present invention is embodied by an N-channel vertical-gate transistor. In this example, a first conductivity type mentioned in the present invention is an N type and a second conductivity type is a P type. The following description can be similarly applied to a P-channel vertical-gate transistor by inverting the conductivity types of impurity regions in the elements.

FIG. 1is a diagram schematically illustrating the configuration of a semiconductor device according to an exemplary embodiment of the present invention. InFIG. 1, a source electrode and a structure thereon are not shown.FIG. 1is a schematic diagram and the dimensional ratio of constituents is not limited to one shown in the drawing.

As shown inFIG. 1, the semiconductor device with vertical gate according to this exemplary embodiment includes N-type silicon substrate1which is a semiconductor substrate and drain region2including an N-type epitaxial silicon layer formed on N-type silicon substrate1. The impurity concentration of drain region2is set to be lower than the impurity concentration of silicon substrate1. Body region3(first body region) including a P-type impurity region with a relatively-low concentration is formed on drain region2.

In the surface portion of a substrate including N-type silicon substrate1, drain region2, and body region3, plural trenches6penetrating body region3and reaching drain region2are disposed in parallel. Gate electrode12formed of polysilicon is embedded in each trench6with gate insulating film8, which is formed of a silicon oxide film, interposed therebetween. The top surface of each gate electrode12is lower than the top end of each trench6. In this example, each trench6has a width of about 0.18 μm and a depth of about 0.8 μm. Trenches6are arranged with a pitch of 0.6 μm.

Source region17formed of an N-type impurity region is formed in the surface portion of the substrate (the surface portion of body region3) adjacent to each trench6. Source region17includes first source region15and second source region16and is disposed along trench6so as to be adjacent to the top of gate electrode12and trench6.

First source region15is configured such that the width of the impurity region in the direction perpendicular to the side wall of trench6decreases with an increase in distance from the surface in the depth direction of trench6, and is disposed up to the depth position adjacent to the top of gate electrode12. Second source region16is disposed on first source region15along trench6. Second source region16has an impurity concentration higher than that of first source region15. As shown inFIG. 1, second source region16is formed on the side wall of trench6above the top of gate electrode12. More specifically, second source region16is exposed from a region (hereinafter, referred to as an upper side wall portion) extending from the top of trench6by a predetermined depth and a region extending from an end of trench6by a predetermined distance in the substrate surface. Hereinafter, the region in which second source region16is formed is referred to as a top corner portion of trench6.

Body contact region21(second body region) which is adjacent to source region17(second source region16in the example shown inFIG. 1) and which is formed of a P-type impurity region along source region17is disposed in the surface portion of body region3. Body contact region21has an impurity concentration higher than that of body region3and is electrically connected to body region3.

Source region17and body contact region21are electrically connected to each other by a conductive film (not shown) formed on the top surface thereof.

For example, body region3has an impurity concentration of about 1.5×1017cm−3and is intended to control a threshold value of a channel region formed along the side wall of trench6. Body contact region21has an impurity concentration of about 1.0×1020cm−3and is intended to constitute an ohmic contact with the conductive film. First source region15has an impurity concentration of about 2.0×1020cm−3and constitutes a source region of a transistor. Second source region16has an impurity concentration of about 1.0×1021cm−3and is intended to constitute an ohmic contact with the conductive film.

Embedded insulating film19is formed in trench6on gate electrode12. Embedded insulating film19has a function of electrically separating the conductive film, which connects source region17and body contact region21, from gate electrode12. In the semiconductor device with vertical gate according to this exemplary embodiment, embedded insulating film19includes the same type of impurities as the N-type impurities constituting second source region16at least in the lower portion thereof. Embedded insulating film19includes the same type of impurities as the P-type impurities constituting body contact region21at least in the upper portion thereof.

FIGS. 2 to 19are cross-sectional process views illustrating processes of forming the semiconductor device with vertical gate having the above-mentioned structure. InFIGS. 2 to 19, a transistor formation region is shown on the left side and a peripheral region (transistor non-forming region) of the transistor forming region in which interconnections such as a gate drawing interconnection are formed is shown in on the right side. Similarly toFIG. 1,FIGS. 2 to 19are schematic diagrams and dimensional ratios of constituent parts are not limited to the drawings. Hereinafter, if a thin film is formed on a top surface, it is mentioned that a film is formed on a substrate.

As shown inFIG. 2, first, an N-type epitaxial silicon layer is formed on N-type silicon substrate1through an epitaxial growth method. P-type impurities are introduced into the surface portion of the epitaxial silicon layer to form N-type drain region2and P-type body region3on N-type silicon substrate1. For example, the thickness of drain region2can be set to a range of 1 μm to 20 μm and the thickness of body region3can be set to a range of 0.5 μm to 2 μm. Drain region2and body region3may be formed through an epitaxial growth method.

Subsequently, silicon oxide film4with a thickness of 50 nm to 500 nm is formed on the surface of body region3through a thermal oxidation method. As shown inFIG. 3, resist pattern5having an opening in the region in which trench6is formed in the subsequent processes is formed on silicon oxide film4through a known lithography technique. Then, as shown inFIG. 3, silicon oxide film4in the region in which trench6is formed through an etching process using resist pattern5as a mask.

After resist pattern5is removed, as shown inFIG. 4, trench6with a depth of 0.5 μm to 3 μm penetrating body region3and reaching drain region2is formed through a dry etching process using patterned silicon oxide film4as a mask. The width of trench6can be set to a range of 0.15 μm to 0.5 μm and the pitch thereof can be set to a range of 0.4 μm to 1.5 μm.

As shown inFIG. 5, silicon oxide film7with a thickness of about 15 nm to 100 nm is formed on the inner surface of each trench6through a thermal oxidation method. Silicon oxide film7is removed through a wet etching process or the like, as shown inFIG. 6. In this way, by removing silicon oxide film7temporarily formed thereafter, damage of the inner surface of trench6due to the dry etching process can be removed. When removing silicon oxide film7, silicon oxide film4on the substrate surface is also etched. In this exemplary embodiment, the thickness of silicon oxide film4is set such that a part of silicon oxide film4remains even after etching silicon oxide film7.

Subsequently, as shown inFIG. 7, gate insulating film8with a thickness of 8 nm to 100 nm is formed on the inner surface of each trench6. Although not particularly limited, a silicon oxide film is formed as gate insulating film8through a thermal oxidation method herein.

Thereafter, as shown inFIG. 8, conductive polysilicon film9with a thickness of 200 nm to 800 nm serving as a material of the gate electrode is deposited on the entire surface. A polysilicon film given conductivity can be used as polysilicon film9. For example, a doped polysilicon film doped with impurities such as phosphorous can be formed through a CVD (Chemical Vapor Deposition) method. Otherwise, the polysilicon film may be formed by forming a non-doped polysilicon film and then performing an N-type impurity ion implanting process and an annealing process.

Subsequently, as shown inFIG. 9, resist pattern11covering a polysilicon interconnection forming region of a gate drawing interconnection or the like is formed. Then, as shown inFIG. 10, polysilicon film9on silicon oxide film4and trench6is removed by etching polysilicon film9using resist pattern11as a mask. Through this etching, polysilicon film9is removed such that the top surface of the polysilicon film in trench6is located lower by 100 nm to 500 nm than the surface of silicon oxide film4. Accordingly, gate electrode12is formed in trench6in a state where a concave portion remains in the upper portion of trench6. At the same time, polysilicon interconnection13is formed in the transistor non-forming region. Here, polysilicon interconnection13constitutes a gate drawing interconnection connected to gate electrode12in trench6, for example, at an end in the length direction of trench6.

After resist pattern11is removed, as shown inFIG. 11, first insulating film14is formed on the substrate. First insulating film14fills the concave portion on gate electrode12and has a portion of which the thickness increases with an increase in distance from an end of trench6on the substrate surface on both sides of trench6. First insulating film14has only to be formed in the concave portion on gate electrode12but does not have to fully fill the concave portion. The thickness-increasing portion of first insulating film14preferably has a forward tapered shape with a slope of which the angle with respect to the substrate surface is in a range of 30° to 60°. This is intended to excellently form first source region15having a structure which is deep in the vicinity of the upper side wall of trench6to be formed in the subsequent processes and which becomes shallower with an increase in distance in the horizontal direction from the top of trench6. When the angle of the thickness-increasing portion of first insulating film14with respect to the substrate surface is smaller than 30°, an N-type impurity region with a relatively-high concentration is formed in the central part between adjacent trenches6. When the angle of the thickness-increasing portion of first insulating film14with respect to the substrate surface is larger than 60°, the width of the source region in the horizontal direction decreases and thus the contact resistance with the source electrode increases.

First insulating film14can be deposited in a state where high-frequency power is applied to the substrate, for example, through the use of an HDP-CVD (High Density Plasma-CVD) method. When forming a film using the HDP-CVD method, the deposition of a film and the sputter-etching of the film (Ar sputtering) are performed at the same time. The efficiency of the sputter-etching depends on an incidence angle of particles on the film and an etching rate on an inclined surface of which the angle with respect to the substrate surface is about 50° is high. In the sputter-etching, the etching rate on the vertical surface (90°) such as the side wall of trench6or the flat surface (0°) of the substrate is low. As a result, as shown inFIG. 11, first insulating film14having the thickness-increasing portion of a forward tapered shape can be formed well. The relationship (strength) between the deposition of a film and the sputter-etching during formation of the film can be also changed by adjusting the flow rate of source gas introduced at the time of depositing first insulating film14and high-frequency power to be applied at the time of the deposition. Here, since the etching efficiency has the above-mentioned tendency, the angle formed by the inclined surface and the substrate surface converges on 50° with the elapse of process time.

In forming a film using the HDP-CVD, the thickness of first insulating film14can be set to the same degree as the depth (the distance from the substrate surface to the surface of the gate electrode) of the concave portion on gate electrode12or a thickness lower than the top of trench6. By employing this configuration, the inclined surface (the top surface of the thickness-increasing portion) can be brought in contact with the top of trench6or can be disposed in the vicinity of the top of trench6. Accordingly, first source region15can be formed well in the subsequent process. In this exemplary embodiment, since the depth of the concave portion on gate electrode12is in the range of about 100 nm to 500 nm, the thickness of first insulating film14can be set to a range of 100 nm to 500 nm. Although particularly limited, a silicon oxide film is deposited as first insulating film14in this exemplary embodiment.

Subsequently, as shown inFIG. 12, by introducing N-type impurities using first insulating film14and silicon oxide film4formed in this way as a mask, first source region15is formed. The introduction of impurities can be carried out by ion implantation. In the ion implantation, it is preferable that impurities be incident perpendicularly on the substrate. At this time, an acceleration voltage of the ion implantation preferably employs an acceleration voltage with which the impurities do not penetrate a large-thickness portion of first insulating film14and silicon oxide film4below the large-thickness portion and an acceleration voltage with which the impurities are introduced into the region adjacent to the top of gate electrode12in the vicinity of the side wall of trench6. The large-thickness portion of first insulating film14means a portion of first insulating film14, which is formed on the flat substrate surface between trench6and adjacent trench6without an influence of trench6. The thickness of the large-thickness portion is substantially equal to the thickness of first insulating film14deposited in a portion of which the top surface is a horizontal surface parallel to the semiconductor substrate.

For example, a case where the top surface of gate electrode12is located lower by 250 nm than the substrate surface and first insulating film14of which the thickness of the large-thickness portion is 180 nm is deposited on the substrate will be described below. First, ion implantation through first insulating film14is performed using phosphorous as N-type impurities. When implantation energy is set to 70 KeV and implantation dose is set to 8.0×1015cm−2, the projected range Rp of phosphorous ions in the silicon oxide film is 0.0688 μm and the variance σ is 0.0283 μm. That is, Rp+3σ=0.1537 μm and phosphorous ions hardly reach body region3just below the large-thickness portion of first insulating film14with a thickness of 180 nm. On the other hand, in the thickness-increasing portion of first insulating film14, more phosphorous ions than those of a small-thickness portion reach body region3just below. As a result, first source region15is formed which has a structure which is deep in the vicinity of the side wall of trench6and which becomes shallower with an increase in distance from the top of trench6in the horizontal direction. More strictly, in a portion with a very small thickness of first insulating film14in the vicinity of the side wall of trench6, the impurity concentration profile in the depth direction of first source region15exhibits a Gaussian distribution having a peak at a position lower than the substrate surface. The peak depth is a depth based on the projected range of impurity ions in the silicon substrate. Since first insulating film14slowly increases with an increase in distance from the top of trench6in the horizontal direction, the peak depth of the impurity concentration profile in the depth direction of first source region15gradually becomes shallower and the peak concentration thereof becomes smaller. That is, in the substrate surface, an impurity concentration profile in which the impurity concentration slowly decreases with an increase in distance from the top of trench6in the horizontal direction is exhibited. That is, in first source region15, the width of the impurity region in the direction perpendicular to the side wall of trench6decreases with an increase in distance from the substrate surface in the depth direction of trench6and the impurity concentration increases with a decrease in distance from the top of the side wall of trench6.

In this case, the interface between first source region15and body region3has a planar shape inclined with respect to the side wall of trench6. Since impurities introduced into the silicon substrate diffuse at the time of activation annealing, the impurity concentration distribution after the activation annealing is not strictly matched with the impurity concentration distribution just after the ion implantation. Here, the “planar shape inclined with respect to the side wall of trench6” means that the impurity concentration distribution just after the ion implantation of first source region15is the impurity concentration distribution reflecting the shape of the thickness-increasing portion of first insulating film14having an inclined planar shape.

When the ion implantation of phosphorous is completed, as shown inFIG. 13, a stacked film including silicon oxide film4and first insulating film14is etched back to expose the corners of the top of trench6. At this time, the amount of etched-back film can be set to a range of 20 nm to 100 nm. Although not particularly limited, the amount of etched-back film is set to about ⅓ of the stacked thickness of silicon oxide film4and first insulating film14in this exemplary embodiment. For example, when each trench6has a width of 0.18 μm, the trenches are arranged with a pitch of 0.6 μm, and the thickness of the stacked film including silicon oxide film4and first insulating film14is 250 nm, the amount of etched-back film is about 80 nm. At this time, the exposed width of the substrate surface in the horizontal direction from an end of trench6is about 0.1 μm. Any of a dry etching process and a wet etching process may be used for the etching-back.

As shown inFIG. 14, second source region16is formed by introducing N-type impurities using the etched-back stacked film of silicon oxide film4and first insulating film14as a mask. The introduction of impurities can be carried out by ion implantation. In the ion implantation, the impurities are preferably incident perpendicularly on the substrate. Here, by carrying out the ion implantation using arsenic as N-type impurities, second source region16is formed. When the ion implantation is carried out with implantation energy 50 KeV and implantation dose of 8.0×1015cm−2, the projected range and the variance of arsenic ions in the silicon substrate are smaller those of phosphorous ions. Accordingly, second source region16formed in body region3through the ion implantation is included in first source region15formed through the ion implantation of phosphorous ions. In the region in which the substrate surface is exposed, impurities are introduced into the substrate without being hindered by silicon oxide film4or first insulating film14. As a result, second source region16with a higher concentration can be formed at the corners of the top of trench6through the ion implantation of arsenic. A shape corresponding to the exposed substrate surface appears on the bottom of second source region16, but an influence of impurities or the like introduced through the side wall of exposed trench6in this example acts thereon. Accordingly, as shown inFIG. 14, second source region16has a shape in which the width of the impurity region in the direction perpendicular to the side wall of trench6with an increase in distance in the depth direction of trench6from the surface.

In the ion implantation, at least N-type impurities constituting second source region16are introduced into first insulating film14formed on gate electrode12in trench6.

As described above, in this exemplary embodiment, source region17disposed along trench6can be formed to be adjacent to the top of gate electrode12and trench6without using a lithography technique. That is, in the shape, the width of the impurity region in the direction perpendicular to the side wall of trench6decreases with an increase in distance in the depth direction of trench6from the surface. Regarding the impurity concentration, as it gets closer to the top of the side wall of trench6, the impurity concentration increases. First source region15described above can be formed in a self-alignment manner. Second source region is disposed in a region including the substrate surface on both sides of trench6, on the top of first source region15, extending by a predetermined distance from an end of trench6and the side wall of trench6, on first source region15, extending by a predetermined depth from the top of trench6. In this way, second source region16with an impurity concentration higher than that of first source region15can be formed in a self-alignment manner.

When a P-type body contact region can be formed through introduction of P-type impurities to be described later, adjacent first source regions15, which are formed in the process of forming source region17, may be separated from or connected to each other between adjacent trenches6. Since second source region is formed through the introduction of impurities using etched-back first insulating film14and silicon oxide film4as a mask, a high-concentration N-type impurity region is not formed in the region in which the body contact region is formed.

After source region17including first source region15and second source region16is formed as described above, second insulating film18serving as a planarization film reducing unevenness of the substrate is deposited on the substrate as shown inFIG. 15. Although not particularly limited, a silicon oxide film with a thickness of about 500 nm to 1500 nm is deposited as second insulating film18in this exemplary embodiment.

Subsequently, as shown inFIG. 16, second insulating film18, first insulating film14, and silicon oxide film4on body region3and source region17are removed through a dry etching process. This etching is carried out in a state where an etching mask including a resist pattern is disposed on second insulating film18covering the polysilicon interconnection part such as a transistor non-forming region. In the etching, the stacked insulating film including first insulating film14and second insulating film18filled on gate electrode12is etched in a state where it is located lower than the top of trench6. The stacked insulating film filled on gate electrode12becomes an embedded insulating film19filling the top side of gate electrode12in trench6. On the contrary, the stacked insulating film covered with a resist pattern remains as interlayer insulating film20on the substrate. The stacked insulating film on the semiconductor substrate on which the resist pattern is not disposed is removed to expose the substrate surface. The resist pattern is not limited to the polysilicon interconnection part on the substrate but can be disposed to cover the region in which interlayer insulating film20should be formed.

As described above, in this exemplary embodiment, source region17is formed by the ion implantation through first insulating film14. Accordingly, the silicon oxide film which is first insulating film14of the stacked insulating film includes the N-type impurities and the silicon insulating film which is second insulating film18does not include the N-type impurities. As shown inFIG. 15, the thickness of second insulating film18of the stacked insulating film formed between trenches6is smaller than the thickness of second insulating film18of the stacked insulating film formed on gate electrode12. Accordingly, when a dry etching condition that the etching rate of first insulating film14including the N-type impurities is higher than the etching rate of second insulating film18not including the N-type impurities is applied to the dry etching process on the stacked insulating film, the etching rate of the stacked insulating film formed between trenches6can be made to be higher than the etching rate of the stacked insulating film formed on gate electrode12. By employing this dry etching condition, the thickness of embedded insulating film19can be made to be larger, compared with the dry etching condition that the stacked insulating film is etched at the same etching rate. That is, since a thick insulating film can be interposed between a source electrode which is later formed on embedded insulating film19and gate electrode12, a decrease in withstanding voltage due to the decrease in thickness of embedded insulating film19can be suppressed. In this exemplary embodiment, first insulating film14and second insulating film18are formed of a silicon oxide film and phosphorous and arsenic ions are implanted into first insulating film14. Accordingly, in the dry etching process on the silicon oxide film, the etching rate of first insulating film14is naturally higher than the etching rate of second insulating film18. For example, when fluorine-based gas which is generally used to etch a silicon oxide film is used, the etching rate of first insulating film14is higher by about 5% than the etching rate of second insulating film18. In a wet etching process using hydrofluoric acid, the etching rate of first insulating film14is twice as high as the etching rate of second insulating film18.

After depositing second insulating film18and before etching the stacked insulating film, the surface of second insulating film18may be planarized through a CMP (Chemical Mechanical Polishing) process. Accordingly, the thickness of second insulating film18in the stacked insulating film formed between adjacent trenches6can be made to be smaller than the thickness of second insulating film18in the stacked insulating film formed on gate electrode12. As a result, embedded insulating film19can be more easily formed in each trench6. Since the thickness of the stacked insulating film to be etched after the CMP process is reduced by employing the CMP process, embedded insulating film19can be formed with a reduced thickness difference.

As shown inFIG. 16, the bottom and the side of embedded insulating film19are constructed by first insulating film14and the top thereof is constructed by second insulating film18. The bottom of interlayer insulating film20is constructed by first insulating film14and the top thereof is constructed by second insulating film18. However, in the subsequent drawings, a single insulating film is shown for the purpose of convenience.

When the formation of embedded insulating film19is completely, body contact region21is formed, as shown inFIG. 17, by introducing P-type impurities through the exposed substrate surface. The introduction of impurities can be carried out by ion implantation to the entire substrate surface. In the ion implantation, the impurities are preferably incident perpendicularly on the substrate. The ion implantation is carried out with an implantation dose by which the impurity polarity in the vicinity of trench6of source region17is not inverted. Accordingly, P-type body contact region21adjacent to source region17is formed on the top of body region3in a self-alignment manner. In the ion implantation, P-type impurities constituting body contact region21are introduced at least into the top of embedded insulating film19formed on gate electrode12in trench6.

For example, when source region17is formed through the ion implantation under the above-mentioned ion implantation condition and boron is used as the second conductivity type of impurities, body contact region21can be formed with implantation energy of 10 KeV and an implantation dose of 4.0×1015cm−2.

When the formation of body contact region21is completed in this way, a conductive film (source electrode) electrically connecting source region17and body contact region21is formed. Although not particularly limited, the conductive film includes a stacked film of barrier metal film22formed of a titanium film (Ti) and a titanium nitride film (TiN) and metal film23formed of an aluminum film in this exemplary embodiment.

First, as shown inFIG. 18, barrier metal film22with a thickness of about 20 nm to 150 nm is formed on the substrate on which body contact region21is formed through the use of a sputtering method or the like. Then, as shown inFIG. 19, metal film23with a thickness of about 1000 nm to 5000 nm is formed on barrier metal film22through the use of a sputtering method or the like. By applying a lithography technique and an etching technique to barrier metal film22and metal film23, a conductor pattern of a desired shape is formed and thus a vertical-gate transistor is completed.

As described above, in the semiconductor device with vertical gate according to this exemplary embodiment, source region17including first source region15and second source region16and body contact region21can be formed without using a lithography technique. Accordingly, it is not necessary to secure a margin for mask superposition shift and it is possible to form a minute body contact region regardless of capability of lithography equipment. That is, it is possible to reduce the gate electrode pitch, compared with the conventional art. When the gate electrode pitch is further reduced, contact resistance between the source region and the source electrode may increase. However, in this exemplary embodiment, a high-concentration second source region can be disposed at the corners of the top of a trench. Accordingly, it is possible to suppress an increase in contact resistance. As a result, it is possible to implement a semiconductor device with vertical gate with on-resistance smaller than that in the conventional art at a lower cost.

In the semiconductor device with vertical gate according to the conventional art described in Unexamined Japanese Patent Publication No. 2005-209807, a source region is formed through the use of entire-surface ion implantation without using a mask. Accordingly, the impurities constituting source region112may be implanted into the surface portion of the silicon substrate outside the transistor forming region in which trench105is formed. In this case, a parasitic bipolar transistor having an impurity region as a source region and including body region103and drain region102is formed in the peripheral region of the transistor forming region. The device may be destroyed due to the operation of the parasitic bipolar transistor.

On the contrary, in the semiconductor device with vertical gate according to this exemplary embodiment, as shown inFIG. 11, the entire substrate surface is covered with first insulating film14in the N-type ion implantation process for forming source region17. Accordingly, the N-type impurities are not introduced into the peripheral region of the transistor forming region. Even if the N-type impurities are introduced, only a low-concentration impurity region is formed and the low-concentration N-type impurity region is inverted to a P-type impurity region through the entire-surface implantation of P-type impurities to be described later. Therefore, in the semiconductor device with vertical gate according to this exemplary embodiment, an n-type impurity region is not formed in the surface portion of the semiconductor substrate outside the transistor forming region and a parasitic bipolar transistor is not formed. As a result, it is possible to reduce the possibility in which a device is destroyed due to the operation of the parasitic bipolar transistor as in the conventional semiconductor device with vertical gate.

In the above-mentioned embodiment, first source region15is formed by the impurity introduction through non-etched-back first insulating film14and second source region16is formed by the impurity introduction through etched-back first insulating film14. In this configuration, it is possible to form second source region16with a high concentration formed at the corners of the top of trench6while suppressing the enlargement (diffusion to the region in which body contact region21is formed) of first source region15in the horizontal direction, which is particularly desirable.

However, first source region15may be formed in a self-alignment manner by the impurity introduction through etched-back first insulating film14, instead of the impurity introduction through non-etched-back first insulating film14. In this case, both first source region15and second source region16are formed by the impurity introduction through etched-back first insulating film14, and a part of first source region15is introduced into the substrate through the exposed substrate surface. In this case, since the thickness of the thickness-increasing portion of first insulating film14decreases, the enlargement of first source region15in the horizontal direction increases, compared with the impurity introduction through non-etched-back first insulating film14. When the diffusion of N-type impurities into the region in which body contact region21is in the allowable range, it is possible to achieve the same operational advantages as in the above-mentioned configuration.

When first source region15and second source region16are formed by the impurity introduction through etched-back first insulating film14, the process of forming first insulating film14and the process of etching back the stacked film of first insulating film14and silicon oxide film4are successive. Accordingly, when the process of forming first insulating film14and the process of etching back the stacked film of first insulating film14and silicon oxide film4are carried out by the use of the same apparatus, it is also possible to substantially reduce the number of processes.

In the above-mentioned configuration, the thickness of first insulating film14remaining on polysilicon interconnection13constituting a gate drawing interconnection or the like may decrease in the process (FIG. 13) of etching back the stacked film of first insulating film14and silicon oxide film4. In this case, the impurities may be introduced into polysilicon interconnection13in the process of introducing impurities for forming second source region16. When the impurities are introduced into polysilicon interconnection13, the sheet resistance value of polysilicon interconnection13may vary to cause an operation difference between unit cells constituting the semiconductor device with vertical gate or a characteristic difference between manufactured semiconductor device with vertical gates. The impurity introduction into polysilicon interconnection13may occur even when an implantation acceleration voltage is raised in the ion implantation for forming first source region15.

Therefore, the following process may be employed. That is, conductive polysilicon film9with a thickness of 200 nm to 800 nm which is a material of a gate electrode is deposited on the substrate in the process shown inFIG. 8and cap insulating film10with a thickness of 50 nm to 200 nm is then deposited on the substrate as shown inFIG. 20. Although not particularly limited, the same silicon oxide film as the first insulating film stacked thereon later is used as cap insulating film10.

Subsequently, as shown inFIG. 21, resist pattern11covering the region in which the polysilicon interconnection such as a gate drawing interconnection should be formed is formed and cap insulating film10is etched using resist pattern11as a mask. Subsequently, resist pattern11is removed and then polysilicon film9is etched using patterned cap insulating film10as a mask. Accordingly, as shown inFIG. 22, polysilicon film9on silicon oxide film4and trench6is removed and gate electrode12is formed in trench6. At the same time, polysilicon interconnection13, on which cap insulating film10is formed, is formed in the transistor non-forming region. After polysilicon interconnection13is formed, first insulating film14is formed on the substrate as shown inFIG. 23.

In this configuration, polysilicon interconnection13is covered with a thick stacked film including cap insulating film10and first insulating film14. Accordingly, even when the implantation acceleration voltage is raised in the ion implantation (FIG. 24) for forming first source region15to be carried out thereafter, and the ion implantation (FIG. 26) for forming second source region16to be carried out after etching back (FIG. 25) first insulating film14and silicon oxide film4, N-type impurities are not introduced into polysilicon interconnection13. Therefore, it is possible to suppress occurrence of an operation difference or a characteristic difference in the semiconductor device with vertical gate. When polysilicon film9is a polysilicon film having conductivity by forming a non-doped polysilicon film and then performing N-type impurity ion implantation and annealing processes thereon, it may be possible to prevent the external diffusion of impurities from polysilicon film9at the time of annealing by forming cap insulating film10. The thickness of cap insulating film10can be appropriately set within a range in which the above-mentioned advantages can be achieved.

On the other hand, in the process (FIG. 16) of etching first insulating film14, second insulating film18, and silicon oxide film4in the above-mentioned embodiment, the stacked insulating film including first insulating film14and second insulating film18filled on gate electrode12may be etched in a state where the top surface thereof is substantially flush with the top (substrate surface) of trench6. In this case, as shown in FIG.27, the top surface of embedded insulating film19filling the top of gate electrode12in trench6is substantially flush with the top of trench6.

In this case, as shown inFIG. 28, since the side wall of trench6is not exposed in the process of forming body contact region21, the introduction of P-type impurities from the side wall to source region17is suppressed. That is, it is possible to prevent an increase in source resistance.

In this configuration, since source region17and barrier metal film22are in contact with only the top surface of source region17, it is preferable that an entire-surface dry etching process be carried out after forming body contact region21and before forming barrier metal film22. In the entire-surface etching process, as shown inFIG. 29, a part of embedded insulating film19is etched back to expose source region17constituting the side wall of trench6. Accordingly, it is possible to increase the contact area between source region17and barrier metal film22and to suppress an increase in contact resistance to source region17. The amount of embedded insulating film19etched can be set, for example, to a range of 50 nm to 300 nm which is smaller than the thickness of first insulating film14. Although not particularly limited, the etching may be carried out in a state where a resist pattern is formed on interlayer insulating film20, from the viewpoint of preventing a decrease in thickness of interlayer insulating film20.

As shown inFIG. 29, the dry etching process for exposing first source region15from the side wall of trench6is preferably carried out under such a condition to process source region17at the top of the side wall of trench6in a curved shape. This curved surface can be implemented by employing an etching condition (for example, where the etching rate of embedded insulating film19is about twice to five times as high as the etching rate of silicon) that the etching rate of silicon (epitaxial silicon layer) is higher than the etching rate of embedded insulating film19. Alternatively, at the final step of the entire-surface dry etching, inert gas such as Ar can be introduced to carry out a sputter-etching process. Accordingly, the concave portion formed just on embedded insulating film19can be easily embedded with metal film23or the like. The subsequent formation of the barrier metal film and the metal film is as described above. The curved-shape processing step at the top of the side wall of trench6may be applied to the etching process for forming embedded insulating film19shown inFIG. 16.

A semiconductor device according to a modified example of the exemplary embodiment of the present invention will be described below with reference to the accompanying drawings along with the manufacturing method thereof.

FIG. 30is a schematic diagram illustrating a semiconductor device according to a modified example of the exemplary embodiment of the present invention. InFIG. 30, the source electrode and the structure above the source electrode are not shown.FIG. 30is only a schematic diagram and thus the dimensional ratio of constituent parts does not show the actual dimensional ratio. Here, differences fromFIG. 1will be mainly described.

First, inFIG. 1, the depth of source region17becomes smaller as it gets away from the trench. On the other hand, as shown inFIG. 30, the depth of source region17may not substantially vary as it gets away from the trench.

InFIG. 1, embedded insulating film19embeds a part of the concave portion formed on the top of trench6. On the other hand, as shown inFIG. 30, embedded insulating film19may fully embed the concave portion formed on the top of trench6and may embed rectangular region25to be described later to fully cover the top surface of source region17.

InFIG. 1, body contact region21is disposed on the top surface of body region3so as to be adjacent to source region17. On the other hand, as shown inFIG. 30, body contact region21may be disposed on the bottom of second trench24formed on the top surface of body region3. At this time, body contact region21may be disposed at a position lower than the bottom of source region17. Body contact region21may be disposed at a position lower than the top surface of gate electrode12.

InFIG. 1, it is assumed that trench6has a width of about 0.18 μm and a depth of about 0.8 μm and the trenches are arranged with a pitch of 0.6 μm. On the other hand, inFIG. 30, it is assumed that trench6has a width of about 0.15 μm to 0.5 μm and the trenches are arranged with a pitch of 0.4 μm to 1.5 μm. That is, the modified example has a configuration more suitable for a finer semiconductor device.

A method of manufacturing a semiconductor device according to the modified example of the exemplary embodiment of the present invention will be described below with reference toFIGS. 31 to 58. InFIGS. 31 to 58, a transistor forming region is shown on the left side and a peripheral region (transistor non-forming region) of the transistor forming region in which interconnections such as a gate drawing interconnection are formed is shown on the right side. Similarly toFIG. 30,FIGS. 31 to 58are only schematic diagrams and the dimensional ratio of constituent parts does not show the actual dimensional ratio. Hereinafter, if a thin film is formed on the top surface, it is appropriately expressed that a film is formed on a substrate.FIGS. 31 to 40are the same asFIGS. 2 to 11and thus description thereof will not be repeated. The manufacturing method ofFIG. 41and the drawings subsequent thereto will be described below in detail. InFIG. 11, the thickness-increasing portion of first insulating film14has a forward tapered shape with a slope of which the angle with respect to the substrate surface is in a range of 30° to 60°. Here, when the angle is smaller than 30°, the thickness of the central portion of the insulating film in the region interposed between trench6and adjacent trench6decreases and it is thus difficult to achieve the function as a hard mask of an etching process for forming rectangular region25. When the angle is larger than 60°, the thickness of the insulating film deposited on the side wall of the concave portion on gate electrode12increases and it is thus difficult to appropriately shape the substrate surface to be exposed in an isotropic etching process which is carried out subsequently.

First, afterFIG. 40, as shown inFIG. 41, a part of gate insulating film8, silicon oxide film4, and first insulating film14disposed on the upper side wall of trench6are isotropically etched to expose a part of body region3.

Thereafter, as shown inFIG. 42, the exposed part of body region3is removed by etching to form rectangular region25and silicon mesa region26at the same time. At this time, the bottom of rectangular region25is formed at a height equal to or smaller than that of the top surface of gate electrode12.

Then, as shown inFIG. 43, by introducing phosphorous as N-type impurities into the bottom surface of rectangular region25using first insulating film14on gate insulating film8and silicon oxide film4and first insulating film14on silicon mesa region26as a mask, first source region15is formed in body region3. The impurity introduction can be carried out by ion implantation. At this time, the acceleration voltage of the ion implantation preferably employs the acceleration voltage with which impurities are introduced into the region adjacent to the top of gate electrode12. At this time, source region15can be formed under the ion implantation condition of, for example, implantation energy of 40 KeV and an implantation dose of 4.0×1015cm−2.

Subsequently, as shown inFIG. 44, second source region16is formed by carrying out ion implantation using arsenic as N-type impurities. At this time, by setting the implantation energy such that second source region16is shallower than the first source region, the impurity region of second source region16formed in body region3through the ion implantation is included in the impurity region formed through the ion implantation of phosphorous ions. That is, the N-type impurity concentration of the substrate surface can be raised by forming second source region16through the use of the ion implantation of arsenic. At this time, source region16can be formed under the ion implantation condition of, for example, implantation energy of 30 KeV and an implantation dose of 4.0×1015cm−2. In this way, source region17including first source region15and second source region16is formed.

In this ion implantation, N-type impurities constituting source region17are introduced into first insulating film14formed on gate electrode12in trench6and silicon oxide film4and first insulating film14formed on silicon mesa region26.

As shown inFIG. 45, second insulating film18serving as a planarization film reducing unevenness on the substrate is deposited on the substrate. Although not particularly limited, a silicon oxide film with a thickness of about 500 nm to 1500 nm is deposited as second insulating film18in this exemplary embodiment.

As shown inFIG. 46, second insulating film18, first insulating film14, and silicon oxide film4on body region3and source region17are removed by a dry etching process. This etching is preferably carried out in a state where an etching mask including a resist pattern is disposed on second insulating film18covering the polysilicon interconnection part such as a transistor non-forming region. In the etching, it is preferable that the stacked insulating film including first insulating film14and second insulating film18filled on gate electrode12be etched in a state where the stacked insulating film is located lower than the top surface of silicon mesa region26to be embedded insulating film19filling the top of gate electrode12and rectangular region25in trench6and the stacked insulating film covered with the resist pattern remain as interlayer insulating film20on the substrate. The stacked insulating film on the semiconductor substrate on which the resist pattern is not disposed is removed to expose the substrate surface. The resist pattern can be disposed to cover the region in which interlayer insulating film20should be formed, without being limited to the polysilicon interconnection part on the substrate.

As described above, in this modified example, source region17is formed by ion implantation through silicon oxide film4and first insulating film14. Accordingly, silicon oxide film4of the stacked insulating film and the silicon oxide film as first insulating film14include N-type impurities as shown inFIG. 44, and the silicon insulating film as second insulating film18does not include N-type impurities as shown inFIG. 45. As shown inFIG. 45, the thickness of second insulating film18of the stacked insulating film formed on silicon mesa region26between trenches6is smaller than the thickness of second insulating film18of the stacked insulating film formed on gate electrode12and rectangular region25. Accordingly, when the dry etching condition that the etching rate of silicon oxide film4and first insulating film14including N-type impurities is higher than the etching rate of second insulating film18not including N-type impurities is applied to the dry etching process on the stacked insulating film, the etching rate of the stacked insulating film formed on the silicon mesa region between trenches6can be made to be higher than the etching rate of the stacked insulating film formed on gate electrode12and rectangular region25. By employing this dry etching condition, the thickness of embedded insulating film19can be made to be larger than that in the dry etching condition that the stacked insulating film is etched at the same etching rate. That is, since a thick insulating film can be interposed between the source electrode to be formed on embedded insulating film19later and gate electrode12, it is possible to suppress a decrease in withstanding voltage due to the decrease in thickness of embedded insulating film19. In this modified example, since first insulating film14and second insulating film18are formed of a silicon oxide film and phosphorous and arsenic ions are implanted into first insulating film14, the etching rate of first insulating film14naturally becomes higher than the etching rate of second insulating film18in the dry etching process on the silicon oxide film. For example, when fluorine-based gas which is generally used to etch a silicon oxide film is used, the etching rate of first insulating film14is higher by 5% than the etching rate of second insulating film18. In the wet etching process using hydrofluoric acid, the etching rate of first insulating film14is twice as high as the etching rate of second insulating film18.

After depositing second insulating film18and before etching the stacked insulating film, the surface of second insulating film18may be planarized through the use of a CMP (Chemical Mechanical Polishing) process. Accordingly, the thickness of second insulating film18of the stacked insulating film formed on the silicon mesa region between adjacent trenches6can be made to be smaller than the thickness of second insulating film18of the stacked insulating film formed on gate electrode12and rectangular region25. As a result, it is possible to more easily form embedded insulating film19in each trench6. Since the thickness of the stacked insulating film to be etched after the CMP process is reduced by applying the CMP process, embedded insulating film19can be formed with a reduced thickness difference.

Then, as shown inFIG. 47, the substrate surface from which silicon mesa region26is exposed is etched using embedded insulating film19as a mask to form second trench24. At this time, at least embedded insulating film19and the source region are exposed from the side wall of second trench24and body region3is exposed from the bottom surface of second trench24.

Subsequently, as shown inFIG. 48, by introducing P-type impurities, body contact region21is formed. In this ion implantation, it is preferable that the impurities be incident substantially perpendicularly on the substrate. The ion implantation is carried out with an implantation dose by which the impurity polarity of source region17is not inverted. Accordingly, P-type body contact region21is formed on body region3in a self-alignment manner. In the ion implantation, P-type impurities constituting body contact region21are introduced into at least the top of embedded insulating film19formed on gate electrode12and rectangular region25in trench6.

For example, when source region17is formed through the ion implantation under the above-mentioned ion implantation condition and boron is used as the second conductivity type of impurities, body contact region21can be formed with implantation energy of 5 KeV and an implantation dose of 1.0×1015cm−2.

When the formation of body contact region21is completed in this way, a conductive film (source electrode) electrically connecting source region17and body contact region21is formed. Although not particularly limited, the conductive film is formed of a stacked film of barrier metal film22including a titanium film (Ti) and a titanium nitride film (TiN) and metal film23including a tungsten film and an aluminum film in this modified example.

First, as shown inFIG. 49, barrier metal film22with a thickness of about 10 nm to 100 nm is formed on the substrate having body contact region21formed thereon through the use of a CVD method or the like. Then, as shown inFIG. 50, metal film23including a tungsten film with a thickness of about 50 nm to 400 nm and an aluminum film with a thickness of about 1000 nm to 5000 nm is formed on barrier metal film22through the use of a CVD method or the like. By applying a lithography technique and an etching technique to barrier metal film22and metal film23, a conductor pattern of a desired shape is formed and a vertical-gate transistor is completed.

As described above, the semiconductor device with vertical gate according to this modified example has a structure in which source region17, second trench23, and body contact region21can be formed without using a lithography technique. Accordingly, it is not necessary to secure a margin for mask superposition shift and it is possible to further reduce the gate electrode pitch, compared with the conventional art. Body contact region21is formed in the same plane as source region17or below the source region and is connected to the source electrode through the conductor film at low resistance. As a result, it is possible to implement a semiconductor device with vertical gate with smaller on-resistance in which the operation of a parasitic bipolar transistor is suppressed due to lower contact resistance between the body region and the source electrode. In the semiconductor device with vertical gate, since the impurity concentration of source region17formed below the silicon surface of rectangular region25can be made to have a steep impurity concentration gradient or the impurity concentration gradient can be easily controlled, it is possible to easily control the channel length of a vertical MOS transistor along trench6and thus to shrink the vertical transistor in the vertical direction.

After conductive polysilicon film9with a thickness of 200 nm to 800 nm as a gate electrode material is deposited on the entire surface inFIG. 37, silicon oxide film10with a thickness of 50 nm to 200 nm is deposited thereon as shown inFIG. 51. Subsequently, as shown inFIG. 52, resist pattern11covering a polysilicon interconnection forming region of a gate drawing interconnection or the like is formed and silicon oxide film10is etched using resist pattern11as a mask. Polysilicon film9may be etched using patterned silicon oxide film10as a mask after removing the resist. Accordingly, as shown inFIG. 53, polysilicon film9on silicon oxide film4and trench6is removed to form gate electrode12in trench6and to form polysilicon interconnection13having silicon oxide film10formed thereon in the transistor non-forming region at the same time. Subsequently, as shown inFIG. 54, first insulating film14is formed on the substrate. First insulating film14fills the concave portion on gate electrode12and has a portion increasing in thickness with an increase in distance from the top of trench6on the substrate surface on both sides of trench6. At this time, a thick stacked film including silicon oxide film10and first insulating film14is formed on polysilicon interconnection13. Accordingly, as shown inFIGS. 57 and 58, when first source region15and second source region16are formed in the subsequent processes, N-type impurities are not introduced into polysilicon interconnection13even with an implantation acceleration voltage set to be higher. In other words, N-type impurities are introduced into polysilicon interconnection13shown inFIG. 50.

The above-mentioned exemplary embodiment does not limit the technical scope of the present invention and can be modified and applied in various forms without departing from the technical spirit of the present invention, in addition to the above-mentioned. For example, a polysilicon film is used as the material of gate electrode12, but other conductive material such as amorphous silicon may be used. Similarly, the materials of silicon oxide film4, cap insulating film10, first insulating film14, second insulating film18, barrier metal film22, and metal film23are not limited to the above-mentioned materials, but may be appropriately changed. The processes described in the above-mentioned exemplary embodiment can be replaced with known processes equivalent thereto, as long as the advantages of the present invention can be achieved.

The present invention describes a semiconductor device with vertical gate having vertical gate electrodes in which plural trenches6are arranged in parallel, but may be applied to semiconductor device with vertical gates having vertical gate electrodes in which trenches are arranged in a lattice shape in which the trenches cross each other and in a zigzag shape.

According to the present invention, it is possible to form a source region and a body contact region even for a small gate electrode gap. The present invention is useful as a semiconductor device with vertical gate and a method of manufacturing the semiconductor device with vertical gate.